A hygroscopic fiber containing a hygroscopic polyester copolymer

Abstract: A hygroscopic polyester copolymer contains copolymerized units derived from (1) a hydrophilic compound which is preferably a polyoxyalkylene diol and (2) a cross-linking agent and has a release parameter ΔMR of at least 12% so as to be controlled in its moisture absorbing and releasing property. Fibers containing the polyester copolymer may be formed and these may be utilized in materials for underwear, sports wear, interlinings, etc. as highly hygroscopic woven and knitted fabrics, etc.

Description: The present invention relates to a hygroscopic polyester copolymer and a fiber containing it and, in particular, a fiber which can be ideally utilized in clothing materials for inner clothing, intermediate wear, sports wear, etc. Thermoplastic synthetic fibers, typically polyester and polyamide fibers, are widely used mainly for clothing and industrial applications since they are excellent in mechanical intensity, chemical resistance, heat resistance, etc. However, these synthetic fibers are very low in hygroscopicity, and if they are used in direct contact with or near the skin as inner clothing, intermediate wear, sports wear, etc., they are inferior to natural fibers in the feeling of comfort since perspiration from the skin makes the wearer feel stuffy and sticky. Thus, they are restrictively applied in clothing. To overcome the disadvantage, various suggestions have been made. For example, JP-C-60-000475, JP-U-60-040612 and JP-A-60-215835 have proposed attempts to obtain a hygroscopic and comfortable fabric using a combined yarn (i.e. a mixed yarn having different kinds of fiber), a parallelled yarn (i.e. a yarn formed by bringing together filament tows) or a twisted union yarn (i.e. a twisted parallelled yarn) respectively consisting of fibers high in equilibrium moisture regain (coefficient of moisture absorption) and synthetic fibers. These methods certainly improve the feeling of comfort to some extent, but not sufficiently so. Moreover, they have disadvantages in that disperse dyes generally used for dyeing synthetic fibers contaminate the fibers high in equilibrium moisture regain, in that isochroism is poor, and in that stress stretch, etc. are lowered to an extent such that the desired physical properties peculiar to synthetic fibers are lost. It is also known that polyester fibers can be made hygroscopic by graft-polymerizing acrylic acid or methacrylic acid to polyester fibers and substituting the carboxyl groups of the graft polymer by an alkali metal (JP-A-63-085163). However, this method is not applied in practice because polyesters do not allow easy graft polymerization and because color fastness, light fastness, physical properties of fibers, touch, etc. tend to be lowered. Methods of imparting hygroscopicity at a stage after processing cause various problems during dyeing or in view of the properties of the fabric obtained. Thus, in order to impart hygroscopicity at a stage of fiber production, in an attempt to solve the above problems, a conjugated fiber of the sheath-core type using a hygroscopic resin having a coefficient of moisture absorption at a ordinary humidity of 10% or more as the core component and a polyester as the sheath component was proposed in JP-A-02-099612. However, this method has a disadvantage in that the hygroscopic resin used as the core component absorbs water, becomes greatly swollen and so cracks the surface of the fiber and flows out due to its high solubility in water, during hot water treatment such as scouring and dyeing. JP-A-04-108113 discloses a sheath-core type conjugated fiber having a core/sheath ratio of 20/80 to 70/30, with the core in contact with a hollow portion formed within the conjugated fiber, while JP-A-06-136620 discloses the preparation of a hollow fiber by treating a sheath-core type conjugated fiber with hot water. In each case, the core component is a hydrophilic polymer which in fact is not cross-linked. However, it is found that the physical properties (strength-elongation characteristic) of such fibers are liable to deteriorate with the lapse of time. JP-A-51-136924 proposes a sheath-core type conjugated staple fiber with a hydrophilic polyester as the core component and a non-hydrophilic polyester as the sheath component. The hydrophilic polyester used is a polyalkylene glycol copolymer or a polyalkylene glycol copolymer mixed with a sulfonic acid or phosphoric acid ester derivative. Instead of filaments, staple fibers are employed so as to increase the number of fiber ends, the intention being thereby to enhance water absorbability. However, we have found that even though the staple fiber does have improved water absorbability, it does not have improved moisture absorbability. JP-A-53-111116 proposes conjugated fiber of the sheath-core type with a specific polyether ester as the core component. However, the intended effect is merely to make the fiber antistatic, and moreover, since a polyester obtained