THERMALLY STABLE POLYESTERS FORMED UTILIZING ANTIMONY COMPOUNDS AS CATALYSTS

Abstract: This invention relates to a thermally stable polyester, comprising: a polyester resin prepared by adding a dicarboxylic acid to a glycol compound, said dicarboxylic acid selected from the group consisting of aliphatic dicarboxylic acids having a total of from 3 to 16 carbon atoms, alicyclic dicarboxylic acids having 7 to 12 carbon atoms, aromatic dicarboxylic acids containing a total of from 8 to 16 carbon atoms, and combinations thereof, and wherein said glycol is selected from the group consisting of glycols having from 2 to 12 carbon atoms, glycol ethers having from 4 to 12 carbon atoms, and combinations thereof, said polyester resin having been prepared in the presence of a catalyst system consisting essentially of one or more antimony compounds which is not reacted with alpha -hydroxy carboxylic acids, alpha , beta -dicarboxylic acids or derivatives thereof.

Description: THERMALLY STABLE POLYESTERS FORMED UTILIZING ANTIMONY COMPOUNDS AS CATALYSTS Field of the Invention This invention concerns thermally stable polyester resins prepared in the presence of a catalyst system consisting essentially of an antimony compound without the necessity of stabilizers or other metal catalysts. Background of the Invention Traditionally, the synthesis of polyesters requires the use of catalysts to provide a sufficient rate of reaction to be commercially viable. Often, however, the catalysts that encourage the forward polymerization reaction also enhance the rates of degradation reactions. These degradation reactions can result in both an increase in color and a decrease in molecular weight. To minimize these unfavorable side reactions, stabilizing agents such as phosphorus compounds are traditionally added to the reaction mixture. It is believed in the art that such a stabilizer is needed to prepare a material with acceptable color and thermal stability. For example, a common commercial catalyst in the synthesis of polyesters is titanium. Titanium is an extremely active catalyst and requires the addition of phosphorus compounds to provide acceptable thermal stability as well as improve the color. Antimony is also known as a catalyst in the synthesis of polyesters. Although antimony is a less active catalyst than titanium, the art teaches the addition of phosphorus compounds to provide acceptable thermal stability as well as to improve the color. In the production of commercial polyesters, even when phosphorus is added, the polymer formed is typically unacceptably yellow in color. This yellow color is often toned out using bluing agents, such as cobalt compounds, to make it acceptably neutral in color for commercial applications. Cobalt compounds, besides being bluing agents, are also known to* possess catalytic activity for polyester polymerization and degradation reactions. Therefore, the use of cobalt compunds requires an increase in the amount of the phosphorus compound utilized. Although the art teaches that phosphorus compounds are necessary, they are often relatively expensive, require additional capital equipment for their addition to a typical commercial continuous polycondensation reactor, as well as, in some cases, increase the level of particulate haze in the prepared polyester. In fact, United States Patent 3,028,366 to Engle et al. teaches that it is necessary to add a pentavalent phosphorus compound to the polymerization reaction to prevent a discolored polymer. Also, Kamatani et al, (Polymer Journal, Volume 12, No. 2, pp 125 - 130) discloses the stabilizing effect of phosphoric acid on the polymerization of poly(ethylene terephthalate) by Sb(III) compounds. Several other patents teach the necessity of a phosphorus stabilizer in polyester synthesis for the purpose of obtaining acceptable color and thermal stability. These patents include United States Patents 4,501,878 to Adams, 3,567,799 to Prevorsek, 5,017,680 to Sublett, 4,499,226 to Massey, and 3,441,540 to Muller et al. United States Patent 3,651,016 to Hrach et al. relates to the synthesis of polyesters in the absence of a phosphorus stabilizer. However, this patent teaches the method of using metal alloys as catalysts. United States Patent No. 3,732,182 to Chimura et al. relates to the synthesis of novel antimony compounds that do not undergo an undesirable reduction reaction. This article is not pertinent in that it reacts traditional antimony compounds with α-hydroxycarboxylic acid,— a , β— icarboxylic acid or certain derivatives thereof to formulate allegedly novel antimony compounds. United States Patent No. 4,499,226 to Massey et al. relates to high clarity, colorless, antimony catalyzed polyesters based on terephthalic acid reacted with polyhydric alcohols. This article also requires a stabilizer to prevent color and degradation side reactions. This article also discloses cobalt as a bluing agent. At present, in order to improve the apparent whiteness of polyester fibers or neutral color characteristics of polyester plastics, toners can be incorporated into the polyester to mask or neutralize the yellow color. Cobalt acetate is one of the most widely used toners in the industry to mask the yellow color of polymers. However, cobalt acetate has a number of noteworthy disadvantages. For example, cobalt acetate toned materials tend to be unstable during storage and are particularly susceptible to temperature and humidity, and tend to undergo an undesirable color shift toward yellow. Further, when high cobalt concentrations are needed to mask the yellow color of some polymers there is a tendency to impart a gray color to the polymer. Another disadvantage in the use of cobalt acetate is the limitation set by various governmental agencies in the level of cobalt deemed allowable in polyester catalyst systems. Further, cobalt has a strong tendency to form insoluble residues in manufacturing process equipment, thereby leading to production problems. Lastly, cobalt salts tend to lower the resulting polymer's thermal stability and to increase acetaldehyde formation in poly(ethylene terephthalate) . United States Patent No. 2,641,592 discloses polyesters containing dimethyl terephthalate with cobalt acetate and antimony. United States Patent No. 4,745,174, discloses certain 1—cyano—3H—dibenz [f, ij ] iεoquinoline-2 , 7—diones which are useful as organic toners for polyester fibers and plastics and which solve many of the aforementioned problems. These compounds, however, are expensive to manufacture and provide environmental, safety, and provide toxicological concerns relative to their manufacture and use. United States Patent 4,403,092 discloses colorants useful in the practice of this invention. However, no mention is made in the patent regarding the potential utility of the disclosed compounds as components to produce a good toner system for the polyesters of the invention. Certain organic toner dyes have been disclosed in United States Patents 5,372,864; 5,384,377; and 4,745,174. One or more of these patents disclose the use of certain organic toner dyes for use in polyesters generally. No mention was made of a system comprising essentially antimony. For these reasons, a polyester without the addition of stabilizing phosphorus compounds could be particularly advantageous if they could be prepared with equivalent or improved thermal stability and color. Summary of the Invention This invention relates to a thermally stable polyester resin having been prepared in the presence of a catalyst system, consisting essentially of an antimony compound wherein the polyester resin is prepared by adding a dicarboxylic acid to a glycol compound. A thermal stabilizer is not necessary in the preparation of this polyester. More particularly, this invention relates