Process for producing a preform for a Chalcogenide glass optical fibre and process for drawing the fibre therefrom

Abstract: A process for producing a preform for a chalcogenide glass fiber which comprises inserting a cladding tube having contained therein a chalcogenide glass rod for core into a quartz tube having at its bottom a nozzle having an aperture smaller than the outer diameter of the cladding tube, locally heating the bottom of the quartz tube and pulling the preform compositing said cladding tube and glass rod for core through the nozzle of the said quartz tube. Also disclosed is a process for producing a chalcogenide glass fiber by heating and drawing the preform thus obtained, by which processes the devitrification of glass and the generation of bubbles in the core glass or at the core glass-cladding glass interface can be prevented and the adhesion between the core glass and the cladding glass can be improved. In particular, when the glass material for core does not contain Ge, a chalcogenide glass fiber having such a core-cladding structure that the transmission loss of the glass fiber when infrared light pass through the fiber is small and the mechanical strength is high.

Description: BACKGROUND OF THE INVENTION Field of the invention This invention relates to a process for producing a preform for a chalcogenide glass fiber of a core-cladding structure and a process for producing a chalcogenide glass fiber suitable to the transmission of infrared rays, particularly rays of 1 to 14 µm by using the above preform, excellent in infrared ray-transmissibility, particularly suitable to transmission of infrared signal light. Prior Art A cast method has been known as a method for producing a preform of a core-cladding unitary structure using chalcogenide glass. This cast method comprises casting molten core glass into a tube of cladding glass. As other methods, JP-A-1-230,440 proposes a method for producing a preform of a core-cladding unitary structure by inserting a cladding glass tube into a quartz tube closed at its bottom; further inserting a core glass rod into the cladding glass tube, and heating the outer side of the quartz tube of the resulting assembly in this state by means of a ring heater while reducing the pressure in the space between the core glass rod and the cladding glass tube and applying a pressure to the space between the cladding glass tube and the quartz tube, thereby uniting the core glass and the cladding glass. Chalcogenide glass fibers can be obtained by heat and drawing the preform obtained by the above cast method or the method of JP-A-1-230,440. Moreover, there has been also known a method for producing a chalcogenide glass fiber directly from a core glass rod and a cladding glass tube without preparing a preform. As this method, JP-A-1-226,748 proposes a method for producing a glass fiber by inserting a cladding glass tube having contained therein a core glass rod, into a quartz tube having at its bottom a nozzle having an aperture smaller than the outer diameter of the cladding glass tube and drawing the resulting assembly while locally heating the lower portion of the assembly than the lower end of the quartz tube while controlling the gas pressure in the space between the cladding glass tube and the quartz tube so as to become higher than the gas pressure in the space between the core glass rod and the cladding glass tube. It is well known that chalcogenide glass is thermally unstable. Accordingly, in the method for producing a chalcogenide glass fiber by the above-mentioned cast method, there is such a problem that the glass is devitrified in the course of the production of a preform. In addition, the molten core glass easily takes in bubbles during the casting and these bubbles remain as broths at the interface of the core glass and the cladding glass. When the preform containing these broths is formed into fibers, the broths have become a cause of increasing the transmission loss. By this cast method, it has been impossible to produce a preform for a single mode fiber in which the core diameter is much smaller than the cladding diameter. The method stated in JP-A-1-230,440 for obtaining a preform by uniting the core glass and the cladding glass under control of the pressure in a quartz tube whose bottom is closed can considerably inhibit the devitrification of glass and the generation of bubbles in the core glass or at the core glass-cladding glass interface as compared with the cast method. However, the preform obtained cannot be said to be sufficient in adhesion between the core glass and the cladding glass, and an improvement in adhesion has been desired. Also, this