APPARATUS FOR AND METHOD OF MANUFACTURING CASK STAVES

Abstract: There is described a method of manufacturing cask staves comprising the steps of providing a stave blank of required shape and size, and volumetrically heating said stave blank such that chemical changes brought about by the heating are uniform throughout the stave blank. There is also described an apparatus for the manufacture of cask staves comprising volumetric heating means for uniformly heating a stave blank of the required shape and size such that uniform chemical changes take place throughout said stave blank.

Description: APPARATUS FOR AND METHOD OF MANUFACTURING CASK STAVES The present invention relates to a method and apparatus for manufacturing cask staves which can subsequently be either automatically or manually assembled into casks. In the production of Scotch whisky the distilled spirit is placed in oak casks and stored for a minimum of three years to mature and to develop characteristic flavour and colour. The maturation takes place as a result of the reaction between the spirit, heat generated derivatives of the oak and oxygen. The position within the wood at which this reaction occurs moves outwards as time passes and the spirit penetrates the wood. Because of the methods of heating in conventionally made casks, the availability of the wood components required for maturation reduces with dept . In order for maturation to take place these so called precursors are made available within the oak by heating it to cause changes to its complex chemical structure. Traditionally this is achieved by placing newly made casks over a flame, burning the inner face an d transferring heat into the body of the timber b y conduction. Such a process is potentially flawed in that the degree of surface burning, the temperature gradient, and the effect this will have on the chemical structure within the volume of the timber is difficult to control. American law requires that bourbon whisky is mature d in new casks and therefore the Scotch whisky industry has purchased second-hand casks from the bourbon distilleries for many years. It is acknowledged that there is a quality problem arising from the use of casks built to a price specifically for a single fill of bourbon. At the very minimum this has meant that Scotch whisky has to be held in casks for a much longer period to achieve an acceptable degree of maturation. As a result of the dependence on this cheap, if uncontrolled source of casks as well as other economic factors, there has been a large decline in persons skilled in the art of forming the classis barrel "bilge". The cooperages that have survived generally only repair old casks and reassemble American made ones from sets of "knocked down" staves. The object of the present invention is to overcome the problem of providing cask staves of consistent quality from new wood thus allowing the assembly of casks using the existing skill base of the coopers. In accordance with one aspect the present invention provides a method of manufacturing cask staves comprising the steps of providing a stave blank of required shape and size, and volumetrically heating said stave blank such that chemical changes brought about by the heating are uniform throughout the stave blank. The present invention also provides apparatus for the manufacture of cask staves comprising volumetric heating means for uniformly heating a stave blank of the required shape and size such that uniform chemical changes take place throughout said stave blank. The main difference between the traditional method of heat treatment and the heat treatment method of the present invention is in the depth and degree of uniformity of heating which can be achieved throughout the thickness of the stave. The more uniform heat treatment of the stave using the method and apparatus of the present invention has the effect of making more of the precursors available for exchange with the spirit and thereby enhances the maturation both in time and in specific characteristics of flavour and colour. The more uniform heating of the thickness of the stave also provides the benefit of providing a sufficient reserve of precursors for second and subsequent fills of the cask. Since much of the marketable characteristics of whisky arises from the craft of maturation and that in turn is dependent upon the condition of the wood with which the spirit makes contact, it is important that the new method is able to mimic the traditional one as and when required. The traditional method involves heating the inner surface of casks to high temperature e.g. using a flame which has the effect of charring as well as changing the internal wood chemistry. Thus to mimic this process in accordance with one embodiment of the present invention for casks such as whisky casks, a combination of volumetric and surface heating is used. The volumetric heating can be achieved by dielectric heating e.g. using radio frequency electromagnetic radiation or microwave radiation. This cannot be used alone for the production of staves for whisky casks since a burnt inner surface is required to provide colour and flavour. The burnt surface is achieved in accordance with one embodiment of the present invention using radiant heat such as an infrared source. Thus for the production of whisky cask staves in accordance with an embodiment of the present invention a combination of volumetric heating and surface