IMPROVED ORGANOCLAY COMPOSITIONS

Abstract: Organoclay compositions which comprise the reaction product of a smectite-type clay having an ion exchange capacity of at least 50 meq. wt. per 100 g. clay (active basis), and an alkoxylated quaternary ammonium compound having one or two alkoxylated chains containing 0-10 moles ethylene oxide and 3-15 moles of propylene or butylene oxide residues are useful thixotropic materials, especially for the preparation of aqueous systems.

Description: [ IMPROVED ORGANOCLAY COMPOSITIONS BACKGROUND OF THE INVENTION This invention relates generally to organoclays. and. more specifically, to improved organoclays which are produced by the reaction of the organoclay with an alkoxylated quaternary ammonium compound. Organoclays. representing the reaction product of a smectite-type clay with a quaternary ammonium compound, have long been known for use in gelling of organic liquids such as lubricating oils, linseed oil. toluene and the like. A large variety of highly useful products, such as lubricating greases, are producible through use of such gelling agents. The procedures and chemical reactions pursuant to which these organoclays are prepared, are well-known. Thus, under appropriate conditions, the organic compound which contains a cation, will react by ion exchange with the clay which contains a negative layer lattice and exchangeable cations to form the organoclay products. Other uses for such modified organoclays are those such as are disclosed in U. S. Patent 5J 51 J 55. wherein organically modified smectite clays are utilized in a process for deinking wastepaper. and in U. S. Patent 4.677.158. wherein smectite-type clays which have been reacted with quaternary ammonium compounds are utilized as thickeners for aqueous suspensions, particularly latex paints and caulks. These modified organoclays differ from those of the present invention in the type of quaternary ammonium compound with which they are reacted. This modification produces organoclays with markedly superior properties than those of the prior art. OBJECTS OF THE INVENTION It is an object of the present invention to prepare organoclay compositions having improved rheological properties, and thus useful as thixotropes in aqueous compositions. It is further an object ofthe present invention to prepare improved aqueous compositions, especially paint formulations, which possess improved properties by virtue of their inclusion of the organoclay compositions of the present invention. SUMMARY OF THE INVENTION In accordance with the present invention, it has unexpectedly been discovered that the reaction of smectite-type clays with certain alkoxylated quaternary ammonium compounds can produce organoclay products having superior properties when utilized as water-based thixotropes. Thus, the present invention is concerned with an organoclay composition comprising the reaction product of a smectite-type clay having an ion exchange capacity of at least 50 meq. wt. per 100 g. clay (active basis), and an alkoxylated quaternary ammonium compound having the following formula: R: I Θ e R-.-N-R, X (I) Rα wherein R, and R are alike or different, and are selected from the group consisting of C, - C « alkyl. benzyl or 2-hydroxyethyl groups: R, is a C Cχ alkyl. benzyl or 2- hydroxyethyl group, or an alkoxylated chain containing 0-10 moles ethylene oxide and 3-15 moles of an alkylene oxide residue selected from the group consisting of propylene oxide, butylene oxide, and mixtures thereof: and R is an alkoxylated chain containing 0-10 moles ethylene oxide and 3-15 moles of an alkylene oxide residue selected from the group consisting of propylene oxide, butylene oxide, and mixtures thereof: and X is the salt anion. DESCRIPTION OF PREFERRED EMBODIMENTS The smectite clays which are utilized as one of the starting materials o the present invention are those which have been conventionalh utilized in the prior art. Suitable smectite-type clays are those which have a cation exchange capacity of at least 50 milliequivalents (meq.) weight (wt. ) per 100 grams of clay (active basis). Useful clays for such purposes include the naturally occurring Wyoming variety of swelling bentonite and similar clays, and hectoritc. which is a swelling magnesium-lithium silicate clay. The clays are preferably converted to the sodium form if they are not already in this form. This can be effected, again as in known in the art. by a cation exchange reaction, or the clay can be converted via an aqueous reaction with a soluble sodium compound. Smectite-type clays prepared synthetically can also be utilized, such as montmorillonite. bentonite. beidelite. hectoritesaponite. and stevensite. Such clays. and processes for their preparation, are described in U. S. Patents 4.695.402. 