DRIVING SCREW AND METHOD OF FORMING FILM OF LUBRICANT

Abstract: A feed screw including a screw shaft (1), a nut (2) meshed with the screw shaft (1), and a plurality of rolling members (3) inserted between the screw shaft (1) and the nut (2), wherein a solid film (5) of a fluorine-containing polyurethane polymer is formed on any portions in rolling/sliding contact. The molecules of this solid film (5) have urethane bonds, and form a three-dimensional reticular structure. Therefore, the film is unlikely to separate, peel off or wear. Accordingly, the feed screw produces less dust, improves lubricating property and thus elongates its life.

Description: Technical Field The present invention concerns a driving screw and a method for forming a lubricant film thereon. Particularly, the present invention concerns a suitable driving screw for use in an environment, where a conventional grease or oil is not available, such as in vacuum environment, clean environment, corrosion environment, and the like. Background Art As the aforementioned environment, for example, a transporting system, etc., which is installed in a semiconductor manufacturing plant, may be exemplified, however, under such environment, if a grease will be used as lubricant for the driving screw, an inconvenient drawback, such as a deterioration of the lubricating property or contamination in the operational environment, may be caused according to an evaporation of an oily component from the grease. Under such circumstances, hitherto, at least either part in moving faces of screw stem and nut, or surface of ball, is conventionally coated with a solid lubricant, such as soft metal, which includes gold, silver, lead, copper, etc., carbon, and molybdenum bisulfide in a form of film. In the case of using the coating film made of the above mentioned solid lubricant, a dusting caused by slightly slipping off the lubricant film due to rolling and sliding motion of the ball, may be reduced in lower level, comparing with the case where the grease is used, however, said level is still in considerably inadequate level, particularly under the clean environment. In particular, under heavier load condition, a dusting amount is remarkably increased. Besides these, the present inventor has been carried out in coating solid lubricant, in which fluoride resin is mixed with a binder, onto at least one of sliding face between screw stem and nut, and a surface of the ball. In this case, a dusting amount may be significantly reduced comparing with the above discussed conventional case. However, even in said coating film above, dusting due to wear, other than spalling and falling of the lubricant, is remarkably increased under the relatively heavy axial load condition, resulting in shortening the dusting life. Furthermore, if spalling and falling of the lubricating film are occurred, a lubricating function at rolling and sliding sites may be deteriorated, thereby causing trouble with respect to the operable life, such as being liable of causing adhesion due to contact between metallic parts, and accelerating abrasive wear, as well. Whereas, in the environment wherein corrosive gas is present, each constitutional element, which causes spalling and falling of the lubricating film, may be attacked. JP 5648750 discloses a driving screw having a screw stem, nut, which is spirally engaged therewith, but fails to disclose the provision of a solid lubricant film of a fluoride containing polyurethane compound, having a three-dimensional network structure. Accordingly, an object of the present invention is to provide suppressing dusting and improving in lubricating property of the driving screw, resulting in prolonging life thereof. Disclosure of the invention [Constitution] The driving screw according to the present invention is composed of a screw stem, and nut, which are to be spirally attached, and which have a solid film of a fluoride containing polyurethane compound formed on at least one of the sliding parts of screw stem and nut, said solid film having a three dimensional structure. Preferably, the driving screw further comprises plural movement bodies, which are related to screwing parts between the screw stem and nut, and on these elements, said solid film of fluoride containing polyurethane compound is formed in a position of at least rolling and sliding parts. In this connection, said solid film preferably is contained in dispersing state, with fluoride containing polymer, which may be in fluidized state. Further, regarding said fluidizable fluoride containing polymer, those having no functional group are preferable, A method for forming