COMPOSITIONS AND METHODS FOR STABILIZING POLYMERS

Abstract: Compositions and methods for reducing the decomposition rate of polymeric bioadhesives and viscosity enhancers, such as poly(acrylic acids). The compositions include at least one strong, stable chelating agent, preferably an organophosphorous compound such as diethylene triamine penta(methylene phosphonic acid). These biocompatible compositions are especially useful in the ophthalmic field.

Description: COMPOSITIONS AND METHODS FOR STABILIZING POLYMERS FIELD OF THE INVENTION This invention relates broadly to compositions and method for stabilizing polymers. In a preferred embodiment, the invention relates to stabilization of bioadhesives and viscosity enhancers in ophthalmic compositions. DESCRIPTION OF THE RELATED ART Water soluble and water swellable (i.e., hydrophilic but water insoluble) polymeric materials are known to be useful as bioadhesives and viscosity enhancers. For example, poly(acrylic acids) are used in ophthalmic solutions or mixtures to increase viscosity, thereby increasing the retention time in the eye. An example of a commercially available viscosity enhancer is NOVEON™ AA-1 resins (polycarbophil) available from B.F. Goodrich. Typically, polymeric viscosity enhancers and bioadhesives decompose, or are otherwise altered, during extended storage periods. The decomposition of a viscosity enhancer reduces the viscosity of the composition, eventually to a point at which the composition is no longer deemed sufficiently effective. Thus, there exists shelf-life problems with compositions, most notably ophthalmic compositions, which include bioadhesives and viscosity enhancers. Accordingly, there is a need to reduce the rate of decomposition of bioadhesives and viscosity enhancers, and to increase the shelf life of compositions including these polymeric materials. SUMMARY OF THE INVENTION An object of the invention is to provide a means for stabilizing polymeric compositions. Another object of the invention is to provide a means for reducing the decomposition rate of polymeric bioadhesives and viscosity enhancers. A further object of the invention is to provide a means for increasing shelf life of ophthalmic compositions which include polymeric components. One embodiment of the invention is a stabilized composition, which includes at least one polymer selected from the group consisting of bioadhesives and viscosity enhancers, and at least one strong chelating agent (e.g., a phosphonic acid-containing chelating agent) capable of complexing with trace amounts of free catalytic metal ions. The chelating agent is believed to complex with trace amounts of metal ions, thereby reducing the free metal ion concentration. This reduction in free metal ion concentration reduces the decomposition rate of the polymer. The compositions, which are especially useful in the ophthalmic field, exhibit increased shelf life. Another embodiment of the invention is a method of stabilizing a polymeric composition. The method involves providing an ophthalmically compatible composition including a polymer selected from the group consisting of bioadhesives and viscosity enhancers, adding a strong (e.g., a phosphonic acid-containing) chelating agent to the composition, and allowing the chelating agent to complex with free catalytic metal ions in the composition. The composition exhibits a polymer decomposition rate which is less than the decomposition rate of a composition which does not include a strong chelating agent. Thus, the resultant polymeric composition has an improved shelf life. Still another embodiment of the present invention is the use of a phosphonic acid containing chelating agent for stabilizing a polymeric composition, wherein the polymer is selected from the group consisting of poly(acrylic acid), an acrylate copolymer, a crosslinked polyacrylic acid, a polysaccharide, and a mixture thereof. Yet a further embodiment of the present invention is a polymeric composition having a free metal ion concentration less than an amount which will cause substantial polymeric decomposition over a one year storage period at room temperature. DESCRIPTION OF THE PREFERRED EMBODIMENTS The compositions of the present invention include a polymeric material, which acts generally as a bioadhesive