Oil-forming method of chlorine-containing plastic refuse

Abstract: To present an oil-forming method of chlorine-containing plastic refuse capable of obtaining oily product free from chlorine content, while suppressing apparatus corrosion by efficiently capturing hydrogen chloride generated by decomposition of chlorine-containing plastics, the oil-forming method of chlorine-containing plastic refuse is characterized by decomposing chlorine-containing plastic refuse using water in supercritical region as reaction medium and forming into oil, wherein silver nitrate of 0.8 to 2.0 times the reaction equivalent amount of hydrogen chloride generated by decomposition of chlorine-containing plastic refuse is added in the water as reaction medium to decompose and form into oil, and generated hydrogen chloride is removed in a form of silver chloride.

Description: The present invention relates to a method for forming and collecting useful oily matter from chlorine-containing refuse such as vinyl chloride resin. Hitherto, various plastics refuse was mostly disposed of in land fills or by incineration, and not effectively used as a resource in its own right. Since plastics refuse is bulky, disposal by land filling gives rise to a large volume of land utilisation, it becomes difficult to find a suitable filling site, and, after filling, the ground is unstable. Furthermore, if the refuse is incinerated, damage to a furnace can be serious owing to the high calorific value of the solid waste, and incineration is accompanied by the release of harmful gas and a foul smell. Against such a background, there have been recent attempts to regenerate and recycle solid waste plastics without causing pollution, using the waste as a resource in its own right. One such method is to decompose waste plastics material to produce oil using water in its supercritical region (supercritical water) as a reaction medium. Japanese Patent Application JP 06299169A (Enmoto) describes a process in which plastics material is contacted with supercritical water in the presence of an alkali metal catalyst to produce a useful gas such a hydrogen or a gaseous hydrocarbon. WO-A-9 504 796 (University of Akron) discloses a process for decomposing polymers by selective partial oxidation using supercritical water or water at near supercritical conditions, to revert to the original polymers. Neither of these two preceding processes converts polymeric waste to an oily product. When conversion to an oily product with supercritical water is attempted, hydrogen chloride is generated. This has the potential to induce corrosion of the apparatus, and therefore, conventionally, the chlorine-containing plastics are screened and removed beforehand by pre-treatment, and only plastic refuse not containing chlorine-containing plastics is formed into oil. It is therefore a primary object of the invention to provide a method suitable for forming oil from chlorine-containing plastic refuse where the oily product is free from chlorine content, while suppressing or reducing apparatus corrosion by efficiently capturing hydrogen chloride generated by decomposition of chlorine-containing plastics. It is also an object of the invention to suppress corrosion of later stage apparatus such as reactor and heat exchanger due to the generation of hydrogen chloride during the decomposition of chlorine-containing plastics. Silver nitrate, equivalent to or more than the amount of generated hydrogen chloride is capable of capturing the hydrogen chloride as silver chloride. The invention thus provides a method for generating oil from chlorine-containing plastics refuse by reaction with water in its supercritical region, characterised in that the water initially contains silver nitrate in an amount equal to 0.8 to 2.0 times the reaction equivalent of hydrogen chloride generated by decomposition of the refuse. As will be described later in relation to the first of the two embodiments, the hydrogen chloride may be generated during the oil forming reaction, being simultaneously removed by the added silver nitrate. Alternatively, as in the second embodiment, it may be generated in a first reaction step under less severe conditions, and removed at that stage by the added silver nitrate, prior to the oil formation reaction. The decomposition reaction of plastic refuse using water in supercritical region or supercritical water as reaction medium is usually conducted at a minimum temperature of 374°C, preferably 450 to 550°C, but when chlorine-containing plastic refuse is decomposed, hydrogen chloride is generated. In high concentration aqueous solution of hydrogen chloride, corrosion of metal material is excessive, and selection of material to be used in the reaction condition of supercritical water is extremely difficult. Therefore, for decomposition of chlorine-containing plastic refuse, same as in the prior art, either the method of removing chlorine-containing plastics by pretreatment