AN ANTI-CAKING AGENT

Abstract: The present invention relates to an anti-caking agent for the treatment of granulate products, where the anti-caking agent is a salt having the general formula (Ia): R1-AB-R2-BA-R1, or the general formula (Ib): R1-BA-R2-AB-R1, in which the groups R1 independently represent monovalent hydrophobic organic groups, the group R2 represents divalent hydrophobic organic groups, the groups A represent independently anionic groups and the groups B represent independently cationic groups. The groups A preferably represent carboxylate ion groups and the groups B preferably represent ammonium ion groups. An anti-caking agent of this kind is very suitable for inhibiting the caking tendency of fertilizers.

Description: An anti-caking agent The present invention relates to an agent that inhibits the caking tendency of a granular product and to a method for preparing said inhibitor. The invention also relates to the use of said inhibitor for preventing the caking tendency of a granular product and to a granular product containing said inhibitor. The storage and handling of many inorganic salts or salt mixtures and granular products containing said salts, like for example fertilizers, are difficult due to their tendency to caking. The tendency to dusting is also a problem associated with these products. Several solutions have been proposed to handle these problems, like using organic coating agents, possibly in conjunction with a pulverized powdering agent. Hot fertilizer granules can be mixed with particles of a solid ceraceous coating agent causing the wax to melt and spread onto the surface forming a protecting film. Ceraceous compounds may contain waxes and ceraceous organic compounds, like fatty amines, fatty diamines, fatty amides and fatty acids and salts or mixtures thereof. Cooled fertilizer granules are usually coated with oil, which is mixed with different compounds having an improved anti-caking effect. Of these, the most commonly used are fatty amines and -polyamines or derivatives thereof. Amines, containing hydrocarbon chains of 16-20 carbons, like tallow amine or the amine based on hydrated tallow, are most usually used. The use of fatty acids for this purpose has also been reported. The use of long chain diamides, like distearoylhexamethylenediamide or diocta- decylsebasindiamide, for the treatment of ammoniumsaltpeter is known from SU 510460. Other anionic compounds, like sulfonates, have in addition to fatty acids been used to inhibit caking and dusting. Different mixtures of salts of sulfonic acid and alkyl- sulfonates, where a tacky alkylderivative is especially effective in preventing dusting, have been described in patent CA 1276071. The neutralized product between the polyethoxylized amine Rι-N[(R2O) n ι]-H]2 and the polyethoxylized phosphate ester OP[O-(R3O) n 2- 4,R5,R6]3 has been used as a component in the coating agent as described in EP- 1 13687 (Neederlandse Stikstof Maatschappij) together with other ingredients, where Rj represents an alkyl or alkenyl group having 12-20 carbon atoms, R2 and R3 represent alkenyl groups having 2-4 carbon atoms, one of the groups R4, R5, R-5 is a hydrogen and the other alkyl groups having 4-12 carbon atoms or alkylaryl groups having 4-12 carbon atoms, and nj and Ω2 are any number between 0 to 15. According to the patent SE 419 175 (KenoGard), a good result in inhibiting caking and dusting is achieved by using a granular or prilled coating agent, which is comprised of 20-60% inorganic powder, 10-30% by weight cationic amine R-NH2 or R-NH-(CH2) n - H2, in which R represents an aliphatic, hydrophobic group containing at least 12 carbon atoms and n is any number between 1 and 5, or a salt thereof, 5-35% by weight wax, 0-20% by weight fatty amide and 5-35% by weight alkoxylated primary aliphatic alcohol, wherein the alkyl group contains at least 8 carbon atoms. Amines, of which the hydrocarbon chain originates from plant - or animal fats or -oils like tallow, are reported as the most suitable. The amines can occur as salts, e.g. as salts of chlorides, acetates or fatty acids. The patent EP 48226 (KenoGard) is on its part describing a similar anti-caking agent comprising of 20-60% by weight inorganic powder, 10-35% by weight wax or a fatty amide containing at least 12 carbon atoms in its carboxylic acid chain and 20-60% by weight of a mixture of a carboxylic acid having at least 6 carbon atoms in its alkyl chain and an amine R-NH-(CH2) n -NH2. The method for the preparation of the anti-caking agent as described in the patent DDR 207701 uses 5-30% by weight of an aliphatic amine, which can be either primary, secondary or tertiary, 30-90% by weight of an aromatic or aliphatic fatty acid and 5-40% by weight of an aromatic mono- or dicarboxylic acid or a derivative thereof, as raw material mixed in a mineral or fatty oil, in which the combined oil content is limited to between 10-90% by weight of the mixture. The components are reacted by heating the mixture to a temperature of 500 K thereby forming amides. The aliphatic amine may be dipropylenetriamine or a residual from the preparation process of the same. Other by-products or residual amines and fatty acids or derivatives thereof having a carbon to nitrogen product ratio of at least 7: 1, are also included for use. The afore mentioned coating agents are though still experiencing huge difficulties with regard to performance, technical usability and commercial availability. The aim of the present invention is to make available a more powerful anti-caking agent. At the same time the agent should be suitable for as many granular products as possible. It is also important to make the anti-caking agent compatible with coating agents of other granular products in the field. An anti-caking agent fulfilling all of the afore mentioned criteria should also not be too expensive. The afore mentioned goals have been achieved with a new anti-caking agent, which according to the invention, is a salt having the formula (Ia): R!