Lightly crosslinked poly(N-alkylmethylsiloxanes) and methods of producing same

Abstract: The crosslinking and simultaneous alkylation of poly(hydridomethylsiloxanes) to form crosslinked siloxanes having n-alkylmethyl groups is disclosed. Without changing the chain length of the poly(hydridomethylsiloxane) starting material, a family of lightly crosslinked siloxanes having n-alkylmethyl groups, with a range of viscosities, are produced using one or more alpha-olefins along with a small amount of an unconjugated alpha, omega-diene added as a crosslinker. Our poly(hydridomethylsiloxanes) are made from highly pure silanol-free hexamethyldisiloxane and highly pure mixtures of silanol-free tetramethylcyclotetrasiloxane (D H 4) and pentamethylcyclopentasiloxane D H 5 containing no more than 100 parts per million (ppm) water, with anhydrous trifluoromethane sulfonic acid (triflic acid, CF 3 SO 3 H), at room temperature, to provide linear poly(hydridomethylsiloxanes) having degrees of polymerization of up to 250.

Description: This invention is directed to methods for crosslinking linear polysiloxanes and the compositions resulting therefrom. The present invention relates to the crosslinking and simultaneous alkylation of poly(hydridomethylsiloxanes) to form crosslinked siloxanes having n-alkylmethyl groups. Without changing the chain length of the poly(hydridomethyl-siloxane) starting material, a family of lightly crosslinked siloxanes having n-alkylmethyl groups are produced herein using one or more alpha-olefins along with a small amount of an unconjugated alpha, omega-diene added as a crosslinker. The lightly crosslinked siloxanes having n-alkylmethyl groups have a wide range of viscosities. Our poly(hydrido-methylsiloxanes) are made from highly pure silanol-free hexamethyldisiloxane and highly pure mixtures of silanol-free tetramethylcyclotetrasiloxane (D H 4) and pentamethylcyclopentasiloxane (D H 5) containing no more than 100 parts per million (ppm) water, with anhydrous trifluoromethane sulfonic acid (triflic acid, CF 3 SO 3 H), at room temperature, to provide linear poly(hydridomethylsiloxanes) (MD H x M) where x is from 8 to 250. These crude polymers are neutralized by solid NaHCO 3 and then filtered to remove Na+ triflate to provide neutral poly(hydridomethylsiloxanes). To these poly(hydridomethylsiloxanes) are added a reaction mixture consisting of a catalyst, alpha-olefin and a crosslinker which is an unconjugated alpha, omega-diene. The resulting lightly crosslinked siloxanes having n-alkylmethyl groups are waxes or fluids at room temperatures and are useful in a variety of applications where controlling viscosity of the polymer is critical. The compositions of the present inventions are especially useful as an additive to the toner used in photocopiers. The present invention exploits these ultra pure polymers to make a dramatic advance in the art. Heretofore, the available siloxanes having n-alkylmethyl groups were not predominately linear like those provided herein. Rather, the prior art utilized polymers which contained significant branch sites. When crosslinker was added to those branched polymers, the resulting compositions had extremely high viscosities, sometimes forming useless gels. Moreover, adding even incremental amounts of crosslinker to otherwise useful compositions would result in excessively high viscosity materials; this result creates major production difficulties where minor variations in the amount of crosslinker could result in lots varying widely in viscosity or otherwise rendered unusable. The non-branched starting materials of the present invention eliminate this problem. Furthermore, the previously available siloxanes were typically contaminated with highly reactive residual SiH, thereby resulting in unstable compositions whose viscosities increased over time. The crosslinked siloxanes of the present invention do not include detectable amounts of residual SiH and are therefore