A method and apparatus for the growth of a single crystal

Abstract: According to the present invention, in the growth of an oxide single crystal or a compound semiconductor single crystal such as GaAs single crystal by the CZ method or LEC method, the tendency of concave solid-liquid interface shape at the periphery of the growing crystal can be suppressed to prevent polycrystallization without localized heating of the solid-liquid interface, while well controlling the diameter of the growing crystal even when using a crucible with a larger diameter, thus improving the yield of crystal on a commercial scale. The feature consists in that the end of a cylindrical body having an inner diameter of larger than the predetermined diameter of straight part of the growing crystal is immersed in the raw material melt or liquid encapsulant and the crystal is pulled while preventing the shape of the solid-liquid interface from becoming concave by controlling the rotation rate of at least one of a crucible holding the raw materialmelt, the growing crystal and cylindrical body.

Description: This invention relates to a method and apparatus for the growth of an oxide single crystal or a semiconductor single crystal by the liquid encapsulated Czochralskimethod (hereinafter referred to as LEC method), and in particular, it is concerned with a method and apparatus for the Czochralski growth of gallium arsenide bulk single crystal to be used for integrated circuits, electronic devices for communication, optical devices, etc. Generally, a single crystal bulk such as of GaAs is grown by the Czochralski (CZ) method or LEC method, but there arises a problem that polycrystals partly occur during the growth. Fig. 10 is a schematic view of an apparatus for carrying out the LEC method of the prior art, in which at the center of a high pressure chamber 13, a susceptor 14-fitted crucible 1 is supported by a lower shaft 6, the crucible 1 holding a raw material melt 3 and a liquid encapsulant 5, and a seed crystal 9 held by an upper pulling rod 7 is immersed in the raw material melt 3, followed by pulling a single crystal 4. A heater 10 is arranged around the raw material melt 3, a heater 11 is arranged around the single crystal 4 and a heat insulator 12 is arranged inside the high pressure chamber 1. The reason for the polycrystallization, as described above, is considered to consist in that the shape of the solid-liquid interface (S-L) of the growing crystal is concave to the melt near the periphery of the growing crystal and dislocations (D) propagated along a direction perpendicular to the solid-liquid interface accumulate in the periphery, thus rendering polycrystalline (P), as shown in Fig. 11. In order to prevent formation of such polycrystals, therefore, it is necessary to prevent the solid-liquid interface near the periphery of the growing crystal from becoming concave. As a method of preventing the solid-liquid interface from becoming concave in the CZ method or LEC method, it has been proposed to increase the power of a heater arranged in the vicinity of the solid-liquid interface as more as possible whereby to locally heat the side of the growing crystal and to suppress heat flow laterally from the crystal [HITACHI CABLE REVIEW No. 9 (1990), 55]. However, the above described method has the following problems: 1 ○ In order to locally heat the side of the growing crystal, it is necessary to shorten the length of the heater to some extent and apply a larger power. Consequently, the current density flowing through the heater is very large and the service life of the heater is very short. 2 ○ Since heating of the heater is carried out through a susceptor made of carbon, the crystal is uniformly heated in the vertical direction by heat conduction and substantial local heating is impossible. In the case of the LEC method, furthermore, B 2 O 3 used as an encapsulant absorbs the most part of heat radiation and accordingly, it is impossible to effectively heat the most important region, i.e. vicinity of the solid-liquid interface. 3 ○ Since not only the periphery part of the crystal but also the whole of the crystal side surface are heated, heat flow toward the side from the crystal is wholly suppressed and the order of convex to the melt of the solid-liquid interface increases, so large residual strain is contained in the growing crystal and uniformity of the property of a wafer cut out of the crystal is poor. 4 ○ In the CZ method or LEC method, controllability of the diameter of the growing crystal is strongly dependent on the temperature distribution on the surface of the raw material melt. In the prior art, however, it is difficult to stably maintain the above described temperature distribution with good reproducibility and when using a large amount of a raw material at once and using a crucible with a large diameter for high productivity of the single crystal, in particular, control of the diameter further becomes difficult with increase of the gap between the growing crystal and crucible wall. 5 ○ The LEC method is ordinarily used for the growth of a single crystal containing a volatile element, but in this method, the surface temperature cannot be so raised because of the presence of such a problem that a growing crystal pulled out of the liquid encapsulant is damaged through evaporation of the volatile element from the surface thereof. Consquently, the temperature gradient in the axial growth direction is restricted to higher region (temperature gradient in growth of GaAs single crystal: ordinarily about 100 °C/cm) and a crystal with many crystal defects (dislocations) and much residual strain can only be grown because of occurrence of large thermal stress in the growing crystal. 6 ○ Thus, the growth is carried out using a large amount of a liquid encapsulant so that the most part of the growing crystal is covered with the liquid encapsulant, in order to practice the LEC method under a small tempersture gradient (hereinafter referred to as Fully Encapsulated Cz method, i.e. FEC method), but because of the very small heat conductivity of the liquid encapsulant B 2 O 3 , response of the temperature on the surface of the raw material melt is deteriorated and consequently, control of the diameter of the crystal is extremely difficult. This cannot be said a useful growth method. WO 90/04054 relates to a process and device for pulling crystals according to the Czochralski method. It is an object of the present invention to provide an improved method for the LEC growth of an oxide or semiconductor single crystal, in particular, gallium arsenide bulk single crystal to be used for integrated circuits, electronic devices for communication, optical devices, etc. It is another object of the present invention to provide a method and apparatus for the growth of a single crystal with less crystal defects, whereby