3.855.147. 3.852.405. 3.844.979. 3.844.978. 3.671.190. 3.666.407. 3.586.478. and 3.252.757. all of which are herein incorporated by reference. The alkoxylated quaternary ammonium salts which are reacted with the smectite-type clav are of the formula R, R--N-R, X ( I) wherein R, and R : are alike or different, and are selected from the group consisting of C, - A alkyl. benzyl or 2-hydroxyethyl groups: R, is a C,-C x alkyl. benzyl or 2- hydroxyethyl group, or an alkoxylated chain containing 0-10 moles ethylene oxide and 3-15 moles an alkylene oxide residue selected from the group consisting of propylene oxide, butylene oxide and mixtures thereof: and R is an alkoxylated chain containing 0-10 moles ethylene oxide and 3-15 moles of an alkylene oxide residue selected from the group consisting of propylene oxide, butylene oxide and mixtures thereof: and X is the salt anion. The salt anion X is methosulfate. ethosulfate. methylcarbonate. ethylcarbonate. chloride, bromide, or mixtures thereof, and is most preferably a methosulfate ion. The salt anion may also, however, be nitrate, hydroxide, acetate, or mixtures of these. The alkoxylated chains present in the alkoxylated quaternary ammonium compounds of the present invention determine the particularly advantageous properties of the resultant organoclays of the present invention. Thus, the prior art organoclays which contain saturated alkyl groups in the quaternary ammonium compound provide modified organoclays which are too hydrophobic to be useful in aqueous systems. Likewise, the use of the prior art polyethoxylated chain quaternary ammonium compounds provide modified organoclays which are too hydrophilic and which provide organoclays which are difficult to de-water during processing steps. It is thus critical to the present invention to provide quaternary ammonium compounds which, upon reaction with the smectite-type clay, will afford an organoclay composition having the desired hydrophobic/hydrophilic balance, resulting in desirable properties in the end-products. Preferred embodiments ofthe present invention will utilize quaternary ammonium compounds having one or two alkoxylated chains each containing 1 -5 moles ethylene oxide and 4-10 moles propylene oxide and/or butylene oxide residues. Highly preferred embodiments of the present invention are organoclays which comprise the reaction product of smectite-type clays with alkoxylated quaternary ammonium compounds wherein the R, and R 4 chains each contain the residue of 5 moles ethylene oxide and 5 moles propylene oxide, and are thus represented by the followinε formula: ( CH, ), N [ (CH : CH , O) x (CH CH(CH, H wherein x and y = 5 or wherein R, and R, each contain the residue of 1 mole of ethylene oxide and 4 moles of propylene oxide, represented by the formula: (CHP N [ (CH : CHJA (CIPCHfCHJ (0\ ], H wherein x and y = 4 or wherein R, and R, each contain the residue of 1 mole ethylene oxide and 5 moles each of propylene oxide and butylene oxide, represented by the formula: (CH,): N [ (CH : CH : 0\ (CH : CH(CHJO\ (CH,CH(CH,CH-,)O), ], H wherein x=l . y=5 and z=2 Other preferred embodiments of the invention invoh e the reaction product of a smectite-type clay with an alkoxylated quaternary ammonium compound wherein R, R and R, are each a methyl group and R, is an alkoxylated chain containing 1 mole ethylene oxide and 9 moles propylene oxide represented by the formula: (CHP, N [(CH : CH 0) x (CHPH(CHJO) H wherein x= 1 and y=9 or when R A is an alkoxylated chain containing 1 mole ethylene oxide. 5 moles propylene oxide and 5 moles of butylene oxide represented by the formula: (CHp N [(CH : CH : 0) (CH : CH(CHJO\ (CH : CH(CH 2 CHJO)J H wherein x=l . y=5 and z=5. x. y and z when employed herein denote relative reactive molar ratios and the reaction products generally represent a product distribution centered around these ratios. Other quaternary ammonium salts which are particularly useful in the present invention are described in the U.S. Patents 3.123.641. 4.144.122. 