Highly active double metal cyanide complex catalysts

Abstract: Improved double metal cyanide catalysts are disclosed. The substantially amorphous catalysts of the invention are more active for polymerizing epoxides than conventional DMC catalysts, which have a substantial crystalline component. Polyol products made with the catalysts are unusually clear, have exceptionally low unsaturations, and contain no detectable amount of low molecular weight polyol impurities. Methods of making the improved DMC catalysts are also disclosed. In one method, the reactants are intimately combined to produce a catalyst of the invention. In another method, an organic complexing agent is initially present in the reactant solutions.

Description: FIELD OF THE INVENTION The invention relates to double metal cyanide (DMC) complex catalyst compositions. The catalysts are highly active in epoxide polymerizations. The invention includes improved methods for preparing the compositions. Polyether polyol products made using the catalyst compositions have exceptionally low unsaturations. BACKGROUND OF THE INVENTION Double metal cyanide complex compounds are well known catalysts for epoxide polymerization. The catalysts are highly active, and give polyether polyols that have low unsaturation compared with similar polyols made using basic (KOH) catalysis. Conventional DMC catalysts are prepared by reacting aqueous solutions of metal salts and metal cyanide salts to form a precipitate of the DMC compound. The catalysts can be used to make a variety of polymer products, including polyether, polyester, and polyetherester polyols. Many of the polyols are useful in various polyurethane coatings, elastomers, sealants, foams, and adhesives. Conventional DMC catalysts are usually prepared in the presence of a low molecular weight complexing agent, typically an ether such as glyme (dimethoxyethane) or diglyme. The ether complexes with the DMC compound, and favorably impacts the activity of the catalyst for epoxide polymerization. In one conventional preparation, aqueous solutions of zinc chloride (excess) and potassium hexacyahocobaltate are combined by simple mixing. The resulting precipitate of zinc hexacyanocobaltate is then mixed with aqueous glyme. An active catalyst is obtained that has the formula: Zn 3 [Co(CN) 6 ] 2 · xZnCl 2 · yH 2 O · zGlyme Other known complexing agents include alcohols, ketones, esters, amides, ureas, and the like. (See, for example, U.S. Patent Nos. 3,427,256, 3,427,334, 3,278,459, and Japanese Pat. Appl. Kokai Nos. 4-145123, 3-281529 and 3-149222). Generally, the catalyst made with glyme has been the catalyst of choice. The catalysts have relatively high surface areas, typically within the range of about 50-200 m 2 /g. Normally, the complexing agent is added to the reaction mixture following precipitation of the DMC compound. Some references, such as U.S. Pat. No. 5,158,922, indicate that the complexing agent can be included with either or both of the aqueous reactant solutions, but no reference teaches any particular advantage of having the complexing agent present in the reactant solutions. Double metal cyanide compounds prepared in the absence of a complexing agent are highly crystalline by X-ray diffraction analysis (See Fig. 4), and are inactive for epoxide polymerization. When the complexing agents described above are used, the resulting catalysts actively polymerize epoxides. Our X-ray diffraction analyses of active DMC complexes prepared according to methods known in the art suggest that conventional DMC catalysts are actually mixtures of a highly crystalline DMC compound and a more amorphous component. Typically, conventional DMC catalysts--which are generally prepared by simple mixing--contain at least about 35 wt.% of highly crystalline DMC compound. DMC compounds useful as epoxide polymerization catalysts and containing less than about 30 wt.