A PROCESS FOR MAKING GRAFT BLOCK COPOLYMERS BY GRAFTING ANIONIC POLYMER CHAINS ONTO FUNCTIONALIZED POLYOLEFINS

Abstract: A graft block copolymer is comprised of a saturated olefinic backbone with pendent anionic polymer side chains. The polymer is produced by copolymerizing an alpha -olefin with a 1-alkenyl monomer containing a functional group to which an anionically polymerized polymer can be grafted to produce graft block copolymer, anionically polymerizing at least one anionically polymerizable monomer to form living polymer chains, and then grafting the living polymer chains onto the copolymer to form the graft block copolymer.

Description: TITLE : A PROCESS FOR MAKING GRAFT BLOCK COPOLYMERS BY GRAFTING ANIONIC POLYMER CHAINS ONTO FUNCTIONALIZED POLYOLEFINS This invention relates to a method for making graft block copolymers and particularly to making saturated graft block co- polymers without a hydrogenation step. More particularly, the present invention is a process for making saturated graft block copolymers from polyvinyl aromatic hydrocarbons and functiona- lized polyolefins. Anionic polymerization utilizing organo alkali metal initiators has long been used to polymerize conjugated diolefins such as a butadiene and isoprene and to copolymerize such diolefins with styrene and substituted styrenes to make styrene-butadiene- styrene and styrene-isoprene-styrene linear block copolymers and similar linear block copolymers. This reaction is usually car¬ ried out in an inert hydrocarbon solvent such as cyclohexane or toluene and it is necessary to rigorously exclude oxygen, water or any impurity that can react with a highly reactive propagat¬ ing species. Under these conditions, the polymeric molecular weight and block structure can be precisely controlled. Such polymers contain a large amount of aliphatic unsaturation in the diene blocks. Since saturated polymers have certain advantages over unsaturated polymers, such as oxygen and heat stability, it has been desirable to hydrogenate the aliphatic unsaturation in the conjugated diene blocks and this has been accomplished using any of several hydrogenation processes known in the prior art. For instance, the commonly used method is to use a Group VIII metal, particularly nickel or cobalt, catalysts with a suitable reducing agent such as an aluminum alkyl to catalyze the hydro¬ genation of these polymers. Recently it has been found that bis- (cyclopentadienyl)titanium compounds can also be used in t hydrogenation of these polymers. Excellent saturated line block copolymers are the result of such processes. The disadvantage in the prior method of producing saturated li ear block copolymers is the need for the additional hydrogen tion and catalyst removal steps. These steps are equipment a time intensive and thereby increase the complexity and cost producing linear block copolymers. In addition, the hydrogen tion catalysts are sensitive to certain poisons making hydrog nation of polymers containing particular functional groups coupling agent residues difficult or impossible. It would highly advantageous to have a process by which saturated blo copolymers could be produced without the necessity of a hydrog nation step. The present invention provides such a process a also produces graft block copolymers with zero residu unsaturation. The saturated graft block copolymers of the pre ent invention differ from the saturated linear block copolyme of the prior method in the relative location of the compone polymer blocks as illustrated in the following formulae. S t g rrene-Buta d iene-Styrene Linear Block Copolymer O ctene-Styrene Gra f t Block Copolyβer The present invention provides a process of producing graft block copolymers which comprises: (a) copolymerizing an α-olefin with a 1-alkenyl monomer containing a functional group to which an anionic polymer can be grafted, preferably a silane, most preferably a chlorosilane or a hydridosilane, to produce a graft block copolymer, (b) anionically polymerizing at least one anionically polymerizable monomer to from living polymer chains, and (c) grafting the living polymer chains of (b) onto the copolymer of (a) to from an olefinic polymer having pendent anionic polymer side chains. The present invention also includes a graft block copolymer comprised of a saturated olefinic backbone with pendent anionic polymer side chains. The graft block copolymers of this invention may be thermo-plas- tic elastomers, tough impact resistant plastics, or stiff plas¬ tics. Thermoplastics elastomers can be formed from an amorphous polymer backbone and glassy or semicrystalline polymer pendent grafts which phase separate (through differences in solubility parameter or crystallinity) from the backbone to from a physi¬ cally crosslinked network which will be load supporting. When the product graft block copolymer is to be used in applications requiring substantial material strength, then it is preferred that the graft block copolymer contain, on average, at least two grafts. Tough, impact resistance plastics can be formed from an amorphous polymer backbone and glassy or semicrystalline pendent grafts when the weight fraction of the pendent graft is greater than about 0.50. In this case, the graft polymer phase will be the matrix and the amorphous polymer backbone must phase separ¬ ate and will be dispersed. Tough, impact resistant plastics can also be formed from a glassy or semicrystalline polymer backbon with phase-separated pendent amorphous polymer grafts. Stif plastic polymers can be formed from glassy or semicrystallin polymer backbones with glassy or semicrystalline polymer grafts which may exist in a single compatible phase or be phase separ ated. In a preferred embodiment, the α-olefin is C 2 to C 30 , the 1 alkenylhalosilane is dimethylhexenylchlorosilane, and the tw monomers are copolymerized in the presence of a transition meta catalyst. It is preferred that the anionically polymerizabl monomer be selected from the group consisting of vinyl aromati hydrocarbons, conjugated dienes, and mixtures thereof (such tha the living polymer chains can be random or block copolymers o the two different types of monomers) . The most preferred embodiment of the present invention involve making a saturated graft block copolymer without the necessit of a hydrogenation step. This can be done when the anionicall polymerizable monomer is a vinyl aromatic hydrocarbon, or, mor generally, contains a single olefinic moiety. Thus, polyviny aromatic hydrocarbon, preferably polystyrene, polymer sid chains may be grafted onto the saturated