lubricating film onto the driving screw according to the present invention, comprises two subsequent processes, in which the former is the process for adhering a liquid film using a solution, which is made by diluting a fluoride containing polymer having an isocyanate group as a functional group into a solvent, and the latter is the process for forming a solid film of the fluoride containing polyurethane polymer having net work structure by curing said adhered liquid film. A method for forming lubricating film onto the driving screw according to the present invention, preferably comprises two processes, in which the former is a process for forming liquid film onto at least one of the constitutional element of the driving screw with a solution, which is prepared by diluting a solvent with a mixture comprising the fluoride containing polymer having an isocyanate group as a functional group, and the fluoride containing polymer, which contains at least one of hydroxyl group, amino group, and carboxyl group, and the latter is a process for forming a solid film of fluoride containing polyurethane polymer compound having net work structure by curing said adhered liquid film. A method for forming lubricating film onto the driving screw according to the present invention further preferably comprises two processes, in which the former is a process for forming liquid film onto at least one of the constitutional element of the driving screw with a solution, which is prepared by diluting a solvent with a single solution of a fluoride containing polymer having an isocyanate group as a functional group, or a mixture comprising the solution with a fluoride containing polymer, which contains at least one of a hydroxyl group, amino group, and carboxyl group, and the latter is a process for forming a solid film of fluoride containing polyurethane polymer compound having net work structure, in which a fluoride containing polymer contains no functional group and disperses with maintained fluidity, by curing said adhered liquid film. As for the fluoride containing polymer, for example, perfluoro polyether having no functional group, and the like may be used. [Function] The fluoride containing polyurethane compound according to the present invention, discussed above, is of a solid film, in which molecules are densely packed and intimately contacted. Accordingly, when constitutional elements of the driving screw are attached each other in sliding motion, the spalling and abrasion are scarcely caused, and sliding resistance may be alleviated, as well. In particular, when the fluoride containing polymer is added and dispersed in a fluidized state in the solid film of fluoride containing polyurethane compound, said fluidizable fluoride containing polymer contributes as lubricant by oozing thereof out of the fluoride containing polyurethane compound. [Effects] In the driving screw of the present invention, apalling, falling, and abrasive wear of the lubricating material may be suppressed comparing with those of the conventional coating film, and since the solid film, which is capable of alleviating a rolling and sliding resistance, is used, dusting life and lubricating property may be improved, thereby being capable of contributing improvement in production yield of semiconductor products. Brief description of the drawings Fig. 1 schematically shows a vertical cross sectional view of the driving screw of the present invention. Fig. 2 shows an enlarged view of the part B, shown in the Fig. 1. Fig. 3 shows a partial cross sectional view of an alternate embodiment of a groove for rolling ball. Fig. 4 schematically shows a structural view of a solid film of fluoride containing polyurethane polymer compound, which is formed for covering over the driving screw, shown in Fig. 1. Fig. 5 is a graph showing the analytical results on the solid film property of fluoride containing polyurethane compound in a state before curing. Fig. 6 is a graph showing the analytical results on the solid film property of fluoride containing polyurethane compound in a state after curing. Fig. 7 schematically shows a vertical cross sectional view of a testing apparatus in construction. Fig. 8 shows a vertical cross sectional view of the driving screw of another embodiment according to the present invention. Best mode for carrying out the invention In the following, the present invention is further explained in more detail, with referring to the examples, shown in Figs. 1 to 8. Figs. 1 to 7 concern one of the examples of the present invention, in which Fig. 1 is a vertical cross sectional view showing a schematic structure of the driving