Thermoplastic compositions comprising starch and other components from natural origin

Abstract: Biodegradable thermoplastic compositions comprising a starch component, a cellulose ester or ether, a plasticizer for the starchy phase and of the cellulose and derivatives, and a compatibilizer agent selected from polymers compatible with the cellulose and or starchy component, grafted with aliphatic or polyhydroxilated chains; copolymers obtained from hydroxy acids and/or diamines with 2 -24C and aliphatic or aromatic diisocyanates; copolymers obtained from aliphatic polyesters, polyureas and polyalkylene glycols and aliphatic or aromatic diisocyanates; copolymers obtained from polymers compatible with cellulose ester or ethers and/or the starchy component by grafting starch soluble polyols; polymer capable of complexing starch; starch compatible polyols.

Description: The present invention relates to biodegradable thermoplastic composition suitable, in particular for preparing injection moulded articles free from surface defects, comprising a starchy component an a cellulose ester or ether. Biodegradable composition obtained starting from starch and a thermoplastic polymer are well known in the art and available from the market and are disclosed, e. g., in European patent applications EPA 32 802, 327 505, 400 532, 404 723, 404 727, 404 728, and in W090/0671, W071/02025, USP5 095 054. Typically, such compositions can be obtained by blending starch and a synthetic thermoplastic polymer, under extrusion cooking conditions, i.e. in the presence of limited amounts of water (generally 0.5-40% by weight based on starch-water system) or of a plasticiser, by operating under temperature and pressure conditions sufficient to destroy the starch crystallinity and to obtain a thermoplastic molten mass (destructured starch). From European patent application EPA 575 349, biodegradable compositions are known which comprise a starch component and a cellulose ester. The injection moulded articles obtained starting from said compositions are affected from the drawback of displaying unpleasant surface scale due to the poor compatibility between starch and cellulose esters. European patent application EPA 542 155 discloses compositions based on starch and cellulose esters added with a compatibiliser agent (epoxidised soy bean oil and acetylated starch), in order to confer improved mechanical properties to the moulded articles. The moulded articles from the above compositions undergo considerable delamination phenomena due to the insufficient compatibilisation between starch and the cellulose ester. US-5 288 318 discloses compositions comprising starch and cellulose acetate, wherein at least 3% of starch is present as intact starch granules, and wherein plasticizers for only the starch phase or for both the starch and the cellulose acetate phases are indifferently used. From EP-A-0 409 781, compositions are known comprising destructured starch, a cellulose ether or ester substantially compatible with starch and a thermoplastic water-insoluble polymer, wherein the cellulose derivative acts as compatibilising agent between the starch and the water-insoluble polymer. The compositions comprise a very limited amount of plasticizer which is selected, indifferently among the plasticizers suitable for the starch phase or for both the starch and the cellulose phases. We have found now that it is possible to improve the mutual compatibility of starch or starch esters or ethers and cellulose esters or ethers and to obtain moulded articles free from scales unevenness, by using selected classes of compatibilising agents. Beside endowing the resulting compositions with better homogeneity, the use of the compatibilising agents of the invention improves the biodegradability characteristics of the compositions. The compositions according to the present invention comprise: starch or a starch ester or ether with a substitution degree from about 1.2 to 2.5; a cellulose ester or ether with a substitution degree from about 1.2 to 2.5; a plasticizer for the starchy phase and a plasticizer for the cellulose derivatives phase or a plasticizer for both phases; a compatibilizing agent selected from the following classes: (A) polymers compatible with cellulose esters or ethers and/or starch or starch esters and ethers, grafted with aliphatic or polyhydroxylated chains containing from 4 to 40 carbon atoms; (B) copolymers obtained from hydroxy acids and/or diamines with 2-24 carbon atoms and aliphatic or aromatic diisocyanates or epoxy compounds and anhydrides; copolymers obtained from aliphatic polyesters, polyamides or