Cystine-silicone polymers and their use for treating keratin substrates

Abstract: A copolymer comprising cystine, or a derivative thereof, bonded to a silicon-containing group, wherein the silicon containing group is bonded to one or more other silicon-containing groups by siloxane groups. This polymer is useful for treating keratin-containing substrates.

Description: The invention relates to cystine-silicone polymers and their use for treating keratin substrates, such as hair, nails, skin and wool. The invention also relates to a method of making cystine-silicone polymers. The keratin in such substrates are known to be stabilised by disulphide bonds between polypeptide chains, in the form of cystine residues. Cystine residues can be reduced to cysteine residues by the use of reagents such as ammonium thioglycollate, sodium sulphite/bisulphite, thiolactic acid, glyceryl monothioglycollate, cysteine and cysteamine. Disulphide bonds can be reformed by oxidation using reagents such as hydrogen peroxide, or sodium bromate. Such reduction/oxidation processes form the basis of the commercially important cold permanent-wave treatments for hair in which disulphide bonds are broken and reformed in a new configuration. Cysteine treatment of wool has been claimed to be useful in imparting permanent-press characteristics to machine washable fabrics, based on a similar mechanism. In the reduction/oxidation treatment applied to hair and wool keratin some of the cystine and cysteine residues are converted to cysteic acid, resulting in a loss of dry strength and, more particularly, wet strength of the fibres. Similar damage occurs in oxidative bleaching processes resulting in a general deterioration in the "condition" of the hair or wool. Temporary "conditioning" of the keratin fibre can be achieved using, for example, long chain fatty quaternium compounds, cationic polymers, or silicones to treat the surface of the fibres. More-permanent conditioning is possible when the conditioning agent is capable of forming covalent bonds with the hair keratin. Examples of such agents are partially hydrolysed soluble keratins which contain cystine/cysteine residues in their molecules and are capable of forming disulphide links to the hair when included in a reduction/oxidation treatment. Certain high molecular weight soluble keratin polypeptides can be considered to be polyfunctional in terms of thiol groups; such polypeptides are potentially capable of producing multiple disulphide bonding to hair and a consequent strengthening effect. However, such behaviour is largely restricted to the surface of the cuticle due to lack of penetration into the fibres. Conversely low molecular weight hydrolysed keratin may be capable of penetration through the cuticle into the cortex, but even with high cystine content will no longer be multifunctional or capable of a strengthening effect. For example, a keratin hydrolysate with a 5% cystine content and an average molecular weight of 100,000 Daltons (100,000 g mol -1 ) will have, on average, approximately twenty ½ cystine residues per polypeptide molecule, whereas for the same keratin protein with an average molecular weight of 1000 Daltons (1000 g mol -1 ) only 20% of the polypeptides will have even one ½ cystine residue. It will be apparent from the foregoing that a conditioning agent for keratin substrates which is capable of penetrating into the fibres and, at the same time, is capable of producing multi-disulphide links to the keratin through a polymeric chain would offer advantages over existing treatments for strengthening and conditioning the keratin fibres, in addition to any surface conditioning benefits. We have now devised a new material which can be used as such a conditioning agent for keratin substrates. Broadly, the invention provides a polymer comprising two or more units each made up of cystine, or a derivative thereof, bonded to a silicon-containing component containing at least one siloxane link. Thus, the invention provides a polymer comprising cystine, or a derivative thereof, bonded to a silicon-containing component, the silicon-containing group being bonded to one or more other silicon-containing groups by siloxane groups. According to one aspect of the present invention, there is provided a polymer containing two or more units of formula: [-B-A-B'-] where A is HN-CH(COOR x )CH 2 -S-S-CH 2 CH(COOR y )NR z , R x and R y are the same or different and are hydrogen or an alkyl group, R z is hydrogen or an amino modifying group, and B and B' represent silicon-containing groups; wherein the units are linked together by siloxane bonds, the groups B and B' are the same or different, the group B in each unit is the same as or different from the group B in any other unit, and the group B' in each unit is the same as or different from the group B' in any other unit, wherein a terminal group of the polymer is cystine, cysteine or the Bunté salt of cystine, a derivative of cystine wherein one of the amino groups or one or both of the carboxyl groups have been chemically modified, or a silicon-containing group. JP-A-5339132 describes a method for treating hair with a hair cosmetic in which the hair is treated with a first agent containing inter alia a cysteine compound and then treating the hair with a second agent containing an epoxy-modified silicone. A polymer comprising two or more units each made up of cystine or a derivative thereof bonded to a silicon-containing component according to the invention, or containing units of the formula according to the invention would not inevitably result in situ from the method described. EP 0437099A describes thioglycolamide-functional siloxanes obtainable by reacting thioglycolic acid according to a particular formula with certain amine functional siloxanes, the general formula of thioglycolic acid not encompassing cystine, but cysteine. The products are