to a thermally stable polyester, comprising a polyester resin, the polyester resin made by adding a dicarboxylic acid to a glycol compound, the carboxylic acid selected from the group consisting of aliphatic dicarboxylic acids having a total of from 3 to 16 carbon atoms, alicyclic dicarboxylic acids having 7 to 12 carbon atoms, aromatic dicarboxylic acids containing a total of from 8 to 16 carbon atoms, and combinations thereof, and wherein the glycol is selected from the group consisting of glycolε having from 2 to 12 carbon atoms, glycol ethers having from 4 to 12 carbon atoms, and combinations thereof, where the polyester resin has been prepared in the presence of a catalyst system consisting essentially of an antimony compound. Further, this invention relates to a method for imparting good thermal stability to polyesters without the need for stabilizers by employing the catalyst system described above. This invention even further relates to the use of organic dyes in the polyester compositions and in the methods of the present invention. This invention provides the advantages of good thermal stability without the need for stabilizers. It also provides this improved thermal stability in combination with good color for the polyesters described. Detailed Description of the Invention This invention relates to a thermally stable polyester, comprising a polyester resin where the polyester resin is prepared by adding a dicarboxylic acid to a glycol compound in the presence of a catalyst system consisting essentially of an antimony compound. By the term "consisting essentially of", it is meant that other compounds including thermal stabilizers may be used, but not in catalytic amounts. By "catalytic amounts", it is meant that the antimony compound must be present in an amount of about 5 pp to 400 ppm, more preferably, from about 5 ppm to 300 ppm, even more preferably, 165 to 250 ppm, and even more preferably, 175 to 200 ppm. Other compounds besides the antimony compounds may be present in non—catalytic amounts, such as from 0.1 to to 5 ppm in the polyester compositions of the invention. The term "consisting essentially of antimony" specifically excludes phosphorus— ased stabilizers except in non—catalytic amounts. Examples of phosphorus—based stabilizers are phosphorus, phosphates, phosphites, phosphoric acid and phosphoniteε. The term "consisting essentially of antimony" also specifically excludes compounds of titanium, zinc, cobalt, manganese, nickel, germanium and magnesium except in non—catalytic amounts. By the term "catalyst system", we mean compounds used in the process of making the polyester which possess any degree of catalytic activity. The polyesters referred to herein include thermoplastic, crystalline or amorphous polyesters produced by conventional polymerization techniques from one or more diols and one or more dicarboxylic acids. The polyesters normally are molding or fiber grade and have an inherent viscosity (I.V.) of about 0.4 to about 1.2 (dL/g) measured at 25°C in a 60/40 ratio by weight of phenol/tetrachloroethane. The dicarboxylic acid may be selected from the group consisting of aliphatic dicarboxylic acids having a total of from 3 to 16 carbon atoms, alicyclic dicarboxylic acids having 7 to 12 carbon atoms, aromatic dicarboxylic acids containing a total of from 8 to 16 carbon atoms, and combinations thereof. The glycol may be selected from the group consisting of glycols having from 2 to 12 carbon atoms, glycol ethers having from 4 to 12 carbon atoms, and combinations thereof. The term "aliphatic—dicarboxylic acid" is used to denote straight or branched chain alkanedicarboxylic acids containing 3 to 16 carbons. Typical aliphatic dicarboxylic acid include succinic acid, glutaric acid, adipic acid, sebacic acid, suberic, 2,2,4— trimethyladipic, 1, 12—dodecanedioic acid and the like. The term "alicyclic dicarboxylic acid" is used to denote cycloalkane dicarboxylic acids which contain a total of 7 to 12 carbon atoms preferably 1,2-, 1,3- and 1, 4—cyclohexanedicarboxylic acids. The term "aromatic dicarboxylic acid" is used to denote dicarboxylic acid derivatives of benzene, naphthalene, biphenyl, diphenylether, diphenylsulfone and these substitutes with C 1 — C 4 alkyl or halogen (fluorine, chlorine, bromine or iodine) . Typical aromatic dicarboxylic acids, include terephthalic acid, isophthalic acid, phthalic acid, 1, 4—naphthalene dicarboxylic acid, 2, 6—naphthalenedicarboxylic, 4,4'- biphenyldicarboxylic acid, 2—bromoterephalic acid, 2,5- dibromoterephthalic acid, tetrachlorophthalic acid and the like. Terephthalic acid, isophthalic acid and 2,6- naphthalenedicarboxylic acid are the preferred aromatic dicarboxylic acids. Suitable diol components of the described poly¬ esters may be selected from ethylene glycol, 1,4— cyclohexanedimethanol, 1, 2—propanediol , 1, 3—propanediol , 1, 4—butanediol, 2, 2—dimethyl—1, 3-propanediol, 1,6- hexanediol, 1, 2—cyclohexanediol, 1,4—cyclohexanediol, 1, 2—cyclohexanedimethanol, 1, 3—cyclohexanedimethanol, Z, 8-biε(hydroxymethyl)-tricyclo-[5.2.1.0]—decane wherein Z represents 3, 4, or 5; and diols containing one or more oxygen atoms in the chain, e.g., diethylene glycol, triethylene glycol, dipropylene glycol, tripropylene glycol and the like. In general, these diols contain 2 to 18, preferably 2 to 8 carbon atoms. Cycloaliphatic diols can be employed in their cis or tranε configura¬ tion or aε mixtures of both forms. Preferred polyesters comprise at least about 50 mole percent terephthalic acid residues and at least about 50 mole percent ethylene glycol and/or 1,4— cyclohexanedimethanol residues. Particularly preferred polyeεters are those containing from about 75 to 100 mole percent terephthalic acid residues and from about 65 to 100 mole percent ethylene glycol residues. More particularly, preferred polyesters are those containing from about 90 to 100 mole percent terephthalic acid residues and from about 85 to 100 mole percent, preferably 90 to 100 mole percent ethylene glycol residues. Also, particular preferred polyesters are those containing from about 90 to 100 mole percent terephthalic acid and 65 to 75 mole percent ethylene glycol. The polyesterε from thiε invention are necessarily made from the dicarboxylic acids themselves, not the equivalents to these dicarboxylic acids. For inεtance, polyesters made from diesters such as di ethylterephthalate do not form any part of the present invention. The polyesters may be prepared according to polyester forming conditions well known in the art. For example, a mixture of one or more dicarboxylic acids, preferably aromatic dicarboxylic acids, and one or more diols may be heated in the presence of esterification and/or polyesterification catalysts at temperatures in the range of about 150° to about 300°C, and pressures of atmospheric to about 0.2 mm Hg. Normally, the dicarboxylic acid iε eεterified with the diol(ε) at about to 10 to 110 pεi, preferably 20 to 60 pεi above atmospheric pressure and at a temperature at the lower end of the specified range. Polycondensation then is effected by increasing the temperature and lowering the preεεure while excess diol is removed from the mixture. A preferred temperature range for a polyester condensation is about 225°C to about 300°C. It is preferred in the caεes of polyester containing greater than 5 mole % 1,4— cyclohexanedimethanol, based on the glycol components being present at a total of 100 mole percent, that the polycondensation reaction time iε leεε than 8 hours, preferably less than 4.0 hours and more preferably less than 3.0 hours. In a preferred embodiment, organic dyes are useful in the polyesters of the invention. Preferred dyes are ones falling within the classes of anthraquinones and anthrapyridones. When the dyes of the invention