Secondary battery comprising electrode with multiphase, porous active material

Abstract: A secondary battery having a large capacity, and a preferable characteristics in both rapid charge and rapid discharge is provided. A secondary battery which comprises a positive electrode, a negative electrode, and an electrolyte which separates said electrodes, in which any one of the positive electrode or negative electrode contains particles composed of material contributing a charge-discharge reaction, and the particle comprises at least two phases, and fine pores which are formed by dissolving at least one of the phases.

Description: The present invention relates to a secondary battery, a method for manufacturing such a battery and an electrode for a secondary battery according to the preambles of the independent claims. Such a battery, electrode and method are disclosed in EP-A-0 353 837. The secondary batteries under consideration have a large capacity and an improved characteristics in rapid charge and rapid discharge. In accordance with rapidly widespread use of various small sized cordless apparatus, a demand for batteries as a power source increases. Particularly, in view of convenience in use, a request for the batteries having a large capacity, which makes it possible to use the apparatus for a long operating time with one charge of the batteries, increases. The request for increasing capacity of the batteries by consumers has been strong, and accordingly, development in technology for increasing the capacity of batteries has been continued for a long time. As for current batteries which are developed rapidly, there are a nickel-metal hydride battery and a lithium secondary battery. A negative electrode composed of hydrogen storage alloy as a main component is used in the nickel-metal hydride battery. The nickel-metal hydride battery has as an approximately similar characteristics in battery voltage, discharge behavior, and others, as a nickel-cadmium battery, interchangeability with the nickel-cadmium battery, and receives attention as a battery which can be expected to increase the battery capacity by 50-100 %. Further, the lithium secondary battery is a battery with a large capacity as same as the nickel-metal hydride battery because of its high battery voltage and light weight. Accordingly, the nickel-metal hydride battery and the lithium secondary battery are expected to be used in most of the cordless apparatus in near future. Furthermore, in consideration of future exhaustion of oil, environmental problems such as destruction of ozone layer by carbon dioxide, and flattening of power demand, use of the above described batteries will become important as large scale power sources for electric cars and dispersed type power storage. In view of convenience in use of the battery, improvement in a rapid charge characteristics, which indicates how the battery can be charged in a short time, of the battery has been required increasingly. On the other hand, in consideration of apparatus which requires a large discharge current such as an electric car, a rapid discharge characteristics is also important. If the above described characteristics are insufficient, usage of the battery is restricted extremely. Lead battery and nickel-cadmium battery have sufficient characteristics with certain limits both in the rapid charge behavior and the rapid discharge behavior, but the nickel-metal hydride battery and the lithium secondary battery actually do not have any sufficient characteristics in the rapid charge behavior nor the rapid discharge behavior. Hitherto, various methods to improve the nickel-metal hydride battery in its rapid charge-discharge characteristics have been disclosed. For instance, use of an electrode made of hydrogen storage alloy which was composed of ultrafine particles having an average particle size equal to or less than 5 microns (JP-A-60-119079 (1985)), use of a sheet-shaped electrode made of hydrogen storage alloy containing a binder provided with pores having at least 30 microns in diameter (JP-A-61-153947 (1986)), and use of an electrode made of hydrogen storage alloy particles (mother particles), of which surface is coated with p@articles of a metal, a nickel base alloy, or stainless steel having an average diameter of 1/10 ∼ 1/200 (JP-A-64-6366 (1989)) were disclosed. Regarding to lithium battery, a method for improving the rapid charge-discharge characteristics by coating the surface of current collector was disclosed (JP-A-5-159781 (1993)). Generally speaking, an electrode is made of a porous plate which is prepared by pulverizing a material relating to a battery reaction to fine powder, and subsequently, adhering the fine powder to form a sheet by adding an adhesive, or binding the particles of the fine powder by sintering. Accordingly, decreasing the average diameter of the particles causes as porous material layer relating to the battery reaction as much of the decreasing in diameter, and also causes increasing of a field area of the reaction. However, practically, the finer is the material relating to the battery reaction pulverized, the more will the powder fall out from the electrode. Therefore, there are such problems as lowering the capacity of the battery, and forming a coating film composed of impurities at surface of the material relating to the battery reaction in the pulverizing process, the coating film causes a resistance against the battery reaction to make the rapid charge-discharge characteristics worse. Forming pores at surface of the material relating to the battery reaction is effective in increasing the field area for the battery reaction, but the forming pores at surface of the adhesive or a boundary of the particles is futile. Providing the electrode with a plurality of pores will cause the electrode to decrease a packing density of the material relating to the battery reaction, and practically the capacity of the battery is decreased. In accordance with a method wherein conductive particles are arranged around a particle of the material relating to the battery reaction, various shapes of the conductive particle such as fiber or film can be used. And various kind of the conductive particles such as carbon, a metal, and a reaction catalyst can be used as far as it may not harm the conductivity. However, addition of such a material which does not have any effect in the battery reaction, or a material which has the effect very slightly, will cause a problem to decrease a volumetric density. A method of coating the current collector includes various kinds of means, but their sole object is to decrease a contact resistance between the current collector and the material relating to the battery reaction. However, practically, resistances inside the electrode such as a contact resistance between the particles each other, and a reaction resistance at a boundary between the particle and the electrolyte, are significantly larger than the contact resistance between the current collector and the material relating to the battery reaction. As described above, any effective method for improving the rapid charge-discharge characteristics has not been disclosed yet. Citation EP-A-0 353 837 discloses a nickel electrode for an alkaline battery. There, a pores alkaline prove metal fiber substrate is used as a current collector, and active material applied thereto includes nickel hydroxide powder to which zinc or magnesium is added. In order to improve the conductivity between the active material particles and the current collector, cobalt compound powder mixed therewith and dissolved in the battery electrolyte and may than be deposited between the current collector and the active material particles prior to charging. When charge, by virtue of electrochemical oxidation, it changes into highly conductive cobalt oxy-hydroxide. Citation US-5 366 831 discloses a nickel electrode for an alkaline battery. In a paste-type nickel electrode, nickel hydroxide powder is used as an active material. II-group elements and cobalt are included in the nickel hydroxide powder in solid solution state. The object of the present invention is to provide a secondary battery which can widely be used by improving the rapid charge-discharge characteristics of the secondary battery. This object is solved in accordance with the features of the independent claims. Dependent claims are directed on preferred embodiments of the invention. In a secondary battery comprising a positive electrode and a negative electrode which are separated by an electrolyte, either of the positive electrode or the negative electrode includes particles made of a material relating to charge-discharge reactions, the particles are composed of at least two phases, and at least one phase of the above two phases has fine pores. The particles are composed of at least two phases, and at least one phase of the above two phases has fine pores which are formed by dissolution. The fine pores are characterized in existing at surface of the particle where the particle contacts with the electrolyte. Since the fine pores contribute to the battery reaction, the fine pores may exist at least in the surface of the particle where the particle contacts with the electrolyte. The particles of the material relating to the charge-discharge reaction, which form the battery electrode of the present invention, are characterized in having fine pores at the surface of the particles, and in that a composition at the surface of the fine pores differs from the composition at the surface of the particle other than the surface of the fine pores. The fine particles are so-called primary particles. An active coating can exist at the surface of a fine pore which is formed by dissolution and the like, differing from the fine pore formed at interval between particles by agglomerating the particles, due to chemical elements which exist in phases which has been dissolved or evaporated, and to chemical elements which exist at particle boundaries between the phase which has been dissolved and the other phase. The particle is characterized in being composed of a plurality of phases, and that the fine pores are formed by dissolving or evaporating at least one of the plural phases, and at least one of transition metal elements exists at the surface of the fine pore. For instance, the transition metal element exists in a condition of a coated film of an oxide or a hydroxide. When the particle is composed of an alloy, the alloy consists of at least two kinds of chemical elements, and the alloy comprises a first phase and at least a second phase which is precipitated in the first phase, and the particle has fine pores which are formed by dissolving or evaporating at least one phase of the second phase. When a main component of the particle is carbon, the carbon is characterized in having at least one phase, and having fine pores, which are formed by dissolving or evaporating at least one of the phase, at surface of the carbon. The fine pores exist only at a plane which can be contacted with the electrolyte, and the fine pores may not exist inside the particle which can not contact the electrolyte. When the particle is composed of carbon and additive components, the previously described at least one phase may be composed of the additive components or a compound of the additive components with the carbon. When the particle is composed of oxides or sulfides, the oxides or the sulfides contain at least two kinds of chemical elements, and the compounds comprise a first phase and at least a second phase which is precipitated in the first phase, and the particle has fine pores which are formed by dissolving or evaporating at least one phase of the second phase. The particle