HYDROPHILIZED SUPPORT FOR PLANOGRAPHIC PRINTING PLATES AND ITS PREPARATION

Abstract: A method of preparing a substrate for a planographic printing plate comprises contacting a support, for example of aluminium or plastics, with a liquid having a pH of 9 or greater and comprising a silicate solution, for example sodium silicate solution, in which particulate material, for example of alumina or titania, are dispersed. The liquid when cured produces a hydrophilic layer on the support. A substrate per se and a printing plate are also described.

Description: HYDROPHILIZEDSUPPORTFOR PLANOGRAPHICPRINTINGPLATESANDITSPREPARATION This invention relates to planographic printing and provides a method of preparing a substrate for a planographic printing member, a substrate of a planographic printing member and a planographic printing member per se. The invention particularly, although not exclusively, relates to lithographic printing. Lithographic processes involve establishing image (printing) and non-image (non-printing) areas on a substrate, substantially on a common plane. When such processes are used in printing industries, non-image areas are generally hydrophilic and image areas are generally oleophillic. Consequently, oil based inks are repelled from the non-image areas after water has been applied to the substrate. Image and non-image areas can be created by processes which include a step of exposing a layer of image material on the surface of the substrate to radiation. The exposure to radiation creates solubility differences in the image material corresponding to image and non-image areas. During development, the more soluble areas are removed, leaving a pattern on the substrate corresponding to the image. Preparation of the substrate for receiving a layer of the image material must ensure that the image material bonds to the substrate. However, it must allow release of the soluble image material during development. One of the most common substrates used in lithographic printing comprises an aluminium base layer which is treated to make it suitable for use. In general, the aluminium layer comprises high quality aluminium, for example 1050 alloy which is at least 99.5% pure. For preparation of a substrate, the aluminium is roughened, for example by electrograining, anodised and then conditioned by chemical means, for example by treatment with water, a solution of phosphate or silicate salt, or a polycarboxylic acid. Lithographic printing plates which utilise electrograined and/or anodised and/or chemically conditioned aluminium are described in, for example, UK Patent Application No. 1 439 127, US Patent Nos. 3 181 461, 3 963 594, 4 052 275, 4 072, 589, 4 131 518, European Patent Application No. 0 110 417 and Japanese Publication No. 20/3956. One problem with the known processes is that they consume a significant amount of electrical energy in the electrograining and anodising steps. Furthermore, these steps produce waste chemicals which must be disposed of. Additionally, the processes can generally only be run at relatively low speed. Numerous solutions have been proposed for the above described problems; however, few such proposals have been used commercially. For example, PCT Publication No. WO91/12140 discloses a lithographic plate of aluminium metal which carries an oxide layer derived from a zirconia sol. US Patent No. 4 457 971 discloses a lithographic printing plate comprising an aluminium or aluminised substrate bearing a ceramic layer comprising non-metallic inorganic particles and a water resistant phase or phases of a dehydration product of at least one monobasic phosphate. US Patent No. 4 420 549 discloses a lithographic printing plate comprising an aluminium or aluminised substrate bearing a ceramic coating comprising a polymeric form of aluminium phosphate or mixtures of aluminium phosphates wherein the coating is substantially free of particulate matter. US Patent No. 4 542 089 discloses a process for preparing a photosensitive substrate comprising providing a hydrophilic ceramic on an aluminium substrate or aluminised surface of a substrate by applying a slurry of at least one monobasic phosphate and inorganic non¬ metallic particles on at least one surface of the aluminium or aluminised substrate and firing the slurry at a temperature of at least 230° for a time sufficiently long to ensure substantially complete dehydration of the ceramic layer to form a hydrophilic ceramic coating. Italian Patent Application No. MI94 A000448 describes lithographic plates prepared by applying a colloidal mixture comprising fluorosilicate, silica, polyvinylidene fluoride and titanium dioxide to an aluminium support. Polymerisation of the fluorosilicate is carried out at 225°-300°C for 50-180 seconds. One problem associated with the above described processes results from the relatively high temperature required to cure and/or polymerise the coating on the aluminium. High temperatures are found to anneal the aluminium support and reduce its