ADSORBENT FOR CESIUM ION AND METHOD OF MAKING AND USING

Abstract: A method comprises the step of spray-drying a slurry of potassium cobalt hexacyanoferrate (KCOHEX) particles to provide monodisperse, substantially spherical KCOHEX particles. In a further step the spherical KCOHEX particles are activated by heating until their color changes from dark green to purplish black. The particles can be used free flowing, in columns or beds, or entrapped in a porous, nonwoven, fibrous web or matrix, to selectively remove Cs ions from aqueous solutions.

Description: ADSORBENT FOR CESIUM ION AND METHOD OF MAKING AND USING The invention was made with U S Government support under Subcontract 203690-A-F 1 , with Battelle Memorial Institute, Pacific Northwest Laboratories, based on a Contract DE-AC06-76RLO- 1830 awarded by the Department of Energy The U S Government has certain rights in the invention Field of the Invention The present invention pertains to substantially spherical, monodisperse particles of potassium cobalt hexacyanoferrate and a method therefor, and a method of using the particles in loose form, in a column, or enmeshed in a porous web for extraction of cesium, particularly radioactive cesium (Cs), from solution The method is useful in the remediation of nuclear wastes Backeround of the Invention Potassium cobalt hexacyanoferrate is known in the art as an effective adsorbent for cesium ions and has found important use in removing radioactive cesium ions from nuclear wastes via an ion exchange process The method has been described, for example, in U S Patent No 3,296, 123, in "A Review of Information on Ferrocyanate Solids for Removal of Cesium from Solutions," P A Haas, Sep. Sa. Technol. 28 (17-18), 2479-2508 ( 1993), and in "Evaluation of Selected Ion Exchangers for the Removal of Cesium and Strontium from MVST W-25 Supernate," J L Collins, et al , ORNL/TM- 12938, April 1995, and references cited therein Granular potassium cobalt hexacyanoferrate, hereinafter referred to as "KCOHEX," has typically been prepared by a method described in U S Patent No 3,296, 123, wherein an aqueous acidic solution of potassium ferrocyanide is slowly mixed with an aqueous solution of cobalt nitrate, as shown in Formula I potassium ferrocyanide + cobalt nitrate — > KCOHEX + potassium nitrate I Water is removed by centrifugation, the wet cake is washed with water, then dried in an oven to form a dried solid mass. The solid mass is ground and sized, and particles of from about 150 micrometers to about 450 micrometers are packed into columns for subsequent exposure to radioactive wastes containing, in particular, Cesium-137. The method of preparing particulate KCOHEX suffers from two significant drawbacks First, grinding the dried solids must be done carefully so as to minimize formation of unusable fines Second, since a wide range of particle sizes results from grinding, the particulate must be sized through sieves These operations are time-consuming and inevitably cause loss of product As described in the references noted above, sized KCOHEX is then loaded into columns in order to remove cesium from radioactive waste solutions In order to process the large volumes of waste that are in need of treatment, columns of up to 60 cm in length and 14 cm in diameter have been used, and flow rates of 80 L/h have been achieved Spray-drying of solid materials is a method known in the art for preparation of useful solids See, for example, Kirk-Othmer Encyclopedia of Chemical Technology, 4th Ed , John Wiley & Sons, New York, 1993, Vol 8, p 475 - 519, particularly pp 505-508, and C Strumillo and T Kudra, "Drying Principles, Applications and Design," Gordon and Breach, New York, 1986, pp 352 - 359 However, in all of the reports of preparation and use of KCOHEX, a spray drying process has not been described Summary of the Invention Briefly, the present invention provides a method comprising the step of spray-drying a slurry of potassium cobalt hexacyanoferrate (KCOHEX) particles to provide monodisperse, substantially spherical KCOHEX particles In another aspect, the method further comprises the step of heating the spherical KCOHEX particles until their color changes from green to purplish-black. In a further aspect, the spherical KCOHEX particles can be used in columns or beds to selectively remove Cs ions from aqueous solutions. In yet another aspect, the loose KCOHEX particles can be introduced into a Cs ion containing solution, equilibrated with the solution, and then separated from the solution with Cs having replaced K in KCOHEX In a still further aspect, the spherical KCOHEX particles can be enmeshed in porous, nonwoven, fibrous webs. The webs can be used in solid phase extraction (SPE) procedures to selectively remove Cs ions from