method for producing a preform was unable to produce a preform for a single mode fiber in which the core diameter is much smaller than the cladding diameter. On the other hand, in the method stated in JP-A-1-226,748 for producing a glass fiber directly from a core glass rod and a cladding glass tube without preparing any preform, there has been such a problem that since the cladding glass tube having contained therein the core glass rod must be heated at a high drawing temperature from the beginning, the chalcogenide glass tends to be devitrified and the composition tends to be changed by volatilization. The said method for the direct production of a fiber has such a disadvantage that it is difficult to obtain a single mode fiber in which the core diameter is much smaller than the cladding diameter. Moreover, according to the method for the direct production of a fiber, when it is intended to produce fibers having different diameters, a plurality of quartz tubes having drawing nozzles having correspondingly different diameters must be used and when a fiber having a specific diameter has become necessary, it is difficult to obtain such a fiber in a short period of time. Furthermore, as to the chalcogenide glass fiber of a core-cladding structure, the technique stated in, for example, JP-A-3-8,742 has heretofore been known. This technique intends to provide a power transmission fiber in which each of the core glass and the cladding glass is composed of three elements of As (arsenic), S (sulfur) and Ge (germanium) for enhancing particularly the heat resistance and Se (selenium) is substituted for a part of the S (sulfur) in the core glass for controlling the numerical aperture (NA) of the fiber. However, in the case of the above technique, in order to enhance the heat resistance of a power transmission infrared fiber, Ge element is contained in both the core glass and the cladding glass, and hence, the fact that both contain Ge makes it basically difficult to make the transmission loss lower than a certain level. Also, since Ge is contained in both the core glass and the cladding glass, a sufficient difference in thermal expansion between the two is not obtained in the formation of a fiber and hence it is impossible to enhance the mechanical strength of the fiber. In addition, in the case of the above core-cladding structure, there is such a problem that infrared rays passing through the cladding side become a noise when an optical signal is transmitted and the optical signal to be transmitted in the core undergoes a disturbance. SUMMARY OF THE INVENTION The first object of this invention is to provide a process for producing a preform for a chalcogenide glass fiber by which the problems admitted in the above-mentioned prior art methods including devitrification of glass, generation of bubbles in the core glass or at the core glass-cladding glass interface, incomplete adhesion at the core glass-cladding glass interface and the like have been solved. The second object of this invention is to provide a process for producing a preform for a chalcogenide glass fiber suitable for obtaining a single mode fiber in which the core diameter is much smaller than the cladding diameter. The third object of this invention is to provide a process for producing a chalcogenide glass fiber which makes it possible to obtain, from the preform obtained by the processes for producing a preform mentioned in the above first and second objects, a fiber whose diameter is varied depending upon the drawing conditions in a short period of time without using the quartz tube having spinning nozzles different in diameter and without causing devitrification and composition change due to volatilization. According to this invention, there is provided a process for producing a preform for a chalcogenide glass fiber which comprises inserting a cladding chalcogenide glass tube having contained therein a chalcogenide glass material for core, into a quartz tube having at its bottom a nozzle having an aperture smaller than the outer diameter of the cladding glass tube, locally heating the bottom of the quartz tube and pulling out the cladding glass tube having contained therein the glass material for core [this process is referred to hereinafter as the production process (1) in some cases]. According to this invention, there is further provided another process for producing a preform for a chalcogenide glass fiber which comprises inserting, as a glass material for core, the preform obtained by the above production process (1) into a cladding glass tube, repeating at least one time the production process (1) mentioned above using the resulting assembly to obtain a preform for a single mode fiber in which the core diameter is extremely small as compared with the cladding diameter [this process is referred to hereinafter as the production process (2) in some cases]. According to this invention, there is still further provided a process for producing a chalcogenide glass fiber which comprises polymer-coating the preform obtained by the production process (1) or (2) with an polymer-coating material and heat and drawing the coated preform. