WAX DEPOSIT INHIBITORS

Abstract: Novel N-substituted polyalkyleneimines having at least one organic substituent of at least 6 carbon atoms e.g. 2 hydroxy octadecyl, on at least one nitrogen atom are disclosed. They may be prepared by reacting a polyalkyleneimine with either an epoxide or an imine or a compound of formula R-(X)a-Y wherein R is an organic group, X is a polar group, Y is a nucleophilic leaving group and a=0 or 1 e.g. an acid chloride or an acid anhydride. The N-substituted polyalkyleneimines can be used to lower the wax appearance temperature or to reduce the deposition of wax from a hydrocarbon e.g. crude oil containing wax.

Description: WAX DEPOSIT INHIBITORS The present invention relates to wax inhibitors and processes for their preparation and use, particularly in petroleum industry pipelines. Crude oils are complex mixtures comprising hydrocarbons of varying types and molecular weights. One class of hydrocarbon present in the oils is paraffins which are linear, branched chain or cyclic hydrocarbons having at least 18 carbons which can form waxy solids. The solubility of these waxy solid forming components in the crude oils is predominantly temperature-dependant. They are usually soluble in the crude oil under down-hole conditions ie high pressures or high temperatures. However as the oil is brought to the surface its temperature and pressure are reduced. As a result the wax may begin to precipitate out and may form deposits on any cooler surface with which it comes into contact. These wax deposits can cause problems, such as blockage of pipelines, valves and other process equipment. The wax may also deposit in pipelines used to transport crude oil or fractions derived from the total product brought up from down-hole, such as fractions comprising gas, eg natural gas, and/or water, as well as a liquid hydrocarbon body, eg crude (or black) oil or "condensate"; the pipelines may thus be hydrocarbon lines or multi phase transportation lines with oil, gas and/or water. The wax may deposit on surfaces of metal e.g. of ferrous metal. We have now found certain compounds which may be used as effective wax inhibitors. The present invention provides a novel N-substituted polyaUcyleneimine compound with nitrogen atoms, which has at least one organic substituent of at least 6 carbon atoms on at least one nitrogen atom, especially a chain N atom. In the substituted polyalkyleneimine compound each alkylene group usually has 2- 4 carbons, eg 2, 3 or 4 especially 2 carbons. The substituted polyalkyleneimine compound or polyalkyleneimine backbone thereof may have a molecular weight of 600- 1000000 eg 800-100000 such as 1300-3000 but may be 200.000-500,000. The polyalkyleneimine backbone may be linear or branched; the back bone usually has linear and branched sections with branching on each 1-10 nitrogen atoms e.g. 2-5 N atoms. The compound is usually oil soluble to an extent of at least 0.05% w/w in decane at 0 9 C, preferably at least 1 % w/w; it is usually water insoluble, eg with a solubility in water at 25^ of less than 1 % w/w, especially less than 0.05% w/w. The compound is usually a waxy solid, eg of softening point 20-100 9 C e.g. 40-80 e . The organic substituent may be of 6-40 carbon atoms, preferably with a continuous chain of at least 6, eg at least 12, such as 6-24 or 12-20 or 12-24 carbon atoms. The chain, and especially the organic substituent may be branched but is especially linear. The organic substituent may have such a chain bonded directly to a chain or terminal nitrogen atom of the polyalkylene imine or preferably bonded via an intermediate group usually a polar group. The intermediate group which is usually divalent, may be inorganic eg an ether oxygen atom or sulphonyl SO2 group, or the intermediate group may be a functional group containing C and at least one O and/or N atom and optionally at least one hydrogen atom. Examples of such groups are carbonyl (- CO), including 2 hydroxycarbonyleth-1 -yl- 1 -carbonyl (derived from a succinic acid group), a 2-hydroxy (or amino) alkylidene (1,1)- group, or 2-hydroxy (or amino) alkylene (1,2)- group (each alkylidene or alkylene having 2-4 e.g. 2 carbons) such as 2-hydroxy ethylidene HOCH 2 -CH< or 2 hydroxyethylene -(HO)CH-CH2- (or mixtures thereof) and the corresponding amino compounds (or mixtures thereof). The organic substituent may also comprise a group A of at least 