or a viscosity enhancer, and a stabilizer. The compositions may contain a wide variety of other components, including active agents, excipients, compatibilizers, aesthetic colorants, and the like. A preferred group of compositions are those which are ophthalmically acceptable, i.e., those which do not produce substantial irritation or damage when contacted with the eye, ocular tissue, or surrounding fluids. The preferred ophthalmic compositions are those which are aqueous. The innovative compositions and methods of the present invention offer improvements in product quality and stability over extended storage periods. Trace amounts of metal ions (e.g., Fe, Cu, Ca, Mg, transition metals), in solutions or slurries, are believed to catalytically increase the decomposition rate of bioadhesive and viscosity enhancing polymers. Metal ions which catalytically decompose bioadhesive and viscosity enhancing polymers are termed "catalytic metal ions" herein. The strong, stable chelating agents of the present invention are believed to complex with the surrounding metal ions, thereby reducing the free metal ions available to degrade the polymer. Thus, the strong, stable chelating agents reduce the rate of degradation, decomposition, or other inactivation of the polymer which results in the viscosity of the composition decreasing over time. As a result, the shelf life of the composition and the viscosity quality after any given extended storage period is improved by the present compositions and methods. Two theories are offered to explain the improved stability and shelf life of the present compositions to improve the reader's understanding of the invention. However, the invention is not limited by the theoretical explanation of the means by which the invention functions. First, it is believed that the use of chelating agents having an ability to complex with free ions better than EDTA offers improvements in composition stability and shelf life. Increases in strength of the attraction of the chelating agent to metal ions reduces the probability the complex will dissociate to give increased free metal ion concentrations. Second, it is believed that the use of chelating agents which are more chemically stable than EDTA offers improvements in composition stability and shelf life. If the complex degrades, e.g. by oxidation, the metal ion will be released from the complex and will return to solution, where it will increase the polymer degradation rate. Thus, the preferred chelating agents of the present invention have a metal ion complexing strength greater than EDTA and are more stable than EDTA. Preferred stabilizers of the present invention are a group of chelating agents having phosphonic acid or phosphonate groups. A preferred group of chelating agents are organophosphonates, particularly amino tri(lower alkylene phosphonic acids). A variety of such chelating agents are commercially available from Monsanto Company, St. Louis, Missouri, and are sold under the trademark DEQUEST ® . Examples of such compounds include, without limitation, diethylene triamine penta(methylene phosphonic acid); hexa- methylene-diaminetetra (methylenephosphonic acid); ethylenediaminetetra (methylene¬ phosphonic acid); and aminotrimethylene phosphonates. A particularly preferred chelating agent is diethylene triamine penta(methylene phosphonic acid), sold under the trademark DEQUEST ® 2060. A chelating agent is typically present in an amount of from about 0.00001 to 0.5 weight percent, more preferably in an amount of from about 0.0001 to 0.1 weight percent based on the total weight of a composition.. The bioadhesive or viscosity enhancing polymers of the present invention may be chosen from a wide range of polymers which are susceptible to viscosity reduction (i.e., by degradation or decomposition catalyzed by free metal ions) over time periods of about 30 days to about a year. A preferred group of polymers are those which are cross-linked and have carboxy- and/or hydroxy-functional groups. These bioadhesives or viscosity enhancers include, without limitation thereto, poly(acrylic acids), acrylate copolymers, crosslinked polyacrylic acids, and the like and mixtures thereof. Examples of such a polymeric materials which are commercially available are NOVEON (polycarbophil) resins, e.g. Noveon