METHODS FOR THE DESIGN, QUALITY CONTROL, AND MANAGEMENT OF FATIGUE-LIMITED METAL COMPONENTS

Abstract: Improved methods for managing a population of metal components subject to fatigue failure are provided. The residual compressive stress in the critical surfaces of such components, especially in areas of high stress concentration, are measured non-destructively using x-ray diffraction techniques. The measured surface residual compressive stress is used as a management criterion. A component having a surface residual compressive stress greater than a predetermined value can be returned to service. However, once the measured surface residual compressive stress of a component falls below the predetermined value, it can either be removed permanently from service, or it can be reworked to increase its surface residual compressive stress and then returned to service. Additionally, by measuring the surface residual compressive stress of an individual component, the remaining service life of that individual component can be estimated. These methods for management of polulations of such metal components allow for increasing the service life of the components in a safe and effective manner. Methods are also provided for the manufacture and/or design of metal parts with improved performance criterion (e.g., reduction in weight) while maintaining acceptable service life. Methods are also provided for establishing quality control procedures using surface residual compressive stress measurements during and/or after the manufacturing process in order to prevent, for example, introduction of metal parts having insufficient surface residual compressive stress levels for their intended use.

Description: Methods for the Design, Quality Control, and Management of Fatigue-Limited Metal Components Related Application This is a continuation-in-part application of U.S. Patent Application Serial Number 08/245,011, filed May 18, 1994, entitled "Method for Measuring and Extending the Service Life of Fatigue-Limited Metal Components, " which is hereby incorporated by reference. Field of the Invention This invention generally relates to methods for managing the service life of fatigue-limited metal components. This invention also generally relates to a method for managing and extending the service life of fatigue-limited metal components. More specifically, this invention is related to a management method using a non-destructive technique for measuring the remaining useful service life of fatigue-limited metal components by determining the residual compressive stress in the critical surfaces of the individual components. Using the method of this invention, a metal component is removed from service or reworked to increase its residual compressive stress once the residual compressive stress is reduced or falls below a predetermined value. This invention allows an increase in both safety and economy in the management and operation of turbine engines and other machines containing fatigue-limited metal components by providing a reliable means for non- destructively measuring the remaining service life of the fatigue-limited metal components. This invention is especially adapted for managing populations of fatigue- limited rotating parts in gas turbine engines, including aircraft engines, and the like. Using the present methods of this invention to manage and measure the surface residual compressive stress in such parts or components, it is now possible to determine the appropriate time (i.e., prior to permanent deterioration from tensile stress crack initiation) for reworking the part to increase or restore its surface residual compressive stress so that the service life of the part or component can be extended. Using the present methods of this invention, the overall service life of a population of components used in, for example, jet engines or turbine engines, can be maximized without a significant decrease in safety. In fact, the present invention can provide both increased safety and economy for the aviation and other industries. In another embodiment, this invention also generally relates to a method for designing fatigue- limited metal components with selected service life and performance (e.g. , weight) characteristics. More specifically, this embodiment provides a method in which the surface residual compressive stress measurements of a component during manufacture and/or design are used to guide manufacture and/or design so that the component can be manufactured and/or designed to have suitable and predictable service life while adjusting a performance criterion ( e.g. , reducing the weight) or several performance criteria of the component. In effect, a selected performance criterion (or several selected performance criteria) and service life of the component can be balanced to achieve optimum or near optimum performance/service life characteristics for specific components. Using weight reduction as the primary performance criterion, for example, such a method should be especially useful in military fighter aircraft where weight concerns are especially important, more limited component service lives are acceptable, and more frequent inspections are justified. Surface residual compressive stress measurements after one or more appropriate manufacturing step in the manufacturing process can also be used for quality control purposes. Background of the Invention Fatigue-limited metal components of gas turbines or jet engines, or other machine components subject to metal failure or fatigue, must be carefully managed in order to avoid failure during operation. The failure, for example, of a critical component of a jet engine during operation may result in loss of life or other catastrophic consequences. Currently in the aviation industry (commercial and military) , there are three general types of management techniques or approaches used for the management of fa igue-limited machine components in order to prevent possible catastrophic failure due to metal fatigue. Each of these approaches attempts to balance safety and economic concerns based on available data. See, for example, S. Suresh, Fatigue of Metals. 499-502 (1991) , which generally discusses the three commonly used management approaches. The most conservative of these approaches, often termed the "safe life" approach, is based on the estimated fatigue life established through analysis and comparable experience by the engine manufacturer. This approach attempts to estimate the point at which the shortest-lived part or component in the total population would be expected to fail. After allowing for a suitable safety margin, an arbitrary retirement point is adopted for that component. This retirement point is normally measured in total take-off cycles or hours. Once a part reaches the retirement point, it is removed from service and mutilated to prevent further, unauthorized use. Although generally allowing for the greatest margin of safety, significant economically useful service life of such parts is lost. In effect, this "safe life" approach is based on, and controlled by, an estimation of the lifetime of the weakest part or component in the total population. A somewhat less conservative management technique is the so-called "fail safe" approach. In this approach, a maximum service life is determined by the total accumulated service hours or cycles (whichever is shorter) at which the first crack is detected in an actual part (e.g. , disk or drum rotor used in a compressor, turbine, or engine) in the population of like parts. Once a part has developed such a crack, its accumulated service life (in hours or cycles) is effectively used to determine the allowable service life of all similar parts in the population. If a part is later found to develop a crack at an earlier time, then that part is used to redefine (and shorten) the acceptable service life limits of the population. Once a part reaches its acceptable service life, it is removed from service and mutilated to prevent further use. In effect, this "fail safe" approach is also based on, and controlled by, the actual weakest part or component in the total population. Many parts may still have many hours of safe and useful service life remaining beyond that of thiε weakest part. But, since the useful and safe service life of these parts cannot be reliably determined, they must be removed from service in the interest of safety. This "fail safe" approach is generally used in the airline industry for mature fleets where low cycle fatigue cracks have been detected in the relevant component populations. Where sufficient service data have not been developed, the more conservative "safe life" approach is generally used. In each approach, however, parts having many remaining hours of safe and reliable use will be removed from service. More recently, the United States Air Force has successfully adopted an even less conservative management technique, the so-called "retirement for cause" approach, for its management of some critical engine components. In this approach, the parts are periodically examined non-destructively for cracks and other defects using, for example, fluorescent dye penetration, magnaflux, radiographic, or eddy current techniques. Once a crack is observed, that part, but only that part, is immediately retired from service. Other parts, even though they may have accumulated service times equal to or greater than the retired part, are continued to be used until they actually develop cracks. To operate safely, thiε approach requires frequent and periodic inspections of the individual parts. In general, as parts age, the frequency of inspections should be increased. In any event, the frequency of inspections must be such that the period between inspections is less, preferably by a significant margin, than the time normally required for a detectable crack to further deteriorate to the point of actual failure. Although this approach may result in more frequent teardowns for inspection of the individual parts, the potential savings based on achieving, or at least approaching, the maximum lifetimes of the individual parts can be enormous. The major drawback of this approach is that it relies upon detection of an actual crack in the part. Thus, this approach is generally not suitable for parts in which crack formation cannot be detected in a reliable and consistent manner. Once a crack has formed, the part contains, in