A TRANSFER FOR DECORATING TEXTILES WITH COLOURED PATTERNS

Abstract: A transfer capable of applying one- or multi-coloured patterns to textiles under heat and pressure comprises a carrier sheet (1) having a non-binding surface which carries (a) a one- or multi-coloured pattern (5) printed on the carrier sheet using a digitally controlled colour printer; (b) a transparent (6) or white-pigmented (7) elastomer layer of a polymer having a high plasticizing point printed configuratively on the pattern (5); and (c) a heat-activatable thermoplastic polymeric glue layer (8) printed configuratively on the transparent (6) or white-pigmented (7) elastomer layer or a heat-activatable hot melt granulate sprinkled on the elastomer layer while said layer was still wet. An even better encapsulation of the coloured pattern is obtained when the carrier sheet has printed thereon a first transparent elastomer layer of a polymer having a high plasticizing point, and the pattern is printed on this elastomer layer using a digitally controlled colour printer. Additional strength is obtained when both a transparent elastomer layer and a white-pigmented elastomer layer are printed on top of the coloured pattern.

Description: A transfer for decorating textiles with coloured patterns The invention relates to a heat application transfer for decorating textiles with coloured patterns having a par- ticularly high washing and cleaning fastness, wherein the design is produced by means of a digitally controlled colour printer. BACKGROUND OF THE INVENTION The most common way of making transfers for the applica¬ tion on textiles is by means of silk screen printing where each individual colour is applied to a sheet of silicone paper. Some colours, such as vinyl and plastisol colours, are heat-activatable, but are then not very fast without further treatment. To improve the fastness, the colours are usually provided with a hot melt granulate layer in the form of a powder or a fme-gramed granulate mixed m an extender base, which is applied to the col- ours and serves as a special glue layer between textile and colours, thereby considerably improving the fastness. At high temperatures, however, e.g. during tumbling proc¬ esses which use temperatures up to 140 "C in certain cases, they will get loose from the textile or a possible glue layer. Solvent-based two-component colours will be more stable against the action of temperature, but, when having been subjected to industrial washing and tumbling for an extended period of time, they will dry out and peel off from the textile. The international patent application WO 92/07990 dis¬ closes a possible use of a colour copier with a two- component colour toner system m the making of a transfer for textiles. Such a two-component colour toner system, however, is not known in the market for colour copiers today. The present laser colour copiers use colour toners of a one-component thermoplastic resm type where no po¬ lymerization takes place. Furthermore, the svstem de¬ scribed in the above-mentioned international application depends on a colourless two-component extender base layer which is applied on top of the coloured image and, imme¬ diately when wet, is coated with a thermoplastic granu¬ late which serves as a glue layer. This embodiment, how¬ ever, can only be applied to white textiles, and the transferred image will only be sharp on very smooth ιex- tiles. It is prior art to use colour copiers for the transfer of images to a thermoplastics-coated transfer paper F roιτ which it can be transferred by heat and pressure to white cotton textiles. The known products, however, exhibit great washing and cleaning weaknesses and thus ust stand washing at about 40 C for a limited number of times. The reason is primarily that the colour toners are relatively unprotected against mechanical impacts, and that they re- main heat-activatable already at temperatures from about 90 °C. Further, printing is only possible on white ^ex- tiles, and only on textiles where the predominant part consists of cotton. If it is desired to transfer coLour images of this type to dark textiles, up to several addi- tional operations are reguired for the lamination and ad¬ aptation of a white cover layer below the colour toners. This process is both expensive and time-consuming, and it is moreover not possible to make configurative patterns, but only complete cover faces . OBJECT OF THE INVENTION A number of data-controlled colour printers of various types are available which reproduce four-coloured raster images with a resolution of 400 dpi or more with an al¬ most photographic appearance. It is not possible an a pure silk screen printing process to achieve a resolution of more than 100 dpi, and consequently fine details are lost in the reproduction. Accordingly, it would be a great advantage to be able to use such colour printers for the making of coloured and particularly multi¬ coloured configurative transfers for the textile indus ¬ try. Of course, it would also be an advantage to be able to use data programs for the editing of images and de¬ signs together with scanners which transfer original lm- ages to data. The object of the invention is to make a coloured con- figurative transfer for the textile industry which com¬ bines the great advantages achieved by the use of an electronic colour printer as the graphic unit with par¬ ticularly great washing and cleaning fastness. SUMMARY OF THE INVENTION Since colour images generated from ordinary printers to a transfer substrate cannot readily be transferred to a textile m a configurative pattern, this is achieved ac¬ cording to the invention by using silk screen printing processes for making a protective layer and/or cover layer as well as a glue layer m