Adhesive composition

Abstract: Described is an adhesive composition suitable for a hot melt adhesive or hot melt type pressure-sensitive adhesive, which comprises a block copolymer (a) and a tackifier (b), wherein said block copolymer (a) having at least one polymer block A being a hydrogenated butadiene polymer block having a 1,2-bond content of 20 mole% or smaller and at least one polymer block B substantially having an olefin polymer structure different from the polymer block A and having a glass transition temperature of -20°C or lower and heat of crystalline fusion of 8 cal/g or lower, and containing the polymer block A before hydrogenation in an amount of 3 to 80 wt.%; which is excellent in various properties such as process stability, adhesion, creep resistance, flexibility at low temperature and solvent resistance; and which can be used widely for packing, bookbinding, plywood, woodworking, making shoes, adhesion of textile goods and production of various kinds of adhesive goods such as adhesive tapes and labels.

Description: This invention relates to an adhesive composition suitable for a hot melt adhesive or a hot melt type pressure-sensitive adhesive. The adhesive compositions provided by the present invention are so excellent in various properties such as process stability, adhesion, creep resistance, flexibility at low temperature and solvent resistance that they can be used for a variety of applications of, for example, packing, bookbinding, plywood, woodworking, making shoes, adhesion of textile goods and production of various adhesive goods such as various kinds of adhesive tapes and labels. As an adhesive suitable for various applications, a solvent type adhesive has been used widely. The solvent type adhesive has however the problems of air pollution, danger of a fire, worsening of labor environment or industrial hygiene because it contains an organic solvent as a solvent. So, in recent days, a solvent-free adhesive has come to be used widely as a substitute for the solvent type adhesive. Examples of the solvent-free type adhesive include aqueous adhesives and hot melt adhesives. Of these, the hot melt adhesive has come to be used preferably because it requires no drying time or no drying apparatus, and is excellent in energy saving, working properties and productivity. In addition, a pressure-sensitive adhesive is known as a kind of an adhesive. Adhesive goods in which a layer of such a pressure-sensitive adhesive is applied on a base material such as tape, film or sheet of paper, cloth or plastic are used for wide applications as an adhesive tape, adhesive film or adhesive sheet. In the production of such adhesive goods having a pressure-sensitive adhesive layer, it is the common practice to apply a solution of the pressure-sensitive adhesive in an organic solvent to a base material and then to remove the organic solvent to form the pressure-sensitive adhesive layer on the base material. Thus, pressure-sensitive adhesive has also the problems of air pollution, danger of a fire and worsening of the labor environment or industrial hygiene, involved by the use of an organic solvent. Under such circumstances, a solvent-free pressure-sensitive adhesive has been required from the viewpoints of safety, working properties and energy saving. To meet the above requirement, a hot melt type pressure-sensitive adhesive which can be applied to a base material without an organic solvent has been developed . For the hot melt adhesive and hot melt type pressure-sensitive adhesive, a thermoplastic polymer which can be molten by heating is used as a base polymer. Examples of the base polymer used for the hot melt adhesive include copolymers such as ethylene-vinyl acetate copolymer, ethylene-α-olefin copolymer, polyamide, polyester or a block copolymer comprising the polymer block of an aromatic vinyl compound and the polymer block of a conjugated diene such as styrene-butadiene-styrene block copolymer or styrene-isoprene-styrene block copolymer. Examples of the base polymer used for the hot melt type pressure-sensitive adhesive include ethylene-vinyl acetate copolymer, block copolymer comprsing the polymer block of an aromatic vinyl compound and the polymer block of a conjugated diene, and acrylate-based polymer. Among the above-exemplified base polymers, an ethylene-vinyl acetate copolymer is used widely as a base polymer for a hot melt adhesive or hot melt type pressure-sensitive adhesive because of its toughness, its good adhesion with various base materials such as paper, wood, plastics and metal, its good compatibility with other components (tackifier, wax, softening agent or the like) and its excellent hot melt flowability and thermal stability. However, the ethylene-vinyl acetate copolymer has the problem that, owing to its insufficient flexibility at low temperatures, the product using a hot melt type adhesive employing the ethylene-vinyl acetate copolymer as a base polymer or the adhesive goods having a layer of a hot melt type pressure-sensitive adhesive employing the ethylene-vinyl acetate copolymer as a base polymer are not suited for use at low temperatures. Compared with the ethylene-vinyl acetate copolymer, polyamide or polyester has lower compatibility with other components such as tackifier and, moreover, is inferior in handling properties and adhesion with various base materials. A block copolymer, which is not hydrogenated, comprising the polymer block of an aromatic vinyl compound and the polymer block of a conjugated diene, on the other hand, has been used widely as a base polymer for a hot melt adhesive or hot melt type pressure-sensitive adhesive because of its comparatively good adhesion and tackiness at room temperature. Such a block copolymer is however considerably inferior in heat aging resistance and weatherability because it contains an unsaturated carbon-carbon double bond derived from a conjugated diene in its molecule. A hydrogenated product of the block copolymer comprising the polymer block of an aromatic vinyl compound and the polymer block of a conjugated diene is sometimes used for a hot melt adhesive or hot melt type pressure-sensitive adhesive as a base polymer with improved heat aging resistance and weatherability. Since such a hydrogenated product of the block copolymer cannot be applied to a base material at low temperature because of its high melt viscosity, it is difficult to apply the hydrogenated product to a base material having a low heat deformation temperature such as polyethylene film or unwoven fabric made of polyethylene. In addition, the melt viscosity of the hydrogenated product changes largely with a slight temperature difference, and so it is inferior in process stability and has a considerable limitation in the processing conditions of the adhesive composition comprising the hydrogenated product. An object of the present invention is to provide an adhesive composition suitable for a hot melt adhesive or hot melt type pressure-sensitive adhesive, which composition has excellent flexibility at low temperature, good compatibility with a variety of components used in various hot melt type adhesive compositions, a comparatively low melt viscosity to permit easy coating work at low temperature, small change of the melt viscosity on the difference of temperature, excellent process stability, and excellent adhesion, tack and cohesion. The present inventors have carried out an extensive investigation to find that a block