stable over time. Our invention, therefore, is in sharp contrast to the gel containing crosslinked oily materials taught by US-A 2,491,843 or the crosslinked high polymers bearing SiOH end groups, described in the European Polymer Journal , Vol. 29, No. 1, Pages 15-22, (1993). Furthermore, our alkylated products are prepared from highly pure, essentially anhydrous, silanol-free starting materials and contain low or no residual silicon hydride functionality. It is an object of our invention to provide a method of making crosslinked siloxanes having n-alkylmethyl groups from ultra pure poly(hydridomethylsiloxanes) having substantially reduced branch sites which are mixed into a reaction mixture consisting of a platinum catalyst, an alpha-olefin and a crosslinker that is an unconjugated alpha, omega-diene. It is a further object of the invention to introduce a method of controlling the viscosity of crosslinked siloxanes having n-alkylmethyl groups. Previously, it was known that methylhydrogendichlorosilane could be hydrolyzed and condensed to obtain linear poly(hydridomethylsiloxanes) retaining a high proportion of reactive hydrogen, but typically they contain 1% or more of branch sites. The reactions are often difficult to control and the results are erratic (i) sometimes producing useless gels or hard brittle solids instead of fluids and (ii) sometimes providing hydroxyl substitution on silicon which leads to gelation. This limits the usefulness of poly(hydridomethylsiloxanes) as starting materials for polymer synthesis. When impure poly(hydridomethylsiloxane) materials are added to the reaction mixture of catalyst, one or more olefins and a crosslinker as described herein, the resulting compositions may be undesirable gels rather than the waxes and fluids of the present invention. Further, these materials do not exhibit stable viscosities over extended time periods, because relatively high amounts of residual silicon hydride functionality allow further reactions which alter the viscosity. Furthermore, adding incremental amounts of crosslinker to these materials will result in drastic viscosity changes. The above objects are solved by providing a method as claimed in claim 1. Preferred embodiments are described in claims 2 to 6. Thereby the disadvantages mentioned above are surprisingly overcome by utilizing linear poly(hydridomethylsiloxanes) derived from highly pure, essentially anhydrous, silanol-free hexamethyldisiloxane and highly pure, essentially anhydrous,' silanol-free hydridomethyl cyclosiloxanes (D H 4) and (D H 5), as starting materials. Our high molecular weight trimethylsiloxy-endcapped polypoly(hydridomethylsiloxanes) are prepared via an anhydrous triflic acid catalyzed, mild room temperature polymerization, of highly pure, essentially anhydrous, silanol-free hexamethyldisiloxane; highly pure, essentially anhydrous, silanol-free tetramethylcyclotetrasiloxane and/or highly pure, essentially anhydrous, silanol-free pentamethylcyclopentasiloxane. By "silanol-free" is meant that the siloxane starting materials contain no residual ≡SiOH, within the limits of detection by Silicon-29 Nuclear Magnetic Resonance ( 29 Si NMR) and Fourier Transform Infrared Spectroscopy (FTIR), which is one part per million or less. The resulting poly(hydridomethylsiloxanes) are fluids containing less than 0.2% branch sites by 29 Si NMR, that could eventuate in the formation of an undesirable gel. A branch site frequency of 0.2% means that 1 out of 500 silicon atoms contains a branch site. The degree of polymerization of resulting polymer is controlled by the amount of cyclosiloxanes present in the reaction mixture and will result in polymers having siloxane backbones of from 8 to 250 silicone molecules, although degrees of polymerization of from 8 to 100 are preferred and 8 to 60 are most preferred. The term "substantially pure poly(hydridomethylsiloxanes)" as used herein means poly(hydridomethylsiloxanes) which are