Method for preparing a product comprising an organopolysilxane bearing polyoxyalkylene bonded to silicon across alkylene

Abstract: There is disclosed herein a polyoxyalkylene-modified organopolysiloxane that generates almost no odor with the passage of time, and a method for its preparation. This organopolysiloxane bears polyoxyalkylene bonded to silicon across alkylene, and contains 5-1,000 ppm by weight of an antioxidant. It also has a peroxide value not exceeding 5 meq/kg, and a total content of aldehyde plus ketone not exceeding 100 ppm.

Description: This invention referes to a method for preparing a product comprising an organopolysiloxane which carries polyoxyalkylene bonded to silicon across alkylene. Hereinafter, it is referred to as a "polyoxyalkylene-modified organopolysiloxane". More particularly, this method surprisingly provides an odorless polyoxyalkylene-modified organopolysiloxane that does not generate odor with elapsed time. Polyoxyalkylene-modified organopolysiloxanes, synthesized by platinum-catalyzed addition between organohydrogensiloxanes and alkenyl-monoterminated polyoxyalkylenes, are used as base oils for cosmetics due to their excellent feel upon contact with human skin, and excellent spreadability during application. Unfortunately, these prior art organopolysiloxanes readily produce odor with the passage of time, and ultimately emit an unpleasant odor after just extended periods of standing. In response to this problem, JP-A 2-302438 (and its United States equivalents 5,118,764 and 5,228,831), propose a polyoxyalkylene-modified organopolysiloxane that is almost free of odor generation with the passage of time, and a method for preparation. The aforementioned application provides a polyoxyalkylene-modified organopolysiloxane that produces no more than 1,000 ppm of total ketone plus aldehyde when treated under seal with 10 -4 N aqueous hydrochloric acid at 60°C for 24 hours. The preparative method taught therein comprises first treating a conventional polyoxyalkylene-modified organopolysiloxane with an acidic substance, or an aqueous acid solution having a pH of less than or equal to 7, to force production of odiferous substances, and subsequently eliminating the odiferous substances produced. This treatment with aqueous acid solution or an acidic substance has disadvantages. For instance, residual acid or acidic substance remains present, and a thorough washing with water is necessary to eliminate these residues. Moreover, even the resultant polyoxyalkylene-modified organopolysiloxane develops odor when held for a long period of time, preventing its use in some cosmetic applications. To solve this problem, we have discovered that not only must the quantity of ketone and aldehyde not exceed a particular level, but also the peroxide value must not exceed a particular level. It has also been determined that additional beneficial effects are obtained by addition of a small amount of an antioxidant. The Derwent Abstract JP-A-5331021 discloses the use of an extract and/or powder of sage in an amount of 0.005-5 wt.% to prevent odorisation of a composition containing water-soluble silicones. The invention object is to provide a method for preparing an odor-free polyoxyalkylene-modified organopolysiloxane, and more particularly to achieve a polyoxyalkylene-modified organopolysiloxane which produces almost no odor with the passage of time. Our method unexpectedly provides organopolysiloxanes bearing polyoxyalkylene bonded to silicon across alkylene that contain from 5 ppm to 1,000 ppm by weight of an antioxidant, have a peroxide value not exceeding 5 meq/kg, and a total content of aldehyde plus ketone not exceeding 100 ppm. It also introduces a method for preparing the organopolysiloxane bearing polyoxyalkylene bonded to silicon across alkylene. Our method comprises conducting a hydrosilylation reaction in an organic solvent between (A) a polyoxyalkylene bearing alkenyl at a single terminal, having a peroxide value not exceeding 3 meq/kg, and a total content of aldehyde plus ketone not exceeding 100 ppm by weight, (B) an organohydrogenpolysiloxane that contains at least one silicon-bonded hydrogen atom, in the presence of (C) a platinum catalyst, 1-200 ppm of an antioxidant and (D) an organic solvent; removing the organic solvent under reduced