SHEET MATERIAL INCORPORATING PARTICULATE MATTER

Abstract: Sheet material which incorporates selected particulate is produced using a blown film die (1); polymer containing the selected particulate is supplied to the die inlet so that, when the polymer is extruded through the die and expanded to form a blown film (6), the selected particulate is incorporated in the blown film; and the selected particulate is added to a part only of the polymer supplied to the die, so that the particulate will be present in only a certain part, for example a surface, of the blown film and of sheet material produced from the blown film.

Description: SHEET MATERIAL INCORPORATING PARTICULATE MATTER Field of the Invention The present invention relates to a method and apparatus for producing sheet material which incorporates particulate matter In one aspect, the invention relates to a method and apparatus for producing abrasive sheet material. Background of the Invention There are uses in many fields for sheet material with particular properties which result from the presence of particulate matter in and, specifically, at the surface of he sheet material. In particular, sheet materials with abrasive particles at the surface are available in the form of rolls or pre-cut sheets of sandpaper or in the form of abrasive discs and belts, and are used to provide anti-slip surfaces for walkways and similar locations. Also, for example, sheet materials with magnetizable particles at the surface are used as magnetic recording media; and sheet materials with reflective particles at the surface are used for pavement marking purposes and for signs All of those sheet materials are typically produced by comparatively complex coating processes Abrasive sheet materials, for example, are conventionally produced by a coating process which typically involves the steps of applying an adhesive to a substrate, depositing abrasive grit particles on the adhesive (optionally using an electrostatic coater to orient the particles); drying and/or curing the adhesive, and, optionally, applying a size coating to anchor the grit particles more firmly in place The coating process is comparatively slow because it involves multiple coating steps together with long drying and/or curing times, and careful control ofthe coating conditions is required to ensure the continuous output of an acceptable product The process may involve the use of organic solvents, the disposal of which should be carefully controlled to reduce the risk of damage to the environment Moreover, the process does not readily accommodate changes in the various coating materials when it is required to produce a different grade of product. As an alternative to that process, it has been proposed to produce abrasive products by embedding abrasive grit in the softened surface of a substrate. U S. Patent No. 2,712,987 describes a process for making an abrasive belt, in which abrasive particles are distributed over the surface of a nylon substrate softened with a suitable solvent so that the particles become embedded, following which the solvent is dried. U.S. Patent No. 2,899,288 describes a process for making an abrasive product, in which the upper surface of a thermoplastic backing sheet is softened by heating before abrasive material is spread over the surface and pressed into the sheet between rollers U.S Patent No. 3,813,231 describes a process in which abrasive grit is distributed over the surface of a copolymer film which is then heated in a platen press to bond the grit to the film. U.S Patent No 4,240,807 describes a process in which the substrate is paper coated with a heat-activatable binder which is softened by heating; abrasive grit is then distributed over, and allowed to sink into, the softened binder. Polymer-based materials in the form of sheets are also known and can be produced simply and economically by extrusion, either through a blown film die or through a slot die Slot dies can be used to produce comparatively thick cast films and also to coat a film onto a substrate The extrudate from a slot die may be stretched in the longitudinal and transverse directions (tentered) to produce a film which is biaxially oriented. A blown film die is a ring die with a central passageway through which a required volume of air is admitted into the centre ofthe extruded polymer tube, causing the extruded tube to expand substantially to form a so-called "bubble" When the polymer has cooled, the expanded tube is collapsed and can then be cut to provide sheeting material ofthe required shape and size A method and apparatus for producing blown film are described in, for example, U.S Patent No. 5,104,593. It is known, when using both blown film dies and slot dies, to coextrude two or more polymeric materials simultaneously in a single die to form a multilayer sheet (see the "Encyclopaedia of Polymer Science and Technology", Volume 7, page 106 et seq., published in 1987 by John Wiley and Sons) Sheets produced in that way are typically used as packaging materials In addition, it is known to use a blown film die to coextrude a polymeric backing layer and an adhesive coating to produce adhesive strips, as described for example in GB-A-1 553 881, U.S Patent No 5,124,094, and U S Patent No 5,128,076 The use of a coextrusion process to produce a film base which is then coated with magnetizable particles to form a magnetic recording medium is described in U S Patent No 4,603,073 In that process, one ofthe extruded layers can include carbon black beads so that the film base will be opaque A process which involves the extrusion of a polyurethane material, an epoxy resin and an aggregate, to produce an anti-slip tread, is described in GB-A-2 268 748 It is also known to add a mineral, for example, calcium carbonate, as a reinforcement to a polymer which is to be extruded through a blown film die (see Ruiz and Bankole "Mineral Reinforcement of Linear-Low Density Polyethylene Film, Bags and Liners", conference proceedings ofthe Society of Plastics Engineers, 1992) or to add a pigment such as titanium dioxide (see Duchesne, Schreiber, Johnson and Blong "New Approaches to the Processing of Rutile-Filled Polyolefins", Polymer Engineering and Science, August 1990) JP-A-61 112633 refers to a process in which glass beads are injected into the interior ofthe expanded tube and the tube, when subsequently collapsed, is pressed between a pair of nip rollers to form a composite film. Summary of the Invention The present invention provides a method of producing sheet material, comprising (a) supplying composite material to an inlet of a blown film die, the composite material comprising polymer with selected particulate present in only a part thereof, (b) extruding the composite material through the die to form an extrudate, and (c) expanding the extrudate to form a blown film in which the selected particulate is present in only a part ofthe thickness ofthe film The composite