Rubber compositions for tire tread

Abstract: A rubber composition for use in a tread of a pneumatic tire comprises particular amounts of particular nitrogen-containing compound and particular proton acid or derivative thereof based on 100 parts by weight of rubber ingredient, and develops an excellent gripping performance.

Description: This invention relates to a rubber composition for a tire tread developing an excellent gripping performance as well as a pneumatic tire using the same. Recently, it has been strongly demanded to provide pneumatic tires having higher running performances accompanied with improvement of automobile performances, pavement of roads and development of expressway networks. As the running performances of the tire become higher, the automobile can be run accurately and safely at a higher speed. Particularly, the gripping performance exemplified by acceleration performance and braking performance is an important requirement in the tire. In order to obtain a high gripping performance, there has hitherto been proposed a method wherein styrene-butadiene copolymer rubber having a high bound styrene content as a rubber having a high glass transition temperature was used in the rubber composition for the tire tread. According to this method, however, the improvement of the gripping performance is obtained, but there is caused a problem that the value of tan δ lowers with the rise of rubber temperature during the running of the tire and hence the gripping performance rapidly lowers. In order to prevent the degradation of the gripping performance due to the temperature rise, there is proposed a technique of using a copolymer rubber obtained by copolymerizing a monomer such as 1,3-butadiene, styrene, isoprene or the like with a methacrylate compound or acrylate compound containing diphenyl phosphate group such as diphenyl-2-methacryloyloxyethyl phosphate, diphenyl-2-acryloyloxyethyl phosphate or the like (see JP-A-59-187011). However, this technique can not be applied to natural rubber, but also undesirably damages properties inherent to a polymer such as styrene-butadiene copolymer rubber or polybutadiene rubber in accordance with the production conditions. On the other hand, there is a method of increasing the value of tan δ in the rubber composition by using a compounding system filled with great amounts of process oil and carbon black. According to this method, the gripping performance is improved, but the fracture properties and wear resistance are considerably degraded, so that the filling amount is critical and hence it is difficult to render the gripping performance to the required high level. There is another method wherein particular amounts of particular imidazole compounds or imidazoline compounds and particular proton acid derivatives are compounded with the rubber ingredient to increase the value of tan δ and the resulting rubber composition is used in the tire tread to improve the gripping performance (see JP-A-63-139931). In this method, the antiscorching property is somewhat improved as compared with the method described in JP-A-63-10645, but has not yet reached a practical level. It is, therefore, an object of the invention to solve the aforementioned problems of the conventional techniques and to provide rubber compositions having a good scorch time and developing an excellent gripping performance as well as pneumatic tires using the same. According to the invention, there is provided a rubber composition for use in a tire tread comprising, based on 100 parts by weight of rubber ingredient consisting of natural rubber and/or synthetic rubber: 0.1-50 parts by weight of at least one nitrogen-containing compound selected from lactams having a carbon number of 4-19 in a heterocyclic ring and represented by the following formula: (wherein each of R 1 and R 2 is a straight or branched chain alkyl group having a carbon number of 1-8, a hydrogen atom, a phenyl group, or a phenyl group substituted with an alkyl group having a carbon number of 1-8 and wherein R' and R 2 may be the same or different); and 0.1-50 parts by weight of at least one