are used as toners, this means that it is used in an amount sufficient to improve the apparent whiteness of the polyester. This amount is generally from about 0.1 to 10 ppm. These dyes can also uεed in an amount sufficient to impart a substantial amount of color to the polyester. If color is intended to be imparted to the polyester, the dye should be present in an amount greater than io ppm. Typical organic toner dyeε which are useful in the practice of this invention are those disclosed in U.S. Patents 5,372,864; 5,384,377; and 4,745,174. Particularly preferred dyes are oneε deεcribed in United States Patent 5,384,377, incorporated herein by reference. These preferred dyes are certain blue substituted 1, —bis(2, 6—dialkylanilino) anthraguinoneε in combination with selected red anthraquinone and anthrapyridone (3H—dibenz [fi, j ] isoquinoline—2 , 7—dione) compounds. These dyes which provide a toner system useful in imparting a desirable neutral to slightly blue hue to polyesters having a yellow appearance. The thermally εtable colored compoundε have reactive groups and can be incorporated into the polyester polymer structure during polymerization. In this preferred embodiment, a major portion of at least one 1,4—bis (2 , 6-dialkylanilino) anthraquinone (s) of formula (I) is used: ( I wherein : R is selected from the group consisting of hydrogen, C j —C 6 alkyl, halogen, carboxy, and C α —C 6 5 alkoxy—C-; R λ and R 2 are independently C 1 -C 6 -alkyl ; R 3 is selected from the group consisting of 10 hydrogen, halogen, C 1 -C 6 -alkyl, substituted C χ -C 6 alkyl, hydroxy, C —C 6 —alkoxy, substituted C χ —C 6 —alkoxy, cyano, thiocyano^^C 6 -alkylthio, substituted C —C 6 —alkylthio, C —C 6 —alkylsulfonyl, substituted C —C 6 —alkylsulfonyl, C 1 —C 6 —alkoxycarbonyl, carboxy, aryloxy, arylthio, aryl- 15 sulfonyl, and S0 2 N(R 4 )R 5 X when m and/or n are zero; R 4 iε εelected from the group consisting of hydrogen, C^C g —alkyl, substituted C^—Cg—alkyl, C 3 -C 8 -alkenyl , C 3 -C 8 -alkynyl , C 3 -C 7 -cycloalkyl and aryl; R 5 is a linking " group selected from the group 20 consisting of C^C g —alkylene, C-_—C 6 —alkylene—Z—C 1 —C 6 - alkylene, ar 1ene-C-^C 8 -alkylene, arylene-Z-C 1 -C 6 - alkylene, C 3 -c 7 -cycloalkylene, C 1 -C 6 -alkylene—cyclo- alkylene—C 1 —C g —alkylene, 0 —C 6 —alkylene—arylene—C —C 6 — alkylene, and C 1 -C 6 —alkylene-Z-arylene—Z—C 1 —C 6 —alkylene, 25 wherein Z iε εelected from —0—, —S- or S0 2 ; X iε hydrogen or a polyeεter reactive group; and m and n are independently 0 or 1; with the proviso that at least one polyester reactive group is present. The red components which may be blended with blue 30 components of formula I above have the following I I III IV V VI R ' VII VIII IX wherein: R 6 is selected from the group consisting of hydrogen, C j —C g —alkyl, subεtituted C j —C g —alkyl, C 3 —C 7 —cycloalkyl or aryl; R 7 is hydrogen or one to three groups εelected from C j -C 8 —alkyl, substituted C λ —C 6 alkyl, C j —C 6 - alkanoylamino, halogen, hydroxy, C- j^ —C g —alkyl C- j —c 6 — alkoxy, C j -C 8 -alkylthio; R 8 and R 9 are the same or different and are selected from the group consisting of C 2 —C 6 —alkyl, substituted C j —C g —alkyl, C 3 —C 7 —cycloalkyl or aryl; R 10 is selected from the group consisting of C j -C 8 -alkyl, C 3 -C 7 -cycloalkyl or aryl; R ια is selected from the group consisting of hydrogen, C 1 -C 12 -alkyl, substituted C^C^—alkyl, C 3 —C 7 —cycloalkyl and aryl; R 12 is hydrogen or one to three groupε selected from the group consisting of C j —Cg—alkyl, substituted C j —C g —alkyl, C 2 —C 6 —alkoxy, substituted C χ —C 6 -alkoxy, C 2 —C g —alkylthio, substituted C —C 6 —alkylthio, halogen, hydroxy, C j —C 6 —alkanoylamino, aroylamino, C j —C 6 —alkyl— sulfonylamino and arylsulfonylamino; R 13 and R 14 are εelected from hydrogen, cyano or C0 2 R 10 i R 15 iε R 4 or R 5 X aε previously defined; L is —CO— or —S0 2 —; X is aε previouεly defined; m is 0 or 1; p iε 1 or 2; with the provisos that R 13 is hydrogen when m iε 0 and at least one polyester reactive group iε present. The term "polyester reactive group" is used herein to describe a group which iε reactive with at leaεt one of the functional groupε from which the polyester is prepared under polyester forming conditions. Examples of the groups which X may represent include hydroxy, carboxy, an ester group, amino, C- j —C g —alkylamino, etc. The ester radicals may be any radical having the formula -* >? C -- ■R R1,6- ' ' ° r -°-«H-R 16 wherein R 16 is selected from the group consisting of C j -C 8 -alkyl, substituted C^ ^ -C 8 -alkyl, C 3 -C 7 -cycloalkyl or aryl. Reactive group X is preferably hydroxy, carboxy, C j —C 2 —alkoxycarbonyl or acetoxy. In the terms "substituted C 2 —C 6 —alkyl" , "substituted C 1 -C 12 -alkyl" , "substituted C j -C 8 -alkoxy" , "substituted C j -Cg-alkylthio" , "substituted C 2 -C 6 - alkylsulfonyl" , "C 1 -C 6 -alkylsulfonylamido" , "εubstituted alkylene", "C —C 6 -alkoxycarbonyl", the alkyl and alkylene groups or portions of the groups may contain as further substituents one or more groups, preferably one to three groups εelected from the group consisting of hydroxy, halogen, cyano, aryl, aryloxy, arylthio, C^C 4 —alkylthio, C 2 —C 4 —alkylthio, C 3 —C 7 —cycloalkyl, C 1 -C 4 -alkanoyloxy and -(-0-R 17 -) p -R 18 , wherein R 17 is selected from the group conεiεting of c χ —c 6 —alkylene, C 1 —C g —alkylenearylene, cyclohexylene, arylene, and C±—C g —alkylenecyclohexylene; R 18 is selected from the group consisting of hydrogen, hydroxy, carboxy, C 2 -c 4 - alkanoyloxy, C —C^—alkoxycarbonyl, aryl, and C 3 —C 7 — cycloalkyl; and p is 1, 2, 3, or 4. The term "aryl" as used herein preferably denotes phenyl and phenyl εubεtituted with one to three substituents selected from the group consisting of C 1 —C g —alkyl, C } —C 6 -alkoxy, halogen, carboxy, cyano, C α —C 6 —alkylthio, C : —C 6 -alkylsulfonyl, trifluoromethyl, hydroxy, C j —C 6 —alkanoyloxy, C χ —C 6 —alkanoylamino, and C 1 —C g —alkoxycarbonyl. The term "arylene" includeε 1,2—,1,3— and 1, 4—phenylene and such radicals subεtituted one to three timeε with C χ —C 6 -alkyl, C 1 —C 6 —alkoxy, C 1 —C 6 —alkoxy- carbonyl, or halogen. The termε "C 3 -C 8 -alkenyl" and "C 3 -C 8 -alkynyl" are used to denote aliphatic hydrocarbon moieties having 3-8 carbonε and containing at least one carbon—carbon double bond and one carbon—carbon triple bond, reεpectively. The term "halogen" iε used to indicate bromine, chlorine, fluorine, and iodine. The terms "C j -Cg-alkanoyloxy" and "C 1 -C 6 -alkanoyl- amino" are used to represent radicals of the formula R 19 -e-o- and R —C-N(R )- , reεpectively, wherein R 19 iε a εtraight or branched chain C } —C 6 -alkyl radical and R 6 iε as defined above. Thus, the preεent invention provides a polyester suitable for molding, extrusion, packaging, and fibers having copoly erized therein a blue 1,4—bis(2 , 6—dialkylanilino) anthraquinone compounds of Formula (I) plus a red anthraquinone or anthrapyridone compounds of formula (II) - (X) above. Preferred are blends having at least one blue 1,4-biε(2 , 6—dialkyl¬ anilino) anthraquinone compound of formula (I) , along with a red anthraquinone or anthrapyridone compound of formulae (II) — (X) above. The composition may be a neat blend of the red and blue compounds or the composition may be pre—diεsolved in one of the poly- ester's monomeric εpecieε, e.g., ethylene glycol. The total amount of toner componentε added depends, of course, on the amount of inherent yellow color in the polyester. Generally, a maximum concentration of about 10 ppm of combined toner components and a minimum concentration of about 0.5 ppm are required with about 1 - 7 ppm of blue component (I) in combination with about 0.5 — 3 ppm of red components of formulae (II - X) being