material may comprise a core and a surrounding portion, one of which contains particulate. When the surrounding portion contains particulate, a blown film can be produced with particulate in the outer surface. The particulate may include, but not limited to, abrasive particles, frictional particles such as ceramic beads, glass beads and glass bubbles, magnetic particles, and/or decorative particles. The present invention also provides apparatus for producing sheet material, comprising a blown film die having an inlet connected to receive polymer, and a source of selected particulate connected to add particulate to only a part ofthe polymer received at the die inlet whereby the selected particulate is present in only a part ofthe thickness of blown film produced by the die from the polymer. Brief Description of the Drawings By way of example only, processes and apparatus in accordance with the invention will be described with reference to the accompanying drawings, in which: Fig. 1 is a diagram of apparatus for producing sheet material in accordance with the invention; Fig. 2 is a diagrammatic longitudinal cross-section of a cavity transfer mixer used in the apparatus shown in Fig. 1 ; Fig. 3 is a diagrammatic longitudinal cross-section of a blown film die used in the apparatus shown in Fig. 1 ; Fig. 4 is a cross-sectional view on the line IV-IV in Fig. 3; and Figs. 5 to 8 are diagrams of alternative forms of apparatus for producing sheet material in accordance with the invention. Detailed Description of the Invention The apparatus shown in Fig. 1 comprises a blown film die 1 supplied by a hollow cavity transfer mixer (CTM) 2 which has a main input from a screw extruder 3 and an additional input from a pump 4. As will be described in greater detail below, the extruder 3 supplies molten polymer to the CTM 2 and the pump 4 supplies a mixture of molten polymer and particulate material The output ofthe CTM 2, as will also be described below, is a core of molten polymer surrounded by an outer layer which comprises a mixture of molten polymer and particulate The CTM 2 is connected to the input ofthe blown film die 1 by a heated pipe 5 The material supplied to the die 1 is extruded, as will be described below, in the form of a "bubble" 6 of blown film which is pulled away from the die by nip rollers 7 Because the material supplied to the die 1 is in the form of a core of polymer surrounded by an outer portion comprising a mixture of polymer and particulate, the extrudate leaving the die 1 comprises an inner layer of polymer and an outer layer of a mixture of polymer and particulate, provided that no substantial degree of mixing takes place between the core and the outer portion as they pass through the die As the extrudate is expanded to form a blown film, the particulate in the outer portion becomes increasingly exposed with some particles breaking through the surface ofthe film and other particles remaining covered by only a very thin layer of polymer At a certain distance from the die 1, when the extrudate has cooled sufficiently, the "bubble" 6 is collapsed inside a guide frame 8 and is then passed through the nip rollers 7, so forming a flattened tube 9 which is wound onto a roll 10 The CTM 2 and the blown film die 1 will both be described in greater detail below with reference to Figs 2 to 4 First, however, the manner in which material is supplied to the CTM will be described (still with reference to Fig. 1) Solid polymer, typically in the form of pellets, is contained in the hopper 16 ofthe screw extruder 3 and also in the hopper 15 of a second screw extruder 11 and, in each case, the heat generated by the action of compression and shear forces as the polymer passes through the extruder causes the polymer to become molten The molten polymer from the first extruder 3 is supplied directly to the CTM 2, as described above, while the molten polymer from the second extruder 11 is fed to the pump 4 which also receives particulate material from a hopper 13 via a screw feeder 14 The polymer and particulate are blended together in the pump 4 which may be a heated progressing cavity pump with a stator made from the material having the trade designation "Teflon" available from E.I DuPont de Nemours of Wilmington, Delaware, U S A Pumps of that type are available under the trade designation "Moyno" from Robbins & Myers Inc of Springfield, Ohio, U.S A.. The pressure-generating capability ofthe pump is a function ofthe number of stages that it possesses. The hollow CTM 2 is shown in greater detail, in longitudinal cross section, in Fig. 2 The mixer comprises a hollow central rotor 20, which has circumferential rows of recesses 21 in its outer surface, and a surrounding stator 22 which has circumferential rows of recesses 23 in its inner surface The recesses 21, 23 are typically hemispherical in shape On both the rotor and the stator, the recesses in adjacent circumferential rows are circumferentially offset from each other while the rows on the rotor are axially offset from the rows on the stator In that way, a tortuous flow path 29 is established through the recesses 21, 23 between one end of the rotor and the other The flow path 29 comprises a plurality of interconnections which change as the rotor turns within the stator to ensure thorough mixing of material flowing along the outside ofthe rotor. The hollow rotor 20 provides, in addition, a central flow path 21 which extends axially from one end ofthe rotor to the other The central flow path 24 and the outer flow 29 path through the recesses 21, 23 on the outside ofthe rotor both communicate with a common inlet chamber 25 at the inlet end ofthe CTM 2 and with a common outlet chamber 26 at the outlet end ofthe CTM 2 The inlet chamber 25 and the outlet chamber 26 are connected respectively to the screw extruder 3 and to the blown film die 1 (Fig. 1) The output from the pump 4 enters the CTM 2 at an injector inlet 27 which communicates only with the outer flow path 29 on the outside ofthe rotor, on the upstream side ofthe recesses 21, 23 The CTM 2 as shown in Fig 2 functions as follows Molten polymer from the extruder 3 is pushed into the inlet chamber 25 ofthe mixer and divides into two streams, a central stream which flows along the central flow path 24 and a smaller outer stream which flows along the outside ofthe rotor 20 Typically, the volume of polymer flowing along the outside ofthe rotor is about half the volume flowing through the centre ofthe rotor but that ratio can be adjusted by changing an adjustment ring 28 to alter the size ofthe openings between the outer flow path 29 and the chamber 25. At the injector inlet 27, the mixture of molten polymer and particulate from the pump 4 is added to the polymer flowing along the outside of the rotor and the two are mixed thoroughly together as they pass through the recesses 21, 23 The final mixture then enters the outlet chamber 26 ofthe CTM 2 where it surrounds the central