A PROCESS FOR PREPARING MESOPOROUS CRYSTALLINE MATERIAL

Abstract: The present invention relates to a process for preparing mesoporous crystalline material, in particular to a novel process for preparing crystalline material having mesoporous structure by dissolving silica in hydrogen fluoride solution and reacting it on the condition of atmosphere and room temperature for a short reaction time. As the result, the present invention provides a process to use all kinds of silica and to synthesize mesoporous material for a short reaction time.

Description: A PROCESS FOR PREPARING MESOPOROUS CRYSTALLINE MATERIAL BACKGROUND OF THE INVENTION 5 Field of the Invention The present invention relates to a process for preparing mesoporous crystalline material, in particular to a novel process for preparing crystalline material having mesoporous structure by dissolving silica in hydrogen fluoride solution and reacting it on the condition of atmosphere and room l o temperature for a short reaction time. As the result, the present invention provides a process to use all kinds of silica and to synthesize mesoporous crystalline material for a short reaction time. Description of the Prior Art 15 Porous inorganic materials have found great utility as catalysts or separation media for industrial application. The opening of their microstructure allows molecules to access to the relatively large surface areas of these materials that enhance their catalytic and sorptive activity when reaction occurs. 0 The porous materials in use today can be sorted into the broad categories using the details of their microstructure as a basis for classification. These categories are the amorphous support, crystalline molecular sieves and modified layered structures to intercalate small fragments like metal oxide. The microstructure of these materials shows the detailed differences 5 and due to said differences, their specific selectivity is manifested in the catalytic and sorptive behavior. Further, the above difference are ascertained in terms of their surface area, the size of pores and the variability in those size and X-ray diffraction patterns. The microstructure appearance of the materials is also shown through transmission electron microscopy. Generally since amorphous silica or alumina support forms the pore resulting from voids between particles, they don't have uniform pore size and show the pore size of wide range of 13—200 A • 5 In contrast to these structurely ill-defined materials, the solids of regular crystallinity like zeolite have very narrow pore size distribution. The majority of natural or synthetic zeolites have the pore of limited size and mesoporous zeolites having uniform distribution of ZSM series were synthesized in an effort to enlarge the pore size. i o In addition, for using the layered silica and metal phosphate compounds including natural or synthetic clays, the synthesis of fine porous materials was attempted. The pore size distribution is regular compared to amorphous support but irregular compared to crystalline support like zeolite. 1 5 Recently, novel mesoporous crystalline materials were successfully synthesized by Mobil Co. Their pore size can be controlled uniformly in the regime of 20 ~ 100 A . It was named as MCM-41 and U.S. Pat. No. 5,108,725; 5,102,643; 5,098,684 and 5,057,296 describe synthesizing process, reactants for synthesis, composition, physical and structural property. 20 In the above mentioned prior arts, they demonstrated synthesizing process for preparing mesoporous crystalline materials by using tetraammonium hydroxides like tetramethyl ammoniumsilicate solution as well as surfactant in an autoclave at a temperature of 100— 150 * £ for 2~ 7days. The reaction principle of this process is attracting silica or silica 25 allumina crystal on the micelle colloid surface having charge, which is formed by dissolution of surfactant molecules in water. Ignition may form bond and crosslink with the bridge of oxygen between Al and Si in the molecular dimension. To satisfy said circumstance, a large amount of tetraammonium hydroxides is used and reaction condition is controlled at high temperature and high pressure for 2—7 days. Materials prepared by said process have not only uniform pore size but also remarkable thermal property and large surface area of 500—1000 5 m 2 /g. The constituents of framework consist of Si0 2 and Si0 2 /Al 2 0 3 . In view of remarkable physical properties, these new materials will replace the conventional zeolites and be widely used in the future. Silica is hydrolyzed with the form of hydoxide anion in strong i o aqueous alkali solution and dissolved. Formed silicon hydroxides anion at this very moment make wall of pore by forming network by means of silly bonding because polymerization occurs on the micelle colloid surface having positive charge if miscelle colloid of cationic surfactant exits. Generally the solubility of silica largely depends on the kind of alkali, 15 particle size of silica, density, temperature and pressure. Alkali-metal hydroxides is largely used in synthesizing of crystalline silicate but its use is not preferred because a large amount of impurities such as saltstNa-βC NaCl) can be deposited during the neutralization process when used in synthesis of MCM-41. 