COLOURANT COMPOSITION FOR PAINT PRODUCTS

Abstract: The invention relates to colourants (colourant pastes) used for the tinting of paint products. The colourants contain: 2-75 wt.% (A) pigment component comprising one or more organic and/or inorganic pigments and possibly extender pigments; 10-60 wt.% (B) diluent component comprising one or more organic solvents other than aliphatic alcohols or aromatic hydrocarbons, wherein 20-100 % of the total weight of the diluent consists of a biodegradable ester of lactic acid and an alcohol, preferably ethyl or isopropyl lactate 10-50 wt.% (C) binder component (calculated as 100 % non-volatile matter) comprising one or more binders soluble in the diluent (B), wherein 70-100 % of the total weight of the binder consists of a ketone aldehyde, ketone and/or aldehyde resin soluble in aliphatic hydrocarbons and 0-30 % of the total weight of the binder consists of other binders commonly used in colourants, for example acrylic, alkyd or polyester resin and 0-5 wt.% (D) additive component (calculated as 100 % active matter) comprising one or more additives suitable for use in colourants. The binders and additives may be delivered undiluted (solvent-free) or they may contain as a diluent organic solvents that in the colourant are considered as a part of the diluent component (B). The present invention relates not only to the above mentioned colourants but also to their use as a part of a tinting system of solvent-borne paint products.

Description: COLOURANT COMPOSITION FOR PAINT PRODUCTS SUMMARY OF THE INVENTION This invention relates to a colourant composition for use in solvent-borne paint products. The colourant composition comprises 2-75 % by weight of a pigment component (A) consisting of one or more organic and/or inorganic pigments and possibly extender pigments, 10-60 % by weight of a diluent component (B) consisting of one or more organic solvents none of which is an aliphatic alcohol or aromatic hydrocarbon, and 10-50 % by weight of a binder component (C) consisting of one or more binders soluble in the diluent component (B). In addition, the composition may comprise 0-5 % by weight of an additive component (D) consisting of one or more additives suitable for use in colourants. The above- mentioned ranges for the amounts of components (C) and (D) are calculated as 100 % non-volatile/active matter whereupon the solvents possibly contained in the delivery form are included in the diluent component (B). The colourants according to the invention can be used in tinting paints. Preferably, however, they are used in tinting systems containing a series of colourant pastes that allow the tinting of various types of base paints at the paint plant, distribution warehouses, points of sale, or on site by industrial customers themselves. In this specification the term "paint products" is employed in its broad meaning referring to industrial and trade sales coatings, paints, lacquers, varnishes, fillers, woodstains and similar liquid substances for application to various surfaces as a protective and decorative coating. Colourants or colourant pastes are colour, colour strength and rheology-controlled high solids pigment dispersions. COLOURANTS IN GENERAL Tinting systems Paint products can be tinted by adding to them highly coloured tinting paints or, with respect to pigmentation, even more concentrated colourants (= colourant pastes). Tinting is carried out in ready-made paint products, white or coloured, called base paints. The colour and opacity of base paints depends on the amount of pigments, white pigments in particular. Base paints may be replaced by base lacquers/varnishes. Tinting paints are normally product-specific, i.e. they are produced separately for each paint type to be tinted.The number of pigments, colours and kinds of paints is limited. Concentrated colourant pastes can be used as a part of tinting systems. These systems permit the tinting of a broad range of various types of paint products with one series of colourants. The amount of work, number of ready products and need for storage space will be reduced, at the paint plant and distribution outlets which improves and speeds up the service. The system involves tinting machines located at various points ofthe distribution chain. In a paint plant tinting takes place in relatively large batches ("in-plant"), very often according to orders received. Base paints which are delivered to the distribution warehouses and points of sale, are usually tinted directly in sales packings ("in-can"). In the latest tinting systems tinting formulae are recorded in the memory of a PC (a formula databank). The machine dispenses automatically the correct mixing proportions of colourants into the base paint according to the preselected formula. The ingredients are thoroughly mixed in a shaker and the tinted paint is ready for use. Depending on the number of colours desired, 1-10 base paints per each paint type and 5-40 colourants per one tinting system are required. The paint products are mostly tinted in shades given as code numbers on manu¬ facturer's own colour cards or on those colour cards based on national or inter¬ national shade standards (RAL, BS, NCS etc.). It is also possible to connect the tinting machine to a colour matching system which enables tinting according to a colour sample. The number of shades is then practically infinite. It is recommendable to use tinting systems (containing base paints, colourants, the dispensing and mixing system and software for processing colours) always when it is possible. This helps to reduce stocks, minimize costs, ensure quality and improve customer service. Some base paints, especially white bases, are sold in large amounts also untinted. Production of colourants Components Colourants in general comprise a pigment component and a liquid medium into which the pigments are dispersed. The dispersion medium consists of at least one diluent, which is an organic solvent or water, and of a binder and/or dispersing/wetting