Anti-bleed coating for silicone automobile gaskets

Abstract: An oil resistant gasket and method for preparing said oil gasket which comprises applying an organic polymeric coating 15 selected from the group consisting of parylene N, parylene D, parylene C and mixtures thereof; to a porous, elastomeric gasket 14.

Description: The present invention relates to oil permeable internal combustion engine gaskets that are resistant to hydrocarbon oil and a method of rendering these oil permeable elastomeric gaskets resistant to hydrocarbon oil, particularly resistant to absorption and bleeding. A variety of more or less elastomeric materials are used to prepare gaskets used as seals between joined parts of an internal combustion engine to prevent leakage of-hydrocarbon oils at the point of joining. These permeable elastomeric materials include natural or organic and synthetic rubbers, such as EPDM, SBR, butyl nitrile and neoprene, chlorosulfonated polyethylene, fluorocarbon containing compounds, urethanes and the like. Preferably the elastomeric material is silicone rubbers which have excellent molding and extrusion properties and form gaskets with good physical properties such as enhanced high and low temperature stability, resistance to compression set at elevated temperatures, and good tear and tensile strength. Silicones can also be formulated to provide a gasket having a low durometer. Gaskets prepared from low durometer formulations provide excellent seals in applications where mated surfaces are uneven or irregular. In spite of the many advantages offered by elastomeric silicones as a gasket material, these gaskets when exposed to hot oil in an internal combustion engine tend to absorb some of the oil. As a gasket and mating metal surfaces of an engine cool after use, the oil absorbed by the gasket migrates from the gasket in both the inner and outer directions. The cycling which results from alternate heating and cooling causes the absorbed oil to permeate the cross-sectional thickness of the gasket until it reaches the outer surface of the gasket where it "bleeds" through and appears as small beads or drops on the outer surface of the gasket. Other attempts have been undertaken in the past to reduce the absorption characteristics of silicone gaskets to hydrocarbon oil. U.S. 5,380,770 discloses heat cured silicone rubber compositions to which are added a potassium aluminosilicate filler. According to the invention, the filler improves retention of physical properties and resistance to swelling in hot hydrocarbon oils. U.S. 4,580,794, discloses a method for manufacturing an engine gasket having reduced oil permeability where a silicone varnish is applied to at least the inner surface of the engine gasket. Neither of the above references discloses the use of organic coatings such as the parylene series as a means of improving the resistance of elastomeric silicone gaskets to absorption and "bleeding". U.S. 5,075,174, discloses an elastomeric silicone gasket having reduced surface energy and outgassing qualities for use in computers and electronic equipment. The thickness of the parylene coating is disclosed as from 0.1 to 3 microns in thickness. The present invention relates to the use of a gasket material comprising; a heat cured silicone rubber compound having a coating of a material selected from the group consisting of; parylene N, parylene C, parylene D and mixtures thereof as an engine gasket having reduced oil permeability and resistance to bleed. Fig. 1 is a top plan view of an engine gasket 16 of a generally rectangular configuration which is adapted to be received between two conforming surfaces of a vehicle engine. The gasket 16 is held in position by bolts which are received through bolt openings 17. The gasket inner surface 18 is exposed to hot oil. Fig. 2 is a cross sectional view of gasket 16 which consists of a porous, elastomeric layer 14. The porous, elastomeric has a thermoplastic polymer film layer 15 based on para-xylylene which renders the gasket 16 resistant to hydrocarbon oil absorption and bleed. The gasket material is used for internal combustion engine gaskets having improved resistance to hydrocarbon oils. The parylene is applied to the gasket as a coating preferably having a thickness of at least 2.5·10 -6 m, more preferably 5·10 -6 m or more. The present invention also relates to an engine gasket having reduced oil permeability and resistance