accordance with the in¬ vention. In its most simple embodiment the transfer of the inven¬ tion is unique in that it comprises a carrier sheet hav- mg a non-b dmg surface which carries (a) a one- or multi-coloured pattern printed on the car¬ rier sheet using a digitally controlled colour printer; (b) a transparent or white-pig ented elastomer layer of a polymer having a high plasticizing point printed configuratively on the pattern; and (c) a heat-activatable thermoplastic polymeric glue layer printed configuratively on the transparent or white-pigmented elastomer layer, or a heat- activatable hot melt granulate sprinkled on the elastomer layer while this was still wet. It has surprisingly been found according to the invention that the colour toners which are usually used multi¬ colour copiers and which may e.g. be based on thermoplas- tic polyol resins, migrate into the surface of the ap¬ plied transparent or white-pigmented elastomer Layer and harden together with said layer under the action of the isocyanate hardener contained in the elastomer layer. The colour toners hereby lose their thermoplastic nature and remain adhered to the elastomer layer, so that the col¬ oured pattern or the image, after the transfer has been applied to a textile, stands washing, also at ele¬ vated temperatures. If it is desired to encapsulate the coloured pattern or image so that it will be additionally resistant to wear and to the action of washing and cleaning, it may be pro¬ vided with an additional protective layer . In this em¬ bodiment the transfer of the invention is unique that it comprises a carrier sheet having a non-bindmg surface which carries (a) a first transparent elastomer layer of a polymer having a high plasticizing point printed configara- tively on the carrier sheet; (b) a one- or multi-coloured pattern printed on the first elastomer layer using a diqitally controlled colour printer; (c) a second transparent or white-pigmented elastomer layer of a polymer having a high plasticizing point printed configuratively on the pattern; and (d) a heat-activatable thermoplastic polymeric glue layer printed configuratively on the transparent or white-pigmented elastomer layer, or a heat- activatable hot melt granulate sprinkled on the elastomer layer while this was still wet. Further, if the transfer is intended to be applied to very coarse or uneven textiles, and if it is desired to maintain fine details in the coloured pattern or image, the transfer may be provided with both a white-pigmented and a transparent elastomer layer (c) ; m this case the very strongest encapsulation of the coloured pattern or image is achieved when first a transparent elastomer layer and then a white-pigmented elastomer layer are ap- plied. In the latter embodiment the transfer of the invention is unique m that it comprises a carrier sheet having a non- bmdmg surface which carries (a) a first transparent elastomer layer of a polymer having a high plasticizing point printed configura¬ tively on the carrier sheet; (b) a one- or multi-coloured pattern printed on the elastomer layer using a digitally controlled colour printer; (c) a second transparent elastomer layer of a polymer having a high plasticizing point printed configura¬ tively on the pattern; (d) a white-pigmented elastomer layer of a polymer hav- g a high plasticizing point printed configura¬ tively on the second transparent elastomer layer; and (e) a heat-activatable thermoplastic polymeric glue layer printed configuratively on the whi te-pigmented elastomer layer, or a heat-activatable hot melt granulate sprinkled on the elastomer layer wnile this was still wet. The carrier sheet having a non-binding surface may e.g. consist of paper or a heat-resα stant plastics sheet, e.g. of polyester, coated with a thin layer of silicone or polyolefin; or it may e.g. consist of a polyolefin sheet, expediently a sheet of high density (HD) polypropylene. The transparent elastomer Layers may advantageously con¬ sist of an elastomeric polyurethane having a high plastα- cizing point applied m the form of a solution in an or¬ ganic solvent. This is particularly advantageous in con¬ nection with the use of colour copiers of the dry elec- trostatic type which normally apply a thin silicone oil to the surface of the fixing rollers to prevent toner particles from sticking to the rollers. Small amounts of this silicone oil are applied to the colour toners the printing and can be detrimental to the adhesion of the subsequent elastomer layer. But the organic solvent m the polyurethane layer dissolves the silicone film so that the polyurethane and the toners combine to form a homogeneous unit. However, with other types of colour printers, or if other steps are taken to avoid the silicone film, it is also possible to use corresponding polyurethanes in aqueous solution. The white elastomer layer, which may optionally be emit¬ ted if the transfer is to be used for applymg a pattern to white textiles, may advantageously consist of the same type of polyurethane as above, pigmented with a white in¬ organic pigment and applied from an organic or aqueous solution. The final glue layer may advantageously consist of polyu ¬ rethane thermoplastics having a plasticizing pomt in the range 120-160 L C containing dispersed fine particles of a hot melt of copolya ide or high density polyethylene type having a melting point of 100-140 °C m the ratio 1:1, applied m the form of an organic or aqueous solution of the polyurethane with dispersed hot melt powder. A special variation of the glue layer comprises lammat- mg a thermoplastic moulded polyurethane sheet on the transparent or white elastomer layer. A 100 μm thicL transparent or coloured aromatic polyester film having a plasticizing point of about 160 