agent. In addition to a dispersing agent, also other additives may be used. Dispersion and dispersing media Pigments are first mixed with the dispersion medium. Dispersion of pigments has been shown to occur in three stages: 1) wetting of particle surfaces and pores by the medium 2) breakdown and dispersion of pigment particles (agglomerates and aggregates) 3) wetting and stabilization ofthe dispersed primary particles and small agglomerates and aggregates. Dispersion is carried out using equipment the performance of which is based on high shear, impact and/or cavitation forces. Various types of dispersion equipment based on batch or continuous operation may be used; impact, ball, pebble, sand, bead, roller, or colloid mills; attritors, turbo mixers, high-speed disk dispersers etc. The dispersion of pigments often depends more on the process conditions and type of equipment than on the total energy input in the dispersion process. Dispersion medium, on the other hand, plays a major role in a dispersion process. The medium should be able to wet and stabilize pigments well and be compatible with various types of paints. In the wetting phase the liquid dispersion medium first displaces air in the pores and on the surface of pigment agglomerates and aggregates. Factors affecting the wetting ability include for example interfacial tension on the pigment/liquid surface, angle of contact and viscosity ofthe liquid. For effective wetting, these values should all be low. Through electrostatic and/or steric stabilization a layer is formed on the surface of the dispersed pigment particles preventing them from attaching to each other through flocculation or similar mechanisms. If particles remain too big they are separated through sedimentation. Finally, the consistency can be modified by adding a thickener additive to the colourant in order to retard pigment sedimenta¬ tion. The same diluents have been used in the production of colourants as are utilized as solvents in the paints to be tinted. However, binders commonly used in paints can be used in colourants only seldom, because they are not readily compatible with other binders, they often have too high viscosities and poor pigment dispersing/wetting properties. Therefore special colourant binders are used which have better properties with respect to polarity and/or solubility. In binder-free colourants only dispersing agents and diluents, such as water and organic solvents, especially glycols, are used as a medium. Colourants often have product or shade related problems regarding stability, gloss, reproducibility, cleanness of shade, or other similar properties. To overcome these problems various additives, the most important of which are dispersing and wetting agents, are needed in addition to diluents and binders. DESCRIPTION OF THE PRIOR ART Glycol containing and aqueous colourant pastes, so-called universal colourants, are suitable for tinting both water- and solvent-borne decorative paint products. Glycol colourants contain alkylene glycols, usually ethylene or propylene glycol (DE-3 839 294) as a diluent. Aqueous colourants have water (GB-2 266 310) or water and glycol (DE-1 519 254 and EP-555 950) or water and another auxiliary solvent such as diethylene glycol monoethyl ether (EP-462 557) as a diluent. Further essential components of a colourant are pigments and non-ionic and/or anionic dispersing agents. Cellulose ether (DE-1 519 254), polyethylene glycol and hydroxyethyl-ethyleneurea (EP-462 557) among others are used as a binder. The disadvantage of glycol colourants is that they usually contain harmful compo¬ nents when considered from health and safety at work or environmental point of view such as ethylene glycol and dispersing agents ofthe type alkylphenol ethoxy¬ lates, which furthermore impair the properties of solvent-borne paints, especially gloss, drying and water resistance. Pure aqueous colourants are considerably better in terms of safety than glycol containing colourants. Their use in solvent-borne paints is however limited. In attempts to extend the scope of application of colourants to industrial paints, universal colourants not containing water have been developed. These may contain 1) a water-soluble or dispersible binder, and 2) a diluent miscible, partially or completely, both in water and in organic solvents and 3) typically one or more non¬ ionic or anionic dispersing agents. The production of such universal colourants is mentioned for example in patent specification EP-507 202. Colourants in accord¬ ance with the specification contain 0.5-5% of a non-ionic dispersing agent and 20-50 % of a water-miscible organic solvent. Colourants suitable for use in solvent-borne paint products like printing inks, enamel paints, and industrial bake coatings contain for example following diluents: toluene, xylene and other aromatic hydrocarbons, n-butanol and ethylene glycol ethers or ether esters (SE-72 08650-7 and EP-448 347, examples). For example natural resins, alkyd resins, urea resins, aldehyde resins, ketone resins and acrylic resins have been used as a binder. Some ofthe diluents (glycol ethers, glycol ether esters, ethers etc.) mentioned in the patent specifications are considered harmful to health. Very often, solvents used in these products have an offensive odour and/or they are hazardous to health and therefore the packagings must be provided with appropriate danger classification. DETAILED DESCRIPTION OF THE INVENTION It is an object of this invention to provide colourants that are stable in paints and shades without having an adverse effect on paint properties such as gloss, drying/curing times or water resistance. It is another purpose of this invention to create colourants that fulfill the requirements with respect to health and safety at work and environmental aspects; The colourants may not be hazardous to health or to the environment and they may not have an unpleasant odour. These aims were achieved by formulating a new colourant that is suitable for the tinting