screening, or the method of capturing the generated hydrogen chloride immediately should be required. The method of removing chlorine-containing plastics by pretreatment screening is increased in the number of devices and is hence costly, and another problem is the treatment of the removed chlorine-containing plastic refuse. Accordingly, in the invention, the method of capturing the generated hydrogen chloride immediately was employed, the silver nitrate was selected as the capturing agent. Silver chloride produced by reaction with silver nitrate is extremely small in solubility in water, so that the apparatus corrosion may be suppressed. In the invention, chlorine-containing plastic refuse may include not only the water composed of chlorine-containing plastics such as vinyl chloride alone, but also mixed waste with other plastics, and plastic refuse mainly containing chlorine-containing plastics, and other impurities than plastics may be also contained. Incidentally, the method of the invention is not limited to the oil-forming method of chlorine-containing plastic refuse, but may be also applied in removal of hydrogen chloride generated at the time of treatment of chlorine-containing organic waste such as waste agricultural chemical and PCB. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a schematic explanatory diagram showing a constitution of apparatus according to an embodiment of the invention. Fig. 2 is a schematic explanatory diagram showing a constitution of apparatus according to other embodiment of the invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Referring now to the drawings, the invention is described in detail below. Fig. 1 is a schematic explanatory diagram showing a constitution of apparatus according to an embodiment of the invention. In the apparatus in Fig. 1, chlorine-containing plastic refuse A is fed into vertical or lateral dissolving tank 2 having agitating means through a feeder 1. The chlorine-containing plastic refuse heated and dissolved at a temperature of 200 to 400°C, preferably 250 to 300°C in the dissolving tank 2 is pressurized by a pressurizing device 3 having a screw of one shaft or two or more shafts with a conveying mechanism, and is continuously fed under pressure into a mixing tank (or mixing pipe) 7. The pyrolysis gas containing hydrogen chloride generated by partial decomposition of chlorine-containing plastic refuse at the time of dissolving is discharged from the upper portion of the dissolving tank 2, and is sent into an exhaust gas treating process B. To reduce the melt viscosity, part C of generated oil being formed in oil and recovered may be fed again into the dissolving tank 2. Symbol D is heated gas, which is supplied into the dissolving tank 2 and jacket of the pressurizing device 3. Symbol E is its exhaust gas. They are same also in the reactor 9 described below. On the other hand, in a water adjusting tank 4, silver nitrate F of 0.8 to 2.0 times, preferably 1.0 to 1.1 times the theoretical output of hydrogen chloride generated by decomposition of chlorine-containing plastic refuse is dissolved in water W. This water is sent by a pump 5, and heated to 200 to 600°C, preferably 250 to 400°C, in a preheater 6, and is continuously fed under pressure into the mixing tank (or mixing pipe) 7, and is mixed with chlorine-containing plastic refuse in molten state. The adding amount of water W is preferably in a range of 0.05 to 0.3 by weight as the ratio of chlorine-containing plastic refuse to water. The mixture of chlorine-containing plastic refuse in molten state and water dissolving silver nitrate is heated to 374 to 600°C, preferably 450 to 550°C in the reactor 9, and is decomposed into hydrogen carbide of low molecular weight in a short time in a supercritical state of pressure of 22.1 to 40 MPa (mega pascal). The hydrogen carbide of low molecular weight can be decomposed into any desired state from heavy oil to light oil by properly selecting the reaction temperature, reaction pressure, mixed ratio of plastic refuse/water, and reaction time in the reactor 9. In the pressurizing device 3, mixing tank (or mixing pipe) 7 and reactor 9, hydrogen chloride generated by decomposition of chlorine-containing plastic reacts with silver nitrate dissolved in water, and silver chloride precipitates. This reaction is shown in formula (1). The mixture of hydrogen carbide of low molecular weight released from the reactor 9 and the water in supercritical region is cooled by a cooler 10, and the precipitating silver chloride is separated by solid-liquid separator 8, and is sent to a subsequent separation and recovery process G. The silver chloride separated in the solid-liquid separator 8 is sent into a silver nitrate regeneration process H, and silver nitrate is regenerated and recycled. HCl + AgNO 3 → AgCl + HNO 3 Fig. 2 shows a constitution of apparatus according to other embodiment of the invention. In Fig. 2, same elements as in Fig. 1 