effect, a permanent, irreversible defect which will ultimately lead to failure, perhaps catastrophic failure, unless that part is removed from service in a timely manner. Additionally, this approach, of course, is not suitable for use where the normal time between the initial development of a detectable crack and failure of the part is relatively short. Moreover, in parts where actual failure normally does not follow quickly after the development of a crack, if such a crack develops shortly after an inspection, the risk of failure during actual operation increases simply because the length of time in which the part is operated with the defect is maximized. Therefore, this method has an increased safety risk when compared to the "safe life" and "fail safe" approaches. This increased risk, although perhaps small, may still be significant because the detection point iε the actual formation of a detectable crack. The longer that part remains in service, once a crack has formed, the greater the risk of catastrophic failure. It would be desirable, therefore, to provide non-destructive methods to measure the remaining service or useful life of fatigue-limited metal components before crack initiation has begun or, at least, before actual cracks can be observed (i.e. , before permanent and irreversible damage has begun) . It would also be desirable to provide methodε by which the service or useful life of fatigue-limited metal components could be increased without significantly increasing the risk of catastrophic failure of the metal componentε during operation. It would also be desirable to provide a method for manufacture and/or design of fatigue-limited metal components whereby the service life and selected performance criterion (e.g. , weight) of the metal components can be adjusted and balanced to desired interrelated levelε. It would alεo be desirable to provide a non-destructive method for determining the suitability of newly manufactured or reworked parts for their intended use. It would also be desirable to provide improved quality control methods or procedures for use in the manufacture of fatigue-limited metal components. Such methods would provide both increased safety and economy for the aviation industry (commercial and military) . The methods of this invention generally provide such improved methods. Summary of the Invention The present invention relates to methods for the management of populations of fatigue-limited metal components. This invention also relates to methods for the determination of the remaining service life of individual fatigue-limited metal components. The metal componentε to be managed by the present invention include metal components having relatively high levels of residual compresεive stress as manufactured and which are subject to fatigue-related failure. The relatively high residual compressive stress of such a metal component as manufactured may be the result of the actual manufacturing process used and/or εubsequent working of the metal component by shot peening or other cold working processes after actual production to increase the residual compressive εtreεs. Preferably, the residual compressive stress as manufactured is in the range of about 50,000 to 200,000 pounds per square inch and, more preferably, in the range of about 150,000 to 180,000 pounds per εquare inch. Components having residual compresεive stresεeε higher or lower than these ranges can, of course, be managed by the methods of the present invention. However, the components as manufactured should have sufficient residual compressive stresε for their intended uεe. Using the methods of this invention, increases in both εafety and economy in the management of such metal components are expected. In another embodiment, this invention also relates to methods for the manufacture and/or design of fatigue-lirr.ited metal components whereby the surface residual compreεεive εtresseε are monitored and adjusted during manufacture and/or design to yield components having improved performance criterion (e.g. , reduced weight) but still acceptable surface residual compressive stresεes and, thus, acceptable service lifetimes. These methods can also be used during the manufacturing procesε to track and assesε individual process stepε by measuring the surface residual compresεive streεε and comparing it to deεign or target levelε throughout the proceεε. These values can also, if desired, be included in total stress calculations and/or a database for the components to assist in improving, evaluating, and/or understanding component design and performance. Components manufactured and/or designed using this method can then be, if desired, managed in service using the other methods diεcloεed and deεcribed herein for the management of populationε of fatigue-limited metal components. In still another embodiment, this invention also relates to quality control methods whereby the residual compreεεive εtress condition of one or more critical εurfaceε areas is determined prior to entry of that part into service or at various εtages during the manufacturing process. Partε having inεufficient εurface residual compreεεive stress levels for their intended purpose could either be withheld from εervice (and destroyed) or, if appropriate, reworked to increase the surface residual compresεive stresε of the part to acceptable levelε. By avoiding placing partε into service with lesε than acceptable εurface reεidual compressive stress levels and/or reducing the scatter or range of the residual compresεive streεε levelε of parts placed into service, increased safety margins and economies can be obtained. Such quality control methods can also be used during the manufacturing procesε by measuring the residual compressive stress condition of one or more critical surfaceε areaε at various stageε of the manufacturing process and using that measurement to determine whether that component (perhaps with reworking at that or later stages) can be continued in the manufacturing process. By early elimination of components not likely to pass final inspection or quality control requirements, considerable saving could be maintained. Moreover, increased quality control measures at various manufacturing stages will likely result in increased safety margins since potentially defective parts are more likely to be identified before entry into service. Such quality control methods can be used, if desired, on only one or only a few manufacturing steps in the process (e.g. , control and evaluation of the shot peening process only) . Fatigue failures in metal components almost always develop from cracks generated in the surface layer of the metal components exposed to high stress environments. To reduce the likelihood of crack formation, great care iε normally taken in the manufacture of εuch metal componentε to enεure that the initial residual stress in the critical surface layers of the crystalline εtructure of the metal are in relatively high compreεsion (often up to 170,000 pounds per square inch or higher) . Since these initial streεε levelε are not currently meaεured for the aε-manufactured partε, it iε poεsible that parts having less than acceptable residual compressive stress levels could be placed into service. During operation under conditions of high load and operating temperatures, the residual compresεive stresε of the component gradually diminishes over time. Once the residual compressive stress reaches zero, the trend continues and builds up residual tensile streεε in theεe areas. Over time, the residual tensile stress can increase to levelε in exceεs of the ultimate tensile strength of the surface of the material and cracks develop. Such crackε in a component left in service propagate until they reach a critical length, at which time catastrophic failure occurs. If such a part is placed into service with less than acceptable surface residual compressive stress values, catastrophic failure may occur (or at least be at increased risk to occur) before the first scheduled inspection. The present invention provides methodε for managing metal components whereby conditions involving significant residual tensile stress and, therefore, crack initiation are avoided. By monitoring the residual compressive streεε in areaε of high εtreεs concentration and maintaining the metal component under conditions of compressive stress, the present invention provides a management program which does not rely on either expected or actual crack formation aε the management criterion. Further, the preεent invention provideε a quality control method whereby the actual reεidual compressive streεs levelε in as-manufactured parts (and/or at critical stages of the manufacturing process) are measured so that parts without sufficient surface reεidual compressive streεε for their intended purpoεeε are identified (and corrected) before being placed into εervice. In the method of thiε invention, a non- deεtructive technique (i.e. , x-ray diffraction) iε uεed to measure the remaining residual compresεive εtreεε in the relevant metal components. Once the residual compressive streεε of an individual component falls below a predetermined value, that part, but only that part, is effectively flagged for further attention. For metal components having residual compreεsive εtreεε below a predetermined value, there are eεεentially two optionε. In the first option, the metal component is simply removed permanently from service. In the second option, the metal component is reworked (using, for example, shot peening) to increase its residual compressive stresε to an acceptable level and then returned to service. By periodically evaluating such metal componentε using the methods of this invention, the service life of the total population of metal components can be maximized in a safe and efficient manner. For metal components having residual compressive stress higher than the predetermined value, the remaining service life of that component can be determined. The greater the difference between the measured residual compressive stress and the predetermined value, the greater the remaining service life for that component should be. Such information should be useful (especially as conεiderable hiεtorical data for the population become available over time) in matching componentε for uεe in particular engineε or applicationε (i.e. , matching componentε which have comparable remaining service life) or