described as being useful as a reducing agent in the perming or conditioning of hair. EP-B-0505854 describes a process for permanent setting of hair by the action of keratin-reducing setting compositions. The compositions include organopolysiloxanes which contain Bunté salt groups. The general formula of the organopolysiloxanes does not include two or more units each made up of cystine bonded to a silicon-containing component according to the invention, or containing units of the formula according to the invention nor would such a polymer inevitably result in hair in situ. The general formula of the prior Bunté salt does not encompass the Bunté salt of cystine. R z is hydrogen or an amino-modifying group. The amino modifying group may be, for example, R w CO, where R w is an alkyl group, or R w1 (R w2 )(R w3 )N + -CH 2 -CH(OH)-CH 2 -, where R w1 , R w2 and R w3 are the same or different alkyl groups. The polymers of the invention are polyfunctional in terms of cystine residues, can be produced with molecular weight distributions such that the lower molecular weight species are able to penetrate into keratin substrates and when they have been produced in solution are generally capable of further polymerisation on drying. In the cystine-silicone polymers of the invention, the silicone is covalently bonded to the amino groups of the amino acid cystine to form the unit [-B-A-B'-]. These "units" are further linked together by siloxane bonds to form a polymer. The groups B and B' may themselves contain one or more siloxane links. Additional and more significant condensation polymerisation generally occurs when a solution of the cystine-silicone polymer is concentrated by removal of solvent. It will be appreciated that the polymers of the invention will have a terminal group at the end of the polymer chain. This terminal group may be cystine, a derivative thereof (as defined below), cysteine, the Bunté salt of cystine or may be a silicon-containing group. The cystine component is preferably cystine itself, but may be a derivative of cystine in which one of the amino groups or one or both of the carboxyl groups have been chemically modified. The initial step in the production of cystine-silicone polymers of the invention is the reaction of a organofunctional silicone with the amino groups of cystine, or the cystine derivative. At least one, and preferably more than one, of the cystine amino groups must be reacted in this way. Suitable reactive groups on the silicone include epoxide, sulphonyl halide, acyl halide, anhydride and aldehyde groups, but other reactive groups may be used instead. The "silicone" component may be any compound which contains a siloxane group (Si-O-Si), or any silane capable of forming a siloxane in situ by condensation of silanol (Si-OH) groups, or any alkoxysilane or halosilane which hydrolyses to form a corresponding silanol and then condenses to form a siloxane group, provided that the silicone contains at least one silanol group, or group which hydrolyses to form a silanol group, in its structure. The second stage in the production of the cystine-silicone polymer is the joining up of the units to each other or to other silicon-containing units reactive herewith to form linking siloxane groups. Polymerisation of the product from reaction of the organofunctional silicone with cystine can be effected by condensation of silanol groups to form siloxane bonds. This polymerisation condensation reaction may follow the initial reaction of organofunctional silicone with cystine or may take place concurrently, depending upon the reaction conditions. Similarly, the degree of polymerisation may be controlled by selection of reaction conditions. The organofunctional silicone/silane reactant is preferably soluble in a solvent common to cystine for efficient reaction. Water or aqueous/alcohol solutions are generally preferred. In order to achieve the desired degree of reaction and cross-linking it is highly desirable to control carefully the conditions for reaction of the organofunctional silicone/silane with cystine. For reaction of the cystine amino groups to occur it is advantageous for the pH to be above pH7 and preferably within the pH range 8 to 11.5. Reaction may be carried out at ambient temperature, but an elevated temperature is preferred. The invention may be carried out at temperatures in the range 10 to 80°C, but more preferably a temperature of 40-80°C is used. The degree of polymerisation is influenced by solution concentration; higher concentration resulting in increased degree of condensation polymerisation. More complex polymers can be achieved by silanol condensation between the cystine-silicone polymers and other silanol-containing compounds such as dimethyl dihydroxy silane or its condensation products, silanol terminated polydimethyl siloxanes, or protein-silicone copolymers (as described in EP-A2-0540357); or by partial replacement of mono-organofunctional silanes by di-organofunctional silanes such as compounds IV and V set out below. Cystine may represent approximately 2% to 80% of the copolymer, but more preferably 20% to 70% by weight. The inclusion of the cystine-silicone polymer into cosmetic formulations can be at any desired level, but it is generally preferred to use from 0.1 to 5% w/w of the polymer. In one embodiment the organofunctional silanes have the structure: where: R' is a group containing an amino-reactive group capable of reacting with the amino group in the cystine or the cystine derivative. R'' and R''' are the same or different and are an alkyl group or an alkoxy group or OH. R'''' is hydrogen or an alkyl group. Examples of suitable organofunctional silanes containing an epoxy group are illustrated by I-III below. The organofunctional silanes IV and V discussed above are: where n = 1-50, preferably 30-40. where n = 1-50, preferably 12-25. The chemical structure of the