Preparation of aromatic polyesters

Abstract: An improved process for the preparation of aromatic polyesters which comprises (i) providing an amorphous poly(arylester) prepolymer containing hydroxyl and ester groups formed by melt polymerizing at least one dialkyl ester of an aromatic dicarboxylic acid with an aromatic bisphenol in presence of a catalyst, (ii) crystallizing the poly(arylester) prepolymer by suspending it in a diluent and heating at for example reflux temperature for a period in the range of for example 2-4 hours, (iii) separating and drying the crystallized poly(arylester) prepolymer, and (iv) heating the crystallized poly(arylester) prepolymer in such a way that the polymer remains solid, by conventional methods.

Description: This invention relates to an improved process for the preparation of aromatic polyesters from dialkyl esters of aromatic dicarboxylic acids and dihydric phenols, particularly high molecular weight (Mn 12,000-15,000) aromatic polyesters. Aromatic polyesters are a class of polymers generally made from bisphenol(s) and aromatic diacid(s), particularly mixtures of terephthalic acid and isophthalic acid. These polyesters are high performance transparent thermoplastics with a good combination of thermal and mechanical properties. They are processed by injection molding, extrusion and film forming techniques for conversion to different types of useful products. Amorphous polyesters are generally prepared by melt polymerization. One such melt polymerisation is the diacetate process, in which a dihydric phenol is converted to its diester derivative which is then reacted with an aromatic dicarboxylic acid to yield an aromatic polyester. In this context reference may be made to US-A 4,374,239, 4,386,186, 4,330,668 and 4,485,230. Aromatic polyesters made by the diacetate process have a tendency to be coloured which makes them unsuitable for many applications. Another problem is the formation of carboxylic acid as a by-product, which is corrosive and requires special material for reactor construction. DE-A 3,824,069 describes a variation of the diacetate process. In this process the aromatic polyester is produced by reacting a dialkyl ester of an aromatic dicarboxylic acid with bisphenol-A diacetate in presence of a catalyst. Methyl acetate comes out as a by-product, however, and it cannot be recycled in the process. US-A-5,340,908 describes a process for the preparation of aromatic polyesters by melt polymerization using the alcoholysis route. The first step of the process comprises the preparation of a polyester prepolymer having an intrinsic viscosity in the range of 0.10 to 0.30 dl/g by reacting dimethyl esters of terephthalic acid and isophthalic acid with bisphenol-A in the melt phase in presence of solvent and catalyst. The second step consists of the melt polymerization of the purified polyarylate prepolymer in the presence of a catalyst. The drawback of the melt polymerization processes is that melt viscosities increase dramatically with increases in molecular weight, causing problems in agitation and heat transfer and consequent impact on product quality and process economics. Solid state polycondensation is a commonly practised technique to obtain high molecular weight crystalline polymers such as poly(ethylene terephthalate), nylon-6,6 etc. In this technique, polycondensation is generally carried out by heating a semicrystalline prepolymer in a stream of inert gas or under vacuum at a temperature just below the polymer melting temperature. The salient features of solid state polycondensation are (1) the prepolymer is handled in powdered (or chip) form, and thus the process requires a very simple reactor design, (2) the reaction temperatures employed are very much lower than in melt polycondensation, and hence a clean reaction is observed devoid of side reactions of thermal degradation, and (3) very high molecular weight polycondensates can be prepared, which are inaccessible through a melt process. The prior literature reports few variations of the diacetate process for the preparation of aromatic polyesters by a solid state polycondensation of prepolymer. US-A 3,684,766 discloses a process for preparing copolyesters by reacting bisphenol-A diacetate with terephthalic acid and isophthalic acid. The resulting prepolymer is contacted with a crystallization medium. The crystallized prepolymer is heated in a fluidized bed, at a temperature below the melting point, for certain period to achieve a copolyester having inherent viscosity of 0.50 or more. US-A 4,314,051 describes a process for preparing crystalline prepolymers by reacting a diester of a dihydric phenol with an aromatic dicarboxylic acid and then heating the prepolymer below its melting point to form a crystalline polyester having a reduced viscosity