METHOD FOR MAKING AN ARTICLE HAVING A GRADIENT OF COMPOSITION

Abstract: According to the invention, a) at least the first and second compositions of this material in the fluid phase are prepared, b) a sheet (61) of the first composition is poured continuously onto a flat support (4), c) a sheet (62) of the second composition is poured continuously onto sheet (61) of the first composition, and d) the thermal interdiffusion of the materials of the two sheets is ensured so as to obtain the desired gradient of composition in the cooled bar.

Description: METHOD FOR MAKING AN ARTICLE HAVING A GRADIENT OF COMPOSITION The present invention relates to a method and a device for the manufacture of a bar with rectangular cross section made of a material presenting a gradient of composition perpendicular to two opposite longitudinal sides ofthe bar and, more particularly, to such a method and a device which allow the manufacture of a glass bar having one characteristic, such as refractive index, optical density, ionic conductivity, etc., which presents a predetermined profile gradient, established as a result of a variation in its composition, peφendicular to said opposite sides ofthe bar. Optical components are used today, such as lenses made of glass which presents a refractive index gradient which is parallel to the axis ofthe lens. To make such optical components, the starting material is a glass block whose composition varies along the axis ofthe component to be prepared, which variation is estabhshed using various techniques, such as ion exchange (see French Patent Application No. 2,504,515), impregnation with the so-called "sol gel" technique (see U.S. Patent Application No. 5,069,700), the use of starting glass compositions made of powder (U.S. Patent Apphcation No. 4,883,522), the use of selectively doped porous glass (U.S. Patent No. 4,620,861), the assembly by melting of platelets made of glass with varying composition (U.S. Patent Application No. 4,929,065), or other techniques such as exposure to neutron radiation, deposition of glass in the vapor phase, etc, etc. The techniques used in the past share the feature that they apply discontinuous manufacturing processes, that is, in lots; this continuity implies downtimes which have a negative effect on productivity and thus also on the lowering of production costs. The gradients of indices obtained also were found to be insufficient in some applications and the profile insufficiently controlled. The present invention therefore has the purpose of implementing a method and providing a device which allows the manufacture of bars with rectangular cross section made of a material which presents a gradient of composition perpendicular to two opposite longitudinal sides ofthe bar, and notably bars made of glass for the preparation of optical components with an axial gradient of composition, which bars present none of the above-mentioned drawbacks ofthe known methods and devices. This purpose ofthe invention is achieved, as well as others which will become apparent upon reading the following description, with a method for the manufacture of a bar with rectangular cross section made of a material presenting a gradient of composition perpendicular to two opposite longitudinal sides ofthe bar, which material is in the fluid phase at a temperature above ambient temperature, and which method is characterized in that a) at least the first and second compositions of this material are prepared in the fluid phase, b) a sheet ofthe first composition is poured continuously on a flat support, c) a sheet ofthe second composition is poured continuously on the sheet ofthe first composition, d) the interdiffusion ofthe materials ofthe two sheets by a thermal method is ensured so as to obtain the desired gradient of composition in the cooled bar. With the method ofthe invention, a bar can be prepared in a continuous process, which bar consists of a material such as glass which presents the required transverse gradient of composition, where the continuity ofthe method allows for of high productivity and reduced manufacturing costs. For the implementation of this method, the invention provides a device which comprises a support which advances on a looped travel path which presents a flat part, where a number of reservoirs each receive one ofthe compositions of an equal number of different compositions ofthe material, each reservoir being equipped with means for the formation of a sheet ofthe material which flows by gravity from the reservoir, the reservoirs being spaced at intervals along the flat part ofthe travel path ofthe support so that said sheets flow out one above the other, above the support. According to one embodiment ofthe device according to the invention, the device also comprises means for the transverse cutting ofthe bar formed into bar elements, heating means and means to load these elements in these heating means so as to ensure the development ofthe process of interdiffusion ofthe sheets of each element until the desired gradient of composition is established in said element. Other characteristics and advantages ofthe present invention will become apparent upon reading the following description and examining the drawing in the appendix in which: - Figure 1 is a diagrammatic representation ofthe structure of a glass bar obtained by the method according to the present invention, - Figure 2 is a diagram of a device designed for the implementation ofthe method according to the invention, - Figure 3 is a diagram of a variant of a part ofthe device of Figure 2, and - Figure 4 is a diagram illustrating the structure and the operation ofthe means