stream, comprising polymer only, which emerges from the central flow path 24 The output ofthe mixer thus comprises a core of polymer surrounded by an outer portion comprising a mixture of polymer and particulate, as already described When using apparatus ofthe type shown in Fig. 1, the amounts of material delivered by the two extruders 3, 11 to the CTM 2 can be varied by changing the speeds ofthe extruders and, as explained above, the manner in which the polymer from the first extruder 3 is divided between the central and outer paths 24, 29 through the CTM can also be adjusted The volume of polymer from the first extruder 3 that flows around the outside ofthe CTM rotor is generally within the range of from 20% to 70% ofthe volume that flows through the rotor, and is typically about 50% of that volume The amount of particulate material that is supplied to the injector inlet ofthe CTM is generally within the range of from 20% to 40% by weight ofthe total amount of material flowing around the outside ofthe rotor and typically within the range of from 25% to 35% by weight A cavity transfer mixer suitable for use in the apparatus of Fig 1 is described in U.S. Patent No. 4,419,014, incoφorated herein by reference The blown film die 1 is shown in greater detail in Figs. 3 and 4 and comprises a cylindrical die head 30 with a central inlet 31 which opens out into an annular channel 32 leading to a ring die opening 33 Within the ring die is an air supply channel 34 through which air can be admitted into the centre ofthe tube of extrudate that emerges from the die opening 33 As already described, the extrudate is pulled away from the die by nip rollers 7 (Fig 1) which also ensure that the air admitted by the supply channel 34 is contained within the tube of extrudate and causes the extrudate to expand as it leaves the die to form the "bubble" 6 of blown film To assist in cooling the expanded film 6 before it is collapsed inside the guide frame 8, a second air channel (not shown) may be provided in the die 1 to direct air over the external surface ofthe extrudate as it leaves the die opening 33 Alternatively, the second air channel may be used to direct hot air over the extrudate so that it will stay soft over a greater distance from the die opening and can be stretched to a greater extent The diameter ofthe ring die opening 33 in the blown film die is typically about 50 mm and the width ofthe opening is about 1 mm, although those sizes may vary, depending on the die that is used The diameter ofthe die may, for example, be as large as one meter while the width ofthe die opening is selected having regard to the desired thickness ofthe blown film, the nature ofthe polymer and the particle size ofthe particulate The distance between the die opening 33 and the nip rollers 7 (Fig 1) is typically about 800 mm, although that distance may vary, depending on the size ofthe die and the operating parameters Blown film dies ofthe type illustrated in Figs 3 and 4 are known and any suitable, commercially available, blown film die may be used in the apparatus shown in Fig 1 provided that it does not cause any substantial mixing in the material passing from the central inlet 31 to the die opening 33 As already mentioned, it is important that the structure ofthe material supplied to the die by the CTM 2 (i e a core of polymer surrounded by an outer layer of a mixture of polymer and particulate) is not disturbed as the material passes through the die One blown film die that can be used is available from Kilhon Extruders Inc of Cedar Grove, New Jersey, U S A Typically, a blown film die can expand the extrudate so that the transverse diameter ofthe bubble 6 is up to three or four times the diameter ofthe ring die opening 33 The thickness ofthe resulting blown film is dependent on the rate at which the extrudate is pulled away by the nip rollers 7 and is also dependent on the transverse diameter ofthe bubble 6 and hence on the volume ofthe contained air Fig 5 illustrates a modified form ofthe apparatus shown in Fig. 1, the modification residing in the provision of a pin mixer 12 which receives the polymer from the extruder 11 and the particulate from the screw feeder 14 and blends them together before they are fed to the pump 4. Figure 6 illustrates another modified form ofthe apparatus shown in Fig. 1, the modification again residing in the manner in which the mixture of polymer and particulate is supplied to the CTM 2 In this case, instead of the progressing cavity pump 4, an extruder 50 is used to supply the mixture of polymer and particulate to the injector inlet 27 (Fig 2) ofthe CTM, the mixture itself being formed on a two roll mill (not shown) and loaded into the hopper 45 ofthe extruder 50 in the form of small granules The extruders 3, 1 1, 50 used in the apparatus of Figs 1, 5 and 6 can be single screw or twin screw extruders, or any other equivalent extrusion machine Generally, the operating temperatures and flow rates ofthe extruders will be dependent in part on the polymers and particulates employed Apparatus ofthe type shown in Fig 6 has been operated using polyethylene as the polymer in both extruders and with operating temperatures in the ranges of: from about 150° C to about 190° C at the first extruder 3 (supplying polymer only); from about 160° C to about 230° C at the second extruder 50 (supplying the mixture of polymer and particulate material); from about 160° C to about 190° C at the CTM 2 and from about 160° C to about 180° C at the blown film die 1. Typically, the capacities of the various components ofthe apparatus are such that the flow rate of material into the CTM 2 from the first extruder 3 is within the range of from 3 0 to 6.0 kg/hr and the flow rate of material into the CTM from the second extruder 50 is within the range of from 0 5 to 2 0 kg/hr Generally, when using apparatus ofthe type shown in Fig. 1, Fig. 5 or Fig. 6, the polymer supplied through the extruders may be any suitable extrudable thermoplastic polymer or mixtures thereof It is not necessary for the same polymer to be supplied through both extruders Polymers that are generally suitable include polypropylene, polyethylene, polycarbonates, polyetherimides, polyesters, polysulfones, polystyrenes, acrylonitrile-butadiene-styrene block copolymers, acetyl polymers, polyacrylates, polyvinyls and polyamides and combinations thereof. The polymer or polymers selected should have properties appropriate to the intended use ofthe blown film: for example, if the blown film is to be used for abrasive sheet material as described below, the polymer or polymers in the blown film extrudate should have a relatively-high melting temperature, heat and water resistance, and a degree of toughness appropriate to such a use. Various additives can be included with the polymers, depending on the desired properties ofthe blown film. Those additives include, for example, coupling agents, reinforcers, toughening agents, polymer