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a crosssectional view showing the process for producing a preform of this invention. Fig. 2 is a crosssectional view showing the process for producing a fiber of this invention. Fig. 3 is a crosssectional view showing the preform obtained in Example 4. Fig. 4 is a crosssectional view showing the fiber obtained in Example 4. In Figs. 1 to 4, 1 refers to a quartz tube, 2 to a core rod, 3 to a cladding glass tube, 4 to the bottom of the quartz tube, 5 to a nozzle, 6 to the upper part of the quartz tube, 7 to a pressurizing tube, 8 to the space between the quartz tube and the cladding tube, 9 to the space between the cladding glass tube and the core rod, 10 to a pressure-reducing tube, 11 to a preform, 12 to a heat-shrinkable resin tube, 13 to a ring heater, 14 to a fiber, 15 to the tip of the preform, 16 to a weight, 17 to core glass, 18 to cladding glass of the first composition, 19 to cladding glass of the second composition and 20 to a heat-shrunk resin layer. DETAILED DESCRIPTION OF THE INVENTION First of all, an explanation is made of the production process (1) below. The production process (1) comprises inserting a cladding chalcogenide glass tube having contained therein a chalcogenide glass material for core, into a quartz tube having at its bottom a nozzle having an aperture smaller than the outer diameter of the cladding glass tube, locally heating the bottom of the quartz tube and pulling out the cladding glass tube having contained therein the glass material for core, thereby obtaining a preform for a chalcogenide glass fiber. According to the production process (1), unlike the conventional cast method in which the whole of the glass material for core is heated and melted, the glass material is heated only at the bottom of the quartz tube, whereby the problems of devitrification of glass and generation of bubbles in the core glass or at the core glass-cladding glass interface which problems are seen in the conventional cast method have been solved. Also, according to the production process (1), the core glass and the cladding glass are forcibly melt-united in such a dynamic state that the cladding glass tube having contained therein the glass material for core is heated and then pulled from the nozzle at the bottom of the quartz tube, thereby obtaining a preform. Therefore, as compared with the method stated in JP-A-1-230,440 in which a cladding glass tube having contained therein a glass material for core is statically heated in a bottom-closed quartz tube having no nozzle at the bottom to unite the core glass and the cladding glass, the production process (1) is advantageous in that a preform excellent in adhesion between the core glass and the cladding glass is obtained. In the production process (1), it is preferable that the pressure in the space (i) between the glass material for core and the cladding glass tube is made relatively lower than the pressure in the space (ii) between the cladding glass tube and the quartz tube, whereby the devitrification of glass and generation of bubbles in the core glass or at the core glass-cladding glass interface can be more effectively inhibited and the adhesion between the core glass and the cladding glass is further enhanced. In particular, it is more preferable to keep the space (i) under reduced pressure and the space (ii) under elevated pressure. The pressure in the space (i) between the glass material for core and the clad glass tube is preferably 15 Pa or less, more preferably 1.5 Pa or less. The pressure in the space (ii) between the cladding glass tube and the quartz tube is preferably 2.0 x 10 4 Pa or more, more preferably 2.0 x 10 5 Pa or more. In the production process (1), it is preferable to control the heating temperature at the bottom of the quartz tube to a temperature lower than the drawing temperature, whereby it becomes possible to obtain a preform having a large diameter and also prevent the devitrification of glass in the production of the preform. The heating temperature (Th) at the bottom of the quartz tube is particularly preferably controlled to a temperature 40-150°C lower than the drawing