silanol-free and which have a branch site frequency of 0.2% or less. Our reaction conditions are mild so that branch sites are not formed during polymerization. Thus, the preferred temperature range is 20-30°C (68-86°F), although if desired, temperatures up to 100°C can be employed, consistent with the desire to avoid the formation of branch sites. The methods of preparing these poly(hydridomethylsiloxanes) are more fully described in US-A 5,516,870. To prepare the polymers of the present invention, these high purity poly(hydridomethylsiloxanes) are added to a reaction mixture consisting of alpha-olefin, crosslinker and catalyst. The mixture is stirred until an exotherm occurs, typically at between 60°-120°C. The mixture is then stirred continuously at the exotherm temperature until the reaction is complete, at which point an FTIR analysis will give 0 ppm SiH. The alpha-olefins, CH 2 =CR'R" (where R'=H or methyl and R" is alkyl group having from 2-30+ carbon atoms), used in the reaction mixture include alkenes with 2-30+ carbon atoms, preferably 6-30 carbon atoms and, most preferably, 6-18 carbon atoms. Particular care should be taken to insure that the alpha-olefin(s) is anhydrous. Some suitable alpha-olefins are ethylene, propene, 1-butene, isobutylene (2-methylpropene), 1-pentene (C5), 2-methyl-1-butene, 3-methyl-1-butene, 1-hexene, 2-methyl-1-pentene, 3-methyl-1-pentene, 4-methyl-1-pentene, 1-heptene, 2-methyl-1-hexene, 1-octene, 2-methyl-1-heptene, 1-nonene, 1-decene (C10), 1-undecene, 1-dodecene, 1-tridecene, 1-tetradecene, 1-pentadecene (C15), 1-hexadecene, 1-octadecene, 1-nonadecene, 1-eicosene (C20) and those alpha-olefin fractions containing varying percentages of C 22 -C 30+ alpha-olefins sold under the trademarks GULFTENE® 24-28 and GULFTENE® 30+, by Chevron Chemical Company, Houston, Texas. It will be readily understood by those skilled in the art that different mixtures of the foregoing alpha-olefins will also produce acceptable compositions of this invention. The crosslinker of the present invention is an unconjugated alpha, omega-diene. These crosslinkers are characterized by the fact that they have two functional groups that will react with silicone hydride and are hydrolytically and/or oxidatively stable. The preferred crosslinker is 1,5 hexadiene, although 1,7-octadiene, 1,9-decadiene and 1,3-tetradecadiene can also be used in the practice of the present invention. The advantage of using an unconjugated alpha, omega-diene for this modification is that the chemical reactivity of the olefinic groups of the diene is similar to the chemical reactivity of the olefinic groups of the alpha-olefin. This similarity permits hydrosilylation of the alpha-olefin and the alpha, omega-diene to proceed simultaneously (same time and same rate) thereby leading to both better process and product reproducability. The ratio of alpha, omega-diene to alpha-olefin(s) which can be employed in this process is dependent upon the chain length of the poly(hydridomethylsiloxane) material. For short polymers (e.g., having a degree of polymerization of less than 20) the ratio may range up to 2/100. The amount of alpha, omega-diene used is generally quite small and is 0.5-3% relative to the alpha-olefin. Excessive amounts of alpha, omega-diene will cause gelation of the polymeric product; typical preparations of our claimed compositions include 0.3 to 0.6% by weight of crosslinker per 100 parts by weight of poly(hydridomethylsiloxane) and olefin(s). Equivalent amounts of ≡Si-H containing reactants and unsaturated alpha-olefin reactants should be employed in our process and one ethylenic linkage is the theoretical equivalent of one silicon bonded hydrogen atom. It may be necessary, however, to use an excess of alpha-olefin to totally consume ≡SiH in the siloxane product. The maximum amount of platinum catalyst employed is determined by economical considerations and the minimum amount by the type and purity of reactants