-AB-R 2 -BA-Rι (Ia) or the general formula (Ib): R!-BA-R 2 -AB-Rι (Ib) in which the groups Rj independently represent monovalent hydrophobic organic groups, the group R2 represents divalent hydrophobic organic groups, the groups A represent independently anionic groups and the groups B represent independently cationic groups. The salt according to the invention is novel and differs significantly from the prior art. The salt is hence a patentable invention. It has thus been discovered, that a salt having a structure consisting of regular layers, in which hydrophobic organic groups and anionic-cationic salt groups alternate, results in a more powerful anti-caking agent. The cationic groups B having the general formula (Ia) or (Ib) may be any cationic group, which together with the anionic groups form an ionic pair, i.e. a salt. The cationic groups B are preferably selected among -onium ion groups. Such groups are for example the oxonium-, sulfonium-, ammonium-, carbonium-, phosphonium-, arsenioum-, antimonium- and bismuthonium groups. The mentioned -onium ion group being an ammonium group is especially favourable, in particular, when both of the cationic groups B having the formula (Ia) and (Ib) represent ammonium groups. The anionic groups A having the formulae (Ia) and (Ib) can be any group which together with the cationic groups B form an ionic pair, i.e. a salt. It is however preferable when the afore mentioned anionic groups A represent anionic groups made from acids substituted with an organic moiety. Inorganic oxyacids, like carbonic acid, sulphuric acid, sulphurous acid, phosphoric acid, polyphosphoric acids, phosphorous acid, where one or several hydroxyl groups are replaced with one or several hydrocarboxy- or hydrocarbyl groups, are referred to as an acid substituted with an organic moiety. It is however preferable when at least one and in particular all of the anionic groups A are carboxylate ion groups. The salt compositions between the dicarboxylic acid and amine or the carboxylic acid and a diamine can, according to their way of preparation, react partly into the form of an amide. Hereby it is, however, essential that at least a part of the carboxylic and amino groups are in unreacted form. This can be indicated e.g. by heating the product to the formation temperature of the amide, whereby a drop of weight due to the evaporation of water takes place. The afore mentioned groups R\ according to the formulae (Ia) and (Ib) may be any hydrophobic group, but preferably longer chained groups, which may be saturated or unsaturated, substituted or unsubstituted, cyclic or acyclic, straight or branched, or possibly contain aromatic chains, and their skeleton may contain inorganic atoms and heteroatoms. Rl is very miscible in oil or wax and thus suitable as part of the inhibitant when the compound according to the invention is used together with an oil or a wax. In the case of mineral oils or waxes, R\ is preferably a hydrocarbon chain. R\ can contain polarity increasing atoms or groups, when a more polar oil or wax, like for example natural oil or wax, is used. R\ preferably also contains silicone or fluorinated carbons, if the oil or wax is comprised therof. The afore mentioned specified for the group R\ also applies for R2. Rl in the formulae (Ia) and (Ib) is according to a preferred embodiment a hydro¬ carbon- or a hydrocarbyl group, preferably a hydrocarbyl group having at least 7 carbon atoms and in particular a hydrocarbyl group having 10-22 carbon atoms. R2 is according to a preferred embodiment a hydrocarbylene group, i.e. a divalent hydrocarbon group having 1-22 carbon atoms and in particular 2-8 carbon atoms. The anti-caking agent according to the invention is preferably a salt having the general formula (II): Rl-N(R3R 4 R5) + -OOC-R2-COO + -N(R4R 5 R 6 )-R 1 (II) in which R] and R2 are the same as previously defmed and R3, R4 and R5 represent hydrogens and alkyl groups having 1 or 2 atoms, and preferably all of the groups R- * -, R4 and R represent hydrogens. It may also preferably be a salt having the general formula (III): R] -COO- + N(R R4R5)-R2-N(R4R 5 R 6 ) + -OOC-Rl (III) in which Rj and R2 are as previously defined and R3, R4 and R5 represent hydrogens and alkyl groups having 1 and 2 atoms, and in particular all ofthe groups R3, R4 and R5 represent hydrogens. The invention also relates to an anti-caking agent containing 0,2-20% by weight, preferably 0,5-5% by weight, of a salt according to the general formula (Ia) or (Ib), as well as oil or wax, possibly a filling agent, various anti-caking agents, protecting agents or other additives. As mentioned, the invention also relates to a method for the preparation of an anti- caking agent for a granular product according to any of the previously described claims. The method is characterized in that a compound having the formula (IV) : is reacted with a compound having the formula (V): B0-R2-B0 (V) to form a salt having the formula (Ia): R1-AB-R2-BA-R1 (Ia) or a compound having the formula (VI): Rl-Bo (VI) is reacted with a compound having the formula (VII): Ao-R 2 -A 