6 carbons which may be an alkyl group of 6-30 eg 12-24 carbon atoms, such as octyl, decyl, dodecyl lauryϊ. tetradecyl, hexadecyl palmityl, octadecyl stearyl or may be an alkenyl group of 6-30 eg 12-24 carbon atoms such as octadecenyl, hexadecenyl or dodecenyl. The organic substituent may also comprise an aryl group A. eg an aromatic hydrocarbyl group, which may be optionally substituted by at least one ether group, eg alkoxy of 1-6 carbons such as methoxy or ethoxy; the aryl group may contain 6-30 carbons, such as 6-14 and especially 6-9 carbon atoms, preferably phenyl, tolyl, xylyl dodecyl-phenyl or naphthyl or methoxy phenyl. The organic substituent may also comprise a cycloalkyl group A eg of 5-1 carbons such as cyclopentyl or cyclohexyl, either of which may be substituted by at least one hydrocarbyl group eg alkyl of 1-6 carbons such as methyl, or alkoxy eg of 1-6 carbons such as methoxy or ethoxy. The organic substituent may also comprise an arylalkylene group A or cycloalkylalkylene group A each of 7 to 30 carbons eg 7-12 or 14-20 carbons. in which the aryl group and cycloalkyl groups may be as defined above and the alkylene group may contain 1-4 carbons, especially methylene and 1.2-ethylene, such as benzyl, 2- phenylethyl or cyclohexylmethyl. The orgamc substituent may also compnse an arylalkenylene group A, wherein aryl is as defined above and alkenylene has 2-4 carbons such as 1,2-ethylene as in 2-phenyleth-l-enyl. T e organic substituent preferably consists of said intermediate group and said group A or consists of said group A. However the organic substituent may also be a group B of formula R! -C-(R2)-R3, wherein R^ compπses an optionally hydroxy or amino substituted organic group (eg with at least one carbon atom, particularly as defined for A above), especially with the HO or H 2 N group in the 2 position to the free valency such as hydroxy methyl or amino methyl and R^ may be hydrogen or an organic group (eg as defined for A above) and R^ may be hydrogen or an orgamc group (eg as defined for A above) Examples of the above compounds of the invention are polyethyieneimines with at least one N-subsQtuent which is a 1 -alkyl or aryl 1-hydroxymethyl 1-methyl group eg 1- hexadecyl-1-hydroxymethyl 1-methyl group, 1 -phenyl- 1 -hydroxymethyl- 1-methyl group, or 2-alkyl or aryl- 2 hydroxy ethyl- 1- group such as 2-hexadecyl-2 hydroxy ethyl (2 - hydroxy octadecyl) or 2-phenyl 2 hydroxy ethyl group, a fatty acid acyl group eg stearoyl or lauroyl, or arylacyl group eg benzoyl or arylalkylene acyl group e.g. cinnamoyl, aryl sulphonyl group eg benzene- or toluene sulphonyl group, 1 -alkyl or aryl-l amιnomethyl-1 - methyl group, or alkenyl succinyl group, eg fatty alkenyl succinyl group eg octadecenyl succ nyl group. The compounds of the invenuon contain at least one alkyleneimine of the above substituents eg 0 1-1 substituent per mtrogen atom in the polyalkyleneimine chain, especially 0.5-1 per secondary nitrogen atom in the polyalkylene imine chain, and/or per primary nitrogen atom in said chain The compounds of the invention may have at least one alkyleneimine unit, eg at least one repeating unit of formula -C n H2 n -N-(X) a -R where a is 0 or 1, n is 2 - 4, eg 2, X is an inorganic or organic intermediate group (eg as defined above) and R is an orgamc group, eg as descπbed for A above. The compounds may contain 10-100 of such units and/or -CH2CH2-NH- units. The compounds may have NH2 or -NH-(X) a -R or HO termination groups The substituted polyalkylene diamines may be prepared by a process according to a further aspect of the invention which process comprises reacting a polyalkyleneimine with a compound of formula R-(X) a - Y, wherein R, X and a are as defined above and Y is a nucleophilic leaving group such as a halide eg chloride or bromide or hydroxy group or ester thereof, eg a sulphonate ester, such as one of 1-10 carbons eg methane-, benzene-, toluene- or xylene-sulphonate ester group. Examples of compounds of formula R(X) a Y are acid chlorides (or the acids themselves) from lauric, palmitic, stearic, oleic acids benzoic or cinnamic acids or sulphonyl chlorides from benzene, toluene or xylene sulphonic acids, or an acid anhydride (or acid itself) such as a substituted succinic acid e.g. octadecenyl succinic anhydride, or an alkyl halide, alkyl benzyl halide or benzyl halide especially a bromide, such as lauryl cetyl, dodecyl, stearyl, benzyl