polyureas and aliphatic or aromatic diisocyanates; copolymers obtained from aliphatic or aromatic diisocyanates and polyalkylene glycols; (C) copolymers obtained from polymers'compatible with cellulose esters or ethers and/or starch or starch esters or ethers, by grafting starch soluble polyols or structures capable of complexing starch. (D) polymers capable of complexing starch such as ethylene - vinyl alcohol or ethylene acrylic acid copolymers, aliphatic polyesters or polyamides. (E) starch compatible polyols selected from the monomers and the low molecular weight polyols (MW lower than 10.000) such as glycerol, sorbitol,erythritol, polyglycerol, dextrins, polyvinylalcohol, and the above polyols grafted with alkylene oxides or polyalkyleneoxides. The compatibilizer agents indicated under (A) are obtained by grafting aliphatic chains with 4-40 carbon atoms optionally containing up to three unsaturations and or heteroatoms or still other functional groups, to polymers compatible with cellulose esters or cellulose ethers. Preferably, the chains derive from animal or vegetable fats, such as oleic, lauric, myristic, palmitic, stearic, euric, linoleic, ricinoleic acids or phospholipids with terminal end groups which allow the chains to be grafted to the polymers compatible with cellulose esters or ethers. The terminal group can be carboxy, ester, or salt groups; the chains can also be modified in order to obtain terminal groups such as alcohol, aldehyde, amine, amide, acid chloride, isocyanate, mercaptan epoxy and anhydride groups. The polymers to which the above said lipidic chains are grafted can display different degrees of affinity with cellulose derivatives and starch esters or ether; some of them can even be miscible with said cellulose derivatives and starch ester or ethers; others, with a lower compatibility degree, can anyway result to be interesting because they can be easily transformed into compatible derivatives. Such polymers can be of either natural or synthetic origin. Furthermore, they can be used as such, or modified or depolymerized to trimer level by hydrolysis, saponification, cracking o by means of enzymatic reactions. Examples of the above polymers are: (a) cellulose esters with various DS (Degree of Substitution); (b) cellulose ethers with various DS; (c) cellulose ethers/esters with various DS values; (d) starch ester with various DS values, as acetates; (e) starch ethers with various DS values, such as the reaction products of starch with ethylene or propylene glycols; (f) starch ethers/esters with various DS values; (g) partially hydrolysed polyvinyl acetate; (h) aliphatic polyesters and copolyesters, optionally also grafted with those products as listed under (a) - (g) above. In this case, polymers are preferred which are obtained by grafting low molecular weight(350-1000) polycaprolactone (PCL) to polyvinyl alcohol copolymer or, also, by grafting PCL to regenerated cellulose or starch; (i) aliphatic/aromatic or aromatic copolyesters optionally grafted with above (a)-(g) products; (j) polymers from natural origin such as cellulose, hemicellulose, lignin, cellulose ethers and xanthates, regenerated cellulose, pullulan, chitin, chitosan,pectins, proteins, vegetable and animal gelatines, zein, gluten, casein, albumen, natural or modified rubbers, alginates, rosin derivatives. The aliphatic chains can be grafted by means of any known type of reaction, and generally by: (1) transesterification of ester group; (2) esterification of hydroxy groups; (3) urethanizing hydroxy groups by means of isocyanates; (4) epoxidizing hydroxy groups with aliphatic epoxides; (5) acetalization of hydroxy groups with aliphatic aldehydes. The compatible polymers with the cellulose derivatives and starch esters or ethers can be grafted for example with the following polyols soluble in starch or capable of complexing starch: modified amylose and its hydrolysis product; polyvinyl alcohol with various hydrolysis degrees, ethylene-vinyl alcohol copolymers, polyols of glycerol, polyglycerol, saccharides, oligosaccharides, trimethylol propane, pentaerythritol. The number of grafted chains are comprised within the range of from 0.1 to 30 grafted chains per each 100 monomeric units in the polymer chain, preferably from 0.2 to 20, and still more preferably, from 0.3 to 10. grafted chains for each 100 monomeric units. Besides the compatibilizers of above (A) type which require that polymeric products are modified by grafting lipidic chains, also copolymers of above (B) type can be advantageously used, particularly those obtained from such aliphatic polyesters such as polycaprolactone