0 If bulk density of silica is sufficiently low and particle size is sufficiently small, the large quantity of silica may be dissolved comparatively in the organic base such as tetramethyl ammonium hydroxides. But these procedures have disadvantages that the kind of usable silica is limited and particular condition of high temperature, high pressure and long period time 5 is required. Moreover, tetramethyl amonium hydroxides is expensive and decomposed to amine and alcohol at high temperature and it is technically and economically difficult to manufacture and operate reaction apparatus of high temperature and pressure. In said process, a large amount of tetra ammonium hydroxides of high price are used and it is not economical. And there are additional disadvantages in the process that reaction ought to be carried at high 5 temperature and high pressure for a long time as well as disadvantage that only raw material of silica, for example highsil, ultrasil or fumed silica, which are voluminous and easy to fly is used to facilitate dissolution. Accordingly, in order to solve the above mentioned problems, inventors have made effort to manufacture more economically and in a short i o time the crystalline materials having conventional mesoporous structure named MCM-41 by using all kinds of silica. And finally, we have developed a novel process for preparing mesoporus crystalline materials by using hydrogen fluoride solution with all kinds of silica for a few hours at a temperature range of 25— 80 ϊ. 1 5 SUMMARY OF THE INVENTION An object of the present invention is to provide a novel process that prepare mesoporous crystalline materials for a short time in the condition of room temperature and atmosphere. 20 Description of the drawings Fig. 1 is a X-ray diffraction pattern diagram of the final product of the present invention from Example 1, Fig. 2 is a X-ray diffraction pattern diagram of the final product of the present invention from Example 2, 25 Fig. 3 is a X-ray diffraction pattern diagram of the final product of the present invention from Example 3, Fig. 4 is a X-ray diffraction pattern diagram of the final product of the present invention from Example 4, Fig. 5 is a X-ray diffraction pattern diagram of the final product of the present invention from Example 5, Fig. 6 is a X-ray diffraction pattern diagram of the final product of the present invention from Example 6. 5 DETAILED DESCRIPTION OF THE INVENTION The crystalline materials having mesoporous structure of this invention are prepared by the following steps of a) dissolving 2-10 part by weight of silica only or a mixture of metal ι o salts or metal alkoxide in 100 part by weight of 5-50% hydrogen fluoride solution, b) adding said solution to the solution of 2-10 part by weight of cationic surfactant and 20-30 part by weight of cone, ammonia solution in 100 part by weight of distilled water 1 5 c) aging at a temperature of 25-80 lc for 2-3 hours, and d) calcining at a temperature of 500-800 τ for 4-6 hours. The present invention is described in more detail by the following. The present invention relates to a novel process for preparing mesoporous crystalline materials having uniform pore size and remarkable 20 thermal property. Through the use of hydrogen fluoride solution as silica solvent, the present invention has advantages that all kinds of silica are used freely as well as that a large amount of silica can be dissolved under room temperature and atmosphere for a short time. Synthetic principle comprises dissolving silica 25 with the form of H j SiF,, in hydrogen fluoride solution and forming SiF 6 2" in alkalic solution of cationic surfactant for a moment and SiF 6 2 is crystallized with the form of SiO z by hydrolysis condensation polymerization on the micelle surface of cationic surfactant. This synthetic steps can be considered as a remarkable improvement of conventional reaction process because it is achieved at room temperature and atmosphere for a short time. Synthetic process of the present invention is described in more detail by the following. 