screw; Fig. 2 is an enlarged view of part B in Fig. 1; Fig. 3 is a partial cross sectional view showing another embodiment of ball rolling groove; Fig. 4 is a structural view, in a shematical manner, of a solid film of the fluoride containing polyurethane compound; Fig. 5 is a graph showing analytical result of fluoride containing polyurethane compound in a property before curing thereof; Fig. 6 is a graph showing analytical result of fluoride containing polyurethane compound in a property after curing thereof; and Fig. 7 is across sectional view, schematically showing a testing apparatus. In these figures, A is driving screw; 1 is screw stem; 2 is nut; 3 is ball; 4 is circulator tube; and 5 is solid film of the fluoride containing polyurethane compound. The screw stem 1 provides spiral groove 11 on the outer surface thereof. The nut 2 is fitted onto the exterior of the screw stem 1, an inner exterior surface of which forms spiral groove 21 corresponding to the spiral groove 11 of the screw stem 1. Plural number of balls 3 are interposed between the spiral groove 11 of the screw stem 1 and the spiral groove of the nut 2. The circulator tube 4 is provided for ratably circulating ball 3, which is interposed between both spiral grooves 11 and 21, due to a rotation of either screw stem 1 or nut 2, and is attached to the nut 2. A cross sectional shape of the spiral groove 11 of the screw stem 1 and of the spiral groove 21 of the nut 2 is in a form of Gothic arch, in other words, is formed in a nearly V letter shape by combination of two circles, each of which has distinctive center of curvature. Alternately, the cross sectional shape of both spiral grooves 11, and 21, may be formed in arc, as shown in Fig. 3. These elements, i.e., screw stem 1, nut 2, ball 3, and circulator tube 4, are made of a corrosion resistive material. In more detail, an example of the material for screw stem 1 and nut 2, includes martensite series stainless steel of SUS 440 in JIS Standard, with hardening treatment, and heat-resisting steel, such as SKH 4 in JIS Standard, and M-50 in ASTM Standard. The boll 3 may be made of ceramic material, other than the above mentioned steels. Further, the circulator tube 4 maybe formed of , for example, stainless steel, such as SUS 304. An example of the afore-mentioned ceramic materials preferably includes those mainly composed of silicone nitride (Si 3 N 4 ) with yttoria (Y 2 O 3 ), and alumina (Al 2 O 3 ), and optionally aluminum nitride (AlN), titanium dioxide (TiO 2 ), or spinel (MgAl 2 O 4 ) as a binding aids, alumina (AL 2 O 3 ), silicon carbide (SiC), ziruconia (ZrO 2 ), or aluminum nitride (AlN). If the driving screw A may be made of such materials, a corrosion resistance is not to be required in consideration, even when the driving screw A is used in the presence of halide series corrosive gas, which is used, for example, in semiconductor manufacturing apparatus. Beside these, at rolling and sliding sites in the screw stem 1, nut 2, ball 3, and circulator tube 4, a solid film 5 of fluoride containing polyurethane compound is formed. However, regardless of the fact that a solid film 5 is shown only at a spiral groove 11 of the screw stem 1, spiral groove 21 of the nut 2, ball 3, and inside surface of the circulator tube, in the figures, it should be noted that the solid film is provided also on the exterior surface thereof. The solid film 5 of fluoride containing polyurethane compound has a principal structure unit represented by formula: -- C x F 2 -- (wherein x is an integer of 1 to 4), and has a three dimensional net work structure, each of which has an average molecular weight of several millions, and has intermolecular urethane bonding formed by curing reaction. The three dimensional structure, used herein, is a technical term in chemical field, which means not forming net work structure in cross section of the film, but forming continuous intermolecular connection to form net work and forming densely packed and homogeneous structure. An example of such a polymer may be derived in chemical formula from fluoride containing polymer. having a terminal group of an isocyanate functional group, as shown in the following chemical formulae. An example of the fluoride containing polymer having isocyanate functional group at terminal end, which may be adequately used, includes a derivative of perfluoro polyether (PFPE), and concretely, for example, Fonbrin Z Disoc (trade name of Monte Catini, Company). Next, one embodiment of a method for forming the solid film of the fluoride containing polyurethane polymer, mentioned above, is explained. (a) A solution for obtaining