with various molecular weight and polyethylene succinates, from alipathic or aromatic diisocyanates or copolymers obtained from C 2 -C 24 hydroxy acids, or aliphatic or aromatic diisocyanates, or copolymers of above (C) type. For the preparation of copolymers of above (B) type, preferred diisocyanates are: 4,4'-diphenylmethane diisocyanate, hydrogenated 4,4'-diphenylmethane diisocyanate, toluidene diisocyanate, isoforone or hexamethylene-diisocyanate. Estane (a caprolactone:urethane copolymer traded by Goodrich as "54351 grade") is a representative copolymer of (B) class. The compositions comprise the starchy component and the cellulose derivatives in ratios bt weight comprised within the range from 1:90 to 90:1, preferably from 1:40 to 40:1 and still more preferably of 1.5:5 to 1:1.5. The compatibilizer agents are present in amounts comprised from 0.1 to 20% by weight, preferably of from 0.5 to 10% The plasticiser for cellulose phase and the starchy phase are present in amounts respectively comprised from 5 to 40%, and still more preferably,of from 10 to 30%, by weight. Compounds which act as plasticizers for both phases, such as, diacetins, can be used. The total amount of plasticizer is generally comprised from 5 to 40% based on total weight of the composition, preferably from 10 to 30%. Besides the components indicated above, the composition can also contain synthetic polymers in amount up to about 30% by weight, preferably less than 10%. Examples of synthetic polymers which can be used are polyvinylalcohol, polyvinyl acetate, thermoplastic polyesters, such as polycaprolactone, copolymers of caporolactone with isocyanates, lactic acid polymers, polyethylene or polybutylene adipate or sebacate. The starch which can be used to prepare the compositions according to the present invention generally is a native starch, extracted from various plants, such as maize, potato wheat, tapioca and cereal starch. Under the term "starch" are also included high amylopectin starches ("waxy" starches), high-amylose starches, chemically and physically modified starches e.g., starches the acid number of which is reduced down to a value comprised within the range from 3 to 6; starches in which the type and concentration of cations associated with phosphate groups are modified, starch ethoxylated,starch acetates, cationic starches, hydrolysed starches, oxidized and crosslinked starches. Representative cellulose esters comprise cellulose acetates, propionates and/or butyrates, with various degrees of substitution. Cellulose acetate with degree of substitution comprised from 1,5 to 2.5 are preferred. Example of cellulose and starch ethers are ethyl or propyl ethers. Cellulose esters or ethers in neat form, mainly the acetate esters, have so high processing temperature as to cause the matrix to undergo severe degradation. They require the use of a plasticizer which can be selected from: glycerol esters with alipathic acids containing up to 6 carbon atoms, in particular diacetin and triacetin; esters of citric acid , in particular trimethyl or tryethyl citrate, as well as acetyl-triethyl-citrate; diakyl esters or tartaric acid; esters of alipathic acids, lactones and lactides; dialkyl esters of aliphatic acids such as those derived from oxalic, glutaric, adipic, sebaceic, suberic, azelaic acids, mainly dibutyl adipate and dibutyl sebacate; dialkyl esters of aromatic acids in which the alkyl group contains from 1 to 10 carbon atoms, in particular dimethyl phthalate, diethyl phthalate, methoxy and ethoxy ethyl phthalate; polyethylene glycol adipate, glutarate or sebacate; alkyl and aryl phosphates, in particular triethyl and tricresyl phosphates; alkyl ester or fatty acids, such as butyl oleate; polymeric plasticizers as the product traded as Paraplex by Rohm and Haas; Admex 719 from Arche Daniels Midland; the Flexol series from Union Carbide; non-bleeding plasticizers as : mixed aliphatic-aromatic esters of trimethlyol propane and pentaerythritol; alkyl phosphate terminated polyethylene glycols. In order to obtain the thermoplastic character of the starchy phase, in particular at low humidity contents, polar substances are added, which are capable of forming hydrogen bonds with amylose and amylopectin. Suitable substances for that purpose are polyols with 1-20 repeating hydroxylated units, each containing from 2 to 6 carbon atoms; ethers, thioethers, organic and inorganic esters, acetates and amino derivatives of the above polyols; the reaction products of the polyols with chain extenders; polyol oxidation products containing at least one aldeydic or carboxy group. Plasticizers of this type