% of highly crystalline DMC compound are not known. Double metal cyanide catalysts generally have good activity for epoxide polymerizations, often much greater than conventional basic catalysts. However, because the DMC catalysts are rather expensive, catalysts with improved activity are desirable because reduced catalyst levels could be used. Double metal cyanide catalysts normally require an "induction" period. In contrast to basic catalysts, DMC catalysts ordinarily will not begin polymerizing epoxides immediately following exposure of epoxide and starter polyol to the catalyst. Instead, the catalyst needs to be activated with a small proportion of epoxide before it becomes safe to begin continuously adding the remaining epoxide. Induction periods of an hour or more are typical yet costly in terms of increased cycle times in a polyol production facility. Reduction or elimination of the induction period is desirable. An advantage of DMC catalysts is that they permit the synthesis of high molecular weight polyether polyols having relatively low unsaturation. The adverse impact of polyol unsaturation on polyurethane properties is well documented. (See, for example, C.P. Smith et al., J. Elast. Plast ., 24 (1992) 306, and R.L. Mascioli, SPI Proceedings, 32nd Annual Polyurethane Tech./Market. Conf. (1989) 139.) When a DMC catalyst is used, polyols having unsaturations as low as about 0.015 meq/g can be made. Polyether polyols with even lower unsaturations can be made if a solvent such as tetrahydrofuran is used to make the polyol. See, for example, U.S. Pat. Nos. 3,829,505 and 4,843,054. However, for commercial polyol production, the use of a solvent is not particularly desirable. Thus, other ways to further reduce polyol unsaturation are needed. When conventional DMC catalysts are used to polymerize epoxides, the polyether polyol products contain relatively low levels (about 5-10 wt.%) of low molecular weight polyol impurities. A way to eliminate these polyol impurities is desirable because improved polyurethanes could result from the use of more monodisperse polyols. Double metal cyanide complex catalyst residues are often difficult to remove from polyether polyols, and a wide variety of methods have been developed to cope with the problem. Removal of DMC catalyst residues from the polyols promotes long-term storage stability and consistent polyol performance in urethane formulation. Most methods involve some kind of chemical treatment of the polyol following polymerization. There has been little progress made in developing catalyst preparation methods that ultimately facilitate catalyst removal from the polyol products. SUMMARY OF THE INVENTION This invention relates to a method of making a double metal cyanide (DMC) complex, which method comprises reacting an aqueous solution of a metal salt and an aqueous solution of a metal cyanide salt wherein one or both of the reactant solutions contains an organic complexing agent and wherein the metal cyanide salt solution is added to the metal salt solution. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 shows a plot of propylene oxide consumption versus time during a polymerisation reaction with one of the catalyst compositions of the invention at 250 ppm catalyst. The induction time for the run is measured as discussed in Example 6 from the intersection of the extended baseline and slope measurements. Figures 2-10 are powder x-ray diffraction patterns of various double metal cyanide compounds. These are described more fully below. DETAILED DESCRIPTION OF THE INVENTION The catalysts of the invention, unlike conventional DMC compounds known in the art as useful for epoxide polymerization, comprise at least about 70 wt.% of a substantially amorphous DMC complex. More preferred catalysts of the invention comprise at least about 90 wt.% of a substantially amorphous DMC complex; most preferred are catalysts comprising at least about 99 wt.% of a substantially amorphous DMC complex. As defined in this application, "substantially amorphous" means substantially noncrystalline, lacking a well-defined crystal structure, or characterized by the substantial absence of sharp lines in the X-ray diffraction pattern of the composition. Powder X-ray diffraction (XRD) patterns of conventional double metal cyanide catalysts show characteristic sharp lines that correspond to the presence of a substantial proportion of a highly crystalline DMC component (see Figs. 2 and 3). Highly crystalline zinc hexacyanocobaltate prepared in the absence of an organic complexing agent, which does not actively polymerize epoxides, shows a characteristic XRD fingerprint of sharp lines at d-spacings of about 5.07, 3.59, 2.54, and 2.28 angstroms (see Fig. 4). When a DMC catalyst is made in the presence of an organic complexing agent according to conventional methods, the XRD pattern shows lines for the highly crystalline material in addition to broader signals from relatively amorphous material, suggesting that conventional DMC epoxidation catalysts are actually mixtures of highly crystalline DMC compound and a more amorphous component (see Fig. 3). Typically, conventional DMC catalysts, which are generally prepared by simple mixing, contain at least about 35 wt.