pressure; then blending in a quantity of water that is at least one weight percent of the total of components (A) and (B), subsequently eliminating the water under reduced pressure; and thereafter adding from 4 to 800 ppm of antioxidant, and optionally from 1 to 500 ppm of buffer having a pH from 5.5 to 8 when dissolved in water. The polyoxyalkylene-modified organopolysiloxane of this invention must contain from 5 to 1,000 ppm antioxidant, and preferably from 10 to 400 ppm antioxidant. The nature of the antioxidant is not critical, as long as it has the capacity to inhibit oxidation of the polyoxyalkylene. The antioxidant is exemplified by vitamins such as D 2 , D 3 , D 4 , and E; or hindered phenols such as 2,6-di-tert-butyl-p-cresol, 4,4-dihydroxyphenylisopropane, and 4,4-thiobis(6-tert-butyl-m-cresol). Vitamin E is most preferred. The peroxide value must not exceed 5 meq/kg, since odor will be produced with the passage of time. Moreover, the total quantity of aldehyde plus ketone must not exceed 100 ppm. The type of polyoxyalkylene-modified organopolysiloxane used herein is not critical as long as it is an organopolysiloxane bearing polyoxyalkylene bonded to silicon across an alkylene radical. Such polyoxyalkylene-modified organopolysiloxanes include compounds defined by the following general formulas: where R 1 denotes a monovalent hydrocarbon group; R 2 is alkylene; R 3 is a hydrogen atom, a C 1 to C 6 alkyl group, or an acyl group; A is R 1 or a group defined by the general formula -R 2 -O(C p H 2p O) x R 3 ; k is zero or a positive integer; l is zero or a positive integer; p is an integer with a value from 2 to 4; x is an integer with a value from 1 to 100; with the proviso that when l is zero, at least one of the groups A has the formula -R 2 -O(C p H 2p O) x R 3 ); and where R 1 , R 2 , R 3 , p , and x are defined as above; m is an integer with a value from 0 to 8; n is an integer from 1 to 8; and m + n is an integer from 3 to 8. Polyoxyalkylene (A) is an essential precursor in our method. Examples of polyoxyalkylene (A) are compounds of general formula LO(Cp H 2p O) x R 3 in which L is an alkenyl group such as vinyl or allyl; R 3 is a hydrogen atom, a C 1 -C 6 alkyl such as methyl, ethyl, or propyl, or an acyl group; p is an integer with a value from 2 to 4; and x is an integer with a value from 1 to 100. These compounds (A) are exemplified by: CH 2 =CHCH 2 O(CH 2 CH 2 O) 10 H, CH 2 =CHCH 2 O(CH 2 CH 2 O) 12 H, CH 2 =CHCH 2 O(CH 2 CH 2 O) 14 H, or Compounds with general formulas below are examples of organohydrogenpolysiloxane (B): wherein B is R 1 or the hydrogen atom, wherein R 1 , k , and l are defined above, and wherein R 1 is defined above and q is an integer with a value from 3 to 8. Compounds of the following formula are preferred among the above organohydrogenpolysiloxanes: where Me is methyl, k is 0 or a positive integer, and l is a positive integer. Polyoxyalkylene (A) and organohydrogenpolysiloxane (B) are addition reacted in organic solvent in the presence of a platinum catalyst (C) in our preparative method. This reaction, known as a hydrosilylation reaction, consists of the addition of the alkenyl in component (B) to the silicon-bonded hydrogen in component (A). This reaction is carried out in an organic solvent, i.e., component (D). The type of organic solvent is not critical as long as it is able to dissolve both components (A) and (B). The organic solvent is exemplified by ethanol, isopropyl alcohol, toluene, and xylene. After reaction, the organic solvent is removed under reduced pressure, from the reaction product of components (A) and (B). After solvent elimination, a quantity of water, that is at least 1 weight % of the total of components (A) plus (B), is first mixed into the reaction product, and subsequently eliminated under reduced pressure. The antioxidant is then mixed into the reaction product obtained at from 4 to 800 ppm by weight. This preparative method also include preliminary addition of a portion of antioxidant to the starting polyoxyalkylene (A), for maintaining stability of the polyoxyalkylene during the production process; in which case, 1 to 200 ppm of antioxidant is first mixed into starting component (A). A buffer can also be used on an optional basis. The function of buffer is to also stabilize the