ABRASION RESISTANT QUASI MONOFILAMENT AND SHEATHING COMPOSITION

Abstract: Aquasi monofilament having a high strength polyethylene fiber core with an adherent, abrasion resistant polymer sheath is prepared by feeding the core yarn through a crosshead die, while simultaneously supplying a polymer melt at a temperature greater than themelting point of the core yarn to the die, for sheathing the core yarn within the die with the melt under a sufficient pressure to cause the melt to adhere to the core yarn. The abrasion resistant polymer sheath includes an effective amount of a first polymer having ethylene crystallinity, a density of at least about 0.94 g/cm<3>, and a melt index of less than about 0.1 g/10 min. The composition used to sheath the core yarn is characterized by a weight average tensile strength at yield of greater than about 13.8 MPa. The quasi monofilament has utility in applications subjected to high abrasion, such as sports fishing lines, kite lines, dental floss, "weedeater" lines and tennis racket strings.

Description: ABRASION RESISTANT QUASI MONOFILAMENT AND SHEATHING COMPOSITION BACKGROUND OF THE INVENTION 1 Field of the Invention The present invention relates to an abrasion resistant quasi monofilament, as well as to a sheathing composition used in a process to make the quasi monofilament. More particularly, this invention relates to a quasi monofilament having a high strength polyethylene fiber core with an adherent, abrasion resistant polymer sheath and to the sheathing composition used to make same. 2. Prior Art Polyethylene yarns having very high tenacity have previously been described in U.S. Patents 4,413,110, 4,430,383, 4,436,689, 4,536,536, and 4,545,950. The nature of the spinning processes used to prepare these yarns is such that individual filaments are typically of low denier and consequently break at low applied loads. To remedy this, multi-filament yarns may be used or several multi-filament yarns may be formed into a braid. However, such multi-filament yarns or braids are "limp", i.e., they have little flexural rigidity, and consequently bend easily when subjected to a transverse force. Additionally, in applications subjected to high abrasion, the individual low denier filaments of the multi- filament yarns may be rapidly worn through to produce debris or fibrillations which can snag or otherwise compromise the utility of the yam or braid. In such applications it would therefore be highly desirable to have an article of high tenacity and high denier possessing high absolute breaking load together with flexural rigidity and high abrasion resistance. Examples of such applications are sports fishing lines, kite lines, dental floss, "weedeater" lines and tennis racket strings. High strength polyethylene fibers or yams coated with polyethylene or in a polyethylene matrix material are known. U.S. Patent No. 4,501,856 discloses a composite of high strength polyethylene fibers in a matrix material which "may be any of the various known forms of polyethylene, including low density polyethylene (density of between 0.90 and 0.94 g/cm 3 ), high density (between 0.94 and 0.98 g/cm 3 ), linear low density or other conventional forms." U.S. Patents 4,543,386 and 4,563,392 describe composites wherein high strength polyethylene fibers are coated on at least a portion of their surface with a solution of high density or low density polyethylene. U.S. Patents 4,403,012 and 4,916,000 also mention coating high strength polyethylene fibers with polyethylene. JP-A-6022666 describes the preparation of fishing line which is composed of ultrahigh molecular weight polyethylene fibers which have been dipped in polyethylene wax at less than 90°C. The extrusion coating of aramid fiber bundles or ropes with polyethylene is also known. U.S. Patent 4,202,164 describes a thermoplastic coated aramid rope wherein the coating can be polyethylene extruded under pressure into the interstices of the rope. U.S. Patent 4,050,230 describes covering an uncured, thermosetting resin-coated bundle of aramid or glass fibers with molten polyethylene, for example by extrusion coating with the melt at a temperature of 200° C. and under vacuum. None of these publications, however, describes a product prepared by crosshead pressure extrusion sheathing at a temperature above the melting point of the core fibers. These documents also tail to describe a sheathing composition comprising as a critical component thereof a polymer having ethylene crystallinity, a density of at least 0.94 g/cm 3 , and a melt index of less than about O. lg/lO min. SUMMARY OF THE INVENTION There is provided according to the present invention a quasi monofilament of indefinite length comprising (a) a core of polyethylene