olefinic backbone t create a saturated graft block copolymer. The first step of this process involves copolymerizing an α olefin with a 1-alkenyl functionalized monomer to form a copo lymer which is intended to form the backbone of the graft bloc copolymer of the present invention. This polymerization step ma be carried out by using a Ziegler-Natta or metallocene catalys polymerization process or by using a cationic polymerizatio process. Other possible methods include free radical or Lewi acid catalyzed processes. In general, any α-olefin can be used in the practice of this invention but it is preferred that the α-olefin be a C 2 to C 30 olefin. The choice of α-olefin will depend on the intended application for the product graft block copolymer. If a soft, thermoplastic elastomer is desired, then the graft block copoly¬ mer will be composed of an amorphous polymer backbone and glassy or semicrystalline polymer grafts. In this case, it is preferred that the α-olefin be a C 4 to C 30 olefin or a mixture of C 2 to C 30 olefins. These olefins are preferred because they invariably produce amorphous materials with relatively low glass transition temperatures (T_) . When graft block copolymers are produced from these olefinic backbones and glassy or semicrystalline anionic polymer grafts as described above, the low T_ of the polyolefin provides for retention of elastomeric properties of the graft block copolymer down to low temperatures and a broad service temperature range. C 4 to C 16 α-olefins and mixtures thereof are preferred because they produce soft, tacky amorphous polymer. If a tough, impact resistant plastic is desired composed of an amorphous polymer backbone and glassy or semicrystalline polymer grafts in which the weight fraction of the grafts is greater than about 0.50, then an α-olefin that produces an amorphous polymer will again be chosen. It is preferred that the α-olefin be a C 4 to C 30 olefin or a mixture of C 2 to C 30 olefins because the low T_ of the product polymer will allow the graft block copolymer to retain ductile behaviour of the dispersed phase down to low temperatures and a broad service temperature range. If a tough, impact resistant plastic is desired composed of a glassy or semicrystalline polymer backbone and amorphous polymer grafts then α-olefins that produce a glassy or crystalline poly¬ mer will be chosen. In this case, it is preferred that the α- olefin be a C 2 to C 5 olefin. If a stiff plastic material desired then α-olefin that produce a glassy or semicrystalli polymer will be chosen. In this case, it is preferred that t α-olefin be a C 2 to C 5 olefin. There are many monomers which can be used to place "hooks" the backbone to which anionic polymers can be grafted. Specif cally included within the scope of this invention are monome of the formula R R R R CH 2 =CH-(CH 2 ) n - C I = CI — CI = CI — R where n>0 and where R may be alkyl or hydrogen and may be di ferent or the same. 1,3,7-octatriene is one example. Other pr ferred monomers are those having the formula CH 2 =CH-(CH 2 ) n -Y where n>0 and Y is selected from the group including halosila groups, hydridosilane groups, ester groups, aldehyde group ketones, halogens, epoxides, and phosphorous groups of the fo mula P-Z 2 where Z is Cl, Br, I, F, hydrogen, ester groups, combinations of these. The preferred 1-alkenylhalosilane compounds which can be used the present invention include H 2 C=CH-(CH 2 ) n -SiX 3 where n> X=halogen, R, H or combination thereof, R is alkyl or aryl a at least one X must be halogen. H 2 C=CH-CH 2 -SiMe 2 Cl is preferr because when the presence of ungrafted anionic polymer in t final product is undesirable this halosilane may easily removed from the backbone copolymer due to its high volatility Also preferred for the same reason are hydridosilane compoun of the formula CH2=CH-(CH 2 ) n -SiH 2 R y where n>0 , x+y=3 , x>l , and y>0. Most preferred compounds have these structures : CH 2 =CH-CH 2 -SiH 3 , CH 2 =CH-SiH 3 , CH 2 =CH-SiH 2 CH 3 , and CH 2 =CH-CH 2 -SiH 2 CH 3 . In the last two structures halogen may take the place of H, in which case the silanes would be halosilanes. Methods for carrying out the copolymerization of the α- olefin and the 1-alkenyl functionalized monomer include the use of metallocene and Ziegler-Natta catalysis as well as cationic polymerization. Metallocenes catalysts are organometallic coordination compounds obtained as a cyclopentadienyl derivative of a transitional metal or metal halide. Their use in the polymerization of olefins in well known. A useful Ziegler-Natta catalysis process is described in U.S. Patent 5,045,597 which is herein incorporated by reference. The Ziegler-Natta method of polymerization requires the presence of a catalyst which includes a transition metal compound and which also utilizes an aluminium compound as well as an electron donor. Such transition metal compounds include titanium halides such as titanium trichloride and titanium tetrachloride as well as magnesium chloride supported titanium tetrachloride, mag¬ nesium alkoxide supported titanium tetrachloride and certain metallocenes of zirconium, titanium, and hafnium which are known from the art to polymerize α-olefins. The aluminum compound is usually an organo aluminum compound which is preferably selected from the group consisting of trialkyl aluminum, dialkyl aluminum halides, alkyl aluminum sesquihalides and alkyl aluminum dihali- des, and aluminoxanes. There are a wide variety of electron donors which can be used and they are usually oxygen or nitrogen containing compounds such as ethers, esters, alkoxy-silicon com¬ pounds, orthoethers, heterocyclic aromatic nitrogen compounds. The Ziegler-Natta polymerization may be conduced in neat mono¬ mer, solvent polymerization, or vapour phase polymerization. Generally, polymerization is conduced at a temperature of from 30 β C to 100°C under a pressure of from atmospheric to the vapour pressure of the 1-alkenyl functionalized monomer at the polymerization temperature and optionally in the presence of a molecular weight control agent such as hydrogen. If a soft, thermoplastic elastomer or a tough, impact resistant plastic composed of an amorphous polymer backbone and glassy or semicrystalline polymer grafts as described above is desired, then it is important that the catalyst which is chosen is one which tends to produce amorphous polymers. Such catalysts are described in U.S. Patent 5,122,494, 5,188,767, 5,089,573, 5,118,768, 4,874,737, 4,971,936, and 5,229,477, which are all herein incorporated by reference. A preferred catalyst is