% of highly crystalline DMC compound. The catalysts of the invention are distinguishable from conventional DMC compositions based on their substantial lack of crystalline material. The substantial lack of crystallinity is evidenced by an XRD pattern showing that little or no highly crystalline DMC compound is present. When a zinc hexacyanocobaltate catalyst is prepared according to the method of the invention using tert-butyl alcohol as a complexing agent, for example, the X-ray diffraction pattern shows essentially no lines for crystalline zinc hexacyanocobaltate (5.07, 3.59, 2.54, 2.28 angstroms), but instead has only two major lines, both relatively broad, at d-spacings of about 4.82 and 3.76 angstroms (see Fig. 5). A similar pattern is observed when the method of the invention is used with glyme as a complexing agent (see Fig. 6). Spiking experiments demonstrate that DMC catalysts prepared by the method of the invention typically contain less than about 1 wt.% of highly crystalline DMC compound. (See Fig. 7, which shows that even 1 wt.% of highly crystalline DMC compound can be detected by X-ray analysis when spiked into a sample of a substantially amorphous catalyst of the invention). Fig. 8 shows a mixture that contains a substantially amorphous DMC catalyst spiked with 5 wt.% of highly crystalline DMC compound. Fig. 9 shows a mixture that contains a substantially amorphous DMC catalyst spiked with 25 wt.% of highly crystalline DMC compound. (Such a catalyst falls within the scope of the invention, which contains at least 70 wt.% of a substantially amorphous DMC catalyst.) Finally, Fig. 10 shows that the X-ray pattern for a substantially amorphous catalyst of the invention, when spiked with 40 wt.% of highly crystalline DMC compound, closely resembles the pattern observed for a DMC catalyst made by a conventional catalyst preparation. Some of the X-ray results are summarized in Table 1. Conventional DMC catalysts typically contain at least about 35 wt.% of highly crystalline DMC compound. No one has previously recognized the desirability of preparing substantially amorphous catalysts, and the potential value of reducing the content of highly crystalline DMC compounds in these catalysts. It appears, based on our results, that the highly crystalline DMC compound acts as either a diluent or as a poison for the more active amorphous form of the catalyst, and its presence is preferably minimized or eliminated. The invention includes compositions which comprise at least about 70 wt.% of the substantially amorphous DMC complex catalysts of the invention and up to about 30 wt.% of a highly crystalline DMC compound. More preferred compositions of the invention comprise at least about 90 wt.% of the substantially amorphous DMC complex catalyst and up to about 10 wt.% of the highly crystalline DMC compound. Most preferred are compositions that contain at least about 99 wt.% of the substantially amorphous DMC complex catalyst and up to about 1 wt.% of the highly crystalline material. The catalyst compositions of the invention have relatively low surface areas. Conventional DMC compounds have surface areas within the range of about 50 to about 200 m 2 /g. In contrast, the surface areas of the catalysts of the invention are preferably less than about 30 m 2 /g. More preferred compositions have surface areas less than about 20 m 2 /g. Double metal cyanide compounds useful in the invention are the reaction products of a water-soluble metal salt and a water-soluble metal cyanide salt. The water-soluble metal salt preferably has the general formula M(X) n in which M is selected from the group consisting of Zn(ll), Fe(ll), Ni(ll), Mn(ll), Co(II), Sn(ll), Pb(ll), Fe(lll), Mo(lV), Mo(VI), Al(lll), V(V), V(IV), Sr(ll), W(lV), W(VI), Cu(ll), and Cr(lll). More preferably, M is selected from the group consisting of Zn(ll), Fe(ll), Co(ll), and Ni(ll). In the formula, X is preferably an anion