may be composed of particles having an average diameter equal to or less than 2 mm, and the fine pores may have an average diameter in a range from 1/150 to 1/2 of the average diameter of the particle. The diameter is called primary diameter. The material relating to the charge-discharge reaction of the present invention is in a form of particles of a diameter of at most 2 mm, preferably in a range from 20 nanometers to 500 microns. The particles are manufactured to be a porous electrode by one of various methods such as adhering the particles with an adhesive agent, pulverizing mechanically, sintering thermally, and agglomerating chemically. If the particle has a diameter larger than 2 mm, any significant effect for improving the characteristics can not be observed even if fine pores as described above are provided. Advantageous particles have a diameter preferably in a range from 20 nanometers to 500 microns. The average diameter of the fine pores is in a range from 1/150 to 1/2 of the average diameter of the particles, preferably in a range from 1/50 to 1/5. If the average diameter of the fine pores is larger than 1/2 of the average diameter of the particles, holding power for the electrolyte decreases, and consequently, an amount of the electrolyte held by the fine pores is decreased, and the field area for the reaction is also decreased. On the contrary, if the average diameter of the fine pores is smaller than 1/150 of the average diameter of the particles, air bubbles in the fine pores are hardly replaced with the electrolyte, and consequently, the amount of the electrolyte held by the fine pores is decreased, and the field area for the reaction is decreased. Preferably, the total area of the surface occupied by the fine pores is in a range from 5 % to 80 % of the surface area of the particle. The fine pores existing in the above particle occupy a surface area of the particle in a range from 5 % to 80 %, preferably a range from 10 % to 50 %. If the occupied surface area is smaller than 5 %, the advantages of the improvement, is small. If the occupied surface area is larger than 80 %, the volumetric density is decreased, because the packed density of the particles is decreased. The particle may be such that the fine pores occupy the volume of the particle in a range from 0.2 % by volume to 60 % by volume of the particle. The fine pores existing in the particle occupy the volume of the particle in a range from 0.2 % by volume to 60 % by volume, preferably a range from 1 % by volume to 40 % by volume. If the occupied volume is less than 0.2 % by volume, the advantages is small. If the occupied volume is larger than 60 %, the volumetric density is decreased, because the packed density of the active material is decreased. When the negative electrode comprises hydrogen storage alloy particles, the particles are composed of an alloy comprising at least one chemical element selected from a group consisting of magnesium, lanthanum, cerium, praseodymium, neodymium, titanium, zirconium, hafnium, palladium, yttrium, scandium, calcium, aluminum, cobalt, chromium, vanadium, manganese, tin, boron, molybdenum, tungsten, carbon, lead, iron, nickel, potassium, sodium, and lithium. The particle may also be composed of at least two phases, and has fine pores which are formed by dissolving at least one phase of the above described phases. For instance, the phase to be dissolved is in a dispersed state in the mother phase as explained above. The phase to be dissolved can be a phase which is soluble in an alkaline solution. In accordance with the present invention, the phase formed by dissolution is understood to include a phase which is dissolved with an acid, an alkali, an oxidizing agent, and a reducing agent, and a phase which is formed by contacting and evaporating with a reactive gas. The above alloys (intermetallic compounds) can be prepared by an arc-melting or a high frequency melting, and subsequently, gradually cooling the molten alloys to a temperature or holding at the temperature whereat a phase, which is soluble into an alkaline solution, can be obtained. The phase to be solved in the negative electrode containing the hydrogen storage alloy particles preferably contains at least one metal selected from a group consisting of aluminum,. vanadium., manganese, tin, boron, magnesium, molybdenum, tungsten, zirconium, potassium, sodium, lithium, nickel, and titanium at least 40 % by weight. The phase wherein a content of the above component is within the above range is suitable for forming fine pores by dissolution, and preferable fine pores can be formed. The phase to be solved can be a phase which is extremely soluble into an alkaline electrolyte. The phase to be solved can be prepared by sintering or melting, or mixing by a mechanical alloying method or a mechanical grinding method. The objective negative electrode (or the particles forming the negative electrode) is prepared by adjusting the degree of alloying in accordance with controlling rotations per unit time and operating time in the mechanical alloying method or the mechanical grinding method so as to obtain the phase to be solved into the alkaline solution in a segregated condition, not so uniform condition. The fine pore may be formed by dissolving into the electrolyte. The electrolyte may be the one generally used in a nickel metal hydride battery. The fine pore may exist only on a plane which contacts with the electrolyte, and does not exist inside the particle which can not contact with the electrolyte. The negative electrode may be composed of carbon as a main component, the carbon contains at least a phase which is composed of at least one of chemical elements or oxides of chemical element which is selected from a group consisted of iron, nickel, sulphur, silicon, tin, lithium, sodium, potassium, and lead, and one of the above phase comprises fine pores which are formed by dissolution or evaporation with at least one of an acid, an alkali, an oxidizing agents, or a reducing agent. The negative electrode is preferably suitable for a negative electrode of a lithium secondary battery, for instance. The positive electrode or the negative electrode may be composed of a conductive polymer, the conductive polymer contains at least a phase which is composed of at least one chemical element or oxides of chemical element which is selected from a group consisting of iron, nickel, sulphur, silicon, tin, lead, lithium, sodium, and potassium, and one of the above phase comprises fine pores which are formed by dissolution or evaporation with at least one of an acid, an alkali, an oxidizing agents, or a reducing agent. The positive electrode or the negative electrode is preferably suitable for a positive electrode or a negative electrode of a lithium secondary battery, for instance. The negative electrode may be composed of an alloy, and that the alloy contains at least one element selected from a group consisting of nickel, silicon, germanium, magnesium, copper, and manganese, the alloy is composed of at least two phases, and one of the phases comprises fine pores which are formed by dissolution or evaporation with at least one of an acid, an alkali, an oxidizing agents, or a reducing agent. The negative electrode is preferably suitable for a negative electrode of lithium secondary battery, for instance. The positive electrode may comprise a first phase composed of an oxide containing at least one of chemical element selected from a group consisting of lead, manganese, vanadium, iron, nickel, cobalt, copper, chromium, molybdenum, titanium, niobium, tantalum, strontium, and bismuth, or a sulfide containing at least one of chemical elements selected from a group consisted of titanium, molybdenum, iron, tantalum, strontium, lead, niobium, copper, nickel, vanadium, bismuth, and manganese, or a complex oxides compound or a complex sulfides compound containing the above oxides and lithium or the above sulfides and lithium, and a second phase composed of an oxide containing at least one of chemical elements or oxides selected from a group consisted of aluminum, tin, boron, magnesium, potassium, and sodium, and that one of the above two phases comprises fine pores which are formed by dissolution or evaporation with at least one of an acid, an alkali, an oxidizing agents, or a reducing agent. The positive electrode is preferably suitable, for instance, for a positive electrode of lithium secondary battery. A method for manufacturing the positive electrode and the negative electrode, which are used in a secondary battery wherein the positive electrode and the negative electrode are arranged to be separated by an electrolyte, comprises the steps of forming the negative electrode by compacting particles of a material which relates to the battery reaction, the negative electrode comprising a first phase and at least a second phase which exists in the first phase, and forming fine pores by dissolving or evaporating at least a phase of the second phase with any one of an acid, an alkali, an oxidizing agents, or a reducing agent. For instance, the method comprises the steps of dispersing particles of the material relating to the battery reaction, wherein a first phase exists and a second phase is dispersed in the first phase, by chemical reaction of the components in the first phase with the components in the second phase for dispersing the second phase into the first phase, pulverizing the first phase wherein the second phase is dispersed, forming fine pores at surface of the particle by dissolving or evaporating the second phase in the pulverized particles with any one of an acid, an alkali, an oxidizing agents, or a reducing agent, and fabricating the particles having the fine pores to a plate. In the above method, the chemical reaction can be performed by a mechanical alloying method, a solid reaction, a liquid reaction, a gaseous reaction, and a synthetic method using atomized gas (nebulizing at a temperature near a precipitating temperature of the second phase, etc.). In the above case, the conditions such as particle size, the amount of the second phase, and the others are as same as previously designated. The particles having the fine pores can be fabricated to a plate by a method comprising the steps of mixing the components for the first phase and the components for the second phase, melting at least the components for the first phase, cooling and pulverizing the mixture, and forming fine pores at surface of the particle by dissolving or evaporating the second phase in the pulverized particles with any one of an acid, an alkali, an oxidizing agents, or a reducing agent. Naturally, the fine pores can be formed by evaporating the second phase selectively by contacting with a reactive gas as previously described. The second phase can be contained in the first phase by adding the components for the second phase into the molten components for the first phase. The electrode can be fabricated to a necessary shape such as a plate after forming the fine pores by the steps of preparing the second phase (a precipitated phase) with an alloy, an intermetallic compound, or chemical elements, all of which are selectively soluble with any one of an acid, an alkali, an oxidizing agent, or a reducing agent, and dissolving the second phase with the agent which can dissolve the second phase to form the fine pores. Otherwise, the electrode is fabricated first to a necessary shape, and subsequently, the fine pores can be formed by dissolving the second phase. The present invention can be applied to a secondary battery which is composed of a positive electrode, a negative electrode, and an electrolyte distributed in the battery. A separator can be provided between the