Neutral, high performance, durable low-e glass coating system, insulating glass units made therefrom, and methods of making same

Abstract: A sputter-coated layer system on a glass substrate particularly useful in insulating glass (IG) units, enables normal emissivity values (E n ) of 0.06 or less, good durability and neutral color. The layer system includes two layers of Si 3 N 4 combined with a sufficient amount of stainless steel sandwiching a layer of silver to achieve its unique low-E, neutral color, non-mirrorlike solar management properties.

Description: FIELD OF THE INVENTION This invention relates to coating systems for glass substrates which exhibit very low emissivity values and are substantially neutral in color. More particularly, this invention relates to glass articles, such as insulating glass units (e.g. doors and windows) which are provided with these coating systems, and methods of making them. BACKGROUND OF THE INVENTION The importance of sputter-coated glass layer systems for achieving solar management properties in many types of glass articles, such as architectural windows and doors, is now well established in commerce. In addition, the importance of using such layer systems in insulating glass units (known as "IG" units in the art) is equally well established. Examples of this latter use include multipaned windows and doors made up of at least two panes of glass sealed at their peripheral edges to form an insulating chamber therebetween. Such chambers, in this respect, are often made by evacuating the air from the chamber, heat sealing the glass panes at their edges and filling the chamber formed with a gas other than air, such as argon. Important to the acceptance of solar management glasses, including IG units, in the marketplace are the following characteristics which relate directly to the sputter-coated layer system employed: 1) the desired amount of visible transmittance coupled with an acceptable level of infrared radiation reflectance; 2) a non-mirror-like appearance (i.e. a low visible "reflectance" as defined below); 3) a substantially neutral visible reflected color when viewed from the glass side (i.e. a color falling within the range of from colorless to slightly blue); 4) resistance to weathering or other chemical attack, often referred to as "chemical durability" (this term is defined below); and 5) resistance to abrasion (often referred to as "mechanical durability", a term also defined below) during handling, particularly during the various steps necessary to produce an IG window or door from two or more sheets of glass, at least one of which has been pre-sputter-coated with the aforesaid layer system. In addition to these physical characteristics, the coating system employed must be economical to produce. If it is not, the ultimate product, such as in an IG unit, may become so expensive as to inhibit demand. It is well-known in the art that these desired characteristics often conflict when attempting to achieve them, and that, therefore, trade-offs often become necessary. For example, achievement of acceptable levels of transmittance or IR (infrared) reflection may have to be at the expense of durability (either chemical or mechanical, or both). In other trade-offs, undesirable colors and mirror-like windows (or doors) become unavoidable. In still further trade-offs, cost of production becomes a significant factor. Such problems create a need in the art for a new sputter-coated layer system which can achieve a better balance among these characteristics. In U.S. Patent No. 5,344,718 there are disclosed various excellent sputter-coated layer systems which achieve acceptably low values of emissivity (E), and thus are properly classified as a family of "Low-E" systems (i.e. a family of high IR reflectance coatings). In addition, such coating systems, as a family, generally exhibit durability characteristics which approach or equal those of pyrolytic coatings and thus are quite acceptable. Still further, these coatings, particularly in their preferred embodiments, exhibit high visible transmittance. At the same time they also exhibit a reasonably neutral color, ranging somewhat into the green side of blue which is, however, reasonably masked by the level of visible reflectance achieved to thereby appear substantially neutral. In addition, these visible reflectance characteristics are below 20% and thus also avoid an undesirable mirror-like appearance when viewed from either the inside or outside when used, for example, as a window or door. The family of layer systems disclosed in U.S. Patent No. 5,344,718 employs various layers of Si 3 N 4 and nickel or nichrome to sandwich one or more layers of IR reflecting metallic silver between them, in a selected order, thereby to achieve the desired end properties. The entire disclosure of this patent, including the "BACKGROUND" section thereof is incorporated herein by reference. Generally speaking this prior patent ('718) achieves its unique results by the use of a system comprised of five or more layers wherein from the glass outwardly the system comprises: a) an undercoat layer of Si 3 N 4 ; b) a layer of nickel or nichrome; c) a layer of silver; d) a layer of nickel or nichrome; and e) an overcoat layer of Si 3 N 4 . When the system consists essentially of these five (5) layers, the following thicknesses are generally employed: Layer Range (approx.) a (Si 3 N 4 ) 400Å - 425Å b (Ni or Ni:Cr) 7Å or less c (Ag) 95Å - 105Å d (Ni or Ni:Cr) 7Å or less e (Si 3 N 4 ) 525Å - 575Å When, in this prior patent ('718), more than five layers are employed, such as when two silver layers are employed, the system from the glass outwardly usually includes the following layers: glass/Si 3 N 4 /Ni:Cr/Ag/Ni:Cr/Ag/Ni:Cr/Si 3 N 4 , and the total thickness of the silver remains the same (e.g. 95Å - 105Å) such that each layer of silver itself is only about 50Å, to make up the total. While such systems as disclosed in this prior '718 patent constitute a significant improvement over then existing prior art systems, particularly those discussed in the "BACKGROUND" section of that patent; nevertheless, there remained room for improvement in the characteristic of "emissivity". For example, in the systems of the '718 patent, normal emissivity (E n ) was generally less than or equal to about 0.12 while hemispherical emissivity (E h ) was generally less than about 0.16. However, in practice, the lower limits realistically or commercially achievable were generally, for E n about 0.09 and for E h were about 0.12. Achievable sheet resistances (R s ) in this respect were generally from about 9-10 ohms/ sq. Inhibiting the achievement of better IR reflection (i.e. decreased "E" values) was the generally held belief that if the thickness of silver were increased to achieve higher IR reflectance (and thus lower "E" values) at least one or more of the following four detrimental effects would occur: (1) there would result a loss of durability; (2) the ultimate product would be too highly reflective, and thus become mirror-like; (3) the color would be driven to an unacceptably high purple or red/blue appearance; and/or (4) visible transmittance would become unacceptably low. Durability, both mechanical and chemical, is an important factor to achieve in architectural glass generally whether used as a monolithic sheet or, for example, when used in an IG unit. As aforesaid, the handling, assembling and sealing of IG units places a premium on mechanical durability, while the need to edge seal the panes to create an insulating chamber therebetween creates the need for chemical durability due primarily to the nature of the sealant which inevitably contacts the coating. Aesthetically, both mirror-like and purple color qualities may eliminate the marketability of