Method for preparing photographic elements comprising loaded latex compositions

Abstract: Photographic elements comprising loaded latex compositions are prepared by (a) combining under conditions of low or moderate shear, in the presence of surfactant, and in the substantial absence of water-miscible or volatile organic solvents, a liquid organic composition comprising at least one photographically useful compound with an aqueous polymer latex, (b) holding the combination resulting from (a) in a liquid state for sufficient time for substantial loading of the organic composition into the polymer latex to occur, and (c) coating the loaded latex resulting from (b) on a support.

Description: Field of the Invention The present invention relates to a method for forming photographic dispersions and photographic elements comprising hydrophobic photographically useful compounds dispersed in an aqueous solution. More particularly, it relates to the use of polymer latexes in such a method. Background of the Invention One approach to preparing photographic dispersions containing polymer is to load a hydrophobic photographically useful compound into a polymer latex. Manufacturing advantages of loaded latex dispersions can include avoiding the high-shear or turbulent mixing required to prepare conventional emulsified photographic dispersions, and the reduction or elimination of high-boiling solvents, known as coupler solvents. Also, photographic advantages of polymer-containing photographic dispersions can be obtained with loaded latex compositions, including improved image permanence, improved dye hue and color reproduction, and improved dry and wet film physical properties. The use of latex or dispersed polymers in the preparation of photographic dispersions has been described in U.S. Patents 2,772,163; 2,852,382; 4,133,687; 4,199,363; 4,203,716; 4,214,047; 4,247,627; 4,368,258; 4,448,850; 4,497,929; 4,608,424; 4,684,608; 4,724,197; 4,822,728; 4,840,885; 4,891,309; 4,914,005; 4,990,435; 5,026,631; 5,047,316; 5,091,296; 5,279,931; British Patent GB 1,287,013; Canadian Patent No. 616,178; European Patent Application EP 483,416; Japanese patent application JP 032 558; and Research Disclosure 181,072. Usually these latex polymers are prepared by emulsion polymerization, although emulsified dispersions of organic-soluble polymers are also described, as in U.S. Patents 4,388,403; 4,840,885 and 5,026,631. The usual procedure for preparing a loaded latex described in the prior art is to combine a solution of the hydrophobic photographically useful compound in a water-miscible organic solvent with the aqueous latex. The resulting mixture that typically has about a 1:1 ratio of water to organic solvent, is either diluted with water or the organic solvent is removed by evaporation, with the result that the hydrophobic compound becomes associated with or dissolved in the latex particles. Variations on this procedure vary the order of addition of the organic solution and aqueous latex, substitute volatile, but not entirely water-immiscible auxiliary solvents for the water-miscible auxiliary solvents, incorporate water-miscible or volatile organic solvent in the emulsion polymerization step that is also present during dispersion preparation, or require the formation of intermediate water-in-oil emulsions of the latex in volatile organic solvent before the formation of the final oil-in-water loaded latex dispersion. In some cases, photographically useful compounds are dissolved in the organic monomers prior to emulsion polymerization. Procedures are also described in which base-ionizable couplers and / or base-ionizable latex polymers are combined at high pH, often with auxiliary solvent present, followed by neutralization and / or addition of magnesium salts or alkaline-earth metal salts, to form a dispersion of coupler and polymer. Problems To Be Solved All of these procedures for preparing loaded-latex or latex-containing dispersions present severe practical difficulties. Rigid requirements exist for both the hydrophobic compound to be loaded and the latex, especially for the procedures that use water-miscible organic solvent. In the initial mixture of hydrophobic compound, water-miscible organic solvent, and latex, the hydrophobic compound must not be precipitated by the aqueous environment, and the latex must not be coagulated by the large amount of organic solvent present. Many patents in the prior art describe a test for latex loadability, in which a suitable latex must not coagulate when mixed with an equal volume of the water-miscible organic solvent used in the dispersion preparation. Most latex polymers do not meet this requirement. A second difficulty is that auxiliary solvent is used in the process at all, causing severe manufacturing, environmental and safety problems. A third concern is that free-radical emulsion polymerization of monomers with photographically useful compounds dissolved in the monomers can cause chemical destruction of the compounds and can impair the polymerization process, leading to unwanted crosslinking, or lowered polymer molecular weight, and to higher levels of residual monomer. Polymerization processes other than free-radical polymerizations, including most condensation polymerizations, are poorly adapted to production of emulsion polymers, and also present similar difficulties with unwanted reactions of the photographically useful compounds under polymerization conditions or with the polymerization reagents, and unwanted effects of the compounds on the polymerization process, including chain termination or crosslinking. None of this prior art describes procedures for loading latex polymers without the use of substantial amounts of water-miscible or volatile auxiliary solvent at some point in the procedure. A fourth problem is that it is often difficult or impossible to achieve high loading levels, i.e., greater than about a 1:1 ratio, of the hydrophobic compound or compounds in the latex, using the known methods. We have recently discovered (cf. co-pending EP-A-0 727 704) that subjecting a mixture liquid oil-phase and an aqueous polymer latex to conditions of high shear and/or turbulence can lead to formation of loaded latex compositions, even in the absence of water-miscible or volatile organic solvent. This method is applicable to a wider variety of latex polymers and hydrophobic photographically useful compounds than the other methods described above, and higher loading levels can be achieved. This method, however, still requires the energy to cause high-shear and/or turbulent mixing of the dispersion containing the latex and the photographically useful compound. Summary of the Invention With the present invention we have unexpectedly discovered that hydrophobic photographically useful compounds and polymer latex dispersions, in the presence of surfactant, form loaded latex dispersions after simple low-shear mixing of the latex with a liquid oil-phase, in the absence of any significant amount of water-miscible or volatile solvent, when such mixtures are held in a liquid state for a sufficient length of time. One embodiment of the invention comprises a method for preparing a photographic element comprising at least one hydrophilic colloid layer coated on a support, comprising (a) combining under conditions of low or moderate shear, in the presence of surfactant, and in the substantial absence of water-miscible or volatile organic solvents, a liquid organic composition comprising at least one photographically useful compound with an aqueous polymer latex, (b) holding the combination resulting from (a) in a liquid state for sufficient time for substantial loading of the organic composition into the polymer latex to occur, and (c) coating the loaded latex resulting from (b) on a support. In a preferred embodiment of the invention, a coarse aqueous dispersion of liquid oil phase (e.g., a dispersion containing liquid oil phase particles of from 0.4 to 20 µm) comprising a photographically useful compound that is essentially free of water-miscible or volatile solvent, is prepared by low- or moderate-shear mixing of the hydrophobic oil solution with an aqueous solution containing surfactant to promote loading, and the polymer latex is mixed with this coarse dispersion, leading to the formation of loaded latex after some time. In another preferred embodiment, the liquid oil solution is mixed directly, under conditions of low to moderate shear, with an aqueous solution containing the polymer latex and surfactant, leading to the formation of the loaded latex after some time. In yet another preferred embodiment, a fine-particle photographic dispersion of a liquid hydrophobic solution comprising a photographically useful compound (e.g., a dispersion containing liquid oil phase particles of from 0.05 to 0.4 µm) is prepared by means known in the art (including high-shear and or turbulent mixing) and in such a way that the dispersion is essentially free of water-miscible or volatile solvent, and the dispersion is mixed under conditions of low shear with an aqueous latex in the presence of surfactant to cause loading of the latex. In a preferred embodiment of the invention, the combination resulting from (a) is held for a sufficient time for essentially complete loading of the organic composition into the polymer latex to occur in order to achieve more consistent photographic properties in the resulting elements. It has been found that loading of a liquid organic composition into a latex polymer may require holding for an extended length of time in a liquid state for substantial loading, and even greater length of time for essentially complete loading to occur. For the purposes of this invention, "substantial" loading is defined as the amount of loading of a photographically useful compound into a polymer latex necessary to generate a measurable difference in the photographic properties of the resulting photographic element compared to a non-loaded mixture of photographically useful compound and polymer latex, while "essentially complete" loading is defined as the level of loading required to attain 75% of the difference in the photographic properties of a photographic element comprising a completely loaded latex compared to a photographic element comprising a non-loaded mixture of photographically useful compound and polymer latex. In a most preferred embodiment of the invention, the liquid organic composition loaded into the polymer latex comprises a photographic coupler. With the extensive prior art describing loaded latex compositions prepared by using large amounts of water-miscible or volatile organic solvent, in processes that were complex, tedious, labor intensive, energy intensive, and environmentally objectionable, we were surprised to see the formation of loaded-latex dispersions made possible by such a simple procedure. Certainly, not all combinations of photographically useful compounds, latex polymers, and surfactants lead to formation of loaded latex formulations, but for combinations where loading does occur, this method provides an extremely simple and attractive procedure. One object of the invention is the control of photographic dispersion particle size by the use of a latex polymer. Another object of this invention is the preparation of dispersions with a wide range of ratios of hydrophobic compound to polymer, from about 50:1 to 1:20, more preferably from about 10:1 to 1:10. Yet another object of this invention is to prepare photographic dispersions with superior stability toward crystallization of the loaded component. Another object is the preparation of photographic elements with superior attributes, comprising such dispersions. These improved attributes include color reproduction, natural aging properties, image preservability toward light, heat, and humidity, and resistance to scratching or delamination. Another object is the preparation of photographic elements comprising loaded latex dispersions of latex polymers which impart favorable photographic properties, but that fail "tests of latex loadability" described in the prior art. Other objects of this invention will be apparent in this disclosure and the examples described. Detailed description of the Invention In one embodiment of the invention, the liquid organic composition is formed by combining one or more hydrophobic photographically useful compounds with one or more high-boiling solvents at a temperature sufficient to prepare a homogeneous organic solution, and the organic solution is then mixed with an aqueous solution containing gelatin, surfactant, and the