bromide and dodecyl benzyl bromide. The polyalkyleneimine may be of a structure as described for the polyalkyleneimine back bone above; the polyalkylene imine usually has secondary or tertiary internal chain N atoms and usually primary terminal N atoms; the ratio of primary to secondary to tertiary N atoms is usually 0.5-2: 1 -4:0.5-2 e.g. about 1 :2: 1. The reaction may be performed with heating usually at 30-250 g C such as 100-200^ and may be in the presence of a base eg an acid acceptor (for HY); examples are particulate inorganic hydroxides and carbonates, such as calcium carbonate and organic tertiary bases such as NN dimethylaniline. When the Y group is OH, the reaction may be performed with continuous removal of by product water eg azeotroping in a Dean and Stark apparatus, or by evaporation under vacuum; the latter may also be used when Y is a halide. The reaction may be performed with a molar ratio of R(X) a -Y compound equivalent of to NH group in the polyalkyleneimine of 0.1-10:1. The reaction may be performed in the presence of an inert solvent or diluent eg hydrocarbon solvent such as xylene or cyclohexane. The reaction may be continued until substantially all the secondary and/or primary NH groups have been reacted. In another aspect of the present invention, the process comprises reacting a polyalkyleneimine with an epoxide or a mixture of at least two epoxides, or an imine eg with a terminal epoxy or imine group. Examples of such epoxides or imines are those which are R substituted ethylene oxides or ethylene imines such as 1,2 -epoxy octadecane, 1.2-epoxy eicosane and 1 ,2-epoxy docosane and mixtures thereof. The epoxide or imine may also have an internal epoxy or imine group as in epoxidised internal alkadienes or alkenes. eg octadiene or epoxidised ricinoleic acid. Apart from use of the epoxide or imine the reaction conditions, proportions etc may be as described above. The products are ones in which the organic substituent is bonded to the polyethylene imine by an intermediate group, which is a hydroxy (or amino) alkylene or alkylidene group (or a mixture thereof). The acyl substituted polyethylene imines which are predominantly linear may also be made by canonic polymeπsation of 2-alkyl oxazo nes, while other N-organo substituted polyethylene imines may be made by cationic polymeπsation of the corresponding N-substituted aziπdines. At the end of the reactions of the mvention. the products may be used as such or after working up, eg by filtraαon or extraction of any products from the acid acceptor, and opuonally evaporauon of any solvent or diluent. The invenuon also provides the substituted polyalkylene imines obtainable by or obtained by the processes of the present invention. The substituted polyalkylene irmnes are used as such or in solution in a hydrocarbon solvent, such as decane or xylene, eg as 0.5-10% w/w solutions They may be used to lower the wax appearance temperature (WAT) of wax in a condensed state hydrocarbon e.g. solid or hquid hydrocarbon. The hydrocarbon is usually primarily ahphauc in nature, but may contain up to 50% w/w liquid aromatic compounds. The hydrocarbon may be a crude or black oil or a distillate or non volatile fracuon therefrom, such as a vacuum or thermal residue. Preferably the hydrocarbon is an oil field product, eg either a whole well product, the multiphase mixture in or from the well bore, or one at the well head after at least partial separauon of gas and/or water, and may be flowing up a well bore, or on a production platform or between platforms or from a platform to a collecuon or storage facility eg from offshore to onshore. Particularly of interest are hydrocarbons moved in pipelines under the sea under low temperature conditions eg in latitudes of greater than 50° N or S or in Gulf of Mexico The hydrocarbon may contain upto 50% by weight of wax e.g. 0.5-50% usually 0.5-30% or 1-15% especially 2-9%. The hydrocarbons may contain dissolved gas (eg with amounts of up to 10% gas) or water or water droplets eg with 5-40% water (eg as in water in oil emulsions, so called "chocolate mousse"). There may also be gas and/or water as a physically separate phase. The hydrocarbons may in the absence of the compounds of the invention, have a WAT value of at least 0°C eg 0-50°C such as 25-50 e C; pour point of such hydrocarbons may be 10-30^ eg 20*0 lower than the WAT value. The