Method of producing inflation film, apparatus therefor and molded articles thereof

Abstract: A method of producing an inflation film (31) comprising the steps of melting an ultra-high-molecular-weight polyolefin in an extruder (1), extruding the molten polyolefin from a screw die (20), and blowing a gas into a molten tubular film formed by extrusion. An apparatus for producing an inflation film comprises an extruder (1) provided with a first screw (3), and a screw die (20) having an L/D of at least 5 and is provided at the end of the extruder (1), wherein the screw die (20) comprises a second screw (21) which rotates independently of the first screw (3), a mandrel (23) coupled to the end of the second screw (21) and rotates together with the second screw (21), an outer tube die (22) in which the mandrel (23) is inserted, and a gas passage extending in the second screw (21) and in the mandrel (23). An inflation film (31) comprises an ultra-high-molecular-weight polyolefin having a tensile strength at break of greater than 1660 kg/cm 2 in a machine direction and greater than 1600 kg/cm 2 in a transverse direction, an impact strength of greater than 9500 kg·cm/cm, a thickness of from 10 to 1000 µm, an R-value of not larger than 10 µm and an intrinsic viscosity [η] of at least 7 dl/g.

Description: The present invention relates to a method of producing an inflation film, an apparatus therefor, and an inflation film obtained thereby. More specifically, the invention relates to a method of producing an inflation film of which the mechanical properties such as tensile strength, impact strength, etc. and the thickness can be adjusted over wide ranges, to an apparatus therefor, and to an inflation film having excellent properties obtained thereby. An ultra-high-molecular-weight polyolefin features superior impact strength, abrasion resistance, resistance against chemicals and tensile strength to those of general-purpose polyolefins, and is finding spreading applications as an engineering resin. However, the ultra-high-molecular-weight polyolefin exhibits a very higher melt-viscosity and poorer fluidity than those of the general-purpose polyolefins. Therefore, the ultra-high-molecular-weight polyolefin alone cannot be molded by using a molding machine for general-purpose polyolefins. Therefore, the present applicant has previously proposed a method of producing a biaxially drawn film by extrusion-molding the ultra-high-molecular-weight polyolefin to which is mixed large amounts of a plasticizer (Japanese Patent Publication No. 16330 /1992). When this method is employed, however, a plasticizer must be extracted from the obtained polyolefin film depending upon the applications. The present applicant has further proposed a method of producing an inflation film by using a tube die having a mandrel that rotates accompanying the rotation of a screw of an extruder without using a plasticizer (Japanese Patent Publication No. 55433 /1994 which corresponds to the European Application EP 0 213 807 A2. According to this method, however, the tubular film that is extruded is turned sideways, permitting the upper portion to become thin and lower portion to become thick, causing a difference in the thickness between the upper portion and the lower portion. In order to increase the rate of production, furthermore, the rotating speed of the mandrel must be increased accompanying an increase in the rotating speed of the screw giving rise to the occurrence of a problem in that the resin is deteriorated due to friction. In order to erase flight marks of the resin, furthermore, it is required to employ a mandrel of an increased length. There is also a problem that the apparatus becomes large-sized and its installation space becomes wide. In order to provide optimum inflation films depending upon the applications, furthermore, it becomes necessary to adjust the mechanical properties such as tensile strength and impact strength as well as the thickness of the obtained inflation films over wide ranges. In view of the above-mentioned technical assignments, the present inventors have conducted study to solve problems, and have found the fact that the mechanical properties such as tensile strength and impact strength, drawing ratio in machine direction and thickness can be adjusted over wide ranges, and an inflation film can be formed permitting the molecular weight to drop less than those of the conventional film-producing methods, by melting a thermoplastic resin in an extruder, by using a screw die having an L/D (as defined hereinafter) of at least 5 and having a mandrel which rotates independently of the screw of the extruder, the mandrel rotating at a speed as low as possible, and have confirmed that the inflation film exhibits excellent properties of an ultra-high-molecular-weight