CLEANING COMPOSITION

Abstract: Cleaning composition for use in removing ink comprising 65-90 % by weight of an aliphatic hydrocarbon solvent, 10-30 % by weight of a monohydric aliphatic alcohol containing 8-16 carbon atoms and 0.01-5 % by weight of emulsifier, which composition has a flash point of more than 80 DEG C, and contains at most 1 % by weight of aromatic hydrocarbons.

Description: CLEANING COMPOSITION The present invention relates to cleaning composi¬ tions for use in removing ink, more specifically in removing ink from printing machines. In the off-set industry it is very important that ink can be removed quickly and thoroughly from the printing surface without harming the metal or rubber components of the apparatus. Further, there is a tendency to require that the cleaning compositions are environmentally friendly in that they contain no or hardly any aromatic compounds, volatile organic compounds and/or halogen containing compounds. A further trend is to require that the compositions fulfil strict safety regulations. In the present applicant's non-prepublished WO 95/18843 a cleaner composition is disclosed, comprising one or more aliphatic hydrocarbon solvents, from 2-40 wt% of one or more monohydric alcohols and/or polyhydric alcohols, and optionally up to 30 wt% of one or more glycol ethers and/or esters, the composition having a flash point of 50-80 °C and containing at most 1 wt% of aromatic hydrocarbons. In order to fulfil the safety regulations, it is preferred that the compositions have a flash point of more than 80 °C, more preferably a flash point of 90 °C or more. This makes them very safe for transportation, storage and use. A composition has now been found which gives a good performance in that ink is readily removed while the above requirements are met. The present invention relates to cleaning composi- tions for use in removing ink, comprising, based on the total composition: a) 65-90% by weight of an aliphatic hydrocarbon solvent, b) 10-30% by weight of a monohydric aliphatic alcohol containing 8-16 carbon atoms, and c) 0.01-5% by weight of an emulsifier, which composition has a flash point of more than 80 °C and contains at most 1% by weight of aromatic hydrocarbons. In Derwent Publications Ltd. , London, GB, AN 93-164790, a detergent composition has been described containing (A) 100 parts by weight of a hydrogenated kerosene fraction, (B) 0-40 parts by weight of one or more of a monohydric alcohol, ether, ester, ethoxylated alcohol and aprotic polar solvents, (C) 0.1-20 parts by weight of a surfactant, which is preferably nonionic (D) 0.001-5 parts by weight of an enzyme and (E) water. The composition is described to be effective against fats and oils, greases, rosin type fluxes and proteins. The present invention differs from the composition described in AN 93-164790, in that the composition of the present invention has a flash point of more than 80 °C. Furthermore, the composition of the present invention does not harm the metal or rubber components of the printing machine. Esters and ethers tend to give a strong rubber swell while aprotic solvents tend to be too aggressive. Further, the present composition is especially suitable for removing ink. During drying, ink will generally polymerise to form a network. The surfactant properties necessary for removing such network are different from the surfactant properties for removing fats and oils, greases, rosin type fluxes and proteins. In view of the safety regulations, the flash point of the composition is to be more than 80 °C, preferably 90 °C or more. More preferably, the flash point is between 100 and 200 °C, most preferably between 100 and 150 °C. The flash point is to be measured according to ASTM D 93. A preferred aliphatic hydrocarbon solvent has a boiling range of 175 to 350 °C, and contains at most 0.5% by weight of aromatic hydrocarbons based on the total amount of hydrocarbon compounds of the solvent. More preferably, the aliphatic hydrocarbon solvent contains at most 0.3% by weight of aromatic hydrocarbons and has a boiling range of between 200 to 300 °C. Due to the substantial absence of aromatic hydrocarbons, the solvent will primarily consist of paraffins, isoparaffins and naphthenes. For greater dissolving power, it is preferred that the solvent comprises at least 34% by weight of naphthenes, more preferably at least 45%. The aromatic content is to be measured with the help of the ultra¬ violet test method described in SMS 2728 (SMS methods are issued