A method and apparatus for adjusting casting sand using the optimum compactibility

Abstract: An adjusting method and apparatus is provided for optimizing the CB of casting sand relative to the deformation properties of a casting mold. The method consists of measuring compactibility of casting sand by compactibility measuring means 4 and a value of compressive deformation of a sample mold 10 corresponding to the compactibility by compressive deformation measuring means 5, repeating the measuring step at least three times, and operating the optimum compactibility, at which the value of compressive deformation of the sample mold 10 is the minimum, by operation means 7.

Description: Background of the Invention This invention relates to a method of adjusting casting sand, and more particularly to a method and apparatus for determining the optimum compactibility (hereinafter referred to as CB) of the casting sand, and for adjusting the casting sand accordingly. It is well-known that CB is controlled to adjust casting sand in kneading batches (see, for example, Japanese Patent Publication No. 3-76710). In this method, the CB of casting sand is controlled by adding water, while amounts of additives, such as bentonite, new sand, and fine powder, are kept constant in a batch so as to achieve a given target value of the CB. However, the CB of casting sand, as a target value for the control, has been only empirically set, and there has been no method of determining its optimum CB. On the one hand, there is a method of adjusting the amounts of additives, such as bentonite, new sand, and fine powder, to adjust casting sand on a long-term basis. In this method, the amounts of additives, such as bentonite, are adjusted by measuring the degree of ventilation, the resisting force, the percentage of active clay, and the percentage of total clay, on an hourly or a daily basis. The purpose of this is to keep constant the properties of the casting sand, such as the particle size distribution and percentage of clay thereof. This is because the casting sand is differently affected by heat when being circulated, including during kneading, molding, casting, demolding, and recovery, depending on the weights, shapes, and ratios of sand to metal, of the cast products, and because the casting sand is carried away with the product or through a dust collector. However, there has been almost no such long-term adjusting method, wherein the deformation property of a casting mold has been considered. In other words, the deformity of a casting mold results from transportation thereof, casting of molten metal thereinto, or loading of weights thereon. Further, this deformity of the mold affects high-precision or thin-walled cast products, which are now strongly demanded in the industry. However, in a conventional long-term adjusting method for casting sand, these relationships relative to the deformities of a casting mold have not been considered, not to mention that there has been no idea to connect the long-term adjustment of the casting sand to the CB. Thus, heretofore there has been no attempt to optimize the target value of the CB on a batch basis or long-term basis. So, US-4,291,379 discloses a method for adjusting sand by intermittently measuring the compactibility of a test sample of casting sand during a regeneration process by determining the reduction in height of the sample under the action of a predetermined force. Based on these measurements and the temperature of the sample, the quantity of water to be added to the sand is calculated in order to obtain sand having the desired properties. The compressive strength of the test sample is then measured. Based on both measurements, the quantity of bentonite and other additives to be added is calculated. In a similar way, an apparatus as described in EP-0 042 598 measures the compressibility of casting sand and the compressive strength by compressing a test sample of the sand within a cylinder. Since these known methods measure the deformation of test samples of casting sand to be adjusted for general-molding-sand-characteristics but do not measure any sample which truly represents the deformation properties of a sample mold molded from the casting sand, the above-mentioned problems can occur. By considering such present circumstances, this invention was devised to provide a method for determining the optimum compactibility of casting sand, which is connected to the deformation properties of the casting mold in adjusting the casting sand. To achieve the above-mentioned purpose, the method of this invention for determining the optimum compactibility of casting sand comprises measuring the compactibility of a sample of the casting sand and a value of the compressive deformation of a sample mold formed from the sample, thereby generating measurements indicative of the compactibility and the compressive deformation, repeating the measuring step at least three times, each time on a different sample of the casting sand, and processing the resulting measurements to determine an optimum compactibility of the casting sand at which the value of the compressive deformation of the casting sand is the minimum, based on a relationship between the values of the compactibility and the compressive deformation of the casting sand. This invention can determine the optimum CB of casting sand, wherein a value of compressive deformation of an actual casting mold is the minimum, by using the above-mentioned means of resolving these matters. This invention was based on the following observations. The inventor found that the value of compressive deformation could be associated with CB by selecting the deformation value as a casting-mold characteristic. That is, a case is estimated wherein the value of deformation of an actual casting mold is the minimum, by forming a sample casting mold, and by measuring the value of compressive deformation thereof. The representative characteristics of casting sand are then replaced by those of the