a solid film 5 of fluoride containing polyurethane polymer compound was prepared. Screw stem 1, nut 2, ball 3, and circulator tube 4 were submerged into said solution, individually, or alternately, a driving screw A, which was assembled in complete form, was immersed in a lubricating oil, and the screw stem was revolved several times so as to attach liquid film onto a whole surface of the screw stem 1, nut 2, ball 3 and circulator tube 4 (attaching treatment) . The solution, prepared in this stage, was of a fluoride containing polymer having an isocyanate function group at the terminal end (Fonblin Z Disco, derivatives), which was diluted with a diluting solvent (fluoride type solvent, Sv 90 D) to as thin as 1 mass % concentration of fluoride polymer. (b) The driving screw A, as a whole, on which said liquid film was attached, was heated to 40 to 50 °C, for 1 minute, to remove a solvent from the liquid film (drying treatment). At this stage, the liquid film was maintained, as it was, in fluid state. (c) Thereafter, the driving screw A was heated to, for example, 100 to 200 °C, for 20 hours (curing treatment). By way of said treatment, the solid film of the fluoride containing polyurethane compound was obtained by curing reaction due to a change in chemical formula of the liquid film. In this connection, during the curing treatment, each of the fluoride containing polymer having a functional group in the liquid film was carried out in 4 types curing reactions, shown in following chemical schemes 2 to 5, resulting in disappearing the terminal isocyanate group (NCO), and forming urethane bondings by connecting fluoride polymer having a functional group, into three dimensional net work structure. The urethane bonding was linearly cross linked, as schematically shown in Fig. 4(a), by the curing reaction , shown in Figs. 2 and 3, and formed cross linking in three dimension direction, as schematically shown in Fig. 4(b), by the curing reaction shown in Figs. 4 and 5. Furthermore, in Fig.4, It is schematically shown as Y-X~~~~~~~X-Y According to such treatments as discussed above, in the structural elements of the driving screw A, the solid film 5 of the fluoride containing polyurethane compound may be formed with suitable thickness in at least respective contacting site thereof. Further, the treatments (a) and (b) may be repeatedly carried out in several times, on demand, so that a thickness of the fluoride containing polyurethane compound may be optionally defined, for example, within 0.1 to 3 µm, as a final thickness. Hereinbelow, since a property of the film was analyzed, which was formed into films by the following two methods, wherein, in the former, the solution, prepared in the treatment step (a), was simply concentrated and dried (which is still maintaining fluidity), and in the latter, the same solution was cured by coating on a specimen, such as stainless steel plate, a property is discussed. In the former case, the property is analyzed by FT-IR method (Fourier transform infrared spectroscopy, liquid film method). From the results, shown in a graph of Fig. 5, it is confirmed that other than a peak for fluorine series, peaks of NH (3300 cm -1 ), N=C=O (2279 cm -1 ), N(H)C=O (1712 cm -1 , 1546 cm -1 ), and benzene (1600 cm -1 ) were found, accordingly a benzene ring, urethane bonding, and isocyanate, as a functional group, were existing. In this analysis, a study is made both on thin and thick films, and analysis was made regardless of the film thickness. In the latter case, the result was analyzed by FT-IR method (Fourier transform infrared spectroscopy, high sensitivity reflection method). From the results, shown in a graph of Fig. 6, it is confirmed that peaks of benzene ring and urethane were found, but no isocyanate peak was found. That is, according to the results above, a chemical structural change was confirmed, as shown in Figs. 2 to 5, above. As discussed above, since the solid film 5 of the fluoride containing polyurethane polymer compound has an own three dimensional structure, elaborately covers over the object material, and possesses self-lubrication property, dustings due to abrasion and spallings, caused by rolling and sliding movements in the structural element of the driving screw A, may be suppressed, resulting in being capable of overcoming direct contact of structural elements in the driving screw A, each other. As for another alternate embodiment of the present invention, the solid film 5 of fluoride containing polyurethane compound, discussed in the above embodiment, may be formed in a structure that a fluoride containing polymer, such as fluoro polyether