Silicon containing charge transport compounds

Abstract: A silicon-containing charge transporting material represented by formula wherein A denotes an organic group derived from a charge transporting compound having an ionization potential within the range of 4.5-6.2 e V, which is a tertiary amine having a plurality of aromatic groups, R 1 is an alkylene group of 1-18 carbon atoms, R 2 is a monovalent hydrocarbon group or a halogen-substituted monovalent hydrocarbon group of 1-15 carbon atoms , Q is a hydrolyzable group; and n and p are each integers from 1-3.

Description: This invention is directed to new charge transporting substances used in electrophotographic organic photoconductor. Electrophotographic organic photoconductor utilizing organic photoconductive materials have been attracting attention from the standpoint of productivity, facility of material design, and safety. They have undergone various improvements and are widely in use. In recent years, the configuration referred to as function-separation type, in which the layer which generates electric charge and the layer which transports electric charge are separated, has been both proposed and applied. An electrophotographic organic photoconductor with this configuration has two layers. One layer is composed of the electric charge generating substance and an appropriate resin as binding agent. Another layer above is the charge transporting substance dispersed or dissolved in a binder resin. The layer containing the charge transporting substance often contains a charge transporting material, and a binder which is a thermoplastic resin such as a polycarbonate, polyester, acrylic, and polystyrene; or a thermosetting resin such as polyurethane or epoxy. In this latter case, it is necessary to apply a negative charge through a corona discharge device to the surface of the electric charge generating layer. However, this process generates ozone which causes degradation of the resin, reduces sensitivity, and reduces electrostatic chargeability of the resin. This leads to mechanical damage in the subsequent process of development, transfer of an image onto paper, and friction generated during cleaning. The reduction in properties of the organic photoconductor caused by such factors has been a persistent problem. Various studies have been conducted to solve these problems. For example, various attempts have been made to blend the polysiloxane resin with either a copolymer constituent or another resin, such as the use of a thermosetting polysiloxane resin as the charge transporting layer, JP-A 61-238062; the use of a protective layer containing a polysiloxane resin, JP-A 62-108260; the use of a protective layer of a thermosetting polysiloxane resin in which silica gel, urethane resin, and/or a fluoro resin have been dispersed, JP-A 4-346356; and the use of a resin in which a thermosetting polysiloxane resin has been dispersed as a protective layer or as an electric charge transporting material binder resin, JP-A 4-273252. Studies have also been made to improve the performance, extend the life, and improve the cleaning property of organic photoconductor by utilizing the properties of a polysiloxane. Polysiloxane resins possess characteristics such as transparency, ability to withstand dielectric breakdown, photostability, and low surface tension, which are not seen in other resins. But because they are incompatible with organic compounds, they are not used alone as the resin constituting the charge transporting material. Rather, polysiloxane resins are used to improve the quality of the resin making up the charge transporting material through copolymerization or blending. For polysiloxane resins to be used alone, as the binder making up the charge transporting layer, it is necessary that a charge transporting substance also be dissolved in the polysiloxane resin. Thus, the purpose of our invention is to provide a method of manufacturing such a charge transporting material which is uniformly dissolved in the polysiloxane resin, and which imparts an electric charge transporting property to the resin that is used in an electrophotographic organic photoconductor The invention provides a silicon-containing charge transporting material represented by formula A-[R 1 SiR 2 3-n Q n ] p wherein A denotes an organic group derived from a charge transporting compound having an ionization