multi-filament ya having a tenacity of at least about 15 grams per denier (g/d) and a tensile modulus of at least about 500 g d; and adhered thereto (b) an abrasion resistant sheath comprising an effective amount of a first polymer having ethylene crystallinity, a density of at least about 0.94 g cm 3 and a melt index of less than about 0.1 g/10 min. The sheath preferably also comprises an effective amount of a compatible processing aid. The present invention is also a composition for sheathing a core of polyethylene multi-filament yam having a tenacity of at least about 15 g/d and a tensile modulus of at least about 500 g/d to make the ya abrasion resistant. The composition is characterized by a weight average tensile strength at yield of greater than about 13.8 MPa and by an ability to crosshead die sheathe under pressure a polyethylene core yam when the composition is in a melt state and at a temperature higher than the melting point of the ya . The quasi monofilament of the invention is a unique and useful article possessing the high tensile properties and low elongation of the core yam combined with the flexural rigidity of a monofilament. It is particularly advantageous as sports fishing line and in numerous other applications. BRIEF DESCRIPTION OF THE DRAWINGS The invention will be more fully understood and further advantages will become apparent when reference is made to the following detailed description of the invention and the accompanying drawings in which: FIG. 1 is a top view in section of apparatus used in Comparative Examples 19 through 27 and in Examples 28 through 55 of the invention; FIG.2 is a top view in section of apparatus similar to that used in Comparative Examples 1 through 18; and FIG.3 is a scanning electron micrograph of the cross-section of the quasi monofilament prepared in Example 45. DESCRIPTION OF THE PREFERRED EMBODIMENTS By "quasi monofilament" is meant an article which has the look and feel of a monofilament, i.e., a single untwisted synthetic filament, but which actually comprises a sheathed multi-filament core yarn, which may have been twisted prior to sheathing. The present invention is a quasi monofilament of indefinite length comprising (a) a core of polyethylene multi-filament yam of very high tenacity and tensile modulus and (b) an adherent, abrasion resistant sheath of a polymeric material deposited on the core by a process of crosshead pressure extrusion at melt temperatures in excess of the melting point of the core yam. This structure is new, novel and useful. Preferably, the core yam consists of polyethylene filaments having a weight average molecular weight in excess of about 300,000 kg/kg-mole, a tenacity of at least about 15 g d, and a tensile modulus of at least about 500 g/d. The intrinsic viscosity of the core yam may be about 3 to about 29 dl/g as measured in decalin at 135°C, more preferably about 7 to about 15 dl/g. The core yam of this invention can be made by the method of U.S. Patents 4,551,296 or 4,413,110 or by the methods described in EP 205 960B, all of which are hereby incorporated by reference. Tensile properties referred to herein are determined through utilization of an Instron tensile tester using a 10 inch gauge length and a strain rate of 100 percent per minute, in accordance with ASTM D2256. The polyethylene core yam may be composed of from about 5 to about 9600 individual filaments of about 0.5 to about 20 denier/filament (dpf). More preferably, the core yam is composed of from about 30 to about 400 filaments of about 1 to 10 dpf. The core yam may be twisted or untwisted, but preferably is twisted with about 0.1 to about 20 turns/inch (tpi), more preferably with about 0.5 to about 15 tpi, the lower twist count being used for higher yam deniers and the higher twist count being used for lower yam deniers. The sheathing composition can be any polymeric material that exhibits satisfactory adhesion to the core yam and resistance to abrasion in accordance with Federal Motor Vehicle Safety Standard 209, modified as follows. The quasi monofilament to be tested for adhesion and abrasion resistance is clamped at one end and subjected to a reciprocating motion in a horizontal direction over a distance of 32 cm at a frequency of 0.5 Hz. To the other end of the line is suspended a 1 oz. weight. At a point between the two ends of the line, it passes through and bears against a fishing rod guide ("Hardloy" silicon carbide guide by Fuji) of 8 mm diameter. As the line passes through the guide, the direction of the line is changed from horizontal to vertical. At the completion of 2500 cycles of reciprocating motion against the fishing rod guide, the line is detached from the apparatus and visually examined for signs of abrasion or