BLENDED POLYMER GEL ELECTROLYTES

Abstract: An electrolyte system (40) for use in connection with an electrochemical cell (10). The cell (10) includes a positive electrode (20) and a negative electrode (30) with the electrolyte system (40) disposed therebetween. The electrolyte system is a blended polymer gel electrolyte system including a liquid electrolyte species which may be either aqueous or non-aqueous and a blended polymer gel electrolyte support structure. The blended polymer gel electrolyte support structure includes at least a first phase adapted to absorb or otherwise engage the electrolyte active species and a second phase which is substantially inert and does not absorb the electrolyte active species. The second phase may be divided to reduce swelling of the gel electrolyte in the presence of the electrolyte active species, and further to enhance mechanical integrity of the support structure.

Description: BLENDED POLYMER GEL ELECTROLYTES Technical Field This invention relates in general to the field of electrolytes for electrochemical cells, and more particularly to polymer electrolytes for such cells. Background of he Invention There has been a great deal of interest in developing better and more efficient methods for storing energy for applications such as radio communication, satellites, portable computers, and electric vehicles to name but a few. Accordingly, there have been recent concerted efforts to develop high energy, cost effective batteries having improved performance characteristics. Rechargeable, or secondary cells are more desirable than primary (non-rechargeable) cells since the associated chemical reactions which take place at the positive and negative electrodes of the battery are reversible. Electrodes for secondary cells are capable of being regenerated (i.e. recharged) many times by the application of an electrical charge thereto. Numerous advanced electrode systems have been developed for storing electrical charge. Concurrently, much effort has been dedicated to the development of electrolytes capable of enhancing the capabilities of electrochemical cells. Heretofore, electrolytes have been either hquid electrolytes as are found in conventional wet cell batteries, or solid films as are available in newer, more advanced battery systems. Each of these systems have inherent limitations, and related deficiencies which make them unsuitable for various applications. Liquid electrolytes, while demonstrating acceptable ionic conductivity, tend to leak out of the cells into which they are sealed. While better manufacturing techniques have lessened the occurrence of leakage, cells still do leak potentially dangerous liquid electrolytes from time to time. This is particularly true of current lithium ion cells. Moreover, any leakage in the cell lessens the amount of electrolyte available in the cell, thus reducing the effectiveness of the cell. Cells using liquid electrolytes are also not available for all sizes and shapes of batteries. Conversely, solid electrolytes are free from problems of leakage. However, they have vastly inferior properties as compared to liquid electrolytes. For example, conventional solid electrolytes have ionic conductivities in the range of IO" 0" S/cm (Siemens per centimeter). Whereas acceptable ionic conductivity is > 10 ~ 3 S/cm. Good ionic conductivity is necessary to ensure a battery system capable of delivering usable amounts of power for a given application. Good conductivity is necessary for the high rate operation demanded by, for example, cellular telephones and satellites. Accordingly, solid electrolytes are not adequate for many high performance battery systems. While solid electrolytes are intended to replace the combination of liquid electrolytes and separators used in conventional batteries, the limitations described hereinabove have prevented them from being fully implemented. One class of solid electrolytes, specifically gel electrolytes, have shown some promise. Gel electrolytes contain a significant fraction of solvents (or plasticizers) in addition to the salt and polymer of the electrolyte itself. One processing route that can be used to assemble a battery with a gel electrolyte is to leave out the solvent until after the cell is fabricated. The cell may then be immersed in the solvent and a gel is formed as the solvent is absorbed. Two problems, however, may arise during solvent absorption: (1) the gel electrolyte may lack sufficient mechanical integrity to prevent shorting between the electrodes; and/or (2) excessive swelling accompanies the gel formation. Each of these problems is a significant limitation to the successful implementation of gel electrolytes in electrochemical cells. Accordingly, there exists a need for a new electrolyte system which combines the properties of good mechanical integrity, as well as the ability to absorb sufficient amounts of liquid electrolytes so as to produce an electrolyte with the high ionic conductivity of liquid electrolytes. The electrolytes so formed should also avoid excessive swelling, and all the problems associated therewith Brief Description ofthe Drawings FIG. 1 is a schematic representation of an electrochemical cell in accordance with the instant invention; FIG. 2 is a chart illustrating the weight increase in percent for various polymer and polymer blend materials as a function of time; FIG. 