temperature (Tf). The reason therefor is as follows: When Th > (Tf - 40) and the temperature Th is relatively high, the thermally unstable chalcogenide glass is easy to devitrify and crystallization tends to be caused particularly in the core glass or at the core glass-cladding glass interface. When the preform obtained under such conditions is drawn into a fiber, the transmission loss of the fiber obtained becomes remarkably large, and the volatilization of the glass component causes a change in composition. On the other hand, when Th < (Tf - 150) and the temperature Th is relatively low, the chalcogenide glass is not sufficiently softened, and it becomes impossible to pull out the cladding glass united with the core glass from the nozzle of the quartz tube or even if the pulling is possible, a sufficient adhesion between the core glass and the cladding glass is not obtained, the transmission loss becomes large and the fiber strength becomes low. When the cladding glass tube having contained therein the glass material for core is pulled from the quartz tube, it is preferable to hang a weight from the tip of the cladding glass tube. When a weight is hung the following effects can be obtained: (a) The preform is formed into a straight rod and hence the fiber yield is increased when this preform is drawn into a fiber. (b) The drawing speed of the preform becomes constant and hence the diameter of preform is stabilized and the same effect as in (a) (increase of the fiber yield) is obtained. The weight can be suitably determined and generally, a weight of 50 g or more is preferred. An explanation is further made of the production process (2) below. The production process (2) uses the preform for a chalcogenide glass fiber obtained by the production process (1) as a glass material for core and is characterized by repeating at least one time the production process (1) using a cladding glass tube having the preform contained therein, whereby a preform for a single mode fiber having a core diameter much smaller than the cladding diameter can be obtained. The production process (2) is basically the repetition of the production process (1) and hence, as a matter of course, the advantage obtained by the production process (1) (inhibition of devitrification of glass, inhibition of generation of bubbles and improvement of adhesion) can also be brought about by carrying out the production process (2). The preforms for a glass fiber obtained by the production processes (1) and (2) can be drawn in a conventional manner into glass fibers, and it is possible to form a protective coating layer consisting of a resin on the glass fiber thus obtained by passing the glass fiber through a vessel containing the resin. The resin used is preferably a UV curable resin; however, this is not critical and any resin can be used as far as it has a fiber-protective function. For example, a thermosetting resin can be used. Next, the process for producing a chalcogenide glass fiber is explained. The process for producing a chalcogenide glass fiber comprises adhesion-coating the preform for a chalcogenide glass fiber obtained by the production process (1) or (2) with an adhesion-coating material and heating and drawing the coated preform to obtain a chalcogenide glass fiber. According to the above process for producing a glass fiber, the coating of the preform with an adhesion-coating material makes it possible to produce fibers having varying diameters freely by varying the processing conditions including drawing temperature, drawing speed and the like without using an expensive quartz tube at the time of drawing. Also, by previously preparing the preform, the fiber can be produced whenever necessary in a short time. According to said process for producing a glass fiber, the adhesion-coating material applied to the preform can inhibit the composition change due to volatilization of a chalcogenide glass fiber upon heating at the time of drawing can be inhibited, whereby a chalcogenide glass fiber having the desired properties can be obtained. The above adhesion-coating material may be any material as far as it is good in adhesion to the preform and can prevent the chalcogenide glass fiber from being volatilized upon heating at the time of drawing. In particular, the use of a heat-shrinkable tube renders the adhesion-coatability on the preform particularly good and makes it possible to markedly inhibit the glass component from being volatilized from the preform. The heat-shrinkable tube is generally smoother at its opening portion than the quartz tube and hence when the other area of the preform than its end portion is adhesion-coated with the