FIRE-RETARDANT ADHESIVE THERMOPLASTIC FILM

Abstract: A fire-retardant thermoplastic film having a water-based pressure-sensitive adhesive. Liquid thermoplastic resin is mixed with a fire-retardant material, then subjected to a blow molding process to form a film. An adhesive is then applied to one side of the film. The film is used for protecting various surfaces in the maritime industry during construction.

Description: FIRE RETAROANT ADHESIVE THERMOPLASTIC FILM Field of the Invention The present invention relates to fire-retardant protective coverings. More particularly, the invention relates to fire-retardant thermoplastic film and its use in protecting surfaces in the maritime industry. Background of the Invention During construction aboard ships, it is necessary to protect various surfaces from damage caused by workers' activities such as construction, painting, refit, new build, maintenance and repair. Surfaces requiring such protection include carpet, glass, decks, tile, flooring, fiberglass and bulkheads. Current methods of temporarily protecting such surfaces include the use of drop cloths, tarps, polycarbonate sheeting and polyethylene sheeting with pressure sensitive adhesive (AMERICOVER CARPET COVER '" , Maritime Resource Group, San Diego, CA; Carpet Mask, Poly-Tak Protection Systems, Huntington Beach, CA). Fire safety is increasingly recognized as being important aboard ships and in many other industries, especially during building and construction. These are particularly dangerous periods because the chance of fire is significantly increased during these activities. Fires are particularly life threatening aboard a ship. Although some ship owners require that such materials be fire-retardant, no laws exist in the United States or Europe requiring such protective materials to be fire retardant in the maritime industries. Fire-retardant materials currently used as temporary protective coverings include non-adhesive fire- retardant 10-30 mil polyvinyl chloride (PVC) or polyethylene film (COVERGUARD " , Bainbridge Aquabatten, Canton, MA; MEGA FILM", Mega Film Ltd., Berkshire, U.K.), fire-retardant plywood, door skins, herculite, bergboard and foil paper. Each of these materials must be taped in place, a cumbersome, time-consuming process considering the typical areas on a ship which must be covered prior to construction activity and the area shapes and sizes aboard a ship to be protected. Because commercial ships are rarely out of commission for more than 15 days during a wet or dry dock, the time taken to protect surfaces before work can commence is critical. Moreover, the majority of these materials are fairly expensive. In addition to the maritime industries, there are numerous other situations in which protective coverings can advantageously be applied to surfaces. Those situations include conventional building construction and renovation, aircraft repairs, painting, automobile maintenance, and the like. Although the need for fire retardant properties in such coverings has not been well realized in the prior art, such properties provide a significant advantage. Thus, there is a need for an easy-to-install, effective, inexpensive temporary fire-retardant protective covering for ship surfaces and other surfaces. The present invention satisfies this need. Summary of the Invention One embodiment of the present invention is a temporary surface protectant comprising a thermoplastic film containing a fire-retardant material, said film having a releasable, pressure sensitive adhesive on one of its sides. Advantageous adhesives include water-based adhesives, such as water-based emulsions. Preferably, the thermoplastic film comprises polyvinyl chloride, nylon, polyethylene, polyolefin or polycarboπate; more preferably, the polymer is polyethylene; most preferably, the polyethylene is a blend of about 70% linear low density polyethylene and about 30% low density polyethylene. According to another aspect of this preferred embodiment, the surface is carpet, glass, fiberglass, stainless steel, bulkheads, soft panels, furnishings or marble. Advantageously, the surface is carpet. Preferably, the thermoplastic film has a thickness of between about 0.5 and about 30 mils; more preferably, the thermoplastic film has a thickness between about 6 and about 10 mils; most preferably, the thermoplastic film has a thickness of about 8 mils. In another aspect of this preferred embodiment, the thermoplastic film has a thickness of between about 2 and about 4 mils; more preferably about 3 mils. Advantageously, the fire retardant material comprises an acrylic emulsion or antimony oxide and the adhesive is an acrylic adhesive. Preferably, the covering is used for up to about 45 days. Another embodiment of the invention is a method for protecting a surface, comprising applying to the surface a thermoplastic film containing a fire-retardant material, the thermoplastic film having a pressure- sensitive