Hydroxyphenyl-containing polyorganosiloxanes

Abstract: The present invention relates to a hydroxyphenyl-functional polyorganosiloxane compound having the formula wherein R is independently a monovalent hydrocarbon group free of aliphatic unsaturation, A is a substituted or unsubstituted hydroxyphenyl group, B is selected from the group consisting of alkyleneoxyalkylene groups having at least two carbon atoms and alkylene groups having at least 2 carbon atoms, m is zero or 1, and n is an integer from 0 to 400. The hydroxyphenyl-functional polyorganosiloxanes of this invention are useful as surfactants or as additives for organic polymers.

Description: BACKGROUND OF THE INVENTION This invention relates to novel hydroxyphenyl-functional polyorganosiloxanes. More particularly, this invention relates to novel hydroxyphenyl-functional polyorganosiloxanes that have at least two hydroxyphenyl groups at one molecular chain terminal. Organofunctional polyorganosiloxanes have a variety of uses, namely as surfactants, fiber-treatment agents, and as additives for organic polymers. The chemical structures of organofunctional polyorganosiloxanes can be differentiated based on the type, number, and bonding position of the organofunctionality, and the nature of the particular application determines the selection of the suitable chemical structure. For example, with regard to an application as an additive for organic polymers and specifically in the case where the organofunctional polyorganosiloxane is used as a precursor to a copolymer in which the polyorganosiloxane is inserted into the organic polymer molecule, one must select an organofunctional group that is copolymerizable with the organic polymer and must very carefully control the group's frequency of occurrence and bonding position. Organofunctional polyorganosiloxanes, for example, can have organofunctionality at both molecular chain terminals or can have one organofunctional group at one and only one molecular chain terminal. Polyorganosiloxanes having organofunctionality at both molecular chain terminals are used as additives for organic polymers prepared mainly by polycondensation, for example, polyesters, polyamides, polycarbonates, and polysulfones. However, the copolymerization of this type of polyorganosiloxane with the monomer precursor for the organic polymer cannot give a copolymer in which the polyorganosiloxane chain branches from the molecular chain of the organic polymer, that is, a so-called graft copolymer. Also, the use of polyorganosiloxanes having one organofunctional group at one and only one molecular chain terminal, do not yield a satisfactory improvement in the properties of the organic polymer product. In order to solve this problem, Japanese Patent Application Laid-Open No. 4-323222 (323,222/1992) discloses polyorganosiloxanes having at least two organofunctional groups at one and only one molecular chain terminal. However, the polyorganosiloxane described cannot be used as an additive for organic polymers such as polycarbonates and polysulfones because its organofunctional group is limited to an amino, carboxyl, hydroxyl, or epoxy group. EP-A-0 433 746 discloses that a silicone cyclic, such as hexaorganotrisiloxane is lithiated with an alkyl lithium compound followed by treatment with a diorganohalosilane to produce a polydiorganosiloxane having a terminal diorganohydridesiloxy unit. The platinum catalyzed addition of a 2-alkenyl-6-organophenol results in the production of a phenol-siloxane macromer. Conversion of the phenol-siloxane macromer to a silicone polyphenylene ether graft copolymer is effected by oxidatively coupling the 2,6-diorganophenol to the phenol-siloxane macromer. EP-A-0 540 273 discloses an oxidative coupling method using a diorganophenol such as 2,6-xylenol and a silicone macromer having terminal phenol groups such as the hydrosilylation reaction product of eugenol. Thermoplastic polymeric products such as silicone-polyphenylene ether block copolymers, which can be flame retardant, as well as blends thereof with thermoplastic polymers, such as polyphenylene ether, are also disclosed in EP-A-0 540 273. EP-A-0 412 550 discloses an organohydrogenpolysiloxane which does not have an average chemical structure as encountered with organopolysiloxanes prepared by equilibration polymerization reactions, but rather which has a clear, defined chemical structure in which the position and number of silicon-bonded hydrogen groups is clearly defined. The organopolysiloxane has a branched structure in the vicinity of one terminal of the molecular chain and has the silicon-bonded hydrogen group at each of each of the resulting derivative terminals.The organopolysiloxanes can be addition-reacted with, for example, organic compounds having various functional groups to give organopolysiloxane having two organofunctional groups clustered at one terminal. EP-A-0 516 143 discloses