heating is able to mimic the traditional technique whilst providing the additional benefit of a more uniform heating of the wood. With spirits other than Scotch whisky, e.g. other whiskies, brandies and wines, the heating process to provide the required colour and flavour to the spirit may only require the volumetric heating of the cask staves. During the volumetric heating the process for the production of cask staves, in order to reduce surface heat loss and enhance the uniform heating of the cask staves, hot air can be circulated around the staves. During the volumetric heating the staves are typically heated to a temperature of 100°C and 140° and the temperature of the air being circulated can be of a similar range. In order to avoid damage to the structure of the wood the rate of temperature rise must be controlled and it has been found that the time taken to reach the maximum temperature should be in the region of at least two or three minutes. Although in the embodiment described hereinafter the surface heating of the staves takes place after the volumetric heating, the present invention is not limited to this since it is believed that the two heating stages, if carried out, can be carried out in any order. In order to achieve the desired toasting of the surface of the cask staves preferably the radiant heater operates at a temperature in the range of 600°C to 900°C. The duration of the surface heating will then be determined by the degree of toasting which is required and this is determined by the requirements of the spirit to be matured. In accordance with the second aspect of the present invention a method of preforming a cask stave comprises the steps of supporting a pre-cut elongate stave on two supports such that said stave is supported just inboard of ends of said stave, and applying a force to a point on said stave between said supports until said stave achieves a desired degree of curvature. In accordance with the second aspect the present invention also provides apparatus for preforming cask staves comprising a support arrangement for supporting a pre-cut elongate stave, said support arrangement comprising two supports to support said stave just inboard of ends of said stave, and a press for applying a force to a point on said stave between said supports until said stave achieves a desired degree of curvature. Thus in accordance with the second aspect of the present invention staves can be pressed automatically to the desired shape. The shape is held for the time necessary for the shape to be set whereby the finished stave can then be made available for assembly into a cask. This method of pressing the staves into the necessary shape is applicable to staves which have been heat treated in accordance with the first aspect of the present invention and to cask staves which have undergone no beat treatment. For certain spirits and even for non-spirits heat treatment is not required. In accordance with one embodiment where the staves to be pressed have undergone the heat treatment process, the staves are passed straight into the press to be pressed whilst still hot. Where the staves have not undergone the heat treatment, or have been allowed to cool off, in accordance with one embodiment of the present invention the staves can be heated either directly before or during the pressing process. In accordance with one embodiment the apparatus is able to press a plurality of cask staves simultaneously and comprises conveying means for conveying a plurality of the staves between the support arrangement and the press, wherein the support arrangement is arranged to support a — o — plurality of the staves simultaneously and the press is arranged to apply a force to the plurality of staves simultaneously. Conveniently the conveying means comprises two parallel conveyors arranged to support and convey a plurality of substantially parallel spaced staves. In this arrangement the conveyors are preferably arranged to be deflected when the force is applied to the staves by the press such that the staves become supported by the support arrangement. There is a risk of stave breakage during the pressing operation. It has been found that the addition of water to the back face of the stave immediately before or during the application of pressure to it minimises this risk. The water can be applied in a number of ways including full immersion, wiping and spraying. In order for the final shape of the stave to be held, it is preferable for the press to apply the force for between two and five minutes. An embodiment of the present invention will now be described with reference to the drawings, in which:- Figure 1 is a schematic side elevation view of a cask stave forming apparatus in accordance with one embodiment of the present invention; Figure 2 is a planned view of the arrangement of Figure 1; Figure 3a is a side elevation of the press of Figure 1 during the press operation; and Figure 3b is a planned view of the press of Figure 1 showing the components in more detail. The drawings illustrate apparatus for the manufacture of cask staves in accordance with one embodiment of the present invention. As can be seen in the drawings, a heating section generally indicated by A is provided and includes a continuously operating conveyor 1 onto which staves 10 which have been pre-cut to the desired shape and size can be loaded at one end. The staves are generally flat elongate pieces