copolymer comprising a specific hydrogenated butadiene polymer block and a specific olefin polymer block has excellent compatibility with a tackifier or other components used in a hot melt adhesive or hot melt type pressure-sensitive adhesive; and that a composition obtained by blending a tackifier with the block copolymer, which is a base polymer, has good flexibility at low temperature, small change of a melt viscosity on the difference of temperature and has therefore excellent process stability so that it is suitable for a hot melt adhesive or hot melt type pressure-sensitive adhesive. According to these findings, the present inventors have accomplished the present invention. The present invention provides an adhesive composition which comprises a block copolymer (a) and a tackifier (b) wherein: (i) the block copolymer (a) has at least one polymer block A comprising a hydrogenated butadiene polymer and at least one polymer block B comprising a polymer substantially having an olefin polymer structure different from the above polymer block A; (ii) the polymer block A in the block copolymer (a) is a hydrogenated butadiene polymer having a 1,2-bond content of 20 mole% or smaller before hydrogenation; (iii) the polymer block B in the block copolymer (a) has a glass transition temperature of -20°C or lower and heat of crystalline fusion of 33.5 J/g (8 cal/g) or or lower; and (iv) in the block copolymer (a), the content of the polymer block A before hydrogenation is 3 to 80 wt.% based on the weight of the block copolymer (a) before hydrogenation. The present invention is described in detail. The term "adhesive" or "adhesive composition" as used hereinafter means an adhesive or adhesive composition including a pressure-sensitive adhesive or a pressure-sensitive adhesive composition, respectively. The term "hot melt adhesive" or "hot melt adhesive composition" as used hereinafter means an adhesive or adhesive composition which is used for the adhesion effected by melting an adhesive or adhesive composition by heating, applying it to an adherend in a molten state and then solidifying it at low temperature. The term "pressure-sensitive adhesive" or "pressure-sensitive adhesive composition" as used hereinafter means an adhesive or adhesive composition which carries out pressure sensitive adhesion with tack. The term "hot melt type pressure-sensitive adhesive" or "hot melt type pressure-sensitive adhesive composition" as used hereinafter means an adhesive or adhesive composition which, upon production of adhesive goods such as adhesive tape or adhesive sheet by applying an adhesive or adhesive composition to a base material such as paper, cloth or plastic film, is capable of forming a layer of the pressure-sensitive adhesive or pressure-sensitive adhesive composition on the base material by applying it to the base material in a hot-melted form. The adhesive composition provided by the present invention comprises a specific block copolymer (a) as a base polymer and a tackifier (b). In the adhesive composition provided by the present invention, the block copolymer (a) has the following features: (i) the block copolymer (a) has at least one polymer block A (hereinafter simply referred to as "block A") comprising a hydrogenated butadiene polymer and at least one polymer block B (hereinafter simply referred to as "block B") comprising a polymer substantially having an olefin polymer structure different from the above block A; (ii) block A in the block copolymer (a) has a 1,2-bond content of 20 mole% or smaller before hydrogenation; (iii) block B in the block copolymer (a) has a glass transition temperature of -20°C or lower and heat of crystalline fusion of 8 cal/g or lower; and (iv) the content of the polymer block A in the block copolymer (a) before hydrogenation is 3 to 80 wt.% based on the weight of the block copolymer (a) before hydrogenation. There are two types for the polymerization of butadiene, that is, 1,4-bond in which four carbon atoms of butadiene are all incorporated in the main chain of the polymer and 1,2-bond in which only two carbon atoms of butadiene are incorporated in the main chain of the polymer and the remaining two carbon atoms become side chains or branched chains. In the adhesive composition of the present invention, it is necessary that block A in the block copolymer (a) has a 1,2-bond content of 20 mole% or smaller before hydrogenation [the above feature (ii)]. When the 1,2-bond content of block A before hydrogenation (hereinafter the block A before hydrogenation is simply referred to as "unhydrogenated block A") exceeds 20 mole%, the tendency of crystallization of the block copolymer (a) is lowered and the resulting adhesive composition has poor cohesion and cannot provide good adhesion. It is preferred that in order to provide an adhesive composition having excellent adhesion, the unhydrogenated block A has a 1,2-bond content of 15 mole% or smaller. With a view to provide an adhesive composition excellent in adhesion and also in heat aging resistance and weatherability, block A has a hydrogenation ratio preferably not lower than 70%, more preferably not lower than 80%. Block B, which is another component of the block copolymer (a), is required to be a polymer block different from block A and substantially having an olefin polymer structure. The term "block B substantially having an olefin polymer structure" as used herein means that block B is formed of a polymer of isobutylene, propylene, ethylene or another α-olefinic compound and/or is substantially formed of a polymer available by hydrogenation of a polymer of a conjugated diene such as isoprene, 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, 1,3-hexadiene or butadiene, which has a structure substantially similar to that of a polymer available by the polymerization of an α-olefin. The block of a hydrogenated butadiene polymer is classified in "a polymer block substantially having an olefin polymer structure". It is, however, structurally necessary that the block copolymer (a) used in the adhesive composition of the present invention has block B comprising a polymer block different from block A, so that the block of a hydrogenated butadiene polymer having a 1,2-bond content of 20 mole% or smaller is not included in block B. Block B is formed of one or more than one compounds selected from the group consisting of the above-described α -olefins and conjugated dienes unless it is the block of a hydrogenated butadiene polymer having a 1,2-bond content of 20 mole% or smaller. Here, when a conjugated diene is employed, it is necessary that the block B has acquired an olefin polymer structure by hydrogenation. When block B is formed of at least two of the above-described compounds, its structure can be any one of random, block and taper. Among them, random structure is preferred. In addition, block B can be formed of a polymer block such as alternating copolymer of ethylene and propylene, random copolymer of ethylene and propylene, random copolymer of ethylene and isobutylene, hydrogenated isoprene polymer or hydrogenated copolymer of isoprene and butadiene. It is preferred to form block B from a hydrogenated isoprene polymer or hydrogenated copolymer of isoprene and butadiene, in view of the adhesion of the resulting adhesive composition. When block B is formed of a conjugated diene such as butadiene or isoprene, it is preferred that the block B has a 1,2-bond and 3,4-bond content of 50 mole% or smaller before hydrogenation, with a view to provide an adhesive composition having good characteristics at low temperature. When block B is formed of a conjugated diene such as butadiene or isoprene, the hydrogenation ratio is preferably 70% or higher, more preferably 80% or higher, with a view to provide an adhesive composition having excellent heat aging resistance and weatherability. Block B can contain a small amount (generally, smaller than 30 wt.