THERMOPLASTIC PROPYLENE ELASTOMERS AND ONE POT/TWO CATALYSTS PROCESS TO PRODUCE THEM

Abstract: This invention relates to polypropylene blends, particularly blends of high molecular weight amorphous polypropylene with lower molecular weight isotactic polypropylene. These blends exhibit unusual elastomeric properties. This invention also relates to the production of polypropylene blend compositions using at least two catalyst systems, one for producing amorphous polypropylene and one for producing crystalline polypropylene.

Description: THERMOPLASTIC PROPYLENE ELASTOMERS AND ONE POT/TWO CATALYSTS PROCESS TO PRODUCE THEM Field of the Invention This invention relates to thermoplastic elastomers comprising alpha-olefins, preferably propylene, and a process to produce those thermoplastic elastomers comprising selecting two separate catalyst systems and polymerizing alpha-olefins using those catalyst systems. The thermoplastic elastomer products thereof have improved properties. Background of the Invention: It is well recognized that amoφhous polypropylene(aPP) is a soft, rubbery, gel-like material which possesses very low crystallinity and therefore poor physical properties. Because of its poor mechanical strength, this material has found few practical uses compared to other forms of polypropylene such as isotactic polypropylene(iPP) and syndiotactic polypropylene (sPP), both of which are crystalline and therefore have good mechanical properties. Individual polyolefins having certain characteristics are often blended together in the hopes of combining the positive attributes of the components. TypicaUy, however, the result is a blend which displays a weighted average of the individual properties of the individual resins. For example European Patent AppUcation 0527 589 published February 17, 1993, blends flexible low molecular weight amorphous polypropylene (aPP) with higher molecular weight stiff and strong isotactic polypropylene (iPP) to obtain compositions with balanced mechanical strength and flexibiUty. The composition shows better flexibiUty compared to the isotactic polypropylene but the elastic recovery properties are still poor. Yet it is desirable to find a composition that is both very flexible and very strong. It is an object of this invention to provide such a composition. Summary of the Invention This invention relates to polyolefin compositions comprising: (1) amorphous poly-α-olefin having a weight average molecular weight (Mw) of at least about 150,000 and (2) crystalline poly-α-olefin having an Mw of less than about 300,000, provided that the Mw of the amorphous poly-α-olefin is greater than the Mw of the crystaUine poly-α-olefin. This invention further relates to a method to produce such poly-α-olefin compositions comprising polymerizing α- olefin in the presence of two different cyclopentadienyl transition metal compounds, or alternatively by producing said polymers independently and subsequently blending them together. Brief Descriptions of the Drawings Figure 1 contains the GPC molecular weight distribution curves for examples 2, 3 and 4 in Table 5. Description of Preferred Embodiments. In a preferred embodiment this invention relates to polypropylene compositions comprising: amorphous polypropylene (aPP) having a weight average molecular weight of at least about 150,000 and crystalline polypropylene (cPP) having a weight average molecular weight of less than about 300,000, provided that the Mw of the amoφhous polypropylene is greater than the Mw of the crystalUne polypropylene. In additionally preferred embodiments, the amoφhous polypropylene has a weight average molecular weight at least about 50,000 daltons greater than the crystalUne polypropylene, preferably at least about 70,000 daltons greater, even more preferably about 100,000 daltons greater. In a preferred embodiment the amoφhous polypropylene has an Mw of at least about 300,000. Likewise in a preferred embodiment the crystalUne polypropylene has an Mw bewteen about 150,000 and about 20,000. For puφoses of this invention, the term alpha-olefin shaU mean C3 to C20 Unear, branched or cycUc olefins. In another preferred embodiment this invention relates to the in situ production of a blend (in situ blend) of amoφhous polypropylene and crystalline polypropylene, such as isotactic polypropylene or syndiotactic polypropylene, by using two different cyclopentadienyl transition metal compounds with one or more activating agents, such an alumoxane or a non-coordinating anion activator, in the same polymerization zone under the same polymerization conditions at relatively the same time. The resulting product exhibits a good balance of physical strengths and elastic recovery properties. In another embodiment of this invention, the polypropylene compositions can be produced in two separate reactors using different catalysts and subsequently physically blending these polymers together (physical blend). Iptimate Blends Preferred blends of polypropylene preferably comprise about 10 to about 90 weight percent of an amoφhous polypropylene having an Mw of at least about 150,000 and about 90 to about 10 weight percent, based upon the weight of the polymers, of a crystalline polypropylene having an Mw of less than about 300,000, provided that the Mw of the amoφhous polypropylene is greater than the Mw of the crystalline polypropylene. In a further preferred embodiment the blend comprises about 30 to about 90 weight percent of an amoφhous polypropylene and about 70 to 10 weight percent of a crystalline polypropylene. In a particularly preferred embodiment the blend comprises about 50 to about 90 weight percent of an amoφhous polypropylene and about 50 to 10 weight percent of a crystalUne polypropylene. In particularly preferred embodiments the crystaUine polypropylene is an isotactic polypropylene. The preferred intimate blends described above are preferably produced by simultaneously or in series polymerizing propylene with two or more cyclopentadienyl transition metal compounds selected to produce the desired molecular weights and crystalline or amoφhous character. For example, one could choose two catalysts, one known to produce isotactic polypropylene and the other known to produce amoφhous polypropylene, and use them simultaneously or in series to produce an intimate blend of the two polypropylene polymers so produced. In commercial process, isotactic polypropylene/amoφhous polypropylene blends may be produced through mixed catalysts in a conventional solution or slurry process. In a preferred embodiment the cyclopentadienyl transition metal compounds are activated with the same a non-coordinating anion activator or alumoxane. It is a preferrred aspect of this invention that two cyclopentadienyl transition metal compounds can be used at the same time and combined with the same non-coordinating anion activator or alumoxane to produce two active sites in the polymerization zone. Each of which is very specific for a particular polymer product. Catalyst System and Selection The catalyst systems comprise two or more transition metal components and an activator which can be either a conventional Lewis acid activator such as an alumoxane or a modified alumoxane or a non-coordinating anion activator. The transition metal components of the catalyst are preferably a cyclopentadienyl derivatives of a Group 4 metal of the periodic table of the elements, including mono-, di- and tri-cyclopentadienyls and their derivatives of the transition metals. Particularly, transition metal components are derivatives of the Group 4 metals, preferably titanium, zirconium and hafnium, (preferably hafnium and zirconium for bis-cyclopentadienyl compounds and titanium for mono-cyclopentadienyl compounds). The activator is preferably methylalumoxane, a modified alumoxane or a non-coordinating anion activator comprising boron. In general at least two transition metal components are employed in formation of the catalyst system with one activator, however other multiple combinations of transition metal compounds and activators are also within the scope of this invention. Catalyst System - General Description The process of this invention is practiced with that class of catalysts referred to, disclosed, and described in EPA 277 003 and EPA 277 004, both published 8-3-88 and EPA 520,732, U.S. Patents 5,055,438; 5,198,401; 5,055,438; 5,264,405; 5,324,800; 5,017,714; and 5,096,867; and WO 9200333. The catalysts used in this invention can be represented by one of the following general formulae (all references to Groups being the new Group notation of the Period Table of the Elements as described by Chemical and Engineering News, 63(5), 27, 1985): 1. [{[(A-Cp)MX 1 ]+} d ] { [B , ]d- } 2. [{[(A-Cp)MX 1 L]+} d ] { [B']d-} 3. wherein: (A-Cp) is either (Cp) (Cp*) or Cp-A'-Cp*; Cp and Cp* are the same or different cyclopentadienyl rings substituted with from zero to five substituent Groups S, each substituent Group S being, independently, a radical Group which is a hydrocarbyl, substituted-hydrocarbyl, halocarbyl, substituted-halocarbyl, hydrocarbyl-substituted organometalloid, halocarbyl-substituted organometalloid, disubstituted boron, disubstituted pnictogen, substituted chalcogen or halogen radicals, or Cp and Cp* are cyclopentadienyl rings in which any two adjacent S Groups are joined forming a C4 to C20 ring to give a saturated or unsaturated polycycUc cyclopentadienyl Ugand; A' is a bridging Group; (C5H5.y-.xSx) is a cyclopentadienyl ring substituted with from zero to five S radicals as defined above; x is from 0 to 5 denoting the degree of substitution; M is titanium, zirconium or hafnium; X\ is a hydride radical, hydrocarbyl radical, substituted-hydrocarbyl radical, hydrocarbyl-substituted organometalloid radical or halocarbyl-substituted organometaUoid radical which radical may optionally be covalently bonded to both or either M and L or L'or all or any M, S or S', and provided that Xi is not a substituted or unsubstituted cyclopentadienyl ring; (JS'z-l-y) is a heteroatom Ugand in which J is an element from Group 15 of the Periodic Table of Elements with a coordination number of 3 or an element from Group 16 with a coordination number of 2; S' is a radical Group which is a hydrocarbyl, substituted hydrocarbyl, halocarbyl, substituted halocarbyl, hydrocarbyl-substituted organometaUoid, or halocarbyl-substituted organometaUoid; and z is the coordination number of the element J; y is O or l; L is an olefin, diolefin or aryne Ugand. L' is the same as L, and can additionally be an amine, phosphine, ether, or sulfϊde Ugand, or any other neutral Lewis base; L' can also be a second transition metal compound of the same type such that the two metal center M and M* are bridged by X\ and X'\, wherein M* has the same meaning as M, X' \ , X2 and X'2 have the same meaning as X \ , where such dimeric compounds which are