any product exhibiting these characteristics. Loss of visible transmittance while undesirable, does not become truly objectionable until, in a monolithic sheet, it drops below about 70% and in an IG unit it drops below about 63%. However, in certain uses, particularly where low shading coefficients (i.e. less than about 0.6) are desired, transmittance may actually be too high, even though emissivity is reasonably low. Generally speaking, where shading qualities are desired (i.e. to lower air conditioning costs), monolithic visible transmittance should be kept below 75% and preferably below 73%, while in a typical IG unit visible transmittance should be about 65% to 68%. In partial confirmation of the above beliefs, is the rather complex layer system disclosed in U.S. Patent No. 5,302,449 as well as its presumed commercial counterpart in IG unit form, known as Cardinal 171 sold by Cardinal IG Company. The layer system as taught in this patent varies the thicknesses and types of materials in the layer stack to achieve certain solar management qualities, as well as employing an overcoat of an oxide of zinc, tin, indium, bismuth, or oxides of their alloys including the oxide of zinc stannate, to achieve abrasion resistance. In addition, the system employs one or two layers of gold, copper or silver to achieve its end results. When two layers of silver are used it is said that the first is between 100Å - 150Å and preferably about 125Å in thickness while the second, based thereon, is to be between 125Å - 175Å. When only one silver layer is employed, it is taught that its thickness is to be about 100Å - 175Å, and preferably 140Å. Nowhere does this patent disclose the use of nickel or nichrome, nor the use of silicon nitride as an element(s) in the stack arrangement. In actual commercial practice, the aforesaid Cardinal IG units have been found to achieve quite acceptable solar management properties including acceptable color characteristics and relatively good non-mirror-like visible reflectance (an example is reported hereinbelow for comparison). However, this otherwise quite acceptable system has been found lacking in chemical durability, and, as defined herein, may be said to lack chemical durability since it fails the prescribed boil test. While the precise reason for this is not known, the simple conclusion is that, as has been indicative of the prior art, sacrifices had to be made in at least one desirable characteristic, in order to achieve desirable levels of the others. In addition, due to the nature of the stack and elements used, the system is quite expensive to produce principally due to the number and thickness of the layers required to achieve the desired result. In the "BACKGROUND" section of the aforesaid '718 patent there is disclosed a further prior art architectural glass layer system which commercially has become known as Super-E III, a product of the Airco Corporation. This system, from the glass outwardly consists of the following layer stack: Si 3 N 4 /Ni:Cr/Ag/Ni:Cr/Si 3 N 4 It has been found in practice that in this Super-E III system the Ni:Cr alloy is 80/20 by weight Ni/Cr, respectively (i.e. nichrome), the two nichrome layers are reported as being 7Å thick, the Ag layer is specified as being only about 70Å thick [except that it is stated that the silver may be about 100Å thick], and the Si 3 N 4 layers are relatively thicker (e.g. 320Å for the undercoat and about 450Å for the overcoat). In reality, because of its thinness (i.e. about 70Å), the silver (Ag) layer has been found, in practice, to actually be rather semi-continuous in nature. While this coating achieved good "durability" (i.e. the coating was scratch resistant, wear resistant and chemically stable) and thus achieved an important measure of this characteristic as compared to pyrolytic coatings, for glass at about 3mm thick, E h is only about 0.20 - 0.22, and E n is about 0.14 - 0.17. Both of these emissivity values are rather high. In addition, sheet resistance (R s ) measures a relatively high 15.8 ohms/ sq. (the more acceptable value being about 10.5 or less). Thus, while both mechanical and chemical durability are found to be quite acceptable and its monolithic sheet visible transmittance was a rather high 76±1%, and while these coatings also proved to be compatible with conventional sealants used in IG units, its ability to handle IR radiation was less than desirable. In addition, its rather high monolithic visible transmittance of 76±1% made such a system rather undesirable when lower shading characteristics were required. Airco has followed its Super-E III system with what it has designated as its Super-E IV system. This system includes as its layer stack from the glass outwardly the following: Element Thickness (Å) Ti0 2 Approx. 300 NiCrN x Approx. 8 Ag Approx. 105 NiCrN x Approx. 8 Si 3 N 4 Approx. 425 This system is quite similar in performance to the Super-E III except that visible transmittance is higher (e.g. greater than 80%), emittance is lower (e.g. less than about 0.10) and shading coefficient is significantly higher (e.g. approx. 0.80). In addition, due to the use of TiO 2 as an undercoat, the system is expensive to produce. Another layer system, somewhat similar perhaps to Super-E III and IV, is reported in U.S. Patent No. 5,377,045. In the systems therein reported, a single silver layer (for example) is sandwiched between two nichrome layers which, in turn, are sandwiched between a lower layer of, for example, Ti0 2 or Si 3 N 4 doped with Zr; and an outer layer of Si 3 N 4 or Si 3 N 4 doped with Zr. The layer systems of this patent, in practice, are known to generally be of a purple color, have been found not to be chemically durable as defined by the below-described boil test, are not heat treatable, and have a rather high emissivity. According to this patent, in this respect, special sputtering techniques are said to be needed in order to reduce what is referred to as the "intrinsic stress" in one of the dielectric layers in order to achieve mechanical and chemical desirability according to the tests reported therein used to define these two characteristics. A significant improvement in the prior art is disclosed in our co-pending application Serial No. 08/356,515 filed December 15, 1994, now U.S. Patent No. US-A-5 514 476 (published on May 7, 1996), and entitled LOW-E GLASS COATING SYSTEM AND INSULATING GLASS UNITS MADE THEREFROM. The disclosure of this application is incorporated herein by reference. In this pending application there is disclosed a unique layer system comprised of a silver layer sandwiched between two nichrome layers which, in turn, are sandwiched between a lower and outer layer of Si 3 N 4 . By appropriate adjustment of layer thicknesses, the coating systems of that invention achieved advantageously low emissivities (i.e. E n <0.7, E h <0.075, R s <5.5 ohms/ sq. ). In addition, the reflectance characteristics (reflectance and extinction) made them quite acceptable (i.e. no mirrorlike appearance) for use in insulating glass units ("IG's"). The transmittance characteristics, as well, were in the appropriate range and the problem of undesirable purple color of past prior art systems was eliminated. While these layer systems were quite advantageous, it has been found that as one seeks to achieve even lower emissivity values (i.e. reduced infrared transmission, which is a principal object of many layer systems used in architectural and automotive glass), principally through the attempt to thicken the silver layer (the primary IR-reflecting layer), visible transmittance, color, and reflectance characteristics are adversely affected. For example, thickening of the silver layer has been found to severely decrease visible transmittance to below the acceptable 70% level. In addition, the