Semiconductor light emitting device and method for fabricating the same

Abstract: In a II-VI group semiconductor laser, on an n type GaAs substrate, n type ZnSe layer, a multiquantum well layer of a ZnCdSe well layer and a ZnSe barrier layer, and a p type ZnSe layer are deposited in this order. A polycrystalline ZnO layer is provided on both sides of the p type ZnSe layer for constricting current. Multifilm reflecting mirrors, respectively constituted with a polycrystalline SiO 2 layer and a polycrystalline TiO 2 layer, for obtaining laser oscillation are provided on, the p type ZnSe layer as well as on a surface of the n type ZnSe layer exposed by etching the GaAs substrate. Furthermore, a p type AuPd electrode and an n type AuGeNi electrode are respectively provided. Alternatively, on an n type GaAs substrate, an n type ZnSe epitaxial layer, an n type ZnMgSSe cladding layer, an n type ZnSSe optical waveguide layer, a ZnCdSe active layer, a p type ZnSSe optical waveguide layer, a p type ZnMgSSe cladding layer, a p type ZnTe contact layer and a polycrystalline ZnO burying layer are respectively formed. Furthermore, a p type AuPd electrode and an n type In electrode are respectively provided.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention: The present invention relates to a method for fabricating a semiconductor light emitting device comprising the step of forming a ZnO layer on a II-VI group semiconductor epitaxial layer. Furthermore, the present invention concerns a method for fabricating a vertical resonator type light emitting device comprising the step of forming a ZnO layer on an epitaxial layer made of a II-VI group semiconductor material. 2. Description of the Related Art: Since a ZnSe series II-VI group compound semiconductor is a direct transition type semiconductor material which has a wide band gap, the development a semiconductor laser which emits blue laser light (referred to as a "blue semiconductor laser", hereinafter) employing this material is actively being conducted recently. Figure 13 is a cross-sectional view illustrating an example of a structure for a conventional blue semiconductor laser 2500 using a ZnSe series II-VI group semiconductor material. Specifically, the structure includes a Cl-doped n type ZnSe epitaxial layer 2502 , a Cl-doped n type ZnMgSSe cladding layer 2503 , a Cl-doped n type ZnSSe optical waveguide layer 2504, a ZnCdSe active layer 2505, an N-doped p type ZnSSe optical waveguide layer 2506 , and an N-doped p type ZnMgSSe cladding layer 2507 , which are deposited in this order on an Si-doped n type GaAs substrate 2501 . The p type ZnMgSSe cladding layer 2507 is formed so that a portion thereof takes a stripe shape, and an N-doped p type ZnTe contact layer 2508 is formed on the stripe portion. On the other hand, on the portion of the p type ZnMgSSe cladding layer 2507 except the stripe portion is provided a polycrystalline SiO 2 burying layer 2509 so as to interpose the stripe portion therebetween. Furthermore, a p type AuPd electrode 2510 is provided on the p type ZnTe contact layer 2508 and the polycrystalline SiO 2 burying layer 2509 . On the other hand, an n type In electrode 2511 is provided under the n type GaAs substrate 2501 . A conventional blue semiconductor laser 2500 having a structure such as the one described above has the following problems to be solved. First, the polycrystalline SiO 2 burying layer 2509 used in the conventional blue semiconductor laser 2500 is formed by chemical vapor deposition or the like. However, the crystal growth temperature of a ZnSe series II-VI group compound semiconductor material is generally about 250°C, which is very low. Therefore, in order not to generate a crystal deterioration in the ZnSe series II-VI group compound semiconductor layer during the step of forming the polycrystalline SiO 2 burying layer 2509 which is conducted after the formation of a layer made of a ZnSe series II-VI group compound semiconductor material, the polycrystalline SiO 2 burying layer 2509 must be formed with a temperature lower than the growth temperature of the ZnSe series II-VI group compound semiconductor layer. However, SiO 2 formed with such low temperature becomes porous polycrystalline. As a result, the adhesion to a ZnSe layer or the like becomes extremely poor so that peeling or the like easily occurs. Therefore, it is questionable to use SiO 2 as an insulating burying layer. Moreover, even in a case where the polycrystalline SiO 2 burying layer 2509 is used as a mask during etching, side etch is likely to occur due to the poor adhesiveness or the porous property, and it is not a valuable mask material. Secondly, since the thermal conductivity of polycrystalline SiO 2 is considerably small, generated heat does not efficiently diffuse. As a result, the threshold value of the laser oscillation increases and the life of the light emitting device is shortened. Figure 14, on the other hand, is a cross-sectional view illustrating an example of a structure of a conventional vertical resonator type blue semiconductor laser 2600 using a ZnSe series II-VI group semiconductor material. Specifically, the structure includes a Cl-doped n type ZnSe epitaxial layer 2602 , a ZnCdSe active layer 2603 , an n-doped p type ZnSe epitaxial layer 2604, and a multi-film reflecting mirror 