polyolefin, and have thus arrived at the present invention. The aim of the present invention therefore is to provide a method of producing an inflation film capable of adjusting the mechanical properties such as tensile strength and impact strength as well as drawing ratio in a machine direction and thickness of the inflation film over wide ranges, an apparatus therefor, and an inflation film which suppresses the reduction in the molecular weight at the time of molding, exhibits properties of an ultra-high-molecular-weight polyolefin and features uniform thickness. The present invention was proposed in order to achieve the above-mentioned object, and features the formation of an inflation film by a particular method by using a screw die having an L/D of at least 5 and having a mandrel which rotates independently of a screw of an extruder, the mandrel rotating at a speed as low as possible, the obtained inflation film featuring excellent tensile strength and impact strength since a drop in the molecular weight is suppressed during the molding and without unevenness in the thickness. That is, according to the present invention, there is provided a method of producing an inflation film comprising the steps of melting an ultra-high-molecular -weight polyolefin in an extruder equipped with a first screw, extruding the ultra-high-molecular-weight polyolefin in a molten state from a screw die having an L/D of at least 5 and having a second screw and a mandrel connected thereto, the second screw being permitted to rotate independently of the first screw of the extruder, and blowing a gas into a tubular film of a molten state formed by extrusion. According to the present invention, furthermore, there is provided a method of producing an inflation film wherein the rotating speeds of the first screw and of the second screw are variable independently of each other, and the rotating speed of the second screw is set to be lower than the rotating speed of the first screw. According to the present invention, furthermore, there is provided a method of producing an inflation film wherein the ultra-high-molecular-weight polyolefin has an intrinsic viscosity [η] of not smaller than 5 dl/g. According to the present invention, furthermore, there is provided a method of producing an inflation film wherein the ultra-high-molecular-weight polyolefin is an ultra-high-molecular-weight polyethylene. According to the present invention, there is provided an apparatus for producing an inflation film comprising an extruder provided with a first screw, and a screw die having an L/D of at least 5 and is provided at the end of the extruder, wherein the screw die comprises a second screw which rotates independently of the first screw, a mandrel coupled to the end of the second screw and rotates together with the second screw, an outer tube die in which the mandrel is inserted, and a gas passage extending in the second screw and in the mandrel. According to the present invention, furthermore, there is provided an apparatus for producing an inflation film wherein a stabilizer rod is coupled to an end of the mandrel. According to the present invention, furthermore, there is provided an inflation film comprising an ultra-high-molecular-weight polyolefin having an intrinsic viscosity [η] of at least 7 dl/g and a thickness of from 10 to 1000 µ m, the inflation film further having a tensile strength at break of greater than 1660 kg/cm 2 in a machine direction and greater than 1600 kg/cm 2 in a transverse direction, an impact strength of greater than 9500 kg·cm/cm, and an R-value, which is an index of uniformity of the film thickness, of not larger than 10 µ m. According to the present invention, furthermore, there is obtained an inflation film comprising an ultra-high-molecular-weight polyolefin having a tensile strength at break of greater than 1660 kg/cm 2 in a machine direction and greater than 1600 kg/cm 2 in a transverse direction, an impact strength of greater than 9500 kg·cm/cm, a thickness of from 10 to 1000 µ m, an R-value of not larger than 10 µ m and an intrinsic viscosity [η] of at least 7 dl/g, said inflation film being obtained by melting the ultra-high-molecular-weight polyolefin in an extruder, extruding the molten ultra-high-molecular-weight polyolefin from a screw die having an L/D of at least 5 and having a mandrel which rotates independently of the screw of the extruder, and blowing a gas into the molten tubular film formed by the extrusion to accomplish both an inflation ratio and a drawing ratio in the machine direction which are not smaller than 7. According to the present invention, furthermore, there is provided an inflation film wherein the ultra-high-molecular-weight polyolefin is an ultra-high-molecular-weight polyethylene. The present invention