aqueous solutions In yet another aspect, the invention provides an SPE device comprising a pleated porous, fibrous non-woven SPE web comprising spherical, monodisperse potassium cobalt hexacyanoferrate particulate and poly(m- or p-terephthalamide) fibers enclosed in a cartridge device In yet another embodiment, the invention provides a method of removing cesium ions from an aqueous solution comprising passing the aqueous solution through a porous, fibrous non-woven SPE web comprising spherical, monodisperse potassium cobalt hexacyanoferrate particulate In another embodiment, the invention provides a method of removing cesium ions from an aqueous solution comprising passing the aqueous solution through an SPE column comprising spherical, monodisperse potassium cobalt hexacyanoferrate particulate In this application, "size" means the diameter of a spherical particle, "monodisperse" means a monomodal particle size distribution having a range of up to about 500 micrometers, preferably about 60 micrometers, and "drain time" means the time required to dewater a slurry of particles and fibers when making a sheet The advantages of the particles of the invention include reduced drain time by a factor of at least two compared to non-spherical, irregularly shaped, prior art particles typically obtained from a grinding process, when making a sheet article Further, the overall process yield in making a sheet article comprising the particles of the invention is 80-90 percent or more compared to a yield of about 60 percent when using prior art ground and sieved particles. Additionally, free-flowing spherical particles will pack more uniformly in columns, resulting in less channeling during extraction compared with irregularly shaped prior art KCOHEX particles Detailed Description of Preferred Embodiments It is now recognized that spherical KCOHEX particles can be prepared by mixing at 0° to 5°C an aqueous solution of potassium ferrocyanide (available from Aldrich Chemical Co., and many other suppliers) with an aqueous solution of cobalt nitrate, buffered to a pH of 5-6 using acetic acid as the buffering agent The immediately formed precipitate of KCOHEX is collected and thoroughly washed with water The wet KCOHEX precipitate which comprises particles of irregular shapes is slurried with liquid, preferably water, and then spray-dried preferably using a spinning disk atomizer and collecting the resulting substantially spherical KCOHEX particles having a size in the range of about 1 to 500 micrometers, preferably about 1 to 60 micrometers, more preferably 5 to 15 micrometers, with a most preferred average size of about 9 to 12 micrometers Preferably, the spherical KCOHEX particles are then heated until the color changes from green to purplish black but the particle size remains substantially unchanged Spherical KCOHEX particles in the size range of about 100 to 500 micrometers can be useful in industrial separations Spray-drying of the KCOHEX slurry can be accomplished using well-known techniques which include the steps of 1 ) atomization, using a spinning disk, of the material introduced into the dryer, 2) evaporation of moisture by contact of the material with hot gas, and 3) separation of dry product from the exhaust drying agent The slurry preferably has a solids content of less than 8 percent by weight, more preferably 7 5 percent by weight, to ensure smooth operation of the apparatus After spray-drying, the particles are dark green in color; they are free- flowing with most preferred average diameters in the range of 9-12 micrometers The particles of the invention can be enmeshed in various porous, fibrous, nonwoven webs or matrices Types of webs or matrices include fibrillated polytetrafluoroethylene (PTFE), microfibrous webs, macrofibrous webs, and polymer pulps 1. Fibrillated PTFE The PTFE composite sheet material of the invention is prepared by blending the particulate or combination of particulates employed with a PTFE emulsion until a uniform dispersion is obtained and adding a volume of process lubricant up to approximately one half the volume of the blended particulate Blending takes place along with sufficient process lubricant to exceed sorptive capacity of the particles in order to generate the desired porosity level of the resultant article Preferred process lubricant amounts are in the range of 3 to 200 percent by weight in excess of that required to saturate the particulate, as is disclosed in U S Patent No 5,071,610 The aqueous PTFE dispersion is then blended with the particulate mixture to form a mass having a putty-like or dough-like consistency The sorptive capacity of the solids of the mixture is noted to have been exceeded when small amounts of water can no longer be incorporated into the mass