AA1 (B.F. Goodrich, Cleveland, Ohio), which are water insoluble poly(acrylic acids). Other examples are CARBOPOL ® resins, e.g. Carbopol ® 940 (B.F. Goodrich) which are water soluble poly(acrylic acids). Other bioadhesive or viscosity enhancing polymers of the present invention may be chosen from polysaccharides such as e.g. cellulose or a derivative thereof such as hydroxyethyl¬ cellulose, hydroxyethylcellulose or hydroxypropylcellulose; other polysaccharides such as dextran, hyaluronic acid or chitosan and mixtures thereof. The amount of a bioadhesive or viscosity enhancing polymer which is present in a composition of the present invention typically depends on its purpose. A composition of the present invention is in particular aqueous and may exhibit a viscosity in the range of from low to high. Accordingly the amount of a bioadhesive or viscosity enhancing polymer present is preferably in the range of from about 0.01 to 20.0 weight %, more preferably in the range of from about 0.05 to 10 weight % and in particular in the range of from about 0.1 to 2.0 weight % based on the total weight of the composition. In one embodiment, the present compositions are ophthalmic compositions which include a tonicity agent. The tonicity agent is preferably an alkali metal salts, especially sodium chloride. The tonicity agent is present in an amount which is sufficient to achieve an ophthalmically compatible composition. The tonicity agent may be present in an amount from about 0 to 1.2 weight percent, more preferably about 0.6 to 1.2 weight percent, and most preferably about 0.9 weight percent. The ophthalmic composition may include an ophthalmic delivery agent. The ophthalmic delivery agents useful in accordance with the present invention may be selected from a wide variety of ophthalmically acceptable agents, including beneficial pharmaceutical agents, diagnostic agents, vitamins, nutrients, lubricants, and the like. The ophthalmic delivery agent may include, without limitation thereto, 3H-thymidine, acetylcholine chloride, acyclovir, adrenaline, amethocaine, aminocaproic acid, antazoline phosphate, arachidonic acid, atropine, benoxinate hydrochloride, betaxolol hydrochloride, bupivacaine, carbachol, carteolol, chloramphenicol, chlortetracycline hydrochloride, chymatrypsin, clonidine, cocaine, corynanthine, cromolyn sodium, cyclopentolate, demecarium bromide, dexamethasone, dibutoline, dichlorphenamide, diclofenac, dipivefrin hydrochloride, echodtiophate iodide, ephedrine, epinephrine bitartrate, erythromycin, ethambutol, etidocaine, eucatropine, fluoromethalone, fluorometholone, gentamicin sulfate, gramicidine, H-thymidine, homatropine hydrobromide, hyaluronic acid, hydrocortisone, idoxuridine, indomethacin, inositol triphosphate, inositol phosphates, isoflurophate, isosorbide, lachesine, levobunolol, levocabastine, lidocaine, lignocaine, medrysone, mepivacaine, methacholine, methazolamide, naphazoline hydrochloride, natamycin, neomycin sulfate, neostigmine, noradrenaline, ofloxacin, oxybuprocaine, oxymetazolin, oxyphenonium, pheniramine maleate, phenylephrine hydrochloride, phosphatidylinositol phosphates, physostigmine, pilocarpine hydrochloride, polyhexamethylene biguanides, polymyxin B sulfates, prednisolone sodium phosphate, proparacaine hydrochloride, proxymethacaine, pyrilamine maleate, scopolamine hydrobromide, sorbinil, sulfacetamide, sulfisoxazole disolamine, tamoxifen, tetracaine hydrochloride, tetracycline, tetrahydrozoline hydrochloride, timolol maleate and hemihydrate, trifluridine, tropicamide, vidarabine, and salts, and other ophthalmically acceptable salts and mixtures thereof. While the ideal concentration of the ophthalmic delivery agent will depend on a number of factors, the concentration will generally fall within 0.001 and 10 weight percent. Preferably, the ophthalmic delivery agent is present in an amount from about 0.01 to 2.0 weight percent. More preferably, the concentration of ophthalmic delivery agent is about 0.1 to 1.5 weight percent. The ophthalmic composition may include a demulcent, such as, for example, a glucose biopolymer such as dextran, cellulose or derivatives thereof such as e.g. hydroxyethyl- cellulose or hydroxypropylcellulose. A preferred glucose biopolymer is dextran. Preferably, the glucose