C C, a hardness o 93 Shore and an elasticity of 400 is particularly useful for the purpose. The silk screen printed polyurethane layers and the polyurethane sheet can be laminated to¬ gether at 160 'C under slight pressure, so that the sheet does not melt, but only adheres to the applied layer. During application of the finished transfer to a textile, which takes place at 200 C C and 320 kPa in 12 seconds, the polyurethane sheet melts and forms a very stronq glue layer between the textile and printed image. In an advantageous embodiment of the invention, the transparent elastomer layers, the white elastomer layer and the glue layer are printed on the carrier sheet by silk screen printing processes in the same register and configuration on top of one another. Owing to possible inaccuracies in the register, however, the glue layer normally protrudes 1-2 mm beyond the configuration of the other layers in practice. As stated, the one- or multi-coloured pattern is printed on the first elastomer layer using a digitally controlled colour printer. The invention is very flexible wiLh re¬ spect to the selection of colour printer. A rough dis- tinction may be made between diqitally controlled coloui printers which work with powder toners, liquid dyes or colour ribbons. Accordingly, the coloured pattern in a transfer of the mvention will normally be printed on the first transpar¬ ent elastomer layer by means of a dry electrostatic col¬ our toner printer, an ink jet printer with liquid dyp or a thermotransfer colour printer, all of whicLi are digi- tally controlled. The invention also comprises a method of making a trans¬ fer as described above, said method being unique by, on a carrier sheet having a non-b dmg surface, (a) printing a one- or multi-coloured pattern using a digitally controlled colour printer; (b) on top of the pattern, configuratively printing a transparent or white-pigmented elastomer layer of a polymer having a high plasticizing point; and (c) on top of the transparent or white-pigmented elas¬ tomer layer, printing a heat-activatable thermoplas¬ tic polymeric glue layer, or, while the elastomer layer is still wet, sprinkling a heat-activatable hot melt granulate on said layer. Another embodiment of the method of the invention is unique by, on a carrier shet (1) having a non-binging surface, (a) configuratively printing a first transparent elas- to er layer (4) of a polymer having a high plasticiz¬ ing point; (b) on top of the first elastomer layer (4) , printing a one- or multi-coloured pattern (5) using a digitally controlled colour printer; (c) on top of the pattern (5) , configuratively printing a second transparent (6) or white-pigmented (7) el as- tomer layer of a polymer having a high plasticizing point; and (d) on top of the transparent (6) or white-pigmented (7) elastomer layer, configuratively printing a heat- activatable thermoplastic polymeric glue layer (8), or, while the elastomer layer is still wet, sprin ¬ kling a heat-activatable hot melt granulate on said layer. Another embodiment of the method of the mvention is unique by, on a carrier sheet having a non-bmding sur ¬ face, (a) configuratively printing a first transparent elas ¬ tomer layer of a polymer having a high plasticizing point; (b) on top of the first elastomer layer, printing a one- or multi-coloured pattern using a digitally con ¬ trolled colour printer; (c) on top of the pattern, configuratively printing a second transparent elastomer layer of a polymer hav ¬ ing a high plasticizing point; (d) on top of the second elastomer layer, configuratively printing a white-pigmented elastomer layer of a poly¬ mer having a high plasticizing point; and (e) on top of the white-pigmented elastomer layer, con¬ figuratively printing a heat-activatable thermoplas¬ tic polymeric glue layer, or, while the elastomer layer is still wet, sprinkling a heat-activatable hot melt granulate on said layer. In accordance with the disclosure above, the transparent elastomer layers are advantageously applied the form of an organic solution of an elastomer polyurethane hav¬ mg a high plasticizing point; but it may also take place in the form of an aqueous solution. The white elastomer layer may then be applied in the form of a correspondmg organic or aqueous polyurethane solu¬ tion which is pigmented with a white pigment. Furthermore, the glue layer may advantageously be applied in the form of an organic or aqueous solution of polyαre- thane thermoplastics having a plasticizing pomt in the range 120-160 U C, m which a fine hot melt powder of co- polyamide or high density polyethylene type having a melting point of 100-140 "C is dispersed in the ratio 1:1. In an advantageous embodiment of the method of the inven¬ tion, the transparent elastomer layers, the white eLas- tomer layer and the glue layer are printed on the carrier sheet by silk screen printing processes m the same reg¬ ister and configuration on top of one another. But, as mentioned before, owing to possible inaccuracies the register, the glue layer will normally be printed in a configuration which protrudes 1-2 mm beyond the configu¬ ration of the other layers. Furthermore, the coloured pattern is generally printed on the first transparent elastomer layer by means of a dry electrostatic colour toner printer, an ink et printer with liquid dye or a thermotransfer colour printer, all of which are digitally controlled. According to the invention, if the transfer is to be used for applymg a pattern to white textiles, it is possible to omit the white elastomer layer and to print the glue layer directly on the second transparent elastomer layer. According to the invention, if the transfer is to be used for applying a pattern to textiles having a very even and non-textured