High-strength copper based alloy free from smutting during pretreatment for plating

Abstract: A high-strength Cu based alloy, consists essentially of: Ni: 0.5 to 2.0 %; Sn: 1.2 to 2.5 %; Si: 0.04 to 0.1 %; Zn: 0.1 to 1 %; Mg: 0.0001 to 0.02 %; Mn: 0.0001 to 0.1 %; P: 0.0001 to 0.02 %; and Cu and inevitable impurities: the balance, wherein the total content of Mg, Mn and P is 0.001 to 0.12 %. The Cu based alloy is suitable for use as a material of electrical and electronic parts, and free from smutting during pretreatment for plating thereof.

Description: BACKGROUND OF THE INVENTION Field of the Invention This invention relates to a copper based alloy having high strength, for use as a material of electrical and electronic parts, which is free from smutting during pretreatment for plating thereof. Prior Art For the manufacture of electrical and electronic parts, such as terminals, connectors, and lead frames of semiconductor devices, a copper (Cu) based alloy is known in the art as proposed in Japanese Laid-Open Patent Publication (Kokai) Ni. 1-272733 (hereinafter referred to as "the conventional Cu based alloy"), which has a chemical composition consisting essentially, by weight % (hereinafter referred to as "%"), of 1.24 % nickel (Ni), 1.80 % tin (Sn), 0.052 % silicon (Si), 0.55 % zinc (Zn), 0.0052 % calcium (Ca), 0.0245 % magnesium (Mg), 0.0058% lead (Pb), and the balance of copper and inevitable impurities. The percentage used throughout the present specification is percent by weight. The conventional Cu based alloy is generally rolled into a sheet, and the sheet is then subjected to working, such as blanking and bending, to be formed into electrical or electronic parts with a predetermined shape, followed by plating the thus formed electrical or electronic parts, to thereby obtain final products. To plate the thus formed electrical or electronic parts, e.g. to plate the outer surfaces of leads for a semiconductor device with a solder, the leads for the semiconductor device are subjected to a pretreatment consisting of steps of alkaline electrolytic cleaning, water washing, etching, water washing, smut removing, and water washing. Then, the thus pretreated leads are subjected to plating consisting of steps of pre-dipping, solder plating, water washing, neutralization, water washing, water bathing, blowing, and drying. Electrical and electronic parts are always demanded to be manufactured at lower costs, and to meet the demand, it is required that electrical and electronic parts should be manufactured by more efficient steps. However, electrical and electronic parts formed from the conventional Cu based alloy undergo smutting during the above-mentioned pretreatment for plating, particularly during the etching step. To remove the smut, a great deal of time period is required, which unfavorably impedes an improvement in the productivity. SUMMARY OF THE INVENTION It is the object of the invention to provide a high-strength Cu based alloy for use as a material of electrical and electronic parts, which is free from smutting during the pretreatment for plating. To attain the above object, the present invention provides a Cu based alloy consisting, by weight %, of 0.5 to 2.0 % Ni, 1.2 to 2.5 % Sn, 0.04 to 0.1 % Si, 0.1 to 1 % Zn, 0.0001 to 0.02 % Mg, 0.0001 to 0.1 % Mn, 0.0001 to 0.02 % P, and the balance of Cu and inevitable impurities, wherein the total content of Mg, Mn and P is 0.001 to 0.12 %. The above and other objects, features and advantages of the invention will be more apparent from the following detailed description. The features described can be used individually or collectively in arbitrary combination without departing from the scope of the invention. DETAILED DESCRIPTION From a viewpoint that electrical and electronic parts formed by a Cu based alloy which is free from smutting during the etching step can curtail a time period required for removing smut during the pretreatment for plating to thereby greatly improve the productivity, the present inventors have made studies in order to obtain a Cu based alloy having high strength, which is free from smutting during the etching step, and have reached the following finding: If a Cu based alloy has a chemical composition consisting, by weight %, of 0.5 to 2.0 % Ni, 1.2 to 2.5 % Sn, 0.04 to 0.1 % Si, 0.1 to 1 % Zn, 0.0001 to 0.02 % Mg, 0.0001 to 0.1 % Mn, 0.0001 to 0.02 % P, and the balance of Cu and inevitable impurities, wherein the total content of Mg, Mn and P is 0.001 to 0.12 %, the Cu based alloy is not only as excellent as the conventional Cu based alloy in mechanical properties, such as tensile strength, elongation, and bendability, solder-heat exfoliation resistance, and electric conductivity, but also free from smutting during the pretreatment for plating. As a result, if this Cu based alloy is used for manufacturing electrical and electronic parts such as lead frames, a working time period required for the pretreatment for plating can be drastically reduced compared with the time period required for manufacturing lead frames from the conventional Cu based alloy, leading to increased productivity thereof. The present invention is based upon the above finding. The contents of the component elements of the Cu based alloy according to the invention have been limited as stated above, for the following reasons: (1) Ni The Ni component acts to improve the strength and bendability of the Cu based alloy. However, if the Ni content is less than 0.5 %, the above action cannot be performed to a desired extent, whereas if it exceeds 2 %, the electric conductivity of the alloy is undesirably degraded. Therefore, the Ni content has been limited to the range of 0.5 to 2 %. Preferably, the Ni content should be limited to a range of 0.8 to 1.8 %. (2) Sn The Sn component acts, in cooperation with the Ni component, to further improve the strength and bendability of the Cu based alloy. However, if the Sn content is less than 1.2 %, the above action cannot be performed to a desired extent, whereas if it exceeds 2.5 %, the hot workability of the alloy is undesirably degraded. Therefore, the Sn content has been limited to the range of 1.2 to 2.5 %, and preferably the Sn content should be limited to a range of 1.4 to 2.2 %. (3) Si The Si component acts to deoxidize the Cu based alloy during melting for casting, as well as to form a nickel silicide in cooperation with the Ni component to improve the thermal resistance of the Cu based alloy. However, if the Si content is less than 0.04 %, the above actions cannot be performed to a desired extent, whereas if it exceeds 0.1 %, the amount of smut undesirably increases during etching in the pretreatment for plating. Therefore, the Si content has been limited to the range of 0.04 to 0.1 %, and preferably the Si content should be limited to a range of 0.05 to 0.09 %. (4) Zn The Zn component acts to further improve the solder-heat exfoliation resistance. However, if the Zn content is less than 0.1 %, the above action cannot be performed to a desired extent, whereas if the Zn content exceeds 1 %, the solderability of the alloy can be spoiled. Therefore, the Zn content has been limited to the range of 0.1 to 1 %. Preferably, the Zn content should be limited to a range of 0.2 to 0.8 %. (5) Mg, Mn and P These Mg, Mn and P components act to desulfurize the alloy as well as to fix free sulfur during melting for casting, to thereby improve the hot workability of the alloy or perform deoxidation of the same. However, if the Mg, Mn and P contents are each less than 0.0001, and at the same time the total content thereof is less than 0.001 %, the above action cannot be performed to a desired extent. On the other hand, if the Mg, Mn and P contents exceed 0.02 %, 0.1 % and 0.02 %, respectively, and at the same time the total content thereof exceeds 0.12 %, a further improvement in the hot workability attributed to the desulfurization and the fixing of free sulfur cannot be achieved or the effect of the deoxidation is saturated. Therefore, the Mg, Mn and P contents are limited to the ranges of 0.0001 to 0.02 %, 0.0001 to 0.1 %, and 0.0001 to 0.02 %, respectively, and at the same time the total content of the Mg, Mn and P components to 0.001 to 0.12 %. Preferably, the Mg, Mn and P contents should be limited to a range of 0.0003 to 0.015 %, 0.0005 to 0.08 %, and 0.0005 to 0.018 %, respectively, and at the same time the total content of the Mg, Mn and P components to 0.004 to 0.11 %. To produce the high-strength Cu based alloy according to the present invention, starting materials are charged into a melting furnace in such proportions that the resulting Cu based alloy has the predetermined chemical composition as described above, and they are melted in the atmospheric air with the surface