Sheet blow molding and molding method

Abstract: An integral lightweight laminated panel molding comprising a core (8) inside thermoplastic plastic sheet (9) as a surface material and a method of blow molding the same with which there is no substantial exposure of the core of the molding and it is possible to adhere the surface material and the core together securely without using an adhesive by making parts of the core become embedded in parts of the surface material during molding.

Description: This invention relates to a method of manufacturing a lightweight laminated panel used as a building material for floors, walls and ceilings and the like or as a material for walls or housings of vehicles, aircraft, ships, refrigerators and office equipment and so on, by sheet blow molding with a core. Because lightweight laminated panels have good wall surface load resistance and are insulating, soundproofing and vibration-absorbing, lightweight laminated panels of various materials and structures have been put on the market. These include many laminated panels having boards with honeycomb-like structures, foam boards, plaster boards and the like as cores and having thermoplastic plastic films, sheets or plates (hereinafter called thermoplastic plastic sheets) as surface materials. Also, laminated panels made by molding thermoplastic plastic sheets into a container member and a cover member by vacuum molding or thermal molding, putting a core inside the container member and then fitting the cover member and sealing the container member and the cover member together with an adhesive have also been known. Conventional sheet blow moldings and molding methods, on the other hand, because they have generally been for containers, have been completely hollow structure formation technology. In conventional lightweight laminated panels having thermoplastic plastic sheets as surface materials, because they have the construction described above, the core is exposed at the side of the panel, and because they consequently lack strength and invasion of water and the like also tends to occur, functional deterioration of the core has readily occurred. Also, particularly when a honeycomb-like core is used, when adhering the core and the surface materials together it is difficult to secure a sufficient area of adhesion and it has always been difficult to avoid problems of peeling, and to obtain a sufficient adherence large quantities of adhesive have been necessary. In the case of lightweight laminated panels made by box formation using vacuum molding or thermal molding, on the other hand, there have been numerous problems of process and raw material complexity, such as that a container member and a cover member have been made separately and to adhere the two together a heat-sealing step or an adhering step using an adhesive has been necessary, of difficulty of securing adherence, and so on. Another method for manufacturing laminated sandwich panels of the type of the preamble of claim 1 is known from AN:94-313267 and JP-A-6,238,783, where a honeycomb core is suspended in a parison of a blow molder. Accordingly, the object of the present invention is to provide an integral molding of a lightweight laminated panel having thermoplastic plastic sheet as a surface material wherein molding the same does not necessitate a separate adhering step for adhering the surface material to a core and with which furthermore it is possible to amply secure adhesion of the surface material if necessary and there is no substantial exposure of the core. In accordance with the present invention this object is solved by a method comprising the features of claim 1. Improved embodiments of the invention are subject matter to the dependent claim. As a result of accumulating assiduous research in order to achieve this object and other objects, the present inventors have solved the above-mentioned problem by succeeding in realizing a novel technological idea based on sheet blow molding technology (also called double sheet molding or twin composite molding), which has hitherto chiefly been used for the formation of ordinary, simple hollow structures. A panel-shaped body with a honeycomb-like structure, with which strength can be secured even in a light and thin molding, is preferable as the core; a first aspect of the invention provides a method of molding a sheet blow molding containing a core wherein a core (8) is disposed between two thermoplastic plastic sheets (1, 1') facing each other with a predetermined gap therebetween, the edges of the sheets are clamped and thereby made to form a closed space S and then the thermoplastic plastic sheets (1, 1') are clamped between a pair of molds 6, 6', blow-molded and pinched off; and a second aspect of the invention provides a preferable thickness of a core used in this molding