2605 comprising a set of polycrystalline SiO 2 layers and polycrystalline SiN layers, which are deposited in this order on an Si-doped n type GaAs substrate 2601 . An aperture of a predetermined shape is provided in the GaAs substrate 2601 . Another multi-layer reflecting mirror 2605 , which also comprises a set of polycrystalline SiO 2 layers and polycrystalline SiN layers, is provided on the n type ZnSe epitaxial layer 2602 exposed through the aperture. Laser oscillation occurring in such structure by optical excitation is disclosed in, for example, P. D. Floyd, J. K. Furdyna, H. Luo, J. L. Merz, Y. Yamada, and T. Yokogawa, Proc. Int. Workshop on ZnSe-Based Blue-Green Laser Structures, Wurzburg, Germany, September 18-23, 1994, p.77, Phys. Stat. Sol. (b) 187 (1995) 355. The oscillated laser light is emitted in the direction indicated by an arrow in Figure 26, through the aperture of the GaAs substrate 2601 used as the "window". A conventional blue semiconductor laser 2600 having a structure such as the one described above has the problem that it is difficult to form an electrode by a low temperature process on the n type GaAs substrate 2601 after a window from which laser light is to be emitted is formed in the GaAs substrate 2601. A method for fabricating a semiconductor light emitting device as acknowledged in the opening clause of claim 1 as well as a method for fabricating a vertical resonator type light emitting device as acknowledged in the opening clause of claim 2 are known from GB-A-1 382 401. Furthermore, EP-A 0 632 553 shows a surface emitting second harmonic generating device, in which II-VI compound semiconductors are used, interalia as the substrate, whereas alternating layers of SiO 2 are employed as a dielectric film forming a reflector. SUMMARY OF THE INVENTION It is the object of the invention to provide a method for fabricating a semiconductor light emitting device as acknowledged in the opening clause of claim 1 and a method for fabricating a vertical resonator type light emitting device as acknowledged in the opening clause of claim 2 in which plasmarized oxygen is used for improving the quality of the layers. This object is achieved by the features of claims 1 and 2 respectively. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a cross-sectional view of a blue semiconductor laser in accordance with a first embodiment of the present invention. Figure 2A through 2E are cross-sectional views illustrating fabricating steps of the blue semiconductor laser shown in Figure 1. Figure 3 is a cross-sectional view illustrating an apparatus for fabricating a ZnO layer in which plasmarized oxygen is utilized. Figure 4A is an isometric view illustrating a vertical resonator type blue semiconductor laser in accordance with a second embodiment of the present invention, Figure 4B is a cross-sectional view taken along line 13B-13B in Figure 4A, and Figure 4C is a view three-dimensionally illustrating the cross-sectional view shown in Figure 4B. Figures 5A through 5E are cross-sectional views illustrating fabricating steps of the blue semiconductor laser shown in Figures 4A through 4C. Figure 6 are graphs showing current vs. laser output characteristic and current vs. voltage characteristic of the blue semiconductor laser shown in Figures 4A through 4C. Figure 7 is a graph showing a spectrum obtained from the blue semiconductor laser shown in Figures 4A through 4C. Figure 8 is a graph showing a far-field pattern for the blue semiconductor laser shown in Figures 6A through 6C. Figure 9 is a graph showing the etching rate vs. acceleration voltage characteristic of the blue semiconductor laser shown in Figures 4A through 4C. Figure 10A is a cross-sectional view schematically illustrating a resultant configuration obtained by a dry-etching in accordance with the present invention using CH 4 and H 2 with introduced Ar, and Figure 10B is a cross-sectional view schematically illustrating a resultant configuration obtained by a conventional dry-etching technique using Cl 2 . Figure 11 is a graph illustrating changes in PL intensities before and after the dry-etching. Figure 12 is a graph illustrating reflectivity distribution of the multifilm reflecting film in the vertical resonator type blue semiconductor laser shown in Figures 4A through 4C. Figure 13 is a cross-sectional view illustrating a conventional blue semiconductor laser. Figure 14 is a cross-sectional view illustrating a conventional vertical resonator type blue semiconductor laser. DESCRIPTION OF THE PREFERRED EMBODIMENTS Example 1 A first embodiment of the present invention will be described with reference to the figures. Figure 1 is a cross-sectional view illustrating the structure of a blue semiconductor laser 100 using ZnSe series II-VI group semiconductor according to the first embodiment of the present invention. In the semiconductor laser 100 , a Cl-doped n type ZnSe epitaxial layer 1012 (0.03 µm thickness), a Cl-doped n type ZnMgSSe cladding layer 1013 (Zn 0.9 Mg 0.1 S 0.1 Se 0.9 , 1.0 µm thickness), a Cl-doped n type ZnSSe optical waveguide layer 1014 (ZnS 0.06 Se 0.94 , 0.12 µm thickness), a ZnCdSe active layer 1015 (Zn 0.8 Cd 0.2 Se, 0.006 µm thickness), and an N-doped p type ZnSSe optical waveguide layer 1016 (ZnS 0.06 Se 0.94 , 0.12 µm thickness) are deposited in this order on