tensile strength. Additionally, high temperatures may deform the plate and cause it to have a wavy structure. Both of these effects can be problematical when the plates are run on a printing press. Another solution to the problem of electrograining and/or annealing is described in PCT Patent Application No. GB93/01910. The document discloses making a lithographic printing plate by plasma spraying A1 2 0 3 powder onto aluminium alloy sheet. As an alternative to aluminium, plastics materials, for example polyesters, may be used as supports. Again, there are numerous disclosures of surface coatings for such materials. For example , US 4 330 605 discloses a photolithographic receptor sheet capable of being imaged by a silver salt diffusion transfer process which comprises coating a polyethylene terephthalate film with a mixture of colloidal silica and dry silica powder. EP 0 619 524, EP 0 619 525 and EP 0 620 502 also disclose various coatings for polyethylene terephthalate film. It is an object of the present invention to address problems associated with known planographic printing plates, parts thereof and methods of their production. According to the invention, there is provided a method of preparing a substrate for a planographic printing member including the step of forming a hydrophilic layer on a support by contacting the support with a liquid comprising a silicate solution in which particulate material is dispersed. Preferably, said planographic printing member is a printing plate. Said silicate solution may comprise a solution of any soluble silicate including compounds often referred to as water glasses, etasilicates , orthosilicates and sesquisilicates. Said silicate solution may comprise a solution of a modified silicate for example a borosilicate or phosphosilicate. Said silicate solution may comprise one or more, preferably only one, metal or non-metal silicate. A metal silicate may be an alkali metal silicate. A non-metal silicate may be quaternary ammonium silicate. Said silicate solution may be formed from silicate wherein the ratio of the number of moles of Si species, for example Si0 2 , to the number of moles of cationic, for example metal species is in the range 0.25 to 10, preferably in the range 0.25 to about 6, more preferably in the range 0.5 to 4. Said silicate is preferably alkali metal silicate. In this case, the ratio of the number of moles of Si0 2 to the number of moles of M 2 0 in said silicate, where M represents an alkali metal may be at least 0.25, suitably at least 0.5, preferably at least 1, more preferably at least 1.5. Especially preferred is the case wherein said ratio is at least 2.5. Said ratio may be less than 6, preferably less than 5 and more preferably less than 4. Preferred alkali metal silicates include lithium, sodium and potassium silicates, with lithium and/or sodium silicate being especially preferred. A silicate solution comprising only sodium silicate is most preferred. Said liquid may comprise 2 to 30 wt% of silicate (e.g. dissolved sodium silicate solid) , preferably 5 to 20 wt%, more preferably 8 to 16 wt%. The liquid may be prepared using 10 to 60 wt%, preferably 30 to 50 wt%, more preferably 35 to 45 wt% of a silicate solution which comprises 30 to 40 wt% silicate. Said liquid may include 5 to 60 wt% of particulate material. Preferably, the liquid includes 10 to 50 wt%, more preferably 15 to 45 wt%, especially 20 to 40 wt% of particulate material. The ratio of the weight of silicate to the weight of particulate material in the liquid is preferably in the range 0.1 to 2 and, more preferably, in the range 0.1 to 1. Especially preferred is the case wherein the ratio is in the range 0.2 to 0.6. Said liquid may include more than 20 wt%, preferably more than 30 wt%, more preferably more than 40 wt%, especially more than 45 wt% water (including water included in said silicate solution) . Said liquid may include less than 80 wt%, preferably less than 70 wt%, more preferably less than 65 wt%, especially less than about 60 wt% water. Said particulate material may be an organic or an inorganic material. Organic particulate materials may be provided by latexes. Inorganic particulate materials may be selected from alumina, silica, silicon carbide, zinc sulphide, zirconia, barium sulphate, talcs, clays (e.g. kaolin) , lithopone and titanium oxide. Said particulate material may comprise a first material which may have a hardness of greater than 8 Modified Mohs (on a scale of 0 to 15) , preferably greater than 9 and, more preferably, greater than 10 Modified Mohs. Said first material may comprise generally spherical particles. Alternatively, said material may comprise flattened particles or platelets. Said first material may have a mean particle size of at least 0.1 μm and preferably at least 0.5 μm. Said first material may have a mean particle size of less than 45 μm, preferably less than 20 μm, more preferably less than 10 μm. The particle size distribution for 95% of particles of the first material may