potential within the range of 4.5-6.2 e V, which is a tertiary amine having a plurality of aromatic groups, R 1 is an alkylene group of 1-18 carbon atoms, R 2 is a monovalent hydrocarbon group or a halogen-substituted monovalent hydrocarbon group of 1-15 carbon atoms , Q is a hydrolyzable group; and n and p are each integers from 1-3 and a method for its manufacture. R 1 is preferably an alkylene group of 2-18 carbon atoms. Our silicone-type charge transporting material is characterized in that it represents an aromatic substituted tertiary amine which has a plurality of aromatic groups, a silyl group which is hydrolyzable, and wherein the silyl group is introduced via a hydrocarbon group into an aromatic ring of at least one of the aromatic groups of the compound with the charge transporting properties having the ionization potential of 4.5-6.2 electron volts. Examples of the hydrolyzable group Q include hydroxyl, methoxy, ethoxy, butoxy, methylethylketoximo, diethylamino, acetoxy, propenoxy, and Cl. Of these groups, the hydroxyl and alkoxy groups, especially alkoxy groups with 1-6 carbon atoms, are preferable. Silicon-type charge transporting compounds according to our invention have an ionization potential of 4.5-6.2 eV. When the ionization potential is less than 4.5 eV, the silicon-type charge transporting material is easily oxidized and deteriorated making it undesirable. When the ionization potential exceeds 6.2 eV, injection of charge from the charge generating layer is inhibited, resulting in decreased sensitivity also making it undesirable. The ionization potential in our invention was measured by open-air photoelectric spectrometry using surface analyzer AC-1 manufactured by Riken Keiki™ Company. In the silicon-type charge transporting material provided by our invention, the organic silicon group is bonded to an electron-donor group via a hydrocarbon group. If it is bonded directly without hydrocarbon, the p electron of the aromatic group in the charge transporting material is affected by the p-d interaction effect with the d electron of silicon; and this changes the ionization potential from that of the base material. Bonding via a hydrocarbon group prevents this phenomenon and facilitates designing of our organic photoconductor. One method of introducing a hydrocarbon group between an aromatic ring and a silicon atom is to bond an unsaturated aliphatic group to at least one of the multiple aromatic rings in the charge transporting compound, with an alkoxysilane whose essential substituent for the silicon atom is hydrogen atom or an alkoxy group, by means of a hydrosilylation reaction. For example, the silicon-type charge transporting material manufactured by means of a hydrosilylation reaction between a vinyl group substituted onto an aromatic ring that is bonded to a nitrogen atom of an aromatic substituted tertiary amine, whose ionization potential is 4.5-6.2 eV, and an organic silicon compound with a hydrogen atom bonded to silicon. One method of introducing the vinyl group to the aromatic group is to first formylate the hydrogen atom or the methyl group on the aromatic ring, and finally convert the resulted aldehyde group to the vinyl group by the Wittig reaction. After this process, the hydrosilylation reaction can be employed. Another method starts with a saturated hydrocarbon group substituted on the aromatic group, e.g. a methyl group, which is brominated, e.g. bromomethylated, then a lithium complex is formed and the complex is reacted with a halogenated alkoxy silane. Our aromatically substituted tertiary amine , with an ionization potential of 4.5-6.2 eV may constitute any of the following compounds (Groups 1-18). Each of the eighteen groups is contained on a single page, and a total of 72 compounds are enumerated. In these formulae, and hereinafter, Me is methyl, Et is ethyl, Ph is phenyl, Bu is butyl, and Pr is propyl. Following are representative oxidation and ionization potentials for some (51) of the aromatic substituted tertiary amines (A), shown supra (72 total compounds). These oxidation and ionization potentials refer only to those specific compounds identified above by means of a reference numeral, such as 1A. 1A - Ionization potential: 5.7 eV 1B - Oxidation potential: 0.78 V Ionization potential: 5.42 eV 1C - Oxidation potential: 0.81 V Ionization potential: 5.45 eV 3A - Oxidation