polyoxyalkylene-modified organopolysiloxane. The buffer has a pH from 5.5 to 8 when dissolved in water. It is exemplified by sodium citrate, potassium citrate, sodium acetate, potassium acetate, sodium phosphate, potassium phosphate, sodium borate, and potassium borate. Because it is odor free and does not generate odor with the passage of time, the polyoxyalkylene-modified organopolysiloxane of our preparative method is well suited for use as a base oil for cosmetics. This invention is explained in greater detail below with reference to working examples. In the examples, % denotes weight percent and Me denotes methyl group. The peroxide value, total aldehyde plus ketone, and odor were measured as follows. Measurement of peroxide value A sample of approximately 1 g was weighed into a 200 ml Erlenmeyer flask equipped with a ground stopper. 10 ml of chloroform were added and the sample was completely dissolved. 15 ml of acetic acid were then added. Next, the flask was stoppered and thoroughly shaken. The entire flask was then wrapped in aluminum foil for protection from light, 2 ml of saturated methanolic potassium iodide solution was added, and the flask was held in the dark at ambient temperature for 30 minutes. This was followed by addition of 30 ml of distilled water, and transfer of the free iodine into the aqueous layer. Approximately 0.2 g of 10% starch solution was dripped in from a dropping pipette, and titration with N/100 sodium thiosulfate standard solution was then carried out until the aqueous layer became colorless. A blank test was run concurrently. The peroxide value was calculated from the equation: peroxide value (meq/kg) = (A - B) x F x 10 x (1/S) where: A is the number of milliliters of N/100 sodium thiosulfate standard solution consumed in the test on the sample; B is the number of milliliters of N/100 sodium thiosulfate standard solution consumed in the blank test; F is the titer of the N/100 sodium thiosulfate standard solution; and S is the polyoxyalkylene-modified organopolysiloxane sample size. Measurement of total content of aldehyde plus ketone 50 g of the sample were precisely weighed into a 100 ml beaker, and a solution of hydroxylamine hydrochloride (prepared by dissolving 50 g of hydroxylamine into 150 ml of pure water and bringing to 1 I with methanol), was added, using a whole pipette, followed by thorough mixing and later standing for 1 hour. After addition of 50 ml methanol with a graduated cylinder, potentiometric titration was performed using N/10 methanolic potassium hydroxide standard solution from Kanto™ Kagaku Kabushiki Kaisha. A blank test was run simultaneously. The total content of aldehyde plus ketone (ppm) was calculated from the equation: [(A - B) x F x 0.29]/S x 10,000 where A is the number of milliliters of N/10 methanolic potassium hydroxide standard solution consumed in the test on the sample; B is the number of milliliters of N/10 methanolic potassium hydroxide standard solution consumed in the blank test; F is the titer of the N/10 methanolic potassium hydroxide standard solution; and S is the polyoxyalkylene-modified organopolysiloxane sample size. Odor measurement Approximately 50 cm 3 samples were placed in each of six 100 cm 3 glass bottles, which were then held at quiescence for 2 hours in an oven at approximately 30°C. With one sample, an odor sensor (i.e., a metal oxide semiconductor sensor from Kalmor™ Company) was set in place as soon as the cap was opened, and the odor value was measured after 1 minute had elapsed. With the other 5 samples, the odor was organoleptically evaluated by 5 investigators immediately after opening the bottle. The results of this evaluation were scored on the following 4-level scale: + + + is almost odor-free, i.e., odor-free evaluation by at least 4 investigators; + + is slight odor, i.e., slight odor determined by no more than 3 investigators; + is odor present, i.e., odor found by five investigators although in varying degrees; and x is pungent odor. Example 1 Natural vitamin E obtained by extraction and abbreviated below as extracted natural vitamin E, sufficient to provide 200 ppm, was mixed into a polyoxyalkylene allyl ether having a peroxide value of 2 meq/kg, total aldehyde plus ketone of 5.3 ppm, and the formula CH 2 =CHCH 2 O(CH 2 CH 2 O) 12 H. 705 g of this polyoxyalkylene allyl ether, 295 g of methylhydrogenpolysiloxane with the average compositional formula: and 300 g isopropanol, were then mixed to homogeneity in a 2 l four-neck flask equipped with a reflux condenser and thermometer. After 1 ml of 2% isopropanolic chloroplatinic acid solution had been mixed to homogeneity into the mixture, a reaction was run for 4 hours under reflux. To eliminate unreacted Si-H, 100 g of ethanol were then added with heating under reflux for another 2 hours. This was followed by distillation under reduced pressure to a maximum attained temperature of 120°C, and then cooling to 40°C to give a reaction product 1. 