described in U.S Patent 5,122,494. The catalyst is formed by contacting, in the presence of an inert diluent, an alkyl aluminum halide halogenating agent with a complex magnesium-con¬ taining, titanium-containing alkoxide compound prepared by reac¬ tion of magnesium alkoxide, titanium tetra-alkoxide and phenolic compound. The complex alkoxide compounds are of somewhat vari able stoichiometry but have the general illustrative formula Mg 3 Ti(OR) 8 X 2 wherein R independently is alkyl of up to four carbon atoms in¬ clusive and X independently is a monovalent anion derived from a phenolic compound as described below. The diluent is the removed to produce, as a particulate solid, the complex alkoxide compound. This solid is treated with alkyl aluminium halide t produce the olefin polymerization catalyst. The preferred alkoxides are magnesium ethoxide and titanium tetra ethoxide. The phenolic compound is selected from phenol or an activated phenol (a monohydroxilic phenol of one aromatic ring having aromatic ring substituents other than hydrogen which serve to alter the pKa of the phenolic compound) . Suitable phenolic compounds are phenol, o-cresol, and 2, 6-di-t-butyl-4- methylphenol (BHT) . The α-olefin and the functionalized monomer may be cationically polymerized by reacting them in the presence of a cationic polymerization initiator in the presence of a Lewis acid and, generally, an electron donor. The Lewis acid and the electron donor may be complexed together. Lewis acids which can be util¬ ized herein include metal halides, such as aluminium trichloride (and molten salts containing aluminium trichloride) , boron tri¬ chloride, boron trifluoride and titanium tetrachloride, and organometallic derivatives, such as ethylaluminumdichloride and triethyl aluminium, and oxyhalides, such as phosphorous oxychlo- ride. Electron donors which are useful herein include alkyl ami¬ nes, pyridines, such as 2,6-lutidine and 2,4, 6-collidine, tri- aryl or trialkyl phosphines, benzaldehyde, and veratrole. The cationic polymerization initiators are generally taken from the group consisting of tertiary alkyl halides such as t-butylchlo- ride and triphenylmethylfluoride. The preferred Lewis acids are aluminium trichloride and boron trichloride because of their higher activity. The preferred electron donors are 2,6-lutidine and collidine because they have been shown to give random copolymers and highly amorphous poly¬ mers, respectively (U.S. 5,134,209 and U.S. 5,229,477). The pre¬ ferred cationic polymerization initiators are cumyl-type deriva- tives like cumylchloride, alkoxide, or aliphatic tertiary chlor ides. The cationic polymerization may be a batch, semi-continuous, o a continuous process. Generally, the polymerization is carrie out at a temperature of from about -100 to about 0°C under pressure of from 0 to 10 atm. Another method for copolymerizin the α-olefins and the functionalized monomers is free radica polymerizations. The α-olefin/functionalized monomer copolymers are used in th present invention as precursors to making the graft bloc copolymers of the present invention. These copolymers are gen erally characterized in that they are high molecular weigh copolymers with a random distribution of the monomer components The halosilane groups of these copolymers may also be derivati zed to other functional groups by reaction with appropriat reagents such as H 2 0, alcohols, metal hydrides, and the like They have other uses as modifiers for polyolefins, such a polypropylene, polyethylene and polybutylene, as a way to incor porate impact resistance and/or polarity into these polymers o blends of these polymers. The halosilanes may be homopolymerize to form high molecular weight polymers by the above processes a well. Such halosilane homopolymers are characterized in tha they may have high melting points and may exhibit crystallinit because of chain end tacticity control. These homopolymers ar useful for polymer derivatization reactions such as mentione above for the copolymers to produce engineering thermoplastic or modifiers for engineering thermoplastics. Any anionically polymerizable monomer should be effective i this invention. Particular monomers which can be used includ acryla ides, acrylonitriles, vinylisocyanate, anhydrides, nitro butene, methacrylates, including methyl methacrylate, alkyl and aryl acrylates, vinylpyridines, carbodiimides, lactones, dienes, lactams, styrene and styrene derivatives including alkylstyre- nes, halogenated methoxy styrenes and nitrostyrene, as well as 1,3-pentadiene and 1,3-octadiene, cyclic siloxanes, ethylene. The anionically polymerized polymers, included herein include polyethers (polyalkylene oxides, polyfurans, etc.) , polyesters, polyacetals, and polyphenylene oxide (PPO and PPE) . Also useful herein are acrylic monomers, especially including those with the structure H,C= C — C — O — R, 2 I II 2 R λ 0 where R α is hydrogen, phenyl or an alkyl radical which is linear or branched and has from 1 to 10 carbon atoms and R 2 is an alkyl radical which has from 1 to 14 carbon atoms, may contain a ter¬ tiary amine or an ether linkage, and may be a cyclic hydrocar¬ bon. More specifically, polymer chains which may be used accord¬ ing to the present invention are polymer chains which include acrylic monomers of the formula described above such as alkyl methacrylates or derivatives of alkyl methacrylates such as hydrolysed alkyl methacrylates or anhydride derivatives thereof. Other suitable acrylic monomers include acrylates, such as t- butylacrylate, cyclic alkyl methacrylates, such as 2, 5-dimethyl- cyclohexyl methacrylate, and acrylates in which the alkyl group contains an ether linkage, such as tetrahydrofuran aerylate. As is well known, polymers containing both aromatic and/or ethylenic unsaturation can be prepared by copolymerizing one or more polyolefinis, particularly a diolefin, by themselves or with one or more alkenyl aromatic hydrocarbon monomers. The copolymers may, of course, be random, tapered, block, star, radial or a combination of these. When the double bonds in th polyolefin are separated by three or more carbon atoms, th ethylenic unsaturation incorporated into the polymer will b contained in a branch extending outwardly from the main polyme chain but when the polyolefin is conjugated at least a portio of the ethylenic unsaturation incorporated into the polymer ma be contained in the polymer backbone. As is well known polymers containing ethylenic unsaturation o both aromatic and ethylenic unsaturation may be prepared wit anionic initiators or polymerization