Planar isolation in integrated circuits

Abstract: The invention provides a method for producing an isolation region on a surface of a semiconductor substrate comprising the steps of: forming and patterning a masking layer; forming an isolating layer so that a notch exists between an edge of the masking layer and the upper surface of the isolating layer; forming a filling layer over the masking layer and the isolating layer, so that it completely fills the notch; forming field protection spacers adjacent to the masking layer; partially removing the filling layer to expose the upper surface of the isolation layer, the notch remaining filled with a part of the filling layer; and partially removing the isolating layer from its upper limit until this upper limit is substantially coplanar with the upper surface of the semiconductor substrate.

Description: The invention relates to a method for manufacturing semiconductor integrated circuits; more particularly to a method for forming isolation regions in a semiconductor substrate between regions containing active circuitry. Figure 1 shows a well known method for forming an isolation region in a semiconductor substrate. In figure 1A, a semiconductor substrate 10, such as monocrystalline silicon, is covered with a first buffer layer 12, such as a 12nm thick layer of silicon oxide. This covering is typically performed by heating the substrate in a dry, oxygen containing atmosphere. A second buffer layer 14 is deposited above this first buffer layer. This may be a 50nm thick polycrystalline or amorphous silicon layer. A masking layer 16 is deposited over the second buffer layer. This masking layer may be a 160nm thick layer of silicon nitride. The layers 14, 16 are deposited by chemical vapour deposition or any other suitable technique. In figure 1B, a photographic step followed by an etch has removed the masking layer 16 and the second buffer layer 14 from a selected region 18, which is the field region. The region 20 which remains covered with the masking and second buffer layers is the active region. In figure 1C, the structure is heated in an oxidising atmosphere of hydrogen and oxygen gases at a temperature of 900 to 1100°C for a controlled time period, to grow a silicon dioxide isolating layer 22 of field oxide to a desired thickness t 1 , typically in the range 500 to 600nm. In an intermediate region 23, between the active region and the field region, the field oxide 22 penetrates under the masking layer 16, consuming part of the second buffer layer 14, to form a "bird's beak" of field oxide. A notch 26 is formed between the tapering surface of the field oxide 22 and the masking layer 16. The bird's beak reduces the effective size of the active region, but does not provide an area of acceptable isolation. It is of limited use, and often regarded as wasted space. During the oxidation step, a thin native oxide is formed over the masking layer 16. This needs to be removed with an etching step, such as a dip in dilute hydrofluoric acid. As a side effect, some of the field oxide 22 is removed, and now has a thickness of t 2 . The etch causes a hollow 23a to be etched in the surface of the field oxide. In figure 1D, an isotropic etch step has been used to remove the masking layer. Such an etch may be performed using phosphoric acid to remove a silicon nitride masking layer 16. In figure 1E, the second buffer layer has been removed by a further isotropic etch step, to expose the first buffer layer 12. A suitable plasma etch may be performed to remove a polycrystalline or amorphous silicon layer. In figure 1F, an upper surface 24 of the semiconductor substrate 10 has been exposed by removing the first buffer layer 12, and with it, some of the field oxide 22. This etch may be performed using dilute hydrofluoric acid to remove a silicon dioxide first buffer layer. The etch may be carried out for a time long enough to etch 30nm of silicon dioxide. This ensures that all of the first buffer layer is removed, but also 30nm of field oxide. This field oxide then has a thickness t 3 , somewhat less than half of which lies above the upper surface 24 of the semiconductor substrate. There is thus a difference in height of almost 1/2t 3 between the upper surface of the semiconductor substrate and the upper surface of the field oxide. A sacrificial layer of silicon dioxide is then grown, typically to a thickness of between 10nm and 80nm, over the upper surface 24 of the semiconductor substrate, by heating the substrate 10 in a dry, oxygen containing environment, and is later etched away. This serves to clean the upper surface 24. Figure 2 reproduces a photograph of a cross section of a structure according to the described process. A wide field oxide region 22 is shown. The field oxide thickness t 3 may typically be 450 to 550nm, giving a difference in height d between the active region and the field region of about 200nm. The hollow 23a is present in the