detachment of the sheath from the core. If there are no signs of detachment, the adhesion/abrasion property of the sheath is rated as "satisfactory". If abrasion has exposed areas of the core yarn, the adhesion/abrasion property of the sheath is rated as "unsatisfactory." Preferably, the sheathing composition possesses a weight average tensile strength at yield in excess of about 13.8 MPa by application of the rule of mixtures to its components. By "weight average tensile strength at yield" is meant the sum of the products of the weight fractions and tensile strengths of each of the components. The tensile strength at yield of the individual components is measured by ASTM Standard D638. Higher weight average tensile strengths of the sheathing composition and higher twist levels of the core fibers are preferred so as to provide greater flexural rigidity and also to reduce flattening of the article in the fishing line application caused by bearing against the fishing pole guides. Preferably the sheathing composition comprises a polyolefin, polyolefin copolymer or polyolefin blend. Components of the sheath may include, but are not limited to, high density polyethylene, low density polyethylene, linear low density polyethylene, ethylene copolymers with non-olefinic monomers, ethylene- propylene copolymer, polyethylene wax, antioxidant, colorant and ultraviolet light stabilizer. The sheathing composition preferably includes a processing aid in combination with an effective amount of a first polymer having ethylene crystallinity, a density of at least about 0.94 g/cm 3 as measured by ASTM D972, and a melt index of less than about 0.1 g/10 min. as measmed by ASTM D1238 at condition 190°C./2.16 kg. The Comparative Examples which follow will show that using polymers having a density of less than about 0.94 g/cm 3 and a melt index of greater than about 0.1 g/10 min. for the first sheath polymer produces sheathed yams having poor adhesion and abrasion resistance. The processing aid has the effect of increasing the flow of the first sheath polymer. The choice of processing aid is not critical so long as its melting point is below the processing temperature, its melt index is greater than that of the first sheath polymer, and it is thermally stable at the processing temperature. A processing aid meeting these characteristics is deemed compatible with the first sheath polymer. Suitable processing aids may include polymers having ethylene crystallinity and a melt index exceeding about 1 g/10 min, as well as waxes. In a preferred embodiment, the sheathing composition is a blend which includes about 15 to about 95, more preferably about 25 to about 75, weight percent of the first polymer as defined above, which is preferably polyethylene. The blend further comprises, as a processing aid, about 5 to about 85, more preferably about 25 to about 75, weight percent of a polymer having ethylene crystallinity, a melt index exceeding about 1 g/10 min and a density of greater than about 0.94 g/cm 3 . The preferred melt index for the second polymer ranges from about 1 to about 100 g/10 min. The sheathing composition optionally comprises about 1 to about 20 weight percent, more preferably about 2 to about 10, weight percent of a processing aid consisting of a wax, preferably polyethylene wax. The polyethylene wax has a density of at least about 0.92 g/cm 3 and a viscosity at 140°C. of at least about 50 cps Brookfield viscosity. All weight percents are on the weight of the blend. Blends of blends can also be used. The sheath should form about 10 to about 90 weight percent of the quasi monofilament article, the proportion to be determined in relation to the end-use application. For fishing line, the sheath preferably forms about 15 to about 60 weight percent of the quasi monofilament article, and most preferably about 20 to about 45 weight percent. A process by which the quasi monofilament of the present invention can be made minimally comprises the following steps: (a) continuously feeding the core polyethylene multi-filament yam through a crosshead die, while simultaneously (b) supplying a polymer melt at a temperature greater than the melting point of the core yam to the die, for (c) sheathing the core yam within the die with the melt under a sufficient pressure to cause the melt to adhere to the core yam; and (d) cooling the sheathed ya to below the melting point of the polymer melt. These process steps and associated conditions will be described in detail below. There are also several optional process steps. These steps include twisting the core yam prior to the feeding step; pretreating the core yam, preferably after twisting, to enhance adherence of the melt to the core yam; stretching the core yam