will be further described by way of example with reference to the accompanying Figure, Fig. 1, which is a sectional view of an apparatus for producing an inflation film according to the present invention. Reference numeral 1 denotes an extruder, 3 denotes a first screw, 20 denotes a screw die, 21 denotes a second screw, 22 denotes an outer tube die, 23 denotes a mandrel, 24 denotes a gas passage, 26 denotes a stabilizer rod, and 27 denotes a windbreak cylinder. A first invention (claims 1 to 4) of the present invention is concerned with a method of producing an inflation film, wherein a feature resides in that a screw die having an L/D of at least 5 rotates independently of a screw of an extruder to extrude an ultra-high-molecular-weight polyolefin in a molten state. That is, according to this method of producing an inflation film, the mandrel of the screw die having the second screw rotates independently of the first screw of the extruder. It is therefore allowed to rotate the second screw at a speed lower than the rotating speed of the first screw by increasing the diameter of the screw die and, hence, to prevent the resin from being deteriorated by the heat of friction between the mandrel and the resin. It is therefore made possible to produce an inflation film enabling the mechanical properties such as tensile strength (in both the machine direction and the transverse direction) and impact strength as well as the drawing ratio in the machine direction and the thickness to be adjusted over wide ranges. A gas is blown into the tubular film extruded from the screw die, whereby the tubular film inflates and is, then, drawn and cooled simultaneously to obtain a film which is a finished product. In the present invention, it is important that the ratio of the inner diameter of an outer tube die 22 at a screw die outlet 20C to the length of from an outer die inlet 20A to the screw die outlet 20C, i.e., L/D of the screw die, is not smaller than 5, preferably, is not smaller than 15 and, more preferably, is from 20 to 70. When the screw die has the L/D of not larger than 5, the thermoplastic resin is not completely uniformly melted before it is extruded from the die. When the air is blown into the tubular film that is extruded from the die, therefore, the tube is often nonuniformly inflated or is broken, making it difficult to obtain a good film. Though there is no particular upper limitation, it is desired that the upper limit of L/D is not larger than 70 from the practical point of view. The ratio L/D of the screw die has a relationship to the productivity, and a forming speed can be increased with an increase in the L/D. Though the air is usually blown into the tubular film, nitrogen may be blown, too. When a gas is to be blown into the tubular film of a molten state, it is desired that the inflation ratio is not smaller than 7, preferably, from 7 to 20 and, particularly, from 8 to 12. When the inflation ratio is smaller than 7, the thickness tends to become nonuniform in the transverse direction (TD). Besides, since the crystalline orientation is small in the transverse direction, it becomes difficult to improve mechanical properties such as tensile strength and impact strength. When the inflation ratio exceeds 20, on the other hand, the film becomes turbid appearing white and tends to be ruptured. In the present invention, it is desired that the drawing ratio in the machine direction is not smaller than 7, preferably, from 7 to 40 and, particularly, from 8 to 30. When the drawing ratio in the machine direction is not larger than 7, the balloon (inflation tube) tends to swing and, as a result, the thickness becomes nonuniform in the machine direction (MD) and in the transverse direction (TD) exhibiting a great fluctuation in the mechanical properties. When the drawing ratio in the machine direction exceeds 40, on the other hand, the film tends to be ruptured. In the present invention, the inflation ratio stands for a ratio of the circumferential length of the tube of before being inflated at the screw die outlet (practically, calculated as the inner diameter of the outlet of the outer tube die) to the circumferential length of the tube after inflated, and the drawing ratio in the machine direction stands for a ratio of the take-up speed of the pinch roll to the speed (linear velocity) of the resin flowing out from the die. In the present invention, furthermore, it is desired that the ultra-high-molecular-weight polyolefin is extrusion-molded at a temperature which is usually higher than its melting point but is lower than 370°C and, preferably, from 160°C to 350°C though it may vary depending upon the kind of the ultra-high-molecular-weight polyolefin. When the extrusion-molding temperature is lower than the melting point, the resin tends to