upper surface of the field oxide layer. The position of this hollow approximately corresponds to the position of an edge of the masking layer 16. It is typically separated from the interface between the field oxide and the upper surface 24 of the substrate by a distance s of about 160nm. At the lowest point of this hollow, the thickness h of the field oxide is about 160nm. A minimum width field region 25a of width wf equal to the minimum width allowed in the process (about 700nm) is also shown. It is separated from the first field region 22 by an active region of minimum width wa , such as 400nm. The minimum width field region 25a has a height above the upper surface 24 of the substrate somewhat less than d. A later deposited layer 25b, has an upper surface 25c, which is very uneven, due to the heights of the field regions below. Highly planar isolation techniques are needed in current and future integrated circuit fabrication processes. The raised surfaces of field oxide regions in the known process described above cause problems with the control of transistor gate lengths when these gate lengths are inferior to 0.6µm. Current production of processes with a minimum feature size of 0.5µm and development of processes with a minimum feature size of 0.35µm, the minimum feature size often being used to define transistor gate lengths is impeded by problems caused by reflection of light from slanted edges of the field oxide during the photographic definition of the transistor gate features. In later steps of the process, referring again to figure 1F, a gate insulator layer, such as a 10nm layer of silicon dioxide, is deposited on the upper surface 24 and the field oxide 22. A conductive layer, such as polycrystalline silicon is then deposited over this gate insulator layer. A photolithography step defines transistor gate electrodes. The definition of the gate electrodes is hindered by the reflection of light from slanting edges of the field oxide. This may cause the final gate electrode to be shorter than desired, as the reflected light may act to expose the edges of the photoresist under opaque portions of the mask. The effect varies with distance from the interface region 23. The gate lengths produced may vary by as much as 0.1µm. This represents an intolerable variation for gate lengths of 0.5µm or less. To overcome the problem, the masks used define gate lengths 0.1µm longer than necessary, meaning that transistor gates far from the field regions will have gate lengths longer than necessary, and the potential speed and current capabilities will not be achieved. Variations in the transistor gate lengths also lead to variations in several important transistor parameters, such as on-state saturation current, off-state leakage current and channel breakdown or punchthrough voltage. The difference in height between the active and field regions could cause some defocusing effects in one region due to the limited depth of focus of the photographic step, and step coverage problems in later deposited conductive layers. During formation of transistors in the semiconductor substrate, spacers are formed on the gate electrode. The difference in height between active and field regions may cause parasitic spacers to be formed on the slanting edges of the field oxide, which later cause problems with interconnect lines running over field regions to connect different active regions together. Later deposited layers, such as polycrystalline silicon interconnect, metal interconnect and photoresist layers at each masking step are thinner at the point that they cross the intermediate region 23, due to step coverage problems. For all of these reasons, it is wished to be able to produce a semiconductor substrate with isolating field regions that are coplanar with the upper surface of the semiconductor substrate. Several techniques are known for achieving a field isolation region which is relatively coplanar with the upper surface of the semiconductor substrate. A "double field oxidation", process exists, whereby field 18 and active 20 regions are defined as shown in figures 1A, 1B. A first oxidation step takes place, similarly to that shown in figure 1C. This first field oxide is then completely etched away, leaving the field region with a recess in the semiconductor surface to a depth of about 1/2t 1 below the upper surface 24 of the semiconductor substrate. A second oxidation step is then performed. If a second oxide of thickness t 1 is formed, the upper surface of this oxide will be approximately coplanar with the upper surface 24 of the semiconductor substrate. This process causes the extension of the bird's beak. As two oxidation process steps are performed, the beak is twice the length of the beak formed in processes using only one oxidation step. This process requires a large number of process steps. The processing time is raised by the need for two oxidation steps, at 5 or 6 hours each. A large "bird's head" is formed, by the deformation of the birds head over the edge of the recess, reducing the planarity achieved, and making formation of later deposited, overlying layers more difficult. The problem of the raised field oxide surface may also be treated by introducing an etchback or polishing step, after the formation of the field oxide 22. Figures 3A to 3C show a sequence of process steps illustrating the etchback technique. Features common to figure 1 have identical reference labels. In figure 3A, a field oxide 22 is formed to a thickness t 1 in the field region 18, according to the process of figures 1A to 1C. A notch 26 is present between the edge of the masking layer 16 and the upper surface of the field oxide 22. In the region of this notch, the thickness of the field oxide is reducing, as the "bird's beak" begins. A selective etch step is then used to remove some of the field oxide from its upper surface until this upper surface is only slightly higher than the upper surface 24 of the semiconductor substrate. Figure 3B shows the oxide, etched to have a thickness of t 4 . This etch step, however, causes a gap 28 to be formed under the masking and second buffer layers, exposing a part of the semiconductor substrate 10. In figure 3C, the layers 16, 14 have been removed by selective etching. The first buffer layer 12 has also been removed, to expose the upper surface 24 of the semiconductor substrate 10. Some or all of these etch steps have the effect of also reducing the thickness of the field oxide. At the end of the process, the upper surface of the field oxide is at a height d above the upper surface of the semiconductor substrate 10. Figure 4 reproduces a photograph of a cross section of a structure according to this process. The total field oxide thickness t 4 may typically be 300 to 400nm. The difference in height d between the active region and the field region when produced according to this process is about 100nm. The gap 28 is present. It is a more extreme form of the hollow 25 discussed earlier. This is caused by the etching step applied to the field oxide being active for longer on exposed parts of the field oxide than on parts which were covered by masking layer 16 or second buffer layer 14. In the diagram, the gap is shown as not exposing an edge of the active region, but a thin region 28a of field oxide remains. This is, however, difficult to control and edges of the active region are often exposed. At the lowest point of the surface of the field oxide, in this gap, the thickness h of the field oxide is about 80nm. This lowest point is separated from the edge of the active area by a distance s of about 0.15 to 0.2µm, typically 0.16µm. Again, a minimum width field region 25a of width wf equal to the minimum width allowed in the process is also shown. This field region has a height above the substrate surface 24 somewhat less than d . A later deposited layer 25b, has an upper surface 25c. This upper surface is more planar than that of the previous process, shown in figure 2, as the field region 22 is more nearly coplanar with the surface 24 of the substrate. The gap 28 and the thin or missing portion 28a of field oxide, which are introduced by the use of this etchback process, introduce unacceptable electrical problems. They cause a defectivity site at the edge of the active region. This causes defects in a later formed gate oxide and allows current leakage paths in the final circuit. A similar, but alternative method involves forming a field oxide as in figure 3A, then subjecting the structure to a chemical-mechanical polishing (CMP) step, to planarise the field oxide with the active region, and remove the barrier layers. Such a CMP step must be controlled to stop on the surface 24 of the semiconductor substrate, which is difficult in the case of a silicon substrate, as silicon of the substrate 10 will be polished faster than the field oxide 22. The introduction of a polishing step into a process is time consuming and complicated. In either of these two processes, spacers may be formed on the masking layer 16, which then separates the field oxide formation from the masking and buffer layers, and reduces the length of the bird's beak under the masking layer 16. This has no effect on the planarity of the final structure. Figures 5A to 5D show this process variant. In figure 5A, after the definition of the field region 18 and the active region 20, a layer 30 of spacer material, such as silicon nitride, is deposited over the surface of the structure. This layer is then etched, to leave a spacer, 32, as shown in figure 5B. The field region is then oxidised, figure 5C, to form a field oxide 22 having a thickness t 1 , typically 500 to 600nm. As the bird's beak formed in this oxidation penetrates under the spacer 32 as well as under the masking layer 16, the length of the bird's beak under the masking layer is reduced by the width of the spacer 32. As shown in