sample mold, whose value of compressive deformation is the minimum. Conversely, it was deemed that a casting mold, whose value of deformation is the minimum, can be made by controlling the representative characteristics of the casting sand. The representative characteristics of the casting sand include a particle-size index, a percentage of total clay, or an ignition loss of the cumulatively kneaded sand. However, it was difficult to grasp relationships in a kneading batch between a compressive-deformation value and a particle-size index, or a total-clay percentage, or an ignition loss. Therefore, I found a method wherein the compressive-deformation value of casting sand was indirectly controlled by assuming the CB to be a representative characteristic, since the control of the CB in a kneading batch is comparatively easy. Although it has been unclear what the relationship is between the compressive-deformation value of casting sand and the CB, the inventor found the relationships as in Fig. 1 after repeated experiments on this point. Fig. 1 shows the relationships between the CB percentages and values of distortion when a constant compressive load is applied to sample casting molds. In kneading recovered sand A and B and new sand, they have their respective different relationships between the CB percentages and compressive-deformation values, and the CB percentage, where the compressive-deformation value is the minimum, becomes smaller in sequence from the recovered sand A to B to new sand. Further, even if the kinds of sand differ, as for A, B, and the new one, the curves are always convex downward within a range of the CB percentages usually in use. Thus, to minimize the compressive-deformation value the CB may be controlled so as to minimize its compressive-deformation value. As stated above, this invention aims to find the relationship between the CB and distortion values when a constant compressive load is applied thereto, and to adjust the optimum casting sand by applying this relationship to the control of the CB. Brief Description of the Drawings Fig. 1 shows graphs showing relationships between the compressive deformation of sample casting molds formed from various types of casting sand and the CB. Fig. 2 is a schematic diagram of an embodiment of this invention. Preferred Embodiments An embodiment of this invention will now be explained in detail by reference to the drawings. Fig. 2 exemplifies a constitution for implementing this invention. Sampling means 2 is provided by a kneader 1. The sampling means 2 samples casting sand 3 being kneaded. Under the sampling means 2, measuring means 30 is provided for measuring the properties of the casting sand 3, which consists of CB-measuring means 4 for measuring the CB of the casting sand and compressive-deformation measuring means 5 for measuring the compressive-deformation value of a sample mold 10 formed from the casting sand 3. Both the CB-measuring means 4 and compressive-deformation measuring means 5 are electrically connected to store means 6. Processing means 7 is also electrically connected to the store means 6, which is electrically connected to CB-control means 8. The details of each means will now be explained. The CB-measuring means 4 measures the rate of the fall of the casting sand 3 when a fixed quantity of the casting sand 3 is measured and put into a test cylinder 9, and then compressed. The value of the fall is actually measured by an encoder 13 mounted on a servomoter 11. The CB-measuring means 4 is well-known by, for example, Japanese Patent Publication No. 1-15825. Although the compressive-deformation measuring means 5 should measure an actual mold formed from the molding sand having target CB, to do so is practically impossible. Thus, it should be noted that in this invention sample molds are used that can practically represent the properties of the actual casting molds, although the measuring means are substantially the same as those of the conventional ones. The compressive-deformation (compressability) measuring means 5 for the sample mold operates as follows: for example, a cylindrical sample mold 10 (50mm in diameter and 50mm in height) is formed by compressing a fixed amount of the casting sand 3, which has been measured and put into the test cylinder 9; the compressive-deformation value is measured while the test mold 10 is being compressed both from the upper and lower ends; actually, the load is measured as a resisting force by a load cell 12, and the test mold 10 is measured by the encoder 13, while the speed and torque are controlled by the servomotor 11. The compressive-deformation measuring means 5 consists of the load cell 12 mounted on a well-known apparatus, as shown in, for example, Japanese Utility Model Early-publication No. 5-71752. A microcomputer is used as the store means 6 and the processing means 7. The CB control means 8 operates as follows: when the kneader 1 starts kneading the casting sand 3, the properties of the casting sand 3 are measured by an automatic measuring device; the resultant measurements are sent to the control means so as to calculate the quantity of water needed to be added to enable the casting sand 3 being kneaded to achieve the target CB value; the water is thus supplied from a water tank or a supply pipe. The CB control means 8 is well-known, for example, by Japanese Utility Model Publication No. 63-34775. The operations of the apparatus constituted as described above will now be explained. The sampling means 2 disposed by the kneader 1 samples the casting sand 3 while the sand 3 is being loosened by a spring 2a. The casting sand 3 is put into the CB measuring means 4 to measure the CB. The casting sand 3 of the same CB is put into the compressive-deformation-value measuring means 5 to form the sample mold 10 so as to measure the resisting force and distortion. Next, the data on the values of the CB, resisting force, and distortion, are read out from the store means 6 to calculate the value of the CB and distortion