%) of a structure different from an olefin polymer structure (for example, a structure in which a conjugated diene has not been hydrogenated, or a structure which is derived from a monomer different from olefinic compound or conjugated diene). In the present invention, it is necessary that the block B in the block copolymer (a) has a glass transition temperature of -20°C or lower and heat of crystalline fusion of 8 cal/g or lower [the above feature (iii)]. When block B has a glass transition temperature higher than -20°C, the elastomeric properties of the block copolymer (a) is lowered and the resulting adhesive composition has poor flexibility at low temperature. When block B has heat of crystalline fusion exceeding 8 cal/g, the block copolymer (a) has poor flexibility at room temperature and poor characteristics at low temperature, and embrittlement occurs in the resulting adhesive composition at low temperature. It is desired, for example, to adjust the content of an alkyl branch or the like in the block B in order to have the glass transition temperature and heat of crystalline fusion of block B fall within the above range. In order to impart the adhesive composition with better flexibility and characteristics at low temperature, it is preferred that the glass transition temperature and heat of crystalline fusion of block B is not higher than -30°C and not higher than 20.9 J/g (5 cal/g), respectively. The term "glass transition temperature of block B" as used herein means the value of the glass transition temperature of block B as measured by DSC (differential scanning calorimetry). Its details will be described later in Examples. The term "heat of crystalline fusion of block B" as used herein means the value of the heat of crystalline fusion of block B as measured also by DSC. Its details will be also described later in Examples. It is necessary that in the adhesive composition of the present invention, the content of the polymer block A in the block copolymer (a) before hydrogenation is 3 to 80 wt.% based on the weight of the block copolymer (a) before hydrogenation [the above feature (iv)]. If the content of the polymer block A before hydrogenation is less than 3 wt.% in the block copolymer (a) before hydrogenation, the resulting adhesive composition has little cohesion and cannot provide good adhesion. When the content of the polymer block A before hydrogenation exceeds 80 wt.% in the block copolymer (a) before hydrogenation, the resulting adhesive composition has poor flexibility and, when used as a pressure-sensitive adhesive, cannot play a function as a pressure-sensitive adhesive due to its low adhesion. It is therefore preferred that the content of the polymer block A before hydrogenation in the block copolymer (a) before hydrogenation falls within a range of from 5 to 70 wt.%. No particular limitation is imposed on the molecular weights of block A and block B in the block copolymer (a) and also the molecular weight of the block copolymer (a). From the viewpoint of providing an adhesive composition having good processability, however, the unhydrogenated block A has a number-average molecular weight preferably of 2,500 to 200,000, more preferably of 3,000 to 50,000; block B has a number-average molecular weight preferably of 3,000 to 300,000, more preferably of 30,000 to 200,000; and the block copolymer (a) has a number-average molecular weight preferably of 10,000 to 1,000,000, more preferably of 20,000 to 300,000. No particular limitation is imposed on the number or bonding form of block A and block B in the block copolymer (a) insofar as the block copolymer (a) has at least one block A and at least one block B. Block A and block B can be bonded linearly or in branched form including radial form. The block copolymer (a) can, for example, have a linear or branched structure represented by the following formulas: A-(B-A)p, B-(A-B)q, (A-B)r, or (A-B)s - X wherein A represents block A; B represents block B; p,q and r each represents an integer of 1 or greater; s represents an integer of 2 or greater and X represents a residue derived from a coupling agent. It should however be understood that the structure of the block copolymer (a) is not limited by the above formulas. Of these, the block copolymer (a) with a linear triblock structure represented by the formula: A-B-A is preferred in view of the cohesion of the resulting adhesive composition. The block copolymer (a) can have a functional group such as carboxyl group, acid anhydride group, hydroxyl group, epoxy group, amino group or halogen atom at terminal end of the molecule and/or in the molecular chain. No particular limitation is imposed on the preparation process of the block copolymer (a). The block copolymer (a) can be prepared by forming an unhydrogenated block copolymer comprising unhydrogenated block A and unhydrogenated block B through anionic polymerization, cationic polymerization, polymerization in the presence of a Ziegler catalyst, single site polymerization, radical polymerization or the like, then subjecting the unhydrogenated block copolymer to hydrogenation in an appropriate manner. For example, the block copolymer (a) can be prepared by (1) forming an unhydrogenated block copolymer comprising unhydrogenated block A and unhydrogenated block B by sequential addition of monomers constituting each blocks for polymerization using, as a polymerization initiator, an alkyl lithium compound having an alkyl group with a number of carbon atoms of 1 to 10 (preferably methyl lithium, ethyl lithium, pentyl lithium or butyl lithium) or forming an unhyrogenated block copolymer comprising unhydrogenated block A and unhydrogenated block B through a coupling method with a coupling agent such as dichloromethane, dibromomethane, dichloroethane, dibromoethane, dibromobenzene or phenyl benzoate; (2) subjecting the unhydrogenated block copolymer obtained in the above step (1) to hydrogenation with a known method, e. g. by reacting with hydrogen under the presence of a hydrogenating catalyst (Raney nickel, heterogeneous catalyst in which a metal such as Pt, Pd, Ru, Rh or Ni are supported on a carrier such as carbon, alumina or kieselguhr, or Ziegler-type catalyst composed of a transition metal and an alkyl aluminum compound or alkyl lithium compound); and then (3) recovering the hydrogenated block copolymer obtained. In the above-described preparation process of the block copolymer (a), the polymerization reaction in the above step (1) is preferably conducted using the polymerization initiator in an amount of 0.01 to 0.2 part by weight per 100 parts by weight of all the monomers in an organic solvent inert to the polymerization initiator (preferably, an aliphatic hydrocarbon or aromatic hydrocarbon with a number of carbon atoms of 6 to 12, such as hexane, heptane, cyclohexane, methylcyclohexane or benzene) at 0°C to 80°C for 0.5 to 50 hours. The hydrogenation reaction described in the above step (2) is conducted at a reaction temperature ranging from ordinary temperature