Acrylic copolymer elastomer, its blend rubber and blend rubber composition

Abstract: A copolymer comprising an alkyl acrylate and an unsaturated ester compound represented by the following general formula: CH 2 =CRCOO(CH 2 )nPhOR', CH 2 =CRCOO(CH 2 )nOCO(CH 2 )mPhOR', CH 2 =CHOCO(CH 2 )nOCO(CH 2 )mPhOR', CH 2 =CHO(CH 2 )nOCO(CH 2 )mPhOR' or CH 2 =CHPh(CH 2 )nOCO(CH 2 )mPhOR' where R is a hydrogen atom or a methyl group; R' is a hydrogen atom, an acyl group or a trialkylsilyl group; and Ph is a phenylene group, forms a blend rubber having a good heat resistance and a good amine resistance with a fluorine-containing elastomer.

Description: BACKGROUND OF THE INVENTION 1. FIELD OF THE INVENTION The present invention relates to an acrylic copolymer elastomer, its blend rubber and a vulcanizable blend rubber composition, and more particularly to an acrylic copolymer elastomer blendable with a fluorine-containing elastomer, a blend rubber of the acrylic copolymer elastomer and a fluorine-containing elastomer, and a vulcanizable blend rubber composition. 2. RELATED PRIOR ART Acrylic copolymer elastomers (acrylic rubber) have good oil resistance and heat resistance and are cheap, and thus have been widely used as vulcanization-molding materials such as automobile sealing materials, etc. Due to recent higher efficiency of automobile engines and consequent higher temperature in the use circumstances, materials of much higher heat-resistance are in demand. Fluorine-containing elastomers (fluorine rubber), on the other hand, are used particularly at positions requiring a higher heat resistance among the automobile engine sealing materials owing to their distinguished heat resistance, but are very expensive. Furthermore, the fluorine rubber has such a disadvantage as a poor amine resistance, as compared with acrylic rubber. Various attempts, for example, formulation change, etc. have been so far made to improve the disadvantage, but no better amine resistance has been obtained yet. In the circumstances using an automobile engine oil containing an amine-based additive, there are fears of functional deterioration in the fluorine rubber product. Thus, the improvement of amine resistance is still keenly desired for the fluorine rubber. In these situations, many attempts have been also made to blend acrylic rubber with fluorine rubber, thereby satisfying the required heat resistance and cost at the same time, but the conventional technique of cross-linking these two rubbers by a cocross-linking agent capable of cocross-linking these two rubbers can hardly satisfy even the intermediate heat resistance between the heat resistance of acrylic rubber and that of fluorine-containing, and no satisfactory amine resistance has been obtained yet. CH-A-540 940 discloses compositions which are useful in stabilising organic compounds against the effects of ultraviolet light. It discloses a process for preparing a polymer by co-polymerising a monomer of the formula: wherein the bridging group -A- represents -OC n H 2n - or -(OC x H 2x ) y - (n is an integer of 3 or more and x and y are 2 or 3) with a comonomer selected from an alkyl acrylate, methacrylate, styrene, vinyl ester, butadiene or isoprene. SUMMARY OF THE INVENTION An object of the present invention is to provide an acrylic copolymer elastomer blendable with a fluorine-containing elastomer, which can give a blend rubber having an intermediate heat resistance between the heat resistance of acrylic copolymer elastomer and that of fluorine-containing elastomer, when blended with the fluorine-containing elastomer, and also having a good amine resistance. Another object of the present invention is to provide a blend rubber comprising such a acrylic copolymer elastomer as above and a fluorine-containing elastomer, and also provide its vulcanizable composition. According to the present invention, there is provided an acrylic copolymer elastomer, which is a copolymer of an alkyl acrylate having an alkyl group having 1 to 8 carbon atoms with an unsaturated ester compound having a hydroxyphenyl group, an acetoxyphenyl group or a trialkylsilyloxy group as a terminal group. According to the present invention, the acrylic copolymer elastomer can be formed into a blend rubber by blending with a fluorine-containing elastomer, and the blend rubber can be formed into a vulcanizable composition by adding to the blend rubber (1) a vulcanizing system comprising a quaternary onium salt and an acid acceptor, (2) a vulcanizing system comprising a tertiary sulfonium salt and an acid acceptor, or (3) a vulcanizing system comprising a tertiary phosphine compound, an epoxy compound and an acid acceptor. DETAILED DESCRIPTION OF THE INVENTION The acrylic copolymer elastomer for use in the present invention comprises 60 to 99. 9% by weight, preferably 80 to 99% by weight, of alkyl acrylate having an alkyl group having 1 to 8 carbon atoms as the main component. The alkyl acrylate includes, for example, alkyl acrylates, whose alkyl group is methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, n-amyl, n-hexyl, 2-ethylhexyl, n-octyl, and alkyl acrylates having a substituted alkyl group, such as 2-cyanoethyl acrylate. Preferably, ethyl acrylate and n-butyl acrylate are used. These alkyl acrylates can be used in a mixture of at least two thereof. The unsaturated ester compound having a hydroxyphenyl group, an acetoxyphenyl group or a trialkylsilyloxy group as a terminal group for use in copolymerization with the alkyl acrylate includes the following compounds (1) to (5), where copolymers of (1) to (4) with the alkyl acrylate each provide novel acrylic copolymer elastomers: (1) CH 2 =CRCOO(CH 2 )nPhOR' (2) CH 2 =CRCOO(CH 2 )nOCO(CH 2 )mPhOR' (3) CH 2 =CHOCO(CH 2 )nOCO(CH 2 )mPhOR' (4) CH 2 =CHO(CH 2 )nOCO(CH 2 )mPhOR' (5) CH 2 =CHPh(CH 2 )nOCO(CH 2 )mPhOR' where R: hydrogen atom or a methyl group R': hydrogen atom , an acyl group or