20 g of purified water, 0.2 g of extracted natural vitamin E, and 5 g of a 2% methanolic sodium acetate solution were subsequently mixed into reaction product 1, which was then distilled under reduced pressure by heating to a maximum attained temperature of 110°C. Cooling afforded a reaction product 2. Reaction product 2 was purified by filtration to give a polyoxyalkylene-modified dimethylpolysiloxane. The peroxide value, total content of aldehyde plus ketone, and odor, were measured using a sample taken immediately after preparation, and on a sample that had been stored for 30 days in an oven at 50 ± 3 °C. These results are shown in Tables 1 and 2. Example 2 Extracted natural vitamin E sufficient to provide 200 ppm was mixed into a polyoxyalkylene allyl ether having a peroxide value of 2 meq/kg, total aldehyde plus ketone of 5.3 ppm, and the formula CH 2 =CHCH 2 O(CH 2 CH 2 O) 12 H. 275 g of this polyoxyalkylene allyl ether, 725 g of methylhydrogenpolysiloxane with the average compositional formula: and 300 g of isopropanol, were then mixed to homogeneity in a 2 l four-neck flask equipped with a reflux condenser and thermometer. After 1 ml of 2% isopropanolic chloroplatinic acid solution had been mixed to homogeneity into the mixture, a reaction was run for 4 hours under reflux. To eliminate unreacted Si-H, 100 g of ethanol were then added with heating under reflux for another 2 hours. This was followed by distillation under reduced pressure to a maximum attained temperature of 120°C, and then cooling to 40°C, to provide reaction product 1. 20 g of purified water, 0.2 g of extracted natural vitamin E, and 5 g of a 2% methanolic sodium acetate solution, were subsequently mixed into reaction product 1, which was then distilled under reduced pressure by heating to a maximum attained temperature of 110°C. Cooling afforded a reaction product 2. Reaction product 2 was purified by filtration to give a polyoxyalkylene-modified dimethylpolysiloxane. The peroxide value, total content of aldehyde plus ketone, and odor, were measured on a sample taken immediately after preparation, and on a sample that had been stored for 30 days in an oven at 50 ± 3 °C. The results are shown in Tables 1 and 2. Example 3 Extracted natural vitamin E sufficient to provide 200 ppm, was mixed into a polyoxyalkylene allyl ether having a peroxide value of 2 meq/kg, total aldehyde plus ketone of 5.3 ppm, and the formula CH 2 =CHCH 2 O(CH 2 CH 2 O) 12 H. This polyoxyalkylene allyl ether, 236 g of methylhydrogenpolysiloxane with the average compositional formula: and 764 g of isopropanol, were then mixed to homogeneity in a 2 I four-neck flask equipped with a reflux condenser and thermometer. After 1 ml of 2% isopropanolic chloroplatinic acid solution had been mixed to homogeneity into the mixture, a reaction was run for 4 hours under reflux. To eliminate unreacted Si-H, 100 g of ethanol were then added with heating under reflux for another 2 hours. This was followed by distillation under reduced pressure to a maximum attained temperature of 120°C, and then cooling to 40°C, to provide a reaction product 1. 