precursors to the cationic portion of the catalyst are represented by the formula: 4. wherein w is an integer from 0 to 3; B is a chemicaUy stable, non-nucleophiUc anionic complex having a molecular diameter about or greater than 4 angstroms or an anionic Lewis-acid activator resulting from the reaction of a Lewis-acid activator with the precursor to the cationic portion of the catalyst system described in formulae 1-4. When B' is a Lewis-acid activator, X\ can also be an alkyl Group donated by the Lewis-acid activator; and d is an integer representing the charge of B. The catalysts are preferably prepared by combining at least two components. In one preferred method, the first component is a cyclopentadienyl derivative of a Group 4 metal compound containing at least one Ugand which will combine with the second component or at least a portion thereof such as a cation portion thereof. The second component is an ion-exchange compound comprising a cation which will irreversibly react with at least one Ugand contained in said Group 4 metal compound (first component) and a non-coordinating anion which is either a single coordination complex comprising a plurality of lipophilic radicals covalently coordinated to and shielding a central formaUy charge-bearing metal or metalloid atom or an anion comprising a plurality of boron atoms such as polyhedral boranes, carboranes and metallacarboranes. In general, suitable anions for the second component may be any stable and bulky anionic complex having the foUowing molecular attributes: 1) the anion should have a molecular diameter greater than 4 angstroms; 2) the anion should form stable ammonium salts; 3) the negative charge on the anion should be delocalized over the framework of the anion or be locaUzed within the core of the anion; 4) the anion should be a relatively poor nucleophile; and 5) the anion should not be a powerful reducing to oxidizing agent. Anions meeting these criteria - such as polynuclear boranes, carboranes, metaUacarboranes, polyoxoanions and anionic coordination complexes are weU described in the chemical Uterature. The cation portion of the second component may comprise Bronsted acids such as protons or protonated Lewis bases or may comprise reducible Lewis acids such as ferricinum, tropyUum, triphenylcarbenium or silver cations. In another preferred method, the second component is a Lewis-acid complex which wiU react with at least one Ugand of the first component, thereby forming an ionic species described in formulae 1-4 with the Ugand abstracted from the first component now bound to the second component Alumoxanes and especially methylalumoxane, the product formed from the reaction of trimethylaluminum in an aUphatic or aromatic hydrocarbon with stoichiometric quantities of water, are particularly preferred Lewis-acid second components. Modified alumoxanes are also preferred. Alumoxanes are well known in the art and methods for their preparation are Ulustrated by U.S. Patent No.'s 4,542,199; 4,544,762; 5,015,749; and 5,041,585. A technique for preparing modified alumoxanes has been disclosed in U.S. Patent 5,041,584, in EPA 0516476, and in EPA 0561 476, which are incoφorated by reference herein. Upon combination of the first and second components, the second component reacts with one of the ligands of the first component, thereby generating an anion pair consisting of a Group 4 metal cation and the aforementioned anion, which anion is compatible with and noncoordinating towards the Group 4 metal cation formed from the first component. The anion of the second compound must be capable of stabUizing the Group 4 metal cation's abiUty to function as a catalyst and must be sufficiently labile to permit displacement by an olefin, diolefin or an acetylenicaUy unsaturated monomer during polymerization. The catalysts of this invention may be supported. U.S. Patents 4,808,561, issued 2-28-89; 4,897,455 issued 1-3-90; 5,057,475 issued 10-15-91; U.S. Patent AppUcation 459,921 (published as PCT International publication WO 91/09882), Canadian Patent 1,268,753, US patent 5,240,894 and WO 9403506 disclose such supported catalysts and the methods to produce such and are herein incoφorated by reference. A. The Transition Metal Components The Group 4 metal compounds; i.e., titanium, zirconium and hafnium metaUocene compounds, useful as first compounds in the preparation of the catalyst of this invention are cyclopentadienyl derivatives of titanium, zirconium and hafnium. In general, useful titanocenes, zirconocenes and hafnocenes may be represented by the foUowing general formulae: 5. (A-Cp)MX!X 2 6. (A-Cp)ML 7. (Cp*)(CpR)MX! wherein: 1. (A-Cp) is either (Cp)(Cp*) or Cp-A'-Cp*; Cp and Cp* are the same or different cyclopentadienyl rings substituted with from zero to five substituent Groups S, each substituent Group S being, independently, a radical group which is a hydrocarbyl, substituted-hydrocarbyl, halocarbyl, substituted-halocarbyl, hydrocarbyl-substituted organometaUoid, halocarbyl-substituted organometalloid, disubstituted boron, disubstituted pnictogen, substituted chalcogen or halogen radicals, or Cp and Cp* are cyclopentadienyl rings in which any two adjacent S Groups are joined forming a C4 to C20 ήng to give a saturated or unsaturated polycycUc cyclopentadienyl Ugand; R is a substituent on one of the cyclopentadienyl radicals which is also bonded to the metal atom; A' is a bridging Group; y is 0 or 1 ; (C5H5_y_ x S x ) is a cyclopentadienyl ring substituted with from zero to five S radicals as defined above; x is from 0 to 5 denoting the degree of substitution; (JS' z _ι_y) is a heteroatom Ugand in which J is an element from Group 15 of the Periodic Table of Elements with a coordination number of 3 or an element from Group 16 with a coordination number of 2, S' is a radical Group which is a hydrocarbyl, substituted hydrocarbyl, halocarbyl, substituted halocarbyl, hydrocarbyl-substituted organometalloid, or halocarbyl-substituted organometaUoid; and z is the coordination number of the element J; L is an olefin, diolefin or aryne Ugand. L' is the same as L and can additionaUy be an amine, phosphine, ether, or sulfide Ugand, or any other neutral Lewis base; L' can also be a second transition metal compound of the same type such that the two metal centers M and M* are bridged by Xj and X'\, wherein M* has the same meaning as M, X' j has the same meaning as Xj and X'2 has the same meaning as X2 where such dimeric compounds which are precursors to the cationic portion of the catalyst are represented by the formula: 9. w is an integer from 0 to 3; and X] and X2 are, independently, hydride radicals, hydrocarbyl radicals, substituted hydrocarbyl radicals, halocarbyl radicals, substituted halocarbyl radicals, and hydrocarbyl- and halocarbyl-substituted organometalloid radicals, substituted pnictogen radicals, or substituted chalcogen radicals; or X\ and X2 are joined and bound to the metal atom to form a metaUacycle ring containing from about 3 to about 20 carbon atoms; or X\ and X2 together can be an olefin, diolefin or aryne Ugand; or when Lewis-acid activators, such as methylalumoxane, which are capable of donating an Xi Ugand as described above to the transition metal component are used, X\ and X2 may independently be a halogen, alkoxide, aryloxide, amide, phosphide or other univalent anionic Ugand or both X] and X2 can also be joined to form a anionic chelating Ugand and with the proviso that Xj and X 2 are not a substituted or unsubstituted cyclopentadienyl ring. Tables A and B depict representative constituent moieties for the metaUocene components of formulae 5-8. The list is for iUustrative puφoses only and should not be construed to be limiting in any way. A number of final components may be formed by permuting aU possible combinations of the constituent moieties with each other. IUustrative compounds of the formula 5 type are: bis(cyclopentadienyl)hafhium dimethyl, ethylenebis(tetrahydroindenyl)zirconium dihidryde, b--s(pentamethyl)zirconium diethyl, dimethylsilyl(l-fluorenyl)(cyclopentadienyl)titanium dichloride and the like. IUustrative compounds of the formula 6 type are: bis(cyclopentadienyl)(l,3- butadiene)zirconium, bis(cyclopentadienyl)(2,3-dimethyl-l ,3-butadiene) zirconium, bis(pentamethylcyclopentadienyl)(benzene) zirconium, bis(pentamethylcyclopentadienyl) titanium ethylene and the like. IUustrative compounds of the formula 7 type are: (pentamethylcyclopentadienyl)- (tetramethylcyclopentadienylmethylene) zirconium hydride, (pentame ylcyclopentadienyl)-(tetr--methylcyclopentadienylmemylene) z--rconium phenyl and the like, ϋlustrative compounds of the formula 8 type are: dimethylsilyl(tetramethylcyclopentadienyl) (t-butylamido)zirconium dichloride, ethylene(methylcyclopentadienyl)(phenylamido)titanium dimethyl, methylphenylsUyl(-ndenyl)(phenyphosphido)haft-ium dihydride and (pentamemylcyclopentadienyl)(di-t-butyl----mdo)hafnium dimethoxide. The conditions under which complexes containing neutral Lewis base Ugands such as ether or those which form dimeric compounds is determined by the steric bulk of the Ugands about the metal center. For example, the t-butyl Group in Me2Si(Me4C5)(N-t-Bu)ZrCl2 has greater steric requirements that the phenyl Group in Me2Si(Me4C5)(NPh)ZrCl2*Et2θ thereby not permitting ether coordination in the former compound in its soUd state. Similarly, due to the decreased steric bulk of the trimethylsilylcyclopentadienyl Group in [Me2Si(Me3SiC5H3)(N-t-Bu)ZrCl2l2 versus that of the tetramethylcyclopentadienyl Group in Me2Si(Me4C5)(N-t-Bu)ZrCl2, the former compound is dimeric and the latter is not TableA Table B B. The Activator Component Ionic catalysts can be prepared by reacting a transition metal compound with some neutral Lewis acids, such as which upon reaction with the hydrolyzable Ugand (X) of the transition metal compound forms an anion, such as ([B(C6F5)3(X)] ~ ), which stabilizes the cationic transition metal species generated by the reaction. The catalysts can be, and preferably are, prepared with activator components which are ionic compounds or compositions. However preparation of activators utilizing neutral compounds is also contemplated by this invention. Compounds useful as an activator component in the preparation of the ionic catalyst systems used in the process of this invention comprise a cation, which is preferably a Bronsted acid capable of donating a proton, and a compatible non- coordinating anion which anion is relatively large (bulky), capable of stabilizing the active catalyst species (the Group 4 cation) which is formed when the two compounds are combined and said anion wiU be sufficiently labile to be displaced by olefinic diolefϊnic and acetylenicaUy unsaturated substrates or other neutral Lewis bases such as ethers, nitriles and the like. Two classes of compatible non- coordinating anions have been disclosed in EPA 277,003 and