glass side appearance of an article (e.g. IG unit) so coated with too thick a silver layer can often become highly purple and mirrorlike. Thus while the above system described in our aforesaid co-pending application achieved properties theretofore unachieved in combination by the prior art, there was still a need for improvement, if at all possible. In addition to the layer systems described above, other coatings containing silver and/or Ni:Cr as layers for infrared reflectance and other light management purposes have been reported in the patent and scientific literature. See, for example, the Fabry-Perot filters and other prior art coatings and techniques disclosed in U.S. Patent Nos. 3,682,528 and 4,799,745 (and the prior art discussed and/or cited therein). See also the dielectric, metal sandwiches created in numerous patents including, for example, U.S. Patent Nos. 4,179,181; 3,698,946; 3,978,273; 3,901,997; and 3,889,026 just to name a few. While such other coatings have been known or reported, it is believed that prior to our invention, none of these prior art disclosures teach or have achieved the ability to employ the highly productive sputter-coating process and, at the same time, achieve an architectural glass which not only approaches or equals the durability of pyrolytic coatings, but which also achieves excellent solar management qualities as well. In view of the above, it is apparent that there exists a need in the art for a sputter-coated layer system which optimizes rather than unduly sacrifices on a perceived priority basis, the above-described characteristics for coated glass sheets generally, and IG units more particularly, in an economical way. It is a purpose of this invention to fulfill this and other needs in the art which will become more apparent to the skilled artisan once given the following disclosure. SUMMARY OF THE INVENTION This invention achieves its purposes by the unexpected finding that by either admixing the layers of Si 3 N 4 in the layer system of our aforesaid co-pending application with stainless steel or optionally placing under these admixed layers an undercoat layer of Ti0 2 , a still further, unexpected lowering of emissivity can be achieved and, equally unexpectedly, the visible reflectance and color appearance of the article when viewed from the glass side remains non-mirrorlike and is substantially neutral (i.e. falls within the color range of truly neutral to only slightly blue), and remains chemically and mechanically durable, despite at times an increase in silver layer thickness. In certain embodiments the layer systems are heat treatable. As such, the layer systems of this invention find particular utility as layer systems in insulating glass units such as IG doors and windows, especially when such units are manufactured using heat sealing techniques. In one aspect of this invention then there is provided a sputter-coated glass article comprised of a glass substrate having on one of its planar surfaces, from the glass outwardly, a layer system including: a) a layer comprised of Si 3 N 4 and stainless steel, wherein the stainless steel is in an amount of about 0.5%-15% by weight of said layer; b) a layer of nickel or nichrome; c) a layer of silver; d) a layer of nickel or nichrome; and e) a layer comprised of Si 3 N 4 and stainless steel, wherein the stainless steel is in an amount of about 0.5%-15% by weight of said layer, wherein when the glass substrate has a thickness of about 2mm-6mm, the coated glass substrate has a normal emissivity (E n ) of about 0.06 or less, a hemispherical emissivity (E h ) of about 0.07 or less, a sheet resistance (R s ) of about 5.0 ohms/ sq. or less and has a substantially neutral visible reflected color when viewed from the glass side. In certain embodiments of this invention the layer system consists essentially of the above-described five (5) layers. In certain other embodiments of this invention the layer system further includes an undercoat of Ti0 2 . In both such embodiments, the relative thicknesses of the layers are adjusted so that in further preferred embodiments the layer system is "heat treatable" as this term is defined below. In certain further embodiments of this invention an aforesaid single sheet of glass of about 2mm-6mm having a layer system as contemplated by this invention on one of its planar surfaces, has the following reflectance and color coordinate characteristics: a) when viewed from the GLASS SIDE R G Y is about 8 to 18 a h is about -3 to +3 b h is about 0 to -15 and b) when viewed from the FILM SIDE R F Y is about 4 to 15 a h is about 0 to +8 b h is about -5 to -20 wherein RY is reflectance and a h , b h are the color coordinates as measured in Hunter units, Ill. C, 10° observer. In certain further embodiments of this invention a sheet of glass, provided on one of its surfaces with a layering system as above-described, is employed with at least one other sheet of glass such that each is substantially parallel to the other, but spaced therefrom and sealed at their peripheral edges to form an insulating chamber therebetween thereby to form an insulating glass unit useful as a window, door or wall wherein the layer system is located on surface 24 as shown in Figure 2 such that the reflectance and color coordinate characteristics when viewed from outside are: R G Y, about 14 to 20 a h , about -2 to +2 b h , about 0 to -10 and when viewed from inside are: R F Y, about 11 to 18 a h , about 0 to +4 b h , about 0 to -10 and the visible transmittance is at least about 61%. When the coating system is located on surface 26, the reflectance and color coordinates are reversed from that above, but the transmittance remains the same. The term "outside" as used herein means as observed by a viewer from outside the dwelling in which the coated glass sheet (i.e. IG unit) is employed. The term "inside" as used herein means the opposite of "outside", i.e. the side as observed by a viewer from inside the dwelling in which the unit is placed (e.g. from within a room of a house or office building looking toward the "outside"). As stated above, it is further contemplated by this invention that certain of the layer systems that are within the scope of this invention have the characteristic of being heat treatable. As used herein, the term "heat treatable" means that a layer system is capable of being subjected to at least one of the following conventional heating processes and not have its desired end-characteristics adversely affected thereby. The conventional heating processes contemplated are tempering, bending, heat strengthening or the heat sealing step(s) employed to seal two or more glass sheets together when forming an IG unit. In this latter instance, this may or may not include heating the glass stack sufficiently high to slump the edges of the glass sheets themselves. By having the characteristic of being heat treatable, a particular coating system of this invention may be chosen for a particular end use. For example, if the layer system is to be used in an automotive bent and/or tempered windshield, it will be one chosen so as to be capable of going through these processes. If useful in architectural windows requiring the same appearance in both untempered and tempered panes, as another example, then the coating is so chosen to achieve this result by being heat treatable via the tempering process. Of course, to be "heat treatable" the coating need only be capable of going through at least one, but not all, of the above-listed heat treatments. In this respect, certain coatings contemplated may or may not be capable of withstanding tempering, hardening or bending, but are still considered "heat treatable" if they can withstand the heat employed to seal an IG unit during its fabrication (either