0 (VII) to form a salt having the formula (Ib): R1 -BA-R7-AB-R1 (Ib) in which the groups Ao of the formulae (Ia), (Ib), (IV), (V), (VI) and (VII) represent anionic groups, the groups Bo represent cationic groups, the groups Rj represent mono¬ valent hydrophobic organic groups, the groups R2 represent divalent hydrophobic groups, the groups A represent the corresponding anionic groups formed by the groups Ao and the groups B represent the corresponding cationic groups formed by the groups BQ. It is thereby preferable if the groups Bo represent members of the -onium group. Preferably at least one and in particular two of the groups Bo are amino groups or ammonium salts thereof When the group BQ is attached to the group R2 forming a diamine as depicted in the formula (V), the diamine can either be a simple terminal diamine where two amino groups are attached to the hydrocarbon skeleton or a polyamine having several amino groups in its chain. Useful commercial amines are ethylenediamine (EDA), diethylenetriamine (DET A), triethylenetefraamine (TET A), tetraethylenepentamine (TEPA), pentaethylenehexamine(PEHA), aminoethylpiperazine (AEP), piperazine (DEDA), propylenediamine (1,2-PDA), 1,3 -diaminopropane (1,3-PDA), mtinobispropylamine (IBPA), dimethylam opropylamine (DMAP A), menthyl- diamine (MDA), triethylenediamine (TEDA), N,N,N N'-tetramethylenediamine (TMEDA), N,N,N\N^etramethyl -1,3-butanediamine (TMBDA) and 1,3-butanedi- am ehexamethylenediamine (HMDA). Typical monoarnines like methylamine, ethylamine, n-propylamine, n-butylamine, n-amylamine or pentylamine, n-hexylamine, n-octylamine, n-decylamine, lauryl- amine, myrisitylamine, palmitylamine, oleylamine and stearylamine are being formed when the group Bo is attached to the group Rj according to formula (VI). The groups Ao having the afore mentioned formulae (IV) and (V) are preferably selected among the acidic groups of acids containing organic substituents. Groups like these form when the hydroxyl group of a hydroxyl group containing inorganic acid is substituted with a hydrocarbyl group like alkyl or with a hydrocarboxy group like alkoxy. The most preferred acidic groups of acids containing organic substituents are the carboxylic groups originating from carbonic acid. Also the salts of acidic groups like the salts of carboxylic acids may be used, in which case an ionic exchange between the salts take place foπrύng an anti-caking agent according to the invention. According to a preferable embodiment at least one and in particular two of the Ao groups are carboxylic acid groups or salts thereof. The group Ao may represent any carboxylic moiety of the following acids by forming preferably a monocarboxylic acid by being attached to the group Rl as depicted in the formula (IV): butyric acid (butanoic acid), caproic acid (hexanoic acid), caprylic acid (octanoic acid), capric acid (decanoic acid), lauric acid (dodecanoic acid), myristic acid (tetradecanoic acid), palmitic acid (hexadecanoic acid), stearic acid (octadecanoic acid), arachid acid (eicosanoic acid), behenic acid (docosanoic acid), lignoseric acid (tetracosanoic acid), kerotinic acid (hexacosanoic acid) or a correspondmg unsaturated acid of the same type like oleic acid (Δ-9, 10- octadecanoic acid). The group Ao may be any of the following, when it is attached to the group R2 as depicted in the formula (VII) forming a dicarboxylic acid: oxalic acid, malonic acid, amber acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, nonanedicarboxylic acid, decanedicarboxylic acid, undecanedi- carboxylic acid and dodecanedicarboxylic acid. A preferable alternative is also a mixture of amber acid, adipic acid and glutaric acid, which is obtained as a by¬ product of the adipic acid process. As previously mentioned in connection with the treatment of the groups Rj and R2 of the product according to the invention, the acids and/or the amines may contain heteroatoms in the chain or as substituents of the chain. The chains can also be formed from siloxane units and/or fluorinated hydrocarbons depending upon the field of application ofthe anti-caking agent and the additives. With regard to the method according to the invention, the substituents R\ and R2 are the same as specified in connection with the product. In particular according to the method described in the invention, a compound R j -Ao having the formula (VIII): Ri-COOH (VIII) or its reactive derivative, like anhydride, acid chloride or salt, is reacted with the compound B0-R2-B0 having the formula (IX): H7N-R2-NH (IX) or with its ammonium salt or another salt, where R\ and R2 are the same as previously defined. It is also favourable according to the method of the invention, if a compound R j -BQ having the formula (X) or an ammonium salt or another salt thereof R1-NH2 (X) is reacted with the compound A0-R2- 0 having the formula (XI) HOOC-R2-COOH (XI) or a reactive derivative like anhydride, acid chloride or salt thereof, where R\ and R2 are as previously defined. When the salt according to the invention is prepared from monofunctional and difunctional compounds in the mole ratio Rι :R2 of 2: 1, the anionic and the cationic components neutralize each other. To depart fom this equivalent ratio either in the anionic or cationic direction has however been shown to be preferable resulting in better anti-caking properties for some fertilizers. According to an embodiment of the invention, the afore mentioned compounds are reacted with each other by varying the molar ratio Rj :R2 1-60%, preferably by 1-20%, in any direction of the 