positive electrode and the negative electrode if it is necessary. Particularly, the present invention is preferably applicable to a sealed type battery such as a nickel-metal hydride battery and a lithium battery. The alloys which are used in the present invention must be understood to include so-called intermetallic compounds. For instance, the present invention can be a secondary battery composed of a positive electrode and a negative electrode made of a hydrogen storage alloy, both of which are contained in a vessel with electrolyte. The negative electrode made of a hydrogen storage alloy is preferably formed by compacting the hydrogen storage alloy particles. A separator can be arranged between the positive electrode and the negative electrode. When applying the present invention to a negative electrode made of the hydrogen storage alloy, a catalytic effect of the hydrogen occluding reaction can be obtained. The rapid charge-discharge characteristics of the battery can be improved and a long life time of the battery can be obtained by the catalytic effect of active species (it can be assumed to be an active chemical element having vacancy and unpaired electron) which remains in the fine pores. The present invention can be applied to the second battery which is composed of a positive electrode and a negative electrode, both of which are contained in a vessel with a non-aqueous electrolyte, wherein the charge-discharge reaction is performed by holding and releasing alkaline metal ions (for instance, lithium ions) at the positive electrode and the negative electrode. In a case when carbon or a conductive polymer is used for composing the negative electrode, taking the carbon for example, lithium is inserted into the carbon at an edge portion of the six-membered ring, and an intercalation reaction proceeds. Owing to the fine pores, a large number of the edge portion of the six-membered ring, so-called terminal portions, exist, and the reaction is facilitated to proceed. Accordingly, the rapid charge-discharge characteristics of the battery can be improved and an increased capacity of the battery can be obtained. In a case when the conductive polymer is used for composing the positive electrode, an amount of the electrolyte absorbed into the fine pores can be increased, because the active material at the positive electrode is anion in the electrolyte, and accordingly, the charge-discharge reaction can be proceeded smoothly. In a case when an oxide or a sulfide of metal is used for composing the positive electrode, defects can be generated by adding a transition metal into the oxide or the sulfide to replace the metal in the positive electrode with the transition metal. As lithium can be filled into the defect, increase of the defect enables to increase reaction sites of the lithium, and consequently, the capacity of the battery can be increased. Shapes of the particles of the material relating to the battery reaction and of the fine pores can be spherical, oval, conical, fibrous, doughnut-like, cubic, rectangular parallelepiped-like, and amorphous. For instance, the present invention can be applied to the following electrodes of batteries. Naturally, if a batteries performance can be improved by forming the above fine pores, the invention can be applied to such batteries which are not particularly described here. As a material relating to the charge-discharge reaction at the negative electrode of nickel metal hydride battery, the hydrogen storage alloy composed of the following components can be used. Furthermore, the following alloys and the like (the first phase) having the phase to be dissolved (the second phase) relating to the present invention can be used: An alloy which is composed of components of nickel combined with at least one element selected from a group consisting of magnesium, lanthanum, cerium, neodymium, praseodymium, titanium, zirconium, hafnium, palladium, yttrium, scandium, and calcium; and An alloy which is composed of components of the above alloy combined with at least one element selected from a group consisting of aluminum, calcium, chromium, vanadium, manganese, tin, barium, molybdenum, tungsten, carbon, lead, iron, potassium, sodium, and lithium. For instance, the present invention can be carried out with alloys composed of the following components : and Where, the ratio of a sum of (La-Ce-Nd-Pr) to a sum of (Ni-Mn-Al-Co-X), wherein X is nil, or any one of B, W, or Mo, is within a range of 1 : 4.5∼5.5 by atomic ratio. Furthermore, an alloy composed of (Zr)-(Ni-V-Mn-Z) can be used. Where, Z is nil, or at least any one of Co, Fe, Cr, and Sn, such as Co-Fe, Co-Sn, Cr-Fe, Co-Cr, and the like, and a ratio of (Zr) to a sum of (Ni-V-Mn-Z) is within a range of 1 : 1.5∼2.5 by atomic ratio. Arbitrarily, Ti can be added to (Zr). In this case, the above atomic ratio must be calculated based on a sum of (Zr-Ti). Furthermore, an alloy composed of (Mg-Zr)-(Ni-Al-Mn-Co) can be used. The ratio of a sum of (Mg-Zr) to a sum of (Ni-A-Mn-Co) is within a range of 2 : 0.5∼1.5 by atomic ratio. Arbitrarily, Ti can be added to (Mg-Zr). In this case, the above atomic ratio must be calculated based on a sum of (Mg-Zr-Ti). As a phases to be dissolved in the hydrogen storage alloy, a phases composed of the following components, for instance, can be used: A phase composed of V and Ti added with at least any element selected from a group consisting of B, C, Cr, W, Mo, Sn, Mg, K, Li, or Na; A phase composed of Al and Mn added with at least any element selected from a group consisting of B, W, or Mo; and A phase composed of any combination of Ni-Ti, Zr-Ni, Zr-Mn, B-Al-Co, B-Ni-Mn, and the like. As materials contributing to the charge-discharge reaction at the positive electrode of the lithium battery, the following compounds (alloys) can be used. Furthermore, the following compounds (first phase) including the above phase to be dissolved (second phase) can be used: A compound (alloy) composed of oxygen and at least one of the following elements: lead, manganese, vanadium, iron, nickel, cobalt, copper, chromium, molybdenum, titanium, niobium, tantalum, strontium, and bismuth (The compounds can be so-called a complex oxides.); A compound (so-called sulfide) composed of sulfur and at least one of the following elements: lead, manganese, vanadium, iron, nickel, copper, molybdenum, titanium, niobium, tantalum, strontium, and bismuth; A compound (alloy) composed of the same composition as the above compounds containing oxygen, or sulfur, except a point that lithium is additionally added (The compounds can be so-called oxides, or sulfides); A conductive polymer (for instance, polyaniline, polyparaphenylene, polyacene, polypyrrol), or the conductive polymer added with at least one of the following elements: iron, silicon, sulfur, copper, lead, nickel, and vanadium; and Carbon, or the carbon added with at least one of the following elements: iron, silicon, sulfur, copper, lead, nickel, and vanadium. As for the materials contributing to the charge-discharge reaction at the positive electrode of the lithium battery, the compounds having the following composition can be used: LiCoO x , LiMnO x , LiNiO x , LiFeO x , LiNi 0.5 Co 0.5 O x , LiCo 0.5 Mn 0.5 O x , LiNi 0.5 Mn 0.5 O x , LiNi 0.5 Fe 0.5 O x , LiFe 0.5 Co 0.5 O x , LiNi 0.5 Fe 0.5 O x , LiMn 2 O 2x , TiS x , MoS x , LiV 3 O 2x , or CuV 2 O 3x , where, x is in a range from 1.5 to 2.5.; and LiNi m Co n O x , LiCo m Mn n O x , Ni m Mn n O x , LiNi m Fe n O x , LiFe m CO n O x , LiFe m Mn m O x , where, (m + n) is in a range from 0.8 to 1.3, not necessarily to be evenly shared as 0.5 each, and x is in a range from 1.5 to 2.5. As materials contributing to the charge-discharge reaction at the negative electrode of the lithium battery, the compounds (alloys) composed of the following components can be used. Furthermore, the following compounds (first phase) including the above phase to be dissolved (second phase) can be used: Carbon (carbon black, furnace black, pitch group carbon, meso phase group carbon, PAN group carbon, glassy carbon, graphite, amorphous carbon, and a combined material of the above carbons); A compound composed of the above carbon and at least an element selected from a group consisted of iron, silicon, sulfur, copper, lead, nickel, and vanadium; A conductive polymer (for instance, polyaniline, polyacene, and polypyrrol); A compound composed of the above conductive polymer and at least an element selected from a group consisting of iron, silicon, sulfur, copper, lead, nickel, and vanadium; and An alloy composed of a combination of at least an element selected from a group consisting of manganese, nickel, copper, calcium, and magnesium, and at least an element selected from a group consisted of germanium, silicon, tin, and lead. For instance, Si-Ni, Ge-Si, Mg-Si, Si-Ni-Ge, Si-Ni-Mg, Si-Ni-Mn, Si-Ni-Cu, and the like can be used practically. When the material contributing to the charge-discharge reaction, which is composed of an alloy, is prepared, the components of the alloy are melted, and subsequently, a precipitated phase (segregated phase) to be dissolved with an acid or an alkali is formed by an aging treatment or controlling cooling speed (for instance, gradual cool). The components for forming the alloy can be adjusted by adding additive elements in order to disperse the precipitated phase having a desired size. The additive elements desirably have an effect to induce the precipitation. For instance, the phase to be dissolved is formed so as to disperse in the prepared alloy (if the additive element exists as a particle, it is a primary particle). Further, the material composed of an alloy can be prepared by mixing the components with a mechanical alloying method, or a mechanical grinding method. The objective negative electrode (or particles to form the negative electrode) is manufactured so as not to precipitate the phase to be dissolved so homogeneously by controlling the degree of alloying by regulating the rotation per unit time, and the operating time in the mechanical alloying method, or the mechanical grinding method. The phase to be dissolved is preferable dispersed in the mother phase, and has a desired size. When the material contributing to the charge-discharge reaction, which is composed of carbon or a conductive polymer, is prepared, the components for the phase to be dissolved are mixed with other raw materials, and the components are preferably melted to disperse in the raw materials such as carbon or the conductive polymer (if the raw material exists as a particle, it is a so-called primary particle), and are cooled to form the material. This method can be applied even if the material contributing to the charge-discharge reaction is oxides (complex oxides) or sulfides (complex sulfides). For instance, the components for the phase to be dissolved are mixed with the carbon or the conductive polymer, and the mixture is treated with heating to melt and to disperse the material to be dissolved into the carbon or the conductive polymer. The temperature of the heat treatment is preferably in a range from 300 °C to 3500 °C. When the material is used for the positive electrode of the lithium battery, the temperature of the heat treatment is preferably in a range from 300 °C to a few hundreds °C, and when the material is used for the negative electrode, the temperature of the heat treatment is preferably in a range from 1000 °C to 3500 °C. For instance, a material relating to the charge-discharge reaction (so-called an active material), which is suitable for the battery, can be obtained by forming the fine pores by dissolving with an acid, and subsequent heat treatment. Instead of the above dissolution, evaporation by