to 250°C for 1 to 100 hours under a hydrogen pressure ranging from normal pressure to 200 kg/cm 2 . The block copolymer (a) obtained can be recovered by adding methanol or the like to the reaction mixture to permit the block copolymer (a) to be coagulated and then drying the block copolymer (a) by heating or under reduced pressure; or can be recovered by pouring the reaction mixture to hot water to remove the solvent azeotropically and then drying the block copolymer (a) as described above. The adhesive composition provided by the present invention contains a tackifier (b) together with the block copolymer (a). The tackifier (b) is used mainly for imparting the adhesive composition with hot tack and, at the same time, lowering its melt viscosity to improve its properties for working such as coating. In the adhesive composition of the present invention, a tackifier conventionally employed either in a hot melt adhesive or hot melt type pressure-sensitive adhesive can be used as the tackifier (b). Examples of the tackifier (b) used in the adhesive composition of the present invention include cumarone-indene resin, phenol resin, p-t-butylphenol-acetylene resin, phenol-formaldehyde resin, terpene-phenol resin, polyterpene resin, xylene-formaldehyde resin, aromatic hydrocarbon resin, aliphatic hydrocarbon resin, oligomer of mono-olefin or di-olefin, hydrogenated terpene resin, hydrogenated aromatic hydrocarbon resin, hydrogenated aliphatic hydrocarbon resin, alicylic saturated hydrocarbon resin, polybutene, a polyhydric alcohol ester of rosin, hydrogenated rosin, and ester of hydrogenated rosin with monoalcohol or polyhydric alcohol. These tackifiers can be used either singly or in combination. Of these, hydrogenated terpene resin, hydrogenated aliphatic hydrocarbon resin, hydrogenated aromatic hydrocarbon resin and alicylic saturated hydrocarbon resin are preferably used as the tackifier (b). In the adhesive composition of the present invention, with a view to provide an adhesive composition having excellent adhesion and tack together with excellent flexibility at low temperature and cohesion, the tackifier (b) is used preferably in an amount of 10 to 2000 parts by weight, more preferably in an amount of 40 to 500 parts by weight, based on 100 parts by weight of the block copolymer (a). The adhesive composition comprising the block copolymer (a) and the tackifier (b) has generally tack at oridinary temperature and therefore can be used sufficiently, as it is, as a hot melt type pressure-sensitive adhesive. In addition, this adhesive composition has excellent adhesion so that it can be used as a hot melt adhesive. When used as a hot melt type pressure-sensitive adhesive, a softening agent which has conventionally been employed in a pressure-sensitive adhesive can be added to this adhesive composition in order to make the tack of the adhesive composition higher and to improve the handling properties of the composition as a pressure-sensitive adhesive. Examples of the softening agent include phthalic acid derivatives such as di-(2-ethylhexyl)phthalate, mineral oil, vegetable oil, lanolin, liquid polybutene and liquid polyacrylate and the like. These softening agents can be used either singly or in combination. Among these, mineral oil is preferably used as a softening agent in the adhesive composition of the present invention. The softening agent is used preferably in an amount of 1000 parts by weight or smaller, more preferably in an amount of 300 parts by weight or smaller, based on 100 parts by weight of the block copolymer (a). Amounts of the softening agent greater than 1000 parts by weight based on 100 parts by weight of the block copolymer (a) cause bleeding of the softening agent, so that the resulting adhesive composition has poor quality for the pressure-sensitive adhesive. Generally, a pressure-sensitive adhesive composition and adhesive goods using a pressure-sensitive adhesive composition such as adhesive tape or adhesive film, are used in various forms and for various applications. They are sometimes required to form temporary adhesion to an adherend and, after use, be peeled off completely; or to form semipermanent adhesion to an adherend without peeling. Upon preparation of the pressure-sensitive adhesive composition of the present invention, it is necessary to adjust the properties of the composition such as adhesion, tack or cohesion to be suitable for its usage or manner in use by selecting the details, kind or blending ratio of each of the block copolymer (a) and tackifier (b) and, kind or blending ratio of other additional components. On the other hand, when the adhesive composition according to the present invention comprising a block copolymer (a) and a tackifier (b) is used as a hot melt adhesive, a wax can be added to the adhesive composition in order to impart the preferred propeties as a hot melt adhesive to the adhesive composition, with lowering or removing adhesion of the adhesive composition at ordinary temperature to make it suitable in handling as a hot melt adhesive; lowering the melt viscosity of the adhesive composition; or adjusting the physical properties of the adhesive composition such as open time, softening temperature, hardness, hot tack or blocking tendency. As a wax, wax which has conventionally been employed for a hot melt adhesive and has a melting point ranging from 40°C to 160°C is preferred. Examples of such a wax include paraffin wax, microcrystalline wax, Fischer-Tropsch wax, polyethylene wax, modified wax and α-olefin wax, each having a melting point of 40°C to 160°C. These waxes can be used either singly or in combination. Of the above-exemplified waxes, paraffin wax is preferred in the adhesive composition of the present invention. The wax is used preferably in an amount of 500 parts by weight or smaller, more preferably in an amount of 300 parts by weight or smaller, based on 100 parts by weight of the block copolymer (a). Amounts of the wax greater than 500 parts by weight based on 100 parts by weight of the block copolymer (a) make the adhesion of the resulting adhesive composition lower. The adhesive composition of the present invention can contain additives such as anti-oxidant or UV absorbent for the improvement of heat resistance or weatherability. The adhesive composition of the present invention can also contain a filler such as calcium carbonate or titanium oxide, or fiber such as glass fiber or organic fiber. Furthermore, the adhesive composition of the present invention can contain another polymer such as unhydrogenated styrene-butadiene block copolymer, hydrogenated styrene-butadiene block copolymer, ethylene-vinyl acetate copolymer or polyolefin. No particular limitation is imposed on the method for preparation of the adhesive composition of the present invention insofar as it is a method which can uniformly mix the block copolymer (a), the tackifier (b) and additional components. These components are subjected to melt mixing by, for example, high-speed mixer, kneader, melting oven, internal mixer or extruder such as monoaxial extruder or biaxial extruder. The adhesive composition of the present invention can be formulated in a suitable form according to its usage or manner in use. It can be prepared, for example, in the form of block, powder, flake, pellet, rod, film or sheet, and can be used for an adhesive or for the production of various adhesive goods. The adhesive composition of the present invention can