1,3,4-Thiadiazole ether curing systems for chlorine containing polymers

Abstract: The present invention provides an improved curing system for chlorinated polymers using as a curing agent alkyl ether and alkyl thioether derivatives of 2,5-dimercapto-1,3,4-thiadiazole and of its dimer.

Description: BACKGROUND OF THE INVENTION The present invention relates to curing systems based on ether derivatives of 2,5-dimercapto-1,3,4-thiadiazole compounds and their use in curing chlorine-containing polymers. In the past, chlorine-containing polymers have been compounded with curatives and other ingredients for vulcanization into vulcanizates for use in various industrial and consumer applications. Many known curing accelerators, however, are highly active at relatively low temperatures and consequently may cause premature vulcanization or scorching. This phenomenon may lead to unsatisfactory physical properties of the vulcanizate. Another problem of known 1,3,4-thiadiazole curing agents is poor bin storage stability. That is, the viscosity tends to increase during storage of the chlorinated polymer compounded with the thiadiazole based curative. The increased viscosity requires tedious process control, as for example frequent adjustment of machine settings. Known accelerators based on 2,5-dimercapto-1,3,4-thiadiazole compounds are disclosed in U.S. Pat. No. 4,128,510 and U.S. Pat. No. 5,391,621. Surprisingly, it has been discovered that certain ether derivatives of 2,5-dimercapto-1,3,4-thiadiazole are effective curing agents for chlorinated polymers. These ether derivatives provide a long scorch time as well as rapid crosslinking once the onset of cure is reached. Another unexpected benefit for the subject ether derivatives is improved bin storage stability. Thus mixed stock can be used for extended periods of time without affecting process conditions. SUMMARY OF THE INVENTION In accordance with the invention, there is provided an improved curing system for chlorinated polymer compositions. The curable compositions comprise a mixture of saturated and unsaturated chlorine containing polymers end an ether 2,5-dimercapto-1,3,4-thiadiazole having the formulae I and II and wherein n = 1-2, X represents O or S, R 1 and R 2 are selected independently from linear or branched chain alkyl groups having 1 to 8 carbon atoms, and R 3 and R 4 represent hydrogen or alkyl groups having 1 to 8 carbon atoms and wherein the chlorinated polymer contains at least 1 % by weight of chlorine based on the total weight of polymer and both (a) the ether or thioether derivative and (b) the chlorine in the chlorinated polymer are present in an amount sufficient to result in curing of the chlorinated polymer. DETAILED DESCRIPTION OF THE INVENTION The 2,5-dimercapto-1,3,4-thiediazoles useful as curing agents or curing accelerators in accordance with the invention are ether or thioether derivatives. The compounds are derived either from one molecule of 2,5-dimercapto-1,3,4-thiadiazole or its dimer and have the structural formulae or wherein n=1-2,X represents O or S. The R 1 , R 2 , R 3 and R 4 groups are the same or different alkyl groups having 1 to 8 carbon atoms and R 3 and R 4 can be hydrogen. Examples of suitable groups include linear or branched alkyl radicals such as methyl, ethyl, propyl, butyl, isobutyl, hexyl, 2-ethylhexyl, octyl. The compounds are not novel per se. The ether, compounds within the scope of the above formulae are described in U.S. Pat. No. 5,194,621 and are useful antiwear agents and antioxidants for lubricants. The ether derivatives are disclosed as useful for photographic applications in U.S.Pat. No. 4,895,794. Any saturated or unsaturated chlorine containing polymer containing at least one percent and preferably about five percent by weight of chlorine may be crosslinked in accordance with the invention. Typical of the chlorine containing polymers are, among others, homopolymers of epichlorohydrin, copolymers of epichlorohydrin and ethylene oxide or propylene oxide, polychloroprene, chlorinated polyolefins, chlorosulfonated polyolefin, polychloroalkylacrylates and chlorobutyl rubber. The polymers are well known and available commercially. The chlorine containing polymers may be blended with non-halogen containing polymers provided there is a sufficient chlorine content present to effect crosslinking. The blends can include natural rubber, polybutadiene, polyolefins, copolymers of butadiene with styrene (SBR) or acrylonitrile (NBR), copolymers of ethylene-propylene-diene (EPDM), butyl rubber and the like. Such blends may contain from about 10 to about 90% by weight of each type of polymer, more preferably from about 25 to 75% by weight, based on the polymer content of the blend. The most preferred blends are those containing the chlorinated polymer at levels of from about 25 to 75% by weight. The ether and thioether derivatives of this invention may be incorporated into the polymer composition in their pure form or they may be mixed with one or more liquid diluents. They may also be adsorbed onto the surface of finely divided, inert carrier to provide a powdered product. Suitable diluents, among others, include aromatic, naphthenic and paraffinic hydrocarbon oil; polyglycols and glycols; alkyl esters of dibasic acids, e.g. dioctyl phthalate, dioctyl sebacate, dioctyl adipate, diisodecyl glutarate, dioctyl azolate; alkyl sulfides; fatty acid esters, e.g., butyl oleate, butyl