preferred. In a preferred embodiment of the present invention, the blue anthraquinone compound correspondε to εtructure (I) above, wherein R iε hydrogen; R 2 and R 2 are independently selected from methyl and ethyl; R 3 is hydrogen, methyl, or bromo; R 4 is hydrogen, C 1 -C 4 -alkyl or aryl; R 5 is εelected from the group consisting of C 1 -C 6 -alkylene, C 1 —C 4 —alkylene-0-C 1 -C 4 —alkylene, -CH 2 C 6 H :0 CH 2 -, arylene, or -CH 2 —arylene- and the red component corresponds to formula (V) , wherein R 7 is C j —Cg—alkoxy and R 4 and R 5 are as defined above for the preferred blue component (I) . In an especially preferred embodiment of the present invention, the blue compound of formula (I) is and the red compound of formula (V) is The blue anthraquinones of formula (I) can be prepared in general by reaction of leuco quinizarin (1, , 9 , 10—tetrahydroxyanthracene) compounds with an excess aromatic amines, preferably in the presence of acid catalysts such as boric acid as deεcribed m U.S Patent No. 3,918,976, incorporated herein by reference and as follows: (I) The 1, 4—bis(2 ,6—dialkylanilino) anthraquinone compounds thus produced are readily functionalized if needed by first chlorosulfonating with chlorosulfonic acid to produce di—εulfonyl chlorides which can be reacted with amines containing polyester reactive groupε, the general method being diεcloεed in U.S. Patent No. 2,731,476, incorporated herein by reference. Typical amines correεponding to formula HN(R 4 )R 5 X include 2-aminoethanol , 2 , 2—i inodiethanol , 1—amino-2,3- propandiol, 2—methyla inoethanol , 2-ethylaminoethanol , 2—anilinoethanol, methyl anthranilate, methyl m-amino benzoate, p—aminobenzoic acid, m—aminophenol, 6—amino- hexanoic acid, β—alanine, glycine ethyl ester, 2—(p—a inophenyl) ethanol, 2—(p—aminophenoxy)ethanol 4—aminomethylcyclohexanemethanol and 3—amino—2,2— dimethyl—1—propanol. Red compounds (II) can be prepared by reacting 1, 5—dichloroanthraquinone and/or 1,8—dichloro— anthraquinone or mixtures thereof with o, - and p—aminobenzoic acids (and esters thereof) by a modified Ullmann reaction involving nitrogen arylation of the anilines in the preεence of copper catalysts (see U.S. Patent No. 4,359,580, incorporated herein by reference) . Red compounds of formula (III) can be prepared as deεcribed in U.S. Patent No. 4,420,581 and compounds of formula (VI) can be prepared aε in U.S. Patent No. 4,999,418, incorporated herein by reference. Red anthraquinone compoundε of formula (IV) can be prepared by reacting 1, 5— ichloroanthraquinone and l, 8—dichloroanthraquinone or mixtures thereof with substituted benzyl amines by procedures similar to those used in preparing compounds of formulae (III) and (VI) . Red anthrapyridone compoundε (VII) can be prepared aε diεcloεed in U.S. Patent No. 4,790,581 incorporated herein by reference; procedureε uεeful in preparing red- violet anthrapyridone compounds (VIII) and (IX) are disclosed in U.S. Patent No. 4,745,174, incorporated herein by reference. The organic dyeε useful in the polyester compoεitionε of the present invention can be added before or during polymerization. The antimony compounds utilized in the present invention can be generally any trivalent organic antimony compound known to the art. The antimony compounds uεeful in the present invention do not include compounds further reacted with α-hydroxycarboxylic acid or derivatives thereof and/or α, β—dicarboxylic acid or derivatives thereof. Examples of antimony compounds uεeful in the context of the invention include, but are not limited to the following: tributyl antimony oxide, KSb(0H) 6 , NH 4 SbF 6 and SBS 3 , antimonate esters of inorganic acids, cyclic alkyl antimonate esters and aryl anti onic acid compounds such as potassium antimony, antimony oxide, antimony trioxide, antimony alkoxide, εuch aε antimony iεopropoxide, antimony halide, εuch aε antimony chloride, antimony bromide, and antimony fluoride, antimony sulfide, sodium or potassium antimonate, antimony carboxylate such aε antimony acetate, antimony glycolate and the like. Examples of preferred antimony compounds are: antimony carboxylate, eεpecially antimony triacetate, antimony oxide, antimony trioxide, antimony glycolate (either formed εeparately or during polymerization) , and the like. The antimony compound deεirably iε added to the condenεation stage or step of the polymerization. Examples of α—hydroxycarboxylic acids which are reacted with antimony compounds to form products which are not included within the scope of the invention are ones containing 2 to 30 carbon atomε. For example, glycolic acid, lactic acid, a— hydroxystearic acid and α—hydroxyisobutyric acid. But, those which have either a total of at leaεt three hydroxyl and carboxyl groupε or at least one aromatic ring in the —position in relation to the carboxyl group, are particularly preferred in the present invention. Preferable α—hydroxycarboxylic acids include, for example, malic acid, —methylmalic acid, citric acid, tartaric acid, α-methyltartaric acid, α- hydroxy-α'—methylεuccinic acid, a— ydroxyglutaric acid, glyceric acid, α, β—dihydroxyisobυtyric acid, dihydroxyfu aric acid, gluconic acid, tartronic acid, benzilic acid, α-phenyllactic acid and mixtures thereof. Examples of a , β—dicarboxylic acids which are reacted with antimony compounds to form products which are not included within the εcope of the invention are thoεe having 4 to 30 carbon atomε which are selected from the compounds represented by the following formulae and their functional derivatives. wherein R l t R 2 , R 3 , and R 4 are identical with or different from each other and selected from a hydrogen atom and unsubstituted or subεtituted alkyl, cycloalkyl, aryl, aralkyl, allyl and alkoxyl groups, εaid substituted groups having a substituent selected from carbonyl group, halogen and carboxyl groups; W, X, Y and Z are identical with or different from each other and selected from a hydrogen atom and alkyl, hydroxyl and carboxyl groups; and n iε an integer of at leaεt l. Such α, β—dicarboxylic acidε include, for example, maleic acid, dimethylmaleic acid, phenyl aleic acid, fumaric acid, εuccinic acid, methylsuccinic acid, 2— methyl—3—ethylεuccinic acid, tetramethylsuccinic acid, tetra ethylsuccinic acid, phenylsuccinic acid, cyclohexylεuccinic acid, ethoxysuccinic acid, itaconic acid, cyclopropane-1, 2—dicarboxylic acid, 1— phenylcyclopropane—2 , 3—dicarboxylic acid, cyclobutane— 1, 2—dicarboxylic acid, 1, 2— imethylcyclobutane— 3 , 4 ,dicarboxylic acid, cyclopentane—1, 2—dicarboxylic acid, cyclohexane-1, 2—dicarboxylic acid, oxalacetic acid, phthalic acid, 3—methylphthalic acid, 4,5— di ethylphthalic acid, 4—hydrophthalic acid, trimellitic acid, 1—butene-2 , 3 ,4—tricarboxylic acid, pyromellitic acid and mixtureε thereof. The preferred organic toner dyes are selected from the classes of anthraquinones and anthrapyridones which are thermally stable at the reactor temperatures used to produce the polyeεterε. Thiε invention iε not limited to the dyeε εpecifically described in theεe patentε, however. The levelε of dyes present in the invention may vary depending on the extinction coefficient of the particular compound as well as the amount of color generated under the polymerization conditions. The polyester compositions of the invention may contain other additives such as branching agentε and chain extenεion agentε, free radical εtabilizerε εuch as hindered phenolε, flame retardantε, toughenerε, epoxy compoundε, mold release agentε, nucleating agents, and other colorants which may alεo be deεirable in εuch formulations. Such additives are generally present at 0.1 to about 20 weight % baεed on the total weight of εaid polyeεter composition. Useful flame retardantε, include, but are not limited to, brominated