POLYMERS FOR ANTIFOULING COATINGS AND A PROCESS FOR THE PREPARATION THEREOF

Abstract: Polymer for antifouling coatings which comprises units corresponding to the following monomers: A) 5 to 100 mol-% of one or more c ompounds of general formula (I), in which: X = H, CI, Br or F; R = Ph(R<1>)m or benzyl; R<1> = each independently selected from halogen, -C(O)H, -COOR<2>, -CH2-COOR<2>, -O-R<2>, -O-CO-R<2>, -NH-CO-R<2>, -NH-COOR<2>, -SO3H, and optionally substituted thiadiazolyl and thiazolylsulfamyl groups; Ph = phenyl; m = 1 - 3; R<2> = H or optionally halogen substituted alkyl, aryl, cycloalkyl, aralkyl groups with 1 - 10 C atoms; and B) 0 to 95 mol-% of one or more other ethylenically unsaturated compounds. Process for preparing the polymers defined above, paints containing said polymers, and the use of the monomers of formula (I) for preparing polymers for antifouling coatings.

Description: Polymers for antifouling coatings and a process for the preparation thereof The present invention relates to tin-free, hydrolysable polymers for use in antifouling coatings and a process for the preparation of tin-free, slowly hydrolysable, polymerisable compounds which can be used for the preparation of binder systems for antifouling coatings to protect underwater surfaces against the growth of marine organisms. Under suitable conditions, surfaces which are permanently exposed to sea water such as ships, buoys, drilling platforms, underwater pipelines, fishing nets etc. very quickly become overgrown with marine organisms such as algae, sea grass, mussels, tube worms, sponges etc. This growth proves extremely troublesome in a lot of cases; it restricts, and is prejudicial to the characteristics pertaining to the use of many types of equipment. For example, the growth on underwater surfaces of ships results in a limitation of their manoeuvrability and a substantial additional consumption of fuel because of the increased frictional resistance in the water. For these reasons coatings known as antifouling paints which prevent such growths are widely used to protect underwater surfaces against the settlement of these organisms. These paints generally consist of a biocidal or non-biocidai polymeric film- forming binder, together with cobiocides and pigments. Antifouling paints which have frequently been used in recent years not only prevent growths but also possess self-polishing film properties ("self-polishing" copolymers). In these systems, the self-polishing effect is obtained by the controlled hydrolysis of functional groups which cause the paint surface to become hydrophilic and hence erodible. These paints are for example described in EPA-0289481. Antifouling paints whose copolymers contain thorgano tin esters, in particular tri-n-butyl and triphenyl tin esters, are widely used. Examples are described in GB 457590. Because of the slow and controlled hydrolysis of the triorgano tin ester group, these systems have self-polishing properties and also excellent antifouling characteristics because of the biocidal effect of the tributyl/triphenyl-tin compound. This particularly favourable combination of properties has resulted in the widespread use of tin-based antifouling paints. In recent years the use of paints which contain tributyl/triphenyl-tin has been the subject of controversy as the strong biocidal effect of these systems does not appear to be necessary in ail areas. In some countries, the use of antifouling paints which contain tributyl/triphenyl-tin on yachts and ships with a length of less than 25 m has been limited or even prohibited. There is therefore a need for effective, tin-free, slow and controlled hydrolysable antifouling paint systems. Various examples of antifouling paints characterized by groups which are hydrolysable in sea water are described in the relevant literature. For example, WO 84/02915 lists a large number of possible structures which are reported to form readily hydrolysable compounds with groups