Curable compositions and their use for the formation of a printing material

Abstract: A curing composition comprising a water soluble high-molecular compound (P1) having a cationic group in a molecule and a water soluble high-molecular compound (P2) having a side chain provided with a condensable functional group. A curing composition comprising a water soluble high-molecular compound (P1) having a cationic group in a molecule and a polyfunctional hydrophilic monomer or oligomer (P3) having two or more (meth)acryloyl groups in a molecule. Printing media comprising said curing compositions and process for producing a print product with the use of said curing compositions.

Description: BACKGROUND OF THE INVENTION Field of The Invention The present invention relates to an improved curing composition comprising a specific water soluble high-molecular compound having a cationic group in the principal molecular chain thereof and another specific water soluble high-molecular compound having a crosslinking property, which is capable of providing a condensed and crosslinked structure or a polymerized and crosslinked structure upon the application of thermal energy or the irradiation of ultraviolet rays and which enables to form a desirable ink-receiving layer which excels in waterfastness and ink receiving property. The present invention includes a printing medium formed of said curing composition and a process for producing a print product with the use of said curing composition. Related Background Art In recent years, an ink jet recording system has made a rapid progress in the digital recording system field, and it has been widely using as an outputting terminal printer for personal computers, particularly used in offices. This situation is based on an outcome that a recording apparatus having a desirable printability for a recording medium having a hygroscopic property to water-based ink has been developed. As such ink jet recording system, there have been proposed various ink jet recording apparatus. These ink jet recording apparatus are mostly of the so-called bubble jet system in which thermal energy is utilized for discharging ink. In the bubble jet recording apparatus, there is usually used water-based ink for performing printing for a printing medium. Therefore, particularly in the case where the bubble jet recording apparatus is used as a printing apparatus for producing a volume of print products, a due care is necessary to be made about printing mediums to be dedicated for printing because they are often poor in absorption of said water-based ink. As such printing medium dedicated for printing in this, there can be mentioned, for examples, metal members, plastic members, rubber members, ceramics, fabrics, leathers, glass products, and food products. In the case where the printing medium does not have a sufficient property of absorbing the water-based ink, the printing medium is necessary to be designed such that it has an ink-absorptive layer (that is, an ink-receiving layer). By the way, there are known coating compositions for OHP films which have been designed to be suitable for the printing by the ink jet printing apparatus. However, these coating compositions are not suitable for use in the case of industrially printing any of the above mentioned materials poor in absorption of the water-based ink by the ink jet printing apparatus, because any of the coating compositions is difficult to form a film as an ink-receiving layer which is insufficient in adhesion, coating suitability, and durability against a substrate comprising any of the above mentioned materials dedicated for printing by the ink jet printing apparatus. Now, as for the ink-receiving layer formed on such material poor in absorption of the water-based ink so that printing by the ink jet printing apparatus can be desirably conducted, the ink-receiving layer is necessary to be formed of a material which satisfies the following conditions: (i) the material enables to form a desirable film as an ink-receiving layer within a short period of time, (ii) the material enables to form a desirable film as an ink-receiving layer which has a sufficient adhesion against a substrate, (iii) the material enables to form a desirable film as an ink-receiving layer which allows ink to be shortly fixed thereon, (iv) the material enables to form a desirable film as an ink-receiving layer which allows coloring components (dyes and pigments) of ink to be strongly fixed thereon, (v) the material enables to form a desirable film as an ink-receiving layer which allows the formation of a clear image at a high resolution thereon, and (vi) the material enables to form a desirable film as an ink-receiving layer which excels in fastness properties. As the material by which a desirable film as an ink-receiving layer which satisfies these requirements is formed, it is considered effective to use a crosslinkable high-molecular compound and an activation energy-curable hydrophilic oligomer. As for the recording medium, particularly for instance, the OHP film, dedicated for the printing by the ink jet printing apparatus, there have been made various proposals in view of attaining a desirable ink absorption therefor and attaining a desirable waterfastness for a print product. Such proposals are disclosed, for example, in Japanese Unexamined Patent Publications Nos. 94379/1987 (corresponding to U.S. Pat. No. 4,741,969), 94380/1987, 221591/1987, 242578/1987, 229685/1989, and 286886/1989. Particularly, U.S. Pat. No. 4,741,969 discloses an aqueous ink recording sheet having an ink-receiving layer formed by photo-curing an anionic synthetic resin having a photopolymerizable double bond. However, in the formation of the ink-receiving layer in this document, it is essential to use polymer reaction of bonding an independent reactive monomer to a side chain of a given high-molecular compound. Because of this, there is a problem in that the production cost of the aqueous ink recording sheet unavoidably becomes high. In addition, there is also another problem in that it is quite difficult to stably synthesize a desired synthetic resin at a high reproducibility. Japanese Unexamined Patent Publication No. 94380/1987 discloses an aqueous ink recording sheet having an ink-receiving layer formed by photo-curing a cationic synthetic resin having a photopolymerizable double bond. However, in the formation of the ink-receiving layer in this document, it is essential to use polymer reaction of bonding an independent reactive monomer to a side chain of a given high-molecular compound. Because of this, there is a problem in that the production cost of the aqueous ink recording sheet unavoidably becomes high. In addition, there is also another problem in that it is quite difficult to stably synthesize a desired synthetic resin at a high reproducibility. Japanese Unexamined Patent Publication No. 221591/1987 discloses an aqueous ink recording sheet having a two-layered ink-receiving layer comprising a coating layer