for loading glass bar elements in heating means ofthe device of Figure 2. The present invention relates to the manufacture of a bar 1 (see Figure 1) made of a vitreous material, in particular an optical or ophthalmic glass, presenting a rectangular cross section and a gradient of composition along arrow F, that is, along a direction perpendicular to the two opposite sides of said bar. In the optical or ophthalmic applications considered primarily, but not exclusively, by this invention, the gradient of composition ensures the formation of a corresponding gradient of an optical property such as refractive index or optical density. By cutting the bar 1 transversely (either perpendicular to its axis, parallel to the arrow F,) prepared according to the invention, into separate elements, preforms can be made, for example, of optical lenses which are then shaped by grinding and mechanical polishing, or by molding, and which present an optical axis which is parallel to the arrow F. These lenses then present, once they are finished, an axial gradient ofthe desired optical property, for example, the refractive index. To prepare such lenses, the glass bar of Figure 1 is first manufactured using the device represented in Figure 2. The latter comprises n reservoirs 2,, 2^ 2 3 , (rj = 3 in the example represented), all designed to contain glass in the fluid state. Classically, the glass is maintained in this state by heating means (not shown) which are incoφorated in the reservoirs. According to the invention, the composition ofthe glass varies from one reservoir to the other so that the refractive indices, for example, ofthe three compositions, are different, with an incremental progression, for example. The bottom of each reservoir 2,, 2 2 , 2 3 is equipped with a casting slit 3„ 3 2 , 3 3 , respectively, designed to form a sheet of glass in the fluid state from the glass contained in the reservoir and to deposit this sheet onto a support 4, consisting, for example, of a belt which travels in a closed-loop path around two rollers 5 t and 5 2 which define between them a flat travel path for the beh 4. The reservoirs 2„ 2 2 and 2, and the slits 3„ 3 2 and 3 3 are spaced at intervals along this travel path so that the sheet of glass 6, exiting from slit 3, falls directly onto beh 4, possibly assisted by a shoe 7 placed at the drop point, so that sheet 6 2 exiting from slit 3 2 falls onto sheet 6, placed on the belt, and sheet 6 3 exiting from reservoir 3 3 falls onto sheet 6 2 . Heating means 8,, 8 2 and 8 3 are arranged in parallel to be 4 to maintain the sheets in paste-like condition (at a temperature much higher than the vitreous transition temperature T g ) as they are stacked on the belt. Walls (not shown), made of graphite, for example, limit the transverse extension ofthe sheets on the belt. At the moment ofthe forming ofthe bar, the interface between the two sheets can be slightly arched because ofthe friction on the graphite walls and the effect of surface tension. This defect can be corrected, if necessary, using rollers, such as the lamination roller 10 shown in Figure 3, placed downstream from each one ofthe slits, in contact with the sheet of material deposited through the slit. One can see that in this manner that a composite glass bar with a rectangular cross section is formed, which leaves the belt 4 (to the right ofthe point of view represented in Figure 2), the composition of this bar varying abruptly at the two interfaces between the sheets 6, and 6 2 on the one hand, and 6 2 and 6 3 on the other. Indeed, the phenomenon of heat diffusion which can cause a certain degree of interdiffusion between the two sheets at each one of these interfaces during the stacking ofthe sheets on the belt has very low sensitivity because such a diffusion requires a high temperature and a long contact time. The glass bar which Ieaves the belt thus does not present a composition which varies progressively in the direction of its thickness, when it may in fact be desirable to establish such a progression for certain optical components with a gradient of refractive indices, for example. As explained in French Patent Application No. 95,04646 filed on April 19, 1995, by the applicant, the required gradient of composition can be obtained then by the interdiffusion at high temperature of chemical elements which are capable of significantly modifying the value ofthe refractive index of glass, as a function of their local concentration in the glass. The interdiffusion takes place at the interfaces ofthe glass sheets. The selection ofthe glasses for these sheets depends on the desired difference in indices and the required type of profile. In the extreme case where there is no interdiffusion, a profile with discontinuous composition is obtained (stepwise). With reference to Figure 2 ofthe above-mentioned patent application, the appearance of "S" profiles of indices can be examined, which can be obtained by interdiffusion, the inflection point ofthe profile being located in the vicinity of an interface between glass sheets or layers. To establish a gradient of indices which varies progressively over the entire thickness of glass bar 1 by means ofthe device according to the invention, the glass bar must undergo, at the exit point of belt 4, a heat treatment at high temperature (temperature of diffusion) for several tens of hours, for example. According to a particular embodiment ofthe present invention, this treatment can be achieved by first cutting bar 1 into elements 1,, lj, ... lj... at a cutting station 11. This cutting operation is regular and it is conducted in the standard manner, with triggering by