potential: 0.84 V Ionization potential: 5.47 eV 5A - Oxidation potential: 0.57 V lonization potential: 5.22 eV 5B - Oxidation potential: 0.75 V Ionization potential: 5.40 eV 5C - Oxidation potential: 0.76 V Ionization potential: 5.40 eV 5D - Oxidation potential: 0.86 V Ionization potential: 5.49 eV 6A - Oxidation potential: 0.76 V Ionization potential: 5.40 eV 6B - Oxidation potential: 0.79 V Ionization potential: 5.43 eV 6C - Oxidation potential: 0.75 V lonization potential: 5.40 eV 6D - Oxidation potential: 0.77 V Ionization potential: 5.41 eV 7A - Oxidation potential: 0.80 V Ionization potential: 5.44 eV 7B - Oxidation potential: 0.79 V Ionization potential: 5.43 eV 7C - Oxidation potential: 0.88 V Ionization potential: 5.51 eV 8A - Oxidation potential: 0.76 V lonization potential: 5.40 eV 8B - Oxidation potential: 0.74 V Ionization potential: 5.38 eV 8C - Oxidation potential: 0.77 V lonization potential: 5.41 eV 9A - Oxidation potential: 0.63 V Ionization potential: 5.28 eV 9B - Oxidation potential: 0.62 V Ionization potential: 5.27 eV 9C - Oxidation potential: 0.58 V Ionization potential: 5.22 eV 9D - Oxidation potential: 0.59 V Ionization potential: 5.23 eV 10A - Oxidation potential: 0.80 V Ionization potential: 5.44 eV 10B - Oxidation potential: 0.78 V Ionization potential: 5.43 eV 10C - Oxidation potential: 0.78 V Ionization potential: 5.43 eV 10D - Oxidation potential: 0.76 V Ionization potential: 5.41 eV 11A - Oxidation potential: 0.58 V Ionization potential: 5.23 eV 11 B - Oxidation potential: 0.58 V Ionization potential: 5.23 eV 11C - Oxidation potential: 0.63 V Ionization potential: 5.28 eV 11D - Oxidation potential: 0.77 V Ionization potential: 5.41 eV 12A - Oxidation potential: 0.83 V Ionization potential: 5.47 eV 12B - Oxidation potential: 0.83 V Ionization potential: 5.47 eV 12C - Oxidation potential: 0.84 V Ionization potential: 5.47 eV 12D - Oxidation potential: 0.83 V Ionization potential: 5.47 eV 13A - Oxidation potential: 0.83 V Ionization potential: 5.47 eV 13B - Oxidation potential: 0.85 V Ionization potential: 5.48 eV 13C - Oxidation potential: 0.74 V Ionization potential: 5.38 eV 13D - Oxidation potential: 0.80 V Ionization potential: 5.44 eV 14A - Oxidation potential: 0.83 V Ionization potential: 5.47 eV 14B - Oxidation potential: 0.84 V Ionization potential: 5.47 eV 14C - Oxidation potential: 0.72 V Ionization potential: 5.36 eV 14D - Oxidation potential: 0.73 V Ionization potential: 5.38 eV 14E - Oxidation potential: 0.81V Ionization potential: 5.45 eV 17A - Oxidation potential: 0.78 V Ionization potential: 5.43 eV 17B - Oxidation potential: 0.76 V Ionization potential: 5.40 eV 17C - Oxidation potential: 0.82 V Ionization potential: 5.46 eV 17D - Oxidation potential: 0.82 V Ionization potential: 5.45 eV 18A - Oxidation potential: 0.89 V Ionization potential: 5.52 eV 18B - Oxidation potential: 0.81 V Ionization potential: 5.45 eV 18C - Oxidation potential: 0.84 V Ionization potential: 5.47 eV 18D - Oxidation potential: 0.79 V Ionization potential: 5.43 eV There is no limitation as to which position on the aromatic ring of the tertiary amine that the alkoxysilane is introduced, nor is it necessary for alkoxysilane groups to be bonded to all aromatic rings. Such determinations are made by considering factors such as solubility in the polysiloxane resin. In this case, the method of introducing a vinyl group to an aromatic ring that is bonded to a nitrogen atom is to formylate the hydrogen or the methyl group substituted on the aromatic ring, and finally to convert the aldehyde group to the vinyl group by the Wittig reaction. It is also produced by means of the dehydrohalogenation between the hydrogen on a secondary amine and a halogenated aromatic group compound, which has been substituted by a vinyl group. The hydrogenated organic silicon compound which is able to react with the vinyl group bonded to an aromatic ring of the tertiary amine , with ionization potential of 4.5-6.2 eV, is a hydrogenated organic silicon compound whose substituents on the silicon atom in its molecule comprise at least one hydrogen atom. This compound is added to the vinyl group by a hydrosilylation reaction. Hydrogen, directly bonded to silicon, is an indispensable component of the hydrosilylation reaction to add to the vinyl group. Another indispensable component is a hydrolyzable group, such as an alkoxy group -OR 3 . R 3 