of solvent- borne paint products. The said colourant composition consists of a pigment compo¬ nent (A), a diluent component (B), a binder component (C) and possibly of an additive component (D), characterized essentially in that 20-100 % ofthe total weight ofthe diluent component (B) is a biodegradable ester of lactic acid and a Cj-Cio-alcohol and 70-100 % ofthe total weight ofthe binder component (C) is a ketone aldehyde resin, ketone resin and/or aldehyde resin which are at least partly soluble in solvents used in paints including aliphatic hydrocarbons. Although esters of lactic acid and the mentioned resins are already previously known, the combination now being presented is a new one and, based on compara¬ tive tests, it also shows synergy. It has now been discovered that the said problems can, to a great extent, be avoided ifthe dispersing medium in colourants for paint products is a binder solution where 1) the diluent comprises at least one organic solvent (other than an aliphatic alcohol or aromatic hydrocarbon) which has a proper level of polarity and volatility, and of which 20-100 % is a biodegradable ester of lactic acid and a lower alcohol, preferably ethyl or isopropyl lactate, classified as not harmful. 2) 70-100 % ofthe binder component comprises at least one relatively low mole- cular mass ketone aldehyde, ketone and/or aldehyde resin soluble in the afore mentioned diluent, and possibly 0-30% of another colourant binder compatible with the mentioned resin part. Colourants ofthe present invention are suitable for use for the tinting of solvent- borne paint products, also those diluted in aliphatic hydrocarbons (white spirit) and/or with high solids content (so-called HS paints). They can be used especially in paints, the volatile organic compounds of which should be as safe as possible in terms of health and safety at work and environmental aspects. The amount of colourants added is in general 0-15 % by volume ofthe paint and therefore the solvent content of a colourant more or less affects the amount and quality ofthe solvents present in the tinted paint. Contrary to the previously known solutions the addition of e.g. alkylphenol based dispersing agents, which are classified as environmentally toxic and hazardous to fish in particular, is not necessary. Generally speaking the use of large amounts of dispersing agents has an adverse effect on the properties of a paint film. Dispersing agents may also contain non-desired solvents as a diluent. The weight composition of colourants ofthe present invention lies within the following limits: % (A) Pigment 2-75 (B) Diluent 10-60 (C) Binder ( 100 % non-volatiles) 10-50 (D) Additives (100 % active matter) 0-5 The weight percentage of coloured pigments in a colourant ofthe present invention varies from 2 to 75 % and of extender pigments from 0 to 50 %. Component classes (B), (C) and (D) are described in more detail below. It is possible to choose many other components besides those mentioned and therefore the presentation is only to illustrate, not to limit the invention. Pigment component (A) The colourants ofthe present invention are pigment concentrations which are con¬ centrated in coloured pigments in relation to volume. The selected pigments should enable covering a very extensive range of shades and they may not affect adversely the application and durability properties of various types of paints. Based on their chemical structure organic colour pigments can be categorised for example as follows: azo (monoazo, disazo, β-naphthol, naphthol AS, benz¬ imidazolone, disazo condensation etc.), metal-complex, isoindolinone and iso- indoline, phthalocyanine, quinacridone, perinone and perylene, anthraquinone, diketopyrrolopyrrole (DPP), dioxazine, quinophthalone and fluorescent pigments. As main categories are often given 1) azo pigments and 2) non-azo or polycyclic pigments. The corresponding categories of inorganic pigments are for example: pigments in elementary form (carbon, aluminium etc.), oxide and oxide hydroxide pigments (Tiθ2, Fe2θ3, FeO(OH) etc.), oxide mixed-phase pigments (4BiVθ4-3Bi2Moθ6, (Co,Ni,Zb)2Tiθ4, Cu(Fe,Cr)2C»4 etc.), sulphide und sulphate pigments (ZnS, BaSθ4, ZnS+BaS04 etc.), chromate and chromate molybdate mixed-phase pigments (PbCrθ4+PbSC>4, PbCrC>4+PbSθ4+PbMoθ4 etc.), complex salt pigments (for example iron blues are complex salts of ammonium and sodium ferriferrocyanides) and silicate pigments (ultramarines (Na7Al(>Si6θ24S3) etc.). The use of inorganic cadmium, lead, zinc and chromate pigments should be avoided because of their toxicity. The following organic and inorganic pigments among others may be used in colourant pastes (trade names vary depending on the manufacturer): Organic pigments: Chemical name CI. (= ( - yellows Flavanthrone PY 24 Monoazo PY 74 Diarylide PY 83 Monoazo PY 97 Anthrapyrimidine PY 108 Isoindolinone PY 109 Isoindolinone PY 110 Benzimidazolone PY 120 Disazo condensation PY 128 Quinophthalone PY 138 Isoindoline PY 139 Benzimidazolone PY 151 Benzimidazolone PY 154 Bisacetoacetarylide PY 155 Isoindolinone PY 173 B enzimidazolone PY 175 Benzimidazolone PY 194 - oranges Benzimidazolone P0 36 Perinone P0 43 Pyranthrone P0 51 Benzimidazolone P0 62 Pyrazoloquinazolone P0 67 Isoindoline P0 69 - reds BONA Mn PR 48:4 BONA Mn PR 52:2 Thioindigo PR 88 Naphthol AS PR 112 Quinacridone PR 122 Perylene PR 123 Disazo condensation PR 144 Disazo condensation PR 166 Anthantrone PR 168 Naphthol AS PR 170 Anthraquinone PR 168 Perylene PR 178 Perylene PR 179 Naphthol AS PR 188 Quinacridone PR 202 Disazo condensation PR 242 Pyrazoloquinazolone PR 251 Naphthol AS PR 253 Diketo pyrrolo pyrrol PR 254 Diketo pyrrolo pyrrol PR 264 - violets Quinacridone PV 19 Dioxazine PV 23 Perylene PV 29 Dioxazine PV 37 - blues Phthalocyanine α-mod. PB 15:2 Phthalocyanine β-mod. PB 15:3 Phthalocyanine β-mod. PB 15:4 Phthalocyanine ε-mod. PB 15:6 Metal-free phthalocyanine PB 16 Indanthrone PB 60 - greens Phthalocyanine PG 7 Phthalocyanine PG 36 Disazo condensation PBr23 