5 First, 100 part by weight of hydrogen fluoride solution having 5— 50% concentration is sampled and 2 — 10 part by weight of silica only or the mixture of metal salts and metal alkoxide is dissolved in the above solution. Wherein, if the concentration of hydrogen fluoride solution is less than 5%, the solubility of silica is so low that sufficient amount of silica can't be l o dissolved, if more than 50%, it has adverse effects of increasing ammonia consumption on the precipitation process as well as wasting hydrogen fluoride solution unnecessarily. In the present invention, all kinds of available silica can be used without limit of particle size, compared to fine particle used in the 1 5 conventional process such as highsil, ultrasil and silica used for tetramethyl ammonium silicate. And metal salts can be used such as A1(N0 3 ) 3 , Al(S0 4 )j, AlCl j or NaA10 2 and metal alkoxide, such as titanium(IV) alkoxide, aluminium alkoxide or silicon alkoxide. The above mentioned silica mixed with small amount of metal salts or metal alkoxide, or 2 — 10 part by 20 weight of silica only to 100 part by weight of hydrogen fluoride solution is dissolved, in order to prepare silica-hydrogen fluoride solution(H 2 SiF 6 ). The more silica component is dissolved, the more it is advantageous. Apart from the above mentioned process, after 2 — 10 part by weight of cationic surfactant to 100 part by distilled water is dissolved, and then 20— 25 30 part by weight of cone, ammonia solution is added and stirred. Wherein, alkyltrimethylammonium salts having hydrocarbon chain of more than 10 carbon atom can be used as cationic surfactant. The representing surfactant of them is cetyltrimethylammonium bromide or cetyltrimethylammonium chloride. If the additive quantity of said surfactant is less than 2 part by weight to 100 part by weight of distilled water, the formation of desired micelle template becomes difficult. If more than 10 part by weight, the formation of micelle template of the layered lamella 5 type is possible, which is not sphere or cylinder type. Also, when final product is washed, economic loss and environmental pollution are caused due to a large quantity outflow of remaining surfactant. Said silica dissolved by hydrogen fluoride solution is added to cationic surfactant at a time and stirred, and then is aged at 25—80x for 2—3 hrs. When aging l o temperature deviate the above range, it is not preferred due to complexity in apparatus design and operation management because it is reacted in the autoclave. The aged material is filtered and its precipitate is collected, and then washed. The mesoporous crystalline material of the present invention is prepared by calcining at a temperature of 500— 800 ; for 4 —6 hrs. 15 Mesoporous crystalline material prepared in said process has Si0 2 structure only or structure replaced Si site by a portion of Al or Ti, wherein the molar ratio of Si/Al or Si/Ti was more than 10. X-ray powder diffraction data to sample prepared in said process were collected using an automated diffraction system(Rigaku Co., Japan) with 0 Ni-filtered Cu K« radiation operating at 15 mA and 35 kV. Relative intensity was measured at rotation angle(20 ) of 1.5—20° with the count range of 5000 cps. And, after nitrogen adsorption isotherms were obtained at liquid nitrogen temperarure(77K), the measurement of surface area was calculated by 5 analyzing the value of the adsorption at 5—1 OOtorr of nitrogen through the BET(Brunauer Emmett Teller) formula. Micrometies ASAP 2000 was used as adsorption apparatus. After all the samples were evacuated at vacuum and 300 T for 4 hrs, N 2 adsorption experiment was carried out. The distribution of pore size was calculated through BJH(Barret Joyner Halenda) formula. According to X-ray diffraction analysis and surface area measurement, d- spacing is in the the range of 35— 45 A - And it shows the same aspect 5 with MCM-41 of crystalline materials having conventional mesoporous structure and the shape of pore showed regularly hexagonal arrangement like a nest of hornets. The surface area of materials was 800—1000 n /g and the pore size was distributed at the range of 35-40° intensively. As the above mentioned description, the synthetic process of the i o present invention includes various kinds of silica available and the preparation of crystalline materials of mesoporous structure of conventional MCM-41 series having remarkable thermal property and large surface area without using tetraammonium hydroxide. The following examples serve to illustrate the present invention, such 15 examples given for the purpose of illustration and not for purposes of limiting the present invention. EXAMPLE 1 lOOg of 24% hydrogen fluoride solution was loaded into the polyethylene beaker and 3g of silica(White carbon, OCI) was dissolved 20 completely in the solution. lOOg of distilled water was loaded in the another beaker and 4g of cetyltrimethylammonium bromide was dissolved, and then was stirred vigorously at 50 Tj for 10 mins., adding 25g of cone, aqueous ammonia solution. The prepared silica in hydrogen fluoride solution was added to this solution at a time. The resulting mixture was stirred for 10 25 mins. carefully, and then was aged at temperature of 30 T for 2—3 hours. The product was filtered, precipitated and washed several times with distilled water. Dried powder was calcined at a temperature of 600 TJ for 4 hours. The X-ray diffraction pattern of calcined product was identical with that illustrated in Fig. 1 and showed 40.8° units d-spacing with relatively strong intensity. This pattern has been found to characteristic peak of MCM-4 . The pore observed by transmission electron microscopy(TEM) showed 5 the regularly hexagonal arrangement like nest of hornet. The surface area obtained from BET formula was 880 mVg and pore size was distributed in the 35 A intensively. EXAMPLE 2 The procedure of this example is similar to that of example 1. The i o difference resides in the fact that lOOg of 24% hydrogen fluoride solution was loaded in the polyethylene beaker and 3g of silica was dissolved completely in the solution, and then to this solution is added 0.5g of A1(N0 3 ) 3 9H 2 0. The crystal obtained from this example showed structure having Si framework replaced by a portion of Al, wherein the ratio of Si/Al was 40. 