4.432.833 and 5.296.627. which are incorporated herein by reference. The alkoxylated quaternary ammonium compounds useful in the present invention of the present invention can be prepared by various methods known by those of ordinary skill in the art. In a preferred method, the quaternary ammonium compound is prepared by the reaction of a tertiary amine and an alkylating agent. Some alkylating agents, well known to those practicing the art. include organic halides such as methyl chloride, diorganosul fates such as dimethyl sulfate. or diorgano carbonates, such as dimethyl carbonate. This method of preparation is described in ENCYCLOPEDIA OF CHEMICAL TECHNOLOGY edited by Kirk/Othmer (Third Edition. Vol 19. page 521-531 ) which is incorporated herein by reference. The tertiary amine. useful in preparing the quaternary ammonium salt, is preferably a polyalkoxylated amine produced by reacting ammonia, a primary amine. or a secondary amine with an alkoxylating agent. Suitable alkoxylating agents include alkyl epoxides such as ethylene oxide, propylene oxide, and butylene oxide. Tertiary polyalkoxylated amines which can also be employed in the present invention are prepared by reacting ammonia, a primary amine. or a secondary amine with a polyalkoxylated alcohol or polyakoxylated glycol. Especially useful tertiary amines may also be made by alkylating a primary, or secondary alkoxylated amine. such as the available JEFFAMINE E* series of alkoxylated amines available from Huntsman Chemicals (JEFFAMINE1 is a registered mark of Huntsman Chemicals Inc.) or the available TECTRONIC B ' series of alkoxvlated amines available form BASF Corporation (TECTRONIC& is a registered trademark of BASF Corporation). Examples of other tertiary amines useful in the present invention can be found in U.S. Patent Nos. 3.654.370. 4.739.094. 4.960.942. 4.967.005. 5.344.984 and 5347.051. which are incorporated herein by reference. The amount of the alkoxylated quaternary ammonium compound reacted with the smectite-type clay depends upon the specific clay and the desired degree of hydrophobicity. Typically, the amount of cation ranges from about 0.1 to about 150%. preferably from about 100 to about 130% of the cation exchange capacity of the clay. Thus, for example, when bentonite is used, the amount of cation reacted with the clay will range from about 85 to about 1 3 milliequivalents. preferably from about 95 to about 124 milliequivalents per 100 grams of clay. 100% active basis. A further embodiment of the present invention is the process for preparing the organoclay composition comprising the reaction product of a smectite-type clay having an ion exchange capacity of at least 50 meq. wt. per l OOg. clay (active basis), and an alkoxylated quaternary ammonium compound o the formula: j e e RAJ-R, X ( 1 ) R, wherein R, and R : are alike or different, and are selected from the group consisting of C, - C s alkyl. benzyl or 2-hydroxyethyl groups: R ; is a C,- alkyl. benzyl or 2- hydroxyethyl group, or an alkoxylated chain containing 0-10 moles ethylene oxide and 3-15 moles an alkylene oxide residue selected from the group consisting of propylene oxide, butylene oxide and mixtures thereof: and R 4 is an alkoxylated chain containing 0-10 moles ethylene oxide and 3-15 moles of an alkylene oxide residue selected from the group consisting of propylene oxide, butylene oxide and mixtures thereof: and X is the salt anion: which comprises: a) dispersing a smectite type clay having an ion exchange capacity of at least 50 meq. wt. per 100 g. clay in an aqueous media: b) heating the dispersing of step (a) to a temperature in excess of 30° C: c) adding the heated dispersion of step (b) of a quaternary ammonium salt of the formula R: I © Θ R--N-R, X ( I ) R wherein R, and R are alike or different, and are selected from the group consisting of C, - C s alkyl. benzyl or 2-hydroxyethyl groups: R, is a C,-C 3 alkyl. benzyl or 2- hydroxyethyl group, or an alkoxylated chain containing 0-10 moles ethylene oxide and 3-15 moles an alkylene oxide residue selected from the group consisting of propylene oxide, butvlene oxide and mixtures thereof: and R 4 is an alkoxylated chain containing 0-10 moles ethylene oxide and 3-15 moles of an alkylene oxide residue selected from the group consisting of propylene oxide, butylene oxide and mixtures thereof: and X is the salt anion. in the desired milliequivalent ratio: and d) agitating the mixture of step (c ) to effect completion of the reaction. The organoclay composition of the present invention is thus prepared by admixing an aqueous dispersion of the smectite-type clay, warmed to a temperature in excess of 30°C. with an alkoxylated quaternary ammonium compound of formula I to exchange the metal counterions that are naturally present in the smectite-type clay. The reaction is typically conducted at a temperature within the range of from about 40°C. to about 100 °C. for a period of time sufficient for the alkoxylated quaternary ammonium compound to react with the clay particles. Preferably, the clay is dispersed in the water at a concentration from about 3% to about 15% by weight and the slurry is centrifuged to remove non-clay impurities. The slurry is then agitated and heated to the desired temperature, and the quaternary ammonium salt added in the desired milliequivalent ratio. The alkoxylated quaternary ammonium compounds are typically liquids, but they can be dispersed in water to facilitate the reaction. Agitation is continued to effect completion ofthe reaction. The amount of the alkoxylated quaternary ammonium compound added to the smectite-type clay for the purposes of this invention must be sufficient to impart to the clay the enhanced characteristics desired. The milliequivalent ratio is defined as the number of milliequivalents of the alkoxx lated quaternary ammonium compound, per 100 grams of cla\ . 