ELECTRIC INCANDESCENT LAMP WITH A QUARTZ GLASS LAMP VESSEL

Abstract: The electric incandescent lamp has a quartz glass lamp vessel (1) or envelope (4') around the lamp vessel, which has a red coloured dope in the area at the side of the incandescent body (3). The quartz glass with red dope contains samarium<II> oxide, aluminium oxide, titanium dioxide, and silicon dioxide, the analysis of the glass in its oxidized form being Sm2O3 1 to 3 % by weight, Al2O3 up to 3 % by weight, TiO2, rest SiO2, the molar ratio Al/Sn being at least about 2 and the molar ratio Sm/Ti being from 2 to 8.

Description: Electric incandescent lamp with a quartz glass lamp vessel. The invention relates to an electric incandescent lamp with a quartz glass lamp vessel having an axis, an incandescent body being positioned in an axial portion of said lamp vessel and being laterally surrounded by quartz glass with samarium 11 oxide as a red dopant, which quartz glass upon analysis in oxidized form comprises, besides SiO 2 and oxides of trace elements, 1 to 3% Sm 2 O 3 by weight and up to 3% Al 2 O 3 by weight, the molar ratio Al/Sm being at least approximately 2. Such an electric lamp is known from EP-A-0 643 021. The known lamp can be used as an IR radiation source. A major portion of the light generated by the lamp, which would be undesirable, is removed by the red color of the doped quartz glass. Samarium is trivalent in the stable form of samarium oxide. This oxide is substantially colorless. Samarium" oxide is a dark red, but it is readily oxidized so that it is not available as such. Accordingly, metallic silicon or SiO is added to the batch during the manufacture of the quartz glass doped with samarium" oxide so as to reduce Sm" 1 to Sm 11 in the melt. An attractive feature is that SiO 2 is created thereby, so that no additional component is introduced into the glass. It is a disadvantage of the known lamp that comparatively many elongate gas bubbles occur in the doped quartz glass, which give the glass a striped appearance. These gas bubbles have little influence on the spectrum radiated by the lamp, but they do reflect radiation and give an impression of indifferent quality. It is an object of the invention to provide an electric incandescent lamp of the kind described in the opening paragraph of which the doped quartz glass has few or no gas bubbles. According to the invention, this object is achieved in that the quartz glass doped with samarium" oxide also comprises TiO 2 , the molar ratio Sm/Ti lying within a range from 2 to 8. The TiO 2 originates from TiO in the batch and is formed during the reduction of Sm 2 O 3 . It was found that the use of TiO strongly reduces the number of gas bubbles, or even prevents them altogether. This is in contrast to the number of bubbles arising when metallic Ti is added to the batch. The Sm/Ti ratio in the glass is accordingly lower than it could be theoretically, i.e. if half the quantity of metallic Ti were added to the batch. The quantity of ingredients of the doped quartz glass other than SiO 2 is limited in order to prevent the properties of the glass changing too much and to prevent the glass having too low a softening temperature or being too brittle. Al 2 O 3 is present in the glass for achieving a sufficient solubility of the samarium in the glass, and accordingly achieving a homogeneous and deeper coloring. The Al/Sm ratio is at least approximately 2 for this purpose, but on the other hand the quantity of Al 2 O 3 is limited to avoid said undesirable changes in the properties of the quartz glass. The quantity of Sm 2 O 3 is bound to a minimum on the one hand, so as to realize a sufficient red coloring of the glass, and to a maximum on the other hand so as to prevent the glass being insufficiently homogeneous for practical applications. The maximum quantity of TiO 2 in relation to the quantity of Sm 2 O 3 is also limited to that which is theoretically necessary for reducing the quantity of Sm m to Sm π , in order to prevent undesirable changes in the properties of the quartz glass. On the other hand, the minimum quantity of TiO 2 is determined by the required color of the doped quartz glass. In general, the Sm/Ti ratio will be chosen to lie between 3 and 6, preferably between approximately 4 and approximately 5. Trace elements which may be present as impurities may be sodium and potassium, each to a quantity of several ppm by weight, and iron, up to a few tenths of a ppm by weight. The lamp according to the invention may be used for heating purposes, for example for heating of rooms, the preparation of foods, such as cooking, or as a heat source for industrial processes such as drying of ink or paint. The purpose of the red quartz glass is to prevent the light generated by the lamp from being radiated with an unpleasant intensity. In spite of its color, a tube made of the doped quartz glass can be processed, for example for providing a vacuumtight seal therein. It is necessary, however, to use a stronger heat source for this than for a corresponding tube of colorless quartz glass because the red quartz glass radiates much heat. Those skilled in the art may readily ascertain in a few tests the configuration of heat sources, such as burners, required for a certain tube and the processing thereof, for example bending, inflating, upsetting-and- inflating, pulling-out, etc. Alternatively, a tube made of such quartz glass may be, for example, fused to tubes of non-doped quartz glass at both ends and the resulting tube may be processed into a lamp vessel, so that the lamp vessel is formed by the doped quartz glass over an axial portion only which laterally surrounds the incandescent body. The doped quartz glass may be present around the lamp vessel in the form of a tube or may be coupled thereto, for example detachably, or, for example, by means of resilient members. Alternatively, the tube may be held by a lamp cap connected to the lamp vessel, for example, may be enclosed between two lamp caps connected to the lamp vessel and placed opposite one another. It is favorable when a metal holder is accommodated in each lamp cap and has an end portion which encloses an end portion of the tube so as to keep the tube securely fixed. The quartz glass with the red dope has an orange-red to dark red color and can be readily manufactured from the batch at a temperature of, for example, approximately 2,000 °C, for example in vacuum or in a reducing atmosphere such as, for example, He/H 2 , for example He/H 2 7/3 (by volume), and can be given a tubular shape by usual techniques. The presence of Sm" manifests itself in the color of the doped quartz glass and its transmission spectrum. It is difficult, however, to determine the Sm" content of the glass besides any Sm jjj , if present, analytically because of the proneness to oxidation of the former. An embodiment of the electric incandescent lamp according to the invention is shown in the drawing, in which Fig. 1 shows a lamp in side elevation, partly broken away; Fig. 2 shows the transmission spectrum of the doped quartz glass of Fig. 1. In Fig. 1, the electric incandescent lamp has a quartz glass lamp vessel 1 with an axis 2, and an incandescent body 3 is arranged in an axial portion of this lamp vessel. The lamp vessel is filled with an inert gas comprising hydrogen bromide. The incandescent body is laterally surrounded by quartz glass 4 with samarium" oxide as a red dopant. This quartz glass, when analyzed in oxidized form, is found to comprise besides SiO 2 and oxides of trace elements also 1 to 3% Sm 2 O 3 by weight and up to 3% Al 2 O 3 by weight. The molar ratio Al/Sm is at least approximately 2. The quartz glass 4 doped with samarium" oxide also comprises TiO 2 . The molar ratio Sm/Ti here lies within the range from 2 to 8, in particular within the range from 3 to 6. In Fig. 1 , a tube made of the quartz glass 4 doped with samarium" oxide and having end portions 4' surrounds the lamp vessel 1. The lamp vessel has two mutually opposed lamp caps 5 in each of which a metal holder 6 is accommodated having an end portion 6' which encloses an end portion 4' of the relevant tube so as to keep this tube securely fixed. Contact pins 7 project from the lamp caps 5. To manufacture the quartz glass tube, 290 g SiO 2 , 4.1 g Al 2 O 3 , and 7.0 g Sm 2 O 3 were mixed and fired in the air at approximately 1 ,300 °C so as to drive out moisture. The mixture was granulated and mixed with 0.67 g TiO. The batch thus obtained was melted at approximately 2, 100 °C under 70% He and 30% H 2 by volume, and the molten material was drawn into a tube shape. The doped glass thus obtained has the following composition in oxidized form: approximately 290 g SiO 2 , approximately 4.1 g Al 2 O 3 (1.3% by weight), approximately 7.0 g Sm 2 O 3 (2.3% by weight), and approximately 0.83 g TiO 2 . The molar ratio Al/Sm is 2 and the molar ratio SmTi is 4. The glass has the transmission spectrum of Fig. 2 measured for a glass thickness of 1 mm. It is apparent therefrom that the glass is fully opaque to radiation below approximately 525 nm.