be clogged in the die causing the apparatus to be broken. When the molding is conducted under such temperature conditions that the temperature of the extruder is from 230°C to 350°C, that the temperature at the inlet portion to the intermediate portion of the screw die is from 190°C to 230°C, and that the temperature at the intermediate portion to the outlet portion of the screw die is from 180°C to 160°C, then, no land-melt fracture occurs in the screw die, which is desirable. The inflated film is cooled over its outer portion by the air that is uniformly blown from an air ring equipped with a blower, or is cooled by a cooling ring of the water-cooled type or the air-cooled type that comes into intimate contact with the film. The film after cooled is gradually folded by a customary manner, i.e., by a stabilizer board, and is turned into a flat film consisting of two pieces by the pinch roll, and is taken up by a product winder. The film obtained according to the present invention can be heat-set in advance to lower the thermal shrinkage factor to smaller than about 10%. As the ultra-high-molecular-weight polyolefin, there can be preferably used an ultra-high-molecular-weight polyolefin having an intrinsic viscosity [η] of not smaller than 5 dl/g, preferably, not smaller than 7 dl/g and, more preferably, from 8 to 25 dl/g as measured in a decalin solution at 135°C. The ultra-high-molecular-weight polyolefin having an intrinsic viscosity of smaller than 5 dl/g fails to exhibit satisfactory mechanical properties such as tensile strength and impact strength. Moreover, because of its low melt viscosity, the molten ultra-high-molecular-weight polyolefin rotates together with the mandrel in the screw die and is twisted. Or, the thickness becomes nonuniform due to deflection of the mandrel, making it difficult to obtain a uniform film. Though there is no particular limitation on the upper limit of the intrinsic viscosity [η], those having an intrinsic viscosity in excess of 25 dl/g exhibit too high melt viscosity and can be extrusion-molded less favorably. As the ultra-high-molecular-weight polyolefins, ultra-high-molecular-weight polyethylene and ultra-high-molecular-weight polypropylene may be used. However, among the ultra-high-molecular-weight polyolefins, an ultra-high-molecular-weight polyethylene can be favorably used. The ultra-high-molecular-weight polyethylene has a straight-chain molecular structure. Upon drawing, therefore, the inflation film that is molded exhibits further increased strength and elasticity. Desirably, the inflation film of the ultra-high-molecular-weight polyethylene produced according to the present invention exhibits an intrinsic viscosity [η] of not smaller than 7 dl/g and, more preferably, from 8 to 25 dl/g. The apparatus for producing an inflation film which pertains to a second invention (claims 5 and 6) of the present application has a feature in regard to the screw die coupled to the extruder. That is, the screw die of the present invention has a second screw separately from the first screw, and a mandrel coupled to the end of the second screw rotates together with the second screw. Besides, the first screw of the extruder and the second screw rotates at speeds independent of each other, and the second screw can be rotated at a speed lower than the rotating speed of the first screw. Owing to this constitution, the mechanical properties of the inflation film such as tensile strength, impact strength, drawing ratio in the machine direction and the film thickness can be adjusted over wide ranges in the same manner as stated in claim 1. In the apparatus for producing the inflation film, furthermore, a stabilizer rod is provided at the end of the mandrel in order to prevent the ultra-high-molecular-weight polyolefin of the molten state extruded in the form of a pipe from oscillating in the transverse direction being caused by the pressure of the air blown from the air ring. Therefore, the inflated film features further improved thickness precision. The inflation film produced by using the apparatus of the present invention has a difference (R-value) between a maximum thickness and a minimum thickness in the circumferential direction of film of not larger than 10 µ m. The apparatus for producing the inflation film of the present invention will now be described with reference to the drawing. Referring to Fig. 1, an extruder 1 is equipped with a grooved cylinder 2 and a first screw 3 having a compression ratio of from 1 to 2.5 and, preferably, from 1.3 to 1.8. A torpedo 10 is coupled by screws to an end of the first screw 3. It is desired that the torpedo 10 has a conical shape to prevent the resin from staying at the end of the first screw 3. A screw die 20 is provided at the end of the torpedo 10, i.e., on the downstream