polymer latex. In another embodiment of the invention, the liquid organic composition is first combined with an aqueous solution containing gelatin and surfactant to form an aqueous dispersion of the liquid organic composition, and the resulting dispersion is then combined with another aqueous solution containing the polymer latex. Photographic coating solutions containing gelatin are generally held above 35-40°C in order to avoid setting of the gelatin. If the temperature of such solutions is raised too high, however, excessive evaporation may occur, as well as other detrimental effects depending upon the composition of the solution (e.g., solutions containing silver halide emulsions may become fogged). Also, in multilayer coating operations, thermal uniformity of the multiple layers is an important coating parameter. Accordingly, such photographic coating solutions are generally held before coating at a relatively uniform temperature above the gel-set temperature, but below 60°C. It has been found that latex polymers having a glass transition temperature (Tg) above the hold temperature for gelatin containing dispersions, e.g. above 60°C and especially above 90°C, generally require longer times to load than polymers having a Tg below such temperatures. Accordingly, where gelatin is also combined with the liquid organic composition and the polymer latex, and the polymer has a Tg of 60°C or more or 90°C or more, in a preferred embodiment of the invention the combination resulting from (a) is held for at least 1 hour, more preferably at least 2 hours and most preferably at least 3 hours, in a liquid state below 60°C before coating on the support. The factors that contribute to improved likelihood that latex loading will occur when a polymer latex is combined with a dispersion of a hydrophobic photographically useful compound or mixture and held for a given length of time in a liquid state include the following: (1) Hydrophobic photographically useful compounds with low logP (less than about 9) are more likely to load rapidly compared to compounds with higher logP. LogP is defined as the logarithm of the value of the octanol/water partition coefficient (P) of the compound, a parameter highly correlated with measured water solubility for compounds spanning a wide range of hydrophobicity. The high partition coefficients of many photographically useful compounds are difficult to measure experimentally. It is also possible to estimate logP by using logP (calc) , a value calculated using MedChem 3.54, a software package available from the Medicinal Chemistry Project, Pomona College, Claremont, California (2) Polymers with lower glass transition temperatures (T g ) load more rapidly than polymers with high T g . This effect is observable experimentally in some cases, and may relate to the rate of mass-transport of a hydrophobic molecule in the environment of the polymer. For a given hold temperature, polymers having a Tg below the hold temperature tend to be loaded must faster than polymers having a Tg above the hold temperature. (3) The presence of surfactant promotes loading. This effect may be related to micellar transport of hydrophobic molecules in the aqueous environment of the dispersion. Customary levels of surfactant used in forming oil-in-water dispersions of photographic compounds are generally sufficient to promote loading in accordance with the invention. Often, the same surfactant used for the emulsion polymerization may be sufficient for the preparation of the photographic elements and dispersions of the invention. (4) Combinations of photographically useful compounds and polymers that are miscible with each other are a common feature of loaded dispersions. An important driving force for loading is the favorable mixing of polymer with the oil components of the dispersion, and combinations of polymers and dispersion oil components that are immiscible are less likely to form loaded latex dispersions under any given set of conditions. The presence of high-boiling solvents, (coupler solvents) can improve the solubility of photographically useful compounds in the polymer, and in this way can promote formation of loaded latex dispersions. Mixtures of photographically useful compounds can be employed in the absence of any high-boiling solvents, as can a single photographically useful compound. The examples in this disclosure describe some combinations of photographically useful compounds, latex polymers, and dispersion conditions that lead to formation of loaded latex dispersions according to the invention. Any of several indications may be taken as evidence that a loaded latex dispersion has been formed. Direct evidence of phase mixing of the polymer latex and the photographically useful compound or compounds may be obtained by a number of measurement techniques, including Differential Scanning Calorimetry (DSC) and dielectric loss measurements. In general, loaded latex dispersions will show a single glass transition temperature (T g ) for the mixture, while unassociated polymer latex phases and photographic dispersed oil phases will exhibit separate T g 's unaffected by their combination. Another evidence of latex loading is the effect of the loading process on dispersion particle size. Often loaded latex dispersions will show a single distribution of particle size, usually smaller than the distribution of size seen in a conventional photographic dispersion. Unassociated polymer latex and photographic dispersion will maintain their individual particle size distributions when combined, manifested typically as a bimodal particle size distribution. One possible reason for many loaded latex dispersions showing smaller apparent particle size is that typical polymer latices have a monodisperse distribution of particle diameters, usually between 0.020 and 0.200 µm, while conventional milled photographic dispersions have a wider distribution of particle sizes centered between 0.05 and 0.4 µm, typically between 0.150 and 0.400 microns. In one proposed mechanism to explain latex loading, the dispersion particles composed of photographically useful compounds dissolve or disappear as loading occurs, so that in the final loaded latex dispersion, the combined mass of polymer and photographically useful compounds are distributed among a similar number of particles that comprised the initial polymer latex. Often this number is much larger than the initial number of dispersion particles comprising the oil solution of photographically useful compounds, so the average size of the loaded particles is smaller than that of the initial photographically useful compound dispersion particles. However, the loading process may occur with little change in apparent particle size or with an apparent increase in dispersion size, particularly if the oil:polymer ratio is large, or the initial latex particle size is large. A contributing factor why loaded latex dispersion may often appear to be smaller than conventional dispersions is that many useful particle size measurement techniques do not accurately measure extremely broad or multimodal distributions of particle size. Many useful techniques are most sensitive to the larger particles in a broad distribution. Turbidity measurement can be very useful, and turbidity changes as latex loading occurs can be a very dramatic evidence for latex loading. Typically, the conventional photographic dispersion is much larger than the latex and is largely responsible for the light scattering in the sample immediately after mixing. As loading occurs, the decrease in scattering due to disappearance of the large conventional dispersion droplets dominates the measurement, and the increased scattering from the smaller latex particles as their size increases is less apparent. Another useful technique for measuring particle size is Photon Correlation Spectroscopy (PCS), a dynamic light scattering technique that derives particle sizes and distributions from particle motion in a medium, typically water for photographically useful dispersions. Again, because the measurement is based on light scattering, the small signal from a monodisperse small-diameter latex is often masked by the presence of a typical photographic dispersion that causes much more light scattering. In this case, as loading occurs, the measurement will often indicate a substantial decrease in particle size. Similarly, microscopic techniques, particularly optical microscopy, are well adapted for observing conventional photographic dispersions larger than about 0.250 µm, but are usually unable to resolve the much smaller latex particles. As loading occurs, the apparent particle size observed by optical microscopy often decreases, and the final loaded dispersion may be sufficiently small to be unresolvable by the technique, with the net observation that the initial dispersion particles have "disappeared." Another evidence of formation of loaded latex dispersions of the invention is the effect of the dispersions on the photographic performance. It has been shown that polymer containing dispersions can affect the reactivity and hue of photographic couplers, the stability of the unprocessed photographic element, the stability of dispersions toward crystallization, and the stability of the final photographic image toward heat, light and humidity. Even in the absence of direct evidence, indirect evidence of loading can be derived from photographic performance, particularly where the effects are consistent with known performance of polymer-containing dispersions prepared by other means, including the emulsification of a mixed solution of polymer, photographically useful compound, and auxiliary solvent. The process of the invention is generally applicable to forming loaded latex dispersions of photographically useful compounds that may be used at various locations throughout a photographic element. Photographically useful compounds that can be loaded into polymer latices include photographic couplers, (including yellow, magenta and cyan image-forming couplers, colored or masking couplers, inhibitor-releasing couplers, and bleach accelerator-releasing couplers, dye-releasing couplers, etc.), UV absorbers, dyes, high-boiling organic solvents, reducing agents (including D ox scavengers and nucleators), stabilizers (including image stabilizers, stain-control agents, and developer scavengers), developing agents, optical brighteners, lubricants, etc. Oil components of the dispersions of the invention preferably include couplers. Image dye-forming couplers may be included in the element such as couplers that form cyan dyes upon reaction with oxidized color developing agents which are described in such representative patents and publications as: U.S. Patents 2,772,162; 2,895,826; 3,002,836; 3,034,892; 2,474,293; 2,423,730; 2,367,531; 3,041,236; 4,883,746 and "Farbkuppler - Eine Literature Ubersicht," published in Agfa Mitteilungen, Band III, pp. 156-175 (1961). Preferably such couplers are phenols and naphthols that form cyan dyes on reaction with oxidized color developing agent. Couplers that form magenta dyes upon reaction with oxidized color developing agent are described in such representative patents and publications as: U.S. Patents 2,600,788; 2,369,489; 2,343,703; 2,311,082; 3,152,896; 3,519,429; 3,062,653; 2,908,573 and "Farbkuppler - Eine Literature Ubersicht," published in Agfa Mitteilungen, Band III, pp. 126-156 (1961). Preferably such couplers are pyrazolones, pyrazolotriazoles, or pyrazolobenzimidazoles that form magenta dyes upon reaction with oxidized color developing agents. Couplers that form yellow dyes upon reaction with oxidized and color developing agent are described in such representative patents and publications as: U.S. Patents 2,875,057; 2,407,210; 3,265,506; 2,298,443; 3,048,194; 3,447,928 and "Farbkuppler - Eine Literature Ubersicht," published in Agfa Mitteilungen, Band III, pp. 112-126 (1961). Such couplers are typically open chain ketomethylene compounds. In a preferred embodiment of the invention, an acetanilide yellow coupler is used which has the formula: wherein R 1 is an alkyl, aryl, anilino, alkylamino or heterocyclic group; Ar is an aryl group; and X is hydrogen or a coupling-off group. The R 1 , Ar and X groups may each contain further substituents as is well known in the art. R 1 is preferably: In particularly preferred embodiments of the invention a pivaloylacetanilide yellow coupler is used wherein R 1 is t-butyl. Ar is preferably substituted phenyl wherein at least one substituent is halo, alkoxy or aryloxy. Ar preferably additionally contains a ballasting