adhesive on one of its sides. According to one aspect of this preferred embodiment, the adhesive is water-based. Preferably, the thermoplastic film comprises polyvinyl chloride, nylon, polyethylene, polyolefin or polycarbonate; more preferably, the polymer is polyethylene; most preferably, the polyethylene is a blend of about 70% linear low density polyethylene and about 30% low density polyethylene. According to another aspect of this preferred embodiment, the surface is carpet, glass, fiberglass, stainless steel, bulkheads, soft panels, furnishings or marble. One example of such a surface is carpet. Preferably, the thermoplastic film has a thickness of between about 0.5 and about 25 mils; more preferably, the thermoplastic film has a thickness between about 6 and about 10 mils; most preferably, the thermoplastic film has a thickness of about 8 mils. In another aspect of this preferred embodiment, the thermoplastic film has a thickness of between about 2 and about 4 mils; more preferably about 3 mils. Advantageously, the fire retardant material comprises antimony oxide and the adhesive is an acrylic adhesive. Preferably, the covering is used for up to about 45 days. Detailed Description of the Preferred Embodiments The present invention provides temporary protective thermoplastic films containing a fire-retardant material. A water-based pressure sensitive releasable adhesive is applied to one side of the thermoplastic film. The films may be used as protective coverings for up to about 45 days without transfer of the adhesive to the surface onto which the films are placed. The adhesive is applied to one side of the film and the film is reverse rolled, with or without a release coating or release paper, allowing the film to be rolled onto a desired surface quickly and easily. The thermoplastic films of the invention are effective, fire safe, and easy to install and remove. Traditional protective coverings must be cut and taped into place, a time-consuming and labor-intensive process. Furthermore, tape rarely provides satisfactory adhesion and thus will not hold up well to construction activities. Moreover, constant touch-up repairs are necessary and there is a trip hazard associated with shifted or damaged floor coverings. In contrast, the film of the present invention will remain adhered to the surface and will not present such a hazard. The instant films leave no residue when removed, compared to conventional duct tape used to secure other temporary protective coverings which leaves a difficult to remove residue on almost every surface. The films of the invention can be installed and removed, on average, in less than 50% of the time necessary to install and remove traditional forms of temporary protection. As used herein, the term "thermoplastic" refers to a high polymer that softens when exposed to heat and returns to its original condition when cooled to room temperature. Many such materials are known in the art and are contemplated for use in the present invention, including polyvinyl chloride (PVC), nylons, fluorocarboπs, low density polyethylene, linear low density polyethylene, linear high density polyethylene, polyurethane prepolymer, polystyrene, polypropylene, polycarbonate, polyethylene terephthalate, ethylene vinyl acetate, polyolefins, cellulosic resins, acrylic resins and copolymers, block copolymers, blends, and mixtures thereof. A blend of about 70% linear low density polyethylene and about 30% low density polyethylene is particularly preferred for use in the present invention. In a preferred embodiment, the thermoplastic films of the invention have thicknesses of between about 0.5 mils and about 25 mils. The determination of which thickness to use will depend on the particular application desired. For example, in carpet and glass protection, the film can have a thickness between about 2 and about 4 mils. In a particularly preferred embodiment, the film has a thickness of about 3 mils. For glass protection from harsher construction activities including painting, sandblasting and welding operations, it is preferred that the thickness be between about 6 and about 10 mils, most preferably about 8 mils. The films of the invention range in width from about 6 to about 96 inches and in length from about 50 to about 3000 feet. Of course, the films may be cut to fit any particular area. Nonlimitiπg examples of surfaces contemplated for protection by the films of the invention include carpets, decks, furniture, soft panels, floors, bulkheads, marble, cultured marble, mirrors, glass, plexigias, stainless steel, aluminum, high and low pressure laminates and fiberglass. Many fire-retardant agents may be used to form the films of the present invention. As defined herein, a fire retardant is a substance applied to or incorporated in a combustible material to reduce or eliminate its tendency to ignite when exposed to a low-energy flame such as a match or cigarette. The