an Si-doped n type GaAs substrate 1011 . On the p type ZnSSe optical waveguide layer 1016 is formed a p type ZnMgSSe cladding layer 1017 such that a part thereof has a stripe shape, and an N-doped p type ZnTe contact layer 1018 is formed on the stripe portion. On the other hand, on the portion of the p type ZnMgSSe cladding layer 1017 except the stripe portion is provided a polycrystalline ZnO burying layer 1019 so as to interpose the stripe portion therebetween. Furthermore, a p type AuPd electrode 1110 is provided on the p type ZnTe contact layer 1018 and the polycrystalline ZnO burying layer 1019. An n type In electrode 1111 is provided, on the other hand, under the n type GaAs substrate 1011 . Among respective layers deposited as described above, the n type ZnSe epitaxial layer 1012 does not lattice-match with the GaAs substrate 1011 , but functions as a buffer layer between the GaAs substrate 1011 and the upper structure constituted of the II-VI group semiconductor materials. On the other hand, the n type ZnMgSSe cladding layer 1013 and the n type ZnSSe optical waveguide layer 1014, which are deposited on the n type ZnSe epitaxial layer 1012, lattice-match with the GaAs substrate 1011 . Moreover, the ZnCdSe active layer 1015 deposited on the n type ZnSSe optical waveguide layer 1014 does not lattice-match with the GaAs substrate 1011, but since its thickness is as thin as 0.006 µm, which is lower than the critical film thickness, dislocation due to lattice mismatch does not occur. As described above, in the semiconductor laser. 100 of the present embodiment, the burying layer 1019 made of polycrystalline ZnO is provided which has roles of current constriction and light confinement. Because of good thermal radiation of the ZnO, the reduction of the threshold current density and the long life of the device can be realized. Moreover, due to effective light confinement, single transverse mode laser oscillation can be obtained. Although the burying layer 1019 is constituted of the polycrystalline ZnO in the present embodiment, it can be constituted of monocrystalline ZnO to obtain a similar effect. Furthermore, ZnO is used as a material for the burying layer 1019 in the above description, polycrystalline ZnS can be used as a material for the burying layer 1019 . However, the polycrystalline ZnS has high water absorption and is likely to undergo degradation due to water absorption. Furthermore, since it is brittle in terms of material strength, its adhesiveness to ZnSe or the like is poor. Therefore, it cannot be said that it is a highly valuable material for an insulating burying layer or an etching mask. Contrary to this, as in the present embodiment described above, by constituting the burying layer 1019 using ZnO, the burying layer 1019 which has low water absorption rate and has excellent adhesiveness to II-VI group compound semiconductor materials can be obtained, and a semiconductor laser with a low threshold value can be realized. Next, an example of the production steps of the semiconductor laser 100 in the present embodiment will be described with reference to Figures 2A to 2E. In the production steps in the present embodiment to be described hereinafter, molecular beam epitaxy is used as a growth method of ZnSe series II-VI group semiconductor materials. First, as shown in Figure 2A , an n type GaAs substrate 1011 is prepared. Then, as shown in Figure 2B , a Cl-doped n type ZnSe epitaxial layer 1012 , a Cl-doped n type ZnMgSSE cladding layer 1013 , a Cl-doped n type ZnSSe optical waveguide layer 1014, a ZnCdSe active layer 1015 , an N-doped p type ZnSSe optical waveguide layer 1016, an N-doped p type ZnMgSSe cladding layer 1017 , and an N-doped p type ZeTe contact layer 1018 are successively epitaxially grown on the GaAs substrate 1011 . Next, a pattern for a resist 1112 of stripe shape is formed by photolithography on the grown layers, specifically on the p type ZnTe contact layer 1018 which is the uppermost layer. Then, by using the pattern as a mask, the grown layers are etched into a stripe shape. Specifically speaking, as shown in Figure 2C, regions of the N-doped p type ZnMgSSe cladding layer 1017 and the N-doped p type ZnTe contact layer 1018 which are not covered with the resist mask 1112 are etched using a saturated bromine solution. The etchant is a mixed solution of the ratio of saturated bromine solution : phosphoric acid : water = 1:2:3. Next, a ZnO layer 1019 is formed on the entire surface of the wafer by sputtering at a room temperature. After the formation of the ZnO layer 1019 , the resist layer 1112 and portion of the ZnO layer deposited on the resist layer 1112 are removed with lift-off by acetone (see Figure 2D). Thereafter, a p type AuPd electrode 1110 is formed over the entire upper surface of the wafer using vapor deposition as shown in Figure 2E . Furthermore, an n type In electrode 1111 is deposited on the lower surface of the GaAs substrate 1011 also by vapor deposition. This completes the formation of the semiconductor laser 100. In the above description, sputtering is used for the formation of the ZnO layer. In order to increase the deposit speed of the ZnO layer even when the process temperature is sufficiently low, it is effective to introduce oxygen in plasma form to the sputtering apparatus. Figure 3 is a schematic