the above described disadvantages of the prior art can be overcome and the tendency of concave solid-liquid interface shape at the periphery of the growing crystal can be suppressed to prevent polycrystallization thereof without localized heating of the solid-liquid interface, while well controlling the diameter of the growing crystal even when using a crucible with a larger diameter. It is a further object of the present invention to provide a method and apparatus for the growth of a single crystal with less crystal defects, whereby the above described disadvantages of the prior art can be overcome and the tendency of becoming concave at the periphery of the growing crystal can be suppressed to prevent formation of polycrystals without localizing heating of the solid-liquid interface. Accordingly, the present invention provides a method for the growth of a single crystal, which method comprises pulling a crystal out of a raw material melt by the Liquid Encapsulated Czochralski method, characterized in that the end of a cylindrical body having an inner diameter at said end larger than a predetermined diameter of a straight part of the growing crystal is immersed in the raw material melt or liquid encapsulant and the crystal is pulled while preventing the shape of the solid-liquid interface at the periphery of the growing crystal from becoming concave by controlling the relative rotation rate of the cylindrical body with respect to a crucible holding the raw material melt or the growing crystal. In the present invention, the single crystal generally consists of a semiconductor single crystal, i.e. a Group IV element of the Periodic Table, such as Si, a Group III-V compound semiconductor, such as GaAs, InP, InGaAs, etc., a Group II-VI compound semiconductor, such as ZnSe, CdTe, etc., or an oxide single crystal, such as Bi 12 SiO 20 (BSO), LiNbO 3 (LNO), Li 2 B 4 O 7 (LBO), etc. The accompanying drawings are to illustrate the principle and merits of the present invention in more detail. Fig 1 is a schematic view illustrating a state where the convection of the raw material melt is changed by the cylindrical body (not in accordance with the present invention). Fig. 2 is a schematic view illustrating a state in the vicinity of the solid-liquid interface when the cylindrical body of the present invention is immersed in a raw material melt and a crystal with a straight part is pulled upward. Fig. 3 is a schematic view illustrating a state of convection in a raw material melt when the lower end of the cylindrical body of the present invention is immersed in an encapsulant. Fig. 4 is a schematic view illustrating such a state that the solid-liquid interface near the periphery of a growing crystal is rendered concave by a convection in a raw material melt in the CZ method of the prior art. Fig. 5 is a schematic view illustrating a state of a convection in a raw material melt in the LEC method. Fig. 6 is a schematic view illustrating one embodiment (not in accordance with the present invention) in a case of supporting the cylindrical body by a heat insulator. Fig. 7 is a schematic view illustrating one embodiment (not in accordance with the present invention) in a case of supporting the cylindrical body by the upper pulling rod. Fig. 8 is a schematic view illustrating another embodiment in a case of supporting the cylindrical body of the present invention by a heat insulator. Fig. 9 is a schematic view illustrating another embodiment in a case of supporting the cylindrical body of the present invention by the an upper pulling rod. Fig. 10 is a vertical cross-sectional view of an apparatus for practicing the LEC method of the prior art. Fig. 11 is a schematic view illustrating a state of polycrystallization in the solid-liquid interface in the prior art. Fig. 12 is a schematic view showing growth striations of a crystal obtained in Example 1. Fig. 13 is a schematic view showing growth striations of a crystal obtained in Example 2. Fig. 14 is a schematic view showing growth striations of a crystal obtained in Comparative Example (LEC method of the prior art). Fig. 15 is a graph showing radial distributions of dislocation density in wafers cut out of crystals obtained in Examples 3, 4 and 5. Fig. 16 is a schematic view of an apparatus for the growth of a crystal, comprising the cylindrical body of the present invention, connected with an As reservoir. Fig. 17 is a schematic view showing growth striations of a crystal obtained in Example 7. Fig. 18 is a schematic view showing growth striations of a crystal obtained in Example 9. Fig. 19 is a graph showing radial distributions of dislocation density in wafers cut out of crystals obtained in Examples 7 and 9. Fig. 20 is a schematic view of an apparatus for the growth of a crystal, comprising the cylindrical body of the present invention, connected with a reservoir of a Group V element raw material. The inventors have made various efforts to improve a method for the growth of a single crystal by the LEC method and, consequently, have found a means for preventing the solid-liquid interface from becoming concave at the periphery and realizing good controllability of the diameter. The present invention is accomplished based on this finding. The specified constructions of the invention will be summarized below: (1) A method for the growth of a single crystal, which method comprises pulling a crystal out of a raw material melt by the Liquid Encapsulated Czochralski method, characterized in that the end of a cylindrical body having an inner diameter at said end larger than a predetermined diameter of a straight part of the growing crystal is immersed in the raw material melt or liquid encapsulant and the crystal is pulled while preventing the shape of the solid-liquid interface at the periphery of the growing crystal from becoming concave by controlling the relative rotation rate of the cylindrical body with respect to a crucible holding the raw material melt or the growing crystal. (2) The method in the above (1), wherein said end of the cylindrical body has an inner diameter larger by 5 to 30 mm, preferably 5 to 20 mm, than the predetermined diameter of the straight part of the growing crystal. (3) The method in the above (1) or (2), wherein said end of the cylindrical body immersed in the liquid encapsulant has a uniform diameter. (4) The method in any one of the above (1) to (3), wherein the depth that the end of the cylindrical body is immersed in the raw material melt or the liquid encapsulant remains constant during growth of the single crystal. (5) The method in any one of the above (1) to (4), wherein the relative rotation rate of the cylindrical body and an upper pulling rod is controlled to control the diameter of the growing crystal. (6) The method in any one of the above (1) to (5) wherein, in place of the cylindrical body, a