heat-shrinkable tube and the preform is heated and drawn, the fiber can be prevented from being wounded. The heat-shrinkable tube includes (a) heat-shrinkable tubes of fluoroplastics such as Teflon FEP (tetrafluoroethylene-hexafluoropropylene copolymer), polyvinylidene fluoride, Teflon PFA (tetrafluoroethylene-perfluoroalkoxyethylene copolymers), Teflon TFE (polytetrafluoroethylene resin) and the like; (b) heat-shrinkable tubes of silicone rubbers; (c) heat-shrinkable tubes of synthetic rubbers such as neoprene, Viton and the like; (d) heat-shrinkable tubes of polyolefins such as cross-linked polyolefins and the like; (e) heat-shrinkable tubes of vinyl chloride resins and the like. The use of a heat-shrinkable tube having a melting point or softening point close to that of chalcogenide glass is preferable because said use makes it possible to carry out simultaneously the adhesion-coating of the preform with a heat-shrinkable tube and the drawing of the preform into a fiber. As such a heat-shrinkable tube, there is mentioned a tube made of a fluoroplastic such as Teflon or the like. This fluoroplastic is preferred because it is excellent in heat-conductivity, and hence, the time required for heating can be shortened and the yield can be increased as compared with the case where a quartz tube is used. The whole area of the preform may be coated with the adhesion-coating material, or the other area of the preform than its end portion to be subjected to heating and drawing may be coated with the polymer-coating material. In the former case, the preform and the adhesion-coating material are simultaneously subjected to heating and drawing, thereby obtaining a glass fiber having a triple layer structure of core glass, cladding glass and polymer-coating material. In the latter case, only the preform is subjected to heating and drawing, so that a glass fiber having a double layer structure of core glass and cladding glass is obtained. In this case, the double layer structure fiber after the drawing can be passed through a vessel containing a resin to form a protective coating layer consisting of the resin. The resin used is preferably a UV curable resin as already mentioned above; however, any resin such as a thermosetting resin or the like can be used as far as it has a fiber-protecting function. Explanations have been made above concerning the preform production processes (1) and (2) as well as the fiber production process. The term "chalcogenide glass" used herein should be interpreted broadly and refers generically to a glass comprising basically a chalcogen element S, Se or Te among the elements of the VIB Group of the Periodic Table and other component As, P, Sb, Si, Ge, Sn or the like. In addition, the process of this invention can also be applied to a glass having a volatility such as a fluoride glass. WORKING EXAMPLE Example 1 (1) Preform-Production Example First of all, an example is explained according to Fig. 1. A cladding tube 3 having inserted thereinto a core rod 2 was sealed into a quartz tube 1. At the bottom 4 of the quartz tube 1, a nozzle 5 having a smaller aperture than the outer diameter of the cladding tube 3 was provided. In the upper part 6 of the quartz tube 1, a pressurizing tube 7 connected to the space 8 between the quartz tube 1 and the cladding tube 3 was installed. A very slight amount of an Ar gas was introduced through the pressurizing tube 7 to fill the space 8 with the Ar gas. On the other hand, the pressure of the space 9 between the core rod 2 and the cladding tube 3 was reduced to 1.5 Pa by a vacuum pump through a pressure-reducing tube 10 installed so as to be connected to the space 9. The glass composition of the core rod 2 was adjusted to Ge 5 atm %/As 42 atm %/S 53 atm % and the glass composition of the cladding tube 3 was adjusted to Ge 5 atm %/As 40 atm %/S 55 atm %. In this case, the outer diameter of the cladding tube 3 was adjusted to 12.5 mm and the inner diameter thereof was adjusted to 10.5 mm. The outer diameter of the core rod 2 was adjusted to 9.5 mm and the aperture of the nozzle 5 of the quartz tube 1 was adjusted to 9 mm. The vicinity of the nozzle 5 of the quartz tube 1 was heated by a ring heater 13 to 300°C and when the tip of the cladding tube 3 was softened and closely contacted with the nozzle 5, an Ar gas was introduced through the pressurizing tube 7 to adjust the pressure of the space 8 to 2 x 10 5 Pa. When the tip 15 of the preform was extruded through the nozzle 5 of the quartz tube 1, a weight of 100 g was immediately hung from the tip 15 of the preform 11 in the predetermined manner. The preform 11 was pulled at a speed of 4 mm/min. The outer diameter