simultaneous with the sheathing step; and or post-stretching the sheathed core yam at a temperature within about 10°C. of the melting point of the core yam at a stretch rate of less than about 1 sec '1 and cooling under tension sufficient to maintain the high orientation of the core ya . The preferred process will depend upon the application; with sports fishing lines, the preferred process includes the optional step of twisting. The quasi monofilament article can be made by contacting the core yam with the desired sheath material where the sheath material is in a melt state. Advantageously, the core yam is withdrawn from a supply source and continuously fed through a melt of the sheath material in a crosshead pressure extrusion die where it is sheathed. From the die, the sheathed yam travels through a cooling zone to be taken up. A crosshead pressure extrusion die is also known as a wire-coating pressure die. A description of such a die is to be found in the Encyclopedia of Polymer Science and Engineering, Vol. 11, p.273, John Wiley & Sons, New York, 1988. In Figure 1, die 23 is held in place against crosshead die body 21 with die retaining ring 24 and associated bolt 25. Crosshead die body 21 has a melt feed channel 28 therein, characterized, as is typical of crosshead dies, by a 90 degree bend. Core tube 27 and associated guider tip 22, which have an axial bore 29 for passage of core yam 26 therethrough, are mounted within crosshead die body 21 so as to define an annular melt delivery channel at the exit end of guider tip 22. The exit end of guider tip 22 is within die 23. Core yam 26 enters axial bore 29 of core tube 27 and exits from guider tip 22 (left to right in the drawing figure). The melt, supplied by an extruder (not shown) to melt delivery channel 28 through entrance 30, flows around the 90 degree bend into the annular melt delivery channel to contact moving yam 26 at the exit end of guider tip 22 inside die 23. The melt sticks to and is pulled by moving yam 26 to sheathe the core yam 26. From the exit of die 23, the sheathed yam passes through an air gap to a water bath (not shown) where it is cooled to below the melting point of the polymer melt. From the water bath, the cooled sheathed yam is taken up (also not shown). The water bath can be eliminated by providing an air gap sufficient in length to cool the sheathed yam to below the melting point of the polymer melt; in this case, the yam runs through the cooling zone (air gap) to a pair of rubber covered nip rolls to be taken up. If the option of stretching the core yam simultaneous with sheathing is desired, a conventional yam feeding device can be provided, upstream of the crosshead die, with the capability of restraining the yam against the tension of a take-up device located on the exit side of the crosshead die. The processing conditions, particularly the melt temperature, pressure, and flow rate, and the yam velocity are such that the sheath material adheres to the core yam. Adhesion is generally benefited by higher melt temperatures, pressures and flow rates and lower ya velocity through the melt. However, it will be recognized that if melt temperature is too high and yam velocity is too low, the yam will lose a large proportion of its molecular orientation and strength in the crosshead die. At sufficiently high melt temperature and low yam velocity, the yam will melt and sheathing becomes impossible. Surprisingly, it is found that the requisite combination of adhesion and operability are obtained when the melt temperature of the sheath material is above the melting point of the core yam. Yam melting point is determined by Differential Scanning Calorimeter (DSC) at a heating rate of 10°C./min. Preferably the melt temperature is at least about 25°C, more preferably at least about 50°C, above the yam melting point. As a practical matter, melt temperatures range from about 190 to about 260°C. Melt temperature is measured by means of a thermocouple inserted in the melt stream within or immediately preceding the crosshead die. Pressure of the melt on the core yam in the crosshead die assists adhesion. It is preferred that the crosshead melt pressure at the melt entrance 30 be at least about 3.4 MPa. It will be understood that the actual pressure of the melt on the core yam will be somewhat less than measured as a result of pressure drops in the die. Preferred ya velocities range from about 90 to about 900 meters per minute (m/min), more preferably about 150 to about 600 rri/ in. The melt is supplied at a melt throughput sufficient to form from about 10 to about 90, more preferably about 15 to about 60, most preferably about 20 to about 45 weight percent of the sheathed core yam. The preferred melt flow rate, or