be used, without particular limitation, for the applications similar to those of the conventional hot melt adhesive or hot melt type pressure-sensitive adhesive, including adhesion of various materials. For example, it can be used for the adhesion of plastic film or sheet made of polyethylene, polypropylene, polyester or the like, paper, wood, textile goods, metal foil or leather. More specifically, the adhesive composition of the present invention can be used for packing such as formation of bag, sealing of small box or corrugated board box, or production of a can of aluminum foil; bookbinding; production of plywood; woodworking; making shoes; production of fiber products such as carpet backing or binder of unwoven fabric; production of various sanitary goods such as paper diaper; adhesive tape for packing; wire-insulating tape or film; adhesive tape or adhesive sheet for surface protection of various goods; various adhesive films or adhesive sheets used in a semiconductor wafer fabrication process; tying and fixing of pipes or the like; sealant; or adhesive for a label. In the case where the adhesive composition of the present invention is a hot melt adhesive, adhesion can be carried out using a conventionally-used applicator for hot melt adhesive by melting the composition by heating, applying the molten adhesive to adherends, and then solidifying the adhesive with the two adherends being attached together. In the case where the adhesive composition of the present invention is a hot melt type pressure-sensitive adhesive, adhesive goods such as adhesive film or adhesive sheet can be prepared by applying a hot melt type pressure-sensitive adhesive, in a molten state, to one or both surfaces of a base material such as paper, cloth, plastic film or sheet, or metal foil, to form a layer of the pressure-sensitive adhesive on the base material. Whether the adhesive composition of the present invention is a hot melt adhesive or hot melt type pressure-sensitive adhesive, it can easily be molten generally by heating to about 120°C to 200°C and its melt viscosity does not show a large change on the difference of the temperature. Thus, the adhesive composition of the present invention has good process stability so that it permits smooth adhesion or stable production of adhesive goods such as adhesive film. The adhesive composition provided by the present invention is excellent in various properties such as process stability, adhesion or tack, cohesion, characteristics at low temperature, flexibility, oil resistance and solvent resistance. In addition, the adhesive composition of the present invention can be used as a hot melt adhesive or pressure-sensitive adhesive without an organic solvent so that it is free from the problems of air pollution, danger of a fire, worsening of labor environment or industrial hygiene or the like. Furthermore, it can be used without water so that it does not require any drying time or drying apparatus to make the time for adhesion of adherends or preparation of adhesive goods shorter. Thus, it is also excellent in energy saving, working properties and productivity. Other features of the present invention will become apparent in the course of the following descriptions of the exemplary embodiments which are given for illustration of the present invention and are not intended to be limiting thereof. EXAMPLES In the following examples, a number-average molecular weight of the block copolymer before hydrogenation, a number-average molecular weight of the butadiene polymer block before hydrogenation, a number-average molecular weight of an isoprene polymer block before hydrogenation or that of a copolymer block of butadiene and isoprene before hydrogenation, a content of block A before hydrogenation in the block copolymer before hydrogenation, a 1,2-bond content in block A before hydrogenation, a hydrogenation ratio of block A and block B, a glass transition temperature of block B and heat of crystalline fusion of block B are determined as described below. Number-average molecular weights of block copolymer before hydrogenation, block A before hydrogenation and block B before hydrogenation: The number-average molecular weight of the block copolymer before hydrogenation was determined in terms of polystyrene with gel permeation chromatography (GPC). The number-average molecular weights of block A before hydrogenation and block B before hydrogenation were calculated based on the number-average molecular weight of the block copolymer before hydrogenation and charges of the monomers forming block A and the monomers forming block B, respectively. Content of block A before hydrogenation in block copolymer A content of block A before hydrogenation in the block copolymer before hydrogenation was determined from the total charge (W A ) of the monomers forming block A and the total charge (W B ) of the monomers forming block B in accordance with the following formula: Content of block A (wt.%) = [W A / (W A + W B )] x 100 wherein W A means total charge (weight) of the monomers forming block A and W B means total charge (weight) of the monomers forming block B. 1,2-Bond content in block A before hydrogenation The block copolymer before hydrogenation was analyzed by 1 H-NMR and the 1,2-bond content in block A before hydrogenation was calculated. Hydrogenation ratio of block A and block B The block copolymer after hydrogenation was analyzed by 1 H-NMR and hydrogenation ratios of block A and block B were determined. Glass transition temperature of block B With DSC (differential scanning calorimetry), the top peak temperature of differential endothermic curve corresponding to block B of the block copolymer after hydrogenation was found and it was designated as a glass transition temperature of block B. Heat of crystalline fusion of block B With DSC (differential scanning calorimetry), the area of the endothermic curve corresponding to block B of the block copolymer after hydrogenation was found. After converted into the area of the curve per weight of the block copolymer, it was designated as heat of crystalline fusion of block B. Referential Example 1 [Preparation of a hydrogenated triblock copolymer] (1) In a reaction vessel with an internal volume of 5 liter, 3,500 ml of cyclohexane was charged. After purging with dry nitrogen, 12 g (concentration: 10 wt.%) of a solution of n-butyl lithium in cyclohexane was charged, followed by filling with 90 g of butadiene. The butadiene was polymerized for 2 hours under the conditions of a temperature of 50°C and a pressure of 1.0 kg/cm 2 . (2) Next, 420 g of isoprene was charged in the reaction vessel, followed by polymerization for 5 hours under the conditions of a temperature of 50°C and a pressure of 1.1 kg/cm 2 . (3) Furthermore, 90 g of butadiene was charged in the reaction vessel, followed by polymerization for 3 hours under the conditions of a temperature of 50°C and a pressure of 1.1 kg/cm 2 , to give a triblock copolymer of a butadiene polymer block - isoprene polymer block - butadiene polymer block. Concerning the triblock copolymer obtained, the number-average molecular weight of the block copolymer, the number-average molecular weight of each of the butadiene polymer block and isoprene polymer block, content of butadiene polymer block in the block copolymer and 1,2-bond content in the butadiene polymer block were determined in accordance with the above-described methods, respectively. The results are shown in Table 