proton acid or derivative thereof selected from the group consisting of succinic acid, resin acid, maleic acid, benzoic acid, p-methoxybenzoic acid, p-chlorobenzoic acid, p-nitrobenzoic acid, cinnamic acid, d-naphthylcarboxylic acid, phthalic acid, trimellitic acid, pyromellitic acid, anhydrous phthalic acid, naphthoic acid, 4,4'-butylidene-bis(3-methyl-6-tert-butylphenol), 4,4'-thiobis (3-methyl-6-butylphenol), triethyleneglycol-bis[3-(3-tert-butyl-5-methyl-4-hydroxyphenyl) propionate], and 1,1'-bis(4-hydroxyphenyl) cyclohexane. In the rubber composition according to the invention, the proton acid or derivative thereof is selected from succinic acid, resin acid, maleic acid, benzoic acid, p-methoxybenzoic acid, p-chlorobenzoic acid, p-nitrobenzoic acid, cinnamic acid, d-naphthylcarboxylic acid, phthalic acid, trimellitic acid, pyromellitic acid, anhydrous phthalic acid, naphthoic acid and certained defined phenolic derivatives. In a pneumatic tire according to the invention, the above-defined rubber composition is used in a tread portion of the tire. The rubber ingredient used in the invention is natural rubber, synthetic rubber or a blend thereof. The synthetic rubber may be synthetic polyisoprene rubber, polybutadiene rubber, styrene-butadiene rubber or the like. The lactams comprising the nitrogen-containing compounds used in the invention include ε-caprolactam, ω-heptalactam, ω-laurolactam, N-phenyl-ω-laurolactam, and compounds in which each of R 1 and R 2 is -H or -CH 3 . Particularly, ω-laurolactam is most preferable. In the formula showing the nitrogen-containing compounds, the reason why each of R 1 and R 2 is restricted to an alkyl group having a carbon number of 1-8 or the like is due to the fact that if the carbon number exceeds the upper limit, the molecular weight of the nitrogen compound is too large and hence the amount of the nitrogen-containing compound compounded becomes too large. Further, the reason why the carbon number constituting the heterocyclic ring is limited to 4-19 is due to the fact that the lactams having such a carbon number are available in industry. Particularly, lactams having a carbon number of 4-12 are preferable in view of properties relating to the compounding amount and the like. The nitrogen-containing compound used in the invention has an effect of enhancing the interaction between rubber molecules to provide a rubber composition having a large value of tan δ even at a gripping zone (about 30°C). According to the invention, therefore, these nitrogen-containing compounds may be used alone or in admixture of two or more compounds. The reason why the amount in total of the nitrogen-containing compound compounded is restricted to 0.1-50 parts by weight based on 100 parts by weight of the rubber ingredient is due to the fact that when the amount is less than 0.1 part by weight, the effect aimed at by the invention can not be obtained, while when it exceeds 50 parts by weight, the effect corresponding to the increase of the amount is not obtained but also the properties after vulcanization are badly influenced to bring about a poor result. When the nitrogen-containing compounds are compounded with the rubber ingredient, they may be mixed prior to the compounding or may separately be compounded with the rubber ingredient. The proton acids and derivatives thereof used in the invention may be used alone or in admixture of two or more compounds. The derivatives of proton acids, are selected from 4,4'-butylidene-bis (3-methyl-6-tert-butylphenol), 4,4'-thiobis(3-methyl-6-butylphenol), triethyleneglycol-bis[3-(3-tert-butyl-5-methyl-4-hydroxyphenyl) propionate], and 1,1'-bis(4-hydroxyphenyl) cyclohexane. The reason why the amount in total of the proton acid and derivatives thereof compounded is limited to 0.1-50 parts by weight based on 100 parts by weight of the rubber ingredient is due to the fact that when the amount is less than 0.1 part by weight, a sufficient effect can not be developed, while when it exceeds 50 parts by weight, there is a possibility of badly influencing the other properties. If necessary, various additives usually