without separation This condition should be maintained throughout the entire mixing operation The putty-like mass is then subjected to intensive mixing at a temperature and for a time sufficient to cause initial fibrillation of the PTFE particles Preferably, the temperature of intensive mixing is up to 90°C, preferably it is in the range of 0° to 90°C, more preferably 20° to 60°C Minimizing the mixing at the specified temperature is essential in obtaining extraction media and chromatographic transport properties Mixing times will typically vary from 0 2 to 2 minutes to obtain the necessary initial fibrillation of the PTFE particles Initial mixing causes partial disoriented fibrillation of a substantial portion of the PTFE particles Initial fibrillation generally will be noted to be at an optimum within 60 seconds after the point when all components have been fully incorporated into a putty-like (dough-like) consistency Mixing beyond this point will produce a composite sheet of inferior extraction medium and chromatographic properties Devices employed for obtaining the necessary intensive mixing are commercially available intensive mixing devices which are sometimes referred to as internal mixers, kneading mixers, double-blade batch mixers as well as intensive mixers and twin screw compounding mixers The most popular mixer of this type is the sigma-blade or sigma-arm mixer Some commercially available mixers of this type are those sold under the common designations Banbury mixer, Mogul mixer, C W Brabender Prep mixer and C W Brabender sigma blade mixer Other suitable intensive mixing devices may also be used The soft putty-like mass is then transferred to a calendering device where the mass is calendered between gaps in calendering rolls preferably maintained at a temperature up to 125°C, preferably in the range of 0° to about 100°C, more preferably in the range of 20°C to 60°C, to cause additional fibrillation of the PTFE particles of the mass, and consolidation while maintaining the water level of the mass at least at a level of near the sorptive capacity of the solids, until sufficient fibrillation occurs to produce the desired extraction medium Preferably the calendering rolls are made of a rigid material such as steel A useful calendering device has a pair of rotatable opposed calendering rolls each of which may be heated and one of which may be adjusted toward the other to reduce the gap or nip between the two Typically, the gap is adjusted to a setting of 10 millimeters for the initial pass of the mass and, as calendering operations progress, the gap is reduced until adequate consolidation occurs At the end of the initial calendering operation, the resultant sheet is folded and then rotated 90° to obtain biaxial fibrillation of the PTFE particles Smaller rotational angles (e g , 20° to less than 90°) may be preferred in some extraction and chromatographic applications to reduce calender biasing, i.e., unidirectional fibrillation and orientation Excessive calendering (generally more than two times) reduces the porosity which in turn reduces the solvent wicking in thin layer chromatography (TLC) and the flow-through rate in the filtration mode. During calendering, the lubricant level of the mass is maintained at least at a level of exceeding the absorptive capacity of the solids by at least 3 percent by weight, until sufficient fibrillation occurs and to produce porosity or void volume of at least 30 percent and preferably 40 to 70 percent of total volume. The preferred amount of lubricant is determined by measuring the pore size of the article using a Coulter Porometer as described in the Examples below. Increased lubricant results in increased pore size and increased total pore volume as is disclosed in U S Patent No. 5,071 ,610. The calendered sheet is then dried under conditions which promote rapid drying yet will not cause damage to the composite sheet or any constituent therein. Preferably drying is carried out at a temperature below 200°C The preferred means of drying is by use of a forced air oven The preferred drying temperature range is from 20°C to about 70°C The most convenient drying method involves suspending the composite sheet at room temperature for at least 24 hours. The time for drying may vary depending upon the particular composition, some particulate materials having a tendency to retain water more than others The resultant composite sheet preferably has a tensile strength when measured by a suitable tensile testing device such as an Instron (Canton, MA) tensile testing device of at least 0 5 MPa The resulting composite sheet has uniform porosity and a void volume of at least 30 percent of total volume The PTFE aqueous dispersion employed in producing the PTFE composite sheet of the