A process for preparing diols by using a modified raney nickel catalyst

Abstract: The present invention relates to a modified Raney nickel catalyst which can serve as a hydrogenation catalyst for hydroxy aldehydes, such as 4-hydroxy-butanal, and 2-methyl-3-hydroxypropanal and hydroxy cyclic ethers such as 2-hydroxy-tetrahydrofuran. Further, a process for preparing diols by using the modified Raney nickel catalyst is provided.

Description: 1. Field of the Invention The present invention relates to a modified Raney nickel catalyst and a process for preparing diols by using the modified Raney nickel catalyst. 2. Background of the Invention Conventionally, 4-hydroxy-butanal, 2-hydroxy-tetrahydrofuran, and 2-methyl-3-hydroxypropanal are industrially prepared by hydroformylating allyl alcohol carbon monoxide, and hydrogen in the presence of rhodium as a catalyst. The reactions of the conventional processes are shown as follows: 4-hydroxy-butanal and 2-hydroxy-tetrahydrofuran can be used for producing 1,4-butanediol through hydrogenation while 2-methyl-3-hydroxypropanal can be used for producing 2-methyl-1,3-propanediol through hydrogenation. The reactions thereof are shown as follows: HCOCH 2 CH 2 CH 2 OH+H 2 →CH 2 OHCH 2 CH 2 CH 2 OH The hydrogenation of 4-hydroxy-butanal and 2-methyl-3-hydroxypropanal is subject to hydrogenation of the carbonyl group. Presently, the catalyst used in the process of hydrogenation of the carbonyl group is selected from precious metals including palladium, which is disclosed in Biochemistry Journal , 1943, Vol. 37, p.726; platinum, which is disclosed in Journal of American Chemical Society, 1948, Vol. 70. p.664; ruthenium, which is disclosed in U.S. Patent No. 3,144,490; rhenium, which is disclosed in Journal of Organic Chemistry, 1959, Vol. 24, p.1847; copper chromite, which is disclosed in Industrial and Engineering Chemistry , 1946, Vol. 38, p.251; copper, which is disclosed in British Patent No. 659,981; nickel, which is disclosed in Journal of Chemical Society, Japan, Industrial Chemistry Section, 1943, Vol. 46, p.901; Raney nickel, which is disclosed in Journal of American Chemical Society, 1948, Vol. 70, p.695; Raney cobalt, which is disclosed in Journal of Applied Chemistry, 1958, Vol. 8, p.492; and so on. EP-A-0572812 discloses the production of 1,3-propane diol by catalytic hydrogenation of 3-hydroxypropionaldehyde. Through long-term experiments, it has been found by the inventors that the hydrogenations of 4-hydroxy-butanal, 2-hydroxy-tetrahydrofuran, and 2-methyl-3-hydroxypropanal differ from those of other carbonyl groups. For instance, the use of palladium or zinc copper oxide as catalyst shows almost no reaction activity; and the use of ruthenium or copper chromite as catalyst shows only relatively low reaction activity to the hydrogenation, which provides little utilization value. Only nickel and Raney nickel provide higher reaction activity to the hydrogenation. However, a drawback has subsequently been found to the use of nickel or Raney nickel as catalyst in the aforementioned hydrogenation process in that their reaction activities rapidly decay after repetitive use. More specifically, after batchwise repetitive use exceeding 33 batches or continuous use exceeding 30 hours, their reaction activity significantly decreases to a low level that cannot practically be used further. Accordingly, the use of nickel or Raney nickel as catalyst in the hydrogenation process for producing 1,4-butanediol, 2-methyl-1,3-propanediol from 4-hydroxy-butanal, 2-hydroxy-tetrahydrofuran, and 2-methyl-3-hydroxypropanal is still not a practical approach in the chemical industry. 