be in the range 0.01 to 150 μ , preferably in the range 0.05 to 75 μm, more preferably in the range 0.05 to 30 μm. Said first material preferably comprises an inorganic material. Said first material preferably comprises alumina which term includes Al 2 0 3 and hydrates thereof, for example A10 3 .3H 2 0. Preferably, said material is A1 2 0 3 . Said particulate material in said liquid may include at least 20 wt%, preferably at least 30 wt% and, more preferably, at least 40 wt% of said first material. Said liquid may include 5 to 40 wt%, preferably 5 to 30 wt%, more preferably 7 to 25 wt%, especially 10 to 20 wt% of said first material. Said particulate material may comprise a second material. Said second material may have a mean particle size of at least 0.001 μm, preferably at least 0.01 μm. Said second material may have a mean particle size of less than 10 μm, preferably less than 5 μm and, more preferably, less than 1 μm. Mean particle sizes of said first and second materials suitably refer to the primary particle sizes of said materials. Said particulate material in said liquid may include at least 20 wt%, preferably at least 30 wt% and, more preferably, at least 40 wt% of said second material. Said liquid may include 5 to 40 wt%, preferably 5 to 30 wt%, more preferably 7 to 25 wt%, especially 10 to 20 wt% of said second material. Said second material is preferably a pigment. Said second material is preferably inorganic. Said second material is preferably titanium dioxide. Said first and second materials preferably define a multimodal, for example a bimodal particle size distribution. Where the liquid comprises a silicate and said particulate material comprises a first material and a second material as described, the ratio of the wt% of silicate (e.g. dissolved sodium silicate solid) to the wt% of said first material may be in the range 0.25 to 4, preferably in the range 0.5 to 1.5 and more preferably about 1. Similarly, the ratio of the wt% of silicate to the wt% of said second material may be in the range 0.25 to 4, preferably in the range 0.5 to 1.5 and more preferably about 1. The ratio of the wt% of first material to the wt% of second material may be in the range 0.5 to 2, preferably in the range 0.75 to 1.5, more preferably about 1 to 1. Said particulate material may include a third material which is preferably adapted to lower the pH of the silicate solution. Said third material may be a colloid, suitably colloidal silica or an inorganic salt, suitably a phosphate, with aluminium phosphate being preferred. Where a third material is provided, preferably less than 30wt% more preferably less than 20wt%, especially less than 10wt% of said particulate material is comprised by said third material. The pH of said liquid may be greater than 9.0, is preferably greater than 9.5 and, more preferably, greater than 10.0. Especially preferred is the case wherein the pH is greater than 10.5. The pH is suitably controlled so that the silicate remains in solution and does not form a gel. A gel is generally formed when the pH of a silicate solution falls below pH9. The pH of said liquid is preferably less than 14, more preferably less than 13. It is understood that the pH of the liquid affects the adhesion of the hydrophilic layer on the support. It is found that the use of a liquid having a pH as described can lead to good adhesion. The liquid may include other compounds for adjusting its properties. For example, the liquid may include one or more surfactants. Said liquid may include 0 to 1 wt% of surfactant(s) . A suitable class of surfactants comprises anionic sulphates or sulphonates. The liquid may include viscosity builders for adjusting the viscosity of the liquid. Said liquid may include 0 to 10 wt%, preferably 0 to 5 wt% of viscosity builder(s) . Also, the liquid may include dispersants for dispersing the inorganic particulate material throughout the liquid. Said liquid may include 0 to 2 wt% of dispersant(s) . A suitable dispersant may be sodium hexametaphosphate. Hydrophilic layers of planographic printing plates have been proposed which include organic polymers, for example thermoplastic polymers, for increasing the strength and/or hardness of the hydrophilic layers. Said liquid used in the method of the present invention preferably does not include a thermoplastic organic polymeric material, for example polyvinylidene fluoride or the like. Said liquid may have a viscosity of less than 100 centipoise when measured at 20°C and a shear rate of 200s' 1 using a Mettler Rheomat 180 Viscometer incorporating a double gap measuring geometry. Preferably, said viscosity is less than 50 centipoise, more preferably less than 30 centipoise when measured as aforesaid. Especially preferred is the case wherein the viscosity is less than 20 centipoise. Said liquid may be applied to said support by any suitable means which is preferably non-electrochemical. Said liquid may be applied to both sides of said support in order to form a hydrophilic layer on