throughput, ranges from about 0.4 to about 10 kg/hr, more preferably about 2 to about 5 kg/hr. Yam residence time in die 23 typically ranges from about 0.001 to about 0.10, more preferably about 0.01 to about 0.05, seconds. Pretreatment of the core yam to enhance adherence of the melt thereto preferably occurs after twisting just prior to extrusion sheathing. There are several alternate pretreatments available. The surface of the core yam can be exposed to a high voltage corona or plasma. Greater detail on plasma treatment can be found in Kaplan, S.L. et al., Gas Plasma Treatment of SpcctraΦFibcr. SAMPE Quarterly, Vol. 19, No. 4, July 1988, pp. 55-59, hereby incorporated by reference. Additionally or altematively, the surfaces of the individual fibers of the core ya can be primed with an effective amount of a resin having ethylene crystallinity and a melting point of less than about 135°C. Preferred primers are PRIMACOR® ethylene-acrylic acid copolymers, grades 5980 and 5990 manufactured by the Dow Chemical Company, and A-CΦX-413 ethylene-acrylic acid polyamide graft copolymers manufactured by AlliedSignal, Inc. The primers are preferably applied to the yam as a dispersion in water and the yam then dried. Altematively, the surface of the core yam can be scoured to remove any residual finish therefrom. As yet another alternative/additional pretreatment, the surface of the core ya can be wetted with an effective amount of mineral oil to soften or solvate the surface: These two latter pretreatments preferably occur prior to twisting. The post-stretching step takes place after the sheathed yam has been cooled. Preferably the sheathed core yam is post-stretched at least about 50 percent, more preferably at least about 100 percent, at a temperature within about 10°C. of the melting point of the core yarn, at a stretch rate of less than about 1 sec '1 , and the ost-stretched sheathed ya is cooled under tension sufficient to retain the highly oriented state of the core yam. By stretch rate is meant the stretching velocity difference divided by the length of the stretching zone. For example if fiber or ya being stretched is fed to the stretch (draw) zone often meters at ten meters per minute (m/min) and withdrawn at a rate of twenty m/min; the stretching rate would be (20 m/min- 10 m/min) divided by 10 m which equals one minute "1 . See U.S. 4,422,993, hereby incorporated by reference, at column 4, lines 26 to 31. Post-stretching is described in greater detail in EP 205 960B. The advantageous properties achieved through post-stretching the sheathed core ya are higher tenacity, higher tensile modulus, lower ultimate elongation and smoother surface texture. The quasi monofilament thus prepared consists of the core yam and a surrounding adherent sheath. Some penetration of the core yam by the sheath polymer has occurred but the sheath does not fill the interstices of the polyethylene core like "coated" fibers of the prior art. Here, the sheath material is prima- iή it '.he surface with some penetration into the core fiber bundle, as illustrated :n Figure 3. In the prior art, the coating completely penetrated the ya bundle. Thus, at equal deniers of the base yams and final products, the diameter of the quasi monofilament of the present invention is larger than that of the solution coated yam bundle of the prior art where the coating would primarily lie in the interstices between filaments. The invention will be illustrated by the examples and comparative examples which follow. A description of the components of the sheathing compositions evaluated is given in Table I. Comparative Examples 1 - 8 A single screw extruder of 2.54 cm diameter and 25:1 L/D was fitted with a crosshsad diϊ of 0.107 cm exit diameter. Polymer feed to the extruder consisted of an ethylene-acrylic acid copolymer containing 19.6 percent acrylic acid available from Dow Chemical under the designation XU-6075 1.15 (Table I). The polymer had a 270 melt index measured by ASTM D1238 at 125°C./2.16 kg and a tensile strength at yield of 7.58 MPa. The polymer was melted and conveyed by the screw extruder to a crosshead vacuum die similar to that depicted in Figure 2, which is found in the Handbook of Plastic Materials and Technology, p. 1208, John Wiley & Sons, Inc., New York (1990). Parts which correspond to those of Figure 1, previously described, are designated by the same numeral with a prime. The design of the crosshead die was such that the extruded polymer melt contacted core yam 26 immediately at the exit of die 23' rather than in the interior of die 23'. A vacuum connection to the interior of die 23' along the yam path aided in pulling the melt into contact with yam 26. The pressure of the melt on the core yam was equal to the