FLOORING MATERIAL

Abstract: A flooring material comprises 30-70 parts by weight of a copolymer of ethylene and an alpha -olefin having 4-10 carbon atoms, preferably an ethylene/octene copolymer, 20-40 parts by weight of polypropylene, 5-20 parts by weight of a cross-linked ethwlene polymer, preferably a copolymer of ethylene and an ethylenically unsaturated silane compound, 10-25 parts by weight of an organic filler, preferably polyethylene having a melt index below 0.1 g/10 min (190 DEG C/21.6 kg) and a phase stability in the flooring material of at least about 200 DEG C, 0.2-7 parts by weight of a flame retardant, preferably silicone and magnesium stearate, 0.1-2 parts by weight of an antistatic agent, and 0.1-1 part by weight of a stabiliser. The flooring material is free from inorganic fillers.

Description: FLOORING MATERIAL The invention relates to a flooring material, and more specifically concerns a halogen-free flooring mate¬ rial that is free from inorganic fillers. In order to be acceptable, a flooring material has to possess a number of different properties, which are more or less incompatible. One such property is process¬ ibility, i.e. it has to be possible to process the mate¬ rial so as to form it into a sheetlike or weblike floor¬ ing material. In this context, it is of primary impor- tance that the material is easily calendered. Further¬ more, the flooring material should be wear- and scratch- resistant, and its surface should exhibit such friction as to be suited for use, for instance by people walking on it. In addition, the material should be weldable, enabling the provision of tight joints when putting down a floor. The flooring material should, moreover, enable optimum cleaning, and should thus be polishable and pre¬ ferably have a dirt-repellent surface. The resilience and the softness of the flooring material, which are measured by indentation-recovery, are essential qualities, which are of importance in order to avoid lasting indentations of furniture and rolling objects, such as office chairs, and which also affect the walking comfort. Moreover, the fire resistance is vital, and the flooring material should be as fire-resistant as possible while, if catch¬ ing fire, giving off as little irritant smoke as pos¬ sible. Using polyvinyl-chloride-based materials, such as polyvinyl chloride (PVC) and vinyl chloride copolymers, primarily copolymers of vinyl chloride and vinyl acetate, as flooring materials is previously known. These mate¬ rials have many advantages, such as fetching a low price, being easy to process, and having a great range of varia¬ tion, i.e. the properties of the material are easily adjusted with the aid of various additives, such as plas- ticisers and pigments. However, PVC-based flooring materials also suffer from a number of drawbacks. In recent years, attention has focused on these drawbacks, and efforts have been made to provide other synthetic flooring materials not based on PVC. Among other things, PVC-based flooring materials are disadvantageous in that they contain chlo¬ rine (halogen), which forms hydrogen chloride upon com- bustion. Also, the various additives included in PVC- based flooring materials and typically containing diffe¬ rent metal compounds yield metal-containing residues when combusted. For reasons of costs and properties, PVC-based flooring materials further contain considerable amounts of fillers which generally are of inorganic type, such as calcium carbonate, clays, and aluminium trihydrate. These inorganic fillers are non-combustible and thus leave a contaminating residue, which has to be deposited, when the flooring material is combusted. When PVC-based floor- ing materials are combusted, various additives, such as lime or dolomite, are used for binding released chlorine. As a result, larger amounts of material have to be depo¬ sited, and the costs are increased. Also, an addition of inorganic fillers has an adverse effect on the wear resistance of the material. In an effort to obviate the above-mentioned draw¬ backs of the PVC-based flooring materials, one has, in recent years, tried to develop halogen-free flooring materials, which usually are based on different mixtures of olefin polymers. US Patent 5,276,082 teaches such a halogen-free flooring material, which comprises a mixture of a silane-grafted polymer and an ungrafted polymer. To be more specific, the mixture contains