group. Ballasting groups usually comprise one or more 5 to 25 carbon atom containing organic moieties whose function is to immobilize the coupler and the formed image dye during photographic development by imparting poor water diffusibility to the coupler compound. X is a hydrogen or a coupling-off group. Coupling-off groups are generally organic groups which are released during photographic processing. The released coupling-off group can be a photographically useful group. Coupling-off groups are well known in the art. Such groups can determine the chemical equivalency of a coupler, i.e., whether it is a 2-equivalent or a 4-equivalent coupler, or modify the reactivity of the coupler. Such groups can advantageously affect the layer in which the coupler is coated, or other layers in the photographic recording material, by performing, after release from the coupler, functions such as dye formation, dye hue adjustment, development acceleration or inhibition, bleach acceleration or inhibition, electron transfer facilitation, color correction. Generally the presence of hydrogen at the coupling site provides a 4-equivalent coupler, and the presence of another coupling-off group usually provides a 2-equivalent coupler. Representative classes of such coupling-off groups include, for example, chloro, alkoxy, aryloxy, hetero-oxy, sulfonyloxy, acyloxy, acyl, heterocyclyl, sulfonamido, mercaptotetrazole, benzothiazole, mercaptopropionic acid, phosphonyloxy, arylthio, and arylazo. These coupling-off groups are described in the art, for example, in U.S. Patents 2,455,169; 3,227,551; 3,432,521; 3,476,563; 3,617,291; 3,880,661; 4,052,212; and 4,134,766; and in U.K. Patents and published application Nos. 1,466,728; 1,531,927; 1,533,039; 2,006,755A; and 2,017,704A. It may be useful to use a combination of couplers any of which may contain known ballasts or coupling-off groups such as those described in U.S. Patents 4,301,235; 4,853,319 and 4,351,897. The coupler may also be used in association with "wrong" colored couplers (e.g. to adjust levels of interlayer correction) and, in color negative applications, with masking couplers such as those described in EP 213,490; Japanese Published Application 58-172,647; U.S. Patent 2,983,608; German Application DE 2,706,117C; U.K. Patent 1,530,272; Japanese Application A-113935; U.S. Patents 4,070,191 and 4,273,861; and German Application DE 2,643,965. The masking couplers may be shifted or blocked. Typical couplers that can be used with the elements of this invention include those shown below. The invention materials may also be used in association with materials that accelerate or otherwise modify the processing steps e.g. of bleaching or fixing to improve the quality of the image. Bleach accelerator releasing couplers such as those described in EP 193,389; EP 301,477; U.S. Patents 4,163,669; 4,865,956; and 4,923,784, may be useful. Also contemplated is use of the compositions in association with nucleating agents, development accelerators or their precursors (UK Patent 2,097,140; U.K. Patent 2,131,188); electron transfer agents (U.S. Patents 4,859,578 and 4,912,025); antifogging and anti color-mixing agents such as derivatives of hydroquinones, aminophenols, amines, gallic acid; catechol; ascorbic acid; hydrazides; sulfonamidophenols; and non color-forming couplers. Suitable hydroquinone color fog inhibitors include, but are not limited to compounds disclosed in EP 69,070; EP 98,241; EP 265,808; Japanese Published Patent Applications 61/233,744; 62/178,250; and 62/178,257. In addition, specifically contemplated are 1,4-benzenedipentanoic acid, 2,5-dihydroxy-delta,delta,delta',delta'-tetramethyl-, dihexyl ester; 1,4-Benzenedipentanoic acid, 2-hydroxy-5-methoxy-delta,delta,delta',delta'-tetramethyl-, dihexyl ester; and 2,5-dimethoxy-delta,delta,delta',delta'-tetramethyl-, dihexyl ester. In addition, it is contemplated that materials of this invention may be used with so called liquid ultraviolet absorbers such as described in U.S. Patents 4,992,358; 4,975,360; and 4,587,346. Various kinds of discoloration inhibitors can be used in conjunction with elements of this invention. Typical examples of organic discoloration inhibitors include hindered phenols represented by hydroquinones, 6-hydroxychromans, 5-hydroxycoumarans, spirochromans, p -alkoxyphenols and bisphenols, gallic acid derivatives, methylenedioxybenzenes, aminophenols, hindered amines, and ether or ester derivatives obtained by silylation, alkylation or acylation of phenolic hydroxy groups of the above compounds. Also, metal complex salts represented by (bis-salicylaldoximato)nickel complex and (bis-N,N-dialkyldithiocarbamato)nickel complex can be employed as a discoloration inhibitor. Specific examples of the organic discoloration inhibitors are described below. For instance, those of hydroquinones are disclosed in U.S. Patents 2,360,290; 2,418,613; 2,700,453; 2,701,197; 2,710,801; 2,816,028; 2,728,659; 2,732,300; 2,735,765; 3,982,944 and 4,430,425; and British Patent 1,363,921; 6-hydroxychromans, 5-hydroxycoumarans, spirochromans are disclosed in U.S. Patents 3,432,300; 3,573,050; 3,574,627; 3,698,909 and 3,764,337; and Japanese Published Patent Application 52-152,225; and so on; spiroindanes are disclosed in U.S. Patent 4,360,589; those of p -alkoxyphenols are disclosed in U.S. Patent 2,735,765; British Patent 2,066,975; Japanese Published Patent Applications 59-010,539 and 57-019,765; and so on; hindered phenols are disclosed, for example, in U.S. Patents 3,700,455; 4,228,235; Japanese Published Patent Applications 52-072,224 and 52-006,623; and so on; gallic acid derivatives, methylenedioxybenzenes and aminophenols are disclosed in U.S. Patents 3,457,079; 4,332,886; and Japanese Published Patent Application 56-021,144, respectively; hindered amines are disclosed in U.S. Patents 3,336,135; 4,268,593; British Patents 1,326,889; 1,354,313 and 1,410,846; Japanese Published Patent Applications 51-001,420; 58-114,036; 59-053,846; 59-078,344; and so on; those of ether or ester derivatives of phenolic hydroxy groups are disclosed in U.S. Patents 4,155,765; 4,174,220; 4,254,216; 4,279,990; Japanese Published Patent Applications 54-145,530; 55-006,321; 58-105,147; 59-010,539; 57-037,856; 53-003,263; and those of metal complexes are disclosed in U.S. Patents 4,050,938 and 4,241,155. Stabilizers that can be used with the invention include but are not limited to the following. In a preferred embodiment of the invention, a bisphenol stabilizer, such as ST-6, ST-7, ST-8, or ST-18, is combined with a yellow dye forming coupler in a loaded latex dispersion of the invention. Such combinations have been found to possess particularly advantageous light stability. The liquid organic, or oil phase, components of the dispersions of the invention may also include high-boiling or permanent organic solvents. High boiling solvents have a boiling point sufficiently high, generally above 150°C at atmospheric pressure, such that they are not evaporated under normal dispersion making and photographic layer coating procedures. Non-limitive examples of high boiling organic solvents that may be used include the following. S-1 Dibutyl phthalate S-2 Tritolyl phosphate S-3 N,N-Diethyldodecanamide S-4 Tris(2-ethylhexyl)phosphate S-5 Octyl oleate monoepoxide S-6 2,5-Di-t-pentylphenol S-7 Acetyl tributyl citrate S-8 1,4-Cyclohexylenedimethylene bis(2-ethylhexanoate) S-9 Bis(2-ethylhexyl) phthalate S-10 2-phenylethyl benzoate S-11 Dibutyl sebacate S-12 N,N-Dibutyldodecanamide S-13 Oleyl alcohol S-14 2-(2-Butoxyethoxy)ethyl acetate The dispersions of the invention may also include UV stabilizers. Examples of UV stabilizers are shown below. The aqueous phase of the dispersions of the invention may comprise a hydrophilic colloid, preferably gelatin. This may be gelatin or a modified gelatin such as acetylated gelatin, phthalated gelatin, oxidized gelatin, etc. Gelatin may be base-processed, such as lime-processed gelatin, or may be acid-processed, such as acid processed ossein gelatin. The hydrophilic colloid may be another water-soluble polymer or copolymer including, but not limited to poly(vinyl alcohol), partially hydrolyzed poly(vinylacetate/vinylalcohol), hydroxyethyl cellulose, poly(acrylic acid), poly(1-vinylpyrrolidone), poly(sodium styrene sulfonate), poly(2-acrylamido-2-methane sulfonic acid), polyacrylamide. Copolymers of these polymers with hydrophobic monomers may also be used. The loaded latex dispersions of the invention include surfactants. Useful surfactants include those customarily used in forming latex dispersions by emulsion polymerization and those used in forming small particle oil-in-water photographic dispersions. Such surfactants may be cationic, anionic, zwitterionic or non-ionic. In a preferred embodiment of the invention, the loaded latex dispersions are formed in the presence of anionic and/or nonionic surfactants. Ratios of surfactant to liquid organic solution typically are in the range of 0.5 to 25 wt.% for forming small particle photographic dispersions, which ratios are also useful for the invention dispersions. Useful surfactants include, but are not limited the following. CF 3 - (CF 2 ) 7 - SO 3 Na CH 3 - (CH 2 ) n - SO 3 Na n = 12-14 CH 3 - (CH 2 ) 11 - OSO 3 Na For the purposes of this invention, "high shear or turbulent" conditions defines shear and turbulence conditions sufficient to generate a small particle conventional photographic dispersion of a coupler with a coupler solvent, such as the formulation of Dispersion 301 of Example 3 below, with an average particle size of less than about 0.4 µm, while "low or moderate shear" mixing defines shear and turbulence conditions insufficient to generate such small particle dispersions for such formulations. Devices suitable for low or moderate shear mixing of the dispersions of the invention include standard mixing equipment used in the art to maintain overall thermal and chemical uniformity of a vessel of liquid material, including stirrers, propellers, circulating pumps, and moderate-shear blade mixers. Devices suitable for the high-shear or turbulent mixing of small-particle conventional dispersions that are subsequently combined with polymer latex to form dispersions of the invention include those generally suitable for preparing submicron photographic emulsified dispersions. These include but are not limited to blade mixers, rotor-stator mixers, devices in which a liquid stream is pumped at high pressure through an orifice or interaction chamber, sonication, Gaulin mills, homogenizers, blenders, etc. More than one type of device may be used to prepare the dispersions. Preferred latex polymers of the invention include addition polymers prepared by emulsion polymerization. Especially preferred are polymers prepared as latex with essentially no water-miscible or volatile solvent added to the monomer. Also suitable are dispersed addition or condensation polymers, prepared by emulsification of a polymer solution, or self-dispersing polymers. Especially preferred latex polymers include those prepared by free-radical polymerization of vinyl monomers in aqueous emulsion. Polymers comprising monomers that form water-insoluble homopolymers are preferred, as are copolymers of such monomers, which may also comprise monomers which give water-soluble homopolymers, if the overall polymer composition is sufficiently water-insoluble to form a latex. Examples of suitable monomers include allyl compounds such as allyl esters (e.g., allyl acetate, allyl caproate, etc.); vinyl ethers (e.g., methyl vinyl ether, butyl vinyl ether, methoxyethyl vinyl ether, ethoxyethyl vinyl ether, chloroethyl vinyl ether, 1-methyl-2,2-dimethylpropyl vinyl ether, hydroxyethyl vinyl ether, diethylene glycol vinyl ether, dimethylaminoethyl vinyl ether, butylaminoethyl vinyl ether, benzyl vinyl ether, tetrahydrofurfuryl vinyl ether, etc.); vinyl esters (such as vinyl acetate, vinyl propionate, vinyl butyrate, vinyl isobutyrate, vinyl dimethyl propionate, vinyl ethyl butyrate, vinyl chloroacetate, vinyl dichloroacetate, vinyl methoxyacetate, vinyl phenyl acetate, vinyl acetoacetate, etc.); vinyl heterocyclic compounds (such as N-vinyl oxazolidone, N-vinylimidazole, N-vinylpyrrolidone, N-vinylcarbazole, vinyl thiophene, N-vinylethyl acetamide, etc.); styrenes (e.g., styrene, divinylbenzene, methylstyrene, dimethylstyrene, ethylstyrene, isopropylstyrene, sodium styrenesulfonate, potassium styrenesulfinate, butylstyrene, hexylstyrene, cyclohexylstyrene, benzylstyrene, chloromethylstyrene, trifluoromethylstyrene, acetoxymethylstyrene, acetoxystyrene, vinylphenol, ( t -butoxycarbonyloxy)styrene, methoxystyrene, 4-methoxy-3-methylstyrene, dimethoxystyrene, chlorostyrene, dichlorostyrene, trichlorostyrene, bromostyrene, iodostyrene, fluorostyrene, methyl vinylbenzoate ester, vinylbenzoic acid, etc.); crotonic acids (such as crotonic acid, crotonic acid amide, crotonate esters (e.g., butyl crotonate, etc.)); vinyl ketones (e.g., methyl vinyl ketone, etc ); olefins (e.g., dicyclopentadiene, ethylene, propylene, 1-butene, 5,5-dimethyl-1-octene, etc.); itaconic acids and esters (e.g., itaconic acid, methyl itaconate, etc.), other acids such as sorbic acid, cinnamic acid, methyl sorbate, citraconic acid, chloroacrylic acid mesaconic acid, maleic acid, fumaric acid, and ethacrylic acid; halogenated olefins (e.g., vinyl chloride, vinylidene chloride, etc.); unsaturated nitriles (e.g., acrylonitrile, etc.); acrylic or methacrylic acids and esters (such as acrylic acid, methyl acrylate, methacrylic acid, methyl methacrylate, ethyl acrylate, butyl acrylate, butyl methacrylate, 2-hydroxyethyl methacrylate, 2-acetoacetoxyethyl methacrylate, sodium-2-sulfoethyl acrylate, 2-aminoethylmethacrylate hydrochloride, glycidyl methacrylate, ethylene glycol dimethacrylate, etc.); and acrylamides and methacrylamides (such as acrylamide, methacrylamide, N -methylacrylamide, N,N -dimethylacrylamide, N -isopropylacrylamide, N - s -butylacrylamide, N - t -butylacrylamide, N -cyclohexylacrylamide, N -(3-aminopropyl)methacrylamide hydrochloride, N -(3-dimethylaminopropyl)methacrylamide hydrochloride, N,N -dipropylacrylamide, N -(1,1-dimethyl-3-oxobutyl)acrylamide, N -(1,1,2-trimethylpropyl)acrylamide, N -(1,1,3,3-tetramethylbutyl)acrylamide, N -(1-phthalamidomethyl)acrylamide, sodium N -(1,1-dimethyl-2-sulfoethyl)acrylamide, N -butylacrylamide, N -(1,1-dimethyl-3-oxobutyl)acrylamide, N -(2-carboxyethyl)acrylamide, 3-acrylamido-3-methylbutanoic acid, methylene bisacrylamide.). In a preferred embodiment of the invention, the latex polymer comprises at least about 50% N-alkylacrylamide monomer units, where the alkyl substituent preferably has from 3-8 carbon atoms, such as N-tert-butylacrylamide units, which impart particularly desirable photographic performance in the elements of the invention. Polymers of similarly high glass transition temperature (Tg), e.g., higher than 60 °C and more preferably higher than 90°C, are also particularly preferred. Latex polymers generally comprise polymer particles having an average particle diameter of from about 0.02 to 2.0 µm. In a preferred embodiment of the invention, latex particles having an average diameter of from about 0.03 to 0.5 µm are used in the dispersions of the invention. In a more preferred embodiment, latex particles having an average diameter of from about 0.03 to 0.2 µm are used. The latex polymer average molecular weight generally ranges from about 1000 to 5,000,000 in non-crosslinked form. In a preferred embodiment of the invention, loaded latex dispersions of latex particles having an average molecular weight of from about 300,000 to 5,000,000 are formed. Dispersions with polymers having high molecular weight such as these are not easily formed by prior processes wherein a solution containing the polymer is emulsified and dispersed. In accordance with a further embodiment of the invention, where the latex polymers comprise crosslinked polymers, their molecular weight may far exceed 5,000,000. Specific examples of useful polymer latex materials are given below. Copolymer ratios indicated are weight ratios unless otherwise specified. P-1 Poly( N - tert -butylacrylamide) Tg ∼ 146°C P-2 Poly( N -cyclohexylamide) P-3 Poly( N - sec -butylacrylamide) P-4 Poly( N -(1,1,3,3-tetramethylbutyl)acrylamide) P-5 Poly( N -(1,1,2-trimethylpropyl)acrylamide) P-6 Poly( N -(1,1-dimethyl-3-oxobutyl)acrylamide) P-7 Poly( N -(1-phthalimidomethyl)acrylamide) P-8 Poly( N,N -di- n -propylacrylamide) P-9 N - tert -butylacrylamide/methylene bisacrylamide copolymer (98/2) P-10 N -cyclohexylacrylamide/methylene bisacrylamide copolymer (98/2) P-12 N -cyclohexylacrylamide/methylene bisacrylamide copolymer (98/2) P-13 1,1-dimethyl-3-oxobutyl)acrylamide/methylene bisacrylamide copolymer (98/2) P-13 Methyl acrylate/2-acrylamido-2-methylpropane sulfonic acid copolymer (96/4) P-14 Methyl acrylate/2-acrylamido-2-methylpropane sulfonic acid copolymer (98/2) P-15 Methyl acrylate/2-acrylamido-2-methylpropane sulfonic acid/2-acetoacetoxyethyl methacrylate copolymer (91/5/4) Tg ∼ 24°C P-16 Methyl acrylate/2-acrylamido-2-methylpropane sulfonic acid/ethylene glycol dimethacrylate copolymer (96/2/2) P-17 Butyl acrylate/2-acrylamido-2-methylpropane sulfonic acid sodium salt/2-acetoacetoxyethyl methacrylate copolymer (90/6/4) Tg ∼ -42°C P-18 Butyl acrylate/2-acrylamido-2-methylpropane sulfonic acid/ethylene glycol dimethacrylate copolymer (90/6/4) P-19 Butyl acrylate/styrene/methacrylamide/2-acrylamido-2-methylpropane sulfonic acid sodium salt copolymer (55/29/11/5) P-20 Butyl acrylate/styrene/2-acrylamido-2-methylpropane sulfonic acid sodium salt copolymer (85/10/5 P-21 Poly(butyl acrylate) P-22 Poly(hexyl acrylate) P-23 Poly(butyl methacrylate) P-24 Poly(hexyl methacrylate) P-25 Poly(vinylidene chloride) P-26 Poly(vinyl chloride) P-27 Styrene/vinyl acetate copolymer (1/1 molar) P-28 Styrene/methyl vinyl ether copolymer (1/1 molar) P-29 Ethylene/vinyl acetate copolymer (1/1 molar) P-30 Poly(glycidyl methacrylate) P-31 Poly(methyl methacrylate) Tg ∼ 110°C P-32 Glycidyl methacrylate/ethylene glycol dimethacrylate copolymer (95/5) P-33 Poly(acrylonitrile) P-34 Acrylonitrile/vinylidene chloride/acrylic acid copolymer (15/79/6) P-35 Styrene/butyl methacrylate/2-sulfoethyl methacrylate sodium salt copolymer (30/60/10) P-36 Polystyrene P-37 Poly(4-acetoxystyrene) P-38 Poly(4-vinylphenol) P-39 Poly(4- t -butoxycarbonyloxystyrene) P-40 2-(2'-Hydroxy-5'-methacrylyloxyethylphenyl)-2H-benzotriazole/ethyl acrylate/2-acrylamido-2-methylpropane sulfonic acid sodium salt copolymer (74/23/3) P-41 N - tert -butylacrylamide/3-acrylamido-3-methylbutanoic acid copolymer (99.5/0.5) P-42 N - tert -butylacrylamide/3-acrylamido-3-methylbutanoic acid copolymer (99.0/1.0) P-43 N - tert -butylacrylamide/3-acrylamido-3-methylbutanoic acid copolymer (98/2) P-44 N - tert -butylacrylamide/3-acrylamido-3-methylbutanoic acid copolymer (96/4) P-45 N - tert -butylacrylamide/3-acrylamido-3-methylbutanoic acid copolymer (92/8) P-46 N - tert -butylacrylamide/methyl acrylate copolymer (25/75) P-47 N - tert -butylacrylamide/methyl acrylate copolymer (50/50) P-48 N - tert -butylacrylamide/methyl acrylate copolymer (75/25) P-49 Poly(methyl acrylate) P-50 Methyl methacrylate/methyl acrylate copolymer (75/25) P-51 Methyl methacrylate/methyl acrylate copolymer (50/50) P-52 Methyl methacrylate/methyl acrylate copolymer (25/75) P-53 N - tert -butylacrylamide/2-acrylamido-2-methylpropane sulfonic acid sodium salt copolymer (98/2) P-54 N - tert -butylacrylamide/2-acrylamido-2-methylpropane sulfonic acid sodium salt copolymer (99/1) P-55 Methyl methacrylate/2-acrylamido-2-methylpropane sulfonic acid sodium salt copolymer (98/2) Suitable free-radical initiators for the polymerization include, but are not limited to the following compounds and classes. Inorganic salts suitable as initiators include potassium persulfate, sodium persulfate, potassium persulfate with sodium sulfite, etc. Peroxy compounds that may be used include benzoyl peroxide, t-butyl hydroperoxide, cumyl hydroperoxide, etc. Azo compounds that may be used include azobis(cyanovaleric acid), azobis(isobutyronitrile), 2,2'-azobis(2-amidinopropane) dihydrochloride. The latex polymers may additionally comprise photographically useful groups covalently bonded thereto, such as groups which function as photographic couplers, (including yellow, magenta and cyan image-forming couplers, colored or masking couplers, inhibitor-releasing couplers, and bleach accelerator-releasing couplers, dye-releasing couplers, etc.), UV absorbers, dyes, reducing agents (including oxidized developer scavengers and nucleators), stabilizers (including image stabilizers, stain-control agents, and developer scavengers), developing agents, optical brighteners, lubricants, etc. The process of the invention is generally applicable to a wide range of latex polymer to loaded liquid organic solution weight ratios. Preferred loading ratios are from about 50:1 to 1:20, more preferred ratios being from about 10:1 to 1:10. Advantaged photographic performance is often seen with ratios from 1:1 to 1:5, particularly for loaded latex dispersions of image forming couplers. These higher ratios of liquid organic solution to polymer are not often readily prepared by prior latex loading procedures. The photographic elements comprising the dispersions of the invention can be single color elements or multicolor elements. Multicolor elements contain image dye-forming units sensitive to each of the three primary regions of the spectrum. Each unit can comprise a single emulsion layer or multiple emulsion layers sensitive to a given region of the spectrum. The layers of the element, including the layers of the image-forming units, can be arranged in various orders as known in the art. In an alternative format, the emulsions sensitive to each of the three primary regions of the spectrum can be disposed as a single segmented layer. A typical multicolor photographic element comprises a support bearing a cyan dye image-forming unit comprised of at least one red-sensitive silver halide emulsion layer having associated therewith at least one cyan dye-forming coupler, a magenta dye image-forming unit comprising at least one green-sensitive silver halide emulsion layer having associated therewith at least one magenta dye-forming coupler, and a yellow dye image-forming unit comprising at least one blue-sensitive silver halide emulsion layer having associated therewith at least one yellow dye-forming coupler. The element can contain additional layers, such as filter layers, interlayers, overcoat layers, subbing layers. In a preferred embodiment, the loaded latex dispersions of the invention are used in a photographic element that may be displayed for extended periods under illuminated conditions, such as a color paper photographic element which comprises photographic layers coated on a reflective support. If desired, the photographic element can be used in conjunction with an applied magnetic layer as described in Research Disclosure , November 1992, Item 34390 published by Kenneth Mason Publications, Ltd., Dudley House, 12 North Street, Emsworth, Hampshire P010 7DQ, ENGLAND. In the following discussion of suitable materials for use in the emulsions and elements that can be used in conjunction with this photographic element, reference will be made to Research Disclosure , September 1994, Item 36544, available as described above, which will be identified hereafter by the term " Research Disclosure ." The Sections hereafter referred to are Sections of the Research Disclosure , Item 36544. The silver halide emulsions employed in these photographic elements can be either negative-working or positive-working. Suitable emulsions and their preparation as well as methods of chemical and spectral sensitization are described in Sections I, and III-IV. Vehicles and vehicle related addenda are described in Section II. Dye image formers and modifiers are described in Section X. Various additives such as UV dyes, brighteners, luminescent dyes, antifoggants, stabilizers, light absorbing and scattering materials, coating aids, plasticizers, lubricants, antistats and matting agents are described, for example, in Sections VI-IX. Layers and layer arrangements, color negative and color positive features, scan facilitating features, supports, exposure and processing can be found in Sections XI-XX. It is also contemplated that the materials and processes described in an article titled "Typical and Preferred Color Paper, Color Negative, and Color Reversal Photographic Elements and Processing," published in Research Disclosure , February 1995, Volume 370 may also be advantageously used with elements of the invention. Various types of hardeners are useful in conjunction with elements of the invention. In particular, bis(vinylsulfonyl) methane, bis(vinylsulfonyl) methyl ether, 1,2-bis(vinylsulfonyl-acetamido) ethane, 2,4-dichloro-6-hydroxy-s-triazine, triacryloyltriazine, and pyridinium, 1-(4-morpholinylcarbonyl)-4-(2-sulfoethyl)-, inner salt are particularly useful. Also useful are so-called fast acting hardeners as disclosed in U.S. Patents 4,418,142; 4,618,573; 4,673,632; 4,863,841; 4,877,724; 5,009,990; 