3. Summary of the Invention It is therefore a primary objective of the present invention to provide a modified Raney nickel catalyst which is of high and long-lasting reaction activity for the hydrogenation of 4-hydroxy-butanal, 2-hydroxytetrahydrofuran, and 2-methyl-3-hydroxypropanal. It is another objective of the present invention to provide an improved process for preparing diols by using the modified Raney nickel catalyst. In accordance with the foregoing and other objectives of the present invention, there is provided a modified Raney nickel catalyst and a process for preparing diols by using the modified Raney nickel catalyst. It is found through experiments that Raney nickel modified by the addition of iron or iron and at least one metal selected from the group consisting of chromium, molybdenum, tungsten, cobalt, manganese, and titanium shows a relatively high reaction activity to the process for preparing diols and allows long-term use thereof as the catalyst for the process for preparing diols. The provision of the catalyst according to the present invention thus enables the preparation of 1,4-butanediol and 2-methyl-1,3-propanediol through hydrogenation of 4-hydroxy-butanal, 2-hydroxytetrahydrofuran, and 2-methyl-3-hydroxypropanal to have high commercial value. 4. Detailed Description of the Invention The modified Raney nickel catalyst according to the present invention consists essentially of 40-98 wt% of nickel, 1-50 wt% of aluminium, and 0.05-15 wt% of iron. If necessary, the modified Raney nickel catalyst can be further added with 0.05-10 wt% of at least one metal selected from the group consisting of chromium, molybdenum, tungsten, cobalt, manganese, and titanium. The process for producing the modified Raney nickel catalyst according to the present invention is essentially similar to conventional ones for producing Raney nickel catalyst. Typically, predetermined amounts of nickel, aluminium, and iron are mixed first and, if necessary, at least one metal selected from the group consisting of chromium, molybdenum, tungsten, cobalt, manganese, and titanium may be added thereto. The mixture is then melted at a temperature of 1200 to 2000°C to produce a precursor alloy. After being sat still and cooled, the precursor alloy is crushed into powder or granules with suitable size and then developed in a solution of alkali metal hydroxide. Finally, the thus-obtained product is washed with distilled or ion-exchanged water to obtain the modified Raney nickel catalyst. The modified Raney nickel catalyst according to the present invention is useful as a catalyst in the hydrogenation of hydroxy aldehydes, particularly 4-hydroxybutanal and 2-methyl-3-hydroxypropanal, and hydroxycyclic ethers, particularly 2-hydroxy-tetrahydrofuran. Moreover, the modified Raney nickel catalyst according to the present invention can be used in a process for producing diols. In the process, hydroxy aldehyde is hydrogenated under a temperature of 50 to 200°C, preferably 75 to 150°C, and a pressure of 980 kPa (10 kg/cm 2 G) to 19600 kPa (200 kg/cm 2 G), preferably 1960 kPa (20 kg/cm 2 G) to 7850 kPa (80 kg/cm 2 G) to obtain diols. In the foregoing process, the reactor used therefor depends on the form of catalyst used. If the catalyst is powder type, then a slurry bed reactor is used; while if the catalyst is granule type, a fixed bed reactor is used. The process can be proceeding continuously or in a batchwise manner. In the case of the slurry bed reactor, the amount of the catalyst used is 0.5-20 wt% based on the total weight of solution; and in the case of the fixed bed reactor, the liquid