Aromatic polysulfone resin composition

Abstract: An aromatic polysulfone resin composition comprising 100 parts by weight of an aromatic polysulfone resin and 0.001 - 50 parts by weight of at least one compound, added to said resin, selected from oxides, peroxides, double oxides and carbonates of a metal belonging to the Group IA or IIA in the periodic table of elements and having a water absorption of 2 % or less. Said aromatic polysulfone resin composition has an extremely decreased rate of corrosive gas in molded products thereof, retains mechanical strength and heat resistance inherent in aromatic polysulfone resin, is excellent in granulation and molding properties and is suitable for electric and electronic parts.

Description: The present invention relates to an aromatic polysufone resin composition which has an extremely decreased rate of corrosive gas generation from molded products thereof and which is suitable for electric and electronic parts. Aromatic polysulfone resins are materials suitable for electronic parts for which high dimensional stability and high heat resistance are required, owing to the facts that they are amorphous and hence are isotropic and have a small mold shrinkage factor, and that they have a higher glass transition temperature than those of other high heat resistance resins such as polyphenylene sulfides or polyether ketones and thus keep properties, such as mechanical strength, elasticity and creep resistance, at a less lowered level up to a higher temperature as compared with said other resins. Particularly, a material in which an aromatic polysulfone resin is compounded with fibrous materials such as glass fibers has a decreased mold shrinkage factor and improved strength and elasticity and therefore is applied, for example, to relays, switches, connectors, sockets and coil bobbins. Since aromatic polysulfone resins have relatively high melt viscosity, they need a higher molding temperature, injection pressure and molding speed, when they are used for injection molding of electronic parts having a small size and a complicated shape or electronic parts having a thin thickness region. Due to such facts, decomposition gas may be generated by heat on molding and a part of the gas may be occluded in molded products. Said occluded gas may be released from the molded products upon practical use and may create various problems. In particular, when the electronic part is a relay (or case, base, armature or coil bobbin) and the occluded gas is a corrosive gas, a problem may be created that metal contacts are corroded to cause insulation failure even if the released amount of occluded gas is very small. The fact that the gas generated from molded products mainly composed of an aromatic polysulfone resin contains corrosive SO 2 has been confirmed by gas chromatography and mass spectrography. While SO 2 is a gas derived from the aromatic polysulfone resin and it is supposed that the gas is formed by heat decomposition in the course of molding and occluded in the molded products, the detail of mechanism of its production is still unclear. On the other hand, as a means for decreasing gas generation, JP-A-60-186561 discloses that generation of corrosive gases such as SO 2 gas and H 2 S gas which may be formed by decomposition of polyphenylene sulfide (PPS) can be decreased by adding a hydrotalcite to PPS resin. Further, JP-A-62-167356 and JP-A-62-295956 disclose that the formation of corrosive gases can also be decreased by adding zeolites to PPS resin. In addition, JP-A-2-194056 discloses that generation of corrosive gases and aliphatic hydrocarbons with lower boiling points can be decreased when hydrotalcite or zeolites are added to a resin mainly composed of an aromatic polysulfone resin. Additionally, JP-A-3-199265 discloses that formation of corrosive gases can be reduced by adding magnesium oxide to a polyether sulfone resin. Still, JP-A-3-215560 discloses that formation of corrosive gases can be reduced by adding magnesium carbonate to a polyether sulfone resin. However, while an effect is obtained in decreasing SO 2 at a specific adding amount when hydrotalcite or zeolites are mixed to an aromatic polysulfone resin in order to decrease the amount of SO 2 gas generated from the aromatic polysulfone resin composition, granulation becomes difficult due to deterioration in winding of the resin mixture around a screw of an extruder for producing a composition or in taking up of strands and thus inconveniences may occur in practical use. An object of the present invention is to provide an aromatic polysulfone resin composition which has an extremely decreased