processing aids, plasticizers, fillers, stabilizers, UV absorbers and lubricants. The amounts of polymer additives used are selected to give the desired properties without adversely affecting the processing. The additives may be in particulate form but, in that case, are not to be equated with the selected particulate added to the CTM 2 through the injector inlet 27. If the polymer additives are present in the polymer in extruder 11 or 50 but not the polymer in extruder 3, they will also be present only in the outer surface ofthe blown film bubble 6. If, on the other hand, the polymer additives are present only in the polymer in extruder 3, they will be present throughout the blown film (although to a lesser extent in the outer surface). The particulate that is used can be selected from a wide range of materials, provided that it will mix with a polymeric material, as described, and pass through the blown film die. Suitable particulates include, but are not limited to, abrasive particles, frictional particles such as ceramic beads, glass beads, and glass bubbles, magnetic ferrite particles, and decorative particles such as gold glitter. Depending on the nature ofthe particulate material, the blown film produced by the apparatus can have widely different properties and, consequently, widely different potential uses as will be described below. A blown film having abrasive properties, which can be used to produce abrasive belts or sheets, or friction sheeting for use as a non-slip flooring material, can be produced by using abrasive grains as the particulate. The quality ofthe abrasive product is dependent on nature and sizes ofthe abrasive grains, the nature ofthe polymer and the extent to which the film is expanded as it leaves the blown film die The particle size ofthe abrasive particles in the blown film can range from about 0 1 to 1500 micrometers, typically from about 1 to 150 micrometers Examples of conventional abrasive particles, suitable for producing an abrasive product, include silicon carbide, alumina zirconia, and aluminum oxide (including sintered, sol gel, fused, and heat-treated aluminum oxide) The abrasive product may contain a mixture of two or more different abrasive particles This mixture may, for example, comprise a mixture of hard abrasive particles (1 e particles having a Mohs hardness equal to, or greater than, 8) and soft abrasive particles (i e particles having a Mohs hardness less than 8) or a mixture of two soft or two hard abrasive particles The abrasive particles may have specific shapes associated with them Examples of such shapes include rods, triangles, pyramids, cones, solid spheres and hollow spheres Alternatively, the abrasive particles may be randomly shaped The abrasive particles can be treated to provide a surface coating thereon A surface coating can be used to improve the adhesion between the abrasive particle and the polymer in the abrasive product Alternatively, or in addition, a surface coating can alter and improve the abrading characteristics ofthe abrasive particles The abrasive particle may have multiple coatings The abrasive particles may also be abrasive agglomerates An abrasive agglomerate comprises a plurality of individual abrasive particles bonded together to form a shaped mass The abrasive agglomerates may be irregularly or randomly shaped or have a predetermined shape such as rods, triangles, pyramids, cones, and solid spheres The abrasive agglomerate may utilize an organic binder or an inorganic binder to bond the abrasive particles together Examples of abrasive agglomerates are described in U S Patent Nos 4,652,275, 4,799,939, 5,500,273, and 5,549,962, incoφorated herein by reference It has already been mentioned that the polymer material used in the apparatus of Figs 1 and 5 may comprise optional additives, such as coupling agents, reinforcers, toughening agents, polymer processing aids, plasticizers, fillers (which term includes grinding aids), stabilizers, UV absorbers and lubricants. Other optional additives include curing agents, expanding agents, fibers, initiators, suspending agents, photosensitizers, wetting agents, surfactants, dyes, and fire retardants The amounts of these additives are selected to provide the properties desired. In general, in the case of an abrasive sheet material, the addition of a plasticizer will increase the erodibility ofthe coating. The plasticizer should be compatible with the polymeric material ofthe blown film Examples of plasticizers include polyvinyl chloride, dibutyl phthalate, alkyl benzyl phthalate, polyvinyl acetate, polyvinyl alcohol, cellulose esters, phthalate, silicone oils, adipate and sebacate esters, polyols, polyol derivatives, tricresyl phosphate and castor oil A filler generally has an average particle size ranging from 0.1 to 50 micrometers, typically from 1 to 30 micrometers Examples of useful fillers for the polymer, in the case of an abrasive sheet material are calcium carbonate and silicate A grinding aid is defined as a material, the addition of which to an abrasive article has a significant effect on the chemical and physical processes of abrading and results in improved performance It is believed in the art that a grinding aid will either 1) decrease the friction between the abrasive particles and the workpiece being abraded, 2) prevent the abrasive particle from "capping", i.e prevent metal particles from becoming welded to the tops ofthe abrasive particles, 3) decrease the interface temperature between the abrasive particles the workpiece or 4) decrease the grinding forces In general, the addition of a grinding aid increases the useful life of an abrasive product Grinding aids encompass a wide variety of different materials and can be inorganic or organic based Examples of grinding aids are cryolite and potassium tetrafluoroborate A combination of different grinding aids may be used and, in some instances, this may produce a synergistic effect The addition of filler particles and/or grinding aid particles in some instances increases the erodibility o the resulting abrasive coating, which can be desirable A blown film incorporating abrasive particles, in accordance with the invention, may be collected as a tube as described with reference to Fig 1 and then cut transversely to form seamless abrasive belts Alternatively, the tube may be slit longitudinally and then cut or stamped into abrasive sheets or discs If required, a backing could be applied to an abrasive article produced from the blown film The backing may be sealed or porous and may, for example, be cloth, polymeric film, fiber, metallic foil, a metal plate, paper, or a non-woven web The backing may improve the strength or rigidity of the abrasive product, or provide a means of attaching the abrasive product to support means such as a back¬ up pad More specifically, the backing may be a loop-type fabric or a sheet material with projecting hooking stems, either of which would