comprised of an anionic acrylic copolymer cured with the irradiation of ultraviolet rays as a principal component and a coating layer comprised of a cationic acrylic copolymer cured with the irradiation of ultraviolet rays as a principal component. The two-layered ink-receiving layer described in this document is featured in utilizing an ion complex present in the interfacial region between one layer comprised of an electrolytic high-molecular compound having a cationic property and the other layer comprised of an electrolytic high molecular compound having an anionic property. And according to the description of this document, it is understood that due to the presence of a solvent of an aqueous ink and molecules of a dye in a strong interaction (or an attraction) between an anion and cation which are locally distributed in the two-layered ink-receiving layer, not only molecules of the solvent but also the dye molecules are strongly prevented from being mobilized to result in providing an improvement in the apparent ink-fixing property and waterfastness. However, in practice, the use of the two-layered ink-receiving layer entails a drawback in that the aqueous ink is difficult to be shortly dried and therefore, there cannot be attained desirable fixing for the aqueous ink. Japanese Unexamined Patent Publication No. 242578/1987 discloses a composition comprising a mixture of a cationic high-molecular compound and a high-molecular compound crosslinkable with the irradiation of ultraviolet rays which is suitable for the formation of an ink-receiving layer. According to the description of this document, it is understood that an ink-receiving layer formed of said composition is capable of trapping a dye of an aqueous ink by virtue of the cationic functional group of the cationic high-molecular compound, and when the ink-receiving layer is crosslinked with the irradiation of ultraviolet rays, it becomes to have a structure with waterfastness. However, as for the ink-receiving layer, there are problems in that the two high-molecular compounds by which the ink-receiving layer is constituted are liable to form a polyion complex between them, resulting in a marked reduction in the solubility of the composition to solvents used upon the formation of the ink-receiving layer by way of a coating process, and in addition, the ink-receiving layer formed is of a remarkably inferior preservation stability even at room temperature and because of this, the ink-receiving property of the ink-receiving layer is gradually deteriorated during the storage. Japanese Unexamined Patent Publication No. 229685/1989 discloses an ink-receiving layer formed by subjecting a composition composed of a water soluble high-molecular compound and a hydrophilic oligomer having a terminal acryloyl group to crosslinking treatment. However, in practice, there is a considerable difference between the hydrophilic property possessed by the ink-receiving layer and the hydrophilic property required for an ink-receiving layer used in the ink jet printing using a water-based ink. Particularly, the ink-receiving layer described in this document is difficult to satisfy the requirements relating to the ink receiving quantity and ink penetration speed in the printing by means of a color ink jet printing apparatus which has been widely using in recent years. Japanese Unexamined Patent Publication No. 286886/1989 discloses curing materials comprising monofunctional or multifunctional monomers or oligomers which are suitable for the formation of an ink-receiving layer. This document also discloses materials capable of providing a cationic group required for the fixing of a dye. However the materials capable of providing a cationic group described in this document are monofunctional monomers and the multifunctional materials described in this document have no cationic group and therefore, they cannot attain the formation of an ink-receiving layer having a desirable ink absorption rate and a desirable waterfastness at a curing rate practically employed upon the layer formation. US-A-3,629,161 discloses a water-insoluble, cationic, perm-selective membrane comprising an ionene polymer cross-linked to a polyvinyl alcohol substrate. The ionene polymer is represented by the formula shown on column 2, lines 22 to 25 of this document and can be prepared by reacting a ditertiary amine with a dihalogen organic compound shown on column 2, line 44 of this document. After curing, a reaction product comprising polyvinyl alcohol having a side-chain provided with a condensable functional group is contained in the polymeric hardened composition. Thus, D1 provides perm-selective materials for water-insoluble polyelectrolytic membranes, e.g. for separator membranes of various types of batteries, wherein the ionene polymer improves the ionicity to influence the permeation properties of the polyelectrolytic membranes. WO-A-96/18496 provides a composition for an ink-receptive layer comprising a random copolymer and a cationic resin. The random copolymer may be prepared from a vinyl amide, preferably vinyl pyrollidone and acrylic acid or methacrylic acid or their esters. The cationic resin may be a conventional one, preferably a high molecular weight poly(hydroxyalkene dimethylammonium chloride) manufactured under the designation AGEFLOC® A-50HV. The latter document is prior art according to Art. 54(3)(4) EPC. As apparent from the above description, in the prior art, there has not proposed a crosslinkable composition which enables to form an ink-receiving layer of exhibiting a desirable absorptivity and absorption rate for water-based ink while exhibiting a fixing property for a coloring material of said water-based ink which are well compatible with the performance of the color ink jet printing apparatus which has been widely using in recent years. SUMMARY OF THE INVENTION A principal object of the present invention is to solve the foregoing problems in the prior art and enable to conduct printing for various products poor in absorption of water-based ink such as metal members, plastic members, rubber members, fabrics, ceramics, leathers, glass products, and food products by means of the ink jet printing apparatus using water-based ink. Another object of the present invention is to provide a curing composition comprising a specific water soluble high-molecular compound having a cationic group and another specific water soluble high-molecular compound having a crosslinking property, which is capable of forming a desirable ink-receiving layer which enable to desirably conduct printing for any of those products above described to thereby obtain print products by the ink jet printing apparatus using water-based ink. A further object of the present invention is to provide a curing composition comprising a specific water soluble high-molecular compound and another specific water soluble high-molecular compound having a crosslinking property, which is capable of forming an ink-receiving layer of exhibiting a desirable