are disclosed in WO 92/19680 application, the disclosure of which is incorporated herein by reference. Preferred plasticizers are those which act as plasticizers for both the starchy and the cellulosic phase and the acetins belong to this preferred class. The starchy phase is normally plasticised directly during the compounding step, in mixture with all the other components. However, also a two step process can be used in which the starchy phase and the cellulosic phase are individually plasticized and/or the starchy phase is plasticized prior to the final compounding step. Preferred plasticizer comprise: water glycerol, glycerol ethoxylate, ethylene or propylene glycol, polyethylene glycol polypropyleneglycol, 1,2- propanediol, 1-3 propanediol, 1-2, 1,3-, 1,4- butanediol, 1,5- pentanediol, 1,6-, 1,5-hexanediol, 1, 2, 6, 1,3,5,-hexanetriol, neopentylglycol, sorbitol acetate, sorbitol diacetate, sorbitol monoethoxylate, sorbitol diethoxylate, trimethol propane monoethoxylate, mannitol monoacetate, mannitol monoethoxylate, butyl glucoside, glucose monoethoxylate, sodium salt of carboxymethylsorbitol, polyglycerol monoethoxilate. The preparation of the composition according to the present invention comprises blending the components in a heated extruder or in any device which may secure temperature shear stress conditions sufficient to cause the conversion of the starchy material and the cellulose derivatives into a thermoplastic state and to render the components compatible with each other as regard their rheology, operating at a temperature comprised within the range of from 80 to 210° C in the presence of water and a plasticizer. The preferred method for preparing the compositions comprises: a first step consisting in conveying the components through an extruder with residence times of the order of from 2 to 50 seconds, during which the starchy components and cellulose derivatives are caused to undergo swelling due to the action of the plasticizer and optionally added water, by operating at a temperature comprised within the range from 80 to 180°C; a blending step during which the mixture from the preceding step is submitted to shear stress conditions which correspond to similar viscosity values of the cellulose derivatives and the starchy components; optionally a step of venting under controlled pressure conditions or in vacuo in order to obtain a molten mass preferably at a temperature comprised within the range from 130 to 180° C with a water content preferably smaller than 6% such as not to have bubbles formation at atmospheric pressure, e.g., at the extruder outlet, if producing foamed products is not desired. This condition is satisfied when it is desired to obtain not foamable products. In the case of foamable products, the water content in the blend may be as high as 20%, preferably up to 18%. The resulting molten mass can be then directly extruded into pellets from which articles are then fabricated by means of the conventional processes. The following examples are supplied in order to illustrate the invention without limiting it. EXAMPLES Examples 1-8 are comparison examples; examples 9-22 are according to the invention. (A) Blending The compositions were prepared by using a twin-screw APV extruder Mod. 2030 of 30mm of diameter, with L:D = 25. The temperature profile of the 16 temperature controlled zones was as follows: 60°C × 1 - 100°C × 1 - 180°C × 14 The screw revolution speed was 120 rpm. (B) Injection moulding The pellets obtained form the extruder were fed to a Sandretto injection press Series 60 in order to obtain dumbbell-shaped specimens. The test results are reported in following table 1 LEGEND 1) Aceplast LS is a cellulose acetate with substitution degree 2.5, traded by Società acetati S.p.A. of Verbania, Italy. 2) CAB is a cellulose acetate/butyrate traded by Eastman chemicals under their trademark CAB 831-20. 3) The composition of both MAT-1 and MAT-2 products, obtained according to as reported in EP-A-0 400532 is as follows: MAT-1 MAT-2 Starch 39 36 EAA-20 3 -- EVOH 36 22 PVOH -- 22 Glycerol 16.7 15.2 Urea 5 4.5 Armid-E 0.3 0.3 4) Acetylated starch with DS=1.3 is manufactured by national Starch and is referred to as "78-0403 GDS-1233". Acetylated starch with DS=2 is a laboratory sample obtained in pyridine with acetic anhydride. 