for scheduling routine teardowns and maintenance. I n the method of the present invention directed to manufacture and/or deεign/development of fatigue- limited metal components, the surface residual compresεive stress is monitored during the manufacture and/or design/development proceεs and used as a guide to obtain metal components having, for example, reduced weight but acceptable strength and service lifetimes. By measuring the surface residual compressive stresses during various stages of the manufacturing and especially during the course of the design and/or development process, the minimum (or near minimum) weight necessary for a given part or area of a part can be achieved while still maintaining an acceptable residual compressive streεs in the critical εurface areaε of the part. Thus, using this method it is possible to manufacture and/or II deεign fatigue-limited metal componentε with reduced weightε and acceptable service lifetimes and inspection/maintenance schedules. This method will be especially uεeful in manufacturing and/or designing metal componentε (e.g. , jet engine diskε) for military aircraft. In effect, the design process of this invention allows the total stress (applied plus residual stresseε) of the component during uεe to be taken into account in the deεign and/or manufacture procedureε. In prior art design proceεεes, generally only the applied stress could be taken into account. One object of the present invention iε to provide a method for managing a population of metal partε in order to determine when to remove an individual metal part from εervice, wherein said metal parts are manufactured having relatively high levels of residual compressive stress and said metal parts are subject to fatigue-related failure, said method comprising: (1) selecting an individual metal part from the population; (2) determining the remaining residual compresεive εtreεs of the surface of the selected individual metal part in one or more areas of stress concentration using x-ray diffraction techniques; and (3) removing the selected individual metal part from service if the remaining residual compressive stress measured in one or more areas of streεε concentration has fallen below a predetermined level. Another object of the present invention is to provide a method for managing a population of metals parts in order to extend the service life of individual metal parts in the population, wherein said metal parts are manufactured having relatively high levels of residual compressive stress and said metal parts are εubject to fatigue-related failure during service, said method comprising, for each individual metal part in the population: (1) removing the individual metal part from the population from service; (2) measuring the remaining residual compressive stress of the surface of the individual metal part in one or more areas of stress concentration using x-ray diffraction techniques; (3) comparing the remaining residual compressive stress measured in one or more areas of stress concentration to a predetermined level; and (4) if the remaining residual compressive stress remains above the predetermined level, returning the individual metal part to service; or (5) if the remaining residual compreεεive εtreεs iε at or below the predetermined level, reworking the individual metal part to increaεe the residual compreεεive stress to a reworked level above the predetermined level and then returning the individual metal part to service. Although the present invention iε preferably directed towardε methods for the management of large populations of similar type metal parts, it can also be used to test individual metal parts. Thus, for example, the present invention can also be used for εpot checking metal partε throughout their expected εervice life aε part of routine or εcheduled preventive maintenance or during repairε or teardown procedureε neceεεitated by breakdownε. Thuε, still another object of the present invention is to provide a method for determining when to remove a metal part from service, wherein said metal part is manufactured having relatively high levels of residual compreεsive stresε and said metal part iε subject to fatigue-related failure, said method comprising: (1) meaεuring the remaining reεidual compreεsive stress of the surface of the metal part in one or more areas of stress concentration using x-ray diffraction techniques; (2) comparing the remaining residual compressive stresε meaεured in one or more areas of high stresε concentration to a predetermined value; and (3) removing the metal part from service if the remaining residual compressive stress measured in one or more areas of stress concentration is less than the predetermined level. Still another object of the present invention is to provide a method for extending the service life of a metal part, wherein said metal part is manufactured having relatively high levels of residual compressive stress and said metal part is subject to fatigue-related failure during εervice, said method comprising: '1) measuring the remaining residual compresεive εtreεε of the surface of the metal part in one or more areas of stress concentration using x-ray diffraction techniques; (2) comparing the remaining residual compressive εtreεε meaεured in one or more areas of εtreεε concentration to a predetermined level; and (3) if the remaining reεidual compreεεive εtress remainε above the predetermined level, returning the metal part to service; or (4) if the remaining residual compressive stress is at or below the predetermined level, reworking the metal part to increase the residual compressive stress to a reworked level above the predetermined level and then returning the metal part to service. Still another object of the present invention is to provide a method for designing a fatigue-limited metal part whereby a selected performance criterion for the metal part is improved while maintaining sufficient residual compressive stress to achieve an acceptable service life for the metal part, said method comprising: (1) providing a prototype of the metal part; (2) measuring the residual compressive stress in one or more critical surface areas of the prototype during the course of design of the metal part; (3) modifying the prototype using the difference between the measured residual compressive streεε and a predetermined reεidual compressive stresε design level as a guide to improve the selected performance criterion; (4) remeasuring the reεidual compressive stresε in the one or more critical surface areas of the modified prototype to determine the remeaεured residual compressive stress in comparison to the predetermined residual compressive streεε deεign level in order to gauge the effect of the modification; and (5) repeating steps (2) through (4) for the one or more critical surface areas until an acceptable and functional metal part iε obtained, wherein the acceptable and functional metal part haε itε selected performance criterion improved and haε εufficient reεidual compreεsive εtreεs in the one or more critical surface areas for its intended use. Still another object of the present invention is to provide a method for deεigning a fatigue-limited metal part whereby the weight of the metal part is reduced while maintaining sufficient residual compressive stresε to achieve an acceptable εervice life for the metal part, said method comprising: (1) providing a prototype of the metal part; (2) meaεuring the reεidual compreεεive εtress in one or more critical surface areas of the prototype during the course of the design of the metal part; (3) modifying the prototype using the difference between the measured residual compresεive εtresε and a predetermined residual compressive stress design level as a guide; (4) remeasuring the residual compressive stress in the one or more critical surface areas of the modified prototype to determine the remeasured residual compresεive streεε in compariεon to the predetermined residual compresεive εtreεε design level in order to gauge the effect of the modification; and (5) repeating stepε (2) through (4) for the one or more critical surface areas until an acceptable and functional metal part is obtained having reduced weight and sufficient residual compresεive stresε in the one or more critical εurface areaε for itε intended uεe. Still another object of the present invention is to provide a method for designing a fatigue-limited metal part whereby the weight of the metal part is minimized while maintaining sufficient residual compresεive εtress to achieve an acceptable εervice life and safety factor for the metal part, εaid method compriεing: (1) providing a prototype of the metal part; (2) meaεuring the reεidual compreεεive stress in one or more critical surface areas of the prototype during the course of the design of the metal part; (3) modifying the prototype by reducing its weight using the difference between the measured residual compreεεive εtress and a predetermined residual compresεive εtress design level as a guide; (4) remeasuring the residual compresεive εtreεs in the one or more critical surface areas of the modified prototype to determine the remeaεured reεidual compreεεive εtress in comparison to the predetermined residual compressive stresε deεign level in order to gauge the effect of the modification; and (5) repeating steps (2) through (4) for the one or more critical surface areas until an acceptable and functional metal part iε obtained having minimal weight and sufficient residual compressive stress in the one or more critical surface areas to achieve an acceptable service life and safety factor for the metal part. Still another object of the preεent invention iε to provide a quality control method for the manufacture of fatigue-limited metal componentε, said method comprising meaεuring the residual compresεive stress in one or more critical surface areas for each metal component after its manufacture and before placing it into service, comparing the measured residual compresεive εtress in one or more critical surface areas to a corresponding predetermined residual compressive stress level for the one or more critical surfaces, and flagging each metal component which haε its measured residual compresεive εtress below its corresponding predetermined residual compressive streεε level, whereby flagged metal componentε are not placed in εervice. For purpoεes of thiε invention, "after its