of 0.45 to 1.20 dl/g. US-A 4,994,546 describes a process for the preparation of an aromatic polyester from a prepolymer prepared by reacting bisphenol-A, acetic anhydride and an aromatic dicarboxylic acid. The prepolymer is polycondensed under agitation to form a powdery solid which is further polymerized until the desired molecular weight is achieved. US-A 5,164,478 discloses a process for the preparation of an aromatic polymer having low colour wherein bisphenol-A, acetic anhydride, terephthalic acid and isophthalic acid are melt polymerized to form a prepolymer. The prepolymer is then treated with a crystallization medium and then further polymerized in the solid state by heating the prepolymer below its melting point under an inert gas flow. The prior art solid state polycondensation processes use prepolymers prepared by acidolysis of bisphenol-A diacetate by terephthalic acid and isophthalic acid. The prepolymers contain acetate and carboxylic end groups which react further under solid state polycondensation conditions yielding high molecular weight polyester with the formation of acetic acid as a by-product. The disadvantage of the above process is that it is not easy to remove acetic acid. Furthermore, acetic acid handling requires equipment constructed with special materials. Furthermore, the presence of traces of acetic acid in the product may affect the thermal stability of the polyester. An object of the present invention is to provide an improved process for the preparation of aromatic polyesters employing poly(arylester) prepolymers containing dialkyl and ester groups. Accordingly, the invention uses poly(arylester) prepolymers which contain hydroxyl and ester end groups, employs solid state polycondensation methods and yields high molecular weight (Mn = 12,000-15,000) products. In the present process, methyl alcohol is formed as a by-product. Since methyl alcohol is a low boiling compound it can be removed conveniently and efficiently from the reactor. The recovered methyl alcohol can be effectively used. Poly(arylester) prepolymers containing hydroxyl and ester groups have not been used in the prior art for preparation of aromatic polyesters by solid state polycondensation techniques. The main objective of the present invention is therefore to provide an improved process for the preparation of high molecular weight aromatic polyesters overcoming the drawbacks of hitherto known processes. Accordingly, the present invention provides an improved process for the preparation of aromatic polyesters which comprises (i) providing an amorphous poly(arylester) prepolymer containing hydroxyl and ester groups formed by melt polymerizing at least one dialkyl ester of an aromatic dicarboxylic acid with an aromatic bisphenol in presence of a catalyst, (ii) crystallizing the poly(arylester) prepolymer by suspending it in a diluent and heating (preferably at reflux temperature) for a period in the range of for example 2-4 hrs, (iii) separating and drying the crystallized poly(arylester) prepolymer, and (iv) heating the crystallized poly(arylester) prepolymer in such a way that the polymer remains solid, by conventional methods. During the heating step (iv) the poly(arylester) prepolymer undergoes further polymerization in the solid state with an increase in molecular weight. In one of the embodiments of the invention the prepolymer suitable for the process is generally amorphous and has an intrinsic viscosity of approximately 0.20-0.30 dl/g, corresponding to number average molecular weight in the range of 2,800-6,000. In another embodiment of the invention, the poly(arylester) prepolymer can be prepared by melt polycondensation process as described in US-A 5,340,908 by reacting esters of aromatic dicarboxylic acids with aromatic bisphenol(s) in presence of a catalyst. These poly(arylester) prepolymers do not show any crystalline peak either in Differential Scanning Calorimetry (DSC) or X-ray diffraction (XRD) and are hence termed amorphous. The dialkyl esters used may be dimethyl terephthalate, dimethyl isophthalate or mixtures thereof, as well as 2,6-naphthalene dicarboxylic acid esters and alkyl substituted homologues of such dicarboxylic acid esters wherein the alkyl groups contain 1 to 4 carbon atoms. The bisphenol used may be bisphenol-A, halo substituted bisphenol-A, alkyl-substituted bisphenol-A, hydroquinone, resorcinol or various types of other polyphenols. The catalyst employed in step (i) may include alkoxides of Group IVB metals and derivatives of Group IVA metals. The diluents used can be chosen from organic solvents such as ethyl acetate, acetone, toluene or xylene or combinations thereof or the like. The diluent may be any solvent that will promote crystallization but not dissolve the poly(arylester) prepolymer. The heterogeneous