Catalyst and alkyne hydrogenation process

Abstract: C 2 -C 6 alkynes (preferably acetylene) contained in feeds which also contain sulfur impurities are hydrogenated to the corresponding alkenes in the presence of a supported palladium catalyst which has been promoted with alkali metal fluoride (preferably potassium fluoride).

Description: Background of the Invention This invention relates to a catalyst and to a process for catalytically hydrogenating alkyne-containing feeds which also comprise sulfur impurities. The selective hydrogenation of alkynes, which generally are present in small amounts in alkene-containing streams (e.g., acetylene contained in ethylene streams from thermal ethane crackers), is commercially carried out in the presence of alumina-supported palladium catalysts. In the case of the selective hydrogenation of acetylene to ethylene, preferably an alumina-supported palladium/silver catalyst in accordance with the disclosure in U.S. Patent 4,404,124 and its division, U.S. Patent 4,484,015 is used. The operating temperature for this hydrogenation process is selected such that essentially all acetylene is hydrogenated to ethylene (and thus removed from the feed stream) while only an insignificant amount of ethylene is hydrogenated to ethane (to minimize ethylene losses and to avoid a "runaway" reaction which is difficult to control, as has been pointed out in the above-identified patents). It is generally known by those skilled in the art that sulfur impurities (such as H 2 S, COS, mercaptans and organic sulfides) when present in alkyne-containing feeds can poison and deactivate these palladium-containing catalysts. The present invention is directed to the use of an improved palladium catalyst in the selective hydrogenation alkynes to alkene, in particular of acetylene to ethylene, in the presence of sulfur-containing impurities. EP-A-0 693 315 and EP-A-0 689 872 which both are prior art under Articles 54(3) and (4) EPC for certain designated contracting states, disclose supported hydrogenation catalysts containing palladium and silver. The catalyst of EP-A-0 693 315 further comprises alkali metal fluoride and is used in the selective hydrogenation of C 4 -C 10 diolefins with hydrogen gas to the corresponding C 4 -C 10 monoolefins. The catalyst of EP-A-0 689 872 is used in the selective hydrogenation of acetylene to ethylene. Summary of the Invention It is an object of this invention to carry out the selective hydrogenation of C 2 -C 6 alkyne(s) to the corresponding alkene(s) in the presence of sulfur impurities employing an improved palladium-containing catalyst. It is a particular object of this invention to carry out the selective hydrogenation of acetylene to ethylene in the presence of sulfur compounds. Other objects and advantages will be apparent from the detailed description and appended claims. In accordance with this invention, a catalyst as defined in claim 1, and a process as defined in claim 7, for selectively hydrogenating at least one alkyne containing 2-6 carbon atoms per molecule are provided. Preferred embodiments of the invention are defined in the dependent claims. Preferably, the catalyst used in the process also comprises silver. The presently preferred alkali metal fluoride is potassium fluoride. Preferably, the at least one alkyne is acetylene (ethyne) and the at least one alkene is ethylene (ethene). Detailed Description of the Invention The catalyst which is employed in the selective hydrogenation process of this invention is a supported palladium catalyst composition as defined in claim 7, which also comprises at least one alkali metal fluoride, preferably potassium fluoride. Preferably, silver is also present in the catalyst composition. This catalyst composition can be fresh or it can be a used and thereafter oxidatively regenerated catalyst composition. This catalyst contains an inorganic support material selected from the group consisting of alumina, titania, zirconia, and mixtures thereof. The presently more preferred support material is alumina, most preferably alpha-alumina. This catalyst generally contains 0.01-1 (preferably 0.01-0.2) weight-% palladium and 0.05-1.5 (preferably 0.1-0.4) weight-% fluorine (chemically bound as alkali metal fluoride), preferably at a F:Pd