hourly space velocity (LHSV) is 0.1 to 10hr -1 . In the process according to the present invention, the hydroxy aldehyde used can be 4-hydroxy-butanal, 2-hydroxytetrahydrofuran, or 2-methyl-3-hydroxypropanal. It is a primary benefit of the modified Raney nickel catalyst according to the present invention that it is of high reaction activity and long use life. Examples used to illustrate the present invention are respectively carried out in slurry bed reactor and fixed bed reactor and described in the following. It is to be understood that the scope of the present invention is not to be limited by the following disclosed examples. 1. Experiments with Slurry Bed Reactor EXAMPLE 1: 0.781 g of carbonylhydrotris(triphenyl phosphine)rhodium, 21.6 g of triphenyl phosphine, 55.4 g of allyl alcohol, and 73.6 g of toluene were charged to a pressure-resistant glass stirring reactor controlled at a temperature of 60°C and filled with carbon monoxide and hydrogen (in a molar ratio of 1) to have a pressure of 7 kg/cm 2 G to carry out hydroformylation for a period of 6.5 hours. Then the solution was extracted by deionized water to obtain a top layer of toluene solution containing hydroformylation catalyst and a bottom layer of aqueous solution containing 4-hydroxy-butanal, 2-hydroxytetrahydrofuran, and 2-methyl-3-hydroxypropanal. An alloy containing 38.5 wt% of nickel (Ni), 58.4 wt% of aluminium (Al), 1.4 wt% of iron (Fe), and 1.7 wt% of chromium (Cr) was melted at a temperature of 1650°C. After cooling, the thus-obtained alloy was granulated to a granularity of 20-150µm. 30 g of sodium hydroxide was then dissolved in 150 ml of water under stirring while the temperature was lowered to 50 to 60°C. 20 g of the alloy powder was added to the sodium hydroxide solution and the thus-obtained solution was then heated to a temperature of 50 to 100°C followed by stirring for a period of 30 to 120 minutes to disperse the alloy powder. After dispersal, the solution was washed with deionized water until the pH of the washings was in the range between 8 and 9. Then a Raney nickel catalyst for hydrogenation containing 85 wt% of nickel (Ni), 9.5 wt% of aluminium (Al), 2.5 wt% of iron (Fe), and 3.0 wt% of chromium (Cr) was obtained. 420 ml of the solution containing 4-hydroxy-butanal, 2-hydroxy-tetrahydrofuran, and 2-methyl-3-hydroxypropanal was charged to a stainless jacket-stirring reactor equipped with a metal powder-sintered filtering core followed by adding 9.38 g of the thus-obtained hydrogenation catalyst (65% of which has a granularity less than 50µm). The temperature in the reactor was controlled at 115°C and the pressure in the reactor was maintained at 5880 kPa (60 kg/cm 2 G) by the supply of hydrogen to effect hydrogenation for 2 hours under stirring. After the supply of hydrogen was cut off, the stirring was stopped and the solution was set still for 30 minutes to precipitate the catalyst. The solution was filtrated via the filtering core by the hydrogen pressure in the reactor, then about 400 ml of the top layer of the solution was removed and analyzed by gas chromatograph to obtain a result of 16.64 wt% of 1,4-butanediol, 3.25 wt% of 2-methyl-1,3-propanediol, 80.11 wt% of other reactants and water. Another 400 ml aqueous solution of 4-hydroxybutanal, 2-hydroxy-tetrahydrofuran, and 2-methyl-3-hydroxypropanal was then added to the reactor and subjected to hydrogenation for 2 hours under the same conditions. This process was repeated for 50 batches. The conversion thereof was maintained consistently at about 95-98%, which was calculated by the results obtained from gas chromatograph (GC) according to the