of the alkoxy group is a relatively short chain, i.e., 1-6 carbon atoms, such as methyl, ethyl, propyl, butyl, amyl, and hexyl or, R 3 is a branched alkyl. The selection of R 3 depends on the intended use of the product, stability during hydrosilylation process, and the hydrolyzable properties desired. Integer n in formula (I) denotes the number of alkoxy groups substituted on silicon. When n is greater than 1, the hydrophilic property of the compound is improved. When there are several groups that are condensed, the compound also acts as a cross-linking agent; so the selection must be made taking into account the hardness of the resin, as a result of the crosslinking, as well as its hydrophilic property. Organic group R 2, other than hydrogen atom or alkoxy, which is directly bonded to the silicon atom, is selected according to the type of substituent on the silicon atom in the polysiloxane resin, and according to the various properties such as solubility in the resin, reactivity for hydrosilylation reaction, and other property adjustments of the polysiloxane resin. R 2 is an alkyl group such as methyl, ethyl, propyl, butyl, amyl, and hexyl; an alkenyl group such as vinyl or allyl; halogenated hydrocarbon groups; aryl group such as phenyl or tolyl; halongenated hydrocarbon groups such as chloromethyl, chloroethyl and and chloropropyl; and fluorohydrocarbon groups represented by trifluoropropyl, heptafluoropentyl, and nonafluorohexyl. If the substituent on silicon in the polysiloxane resin is methyl, the solubility is better if R 2 is also methyl. Our curable polysiloxane resin is a resin soluble in organic solvents, and primarily constituting silicon-type macromolecules known as MT resins, MQ resins, T resins, and polysilsesquioxanes. Methods of manufacturing such resins are known, such as the method described on Page 71 of "Silicon-Based Polymer Science", edited by John M. Ziegler and F. W. Gordon Fearon, ACS Series 224, The American Chemical Society (1990). The hydrosilylation reaction is conducted using a platinum catalyst or an organic peroxide catalyst. The platinum catalyst is a platinum compound used in standard hydrosilylation reactions and addition-type silicone rubbers; platinum chloride; chloroplatinic acid; platinum-olefin complexes; platinum-phosphine complexes; substances in which platinum is supported by a carrier, such as platinum/carbon, platinum/silica gel, and platinum/macromolecules. The quantity of platinum catalyst is that amount used conventionally. In terms of mole ratio, the quantity of platinum metal to alkenyl groups of electron-donor groups is within the range of 1/10 to 1/100,000. The hydrosilylation reaction temperature varies depending on the type of platinum catalyst used, its quantity, reaction group materials, and reaction conditions. However, from the standpoint of efficiency, it is desirable that the temperature be below the decomposition temperature of the platinum catalyst, i.e., below 200°C. In the case of an organic peroxide catalyst, the only limitation is that its half-life be above room temperature. Organic peroxides which are useful are radical polymerization initiators such as lauryl peroxide, butyl peroxide, and benzoyl peroxide. Products of hydrosilylation reactions are divided into two groups. In one group, the silicon atom is added to the alpha position of the vinyl group. In the other group, the silicon atom is added to the beta position of the vinyl group. The position depends on reaction conditions, such as the type of vinyl compound substituent and the type of catalyst used. In our invention, there is no adverse effect of a mixture on the alpha-additions and beta-additions in the hydrosilylation process. In fact, having a mixture is preferable since it prevents aggregation of electron hole transferring materials which tend to easily form aggregates. Practical Example 1 Synthesis of 4-[2-(triethoxysilyl) ethyl] triphenylamine and Synthesis of 4-(N,N-diphenylamino) benzaldehyde 101.4 g of triphenylamine and 35.5 mL of dimethyl formamide (DMF) were placed in a three-neck flask, and while stirring with cooling in ice water, 84.4 ml of phosphorus oxychloride was dropped into the flask. The temperature was raised to 95°C, and the mixture was reacted for 5 hours. The reaction solution was poured into 4l of warm water and stirred for 1 hour. The precipitate was then collected