used in the rubber industry such as fillers, softening agents, antioxidants, vulcanization accelerators, accelerator activators, vulcanizing agents and the like may be added to the rubber composition according to the invention within a range of usual amounts. The following examples are given in illustration of the invention and are not intended as limitations thereof. An unvulcanized rubber composition is prepared according to a compounding recipe as shown in Table 1. Styrene-butadiene rubber 100 parts by weight Aromatic oil 17 parts by weight Carbon black ISAF 75 parts by weight Zinc white 2.5 parts by weight Stearic acid 2 parts by weight N-t-butyl-2-benzothiazyl sulfenamide 1.5 parts by weight Sulfur 1.5 parts by weight Bisphenolic antioxidant (proton acid) 4.5 parts by weight Nitrogen-containing compound (see Table 2) 0.03 mol As to each of the resulting unvulcanized rubber compositions (Examples 1-3 and Comparative Examples 1-2), a Mooney scorch time t 5 is measured at 130°C according to a method defined in JIS, and a value of tan δ at 30°C in a vulcanizate after the vulcanization of the unvulcanized rubber composition is measured by using a testing machine for the measurement of viscoelasticity made by Rheometrix Corp. under a condition of a dynamic strain of 1% to obtain results as shown in Table 2. As seen from Table 2, when using the nitrogen-containing compound according to the invention, the scorch time is improved as compared with Comparative Example 2 using imidazole. Furthermore, it is understood that the value of tan δ at 30°C is improved by using the nitrogen-containing compound and proton acid according to the invention together. An unvulcanized rubber composition is prepared according to a compounding recipe as shown in Table 3 and then vulcanized. Thereafter, the value of tan δ at 30°C in the vulcanizate is measured in the same manner as in Example 1 to obtain results as shown in Table 4. Styrene-butadiene rubber 100 parts by weight Aromatic oil 17 parts by weight Carbon black ISAF 75 parts by weight Zinc white 2.5 parts by weight Stearic acid 2 parts by weight N-t-butyl-2-benzothiazyl sulfenamide 1.5 parts by weight Sulfur 1.5 parts by weight ω-laurolactam 3 parts by weight Proton acid (see Table 4) 4.5 parts by weight Comparative Example 3 Example 4 Example 5 Example 6 Proton acid none 4,4'-butylidene-bis(3-methyl-6-tert-butylphenol) benzoic acid p-methoxybenzoic acid Value of tan δ (30°C) 0.3751 0.4605 0.4874 0.4830 As seen from Table 4, the effect of increasing the value of tan δ is obtained by using various proton acids. Particularly, this effect is large in Examples 4-6 using 4,4'-butylidene-bis(3-methyl-6-tert-butylphenol), benzoic acid and p-methoxybenzoic acid, respectively. A pneumatic tire having a tire size of 195/65R15 is manufactured by using in a tread a general-purpose rubber composition (Comparative Example 4), a general-purpose rubber composition compounded with 3 parts by weight of ω-laurolactam, 3.4 parts by weight of benzoic acid and 1.1 parts by weight of 4,4'-butylidene-bis(3-methyl-6-tert-butylphenol) (Example 7), a high-performance rubber composition (Comparative Example 5), or a high-performance rubber composition compounded with 5 parts by weight of ω-laurolactam and 7.5 parts by weight of 4,4'-butylidene-bis(3-methyl-6-tert-butylphenol) (Example 8). A steering stability test on a circuit course of dry road surface is carried out by two professional test drivers. The steering stability is evaluated by evaluation points of 0: equal to control, +1: level of feeling the improvement of property by a professional driver, +2: level of feeling the improvement of property by a sensitive driver and +3: level of feeling the improvement of property by a general driver to obtain results as shown in Table 5. Comparative Example 4 Example 7 Comparative Example 5 Example 8 ω-laurolactam none 3 parts by weight none 5 parts by weight 4,4-butylidene-bis(3-methyl-6-tert-butylphenol) none 1.1 parts by weight none 7.5 parts by weight Benzoic acid none 3.4 parts by weight none none Evaluation point in steering stability test on dry road