are identified with same reference numerals and explanations are omitted. In this embodiment, in the process up to the mixing tank (or mixing pipe) 7, in the condition of 200 to 600°C/1.55 to 40 MPa, almost all quantity of hydrogen chloride is generated, and the precipitating silver chloride is separated in the solid-liquid separator 8 installed before the reactor 9, and this mixture is fed into the reactor 9, and the separation reaction is completed at 374 to 600°C, preferably 450 to 550°C and pressure of 22.1 to 40 MPa in supercritical state. In this embodiment, it is effective to avoid risk of clogging in the reactor 9 due to generated silver chloride. [Examples] Referring to the following examples, the method of the invention is more specifically described below. (Examples) Using the apparatus shown in Fig. 2, oil-forming tests were conducted by using polyethylene (PE), polypropylene (PP), polystyrene (PS), polyvinyl chloride (PVC), and their mixture. In the testing method, each sample was dissolved in the dissolving tank 2 kept at 270°C, and mixed with water heated to 350°C (in tests 4 and 5, water dissolving silver nitrate by 1.05 equivalent to the theoretical generation quantity of hydrogen chloride) in the mixing tank 7, and was fed into the reactor 9 for oil-forming reaction directly in tests 1 to 3, and after removing the precipitating silver chloride in the solid-liquid separator 8 in tests 4 and 5. The reaction conditions and results are shown in Table 1. As known from Table 1, according to the oil-forming method of the invention, a high removal rate of hydrogen chloride over 99% and a high oil-forming rate are obtained in chlorine-containing plastics. Test No. 1 2 3 4 5 Condition Reaction Temperature(°C) 500 500 500 500 500 Reacton Pressure (MPa) 30 30 30 30 30 Plastics/water ratio by weight(-) 0.15 0.15 0.15 0.15 0.15 Reaction time (min) 2 2 0.5 2 2 Sample composition wt% PE 100 0 0 0 32 PP 0 100 0 0 21 PS 0 0 100 0 24 PVC 0 0 0 100 23 Product Transforming rate wt% Gas 7 10 6 21 14 Oil 93 90 94 34 75 Residue 0 0 0 3 1 HCl - - - 42 10 HCl removal rate( wt%) - - - 99.4 99.9 Chlorine content in produced oil - - - 0.7 ≤0.1 According to the oil-forming method of plastic refuse of the invention, hydrogen chloride can be removed efficiently from chlorine-containing plastic refuse, and decomposition and transformation into oil can be conducted without practical risk of corrosion of the apparatus. The obtained oily product is almost free from chlorine content, and is effectively usable as fuel oil or other resource.

Claims: A method for generating oil from chlorine-containing plastics refuse by reaction with water in its supercritical region, characterised in that the water initially contains silver nitrate in an amount equal to 0.8 to 2.0 times the reaction equivalent of hydrogen chloride generated by decomposition of the refuse. A method according to claim 1 wherein the reaction to generate oil from the refuse is performed at a temperature in the range 374 to 600°C. A method according to claim 1 or claim 2 wherein the reaction to generate oil from the refuse is performed at a temperature in the range 450 to 550°C. A method according to any preceding claim wherein the reaction to generate oil from the refuse is performed at a pressure in the range 22.1 to 40MPa. A method according to any preceding claim wherein a first reaction is performed so as to generate hydrogen chloride from the refuse for reaction with the silver nitrate, and the reaction to generate oil from the refuse is completed subsequently to the first reaction. A method according to claim 5 wherein the first reaction is performed at a temperature in the range 200 to 600°C, and under a pressure in the range 1.55 to 40MPa, to generate hydrogen chloride from the refuse for reaction with the silver nitrate. A method according to claim 5 or claim 6 and comprising the further step of separating out precipitated silver chloride from the reaction medium prior to the reaction to generate oil from the refuse. A method according to any one of claims 1 to 6 and comprising the further step of separating out precipitated silver chloride from the reaction medium after the reaction to generate oil from the refuse. A method according to any preceding claim wherein the amount of silver nitrate initially present in the water is in the range of 1.0 to 1.1 times the reaction equivalent of hydrogen chloride generated by reaction of the refuse. A method according to any preceding claim wherein the plastics refuse contains polyvinyl chloride.

Inventors: HASEGAWA SHIGEO, MAKIHARA HIROSHI, MATSUBARA WATARU, HASEGAWA, SHIGEO, MAKIHARA, HIROSHI, MATSUBARA, WATARU, HASEGAWA, SHIGEO, MITSUBISHI JUKOGYO K.K., Makihara, Hiroshi, Mitsubishi Jukogyo K.K., Matsubara, Wataru, Mitsubishi Jukogyo K.K.
Applicants: MITSUBISHI HEAVY IND LTD, MITSUBISHI JUKOGYO KABUSHIKI KAISHA
Application year: 1996
Main classification: C10G1
IPC codes: A62D3, C08L27, B09B3, C10G1