thermal shock or heat or sawing, as is well known. The length ofthe elements 1 ; is selected, for example, as a function ofthe dimensions of optical lenses with a gradient of indices to be formed by grinding or polishing, or by molding, ofthe material for each element, which then constitutes a preform for the desired lens. Preform 1*, so individualized, is placed by automatic mechanical means (not shown) in the mold 12 which then is conveyed into heating means 13 where the interdiffusion ofthe portions of sheets 6,, 6 2 and 6 3 which constitute the preform 1 ; will take place. These means consist of an arch through which a moving belt 14 passes, which conveys the preform l j5 over the entire length ofthe arch, between heating elements 15, and 15 2 . The latter establish in the arch the temperature profile T shown in Figure 2. This profile comprises a part a in which the temperature ofthe preform gradually increases up to the temperature T^ of diffusion, a part fc which corresponds to the greatest part of the length ofthe arch, where the diffusion proper takes place, and a part c where the temperature ofthe preform 1 ; is lowered to a value which allows the removal from the molds ofthe preforms at the exit ofthe arch, so that subsequent process can be performed on these preforms to make lenses from them with an axial gradient of indices, the axis ofthe lens being then oriented in parallel to the thickness ofthe preform (vertical, from the point of view of Figure 2). The parameters which allow the modification ofthe profile of indices obtained are the diffusion time (corresponding to the time it takes the preform to travel through the part of arch 13 which corresponds to the threshold b ofthe temperature profile T) and the positions ofthe interfaces ofthe sheets. By increasing the number n ofthe sheets, it is possible to shape the form ofthe profile more precisely and to obtain, for example, a parabolic profile. Regardless ofthe number of sheets, the densities ofthe glasses which comprise them must be selected so that they are stacked one atop the other in decreasing order of density so as to preserve the gradient during the passage in the arch, where the glass can return to the hquid phase because ofthe high temperature established in this arch. In the latter case, the lamination rollers described in connection with Figure 3 are no longer necessary. The positioning ofthe interfaces also depends on the thickness ofthe sheets. In this regard, the parameters which can be modified are the flow rates ofthe glass from reservoirs 2 ; (and the ratios of these flow rates) as well as the speed ofthe beh 4, which can ensure a predetermined drawing ofthe sheets and thus a modification of their thicknesses. As an illustrative and nonlimiting example, the method and the device according to the invention allow the manufacture of 100 kg/h of preforms into a bar with a rectangular cross section 80 x 10 mm, formed of two glass sheets with a thickness of 5 mm (made of a commercial white glass or a lead-containing glass, for example). For this purpose, an arch 13 with a length of 30 m is constructed, which is heated at a diffusion temperature of 1200°C. The mold which supports the preform is made of graphite or of boron nitride. An inert atmosphere (nitrogen, for example) is then required in the arch to ensure the maintenance ofthe temperature ofthe mold. The glass bar exits the belt 4 at a speed of 1.157 cm/sec. The speed ofthe mold in the preform is 1 m h for a residence time of 30 h. Since the speed (30 m/h) of belt 14 in the arch is slow compared to the exit speed ofthe glass bar from belt 4, h is advantageous to have loading means 16 in the arch ofthe preforms cut into the bar, which absorb the differences in the glass flows. According to the present invention, these loading means 16 have the form shown in Figure 4, which represents diagrammatically in a top view glass bar 1 exiting belt 4, to be cut at station 11. After the cutting, mechanical transfer means (not shown) place each preform in a mold, and the molds so loaded are aligned transversely to beh 14 of arch 13 before being placed on this beh. Thus, several preforms are heat treated in the arch in parallel. It is sufficient to select the width ofthe belt 14 which exactly adapts the flow rate of belt 4 to that of belt 14. With the numbers indicated above, this adaptation is obtained by placing preforms in molds side by side in arch 41 and in that case, belt 14 has an approximate width of 3.3 m. It now becomes apparent that the invention does in fact realize the stated purpose, that is to provide a method and a device for the manufacture of elements with rectangular cross section made of a material presenting a gradient of composition peφendicular to two opposite sides ofthe element, which do not present the drawbacks ofthe discontinuous methods ofthe prior art. Thanks to its continuous character, the method according to the invention allows the increasing of productivity and the decreasing of production costs. It should also be noted that the method according to the invention allows the modification, by very simple means, ofthe composition ofthe bars by the addition of additional sheets, without changing the subsequent steps of heat treatment. Naturally, the invention is not limited to the embodiment which has been described and represented only as an example. Thus, the invention is not limited to the manufacture of lenses with a gradient of refractive indices for optical or ophthalmic use; it can also be applied to the manufacture of filters with variable optical density or blocks of materials with variable ionic conductivity, for example.