selected from the group consisting of halide, hydroxide, sulfate, carbonate, cyanide, oxalate, thiocyanate, isocyanate, isothiocyanate, carboxylate, and nitrate. The value of n is from 1 to 3 and satisfies the valency state of M. Examples of suitable metal salts include, but are not limited to, zinc chloride, zinc bromide, zinc acetate, zinc acetonylacetate, zinc benzoate, zinc nitrate, iron(ll) sulfate, iron(ll) bromide, cobalt(ll) chloride, cobalt(ll) thiocyanate, nickel(ll) formate, nickel(ll) nitrate, and the like, and mixtures thereof. The water-soluble metal cyanide salts used to make the double metal cyanide compounds useful in the invention preferably have the general formula (Y) a M'(CN) b (A) c in which M' is selected from the group consisting of Fe(II), Fe(lll), Co(ll), Co(lll), Cr(ll), Cr(lll), Mn(ll), Mn(lll), lr(lll), Ni(ll), Rh(lll), Ru(II), V(lV), and V(V). More preferably, M' is selected from the group consisting of Co(ll), Co(lll), Fe(ll), Fe(lll), Cr(lll), lr(lll), and Ni(ll). The water-soluble metal cyanide salt can contain one or more of these metals. In the formula, Y is an alkali metal ion or alkaline earth metal ion. A is an anion selected from the group consisting of halide, hydroxide, sulfate, carbonate, cyanide, oxalate, thiocyanate, isocyanate, isothiocyanate, carboxylate, and nitrate. Both a and b are integers greater than or equal to 1; the sum of the charges of a, b, and c balances the charge of M'. Suitable water-soluble metal cyanide salts include, but are not limited to, potassium hexacyanocobaltate(III), potassium hexacyanoferrate(II), potassium hexacyanoferrate(III), calcium hexacyanocobaltate(III), lithium hexacyanoiridate(III), and the like. Examples of double metal cyanide compounds that can be used in the invention include, for example, zinc hexacyanocobaltate(III), zinc hexacyanoferrate(III), zinc hexacyanoferrate(II), nickel(ll) hexacyanoferrate(II), cobalt(ll) hexacyanocobaltate(III), and the like. Further examples of suitable double metal cyanide compounds are listed in U.S. Patent No. 5,158,922, the teachings of which are incorporated herein by reference. The catalyst compositions of the invention are prepared in the presence of a complexing agent. Generally, the complexing agent must be relatively soluble in water. Suitable complexing agents are those commonly known in the art, as taught, for example, in U.S. Patent No. 5,158,922. The complexing agent is added either during preparation or immediately following precipitation of the catalyst. As is explained elsewhere in this application, the manner in which the complexing agent is introduced into the DMC complex can be extremely important. Usually, an excess amount of the complexing agent is used. Preferred complexing agents are water-soluble heteroatom-containing organic compounds that can complex with the double metal cyanide compound. Suitable complexing agents include, but are not limited to, alcohols, aldehydes, ketones, ethers, esters, amides, ureas, nitriles, sulfides, and mixtures thereof. Preferred complexing agents are water-soluble aliphatic alcohols selected from the group consisting of ethanol, isopropyl alcohol, n-butyl alcohol, isobutyl alcohol, sec-butyl alcohol, and tert-butyl alcohol. Tert-butyl alcohol is most preferred. The conventional method of preparing DMC compounds useful for epoxide polymerization is fully described in many references, including U.S. Patent Nos. 5,158,922, 4,843,054, 4,477,589, 3,427,335, 3,427,334, 3,427,256, 3,278,457, and 3,941,849, and Japanese Pat. Appl. Kokai No. 4-145123. The teachings of these references related to conventional catalyst preparation and suitable DMC compounds are incorporated herein by reference in their entirety. The invention includes methods for making substantially amorphous DMC catalyst compositions of the invention. We surprisingly found, however, that when an organic complexing agent is present in one or both of the reactant solutions before they are combined a much more active catalyst results if the metal cyanide salt solution is added to the metal salt solution. See Examples 13-14 below. Thus, in accordance with the method of this invention, it is necessary to add the metal cyanide salt solution to the metal salt solution. The invention includes a process for making an epoxide polymer. This process comprises polymerizing an epoxide