which contain carboxylic acid. Further tin-free antifouling coatings are described in EP-A-0 204444, EP-A-0 331 147 and GB 2 152 947. However, all these systems have either not been used commercially or else require a multi-stage and relatively complex process of synthesis for their preparation. From WO 94/17126, US 4 111 879 and US 5 288408 it is known that polymeric binders, which contain N-substituted maleimides, can show a growth-impeding effect. A disadvantage concerning these systems is however that the N-substituted maleimides either are only physically mixed into a polymeric binder or are chemically fixed into a highly cross-linked polymer system. This means that the N-substituted maleimide compounds are either leached out in water rapidly or, due to their strong fixation, show no or an insufficient slow hydrolysis. We have discovered that, unlike polymer systems which are structured solely on an acrylic or methacrylic basis with a corresponding slow and insufficient hydrolysis, copolymers based upon N-(substituted aryl) maleimides and acrylic or methacrylic monomers can be hydrolysed in an alkaline environment (sea water pH: 8.1-8.3). This hydrolysis is a prerequisite firstly for the self-polishing properties and secondly for a growth-impeding effect of the paint as a result of the slow and continuous release of the hydrolysed compounds. Furthermore we have discovered that the use of N- (substituted aryl) maleimides and/or N-benzyl maleimide has several advantages in comparison to N-alkyl maleimides. Especially the easier synthesis, leading to higher yields, their copolymerisability, film forming properties and mechanical film properties as well as their constant hydrolysis rates are worth mentioning. Special functional groups (substituents on the phenyl ring of the aryl maleimides) result in extraordinary favourable copolymers, especially compared with N-(substituted alkyl) maleimide based copolymers. in addition, a special advantage of the present invention is that the N-substituted maleimide monomers are chemically bond into a linear, nearly non- branched or non-cross-linked polymer chain. Thus a slow and controlled hydrolysis of the maleimide groups is possible which leads to a partial hydrophilic polymer surface that by this means becomes soluble and erodible. The present invention accordingly relates to a polymer for use in antifouling coatings and it is characterized in that it comprises units corresponding to the following monomers A) 5 to 100 mol-% of one or more compounds of the general formula I I in which: X = H, CI, Br or F R = Ph(R 1 ) m or benzyl R 1 = each independently selected from halogen, -C(O)H, -COOR 2 , -CH 2 -COOR 2 , -O-R 2 , -O-CO-R 2 , -NH-CO-R 2 , -NH-COOR 2 , -SO 3 H, and optionally substituted thiadiazolyl and thiazolylsulfamyl groups Ph = phenyl m = 1 - 3 R 2 = H or optionally halogen substituted alkyl, aryl, cycloalkyl, aralkyl groups with 1 - 10 C atoms and B) 0 to 95 mol-% of one or more other ethylenically unsaturated compound The optionally substituted thiadiazolyl groups as R 1 in the general formula I can be 1 ,2,4-thiadiazolyl unsubstituted or substituted with halogen, alkyl with 1 - 4 C atoms or phenyl. The optionally substituted thiazolylsulfamyl groups as R 1 in the general formula I can be unsubstituted or substituted with halogen or alkyl with 1 - 4 C atoms. Another object of the invention is a process for the preparation of binders for use in antifouling coatings by homopolymerisation or copolymerisation of polymerisable monomers, characterized in that the polymerisable monomers which are polymerised consist of mixtures of one or more of component A) and one or more of component B). Other features of the invention are as defined in the claims. Examples of the substances which may be used as component A) for the preparation of binders for antifouling coatings include substituted N-(phenyl) maleimides, such as N-(2-chlorophenyl) maleimide, 5 