following equation: Conversion = HBA1 - HBA2 HBA1 * 100% wherein HBA1 represents the concentration of the solution of 4-hydroxy-butanal, 2-hydroxy-tetrahydrofuran, and 2-methyl-3-hydroxypropanal obtained via GC analysis before hydrogenation; and HBA2 represents the concentration of the solution of 4-hydroxy-butanal, 2-hydroxy-tetrahydrofuran, and 2-methyl-3-hydroxypropanal obtained via GC analysis after hydrogenation. EXAMPLE 2: Hydrogenation was carried out in the same manner as that of Example 1 except that 57% of the Raney nickel catalyst for hydrogenation was of a granularity of less than 50µm and the composition of the catalyst consisted of 87.1 wt% of nickel (Ni), 9.9 wt% of aluminium (Al), 3.0 wt% of iron (Fe). The process was repeated for 50 batches. The conversion was consistently maintained at about 93-98%. EXAMPLE 3: Hydrogenation was carried out in the same manner as that of Example 1 except that 90% of the Raney nickel catalyst for hydrogenation was of a granularity of less than 87 µm and the composition of the catalyst consisted of 87.0 wt% of nickel (Ni), 9.9 wt% of aluminium (Al), 0.1 wt% of iron (Fe), and 3.0 wt% of chromium (Cr). The process was repeated for 46 batches. The conversion was consistently maintained at about 90-98%. EXAMPLE 4: Hydrogenation was carried out in the same manner as that of Example 1 except that 90% of the Raney nickel catalyst for hydrogenation was of a granularity of less than 162 µm and the composition of the catalyst consisted of 92.0 wt% of nickel (Ni), 6.1 wt% of aluminium (Al), 0.7 wt% of iron (Fe), and 1.2 wt% of molybdenum (Mo). The process was repeated for 45 batches. The conversion was consistently maintained at about 90-98%. EXAMPLE 5: Hydrogenation was carried out in the same manner as that of Example 1 except that 65% of the Raney nickel catalyst for hydrogenation was of a granularity of less than 50 µm and the composition of the catalyst consisted of 86.0 wt% of nickel (Ni), 9.5 wt% of aluminium (Al), 0.5 wt% of iron (Fe), 0.2 wt% of titanium (Ti), and 2.0 wt% of tungsten (W). The process was repeated for 40 batches. The conversion was consistently maintained at about 90-98%. EXAMPLE 6: Hydrogenation was carried out in the same manner as that of Example 1 except that 46.8% of the Raney nickel catalyst for hydrogenation was of a granularity of less than 44 µm and the composition of the catalyst consisted of 87.0 wt% of nickel (Ni), 11.6 wt% of aluminium (Al), 1.2 wt% of iron (Fe), and 0.2 wt% of manganese (Mn). The process was repeated for 38 batches. The conversion was consistently maintained at about 90-98%. COMPARATIVE EXAMPLE 1 : Hydrogenation was carried out in the same manner as that of Example 1, except that 83.0% of the Raney nickel catalyst for hydrogenation was of a granularity of less than 50 µm and the composition of the catalyst consisted of 92.7 wt% of nickel (Ni), 6.1 wt% of aluminium (Al), and 1.2 wt% of molybdenum (Mo). The process was repeated for 33 batches. The conversion was then reduced from 90% to 70%. COMPARATIVE EXAMPLE 2: Hydrogenation was carried out in the same manner as that of Example 1, except that the composition of the Raney nickel catalyst for hydrogenation consisted of 87.2 wt% of nickel (Ni), 3.6 wt% of aluminium (Al), and 9.2 wt% of manganese (Mn). The process was repeated for 15 batches. The conversion was reduced from 90% to 30%. COMPARATIVE EXAMPLE 3: Hydrogenation was carried out in the same manner as that of Example 1, except that 60% of the Raney nickel catalyst for hydrogenation was of a granularity of less than 50 µm and the composition of the catalyst consisted of 92.7 wt% of nickel (Ni), and 