surface, it is also possible to om t the second transparent elastomer layer and to print the white elastomer layer directly on the one- or multi-coloured pattern. Finally, according to the invention, it is also possible to omit the glue layer and, where application to white textiles is involved, optionally also the wh te elastomer layer, m which case the surface of the white elastomer layer and the second transparent elastomer layer, respec- tively, are modified to be heat-activatable. Ihis is done most expediently according to the invention m that imme¬ diately after the printing of the elastomer layer, while this is still wet, a fine hot melt powder of copolyamidc or high density polyethylene type having a melting point of 100-140 C is sprinkled on the surface. The invention also comprises textile products on which a one- or multi-coloured pattern is attached by application from a transfer of the invention. The method and the transfer of the mvention g ve evident cost-saving advantages particularly m case of a low num¬ ber of printed copies. DETAILED DESCRIPTION OF THE INVENTION The invention will be illustrated more fully by the fol¬ lowing detailed description of various embodiments of it with reference to the drawing, which schematically shows the structure of a transfer of the invention. The drawing shows a carrier sheet (1) composed of a sheet of paper or a heat-resistant plastics sheet (2) coated with a thin release layer of silicone or polyolefin (3) . A first transparent elastomer layer (4) is configura¬ tively printed by silk screen printing on the silicone or polyolefin surface, and, on top of said elastomer layer, a one- or multi-coloured pattern (5) is printed with a digitally controlled colour printer. On top of the col¬ oured pattern, a second transparent elastomer layer (6) is configuratively printed, agam by silk screen print¬ ing, and, in the same manner, a white-pigmented elastomer layer is printed on said second elastomer layer. Upper¬ most, a heat-activatable thermoplastic polymeric glue layer (8) is printed in the same manner. A thin transparent elastomer layer (4), e.g. an organic solution of an elastomeric polyurethane having a high plasticizing point, is applied by silk screen printing with a 34T blanket in a desired configuration on a car- rier sheet (1) having a non-binding surface, e.g. of pa¬ per or heat-resistant plastics sheet ( 2 ) coated with silicone or polyolefin (3) or entirely of polyolefin, e.g. HD polypropylene. This first elastomer layer (4) is then dried an frared/hot air drying tunnel at about 70-80 D C. The desired pattern (5) is now printed in mirror-mverted fashion on the carrier sheet (1) with applied elastomer layer (4) with the elastomer-coated area by means of a colour printer, e.g. a four-colour copier of the "Ricoh NC5006" type, which works with a dual powder toner system and a resolution of 400 dpi. After the print has been fixed in the heat section of the machine, th^ toners, which consist of thermoplastics, are still heat- activatable even at relatively low temperatures (about 90 °C) . To stabilize the toners so that they can later stand higher temperatures, a second transparent elastomer layer (6) is printed on top of the colour toners, e.g. of the same polyurethane solution as the elastomer layer (4) . The solvent of the polyurethane layer neutralizes the silicone film, which is applied to th^ toners during the heat fixation in the colour copier, and the pol y- mer/isocyanate mixture combines with the toners to form a homogeneous unit which hardens at room temperature by means of the atmospheric humidity. A well protected col- our layer has now been provided between two polyurethane layers which are not heat-activatable at the application temperature of the transfer. Since the covering power of the toners is none too good on others than white textiles, a white-pigmented elas¬ tomer layer (7), e.g. of a polyurethane with the same chemical composition as the preceding transparent layers and in the same configuration as the other layers, is now applied. A heat-activatable granulate of a polyamide- based hot melt, which serves as a glue layer between the transfer and the substrate, may now be applied to the elastomer layer (7) while it is still wet, or a heat- activatable thermoplastic polymeric glue layer (8), e.g. consisting of heat-activatable polyurethane thermoplas- tics mixed with a fine hot melt powder of copolyamide in the ratio 1:1, is applied to the white cover layer (7) . The transfer may now be applied to all ordinary textiles in the usual manner at 170-180 °C in 8-12 seconds and a pressure of about 310 kPa. With respect to useful colour printers, a rough distinc¬ tion may be made between digitally controlled colour- printers working with powder toners, liquid dyes or col- our ribbons. Examples of colour copiers using powder ton¬ ers in a dry electrostatic process, include: "Canon® CLC 700", "Ricoh® NC 5006", and "Rank Xerox® 5775". Examples of digitally controlled colour printers using liquid dyes include: "Indigo Eprmt 1000", "IBM Color Jetpnnter PS 4079" and "Canon® BJC-880". Finally, examples of digi¬ tally controlled so-called ther otransfer colour printers working with colour ribbons include: "ABDICK", "Seiko® ColorPomt 2 PSF-14" and "Fargo Pictura 310". Each system has its cost/quality parameters between which one may choose freely. The elastomer layers encapsulating the colour layer may be adapted to the various printers e.g. by means of surface-active additives or electronic surface treatment. This applies to both water-based and solvent-based polymers. If, however, liquid dyes are used, waterproof dyes will always be preferred. Modern digitally controlled colour printers are compati¬ ble with a number of standard