compounds of the invention may reduce the WAT value of the hquid hydrocarbon by at least 5°C eg 5-20°C such as 10- 15°C, but may be 0.5-5°C. The compounds may delay the onset of wax nucleation eg as shown by hght scattering and/or the rate of wax deposition per unit time. In addition they may also reduce the pour point and/or modify the wax crystals or disperse the wax Amounts of 100-1 .000 ppm eg 200-5000ppm especially 400-2,000 ppm (usually based on the weight of the hydrocarbon) of the compounds of the invenαon may be added to the hydrocarbon containing wax Thus the present invention also provides a method of lowering the wax appearance temperature of a hydrocarbon contaimng a wax, which compπses adding thereto at least one substituted polyalkylene imine of the invention or one obtained by or obtainable by the process of the invention. There is also provided a method of reducing the deposition of wax from a hydrocarbon containing wax, which compπses adding thereto at least one substituted polyalkylene imine of the invention or obtainable by or obtained by the process of the invention. The compounds of the invention may be added in a portion to the hydrocarbon to be protected or may be mixed batch wise, continually or continuously with a moving usually hquid body of that hydrocarbon, preferably added to a line containing flowing liquid hydrocarbon to be protected, upstream of a cooler location where wax deposition may occur in the absence of said compound. The invention is illustrated in the following Examples:- Example 1 A polyethyleneimine of molecular weight 1800 (obtained from Polysciences Limited and beheved to have a linear and branched structure) (4.3g) was heated with stirring under mtrogen with 1,2-epoxyoctadecane (26.8g about an equivalent of epoxy per N atom in the polyalkylene imine) for 16hrs at 180°C The reaction product was allowed to cool The product accorded with a structure formed from addition of an NH group in the polyethyleneimine to the epoxy ring. Examples 2-4 In these Examples, the effectiveness of the product of Ex 1 in affecting wax formation or deposition was compared to a blank with no additive. The tests were performed on 2 wax test solutions C and D of the following weight composition Wax Solution C 5% crystals of wax (Ref 58/60 refinery fraction), 5% toluene and 90% decane fraction. Wax Solution D 10% crystals of above wax. 5% toluene and 85% decane fraction Wax Solution E 10% crystals of wax (Ref: 150/155 refinery fraction), 5% toluene and 85% decane fraction. In each case the inhibitor solutions were made up in 1% w/w solution in decane, and appropriate amounts added to provide concentrations of 400 ppm or 1000 ppm in the test solution with the wax. Example 2 In this Example the property of affecting wax nucleation was tested, by determination of the first appearance of crystals in the test solution (with wax) by light scattering. Into the test solution in a vial maintained in a constant temperature enclosure at 18 S C or 20 Q C was passed monochromatographic hght and the amounts of hght transmitted through the vial and that scattered at 90 Q thereto were detected on solid state detectors and the information fed to a computer and the time of first appearance of wax crystals noted. Each vial contained 20g of the wax solution C or D, together if required with appropriate amount of additive (in decane); after mixing the components at 50 S C, the solutions were stored at 50 9 C ready for use. The results were as follows:- "Stopped" means that the test was stopped even though no crystals had formed. In an alternative test the lowest temperature at which a solution will not show nucleation for 6 hours was determined. For solution C and no additive, the lowest temperture was 18.5°C, while for solution C with 400ppm of the product of Ex.l it was 15.8°C. Example 3 This example describes tests on the rate of build up of wax deposits in a pipeline as evidenced by the temperature at which blockage occurs. The apparatus comprised a stainless steel coil of 1.88 mm internal diameter tube 3.2m long which was maintained in a constant temperature bath and the solution at 55°C containing wax to be tested was passed through this coil at 5ml/min. giving a 2 minute retention time. Initially the bath was at 40 Q C and then the temperature of the bath was reduced to 10°C, well below the temperature at which wax would deposit