in the presence of a double metal cyanide catalyst composition of the invention. Preferred epoxides are ethylene oxide, propylene oxide, butene oxides, styrene oxide, and the like, and mixtures thereof. The process can be used to make random or block copolymers. The epoxide polymer can be, for example, a polyether polyol derived from the polymerization of an epoxide in the presence of a hydroxyl group-containing initiator. Other monomers that will copolymerize with an epoxide in the presence of a DMC compound can be included in the process of the invention to make other types of epoxide polymers. Any of the copolymers known in the art made using conventional DMC catalysts can be made with the catalysts of the invention. For example, epoxides copolymerize with oxetanes (as taught in U.S. Patent Nos. 3,278,457 and 3,404,109) to give polyethers, or with anhydrides (as taught in U.S. Patent Nos. 5,145,883 and 3,538,043) to give polyester or polyetherester polyols. The preparation of polyether, polyester, and polyetherester polyols using double metal cyanide catalysts is fully described, for example, in U.S. Patent Nos. 5,223,583, 5,145,883, 4,472,560, 3,941,849, 3,900,518, 3,538,043, 3,404,109, 3,278,458, 3,278,457, and in J.L. Schuchardt and S.D. Harper, SPI Proceedings, 32nd Annual Polyurethane Tech./Market. Conf. (1989) 360. The teachings of these U.S. patents related to polyol synthesis using DMC catalysts are incorporated herein by reference in their entirety. The substantially amorphous DMC catalysts of the invention are highly active compared to conventional DMC catalysts. For example, a zinc hexacyanocobaltate catalyst made using tert-butyl alcohol as a complexing agent and made by homogenization (and containing less than 1 wt.% of crystalline DMC compound by X-ray analysis) is about 65% more active at 100 ppm, and 200% more active at 130-250 ppm, than the same catalyst made by simple mixing (and containing about 35 wt.% crystalline DMC compound). A consequence of higher polymerization rates is that polyol producers can use less of the relatively expensive DMC catalyst and save money. More active catalysts also permit the producer to reduce batch times and increase productivity. The substantially amorphous catalyst compositions of the invention show a reduced induction period compared with conventional catalysts in a polyether polyol synthesis. Conventional DMC catalysts are not immediately active toward epoxide polymerization. Typically, a starter polyol, the catalyst, and a small amount of epoxide are combined and heated to the desired reaction temperature, and no epoxide polymerizes immediately. The polyol manufacturer must wait (often for several hours) until the catalyst becomes active and the charged epoxide begins to react before additional epoxide can safely be continuously added to the polymerization reactor. The substantially amorphous catalysts of the invention are more rapidly activated than conventional catalysts that contain up to 35 wt.% of crystalline DMC compound. This feature of the catalysts is also an economic advantage because delays in adding the epoxide are reduced. Polyether polyols prepared using the catalysts of the invention have exceptionally low unsaturations, consistently less than about 0.007 meq/g. These unsaturations are at least about 50% lower than polyol unsaturations available from the DMC catalysts previously known. Preferred polyols of the invention have unsaturations less than about 0.006 meq/g, and more preferably less than about 0.005 meq/g. The reduction in unsaturation compared with polyols previously available from conventional DMC catalysts should offer some advantages for polyurethanes made with the polyols of the invention. Polyether polyols made with the catalysts of the invention preferably have average hydroxyl functionalities from about 2 to 8, more preferably from about 2 to 6, and most preferably from about 2 to 3. The polyols preferably have number average molecular weights within the range of about 500 to about 50,000. A more preferred range is from about 1,000 to about 12,000; most preferred is the range from about 2,000 to about 8,000. Polyols prepared with the catalysts of the invention also have substantially lower levels of low molecular weight polyol impurities compared with polyols prepared with conventional catalysts. Gel permeation chromatography (GPC) analysis of these polyols shows no detectable low molecular weight polyol impurities. In contrast, conventional DMC catalysts made in the usual way with glyme as a complexing agent show a marked GPC peak corresponding to about 5-10 wt.