2: 1 stochiometric ratio. The addition of an anionic or cationic excess can occur either to a previously prepared product according to the invention, to the oil or wax used in the coating agent mixture, or to the coating agent mixture consisting of the compound according to the invention and an oil or a wax. According to an embodiment of the invention, the charge is changed to anionic by adding an excess of either the same anionic surfactant, which the salt according to the invention contains, or another valid anionic surfactant. It is preferable to alter the charge of the anti-caking agent of the invention to cationic by adding an excess amount of cationic surfactant, which can be the same or different as the component used in the salt according to the invention. The method according to the invention is implemented physically bv e.g. either adding each of the reactants, which preferably are an acid and an amine, to a different oil batch under simultaneous mixing and possible heating, or by mixing and possibly heating the reactants in the same oil batch. Typically approximately two moles of the compound Rl-Ao or Ri-Bo are mixed in the oil used for the coating and approximately one mole of the compound B0-R2-B0 or correspondingly A0-R2-A0 is mixed separately in the mixture used for the coating. The mixtures are mixed together and if necessary heated. Alternatively the compounds Rj-Aø and B0-R2-B0 (or R1-B0 and A0-R2-A0) are mixed in the same oil batch, which is heated, forming the salt spontaneously in the mixture. For example the salts of a primary or a secondary diamine and a carboxylic acid or the salts of a dicarboxylic acid and a primary or a secondary amine are possible to prepare by using this method. According to a second embodiment of the invention, the reactants are either added to separate solvent batches, which are then mixed together, or added to the same solvent batch forming a salt after evaporation of the solvent. Two moles of the compound R1 -A0 or RJ-BQ and approximately one mole of the compound B0-R2- BQ or correspondingly A0-R2-A0 are thus typically dissolved separately in an organic solvent followed by adding the solvents together, or the compounds are alternatively dissolved in the same solvent batch and mixed. The salt of the afore mentioned compounds is obtained after evaporating the solvent. According to a third physical embodiment of the invention, the reactants which preferably are an acid salt and an ammonium salt, are either each added to a separate water batches which are then combined followed by mixing, or added to the same water batch followed by separating the precipitated product from water. Typically approximately two moles of the compounds RJ-AQ or RJ-BQ and one mole of the compound B0-R2-B0 or correspondingly A0-R2-A0 are dissolved together or preferably separately in water. The salt that is forming is separating almost completely into the non-aqueous phase, from where it can be removed mechanically (if necessary by heating) and/or e.g. extracting with an organic solvent followed by subsequent evaporation. This method is suitable for the preparation of the salts according to the invention, when either of the compounds RJ-AQ (RJ-BO) or B0-R2-B0 (A0-R2-A0) or both of them are in the form of a salt, for example as a quaternary ammonium halogenide and an alkali metal carboxylate. The counterions, for example halogenide and alkali metal, will then remain in the water solution. The afore mentioned is of course associated with the fact, that a balanced stochio- metric ratio within certain limits improves the anti-caking properties ofthe product. According to another embodiment of the invention, the reactants are added to the coating of the particles of the granular product and reacted in the increased coating temperature environment of the particles. Typically the anionic and cationic precursor of the salt according to the invention is added separately into an oily or melted ceraceous material at the time of the coating agent preparation procedure. If the hereby obtained mixture is used in a temperature, which exceeds the melting point of the salt according to the invention, the anti-caking salt according to the invention does not form until the coating agent is cooled on the surface of the treated granular product. The invention also relates to a salt having the general formula (Ia) R 1 -AB-R 2 -BA-R 1 (Ia) or the general formula (Ib): R^BA^-AB-Ri (Ib) in which the groups R\ independently represent monovalent hydrophobic organic groups, the group R2 represents a divalent hydrophobic organic group, the groups A independently represent anionic groups and the groups B independently represent cationic groups, and to the use of said salt as an anti-caking agent for a granular product or as a component of said agent. The afore mentioned specifications set forth in connection with the description of the product and method according to the invention, also apply in connection with the use of the agent. When implementing the invention in practice, the afore mentioned salt can be uniformly applied as a ceraceous coating on the warm granular product, in which case an anti-caking protecting film is formed on the granular surface. According to another embodiment, the afore mentioned salt is a component of an oily or ceraceous coating mixture, thus protecting the anti-caking of the granular product in an unprecedented way. A preferable method of usage is as a mixing agent in an oily or ceraceous coating agent mixture, which is applied on the surface of the granular product by spraying pulverized droplets. The temperature of the salt containing an oily or ceraceous coating agent mixture is preferably held so high that the salt according to the invention essentially dissolves or disperses into the used oil, which adjusts the viscosity of the mixture to a sufficiently low level thereby allowing the mixture to be sprayed. Besides oil, waxes in a melting state are also suitable. The invention also relates to a granular product, which is characterized by having its particles treated with an anti-caking agent or a mixture containing said anti-caking agent, wherein said anti-caking agent is a salt having the following formula (Ia) Rl-AB-R 2 -BA-R] (Ia) or the general formula (Ib) R!