Synthesis of diamond single crystal from hydrogenated amorphous carbon

Abstract: Hydrogenated amorphous carbon mainly composed of sp 3 structure is prepared by adding hydrogen to carbon or decomposing hydrogenated carbon gas, and then rapidly cooling the mixed or decomposed gas on a substrate. The hydrogenated amorphous carbon is irradiated with X ray to excite electrons on the ls shells of carbon atoms. The carbon atoms are rendered to a state excited with 2 + ion due to Auger effect caused by the excitation, so as to form atomic vacancies and interlattice atomic couples. The hydrogenated amorphous carbon is then annealed, and carbon atoms are rearranged to rotated triangular pattern. Thus, diamond good of crystallinity useful as a high-temperature semiconductor device, ultraviolet laser diode or protect film can be synthesized at a relatively low temperature and a low pressure. The process is applicable for the growth of a diamond single crystal thin film on a single crystal substrate such as amorphous carbon, silicon, a III-V or II-VI compound semiconductor.

Description: The present invention relates to the synthesis of diamond single crystal expected to be used in various techincal fields such as a high-temperature semiconductor device, ultraviolet laser diode or transparent protect single crystal film excellent in hardness. Synthetic diamond has been used as abrasive grains or cutting tools due to its high hardness, and as a heat sink for a laser element due to its excellent thermal conductivity. Since the diamond exhibits big band gap, it is expected to be used as a semiconductor ultraviolet laser or emitting source, too. Recently, the applicability of the diamond has been researched in the fields of optoelectronics, high -temperatue semiconductor devices or the like suitable for high-speed data processing with high-density. According to a conventional method, such synthetic diamond is produced by heating the mixture of graphite with a catalyst in a high-temperature diamond stable zone at a high pressure. The catalyst used in this method is the Group-VIII transition metal or its alloy having the function to melt the graphite in the diamond stable zone and to precipitate diamond particles having small solubility. Synthetic diamond may be produced by synthesizing a quasi-diamond thin film on a substrate from the mixed gas of hydrocarbon with hydrogen or by photodissociating hydrogenated carbon gas to polycrystalline or nanocrystalline thin film. Synthetic diamond obtained in any of the conventional methods contains impurities in fairly large amount, since it is inevitable to inhibit the inclusion of dissimilar components from the atmosphere. The product is of polycrystalline structure or nanocrystalline aggregate, too. Consequently, the obtained synthetic diamond does not satisfy the requirement necessary as the semiconductive or photosemiconductive material which must have crystallinity highly controlled. The object of the present invention is to obtain diamond single crystal excellent in crystallinity by forming atomic vacancies and interlattice atomic couples which effectively induce the kinetic motion of interlattice atoms in hydrogenated amorphous carbon so as to rearrange carbon atoms to rotated triangular pattern at a low temperature. According to the present invention, hydrogenated amorphous carbon mainly composed of sp 3 structure is irradiated with X ray from emitted light to excite electrons on the ls shells of carbon atoms. The carbon atom is rendered to the 2 + ion excited state due to Auger effect caused by the excitation, so as to form atomic vacancies and interlattice atoms in the hydrogenated amorphous carbon. The hydrogenated amorphous carbon is then annealed at a temperature sufficiently lower than its melting point. The annealing promotes the rearrangement of carbon atoms to rotated triangular pattern only by the kinetic energy of the interlattice atoms. The hydrogenated amorphous carbon mainly composed of sp 3 structure is prepared by adding hydrogen to carbon, decomposing hydrogenated carbon gas and rapidly cooling the decomposed gas on a substrate, or sputtering graphite with hydrogen atoms. The synthesis method is applicable to the growth of the thin film of diamond single crystal on a substrate such as amorphous carbon, silicon single crystal or Group III-V or II-VI compound semiconductor. Fig. 1 is a schematic view illustrating a chamber for manufacturing hydrogenated amorphous carbon by decomposition with high-frequecny plasma. Fig. 2 is a graph showing the distribution of cordinations in hydrogenated amorphous carbon. Fig. 3 is a ideal view for explaining the diamond synthesizing process according to the present invention. Fig. 4 is a graph showing the distribution of cordinations in electronically excited hydrogenated amorphous carbon. Fig. 5 is a graph showing the distribution of cordinations in an annealed diamond thin film. Fig. 6 is a spectral atlas showing Raman spectrum (A) of hydrogenated amorphous carbon, Raman spectrum (B) of electronically excited hydrogenated amorphous carbon and Raman spectrum (C) of a diamond thin film obtained in the example. According to the present invention, carbon having sp 2 structure (graphite) is hydorgenated to amorphous carbon having sp 3 structure. The hydrogenation of carbon gas is performed by decomposing the mixed gas of 10-40 at.