a first component, which is a copolymer of ethylene and another monomer selected from the vinyl esters of saturated and unsatu¬ rated carboxylic acids, preferably vinyl acetate, and a second component, which consists of a silane-grafted ver- sion of the above-mentioned ethylene copolymer, i.e. pre¬ ferably silane-grafted ethylene/vinyl acetate. A third essential component of the mixture is a filler, prefer¬ ably calcium carbonate, clay or aluminium trihydrate, which is present in an amount of 30-90% by weight. Even though the flooring material according to US Patent 5,276,082 is free from halogen, it has, like other prior-art flooring materials, a high content of inorganic fillers, which result in the formation of environmentally questionable or objectionable metal-containing substances and ash when destroyed by combustion of the flooring material. This invention aims at obviating the drawbacks of the prior art by providing a halogen-free flooring mate- rial which is not based on PVC and, in addition, is free from inorganic fillers. According to the invention, this aim is achieved by a flooring material comprising a defined composition of olefin polymers in combination with an organic filler and certain additives. To be more specific, the invention provides a floor¬ ing material which is characterised in that it comprises 30-70 parts by weight of a copolymer of ethylene and an α-olefin having 4-10 carbon atoms, 20-40 parts by weight of polypropylene, 5-20 parts by weight of a crosslinked ethylene polymer, 10-25 parts by weight of an organic filler, 0.2-7 parts by weight of a flame retardant, 0.1-2 parts by weight of an antistatic agent, and 0.1-1 part by weight of a stabiliser, and that the material is free from inorganic fillers. Preferably, the flooring material according to the invention comprises 40-60 parts by weight of a copolymer of ethylene and an α-olefin having 4-10 carbon atoms, 25-30 parts by weight of polypropylene, 5-15 parts by weight of a crosslinked ethylene polymer, 10-20 parts by weight of an organic filler, 0.6-4 parts by weight of a flame retardant, 0.1-1 part by weight of an antistatic agent, and 0.1-1 part by weight of a stabiliser. These and other distinctive features and advantages of the invention will appear in more detail from the fol¬ lowing description as well as the appended claims. As indicated above, the flooring material according to the invention contains a first component in the form of 30-70 parts by weight, preferably 40-60 parts by weight, of a copolymer of ethylene and an α-olefin having 4-10 carbon atoms. This component is intended to impart elasticity to the material and to reduce its melting tem¬ perature, resulting in a wider temperature range for processing and hence improving the processibility of the material. The copolymer also improves the properties of the flooring material as regards wear resistance and indentation-recovery. In order to attain an aimed-at pro¬ cessing range of about 150-200°C, the melting point of the copolymer should be below 120°C, preferably ranging between about 50°C and 100°C. The density of the copoly¬ mer is about 0.87-0.92 g/cm . Octene is a preferred α-olefin comonomer, and an instance of a preferred copo¬ lymer is the ethylene/octene copolymer available from Dow under the designation DSH 8501.00. As a second component, the flooring material accord¬ ing to the invention contains 20-40 parts by weight of polypropylene, preferably 25-30 parts by weight. This component enhances the hardness of the material and reduces its friction. In addition, the dirt-repellent qualities of the material are improved, i.e. the floor¬ ing material becomes easier to clean. An example of a preferred propylene polymer is the one available from Borealis AB under the tradename of Embryon" HG 770 J having a density of 0.903 g/cm and a melt flow of 25 g/ 10 min (230°C/2.16 kg). As a third component, the flooring material accord¬ ing to the invention contains 5-20 parts by weight, pre¬ ferably 5-15 parts by weight, of a crosslinked ethylene polymer, preferably a silane-crosslinked ethylene poly- mer. The preferred silane-crosslinked ethylene polymer may consist of either a graft copolymer of ethylene and an ethylenically unsaturated, hydrolysable silane com¬ pound or, which is preferred, a copolymer of ethylene and an ethylenically unsaturated, hydrolysable silane com- pound. As silane compound, use