with or without glass slumping), particularly when the method of forming the IG unit includes the step of evacuating the air from (i.e. degassing) the insulating chamber during sealing and leaving the chamber in vacuum or refilling it with an inert gas such as argon. Thus in certain embodiments of this invention there is fulfilled yet another need in the art by providing: in a method of making an insulating glass unit comprised of at least two sheets of glass sealed at their peripheral edges to each other thereby to define at least one insulating chamber therebetween, the method including the steps of spacing the sheets apart, heating the sheets at an elevated temperature, and sealing the peripheral edges of the sheets to each other at or above the elevated temperature, the improvement comprising using on a planar surface of at least one of the glass sheets, a sputter-coated, heat treatable layer system according to this invention so located that the layer system is within the insulating chamber of the IG unit formed by sealing the glass sheet edges to one another. This invention will now be described with respect to certain embodiments thereof, along with reference to the accompanying illustrations, wherein: IN THE DRAWINGS Figure 1 is a partial side sectional view of an embodiment of a layer system according to this invention. Figure 1A is a partial side sectional view of another embodiment of a layer system according to this invention. Figure 2 is a partial cross-sectional view of an IG unit as contemplated by this invention; Figure 3 is a partial schematic perspective view of a house employing as a window, door and wall an IG unit such as illustrated in Figure 2; and Figure 4 is a partial cross-sectional schematized view of an embodiment of an IG unit in its pre-fabrication stage prior to evacuation and sealing as contemplated by this invention. DETAILED DESCRIPTION OF EMBODIMENTS OF THE INVENTION Certain terms are prevalently used in the glass-coating art, particularly when defining the properties and solar management characteristics of coated glass used in the architectural field. Such terms are used herein in accordance with their well-known meaning. For example, as used herein: Intensity of visible wavelength light, "reflectance" is defined by its percentage and is reported as R X Y (i.e. the Y value cited below in ASTM 308-85), wherein "X" is either "G" for glass side or "F" for film side. "Glass side" (e.g. "G") means, as viewed from the side of the glass substrate opposite that on which the coating resides, while "film side" (i.e. "F") means, as viewed from the side of the glass substrate on which the coating resides. When reported for an IG unit the subscript "G" denotes "outside" and "F" denotes "inside" (i.e. from "outside" the dwelling, or from "inside" the dwelling, as the case may be). Color characteristics are measured on the "a" and "b" coordinates. These coordinates are indicated herein by the subscript "h" to signify the conventional use of the Hunter method (or units) Ill. C, 10° observer, according to ASTM D-2244-93 "Standard Test Method for Calculation of Color Differences From Instrumentally Measured Color Coordinates" 9/15/93 as augmented by ASTM E-308-85, Annual Book of ASTM Standards, Vol. 06.01 "Standard Method for Computing the Colors of Objects by Using the CIE System". The terms "emissivity" and "transmittance" are well understood in the art and are used herein according to their well-known meaning. Thus, for example, the term "transmittance" herein means solar transmittance, which is made up of visible light transmittance, infrared energy transmittance, and ultraviolet light transmittance. Total solar energy transmittance is then usually characterized as a weighted average of these other values. With respect to these transmittances, visible transmittance, as reported herein, is characterized by the standard Illuminant C technique at 380 - 720 nm; infrared is 800 - 2100 nm; ultraviolet is 300 - 400 nm; and total solar is 300 - 2100 nm. For purposes of emissivity, however, a particular infrared range (i.e. 2,500 - 40,000 nm) is employed, as discussed below. Visible transmittance can be measured using known, conventional techniques. For example, by using a spectrophotometer, such as a Beckman 5240 (Beckman Sci. Inst. Corp.), a spectral curve of transmission is obtained. Visible transmission is then calculated using the aforesaid ASTM 308/2244-93 methodology. A lesser number of wavelength points may be employed than prescribed, if desired. Another technique for measuring visible transmittance is to employ a spectrometer such as a commercially available Spectragard spectrophotometer manufactured by Pacific Scientific Corporation. This device measures and reports visible transmittance directly. As reported and measured herein, visible transmittance (i.e. the Y value in the CIE tristimulus values, ASTM E-308-85) uses the Ill. C., 10° observer. "Emissivity" (E) is a measure, or characteristic of both absorption and reflectance of light at given wavelengths. It is usually represented by the formula: E = l - Reflectance film For architectural purposes, emissivity values become quite important in the so-called "mid-range", sometimes also called the "far range" of the infrared spectrum, i.e. about 2,500 - 40,000 nm., for example, as specified by the WINDOW 4.1 program, LBL-35298 (1994) by Lawrence Berkley Laboratories, as referenced below. The term "emissivity" as used herein, is thus used to refer to emissivity values measured in this infrared range as specified by the 1991 Proposed ASTM Standard for measuring infrared energy to calculate emittance, as proposed by the Primary Glass Manufacturers' Council and entitled "Test Method for Measuring and Calculating Emittance of Architectural Flat Glass Products Using Radiometric Measurements". This Standard, and its provisions, are incorporated herein by reference. In this Standard, emissivity is reported as hemispherical emissivity (E h ) and normal emissivity (E n ). The actual accumulation of data for measurement of such emissivity values is conventional and may be done by using, for example, a Beckman Model 4260 spectrophotometer with "VW" attachment (Beckman Scientific Inst. Corp.). This spectrophotometer measures reflectance versus wavelength, and from this, emissivity is calculated using the aforesaid 1991 Proposed ASTM Standard which has been incorporated herein by reference. Another term employed herein is "sheet resistance". Sheet resistance (R s ) is a well-known term in the art and is used herein in accordance with its well-known meaning. Generally speaking, this term refers to the resistance in ohms for any square of a layer system on a glass substrate to an electric current passed through the layer system. Sheet resistance is an indication of how well the layer is reflecting infrared energy, and is thus often used along with emissivity as a measure of this characteristic. "Sheet resistance" is conveniently measured by using a 4-point probe ohmmeter, such as a dispensable 4-point resistivity probe with a Magnetron Instruments Corp. head, Model M-800 produced by Signatone Corp. of Santa Clara, Calif. "Chemical durability" or "chemically durable" is used herein synonymously with the term of art "chemical resistance" or "chemical stability". Chemical durability is determined by boiling a 2"x5" sample of a coated glass substrate in about 500 cc of 5% HCl for one hour (i.e. at about 220°F.). The sample is deemed to pass this test (and thus the layer system is "chemically durable" or is deemed to have "chemical durability") if the sample's layer system shows no pinholes greater than about 0.003" in diameter after this one hour boil. "Mechanical durability" or "mechanically durable" as used herein is defined by one of two