Formation of gratings in polymer-coated optical fibers

Abstract: Recognizing the rate-determining nature of the coating removal and recoating steps, applicants have demonstrated that with proper combination of low absorbing polymer, glass and low intensity radiation, UV-induced gratings can be side-written into polymer coated fibers without removing the polymer, thus permitting the possibility of high speed fabrication of fiber gratings. FIG.2, which shows typical apparatus for practicing the method, includes a typical fiber (20) comprising a core (21), a cladding (22) surrounding the core, and an outer polymer coating (23). UV light from laser (24) passes through mask (25) the polymer coating (23), and the cladding (22) to write a pattern of index changes along the photosensitive core (21). Alternatively, the pattern can be defined by two interfering beams of UV radiation. The UV radiation should be at a sufficiently low intensity that it does not seriously damage the polymer coating. A methylsilsesquioxane-coated fiber treated with D 2 was exposed to UV light from a KrF excimer laser. An amplitude mask was used to produce long period gratings. The fiber was held taut to the amplitude mask, and its side adjacent to the mask was exposed to the UV radiation. At 130mJ/cm 2 1 dB loss developed at the selected wavelength after exposure for approximately 5 mintues. Examination of the fiber surface showed some physical damage to the polymer with periodicity comparable to the amplitude mask, but the coating remained intact and the damage appeared superficial. Decreasing the power to 100 mJ/cm 2 resulted in 0.5 dB loss, and minor damage to the surface of the polymer.