weight ratio of 3:1 to 30:1. Preferably, 0.01-10 (more preferably 0.02-2) weight-% silver is also present in the catalyst. Preferably, the Ag:Pd weight ratio in the catalyst is 2:1 to 10:1. Particles of this catalyst generally have a size of 1-10 mm (preferably 2-6 mm) and can have any suitable shape (preferably spherical or cylindrical). Generally, the surface area of this catalyst (determined by the BET method employing N 2 ) is 1-100 m 2 /g. The above-described catalyst which is employed in the hydrogenation process of this invention can be prepared by any suitable, effective method. The alkali metal fluoride can be incorporated (e.g., by impregnation or spraying) into the support material before it is impregnated with a suitable Pd compound, and preferably also with a suitable Ag compound. Or the alkali metal fluoride can be incorporated (e.g., by impregnation or spraying) into the catalyst simultaneously with or after the impregnation with a suitable Pd compound. When silver is also present in the catalyst composition, the alkali metal compound can be incorporated between the Pd and Ag impregnation steps or after the impregnation with Pd and Ag compounds. The presently preferred catalyst preparation comprises the impregnation of a Pd/Ag/Al 2 O 3 catalyst material (more preferably the "skin" catalyst obtained by the method described in U.S. Patents 4,404,124 and 4,484,015) with an aqueous solution of potassium fluoride (KF), followed by drying and calcining (preferably in air at a temperature of 300-450°C, more preferably 350-400°C, generally for 1-10 hours). If a "wet reducing" step is applied, this means treatment with dissolved reducing agents such as hydrazine, alkali metal borohydrides, aldehydes such as formaldehyde, carboxylic acids such as forming acid or ascorbic acid, reducing sugars such as dextrose, and the like. The thus-prepared catalyst composition which has been dried (and preferably also calcined, as described above) can then be employed in the process of this invention for hydrogenating at least one C 2 -C 6 alkyne, preferably acetylene, to at least one corresponding alkene in the presence of at least one sulfur compound. Optionally, the catalyst is first contacted, prior to the alkyne hydrogenation, with hydrogen gas or with gaseous hydrocarbon generally at a temperature in the range of 30°C to 100°C, for a time period of 4 to 20 hours. During this contacting with H 2 or hydrocarbon(s) before the selective alkyne hydrogenation commences, palladium and silver compounds (primarily oxides) which may be present in the catalyst composition after the drying step and the optional calcining step (described above) are substantially reduced to palladium and silver metal. When this optional reducing step is not carried out, the hydrogen gas present in the reaction mixture accomplishes this reduction of oxides of Pd and Ag during the initial phase of the alkyne hydrogenation reaction of this invention. The selective hydrogenation process of this invention is carried out by contacting (a) a feed gas which comprises at least one C 2 -C 6 alkyne (preferably a C 2 -C 6 alkene stream containing said at least one alkyne as an impurity, generally at a level of 1 ppm by weight to 50,000 ppm by weight alkyne) and at least one sulfur compound and (b) hydrogen gas with (c) the catalyst composition which comprises Pd, Ag, at least one alkali metal fluoride and an inorganic support material. Preferred feed alkynes include acetylene, propyne, butyne-1, butyne-2 and mixtures thereof. Particularly preferred is acetylene. These alkynes are primarily hydrogenated to the corresponding alkenes, i.e., acetylene is primarily hydrogenated to ethylene, propyne is primarily hydrogenated to propylene, and the butynes are primarily hydrogenated to the corresponding butenes (butene-1, butene-2). In order to best attain substantially complete removal of the alkyne(s), there should be at least one mole of hydrogen for each mole of alkyne present. Gases (a) and (b) are generally premixed before their contact with the catalyst composition (c). Suitable sulfur compounds which are present in the feed include (but are not limited to) hydrogen sulfide, carbonyl sulfide (COS), mercaptans (RSH), organic sulfides (R-S-R), organic disulfides (R-S-S-R) and