by Shell Internationale Research Maatschappij BV, The Hague, the Netherlands) . The boiling point range is to be determined with the help of the test method described in ASTM D86. An aliphatic solvent which can be used in the present invention is "SHELLSOL D90" , having a typical initial boiling point of 220 °C, an end boiling point of 275 °C, a flash point of 95 °C and containing less than 0.2% by weight of aromatic compounds. Another solvent which is most preferred to be used is "SHELLSOL D100", having a typical initial boiling point of 240 °C, an end boiling point of 270 °C, a flash point of 105 °C and containing less than 0.2% by weight of aromatic compounds. (SHELLSOL is a trademark.) Kerosene fractions are not suitable in view of their relatively high aromatic content. Preferably, the monohydric alcohol is an alkanol or alkenol of 8 to 16 carbon atoms. A monohydric alcohol with less than 8 carbon atoms is likely to lower the flash point of the composition too much. Further, alcohols containing more than 16 carbon atoms tend to be too viscous for use in the present composition. It was found that poly-alcohols tend to lead to phase separation of the components of the composition, which makes them less suitable. A specific monohydric alcohol which can be used in the present invention is a mixture of nonanol, decanol and undecanol, which is commercially available under the trademark "DOBANOL 91", and/or a mixture of dodecanol and tridecanol, which is commercially available under the trademark "DOBANOL 23". (DOBANOL is a trademark.) "DOBANOL 91" has a flash point of 107 °C and "DOBANOL 23" has a flash point of 132 °C. Due to the flash point requirement, low molecular weight alcohols such as ethanol, iso-propanol and tertiary butanol are not suitable as the monohydric alcohol component for use in the present invention. In principle, the emulsifier to be used in the present invention can be any commercial package sold for making polar and apolar compounds miscible, while not disturbing the ink dissolving power of compounds a) and b) or harming the metal or rubber components of the printing apparatus. It has been found that emulsifiers fulfilling these requirements can comprise a polyoxy- ethylene glycol ester of a carboxylic acid which carboxylic acid contains between 15 and 25 carbon atoms and/or an alkanol amide. A preferred polyoxyethylene glycol ester comprises between 2 and 5 oxyethylene units and as the carboxylic acid an unsaturated acid containing between 15 and 20 carbon atoms, e.g. oleic acid. The alkanol amide preferably is a dialkanol amide of which the alkanol units comprise between 1 and 6 carbon atoms, and the acyl moiety comprises between 2 and 30 carbon atoms, preferably between 5 and 25 carbon atoms. A preferred alkanol amide is diethanol amide of which the acyl moiety comprises between 5 and 25 carbon atoms. Commercially available emulsifiers which are suitable for use in the present invention are "MARLOWET MA" (MARLOWET MA is a trademark) which can be obtained from Huels, DOBANOL 91-8 and DOBANOL 25-3. The ratio of the amount of compound a) to the amount of compound b) influences the ink removal properties of the composition. It has been found that good results are obtained if compound a) is present in an amount of 65-90% by weight, while compound b) is present in an amount of 10-30% by weight. Preferably, the ratio of compound a) to compound b) is between 90:10 and 60:40, more preferably between 85:15 and 65:35. Especially good results have been obtained with a composition containing the compounds in a ratio of between 78:22 and 82:18. Preferably, the cleaning composition according to the present invention also contains as component d) a corrosion inhibitor, in an amount of 0.01-1% by weight based on the total composition. The corrosion inhibitor, when present, should be miscible with the cleaning composition but better soluble in water. Suitable as such are sodium- and potassium-2-ethyl hexanoate. The composition of the present invention is to be used for removing ink from printing machines, more specifically from off-set printing machines. The use of the composition comprises treating the printing surface with the cleaning composition, e.g. by brushing or wiping the surface with a cloth treated with the composition, followed by rinsing the treated surface to remove the remaining composition. Usually, the surface will be rinsed with water. Rinsing after treating the surface with the composition, is necessary in view of the high