and washed in a 1:1 mixture solution of ethanol/water, and 4-(N,N-diphenylamino) benzaldehyde was obtained. The yield was 91.5 g (yield rate of 81.0%). Synthesis of 4-vinyltriphenylamine 14.6 g of sodium hydride and 700 ml of 1,2-dimethoxyethane were placed in a three-neck flask, and while stirring at room temperature, 130.8 g of tetramethylphosphonium bromide was added. After adding one drop of anhydrous ethanol, the mixture was reacted for 4 hours at 70°C. Then 100 g of 4-(N,N-diphenylamino) benzaldehyde was added to the mixture. The temperature was raised to 70°C, and the mixture was reacted for 5 hours. The reaction solution was filtered, and an ether extract of the precipitate and the filtrate were washed in water. Next, the ether solution was dehydrated with calcium chloride, the ether was removed, and the reaction mixture was obtained. This was recrystallized from ethanol, and a needle-form, lemon-yellow vinyltriphenylamine was obtained. The yield was 83.4 g (yield rate of 84.0%). Hydrosilylation of 4-vinyltriphenylamine 40 ml of toluene, 9.9 g (60 mmol) of triethoxysilane, and 0.018 mmol of a toluene solution of tris-(tetramethyldivinyldisiloxane) diplatinum (0, i.e., zero oxidation number of platinum in the molecule) were placed in a three-neck flask, and while stirring under room temperature, 20 ml of a toluene solution of 8.2 g of 4-vinyltriphenylamine was dropped into the flask. Upon completion of the addition of the drops, the mixture was stirred for 3 hours at 70 °C, then the solvent was removed under reduced pressure. As a result, a lemon-yellow oily substance of 4-[2-(triethoxysilyl) ethyl] triphenylamine was obtained. The amount obtained was 12.1 g (yield 91.7%). Practical Example 2 Synthesis of 4-[2-(methyldiethoxysilyl) ethyl] triphenylamine and Hydrosilylation of 4-vinyltriphenylamine 40 ml of toluene, 8.1 g of methyl diethoxy silane, and 0.018 mmol of a toluene solution of tris-(tetramethyldivinyldisiloxane) diplatinum (0) were placed in a three-neck flask, and while stirring under room temperature, 20 ml of a toluene solution of 8.2 g of 4-vinyltriphenylamine was dropped into the flask. Upon completion of the addition of the drops, the mixture was stirred for 3 hours at 70°C, then the solvent was removed under reduced pressure. As a result, a lemon-yellow oily substance of 4-[2-(methyldiethoxysilyl) ethyl] triphenylamine was obtained. The amount obtained was 11.2 g (yield 91.4%). Practical Example 3 Synthesis of 4,4',4"-tris-[2-(triethoxysilyl) ethyl] triphenylamine and Synthesis of tri-(4-formylphenyl) amine 50.7 g of triphenylamine and 53.3 ml of DMF were placed in a three-neck flask, and while stirring while cooling in ice water, 126.6 ml of phosphorus oxychloride was dropped into the flask. Upon completion of the addition of the drops, the mixture solution was reacted for 5 hours at 95°C, then poured into 5 I of warm water, and stirred for 1 hour. The precipitate was then collected by filtering and washed in a 1:1 mixture solution of ethanol/water. As a result, tris-(4-formylphenyl) amine was obtained in an amount of 65.3 g (yield 95.9%). Synthesis of tri-(4-vinylphenyl) amine 14.6 g of sodium hydride and 700 ml of 1,2-dimethoxy ethane were placed in a three-neck flask, and while stirring at room temperature, 130.8 g of tetramethyl phosphonium bromide was added. Anhydrous ethanol was then added by dripping, and after completion of dripping, a reaction was carried out for 4 hours at 70°C. The reaction mixture was then combined with 40.2 g of tri-(4-formylphenyl) amine, and the reaction was continued for 5 hours at 70°C. The reaction product was filtered. The filtrated cake was extracted with ethanol, and after being combined with the filtrate, was washed with water. After dehydrating the ether solution with calcium chloride, the ether was removed, and a reaction mixture was obtained. This mixture was twice recrystallized with ethanol. As a result, a needle-like lemon-yellow substance of tri-(4-vinylphenyl) amine was obtained. The amount obtained was 38.4 g (yield 97.3%). Hydrosilylation of tri-(4-vinylphenyl) amine 40 ml of toluene, 9.9 g (60 mmol) of triethoxysilane, and 0.018 mmol of a toluene solution of tris-(tetramethyldivinyldisiloxane) diplatinum (0) were placed in a three-neck flask, and while stirring under room temperature, 20 ml of a toluene solution of 3.3 g (13 mmol) of tri-(4-vinylphenyl) amine