1. (4) In a reaction vessel with an internal volume of 5 liter, 500 g of the triblock copolymer obtained in the above step (3) was charged, followed by the addition of 5 parts by weight of a hydrogenation catalyst (Raney nickel) per 100 parts by weight of the triblock copolymer. Hydrogenation reaction was conducted for 10 hours under the condition of a hydrogen pressure of 50 kg/cm 2 and a temperature of 100°C to give a hydrogenated triblock copolymer. The hydrogenation ratio of each of the butadiene polymer block and isoprene polymer block in the hydrogenated triblock copolymer obtained and glass transition temperature and heat of crystalline fusion of the hydrogenated isoprene polymer block were determined in accordance with the above-described methods, respectively. The results are shown in Table 1. Referential Examples 2 and 3 [Preparation of hydrogenated triblock copolymer] In each of Referential Examples 2 and 3, in a similar manner to the polymerization steps (1) to (3) of Referential Example 1 except that the amounts of butadiene and isoprene charged to the reaction vessel were changed so that the content of the butadiene polymer block in the triblock copolymer before hydrogenation would be the value as shown in Table 1; and the polymerization time was changed to 2 hours, 5 hours and 2 hours in the polymerization steps (1) to (3), respectively, the polymerization was conducted to give a triblock copolymer of a butadiene polymer block - isoprene polymer block - butadiene polymer block. Concerning the triblock copolymer obtained, the number-average molecular weight of the block copolymer, the number-average molecular weight of each of the butadiene polymer block and the isoprene polymer block, content of the butadiene polymer block in the block copolymer and 1,2-bond content in the butadiene polymer block are shown in Table 1. The triblock copolymer obtained was then subjected to hydrogenation in a similar manner to the step (4) of Referential Example 1 to give a hydrogenated triblock copolymer. The hydrogenation ratio of each of the butadiene polymer block and the isoprene polymer block in the hydrogenated triblock copolymer, and glass transition temperature and heat of crystalline fusion of the hydrogenated isoprene polymer block are shown in Table 1. Referential Example 4 [Preparation of a hydrogenated triblock copolymer] In a similar manner to the polymerization steps (1) to (3) of Referential Example 1 except that an equimolar mixture of butadiene and isoprene was used instead of isoprene in the polymerization step (2) described in Referential Example 1; amounts of butadiene and isoprene charged to the reaction vessel were changed so that the content of the butadiene polymer block in the triblock copolymer before hydrogenation would be the value as shown in Table 1; and polymerization time was changed to 2 hours, 6 hours and 2 hours in the polymerization steps (1) to (3), respectively, the polymerization was conducted to give a triblock copolymer of a butadiene polymer block - copolymer block of butadiene and isoprene - butadiene polymer block. Concerning the triblock copolymer obtained, the number-average molecular weight of the block copolymer, number-average molecular weight of each of the butadiene polymer block and the copolymer block of butadiene and isoprene, content of the butadiene polymer block in the block copolymer, and 1,2-bond content in the butadiene polymer block are shown in Table 1. The triblock copolymer obtained was subjected to hydrogenation as in the step (4) of Referential Example 1 to give a hydrogenated triblock copolymer. The hydrogenation ratio of each of the butadiene polymer block and the copolymer block of butadiene and isoprene in the hydrogenated triblock copolymer, and a glass transition temperature and heat of crystalline fusion of the hydrogenated copolymer block of butadiene and isoprene are shown in Table 1. Referential Example 5 [Preparation of a hydrogenated tetrablock copolymer] In a similar manner to Referential Example 1 except that a further step for forming an isoprene polymer block [polymerization step (3a)] was carried out after the polymerization steps (1) to (3) of Referential Example 1; amounts of butadiene and isoprene charged to the reaction vessel were changed so that the content of the butadiene polymer block in the tetrablock copolymer before hydrogenation would be the value as shown in Table 1; and polymerization time was set at 2 hours, 3 hours, 2 hours and 2 hours in the polymerization steps (1) to (3) and (3a), respectively, the polymerization was conducted to give a tetrablock copolymer of a butadiene polymer block - isoprene polymer block - butadiene polymer block - isoprene polymer block. Concerning the tetrablock copolymer obtained, the number-average molecular weight of the tetrablock copolymer, number-average molecular weight of each of the butadiene polymer block and isoprene polymer block, content of the butadiene polymer block in the block copolymer, and 1,2-bond content in the butadiene polymer block are shown in Table 1. The tetrablock copolymer obtained was subject to hydrogenation as in the step (4) of Referential Example 1 to give a hydrogenated tetrablock copolymer. The hydrogenation ratio of each butadiene polymer block and isoprene polymer block in the hydrogenated tetrablock copolymer, and a glass transition temperature and heat of crystalline fusion of the hydrogenated isoprene polymer block (glass transition temperature and heat of crystalline fusion here being the mean value of two hydrogenated isoprene polymer blocks) are shown in Table 1. Referential example 1 Referential example 2 Referential example 3 Referential example 4 Referential example 5 Symbol of block copolymer R - 1 R - 2 R - 3 R - 4 R - 5 Structure A-I-A A-I-A A-I-A A-C-A A-I-A-I Number-average molecular weight Block copolymer 48000 64000 74000 70000 63000 Block A 7200×2 9000×2 18500×2 10500×2 9500×2 Block B 33600 46000 37000 49000 22000×2 Content of block A ( wt.%) 30 28 50 30 30 1,2-Bond content of block A (mole%) 7 7 7 7 7 Hydrogenation ratio of block A (%) 99 100 97 100 92 Hydrogenation ratio of block B (%) 98 99 95 100 88 Glass transition temperature of block B (°C) -53 -53 -52 -51 -52 Heat of crystalline fusion of block B (cal/g) Less than 0.1 Less than 0.1 Less than 0.1 4.2 Less than 0.1 Example 1 (1) 100 parts by weight of the hydrogenated triblock copolymer obtained in Referential Example 1, 200 parts by weight of a tackifier [alicyclic saturated hydrocarbon resin, "ARKON P-100", trade name; product of ARAKAWA CHEMICAL INDUSTRIES CO., LTD.], 100 parts by weight of a softening agent [mineral oil, "Diana Process Oil PW-90", trade name; product of Idemitsu Kosan Co., Ltd.] and 1 part by weight of an anti-oxidant [hindered phenol type, "Irganox 1010", trade name; product of Ciba-Geigy Inc.] were kneaded at 170°C using a kneader to give a hot melt type pressure-sensitive adhesive composition. (2) In order to evaluate the process stability of the pressure-sensitive adhesive composition obtained in the above step (1), the melt viscosities of the pressure-sensitive adhesive composition at 110°C and 140°C were measured by a Brookfield type viscometer to determine a melt viscosity ratio (melt viscosity at 110°C/melt viscosity at 140°C). The results are shown in Table 2. The lower the melt viscosity ratio is, the better the handling properties and process stability of the pressure-sensitive adhesive composition are, because