casing having a cross-sectional shape as the habit of the growing crystal is used. (7) The method in any one of the above (1) to (6), wherein in the growth of a crystal for cutting a wafer in a direction not perpendicular to the growth axis, a casing having an oval shape in cross-section is used in place of the cylindrical body. (8) The method in any one of the above (1) to (7), wherein the revolution of the cylindrical body is stopped and the growing crystal is pulled up. (9) The method in any one of the above (1) to (7), wherein the growing crystal is pulled up while rotating the cylindrical body and pulling rod as one body. (10) The method in any one of the above (1) to (7), wherein the growing crystal is pulled up while rotating the cylindrical body with a rotation rate different from that of the pulling rod and crucible. (11) The method in any one of the above (1) to (10), wherein the cylindrical body is heated. (12) The method in any one of the above (1) to (11), wherein the upper end of the cylindrical body is closed and a vapour pressure of a volatile element constituting the growing crystal is applied to the cylindrical body. (13) The method in any one of the above (1) to (5), wherein said end of the cylindrical body has an inner diameter larger by 5 to 30 mm, preferably 5 to 20 mm, than the predetermined diameter of the straight part of the growing crystal, the growing crystal is rotated with a relative rotation rate of 0 to 5 rpm, preferably 0 to 3 rpm, with respect to the cylindrical body, and the cylindrical body is rotated with a relative rotation rate of at least 5 rpm, preferably 10 to 30 rpm, with respect to the crucible, whereby a single crystal is pulled upward while preventing the solid-liquid interface at the periphery of the growing crystal from becoming concave. (14) The method in the above (13), wherein the distance from the raw material melt surface to said end of the cylindrical body immersed in the liquid encapsulant is at most 30 mm, preferably at most 10 mm. (15) The method in any one of the above (1) to (14), wherein the single crystal is a semiconductor single crystal selected from Group IV elements, Group III-V compound semiconductors, Group II-VI compound semiconductors or an oxide single crystal. (16) An apparatus for the growth of a single crystal wherein a crystal is pulled out of a raw material melt by the Liquid Encapsulated Czochralski method, the apparatus comprising a cylindrical body for immersion into the raw material melt or a liquid encapsulant, wherein the immersion end of the cylindrical body has an inner diameter larger than a predetermined diameter of a straight part of the growing crystal, a crucible for holding the raw material melt, the crucible being supported by a lower shaft so as to enable rotation and vertical movement of the crucible, an upper pulling rod having a lower end for supporting a seed crystal so as to enable rotation and vertical movement of the seed crystal, and means for controlling the rotation rates and vertical moving rates of the lower shaft and upper pulling rod in accordance with changes in the shape of the solid-liquid interface. (17) The apparatus in the above (16), wherein the end of the cylindrical body to be immersed in the raw material melt or the liquid encapsulant has a uniform diameter. (18) The apparatus in the above (16) or (17), wherein the weight and shape of the cylindrical body is controlled in such a manner that the cylindrical body is floated on the raw material melt to satisfy the immersion condition. (19) The apparatus in any one of the above (16) to (18), wherein the cylindrical body is supported so as to be rotatable with the pulling rod as one body. (20) The apparatus in any one of the above (16) to (18), wherein the cylindrical body is supported so as to be rotatable independently of the lower shaft and upper pulling rod. (21) The apparatus in the above (16) or (17), wherein the cylindrical body is fixed to a non-movable part of the growth apparatus. (22) The apparatus in any one of the above (16) to (21), wherein, in place of the cylindrical body, a casing having a cross-sectional shape as the habit of the growing crystal is used. (23) The apparatus in any one of the above (16) to (22), wherein, in the growth of a crystal for cutting a wafer in a direction not perpendicular to the growth axis, a casing having an oval shape in cross section is used in place of the cylindrical body. (24) The apparatus in any one of the above (16) to (23), further comprising means for heating the cylindrical body. (25) The apparatus in any one of the above (16) to (24), wherein, as the cylindrical body, there is used a cylindrical body whose upper end is closed, and wherein a reservoir holding a volatile element constituting the growing crystal is arranged to be connected with the cylindrical body in such a manner that the vapour pressure of a volatile element in the cylindrical body can be controlled by controlling heater power of the reservoir. (26) The method in any one of the above (1) to (15), wherein the liquid encapsulant is B 2 O 3 . The inventors have investigated the convection of a raw material melt 3 when a single crystal 4 is grown by the LEC method and, consequently, have found that there is a natural convection that rises near the side wall of a crucible 1 and flows towards the growing crystal 4 and a forced convection that whirls near the solid-liquid interface with due to rotation of the crystal, as shown by arrows in Fig. 4. The melt temperature in the vicinity of the outer periphery of the solid-liquid interface is raised by these convections to render the periphery part of the solid-liquid interface concave to the melt. The present invention has succeeded in preventing the periphery part of the solid-liquid interface from local temperature rising and preventing the solid-liquid interface from becoming concave by arranging a cylindrical body 2 round a growing crystal 4 and immersing the end thereof in a raw material melt 3, as shown in Fig. 2, or a liquid encapsulant 5, as shown in Fig. 3, thereby cutting off the natural convection near the surface of the raw material melt and extending the flow of the melt at a high temperature outside the growing crystal by a forced convection by the cylindrical body. In the present invention, when crystal growth is carried out by immersing a cylindrical body in a raw material melt, the diameter of the growing crystal approaches the inner diameter of the cylindrical body and a meniscus formed between the growing crystal and the raw material melt is subject to a force from the cylindrical body, thus resulting in an effect of suppressing fluctuation of the diameter of the growing crystal. Since this force is changed by the relative rotation rate of the cylindrical body and growing crystal, however, it is desired to control the rotation rate of