both sides. A support with such a layer on both sides may be used to prepare a double-sided lithographic plate. Alternatively, if such a support is used for a single- sided plate, the side of the plate which does not carry an image layer may be protected by the hydrophilic layer. Said liquid is preferably applied to only one surface of said support. Said liquid may be applied to said support to form a hydrophilic layer having an average thickness after drying, of less than 20 μm, preferably less than 10 μm and, more preferably, less than 5 μm. Especially preferred is the case wherein the average thickness is less than 3 μm. The thickness of the hydrophilic layer may be greater than 0.1 μm, preferably greater than 0.3 μm and, more preferably, greater than 0.5μm. Said particulate material preferably defines formations in said hydrophilic layer which render said layer non-planar and which are arranged such that, when an image layer is applied over said hydrophilic layer, corresponding formations are defined on the surface of the image layer in a manner similar to that described in U.K. Patent Application No. GB 2 277 282, the contents of which are incorporated herein by reference. The method preferably includes the steps of providing suitable conditions for the removal of water from the liquid after it has been applied to the support. Suitable conditions may involve passive or active removal of water and may comprise causing an air flow over the support and/or adjusting the humidity of air surrounding the support. Preferably, the method includes the step of arranging the support in a heated environment. The support may be placed in an environment so that its temperature does not exceed 230°C, preferably does not exceed 200°C and, more preferably, does not exceed 175°C. Especially preferred is the case wherein the support temperature does not exceed 150°C. The support may be arranged in the heated environment for less than 180 seconds, preferably less than 120 seconds and, more preferably, less than 100 seconds. The support may comprise aluminium or an alloy. In this event, it is found to be advantageous to arrange the support in an environment wherein the temperature is less than 230°C as described above since, at this temperature, annealing of the support is not significant and, therefore, the tensile strength of the support is maintained at an acceptable level. More particularly, the tensile strength of the aluminium, suitably measured using a Hounsfield tensile testing machine, may be at least 100 MPa, preferably at least 110 MPa and, more preferably, at least 120 MPa. Especially preferred is the case wherein the tensile strength is at least 140 MPa. The liquid described above may also be advantageously applied to a plastics support, for example of polyester, in order to provide a hydrophilic layer thereon, in view of the fact that the liquid needs only to be cured at a relatively low temperature for a short time. As will be appreciated, curing at a relatively high temperature for long periods might otherwise detrimentally affect the properties of the plastics material. The removal of water from the liquid applied to the support is believed to cause the silicate to polymerise and bind the inorganic particulate material in position. Thus, it should be appreciated that one advantage of the method of the present invention may be that a relatively wide range of support materials may be used. For example, where the support material is aluminium or an alloy, a relatively low grade metal could be used compared to the grade of metal usually used for lithographic plates. Additionally and/or alternatively, a metal which is more resistant to, for example developer chemicals, could be used. Furthermore, the method may be used to apply a hydrophilic layer to other types of support materials, for example other metals, foil coated paper and plastics. A support material may be pretreated prior to the application of said hydrophilic layer. Where the support material is aluminium or an aluminium alloy, it may be pretreated by one or more conventional methods used in the surface treatment of aluminium, for example caustic etch cleaning, acid cleaning, brush graining, mechanical graining, slurry graining, sand blasting, abrasive cleaning, electrocleaning, solvent degreasing, ultrasonic cleaning, alkali non-etch cleaning, primer coating, grit/shot blasting and electrograining. Details of such methods are provided in: "The surface treatment and finishing of aluminium and its alloys" S. Wernick, R. Pinner and P. G. Sheasby published by Finishing Publication Ltd., ASM International, 5th edition 1987. Where the support material is pretreated, preferred pretreatments are those which involve adjusting the character of the surface of the support material, for example those involving cleaning, graining or the like. If a surface coating is, however, applied on the surface of the support material, the coating is preferably applied as a liquid. Preferably, said liquid