N-(4-chlorophenyl) maleimide, N-(4-bromophenyl) maleimide, N-(2,3-dichlorophenyl) maleimide, N-(2,4,6-trichlorophenyl) maleimide, N-(2,4,6-tribromophenyl) maleimide, N-(4-methoxyphenyl) maleimide, N-(4-hydroxyphenyl) maleimide, N-(4-carboxyphenyl) maleimide, N-(4-sulfophenyl) maleimide, N-(4-acetoxyphenyl) maleimide, N-(3-ethyloxycarbonylphenyl)maleimide, N-(4-methyloxycarbonylphenyl) ιo maleimide, N-(4-ethyloxycarboriylphenyl)maleimide, N-(4-formylphenyl) maleimide, N-(4-acetylaminophenyl) maleimide, N-(4-carboxymethylphenyl) maleimide, . N-(thiazolylsulfamyl) maleimide; N-substituted 2,3-dichloromaleimides,such as N-(4-carboxyphenyl)-2,3- i5 dichloromaleimide, N-(4-chlorophenyl)-2,3-dichloromaleimide, N-(4-ethyloxycarbonylphenyl)-2,3-dichlorαmaleimide. Preferred examples are N-(4-chlorophenyl) maleimide, N-(2,4,6-trichlorophenyl) maleimide, N-(2,4,6-tribromophenyl) maleimide, N-(4-hydroxyphenyl) maleimide, 20 N-(4-carboxyphenyl) maleimide, N-(4-acetoxyphenyl) maleimide, N-(4-ethyloxycarbonylphenyl)maleimide, N-(thiazolylsulfamyl) maleimide, N-(4-chlorophenyl)-2,3-dichloromaleimide,N-(4-ethyioxycarbonylphenyl)-2,3- dichloromaleimide. 25 The ethylenically unsaturated compounds B) which may also be used in conformity with the invention, are monomers such as: 1) Compounds containing carboxylic groups, e.g. acrylic acid, methacrylic acid, maleic acid and itaconicacid. 30 2) C,-C 18 esters of acrylic or methacrylic acid, such as e.g. methyl acrylate, ethyl acrylate, propyl acrylate, n-butyl acrylate, n-hexyl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, i-propyl methacrylate, n- butyl methacrylate, n-hexyl methacrylate or n-dodecyl methacrylate; s C 2 -C 18 alkoxy esters of acrylic acid or methacrylic acid such as methoxy ethyl acrylate, methoxy ethyl methacrylate, methoxy butyl acrylate, methoxy butyl methacrylate, ethoxy butyl acrylate or ethoxy butyl methacrylate; C 2 -C 8 hydroxy alkyl acrylates or hydroxy alkyl methacrylates such as hydroxy ethyl acrylate, hydroxy ethyl methacrylate, hydroxy propyl acrylate or hydroxy o propyl methacrylate; silicon containing esters of acrylic acid or methacrylic acid such as (3-methacryloyloxypropyl)-trimethoxysilane, (3-methacryloyloxypropyl)- triethoxy-silane, trimethylsilyl methacrylate. s 3) Vinyl compounds such as styrene, α-methyl styrene, vinyl toluene, p-chlorostyrene, vinyl acetate, 4-vinyl pyridine or vinyl pyrrolidone. The preparation of antifouling binder systems can be effected by radical or ionic copolymerisation of the monomers A) of formula I, usually together with ethylenically 0 unsaturated compounds B). Compounds containing conventional peroxide or azo groups may be used as the radical starter (initiator) e.g. dibenzoyl peroxide, bis-(α-,α- dimethyl benzyl) peroxide, tert-butyl hydroperoxide, potassium peroxo-disulphate, 2,2'-azobis isobutyronitrile and 2,2'-azobis-(2-methyl butyronitrile) normally in concentrations of 0.01 to 5 % by weight of the monomer mixture which is used. The 5 copolymerisation is preferably carried out in suitable solvents by means of solution or precipitation polymerisation. The following are examples of which substances may be used for this purpose: aromatic or aliphatic hydrocarbons such as toluene, xylene, hexane, heptane, petroleum ether; esters such as ethyl acetate, butyl acetate; ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone; ethers such as 0 ethylene glycol dimethyl ether, diethylene glycol dimethyl ether (diglyme), dibutyl ether, 1 ,4-dioxane, tetrahydrofurane, 1-methoxy-2-propanol or solvents such as N,N-dimethyl formamide, N-methylpyrroiidin-2-one, dimethyl sulphoxide, water or butanol, possibly as a mixture. Depending on the desired viscosity, the monomer concentration can range between 5 and 80% by weight with reference to the total solution. The copolymerisation itself can be carried out by means of known techniques such as heating of the monomers with the initiators in the solvent or by dropping the monomers and