software editing programs, e.g. Windows 3.X, IBM OS/2, Apple System 6 and 7 as well as the more advanced Adobe Postscript Level 2. Preferred polymers having a high plasticizing point for making the elastomer layers (4) , (6) and (7) are elas ¬ tomeric polyurethanes, such as a one-component fully re- acted linear polyurethane on the basis of polyester and aliphatic diisocyanate or a one-component fully reacted polyurethane on the basis of polyester and aromatic di¬ isocyanate. The thermoplastic polymer for use in the glue layer (8) is preferably a corresponding polyurethane ad- justed to have a lower plasticizing point and thus to be heat-activatable together with the hot melt powder. Examples of other useful elastomer systems include two- component polyurethane textile colours e.g. "Bargoscreen S18/50" from the company Aaberg or "Maraflor T'K" froir the company Marabu. These colour systems consist of 1- methoxy-2-propyl acetate and 3-methoxy-n-buty acetate to which polyurethane binders are added. Diisocyanate is used as a binder. The recommended diluents for these sys- terns - cyclohexanone or ethyl glycol acetate - are rela¬ tively aggressive against the toners thp image layer and must therefore be added m as small amounts as possi ¬ ble, while the carrier sheet should be treated carefully without greater mechanical impacts until the elastomer layer on the toners has dried. It should be stressed that, addition to said polyure¬ thane components, a large number of other thermoplastic resms may also be used, such as e.g. polyolefins, ethyl¬ ene vinyl acetate copolymers, ethylene ethyl acrylate co- polymers, ethylene acrylic acid copolymers, lonomers, polyesters, polyamides, acrylic resms, etc. When using elastomer systems which are water-dispersed and therefore do not contain solvents, washing may give rise to separation problems between the toner layer and the subsequently applied transparent layer. The reason is that colour copiers of the dry electrostatic type nor¬ mally use a thin silicone oil on the surface of the fix¬ ing rollers which prevents toner particles from sticking to the rollers. It is mevitaole that small amounts of silicone oil are left on the surface of the colour toners and cause separation or formation of air pockets between the toner layer and the subsequently applied polyurethane layer, particularly during washing. If it is desired to use a water-based colour/lacquer system, the problem may be solved by using infrared heat fixing of the toners alone, or ceramic fixing rollers, or other rollers whicti do not require silicone oil. Preferred method of preparation: As will appear from the drawing, several successive poly¬ mer and image layers, which form the finished transfer, are printed individually on a carrier sheet (1) normally consistmg of a sheet of paper of about 105 g/m (2) coated with a release layer of silicone (3) . First a transparent elastomer layer (4) is printed, pref¬ erably consisting of a polyurethane having the highest possible melting point, which following transfer to the substrate forms a protective top layer. Particularly use¬ ful was a 2 solution in propylene glycol methyl ether of a linear fully reacted polyurethane on the basis of polyester and aliphatic diisocyanate having a plasticiz¬ ing point of 195-205 "C. Then the desired image (5) is printed m a dry electro¬ static colour copier. A particularly suitable colour cop¬ ier is a "Ricoh NC5006" which produces colour copies with a resolution of 400 dpi with 256 shades per pomt. In other colour copiers, the copying paper runs about a drum, and this restricts the selection of copying materi¬ als. NC5006 therefore uses a transfer belt for transfer¬ ring the original image to the copying sheet. The straight paper movement allows copying on different types of paper and transparencies. A transparent elastomer layer (6) is now printed, said layer combining with the toners and consisting of the same composition as the first elastomer layer (4) . The toners are now well protected between the two elastomer layers. Then, a white cover layer (7) is printed, con¬ sisting of the same polyurethane type as the first and second transparent elastomer layers, but pigmented with organic or inorganic colour pigments, e.g. titanium dLOX- ide. Finally, a glue layer (8) connecting the transfer (3) with the textile is printed. The glue layer consists of a mixture of a polyurethane which is a more softly adjusted one-component polyurethane having a melting point of 150- 160 °C, and a hot melt powder on copolyamide basis in the ratio 1:1. The melting point of the hot melt powder is about 115-130 C, and the gram size is not above 80 μm. A particularly suitable hot melt powder has been found to be a copolyamide on the basis of polymerized, predorm - nantly dimeπzed fatty acids or their esters and substan ¬ tially aliphatic diammes. These hot melts possess great resistance to washing and cleaning agents, even at high temperatures (80-90 C) . The one-component polyurethane glue primarily serves as a filler for the powdered hot melt, but also serves per se as thermoplastics. For example, a 35 c solution in dime ¬ thyl formam de/toluene/methyl ethyl ketone of a one- component polyurethane glue on the basis of polyester and aromatic diisocyanate having a plasticizing point of 150- 160 C is particularly useful for the purpose. The glue layer serves as a purely reversible thermoplas ¬ tic, i.e. no hardening or cross-linking takes place the application of the transfer to the textile by means of heat and pressure. Under the action of heat and pres¬ sure in the application to the textile, both the hot melt and the one-component poyurethane melt and are pressed down between the textile fibres and thereby anchor the transfer