of the resulting preform 11 was 6 mm. In the preform 11 obtained, devitrification of glass was not observed nor the generation of bubbles in the core glass or at the core glass-cladding glass interface was observed. The preform 11 was also excellent in adhesion at the core glass-cladding glass interface. (2) Glass Fiber-Production Example A glass fiber was obtained using the preform obtained in (1) above. As shown in Fig. 2, the periphery of the preform 11 obtained in (1) above was adhesion-coated with a heat-shrinkable tube 12 composed of a fluoroplastic (Teflon FEP), and the lower periphery of the preform 11 was heated to 390°C by a ring heater 13 and drawn into a fiber 14. The fiber 14 thus obtained had a triple layer structure of core glass, cladding glass and heat-shrunk resin, and the transmission loss at a wavelength of 2.4 µm was 0.1 dB/m. (3) Comparative Production Example For comparison, the same core rod and cladding tube as in (1) above were used to prepare a preform by the method stated in JP-A-1-230,440 in which a core rod-containing cladding tube was heated in a quartz tube closed at the bottom. Subsequently, the preform obtained was heated and drawn in the same manner as in (2) above to obtain a glass fiber. The glass fiber obtained was subjected to the same test as in (2) above to find that the transmission loss at a wavelength of 2.4 µm was 0.4 dB/m. For further comparison, the same core rod and cladding tube as in (1) above were used and the core rod-containing cladding tube was inserted into a quartz tube having a nozzle at the bottom, after which a glass fiber was directly produced therefrom according to the method stated in JP-A-1-226,748 without preparing a preform. The transmission loss of the glass fiber thus obtained was 0.3 dB/m at a wavelength of 2.4 µm. Example 2 (1) Preform-Production Example The same procedure as in Example 1 (1) was repeated, except that the glass composition of the core rod 2 was adjusted to Ge 27 atm %/As 30 atm %/Se 43 atm % and the glass composition of the cladding tube 3 was adjusted to Ge 25 atm %/As 29 atm %/Se 46 atm %. In this case, the outer diameter of the cladding tube 3 was adjusted to 12.5 mm, the inner diameter thereof was adjusted to 10.5 mm, the outer diameter of the core rod 2 was adjusted to 9.5 mm and the aperture of the nozzle 5 of the quartz tube 1 was adjusted to 9 mm. The heating temperature was 400°C and the pulling speed was 2 mm/min. The preform 11 obtained had an outer diameter of 6.5 mm, and similarly to the preform obtained in Example 1, neither devitrification of glass nor generation of bubbles were observed and the adhesion between the core glass and the cladding glass was excellent. (2) Glass Fiber-Production Example The periphery of the preform 11 obtained in (1) above was coated with a heat-shrinkable tube 12 composed of a heat-shrinkable fluoroplastic (vinylidene fluoride resin) and the lower periphery of the preform 11 was heated by a ring heater 13 to 500°C and drawn into a fiber 14. The transmission loss of the fiber 14 thus obtained was 0.4 dB/m at a wavelength of 6 µm. (3) Comparative Production Example Using the same core rod and the same cladding tube as in (1) above, a preform was prepared by the method stated in JP-A-1-230,440. Then, the preform was subjected to heating and drawing in the same manner as in (2) above to prepare a glass fiber. The glass fiber thus obtained was subjected to the same measurement as in (2) above to find that the transmission loss at a wavelength of 6 µm was 0.6 dB/m. Separately, using a core rod and a cladding tube having the same respective compositions as in (1) above, a glass fiber was directly prepared by the method stated in JP-A-1-226,748 without preparing a preform. The glass fiber thus obtained was subjected to the same measurement as in (2) above to find that the transmission loss at a wavelength of 6 µm was 0.55 dB/m. Example 3 (1) Preform-Production Example The same procedure as in Example 1 (1) was repeated, except that the glass composition of the core rod 2 was Ge 24 atm %/Se 21 atm %/Te 55 atm % and the glass composition of the cladding tube 3 was Ge 23 atm %/Se 24 atm %/Te 53 atm %. In this case, the outer diameter of the cladding tube 3 was 12.5 mm, the inner diameter of the cladding tube 3 was 10.5 mm, the outer diameter of the core rod 2 was 9.5 mm, and the aperture of the nozzle 5 of the quartz tube 1 was 9 mm. The heating temperature was 400°C and the pulling speed was 2 mm/min. The outer diameter of the preform 11 obtained was 8.0 mm and, similarly to the preform obtained in Example 1, neither devitrification of glass nor generation of bubbles were observed. The