view of the apparatus 1300 to be used when the ZnO layer is formed using oxygen in plasma form. In the construction shown in Figure 3 , a II-VI group semiconductor material wafer 1331 is disposed on an electrode 1336 provided within a vacuum chamber 1330. Moreover, a ZnO target 1332 is disposed on another electrode 1337 so as to oppose to the wafer 1331. Furthermore, an argon gas supply tube 1333, oxygen gas supply tube 1334, and an exhaust system 1335 are provided to the vacuum chamber 1330. Specifically, while maintaining the ZnO target 1332 at negative voltage with respect to the wafer 1331, the discharge gas introduced in the vacuum chamber 1330 , for example the Ar gas, is depressurized to initiate the electrical discharge. The Ar ions are, thereby, accelerated toward and bombarded on the ZnO target 1332 which is being maintained at the negative voltage. The ZnO which is detached from the target 1332 due to this bombardment is deposited on the II-VI group semiconductor wafer (substrate) 1331 located nearby. In the construction of.the apparatus 1300 illustrated in Figure 3 , while the Ar gas is introduced into the vacuum chamber 1330 through the Ar gas supply tube 1333, oxygen is simultaneously introduced into the vacuum chamber 1330 through the oxygen gas supply tube 1334. The oxygen which becomes plasmarized due to the electrical discharges is taken into the ZnO film deposited on the II-VI group semiconductor substrate 1331 . This prevents the oxygen from being missed in the ZnO film to be deposited, thereby obtaining a high quality ZnO film. Furthermore, even at a low process temperature, the deposit rate is several times faster than in a depositing method of the conventional art. Example 2 A second embodiment of the present invention will be described with described with reference to the figures. Figures 4A, 4B, and 4C illustrate the structure of a vertical resonator type blue semiconductor laser 400 using a ZnSe series II-VI group semiconductor according to the present invention. Specifically, Figure 4A is an isomeric view illustrating the appearance of the semiconductor laser 400, Figure 4B is cross-sectional view taken along the line 4B-4B in Figure 4A, and Figure 4C expresses the cross-section shown in Figure 4B three-dimensionally. In the semiconductor laser 400, a Cl-doped n type ZnSe epitaxial layer (cladding layer) 4012, a multiquantum well layer 4013 which is constituted of ZnCdSe well layers and ZnSe barrier layers and functions as an active layer, and an N-doped p type ZnSe epitaxial layer (cladding layer) 4014 are deposited in this order on an Si-doped n type GaAs substrate 4011 . Disposed on both sides of the p type ZnSe epitaxial layer 4014 is a polycrystalline ZnO burying layer 4015 to constrict current. Multifilm reflecting mirrors 4017p and 4017n are formed on the p type ZnSe epitaxial layer 4014 and on the surface of the n type ZnSe layer 4012 exposed by etching a part of GaAs substrate 4011 , respectively, and they functions as reflecting mirrors for obtaining laser oscillation. Furthermore, a p type AuPd electrode 4016 is formed on the ZnO burying layer 4015 so as to cover the reflecting mirror 4017p, and on the other hand, an n type AuGeNi electrode 4018 is provided on the rear surface of the n type GaAs substrate 4011. In Figure 4A , the reflecting mirror 4017p is invisible as it is covered with the electrode 4016 . The reflecting mirror 4017n is also invisible in Figure 4A which is formed at the location corresponding to the bottom of an aperture (window) 4020 formed at the center of the GaAs substrate 4011. From Figure 4C, it can be seen that the reflecting mirror 4017p is cylindrical in shape. When voltage of 20 V is applied between the p type electrode 4016 and the n type electrode 4018 of this semiconductor laser 400, the current injected through the p type electrode 4016 does not flow through the portion of the ZnO burying layer 4015 . That is, the current is constricted and flows into the multiquantum well layer 4013 through the ring-shaped area between the ZnO burying layer 4015 and the reflecting mirror 4017p , thereby generating light. The generated light is reflected by the upper/lower reflecting mirrors 4017p and 4017n . The reflecting mirror 4017p has high reflectivity due to a large number of layers being deposited. Typically, the reflectivity of the reflecting mirror 4017p is 99%. On the other hand, the reflectivity of the reflecting mirror 4017n is typically 95%. Therefore, laser light is emitted from the side of the reflecting mirror 4017n, as illustrated by an arrow. Next, production steps of the semiconductor laser 400 will be described with reference to Figures 5A to 5E . Molecular beam epitaxy is used as a growth method of a ZnSe series II-VI group semiconductor material in the present embodiment. First, a Cl-doped n type ZnSe epitaxial layer 4012 , a multiquantum well layer 4013 constituted of ZnCdSe well layers and ZnSe barrier layers, and an N-doped p type ZnSe epitaxial layer 4014 are epitaxially grown in this order on an Si-doped n type GaAs substrate 4011 . In Figures 5A to 5E, however, boundaries among the GaAs substrate 4011 , the n type ZnSe epitaxial layer 4012, and the multiquantum well layer 4013 are not drawn for simplification. Next, processes for the upper surface side of the semiconductor