Dielectric material comprising Ta2O5 doped with TiO2 and devices employing same

Abstract: Applicant has discovered that the dielectric constant of Ta 2 O 5 can be significantly enhanced by the addition of small quantities of TiO 2 . Specifically, if Ta 2 O 5 is doped with more than about 3 mole percent of TiO 2 the doped material will have a dielectric constant higher than the undoped material. For example, at a ratio of 0.92 Ta 2 O 5 :0.08 TiO 2 , the dielectric constant is enhanced by a factor of more than three. Because both Ta and Ti are compatible with current microelectronics processing, the new dielectric can be used to make capacitors of reduced size with but minor modifications of conventional processes.

Description: Field of the Invention This invention relates to dielectric materials and, in particular, to dielectric materials comprising Ta 2 O 5 doped with TiO 2 to enhance their dielectric constants. These materials are particularly useful for providing dielectric layers in capacitors. Background of the Invention As microelectronic circuits become increasingly integrated, the demand for smaller components becomes stronger. For the capacitive components, the materials presently employed have inadequate dielectric constants to be used with lower area. To remedy this problem, exotic high dielectric constant materials such as Barium Strontium Titanate (BST) are presently in the research stage in many laboratories, especially for their potential use in DRAM applications. Such materials, however, invariably require the use of chemical elements foreign to the usual microelectronics manufacturing procedures and therefore require alteration of manufacturing processes and extensive compatibility testing. Accordingly, there is a need for a new improved dielectric material compatible with conventional microelectronic processing. European Patent Application 210,033 to Sony Corporation published January, 1987 describes a dielectric amorphous material composed of Ta 2 O 5 and TiO 2 . The Sony application states that in order to obtain a Ta 2 O 5 thin film having a high dielectric strength, the film must be grown at a temperature as high as possible in the range in which an amorphous film can be obtained. Summary of the Invention Applicant has discovered that the dielectric constant of Ta 2 O 5 can be significantly enhanced by the addition of small quantities of TiO 2 . Thus, according to the present invention there is provided a dielectric as defined in claim 1. The present invention also provides a capacitor as defined in claim 3. Specifically, if Ta 2 O 5 is doped with more than about 3 mole percent of TiO 2 the doped material will have a dielectric constant higher than the undoped material. For example, at a ratio of 0.92 Ta 2 O 5 : 0.08TiO 2 , the dielectric constant is enhanced by a factor of more than three. Because both Ta and Ti are compatible with current microelectronics processing, the new dielectric can be used to make capacitors of reduced size with but minor modifications of conventional processes. Brief Description of the Drawings The advantages, nature and features of the invention will appear more fully upon consideration of the illustrative embodiments now to be described in detail in connection with the accompanying drawings. In the drawings: PIG.1 is a graphical illustration of the dielectric constant at 1 MHz of (Ta 2 O 5 ) 1-x (TiO 2 ) x at 20°C. FIG. 2 is a graphical illustration of the dielectric constant at 1 MHz of (Ta 2 O 5 ) 0.92 (TiO 2 ) 0.08 at various temperatures. FIG. 3 shows the variation of the dielectric constant with temperature for several different compositions of doped Ta 2 O 5 . FIG. 4 is a schematic cross section of a capacitor comprising a dielectric layer of Ta 2 O 5 doped with TiO 2 . It is to be understood that these drawings are for purposes of illustrating the concepts of the invention and, except for the graphs, are not to scale. Detailed Description Applicant has found that the dielectric constant of Ta 2 O 5 is enhanced by small quantities of TiO 2 dopant It was determined that the dielectric constant K of(Ta 2 O 5 ) 1-x (TiO 2 ) x exceeds that of undoped Ta 2 O 5 for x ≤ 0.03. K is doubled over the approximate range 0.05 < x < 0.15, and it achieves a maximum of more than three times the undoped value at x ≈ 0.08. The remaining discussion is divided into three parts. Part A describes preparation of the bulk material. Part B describes its properties, and Part C shows its use in making improved capacitors. A. Material Preparation In a series of experiments, ceramic samples in the Ta 2 O 5 - TiO 2 chemical system were made by standard ceramic processing techniques. High purity tantalum oxide and titanium oxide were first mixed in a predetermined molar ratio, mechanically ground, and fired for several nights in dense Al 2 O 3 crucibles in air between 1350 and 1400°C with intermediate grinding. The powders were then pressed into 1.27 cm (0.5 inch) diameter pellets approximately 0.375 cm (0.125 inch) thick and fired in air on powder of their own composition for 16-24 hours at 1400°C. They were cooled to 100°C at 200°C/hr. before the furnace was turned off. B. Properties Surfaces of the pellets were then sanded smooth and 1:1 mole ratio