mechanically. EXAMPLE 1 A four-coloured pattern or image (5) of a two-component toner having a particle size of 6.4 μm was applied di¬ rectly to the non-bmd g surface of a carrier sheet (1) a Ricoh NC 5006 colour copier. Subsequently, a hifp- pigmented two-component polyurethane elastomer sheet (7) was applied on top of the toner image by silk screen printing. The two-component elastomer used was "Bargoscreen S18/50" polyurethane textile colour from Aa- berg Druckfarben, Aaberg, Switzerland, admixed with 10 polydnsocyanate hardener. It is essential to the dura¬ bility of the transfer that the toner res has an ex¬ tremely good contact with the white two-romponent polyuethane elastomer, so that common polymerization of the two materials takes place. As the heat fixing unit in the copier uses dimethyl polysiioxane silicone oil as a release agent on the heat rollers, small amounts of it will be transferred to the surface of the toner layer and thereby reduce the surface tension. It was therefore nec¬ essary to add a small amount of a wetting agent to the white-pigmented polyurethane elastomer to increase its wetting capacity, and 0.5 C < wetting agent of the brand "BYK 358" from BYK-Chemie GmbH, Wessel, Germany was added. The carrier sheet was fed through a tunnel drying oven in 105 "C hot air to dry the white layer before fur ¬ ther processing. Then a transparent two-component polyu¬ rethane layer from the same series, "Bargoscreen S18/50", as the white layer was applied by silk screen printing, and while it was still wet, a layer of hot melt co- polyamide granulate of the brand "Kiwomelt 2095 F" from Kissel & Wolf GmbH, Wiesloch, Germany, was added, forming the glue layer. The finished transfer was applied tn a cotton/polyester textile at 165 "C at a pressure of 310 kPa in 10 seconds. This type of transfer is very versa¬ tile and is suitable for most types of textiles. EXAMPLE 2 A transparent elastomer layer (4) of a linear one- component polyurethane on the basis of polyester and ali¬ phatic diisocyanate was applied in a desired configura¬ tion by silk screen printing with a 34T blanket on a car¬ rier sheet (1) consisting of a 105 g/m sheet of paper (2), coated with a release layer of silicone (3) . Then the carrier sheet with the applied elastomer layer was introduced mto a Ricoh colour copier of the type NC5006, and a four-coloured pattern (5) of a two-component toner having a particle size of 6.4 μm was transferred withm the area of the elastomer layer (4) . A transparent elas- tomer layer (6) on the basis of the said one-component polyester urethane with the same configuration as the first elastomer layer was printed on top of the toner layer. Further, a titanium dioxide-pigmented white polyu¬ rethane layer (7) of the same structure as the preceding layers was printed. Finally, a glue layer (8) was printed, consisting of a mixture of a 35, solution in di¬ methyl formamide/toluene/methyl ethyl ketone of a one- component polyurethane glue on the basis of polyester and aromatic diisocyanate having a plasticizing point of ISO- 160 C and a non-dissolved hot melt powder based on co- polyamide . In this example, the individual elastomer lay¬ ers were adjusted relatively softly, viz. with an ulti¬ mate/tensile strength of about 700-800" . Between the printing of the individual layers, elastomer layer, white cover layer and glue layer, these are dried in a hot air/infrared drying oven at 70-80 D C, and the transfer is then dry, while the final hardening is completed only af¬ ter about 10 hours at room temperature or 3-4 hours in a heating cabinet at 60 °C. The finished transfer was transferred to a cotton/polyester textile at 180 'C and a pressure of 310 kPa in 10 seconds. This type of transfer is particularly suitable for textured elastic textiles. EXAMPLE 3 Like m the preceding example, an elastomer layer (4) , a toner ayer (5), an elastomer layer (6), a white cover layer (7) and finally a glue layer (8) were printed suc¬ cessively on a carrier sheet (1) m the described manner. Th s time a polyurethane with a somewhat harder setting was used, viz. with an ultimate/tensile strength of 100- 200 . The powdered hot melt was also the same as men¬ tioned above. The transfer is applied to the textile the same manner as in example 1. Such a setting is suit¬ able particularly for non-elastic woven textiles for work clothes . Conclusively, the described transfer material, accorαing to the field of use, may be adapted for various textiles, as the various elastomer layers may have a soft or a hard setting and thereby affect the elasticity and the resis¬ tance to temperatures and mechanical conditions. Of course, it is possible to modify and vary the proαuct of the invention withm the scope of the invention. Thus, e.g. a silicone-coated plastics sheet may be used instead of paper as a carrier sheet. Further, it is also possiDle to omit the white cover layer if the transfer is just used on white textiles and to apply a transparent elas¬ tomer layer on the colour toner layer and then the qlue layer. Moreover, while the white cover layer (7) or the last transparent elastomer layer (6) is still wet, it may also be decided to apply to said layer a layer of hot melt powder which is fused mto the elastomer in an n¬ frared/hot air drying oven. This method saves a printing operation, but the transfer has a somewhat harder appear¬ ance on the textile. Finally, the white cover layer may be printed directly on the toners, thereby allowing the one elastomer layer to be omitted. However, this varia¬ tion can be used only where a textile havmg a very even non-textured surface is involved, since, otherwise, the white elastomer will pull the toners apart durmg the ap¬ plication and thereby create a more blurred image.