invention is a milky-white aqueous suspension of minute PTFE particles. Typically, the PTFE aqueous dispersion will contain about 30 percent to about 70 percent by weight solids, the major portion of such solids being PTFE particles having a particle size in the range of about 0 05 to about 0.5 micrometers The commercially available PTFE aqueous dispersion may contain other ingredients, for example, surfactant materials and stabilizers which promote continued suspension of the PTFE particles Such PTFE aqueous dispersions are presently commercially available from Dupont de Nemours Chemical Corp , for example, under the trade names Teflon™ 30, Teflon™ 30B or Teflon™ 42 Teflon™ 30 and Teflon™ 30B contain about 59 percent of about 61 percent solids by weight which are for the most part 0.05 to 0.5 micrometer PTFE particles and from about 5 5 percent to about 6.5 percent by weight (based on weight of PTFE resin) of non-ionic wetting agent, typically octylphenol polyoxyethylene or nonylphenol polyoxyethylene Teflon™ 42 contains about 32 to 35 percent by weight solids and no wetting agent but has a surface layer of organic solvent to prevent evaporation A preferred source of PTFE is FLUON™, available from ICI Americas, Inc Wilmington, DE It is generally desirable to remove, by organic solvent extraction, any residual surfactant or wetting agent after formation of the article In other embodiments of the present invention, the fibrous membrane (web) can comprise non-woven, macro- or microfibers preferably selected from the group of fibers consisting of polyamide, polyolefm, polyester, polyurethane, glass fiber, polyvinylhalide, or a combination thereof The fibers preferably are polymeric (If a combination of polymers is used, a bicomponent fiber may be obtained ) If polyvinylhalide is used, it preferably comprises fluorine of at most 75 percent (by weight) and more preferably of at most 65 percent (by weight) Addition of a surfactant to such webs may be desirable to increase the wettability of the component fibers 2. Macrofibers The web can comprise thermoplastic, melt-extruded, large-diameter fibers which have been mechanically-calendered, air-laid, or spunbonded These fibers have average diameters in the general range of 50 μm to 1 ,000 μm Such non-woven webs with large-diameter fibers can be prepared by a spunbond process which is well known in the art (See, e g , U S Patent Nos 3,338,992, 3,509,009, and 3,528, 129 ) As described in these references, a post-fiber spinning web-consolidation step (i e., calendering) is required to produce a self-supporting web Spunbonded webs are commercially available from, for example, AMOCO, Inc (Napierville, IL) Non-woven webs made from large-diameter staple fibers can also be formed on carding or air-laid machines (such as a Rando-Webber™ Model 12BS made by Curlator Corp , East Rochester, NY), as is well known in the art See, e g , U.S Patent Nos 4,437,271 , 4,893,439, 5,030,496, and 5,082,720 A binder is normally used to produce self-supporting webs prepared by the air-laying and carding processes and is optional where the spunbond process is used Such binders can take the form of resin systems which are applied after web formation or of binder fibers which are incorporated into the web during the air laying process Examples of common binder fibers include adhesive-only type fibers such as Kodel™ 43 UD (Eastman Chemical Products, Kingsport, TN) and bicomponent fibers, which are available in either side-by-side form (e g , Chisso ES Fibers, Chisso Corp , Osaka, Japan) or sheath-core form (e g , Melty 1 M Fiber Type 4080, Unitika Ltd , Osaka, Japan) Application of heat and/or radiation to the web "cures" either type of binder system and consolidates the web Generally speaking, non-woven webs comprising macrofibers have relatively large voids Therefore, such webs have low capture efficiency of small-diameter particulate (reactive supports) which is introduced into the web Nevertheless, particulate can be incorporated into the non-woven webs by at least four means First, where relatively large particulate is to be used, it can be added directly to the web, which is then calendered to actually enmesh the particulate in the web (much like the PTFE webs described previously) Second, particulate can be incorporated into the primary binder system (discussed above) which is applied to the non-woven web Curing of this binder adhesively attaches the particulate to the web Third, a secondary binder system can be introduced into the web Once the particulate is added to the web, the secondary binder is cured (independent of the primary system) to adhesively incorporate the particulate into the web Fourth, where a binder fiber has been introduced into the web during the air laying or carding