absorptivity and absorption rate for water-based ink and a desirable waterfastness while exhibiting a fixing property for a coloring material of said water-based ink which are well compatible with, particularly, the performance of the color ink jet printing apparatus in which water-based ink is used. A further object of the present invention is to provide a printing medium formed using said curing composition. A further object of the present invention is to provide a process for producing a print product using said printing medium. DESCRIPTION OF THE INVENTION AND PREFERRED EMBODIMENTS A first aspect of the present invention lies in a curing composition comprising a water soluble high-molecular compound (P1) having a cationic group in the principal molecular chain thereof, compound (P1) being defined according to claim 1 and a water soluble high-molecular compound (P2) having a side chain provided with a condensable functional group. A second aspect of the present invention lies in a printing medium comprising a substrate and an ink-receiving layer disposed on said substrate, said ink-receiving layer comprising a solid layer obtainable by curing the above curing composition. A third aspect of the present invention lies in the use of the above printing medium for ink-jet printing by performing printing on the ink-receiving layer provided on the substrate of said printing medium with the use of ink, to thereby obtain a print product. In the following, description will be made of the water soluble high-molecular compound (P1) having a cationic group in the principal molecular chain thereof (hereinafter referred to as "compound P1" for simplification purpose) which is used in the present invention. The compound P1 contained in the curing composition according to the present invention exhibits a function of fixing coloring materials such as dyes, pigments, dispersants and the like while exhibiting a function of allowing an ink solvent to readily expand and penetrate chiefly because of the cationic group possessed by the compound P1. The compound P1 may be produced by adding a cationic group to a given water soluble high-molecular compound. Particularly, the compound P1 may be produced, for example, by a manner (1) of providing a water soluble high-molecular compound and introducing a cationic ammonium group into the principal chain of the high-molecular compound or a manner (2) of providing a water soluble high-molecular compound having a side chain with a terminal hydroxyl group and cationizing the hydroxyl group of the high-molecular compound by means of a cationizing agent such as an amino group-bearing compound or the like. In the following, each of the manners (1) and (2) will be detailed. The manner (1) embodying the principal manner of obtaining the high-molecular weight compound (P1) includes (A) alternative addition polymerization between epichlorohidrin and dialkylamine or dialkanol amine to obtain water soluble high-molecular compounds preferably having a number average molecular weight of 2000 to 50000, and (B) alternative addition polymerization between hydrophilic oligomer having opposite molecular chain terminals each having a glycidyl group and asymmetric diamine, dialkylamine or dialkanolamine to obtain water soluble high-molecular compounds preferably having a number average molecular weight of 2000 to 50000. As a typical example of the alternative addition polymerization (A), there can be mentioned the following alternative addition polymerization reaction between epichlorohydrin and dimethylamine. As a specific example of a water soluble high-molecular compound obtained in this case, there can be mentioned a commercially available WISTEX T101 (trademark name, produced by Nagasekasei Kogyo Kabushiki Kaisha; number average molecular weight: about 6000) which has the above described chemical structure. This water soluble high-molecular compound WISEX T101 will be hereinafter referred to as compound P1 (a). As another typical example of the alternative addition polymerization (A), there can be mentioned the following alternative addition polymerization reaction between epichlorohydrin and diethylamine. (wherein, Et indicates CH 2 CH 3 .) As a further typical example of the cross addition polymerization (A), there can be mentioned the following alternative addition polymerization reaction between epichlorohidrin and diethanolamine. (wherein, Et-OH indicates CH 2 CH 2 OH) As a typical example of the cross addition polymerization (B), there can be mentioned the following alternative addition polymerization reaction. (wherein RX indicates a compound such as HC1 or lactic acid.) Specific examples of a water soluble high-molecular compound by way of the alternative addition polymerization (B) are lactates of high-molecular compounds (hereinafter referred to as compound P1 (b)) obtained by way of the following alternative addition polymerization reaction between polyethylene glycol diglycidyl ether which is obtained by reacting polyethylene glycol of 1000 in number average molecular weight with epichlorohidrin, and dimethylamine. Further specific examples of a water soluble high-molecular compound by way of the alternative addition polymerization (B) are high-molecular compounds having a principal chain provided with an ammonium group (hereinafter referred to as compound P1 (c)) obtained by way of the following alternative addition polymerization reaction between polyoxyethylene polyoxypropylene diglycidyl ether which is obtained from a block copolymer of 2000 in number average molecular weight comprising polyethylene oxide and polypropylene oxide by way of glycidylation of the terminal hydroxyl group of said block copolymer, and diethanolamine. Specifically, the water-soluble high-molecular weight compound (P1) may be obtained by the following manner (2). Description will be made of the manner (2). As above described, the manner (2) comprises providing a water soluble high-molecular compound having a side chain with a terminal hydroxyl group and cationizing the hydroxyl group of the high-molecular compound by means of a cationizing agent such as an amino group-bearing compound or the like. The cationizing agent used in the manner (2) can include, for example, those compounds which will be mentioned below. 2,3-epoxypropyltrimethylammonium chloride (trademark name: WISTEX E-100, produced by Nagasekasei Kogyo Kabushiki Kaisha) which has the following chemical structure. 