method. As shown in Fig. 1, a sheet blow molding of this invention comprises a core 8 inserted inside a blow molded container member formed by a surface material 9 integrally molded with a parting line. The thermoplastic plastic sheet (also just called a sheet) used for the surface material 9 can be suitably selected according to the application for which the molding is to be used, and thermoplastic plastic sheets made of vinyl chloride resins such as copolymers having polyvinyl chloride and vinyl chloride as main components, acrylic resins such as polymethyl methacrylate and copolymers thereof, olefin resins such as polyethylene and ethylene copolymers or polypropylene, polyester resins such as polyethylene terephthalate and polybutylene terephthalate, thermoplastic resins such as polycarbonate resin and polyamide resin, or polymer blends and grafts with these as main components or various other thermoplastic compositions can be used. A sheet thickness suitable for this invention is 1 to 10mm, and the materials and colors of the two thermoplastic plastic sheets 1, 1' may be different. As the core, any plate-shaped body of a lightweight structure and having heat-resistance and a structure which does not obstruct blow molding can be used. Materials which can be used for the core include organic materials such as plastic, paper and wood, inorganic materials such as metal, glass, asbestos, ceramics and plaster and composites of these. Shapes and structures which can be used for the core include panels of honeycomb-like structure having multiple open passages (which may be of any shape such as square, hexagonal or circular) extending in the thickness direction of the panel, porous bodies, columnar bodies, frame-shaped bodies, corrugated bodies and so on. In particular, a honeycomb-like panel such as that shown in Fig. 2 is preferable for increasing the resistance to surface loads and the insulating and soundproofing performance of a molding of the invention. Also, preferably, to ensure a free flow of air during blow molding, irregularities or wave forms are provided in the upper and lower surfaces of the panel-shaped core to form a continuous space between the sheet and the core or the core is disposed divided into a plurality of pieces. With a panel of honeycomb-like structure having open passages in its thickness direction, the blow-moldability can be further improved by providing ventilation holes in the walls of the passages. The size (in the example shown in Fig. 2, the height X', the width Y' and the thickness T') of the core is less than the size of the molding (in the example shown in Fig. 1, the height X, the width Y and the thickness T) and can be suitably set in a range such that its blow-moldability is not impaired according to the application in which the molding is to be used. Fig. 1 is a partially cutaway perspective view of an example of a sheet blow molding according to the invention (wherein the core is a panel of honeycomb-like structure); Fig. 2 is a perspective view of a panel of honeycomb-like structure) as an example of a core; Fig. 3 is a sectional view of a blow molding apparatus illustrating commencement of heating in a molding method according to the invention; Fig. 4 is a sectional view of the same blow molding apparatus illustrating commencement of air blowing in a molding method according to the invention; Fig. 5 is a sectional view of the same blowing apparatus illustrating completion of air blowing in a molding method according to the invention; Fig. 6 is a sectional view on the line A-A' in Fig. 1; Fig. 7 is a plan view showing the positioning of the core 8 in a first preferred embodiment of the invention; Fig. 8 is a sectional view of the blow molding apparatus illustrating the commencement of air blowing in the first preferred embodiment of the invention; Fig. 9 is a plan view showing the positioning of the core 8 in a second preferred embodiment of the invention; and Fig. 10 is a sectional view of the blow molding apparatus illustrating the commencement of air blowing in the second preferred embodiment of the invention. A preferred mode of practicing a method of molding a sheet blow molding with a core according to the invention will now be described with reference to the accompanying drawings. First, as shown in Fig. 3, in a sheet blow molding apparatus, a core 8 is placed on a thermoplastic plastic sheet 1' and then the thermoplastic plastic sheet 1' and a thermoplastic plastic sheet 1 are held a predetermined distance apart by a spacer 2 and clamped by clampers 3, 3' and a closed space S is thereby formed. If necessary, part of the core can be provisionally fixed to the sheet 1' by being adhered thereto with an adhesive or with a hot melt adhesive such as wax or a low melting point resin-form substance or with a pressure sensitive adhesive. The