biopolymer is present in an amount from about 0.05 to 5.0 weight percent. The ophthalmic composition may include other demulcents, such as, for example, a polyalkylene glycol. The polyalkylene glycol is preferably a polyethylene glycol, a polypropylene glycol, or a mixture thereof. Preferably, the polyalkylene glycol is present in an amount from about 0.1 to 2.0 weight percent. Thus, in a particularly preferred embodiment, the ophthalmic composition includes: (a) about 0.01 to 2.0 weight percent of a bioadhesive or viscosity enhancing polymer; (b) about 0.0001 to 0.1 weight percent of a chelating agent having at least one phosphonic acid group; (c) about 0.1 to 2.0 weight percent poly(alkylene glycol); (d) about 0 to 0.9 weight percent of a tonicity enhancer; (e) about 0.01 to 5.0 weight percent of a glucose biopolymer; (f) about 0.001 to 10 weight percent of a delivery agent; and (g) water. The present method of stabilizing a polymeric compositions, generally includes providing an ophthalmically compatible composition including a bioadhesive or viscosity enhancing polymer; adding at least one strong, stable chelating agent, preferably including at least one phosphonic acid group, to the composition; and allowing the chelating agent to complex with the free metal ions present in the composition, which free metal ions may degrade the polymer, i.e., "catalytic metal ions". This method is believed to allow for the formation of a metal ion complex and polymer formulation which has a decomposition rate which is less than the decomposition rate of the polymer containing trace amounts of free catalytic metal ions. The order of mixing the components is not believed to be critical. Thus, each of the components of the ophthalmic composition may be, separately and serially, added to a vessel containing water, or all the components may be added simultaneously. Preferably, the components are added separately, with dispersion or dissolution of each separate component being achieved prior to addition of the next component. However, the present stabilization method is not limited by the order of addition or contact of the components. Accordingly another embodiment of the present invention relates to a process for the manufacture of a stabilized and in particular ophthalmic composition, characterized in that the components of a composition according to the main claim may be, separately and serially, added to a vessel containing water, or all the components may be added simultaneously. In a preferred process the components are added separately, with dispersion or dissolution of each separate component being achieved prior to addition of the next component. Alkylene means linear or branched alkylene with up to and including 18 C-atoms. Examples are decylene, undecylene and dodecylene. Preferred alkylenes are lower alkylenes. The term "lower" denotes that the radicals so defined contain up to 8 carbon atoms, preferably up to 6 carbon atoms and more preferably up to 4 carbon atoms. Accordingly in the present invention lower alkylene means linear or branched alkylene with up to and including 8 C-atoms, more preferably linear or branched alkylene with up to and including 6 C-atoms, and in particular linear or branched alkylene with up to and including 4 C-atoms. Examples are methylene, ethylene, 1 ,3-propylene, 1 ,2-propylene, 1 ,5-pentylene, 1 ,6-hexylene, 2,5-hexylene, 1 ,7-heptylene or 1 ,8-octylene. The previous disclosure will enable one having ordinary skill in the art to practice the invention. In order to better enable the reader to understand specific embodiments and the advantages thereof, reference to the following examples is suggested. EXAMPLE I A composition is prepared by mixing NOVEON AA1 (BFGoodrich), sodium chloride, PEG 400 (a 400 molecular weight polyethylene glycol, available from Fisher Scientific), and Dextran 70 (Spectrum Chem. Mfg. Corp., New Brunswick, NJ) in water in amounts sufficient to produce the following weight percentages: 0.625% NOVEON AA1 0.6% NaCl 0.2% PEG 400 0.1 % dextran Q.S. with water The pH is adjusted to 6.8 by adding diluted sodium hydroxide solution. The viscosity of the composition is measured initially and after exposure to a temperature of about 45 °C for about 13 months. An elevated temperature is used in