of wood with tapering ends. In cross-section the upper (inner) surface is slightly concave whilst the lower (outer) surface is slightly convex. The cross-sectional shape is necessary to form the bilge. The staves 10 are then transported by the conveyor 1 into a volumetric heating section 2 which provides volumetric heating by the application of radio frequency electromagnetic radiation. The volumetric heating section 2 comprises a radio frequency heating section in this embodiment and includes a matching box 3 and an RF electrode 4 which is suspended above the conveyor. Once the staves 10 have been volumetrically heated as they pass through the radio frequency (RF) section 2, they pass on the conveyor 1 into a radiant heating section 5. The radiant heating section 5 comprises an array of infrared emitters 6 suspended above the conveyor 1 to thereby toast the upper (inner) surface of the cask staves 10 as they pass through the radiant heating section 5. Once the staves 10 have passed on the conveyor 1 through the radiant heating section 5 they are discharged into a buffer store 7 whereafter they are transferred into the pressing section generally indicated by B in the drawings. The pressing section B comprises a conveyor arrangement 11 for conveying a plurality of parallel spaced heated staves 10 through the press arrangement 12. The conveyor arrangement 11 comprises two parallel chain conveyors 11a and lib which support the staves 10 just inboard of their outer ends. The chain conveyors 11a and lib carry locators 13 to position each stave 10 so that it is presented correctly to the press arrangement 12. The conveyor arrangement 11 conveys the staves 10 into the press arrangement 12. The press arrangement 12 comprises a male press part 14 comprising a plurality of male press faces 15. The male press part 14 is arranged to lie above the centre of a plurality (in the illustrated example 10) of staves 10. The male press part 14 is connected to and driven by two actuators 16a and 16b which can operate to force the male press member against the upper surfaces of the centre part of the staves 10 as shown in Figure 3a. The faces 15 of the press male part 14 have a convex surface in two orthogonal directions so that when they contact the upper surface of the centre portion of the staves 10 they tend to induce a curvature along the elongate axis of the staves 10 and fit into the concave shape of the upper (inner) surface of the stave without damaging its edges. As can be seen in Figure 1, beneath the chain conveyors 11a and lib there is provided a female press arrangement 17 which can be seen in Figure 3b as comprising two parallel bars 17a and 17b arranged at or near the ends of the staves 10. As can be seen more clearly in Figure 3a, during operation of the press 12, the actuators 16a and 16b force the male press part 14 against the upper surfaces of a plurality of staves 10, whereby the chain conveyors lla and lib are deflected such that the ends of the staves 10 come into contact with the female press arrangement 17 comprising the bars 17a and 17b. Further force by the actuators 16a and 16b causes the curving of the staves 10. The pressing section B also includes a hopper 18 to receive the formed staves. Alternatively the formed staves can be discharged into an assembly jig for the automatic forming of casks. The operation of the cask stave manufacturing apparatus will now described. Staves which have been pre-cut to the required shape and size from new wood are loaded onto the conveyor bait 1 of the heating section A and continually pass first through a radio frequency heated zone 2 where the temperature of the body of the stave 10 is raised to a predetermined temperature which is preferably in the order of 100°C to 140°C. This has the effect of changing the chemical structure of the wood to release the chemical precursors. This heating process also makes the structure of the wood more pliable for later forming. The rate of temperature rise must be controlled to avoid damage to the structure of the wood and it has been found that three minutes is a satisfactory time in which to raise the temperature with minimum damage. In the volumetric heating section 2 in order to ensure a more even heating of the staves 10, heated air can be simultaneously applied in order to prevent heat loss from the surface of the staves 10. A convenient air temperature for this is in the region of 130°C. The stave blanks 10 are then carried into a surface toasting zone which is the radiant heating section 5 which can either be electrically or gas operated. In the radiant heating section 5 what will become the inner cask surface is then heated using a high power density non-contact heating system which can conveniently be a medium wave electric or gas infrared heater with an emitter surface temperature in the range of 600°c to 900°c. The so-called "toasting" of the surface causes local changes to the wood chemistry manifest by a colour change. The degree of toasting is controlled by the duration of the heating to achieve the desired flavour and colour characteristics as specified by a distiller. Once the staves 10 have been heated in the two stages they can be transferred automatically or manually to the pressing section B, where by mechanical or hydraulical means the stave is formed to the desired shape whilst still hot. The staves 10 are transferred onto a conveyor arrangement 11 and are