7.3 wt% of aluminium (Al). The process was repeated for 10 batches. The conversion was reduced from 80% to 30%. COMPARATIVE EXAMPLE 4: Hydrogenation was carried out in the same manner as that of Example 1, except that an RCH55/10 catalyst manufactured by the Hoechst Company of Germany was used. The RCH55/10 catalyst consists of 55 wt% of nickel (Ni) based on diatomaceous earth. The process was repeated for 3 batches. The conversion was reduced from 80% to 20%. COMPARATIVE EXAMPLE 5: Hydrogenation was carried out in the same manner as that of Example 1, except that a Ni-1404P catalyst manufactured by the Harshaw company of USA was used. 100% of the Ni-1404P catalyst is of a granularity of less than 100 µm, the composition of which consists of 66 wt.% of nickel (Ni) based on SiO 2 -Al 2 O 3 . The process was repeated for 3 batches. The conversion was reduced from 85% to 35%. COMPARATIVE EXAMPLE 6: Hydrogenation was carried out in the same manner as that of Example 1, except that a 19A catalyst manufactured by the Johnson Matthey company of Britain was used. The 19A catalyst consists of 5 wt% of Ru based on active carbon. The process was carried out for just one batch and the conversion was only 16%. COMPARATIVE EXAMPLE 7 : Hydrogenation was carried out in the same manner as that of Example 1, except that an N-203SD catalyst manufactured by the Nikki company of Japan was used. The N-203SD catalyst consists of CuO and Cr 2 O 3 . The process was carried out for just one batch and the conversion was only 9%. COMPARATIVE EXAMPLE 8: Hydrogenation was carried out in the same manner as that of Example 1, except that a G-66D catalyst manufactured by the Girdler company of Japan was used. The G-66D catalyst consists of 33 wt% CuO and 65 wt% of ZnO. The process was carried out for just one batch and the conversion was 0%. COMPARATIVE EXAMPLE 9: Hydrogenation was carried out in the same manner as that of Example 1, except that a catalyst manufactured by the Engelhard company of Japan was used. The catalyst consists of 2 wt% of Pd based on Al 2 O 3 . The process was carried out for just one batch and the conversion was 0%. The results depicted in Examples 1-6 and Comparative Examples 1-9 are summarized in the table 1 below. (with slurry bed reactor) Composition of the Catalyst (wt%) Number of Batches Conversion % Example 1 Ni:Al:Fe:Cr=(85):(9.5):(2.5):(3) 50 95-98% Example 2 Ni:Al:Fe=(87.1):(9.9):(3) 50 93-98% Example 3 Ni:Al:Fe:Cr=(87.0):(9.9):(0.1):(3) 46 90-98% Example 4 Ni:Al:Fe:Mo=(92):(6.1):(0.7):(1.2) 45 90-98% Example 5 Ni:Al:Fe:Ti:W=(86):(9.5):(0.5):(2):(2) 40 90-98% Example 6 Ni:Al:Fe:Mn=(87):(11.6):(1.2):(0.2) 38 90-98% Comparative Example 1 Ni:Al:Mo=(92.7):(6.1):(1.2) 33 reduced from 90% to 70% Comparative Example 2 Ni:Al:Mn=(87.2):(3.6):(9.2) 15 reduced from 90% to 30% Comparative Example 3 Ni:Al:=(92.7):(7.3) 10 reduced from 80% to 30% Comparative Example 4 55 wt% of nickel (Ni) based on diatomaceous earth 3 reduced from 80% to 20% Comparative Example 5 66 wt% of nickel (Ni) based on SiO 2 -Al 2 O 3 3 reduced from 85% to 35% Comparative Example 6 5 wt% of Ru based on active carbon 1 16% Comparative Example 7 CuO and Cr 2 O 3 1 9% Comparative Example 8 33 wt% of CuO and 65 wt% of ZnO 1 0% Comparative Example 9 2 wt% of Pd based on Al 2 O 3 1 0% 2. Experiments with Fixed Bed Reactor EXAMPLE 7 0.781 g of carbonyl hydrotris (triphenyl phosphine) rhodium, 21.6 g of triphenyl phosphine, 55.4 g of allyl alcohol, and 73.6 g of toluene were charged to a pressure-resistant glass stirring reactor controlled at a temperature of 60°C and a pressure of 686 kPa (7 kg/cm 2 G)maintained by the supply