catalysts. Such polymer may be prepared using bulk, solution or emulsion techniques. In general, when solution anionic techniques are used anionically polymerizable polymers including conjugated diolefi polymers, alkenil aromatic hydrocarbons, and copolymers of con jugated diolefins and alkenyl aromatic hydrocarbons are prepare by contacting the monomer or monomers to be polymerized simulta neously or sequentially with an anionic polymerization initi ator. Such initiators include Group IA metals, their alkyls amides, silanolates, naphtalides, biphenyls and anthraceny derivatives. It is preferred to use an organoalkali metal com pounds in a suitable solvent at a temperature within the rang from about -150°C to about 300°C, preferably at a temperatur within the range from about 0°C to about 100°C. Particularl effective anionic polymerization initiators are organolithiu compounds having the general formula: RLi n wherein R is an aliphatic, cycloaliphatic, aromatic or alkyl substituted aromatic hydrocarbon radical having from 1 to abou 20 carbon atoms; and n is an integer of 1 to 4. Conjugated diolefins which may be polymerized anionically include those conjugated diolefins containing from 4 to about 12 carbon atoms such as 1, 3-butadiene, isoprene, piperylene,methyl- pentadiene, phenylbutadiene, 3 ,4-dimethyl-l,3-hexadiene, 4,5- diethyl-l,3-octadiene and the like. Conjugated diolefins con¬ taining from 4 to about 8 carbon atoms are preferred for use in such polymers. Alkenyl aromatic hydrocarbons which may be copo- lymerized include vinyl aryl compounds such as styrene, various alkyl-substituted styrenes, alkoxy-substituted styrenes, 2-vinyl pyridine, 4-vinyl pyridine, vinyl naphthalene, alkyl-substituted vinyl naphthalenes and the like. In general any of the solvents known in the prior art to be use¬ ful in the preparation of such polymers may be used. Suitable solvents then, include straight- and branched-chain hydrocarbons such as pentane, hexane, heptane, octane and the like as well as alkyl-substituted derivatives thereof; cycloaliphatic hydrocar¬ bons such as cyclopentane, cyclohexane, cycloheptane and the like, as well as alkyl-substituted derivatives thereof; aromatic and alkyl-substituted derivatives thereof; aromatic and alkyl- substituted aromatic hydrocarbons such as benzene, naphtalene, toluene, xylene and the like; hydrogenated aromatic hydrocarbons such as tetralin, decalin and the like; linear and cyclic ethers such as methyl ether, methyl ethyl ether, diethyl ether, tetra- hydrofuran and the like; ketones such as methylketone (acetone) , methyl ethyl ketone, ethyl ketone (3-pentanone) and the like. The polymerization of the anionically polymerized monomers is not ended by the addition of chain terminating agents such as alcohols or hydrogen. It is very important that living anioni¬ cally polymerized polymer chains remain to be reacted with the copolymer in the third step of the process of the present inven- tion. By living polymer chains it is meant that the polymeriza tion initiator is still part of the polymer chain and is activ and available for further polymerization if more monomer become available. In this case, the polymerization is ended when th monomer supply is exhausted. For example, when polystyrene i polymerized and an organo lithium compound is used as the initi ator, the living polymer chain can be represented as: PS~Li + This is known as polystyryl lithium. The most preferred embodiment of the present invention is saturated graft block copolymer produced without the necessit for a hydrogenation step. Saturated graft block copolymers ar produced herein when the anionically polymerized monomer is on which contains a single carbon-carbon double bond. Examples ar vinyl aromatic hydrocarbons, particularly styrene and substi tuted styrenes, methacrylates, particularly t-butylmethylacryla te, vinylpyridines, and ethylene. When these monomers are util ized in the second step of the process of the present invention, the result is a saturated graft block copolymer. The final step of the process is accomplished by grafting th living polymer chains onto the copolymer. For halosilanes, thi takes place by replacement of a halogen attached to the silico with the living polymer chain. This is accomplished by reactin the two polymers in the presence of an activator such a tetramethylethylendiamine or ethers such as glyme, o-dimeth oxybenzene, or ethylenglycoldiethylether, at a temperature of 3 to 100°C and a pressure of 1 to 10 atm. This step also can b carried out in the absence of activators but it proceeds mor slowly to completion. The copolymerization of the α-olefin and the 1-alkenyl fun- ctionalized monomer produces a polymer with a saturated olefinic backbone having pendent saturated alkyl chains with a functional group attached thereto which may be a terminal group or which may be in the internal portion of the chain. In the case of halosilanes, such copolymers may be represented by the follow¬ ing: The living polymer chains react with these copolymers at the silicon trichloride sites and the polymer chain actually takes the place of a chloride on the silicon trichloride group in the polymer so that it becomes part of a pendent side chain. In the case of a polystyryl lithium living polymer, the above copolymer is converted to a saturated graft block copolymer with the fol¬ lowing formula: When the appropriate backbone polymer, graft polymer and weight fraction of graft polymer are chosen, the polymers of the pres¬ ent invention are excellent thermoplastic elastomers.For example block graft copolymers as exemplified in the above formula with a polystyrene weight fraction from about 0.05 to about 0.50 have dispersed polystyrene domains in an amorphous, rubbery matrix. These materials exhibit high elongation under tensile stress with nearly complete recovery after the stress is removed. Once deformed, the material may be moulded by the application of heat and pressure or cast from an appropriate solvent. The original properties of the material are then once again obtained. Other thermoplastic elastomers within the scope of the invention are those with other types of polymeric grafts which are glassy or semicrystalline and phase separate from the backbone polymer forming a dispersed phase. These include block copolymer grafts, such as polystyrene-b-polybutadiene or polystyrene-b-polyisopre- ne, t-butyl-methacrylate grafts, polyvinylpyridine grafts, poly- phenylene ether grafts, polyethylene grafts, and the like. When a thermoplastics elastomer with substantial strength is desired, it