enable the abrasive article to be secured to a back-up pad with a hook-and-loop type of attachment Hook-and- loop attachment systems are described, for example, in U S Patent Nos 4,609,581 and 5,254, 194, and in U.S Patent No 5,505,747, all of which are incoφorated herein by reference Another form of backing is a non- woven or open-weave scrim which can be laminated to an abrasive article to impart strength and/or rigidity It is also possible to apply a coating to one side of an abrasive article produced from the blown films The coating can be applied for various reasons; for example, a carbon black coating can be applied to the backing side of an article to reduce static charge generated during grinding, or a supersize coat, having a grinding aid such as KBF can be applied to the abrasive side to increase cutting performance If required, a coating could be applied to the extrudate to produce a coated abrasive sheet For example, a pressure sensitive adhesive could be extruded with the polymer using a multilayer feed block system such as that available from The Cloeren Company of Orange, Texas, U S A to coat the inside surface ofthe extruded tube The adhesive coating would then be expanded with the polymer and the resulting blown film would be slit into sheets before being collected Representative examples of suitable pressure sensitive adhesives include latex crepe, rosin, acrylic polymers and copolymers e.g., polybutylacrylate, polyacrylate ester, vinyl ethers, e.g. polyvinyl n-butyl ether, alkyd adhesives, rubber adhesives, e.g. natural rubber, synthetic rubber, chlorinated rubber, and mixtures thereof One preferred pressure sensitive adhesive is an isooctylacrylate: acrylic acid copolymer If required, a further polymer layer or layers could be extruded through the blown film die 1 with the output ofthe CTM 2, e.g., to form a backing on the inside ofthe blown film 6. As described above, more than one type of particulate may be present in the mixture supplied to the CTM 2 (Fig. 1, 5 or 6) through the injector inlet 27, and different polymeric materials, or different blends of polymeric materials may be supplied to the CTM through the injector inlet 27 and from the hopper 16 In general, the particulate may be supplied to the CTM in a mixture with any suitable carrier material For example, the particulate may be mixed with polypropylene when the material supplied to the CTM from the hopper 16 is polyethylene. As a further example, the particulate may be mixed with a liquid polymeric material when the material supplied to the CTM from the hopper 16 is a solid polymeric material. In the latter case, the apparatus for producing the blown film may be as shown in Fig 7 or as shown in Fig. 8. The apparatus shown in Fig 7 is generally similar to that shown in Fig 1 except that the extruder 1 1 and associated hopper 15 are replaced by a pump 71 which receives liquid polymer from a container 72 and supplies the liquid polymer to the progressing cavity pump 4 where it is mixed with the particulate from hopper 13 The apparatus shown in Fig. 8 is generally similar to that shown in Fig 6 except that the extruder 50 and associated hopper 45 are replaced by a pump 51 which receives, from a container 52, a slurry of particulate and liquid polymer. The pump 51 is connected to supply the slurry to the injector inlet 27 (Fig. 2) ofthe CTM 2 The pump 51 may, for example, be a 5 mm pneumatic pumping system available from Williams Instruments Company Inc. of Humble, Texas, U.S.A. Although the apparatus shown in Figs. 1 and 5 to 8 uses a hollow CTM 2 to provide the input to the blown film die, that is not essential. Any appropriate system could be used to provide an input to the blown film die 1 in the form of a composite material comprising a central core of polymeric material with a surrounding layer which comprises a mixture of polymeric material and particulate. For example, a CTM without a hollow rotor could be used simply to form the mixture of polymer and particulate, which could then be layered around the separately-formed core of polymer material. The use of a hollow CTM 2 as described above does, however, have the effect of putting polymer from one source (i.e. the hopper 16) into both the central core and the surrounding layer and may avoid adhesion problems across the thickness ofthe blown film. It is also not essential, when a CTM is employed, that the cavities 21, 23 in the rotor and stator, should be hemispherical as shown in Fig. 2: the cavities can have any shape that will achieve the desired mixing of polymer and particulate. It is also not essential for a mixture of polymer and particulate to be layered around a core of polymer at the outlet from the CTM 2 Instead, a polymer material could be layered around a core of a mixture of polymer and particulate with the result that the particulate would be on the inside ofthe blown film bubble 19. Alternatively, when a mixture of polymer and particulate is layered around a core of polymer, another layer, of polymer alone could be formed around the layer ofthe mixture. The blown film bubble from this assembly would have polymer inner and outer layers with a layer of polymer and particulate between them. It will be appreciated from the above description that particulate is present in only a part ofthe thickness ofthe blown film. The location ofthe particulate in the film depends on the apparatus used. Apparatus and processes which enable particulate to be located in the exterior region or the interior region of a film have both been described. The percentage, by weight, of particulate in a film depends on several factors including, for example, the amount provided initially to the CTM 2. The following Examples illustrate the use of abrasive particles as the particulate material in apparatus ofthe type shown in Fig. 6. Examples EXAMPLE 1 Using apparatus ofthe type shown in Fig. 6, a polymer melt comprising a medium density polyethylene ("MDPE") having a density of 940 kg/m 3 , commercially available from British Petroleum Chemicals Limited, Middlesex, England under the trade designation "Novex", was supplied by a first extruder (similar to the extruder 3) to a CTM (similar to the CTM 2) at a rate of 1 15 g/min. The CTM was adjusted so that 62% ofthe melt passed along the central path through the CTM and 38% passed along the outside path. A mixture comprising 40% by weight of a low density polyethylene ("LDPE") having a density of 920 kg/m 3 , commercially available from British Petroleum Chemicals Limited, Middlesex, England under the trade designation "Novex", and 60% by weight abrasive particles (fused aluminium oxide, Grade P320 (FEPA)) was supplied by a second extruder to the CTM through the injector inlet 12 (Figure 1) at a rate of 30 g min. The temperature in the first extruder ranged from 150° C at the input end to 160° C at the output end; the temperature in the second extruder ranged from 185° C at the input end