laser 400 will be described as follows. A resist pattern 4019 of a cylindrical shape (16 µm diameter) is formed on the N-doped p type ZnSe epitaxial layer 4014 by photolithography. Then the N-doped p type ZnSe epitaxial layer 4014 is etched using the resist pattern 4019 as a mask. By doing so, as shown in Figure 5A, the thickness of a region of the p type ZnSe epitaxial layer 4014 which is covered with the resist pattern 4019 is maintained while the thickness of other regions thereof is reduced. Thereafter, a polycrystalline ZnO burying layer 4015 is deposited by sputtering on the region of the p type ZnSe epitaxial layer 4014 whose thickness has been reduced. Furthermore, by conducting lift-off, a polycrystalline ZnO burying structure for current constriction is produced as shown in Figure 5B. Next, a resist pattern to be a window (12 µm diameter) for forming a multifilm reflecting mirror 4017p is formed by photolithography, and the multifilm constituted of polycrystalline SiO 2 layers and polycrystalline TiO 2 layers is deposited thereon by sputtering. Lift-off is, then, conducted to form the multifilm reflecting mirror 4017p of a cylindrical shape of a diameter of 12 µm on the upper surface side of the semiconductor laser 400 as shown in Figure 5C. Next, a p type AuPd electrode 4016 is formed on the N-doped p type ZnSe epitaxial layer 4014 . Specifically, a Pd layer of 10 nm thickness is deposited over the entire surface of the p type ZnSe epitaxial layer 4014 , and an Au layer of 200 nm thickness is deposited thereon. By doing this, the p type electrode structure in which the AuPd electrode 4016 makes contact with the N-doped p type ZnSe epitaxial layer 4014 in the ring-shaped area can be produced. Next, processes on the rear surface side of the semiconductor laser 400 will be described. First, in order to facilitate the photolithographic process, the In sticking to the Si-doped n type GaAs substrate 4011 is removed by etching by using an HCl solution. Next, an alloy layer remaining on the exposed surface is removed by grinding, and the GaAs substrate 4011 is further etched until the thickness thereof becomes 140 µm using a mixed solution whose mixing ratio is H 2 SO 4 :H 2 O 2 :H 2 O = 1:8:1. Next, the GaAs substrate 4011 is further etched and a window of 30 µm diameter is opened to expose the n type ZnSe epitaxial layer 4012. This is the region where the multifilm reflecting mirror 4017n to be formed on the rear surface of the semiconductor laser 400 makes contact, and the process is conducted considering the fact that the GaAs substrate 4011 is not transparent to wavelengths of the color blue. Specifically, a resist pattern is formed by photolithography and, then, the GaAs substrate 4011 is etched by using a mixed solution as an etchant whose mixing ratio is NH 4 OH:H 2 O 2 :H 2 O = 3:66:20 to open a window of a desired shape and size. Since the etching rate of the above-mentioned etchant for GaAs is 20 times larger as that of the same etchant for ZnSe, the etching halts when all GaAs is etched off and the ZnSe is exposed. By doing this, an extremely flat ZnSe surface can be exposed. Furthermore, with the prescribed window 4020 provided in the GaAs substrate 4011 , the multifilm constituted of polycrystalline SiO 2 layers and polycrystalline TiO 2 layers is deposited, by sputtering, on the GaAs substrate 4011 as well as on the n type ZnSe epitaxial layer 4012 exposed at the bottom of the window 4020. Lift-off is then conducted and the multifilm reflecting mirror 4017 n (see Figures 4B and 4C ), which is to be an emitting window of laser light on the rear surface side of the semiconductor laser 400, is produced. The composition of the etchant which can be used in the present embodiment is not limited to the above described values. Specifically, provided that NH 4 OH is in the range of 2 to 5, H 2 O 2 is in the range of 30 to 70, and H 2 O is in the range of 10 to 40, the similar effect can be obtained. Furthermore, the area of the multifilm reflecting mirror 4017n is again covered with a resist pattern by photolithography and, then, an Ni film of 5 nm thickness, a Ge film of 20 nm thickness, an Au film of 30 nm thickness, a Ge film of 20 nm thickness, an Au film of 60 nm thickness, an Ni film of 40 nm thickness, and an Au film of 100 nm thickness are deposited thereon in this order. Lift-off is finally used to produce an n type AuGeNi electrode 4018. The heat treatment temperature then is typically 230°C. Although a multifilm of Ni/Ge/Au is used in the present embodiment for forming the n type AuGeNi electrode 4018 , if the thickness of the Ni film as the first layer is set in the range of 5 to 20 nm, then the direct deposition of an AuGe alloy thereon yield the similar effect. Figure 6 is a graph illustrating the current versus laser output characteristics and the current versus voltage characteristics of the vertical resonator type blue semiconductor laser 400 of the present embodiment. Specifically, it shows the measured results obtained during a pulsed operation at the liquid nitrogen temperature (77K). From the figure, the current value at which laser output rises, i.e., the threshold current is about 3 mA, and extremely small threshold current is being obtained. Figure 7 shows a spectrum of the emitted light from the vertical resonator