100% active basis. The typical smectite-type clays of this invention have a milliequivalent ratio of 1 ' rom about 10 to about 150. The preferred milliequivalent ratio will vary depending on the characteristics of the particular alkoxylated quaternary ammonium compound utilized and the end use for the resultant product. When the composition of the present invention is utilized for its rheological properties for application as to control sagging of fluid films and prevent settling and hard packing of pigments present in paint compositions, particularly latex paint compositions, it is typically employed in an amount of about 5 lb. to about 95 lb./lOO gallons paint composition. The present invention thus contemplates the preparation of latex paint formulations having improved properties which comprise the addition of the improved organocla\ composition which is the reaction product of a smectite-type clay having an ion exchange capacity of at least 50 meq. wt. per 100 g. clay and an alkoxylated quaternary ammonium compound ofthe general formula I. Typically, the latex paint formulation will contain the improved organoclay composition is an amount of about 2 to about 10% by weight of the finished latex paint formulation. Preferred formulations contain the organoclay thixotrope in an amount of about 3 to about 6% by weight of the finished latex paint formulation. Latex paint formulations containing the organocla> composition of the instant invention exhibit superior characteristics when brush out. roll out and spray out applications were compared with standard commercially available latex paint formulations. The latex paints formulated using the organoclay compositions exhibited a high low -shear viscosity and a low high-shear viscosity in contrast to the commercial paints which exhibited lower low-shear values and higher high-shear values. When sheared, theses latex paint formulations thinned out to a flowable and workable viscosity. The low high-shear viscosity of the these latex paints results in excellent atomization in airless spray application. In addition, the presence ofthe organoclay in the latex paint formulations improved the sag characteristics of these paints to such a degree that sprayouts of thirty mils or higher were common. The invention will now be illustrated b> a series of Examples, which are intended to set forth typical and preferred procedures to be utilized in the practice ofthe invention. EXAMPLE 1 The preparation of a smectite-type clay composition comprising the reaction product of a smectite-type clay and a quaternary ammonium compound ofthe formula I wherein the R, and R are each a methyl group and the R, and R 4 chains each contain the residue of 5 moles ethylene oxide and 5 moles propylene oxide is prepared as follows: 5000 Grams of an aqueous three pass slurry of montmorillonite SCPX 818 containing 3.72 % solids in a 5 gallon tank is heated on a lightening mixer to 60 °C. (140 °F). To this heated slum' is then added 87.19 grams ofthe alkoxylated quaternary ammonium compound of formula I wherein the R, and R 2 are each a methyl group and the R-, and R chains each contain the residue of 5 moles ethylene oxide and 5 moles propylene oxide (A R 94005 Lot =94016RS-T) at 30 MER. w hich mixture is then stirred for fifteen minutes until the clay swells and mixing is no longer possible. After transfer to a quart jar. no separation was observed after twenty-four hours, indicating completion of the reaction. This was calculated 5.03% solids 255.89 grams drv cla\ EXAMPLE 2 The preparation of a smectite-type clay composition comprising the reaction product of a smectite-type cla\ and a quaternan ammonium compound ofthe formula I wherein the R, and R are each a methyl group and the R, and R 4 chains each contain the residue of 1 mole ethylene oxide and 5 moles propylene oxide is prepared as follows: 5000 Grams of an aqueous three pass slurry of montmorillonite SCPX 818 containing 3.72 % solids in a 5 gallon tank is heated on a lightening mixer to 60 °C. (140 °F). To this heated slurry is then added 43.6 grams of the alkoxylated quaternary ammonium of formula I wherein the