rate of corrosive gas generation from molded products thereof, which retains mechanical strength and heat resistance inherent in aromatic polysulfone resin, which is excellent in granulation and molding properties and which is suitable for electric and electronic parts. This object could be attained by adding a specific amount of calcium oxide having a water absorption of 2% or less to an aromatic polysulfone resin. Accordingly, the present invention relates to an aromatic polysulfone resin composition comprising 100 parts by weight of an aromatic polysulfone resin and 0.001 - 50 parts by weight of calcium oxide added to said resin. The aromatic polysulfone resin is defined as a polyarylene compound in which three of an arylene unit, an ether bond and a sulfone bond are essential constitutional units and in which the arylene units are disorderly or orderly arranged together with ether and sulfone bonds. Typical examples include, without limitation, those having the following repeating units. wherein the polymer comprising the structural unit (II) includes random copolymers; R 1 represents an alkyl group of 1 to 6 carbon atoms, an alkenyl group of 3 to 10 carbon atoms, a phenyl group or a halogen atom; p is an integer of 0 to 4; m and n indicate the average number of repeating units and are positive numbers of 0.1 - 100; R 1 's on the same or different nuclei may be different from one another; and p's may be different from one another. wherein the polymer comprising the structural unit (III) includes random copolymers; R 1 represents an alkyl group of 1 to 6 carbon atoms, an alkenyl group of 3 to 10 carbon atoms, a phenyl group or a halogen atom; p is an integer of 0 to 4; q, m and n indicate the average number of repeating units and q is a positive number of 1 - 3, and m and n are positive numbers of 0.1 - 100; R 1 's on the same or different nuclei may be different from one another; and p's may be different from one another. It is preferred that, in the aromatic polysulfone resin used in the present invention, m / (m + n) in the structural unit (II) is 0.8 or more; and it is preferred that m / (m + n) in the structural unit (III) is 0.8 or more and q is 1. Among the resin, the preferred one has repeating structural units (I) and (II). Examples include SUMIKAEXCEL PES 3600P, 4100P and 4800P (trade names), manufactured by Sumitomo Chemical Co., Ltd., having (I), and UDEL P-1700 (trade name), manufactured by AMOCO, having (II). Among them, aromatic polysulfones having a repeating structural unit (I) are particularly preferred. The terminal structure of the aromatic polysulfone resins used in the present invention depends on the process for producing each resin and includes, without limitation, Cl, OH and OR (wherein R is an alkyl group). Said calcium oxide has a water absorption of 2 % or less, preferably 1.5 % or less and more preferably 1 % or less. The compound can be used after decreasing the water absorption by means of e.g. dehydrating by heating or reduction of pressure. Compounds having a water absorption of more than 2% are not preferred because granulating properties are deteriorated by use of such compound. The term water absorption refers to the loss in weight (%) of a sample when said sample is heated from room temperature to 400°C at a rate of 10°C per minute using a thermogravimetric analysis apparatus. The amount of calcium oxide to be added is 0.001 - 50 parts by weight and preferably 0.005 - 30 parts by weight based on 100 parts by weight of the aromatic polysulfone resin. When the amount of the calcium oxide is less than 0.001 part by weight, almost no effect is obtained for decreasing corrosive gases generated from the molded products. To the contrary, when more than 50 parts by weight of the compound is added, the effect does not increase proportionally for decreasing corrosive gases generated from the molded products but difficulties in granulation occur that the mechanical properties of the molded products are lowered and, winding of resin mixture to the extruder is deteriorated and extruded strands are not taken up smoothly. The average particle size of the calcium oxide used in the present invention, is 0.01 - 100 µm and preferably 0.1 - 50 µm. An average particle size of less than 0.01 µm is not preferred because the compound aggregates during granulation of the composition. Also, an average particle size of more than 100 pm is not preferred because the surface area per unit weight is lowered and the effect of decreasing corrosive gases thus becomes insufficient. Further, in the present invention, it is possible to add one or more materials selected from fibrous