initiators into the heated solvent. Depending on the composition of the monomer mixture and the chosen copolymerisation conditions, copolymers with varying composition and with average molecular weights in the 5000 to 200,000 range can be obtained. The antifouling binders which are prepared in this way can be mixed with auxiliary substances and additives such as pigments, biocides and stabilizers as described in US 5 332 430. Examples of pigments include titanium dioxide, activated carbon, iron oxide and blue pigments. Examples of biocidal agents include cuprous oxide, cuprous thiocyanate, zinc oxide, zinc pyrithion, zinc-bis(dimethyl-dithio carbamate) together with compounds which contain e.g. benzothiazols, dithiocarbamates, triazine, thiodiazine, thiadiazole, isothiazoline and quaternary ammonium salts. Examples of other additives include fillers such as silicon dioxide, kaolin, talcum and auxiliary substances such as bentonite, aerosil and similar compounds. The present invention is described in more detail in the following examples. Examples Example 1 General synthesis instructions for the preparation of monomers A three-necked flask is charged with 0.7 mol maleic anhydride, 450 ml N,N-dimethyl formamide and 0.7 mol of the appropriate starting compound with a primary amino group. The mixture is stirred at room temperature under a nitrogen atmosphere for 5 h, then poured into a large amount of cold water to precipitate the corresponding maleamic acid. The crude maleamic acid is filtrated, washed with water and. dried in a vacuum oven. A mixture of the maleamic acid, 300 ml acetic anhydride and 8.2 g sodium acetate is stirred at 60°C for 2 h. The resulting solution is poured into a large amount of cold water to obtain the crude N-substituted maleimide. After filtration, washing with water and drying in a vacuum oven the product is recrystallized from methanol / water (6:1 , v/v) or cyclohexane. Example 2 General synthesis instructions for the preparation of monomers A three-necked flask is charged with 0.8 mol maleic anhydride and 50 ml of toluene. The mixture is slurried with vigorous stirring and a mixture of 0.8 mol of the appropriate starting compound with a primary amino group in 150 ml toluene is added slowly from a dropping funnel. The resulting solution is refluxed for 1 h and then filtrated warm to obtain the crude corresponding maleamic acid. A mixture of the vacuum dried maleamic acid, 500 ml acetic anhydride and 35 g sodium acetate is stirred at 70 β C for 2 h, then poured into a large amount of cold water. The crude N-substituted maleimide is filtered off, washed with water and dried in a vacuum oven. For purification it is recrystallized from ethanol or cyclohexane. Example 3 General synthesis instructions for the preparation of monomers A three-necked flask, equipped with thermometer, water separator, dropping funnel and stirrer is charged with 0.5 mol maleic anhydride and 350 ml of xylene. A mixture of the appropriate starting compound with a primary amino group is added slowly from the dropping funnel at room temperature. Afterwards the mixture is stirred at 65°C for 2 h. Then, 2 g of sulphuric acid are added and the reaction is carried out with stirring at 135 -140°C, with the water formed during the reaction expelled out of the reaction system by azeotropic distillation with the help of the water separator. After the reaction, the mixture is poured into 750 ml cold water. The N-substituted maleimide is filtered off, washed with water and dried in a vacuum oven. The product is recrystallized from ethanol or cyclohexane. Table 1 : Synthesis of monomers Product Starting Compound Synthesis pursuant Yield Melting to Example-No. point N-(4-chlorophenyl)maleimide maleic anhydride (68.6 g) / 4-chloro-aniline(89.3 g) 1 51 % 110 - 112°C N-(2,4,6-tribromophenyl)maleimide maleic anhydride (49.0 g) / 2,4,6-tribromoaniline(164.9 g) 3 53 % 142°C N-(4-carboxyphenyl)maleimide maleic anhydride (68.7 g) / 