Benzimidazolone PBr25 Isoindoline PBr38 Aniline PBkl Perylene PBk31 Perylene PBk32 Inorganic pigments: yellows Iron oxide PY42 Nickel rutile PY53 Bismuth vanadate PY184 reds Iron oxide PR 101 - violets Ultramarine PV15 blues Iron Blue PB27 Cobalt PB28 Ultramarine PB29 Cobalt PB36 - greens Chromium oxide PG17 Cobalt PG26 Cobalt PG50 browns Iron oxide PBr6 Umbra PBr7 Chrome rutile PBr24 blacks Lamp Black PBk6 Carbon Black PBk7 Iron oxide PBkll Spinel Black PBk22 Iron copper PBk23 Cobalt PBk27 Chrome oxide PBk 30 Colourants may contain in addition to coloured pigments also white pigments and extender pigments, for example: Chemical name CI. (= Colour Index) Titanium dioxide PW 6 Lithopone PW 5 Aluminium silicate PW 19 Mica PW 20 Barium sulphate PW 21 Barium sulphate, baryte PW 22 Aluminium hydrate PW 24 Talc PW 26 Silica PW 27 In selecting pigments attention is paid to the various types of paint for which the colourants are used. Important pigment properties besides colour, hiding power and tinting strength are also reactivity in acidic or alkaline conditions, ease of dispersion (wetting properties, oil absorption), fineness (average particle size and particle size distribution), specific area, brightness, lightfastness, resistance to chemicals, exterior durability and heat resistance. Pigments are usually delivered in powder form (particle size 20-100 μm) or granu¬ late form (particle size 2000-5000 μm), in which pigment crystals i.e. primary particles form loosely bonded agglomerates or aggregates as smaller and denser clusters. The average size of primary particles of organic pigments is from 0.01 to 0.1 μm, for inorganic and white pigments with good opacity from 0.1 to 1.0 μm, and for extender pigments from 1 to 5 μm. The purpose of grinding is to reduce the particle size of pigments sufficiently fine to achieve a desired shade with maximum tinting strength. A variety of pigments can be used to produce colourants ofthe present invention, also pigments with poor dispersibility, like quinacridones. Diluent component (B ) To minimize harmful environmental impact of a colourant, attention is paid to select rapidly biodegradable organic solvents as a diluent for colourants ofthe present invention. The solvents evaporate during drying/curing phase and therefore the rest ofthe colourant remaining in the paint film is by no means readily biodegradable. Substances are considered to be readily degradable ifthe following levels of biodegradation are achieved in a 28 day biodegradation study (test instructions of OECD or EU): in tests based on dissolved organic carbon (DOC): 70 % in tests based on oxygen consumption or carbon dioxide generation: 60 % ofthe theoretical maximum. These levels of biodegradation must be achieved within 10 days from the start of degradation, which point is taken as the time when 10 % ofthe substance has been degraded. In addition, the ratio of biological and chemical consumption of oxygen can be used in the determination of biodegradability. Ifthe BOD5/COD ratio (subindex means 5 days' test period) is greater than 0.5, the substance can be considered readily biodegradable. The diluent should contain mainly solvents that do not need a special danger classi¬ fication for a health or environmental hazard. Part of readily biodegradable products, such as 2-butanol (BOD5/COD = 0.89) have been classified as harmful to health and/or the environment and they do not fulfill the said requirement. Solvents ofthe present invention may not contain aromatic hydrocarbons. In selecting a solvent e.g. Hansen solubility parameters δr_)_δp.δH (D = "dispersion", P = "polar" and H = "hydrogen"), relative volatility (=100 with n- butylacetate) and odour must be taken into account. The solubility parameter range of a diluent must enable combinations with various types of paints. Volatility requirements partly depend on the type of paint product the colourant is intended for. Colourants for stoving enamels, for example, may contain solvents with lower volatility than for air drying paints. At least 20 % by weight, preferably 20-50 % by weight, of a colourant diluent ofthe present invention must comprise of esters of lactic acid, i.e. esters of 2-hydroxypropane acid and alcohols like methanol, ethanol, propanols or butanols ofthe following general formula: CH3-CH(OH)-CO-OR (lactate) where R = C \ -C4 -alkyl . It is most preferable to use ethyl or isopropyl lactate with relative volatilities of 22 and 18 respectively. These together with colourant binders ofthe present invention form solutions with low viscosity and good pigment wetting/dispersing properties. They are furthermore water-soluble, non-harmful to the environment (CO2 and H2O as biodegradation products), practically harmless to health, stable at normal temperatures and mild odoured. Lower lactates are extremely well suited as solvents for a large variety of paint binders. Their good pigment wetting ability is most likely due to the fact that the molecule has both a polar hydroxyl group and an ester group. The diluent of a colourant ofthe present invention may comprise from 0 to 80 % by weight, preferably from 50 to 80 % by weight, of other solvents than lactates. Lower ethers or ether esters of propylene glycol may be used. The following commercially available grades (manufacturer Dow) are mentioned as an example: Chemical name Trade name Relative volatility PG monomethyl ether Dowanol PM 70 PG mono-n-butyl ether PnB 7 PG monomethyl ether acetate PMA 35 PG mono-n-butyl ether acetate PnBA 38 Di-PG-dimethyl ether Proglyde DDM 16 Common features of these solvents are low toxicity, biodegradability and mild odour. They can be distinguished from each other in volatility, water-solubility and chemical reactivity. Dowanol PnBA is a water- insoluble, inert, and readily bio- degradable solvent. It is suitable as a diluent for colourants used for the tinting of 2-component polyurethane coatings. The colourants for urethane coatings must not contain water or solvents, such as aliphatic C1-C4 -alcohols, that