Description: Field of the Invention This invention relates to methods for forming gratings, such as Bragg gratings, in optical fibers and, in particular, to a method for forming photo-induced gratings in polymer-coated optical fibers without removing the polymer. Background of the Invention The dominant method for writing photo-induced gratings in optical fibers is side-writing with ultraviolet (UV) light through the fiber cladding. An optical fiber having a photosensitive glass core and a surrounding cladding is exposed to ultraviolet light having an intensity which varies periodically along a length of the fiber. The periodically varying intensity pattern is typically provided by applying a UV beam to an optical phase grating as described in Anderson et al United States Patent No. 5,327,515 issued July 5, 1994 which is incorporated herein by reference. Alternatively, the intensity pattern can be provided by an amplitude mask or by interfering a pair of coherent UV beams as described in W. H. Glenn et al United States Patent No. 4,725,110 issued February 16, 1988, incorporated herein by reference. In each of these conventional techniques, the source of UV light is typically a high intensity Excimer laser. Surprisingly, the rate-determining step in conventional fiber grating manufacture is not writing the grating but rather removing and subsequently reapplying the protective polymer coating that the fiber was provided at manufacture. These coatings are needed to protect the sensitive fiber from contamination and mechanical damage, but typical coatings significantly absorb UV radiation and interfere with grating formation. Moreover the coating would be damaged by UV laser beams. Thus, an initial step in conventional grating formation is stripping the polymer coating, as by soaking the fiber in hot sulfuric acid. A new coating must be applied and cured after the grating is formed. The coating removal and reapplication steps consume more than half the time required to write a grating in the conventional process. Summary of the Invention The present invention concerns a method of forming a grating in an optical fiber, as defined in claim 1. Recognizing the rate-determining nature of the coating removal and recoating steps, applicants have demonstrated that with proper combination of low absorbing polymer, glass and low intensity radiation, UV-induced gratings can be side-written into polymer coated fibers without removing the polymer, thus permitting high speed fabrication of fiber gratings. Brief Description of the Drawings The advantages, nature and various additional features of the invention will appear more fully upon consideration of the illustrative embodiments now to be described in detail in connection with the accompanying drawings. In the drawings: FIG. 1 is a flow diagram depicting the steps involved in forming a grating in polymer coated fiber. FIG. 2 is a schematic view in partial cross section showing the arrangement used in grating formation. It is to be understood that these drawings are for purposes of illustrating the concepts of the invention and are not to scale. Detailed Description Referring to the drawings, FIG. 1 is a flow diagram depicting the steps in forming a grating in polymer-coated fiber. The grating can be a Bragg grating or a long period grating. As shown in block A of FIG. 1, the first step is to provide an optical fiber waveguide having a polymer coating with low ultraviolet absorption polymer. The optical fiber, as is well known, comprises an inner core of relatively high refractive index and an outer cladding. The inner core is made of UV photosensitive glass, such as germanosilicate, so that a grating can be written by UV radiation. The outer polymer coating should be of low UV absorbing polymer such as an aliphatic poly(meth)acrylate, a silsesquioxane, a vinyl ether, or an alkyl substituted silicone. Advantageously, the fiber is sensitized to UV radiation as by treating the fiber with deuterium D 2 . This preferably involves placing the fiber in a D 2 gas environment, advantageously at an elevated pressure and temperature, so that D 2 will diffuse through the polymer, the cladding and into core. Typical treatment conditions are 3500 psi, 50-70°C for 3 days. The treatment enhances the sensitivity of the UV photosensitive core so that the grating can be written at lower intensity. FIG. 2, which shows typical apparatus for practicing the method, includes a typical fiber 20 comprising a core 21, a cladding 22 surrounding the core, and an outer polymer coating 23. Block B shows that the next step is to expose the fiber by side writing through the polymer and cladding, a pattern of UV radiation corresponding to the desired grating. Successive radiation intensity peaks are spaced apart by the desired grating spacing. The grating pattern can be defined by a mask along the fiber such as an amplitude mask or a phase mask schematically illustrated in FIG. 2. UV light from laser 24 passes through mask 25, the polymer coating 23, and the cladding 22 to write a pattern of index changes along the photosensitive core 21. Alternatively, the pattern can be defined by two interfering beams of UV radiation. The UV radiation should be at a sufficiently low intensity that it does not seriously damage the polymer coating. Methods for forming gratings in polymer-coated fiber can be better understood by consideration of the following specific examples. Example 1 A methylsilsesquioxane-coated fiber treated with D 2 was exposed to UV light from a KrF excimer laser. An amplitude mask was used to produce long period gratings. The fiber was held taut next to the amplitude mask, and its side adjacent to the mask was exposed to the UV radiation. At 130 mJ/cm 2 1 dB loss developed at the selected wavelength after exposure for approximately 5 minutes. Examination of the fiber surface showed some physical damage to the polymer with periodicity comparable to the amplitude mask, but the coating remained intact and the damage appeared superficial. Decreasing the power to 100 mJ/cm 2 resulted in 0.5 dB loss, and minor damage to the surface of the polymer. Example 2 In this example, using a similar methylsilsesquioxane coated fiber, UV laser pulses at 242 nm were obtained from a frequency-doubled dye laser (which was pumped by a KrF excimer laser). The radiation was defocused to decrease the fluence. In the first attempt, the focal point was moved 2 inches behind the fiber. After - 3 minutes of exposure at 20 mW there was no evidence of a grating impressed in the fiber core. In the second attempt, the focal point was moved to within 1 inch of the fiber. A weak reflector (∼ 3%) was observed. In subsequent attempts a 10% reflector was grown in less than 1.5 minutes and an - 70% reflector was grown after 6 minutes of exposure. In none of these cases was damage to the polymer coating detected.

Claims: A method for forming a grating in an optical fiber comprising the steps of: providing a polymer-coated optical fiber, said fiber having a cladding and a photosensitive core and the polymer which coats the fiber being made of a low ultraviolet absorbing material; and without removing said polymer, exposing said core by side writing through said polymer and cladding, to a pattern of ultraviolet radiation corresponding to the grating to be formed. The method of claim 1 wherein said polymer-coated fiber is coated with a polymer selected from the group consisting of aliphatic poly(meth)acrylates, silsesquioxanes, alkyl-substituted silicones and vinyl ethers. The method of claim 1 wherein said polymer coated fiber is coated with methylsilsesquioxane. The method of claim 1 further comprising the step of loading D 2 into the core of said fiber prior to exposing said core.

Inventors: ASPELL JENNIFER, INNISS DARYL, KUCK VALERIE JEANNE, PACZKOWSKI MARK ANTHONY, SIMOFF DEBRA ANN, ASPELL, JENNIFER, INNISS, DARYL, KUCK, VALERIE JEANNE, PACZKOWSKI, MARK ANTHONY, SIMOFF, DEBRA ANN
Applicants: AT & T CORP, AT&T CORP.
Application year: 1996
Main classification: G02B6
IPC codes: C03B37, G02B6, G02B5