to 215° C at the output end; the temperature in the CTM was 165° C, and the temperature at the die opening ofthe blown film die was 170° C. The resulting blown film had an abrasive surface EXAMPLE 2 The process described in Example 1 was followed except that the mixture of polymer and abrasive particles was supplied to the CTM at a rate of 51 g/min to yield a slightly higher concentration of abrasive particles in the blown film. In addition, the temperatures at the outlet ends ofthe first and second extruders and in the CTM were higher, at 175°C, 230°C and 170°C respectively. EXAMPLE 3 The process described in Example 1 was followed except that the abrasive particles used were Grade PlOO (FEPA) and the mixture of polymer and abrasive particles was supplied to the CTM 2 at a rate of 48 g/min The operating temperatures were as in Example 2 EXAMPLE 4 The process described in Example 1 was followed except that the polymer melt was supplied by the first extruder to the CTM at a rate of 90g/min, the abrasive particles used were Grade PlOO (FEPA), and the mixture of polymer and abrasive particles was supplied to the CTM at a rate of 49 g min The operating temperatures were as in Example 2 Samples 1 to 4, which were products ofExample 1 to 4 respectively, were tested using the following test procedures as designated Test procedure A utilized a Coburn opthalmic lens grinding machine Abrasive sheet material (cut into a daisy shape and mounted on a lap) was used in the machine to grind a plastic lens for a period of 90 seconds The lens was then taken out ofthe machine and the caliper loss (I e the depth of material that had been removed from the centre ofthe lens) was measured The surface finish ofthe lens was also evaluated by measuring, around a fixed circumference ofthe lens, the average peak-to-valley height (Ra) ofthe ridges remaining in the surface and the average peak-to- valley height (Rtm) ofthe five highest of those ridges Test procedure B utilized a Desoutter Model Auto 567 sanding machine A 150 mm disk of abrasive sheet material, mounted on a back-up pad (available, under the trade designation "07317", from Minnesota Mining and Manufacturing Company of St Paul, Minnesota, U S A ) was used in the machine, with an applied pressure of 25N, to abrade aged car primer paint (two-pack "Standox HS Fuller" primer) on a flat steel panel The weight loss, in grams, ofthe panel after periods of 1 minute and 2 minutes was measured Table 1 below shows the results obtained using Samples 1 and 2 as the abrasive sheet material in test procedure A: Table 1 Sample Caliper loss (microns) Ra (microns) Rtm (microns) Sample 1 260 45 296 Sample 2 270 42 306 Table 2 below shows the results obtained using samples 3 and 4 as the abrasive sheet material in test procedure B : Table 2 Sample Weight loss after 1 min. (g) Weight loss after 2 min. (g) Sample 3 0.87 1.28 Sample 4 0.97 1.41 The results summarized in Tables 1 and 2 show that the samples 1 to 4 possessed abrasive properties. EXAMPLE 5 The process described in Example 1 was followed except that: the polymer melt was supplied by the first extruder to the CTM at a rate of 88 g/min; the CTM was adjusted so that two thirds ofthe melt passed along the central path through the CTM and one third passed along the outside path; the mixture supplied by the second extruder to the CTM comprised 25% by weight polymer (16% LDPE commercially available from British Petroleum Chemicals Ltd., Middlesex, England under the trade designation "Novex VS/55" and 9% polyethylene wax, available under the trade designation "AC-6" from Allied Signal of Morristown, New Jersey, U.S.A.) and 75% by weight ceramic beads, and the second extruder was set so that it would deliver polyethylene at a rate of 20g/min. In addition, the temperature in the first extruder ranged from 159°C at the input end to 185°C at the output end; the temperature in the second extruder varied from 160°C at the input end to 185°C at the output end; the temperature in the CTM was 180°C and the temperature at the die opening ofthe blown film die was 176°C. The resulting blown film showed ceramic beads in the outer surface. EXAMPLE 6 Examples 1 to 4 were repeated with the addition of a solid red pigment commercially available from Hubron Ltd., Manchester, England, under the trade designation "PEC 535" at a loading of about 1% by weight to the granules supplied to a second extruder. In each case, the outer layer ofthe resulting blown film was colored. The examples were then repeated with the color being added instead, at the same loading, to the polymer supplied to a first extruder. In each case, the inner layer ofthe resulting blown film was colored and the comparatively small amount of pigment present in the outer layer was not noticeable to the human eye. The addition of a pigment to one or both sides ofthe blown film in that manner provides a way of indicating, for example, the grade ofthe abrasive blown film material. It was mentioned above that, by using other particulate materials instead of abrasive grains, sheet materials having other properties can be produced. For example, by using magnetic particles as the particulate material, a sheet material that exhibits a hysteresis curve can be produced. This type of material could then be used as a magnetic recording medium. By using glass beads or glass bubbles as the particulate material, a sheet material that reflects light can be produced. By using ceramic beads as the particulate material, a sheet material with a non-slip surface can be produced; this type of material could be used as a non-slip flooring material. Many other alternatives exist including, for example, the use of decorative particles to produce packaging material; the use of carbon black to produce a film which is electrically conductive on one surface; and the use of a pigment (as described in Example 6 but without the abrasive grains) to produce a colored film. Generally, it is possible to use any particulate material that will mix with a polymeric material and pass through the blown film die. The following examples illustrate the use of some of those other particulate materials in apparatus ofthe type shown in Fig 6 or Fig 8 EXAMPLE 7 A polymer melt comprising a MDPE polymer having a density of 940 kg/m 3 , commercially available from British Petroleum Chemicals Ltd., Middlesex, England, under the trade designation "Novex", was supplied by a first extruder (similar to the extruder 3) to a CTM (similar to the CTM 2) at a rate of 88 3 g/min and the valve member (10A in Fig 1) in the inlet chamber ofthe CTM was adjusted so that approximately two thirds ofthe melt passed along the central path through the CTM and one third passed along the outside path A mixture comprising 16 % LDPE (commercially available from British Petroleum Chemicals Ltd , Middlesex, England, under the trade designation "Novex VS/55"), 9% polyethylene wax (commercially available from