polystyrene combined with sodium antimonate. Examples of reinforcing agents used in combination with the polyesters of its invention include are glass fibers, carbon fibers, mica, clay, talc, wollastonite, and calcium carbonate. A particularly preferred reinforcing agent is glass fiber. It is preferable that the glass fibers be present in the polyester composition at from 0.1 to 40 %, preferably 0.1 to 30 %, by weight based on the total weight of said polyester composition. Glasε fibers suitable for use in compositionε containing the polyesters of the invention may be in the form of glaεs filaments, threads, fibers, or whiskers, etc. , and may vary in length from about 1/8 inch to about 2 inches. Chopped glasε strands having a length of about 1/8 inch to about 1/4 inch are preferred. Such glass fibers are well known in the art. Of course, the size of theεe glaεs fibers may be greatly diminished depending on the blending means employed, even to lengths of 300 to 700 microns or lower. The polyester compositions of the invention may be reinforced with a mixture of glasε and other reinforcing agents as described above, such aε mica or talc, and/or with other additives. This invention can be further illustrated by the following examples of preferred embodiments thereof, although it will be understood that these examples are included merely for purposes of illustration and are not intended to limit the εcope of the invention unleεε otherwise specifically indicated. The starting materials are commercially available unleεs otherwise indicated. EXAMPLES The poly(ethylene terephthalate) and poly(ethylene terephthalate—co—1, 4—cyclohexanedimethylene terephthalate) polyesters described in Tables 1 and 2 were prepared by standard melt polymerization techniques known to the art. Terephthalic acid, ethylene glycol and 1,4—cyclohexanedimethanol (CHDM) were first pre- esterified to form the bis (2—hydroxyethyl) terephthalate or the equivalent CHDM co—terephthalate monomers in a presεurized vessel. This was required due to the high temperature necessary to disεolve terephthalic acid in the polyhydric alcohols. However, this should not be limited to such a procedure, as a continuous process, or any other polyester synthesis based on TPA (terephthalic acid) known the art, could also be used. Once formed, the monomers were added to a 4—necked 500 mL round bottom glaεε flask which was equipped with a nitrogen inlet, an additive inlet, a condenεate outlet and a εtirrer. Catalysts, εtabilizerε and toner dyeε, aε indicated in Table 1, were also added to thiε same reaction vessel. The reaction flask was then purged with nitrogen and then immerεed in a metal bath which waε preheated to 225°C. The mixture waε εtirred and held at thiε temperature for 15 minuteε to form a homogeneouε melt. The temperature waε then raiεed to 280°C and vacuum waε applied incrementally until a vacuum of < 1 mm Hg waε obtained. The reaction mixture waε εtirred and maintained under these conditions for 45 minuteε. The formed polyeεter waε then iεolated, and analyzed for color, molecular weight, and thermal stability. Inherent viscosity was measured to evaluate molecular weight and was determined at 25°C uεing 0.5 gram of polymer per 100 L of a solvent compoεed of 60 wt% phenol and 40 wt% tetrachloroethane. The color valueε L*, a* and b* were determined using a Hunter Lab Ultraεcan Spectra Colorimeter manufactured by Hunter Associates Lab Inc. , Reston, VA. The colors determinationε were taken at random locations on the sample and averaged. They were determined by the L*a*b* color system of the CIE (International Commission on Illumination) (translated) . The thermal εtability is assessed by an evaluation of the degradation rate constant (K d ) as evaluated by monitoring the melt viscosity in air at 285°C for polyethylene terephthalate and 270°C for the copolyester used in a capillary rheometer by the method described by J. Devaux et al in Makromol. Chem. 179, 2201, 2209 (1978). With this convention, the smaller the K d , the more thermally εtable the material is. Calculations are conventional aε known by thoεe εkilled in the art. By "thermally εtable", it is meant that the K d iε lower for the polyeεterε of thiε invention when compared to polyesters of the same composition prepared by most known catalyst syεtemε where stabilizers are not employed. K d is defined by the equation: η η o η = Melt viεcosity at time t (dynes'sec) η = Melt viεcosity at time t = 0 (dynes ^ sec) o a = Constant [0.294] K d = Thermal degradation constant ϋ = time in minutes It is preferred that the sample be dry for thiε analyεis. K d iε determined from the εlope of the line obtained by plotting l/ιj a vε. time and εhould be linear. Thiε value of K d iε also dependant on the temperature at which it iε measured. For example, a thermally stable poly(ethylene terephthalate) preferably has a K d measured at 285°C in an air environment of lesε than 0.001. Units of K d are as follows: Example 1 showε poly(ethylene terephthalate) polymerized utilizing an antimony catalyεt in the absence of a phosphorus stabilizer. Examples 2-4 also εhow poly(ethylene terephthalate) synthesized with an antimony catalyst, however a phosphoruε stabilizer waε included at increasing levels. From Table 2, it can be seen that the addition of the phosphorus stabilizer does not decrease the color, and in addition the phosphoruε stabilizer actually increased the degradation rate constant indicating a less thermally εtable material. Example 5 shows a poly(69 mole % ethylene terephthalate—co—31 mole % 1,4—cyclohexanedimethylene terephthalate) polymerized using a conventional catalyst syεtem of titanium with a cobalt bluing agent and a phoεphoruε stabilizer. From Table 2 it can be seen that this polyester has high I.V. and reasonable color. However, Example 5 has a relatively high thermal degradation rate constant (K d ) of 2.12 X 10 ~4 aε measured at 270°C, even though a phosphorus stabilizer was used. In contrast, Example 6 utilizes only antimony acetate as a catalyst, haε slightly lower I.V., but good color and a low degradation rate constant of 1.10 X IO -4 as measured at 270°C, despite the fact that no stabilizer was utilized. Example 7 shows the essentially the same polymer aε 6, but with toner dyes added to improve the color aε indicated by both the a* and b* values reported in Table 2. Example 8 is also essentially identical to 6, but this time a phoεphoruε stabilizer was added. Aε seen from the resultε in Table 2, Example 8 has essentially identical properties as 6 indicating that the phosphorus stabilizer is not needed. These results show conclusively that when antimony acetate is used as a catalyεt the phoεphoruε stabilizer is not neceεεary to provide thermal stability or low color. Furthermore if antimony acetate is utilized as a catalyεt in conjunction with a nonreactive organic bluing agent a thermally stable polyester with excellent color is achievable. Table 1 * Concentrations are in parts per million (ppm) P = Phosphorus added aε Merpol A which iε commercially available from DuPont Ti = Titanium added aε Titanium isopropoxide Co = Cobalt added as Cobalt Acetate Sb = Antimony added aε Antimony acetate TPA = terephthalic acid RT = Red Dye having the following structure: = Blue Dye having the following εtructure: Table 2 The invention haε been deεcribed in detail with particular reference to preferred embodimentε thereof, but it will be underεtood that variations and modifications can be effected within the spirit and scope of the invention. Moreover, all patents, patent applications (published and unpublished, foreign or domestic) , literature references or other publications noted above are incorporated herein by reference for any disclosure pertinent to the practice of thiε invention.