sheets 1, 1' are then heated with movable far infrared heaters 5, 5'. Here, if necessary, an air nozzle 4 for pretensioning can be operated. Next, as shown in Fig. 4, when the sheets 1, 1' have softened to a suitable extent, the heaters 5, 5' are moved away and immediately after this an air nozzle 7 for blow molding is passed into the closed space S and air starts to be blown into the closed space S. Closing of molds 6, 6' is then carried out. By the steps described above, as shown in Fig. 5 the core 8 is insert-molded inside a container member formed by the surface material 9 molded against the inner surfaces of the molds 6, 6', the surface material 9 is pinched off by the molds 6, 6' and a blow molding M with a parting line 10 is formed. When the thickness of the blow-molded surface material 9 is written t and the thickness of the molding is written T, if as shown in Fig. 6 the thickness T' of the core is set so that T>T'>T-2t , parts of the core 8 become embedded in parts of the surface material 9 of the molding during molding and the core 8 is thereby fixed to the surface material 9 without any adhesive being required. Preferred embodiments of the invention will now be described. First Preferred Embodiment According to the preferred mode of practicing the invention described above, a panel-shaped blow molding with a core (X=800mm, Y=500mm, T=30mm) was manufactured under the following conditions: [1] As the sheets 1, 1', acrylic modified high-impact vinyl chloride plates of thickness 0.2mm were used. [2] The sheet surface temperature at the sheet surface to which the sheets were heated in the step illustrated in Fig. 3 was 180°C. [3] An X'=760mm, Y'=460mm, T'=27mm paper honeycomb of the structure shown in Fig. 2 was used as the core 8. [4] The core 8 was disposed on the sheet 1' as shown in Fig. 7. [5] The air nozzle 7 for blow molding was disposed at the end of the molding, as shown in Fig. 8, and the nozzle insertion position P was made the position shown in Fig. 7 and Fig. 8. [6] The mold clamping gauge pressure in the step illustrated in Fig. 8 (the same step as that of Fig. 4) was made 80kg/cm 2 and the pressure of the blown air was made 3kg/cm 2 . Second Preferred Embodiment Two X'=380mm, Y'=460mm, T'=27mm cores 8 were disposed on the sheet 1' as shown in Fig. 9, the air nozzle 7 for blow molding was disposed centrally as shown in Fig. 10 and the nozzle insertion position P was made the position shown in Fig. 9 and Fig. 10. Otherwise in exactly the same way as in the first preferred embodiment, a panel-shaped blow molding with a core the same size as that of the first preferred embodiment was manufactured. Some of the effects and benefits of the invention are as follows: 1. Because a sheet blow molding according to the invention comprises a lightweight core inside a practically integrally formed hollow container member its resistance to surface loads is good, incidents of gas and water invading do not readily occur and its insulating and soundproofing performance are excellent. 2. When a panel of honeycomb-like structure having multiple open passages in its thickness direction is used as the core, the core is well suited to blow molding and a light molding having particularly good insulating and soundproofing performance can be obtained. Also, in this case, if ventilation holes are provided in the walls forming the honeycomb-like structure, the suitability of the core for blow molding is increased further. 3. It is possible to use a conventional sheet blow molding method as the method of molding a blow molding with a core according to the invention, and furthermore it is possible to make a molding of high added value which cannot be obtained with conventional technology. 4. By setting the thickness of the core within a predetermined range it is possible to make parts of the core become embedded in parts of the surface material constituting the container body of the molding and thereby fix the core to the surface material without adhesive.

Claims: Method of manufacturing a lightweight laminated panel including a panel-shaped core and a thermoplastic cover, characterized in that , the core (8) is disposed between two thermoplastic sheets (1, 1') facing each other a predetermined distance apart, the edges of the sheets are clamped and made to form a closed space (S) and then the thermoplastic plastic sheets (1, 1') are clamped between a pair of molds (6, 6'), blow-molded and pinched off. Method according to claim 1, wherein the core (8) has a thicknes (T') such that it is embedded in part of a surface material (9) of the molding.

Inventors: NAITOU KAZUNORI, SEKI YUUKI, NAITOU, KAZUNORI, SEKI, YUUKI
Applicants: TSUTSUNAKA PLASTIC KOGYO, TSUTSUNAKA PLASTIC INDUSTRY CO., LTD.
Application year: 1996
Main classification: B29C49
IPC codes: B29C49, B32B3, B29L9, B29D24, B29L31