the like, and mixtures thereof, wherein each R can be an alkyl or cycloalkyl or aryl group containing 1-10 carbon atoms. It is within the scope of this invention to have additional compounds (such as methane, ethane, propane, butane, carbon monoxide, water, alcohols, ethers, ketones, carboxylic acids, esters and other oxygenated compounds) present in the feed gas, as long as they do not significantly interfere with the selective hydrogenation of alkyne(s) to alkene(s). Generally, the sulfur compounds are present in the feed gas in trace amounts, preferably at a level of less than 1 weight percent sulfur, and preferably at a level of 1-1,000 ppm by weight sulfur (i.e., 1-1,000 parts by weight S per million parts by weight feed). The temperature necessary for the selective hydrogenation of alkyne(s) to alkene(s) depends largely upon the activity and selectivity of the catalysts, the amounts of sulfur impurities in the feed, and the desired extent of alkyne removal. Generally, a reaction temperature in the range of 40°C to 200°C is employed. Preferably, the reaction temperature is 60-150°C. Any suitable reaction pressure can be employed. Generally, the total pressure is in the range of 0.79 to 7.0 MPa (100 to 1,000 pounds per square inch gauge (psig)). The gas hourly space velocity (GHSV) of the hydrocarbon feed gas can also vary over a wide range. Typically, the space velocity will be in the range of 1,000 to 10,000 m 3 of feed per m 3 of catalyst per hour, more preferably 2,000 to 8,000 m 3 /m 3 /hour. The GHSV of the hydrogen gas stream is chosen so as to provide a molar ratio of H 2 to said at least an alkyne in the range of 0.5:1 to 100:1, preferably 1:1 to 50:1. Regeneration of the catalyst composition can be accomplished by heating the catalyst composition in air (at a temperature which preferably does not exceed 700°C) so as to burn off any sulfur compounds, organic matter and/or char that may have accumulated on the catalyst composition. Optionally, the oxidatively regenerated composition is reduced with H 2 or a suitable hydrocarbon (as has been described above) before its redeployment in the selective alkyne hydrogenation of this invention. The following examples are presented to further illustrate this invention and are not to be construed as unduly limiting its scope. Example I This example illustrates the preparation of supported, potassium-promoted palladium catalysts (to be used for acetylene hydrogenation). Catalyst A (Control) was a commercial Pd/Ag/Al 2 O 3 catalyst which contained 0.023 weight-% Pd, 0.065 weight-% Ag and about 99 weight-% alumina. It had a BET/N 2 surface area of 3-5 m 2 /g, and had been prepared substantially in accordance with the method described in U.S. Patent 4,404,124 (column 4, lines 32-45). Catalyst A had been provided by United Catalysts Inc. (UCI), Louisville, KY, under the product designation of "G-83C". Catalyst B (Control) was prepared by soaking 70.8 grams of Catalyst A in a solution of 0.51 gram KOH in 21.9 grams of distilled water for 1 hour. The thus-impregnated catalyst material was dried for 3 hours at 82°C and then calcined in air for 3 hours at 370°C. Catalyst C (Invention) was prepared by soaking 70.9 grams of Catalyst A in 100 cm 3 of an aqueous solution containing 10.0 grams KF (potassium fluoride) for 1.5 hours. The thus-impregnated catalyst material washed three times with distilled water, soaked in distilled water overnight, and dried at 82°C for 2 hours. Thereafter, the catalyst material was soaked again with an aqueous solution containing 0.53 gram KF in 21.5 grams of water for 1.5 hours. The twice-impregnated catalyst material was dried at 82°C and then calcined in air at 370°C for 3 hours. Catalyst D (Control) was prepared by impregnating 23.1 grams of a Pd/Al 2 O 3 catalyst (containing about 0.02 weight-% Pd, no Ag; provided by UCI under the product designation of "G-83A") with a solution of 0.157 gram KOH in 7.06 grams of distilled water, followed by drying at 82°C for several hours and calcining in air at 370°C for 2 hours. Catalyst D contained 0.5 weight-% K. Catalyst E (Invention) was prepared soaking 23.1 grams of "G-83" (Pd/Al 2 O 3 ) in a solution of 4.33 grams of KF in 100 cm 3 H 2 O for 3 hours. The supernatant KF solution was decanted, and the