stearate, octyl epoxy tallate, trioctyl trimellitate; polyester plasticizers, e.g. polymeric di(butoxy-ethoxy-ethyl) adipate, polymer of bis(ethyleneoxy)methane with disulfide linkages; petroleum sulfonates; alkyl trimellitates; and polymeric esters. Suitable finely divided carrier materials include carbon black, metal oxides, such as aluminum oxide; alumina; silica; mineral fillers such as clay, talc and bentonite; aluminosilicates; zeolites, calcium silicate and similar carriers. The amount of the ether or thioether active ingredient effective to cure the chlorinated polymer composition will vary as a function of the chlorine content of the elastomer. Generally, it is employed in the range from about 0.1 to about 10.0 parts by weight per 100 parts by weight of chlorinated polymer present in the curable composition, more preferably in the range of about 0.5 to about 5.0 parts by weight per 100 parts by weight of chlorinated elastomer. Where the ether derivatives are diluted or combined with a finely divided carrier, higher levels of the resulting material may be used to provide the required level of active ingredient. In case of polymers having relatively unreactive chlorine substituent, it is preferable to use a secondary accelerator of the aliphatic or aromatic amine type. Suitable accelerators, among others, include the reaction product of butyraldehyde and aniline, available commercially under the trade name VANAX® 808 from R.T. Vanderbilt Company, Inc., fatty amines, and quaternary ammonium salts, such as tetrabutylammonium bromide and tetraethylammonium chloride. For curing blends of chlorinated and non-chlorinated polymers, sulfur or other well known sulfur-containing curatives for unsaturated elastomers may be included in the composition. Examples of such compounds are sulfur, benzothiazyl disulfide, N-oxydiethylene benzothiazole-2-sulfenamide, 2-mercaptobenzothiazole, alkyl phenol disulfides, tetraalkylthiuram disulfide having normal or branched chain alkyl groups, m-phenylene-bismaleimide, N,N'-diarylguanidines, and like known materials. Other additives that may be desirable for crosslinking with the ether and thioether derivatives include basic metal oxides, metal hydroxides and metal salts of carboxylic acids. Typical additives include zinc oxide, magnesium oxide, zinc stearate and sodium acetate. The magnesium oxide may be synthetic or a natural magnesite mineral. The magnesite may be calcined or treated by other similar processes to yield a predominantly magnesium oxide product. In addition to the curatives, the polymer composition may include antioxidants as for example octylated diphenylamine, diphenyl-p-phenylenediamine and styrenated phenol type antioxidants. The vulcanizable composition may be prepared and blended using any suitable mixing device such as a two-roll mill, an internal mixer (Brabender® Plasticorder), a Banbury Mixer, a kneader or a similar mixing device. The processing and vulcanization techniques are well known in the art. Thus, the invention also relates to a method for preparing a vulcanized composition of a chlorinated polymer selected from the group consisting of polychloroprene, chlorinated polyolefins, chlorosulfonated polyolefins, polychloroacrylates, chlorinated butyl rubber, homopolymers of epichlorohydrin, copolymers of epichlorohydrin and ethylene oxide or propylene oxide and mixtures thereof, comprising the steps of (a) premixing said chlorinated polymer with an ether or thioether derivative of 2,5-dimercapto-1,5,4-thiadiazole having the formulae I and II and wherein n = 1-2, X represents 0 or S, R 1 and R 2 represent linear or branched chain alkyl groups having 1 to 8 carbon atoms, and R 3 and R 4 represent hydrogen or alkyl.groups having 1 to 8 carbon atoms in an amount ranging from about 0.1 to 10 parts by weight per hundred parts by weight of said chlorinated polymers, (b) adding other compounding ingredients and (c) curing said composition. The following examples are given to further illustrate the invention. All percentages and parts are based on weight unless otherwise indicated. EXAMPLE 1 Vulcanizate compositions were prepared by compounding neoprene® W with compounding ingredients and the 2,5-dimercapto-1,3,4-thiadiazole (DMTD) curing agents of the invention as indicated in Table I. The dimer described therein is 2,2'-di(butoxyimethylthio)5,5'-dithiobis(1,3,4-thiadiazole). The vulcanizates were press cured at 160°C for 20 minutes. The physical properties of the vulcanizates were evaluated by the following test methods: Torque and scorch time by ASTM D2084, Mooney parameters by ASTM D1646 using a rotor, physical properties by ASTM D412 and D2250 and compression set by ASTM D395, Method B. The results compiled in Table I demonstrate the improved storage characteristics of vulcanizates cured with the curative of the invention. The improved curatives showed a long delay before the onset of the cure as indicated by the scorch times and they attained full cure in 2 to 4 minutes once crosslinking began. See the results of times tc 90 minus ts 2. The rheometer cure tests further indicate the desirable curing characteristics of the components of the invention. The above embodiments have shown various aspects of the present invention. Other variations will be evident to those skilled in the art and such modifications are intended to be within the scope of the invention as defined by the appended claims.