R, and R, are each a methyl group and the R- and R 4 chains each contain the residue of 1 mole ethylene oxide and 5 moles propylene oxide (ARK 94006 Lot #94016RS-T) at 20 MER. which mixture is then stirred for fifteen minutes until the clay swells and mixing is no longer possible. After transfer to a quart jar. no separation was observed after twenty-four hours, indicating completion ofthe reaction. This was calculated 4.38% solids 220.91 grams dry cla\ EXAMPLE 3 A latex paint formulation consisting of: Volume Material Weight 5.85 SM/OC CEP/HRD Thixotrope prepared as in Example 1 49.70 14.42 Water 120.30 0.09 Trovsan 142-Bacteriostat 1.00 6.00 1.00 3.00 1.00 22.00 2.00 Procedure for preparation: Add together the follow ing and mix: Then, mix and add: 31.27 UCAR 376 Latex 283.00 Check the following specs: A latex paint formulation consisting of: Volume Material Weight 8J9 SM/OC CEP/HRD Thixotrope prepared as in Example 1 69.58 100.42 1.00 6.00 1 .00 3.00 1 .00 22.00 2.00 Procedure for preparation: Add together and mix the following Then, mix and add: 31.27 UCAR 376 Latex 283.00 Check the following specs: EXAMPLE 5 A latex paint formulation consisting o : Volume 0.27 Bubble Breaker 748 2.00 Procedure for preparation: Add the following ingredients together and mix: 175.00 100.00 80.00 175.00 142.54 2.00 45.66 9.00 Then, mix and add: 31.27 UCAR 376 Latex 283.00 Check the following specs: EXAMPLE 6 A latex paint formulation consisting of the following: Volume Procedure for preparation: Add the following together and mix: Then, mix and add: J J7 UCAR 376 Latex 283.00 Check the following specs: EXAMPLE 7 A latex paint formulation consisting of: Procedure for preparation: Add together the following and mix: 175.00 100.00 17500 75.00 14.40 2.00 repared as in Ex. 2 170.00 9.00 Then, mix and add: 0 i l .27 UCAR 376 Latex 283.00 D 0 5 EXAMPLE 8 A latex paint formulation consisting of: Volume Material Weight 40.00 SM/OC CEP/HRD Thixotrope prepared as in Example 2 340.00 Thixotrope load adjusted on a dry solids basis (Thix. -r water = 170.0grams) 0.09 Troysan 142-Bacteriostat 1.00 0.65 Tamol 731 6.00 0.05 Potassium Tripolyphosphte 1.00 0.34 Triton N-l 01 ' 3.00 0J3 AMP-95 1.00 2.55 Propylene Glycol 22.00 0.27 Bubble Breaker 748 2.00 Procedure for preparation: Add together the following and mix: 175.00 100.00 80.00 175.00 18.20 2.00 9.00 Then, mix and add: 31.27 UCAR 376 Latex 283.00 EXAMPLE 9 Comparison of Paint Formulations A. An aqueous slurry of non-exchanged montmorillonite added to paint at a rate of 6 dry lbs/100 gallons paint was found to have the following characteristics: Brookfield Viscosity 1 RPM (rotations per minute) 94.400 cps. 10 RPM 17.880 cps. 100 RPM 2.884 cps. Krebs Stormer Viscosity 99 KU ICI Cone and Plate Viscosity 0.9 10 30 8.55 23.6 1 1.90 weight/gallon Syneresis Settling Rating 120/10D % ; .6. " Scrub rating Brush Drag Rating Brush Out Rating Roller Splatter Rating Spray Out Rating Good Atomization at 12-1 mil. Roll Out Rating 2 Splatter Fine Texture B. An aqueous slurry of montmorillonite exchanged with the quat ACAR 94005 (prepared as in Example 1. at 30 milliequivalenceJ OO grams montmorillonite) added to the same paint as A at 7 dry lbs/100 gallons paint was found to have the following characteristics: Brookfield Viscosity 1 RPM (rotations per minute) 80.000 cps. 10 RPM 14.400 cps. 100 RPM 2.628 cps. Krebs Stormer Viscosity 97 KU ICI Cone and Plate Viscosity 0.8 8 4 8.57 23.7 1 1 .92 weight/gallon Syneresis Settling Rating 120/10D % Scrub Rating 1 15/188 148/21 1 Brush Drag Rating Brush Out Rating Good Loading Poor Leveling Roller Splatter Rating 6-7 Spray Out Rating Good Atomization at 20 mils. Roll Out Rating 5 Splatter Med Texture 10 C. An aqueous slurry of montmorillonite exchanged with the quat ACAR 94006 (prepared as in Example 2 at 20 milliequivalence/1 0 grams montmorillonite added to the same paint as A at 6 dry lbs/100 gallons paint was found to have the following characteristics: Brookfield Viscosity 1 RPM (rotations per minute) 92.000 cps. 10 RPM 19.400 cps. 100 RPM 3.648 cps. Krebs Stormer Viscosity 109 KU ICI Cone and Plate Viscosity 0.9 Leneta Chart Sag Reading 10 Leveling Reading 4 pH 8.61 Temp. C° Pounds/Gallons 1 1.95 weight/gallon Syneresis Settling Rating 120/10D % 1.65 Scrub Rating 101/136 101/152 Brush Drag Rating Brush Out Rating OK Loading Poor Leveling Roller Splatter Rating Spray Out Rating Good Atomization at 18 mils. Roll Out Rating 5 Splatter Coarse Texture D. An aqueous slurry of non-exchanged montmorillonite added to paint at a rate of 6 dry lbs/100 gallons paint was found to have the following characteristics: Brookfield Viscosity 1 RPM (rotations per minute) 104.000 cps. 10 RPM 28.400 cps. 