Etching process of CoSi2 layers and process for the fabrication of Schottky-barrier detectors using the same

Abstract: Etching process of CoSi 2 layers in semiconductor processing by means of a HF-based solution, wherein the etching rate of CoSi 2 is controlled by regulating the pH value of the HF-based solution.

Description: Object of the invention The present invention is related to an etching process of CoSi 2 layers in semiconductor processing. The present invention is also related to the use of this etching process for the formation of Schottky barrier infrared detectors. State of the art The use of cobalt disilicide (CoSi 2 ) in microelectronics applications is becoming more and more important. In CMOS technology, with scaling down of dimensions, especially for CMOS technology manufacturing transistor with a gate length smaller than 0.35 µm, CoSi 2 has become an attractive material due to its better characteristics when compared to the more frequently used TiSi 2 . The interaction of a silicide film with chemicals and reactive gasses during further processing is an important issue to maintain the integrity of the film in the fully integrated structure. TiSi 2 is known to be very reactive with chemicals such as NH 4 OH- and HF-based solutions. CoSi 2 is much more robust in that respect. Wet etching of CoSi 2 has even been considered very difficult in general. The document Journal of Applied Physics, vol. 72, nos, pages 1864- 1873, published in September 1992 discloses that CoSi 2 is etched in suffered acide etch at a rate of about 5 nm/mn at room temperature. The document Journal of Crystal fourth, vol. 127, n° 1-4, pages 659-662, published in February 1993 discloses the manufacture of Schottky-barrier infrared detectors using CoSi 2 contacts. In this document, CoSi 2 is etched with suffered HF. Aims of the present invention The present invention aims to suggest as a first object an etching process of CoSi 2 layers in semiconductor processing which can be accurately controlled. Furthermore, the present invention aims to suggest the use of the etching process according to the present invention in order to obtain selective etching steps. A further object of the present invention is to manufacture Schottky barrier infrared detectors which will be improved compared to the ones suggested by the state of the art. Main characteristics of the present invention The present invention is related to an etching process of CoSi 2 layers in semiconductor processing by means of a HF-based solution wherein the etching rate of CoSi 2 is controlled by regulating the pH value of the HF-based solution. The pH of this solution is regulated by adding chemicals to said solution modifying the pH such as H 2 SO 4 or Hcl in order to reduce the pH or NH 4 OH in order to increase the pH of the HF-based solution. The HF-based solution can be a buffered solution or not. According to a first preferred embodiment, the pH of the HF-based solution is regulated at a pH comprised between 0 and 1.5 in order to have a rather fast etching rate of the CoSi 2 layer. This particular preferred embodiment will be used in order to have Schottky barrier infrared detectors with CoSi 2 /Si or CoSi 2 /Si 1-x Ge x interface. As a first object, the present invention is related to an etching process for CoSi 2 layers as defined in claim 1. As a second object, the present invention is related to process of manufacturing CoSi 2 /Si Schottky barrier infrared detectors, preferably CoSi 2 /Si 1-x Ge x Schottky barrier infrared detectors comprising the steps of: growing a Si 1-x Ge x layer on a silicon substrate; growing a Si sacrificial layer on the top of the Si 1-x Ge x layer; depositing a Co layer on said Si sacrificial layer; heating the Co layer in order to obtain a CoSi 2 layer; depositing a photoresist strip on said CoSi 2 layer; developing the photo-resist strip using a masking layer in order to create the required patterning of the CoSi 2 layer; etching the CoSi 2 layer with a HF-based solution having a pH value smaller than 1.5; removing the photoresist strip; Description of the figures Figure 1 shows the sheet conductance of CoSi 2 layers as a function of etching time in a HF 2wt.