EPA 277,004 pubUshed 1988: 1) anionic coordination complexes comprising a plurality of Upophilic radicals covalently coordinated to and shielding a central charge-bearing metal or metaUoid core, and 2) anions comprising a plurahty of boron atoms such as carboranes, metaUacarboranes and boranes. In general, the activator compounds containing single anionic coordination complexes which are useful in this invention may be represented by the foUowing general formula: 10. [(L"-H)+] d [(M') m+ Qι ...Q n ] d - wherein: H is a hydrogen atom; [L"-H] is a Bronsted acid; M' is a metal or metalloid; Ql t0 Qn are ' independently, bridged or unbridged hydride radicals, dialkylamido radicals, alkoxide and aryloxide radicals, hydrocarbyl and substituted- hydrocarbyl radicals, halocarbyl and substituted-halocarbyl radicals and hydrocarbyl and halocarbyl-substituted organometalloid radicals and any one, but not more than one, of Q\ to Q n may be a haUde radical; m is an integer representing the formal valence charge of M; and n is the total number of Ugands q. As indicated above, any metal or metalloid capable of forming an anionic complex which is stable in water may be used or contained in the anion of the second compound. Suitable metals, then, include, but are not limited to , aluminum, gold, platinum and the like. Suitable metalloids include, but are not limited to, boron, phosphorus, silicon and the like. Compounds containing anions which comprise coordination complexes containing a single metal or metaUoid atom are, of course, well known and many, particularly such compounds containing a single boron atom in the anion portion, are available commerciaUy. In Ught of this, salts containing anions comprising a coordination complex containing a single boron atom are preferred. The preferred activator compounds comprising boron may be represented by the foUowing general formula: 11. [L"-H] + [BAr 1 Ar 2 X3X4]- wherein: B is a boron in a valence state of 3; Arj and Ar2 are the same or different aromatic or substituted-aromatic hydrocarbon radicals containing from about 6 to about 20 carbon atoms and may be linked to each other through a stable bridging Group; and X3 and X4 are, independently, hydride radicals, hydrocarbyl and substituted-hydrocarbyl radicals, halocarbyl and substituted-halocarbyl radicals, hydrocarbyl- and halocarbyl-substituted organometaUoid radicals, disubstituted pnictogen radicals, substituted chalcogen radicals and haUde radicals, with the proviso that X3 and X4 wUl not be halide at the same time. In general, Arj and Ar2 may, independently, be any aromatic of substituted-aromatic hydrocarbon radical. Suitable aromatic radicals include, but are not limited to, phenyl, naphthyl and anthracenyl radicals. Suitable substituents on the substituted-aromatic hydrocarbon radicals, include, but are not necessarily Umited to, hydrocarbyl radicals, organometalloid radicals, alkoxy and aryloxy radicals, alkylamido radicals, fluorocarbyl and fluorohydrocarbyl radicals and the like such as those useful as X3 and X4. The substituent may be ortho, meta or para, relative to the carbon atoms bonded to the boron atom. When either or both X3 and X4 are a hydrocarbyl radical, each may be the same or a different aromatic or substituted-aromatic radical as are Arj and Ar2, or the same may be a straight or branched alkyl, alkenyl or alkynyl radical, a cycUc hydrocarbon radical or an alkyl-substituted cychc hydrocarbon radical. X3 and X4 may also, independently be alkoxy or dialkylamido radicals wherein the alkyl portion of said alkoxy and dialkylamido radicals, hydrocarbyl radicals and organometaUoid radicals and the like. As indicated above, A and Ar2 could be linked to either X3 or X4. FinaUy, X3 and X4 may also be Unked to each other through a suitable bridging Group. Illustrative, but not Umiting, examples of boron compounds which may be used as an activator component in the preparation of the improved catalysts of this invention are trialkyl-substituted ammonium salts such as triethylammonium tetra(phenyl)boron, tripropylammonium tetra(phenyl)boron, tri(n-butyl)ammonium tetra(phenyl)boron, trimethylammonium tetra(p-tolyl)boron, trimethylammonium tetra(o-tolyl)boron, tributylammonium tetra(pentafluorophenyl)boron, tripropylammonium tetra(o,p-dimethylphenyl)boron, tributylammonium tetra(m,m- dimethylphenyl)boron, tributylammonium tetra(p-tri-fluoromethylphenyl)boron, tri(n-butyl)ammonium tetra(o-tolyl)boron and the like; N,N-dialkyl amlinium salts such as N,N-dimethylamlinium tetra(pentafluorophenyl)boron, N,N-di- ethylanilinium tetra(phenyl)boron, N,N-2,4,5-pent--unethyl--m--liniι-m tetra(phenyl)boron and the like; dialkyl ammonium salts such as di(i- propyl)ammonium tetra(pentafluorophenyl)boron, dicyclohexylammonium tetra(phenyl)boron and the like; and triaryl phosphonium salts such as triphenylphosphonium tetra(phenyl)boron, tri(methylphenyl)phosphonium tetra(phenyl)boron, tri(dimethylphenyl)phosphonium tetra(phenyl)boron and the like; carbonium salt such as trityl teta(pentafluorophenyl)boron and the like. Similar lists of suitable compounds containing other metals and metaUoids which are useful as activator components may be made, but such Usts are not deemed necessary to a complete disclosure. In this regard, it should be noted that the foregoing Ust is not intended to be exhaustive and that other useful boron compounds as weU as useful compounds containing other metals or metalloids would be readily apparent to those skilled in the art from the foregoing general equations. The most preferred activator compounds comprising boron may be represented by the following general formula: 12. [L"-H]+[B(C6F 5 )3Q1- wherein: F is fluorine, C is carbon and B, L', and Q are defined hereinabove. πiustrative but not limiting, examples of most preferred activator compounds comprising boron which may be used in the preparation of the improved catalysts of this invention include N,N-dialkylaniUnium salts (L' = N,N-dialkylanUine) where Q is a simple hydrocarbyl such as methyl, butyl, cyclohexyl, or phenyl or where Q is a polymeric hydrocarbyl of indefinite chain length such as polystyrene, polyisoprene, or poly-paramethylstyrene. Polymeric Q substituents on the most preferred anion offer the advantage of providing a highly soluble ion-exchange activator component and final ionic catalyst. Soluble catalysts and/or precursors are often preferred over insoluble waxes, oils, phases, or soUds because they can be diluted to a desired concentration and can be transferred easily using simple equipment in commercial processes. Activator components based on anions which contain a pluraUty of boron atoms may be represented by the foUowing general formulae: 13. [L"-H] c [(CX)a(BX) m Xb]c- or 14. [L"-H]d'[[[(CX6)a'(BX7)m'(X8)b , ] c '-]2Mn'+]d'- wherein [L"-H] is either H+ or a Bronsted acid derived from the protonation of a neutral Lewis base; X, X', X", X6, X7 and X$ are, independently, hydride radicals, haUde radicals, hydrocarbyl radicals, substituted-hydrocarbyl radicals, halocarbyl radicals, substituted-halocarbyl radicals, or hydrocarbyl- or halocarbyl-substituted organometaUoid radicals; M is a transition metal; a and b are integers > 0; c is an integer > l; a + b + c = an even-numbered integer from 2 to about 8; and m is an integer ranging from 5 to about 22; a and b are the same or a different integer 0; c is an integer > 2; a + b + c = an even-numbered integer from 4 to about 8; m is an integer from 6 to about 12; n is an integer such that 2c - n = d; and d is an integer > 1. Preferred anions of this invention comprising a plurality of boron atoms comprise: ( 1 ) A trisubstituted ammonium salt of a borane or carborane anion satisfying the general formula: 15. [(CH)aχ(BH) b χ]cx- wherein: ax is either 0 or 1 ; ex is either 1 or 2; ax + ex = 2; and bx is an integer ranging from about 10 to 12; (2) A trisubstituted ammonium salt of a borane or carborane or a neutral borane or carborane compound satisfying the general formula: 16. [(CH) ay (BH) my (H)by]cy- wherein: ay is an integer from 0 to 2; by is an integer from 0 to 3; cy is an integer from 0 to 3; ay + by + cy = 4; and my is an integer from about 9 to about 18; or (3) A trisubstituted ammonium salt of a metaUaborane or metaUacarborane anion satisfying the foUowing general formula: 17. [[[(CH)az(BH) mz (H)bz] cz -]2Mnz+]dz- wherein: az is an integer from 0 to 2; bz is an integer from 0 to 2; cz is either 2 or 3; mz is an integer from about 9 to 11; az + bz + cz = 4; and nz and dz are, respectively, 2 and 2 or 3 and 1. -Qlustrative, but not limiting, examples of second components which can be used in preparing catalyst systems utilized in the process of this invention wherein the anion of the second component contains a plurality of boron atoms (as in formulae 10-17) are mono-, di-, trialkylammonium and phosphonium and dialkylarylammonium and -phosphonium salts such as bis[tri(n-butyl)ammonium] dodecaborate, bis[tri(n-butyl)ammomum]decachlorodecaborate, tri(n- butyl)ammonium dodecachlorododecaborate, tri(n-butyl)ammonium 1- carbadecaborate, tri(n-butyl)ammonium 1-carbaudecaborate, tri(n-butyl)ammonium 1-carbadodecaborate, tri(n-butyl)ammonium 1-trimethylsilyl-l -carbadecaborate, tri(n-butyl)ammonium dibromo-1-carbadodecaborate; borane and carborane complexes and salts of borane and carborane anions such as decaborane(14), 7,8- dicarbaudecaborane(13), 2,7-dicarbaundecaborane(13), undecahydrido-7,8- dimethyl-7,8-dicarbaundecaborane, tri(n-butyl)ammonium 6-carbadecaborate(12), tri(n-butyl)ammonium 7-carbaundecaborate, tri(n-butyl)ammonium 7,8- dicarbaundecaborate and metaUaborane anions such as tri(n-butyl)ammonium bis(nonahydrido- 1 ,3-dicarbanonaborato)cobaltate(III), tri(n-butyl)ammonium bis(undecahydrido-7,8-dicarbaundecaborato) ferrate(I-Q), tri(n-butyl)ammonium bis(undecahydrido-7,8-dicarbaundecaborato) cobaltate(III), tri(n-butyl)ammonium bis(undecahydrido-7,8-dicarbaunaborato) nikelate(III), tri(n-butyl)ammonium bis(nonahydrido-7,8-dimethyl-7,8-dicarbaundecaborato)ferrate(III), tri(n- butyl)--mmonium bis(tribromooctahydrido-7,8-dic--rbaundecaborato)cobaltate(iπ), tri(n-butyl) ammonium bis(υndecahydridodicarbadodecaborato) cobaltate(HI) and bis[tri(n-butyl)ammonium] bis(undecahydrido-7-carbaιmdecaborato) cobaltate(III). A similar Ust of representative phosphonium compounds can be recited as iUustrative second compounds, but for the sake of brevity, it is simply noted that the phosphonium and substituted-phosphonium salts corresponding to the Usted ammonium and substituted-ammonium salts could be used as second compounds in the present invention. The preferred activator compounds comprising Lewis-acid activators and in particular alumoxanes are represented by the foUowing general formulae: 18. (R3-Al-O)p 19. R4(R5-A1-O) P -A1R6 2 20. (M'p+Q'm An alumoxane is generaUy a mixture of both the linear and cycUc compounds. In