100 RPM 4.470 cps. Krebs Stormer Viscosity 1 15 KU 0 ICI Cone and Plate Viscosity 0.9 14 1 -2 8.1 7 22.6 1 1 .77 weight/gallon 1.85 166/200 137/216 Brush Drag Rating 2.5 30 Brush Out Rating Good Loading Roller Splatter Ratim 7-8 Spray Out Rating Good Λtomization at 16 mils. J3 Roll Out Rating 4 Splatter Fine Texture E. An aqueous slurry of montmorillonite exchanged with the quat ACAR 94005 (prepared as in E.xample 1. at 30 milliequivalenceJ O grams montmorillonite) added to the same paint as D at 7 dry lbs/100 gallons paint was found to have the following characteristics: Brookfield Viscosity 1 RPM (rotations per minute) 81.600 cps. 10 RPM 16.360 cps. 100 RPM 2.840 cps. Krebs Stormer Viscosity 101 KU ICI Cone and Plate Viscosity 0.8 Leneta Chart Sag Reading 8-9 Leveling Reading pH 8.24 Temp. C° 22.6 Pounds/Gallons 1 1.95 weight/gallon Syneresis Settling Rating 120/10D % 1 .79 Scrub Rating i 54/183 122/159 Brush Drag Rating 2.5-3 Brush Out Rating Good Loading Roller Splatter Rating Spray Out Rating Good Atomization at 17 mils. Roll Out Rating 2 Splatter Fine Texture F. An aqueous slurry of montmorillonite exchanged with the quat ACAR 94005 (prepared as in Example 1. at 30 milliequivalence; 1 0 grams montmorillonite) added to the same paint as D at 8 dry IbsJ OO gallons paint was found to have the following characteristics: ICI Cone and Plate Viscosity Leneta Chart Sag Reading 16 Leveling Reading 1 pH 8.21 Temp. C c 22.8 Pounds/Gallons .84 weight/gallon Syneresis Settling Rating 120/10D % Scrub Rating 137/154 103/167 Brush Drag Rating 2.5-3 Brush Out Rating Good Loading Roller Splatter Ratins. 9 Spray Out Rating Good Atomization at 18 mils. Roll Out Rating 5 Splatter Fine Texture G. An aqueous slum of montmorillonite exchanged with the quat ACAR 94006 (prepared as in Example 2 at 20 milliequπ alence/ 100 grams montmorillonite) added to the paint at 6 dry Ibs'l OO gallons paint was found to have the following characteristics: Brookfield Viscosity 1 RPM (rotations per minute) 130.000 cps. 10 RPM 27.000 cps. 100 RPM 4.640 cps. Krebs Stormer Viscosity 1 18 KU ICI Cone and Plate Viscosity 0.9 Leneta Chart Sag Reading 12- 13 Leveling Reading pH 8.18 Temp. C° 22.7 Pounds/Gallons 1.90 weight/gallon Syneresis Settling Rating 120/10D % 1.67 Scrub Rating 165/197 177/208 Brush Drag Rating 2.5-3 Brush Out Rating Good Loading Roller Splatter Rating 8-9 Spray Out Rating Good Atomization at 20 mils. Roll Out Rating 2 Splatter Medium Texture 23 H. An aqueous slurry of montmorillonite exchanged with the quat ACAR 94006 (prepared as in Example 2 at 20 milliequivalence/100 grams montmorillonite) added to the paint at 6 dry IbsT 00 gallons paint was found to have the following characteristics: Brookfield Viscositλ 1 RPM (rotations per minute) 81 .000 cps. 10 RPM 23.100 cps. 100 RPM 4.290 cps. Krebs Stormer Viscosin 1 14 KU ICI Cone and Plate Viscosity 0.9 Leneta Chart Sag Reading 12 Leveling Reading 2-3 pH 8.30 Temp. C° 22.6 Pounds/Gallons 1 1 .88 weight/gallon Syneresis Settling Rating 120/10D % 172 Scrub Rating 182/236 170/220 Brush Drag Rating Brush Out Rating OK Loading Roller Splatter Rating 7-8 Spray Out Rating Good Atomization at 25-30 mils. Roll Out Rating 3 Splatter Medium Texture I. An aqueous slurry of montmorillonite exchanged with the quat ACAR 94006 (prepared as in Example 2 at 20 milliequivalence/ 100 grams montmorillonite) added to the paint at 7 dry lbs 100 gallons paint was found to have the following characteristics: Brookfield Viscosity 1 RPM (rotations per minute ) 121.000 cps. 10 RPM 37.400 cps. 100 RPM 6.900 cps. Krebs Stormer Viscosity 136 KU ICI Cone and Plate Viscosity Leneta Chart Sag Reading 18 Leveling Reading 1 PH Temp. C° - Pounds/Gallons 1 1 .81 weight/gallon Syneresis Settling Rating 120/10D % 1 .61 Scrub Rating 145/1 96 157/196 Brush Drag Rating 3.5 Brush Out Rating Ex. Loading Roller Splatter Rating 8-9 Spray Out Rating Good Atomization at 18 mils. Roll Out Rating 5 Splatter Medium Texture J. An aqueous slurry of montmorillonite exchanged with the quat ACAR 94005 (prepared as in E.xample 1 at 30 milliequh alence/ 100 grams montmorillonite) added to the paint at 7 dry lbs/ 100 gallons paint was found to have the following characteristics: Brookfield Viscosit\ 1 RPM (rotations per minute) 86.800 cps. 10 RPM 17.880 cps. 100 RPM 3.192 cps. Krebs Stormer Viscosity 100 KU ICI Cone and Plate Viscosity 0.8 Leneta Chart Sag Reading 10 Leveling Reading pH 8.48 Temp. C° 23.0 Pounds/Gallons 1 1.90 weight/gallon Syneresis Settling Rating 120/10D % 1.61 Scrub Rating 145/190 163/194 Brush Drag Rating Brush Out Rating OK Loading Easy Roller Splatter Ratinj. 