employed. Very low concentrations of platinum catalyst such as 1x10 -6 moles of catalyst per equivalent of the alpha-olefin compound, may be used when the reactants are extremely pure. However, it is possible to use 1x10 -5 moles of catalyst per equivalent weight of alpha-olefin compound and even 1x10 -4 moles of catalyst, per equivalent weight of alpha-olefin(s). "Moles" of platinum catalyst are measured in terms of one mole providing one unit atom (e.g. one gram atom) of platinum. An "equivalent weight" of alpha-olefin is the amount of reactant furnishing one unit weight of ethylenic unsaturation (i.e. equivalent to one unit weight of ≡Si-H), regardless of what other reactive, or potentially reactive, substitutents may be present. Thus, an equivalent weight of ethylene is its molecular weight. The preferred hydrosilylation catalyst is a neutral, soluble zero valent platinum catalyst or platinum supported on active carbon having a particle diameter of 1-2 mm. The amount of platinum supported on the active carbon can vary from 0.1-5% by weight, based on the weight of active carbon. Care should be taken to insure that the platinum on carbon catalyst is dried so that it is anhydrous. The reaction temperature can vary and optimum temperatures depend upon the concentration of platinum catalyst and the nature of the reactants. The reaction is initiated at a temperature below room temperature (20°C to -10°C) and is exothermic once begun. The temperature should be one at which all reactants are in the liquid or gaseous state. The maximum temperature is determined by the volatility and stability of the reactants. Ordinarily, it is best to keep the reaction temperature below 130°-150°C. Best results, with most reactants, are obtained by initiating the reaction at 50° to 180°C and maintaining the reaction within reasonable limits of this range. The exothermic nature of the reaction may push the temperature up to 150°C for a short time, however. The optimum reaction time is variable, dependent upon the reactants, reaction temperature and platinum catalyst form and concentration. Ordinarily, there is no benefit in extending the contact time of the reactants beyond 16 or 17 hours, but likewise there is usually no harm, unless an extremely elevated temperature is employed. With many reactants, a practical quantitative yield of product is obtained in 120 minutes or less. The reaction can be carried out at atmospheric, sub-atmospheric or super-atmospheric pressure. Here again, the choice of conditions is largely a matter of logic, based upon the nature of the reactants and the equipment available. Non-volatile reactants are especially adaptable to being heated at atmospheric pressure, with or without a reflux arrangement. Reactants which are gaseous at ordinary temperatures, are preferably reacted at substantially constant volume under autogenous or induced pressure. The best results are obtained by maintaining all reactants in the liquid phase. In the following examples, viscosities were measured using a Brookfield™ Viscometer (Stoughton, Ma.). Parts of residual SiH were measured by 29 Si NMR and FTIR. The siloxane polymers used herein, except for those in the Comparative Examples, were substantially pure polymers made from highly pure silanol-free hexamethyldisiloxane and highly pure mixtures of silanol-free tetramethylcyclotetrasiloxane (D H 4) and pentamethylcyclopentasiloxane (D H 5) containing no more than 100 parts per million (ppm) water, with anhydrous trifluoromethane sulfonic acid (triflic acid, CF 3 SO 3 H), at room temperature, as described herein and in US-A 5,516,870. Reference is also made, for comparison purposes, to DC-1107, a commercially available product from the Dow Corning™ Corporation (Midland, Mi.) having the average formula (CH 3 ) 3 O(HCH 3 SiO) 60 (CH 3 ) 3 , [MD' 60 M]. DC-1107 is produced by cohydrolysis of HCH 3 SiCl 2 and (CH 3 ) 3 SiCl rather than the methods set forth herein. For purposes of