tests. The first test uses a Pacific Scientific Abrasion Tester (or equivalent) wherein a 2"x4"x1" nylon brush is cyclically passed over the layer system in 500 cycles employing 150 gm of weight, applied to a 6"x17" sample. In the other, alternative test, a conventional Taber abrader (or equivalent) is used to subject a 4"x4" sample to 300 revolutions of two C.S. 10F abrasion wheels each having attached a 500 gm weight. In either test, if no substantial, noticeable scratches appear when viewed with the naked eye under visible light, the test is deemed passed, and the article is said to be mechanically durable. Thicknesses of the various layers in the systems reported are measured by, and thus the term, "thickness" as used herein is defined by alternative techniques. In one technique, known optical curves, or, in the alternative, the use of a conventional needle ellipsometer (i.e. profilometer) is employed. In another and particularly advantageous technique, an "n & k" analyzer is used (n & k Technology, Inc., Santa Clara, California). This technique is believed to be generally described in U.S. Patent No. 4,905,170, along with the ability to determine the "n" (i.e. refractive index) and "k" (i.e. the coefficient of extinction) values of the film under investigation. The disclosure of this patent is incorporated herein by reference. Such procedures and techniques are well-known to the skilled artisan and thus need no further explanation, except to note that thicknesses reported and used herein are reported in angstrom units. Turning now to Figures 1 and 1A, there is shown a partial cross-sectional sketch of two embodiments of this invention. As can be seen, there is employed a conventional glass substrate 1 used in the architectural art. Such glass is preferably made by the conventional "float" process and thus is referred to as "float glass". The usual thickness thereof may be from about 2mm - 6mm. The composition of the glass is not critical, and may vary widely. Typically, the glass employed is one of the soda-lime-silica family of glass well-known in the glass art. The process and apparatus used to form the various layers on glass substrate 1 may be a conventional multi-chamber (multi-target) sputter-coating system such as is produced by Airco, Inc. In this respect, the preferred sputter-coating process for use herein is the same as that disclosed in U.S. Patent No. 5,344,718, the entire disclosure of which has been previously incorporated herein by reference. It is to be noted here that it is an aspect of this invention that its unique results are achieved through the use of conventional sputter-coating techniques without the need for special processes to relieve intrinsic stresses as reported in U.S. Patent No. 5,377,045 discussed above. Turning first to the layer system shown in Fig. 1, five layers (a)-(e) are employed. From the glass outwardly the layers and a preferred range of thicknesses, measured by the "n & k" technique above, for this particular embodiment are: layer ingredient thickness (Å) a Si 3 N 4 /SS about 200-600 b Ni or nichrome about 7-50 c silver about 115-190 d Ni or nichrome about 7-30 e Si 3 N 4 /SS about 50-600 In particularly preferred embodiments, the thicknesses of the layers are: layer thickness (Å) a about 400-500 b about 7-30 c about 140-170 d about 7-15 e about 400-600 In the five (5) layer embodiments represented by Fig. 1, particularly preferred thicknesses of the layers are about: layer thickness (Å) a 450 b 20 c 155 d 7 e 550 In sputter-coating the layers (a) and (e), silicon (Si) targets are preferably employed which have admixed with the Si, the desired amount of stainless steel (e.g. #316) to achieve the desired end amount in the film layer. By conducting the sputtering in nitrogen, Si 3 N 4 is formed and at least some of the chromium in the stainless steel forms chromium nitride. Optionally, aluminum may also be employed as a dopant in small amounts (e.g. 6% by wt.) for the purpose of keeping the target conductive. However, stainless steel also serves this purpose, and thus Al is not required to achieve the desired level of conductivity. In this respect, it is stated herein that, in general, the amount of stainless steel generally contemplated for use in each layer is about 0.5%-15% by weight of the film. Since the sputter process generally involves sputtering the Si, and stainless steel (and Al if optionally present) at approximately the same rate, the amount of each ingredient employed (if reasonably uniformly disbursed) in the target itself may be assumed to be with reasonable accuracy for the purposes of this invention, the resultant amount in the layer after sputter-coating (as confirmed by analysis). Thus when stating herein that a layer includes a certain weight percent of stainless steel, it generally means that it was about that amount that was employed in the target. Reference is now made to Fig. 1A where a six (6) layer embodiment of this invention is illustrated. Here the five top layers (a')-(e') are of the same ingredients as their counterpart layers (a)-(e) in Fig. 1. Added thereto, however, is undercoat layer UC of Ti0 2 such that the thicknesses of these layers are preferably about: layer thickness (Å) UC 100-400 a' 20-120 b' 7-50 c' 75-225 d' 7-30 e' 50-600 In certain preferred embodiments the layers have about the following thicknesses: layer thickness (Å) UC 200-250 a' 40-60 b' 7-30 c' 150-180 d' 7-15 e' 400-500 In the six (6) layer embodiments of Fig. 1A, in this respect, particularly preferred thicknesses are about: layer thickness (Å) UC 225 a' 50 b' 20 c' 165 d' 7 e' 450 As stated above, the unique use of stainless steel in the Si 3 N 4 layers has proven to give rise to a generic layer system (as represented by the examples of Figs. 1 and 1A) which, if provided on the planar surface of a monolithic sheet of glass (e.g. "float glass") having a thickness of about 2mm-6mm, produces a glass article having a normal emissivity (En) of about 0.06 or less, a hemispherical emissivity (E h ) of about 0.07 or less, a sheet resistance (R s ) of about 5.0 ohms/ sq. or less and exhibits a substantially neutral visible reflected color (i.e. from neutral to slightly blue) when viewed from the glass side. By choosing the appropriate thicknesses, the visible transmittance is at least about 70%, and the monolithic sheet may be rendered heat treatable as defined above. A typical range of reflectance and color coordinates for the embodiments of this invention using the thicknesses of monolithic glass sheet and layers as described above, are: GLASS SIDE R G Y, about 8 to 18 a h , about -3 to +3 b h , about 0 to -15 FILM SIDE R F Y, about 4 to 15 a h , about 0 to +8 b h , about -5 to -20 In preferred embodiments such characteristics are: GLASS SIDE R G Y, about 9 to 15 a h , about -1 to +3 b h , about -4 to -10 FILM SIDE R F Y, about 4 to 10 a h , about +3 to +7 b h , about -10 to -20 In the embodiments of Fig. 1 when the particularly preferred thicknesses above set forth for this five (5) layer embodiment are employed, the reflectance and color coordinates are: GLASS SIDE R G Y, about 10.2 a h , about 0.4 b h , about -4.7 FILM SIDE R F Y, about 4.6 a h , about 6.5 b h , about -15.8 In the embodiments of Fig. 1A when the particularly preferred thicknesses, above set forth for this six (6) layer embodiment are employed, the reflectance and color coordinates are: GLASS SIDE R G Y, about 11.0 a h , about 2.3 b h , about -8.8 FILM SIDE R F Y, about 6.0 a h , about 5.4 b h , about -17.5 Such a monolithic glass sheet so produced from clear float glass, has in fact been found to have a visible transmittance of about 76%, while the visible transmittance of the above-described particularly preferred five (5) layer system is about 71%. In both instances the layer