a trialkylsilyl group Ph: a phenylene group, preferably a p-phenylene group, the phenylene group may have an alkyl group, an alkoxyl group, an alkoxyalkyl group, as a substiuent group n: an integer of 1 to 6 m: 0 or an integer of 1 to 3 The unsaturated ester compound represented by the foregoing formula (1) includes, for example: The unsaturated ester compound represented by the foregoing formula (2) includes, for example: The unsaturated ester compound represented by the foregoing formula (3) includes, for example: The unsaturated ester compound represented by the foregoing formula (4) includes, for example: The unsaturated ester compound represented by the foregoing formula (5) includes, for example: These compounds are synthesized in the following manner: (1) CH 2 =CRCOX + HO(CH 2 )nPhOH → CH 2 =CRCOO(CH 2 )nPhOH (X: halogen atom) This reaction can be carried out as a condensation reaction of (meth)acrylic acid halide with 4-hydroxybenzyl alcohol or 4-hydroxyphenetyl alcohol in the presence of a catalyst such as triethylamine. HO(CH 2 )nPhOH → CH 2 =CRCOO(CH 2 )nPhOR' This reaction can be carried out under the reaction conditions for the ordinary acylation reaction or trialkylsilylation reaction by adding to 4-hydroxybenzyl alcohol or 4-hydroxyphenetyl alcohol an acylating agent, for example, an acid anhydride such as acetic anhydride, propionic anhydride or butyric anhydride, or an acid halide such as acetyl halide, propionyl halide or butryl halide, or trialkylhalogenosilane such as trimethylhalogenosilane or triethylhalogenosilane. Or, the synthesis can be carried out through a direct condensation reaction, using 4-acetoxybenzyl alcohol, as a raw material, as given by the following reaction equation: CH 2 =CRCOX + HO(CH 2 )nPhOR' → CH 2 =CRCO(CH 2 )nPhOR' (X: halogen atom) (2) CH 2 =CRCOO(CH 2 )nOH + HOCO(CH 2 )mPhOH → CH 2 =CRCOO(CH 2 )nOCO(CH 2 )mPhOH This reaction can be carried out as a condensation reaction of ω-hydroxyalkyl (meth)acrylate with 4-hydroxybenzoic acid or 4-hydroxyphenylacetic acid in the presence of a dehydrating agent such as N,N'-cyclohexylcarbodiimide. The reaction can be also carried out as a dehydrohalogenation reaction using an acid halide of 4-hydroxybenzoic acid or 4-hydroxyphenylacetic acid in place of these acids. Then, the reaction for -PhOH → -PhOR' can be carried out in the same manner as in (1). (3) CH 2 =CHOCO(CH 2 )nX + HOCO(CH 2 )mPhOH → CH 2 =CHOCO(CH 2 )nOCO(CH 2 )mPhOH (X: halogen atom) Synthesis can be carried out as a condensation reaction of vinyl monohalogenocarboxylate such as vinyl monochloroacetate with 4-hydroxybenzoic acid or 4-hydroxyphenylacetic acid in the presence of a triethylamine catalyst. Then, the reaction for -PhOH → -PhOR' can be carried out in the same manner as in (1). (4) CH 2 =CHO(CH 2 )nX + HOCO(CH 2 )mPhOH → CH 2 =CHO(CH 2 )nOCO(CH 2 )mPhOH (X: halogen atom) Synthesis can be carried out as a condensation reaction of ω-halogenoalkyl vinyl ether such as 2-chloroethyl vinyl ether with 4-hydroxybenzoic acid or 4-hydroxyphenylacetic acid in the presence of an aqueous solution of sodium hydroxide as a catalyst. Then, the reaction for -PhOH → -PhOR' can be carried out in the same manner as in (1). (5) CH 2 =CHPh(CH 2 )nX + HOCO(CH 2 )mPhOH → CH 2 =CHPh(CH 2 )nOCO(CH 2 )mPhOH (X: halogen atom) Synthesis can be carried out as a condensation reaction of halogenoalkylstyrene such as p-chloromethylstyrene with 4-hydroxybenzoic acid or 4-hydroxyphenylacetic acid in the presence of a triethylamine catalyst. Then, the reaction for -PhOH → -PhOR' can be carried out in the same manner as in (1). These copolymers can be each further copolymerized with other vinyl monomers, olefin monomers, diene monomers, to such an extent as not to deteriorate characteristics of the resulting copolymers (e.g. not more than 40% by weight, preferably not more than 20% by weight, on the basis of the resulting copolymer). The other vinyl monomers include, for example, alkoxyalkyl acrylates having an alkoxyalkyl group having 2 to 8 carbon atoms, such as methoxymethyl acrylate, ethoxymethyl acrylate, 2-methoxyethyl acrylate, 2-ethoxyethyl acrylate, 2-butoxyethyl acrylate, cyanoalkyl acrylate, vinyl chloride, vinylidene chloride, acrylonitrile, styrene, vinyl acetate, ethyl vinyl ether, alkyl methacrylate, furfuryl acrylate, 2-acetoxyethyl acrylate, 2-propoxyethyl acrylate, 4-acetoxybutyl acrylate, 4-propoxybutyl acrylate, ethylene glycol dimethacrylate. Furthermore, the copolymers can be each copolymerized with a cross-linkable group-containing vinyl monomer such as vinyl monochloroacetate, glycidyl methacrylate, acrylic acid or vinylsilyl group-containing acrylate. The olefin monomers include, for example, ethylene, propylene, and the diene monomers include, for example, divinylbenzene, isoprene, pentadiene or ethylidene-norbornene. Copolymerization reaction can be carried out in the presence of an ordinary radical polymerization initiator by any one of emulsion polymerization, suspension polymerization, solution polymerization or bulk polymerization, preferably by emulsion polymerization. A redox polymerization initiator can be also used. In the resulting acrylic copolymer elastomer, 50 to 90% by weight of the unsaturated ester compound is copolymerized at a degree of polymerization of, for example, 90%. The acrylic copolymer elastomer has a Mooney viscosity (100°C) of generally 10 to 100 pts, preferably 20 to 60 pts. The acrylic copolymer elastomer (acrylic rubber) is blended with a fluorine-containing elastomer (fluorine rubber) in a blend ratio of acrylic rubber to fluorine rubber of 90 to 10 : 10 to 90% by weight, preferably 80 to 20 : 20 to 80% by weight, the sum total being 100% by weight. The blend rubber within the above-mentioned ratio range shows an intermediate heat resistance between the heat resistance of acrylic rubber and that of fluorine rubber, and also has a good amine resistance. Blending