the following examples, the term "platinum catalyst" refers to a complex of Pt(0) and (CH 2 =CH(CH 3 ) 2 Si) 2 O. Comparative Example I To a stirred homogeneous solution of 1-octadecene (482 g, 1.91 moles) and platinum catalyst (0.14 ml, 2.5 ppm Pt) were added DC-1107 (100 g, 0.027 mole) at a dropwise rate. The reaction exothermed to 90°C and was maintained at this temperature for 24 hours. At this point, the excess olefin was stripped off (pot temp. 180-200°C, 2 mm Hg [266.6 Pa]) to afford an uncrosslinked white wax (mp 46-48°C) with 164 ppm residual SiH as measured by FTIR and melt viscosities of 1275 mPa·s (cps) at 50°C and 160 mPa·s (cps) at 175°C. Comparative Example II To 20 g (0.053 mole) of DC-1107 were added 15 ml of a mixture of 1-octadecene (96.4 g, 0.383 mole) and 1,5-hexadiene (220 mg, 0.19 wt% of the total reagents) followed by stirring at room temperature. To this solution were added a platinum catalyst (0.026 ml, 2.5 ppm Pt) with the balance of the octadecene/hexadiene solution added dropwise at a slow rate. After a rapid exotherm to 140°C, the reaction was maintained at 120°C for 16 hours. The reaction mixture was stripped by distillation of excess olefin (200-260°C, 2 mm Hg [266.6 Pa]) to provide a white wax (melting point 39-41°C) with 0.5% residual olefin and 108 ppm residual SiH as measured by FTIR. The melt viscosity at 180°C was 800 mPa·s (cps). Comparative Example III To 20 g (0.0053 mole) of DC-1107 were added 15 ml of a mixture of 1-hexene (32 g, 0.383 mole) and 1,5-hexadiene (182 mg, 0.35 wt% of total reagents) followed by stirring at room temperature. To this solution were added a platinum catalyst (0.016 ml 2.5 ppm Pt) with the balance of the hexene/hexadiene solution added dropwise at a slow rate. After a rapid exotherm to 110°C, the reaction was maintained at 120°C for 18 hours. The reaction mixture was stripped by distillation of excess olefin (140-250°C, 2 mm Hg [266.6 Pa]) to provide a slightly yellow wax (melting point 27-29°C) with 120 ppm residual SiH. The melt viscosity at 25°C was 82,000 mPa·s (cps) and at 180°C was 22,000 mPa·s (cps). Using conventional methods, an increase in melt viscosity from 800 mPa·s (cps) (see Comparative Example II) to 22,000 mPa·s (cps) was observed by merely doubling the amount .of crosslinker. This represents an increase in viscosity of almost 27 times the original crosslinked material. Therefore, very small increments of crosslinker increase the viscosity drastically in the conventional method, making control of the viscosity difficult during production. Examples IV, V and VI use the ultra pure poly(hydrido methylsiloxanes) as starting materials and therefore do not show the dramatic viscosity increase when the amounts of crosslinker are increased. Example IV Preparation of Me 3 SiO(MeC 18 H 37 SiO) 60 SiMe 3 , [MD 18 60 M]. To a stirred homogeneous solution of 1-octadecene (24.16 g, 0.0065 mole) and platinum catalyst (2.4% Pt in toluene, 2.5 ppm, 0.02 ml) were added substantially pure Me 3 SiO(MeHSiO) 60 SiMe 3 (117 g, 0.46 mole) at a dropwise rate over 0.5 hours. The reaction exothermed to 80°C and was maintained at that temperature via external heating for 4 hours. FTIR analysis gave 0 ppm residual SiH. The olefin was then stripped (0.2 mm Hg [26.7 Pa], 180-220°C) from the mixture to afford a white wax melting at 41-44°C with a melt flow viscosity of 140 mPa·s (cps) when measured at 180°C. Example V Preparation of Me 3 SiO(MeC 18 H 37 SiO) 60 SiMe 3 , [MD 18 60 M] To a stirred homogeneous solution of 1-octadecene (3056 g, 12.5 moles), 1,5-hexadiene (0.55% by weight of total reagents, 7.62 g) and platinum catalyst (2.4% Pt in toluene, 2.5 ppm, 0.454 ml) were added substantially pure Me 3 SiO(MeHSiO) 60 SiMe 3 made from cyclics (654 g, 0.1739 mole) at a dropwise rate over 2 hours. The reaction exothermed to 80°C and was maintained at that temperature via external heating for 16 hours. FTIR analysis gave 0 ppm residual SiH. The olefin was