of carbon monoxide and hydrogen with a molar ratio of 1 to carry out hydroformylation for 6.5 hours. Then the solution was extracted by deionized water to obtain a top layer of toluene solution containing hydroformylation catalyst and a bottom layer of aqueous solution containing 4-hydroxy-butanal, 2-hydroxytetrahydrofuran, and 2-methyl-3-hydroxypropanal. To prepare the hydrogenation catalyst, an alloy containing 40 wt% of nickel (Ni), 58 wt% of aluminium (Al), 0.5 wt% of iron (Fe), and 1.5 wt% of chromium (Cr) was melted at a temperature of 1650°C. After cooling, the thus-obtained alloy was granulated to a granularity of 3-10 mesh. 80 g of sodium hydroxide was then dissolved in 400 ml of water under stirring while the temperature was lowered to 50-60°C. After that, 60 g of the granulated alloy was added to the sodium hydroxide solution which was then heated to a temperature of 50 to 100°C. The solution was stirred for 30-120 minutes to disperse the alloy and then washed with pure water until the washings were of a pH in the range of 8 to 9. A Raney nickel catalyst for hydrogenation containing 57 wt% of nickel (Ni), 40.2 wt% of aluminium (Al), 0.7 wt% of iron (Fe), and 2.1 wt% of chromium (Cr) was thus obtained. A solution of 4-hydroxy-butanal, 2-hydroxytetrahydrofuran, and 2-methyl-3-hydroxypropanal was pumped with a flow rate of 1.5 ml/min into a tubular reactor having a inner diameter of 1 cm. Inside the tubular reactor was placed 30 ml of the Raney nickel catalyst for hydrogenation. The reactor was controlled at a temperature of 115°C and a pressure of 5880 kPa (60 kg/cm 2 G) maintained by the supply of hydrogen to carry out hydrogenation for one day. The thus-obtained solution was analyzed via gas chromatograph to obtain a result of 17.38 wt% of 1,4-butanediol, 1.98 wt% of 2-methyl-1,3-propanediol, and 80.64 wt% of other reactants and water. The reaction was then continued for a period of 20 days. The conversion was consistently maintained at about 96-100%. EXAMPLE 8: Hydrogenation was carried out in the same manner as that of Example 7 except that a Raney nickel catalyst for hydrogenation consisting of 50.4 wt% of nickel (Ni), 47 wt% of aluminium (Al), and 2.6 wt% of iron (Fe) was used. The reaction was carried out for 20 days. The conversion was consistently maintained at about 95-100%. EXAMPLE 9 : Hydrogenation was carried out in the same manner as that of Example 7 except that a Raney nickel catalyst for hydrogenation consisting of 53.5 wt% of nickel (Ni), 42.4 wt% of aluminium (Al), 0.1 wt% of iron (Fe), and 4.0 wt% of molybdenum (Mo) was used. The reaction was carried out for 20 days. The conversion was consistently maintained at about 94-100%. EXAMPLE 10: Hydrogenation was carried out in the same manner as that of Example 7 except that a Raney nickel catalyst for hydrogenation consisting of 47.5 wt% of nickel (Ni), 48 wt% of aluminium (Al), 0.5 wt% of iron (Fe), 3.0 wt% of manganese (Mn), and 1.0 wt% of cobalt (Co) was used. The reaction was carried out for 20 days. The conversion was consistently maintained at about 90-100%. COMPARATIVE EXAMPLE 10: Hydrogenation was carried out in the same manner as that of Example 7 except that a Raney nickel catalyst for hydrogenation consisting of 52 wt% of nickel (Ni) and 48 wt% of aluminium (Al) was used. After the reaction was carried out for 1.5 days, the conversion was reduced from 90% to 25%. COMPARATIVE EXAMPLE 11 : Hydrogenation was carried out in the same manner as that of Example 7 except that a Raney nickel catalyst for hydrogenation consisting of 48.7 wt% of nickel (Ni), 48.4 wt% of aluminium (Al), and 2.9 wt% of Cobalt (Co) was