-BA-R 2 -AB-R! (Ib) in which the groups R\ independently represent monovalent hydrophobic organic groups, the group R2 represents divalent hydrophobic organic groups, the groups A represent independently anionic groups and the groups B represent independently cationic groups. The afore mentioned specifications set forth in connection with the description of the anti-caking agent according to the invention, the preparation method and the use of the same, also apply for the granular product. The salt used as an anti-caking agent for a granular product is preferably having the general formula (II) Rl-N(R 3 R4R5) + -OOC-R2-COO- + N(R4R 5 R 6 )-R 1 (II) in which Rj and R2 are the same as above and R3, R4 and R5 represent hydrogens and alkyl groups having 1 to 2 atoms, and in particular all of R3, R4 and R5 represent hydrogens. Alternatively the salt is preferably having the general formula (III) Rl-COO- + N(R 3 R4R5)-R2-N(R4R 5 R 6 ) + -OOC-Rl (III) in which Rl and R2 are the same as above and R3, R4 and R5 represent hydrogens and alkyl groups having 1 to 2 atoms, and in particular all of R3, R4 and R5 represent hydrogens. The granular product according to the invention may be coated only with the afore mentioned anti-caking agent or with a mixture containing in addition to said salt also oil or wax, possibly fillers and other anti-caking agents, protecting agents and additives. The granular product according to the invention may be for example powder, flour, dust, scales, grits, grain, granulate or a granular product. The product can also be an inorganic salt, an inorganic salt mixture or a granular product containing afore mentioned products. In particular, the granular product may be a fertilizer like the N-P-K fertilizer, which usually easily tends to cake. The anti-caking agent of the invention is surprisingly well suited for a fertilizer of this type. Examples The invention is described closer with the aid of these examples. Example 1 A 2: 1 mole ratio salt (the salt according to the invention) was prepared from primary technical-grade stearylamine (Noram S/CECA) and adipic acid. The sample was prepared using an adipic acid amount of 2,9 g. Methanol was used as solvent for the adipic acid and ether for the amines. Example 2 Comparison. A salt was prepared according to the procedure outlined in example 1, but instead of stearylmonamine a corresponding amount of technical-grade stearyl- diamine R-NH-CH 2 -CH 2 -CH2-NH2 (Inipol DS/CECA) was used. Example 3 1 part by weight of the aminedicarboxylic acid salts prepared in examples 1 -2 was mixed with 9 parts by weight of paraffin mineral oil at a temperature of 80 °C. The prepared coating agent mixtures were tested in order to prevent caking of the fertilizer 20-0-15 (N-P-K) by spraying an 80 °C coating agent mixture at a dosage rate of 2 g/kg or 4g/kg onto the surface of the 40 °C warm fertilizer followed by powdering the surface with talcum, Finntalk P 40, at a dosage rate of 4g/kg. The coated fertilizers were moisturized for 2 h at 25 °C in a relative humidity of 75%. Five fertilizer containing portions, each weighing 100 g, were placed in plastic bags followed by subjecting the bags to a pressure of lkg/cm-2 for 1 day after which the bags were dropped one by one lengthwise from an altitude of 50 cm. The fertilizers were then sieved through a 7, 1 mm sieve. The caking tendency was measured by determining the portion of fertilizer granules left on the sieve. The following results were obtained: Moisture content % Crust content % Uncoated: 1,4 47 The salt of example 1 (according to the invention) 2 % coating 1, 1 4 4 % coating 1,2 0 The salt of example 2 (comparison) 2 % coating 1,5 46 4 % coating 1,5 42 Example 4 The paraffin mineral oil was blended with 4% by weight of the salt according to example 1 prepared from adipic acid and technical-grade monostearylamine. The mixture was tested in inhibiting the caking tendency of the fertilizer 20-0-15 (N-P- K) following the procedure as outlined in example 4. A readily available commercial coating agent mixture was selected as a comparison agent to this fertilizer. The following results were obtained: Moisture content % Crust content % Uncoated: 1,4 47 4 % of the salt according to example 1 in oil 2 % coating 1,2 13 4 % coating 1,2 6 A commercial coating agent mixture (comparison) 2 % coating 1,4 28 4 % coating 1,3 23 Example 5 The coating oil was prepared by mixing paraffin mineral oil with 4% by weight adipic acid and the salt of technical-grade monostearylamine both in the theoretical 1 :2 mole ratio as well as modified with an excess anionic or cationic component. The caking tendency of the NPK fertilizer 20-4-8 (N-P-K) was measured by using the method described in example 3 where 2 kg coating oil and 2.5 kg talcum (caking I) and 4 kg coating oil and 4 kg talcum (caking II) were