is important to control the number of pendent anionic polymer side chains. If there are, on average, less than 2 side chains per backbone polymer, then the resulting graft block copolymer will have low strength.The number of side chains is controlled by the composition of the backbone copolymer and the ratio of graft and backbone polymer chains. It is highl preferred that the graft block copolymer contains, on average, from 2 to 200 pendent anionic polymer side chains per backbone polymer so long as these pendent groups do not exceed 50% b.w. of the total composition. This is preferred because when th graft block copolymers contain greater than 50%w anionic polymer side chains, the glassy or semicrystalline graft polymer becomes the matrix with dispersed amorphous backbone polymer and th resulting graft block copolymer is no longer elastomeric, bu will behave like a toughened plastic. The polymers made according to the present invention have a extremely wide variety of uses. Elastomeric graft block copo lymers may be used in all of the applications for which othe thermoplastic elastomers have been used. For example other ther¬ moplastic elastomers are useful in adhesives, sealants, coating, polymer modification (blending with other thermoplastic polymers such as polyolefins, polycarbonate, polyphenyloxide, etc. to enhance or alter the properties thereof) , polymer blend compati- bilization, tie layers, asphalt modification, viscosity index improvers and the like. Block graft copolymers which are tough, impact resistant plastics or stiff plastics may be used in moulded and extruded goods, fibers, films, polymer modification, polymer blend compatibilization and tie layers. The polymers may also be crosslinked to provide additional strength and environ¬ mental, chemical, and thermal resistance. Examples Example l 1.72 grams (7 millimoles) of 7-octenyltrichlorosilane and 14.4 grams (103 millimoles) of 1-decene were polymerized at 65°C for approximately 16 hours in a sealed glass reactor under a nitrogen atmosphere. The polymerization was carried out in the presence of 40 milligrams of Mg 6 (OCH 2 CH 3 ) iQ ^TiCl^salicylaldehy- de) ! 5 catalyst containing 5% or 2 milligrams of titanium and 88 milligrams of ethylaluminumdichlorides as a 25% solution in toluene (0.7 mmoles of aluminum) and 60 milligrams of triethyla- luminum as a 25% solution in toluene (0.53 mmoles aluminum) which contain a total of 1.23 mmoles of aluminum. Therefore, the aluminum:titanium ratio was about 31:1. The copolymer produced was then dissolved in toluene at 10% solids. Next, polystyrene was polymerized by placing 16 grams of styrene and 32 grams of cyclohexane in a nitrogen purged glass reactor and adding 11 mmoles of sec-butyl lithium. The reaction was initiated at room temperature and then the temperature was increased to 50°C for 30 minutes to polymerize styrene. The rea ction was not terminated so the resulting product was a livin polystyryllithium polymer chain with a molecular weight of 130 g/mole. The living polystyryllithium polymer was added to th solution of the copolymer in toluene along with 9.5 mmoles o dioxo(diethoxyethane) . The reaction was allowed to take plac until the orange color of the living polystyrene polymer disap peared (30 min. at 70°C) and then 14 mmoles of butyllithium wa added to the reaction mixture for the purpose of deactivatin the remaining Si-Cl bonds. Then the reaction mixture was heate at 80°C for 1 hour and terminated with isopropyl alcohol (IPA) . The polymer cement was coagulated with isopropyl alcohol an dried under high vacuum for two hours at 75°C. Then it wa redissolved in isooctane (to leave behind ungrafted poly styrene) . The cement was then centrifuged and part of th supernatant solution was again coagulated with isopropyl alco hol, dried, and analyzed. GPC analysis showed the presence o ungrafted homopolystyrene in the product, so further purifica tion was performed as described below. The product was redissolved in toluene and the resultin solution was then carefully coagulated by adding isopropyl alco hol dropwise until the rubber precipitated. GPC analysis of th dried rubber showed that all of the ungrafted homopolystyren had been removed in this manner. GPC analysis also showed tha the product graft block copolymer has a UN absorption due to th grafted polystyrene (the copolymer backbone itself does no absorb in the ultraviolet region of the GPC detector) . GPC ana lysis of the crude reaction mixture showed two ungrafted homo polystyrene peaks at 1300 and 2700 g/mole (in a ratio of abou 1:2) which are derived, respectively, from reaction of 1 and living polystyrene polymers with a 7-octenyltrichlorosilane mol¬ ecule which was not incorporated into the backbone copolymer. Due to the nature of the synthesis, the grafted polystyrene must also have a molecular weight of 1300 g/mole. It may also be as¬ sumed that polystyrene grafts in a similar manner to 7-octenyl- trichlorosilane which is incorporated into the copolymer such that one-third of the SiCl 3 groups contain 1 polystyrene graft and two-thirds contain 2 polystyrene grafts. The total bound polystyrene content as determined by NMR analysis 37% by weight. Example 2 The procedure and reactants in this example were the same as in Example 1. The only differences are in the amounts of the reac¬ tants used. 0.89 grams (3.6 mmoles) of 7-octenyltrichlorosilane and 21.8 grams (156 mmoles) of 1-decene were used. The polymerization was carried out in the presence of 40 milligrams of Mg 6 (OCH 2 CH 3 ) 10 . 5 - TiCl 4 (salicylaldehyde) 1>5 catalyst containing 5% or 2 milligrams of titanium and 95 milligrams of ethylaluminumdichloride as a 25% solution in toluene (0.75 mmoles aluminum) and 65 milligrams of triethylaluminum as a 25% solution in toluene (0.57 mmoles aluminum) which contained a total of 1.32 mmoles of aluminum. Therefore, the aluminum:titanium ratio was about 33:1. 