5,236,822. The invention may also be used in combination with photographic elements containing filter dye layers comprising colloidal silver sol or yellow, cyan, and/or magenta filter dyes, either as oil-in-water dispersions, latex dispersions or as solid particle dispersions. Additionally, they may be used with elements containing "smearing" couplers (e.g. as described in U.S. Patent 4,366,237; EP 96,570; U.S. Patents 4,420,556 and 4,543,323.) Also, the compositions may be blocked or coated in protected form as described, for example, in Japanese Application 61/258,249 or U.S. Patent 5,019,492. The invention materials may further be used in combination with a photographic element containing image-modifying compounds such as "Developer Inhibitor-Releasing" compounds (DIR's). Due to a desire for rapid development, preferred emulsions for color paper are high in silver chloride. Typically, silver halide emulsions with greater than 90 mole % chloride are preferred, and even more preferred are emulsions of greater than 95 mole % chloride. In some instances, silver chloride emulsions containing small amounts of bromide, or iodide, or bromide and iodide are preferred, generally less than 5.0 mole % of bromide less than 2.0 mole % of iodide. Bromide or iodide addition when forming the emulsion may come from a soluble halide source such as potassium iodide or sodium bromide or an organic bromide or iodide or an inorganic insoluble halide such as silver bromide or silver iodide. Soluble bromide is also typically added to the emulsion melt as a keeping addendum. Color paper elements typically contain less than 0.80 g/m 2 of total silver. Due to the need to decrease the environmental impact of color paper processing, it is desired to decrease the amount of total silver used in the element as much as possible. Therefore, total silver levels of less than 0.65 g/m 2 are preferable, and levels of 0.55 g/m 2 are even more preferable. It is possible to reduce further the total silver used in the color paper photographic element to less than 0.10 g/m 2 by use of a so-called development amplication process whereby the incorporated silver is used only to form the latent image, while another oxidant, such as hydrogen peroxide, serves as the primary oxidant to react with the color developer. Such processes are well-known to the art, and are described in, for example, U.S. Patents 4,791,048; 4,880,725; and 4,954,425; EP 487,616; International published patent applications Nos. WO 90/013,059; 90/013,061; 91/016,666; 91/017,479; 92/001,972; 92/005,471; 92/007,299; 93/001,524; 93/011,460; and German published patent application OLS 4,211,460. The emulsions can be spectrally sensitized with any of the dyes known to the photographic art, such as the polymethine dye class, which includes the cyanines, merocyanines, complex cyanines and merocyanines, oxonols, hemioxonols, styryls, merostyryls and streptocyanines. In particular, it would be advantageous to use the low staining sensitizing dyes disclosed in U.S. Patents 5,316,904; 5,292,634; 5,354,651; and EP Patent Application 0 599 384, in conjunction with elements of the invention. Any photographic processor known to the art can be used to process the photosensitive materials described herein. For instance, large volume processors, and so-called minilab and microlab processors may be used. Particularly advantageous would be the use of Low Volume Thin Tank processors as described in the following references: WO 92/10790; WO 92/17819; WO 93/04404; WO 92/17370; WO 91/19226; WO 91/12567; WO 92/07302; WO 93/00612; WO 92/07301; WO 92/09932; U.S. Patent 5,294,956; EP 559,027; U.S. Patent 5,179,404; EP 559,025; U.S. Patent 5,270,762; EP 559,026; U.S. Patent 5,313,243; U.S. Patent 5,339,131. EXAMPLES: Example 1: Preparation of latex polymer P-1: t -Butylacrylamide (400 g, Chemie Linz) was slurried with vigorous mixing in a solution of water (968 g) and surfactant F-3 (25.0 g of a 40% aqueous solution). This slurry was added continuously over 15 minutes to an 80 °C stirred 1L Morton flask equipped with a condenser, under N 2 atmosphere, charged with water (600 g), surfactant F-3 (8.3 g of a 40% aqueous solution), and initiator (azobis(cyanovaleric acid) 75%, 4.0 g, Aldrich). The resulting translucent latex was stirred at 80° C for an additional 2 h. The latex was cooled and filtered, yielding 1959 g latex at 21.3% solids. Photon correlation spectroscopy showed an average particle size of 0.067 µm. A sample of the latex was freeze-dried. Proton nuclear magnetic resonance results: 1 H NMR (300 MHz, CDCl 3 ), δ = 1.15 (s, 9H), 1.2-2.2 (m, 3H), 5.6-6.5 (s, broad, 1H). Differential scanning calorimetry (DSC) showed a T g of 146 °C. Preparation of latex polymer P-31: Methyl methacrylate (500 g) was combined with water (925 g) and surfactant F-3 (25.0 g of a 40% aqueous solution). The monomer emulsion was pumped over ca. 60 minutes into an 80° C stirred Morton flask equipped with a condenser, under N 2 atmosphere, charged with water (625 g), surfactant F-3 (8.3 g of a 40% aqueous solution), and initiator potassium persulfate, 5.0 g. The resulting latex was stirred at 80° C for an additional 240 minutes. The latex was cooled and filtered, yielding 1933 g latex at 26.26% solids. Photon correlation spectroscopy showed an average particle size of 0.064 µm. These examples show that useful latex polymers, including polymers with high T g above 60°C and even above 90°C can be readily prepared by an emulsion polymerization process that uses no volatile or water-miscible organic solvent, and that such polymerization is also possible for polymers derived from solid, hydrophobic monomers that do not dissolve substantially in water. While both of these polymers form useful loaded latex dispersion of the invention with desirable photographic properties, methods in the prior art for preparing loaded latex dispersions are not suitable for use with these polymers. In particular, mixing the latex of either polymer P-1 or P-31 with an equal volume of water miscible organic solvent (specifically acetone, tetrahydrofuran, dimethylformamide, or acetonitrile) leads to rapid coagulation of the latex, showing that these polymers fail the "test of latex loadability" described in the prior art, e.g., in U.S. Patent 4,203,716. Example 2: Dispersion 101 was prepared by combining coupler Y-3 (45.0 g) and dibutyl phthalate (S-1) (25.2 g), and heating to 141° C, yielding an oil solution. This was combined with 329.8 g of an aqueous solution at 72° C containing 39.0 g gelatin and 4.0 g surfactant F-1, and the mixture was mixed for three minutes at 72° C with a blade mixer, yielding a moderately coarse dispersion. Average particle size, measured by PCS (Malvern Autosizer 2c) was found to be about 0.570 µm. (This particular PCS instrument can measure sizes this large, but in general measurements larger than about 0.350 µm tend to be somewhat imprecise, giving replication errors of about 0.050 µm on repeated measurements of the same sample.) Dispersion 102 was prepared by combining 8.0 g of dispersion 101, at 45° C, with 7.0 g of water at 45° C, and stirring the mixture by hand to obtain a uniform mixture. The sample was maintained at 45° C in a sealed container. Dispersions 103-105 were prepared similarly to dispersion 102, by combining 8.0 g of dispersion 101 with 7.0 g of an aqueous polymer latex of polymer P-1, with an average latex particle size of 0.067 µm, at the proper polymer concentration to achieve ratios of coupler Y-3 : polymer P-1 of 1.0 : 0.5, 1.0 : 1.0, and 1.0 : 1.5 respectively. Dispersions 106-108 were prepared similarly to dispersion 103-105, by combining 8.0 g of dispersion 101 with 7.0 g of an aqueous polymer latex of polymer P-15, (T g = 24° C) with an average latex particle size of 0.120 microns, at the proper polymer concentration to achieve ratios of coupler Y-3 : polymer P-15 of 1.0 : 0.5, 1.0 : 1.0, and 1.0 : 1.5 respectively. Dispersion 201 was prepared by passing 120 g of dispersion 101 three times at 72° C through a Microfluidizer model 110 homogenizer at a pressure of 68 MPa, yielding a fine-particle photographic dispersion. Average particle size by PCS was found to be about 0.300 µm. Dispersions 202-208 were prepared similarly to dispersions 102-108, comprising the same components, but by combining 8.0 g of the finer particle dispersion 201 with 7.0 g of water or an aqueous polymer latex of polymer P-1 or P-15, to achieve the coupler Y-3 : polymer ratios of 1.0:0.5, 1.0:1.0, and 1.0:1.5. The samples were maintained at 45° C without stirring after being prepared, and the apparent particle size was measured by PCS at various times after the samples were prepared. As mentioned before, PCS measurements are most sensitive to the larger size particles in a broad distribution, so the measurement effectively measures the larger coupler dispersion particles in the freshly prepared dispersions, rather than the much smaller latex particles. The PCS results are shown in the following tables, for samples 102-108, and 202-208. Sample Latex Coupler: Latex Ratio PCS at 8 min, µm PCS at 132 min, µm PCS at 1440 min, µm Comment 102 ― 1.0:1.0 0.564 0.541 0.670 Comparison 103 P-1 1.0:0.5 0.692 0.543 0.268 Invention 104 P-1 1.0:1.0 0.614 0.614 0.200 Invention 105 P-1 1.0:1.5 0.623 0.410 0.186 Invention 106 P-15 1.0:0.5 0.574 0.288 0.282 Invention 107 P-15 1.0:1.0 0.404 0.225 0.243 Invention 108 P-15 1.0:1.5 0.333 0.150 0.190 Invention Sample Latex Coupler: Latex Ratio PCS at 4 min, µm PCS at 1440 min, µm Comment 202 ― 1.0:1.0 0.309 0.273 Comparison 203 P-1 1.0:0.5 0.258 0.189 Invention 204 P-1 1.0:1.0 0.280 0.129 Invention 205 P-1 1.0:1.5 0.266 0.135 Invention 206 P-15 1.0:0.5 0.261 0.196 Invention 207 P-15 1.0:1.0 0.252 0.180 Invention 208 P-15 1.0:1.5 0.222 0.179 Invention As can be seen from the tables, the particle size of the comparison example 102 remains essentially unchanged during the experiment, within the accuracy of the measurement technique for such large particles. The dispersions of the invention, 103-108 all show a significant net decrease in measured particle size. Visual turbidity changes also corroborate this, with the comparison sample 102 remaining turbid and visually unchanged throughout the experiment, but the dispersions of the invention all became markedly less turbid. As can also be seen, the effect of increasing latex level in the dispersions, for both polymer P-1 and polymer P-15, is to accelerate the rate of particle size reduction and decrease the final particle size measured at 1440 minutes. Also apparent is the effect of the polymer identity on the rate of particle size decrease with time. Polymer P-15 decreases particle size rapidly, even after only 8 minutes, particularly at the highest level, while little particle size change is apparent for any of the samples containing polymer P-1 at 8 minutes. At 132 minutes, most of the particle size reduction has already occured for polymer P-15, and comparatively modest size reductions have occurred for the samples containing polymer P-1. Presumably, this faster rate of latex loading with polymer P-15 compared to polymer P-1, evidenced by a more rapid particle size reduction, is due primarily to the much lower T g of polymer P-15. Similar trends are observed for samples 202-208, where the loaded latex dispersions of the invention were prepared by combining a conventional small-particle dispersion with the latex. Little particle size change is noted for the comparison dispersion 202 with no latex. It is also notable that polymer P-15 appears to load more rapidly for samples 206-208, but that an ultimately smaller particle size is obtained for samples 203-205 containing polymer P-1. Example 3: Dispersion 301 was prepared by combining coupler Y-3 (237.7 g) and dibutyl phthalate (S-1) (133.1 g), and heating to 141° C, yielding an oil solution. This was added to 1640 g of an aqueous solution at 80° C, rapidly stirred with a rotor-stator mixer, said solution containing 156.0 g gelatin and 14.4 g surfactant F-1, yielding a coarse dispersion. This dispersion was homogenized at 34 MPa with a Crepaco homogenizer to yield a fine-particle photographic dispersion, with and average particle size (by PCS) of 0.277 µm. The dispersion was chill-set before being remelted for coating. Dispersion 302 was prepared by adding polymer latex P-1, with low-shear mixing, to a freshly prepared sample of dispersion 301, in an amount such that the coupler Y-3 : Polymer P-1 ratio was 1.00 : 0.80. The dispersion was stirred at 50°C for 30 minutes before chill-setting. The average particle size of the dispersion measured by PCS