Liquid sorptive coating for ink jet recording media

Abstract: The present invention is directed to a liquid sorptive coating for an ink jet recording media. The liquid sorptive coating contains a hydroxyalkyl methylcellulose and at least one nitrogen-containing component. The hydroxyalkyl methylcellulose is preferably present in the coating in an amount of about 70 to about 98%, based on the amount of solids in the coating. The hydroxyalkyl methylcellulose also preferably has a hydroxyalkyl content of from about 3 mol.% to about 15mol.% and a methoxyl content of from about 15mol.% to about 28 mol.%.

Description: Field of the invention This invention relates to an ink jet printing process and to a liquid sorptive coating that can be used for ink jet recording media for use in such printing process. Background of the invention Coatings used for ink jet recording media have to meet a number of performance requirements. These requirements include dry time, color density, resolution, tack, color fidelity, lightfastness, as well as cost. For pigment based inks, ink layer cracking is also an important performance parameter. There are many materials, both organic and inorganic, that have been proposed for this application. Among them, cellulose derivatives have shown promising performance. For example, U.S. Patent 4,555,437 describes a hydroxyethylcellulose coating, U.S. Patent 4,269,891 describes a carboxymethylcellulose coating and a hydroxyethylcellulose coating, U.S. Patent 4,575,465 and U.S. patent 5,141,797 describe hydroxypropyl cellulose, U.S. 4,592,954 describes a mixture of carboxymethyl cellulose and a polyethylene oxide, U.S. Patent 4,092,457 and U.S. Patent 4,868,581 generally mention cellulose ethers and cellulose derivatives. Japanese Patent Application 61-287782 generally describes water soluble cellulose derivative such as methyl cellulose, hydroxypropyl methyl cellulose or the like. Japanese Patent Application 61-1933879 describes water soluble cellulose prepared by substituting the -OH group of cellulose by another radical to impart water-soluble nature in admixture with polyvinyl pyrrolidone. EP-A-0 286 427 describes ink jet recording medium of a two layer structure comprising an ink-retaining underlayer which may comprise hydroxypropyl methyl cellulose and an ink-transporting surface layer which surface layer comprises a colorant fixing material to fix the ink colorant in the surface layer. However, not all cellulose derivatives perform well or equally. As a matter of fact, none of the specific cellulose derivatives described in the above-referenced patents give satisfactory performance. The success of a design based on cellulose derivatives depends upon the chemical nature and physical properties of the cellulose derivatives, such as functionality. Furthermore, cellulose derivatives alone seldom offer a design that is suitable for most commercial applications. Other functional components are usually needed to achieve desired results. Summary of the Invention The objective of the present invention is to provide an improved ink jet printing process and more particularly to provide an improved liquid sorptive coating to which the ink droplets are jetted in the process of the invention. Specifically, the invention provides a hydroxyalkyl methylcellulose based liquid sorptive coating that can be used for ink jet media. The coating contains a hydroxyalkyl methylcellulose and at least one nitrogen-containing component. The hydroxyalkyl methylcellulose used in the liquid sorptive coating preferably has a hydroxyalkyl content from 3 mol.% to 25 mol.% and a methoxyl content from 15 mol.% to 28 mol.%. Further, the hydroxyalkyl methylcellulose concentration in the liquid sorptive coating is preferably from 70% to 98% on a weight/weight bases. The nitrogen containing is preferably selected from the group consisting of poly(vinyl pyrrolidone), a polyimine, a gelatin and a quaternary polymer. Detailed Description of the Invention The following detailed description is provided as an aid to those desiring to practice the present invention. However, it is not to be construed as being unduly limiting to the present inventive discovery, since those of ordinary skill in the art will readily recognize that the embodiments of the inventors' discovery disclosed herein may be modified using standard techniques and materials known in the art. The liquid sorptive coating contains hydroxyalkyl methylcellulose and at least one nitrogen-containing component. The typical examples of hydroxyalkyl methylcellulose include hydroxypropyl methylcellulose, hydroxyethyl methylcellulose and hydroxybutyl methylcellulose, and the like. The hydroxyalkyl methylcellulose preferably has a hydroxyalkyl content of from 3mol.