cystine silicone polymers according to the invention are likely to be complicated, but can be illustrated by the general simplified structure VI indicated below. where: X is a link group resulting from the reaction of an amino group on the cystine or cystine derivative with an amino reactive group of the silicon-containing group; R, in the group A, is H or CH 2 CH 3 ; Y is H or or an amino-modifying group; R 1 to R 10 are the same or different, and are CH 3 , OH or Z, where Z is one of: or where R 11 to R 22 are the same or different and are CH 3 , OH or Z, and R 23 and R 24 are CH 3 or OH, and m is from 0 - 100 p is from 0 - 100 r is from 0 - 100 s is from 0 - 100 t is from 0 - 100 u is from 0 - 100 v is from 0 - 100 Values of r,s,t,u and v may be the same or different. At least one of the Groups R 1 to R 10 should contain at least one Z group containing an A group. The cystine-silicone polymers according to the invention as described above have been found to exhibit physical and chemical properties which make them valuable for cosmetic formulations used for conditioning hair, skin or nails and for textile applications in the treatment of wool. In order that the invention may be more fully understood the following examples are given by way of illustration only. Example 1 A cystine-silicone polymer was prepared by reaction of organofunctional silane I with cystine, according to the following procedure. 50g L-cystine was dispersed in 450g deionised water and the pH raised to 10 using 47% sodium hydroxide solution. The temperature was raised to 60°C and then 49.1g silane I was added over a period of 2 hours whilst stirring and maintaining the pH at 10 by addition of further sodium hydroxide, and maintaining the temperature at 60°C. After a further 4 hours the product was filtered to give a clear solution of the copolymer. The degree of modification of cystine amino groups was determined as 60% based on a modified formol titration procedure. Example 2 A reduced form (as the Bunté salt) of the cystine-silicone polymer was prepared as follows. 12gNa 2 SO 3 .7H 2 O was dissolved in 100g copolymer solution. The solution remained clear on reducing the pH to 7. Example 3 The molecular weight distributions of the reduced and non-reduced forms of the polymer were determined by size exclusion hplc using a GMPWXL column and polystyrene sulphonate molecular weight standards and compared with cysteine. The cysteine elution peak corresponded to an approximate molecular weight of 150 (150 g mol -1 ) (compared with actual value of 122 (122 g mol -1 )). The major peak for cystine-silicone polymer occurred at approx. 16,000 Daltons (16,000 g mol -1 ), with a smaller peak at approx. 1000 Daltons (1000 g mol -1 ). For the reduced polymer, the major peak occurred at approx. 1000 Daltons (1000 g mol -1 ) with a smaller peak at 16,000 Daltons (16,000 g mol -1 ). No peak or shoulder was observed corresponding to free cysteine. This data showed that a polymer had been produced containing disulphide links which could be broken using sulphite, a reducing agent commonly used in the cosmetic and textile industries. The reduced form of the copolymer contained a significant proportion of molecules small enough to penetrate into hair. Example 4 5% active solutions of polymer in 6% ammonium thioglycollate were prepared at pH 9.5. The solutions were clear and remained clear on lowering the pH to 5. Example 5 The cross-linking/polymerisation potential of the cystine-silicone polymer was demonstrated as follows. 1g of the polymer solution was weighed into a 250ml glass beaker and dried to a film in an oven at 60°C for 4 hours. The beaker was cooled in a dessicator and then 250ml of pH 10 buffer was added and stirred vigorously at 25°C until no further polymer dissolved (as evidenced by monitoring A 220 ). Only 12% of the polymer was soluble, indicating polymerisation had occurred. When cystine-silicone polymer in its sulphite-reduced form was tested in a similar way cross-linking similarly occurred, with only 50% of the polymer dissolving. Example 6 The potential for disulphide bond interchange with hair was demonstrated as follows. A set of 4 hairs was reduced with ammonium thioglycollate solution to achieve approximately 20%, 30%, 40% and 60% breakage, respectively, of the original disulphide bonds in the hair. This was determined by studies on the mechanical behaviour of the hair. Rinsing of the hair fibres, in their reduced state, with water at pH9 had a negligible effect on bond reformation. In contrast, when treated with a 2% active solution of cystine-silicone polymer, at pH 9, an increase in mechanical strength of the hair fibres equivalent to approximately 15% reformation of the original disulphide bonds in the hair was achieved. This indicates that the cystine-silicone polymer penetrates hair and undergoes disulphide interchange with the hair fibres in their reduced state. 2% active cystine-silicone polymer was included in a shampoo based on sodium lauryl ether sulphate and used to treat hair switches. The switches were treated with shampoo by rubbing the shampoo into the pre-wetted hair for one minute. The switches were then rinsed with lukewarm running water for 1 minute prior to assessment of wet compatability, which was markedly improved over that of the control switches. Hair switches were treated with 1% active cystine-silicone polymer and crosslinked by drying onto PTFE rollers. A tighter and shorter curl was produced compared to the control. Example 7 The potential for permanent setting of wool fabrics was demonstrated by treating wool fabrics with cystine-silicone polymer, then steam pressing the fabrics. After this treatment the fabrics showed improved setting characteristics over the untreated control fabrics. Whilst certain embodiments of the invention have been described above, it will be appreciated that modifications may be made.