5) The compatibilizer agents reported in the Table were obtained from starch acetate (SAc) with SD 1.3 and 2.1 and cellulose acetate (CAc) with SD 2.1 The substitution percent rate is indicated as a suffix to the designation of the grafted acyl radical; it is expressed as the number of the resulting grafted radicals per each 100 monomeric units of substrate. The fatty acid grafting reaction was carried out using lauric and oleic acid chlorides in dimethyl acetamide. After neutralisation with pyridine, the compatibilizer agents deriving from starch acetate and cellulose acetate were precipitated with ethyl ether and water respectively. 6) Estane is a caprolactone/urethane copolymer traded by Goodrich as grade 54351. 7) AC/EVOH is a copolymer of cellulose acetate grafted with 10% of a copolymer of ethylene with vinyl alcohol. Cellulose acetate with SD of 2.9 is plastified in a monoscrew extruder OMC with 20mm diameter, with 27% by weight of triacetin. The extruder was operated at 195° and 140 rpm. The pellets were added with 1.3 w% of examethylendiamine disocyanate and extruded again at 170° C and 140 rpm. The pellets thus obtained were added with 10w% of EVOH A4412 of Nippon Goshei and extruded at 180°C and 6 rpm. Footnotes to table 1 (A): the material was tested for biodegradability (see data reported in table 2; (b): the dumbbell specimen, obtained by injection moulding operating according to above "B" condition, undergoes severe delamination; (c): the dumbbell specimen, obtained by injection moulding according to above "B" operating condition, tends to delaminate; (d) : the morphology of the surface of the dumbbell specimen appears to be homogeneous, with no scales apparent (see photographs). Biodegradability of the compositions disclosed in the Examples The biodegradability of the materials was tested by recording the weight loss of specimens enclosed inside polypropylene nets (with 1mm mesh) embedded inside a substrate of an aged composite with 55% of moisture and heated at 50% inside an incubator. A plurality of specimen, i.e., one specimen each net, are charged, so as to able to follow the course of degradation over time. Per each specimen, 50 g of composite is used. The initial weight of the specimen does not exceed 1 g. After every week, one net is recovered, which is first washed with water and then with ultrasounds at 20°C and 55% RH, and is finally weighed. Surface morphology of dumbbell specimens The inspection of the dumbbell specimens for their surface morphology was carried out by optical microscopy (Wild Macroscope M-420) and SEM electronic microscopy (Stereoscan 260 ex Cambridge Instruments). The optical microphotographs are in reflected light, with 45 x magnification. For SEM microphotographs, the magnification rate is reported on the images. As one will observe from the picture, the addition of the compatibilizer according to the present invention causes a sharp increase in dumbbell specimen surface quality (in the most meaningful cases, the microphotographs obtained from both techniques are reported). Following pictures No 1 and 2 relate to Example 20 and 21 respectively.

Claims: Biodegradable thermoplastic composition comprising starch or a starch ester or ether, a cellulose ester or ether, a plasticizer for the starchy phase, a plasticizer for the cellulose ester or ether phase, or a plasticizer for both phases, and a polymeric compatibilizing agent for the starchy phase and the cellulose ester or ether phase containing copolymers obtained from polymers compatible with cellulose esters or ethers and/or starch or starch esters and ether, by grafting starch soluble polyols or polymers capable of complexing starch selected from ethylene-vinyl alcohol or ethylene acrylic acid copolymers, aliphatic polyesters or polyamides. Compositions according to claim 1, in which the ratio of starchy component to cellulose derivative, is comprised within the range from 1: 90 or to 90:1 by weight, and the compatibilizer agent is used in amounts from 1 to 20% by weight based on the total amount of starchy components and the cellulose derivatives. Biodegradable thermoplastic composition comprising starch or a starch ester or ether, a cellulose ester or ether, a plasticizer for the starchy phase, a plasticizer for the cellulose ester or ether phase, or a plasticizer for both phases, and a polymeric compatibilizing agent for the starchy phase and the cellulose ester or ether phase, in which the compatibilizing agent is selected from polymers or copolymers compatible with starch or starch esters or ethers and/or cellulose esters or ehers grafted with aliphatic chains containing 4 to 40 carbon atoms, in which the grafting degree is comprised within the range from 0.1 to 30 grafted aliphatic chains per each 100 monomeric units in the polymer chain. Compositions according to claim 3, in which the grafted chains present in the compatibilizer derive from animal or vegetable fats. Compositions