adhesion between the core glass and the cladding glass was excellent. (2) Glass Fiber-Production Example The periphery of the preform 11 obtained in (1) above was coated with a heat-shrinkable tube 12 composed of heat-shrinkable fluoroplastic (Teflon FEP), and the lower periphery of the preform 11 was heated to 440°C by a ring heater 13 and drawn into a glass fiber 14. The transmission loss of the glass fiber thus obtained was 0.4 dB/m at a wavelength of 8 µm. (3) Comparative Production Example Using a core rod and a cladding tube having the same respective compositions as in (1) above, a preform was prepared by the method stated in JP-A-1-230,440 and then heated and drawn in the same manner as in (2) above to obtain a glass fiber. The glass fiber thus obtained was subjected to the same measurement as in (2) above to find that the transmission loss at a wavelength of 8 µm was 0.6 dB/m. Separately, using a core rod and a cladding tube having the same respective compositions as in (1) above, a glass fiber was directly prepared without preparing a preform by the method stated in JP-A-1-226,748. The glass fiber obtained was subjected to the same measurement as in (2) above to find that the transmission loss at a wavelength of 8 µm was 0.55 dB/m. Example 4 (1) Preform-Production Example The same procedure as in Example 1 (1) was repeated, except that the glass composition of the core rod 2 was As 40 atm %/S 60 atm % and the glass composition of the cladding tube 3 was Ge 2 atm %/As 37 atm %/S 61 atm % (the first composition). In this case, the outer diameter and inner diameter of the cladding tube 3 were 15.5 mm and 8.0 mm, respectively, the inner diameter of the core rod 2 was 7.5 mm, and the aperture of the nozzle 5 of the quartz tube 1 was 8 mm. The heating temperature was 310°C and the pulling speed was 2 mm/min. The outer diameter of the preform 11 obtained was 6.5 mm, and, similarly to the preform obtained in Example 1, neither devitrification of glass nor generation of bubbles were observed. The adhesion between the core glass and the clad glass was excellent. The same procedure as above was repeated, except that the preform 11 obtained above was used as the core rod 2 and the glass composition of the cladding tube 3 was adjusted to Ge 2 atm %/As 37 atm %/S 61 atm % (the first composition). In this case, the outer diameter and the inner diameter of the cladding tube 3 were 15.5 mm and 7.5 mm, respectively, the outer diameter of the core rod 2 was 6.5 mm, the aperture of the nozzle 5 of the quartz tube 1 was 8 mm. The heating temperature was 310°C and the pulling speed was 2 mm/min. The preform 11 obtained had an outer diameter of 6.5 mm and, similarly to the preform obtained in Example 1, neither devitrification of glass and generation of bubbles were observed. The adhesion between the core glass and the cladding class was excellent. The same procedure as above was repeated twice, except that the preform 11 obtained above was used as the core rod 2. This procedure was repeated, except that the preform 11 thus obtained was used as the core rod 2 and the glass composition of the cladding tube 3 was adjusted to Ge 1.5 atm %/As 38 atm %/S 60.5 atm % (the second composition). The preform 11 thus obtained had an outer diameter of 6.5 mm and, similarly to the preform obtained in Example 1, neither devitrification of glass nor generation of bubbles were observed. The adhesion between the core glass and the cladding glass was excellent. As stated above, the above procedure was repeated five times in total to obtain a preform 11 as shown in Fig. 3 in which the outer diameter of the core glass 17 was 0.12 mm, the outer diameter of the cladding glass 18 of the first composition consisting of four layers was 2.6 mm and the outer diameter of the cladding glass 19 of the second composition was 6.5 mm. (2) Glass Fiber-Production Example The periphery of the preform 11 thus obtained was coated with a heat-shrinkable tube 12 composed of a heat-shrinkable fluoroplastic (Teflon FEP) and the lower periphery of the preform 11 was heated by a ring heater 13 to 390°C and then drawn into a single mode glass fiber 14. The cross-sectional view of the single mode glass fiber 14 was as shown in Fig. 4. As is clear from Fig. 4, in this single mode glass fiber 14, the outer diameter of the core glass 17 was 2.3 µm, the outer diameter of the cladding glass 18 of the first composition was 50 µm, the outer diameter of the clad glass 19 of the second composition was 125 µm, the outer diameter of the fiber including the heat-shrunk resin layer 20 was 135 µm. The transmission loss of the glass fiber 14 was 0.08 dB/m at a wavelength of 2.4 µm.