under a constant compressive load, by the processing means 7. The value of the CB, at which value the amount of distortion under the constant compressive load is the minimum, is calculated by the processing means 7 to obtain a relationship between the CB and distortion so as to obtain the CB at which the distortion is the minimum. For this calculation, for example, the least square method can be used. The target CB value is then obtained by replacing the CB at which the distortion is the minimum under the constant compressive load with the target CB value. By using the obtained target CB value, the quantity of water to be added to the casting sand being kneaded is controlled by the CB control means 8 so as to achieve a mold characteristic, which enables the compressive deformation value of the casting sand 3 to be the minimum. As stated above, this invention can provide a method of determining the optimum CB, enabling the compressive deformation value to be the minimum, by indirectly monitoring the compressive deformation value, which is one of the casting mold's characteristics. In this embodiment, a method incorporated in a sand adjusting line has been disclosed. However, the apparatus of this invention may also be disposed in a place remote from the sand adjusting line, for example, in a laboratory, and there the optimum CB value of the casting sand can be determined so as to operate the CB control means 8 by replacing the target CB value with that value. Further, the means for determining the target CB value in the sand adjusting line can be disposed in any location, for example, near the mold-forming means, instead of a position just under the kneader. For the actual control of the CB, the target CB may be set by considering variations of the casting sand being carried, based on the optimum CB. Although the compressive-deformation value was obtained from the values of the resisting force and distortion of the sample mold 10 formed from the casting sand, the CB of which mold was measured, this method is not limited thereto. Although a cylindrical sample casting mold was used to measure the compressive-deformation value, any shape or size mold may also be used. In short, any type of casting mold may be used so long as the CB of the casting mold and the compressive deformation value corresponding to the CB can be measured. As can be seen from the above-mentioned descriptions, the method of this invention for adjusting casting sand enables the acquisition of the optimum CB or the casting sand, with which the minimum value of the compressive deformation of an actual mold is obtained, to be adjusted. Thus, this invention has significant effects in the industry in that the deformation of a casting mold during transportation or the expansion of a casting mold during casting can be kept to the minimum.

Claims: A method of determining the optimum compactibility of casting sand (3), comprising the steps of measuring the compactibility of a sample of the casting sand (3) and a value of compressive deformation of a sample mold (10) formed from the sample, thereby generating measurements indicative of the compactibility and of the compressive deformation, repeating the measuring step at least three times, each time on a different sample of the casting sand (3), and processing the resulting measurements to determine an optimum compactibility of the casting sand (3) at which the value of the compressive deformation of the casting sand (3) is the minimum, based on a relationship between the values of the compactibility and the compressive deformation of the casting sand. Method of claim 1, wherein the compressive deformation measuring means (5) for the sample mold (10) comprises measuring the compactibility of the casting sand, and measuring values of a resisting force and distortion of a sample mold (10), formed from the casting sand whose compactibility corresponds to said compactibility. Method of claim 1, wherein the step of processing the resulting measurements to determine the optimum compactibility of the casting sand comprises storing measurements of compactibility, a resisting force, and distortion, by storing means (6), and calculating a compactibility value, at which the distortion value under a constant compressive load is the minimum, by using data read out from the storing means (6). An apparatus for determining the optimum compactibility of casting sand comprising compactibility measuring means (4) for measuring the compactibility of the casting sand, compressibility measuring means (5) for measuring values of compressive deformation of a sample mold (10), molded with casting sand of the same compactibility, and processing means (7) for processing the measurements of the compactibility measuring means for determining the optimum compactibility, at which a compressive deformation value of the sample mold (10) is at its minimum. A method of adjusting casting sand, wherein casting sand (3) in kneading means (1) is sampled by sampling means, mounted on the kneading means (1), and wherein the casting sand (3) is adjusted by adding water in response to a measurement of compactibility values of the sampled casting sand (3) so as to obtain a target compactibility value, the method comprising measuring the compactibility of a sample of the casting sand (3) being kneaded in the kneading means (1), and measuring values of a resisting force and distortion of a sample mold (10) formed from the casting sand (3) to calculate the compressive deformation of the sample mold (10), determining an optimum compactibility at which a value of compressive deformation of the sample mold (10) is the minimum utilizing processing means (7) for processing the measurement values, and replacing a target compactibility value according to the optimum compactibility.

Inventors: NISHIDA TADASHI, NISHIDA, TADASHI
Applicants: SINTOKOGIO LTD, SINTOKOGIO, LTD.
Application year: 1996
Main classification: B22C19
IPC codes: B22C1, B22C23, B22C5, B22C19, G01N33, B22C9