used per each ton of fertilizer. Coating agent Caking % I II Theoretical mole ratio 19 7 Stearylamine 9,9 mole % excess 9 7 Stearylamine 19,7 mole % excess 8 3 Adipic acid 4, 1 mole % excess 1 1 5 Adipic acid 8,2 mole % excess 3 3 Example 6 The test in example 5 was continued by increasing the anionic or cationic character of the coating oil, which contained the 1 :2 molar ratio salt between adipic acid and technical-grade monostearylamine, by adding an excess of octylamine or octanoic acid. Coating agent Caking % I II Octylamine 25 mole % excess 7 4 Octylamine 50 mole % excess 4 2 Octanoic acid 22 mole % excess 3 3 Octanoic acid 44 mole % excess 6 2 Example 7 The test according to examples 5-6 was repeated using the fertilizer NPK (20-0-15) together with the salt between adipic acid and stearyl amine, which produced an excellent result even when a theoretical molar ratio was used. The tendency to form clusters by the test samples was further decreased by increasing the cationic or anionic character of the coating agent: Coating agent Caking % I II Theoretical molar ratio 9 3 Stearylamine 9,9 mole % excess 6 1 Stearylamine 19,7 mole % excess 5 5 Adipic acid 4, 1 mole % excess 7 1 Adipic acid 8,2 mole % excess 5 1 Octylamine 25 mole % excess 2 1 Octylamine 50 mole % excess 4 0 Octanoic acid 22 mole % excess 3 9 Octanoic acid 44 mole % excess 1 6 Example 8 (preparation in oil) 50 g fertilizer coating oil was prepared which contained 96% by weight of oil containing paraffin and 4% by weight of a compound formed between stearic acid and ethylene diamine: 1.79 g stearic acid was dissolved in warm oil in which it melted. 0.21 g of ethylene diamine was gradually added at a temperature of 80 °C. The clear solution became turbid but retained a sufficiently low viscosity at 70-80 °C to be applied by means of nozzles. Example 9 (excess of amine) Fertilizer coating oil was prepared which contained 97% by weight of oil, 2% by weight of a compound between stearic acid and ethylene diamine and 1% by weight of technical stearylic amine so that one part of the coating oil of example 8 was mixed with one part of a mixture containing technical stearylic amine dissolved in a basic oil of the same quality. The sample was stored at a temperature of 70-80 °C and the viscosity remained suitable for coating by means of nozzles. Example 10 (comparative example) Ethylene bis-stearylic amide R-CO-NH-CH2-CH2-NH-CO-R, wherein R is a hydrocarbon group originating from stearic acid was prepared, according to Kirk- Othmer, Vol. 2, p. 252, 3rd. Ed. (1978) so that 1 mole of ethylene diamine was gradually mixed with two moles of stearic acid and heated to 165-175 °C under nitrogen atmosphere and heating at 180-185 °C was continued until the weight of the product remained unchanged. After cooling the product was wax-like. The sample was analyzed by Differential Scanning Calorimetry (DSC) whereby a sample of about 2 mg was heated at a rate of 4 °C/min. An endothermic peak corresponding to the melting of a diamide occured at about 142 °C. Example 1 1 (comparative example) A coating agent corresponding to example 10 was prepared. In the preparation the stearic acid and the ethylene diamine was replaced by the corresponding molar amount of a diamide prepared according to example 10. The diamide was mixed with an oil heated to 80 °C by means of a dispersion apparatus but it did not dissolve. To the resulting mixture was then added a mixture of oil and stearylic amine at 80 °C and the temperature was raised while mixing until the diamide dissolved at a temperature of 126 °C. At this temperature the mixture remained viscous but when cooling it formed harmful solidifications. The composition of the mixture contained 97.1% by weight of oil, 1.9% by weight of ethylene bis-stearylic amide and 1% by weight of technical stearylic amine. Example 12 (dry compounds) A mixture ready for delivery in dry form and for use as a component in anti-caking products by mixing it together with possible other components into warm oil. was prepared as follows: 10.7 g ethylene diamine was mixed into 89.3 g of dry stearic acid in powder form. Thereby the temperature rose to 49 °C. The mixture was allowed to cool after which any formed clods were disintegrated. Thus a dry, finely divided and easily manageable product was formed, in the DSC-analysis of which a large endothermic peak was found at about 96°C and a small peak was found at the melting point of stearic acid, i.e. at 55 °C. By means of a thermic weighing apparatus it was established that during heating the weight of the sample started to sink above about 100 °C, at first gently but above about 160 °C more steeply. This shows that the sample contained carboxylic and amino groups, in the reaction of which water was released. Also other solid mechanical mixtures of solid compounds according to the invention, such as adipinic acid and stearylic amine are similarly suited to be used as anti-caking agents. In this case the compound according to the invention is primarily formed only when the mixture is dissolved in warm oil. Example 13 (concentrate in oil) 44.6 g of stearic acid was melted into 50 g of oil at about 55 °C. Then 5.36 g of technical ethylene diamine was added to the mixture. After cooling a yellowish suspension was obtained in the DSC-analysis of which an endothermic peak was found at 93 °C. By means of thermic weighing device it was established that when heating the sample its weight started to decrease above about 100 °C, at first gently and above about 160 °C more steeply.