can be carried out by any of a kneading method using an open roll or a mixer, a method of mixing in a latex state and then coprecipitation by salting-out and a method of mixing in a solution state and solvent removal. The fluorine-containing elastomer for use in the blending is vinylidene fluoride copolymer rubbers including, for example, terpolymer rubber of vinylidene fluoride - hexafluoropropene - tetrafluoroethylene, copolymer rubber of vinylidene fluoride - hexafluoropropene, terpolymer rubber of vinylidene fluoride - tetrafluoroethylene - chlorotrifluoroethylene, copolymer rubber of vinylidene fluoride - chlorotrifluoroethylene, terpolymer rubber of vinylidene fluoride - tetrafluoroethylene - propylene. Besides, copolymer rubber of tetrafluoroethylene - propylene can be also used. These fluorine-containing elastomers may be copolymer elastomers obtained by copolymerization in the presence of a saturated or unsaturated compound containing at least one of bromine and iodine. The thus obtained blend rubber can be made into a vulcanizable blend rubber composition by adding thereto (1) a vulcanizing system comprising a quaternary onium salt and an acid acceptor, (2) a vulcanizing system comprising a tertiary sulfonium salt and an acid acceptor, or (3) a vulcanizing system comprising a tertiary phosphine compound, an epoxy compound and an acid acceptor. As a quaternary onium salt, 0.1 to 30 parts by weight, preferably 1 to 20 parts by weight, of at least one of an ammonium salt and a phosphonium salt represented by the following general formula can be used per 100 parts by weight of blend rubber. Below 0.1 parts by weight, no vulcanization products having desired properties can be obtained, whereas above 30 parts by weight vulcanization products have a smaller stretchability and are less practical: (R 1 R 2 R 3 R 4 N) + X - (R 1 R 2 R 3 R 4 P) + X - where R 1 to R 4 are each an alkyl group having 1 to 25 carbon atoms, an alkoxy group, an aryl group, an alkylaryl group, an aralkyl group or a polyoxyalkylene group, or two or three of which may form a heterocyclic structure together with P or N; and X - is an anion such as Cl - , Br - , I - , HSO 4 - , H 2 PO 4 - , RCOO - , ROSO 2 - , RSO - , ROPO 2 H - or CO 3 -- . Specifically, the quaternary onium salt includes, for example, quaternary ammonium salts such as tetraethylammonium bromide, tetrabutylammonium chloride, tetrabutylammonium bromide, tetrabutylammonium iodide, n-dodecyltrimethylammonium bromide, cetyldimethylbenzylammonium chloride, methylcetyldibenzylammonium bromide, cetyldimethylethylammonium bromide, octadecyltrimethylammonium bromide, cetylpyridinium chloride, cetylpyridinium bromide, cetylpyridinium iodide, cetylpyridinium sulfate, 1-benzylpyridinium chloride, 1-benzyl-3,5-dimethylpyridinium chloride, 1-benzyl-4-phenylpyridinium chloride, 1, 4-dibenzylpyridinium chloride, 1-benzyl-4-(pyrrolidinyl)pyridinium chloride, 1-benzyl-4-pyridinopyridinium chloride, tetraethylammonium acetate, trimethylbenzylammonium benzoate, trimethylbenzylammonium-p-toluene sulfonate, trimethylbenzylammonium borate, 8-benzyl-1,8-diazabicyclo [5, 4, 0]-undec-7-enium chloride, 1,8-diazabicyclo [5, 4, 0]-undecen-7-methylammonium methosulfate, 5-benzyl-1,5-diazabicyclo[4, 3, 0] -5-nonenium chloride, 5-benzyl-1,5-diazabicyclo-[4, 3, 0] -5-nonenium bromide, 5-benzyl-1,5-diazabicyclo[4, 3, 0]-5-nonenium tetrafluoroborate or 5-benzyl-1,5-diazabicyclo[4, 3, 0]-5-nonenium hexafluorophosphate, and quaternary phosphonium salts such as tetraphenylphosphonium chloride, triphenylbenzylphosphonium chloride, triphenylbenzylphosphonium bromide, triphenylmethoxymethylphosphonium chloride, triphenylmethylcarbonylmethylphosphonium chloride, triphenyl ethoxycarbonylmethyl phosphonium chloride, trioctylbenzylphosphonium chloride, trioctylmethylphosphonium bromide, trioctylethylphosphonium acetate, trioctylethylphosphonium dimethyl phosphate, tetraoctylphosphonium chloride or cetyldimethylbenzylphosphonium chloride. As a tertiary sulfonium salt, 0.1 to 10 parts by weight, preferably 0. 5 to 5 parts by weight, of at least one of phosphonium salts, represented by the following formula, preferably aromatic sulfonium salts, is used per 100 parts by weight of blend rubber. Below 0.1 parts by weight no vulcanization products having desired properties can be obtained, whereas above 10 parts by weight vulcanization products have a smaller stretchability and are less practical: where R 1 , R 2 and R 3 are an aryl group having 4 to 20 carbon atoms or an alkyl group having 1 to 20 carbon atoms, and at least one of which is an aryl group; Z is O, S, S=O, C=O, SO 2 , NR(where R is an aryl group or an acyl group), C-C or CR 4 R 5 (where R 4 and R 5 each are H, a lower alkyl group or an alkenyl group having 2 to 4 carbon atoms); n is 0 or 1; and X - is such an anion as a chloride ion, a bromide ion, a sulfate ion, a bisulfate ion, a nitrate ion, a hydroxy ion, a perchlorate ion, a trifluoromethane sulfonate ion, an acetate ion, a benzene sulfonate ion, a phenate ion, a tetrafluoroborate ion, a hexachlorophosphate ion, hexafluorophosphate ion, a hexachlorostannate ion, a hexafluoroarsenate ion, or a hexafluoroantimonate ion. Specifically, the aromatic sulfonium salt includes, for example, triphenylsulfonium chloride, methyldiphenylsulfonium tetrafluoroborate, triphenylsulfonium hexafluorophosphate, triphenylsulfonium sulfate, diphenylnaphthylsulfonium trifluoromethane sulfonate, tritolylsulfonium nitrate, anisyldiphenylsulfonium hexafluoroantimonate, 4-butoxyphenyldiphenylsulfonium tetrafluoroborate, 4-chlorophenyldiphenylsulfonium acetate, tris (4-phenoxyphenyl) sulfonium hexafluorophosphate, di(4-ethoxyphenyl)methylsulfonium hexafluoroarsenate, 4-acetoxy-phenyldiphenylsulfonium carbonate, tris (4-thiomethoxyphenyl)sulfonium hexafluorophosphate, di(methoxysulfonylphenyl)methylsulfonium chloride, di(methoxynaphthyl)methylsulfonium