a novel method for the preparation of an organopolysiloxane which has two or three diorganohydrogensiloxy groups at one and only one end of the molecular chain terminal. The method disclosed in EP-A-0 516 143 is particularly useful in that it produces high yields of the desired organopolysiloxane. The method comprises causing a condensation reaction between (A) a hydrogen or lithium terminated polysiloxane and (B) an organopolysiloxane having two or three diorganohydrogensiloxy groups at one terminal of the molecular chain and a halogen at the other terminal of the molecular chain. EP-A-0 385 732 discloses a hydroxyphenyl group-containing siloxane compound which has the following formula (I): wherein R is C 1-4 alkyl; R 1 represents R or R 2 , where R 2 represents or R 3 is a C 1-20 monovalent organic group and m and n are each 0 or a positive integer, provided that m+n is 1 or more. The siloxanes (I) may be prepared by reacting p-tert-butoxystyrene with the corresponding Si-H moiety-containing siloxane and hydrolyzing the product. SUMMARY OF THE INVENTION This invention relates to a novel hydroxyphenyl-functional polyorganosiloxanes having at least two hydroxyphenyl groups at one molecular chain terminal. It is an object of the present invention to provide novel polyorganosiloxanes having at least two hydroxyphenyl groups at one molecular chain terminal. DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a hydroxyphenyl-functional polyorganosiloxane having the formula wherein each R is independently a monovalent hydrocarbon group free of aliphatic unsaturation, A is a substituted or unsubstituted hydroxyphenyl group, B is selected from the group consisting of alkyleneoxyalkylene groups having at least two carbon atoms and alkylene groups having at least 2 carbon atoms, m is zero or 1, and n is an integer from 0 to 400. In the formula above, each R is independently selected from monovalent hydrocarbon groups which are free of aliphatic unsaturation. Specific examples of R are alkyl groups exemplified by methyl, ethyl, propyl, butyl, pentyl, or hexyl, aryl groups exemplified by phenyl, tolyl, or xylyl, and aralkyl groups exemplified by benzyl or phenethyl. The group A is a substituted or unsubstituted hydroxyphenyl group. The group A preferably is a group having the formula: wherein R 1 is selected from the group consisting of an alkyl group having from 1 to 4 carbon atoms and an alkoxy group having from 1 to 4 carbon atoms, and a is an integer having a value of 0 to 4. The group A is exemplified by 2-hydroxyphenyl, 3-hydroxyphenyl, 4-hydroxyphenyl, 4-hydroxy-3-methoxyphenyl, 4-hydroxy-2-methoxyphenyl, 3-hydroxy-4-methoxyphenyl, 3-hydroxy-2-methoxyphenyl, 2-hydroxy-4-methoxyphenyl, or 2-hydroxy-3-methoxyphenyl. The group B is an alkyleneoxyalkylene group or alkylene group having at least 2 carbons. The alkylene group is specifically exemplified by ethylene, propylene, butylene, pentylene, or hexylene, while the alkyleneoxyalkylene group is specifically exemplified by ethyleneoxypropylene or ethyleneoxybutylene. The subscript m in the formula for the hydroxyphenyl-functional polyorganosiloxane is 0 or 1. When m is 0 the polyorganosiloxane of this invention has 3 hydroxyphenyl groups at the one end of the molecular chain, and when m is 1 it has 2 hydroxyphenyl groups at the one end of the molecular chain. The subscript n is an integer from 0 to 400 and preferably from 1 to 200. Values for n in excess of 400 cause a decline in the copolymerizability with the precursor monomer for the organic polymer. Hydroxyphenyl-functional polyorganosiloxanes according to this invention are exemplified by: and The hydroxyphenyl-functional polyorganosiloxanes of this invention can be prepared, for example, by an addition reaction in the presence of hydrosilylation catalyst, for example, a platinum catalyst, between a polyorganosiloxane having at least 2 silicon-bonded hydrogen atoms at the one molecular chain terminal which are exemplified by compounds having the formula wherein R, B, m, and n are as defined hereinabove, and an aliphatically unsaturated hydrocarbon compound whose molecule contains a phenol group whose hydroxyl group is protected, for example, by a triorganosilyl group, and by subsequently removing the triorganosilyl group by adding an alcohol exemplified by methanol, and heating the mixture in the presence of an acid catalyst. The preparation of the compounds of this invention can also employ an aliphatically unsaturated hydrocarbon compound which contains a phenol group whose hydroxyl group is not protected, for example by a triorganosilyl group. Polyorganosiloxanes having at least 2 silicon-bonded hydrogen atoms at the one molecular chain terminal can be prepared, for example, by a condensation reaction between an organosilane having the formula wherein R and n are defined as above and X is a hydrogen or lithium atom, or a siloxane having the formula