was dropped into the flask. Upon completion of the addition of the drops, the mixture was stirred for 3 hours at 70°C, then the solvent was removed under reduced pressure. As a result, a lemon-yellow oily substance of 4,4',4'-[2-(triethoxysilyl) ethyl] triphenylamine was obtained, and the amount obtained was 7.8 g (yield 80.6%). Practical Example 4 Synthesis of 4-[N,N-bis-(3,4-dimethylphenyl) amino]-[2-(triethoxysilyl) ethyl] benzene and Synthesis of N,N-bis-(3,4-dimethylphenyl) aminobenzene 38.5 g (166 mmol) of 4-iodo-o-xylene, 22.9 g (166 mmol) of anhydrous potassium carbonate, and 7.0 g of copper powder were added to 20 ml of nitrobenzene, and heat-refluxed for 8 hours while stirring. The mixture was cooled, filtered, and the filtrate was removed. The obtained reaction mixture was passed through a silica gel column, and N,N-bis-(3,4-dimethylphenyl) aminobenzene was obtained. The amount obtained was 15.7 g (yield rate of 69%). Synthesis of 4-[N,N-bis-(3,4-dimethylphenyl) amino] benzaldehyde 124.6 g of 4-[N,N-bis-(3,4-dimethylphenyl) amino] benzene and 35.5 ml of DMF were placed in a three-neck flask, and while stirring while cooling in ice water, 84.4 ml of phosphorus oxychloride was dropped into the flask. Upon completion of the addition of the drops, the mixture solution was reacted for 5 hours at 95°C, then poured into 4 l of warm water, and stirred for 1 hour. The precipitate was collected and washed in a 1:1 mixture solution of ethanol/water, and 4-[N,N-bis-(3,4-dimethylphenyl) amino] benzaldehyde was obtained. The amount obtained was 107.6 g (yield rate of 79.0%). Synthesis of 4-[N,N-bis-(3,4-dimethylphenyl) amino] styrene 12.1 g of sodium hydride and 580 ml of 1,2-dimethoxyethane were placed in a three-neck flask, and while stirring at room temperature, 108.5 g of tetramethyl phosphonium bromide was added. After adding one drop of anhydrous ethanol, the mixture was reacted for 4 hours at 70°C. 100 g of 4-[N,N-bis-(3,4-dimethylphenyl) amino] benzaldehyde was added to the reaction mixture, and the mixture was reacted for 5 hours at 70°C. The reaction solution was filtered, and an ether extract of the filtered cake and filtrate were washed in water. The ether solution was dehydrated with calcium chloride. The ether was removed and the reaction mixture was obtained. This was recrystallized twice with ethanol, and a needle-form of 4-[N,N-bis-(3,4-dimethylphenyl) amino] styrene was obtained. The amount obtained was 84.5 g (yield rate of 85.0%). Hydrosilylation of 4-[N,N-bis-(3,4-dimethylphenyl) amino] styrene 40 ml of toluene, 6.0 g of triethoxysilane, and 0.54 mmol of a toluene solution of tris-(tetramethyldivinyldisiloxane) diplatinum (0) were placed in a three-neck flask, and while stirring under room temperature, 20 ml of a toluene solution of 9.9 g of 4-[N,N-bis-(3,4-dimethylphenyl) amino] styrene was dropped into the flask. Upon completion of the addition of the drops, the mixture was stirred for 3 hours at 70°C. The solvent was removed under reduced pressure, and a lemon-yellow oil of 4-[N,N-bis-(3,4-dimethylphenyl) amino]-[2-(triethoxysilyl) ethyl] benzene was obtained. The amount obtained was 13.4 g (yield rate of 90.1%). Practical Example 5 Synthesis of 4-[N,N-bis-(3,4-dimethylphenyl)amino]-[2-(triethoxysilyl) ethyl] benzene and Hydrosilylation of 4-[N,N-bis-(3,4-dimethylphenyl) amino] styrene 40 ml of toluene, 6.0 g (37 mmol) of triethoxysilane, and 0.34 mmol of dichloro-( n -cycloocta-1,5-diene) platinum were loaded into a three-neck flask. While being stirred at room temperature, 20 ml of a toluene solution of 9.9 g of 4-[N,N-bis-(3,4-dimethylphenyl) amino] styrene was dropped into the flask. Upon completion of the addition of the drops, the mixture was stirred for 3 hours at 70°C. The solvent was removed under reduced pressure, and a lemon-yellow oily substance of 4-[N,N-bis-(3,4-dimethylphenyl) amino]-[2-(triethoxysilyl) ethyl] benzene was obtained. The amount obtained was 14.0 g (yield was 94.2%). Practical Example 6 Synthesis of 4-[3-(triethoxysilyl) propyl] triphenylamine)-(4-bromotriphenylamine) 8.0 g (45 mmol) of N-bromosuccinimide (NBS) and 10.0 g (41 mmol) of triphenylamine were loaded in a 200 ml three-neck flask and then 150 ml of N,N-dimethyl formamide was added. The components were stirred overnight at room temperature. N,N-dimethyl formamide was removed, and the solid substance obtained was extracted with carbon tetrachloride. Carbon tetrachloride was removed, and the reaction mixture was twice recrystallized with ethanol. As a result, a solid white substance of 4-bromotriphenylamine was obtained in an amount of 8.2 g (yield was 61.7%). Synthesis of 4-N,N-diphenylaminoallyl benzene A 300 ml four-neck flask was filled with 1.0 g (40 mmol) of magnesium metal and the flask was filled with nitrogen. Diethyl ether was added in an amount of 100 ml, and stirring was initiated. 