% to 25mol.% and a methoxyl content of from 15 mol.% to 28 mol.%. Typical examples of the nitrogen-containing component used in the inventive coating include poly(vinyl pyrrolidone), polyimines, gelatins, quaternary polymers (such as quaternary cellulose ethers), and the like. The liquid sorptive coatings of the present invention preferably contain 70% to 98% of hydroxyalkyl methylcellulose, more preferably 80% to 92%, on a weight/weight basis. The thickness of the inventive coatings is not particularly restricted, but should generally be in the range of from 2 grams per square meter to 30 grams per square meter. The liquid sorptive coatings of the present invention can be applied to transparent plastics, translucent plastics, matte plastics, opaque plastics or papers. Suitable polymeric materials for use as the base substrate include polyester, cellulose esters, polystyrene, polypropylene, poly(vinyl acetate), polycarbonate, and the like. Poly(ethylene terephthalate) film is a particularly preferred base substrate. Further, while almost any paper can be used as the base substrate, clay coated or polyolefin coated papers are particularly preferred as base substrate papers. The thickness of the base substrate is not particularly restricted, but should generally be in the range of from 25.4 to 254 µm (1 mil to 10 mils), preferably from 76.2 to 127 µm (3.0 mils to 5.0 mils). The base substrate may be pretreated to enhance adhesion of the polymeric underlayer coating thereto. According to a preferred embodiment of the invention, the liquid sorptive coating may further comprise 0.1% to 15% by weight of a particulate therein based on the weight of dry coating. For example, particulates that can be used in the coating to modify the surface properties of the coating include inorganic particulates such as silica, alumina, kaolin, glass beads, calcium carbonate, titanium oxide, and the like; and organic particulates such as polyolefins, polystyrene, starch, polyurethane, poly(methyl methacrylate), polytetrafluoroethylene, and the like. In practice, various additives may also be employed in the liquid sorptive coating. These additives are generally well-known in the art and include surface active agents that control the wetting or spreading action of the coating solutions, antistatic agents, suspending agents, and acidic compounds to control the pH of the coatings. Other additives may also be used, if so desired. The surface of the base substrate that does not bear the liquid sorptive coating may have a backing material placed thereon in order to reduce electrostatic charge, to reduce sheet-to-sheet friction and sticking and to reduce curl, if so desired. The backing material may either be a polymeric coating, a polymer film or a paper. Any of a number of coating methods that are well-known in the art may be employed to coat the liquid sorptive coating onto the substrate, such as roller coating, blade coating, wire-bar coating, dip coating, extrusion coating, air knife coating, curtain coating, slide coating, doctor coating or gravure coating. The following examples illustrate the invention. Solid content in the following Examples is presented as parts on a weight/weight basis. EXAMPLE 1 A coating composition was prepared according to the following formulation. Liquid Sorptive Coating Hydroxypropyl methylcellulose 4.5 parts Poly(vinyl pyrrolidone) 0.5 parts Water 95 parts The coating was applied to a polyester film (ICI Films) using a No. 60 Meyer rod. The liquid sorptive coating was dried at 130°C for 2 minutes. EXAMPLE 2 A coating composition was prepared according to the following formulation. Liquid Sorptive Coating Hydroxypropyl methylcellulose 5 parts Cationic derivative of hydroxyethyl cellulose 1 part Water 94 parts The coating was applied to a polyester film (ICI Films) using a No. 54 Meyer rod. The liquid sorptive coating was dried at 130°C for 2 minutes. COMPARATIVE EXAMPLE 1 A coating composition was prepared according to the following formulation. Liquid Sorptive Coating Hydroxyethyl cellulose 5 parts Cationic derivative of hydroxyethyl cellulose 1 part Water 94 parts The coating was applied to a polyester film (ICI) using a No. 60 Meyer rod. The liquid sorptive coating was dried at 130°C for 3 minutes. COMPARATIVE EXAMPLE 2 Liquid Sorptive Coating Carboxymethylcellulose 5 parts Water 95 parts The coating was applied to a polyester film (ICI Films) using a No. 60 Meyer rod. The liquid sorptive coating was dried at 130°C for 2 minutes. Samples from each of the above Examples (and Comparative Examples) were tested for black density, ink cracking and dry time. Test results are reported in Table 1, below. The samples were evaluated on a Hewlett Packard DeskJet 660C printer using HP 51629A and HP 51649A ink cartridges. The black ink density was measured with a Macbeth TD 904 densitometer using the beige filter setting. The results are the average of three measurements. The pigmented ink cracking was quantitatively rated with a numerical scale (0=worst, 5=best). When ink cracking is rated below 3, visible ink cracking is observed and the ink jet recording media are not suitable for many commercial applications. Dry time of the image was evaluated by blotting imaged samples with Xerox 4200 copier paper. The dry time is defined by the time when no ink transfer to the paper is observed. COMPARATIVE TESTING PERFORMANCE EVALUATION OF THE COATINGS Examples Black Density Ink Cracking Dry Time Ex. 1 1.8 4.0 <5 Minutes Ex. 2 1.6 3.0 <5 Minutes Comp. Ex. 1 0.9 1.0 >12 Minutes Comp. Ex. 2 1.1 0.0 >12 Minutes The comparative testing results provided in Table 1 show that the inventive coatings disclosed herein offer an unexpectedly superior and advantageous performance in optical density, ink cracking and dry time. As a result of these properties, the coatings of the present invention offer a great impact on overall image quality and applications for ink jet recording media.

Claims: An ink jet printing process, comprising jetting ink droplets onto a liquid ink sorptive coating, characterized in that ink droplets are jetted onto a coating that contains a hydroxyalkyl methylcellulose and at least one nitrogen containing component. An ink jet printing process according to claim 1, characterized in that said coating contains a hydroxyalkyl methylcellulose having a hydroxyalkyl content of from 3 to 25 mol.% and a methoxyl content of from 15 to 28 mol.%. An ink jet printing process according to claim 1, characterized in that said coating contains 70% to 98% of hydroxyalkyl methylcellulose, based on the total weight of solids in the coating. An ink jet printing process according to claim 3, characterized in that said coating contains 80 to 92% of hydroxylalkyl methylcellulose, based on the total weight of solids in the coating. An ink jet printing process according to claim 1, characterized in that said hydroxyalkyl methylcellulose is selected from the group consisting of hydroxypropyl methylcellulose, hydroxyethyl methylcellulose and hydroxybutyl methylcellulose. An ink jet recording medium comprising a liquid sorptive coating containing a hydroxyalkyl methylcellulose and at least one nitrogen-containing component, characterized in that said nitrogen-containing component is selected from the group consisting of poly (vinyl pyrrolidone), a polyimine, a gelatin and a quaternary polymer. A recording medium according to claim 6, characterized in that said liquid sorptive coating further contains an inorganic particulate that is selected from the group consisting of silica, alumina, kaolin, glass beads, calcium carbonate and titanium oxide. A recording medium according to claim 6, characterized in that said liquid sorptive layer further contains an organic particulate that is selected from the group of polyolefins, polystyrene, starch, polyurethane, poly(methyl methacrylate) and polytetrafluoroethylene.

Inventors: RUNDUS JOSHUA, SARGEANT STEVEN J, RUNDUS, JOSHUA, SARGEANT, STEVEN J.
Applicants: ARKWRIGHT INC, ARKWRIGHT INC.
Application year: 1996
Main classification: B41M5
IPC codes: B41M5, C09D11, C08J7