3 is a photograph, taken with optical microscopy illustrating the structure ofthe polymer blend electrolyte system support structure in accordance with the instant invention; and FIG. 4 is a chart illustrating a series of charge/discharge curves for an electrochemical cell incorporating a polymer blend support structure in accordance with the instant invention. Detailed Description ofthe Preferred Embodiment While the specification concludes with claims defining the features of the invention that are regarded as novel, it is believed that the invention will be better understood from a consideration of the following description in conjunction with the drawing figures, in which like reference numerals are carried forward. Referring now to FIG. 1, there is illustrated therein a schematic representation of an electrochemical cell in accordance with the instant invention. The cell 10 includes a positive electrode 20 and a negative electrode 30. The positive electrode 20 may be fabricated of any of a number of chemical systems known to those of ordinary skill in the art. Examples of such systems include manganese oxide, nickel oxide, cobalt oxide, vanadium oxide, and combinations thereof. The negative electrode 30 may likewise be fabricated from any of a number of electrode materials known to those of ordinary skill in the art. Selection of the negative electrode material is dependent on the selection of the positive electrode so as to assure an electrochemical cell which will function properly for a given application. In this context, the negative electrode may be fabricated from alkali metals, alkali metal alloys, carbon, graphite, petroleum coke, and combinations thereof. The types of negative and positive electrode materials recited above are typically associated with lithium battery cells. It is to be noted however that the invention is not so limited; the blended polymer electrolyte system of the instant invention may be advantageously employed with nickel-cadmium, nickel-metal hydride, lead-acid, or any other battery system. Operatively disposed between the positive 20 and negative 30 electrodes is an electrolyte system 40. The electrolyte system 40 comprises a polymer blend including at least two polymers adapted to function as a support structure and an electrolyte active species. The electrolyte active species may be either a liquid or solid, and may further include a plasticizer or solvent. Preferably, the electrolyte active species is a liquid electrolyte adapted to promote ion transport between the positive and negative electrodes, which liquid is absorbed into the blended polymer support structure. As noted above, in the fabrication of polymer gel electrolytes, two problems arise during solvent absorption. The first problem relates to the lack of sufficient mechanical integrity to prevent electrical shorting between the electrodes and the second problem relates to excessive swelling which often accompanies the gel formation as the polymer is being immersed in the liquid electrolyte species. The instant polymer blend electrolyte system solves these problems by providing a polymer blend, such as a two phase polymer blend, in which at least one polymer is provided for purposes of absorbing the electrolyte active species, while at least a second polymer, which either does not absorb electrolytes or at best absorbs very little electrolyte, provides mechanical integrity. As the mechanical integrity is improved, shorting between the electrodes is reduced or eliminated. In addition to improving the mechanical integrity of the electrolyte, the second polymeric phase reduces the rate of electrolyte absorption. By slowing the rate of absorption, excessive swelling can be avoided and hence the problems encountered in the prior art devices. It is to be understood that while the system is described above refers to two phases, the invention is not so limited. Indeed, the polymer blend electrolyte system may be a multiphase system in which one or more phases contribute to electrolyte active species absorption, and one or more phases contributes to improved mechanical integrity. The operative distinction however is the presence of discrete phases in a polymer blend, as opposed to the co-polymers common in other polymeric electrolyte systems. The liquid electrolyte absorbed by the support structure is selected to optimize performance of the positive 20 and negative 30 electrode couple. Thus, for lithium type cells the liquid electrolyte absorbed by the support structure is typically a solution of an alkali metal salt, or combination of salts, dissolved in a non-protonic organic solvent or solvents. Typical alkali metal salts include, but are not limited to, salts having the formula M + X" where M+ is an alkali metal cation such as Li + , Na + , K + and combinations thereof; and X" is an anion such as Cl", Br", I", CIO4", BF4", PF6 " , AsF6 " , SbF6 " , CH3CO2-, CF3SO3-, (CF3θ2)2N " (CF3S02)2N", (CF3Sθ2)3C", and combinations thereof. Non-protonic organic solvents include, but are not limited to, propylene carbonate, ethylene carbonate, diethyl carbonate, dimethyl carbonate, dipropyl carbonate, dimethyl sulfoxide, acetonitrile, dimethoxyethane, diethoxyethane, tetrahydrofuran, and combinations thereof. For other electrode combinations, other electrolyte active species are preferred, such as KOH, may be employed. Referring