the cylindrical body and/or growing crystal so that the above described effect can be optimized. Furthermore, when using a crucible with a large diameter, in general, it is difficult to control the diameter of the growing crystal, but according to the method of the present invention, control of the diameter is rendered possible even if a crucible with a large diameter is used for high productivity of crystal growth. The immersion depth of the cylindrical body is not so important, since the effects of the cylindrical body according to the present invention in the case of immersing the end of the cylindrical body in the raw material melt are not affected by the immersion depth in the practical range, but the inner diameter of the cylindrical body should preferably be adjusted to larger by 5 to 30 mm, more preferably 5 to 20 mm than the predetermined diameter of staight part of the growing crystal. In the present invention, when a liquid encapsulant 5 is placed on a raw material melt 3, a cylindrical body 2 similar to that of Fig. 1 is immersed in the raw material melt 3 and a seed crystal fitted to an upper pulling rod (not shown) is immersed in the raw material melt 3, subjected to growth of a crystal and pulled upward to a straight part, as shown in Fig. 2, the thickness of the liquid encapsulant 5 in the cylindrical body 2 becomes considerably thicker than at the initial state, but the thickness of the outside liquid encapsulant is not changed, as shown in Fig. 2, resulting in a large difference in thickness of the liquid encapsulant between the inside and outside, and the surface of the raw material melt outside the cylindrical body is higher than the surface of the raw material melt inside the cylindrical body due to pressure difference between inside and ouside the cylindrical body. Consequently, a wall of the raw material melt at a high temperature, having a high thermal conductivity, is formed outside the cylindrical body and above the solid-liquid interface to further improve the temperature stability near the solid-liquid interface. Since the thickness of the liquid encapsulant can be made considerably thicker inside the cylindrical body independently of the diameter of a crucible when the straight part is pulled upward according to the present invention, furthermore, evaporation of the volatile element from the surface of the growing crystal can be prevented in a similar manner to the foregoing FEC method. Consequently, the temperature gradient near the solid-liquid interface can be decreased and the thermal strain in the crystal can largely be decreased. Even under such a state, there is no problem on control of the diameter of the growing crystal according to the method of the present invention, as described above, and accordingly, it is rendered possible to produce a single crystal excellent in crystallinity. When the cylindrical body is heated, the liquid encapsulant inside the cylindrical body and/or the pulled crystal can well be kept warm to decrease the temperature gradient near the solid-liquid interface and accordingly, so the same effects as described above can be expected. When the lower end of the cylindrical body is slightly bent inward to prevent the natural convection outside the cylindrical body from taking a roundabout way inside the cylindrical body, thus resulting in a large cutting off effect of such a natural convection. For another preferred embodiment of the present invention using a liquid encapsulant, moreover, the invenotors have made detailed study on a natural convection of a raw material melt and a forced convection caused by rotation of a growing crystal, when the single crystal is grown while rotating the growing crystal and a crucible by the LEC method of the prior art, and consequently, it is found that concerning the flows of the raw material melt and liquid encapsulant, a convection (natural convection) due to the vertical temperature gradient in the crucible, a convection due to rotation of the crucible and a convection due to rotation of the growing crystal are interacted each other and that the liquid encapsulant is rotated with a rotation rate as similar to that of the crucible as approaching it and a rotation rate as similar to that of the growing crystal as approaching it, but is strongly affected by the rotattion of the crucible, since the crucible is contacted with the liquid encapsulant at a larger area. As a resut, it is considered that in the raw material melt 3, the natural convection rising near the side wall of the crucible 1 and flowing toward the growing crystal 4 is dominant as shown by arrows in Fig. 5 and the forced convection caused by rotation of the growing crystal is restricted below the solid-liquid interface, since the rotation of the crucible and that of the liquid encapsulant having a larger influence more affect than the rotation of the growing crystal. Accordingly, the melt temperature near the periphery of the solid-liquid interface becomes higher to render concave the solid-liquid interface at the periphery of the crystal. The inventors have noted that a liquid encapsulant 5 such as B 2 O 3 has a larger viscosity and reached the present invention, in which the lower end of a cylindrical body 2 arranged round a growing crystal 4 is immersed in the liquid encapsulant 5 as shown in Fig. 3, and such an extent that the liquid encapsulant is affected by rotation of the crucible is moderated by (1) fixing the cylindrical body to a non-movable part in a growth apparatus, (2) rotating the cylindrical body with the growing crystal as one body or (3) rotating the cylindrical body independently of the growing crystal and crucible, whereby to suppress a natural convection of the raw material melt in the vicinity of the solid-liquid interface, to enlarge the range of a forced convection in the vicinity of the solid-liquid interface due to rotation of the growing crystal and to prevent the periphery of the solid-liquid interface from becoming concave. That is, in the present invention, a natural convection near the surface of a raw material melt is weakened to enlarge the range of a forced convection near the solid-liquid interface due to rotation of a growing crystal, preferably by choosing 1 ○ an inner diameter of a cylindrical body to a diameter of a straight part of a growing crystal (an inner diameter of 5 to 30 mm larger than the diameter of the straight drum part), 2 ○ a depth of a liquid encapsulant during growth of a straight part, 3 ○ an immersion depth in a liquid encapsulant of a cylindrical body and 4 ○ a rotating direction and rotation rate of a cylindrical body to rotations of a crucible and growing crystal, so that the influence of rotation of the crucible upon rotation of the liquid encapsulant may be suppressed. The above described factors to be controlled are preferably selected from the following