vacuum reading as set forth in Table π. Traversing through the crosshead die in a direction perpendicular to the axis of the extruder was a 60 filament SPECTRA® 900 high strength polyethylene yam of 650 total denier, commercially available from AlliedSignal, Inc. It was of 28 g/d tenacity, 1200 g/d modulus, 1,300,000 kg/kg-mole molecular weight and possessed a melting point of 147°C. After contacting the polymer melt at the exit of the crosshead die and passing through an air gap of 20.3 cm, the sheathed ya was quenched in a water bath. An extrusion sheathed quasi monofilament consisting of the multi-filament core yam and its polymer sheath was thereby produced. Melt temperatures, yam take-up speeds, sheathed ya deniers and sheathing composition content were varied as given in Table II. Testing of the quasi monofilaments made in these examples showed that the sheaths had poor adhesion to the core yarn, could easily be stripped or abraded from the core yam and were therefore unsatisfactory Comparative Example 9 In Comparative Example 9, a quasi monofilament was prepared in the same manner as described in Example 1 but the sheathing composition was Dow PRIMACOR® 3460 of 20 g/10 min melt index at 190 β C./2.16 kg, 9.5 percent acrylic acid content, and 7.34 MPa tensile strength at yield (Table I). Sheath adhesion/abrasion resistance of this sample was somewhat improved but was still unsatisfactory. Comparative Examples 10 -14 In Comparative Examples 10 through 14, quasi monofilaments were prepared in the same manner as described above but the sheathing compositions were 50/50 and 67/33 blends of Dow 60751.15/PRIMACOR 3460 as shown in Table H The blends were formed by feeding a pellet mixture to the extrusion coating extruder. Weight average tensile strength of the blends was less than 7.4 MPa. In Comparative Example 10 only, the core yam was an AlliedSignal, Inc., commercially available product, SPECTRA® 1000 polyethylene yarn, of 215 denier, 60 filaments, 33 g/d tenacity, 1500 g d modulus, 1,300,000 kg/kg-mole molecular weight and 147°C. melting point. Sheath adhesion/abrasion resistance of all samples was unsatisfactory. Comparative Examples 15 - 18 In Comparative Examples 15 through 18, quasi monofilaments were prepared in the same manner as described above but the sheathing resins were Tenite 812A low density polyethylene (LDPE) of 7.31 MPa tensile strength or Tenite M2001 -P high density polyethylene (HDPE) of 22.06 MPa tensile strength. Sheath adhesion/abrasion resistance of all samples was unsatisfactory (Table II). Comparative Examples 19 - 27 The type of crosshead extrusion die was changed to one in which the sheathing composition was brought into contact with the fiber bundle under pressure within the interior of the die as illustrated in Figure 1 and previously described. The exit diameter of bore 29 at guider tip 22 was 0.046 cm, and the exit diameter from die 23 was 0.061 cm. Tenite M2001-P HDPE was used as the primary polymer resin in Comparative Examples 19 through 22. A blend of Tenite M2001-P and AlliedSignal, Inc., AC-735 polyethylene wax formed the sheathing composition in Comparative Examples 23 through 27. The blends were formed by feeding a pellet mixture to the extrusion coating extruder. Sheath adhesion/abrasion resistance of the quasi monofilaments of these Comparative Examples was slightly improved but still unsatisfactory. Table m shows the conditions under which these Comparative Examples were prepared. Examples of the Invention 28 - 33 The quasi monofilaments of Examples 28 through 30 were prepared in the same manner as that of Comparative Example 19 but the sheathing composition was a blend of 72 weight percent Tenite M2001 -P, 18 weight percent Paxxon 4261 and 10 weight percent AC-735. The blends were formed by feeding a pellet mixture to the extrusion coating extruder. Sheath adhesion and abrasion resistance of these Examples was satisfactory (Table HI). Comparison of these examples with Comparative Examples 23 through 27 shows the benefit of inclusion of 18 weight percent of the low melt index Paxxon 4261 component in the blend. This is an intrinsically tougher, more abrasion resistant component. It will also be noted that, remarkably, meh temperatures in these examples were over 50°C. higher than the melting point of the core yam, and melt pressures were in excess of 13.0 MPa. Both of these factors aided in adherence of the sheath to the core yam. The quasi monofilaments of Examples 31 through 33 were prepared in the same manner as those of Examples 28 through 30 but the sheathing composition included a higher concentration of the low melt index Paxxon 4261 component. The blend contained 54 weight percent Tenite 2001-P, 36 weight percent Paxxon 4261, and 