4-amino-benzoicacid (95.9 g) 1 65 % 232 - 234°C N-(4-acetoxyphenyl)maleimide maleic anhydride (75.0 g) / 4-amino-phenol (54.0 g) 2 48 % 157 - 158°C N-(4-ethyloxycarbonylphenyl)maleimide maleic anhydride (68.7 g) / 4-amino-benzoicacid ethyl ester 1 72 % 111 - 112°C (115.6 g) N-(thiazolylsulfamyl)maleimide maleic anhydride (68.7 g) / sulfathiazol (178.7 g) 1 78 % 168 - 175°C N-(4-chlorophenyl)-2,3-dichloromaleimide 2,3-dichloro-maleicanhydride (116.9 g) / 1 65 % 175°C 4-chloroaniline(89.3 g) N-(4-ethyloxycarbonylphenyl)-2,3- 2,3-dichloro-maleicanhydride (16.7 g) / 1 54 % 197°C dichloromaleimide 4-aminobenzoicacid ethyl ester (16.5 g) N-Benzyl maleimide maleic anhydride (98.1 g) / benzyl amine ( 107.2 g) 3 62 % 69 - 70°C All the above monomers have a hydrolysis rate >95% after 24 hours. Example 4 General instructions for copolymerisation of the monomers The amount of component A (N-substituted maleimide) and of components B (comonomers) corresponding to the desired copolymer composition are transferred to a three-necked flask together with the solvent and the initiator. To remove oxygen, the solution is stirred for 30 minutes in a constant stream of nitrogen. The mixture is then heated to 80°C and copolymerised for 4 hours under these conditions. The solids content of the solution is determined. The copolymer can be recovered in the pure state by precipitation in methanol or petroleum ether and isolation in a known manner (filtration). 10 Example 5 is General instructions for the preparation of antifouling paints 75 g of the copolymer (e.g. P1-P13, VP1-VP2) as a 40-50% solution, 5 g of cuprous oxide, 13 g of zinc oxide, 11.1 g of Bentone 38 (gelling agent based on Montmorillonite earth, made by Titangesellschaft, 6% solution in xylene) and 10 g of xylene are ground intensively for one hour. Table 2: Copolymerisation No. ComponentA Component B Solvent Initiator Solids Content P 1 N-(4-bromophenyl) maleimide (75.6 g) butyl methacrylate (43.2 g) / butyl acetate (223.0 g) AMBN 3) ( 3.28 g) 48.7 % dodecyl methacrylate (102.8 g) P 2 N-(4-chlorophenyl)maleimide (51.9 g) butyl methacrylate (36.6 g) butyl acetate (87.5 g) AIBN (1.23g) 49.2 % P 3 N-(4-acetoxyphenyl)maleimide(18.5 g) butyl methacrylate (11.4 g) NMP 4) (70.0 g) AIBN (O.Oδ g) 29.2 % P 4 N-(4-acetoxyphenyl)maleimide (35.0 g) butyl methacrylate (21.6 g) / 1,4-dioxane(108.0g) AMBN (1.46 g) 45.0 % dodecyl methacrylate (51.4 g) P 5 N-(4-carboxyphenyl)maleimide(17.4 g) butyl methacrylate (11.4 g) NMP (67.2 g) AIBN (0.08 g) 30.0 % P 6 N-(thiazolylsulfamyl)maleimide(16.8g) butyl methacrylate (7.1 g) 1,4-dioxane(55.7g) AIBN (0.05g) 30.0 % P 7 N-(4-ethyloxycarbonylphenyl)maleimide dodecyl methacrylate (55.0 g) xylene (66.0 g) / 1-methoxy- AMBN (1.25 g) 45.0 % (53.0 g) 2-propanol(66.0 g) P 8 N-(4-ethyloxycarbonylphenyl)maleimide methyl methacrylate(10.9 g) / xylene (60.0 g) / 1-methoxy- AMBN (1.57 g) 50.0 % (40.0 g) dodecyl methacrylate (69.1 g) 2-propanol(60.0 g) P 9 N-(4-ethyloxycarbonylphenyl)maleimide butyl methacrylate (23.5 g) / xylene (60.0 g) / 1-methoxy-2- AMBN (1.59 g) 50.0 % (40.5 g) dodecyl methacrylate (56.0 g) propanol (60.0 g) P 10 N-(4-ethyloxycarbonylphenyl)maleimide butyl methacrylate (24.9 g) / xylene (60.0 g) / 1-methoxy- AMBN (1.68 g) 50.0 % (42.9 g) dodecyl methacrylate (44.6 g) / 2-propanol(60.0 g) 2-methoxy-ethylacrylate(7.6 g) P 11 N-(4-ethyloxycarbonylphenyl)maleimide butyl methacrylate (23.5 g) / dodecyl xylene (60.0 g) / 1-methoxy-2- AMBN (1.59 g) 50.0 % (40.6 g) methacrylate (42.1 g) / 3-methacryloyloxy- propanol (60.0 g) propyl trimethoxy silane (13.7 g) 12 N-(4-chlorophenyl)-2,3-dichloromaleimide butyl methacrylate (71.1 g) / 3-meth- xylene (11.7.0 g) / 1-methoxy- AIBN (3.61 g) 47.2 % No. Component A Component B Solvent Initiator Solids Content (138.3 g) acryloyloxypropyltrimethoxy silane (24.8 g) 2-propanol(117.0g) P 13 N-(4-ethyloxycarbonylphenyl)-2,3- butyl methacrylate (142.2 g) / 3-meth- xylene (182.0 g) / 1-methoxy- AIBN (5.25 g) 46.3 % dichloromaleimide(157.0 g) acryloyloxypropyltrimethoxy silane (24.8 g) 2-propanol(182.0g) VP 1 tri-n-buty Itin methacrylate (37.5 g) methyl methacrylate (20.2 g) xylene (57.5 g) AIBN (0.25 g) 49.0 % VP 2 — n-butyl methacrylate (142.2 g) xylene (142.2 g) AIBN (2.46 g) 49.7 % 1) N,N-dimethylformamide ) 2,2'-azobisisobutyronitrile 3) 2,2'-azobis-(2-methylbutyronitrile) 4) N-methylpyrrolidin-2-one Determination of the hydrolysis rate in alkaline environment (pH 12) To determine the hydrolysis rates of the binder systems in an alkaline environment, the conductivity or pH value changes are measured as a function of time. A direct measurement in sea water (pH: 8.1 to 8.3) is impossible for technical measurement reasons (high inherent conductivity because of the salt content). The measurements were performed as follows: 300 ml of bidistilled and degassed water are set to a pH value of 12 in a three-necked flask, equipped with a stirrer, pH electrode (WTW, Type E50-1.5) and a conductivity electrode (WTW, Type LTA 1 , cell constant 0.996) by adding NaOH pellets. The entire system is thermostatically set to 25 ± 0.1 °C (Haake Thermostat GH-D8). The measuring instruments which are used consist of a pH meter (WTW, Type pH 192) and a conductivity measuring instrument (WTW, Type LF 530). The monomer compounds shown in table 1 are introduced into an aqueous solution; in the case of the binder system in solution as shown in table 2, the substance is applied to glass beads with a diameter of 3 mm to achieve convenient layer thicknesses for practical use and the solvent is then removed with the aid of a vacuum pump. The quantity of the polymer binder system which is weighed in, is chosen in such a way that after theoretically complete hydrolysis a pH-value of 7 should be measured in the solution. To determine the hydrolysis rates, the coated glass beads are introduced into the above solution. The pH value and conductivity changes are determined directly, as a function of time, in the solution which is stirred under a stream of nitrogen to ensure better mixing. The measuring period totals 24 hours. The calculation of the hydrolysis rate is based on the change in the pH-vaiue, which decreases due to the hydrolysis of the polymeric binder system resulting in the formation of carboxylic groups as substituents on the polymer backbone. Measuring the pH-value after 24 h (starting pH: 12.00) and calculation of the functional groups based on the weighed copolymers enable a determination of the hydrolysis rate (%, based on the number of functional groups). The following table 3 clearly shows that the polymer binder systems according to the invention undergo hydrolysis in an alkaline environment under the chosen conditions. Table 3: Hydrolysis of polymer binder systems Binder System Hydrolysis rate (24 h) P1 28.3 % P2 25.2 % P3 35.8 % P4 32.6 % P5 40.1 % P6 21.4% P7 31.6% P8 26.5 % P9 22.3 % P10 31.9% P11 33.9 % P12 21.8% P13 23.0 % VP 1 (comparison) 30.9 % VP 2 (comparison) 3.2 % Determination of Hydrolysis Products of selected Maleimide Copolymers in Sea Water Four different copolymers have been synthesised according to example 4 for a demonstration of hydrolysis and an investigation of hydrolysis products of the described maleimide copolymers. Dodecyl methacrylate (DMA) is used as a hydrophobic comonomer in all cases. A tri-n-butyl methacrylate (TBTMA) / methyl methacrylate (MMA) copolymer and a butyl methacrylate (BMA) polymer have been included for comparison. The copolymer composition is shown in table 4. Table 4: Composition of copolymers for hydrolysis tests Functional monomer Comonomer Molar Solvent Non¬ Ratio volatile- matter N-(4-Ethyloxycarbonylphenyl) n-Dodecyl 1 : 1 methoxy propanol / 54.3 % maleimide [EPMI] methacrylate xylene (1/1, v/v) N-(4-Bromophenyl) maleimide n-Dodecyl 1 : 1 butyl acetate 27.7 % [BPMI] methacrylate N-(4-Carboxyphenyl) maleimide n-Dodecyl 1 : 1 methoxy propanol / 20.0 % [CPMI] methacrylate xylene (1/1, v/v) N-(4-Acetoxyphenyl) maleimide n-Dodecyl 1 : 1 1 ,4-dioxane 29.7 % [APMI] methacrylate Tri-n-butyltin methacrylate Methyl 1 : 2 xylene 49.0 % [TBTMA] methacrylate n-Butyl 1 xylene 49.7 % methacrylate All copolymers are precipitated in methanol or petroleum ether, separated from all solvents, washed with the precipitation agent and dried. Approx. 