of the molten alloy covered with charcoal. Next, an example of the Cu based alloy according to the invention will be described. Example The following embodiment is exemplary and does not represent an exhaustive enumeration of inventive configurations. Electrolytic copper was melted in a medium-frequency channel coreless smelting furnace in the atmospheric air with the surface of the molten copper covered with charcoal. The alloy component elements were added to the molten copper individually or in the form of a mother alloy, to prepare Cu based alloys having chemical compositions as shown in Tables 1 and 2. The thus prepared Cu based molten alloys were subjected to semi-continuous casting to produce ingots each having a size of 160 mm in thickness, 600 mm in width, and 4400 mm in length. The ingots were hot-rolled at a temperature of 850 °C into hot-rolled plates each having a thickness of 11 mm, and the plates were immediately water-cooled, followed by scalping for removing scales therefrom. Then, the plates were repeatedly subjected to a sequence of steps of cold rolling, annealing and pickling to obtain cold-rolled sheets each having a thickness of 0.375 mm. Further, the sheets were annealed in a continuous annealing furnace at a temperature of 750 °C, and then cold-rolled to obtain cold-rolled sheets each having a thickness of 0.15 mm, followed by final annealing of the cold-rolled sheets in the continuous annealing furnace at a temperature of 500 °C for 20 sec, to relieve strain, to thereby produce cold-rolled sheets of Cu based alloys Nos. 1 to 15 according to the present invention and a conventional Cu based alloy Ni 1. The cold-rolled sheets of the Cu based alloys Nos. 1 to 15 according to the present invention and the conventional Cu based alloy Ni. 1, which each have a thickness 0.15 mm, were cut into specimens each having a size of 35 mm in width and 45 mm in length. The specimens were subjected to electrolytic decreasing in an aqueous solution containing: NaOH 60 g/liter, and 2Na 2 O · SiO 2 40 g/liter, under the following conditions: Bath temperature 43 °C, Bath voltage 5 V, and Energization time 120 sec. The specimens were then washed with water, and subjected to a pretreatment for plating, i.e. etching, water-washing and drying. The etching was conducted in an aqueous solution containing: H 2 O 2 60 g/liter, and H 3 PO 4 100 ml/liter, under the following conditions: Bath temperature 35 °C, and Soaking time 60 sec. The surfaces of the specimens thus pretreated were examined for the presence of smut. Results of the examination are shown in Tables 1 and 2. As is clear from the results shown in Tables 1 and 2, smut was perceived on the surface of the conventional Cu based alloy specimen 1, but no smut was perceived on the surface of any of the Cu based alloy specimens 1 to 15 according to the present invention. Therefore, in manufacturing electrical and electronic parts such as lead frames of semiconductor devices formed of the Cu based alloy sheets according to the present invention, the working time required for the pretreatment steps for plating can be drastically curtailed and hence the productivity can be greatly improved to thereby reduce the manufacturing cost, which brings about industrially useful effects.

Claims: A Cu based alloy having high strength, which is free from smutting during pretreatment for plating thereof, consisting, by weight %, of: Ni: 0.5 to 2.0 %; Sn: 1.2 to 2.5 %; Si: 0.04 to 0.1 %; Zn: 0.1 to 1 %; Mg: 0.0001 to 0.02; Mn: 0.0001 to 0.1 %; P: 0.0001 to 0.02 %; and Cu and inevitable impurities: the balance, wherein the total content of Mg, Mn and P is 0.001 to 0.12 %. The Cu based alloy having high strength, as claimed in claim 1, consisting, by weight %, of: Ni: 0.8 to 1.8 %; Sn: 1.4 to 2.2 %; Si: 0.05 to 0.09 %; Zn: 0.2 to 0.8 %; Mg: 0.0003 to 0.015 %; Mn: 0.0005 to 0.08 %; P: 0.0005 to 0.018 %; and Cu and inevitable impurities: the balance, wherein the total content of Mg, Mn and P is 0.004 to 0.11 %.

Inventors: CHIBA SHUNICHI, FUTATSUKA RENSEI, KUMAGAI JUNICHI, CHIBA, SHUNICHI, FUTATSUKA, RENSEI, KUMAGAI, JUNICHI, Chiba, Shunichi, Mitsubishi Shindoh Co., Ltd., Futatsuka, Rensei Mitsubishi Shindoh Co., Ltd., Kumagai, Junichi, Mitsubishi Shindoh Co., Ltd.
Applicants: MITSUBISHI SHINDO KK, MITSUBISHI SHINDOH CO., LTD.
Application year: 1996
Main classification: C22C9
IPC codes: C22C9, H01L23