10 weight percent AC-735. Sheath adhesion/abrasion resistance of the sheath to the core yam was satisfactory (Table III). Examples of the Invention 34 - 39 Table IV shows the production conditions for these examples. The core yam was 60 filament SPECTRA®900, 650 denier with 0.9 tpi of twist. The compositions of polymer blends SK-1 and SK-2 are given in Table VI. Prior to extrusion coating, the components of the blend were dry blended and fed to a Killion single screw extruder of 2.54 cm nominal diameter with a screw having a 1.4 to 1 extrusion screw compression ratio and a length to diameter ratio of 30 to 1. This material was extruded at a temperature of 233 - 239°C. through a 0.318 cm diameter rod die and quenched and pelletized. The quasi monofilaments of these Examples possessed satisfactory sheath adhesion/abrasion resistance. Following extrusion coating, the yam from Example 35 was post-stretched to produce the lower denier, higher tenacity sample of Example 36. Post- stretching was conducted in two in-line stages. The first stage stretch was 165 percent at a stretch rate of 0.012 sec "1 at 157°C. The second stage stretch was 15 percent at a stretch rate of 0.009 sec "1 at 159°C. Fiber physicals are set forth in Table Vπ. Examples of the Invention 40 - 44 Table V shows the production conditions for these examples. The core ya was 60 filament SPECTRA® 900, 650 denier with 5.0 tpi of twist. In Example 42, the yam was pretreated with 3.5 percent mineral oil. In Example 43, the yam was pretreated with 6.5 percent of PRIMACOR 5980, melting point 79°C, applied as a water based dispersion and then dried. In Example 44, the yam was pretreated with 6.8 percent of A-C®X-4 13, Mettler Drop Point 99- 107°C. (ASTM D3954), similarly applied as a water based dispersion. All percentages are weight percent based on the weight of the untreated yam. Pretreatment occurred prior to twisting in Example 42; pretreatment occurred after twisting in the other examples. In Example 40, the polymer blend composition was SK-6. In Examples 41 through 44, the polymer blend composition was SK-9. The composition of polymer blends SK-6 and SK-9 are given in Table VI. Prio. to extrusion coating, the components of the blends were dry blended and fed to a compounding extruder having a length to diameter ratio of 30 to 1. The materials were extruded at a temperature of 233 - 239°C. through a 0.318 cm diameter rod die and quenched and pelletized. The quasi monofilaments of Examples 40 through 44 possessed satisfaαory sheath adhesion/abrasion resistance. The adhesion/abrasion resistance of the quasi monofilaments of Examples 41 through 44 were greater than that of Example 40, which demonstrates the benefit of the composition of blend SK-9 over that of SK-6 and the benefits of the various pretreatments. Examples of the Invention 45-55 Table V also shows the production conditions for these examples. The core yam was a 120 filament SPECTRA® 1000 high strength polyethylene yam of 430 total denier, nominally 36.5 g/d tenacity, 1400 g/d modulus, 1,300,000 kg/kg-mole molecular weight, melting point about 147°C, with 5.0 tpi of twist. The exit diameter of bore 29 at guider tip 22 was 0.038 cm, and the exit diameter from die 23 was 0.046 cm. The length of the air gap was increased to vary from about 165 to 432 cm. The core yam in Example 45 received no pretreatment. The core yam in Example 46 received plasma treatment. Examples 49, 51 and 52 received corona treatment. In Example 49, the corona treatment was followed by application of 5.7% A-C®X-413. In Example 51, the corona treatment was followed by application of 5.0% PRIMACOR 5980. In Examples 47 and 48, the core yams received applications of A-C®X-413 or PRIMACOR 5980 without prior corona treatment. In Example 50, the core yam was scoured prior to twisting to remove finish oils applied during yam manufacture. The yam in Examples 53-55 received no pretreatment but the air gap was increased in these Examples from 165 cm to 229 cm to 432 cm, respectively, with elimination of the water bath in Example 55. In all of these examples, the polymer blend composition was SK-9. The plasma treatment of Example 46 utilized a PS1010 continuous reactor, available from Airco, Plasma Science Division. Conditions were as follows: 300 watts power, 1 minute residence time, 0.5 torr pressure, with mixtures of oxygen and gaseous fluorocarbons. The corona treatment of Examples 49, 51 and 52 utilized a double-sided corona treater, model CMD-150-MMS, with two corona g-Λierators, model SOA-150, commercially available from Softal of America, Incorporated, of Pawtucket, Rhode Island. Conditions were as follows: 0.6 kilowatts on each generator, 0.35 to 0.45 mil gap for twisted core yam to pass