Claims: CLAIMS 1. An anti-caking agent for a granular product, characterized in that it is a salt having the general formula (Ia): Rl-AB-R 2 -BA-Rι (Ia) or the general formula (Ib): R1 -BA-R9-AB-R1 (lb) in which the groups R\ independently represent monovalent hydrophobic organic groups, the group R2 represents divalent hydrophobic organic groups, the groups A represent independently anionic groups and the groups B represent independently cationic groups. 2. An anti-caking agent according to claim 1, characterized in that the cationic groups B represent -onium groups, and preferably at least one, in particular both represent ammonium ion groups. 3. An anti-caking agent according to claim 1 or 2, characterized in that the anionic groups A represent anionic groups made from acids substituted with an organic moiety, and preferably at least one, in particular both represent a carboxylate ion group. 4. An anti-caking agent according to claim 1, 2 or 3, characterized in that the group Rj is a hydrocarbyl group, preferably a hydrocarbyl group having at least 7 carbon atoms, in particular a hydrocarbyl group having 10-22 carbon atoms. 5. An anti-caking agent according to any ofthe previous claims, characterized in that R2 represents a hydrocarbylene group having 1-22 carbon atoms, preferably a hydrocarbylene group having 2-8 carbon atoms. 6. An anti-caking agent according to any of the claims 1-5, characterized in that it is a salt having the general formula (II): Rl-N(R3R4R5) + -OOC-R2-COO- + N(R4R 5 R6)-Rι (II) in which Rl and R2 are the same as above and R3, R4 and R5 represent hydrogens and alkyl groups having 1 or 2 atoms, and preferably all of the groups R3, R4 and R5 represent hydrogens. 7. An anti-caking agent according to any ofthe claims 1-5, characterized in that it is a salt having the general formula (III): Rl -COO- + N(R3R4R 5 )-R -N(R4R5R6) + -OOC-Rι (III) in which Rl and R2 are the same as above and R3, R4 and R 5 represent hydrogens and alkyl groups having 1 and 2 atoms, and in particular all of the groups R3, R4 and R5 represent hydrogens. 8. An anti-caking agent, characterized in that it contains 0,2-20% by weight, preferably 0,5-5% by weight of a salt having the general formula (Ia) or (Ib) in addition to oil or wax, possible fillers and other anti-caking agents, protecting agents and additives. 9. An anti-caking agent according to any of previous claims, characterized in that it for the purpose of adjusting the charge ofthe salt R1-AB-R2-BA-R1 or R1-BA-R2-AB-R1 additionally contains about 5-100 mole % of an excess of an anionic or preferably a cationic surface active compound. 10. A method for the preparation of an anti-caking agent for a granular product according to any of the previously described claims, characterized in that a compound having the formula (IV) : Rl-Ao (IV) is reacted with a compound having the formula (V): B0- 2-B0 (V) to form a salt having the formula (Ia): R1-AB-R2-BA-R1 (Ia) or a compound having the formula (VI): Rl-Bo (VI) is reacted with a compound having the formula (VII): A0-R2-A0 (VII) to form a salt having the formula (Ib): R1-BA-R2-AB-R1 (Ib) in which the groups Ao of the formulae (Ia), (Ib), (IV), (V), (VI) and (VII) represent anionic groups, the groups Bo represent cationic groups, the groups R] represent monovalent hydrophobic organic groups, the groups R2 represent divalent hydrophobic groups, the groups A represent anionic groups formed by the corresponding groups Ao and the groups B represent cationic groups formed by the corresponding groups Bo- 11. A method according to claim 10, characterized in that the groups BQ represent groups belonging to the -onium ion group, and preferably at least one and in particular two of the groups BQ represent an amino group or its ammonium salt. 12. A method according to claim 10 or 1 1, characterized in that the groups Ao are selected among the anionic groups constituting of acids with organic substituents, and preferably at least one and in particular two of the groups Aø are carboxylic acids or salts thereof. 13. A method according to claims 10, 11 or 12, characterized in that Ri is a hydrocarbyl group, preferably a hydrocarbyl group containing at least 7 carbon atoms, in particular a hydrocarbyl group containing 10-22 carbon atoms. 14. A method according to any of the claims 10-13, characterized in that R is a hydrocarbylene group having 1-22 carbon atoms, preferably a hydrocarbylene group having 2-8 carbon atoms. 