is added and dispersed in the three dimensional structure, in which urethane bonding was formed in inner molecule. In this case, concretely, the solution prepared in attaching treatment (a) under a forming method of the embodiment, may be used as a mixture of a fluoride containing polymer having isocyanate terminal group (for example, Fonblin Z Disoc, derivatives, trade name), and a fluoride containing polymer having no function group, as a fluoride containing compound (for example, Fonblin Z-60, derivatives, trade name) in a specific ratio. Under the circumstances, since the fluoride containing polymer having no function group will not connect to the fluoride containing polymer having a functional group, in the curing treatment (c), the fluoride containing polymer having no functional group shows fluidity in the solid film 5 of fluoride containing polyurethane compound, resulting in exhibiting lubrication by oozing out of the solid film 5 of the fluoride containing polyurethane compound. Further, the fluoride containing polymer is not restricted to those having a functional group, as stated above, and the fluoride containing polymer shown in Figs. 6, 7, and 8, may be used. Since a dusting life and torque life of the solid film 5 of fluoride containing polyurethane compound, were evaluated, these are explained as follows. The evaluations are discussed on total five examples, i.e., Examples 1 to 4, and Comparative Example. In Examples 1 to 4, the solid film 5 of the fluoride containing polyurethane compound was formed over the whole surfaces of screw stem, nut, ball, and circulator tube, and the thickness thereof was defined as in 1 µm. The solid film of the fluoride containing polyurethane compound used in Example 1, was obtained by exclusively using fluoride containing polymer having an isocyanate functional group (Fonblin Z Disoc, derivative). The solid film of the fluoride containing polymer used in Example 2 was obtained by adding fluoride containing polymer having a hydroxyl (-OH) functional group at terminal end (Fonblin Z Dol, derivative) to fluoride containing polymer having isocyanate functional group at terminal end (Foblin Z Disoc, derivative). The solid film of the fluoride containing polymer used in Example 3 was obtained by adding fluoride containing polymer having no functional group (Fonblin Z-60, derivative) to fluoride containing polymer having isocyanate functional group at terminal end (Foblin Z Disoc, derivative). The solid film of the fluoride containing polymer used in Example 4 was obtained by adding fluoride containing polymer having hydroxyl group (Fonblin Z Dol, derivative), and fluoride containing polymer having no functional group (Fonblin Z-60, derivative) to fluoride containing polymer having isocyanate functional group at terminal end (Foblin Z Disoc, derivative). In Comparative Example, a coating film was covered on whole surface of the screw stem, nut, ball, and circulator. Said coating film was made by dispersing and mixing polytetrafluoroethylene in a binder of thermocurable resin (polyimide) and was formed into film having thickness of 1 µm. In said coating film, a relatively hard and dense thermocurable resin forms "sea", and heterogeneous polytetrafluoroethylene forms scattered "island", and both parts are connected with weak bondings. The evaluation test was conducted using an apparatus shown in Fig.7. In the Fig.7, 60 is screw shaft of the driving screw A; 61 is a support bearing for driving screw A; 62 is a spring against load; 63 is particle counter; 64 is a nut for driving screw A; 65 is a support plate; 66 is a housing for nut 64; 67 is a stopper for rotating of the housing; 68 is a motor; and 69 is a coupling between motor 68 and screw shaft 60. Testing conditions are as follows: Revolving speed 120 r.p.m. Load Axial load (25 N, 50 N, 75 N) Stroke 50 mm Atmosphere Open air in a clean bench (Class 10), Vacuum (2.6 x 10 -4 Pa or lower) Environment temperature Room temperature Measurement condition Dusting number of grains having grain size of 0.1 µm, or larger The driving screw A, used in the test has nominal identification numbers of 1404, 7TS3, and 5C7, which have 14 mm of shaft diameter in screw shaft 1, ball 3 having a diameter of 2 mm (3.5 rolls, 1 row), and lead having 3/16 inches (4.763 mm). In the dusting life test, the atmosphere, environment temperature, and axial load were set to open air, room temperature, and 75 N, respectively. In a dusting life test a time was measured, repeatedly 10 cycles, in which a total dusting amount reached to 0.1 cf/1000 ea. Each measurement was carried out with 10 minutes intervals. In each