react easily with isocyanate groups. Conventional solvents other than alcohols, for example esters, ethers, ketones, aliphatic or alicyclic hydrocarbons etc. can be used as colourant diluents as long as they have not been classified as hazardous to health or the environment. On the other hand, a limiting factor for their use may be a strong odour (n-butyl acetate, ketones, etc.) Binder component (C) At least 70 % by weight, preferably 80-100 % by weight, ofthe binder of colourants ofthe present invention consists of a preferably low molecular mass (number average of molecular mass M n being within the range 500-3000) ketone aldehyde, ketone and/or aldehyde resin soluble in all major paint solvents including aliphatic hydrocarbons (white spirits, isoparaffins). The softening points of resins of this type are normally 65-90°C They form in the majority of organic solvents colourless low viscosity solutions enabling a high pigment concentration in a colourant. The diluent/binder combinations ofthe present invention have proven as very effective dispersion media for organic and inorganic colour pigments. Their good performance is manifested in that the colourants hardly require dispersing/wetting agents, the use of which has been until now almost a rule. The production ofthe ketone aldehyde resins and ketone resins suitable for colourants ofthe present invention usually involves polycondensation of aldol type with an alkaline catalyst and as reactants non-cyclic or cyclic aliphatic ketones (e.g. cyclohexanone) alone or more commonly with aliphatic aldehydes (e.g. formaldehyde). A more detailed description ofthe production of such resins is available in literature (e.g. DE-28 31613 and D. Katti & S. Patil: Paintindia, Vol. 43, No. 9 (Sept. 1993), pp. 15-20). The properties of these resins regarding e.g. softening point, solubility and compatibilty vary depending on raw material basis and production method. What they have in common is, however, that they are at least partially soluble in aliphatic hydrocarbons. Aldehyde resins are manufactured from urea and aliphatic aldehydes such as formaldehyde and isobutyraldehyde using cyclo- and polycondensation reactions. The manufacture of such resins is known from e.g. BASF patent specification EP-0 002 794 Bl and DE-OS-3 641 997 Al . The following commercially available products among others can be mentioned as suitable binders for colourants: Synthetic Resin EP TC, a ketone formaldehyde resin (softening point approximately 70°C) produced by Hiils AG; Laropal K 80, a polycondensation product of cyclohexanone (softening point 75-85°C) produced by BASF AG; and Laropal A 81, an aldehyde resin based on urea and aliphatic aldehydes (softening point 80-90°C) produced by BASF AG. The mentioned resins are delivered as pellets soluble in hydrocarbons, alcohols, esters, ketones, glycol ethers etc. paint solvents. Although these compounds are typically soluble in aliphatic hydrocarbons, some of them may have only a limited solubility in dilute solutions of aliphatic hydrocarbons. Solutions made ofthe said resins in lactates combine well with solvent-borne paint products. Compatibilty tests have been carried out for a group of various types of paint with binders such as alkyd resins, modified alkyd resins (styrenated, urethane and silicone alkyds), thermoplastic and reactive acrylic resins, melamine and urea resins, polyester resins, epoxy resins and their combinations with vinyl polymers, nitrocellulose (NC) and cellulose acetate butyrate (CAB). The present invention allows the replacement of maximum 30 % by weight, preferably 0-20 % by weight, of ketone aldehyde, ketone and/or aldehyde resin with other suitable colourant binders such as certain modified thermoplastic acrylic resins, of which Plexigum P 28 (Rohm) and Disperse-Ayd 8 and 15 (Daniel Products) can be mentioned as examples. The resins are available as pellets (100 % solids content) or as solutions (50-70 % solids content) in organic solvents (PG monomethyl ether acetate, white spirit etc.). Additive component (D) Colourants ofthe present invention require additives only in exceptional cases. Additives comprise a total of 0-5 % (calculated as 100 % active matter) ofthe weight ofthe colourant. Additives may not contain components that are hazardous to health or to the environment. Dispersing agents may be added to colourants which contain pigments with poor dispersibility. Possible dispersing agents include ordinary, non-ionic (alkylether ethoxylates, alkylglucosides, alkylamide ethoxylates, esters of glycerol, sorbitan esters etc., but not alkylphenol derivates), anionic (fatty acid soaps, alkylbenzene- and alkylsulphonates, alkylsulphonate methylesters, alkylether- and alkylsulphates, alkylphosphates etc.) and ampholytic (alkylsulpho- and alkylbetaine, technical soya lecithins etc.) dispersing agents and often mixtures thereof. The use of so-called polymeric dispersing agents whose performance is based on steric stabilization of pigment is very advantageous in a non-aqueous medium. The polymeric dispersing agents are usually delivered diluted in an organic solvent to facilitate handling. Colourants containing polymeric dispersing agents have excellent storage stability, i.e. gloss, shade and other properties ofthe tinted paint do not change even during a long period of storaging. The amount to be added depends on the pigment used and is usually 2-10 %, in the present invention 0-5 % (calculated as 100 % active matter) ofthe colourant weight. Below are given a few examples of commercially available products: Solsperse (Zeneca Colours), Disperbyk 160 (Byk-Chemie), Elvacite (Du Pont) and Efka Polymer (Efka Chemicals) ranges of dispersing agents. More detailed information about their chemical structure, mechanism of function and applications can be found in manufacturers' product information and literature, e.g. J.D. Schofield, "Polymeric dispersants", Handbook of Coatings Additives, ed. L.J. Calbo, Marcel Dekker, Volume 2, pp. 71-104. Also other additives