figure 5D, the field oxide 22 and the spacer 32 may be etched to improve planarity, but the problem of the gap 28 remains. The remaining thickness t 4 of field isolation still protrudes significantly above the upper surface 24 of the semiconductor substrate. The 1987 Symposium on VLSI Technology Digest of Technical Papers May 18-21, 1987, at pages 19-20 describes a process for forming a relatively planar isolation region. According to that process 200 nm of oxide is deposited prior to planarisation to fill the moats at the edges of the stack. The field oxide and the stack are etched back simultaneously by RIE. Other techniques are known, which aim to improve the planarity of the isolation area whilst eliminating or reducing the length of the bird's beak. For example, a cavity may be etched in the surface of the semiconductor, which is then filled with a deposited isolating material. This deposited isolating material is then etched or polished to be coplanar with the upper surface of the semiconductor. This however is a complex process, and the isolating material (commonly silicon dioxide) deposited is often of a relatively poor quality, containing impurities, and having a low dielectric strength. In current and future semiconductor fabrication techniques, the control of the length of transistor gate electrodes is more important than the space savings that could be made by the reduction in the length of the bird's beak. The current invention therefore does not address the reduction in size of the bird's beak, but provides a simple process for the production of a coplanar isolation region, without introducing the defectivity problems of the prior art. The object of the current invention is, in a semiconductor device, to provide a simple method of producing field isolation regions, whose upper surface is approximately coplanar with the upper surface of the semiconductor substrate, while preventing the exposure of the edges of active regions. Accordingly, the invention provides a method for producing an isolation region on an upper surface of a semiconductor substrate comprising the steps defined in claim 1. According to an embodiment of the invention, a first buffer layer is formed on the upper surface of the semiconductor substrate, under the masking layer. The active and field regions are then defined by patterning the masking layer. According to an embodiment of the invention, a second buffer layer is formed on the first buffer layer and the semiconductor substrate. According to an embodiment of the invention, the portion of the filling layer filling the notch is removed at the same time as the masking layer. According to an embodiment of the invention, the semiconductor substrate is composed of silicon, the masking layer is composed of silicon nitride, the isolating layer is composed of silicon dioxide and the filling layer is composed of silicon nitride. According to an embodiment of the invention, the first buffer layer is composed of silicon dioxide, and the second buffer layer is composed of polycrystalline silicon, or amorphous silicon. A certain embodiment of the current invention will be described, by way of example, with reference to the accompanying diagrams, wherein: figures 1A - 1F are sectional views illustrating successive steps of a prior art method of producing a field isolation region in a semiconductor substrate; figure 2 shows a cross section of a structure produced according to the method of figure 1; figures 3A - 3C are sectional views illustrating successive steps of an alternative prior art method of producing a field isolation region in a semiconductor substrate; figure 4 shows a cross section of a structure produced according to the method of figure 3; figures 5A - 5D are sectional views illustrating successive steps of a variant of the process of figure 3; figures 6A - 6G are sectional views illustrating successive steps of a method of forming a field isolation region which is approximately coplanar with the semiconductor substrate surface, according to the invention; and figure 7 shows, figuratively, the characteristic cross-section of an isolation region produced according to the method of the invention. According to the invention, a method is provided for producing field isolation regions in semiconductor devices, whose upper surfaces are approximately coplanar with the upper surface of the semiconductor substrate, and which do not have gaps formed in the isolation at edges of active regions. Figures 6A to 6G show stages in the process of the invention. In figure 6A, a semiconductor substrate 10 has been provided with a first buffer layer 12, a second buffer layer 14 and a masking layer 16, all overlying an active region 20; and a field isolation layer 22 of thickness t 1 , in a field region 18. This structure may be prepared according to the method described in relation to figures 1A - 1C. Notch 26 is present between the masking layer 16 and the upper