or needle-like reinforcing materials such as glass fibers, silica-alumina fibers, alumina fibers, carbon fibers and aluminum borate whiskers, inorganic fillers such as talc, mica, clay or glass beads, release promoters such as a fluorine resin or metal soap, coloring agents such as a dye or pigment, and usual additives such as an antioxidant, heat stabilizer, ultraviolet light absorber, antistatic agent or surfactant, as necessary. Also, it is possible to add one, two or more resins selected from a small amount of a thermoplastic resin, for example, polyamide, polyester, polyphenylene sulfide, polyether ketone, polycarbonate, polyphenylene ether and its modification product or polyether imide, and a small amount of a thermosetting resin, for example, phenol resin, epoxy resin or polyimide resin. There is no limitation in means for compounding the raw materials in order to produce the resin composition of the present invention. The compounding is generally effected by mixing an aromatic polysulfone; the calcium oxide having a water absorption of 2 % or less and, as necessary, a reinforcing material such as glass fibers, inorganic fillers, a releasing promoter and a heat stabilizer using a Henschel mixer or tumbler, and then melt-kneading using an extruder. The melt-kneading may be conducted by mixing all the raw materials in one batch and feeding to an extruder or, if necessary, by feeding raw materials such as glass fibers and inorganic fillers separately from raw materials mainly composed of a resin. The product molded using the aromatic resin composition of the present invention may be heat-treated in order to further decrease the amount of corrosive gases. Conditions for such heat-treatment are not particularly limited. Since the aromatic polysulfone resin composition of the present invention has a decreased relative amount of corrosive gas generated from molded products, retains mechanical strength and heat resistance inherent in aromatic polysulfone resin and is excellent in granulation and molding properties, it is very useful as a resin for electric and electronic parts. EXAMPLES The present invention will now be illustrated with Examples, which should not be construed as a limitation upon the present invention. In the Examples, determination of corrosive gases released from the molded product, measurement of various properties and comparison of granulation properties were carried out according to the following methods. (1) The amount of the corrosive gas (SO 2 ) released from molded products: The aromatic polysulfone resin composition of the present invention was molded into a plate of 64 mm in length, 64 mm in width and 1 mm in thickness using an injection molding machine (manufactured by Nissei Plastics Co.,Ltd., trade name PS40E5ASE) at a cylinder temperature of 360°C - 370°C and a mold temperature of 150°C. The obtained molded product was cut into chips of 5 mm in length, 5 mm in width and 1 mm in thickness. After washing with water, the chip was placed in a 20 ml vial dried with hot air and combined with 5 ml of deionized water. The vial was sealed with a polytetrafluoroethylene packing material and the content therein was stirred at 80°C for 20 hours to extract SO 4 2- The extract water was cooled and a predetermined amount of it was charged into an ion-chromatogram (type 4510i manufactured by DIONEX; column: AG4A + AS4A + AMMS; eluate: 1.8 mM Na 2 CO 3 , 0.9 mM NaHCO 3 ; flow rate: 1.5 ml/min.) in order to detect SO 4 2- and the amount of SO 4 2- per weight of the chip was calculated. Since it was known that the corrosive gas SO 2 supposed to be occluded in the molded product was completely oxidized to SO 4 2- under the above extracting conditions, a larger amount of SO 4 2- was extracted from the molded product means that a larger amount of the corrosive gas was released. (2) Tensile strength and deflection temperature under load An ASTM No.4 dumbbell and a test piece of 127 mm in length, 12.7 mm in width and 6.4 mm in thickness were molded from the aromatic polysulfone resin composition of the present invention at a cylinder temperature of 360 - 370°C and a mold temperature of 150°C and subjected to measurement according to ASTM D638 and ASTM D648, respectively. (3) Comparison of granulating properties Granules of the aromatic polysulfone resin of the present invention and granules of that of Comparative Example 1, prepared by methods shown in Example and Comparative Example, respectively, were compared in respect of feeding property to twin-screw extruder and taking-up property of the extruded strands and the results are shown with a score and criteria: ○, equivalent; Δ, slightly