tetrafluoroborate, tris(carbomethoxyphenyl)sulfonium hexafluorophosphate, 4-acetamidophenyldiphenylsulfonium perchlorate or methyl(n-butylphenothiazinyl) sulfonium bromide. Preferably, triphenylsulfonium chloride is used. The tertiary phosphine compound for use in the present invention is represented by the following general formula: PR 1 R 2 R 3 , where R 1 , R 2 and R 3 are each a hydrocarbon group, for example, an alkyl group having 1 to 20 carbon atoms, an aryl group such as a phenyl group, an aralkyl group such as a benzyl group, or an alkoxyl group having 1 to 20 carbon atoms. Specifically, the tertiary phosphine compound includes, for example, trimethylphosphine, triethylphosphine, tributylphosphine, trioctylphosphine, triphenylphosphine, triethyl phosphite, tributyl phosphite or tridecyl phosphite. Preferably, triphenylphosphine is used. The epoxy compound for use together with the tertiary phosphine compound includes, for example, various monofunctional or multifunctional epoxy compounds such as styrene oxide, 2-ethylhexylglycidyl ether, phenylglycidyl ether, divinylbenzene diepoxide, 2- (2, 3-epoxypropyl)phenylglycidyl ether, 2, 6-(2, 3-epoxypropyl)phenylglycidyl ether, vinylcyclohexene-3-diepoxide, ethylene glycol diglycidyl ether, phthalic acid diglycidyl ester, epoxide of bisphenol A - epichlorohydrin condensation type or triepoxypropyl cyanurate. Besides, epoxy compounds given in Examples which follow can be also used. 0.1 to 10 parts by weight, preferably 0.5 to 5 parts by weight, of each of the tertiary phosphine compound and the epoxy compound is used per 100 parts by weight of blend rubber. Below 0.1 parts by weight, no vulcanization products having desired properties can be obtained, whereas above 10 parts by weight vulcanization products have a smaller stretchability and are less practical. The tertiary phosphine compound and the epoxy compound are used in a ratio of the former to the latter of 1 : 0.5 to 2 by weight. When the epoxy compound is in a ratio of less than 0.5, no effective vulcanization can be obtained, whereas, when the epoxy compound is in a ration of higher than 2, vulcanization products have a smaller stretchability. Besides these quaternary onium salt, tertiary sulfonium salt or tertiary phosphine compound - epoxy compound, the blend rubber vulcanization system contains an acid acceptor as an essential component to provide a vulcanizable blend rubber composition. As an acid acceptor, 0.1 to 30 parts by weight, preferably 1 to 20 parts by weight, of at least one of oxides and hydroxides of metals of divalency or higher valency such as calcium hydroxide, magnesium oxide, zinc oxide, titanium oxide or lead oxide is used per 100 parts by weight of blend rubber. It is preferable that the vulcanization system further contains 0.1 to 5 parts by weight of aromatic carboxylic acid per 100 parts by weight of blend rubber. The aromatic carboxylic acid includes, for example, unsubstituted or substituted monocarboxylic acids or polycarboxylic acids such as benzoic acid, phthalic acid, terephthalic acid, methylbenzoic acid, chlorobenzoic acid, nitrobenzoic acid or hydroxybenzoic acid. Preferably, benzoic acid is used. These aromatic carboxylic acids can be also used as equimolar molecule compounds with the quaternary phosphonium salt (see JP-B-59-23577). It is known that when benzoic acid is added to a blend rubber of acrylic copolymer elastomer and fluorine-containing elastomer, the anti-scorching property can be improved (see JP-A-58-63740). In other words, the addition of benzoic acid shows an action to lower the cross-linking rate, whereas in case of blending the present acrylic copolymer elastomer with fluorine-containing elastomer, the addition of benzoic acid can effectively improve the cross-linking rate in contrast to the ordinary knowledge. The present blend rubber composition can contain, besides the above-mentioned essential components, other additives, such as a reinforcing agent, a filler, an antioxidant, a stabilizer, a plasticizer or a lubricant, if required and can be prepared by kneading with an open roll mixer, a Banbury mixer or a kneader, and vulcanized (cocross-linked) by press vulcanization (press cure) at a temperature of 150 to 220°C for one to 30 minutes and by gear oven vulcanization (post cure) at a temperature of 150 to 220°C for 2 to 70 hours. According to the present invention, cocross-linked vulcanization products having an intermediate heat resistance between the heat resistance of acrylic rubber and that of fluorine rubber and a good amine resistance can be provided by blending the present acrylic copolymer elastomer (acrylic rubber) with fluorine-containing rubber (fluorine rubber). BRIEF DESCRIPTION OF THE DRAWING Fig. 1 is a diagram showing vulcanization curves in Examples 48 and 49. PREFERRED EMBODIMENTS OF THE INVENTION The present invention will be described in detail below, referring to Examples. REFERENCE EXAMPLE 1 (Synthesis of 4-hydroxybenzyl acrylate) 1400g of methyl isobutyl ketone, 50g of 4-hydroxybenzyl alcohol and 40g of triethylamine were charged into a separable flask having a capacity of 3 liters, provided with a stirrer and a nitrogen gas feed tube, and deaerated for 30 minutes, and then 33g of acrylic acid chloride was dropwise added thereto at 3°C over 50 minutes. Then, stirring was continued at room temperature for 3 hours. After completion of the reaction, the reaction mixture was recovered by filtration. The filtrate was washed with 0.5N hydrochloric acid and with water, dehydrated over anhydrous sodium sulfate, and then subjected to silica gel column chromatography (eluent: n-hexane / ethyl acetate = 10 / 1 by volume) to obtain the desired fraction. By distilling off the methyl isobutyl ketone solvent from the fraction under reduced pressure, 15g of 4-hydroxybenzyl acrylate of the following chemical formula was obtained (yield: 26%): REFERENCE