side in a direction in which the molten resin flows in a manner that the axis of the screw die 20 is at right angles with the axis of the torpedo 10. The screw die 20 has a second screw 21 at a position opposed to the torpedo 10. The second screw 21 is rotated by a drive means (not shown) independently of the first screw 3. The second screw 21 has a hollow outer tube die 22 in which is formed space of nearly a cylindrical shape which gradually contracts toward the upper direction in Fig. 1. A mandrel 23 is inserted in space of the outer tube die 22. The mandrel 23 is secured to an end (upper end) of the second screw 21 and rotates together with the second screw 21. A gas passage 24 is formed in the second screw 21 and in the mandrel 23. The gas passage 24 runs from the lower end of the second screw 21 up to the end of the stabilizer rod 26 passing through a metal shaft. In the apparatus for producing the inflation film, the ultra-high-molecular-weight polyolefin powder is stably supplied toward the front side of the extruder through a groove 2A of the grooved cylinder 2. The screw die 20 has an L/D of not smaller than 5, preferably, not smaller than 15 and, more preferably, from 20 to 70. The ratio (S1/S2) of a sectional area S2 of the resin flow passage at an intermediate portion 20B of the screw die to a sectional area S1 of the resin flow passage at an end 20A of the second screw is from 0.5 to 2.0 and, preferably, from 0.8 to 1.5. Furthermore, the ratio (S2/S3) of a sectional area S3 of the resin flow passage at an outlet 20C of the screw die to the sectional area S2 is from 2.0 to 10.0 and, preferably, from 3.0 to 6.0. There arises no particular problem when the ratio S1/S2 lies within a range of from 0.5 to 2.0. When the ratio S2/S3 becomes smaller than 2.0, however, the molten resin is not completely uniformalized. When the ratio S2/S3 exceeds 10, on the other hand, the resin pressure becomes so great that it becomes difficult to extrusion-mold the tubular film. Basically as described above, the area of the resin flow passage of the screw die 20 becomes narrow toward the outlet 20C of the screw die. That is, though the screw die is tapered, it is desired that the upper end of the screw die (portion on the upper side of 20C) has a constant area of resin flow passage, i.e., remains straight from the standpoint of maintaining a high dimensional precision of the molded articles. The straight portion usually has an L/D of from about 0.1 to about 0.5. The apparatus for producing the inflation film of the present invention has a significant feature in the above-mentioned constitution. The apparatus is further equipped, on the downstream side of the screw die 20, with a stabilizer plate for folding and taking up an inflation film 31 having a thickness of from 10 to 1000 µ m which is obtained by cooling a pipe-like parison 30 extruded from the screw die 20 by the air ring 25 and by inflating it with a gas such as the air at an inflation ratio of not smaller than 7 through the gas passage 24, a pinch roll, and a take-up device (which are not shown) which have been employed in the conventional inflation film-forming machines. As required, furthermore, a stabilizer rod 26 is provided at an upper portion of the outer die 22 in a manner of passing through the air ring 25 and a windbreak cylinder 27. The stabilizer rod 26 is constituted by a metal shaft and a pipe-like member loosely fitted to the shaft. The metal shaft is coupled by screws to an end of the mandrel. The metal shaft rotates following the rotation of the second screw 21. However, the pipe-like member is loosely fitted to the shaft and, hence, the parison 30 is not twisted though it is linearly extruded in contact with the outer surface of the pipe-like member. Preferred materials for the pipe-like members includes fluorine-containing polymers such as polytetrafluoroethylene. The molten resin extruded from the extruder 1 of the apparatus for producing the inflation film is received by the second screw 21 of the screw die 20. The rotating speed of the second screw 21 has been so set that a pressure of the extruder 1 indicated by a pressure gauge 11 of Fig. 1 lies within a predetermined range. The molten parison extruded from the screw die 20 is taken up at a speed faster than the speed of extrusion. Then, the parison is inflated at a predetermined inflation ratio with a gas released from the end of the stabilizer rod through the gas passage to thereby obtain an inflation film. The third invention of the present application is concerned with a homogeneous inflation film obtained by the above-mentioned method and apparatus, and having nearly a uniform tensile strength in both the machine direction and the transverse direction, having excellent impact strength without fluctuation in