mixture of poly(arylester) prepolymer and the diluent is then heated to the respective refluxing temperatures. The optimum temperature and time for crystallization will depend upon the nature of the diluent. Subsequently the diluent is removed by distillation and the product is dried in vacuum at 70-80°C for 3-4 hours. The dried poly(arylester) prepolymers show appreciable crystallinity as observed by the appearance of crystalline melting peaks in DSC in the range of 190-250°C. The catalyst employed in step (ii) may be a dibutyltin diester, tin phenoxide, silicon phenoxide etc. The amount of catalyst employed may be in the range of 0.05 to 0.50 weight percent based on prepolymer. The crystallized poly(arylester) prepolymer may be post-polymerized in step (iv) in solid state at different pressures ranging from atmospheric pressure to sub-atmospheric pressure. Generally 1 atm (760 mm, Hg) is maintained during the initial phase and subsequently the pressure is reduced to 1.0 to 0.1 mm, Hg or even lower. The temperature of the reaction may be in the range of 170-240°C. The heating time may be between 8-15 hours, depending on the molecular weight range desired. Alternatively the crystallized poly(arylester) prepolymer can be heated in a fluidized bed at a temperature below the melting point of the polymer using a hot inert gas for a period of time which is sufficient to achieve an intrinsic viscosity of 0.60 dl/g. The inert gas can be chosen amongst nitrogen, argon, carbon dioxide or helium. The process of the invention is described below by examples which illustrate the invention. EXAMPLE 1 A prepolymer (1 g, having intrinsic velocity [n] = 0.20 dl/g in chloroform at 30°C) was taken in a 100 ml round bottomed flask along with 25 ml ethyl acetate and 5x10 -4 g of dibutyltin dilaurate and refluxed at 80-90°C for 4 hours. Thereafter the ethyl acetate was removed by distillation and the poly(arylester) prepolymer dried in vacuum (1 mm Hg) at 70-80°C. The poly(arylester) prepolymer was mechanically crushed and particles passing through 22 mesh screen were collected. 0.75 g of this poly(arylester) prepolymer were heated to 170°C under nitrogen over a period of 1 hour. Thereafter the pressure was reduced to 1mm Hg and the prepolymer was held at 170°C for 5 hours at the first instance and 2 hours each at 200°C, 220°C and 240°C respectively. Subsequently the poly(arylester) was cooled to room temperature. The resulting poly(arylester) had an intrinsic viscosity [n] of 0.35 dl/g at 30°C in chloroform. EXAMPLE 2 A poly(arylester) prepolymer (1 g, having intrinsic velocity [n] = 0.20 dl/g in chloroform at 30°C) was taken in a 100 ml round bottomed flask along with 25 ml ethyl acetate and 5x10 -4 g of dibutyltin dilaurate and refluxed at 80-90°C for 4 hours. Thereafter the ethyl acetate was removed by distillation and the poly(arylester) prepolymer dried in vacuum (1 mm Hg) at 70-80°C. The poly(arylester) prepolymer was mechanically crushed and particles passing through 22 mesh screen were collected. 0.75 g of poly(arylester) prepolymer was heated to 170°C under nitrogen over a period of 1 hour. Thereafter the pressure was reduced to 1 mm Hg and the prepolymer was held at 170°C for 5 hours at the first instance and 2 hours each at 200°C, 220°C and 240°C. Subsequently the poly(arylester) was cooled to room temperature. The resulting poly(arylester) had an intrinsic viscosity [n] of 0.54 dl/g at 30° chloroform. EXAMPLE 3 A poly(arylester) prepolymer (1 g, having intrinsic velocity [n] = 0.20 dl/g in chloroform at 30°C) was taken in a 100 ml round bottomed flask along with 25 ml acetone and 5x10 -4 g of dibutyltin dilaurate and refluxed at 60-70°C for 4 hours. Thereafter the acetone was removed by distillation and the poly(arylester) prepolymer dried in vacuum (1 mm Hg) at 70-80°C. The poly(arylester) prepolymer was mechanically crushed and particles passing through 22 mesh screen were collected. 0.75 g of this poly(arylester) prepolymer were heated to 170°C under nitrogen over a period of 1 hour. Thereafter the pressure was reduced to 1mm Hg and the poly(arylester) prepolymer was held at 170°C for 5 hours at the first instance and 2 hours each at 180°C, 200°C, 220°C and 240°C. Subsequently the poly(arylester) was cooled to room temperature. The resulting poly(arylester) had an intrinsic viscosity [n] of 0.50 dl/g at 30°C in chloroform. EXAMPLE 4 A poly(arylester) prepolymer (1 g, having intrinsic velocity [n] = 0.30 dl/g in chloroform at 30°C) was taken in a 100 ml round bottomed flask along with 25 ml toluene and 5x10 -4 g of dibutyltin dilaurate and refluxed at 110-120°C for 4 hours. Thereafter the toluene was removed by distillation and the poly(arylester) prepolymer dried in vacuum (1 mm Hg) at 70-80°C. The poly(arylester) prepolymer was mechanically crushed and particles passing through 22 mesh screen were collected. 