may, for instance, be made of vinyl silanes, such as vinyl trimethoxy silane. Such silane (graft) copolymers are crosslinked under the action of water and a silanol condensation catalyst, such as dibutyltin dilaurate. The crosslinked ethylene polymer component improves the processing properties of the mix¬ ture by increasing the viscosity of the material and hence reducing the mobility therein, thereby facilitating the achievement of the aimed-at patterns. Furthermore, the crosslinked ethylene polymer improves the properties of the material as regards wear and indentation-recovery. In order to optimise the effect of the crosslinked ethy¬ lene polymer component in the composition, the degree of crosslinking should not be too high. Preferably, the silane compound constitutes about 1-30% by weight, pre- ferably about 1-15% by weight, of the crosslinked ethy¬ lene polymer. As an example of a preferred crossiinkable ethylene polymer, mention may be made of the products LE 4421 and LE 4438 available from Borealis AB. The former is the polymer itself, whereas the latter is the cross- linking catalyst. As a fourth component, the flooring material accord¬ ing to the invention contains 10-25 parts by weight, pre¬ ferably 10-20 parts by weight, of an organic filler. By the term "organic filler" is meant an organic material which, upon combustion, leaves a residue of no more than 10% by weight, preferably no more than 5% by weight, and which preferably consists chiefly, i.e. to at least 95% by weight, of carbon, hydrogen and oxygen. According to the invention, this organic filler is intended to replace, either by itself or in combination with the other components, the inorganic fillers generally used in prior-art flooring materials. In order to be able to per¬ form its function properly, the organic filler should be phase-stable, i.e. form a phase of its own in the form of discrete particles in the flooring material, when the flooring material is being processed. Since the flooring material is normally processed at a temperature below about 200°C, this means that the organic filler should be phase-stable or "particle-stable", i.e. be present in the form of discrete particles in the flooring material, up to a temperature of at least about 200°C. According to the invention, the organic filler preferably is a polymer material selected from one or more of: starch, cellulose and polyethylene, the polyethylene having a melt index below 0.1 g/10 min (190°C/21.6 kg) and a phase stability to at least about 200°C. When used as fillers, starch and cellulose are advantageous in that they both have fairly high contents of hydroxyl groups, which are cross-linked with the silane groups of the crossiinkable ethylene polymer component. This provides yet another possibility of adjusting the properties of the material. As an exam- pie of a preferred polyethylene filler, mention may be made of the polymer marketed under the tradename of Lupolen UHM 201 by BASF and having a density of 0.93 g/ cm 3 and a melt flow below 0.1 g/10 min (190°C/21.6 kg). This polyethylene filler also contributes to giving the flooring material a harder surface. Apart from the components mentioned above, the flooring material according to the invention contains certain additives, as appears from the foregoing and will be described in more detail below. In order to obtain the aimed-at flame resistance, the material contains 0.2-7 parts by weight of a flame retardant, preferably 0.6-4 parts by weight. Even though conventional flame retardants are not excluded from the flooring material according to the invention, it is espe¬ cially preferred that the flame retardant is a silicone replacing conventional antimony- or halogen-containing flame retardants. The effect of the silicone is enhanced by combining it with an organic metal salt, more speci¬ fically an organic salt of a metal from the group IIA of the Periodic table. Preferably, the organic metal salt is magnesium stearate. The above flame retardant con- tents include both the silicone and the organic metal salt. Normally, the silicone is present in an amount of 0.1-5 parts by weight, preferably 0.5-3 parts by weight, while the organic metal salt is present in an amount of 0.1-2 parts by weight, preferably 0.1-1 part by weight. In addition to imparting the aimed-at flame-retardant properties to the material, the flame retardant has a lubricating