contacting with a reactive gas can be used. The present invention is hardly applicable to the material contributing to the charge-discharge reaction (if it exists as a particle, it is a so-called primary particle), wherein the components of the material are distributed homogeneously as a whole by a designated heat treatment (for instance, homogenizing treatment, etc.). The precipitated phase (second phase), which is more soluble by an acid or an alkali than the mother phase (first phase), is preferably dispersed. As explained above, the phase to be dissolved can be formed by precipitation, if the material is composed of an alloy. If the material is composed of a carbon or a conductive polymer, the phase to be dissolved can be included as particles in the mother phase (first phase) composed of the carbon or the conductive polymer. The electrode relating to the present invention can be formed as a porous electrode by any method selected from adhering the particle with an adhesive agent, mechanical compacting, thermally sintering, or chemically agglomerating. The electrode particularly suitable for the present invention is preferably applied to an electrode, wherein the material contributing to the charge-discharge reaction in the electrode is so-called intercalation type. The advantages of the fine pores relating to the present invention is not sufficiently realized when the charging and discharging are repeated, if the electrode is so-called dissolution-precipitation type, wherein components of the material contributing to the charge-discharge reaction in the electrode dissolve from surface of the electrode into the electrolyte by charge-discharge reaction. As the acid, the alkali, the oxidizing agent, and the reducing agent, for dissolving the material to form fine pores as the present invention, the following reagents can be used. But, the following reagents are exemplified to describe the present invention in detail, and not to restrict the scope of the present invention: Acids : nitric acid, fluoric acid, hydrochloric acid, sulfuric acid; Alkalis : potassium hydroxide, sodium hydroxide; Oxidizing agents : sodium hypochlorite, potassium hypochlorite, hydrogen peroxide aqueous solution; Reducing agents : formalin, sodium boron hydride, potassium hypophosphite, sodium hypophosphite. As gases used for forming the fine pores by evaporating the material, a reactive gas such as halogen and the like can be used. For instance, a halogen gas such as F 2 , Cl 2 , and Br 2 , is contacted with the phase to be evaporated to evaporate the phase selectively. In accordance with the present invention, a rapid charging characteristics and a rapid discharging characteristics of secondary batteries are significantly improved. Furthermore, increase of the capacity and life time of the batteries can be realized. The material which contributes to the charge-discharge reaction (if it exists as a particle, it is a so-called primary particle) has fine pores formed by dissolution with an acid or an alkali. In accordance with the present invention, a packed density of the material contributing to the charge-discharge reaction in the electrode can be increased higher than the packed density of the material contained in an electrode prepared by compression or fabrication of powder, wherein specific surface of the material is increased by being provided with the fine pores formed in intervals between particles, or being provided with deposit (for instance, carrier, etc.) on surface of primary particles. Accordingly, the capacity of the battery can be increased. Because the electrolyte can be retained in the fine pores, the charge-discharge reaction can proceed smoothly. The particle which is provided with the fine pores relating to the present invention firstly differs from the particles, which are provided with metallic powder or catalytic powder, in an increased specific surface area of the material relating to the charge-discharge reaction, and a widely spread reaction field. Accordingly, the rapid charge and discharge reaction proceeds smoothly. The particles having the fine pores relating to the present invention can contribute to the reaction sufficiently. Accordingly, in comparison with the electrode which is treated only at the surface by heating to a high temperature after fabrication, the electrode relating to the present invention hardly cause current concentration etc, and an extended duration time can be obtained. The fine pores relating to the present invention differ from fine pores which are composed of intervals between the particles, the intervals are formed by dissolving phases which are soluble in an extremely reactive agent such as an acid, an alkali, an oxidizing agent or a reducing agent, and the fine pores relating to the present invention can increase further the reactivity of the particles because an inactive film (for instance, an insulating film) such as an rigid oxidized coating film which is usually generated is hardly formed. A coating film having a strong activity (for instance, a conductive oxidized coating film), which is not so rigid as an oxidized coating film usually formed on surface at periphery of the fine pores, are generated. The surface of the fine pores generated by dissolving the phases has a discontinuous and non-equilibrium atomic arrangement. Accordingly, defects and vacancies are generated, and an electronically charged condition positively or negatively are formed, and consequently, the surface is deemed to contribute to increase the activity. Depending on the kinds of chemical elements existing in the phase to be dissolved or in the particle boundary between the phase to be dissolved and another phase, a dissolving speed varies significantly in a short time, and consequently, the composition at the surface of the fine pore changes to an active layer which has a composition different from the composition before the treatment. Therefore, the surface of the fine pore has a strong activity, because the surface is not only being the surface of fine pores but also having the electronic vacancies and positive holes, or forming a catalytic layer which is etched delicately or an unstable layer (for instance, the previously described charged layer). Accordingly, the electrolyte can be retained in the fine pores by not only a capillary action but also an electronic absorption, and the reaction speed is increased by catalytic activation of the reactive materials. As explained above, the fine pores relating to the present invention differ from the fine pores formed in intervals between particles of a porous electrode. The fine pores relating to the present invention are formed at the surface of the particle whereon a dissolving agent contacts, because the fine pores are formed by dissolving the phases to be dissolved (secondary phase, or precipitated phase) with the dissolving agent such as an acid, an alkali, an oxidizing agent, or a reducing agent. For instance, the fine pores exist only on the surface which can be contacted with the electrolyte, and an active reaction field is formed. Accordingly, the composition of the phase to be dissolved, which exists in the closed portion inside the particle and has not been dissolved, remains inside the particle in an unchanged condition, and an existence of the phase to be dissolved is readily determined by analysis of the chemical elements. As the phase to be dissolved is formed for being dissolved, this portion contributes to the charge-discharge reaction not at all, or with a small effect or a small capacity. Therefore, in order to make the remained amount of the composition of the phase to be dissolved as small as possible, it is important to select an appropriate dissolving condition of the dissolving agent. In order to dissolve certainly, it is desirable to dissolve the phase to be dissolved certainly with heating externally such as a warm acid or a warm alkali. When the electrolyte is acidic or alkaline and can dissolve the phase to be dissolved, the phase (secondary phase, or precipitated phase) to be dissolved, which has not been dissolved in a previous dissolving operation, is dissolved into the electrolyte in a battery by contacting with the electrolyte. Therefore, the composition of the phase (secondary phase, or precipitated phase) to be dissolved is dissolved into the electrolyte, and its existence can be confirmed by analysis of the electrolyte. In a case when the phase to be dissolved can be dissolved into the electrolyte, even if breakage such as fracture of the particle are generated by operation of the battery, the new fine pores existing at the surface of the particle composed of the material relating to the charge-discharge reaction can be re-formed by contacting new fractured surface of the particle with the electrolyte, and consequently, the charge-discharge reaction can be maintained preferably. The composition dissolved into the electrolyte is not necessarily recovered positively by utilizing an effect such as precipitating the components at a desirable place. The advantages of the present invention can be realized only by forming the fine pores by dissolution. The composition of the electrolyte and the reaction products can be retained inside the fine pores. In this case, even if the material relating to the charge-discharge reaction in the electrode is broken (including fracturing, breakage etc.) during the charge-discharge reaction and a new cleaved surface contacting the electrolyte is generated, the phase to be dissolved existing at the new cleaved surface contacts with the electrolyte, and new fine pores can be re-formed. Brief Description of the Drawings These and other objects, features, and advantages of the present invention will be understood more clearly from the following detailed description with reference to the accompanying drawings, wherein; FIG. 1 is a set of photographs indicating an analytical result of segregated phases obtained by the embodiment 1, FIG. 2 is a set of photographs indicating an analytical result of segregated phases obtained by the embodiment 1 after melting, FIG. 3 is a schematic partial exploded view illustrating a structure of a sealed battery, FIG. 4 is a set of photographs indicating an analytical result of the alloy obtained by the comparative example 1, FIG. 5 is a set of photographs indicating an analytical result of the alloy obtained by the comparative example 1 after melting, FIG. 6 is a graph indicating a relationship between a ratio of an average diameter of fine pores to an average diameter of the alloy particles and their volumetric ratio obtained by the embodiment 4, and the comparative examples 6 and 7, FIG. 7 is a graph indicating a relationship between a ratio of a cross sectional area of fine pores to a surface area of particles and their volumetric ratio obtained by the embodiment 5, and the comparative examples 8 and 9, and FIG. 8 is a graph indicating a relationship between a ratio of a total volume of fine pores to a total volume of particles and their volumetric ratio obtained by the embodiment 5, and the comparative examples 8 and 9. Description of the Preferred Embodiments The present invention is explained in detail referring to embodiments, wherein the present invention is applied to a secondary battery. The present invention can be applied to power sources for apparatus having large power consumption such as high performance personal computers, electric automobiles which requires a high power, power sources for electric power storage, etc. (Embodiment 1) An alloy of Ti 0.2 Zr 0.8 Ni 1.1 Mn 0.6 V 0.2 B 0.03 was used as a hydrogen storage alloy for composing a negative electrode. The alloy was obtained by melting at a temperature in a range of 1100 °C