3-chloro-2-hydroxypropyltrimethylammonium chloride (trademark name: WISTEX N-50, produced by Nagasekasei Kogyo Kabushiki Kaisha) which has the following chemical structure. The compound P1 may be produced in accordance with the manner (2) while using any of the above compounds as the cationizing agent. The compound P1 obtained in accordance with the manner (2) includes: (C) water soluble acrylic polymers obtained by cationizing an acrylic ester series copolymer having a side chain with a terminal hydroxyl group, and (D) water soluble cationized polyvinyl alcohols having a molecular chain containing 2 to 15 mole% of cationic group which are obtained from a polyvinyl alcohol of 80 mole% or more in saponification value by cationinzing the hydroxyl group of the polyvinyl alcohol. Specific examples of the water soluble acrylic polymer (C) are water soluble high-molecular compounds obtained from acrylic resin of 150000 in weight average molecular weight comprising a copolymer of 2-hydroxyethylmethacrylate, methymethacrylate, acrylamide and n-butylacrylate being copolymerized at a monomer weight ratio of 20 : 30 : 35 : 15, by cationizing 50% of the hydroxyl groups of the acrylic resin with the use of a cationizing agent comprising 3-chloro-2-hydroxypropyltrimethylammonium chloride (trademark name: WISTEX N-50). These water soluble high-molecular compounds will be hereinafter referred to as compound P1 (d). Another specific examples of the water soluble acrylic polymer (C) are water soluble high-molecular compounds obtained from acrylic resin of 130000 in weight average molecular weight comprising a copolymer of 2-hydroxyethylmethacrylate, methymethacrylate, acrylamide and acrylonitrile being copolymerized at a monomer weight ratio of 20 : 30 : 35 : 10, by cationizing 60% of the hydroxyl groups of the acrylic resin with the use of a cationizing agent comprising 2,3-epoxypropytrimethylammonium chloride (trademark name: WISTEX E100). These water soluble high-molecular compounds will be hereinafter referred to as compound P1 (e). In any case, when a monomer capable of providing a high-molecular compound having a side chain provided with a hydroxyl group such as 2-hydroxyethylmethacrylate is used, it is desired to be used in an amount of 5 to 50 wt.%. As for the quantity of the cationic groups provided, it is desired to be less than 15% based on the repeating units as for the entire molecular chains. Specific examples of the water soluble cationized polyvinyl alcohol (D) are water soluble high-molecular compounds obtained from polyvinyl alcohol of 60000 in average molecular weight and 85 mole% in saponification value by cationizing about 15% of its hydroxyl groups with the use of a cationizing agent comprising 2,3-epoxypropytrimethylammonium chloride (trademark name: WISTEX E100). These water soluble high-molecular compounds will be hereinafter referred to as compound P1 (f). Another specific examples of the water soluble cationized polyvinyl alcohol (D) are water soluble high-molecular compounds obtained from polyvinyl alcohol of 30000 in average molecular weight and 83 mole% in saponification value by cationizing about 10% of its hydroxyl groups with the use of a cationizing agent comprising 2,3-epoxypropytrimethylammonium chloride (trademark name: WISTEX E100). These water soluble high-molecular compounds will be hereinafter referred to as compound P1 (g). In any case, the cationization rate is desired to be in the range of 2 to 15%. In the case where the cationization rate is made to be less than 2%, there is a tendency that the ink-receiving layer containing such water soluble high-molecular compound is inferior in terms of dye-fixing property and waterfastness. In the case where the cationization rate is made to be exceeding 15%, there is a tendency of entailing problems such that the ink-receiving layer containing such water soluble high-molecular compound is insufficient in adhesion to the substrate and in addition, the dye-fixing is liable to occur at the surface of the ink-receiving layer, resulting in preventing ink from being effectively penetrated. In view of this, as for the quantity of the cationic groups provided, it is desired to be preferably in the range of 5 to 15% or more preferably, in the range of 7 to 12%, based on the repeating units as for the entire molecular chains. In the following, description will be made of the water soluble high-molecular compound (P2) having a side chain provided with a condensable functional group (hereinafter referred to as "compound P2" for simplification purpose) which is used in the present invention. The compound P2 contained in the curing composition according to the present invention functions to establish a crosslinking structure whereby curing the curing composition to provide a solid layer as an ink-receiving layer without deteriorating its hydrophilic property even when the condensable functional group is condensed. The compound P2 includes: (E) acrylamide series high-molecular compounds having an acrylamide-bearing alkylol group as a side chain, and (F) acrylic ester series high-molecular compounds having a hydrolyzable trialkylsilyl group. The high-molecular compounds (E) and (F) are desired to be of a number average molecular weight preferably in the range of 30000 to 300000 or more preferably, in the range of 50000 to 200000. The high-molecular compounds (E) and (F) can include hydrophilic acrylic polymers obtained by way of copolymerization of copolymerizable components including a monomer having a condensing and crosslinking property (hereinafter referred to as condensable and crosslikable monomer) preferably at about 0.1 to 20% in terms of weight basis. As the condensable and crosslikable monomer, there can be mentioned N-alkylolacrylamides and condensable vinylalkoxysilanes. Specific examples of the N-alkylolacrylamide are N-methylolacrylamide, N-methylolmethacrylamide, N-butoxymethylacrylamide, and N-butoxymethylmethacrylamide. Specific examples of the condensable vinylalkoxysilane are vinyltrimethoxy silane, vinyltriethoxy silane, vinyltris(β-methoxyethoxy) silane, vinylmethyldiethoxy silane, and γ-methacryloyloxypropyltrimethoxy silane. Any of these condensable and crosslinkable monomers is capable of readily providing a crosslinking structure either by way of self-crosslinking or with the addition of a condensation and crosslinking accelerator. The condensation and crosslinking accelerator usable in this case can include p-toluenesulfonic acid, phosphoric acid, hydrochloric acid, and amine salts of these acids; ammonium salt, sodium salt; carboxylic acids such as acetic acid, lactic acid, lauric acid, crotonic acid, succinic acid, glutaric acid; adipic acid, azelaic acid, pimeic acid, and sebacic acid; and salts of these carboxylic acids. As above described, as for the amount of any of these condensable and crosslinkable monomers used, it is desired to be about 0.1 to 20% in terms of weight basis. In a more preferred embodiment, it is in the range of 1 to 10% in terms of weight basis. Further, in the most preferred embodiment, being somewhat different depending upon the kind of the condensable and crosslinkable monomer to be used, it is, in general, in the range of 1 to 5% in terms of weight basis. As another monomer capable of being copolymerized together with the foregoing condensable and crosslinkable monomer, it is desired to use any of the following monomers (1) to (4) because any of them is capable of imparting a hydrophilic property to the acrylic polymer. (1) acrylic esters having an ethylene glycol chain: monomers represented by the following general formula. CH 2 =C(R)-COO-(CH 2 CH 2 O) n -H, with n being in the range of 2 to 24 and R being an alkyl group or H.As specific examples of such monomer, there can be illustrated such commercially available acrylic esters as will be described below.BLENMER PE-90 (trademark name, produced by Nippon Oil & Fats Co., Ltd.) having the following chemical structure: CH 2 =C(CH 3 )-COO-(CH 2 CH 2 O) n -H, with n being 1.9;BLENMER PE-200 (trademark name, produced by Nippon Oil & Fats Co., Ltd.) having the following chemical structure: CH 2 =C(CH 3 )-COO-(CH 2 CH 2 O) n -H, with n being 4.4; andBLENMER PE-350 (trademark name, produced by Nippon Oil & Fats Co., Ltd.) having the following chemical structure: CH 2 =C(CH 3 )-COO-(CH 2 CH 2 O) n -H, with n being 7.7. (2) acrylic esters having an ethylene glycol chain with an alkyl ether terminal: monomers represented by the following general formula. CH 2 =C(R)-COO-(CH 2 CH 2 O) m -(CH 2 ) p H, with m being in the range of 2 to 24, p being in the range of 1 to 16, and R being hydrogen atom or an alkylAs specific examples of such monomer, there can be illustrated such commercially available acrylic esters as will be described below. methoxytriethylene glycol acrylate NK ESTER AM-30G (trademark name, R = H, m = 3, p = 1); methoxypolyethylene glycol #400 acrylate NK ESTER AM-90G (trademark name, R = H, m = about 10, p = 1); methoxydiethylene glycol methacrylate NK ESTER M-20G (trademark name, R = CH 3 , m = 2, p = 1); methoxytetraethylene glycol methacrylate NK ESTER M-40G (trademark name, R = CH 3 , m = 4, p = 1); methoxypolyethylene glycol #400 methacrylate NK ESTER M-90G (trademark name, R = CH 3 , m = about 10, p = 1); methoxypolythylene glycol #100 methacrylate NK ESTER M-230G (trademark name, R = CH 3 , m = about 24, p = 1); and methoxydiethylene glycol acrylate NK ESTER AB-20G (trademark name, R = H, m = 2, p = 4). (3) acrylic esters having a tertiary amino group: Specific examples are N,N-dimethylaminoethylmethacrylate, N,N-dimethylaminoethyl acrylate, N,N-dimethylaminopropylmethacrylate, and N,N-dimethylaminopropylacrylate. (4) acrylamides: Specific examples are N,N-dimethylaminoacrylamide, N,N-dimethylaminomethacrylamide, N,N-dimethylaminoethylmethacrylamide, N,N-dimethylaminopropylacrylamide, N,N-dimethylaminopropylmethacrylamide, N,N-dimethylamino-2-hydroxypropylacrylamide, and N,N-dimethylamino-2-hydroxypropylmethacrylamide. Other than the foregoing monomers, other copolymerizable monomers such as methyl(meth)acrylate, ethyl(meth)acrylate, and 2-hydroxyethyl(meth)acrylate are also usable. In the following, there will be illustrated specific examples of copolymers which are desirably usable as the compound P2. Compound P2 (a): copolymer comprising N-methylolacrylamide, 2-hydroxyethylmethacrylate, and methylmethacrylate being copolymerized at a monomer weight ratio of 10 : 30 : 60. Compound P2 (b): copolymer comprising N-butoxymethylacrylamide, 3-chloro-2-hydroxypropylmethacrylate, and methoxytriethyleneglycolacrylate being copolymerized at a monomer weight ratio of 5 : 30 : 65. Compound P2 (c): copolymer comprising N-methylolmethacrylamide, N,N-dimethylamino-2-hydroxypropylmethacrylamide, and ethylmethacrylate being copolymerized at a monomer weight ratio of 8 : 25 : 67. Compound P2 (d): copolymer comprising vinyltris(β-methoxyethoxy) silane, BLENMER PE-200, and ethylmethacrylate being copolymerized at a monomer weight ratio of 5 : 20 : 75. Compound P2 (e): copolymer comprising vinyltriethoxy silane, N,N-dimethylaminoethylmethacrylate, 2-hydroxyethylmethacrylate, and ethylmethacrylate being copolymerized at a monomer weight ratio of 5 : 15 : 10 : 70. These high-molecular compounds are relatively low in solubility to pure water. Therefore, when these high-molecular compounds are polymerized or dissolved, it is desired to use a polar solvent comprising glycol ether, alcohol or the like. The curing composition according to the present invention is desired to contain any of the foregoing compounds P1 and any of the foregoing compounds P2 at a weight ratio preferably in the range of from 100 : 10 to 100 : 50 or more preferably, in the range of from 100 : 20 to 100 : 40. The curing composition according to the present invention may contain an appropriate component if necessary, in addition to the compounds P1 and P2. As such component, there can be mentioned, for example, water soluble high-molecular compounds having no cationic group. Such water soluble high-molecular compound having no cationic group has a tendency of causing a reduction in the waterfastness of a print product but it exhibits a function of adjusting the physical properties of the curing composition promoting so that the ink absorption rate of the ink-receiving layer is promoted. Therefore, the curing composition according to the present invention may additionally contain such water soluble high-molecular compound having no cationic group within a range wherein the compatibility thereof with the compounds P1 and P2 can be allowed. As such water soluble high-molecular compound having no cationic group usable in the present invention, there can be mentioned polyvinyl alcohol, polyvinyl alcohol-polyvinyl acetate copolymer, polyvinyl formal, polyvinyl butyral, gelatin, carboxymethylcellulose, hydroxyethylcellulose, hydroxypropylcellulose, hydroxyethylstarch, polyethyloxazoline, polyethyleneoxide, polyethylene glycol, polypropyleneoxide, and polyethyleneoxide/propyleneoxide block copolymer. As for the amount of any of these water soluble high-molecular compounds to be contained in the hardening composition according to the present invention, it is desired to be in the range of 10 to 50 parts by weight versus 100 parts by weight of the sum of the compounds P1 and P2. The formation of a solid layer as the ink-receiving layer using the curing composition according to the present invention is conducted in a manner of providing a coating composition comprising the curing composition dispersed in a solvent, applying the coating composition onto a substrate (or an object), which is to be dedicated for printing by means of an ink jet printing apparatus, such as a film (for example, a film made of polyethylene terephthalate) in an amount to provide a thickness of 5 to 50 um when dried to form a coat composed of the curing composition on the substrate, and subjecting the coat to heat treatment to dry the coat while vaporizing the solvent contained therein to remove and while crosslinking the coat, whereby a solid layer as the ink-receiving layer is formed on the substrate. The application of the coating composition onto the substrate may be conducted by means of a spinner, roll coater, or spray coater, or by way of screen printing. The heat treatment of the coat formed on the substrate is desired to be conducted at a temperature of 75 °C to 150 °C. Particularly, under condition of using no catalyst, the heat treatment is desired to be conducted at a temperature of about 150 °C for 3 minutes or