Device comprising films of beta-C3N4

Abstract: The present inventors have discovered how to make continuous films of single-phase crystalline β-C 3 N 4 using microwave plasma chemical vapor transport. The films are hard, translucent nanocrystalline films useful for protecting a substrate.

Description: Field of the Invention This invention relates to devices comprising films of β-C 3 N 4 and to a method for making such devices The films provide a substrate with a protective layer of translucent material having a hardness which can exceed that of diamond, a high energy bandgap and ultraviolet (UV) light transparency. They can be formed on a substrate by microwave plasma chemical vapor transport. Background of the Invention Carbon nitride, C 3 N 4 , can exist in two possible phases designated α-C 3 N 4 and β-C 3 N 4 . It has long been predicted that crystals of β-C 3 N 4 , if they could be made, would possess exotic characteristics such as a hardness exceeding that of diamond, a high energy bandgap and transparency to UV light. Unfortunately, efforts to synthesize this material have produced only amorphous material or impure carbon-rich phases. A continuous coating of crystalline β-C 3 N 4 has not heretofore been obtained, and films exhibiting the predicted properties have not been realized. WO-A-95 01709 (Harvard College; C.M. Lieber et al., January 26, 1995 discloses an extended nitride material that comprises some β-C 3 N 4 , and also discloses a method of making such a material. US Patent 5.110,679 issued May 5, 1992, discloses a C-N material that contains about 5% by volume of crystallites of β-C 3 N 4 , and also discloses a method of making such material. K.M. Yu et al., Physical Review B, Vol.49(7), page 5034, February 1994 disclose substantially the material and method of the '679 US patent. Summary of the Invention The invention is defined in the claims. The present inventors have discovered how to make continuous films of single-phase crystalline β-C 3 N 4 using microwave plasma chemical vapor transport. The films are hard, translucent nanocrystalline films useful for protecting a substrate. Brief Description of the Drawings The advantages, nature and various additional features of the invention are described in detail in connection with the accompanying drawings. In the drawings Fig. 1 is a cross section of a substrate having a surface coated with a continuous film of β-C 3 N 4 . Fig 2 is a schematic illustration of apparatus useful in making the coated substrate of Fig. 1; Fig. 3 is a Rutherford backscattering spectrum for a typical film; Figs. 4 and 5 are X-ray photoelectron spectra for carbon and nitrogen in the film, Fig. 6 is a TEM microphotograph of the film; FIG. 7 is a dark field TEM microphotograph; and FIG. 8 is a transmission electron diffraction pattern. It is to be understood that these drawings are for purposes of illustrating the concepts of the invention and, except for graphical illustrations and photographs, are not to scale. Detailed Description Referring to the drawings, FIG. 1 is a cross sectional illustration of a substrate 17 having a surface 110 coated with a continuous film 120 of β-C 3 N 4 . The material of film 120 approaches the ideal composition of C 3 N 4 having a typical stoichiometry of 43% carbon, 49-54% nitrogen and, in air, 3-9% oxygen. The film is translucent with a light yellow or olive coloration. Crystallization and the lattice spacings of single-phase β-C 3 N 4 are manifested by electron diffraction from the film. The substrate can be a semiconductor, such as silicon, for which the film can provide a protective coating or a metal, such as steel, for which the film provides hard cutting or wear-resistant surface. On semiconductor or insulating substrates the film is also useful as a protective window permitting influx of ultraviolet light. FIG. 2 illustrates apparatus useful in making the product of FIG. 1 comprising a plasma reactor 10 composed of an evacuable chamber 11 having a microwave transparent wall 12 such as a quartz window. The reactor is a modified Vactronic Laboratories Model M-60. Within the chamber 11, mounted on a turnable bottom plate 25 are a carbon (graphite) disk 13 supported by a pedestal of boron nitride plates 14 and a carbon (graphite) filament 15 supported horizontally by a ceramic post 16. The substrate 17 was placed in the duct 18 linking a viewport 19 to the wall of chamber 11. The graphite filament and silicon strip are aligned along the cavity center line with the filament 7-15 mm above the substrate. Microwave energy passing through transparent wall 12 can produce two plasma modes individually or simultaneously. The primary-mode plasma 20 produces a broad reaction with the center region of the filament at the temperature range 900-1050°C. The secondary-mode plasma 21 is generated at the free-suspended tip of the filament 15 at a temperature range 650-850°C. The reactor is equipped with a gas inlet 22 in the upstream section. Through the inlet a number of different gases can be introduced into the reactor. The flow rate of each gas can be independently controlled by a flow-rate controller (not shown). The reactor is also equipped with a pumping system (not shown) in the downstream section. Gas can be pumped out from the reactor through outlet 23 and a throttle valve (not shown). The preferred gases are nitrogen and helium. Typical operating parameters for β-C 3 N 4 synthesis are 650 watts of microwave power in the cylindrical TM 01 mode, nitrogen flow at 50-200 sccm, and helium flow at 100-300 sccm. The preferred flow ratio is N 2 /He in the range 33-60%. The graphite temperature at the center region is 650-900°C and at the free suspended tip, 650-900°C. The substrate temperature is estimated at 300-500°C. An exemplary run involves setting the helium and nitrogen to preset flow rates of 200 sccm He, 75 sccm N 2 . The reactor pressure is set to a preset level of 120 torr, and the gas and pressure controllers are turned on. Until the Bows and pressure are stabilized, the throttle valve maintains the reactor in a constant pressure range, and all gases maintain a constant flow rate. The high voltage of the microwave power supply is turned on, and the plasma is ignited in the primary and secondary modes. These two modes of plasma heat the graphite filament to a temperature in the range 600-1100°C, and synthesis of the β-C 3 N 4 coating begins. Applicants attribute crystallization of β-C 3 N 4 to the generation by the microwave plasma of carbon-nitrogen radicals such as CN*. CN* is believed to be the key precursor leading to β-C 3 N 4 crystallization. Each of the CN* species can provide up to two unpaired electrons on the N side and up to 3 unpaired electrons on the C side, providing a strong tendency to bond CN* species together to form a lattice structure of β-C 3 N 4 . This deposition takes place at the lower end of a temperature gradient (600-1100°C). After deposition of a desired thickness, the high voltage of the microwave power is turned off. The gas flow is maintained until the reactor cools. After cooling, the gases are turned off, and the reactor is vented. The resulting films showed clear evidence for the crystallization of β-C 3 N 4 . FIG. 3 is a typical Rutherford backscattering spectroscopy (RBS) spectrum of the film. RUMP fitting shows a composition of 43% carbon, 54% nitrogen and 3% oxygen. FIG. 4 is a deconvoluted X-ray photoelectron spectroscopy (XPS) spectrum for carbon. It shows three C is features: the feature at 285.0 eV, interpreted as C-C, accounts for 16% of the C 1s intensity. The feature at 288.0 eV is attributed to the formation of C-N bonds and accounts for 67% of the C 1s intensity. The third feature at 289.7 eV probably reflects reaction with oxygen and accounts for 17% of the C 1s intensity. FIG. 5 is a deconvoluted XPS spectrum for nitrogen showing two features in the N 1s spectrum. The low energy feature at 398.6 eV is attributable to N 1 and accounts for 59% of the intensity. The higher energy feature at 400.5 eV attributable to N 2 accounts for 41% of the intensity. FIG. 6 is a cross section image of the film taken by transmission electron microscopy (TEM). An amorphous layer grows at the bottom and a crystalline layer grows at the top. The growth morphology is columnar, and the boundary is well-defined. FIG. 7 is a dark field TEM image of the same area shown in FIG. 6. FIG. 7 shows crystallization of the continuous top layer and discrete nano-crystals embedded in the amorphous layer grown on the bottom. FIG. 8 is the transmission electron diffraction pattern of the film. The cross-section and the plan-view electron diffraction data are listed in Table 1. Three peaks match closely to predicted β-C 3 N 4 lattice spacings: 2.78 angstroms corresponding to β-C 3 N 4 <200>; 1.96 angstroms corresponding to <111> and 1.49 angstroms corresponding to <301>. Cross-section (A) Plan-view (A) Calculated (A) <hkl> 3.21 3.215 110 2.80 2.784 200 2.53 2.53 2.46 001 2.06 2.11 2.104 210 1.99 1.953 111 1.86 1.84 1.856 300 1.54 1.54 1.544 310 1.49 1.481 301 1.39 1.392 400 1.323 1.308 311 1.283 1.278 1.278 320 1.229 1.230 002 1.209 1.211 401 1.147 1.149 112 1.133 1.134 321 1.112 1.114 500 1.089 0.089 1.089 411 1.056 1.052 420 0.834 0.838 521 0.809 0.808 332 Thus continuous crystalline films of β-C 3 N 4 have been synthesized on a substrate by microwave plasma reaction of graphite and nitrogen. A heterogeneous chemical reaction generates active carbon-nitrogen radicals such as CN*. These species act as precursors which lead to the subsequent crystallization. In this technique, no sputtering, ablation, or thermal dissociation of the graphite was involved. Precipitation of the carbon nitride compound is the result of quenching due to diffusion of the carbon-nitrogen radical precursors out of the plasma region. The unpaired electrons in the radicals tend to bond each species together to form crystals. The microwave plasma provides the generation of radical precursors at appropriate moderate temperatures (600-1100°C) to form β-C 3 N 4 . It is to be understood that the above-described embodiments are illustrative of only a few of the many possible specific embodiments which can represent applications of the principles of the invention. Numerous and varied other arrangements can be made by those skilled in the art without departing from the scope of the invention as defined in the claims.