order to accelerate the stability testing. The results are presented in Table 1. COMPARATIVE EXAMPLE II A second mixture is prepared by mixing components and adjusting pH as in Example I, with the addition of disodium EDTA (ethylene diamine tetraacetate). The second mixture has the following composition: 0.625% NOVEON AA1 0.6% NaCl 0.2% PEG 400 0.1 % Dextran 70 0.025% disodium EDTA Q.S. with water The composition is adjusted to a pH of about 6.8. The viscosity of the composition is measured initially and after exposure to a temperature of about 45 °C for about 13 months. The results are presented in Table 1. COMPARATIVE EXAMPLE III A third mixture is prepared by mixing components and adjusting pH as in Example I, with the addition of DEQUEST ® 2060 (solids content 50%, Monsanto Company, St. Louis, MO). The third mixture has the following composition: 0.625% NOVEON AA1 0.6% NaCl 0.2% PEG 400 0.006% DEQUEST ® 2060 0.1% Dextran 70 Q.S. with water The composition is adjusted to a pH of about 6.8. The viscosity of the composition is measured initially and after exposure to a temperature of about 45 °C for about 13 months. The results are presented in Table 1. TABLE 1 Example Stabilizer Initial Viscosity (cps) Viscosity (cps) after 13 mos. at 45 °C I none 932.5 250.4 II 0.025% disodium EDTA 924.8 235.0 III 0.006% DEQUEST ® 2060 853.3 955.5 EXAMPLE IV A fourth mixture is prepared by mixing components and adjusting pH as in Example I. The fourth mixture has the following aqueous composition, which is substantially the same as the composition of Example I, except that the amount of NOVEON differs slightly: 0.570% NOVEON AA1 0.6% NaCl 0.2% PEG 400 0.1% Dextran 70 Q.S. with water The composition is adjusted to a pH of about 7. The viscosity of the composition is measured initially and after exposure to a temperature of about 100 °C for about 7 days. The results are presented in Table 2. COMPARATIVE EXAMPLE V A fifth mixture is prepared by mixing components and adjusting pH as in Example I, with the addition of DEQUEST ® 2060. The fifth mixture has the following aqueous composition: 0.570% NOVEON AA1 0.6% NaCl 0.2% PEG 400 0.1% Dextran 70 0.006% DEQUEST ® 2060 Q.S. with water The composition is adjusted to a pH of about 7. The viscosity of the composition is measured initially and after exposure to a temperature of about 100 °C for about 7 days. The results are presented in Table 2. DISCUSSION OF RESULTS Examples I and IV show that the viscosity of poly(acrylic acid) mixtures decreases substantially over time. Example II shows that disodium EDTA does not have a significant impact on the polymer stability. However, surprisingly, Examples III and V show that poly(acrylic acid) mixtures stabilized with a stabilizer containing phosphonic acid groups does not exhibit significantly reduced viscosity during accelerated test procedures. Further, the DEQUEST ® 2060 stabilizer concentration was less than about 12% of the disodium EDTA stabilizer concentration. The invention has been described in detail, with reference to certain preferred embodiments, in order to enable the reader to practice the invention without undue experimentation. However, a person having ordinary skill in the art will readily recognize that many of the components and parameters may be varied or modified to a certain extent without departing from the scope and spirit of the invention. Furthermore, titles, headings, or the like are provided to enhance the reader's comprehension of this document, and should not be read as limiting the scope of the present invention. Accordingly, the intellectual property rights to this invention are defined only by the following claims and reasonable extensions thereof.