1 5 And the X-ray diffraction pattern of the calcined product of this example was shown in Fig. 2. Characteristic peak of MCM-41 is shown in this figure and it was noted that relatively strong intensity is 46.8 A d-spacing. The calcined product of this example proved to have a surface area of 900 mVg and pore size distribution of 38 A • 0 EXAMPLE 3 This example is identical with the above example 2 except using 0.86g of A1(S0 4 ) 3 18H 2 0 instead of A1(N0 3 ) 3 9H 2 0. The crystal obtained from this example showed structure having Si framework replaced by a portion of Al, wherein the molar ratio of Si/Al was 37. 5 The X-ray diffraction pattern of the calcined product of this invention is shown in Fig. 3 and was consistent with the characteristic peak of MCM- 41. The calcined product of this invention proved to have 43.0 A d-spacing, a surface area of 1,000 irf/g and pore size distribution of 36 A - EXAMPLE 4 Except using 0.47g of A1C1 3 6H 2 0 instead of A1(N0 3 ) 3 9^0, this example is identical with example 2, wherein the ratio of Si/Al was 40. X- 5 ray diffraction pattern of the crystal obtained from example 4 is shown in Fig. 4 and was consistent with the characteristic peak of MCM-41. The calcined product of this example proved to have 43.0 A d-spacing, a surface area of 980 nf/g and pore size distribution of 36 A. EXAMPLE 5 l o Except using O.lg of NaA10 2 instead of A1(N0 3 ) 3 9H 2 0, this example is identical with the above example 2, wherein the ratio of Si/Al was 41. X-ray diffraction pattern of the crystal obtained from this example is shown in Fig. 5 and was consistent with the characteristic peak of MCM-41. The calcined product of this example proved to have a 45.6 A i 5 d-spacing, a surface area of 950 rrf/g and pore size distribution of 37 A • EXAMPLE 6 100 g of 24% hydrogen fluoride solution was loaded in polyethylene beaker and 3 g of silica was dissolved completely in the solution, and then dissolved uniformly by adding 0.38g of titanium(IV) alkoxide in addition. 20 The following experiment steps are carried out as those of the above example 1 with the same manner. The crystal obtained from this example showed structure having Si framework replaced by a portion of Ti wherein, the ratio of Si/Ti was 37. And, X-ray diffraction pattern of the calcined product is shown in Fig. 25 6 and was consistent with the characteristic peak of MCM-41. The calcined product of this example proved to have 41.2 A d-spacing, a surface area of 1000 nf/g and pore size distribution of 35 A.

Claims: WHAT IS CLAIMED IS : 1. A process for preparing crystalline materials having mesoporous structure characterized by comprising the following steps of 5 a) dissolving 2-10 part by weight of silica only or a mixture of metal salts or metal alkoxide in 100 part by weight of 5-50% hydrogen fluoride solution, b) adding said solution to the solution of 2-10 part by weight of cationic surfactant and 20-30 part by weight of cone, ammonia ι 0 solution in 100 part by weight of distilled water, c) aging at a temperature of 25-80 T for 2-3 hours, and d) calcining at a temperature of 500-800 T for 4-6 hours. 15 2. The process in claim 1, wherein said metal salts are selected from the group consisting of A^NO^, A1(S0 4 ) V A1C1 3 and NaAlG,. 3. The process in claim 1, wherein said metal alkoxide is selected from the group consisting of titanium(IV) alkoxide, aluminium alkoxide and 0 silicon alkoxide. 4. The process in claim 1, wherein said cationic surfactant is cetyltrimethylammonium bromide or cetyltrimetylammonium chloride. 5 5. The process in claim 1, wherein crystalline materials having mesoporous structure prepared by said process have that the molar ratio of Si/Ti or Si/Al is more than 10.

Inventors: JEONG SOON-YONG, JIN HANG-KYO, KWON OH YUN, LEE JUNG-MIN, SUH JEONG-KWON, JEONG, SOON-YONG, JIN, HANG-KYO, KWON, OH, YUN, LEE, JUNG-MIN, SUH, JEONG-KWON
Applicants: JEONG SOON YONG, JIN HANG KYO, KOREA RES INST CHEM TECH, KWON OH YUN, LEE JUNG MIN, SUH JEONG KWON, JEONG, SOON-YONG, JIN, HANG-KYO, KOREA RESEARCH INSTITUTE OF CHEMICAL TECHNOLOGY, KWON, OH, YUN, LEE, JUNG-MIN, SUH, JEONG-KWON
Application year: 1996
Main classification: C01B33
IPC codes: B01J29, C01B33, C01B37, C01B39, C03B8, C03C10, C03C11