the thickness over the whole film surfaces. The inflation film of the present invention comprises an ultra-high-molecular-weight polyolefin having an intrinsic viscosity [η] of not smaller than 7 dl/g and, preferably, from 8 to 25 dl/g and a thickness of from 10 to 1000 pm. The inflation film has a tensile strength at break of greater than 1660 kg/cm 2 and, preferably, greater than 2000 kg/cm 2 in the machine direction, and greater than 1600 kg/cm 2 and, preferably, greater than 1700 kg/cm 2 in the transverse direction, an impact strength of greater than 9500 kg·cm/cm and, particularly, greater than 9700 kg·cm/cm, and an R-value of not larger than 10 µ m. A typical inflation film comprises an ultra-high-molecular-weight polyolefin having a tensile strength at break of greater than 1660 kg/cm 2 , preferably, greater than 2000 kg/cm 2 and, more preferably, greater than 2400 kg/cm 2 in a machine direction (MD) and greater than 1600 kg/cm 2 and, preferably, greater than 1700 kg/cm 2 in a transverse direction (TD), an impact strength of greater than 9500 kg·cm/cm and, preferably, greater than 9700 kg·cm/cm, a thickness of from 10 to 1000 µ m, an R-value of not larger than 10 µ m and an intrinsic viscosity [η] of at least 7 dl/g, said inflation film being obtained by melting the ultra-high-molecular-weight polyolefin in an extruder, extruding the molten ultra-high-molecular-weight polyolefin from a screw die having an L/D of at least 5 and having a mandrel which rotates independently of the screw of the extruder, and blowing a gas into the molten tubular film formed by the extrusion to accomplish both an inflation ratio and a drawing ratio in the machine direction which are not smaller than 7. Here, the machine direction (MD) stands for a direction in which the film is taken up, and the transverse direction (TD) stands for a direction at right angles thereto. The R-value is an index of the uniformity of the film thickness and indicates a difference between a maximum thickness and a minimum thickness measured at 32 points at regular intervals in a transverse direction of the inflation film. The unevenness of thickness in the MD direction of the inflation film is generally a considerably lower value than the R value. The film is formed as suppressing a drop in the molecular weight during the molding and exhibits highly strong properties of the ultra-high-molecular-weight polyolefin. Besides the inflation film which is a molded product has a difference between a maximum thickness and a minimum thickness of not larger than 10 µ m, and is substantially free of fluctuation in the thickness. In this respect, the inflation film of the present invention is radically distinguished over the conventional ultra-high-molecular-weight polyolefin films. The ultra-high-molecular-weight polyolefin inflation film obtained by the present invention can be used as lining materials such as of silos, hoppers, chutes, etc., separators for electrolytic cells and non-aqueous electrolytic cells such as alkali cells, lithium ion cells, lead storage batteries, nickel-hydrogen cells and nickel-cadmium cells, contraction films for covering rolls, pipes and steel pipes, packaging films for packaging foods, packages, containers, and sporting goods such as helmets, sailboards, gliding surfaces of skis, etc. Concretely speaking, furthermore, the ultra-high-molecular-weight polyolefin inflation film of the present invention can be used as sliding tapes, thrust washers, gliding sheets, guides, doctor knives, cassette tape liners, slit sheet for cassette tapes, bags withstanding very low temperatures, heat-shrinking films, bags for preservation at low temperatures, tapes for packaging, starting material for obtaining highly strong drawn yarns, films for capacitors, insulating films, polyolefin-coated rubber rolls, packages for goods, packages for blood, split yarns, ropes for climbing, woven fabrics, nonwoven fabrics, drawn tapes, filters for preventing blood platelets from freezing, sail cloths, explosion-preventing sheets, protection cloths against cutting, safety gloves, overlapped cloths, electric cables, tension members, vibration board of speakers, armor plates, radar dome, synthetic papers, printing papers for outdoor exhibits, envelopes for air mail, packaging materials for water-absorbing agents or oxygen-absorbing agent, air-permeable packages, pasteurized and sterilized packaging materials, base fabric for medical treatment, packaging material for medical instruments, sealing/package for water-adjusted articles, separator films, filtering material for filters, carrier of filters, agricultural film such as mulch-film, green film, electret film, construction material such as house wrapping, etc. (EXAMPLES) The invention will now be described by way of Examples. (Example 1) An