Claims: CLAIMS 1. A stabilized composition, comprising: (a) at least one polymer selected from the group consisting of bioadhesives and viscosity enhancers; and (b) at least one strong and stable chelating agent, wherein said chelating agent is capable of complexing with free catalytic metal ions, and wherein said chelating agent has a metal ion complexing strength greater than EDTA and said chelating agent is more stable than EDTA. 2. A composition of claim 1 , wherein said chelating agent includes at least one phosphonic acid group. 3. A composition of claim 1 , wherein said composition is ophthalmically compatible. 4. A composition of claim 3, further including an ophthalmic delivery agent. 5. A composition of claim 4, wherein said ophthalmic delivery agent is selected from the group consisting of ophthalmically beneficial pharmaceutical agents, diagnostic agents, vitamins, nutrients, lubricants, and mixtures thereof. 6. A composition of claim 5, wherein said ophthalmic delivery agent is selected from the group consisting of 3H-thymidine, acetylcholine chloride, acyclovir, adrenaline, amethocaine, aminocaproic acid, antazoline phosphate, arachidonic acid, atropine, benoxinate hydrochloride, betaxolol hydrochloride, bupivacaine, carbachol, carteolol, chloramphenicol, chlortetracycline hydrochloride, chymatrypsin, clonidine, cocaine, corynanthine, cromolyn sodium, cyclopentolate, demecarium bromide, dexamethasone, dibutoline, dichlorphenamide, diclofenac, dipivefrin hydrochloride, echodtiophate iodide, ephedrine, epinephrine bitartrate, erythromycin, ethambutol, etidocaine, eucatropine, fluoromethalone, fluorometholone, gentamicin sulfate, gramicidine, H-thymidine, homatropine hydrobromide, hyaluronic acid, hydrocortisone, idoxuridine, indomethacin, inositol triphosphate, inositol phosphates, isoflurophate, isosorbide, lachesine, levobunolol, levocabastine, lidocaine, lignocaine, medrysone, mepivacaine, methacholine, methazolamide, naphazoline hydrochloride, natamycin, neomycin sulfate, neostigmine, noradrenaline, ofloxacin, oxybuprocaine, oxymetazolin, oxyphenonium, pheniramine maleate, phenylephrine hydrochloride, phosphatidylinositol phosphates, physostigmine, pilocarpine hydrochloride, polyhexamethylene biguanides, polymyxin B sulfates, prednisolone sodium phosphate, proparacaine hydrochloride, proxymethacaine, pyrilamine maleate, scopolamine hydrobromide, sorbinil, sulfacetamide, sulfisoxazole disolamine, tamoxifen, tetracaine hydrochloride, tetracycline, tetrahydrozoline hydrochloride, timolol maleate and hemihydrate, trifluridine, tropicamide, vidarabine, other ophthalmically acceptable salts thereof and mixtures thereof. 7. A composition of claim 1 , wherein said polymer is selected from the group consisting of poly(acrylic acids), acrylate copolymers, crosslinked polyacrylic acids, and mixtures thereof. 8. A composition of claim 7, wherein said polymer is a poly(acrylic acid). 9. A composition of claim 2, wherein said chelating agent is an amino tri(lower alkylene phosphonic acid). 10. A composition of claim 9, wherein said chelating agent is selected from the group consisting of diethylene triamine penta(methylene phosphonic acid); hexamethylene- diaminetetra (methylenephosphonic acid); ethylenediaminetetra (methylenephosphonic acid); aminotrimethylene phosphonates; and mixtures thereof. 11. A composition of claim 10, wherein said chelating agent is diethylene triamine penta(methylene phosphonic acid). 12. A composition of claim 1 , comprising: (a) about 0.1 to 2.0 weight percent of said polymer; (b) about 0.0001 to 0.1 weight percent of said chelating agent; and (c) water. 13. A composition of claim 1 , further comprising about 0.1 to 2.0 weight percent poly(alkylene glycol). 14. A composition of claim 1 , further comprising about 0.6 to 1.2 weight percent of a tonicity enhancer. 15. A composition of ciaim 14, wherein said tonicity enhancer is sodium chloride. 16. A composition of claim 1 , further comprising about 0.05 to 5.0 weight percent of a glucose biopolymer. 17. A composition of claim 16, wherein said glucose biopolymer is dextran. 18. A composition of claim 1 , comprising: (a) about 0.01 to 2.0 weight percent of said polymer; (b) about 0.0001 to 0.1 weight percent of said chelating agent; (c) about 0.1 to 2.0 weight percent poly(alkylene glycol); (d) about 0 to 1.2 weight percent of a tonicity enhancer; (e) about 0.05 to 5.0 weight percent of a glucose biopolymer; (f) about 0.001 to 10 weight percent of a delivery agent; and (g) water. 19. A composition of claim 18, comprising: (a) about 0.01 to 2.0 weight percent of a polymer selected from the group consisting of poly(acrylic acids), acrylate copolymers, crosslinked polyacrylic acids, and mixtures thereof; (b) about 0.0001 to 0.1 weight percent of an organophosphorus chelating agent; (c) about 0.1 to 2.0 weight percent poly(alkylene glycol) selected from the group consisting of polyethylene glycol, polypropylene glycol, and mixtures thereof; (d) about 0 to 1.2 weight percent of an ophthalmically compatible alkali halide tonicity enhancer; (e) about 0.05 to 5.0 weight percent of a glucose biopolymer; (f) about 0.001 to 10.0 weight percent of a delivery agent; and (g) water. 