ranges to control the convection of the raw material melt and prevent the solid-liquid interface from becoming concave, so that polycrystallization may be prevented and a high quality single crystal with a small dislocation density may be pulled. Namely, these effects can be obtained by adjusting the inner diameter of a cylindrical body to larger by 5 to 30 mm, preferably 5 to 20 mm than the predetermined diameter of straight drum part of the growing crystal, the distance of from the raw material melt to the end of the cylindrical body immersed in the liquid encapsulant to at most 30 mm, preferably at most 10 mm, the rotation rate of the crucible to at least 5 rpm, preferably 10 to 30 rpm, the relative rotation rate of the growing crystal, i.e. pulling rod to the cylindrical body to 0 to 5 rpm, preferably 0 to 3 rpm and the relative rotation rate of the cylindrical body to the crucible to at least 5 rpm, preferably 10 to 30 rpm. In the present invention, in general, arrangement of the above described cylindrical body can be carried out by methods comprising 1 ○ floating the cylindrical body on a raw material melt, 2 ○ fixing and supporting the cylindrical body independently of a crucible and growing crystal, 3 ○ rotating the cylindrical body with a pulling shaft as one body and 4 ○ rotating the cylindrical body independently of a crucible and growing crystal. The floating method 1 ○ has an advantage that the above described immersion depth can be maintained constant by controlling the weight and shape of a cylindrical body. On the other hand, since the cylindrical body is floated on the raw material melt and rotated with a liquid encapsulant, the cylindrical body cannot generate a forced convection. Thus, this method is effective only in the case of immersing the cylindrical body in the raw material melt. Even in the floating method, It is preferable to maintain the cylindrical body at the center by a stanchion, etc. so that the cylindrical body be in agreement with the central axis of a crucible. 2 ○ In the method of fixing and supporting the cylindrical body independently of a crucible and growing crystal, the upper end of the cylindrical body 2 is fixed to a non-movable part 8 such as insulator in a chamber, as shown in Fig. 6 (not in accordance with the present invention) or 8. In this case, it is required so as to maintain the immersion depth of the cylindrical body constant by raising the lower shaft 6 with the same rate as the decreasing rate of the melt depth. This method gives a larger convection controlling effect as compared with the above described method 1 ○. 3 ○ In the method of rotating the cylindrical body with a pulling rod as one body, the upper end of the cylindrical body 2 is supported by the upper pulling rod 7 and it is required to provide a mechanism for moving downward the cylindrical body 2 with pulling upward the growing crystal, as shown in Fig.7 (not in accordance with the present invention) or 9. When the cylindrical body 2 is rotated with the crystal, the effect of controlling the convection is larger near the solid-liquid interface. 4 ○ In the method of rotating the cylindrical body independently of a crucible and growing crystal, in particular, the cylindrical body is rotatably supported independently of the crucible and growing crystal and a desired convection can be obtained by suitably selecting the rotation rate the three. On the other hand, a single crystal with high quality can be obtained, even when the crystal is grown under the low the temperature gradient at the solid-liquid interface, using a cylindrical body 2 whose upper end is closed, to which a reservoir 17 for holding a volatile element 15 constituting the growing crystal 4 is connected to be gass-passable, by controlling the power of a heater (not shown) arranged round the reservoir and controlling the vapor pressure of the volatile element in the cylindrical body to prevent evaporation of the volatile element from the growing crystal, as shown in Fig. 16 or Fig. 20. In the present invention, as another means, an air-tight vessel can be used for covering the whole of a crucible, capable of applying a volatile element vapor by providing a valve mechanism, but in a preferable embodiment, control of the vapor pressure can be carried out without needing such a large sized air-tight vessel by providing the closed cylindrical body with a relatively simple structure such as the above described reservoir. The shape of the cylindrical body used in the present invention is generally circular in cross section, but in the growth of a crystal with a strong crystal habit, a casing having a cross-sectional shape as the habit of the growing crystal is used and in the growth of a crystal for cutting a wafer in a direction not perpendicular to the growth axis, a casing having an oval shape in cross section is used. The cylindrical body used in the present invention can be made of carbon, PBN, quartz and the like. Advanatges of the Invention As illustrated above, according to the present invention, the growing crystal can be prevented from becoming concave at the periphery of the solid-liquid interface and from polycrystallization due to accumulation of dislocations. Furthermore, control of the diameter of the growing crystal can well be carried out and the yield of the crystal can largely be improved. The following examples are given in order to illustrate the invention in detail without limiting the same. Example 1 GaAs single crystal was grown floating a cylindrical body on a raw material by the LEC method. When a predetermined diameter of straight part of the growing crystal was adjusted to 110 mm and the cylindrical body made of pBN, having an inner diameter of 120 mm and a thickness of 1 mm was floated on the raw material melt, there was obtained an immersion depth of 10 mm in the raw material melt. 10 kg of GaAs raw material and 500 g of B 2 O 3 were charged in a crucible of pBN, having a susceptor of carbon and an inner diameter of 200 mm, and subjected to growth of the single crystal by adjusting the rotation rate of the crucible during growth of the straight part to 10 rpm, the rotation rate of a seed crystal to 2 rpm in the opposite direction and the pulling-up rate of the same to 5 mm/hr. The thus resulting crystal was a single crystal having a length of 200 mm and a maximum diameter of 110 mm. When the crystal was sliced along the growth axis and subjected to observation of the growth striations revealed by photo A/B etching, i.e. immersing the resulting wafer in an etching solution containing 40 ml of 50 % HF, 100 g of CrO 3 and 520 ml of H 2 O and effecting etching for 10 minutes while irradiating a light in order to investigate the shape of the solid-liquid interface of the single crystal, they were substantially flat at the periphery part as shown in Fig. 12, from which it was