20 g of purified water, 0.2 g of extracted natural vitamin E, and 5 g of a 2% methanolic sodium acetate solution, were subsequently mixed into reaction product 1, which was then distilled under reduced pressure by heating to a maximum attained temperature of 110°C. Cooling afforded a reaction product 2. Reaction product 2 was purified by filtration to provide a polyoxyalkylene-modified dimethylpolysiloxane. The peroxide value, total content of aldehyde plus ketone, and odor, were measured on a sample taken immediately after preparation, and on a sample that had been stored for 30 days in an oven at 50 ± 3 °C. These results are shown in Tables 1 and 2. Comparative Example 1 A polyoxyalkylene-modified dimethylpolysiloxane was prepared as in Example 1, but without addition of extracted natural vitamin E to reaction product 1. The properties of the resulting polyoxyalkylene-modified dimethylpolysiloxane were measured as in Example 1, and the results are shown in Tables 1 and 2. Comparative Example 2 A polyoxyalkylene-modified dimethylpolysiloxane was prepared as in Example 1, but neither extracted natural vitamin E nor the 2% methanolic sodium acetate solution were added to reaction product 1. The properties of the resulting polyoxyalkylene-modified dimethylpolysiloxane were measured as in Example 1, and the results are shown in Tables 1 and 2. Comparative Example 3 A polyoxyalkylene-modified dimethylpolysiloxane was prepared as in Example 1, but neither extracted natural vitamin E nor the 2% methanolic sodium acetate solution were added anywhere in the process. The properties of the resulting polyoxyalkylene-modified dimethylpolysiloxane were measured as in Example 1, and the results are shown in Tables 1 and 2. Results of evaluation immediately after preparation peroxide value total aldehyde plus ketone odor (sensor) odor (organoleptic) Example 1 1.8 3.0 220 + + + Example 2 0.8 2.4 170 + + + Example 3 1.5 10.5 280 + + Comparative Example 1 5.0 20.0 360 + + Comparative Example 2 5.8 23.0 350 + + Comparative Example 3 10.0 56.0 700 + Results of evaluation after holding for 30 days at 50 ± 3 °C peroxide value total aldehyde plus ketone odor (sensor) odor (organoleptic) Example 1 2.0 6.5 210 + + + Example 2 0.8 2.8 180 + + + Example 3 2.5 13.5 295 + + Comparative Example 1 8.0 30.0 460 + +/+ Comparative Example 2 15.8 80.0 550 + +/+ Comparative Example 3 21.0 300.3 1250 x The polyoxyalkylene-modified organopolysiloxane prepared by the method of this invention is odor-free. In particular, it generates almost no odor with elapsed time, since (i) it contains 5-1,000 ppm by weight of an antioxidant, (ii) it has a peroxide value not exceeding 5 meq/kg, and (iii) it has a total content of aldehyde plus ketone not exceeding 100 ppm. Moreover, our preparative method has an ability to produce such organopolysiloxanes in a highly efficient manner.

Claims: A method for preparing a product comprising an organopolysiloxane bearing polyoxyalkylene bonded to silicon across alkylene comprising (i) conducting a hydrosilylation reaction in (D) an organic solvent between (A) a polyoxyalkylene bearing alkenyl at a single terminal and having a peroxide value not exceeding 3 meq/kg, and a total content of aldehyde plus ketone not exceeding 100 ppm by weight; (B) an organohydrogenpolysiloxane that contains at least one silicon-bonded hydrogen atom in the molecule; in the presence of (C) a platinum catalyst and in presence of 1-200 ppm of an antioxidant; (ii) removing the organic solvent under reduced pressure; (iii) blending in an amount of water equivalent to at least one weight percent of the total amount of components (A) and (B) ; (iv) eliminating the water under reduced pressure; and (v) thereafter adding 4-800 ppm of an antioxidant. Method of claim 1 further comprising adding 1-500 ppm of a buffer having a pH of 5.5-8 when dissolved in water in step (v). A method according to Claim 1 wherein the polyoxyalkylene bearing alkenyl at a single terminal has the formula LO(C p H 2p O) x R 3 where L is alkenyl; R 3 is hydrogen atom, a C 1 -C 6 alkyl group, or an acyl group; p is 2-4; and x is 1-100. A method according to Claim 3 wherein component (B) has the formula where R 1 is a monovalent hydrocarbon group; k is zero or a positive integer; l is zero or a positive integer; and B is R 1 or hydrogen. A method according to Claim 4 wherein the organic solvent is ethanol, isopropyl alcohol, toluene, or xylene. A method according to Claim 2 wherein the buffer is sodium citrate, potassium citrate, sodium acetate, potassium acetate, sodium phosphate, potassium phosphate, sodium borate, or potassium borate.

Inventors: HARASHIMA ASAO, HARASHIMA, ASAO, Harashima, Asao, Dow Corning Toray Sil. Co., Ltd.
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE CO., LTD.
Application year: 1996
Main classification: C08G77
IPC codes: C08L71, C08G65, C08G77, C08L83, C08K5, C08K3