comprising a silicate solution as described above is applied to a substantially dry surface on said support. Preferably, said liquid is applied directly onto said support material of said support. Preferably, the support material is cleaned and/or etched prior to being contacted with said liquid. Cleaning and/or etching may be achieved using an alkaline liquid, for example sodium hydroxide, optionally with additives such as sodium gluconate and/or sorbitol. The support material may also be subjected to a desmutting treatment, suitably using nitric acid. After this treatment, the support material should be rinsed and/or dried prior to being contacted with said liquid. The method of preparing a substrate preferably includes the step of adjusting the pH of the surface of the hydrophilic layer formed on said support by contacting the surface with aluminium sulphate so that said hydrophilic layer is compatible with an image layer. The method preferably includes the step of creating an image layer, suitably directly on said hydrophilic layer, so that the hydrophilic layer is located between the image layer and the support. The term "image layer" includes a layer that can subsequently be partially removed in order to define areas to be printed and includes a layer which already defines areas to be printed. The image layer may be provided over the entire surface of said hydrophilic layer. It may comprise any known photosensitive material whether arranged to form a positive or negative plate. Examples of photosensitive materials include diazonium/diazide materials, polymers which undergo depo 1y er i sat ion or addition photopolymerisation and silver halide gelatin assemblies. Examples of suitable materials are disclosed in GB 1 592 281, GB 2 031 442, GB 2 069 164, GB 2 080 964, GB 2 109 573, EP 0 377 589, US 4 268 609 and US 4 567 131. Preferably, the light sensitive material is a quinone diazide material. Alternatively, said image layer in the form of a desired image for use in planographic printing may be deposited over said hydrophilic layer by a deposition process such as ink jet or laser ablation transfer. An example of the latter is described in US 5 171 650. Said image layer is preferably arranged over said hydrophilic layer so that formations are defined on the surface of the layer due to formations formed in said hydrophilic layer by particulate material therein. The formations may suitably be arranged to define channels between the light-sensitive layer and a mask so that air can escape from between the layer and the mask in order to decrease the draw-down time of the mask on the layer prior to exposure of the printing plate. The invention extends to a substrate for a planographic printing member preparable by the method described. It has been found that a substrate prepared in the method includes a hydrophilic layer which adheres well to the support. Where the support is aluminium or an alloy, this is believed to be due to the formation of aluminium silicate (or at least alumino silicate bonds) on the surface of the support. Thus, the invention suitably provides a substrate wherein chemical bonds are formed between a support material and a hydrophilic layer on the support material. Furthermore, when used in printing, the substrate is found to have wear resistance which is comparable to that of conventional electrograined and anodised substrates. Preferably, a substrate for a planographic printing plate comprises a support and a hydrophilic layer which includes a binder material derived or derivable from a silicate solution and a particulate material. Said silicate solution may be as described in any statement herein. It is believed that said binder material derived from a silicate solution of the type described contains extremely small three-dimensional silicate polymer ions carrying a negative charge. Removal of water from the system as described above causes condensation of silanol groups to form a polymeric structure which includes -Si-0- Si- moieties. Accordingly, the invention extends to a substrate for a planographic printing member comprising a support and a hydrophilic layer which includes a binder material comprising a polymeric structure which includes - Si-O-Si- moieties in which a particulate material is arranged. Said particulate material may be as described in any statement herein. Preferably, 30 to 80 wt%, more preferably 40 to 70 wt%, of said hydrophilic layer is composed of said particulate material. Said particulate material preferably includes a first material as described in any statement herein. Said first material preferably has a hardness of greater than 8 Modified Mohs (on a scale of 0 to 15) , preferably greater than 9 and, more preferably, greater than 10 Modified Mohs. Said first material in said hydrophilic layer may have a mean particle size and/or particle size distribution as described above for said first material when in said liquid. Said particulate material on said substrate may include at least 20 