Claims: Claims 1. Method for the manufacture of a bar with rectangular cross section made of a material presenting a gradient of composition perpendicular to two opposite longitudinal sides ofthe bar, which material is in the fluid state at a temperature which is higher than ambient temperature, characterized in that: a) at least the first and second compositions of this material in the fluid state are prepared, b) a sheet (6,) ofthe first composition is poured continuously onto a flat support (4), c) a sheet (6 2 ) ofthe second composition is poured continuously on sheet (6,) of the first composition, and d) the interdiffusion ofthe materials ofthe two sheets is ensured by a thermal method to obtain the desired gradient of composition in the cooled bar. 2. Method according to Claim 1, characterized in that a predetermined profile of the gradient of composition is prepared by selecting the position ofthe interface ofthe two sheets and by regulating the temperature and the duration of their thermal interdifiusion. 3. Method according to Claim 2, characterized in that the ratio ofthe pouring flow rates ofthe two sheets is regulated to adjust the position ofthe interface. 4. Method according to any one of Claims 1 to 3, characterized in that n different compositions ofthe material in the fluid state are prepared (n > 2) and in that n (6j) sheets of these compositions are poured one atop the other, in order of decreasing density. 5. Method according to any one ofthe preceding claims, characterized in that, after solidification, the formed bar ( 1 ) is cut continuously into bar elements ( 1 ) and in that these elements are subjected to a heat treatment to ensure the interdifiusion ofthe layers which comprise them. 6. Method according to any one ofthe preceding claims, characterized in that the established gradient of composition corresponds to a predetermined gradient of refractive indices. 7. Device for the implementation ofthe method according to any one of Claims 1 to 6, characterized in that it comprises moving support (4) which moves in a looped travel path presenting a flat part, a number of reservoirs (2,, 2^ 2 3 ) each receiving one of the compositions of an equal number of different compositions of said material, each reservoir being equipped with means for the formation (3,, 3 2 , 3 3 ) of a sheet (6 l5 6 2 , 6 3 ) ofthe material which flows by gravity from the reservoir; the reservoirs (2,, 2^ 2 3 ) being spaced at intervals along this flat part ofthe travel path of support (4) so that said sheets flow one atop the other above support (4). 8. Device according to Claim 7, characterized in that it comprises lamination roller (10) associated with each reservoir to laminate the sheet which exits from h onto the underlying sheet. 9. Device according to any one of Claims 7 and 8, characterized in that the sheets (6,, 6 2 , 6 3 ) are stacked one atop the other in order of decreasing density. 10. Device according to any one of Claims 7 to 9, characterized in that it comprises means for the adjustment ofthe speed ofthe moving support as a function of a predetermined thickness of at least one ofthe sheets on the support. 11. Device according to any one of Claims 7 to 10, characterized in that comprises means (11) for transversely cutting the formed bar (1) into bar elements (l , heating means (13) and means (16) to load these elements (lj) in these heating means (13) so as to ensure the development ofthe process of interdiffusion ofthe portions of sheets of each element (2 until the desired gradient of composition is established in said element (lj. 12. Device according to Claim 11, characterized in that said loading means (16) have a number of elements (I) aligned such that they can be passed in parallel to said heating means (13). 13. Preform ( l of an optical device with an axial gradient of an optical property, obtained by cutting a bar (1) made of a vitreous material manufactured by the method according to any one of Claims 1 to 6.

Inventors: GILLE CLAUDE FRANCOIS MAURICE, KERDONCUFF ALAIN, PRASSAS MICHEL, GILLE, CLAUDE, FRANCOIS, MAURICE, KERDONCUFF, ALAIN, PRASSAS, MICHEL
Applicants: CORNING INC, GILLE CLAUDE FRANCOIS MAURICE, KERDONCUFF ALAIN, PRASSAS MICHEL, CORNING INCORPORATED, GILLE, CLAUDE, FRANCOIS, MAURICE, KERDONCUFF, ALAIN, PRASSAS, MICHEL
Application year: 1996
Main classification: C03B13
IPC codes: C03B17, C03B19, C03B32, C03B37