ability, which facilitates the processing of the material and further enhances its impact resistance. As an instance of a preferred flame retardant, mention may be made of the product available under the tradename of SFR 100 Silicone Fluid from General Electric. Further details of this flame retardant are found in US Patent 4,387,176. Moreover, the flooring material according to the invention contains 0.1-2 parts by weight of an antistatic agent, preferably 0.1-1 part by weight. This is an addi¬ tive required in order to avoid static charging of the flooring material and to improve the dirt-repellent pro¬ perties of the finished material. The antistatic agent employed in the flooring material according to the inven¬ tion can be selected from known antistatic agents, but preferably consists of glycerol stearate, for instance in the form of the product available from Hoechst under the tradename of Hostastat FE-2. Finally, the flooring material contains a stabi¬ liser, which has a stabilising effect as regards oxida¬ tion and decomposition (yellowing), which otherwise may occur, for instance in the presence of the antistatic agent mentioned above. As an example of a suitable sta¬ biliser, mention may be made of sterically hindered phe¬ nols, for instance those available from Ciba under the tradename of Irganox 1010. Apart from the components indicated above, the flooring material according to the invention may contain optional conventional additives and pigments. With the composition described above, in particular the lack of inorganic fillers, the flooring material according to the invention have only marginal contents of metals that are questionable or objectionable from the point of view of the environment and are released by leaching, biological-chemical decomposition or combus- tion, i.e. the content of such metals as aluminium, lead, cadmium, copper, chromium and zinc is basically zero. The inventive flooring material of the above compo¬ sition can be produced by using conventional techniques and conventional equipment. There should thus be no need of any detailed description of the production of the flooring material according to the invention. As an exam¬ ple of such production, it may, however, be mentioned that the components and the additives may first be weigh¬ ed and mixed in cold state, whereupon the resulting mix- ture is melted and extruded in the form of bands, which are fed to a rolling mill and there are processed to webs. The resulting webs are cut to pieces or crushed and may then immediately be rolled or pressed to form the finished flooring material. Alternatively, the cut or crushed webs may first be stored and then at a suitable moment be heated and rolled or pressed to form the finished flooring material. The invention will now be further elucidated with the aid of a few non-restricting Examples. The following comparison is based on two apparently equivalent, 2-mm- thick homogeneous flooring materials intended for public use. The one flooring material is produced in accordance with the invention, while the other flooring material is a PVC-based flooring material of known composition. The upper side and the lower side of the flooring material according to the invention and the upper side of the PVC-based flooring material were subjected to a corona treatment in order to increase the adhesion. Then, the upper side and the lower side of the flooring mate¬ rial according to the invention were coated with 5 g (based on dry solids) of a primer (based on RIC from PPG Industries) per m . Finally, the one surface (the upper side) of the two flooring materials was coated with 10 g (based on dry solids) of polyurethane (based on NeoRez R- 986 from Zeneca Resins) per m . The purpose of this poly¬ urethane layer is to make the flooring materials easier to clean and enhance their dirt-repellent capacity. Since the polyurethane layer affects the wear resistance, the wear-resistance test in Example 1 was also performed on flooring materials having no such surface layer of poly¬ urethane. The other properties of the flooring material are only marginally affected by the polyurethane layer. The two flooring materials have the following compo¬ sition. Flooring Material According to the Invention Parts weight Tradename Designation Supplier 47.7 DSH 8501.00 Ethylene-α-olefin DOW Chemicals copolymerisate ® 26 Embryon ^ HG770J Polypropylene Borealis 