wt%, preferably at least 30 wt%, more preferably, at least 40 wt% of said first material. Said particulate material preferably includes a second material as described in any statement herein. Said second material in said hydrophilic layer may have a mean particle size and/or particle size distribution as described above for said second material when in said liquid. Said particulate material on said substrate may include at least 20 wt%, preferably at least 30 wt%, more preferably, at least 40 wt% of said second material. In the layer, the ratio of the wt% of first material to the wt% of εecond material may be in the range 0.5 to 2 , preferably in the range 0.75 to 1.5, more preferably, about 1 to 1. Said particulate material may include a third material as described in any statement herein. Said hydrophilic layer preferably does not include a thermoplastics organic polymeric material, for example polyvinylidene fluoride or the like. Said hydrophilic layer preferably has an average thickness of less than 20 μm, preferably less than 10 μm and, more preferably, less than 5 μm. Said hydrophilic layer preferably has an average thickness of greater than 0.1 μm, preferably greater than 0.3 μm, more preferably, greater than 0.5 μm. Said hydrophilic layer may have an Ra, measured using a stylus measuring instrument (a Ho melmeter T2000) with an LV-50 measuring head, in the range 0.1 to 2 μm, suitably in the range 0.2 to 2 μm, preferably in the range 0.2 μm to 1 μm, more preferably in the range 0.3 to 0.8 μm, especially in the range 0.4 to 0.8 μm. Said hydrophilic layer may include 1 to 20 g of material per metre squared of substrate. Preferably said layer includes 5 to 15 g, more preferably 8 to 12 g, of material per metre squared of substrate. Most preferably, said layer includes about 10 g of material per metre squared. Said support may comprise any type of support conventionally used for printing members. For example, it may comprise a metal such as aluminium, steel, tin or alloys thereof; paper coated with a metal such as aluminium foil; a plastics material such as polyester; or plastics material coated with a metal. Preferably, the support is aluminium or an alloy. The method of the present invention can be used to optimise the tensile strength of aluminium by reducing/eliminating annealing of the metal during curing of the hydrophilic layer. Thus, the support of the present invention preferably has a tensile strength of at least 100 MPa, preferably at least 110 MPa and, more preferably, at least 120 MPa. Especially preferred is the case wherein the tensile strength is at least 140 MPa. Additionally, the method of the present invention may minimise deformation of the support material during support preparation. For example, it is found that, using the method described on an aluminium support, the maximum wave height may only be about 2 mm and the maximum number of waves per metre may be 3. The invention extends to a planographic printing member comprising a substrate as described above and an image layer over the hydrophilic layer of the substrate. Preferably, the particulate material in the hydrophilic layer is arranged between the surface of the support and the image layer so that formations are provided on the surface of the image layer as a result of particulate material under the layer. Said image layer preferably comprises a light sensitive material, a quinone diazide material being preferred. Any feature of any aspect of an invention described herein may be combined with any feature of any other invention described herein. The invention will now be described by way of example. Preparation of lithographic printing plate. Example 1 Step 1 Preparation of Aluminium A 0.3 mm gauge aluminium alloy sheet of designation AA1050 was cut to a size of 230 mm by 350 mm, with the grain running lengthways. The sheet was then immersed face up in a solution of sodium hydroxide dissolved in distilled water (lOOg/1) at ambient temperature for 60 seconds and thoroughly rinsed with water. Step 2 Preparation of coating formulation The following reagents are used in the preparation: - Sodium silicate solution having a ratio Si0 2 : Na 2 0 in the range 3.17 to 3.45 (average about 3.3) ; a composition of 27.1 - 28.1 wt% Siθ 2 , 8.4 - 8.8 Wt% Na 2 0, with the balance being water; and a density of about 75 Twaddel (°Tw) , equivalent to 39.5 Baume (°Be) and a specific gravity of 1.375. - Deionised water having a resistivity of 5 Mohm.cm - A1 2 0 3 powder comprising alumina (99.6%) in the shape of hexagonal platelets. The mean particle size is 3 μm. The powder has a hardness of 9 Moh (on a 0 - 10 hardness scale) . - Rutile titanium dioxide provided with an inorganic coating of A1 2 0 3 , ZnO and ZnP0 4 . The mean crystal size is 0.23 μm. Deionised water (48g; 24 wt%) and sodium silicate solution (80 g; 40 wt%) were added to a 250ml beaker and the solution sheared using a Silverson high shear mixer operating at maximum speed. Titanium dioxide powder (36g; 18 wt%) was then