system has been found to be heat treatable, mechanically durable, and chemically durable. While the amount of stainless steel may be varied to meet individual requirements, it has been found preferable in sputter-coating either the five layer or six layer embodiments of Fig. 1-1A to employ a silicon (Si) target having about 6% by weight stainless steel, and thus by the above-described assumption creating a layer with about 6% by weight stainless steel. It is also preferred in the practice of this invention when sputter-coating the two sandwiching nucleating layers b,d or b'd' for the silver layer c or c' to conduct that sputtering in a nitrogen environment if nichrome (e.g. 80/20, Ni/Cr by wt.) is employed, thereby to convert at least a portion of the chromium in the nichrome to a nitride. Similarly, of course, at least a portion of the chromium in the stainless steel will form a nitride when sputtering the Si/SS target in a nitrogen environment to form Si 3 N 4 (i.e. silicon nitride). As referenced above, Figure 2 illustrates, somewhat schematically, a typical IG unit in accordance with this invention. In order to differentiate the "inside" of the IG unit labelled "In" from its "outside" labelled "Out", the sun 9 is schematically presented. As can be seen such an IG unit is made up of "outside" glass pane 11 and "inside" glass pane 13. These two glass panes (e.g. 2mm - 6mm thick) are sealed at their peripheral edges by a conventional sealant 15 and desiccant strip 17. The panes are then retained in a conventional window or door retaining frame 19 (shown in partial schematic form). By sealing the peripheral edges of the glass sheets and replacing the air in chamber 20 with a gas such as argon, a typical, high insulating value IG is formed. Chamber 20 in this respect is typically about 1/2" in width. By employing the layer systems of this invention, as above-described, as layer system 22 on wall (i.e. inner planar surface) 24 of outside glass sheet 11 within the chamber 20, as illustrated, or alternatively on wall (i.e. inner planar surface) 26 of the inside glass sheet 13 within chamber 20 (not shown), a particularly unique, non-mirror-like IG unit is formed which is substantially neutral in color when viewed from either the inside or outside of the dwelling in which the IG unit is installed. In this respect, it is understood, of course, that Figure 2 illustrates only one embodiment of an IG unit in which the unique layer systems of this invention may be employed. In fact, the layer systems of this invention are available for use in a wide variety of IG units generally, including those having more than two panes of glass. Generally speaking, however, the IG units of the subject invention, when the layer system is located on the wall of either glass sheet within an insulating chamber of the IG unit, will typically have the following range of characteristics: Performance Characteristics Wall 24 Wall 26 Range Preferred Range Preferred Visible Transmittance (%) >61 70 >61 70 Reflection (%, visible, outside) 14-20 16 11-18 13 Reflection (%, visible inside) 11-18 13 14-20 16 Shading coefficient (S.C.) 0.45-0.60 0.53 0.55-0.69 0.63 Solar heat gain coefficient 0.38-0.58 0.45 0.47-0.60 0.55 U (Winter) [BTU/ft 2 /hr/°F] 0.23-0.28 0.25 0.23-0.28 0.25 U (Summer) [BTU/ft 2 /hr/°F] 0.23-0.28 0.25 0.23-0.28 0.25 Relative heat gain [BTU/ft 2 /hr/°F] 90-120 110 110-150 130 In this respect, in certain embodiments typical reflectance and color coordinates will fall within the following range when viewed from the outside or inside: OUTSIDE INSIDE R G Y about 14 to 20 R f Y about 11 to 18 a h about -2 to +2 a h about 0 to +4 b h about 0 to -10 b h about 0 to -10 and the visible transmittance is at least 61% and preferably at least 63%. In addition to the above characteristics, in certain preferred embodiments where the aforesaid particularly preferred five layer system represented by Fig. 1 (using the particularly preferred thickness listed above), the following performance characteristics are achieved if such a system is used in an IG unit with a 1/2" wide chamber 20 filled with Argon as those characteristics are computed according to the software program known as "WINDOW 4.1" from Lawrence Berkley Laboratories of Berkeley, California; and, in addition, using a Hitachi spectrophotometer to get input data for: (1) visible and solar transmittance; (2) solar reflection, film side and glass side; and (3) a Beckman infrared spectrophotometer to measure emittance. The WINDOW 4.1 program, 1988-1994 is a copyrighted program of the Regents of the University of California entitled "Fenestration Production Thermal Analysis Program." In like manner using the same technique of measurement, the following performance characteristics are achieved in the aforesaid system when the particularly preferred six layer system represented by Fig. 1A (using the particularly preferred thicknesses listed above) is the layer system on either Wall 24 or Wall 26 (Fig. 2) as noted below: In both these embodiments, the monolithic glass sheet may be subjected to both the boil test to determine chemical durability and the aforesaid Pacific Scientific Abrasion tester to determine mechanical durability. Both tests are passed for both embodiments. SPECIFIC EXAMPLES An Airco ILS-1600 research coater was employed to form the layer stacks of both Fig. 1 and Fig. 1A. This coater has the capability of employing either three or four targets (in the case of four targets, two at least must be by c-mag, e.g. Si and Ti). Here, for the embodiment of Fig. 1A, cathode #1 is titanium; cathode #2 is silicon with 5% Al and 6% #316 stainless steel admixed; cathode #3 is silver; and cathode #4 is nichrome (80/20 by weight Ni/Cr). As stated, cathode #1 and #2 may be in c-mag form. For the embodiment of Fig. 1, the titanium cathode is eliminated and the other three remain the same. The two layer stacks are formed on a monolithic, clear glass sheet of soda-lime-silica float glass having a thickness of 0.087 inches. The following coater settings are employed: (Five Layer System - Fig. 1) LAYER MATERIAL N 2 % Ar% PRESSURE (Torr) CATHODE POWER CATHODE VOLTAGE CATHODE AMPS % LINE SPEED No. OF PASSES 1 Silicon 50 50 4.0 x 10 -4 4.9 KW 483 V 10.5 A 42.5 9 2 Nichrome 50 50 3.1 x 10 -4 0.7 KW 387 V 2.0 A 100 1 3 Silver 0 100 5.7 x 10 -4 5.0 KW 498 V 5.0 A 100 1 4 Nichrome 50 50 3.1 x 10 -4 0.3 KW 344 V 1.0 A 100 1 5 Silicon 50 50 4.0 x 10 -4 4.9 KW 483 V 10.5 A 45 11 The thicknesses, measured by the "n & k" technique above-described, are: (Five Layer System - Fig. 1) (Six Layer System - Fig. 1A) Layer (Å) Layer (Å) UC 225 a 450 a' 50 b 21 b' 21 c 155 c' 166 d 7 d' 7 e 550 e' 450 The optical and electrical properties of each system are as follows: These two layer systems, as above described, are each formed into an IG unit of the type shown in Fig. 2 (coating on Wall 24, 1/2" Argon insulating chamber or vacuum chamber). Its optical, thermal and electrical properties (by applying the above-described WINDOW 4.1 technique) are: Six Layer Five Layer RY outside , 15.5 15.0 a h -0.2 -1.9 b h -2.6 -1.0 RY inside , 12.6 11.5 a n 0.9 2.0 b h -5.6 -4.9 Vis. Trans. 