7 g of the precipitated copolymers (white to light yellow powders) are weighed exactly and suspended in 250 ml of sea water (starting pH : 8.2). The suspensions are vigorously stirred for 14 days at room temperature with a permanent monitoring of the pH-values. The suspensions are filtered and the separated copolymer powders are washed intensively and dried. The filtrate and the washing water are extracted twice with chloroform. After drying of the organic solution (Na 2 SO 4 ) the chloroform is removed in vacuum. The residues are weighed and analysed by 1 H-NMR. The results of these determinations are given in tables 5 and 6. Table 5: Results of the hydrolysis tests Copolymer pH: PH: Weight of the Weight of the Suspension Suspension extracted extracted hydrolysis after 7 d after 1 d hydrolysis products [%] stirring stirring products [g] (based on total copolymer amount) EPMI / DMA 8 7.5 0.84 11.95 BPMI / DMA 7 6 0.75 12.21 CPMI / DMA 3 2 0.83 13.85 APMI / DMA 7 7 0.48 7.74 TBTMA / MMA 7 6 1.15 16.39 BMA 8 8 0.12 1.66 Table 6: Results of the spectroscopic determinations of extracted hydrolysis products Copolymer Signals 1 H-NMR [ppm] 7.5 (m, 2 H ar.) anilinic hydrolysis product EPMI / DMA 7.7 (m, 2 H ar.) anilinic hydrolysis product 4.25 (t, 2 H) and 0.8 - 1.8 (m) hydrolysis products from dodecyl methacrylate 7.5 (m, 2 H ar.) anilinic hydrolysis product BPMI / DMA 7.7 (m, 2 H ar.) anilinic hydrolysis product 4.3 (t, 2 H) and 0.8 - 1.8 (m) hydrolysis products from dodecyl methacrylate 7.55 (m, 2 H ar.) anilinic hydrolysis product CPMI / DMA 7.8 (m, 2 H ar.) anilinic hydrolysis product 4.35 (t, 2 H) and 0.8 - 1.8 (m) hydrolysis products from dodecyl methacrylate 7.6 (m, 2 H ar.) anilinic hydrolysis product APMI / DMA 7.8 (m, 2 H ar.) anilinic hydrolysis product 4.25 (t, 2 H) and 0.8 - 1.8 (m) hydrolysis products from dodecyl methacrylate Anilinic hydrolysis products and hydrolysis products from dodecyl methacrylate (dodecanol) could be detected in all cases by 1 H-NMR. The results prove that the maleimide based copolymers show hydrolysis reactions with a release of hydrolysis products even in combination with long-chain, hydrophobic comonomers like dodecyl methacrylate. The hydrolysis rates of the copolymers can be adjusted by the amount of N- substituted maleimide and the type and amount of comonomers. Sea water exposure of antifouling coatings The antifouling effectiveness of the maleimide based copolymers according to the invention against marine organisms was determined by exposure tests in the North Sea (Cuxhaven, Germany). For this purpose, test sheets of polyvinyl chloride (10 x 15 x 1.4 cm) were provided with antifouling paints which were prepared according to example 5. The PVC sheets were degreased and subsequently coated with the antifouling paint and dried for 48 hours. The dry film thickness was 100 - 150 μm. The PVC sheets are clamped in a plastic frame and immersed in sea water at a depth of 1 meter for 8 months (February to October). Table 7 clearly shows that the test sheets with the paints according to the invention were free from animal and algae fouling during this period. The test sheets without the compounds according to the invention (comparison example VP 2, polybutyl methacrylate) showed considerably fouling by algae, mussels and barnacles. Table 7: Results of sea water exposure of test panels in the North Sea Antifouling Paint Example 4 months exposure 8 months exposure P1 0 0 P2 0 0 P3 0 5-10 P4 0 5 P5 0 0 P6 0 0 P7 0 5-10 P8 0 5 P9 0 0 P10 0 0 P11 0 5 P12 0 0 P13 0 0 VP1 0 0 VP2 40 100 0 no fouling 100 complete fouling