was 0.145 µm. Dispersion 303 was prepared in the same manner as dispersion 302, with a coupler Y-3 : Polymer P-1 ratio of 1.00 : 0.60. Coating sample 401, a blue-sensitive photographic element containing dispersion 301 in the emulsion layer was prepared by simultaneously coating the following layers. LAYER COMPONENT AMOUNT 3 F-2 0.004 g/m 2 Gelatin 1.076 g/m 2 2 UV-1 0.113 g/m 2 UV-2 0.640 g/m 2 ST-4 0.086 g/m 2 S-8 0.251 g/m 2 Gelatin 1.399 g/m 2 1 AG-1 Blue sensitive Ag 0.247 g Ag/m 2 Y-3 from dispersion 301 0.538 g/m 2 ST-15 0.009 g/m 2 Gelatin 1.539 g/m 2 Support Polyethylene laminated paper with TiO 2/ ZnO in the polyethylene laminated in the first layer side, precoated with 3.23 g/m 2 gelatin. In the layer 2, bis(vinylsulfonylmethyl) ether (0.143 g/m 2 ) was added as hardener. AG-1 Blue Emulsion : A high chloride silver halide emulsion was precipitated by equimolar addition of silver nitrate and sodium chloride solutions into a well-stirred reactor containing gelatin peptizer and thioether ripener. Cs 2 OS(NO)Cl 5 was added during the silver halide grain formation for most of the precipitation, followed by shelling without dopant. The resultant emulsion contained cubic shaped grains of 0.74 µm in edgelength size. This emulsion was optimally sensitized by the addition of water insoluble gold compound and heat ramped up to 60 °C during which time blue sensitizing dye BSD-1, 1-(3-acetamidophenyl)-5-mercaptotetrazole and potassium bromide were added. In addition, iridium dopant was added during the sensitization process. Coating samples 402-407 were prepared in the same manner as sample 401, using dispersion 301, to which polymer latex P-1 was added to the coating melt at various times before being applied to the support. The time the melt was held between adding the polymer and coating is shown in the table below. In each coating the coupler Y-3 : polymer P-1 ratio was 1.00 : 0.80. Coating sample 408 was prepared in the same manner as sample 401, using dispersion 302. Coating sample 409 was prepared in the same manner as sample 401, using dispersion 301, to which polymer latex P-1 in a coupler Y-3 : polymer P-1 ratio of 1.00 : 0.60 was added to the coating melt 45 minutes before being applied to the support. Coating sample 410 was prepared in the same manner as sample 401, using dispersion 303. The coatings 401-410 were exposed for 0.10 s at a color temperature of 3000 K through a Wratten W98 filter and a 0-3 density 21-step tablet, and were processed through the Kodak RA-4 process, described in the British Journal of Photography Annual of 1988, Pp 198-199, comprising the following processing solutions, times and temperatures. Kodak RA-4 process Developer 0'45" 35° C Bleach-Fix 0'45" 35° C Wash 1'30" 33-34° C The processed coatings were subjected to 14 day 50 klx irradiation with a daylight source. The light stability of each coating was measured as blue reflection density loss from density 1.0 and 0.5. Also, each processed coating was subjected to 28 days in a dark oven at 75° C and 50% R.H., and the density loss from density 1.7 was measured. The results are shown in the table below. Sample Coupler: Polymer P-1 Ratio Melt Time After P-1 Added 14 Day 50 klx Loss From 1.0 14 Day 50 klx Loss From 0.5 28 Day 75°C 50% RH Loss From 1.7 Comment 401 1.0 : 0.0 -- -0.50 -0.29 -0.12 Comparison 402 1.0 : 0.8 1 min -0.32 -0.20 -0.05 Invention 403 1.0 : 0.8 5 min -0.31 -0.20 -0.04 Invention 404 1.0 : 0.8 10 min -0.30 -0.20 -0.05 Invention 405 1.0 : 0.8 20 min -0.28 -0.19 -0.05 Invention 406 1.0 : 0.8 30 min -0.25 -0.16 -0.04 Invention 407 1.0 : 0.8 45 min -0.18 -0.12 -0.04 Invention 408 1.0 : 0.8 >200 min -0.14 -0.09 -0.04 Invention 409 1.0 : 0.6 45 min -0.23 -0.15 -0.05 Invention 410 1.0 : 0.6 >200 min -0.19 -0.12 -0.05 Invention As is evident from the table, the photographic elements of the invention show substantially improved image preservability toward both heat and light in comparison the sample containing no polymer. The time dependence of latex loading is also apparent from 402-408, with longer melt times after the addition of the latex polymer allowing more loading to occur, as manifest by improved light stability of the image formed. Comparison of sample 407 with 409, and 408 with 410 shows the expected trend that improved image preservability results from increasing amounts of polymer latex in the dispersion. Example 4: A dispersion was prepared by combining coupler Y-3 (30.0 g), stabilizer ST-6 (13.2 g) and dibutyl phthalate (S-1) (16.8 g), and heating to 141° C, yielding an oil solution. This was combined with 440 g of an aqueous solution at 70° C containing 26.0 g gelatin and 2.4 g surfactant F-1, and the combination at 70° C was mixed for 3 minutes with a blade mixer, yielding a coarse dispersion. This dispersion was homogenized at 68 MPa with a Microfluidizer model 110 homogenizer to yield a fine-particle dispersion. The dispersion was chill-set before use. Coating sample 501, a blue-sensitive photographic element containing this dispersion in the emulsion layer was prepared by sequentially coating the following layers on a support. LAYER COMPONENT AMOUNT 2 F-1 0.054 g/m 2 F-2 0.004 g/m 2 Dye-1 0.018 g/m 2 Gelatin 1.076 g/m 2 1 AG-1 Blue sensitive Ag 0.247 g Ag/m 2 Y-3 0.538 g/m 2 ST-6 0.237 g/m 2 S-1 0.301 g/m 2 ST-15 0.009 g/m 2 F-1 0.054 g/m 2 Gelatin 1.539 g/m 2 Support Polyethylene laminated paper with TiO 2/ ZnO in the polyethylene laminated in the first layer side, precoated with 3.23 g/m 2 gelatin. In the final layer bis(vinylsulfonylmethyl) ether (0.105 g/m 2 ) was added as hardener. Coating sample 502 was prepared in a similar manner, adding the appropriate amount of latex polymer P-1 to achieve a coating with 0.430 g/m 2 polymer, to the coating solution approximately 2 hours before the coating was prepared. In a similar manner, coating samples 503-532 were prepared with the variations of dispersion components and polymer changes in the emulsion layer 1 shown in the table below. Sample Coupler, g/m 2 Latex, g/m 2 ST-6, g/m 2 S-1 g/m 2 Comment 501 Y-3, 0.538 -- 0.237 0.301 Comparison 502 Y-3, 0.538 P-1, 0.430 0.237 0.301 Invention 503 Y-3, 0.538 -- -- 0.301 Comparison 504 Y-3, 0.538 P-1, 0.430 -- 0.301 Invention 505 Y-16, 0.969 -- 0.426 0.542 Comparison 506 Y-16, 0.969 P-1, 0.581 0.426 0.542 Invention 507 Y-16, 0.969 P-1, 1.162 0.426 0.542 Invention 508 Y-16, 0.969 -- -- 0.542 Comparison 509 Y-16, 0.969 P-1, 0.581 -- 0.542 Invention 510 Y-16, 0.969 P-1, 1.162 -- 0.542 Invention 511 Y-11, 0.538 -- -- 0.301 Comparison 512 Y-11, 0.538 P-1, 0.538 -- 0.301 Invention 513 Y-11, 0.538 P-1, 1.076 -- 0.301 Invention 514 Y-11, 0.538 -- 0.237 0.301 Comparison 515 Y-11, 0.538 P-1, 0.538 0.237 0.301 Invention 516 Y-11, 0.538 P-1, 1.076 0.237 0.301 Invention 517 Y-12, 0.538 -- -- 0.301 Comparison 518 Y-12, 0.538 P-1, 0.538 -- 0.301 Invention 519 Y-12, 0.538 P-1, 1.076 -- 0.301 Invention 520 Y-12, 0.538 P-17, 1.076 -- 0.301 Invention 521 Y-12, 0.538 -- 0.237 0.301 Comparison 522 Y-12, 0.538 P-1, 0.538 0.237 0.301 Invention 523 Y-12, 0.538 P-1, 1.076 0.237 0.301 Invention 524 Y-12, 0.538 P-17, 1.076 0.237 0.301 Invention 525 Y-13, 0.538 -- -- 0.301 Comparison 526 Y-13, 0.538 P-1, 0.538 -- 0.301 Invention 527 Y-13, 0.538 P-1, 1.076 -- 0.301 Invention 528 Y-13, 0.538 P-17, 1.076 -- 0.301 Invention 529 Y-13, 0.538 -- 0.237 0.301 Comparison 530 Y-13, 0.538 P-1, 0.538 0.237 0.301 Invention 531 Y-13, 0.538 P-1, 1.076 0.237 0.301 Invention 532 Y-13, 0.538 P-17, 1.076 0.237 0.301 Invention The coatings 501-532 were exposed for 0.10 s at a color temperature of 3000 K through a Wratten W98 filter and a 0-3 density 21-step tablet, and were processed through the Kodak RA-4 process described above. To obtain light stability information, each coating was covered with a UV filter layer coated on cellulose acetate support, containing 0.65 g/m 2 of a 15:85 by weight mixture of UV absorbers UV-1 and UV-2, 0.22 g/m 2 of solvent S-8, 0.074 g/m 2 of ST-4, and 1.26 g/m 2 of gelatin. The coatings were subjected to 14 day 50 klx irradiation with a daylight source. The light stability of the coating was measured as blue reflection density loss from density 1.7, 1.0 and 0.5. The hue of each processed coating was also measured at the exposure step nearest a blue optical density of 1.0. The position of the bathochromic edge of the absorption curve is indicated in the next column, which gives a normalized density at 500 nm, relative to a density of 1.0 at λ max for the dye. A smaller number means a sharper-cutting bathochromic edge of the dye absorption envelope. The results are shown in the table below. Sample Coupler, Polymer 14 Day 50 klx Loss From 1.7 14 Day 50 klx Loss From 1.0 14 Day 50 klx Loss From 0.5 Hue, 500nm Comment 501 Y-3, -- -0.31 -0.18 -0.15 0.572 Comparison 502 Y-3, P-1 -0.17 -0.10 -0.08 0.497 Invention 503 Y-3, -- -0.91 -0.54 -0.33 0.577 Comparison 504 Y-3, P-1 -0.29 -0.17 -0.13 0.482 Invention 505 Y-16, -- -0.48 -0.22 -0.17 0.399 Comparison 506 Y-16, P-1 -0.37 -0.16 -0.11 0.397 Invention 507 Y-16, P-1 -0.23 -0.10 -0.08 0.430 Invention 508 Y-16, -- -0.64 -0.30 -0.20 0.443 Comparison 509 Y-16, P-1 -0.40 -0.16 -0.09 0.442 Invention 510 Y-16, P-1 -0.20 -0.10 -0.08 0.433 Invention 511 Y-11, -- -0.92 -0.67 -0.39 0.535 Comparison 512 Y-11, P-1 -0.35 -0.22 -0.18 0.510 Invention 513 Y-11, P-1 -0.20 -0.14 -0.12 0.499 Invention 514 Y-11, -- -0.26 -0.18 -0.21 0.522 Comparison 515 Y-11, P-1 -0.18 -0.12 -0.15 0.511 Invention 516 Y-11, P-1 -0.10 -0.10 -0.09 0.502 Invention 517 Y-12, -- -1.18 -0.78 -0.40 0.512 Comparison 518 Y-12, P-1 -0.48 -0.30 -0.21 0.498 Invention 519 Y-12, P-1 -0.24 -0.16 -0.12 0.487 Invention 520 Y-12, P-17 -0.51 -0.38 -0.32 0.497 Invention 521 Y-12, -- -0.31 -0.24 -0.27 0.509 Comparison 522 Y-12, P-1 -0.17 -0.15 -0.16 0.492 Invention 523 Y-12, P-1 -0.11 -0.09 -0.09 0.487 Invention 524 Y-12, P-17 -0.24 -0.17 -0.18 0.495 Invention 525 Y-13, -- -1.17 -0.72 -0.38 0.527 Comparison 526 Y-13, P-1 -0.87 -0.56 -0.33 0.523 Invention 527 Y-13, P-1 -0.48 -0.32 -0.26 0.516 Invention 528 Y-13, P-17 -0.61 -0.37 -0.29 0.521 Invention 529 Y-13, -- -0.23 -0.18 -0.21 0.510 Comparison 530 Y-13, P-1 -0.19 -0.15 -0.20 0.511 Invention 531 Y-13, P-1 -0.13 -0.12 -0.15 0.507 Invention 532 Y-13, P-17 -0.20 -0.17 -0.19 0.516 Invention As can be seen from the table, the latex-loaded photographic elements of the invention all show decreased dye fade on irradiation relative to the corresponding comparison elements without polymer. Most of the elements of the invention also have less unwanted absorption of green light by the yellow dye, relative the the corresponding comparison elements without polymer. Coating samples 601-616 were prepared similarly to coating 503, using coupler Y-3 (0.538 g/m 2 ) and S-1 (0.301 g/m 2 ) in the emulsion layer 1, adding latex polymers to the coating solutions in the amounts shown in the table below. The coatings 601-616 were exposed and processed in the same manner as coating 503. The reactivity of the coupler was determined by measuring the maximum dye density formed for each coating. The hue of the dye formed and the stability of the image to irradiation were evaluated in the same manner as coating 503. Sample Polymer, g/m 2 Blue Dmax 14 Day 50 klx Loss From 1.7 14 Day 50 klx Loss From 1.0 14 Day 50 klx Loss From 0.5 Hue, 500nm Comment 503 -- 2.59 -0.91 -0.54 -0.33 0.577 Comparison 601 P-1, 0.538 2.53 -0.24 -0.12 -0.10 0.504 Invention 602 P-41, 0.538 2.60 -0.14 -0.09 -0.06 0.500 Invention 603 P-42, 0.538 2.57 -0.15 -0.08 -0.06 0.503 Invention 604 P-43, 0.538 2.59 -0.18 -0.11 -0.07 0.504 Invention 605 P-44, 0.538 2.58 -0.22 -0.10 -0.06 0.500 Invention 606 P-45, 0.538 2.58 -0.18 -0.11 -0.06 0.501 Invention 607 P-44, 0.753 2.47 -0.20 -0.10 -0.05 0.490 Invention 608 P-44, 0.969 2.35 -0.11 -0.05 -0.02 0.483 Invention 609 P-46, 0.538 2.60 -0.25 -0.13 -0.10 0.508 Invention 610 P-47, 0.538 2.62 -0.20 -0.11 -0.07 0.505 Invention 611 P-48, 0.538 2.63 -0.18 -0.10 -0.06 0.502 Invention 612 P-31, 0.538 2.63 -0.50 -0.30 -0.22 0.540 Invention 613 P-49, 0.538 2.65 -0.29 -0.17 -0.12 0.521 Invention 614 P-50, 0.538 2.74 -0.22 -0.14 -0.10 0.529 Invention 615 P-51, 0.538 2.75 -0.25 -0.12 -0.10 0.525 Invention 616 P-52, 0.538 2.66 -0.24 -0.13 -0.11 0.524 Invention It is apparent from this table that many polymers and copolymers may be advantageously employed in the photographic elements of the invention. The polymer containing coatings of the invention all show excellent dye-forming properties and high dye densities. The coating samples with the various polymers and copolymers all exhibit improved stability of the image dye toward irradiation, as well as improved dye