% hydrogen with 32 at.% benzene, 31 at.% cyclohexane, 28 at.% n-hexane, 30 at.% methane or 40 at.% propane by irradiation with electromagnetic wave of radio frequency in a vacuum chamber. When the hydrogenated carbon gas is decomposed and precipitated on a semiconductor substrate held at 100-350 °C in a sufficient hydrogen atmosphere, hydrogenated amorphous carbon mainly composed of sp 3 structure is formed. When hydrogenated amorphous carbon is irradiated with X ray using emitted light, electrons on the ls shells of carbon atoms are selectively excited so as to effectively render the carbon atoms to excited state due to Auger effect. Since the ls shell of carbon atom is of 284 eV in energy level, monochromatic light (emitted light) at a higher energy level is used as an exciting source. Electrons are discharged to the vacuum atmosphere by the excitation of the 1s shell, 2p electrons are dropped from a valence electron band to the 1s shell so as to fill the resultant electron vacancies, and 2p electrons having momentum reversal to the energy are simultaneously discharged from the valence electron band to the vacuum atmosphere. As a result, carbon atoms in the state ionized to 2 + are excited. Consequently, the movement of carbon atoms is induced with high density, and atomic vacancies and interlattice atomic couples are formed in the hydrogenated amorphous carbon. The atomic vacancy is the trace where carbon atom is discharged, and so lower of approximately 0.5 eV in kinetic energy with which adjacent carbon atom moves to the atomic vacancy that the movement of carbon atoms is promoted by low-temperature annealing at approximately 100-250 °C. The interlattice atom being coupled with the atomic vacancy is as the same lower level of approximately 0.5 eV as that of the atomic vacancy. As a result, the movement of interlattice atoms is facilitated by the low-temperature annealing. The hydrogenated amorphous carbon in which the atomic vacancies and the interlattice atomic couples are formed has four-coordinated structure. When this hydrogenated amorphous carbon is annealed at a relatively lower temperature, the movement of interlattice atoms at a lower energy level is efficiently induced by the atomic hole mechanism. In short, carbon atoms are rearranged to diamond structure only by the kinetic energy of the interlattice atoms, so as to obtain diamond single crystal excellent in crystallinity. The atomic hole mechanism derived from the atomic vacancies and interlattice atomic couples is recognized by computer simulation according to the first principle molecular dynamic process. The process is the calculation method which enables to non-experientially determine the motion of atoms and the state of electrons according to quantum mechanics using atomic numbers as input parameters. The process is suitable for the analysis of reaction or dynamics in a complicated system. Hydrogenated amorphous carbon is reacted with amorphous carbon in a computer according to the first principle molecular dynamic process. The simulation reached the conclusions that the ratio of carbon having four-coordinated sp 3 structure in the hydrogenated amorphous carbon is increased to 80-90%, although three-coordinated sp 2 structure shears 80-90% of amorphous carbon. This result means that an amorphous state locally having structure and hardness similar to diamond is obtained. Two-coordinated dangling bond and five-coordinated floating bond are detected as faults in the hydrogenated amorphous carbon. Expecially in the case of the dangling bond, sp 2 and sp 3 structures are both degenerated, and there are two metastable states. When atomic vacancies are formed by exciting the ls shells of carbon atoms accompanying those faults, electrons are dropped from the 2p valence bands of carbon atoms toward the vacancies in the ls shells, and 2p electrons at the same energy level but the reversal momentum are simultaneously discharged from the valence electron bands to the vacuum atmosphere. Carbon atoms excited to 2 + ion state exist for a several picoseconds, during which carbon atoms accompanying the dangling bonds move in a long distance to form atomic vacancies and interlattice atomic couples. As the result of the simulation test, the kinetic energy of interlattice atoms is of 0.5 eV smaller in one shift as compared with the atomic vacancy forming energy of 5 eV. Consequently, the hydrogenated amorphous carbon is mainly composed of four-coordinated structure, the