A thin film solar cell comprising a I-III-VI(2) type compound semiconductor for its absorption layer and method for manufacturing the same

Abstract: A thin film solar cell having high conversion efficiency is provided. The thin film solar cell can control its band gap while keeping the quality superior to conventional solar cells. The absorber layer for photovoltaic energy conversion is a Cu(In 1-X Ga X ) (Se 1-Y S Y ) 2 based solid solution where X and Y are in the range of the following Equation: 0.317 + 0.176Y ≧ X ≧ 0.117 + 0.176Y 1 > X + Y > 0 Y > 0. The Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 based solid solution has a specific chalcopyrite type crystal structure and its lattice constant ratio of a-axis to c-axis is extremely closer to two. It is most preferable that the band gap is 1.4eV, X is 0.3 and Y is 0.4, since the conversion efficiency of a homojunction solar cell will become the highest.

Description: This invention relates to a thin film solar cell comprising a I -III-VI 2 type compound semiconductor for its absorber layer. Thin films of a I -III-VI 2 type compound whose band gap ranges from 1.0 to 1.8eV, such as CuInSe 2 , are used for solar cells. Multi-source evaporation and selenization are known as methods for forming a CuInSe 2 thin film (cf. A. Rockettand R.W. Birkmire, J. Appl. Phys. Vol.70, No.7, p.81). In the multi-source evaporation, a CuInSe 2 film is formed on a heated substrate by evaporating the elements (Cu, In, and Se) from the respective evaporation sources. Several well-known evaporation processes, which provide highly efficient solar cells, include a process for forming a Cu-In-Se film in a Cu-rich composition (Cu/In > 1). The reason is as follows. If a thin film is formed on a substrate at a temperature of at least 500°C in a Cu-rich condition for the composition, Cu-Se based impurities are deposited as well as the CuInSe 2 . The Cu-Se based impurities function as flux, and thus the crystal particles of the CuInSe 2 grow bigger. In another case, the band gap (Eg) of the CuInSe 2 (absorber layer) is made closer to the best value for absorption of sun light (1.4eV), so that the efficiency of the solar cell is improved. In general, the band gap of the absorber layer is increased by dissolving CuGaSe 2 (Eg = 1.68eV) in the CuInSe 2 (Eg = 1.0eV). When Cu(In 1-X Ga X )Se 2 solid solution is used for an absorber layer, the band gap will be enlarged as the Ga solid solution quantity (X) rises. The conversion efficiency of the solar cell, however, does not increase so easily even if the solid solution thin film is used for the layer. The conversion efficiency is maximum when the Ga quantity (X) is about 0.2 to 0.3 (Eg = about 1.15eV). The conversion efficiency, however, starts lowering if the value (X) continues to rise (cf. H.W. Schock, MRS BULLETIN, Vol.18, No.10, pp.42-44). This phenomenon is caused, probably, by the deterioration of the crystal property of the Cu(In 1-X Ga X )Se 2 solid solution thin film in a Ga-rich region. In order to solve these and other problems, this invention aims to provide a thin film solar cell having high conversion efficiency. The absorber layer of the solar cell is a CuInSe 2 based compound semiconductor thin film which permits band gap control while keeping its quality. For the present purposes, a solar cell of this invention is defined in the claims. The solar cell comprises a photovoltaic energy conversion absorber layer of Cu(In 1- X Ga X )(Se 1-Y S Y ) 2 , and X and Y of the formula are in the range of the following Equation (1): 0.317 + 0.176Y ≧ X ≧ 0.117 + 0.176Y 1 > X + Y > 0 Y > 0. It is preferable that the absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 is in the range indicated in the following Equation (2). X = 0.217 + 0.176Y 1 > X + Y > 0 Y > 0. It is specifically preferable in the absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 that X = 0.3, and Y = 0.4. The absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 has a chalcopyrite type crystal structure where the lattice constant ratio of the c-axis to the a-axis is about two. More specifically, the ratio ranges from 2.01 to 1.99. A first method for manufacturing a thin film solar cell of this invention comprises formation of an absorber layer of Cu(In 1-X Ga X ) (Se 1-Y S Y ) 2 by evaporating Cu, Ga, In, Se and S, where X and Y are indicated by Equation (1). A second method for manufacturing a thin film solar cell of this invention comprises formation of an absorber layer Cu(In 1-X Ga X ) (Se 1-Y S Y ) 2 by evaporating Cu, Ga, In, Se and In sulfide, where X and Y are indicated by Equation (1). It is preferable in the second method that the In sulfide is In 2 S 3 . A third method for manufacturing a thin film solar cell of this invention comprises formation of an absorber layer Cu(In 1-X Ga X ) (Se 1-Y S Y ) 2 by evaporating Cu, Ga, In, Se and Ga sulfide, where X and Y are indicated by Equation (1). It is preferable in the third method that the Ga sulfide is GaS. According to this invention, excellent crystal properties are maintained even if the band gap of the CuInSe 2 based compound semiconductor thin film for the absorber layer is controlled in a wide range, so that a high conversion efficiency is achieved. FIGs. 1A and 1B are transmission electron microscope (TEM) pictures to show cross sections of a solar cell having an absorber layer of CuInSe 2 thin film formed by a multi-source evaporation of one embodiment of this invention. FIG. 1A is the bright field image and FIG. 1B is the dark field image. FIG. 2 is a TEM picture to show a cross section of the portion near the surface of the Cu-rich composition CuInSe 2 thin film sample of another embodiment of this invention. FIGs. 3A and 3B show electron beam diffraction patterns of the Cu 2 Se part and that of the CuInSe 2 part of the TEM picture respectively (FIG. 2). FIG. 4 is a high resolution TEM picture to show the portion near the interface of the segregated Cu 2 Se phase and of the CuInSe 2 phase of one embodiment of this invention. FIG. 5 is a diagram to show the concept the system of the CuInSe 2 thin film growth in the multi-source evaporation of one embodiment of this invention. FIG. 6 is a graph to show the relationship between the band gap of the Cu(In 1-X Ga X )Se 2 based solid solution of one embodiment and the lattice constant ratio of the c-axis to the a-axis (c/a). FIG. 7 is a graph to show the composition range of the Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 based solid solution of one embodiment of this invention. The conversion efficiency of a solar cell is improved by using a Cu(In 1-X Ga X )Se 2 based solid solution for its absorber layer. When the quantity of Ga solid solution (X) exceeds the range from 0.2 to 0.3 (Eg = about 1.15eV), however, the conversion efficiency lowers. In order to examine how this phenomenon is caused, the microstructures of the cross sections of CuInSe 2 based absorber layers having varied compositions were observed by using TEM. FIGs. 1A and 1B are TEM pictures to show cross sections of a solar cell provided with an absorber layer of a CuInSe 2 (CIS) thin film which is formed by a multi-source evaporation. The solar cell is formed by laminating ITO, ZnO, CdS, CIS, molybdenum (Mo), and glass by turns. Here, CIS indicates CuInSe 2 , and ITO is a transparent conductive film of, for example, indium-tin oxide alloy. ZnO/CdS is a buffer layer consisting of a ZnO layer and a CdS layer. CIS is an absorber layer and Mo is a back contact. These TEM pictures show that a lot of twin crystals or stacking faults exist in the absorber layer. Such a lattice defect is indicated with a mark T. Mark V indicates a void. These defects can have an adverse influence on the performance of the solar cell. In the next step, a Cu-rich composition CuInSe 2 thin film formed by the multi-source evaporation was analyzed to see why such crystal defects of the CuInSe 2 were created. In the multi-source evaporation, the Cu-In-Se film formation under the Cu-rich composition condition is an important process to make the CuInSe 2 crystal particles bigger. Therefore, the process should be observed carefully to clarify how the CuInSe 2 thin film is formed. The composition of the Cu-rich composition film was analyzed by using an electron probe microanalyzer (EPMA). The ratio was as follows. Cu : In : Se = 43.6 : 12.1 : 44.3 (atomic %). When the composition is expressed with Cu 2 Se and CuInSe 2 , the ratio becomes as follows. Cu 2 Se : CuInSe 2 =5:4, namely, Cu was contained quite excessively in the sample. FIG. 2 is a TEM picture to show the cross section of a portion near the surface of this sample. Identification of each phase was conducted by using the EPMA. In FIG. 2, the direction perpendicular