term "fire-retardant" is intended to include single fire-retardant agents or combinations thereof. The fire retardant may be applied to the thermoplastic film as a coating or surface finish. Alternatively, the fire retardant may be applied in the form of a solution or may be blended with the liquid polymer prior to formation of the thermoplastic film. The amount of fire retardant added to the polymer will vary depending on the degree of protection required, although the amount added typically ranges from about 0.01 % to about 30; preferably from about 0.1 % to about 10% or about 1% to about 5%; and most preferably about 2.5%. Fire-retardaπts contemplated for use in the invention include inorganic fire retardants such as ammonium sulfamate, zinc borate, antimony oxide, antimony oxychloride ammonium bromide, hydrated aluminum oxide, phosphonitriiic chloride; and organic fire retardants such as halogenated organic fire retardants (i.e., brominated alkoxydiphenyl sulfone, chlorendic anhydride, chlorinated paraffins, halogenated organic polyphosphonate); vinyl acetate; vinyl chloride and acrylic emulsions (i.e. methyl methacrylate); alkyl diaryl phosphate; cresyl diphenyl phosphate, octyl diphenyl phosphate, trialkyi boron ester; tris (dichloropropyl) phosphate; phosphonate esters and tricresyl phosphate. The various phosphate and antimony oxide formulations are particularly preferred. The carpet used on cruise ships is tested to C.F.R. 1630 standards. Accordingly, the thermoplastic film of the invention will also meet or exceed this government standard. The fire-retardant thermoplastic films of the invention for use in the U.S. Military will also meet Federal GSA Standard 191 Method 5903 for fire retardant material. The pressure-sensitive adhesives of the invention vary in tack from 0.5 oz. to 30 oz. per inch to provide adequate adhesion and release from various surfaces without depositing adhesive residue thereon. Preferred adhesives contemplated for use in the invention include water-based emulsions. Exemplary preferred materials are acrylic adhesives (i.e., vinyl acetate 2-ethylhexyl copolymer; FLEXCRYL" GP-5 acrylic adhesive (Air Products, Allentown, PA)). Other suitable adhesives include blends of polyvinyl acetate and polyethylene emulsions (U.S. Patent No. 4,833,132), Type 33-4030 water-based pressure sensitive emulsion (National Starch and Chemical Corp., Bridgewater, NJ) and AQUALOCK™ 8002 brand adhesive (B.F. Goodrich, Adhesive Systems Division, Akron, OH). However, any releasable adhesive having these properties is contemplated for use in the invention. The use of solvent-based pressure sensitive adhesives is also contemplated. These adhesives are solubilized in an organic solvent which is allowed to evaporate after application of the solution. One example of such an adhesive is polyurethane. However, many such adhesives are known to one of ordinary skill in the art. Cross-linkers, tackifiers, detackifiers and other conventional additives may also be incorporated into the adhesive to promote or reduce pressure sensitive qualities, in accordance with manufacturer's instructions or conventional industry practices. The fire retardant material can be incorporated into the adhesive, into the film, or both. The adhesives may be applied to the thermoplastic film by any conventional method, such as by brushing, flow brushing, dipping, manual glue gun, simple roller, flow roller, spraying or roll coating. Alternatively, a sheet having release properties may be coated with adhesive, which is then transferred to the film, as by rolling the coated sheet and the film together. The films of the present invention are typically formed by conventional blown film extrusion. This process involves melting thermoplastic resin pellets or powder to produce a thermoplastic liquid, extruding the liquid through a cylindrical die, and blowing cooling air into the interior of the resulting tubular extrusion to expand and cool the film. The film is subsequently slit and rolled. In an alternative embodiment, the film may be formed by flat sheet extrusion, a process in which a liquid thermoplastic dispersion is forced through a metal forming die, followed by cooling or chemical hardening. Film is made by passing a low-viscosity mixture through a narrow slit. Details of these conventional film manufacturing processes are described, for example, in U.S. Patent Nos. 5,186,782, 4,626,397, 4,683,094 and 5,204,032, the entire contents of which are hereby incorporated by reference. A representative example of preparation of a film of the present invention is provided below. Example 1 Polyolefin pellets are melted and mixed with 2.5% antimony oxide. The mixture is blow molded into a film, allowed to dry and cut into sheets. One surface of the film is sprayed with vinyl acetate 2-ethylhexyl copoiymer and the adhesive is allowed to dry. The film is then reverse rolled and applied to a desired surface.