movement of interlattice atoms at a relatively lower energy level is efficiently promoted by the relatively low -temperature annealing, and carbon atoms are rearranged to diamond structure only by the kinetic energy of the interlattice atoms. EXAMPLE A semiconductor substrate was disposed as a target 2 in a vacuum chamber 1, as shown in Fig. 1. The chamber 1 was held at the vacuum degree of 10 -4 -10 -5 mmHg. Hydrogenated carbon was introduced into the chamber 1 and decomposed with high-frequency plasma. Hydrogenated amorphous carbon 3 was precipitated as the decomposition product on the semiconductor substrate 2. When the hydrogenated amorphous carbon was analyzed by Raman spectrum, four-coordinated structure generated by the hydrogenation was detected together with three-coordinated structure, as shown in Fig. 2. The semiconductor substrate on which the hydrogenated amorphous carbon was deposited was then transferred to a synchrotron light emitting device. The interior of the device was held at the high vacuum degree of 10 -11 mm Hg at an ordinary temperature, and the hydrogenated amorphous carbon was excited by irradiation with SOR light, as shown in Fig. 3. The Raman spectrum analysis of the hydrogenated amorphous carbon after being excited is shown in Fig. 4. It is noted from Fig. 4 that the ratio of carbon atoms having sp 2 structure was increased due to the formation of atomic vacancies. After the exciting treatment, the hydrogenated amorphous carbon was annealed at a relatively low temperature of 300 °C, to obtain a diamond thin film. The Raman spectrum analysis of the obtained diamond thin film is shown in Fig. 5. It is noted from Fig. 5 that the deposit was converted to diamond consisting of sp 3 structure only. The result suggests that the annealing facilitated the movement of atoms through atomic vacancies so as to convert the deposit to a single crystal state, i.e. diamond. The conversion from hydrogenated amorphous carbon to diamond is noted from Raman spectrum shown in Fig. 6, too. That is, the Raman spectrum of the hydrogenated amorphous carbon has two peaks, one of which is at 2800 cm -1 originated in sp 2 structure and the other of which is at 3300 cm -1 originated in four-coordinated sp 3 structure, as shown by the curve (A) in Fig. 6. Raman spectrum after the exciting treatment is shown by the curve (B) , wherein the peak of 2800 cm -1 was higher a little bit, but the curve (B) is not substantially deviated from the curve (A). On the other hand, after the excited hydrogenated amorpous carbon was annealed, only the peak of 3300 cm -1 was detected, but the peak of 2800 cm -1 was diminished as shown by the curve (C). As a result, it is confirmed that the obtained thin film was composed of diamond having four-coordinated sp 3 structure. According to the present invention as aforementioned, atomic vacancies and interlattice atomic couples are formed in hydrogenated amorphous carbon by irradiation with X ray, and the movement of interlattice atoms at a lower energy level is efficiently induced by atomic hole mechanism so as to rearrange atoms in the hydrogenated amorphous carbon to diamond single crystal. Consequently, diamond excellent in crystallinity is synthesized at a relatively lower temperature and a lower pressure. The obtained diamond or diamond thin film is useful as the high-functional material, e.g. semiconductor device, ultraviolet laser diode or transparent single crystal film, which may be reformed to type-n or type-p by proper doping treatment. Especially, the use as a high-temperature device is expected, since the diamond is stable at a high temperature.

Claims: A method of synthesizing diamond single crystal from hydrogenated amorphous carbon, comprising the steps of: preparing hydrogenated amorphous carbon mainly composed of sp 3 structure, irradiating said hydrogenated amorphous carbon with X ray to form atomic vacancies and interlattice atomic couples, and then annealing said hydrogenated amorphous carbon to rearrange carbon atoms to rotated triangular pattern. The method defined by Claim 1, wherein the hydrogenated amorphous carbon is prepared by decomposing and rapidly cooling hydrogenated carbon gas on a substrate. The method defined by Claim 1, wherein the hydrogenated amorphous carbon is prepared by sputtering graphite with hydrogen atoms. The method defined by any of Claims 1 to 3, wherein the irradiated hydrogenated amorphous carbon is annealed at a temperature lower than its melting point. The method defined by any of Claims 1 to 4, wherein the synthesized diamond is grown up as a thin film on a substrate selected from the group consisting of amorphous carbon, silicon and Group III-V or II-VI compound semiconductor.

Inventors: YOSHIDA HIROSHI, YOSHIDA, HIROSHI
Applicants: JAPAN RES DEV CORP, RESEARCH DEVELOPMENT CORPORATION OF JAPAN
Application year: 1996
Main classification: C30B1
IPC codes: B01J19, C30B29, C01B31, C30B1