% solution. Figures 2 represent SEM pictures of CoSi 2 film (60 nm) surface : a) after 20 s etching; b) after 160 s etching in HF 2%. Figure 3 represents RBS spectra of CoSi 2 film (60 nm) etched for 40, 140 and 200 s in HF 2%. Figure 4 represents the CoSi 2 (60 nm) sheet conductance as a function of etching time for different HF solutions. a function of etching time in HF2%, for different pH values. Figure 6 represents the concentration of the different species present in a diluted HF solution as a function of its pH. Figure 7 represents the etch rate of CoSi 2 in HF 2% as a function of the pH of the mixture. Figures 8 are representing schematic views of the several steps of etching CoSi 2 layers in order to be used in fabrication of CoSi 2 /Si or CoSi 2 /Si 1-x Ge x Schottky barrier detectors. Detailed description of several embodiments of the present invention As an example, cobalt silicides are formed on n-type <100> oriented silicon, 125 mm wafers. A standard RCA cleaning followed by an HF dip for hydrogen passivation of the silicon surface were performed just before loading the wafers into the deposition system. Co layers with thickness of 8 nm, 16 nm and 40 nm were deposited using a BALZERS BAS450 DC magnetron sputtering system. The base pressure was always better than 3.0 x 10 -4 Pa (3.0 x 10 -6 mbar). A two-step silicidation process was carried out in an AST rapid thermal processor, in a nitrogen ambient. The temperatures of the first and second annealing steps were 550°C and 700°C, respectively. Between these two annealing steps, a selective etch in a H 2 SO 4 /H 2 O 2 solution was done to remove the unreacted metal on top of the silicide. To investigate the etching rate of CoSi 2 in hydrogen fluoride (HF) based solutions, concentrations of 0.5 and 2wt% of HF were used, as well as a buffered hydrogen fluoride (BHF) solution, which is formed from 1 part of HF 50% and 7 parts of NH 4 F 40%. Etching times from 10 seconds to 15 minutes were tested. H 2 SO 4 or HCl or NH 4 OH were added to the solutions to change their pH. The pH values of the solutions were measured with pH paper. The thinning of the CoSi 2 layers was monitored by four point probe sheet resistance measurements (before and after etching). The samples were also characterised by scanning electron microscopy (SEM) and Rutherford backscattering spectroscopy (RBS). Tables 1 & 2 are summarizing the experimental results obtained. Figure 1 shows the sheet conductance of three different CoSi 2 layers as a function of etching time in a HF 2wt.% solution. The thickness of the original CoSi 2 layers was 29, 60 and 150 nm resulting in a sheet resistance of 5.5, 2.6 and 1.1 ohm/sq., respectively. For a homogeneous layer the inverse of sheet resistance (sheet conductance) is directly proportional to its thickness. It is clear that the values of the sheet conductance decrease with increasing etch time. This indicates that the CoSi 2 film is being attacked by the HF solution. Moreover, the silicide etching rate (determined by the slope of the curve) is constant and independent of the layer thickness. The near-zero values of the sheet conductivity are related to the conductance of the silicon substrate, indicating that the silicide was removed. A sequence of SEM pictures taken after different etching times in figure 2 reveal surface morphology changes of the 60 nm CoSi 2 film. Figure 2a shows the CoSi 2 layer surface after etching for 20 seconds. In figure 2b the sample was etched for 160 seconds and it is possible to see a delineation of the grain boundaries of the silicide film. It seems that the film is etched a little faster at the grain boundaries. After 300 seconds etching (not shown) the silicide is completely removed and the patterns observed are foot prints of the silicide grains on the silicon substrate surface. RBS spectra of samples etched for 40, 140 and 200 seconds as represented in figure 3 confirm the thinning of the silicide layers with etch time. These results strongly suggest a layer-by-layer etching mechanism of the CoSi 2 film. Etching of CoSi 2 in HF 0.5wt.% and BHF solutions were then investigated. Sheet conductance as a function of etching time is plotted for different HF solutions in figure 4, starting from 60 nm CoSi 2 . The silicide etch rate is slightly lower for HF 0.5wt.% than for HF 2wt.