ultra-high-molecular-weight polyethylene inflation film was prepared by using an apparatus shown in Fig. 1 having the following specifications. Specifications of the apparatus. Outer diameter of first screw of extruder 50 mm Effective length of screw 1210 mm (L/D=22) Flight pitch 30 mm constant Compression ratio of screw 1.8 Effective length of screw die erected on the extruder 1075 mm (L/D=30) Inner diameter of outer tube die at die outlet 36 mm Outer diameter of mandrel at die outlet 30 mm S1/S2 1.16 S2/S3 3.07 Outer diameter of second screw of screw die 50 mm Effective length of second screw 160 mm (L/D=3.2) Flight pitch 30 mm constant Compression ratio of second screw 1.0 Outer diameter of stabilizer rod 26 mm Length of stabilizer rod 400 mm The apparatus is equipped with a gas passage of a diameter of 8 mm extending in the second screw, in the mandrel and in the stabilizer shaft, and with a stabilizer plate, a pinch roll and a product take-up device. Production of an inflation film. An ultra-high-molecular-weight polyethylene inflation film having a folding width of 510 mm and a thickness of 25 µ m was stably produced by using a powder of an ultra-high-molecular-weight polyethylene having [η] of 14.0 dl/g, an MFR of not larger than 0.01 g/10 min., a melting point of 136°C and a bulk density of 0.47 g/cm 3 , setting the extruder, a joint portion (J), a die base (D1) and a die end (D2) shown in Fig. 1 at temperatures of 280°C, 230°C, 200°C and 170°C, respectively, rotating the first screw at 15 rpm and the second screw at 5 rpm, blowing the compressed air from the gas passage of a diameter of 8 mm extending in the second screw, in the mandrels and in the stabilizer rod while taking up the parison by the pinch roll at a speed of 5 m/min so that the parison is inflated about 9 times as great as the inner diameter (36 mm) of the outer tube die. (Example 2) An ultra-high-molecular-weight polyethylene inflation film was produced under the conditions of Example 1 but setting the specifications of the apparatus as follows: Outer diameter of second screw 60 mm Effective length of second screw 190 mm (L/D=3.2) Flight pitch 36 mm Inner diameter of outer tube die at die outlet 40 mm Outer diameter of mandrel at die outlet 30 mm Effective length of die 1075 mm (L/D=27) S1/S2 1.8 S2/S3 2.0 and setting the take-up speed to be 1.1 m/min, inflation ratio to be 8.0, folding width to be 503 mm, and thickness to be 100 µ m. (Example 3) An ultra-high-molecular-weight polyethylene inflation film was produced under the conditions of Example 1 but setting the specifications of the apparatus as follows: Rotating speed of first screw 7.5 rpm Rotating speed of second screw 2.5 rpm Take-up speed 3.3 m/min Inflation ratio 10.0 Folding width 565 mm Thickness 15 µm (Example 4) An ultra-high-molecular-weight polyethylene inflation film was produced under the conditions of Example 3 but setting the specifications of the apparatus as follows: Take-up speed 1.72 mm/min Inflation ratio 8.0 Folding width 452 mm Thickness 40 µm (Example 5) A film of a thickness of 25 µ m was stably produced under the conditions of Example 1 but setting the specifications of the apparatus as follows: Effective length of screw die erected on the extruder 250 mm (L/D=7) Rotating speed of first screw 5 rpm Rotating speed of second screw 1.5 rpm Speed of pinch roll 1.74 m/min (Example 6) A film of a thickness of 25 µ m was stably produced under the conditions of Example 1 but using a powder of an ultra-high-molecular-weight polyethylene having [η] of 8.1 dl/g, an MFR of 0.01 g/10 min, a melting point of 136°C and a bulk density of 0.45 g/cm 3 and by setting the temperature of the extruder at 240°C. (Comparative Example 1), It was attempted to form a film of a thickness of 25 µ m under the conditions of Example 5 but setting the effective length of the screw die erected on the extruder to be 150 (L/D = 4.2). However, flight marks of the second screw did not disappear, the parison could not be favorably drawn, and no film could be obtained. (Comparative Example 2) It was attempted to form a film of a thickness of 25 µ m under the conditions of Example 1 but setting the inner diameter of the outer tube die to be 46 mm, S1/S2 to be 1.16, and S2/S3 to be 1.0. However, flight marks of the second screw did not disappear, the parison could not be favorably drawn, and no film could be obtained. (Comparative Example 3) It was attempted to form a film of a thickness of 25 µ m under the conditions of Example 1 by using a commercially available polyethylene having [η] of 3.2 dl/g, an MFR of 0.03 g/10 min and a density of 0.950 g/cm 3 . However, the melt viscosity of the resin was so low that the parison rotated being drawn by the rotation of the mandrel and was twisted, making it difficult to stably form the