apparent that the periphery part of the solid-liquid interface was prevented from becoming concave. In Fig. 12, C designates the central line. Example 2 GaAs single crystal was grown in an analogous manner to Example 1 except rotating the cylindrical body 2 with the same rotation rate the pulled crystal 4 by the upper pulling rod 7 as shown in Fig. 7. The upper pulling rod, whose cross section was not circular, was set in a hole having the same shape as the upper pulling rod in cross section, made on the upper part of the cylindrical body so that the rotation of the upper pulling rod was transmitted to the cylindrical body. The cylindrical body was supported by an insulator so that it was not vertically moved. The immersion depth of the cylindrical body was maintained constant by moving upward the lower shaft at the same rate as the decreasing rate of the depth of the raw material melt with growth of the crystal. The thus resulting crystal was a single crystal having a length of 210 mm and a maximum diameter of 108 mm. When the growth striations were observed in the same manner as Example 1, there was a tendency of becoming convex at the periphery part of the solid-liquid interface, as shown in Fig. 13, which taught the effect of a forced convection by the cylindrical body. Comparative Example 1 GaAs single crystal was grown in an analogous manner to Example 1 except omitting the cylindrical body. The thus resulting crystal was a single crystal having a length of 200 mm and a maximum diameter of 111 mm. When the gowth rings were observed in the same manner as Example 1, there were a remarkable tendency of becoming concave at the periphery part of the solid-liquid interface and polycrystallization from a position marked by an arrow P, as shown in Fig. 14 Comparative Example 2 When the inner diameter of the cylindrical body was rendered smaller than the predetermined diameter + 5 mm, the diameter of the growing crystal did not reach the predetermined diameter so readily. On the other hand, when the immersion depth of the cylindrical body in the raw material melt was adjusted to 10 mm and the inner diameter thereof was adjusted to larger by + 40 mm than the predetermined diameter, there were a tendency of becoming concave at the periphery part of the solid-liquid interface similarly to Comparative Example 1 and polycrystallization similarly to Comparative Example 1. Example 3 GaAs single crystal was grown using the same apparatus as that of Example 1 except fixing the cylindrical body 2 to an insulator 8 so that it was not rotated, as shown in Fig. 6. The rotation rate of the crucible was adjusted to 10 rpm and the rotation rate of the growing crystal was adjusted to 2 rpm. The thus resulting crystal was a single crystal having a length of 200 mm and a maximum diameter of 110 mm. When the growth striations were observed in the same manner as Example 1, the shape of the periphery part of the solid-liquid interface was found to be the order between those of Examples 1 and 2. A wafer (100) was quarried out of the resulting crystal, etched with melted KOH and subjected to examination of radial distribution of the dislocation density in plane to obtain results as shown in Fig. 15 (Curve marked O). The average value of the dislocation density in plane was 57300 cm -2 . Example 4 Growth of a crystal was carried out in an analogous manner to Example 3 except increasing twice the quantity of B 2 O 3 from 500 g to 1000 g. The thickness of B 2 O 3 in the cylindrical body was about two times as large as that of Example 3 during crystal growth of the straight part. The thus resulting crystal was a single crystal having a length of 190 mm and a maximum diameter of 113 mm. The average diameter thereof was somewhat large because of rapid growth of the cone part and fluctuation of the diameter was on the same level as in Example 1, resulting in very good controllability of the diameter. A wafer (100) was cut out of the resulting crystal, etched with molten KOH and subjected to investigation of radial distribution of the dislocation density in a wafer to obtain results as shown in Fig. 15 (Curve marked □) in comparison with Example 3. With increase of the thickness of B 2 O 3 , the temperature gradient in the direction of the growth axis was decreased and consequently, the dislocation could be decreased. The average value of the dislocation density in plane was 29700 cm -2 , less than that of Example 3. Example 5 Using a cylindrical body 2 whose upper end was closed as shown in Fig. 16, GaAs single crystal 4 was grown in an analogous manner to Example 3 except applying As vapor to the cylindrical body 2 by connecting reservoir 17 of As 15 thereto. The temperature gradient in the direction of the growth axis in B 2 O 3 before growth of the crystal could be suppressed to small, i.e. about 30 °C/cm because of the growth under As vapor pressure, as compared with about 100°C/cm in Example 3. The thus resulting crystal was a single crystal having a length of 220 mm and a maximum diameter of 107 mm. When GaAs single crystal was grown under a low temperature gradient, in general, As element was evaporated, but the GaAs single crystal obtained herein had a surface with a metallic lustre and there was found no evaporation of As. Because of the low temperature gradient, the solid-liquid interface at the central part became convex to a small extent, but the periphery part of the solid-liquid interface was hardly changed from Example 3. A wafer (100) was cut out of the resulting crystal, etched with molten KOH and subjected to investigation of radial distribution of the dislocation density in a wafer to obtain results as shown in Fig. 15 (Curve marked Δ). The average value of the dislocation density in plane was 7420 cm -2 , which was further decreased from that of Example 4. Comparative Example 3 In Example 3, the rotation rate of the crucible was maintained constant at 10 rpm and that of the crystal was changed to investigate the effect of the relative rotation rate of the crystal and cylindrical body on controllability of the diameter. Namely, when the rotation rate of the crystal was increased from 2 rpm to 5 rpm in opposite direction to revolution of the crucible, a force the meniscus took from the cylindrical body was too large and a part of the meniscus fell during growth of the crystal. When the rotation of the crystal was stopped, on the other hand, the force the meniscus took was too small and the crystal was grown until the diameter of the crystal was brought into contact with the cylindrical body. Falling of the meniscus is a phenomenon such that a part of the crystal is cut from the melt to form a scoop on the growing crystal. Example 6 In Example 3, using a cylindrical body of pBN, the outer surface of which was coated with a carbon heater, the cylindrical body was heated and the rotation rate