Claims: Patent claims 1. Polymer for antifouling coatings characterized in that it comprises units corresponding to the following monomers A) 5 to 100 mol-% of one or more compounds of the general formula I in which: 10 X = H. CI, Br or F R = Ph(R 1 ) m or benzyl R 1 = each independently selected from halogen, -C(O)H, -COOR 2 , -CH 2 -COOR 2 , -O-R 2 , -O-CO-R 2 , -NH-CO-R 2 , -NH-COOR 2 , -SO 3 H, i5 and optionally substituted thiadiazolyl and thiazolylsulfamyl groups Ph = phenyl m = 1 - 3 R 2 = H or optionally halogen substituted alkyl, aryl, cycloalkyl, aralkyl groups with 1 - 10 C atoms 20 and B) 0 to 95 mol-% of one or more other ethylenically unsaturated compounds. 25 Polymer in accordance with claim 1 , characterized in that it comprises units corresponding to 30 to 60 mol-% of component A) and 40 to 70 mol-% of component B). 3. Polymer in accordance with claim 2, characterized in that it comprises units corresponding to 40 to 55 mol-% of component A) and 45 to 60 mol-% of component B). 4. Polymer in accordance with any of claims 1 , 2 and 3 characterized in that it as component A comprises units corresponding to compounds of the general formula I I in which: X = H or CI R = Ph(R 1 ) m R 1 = each independently selected from halogen, -COOR 2 , -O-R 2 , -O-CO-R 2 and optionally substituted thiazolylsulfamyl groups Ph = phenyl m = 1 - 3 R = H or alkyl groups with 1 - 10 C atoms 5. Polymer in accordance with any of claims 1 , 2 and 3 characterized in that it comprises units corresponding to monomers selected from: as component A): N-(4-chlorophenyl) maleimide, N-(2,4,6-trichlorophenyl) maleimide, N-(2,4,6-tribromophenyl) maleimide, N-(4-hydroxyphenyl) maleimide, N-(4-carboxyphenyl) maleimide, N-(4-acetoxyphenyl) maleimide, N-(4-ethyloxycarbonylphenyl) maleimide, N-(thiazolylsulfamyl) maleimide, N-(4-chlorophenyl)-2,3-dichloromaleimide, N-(4-ethyloxycarbonylphenyl)-2,3- dichloromaleimide and as component B): butyl acrylate, methyl methacrylate, butyl methacrylate, n-hexyl methacrylate, n-dodecyl methacrylate, 2-hydroxy ethyl methacrylate, methoxy ethyl acrylate, 3-methacryloyloxypropyl trimethoxy silane. 6. Process for the preparation of binders for antifouling coatings by homopolymerisation or copolymerisation of polymerisable monomers, characterized in that, as polymerisable monomers, a mixture of A) 5 to 100 mol-% of one or more compounds of the general formula I I in which: X = H, CI, Br or F R = Ph(R ) m or benzyl R 1 = each independently selected from halogen, -C(O)H, -COOR 2 , -CH 2 -COOR 2 , -O-R 2 , -O-CO-R 2 , -NH-CO-R 2 , -NH-COOR 2 , -SO 3 H, and optionally substituted thiadiazolyl and thiazolylsulfamyl groups Ph = phenyl m = 1 - 3 R 2 = H or optionally halogen substituted alkyl, aryl, cycloalkyl, aralkyl groups with 1 - 10 C atoms and B) 0 to 95 mol-% of one or more other ethylenically unsaturated compound are polymerised in the presence of radical-forming initiators and inert solvents 7. Antifouling paints containing polymers in conformity with any of claims 1-5, together, when appropriate, with auxiliary substances and additives such as pigments, anti-settling agents, solvents, biocides and stabilizers. 8. The use of monomers of the general formula I in which: X = H, CI, Br or F R = Ph(R 1 ) m or benzyl R 1 = each independently selected from halogen, -C(O)H, -COOR 2 , -CH 2 -COOR 2 , -O-R 2 , -O-CO-R 2 , -NH-CO-R 2 , -NH-COOR 2 , -SO 3 H, and optionally substituted thiadiazolyl and thiazolylsulfamyl groups Ph = phenyl m = 1 - 3 R 2 = H or optionally halogen substituted alkyl, aryl, cycloalkyl, aralkyl groups with 1 - 10 C atoms for the preparation of polymers for antifouling coatings.

Inventors: DAHLING MARIT, NILSEN MARIANNE TERLAND, UNDRUM THORALV, DAHLING, MARIT, NILSEN, MARIANNE, TERLAND, UNDRUM, THORALV
Applicants: DAHLING MARIT, JOTUN AS, NILSEN MARIANNE TERLAND, UNDRUM THORALV, DAHLING, MARIT, JOTUN A/S, NILSEN, MARIANNE, TERLAND, UNDRUM, THORALV
Application year: 1996
Main classification: C09D5
IPC codes: C08F22, C09D5