70.0 66.0 a h -2.4 -2.1 b h 1.5 4.8 Winter U-value 0.25 (Argon chamber), .26 0.05 (vacuum chamber) --- R value 4 (Argon chamber), 3.85 20 (vacuum chamber) --- Shading Coefficient 0.53 0.51 R s 4.8 4.7 E n 0.05 0.06 E h 0.06 0.07 The effect of the stainless steel on the optical and electrical properties is demonstrated by a comparison of the above five layer system characteristics (with 6% by wt. #316 stainless steel) with a duplicated five layer system of substantially the same thicknesses employing the same three targets, but in the duplicated system employing a Si target doped with 5% Al without any stainless steel admixed therein. Here, the coater settings for the duplicated, non-stainless steel layer system are: LAYER MATERIAL N 2 % Ar% PRESSURE (Torr) CATHODE POWER CATHODE VOLTAGE CATHODE AMPS % LINE SPEED No. OF PASSES 1 Silicon 80 20 2.0 x 10 -3 244 KW 429 V 569 A 175 1 2 Nichrome 80 20 2.0 x 10 -3 1.16 KW 312 V 3.7 A 175 1 3 Silver 0 100 2.0 x 10 -3 8.6 KW 382 V 22.5 A 175 1 4 Nichrome 80 20 2.0 x 10 -3 0.4 KW 350 V 1.1 A 175 1 5 Silicon 80 20 2.0 x 10 -3 322 KW 394 V 817 A 175 1 The optical and electrical properties of this duplicated monolithic five layer system (on the same glass substrate) without stainless steel are: As can be seen, the use of stainless steel creates a significant improvement in the characteristics of the glass article, particularly in the lowering of the E values, which, in the case of the six layer system, are even lower. By way of further comparison, and in contrast to the characteristics of the above two embodiments of this invention are the following characteristics by applying the above-described WINDOW 4.1 technique (1/2" Argon chamber) to the aforesaid prior art commercial IG product "Cardinal -171". It is to be pointed out, in this respect, that this Cardinal - 171 IG product has achieved significant commercial acceptability in the marketplace. Its only real drawback is its lack of chemical durability. Its precise layer stack system is not known. However, it is believed to be consistent with that as taught in the aforesaid U.S. Patent No. 5,302,449. As can be seen, by comparing the results of this invention with those of this already commercially accepted product, the subject invention has achieved a high level of competitiveness using a significantly different and less expensive layering system. For example, while the Cardinal product achieves a bit higher visible transmittance than the embodiment of the subject invention (73% vs. 70%), nevertheless this 70% is not only well within acceptable levels but, when lower shading coefficients as explained above, are desirable (e.g. to reduce air conditioning costs in hot weather), this 70% is more desirable commercially than the 73%. Of particular importance, however, is this invention's achievement of superior chemical durability. Both products have very low emissivities and substantially equal and excellent U values. With respect to the above-referenced IG performance characteristics not previously defined herein, such as U Winter , R value etc., those terms are well understood in the art and are used here in accordance with their accepted meaning. For example, the "U" value is a measure of the insulating property of the IG system. U Winter and U Summer are determined according to NFRC 100-91 (1991), a standard subsumed in the WINDOW 4.1 software. "Shading coefficient" ("S.C.") is determined in accordance with NFRC 200-93 (1993), by first determining "Solar heat gain coefficient" and dividing by 0.87. "Relative heat gain" (r.h.g.) is determined by this same NFRC 200-93 procedure. "T solar " means total solar energy transmittance, a known combination of UV, visible and IR transmittance. "R solar " similarly, means total solar reflectance, a known combination of UV, visible, and IR reflectance. Figure 3 is a partial schematic view of a typical family dwelling 28 having various portals in which the subject invention may be employed. For example, window 30 may employ either a monolithic sheet of glass having a layer stack of this invention thereon, or employ as a "storm window" an IG unit of this invention such as is illustrated in Figure 2. Similarly, sliding wall panel 32 or non-sliding wall panel 34 as well as front door panel 36 may be so constructed by employing this invention, either as a monolithic glass sheet or as an IG unit. Figure 4 is a schematic illustration of a typical two-pane IG unit stack prior to sealing. In certain embodiments of this invention, as stated above, the layer systems are heat treatable. In this Figure, the prestack employs two typical, clear float glass sheets 31 and 33 separated a selected distance (e.g. 0.1mm) by glass beads 35. Lower sheet 33, of slightly larger size than upper sheet 31, has a layer system 37 according to this invention sputter-coated onto its inner planar surface (optionally, the inner planar surface of sheet 31 may be used for the layer coating). A conventional sealant 39 (e.g. a low melting ceramic) is then provided in the peripheral area 41 defined by centering the smaller sheet 31 on the larger sheet 33. In conventional fashion, sufficient heat (e.g. approx. 500°C) is applied to flow sealant 39 to thereby create an insulating chamber 43. During this process a vacuum is applied to remove as much air and water vapor as is economically feasible, and optionally to either leave a vacuum or replace the air and water vapor with an inert gas such as Argon. In an alternative technique the edges of the glass are flame sealed, rather than using a sealant. In either instance, heat must be applied to create the seal and drive off the water vapor. Thus the heat treatable embodiments of this invention find unique applicability in IG units of the type shown in Fig. 4 wherein the layer system must be able to withstand the heat employed during sealing without adversely affecting its desired characteristics. In yet another alternative, a vacuum process is not employed and a spacing of 12.7 mm (1/2") for the chamber is effected by various known, conventional techniques. In such a process the insulating chamber is usually filled with Argon so as to displace the air and any water vapor (i.e. humidity or moisture) that might be present. Once given the above disclosure many other features, modifications and improvements will become apparent to the skilled artisan. Such other features, modifications and improvements are therefore considered to be a part of this invention, the scope of which is to be determined by the following claims:

Claims: A sputter-coated glass article comprised of a glass substrate having on a planar surface thereof, from the glass outwardly, a layer system including: a) a layer comprised of Si 3 N 4 and stainless steel wherein said stainless steel is in an amount of about 0.5%-15% by weight of said layer; b) a layer of nickel or nichrome; c) a layer of silver; d) a layer of nickel or nichrome; and e) a layer comprised of Si 3 N 4 and stainless steel, wherein said stainless steel is in an amount of about 0.5%-15% by weight of said layer, and wherein when said glass substrate has a thickness of about 2mm-6mm, said coated glass substrate has a normal emissivity (E n ) of about 0.06 or less, a hemispherical emissivity (E h ) of about 0.07 or less, a sheet resistance (R s ) of about 5.0 ohms/ sq. or less and having a substantially neutral visible reflected color when viewed from the glass side. A sputter-coated glass article according to claim 1 wherein said coated glass substrate has a visible transmittance of at least about 70%. A sputter-coated glass article according to claim 1 wherein said glass article is heat treatable. A sputter-coated glass article according to claim 1 wherein said layer system further includes an undercoat layer comprised of Ti0 2 , and the layers have about the following thicknesses: layer thickness (Å) undercoat 100-400 a 20-120 b 7-50 c 75-225 d 7-30 e 50-600 A sputter-coated glass article according to claim 4 wherein said glass substrate has a normal emissivity (E n ) of about 0.05 or less, a hemispherical emissivity (E h ) of about 0.06 or less, a sheet resistance (R s ) of about 5.0 ohms/ sq. or less. A sputter-coated glass article according to claim 5 consisting essentially of said undercoat layer and layers (a)-(e) and wherein said stainless steel in said layers (a) and (e) is in an amount of about 6% by wt. of said layer. A sputter-coated glass article