and block the tube in the absence of inhibitor. The liquid exiting the coil was recycled to a heating bath at 55°C to melt any wax crystals m it and then returned to the cold coil. In this way the only sohd involved in the expeπment is that deposited in the coil. The pressure difference across the coil was monitored to determine the build up of deposit and the temperature for complete blockage noted; this was deemed to occur when the pressure difference across the coil was greater than 86.2KPa (12.5 psi). For test solution C this was about 25°C and for test solution D it was about 26.5 9 C The experiments were repeated with the test solutions also containing the compounds for testing. The results were as follows:- For test solution D, with the product of Ex. 1 at 400 and 1000 ppm, blockage occurred at 26^, while with test solution C, with the product of Ex. 1 at 400 and 1000 ppm, blockage occuπed at 23.2 9 C and 19.4 e C respectively Example 3a The process of Ex.3 was performed in a similar fashion but the initial bath temperature was 20°C and the solution containing wax circulated for 18 hours. Subsequently the bath temperature was dropped by a small interval and the process repeated one or more times until complete blockage occurred. The results were as follows, for test solution C, with no additive blockage occurred at 17.1 °C. For test solution C with the product of Ex.1 at 400 and 800ppm, blockage occurred at 12.9°C and 13.2°C respectively For a commercially available wax inhibitor at 800ppm. blockage occurred at 15. C. Example 4 The wax appearance temperature was determined from the highest temperature at which wax crystals deposited from solution. Each solution for testing was loaded into a flat cross section microscope capillary tube, which was then sealed. The tube was mounted on a thermostated stage of a microscope whose temperature was then reduced at 0.1°C/mιn and the solution inspected. The temperature of appearance of wax was noted. The absolute results here are different from those in Ex. 2 because in this case the sample is cooled in a preprogrammed way. while in Ex 2 the sample is held at a constant temperature. With solution C. and no additive the WAT was 17.6°C. while with 400 ppm of product of Ex. 1 , the WAT was 16.8°C, while with solution D and no additive the WAT was 24.3"C and with 400 ppm of the product of Ex. 1 was 22.4 υ C. With solution E. and no additive the WAT was 349°C. while with 400ppm of product of Ex 1 , the WAT was 342°C Example 5 The process of Example 1 was repeated except that an epoxidised C20/C22 α- olefin was used instead of 1,2-epoxyoctadecane. The epoxidised C20/C22 α-olefin was prepared as follows 30g crude (-80%) m-chloroperbenzoic acid was washed with 300ml of a phosphate buffer solution (pH7.8) to obtain a fine suspension The suspension was filtered, the separated solid dissolved in dichloromethane and the resulting solution dned Mixed C20 C22 α-olefin (25g) (containing 66% eicosane and 22% docosane) was dissolved in 200ml dichloromethane and 400ml of a phosphate buffer solution (pH7 8) added at room temperature The mixture was stirred and the m-chloroperbenzoic acid solution added in 50ml portions over a peπod of 2 hours with the stirring continuing overnight to produce an organic phase and an aqueous phase. The organic phase was separated, dned and the solvent removed under vacuum to leave a residue The residue was redissolved in dichloromethane (200ml) and washed with further phosphate buffer solution (3x50ml), separated, dned and evaporated. This purification stage was repeated a further time using IM sodium carbonate solution and the product worked up as above to leave a product, the NMR of which accorded the structure of a product of a mixture of 1.2-epoxyeιcosane and 1,2-epoxydocosane of 87.7% puπty with 3.5% m-chlorobenzoic The process of Example 1 was repeated using the above produced epoxidised C20 C22 α-olefin instead of epoxyoctadecane. The product obtained had a structure whose nmr spectrum accorded with a structure from addition of at least one NH group in the polyethyleneimine to the epoxy rings Example 6 The wax appearance temperature for solution D with 400ppm of the product of Ex 5 and solution D with no additive, were determined according to the method of Example 4. The results were as follows- for solution D with no additive, the WAT was 24 3°C, and with 400ppm of the product of Ex.5 it was 22 1°C Example 7 The process of Example 3a was repeated For test solution C with the product ot Ex 5 at 400 and 800 ppm, blockage occurred at 144 and 14 38 °C respectively