Examples, a concentration of the Foblin derivatives was varied as follows; 1 mass % of the Foblin Z Disoc, derivative in Example 1; 1 mass % of Foblin Z Disoc, derivative, as a base, and 0.25 mass % of Foblin Z Dol, derivative, added, in Example 2; 1 mass % of Foblin Z Disoc, derivative, as a base, and 0.25 mass % of Foblin Z-60, derivative, added, in Example 3; and 1 mass % of Foblin Z Disoc, derivative, as a base, and 0.25 mass % of total Foblin Z Dol, and Foblin Z-60, derivatives, added, in Example 4. As the results, the life in each Example was obtained as, 200 hours in Comparative Example, 300 hours in Example 1, 1400 hours in Example 3, and 1350 hours in Example 4. A time of dusting life in from long to short may be shown in an order of Example 3, Example 4, Example 2, Example 1, and Comparative Example. That is to say, even the solid film of fluoride containing urethane polymer compound, obtained by only using Foblin Z Disoc, derivative, as in Example 1, is superior in the dusting life to those of Comparative Example, however, the solid film 5, obtained by adding Foblin Z derivative, having a functional group at the side chain, or Foblin Z derivative having no functional group at the side chain, to the Foblin Z Disoc, derivative as a base, which was used in Examples 2 to 4, was further more superior to those of the Example 1. That is to say, since the solid film 5 of the fluoride containing polyurethane compound, used in Examples 1 to 4, forms three dimensional net work structure, and dense homogeneous film, when rolling and sliding movement was caused between each constitutional element of the driving screw A, a spalling and abrasion wear may be hardly caused. For instances, in Examples 3 and 4 , when the axial load was 50 N, the dusting life becomes 5600, and 5500 hours, respectively, whereas the axial load is 20 N, the dusting life was to be improved in as 14000, and 139000 hours, respectively. In the case of Examples 2 and 1, the dusting life was also improved in the same ratio as in the case of the Examples 3 and 4, above. On the other hand, in the Comparative Example, when the axial load is 50 N, the dusting life is prolonged to as long as 260 hours, however, it is of fairly lower level improvement, comparing with those in Examples 3 and 4. Accordingly, the material of the solid film may be preferably selected, depending on a object element, from any solid film, used in Examples 1 to 4. From the results discussed above, it is understood that as regarding the solid film of the fluoride containing polyurethane compound, those made of the fluoride containing polymer, prepared by adding fluoride containing polymer having fluidity is more preferable than those made by exclusively using the fluoride containing polymer having an isocyanate functional group at terminal end. As for the fluoride containing polymer to be added, it is also understood that the fluoride containing polymer having no functional group is the most preferable. Under the circumstances, an addition amount of the lubricants is considered below. The dusting life under 100 N of the axial load, was tested using 1 mass % of Fonblin Z Disoc, derivative, as a base polymer, with adding Foblin Z-60, derivative, in a concentration of 0.25 mass %, and 0.5 mass % respectively. The result shows 1400 hours and 990 hours, in a case of concentrations in 0.25 mass % and 0.5 mass %, respectively, and the result in a case of concentration in 0.25 mass % is considered to be adequate. However, as regarding the addition amount, with leaving a margins of upper and lower limits in a certain extent, a concentration of the Foblin Z-60 derivative, which is to be added to 1 mass % of Foblin Z Disoc derivative, as a base, may be within a range of 0.1 to 0.75 mass %. Further, a concentration of the Foblin Z Disoc derivative, as a base, may be within a range of 1 to 10 mass %. In this case, when the concentration of the Fonblin Z Disoc derivative, as abase, takes, for example, 5 mass %, which is the upper limit thereof, a concentration of the Foblin Z-60 derivative, added, may also be within a range of 0.5 to 2.5 mass %, so that both concentrations are established in always constant level. However, when the concentration of the base becomes thicker, the dusting life tends to be lowered. Furthermore, the present invention is not limited to the examples above, and several application and variation may be considered. (1) At one or both ends of the axis direction of nut 2, a non-contacting type seal, which is proximity to a spiral groove 11 of the screw stem 1 may be provided, on demand, and may contribute in more lowering dusting