Claims: CLAIMS: 1. An electric incandescent lamp with a quartz glass lamp vessel (1) having an axis (2), an incandescent body (3) being positioned in an axial portion of said lamp vessel and being laterally surrounded by quartz glass (4) with samarium" oxide as a red dopant, which quartz glass upon analysis in oxidized form comprises, besides SiO 2 and oxides of trace elements, 1 to 3% Sm 2 O 3 by weight and up to 3% Al 2 O 3 by weight, the molar ratio Al/Sm being at least approximately 2, characterized in that the quartz glass (4) doped with samarium 11 oxide also comprises TiO 2 , the molar ratio Sm/Ti lying within a range from 2 to 8. 2. An electric incandescent lamp as claimed in Claim 1 , characterized in that the molar ratio Sm/Ti of the quartz glass (4) doped with samarium" oxide lies in the range from 3 to 6. 3. An electric incandescent lamp as claimed in Claim 1 or 2, characterized in that the quartz glass lamp vessel (1) consists of the quartz glass (4) doped with samarium" oxide. 4. An electric incandescent lamp as claimed in Claim 1 or 2, characterized in that a tube made of the quartz glass (4) doped with samarium" oxide and having end portions (4') surrounds the lamp vessel (1). 5. An electric incandescent lamp as claimed in Claim 4, characterized in that the lamp vessel (1) has two mutually opposed lamp caps (5) in each of which a metal holder (6) is accommodated which has an end portion (6') which encloses an end portion (4') of the tube so as to keep said tube securely fixed.

Inventors: PET ROBERT J, TIMMERMANS JOSEPHUS J, PET, ROBERT, J., TIMMERMANS, JOSEPHUS, J.
Applicants: PHILIPS ELECTRONICS NV, PHILIPS NORDEN AB, PHILIPS ELECTRONICS N.V.
Application year: 1996
Main classification: C03C3
IPC codes: C03B20, C03C3, H01K1