a difference in the temperature of the composition does not cause a large change in the melt viscosity of the composition. (3) The pressure-sensitive adhesive composition obtained in the above step (1) was heated to 150°C for melting and coated onto one surface of a polyethylene terephthalate film of thickness of 50 µm to give a layer of the composition of thickness of 50 µm, followed by cooling to room temperature. Thus an adhesive film having the layer of pressure-sensitive adhesive composition on a polyethylene terephthalate film was prepared. (4) The tack of the adhesive film obtained in the above step (3) was determined at a temperature of 25°C by the ball-tack method in accordance with JIS Z0237. The results are shown in Table 2. (5) The adhesion of the adhesive film obtained in the above step (3) was determined in accordance with JIS Z0237 as follows. An adhesive film cut into 10 mm x 20 mm in size was adhered onto a SUS 304 plate (cold-rolled stainless steel plate) and adhesion at the time when it was peeled under the conditions of a temperature of 25°C, a peel angle of 180 ° and a peel speed of 300 mm/min was determined. The results are shown in Table 2. (6) The cohesion of the adhesive film obtained in the above step (3) was determined in accordance with JIS Z0237 as follows. An adhesive film cut into 25 mm x 25 mm in size was adhered onto a SUS 304 plate and was perpendicularly fixed and maintained. A load of 1 kg was suspended at the lower center of the adhesive film. The time until the adhesive film was peeled off to fall down at a temperature of 40°C was measured, which was designated as cohesion. The results are shown in Table 2. Examples 2 to 5 (1) In Examples 2 to 5, in a similar manner to the step (1) in Example 1 except that the hydrogenated triblock copolymers obtained in Referential Examples 2 to 4 and the hydrogenated tetrablock copolymer obtained in Referential Example 5 were used instead of the hydrogenated triblock copolymer obtained in Referential Example 1, the pressure-sensitive adhesive compositions were prepared, respectively. The process stability (melt viscosity rate) of each of the compositions was evaluated as in the step (2) in Example 1. The results are shown in Table 2. (2) Adhesive films were prepared in a similar manner to the step (3) in Example 1 using pressure-sensitive adhesive compositions obtained in the above step (1) and their tack, adhesion and cohesion were determined as in the steps (4) to (6) in Example 1. The results are shown in Table 2. Comparative Example 1 (1) In a similar manner to the step (1) in Example 1 except that a commercially-available triblock copolymer of styrene polymer block - hydrogenated isoprene polymer block - styrene polymer block ["SEPTON 2002", trade name; product of Kuraray Co., Ltd.] was used instead of the hydrogenated triblock copolymer obtained in Referential Example 1, a pressure sensitive-adhesive composition was prepared. The process stability (melt viscosity ratio) of the composition was evaluated as in the step (2) in Example 1. The results are shown in Table 2. (2) In a similar manner to the step (3) in Example 1 except that the pressure-sensitive adhesive composition obtained in the above step (1) was used, an adhesive film was prepared. The tack, adhesion and cohesion were determined as in the steps (4) to (6) in Example 1. The results are shown in Table 2. Example 1 Example 2 Example 3 Example 4 Example 5 Comparative example 1 [Composition] Base polymer Kind R - 1 R - 2 R - 3 R - 4 R - 5 SEPS Amount (parts by weight) 100 100 100 100 100 100 Tackifier (" ARKON P100") Amount (parts by weight) 200 200 200 200 200 200 Softening agent ("Diana Process Oil PW-90") Amount (parts by weight) 100 100 100 100 100 100 Anti-oxidant ("Irganox1010") Amount (parts by weight) 1 1 1 1 1 1 [Physical properties of pressure-sensitive adhesive composition] Melt viscosity (poise) 140°C 19 64 60 64 61 27 110°C 53 150 180 155 135 150 Melt viscosity ratio (110°C/140°C) 2.8 2.3 3.0 2.4 2.2 5.6 Ball-tack (No.) 5 5 2 5 8 8 Adhesion (g/cm) 450 790 500 800 950 900 Cohesion (minute) 215 244 300 242 200 240 From the results shown in Table 2, it has been found that compared with the pressure-sensitive adhesive composition of Comparative Example 1 using a triblock copolymer of a styrene polymer block - hydrogenated isoprene polymer block - styrene polymer block, the pressure-sensitive adhesive compositions obtained in Examples 1 to 5 using the block copolymers of Referential Examples 1 to 5, respectively, and of the above features (i) to (iv) have a low melt viscosity ratio (melt viscosity at 110°C / melt viscosity at 140°C) and do not show a large change in the melt viscosity on the difference in the temperature of the composition. Thus the pressure-sensitive adhesive composition of Examples 1 to 5 are excellent in process stability. In addition, Table 2 shows that some of the adhesive films using the pressure-sensitive adhesive compositions of Examples 1 to 5 has a small ball-tack, adhesion or cohesion compared with those of the adhesive film using the pressure-sensitive adhesive composition of Comparative Example 1. However, as described before, a pressure-sensitive adhesive composition and adhesive goods such as adhesive tape or adhesive film using a pressure-sensitive adhesive composition are generally used in various forms or for various applications. Some of them are required to adhere to an adherend temporarily and, after use, to be peeled off completely. Some of them are required to adhere to an adherend semipermanently without being peeled. It is therefore necessary to adjust the adhesion, tack or cohesion of them, depending on their usage or manner in use. It is to be noted that even if the adhesion, ball tack or cohesion of the adhesive films obtained in Examples 1 to 5 happens to be low compared with that of the adhesive film obtained in Comparative Example 1, adhesive films obtained in Examples 1 to 5 are not inferior to that obtained in Comparative Example 1. Adhesive films obtained in Examples 1 to 5 have physical properties sufficient for practical use. Example 6 (1) To 100 parts by weight of a hydrogenated triblock copolymer obtained in the above Referential Example 1, 100 parts by weight of a tackifier (ester of hydrogenated rosin, "ESTERGUM H", trade name; product of ARAKAWA CHEMICAL INDUSTRIES CO., LTD.), 50 parts by weight of a wax (paraffin wax, "Paraffin Wax 155", trade name; product of NIPPON SEIRO CO., LTD.) and 1 part by weight of an anti-oxidant (hindered phenol type, "Irganox 1010", trade name; product of Ciba-Geigy Inc.) were kneaded at 170°C using a kneader to give a hot melt adhesive composition. The hot melt adhesive composition obtained did not show tack at normal temperature. (2) In order to evaluate the process stability of the hot melt adhesive composition obtained in the above step (1), the melt viscosities of the adhesive composition at 110°C and 140°C were measured by a Brookfield viscometer to determine a melt viscosity ratio (melt viscosity at 110°C / melt viscosity at 140°C). The results are shown in Table 3. (3) The hot melt adhesive composition obtained in the above step (1) was heated to 150°C for melting and coated on one surface of an aluminum plate of thickness of 0.5 mm to give a layer of the composition of thickness of 50 µm. Two such aluminum plates were prepared. These two aluminum plates coated with the composition were laminated with the coated surfaces faced