EXAMPLE 2 (Synthesis of 4-hydroxyphenetyl acrylate) Reaction was carried out in the same manner as in Reference Example 1, except that 55g of 4-hydroxyphenetyl alcohol was used in place of 4-hydroxybenzyl alcohol, and 21g of 4-hydroxyphenetyl acrylate of the following chemical formula was obtained (yield: 34%): REFERENCE EXAMPLE 3 (Synthesis of 4-acetoxybenzyl acrylate) 1400g of isopropyl ether, 100g of 4-hydroxybenzyl acrylate and 53g of pyridine were charged into a separable flask of the same type as used in Reference Example 1, and the flask inside gas was replaced with a nitrogen gas over 30 minutes, while ice cooling the flask. Then, 125g of acetic anhydride was dropwise added thereto at 3°C over 2 hours, and stirring was continued at room temperature for 3 hours. After completion of the reaction, the reaction mixture was washed with 0.5N hydrochloric acid and then with water. By distilling off isopropyl ether from the reaction mixture, 113g of 4-acetoxybenzyl acrylate of the following chemical formula was obtained (yield:91%): REFERENCE EXAMPLE 4 (Synthesis of p-trimethylsilyloxybenzyl acrylate) 1500g of methyl isobutyl ketone and 100g of 4-hydroxybenzyl acrylate were charged into a separable flask of the same type as used in Reference Example 1, and cooled to -5°C while replacing the flask inside gas with a nitrogen gas, and then 67g of trimethylchlorosilane was dropwise added thereto over one hour, and then stirring was continued for 2 hours. After completion of the reaction, the reaction mixture was washed with water and methyl isobutyl ketone was distilled off, whereby 83g of p-trimethylsilyloxybenzyl acrylate of the following chemical formula was obtained (yield: 59%): REFERENCE EXAMPLE 5 (Synthesis of p-hydroxybenzoyloxybutyl acrylate) 2000g of dichloromethane, 40.0g of 4-hydroxybenzoic acid, 39.6g of 4-hydroxybutyl acrylate and 0.05g of methoquinone were charged into a separable flask of the same type as used in Reference Example 1, and then a liquid mixture consisting of 54.0g of N,N'-dicyclohexylcarbodiimide, 5.9g of dimethylaminopyridine and 60g of dichloromethane was dropwise added thereto at room temperature over 4 hours, while replacing the flask inside gas with a nitrogen gas. After the same treatment as in Reference Example 1, 3.8g of p-hydroxybenzoyloxybutyl acrylate of the following chemical formula was obtained (yield: 5%): REFERENCE EXAMPLE 6 (Synthesis of vinyl p-hydroxybenzoyloxy acetate) 1500g of methyl isobutyl ketone, 69g of 4-hydroxybenzoic acid and 58.0g of triethylamine were charged into a separable flask of the same type as used in Reference Example 1, and heated to 80°C, while replacing the flask inside gas with a nitrogen gas, and then 57g of vinyl monochloroacetate was dropwise added thereto over 2 hours, and then stirring was continued for 6 hours. After completion of the reaction, the reaction mixture was washed with water and dehydrated over anhydrous sodium sulfate. After the same treatment as in Reference Example 1, 34.8g of vinyl p-hydroxybenzoyloxy acetate of the following chemical formula was obtained (yield: 60%): REFERENCE EXAMPLE 7 (Synthesis of p-hydroxybenzoyloxyethyl vinyl ether) Reaction was carried out in the same manner as in Reference Example 6, except that 45.3g of 2-chloroethyl vinyl ether was used in place of vinyl monochloroacetate and 280g of an aqueous 10% sodium hydroxide solution was used in place of triethylamine, whereby 29.6g of p-hydroxybenzoyloxyethyl vinyl ether of the following chemical formula was obtained (yield: 28%): REFERENCE EXAMPLE 8 (Synthesis of p-hydroxybenzoyloxymethylstyrene) Reaction was carried out in the same manner as in Reference Example 6, except that 72.4g of p-chloromethylstyrene was used in place of vinyl monochloroacetate. After completion of the reaction 3 liters of water was added to the reaction mixture and the precipitated powder was recovered therefrom and washed with n-hexane, whereby 36.2g of p-hydroxybenzoyloxymethylstyrene of the following chemical formula was obtained (yield: 30%): EXAMPLE 1 The following compounds were charged into a separable flask having a capacity of 3 liters, provided with a stirrer, a nitrogen gas feed tube and a depressurizing means: Ethyl acrylate 250g n-Butyl acrylate 250g HBAC of Reference Example 1 25g Sodium laurylsulfate 27.5g Water 750g After repetitions of deaeration and nitrogen gas replacemant to completely remove oxygen from the flask, a polymerization initiator mixture consisting of the following compounds was added thereto to start polymerization reaction at room temperature: Sodium hydrosulfite 0.05 g Sodium formaldehyde sulfoxylate 0.01 g t-Butyl hydroperoxide 0.025 g Then, the reaction was continued at 50°C for 6 hours until the polymerization conversion reached to 90%. The resulting latex was coagulated, thoroughly washed with water and dried, whereby acrylic copolymer elastomer A having Mooney viscosity (100°C) of 42 pts and a HBAC copolymerization ratio of 4.3% by weight (determined by 1 H-NMR) was obtained. EXAMPLES 2 TO 11 Copolymerization reaction was carried out in the same manner as in Example 1, using monomer charge compositions given in the following Table 1, and acrylic copolymer elastomers B to K were obtained. Example No. 2 3 4 5 6 7 8 9 10 11 [Monomer; g] Ethyl acrylate 250 250 250 250 250 250 250 250 250 250 n-Butyl acrylate 250 150 225 250 250 150 200 250 250 250 2-Methoxyethyl acrylate 100 Styrene 25 HBAC of Ref. Ex. 1 15 25 25 HPheAC of Ref. Ex. 2 25 AcOBAC of Ref. Ex. 3 25 TMSiOBAC of Ref. Ex. 4 25 HBOBAC of Ref. Ex. 5 25 HBOVAc of Ref. Ex. 6 25 HBOEVE of Ref. Ex. 7 25 HBOMSt of Ref. Ex. 8 25 [Copolymer elastomer] Abbreviation B C D E F G H I J K Mooney viscosity (pts) 42 42 38 32 40 33 34 37 35 40 Copoly. ratio of components of Ref. Ex. 1 to 8 (%) 2.7 4.2 4.0 4.1 2.4 2.6 3.2 4.0 3.7 3.1 COMPARATIVE EXAMPLE 1 Copolymerization reaction was carried out in the same manner