to the substrate was indicated by ↑ n . It is clear from FIG. 2 that the segregated Cu 2 Se exists on the surface of the CuInSe 2 . FIGs. 3A and 3B indicate the electron beam diffraction patterns of the Cu 2 Se part and that of the CuInSe 2 part of the cross-sectional TEM picture respectively (FIG. 2). Though the sample was displaced a little during the measurements, it was not inclined. Therefore, the orientations of their electron diffraction patterns accord with each other. The electron beam diffraction pattern of the above-mentioned Cu 2 Se was indexed based on the structural parameter of a pseudo-cubic system (a = 11.6 angstrom (1.16nm)), more precisely, a tetragonal system (a = 11.52 angstrom (1.152nm), c= 11.74 angstrom (1.174nm)). The zone axis is [011] axis. The electron beam diffraction pattern of the above-mentioned CuInSe 2 (FIG. 3B) was indexed based on the structural parameter of a sphalerite phase (a = 5.78 angstrom (0.578nm)) of a tetragonal system. The zone axis is [011] axis, too. The arrows indicate the diffraction points corresponding to the {1/2, 1/2, 1/2} reflections, which are not found in either the sphalerite phase or the chalcopyrite phase. In general, these diffraction points are found in a CuPt phase. It is clear from the comparison between the electron beam diffraction patterns of Cu 2 Se and of CuInSe 2 , that the [011] axis orientation of Cu 2 Se and that of CuInSe 2 are parallel. In addition, (11 1 ) direction of Cu 2 Se and (11 1 ) direction of CuInSe 2 , (2 2 2) direction of Cu 2 Se and (1 1 1) direction of CuInSe 2 accord with each other. Therefore, the (111) faces of Cu 2 Se and CuInSe 2 are parallel. Namely, the orientation relationship can be described in the following Equation (3). [011], (11 1 ) CuInSe 2 || [011], (11 1 ) Cu 2 Se FIG. 4 is a high-resolution TEM picture to show a portion near the interface of the segregated Cu 2 Se phase and CuInSe 2 phase. The Cu 2 Se phase exists around the surface while the CuInSe 2 phase exists on the substrate side. In FIG. 4, a lattice image of 6.8 angstrom (0.68nm) intervals specific to Cu 2 Se phase and a lattice image of 3.3 angstrom (0.33nm) intervals specific to CuInSe 2 phase are clearly shown. The lattice image of the CuInSe 2 phase having 3.3 angstrom (0.33nm) intervals is seen at the bottom of FIG. 4. In the middle of these phases, there is a portion of 6.7 angstrom (0.67nm). The intermediate portion is a CuPt phase. In the electron beam diffraction patterns (FIGs. 3A and 3B), diffraction points corresponding to {1/2, 1/2, 1/2} reflections are found. Such reflections are not seen either in a sphalerite phase (CuPt phase) or in a chalcopyrite phase. These observation results clearly indicate the mechanism of the CuInSe 2 thin film growth in a multi-source evaporation. The concept is shown in FIG. 5. CuInSe 2 crystals basically grow through the Cu-Se based liquid layer on the thin film. It was believed that the chalcopyrite type CuInSe 2 crystals grew directly from the Cu-Se based liquid layer (cf. J.R. Tuttle et al., J. Appl. Phys. Vol.77, No.1, pp.153-161). Actually however, the Cu-Se based liquid layer co-exists with the Cu 2 Se solid phase as shown in the enlarged view of the thin film surface (FIG. 5). The Cu 2 Se solid phase and In diffused from the surface react with each other, and thus CuInSe 2 is generated. CuInSe 2 of the CuPt phase or sphalerite phase (metastable phases) is first generated from Cu 2 Se. The metastable phases gradually change to CuInSe 2 of chalcopyrite phase (stable phase). Both FIGs. 3 A, B (the electron beam diffraction pattern) and FIG. 4 (high-resolution TEM picture) indicate that there is a three-dimensional crystal orientation relationship between the Cu 2 Se (the starting material) and the generated CuInSe 2 (the product). Such a chemical reaction is called a Topotactic Reaction. The fact that the crystal structures of the Cu 2 Se and the CuInSe 2 are so similar to each other is important for the Topotactic Reaction. If Cu 2 Se, which is based on an anti-fluorite structure, changes to CuInSe 2 having sphalerite structure, the Se location of the compounds, namely, the cubic closest packing structure of Se, does not change. It is CuInSe 2 of sphalerite phase or of CuPt phase that is generated first from Cu 2 Se. The CuInSe 2 of these phases has an isotropic crystal structure. Such metastable