KF-treated catalyst material was rinsed several times with distilled water and soaked in 300 cm 3 distilled water overnight, followed by drying at 82°C for several hours. Thereafter, the catalyst material was impregnated again with an aqueous KF solution containing 0.17 grams KF and 7.1 grams of H 2 O. The twice impregnated catalyst material was dried at 82°C for several hours and calcined in air at 340°C for several hours. Catalyst E contained 0.5 weight-% K. Example II This example illustrates the poisoning effect of hydrogen sulfide on the performance of two acetylene hydrogenation catalysts (Catalysts B and C). The selective acetylene hydrogenation tests were carried out as follows. About 20 cm 3 of Catalyst B or Catalyst C was placed into a stainless steel reactor tube having a 12.7 mm (0.5 inch) inner diameter and a length of about 0.46 m (18 inches). Each catalyst was treated with flowing hydrogen gas under a pressure of 1.48 MPa (200 psig), at a temperature of about 54.4 to 65.6 °C (130-150°F), for about 16 hours. Thereafter, the reactor tube was cooled to about 48.9°C (120°F), and a hydrocarbon-containing feed gas containing 27.1 weight-% methane, 15.9 weight-% ethane, 55.3 weight-% ethylene, and 0.30 weight-% acetylene and 1.35 weight-% hydrogen was introduced into the reactor tube at a rate of about 900 cm 3 /minute. The reactor temperature was gradually increased to the desired reaction temperature, and samples of the formed product were analyzed by means of a gas chromatograph at various time intervals. In order to evaluate the effect of hydrogen sulfide on the two catalysts, nitrogen gas containing about 1 volume-% H 2 S was passed over 20 cm 3 of each catalyst placed in the above-described reactor tube, at a flow rate of about 100 cm 3 /minute. The temperature was about 23°C (73°F)and the pressure was 1 atm. After H 2 S breakthrough was detected (by means of an aqueous CdSO 4 solution which formed yellow CdS precipitate), the flow of the N 2 /H 2 S gas was stopped. In the case of Catalyst B, H 2 S breakthrough was detected after about 650 cm 3 of the N 2 /H 2 S gas had passed through the reactor, whereas in the case of Catalyst C, H 2 S breakthrough occurred after about 350 cm 3 of the N 2 /H 2 S gas had flowed through the reactor. The reactor tube was then purged for about 20 hours with flowing hydrogen gas (flow rate: about 100 cm 3 /minute) at a temperature of about 93.3°C (200°F) and a pressure of about 0.45 MPa (50 psig). Thereafter, the selective acetylene hydrogenation test (using the above-described hydrocarbon feed gas and the above-described test procedure) was started for each of the H 2 S-poisoned catalysts. Pertinent test results are summarized in Table I. Test results in Table I clearly show that the H 2 S-poisoned Catalyst B (KOH-promoted Pd/Ag/Al 2 O 3 ) was essentially useless as a selective acetylene hydrogenation catalyst because even at temperatures above 149°C (300°F), all acetylene had not been completely hydrogenated, while a substantial amount of ethylene had been hydrogenated to ethane (as indicated by a significantly decreased ethylene/ethane ratio). In the case of H 2 S-poisoned Catalyst C (KF-promoted Pd/Ag/Al 2 O 3 ), however, essentially complete acetylene hydrogenation had occurred at about 129°C (264°F), while the undesirable hydrogenation of ethylene to ethane occurred only to an insignificant extent; as evidenced by an ethylene/ethane ratio which had decreased only about 2% from the initial value of 3.72. Even at a relatively high temperature of 231°C (447°F), this ratio had decreased only about 5%. This above-outlined difference between H 2 S-poisoned Catalysts B and C is truly unexpected in view of the fact that the performance of the unpoisoned Catalysts B and C was substantially the same (as indicated by essentially the same "cleanup" temperature at which complete acetylene hydrogenation was achieved and essentially the same "runaway" temperature at which the ethylene/ethane ratio had decreased about 10% from its initial value). Example III This example illustrates the poisoning effect of an organic disulfide on the performance of two K-promoted Pd/Ag/Al 2 O 3 catalysts (Catalysts B and C, described in Example I in acetylene hydrogenation). First, unpoisoned Catalysts B