of the crystal was adjusted to 5 rpm to obtain similar results to Comparative Example 3. Even if the crystal growth was carried out while stopping the rotation thereof, the diameter of the crystal was not changed and there was found no contact with the cylindrical body. Example 7 GaAs single crystal was grown by the LEC method using a growth apparatus as shown in Fig. 8, in which the cylindrical body 2 was fixed to an insulator 8. When a predetermined diameter of straight part of the growing crystal was adjusted to 110 mm and the cylindrical body made of pBN, having an inner diameter of 120 mm and a thickness of 1 mm was used. 10 kg of GaAs raw material and 800 g of a liquid encapsulant, B 2 O 3 were charged in a crucible of pBN, having an inner diameter of 200 mm, and subjected to growth of the single crystal, with a thickness of the liquid encapsulant, B 2 O 3 of about 23 mm during growth of the straight part, by adjusting the rotation rate of the crucible during growth of the straight part to 10 rpm, the rotation rate of a seed crystal to 2 rpm and the pulling-up rate of the same to 5 mm/hr. The end of the cylindrical body was arranged to be in the liquid encapsulant apart from the raw material melt by 5 mm. The thus resulting crystal was a single crystal having a length of 210 mm and a mean diameter of 108 mm. When the crystal was sliced along the growth axis and subjected to observation of the growth rings by photo A/B etching, i.e. immersing the resulting wafer in an etching solution containing 40 ml of 50 % HF, 100 g of CrO 3 and 520 ml of H 2 O and effecting etching for 10 minutes while irradiating a light in order to investigate the shape of the solid-liquid interface of the single crystal, they were substantially flat at the periphery part as shown in Fig. 17, from which it was apparent that the periphery part of the solid-liquid interface was prevented from becoming concave. A wafer (100) was cut out of the resulting crystal, etched with molten KOH and subjected to investigation of radial distribution of the dislocation density in a wafer to obtain results as shown in Fig. 19 (Curve marked  ). The average value of the dislocation density in plane was 58800 cm -2 . Example 8 GaAs single crystal was grown in an analogous manner to Example 7 except rotating the cylindrical body 2 with the same rotation rate of the growing crystal 4 as shown in Fig. 9. The upper pulling rod, whose cross section was not circular, was set in a hole having the same shape as the upper pulling rod in cross section, made on the upper part of the cylindrical body so that the rotation of the upper pulling rod was transmitted to the cylindrical body. The cylindrical body was supported by an insulator so that it was not vertically moved. The relationship of the end of the cylindrical body and the surface of the raw material melt was maintained constant by moving upward the lower shaft at the same rate as the decreasing rate of the depth of the raw material melt with growth of the crystal. The thus resulting crystal was a single crystal having a length of 200 mm and a mean diameter of 110 mm. When the growth rings were observed in the same manner as Example 7, there was a tendency of becoming convex at the periphery part of the solid-liquid interface, as shown in Fig. 18. Comparative Example 4 GaAs single crystal was grown in an analogous manner to Example 7 except omitting the cylindrical body. The thus resulting crystal was a single crystal having a length of 200 mm and a maximum diameter of 111 mm. When the gowth striations were observed in the same manner as Example 7, there were a remarkable tendency of becoming concave at the periphery part of the solid-liquid interface and polycrystallization from a position marked by an arrow P, as shown in Fig. 14 Comparative Example 5 When using a cylindrical body whose inner diameter was the predetermined diameter of the growing crystal + 5 mm in Example 7, the crystal was substantially grown to the limit of the cylindrical body due to fluctuation of the diameter of the crystal and brought into contact with the cylindrical body. Thus, the crystal growth could not be continued. When using a cylindrical body whose inner diameter was the predetermined diameter of the growing crystal + 40 mm, there was found a tendency of becoming concave at the periphery of the solid-liquid interface and polycrystallization occurred. Moreover, when the cylindrical body was fixed to a heat insulator and the crucible and crystal were rotated respectively at 5 rpm and 2 rpm, the tendency of becoming concave at the periphery of the solid-liquid interface was somewhat improved, but there was still remained a tendency of becoming concave. Moreover, when the cylindrical body was fixed to a heat insulator and the crucible and crystal were rotated respectively at 10 rpm and 5 rpm, the tendency of becoming concave at the periphery of the solid-liquid interface was somewhat improved, but there was still remained a tendency of becoming concave. Example 9 Using a cylindrical body 2 whose upper end was closed as shown in Fig. 20, GaAs single crystal 4 was grown in an analogous manner to Example 7 except applying As vapor to the cylindrical body 2 by connecting reservoir 17 of As 15 thereto. The temperature gradient in the direction of the growth axis in B 2 O 3 before growth of the crystal could be suppressed to small, i.e. about 30 °C/cm because of the growth under As vapor pressure, as compared with about 100 °C/cm in Example 7. The thus resulting crystal was a single crystal having a length of 215 mm and a mean diameter of 107 mm. When GaAs single crystal was grown under a low temperature gradient, in general, As element was evaporated, but the GaAs single crystal obtained herein had a surface with a metallic lustre and there was found no evaporation of As. Because of the low temperature gradient, the solid-liquid interface at the central part became convex to a small extent, but the periphery part of the solid-liquid interface was hardly changed from Example 7. A wafer (100) was cut out of the resulting crystal, etched with molten KOH and subjected to investigation of radial distribution of the dislocation density in a wafer to obtain results as shown in Fig. 19 (Curve marked ▴ ). The average value of the dislocation density in plane was 7750 cm -2 . Example 10 In Example 7, using a cylindrical body of pBN, the outer surface of which was coated with a carbon heater, the cylindrical body was heated and the other conditions were maintained similar to Example 7. Consequently, the tendency of becoming concave at the periphery of the solid-liquid interface was more improved than in Example 7 and there was found a tendency of becoming convex, similarly to Fig. 18. This effect is probably due to that heat flow from the crystal to the side is suppressed by heating the cylindrical body.