15. A method according to any of the claims 10-14, characterized in that a compound RJ-AQ having the formula (VIII): Rl-COOH (VIII) or its reactive salt, is reacted with the compound B0- 2-B0 having the formula (IX): H 2 N-R 2 -NH 2 (IX) or with its ammonium salt, where Ri and R2 are the same as above. 16. A method according to any of the claims 10-14. characterized in that a compound R] -Bo having the formula (X) Rl-NH 2 (X) or its ammonium salt is reacted with the compound A0-R2-A0 having the formula (XI) HOOC-R2-COOH (XI) or its reactive salt, where R\ and R2 are the same as above. 17. A method according to any of the claims 10-16, characterized in that the molar ratio R\ :R of the compounds to be reacted differ by 1-60%, preferably by 1- 20%, in any direction of the 2: 1 stochiometric ratio. 18. A method according to any of the claims 10-17, characterized in that the reactants, which preferably are an acid and an amine, are each added to a separate oil batch under simultaneous mixing and possible heating, or by adding the reactants to the same oil batch followed by possible heating. 19. A method according to any of the claims 10-17, characterized in that the reactants are either each added to a separate solvent batch, which are then combined, or added to the same solvent batch forming a salt after evaporation of the solvent. 20. A method according to any of the claims 10-17, characterized in that the reactants which preferably are an acid salt and an ammonium salt, are either each added to a separate water batch, which are then combined, or added to the same water batch followed by separating the precipitated product from water. 21. A method according to any of the claims 10-20, characterized in that the reactants are added to the coating of the particles of the granular product and reacted in the increased coating temperature environment of the particles. 22. The use of a salt having the general formula (Ia): or the general formula (Ib): R!-BA-R 2 -AB-R! (Ib) in which the groups R\ independently represent monovalent hydrophobic organic groups, the group R2 represents divalent hydrophobic organic groups, the groups A represent independently anionic groups and the groups B represent independently cationic groups, as an anti-caking agent for a granular product or as a component of said agent. 23. The utilization according to claim 22, whereby an oily or ceraceous coating agent mixture is heated to produce a liquid, low-viscous mixture which readily dissolves and disperses the afore mentioned salt and which subsequently can be spread onto the surface of the particles of the granulate product by spraying in the form of fine droplets. 24. A granular product, characterized in that the particles of the product are treated with an anti-caking agent, which is a salt having the following formula (Ia): or the general formula (Ib): Rl-BA-R 2 -AB-Rι (Ib) in which the groups Ri independently represent monovalent hydrophobic organic groups, the group R2 represents divalent hydrophobic organic groups, the groups A represent independently anionic groups and the groups B represent independently cationic groups. 25. A granular product according to claim 24, characterized in that the salt has the general formula (II): Rl-N(R3R4R5) + -OOC-R2-COO- + N(R4R 5 R6)-Rι (II) in which Rl and R2 are the same as above and R3, R4 and R5 represent hydrogens and alkyl groups having 1 or 2 atoms, and in particular all of R3, R4 and R5 represent hydrogens. 26. A granular product according to claims 24 or 25, characterized in that the salt has the general formula (III): R ] -COO- + N(R 3 R4R5)-R2-N(R4R5R6) + -OOC-R 1 (III) in which Rl and R2 are as previously defined and R3, R4 and R5 represent hydrogens and alkyl groups having 1 and 2 atoms, and in particular all of R3, R4 and R5 represent hydrogens. 27. A granular product according to claims 24, 25 or 26, characterized in that the coating of the particles is treated with a mixture containing in addition to said salt also oil or wax, possibly fillers and other anti-caking agents, protecting agents and additives. 28. A granular product according to any of the claims 10-17, characterized in that it is a fertilizer, preferably a N-P-K fertilizer.

Inventors: AHLNAES THOMAS, KANKAANPAEAE TEIJA, LOEFGREN TIMO, AHLNAES, THOMAS, KANKAANPAEAE, TEIJA, LOEFGREN, TIMO
Applicants: AHLNAES THOMAS, KANKAANPAEAE TEIJA, KEMIRA AGRO OY, LOEFGREN TIMO, AHLNAES, THOMAS, KANKAANPAEAE, TEIJA, LOEFGREN, TIMO
Application year: 1996
Main classification: C05G3
IPC codes: B01J2, C05G3