may be added to colourants. Most common of them are rheology additives which are used to improve the consistency, fluidity and similar rheological properties of a colourant. The amount to be added varies from 0 to 2 % of colourant weight (calculated as 100 % active matter). The present invention furthermore relates to the use ofthe mentioned colourant alone or as part of a series of colourants for solvent-borne paint products, including paints diluted in white spirits and paints with high solids content (so-called HS- paints). Examples The preparation of colourants ofthe present invention is illustrated with practical examples. Some comparative examples are included in which colourants were produced using methods of already known level of technology. Tinting tests were made using various types of base paints with the colourants. Preparation of colourants and colourant properties The following colourants were prepared (see Table 1) Examples Comparative examples 1. Iron oxide colourants (yellows) 1, 2, 3, 4, 5 A, B, C 2. Iron oxide colourants (reds) 6, 7 D 3. Quinacridone colourants 8, 9 E 4. Carbon black colourants 10, 11 F The colourants were tested (see Table 2) as such immediately after preparation on the following properties: Method a) Fineness of grind SFS-ISO 1524 b) Krebs-Stormer viscosity ASTM D 562 The stability of colourants was tested also after 6 weeks storage period using the same tests. An increase or decrease in the viscosity should remain within acceptable limits. Tinting tests with colourants Colourants were tested by tinting the following paint types: 1. Alkyd paint 2. Polyurethane paint 3. Epoxy paint. The formulae ofthe white base paints (so-called A base paints) used in the tinting tests are given in Table 3. The colourants are naturally suitable for tinting also other solvent-borne paint products ofthe same or different type, in addition to the said paint types. The tests were performed by dispensing colourant into a base paint and shaking the mixture in a paint shaker for 2 minutes. The following properties ofthe tinted paint were tested at standard conditions (temperature +23 °C and relative humidity 50 %): Method c) Flocculation Rub-out d) Gloss SFS 3632 and ISO 2813 e) Pendulum hardness SFS 3642 and ISO 1522 A flocculation test is carried out by adding 9.5 ml of a colourant to 250 ml of base paint. A draw-down ofthe tinted paint is made with an applicator (e.g. 150 μm) on a draw-down paper. As soon as the draw-down is almost surface dry a droplet of fresh paint is added on it and the wet paint is rubbed against the dry paint with a finger tip in circular movements until the paint becomes adherent. The test piece is then left to dry and the shade ofthe rubbed-out area is compared to the shade ofthe rest ofthe paint film. An eventual shade difference is a sign of flocculation which is rated using a relative scale from 0 to 3 : 0 = no flocculation 3 = strong flocculation. The acceptance ofthe added colourants in a base paint of a tinting system is critical in the sense that the less flocculation occurs the better it is for achieving e.g. reproducibility of a shade. In pendulum hardness and gloss tests 25 ml of colourant is added to 250 ml of base paint. Two draw-downs are made on glass plates, one with a 150 μm and one with a 300 μm applicator. The hardening process is followed by measuring pendulum hardness for both film thicknesses after 1, 3, 7 and 14 days of drying. Gloss values at 60° are measured after 14 days with a glossmeter. In a tinting system colourants may not affect the physical properties of base paints too much. Colourants are not suitable for tinting if, for example, the loss of gloss is significant. The results of tests with the prepared test colourants are shown in Table 4 and 5. SUMMARY Colourant composition The colourants of comparative examples from A to C and of examples from 1 to 5 are yellow iron oxide colourants. Colourant A was prepared according to example Al in the patent specification EP-507 202 by grinding the pigment to a particle size of less than 10 μm. Colourant B has the same dispersion medium as the colourant A. The pigment content was, however, increased from 35 % to 44 %, i.e. to the same level as in example 2. The diluent of colourant C is xylene, formerly common in use. In other respects the composition is similar to that ofthe colourant 3. Colourants A and B contain 6-7 % of a dispersing agent, whereas colourants 1-5 and C do not contain any dispersing agent at all. The binder ofthe red iron oxide colourant of comparative example D is an acrylic resin (Disperse- Ayd 15) delivered as a 60 % solution in propylene glycol mono- methyl ether acetate. Isopropyl lactate ofthe present invention was used as an auxiliary diluent. The colourant of example 6 has an aldehyde resin as the binder, whereas the colourant of example 7 an aldehyde resin combined with the above¬ mentioned acrylic resin. Quinacridones are organic pigments with poor dispersibility. Small amounts of dispersing agents may be added to colourants ofthe present invention to facilitate the grinding ofthe pigment. The colourant ofthe example 8 contains 0.2 %, the colourant ofthe example 9 contains 2.5 % of a polymeric dispersing agent. Colourant ofthe comparative example E was made up using similar pigmentation as in the colourants of examples 8 and 9 but the same dispersing medium as used for the colourant A. Colourant E contains approximately 9 % of a non-ionic dispersing agent. Carbon blacks are also demanding pigments when used in colourant formulations. Therefore, also the black colourants 10, 11 and F all with pigment content of 8.6 % were prepared. The colourants of examples 10 and 11 differ from each other as to both their binders and diluents. Neither ofthe colourants contains a dispersing agent. The dispersion medium ofthe comparative example F is the same as in colourant A. The colourant F contains approximately 10 % of a dispersing agent. The said contents of dispersing agent are calculated as 100 % active