30 ml of a diethyl ether solution of 8.6 g (27 mmol) of 4-bromotriphenylamine was slowly added by dripping into the stirred mixture. After the dropped amount reached 3 ml, refluxing was slowly started. In the course of refluxing, the addition of diethylether solution by dripping was continued. Upon completion of dripping, refluxing was carried out for another hour. A Grignard reagent solution obtained in the manner described above was cooled to room temperature, and combined with 40 ml of a diethylether solution of 2.1 g (27 mmol) of allyl chloride added slowly by dripping. Upon completion of dripping, the reaction mixture was refluxed for 2 hours, and allowed to cool. Ice-cold water was added in an amount of 50 ml, and hydrolysis was carried out. The ether layer was extracted, washed once with an aqueous saturated sodium bicarbonate solution, and twice with water. The product was dried with anhydrous sodium sulfate. After drying, diethylether was removed, and a white solid substance of 4-N,N-diphenyl aminoallyl benzene was obtained in an amount of 4.9 g (yield 63.2%). Hydrosilylation of 4-N,N-diphenylaminoallyl benzene 40 ml of toluene, 6.0 g (37 mmol) of triethoxysilane, and 0.54 mmol of a toluene solution of tris-(tetramethyldivinyldisiloxane) diplatinum (0) were loaded into a three-neck flask. While being stirred at room temperature, 20 ml of a toluene solution of 9.7 g (34 mmol) of 4-[N,N-diphenylaminoallyl benzene was dropped into the flask. Upon completion of addition of drops, the mixture was stirred for 3 hours at 70°C. The solvent was removed under reduced pressure, and a lemon-yellow oily substance of 4-[3-(triethoxysilyl) propyl] triphenylamine was obtained. The amount obtained was 10.7 g (yield was 70.1%). Practical Example 7 Synthesis of 4-[4-(triethoxysilyl) butyl] triphenylamine and Synthesis of 4-methyltriphenylamine 4.5 g (27 mmol) of diphenylamine, 11.0 g (51 mmol) of p-iodotoluene, 5.5 g (40 mmol) of anhydrous potassium carbonate, and 1.1 g of copper chips were added to 30 ml of o-dichlorobenzene. The mixture was subjected to heating and refluxing for 7 hours under stirring conditions. Upon completion of the reaction, the reaction solution was filtered, the filtrate was washed with a 3-5% aqueous solution of sodium thiosulfate, and then with saturated brine. After drying the organic layer with anhydrous sodium sulfate, the solvent was removed. The reaction mixture obtained was recrystallized with ethanol, and 4-methyltriphenylamine was obtained in an amount of 5.7 g (yield 81.4 %). Synthesis of 4-bromomethyltriphenylamine 6.9 g (39 mmol) of N-bromosuccinimide and 9.1 g (35 mmol) of 4-methyltriphenylamine were loaded in a 300 ml three-neck flask, and 100 m of carbon tetrachloride was added. The components were stirred overnight. Upon completion of the reaction, the reaction solution was cooled and then filtered. The solvent was removed. The reaction mixture obtained was recrystallized with ethanol. As a result, the substance 4-bromomethyltriphenylamine was obtained in an amount of 10.8 g (yield was 91.2%). Synthesis of 4-N,N-diphenylaminophenyl-1-butene A 200 ml four-neck flask was filled with 1.0 g (40 mmol) of magnesium metal, and the flask was filled with nitrogen. Diethyl ether was added in an amount of 100 ml, and stirring was initiated. 