Claims: CLAIMS We claim: 1. A thermally stable polyester, comprising: a polyester resin prepared by adding a dicarboxylic acid to a glycol compound, said dicarboxylic acid selected from the group consisting of aliphatic dicarboxylic acids having a total of from 3 to 16 carbon atomε, alicyclic dicarboxylic acids having 7 to 12 carbon atoms, aromatic dicarboxylic acids containing a total of from 8 to 16 carbon atoms, and combinations thereof, and wherein said glycol is selected from the group consisting of glycols having from 2 to 12 carbon atomε, glycol ethers having from 4 to 12 carbon atomε, and combinationε thereof, said polyester resin having been prepared in the presence of a catalyst system consisting essentially of one or more antimony compounds which is not reacted with α—hydroxy carboxylic acids, o. , β—dicarboxylic acids or derivatives thereof. 2. The polyester of Claim 1 wherein said glycols comprise ethylene glycol, 1,4— cyclohexanedimethanol, 1, 2—propanediol, 1,3- propanediol, 1, 4—butanediol, 2 ,2—dimethyl—1, 3— propanediol, 1,6—hexanediol, 1,2—cyclohexanediol, 1, —cyclohexanediol, 1,2—cyclohexanedimethanol, 1, 3—cyclohexanedimethanol, Z, 8—bis(hydroxymethyl)- tricycle—[5.2.1.0]— ecane wherein Z representε 3, 4, or 5, diethylene glycol, triethylene glycol, dipropylene glycol and tripropylene glycol. 3. The polyester of Claim 2 wherein said glycol compriseε ethylene glycol. 4. The polyester of Claim 3 wherein εaid ethylene glycol is present in the amount of 65 to 100 mole percent based on the total percentages for all glycol components being 100 mole %. 5. The polyester of Claim 2 wherein said glycols comprise ethylene glycol and 1,4— cyclohexanedimethanol. 6. The polyester of Claim 5 wherein said polyester comprises at least about 50 mole percent ethylene glycol, 1, 4—cyclohexanedimethanol and mixtures thereof. 7. The polyester of Claim 1 wherein said dicarboxylic acid comprises terephthalic acid, isophthalic acid, 1 , 4—cyclohexanedicarboxylic acid, 1,3- cyclohexanedicarboxylic acid, εuccinic acid, glutaric acid, adipic acid, sebacic acid, 1,12— dodecanedioic acid, 2 , 6-naphthalenedicarboxylic acid, and 2, 7—naphthalenedicarboxylic acid. 8. The polyeεter of Claim 7 wherein εaid dicarboxylic acid comprises an aromatic dicarboxylic acid. 9. The polyeεter of Claim 8 wherein said aromatic dicarboxylic acid comprises terephthalic acid, isophthalic acid, and 2 , 6—naphthalenedicarboxylic acid. 10. The polyeεter of Claim 9 wherein εaid dicarboxylic acid compriεeε terephthalic acid. 11. The polyester of Claim 10 wherein said terephthalic acid is present in the amount of at least 50 mole \ baεed on the total mole percentages of the acids present in the polyester being 100 mole %. 12. The polyester of Claim 11 wherein said terephthalic acid is present in the amount of 75 to 100 mole % based on the total mole percentages of the acids present in the polyester being 100 mole %. 13. The polyester of Claim 12 wherein said terephthalic acid is present in the amount of 90 to 100 mole % based on the total mole percentages of the acids present in the polyester being 100 mole %. 14. The polyeεter of Claims 12 and 13 wherein said polyester further comprises 65 to 100 mole % ethylene glycol. 15. The polyester of Claim 1 wherein said antimony compound is a trivalent organic antimony compound. 16. The polyester of Claim 1 wherein said antimony compounds comprises tributyl antimony oxide, antimony alkoxides, KSb(0H) 6 , NH 4 SbF 6 and SBS 3 , antimonate esters of inorganic acids, cyclic alkyl antimonate esters, and aryl antimonic acid compounds, antimony oxide, antimony trioxide, antimony carboxylate, antimony glycolate, antimony halide, antimony sulfide, sodium, potassium antimonate, antimony carboxylate, antimony trioxide and antimony glycolate. 17. The polyester of Claim 16 wherein said antimony compound comprises antimony carboxylate, antimony glycolate, and antimony trioxide. 18. The polyester of Claims 1, 4, and 9 comprising organic dyes. 19. The polyester of Claim 18 wherein said organic dye is an anthraquinone dye comprising at least one blue 1, -bis(2 , 6-dialkylanilino) anthraquinone compound of Formula (I) (I) wherein: R is selected from the group conεiεting of hydrogen, alkoxy—C—; R 2 and R 2 are independently C 1 —C 6 —alkyl; R 3 is selected from the group consiεting of hydrogen, halogen, C j —C 6 —alkyl, substituted C 1 —C 6 alkyl, hydroxy, C^—C g —alkoxy, subεtituted C^ ^ —C g —alkoxy, cyano, thiocyano,C 1 —C g —alkylthio, substituted C 2 —C 6 —alkylthio, Q χ —C g —alkylsulfonyl, substituted C j —C 6 —alkylεulfonyl, C- L —C g —alkoxycarbonyl, carboxy, aryloxy, arylthio, arylεulfonyl, and S0 2 N(R 4 )R 5 X when m and/or n are zero; R 4 iε selected from the group consisting of hydrogen, C-^C 8 -alkyl, subεtituted C 1 -C 6 -alkyl, C 3 -C 8 —alkenyl , C 3 -C 8 -alkynyl , C 3 —C 7 —cycloalkyl and aryl; R 5 is a linking group εelected from the group conεisting of C- j —C 8 —alkylene, C α —C 6 —alkylene—Z—C 1 —C 6 — alkylene, arylene-C 1 —C 6 -alkylene, arylene—Z-C-^C 6 alkylene, C 3 —C 7 —cycloalkylene, C : —C 6 —alkylene—cycle— alkylene-^—C g —alkylene, C-^—C 6 —alkylene—arylene—C 2 —C 6 - alkylene, and C —C 6 —alkylene-Z— rylene—Z—C 1 —C 6 —alkylene, wherein Z iε selected from —0—, —S— or S0 2 ; X iε hydrogen or a polyester reactive group; and m and n are independently 0 or 1; with the proviso that at leaεt one polyester reactive group is present; along with at least one red anthraquinone or anthrapyridone compound εelected from formula (II) - (X) below: p ( C P I I III IV V VI 20 VII 25 50 VIII IX wherein : R 6 is selected from the group consisting of hydrogen, C 1 —C 6 —alkyl, substituted C j —C g —alkyl, C 3 —C 7 —cycloalkyl or aryl; R 7 is hydrogen or one to three groupε εelected from C α —C 6 —alkyl, C 1 —C 6 —subεtituted