Claims: WHAT IS CLAIMED IS: 1. A temporary surface protectant comprising a thermoplastic film containing a fire-retardant material, said film having a pressure-sensitive adhesive on one of its sides. 2. The protectant of Claim 1, wherein said thermoplastic film comprises a polymer selected from the group consisting of polyvinyl chloride, nylon, polyethylene, polyolefin and polycarbonate. 3. The protectant of Claim 2, wherein said polymer is polyethylene. 4. The protectant of Claim 3, wherein said polyethylene comprises a blend of about 70% linear low density polyethylene and about 30% low density polyethylene. 5. The protectant of Claim 1, wherein said thermoplastic film has a thickness of between about 0.5 and about 30 mils. 6. The protectant of Claim 5, wherein said thermoplastic film has a thickness between about 6 and about 10 mils. 7. The protectant of Claim 6, wherein said thermoplastic film has a thickness of about 8 mils. 8. The protectant of Claim 5, wherein said thermoplastic film has a thickness of between about 2 and about 4 mils. 9. The protectant of Claim 8, wherein said thermoplastic film has a thickness of about 3 mils. 10. The protectant of Claim 1, wherein said fire-retardant material comprises an acrylic emulsion or antimony oxide. 1 1. The protectant of Claim 1, wherein said adhesive is a water-based adhesive. 12. The protectant of Claim 11, wherein said water-based adhesive is an acrylic adhesive. 13. A method of temporarily protecting a surface, comprising applying to said surface a thermoplastic film containing a fire-retardant material, said thermoplastic film having a water-based pressure- sensitive adhesive on one of its sides. 14. The method of Claim 13, wherein said surface is selected from the group consisting of carpet, glass, fiberglass, stainless steel, soft panels, furnishings and marble. 15. The method of Claim 14, wherein said surface is carpet. 16. The method of Claim 13, wherein said thermoplastic film comprises a polymer selected from the group consisting of polyvinyl chloride, nylon, polyethylene, polyolefin and polycarbonate. 17. The method of Claim 16, wherein said polymer is polyethylene. 18. The method of Claim 17, wherein said polyethylene comprises a blend of about 70% linear low density polyethylene and about 30% low density polyethylene. 19. The method of Claim 13, wherein said thermoplastic film has a thickness of between about 0.5 and about 30 mils. 20. The method of Claim 19, wherein said thermoplastic film has a thickness between about 6 and about 10 mils. 21. The method of Claim 20, wherein said thermoplastic film has a thickness of about 8 mils. 22. The method of Claim 19, wherein said thermoplastic film has a thickness of between about and about 4 mils. 23. The method of Claim 22, wherein said thermoplastic film has a thickness of about 3 mils. 24. The method of Claim 13, wherein said fire-retardant material comprises antimony oxide. 25. The method of Claim 13, wherein said adhesive is a water-based adhesive. 26. The method of Claim 25, wherein said water-based adhesive is an acrylic adhesive. 27. The method of Claim 13, wherein said covering is used for up to about 45 days. AMENDED CLAIMS [received by the International Bureau on 24 September 1996 (24.09.96) ; original claims 1 and 13 amended; remaining claims unchanged (2 pages) ] 1. A temporary protectant for a surface within a living area comprising a thermoplastic film having a fire-retardant material incorporated directly therein, said film having a pressure-sensitive releasable adhesive on one of its sides that leaves substantially no adhesive residue upon removal of the protectant from a living area surface. 