through, and line speed of about 12.2 m/m. The scouring in Example 50 took place as follows: An end of yam was run through a first water bath at ambient temperature until wetted out. The yam was then passed through a second water bath containing 0.1 g/liter of a nonionic surfactant, Hostapur CX, 0.5 g/liter of trisodium phosphate, and a sufficient amount of sodium hydroxide to bring the pH of the bath tυ about 9.0-9.5, at a temperature of 49°C. The yam was then passed through two rinse baths at 49°C and 27°C, respectively. The rinsed yam was rolled into a bundle and dried at about 100°C in a vacuum oven. The quasi monofilaments produced in Examples 45-55 possessed satisfactory sheath adhesion/abrasion resistance. The adhesion/abrasion resistances of the products of Examples 46-51 were equal to or greater than that of product from Example 45, which demonstrates the benefit of the various pretreatments. The adhesion abrasion resistance of the product of Example 45 was superior to that of product from Example 41, and the adhesion/abrasion resistances of quasi monofilaments produced in Examples 54 and 55 were superior to that produced by Example 45, which demonstrates the benefit of a longer air gap. FIG. 3 is a scanning electron micrograph of the cross-section of the sheathed quasi monofilament prepared in Example 45. This is illustrative of the sheath- core structure of the quasi monofilaments of the invention. No primer was used in Example 45. It will be recognized that application of a primer will tend to fill in the spaces between the inner filaments but that the sheath material will still constitute an annular ring surrounding and penetrating the spaces between the outer layers of the core yam. Table I Properties of Materials in Extrusion Coating Trials ASTM Method D792 D1238 at D838 190*C/ 2.16 kg; • 125'C/ 2.16 kg TABLE II COMPARATIVE EXAMPLES t» TABLE III COMPARATIVE EXAMPLES (Continued) TABLE IV EXAMPLES OF THE INVENTION ro o TABLE V TABLE VI COMPOSITIONS OF BLENDS Table Vπ Fiber Phvsicoh ASTM Method D885 strain rate 100% per minute

Claims: WE CLAIM: 1. A quasi monofilament comprising: a. a core of polyethylene multi-filament yarn having a tenacity of at least about 15 g/d and a tensile modulus of at least about 500 g/d; and adhered thereto b. an abrasion resistant sheath, comprising an effective amount of a first polymer having ethylene crystallinity, a density of at least about 0.94 g/cm 3 , and a melt index of less than about 0.1 g/10 min. 2. The quasi monofilament of claim 1 wherein the sheath is formed from a blend comprising: a. about 15 to about 95 weight percent, on the weight of the blend, of the first polymer, in combination with b. about 5 to about 85 weight percent, on the weight of the blend, of a compatible processing aid. 3. The quasi monofilament of claim 2 wherein the processing aid comprises a second polymer having ethylene crystallinity, a density of at least about 0.94 g/cm 3 , and a melt index that is higher than the melt index of the first polymer. 4. The quasi monofilament of claim 3 wherein both the first and second polymers are polyethylene. 5. The quasi monofilament of claim 3 wherein said processing aid further comprises a wax. 6. The quasi monofilament of claim 1 wherein the core yarn is comprised of about 5 to about 9600 filaments having a dpf of about 0.5 to about 20. 7. The quasi monofilament of claim 1 wherein the core yam has about 0.1 to about 20 tpi. 8. A composition for sheathing a core of polyethylene multi-filament ya having a tenacity of at least about 15 g/d and a tensile modulus of at least about 500 g d to make the yam abrasion resistant, said composition being characterized by a weight average tensile strength at yield of greater than about 13.8 MPa and by an ability to crosshead die sheathe under pressure a polyethylene core yam when the composition is in a melt state and at a temperature higher than the melting point of the yam. 9. The composition of claim 8 comprising an effective amount of a first polymer in combination with a compatible processing aid, said first polymer having ethylene crystallinity, a density of at least about 0.94 g/cm 3 , and a melt index of less than about 0.1 g/10 min. 10. The composition of claim 9 wherein said processing aid comprises a second polymer having ethylene crystallinity, a melt index of greater than about 1 g 10 min, and a density of greater than about 0.94 g/cm 3 .

Inventors: CUNNINGHAM DAVIS VERLIN, GRIFFIN CHRISTOPHER PATRICK, KAVESH SHELDON, CUNNINGHAM, DAVIS, VERLIN, GRIFFIN, CHRISTOPHER, PATRICK, KAVESH, SHELDON
Applicants: ALLIED SIGNAL INC, ALLIEDSIGNAL, INC.
Application year: 1996
Main classification: D01D11
IPC codes: A01K91, A61C15, C08L23, C08L57, D01D11, D01F8, D02G3, D06M15, D06M101