wherein R, B, and m are defined as above and Y is a halogen atom, such as is taught in Japanese Patent Application Laid-Open No. 4-353523 (353,523/1992). Since the polyorganosiloxanes of this invention have two or more hydroxyphenyl groups at one but only one molecular chain terminal, its copolymerization with monomer precursors for organic polymers will give organic polymers in which the polyorganosiloxane chain is bonded in graft form. The polyorganosiloxanes of this invention are therefore useful as surfactants or as additives for organic polymers exemplified by polycarbonates, polysulfones, polyacrylates, or epoxy resins. Example 1 A mixture of 240 ml of isopropyl alcohol, 120 ml of concentrated hydrochloric acid, and 240 ml of water was cooled on an ice water bath to reach a liquid temperature not exceeding 10°C. This was followed by the introduction of 120.6 grams (g) of 1,1,3,3-tetramethyldisiloxane and then the dropwise addition of 54.5 (g) of methyltrimethoxysilane. After the completion of this addition, the ice water bath was removed and the reaction was stirred for 1 hour. The aqueous layer was then removed and the organic layer was neutralized by the addition of sodium bicarbonate and repeatedly washed with water until the aqueous layer was neutral, and then dried over sodium sulfate. Subsequent distillation under reduced pressure gave 45.5 (g) of a fraction at 97-98°C/83 mmHg. This fraction was confirmed to be methyltris(dimethylsiloxy)silane by 1 H-nuclear magnetic resonance analysis (NMR) and infrared spectrochemical analysis (IR). Next, 120 (g) of the methyltris(dimethylsiloxy)silane was placed in a four-neck flask equipped with a stirrer and a sufficient amount of platinum-tetramethyldivinyldisiloxane complex was introduced to give 20 ppm platinum metal based on the total weight of the reaction mixture (methyltris(dimethylsiloxy)silane plus dimethylvinylchlorosilane). Next, the resulting mixture was heated to 80°C, and then 21.5 (g) of dimethylvinylchlorosilane was added dropwise and the reaction mixture was stirred at 90°C to 100°C for 1 hour after the completion of this addition. Analysis of the reaction mixture at this point by gas chromatography (GLC) demonstrated that the peak for the starting dimethylvinylchlorosilane had disappeared, which confirmed completion of the reaction. Distillation under reduced pressure then gave 47.6 (g) of a fraction at 89-91°C/1 mmHg. Analysis of this fraction by NMR and IR confirmed it to be a silicone compound, designated hereinafter as polymer T, having the average formula Next, 60 (g) of hexamethylcyclotrisiloxane and 60 (g) of tetrahydrofuran were introduced into a four-neck flask equipped with a stirrer and were cooled with ice water to a liquid temperature not exceeding 20°C. While stirring under a dry nitrogen blanket 32.43 mmol n-butyllithium in n-hexane solution was introduced and stirring was then continued at room temperature. The development of the polymerization reaction during stirring was monitored by GLC analysis of the reaction mixture. The hexamethylcyclotrisiloxane conversion was 98.4% after six hours, at which point 0.66 (g) of triethylamine and then 13.89 (g) of polymer T were added in order to terminate the polymerization reaction. Filtration of the salt by-product and distillation of the solvent and low boilers by heating under reduced pressure then gave a colorless and transparent reaction product. Analysis of this reaction product by NMR, IR, and GPC and iodometric determination of the SiH group weight% confirmed it to be a polyorganosiloxane, designated hereinafter as polymer 1, having the average formula having an SiH group weight% of 0.093%, having a number-average molecular weight (Mn) of 2,288, and a dispersity of 1.13. Next, 60 (g) of hexamethylcyclotrisiloxane and 60 (g) tetrahydrofuran were introduced into a four-neck flask equipped with a stirrer and were cooled with ice water to a liquid temperature not exceeding 20°C. While stirring under a dry nitrogen blanket 10.81 mmol of n-butyllithium in n-hexane solution was introduced and stirring was then continued at room temperature. The development of the polymerization reaction during stirring was monitored by GLC analysis of the reaction mixture. The hexamethylcyclotrisiloxane conversion was 98.6% after six hours, at which point 0.22 (g) triethylamine and then 4.63 (g) of polymer T as described above were added in order to terminate the polymerization reaction. Filtration of the salt by-product and distillation of the solvent and low boilers by heating under reduced pressure then gave a colorless and transparent reaction product. Analysis of this reaction product by NMR, IR, and GPC and iodometric determination of the weight percent of SiH confirmed it to be a polyorganosiloxane, designated hereinafter as polymer 2, having the formula having 0.034 weight% SiH groups, a number-average molecular weight (Mn) of 