matter. Colourant properties All colourants, excluding comparative examples C and E, were easy to grind and their KU viscosity and stability were within tolerances. Tinting tests in paints The colourants (examples 1-11) of the present invention did not flocculate in any of the test paints. The colourants ofthe comparative examples, except D, flocculated in two or three ofthe test paints (colourants B and F worst). Epoxy paints suffered from a reduction in gloss with colourants B and D of comparative examples; with colourant B the values were approximately half of the values of an untinted paint. Gloss values did not change essentially in examples where colourants ofthe present invention or colourants A, C, E and F of comparative examples were used. Tinting had hardly any influence on the development of pendulum hardness of alkyd paint films that were applied with an 150 μm applicator and there was rather an increase in hardness of films applied with a 300 μm applicator. The average hardness of polyurethane and epoxy coatings decreased; slightly in films applied with an 150 μm applicator, more in films applied with a 300 μm applicator. Because the level of colourant addition was quite high (10 % by volume) and each colourant was added separately, the reduced pendulum hardness values mentioned are still acceptable. In practice colours are usually made by mixing several colourants (according to the colour formula) and the added amounts are smaller. The effects of colourants on hardness and other film properties can be controlled by paying more attention for example to volatility ofthe solvent blends and solvent retentions ofthe binders used in coating/paint formulations. TABLE 1. Colourants Examples: Comparative examples: Composition (% by weight): 1 2 3 4 5 6 7 8 9 10 11 A B C D E F Pigment 43.0 44.0 41.2 47.6 41.2 61.9 61.9 16.6 16.6 8.6 8.6 35.0 44.0 41.2 61.9 16.6 8.6 Diluent 31.5 33.9 39.4 30.7 39.4 14.4 14.4 53.1 49.8 52.7 52.6 41.1 35.4 39.4 14.3 52.8 57.8 Binder (100 % solids) 25.5 22.1 19.4 21.8 19.4 19.0 19.0 29.8 28.0 38.7 38.8 15.6 13.4 19.4 19.0 20.0 21.9 Additives (diluted) 4.8 4.8 0.5 5.6 8.3 7.1 4.8 10.6 1 1.7 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 Dispersion medium: - Synthetic Resin EP-TC, ketone aldehyde resin (Huls) 25.5 22.1 9.7 16.3 9.7 29.8 28.0 38.7 19.4 9.7 - Laropal K 80, ketone resin (BASF) 9.7 9.7 - Laropal A 81 , aldehyde resin (BASF) 9.7 19.0 13.3 19.4 - Plexigum P 28, acrylic resin (Rohm) 5.4 15.6 13.4 20.0 21.9 - Disperse- Ayd 15, acrylic resin* (Daniel Products) 8.8 29.2 - Purasolv IPL, isopropyl lactate (Purac Biochem) 31.5 17.0 29.5 22.4 29.5 5.0 5.0 53.1 12.5 52.7 40.0 4.2 - Dowanol PMA (Dow) 17.0 9.9 8.3 9.9 5.0 2.0 12.6 39.6 34.2 50.9 55.8 - Dowanol PM (Dow) 4.3 4.3 17.4 - Dowanol PnBA (Dow) 19.9 l - Xylene 1.5 1.3 39.4 1.9 2.1 - Troysol UGA, 85 % non-ionic dispersing agent (Troy) 8.1 7.0 10.4 1 1.4 - Efka 46, 40 % polymeric dispersing agent (Efka) 0.5 - Disperbyk 163, 45 % polymeric dispersing agent (Byk) 4.3 4.3 5.6 4.3 - Bentone 34, thickener (Rheox) 0.2 0.1 0.2 0.2 - MPA 2000 X, thickener (Rheox) 0.5 0.5 0.5 Pigments: - Bayferrox 3910 (CI. PY 42) (Bayer) 43.0 44.0 41.2 47.6 41.2 35.0 44.0 41.2 - Bayferrox 130 M (CI. PR 101) (Bayer) 61.9 61.9 61.9 - Hostaperm Rotviolett ER 02 (CI. PV 19) (Hoechst) 16.6 16.6 16.6 - Spezialschwarz 6 (CI. PBk 7) (Degussa) 8.6 8.6 8.6 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 Diluent (does not contain diluent of additives): - lactate 100 50 75 73 75 35 35 100 25 100 76 0 0 0 29 0 0 - other solvent 0 50 25 27 25 65 65 0 75 0 24 100 100 100 71 100 100 Binder (100 %): , - ketone aldehyde, ketone and/or aldehyde resin 100 100 100 75 100 100 70 100 100 100 100 0 0 100 0 0 0 - other resin 0 0 0 25 0 0 30 0 0 0 0 100 100 0 100 100 100 t * 65 % solids in PG monomethyl ether acetate. TABLE 3. Base paints used in tinting tests % by weight 1) Alkyd paint/long oil alkyd, glossy: Millbase: - air-drying long-oil alkyd, 55 % in white spirit 20,0 - thickener 0,3 - dispersing agent 0,1 - Ca drier (10 % Ca) 0,4 - titanium dioxide (rutile) 22,3 Let down: - air-drying long-oil alkyd, 55 % in white spirit 50,0 - Co drier (10 % Co) 0,2 - Zr drier (12 % Zr) 0,9 - white spirit 5,6 - anti-skinning agent 0.2 100,0 2) Polyurethane paint/2-component, glossy: Component A: - OH functional acrylic resin, 60 % in xylene 49,0 - thickener 0,5 - anti-settling agent 0,5 - surfactant 0,3 - dispersing agent 0,2 - synthetic barium sulphate 7,5 - titanium dioxide (rutile) 19,0 - Shellsol A (Shell) 8,5 Component B: - aliphatic polyisocyanate, 75 % in solvent blend 12,5 - Dowanol PMA/xylene 1 : 1 - Dowanol PMA (Dow) 2.0 100,0 3) Epoxy paint/2-component: Component A: - bisphenol-A epoxy resin, 75 % in xylene 28,0 - urea/formaldehyde resin 2,0 - thickener 0,6 - anti-settling agent 0,6 - dispersing agent 0,3 - levelling agent 0,5 - titanium dioxide (rutile) 19,0 - talc 8,0 - barium sulphate 8,0 - Shellsol A 9,0 - isobutanol 5,4 Component B: - diethylene triamine adduct (hardener) 8,0 - xylene 3,2 - Dowanol PM (Dow) 4,0 - n-butanol 3.4 100,0 TABLE 4. Flocculation and gloss tests of Exampl es: Comp arative examples: colourants c) Flocculation test (0 = best, 3 = poor): 1 2 3 4 5 6 7 8 9 10 11 A B C D E F 1) Alkyd paint 0 0 0 0 0 0 0 0 0 0 0 1 2 1 0 1 0 2) Polyurethane paint 0 0 0 0 0 0 0 0 0 0 0 1 0 0 0 1 2 3) Epoxy paint 0 0 0 0 0 0 0 0 0 0 0 1 1 1 0 1 3 d) Gloss (glossmeter/60°, units): Time Blank test 1) Alkyd paint: - 150 μm applicator 14 d 93 93 93 88 90 90 92 88 89 90 - 300 μm applicator 14 d 93 93 93 89 90 90 93 89 89 90 2) Polyurethane paint: - 150 μm applicator 14 d 95 89 94 90 91 87 93 90 89 90 - 300 μm applicator 14 d 96 87 93 91 92 84 92 91 90 91 3) Epoxy paint: - 150 μm applicator 14 d 60 60 58 65 64 62 19 48 58 61 - 300 μm applicator 14 d 70 67 68 65 65 63 30 48 64 62 d = days blank test = with untinted base paint