to bleed, comprising; a heat cured silicone rubber compound having a coating of a material selected from the group consisting of; parylene N, parylene C, parylene D and mixtures thereof. The coated gaskets exhibit enhanced resistance to oil absorption and bleeding. When parylene is applied to the inner surface 18, it provides the engine gasket with increased resistance to engine oil absorption. When parylene is used to coat the surface of the gasket opposite the inner surface 18, the coating inhibits bleeding. The engine gasket according to the invention has at least the surface opposite the inner surface 18 (hereinafter the "outer surface") coated with at least one parylene. The unsubstituted homopolymer poly-p-xylylene has the structure (hereinafter referred to as parylene N) and substituted homopolymers may be illustrated by the following structures: (hereinafter referred to as parylene C) (hereinafter referred to as parylene D) The use of parylene C is most preferred. A description of parylene, processes for making it, and the apparatus in which parylene deposition can be effected may be found in US 3,246,627; 3,301,707 and 3,600,216. It will be observed, however, that the term "parylene" is not used in these patents. Instead, the term poly-p-xylylene is used generically and this term is considered to include both the unsubstituted and substituted varieties in the form of homopolymers or copolymers. Methods of making elastomeric engine gaskets are well known in the art. The parylene coated gaskets of the present invention are of heat curable silicone rubbers (HCR) The formulations of silicone rubbers include silicone polymers, crosslinking agents, crosslinking catalysts, fillers and various additives. In general the preferred silicone polymer is an organopolysiloxane having an average of at least two aliphatically unsaturated hydrocarbon radicals and have recurring units of the formula R x SiO 4-x 2 where R is selected from the group consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals in which an average of at least two of the monovalent hydrocarbon radicals contain aliphatically unsaturated groups per molecule and x is an integer of from 1 to 3, with an average value of from about 1.7 to about 2.1. It is preferred that the hydrocarbon radicals and substituted hydrocarbon radicals represented by R each contain from 1 to 18 carbon atoms. Examples of suitable hydrocarbon radicals are alkyl radicals, such as the methyl, ethyl, n-propyl and isopropyl radicals, as well as the octadecyl radicals; cycloalkyl radicals such as the cyclohexyl and the cycloheptyl radicals; aryl radicals such as the phenyl radical; alkaryl radicals such as the tolyl radicals and aralkyl radicals such as the benzyl and the beta-phenylethyl radicals. Examples of substituted hydrocarbon radicals represented by R are halogenated hydrocarbon radicals, such as the 3,3,3-trifluoropropyl radical and o-, m- and p-chlorophenyl radicals. Because of their availability, it is preferred that at least 80% of the R radicals be methyl radicals. Examples of hydrocarbon radicals having aliphatic unsaturation are vinyl, allyl, methallyl and butadienyl radicals, with vinyl being the preferred radical. These organopolysiloxanes preferably have a viscosity of from about 5 to 10,000,000 mPa.s at 25°C and more preferably from about 40 to about 500,000 mPa.s at 25°C. The organopolysiloxanes employed in the compositions of this invention are produced by the hydrolysis and condensation of the corresponding hydrolyzable silanes. These organopolysiloxanes are preferably linear polymers containing diorganosiloxane units of the formula R 2 SiO; however, these polymers may also contain minor amounts of other units, such as RSiO 3/2 units, R 3 SiO 0.5 and/or SiO 4/2 units, in which R is the same as above. The preferred organopolysiloxane is a diorganopolysiloxane having the general formula where n is a number such that the organopolysiloxane has a viscosity of from about 40 to 100,000 mPa.s at 25°C. Organohydrogenpolysiloxanes employed in the compositions of this invention generally consist of units of the formula R 1 m SiO 4-m 2 where R 1 represents hydrogen, a monovalene hydrocarbon radical or a halogenated monovalent hydrocarbon radical having from 1 to 18 carbon atoms, in which at least two and preferably three Si-bonded hydrogen atoms are present per molecule and m is 1, 2 or 3. Preferred compounds are those consisting