process, such a fiber can be heated above its softening temperature This adhesively captures particulate which is introduced into the web Of these methods involving non-PTFE macrofibers, those using a binder system are generally the most effective in capturing particulate Adhesive levels which will promote point contact adhesion are preferred Once the particulate (reactive supports) has been added, the loaded webs are typically further consolidated by, for example, a calendering process This further enmeshes the particulate within the web structure Webs comprising larger diameter fibers (i e , fibers which average diameters between 50 μm and 1 ,000 μm) have relatively high flow rates because they have a relatively large mean void size 3. Microfibers When the fibrous web comprises non-woven microfibers, those microfibers provide thermoplastic, melt-blown polymeric materials having active particulate dispersed therein Preferred polymeπc materials include such polyolefins as polypropylene and polyethylene, pieferably further comprising a surfactant, as described in, for example, U S Patent No 4,933,229 Alternatively, surfactant can be applied to a blown microflbrous (BMF) web subsequent to web formation Polyamide can also be used Particulate can be incorporated into BMF webs as described in U S Patent No 3,971,373 Microflbrous webs of the present invention have average fiber diameters up to 50 μm, preferably from 2 μm to 25 μm, and most preferably from 3 μm to 10 μm Because the void sizes in such webs range fiom 0 1 μm to 10 μm, preferably from 0 5 μm to 5 μm, flow thiough these webs is not as great as is flow through the macrofibrous webs described above 4. Cast Porous Membranes Solution-cast porous membranes can be provided by methods known in the art Such polymeric porous membranes can be, for example, polyolefin including polypropylene, polyamide, polyester, polyvinyl chloride, and polyvinyl acetate fibers 5. Fibrous Pulps The present invention also provides a solid phase extraction sheet comprising a porous fibrous pulp, preferably a polymeric pulp, comprising a plurality of fibers that mechanically entrap active particles, and preferably a polymeric hydrocarbon binder, the weight ratio of particles to binder being at least 13 1 and the ratio of average uncalendered sheet thickness to effective average particle diameter being at least 125 1 Generally, the fibers that make up the porous polymeric pulp of the SPE sheet of the present invention can be any pulpable fiber (i e , any fiber that can be made into a porous pulp) Preferred fibers are those that are stable to radiation and/or to a variety of pHs, especially very high pHs (e g , pH = 14) and very low pHs (e g , pH = 1) Examples include polyamide fibers and those polyolefin fibers that can be formed into a pulp including, but not limited to, polyethylene and polypropylene Particularly preferred fibers are aromatic polyamide fibers and aramid fibers because of their stability to both radiation and highly caustic fluids Examples of useful aromatic polyamide fibers are those fibers of the nylon family Polyacrylic nitrile, cellulose, and glass can also be used Combinations of pulps can be used Examples of useful aramid fibers are those fibers sold under the trade name Kevlar™ (DuPont, Wilmington, DE) Kevlar I M fiber pulps are commercially available in three grades based on the length of the fibers that make up the pulp Regardless of the type of fiber(s) chosen to make up the pulp, the relative amount of fiber in the resulting SPE sheet (when dried) ranges from about 12 5 percent to about 30 percent (by weight), preferably from about 15 percent to 25 percent (by weight) Useful binders in the SPE sheet of the present invention are those materials that are stable over a range of pHs (especially high pHs) and that exhibit little or no interaction (i e , chemical reaction) with either the fibers of the pulp or the particles entrapped therein Polymeric hydrocarbon materials, originally in the form of latexes, have been found to be especially useful Common examples of useful binders include, but are not limited to, natural rubbers, neoprene, styrene-butadiene copolymer, acrylate resins, and polyvinyl acetate Preferred binders include neoprene and styrene-butadiene copolymer Regardless of the type of binder used, the relative amount of binder in the resulting SPE sheet (when dried) is about 3 percent to about 7 percent, preferably about 5 percent The preferred amount has been found to provide sheets with nearly the same physical integrity a sheets that include about 7 percent binder while allowing for as great a particle loading as possible. It may be desirable to add a surfactant to the fibrous pulp, preferably in small amounts up to about 0.25 weight percent