more. Under condition of using a catalyst, the heat treatment is desired to be conducted at a temperature of about 70 °C for 5 minutes or more. It is possible to conduct aging treatment after the heat treatment, wherein the crosslinking of the coat (the solid layer) is more effectively completed. As apparent from the above description, the curing composition comprising the foregoing compound P1 and the foregoing compound P2 is of the type that is cured (crosslinked) with the application of thermal energy. Now, as the water soluble high-molecular compound (P1) contained in this curing composition, any of those high-molecular compounds which have been previously illustrated as being usable as the compound P1 may be used. Now, the foregoing curing composition comprising the compounds P1 and P2 according to the present invention is suitable for the production of a sheet for an overhead projector (OHP). The substrate usable in this case can include, for example, various films used in graphic arts. Specific examples of such film are polyethylene terephthalate films, cellulose acetate films, polycarbonate films, polyvinyl chloride films, polystyrene films, polysulfone films, and aliphatic polyester films. In the production of the sheet for an OHP using the curing composition according to the present invention, it is possible for the curing composition to contain pore-bearing fine particles of an inorganic or organic material in order to attain a quick absorption capacity (in terms of absorption speed and absorption volume) for the resulting ink-receiving layer. Such inorganic or organic particles can include pigments such as titanium oxide, silica, alumina, talc and clay; inorganic salts; and organic materials. Further, the foregoing curing composition comprising the compounds P1 and P2 according to the present invention makes it possible to effectively conduct printing for various objects, even if they are poor in absorption of water-based ink, by means of an ink jet printing apparatus, by forming an ink-receiving layer comprised of the curing composition thereon, wherein print products of the objects can be efficiently produced. Such object can include, for example, leathers, fabrics, plastic members, metal members, papers, fiberboards, ceramics, and the like. Specific examples are prepaid cards, musical compact discs, CDROMs, digital video discs, ID cards, magnetic cards, lighting acrylic resin plates, polycarbonate plates, signboards, display panels, goods exhibition panels, door plates, name plates, wrapping boxes, envelopes, and the like. In the following, the present invention will be described in more detail with reference to examples. It should be understood that these examples are only for the illustrative purpose but are not intended to restrict the scope of the present invention to these examples. Example 1 There was provided a 85 µm thick PET (polyethylene terephthalate) film as a substrate. Separately, there was provided a coating composition composed of: 200 parts by weight of a 50 wt.% aqueous solution of the foregoing compound P1 (a) (that is, the water soluble cationic group-bearing high-molecular compound); 100 parts by weight of a 20 wt.% ethylene glycol monomethyl ether solution of the foregoing compound P2 (a) (that is, the condensable functional group-bearing copolymer); and 1.5 parts by weight of p-toluenesulfonic acid. The coating composition was applied onto the PET film in an amount to provide a thickness of 20 µm when dried by means of a bar coater, followed by drying at a temperature at 85 °C for 10 minutes, whereby forming a 20 µm thick solid layer as an ink-receiving layer on the PET film. Thus, there was obtained a printing medium. Example 2 There was provided a 85 µm thick PET (polyethylene terephthalate) film as a substrate. Separately, there was provided a coating composition composed of: 200 parts by weight of a 50 wt.% aqueous solution of one of the water soluble cationic group-bearing high-molecular compounds previously mentioned as the compound P1 (b); 75 parts by weight of a 20 wt.% ethylene glycol monomethyl ether solution of the foregoing compound P2 (b) (that is, the condensable functional group-bearing copolymer); and 1 part by weight of ammonium chloride. The coating composition was applied onto the PET film in an amount to provide a thickness of 20 µm when dried by means of the bar coater, followed by drying at a temperature at 85 °C for 10 minutes, whereby forming a 20 um thick solid layer as an ink-receiving layer on the PET film. Thus, there was obtained a printing medium. Example 3 There was provided a 85 µm thick PET (polyethylene terephthalate) film as a substrate. Separately, there was provided a coating composition composed of: 250 parts by weight of an aqueous solution comprised of hydrochloride salt of one of the water soluble cationic group-bearing high-molecular compounds previously mentioned as the compound P1 (d) in an amount of 25 wt.% dissolved in pure water; 50 parts by weight of a solution comprised of the foregoing compound P2 (d) in an amount of 30 wt.% dissolved in a solvent composed of ethylene glycol monomethyl ether and NMP; and 1 part by weight of citric acid. The coating composition was applied onto the PET film in an amount to provide a thickness of 25 pm when dried by means of the bar coater, followed by drying at a temperature at 120 °C for 10 minutes, whereby forming a 25 um thick solid layer as an ink-receiving layer on the PET film. Thus, there was obtained a printing medium. Example 4 There was provided a 85 µm thick PET (polyethylene terephthalate) film as a substrate. Separately, there was provided a coating composition composed of: 150 parts by weight of an aqueous solution comprised of hydrochloride salt of one of the water soluble cationic group-bearing high-molecular compounds previously mentioned as the compound P1 (e) in an amount of 20 wt.% dissolved in pure water; 50 parts by weight of a solution comprised of the foregoing compound P2 (e) in an amount of 20 wt.% dissolved in ethylene glycol monomethyl ether; and 1 part by weight of citric acid. The coating composition was applied onto the PET film in an amount to provide a thickness of 25 µm when dried by means of the bar coater, followed by drying at a temperature at 120 °C for 10 minutes, whereby forming a 25 µm thick solid layer as an ink-receiving layer on the PET film. Thus, there was obtained a printing medium. Comparative Example 1 The procedures of Example 3 were repeated, except that the compound P2 contained in the coating composition in Example 3 was replaced by dibutyltin dilaurate, to obtain a printing medium having a 25 µm thick ink-receiving layer (solid layer). Comparative Example 2 There was provided a 85 µm thick PET (polyethylene terephthalate) film as a substrate. Separately, there was provided a coating composition composed of: 100 parts by weight of an aqueous solution comprised of polyvinyl alcohol of 85% in saponification value in an amount of 25 wt.