7,218, and a dispersity of 1.08. Next, the following were heated together for 2 hours at 100°C: 30 (g) of polymer 1 (having 27.9 milliequivalents of SiH) as described above, 8.64 (g) of trimethylsilyl-o-allylphenol, and a sufficient amount of platinum-tetramethyldivinyldisiloxane complex to give 10 ppm platinum metal. IR analysis of the resulting reaction mixture then confirmed that the characteristic absorption of the SiH group had disappeared. Distillation of the low boilers from the reaction mixture by heating under reduced pressure then yielded a transparent fluid. Analysis of this fluid by NMR and IR confirmed it to be polyorganosiloxane having the formula Next, 30 g of this polyorganosiloxane and 7.97 g methanol were mixed and then stirred at 50°C for 3 hours. Subsequent distillation of the low boilers by heating under reduced pressure yielded a transparent fluid. Analysis by NMR and IR and titrimetric determination of the weight% of phenolic hydroxyl groups confirmed this fluid product to be a polyorganosiloxane having the formula and having an OH group content of about 1.42 weight%. Example 2 The following were heated together for 2 hours at 100°C, 50 (g) of polymer 2 (having 10.2 milliequivalents of SiH) as described above, 3.16 g of trimethylsilyl-o-allylphenol, and a sufficient amount of platinum-tetramethyldivinyldisiloxane complex to give 10 ppm platinum metal. IR analysis of the resulting reaction mixture then confirmed that the characteristic absorption of the SiH group had disappeared. Distillation of the low boilers from the reaction mixture by heating under reduced pressure then yielded a transparent fluid. Analysis of this fluid by NMR and IR confirmed it to be a polyorganosiloxane having the formula Next, about 30 g of this polyorganosiloxane and 7.97 g of methanol were mixed and then stirred at 50°C for 3 hours. Subsequent distillation of the low boilers by heating under reduced pressure yielded a transparent fluid. Analysis by NMR and IR and titrimetric determination of the weight% of phenolic hydroxyl groups confirmed this fluid product to be polyorganosiloxane having the formula having an OH group content of about 0.56 weight%.

Claims: A hydroxyphenyl-functional polyorganosiloxane compound having the formula wherein R is independently a monovalent hydrocarbon group free of aliphatic unsaturation, A is a substituted or unsubstituted hydroxyphenyl group, B is selected from the group consisting of alkyleneoxyalkylene groups having at least two carbon atoms and alkylene groups having at least 2 carbon atoms, m is zero or 1, and n is an integer from 0 to 400. A compound according to Claim 1, wherein R is independently selected from the group consisting of alkyl groups, aryl groups, and aralkyl groups. A compound according to Claim 2, wherein the alkyl group is selected from the group consisting of methyl, ethyl, propyl, butyl, pentyl, and hexyl. A compound according to Claim 2, wherein the aryl group is selected from the group consisting of phenyl, tolyl, and xylyl. A compound according to Claim 2, wherein the aralkyl group is selected from the group consisting of benzyl and phenethyl. A compound according to Claim 1, wherein A is a group having the formula: wherein R 1 is selected from the group consisting of an alkyl group having from 1 to 4 carbon atoms and an alkoxy group having from 1 to 4 carbon atoms, and a is an integer having a value of 0 to 4. A compound according to Claim 1, wherein A is selected from the group consisting of 2-hydroxyphenyl, 3-hydroxyphenyl, 4-hydroxyphenyl, 4-hydroxy-3-methoxyphenyl, 4-hydroxy-2-methoxyphenyl, 3-hydroxy-4-methoxyphenyl, 3-hydroxy-2-methoxyphenyl, 2-hydroxy-4-methoxyphenyl, and 2-hydroxy-3-methoxyphenyl. A compound according to Claim 1, wherein B is an alkylene group. A compound according to Claim 8, wherein the alkylene group is selected from the group consisting of ethylene, propylene, butylene, pentylene, and hexylene. A compound according to Claim 1, wherein B is an alkyleneoxyalkylene group. A compound according to Claim 10, wherein the alkyleneoxyalkylene group is selected from the group consisting of ethyleneoxypropylene and ethyleneoxybutylene. A compound according to Claim 1, wherein m has a value of 1. A compound according to Claim 1, where n is an integer of 1 to 200. A compound according to Claim 1, wherein the hydroxyphenyl-functional polyorganosiloxane is selected from the group consisting of and

Inventors: FURUKAWA HARUHIKO, MORITA YOSHITSUGU, OKAWA TADASHI, UEKI HIROSHI, FURUKAWA, HARUHIKO, MORITA, YOSHITSUGU, OKAWA, TADASHI, UEKI, HIROSHI, Furukawa, Haruhiko c/o Dow Corning T. S. Co., Ltd., Morita, Yoshitsugu, Dow Corning T. S. Co., Ltd., Okawa, Tadashi, c/o Dow Corning T. S. Co., Ltd., Ueki, Hiroshi, c/o Dow Corning T. S. Co., Ltd
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE COMPANY, LIMITED
Application year: 1996
Main classification: C08G77
IPC codes: C08G77