22.7 g of styrene in 50 grams of cyclohexane was reacted in the presence of 9.3 mmoles of sec-butyl lithium. The resulting polystyryl lithium molecular weight was 2000 g/mole by GPC analysis. When the two polymers were combined as in Example 1 they were reacted in the presence of 9 mmoles of dioxo and 3 mmoles of butyl lith¬ ium were used to deactivate the Si-Cl bonds. The total bound polystyrene content of the product graft block copolymer as de- termined by NMR analysis is 33% weight, after removal o ungrafted homopolystyrene as described in Example l. Example 3 The procedure used in this example is the same as Example except for the amounts of the reactants and that the olefin use in the first step was l-octene. The catalyst was 40 milligram Mg 6 (OCH 2 CH 3 ) 10 TiCl 4 (benzaldehyde) 2 containing about 5% Ti and 6 mg of ethylaluminumdichloride as a 25% solution in toluene (0.4 mmoles) and 40 mg of triethylaluminum as a 25% solution i toluene (0.35 mmoles). Therefore the Al:Ti ratio was about 20:1 In the first step, 70 grams (625 mmoles) of l-octene wer polymerized with 1 gram (4.06 mmoles) of 7-octenyltrichlorosila ne. The polymerization was carried out at 75°C and held over night at 80°C to insure complete reaction. In the second step, grams of styrene were dissolved in 27 grams of cyclohexane an reacted in the presence of l.l mmoles of sec-butyl lithium an heated at 50°C for one hour. The resulting polystyryl lithiu molecular weight was 8600 g/mole by GPC analysis. The copolymer and the polystyryl lithium were added together an heated at 80°C until the orange color disappeared. Most of th color faded within several minutes. The reaction was carried ou for 15 minutes followed by the addition of 7 mmoles of sec-buty lithium to deactivate any remaining Si-Cl groups. The polyme was coagulated with acetone to remove ungrafted polystyrene. NM analysis gave a bound polystyrene content of 6% weight. Aceton coagulation proved to be a very effective method of removin ungrafted homopolystyrene (86% effective in this case) . Thi method of purification was used for all subsequent examples an was very convenient as well as effective. Example 4 The procedure used in this example is the same as Example 1 except for the amounts of reactants and that the olefins used in the first step were l-octene and 5-hexenyldimethylchlorosilane. 160 mg of Mg 6 (OCH 2 CH 3 ) 10 TiCl 4 (benzaldehyde) 2 catalyst was used, containing about 5.5% Ti and 239 mg of ethylaluminumdichloride as a 25% solution in toluene (1.88 mmoles) and 160 mg of triet- hylaluminum as a 25% solution in toluene (1.4 mmoles). Theref¬ ore, the Al:Ti ratio was about 20:1. In the first step, 280 grams (2.5 moles) of l-octene were polymerized with 4 grams (18.4 mmoles) of 5-hexenyldimethyl- chlorosilane. The polymerization was carried out at 75°C and held overnight at 80°C to insure complete reaction. In the sec¬ ond step, 2 mmoles of 500 molecular weight high vinyl polybuta- diene was prepared by anionic polymerization in cyclohexane con¬ taining 1000 ppm of dioxo as modifier. Following polymerization of the butadiene, sufficient styrene monomer was added to polymerize a 7000 molecular weight polystyrene block. To the living polybutadiene-polystyrene block polymer was added 150 g of a solution containing 11% by weight of the poly(l-octene) -co- hexenyldimethylchlorosilane prepared as described above. The po¬ lymers were reacted at 70°C for 30 minutes, followed by the addition of 3 mmoles of s-butyllithium to deactivate any remain¬ ing Si-Cl groups. The reagents were allowed to react at 80°C for 1 hour. The reaction was terminated by addition of 1 ml of iso- propanol. The graft polymer was recovered by precipitation into acetone to remove any ungrafted polybutadiene-polystyrene block copolymer, which is expected to be highly soluble in acetone due to the very high polystyrene content (96% by wt.). NMR of the final product showed a polystyrene content of 24% weight, a 1,2- butadiene content of about 1% weight, and a 1,4-butadiene con- tent of less than 1% weight. The cast film had an ultimate ten sile strength of 574 psi, an ultimate elogenation of 382%, and tensile set after break of 38%. The Tg's observed by dynamic me chanical thermal analysis are -38°C for the polyoctene backbon and 116°C for the polystyrene grafts. Example 5 The backbone octene/5-hexenyldimethylchlorosilane copolymer wa prepared as described in Example 4. In the second step, 10 gram of styrene in 50 grams of cyclohexane was polymerized with mmoles of sec-butyllithium for 30 minutes at 50°C to obtain 2000 g/mole polystyrene polymer. Then 30 grams of a 15% b.w. so lution of 4-vinyl-N,N'-diethylbenzylamine in cyclohexane (4,5 of 4-vinyl-N,N'-diethylbenzylamine) was added along with 100 ppm dioxo. The 4-vinyl-N,N'-diethylbenzylamine was polymerize at 50 β C for 15 minutes. After polymerization 1 ml of styrene wa added to cap the living polymer chain for more efficient coupl ing with the Si-Cl groups of the copolymer. The living copolyme was added to 140 g of the solution of the backbone copolyme prepared in Example 4 (about 15 grams of copolymer) and reacte at 80°C for 60 minutes. 5 mmoles of sec-butyllithium was the added to deactivate any remaining Si-Cl bonds and reagents wer allowed to react at 80°C for 15 minutes. The polymer was termin ated with methanol and coagulated from acetone to remove any un grafted polystyrene-b-poly(4-vinyl-N,N'-diethylbenzylamine) . Th polymer was redissolved in toluene and recoagulated from aceton to insure complete removal of ungrafted anionic polymer. Afte washing with methanol and drying under vacuum the polymer wa analyzed by elemental analysis for nitrogen and show to hav about 3 percent by weihgt functionalized aminostyrene monome incorporated as pendent block. The graft block copolymer wa dissolved in toluene and a film was cast for property studies. The cast film had an ultimate tensile strength of 261 psi, an ultimate elongation of 1455% and a tensile set after break of 158%. A Tg of -33°C was observed by dynamic mechanical thermal analysis for the polyoctene backbone. The Tg of the polystyrene- b-poly(4-vinyl-N,N'-diethylbenzylamine) was not detected. Example 6-33 A number of polymers were made with different rubber backbones and functional α-olefins as described in Table 1, below. The physical properties of selected graft block copolymers are given in Table 2, below. Type and wt. % of total unfunctionalized α-olefin added to polymerize graft block copolymer back bone. Type and percent mole of functional α-olefin added to polymerize graft block copolymer backbone. Determined by Gel Permeation Chromatography on crude reaction mixture after formation of the gra block copolymer. Values reported are the weight average molecular weight determined for unreacte homopolystyrene which must be equivalent to the weight average molecular weight of the polystyren grafts of the graft block copolymer due to the nature of the synthesis. Determined by H NMR analysis on product graft block copolymer. Type and wt. % of total unfunctionalized α-olefin added to polymerize graft block copolymer back¬ bone. Type and percent mole of functional α-olefin added to polymerize graft block copolymer backbone. Determined by Gel Permeation