% solutions. Furthermore, the etching of the silicide layer in HF 0.5% starts after approximately 120 seconds. It is not clear at the moment whether this delay can be attributed to the time necessary to remove the native oxide on the CoSi 2 . It has also to be considered the concentration of H + in this solution : initially it is insufficient to start the reaction, but due to an autocatalytic reaction the H + concentration increases and the silicide can be etched. When BHF is used the silicide layer is attacked at a significant lower rate than in the case of HF 2%. This is unexpected since from experience of SiO 2 etching, BHF is a much stronger etch solution with a significantly higher etch rate than HF 2%. In BHF the most abundant forms of the fluoride are F - and HF 2 - , whereas HF and H 2 F 2 are more important in HF 2%. This difference in composition yields a lower acid grade for BHF (pH = 4.5) than for a HF 2% solution (pH = 1.5). To check out a possible influence of the pH on the etching of CoSi 2 in HF solutions, either H 2 SO 4 or NH 4 OH were added to a HF 2% to change its pH from values of near zero to 8.5. Figure 5 represents the sheet conductance values as a function of etch time for 2% HF solutions with varying pH. By forming a more acid solution the etch rate is increased. A 60 nm CoSi 2 layer is removed in less than 30 seconds when the pH of the solution is almost zero. On the other hand, the silicide layer does not seem to be attacked for the solution with the highest pH tested (pH = 8.5). It is worth noticing that the sulphuric acid itself does not attack the silicide. In a solution with the same amount of H 2 SO 4 , but no HF, the silicide is not etched at all. The same experiment performed in diluted BHF showed the same trend : solutions with higher pH values etch cobalt silicide films at lower rates than solutions with lower pH values. These results confirm that the etching of CoSi 2 in HF based solutions is controlled predominantly by the H + concentration. In order to describe quantitatively the CoSi 2 etch rate in HF 2%, the concentrations of the different species present in diluted HF solutions were calculated. In these calculations the following equilibria were used: HF = H + + F - HF + F - = HF 2 - 2HF = H 2 F 2 The result is shown in figure 6, where the species concentration is plotted as a function of the pH of the mixture. As can be seen, for low pH values (pH < 1.5) HF and H 2 F 2 are dominant and their concentrations remain constant. For intermediate pH values the concentrations of F - and HF 2 - increase and for high pH values the solution is practically formed by F - . The etch rate (ER) of CoSi 2 in HF 2% as a function of the pH of the mixture is plotted in figure 7. In the region where pH < 1.5 the silicide is etched very fast. Since the concentration of all fluoride containing species is constant in this region, H + plays an important role, being the dominant etching species. Between pH values of 1.5 and 5.5 the etch rate is lower and basically constant, and for pH values higher than 5.5 the silicide seems not to be attacked. A second object of the present invention is to manufacture CoSi 2 /Silicon Schottky barrier detectors. Schottky barrier infrared detectors using silicide/silicon Schottky diodes are of a high interest for applications in the range of 1 -10 µm. Among these detectors PtSi/Si Schottky IR detectors are the most developed devices with a cut-off wavelength of approximately 5 -6 µm. In these past years, COSi 2 /Si Schottky detectors have been proposed as a promising candidate for IR applications in the range 1 -3 µm. Figs. 8 more precisely represent the several steps of the etching process of a CoSi 2 layer strained to a Si substrate using a HF-based solution having a pH less than 1.5. More particularly fig. 8a represents the Si substrate on which a CoSi 2 layer has been deposited. Fig. 8b represents the coating of a photo-resist strip and the lithographic step in order to have a required patterning of the CoSi 2 layer; Fig. 8c represents the result obtained after the wet etching in a HF-based solution of the CoSi 2 layer not covered by the photo-resist stip. Fig. 8d represents the removal of the photo-resist strip leaving the required CoSi 2 patterning on the Si substrate. In order to illustrate the method of etching of the CoSi 2 layer, the manufacture of CoSi 2 /Si 1-x Ge x infrared detector is described hereunder as a preferred embodiment of this process. This fabrication could also advantageously be integrated into CMOS processes. For silicidation studies, lightly doped (N A =5x10 16 cm- 3 ) p-type <100>Si wafers are used, whereas for detector experiments highly doped (N A =5x10 18 cm- 3 ) wafers with lightly doped (N A =5x10 16 cm- 3 ) epitaxial surface layers on top are used. Pseudomorphic Si 1-x Ge x layers and sacrificial Si surface layers are grown epitaxially on these samples. The deposition of the Si sacrificial layer on the SiGe layer is necessary in order to prevent any reaction of cobalt with the SiGe layer. For the silicidation study samples, the buffer layer, the graded layer, the strained layer and the Si sacrificial layer