of RSiO-units, R 2 SiO- and R 3 SiO 0.5 units, in which an Si-bonded hydrogen atom is present for each 3 to 100 silicon atoms and R is the same as above. It is preferred that the organohydrogenpolysiloxanes have a viscosity of from about 10 to 50,000 mPa.s and more preferably from 100 to 20,000 mPa.s at 25°C. The organohydrogenpolysiloxanes may also contain monovalent hydrocarbon radicals having aliphatic unsaturation as well as Si-bonded hydrogen atoms in the same molecule. Catalysts employed in this invention may consist of any catalysts previously used to promote the cure of HCR elastomers. These may include organic peroxides, platinum and platinum compounds. Preferred peroxide curing agents are the thermal decomposition organic peroxides and are described in Noll "Chemistry and Technology of Silicones", 1968, pages 392-395. Suitable peroxide catalysts include dialkyl peroxides such as di-tertiary-butyl peroxide, tertiary-butyl-triethyl-methyl peroxide, di-tertiary-butyl-tertiary-triphenyl peroxide, and butyl per benzoate and a di-teriary-alkyl peroxide such as dicumyl peroxide. A preferred peroxide catalyst is 2,5-dimethyl-2,5-di(t-butylperoxy)hexane. A platinum catalyst employed in this invention may consist of finely dispersed platinum as well as platinum compounds and/or platinum complexes which have been used heretofore to promote the addition of Si-bonded hydrogen atoms to compounds having aliphatically unsaturated groups. Examples of platinum catalysts which can be used in this invention are finely dispersed platinum on carriers, such as silicon dioxide, aluminum oxide or activated charcoal, platinum halides, such as PtCl 4 , chloroplatinic acid and Na 2 PtCl 4-n H 2 O, platinum-olefin complexes, for example, those with ethylene, propylene or butadiene, platinum-alcohol complexes, platinum-styrene complexes such as those described in U.S. 4,394,317 to McAfee et al., platinum-alcoholate complexes, platinum-acetylacetonate, reaction products comprising chloroplatinic acid and monoketones, for example, cyclo-hexanone, methyl ethyl ketone, acetone, methyl-n-propyl ketone, diisobutyl ketone, acetophenone and mesityl oxide, as well as platinum-vinylsiloxane complexes, such as platinum-divinyltetramethyldisiloxane complexes with or without a detectable amount of inorganic halogen. The platinum-divinylsiloxane complexes are described, for example, in US. 3,715,334, 3,775,452 and 3,814,730 to Karstedt. Mixtures of various platinum catalysts, for example, a mixture consisting of the reaction product of chloroplatinic acid and cyclohexanone and a platinum-divinyltetramethyldi-siloxane complex which is free of detectable inorganic halogen, may be used in the compositions of this invention. Fillers which may be incorporated in the compositions of this invention are reinforcing fillers, i.e., fillers having a surface area of at least 50 m 2 /gm. Examples of such fillers are precipitated silicon dioxide having a surface area of at least 50 m 2 /gm and/or pyrogenically produced silicon dioxide. Examples of other reinforcing fillers are the aerogels, alumina, carbon blacks and graphite. A portion of the fillers can be semi- or non-reinforcing fillers, i.e., fillers which have a surface area of less than 50 m 2 /gm. Examples of semi- or non-reinforcing fillers are metal oxides, metal nitrides, cork, organic resins, poly-tetrafluoroethylene polychlorotrifluoroethylene, polyvinyl chloride, carbon black, graphite, bentonite, diatomaceous earth, crushed quartz, mica, metal fibers, flass beads, bubbles or fibers and mixtures thereof. Preferred examples of metal oxides are zinc oxide, ferric oxide, alumina and titanium oxide. The fillers may also be treated with, for example, triorgano-alkoxy-silanes, such as trimethylethoxysilane to coat the surfaces with organosiloxy groups. Other additives which may be incorporated in the compositions of this invention include pigments, compression set additives, oxidation inhibitors, plasticizers, adhesion promoters, base stabilizers, processing aids and other materials. In general the gasket is formed by blending or milling together the various constituents to form an uncured rubber composition. In a preferred embodiment an uncured silicone rubber composition is injected into a mold cavity which can contain reinforcing rails. The silicone rubber composition is then heat cured in the mold to bond to any reinforcing rails to the silicone rubber