9 Spray Out Rating Good Atomization at 16 mils. Roll Out Rating 5 Splatter Rough Texture K. An aqueous slurry of montmorillonite exchanged with the quat ACAR 94006 (prepared as in Example 2 at 20 milliequh alence 100 grams montmorillonite) added to the paint at 5 dry lbs/100 gallons paint was found to have the following characteristics: Brookfield Viscosit\ per minute) 76.000 cps. 10 RPM 15.520 cps. 100 RPM 2.680 cps. Krebs Stormer Viscosit y 95 KU ICI Cone and Plate Viscosity 0.8 Leneta Chart Sag Reading 10 Leveling Reading 4 pH 8.32 Temp. C° 22 7 Pounds/Gallons 1 1 .89 weight/gallon Syneresis Settling Rating 120/10D % 2.42 Scrub Rating 131 /197 160/200 Brush Drag Rating Brush Out Rating Ex. Loading Easy Roller Splatter Rating 8 Spray Out Rating Good Λtomization at 19 mils. Roll Out Rating 2 Splatter Medium Splatter L. Benjamin Moore Contractor Flat Enhance Vinyl Latex paint was found to have the following characteristics: Brookfield Viscosity 1 RPM (rotations per minute) 22.000 cps. 10 RPM 6.960 cps. 100 RPM 2.548 cps. Krebs Stormer Viscosity 102 KU ICI Cone and Plate Viscosity Leneta Chart Sag Reading Leveling Reading pH 8.50 Temp. C° 23.6 Pounds/Gallons 12.14 weight/gallon Syneresis Settling Rating 120/10D % < 1 Scrub Rating 30/70 30/70 Brush Drag Rating Brush Out Rating Good Loading Leveling OK Roller Splatter Rating Spray Out Rating Fair Atomization at 12 mils. Roll Out Rating 5 Splatter Leveling OK M. Benjamin Moore Regal Wall Satin paint was found to have the following characteristics: Brookfield Viscosity 1 RPM (rotations per minute) 20.800 cps. 10 RPM 4.500 cps. 100 RPM 1.420 cps. Krebs Stormer Viscosity 87 KU ICI Cone and Plate Viscosity 1.4 Leneta Chart Sag Reading 15 Leveling Reading 7 pH 7.54 Temp. C° Pounds/Gallons 10.82 weight/gallon Syneresis Settling Rating ' 120/10D % <1 Scrub Rating 130/180 120/200 Brush Drag Rating Brush Out Rating Good Loading Leveling OK Roller Splatter Rating 7 Spray Out Rating Fair Atomization at 12 mils. Roll Out Rating 5 Splatter Leveling OK N. Benjamin Moore Contractor Flat with added paint was found to have the following characteristics: Krebs Stormer Viscosity 97 U ICI Cone and Plate Viscosity 1 .5 Leneta Chart Sag Reading 1 Slight color change when comparing sealed leneta chart drawdown versus unsealed leneta chart drawdown. O. Benjamin Moore paint with added tint was found to have the following characteristics: Krebs Stormer Viscosity 100 KU ICI Cone and Plate Viscosity 1 A Leneta Chart Sag Reading 18 Slight color change when comparing sealed leneta chart drawdown versus unsealed leneta chart drawdown. P. Product of Example 2 with commercial antisplattering Associative Thickener (Rohm & Haas) agent added. ICI Cone and Plate Viscosity 1.2 Roller Splatter Rating 8 TEST METHODS Sag and leveling were conducted on Leneta antisag bar and leneta leveling bar on leneta form 7B.

Claims: WHAT IS CLAIMED IS: 1. An organoclay composition comprising the reaction product of a smectite- type clay having an ion exchange capacity of at least 50 meq. wt. per 100 g. clay (active basis), and an alkoxylated quaternary ammonium compound having the following formula: R : I Θ Θ R.-N-R, X (I ) j R 4 wherein R, and R 2 are alike or different, and are selected from the group consisting of C,-C 8 alkyl. benzyl or 2-hydroxyethyl groups: R, is a C,-C 8 alkyl. benzyl or 2- hydroxyethyl group, or an alkoxylated chain containing 0-10 moles ethylene oxide and 3-15 moles of an alkylene oxide residue selected from the group consisting of propylene oxide, butylene oxide and mixtures thereof: and R 4 is an alkoxylated chain containing 0- 10 moles ethylene oxide and 3-15 moles of an alkylene oxide residue selected from the group consisting of propylene oxide, butylene oxide and mixtures thereof: and X is the salt anion. 2. The composition according to Claim 1 wherein the alkoxylated quaternary ammonium compound of formula I has the formula wherein R 3 and R are each independently an alkoxylated chain containing 1 -5 moles ethylene oxide and 4-10 moles of an alkylene oxide residue selected from the group consisting of propylene oxide, and/or butylene oxide and mixtures thereof. 3. The composition according to Claim 2 wherein the alkoxylated quaternary ammonium compound of formula I has the formula wherein R ? and R 4 each contain the residue of 5 moles ethylene oxide and 5 moles propylene oxide. 4. The composition according to Claim 2 wherein the alkoxylated quaternary ammonium compound of formula I has the formula wherein R, and R 4 each contain the residue of 1 mole of ethylene oxide and 4 moles of propylene oxide. 5. The composition according to Claim 2 wherein the alkoxylated quaternary ammonium compound of formula I has the formula wherein R, and R 4 each contain the residue of 1 mole ethylene oxide and 5 moles each of propylene oxide and butylene oxide. 