Ga:In alloy solder electrodes were applied. Measurements of the dielectric constants and dissipation factors were then made at 1 MHz and 100 KHz using an HP4192A impedance analyzer. The data for the 1 MHz measurements is summarized in Table 1. The dielectric constant, dissipation factor, total variation in dielectric constant, and temperature coefficient of dielectric constant (TCK) in a -20 to 60°C temperature range are tabulated for each composition studied. Dielectric Properties of Bulk Polycrystalline Ta 2 O 5 - TiO 2 Ceramics Measured at 1 MHz Composition K at 20°C D at 20°C Total Change in K(%) -20 to + 60°C TCK ppm/°C Ta 2 O 5 TiO 2 1.00 0.00 35.4 0.006 +4.8 600 0.98 0.02 20.3 0.016 +7.6 950 0.96 0.04 46.6 0.038 +20.6 2580 0.94 0.06 94.0 0.016 +22.5 2810 0.92 0.08 126.2 0.010 +23.4 2930 0.90 0.10 97.8 0.026 +24.3 3040 0.875 0.125 88.6 0.008 +16.9 2110 0.85 0.15 69.1 0.008 +13.0 1620 0.80 0.20 59.4 0.009 +11.4 1420 0.70 0.30 57.6 0.021 +12.1 1510 0.60 0.40 42.2 0.009 +9.7 1210 FIG. 1 plots the dielectric constant K at 1 MHz and 20°C for various compositions of (Ta 2 O 5 ) 1-x (TiO 2 ) x . As can be seen, K drops for low level doping of TiO 2 less than about 3 mole percent and thereafter increases over that of the undoped material. The greatest enhancement of K occurs at compositions between 5% TiO 2 and 15% TiO 2 where K more than doubles. The graph shows a strong peak of K=126 at about 8% TiO 2 doping. As the TiO 2 component increases beyond about 40% it becomes increasingly difficult to form films of the material with enhanced properties. Similar behavior was observed at 100 KHz. FIG. 2 plots the temperature dependent dielectric constant for a 0.92 Ta 2 O 5 :0.08 TiO 2 polycrystalline pellet. The increased dielectric constant that results from TiO 2 doping of Ta 2 O 5 is accompanied by a significant increase in TCK. FIG. 3 plots the temperature variation of K for several compositions. The graph shows that materials near the highest K have similar TCKs. It also shows that an enhancement of the dielectric constant by a factor of 2 over Ta 2 O 5 with lower TCK than the 0.92:08 material is possible for compositions near 85% Ta 2 O 5 . The composition region between approximately 94 and 88% Ta 2 O 5 yields the best materials if the value of K is the primary consideration. Characterization of the materials by conventional powder X-ray diffraction (CuK x-radiation) showed that the enhanced dielectric constant for 8%-15% TiO 2 doping is associated with the presence of the H' monoclinic Ta 2 O 5 solid solution phase. Thus the TiO 2 doping resulted in the formation of a crystallographic phase different from that obtained in pure Ta 2 O 5 . Table 1 also shows the values of the dielectric dissipation (D) at 1 MHz. Unlike the other dielectric data, the D values do not systematically change with composition. This suggests that the loss values are dominated by uncontrolled parameters in the present processing procedure, such as the presence or absence of oxygen vacancies, well known to occur in titanium based oxides. In any case the dissipation factor measured for the 0.92:0.08 composition is not more than a factor of 2 higher than that for pure Ta 2 O 5 , and may actually be of the same magnitude as that of Ta 2 O 5 in properly processed materials, as is suggested by the lower D values for other materials in the table. C. Exemplary Device Application FIG. 4 is a schematic cross section of a capacitor 10 comprising a dielectric layer 40 of TiO 2 doped Ta 2 O 5 disposed between a pair of electrodes 41 and 42. In preferred applications electrode 41 is supported on a substrate 43 containing other microelectronic components (not shown) and layer 40 is preferably (Ta 2 O 5 ) 1-x (TiO 2 ) x where 0.03 ≤ x ≤ 0.4 and preferably 0.05 ≤ x ≤ 0.15. A thin film of the dielectric can be deposited on electrode 41 from the bulk material by conventional sputtering or laser ablation processes. Preferred electrodes can be made of doped polysilicon. The advantage of using this dielectric material is that because of its enhanced dielectric constant, the area on the substrate consumed by the capacitor can be reduced, thereby permitting a higher density of components. Use of material with x ≈ 0.08 permits the same capacitance in one-third the area as that for x=0. It is to be understood that the above-described embodiments are illustrative of only a few of the many possible specific embodiments of the invention. Numerous and varied other arrangements can be made by those skilled in the art without departing from the scope of the invention as defined by the appended claims.

Claims: A dielectric polycrystalline ceramic material composed of (Ta 2 O 5 ) 1-x (TiO 2 ) x where x ranges from 0.05 to 0.10. The dielectric material of claim 1 where x is approximately 0.08. A capacitor comprising a pair of conductive electrodes and, disposed between the electrodes, a layer of dielectric polycrystalline ceramic material composed of (Ta 2 O 5 ) 1-x (TiO 2 ) x where x ranges from 0.05 to 0.10. The capacitor of claim 3 where x is approximately 0.08.

Inventors: CAVA ROBERT JOSEPH, CAVA, ROBERT JOSEPH
Applicants: AT & T CORP, AT&T IPM CORP.
Application year: 1996
Main classification: H01G4
IPC codes: C04B35, H01G4, H01B3