as in Example 1, except that 10g of p-chloromethylstyrene was used in place of HBAC of Reference Example 1, whereby acrylic copolymer elastomer L having Mooney viscosity of 45 pts was obtained. COMPARATIVE EXAMPLE 2 Copolymerization reaction was carried out in the same manner as in Example 1, except that 15g of p-hydroxystyrene was used in place of HBAC of Reference Example 1. During the reaction yellow precipitates were observed on the latex surface just after the addition of the polymerization initiator mixture, and at the end of copolymerization reaction yellowish brown resinous precipitates were observed. The latex freed from the resinous precipitates was coagulated, thoroughly washed with water and dried, whereby acrylic copolymer elastomer M was obtained. It was observed by 1 H-NMR analysis of the thus obtained acrylic copolymer elastomer M that no benzene ring peak was observed around 7ppm and it was found that p-hydroxystyrene was not copolymerized. REFERENCE EXAMPLE 9 (Production of VdF-HFP-TFE terpolymer rubber) 1500ml of deionized water and 7.5g of ammonium perfluorooctanoate were charged into an autoclave having a capacity of 3 liters, and after the autoclave inside gas was thoroughly replaced with a nitrogen gas, the autoclave was pressurized to an inside pressure of 8 kg/cm 2 gauge with a feed gas mixture of vinylidene fluoride (VdF) / hexafluoropropene (HFP) / tetrafluoroethylehe (TFE) in a ratio of 22 / 66 / 12 by weight and then the autoclave inside temperature was elevated to 60°C with stirring. Then, 3.5g of ammonium persulfate dissolved in 50ml of deionized water was added thereto under pressure. Then, a supplementary gas mixture of VdF / HFP / TFE in a ratio of 39 / 46 / 15 by weight was added thereto until the autoclave inside pressure reached 10 kg/cm 2 gauge to start polymerization. Immediately after the start of polymerization reaction, the autoclave inside pressure started to decrease, and when the autoclave inside pressure was lowered to 9 kg/cm 2 gauge, the autoclave was repressurized to 10 kg/cm 2 gauge with the latter gas mixture. The polymerization reaction was continued for 5 hours, while maintaining the autoclave inside pressure at a pressure of 9 to 10 kg/cm 2 gauge likewise. Then, the unreacted gas mixture was purged from the autoclave to discontinue the reaction. The thus obtained latex was coagulated, thoroughly washed with water and dried, whereby fluorine-containing elastomer A having a molar composition ratio of VdF / HFP / TFE = 60 / 19 / 21 (determined by 19 F-NMR analysis) and a Mooney viscosity of 74 pts was obtained. REFERENCE EXAMPLE 10 In Reference Example 9, the feed gas mixture composition was changed to VdF / HFP in a ratio of 24.5 / 75.5 by weight and the supplementary gas mixture composition to VdF / HFP in a ratio of 63.5 / 36.5 by weight. Fluorine-containing elastomer B having a molar composition ratio of VdF / HFP = 78 / 22 and a Mooney viscosity of 92 pts was obtained. REFERENCE EXAMPLE 11 In Reference Example 9, the feed gas mixture composition was changed to VdF / HFP / TFE in a ratio of 27 / 57 / 16 by weight and the supplementary gas mixture composition to VdF / HFP / TFE in a ratio of 40 / 34 / 26 by weight. Furthermore, 4.4g of 1-bromo-2-iodoperfluoroethane was added to the reaction mixture under pressure before the addition of the aqueous ammonium persulfate solution. Fluorine-containing elastomer C having a molar composition ratio of VdF / HFP / TFE = 58 / 20 / 22 and a Mooney viscosity of 81 pts was obtained. REFERENCE EXAMPLE 12 In Reference Example 9, the feed gas mixture composition was changed to VdF / HFP / CTFE (chlorotrifluoroethylene) in a ratio of 43 / 55 / 2 by weight and the supplementary gas mixture composition to VdF / HFP / CTFE in a ratio of 73 / 25.5 / 1.5 by weight. Fluorine-containing elastomer D having a molar composition ratio of VdF / HFP / CTFE = 77 / 21.8 / 1.2 and a Mooney viscosity of 65 pts was obtained. EXAMPLE 12 Acrylic copolymer elastomer A and fluorine-containing elastomer A were mixed in a ratio of 50 : 50 by weight by open roll (roll method), whereby blend rubber A having a Mooney viscosity of 38 pts was obtained. EXAMPLE 13 Acrylic copolymer elastomer A and copolymer rubber of vinylidene fluoride / propylene (Aflus 200, trademark of a product made by Asahi Glass K. K., Japan) were mixed in a ratio of 50 : 50 by weight by roll method, whereby blend rubber B having a Mooney viscosity of 49 pts was obtained. EXAMPLES 14 TO 29 Blend rubbers C to R were prepared by latex method of mixing a copolymer latex at the production stage of acrylic copolymer elastomer (acrylic rubber) and a copolymer latex at the production stage of fluorine-containing elastomer (fluorine rubber) in such ratios as to provide desired ratios of the acrylic rubber to the fluorine rubber by weight, as given in the following Table 2, and stirring the mixture for 30 minutes, followed by coagulated, thorough washing with water and drying. Example No. Acrylic rubber (parts by weight) Fluorine rubber (parts by weight) Blend rubber Mooney viscosity (pts) 14 A 50 A 50 C 48 15 A 75 A 25 D 33 16 A 25 A 75 E 68 17 A 50 B 50 F 50 18 A 50 C 50 G 47 19 A 50 D 50 H 36 20 B 50 A 50 I 35 21 C 50 A 50 J 33 22 D 50 A 50 K 36 23 E 50 A 50 L 34 24 F 50 A 50 M 39 25 G 50 A 50 N 40 26 H 50 A 50 O 46 27 I 50 A 50 P 36 28 J 50 A 50 Q 42 29 K 50 A 50 R 37 COMPARATIVE EXAMPLES 3 TO 6 Blend rubbers S to V were prepared by blending acrylic copolymer elastomer L and fluorine-containing elastomer A or B in various ratios by weight by roll method (Comparative Example 3) or by latex method (Comparative Example 4 to 6). The blend ratios of the copolymer elastomers used and the Mooney viscosity of the resulting blend rubbers are shown in the following Table 3. Comparative Example 3 4 5 6 Acrylic rubber L (parts by weight) 50 50 75 25 Fluorine rubber A (parts by weight) 50 Fluorine rubber B (parts by