Claims: A polymer comprising two or more units each made up of cystine, or a derivative thereof, bonded to a silicon-containing component, wherein the silicon-containing component contains at least one siloxane link. A polymer containing two or more units of formula: [-B-A-B'-] where A is HN-CH(COOR x )CH 2 -S-S-CH 2 CH(COOR y )NR z , R x and R y are the same or different and are hydrogen or an alkyl group, R z is hydrogen or an amino modifying group, and B and B' represent silicon-containing groups; wherein the units are linked together by siloxane bonds, the groups B and B' are the same or different, the group B in each unit is the same as or different from the group B in any other unit, and the group B' in each unit is the same as or different from the group B' in any other unit, wherein a terminal group of the polymer is cystine, cysteine or the Bunté salt of cystine, a derivative of cystine wherein one of the amino groups or one or both of the carboxyl groups have been chemically modified, or a silicon-containing group. A polymer according to claim 1 or 2, wherein the cystine or cystine derivative comprises 20 wt % to 70 wt % of the total weight of the polymer. A polymer according to claim 1, 2 or 3, which has the structure: where: X is a link group resulting from the reaction of an amino group on the cystine or cystine derivative with an amino reactive group on the silicon-containing group; A is HN-CH(COOR x )CH 2 -S-S-CH 2 CH(COOR y )NR z , R x and R y are the same or different and are hydrogen or an alkyl group, R z is hydrogen or an amino modifying group, Y is H or or an amino modifying group; R 1 to R 10 are the same or different, and are CH 3 OH or Z, where Z is one of: or or where R 11 to R 22 are the same or different and are CH 3 , OH or Z, and R 23 and R 24 are CH 3 or OH, and m is from 0 - 100 p is from 0 - 100 r is from 0 - 100 s is from 0 - 100 t is form 0 - 100 u is from 0 - 100 v is from 0 - 100 and at least one of R 1 to R 10 is a Z group which contains an A group. A polymer according to claim 4, wherein X is -(CH 2 ) 3 -O-CH 2 -CH(OH)CH 2 - A method of making a polymer comprising reacting an organofunctional silicon-containing compound with at least one of the amino groups in cystine or a cystine derivative, and polymerising the reaction product of the silicon-containing compound and the cystine or cystine derivative. A method according to claim 6, wherein the organofunctional silicon-containing compound has the structure: where: R' is a group containing an amino-reactive group capable of reacting with the amino group in the cystine or the cystine derivative, R'' and R''' are the same or different and are an alkyl group or an alkoxy group or OH, R'''' is hydrogen or an alkyl group. A method according to claim 7, wherein R' is an epoxide group, a sulphonyl halide group, an aryl halide group, an anhydride group or an aldehyde group; and/or R'' is CH 3 or OCH 3 ; and/or R''' is CH 3 or OCH 3 ; and/or R'''' is CH 3 or CH 2 CH 3 . A method according to claim 6, 7 or 8, wherein the reaction of the organofunctional silicon-containing compound with the cystine or cystine derivative is carried out at a pH in the range 8 to 11.5, and at a temperature in the range 40 to 80°C. The use of a polymer according to any of claims 1 to 5 in the treatment of a keratin-containing substrate. The use according to claim 10, comprising bringing a solution of the polymer into contact with the keratin-containing substance, whereby the polymer is at least partially absorbed into the keratin-containing substance, then further polymerising the polymer to harden the polymer. The use according to claim 11, wherein the polymer is further polymerised by the removal of water. A cosmetic formulation which comprises a polymer as claimed in any of claims 1 to 5. A cosmetic formulation according to claim 13, which comprises 0.1 wt% to 5 w% of the polymer.

Inventors: CHAHAL SURINDER PALL, JONES ROGER TREVOR, CHAHAL, SURINDER PALL, JONES, ROGER TREVOR
Applicants: CRODA INT PLC, CRODA INTERNATIONAL PLC
Application year: 1996
Main classification: A61K7
IPC codes: D06M15, A61K8, C08G77, A61Q5