20 ml of diethyl ether solution of 9.1 g (27 mmol) of 4-bromomethyltriphenylamine was slowly added by dripping to the stirred mixture. After the dropped amount reached 5 ml, refluxing was slowly started. In the course of refluxing, addition of diethylether solution by dripping was continued. Upon completion of dripping, refluxing was carried out for another hour. A Grignard reagent solution obtained in the manner described above was cooled to room temperature, and combined with 20 ml of a diethylether solution of 2.1 g (27 mmol) of allyl chloride which was added slowly by dripping. Upon completion of dripping, the reaction mixture was refluxed for 2 hours, and the reaction was cooled. Ice-cold water was added in an amount of 50 ml, and hydrolysis was carried out. The ether layer was extracted, washed once with an aqueous saturated sodium bicarbonate solution, twice with water. The product was dried with anhydrous sodium sulfate. After drying, diethylether was removed, and a white solid substance of 4-N,N-diphenyl aminophenyl-1-butene was obtained in an amount of 5.5 g (yield 66.7%). Hydrosilylation of 4-N,N-diphenyl aminophenyl-1-butene 40 ml of toluene, 9.9 g (60 mmol) of triethoxysilane, and 0.018 mmol of a toluene solution of tris-(tetramethyldivinyldisiloxane) diplatinum (0) were placed in a three-neck flask. While stirring under room temperature, 20 ml of a toluene solution of 16.7 g (54.7 mmol) of 4-N,N-diphenylaminophenyl-1-butene was dropped into the flask. Upon completion of addition of the drops, the mixture was stirred for 3 hours at 70°C. The solvent was removed under reduced pressure. As a result, a lemon-yellow oily substance of 4-[4-(triethoxysilyl) butyl] triphenylamine was obtained. The amount obtained was 13.9 g (yield 83.2%). In view of the above, it can be seen that our invention provides an electron hole transfer material which allows practical application of low surface energy polysiloxane organic photoconductive resins that have excellent hardness and weather resistant properties, unattainable by conventional technique. The silicon-type electron hole transferring material provided by our invention can be used not only in electrophotographic processes, such as photocopiers and laser beam printers, but also as an electric charge transfer layer necessary in construction of organic electroluminescent elements.

Claims: A silicon-containing charge transporting material represented by formula A-[R 1 SiR 2 3-n Q n ] p wherein A denotes an organic group derived from a charge transporting compound having an ionization potential within the range of 4.5-6.2 e V, which is a tertiary amine having a plurality of aromatic groups, R 1 is an alkylene group of 1-18 carbon atoms, R 2 is a monovalent hydrocarbon group or a halogen-substituted monovalent hydrocarbon group of 1-15 carbon atoms , Q is a hydrolyzable group; and n and p are each integers from 1-3. The silicon-containing charge transporting material of claim 1, wherein the hydrolyzable group is an alkoxy group. The silicon-containing charge transporting material of any of claims 1 or 2, wherein the alkylene group R 1 is bonded directly to an aromatic group of the organic group A. A method for manufacturing a silicon-containing charge transporting material represented by formula A-[R 1 SiR 2 3-n Q n ] p wherein A denotes an organic group derived from a charge transporting compound having an ionization potential within the range of 4.5-6.2 e V, which is a tertiary amine having a plurality of aromatic groups, R 1 is an alkylene group of 1-18 carbon atoms, R 2 is a monovalent hydrocarbon group or a halogen-substituted monovalent hydrocarbon group of 1-15 carbon atoms , Q is a hydrolyzable group; and n and p are each integers from 1-3. by a) subjecting the substituent in the form of an unsaturated hydrocarbon group or some or all of the aromatic groups of the compound with charge transporting properties having an ionization potential within the range of 4.5-6.2 eV which is a tertiary amine having a plurality of aromatic groups to hydrosilylation with an organic silicon compound with a hydrogen atom bonded to silicon and at least one hydrolyzable group; or b) brominating the saturated hydrocarbon group on at least one aromatic group of the compound with charge transporting properties having an ionization potential within the range of 4.5-6.2 eV which is a tertiary amine having a plurality of aromatic groups, then forming a lithium complex and reacting the complex with a halogenated organic silicon compound bearing at least one hydrolyzable group. The method according to claim 4, wherein the hydrolyzable group is an alkoxy group.

Inventors: KUSHIBIKI NOBUO, TAKEUCHI KIKUKO, KUSHIBIKI, NOBUO, TAKEUCHI, KIKUKO, Kushibiki, Nobuo, Dow Corning Aisa, Ltd., Takeuchi, Kikuko, Dow Corning Aisa, Ltd.
Applicants: DOW CORNING ASIA LTD, DOW CORNING ASIA, LTD.
Application year: 1996
Main classification: C07F7
IPC codes: G03G5, C07F7, C08G77, C08L83