8.7 LE 4421 Crossiinkable Borealis ethylene polymer 0.4 LE 4438 Catalyst Borealis 13 Lupolen UHM201 UHMW - PE BASF 1 SFR100 Flame retardant General Electric 0.7 Parma Magnesium Barlocher stearate 0.5 Hostastat FE-2 Antistatic agent Hoechst 0.1 Irganox 1010 Stabiliser Ciba 1.9 Pigment PVC-based Flooring Material (Tarkett Eminent from Tarkett AB Parts bv . weight Tradename Designation Supplier 47.1 Norvinyl S6260 PVC Norsk Hydro Plast AB 17.2 DEHP Diethylhexyl Neste phthalate Chemicals 0.7 Lankromark BaZn Stabiliser Akcros LZ 1694 Chemicals 0.9 Lankroflex EWS Epoxidised soy¬ Akcros bean oil Chemicals 0.3 Tefacid 1 VT65 Stearic acid Tefac AB 12.6 Stradolomit A30 Dolomite Strabruken AB 10.8 Sjόhasten FF Calcium carbonate Malmόkrita AB 8.4 Kaolin FA Kaolin Zavod 2 Pigment Example 1 In this Example, the wear resistance of the flooring material according to the invention was compared with that of the prior-art, PVC-based flooring material. The wear resistance was determined according to the standard EN 660. In the test, the wear resistance of the flooring material according to the invention was found to be 1.4 mm /100 turns for material having a surface layer of polyurethane and 0.65 mm /100 turns for material having no such surface layer, whereas the PVC-based flooring material had a wear resistance of 3.38 mm /100 turns when provided with a surface layer of polyurethane and a wear resistance of 3.06 mm /100 turns when not provided with such a surface layer. Thus, the flooring material according to the invention had a much better wear resis¬ tance than the known PVC-based flooring material. Example 2 In this Example, the fire propagation and the smoke emission of the flooring material according to the inven¬ tion and of the prior-art PVC-based flooring material were tested. The test was carried out in accordance with the standard SIS 024825. According to this standard, the fire propagation should be below 55 cm, and the fire emission should be below 30%. In the test, the flooring material according to the invention was found to have a fire propagation of 40 cm and a smoke emission of 3%, whereas the PVC-based floor¬ ing material was found to have a fire propagation of 22 cm and a smoke emission of 16%. Both materials thus had a fire propagation well below the standard limit. However, the flooring material according to the invention gave off very little smoke and much less than the PVC- based flooring material. In addition to this test, the fire propagation and the smoke emission were tested according to the so-called Radiation Panel Test. According to this test, an accept- ed material should require a power exceeding 0.45 W/cm 2 for fire propagation, and the material should exhibit a smoke emission below 750%-min. In this test, the flooring material according to the invention required 0.50 W/cm in order to catch fire and had a smoke emission of 55%-min, whereas the PVC-based flooring material required 0.99 W/cm 2 in order to catch fire and had a smoke emission of 300%*min. Also in this case, both materials had fire-propagation values and smoke-emission values below the standard limit. However, the flooring material according to the invention gave off much less smoke than the PVC-based flooring material. Example 3 In this Example, the indentation-recovery of the flooring material according to the invention and the PVC- based flooring material were determined in accordance with the standard SIS 923505. In this test, the flooring material according to the invention had an indentation of 0.88 mm after 5 min and a recovery of 89.8% after 24 h. The corresponding values of the PVC-based flooring material were, respec¬ tively, 0.74 mm and 87.8%. Thus, the flooring material according to the invention had a slightly higher inden¬ tation value than did the PVC-based flooring material, but this was compensated for by a higher degree of reco¬ very. Example 4 In this Example, one determined the residues left after combustion of the flooring material according to the invention and the PVC-based flooring material, as well as the deposition requirement created by these com¬ bustion residues. The flooring materials were burnt to ashes at 550°C. The results of the test are indicated in the Table below. Ashes after combustion Deposition requirement for ashes and bound chlorine Flooring kg/m % by weight of kg/m % by weight of material starting material starting material