according to claim 4, in which the grafted chains derive from oleic,lauric, myristic, palmitic, stearic, erucic, linoleic or ricinoleic acid. Biodegradable thermoplastic compositions comprising starch or a starch ester or ether, a cellulose ester or ether, a plasticizer for the starchy phase, a plasticizer for the cellulose ester or ether phase or a plasticizer for both phases and polymeric compatibilising agents, wherein the compatibiliser agent is a copolymer obtained from an aliphatic polyester, a polyamide, a polyurea or a polyalkylene glycol and from an aliphatic or aromatic diisocyanate, and wherein the ratio of the starchy component to the cellulose derivative is comprised with the range from 1:90 to 90:1 by wt. and the compatibilising agent is used in amounts from 1 to 20% by wt. based on the total amount of the starchy components and the cellulose derivatives. Biodegradable thermoplastic compositions comprising starch or a starch ester or ether, a cellulose ester or ether, a plasticizer for the starchy phase, a plasticizer for the cellulose ester or ether phase or a plasticizer for both phases and polymeric compatibilising agents, wherein the compatibilising agent is a copolymer obtained from an aliphatic or aromatic diisocyanate or an epoxy compounds or an anhydride and from a hydroxy acid or a diamine with 2 to 24 carbon atoms, and wherein the ratio of the starch component to the cellulose derivative is comprised within the range from 1:90 to 90:1 by wt. and the compatibilising agent is used in amounts from 1 to 20% based on the total amount of the starchy components and the cellulose derivatives. Compositions according to claims 6 or 7, wherein the diisocyanate is selected from 4, 4'-diphenylmethane diisocyanate, toluidene diisocyanate and hexamethylene diisocyanate. Biodegradable thermoplastic compositions comprising starch or a starch ester or ether, a cellulose ester or ether, a plasticizer for the starchy phase, a plasticizer for the cellulose ester or ether phase or a plasticizer for both phases and polymeric compatibilising agents, wherein the cellulose ester or ether is cellulose acetate, the compatibilising agent is a polymer capable of complexing starch selected from aliphatic polyester, polyamides, copolymers of ethylene with vinylalcohol and copolymers of ethylene with acrylic acid and the plasticizer for the starchy phase and the plasticizer for the cellulose phase or the plasticizer for both phases is used in a total amount from 10 to 30% by wt., and wherein the ratio of the starch component to the cellulose derivative is comprised within the range from 1:90 to 90:1 by wt. and the compatibilising agent is used in amounts from 1 to 20% by wt. based on the total amount of the starchy components and the cellulose derivatives. Biodegradable thermoplastic compositions comprising starch or a starch ester or ether, a cellulose ester or ether, a plasticizer for the starchy phase, a plasticizer for the cellulose ester or ether phase or a plasticizer for both phases and polymeric compatibilising agents, wherein the compatibilising agent is a polymeric polyol with a molecular weight lower than 10,000 or a polyalkylene oxide grafted with said polyols, and wherein the ratio of the starch component to the cellulose derivatives is comprised within the range from 1:90 to 90:1 by wt., the compatibilising agent is used in amounts from 1 to 20% by wt. based on the total amount of the starch components and the cellulose derivative, the compositions being obtainable from a melt comprising the starchy phase and the cellulose ester or ether phase. Compositions according to claims 1 or 2, in which the compatibilizer is a copolymer obtained by grafting a polyol selected from polyvinyl alcohol, ethylene-vinyl alcohol copolymers, glycerol, polyglycerol, saccharides, trimethylol propane, pentaethritol. Compositions according to any of claims 1 to 8 and 10-11, in which the cellulose ester is cellulose acetate with a substitution degree from 1.2 to 2.5. Compositions according to any of claims 1 to 8 and 10 - 12, in which the plasticizer or plasticizers are present in total amount comprised within from 5 to 40% by weight, on the total composition weight. Compositions according to any of claims 1 to 13 in which the plasticiser for the starchy phase and cellulose ester or ether phase is diacetin.

Inventors: BASTIOLI CATIA, BELLOTTI VITTORIO, LOMBI ROBERTO, PEREGO GABRIELE, BASTIOLI, CATIA, BELLOTTI, VITTORIO, LOMBI, ROBERTO, PEREGO, GABRIELE
Applicants: NOVAMONT SPA, NOVAMONT S.P.A.
Application year: 1996
Main classification: C08L1
IPC codes: C08L1, C08K5, C08L3, C08L101