type blue semiconductor laser 400 of the present embodiment. Specifically, it shows the measured results obtained during a pulsed operation at the liquid nitrogen temperature (77K). The solid line (a) represents a spectrum when the drive current takes the value which is twice the threshold current I th and the dotted line (b) is a spectrum when the drive current takes a value which is 0.9 times the threshold current I th . From the figure, it can be confirmed that in (b) where the drive current is below the threshold current, broad naturally-emitted light is observed but, in (a) where the drive current is above the threshold current, a sharply peaked spectral line is obtained, indicating that a laser oscillation is being obtained. The laser oscillation wavelength is 484 nm and the spectral line width of the laser oscillation line is 0.9 nm. Figure 8 shows a far-field pattern of the vertical resonator type blue semiconductor laser 400 of the present embodiment. Specifically, it shows the measured results obtained during a pulsed operation at the liquid nitrogen temperature (77K). From the figure, it can be seen that the radiation angle obtained is about 7°, which is an extremely narrow angle. The reason is as follows. The semiconductor laser 400 of the present embodiment has the p type electrode structure in which the AuPd electrode 4016 makes contact with the N-doped p type ZnSe epitaxial layer 4014 i n the ring-shaped area, and the polycrystalline ZnO burying structure further constricts the current into a cylindrical shape. Consequently, the current flows in cylindrical configuration from the AuPd electrode 4016 in a ring-shape and is injected into the multiquantum well layer 4013 which acts as the active layer. As a result, the laser beam to be emitted becomes round in shape. Since the diameter of the emitting facet is comparatively as large as 12 µm, an extremely small radiation angle can be obtained. In forming the semiconductor laser 400 of the present embodiment, when the N-doped p type ZnSe epitaxial layer 4014 is etched using the resist pattern 4019 of a cylindrical shape (16 µm diameter) as a mask, a mixed solution of'saturated bromine solution, phosphoric acid, and water (mixing ratio being, for example, 1:2:3) can possibly be used to conduct the wet etching instead of the aforementioned etchant. However, in a wet etching, there often arises surface roughness due to etching or the difficulty of obtaining a smoothly etched side wall. On the other hand, a dry etching using a hydrocarbon based gas is recently receiving much attention as a method of fine processing on compound semiconductors, and there have been several reports on a reactive ion etching on ZnSe using a hydrocarbon based gas for example, in Nikaido et al., The Extended abstracts of the Spring Convention of the Japanese Society of Applied Physics (1995), 30p-ZN-15, or in Ohtsuka et al., J. Appl. Phys. 75 (1994) 8231. Even with this dry etching using a hydrocarbon based gas, however, there are some problems such as a slow etching rate. In the present invention, however, an ECR etching which uses a mixed gas which combines Xe gas to CH 4 /H 2 based gas is conducted. Figure 9 is a graph illustrating an acceleration voltage dependence of the etching rate. Specifically, it illustrates data obtained during etching a ZnSe layer and a ZnMgSSe layer grown on a GaAs substrata by MBE with two different gases, one being a mixed gas of CH 4 gas and H 2 gas and another being this mixed gas further including Xe gas. From the graph, it can be seen that when Xe gas is added to discharge gas, the etching rate rapidly increases as the acceleration voltage increases in either case of ZnSe or ZnMgSSe. For example, for an accelerating voltage of 700 V, the etching rate becomes about 20 times greater than that without introducing Xe gas in either case of ZnSe or ZnMgSSe. The data shown in Figure 9 are obtained for the gas flow rate of CH 4 being 1 sccm, the gas flow rate of H 2 being 3 sccm, and the gas flow rate of Xe being 0.8 sccm. However, specific values are not limited thereto, and if a condition that the ratio of the flow rate of the Xe to the flow rate of the CH 4 (Xe/CH 4 ) is more than 0.5 and lees than 1.5 (i.e., 0.5<Xe/CH 4 <1.5) is satisfied, carbon compound formed on the etching surface can effectively be removed due to the action of the Xe gas, and the etching characteristics such as the one described above can possibly be obtained. Figure 10A is a cross-sectional view schematically illustrating the etched shape obtained by a dry etching which uses methane and hydrogen added with Xe gas in accordance with the present embodiment, and Figure 9B is a cross-sectional view schematically illustrating an etched shape obtained by a dry etching which uses chlorine in accordance with the conventional art. According to the method of the present embodiment, as shown in Figure 10A, the etched surface obtained is extremely flat, while the etched surface is roughened in the conventional technique as shown in Figure 10B. In particular, in the vertical direction, a smooth etched side wall with an etching angle of about 80° can be obtained. The side wall having excellent verticality such as this is advantageous in realizing effective current constriction. If the side wall is not formed vertically but has