the general alumoxane formula, R3, R4, R5 and R6 are, independently a C1-C alkyl radical, for example, methyl, ethyl, propyl, butyl or pentyl and "p" is an integer from 1 to about 50. Most preferably, R3, R4, R5 and R6 are, each methyl and "p" is a least 4. When an alkyl aluminum haUde is employed in the preparation of the alumoxane, one or more R3-6 Groups may be halide. M' and M are as described previously and Q' is a partially or fully fluorinated hydrocarbyl. It is recognized that alumoxane is not a discrete material. A typical alumoxane will contain free trisubstituted or trialkyl aluminum, bound trisubstituted or trialkyl aluminum, and alumoxane molecules of varing degree of oUgomerization. Those methylalumoxanes most preferred contain lower levels of trimethylaluminum. Lower levels of trimethylaluminum can be achieved by reaction of the trimethylaluminum with a Lewis base or by vacuum distillation of the trimethylaluminum or by any other means known in the art It is also recognized that after reaction with the transition metal compound, some alumoxane molecules are in the anionic form as represented by equations 1-3, thus for our piuposes are considered "non-coordinating" anions. The activator compositions most preferred for forming the ionic catalyst used in this process are those containing a tetrapentafiuoφhenyl boron anion; two or more tripentafluorophenyl boron anion Groups covalently bond to a central atomic molecular or polymeric complex or particle; or methylalumoxane, or a modified methylalumoxane. Other examples of activator specific compositions which may be used to form an anionic catalyst useful in this invention are identified and more fuUy described in European Patent AppUcation Nos. 0277003 and 0277 004 and WO 92 00333 which are hereby incoφorated by reference. The Choice of Transition Metal Catvlst Components The catalyst system of this invention comprises two or more transition metal compounds as described above. At least one of the compounds must be capable of producing a high molecular weight crystalline poly-a-olefin, preferrably isotatic polypropylene or syndiotactic polypropylene. A second compound must be capable of producing a high molecular weight amoφhous poly-a-olefin, preferrably atactic polypropylene. The preferred choice of transition metal component for the high molecular weight amoφhous polymer fraction is the mono-cyclopentadienyl transition metal component of equation 8 where y is equal to 1. This preferred component is illustrated in equation 21: where A', J, S', Xi, X2, L', z and w as are previously defined and M is titanium. Substituent Sy is defined to be the same as S in equation 8 where the subscript "v" denotes the carbon atom on the cyclopentadienyl ring to which the substituent is bonded and where there can be zero, two or four substituents, S, on the cyclopentadienyl ring provided that the cyclopentadienyl ring is symmetricaUy substituted. Symmetrically substituted is defined to mean that the cyclopentadienyl ring is substituted in the 2 and 5 positions and/or 3 and 4 positions with S groups that are of approximately of the same steric bulk. TypicaUy the size of these S groups are within 2 carbons of each other. Thus a cyclopentadienyl substituted at the 2 and the 5 positions with methyl and ethyl respectively, or substituted at the 3 and the 4 positions with hexyl and octyl, respectively, would be considered symmetric. Likewise, the cyclopentadienyl ring may be substituted at aU four sites with S groups and be considered symmetric as long as each of the symmetrical pairs are of similar steric bulk. AdditionaUy, two adjacent S-groups in the 3 and 4 position may be linked to form a ring provided that the new ring is also symmetrically substituted. Preferred mono-cyclopentadienyl transition metal compounds which, according to the present invention, provide catalyst systems which are specific to the production of high molecular weight atactic poly-α-olefins include diLmemylsUyl(tetramemylcyclopentadienyl)(cyclododecylamido) titanium dichloride, dimethylsUyl(tetramethylcyclopentadienyl)(cyclohexyl-amido) titanium dichloride, d-methyMyl(tetr--methylcyclopentadienyl)(l-adamantylamido) titanium dichloride, dimethylsilyl(tetramethylcyclopentadienyl)(t-butylamido) titanium dichloride, dimethylsilyl(tetramethylcyclopentadienyl)(s-butylamido) titanium dichloride, dimethylsilyl(tetramethylcyclopentadienyl)(n-butylamido) titanium dichloride, dimethylsilyl(tetramethylcyclopentadienyl)(exo-2-norbornylamido) titanium dichloride, diethylsUyl(tetramethylcyclopentadienyl)(cyclododecyl-amido) titanium dichloride, diethylsUyl(tetramethylcyclopentadienyl)(exo-2-norbornylamido) titanium dichloride, diethylalyl(tetr--methylcyclopentadienyl)(cyclohexyl-amido) titanium dichloride, diethylsilyl(tetramethylcyclopentadienyl)(l-adamantylamido) titanium dichloride, methylene(tetramethylcyclopentadienyl)(cyclododecyl-amido) titanium dichloride, methylene(tetramethylcyclopentadienyl)(exo-2- norbornylamido) titanium dichloride, methylene(tetramethylcyclopentadienyl)(cyclohexylamido)-titanium dichloride, methylene(tetramethylcyclopentadienyl)(l-adamantylamido) titanium dichloride, dimethyl-alyl(tetramethylcyclopentadienyl)(cyclododecylamido) titanium dimethyl, dimethylsUyl(tetramethylcyclopentadienyl)(exo-2-norbornylamido) titanium dimethyl, dimethylsilyl(tetramethylcyclopentadienyl)(cyclohexyl-amido) titanium dimethyl, dimemykUyl(tetramethylcyclopentadienyl)(l-adamantylamido) titanium dimethyl, dimethylsilyl(2,5-dimethylcyclopentadienyl)(cyclododecylamido) titanium dichloride, dimethylsilyl(2,5-dimethylcyclopentadienyl)(exo-2-norbornylamido) titanium dichloride, dimethylsUyl(2,5-dimethylcyclopentadienyl)(cyclohexylamido) titanium dichloride, dimethylsUyl(2,5-dimethylcyclopentadienyl)(l- adamantylamido) titanium dichloride, dimethylsUyl(3,4- dimethylcyclopentadienyl)(cyclododecylamido) titanium dichloride, dimethylsilyl(3 ,4-dimethylcyclopentadienyl)(exo-2-norbornylamido) titanium dichloride, d--memyk-lyl(3,4-dimethylcyclopentadienyl)(cyclohexylamido) titanium dichloride, dimethylsilyl(3,4-dimethylcyclopentadienyl)( 1 -adamantylamido) titanium dichloride, dimethylsilyl(2-ethyl-5- methylcyclopentadienyl)(cyclododecylamido) titanium dichloride, dimethylsUyl(2- ethyl-5-methylcyclopentadienyl)(exo-2-norbomylamido) titanium dichloride, dimethylsilyl(2-ethyl-5-methylcyclopentadienyl)(cyclohexylamido) titanium dichloride, dimethylsUyl(2-ethyl-5-methylcyclopentadienyl)( 1 -adamantylamido) titanium dichloride, dimethylsilyl(3-ethyl-4- methylcyclopentadienyl)(cyclododecylamido) titanium dichloride, dimethylsilyl(3- ethyl-4-methylcyclopentadienyl)(exo-2-norbomylamido) titanium dichloride, d-αnemyMyl(3-ethyl-4-memylcyclopentadienyl)(cyclohe-^lamido) titanium dichloride, dimethylsUyl(3-elhyl-4-methylcyclopen-adienyl)(l -adamantylamido) titanium dichloride, dimethylsilyl(2-ethyl-3-hexyl-5-methyl-4- octylcyclopentadienyl)(cyclododecylamido) titanium dichloride, dimethylsUyl(2- ethyl-3-hexyl-5-methyl-4-octylcyclopentadienyl)(exo-2-norbornylamido) titanium dichloride, dimethylsUyl(2-ethyl-3-hexyl-5-methyl-4- octylcyclopentadienyl)(cyclohexylamido) titanium dichloride, dimethylsilyl(2-ethyl- 3-hexyl-5-methyl-4-octylcyclopentadienyl)(l-adamantylamido) titanium dichloride di-memylsUyl(2-tetrahydroindenyl)(cyclododecylamido) titanium dichloride, d-unethylsUyl(2-tetr--hydroindenyl)(cyclohexylamido) titanium dichloride, dimethylsUyl(2-tetrahydroindenyl)(l-adamantylamido) titanium dichloride, dimethylsilyl(2-tetrahydroindenyl)(exo-2-norbornylamido) titanium dichloride and the like. The most preferred species are: dimethylsUyl(tetramethylcyclopentadienyl)(cyclododecylamido) titanium dichloride, dimethylsUyl(tetramethylcyclopentadienyl)(cyclohexyl-amido) titanium dichloride, d--methyls-lyl(tetramethylcyclopentadienyl)(l-adamantylamido) titanium dichloride, dimethylsilyl(tetramethylcyclopentadienyl)(exo-2-norbornylamido) titanium dichloride, dimethyl-alyl(tetramemylcyclopentadienyl)(cyclododecyl--mido) titanium dimethyl, dimethy-LsUyl(tetramethylcyclopentadienyl)(cyclohexyl-amido) titanium dimethyl, dimethylsilyl(tetramethylcyclopentadienyl)(l -adamantylamido) titanium dimethyl, and dimethylsUyl(tetramethylcyclopentadienyl)(exo-2-norbornylamido) titanium dimethyl. The choice of transition metal component for the crystalline polymer fraction is a subset of the transition metal component of equations 5-7. This preferred component is Ulustrated in equation 22: (22) wherein A', M, Xi and X2 are as previously defined in equations 5-7. Substituents S v and S"y are defined as S in equations 5-7 where the subscript "v" denotes the carbon atom on the Cp-ring to which the substituent is bonded. Preferably metaUocene precursors for producing poly-a-olefins having enhanced isotactic character are those of Equation 22 where Sy and S"y are chosen such that the metaUocene framework 1) has no plane of symmetry containing the metal center, and 2) has a C2-axis of symmetry through the metal center. Such complexes, such as rac-Me2Si(indenyl)2---rMe2 and rac-Me2Si(indenyl)2HfMe2, are well known in the art and generally produce isotactic polymers with higher degrees of stereoregularity than the less symmetric chiral systems. Likewise another preferred class of transition metal compounds that can produce isotactic polymers useful in this invention are those monocyclopentadienyl catalysts disclosed in U.S. Patent 5,026,798, which is incoφorated by reference herein. Preferred chiral racemic metaUocene compounds which, according to the present invention, provide catalyst systems which are specific to the production of isotactic poly-α-olefins include dimethy--silylbis(3-methylcyclopentadienyl)zicoι-ium dimethyl, dimethylsUylbis(indenyl) zirconium dihydride, d-methylsUylbis(tetrahydroindenyl) zirconium dimethyl, -hafnium dimethyl and - titanium dimethyl, (lJ,2,2-tetramethyldisUanylene)bis(3-methylcyclopentadienyl) zirconium dimethyl, methylenebis(tetrahydroindenyl) zirconium dimethyl, ethylenebis(tetrahydroindenyl) zirconium dihydride, -dimethyl, and -diphenyl, dimethylsUylbis(2,3-dimethylcyclopentadienyl) zirconium dihydride, dime-hylsilylbis(3-trimethylsilylcyclopentadienyl) zirconium dimethyl, (1,1,2,2- tetr--methyldisUanylene)bis(3-trimethylsUylcyclopentadienyl) zirconium dimethyl and (lJ,3,3-tetramethyldisiloxanylene)bis (tetrahydroindenyl) zirconium dimethyl. Similarly, metaUocene precursors providing tacticity control exist where (A-Cp) is (Cp) (Cp*), both Cp and Cp* having substituents on the cyclopentadienyl rings of sufficient steric bulk to restrict rotation of the cyclopentadienyl Ugands such that the aforementioned symmetry conditions are satisfied. Preferable chiral racemic metallocenes of this type include bis(tricyclo[5.2J.θ2.6]deca-2,5-dienyl) zirconium and -hafnium dimethyl, bis((lR)- 9,9-dimethyltricyclo[6JJ.θ2'6]deca-2,5-dienyl) zirconium dimethyl, bis(tricyclo[5.2J.