% dissolved in pure water; 35 parts by weight of glycerintriglycidylether tri(metha)acrylate; 15 parts by weight of quaternarized hydrochloride salt of N,N-dimethylamino-2-hydroxypropylacrylamide; 5.0 parts by weight of CGI 1700 (produced by Japan Ciba Geigy Company); and 25 parts by weight of isopropyl alcohol. The coating composition was applied onto the PET film in an amount to provide a thickness of 25 µm when dried by means of the bar coater, followed by drying at a temperature at 85 °C for 10 minutes, to thereby form a 25 µm thick dry coat on the PET film. The dry coat thus formed on the PET film was subjected to curing treatment by irradiating ultraviolet rays thereto at 400 mJ/cm 2 in terms of estimation from the high pressure mercury lamp, whereby forming a 25 µm thick solid layer as an ink-receiving layer on the PET film. Thus, there was obtained a printing medium. Evaluation As for each of the printing mediums obtained in Examples 1 to 4 and Comparative Examples 1 and 2, printing test was conducted in the following manner. That is, using a commercially available bubble jet color printer BJC-600J (trademark name, produced by Canon Kabushiki Kaisha), on each printing medium, there were spacedly formed test patches each comprising one of seven colors, i.e., yellow, cyan, magenta, black, green, blue and red using four kinds of aqueous inks each comprising a yellow dye, magenta dye, cyan dye, or black dye, to obtain a print sample. Thus, there were obtained ten print samples each having the foregoing test patches spacedly formed thereon. As for each of the ten print samples thus obtained, evaluation was conducted with respect to transmission density, clearness, and waterfastness & dye-fixing property in the following manner. The evaluated results obtained are collectively shown in Table 1. Evaluation of transmission density: Using a Macbeth transmission densitometer (produced by Macbeth Company), the density of the solid black area of each print sample was measured. The measured result is shown in Table 1 based on the following criteria. AA : the measured density ≧ 1.0, A : 1.0> the measured density ≧ 0.7, and B : the measured density <0.7. Evaluation of clearness: The clearness of the colored area of each print sample was observed by conducting projection using a overhead projector. The observed result is shown in Table 1 based on the following criteria. A : a case wherein the colored area is uniformly colored and transparent, B : a case wherein the colored area is accompanied by a somewhat unevenly colored portion and also a somewhat turbid portion, and C : a case wherein the colored area is unevenly colored and darkened. Evaluation of waterfastness & dye-fixing property: Each print sample was immersed in water contained in a vessel for 1 minute. Thereafter, the print sample was taken out from the vessel, and observation was conducted for the print sample. The observed result is shown in Table 1 based on the following criteria. AA : a case wherein any negative influence of water is not observed, A : a case wherein the occurrence of slight bleeding is observed but this is not problematic in practice, B : a case wherein the occurrence of slight swelling is observed and also the occurrence of a stain due to the dye dissolution is observed at a non-printed area, and C : a case wherein portions where the dyes are bled are observed and the occurrence of peeling at the ink-receiving layer is observed. It should be understood that the case belonging to the criteria AA is the most desirable and the case belonging to the criteria A is practically acceptable. As apparent from the results shown in Table 1, it is understood that the ink-receiving layer formed of the curing composition according to the present invention excels particularly in waterfastness & dye-fixing property and satisfactory in transmission density and clearness, and it is apparently surpassing the ink-receiving layer formed using the conventional water soluble resin or ultraviolet ray-curable resin. transmission density clearness waterfastness & dye-fixing property Example 1 A A A A Example 2 A A A A Example 3 A A A A A Example 4 A A A A A Comparative Example 1 A A A B Comparative Example 2 A B C From the above description, it is understood that in the curing composition according to the present invention, the compound P1 and the compound P2 in combination provide desirable multiplier effects in a well balanced state, and this enables to form a desirable ink-receiving layer which excels in absorption, absorption rate and dye-fixing property with respect to water-based ink and also in waterfastness. And it is also understood that the ink-receiving layer formed of the curing composition according to the present invention has such excellent properties as above described and therefore, it is very suitable for use in printing particularly by means of a ink jet color printer.

Claims: A curing composition comprising a water-soluble high-molecular compound (P1) having a cationic group-bearing principal molecular chain and a water-soluble high-molecular compound (P2) having a side chain provided with a condensable functional group characterized in that said water-soluble high-molecular compound (P1) is a high-molecular compound selected from the group consisting of high-molecular compounds (A) obtained by way of alternative addition polymerization between epichlorohydrin and dialkylamine or dialkanolamine and high-molecular compounds (B) obtained by way of alternative addition polymerization between hydrophilic oligomer having opposite molecular chain terminals each having a glycidyl group and asymmetric diamine, dialkylamine or dialkanolamine. The curing composition according to claim 1, wherein the high-molecular compound (A) is a high-molecular compound obtained by way of alternative addition polymerization between epichlorohydrin and dimethylamine, diethylamine or diethanolamine. The curing composition according to claim 1, wherein the high-molecular compound (B) is a lactate of a high-molecular compound obtained by way of alternative addition polymerization between polyethylene glycol diglycidyl ether which is obtained by reacting polyethylene glycol of 1000 in number average molecular weight with epichlorohydrin, and dimethylamine. The curing composition according to claim 1, wherein the high-molecular compound (B) is a high-molecular compound obtained by way of alternative addition polymerization between polyoxyethylene polyoxypropylene diglycidyl ether which is obtained from a block copolymer of 2000 in number average molecular weight comprising polyethylene oxide and polypropylene oxide by way of glycidylation of the terminal hydroxyl group of said block copolymer, and diethanolamine. The curing composition according to claim 1, wherein the water soluble high-molecular compound (P1) has a number average molecular weight of 2000 to 50000. The curing composition according to claim 1, wherein the water soluble high-molecular compound (P1) has a cationic group-bearing molecular side-chain. The