and C were employed in separate acetylene hydrogenation tests, essentially in accordance with the procedure and employing the hydrocarbon feed described in Example II. Then about 2.1 liters of nitrogen stream which had been passed through a bubbler containing liquid dimethyl disulfide (DMDS) was passed at a rate of about 75 cm 3 /minute over Catalyst B and Catalyst C, respectively, at a temperature of 69.4°C (157°F). Thereafter, the reactor tube containing Catalyst B or C was purged overnight with hydrogen gas at a rate of about 100 cm 3 /minute, at a pressure of about 0.45 MPa (50 psig) and a temperature of about 68.3°C (155 °F). The acetylene hydrogenation test (in accordance with the procedure described in Example I) was then carried with the DMDS-poisoned catalysts. Pertinent test results are summarized in Table II. Test data in Table II demonstrate that Catalyst C (KF promoted Pd/Ag/Al 2 O 3 ) which had been exposed to (poisoned by) dimethyl disulfide (DMDS) performed significantly better as a selective acetylene hydrogenation catalyst than DMDS-poisoned Catalyst B (KOH-promoted Pd/Ag/Al 2 O 3 ), as indicated by the differences in cleanup temperature (98.3°C (209°F) for DMDS-poisoned Catalyst C versus 146°C (295°F) for DMDS-poisoned Catalyst B) and the ethylene/ethane ratio at the cleanup temperature (3.66 for DMDS-poisoned Catalyst C versus less than 3.57 for DMDS-poisoned Catalyst B). Example IV This example illustrates the poisoning effect of H 2 S on the performance of two K-promoted Pd/Al 2 O 3 catalysts (without Ag; Catalysts D and E, described in Example I). The tests were carried out substantially in accordance with the procedure described in Example II. About 900 cm 3 of the N 2 /H 2 S gas mixture containing 1 volume-% H 2 S was passed over Catalyst D and E, respectively. Test results are summarized in Table III. Test data in Table III demonstrate that the H 2 S-poisoned Catalyst D (KOH-promoted Pd/Al 2 O 3 ) had become ineffective in catalyzing the complete hydrogenation of acetylene (at temperatures of 137°C (278°F) and above), whereas in the case of H 2 S-poisoned Catalyst E (KF-promoted Pd/Al 2 O 3 ), complete selective acetylene hydrogenation to ethylene with relatively little hydrogenation of ethylene to ethane (as evidenced by a relatively high ethylene/ethane ratio) was accomplished at about 93.3°C (200°F). These test results (obtained with K-promoted Pd/Al 2 O 3 catalysts) confirm the results obtained in Example II with K-promoted Pd/Ag/Al 2 O 3 catalysts.

Claims: Claims for the following Contracting States: BE, DE, ES, FR, GB, IT, NL A catalyst, comprising palladium, at least one alkali metal fluoride on an inorganic support material selected from alumina, titania, zirconia, and mixtures thereof, with the proviso that the catalyst does not comprise a silver-containing material selected from silver metal and silver compounds. The catalyst according to claim 1, consisting of said palladium, and said at least one alkali metal fluoride on said inorganic support material. The catalyst according to claim 1 or 2, comprising 0.01 - 1 weight-% palladium, and 0.05 - 1.5 weight-% fluorine. The catalyst according to any of claims 1 to 3, wherein the weight ratio of fluorine to palladium is 3:1 to 30:1. The catalyst according to any of the preceding claims, having a particle size of 1 - 10 mm, and BET/N 2 surface area of 1 - 100 m 2 /g. The catalyst according to any of the preceding claims, wherein said inorganic support material is alumina. A process for selectively hydrogenating at least one alkyne containing 2 - 6 carbon atoms per molecule, which is present in a feed also comprising at least one sulfur compound, with hydrogen gas to at least one corresponding alkene containing 2 - 6 carbon atoms per molecule comprising contacting said feed and said hydrogen gas with a catalyst comprising palladium, at least one alkali metal fluoride on an inorganic support material selected from alumina, titania, zirconia, and mixtures thereof, with the proviso that the catalyst has not been contacted with a liquid composition comprising at least one effective reducing agent at a temperature of up to 60°C. The process according to claim 7, wherein the catalyst has a particle size of 1 to 10 mm, and a surface area of 1 to 100 