θ2'6]deca-2,5,8-trienyl) zirconium dimethyl, bis (tricyclo[5.2.2.θ2»6] un deca-2,5,8-trienyl)zirconium and -hafnium dimethyl and bis ((IR, 8R)-7,7,9,9-tetramethyl[6JJ.0 2 ' 6 ]deca-2,5-dienyl) zirconium and -hafnium dimethyl. Preferably metaUocene precursors for the production of poly-α-olefins having enhanced syndiotactic character are also those of Equation 22 where S and S" are chosen such that the two Cp-Ugands have substantiaUy different steric bulk. In order to produce a syndiotactic polymer the pattern of the Groups substituted on the Cp-rings is important. Thus, by steric difference or sterically different as used herein, it is intended to imply a difference between the steric characteristics of the Cp and Cp* rings that renders each to be symmetrical with respect to the A bridging Group but different with respect to each other that controls the approach of each successive monomer unit that is added to the polymer chain. The steric difference between the Cp and Cp* rings act to block the approaching monomer from a random approach such that the monomer is added to the polymer chain in the syndiotactic configuration. Preferable metaUocene precursors for the production of syndiotactic polymers are those of Equation 22 where S and S" are chosen such that 1) the steric difference between the two Cp-Ugands is maximized and 2) there remains a plane of symmetry through the metal center and the Cj and C\' carbon atoms of the Cp-rings in Equation 22. Thus, complexes such as Me2C(η 5 -C5-H4)(l- fluorenyl)MMe2 (where M = Ti, Zr, or Hf) which possess this symmetry are preferred, and generaUy produce the syndiotactic polymer with higher degrees of stereoregularity than similar, but less symmetric, systems. When two transition metal compound based catalysts are used in one reactor as a mixed catalyst system, the two transition metal compounds should be chosen such that the two are compatible or non-reactive to one another. A simple screening method such by 1H or 13 C NMR, known to those of ordinary skill in the art, can be used to determine which transition metal compounds are compatible or non-reactive to one another. It is preferable to use the same activator for the transition metal compounds, however, two different activators, such as a non-coordinating anion activator and an alumoxane, can be used in conjunction. If one or more transition metal compoimds contain an X\ or X2 Ugand which is not a hydride, hydrocarbyl, or substituted hydrocarbyl, then the alumoxane should be contacted with the transition metal compounds prior to addition of the non-coordinating anion activator. Preferred catalysts which produce the higher molecular weight amoφhous polypropylenes include those mono-cyclopentadienyl transition metal compounds having symetrical substitutions on the cyclopentadienyl ring as described above. Likewise preferred catalysts that can produce the lower molecular weight isotactic polypropylene are those described in US patent 5,120,867, which is incoφorated by reference herein. Any catalysts, including supported catalysts, which can be used together or in series, that can also produce the desired polypropylene can be utilized in this invention to produce the in situ blend. Preferred catalysts include cyclopentadienyl transition metals compounds and derivatives thereof used in conjunction with an alumoxane and/or a compatible non-coordinating anion. Particularly preferred combinations of transition metal compounds include: (1) Me 2 Si(Me4C 5 )(N-c-Ci2H23)TiCl2 and Me2Si(H4lnd) 2 Z-Cl2 (H 4 Ind = tetrahydroindenyl)activated with an alumoxane, such as methylalumoxane; (2) Me2Si(Me4C5)(N-c-Ci2H23)TiCl2 and Me2Si(H4-tnd)2Hf l2 activated with an alumoxane, such as methylalumoxane; (3) Me2Si(Me4C5)(N-c-Cj2H23)TiCl2 and Me2Si(2-MeInd)2ZrCl2 activated with an alumoxane, such as methylalumoxane; (4) Me2Si(Me4C5)(N-c-Ci2H23)TiCl2 and Me2Si(2-MeInd)2Hf l2 activated with an alumoxane, such as methyl alumoxane; (5) Me2Si(Mβ4C5)(N-c- Cj2H23)TiMe2 and Me2Si(H4-nd)2ZrMe2 activated with a non-coordinating anion activator, such as N,N-dimethylanilinium tetrakis(pentaflourophenyl)boron or triphenylcarbonium tetrakis(pentaflourophenyl)boron; (6) Me2Si(Me4C5)(N-c- Cj2H23)TiMe2 and Mβ2Si(H4lnd)2HfMe2 activated with a non-coordinating anion activator, such as N,N-d--me yla---ilimum tetrakis(pentaflourophenyl)boron or triphenylcarbonium tetrakis(pentaflourophenyl)boron; (7) Me2Si(Me4C5)(N-c- Cj2H23)TiMe2 and Me2Si(2-MeInd)2ZrMe2 activated with a non-coordinating anion activator, such as N,N-di-methylan-L-inium tetrakis(pentaflourophenyl)boron or triphenylcarbonium tetrakis(pentaflourophenyl)boron; and (8) Me2Si(Me4C5)(N-c-C 12H23)TiMβ2 and Mβ2Si(2-MeInd)2HfMe2 activated with a non-coordinating anion activator, such as N,N-dimemylanilinium tetrakis(pentaflourophenyl)boron or triphenylcarbonium tetrakis(pentaflourophenyl)boron. The two transition metal compounds may be used in any ratio. Preferred ratios of (A) transition metal compound to produce amoφhous polypropylene to (B) transition metal compound to produce crystalUne polypropylene faU within the range of (A:B) about 1:10 to about 50:1, preferably about 1:10 to about 10:1, more preferably about 1:1 to about 5:1, even more preferably about 2:1 to about 4:1. As is weU known in the art, the catalysts may also be supported together on one inert support, or the catalysts may be independently placed on two inert supports and subsequently mixed. Of the two methods, the former is preferred. As an added benefit the in situ blends have properties that are superior even to the physical blend of the isotactic polypropylene and the amoφhous polypropylene. See Table 7 below for a comparison. The polymers produced by the in-situ process using mixed cyclopentadienyl transition metal compounds /23838 PCI7US96/00565 -25- exhibit thermoplastic elastomer type properties, especiaUy strong tensUe strengths and high elastic recoveries. The TPE properties of the insitu blends, especially the high temperature elastic recovery properties, are significantly better than that of similar compositions achieved by the physical blends. In another embodiment this invention relates to physical poly-α-olefin blends comprising amoφhous poly-α-olefϊn and crystalline poly-α-olefin produced by physicaUy blending the two separate polymers. In a preferred embodiment, in either the in situ or physical blend, the poly- α-olefin is polypropylene, preferably propylene homopolymer or copolymer having a minor amount of olefin comonomer. Examples of crystalline polypropylene include isotactic polypropylene and syndiotactic polypropylene. The blends preferably comprise about 10 to about 90 weight percent of an amoφhous polypropylene having an Mw of at least about 150,000 and about 90 to about 10 weight percent, based upon the weight of the polymers, of a crystaUine polypropylene having an Mw of less than about 300,000, preferably between about 150,000 and about 20,000, provided that the Mw of the amoφhous polypropylene is greater than the Mw of the isotactic polypropylene, preferably by about 40,000 daltons or more, even more preferably by about 70,000 daltons ore more, even more preferably by about 100,000 daltons or more. In a further preferred embodiment the blend comprises about 30 to about 90 weight percent of an amoφhous polypropylene and about 70 to 10 weight percent of a crystalline polypropylene. In a particularly preferred embodiment the blend comprises about 50 to about 90 weight percent of an amoφhous polypropylene and about 50 to 10 weight percent of a crystaUine polypropylene. In particularly preferred embodiments, the crystalline polypropylene is an isotactic polypropylene. Preferred amoφhous polypropylenes that can be used in either the in-situ or physical blend methods in this invention include homopolymers of propylene and copolymers of propylene and up to about 40 weight percent, preferably up to about 20 weight percent, even more preferably up to about 10 weight percent, based upon the weight of the copolymer, of another α-olefin. In a preferred embodiment, small quanities of ethylene may also be added such that the polymer contains no more than 10 wt% ethylene. In addition preferred amoφhous polymers have a weight average molecular weight (Mw) of about 150,000 or more, preferably about 150,000 to about 750,000, even more preferably about 150,000 to about 500,000. Preferred amoφhous polymers also have low crystallinity, preferably a crystallinity, as measured by carbon 13 NMR using the conditions described in J. Randall, Polymer Sequence Determination, Carbon- 13 NMR Method. Academic Press 1977, New York, of about 30 % or less of isotactic and syndiotactic pentads combined (rrrr + mmmm), preferably about 20% or less. In another preferred embodiment the amoφhous polymers used or produced in this invention have a narrow molecular weight distribution, (Mw Mn ≤ 5, preferably < 3, even more preferably ≤ 2.5 ). In another preferred embodiment the amoφhous copolymers used or produced in this invention have a composition distribution breadth index (CDBI) of 40% or more, preferabaly 50% or more, preferably 60 % or more, even more preferably 75% or more. High molecular weight amoφhous polymers with a narrow Mw/Mn and/or a CDBI of 50% or more can be produced by the methods described in US Patent Application 07/902,631, filed June 23, 1992, incoφorated by reference herein. In short amoφhous poly-α-olefins particularly polypropylene, are produced using mono-cyclopentadienyl transition metal compounds that are symmetricaUy substituted about the cyclopentadienyl ring, i.e. at the 2, 5 positions and/or the 3, 4 positions, or one substitutent balanced by a bridging Group. Preferred crystaUine propylene polymers useful in this invention include homopolymers of propylene and copolymers of propylene and up to about 40 weight percent of another α-olefin or ethylene, preferably up to about 20 weight percent, based upon the weight of the copolymer. In addition preferred crystaUine polymers have a weight average molecular weight (Mw) of about 300,000 or less, preferably 150,000 or less, even more preferably 100,000 or less. Preferred crystalline polymers also have good crystalUnity, preferably a crystallinity, as measured by carbon 13 NMR, of about 70 % or more isotactic dyads (m) or 70% or more syndiotactic dyads (r), preferably about 80 % or more isotactic dyads (m) or 70% or more syndiotactic dyads (r), even more preferably 90 % or more isotactic dyads (m) or 70% or more syndiotactic dyads (r). In another preferred embodiment the crystalline polymers used in this invention have a narrow molecular weight distribution, (Mw/Mn ≤ 5, preferably < 3, even more preferably ≤ 2.5). In another preferred embodiment the crystalline copolymers used in this invention have a composition distribution breadth index (CDBI) of 40% or more, preferably 50% or