phases having isotropic crystal structures change into CuInSe 2 of a stable chalcopyrite phase. The CuInSe 2 of the chalcopyrite phase is a tetragonal system. Its a-axis is 5.782 angstrom (0.5782nm), and c-axis is 11.619 angstrom (1.1619nm) long. The ratio of the c-axis to the a-axis is 2.0095, namely, the crystals have an anisotropic structure. It has been found that crystal defects are generated when the CuInSe 2 of the isotropic sphalerite phase or of CuPt phase changes to that of chalcopyrite type CuInSe 2 having anisotropic crystal structure (cf. the cross-sectional TEM of FIG. 1). In view of this fact, it is possible to reduce crystal defects including twin crystals and stacking faults by decreasing the anisotropy of the apparent crystal structure of the CuInSe 2 . For this purpose, the composition of the CuInSe 2 will be controlled to make the ratio of the axes (c/a) closer to two. Table 1 shows the lattice constant, ratio of c-axis to a-axis and the band gap for CuInSe 2 and its related compounds. Formulas Eg(eV) a(angstrom) c(angstrom) c/a CuInSe 2 1.04 5.782 11.619 2.0095 CuGaSe 2 1.68 5.612 11.032 1.9657 CuInS 2 1.53 5.523 11.141 2.0172 It is clear from Table 1 that the c/a of CuInSe 2 is 2.0095. Therefore, if CuGaSe 2 having 1.9657 c/a is dissolved in the CuInSe 2 , the band gap will be increased, and in addition, the c/a value will be closer to two. FIG. 6 shows the relationship between the band gap of the Cu(In 1-X Ga X )Se 2 based solid solution and the value of c/a. Though the value of c/a becomes closer to two, the value begins to decrease when X exceeds 0.2. When X = 0.2, the band gap is about 1.15eV. Therefore, if this Cu(In 1-X Ga X )Se 2 based solid solution is applied to an absorber layer of a solar cell, the conversion efficiency becomes maximum when X ranges from 0.2 to 0.3. The conversion efficiency, however, does not rise even if more Ga is added. In order to manufacture a CuInSe 2 based solar cell having high-conversion efficiency, its band gap should be increased while maintaining the c/a value of the CuInSe 2 based absorber layer to be two. For such a purpose, a chalcopyrite type compound having a big band gap and high c/a value should be dissolved in the Cu(In 1-X Ga X ) Se 2 . CuInS 2 is a compound to meet the requirement. Its band gap is as big as 1.53eV and the c/a exceeds two, more specifically, it is 2.0172. Therefore, the band gap can be enlarged while maintaining the c/a value at about two, by simultaneously dissolving CuGaSe 2 (its c/a value is less than two) and CuInS 2 (its c/a value is more than two) in the CuInSe 2 . As a result, a desirable composition of an absorbing layer can be obtained, namely, where the composition is a Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 based solid solution of the formula: X = 0.217 + 0.176Y; where 1 > X + Y > 0; and 1 > Y > 0. Table 2 shows the examples of absorber layer compositions which meet the above-mentioned requirements, and the band gaps. X Y Eg(eV) 0.783 0.000 1.15 0.665 0.100 1.21 0.547 0.200 1.28 0.430 0.300 1.34 0.312 0.400 1.41 0.195 0.500 1.47 0.077 0.600 1.54 In this condition, the band gap of the absorber layer can be controlled from 1.15eV to 1.57eV while maintaining the value of c/a to two. Actually however, it is difficult to control the composition of the Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 based solid solution to be exactly X = 0.217 + 0.176Y, and the process is not desirable from the viewpoint of cost performance. The more practical composition is: 0.317 + 0.176Y ≧ X ≧ 0.117 + 0.176Y, 1 > X + Y > 0, and Y > 0. This composition is also indicated in FIG. 7. It is the most desirable that the band gap is 1.4eV, and X = 0.3 while Y = 0.4 in the composition of the Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 based solid solution, since the highest conversion efficiency will be provided for a homojunction solar cell. This invention will be described more in detail by referring to Examples. Example 1 A Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 based solid solution thin film was formed by a multi-source evaporation. The composition is indicated in Table 3. A soda-lime glass coated with an Mo film of about 1µm thick was used for the substrate. Cu, In, Ga, Se and S were evaporated from respective element sources. In the first step, the elements were deposited to be about 2µm thick in a