Claims: Claims: 1 An N-subsututed polyalkyleneimine characterised in that it has at least one organic substituent of at least 6 carbon atoms on at least one nitrogen atom. 2. A polyalkyleneimine as claimed in claim 1 in which the at least one organic substituent is an optionally hydroxy substituted alkyl group of 12-24 carbon atoms which is bonded to a cham or terminal N atom of the polyalkyleneimine either directly or via a polar group. 3. A polyalkyleneimine as claimed in claim 1 or 2 in which the polar group is an inorganic group or an organic functional group containing carbon and at least one oxygen and/or nitrogen atom and optionally at least one hydrogen atom. 4 A polyalkyleneimine as claimed in claim 3 in which the organic group is a carbonyl group 5 A polyalkyleneimine as claimed in any one of claims 1 -4 m which the at least one orgamc substituent is an optionally hydroxy substituted alkyl or alkenyl group of 6-30 carbon atoms. 6. A polyalkyleneimine as ciauned in any one of claims 1-5 in which the at least one organic substituent is a 2 hydroxy octadecyl group 7 A 2 hydroxy octadecylated polyalkyleneimine obtained by or obtainable by the reaction of a polyethyleneimine with 1.2-epoxyoctadecane. 8. A process for the manufacture of an N-substituted polyalkyleneimine which has at least one organic substituent of at least 6 carbon atoms on at least one nitrogen atom charactensed in that a polyalkyleneimine is reacted with a compound of formula (I) R- (X)a-Y wherein R is an organic group of at least 6 carbon atoms. X is a polar group, Y is a nucleophilic leaving group and a is 0 or 1 at a temperature of 30-250°C. in the presence or absence of a base 9 A process as claimed m daim 8 in which the compound of formula (I) is an acid chloride, an acid anhydride, an alkyl hahde or alkyl benzyl hahde or a benzyl hahde. 1 . process for the manufacture of an N-substituted polyalkyleneimine which has at least one organic substituent of at least 6 carbon atoms on at least one nitrogen atom characterised in that a polyalkyleneimine is reacted with an epoxide or an imine. 11. A process as claimed in claim 10 in which the epoxide is 1.2 epoxy octadecane. 12. A process as claimed in any one of claims 8-11 in which the organic group R is defined as the organic substituent as defined in any one of claims 2-6 or the epoxide or imine contains an organic substituent as defined in any one of claims 2-6 13. An N-substituted polyalkyleneimine as manufactured by a process according to any one of claims 8-12. 14. A method of lowering the wax appearance temperature of a hydrocarbon containing wax which comprises adding thereto at least one N-substituted polyalkyleneimine which has at least one organic substituent of at least 6 carbon atoms on at least one nitrogen atom. 15. A method of reducing the deposition of wax from a hydrocarbon containing wax which comprises adding thereto at least one N-substituted polyalkyleneimine which has at least one organic substituent of at least 6 carbon atoms on at least one nitrogen atom. 16. A method as claimed in claim 14 or 15 in which the hydrocarbon is a crude or black oil or a distillate or non-volatile fraction therefrom. 17. A method as claimed in claim 16 in which the hydrocarbon is crude oil. 18. A method as claimed in any one of claims 14-17 in which the hydrocarbon contains 0.5% to 50% by weight of wax. 19. A method as claimed in any one of claims 14-18 in which the hydrocarbon contains dissolved gas or water or water droplets. 20. A method as claimed in any one of claims 14-19 in which the N-substituted polyalkyleneimine is added to the hydrocarbon in an amount of 400-2000 ppm. 21. A method as claimed in any one of claims 14-20 in which the N-substituted polyalkylene imine is as defined in claims 1-7 or 13.

Inventors: DUNCUM SIMON NEIL, JAMES KEITH, OSBORNE CHRISTOPHER GEORGE, DUNCUM, SIMON, NEIL, JAMES, KEITH, OSBORNE, CHRISTOPHER, GEORGE
Applicants: BP EXPLORATION OPERATING, DUNCUM SIMON NEIL, JAMES KEITH, OSBORNE CHRISTOPHER GEORGE, BP EXPLORATION OPERATING COMPANY LIMITED, DUNCUM, SIMON, NEIL, JAMES, KEITH, OSBORNE, CHRISTOPHER, GEORGE
Application year: 1996
Main classification: C08G73
IPC codes: C08G73, C09K8, C10L1