now to FIG. 2, there is illustrated therein a chart describing the weight increase in percent of various polymer gel electrolyte materials versus time. This chart specifically illustrates the differences found for common homopolymers and copolymers versus polymer blends according to the instant invention. Accordingly, as is shown by line 52, a low crystallinity polyvinylidene fluoride (PVDF) homopolymer known as KYNAR®461 (Kynar is a registered trademark of Elf Atochem North America, Inc.) demonstrated extremely high increases in weight with the absorption of liquid electrolytes in a relatively short period of time. Electrolyte absorption is so high as to cause the resulting gel to expand into the electrodes. This expansion lowers conductivity between the electrodes thereby seriously degrading the electrochemical performance of cells into which the electrolyte is incorporated. Line 54 illustrates the absorption properties of a PVDF/polytetrafluoroethylene copolymer (PTFE) known as KYNAR®7201. It may be appreciated from a perusal of FIG. 2, line 54, that lower electrolyte absorption was demonstrated by the PVDF/PTFE copolymer. This lower absorption substantially reduced the problems associated with gel expansion as experienced by the PVDF homopolymer. However, cells constructed from this copolymer experienced short circuiting between the electrodes due to poor mechanical strength of the gel electrolyte. A polymer blend, as opposed to a copolymer, was prepared using a combination of KYNAR® 461 and 18% high density polyethylene (HDPE). The polymer blend so synthesized displayed good mechanical strength and did not absorb excessive electrolyte as maybe appreciated from line 56 of FIG. 2. Electrochemical cells constructed using this polymer blend did not experience shorting during the assembly, and yielded excellent electrochemical performance. It is to be noted that the three examples described in FIG. 2 employed a liquid electrolyte consisting of IM LiPFβ including a solvent or plasticizer consisting of a 50% propylene carbonate, and 50% ethylene carbonate. While FIG. 2 illustrates the use of a polyvinylidene fluoride-HDPE polymer blend, it is contemplated that the concept of using a polymer blend could easily be extended to other gel electrolyte systems, both aqueous and non-aqueous, in order to improve mechanical strength and/or limit the rate of electrolyte absorption. In this regard, the first polymer in the polymer system or the absorbing or gel forming polymer, may be selected from the group of polymers including PVDF, polyurethane, polyethylene oxide, polyacrylonitrile, polymethylmethacrylate, polyacrylamide, polyvinyl acetate, polyvinylpyrrolidinone, polytetraethylene glycol diacrylate, copolymers of any of the foregoing, and combinations thereof. The second component in the polymer blend, i.e., the nonabsorbing or inert component, may be selected from the group consisting of polyethylene, polypropylene, polytetrafluoroethylene, polystyrene, polyethylene terephthalate, ethylene propylene diene monomer, nylon, and combinations thereof. In this regard, it should be noted that at least one polymer phase in the gel polymer electrolyte acts as a separator in the liquid electrolyte cell. The phase which acts as the separator is typically also the phase which provides mechanical stability to the entire electrolyte system. With respect to the relative amounts of each polymer in the blend, it is contemplated that the second or non-absorbing component may comprise between 10 and 40% of the polymer systems, and preferably between 15 and 25%. Referring now to FIG. 3, there is illustrated a photograph of a polymer blend of PVDF and HDPE in accordance with the instant invention. The photograph is taken with optical microscopy in which the image is magnified 50x. As maybe appreciated from FIG. 3, two separate phases of polymers are present in the polymer blend of the instant invention. In FIG. 3, the electrolyte absorbing phase (PVDF) is identified by groupings or areas 80, 82, 84, 86, 88, while the non-absorbing polymer (HDPE) phase is identified by groupings or areas 90, 92, 94, 96, 98. It may thus be appreciated that the polymer system of the instant invention is a two-phase system as opposed to a copolymer such as that typically used in the prior art. The invention may be further appreciated by the comparative ex :amples provided hereinbelow. EXAMPLES Swelling analysis was conducted on a number of homopolymers, copolymers, and polymer blends in accordance with the instant invention. Each of the polymers was swelled in 100°C IM PF6 in a 50%-50% solution of propylene carbonate/ethylene carbonate (PC/EC) solvent. The results are illustrated in the table below: EXAMPLE I Polymer blends were produced using a bench top extruder heated to temperatures between 150 and 200° C. Polymer blend films were produced by hot pressing polymer blends between polished metal plates, at temperatures between 150 and 200° C. Homopolymer films of Kynar 461 and Kynar 761 as described above demonstrated significant uptake of liquid electrolyte active species (IM LiPFβ in a 50%-50% solution of PC/EC), but generally poor mechanical properties and tended to tear easily. Kynar 461 in particular collapsed as the electrolyte active species content exceeded 75%. The PVDF/PTFE copolymer, Kynar 7201, likewise showed poor mechamcal properties. By blending