manufacturing" is intended to include selected stages during the manufacturing procesε aε well aε after completion of the entire manufacturing process. Likewise, "placed into service" is intended to include continuing beyond a specific manufacturing stage where measurementε are made during the manufacturing stage aε well aε actual placement in service after completion of the manufacturing process. These and other objects and advantages of the present invention will be apparent from a consideration of the present εpecification and drawing. Description of Figures Figure l illustrates a typical disk from a jet engine showing areas of stress concentration in which residual compressive stress should be determined. Figure 2 shows a typical plot of residual compresεive stress as a function of εervice time for turbine diεks operating under different load and temperature conditions. Detailed Description of the Invention The invention generally relates to methods for managing the service life of fatigue-limited metal components and to methods for managing and extending the εervice life of fatigue-limited metal components. The methods of this invention employ a non-destructive technique for measuring the remaining useful service life of fatigue-limited metal components by determining the residual compresεive εtreεε in the critical εurfaceε of the individual component. The εurface reεidual compressive stresε can be correlated with the remaining εervice life of the individual component. If the εurface residual compressive stresε haε not fallen below a predetermined value, the component can be returned to service. If the surface residual compresεive εtreεε reacheε or fallε below a predetermined value, the component can be permanently removed from service. Or, if desired and appropriate, the component can be reworked to increase the surface residual compreεεive stress to a level above the predetermined value, preferably a value approaching the compressive stress of the component as originally manufactured, and then returned to service. It is well establiεhed that fatigue failures develop frc cracks generated in the surface layer of - ie - metal components exposed to high stress environments. For example, failure normally occurs becauεe of crackε forming in areaε of stress concentration in such components. Figure 1 illustrates such a component, specifically a disk 10 for use in a gas turbine engine. Failure of such a disk is often caused by cracks forming in the surface layers of areas of high stresε concentration εuch aε the inside radii or bottom 12 of dovetail or firtree slotε 14. Theεe dovetail or firtree slots are used for attachment of the compresεor and turbine bladeε (not εhown) . To reduce the likelihood of crack formation, great care iε normally taken in the manufacture of εuch componentε to enεure that the initial reεidual εtress in the critical surface layers of the crystalline structure of the metal are in high compression. (The actual value or level of the compresεion iε not, however, determined in current manufacturing procedureε. ) For example, turbine diεks, such as the one illuεtrated in Figure 1, are generally manufactured with reεidual compressive stress in the order of about 170,000 pounds per square inch. During operation in a turbine engine (i.e. , conditions of high load and operating temperatures) , the residual compresεive εtreεs gradually diminiεhes over time as shown in Figure 2. The curves in Figure 2 (labeled 20, 22, 24, 26, and 28) are for different turbine diεkε 10 (i.e. , different εtageε) used in a gas turbine engine. In εuch an engine, each disk is subjected to different load and temperature conditions during operation. Thus, the rate of decrease of the residual compresεive stresε iε different for each disk or stage. Once the residual compresεive stresε reacheε zero, reεidual tensile streεε can build up in these areas. Over time, the residual tensile stress can increase to levels in excesε of the ultimate εtrength of the εurface of the material and crackε will initiate. Such crackε in a component left in service propagate until they reach a critical length, at which time catastrophic failure will occur. Aε seen in Figure 2, the plot of reεidual compressive stress versus cycles is generally linear for a given component. Thus, residual compressive stress measurementε of a given component which fall significantly off that part's linear curve may suggest a significant deviation or problem. For example, once a component departs significantly from the expected curve, the component may, for example, be moving from its elaεtic regime and into itε plaεtic regime. Such deviationε might alεo reεult from εcatter in the original (i.e. , aε-manufactured) residual compresεive εtress conditions since componentε with εignificantly different initial residual compressive streεs levels might have significantly different linear curves. Whatever the cause of the departure (even if the residual compresεive εtreεs value has not fallen below the predetermined value) , the part should be examined more carefully and appropriate action taken (i.e. , removed from service, reworked, or repaired as appropriate) . The methods of this invention monitor the residual compresεive εtreεs in surface areas of streεs concentration in order to prevent the initial formation of crackε in the εurface. By removing the component from εervice before the stresses change from compressive to tensile in nature or by maintaining the εtress in compression, the present methods allow individual components to be used in a manner in which surface cracks are not formed or are, at least, formed at a significantly lower rate as compared to current management methods. The preεent methodε allow for achievement of the maximum εervice life of components without increased failure or safety risks. Moreover, the present methods allow for significantly extending the service life of individual components without increased failure or safety riskε. In practice, for a given type and population of metal compcnents, the residual compressive stress in the surface layer of the individual component is measured in one or more areas of stress concentration using x-ray diffraction techniques. The actual area measured is normally in the range of about M by M inches to about 1 by 1 inch, although smaller or larger areas can be used if desired. Generally it is preferred that the x-ray diffraction measurements be taken approximately normal to the relevant surface. Generally it is also preferred that the multiple x-ray meaεurementε be taken within the relevant εurface area εo that the cryεtalline εtructure of that surface area can be better probed. The measured value (or values or averaged value) is compared to a predetermined value. If the measured value is above the predetermined value, the part can be returned to service. If however, the measured value equals or falls below this predetermined value, the component can be treated in several ways. In a first option, the component can be permanently removed from service. In such cases, it is generally preferred that the component be mutilated, or otherwise marked, to prevent further, unauthorized use. In a εecond option, the component can be reworked to increase its residual compresεive εtress and then returned to service. Normally, such a component can be reworked and returned to service a fixed number of timeε or cycles (i.e. , until other failure mechanisms predominate or the component no longer meets design criterion or εpecificationε) . The acceptable number of cycleε for reworking εuch componentε will generally be determined on a caεe-by-caεe baεiε. For a given component, εuch as the diεk shown in Figure 1, the cycle of service and reworking can generally be repeated so long as the component retains its dimensional and microstructural stability. In some caεes when the residual compressive stresε iε above, but close to or approaching, the predetermined value, it may be preferred to rework that part at that time rather than wait for the residual compression stress to fall below the predetermined value. For example, if the measured residual compressive stresε εuggeεtε that the part haε only a relatively short service life remaining before reworking will be required (see, for example, curve 22 in Figure 2 at 15,000 hours with a predetermined value of zero pounds per εquare inch) , it may be more economical to rework the part during the current scheduled shutdown/teardown event rather that put the part back in εervice and then require an unεcheduled teardown to rework it only a εhort time later. Whether thiε modified approach iε appropriate and deεirable in a given caεe will depend, in larger part, on the expected εervice life before that part will fall below the predetermined value. If the expected remaining εervice life iε εhort (thereby neceεεitating a unscheduled teardown for remeasurement) , it may be more economical to rework that part even though it haε remaining service life. In such a case, the predetermined value is effectively increased for that part only. Aε one εkilled in the art will realize, the predetermined value of the εurface residual compresεive streεs for any given population of components will depend, at least in part, on the surface residual compressive εtreεε of the components aε originally manufactured, the εpecific phyεical and metallurgical characteristics of the components, the environment in which the components are used, and any appropriate safety factors. For populations of different parts, this predetermined value will likely be different becauεe of different designs and/or geometries of the parts and exposure to different stresses during use. Populations of the same parts, but operated under different conditions and environments, may also have different predetermined values. Moreover, for a given component, different areas of stress concentration may have different predetermined values. For example, different areas of metal component will normally be exposed to, or will experience, different levels of stress and may, therefore, experience changes in the compresεive εtress at different rates. In such cases, the area that reaches its predetermined value first will normally control the disposition of that component. It will generally be preferred that the initial surface residual compreεsive streεs of the metal components be measured or otherwiεe known before they are placed in service, or