of the composite Because the capacity and efficiency of the SPE sheet depends on the amount of particles included therein, high particle loading is desirable The relative amount of particles in a given SPE sheet of the present invention is preferably at least about 65 percent (by weight), more preferably at least about 70 percent (by weight), and most preferably at least about 75 percent (by weight) Additionally, the weight percentage of particles in the resulting SPE sheet is at least 13 times greater than the weight percentage of binder, preferably at least 14 times greater than the weight percentage of binder, more preferably at least 15 times greater than the weight percentage of binder Regardless of the type or amount of the particles used in the SPE sheet of the present invention, they are mechanically entrapped or entangled in the fibers of the porous pulp In other words, the particles are not covalently bonded to the fibers Objects and advantages of this invention are further illustrated by the following examples The particular materials and amounts thereof, as well as other conditions and details, recited in these examples should not be used to unduly limit this invention EXAMPLES Example 1. Potassium cobalt hexacyanoferrate (KCOHEX) was prepared by slowly adding an aqueous solution of 1 part 0.3 M potassium ferrocyanide in an acetic acid buffer (approximately 1.8 x 10 "3 M in acetic acid) cooled to between 0°C and 4°C at pH of between 5 and 6 to an aqueous solution of 2.4 parts 0.5 M cobalt nitrate (present in excess) cooled to between 0°C and 4°C with constant stirring. Precipitate was separated from the reaction mixture using a centrifuge (Bird Centrifuge Model IIP200, Bird Machine Co., South Walpole, MA) by separating the initial precipitate, then repeatedly slurrying the precipitate in water and re- centrifuging, for a total of four washings Excess cobalt nitrate is pink in color, so the desired solid material was centrifuged until the supernatant liquid was no longer pink The clean precipitate was again slurried in water at a concentration of 7.5 percent by weight, then spray-dried using a Bowen Model BE- 1 174 spray dryer (Niro Atomizer, Inc., Columbia, MD), as follows Inlet air temperature: 210°C Atomizing pressure 40 psig (276 KPa) Slurry feed rate 1 .25 gal/hr (4 73 L/hr) Outlet temperature 95°C Cyclone differential pressure 4 5 in H 2 O ( 1 1 43 x 1 O ' kg/cm 2 ) Recovered dried potassium cobalt hexacyanoferrate represented 92 percent yield, and was observed under an Olympus BH2 microscope (Olympus America, Inc , Melville, NY) to be spherical in shape Measurement of the particles using a Horiba Model LA-900 Particle Size Analyzer (Horiba Instruments, Inc , Irvine, CA), showed an average particle size of approximately 1 1 micrometers and a particle size distribution of from about 7 micrometers to about 60 micrometers. The spray-dried material was dark green in color The spherical particles were heated in an air-vented oven at approximately 100°C until they changed to a purplish-black color. Recovery from heating was essentially quantitative, and no loss of size or shape was noted as a result of the heating procedure Examtile 2. (Comparative) Potassium cobalt hexacyanoferrate was prepared as described in Example 1, except that the solid precipitate obtained from the final centrifuge wash was spread out in a thin layer about 2.5 cm thick on a drying tray and heated in air at 1 10°C- 1 15°C until the solid had dried and its color had changed from green to purplish- black The dried solid was subjected to cryogenic hammer-milling by means of a Model D Comminutor (Fitzpatrick Co , Elmhurst, IL) using a 325-mesh screen (0 044 mm sieve opening) and the resulting powder was sized in a hydrocyclone (Richard Mozley Ltd , Cornwall, UK). Particles in the range of from about 1 to about 50 micrometers in their largest dimension were retained, with an average particle size of approximately 10- 15 micrometers Yield of sized particles was approximately 60 percent As expected from a milling process, particles were typically irregular in shape (significant deviation from spherical) and a broad particle size distribution was obtained Example 3. A particle-filled porous web was prepared from the spherical potassium cobalt hexacyanoferrate particles of Example 1 An agitated slurry of 20 g Kevlar™ 1F306 dry aramid fiber pulp (DuPont, Wilmington, DE) in 2000 g water was blended in a 4 L Waring' M blender at a low speed for 30 seconds, then mixed with 0.25 g Tamol 850™ dispersant (Rohm & Haas Co , Philadelphia, PA), followed by 8.75 g (3.5 g dry weight) Goodrite l M 1800X73 styrene-butadiene latex binder aqueous slurry (B F. Goodrich Co , Cleveland, OH) Blending was continued for 30 seconds at a low speed To this