20. A composition of claim 19, wherein said organophosphorus chelating agent is an amino tri(lower alkylene phosphonic acid). 21. A method of stabilizing a polymer composition, comprising the steps of: (a) providing an ophthalmically compatible composition including a polymer selected from the group consisting of bioadhesives and viscosity enhancers; (b) adding at least one strong and stable chelating agent, wherein said chelating agent is capable of complexing with free metal ions, and wherein said chelating agent has a metal ion complexing strength greater than EDTA and said chelating agent is more stable than EDTA.; and (c) allowing said chelating agent to complex with free catalytic metal ions, thereby producing a composition with metal ion complexes, whereby the polymer in said composition has a decomposition rate which is less than the decomposition rate of the uncomplexed composition. 22. A method of claim 21 , wherein said chelating agent includes at least one phosphonic acid group. 23. A method of claim 21 , further including an ophthalmic delivery agent selected from the group consisting of ophthalmic beneficial pharmaceutical agents, diagnostic agents, vitamins, nutrients, lubricants, and mixtures thereof. 24. A method of claim 21 , wherein said chelating agent is an amino tri(lower alkylene phosphonic acid). 25. A method of claim 24, wherein said chelating agent is selected from the group consisting of diethylene triamine penta(methylene phosphonic acid); hexamethylene- diaminetetra (methylenephosphonic acid); ethylenediaminetetra (methylenephosphonic acid); aminotrimethylene phosphonates; and mixtures thereof. 26. A method of claim 25, wherein said chelating agent is diethylene triamine penta(methylene phosphonic acid). 27. A method of claim 21 , wherein said polymer composition comprises: (a) about 0.1 to 2.0 weight percent of said polymer; (b) about 0.0001 to 0.1 weight percent of said chelating agent; and (c) water. 28. A method of claim 21 , wherein said polymer composition comprises: (a) about 0.01 to 2.0 weight percent of said polymer; (b) about 0.0001 to 0.1 weight percent of said chelating agent; (c) about 0.1 to 2.0 weight percent poly(alkylene gly ol); (d) about 0 to 1.2 weight percent of a tonicity enhancer; (e) about 0.05 to 5.0 weight percent of a glucose biopolymer; (f) about 0.001 to 10 weight percent of a delivery agent; and (g) water. 29. A method of claim 28, wherein said polymer composition comprises: (a) about 0.01 to 2.0 weight percent of a polymer selected from the group consisting of poly(acrylic acids), acrylate copolymers, crosslinked polyacrylic acids, and mixtures thereof; (b) about 0.0001 to 0.1 weight percent of an organophosphorus chelating agent; (c) about 0.1 to 2.0 weight percent poly(alkylene glycol) selected from the group consisting of polyethylene glycol, polypropylene glycol, and mixtures thereof; (d) about 0 to 1.2 weight percent of an ophthalmically compatible alkali halide tonicity enhancer; (e) about 0.05 to 5.0 weight percent of a glucose biopolymer; (f) about 0.001 to 10 weight percent of a delivery agent; and (g) water. 30. An ophthalmically acceptable polymeric composition having a free catalytic metal ion concentration less than an amount which will cause substantial polymeric decomposition over a one year storage period at room temperature. 31. A composition of claim 30, including a chelating agent. 32. A composition of claim 31, wherein said chelating agent is an organophosphorus compound. 33. A composition of claim 32, wherein said organophosphorus compound is diethylene triamine penta(methylene phosphonic acid). 34. A composition of claim 33, wherein said diethylene triamine penta(methylene phosphonic acid) is present in an amount of about 0.0001 to 0.1 weight percent.

Inventors: TSAO FU-PAO, TSAO, FU-PAO
Applicants: CIBA GEIGY AG, TSAO FU PAO, CIBA-GEIGY AG, TSAO, FU-PAO
Application year: 1996
Main classification: A61K9
IPC codes: A61K9, A61K47, C08K5