alkyl, C 1 —C 6 - alkanoylamino, halogen, C 2 —C 6 —alkyl C } —C 6 —alkoxy, C- L -C 8 -alkylthio; R 8 and R 9 are the same or different and are selected from the group consisting of C 1 —c 6 —alkyl, subεtituted C 2 —C 6 —alkyl, C 3 —C 7 -cycloalkyl or aryl; R 10 is selected from the group conεisting of C- j^ —C g —alkyl, C 3 —C 7 —cycloalkyl or aryl; R 1J is εelected from the group consiεtmg of hydrogen, C l —C 12 ~alkyl , substituted C^C 12 —alkyl , C 3 —C 7 -cycloalkyl and aryl; R 12 is hydrogen or one to three groups selected from the group conεiεting of C- j^ —C g —alkyl , εubstituted C 1 -C 8 —alkyl, C j —C g —alkoxy, εubstituted C-,—C 6 —alkoxy, C 1 —C g —alkylthio, substituted C 2 —C 6 —alkylthio, halogen, hydroxy, C^C 6 —alkanoylamino, aroylamino, C 2 —C 6 — alkylsulfonylamino and arylsulfonylamino; R 13 and R 14 are εelected from hydrogen, cyano or C0 2 R 10 ; R 15 iε R 4 or R 5 X aε previouεly defined; L lε —CO- or —Sθ 2 —; X iε hydrogen or a polyester reactive group; m is 0 or 1; and p lε 1 or 2 ; with the proviεoε that R 13 iε hydrogen when m iε 0 and at least one polyester reactive group is present. 20. The polyeεter of Claim 19, wherein the blue anthraquinone compound(ε) correεpondε to structure (I) above, wherein R is hydrogen; R : and R 2 are independently selected from methyl and ethyl; P, is hydrogen, methyl, or bromo; R 4 iε hydrogen, C-^—C 4 —alkyl or aryl; R 5 iε selected from the group consiεting of C j —C 6 —alkylene, C 1 -C 4 -alkylene-0-C 1 -C 4 -alkylene, -CH 2 C 6 H 10 CH 2 -, arylene, or —CH 2 —arylene— and the red component correspondε to formula (V) , wherein R 7 is C } —C g —alkoxy and R 4 and R 5 are as defined in claim 1. 21. The polyester of Claim 19, wherein the concentra¬ tion of blue and red compounds taken together is from about 0.5ppm to about lOppm. 22. The polyeεter of Claim 19, wherein the total concentration of blue compound(ε) is about 1 to 7ppm and the concentration of red compound(ε) iε about 0.5 to 3ppm. 23. The polyester of Claim 19, wherein the compound of formula (I) iε H r ?= 0 2 NHC 2 H 4 0H 0 2 NHC 2 H 4 OH 24. The polyeεter of Claim 19, wherein the compound of formula (I) iε 25. The polyeεter of Claim 19, wherein the red compound of formula (V) iε 26. The polyeεter of Claim 19, wherein the red compound of formula (V) iε OCH. 27. The polyeεter of Claim 19, wherein the blue compound of formula (I) iε and wherein the red compound of formula (V) iε 28. The polyester of Claim 19, wherein the red compound of formula (II) iε COOH 29. The polyester of Claim 19, wherein the red compound of formula (III) is / H. X > -CH 2 0H 30. The polyester of Claim 19, wherein the red compound of formula (VI) is 31. The polyeεter of Claim 19, wherein the red compound of formula (VIII) is 32. A procesε for producing a thermally εtable polyester resin wherein said polyester resin is prepared by adding a dicarboxylic acid to a glycol compound, said dicarboxylic acid being selected from the group consisting of aliphatic dicarboxylic acids having a total of from 3 to 16 carbon atoms, alicyclic dicarboxylic acids having 7 to 12 carbon atoms, aromatic dicarboxylic acidε containing a total of from 8 to 16 carbon atomε, and combinationε thereof, and εaid glycol being εelected from the group conεiεting of glycolε having from 2 to 12 carbon atoms, glycol ethers having from 4 to 12 carbon atoms, and combinations thereof, εaid polyester reεin being prepared in the presence of a catalyst system consisting esεentially of one or more antimony compounds which is not reacted with α—hydroxycarboxylic acids, a. , β—dicarboxylic acids or derivatives thereof. 33. The proceεε of Claim 32 wherein said glycolε comprise ethylene glycol, 1,4— cyclohexanedimethanol, 1, 2—propanediol, 1,3— propanediol, 1,4-butanediol, 2 , 2-dimethyl-l, 3- propanediol, 1 , 6—hexanediol , 1 , 2—cyclohexanediol , 1 , 4—cyclohexanediol, 1, 2—cyclohexanedimethanol , 1, 3—cyclohexanedimethanol, Z, 8-bis (hydroxymethyl)- tricyclo-[5.2.1.0]—decane wherein Z represents 3, , or 5, diethylene glycol, triethylene glycol, dipropylene glycol and tripropylene glycol. 34. The process of Claim 32 wherein said glycol compriseε ethylene glycol. 35. The process of Claim 34 wherein said ethylene glycol is preεent in the amount of 65 to 100 mole percent based on the total percentages for all glycol components being 100 mole %. 36. The proceεε of Claim 34 wherein said glycols comprise ethylene glycol and 1,4— cyclohexanedimethanol. 37. The procesε of Claim 36 wherein εaid polyeεter comprises at least about 50 mole percent ethylene glycol, 1,4—cyclohexanedimethanol and mixtures thereof. 38. The procesε of Claim 32 wherein εaid dicarboxylic acid compriseε terephthalic acid, iεophthalic acid, 1 , 4—cyclohexanedicarboxylic acid, 1,3— cyclohexanedicarboxylic acid, εuccinic acid, glutaric acid, adipic acid, εebacic acid, 1,12- dodecanedioic acid and 2, 6-naphthalenedicarboxylιc acid and 2 ,7-naphthalenedicarboxylic acid. 39. The polyester of Claim 38 wherein said dicarboxylic acid comprises an aromatic dicarboxylic acid. 40. The polyester of Claim 39 wherein said dicarboxylic acid compriseε terephthalic acid, iεophthalic acid, and 2 , 6-naphthalenedicarboxylic acid. 41. The proceεε of Claim 40 wherein εaid dicarboxylic acid comprises terephthalic acid. 42. The process of Claim 41 wherein said terephthalic acid is present in the amount of at least 50 mole based on the total mole percentages of the acids present in said polyester being 100 mole %. 43. The process of Claim 42 wherein εaid terephthalic acid is present in the amount of 75 to 100 mole % based on the total mole percentages of the acids present in εaid polyester being 100 mole %. 44. The procesε of Claim 43 wherein said terephthalic acid iε present in the amount of 90 to 100 mole % based on the total mole percentages of the acids present in εaid polyeεter being 100 mole %. 