2. The protectant of Claim 1, wherein said thermoplastic film comprises a polymer selected from the group consisting of polyvinyl chloride, nylon, polyethylene, polyolefin and polycarbonate. 3. The protectant of Claim 2, wherein said polymer is polyethylene. 4. The protectant of Claim 3, wherein said polyethylene comprises a blend of about 70% linear low density polyethylene and about 30% low density polyethylene. 5. The protectant of Claim 1, wherein said thermoplastic film has a thickness of between about 0.5 and about 30 mils. 6. The protectant of Claim 5, wherein said thermoplastic film has a thickness between about 6 and about 10 mils. 7. The protectant of Claim 6, wherein said thermoplastic film has a thickness of about 8 mils. 8. The protectant of Claim 5, wherein said thermoplastic film has a thickness of between about 2 and about 4 mils. 9. The protectant of Claim 8, wherein said thermoplastic film has a thickness of about 3 mils. 10. The protectant of Claim 1, wherein said fire-retardant material comprises an acrylic emulsion or antimony oxide. 11. The protectant of Claim 1, wherein said adhesive is a water-based adhesive. 12. The protectant of Claim 11, wherein said water-based adhesive is an acrylic adhesive. 13. A method of temporarily protecting a living area surface, comprising applying to said surface a thermoplastic film containing a fire-retardant material incorporated directly therein, said thermoplastic film having a water-based pressure-sensitive adhesive on one of its sides. 14. The method of Claim 13, wherein said surface is selected from the group consisting of carpet, glass, fiberglass, stainless steel, soft panels, furnishings and marble. 15. The method of Claim 14, wherein said surface is carpet. 16. The method of Claim 13, wherein said thermoplastic film comprises a polymer selected from the group consisting of polyvinyl chloride, nylon, polyethylene, polyolefin and polycarbonate. 17. The protectant of Claim 16, wherein said polymer is polyethylene. 18. The protectant of Claim 17, wherein said polyethylene comprises a blend of about 70% linear low density polyethylene and about 30% low density polyethylene. 19. The protectant of Claim 13, wherein said thermoplastic film has a thickness of between about 0.5 and about 30 mils. 20. The protectant of Claim 19, wherein said thermoplastic film has a thickness between about 6 and about 10 mils. 21. The protectant of Claim 20, wherein said thermoplastic film has a thickness of about 8 mils. 22. The protectant of Claim 19, wherein said thermoplastic film has a thickness of between about 2 and about 4 mils. 23. The protectant of Claim 22, wherein said thermoplastic film has a thickness of about 3 mils 24. The method of Claim 13, wherein said fire-retardant material comprises antimony oxide. 25. The method of Claim 13, wherein said adhesive is a water-based adhesive 26. The method of Claim 25, wherein said water-based adhesive is an acrylic adhesive. 27. The method of Claim 13, wherein said covering is used for up to about 45 days. NSB-37Ϊ7 STATEMENT UNDER ARTICLE 19 The claims as amended recite that the pressure-sensitive adhesive is releasable. Because of this releasability, the protectant will not leave residue on the surfaces to which it is temporarily applied. The patents cited in the search report neither disclose nor suggest this concept. These references only relate to permanent application of thermoplastic films.

Inventors: HINSLEY CONRAD L JR, RIEDEL TEVAN A, HINSLEY, CONRAD, L., JR., RIEDEL, TEVAN, A.
Applicants: HINSLEY CONRAD L JR, RIEDEL TEVAN A, HINSLEY, CONRAD, L., JR., RIEDEL, TEVAN, A.
Application year: 1996
Main classification: C09J7
IPC codes: B08B17, C09J7