flash point which can only be attained with liquids of limited volatility. By rinsing with water, a mixture of the cleaning composition and water is obtained. If this mixture is left for between 0.5 and 3 hours, the liquids separate and the separated cleaning composition can be re-used after distillation and subsequent addition of a suitable amount of emulsifier. The invention is illustrated by the following examples. Examples A. Materials The ink used in the examples is an offset rotation ink marketed by Premier Holland (22.200) . In offset printers nitrylbutadiene rubber (NBR) is commonly used as material for the blanket sheet on the printing cylinders and for the cover of the inkrollers. Accordingly, the influence of the cleaner composition (rubber swell) was tested on the following NBR types: NBR, No. 17925, blankets offset; Shore A hardness 25, Bδttcher NBR, No. 39935, rotation offset; Shore A hardness 35, Bδttcher - NBR, ink roll obtained from the firm Heidelberg For the cleaning tests, aluminium foil was used as the underground. B. Determination of rubber swell (adapted ASTM 471-79) The method for the determination of rubber swell is based on the measurement of the solvent uptake or "absorption" in a rubber specimen after a fixed immersion time. The volume change is obtained by weighing the specimen in air and water before and after immersion. A rubber test specimen of 1 x 1.5 cm 2 , weighing approx. 1.0 g, was immersed in alcohol and dried with filter paper to remove dirt. Next, the specimen was weighed at room temperature in air (Ml) and in distilled water (M2) . Then, the specimen was quickly immersed in alcohol, dried with compressed air and placed in a 30 ml weighing bottle with 25 ml test medium. This bottle was placed in an air conditioned room at 23 °C and 50% relative humidity for 25 hours, following which the specimen was removed from the solvent, quickly immersed in alcohol, dried with compressed air, placed in a tared stoppered weighing bottle and weighed (M3) . After weighing in air, the specimen was removed from the bottle and weighed in distilled water at room temperature (M4) to determine the water displacement after immersion. Each of the steps from removal of the specimen from the test medium to stoppering the weighing bottle and from removal from the weighing bottle to immersion in water took no more than 30 seconds. Any air bubbles clinging to the test specimen were removed before weighing in distilled water. Formulas for determining rubber swell: Change in volume (%) = ( (M3 - M4) - (Ml - M2))/ (Ml - M2) x 100 Change in mass (%) = (M3 - Ml) /Ml x 100 C, Ink cleaning test The testing of the cleaning performance of solvents and solvent blends is based on the dissolution of a film of dried ink. This film was dried for fixed time intervals. The method applied is semi-static, i.e., the amount of external energy applied into the solubility/cleaning process is as low as possible. A strip of aluminium foil (10 x 50 cm 2 ) was thoroughly cleaned with successively xylene and 2- butanone and dried. Next, a film of ink was applied with a 100 micrometer applicator resulting in a dry film with a thickness of about 50 micrometer. After a fixed drying time (2/6 hours, 1/3/7 days) at 23 °C and 50% relative humidity, a small strip (approximately 0.75 x 2 cm 2 ) of ink-coated aluminium foil was cut from the centre of the film and put in a 7 ml vial containing approximately 3 ml of cleaner composition. After 1 day on a slowly revolving rollerbank, the aluminium foil was removed from the solvent and carefully dried by dabbing with a tissue pad. The cleaning efficiency of the cleaner composition was evaluated by the appearance of the treated aluminium foil. The appearance of the solvent was evaluated after 1 day of sedimentation. The cleaning efficiency was rated as follows: 1: no effect 2: soft film of ink 3 : very soft film of ink 4: very soft film of ink and minor part of film of ink removed 5: very soft film of ink and major part of film of ink removed 6: film of ink totally removed 7-9: further ranking on residual blue colour. Results A range of cleaner compositions have been tested, the results of which have been summarised in the table. In Comparative Example 1 "SHEET CLEANER" (SHEET CLEANER is a trademark) was used, obtained from Smeets. The product is based on aromatic hydrocarbon solvents and volatile alcohols. In Comparative Example 2 a composition was used, containing 77% by weight of "SHELLSOL D60", an aliphatic hydrocarbon solvent