added in portions of approximately 2g every ten seconds. On completion of the addition, the liquid was sheared for a further two minutes. Then, alumina powder (36g; 18 wt%) was added in portions of approximately 2g every ten seconds. On completion of the addition, the liquid was sheared for a further two minutes. The viscosity of the liquid is found to be about 10 centipoise when measured at 20°C and a shear rate of 200s "1 using a Mettler Rheomat 180 Viscometer incorporating a double gap measuring geometry. Step 3 Application of coating formulation The coating formulation prepared in Step 2 was coated onto the aluminium sheet prepared in Step 1 using a rotating Meyer bar coater (designation K303) to give a 6 μm wet film thickness. Step 4 Drying the formulation The coated sheet prepared in Step 3 was placed in an oven at 130° for 80 seconds. The plate was then removed from the oven and allowed to cool to ambient temperature. Step 5 Post-drying treatment The dried sheet prepared in Step 4 was immersed in aluminium sulphate (0.1M) for thirty seconds. The sheet was then spray rinsed for about twenty seconds using tap water and fan dried. Step 6 Application of light sensitive coating A printing plate was produced from the sheet prepared in Step 5 by coating, using a Meyer bar, a light sensitive material of the quinone diazide/novolak resin type at a dry coating weight of 2 g/m 2 . The light sensitive material was dried at 130°C for 80 seconds. The printing plate prepared in Step 6 was found to have a comparable performance to commercial printing plates. Advantageously, however, it can be produced at a lower cost. Example 2 The procedure of Example 1 was generally followed except that a different coating formulation was used in step 2. The formulation was prepared by adding the following components to deionized water (40wt%) in the order given. After each addition, the formulation was subjected to high shear mixing. COMPONENT WT% Hombitan LW (Trade Mark) -anatase Ti0 2 (mean 14.2 primary particle size of 0.2 μm) Microgrit C3 (Trade Mark) for alumina powder 14.2 (mean primary particle size of 3 μm) Sodium silicate solution as in Eg.l. 31.2 The printing plate prepared was found to have performance comparable to the plate prepared in Example 1. Example 3 The procedure of Example 2 was followed except that the following components were mixed in step 2 in the order given below. COMPONENT WT% Deionized water. 21.51 Hombitan LW (Trade Mark) as in Eg. 2. 14.15 Alumina powder as in Eg. 2. 14.15 Sodium polysilicate solution - having a Si0 2 : 50.19 Na 2 0 ratio of 5.2 : 1 and containing 22.78% solid. The printing plate prepared was found to have a performance comparable to the plate prepared in Example 1. Example 4 The procedure of Example 2 was followed by mixing the following components in step 2 in the order given below. COMPONENT WT% Deionized water. 33.29 Hombitan LW (Trade Mark) as in Eg. 2. 11.83 Alumina powder as in Eg. 2. 11.83 Bindzil 15/500 (Trade Mark) a colloidal silica 1.1 having average on particle size of 7 nm Sodium polysilicate as in Eg. 3. 41.95 The printing plate prepared was found to have a performance comparable to the plate prepared in Example 1, except for a slight dye stain of the hydrophilic layer. Example 5 The procedure of Example 2 was followed by mixing the following components in step 2 in the order given below. COMPONENT WT% Deionized water. 40 Hombitan LW as in Eg. 2. 14.23 Alumina powder as in Eg. 2. 13.23 Fabutit 748 (Trade Mark) - aluminium phosphate 1.0 Sodium silicate as per Example 1. 31.5 The printing plate prepared was found to have a performance comparable to the plate prepared in Example 1. The reader's attention is directed to all papers and documents which are filed concurrently with or previous to this specification in connection with this application and which are open to public inspection with this specification, and the contents of all such papers and documents are incorporated herein by reference. All of the features disclosed in this specification (including any accompanying claims, abstract and drawings) , and/or all of the steps of any method or process so disclosed, may be combined in any combination, except combinations where at least some of such features and/or steps are mutually exclusive. Each feature disclosed in this specification (including any accompanying claims, abstract and drawings) , may be replaced by alternative features serving the same, equivalent or similar purpose, unless expressly stated otherwise. Thus, unless expressly stated otherwise, each feature disclosed is one example only of a generic series of equivalent or similar features. The invention is not restricted to the details of the foregoing embodiment(s) . The invention extends to any novel one, or any novel combination, of the features disclosed in this specification (including any accompanying claims, abstract and drawings) , or to any novel one, or any novel combination, of the steps of any method or process so disclosed.