by copolymerizing a polyalkylene glycol alone is used as the core component, the physical properties (strength-elongation characteristic) of the fiber deteriorate with lapse of time. Furthermore, the polyether ester is remarkably colored, and so impairs the quality of the final product obtained. JP-A-52-055721 proposes a conjugated fiber with a non-hydrophilic polymer formable into a fiber as the sheath component, a hydrophilic polymer, which in fact is not crosslinked as the core component, and a continuous void in the core and/or between the core and the sheath along the fiber axis. However, again it is found that the physical properties of such fibers deteriorate with the lapse of time. JP-A-62-267352 discloses a polyester composition containing 50 to 70 wt% of a specific polyalkylene glycol. The fibers made of the composition are poor in physical properties (low strength and elongation) and are also poor in color fastness, and so cannot be used for clothing and industrial applications. JP-A-06-123012 discloses a sheath-core type hygroscopic polyester fibre. This fibre has a polymer obtained by blending a block polyether ester with a polyester obtained by copolymerizing an alkylene sulfoisophthalate and a polyoxyalkylene glycol, as the core component. However, the amount of the copolymerized polyalkylene glycol in the core component of the conjugated fiber is too small to obtain sufficient hygroscopicity. JP-A-53-099296, JP-A-58-138753 and JP-A-06-136107 disclose polyether esters prepared using a bisphenol A-ethylene oxide addition product. However, these copolymers are low in hygroscopicity, and moreover, since synthetic fibers containing this polymer suffer a deterioration in their physical properties with lapse of time, for example, they easily suffer a decline in elongation, difficulties are liable to occur during weaving and knitting which render them impractical. EP-A-0386256 discloses a polyester composition comprising (a) an aromatic polyester resin (100 parts by weight) and (b) a polyoxyethylene polyether (0.2 to 30 parts) including a higher oxyolefin content copolymerized with the polyester resin. The copolyester may additionally include a polyfunctional component having more than two carboxylic acid or hydroxyl groups. The composition may provide a component of certain types of conjugate fibre. The present invention seeks to provide a hygroscopic yarn of high commercial value which utilizes a polyester copolymer high in coefficient of moisture absorption and has specific moisture absorbing and releasing characteristic, for overcoming the above problems. To this end, the present invention provides a hygroscopic conjugated fibre comprising a conjugated fibre forming polymer component and a conjugate hygroscopic polyester copolymer component, which polyester copolymer comprises units derived from (i) an acid component and a glycol component capable of forming a polyester; (ii) a hydrophilic compound (A) selected from polyoxyalkylene compounds, polyoxazolines, polyacrylamide and derivatives thereof, polysulfoethyl methacrylate, polyacrylic and polymethacrylic acids and salts thereof, polyhydroxyethyl acrylate and methacrylate, polyvinyl alcohol and polyvinyl pyrrolidone. (iii) a cross-linking agent (B) which is a polyfunctional compound represented by the following formula (II); R 4 O) n R 3 (COOR 5 ) m where R 3 is a trivalent to hexavalent organic residue; R 4 is a hydrogen atom or acetyl group; R 5 is a hydrogen atom or alkyl group; and 3 ≤ m + n ≤ 6; the hydrophilic component (A) being present in the said copolymer in an amount of 40 to 90 wt% based on the total weight of the polyester copolymer; and which polyester copolymer has a release parameter (ΔMR), which defines moisture absorption as hereinafter explained, of at least 12%. The polyester copolymer may be derived from an ester component capable of polymerization, a hydrophilic compound (A) capable of copolymerizing with the ester component and a cross-linking agent (B) capable of a cross-linking reaction with at least units derived from the ester component. However, a proportion of the cross-linking agent (B) may be dispersed in, rather than having already reacted with, the copolyester so as to allow subsequent cross-linking reaction for inhibiting deterioration in physical properties. Especially preferred embodiments of the invention will now be described. The acid component of the polyester copolymer may be one or more dicarboxylic acids, preferably having a molecular weight no greater than about 400, which may be selected from aromatic dicarboxylic acids such as terephthalic acid, isophthalic acid, and naphthalene-2,6-dicarboxylic acid, and aliphatic dicarboxylic acids such as adipic acid and sebacic acid. Having regard to achieving heat resistance and good fiber formability, terephthalic acid is especially preferable. The glycol component may be one or more glycols, preferably having a molecular weight no greater than about 400, which may be selected from, for example, ethylene