then stripped (0.2 mm Hg [26.7 Pa], 180-220°C) from the mixture by distillation to afford a white crosslinked wax with a melt flow viscosity of 1000 mPa·s (cps) when measured at 180°C. Example VI Preparation of Me 3 SiO(MeC 18 H 37 SiO) 60 SiMe 3 , [MD 18 60 M] To a stirred homogeneous solution of 1-octadecene (117 g, 0.464 mole), 1,5-hexadiene (0.55 % by weight of total reagents, 790 mg) and platinum catalyst (2.4% Pt in toluene, 2.5 ppm, 5 mg) was added substantially pure Me 3 SiO(MeHSiO) 60 SiMe 3 made from cyclics (24.16 g, 0.0065 mole) at a dropwise rate over 0.5 hour. The reaction exothermed to 80°C. and was maintained at that temperature via external heating for 16 hours. FTIR analysis gave 0 ppm residual SiH. The olefin was then stripped (0.2 mm Hg [26.7 Pa], 180-220°C) from the mixture by distillation to afford a white crosslinked wax with a melt flow viscosity of 7500 mPa·s (cps) when measured at 180°C. As opposed to Comparative Examples II and III, the doubling of the amount of crosslinker in the polymers of the present invention results only in a viscosity increase of roughly 7.5 times over the original crosslinked compostion. This doubling of the viscosity still results in a polymer having usable properties. Example VII A number of crosslinked and uncrosslinked siloxanes having n-alkylmethyl groups having different degrees of polymerization and different alpha-olefins were prepared using ultra pure poly(hydridomethylsiloxanes). The viscosities of the crosslinked and uncrosslinked siloxanes having n-alkylmethyl groups are set forth in Table 1. Representative methods of making these polymers are also described. MD 6 9.6 M To (CH 3 ) 3 SiO(HCH 3 SiO) 9.6 Si(CH 3 ) 3 , [MD' 9.6 M], (50 g, 0.068 mole) were added a mixture of 1-hexene (66 g, 0.78 mole)/1,5-hexadiene (0.3 wt% of total reagents, 347 mg), platinum catalyst (2.5 ppm, 0.014 ml) very slowly over 20 minutes. The reaction exothermed to 80°C and after addition of olefin, was stirred at 80°C for 3 hours. At this point, FTIR analysis gave O ppm SiH. MD 18 9.6 M To MD' 9.6 M (50 g, 0.068 mole) were added a mixture of 1-octadecene (184 g, 0.73 mole)/1,5-hexadiene (0.3 wt%, 700 mg) and platinum catalyst (2.5 ppm, 0.029 ml) very slowly over 30 minutes. The reaction exothermed to 110°C and after addition of olefin, was stirred at 110°C for 3 hours. At this point, FTIR analysis gave O ppm SiH. 1,5 - Hexadiene Crosslinker Effect on Viscosity Siloxane Xlinker (wt%) Viscosity(cps) [mPa·s] MD 6 9.6 M --- 20 at 25°C MD 6 9.6 M 0.3 170 at 25°C MD 18 9.6 M --- 100 at 70°C MD 18 9.6 M 0.3 200 at 70°C MD 6 60 M --- 100 at 25°C MD 6 60 M 0.3 1000 at 180°C The data in Table 1 clearly show that crosslinking and simultaneous alkylation of poly(hydridomethylsiloxanes) in accordance with our invention results in higher viscosities than uncrosslinked compositions made by previous methods. Example VIII Preparation of Me 3 SiO(MeC 6 H 13 SiO) 60 SiMe 3 , [MD 18 60 M] To a stirred homogeneous solution of 1-hexene (32 g, 0.38 mole) and platinum catalyst (2.4% Pt in toluene, 2.5 ppm, 0.05 ml) were added substantially pure Me 3 SiO(MeHSiO) 60 SiMe 3 (20 g, 0.0053 mole) at a dropwise rate over 0.5 hours. The reaction exothermed to 90°C and was maintained at that temperature via external heating for 3 hours. FTIR analysis gave 0 ppm residual SiH. The product was a viscous fluid and had a viscosity of 80 mPa·s (cps) measured at 25°C. Example IX Preparation of Me 3 SiO(MeC 6 H 13 SiO) 200 SiMe 3 , [MD 6 200 M] To a stirred homogeneous solution of 1-hexene (15 g, 0.62 mole) and platinum catalyst (2.4% Pt in toluene, 2.5 ppm, 0.09 ml) were added substantially pure Me 3 SiO(MeHSiO) 200 SiMe 3 (20 g, 0.0053 mole) at a dropwise rate over 0.5 hours. The reaction exothermed to 100°C and was maintained at that temperature via external heating for 16 hours. FTIR analysis gave 50 ppm residual SiH. The product, a viscous fluid, had a viscosity of 80,000 mPa·s (cps) measured at 25°C. Example