have a thickness of 5 nm, 50 nm, 100 nm and 30 nm, respectively. For the detector samples, the thickness of the buffer layer is 5 nm, the thickness of the graded layer was 50 nm, and the thickness of the strained layer was 30 nm. The doping of the layers is p-type 10 16 cm -3 . The Geconcentration x is x=0.2. The sacrificial Si-layer on top is 40 nm for the detector samples and 30 nm and 100 nm for the silicidation study samples. Before the metal deposition, the wafers are cleaned by an HF-dip d(2%). Co layers of 10 nm are deposited on the silicidation study samples and 7 nm on the detector samples. Since the silicidation conditions could not be controlled such that no reaction with strained Si 1-x Ge x layer could be guaranteed, the thicknesses of the sacrificial Si-layer for the detector samples are chosen to be slightly thicker than the thicknesses to be consumed by the sputtered Co thickness. Afterwards, the silicidation study samples were silicided in an AG Heatpulse rapid thermal processor system in nitrogen ambient at temperatures between 550°C and 700°C for 30 seconds. Detector samples are silicided at 600°C. After silicidation, a selective etch in H 2 SO 4 /H 2 O 2 was carried out to remove the possibly remaining unreacted metal. A CoSi 2 /strained Si 1-x Ge x detector offers the big advantage that no metal leading to states that effectively reduce the minority carrier lifetime, is involved. The Si wafer has the function of the substrate. Since there is an additional layer involved, contacting the silicide becomes more difficult. The contact to the thin CoSi 2 layer requires very critical etching steps and metallization steps after silicidation. Definition of the silicide areas is possible via a self-aligned silicide or also via silicide etching. Composition pH etch rate (nm/s) ml ml ml HF 49% H2O HF2% 1.5 0.22 20 470 HF 49% H2O H2SO4 HF2% 20 370 100 0 2.15 HF 49% H2O H2SO4 (no HF) 0 390 100 0 0 HF 49% H2O H2SO4 HF2% 20 460 10 0.5 0.38 HF 49% H2O NH4OH HF2% 8.5 0 20 430 40 HF 49% H2O NH4OH HF2% 3 0.15 20 450 20 HF 49% H2O NH4OH HF2% 4 0.13 20 440 30 HF 49% H2O NH4OH HF2% 5 0.1 20 435 35 HF 49% H2O NH4OH HF2% 2.5 0.13 20 455 15 HF49% H2O HCl HF2% 0.52 0.34 40 930 30 HF49% H2O HCI HF2% 0.22 0.38 40 900 60 HF49% H2O HCl HF2% 0.04 0.42 40 870 90 HF49% H2O HCl HF2% -0.08 0.47 40 840 120 HF49% H2O 5 485 HF0.5% 0.18 Composition pH etch rate (nm/s) ml ml ml B-HF (from the bottle) 4.5 0.045 500 B-HF H2O BHF 1/12.5 4 0.08 40 460 B-HF H2O NH4OH BHF 1/12.5 6 0.04 40 450 10 B-HF H2O H2SO4 BHF 1/12.5 1.5 0.14 40 450 10 B-HF H2O BHF 1/7.5 4 0.07 60 390 B-HF H2O NH4OH BHF 1/7.5 5.5 0.07 60 380 10 B-HF H2O H2SO4 BHF 1/7.5 2.5 0.09 60 380 10

Claims: Etching process of CoSi 2 layers in semiconductor processing by means of a HF-based solution, characterised in that the etching rate of CoSi 2 is controlled by regulating the pH value of the HF-based solution at a value smaller than or equal to 4.0 and that the pH of the HF-based solution is regulated by adding chemicals to said solution. Etching process of CoSi 2 layers according to claim 1, wherein the HF-based solution is a buffered solution or not. Etching process of CoSi 2 layers according to claim 1 or 2, wherein the chemicals added to the HF-based solution are H 2 SO 4 or HCl or NH 4 OH. Etching process of CoSi 2 layers according to claim 1, wherein the pH of the HF-based solution is regulated at a pH smaller than or equal to 1.5. Process of manufacturing CoSi 2 /Si Schottky barrier infrared detectors preferably CoSi 2 /Si 1-x Ge x Schottky barrier infrared detectors comprising the steps of: growing a Si 1-x Ge x layer on a silicon substrate; growing a Si sacrificial layer on the top of the Si 1-x Ge x layer; depositing a Co layer on said Si sacrificial layer; heating the Co layer in order to obtain a CoSi 2 layer; depositing a photoresist strip on said CoSi 2 layer; developing the photo-resist strip using a masking layer in order to create the required patterning of the CoSi 2 layer; etching the CoSi 2 layer with a HF-based solution having a pH value smaller than 1.5; removing the photoresist strip.

Inventors: BAKLANOV MIKHAIL RODIONOVICH, DEFERM LUDO, DONATON RICARDO ALVES, JANSEN PHILIPPE, MAEX KAREN IRMA JOSEF, ROOYACKERS RITA, VERBEECK RITA, BAKLANOV, MIKHAIL RODIONOVICH, DEFERM, LUDO, DONATON, RICARDO ALVES, JANSEN, PHILIPPE, MAEX, KAREN IRMA JOSEF, ROOYACKERS, RITA, VERBEECK, RITA
Applicants: IMEC INTER UNI MICRO ELECTR, INTERUNIVERSITAIR MICRO-ELEKTRONICA CENTRUM VZW
Application year: 1996
Main classification: H01L21
IPC codes: H01L21, H01L29, H01L31