0.75 g of poly(arylester) prepolymer were heated to 200°C under nitrogen over a period of 1 hour. Thereafter the pressure was reduced to 1mm Hg and the poly(arylester) prepolymer was held at 200° for 5 hours at the first instance and 2 hours each at 220°, 240° and 250°C. Subsequently the poly(arylester) was cooled to room temperature. The resulting poly(arylester) had an intrinsic viscosity [n] of 0.60 dl/g at 30°C in chloroform. EXAMPLE 5 A poly(arylester) prepolymer (1 g, having intrinsic velocity [n] = 0.30 dl/g in chloroform at 30°C) was taken in a 100 ml round bottomed flask along with 25 ml xylene and 5x10 -4 g of dibutyltin dilaurate and refluxed at 140-150°C for 4 hours. Thereafter the xylene was removed by distillation and the poly(arylester) prepolymer dried in vacuum (1 mm Hg) at 70-80°C. The poly(arylester) prepolymer was mechanically crushed and particles passing through 22 mesh screen were collected. 0.75 g of poly(arylester) prepolymer were heated to 200°C under nitrogen over a period of 1 hour. Thereafter the pressure was reduced to 1mm Hg and the poly(arylester) prepolymer was held at 200°C for 5 hours at the first instance and 2 hours each at 220°C, 240°C and 250°C. Subsequently the poly(arylester) was cooled to room temperature. The resulting poly(arylester) had an intrinsic viscosity [n] of 0.55 dl/g at 30°C in chloroform. The main advantages of the invention are: The present process uses the poly(arylester) prepolymer prepared by alcoholysis of aromatic bisphenol(s) by dialkyl esters of aromatic dicarboxylic acid(s). Unlike the poly(arylester) prepolymer prepared by acidolysis of bisphenol(s) diacetate by aromatic dicarboxylic acid(s), the poly (arylester) prepolymer prepared by alcoholysis route is free from residual byproduct as the by-product (methyl alcohol) is a low boiling compound and can be removed efficiently and conveniently. This allows the production of better quality prepolymer. High molecular weight polyesters can be produced by solid state polycondensation of these poly(arylester) prepolymers without any need of operations such as premelting, efficient agitation etc. Aromatic polyester melts have high viscosities and hence cannot be agitated easily to provide uniform heating, and local overheating causes the melt to degrade. On the contrary, solid state polymerization does not require agitation, hence there is no danger of polymer degradation and consequently poly(arylester) with good colour is obtained. Poly(arylester)s of any desired molecular weight can be produced for end applications such as injection molding or extrusion simply by controlling the time temperature profile.

Claims: An improved process for the preparation of aromatic polyesters which comprises (i) providing an amorphous poly(arylester) prepolymer containing hydroxyl and ester groups formed by melt polymerizing at least one dialkyl ester of an aromatic dicarboxylic acid with an aromatic bisphenol in presence of a catalyst, (ii) crystallizing the poly(arylester) prepolymer by suspending it in a diluent and heating at for example reflux temperature for a period in the range of for example 2-4 hours, (iii) separating and drying the crystallized poly(arylester) prepolymer, and (iv) heating the crystallized poly(arylester) prepolymer in such a way that the polymer remains solid, by conventional methods. A process as claimed in claim 1, wherein the catalyst in step (i) is a group IV B metal alkoxide or a group IV A metal or derivative thereof. A process as claimed in claim 1 or claim 2, wherein the diluent in step (ii) is ethyl acetate, acetone, toluene or xylene. A process as claimed in any preceding claim, wherein in step (ii) a catalyst (e.g. a dibutyltin diester) is used in an amount of 0.05 to 0.50 weight % of prepolymer. A process as claimed in any preceding claim, wherein the crystallized poly(arylester) prepolymer is dried under vacuum at a temperature in the range of 70-80°C. A process as claimed in any preceding claim, wherein the crystallized poly(arylester) prepolymer is heated to a temperature in the approximate range of 170-250°C under 1 mm Hg pressure. A process as claimed in any one of claims 1 to 5, wherein the crystallized poly(arylester) prepolymer is heated in a fluidised bed at a temperature below the melting point of the polymer in the presence of an inert gas. A process as claimed in claim 7 wherein the inert gas used in nitrogen, argon, CO 2 or helium.

Inventors: IDAGE BHASKAR BHAIRAVNATH, MAHAJAN SUDHAKAR SADASHIV, SIVARAM SWAMINATHAN, IDAGE, BHASKAR BHAIRAVNATH, MAHAJAN, SUDHAKAR SADASHIV, SIVARAM, SWAMINATHAN
Applicants: COUNCIL SCIENT IND RES, COUNCIL OF SCIENTIFIC AND INDUSTRIAL RESEARCH
Application year: 1996
Main classification: C08G63
IPC codes: C08G63