a cross-section of a trapezoidal shape with a spreading base, the current is not sufficiently constricted but spreads, and the current does not concentrate in the active layer. However, by introducing the Xe gas and conducting the dry etching as in the present embodiment, an etched side wall with excellent verticality is formed and a structure suitable for current constriction is obtained. Figure 11 is a graph illustrating changes in PL intensities measured as grown (before etching), as dry-etched, and as wet-etched after the dry-etching is completed, respectively, for both a dry etching using methane and hydrogen added with Xe gas in accordance with the present embodiment and a dry etching using chlorine in accordance with the conventional art. In the dry etching using chlorine in accordance with the conventional art, the PL intensity rapidly decreases after the implementation of the dry etching. On the other hand, in the dry etching by methane and hydrogen added with Xe gas of the present embodiment, the decrease in the PL intensity is hardly observed even after the implementation of the dry etching. This means that damage inflicted upon the to-be-processed surface by the etching is extremely small in the dry etching by methane and hydrogen added with the Xe gas of the present embodiment. Although, in the above description, etching characteristics toward ZnSe and ZnMgSSe are described, the equivalent etching rats can be realized and a similarly smoothly etched surface can also be obtained for ZnSSe or CdZnSe. The polycrystalline ZnO burying layer 4015 is used for current constriction as described above. This is for the reasons to be described below. In a III-V group compound semiconductor laser such as GaAs, a polycrystalline SiO 2 burying layer is conventionally used. This polycrystalline SiO 2 burying layer is typically formed by chemical vapor deposition or the like. However, the crystal growth temperature of a ZnSe series II-VI group compound semiconductor material is generally about 250°C, which is very low. Therefore, in order not to generate crystal deterioration in the ZnSe series II-VI group compound semiconductor layer during the step of forming the polycrystalline SiO 2 burying layer which is conducted after the formation of a layer made of a ZnSe series II-VI group compound semiconductor material, the polycrystalline SiO 2 burying layer must be formed with a temperature lower than the growth temperature of the ZnSe series II-VI group compound semiconductor layer. However, SiO 2 formed with such low temperature becomes a porous polycrystalline. As a result, the adhesion to a ZnSe layer or the like becomes extremely poor so that a peel or the like easily occurs. Therefore, it is questionable to use SiO 2 as an insulating burying layer. Moreover, also in a case where the polycrystalline SiO 2 burying layer is used as a mask during etching, side etch or the like is likely to occur due to its poor adhesion or porous property, and it is not a valuable mask material. Furthermore, since the thermal conductivity of polycrystalline SiO 2 is considerably small, generated heat does not efficiently diffuse. As a result, the threshold value for laser oscillation increases and the life of the light emitting device is shortened. Therefore, in the present embodiment, the burying layer 4015 is formed by using polycrystalline ZnO as a material which can be formed with good adhesion on the epitaxial layer in the II-VI group semiconductor laser structure, has high thermal conductivity, and has small refractive index so that it can possibly be used for light confinement. The ZnO layer used as a material for the insulating burying layer in the present invention is one of II-VI group compound semiconductor materials, and has extremely excellent adhesiveness for materials such as ZnSe, ZnSSe, and ZnMgSSe. It also has excellent anti-acid and anti-oxidation properties. Furthermore, it has almost zero water absorption property and excels in the stability of shape and dimensions. Moreover, ZnO has extremely a good thermal conductive property and its thermal conductivity is almost 30 times that of SiO 2 . Therefore, by using ZnO as the insulating burying layer, heat generated in the active layer efficiently diffuses through the ZnO insulating burying layer. Furthermore, ZnO has a smaller refractive index compared with ZnSe, ZnSSe, ZnMgSSe, etc., and the difference therebetween is in the preferable range. Specifically, the refractive index of the cladding layer is typically about 2.5 to 2.6, while that of the ZnO layer constituting the insulating burying layer is typically about 2.2. When a difference of refractive index between the cladding layer and the insulating burying layer is in such a range, a stable single transverse mode laser oscillation is achieved even with a cladding layer having a cylindrical portion with an enlarged diameter as large as 5 to 10 µm. Contrary to the above, the conventional SiO 2 insulating burying layer typically has a refractive index of about 1.4, resulting in a large difference with respect to the refractive index of the cladding layer. As a result, in order to achieve a stable single transverse mode laser oscillation, the diameter of the cylindrical portion in the cladding layer has to be reduced to about 2 µm. it is, however, difficult