shortly thereafter. Meaεurement of the surface residual compresεive εtreεε of a component aε originally manufactured can help insure that only components meeting specifications are used and can provide benchmarks for later measurementε of remaining surface residual compressive stress. Moreover, such initial surface reεidual compressive streεε data, along with the data generated by the preεent methods, can be used to define or redefine component specifications and design criterion as appropriate. Moreover, aε detailed herein, εuch initial εurface reεidual compreεεive stress measurements can form an integral part of a comprehensive quality control program. The predetermined value can be expressed in terms of absolute numbers (e.g. , a specific value in suitable units for the residual compressive streεε) or in relative numbers (e.g. , a percentage of the remaining compressive streεε of the component as compared to the reεidual compreεεive stress as originally manufactured) . Moreover, the predetermined value for a given population may change over time as more historical data become available. For example, for newly designed components, it may be desirable to use a relatively high predetermined value to guard against unexpected failures for increased safety. As service life data become available, however, it may be appropriate to decrease the predetermined value if significant safety or failure related problems are not found in the population. By carefully adjusting the predetermined value for a given population of components over time, it should be posεible to approach the optimum value while maintaining operational safety. In some caseε, a predetermined value of about zero pounds per square inch (or other appropriate units) or 100 percent decrease in reεidual compreεεive stresε (i.e. , the point at which εtress moves from compresεive to tensile in nature) may be appropriate. The use of zero pounds per εquare inch or 100 percent decreaεe aε the management criterion might, for example, be appropriate to maximize the εervice life of a component where reworking the component iε not practical or iε otherwiεe not anticipated. In moεt caεeε, however, a predetermined value of a value greater than zero poundε per εquare inch or leεs than 100 percent decrease will generally be preferred and appropriate based on safety considerations. Such higher predetermined values will be especially preferred where reworking of the component to restore all or part of the residual compresεive stress is anticipated. In some cases, however, a predetermined value of less than zero pounds per square inch or greater than 100 percent decrease may be appropriate. As noted above, the residual compressive stress is measured non-destructively using conventional x-ray diffraction techniques. Preferably, the residual compressive stress is measured using portable x-ray diffraction equipment. Examples of such x-ray equipment and techniques can be found in U.S. Patent 4,095,103 (June 13, 1978); U.S. Patent 4,561,062 (December 24, 1985); U.S. Patent 4,686,631 (August 11, 1987); U.S. Patent 5,125,016 (June 12, 1992); Taira & Tanaka, "Residual Stresε Near Fatigue Crack Tips," 19 Transactions of the Iron & Steel Inεtitute of Japan, 411- 18 (1979); Harting & Fritsch, "A Non-destructive Method to Determine the Depth-dependence of Three-dimensional Residual Stresε Stateε by X-ray Diffraction, " 26 J. Phyε. D: Appl. Phyε.. 1814-16 (1993); Kuhn et al. , "An X-ray Study of Creep-deformation Induced Changes of the Lattice Mismatch in γ' -Hardened Monocrystalline Nickel-Base Superalloy SRR 99," 39 Acta Metal1. Mater.. 2783-94 (1991) , all of which are hereby incorporated by reference. Portable x-ray equipment, which is generally preferred in the present invention, can be obtained commercially from, for example, Technology for Energy Corporation (P.O. Box 22996, Lexington Drive, Knoxville, Tennesεee 37933); or American Streεε Technologies, Inc. (61 McMurray Road, Pittsburgh, Pennsylvania 15241) ; or Proto Manufacturing Limited (2175 Solar Creεcent, Oldcaεtle, Ontario, Canada NOR 1L0) . Other typeε and deεignε of x-ray diffraction equipment or techniques can also be used in the present invention. Normally such measurementε εhould be made, at a minimum, during scheduled teardowns and other maintenance events. In some caseε, however, it may be desirable to make such measurements more often than regularly scheduled maintenance events, especially during the early service life of a population of newly designed components lacking a extensive service life history. Normally, such measurements of the residual compressive stress will be made on the individual parts during teardowns. For some components, however, it may be possible to make the necessary measurements without having to perform complete teardowns. As noted above, x-ray diffraction measurementε of reεidual compreεεive stresε should be made in areas of high stress concentration (e.g. , the bottom 12 of the firtree slots 14 on the disk 10 shown in Figure 1) . Generally, areas of high stress concentration are those areas in which crack formation has been observed or is more likely to occur. It is not necessary, however, to make such measurements in each and every area of high stress concentration in a given component, especially where such areas are operated under similar load and temperature conditions. For the diεk in Figure 1, for example, meaεurements might be taken on the bottom 12 of the firtree slots 14 located at 0, 90, 180, and 270 degrees, rather than at the bottom of every slot 14. The individual measurements at these representative locations, or an average of the individual measurements, are compared to the predetermined value. As the database developε, the number and location of meaεurements for a given disk (or other population of components) can be modified aε appropriate. Once a component reacheε or falls below its predetermined value, it can either be removed permanently from service or reworked to increase its residual compreεεive εtress to a level above the predetermined value and then returned to service. For example, using a predetermined value of zero pounds per square inch, the disk represented by curve 28 in Figure 2 should be removed from service or reworked after about 10,000 hourε of εervice; the diεkε repreεented by curveε 24 and 26 εhould be removed from εervice or reworked after about 15,000 hourε; the disks represented by curves 20 (especially) and 22 (to a lesser extent) have service lives greater than 15,000 hours. Preferably, the residual compressive stress in such reworked components is returned to a level approaching the original residual compressive stress as manufactured. Reworking such components can be carried out uεing conventional procedureε for increasing or achieving residual compressive stresε. Such methods include, for example, shot peening and other methods of cold working the surface (e.g. , hammer peening, laser peening, rolling, or burnishing methods) . See, for example, Daly, "Statuε of Controlled Shot-Peening Technology in the United Stateε," International Conference on Impact Treatment Processes (2nd: 1986) in Impact Surface Treatment (Meguid, Ed.), 237-41; Delitizia, "Improving Fatigue Life Through Advanced Shot Peening Techniques, " 92 Manufacturing Engineering, 85-87 (1984) . Of course, such reworking must be carried out before any permanent deterioration occurs from reεidual εtress cracking. Thus, where such reworking is anticipated, the predetermined value used as the management criterion preferably is higher (i.e. , a higher predetermined value of residual compreεεive εtreεε) than in caεeε where reworking iε not anticipated. By setting the management criterion higher in such cases, one moves further away from the condition where crack formation, which may not even be detectable, may occur, thereby providing an increased margin of safety. It is generally preferred that reworking increases the residual compresεive stress to at least 50 percent of the residual compressive stress in the part as originally manufactured. More preferably, the rework level for the residual compressive stress is at least 80 percent of the value as originally manufactured. Even more preferably, the reworked level is comparable to the value as originally manufactured. The methods of this invention generally allow one to maximize the service life of a metal component by providing a procedure to determine when to optimally rework the metal component to restore all or part of the residual compressive stress. Excessive reworking can actually decrease the service life since reworking techniques such aε shot peening can increase the dimension of the metal part in the reworked area. Thus, the likelihood of a metal component moving out of its design specification increases as a function of the number of times it is reworked. The present invention provides procedures whereby the maximum service life can be obtained with the minimum number of reworkings. Of course, the effect of reworking on dimensional stability should be taken into account when establiεhing the appropriate predetermined value for a given component. The preεent methodε for management of population of metal componentε provide conεiderable improvement over management methodε currently in uεe. Both the "εafe life" and "fail εafe" methodε rely on expected εervice life baεed on either predicted valueε or statistical values of crack formation in the weakest component in the population. In theεe methods, service life is not evaluated for individual components. Thus, the vast majority of components are retired while still possessing useful and significant service life. The "retirement for cause" approach relies on the observation of actual crack formation in a given component. Once crack formation is observed, that component is removed from service. Unfortunately, once crack formation can be observed, the component cannot be rehabilitated or reworked for additional service life. Additionally, at leaεt in some cases, waiting for actual crack formation as a management criterion can result in significant safety risks. The methods of the present invention provide improved management procedures by providing management criteria (i.e. , reεidual compressive stresεes compared to predetermined values) which are observable well before irreversible crack initiation or formation occurs. Using the methods of the present invention, the