Claims: A curable composition comprising a major amount of chlorinated polymer selected from the group consisting of polychloroprene, chlorinated polyolefins, chlorosulfonated polyolefins, polychloroacrylates, chlorinated butyl rubber, homopolymers of epichlorohydrin, copolymers of epichlorohydrin and ethylene oxide or propylene oxide and mixtures thereof, and an ether or thioether derivative of 2,5-dimercapto-1,3,4-thiadiazole having the formulae I and II and wherein n=1-2, X represents 0 or S, R 1 and R 2 represent linear or branched chain alkyl groups having 1 to 8 carbon atoms and R 3 and R 4 represent hydrogen or alkyl groups having 1 to 8 carbon atoms and wherein the chlorinated polymer contains at least 1 % by weight of chlorine based on the total weight of polymer and both (a) the ether or thioether derivative and (b) the chlorine in the chlorinated polymer are present in an amount sufficient to result in curing of the chlorinated polymer. A composition of claim 1 wherein said ether or thioether derivative is present at a level ranging from about 0.1 to 10 parts by weight per hundred parts by weight of said chlorinated polymer. A composition of claim 1 wherein R 1 and R 2 alkyl groups contain 1 to 4 carbon atoms and X is oxygen. A composition of claim 1 wherein R 1 and R 2 alkyl groups contain 8 carbon atoms and X is sulfur. A composition of claim 1 which further contains magnesium oxide in an amount effective to co-cure said composition. a composition of claim 1 wherein the ether derivative is mixed with a diluent or carrier. A composition according to claim 1 wherein the ether derivative is 2,5-di(butoxymethylthio)-1,3,4-thiadiazole. A composition according to claim 1 wherein the ether derivative is 2,2'-di(butoxymethylthio)-5,5'-dithiobis(1,3,4-thiadiazole). A method for preparing a vulcanised composition of a chlorinated polymer selected from the group consisting of polychloroprene, chlorinated polyolefins, chlorosulfonated polyolefins, polychloroacrylates, chlorinated butyl rubber, homopolymers of epichlorohydrin, copolymers of epichlorohydrin and ethylene oxide or propylene oxide and mixtures thereof, comprising the steps of (a) premixing said chlorinated polymer with an ether or thioether derivative of 2,5-dimercapto-1,3,4-thiodiazole having the formulae I and II and wherein n = 1-2, X represents 0 or S, R 1 and R 2 represent linear or branched chain alkyl groups having 1 to 8 carbon atoms, and R 3 and R 4 represent hydrogen or alkyl groups having 1 to 8 carbon atoms in an amount ranging from about 0.1 to 10 parts by weight per hundred parts by weight of said chlorinated polymers, (b) adding other compounding ingredients and (c) curing said composition. A method for preparing a vulcanized composition of a chlorinated polymer according to claim 9 wherein the compounding ingredients further comprise magnesium oxide.

Inventors: DOE LESTER A, KAROL THOMAS J, TEPPER RONALD J, DOE, LESTER A., KAROL, THOMAS J., TEPPER, RONALD J.
Applicants: VANDERBILT CO R T, R.T. VANDERBILT COMPANY, INC.
Application year: 1996
Main classification: C08K5
IPC codes: C08L101, C08K5, C08L23, C08L47, C08L33, C08L11, C08L71