% of a low molecular weight polyol impurity. Interestingly, polyols made with the catalysts of the invention are usually clearer than polyols made with conventional glyme catalysts; the former typically remain clear even after weeks of storage at room temperature, while the latter tend to quickly develop a haze during storage. Another advantage of the substantially amorphous catalysts of the invention is that they are more easily removed from polyether polyols following polyol synthesis compared with conventional DMC compounds. The problem of how to remove DMC compounds from polyether polyols has been the subject of many investigations (see, for example, U.S. Patent Nos. 5,144,093, 5,099,075, 5,010,047, 4,987,271, 4,877,906, 4,721,818, and 4,355,188). Most of these methods irreversibly deactivate the catalyst. The catalysts of the invention can be isolated by simply filtering the polyol. Another way to isolate the catalyst is to first dilute the polyol with a solvent such as heptane to reduce viscosity, then filter the mixture to recover the catalyst, and then strip the polyol/heptane mixture to obtain the purified polyol. The methods described in U.S. Patent No. 5,010,047 can also be used to recover the catalysts of the invention from polyols. An advantage of the catalysts of the invention is that they can be removed cleanly from polyols even with a hot filtration in the absence of any solvent. In contrast, when a polyol made with a conventional glyme catalyst is hot-filtered, substantial amounts of the DMC compound remain in the polyol. If desired, the isolated catalyst composition of the invention can be recovered and reused to catalyze another epoxide polymerization reaction because these simple filtration methods do not generally deactivate the catalysts. The following Examples illustrate the invention. EXAMPLE 1 Epoxide Polymerizations: Rate Experiments--General Procedure A one-liter stirred reactor is charged with polyoxypropylene triol (700 mol. wt.) starter (70 g) and zinc hexacyanocobaltate catalyst (0.057 to 0.143 g, 100-250 ppm level in finished polyol. The mixture is stirred and heated to 105°C, and is stripped under vacuum to remove traces of water from the triol starter. The reactor is pressurized to about 1 psi with nitrogen. Propylene oxide (10-11 g) is added to the reactor in one portion, and the reactor pressure is monitored carefully. Additional propylene oxide is not added until an accelerated pressure drop occurs in the reactor; the pressure drop is evidence that the catalyst has become activated. When catalyst activation is verified, the remaining propylene oxide (490 g) is added gradually over about 1-3 h at a constant pressure of 20-24 psi. After propylene oxide addition is complete, the mixture is held at 105°C until a constant pressure is observed. Residual unreacted monomer is then stripped under vacuum from the polyol product, and the polyol is cooled and recovered. To determine reaction rate, a plot of PO consumption (g) vs. reaction time (min) is prepared (see Fig. 1). The slope of the curve at its steepest point is measured to find the reaction rate in grams of PO converted per minute. The intersection of this line and a horizontal line extended from the baseline of the curve is taken as the induction time (in minutes) required for the catalyst to become active. EXAMPLE 2 Polyether Polyol Synthesis: Effect of Catalyst on Polyol Unsaturation, Catalyst Removal, and Polyol Quality A two-gallon stirred reactor is charged with polyoxypropylene triol (700 mol. wt.) starter (685 g) and zinc hexacyanocobaltate catalyst (1.63 g). The mixture is stirred and heated to 105°C, and is stripped under vacuum to remove traces of water from the triol starter. Propylene oxide (102 g) is fed to the reactor, initially under a vacuum of 30 in. (Hg), and the reactor pressure is monitored carefully. Additional propylene oxide is not added until an accelerated pressure drop occurs in the reactor; the pressure drop is evidence that the catalyst has become activated. When catalyst activation is verified, the remaining propylene oxide (5713 