maximum service life of such components can be obtained in a safe and effective manner. Using the methods of the present invention, at least some components can be reworked to increase the residual compressive stress and placed back in service, thereby providing increaεed efficiency without compromising safety. In fact, the methods of the preεent invention are expected to achieve improved efficiency and improved safety as compared to the management methods currently in use since the management criterion is baεed on εurface reεidual compressive streεses rather than on actual or expected crack formation. By uεing εurface reεidual compressive stress as the management criterion, rather than actual or expected crack formation, the margin of safety is expected to be increased, perhaps significantly. The methods of the present invention are ideally suited for augmenting computer tracking of metal components during their service life. Moreover, the data generated from the present methods (i.e. , residual compressive streεε) and data regarding the εervice life and hiεtory of individual componentε can be used to develop a management database for the metal components. As the historical basis of such a database grows, it will be possible to reliably predict the service life of a given part. Thus, once such a database is developed, one will not need to meaεure the compreεεive εtress of each and every component during each teardown or other maintenance event. If the total service life or history of the component is sufficiently short (as determined from the historical data in the database) , meaεurement of the compressive stresε can be delayed. Only εuch components having a service life or history approaching some definable parameter (again as determined from the historical data in the database) will be required to have the actual compressive stress measured and compared to ? the predetermined value. For example, for a given component, the database might show that only components having a service live in excess of 10,000 hours ever have residual compressive stresses approaching or below the predetermined value. In such a case, only components i; with service lives greater than this value will need to have the residual compressive streεε measured during a routine teardown. Of course, components with abnormalities or componentε subjected to extreme service events should be evaluated regardless of the cumulated :: service life. Moreover, it may still be prudent to at least perform some spot checks on components with shorter service lives in order to confirm the continuing validity of the database and its predictive ability. By avoiding actual measurementε for components very unlikely to have 2: residual compresεive εtreεε values lower than the predetermined value, considerable savingε can be obtained. Of course, the method used to predict this likelihood must be proven over time to be both effective and safe. :; The present methods are not, however, intended to replace all non-destructive testing of such metal components. As those skilled in the art will realize, the present methodε are deεigned to manage failures and defects related to crack initiation mechanisms commonly asεociated with the reεidual compreεεive εtreεs and residual tensile streεε levels in the surface layers. Other non-destructive testing methods for identifying other types of failures and/or failure mechanisms, especially early in the service life of such components :-: (i.e. , during the so-called "infant mortality" period), should be continued as appropriate. Incorporation of such data from other non-destructive testing procedures in the management database discussed above may allow even more complete tracking and management of populations of such metal components. Additionally, using the methods of thiε invention, components of approximately equal remaining service life (i.e. , approximately equal residual compresεive stress) can be used together. Normally, the frequency of such teardowns in individual engines will be controlled by the component having the shorteεt remaining εervice life. By avoiding uεe of componentε of widely varying remaining service life, early teardown of engines, necessitated by a single component with only a short remaining service life, can be avoided. By matching components with εimilar remaining service lives in a given engine, the frequency of teardowns over the entire population can be reduced. In another embodiment of this invention, the general techniques discussed above for measuring surface residual compresεive stresε can alεo be uεed to aεεiεt and guide the deεign and development of improved fatigue- limited metal componentε. Uεing thiε method, the εurface residual compreεsive stresses produced by the various stepε in the manufacturing process can be incorporated into, and taken into account in, the overall stress analysis. Effects of modification of the part design (e.g., reduction in weight) throughout the manufacturing and/or design/development procesε can be determined and uεed aε a guide for further modificationε. Using such an iterative approach, reduced-weight fatigue-limited metal parts can be designed having sufficient residual compressive stresses (i.e. , sufficient service lifetimes) for their intended use. Thus, the component design can be fine tuned to reduce component weight without εignificant reduction (or at leaεt reduction to known and acceptable levels) in service lifetimes. The service lifetime and weight characteristics can be balanced to achieve optimum or near optimum performance criterion. For military aircraft, such optimum or near optimum performance criterion may, for example, be related to a reduction in weight to improved thrust to weight ratios. For commercial aircraft, such optimum or near optimum performance criteria may, for example, be related to improved safety margins and/or increased engine performance. Of course, if desired, other appropriate performance criteria may be used to assiεt in deεigning fatigue-limited metal components using the methodε of this invention. Hiεtorically the deεign procedure for critical fatigue-limited metal componentε εuch as disks or other critical aircraft engine components has been the conservative "safe life" approach. This safe life design approach, like the corresponding safe life technique for managing a population of fatigue-limited parts, is generally baεed on manufacturer'ε estimated fatigue life established through analysis, testing, and comparable experience by the part manufacturer. This approach attempts to eεtimate the point, allowing for a suitable safety margin, at which the shortest lived part is expected to fail. The stresε calculationε used in this design approach are primarily based on applied streεε. The present method uεeε the meaεurement of the εurface reεidual compressive streεε during the manufacturing proceεε aε an important component of the deεign approach. The reεidual compressive stress is measured using x-ray diffraction periodically throughout the development and/or design process to- asseεε the effectε of various manufacturing operationε or procedureε used in making the component on the residual compressive streεs in the critical surface areaε of the component. The use of this method in the manufacture and/or design of new fatigue-limited parts will allow quantification of the surface residual compressive stress condition at each step in the manufacturing process; in addition, it will be possible to determine the positive or negative impact on the surface residual compressive stress condition as a result of each operation and, if appropriate, adjust or modify the operation or operations so as to provide the desired level of surface residual compressive stress in the finished metal part. By measuring or remeasuring the εurface reεidual compresεive stress after various machining operations, the design or development of the part may by guided whereby a preselected design or performance criterion (or several criteria) can be improved, and perhaps optimized, while still maintaining an adequate service life. Thus, thiε method can be uεed to εet reεidual compressive stress part requirements and fine-tune component design to provide an optimized or near optimized performance criterion and service life. For example, this method could be used to fine tune component design to reduce the weight of specific aircraft engine parts while maintaining significant (and known) service life. A reduction in weight would, for example, benefit thrust to weight ratio in military aircraft applications and increase commercial aircraft engine performance. Acceptable surface residual compresεive εtress levels determined during the design process can, if desired, be included in component specifications and/or drawings and can be used during actual manufacturing processeε. Such deεigned componentε could be managed using the other embodiments of this invention as described above. Balancing of one or more preselected performance criteria and service life to improve overall performance will be posεible uεing the method of thiε invention. In operation, the manufacturing and/or design/development method of thiε invention is carried out by first measuring the residual compressive stress, preferably using x-ray diffraction techniques, in one or more critical areas of a prototype or partially designed metal part. The prototype is then modified (i.e. , machined or worked) using the difference between measured residual compressive stress and the predetermined residual compresεive stresε design level as a guide to improve the a selected performance criterion. The predetermined design level may be the residual compresεive stresε deεired in the final metal part or an intermediate level or intermediate levelε based on the entire manufacturing procesε. After modifying the part, the reεidual compressive stresε iε remeasured and compared to the predetermined design level to gauge the effect of the modification. Of course, as one skilled in the art realizes, thiε compariεon of the remeaεured reεidual compreεεive εtress could also, if desired, be made to the previously measured residual compressive streεε with εimilar reεultε. The comparison allows the effect of each manufacturing procesε or stage on the residual compresεive εtreεε hiεtory to be determined. Thiε proceεε iε repeated for one or more critical surface areaε until an acceptable and functional metal