the homopolymer (Kynar 461) with either LDPE or HDPE the electrolyte absorption was reduced; however, mechanical properties were substantially improved. For example, after five minutes the 75:25 Kynar 461/LDPE blend absorbed 42% ofthe electrolyte active species (again IM LiPFβ in a 50%-50% solution of PC/EC), while the 82:18 Kynar 461:HDPE blend absorbed 55% ofthe electrolyte active species. Impedance measurements were carried out for each sample, to determine the ionic conductivies ofthe films. For the 75:25 Kynar 461/LDPE blend, conductivity measured lxl0"4 Siemens per centimeter (S/cm), while conductivity for the 82:18 Kynar 461:HDPE blend was 6xl0" 4 S/cm. The conductivity ofthe 82:18 Kynar 461:HDPE blend is particularly suitable for application in lithium electrochemical cells, as is shown in Example II below. EXAMPLE II To demonstrate the suitability of a blended polymer electrolyte for application in lithium ion cells, a cell was constructed using a petroleum coke anode and a LiCoθ2 cathode. The polymer blend electrolyte system comprised the 82:18 Kynar 461:HDPE blend, soaked in IM LiPFβ in a 50%- 50% solution of PC/EC. The electrodes were prepared by mixing and hot pressing powders with the following compositions: anode: 81% petroleum coke, 19% Kynar 461 cathode: 73% LiCoθ2, 15% graphite, 12% Kynar 461. A cell was formed by laminating the electrodes to the blended polymer. A copper mesh current collector was used for the anode and an aluminum mesh current collector for the cathode. The liquid electrolyte active species was introduced by soaking in the solution at 100°C. The resulting electrode dimensions were 1.8cm x 2.0cm x 130μm. A cell so fabricated was cycled at 1.0 milliamps (mA) between 4.2 and 2.7 volts, with one hour rests between each charge/discharge cycle. Referring now to FIG. 4, there is illustrated therein the charge/discharge profiles for the first ten cycles of the cell fabricated according to this example. As may be appreciated from a perusal of FIG. 4, the cell demonstrated good cell reversibility and overall good cell performance using the blended polymer electrode. While the preferred embodiments of the invention have been illustrated and described, it will be clear that the invention is not so limited. Numerous modifications, changes, variations, substitutions and equivalents will occur to those skilled in the art without departing from the spirit and scope ofthe present invention as defined by the appended claims. What is claimed is:

Claims: Claims 1. A polymer gel electrolyte system for use in an electrochemical cell having positive and negative electrodes, said polymer gel electrolyte system comprising: an electrolyte active species adapted to promote ion transport between said positive and said negative electrodes; and a two-phase polymer blend gel electrolyte support structure including at least a first phase including at least one polymer for absorbing said electrolyte active species and a second phase including at least one polymer for enhancing mechanical integrity of the polymer blend. 2. A gel electrolyte system as in claim 1, wherein said electrolyte active species is a liquid electrolyte which is absorbed by said first phase polymer in said polymer blend support structure. 3. A gel electrolyte system as in claim 1, wherein said first phase polymer is selected from the group consisting of polyvinylidene fluoride (PVDF), polyurethane, polyethylene oxide, polyacrylonitrile, polymethylmethacrylate, polyacrylamide, polyvinyl acetate, polyvinylpyrrolidinone, polytetraethylene glycol diacrylate, copolymers of any of the foregoing, and combinations thereof. 4. A gel electrolyte system as in claim 1, wherein said second phase polymer is selected from the group consisting of polyethylene, polypropylene, polytetrafluoroethylene, polystyrene, polyethyleneterephthalate, ethylene propylene diene monomer, nylon, and combinations thereof. 5. A gel electrolyte system as in claim 2, further including a solvent selected from the group consisting of propylene carbonate, ethylene carbonate, diethyl carbonate, dimethylcarbonate, dipropylcarbonate, dimethylsulfoxide, acetonitrile, dimethoxyethane, tetrahydrofuran, and combinations thereof. 6. A gel electrolyte system as in claim 2, wherein said electrolyte active species includes an alkaline metal salt having the formula M + X", where: M+ is an alkaline metal cation selected from the group consisting of Li+ and Na+, K+; and X" is a anion selected from the group consisting of Cl", Br", I", CIO4", BF4 " , PF6 " , AsFβ " , SbFβ " , CH3CO2-, CF3SO3-, (CF3S02)2N2 " , (CF3Sθ2)3C " , and combinations thereof. 7. A gel electrolyte system as in claim 1, wherein said electrolyte active species is LiPFβ, in a propylene carbonate/ethylene carbonate solvent and wherein said polymer blend includes a first phase consisting of polyvinylidene fluoride and a second phase consisting of polyethylene. 8. A gel electrolyte system as in claim 1, wherein the second phase polymer comprises between 10 and 40% of the two phase polymer support structure. 9. A gel electrolyte system as in claim 1, wherein the second phase polymer comprises between 15 and 25% of the two phase polymer support structure.

Inventors: OLIVER MANUEL P, OLIVER, MANUEL, P.
Applicants: MOTOROLA INC, MOTOROLA INC.
Application year: 1996
Main classification: H01M6
IPC codes: H01M2, H01M6, H01M10