Claims: PATENT CLAIMS 1. A transfer capable of applying one- or multi-coloured patterns to textiles under heat and pressure, character- ized m that it comprises a carrier sheet (1) having a non-b dmg surface which carries (a) a one-or multi-coloured pattern (5) printed on the carrier sheet using a digitally controlled colour printer; (b) a transparent (6) or white-pigmented (7) elastomer layer of a polymer having a high plasticizing point printed configuratively on the pattern (5) ; and (c) a heat-activatable thermoplastic polymeric glue layer (8) printed configuratively on the transparent (6) or white-pigmented (7) elastomer layer, or a heat- activatable hot melt granulate sprinkled on the elas¬ tomer layer while this was still wet. 2. A transfer capable of applymg one- or multi-coloured patterns to textiles under heat and pressure, character¬ ized in that it comprises a carrier sheet (1) having a non-bmdmg surface which carries (a) a first transparent elastomer layer (4) of a polymer having a high plasticizing point printed confiqura- tively on the carrier sheet (1) ; (b) a one- or multi-coloured pattern (5) printed on the first elastomer layer (4) using a digitally con¬ trolled colour printer; (c) a second transparent (6) or white-pigmented (7) elas- tomer layer of a polymer having a high plasticizing point printed configuratively on the pattern (5) ; and (d) a heat-act vatable thermoplastic polymeric glue l yer (8) printed configuratively on the transparent (6) or white-pigmented (7) elastomer layer, or a heat- activatable hot melt granulate sprinkled on the elas¬ tomer layer while this was still wet. 3. A transfer capable of applying one- or u.ti-coloured patterns to textiles under heat and pressure, character¬ ized in that it comprises a carrier sheet (1) having a non-bmdmg surface which carries (a) a first transparent elastomer layer (4) of a polymer having a high plastici z ng point printed confiqura- tively on the carrier sheet; (b) a one- or multi-coloured pattern (5) printed on the elastomer layer (4) using a digitally controlled col¬ our printer; (c) a second transparent elastomer layer (6) of a polymer having a high plasticizing point printed configura¬ tively on the pattern (5) ; (d) a white-pigmented elastomer layer (7) of a polymer having a high plasticizing point printed configura¬ tively on the second transparent elastomer layer (6) ; and (e) a heat-activatable thermoplastic polymeric glue layer (8) printed configuratively on the white elastomer layer (7) or a heat-activatable hot melt granulate sprinkled on the elastomer layer while this was still wet . 4. A transfer according to any one of claims 1-3, char¬ acterized in that the carrier sheet (1) consists of paper or a heat-resistant plastis sheet coated with a thin layer of silicone or polyolefin. 5. A transfer according to any one of claims 1-3, char¬ acterized in that the carrier sheet (i) is a polyolefin sheet . 6. A transfer according to claim 5, characterized that the polyolefin sheet consists of high density pcly- propylene . 7. A transfer according to any one of claims 1-6, char¬ acterized in that the transparent elastomer layers (4) and/or (6) consist of an elastomer polyurethane having a high plasticizing point applied in the form of a solution an organic solvent. 8. A transfer according to any one of claims 1-7, char¬ acterized in that the white elastomer layer (7) consists of an elastomer polyurethane having a high plasticizing pomt which is pigmented with a white inorganic pigment, applied in the form of a solution an organic solvent. 9. A transfer according to any one of claims 1-6, char- acterized in that the transparent elastomer layers (4) and/or (6) consist of an elastomer polyurethane having a high plasticizing point applied in the form of an aqueous solution. 10. A transfer according to any one of claims 1-6 and 9, characterized in that the white elastomer layer (7) con¬ sists of an elastomer polyurethane having a high plasti¬ cizing point which is pigmented with a white inorganic pigment, applied in the form of an aqueous solution. 11. A transfer according to any one of claims 1-10, characterized in that the glue layer (8) consists of polyurethane thermoplastics having a plasticizing pomt in the range 120-160 "C containing dispersed fine parti - cles of a hot melt of copolyamide or high density poly¬ ethylene type having a melting point of 100-140 C in the ratio 1:1, applied in the form of a solution of the polyurethane in an organic solvent with dispersed hot melt powder. 12. A transfer according to any one of claims 1-10, char¬ acterized in that the glue layer (8) consists of polyu¬ rethane thermoplastics havmg a plasticizing point in the range 120-160 'C containing dispersed fine particles of a hot melt of copolyamide or high density polyethylene type having a melting point of 100-140 L C in the ratio 1:1, applied the form of an aqueous solution of the pjlyu- rethane with dispersed hot melt powder. 13. A transfer according to any one of claims 1-12, characterized in that the transparent elastomer layers (4) and/or (6) , the white elastomer layer (7) and the glue layer (8) are printed on the carrier sheet (1 ) by silk screen printing processes in the same registei and configuration on top of one another. 14. A transfer according to any one of claims 1-13, characterized in that the coloured pattern (5) is printed on the carrier sheet (1) or the first transparent las- tomer layer (4) by means of a dry electrostatic colour toner printer, an ink et printer with liquid dye or a thermotransfer colour printer, all of which arc digitally controlled. 