more, preferably 60 % or more, even more preferably 75% or more. CrystalUne polymers with a narrow Mw/Mn and/or a CDBI of 50% or more can be produced by the methods described in US Patent 5,120,867, incoφorated by reference herein. CDBI is a measure of the uniformity of comonomer distribution within the sample and is measured by the process described in PCT pubUcation WO 9303093, pubUshed 2-18-93, which is incoφorated by reference herein. The physical blends of this invention are preferably produced by conventional blending or compounding techniques known in the art For example the desired amoφhous polypropylene and crystaUine polypropylene can be dissolved in hot solvent and then precipitated in acetone, washed with water and dried in vacuum to produce a blend according to this invention. Preferred compositions comprising both the amoφhous polypropylene and the isotactic polypropylene described herein have heat of fusion (also caUed enthalpy of melting) as measured by DSC (first peak, second melt) of about 50 J/g or less, even more preferably 35 J/g or less. Another desirable feature of preferred compositions comprising both amoφhous polypropylene and crystalUne polypropylene made herein is that they have a melting point (first peak, second melt) of about 100 °C or more, more preferably about 120 °C or more. In a particularly preferred embodiment these compositions have a Tm between about 130 °C and 160 °C. Likewise in a preferred embodiment the compositions described herein have a heat of fusion of 11 J/g or more. The actual value is dependent on the amount of amoφhous material present. For example in the data presented below, the composition of isotactic polypropylene alone had an enthalphy of melting of 84.5 J/g, The composition produced by using one amoφhous catalyst and one isotactic catalyst together in a one to one ratio had an enthalphy of melting of 33.22 J/g. The composition produced by using one amoφhous catalyst and one isotactic catalyst together in a two to one ratio had an enthalphy of melting of 23.43 J/g. The composition produced by using one amoφhous catalyst and one isotactic catalyst together in a five to one ratio had an enthalphy of melting of 11.4 J/g. Process of Polymerization In accordance with a preferred procedure the selected catalyst system (consisting of a mono-Cp transition metal compound, a bis-Cp transition metal compound and an activator) for the production of an amoφhous/crystaUine polypropylene blend may be used to produce such blends by solution, slurry or bulk polymerization using the propylene or an inert solvent such as toluene or hexane as the polymerization dUuent in which the selected catalyst is dissolved in an amount sufficient to yield the type of polymer blend desired. The most preferred polymerization processes are the solution phase or bulk polymerization processes wherein the reactor is controUed at such a temperature and pressure as to maintain a homogeneous polymer blend in the reactor. Generally the polymerization process is carried out with a pressure of from about 10 to about 1000 psi (68.9 KPa - 6890 KPa), most preferably from about 40 to 600 psi (276 KPa - 4134 KPa). The polymerization dUuent is maintained at a temperature of from about -10°C to about 160°C, preferably from about 20°C to about 140°C, and most preferably from about 30°C to about 120°C. The catalyst systems used by the process of this invention may also be employed in a high temperature/pressure polymerization process. In such, the pressure can be in the range of 5,000-40,000 psi (34 - 276 MPa) and the temperature in the range of 120- 300°C. The polymerization may be carried out as a batchwise slurry, solution or bulk polymerization or as a continuous polymerization process. The procedure of continuous polymerization process is preferred, in which event propylene and catalyst are continuously suppUed to the reaction zone in amounts equal to the propylene and catalyst removed from the reaction zone with the polymer blend in the product stream. The catalyst system described herein may optionally be placed on a support medium and employed in such polymerization processes as gas phase polymerization. The monomer for such process may comprise propylene alone for the production of an amoφhous/crystalUne polypropylene blend. When an alumoxane or aluminum based Lewis acid is used as the activator, the aluminum to transition metal ratio is preferably from about 1:1 to about 2000:1, more preferably from about 1:1 to about 1000:1. When a non-coordinating anion activator is used the activator to transition metal ratio is preferably from about 5: 1 to about 1:5, more preferably from 2:1 to 1:1. The reaction time is preferably from about 1 second to 10 hours depending on the exact process used. AdditionaUy, scavenging agents may be employed during polymerization of olefins. Hydrogen may be used to adjust polymer blend molecular weight The polyolefin compositions of this invention whether formed in situ or by physical blending are preferably used in any thermoplastic elastomer appUcation. Examples include uses in, inter alia, molded parts, films, tubing, hose, sheeting, wire and cable coating, adhesives, shoesoles, bumpers, gaskets, beUows, films, fibers, elastic fibers, nonwovens, surgical gowns and medical devices. Particularly desirable uses include use in diaper waist bands, use in melt blown fibers of woven and non-woven appUcations such as diapers and surgical drapes and gowns. Further desired uses include food wrap appUcations either with the blend alone or in combination with another layer. The products of this invention can also be used in any known thermoplastic elastomer appUcation. Examples Molecular weight (Mw and Mn) were measured by Gel Permeation Chromotography using a Waters 150-CN Gel Permeation Chromatograph equipped with a differential refractive index (DRI) detector and polystyrene standards. Polymer samples were dissolved in trichlorobenzene solvent at 165 °C and the solutions were run at 145°C using three Shodex GPC AT-80 M/S columns in series. This general technique is discussed in "Liquid Chromotography of Polymers and Related Materials III"' J. Cazes Ed., Marcel Decker, 1981, page 207, which is incoφorated by eference herein. No corrections for column spreading were employed; however, data on generally accepted standards, e.g. National Bureau of Standards Polyethylene 1475, demonstrated a precision with 0.1 units for Mw/Mn which was calculated from elution times. The numerical analyses were performed using Expert Ease™ software av∑tilable from Waters Coφoration. The melting temperature (Tm, first peak, second melt) of the polymer is measured by using Dupont Instruments 912 differiential scanning calorimeter (DSC) or a DuPont DSC 9900 each of which is equipped with the standard numerical analysis software. The area under the melting peak represents the enthalpy of melting (or heat of fusion) and is reported in Joules per grams(J/g). Standard procedure involved eqmlibrating the sample at 0° C, increasing the temperature at a rate of 10°C/min to 200°C (first melt); remaining at 200° C for 2 min; decreasing the temperature at a rate of 10°C/min to 0°C (crystalUzation temperature) ;remaining at 0° C for 2 min; and increasing the temperature at a rate of 10°C/min to 20°C (second melt). Typical crystalUzation and second melt plots were recorded between 0° and 180° C. Tensile, elongation, yield stress and modulus were measure according to ASTM D 412 on an Instron TensUe Tester. Percent elastic recovery was determined according to the following equation: % recovery = [(2Lo-L')/Lo] x 100; wherein Lo = original length of the sample, L' is the length of the sample after being held at 200% elongation for 10 minutes and then released and aUowed to relax for 10 minutes at room temperature. Transition metal compounds were prepared as described in U.S. Patent Nos. 5,264,405 and 5,120,867. Non-coordinating anions were prepared as described in U.S. Patent No. 5,120,867. Methylalumoxane (10 wt% in toluene) was purchased from Ethyl Coφoration, (now Albemarle.) Me2Si(IND)2HfMe2 was made according to the procedures described in USSN 08/159,888. Example A: Physical blend Isotactic polypropylene (iPP) and amoφhous polypropylene (aPP) were blended in solution in the ratios shown in Table 1. Desired amounts of each component were dissolved together in hot toluene, precipitated in acetone, washed with water and finally dried in a vacuum oven. The individual components were prepared as foUows: The amoφhous polypropylene used in this study (in both Tables 1 and 3) was synthesized by using a catalyst system of alumoxane in combination with Me2Si(Me4C5)(N-c-Ci2H23)TCl2. The synthesis was done in a 1-Uter zipperclave reactor. At room temperature, 400 ml of propylene was charged into the reactor with 2.0 ml of a ten weight percent solution of methylalumoxane (MAO) in toluene subsequently added as a scavenger. The temperature was then increased to 40°C. A preactivated catalyst solution of Me2Si(Me4C5)(N-c- Ci2H23)TiCl2 (2.09 x 10 -3 mmol) and 2 ml of a ten weight percent solution of methylalumoxane (MAO) in toluene was then pressurized into the reactor via high pressure nitrogen. The reaction was run for 60 minutes prior to venting and cooling and yielded 125.7 g of rubbery polymer once dried. The resulting product had no detectable melting temperature as determined by DSC. The molecular weight as measured by GPC was Mn = 287,800 and Mw/Mn was 2.91. Isotactic polypropylene (iPpl) was synthesized foUowing the general procedure described above. In a one Uter Zipperclave reactor at room temperature, 400 ml of toluene were charged into the reactor. In a separate vial, 50 mg of dimethylsUyl bis(indenyl)hafhium dimethyl and 80 mg of N,N- d-Lmemylanilinium tetrakis(pentaflourophenyl)boron were mixed with 3 ml of toluene. This solution was then pressurized into the reactor via cannula and high pressure nitrogen. Liquid propylene (100 ml) was then charged into the reactor, the temperature was raised to 40 °C and aUowed to react for 10 minutes. The reactor was vented and cooled. The final solution was precipitated in acetone and vacuum dried. Yield was 50 g. This polymer is referred to as iPPl . Melting point of the polymer product was 136.9 °C, the Mn was 159,200, and the Mw/Mn was 1.98. The blends of the amoφhous polypropylene made above and iPPl are reported in Table 1. Table 2 summarizes the crystalline melting temperatures (T m in °C, second melt) and the heats of fusion (Hf in J/g) for these blends, as measured by DSC. The amoφhous polypropylene was also blended with commerciaUy available isotactic polypropylene(iPp2) having the characteristics of an Mn of about 49,100 and Mw/Mn of 5.5. Blends of amoφhous polypropylene and iPP 2 are reported in Table 3. Such iPP 2 is commercially ava able as ESCORENE™ PP1042 Polymer from Exxon Chemical Company. The