composition and form an optionally reinforced gasket of the desired shape. The process for coating a substrate with parylene is conventional and well known in the art. Typical steps and conditions of such a process involve first vaporizing a cyclic dimer which contains the desired repeating unit, e.g., cyclic, di-p-xylylene, under a vacuum of about 10 to about 100 microns and at a temperature of about 150°C to about 200°C; then, pyrolyzing the vaporized cyclic dimer under the same or similar low pressure conditions at about 670°C to about 690°C. The pyrolysis step breaks the benzylic carbon to carbon bonds to provide the p-xylylene monomer referred to as the p-xylylene diradical or just as the diradical, the diradical remaining in the vapor state; and, finally, introducing the vaporous diradical into the deposition chamber containing the heretofore described substrate, again under the same or similar vacuum, but at ambient temperatures in the range of about 20°C to about 30°C., where the diradical condenses and polymerizes on all of the exposed surface of the substrate to provide a parylene film. The above described conventional process may be referred to hereinafter as "vacuum pyrolysis" or "vacuum deposition". A more detailed description of the above coating method is found in U.S. 3,246,627. Further descriptions of variations of the vacuum deposition process are also discussed in the NO-VATRAN Custom Coating Services document entitled "Parylene Conformal Coating System". Having described the invention, the following examples are set forth to further illustrate and should not be considered limiting in nature. In the examples all parts are by weight unless otherwise indicated. Examples 1 to 3 Three 152mm x 152mm x 2mm cured silicone rubber slabs were prepared. The silicone rubber consisted of 100 parts of a mixture of 90 parts vinyldimethyl endstopped polydimethylsiloxane having 4000 siloxane units 10 parts vinyldimethyl endstopped polydimethylsiloxane having 1000 siloxane units having a vinyl content of 3.5% by weight 8 parts hexamethyldisilazane 34 parts fumed silica having a surface area of 300 m 2 /g 0.5 parts divinyltetramethyldisilazane 4 parts magnesium oxide 10 parts Wollastonite 1 part cerric hydrate 0.02 parts SRF carbon black 0.20 parts titanium dioxide 0.80 parts of a 50:50 mixture of 2,5-dimethyl 2,5-di-(t-butyl peroxy) hexane and CaCO 3 . The above ingredients were mixed at room temperature and cold rolled to a predetermined thickness. The rolled silicone composition was then cut into three pieces and cured in a press fitted with a die having the desired dimensions, for 10 minutes at 171°C. Half of each cured slab was coated with parylene-C. Two of the slabs were coated to a coating thickness of 2.5·10 -6 m the remaining slab was coated to a coating thickness of 5·10 -6 m. All three cured slabs were then oil aged by immersion for 70 hours at 149°C in IRM-903 oil. After 70 hours the cured slabs were removed from the oil and blotted dry and observed over time. The results are noted in Table 1. 30 minutes 60 minutes 1440 minutes Slab coating Thickness Coated/uncoated Coated/uncoated Coated/uncoated 2.5·10 -6 m no bleeding slight film/some bleeding no bleeding slight film/bleeding heavy film no bleeding slight film/ bleeding heavy film 2.5·10 -6 m no bleeding slight film/some bleeding no bleeding slight film/bleeding heavy film no bleeding slight film/bleeding heavy film 5·10 -6 m no bleeding slight film/some bleeding no bleeding slight film/bleeding heavy film no bleeding slight film/bleeding heavy film

Claims: Use of a gasket material comprising; a heat cured silicone rubber compound having a coating of a material selected from the group consisting of; parylene N, parylene C, parylene D and mixtures thereof as an engine gasket having reduced oil permeability and resistance to bleed. Use as claimed in claim 1, wherein the coating material is parylene C. Use as claimed in claims 1 or 2, wherein the coating has a thickness of at least 2.5·10 -6 m. Use as claimed in claims 1 to 3, wherein the coating is present on the outer surface only. Use as claimed in claims 1 to 4, wherein the coating is present on the inner surface only.

Inventors: JOHNSON THEODORE D, WALKER FRANCIS J, JOHNSON, THEODORE D., WALKER, FRANCIS J.
Applicants: WACKER CHEMIE GMBH, WACKER-CHEMIE GMBH
Application year: 1996
Main classification: C08J7
IPC codes: F16J15, F02F11, B32B5, C08J7, B60J10, C09K3