m 2 /g. The process according to claim 7 or 8, wherein said at least one alkyne is selected from the group consisting of acetylene, propyne, butyne-1 and butyne-2. The process according to any of claims 7 to 9, wherein said at least one sulfur compound is selected from the group consisting of hydrogen sulfide, carbonyl sulfide, mercaptans, organic sulfides, organic disulfides and mixtures thereof. The process according to any of claims 7 to 10, wherein said at least one sulfur compound is present in said feed at a level of less than 1 weight-% sulfur. The process according to any of claims 7 to 11, wherein said feed contains said at least one alkyne as an impurity in a C 2 -C 6 alkene stream. The process according to claim 12, wherein said feed contains said at least one alkyne at a level of 1 - 50 000 ppm by weight. The process according to any of claims 7 to 13, wherein said contacting is carried out at a reaction temperature of 40 - 200°C, and a molar ratio of hydrogen gas to said at least one alkyne in the range of 0.5:1 to 100:1. The process according to any of claims 7 to 14, wherein the catalyst contains silver. The process according to any of claims 7 to 15, wherein the catalyst comprises 0.01 to 1 weight-% palladium, 0.05 to 1.5 weight-% fluorine, and, if present, 0.01 to 10 weight-% silver. The process according to any of claims 7 to 16, wherein the weight ratio of silver to palladium is 2:1 to 10:1. The process according to any of claims 7 to 17, wherein the weight ratio of fluorine to palladium is 3:1 to 30:1. The process according to any of claims 7 to 14, and 18, wherein the catalyst consists of said palladium and said at least one alkali metal fluoride on said inorganic support material. Claims for the following Contracting State: SE Catalyst comprising palladium, at least one alkali metal fluoride, on an inorganic support material, selected from alumina, titania, zirconia and mixtures thereof. Catalyst according to claim 1, consisting of palladium and, at least one alkali metal fluoride on an inorganic support material, such as alumina, titania, zirconia and mixtures thereof. Catalyst according to claim 1 characterized in that it contains silver. Catalyst according to one of the claims 1 to 3, comprising 0.01 - 1 weight-%, palladium, 0.05 - 1.5 weight-%, fluorine and, if present, 0.01 - 10 weight-%, silver. Catalyst according to one of the preceding claims, wherein the weight ratio of fluorine to palladium is 3:1 to 30:1, and, if present, the weight ratio of silver to palladium is 2:1 to 10:1. Catalyst according to one of the preceding claims having a particle size of 1 - 10 mm, and surface area of 1 -100 m 2 /g. Process for selectively hydrogenating at least one alkyne containing 2 - 6 carbon atoms per molecule, which is present in a feed also comprising at least one sulfur compound, with hydrogen gas to at least one corresponding alkene containing 2 - 6 carbon atoms per molecule comprising contacting said feed and said hydrogen gas with a catalyst as defined in one of claims 1 to 6. Process according to claim 7, wherein said at least one alkyne is selected from the group consisting of acetylene, propyne, butyne-1 and butyne-2. Process according to claim 7 or 8, wherein said at least one sulfur compound is selected from the group consisting of hydrogen sulfide, carbonyl sulfide, mercaptans, organic sulfides, organic disulfides and mixtures thereof. Process according to one of claims 7 to 9, wherein said at least one sulfur compound is present in said feed at a level of less than 1 weight-%. Process according to one of claims 7 to 10, wherein said feed contains at least one alkyne as an impurity in a C 2 -C 6 alkene stream. Process according to claim 11, wherein said feed contains said at least one alkyne, at a level of 1 - 50 000 ppm by weight. Process according to one of claims 7 to 12, wherein said contacting is carried out at a reaction temperature of 40 - 200 °C, and a molar ratio of hydrogen gas to said at least one alkyne in the range of 0.5:1 to 100:1.

Inventors: CHEUNG TIN-TACK P, JOHNSON MARVIN M, CHEUNG, TIN-TACK P., JOHNSON, MARVIN M.
Applicants: CONOCOPHILLIPS CO, CONOCOPHILLIPS COMPANY
Application year: 1996
Main classification: B01J27
IPC codes: C07C7, C07B61, C07C5, B01J27, C07C11, C07B35