various blends and their physical properties are reported in Tables 1, 2, 3 and 4. Table 1 - iPP/aPP Blend ND = Not Determined Table 2 iPP 1 (wt%) T m (°C) H f (J/g) 10 132.2 6.7 20 133.8 10.7 40 134.5 20.2 60 136.6 40.5 100 136.9 68.4 Table 3 - iPP/aPP Blend Not Determined Table 4 iPP 2 (wt%) T m (°C) H f (J/g) 10 157 6.5 100 163 79.8 Example B: In situ blends Example 1. The polymerization run was performed in a 1-Uter autoclave reactor equipped with a paddle stirrer, an external water jacket for temperature control, a regulated supply of dry nitrogen, ethylene, propylene and hexane, and a septum inlet for introduction of other solvents or comonomers, transition metal compound and alumoxane solutions. The reactor was dried and degassed thoroughly prior to use. A typical run consisted of injecting 400 ml of propylene and 2 ml of 10 wt% MAO into the reactor, and heating it to 40 °C. A solution (1.0 ml) contaimng Me2Si(Me4C5)(N-c-Ci2H23)TiCl2 (13.4 mg) dissolved in 10 ml of toluene was then added to the reactor. The reactor was maintained at 40 °C during the 15 minute polymerization. The reaction was ceased by rapidly cooling and venting the system and the catalyst was killed by thoroughly exposing to product to air. The solvent was evaporated off of the polymer by a stream of nitrogen and if needed, the sample was further dried by vacuum. Polypropylene was recovered (64.9 g, Mw = 1,824,000, MWD = 1.767, m = 0.443, mmmm = 0.037, r = 0.557, rrrr = 0.062). Example 2. Using the same reactor design and general procedure already described, 400 ml of propylene and 2 ml of 10 wt% MAO were added to the reactor. The reactor was heated to 40 °C prior to introduction of 1.0 ml of a 10 ml toluene solution containing Me2Si(Me4C5)(N-c-Ci2H23)TiCl2 (17.0 mg) and Me2Si(H4lnd)2ZιCl2 (3.2 mg)(Ind = indenyl). The reactor was maintained at 40°C during the 10 minute polymerization. The reaction was ceased by rapidly cooling and venting the system and the catalyst was kiUed by thoroughly exposing to product to air. The solvent was evaporated off of the polymer by a stream of nitrogen and if needed, the sample was further dried by vacuum. Polypropylene was recovered (63.6 g, Mw = 1,282,000, MWD = 6J7 (bimodal), m = 0.508, mmmm = 0J42, r = 0.493, rrrr = 0.064). Example 3. Using the same reactor design and general procedure already described, 400 ml of propylene and 2 ml of 10 wt% MAO were added to the reactor. The reactor was heated to 40 °C prior to introduction of 1.0 ml of a 10 ml toluene solution containing Me2Si(Me4C5)(N-c-Ci2H23)TiCl2 (9.0 mg) and Me2Si(H4lnd)2ZιCl2 (4.3 mg). The reactor was maintained at 40 °C during the 15 minute polymerization. The reaction was ceased by rapidly cooUng and venting the system and the catalyst was kiUed by thoroughly exposing to product to air. The solvent was evaporated off of the polymer by a stream of nitrogen and if needed, the sample was further dried by vacuum. Polypropylene was recovered (69.8 g, Mw = 914,000, MWD = 12.6 (bimodal), m = 0.577, mmmm = 0.267, r = 0.423, rrrr = 0.073). Example 4. Using the same reactor design and general procedure already described, 400 ml of propylene and 2 ml of 10 wt% MAO were added to the reactor. The reactor was heated to 40 °C prior to introduction of 1.0 ml of a 10 ml toluene solution containing Me2Si(Me4C5)(N-c-Ci2H23)TiCl2 (6.8 mg) and Me2Si(H4lnd)22-rCl2 (6.5 mg). The reactor was maintained at 40 °C during the 15 minute polymerization. The reaction was ceased by rapidly cooUng and venting the system and the catalyst was killed by thoroughly exposing to product to air. The solvent was evaporated off of the polymer by a stream of nitrogen and if needed, the sample was further dried by vacuum. Polypropylene was recovered (71.6 g, Mw = 742,000, MWD = 22.3 (bimodal), m = 0.638, mmmm = 0.353, r = 0.362, rrrr = 0.049). The proportions of the catalysts and the product data are reported in the tables below. The in situ polymer products had bimodal molecular weight distributions(Mw/Mn). They typicaUy had a lower peak at 5 x lθ4 daltons corresponding to the pure isotactic polypropylene and a higher Mw peak at 1.8 xlO^ daltons corresponding to the amoφhous polypropylene. The GPC molecular weight distribution curves of examples 2,3 and 4 from table 5 are presented in figure 1. It has been found that by blending isotactic polypropylene and amoφhous polypropylene together or producing the blend in-situ, we obtained products with greatly improved mechanical strength that also have good rubber recovery properties. For example, by blending 10 wt% of isotactic polypropylene with 90 wt% of amoφhous polypropylene together, we obtained a product with 970 psi(6.7 MPa) tensUe strength and 95% rubber recovery compared to 550 psi (3.8 MPa) tensUe strength and 100% rubber recovery of the pure amoφhous polypropylene. As we increased isotactic polypropylene component to 20 wt%, the tensUe strength increased to 1630 psi (11.2 MPa) whUe the rubber recovery was maintained at 94%. At 40 wt% isotactic polypropylene, the tensile strength further increased to 2290 psi (15.8 MPa) whUe good rubber recovery of 82% was maintained. Furthermore, DSC characterization revealed that the amoφhous polypropylene/isotactic polypropylene blends still retained high crystaUine melting points close to the pure isotactic polypropylene (see Tables 2 and 4 above). In addition we also found that the in situ blends of isotactic polypropylene and amoφhous polypropylene have properties superior to comparable physical blends, especiaUy at higher temperatures. Thus we have found a one step method to produce a desirable thermoplastic elastomer. Table 7 compares Example 3 in Table 6 to 40-60/iPP-amoφhous polypropylene blend in Table 3. Table 5 Ex. wt% Zr wt% wt%* iPP in Tm (°C) Mw cat. Ti cat. product (daltons) 1 0 100 0 amoφhous 1.8 x 10 6 2 16.7 83.3 12 143.6 bimodal 1.8 x 10^ 5.6 x 10 4 3 33.3 66.7 40 146J bimodal 1.9 x 10 6 5.7 x 10 4 4 50.0 50.0 52 146.6 bimodal 1.8 x 10^ 5.7 x 10 4 * wt% was calculated from the heat of fusion as measured by DSC. Tabje6 @ Sample broke during testing. Table 7 Example 5. Using the same reactor design and general procedure already described, 400 ml of hexane and 2 ml of a triisobutyl aluminum scavenger solution (0.1 ml of 25 wt% of triisobutyl aluminum in 2 ml of toluene) were charged into the one Uter Zipperclave reactor. After heating to 40 °C a mixed catalyst solution (1 ml of Solution A and 1.5 ml of Solution B) was cannulated into the reactor. Solution A is 7.49 mg of Me2Si(Ind)2HfMe2 and 12.01 mg of N,N- dimethyl--niUmumtetrakis(pentafluorophenyl)borate (DM AH) in 10 ml toluene. Solution B is 13.12 mg of Me2Si(Me4C5)(N-c-Ci2H23)TiMe2 and 24.02 mg of DMAH in 10 ml of toluene. The reactor was heated to 60 °C and 50 ml of Uquid polypropylene was charged into the reactor and aUowed to polymerize for 30 minutes. The reaction was ceased by rapidly cooling and venting the system and the catalyst was kiUed by thoroughly exposing to product to air. The solution was precipitated in acetone and dried in a vacuum oven. Polypropylene was recovered (18.69 g, Tm = 133 °C (first melt) Mw = 208,000, Mn = 113,000 MWD = 1.84). This example was repeated twice, each time the catalyst ratio was altered. The data are presented in Table 8. Table 8 Ex. 5-1 Ex. 5-2 Ex. 5-3 Catalyst molar ratio (B:A) 3:1 2:1 4:1 Mw 208,000 203,000 227,000 Mn 113,000 111,000 129,000 Elastic Recovery 95% 75% 100% at 25 °C* * sample tested 10 minutes after stress was removed. Example 6. Polymerization was then conducted in a five gallon reactor as follows. Two catalyst solutions were prepared. Solution C was prepared by combining 28.44 mg of Me2Si(Ind)2HfMe2 with 49.72 mg of DMAH in 5 ml of toluene and thereafter diluting to a total volume of 40 ml with toluene. Solution D was prepared by combining 74.43 mg of Me2Si(Me4C5)(N-c-Ci2H23)TiMe2 and 130.64 mg of DMAH in 5 ml of toluene and therefter dUuting to a total volume of 60 ml with toluene. Solution C was then combined with solution D, for a total volume of 100 ml, and thereafter placed in a stainless steel cylinder. The five gaUon reactor was cleaned throughly with toluene followed by hexane, purged with nitrogen and dried at 100 °C for at least an hour. Hexane (22.4 lbs, 10.17 kg) was then added to the reactor with 34 g of trisobutylaluminum scavenger (prepared as in example 5). The reactor was stirred for two minutes then heated to 60 °C. 2J7 pounds (0.99 kg) of Uquid propylene were then charged into the reactor with 25 ml of the catalyst solution. The rest of the catalyst solution was added in 25 ml quantities at 5 minute intervals. The polymerization was aUowed to run for one hour after the last catalyst addition. The solution was then discharged into a stripping tank half-fiUed with water and stripped at 70 °C for four hours. The reaction was repeated 8 more times. The data are presented in Tables 9 & 10. Table 9 * wt% iPP calculated based on DSC heat of fusion. Table 10 Ex. Yield stress Modulus TensUe Elong. Elas. Rec. (psi/MPa) (psi/MPa) (psi/MPa) (%) (%) 6-3 300/2.0 620/4.2 740/5J 2060 85 6-4 301/2.0 620/4.2 740/5J 2060 85 6-5 320/2.2 710/4.8 820/5.6 1860 76 6-6 290/1.9 590/4.0 615/6150 1850 74 6-7 330/2.2 780/5.3 805/5.5 1750 72 6-8 294/2.0 600/4J 770/5.3 2130 84 6-9 320/2.2 770/5.3 820/5.6 1870 90 Comparative Example 7. The procedure and reaction conditions of example 5 were repeated. Instead of charging a mixed metaUocene, only 2 ml of solution A were used. At the end of the polymerization, we obtained 14.45 g of isotactic polypropylene with an Mw of 68,000; Mn of 30,000, Mw/Mn of 2.27 and Tm 126 °C and a heat of fusion of 68 J/g. Comparative Example 8. The procedure and reaction conditions of example 5 were repeated. Instead of charging a mixed metaUocene, only 1 ml of solution B were used. At the end of the polymerization, we obtained 5.4 g of amoφhous polypropylene with an Mw of 453,000; Mn of 254,000, Mw/Mn of 1.78 and no dectectable melting point The compositions described above can be used in many important appUcations such as elastic films, melt blown elastic fibers, woven articles and non- woven articles. For example diaper waist bands can be produced using the elastic films that can be produced using the blends of this invention. Additionally, the described blends wiU be also useful in traditional TPE appUcations such as hose, tubing, sheeting, wire and cable, adhesive, shoe soles, automotive bumpers, window gaskets, beUows, and medical devices. AU references described above, including test methods and priority documents, are incoφorated by reference herein. As is apparent from the foregoing general description and the specific embodiments, whUe forms of the invention have been illustrated and described, various modifications can be made without departing from the spirit and scope of the invention. Accordingly, it is not intended that the invention be limited thereby.