mixture was added 53 6 g potassium cobalt hexacyanoferrate, followed by 20 g powdered alum (aluminum sulfate), and stirring was continued for an additional minute The mixture was poured into a Williams sheet mold (Williams Apparatus Co , Watertown, NY) equipped with a 930 3 cm 2 porous screen having pores of approximately 0 14 mm ( 100 mesh) at the bottom to allow water to drain The resulting wet sheet was pressed in a pneumatic press (Mead Fluid Dynamics, Chicago, IL) at approximately 620 KPa for approximately five minutes to remove additional water Drain time was 25 seconds, and no loss of KCOHEX could be observed in the drain water Finally, the porous web was dried in an oven at 250°F (121°C) for 120 minutes Example 4. (Comparative) Example 3 was repeated using ground and sized particulate as obtained in Example 2 in place of spray-dried particles Drain time was 60 seconds Example 5. A 90 mm diameter disk having a thickness of 3 2 mm was die cut from the particle-filled porous web of Example 3 The disk was placed in a stainless steel disk holder (Cole Parmer Instrument Co., Niles, IL) fitted with inlet and outlet pipes, so that the effective disk diameter was 80 mm The disk was washed with water, then an aqueous solution containing 12 mg/L cesium ion was pumped first through two canister-style prefilters in series (Filtrete™ Cartridges, Memtec America Corp., Timonium, MD) then through the disk at a flow rate of 105 mL/min , which corresponds to 6 49 Bed Volumes/min , wherein Bed Volume means the volume of the disk Cesium removal, reported as C/C 0 , where C represents the cesium concentration in the effluent and C„ represents initial cesium concentration, as a function of Bed Volumes is shown in Table I The pressure drop across the membrane was found to be constant at 55 KPa throughout the evaluation Table 1 Bed Volumes C/Co 0 0 389 0 778 0 1 167 0.019 1557 0 167 1946 0 358 2335 0 60 2724 0.717 3 1 13 0 792 3506 0.833 4186 0 91 7 The data of Table 1 show that spherical KCOHEX particles in a porous web are very effective in removing cesium ions from aqueous solution, and that a typical 90 mm SPE disk has a capacity of approximately 389 mg cesium ion (2000 Bed Volumes x 16.2 mL/Bed Volume x 1 L/ 1000 mL x 12 mg/L Cs 1 ) at approximately 50 percent breakthrough (i.e., 2000 Bed Volumes is taken to be the midpoint on a curve representing the adsorptive capacity of the disk for Cs ions) Various modifications and alterations that do not depart from the scope and spirit of this invention will become apparent to those skilled in the art. This invention is not to be unduly limited to the illustrative embodiments set forth herein.

Claims: I claim: 1 A method comprising the step of spray-drying a slurry of potassium cobalt hexacyanoferrate (KCOHEX) particles to provide monodisperse, substantially spherical KCOHEX particles, and optionally further comprising the step of heating said spherical KCOHEX particles until their color changes from green to purplish black 2 The method according to claim 1 wherein said spherical particles have a size in the range of about 1 to 500 micrometers 3 The method according to claims 1 or 2 wherein said spherical KCOHEX particles have an average size in the range of 9 to 12 micrometers 4 Substantially spherical cobalt hexacyanoferrate (KCOHEX) particles prepared according to the method of any of claims I to 3 5 The KCOHEX particles according to claim 4 which are enmeshed in a porous nonwoven fibrous web or pulp matrix or are packed in a column 6 The KCOHEX particles according to claims 4 or 5 which are enmeshed in a web of fibrillated polytetrafluoroethylene (PTFE) 7 The KCOHEX particles according to claims 4 or 5 which are enmeshed, optionally in the presence of a hydrocarbon binder, in a web or matrix which is a macroporous fibrous web, a microporous fibrous web, or a porous fibrous pulp matrix 8 The KCOHEX particles according to claims 5 or 7 wherein said particles are enmeshed in a fibrous web selected from the group consisting of polyamide, polyolefin, polyester, polyurethane, glass, polyvinylhalide, and combinations thereof. 9. The KCOHEX particles according to claims 5 or 7 which are enmeshed in a porous fibrous pulp matrix selected from classes of pulps consisting of aramid, aromatic polyamide, polyacrylic nitrile, cellulose, glass, and combinations thereof. 10. A method of selectively separating Cs ions from an aqueous solution comprising the step of passing an aqueous solution comprising Cs ions through the packed column or fibrous web or pulp matrix according to any of claims 5 to 9.

Inventors: WHITE LLOYD R, WHITE, LLOYD, R.
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1996
Main classification: C01C3
IPC codes: B01D1, B01J20, C01B17, C01C3, C01D17, C22B26, G21F9