to fabricate the cylindrical portion with such a small diameter. Thus, the ZnO insulating burying layer effectively functions as a light confinement layer in the lateral direction. In the above description, sputtering is used for forming the polycrystalline ZnO burying layer 4015 and the multifilm reflecting mirrors 4017p and 4017n constituted of polycrystalline SiO 2 layers and polycrystalline TiO 2 layers. However, in order to increase the depositing rates of these layers even in a case where the process temperature is sufficiently low, it is effective to introduce oxygen in plasma form to the sputtering apparatus as described in conjunction with the first embodiment with Figure 3 being referred to. The oxygen which turns into plasma by the electrical discharge is taken into a film such as ZnO deposited on the II-VI group semiconductor substrate. This can prevent the oxygen in the deposited film from dropping out, and a good quality film can be obtained. Furthermore, even in a low process temperature, the depositing rate of the film such as ZnO increases several times than of the depositing method of the conventional art. Particularly in the TiO 2 film, when oxygen drops out from a film during the sputtering step, the absorption edge shifts toward the longer wavelength side. As a result, the absorption loss with respect to wavelengths of blue laser light increases, which then introduces the decrease in the reflectivity of the multifilm reflecting mirrors 4017p and 4017n. On the other hand, by introducing oxygen into the sputtering step, the drop out of the oxygen can be suppressed. As a result, the reflectivity of the multifilm reflecting mirrors 4017p and 4017n constituted of the polycrystalline SiO 2 layers and the polycrystalline TiO 2 layers can be raised. For example, in the present embodiment, in the multifilm structure made of polycrystalline SiO 2 layers and polycrystalline TiO 2 layers deposited with the periodicity of the total of eight, a reflectivity higher than 99% for a 490 nm wavelength can be obtained. Figure 12 is a graph illustrating the reflectivity distribution over wavelengths of the multilayer reflecting film formed in accordance with the present embodiment. From this result, it can be said that the multifilm reflecting mirrors 4017p and 4017n which have good controllability on the film thickness, from which the drop-out of oxygen is suppressed, and which has large reflectivity, is obtained from the multifilm constituted of polycrystalline SiO 2 layers and polycrystalline TiO 2 layers according to the present embodiment. Therefore, the multifilm reflecting mirrors 4017p and 4017n which are formed in accordance with the present embodiment are considerably effective as the reflecting mirrors for a vertical resonator type semiconductor laser which must have an extremely large reflectivity. As described above, the n type AuGeNi electrode 4018 is used in the present embodiment for the reasons below. In order to facilitate the photolithographic process toward the rear surface of the semiconductor laser, In sticking to the Si-doped n type GaAs substrate 4011 is removed and then the etching is conducted. That is, in order to conduct the above process, a new n type electrode must be fabricated because the In used for an attachment purpose during crystal growth cannot be used directly as the n type electrode. Since a ZnSe series II-VI group semiconductor generally grows at a low temperature which is lower than 300°C, it is necessary to form an ohmic contact at a process temperature (sinter temperature) as low as possible. For that purpose, it is effective to form the electrode 4018 from n type AuGeNi. Table 1 lists the heat treatment temperatures required for the forming process (i.e., process temperature) and the contact resistances obtained thereby for a variety of metal materials which can be used as the constituting material of the electrode. From the table, when the multilayer structure of AuGeNi is used, an excellent ohmic contact is obtained by the heat treatment at 230°C for five minutes, and the contact resistance is then about 5 × 10 -3 Ω·cm 2 . Material InSn AuSn AuGeNi AuGe Process temperature (°C) 275 245 230 275 Contact resistance (Ω·cm 2 ) 1.84×10 -2 4.15×10 -2 5.00×10 -3 8.18×10 -3

Claims: A method for fabricating a semiconductor light emitting device (100) comprising the step of forming a ZnO layer (1019) on a II-VI group semiconductor epitaxial layer (1018), characterized in that said ZnO layer (1019)is formed by using plasmarized oxygen (O 2 ) and by sputtering a ZnO target (1332) in a sputtering apparatus into which a discharge gas and oxygen (O 2 ) are introduced simultaneously. A method for fabricating a vertical resonator type light emitting device (400) comprising the step of forming a ZnO layer (4015) on an epitaxial layer (4014) made of a II-VI group semiconductor material characterized in that said ZnO layer (4015) is formed by using plasmarized oxygen (O 2 ) and by sputtering a ZnO target (1332) in a sputtering apparatus into which a discharge gas and oxygen (O 2 ) are introduced simultaneously.

Inventors: SASAI YOICHI, YOKOGAWA TOSHIYA, YOSHII SHIGEO, SASAI, YOICHI, YOKOGAWA, TOSHIYA, YOSHII, SHIGEO
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1996
Main classification: H01S5
IPC codes: H01S5, H01L33