having a boiling range between 187 and 211 °C and a flash point (measured according to ASTM D93) of 66 °C, 9% by weight of 2-methyl-2,4- pentanediol and 14% of a mixture of 2,6-dimethyl-4- heptanol and 4,6-dimethyl-2-heptanol. This composition is according to WO 95/18843. In Example 3 a composition according to the present invention was used, containing 79.5% by weight of "SHELLSOL D100", an aliphatic hydrocarbon solvent having a boiling range between 240 and 270 °C and a flash point, measured according to ASTM D93, of 105 °C, 20% by weight of "DOBANOL 91", containing primary alcohols having between 9 and 11 carbon atoms, and 0.5% by weight of "MARLOWET MA", containing a mixture of a polyoxyethylene glycol ester based on oleic acid and comprising between 2 and 5 oxyethylene units and a diethanol amide of a fatty acid. The composition has a flash point, measured according to ASTM D93, of 105 °C. In Comparative Example 4 a composition consisting of "SHELLSOL D100" was used. The results are summarised in the following Table 1. Table 1 Examples 1-4 Example 1 2 3 4 (comp. ) (comp. ) (comp. ) Flash point 12^) 63 105 105 (°C) Cleaning efficiency after x hours/days drying of the film of Premier offset printing ink Rating of cleaning efficiency 2 hours 7 9 9 4 6 hours 7 9 9 4 1 day 8 8 9 3 3 days 8 8 7 3 7 days 5 6 6 3 rubber swell % volume NBR 17925 33 7 0.8 *) NBR 39935 28 5 0.5 *) NBR Ink Rol 31 7 0 *) a) : This flash point has been calculated. *) : Not measured. It will be clear from the above results that the composition according the present invention (Example 3) is highly efficient at removing ink, while having a high flash point which makes it suitable for safe storage, transport and use, and that it causes very little rubber swell. Example 5 Compositions were tested containing differing amounts of "SHELLSOL D100" and "DOBANOL 91" and further containing 0.5% by weight of "MARLOWET MA". These compositions were tested as described in Example 1. Drying was carried out for 1 day. The weight ratios and cleaning efficiencies obtained, are shown in Table 2. Example 5 SHELLSOL D100" :' "DOBANOL 91" cleaning efficiency 100:0 2 90:10 5 b) 80:20 9 70:30 9 60:40 9 50:50 9 c) 25:75 5 0:100 3 b) : although initially there was a high cleaning efficiency, there also was redeposition. c) : slow

Claims: A I M S 1. Cleaning composition for use in removing ink, comprising, based on the total composition: a) 65-90% by weight of an aliphatic hydrocarbon solvent, b) 10-30% by weight of a monohydric aliphatic alcohol containing 8-16 carbon atoms, and c) 0.01-5% by weight of emulsifier, which composition has a flash point of more than 80 °C, contains at most 1% by weight of aromatic hydrocarbons . 2. Composition according to claim 1, wherein the aliphatic hydrocarbon solvent of the composition has a boiling range of between 200 and 300 °C and contains at most 0.3% by weight of aromatic hydrocarbons. 3. Composition according to claim 1 or 2, which composition has a flash point of 100 °C or more. 4. Composition according to claim 3, which has a flash point of between 100 and 150 °C. 5. Composition according to any one of claims 1-4, which composition comprises as emulsifier a polyoxyethylene glycol ester of a carboxylic acid which carboxylic acid contains between 15 and 25 carbon atoms and/or an alkanol amide. 6. Composition according to any one of claims 1-5, in which composition the weight ratio of amount of component a) to amount of component b) is between 90:10 and 60:40. 7. Composition according to claim 6, wherein the weight ratio is between 85:15 and 65:35. 8. Composition according to any one of claims 1-6, which composition contains as component d) a corrosion inhibitor which is miscible in the composition but better soluble in water, in an amount of 0.01-1% by weight based on the total composition. 9. Composition according to claim 8, wherein component d) is chosen from the group of sodium-2-ethyl hexanoate and potassium-2-ethyl hexanoate. 10. Process for removing ink from a printing machine, which process comprises treating the printing surface with a cleaning composition as described in any one of claims 1-6 and subsequently rinsing the treated surface.

Inventors: BEERS NICOLAAS CORNELIS MARIA, KEYZER LUCAS PETRUS SIMON, BEERS, NICOLAAS, CORNELIS, MARIA, KEYZER, LUCAS, PETRUS, SIMON
Applicants: SHELL CANADA LTD, SHELL INT RESEARCH, SHELL CANADA LIMITED, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1996
Main classification: C09D9
IPC codes: B41N3, C09D9, C11D7