hue. Example 5: A dispersion was prepared by combining coupler C-13 (42.66 g), dibutyl phthalate (S-1) (23.46 g), solvent S-14 (3.50 g) and stabilizer ST-4 (0.35 g), heating to 141° C, yielding an oil solution. This was combined with 380 g of a solution containing 42.66 g gelatin, 3.06 g surfactant F-1, and 334.28 g of water, and the mixture was mixed briefly with a blade mixer to yield a coarse dispersion (particle size >> 1 µm). The coarse dispersion was recycled for two turnovers at 68 MPa with a Microfluidizer model 110 homogenizer, yielding a fine particle dispersion. Coating sample 701, a red-sensitive photographic element containing this dispersion and an additional dispersion of ST-4 dissolved in S-1 in the emulsion layer, was prepared by coating the following layers. LAYER COMPONENT AMOUNT 2 F-1 0.054 g/m 2 F-2 0.004 g/m 2 Gelatin 1.076 g/m 2 1 AG-3 Red sensitive Ag 0.198 g Ag/m 2 C-13 0.423 g/m 2 S-1 0.238 g/m 2 ST-4 0.005 g/m 2 F-1 0.054 g/m 2 Gelatin 1.292 g/m 2 Support Polyethylene laminated paper with TiO 2/ ZnO in the polyethylene laminated in the first layer side, precoated with 3.23 g/m 2 gelatin. In the final layer bis(vinylsulfonylmethyl) ether (0.100 g/m 2 ) was added as hardener. AG-3 Red Emulsion : A high chloride silver halide emulsion was precipitated by equimolar addition of silver nitrate and sodium chloride solutions into a well-stirred reactor containing gelatin peptizer and thioether ripener. The resultant emulsion contained cubic shaped grains of 0.40 µm in edgelength size. This emulsion was optimally sensitized by the addition of water insoluble gold compound followed by a heat ramp, and further additions of 1-(3-acetamidophenyl)-5-mercaptotetrazole, potassium bromide and red sensitizing dye RSD-1. In addition, iridium and ruthenium dopants were added during the sensitization process. Coating examples 702-712 were prepared similarly to example 701, adding the appropriate amount of latex polymer to the coating solution, at 40°C, approximately 1 hour before the coatings were prepared, as indicated in the table below. The coatings were exposed for 0.10 s at a color temperature of 3000 K through a Wratten W29 filter and a 0-3 density 21-step tablet, and were processed through the Kodak RA-4 process. The red density loss from 1.0 density for each coating was measured after treatment at 60° C and 50% relative humidity for 28 and 42 days. Three of the coatings, 701, 704, and 706 were tested for ferrous ion sensitivity by treating processed samples of each coating for 5 minutes at 40° C in a nitrogen-purged solution prepared from water (7.0 L), ethylenediaminetetraacetic acid (EDTA, 256.8 g), FeSO 4 (222.4 g) adjusted to pH 5.00 with aqueous ammonia. The coatings were washed with water for 5 minutes, dried, and the density loss at 1.0 initial density was measured within 60 minutes. Sample Polymer Latex/ Amount g/m 2 28 Day 60°C 50% RH Loss 42 Day 60°C 50% RH Loss Fe2+ Loss From 1.0 Comment 701 -- -0.29 -0.37 -0.61 Comparison 702 P-1/0.106 -0.26 -0.35 -- Invention 703 P-1/0.212 -0.23 -0.31 -- Invention 704 P-1/0.423 -0.19 -0.27 -0.44 Invention 705 P-1/0.635 -0.09 -0.15 -- Invention 706 P-1/0.846 -0.02 -0.08 -0.41 Invention 707 P-17/0.212 -0.29 -0.37 -- Invention 708 P-17/0.423 -0.25 -0.34 -- Invention 709 P-17/0.846 -0.22 -0.30 -- Invention 710 P-31/0.212 -0.28 -0.37 -- Invention 711 P-31/0.423 -0.25 -0.34 -- Invention 712 P-31/0.846 -0.20 -0.26 -- Invention As can be seen from the table, the latex-containing coatings of this invention show improved dye thermal stability relative to the comparisons without polymer. Some dispersions of the invention also show decreased cyan leuco dye formation after treatments with ferrous ion. Example 6: A dispersion containing coupler Y-3 and S-1 was prepared according to the same formula and procedure as dispersion 301 in example 2. Coating sample 801, a blue-sensitive photographic element containing this dispersion in the emulsion layer was prepared by coating the following layers simultaneously on a reflective support. The single emulsion layer is derived from two separate coating solutions that were maintained separately at 40° C before coating, and were combined in an in-line mixer at the coating hopper immediately before being applied to the support. One solution, designated 1a, contained primarily the AgCl emulsion components, and the other, designated as 1b, contained primarily the yellow coupler dispersion. The gelatin in the coated layer 1 was divided equally between the two coating solutions. LAYER COMPONENT AMOUNT 3 F-2 0.004 g/m 2 Gelatin 1.076 g/m 2 2 UV-1 0.113 g/m 2 UV-2 0.640 g/m 2 ST-4 0.086 g/m 2 S-8 0.251 g/m 2 Gelatin 1.399 g/m 2 1a AG-1 Blue sensitive Ag 0.258 g Ag/m 2 Gelatin 0.829 g/m 2 1b Y-3 from dispersion 0.538 g/m 2 S-1 from dispersion 0.301 g/m 2 HgCl 2 0.002 mg/m 2 ST-15 0.009 g/m 2 Gelatin 0.829 g/m 2 Support Polyethylene laminated paper with TiO 2/ ZnO in the polyethylene laminated in the first layer side, precoated with 3.23 g/m 2 gelatin. In the layer 2, bis(vinylsulfonylmethyl) ether (0.145 g/m 2 ) was added as hardener. Coating samples 802-810 were prepared as shown in the following table, by adding the appropriate amount of polymer latex to achieve the desired amount of polymer in the coating. The latex was added either to coating solution 1a or 1b approximately one hour before the coating solutions were applied to the support, and the solutions were maintained at 40° C with gentle stirring after the polymer addition until the coatings were prepared. The coatings 801-810 were exposed for 0.10 s at a color temperature of 3000 K through a Wratten W98 filter and a 0-3 density 21-step tablet, and were processed through the Kodak RA-4 process, as previously described. The processed coatings were subjected to 28 day 50 klx irradiation with a daylight source. The light stability of each coating was measured as blue reflection density loss from initial densities of 1.7, 1.0 and 0.5. The results are shown in the table below. Sample Polymer, (g/m 2 ) From 1a Polymer, (g/m 2 ) From 1b 28 Day 50 klx Loss From 1.7 28 Day 50 klx Loss From 1.0 28 Day 50 klx Loss From 0.5 Comment 801 -- -- -1.32 -0.75 -0.35 Comparison 802 -- P-17, 0.54 -0.72 -0.45 -0.30 Invention 803 P-17, 0.54 -- -0.70 -0.44 -0.30 Invention 804 -- P-17, 1.08 -0.43 -0.27 -0.26 Invention 805 P-17, 1.08 -- -0.45 -0.27 -0.25 Invention 806 P-17, 0.54 P-17, 0.54 -0.40 -0.26 -0.24 Invention 807 -- P-1, 0.32 -0.73 -0.42 -0.24 Invention 808 P-1, 0.32 -- -1.09 -0.65 -0.32 Invention 809 -- P-1, 0.43 -0.66 -0.40 -0.25 Invention 810 P-1, 0.43 -- -1.04 -0.62 -0.32 Invention As can be seen from the table, the polymer-containing photographic elements of the invention all exhibited improved light stability compared to the comparative example. The improvement observed in coatings 802-806 with polymer P-17, with a low polymer glass transition temperature (T g = -42° C), depended mostly on the amount of polymer introduced. Only minor differences were seen if the polymer was stirred for one hour with the coupler dispersion or was mixed with the dispersion at the coating hopper immediately before coating, or whether some polymer latex was added to each dispersion. This suggests that the low T g polymer P-17 forms a loaded latex dispersion very readily. This also demonstrates that the methods of preparing loaded latex dispersions can practically include procedures where a solution containing the polymer latex and a solution containing an oil dispersion are combined only an extremely short time before a photographic element is prepared by coating the combined solution. While coatings 807-810 with polymer P-1 (T g = 145° C) were all significantly improved over the comparative example 801, a larger improvement was seen for the coatings prepared by stirring the polymer for one hour with the dispersion, than for the coatings where the polymer was combined with the dispersion at the coating hopper. This suggests that loading into the high T g polymer P-1 occurs more slowly than for polymers with lower T g . Another advantage of the dispersions of the invention is that the hue of the yellow dye formed in all of the coatings of the invention was more pure than that formed in the comparative example 801, showing substantially less unwanted absorption of green light. This was especially pronounced for the coatings with the highest level of polymer P-17, coatings 804-806, as well as samples 807 and 809 containing polymer P-1. Example 7: Coating sample 901 was prepared by coating the following layers on a paper support. LAYER COMPONENT AMOUNT 7 ST-4 0.022 g/m 2 S-1 0.065 g/m 2 F-1 0.009 g/m 2 F-2 0.004 g/m 2 Dye-1 0.018 g/m 2 Dye-2 0.009 g/m 2 Dye-3 0.007 g/m 2 Gelatin 1.076 g/m 2 6 UV-1 0.049 g/m 2 UV-2 0.279 g/m 2 ST-4 0.080 g/m 2 S-8 0.109 g/m 2 S-1 0.129 g/m 2 Gelatin 0.630 g/m 2 5 AG-3 Red sensitive Ag 0.218 g Ag/m 2 C-3 0.423 g/m 2 S-1 0.232 g/m 2 S-14 0.035 g/m 2 ST-4 0.004 g/m 2 Gelatin 1.087 g/m 2 4 UV-1 0.049 g/m 2 UV-2 0.279 g/m 2 ST-4 0.080 g/m 2 S-8 0.109 g/m 2 S-1 0.129 g/m 2 Gelatin 0.630 g/m 2 3 AG-2 Green sensitive Ag 0.263 g Ag/m 2 M-1 0.389 g/m 2 S-1 0.195 g/m 2 S-14 0.058 g/m 2 ST-2 0.166 g/m 2 ST-4 0.039 g/m 2 Gelatin 1.270 g/m 2 2 ST-4 0.094 g/m 2 S-1 0.282 g/m 2 ST-14 0.065 g/m 2 F-1 0.002 g/m 2 Gelatin 0.753 g/m 2 1 AG-1 Blue sensitive Ag 0.243 g Ag/m 2 Y-3 0.538 g/m 2 ST-6 0.237 g/m 2 S-1 0.301 g/m 2 ST-15 0.009 g/m 2 glycerol 0.162 g/m 2 Gelating 1.042 g/m 2 Support Polyethylene laminated paper with TiO 2 /ZnO in the polyethylene laminated in the first layer side. Bis(vinylsulfonylmethyl) ether (1.97% to total gelatin weight) was added as hardener. AG-2 Green Emulsion : A high chloride silver halide emulsion was precipitated by equimolar addition of silver nitrate and sodium chloride solutions into a well-stirred reactor containing gelatin peptizer and thioether ripener. Cs 2 Os(NO)Cl 5 dopant was added during the silver halide grain formation for most of the precipitation, followed by a shelling without dopant. Iridium dopant was added during the late stage of grain formation. The resultant emulsion contained cubic shaped grains of 0.30 µm in edgelength size. This emulsion was optimally sensitized with green sensitizing dye GSD-1, water insoluble gold compound, heat digestion followed by the addition of 1-(3-acetamidophenyl)-5-mercaptotetrazole and potassium bromide. Absorber dyes used were the following: Coating samples 902-918 were prepared similarly to 901, changing the components of the blue-sensitive emulsion layer 1 as shown in the table below. The coating samples of the invention were all prepared by adding the latex polymer with gentle stirring to the coating solution containing the coupler dispersion at 40° C approximately 1 hour before the coatings were prepared. Sample Coupler, g/m 2 Latex/ Size µm Latex g/m 2 ST-6 g/m 2 S-1 g/m 2 Comment 901 Y-3, 0.538 -- -- 0.237 0.301 Comparison 902 Y-3, 0.538 P-17/0.163 1.076 0.237 0.301 Invention 903 Y-3, 0.538 P-17/0.163 1.076 0.237 0.463 Invention 904 Y-3, 0.538 P-15/0.120 0.538 0.237 0.301 Invention P-17/0.163 0.538 905 Y-3, 0.753 P-1/0.067 0.430 0.332 0.421 Invention 906 Y-3, 0.753 -- -- -- 0.421 Comparison 907 Y-3, 0.753 P-1/0.067 0.452 -- 0.421 Invention 908 Y-3, 0.753 P-1/0.067 0.602 -- 0.421 Invention 909 Y-3, 0.753 P-1/0.067 0.753 -- 0.421 Invention 910 Y-3, 0.538 P-15/0.120 0.538 -- 0.301 Invention P-17/0.163 0.538 911 Y-11, 0.484 -- -- 0.213 0.271 Comparison 912 Y-11, 0.377 P-1/0.067 0.754 0.166 0.211 Invention 913 Y-11, 0.484 P-1/0.067 0.968 0.213 0.271 Invention 914 Y-11, 0.592 P-1/0.067 1.184 0.260 0.332 Invention 915 Y-11, 0.484 -- -- -- 0.301 Comparison 916 Y-11, 0.377 P-1/0.067 0.754 -- 0.301 Invention 917 Y-11, 0.484 P-1/0.067 0.968 -- 0.301 Invention 918 Y-11, 0.592 P-1/0.067 1.184 -- 0.301 Invention The coatings 901-918 were exposed for 0.10 s at a color temperature of 3000 K through a Wratten W98 filter and a 0-3 density 21-step tablet, and were processed through the Kodak RA-4 process, as previously described. The processed coatings were subjected to 28 day 50 klx irradiation with a daylight source. The light stability of each coating was measured as blue reflection density loss from initial densities of 1.7, 1.0 and 0.5. The results are shown in the table below. Sample Coupler, Stabilizer Polymer Latex/ Amount g/m 2 28 Day 50 klx Loss From 1.7 28 Day 50 klx Loss From 1.0 28 Day 50 klx Loss From 0.5 Comment 901 Y-3, ST-6 -- -0.97 -0.63 -0.33 Comparison 902 Y-3, ST-6 P-17/1.076 -0.38 -0.28 -0.29 Invention 903 Y-3, ST-6 P-17/1.076 -0.48 -0.42 -0.36 Invention 904 Y-3, ST-6 P-15/0.538 -0.35 -0.24 -0.24 Invention P-17/0.538 905 Y-3, ST-6 P-1/0.430 -0.42 -0.33 -0.25 Invention 906 Y-3, -- -- -1.32 -0.79 -0.40 Comparison 907 Y-3, -- P-1/0.452 -0.46 -0.29 -0.17 Invention 908 Y-3, -- P-1/0.602 -0.39 -0.22 -0.14 Invention 909 Y-3, -- P-1/0.753 -0.35 -0.17 -0.10 Invention 910 Y-3, -- P-15/0.538 -0.42 -0.28 -0.23 Invention P-17/0.538 911 Y-11, ST-6 -- -0.56 -0.52 -0.41 Comparison 912 Y-11, ST-6 P-1/0.754 -0.54 -0.42 -0.30 Invention 913 Y-11, ST-6 P-1/0.968 -0.42 -0.38 -0.29 Invention 914 Y-11, ST-6 P-1/1.184 -0.37 -0.32 -0.28 Invention 915 Y-11, -- -- -1.45 -0.86 -0.42 Comparison 916 Y-11, -- P-1/0.754 -0.63 -0.39 -0.27 Invention 917 Y-11, -- P-1/0.968 -0.48 -0.34 -0.25 Invention 918 Y-11, -- P-1/1.184 -0.39 -0.28 -0.25 Invention As can be seen from the table, the polymer-containing photographic elements of the invention all exhibited improved light stability compared to corresponding comparative examples. The coating samples 901, 902, 905, and 907-909 were tested for wet scratch resistance and wet adhesion to the support after 28 days aging at ambient conditions. The samples were submerged in Kodak RA-4 developer solution at 35°C for 45 seconds, and a perpendicular stylus with a spherical sapphire tip was drawn over the sample surface with a constantly increasing mass load. The load required for the stylus penetrate completely through the coating was measured for both styli of 0.20 mm and 0.38 mm diameter. The table below shows the average of the load for the two sizes of styli required to penetrate the coating. Sample Average grams load Comment 901 47 Comparison 902 56 Invention 905 61 Invention 907 81 Invention 908 76 Invention 909 80 Invention As can be seen from the table, many of the coatings of the invention showed excellent wet scratch resistance, requiring a higher load on the stylus for to scratch the wet coating, compared to the comparison example. Example 8: A coating sample 1001 is prepared by simultaneously coating the following layers on a reflective support. The blue-sensitive emulsion layer 1 comprises a loaded-latex dispersion of coupler Y-11 prepared according to the invention. LAYER COMPONENT AMOUNT 7 ST-4 0.021 g/m 2 S-1 0.064 g/m 2 F-1 0.009 g/m 2 F-2 0.004 g/m 2 Dye-1 0.021 g/m 2 Dye-2 0.009 g/m 2 Dye-3 0.019 g/m 2 Gelatin 1.076 g/m 2 6 UV-1 0.073 g/m 2 UV-2 0.276 g/m 2 ST-4 0.050 g/m 2 S-8 0.109 g/m 2 S-1 0.129 g/m 2 Gelatin 0.624 g/m 2 5 AG-3 Red sensitive Ag 0.212 g Ag/m 2 C-3 0.423 g/m 2 UV-2 0.272 g/m 2 S-1 0.415 g/m 2 S-14 0.035 g/m 2 ST-4 0.004 g/m 2 Gelatin 1.388 g/m 2 4 UV-1 0.073 g/m 2 UV-2 0.276 g/m 2 ST-4 0.050 g/m 2 S-8 0.109 g/m 2 S-1 0.129 g/m 2 Gelatin 0.624 g/m 2 3 AG-2 Green sensitive Ag 0.174 g Ag/m 2 M-2 0.344 g/m 2 S-4 0.564 g/m 2 ST-3 0.107 g/m 2 ST-16 0.180 g/m 2 ST-5 0.180 g/m 2 Gelatin 1.270 g/m 2 0.156 g/m 2 2 ST-4 S-1 0.468 g/m 2 ST-14 0.065 g/m 2 F-1 0.002 g/m 2 Gelatin 0.753 g/m 2 1 AG-1 Blue sensitive Ag 0.246 g Ag/m 2 Y-11 0.484 g/m 2 P-54 0.678 g/m 2 S-1 0.330 g/m 2 ST-15 0.009 g/m 2 Support Gelatin 1.593 g/m 2 Polyethylene laminated paper with TiO 2 /ZnO in the polyethylene laminated in the first layer side. A coating sample 1002 is prepared by simultaneously coating the following layers on a reflective support. The blue-sensitive emulsion layer 1 comprises a loaded-latex dispersion of coupler Y-3 prepared according to the invention. LAYER COMPONENT AMOUNT 7 ST-4 0.021 g/m 2 S-1 0.064 g/m 2 F-1 0.009 g/m 2 F-2 0.004 g/m 2 Dye-1 0.021 g/m 2 Dye-2 0.009 g/m 2 Dye-3 0.019 g/m 2 Gelatin 1.076 g/m 2 6 UV-1 0.073 g/m 2 UV-2 0.276 g/m 2 ST-4 0.129 g/m 2 S-8 0.109 g/m 2 S-1 0.387 g/m 2 Gelatin 1.076 g/m 2 5 AG-3 Red sensitive Ag 0.207 g Ag/m 2 C-13 0.423 g/m 2 UV-2 0.272 g/m 2 S-2 0.415 g/m 2 S-14 0.035 g/m 2 ST-4 0.004 g/m 2 Gelatin 1.388 g/m 2 0.073 g/m 2 4 UV-1 UV-2 0.276 g/m 2 ST-4 0.129 g/m 2 S-8 0.109 g/m 2 S-1 0.387 g/m 2 Gelatin 1.076 g/m 2 3 AG-2 Green sensitive Ag 0.166 g Ag/m 2 M-11 0.323 g/m 2 S-1 0.485 g/m 2 ST-1 0.107 g/m 2 Gelatin 1.270 g/m 2 2 ST-4 0.189 g/m 2 S-1 0.567 g/m 2 ST-14 0.065 g/m 2 F-1 0.002 g/m 2 Gelatin 1.130 g/m 2 1 AG-1 Blue sensitive Ag 0.269 g Ag/m 2 Y-3 0.753 g/m 2 P-54 1.076 g/m 2 ST-6 0.308 g/m 2 S-1 0.422 g/m 2 ST-15 0.009 g/m 2 Gelatin 1.54 g/m 2 Support Polyethylene laminated paper with TiO 2 /ZnO in the polyethylene laminated in the first layer side. A coating sample 1003 is prepared by simultaneously coating the following layers on a reflective support. The blue-sensitive emulsion layer 1 comprises a loaded-latex dispersion of coupler Y-11 prepared according to the invention. LAYER COMPONENT AMOUNT 7 ST-4 0.021 g/m 2 S-1 0.064 g/m 2 F-1 0.009 g/m 2 F-2 0.004 g/m 2 Dye-1 0.021 g/m 2 Dye-2 0.009 g/m 2 Dye-3 0.019 g/m 2 Gelatin 1.076 g/m 2 6 UV-1 0.073 g/m 2 UV-2 0.276 g/m 2 ST-4 0.129 g/m 2 S-8 0.109 g/m 2 S-1 0.387 g/m 2 Gelatin 1.076 g/m 2 5 AG-3 Red sensitive Ag 0.207 g Ag/m 2 C-13 0.423 g/m 2 UV-2 0.272 g/m 2 S-2 0.415 g/m 2 S-14 0.035 g/m 2 ST-4 0.004 g/m 2 Gelatin 1.388 g/m 2 4 UV-1 0.073 g/m 2 UV-2 0.276 g/m 2 ST-4 0.129 g/m 2 S-8 0.109 g/m 2 S-1 0.387 g/m 2 Gelatin 1.076 g/m 2 3 AG-2 Green sensitive Ag 0.166 g Ag/m 2 M-11 0.323 g/m 2 S-1 0.485 g/m 2 ST-1 0.107 g/m 2 Gelatin 1.270 g/m 2 2 ST-4 0.189 g/m 2 S-1 0.567 g/m 2 ST-14 0.065 g/m 2 F-1 0.002 g/m 2 Gelatin 1.130 g/m 2 1 AG-1 Blue sensitive Ag 0.246 g Ag/m 2 Y-11 0.538 g/m 2 P-54 0.985 g/m 2 ST-6 0.237 g/m 2 S-1 0.287 g/m 2 ST-15 0.009 g/m 2 Gelatin 1.54 g/m 2 Support Polyethylene laminated paper with TiO 2 /ZnO in the polyethylene laminated in the first layer side. Coatings 1001, 1002, and 1003 are given red, green and blue exposure and are processed using the Kodak RA-4 process. The elements show excellent color forming attributes, and show excellent image permanence. In particular, neutral color balance is preserved during fading caused by exposure to light. Example 9: A multilayer photographic negative element is produced by coating the following layers on a cellulose triacetate film support (coverage are in grams per meter squared, emulsion sizes as determined by the disc centrifuge method and are reported in Diameter x Thickness in µm). Layer 1 (Antihalation layer): black colloidal silver sol at 0.151; gelatin at 2.44; UV-7 at 0.075; UV-8 at 0.075; DYE-4 at 0.042; DYE-5 at 0.088; DYE-6 at 0.020; DYE-7 at 0.008 and ST-17 at 0.161. Layer 2 (Slow cyan layer): a blend of two silver iodobromide emulsions sensitized with a 1/9 mixture of RSD-2/RSD-3: (i) a small tabular emulsion (1.1 x 0.09, 4.1 mol % I) at 0.430 and (ii) a very small tabular grain emulsion (0.5 x 0.08, 1.3 mol % I) at 0.492; gelatin at 1.78; cyan dye-forming coupler C-2 at 0.538; bleach accelerator releasing coupler B-1 at 0.038; masking coupler MC-1 at 0.027. Layer 3 (Mid cyan layer): a red sensitized (same as above) silver iodobromide emulsion (1.3 x 0.12, 4.1 mol % I) at 0.699; gelatin at 1.79; C-2 at 0.204; D-6 at 0.010; MC-1 at 0.022. Layer 4 (Fast cyan layer): a red-sensitized (same as above) tabular silver iodobromide emulsion (2.9 x 0.13, 4.1 mol % I) at 1.076; C-2 at 0.072; D-6 at 0.019; D-5 at 0.048; MC-1 at 0.032; gelatin at 1.42. Layer 5 (Interlayer): gelatin at 1.29. Layer 6 (Slow magenta layer): a blend of two silver iodobromide emulsions sensitized with a 6/1 mixture of GSD-1/GSD-2: (i) 1.0 x 0.09, 4.1 mol % iodide at 0.308 and (ii) 0.5 x 0.08, 1.3% mol % I at 0.584; magenta dye forming coupler M-5 at 0.269; masking coupler MC-2 at 0.064; stabilizer ST-5 at 0.054; gelatin at 1.72. Layer 7 (Mid magenta layer): a green sensitized (as above) silver iodobromide emulsion: 1.3 x 0.12, 4.1 mol % iodide at 0.968; M-5 at 0.071; MC-2 at 0.064; D-7 at 0.024; stabilizer ST-5 at 0.014; gelatin at 1.37. Layer 8 (Fast magenta layer): a green sensitized (as above) tabular silver iodobromide (2.3 x 0.13, 4.1 mol % I) emulsion at 0.968; gelatin at 1.275; Coupler M-5 at 0.060; MC-2 at 0.054; D-1 at 0.0011; D-4 at 0.0011 and stabilizer ST-5 at 0.012. Layer 9 (Yellow filter layer): AD-1 at 0.108 and gelatin at 1.29. Layer 10 (Slow yellow layer): a blend of three tabular silver iodobromide emulsions sensitized with sensitizing dye BSD-2: (i) 0.5 x 0.08, 1.3 mol% I at 0.295 (ii) 1.0 x 0.25, 6 mol % I at 0.50 and (iii) 0.81 x 0.087, 4.5 mol % I at 0.215; gelatin at 2.51; yellow dye forming couplers Y-14 at 0.725 and Y-15 at 0.289; D-3 at 0.064; C-2 at 0.027 and B-1 at 0.003. Layer 11 (Fast yellow layer): a blend of two blue sensitized (as above) silver iodobromide emulsions: (i) a large tabular emulsion, 3.3 x 0.14, 4.1 mol % I at 0.227 and (ii) a 3-D emulsion, 1.1 x 0.4, 9 mol % I at 0.656; Y-14 at 0.725; Y-15 at 0.289; D-3 at 0.029; C-2 at 0.048; B-1 at 0.007 and gelatin at 2.57. Layer 12 (UV filter layer): gelatin at 0.699; silver bromide Lippman emulsion at 0.215; UV-7 at 0.011 and UV-8 at 0.011. Layer 13 (Protective overcoat): gelatin at 0.882. Hardener bis(vinylsulfonyl)methane hardener at 1.75% of total gelatin weight), antifoggants (including 4-hydroxy-6-methyl-1,3,3a,7-tetraazaindene), surfactants, coating aids, emulsion addenda, sequestrants, lubricants, matte and tinting dyes are added to the appropriate layers as is common in the art. Additional coating samples are prepared similarly using dispersions of the invention comprising polymer P-17 and polymer P-54 with couplers C-2, Y-14, Y-15, and M-5. Polymer:Coupler ratios in the dispersions range from 0.5:1.0 to 5.0:1.0. The dispersions of the invention show lower turbidity than the comparison dispersions, indicating smaller dispersion particle size. The photographic elements of the invention exhibit improved performance in many cases, including enhanced sensitometric performance, improved image permanence and greater physical durability.

Claims: A method for preparing a photographic element comprising at least one hydrophilic colloid layer coated on a support, comprising: (a) combining under conditions of low or moderate shear, in the presence of surfactant, and in the substantial absence of water-miscible or volatile organic solvents, a liquid organic composition comprising at least one photographically useful compound with an aqueous polymer latex, (b) holding the combination resulting from (a) in a liquid state for sufficient time for substantial loading of the organic composition into the polymer latex to occur, and (c) coating the loaded latex resulting from (b) on a support. The method of claim 1 wherein the combination resulting from (a) is held for a sufficient time for essentially complete loading of the organic composition into the polymer latex to occur. The method of claim 1 or 2 wherein the liquid organic composition is formed by combining one or more hydrophobic photographically useful compounds with one or more high-boiling solvents at a temperature sufficient to prepare a homogeneous organic solution, and the organic solution is then mixed with an aqueous solution containing gelatin, surfactant, and the polymer latex. The method of claim 1 or 2 wherein the liquid organic composition is first combined with an aqueous solution containing gelatin and surfactant to form an aqueous dispersion of the liquid organic composition, and the resulting dispersion is then combined with another aqueous solution containing the polymer latex. The method of any one of claims 1-4 wherein gelatin is also combined with the liquid organic composition and the polymer latex, the polymer has a glass transition temperature (Tg) of 60°C or more, and the combination resulting from (a) is held for at least 1 hour in a liquid state below 60 °C before coating on the support. The method of any one of claims 1-5 wherein the polymer latex has an average particle size less than 0.20 µm. The method of any one of claims 1-6 wherein the liquid organic composition comprises a photographically useful compound with a logP less than 9.0 (logP is the logarithm of the value of the octanol/water partition coefficient (P) of the compound). The method of any one of claims 1-7 wherein the liquid organic composition comprises a photographic coupler. The method of any one of claims 1-8 wherein the aqueous polymer latex is selected from polymers which coagulate upon mixing with an equal volume of water-miscible organic solvent, chosen from acetone, tetrahydrofuran, dimethylformamide, or acetonitrile. A photographic element formed by the method of any one of claims 1-9.

Inventors: HONAN JAMES STEPHEN, NIELSEN RALPH BENDT, ROSIEK THOMAS ARTHUR, HONAN, JAMES STEPHEN, NIELSEN, RALPH BENDT, ROSIEK, THOMAS ARTHUR, HONAN, JAMES STEPHEN, C/O EASTMAN KODAK CO., NIELSEN, RALPH BENDT, C/O EASTMAN KODAK CO., ROSIEK, THOMAS ARTHUR, C/O EASTMAN KODAK CO.
Applicants: EASTMAN KODAK CO, EASTMAN KODAK COMPANY
Application year: 1996
Main classification: G03C7
IPC codes: G03C1, G03C7