used. After the reaction was carried out for 1.5 days, the conversion was reduced from 60% to 20%. COMPARATIVE EXAMPLE 12 : Hydrogenation was carried out in the same manner as that of Example 7 except that a E-113T catalyst manufactured by the Mallinckrodt company of USA was used. The E-113T catalyst consists of 1/8" tablets of CuCr. After the reaction was carried out for 4 hours, the conversion was reduced from 10% to 0%. COMPARATIVE EXAMPLE 13 : Hydrogenation was carried out in the same manner as that of Example 7 7 except that a TYPE:50A catalyst manufactured by the Johnson Matthey company of Britain was used. The TYPE:50A catalyst consists of 0.5 wt% based on Al 2 O 3 . During the 4 hours of reaction, the conversion was 0% throughout. The results depicted in Examples 7-10 and Comparative Examples 10-13 are summarized in the table 2 below. (with fixed bed reactor) Composition of the Catalyst (wt%) Period of Reaction Conversion (%) Example 7 Ni:Al:Fe:Cr=(57):(40.2):(0.7):(2.1) 20 days 96-100% Example 8 Ni:Al:Fe=(50.4):(47):(2.6) 20 days 95-100% Example 9 Ni:Al:Fe:Mo=(53.5):(42.4):(0.1):(4) 20 days 94-100% Example 10 Ni:Al:Fe:Mn:Co=(47.5):(48):(0.5):(3):(1.0) 20 days 90-100% Comparative Example 10 Ni:Al=(52):(48) 1.5 days reduced from 90% to 25% Comparative Example 11 Ni:Al:Co=(48.7):(48.4):(2.9) 1.5 days reduced from 60% to 20% Comparative Example 12 CuCr 4 hours reduced from 10% to 0% Comparative Example 13 2 wt% of Pd based on Al 2 O 3 4 hours 0%

Claims: A process in which a modified Raney nickel catalyst, which comprises 40-98 wt% of nickel, 1-50 wt% of aluminium, and 0.05-15 wt% of iron, is used to catalyse the hydrogenation of hydroxy aldehydes and hydroxy cyclic ethers to form diols. The process according to claim 1, in which the modified Raney nickel catalysts further comprises 0.05-10 wt% of at least one metal from the group consisting of chromium, molybdenum, tungsten, cobalt, manganese, and titanium. The process according to claim 1 or claim 2, wherein the hydroxy aldehyde is 4-hydroxy-butanal or 2-methyl-3-hydroxy propanal whereby the diol is 1,4-butanediol or 2-methyl-1,3-propanediol. The process according to claim 1 or claim 2, wherein the hydroxy cyclic ether is 2-hydroxy-tetrahydrofuran. The process according to any preceding claim carried out at a temperature in the range of 50°C to 200°C, and a pressure in the range of 980 kPa (10 kg/cm 2 G) to 19600 kPa (200 kg/cm 2 G). The process according to claim 5 in which the temperature is in the range 75 to 150°C and the pressure is in the range 1960 kPa (20 kg/cm 2 G) to 7850 kPa (80 kg/cm 2 G). A process according to any preceding claim wherein the catalyst is of powder type and the reaction is carried out in a slurry bed reactor. A process according to any of claims 1 to 6 wherein the catalyst is of granule type and the reaction is carried out in a fixed bed reactor. A process according to claim 1 wherein the catalyst has been prepared by a method comprising mixing predetermined amounts of nickel, aluminium, iron and optionally other metals melting the mixture at a temperature of 1200 to 2000°C to produce a precursor alloy, cooling the alloy, crushing the alloy into powder or granules with a suitable size, developing in a solution of alkali metal hydroxide and washing with water to obtain the catalyst.

Inventors: CHEN SHIEN CHANG, CHOU JIUNN YANN, CHU CHENG CHANG, HUANG CHIAN CHONG, LIN FWU SHEN, CHEN, SHIEN CHANG, CHOU, JIUNN YANN, CHU, CHENG CHANG, HUANG, CHIAN CHONG, LIN, FWU SHEN
Applicants: DAIREN CHEMICAL CORP, DAIREN CHEMICAL CORPORATION
Application year: 1996
Main classification: B01J25
IPC codes: B01J25, C07C29