45. The proceεε of Claimε 43 and 44 wherein said polyeεter further compriεeε 65 to 100 mole % ethylene glycol. 46. The polyeεter of Claim 32 wherein εaid antimony compound iε a trivalent organic antimony compound. 47. The polyeεter of Claim 32 wherein said antimony compoundε compriseε tributyl antimony oxide, KSb(OH) 6 , NH 4 SbF 6 and SBS 3 , antimonate eεters of inorganic acids, cyclic alkyl antimonate esters, and aryl antimonic acid compounds, antimony oxide, antimony trioxide, antimony carboxylate, antimony glycolate, antimony halide, antimony sulfide, sodium, potassium antimonate, antimony carboxylate, antimony trioxide and antimony glycolate. 48. The polyester of Claim 47 wherein said antimony compound compriseε antimony carboxylate, antimony glycolate, and antimony trioxide. 49. The proceεε of Claim 32, 35 and 39 compriεing organic dyeε. 50. The proceεε of Claim 49 wherein said organic dye is an anthraquinone dye comprising at leaεt one blue 1,4—bis(2,6—dialkylanilino) anthraquinone compound of Formula (I) (I) wherein: R iε εelected from the group conεiεting of hydrogen, C } —C 6 alkyl, halogen, carboxy, and —c ξι al c Xy Y ; R 1 and R 2 are independently C-^C 8 -alkyl; R 3 is selected from the group consisting of hydrogen, halogen, C j -C 8 -alkyl, substituted C 2 -C 8 alkyl, hydroxy, C j -C 8 -alkoxy, substituted C^C 8 -alkoxy , cyano, thiocyano,C 1 -C 6 -alkylthio, substituted C^C 8 -alkylthio, C 1 -C 6 — alkylsulf onyl, substituted C j -Cg-alkylsulf onyl , C- L -C 8 -alkoxycarbonyl, carboxy, aryloxy, arylthio, arylsulfonyl, and S0 2 N(R 4 )R 5 X when and/or n are zero; R 4 is εelected from the group conεiεting of hydrogen, C j -Cg-alkyl , εubεtituted C 1 -C 6 -alkyl, C 3 -C 8 -alkenyl, C 3 -C 8 -alkynyl , C 3 -C 7 -cycloalkyl and aryl; R 5 is a linking group selected from the group consisting of ^—C g —alkylene, C 1 —C 6 —alkylene-Z—C 1 -c 6 - alkylene, arylene—C 1 -C 6 -alkylene, arylene-Z-C 1 —C 6 alkylene, C 3 -C 7 —cycloalkylene, C χ —C 6 —alkylene-cyclo— alkylene-^-C 8 -alkylene, C 1 -C 6 -alkylene-arylene-C 1 -C 6 - alkylene, and C 1 -C 6 -alkylene-Z-arylene-Z-C 1 -C 6 -alkylene, wherein Z is selected from —0—, —S— or S0 2 ; X iε hydrogen or a polyester reactive group; and and n are independently 0 or 1; with the proviso that at least one polyester reactive group is present; along with at leaεt one red anthraquinone or anthrapyridone compound εelected from formula (II) — (X) below: XI/ < 0θ 2 R 6>p II X sS χ />.-CH"2„X' III ( IV V VI VII 25 30 )R 6 X) πι 55 VIII 60 IX 90 95 100 X wherein: R 6 is selected from the group consisting of hydrogen, C j —C 6 -alkyl, substituted C 1 —C 6 —alkyl, C 3 -C 7 -cycloalkyl or aryl; R 7 is hydrogen or one to three groupε selected from C 1 -C 6 -alkyl, C-^C 8 -substituted alkyl, C-^C 8 - alkanoylamino, halogen, C 2 —C 6 —alkyl C 2 —C 6 —alkoxy, C λ —C 8 -alkylthio; R 8 and R 9 are the same or different and are selected from the group consiεting of C 2 —C 6 —alkyl, εubstituted C 1 —C 6 -alkyl, C 3 —C 7 —cycloalkyl or aryl; R 10 i s selected from the group consisting of c 2 —C 8 -alkyl, C 3 -C 7 -cycloalkyl or aryl; R 12 iε selected from the group consisting of hydrogen, C 1 -C 12 -alkyl, subεtituted C 1 -C 12 -alkyl, C 3 —C 7 —cycloalkyl and aryl; R 12 is hydrogen or one to three groupε εelected from the group consisting of C j —C g —alkyl, substituted C α —C 8 -alkyl, C 1 -C t -alkoxy, substituted C 1 -C 6 -alkoxy, C^C 8 -alkylthio, εubεtituted C 1 -C 6 -alkylthio, halogen, hydroxy, C —C 6 —alkanoylamino, aroylamino, C j —C 6 - alkylεulfonylamino and arylsulfonylamino; R 13 and R 14 are εelected from hydrogen, cyano or CO 2 R 10 ; R 15 iε R 4 or R 5 X as previously defined; L is -CO- or —S0 2 -; X is as previously defined; m iε 0 or 1; and p is 1 or 2 ; with the provisoε that R 13 iε hydrogen when m is 0 and at leaεt one polyester reactive group iε preεent. 51. The proceεs of Claim 49, wherein the blue anthraquinone compound(s) correεpondε to structure (I) above, wherein R iε hydrogen; R α and R 2 are independently εelected from methyl and ethyl; R 3 iε hydrogen, methyl, or bromo; R 4 iε hydrogen, C 2 —C 4 -alkyl or aryl; R 5 iε selected from the group conεiεting of C 1 —C 6 —alkylene, C-^C 4 —alkylene—0—C 1 —C 4 -aIkylene, -CH 2 C 6 H 10 CH 2 -, arylene, or —CH 2 —arylene— and the red component correεponds to formulae (V) , wherein R 7 is C —C g —alkoxy and R 4 and R 5 are aε defined in Claim 1. 52. The process of Claim 50, wherein the concentration of blue and red compoundε taken together iε from about 0.5ppm to about lOpp . 53. The proceεs of Claim 50, wherein the total concentration of blue compound(ε) iε about 1 to 7ppm and the concentration of red compound(s) iε about 0.5 to 3ppm. 54. The procesε of Claim 50, wherein the compound of formula (I) iε 55. The proceεs of Claim 50, wherein the compound of formula (I) is 56. The proceεε of Claim 50, wherein the red compound of formula (V) iε 0 2 NHC 2 H 4 OH 57. The proceεε of Claim 50, wherein the red compound of formula (V) iε 58. The procesε of Claim 50, wherein the blue compound of formula (I) iε 30 and wherein the red compound of formula (V) iε 35 40 0 59. The procesε of Claim 50, wherein the red compound 5 of formula (II) iε 25 60. The process of Claim 50, wherein the red compound of formula (III) is 50 61. The procesε of Claim 50, wherein the red compound of formula (VI) iε 0 62. The proceεε of Claim 50, wherein the red compound of formula (VIII) is 20

Inventors: BRINK ANDREW EDWIN, CHERRY CLINTON DI, PRUETT WAYNE PAYTON, SHACKELFORD KAY HUNT, BRINK, ANDREW, EDWIN, CHERRY, CLINTON +DI, PRUETT, WAYNE, PAYTON, SHACKELFORD, KAY, HUNT
Applicants: EASTMAN CHEM CO, EASTMAN CHEMICAL COMPANY
Application year: 1996
Main classification: C08G63
IPC codes: C08G63, C08K5, C08L67