AlliedSignal, Morristown, NJ under the trade designation "AC-6") and 75% ceramic beads as supplied to the CTM through the injector inlet 12 (Figure 1) The resulting blown film showed ceramic beads in the outer surface EXAMPLE 8 The process described in Example 7 was followed except that the mixture supplied to the CTM through the injector inlet comprised 55% LDPE (commercially available from British Petroleum Chemicals Ltd., Middlesex, England, under the trade designation "Novex VS/55"), 33% polyethylene wax (commercially available from AlliedSignal, Morristown, NJ under the trade designation "AC-6") and 12% glass bubbles available from Minnesota Mining and Manufacturing Company, St Paul, MN under the trade designation "38-4000") The resulting blown film showed glass bubbles in the outer surface EXAMPLE 9 The process described in Example 7 was followed except that the mixture supplied to the CTM through the injector inlet 12 comprised 23% LDPE (commercially available from British Petroleum Chemicals Ltd., Middlesex, England, under the trade designation "Novex VS/55"), 9% polyethylene wax (commercially available from AlliedSignal, Morristown, NJ under the trade designation "AC-6") and 68% glass beads. The resulting blown film showed glass beads in the outer surface. EXAMPLE 10 The process described in Example 7 was followed except that the mixture supplied to the CTM through the injector inlet comprised 63% LDPE commercially available from British Petroleum Chemicals Ltd., Middlesex, England, under the trade designation "Novex VS/55", 25% polyethylene wax (commercially available from AlliedSignal, Morristown, NJ under the trade designation "AC-6") and 12% gold glitter particles. The resulting blown film showed glitter particles in the outer surface. EXAMPLE 11 The process described in Example 7 was followed except that the mixture supplied to the CTM through the injector inlet 12 comprised 42% LDPE (commercially available from British Petroleum Chemicals Ltd., Middlesex, England, under the trade designation "Novex VS/55"), 16% polyethylene wax (commercially available from AlliedSignal, Morristown, NJ under the trade designation "AC-6") and 42% magnetic feπite particles. The resulting blown film showed magnetic ferrite particles in the outer surface. It is also possible to produce a colored sheet material without using pigment throughout the whole thickness ofthe material, thereby enabling the cost to be reduced. For example, a pigment could be added to the mixture supplied to the CTM 2 through the injector inlet and/or to the material that passes along the central path in, for example, any of Examples 7 to 1 1 described herein. The resulting blown film will be colored on the side where the particulate material is located and/or on the other side. Other additives can, if desired, be included in the polymeric materials supplied to the cavity transfer mixer. EXAMPLE 12 Using apparatus ofthe type shown in Fig. 8, a polymer melt comprising a mixture of polypropylenes commercially available from Himont, Lisle, IL, under the trade designations "Moplen EPQ 30 RF" and "Adflex 7029 XCP" (60% "Moplen EPQ 30 RF" and 40% "Adflex 7029 XCP") was supplied by a first extruder (similar to the extruder 3) to a CTM (similar to the CTM 2) at a rate of 112.5 g/min. The CTM was adjusted so that 51.2% ofthe melt passed along the central path through the CTM and 48.8% passed along the outside part. A slurry comprising 50% magnetic ferrite particles in an extrusion carrier liquid (commercially available from Metacol Ltd., under the trade designation "EA 107") was supplied by a pump to the CTM through the injector inlet 12 (Fig. 1) at a rate of 43.7 g/min. The temperature in the first extruder ranged from 156°C at the input end to 180°C at the output end; the temperature in the CTM was 185°C and the temperature at the die opening of the blown film die was 202°C. The resulting blown film showed magnetic ferrite particles in the outer surface. The magnetic properties of a sample of blown film produced by the method ofExample 12 were measured using a BH meter in a magnetic field of 3000 Oe (3/4π x 10 6 Am '1 ). The sample had a coercivity (He) of 768 Oe (0.768/4π x 10 6 Am "1 ) and a squareness (0r/0m) of 0.69. Squareness is the ratio between the remanent saturation magnetization 0r and the saturation magnetization 0m ofthe sample and is a measure ofthe degree of orientation ofthe magnetic particles. For the puφoses of comparison, video tape currently used in VHS cassettes typically has a coercivity of about 760 Oe and a squareness in the range 0.80 to 0.85. EXAMPLE 13 The process described in Example 12 was followed except that the polymer melt supplied by the first extruder to the CTM was an ethylene vinyl acetate copolymer (commercially available from E I DuPont de Nemours Company, Wilmington, DE, under the trade designation "Elvax 360") supplied to the CTM at a rate of 112 5 g/min , the slurry supplied to the injector inlet ofthe CTM comprised 10% carbon black in a liquid extrusion carrier ("EA 107") and was supplied at a rate of 16 5 g/min The temperature in the first extruder ranged from 145°C at the input end to 162°C at the output end. The temperature in the CTM was 160°C The temperature ofthe die opening ofthe blown film die was 158°C. The resulting blown film showed carbon black in the outer surface EXAMPLE 14 Using apparatus ofthe type shown in Fig 6, an ethylene vinyl acetate copolymer melt which had a melt index of 0.5 and contained 12% vinyl acetate (commercially available from Quantum Chemical Coφoration, Cincinnati, OH, under the trade designation "Quantum 657-000") was supplied by the first extruder to the CTM at a rate of 1 kg/hr and the CTM was adjusted so that 10% ofthe melt passed along the outside path and 90% passed along the central path A mixture comprising a blend of 28% carbon black and 72% of an ethylene vinyl acetate copolymer which had a melt index of 5.5 and contained 12% vinyl acetate (commercially available from Quantum Chemical Coφoration, Cincinnati, OH under the trade designation "Quantum UE 656-003") was supplied to the CTM through the injector inlet 12 (Fig 1) at a rate of 0 86 kg/hr The temperatures in the first and second extruders ranged from 153°C at the input ends to 177°C at the output ends The temperature ofthe CTM was 177°C The temperature at the die opening of the blown film die was 177°C The resulting blown film showed carbon black in the outer surface The surface resistivity of samples of blown film produced by the method of Example 14 was measured. The samples varied in thickness from 0.06 to 0.15 mm but in each case the carbon black was located in a region having a thickness of 55% ofthe film thickness. The surface resistivity ofthe inner (carbon black free) surfaces ofthe films ranged from 2 x 10 13 to 1 x 10 14 ohms/sq and the surface resistivity of the outer (carbon black containing) surfaces ofthe films ranged from 8 x 10 3 to 2 x 10 4 ohms/sq.