part is obtained which has its selected performance criterion (or performance criteria) improved and has εufficient reεidual compreεεive εtreεs values (and, therefore, acceptable service life) for itε intended use. Service life can refer to a total service life over the entire life of the part or, in the case where the part is reworked, the individual lifetimes between reworkings or the εum of all individual lifetimeε between reworkingε. The level of acceptable εervice life will, of courεe, vary for different partε. For example, a part which can be reworked easily for a εignificant number of timeε can generally have its selected performance criterion improved by accepting more frequent teardowns and reworkingε. For a part which cannot be reworked or which cannot be reworked easily, it will generally be preferred that the service life (especially between reworkings) be kept relatively long. In any event, the improvement in the selected performance criterion and the length of service life (both total and/or between reworkings) can be balanced and a juεted to optimum or near optimum levelε for that metal part and its intended use and/or service environment. In still another embodiment of this invention, the general techniques discussed above for measuring surface residual compressive stress can also be used to provide a quality control program or mechanism for the manufacture of fatigue-limited metal components. Using this embodiment, the residual compressive streεε in one or more critical surfaces areas is meaεured after the component haε been manufactured but before it iε placed in service. If the reεidual compressive streεε in one or more critical areaε iε below a correεponding predetermined reεidual compreεsive εtreεs value for the one or more critical areas, the component is flagged or otherwise marked for further attention. If the residual compressive streεs levels for the component are within acceptable ranges (i.e. , for each of the one or more critical surface areas, the measured residual compresεive εtreεs iε equal to or greater than the correεponding predetermined reεidual compressive streεε value) , then the component can be placed into service (assuming, of course, it meets other appropriate quality control requirements) . The present quality control method is generally not intended to replace all existing quality control requirements; rather, it preferably supplements and εtrengthenε the existing quality control program for fatigue-limited components. As one of ordinary skill in the art will realize, the predetermined residual compressive values for each of the more than one critical surface areas may be the same or different for other surface areas, depending on the actual geometry of the component and the different service conditions the various εurfaceε will be exposed to during use. Of course, as one skilled in the art will realize, the present quality control procedure can be used during the manufacturing process as well aε for the completed component. In other words, the measured surface residual compresεive stress measurements for the partially completed component during one or more stageε of the manufacturing process can be used to gauge or test the procesε up to that point before moving on in the manufacturing proceεε. It is especially preferred that this quality control procedure be used to measure and control the effect of working the component to increase or modify the surface reεidual compreεsive streεε. Thuε, thiε quality control process is especially useful and preferred for quality control of the shot peening (or other working or reworking technique) step in the manufacturing process. Flagged components (i.e. , components having lower than acceptable residual compressive streεε levels) are not placed into service as manufactured (or, if during the manufacturing proceεε, are not moved to the next step) . Such flagged components can be, if appropriate, destroyed or otherwise mutilated to prevent unauthorized use (or continuation of the manufacturing procesε for that component) . Or in appropriate cases, the flagged metal components are reworked to increase the residual compressive streεε in the one or more critical εurface areas to levels above the correεponding predetermined reεidual compressive stress. Assuming such reworked metal components then meets the surface residual compressive stress and other requirements, the reworked metal components can be placed in service (or the manufacturing process continued with the partially completed and reworked components) . Flagged metal components which are especially suitable for reworking include metal components which only fail to meet the surface residual compressive stresε requirementε (i.e. , all other quality control requirements are within specification) . Appropriate reworking and/or modification of the component can, of course, be uεed to bring other quality control requirementε within specification. Preferably, after reworking, all quality control parameters, including surface residual compresεive streεε levelε, are remeaεured to inεure that the part haε obtained, or re ainε within, the relevant εpecificationε. Preferably, specific surface residual compressive stress levels, ranges, or targets are included in the detailed component specification and also directly on the relevant drawings. Data from meaεured εurface reεidual compreεεive streεε values during the manufacturing process and during later management of the population of parts (identifiable to specific component serial numbers or other identifiers) could be especially useful in failure analysis and statistical analyεiε of component populations. The decision to rework a particular component can be informed by a number of factors, including the amount the measured residual compresεive εtreεε levelε fall below the acceptable valueε for the one or more critical surface areas and/or, if appropriate, the stage in the manufacturing procesε at which the reεidual compressive stress levels fall below the acceptable values for one or more critical surface areas. If the component is only slightly out of specification, it is more likely that reworking will be cost effective. For components which are far out of specification, it may be more cost effective to simply destroy the part (especially if the amount of reworking necessary to bring the part within the surface residual compressive stress requirements iε such that other quality control requirements cannot be achieved or maintained) . Where surface residual compressive stress is measured at different stageε of the manufacturing proceεε, there will likely be stages at which failure to meet the corresponding specification may be more critical or which it will be more difficult to obtain a satiεfactory reεult with reworking. Determining whether reworking iε feaεible and/or appropriate will preferably be, at leaεt initially, on a caεe by caεe basis. Once significant historical data have been generated, a more statiεtical determination or analyεiε can likely be used (both where measurement are taken during various stages of the manufacturing process and/or at the end of the manufacturing process) . The quality control method of this invention offers a number of εignificant advantages over currently conducted manufacturing procedures for fatigue-limited components. First of all, it involves the direct measurement and tracking of an important fatigue-failure related parameter - - the surface residual compressive streεε. Hiεtorically, quality control procedureε have not included the measurement of compressive stresses; rather, they have relied upon other "predicative" parameters which may not have been as directly related to, or as predictive in regard to, fatigue failure as desirable. Moreover, such earlier quality control procedures were likely to reεult in componentε having considerable scatter or ranges for the surface residual compressive stresε levels over the range of the population (even assuming all residual compressive stress levels were above acceptable limits) ; moreover, the actual surface residual compressive stress values for the components are generally not even known. By not knowing the initial surface residual compressive stress levels (i.e. , relying only on other predictive parameters), the ultimate user might place components into use which would fail much sooner than predicted by the prevalent management procedures. Also in the earlier quality control procedures, it was not possible to match components (i.e. , components with similar predictive service lifetime) in order to minimize teardown scheduleε and expenses. Such problems can be avoided to a large extent uεing the methods of thiε invention. For example, partε having similar predicted service lifetimes can be matched in a given jet engine. Teardowns, inspections, and regularly scheduled maintenance procedures can be tailored for the composite predictive lifetimeε. Thuε, where componentε are matched with relatively εhort predictive lifetimeε (but still of acceptable lengths) , appropriate inspections can be scheduled at a shorter time interval as compared to matched parts having a longer predicted lifetime. In this manner, the overall cost, safety, and reliability can be better maximized. In addition, the use of surface residual compresεive stresεeε aε a quality control parameter is also expected to reduce the number of component failures during the so-called "infant mortality" period. The management, design, and quality control methods of thiε invention can alεo be uεed in conjunction with other management, design, and quality control method and/or techniques normally used with fatigue-limited metal components. For example, the present design method can be used with conventional finite element analysis design techniques. Such finite element analysis is generally used to calculate or determine the perceived high stress areas of a given component. By including the residual compresεive εtress levels into total stress considerations, the present methods can be used, for example, to fine tune the results of the finite element analysiε and make it a more realistic and useful tool. As thoεe skilled in the art will realize, the present methods can be used in conjunction with other management, design, and quality control techniques to improve those techniqueε and, overall, provide even better εafety and economy in the uεe of such fatigue-limited components.