Cu-rich condition [Cu / (In + Ga) > 1], and in the next step, the elements were deposited to be about 1µm thick in a (In + Ga)-rich condition [Cu / (In + Ga) < 1]. During this process, the temperature of the substrate was maintained at 540°C. Table 3 shows the composition and the band gap of the Cu(In 1-X Ga X ) (Se 1-Y S Y ) 2 based solid solution thin film. The composition of the film was determined by using an electron probe microanalyzer (EPMA). A solar cell was manufactured using this Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 based solid solution thin film for its absorber layer. The solar cell has a structure of MgF 2 / ITO / ZnO / CdS / CIGSSe / Mo / glass. Here, CIGSSe means Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 . The CdS film was formed by a chemical bath, the ZnO film and the ITO film were formed by magnetron sputtering, and the MgF 2 antireflection film was formed by electron beam evaporation. Table 3 shows the conversion efficiency of the solar cell measured in the condition of AM1.5, 100mW/cm 2 . Number X Y Eg(eV) Conversion efficiency (%) 1 0.20 0.00 1.14 14.8 2 0.23 0.12 1.22 16.7 3 0.25 0.20 1.27 17.2 4 0.26 0.28 1.33 18.3 5 0.28 0.40 1.41 19.0 6 0.30 0.50 1.48 18.2 It is clear from Table 3 that the conversion efficiency rises as the band gap comes closer to 1.4eV. The cross-sections of the absorber layers of these solar cells were observed by using TEM. As a result, the crystal property was excellent, and neither twin crystals nor stacking faults were found. Example 2 A Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 based solid solution thin film was formed by a multi-source evaporation. A soda-lime glass coated with a Mo film of about 1µm thick was used for the substrate. Cu, In, Ga, Se were evaporated from respective element sources, and S was evaporated from In 2 S 3 . In the first step, about 1µm of In-Ga-Se-S film was formed while the substrate temperature was 300°C. Then, only the fluxes of Cu and Se were provided and film-forming was conducted until the composition of the whole film became Cu-rich [Cu / (In + Ga) > 1]. During this process, the temperature of the substrate was raised to about 540°C. This film was irradiated again with the fluxes of In, Ga, Se, and GaS in order to be applied to a solar cell, so that the final composition became (In, Ga)-rich [Cu / (In + Ga) < 1]. Since the substrate temperature varies depending on the compositions, the compositions of the film were checked during the film-forming process by monitoring the substrate temperature, and thus the fluxes were changed properly (see Japanese Journal of Applied Physics , Kohara et al., Vol.34, L1141, 1995). Table 4 shows the composition of the formed Cu(In 1-X Ga X )(Se 1 -Y S Y ) 2 based solid solution thin film. The composition of the film was determined by using an EPMA. The band gap of the Cu(In 1-X Ga X ) (Se 1-Y S Y ) 2 based solid solution thin film is also shown in Table 4. Number X Y Eg(eV) Conversion efficiency (%) 7 0.21 0.02 1.15 15.6 8 0.22 0.05 1.17 16.4 9 0.23 0.10 1.21 16.7 10 0.24 0.14 1.23 17.0 The Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 based solid solution thin film was applied as an absorber layer to a solar cell having the identical structure as that of Example 1. The solar cell was measured in the same condition as in Example 1. It is clear from Table 4 that the conversion efficiency rises as the band gap comes closer to 1.4eV. The cross-sections of the absorber layers of these solar cells were observed by using TEM. As a result, the crystal property was excellent, and neither twin crystals nor stacking faults were found. Example 3 A Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 based solid solution thin film was formed by a multi-source evaporation. A soda-lime glass coated with an Mo film of about 1µm thick was used for the substrate. Cu, In, Ga, Se were evaporated from respective element sources, and S was evaporated from GaS and elemental S. A Knudsen cell was used for the evaporation process. In the first step, about 1µm of In-Ga-Se-S film was formed while the substrate temperature was 300°C. Then, only the fluxes of Cu, Se and S were provided and film-forming was conducted until the composition of the whole film became Cu-rich [Cu / (In + Ga) > 1]. During this process, the temperature of the substrate was raised to about 550°C. This film was