according to claim 6 wherein the layers have about the following thicknesses: layer thickness (Å) undercoat 200-250 a 40-60 b 7-30 c 150-180 d 7-15 e 400-500 A sputter-coated article according to claim 7 wherein said layers (b) and (d) are comprised of chromium nitride, and said stainless steel is comprised of chromium nitride. A sputter-coated article according to claim 8 wherein the layers have about the following thicknesses: layer thickness (Å) undercoat 225 a 50 b 20 c 165 d 7 e 450 and wherein the glass substrate having said layer system thereon has the following characteristics: GLASS SIDE R G Y is about 11.0 a h is about 2.3 b h is about -8.8 FILM SIDE R f Y is about 6.0 a h is about 5.4 b h is about -17.5 wherein RY is the reflectance and a h and b h are the color coordinates as measured in Hunter units, Ill. C, 10° observer, and wherein said layer system is mechanically and chemically durable and has a visible transmittance of about 76%. A sputter-coated article according to claim 9 wherein said layer system is heat treatable. A sputter-coated glass article according to claim 1 wherein said layer system consists essentially of said layers (a)-(e) and said layers have about the following thicknesses: layer thickness (Å) a 200-600 b 7-50 c 115-190 d 7-30 e 50-600 A sputter-coated article according to claim 11 wherein the layers have about the following thicknesses: layer thickness (Å) a 400-500 b 7-30 c 140-170 d 7-15 e 400-600 A sputter-coated article according to claim 12 wherein said layer system is chemically and mechanically durable. A sputter-coated article according to claim 13 wherein said layers have about the following thicknesses: layer thickness (Å) a 450 b 20 c 155 d 7 e 550 and wherein said glass substrate having said layer system thereon has a visible transmittance greater than about 70%. A sputter-coated article according to claim 14 wherein said glass substrate having said layer system thereon has the following characteristics: GLASS SIDE R G Y is about 10.2 a h is about 0.4 b h is about -4.7 FILM SIDE R f Y is about 4.6 a h is about 6.5 b h is about -15.8 wherein RY is the reflectance and a h and b h are the color coordinates as measured in Hunter units, Ill. C, 10° observer. A sputter-coated article according to claim 15 wherein said layer system is heat treatable. A sputter-coated article according to claim 16 wherein said stainless steel in layers (a) and (e) is in an amount of about 6% by weight of said layer. A sputter-coated article according to claim 17 wherein said layers (b) and (c) are comprised of chromium nitride and said stainless steel is comprised of chromium nitride. A sputter-coated article according to claim 1 wherein said stainless steel is No. 316 stainless steel. A sputter-coated article according to claim 1 wherein said glass substrate having said layer system on one of the surfaces thereof has the following characteristics: GLASS SIDE R G Y is about 8 to 18 a h is about -3 to +3 b h is about 0 to -15 FILM SIDE R f Y is about 4 to 15 a h is about 0 to +8 b h is about -5 to -20 wherein RY is the reflectance and a h and b h are the color coordinates as measured in Hunter units, Ill. C, 10° observer. A sputter-coated article according to claim 20 wherein the glass side and film side characteristics are: GLASS SIDE R G Y is about 9 to 15 a h is about -1 to +3 b h is about -4 to -10 FILM SIDE R f Y is about 4 to 10 a h is about +3 to +7 b h is about -10 to -20. A sputter-coated article according to claim 1 wherein said visible transmittance of said coated glass substrate is about 74%-76%. An insulating glass unit comprised of at least two substantially parallel, spaced sheets of glass wherein at least one sheet of glass is a sputter-coated sheet of glass according to claim 1. An insulating glass unit according to claim 23 wherein said two sheets of glass are sealed together at their peripheral edges thereby to define an insulating chamber therebetween, and wherein said layer system is located on a surface of one of said glass sheets within said insulating chamber, and the reflectance and color characteristics when viewed from outside are: R G Y about 14 to 20 a h about -2 to +2 b h about 0 to -10 and when viewed from the inside are: R f Y about 11 to 18 a h about 0 to +4 b h is about 0 to -10 and the visible transmittance is at least about 61%. An insulating glass unit according to claim 24 wherein said unit is an insulating glass window, door or wall and the visible transmittance is at least about 63%. An insulating glass unit comprised of at least two substantially parallel, spaced sheets of glass sealed together at their peripheral edges thereby to define an insulating chamber therebetween, wherein at least one of said glass sheets is a sputter-coated sheet of glass according to claim 4 wherein said layer system is located within said insulating chamber. An insulating glass unit comprised of at least two substantially parallel, spaced sheets of glass and sealed together at their peripheral edges thereby to define an insulating chamber therebetween, wherein at least one of said glass sheets is a sputter-coated sheet of glass according to claim 8 wherein said layer system is located within said insulating chamber. An insulating glass unit comprised of at least two substantially parallel, spaced sheets of glass heat sealed together at their peripheral edges and defining a substantially air-free insulating chamber therebetween, wherein at least one of said glass sheets is a sputter-coated sheet of glass according to claim 10, wherein said layer system is located within said insulating chamber. An insulating glass unit comprised of at least two substantially parallel, spaced sheets of glass sealed together at their peripheral edges thereby to define an insulating chamber therebetween, wherein at least one of said glass sheets is a sputter-coated sheet of glass according to claim 11 wherein said layer system is located within said insulating chamber. An insulating glass unit comprised of at least two substantially parallel, spaced sheets of glass and sealed together at their peripheral edges thereby to define an insulating chamber therebetween, wherein at least one of said glass sheets is a sputter-coated sheet of glass according to claim 13 wherein said layer system is located within said insulating chamber. An insulating glass unit comprised of at least two substantially parallel, spaced sheets of glass heat sealed together at their peripheral edges and defining a substantially air-free insulating chamber therebetween, wherein at least one of said glass sheets is a sputter-coated sheet of glass according to claim 18, wherein said layer system is located within said insulating chamber. Method of making an insulating glass unit comprised of at least two sheets of glass sealed at their peripheral edges to each other thereby to define at least one insulating chamber therebetween, said method including the steps of spacing said glass sheets apart, said sheets at an elevated temperature, and sealing the peripheral edges of said sheets to each other at or above said elevated temperature, and using as at least one of said glass sheets, said sputter-coated glass article of claim 3, so located that said layer system thereon is within said insulating chamber. Method of claim 32 wherein at least one of said glass sheets is the sputter-coated glass article according to claim 10. Method of claim 32 wherein at least one of said glass sheets is the sputter-coated glass article according to claim 16.

Inventors: HARTIG KLAUS W, LARSON STEVEN L, LINGLE PHILIP J, HARTIG, KLAUS W., LARSON, STEVEN L., LINGLE, PHILIP J.
Applicants: GUARDIAN INDUSTRIES, GUARDIAN INDUSTRIES CORP.
Application year: 1996
Main classification: C03C17
IPC codes: B32B17, C03C4, C03C17, E06B3, C03C27