to 1500 °C, cooling by a speed in a range of 0.01 °C/min. to 0.5 °C/min., and subsequently, annealing at a temperature in a range of 300 °C to 500 °C for 2 hours. The alloy was pulverized to particles having an average diameter of 50 microns. The surface of the alloy particle was observed by a scanning electron microscope-electron bean diffraction (SEM-EDX), and it was revealed that the alloy forms a segregated phase of V, B, and Ti having an average diameter of 5 microns. The distributing condition of the above phase is shown in FIG. 1. Then, the alloy was treated with 30 % by weight KOH aqueous solution at 70 °C for 2 hours, and subsequently, the alloy was washed with water sufficiently. The surface of the alloy particle was observed again by the SEM-EDX. The result of the observation is shown in FIG. 2. The V and B in the segregated phase having an average diameter of 5 microns were dissolved completely, and Ti was remained in the fine pores. It reveals discontinuity in composition of the alloy and the peripheral portion of the fine pores, which has been generated depending on difference in dissolving speed of respective chemical elements. At that time, the fine pores occupied 15 % of the total particle surface, and 5 % of the total particle volume. The same result was obtained by reacting and evaporating the segregated phase with flowing a gas such as chlorine or fluorine, other than the dissolving treatment with warm KOH aqueous solution. Then, an electrode made of metal hydride was formed by the steps of mixing hydroxypropylmethyl cellulose to the alloy particles as a binder, packing the mixture into a foamed nickel base, and rolling the packed nickel base with a roller press to a designated thickness. As a nickel electrode, a paste electrode using foamed nickel having a porosity of 95 % as an electrode base was used. A sealed nickel-metal hydride battery of AA-size was prepared with the above electrodes. A structure of the prepared battery is shown in FIG. 3. A positive electrode and a negative electrode were rolled up with a separator made of unwoven cloth of polypropylene resin of 0.17 mm thick, which was inserted between the electrodes, and the rolled electrodes were contained in a battery can. As for an electrolyte, 31 % by weight KOH aqueous solution mixed with a small amount of LiOH was used. The battery capacity was designed to be 900 mAh. The battery was charged to 150 % of the rated capacity with 0.3 C or 3 C (C is a rate of discharge, hereinafter), and after a quiescent time of one hour, the battery was discharged to a terminal voltage of 1.0 V with 0.3 C or 3 C. A discharging capacity of the battery was determined on a case when the battery was charged with 0.3 C and, subsequently, discharged with 0.2 C. Furthermore, ratios of discharging capacities were determined, taking the discharging capacity of 0.2 C discharging after charged with 0.3 C as 100, on the cases of 3 C charge-0.2 C discharge, and of 0.3 C charge-3 C discharge. The discharging capacity of the 0.3 C charge-0.2 C discharge case was as large as 1050 mAh, and a cycle life was as long as 520 cycles. When the discharging was changed to 3 C, the discharge capacity decreased to 95 % of the above 0.3 C charge-0.2 C discharge case . Similarly, when the charging was changed to 3 C, the discharge capacity decreased to 92 %. (Comparative example 1) An alloy of Ti 0.2 Zr 0.8 Ni 1.1 Mn 0.6 V 0.2 was used as a hydrogen storage alloy for composing a negative electrode. The alloy was obtained by melting at a temperature in a range of 1100 °C to 1500 °C, and subsequently, homogenizing by heating at 1050 °C for 3 to 10 hours in an argon gas atmosphere. The alloy was pulverized to particles having an average diameter of 50 microns. The surface of the alloy particle was observed by a scanning electron microscope-electron bean diffraction (SEM-EDX), and it was revealed that the alloy did not form any segregated phase. The distributing condition of the chemical components is shown in FIG. 4. Then, the alloy was treated as same as the embodiment 1 in order to form the fine pores. However, the fine pores could not be formed as shown in FIG. 5. Then, an electrode made of metal hydride was formed by the same steps as the embodiment 1, and a sealed nickel-metal hydride battery of AA-size was prepared with the above electrodes. A discharging capacity of the battery was determined. When the battery was charged with 0.3 C and discharged with 0.2 C, the discharging capacity was as large as 950 mAh, but the cycle life was as short as 380 cycles. When the discharging was changed to 3 C, the discharge capacity decreased to 45 %, and when the charging was changed to 3 C, the discharge capacity decreased to 56 %. (Comparative example 2) An alloy of Ti 0.2 Zr 0.8 Ni 1.1 Mn 0.6 V 0.2 was used as a hydrogen storage alloy for composing a negative electrode, and the alloy particles having an average diameter of 50 microns were prepared by the same method as the comparative example 1. Then, an electrode was formed by the steps of mixing hydroxypropylmethyl cellulose to the alloy particles as a binder, packing the mixture into a foamed nickel base, and rolling the packed nickel base with a roller press to a designated thickness. An electrode was fabricated by providing holes of 100 microns in diameter in a rate of 100 holes/cm 2 at both planes of the rolled body. A sealed nickel-metal hydride battery of AA-size was prepared with the above electrodes as same as the embodiment 1, and the discharging capacity of the battery was determined. When the battery was charged with 0.3 C and discharged with 0.2 C, the discharging capacity was as small as 750 mAh, and the cycle life was as short as 325 cycles. When the discharging was changed to 3 C, the discharge capacity decreased to 72 %, and when the charging was changed to 3 C, the discharge capacity decreased to 70 %. (Comparative example 3) An alloy of Ti 0.2 Zr 0.8 Ni 1.1 Mn 0.6 V 0.2 was used as a hydrogen storage alloy for composing a negative electrode, and the alloy particles having an average diameter of 50 microns were prepared by the same method as the comparative example 1. Then, an electrode was formed by the steps of mixing hydroxypropylmethyl cellulose as a binder and Raney nickel catalyst powder to the alloy particles, packing the mixture into a foamed nickel base, and rolling the packed nickel base with a roller press to a designated thickness. A sealed nickel-metal hydride battery of AA-size was prepared as same as the embodiment 1, and the discharging capacity of the battery was determined. When the battery was charged with 0.3 C and discharged with 0.2 C, the discharging capacity was as slightly small as 850 mAh, and the cycle life was as short as 383 cycles. When the discharging was changed to 3 C, the discharge capacity decreased to 72 %, and when the charging was changed to 3 C, the discharge capacity decreased to 68 %. (Embodiment 2) Graphite powder was used as a carbon material for the negative electrode. The graphite powder was pulverized to fine powder of which average diameter was equal to or less than 0.1 micron. The graphite powder was mixed with copper powder of 0.01 micron in diameter by 0.2 % by weight, and treated thermally at 3000 °C for five hours with agitating. Subsequently, the thermally treated powder is pulverized again in order to obtain the above particle size used in the present invention. The particle was processed by a dissolving treatment with a nitric acid aqueous solution at 70 °C for two hours, and washed sufficiently with water. Subsequently, the surface of the particle was observed by a SEM-EDX, and the fine pores having an average diameter of 0.01 ∼ 0.05 microns and trace of copper were confirmed. Other than the dissolving treatment with a warm KOH aqueous solution, the same result was obtained by flowing chlorine gas or fluorine gas to react with the precipitated phase for evaporation. A carbon electrode having a designated thickness was prepared by the steps of mixing a fluorine group binder with the particles, applying the particles onto a copper foil, and rolling with a roller press. As for a positive electrode, an electrode composed of mainly LiCoO 2 was used. A sealed lithium battery of AA-size was prepared using the above electrodes, and the capacity of the battery was determined. The battery capacity was designed to be 600 mAh. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity was as large as 650 mAh, and the cycle life was as long as 520 cycles. When the discharging was changed to 3 C, the capacity decreased to 92 %, and when the charging was changed to 3 C, the discharge capacity decreased to 89 %. (Comparative example 4) Graphite powder was used as a carbon material for the negative electrode. The graphite powder was pulverized to fine powder of which average diameter was equal to or less than 0.1 micron. The graphite powder was treated thermally at 3000 °C for five hours with agitating. The particle was processed by a dissolving treatment as same as the embodiment 2, and subsequently, the surface of the particle was observed by a SEM-EDX. However, the fine pores were not observed. A carbon electrode having a designated thickness was prepared by the steps of mixing a fluorine group binder with the particles, applying the particles onto a copper foil, and rolling with a roller press. As for a positive electrode, an electrode composed of mainly LiCoO 2 was used. A sealed lithium battery of AA-size was prepared using the above electrodes, and the capacity of the battery was determined. The battery capacity was designed to be 600 mAh. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity was as slightly small as 550 mAh, and the cycle life was as slightly small as 420 cycles. When the discharging was changed to 3 C, the capacity decreased to 72 %, and when the charging was changed to 3 C, the capacity decreased to 69 %. (Embodiment 3) Lithium-cobalt oxides were used as a material for composing the positive electrode. The lithium-cobalt oxides were pulverized to fine powder of which average diameter was equal to or less than 0.1 micron. The lithium-cobalt oxides powder was mixed with aluminum powder of 0.01 micron in diameter by 0.2 % by weight, and treated thermally at 300 °C for five hours with agitating. Subsequently, the thermally treated powder is pulverized again in order to obtain the above particle size used in the present invention. The particles were processed by a dissolving treatment with a KOH aqueous solution at 70 °C for two hours, and washed sufficiently. Subsequently, the surface of the particle was observed by a SEM-EDX, and the fine pores having an average diameter of 0.2 microns were confirmed. The same result was obtained by flowing chlorine gas or fluorine gas to react with the precipitated phase for evaporation. An electrode having a designated thickness was prepared by the steps of mixing a fluorine group binder with the particles, applying the particles onto an aluminum foil, and rolling with a roller press. As for a negative electrode, a carbon electrode was used. A sealed lithium battery of AA-size was prepared using the above electrodes, and the capacity of the battery was determined. The battery capacity was designed to be 600 mAh. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity was as large as 710 mAh, and the cycle life was as long as 580 cycles. When the discharging was changed to 3 C, the capacity decreased to 85 %, and when the charging was changed to 3 C, the capacity decreased to 80 %. (Comparative example 5) Lithium-cobalt oxides were used as a material for composing the positive electrode. The lithium-cobalt oxides were pulverized to fine powder of which average diameter was equal to or less than 0.1 micron, and treated thermally at 300 °C for five hours with agitating. The particles were processed by a dissolving treatment as same as the embodiment 3. Subsequently, the surface of the particle was observed by a SEM-EDX, but no fine pores were confirmed. An electrode having a designated thickness was prepared by the steps of mixing a fluorine group binder with the particles, applying the particles onto an aluminum foil, and rolling with a roller press. As for a negative electrode, a carbon electrode was used. A sealed lithium battery of AA-size was prepared using the above electrodes, and the capacity of the battery was determined. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity was slightly decreased to 570 mAh, and the cycle life was as short as 380 cycles. When the discharging was changed to 3 C, the capacity decreased to 65 %, and when the charging was changed to 3 C, the capacity decreased to 57 %. (Embodiment 4) An alloy of Ti 0.2 Zr 0.8 Ni 1.1 Mn 0.6 V 0.2 was used as a hydrogen storage alloy for composing a negative electrode. The hydrogen storage alloy was mixed with boron having an average diameter of 0.1 ∼ 10 microns by 0.01 to 0.1 by atomic ratio, and the alloy was obtained by the same method as the embodiment 1. The alloy was pulverized to particles having an average diameter of 50 microns. The fine pores were formed by the same method as the embodiment 1. The average diameter of the fine pores obtained by the above procedure was in a range of 0.4 ∼ 25 microns (1/150 to 1/2 of the average particle size of the alloy). Then, an electrode was formed by the same steps as the embodiment 1, a sealed nickel-metal hydride battery of AA-size was prepared with the above electrodes, and the capacity of the battery was determined. A relationship between a ratio of the average diameter of the fine pores to the average diameter of the alloy particles and the capacity ratio is shown in FIG. 6, when the battery was charged with 3 C and discharged with 3 C. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity of the battery was as large as 920 ∼ 1100 mAh, and the cycle life was as large as 500 ∼ 680 cycles. When the discharging was changed to 3 C, the capacity decreased to 75∼95 %, and when the charging was changed to 3 C, the capacity decreased to a range of 75 ∼ 95 %. Especially, the capacity was the largest when the average diameter of the fine pores was in a range of 1/5 to 1/50 of the average particle size of the alloy. (Comparative example 6) An alloy of Ti 0.2 Zr 0.8 Ni 1.1 Mn 0.6 V 0.2 was used as a hydrogen storage alloy for composing a negative electrode. The hydrogen storage alloy was mixed with boron having an average diameter of 0.05 microns by 0.1 by atomic ratio, and the alloy was obtained by the same method as the embodiment 1. The alloy was pulverized to particles having an average diameter of 50 microns. The fine pores were formed by the same method as the embodiment 1. The average diameter of the fine pores obtained by the above procedure was less than 0.3 microns (less than 1/150 of the average particle size of the alloy). Then, an electrode was formed by the same steps as the embodiment 1, a sealed nickel-metal hydride battery of AA-size was prepared with the above electrodes, and the capacity of the battery was determined. A relationship between a ratio of the average diameter of the fine pores to the average diameter of the alloy particles and the capacity ratio is additionally shown in FIG. 6, when the battery was charged with 3 C and discharged with 3 C. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity of the battery was as large as 910 ∼ 950 mAh, and the cycle life was as large as 480 ∼ 520 cycles. When the discharging was changed to 3 C, the discharge capacity decreased to 45∼65 %, and when the charging was changed to 3 C, the capacity decreased to a range of 55 ∼ 68 %. (Comparative example 7) An alloy of Ti 0.2 Zr 0.8 Ni 1.1 Mn 0.6 V 0.2 was used as a hydrogen storage alloy for composing a negative electrode. The hydrogen storage alloy was mixed with boron having an average diameter of 15 microns by 0.1 by atomic ratio, and the alloy was obtained by the same method as the embodiment 1. The alloy was pulverized to particles having an average diameter of 50 microns. The fine pores were formed by the same method as the embodiment 1. The average diameter of the fine pores obtained by the above procedure was more than 30 microns (more than 1/2 of the average particle size of the alloy). Then, an electrode was formed by the same steps as the embodiment 1, a sealed nickel-metal hydride battery of AA-size was prepared with the above electrodes, and a discharging capacity of the battery was determined. A relationship between a ratio of the average diameter of the fine pores to the average diameter of the alloy particles and the capacity ratio is additionally shown in FIG. 6, when the battery was charged with 3 C and discharged with 3 C. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity of the battery was as large as 920 ∼ 970 mAh, and the cycle life was as large as 450 ∼ 500 cycles. When the discharging was changed to 3 C, the capacity decreased to 45∼63 %, and when the charging was changed to 3 C, the capacity decreased to a range of 48 ∼ 66 %. (Embodiment 5) An alloy of Ti 0.2 Zr 0.8 Ni 1.1 Mn 0.6 V 0.2 B x (where, X = 0.01 ∼ 0.8) was used as a hydrogen storage alloy, and the fine pores were formed by the same method as the embodiment 1. A ratio of area occupied by the cross sectional area of the fine pores to the total surface area of the particles was in a range of 5 ∼ 80 %, and a ratio of volume occupied by the total volume of the fine pores was in a range of 0.2 ∼ 60 %. Then, an electrode was formed by the same steps as the embodiment 1, a sealed nickel-metal hydride battery of AA-size was prepared with the above electrodes, and a discharging capacity of the battery was determined. A relationship between a ratio of the cross sectional area of the fine pores to the total surface area of the particle and the capacity ratio is shown in FIG. 7, when the battery was charged with 3 C and discharged with 3 C. Furthermore, a relationship between a ratio of the total volume of the fine pores to the total volume of the particle and the capacity ratio is shown in FIG. 8, when the battery was charged with 3 C and discharged with 3 C. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity of the battery was as large as 920 ∼ 1150 mAh, and the cycle life was as large as 430 ∼ 580 cycles. When the discharging was changed to 3 C, the capacity decreased to 75∼95 %, and when the charging was changed to 3 C, the capacity decreased to a range of 75 ∼ 98 %. Especially, the capacity was large when the fine pores occupied 10 to 50 % in the surface area of the particle, or 1 to 40 % in the volume of the particle. (Comparative example 8) An alloy of Ti 0.2 Zr 0.8 Ni 1.1 Mn 0.6 V 0.2 B x (where, X = 0.001 ∼ 0.005) was used as a hydrogen storage alloy, and the fine pores were formed by the same method as the embodiment 1. A ratio of area occupied by the cross sectional area of the fine pores to the total surface area of the particles was 3 %, and a ratio of volume occupied by the total volume of the fine pores was 0.1 %. Then, an electrode was formed by the same steps as the embodiment 1, a sealed nickel-metal hydride battery of AA-size was prepared with the above electrodes, and a discharging capacity of the battery was determined. A relationship between a ratio of the cross sectional area of the fine pores to the total surface area of the particle and the capacity ratio is additionally shown in FIG. 7, when the battery was charged with 3 C and discharged with 3 C. Furthermore, a relationship between a ratio of the total volume of the fine pores to the total volume of the particle and the capacity ratio is additionally shown in FIG. 8, when the battery was charged with 3 C and discharged with 3 C. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity of the battery was as large as 950 mAh, but the cycle life was as short as 320 cycles. When the discharging was changed to 3 C, the capacity decreased to 50 %, and when the charging was changed to 3 C, the capacity decreased to 55 %. (Comparative example 9) An alloy of Ti 0.2 Zr 0.8 Ni 1.1 Mn 0.6 V 0.2 B x (where, X = 1.0 ∼ 1.8) was used as a hydrogen storage alloy, and the fine pores were formed by the same method as the embodiment 1. A ratio of area occupied by the cross sectional area of the fine pores to the total surface area of the particles was 90 %, and a ratio of volume occupied by the total volume of the fine pores was 70 %. Then, an electrode was formed by the same steps as the embodiment 1, a sealed nickel-metal hydride battery of AA-size was prepared with the above electrodes, and the capacity of the battery was determined. A relationship between a ratio of the cross sectional area of the fine pores to the total surface area of the particle and the capacity ratio is additionally shown in FIG. 7, when the battery was charged with 3 C and discharged with 3 C. Furthermore, a relationship between a ratio of the total volume of the fine pores to the total volume of the particle and the capacity ratio is additionally shown in FIG. 8, when the battery was charged with 3 C and discharged with 3 C. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity of the battery was as slightly small as 720 mAh, and the cycle life was as short as 300 cycles. When the discharging was changed to 3 C, the capacity decreased to 55 %, and when the charging was changed to 3 C, the capacity decreased to 60 %. (Embodiment 6) An alloy selected from the alloys shown in Table 1 was used as a hydrogen storage alloy composing a negative electrode, and a segregated phase was formed. Respective of the chemical elements, Al, V, Mn, Sn, B, Mg, Mo, W, Zr, K, Na, Li, Ni, and Ti, was contained in the segregated phase at least 30 % by weight. The alloy was treated by a dissolving process with an aqueous solution containing any one of an acid, an alkali, an oxidizing agent, or a reducing agent at 50 °C for one hour, washed with water. Then, an electrode was formed by the same steps as the embodiment 1, a sealed nickel-metal hydride battery of AA-size was prepared with the above electrodes, and the capacity of the battery was determined. The results are shown in Table 1. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity of the battery was as large as 970 ∼ 1010 mAh, and the cycle life was as long as 480 ∼ 550 cycles. When the discharging was changed to 3 C, the capacity decreased to 78 ∼ 95 %, and when the charging was changed to 3 C, the capacity decreased to 88 ∼ 95 %. Hydrogen storage alloy Treating solution 0.3 C-0.2 C (mAh) Cycle life (Cycles) 3 C discharge (%) 3C charge (%) (La Ce Nd Pr)-(Ni Mn Al Co) 4.5-5.5 KOH, NaBH 4 960 510 91 98 (La Ce Nd Pr)-(Ni Mn Al Co B) 4.5-5.5 KOH, HF 1000 520 92 90 (La Ce Nd Pr)-(Ni Mn Co W) 4.5-5.5 KOH, NaBH 4 1000 520 88 88 (La Ce Nd Pr)-(Ni Mn Al Co Mo) 4.5-5.5 KOH, HF 1010 510 95 90 (La Ce Nd Pr)-(Ni Mn Al Co Mg) 4.5-5.5 KOH, HF 980 500 94 98 (La Ce Nd Pr)-(Ni Mn Al Co K) 4.5-5.5 KOH, HNO 3 970 550 78 88 (La Ce Nd Pr)-(Ni Mn Al Co Na) 4.5-5.5 KOH, NaClO 970 550 79 89 (La Ce Nd Pr)-(Ni Mn Al Co Pd) 4.5-5.5 KOH, KPH 2 O 2 990 480 80 95 (La Ce Nd Pr)-(Ni Mn Al Co Sn) 4.5-5.5 KOH, NaPH 2 O 2 1000 490 95 98 (La Ce Nd Pr)-(Ni Mn Al Co Fe) 4.5-5.5 KOH, CH 2 O, HF 970 480 88 94 (Ca La Ce Nd Pr)-(Ni Mn Al Co) 4.5-5.5 KOH, H 2 O 2 , HF 1000 490 86 92 (Zr Ti)-(Ni Mn V Co B) 1.5-2.5 KOH, NaBH 4 1010 500 89 91 (Zr Ti Hf)-(Ni Mn V Co Mo) 1.5-2.5 KOH, NaClO 970 510 79 90 (Zr Ti Sc)-(Ni Mn V Co W) 1.5-2.5 KOH, HNO 3 , HF 990 550 93 89 (Zr Ti Mg)-(Ni Mn V Co K) 1.5-2.5 KOH, NaBH 4 990 550 94 88 (Zr Ti)-(Ni Mn V Co Pd) 1.5-2.5 KOH, H 2 O 2 , HF 980 510 79 89 (Zr Ti)-(Ni Mn V Co Sn) 1.5-2.5 KOH, HNO 3 , HF 980 550 81 97 (Zr Ti)-(Ni Mn V Co Fe) 1.5-2.5 KOH, HNO 3 , HF 990 490 84 91 (Zr Ti)-(Ni Mn V Co Cr) 1.5-2.5 KOH, HNO 3 , HF 1000 490 94 97 (Zr Ti)-(Ni Mn V Co Li) 1.5-2.5 KOH, NaBH 4 1010 480 83 90 (Zr Ti)-(Ni Mn V Co Fe) 1.5-2.5 KOH, HNO 3 , HF 1000 490 80 89 (Zr Ti)-(Ni Mn V Co Cr) 1.5-2.5 KOH, NaClO 980 480 90 96 (Zr Ti)-(Ni Mn V Co Al) 1.5-2.5 KOH, NaBH 4 970 500 93 97 (Zr Ti)-(Ni Mn V Co Cr Fe) 1.5-2.5 KOH, HNO 3 , HF 970 540 90 89 (Zr Ti)-(Ni Mn V Co C) 1.5-2.5 KOH, H 2 O 2 980 510 95 88 (Zr Ti)-(Ni Mn V Co Pb) 1.5-2.5 KOH, HNO 3 , HF 1000 490 91 97 (Zr Ti)-(Ni Mn V Co Sn) 1.5-2.5 KOH, HNO 3 , HF 1000 530 79 89 (Mg Zr Ti) 2.0 -(Ni Mn V Co B) 0.5-1.5 KOH, NaBH 4 970 480 78 89 (Mg Zr Ti) 2.0 -(Ni Mn V Co W) 0.5-1.5 KOH, NaClO 970 480 80 92 (Mg Zr Ti) 2.0 -(Ni Mn V Co MO) 0.5-1.5 KOH, NaBH 4 980 520 82 92 (Mg Zr Ti) 2.0 -(Ni Mn V CO) 0.5-1.5 KOH, HNO 3 , HF 1000 540 91 97 (Mg Zr Ti) 2.0 -(Ni Mn Al Co) 0.5-1.5 KOH, H 2 O 2 980 530 95 98 (Mg Zr Ti) 2.0 -(Ni Mn Al Co B) 0.5-1.5 KOH, NaBH 4 970 500 87 92 (Mg Zr Ti) 2.0 -(Ni Mn Al Co W) 0.5-1.5 KOH, HNO 3 , HF 970 510 89 94 (Mg Zr Ti) 2.0 -(Ni Mn V Co Mo) 0.5-1.5 KOH, NaClO 980 490 80 91 (Embodiment 7) Graphite powder was used as a carbon material for the negative electrode. The graphite powder was pulverized to fine powder of which average diameter was equal to or less than 0.1 micron. The graphite powder was mixed any one of the additive element selected from the chemical elements shown in Table 2 by 0.2 % by weight, the additive element was 0.01 micron in diameter, and treated thermally at 3000 °C for five hours with agitating. Subsequently, the thermally treated powder is pulverized again in order to obtain the above particle size used in the present invention. The particle was processed by a dissolving treatment with a nitric acid aqueous solution at 70 °C for two hours, and washed sufficiently with water. Subsequently, the surface of the particle was observed by a SEM-EDX, and the fine pores having an average diameter of 0.01 microns were confirmed. A sealed lithium battery of AA-size was prepared as same as the embodiment 2, and the capacity of the battery was determined. The results of the capacity determination are shown in Table 2. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity was as large as 670 ∼ 750 mAh, and the cycle life was as long as 480 ∼ 520 cycles. When the discharging was changed to 3 C, the capacity decreased to 82 ∼ 85 %, and when the charging was changed to 3 C, the capacity decreased to 79 ∼ 85 %. Additive element 0.3 C charge -0.2 C discharge (mAh) Cycle life (Cycles) 3 C Discharge (%) 3 C Charge (%) Fe 720 510 85 84 Ni 690 490 82 85 S 700 490 82 84 Si 710 500 82 80 Sn 690 520 83 79 Li 700 480 82 79 Na 670 490 82 79 K 750 480 85 80 Pb 740 480 85 79 FeO x 700 520 84 80 NiO x 710 500 82 85 SiO x 750 510 85 83 SnO x 710 510 83 84 LiO x 670 490 84 82 PbO x 680 500 84 81 (Comparative example 10) Graphite powder was used as a carbon material for the negative electrode. The graphite powder was pulverized to fine powder of which average diameter was equal to or less than 0.1 micron. The graphite powder was mixed with iron powder of 0.01 micron in diameter by 55 % by weight, and treated thermally at 3000 °C for five hours with agitating. The particles of the powder were processed by a dissolving treatment with a nitric acid aqueous solution at 70 °C for two hours, and washed sufficiently with water. Subsequently, the surface of the particle was observed by a SEM-EDX, and forming the fine pores having an average diameter of 0.8 microns were confirmed. A sealed lithium battery of AA-size was prepared as same as the embodiment 2, and the capacity of the battery was determined. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity was as small as 470 mAh, and the cycle life was as short as 380 cycles. When the discharging was changed to 3 C, the capacity decreased to 50 ∼ 71 %, and when the charging was changed to 3 C, the capacity decreased to 55 ∼ 64 %. (Comparative example 11) Graphite powder was used as a carbon material for the negative electrode. The graphite powder was pulverized to fine powder of which average diameter was equal to or less than 0.1 micron. The graphite powder was mixed with iron powder of 0.01 micron in diameter by 0.01 % by weight, and treated thermally at 3000 °C for five hours with agitating. The particles of the powder were processed by a dissolving treatment with a nitric acid aqueous solution at 70 °C for two hours, and washed sufficiently with water. Subsequently, the surface of the particle was observed by a SEM-EDX, and forming the fine pores having an average diameter of 0.04 microns were confirmed. A sealed lithium battery of AA-size was prepared as same as the embodiment 2, and the capacity of the battery was determined. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity was as large as 670 mAh, but the cycle life was as short as 280 cycles. When the discharging was changed to 3 C, the capacity decreased to 57 ∼ 72 %, and when the charging was changed to 3 C, the capacity decreased to 55 ∼ 69 %. (Embodiment 8) Polyacetylene powder was used as a conductive polymer material for the positive electrode. The polyacetylene powder was pulverized to fine powder of which average diameter was equal to or less than 0.1 micron. The polyacetylene powder was mixed with any one of the additive element selected from the chemical elements shown in Table 3, the additive element was powder of 0.05 micron in diameter, by 0.2 % by weight, and treated thermally at 300 °C ∼ 500 °C for five hours with agitating. Subsequently, the thermally treated powder was pulverized again in order to obtain the above particle size used in the present invention. The particle was processed by a dissolving treatment with a nitric acid aqueous solution at 70 °C for two hours, and washed sufficiently with water. Subsequently, the surface of the particle was observed by a SEM-EDX, and forming the fine pores having an average diameter of 0.08 microns were confirmed. Other than the dissolving treatment with a warm KOH aqueous solution, the same result was obtained by flowing chlorine gas or fluorine gas to react with the precipitated phase for evaporation. An electrode having a designated thickness was prepared by the steps of mixing a fluorine group binder with the particles, applying the particles onto an aluminum foil, and rolling with a roller press. As for a negative electrode, a carbon electrode was used. A sealed lithium battery of AA-size was prepared using the above electrodes, and the capacity of the battery was determined. The battery capacity was designed to be 500 mAh. The result of the capacity determination is shown in Table 3. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity was as large as 570 ∼ 640 mAh, and the cycle life was as long as 490 ∼ 670 cycles. When the discharging was changed to 3 C, the capacity decreased to 81 ∼ 91 %, and when the charging was changed to 3 C, the discharge capacity decreased to 78 ∼ 87 %. Additive element 0.3 C charge -0.2 C discharge (mAh) Cycle life (Cycles) 3 C Discharge (%) 3 C Charge (%) Fe 610 520 91 87 Ni 640 500 88 84 S 620 490 82 86 Si 640 500 85 87 Sn 600 510 84 85 Li 570 670 81 84 Na 570 620 83 79 K 580 600 84 78 Pb 570 610 82 85 FeO x 590 600 91 78 NiO x 600 490 81 80 SiO x 620 500 85 84 SnO x 590 550 86 87 LiO x 600 520 86 86 PbO x 590 550 82 79 (Embodiment 9) Polyacetylene powder was used as a conductive polymer material for the negative electrode. The polyacetylene powder was pulverized to fine powder of which average diameter was equal to or less than 0.1 micron. The polyacetylene powder was mixed with any one of the additive element selected from the chemical elements shown in Table 4 by 0.2 % by weight, the additive element was powder of 0.01 micron in diameter, and treated thermally at 1000 °C ∼ 3000 °C for five hours with agitating. Subsequently, the thermally treated powder was pulverized again in order to obtain the above particle size used in the present invention. The particle was processed by a dissolving treatment with a nitric acid aqueous solution at 70 °C for two hours, and washed sufficiently with water. Subsequently, the surface of the particle was observed by a SEM-EDX, and forming the fine pores having an average diameter of 0.02 microns were confirmed. Other than the dissolving treatment with a warm KOH aqueous solution, the same result was obtained by flowing chlorine gas or fluorine gas to react with the precipitated phase for evaporation. An electrode having a designated thickness was prepared by the steps of mixing a fluorine group binder with the particles, applying the particles onto a copper foil, and rolling with a roller press. As for the positive electrode, an electrode composed of mainly LiCoO 2 was used. A sealed lithium battery of AA-size was prepared using the above electrodes, and the capacity of the battery was determined. The battery capacity was designed to be 600 mAh. The result of the capacity determination is shown in Table 4. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity was as large as 700 ∼ 860 mAh, and the cycle life was as long as 580 ∼ 700 cycles. When the discharging was changed to 3 C, the capacity decreased to 88 ∼ 93 %, and when the charging was changed to 3 C, the discharge capacity decreased to 82 ∼ 90 %. Additive element 0.3 C charge -0.2 C discharge (mAh) Cycle life (Cycles) 3 C Discharge (%) 3 C Charge (%) Fe 860 660 91 88 Ni 760 700 88 90 S 740 650 90 82 Si 790 600 90 82 Sn 700 580 91 83 Li 710 600 88 85 Na 700 590 88 82 K 700 580 89 86 Pb 710 580 93 83 FeO x 860 580 90 89 NiO x 800 600 93 90 SiO x 810 660 92 88 SnO x 710 690 89 89 LiO x 700 700 93 82 PbO x 700 600 90 85 (Embodiment 10) Any one of the alloys shown in Table 5 was used as the negative electrode. The alloy was molten at a temperature in a range of 1100 °C to 1500 °C, cooled with a speed in a range of 0.01 °C/min. to 0.5 °C/min., and annealed at a temperature in a range of 300 °C to 500 °C. Then, the alloy was pulverized to particles, of which average diameter was equal to or less than 50 micron, processed by a dissolving treatment with a nitric acid aqueous solution at 70 °C for two hours, and washed sufficiently with water. Subsequently, the surface of the particle was observed by a SEM-EDX, and forming the fine pores having an average diameter of 2 microns were confirmed. The same result was obtained by flowing chlorine gas or fluorine gas to react with the precipitated phase for evaporation. An electrode having a designated thickness was prepared by the steps of mixing a fluorine group binder with the particles, applying the particles onto a copper foil, and rolling with a roller press. As for the positive electrode, an electrode composed of mainly LiCoO 2 was used. A sealed lithium battery of AA-size was prepared using the above electrodes, and the capacity of the battery was determined. The battery capacity was designed to be 600 mAh. The result of the capacity determination is shown in Table 5. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity was as large as 700 ∼ 760 mAh, and the cycle life was as long as 480 ∼ 530 cycles. When the discharging was changed to 3 C, the capacity decreased to 85 ~ 91 %, and when the charging was changed to 3 C, the discharge capacity decreased to 88 ~ 98 %. Additive element 0.3 C charge -0.2 C discharge (mAh) Cycle life (Cycles) 3 C Discharge (%) 3 C Charge (%) Si-Ni 760 510 91 98 Ge-Si 720 530 90 90 Mg-Si 700 480 85 91 Si-Ni-Ge 750 480 88 88 Si-Ni-Mg 700 500 91 90 Si-Ni-Mn 720 510 90 88 Si-Ni-Cu 750 480 88 95 (Embodiment 11) Any one of the oxides and sulfides shown in Table 6 was used as the positive electrode. The oxide or the sulfide was pulverized to particles, of which average diameter was equal to or less than 1 micron, mixed with the additive element shown in Table 6 by 0.2 % by weight, the additive element was powder of 0.1 micron in diameter, and treated thermally at 300 °C ∼ 900 °C for five hours with agitating. Then, the mixture was pulverized again in order to obtain particles having the above average diameter suitable for the present invention. The particles were processed by a dissolving treatment with a nitric acid aqueous solution at 70 °C for two hours, and washed sufficiently with water. Subsequently, the surface of the particle was observed by a SEM-EDX, and forming the fine pores having an average diameter of 0.2 microns were confirmed. The same result was obtained by flowing chlorine gas or fluorine gas to react with the precipitated phase for evaporation. An electrode having a designated thickness was prepared by the steps of mixing a fluorine group binder with the particles, applying the particles onto an aluminum foil, and rolling with a roller press. As for the negative electrode, a carbon electrode was used. A sealed lithium battery of AA-size was prepared using the above electrodes, and the capacity of the battery was determined. The battery capacity was designed to be 600 mAh. The result of the capacity determination is shown in Table 6. When the battery was charged with 0.3 C and discharged with 0.2 C, the capacity was as large as 680 ∼ 770 mAh, and the cycle life was as long as 490 ∼ 640 cycles. When the discharging was changed to 3 C, the capacity decreased to 81 ∼ 90 %, and when the charging was changed to 3 C, the discharge capacity decreased to 78 ∼ 85 %. In accordance with the present invention, the secondary battery was improved significantly in increasing the capacity, the rapid charging characteristics, and the rapid discharging characteristics. Composition of positive electrode Additive element 0.3 C charge-0.2 C discharge (mAh) Cycle life (cycles) 3 C discharge (%) 3 C charge (%) LiCoO 1.5∼2.5 Al 760 490 81 82 LiMnO 1.5∼2.5 Sn 770 510 88 85 LiNiO 1.5∼2.5 Mn 690 550 90 85 LiFeO 1.5∼2.5 B 700 540 87 84 Li(Co Cr) 1.0 O 1.5∼2.5 K 710 490 87 78 Li(Co Pb) 1.0 O 1.5∼2.5 Na 700 610 88 85 Li(Co Bi) 1.0 O 1.5∼2.5 Al 700 640 81 79 Li(Ni Nb) 1.0 O 1.5∼2.5 Sn 750 610 90 80 Li(Ni Mo) 1.0 O 1.5∼2.5 Al 680 500 87 79 Li(Ni Sr) 1.0 O 1.5∼2.5 B 710 490 86 80 Li(Ni Ta) 1.0 O 1.5∼2.5 Sn 770 550 88 79 Li(Ni Fe) 1.0 O 1.5∼2.5 Al 750 550 89 79 Li(Ni Co) 1.0 O 1.5∼2.5 Al 700 600 81 78 Li(Co Mn) 1.0 O 1.5∼2.5 Sn 710 610 85 85 Li(Ni Mn) 1.0 O 1.5∼2.5 Al 720 640 84 84 Li(Ni Fe) 1.0 O 1.5∼2.5 Al 740 610 81 81 Li(Fe Co) 1.0 O 1.5∼2.5 B 700 640 90 79 Li(Fe Mn) 1.0 O 1.5∼2.5 Al 680 610 89 85 LiMn 2.0 O 3.0∼5.0 Sn 680 600 90 83 TiS 1.5∼2.5 Al 690 590 90 84 MoS 1.5∼2.5 B 710 490 88 80 (Mo Fe) 1.0 S 1.5∼2.5 Al 690 500 87 80 (Mo Ta) 1.0 S 1.5∼2.5 Sn 680 490 81 80 (Mo Sr) 1.0 S 1.5∼2.5 Al 730 500 89 78 (Mo Ni) 1.0 S 1.5∼2.5 B 680 520 88 83 (Mo Nb) 1.0 S 1.5∼2.5 Al 710 510 87 82 (Mo Pb) 1.0 S 1.5∼2.5 Sn 700 550 89 85 (Mo Cu) 1.0 S 1.5∼2.5 K 680 510 90 80 (Mo V) 1.0 S 1.5∼2.5 K 710 580 88 82 (Mo MN) 1.0 S 1.5∼2.5 B 750 620 87 79 LiV 3 O 6.0∼10.0 B 770 560 87 84 CuV 2 O 4.5∼7.5 B 750 560 82 80

Claims: A secondary battery comprising a positive electrode, a negative electrode, and an electrolyte which separates said electrodes, wherein: said positive electrode or said negative electrode contains particles composed of a material which contributes to a charge-discharge reaction, said particles comprise at least two phases, one phase being disposed within another, and at least one phase of said phases comprises fine pores, characterized in that the pores are formed by dissolution or evaporation of at least one of the phases. A secondary battery as claimed in claim 1, wherein said fine pores exist at the surface of said particles, whereon said particle contacts with said electrolyte. A secondary battery according to claim 1, wherein the composition of the surface of said fine pores differs from the composition of the surface of said particles around said fine pores. A secondary battery as claimed in claim 3, wherein: said fine pores have at least one transition metal at the surface of the pore. A secondary battery as claimed in any one of claims 1 to 4, wherein: said particles are composed of an alloy containing at least two chemical elements, said alloy comprises a first phase and at least another second phase which is precipitated in said first phase, and at least one of said second phases comprises said fine pores. A secondary battery as claimed in any one of claims 1 to 4, wherein: said particles comprise carbon having at least one phase, and the surface of said carbon comprises fine pores formed by dissolution or evaporation of at least one of said phases. A secondary battery as claimed in any one of claims 1 to 4, wherein: said particles are composed of an oxide or a sulfide containing at least two chemical elements, said oxide or sulfide comprises a first phase and at least another second phase which is precipitated in said first phase, and at least one of said second phases comprises said fine pores. A secondary bactery as claimed in claim 1, wherein: said particles have an average particle diameter equal to or less than 2 mm, and said particle comprises fine pores having an average diameter in a range of 1/2 to 1/150 of the average particle diameter of said particles. A secondary battery as claimed in claim 1, wherein: said particle comprises fine pores having a total surface area in a range of 5 % to 80 % of the surface area of said particles. A secondary battery as claimed in claim 1, wherein: said particle comprises fine pores having a total volume in a range of 0.2 % by volume to 60 % by volume of the volume of said particles. A secondary battery according to one of the claims 1 to 10, wherein said particles are hydrogen storage alloy particles in the negative electrode composed of an alloy containing at least a chemical element selected from a group consisting of magnesium, lanthanum, cerium, praseodymium, neodymium, titanium, zirconium, hafnium, palladium, yttrium scandium, calcium, aluminum, cobalt, chromium, vanadium, manganese, tin, boron molybdenum, tungsten, carbon, lead, iron, nickel, potassium, sodium, and lithium, said fine pores being formed by dissolving at least one of said phases to be dissolved. A secondary battery as claimed in claim 11, wherein: said phase to be dissolved contains at least a chemical element selected from a group consisting of aluminum, vanadium, manganese, tin, boron, magnesium, molybdenum, tungsten, zirconium, potassium, sodium, lithium, nickel, and titanium, by at least 40 % by weight. A secondary battery as claimed in claim 11, wherein: said fine pores are formed by dissolution with said electrolyte. A secondary battery as claimed in claim 1, wherein: said negative electrode is composed of carbon as a main component, said carbon comprises at least a phase which is composed of at least a pure material or an oxide of a chemical element selected from a group consisting of iron, nickel, sulfur, silicon, tin, lithium, sodium, potassium, and lead, and said carbon comprises fine pores which are formed by dissolution or evaporation of at least one of said phases with at least one of an acid, an alkali, an oxidizing agent, or a reducing agent. A secondary battery as claimed in claim 1, wherein: said positive electrode or negative electrode is composed of conductive polymers, said conductive polymer comprises at least a phase which is composed of at least a pure material or an oxide of a chemical element selected from a group consisting of iron, nickel, sulfur, silicon, tin, lead, lithium, sodium, and potassium, and said conductive polymer comprises fine pores which are formed by dissolution or evaporation of at least one of said phases with at least one of an acid, an alkali, an oxidizing agent, or a reducing agent. A secondary battery as claimed in claim 1, wherein: said negative electrode is composed of an alloy having at least a chemical element selected from a group consisting of nickel, silicon, germanium, magnesium, copper, and manganese, said alloy comprises at least two phases, and said negative electrode comprises fine pores which are formed by dissolution or evaporation of at least one of said phases with at least one of an acid, an alkali, an oxidizing agent, or a reducing agent. A secondary battery as claimed in claim 1, wherein: said positive electrode comprises a first phase which is composed of: an oxide containing at least a chemical element selected from a group consisting of lead, manganese, vanadium, iron, nickel, cobalt, copper, chromium, molybdenum, titanium, niobium, tantalum, strontium, and bismuth, a sulfide containing at least a chemical element selected from a group consisting of titanium, molybdenum, iron, tantalum, strontium, lead, niobium, copper, nickel, vanadium, bismuth, and manganese, or a complex compounds containing said oxide, or sulfide with lithium, and at least a second phase which is composed of: a pure element, or an oxide containing at least a chemical element selected from a group consisting of aluminum, tin, boron, magnesium, potassium, and sodium, and said positive electrode comprises fine pores which are formed by dissolution or evaporation of at least one of said phases with at least one of an acid, an alkali, an oxidizing agent, or a reducing agent. A method for manufacturing an electrode for a secondary battery as claimed in one of the claims 1 to 17, comprising the steps of: preparing said negative electrode by fabricating particles composed of material which contributes a battery reaction, and forming fine pores by dissolving or evaporating at least one of second phases, which are dispersed in a first phase, with at least one of an acid, an alkali, an oxidizing agent, or a reducing agent. A method as claimed in claim 18, comprising the steps of: forming said particles of a material contributing to a battery reaction, said material including a first phase and a second phase which is dispersed in said first phase, by reacting components of said first phase with components of said second phase, pulverizing said particles including said first phase and said second phase which is dispersed in said first phase, forming fine pores at surface of said particle by any of dissolving or evaporating said second phase of the pulverized particle with any of an acid, an alkali, an oxidizing agent, or a reducing agent, and An electrode for a secondary battery, the electrode containing particles composed of material contributing to a charge-discharge reaction, said particles comprise at least two phases, one phase being disposed within another, and fine pores characterized in that the pores are formed by dissolving or evaporating at least one of said phases. fabricating the particles having said fine pores to a plate like shape. An electrode for a secondary battery as claimed in claim 20, wherein: said particle contains material contributing to said charge-discharge reaction, said particle comprises fine pores at its surface, and a composition at the surface of said fine pores differs from the composition at the surface of said particle around said fine pores. An electrode for a secondary battery as claimed in claim 20, wherein: said fine pore comprises at least one of transition metals at its surface.

Inventors: KYOKO IKAWA, TATSUO HORIBA, YASUSHI MURANAKA, YOSIMI KOMATU, KYOKO, IKAWA, TATSUO, HORIBA, YASUSHI, MURANAKA, YOSIMI, KOMATU
Applicants: HITACHI CHEMICAL CO LTD, HITACHI LTD, HITACHI CHEMICAL CO., LTD., HITACHI, LTD.
Application year: 1996
Main classification: H01M4
IPC codes: H01M4, H01M10