Claims: CLAIMS: 1. A process for producing a polypropylene composition comprising: selecting a first catalyst system comprising a monocyclopentadienyl transition metal compound capable of producing an amoφhous polypropylene having a weight average molecular weight (Mw) of at least about 150,000 and a molecular weight distribution (Mw/Mn) of less than 3; selecting a second catalyst system comprising a bis-cyclopentadienyl transition metal compound capable of producing a crystalline polypropylene having a Mw of less than about 300,000 and a Mw/Mn of less than 3; provided that the first and second catalyst systems are selected such that the Mw of the amoφhous polypropylene is greater than the Mw of the crystaUine polypropylene; and contacting the first and second catalyst systems under polymerization conditions in a polymerization reactor with olefin monomers comprising propylene. 2. The process of claim 1 , wherein the first catalyst system comprises a symmetrically substituted mono-cyclopentadienyl transition metal compound used in combination with an alumoxane or a compatible, non-coordinating anion activator; and the second catalyst system comprises a bridged bis-cyclopentadienyl transition metal compound used in combination with an alumoxane or a compatible, non-coordinating anion activator. 3. The process of any preceding claim wherein the transition metal compound of the first catalyst system is represented by the formula: where A' is a bridging Group; (JS' Z _2) is a heteroatom Ugand in which J is an element from Group 15 of the Periodic Table of Elements with a coordination number of 3 or an element from Group 16 with a coordination number of 2, S' is a radical Group which is a hydrocarbyl, substituted hydrocarbyl, halocarbyl, substituted halocarbyl, hydrocarbyl-substituted organometaUoid, or halocarbyl- substituted organometaUoid; and z is the coordination number of the element J; L' is an olefin, diolefin, aryne, amine, phosphine, ether, or sulfide Ugand, or any other neutral Lewis base; X\ and X2 are, independently, hydride radicals, hydrocarbyl radicals, substituted hydrocarbyl radicals, halocarbyl radicals, substituted halocarbyl radicals, and hydrocarbyl- and halocarbyl-substituted organometaUoid radicals, substituted pnictogen radicals, or substituted chalcogen radicals; or X ] and X2 are joined and bound to the metal atom to form a metaUacycle ring containing from about 3 to about 20 carbon atoms; or Xj and X2 together can be an olefin, diolefin or aryne Ugand; or when Lewis-acid activators which are capable of donating an Xi Ugand to the transition metal component are used, Xj and X2 may independently be a halogen, alkoxide, aryloxide, amide, phosphide or other univalent anionic Ugand or both; or Xi and X2 can also be joined to form a anionic chelating Ugand provided that Xi and X 2 are not a substituted or unsubstituted cyclopentadienyl ring; z is the coordination number of the element J; w is an integer from 0 to 3; M is titanium; S v is a radical group which is a hydrocarbyl, substituted-hydrocarbyl, halocarbyl, substituted-halocarbyl, hydrocarbyl- substituted organometalloid, halocarbyl-substituted organometalloid, disubstituted boron, disubstituted pnictogen, substituted chalcogen or halogen radical where the subscript "v" denotes the carbon atom on the cyclopentadienyl ring to which the substituent is bonded and where there can be zero, two or four substituents, S, on the cyclopentadienyl ring, provided that the cyclopentadienyl ring is symmetricaUy substituted in the 2 and 5 positions and/or 3 and 4 positions with S groups that are within 2 carbons of each other; and the second catalyst system is represented by the formula: wherein M is Ti, Zr or Hf; "v" denotes the carbon atom on the Cp-ring to which the substituent is bonded; each substituent Group S or S" is, independently, a radical group which is a hydrocarbyl, substituted-hydrocarbyl, halocarbyl, substituted-halocarbyl, hydrocarbyl-substituted organometaUoid, halocarbyl- substituted organometaUoid, disubstituted boron, disubstituted pnictogen, substituted chalcogen or halogen radicals; A' is a bridging Group; X\ and X2 are, independently, hydride radicals, hydrocarbyl radicals, substituted hydrocarbyl radicals, halocarbyl radicals, substituted halocarbyl radicals, and hydrocarbyl- and halocarbyl-substituted organometalloid radicals, substituted pnictogen radicals, or substituted chalcogen radicals; or Xj and X2 are joined and bound to the metal atom to form a metallacycle ring containing from about 3 to about 20 carbon atoms; or X\ and X2 together can be an olefin, diolefin or aryne gand; or when Lewis-acid activators which are capable of donating an Xl Ugand to the transition metal component are used, X\ and X2 may independently be a halogen, alkoxide, aryloxide, amide, phosphide or other univalent anionic Ugand or both Xl and X2 can also be joined to form a anionic chelating Ugand and with the proviso that X] and X 2 are not a substituted or unsubstituted cyclopentadienyl ring. 4. The process of any of the preceding claims wherein the first and second catalyst systems comprise one of the following combinations: (1) Me2Si(Me4C5)(N-c-Ci2H23)TiCl2 and Me2Si(H4- d)2Z-Cl2 activated with an alumoxane; (2) Me2Si(Me4C5)(N-c-Ci2H23)TiCl2 and Me2Si(H4lnd)2H l2 activated with an alumoxane; (3) Me2Si(Me4C5)(N-c-Ci2H23)TiCl2 and Me2Si(2-MeInd)2ZrCl2 activated with an alumoxane; (4) Me2Si(Me4C5)(N-c-Ci2H23)TiCl2 and Me2Si(2-MeInd)2HfCl2 activated with an alumoxane; (5) Me Si(Me4C 5 )(N-c-Ci2H23)TiCl2 and Me2C(C 5 H 4 )(l-fluorenyl)ZιCl2 activated with an alumoxane. (6) Me2Si(Me4C5)(N-c-Cj2H23)TiMe2 and Me2Si(H4- d)2ZrMe2 activated with a non-coordinating anion activator; (7) Me2Si(Me4C5)(N-c-Cχ2H23)TiMe2 and Me2Si(H4- d)2HfMe2 activated with a non-coordinating anion activator; (8) Me2Si(Mβ4C5)(N-c-Ci2H23)TiMe2 and Me2Si(2-MeInd)2ZrMe2 activated with a non-coordinating anion activator; (9) Me2Si(Mβ4C5)(N-c-Ci2H23)TiMe2 and Me2Si(2-MeInd)2HfMe2 activated with a non-coordinating anion activator; or (10) Me2Si(Me4C5)(N-c-Ci2H 3)TiMe2 and Me2C(C5H4)(l-fluorenyl)ZrMe2 activated with a non-coordinating anion activator. 5. The process of claim 1 wherein the transition metal compound of the first catalyst system is present at one to ten times, preferably about two to four times, the amount of the transition metal compound of the second catalyst system. 6. A thermoplastic elastomer produced by the process of any one of the preceding claims. 7. A polypropylene blend composition comprising: from about 60 to 90 weight percent of an amoφhous polypropylene having a Mw of at least 150,000 and a Mw/Mn of 3 or less and from about 40 to 10 weight percent of a crystalUne polypropylene having a Mw of less than 300,000, provided that the Mw of the amoφhous polypropylene is greater than the Mw of the crystalUne polypropylene. 8. The composition of claim 7 wherein the amoφhous polypropylene has a Mw of at least 300,000 and or wherein the crystalUne polypropylene has a Mw between 150,000 and 20,000 and/or the amoφhous polypropylene has a Mw/Mn of less than 3 and/or the composition has a bimodal molecular weight distribution. 9. The composition of any preceding claim wherein the amoφhous polypropylene has a heat of fusion as measured by Differential Scanning Calorimetry of about 10 J/g or less and/or the composition has a melting point as measured by Differential Scanning Calorimetry in the range of from 130°C to 160°C. 10. An article of manufacture of the composition of claim 7. 11. The use of the composition of claim 7, in or as, a film, a molded part, a fiber, a tube, a woven article or a non-woven article.

Inventors: CANICH JO ANN MARIE, LICCIARDI GARY FREDERICK, YANG HENRY WU-HSIANG, CANICH, JO, ANN, MARIE, LICCIARDI, GARY, FREDERICK, YANG, HENRY, WU-HSIANG
Applicants: EXXON CHEMICAL PATENTS INC, EXXON CHEMICAL PATENTS INC.
Application year: 1996
Main classification: C08L23
IPC codes: C08F4, C08F110, C08J5, C08L23, D01F6, D03D15