15. A method of making a transfer capable of applying one- or multi-coloured patterns to textiles under heat and pressure, characterized by, on a carrier sheet (1 having a non-bmdmg surface, (a) printing a one- or multi-coloured pattern (5) using d digitally controlled colour printer; (b) on top of the pattern (5) , configuratively printing a transparent (6) or white-pigmented (7) elastomer layer of a polymer having a high plasticizing point; and (c) on top of the transparent (6) or white-pigmented (7) elastomer layer, configuratively printing heat- activatable thermoplastic polymeric glue layer (8) or, while the elastomer layer is still wet, sprin ¬ kling a heat-activatable hot me t granulate on said layer . 16. A method of making a transfer capable of applymg one- or multi-coloured patterns to textiles under heat and pressure, characterized by, on a carrier sheet (1) having a non-binding surface, (a) configuratively printing a first transparent elas¬ tomer layer (4) of a polymer having a high plasticiz¬ ing point; (b) on top of the first elastomer layer (4) , printing a one- or multi-coloured pattern (5) using a digitally controlled colour printer; (c) on top of the pattern (5) , printing a second trans ¬ parent (6) or white-pigmented (7) elastomer layer of a polymer having a high plasticizing point; and (d) on top of the transparent (6) or white-pigmented (7) elastomer layer, configuratively printing a heat- activatable thermoplastic polymeric glue layer (8) or, while the elastomer layer is still wet, sprin¬ kling a heat-activatable hot melt granulate on said layer . 17. A method of making a transfer capable of applying a one- or multi-coloured pattern to textiles under heat and pressure, characterized by, on a carrier sheet (1) having a non-binding surface, (a) configuratively printing a first transparent elas¬ tomer layer (4) of a polymer having a high plasticiz¬ ing point; (b) on top of the first elastomer layer (4) , printing a one- or multi-coloured pattern (5) using a digitally controlled colour printer; (c) on top of the pattern (5) , configuratively printing a second transparent elastomer layer (6) of a polymer having a high plasticizing point; (d) on top of the second elastomer layer (6) , confiqura- tively printing a white-pigmented elastomer layer (7) of a polymer having a high plasticizing point; and (e) on top of the white-pigmented elastomer Layer (7), configuratively printing a heat-activatab e thermo¬ plastic polymeric glue layer (8) or, while the elas- tomer layer is still wet, sprinkling a heat- activatable hot melt granulate on said layer. 18. A method according to any one of claims 15-17, char¬ acterized by applymg the transparent elastomer layers (4) and/or (6) m the form of an organic solution o i an elastomer polyurethane having a high plasticizing point. 19. A method according to any one of claims 15-18, char¬ acterized by applying the white elastomer layer ( ') the form of an organic solution of an elastomer polyure¬ thane having a high plasticizing point which is pigmented with a white inorganic pigment. 20. A method according to any one of claims 15-17, char- acterized by applymg the transparent elastomer liyers (4) and/or (6) in the form of an aqueous solution of an elastomer polyurethane having a high plasticizing po t. 21. A method accordmg to any one of claims 1 -17 anl 20, characterized by applying the white elastomer laye r (7) m the form of an aqueous solution of an elastomer pjlyu- rethane having a high plasticizing point which is pig¬ mented with a white inorganic pigment. 22. A method according to any one of claims 15-21, char¬ acterized by applying the glue layer (8) in the form of an organic solution of polyurethane thermoplastics having a plasticizing point in the range 120-160 c n which a fine hot melt powder of copolamide or high density poly¬ ethylene type having a melting point of 100-140 C is dispersed m the ratio 1:1. 23. A method according to any one of claims 15-21, char¬ acterized by applying the glue layer (8) in the form of an aqueous solution of polyurethane therπioplastics having a plasticizing point in the range 120-160 C in which a fine hot melt powder of copolyamide or high density poly¬ ethylene type havmg a melting point of 100-140 r is dispersed m the ratio 1:1. 24. A method according to any one of claims 15-23, char¬ acterized by printing the transparent elastomer layers (4) and/or (6), the white elastomer layer (7) and the glue layer (8) on the carrier sheet (1) by silk screen printing processes in the same register and configuration on top of one another. 25. A method according to any one of claims 15-24, char¬ acterized by printing the coloured pattern (5) on the carrier sheet (1) or the first transparent elastomer layer (4) by means of a dry electrostatic colour toner printer, an ink jet printer with liquid dye or a thermo- transfer colour printer, all of which are digitally con¬ trolled. 26. A textile product on which a one- or multi-coloured pattern is attached by application from a transfer ac¬ cording to any one of claims 1-14.

Inventors: FRANKE KELL ERIK, FRANKE, KELL, ERIK
Applicants: FRANKE KELL ERIK, STRAND EILIF, FRANKE, KELL, ERIK, STRAND, EILIF
Application year: 1996
Main classification: D06P7
IPC codes: B32B27, B41M5, B44C1, D06P5, D06P7, D06Q1