arranged to lie spaced and parallel with the toasted surface facing upwards. The staves 10 are then transferred into the press arrangement 12. Within the press arrangement 12 a male press member 14 is forced onto the middle section of the toasted upper surface of the staves 10 whereby the conveyor arrangement 11 is deflected downwards until the staves 10 contact the female press arrangement 17. The female press arrangement 17 supports the ends of the staves and further application of force by the male press arrangement 14 causes the staves 10 to bend. In use casks are required to be watertight. To achieve this it is necessary that the formed staves offered up for assembly are slightly under bent so that the metal hoops can pull them to final shape during assembly. It is therefore important that the degree of over-bend and spring-back is controlled accordingly. Provision is made on the press to adjust the position of a stop on the closing stroke to achieve this. There is a risk of stave breakage during the pressing operation and the application of water to the back face of the stave immediately before pressure is applied minimises the risk of breakage. The water can be applied to the stave 10 in a number of ways including immersion, wiping and spraying. In the embodiment illustrated the preferred method is spraying. In order for the stave 10 to achieve final shape, it is necessary for the stave to be held by the press for a minimum time. A typical cycle time of press closure, hold and press release is in the region of three minutes. Although the embodiment of the present invention described hereinabove includes both the heating section A and the pressing section B, the present invention is not limited to the combination of such features although a most useful method of forming cask staves for certain applications is achieved using the combination. For casks for containing liquids which do not require the wood to be heat treated, only the pressing section B need be utilised (although generally heat will still be needed to make the wood pliable) . Further, there is also within the scope of the present invention to only utilise the heating section A to provide cask staves which have been heat treated as desired for assembling into casks using traditional methods. Alternatively the heating section A can be used to heat treat second hand staves which have become "exhausted" by earlier fills. In this case the pressing section B is not required. Although the embodiment illustrated in the drawings uses only two actuators 16a and 16b for the pressing there may be any number. In order to take account of variations in stave dimensions each of the faces 15 of the male press part 14 may be provided with an individual actuator and each face 15 may be of a different shape i.e. curvature.

Claims: CLAIMS 1. A method of manufacturing cask staves comprising the steps of providing a stave bank of required shape and size, and volumetrically heating said stave blank such that chemical changes brought about by the heating are uniform throughout the stave blank. 2. A method as claimed in Claim 1 wherein said stave blanks are dielectrically heated using electromagnetic radiation. 3. A method as claimed in Claim 2 wherein said stave blanks are heated using radio frequency radiation. 4. A method as claimed in Claim 2 wherein said stave blanks are heated using microwave radiation. 5. A method as claimed in any preceding claim including the step of heating a surface of said stave blank. 6. A method as claimed in Claim 5 wherein said surface of said stave blank is heated using radiant heat. 7. A method as claimed in any preceding claim wherein the step of volumetric heating raises the temperature of said stave blank uniformly to between 100°C and 140°C. 8. A method as claimed in Claim 7 wherein the temperature of said stave blanks are raised to between 100°C and 140 C within a time scale of two minutes or more. 9. A method as claimed in Claim 8 wherein said time scale is at least three minutes. 10. A method as claimed using a radiant heater which ooppeerraatteess iinn tthhee rraarnge of 600°C to 900°C and does not contact said surface. 11. A method as claimed in any preceding claim wherein said step of volumetric heating includes the step of circulating hot air around said stave blank. 12. A method as claimed in Claim 11 wherein said air is circulated at a temperature between 100°C and 150°C. 13. A method as claimed in any preceding claim including the step of pressing the heated stave blanks whilst still hot to achieve the desired curvature of the heated stave blanks. 14. A method as claimed in Claim 13 wherein said step of pressing comprises the step of placing said heated stave blank on two supports such that said heated stave blank is supported just inboard of its ends, and applying a force to the centre of said heated stave blank until the desired degree of curvature is achieved. 15. A method as claimed in Claim 13 or Claim 14 including the step of applying water to a second surface of said heated stave blank opposed said surface which has been subject to radiant heating. 16. A method as claimed in Claim 15 wherein said water is applied by immersion, wiping, or spraying. 17. A method as claimed in any one of Claims 13 to 16 wherein the step of pressing takes between two and five minutes. 18. A method as claimed in any preceding claim including the step of cutting said stave blank of the required shape and size from desired timber. 