Claims: IN THE CLAIMS A method of producing sheet material, comprising (a) supplying composite material to an inlet of a blown film die, the composite material comprising polymer with selected particulate present in only a part thereof, (b) extruding the composite material through the die to form an extrudate, and (c) expanding the extrudate to form a blown film in which the said selected particulate is present in only a part ofthe thickness ofthe film 2 A method as claimed in claim 1, including the step of forming the composite material by supplying polymer to die inlet and adding the said selected particulate only to a part ofthe polymer supplied to the die inlet so that the said selected particulate is present in a surface ofthe blown film 3 A method as claimed in claim 2, in which the composite material comprises a core and a surrounding portion, one of which contains the said selected particulate 4 A method as claimed in claim 3, comprising forming two streams of polymer, one of which contains the said selected particulate, and surrounding one stream by the other stream upstream ofthe die inlet 5 A method as claimed in claim 4, in which the two streams are formed by dividing a main stream of polymer into a central stream and a suπounding stream and then adding the said selected particulate to one ofthe streams 6 A method as claimed in claim 5, in which the said selected particulate is mixed with polymer before being added to the said one ofthe streams 7 A method as claimed in claim 5, in which the said selected particulate is added to the suπounding stream of polymer 8 A method as claimed in claim 7, in which the said selected particulate is mixed into the surrounding stream of polymer in a cavity transfer mixer 9 A method as claimed in claim 8, in which the central stream of polymer by¬ passes, or is fed directly through, the cavity transfer mixer 10 A method as claimed in claim 1, in which the said selected particulate comprises abrasive particles 11 A method as claimed in claim 1, including the step of applying a coating to one side at least ofthe extrudate 12 A method as claimed in claim 1, including the step of applying a backing material to one side ofthe blown film 13 Apparatus for producing sheet material, comprising a blown film die having an inlet connected to receive polymer, and a source of particulate connected to add selected particulate to only a part ofthe polymer received at the die inlet whereby the selected particulate is present in only a part ofthe thickness of blown film produced by the die from the polymer 14 Apparatus as claimed in claim 13, in which the source of selected particulate is so arranged that the said selected particulate is present in a surface of blown film produced by the die from the polymer 15 Apparatus as claimed in claim 13, comprising a first supply path connected to supply polymer to the die inlet; and a second supply path connected to receive material from the said source of selected particulate and to supply a mixture of polymer and selected particulate to the die inlet. 16 Apparatus as claimed in claim 15, in which the second supply path is connected to receive polymer from the first supply path 17. Apparatus as claimed in claim 15, wherein one supply path surrounds the other supply path at a point upstream ofthe die whereby the material received at the die inlet comprises a core and a surrounding portion, one of which comprises polymer and the other of which comprises a mixture of polymer and the said selected particulate. 18. Apparatus as claimed in claim 17, including a cavity transfer mixer in which the mixture of polymer and selected particulate is formed. 19. Apparatus as claimed in claim 18, in which one supply path by-passes, or passes directly through, the rotor ofthe cavity transfer mixer and the other supply path passes around the rotor of he cavity transfer mixer 20 Apparatus as claimed in claim 15, in which the source of selected particulate comprises a source of particulate admixed with polymer. 21. Apparatus as claimed in claim 20, in which the source of particulate admixed with polymer comprises a mixer connected to receive separate supplies of particulate and receive polymer 22 Apparatus as claimed in claim 21 , including a progressing cavity pump connected to deliver material from the mixer to the second supply path 23. Apparatus as claimed in claim 21, including a screw extruder connected to deliver material from the mixer to the second supply path. 24. Apparatus as claimed in claim 15, in which the first supply path is connected to receive polymer from a screw extruder. 25. Apparatus as claimed in claim 13, in which the die includes an outlet for applying a coating to one side ofthe extruded material. 26 Apparatus as claimed in claim 13, including a source of backing material, arranged to apply backing material to one side of blown film produced by the die. 27 An abrasive product made by a method as claimed in claim 10.

Inventors: DOUGLAS MALCOLM F, JACKSON GRAHAM V, LENIUS STEVEN J, DOUGLAS, MALCOLM, F., JACKSON, GRAHAM, V., LENIUS, STEVEN, J.
Applicants: DOUGLAS MALCOLM F, JACKSON GRAHAM V, LENIUS STEVEN J, MINNESOTA MINING & MFG, DOUGLAS, MALCOLM, F., JACKSON, GRAHAM, V., LENIUS, STEVEN, J., MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1996
Main classification: B29C47
IPC codes: B24D11, B29C47, B29C55, B29C70, B29K105, B29L7