Claims: CLAIMS 1. A method of preparing a substrate for a planographic printing member including the step of forming a hydrophilic layer on a support by contacting the support with a liquid comprising a silicate solution in which particulate material is dispersed. 2. A method according to Claim 1, wherein said silicate solution is formed from silicate wherein the ratio of the number of moles of Si species to the number of moles of cationic species is in the range 0.25 to about 6. 3. A method according to Claim 1 or Claim 2, wherein said silicate solution is an alkali metal silicate. 4. A method according to any preceding claim, wherein the ratio of the weight of silicate to the weight of particulate material in the liquid is in the range 0.1 to 2. 5. A method according to any preceding claim, wherein said particulate material comprises a first material which has a hardness of greater than 8 Modified Mohs (on a scale of 0 to 15) . 6. A method according to Claim 5, wherein said first material has a mean particle size of at least 0.1 μm. 7. A method according to Claim 5 or Claim 6, wherein said first material comprises alumina. 8. A method according to any preceding claim, wherein said particulate material comprises a second material. 9. A method according to Claim 8, wherein said second material has a mean particle size of at least 0.001 μm. 10. A method according to Claim 8 or Claim ' 9, wherein said second material is a pigment. 11. A method according to any preceding claim, wherein said particulate material includes a third material. 12. A method according to any preceding claim, wherein the pH of said liquid is greater than 9. 13. A method according to any preceding claim, wherein said liquid has a viscosity of less than 100 centipoise. 14. A method according to any preceding claim, wherein said liquid is applied to said support to form a hydrophilic layer having an average thickness after drying of less than 20 μm. 15. A method according to any preceding claim, wherein said εupport comprises aluminium or an alloy or a plastics material. 16. A substrate for a planographic printing member preparable by a method according to any of Claims 1 to 15. 17. A substrate for a planographic printing member comprising a εupport and a hydrophilic layer which includes a binder material derived or derivable from a silicate solution and a particulate material. 18. A substrate for a planographic printing member comprising a support and a hydrophilic layer which includes a binder material comprising a polymeric structure which includes -Si-O-Si- moieties in which a particulate material is arranged. 19. A substrate according to Claim 17 or Claim 18, including particulate material as described in any of Claims 1 to 16. 20. A substrate according to any of Claims 17 to 19, wherein said hydrophilic layer has an average thickness of less than 20 μm. 21. A substrate according to any of Claims 17 to 20, wherein said hydrophilic layer has an Ra in the range 0.1 to 2 μm. 22. A substrate according to any of Claims 17 to 21, wherein said hydrophilic layer includes lg to 20g of material per metre squared of substrate.

Inventors: BHAMBRA HARJIT SINGH, ORGAN ROBERT MICHAEL, BHAMBRA, HARJIT, SINGH, ORGAN, ROBERT, MICHAEL
Applicants: BHAMBRA HARJIT S, HORSELL GRAPHIC IND LTD, ORGAN ROBERT M, BHAMBRA, HARJIT, SINGH, HORSELL GRAPHIC INDUSTRIES LIMITED, ORGAN, ROBERT, MICHAEL
Application year: 1996
Main classification: B41N3
IPC codes: B41N3