Claims: Claims: 1. A colourant composition for solvent-borne paint products comprising 2-75 % by weight of a pigment component (A) consisting of one or more organic and/or inorganic pigments and possibly extender pigments, 10-60 % by weight of a diluent component (B) consisting of one or more organic solvents not being an aliphatic alcohol or aromatic hydrocarbon, 10-50 % by weight (calculated as 100 % non¬ volatile matter) of a binder component (C) consisting of one or more binders soluble in the diluent component (B), and 0-5 % by weight (calculated as 100 % active matter) of an additive component (D) consisting of one or more additives suitable for use in colourants, characterized in that 20-100 % ofthe total weight ofthe diluent component (B) consists of a biodegradable ester of lactic acid and a Cj-Cio- alcohol and 70-100 % ofthe total weight ofthe binder component (C) consists of a ketone aldehyde resin, ketone resin and/or aldehyde resin at least partially soluble in paint solvents including aliphatic hydrocarbons. 2. A colourant according to claim 1, characterized in that 20-50 % by weight with respect to the total weight ofthe diluent component (B) consists of a biodegradable ester of lactic acid and Cj-Cio alcohol. 3. A colourant according to claims 1 and 2, characterized in that the biodegradable ester of lactic acid and Ci -Cjo alcohol ofthe diluent component (B) is an ester which is a lactate ofthe following general formula CH3-CH(OH)-CO-OR where R is a Ci -C4 -alkyl group. 4. A colourant according to claim 3, characterized in that the biodegradable ester of lactic acid and C1-C4 ofthe diluent component (B) is an ethyl lactate or an isopropyl lactate. 5. A colourant according to any ofthe preceding claims, characterized in that 0- 80 % by weight, preferably 50-80 % by weight, with respect to the weight ofthe diluent component (B) consists of a C1-C4 alkyl ether or of a C1-C4 alkyl ether ester of an ethylene glycol or propylene glycol, preferably a propylene glycol monomethyl ether, propylene glycol monobutyl ether, propylene glycol monomethyl ether acetate, propylene glycol mono n-butyl ether acetate or dipropylene glycol dimethyl ether, preferably propylene glycol monobutyl ether acetate. 6. A colourant according to any ofthe preceding claims, characterized in that 80- 100 % by weight with respect to the total weight ofthe binder component (C) consists of a ketone aldehyde resin, ketone resin and/or aldehyde resin also soluble in aliphatic hydrocarbons. 7. A colourant according to any ofthe preceding claims, characterized in that the mentioned ketone aldehyde resin, ketone resin and/or aldehyde resin ofthe binder component (C) is a resin with a softening point between 65 and 90°C. 8. A colourant according to any ofthe preceding claims, characterized in that the mentioned ketone aldehyde resin, ketone resin and/or aldehyde resin ofthe binder component (C) is a resin with a number-average molecular mass M n in the range of 500-3000 g/mol. 9. A colourant according to any ofthe preceding claims, characterized in that the mentioned ketone aldehyde resin ofthe binder component (C) is a resin produced by polycondensation of aldol-type of non-cyclic or cyclic aliphatic ketones and aliphatic aldehydes. 10. A colourant according to any ofthe preceding claims, characterized in that the mentioned ketone resin soluble in aliphatic hydrocarbons ofthe binder component (C) is a resin produced by condensation of aldol-type of non-cyclic or cyclic aliphatic ketones. 11. A colourant according to any ofthe preceding claims, characterized in that the mentioned aldehyde resin soluble in aliphatic hydrocarbons ofthe binder component (C) is a resin produced by cyclo- or polycondensation reaction of urea and an aliphatic aldehyde. 12. A colourant according to any ofthe preceding claims, characterized in that 0- 30 % by weight, preferably 0-20 % by weight, with respect to the total weight ofthe binder component (C) consists of a thermoplastic acrylic resin. 13. A colourant according to any ofthe preceding claims, characterized in that the pigment component (A) consists of one or more organic pigments selected from the following pigment groups: azo pigments, metal-compex pigments, isoindolinone and isoindoline pigments, phthalocyanine pigments, quinacridone pigments, perinone and perylene pigments, anthraquinone pigments, diketopyrrolopyrrole pigments, dioxazine pigments, quinophthalone pigments and fluorecence pigments. 14. A colourant according to any ofthe preceding claims, characterized in that the pigment component (A) consists of one or more inorganic pigments selected from the following pigment groups: elementary pigments, oxide and oxidehydroxide pigments, oxide mixed-phase pigments, sulphide and sulphate pigments, chromate and chromate molybdate mixed-phase pigments, complex salt pigments and silicate pigments. 15. A colourant according to any ofthe preceding claims, characterized in that the additive component (D) consists of one or more additives suitable for use in colourants selected from non-ionic dispersing agents, anionic dispersing agents, ampholytic dispersing agents and/or polymeric dispersing agents. 16. A colourant according to any ofthe preceding claims, characterized in that the additive component (D) consists of one or more rheology additives suitable for use in colourants. 17. The use of a colourant according to any ofthe preceding claims in tinting solvent-borne, including white spirit containing, paint products and paint products having a high solids content (so-called HS-paints).

Inventors: ADOLFSSON MAJ-LEN CARITA, SALORANTA ARJA KAARINA, SILANDER MARIA KATARINA, VARILA SEIJA ANNELI, WIKSTEDT MARTTI VILHELM, ADOLFSSON, MAJ-LEN, CARITA, SALORANTA, ARJA, KAARINA, SILANDER, MARIA, KATARINA, VARILA, SEIJA, ANNELI, WIKSTEDT, MARTTI, VILHELM
Applicants: ADOLFSSON MAJ LEN CARITA, SALORANTA ARJA KAARINA, SILANDER MARIA KATARINA, TIKKURILA CPS OY, VARILA SEIJA ANNELI, WIKSTEDT MARTTI VILHELM, ADOLFSSON, MAJ-LEN, CARITA, SALORANTA, ARJA, KAARINA, SILANDER, MARIA, KATARINA, TIKKURILA OY, VARILA, SEIJA, ANNELI, WIKSTEDT, MARTTI, VILHELM
Application year: 1996
Main classification: C09D17
IPC codes: C09D17