surface of the field oxide layer 22. Typically, the semiconductor substrate is composed of silicon, the first buffer layer 12 and the field isolation region 22 are composed of silicon dioxide, the second buffer layer 14 is composed of polycrystalline silicon, and the masking layer 16 is composed of silicon nitride. During formation of the field isolation layer, a native oxide layer is formed over the nitride masking layer. This is removed, as described earlier, by dipping the structure in dilute hydrofluoric acid, or another equivalent etch step. In figure 6B, a filling layer 34 is formed over the surface of the structure. This layer must be sufficiently thick to fill the notch 26. This filling layer must be able to be selectively etched with respect to the material of the insulating layer, with an easy to detect end point. The filling layer may typically be formed of silicon nitride; a 160nm layer of silicon nitride appears suitable. Such a silicon nitride filling layer may be formed by chemical vapour deposition using a mixture of dichlorosilane (SiH 2 Cl 2 ) and ammonia (NH 3 ) at 750°C. The filling layer 34 thus formed may then be anisotropically etched, such as by using a plasma of carbon tetrafluoride (CF 4 ), trichloromethane (CHF 3 ) and sulphur hexafluoride (SF 6 ). The end point may be detected by the variation in optical spectroscopy of the plasma, when the etch reaches the field oxide layer. Figure 6C shows the structure after this etch step. The filling layer is removed from the entire surface of the structure, except in the notch 26. Here, a small remaining part 36 (a "field protection spacer") remains. An etch step is then performed which selectively etches the material of the isolation layer. This etch step may be an isotropic, wet etch step using dilute hydrofluoric acid to remove 100 to 200nm of field oxide. Figure 6D shows the results of such an etch. The field protection spacer 36 is not removed with the etching step which etches the field isolation region. The etch is applied such that the isolating layer has a thickness of t 5 , selected so that the upper surface of the isolation region is substantially planar with, but slightly higher than, the upper surface of the semiconductor substrate 10. Figures 6E, 6F, 6G show subsequent process steps whereby the masking layer 16, the second buffer layer 14 and the first buffer layer 12 are subsequently removed in suitable etching steps, as previously discussed. As shown in figure 6G, the upper surface 24 of the semiconductor substrate is exposed, and a field isolation region 22 is produced, which does not expose the edge of the semiconductor substrate in the active region. The field isolation region has an upper surface which is higher than the upper surface by an amount t 6 , which is significantly less than the thickness d previously achieved. The isolation region 22 which remains has a characteristic cross section. This is illustrated figuratively in figure 7, which is derived from electron microscope photographs of the structure of the invention. The total field oxide thickness t f may typically be 300 to 400nm. The difference in height t 6 between the active region and the field region when produced according to the process of the invention is about 100nm. This is a compromise between coplanarity of the field oxide and the semiconductor surface 24, and protection of the edge of the semiconductor substrate. A hollow 40 is present in the upper surface of the field oxide layer. This is caused by the etching of the field oxide being more pronounced at the edge of field protection spacer 36, the field oxide 22 being slightly thinner at this point (figure 6C). The position of this hollow approximately corresponds to the position of an edge of the field protection spacer 36. This hollow has a deepest point separated from a nearest edge of the active region by a distance p , which is between 0.25 and 0.35µm, typically 0.27µm, significantly longer than the separation s achieved with previous processes. At the lowest point of this hollow, the thickness h of the field oxide is about 180nm, significantly more than achieved with previous processes. Again, a minimum width field region 25a of width wf equal to the minimum width allowed in the process is also shown. This field region has a height above the substrate surface 24 no more than t 6 . The distance p is an apparent bird's beak length. It is typically 0.25 to 0.30µm. In a typical 0.5µm minimum feature size process, the minimum width field region 25a will have a width wf of less than 1.0µm, such as 0.7µm. The minimum field width wf is equal to the drawn field width (the size of a feature formed in the masking layer prior to oxidation to form the field oxide), extended by a bird's beak length on either side. However, in this case, the minimum field width wf, less two apparent bird's beak lengths of 0.3µm each gives a drawn field width of 0.1µm. This would not be possible