Invention 0.12 5.9 0.12 5.9 PVC 0.84 27.6 2.4 70 It is evident from this Table that the flooring material according to the invention yields less ash and thus involves much smaller deposition requirements than does the PVC-based flooring material. The much greater deposition requirement of the PVC-based flooring material is, inter alia, due to the addition of lime/dolomite to bind released chlorine. Example 5 This Example aims at demonstrating the content of metals, which are environmentally objectionable and ori¬ ginate from fillers and other additives, found in the flooring material according to the invention and the PVC- based flooring material. Thus, the contents of these metals were determined in ashes from the combustion of the flooring materials by dissolving the ashes in con¬ centrated nitric acid. The dissolution was performed by mixing the ashes and the nitric acid in a container of Teflon , whereupon the container was sealed and heated in a microwave oven. Samples that had not been burnt to ashes were used for determining the contents of cadmium and lead. The final determination of the metal contents was performed with the aid of Plasma emission spectro- metry (ICP-AES) or Plasma mass spectrometry (ICP-MS). The metal contents determined appear from the Table below. Invention PVC Test method 2 g/m g/m Aluminium 0.002 12 ICP-AES Lead 0.000 0.015 ICP-MS Cadmium 0.0000 0.0001 ICP-MS Copper 0.000 0.003 ICP-AES Chromium 0.000 0.008 ICP-AES Zinc 0.00 0.15 ICP-AES It is evident from the Table that the flooring mate¬ rial according to the invention causes no, or but insig¬ nificant, environmental pollution owing to its metal con¬ tent. It should be pointed out that the PVC-based floor¬ ing material has an adverse effect on the environment not only as a result of its metal content but also as a result of the addition of lime/dolomite to bind released chlorine.

Claims: CLAIMS 1. A flooring material, c h a r a c t e r i s e d in that it comprises 30-70 parts by weight of a copolymer of ethylene and an α-olefin having 4-10 carbon atoms, 20-40 parts by weight of polypropylene, 5-20 parts by weight of a crosslinked ethylene polymer, 10-25 parts by weight of an organic filler, 0.2-7 parts by weight of a flame retardant, 0.1-2 parts by weight of an antistatic agent, and 0.1-1 part by weight of a stabiliser, and that the material is free from inorganic fillers. 2. A flooring material as set forth in claim 1, c h a r a c t e r i s e d in that it comprises 40-60 parts by weight of a copolymer of ethylene and an α-olefin having 4-10 carbon atoms, 25-30 parts by weight of polypropylene, 5-15 parts by weight of a crosslinked ethylene polymer, 10-20 parts by weight of an organic filler, 0.6-4 parts by weight of a flame retardant, 0.1-1 part by weight of an antistatic agent, and 0.1-1 part by weight of a stabiliser. 3. A flooring material as set forth in claim 1 or 2, c h a r a c t e r i s e d in that the α-olefin employed is octene. 4. A flooring material as set forth in any one of claims 1-3, c h a r a c t e r i s e d in that the cross- linked ethylene polymer is a copolymer of ethylene and an ethylenically unsaturated silane compound. 5. A flooring material as set forth in claim 4, c h a r a c t e r i s e d in that the copolymer contains 1-30% by weight of the silane compound. 6. A flooring material as set forth in any one of claims 1-5, c h a r a c t e r i s e d in that the organic filler is selected from one or more of: starch, cellulose and polyethylene having a melt index below 0.1 g/10 min (190°C/21.6 kg) and a phase stability in the flooring material of at least about 200°C. 7. A flooring material as set forth in any one of claims 1-6, c h a r a c t e r i s e d in that the flame retardant comprises a silicone and a an organic metal salt. 8. A flooring material as set forth in claim 7, c h a r a c t e r i s e d in that the organic metal salt is magnesium stearate. 9. A flooring material as set forth in any one of claims 1-8, c h a r a c t e r i s e d in that the anti¬ static agent comprises glycerol stearate. 10. A flooring material as set forth in any one of claims 1-9, c h a r a c t e r i s e d in that the stabi¬ liser is a sterically hindered phenol.

Inventors: LUNDQUIST ESKIL, LUNDQUIST, ESKIL
Applicants: LUNDQUIST ESKIL, TARKETT AB, LUNDQUIST, ESKIL
Application year: 1996
Main classification: C08L23
IPC codes: C08K5, C08L23, C08L51, C09G1, E04F15