together, followed by adhesion under the conditions of a temperature of 180°C and pressure-applying time of 1.2 second with a heat sealer ("SG600R", trade name; product of SHIGA HOSOKI CO., LTD.) to give a laminate. (4) The adhesion of the laminate obtained in the above step (3) was determined in accordance with JIS Z0237 as follows. A 90 ° peel test was conducted at a temperature of 25°C under the conditions of a peel speed of 300 mm/min to determine the adhesion of the laminate. The results are shown in Table 3. (5) The hot melt adhesive composition obtained in the above step (1) was molded into a test piece of 10 mm x 60 mm x 2 mm in size. The test piece was allowed to stand overnight at a temperature of -15°C in a refrigerator. Immediately after taken out from the refrigerator, the test piece was bent by hands. The test piece which did not crack was evaluated as A and the cracked one was evaluated as B. In this manner, the characteristics at low temperature were evaluated. The results are shown in Table 3. Examples 7 to 10 (1) In Examples 7 to 10, in a similar manner to the step (1) in Example 6 except that the hydrogenated triblock copolymer obtained in Referential Examples 2 to 4 and the hydrogenated tetrablock copolymer obtained in Referential Example 5 were used instead of the hydrogenated triblock copolymer obtained in Referential Example 1, hot melt adhesive compositions were prepared, respectively. The process stability (melt viscosity ratio) of each of the hot melt adhesive composition was evaluated as in the step (2) in Example 6. The results are shown in Table 3. (2) Laminates were prepared in a similar manner to the step (3) in Example 6 using the hot melt adhesive composition obtained in the above step (1). Their adhesion were measured as in the step (4) in Example 6. The results are shown in Table 3. (3) Test pieces were prepared in a similar manner to the steps (5) in Example 6 using the hot melt adhesive compositions obtained in the above step (1). Their characteristics at low temperature were evaluated as in the steps (5) in Example 6. The results are shown in Table 3. Comparative Example 2 (1) In a similar manner to the step (1) in Example 6 except that a commercially available ethylene-vinyl acetate copolymer [product of Du-PONT MITSUI POLYCHEMICALS CO., LTD.] was used instead of the hydrogenated triblock copolymer obtained in Referential Example 1, a hot melt adhesive composition was prepared. The process stability (melt viscosity ratio) of the composition was evaluated as in the step (2) in Example 6. The results are shown in Table 3. (2) In a similar manner to the step (3) in Example 6 except that the hot melt adhesive composition obtained in the above step (1) was used, a laminate was prepared. Its adhesion was measured as in the step (4) in Example 6. The results are shown in Table 3. (3) In a similar manner to the steps (5) in Example 6 except that the hot melt adhesive composition obtained in the above step (1) was used, test piece was prepared. Its characteristics at low temperature were evaluated as in the steps (5) in Example 6. The results are shown in Table 3. Example 6 Example 7 Example 8 Example 9 Example 10 Comparative example 2 [Composition] Base polymer Kind R - 1 R - 2 R - 3 R - 4 R - 5 EVA Amount (parts by weight) 100 100 100 100 100 100 Tackifier ("ESTERGUM H") Amount (parts by weight) 100 100 100 100 100 100 Wax ("Paraffin Wax 155") Amount (parts by weight) 50 50 50 50 50 50 Anti-oxidant ("Irganox 1010") Amount (part by weight) 1 1 1 1 1 1 [Physical properties of hot melt adhesive composition] Melt viscosity (poise) 140°C 100 280 270 290 250 170 110°C 230 690 760 690 570 520 Melt viscosity ratio (110°C/140°C) 2.3 2.5 2.8 2.4 2.3 3.0 Adhesion (g/cm) 150 180 250 170 160 200 Low temperature characteristics A A A A A B From the above results shown in Table 3, it has been found that the hot melt adhesive compositions in Examples 6 to 10 using the block copolymers of Referential Examples 1 to 5, respectively, and of the above features (i) to (iv) have excellent process stability as indicated by a low melt viscosity ratio (melt viscosity at 110°C / melt viscosity at 140°C). It has also been found that, compared with the hot melt adhesive composition of Comparative Example 2 using an ethylene-vinyl acetate copolymer, the hot melt adhesive composition obtained in Examples 6 to 10 have excellent characteristics at low temperature so that they can be used satisfactorily at low temperature. Example 11 (1) In a similar manner to the step (1) in Example 6 except that the paraffin wax was not used, a hot melt adhesive composition was prepared. Its process stability was evaluated as in the step (2) in Example 6 to find that its melt viscosity ratio (melt viscosity at 110°C / melt viscosity at 140°C) was 2.3. (2) In a similar manner to the step (3) in Example 6 except that the hot melt adhesive composition obtained in the above step (1) was used, a laminate was prepared. Its adhesion was measured as in the step (4) in Example 6 to be 130 g/cm. (3) A test piece was prepared in a similar manner to the step (5) in Example 6 except for the hot melt adhesive composition obtained in the above step (1) was used. Its characteristics at low temperature were evaluated as in the step (5) in Example 6. No cracks were found in the test piece. (4) In a similar manner to the step (3) in Example 1 except that the hot melt adhesive composition obtained in the above step (1), an adhesive film was prepared. Its tack, adhesion and cohesion were determined as in the steps (4) to (6) in Example 1. As a result, it has been found that the ball tack (No.) of the composition was 5, adhesion of the composition was 200 g/cm and cohesion of the composition was 400 minutes. Thus the adhesive composition obtained in Example 11 is excellent in both process stability and characteristics at low temperature. It has also been found that the adhesive composition obtained in Example 11 can be used sufficiently as a hot melt type pressure-sensitive adhesive or hot melt adhesive.

Claims: An adhesive composition which comprises a block copolymer (a) and a tackifier (b), (i) said block copolymer (a) having at least one polymer block A comprising a hydrogenated butadiene polymer and at least one polymer block B comprising a polymer substantially having an olefin polymer structure different from the polymer block A; (ii) said polymer block A in the block copolymer (a) being a hydrogenated butadiene polymer block having a 1,2-bond content of 20 mole% or smaller before hydrogenation; (iii) said polymer block B in the block copolymer (a) having a glass transition temperature of -20°C or lower and heat of crystalline fusion of 33.5 J/g (8 cal/g) or lower ; and (iv) the block copolymer (a) containing the polymer block A before hydrogenation in an amount of 3 wt.% to 80 wt.% based on the weight of the block copolymer (a) before hydrogenation. An adhesive composition according to claim 1, which further comprises a softening agent and is a hot melt type pressure-sensitive adhesive composition. An adhesive composition according to claim 1, which further comprises a wax and is a hot melt adhesive composition.

Inventors: HIRAYAMA YOSHIO, MAEDA MIZUHO, NAKATA HIROMICHI, NISHIKAWA MAKOTO, TAKAMATSU HIDEO, HIRAYAMA, YOSHIO, MAEDA, MIZUHO, NAKATA, HIROMICHI, NISHIKAWA, MAKOTO, TAKAMATSU, HIDEO
Applicants: KURARAY CO, KURARAY CO., LTD.
Application year: 1996
Main classification: C09J153
IPC codes: C09J153