Chromatography of crude reaction mixture after formation of the graft block copolymer. Values reported are the weight average molecular weight determined for unreacted homopolystyrene which must be equivalent to the weight average molecular weight of the polystyrene grafts of the graft block copolymer due to the nature of the synthesis. Determined by H NMR analysis on product graft block copolymer. b. Test performed on a Instron Model 4505 using dumbbell shaped specimens with a 1 inch gauge lengt c. Percentage increase on specimen length measured 10 minutes after speciment breakage. d. Sample showed two peaks in the tan delta curve e. Polystyrene transition not detected. f. Test not performed on this sample. The data in Table 2 show that the graft block copolymers of this invention composed of amorphous backbone polymers and glassy polymer grafts in an amount of less than 50% of the total poly¬ mer composition show elastomeric tensile behaviour with high ultimate elongations and good recovery. Examples 27, 28, and 29 containing 51-52% by weight glassy polystyrene grafts do not exhibit elastomeric tensile behaviour. Instead, the samples show plastic-like behaviour indicative of a continuous glassy poly¬ styrene phase and a dispersed amorphous polyolefin phase. Example 34 (2-vinylpyridine example) The backbone polyoctene-co-5-hexenyltrichlorosilane polymer was prepared as described in Example 4. 50 g of this solution (5.4 g of functionalized copolymer) was charged to a reactor bottle.In a separate bottle 12 g styrene in 36 g cyclohexane was polymerized at 50°C for 30 min. with 10 mmoles s-buLi (PS~Li + MW =1200) . To this was added 2 g 2-vinylpyridine (2-VP) which was allowed to polymerize 10 min. @ 50°C to give PS-P-2VP'Li + (P-2VP MW=200) . The solution was then added to the functionalized copo¬ lymer solution along with 1000 ppm ethyleneglycoldiethylether and reacted at 70°C for 1 hour, then terminated with methanol, coagulated with acetone, and dried. Nitrogen elemental analysis showed the polymer product to contain about 1.1% b.w. 2-VP. Example 35 The graft block copolymer prepared in Example 15 was compounded with polystyrene, polypropylene, mineral oil, and stabilizers to produce an elastomeric molding compound as described below. The blend formulation is as follows: Table 3. Blend Formulation Ingredient %w Ex. 15 Graft Block Copolymer 36.941 Mineral Oil (a) 36.941 Polypropylene (b) 18.471 Polystyrene (c) 7.388 Irganox 1010 (d) 0.074 DLTDP (e) 0.185 a. Penreco 4434. White Mineral Oil. b. PP 5820. Huntsman Chemical Corp. c. Piccotex 125. Hercules. d. Tetrakis(methylene(3,5-Di-tert-butyl-4-hydroxyhydrocinnamate)methane. e. Dilaurylthiodipropionate. Antioxidant/stabilizer from American Cyanamid. The oil was first dispersed onto the graft block copolymer which was then dry blended with the other ingredients. The blend was prepared on a Custom Scientific Instruments melt mixer with a 5cm 3 capacity. Mixing was performed at 200°C for 4 min. at 150 rpm. The resulting elastomeric compounds was compression molded into a plaque of approximately 0.017 in thickness for physical property testing. The compression moulded plaque had an ultimate tensile strength of 405 psi, an ultimate elongation of 225%, a tensile set after break of 27%, and a Shore A hardness (stacked samples) of 47. These properties show that a soft, strong, elastomeric compound can be prepared from the block graft copolymers of this invention. Such compounds would be useful in a variety of moulded goods applications. Example 36 The graft block copolymer prepared in Example 4 was cast into a two films (approximate thickness of 0.01 and 0.02 inch) from toluene. The films were crosslinked by exposure to electron beam irradiation. The crosslinked polymer films were then tested for % volume swell in toluene (after approximately 16 hrs) and stress/strain properties. These results, compared to a polymer film before crosslinking are given in Table 4. Table 4 Polymer Film Electron Beam Ultimate Tensile Ultimate Tensile % Toluene Thickness (inch) Crosslinkine Conditions Strength (psi). Elongation (%). Gel, 0.02 none 540 ±22 386± 12 0 0.02 5 Megarads. 170 kvolts 574 ±22 401 ±31 45 0.01 8 Megarads, 165 kvolts 436 ±67 250± 17 100 a. Values reported are the mean S.D. of at least three independent measurements. b. Values reported are the percentage of the original film weight retained after approximately 16 hrs of Immersion in toluene at ambient temperatures. The data in Table 4 shows that the graft block copolymers of this invention can be effectively crosslinked by electron beam irradiation leading to materials with improved environmental and chemical resistance. The following experiments were carried out to demonstrate the superiority and different character of the polymers of the pres¬ ent invention compared to polymers in the prior art. EPDM (Nordel 1320) has about 4% unsaturation from 1,4-hexadiene corao- nomer of which 2.7% is "out-of-chain" and 1.3 is "in-chain".Upon lithiation at allylic positions, the "out-of-chain" olefin can be lithiated either at the terminal carbon (type A) or at the internal carbon (type B) . The "in-chain" olefin will be lithiat¬ ed to give type C. Upon growing the styrene block, one gets PS grafts located in 3 distinct locations (again, types A, B, or C) . Upon ozonolysis (cleavage of the residual olefin) , the fate of the 3 PS graft types and of the EPDM itself is as follows. Type A and C grafts will be cleaved by 0 3 thus resulting in loss of strength (backbone cleavage) . Only type B will survive ozonolysis. However, there are 1.3% "in-chain" olefins, most of which are not grafted sites. These too will undergo scissio with 0 3 resulting in severe backbone degradation. Since the sys tem of the present invention have zero residual unsaturation they show superior resistance to 0 3 . Example 37 (Comparative Example 1 similar to Example 14 U.S 4,761,456) EPDM (Nordel 1320) in cyclohexane at 8.7% solids was lithiate for 3 hours at 10°C with s-buLi/TMEDA (0.9:1 mmoles ratio). The styrene monomer was added (target MW=3600) and polymerized a 50°C for 30 minutes. The reaction was then terminated with meth anol, coagulated into 3 volumes of acetone, dried, and analyzed PS MW=5400; polystyrene content=31% b.w. in EPDM-g-PS produc (about 60% grafted and 40% homopolystyrene resulting from incom plete lithiation of EPDM) . A 0.2% wt. solution of this copolyme in carbon disulfide was treated with an ozone/gas stream at 80°C for 5 minutes and then purged with N 2 gas until the blu color of ozone disappeared. It was warmed to room