glycol, propylene glycol, tetramethylene glycol, diethylene, glycol and neopentyl glycol. Having regard to achieving heat resistance and good fiber formability, ethylene glycol is especially preferable. The polyester copolymer of the present invention has (1), copolymerized in it, a hydrophilic compound (A) to render the copolymer hygroscopic, and as an auxiliary component to further enhance hygroscopicity and also to stabilize the physical properties of the fiber, (2), copolymerized or dispersed in it, a cross-linking agent (B). The amount of the hydrophilic compound (A) copolymerized in the polyester copolymer should be 40 to 99 wt%, preferably 50 to 95 wt%, more preferably 55 to 90 wt% based on the total weight of the polyester copolymer having regard to achieving hygroscopicity and spinnability. The release parameter (hereinafter "ΔMR") defining the moisture absorbing and releasing characteristic of the polyester copolymer is preferably high in order to make the synthetic fiber made from it more hygroscopic. For a polyester copolymer of the present invention ΔMR should be 12% or more, preferably 15% or more, more preferably 18% or more. Realistically ΔMR is preferably 80% or less, and for improved stability in the physical properties of the yarn prepared from the fiber, it is preferably 70% or less. The value ΔMR is the difference (ΔMR (%) MR2 - MR1) obtained by subtracting the coefficient of moisture absorption (MR1) at 20°C and 65% RH from the coefficient of moisture absorption (MR2) at 30°C and 90% RH. The value ΔMR is an indicator of the ability of the fiber to release moisture from the worn clothes into open air, and therefore of the ability of the fiber to ensure a feeling of comfort by the wearer of such clothes. It represents the difference between the coefficient of moisture absorption at 30°C and 90% RH, simulating the temperature and humidity in clothes caused by execution of light to medium work or light to medium motion and the coefficient of moisture absorption at 20°C and 65% RH simulating the temperature and humidity of open air. Thus, ΔMR is a reasonable indicator for the likely feeling of comfort of worn clothes, and a higher ΔMR value means a higher moisture absorbing and releasing capability, hence better feeling of comfort when a fabric is worn. For further enhancing ΔMR, the hydrophilic compound (A) preferably has a number average molecular weight of 600 to 20000, more preferably 2000 to 10000, still more preferably 3000 to 9000. The hydrophilic compound (A) is a compound having one or more groups capable of ester formation and copolymerizable with a polyester, and is selected from polyoxyalkylene compounds, polyoxazolines, polyacrylamide and its derivatives, polysulfoethyl methacrylate, poly(meth)acrylic acid and its salts, polyhydroxyethyl (meth)acrylate, polyvinyl alcohol, and polyvinyl pyrrolidone. Among them, polyoxyalkylene compounds are preferable in view of their compatibility with the polyester. The polyoxyalkylene compounds include, for example, polyoxyethylene compounds, polyoxypropylene compounds and polyoxytetramethylene compounds. Above all, polyoxyethylene compounds are preferable, and polyethylene glycol is especially preferable because it has a large effect in enhancing hygroscopicity. Furthermore, the hydrophilic compound (A) preferably has a polyoxyalkylene component provided, for example, by polyethylene glycol or polyethylene glycol and a crystallization inhibitor component. Such a compound is preferred because its compatibility with the polyester is higher. In this case, the crystallization inhibitor component may be any organic residue existing in a molecular chain or at one or both terminal(s), to disturb the symmetry of the repeating unit of polyethylene glycol. The inhibition of crystallization means that the melting point obtained by differential scanning calorimetry (DSC, temperature rise rate 16°C/min) becomes lower than the melting point of polyethylene glycol with the same molecular weight. Specific compounds include derivatives of polyethylene glycol represented by the following formula (I) where X is -CR 1 R 2 - (R 1 and R 2 are each, independently of one another, a hydrogen atom or alkyl group), -SO 2 -, -O-, -S- or -C(O)-; and n and m are given by 10 ≤ n + m ≤ 450 and for a given residue are whole numbers. A compound having ethylene oxide (EO) added, for example, to bisphenol A or bisphenol S is preferred having regard to achieving higher compatibility with the polyester. It is preferred, for improving heat resistance, that such compounds are mostly polymerized in the polyester, but a proportion thereof may also be dispersed in the polymer. Moreover, the polyester copolymer of the present invention contains the cross-linking agent (B). The cross-linking agent is a compound which can react with the polyester, to form a cross-linked structure, namely a polyfunctional compound represented by the following formula (II) (R 4 O) n R 3 (COOR 5 ) m where R 3 is a trivalent to hexavalent organic