Claims: Method of making a nitrogen and carbon-containing film (120) on a substrate (17), the method comprising depositing, in an evacuable chamber, carbon on the substrate in the presence of nitrogen, such that the nitrogen and carbon-containing film is formed on the substrate; CHARACTERISED IN THAT the method further comprises a) disposing the substrate (17) and a carbon member (13) in the evacuable chamber, with the carbon member being spaced from the substrate; b) introducing a flow of nitrogen and helium into the evacuable chamber; c) introducing microwave energy into the evacuable chamber such that said microwave energy produces a primary mode plasma (20) and a secondary mode plasma (21) spaced from the primary mode plasma, with the secondary mode plasma being proximate to the substrate, said plasma (20,21) heating said carbon to a temperature in the range 600 - 1100°C and generating carbon-nitrogen radicals, d) permitting said radicals to diffuse out of the plasma region and to crystallise on the substrate (17) as β-C 3 N 4 e) removing the substrate with the nitrogen and carbon-containing film from the evacuable chamber. Method of claim 1, wherein the carbon member is a graphite member., Method of claim 1, wherein the continuous crystalline film has approximate composition C 3 N 4 . Method of claim 3, wherein the continuous crystalline film consists substantially of β-C 3 N 4 .

Inventors: JENG GUANG-KAI DAVID, MITCHELL JAMES WINFIELD, JENG, GUANG-KAI DAVID, MITCHELL, JAMES WINFIELD
Applicants: AT & T CORP, AT&T IPM CORP.
Application year: 1996
Main classification: H01L21
IPC codes: C23C14, C23C16, H01L21, C01B21, C30B29