to achieve in a process with a minimum drawn feature size of 0.35µm to 0.5µm, as definition of mask features of less than this minimum feature size is not possible. Furthermore, in the structure of figure 7, the depth of the field oxide below the semiconductor surface 24 in the minimum width portion 25a is over 60% of the depth of the field oxide below the semiconductor surface in the wide field oxide region, 22. This would not be possible with a very narrow drawn field oxide, due to the oxide thinning effect. This effect causes narrow regions of field oxide to be thinner than wide regions, for given oxidation conditions. The effect begins with drawn widths of less than 0.7µm, and would be severe for a drawn width of 0.1µm. This effect is explained, for example, in "Solid State Technology", November 1994, pages 70-71 The above described form of the field regions 25a, 22 is characteristic of a structure produced according to the method of the invention. It can be deduced from the width wf , and the minimum feature size of the technology in question, that the apparent bird's beak length p is not the actual bird's beak length, and that the field protection spacers of the invention have been used. Deeper, narrower minimum width field regions 25a may be produced according to the invention, without the risk of exposing edges of the active area. A later deposited layer 25b has an upper surface 25c. This upper surface is far more planar than that of the previous processes, such as those shown in figures 2, 4. The field oxide 22 is substantially coplanar with the semiconductor surface, and the problems of the prior art concerning reflections of light, and thinning of subsequent layers at the interface between field and active regions, are avoided. Although the invention has been described in relation to one particular embodiment, numerous variations will be apparent to one skilled in the art. One buffer layer may be used instead of two; the buffer layers may be composed of any suitable material. By careful choice of material for the masking layer, the need for a buffer layer may be avoided. The technique may also be adapted for use with deposited isolation regions, the advantage of the invention being to allow the planarisation of an isolation layer without exposing an edge of the underlying semiconductor substrate, which itself causes defects in later formed devices.

Claims: A method for producing an isolation region (22) on an upper surface (24) of a semiconductor substrate (10) comprising the steps of: a) forming a masking layer (16) on the upper surface of the semiconductor substrate; b) defining an active region (20) and a field region (18) by patterning of the masking layer, the active region being covered with the masking layer (16); c) thermally growing an isolating layer (22) having upper and lower limits on the field region such that the lower limit of the isolating layer lies below the upper surface of the semiconductor substrate, and that a notch (26) exists between an edge of the masking layer and the upper limit of the isolating layer; d) conformally depositing a filling layer (34) over the masking layer and the isolating layer, such that it completely fills the notch (26), this filling layer being selectively etchable with respect to the isolating layer; e) selectively etching the filling layer with respect to the isolating layer, to expose the upper limit of the isolating layer, the notch (26) remaining filled with a portion (36) of the filling layer; f) partially removing the isolating layer from its upper limit until this upper limit is substantially coplanar with the upper surface of the semiconductor substrate; and g) removing the masking layer. A method according to claim 1 wherein a first buffer layer (12) is formed on the upper surface of the semiconductor substrate below the masking layer. A method according to claim 2 wherein a further buffer layer (14) is formed over the semiconductor substrate (10) and the first buffer layer (12). A method according to claim 1 wherein the portion (36) of the filling layer (34) filling the notch (26) is removed at the same time as the masking layer (16) is removed. A method according to claim 1 wherein the semiconductor substrate (10) is composed of silicon; the masking layer (16) is composed of silicon nitride; the isolating layer (22) is composed of silicon dioxide; and the filling layer (34) is composed of silicon nitride. A method according to claim 3 wherein the first buffer layer (12) is composed of silicon dioxide and the further buffer layer (14) is composed of polycrystalline silicon. A method according to claim 3 wherein the first buffer layer (12) is composed of silicon dioxide and the further buffer layer (14) is composed of amorphous silicon.

Inventors: GAYET PHILIPPE, GAYET, PHILIPPE
Applicants: ST MICROELECTRONICS SA, STMICROELECTRONICS S.A.
Application year: 1996
Main classification: H01L21
IPC codes: H01L21