Claims: CLAIMS That which iε claimed is: 1. A method for designing a fatigue-limited metal part whereby a selected performance criterion for the metal part is improved while maintaining sufficient residual compressive stress to achieve an acceptable service life for the metal part, said method comprising: (1) providing a prototype of the metal part; (2) measuring the residual compreεsive stress in one or more critical surface areas of the prototype during the course of design of the metal part; (3) modifying the prototype using the difference between the measured residual compressive streεε and a predetermined reεidual compressive streεs design level as a guide to improve the selected performance criterion; (4) remeasuring the reεidual compressive stress in the one or more critical surface areas of the modified prototype to determine the remeasured residual compressive streεε in compariεon to the predetermined reεidual compreεεive εtress design level in order to gauge the effect of the modification; and (5) repeating steps (2) through (4) for the one or more critical surface areas until an acceptable and functional metal part is obtained, wherein the acceptable and functional metal part has its selected performance criterion improved and has sufficient residual compressive streεs in the one or more critical surface areas for itε intended uεe. 2. A method as defined in claim l, wherein the residual compresεive εtreεε and the remeaεured reεidual compressive stress are measured using x-ray diffraction techniques . 3. A method as defined in claim 1, wherein the metal part is a rotating part used in a gas turbine or jet engine. 4. A method as defined in claim 2, wherein the metal part is a rotating part used in a gas turbine or jet engine. 5. A method as defined in claim 3, wherein the metal parts is a disk or a drum rotor. 6. A method as defined in claim 4, wherein the :: metal part is a disk or a drum rotor. 7. A method as defined in claim 1, wherein the selected performance criterion is a reduction in weight of the metal part. 8. A method aε defined in claim 3, wherein the 1 εelected performance criterion iε a reduction in weight of the metal part. 9. A method aε defined in claim 4, wherein the εelected performance criterion iε a reduction in weight of the metal part. :. 10. A method for deεigning a fatigue-limited metal part whereby the weight of the metal part iε reduced while maintaining sufficient residual compresεive εtreεε to achieve an acceptable service life for the metal part, said method comprising: (l) providing a prototype of the metal part; (2) measuring the reεidual compreεεive εtreεε in one or more critical surface areas of the prototype during the course of the design of the metal part; (3) modifying the prototype using the difference between the measured residual compressive stress and a predetermined residual compressive stress design level as a guide; (4) remeasuring the residual compressive stress in the one or more critical surface areas of the modified prototype to determine the remeasured residual compresεive εtresε in comparison to the predetermined reεidual compressive stress design level in order to gauge the effect of the modification; and !5) repeating steps (2) through (4) for the one or more critical surface areas until an acceptable and functional metal part is obtained having reduced weight and sufficient residual compresεive stress in the one or more critical surface areas for its intended use. 11. A method as defined in claim 10, wherein the residual compressive stresε and the remeasured residual compressive stress are measured uεing x-ray diffraction techniqueε. 12. A method as defined in claim 10, wherein the metal part is a rotating part used in a gas turbine or jet engine. j3. A method as defined in claim 11, wherein the metal part is a rotating part used in a gas turbine or jet engine. 14. A method as defined in claim 12, wherein the metal part is a disk or a drum rotor. 15. A method as defined in claim 13, wherein the metal part iε a diεk or a drum rotor. 16. A method for designing a fatigue-limited metal part whereby the weight of the metal part is minimized while maintaining sufficient residual compresεive εtress to achieve an acceptable service life and safety factor for the metal part, said method comprising: (1) providing a prototype of the metal part; (2) measuring the residual compressive stress in one or more critical surface areas of the prototype during the course of the design of the metal part; (3) modifying the prototype by reducing its weight using the difference between the measured residual compreεεive εtreεε and a predetermined reεidual compreεsive stress design level as a guide; (4) remeasuring the residual compresεive εtreεε in the one or more critical surface areas of the modified prototype to determine the remeasured residual compresεive stress in comparison to the predetermined residual compresεive stress design level in order to gauge the effect of the modification; and (5) repeating steps (2) through (4) for the one or more critical surface areas until an acceptable and functional metal part iε obtained having minimal weight and εufficient reεidual compressive stress in the one or more critical surface areas to achieve an acceptable service life and safety factor for the metal part. 17. A method as defined in claim 16, wherein the residual compressive streεε and the remeaεured reεidual compreεεive εtreεε are meaεured uεing x-ray diffraction techniqueε. 18. A method aε defined in claim 16, wherein the metal part is a rotating part used in a gas turbine or jet engine. 19. A method as defined in claim 17, wherein the metal part is a rotating part used in a gas turbine or jet engine. 20. A method as defined in claim 18, wherein the metal part iε a disk or a drum rotor. 21. A method as defined in claim 19, wherein the metal part is a disk or a drum rotor. s 22. A quality control method for the manufacture of fatigue-limited metal components, said method comprising measuring the residual compressive stresε in one or more critical surface areaε for each metal component after its manufacture and before placing K it into service, comparing the measured residual compresεive εtreεε in one or more critical εurface areaε to a correεponding predetermined reεidual compreεsive εtreεε level for the one or more critical εurfaceε, and flagging each metal component which has its measured : residual compresεive εtress below its corresponding predetermined residual compresεive stress level, whereby flagged metal components are not placed in service. 23. A quality control method as defined in claim 22, wherein the flagged metal components are 2; destroyed or otherwise mutilated to prevent unauthorized uεe. 24. A quality control method aε defined in claim 22, wherein the flagged metal componentε are reworked to increase the residual compressive stress in 25 the one or more critical surface areas to levels above the corresponding predetermined residual compresεive εtreεε, whereby the reworked metal componentε can be placed in service. 25. A quality control method aε defined in : ■ : claim 22, wherein the reεidual compreεεive εtreεε in one or more critical εurface areaε for each metal component iε determined using x-ray diffraction techniques. 26. A quality control method as defined in claim 23, wherein the residual compressive stress in one or more critical surface areas for each metal component is determined using x-ray diffraction techniques. 27. A quality control method as defined in claim 24, wherein the residual compressive stress in one or more critical surface areas for each metal component is determined using x-ray diffraction techniques.

Inventors: BERKLEY STANLEY G, BERKLEY, STANLEY, G.
Applicants: FATIGUE MANAGEMENT ASS, FATIGUE MANAGEMENT ASSOCIATES L.L.C.
Application year: 1996
Main classification: G01N23
IPC codes: B23K31, F02C7, G01L1, G01L5, G01N23