irradiated again with the fluxes of In, Ga, Se, and GaS in order to be applied to a solar cell, so that the final composition became (In, Ga)-rich [Cu / (In + Ga) < 1]. Since the substrate temperature varies depending on the compositions, the compositions of the film were checked during the film-forming process by monitoring the substrate temperature, and thus the fluxes were changed properly. This Cu(In 1-x Ga x )(Se 1-y S y ) 2 based solid solution thin film was applied as an absorber layer to manufacture a solar cell having the same structure as those of Examples 1 and 2. The conversion efficiency was as high as the former examples. The cross-sections of the absorber layers of these solar cells were observed by using TEM. As a result, the crystal property was excellent, and neither twin crystals nor stacking faults were found. As mentioned above, a solar cell of this invention has an absorber layer for photovoltaic energy conversion whose composition is indicated by the formula: Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 , where X and Y are in the range of Equation (1). Therefore, the band gap can be controlled while maintaining its quality, and as a result, a solar cell having conversion efficiency superior to that of a conventional technique can be provided. In addition, the solar cell comprises an absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 based solid solution which has a chalcopyrite type crystal structure and whose lattice constant ratio of c-axis to a-axis is extremely close to two, so that the crystal property does not deteriorate even if the band gap of the absorber layer is enlarged.

Claims: A thin film solar cell comprising an absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 for photovoltaic energy conversion, where X and Y are in a range indicated by the following Equation (1): 0.317 + 0.176Y ≧ X ≧ 0.117 + 0.176Y 1 > X + Y > 0 Y > 0, the absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 having a chalcopyrite type crystal structure, wherein the lattice constant ratio of c-axis to a-axis is two. The thin film solar cell according to claim 1, wherein the absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 is in the range of the following Equation (2): X = 0.217 + 0.176Y (2) 1 > X + Y > 0 Y > 0. The thin film solar cell according to claim 1, comprising the absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 , where X = 0.3 and Y = 0.4. A method for manufacturing a thin film solar cell having an absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 for photovoltaic energy conversion, where X and Y are in the range of the following Equation (1), 0.317 + 0.176Y ≧ X ≧ 0.117 + 0.176Y 1 > X + Y > 0 Y > 0, said absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 is formed by evaporating Cu, Ga, In, Se and S and has a chalcopyrite type crystal structure, wherein the lattice constant ratio of c-axis to a-axis is two. A method for manufacturing a thin film solar cell having an absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 for photovoltaic energy conversion, where X and Y are in the range of Equation (1), 0.317 + 0.176Y ≧ X ≧ 0.117 + 0.176Y 1 > X + Y > 0 Y > 0, said absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 is formed by evaporating Cu, Ga, In, Se and In sulfide and has a chalcopyrite type crystal structure, wherein the lattice constant ratio of c-axis to a-axis is two. The method for manufacturing a thin film solar cell according to claim 5, wherein the In sulfide is In 2 S 3 . A method for manufacturing a thin film solar cell having an absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 for photovoltaic energy conversion, where X and Y are in the range of Equation (1), 0.317 + 0.176Y ≧ X ≧ 0.117 + 0.176Y 1 > X + Y > 0 Y > 0, said absorber layer of Cu(In 1-X Ga X )(Se 1-Y S Y ) 2 is formed by evaporating Cu, Ga. In, Se and Ga sulfide and has a chalcopyrite type crystal structure, wherein the lattice constant ratio of c-axis to a-axis is two. The method for manufacturing a thin film solar cell according to claim 7, wherein the Ga sulfide is GaS.

Inventors: KOHARA NAOKI, NISHITANI MIKIHIKO, WADA TAKAHIRO, KOHARA, NAOKI, NISHITANI, MIKIHIKO, WADA, TAKAHIRO, KOHARA, NAOKI,, NISHITANI, MIKIHIKO,, WADA, TAKAHIRO,
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD
Application year: 1996
Main classification: H01L31
IPC codes: H01L31