property. Said seal may be formed into a cylindrical shape of an elastic material, such as synthetic rubber, and may have convex part, having a cross section which is proximity to a spiral groove 11 of the screw stem 1, within a required angle range on an interior surface. (2) In the above Examples, a diving screw of type for providing ball is referred to, however, a driving screw providing no ball, as shown in Fig. 8, may be available according to the present invention. In this case, the solid film 5 may be enough for forming in at least either one of the spiral groove 11 of the screw stem , and spiral groove 21 of the nut 2. (3) In the above Examples, a curing treatment ( c) my utilize an energy of electromagnetic ray (light), such as ultraviolet ray, infrared ray, y ray, and electron beam, in place of heatings. (4) In the above Examples, a drying treatment (b) may be omitted. (5) Although over all of the constitutional elements of the driving screw A in the above Examples, solid film 5 of the fluoride containing urethane polymer compound is formed, the solid film may be formed only over the screw stem 1 and nut 2, or only over ball 3, in the driving screw A, (6) In the above Examples, although the solid film 5 of the fluoride containing polyurethane compound is also formed over the outer face of the coating object, only over the spiral grooves 11, and 21, for the driving screw A, or only over the inner surface for the circular tube, the solid film may be formed, exclusively. In this treatment, a part, where a coating is not required, is covered with masking, and each element, thus covered, is immersed into a solution, prepared in the treatment (a), in advance of assembling thereof into the diving screw A, is cured each optionally. However, if the solid film 5 is also formed over the outer surface, a corrosion resistant effect is enhanced in the utilization under corrosive environment, thereby saving additional corrosion resistant treatment.

Claims: A driving screw, comprising a screw stem (1) and nut (2), each having sliding parts which spirally engage each other, characterized in that at least one of the sliding parts of screw stem and nut have a solid film (5) of a fluoride containing polyurethane compound formed thereon, said solid film having a three dimensional structure. The driving screw according to claim 1, further comprising a plural number of rolling elements (3), which are interposed in a spiral path between the screw stem (1) and the nut (2), wherein said solid film (5) is formed on at least either the rolling elements or the sliding parts. The driving screw according to claims 1 or 2, wherein a fluidizable fluoride containing polymer is dispersed and added in said solid film (5). The driving screw according to claim 3, wherein said fluidizable fluoride containing polymer has no functional group. A method for forming a lubricant film on a driving screw as defined in claim 1, which comprises attaching a liquid film on at least one of the constitutional elements of the driving screw using a solution, in which a fluoride containing polymer having an isocyanate group as a functional group is dissolved with a solvent, and curing the liquid film attached to form a solid film of the fluoride containing polyurethane compound having a net work structure. The method according to claim 5, which comprises using a solution, in which a mixture of a fluoride containing polymer having an isocyanate group as a functional group and a fluoride containing polymer containing at least one of hydroxyl group, amino group, and carboxyl group, is dissolved with a solvent. The method according to claim 5, which comprises using a solution, in which a mixture of a fluoride containing polymer having an isocyanate group as a functional group alone or in combination with a fluoride containing polymer containing at least one of hydroxyl group, amino group, and carboxyl group, and a fluoride containing polymer having no functional group is dissolved with a solvent, and partially curing the liquid film attached to form a solid film of the fluoride containing polyurethane compound having a net work structure, while maintaining a fluidity of the fluoride containing polymer having no functional group.

Inventors: HAYASHIDA KAZUNORI, TAKEBAYASHI HIROAKI, TOYOTA HIROSHI, HAYASHIDA, KAZUNORI, TAKEBAYASHI, HIROAKI, TOYOTA, HIROSHI, HAYASHIDA, Kazunori Koyo Seiko Co., Ltd., TAKEBAYASHI, Hiroaki Koyo Seiko Co., Ltd., TOYOTA, Hiroshi Koyo Seiko Co., Ltd.
Applicants: KOYO SEIKO CO, KOYO SEIKO CO., LTD.
Application year: 1996
Main classification: F16H25
IPC codes: H01L21, C09D175, C10N40, C08G18, F16H25, F16H57