X Preparation of Crosslinked Me 3 SiO(MeC 6 H 13 SiO) 200 SiMe 3 , [MD 6 200 M] To a stirred homogeneous solution of 1-hexene (15 g, 0.62 mole), 1,5-hexadiene (260 mg, 0.1 wt% of reagents) and platinum catalyst (2.4% Pt in toluene, 2.5 ppm, 0.09 ml) were added substantially pure Me 3 SiO(MeHSiO) 200 SiMe 3 (20 g, 0.0053 mole) at a dropwise rate over 0.5 h. The reaction exothermed to 100°C and was maintained at that temperature via external heating for 16 h. FTIR analysis gave 50 ppm residual SiH. The product, a viscous fluid, had a viscosity of 170,000 mPa·s (cps) measured at 25°C. Example XI Preparation of Me 3 SiO(MeC 6 H 13 SiO) 30 (MeC 18 H 37 SiO) 30 SiMe 3 To a stirred homogeneous solution of 1-hexene (29.4 g, 0.35 mole), 1-octadecene (88 g, 0.35 mole) and platinum catalyst (2.4% Pt in toluene, 2.5 ppm, 16 mg) were added substantially pure Me 3 SiO(MeHSiO) 60 SiMe 3 (40 g, 0.0106 mole) at a dropwise rate over 3 hours. The reaction exothermed to 90°C and was maintained at that temperature via external heating for 16 hours. FTIR analysis gave 0 ppm residual SiH. The product was a viscous fluid and had a viscosity of 200 mPa·s (cps) measured at 25°C. Example XII Preparation of Crosslinked Me 3 SiO(MeC 6 H 13 SiO) 30 (MeC 18 H 37 SiO) 30 SiMe 3 To a stirred homogeneous solution of 1-hexene (29 g, 0.35 mole), 1-octadecene (88 g, 0.35 mole), 1,5-hexadiene (0.471 mg, 0.3 wt% of total reagents) and platinum catalyst (2.4% Pt in toluene, 2.5 ppm, 16 mg) were added substantially pure Me 3 SiO(MeHSiO) 60 SiMe 3 (20 g, 0.0053 mole) at a dropwise rate over 1 hour. The reaction exothermed to 90°C and was maintained at that temperature via external heating for 17 hour. FTIR analysis gave 0 ppm residual SiH. The product was a viscous fluid and had a viscosity of 800 mPa·s (cps) measured at 25°C.

Claims: A method of making crosslinked siloxanes having n-alkylmethyl groups comprising the steps of (i) forming a reaction mixture containing at least one alpha-olefin of the formula CH 2 =CR'R" where R' is H or methyl and R" is an alkyl group having 2 to 30 carbon atoms, or different mixtures of such alpha-olefins, a crosslinker and a catalyst, (ii) contacting the reaction mixture with at least one poly(hydridomethylsiloxane) which is silanol-free and which has a branch site frequency of 0.2% or less, and (iii) agitating the mixture and the catalyst at below 150°C to form a crosslinked siloxane having n-alkylmethyl groups. A method according to claim 1 in which the alpha-olefin is an alkene selected from the group consisting of ethylene, propene, 1-butene, isobutylene (2-methylpropene), 1-pentene (C5), 2-methyl-1-butene, 3-methyl-1-butene, 1-hexene, 2-methyl-1-pentene, 3-methyl-1-pentene, 4-methyl-1-pentene, 1-heptene, 2-methyl-1-hexene, 1-octene, 2-methyl-1-heptene, 1-nonene, 1-decene (C10), 1-undecene, 1-dodecene, 1-tridecene, 1-tetradecene, 1-pentadecene (C15), 1-hexadecene, 1-octadecene, 1-nonadecene, 1-eicosene (C20), alpha-olefin fractions containing C 22 -C 30+ alpha-olefins and mixtures thereof. A method according to claims 1 or 2 in which the crosslinker is 1,5-hexadiene. A method according to claim 1 in which said poly(hydridomethylsiloxane) is made by the method comprising (i) forming a reaction mixture containing a silanol-free hexaorganodisiloxane, one or more silanol-free methylhydrogen cyclosiloxanes and less than 100 parts per million water, (ii) contacting the reaction mixture with anhydrous trifluoromethane sulfonic acid catalyst, and (iii) agitating the mixture and the catalyst at below 100°C to form a poly(hydridomethylsiloxane). A method according to claim 4 in which said poly(hydridomethylsiloxane) has a degree of polymerization of 8 to 250. A crosslinked siloxane obtainable by the method of claim 1.

Inventors: BIGGS TIMOTHY NOLEN, LEGROW GARY EDWARD, BIGGS, TIMOTHY NOLEN, LEGROW, GARY EDWARD
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1996
Main classification: C08G77
IPC codes: C08G77