film. Properties of the above-mentioned films were evaluated in accordance with the methods described below. The results were as shown in Table 1. (1) The tensile strength (MD: machine direction) and the tensile strength (TD: direction intersecting the machine direction) were those values (TS: kg/cm 2 ) obtained under the following conditions: Tensile strength testing method and shape of testing piece JIS K 6781 Distance between the chucks 86 mm Pulling speed 200 mm/min Temperature 23°C (2) The impact strengths were the values (kg·cm/cm) of breaking strength obtained under the following conditions: Measuring instrument Film impact tester manufactured by Toyo Seiki Co. Capacity 30 kg·cm Impact ball surface one inch in diameter (3) The thickness ( µ m) of the film was measured under the following conditions: Measuring instrument Thickness measuring instrument, "Digi-Thickness Tester" manufactured by Toyo Seiki Co., detecting ability, 1 µm (detecting precision, 2 µm) Measuring method The film was measured at 32 points at regular intervals in the circumferential direction (TD), an average value thereof was regarded to be a thickness, and a difference between a maximum thickness and a minimum thickness was regarded to be an R-value. Standard JIS Z 1702 Pushing rod 5 mm in diameter Load 125 g Measuring pressure 0.637 kg/cm 2 Temperature 23°C

Claims: A method of producing an inflation film of an ultra-high-molecular-weight polyolefin comprising the steps of: melting the ultra-high-molecular-weight polyolefin in an extruder equipped with a first screw; extruding the molten ultra-high-molecular-weight polyolefin from a screw die having an L/D of at least 5 and having a second screw and a mandrel coupled to the end portion of the second screw, said second screw being allowed to rotate independently of said first screw of the extruder; and inflating the molten film in the form of a tube by blowing a gas into the film to form an inflation film. A method according to claim 1, wherein the rotating speeds of the first screw of the extruder and of the second screw of the screw die are variable independently of each other, and the rotating speed of the second screw is set to be lower than that of the first screw. A method according to claim 1, wherein the ultra-high-molecular-weight polyolefin has an intrinsic viscosity [η] of not smaller than 5 dl/g. A method according to any one of claims 1 to 3, wherein the ultra-high-molecular-weight polyolefin is an ultra-high-molecular-weight polyethylene. An apparatus for producing an inflation film comprising an extruder provided with a first screw, and a screw die having an L/D of at least 5, wherein said screw die comprises a second screw which rotates independently of said first screw, a mandrel coupled to the top end of the second screw and rotates together with the second screw, an outer tube die in which the mandrel is inserted, and a passage extending inside the second screw and the mandrel for introducing gas, wherein said screw die is coupled to the extruder at the bottom portion of the second screw. An apparatus according to claim 5, wherein a stabilizer rod is connected to the top end of the mandrel. An inflation film comprising an ultra-high-molecular-weight polyolefin having an intrinsic viscosity [η] of at least 7 dl/g, said inflation film having a tensile strength at break of greater than 1660 kg/cm 2 in a machine direction and greater than 1600 kg/cm 2 in a transverse direction, an impact strength of greater than 9500 kg.cm/cm, and an R-value, which is an index of uniformity of the film thickness defined by a difference between a maximum thickness and a minimum thickness measured at 32 points at regular intervals in a transverse direction of the film, of not larger than 10 µ m, wherein the inflation film is obtainable by melting an ultra-high-molecular-weight polyolefin in an extruder having a screw, extruding the molten ultra-high-molecular-weight polyolefin from a screw die having an L/D of at least 5 and having a mandrel with a screw which rotates independently of, and at a speed different from the speed, the screw of the extruder, and inflating the molten film in the form of a tube by blowing gas into the film to obtain an inflated and drawn film having both an inflation ratio and a drawing ratio which are not smaller than 7. An inflation film according to claim 7, wherein the ultra-high-molecular-weight polyolefin is an ultra-high-molecular-weight polyethylene.

Inventors: SHIRAKI TAKESHI, SUZUKI IWATOSHI, SHIRAKI, TAKESHI, SUZUKI, IWATOSHI, Shiraki, Takeshi, c/o Mitsui Petrochem. Ind., Ltd., Suzuki, Iwatoshi, c/o Mitsui Petrochem. Ind., Ltd.
Applicants: MITSUI CHEMICALS INC, MITSUI CHEMICALS, INC.
Application year: 1996
Main classification: B29C47
IPC codes: B29C47, B29C55, C08F110, B29K23, B29L7