Claims: A process for producing a preform for a chalcogenide glass fiber which comprises inserting a cladding chalcogenide glass tube (3) having contained therein a chalcogenide glass rod for core (2), into a quartz tube (1) having at its bottom (4) a nozzle (5) having an aperture smaller than the outer diameter of the cladding tube, locally heating the bottom of the quartz tube and pulling out the cladding tube having contained therein the glass rod for core through the nozzle (5) of the bottom (4) of the quartz tube (1). The process for producing a preform for a chalcogenide glass fiber according to Claim 1, wherein the pressure in the space between the glass rod for core (2) and the cladding tuba (3) is adjusted relatively lower than the pressure in the space between the cladding tube (3) and the quartz tube (1). The process for producing a preform for a chalcogenide glass fiber according to Claim 1 or 2, wherein the temperature for heating the bottom (4) of the quartz tube (1) is adjusted lower than the temperature intended for fiber drawing. The process for producing a preform for a chalcogenide glass fiber according to claim 3, wherein the temperature for heating the bottom (4) of the quartz tube (1) is adjusted 40-150°C lower than the temperature intended for fiber drawing. The process for producing a preform for a chalcogenide glass fiber according to any one of Claims 1 to 4, wherein when the cladding tube (3) having contained therein the glass rod for core (2) is pulled out from the quartz tube (1), a weight is hung from the tip of the preform. A process for producing a preform for a chalcogenide glass fiber which comprises inserting into a cladding tube a preform with a core-cladding structure for a chalcogenide glass fiber obtained by the process according to any one of Claims 1 to 5 as a glass rod, repeating the process according to any one of claims 1 to 5 at least one time using the resulting assembly to obtain a preform for a single mode fiber having a very small core diameter as compared with the cladding diameter. A process for producing a chalcogenide glass fiber which comprises polymer-coating a preform for a chalcogenide glass fiber obtained by the process according to any one of Claims 1 to 6 with a polymer-coating material and then heating and drawing the coated preform into a fiber. The process for producing a chalcogenide glass fiber according to Claim 7, wherein the whole of the preform is coated with a polymer-coating material and then heated and drawn into a glass fiber having a triple layer structure of core glass, cladding glass and polymer-coating material. The process for producing a chalcogenide glass fiber according to Claim 7, wherein the preform except for its tip area is coated with a polymer-coating material and then the preform was heated and drawn into a coat-free fiber having a double layer structure of core glass and cladding glass. A process for producing a chalcogenide glass fiber provided with a protective coating layer, which comprises passing through a coating cup with a nozzle at its bottom, a chalcogenide glass fiber obtained by drawing a preform for a chalcogenide glass fiber obtained by the process according to any one of Claims 1 to 6 or a chalcogenide glass fiber obtained by the process according to claim 9.

Inventors: MORIMOTO SHOZO, YAMASHITA TOSHIHARU, YONEDA YOSHITAKA, MORIMOTO, SHOZO, YAMASHITA, TOSHIHARU, YONEDA, YOSHITAKA
Applicants: HOYA CORP, NIPPON SHEET GLASS CO LTD, HOYA CORPORATION, NIPPON SHEET GLASS CO. LTD.
Application year: 1996
Main classification: C03B37
IPC codes: C03B37, C03C13, C03C25