curing composition according to claim 6, wherein the water soluble high-molecular compound (P1) is a water soluble high-molecular compound cationized with a cationizing agent. The curing composition according to claim 7, wherein the cationizing agent is a compound selected from the group consisting of 2,3-epoxypropyltrimethylammonium chloride and 3-chloro-2-hydroxypropyltrimethylammonium chloride. The curing composition according to claim 6, wherein the water soluble high-molecular compound (P1) is a high-molecular compound selected from the group consisting of water soluble acrylic polymers (C) obtained by cationizing an acrylic ester series copolymer having a molecular side-chain with a hydroxyl group terminal and water soluble cationized polyvinyl alcohols (D) having a molecular chain containing 2 to 15 mol-% of cationic groups which are obtained from polyvinyl alcohol of 80 mol-% or more in saponification value by way of cationization of the hydroxyl group of said polyvinyl alcohol. The curing composition according to claim 9, wherein the acrylic polymer (C) is a water-soluble high-molecular compound obtained from an acrylic resin of 150,000 in weight average molecular weight comprising a copolymer of 2-hydroxyethylmethacrylate, methylmethacrylate, acrylamide and n-butylacrylate being copolymerized at a monomer weight ratio of 20:30:35:15, by way of cationization of 50% of the hydroxyl groups of said acrylic resin with the use of 3-chloro-2-hydroxypropyltrimethylammonium chloride. The curing composition according to claim 9, wherein the acrylic polymer (C) is a water-soluble high-molecular compound obtained from an acrylic resin of 130,000 in weight average molecular weight comprising a copolymer of 2-hydroxyethylmethacrylate, methylmethacrylate, methacrylamide and acrylonitrile being copolymerized at a monomer weight ratio of 25:30:35:10, by way of cationization of 50% of the hydroxyl groups of said acrylic resin with the use of 2,3-epoxypropyltrimethylammonium chloride. The curing composition according to claim 9, wherein the polyvinyl alcohol (D) is a high-molecular compound obtained from polyvinyl alcohol of 60,000 in average molecular weight and 85 mole% in saponification value, by way of cationization of 15% of its hydroxyl groups with the use of 2,3-epoxypropyltrimethylammonium chloride. The curing composition according to claim 9, wherein the polyvinyl alcohol (D) is a high-molecular compound obtained from polyvinyl alcohol of 30,000 in average molecular weight and 83 mole% in saponification value, by way of cationization of 10% of its hydroxyl groups with the use of 2,3-epoxypropyltrimethylammonium chloride. The curing composition according to claim 1, wherein the water soluble high-molecular compound (P2) is a high-molecular compound selected from the group consisting of high-molecular compounds (E) having an acrylamide-bearing alkylol group as a side-chain and acrylic ester series high-molecular compounds (F) having a hydrolyzable trialkylsilyl group. The curing composition according to claim 14, wherein the acrylamide series high-molecular compound (E) is a high-molecular compound selected from the group consisting of N-methylolacrylamide, N-methylolmethacrylamide, N-butoxymethylacrylamide, and N-butoxymethylmethacrylamide. The curing composition according to claim 14, wherein the high-molecular compound (F) is a high-molecular compound selected from the group consisting of vinyltrimethoxysilane, vinyltriethoxysilane, vinyltris(β-methoxyethoxy)silane, vinyltriacetylsilane, and γ-methacryloxypropyltrimethoxysilane. The curing composition according to claim 14, wherein the water soluble high-molecular compound (P2) is a copolymer of N-methylolacrylamide, 2-hydroxyethylmethacrylate, and methylmethacrylate. The curing composition according to claim 14, wherein the water soluble high-molecular compound (P2) is a copolymer of N-butoxymethylacrylamide, 3-chloro-2-hydroxypropylmethacrylate and methoxytriethyleneglycolacrylate. The curing composition according to claim 14, wherein the water soluble high-molecular compound (P2) is a copolymer of N-methylolmethacrylamide, N,N-dimethylamino-2-hydroxypropylmethacrylamide and ethylmethacrylate. The curing composition according to claim 14, wherein the water soluble high-molecular compound (P2) is a copolymer of vinyltris(β-methoxyethoxy)silane, a monomer having a structural formula of CH 2 =C(CH 3 )-COO-(CH 2 CH 2 O) n H with n being 4,4, and ethylmethacrylate. The curing composition according to claim 14, wherein the water soluble high-molecular compound (P2) is a copolymer of vinyltriethoxysilane, N,N-dimethylaminoethylmethacrylate, 2-hydroxyethylmethacrylate, and ethylmethacrylate. The curing composition according to claim 14, wherein the water soluble high-molecular compound (P2) has a number average molecular weight of 30000 to 300000. The curing composition according to claim 14, wherein the water soluble high-molecular compound (P2) has a number average molecular weight of 50000 to 200000. The curing composition according to claim 1 which is thermosetting. The curing composition according to claim 1 which contains the water soluble high-molecular compound (P2) in an amount of 10 to 50 parts by weight versus 100 parts by weight of the water soluble high-molecular compound (P1). The curing composition according to claim 1 which contains the water soluble high-molecular compound (P2) in an amount of 20 to 40 parts by weight versus 100 parts by weight of the water soluble high-molecular compound (P1). A printing medium comprising a substrate and an ink-receiving layer provided on said substrate, said ink-receiving layer comprising a solid layer obtainable by curing the curing composition according to any of claims 1 to 26. A process for producing a printing medium, said process comprising the steps of: providing a curing composition according to any of claims 1 to 26, applying said curing composition onto a surface of a substrate to form a coating layer, and subjecting said coating layer formed on said substrate to heat treatment to cure said coating layer. Use of the printing medium according to claim 27 for inkjet printing by performing printing on said ink-receiving layer on the substrate with the use of ink to thereby obtain a print product. The use according to claim 29, wherein the used ink is water-based ink. The use according to claim 29, wherein the printing is conducting by means of an ink jet system. The use according to claim 31, wherein the ink jet system is an ink jet system of imparting thermal energy to the ink to discharge said ink.

Inventors: IKEDA MASAMI, KASHIWAZAKI AKIO, KATAYAMA MASATO, KIMURA MAKIKO, NAKATA YOSHIE, NISHIOKA YUKO, NOGUCHI HIROMICHI, IKEDA, MASAMI, KASHIWAZAKI, AKIO, KATAYAMA, MASATO, KIMURA, MAKIKO, NAKATA, YOSHIE, NISHIOKA, YUKO, NOGUCHI, HIROMICHI
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1996
Main classification: B41M5
IPC codes: C08L63, B41M5, B32B27, C08L79, C09D201, C08G65, C08G59, C08G73, C09D179, C09D163, C08L101