control +2 control +2 As seen from Table 5, the running performance on dry road is improved in the rubber composition according to the invention as compared with the conventional rubber composition. A high-performance unvulcanized rubber composition is prepared according to a compounding recipe as shown in Table 6 and then vulcanized. Thereafter, the value of tan δ at 30°C in the vulcanizate is measured in the same manner as in Example 1 to obtain results as shown in Table 7. Furthermore, the above rubber composition is used in a tread portion to manufacture a pneumatic tire having a tire size of 195/65R14 and then the steering stability on dry road is measured in the same manner as in Example 7 to obtain results as shown in Table 7. Moreover, the rubber composition of Comparative Example 7 does not contain 4,4'-butylidene-bis(3-methyl-6-tert-butylphenol). Styrene-butadiene rubber 100 parts by weight Aromatic oil 20 parts by weight Carbon black ISAF 75 parts by weight Zinc white 2.5 parts by weight Stearic acid 2 parts by weight N-t-butyl-2-benzothiazyl sulfenamide 1.5 parts by weight Sulfur 1.5 parts by weight 4,4'-butylidene-bis(3-methyl-6-tert-butylphenol) 4.5 parts by weight Nitrogen-containing compound (see Table 7) 0.0265 mol Comparative Example 6 Comparative Example 7 Example 9 Example 10 Example 11 Nitrogen-containing compound - ω-laurolactam ε-caprolactam ω-heptalactam ω-laurolactam Compounding amount (parts by weight) 0 5.23 3.00 3.37 5.23 Value of tan δ (30°C) 0.388 0.379 0.543 0.558 0.586 Evaluation point in steering stability test on dry road control ±0 +2 +2 +3 As seen from Table 7, the value of tan δ and the running performance on dry road are excellent in all examples. As mentioned above, according to the invention, the specified amounts of the particular nitrogen-containing compound and the particular proton acid or derivative thereof are compounded with the rubber ingredient, whereby the value of tan δ in the resulting rubber composition at the gripping zone (about 30°C) can be improved. Therefore, when such a rubber composition is used in the tread portion of a pneumatic tire, the lowering of the tan δ value accompanied with the tire temperature rise during the running of the tire is prevented and also the gripping performance during highspeed running is considerably improved. Furthermore, the antiscorching property is largely improved at the practical level.

Claims: A rubber composition for use in a tire tread comprising, based on 100 parts by weight of rubber ingredient consisting of natural rubber and/or synthetic rubber: 0.1-50 parts by weight of at least one nitrogen-containing compound selected from lactams having a carbon number of 4-19 in a heterocyclic ring and represented by the following formula: (wherein each of R 1 and R 2 is a straight or branched chain alkyl group having a carbon number of 1-8, a hydrogen atom, a phenyl group, or a phenyl group substituted with an alkyl group having a carbon number of 1-8 and wherein R 1 and R 2 may be the same or different); and 0.1-50 parts by weight of at least one proton acid or derivative thereof selected from the group consisting of succinic acid, resin acid, maleic acid, benzoic acid, p-methoxybenzoic acid, p-chlorobenzoic acid, p-nitrobenzoic acid, cinnamic acid, d-naphthylcarboxylic acid, phthalic acid, trimellitic acid, pyromellitic acid, anhydrous phthalic acid, naphthoic acid, 4,4'-butylidene-bis(3-methyl-6-tert-butylphenol), 4,4'-thiobis (3-methyl-6-butylphenol), triethyleneglycol-bis[3-(3-tert-butyl-5-methyl-4-hydroxyphenyl) propionate], and 1,1'-bis(4-hydroxyphenyl) cyclohexane. A rubber composition as claimed in claim 1, characterized in that said lactam is ε-caprolactam, ω-heptalactam, ω-laurolactam, N-phenyl-ω-laurolactam, and compounds in which each of R 1 and R 2 is -H or -CH 3 . A pneumatic tire comprising a tread portion made from a rubber composition as claimed in claim 1 or 2.

Inventors: HATAKEYAMA KAZUYA, NOHARA DAISUKE, HATAKEYAMA, KAZUYA, NOHARA, DAISUKE
Applicants: BRIDGESTONE CORP, BRIDGESTONE CORPORATION
Application year: 1996
Main classification: C08K5
IPC codes: C08K5