weight) 50 25 75 Blend rubber S T U V Mooney viscosity (pts) 32 43 36 55 EXAMPLES 30 AND 31 Blend rubber A (roll method) 100 parts by weight (Ex. 30) Blend rubber B (roll method) 100 " (Ex. 31) Stearic acid 1 " Antioxidant (Nocrack CD, trademark of a product made by Ouchi-Shinko Kagaku K. K., Japan) 2 " MT carbon black 30 " Calcium hydroxide 5 " Magnesium oxide 2 " Benzyltriphenylphosphonium chloride 0.4 " The above components were kneaded by open roll and the resulting kneaded mixtures were subjected to press vulcanization (press cure) at 180°C for 10 minutes and then to gear oven vulcanization (post cure) at 180°C for 24 hours. Vulcanization products were subjected to determination or observation for the following items according to JIS K-6301. Physical properties: Measurement of hardness (Hs), 100% modulus (Mo 100), tensile strength (T B ) and elongation (E B ) Heat aging test: Measurement of changes in the physical properties of the vulcanization products before and after heating at 200°C for 70 hours Deterioration test with engine oil: Observation of occurrence of cracks on the test piece surface after dipping the test piece in engine oil (SG grade, 10W-30) at 175°C for 70 hours (used as a simple and practical evaluation method for amine resistance) EXAMPLES 32 In Example 30, blend rubber C (latex method) was used in place of blend rubber A and the amount of benzyltriphenylphosphonium chloride was changed to 3 parts of weight. EXAMPLES 33 TO 48 In Example 30, blend rubbers C to R were used in place of blend rubber A. EXAMPLE 49 In Example 48 using blend rubber R in place of blend rubber A of Example 30, a kneaded product further containing one part by weight of benzoic acid was subjected to vulcanization. Results of determination and tests of the vulcanization products in Examples 30 to 49 are shown in the following Table 4, where no crack occurrence was observed at all in the deterioration test with engine oil throughout the Examples, and vulcanization curves were deterimined at 180°C with JSR-III type curastometer as a measuring instrument in Examples 48 and 49, as shown in Fig.1. Ex. No. Blend rubber Hs (pts) Mo 100 (MPa) T B (MPa) E B (%) Hs change (pts) T B change (%) E B change (%) 30 A 50 1.4 6.3 330 +6 -14 -27 31 B 51 1.9 8.1 190 +6 +20 -40 32 C 50 1.6 6.4 340 +8 +20 -26 33 C 50 1.8 7.1 260 +4 +12 -20 34 D 40 0.7 3.2 540 +15 -29 -40 35 E 59 0.9 4.8 300 +6 +8 -20 36 F 52 1.6 6.3 280 +6 0 -29 37 G 50 0.9 5.5 350 +4 +9 -25 38 H 50 1.4 5.9 300 +8 +10 -40 39 I 50 1.8 6.9 270 +5 +2 -18 40 J 48 1.4 5.5 350 +9 -20 -29 41 K 51 2.1 5.3 300 +4 -25 +27 42 L 50 1.9 6.4 320 +4 +2 -6 43 M 48 1.3 6.0 420 +7 +12 -29 44 N 52 2.1 6.1 290 +4 +2 -10 45 O 49 1.6 6.2 350 +5 -3 -20 46 P 49 1.7 4.8 430 +7 +5 -19 47 Q 50 1.8 5.9 320 +4 +1 -8 48 R 50 1.8 6.1 300 +3 0 -15 49 R 53 2.2 6.5 260 +2 +5 -15 EXAMPLE 50 The following components were kneaded by open roll, and the resulting kneaded mixture was subjected to press vulcanization at 180°C for 15 minutes and then to gear oven vulcanization at 190°C for 24 hours. The vulcanization product was determined for physical properties and also subjected to heat aging test and deterioration test with engine oil in the same manner as in Example 30: Blend rubber R 100 parts by weight Stearic acid 1 " Antioxidant (Nocrack CD) 2 " FEF carbon black 25 " Calcium hydroxide 4 " Benzoic acid 0.5 " Triphenylphosphonium chloride (product made by Fulka Co.) 1 " EXAMPLES 51 TO 59 The following components were kneaded and the resulting kneaded mixtures were subjected to vulcanization, and the vulcanization products were subjected to determination of physical properties and tests in the same manner as in Example 50: Blend rubber R 100 parts by weight Stearic acid 1 " Antioxidant (Nocrack CD) 2 " FEF carbon black 25 " Calcium hydroxide 4 " Triphenylphosphine 4 " (product of Wako Junyaku (Exs. 51 to 58) K. K., Japan) " 2 " (Ex. 59) Epoxy compound (as given below) (Epoxy compound; Gly = glycidyl group) Example 51: Styrene oxide 2 parts by weight (product of Wako Junyaku K. K., Japan) Example 52: C 6 H 5 O(CH 2 CH 2 O) 5 Gly 2 " (Denacol EX-145, trademark of a product made by Nagase Sangyo K. K., Japan) Example 53: Dibromophenyl glycidyl ether 2 " (Denacol EX-147, trademark of a product made by Nagase Sangyo K. K., Japan) Example 54: CH 3 (CH 2 ) 11 O(CH 2 CH 2 O) 15 Gly 2 " (Denacol EX-171, trademark of a product made by Nagase Sangyo K. K., Japan) Example 55: Bisphenol A diglycidyl ether 4 " (Epikote 828, trademark of product made by Yuka-Shell epoxy K. K., Japan) Example 56: Epikote 828 2 " Example 57: GlyO [C 6 H 5 COOCH 2 CH(OH)CH 2 O]nC 6 H 5 COOGly 4 " (U-Quick 103, trademark of a product made by Ueno Seiyaku K. K., Japan) Example 58: Tris(2, 3-epoxypropyl)isocyanurate 4 " (TEPIC, trademark of a product made by Nissan Kagaku Kogyo K. K., Japan) Example 59: N, N, N', N' -tetraglycidyl-bis (p-aminophenyl)-methane 2 " (Epototo YH-434, trademark of a product made by Toto Kasei Kagaku Kogyo K.K., Japan) Results of determination of physical properties and tests in Examples 50 to 59 are shown in the following Table 5, where no crack occurrence was observed at all in the deterioration test with engine oil throughout the Examples. Ex. No. Hs (pts) Mo 100 (MPa) T B (MPa) E B (%) Hs change (pts) T B change (%) E B change (%) 50 63 3.2 7.9 340 +6 +3 -41 51 70 5.1 9.7 210 +2 +3 -23 52 65 3.3 7.5 270 +8 +24 -29 53 67 3.5 8.4 270 +4 +17 -26 54 63 2.7 6.2 250 +8 +36 -37 55 78 7.8 9.5 170 +4 +13 -38 56 72 5.5 9.1 220 +5 +5 -30 57 79 8.4 9.8 170 +3 +17 -32 58 73 6.7 9.6 130 +3 +5 -23 59 77 6.6 9.7 190 +2 -3 -17 COMPARATIVE EXAMPLE 7 The following components were kneaded and vulcanized in the same manner as in Example 30: Acrylic copolymer elastomer L 100 parts by weight Stearic acid 1 " Antioxidant (Nocrack CD) 2 " HAF carbon black 60 " Calcium hydroxide 5 " Magnesium oxide 2 " Bisphenol AF 1 " Benzyltriphenylphosphonium chloride 4 " COMPARATIVE EXAMPLE 8 The following components were kneaded and vulcanized in the same manner as in Example 30: Acrylic copolymer elastomer L 100 parts by weight Stearic acid 1 " Antioxidant (Nocrack CD) 2 " HAF carbon black 60 " 2,4,6-trimercaptotriazine 0.5 " Sodium stearate 2 " COMPARATIVE EXAMPLE 9 Fluorine-containing elastomer A 100 parts by weight MT carbon black 25 " Calcium hydroxide 5 " Magnesium oxide 2 " Bisphenol AF 2 " Benzyltriphenylphosphonium chloride 0.4 " The above components were kneaded and vulcanized in the same manner as in Example 30, except that the secondary vulcanization was carried out at 230°C for 24 hours. Results of determination of physical properties and tests in Comparative Examples 7 to 9 are shown in the following Table 6, where no crack occurrence was observed in the deterioration test with engine oil in Comparative Examples 7 and 8, but crack occurrence were observed in Comparative Example 9. COMPARATIVE EXAMPLES 10 TO 13 The following components were kneaded and vulcanized in the same manner as in Example 30: Blend rubber S 100 parts by weight (Comp. Ex. 10) Blend rubber T 100 " (Comp. Ex. 11) Blend rubber U 100 " (Comp. Ex. 12) Blend rubber V 100 " (Comp. Ex. 13) Stearic acid 1 " Antioxidant (Nocrack CD) 2 " MT carbon black 30 " Calcium hydroxide 5 " Magnesium oxide 2 " Bisphenol AF 1 " Benzyltriphenylphosphonium chloride 0.4 " Results of determination of physical properties and tests in Comparative Examples 10 to 13 are shown in the following Table 6, where no crack occurrence was observed at all in the deterioration test with engine oil throughout Comparative Examples 10 and 13. Comp.Ex.No. Hs (pts) Mo 100 (MPa) T B (MPa) E B (%) Hs change (pts) T B change (%) E B change (%) 7 48 0.4 5.1 460 +19 +4 -69 8 70 6.9 16.7 180 +11 -44 -44 9 72 4.1 11.6 310 +1 +1 -3 10 58 3.1 8.5 260 +7 -33 -28 11 57 2.8 8.1 250 +6 -37 -36 12 48 1.4 3.5 490 +17 +14 -49 13 70 1.3 8.6 330 +5 -42 -21 COMPARATIVE EXAMPLE 14 Acrylic copolymer elastomer M and fluorine-containing elastomer A were blended in a ratio of 50 : 50 by weight by roll method to prepare blend rubber W. The thus obtained blend rubber W was subjected to mixing, kneading and vulcanization in the same manner as in Example 30. No cross-linking reaction took place at all.

Claims: An acrylic copolymer elastomer which comprises a copolymer of an alkyl acrylate having an alkyl group having 1 to 8 carbon atoms and an unsaturated ester compound represented by the following general formula: (1) CH 2 =CRCOO(CH 2 )nPhOR', (2) CH 2 =CRCOO(CH 2 )nOCO(CH 2 )mPhOR', (3) CH 2 =CHOCO(CH 2 )nOCO(CH 2 )mPhOR' or (4) CH 2 =CHO(CH 2 )nOCO(CH 2 )mPhOR' where R is a hydrogen atom or a methyl group; R' is a hydrogen atom, an acyl group or a trialkylsilyl group; Ph is a phenylene group; n is an integer of 1 to 6; and m is 0 or an integer of 1 to 3. An acrylic copolymer elastomer according to Claim 1, wherein the copolymer has a Mooney viscosity (100°C) of 10 to 100 pts. A blend rubber, which comprises a copolymer of an alkyl acrylate having an alkyl group having 1 to 8 carbon atoms and an unsaturated ester compound represented by the following general formula: (1) CH 2 =CRCOO(CH 2 )nPhOR', (2) CH 2 =CRCOO(CH 2 )nOCO(CH 2 )mPhOR', (3) CH 2 =CHOCO(CH 2 )nOCO(CH 2 )mPhOR', (4) CH 2 =CHO(CH 2 )nOCO(CH 2 )mPhOR' or (5) CH 2 =CHPh(CH 2 )nOCO(CH 2 )mPhOR' where R is a hydrogen atom or a methyl group; R' is a hydrogen atom, an acyl group or a trialkylsilyl group; Ph is a phenylene group; n is an integer of 1 to 6; and m is 0 or an integer of 1 to 3, and a fluorine-containing elastomer. A blend rubber according to Claim 3, wherein the blend rubber comprises 90 to 10% by weight of the copolymer of alkyl acrylate and unsaturated ester compound and 10 to 90% by weight of the fluorine-containing copolymer, sum total being 100% by weight. A vulcanizable blend rubber composition, which comprises a blend rubber of Claim 3, a quaternary onium salt and an acid acceptor. A vulcanizable blend rubber composition according to Claim 5, wherein the quaternary onium salt is a quaternary ammonium salt. A vulcanizable blend rubber composition according to Claim 5, wherein the quaternary onium salt is a quaternary phosphonium salt. A vulcanizable blend rubber composition according to Claim 5, wherein the acid acceptor is an oxide or hydoxide of metal having divalency or higher valency. A vulcanizable blend rubber composition according to Claim 5, wherein an aromatic carboxylic acid or an equimolar molecule compound of an aromatic carboxylic with a quaternary phosphonium salt is further contained. A vulcanizable blend rubber composition according to Claim 9, wherein the aromatic carboxylic acid is benzoic acid. A vulcanizable blend rubber composition, which comprises a blend rubber of Claim 3, tertiary sulfonium salt and an acid acceptor. A vulcanizable blend rubber composition according to Claim 11, wherein the acid acceptor is an oxide or hydroxide of metal having divalency or higher valency. A vulcanizable blend rubber composition according to Claim 11, wherein an aromatic carboxylic acid or an equimolar molecule compound of an aromatic carboxylic with a quaternary phosphonium salt is further contained. A vulcanizable blend rubber composition according to Claim 13, wherein the aromatic carboxylic acid is benzoic acid. A vulcanizable blend rubber composition, which comprises a blend rubber of Claim 3, a tertiary phosphine compound, an epoxy compound and an acid acceptor. A vulcanizable blend rubber composition according to Claim 15, wherein the acid acceptor is an oxide or hydroxide of metal having divalency or higher valency.

Inventors: MORIYAMA IWAO, OKABE JUN, SAITO KUNIYOSHI, MORIYAMA, IWAO, OKABE, JUN, SAITO, KUNIYOSHI
Applicants: NIPPON MEKTRON KK, NIPPON MEKTRON, LTD.
Application year: 1996
Main classification: C08F220
IPC codes: C08F212, C08L19, C08L21, C08F216, C08F220, C08L33, C08L27, C08F218