6. The composition according to Claim 1 w herein the alkoxylated quaternary ammonium compound of the formula I has the formula wherein R,. R 2 . and R, are each a methyl group and R 4 is an alkoxylated chain. 7. The composition according to Claim 6 w herein the alkoxylated quaternary ammonium compound of formula I has the formula wherein R 4 is an alkoxylated chain containing 1 mole ethylene oxide and 9 moles propylene oxide. 8. The composition according to Claim 6 wherein the alkoxylated quaternary ammonium compound of formula I has the formula wherein R 4 is an alkoxylated chain containing 1 mole ethylene oxide. 5 moles propylene oxide, and 5 moles butylene oxide. 9. A process for the preparation of an organoclay composition comprising the reaction product of a smectite-type clay having an ion exchange capacity of at least 50 meq. wt. per 100 g. clay (active basis), and an alkoxylated quaternary ammonium compound having the following formula: R; I e e R--N-R, X (I ) I R wherein R, and R-, are alike or different, and are selected from the group consisting of C,-C 8 alkyl. benzyl or 2-hydroxyethyl groups: R ? is a C,-C 8 alkyl. benzyl or 2- hydroxyethyl group, or an alkoxylated chain containing 0-10 moles ethylene oxide and 3-15 moles of an alkylene oxide residue selected from the group consisting of propylene oxide, butylene oxide and mixtures thereof: and R 4 is an alkoxylated chain containing 0- 10 moles ethylene oxide and 3- 15 moles of an alkylene oxide residue selected from the group consisting of the propylene oxide, butylene oxide and mixtures thereof: and X is the salt anion. which comprises: a) dispersing a smectite-type clay having an ion exchange capacity of at least 50 meq. wt. per 100 g. clay, in an aqueous media: b) heating the dispersion of step (a) to a temperature in excess of 30° C: c) adding to the heated dispersion of step (b) of a quaternary ammonium salt R, e R--N-R, X (I ) I R 4 wherein R, and R are alike or different, and are selected from the group consisting of C|-C 3 alkyl. benzyl or 2-hydroxyethyl groups: R, is a C,-C x alkyl. benzyl or 2- hydroxyethyl group, or an alkoxylated chain containing 0-10 moles ethylene oxide and 3-15 moles of an alkylene oxide residue selected from the group consisting of propylene oxide, butylene oxide and mixtures thereof: and R 4 is an alkoxylated chain containing 0-10 moles ethylene oxide and 3-15 moles of an alkylene oxide residue selected from the group consisting of propylene oxide, butylene oxide and mixtures thereof: and X is the salt anion. in the desired milliequivalent ratio: and d) agitating of the mixture of step (c ) to effect completion of the reaction. 10. The process according to Claim 9 wherein the alkoxylated quaternary ammonium compound of formula I has the formula wherein the R, and R 4 substituents are each independently an alkoxylated chain containing 1-5 moles ethylene oxide and 4-10 moles of an alkylene oxide residue selected from the groups consisting of propylene oxide, butylene oxide, and mixtures thereof. 1 1. The process according to Claim 10 wherein the alkoxylated quaternary ammonium compound of formula I has the formula wherein R, and R each contain the residue of 5 moles ethylene oxide and 5 moles propylene oxide. 12. The process according to Claim 10 wherein the alkoxylated quaternan ammonium compound of formula I has the formula wherein R, and R each contain the residue of 1 mole of ethylene oxide and 4 moles of propylene oxide. 13. The process according to Claim 10 wherein the alkoxylated quaternary ammonium compound of formula I has the formula wherein R, and R each contain the residue of 1 mole ethylene oxide and 5 moles each of propylene oxide and butylene oxide. 14. The process according to Claim 9 wherein the alkoxylated quaternan' ammonium compound of formula I has the formula wherein R,. R : . and R-, are each a methyl group and R 4 is an alkoxylated chain. 15. The process according to Claim 14 wherein the alkoxylated quaternan ammonium compound of formula I has the formula wherein R is an alkoxylated chain containing 1 mole ethylene oxide and 9 moles propylene oxide. 16. The process according to Claim 14 wherein the alkoxylated quaternary ammonium compound of formula I has the formula wherein R 4 is an alkoxylated chain containing 1 mole ethylene oxide. 5 moles propylene oxide, and 5 moles butvlene oxide.

Inventors: GADBERRY JAMES F, HOEY MICHAEL, POWELL CLOIS E, GADBERRY, JAMES, F., HOEY, MICHAEL, POWELL, CLOIS, E.
Applicants: AKZO NOBEL INC, SOUTHERN CLAY PROD INC, AKZO NOBEL INC., SOUTHERN CLAY PRODUCTS, INC.
Application year: 1996
Main classification: C04B33
IPC codes: C04B33, C09D7, C09K3