Method of manufacturing semiconductor device having capacitor

Abstract: A platinum bottom electrode film, a dielectric film composed of a high permittivity dielectric material or a ferroelectric material, and a platinum top electrode film are formed on a substrate on which circuit elements and wiring are formed, and the platinum top electrode film and the dielectric film are selectively dry-etched by using etching gas containing chlorine, then plasma generated by discharging gas containing fluorine is irradiated. By this method of manufacturing a semiconductor device including a capacitor, there is almost no residual chlorine, and hence erosion of the dielectric film by residual chlorine is prevented.

Description: BACKGROUND OF THE INVENTION The present invention relates to a method of manufacturing a semiconductor device having a capacitor using a high permittivity dielectric film or a ferroelectric film as a capacitor dielectric film, and in particular, to a method including a step of dry etching of the capacitor dielectric film. Recently, efforts are concentrated on development of a microcomputer incorporating a capacitor using a high permittivity dielectric film or a ferroelectric film, being effective as measures for decreasing extraneous emission which is an electromagnetic noise, and a ferroelectric nonvolatile RAM capable of operating at low voltage and writing/reading at high speed. Etching of these capacitor dielectric films has been done by wet etching as isotropic etching or non-selective ion milling. In these methods, however, high processing accuracy and high etching selectivity cannot be realized, and hence dry-etching technique is lately researched and developed intensively. The etching gas used in dry-etching of capacitor dielectric films and electrodes is halogen represented by chlorine or its compound. For example, chlorine alone, hydrogen chloride and carbon chloride have been reported. A conventional method of manufacturing a semiconductor device is described below by referring to drawings. This method was developped by the present inventors and forms part of an in-house technology. Fig. 3(a), Fig. 3(b), Fig. 3(c), and Fig. 3(d) are sectional views for explaining the method of forming a capacitor included in a conventional semiconductor device. First, as shown in Fig. 3(a), a platinum bottom electrode film 1, a dielectric film 2 comprised of a high permittivity dielectric film or a ferroelectric film, and a platinum top electrode film 3 are formed on a substrate 4 on which a silicon oxide film is deposited. Then, using a photoresist film 5 as mask, the platinum top electrode film 3 and the dielectric film 2 are dry-etched by using etching gas containing chlorine, and processed into a shape as shown in Fig. 3(b). Finally, by dry-etching the platinum bottom electrode film 1, a capacitor is formed. In this conventional manufacturing method, however, a defect 8 may be formed in a side wall 6 of the dielectric film 2 as shown in Fig. 3(c), or the side wall 6 is often degenerated into a difference substance 9 from the dielectric. When such state appears, short circuit of capacitor or increase of leakage current occurs, and the function as the capacitor is lost in an extreme case. The cause of appearance of such phenomenon may be considered as follows. On the side walls 6 of the platinum top electrode film 3 and the dielectric film 2 which are dry-etched, and on the surface 7 of the platinum bottom electrode film 1 which is exposed, atoms, ions or radicals of chlorine generated by decomposition of the etching gas due to discharge are massively deposited. These chlorine atoms, ions or radicals easily react with moisture to form an acidic aqueous solution, that is, hydrochloric acid. The side wall 6 of the dielectric film 2 composed of a dielectric oxide violently reacts with this hydrochloric acid, and the dielectric film 2 is eroded, or degenerated into other substance 9 different from the dielectric. As a result, it is considered to lead to short circuit of capacitor, increase of leakage current, or loss of function as capacitor. This adsorption of moisture occurs always in operation in the manufacturing process of a semiconductor device such as exposure of substrate to the atmosphere or washing in water, and is hence inevitable. Such inconvenience is also noted when using bromine or iodine as etching gas. SUMMARY OF THE INVENTION An object of the present invention is to provide a method of manufacturing a semiconductor device capable of preventing erosion of dielectric film, and suppressing occurrence of short circuit of capacitor and increase of leakage current. According to an aspect of the invention, a method of manufacturing a semiconductor device is defined in present claim 1 and comprises a step of forming a platinum bottom electrode film, a dielectric film, and a platinum top electrode film on a substrate on which circuit elements and wiring are formed, a step of dry-etching selectively first the platinum top electrode film and then the dielectric film by using etching gas containing at least one of chlorine, bromine and iodine, a step of irradiating plasma generated by discharging gas containing fluorine after the step of dry-etching, and a step of etching the platinum bottom electrode film. By the plasma irradiating process after dry-etching, decomposition products of the etching gas containing chlorine, bromine or iodine depositing on the side wall of the dielectric film or on the surface of the platinum bottom electrode film at the time of dry-etching are extremely decreased. It hence suppresses occurrence of defect or degeneration of the dielectric film which is induced by reacting the dielectric film with the acid formed by reaction of these decomposition products with moisture dielectric. Therefore occurrence of short circuit in capacitor and increase of leakage current may be extremely suppressed. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1(a), Fig. 1(b), and Fig. 1(c) are sectional views for explaining a method of forming a capacitor incorporated in a semiconductor device in a first embodiment of the invention. Fig. 2 is a comparative diagram of residual chlorine amount on the substrate in the first embodiments of the invention and a prior art. Fig. 3(a), Fig. 3(b), Fig. 3(c), and Fig. 3(d) are sectional views for explaining a conventional method of forming a capacitor incorporated in a semiconductor device. DESCRIPTION OF THE PREFERRED EMBODIMENTS The preferred embodiment of the invention is described below while referring to Fig. 1(a), Fig. 1(b), and Fig. 1(c). Same parts as in the prior art shown in Fig. 3(a), Fig. 3(b), Fig. 3(c), and Fig. 3(d) are identified with same reference numerals. First, same as in the conventional method, a platinum bottom electrode film 1, a dielectric film 2 composed of a high permittivity dielectric material or a ferroelectric material, and a platinum top electrode film 3 are formed on a substrate 4 on which circuit elements, wiring and an insulating film are formed. Next, as shown in Fig. 1(a), using an etching gas containing chlorine, with a photoresist film (not shown) as mask, the platinum top electrode film 3 and the dielectric film 2 are selectively dry-etched. Consequently, as shown in Fig. 1(b), plasma generated by discharging carbon tetrafluoride gas is irradiated to the substrate 4. At this time, the fluorine plasma obtained by discharge under the irradiating conditions of carbon tetrafluoride of 50 sccm, pressure of 1 Torr (1 torr = 133.3 Pa) and RF power of 100 W load is irradiated for 30 seconds. Then the platinum bottom electrode film 1 is selectively dry-etched, and the capacitor are formed into a specified shape. In thus manufactured semiconductor device, defect and degeneration in the side wall 6 of the capacitor observed in the prior art were hardly noted. As a result of investigation into the rate of occurrence of short circuits in this semiconductor device, a short circuit was observed only in one out of 50 pieces, and the short circuit incidence was extremely decreased to about one-tenth or less of the prior art. Besides, increase of leakage current was not detected. As the gas used in plasma irradiating, aside from the CF 4 above, it is preferred to use CHF 3 , NF 3 , XeF 2 , and SF 6 , and mixture of at least two of these gases. In particular, CF 4 and NF 3 gases are outstanding in the effects for preventing short circuit and suppressing increase of leakage current, and are hence preferred. The reason of suppression of occurrence of short circuit or increase of leakage current by plasma irradiating is not clearly explained yet. At least, however, from the results of measurement of residual chlorine concentration shown in Fig. 2, the following may be said. In Fig. 2, incidentally, the residual chlorine concentration after plasma irradiating is expressed as a relative value in comparison with the residual chlorine concentration right after dry-etching by etching gas containing chlorine. The residual chlorine concentration after plasma irradiating corresponds to the irradiating conditions shown in the first embodiment. The residual chlorine concentration after plasma irradiating is decreased to about one-third of the residual chlorine concentration right after dry-etching. At the time of dry-etching by using etching gas containing chlorine, as shown in Fig. 1(a), decomposition products such as chlorine atoms, ions and radicals formed by decomposition of the etching gas by discharge are massively deposited on the side walls 6 of the platinum top electrode film 3 and the dielectric film 2, and on the surface 7 of the platinum bottom electrode film 1 exposed by etching. Consequently, when the plasma generated by discharging the gas containing fluorine is irradiated, as shown in Fig. 1(b), the decomposition products are replaced by fluorine. In this case, since the chlorine is not strongly bonded with the platinum or dielectric on the side wall 6, the chlorine may be easily removed by irradiating an active fluorine plasma. Then, as shown in Fig. 1(c), the side wall 6 and the surface of the platinum bottom electrode film 1 are covered with fluorine. The role of the fluorine is not clarified. It is considered, among others, that the fluorine hardly reacts with moisture and hardly generates hydrofluoric acid, or hardly reacts with oxide dielectric, or reacts with oxide dielectric to form an inactive form on the surface which prevents reaction from propagating into the dielectric. Any way, the fluorine after plasma irradiating is considered to play a role in prevention of occurrence of defect or degeneration in the side wall of the dielectric film. The invention is not limited to the illustrated embodiment alone, but may be modified in various forms. For example, in the foregoing embodiment, gas containing chlorine is used as etching gas, but the same effects as in the embodiment are obtained by using etching gas containing bromine or iodine, instead of chlorine, or etching gas containing two or more of chlorine, bromine and iodine.

Claims: A method of manufacturing a semiconductor device comprising: a step of forming a platinum bottom electrode film (1), a dielectric film (2) composed of a high permittivity dielectric material or a ferroelectric material, and a platinum top electrode film (3) on a substrate (4) on which circuit elements and wiring are formed; a step of dry-etching selectively said platinum top electrode film (3) by using an etching gas containing at least one of chlorine, bromine and iodine; a step of dry-etching selectively said dielectric film (2) using the same mask as used for the etching of said platinum top electrode film, and by using an etching gas containing at least one of chlorine, bromine and iodine, a step of irradiating the structure with a plasma generated by discharging a gas containing fluorine after said step of dry-etching said dielectric film (2); and a step of etching said platinum bottom electrode film (1). The method of claim 1, wherein said gas containing fluorine is at least one of carbon tetrafluoride, methane trifluoride, nitrogen trifluoride, xenon fluoride and sulfur hexafluoride.

Inventors: FUJII EIJI, NAGANO YOSHIHISA, FUJII, EIJI, NAGANO, YOSHIHISA
Applicants: MATSUSHITA ELECTRONICS CORP, MATSUSHITA ELECTRONICS CORPORATION
Application year: 1996
Main classification: H01L21
IPC codes: H01L21, H01L27