METHOD FOR PRODUCING A HARD WOOD ELEMENT

Abstract: This invention relates to a method for producing hard elements (13) from wood. At least one wood piece (13) is inserted into a press (10) together with a liquid absorbing material (14) after which an isostatic pressure higher than 800 bar is applied on the pieces and the material. The pressure is released and the element (13) and the liquid absorbing material (14), which during the press operation has taken up liquid pressed out from the pieces, are picked out from the press (10).

Description: Method for producing a hard wood element This invention relates to a method for producing hard wood elements. It is previously known to produce hard wood elements by pressing wood material isostaticly at high pressure, see WO 9513908. It has however proved that it is sometimes difficult to achieve a high degree of compaction of the material depending on that the moisture content of the material is so large that the liquid, because of its non compression properties, prevent compressing. The purpose of this invention is to rectify this shortcoming and to make it possible to achieve a high degree of compaction also when the moisture content is large. This is achieved by means of a method having the characteristics mentioned in the claims. An embodiment of the invention will now be described with reference to the accompanying drawing which schematically and in section shows a device for carrying out the method. The Figure shows a so called Quintus-press 10 which is a press having an upper and a lower part 11 and 12 resp. which in a manner not shown in detail are so connected to each other that the press can take up very large press forces. The term "large press forces" in this connection means press forces larger than 10.000 tons. On the lower press part 11 one or several wood pieces 13 are closely packed together with a liquid absorbing, porous material 14 for instance a textile material or a foamed plastic material which has the ability to absorb the liquid leaving the material during the pressing operation. The liquid absorbing material is placed close to the pieces and is preferably so placed that it at least partly surrounds the pieces. Around the pieces an elastic or plastic material 15 is placed ant this material fills out the recesses in the press and transmits the pressure isostaticly to the sides of the pieces. The upper press part comprises a rubber membrane 16 which is the lower border surface for a chamber 17 and which during the initial phase of the press operation together with the press part 11 is moved downwards towards the lower press part. The membrane 16 is thereby streched over the material 14, 15 and will with its outer parts abut the lower press part 12. Then a liquid enters into the chamber 17 and the liquid is exposed to a high pressure, which in this connection means more than 800 bar. Consequently the pieces are exposed to a corresponding isostatic pressure since the membrane and the material 14,15 between the membrane and the pieces transmit the pressure equally to the pieces. During the press operation the liquid in the pieces will be pressed out from the pieces and be absorbed by the liquid absorbing material which means that the pieces will get a higher degree of volume reduction than if the liquid stays in the pieces. When the pressure has been released and the press parts been separated the compressed pieces, which now are hard wood elements, are picked out from the press together with the liquid absorbing material which at a later stage can be squeezed to press out the collected liquid an be reused.

Claims: Claims 1. Method for producing hard wood elements characterized in that at least one wood piece is inserted into a press together with a liquid absorbing material after which an isostatic pressure higher than 800 bar is applied on the pieces and the material, that the pressure is released and that the elements and the liquid absorbing material, which during the press operation has taken up liquid pressed out from the pieces, are picked out from the press. 2. Method according to claim 1 caracterized in that the liquid absorbing material before starting the press operation is placed close to the piece or pieces. 3. Method according to claim 2 characterized in that the liquid absorbing material is placed so that it at least partly surrounds the piece or pieces. 4. Method according to any of the preceding claims characterized in that the liquid absorbing material is a porous material for instance a textile- or a foamed plastic material.

Inventors: CASTWALL LENNART, LINDHE CURT, CASTWALL, LENNART, LINDHE, CURT
Applicants: CASTWALL LENNART, LINDHE CURT, CASTWALL, LENNART, LINDHE, CURT
Application year: 1996
Main classification: B27M1
IPC codes: B27K5, B27M1, B30B5