inferior; ×, clearly inferior. Examples 1 - 9 and Comparative Example 1 - 5 Aromatic polysulfone resin powders (manufactured by Sumitomo Chemical Co., Ltd., trade name Sumika Excel PES 3600P) and a compound such as an oxide of a metal belonging to Group IA or IIA in the periodic table of elements having a water absorption of 2 % or less in a composition shown in Table 1 were mixed with a Henschel mixer and granulated using a twin-screw extruder (manufactured by Ikegai Iron Works, PCM-30) at a cylinder temperature of 340°C to give an aromatic polysulfone resin composition. Similarly, an aromatic polysulfone resin composition without metal compound (Comparative Example 1) was prepared. The granulation properties were evaluated according to the above methods when the resin compositions were granulated. In addition, the resin compositions were molded by injection according to the above method and the molded products were assayed for the amount of SO 4 2- in the molded products, tensile strength and deflection temperature under load of the molded products. The results are shown in Table 1. Formulation of Resin Compositions Amount SO 4 2- (ppm) Tensile Strength (kg/cm 2 ) Deflection Temp. by Load °C Granulation Aromatic Polysulfone (Parts by weight) Additive Kind Water Absoption (%) Amount (Parts by Wt.) Example 1 100 Calcium oxide 0.8 0.02 0.6 880 208 ○ Example 2 100 Calcium oxide 0.8 5 0.4 860 207 ○ Example 3 100 Calcium oxide 0.8 40 0.3 850 205 ○ Example 4 100 Magnesium oxide 1.2 0.02 1.0 880 208 ○ Example 5 100 Magnesium oxide 1.2 5 0.6 880 207 ○ Example 6 100 Barium oxide 0.2 0.03 0.5 880 208 ○ Example 7 100 Barium peroxide 0.2 0.03 0.5 880 208 ○ Example 8 100 Wollastonite 0.7 0.2 0.9 870 206 ○ Example 9 100 Dolomite 0.4 0.2 1.1 870 206 ○ Comp. Ex. 1 100 - - - 7.0 880 208 ○ Comp. Ex. 21 100 Calcium oxide 0.8 0.0005 6.9 880 208 ○ Comp. Ex. 3 100 Calcium oxide 0.8 60 0.3 650 203 × Comp. Ex. 4 100 Calcium oxide 2.9 5 0.8 880 207 Δ Comp. Ex. 5 100 Magnesium oxide 3.7 5 0.9 860 207 Δ It can be clearly seen that the aromatic polysufone resin compositions containing calcium oxide having a water absorption of 2 % or less (Examples 1 - 9), according to the present invention, had an extremely small content of SO 4 2- in the molded product when compared with the aromatic polysulfone resin composition containing no such compound (Comparative Example 1). In other words, in the former, SO 2 gas released from the molded product was clearly decreased. On the other hand, in the composition in which the content of the compound was smaller than 0.001 part by weight (Comparative Example 2), the effect of decreasing SO 4 2- in the molded product was little. In the composition in which the content exceeded 50 parts by weight (Comparative Example 3), while the effect of decreasing SO 4 2- in the molded product was comparable to that in the composition in which the content was 40 parts by weight (Example 3), the tensile strength lowered and the granulation properties were significantly inferior. Further, the aromatic polysufone resin compositions containing at least one compound having a water absorption more than 2 % (Comparative Examples 4 and 5), had lesser effect of decreasing SO 4 2- and granulation properties when compared with the aromatic polysulfone resin composition containing the compound having a water absorption of 2 % or less (Examples 1 - 9).

Claims: An aromatic polysulfone resin composition comprising 100 parts by weight of an aromatic polysulfone resin and 0.001 - 50 parts by weight of calcium oxide having a water absorption of 2 % or less as determined by the method defined below: Water absorption: loss (%) in weight of a sample when said sample is heated from room temperature to 400°C at a rate of 10°C per minute using a thermogravimetric analysis apparatus. The aromatic polysulfone resin composition according to claim 1, wherein the calcium oxide, has a water absorption of 1.5 % or less. An aromatic polysulfone resin composition according to claim 1, wherein the amount of the calcium oxide is 0.005 - 30 parts by weight based on 100 parts by weight of the aromatic polysulfone resin. An aromatic polysulfone resin composition according to claim 1, wherein the average particle size of the calcium oxide is 0.01 - 100 µm. The use of an aromatic polysulfone resin composition according to any one of claims 1 to 4 for the production of electric or electronic parts.

Inventors: NAGASHIMA TOHRU, NOMURA HIDEO, NAGASHIMA, TOHRU, NOMURA, HIDEO
Applicants: SUMITOMO CHEMICAL CO, SUMITOMO CHEMICAL COMPANY LIMITED
Application year: 1996
Main classification: C08K3
IPC codes: H01B3, C08L81, C08K3