19. Apparatus for the manufacture of cask staves comprising volumetric heating means for uniformly heating a stave blank of the required shape and size such that uniform chemical changes take place throughout said stave blank. 20. Apparatus as claimed in Claim 19 wherein said volumetric heating means comprises dielectric heating means for dielectrically heating said stave blank using electromagnetic radiation. 21. Apparatus as claimed in Claim 19 or Claim 20 wherein said dielectric heating means comprises a radio frequency heater. 22. Apparatus as claimed in Claim 19 or Claim 20 wherein said dielectric heating means comprises a microwave heater. 23. Apparatus as claimed in any one of Claims 19 to 22 including a radiant heater for heating a surface of said stave blank. 24. Apparatus as claimed in any one of Claims 19 to 23 including hot air circulating means for circulating hot air around said stave blank during volumetric heating. 25. Apparatus as claimed in any one of Claims 19 to 24 including conveying means for conveying a plurality of said stave blanks continuously through said volumetric heating means. 26. Apparatus as claimed in any one of Claims 19 to 25 including a press for pressing the heated stave blanks whilst still hot to achieve the desired curvature of the heated stave blank. 27. Apparatus as claimed in claim 26 including a second conveying means for conveying a plurality of said heated stave blanks into said press, said press being arranged to press a plurality of said heated stave blanks simultaneously. 28. Apparatus as claimed in Claim 27 wherein said second conveying means comprises two parallel conveyors arranged to support a plurality of substantially parallel spaced said heated stave blanks. 29. Apparatus as claimed in Claim 28 wherein said press includes a male part adapted to be movable to apply a force to the centre of said heated stave blanks on said conveyors and a female part arranged below said conveyors to receive said heated stave blanks as said conveyors are displaced by the force applied by said male part, said female part being arranged to support said heated stave blanks just inboard of their ends whilst said force is applied by said male part to said centre of said heated stave blanks. 30. Apparatus as claimed in any one of Claims 19 to 29 including appliction means for applying water to a second surface of said heated stave blank which is opposed the surface which is subject to the force applied during pressing. 31. A method of preforming a cask stave comprising the steps of supporting a pre-cut elongate stave on two supports such that said stave is supported just inboard of ends of said stave, and applying a force to a point on said stave between said supports until said stave achieves a desired degree of curvature. 32. A method as claimed in Claim 31 wherein a plurality of said staves are pressed simultaneously. 33. A method as claimed in Claim 31 or Claim 32 including the step of heating said stave. 34. A method as claimed in any one of Claims 31 to 33 including the step of applying water to a surface of said stave opposite the surface to which said force is applied. 35. A method as claimed in any one of claims 31 to 34 wherein said force is applied for between two and five minutes. 36. Apparatus for preforming cask staves comprising a support arrangement for supporting a pre-cut elongate stave, said support arrangement comprising two supports to support said stave just inboard of ends of said stave, and a press for applying a force to a point on said stave between said supports until said stave achieves a desired degree of curvature. 37. Apparatus as claimed in Claim 36 including conveying means for conveying a plurality of said staves between said support arrangement and said press, said support arrangement being arranged to support a plurality of said staves simultaneously and said press being arranged to apply a force to said plurality of staves simultaneously. 38 Apparatus as claimed in Claim 37 wherein said conveying means comprises two parallel conveyors arranged to support and convey a plurality of substantially parallel spaced said staves. 39. Apparatus as claimed in Claim 38 wherein said conveyors are arranged to be deflected when said force is applied to said staves by said press, such that said staves become supported by said support arrangement. 40. Apparatus as claimed in any one of Claims 36 to 39 including water appliction means for applying water to a surface of said stave opposed the surface to which said force is applied by said press. 41. Apparatus as claimed in any one of Claims 36 to 40 including heating means for heating said stave during pressing. 42. Apparatus as claimed in any one of Claims 36 to 41 wherein said press has a face which has a curved convex profile in a direction along the length of the stave such that when said stave is pressed concave curvature is produced along an elongate axis of said stave. 43. Apparatus for forming cask staves substantially as hereinbefore described with reference to and as illustrated in the drawings. 44. A method of forming cask staves substantially as hereinbefore described with reference to the drawings.

Inventors: JONES PETER LESLIE, JONES, PETER, LESLIE
Applicants: EA TECH LTD, JONES PETER LESLIE, EA TECHNOLOGY LIMITED, JONES, PETER, LESLIE
Application year: 1996
Main classification: C12G3
IPC codes: B27H3, C12G3