Claims: A method for the growth of a single crystal, which method comprises pulling a crystal out of a raw material melt by the Liquid Encapsulated Czochralski method, characterized in that the end of a cylindrical body having an inner diameter at said end larger than a predetermined diameter of a straight part of the growing crystal is immersed in the raw material melt or liquid encapsulant and the crystal is pulled while preventing the shape of the solid-liquid interface at the periphery of the growing crystal from becoming concave by controlling the relative rotation rate of the cylindrical body with respect to a crucible holding the raw material melt or the growing crystal. A method as claimed in Claim 1, wherein said end of the cylindrical body has an inner diameter larger by 5 to 30 mm, preferably 5 to 20 mm, than the predetermined diameter of 'the straight part of the growing crystal. A method as claimed in Claim 1 or claim 2, wherein said end of the cylindrical body immersed in the liquid encapsulant has a uniform diameter. A method as claimed in any one of Claims 1 to 3, wherein the depth that the end of the cylindrical body is immersed in the raw material melt or the liquid encapsulant remains constant during growth of the single crystal. A method as claimed in any one of Claims 1 to 4, wherein the relative rotation rate of the cylindrical body and an upper pulling rod is controlled to control the diameter of the growing crystal. A method as claimed in any one of Claims 1 to 5 wherein, in place of the cylindrical body, a casing having a cross-sectional shape as the habit of the growing crystal is used. A method as claimed in any one of Claims 1 to 6, wherein in the growth of a crystal for cutting a wafer in a direction not perpendicular to the growth axis, a casing having an oval shape in cross-section is used in place of the cylindrical body. A method as claimed in any one of Claims 1 to 7, wherein the revolution of the cylindrical body is stopped and the growing crystal is pulled up. A method as claimed in any one of Claims 1 to 7, wherein the growing crystal is pulled up while rotating the cylindrical body and pulling rod as one body. A method as claimed in any one of Claims 1 to 7, wherein the growing crystal is pulled up while rotating the cylindrical body with a rotation rate different from that of the pulling rod and crucible. A method as claimed in any one of Claims 1 to 10, wherein the cylindrical body is heated. A method as claimed in any one of Claims 1 to 11, wherein the upper end of the cylindrical body is closed and a vapour pressure of a volatile element constituting the growing crystal is applied to the cylindrical body. A method as claimed in any one of Claims 1 to 5, wherein said end of the cylindrical body has an inner diameter larger by 5 to 30 mm, preferably 5 to 20 mm, than the predetermined diameter of the straight part of the growing crystal, the growing crystal is rotated with a relative rotation rate of 0 to 5 rpm, preferably 0 to 3 rpm, with respect to the cylindrical body, and the cylindrical body is rotated with a relative rotation rate of at least 5 rpm, preferably 10 to 30 rpm, with respect to the crucible, whereby a single crystal is pulled upward while preventing the solid-liquid interface at the periphery of the growing crystal from becoming concave. A method as claimed in Claim 13, wherein the distance from the raw material melt surface to said end of the cylindrical body immersed in the liquid encapsulant is at most 30 mm, preferably at most 10 mm. A method as claimed in any one of claims 1 to 14, wherein the single crystal is a semiconductor single crystal selected from Group IV elements, Group III-V compound semiconductors, Group II-VI compound semiconductors or an oxide single crystal. An apparatus for the growth of a single crystal wherein a crystal is pulled out of a raw material melt by the Liquid Encapsulated Czochralski method, the apparatus comprising a cylindrical body for immersion into the raw material melt or a liquid encapsulant, wherein the immersion end of the cylindrical body has an inner diameter larger than a predetermined diameter of a straight part of the growing crystal, a crucible for holding the raw material melt, the crucible being supported by a lower shaft so as to enable rotation and vertical movement of the crucible, an upper pulling rod having a lower end for supporting a seed crystal so as to enable rotation and vertical movement of the seed crystal, and means for controlling the rotation rates and vertical moving rates of the lower shaft and upper pulling rod in accordance with changes in the shape of the solid-liquid interface. An apparatus as claimed in Claim 16, wherein the end of the cylindrical body to be immersed in the raw material melt or the liquid encapsulant has a uniform diameter. An apparatus as claimed in Claim 16 or Claim 17, wherein the weight and shape of the cylindrical body is controlled in such a manner that the cylindrical body is floated on the raw material melt to satisfy the immersion condition. An apparatus as claimed in any one of Claims 16 to 18, wherein the cylindrical body is supported so as to be rotatable with the pulling rod as one body. An apparatus as claimed in any one of Claims 16 to 18, wherein the cylindrical body is supported so as to be rotatable independently of the lower shaft and upper pulling rod. An apparatus as claimed in Claim 16 or Claim 17, wherein the cylindrical body is fixed to a non-movable part of the growth apparatus. An apparatus as claimed in any one of Claims 16 to 21, wherein, in place of the cylindrical body, a casing having a cross-sectional shape as the habit of the growing crystal is used. An apparatus as claimed in any one of Claims 16 to 22, wherein, in the growth of a crystal for cutting a wafer in a direction not perpendicular to the growth axis, a casing having an oval shape in cross section is used in place of the cylindrical body. An apparatus as claimed in any one of Claims 16 to 23, further comprising means for heating the cylindrical body. An apparatus as claimed in any one of Claims 16 to 24, wherein, as the cylindrical body, there is used a cylindrical body whose upper end is closed, and wherein a reservoir holding a volatile element constituting the growing crystal is arranged to be connected with the cylindrical body in such a manner that the vapour pressure of a volatile element in the cylindrical body can be controlled by controlling heater power of the reservoir. A method as claimed in any one of Claims 1 to 15, wherein the liquid encapsulant is B 2 O 3 .

Inventors: HASHIO KATSUSHI, SAWADA SHIN-ICHI, TATSUMI MASAMI, HASHIO, KATSUSHI, SAWADA, SHIN-ICHI, TATSUMI, MASAMI
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LIMITED
Application year: 1996
Main classification: C30B15
IPC codes: C30B15