temperatur and several grams of triphenylphosphine were added to decompos any reactive oxidation products. The product was analyzed by ge permeation chromatography (GPC) and before ozonolysis, shows strong EPDM-PS peak at about 15 minutes retention time and smaller peak of residual homopolystyrene at about 21-22 minute retention time. After ozonolysis, the GPC shows severe degrada tion of the EPDM-g-PS peak and a large increase in th homopolystyrene peak at 22 minutes retention time. From pea areas, it was determined that 93% of the grafted PS blocks wer cleaved in the ozonolysis experiment and this account for th large increase in the homopolystyrene peak. Thus, only 7% of th grafted PS survived the ozonolysis experiment. This will resul in almost complete loss of properties. Example 38 (Comparative Example 2-present invention) The polymer (from Example 18) whose elastomeric block is composed of a copolymer of 1-hexene and allydimethylchlorosilane and which contains 31% b.w. grafted PS (MW=6000) was ozonolyzed as described in Example 37 for EPDM-g-PS and the GPC's were com¬ pared for this material both before and after ozonolysis. Unlike the EPDM-g-PS example, there was no evidence of degradation of the invention polymer after ozonolysis. From the peak areas it was determined that 100% of the polymer survived the ozone expe¬ riment (0% degradation) . Thus, the superior stability of these materials over EPDM-g-PS has been demonstrated. Similar improve¬ ments in thermal and UN stability can also be expected. Example 39 (1,3,7-octatriene comonomer in ZΝ polymers: potential initiation and grafting sites for PAO-g-PS block copolymers) . Polystyrene was grafted onto a polyoctene backbone containing about 1 mole % 1,3,7-octatriene in which a significant fraction of the monomer had residual pendent diene moieties along the polyalpha-olefin (PAO) chain. Polystyryl lithium was synthesized separately and added to the PAO cement under nitrogen. The grafting reaction was allowed to proceed for 30 min. The polymer was terminated with methanol, coagulated from acetone, and dried in vacuo. The results are show in Table 5. a. Grafting reaction performed at 50 C C. b. Grafting reaction performed at 60 C C in the presence of 1000 ppm ethyleneglycoldiethylether. c. Polystyrene graft molecular weight from GPC. d. Polystyrene content (% by weight) from H NMR

Claims: CLAIMS 1. A process for producing graft block copolymers comprising: (a) copolymerizing an α-olefin with a 1-alkenyl monomer containing a functional group to which an anionic polymer can be grafted to produce a graft block copolymer, (b) anionically polymerizing at least one anionically polymerizable monomer to form living polymer chains, and (c) grafting the living polymer chains of (b) onto the copolymer of (a) to form a graft block copolymer hav¬ ing a satur-ated olefinic backbone with pendent anionic polymer side chains. 2. A graft block copolymer made according to the process of claim 1. 3. The graft block copolymer of claim 2 wherein the anionical¬ ly polymerizable monomer is selected from the group consisting of acrylamides, acrylonitriles, nitrobutene, vinylisocyanate, anhydrides, methacrylates, including methyl methacrylate, alkyl and aryl aerylate, vinyl pyridines, carbodiimides, styrene and styrene derivatives including alkylstyrenes, halogenated methoxy styrene and nitrostyrene, lactones, lactams, dienes, as well as 1,3- pentadiene, 1, 3-octadiene, cyclic siloxanes, and ethylene. 4. The graft block copolymer of claim 2 wherein the living polymer chains are polyether, polyalkylene oxides, polyfurans, polyesters, polyacetals, or polyphenyleneoxide. 5. The graft block copolymer of claim 2 wherein the anionic polymer side chains are completely saturated. 6. The graft block copolymer of claim 5 wherein th anionically polymerizable monomer is styrene. 7. The graft block copolymer of claim 2 wherein the 1-alkeny functionalized monomer is selected from the group consist ing of monomers of the formula CH 2 =CH-(CH 2 ) n Y where n>0 and Y is selected from: halosilane groups, hydridosilane groups, ester groups, aldehyde groups, ketones, halogens, epoxides, and phosphorous groups of th formula P-Z 2 where Z is Cl, Br, I, F, hydrogen, este groups, or combinations thereof. 8. The graft copolymer of claim 7 wherein The 1-alkeny functionalized monomer is a halosilane of the formula CH 2 =CH-(CH 2 ) n -SiX 3 where n>0, X is halogen, R or H, or combinations thereof, and R is alkyl or aryl, and at least one X must be halogen. 9. The graft copolymer of claim 8 wherein the silane i dimethylhexenylchlorosilane. 10. The graft block copolymer of claim 7 wherein the 1-alkeny functionalized monomer is a hydride of silane of the for mula CH 2 =CH-(CH 2 ) n -SiH χ R y where n>0, x>l, y>0, x+y = 3, and R is alkyl or aryl. 11. The graft block copolymer of claim 10 wherein the silane i selected from the group consisting of CH 2 =CH-CH 2 -SiH 3 CH 2 =CH-SiH 3 , CH 2 =CH-SiH 2 CH 3 , and CH 2 =CH-CH 2 -SiH 2 CH 3 . 12. The graft copolymer of claim 2 wherein the 1-alkeny functionalized monomer is of the formula R R R R I I I I CH 2 =CH-(CH 2 ) n C = C — C = C — R where n>0 and where R may be alkyl or hydrogen and may be different or the same. 13. The graft block copolymer of claim 12 wherein the 1-alkenyl functionalized monomer is 1,3,7-octatriene. 14. A crosslinked product comprising the graft block copolymer of claim 2 which has been either chemically or radiation crosslinked. 15. A crosslinked product comprising the graft block copolymer of claim 7 which has been either chemically or radiation crosslinked. 16. Blends of the graft block copolymer of claim 2 and other thermoplastic polymers. 17. Blends of the graft block copolymer of claim 7 and other thermoplastic polymers. 18. The graft block copolymer of claim 2 which is comprised of an amorphous polyolefin backbone and phase-separated glassy or semicrystalline anionically polymerized grafts which comprise 50 percent or less of the total polymer composi¬ tion. 19. The graft block copolymer of claim 2 which is comprised of an amorphous polyolefin backbone and continuous glassy anionically polymerized grafts which comprise more than 50 percent of the total polymer composition.

Inventors: DUBOIS DONN ANTHONY, HOXMEIER RONALD JAMES, JOB ROBERT CHARLES, SPENCE BRIDGET ANN, DUBOIS, DONN, ANTHONY, HOXMEIER, RONALD, JAMES, JOB, ROBERT, CHARLES, SPENCE, BRIDGET, ANN
Applicants: MONTELL TECHNOLOGY COMPANY BV, MONTELL TECHNOLOGY COMPANY B.V.
Application year: 1996
Main classification: C08F299
IPC codes: C08F299, C08G81, C08L87, C08L101