g) is added gradually over about 2 h while maintaining a reactor pressure less than 40 psi. After propylene oxide addition is complete, the mixture is held at 105°C until a constant pressure is observed. Residual unreacted monomer is then stripped under vacuum from the polyol product. The hot polyol product is filtered at 100°C through a filter cartridge (0.45 to 1.2 microns) attached to the bottom of the reactor to remove the catalyst. Residual Zn and Co are quantified by X-ray analysis. Polyether diols (from polypropylene glycol starter, 450 mol. wt.) and triols are prepared as described above using zinc hexacyanocobaltate catalysts made by conventional methods (stirring) and by the method of the invention (homogenization). EXAMPLES 3 and 4 Effect of Order of Addition of Reactant Solutions on Catalyst Activity Tert-Butyl Alcohol Added During Formation of the DMC Compound EXAMPLE 3 Solution 1 is prepared by dissolving zinc chloride (75 g) in tert-butyl alcohol (50 mL) and distilled water (275 mL). Solution 2 is prepared by dissolving potassium hexacyanocobaltate (7.5 g) in distilled water (100 mL). Solution 3 is prepared by mixing tert-butyl alcohol (2 mL) and distilled water (200 mL). Solution 2 is added to solution 1 over 30 min. with homogenization. Mixing by homogenization continues for an additional 10 min. A stir bar is added. Solution 3 is added, and the mixture is slowly stirred magnetically for 3 min. The mixture is filtered under pressure at 40 psig. The filter cake is reslurried in tert-butyl alcohol (130 mL) and distilled water (55 mL), and the mixture is homogenized for 10 min. The mixture is filtered as described before. The cake is reslurried in neat tert-butyl alcohol (185 mL), and is homogenized for 10 min. The mixture is filtered, and the cake is dried under vacuum at 60°C. Yield: 8.6 g. The catalyst is used to polymerize propylene oxide as described in Example 1. The rate of polymerization at 105°C and 10 psig at 100 ppm catalyst is 26.3 g PO/min. EXAMPLE 4 Solution 1 is prepared by dissolving potassium hexacyanocobaltate (7.5 g) in distilled water (300 mL) and tert-butyl alcohol (50 mL). Solution 2 is prepared by dissolving zinc chloride (75 g) in distilled water (75 mL). Solution 3 is prepared from tert-butyl alcohol (2 mL) and distilled water (200 mL). Solution 2 is added to solution 1 over 30 min. with homogenization. Mixing by homogenization continues for an additional 10 min. A stir bar is added. Solution 3 is added, and the mixture is slowly stirred magnetically for 3 min. The mixture is filtered under pressure at 40 psig. The catalyst is isolated, washed, and dried as described in Example 3. The catalyst is used to polymerize propylene oxide as described in Example 1. The rate of polymerization at 105°C and 10 psig at 100 ppm catalyst is 15.6 g PO/min. The results from Examples 3 and 4 show the effect of reversing the order of addition of reagents in a process of the invention. The results show the unexpectedly higher catalyst activity available from a catalyst made by adding the metal cyanide salt solution to the metal salt solution.

Claims: A method of making a double metal cyanide (DMC) complex, which method comprises reacting an aqueous solution of a metal salt and an aqueous solution of a metal cyanide salt wherein one or both of the reactant solutions contains an organic complexing agent and wherein the metal cyanide salt solution is added to the metal salt solution. A method according to claim 1 wherein the complexing agent is selected from an alcohol, aldehyde, ketone; ether, ester, amide, urea, nitrile, sulfide or a mixture thereof. A method, according to claim 2 wherein the alcohol is a water-soluble aliphatic alcohol. A method according to claim 3 wherein the water-soluble aliphatic alcohol comprises ethanol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, tert-butyl alcohol, isobutyl alcohol or a mixture thereof. A method according to claim 4 wherein the water-soluble aliphatic alcohol comprises tert-butyl alcohol. A method according to any preceding claim wherein the DMC complex is a zinc hexacyanocobaltate.

Inventors: BOWMAN PAUL T, HINNEY HARRY R, LE-KHAC BI, BOWMAN, PAUL T., HINNEY, HARRY R., LE-KHAC, BI
Applicants: BAYER ANTWERPEN NV, BAYER ANTWERPEN N.V.
Application year: 1996
Main classification: B01J27
IPC codes: C08G59, C08G65, B01J27, C01C3