residue; R 4 is a hydrogen atom or acetyl group; R 5 is a hydrogen atom or alkyl group; and 3 ≤ m + n ≤ 6. Such cross-linking agents are preferred because their reactivity with the polyester can be easily controlled. At least a proportion of the cross-linking agent, rather than having already reacted with the copolyester, may be merely at least partially dispersed in the polyester, so that at least some of the functional groups are later free to react to provide a cross-linked structure which inhibits any change in the properties of yarns of the fibres with the lapse of time. The cross-linking agent is preferably selected from polyfunctional carboxylic acids such as trimellitic acid, and pyromellitic acid, polyols such as glycerol, trimethylolpropane, and pentaerythritol having regard to the color tone of the polymer. Trimellitic acid is especially preferred. Since the cross-linking agent (B) is present, the polymer is even higher in hygroscopicity, and a cross-linked structure is formed in the polymer, whereby the yarn obtained from fibres thereof is especially resistant to change in physical properties with lapse of time. The amount of the cross-linking agent in the polyester copolymer is preferably 0.01 to 30 mol%, more preferably 0.5 to 15 mol%, still more preferably 1 to 10 mol% based on the total amount of acid component of the entire polyester. This total amount of acid component includes (when component (B) is an acid) that of the cross-linking agent (B). If the amount is in this range, higher hygroscopicity, good spinnability and improved physical properties such as strength of the yarn can be secured. To further enhance the hygroscopicity of the polyester copolymer, the polyester copolymer can contain a compound with one or more polar group which can be selected, for example, from an amino group, sulfonic acid group, carboxyl group, hydroxyl group, amide group or phosphonic acid group. Such may be in the form of a dispersion in the polyester or copolymerized with the polyester. The melt viscosity of the polyester copolymer of the present invention is preferably 500 to 5000 poises (50 to 500 Pa.s) more preferably 600 to 3000 poises (60 to 300 Pa.s), still more preferably 800 to 2000 poises (80 to 200 Pa.s), when measured at 280°C at a shear rate of 50 cm -1 . If the melt viscosity is in this range, the flow during conjugated spinning, for example, is stable to allow spinning without yarn breaking. Furthermore, the polyester copolymer of the present invention has hygroscopic swelling capability. Considering color fastness, the degree of hygroscopic swelling is preferably 1.2 to 3.2 times, more preferably 1.5 to 3.0 times in 20°C water. If the degree of hygroscopic swelling is in this range, a sheath-core type conjugated yarn obtained, for example, may be stable in form and resistant to sheath cracking. To keep the degree of hygroscopic swelling in this range, for example, the phase separated state of the polyester copolymer is selected properly. The polyester copolymer can, of course, contain a pigment such as titanium oxide or carbon black, surface-active agent such as alkylbenzenesulfonic acid, known antioxidant, anticoloring agent, light resisting agent, antistatic agent, etc. provided that the desired properties of a copolyester of the present invention are not seriously impaired. The polyester copolymer of the present invention can be used as a fiber component such as a conjugated component or blended component, together with a polymer capable of fiber formation, to obtain a highly hygroscopic fiber not impaired in physical properties such as strength. In the case of a fiber with a polyester copolymer of the present invention mixed with a polymer capable of fiber formation, the amount of the polyester copolymer is preferably 3 to 40 wt%, more preferably 5 to 35 wt%, still more preferably 7 to 30 wt% based on the total amount of the fiber. The lower limit of the amount is set for imparting sufficient hygroscopicity, and the upper limit is set having regard to maintaining desired spinnability and physical properties of the fiber. The polymer capable of fiber formation which can be utilized in forming a fiber of the present invention can be selected from polyesters, e.g. polythylene terephthalate and polybutylene terephthalate. Above all, a polyester mainly composed of polyethylene terephthalate most generally used for synthetic fibers for clothes is preferable. The synthetic fiber of the present invention may be, for example, a conjugated fiber of the sheath-core type, a conjugated hollow fiber of the sheath-core type, a conjugated fiber of the islands in a sea type, a conjugated fiber of the segment type (where segments adhere together), or a blended fiber. The hygroscopic copolyester of the present invention can be used as a conjugated component in an optional proportional amount. The use of the hygroscopic copolyester of the present invention as a conjugated core or land component is preferable in view of the higher color fastness thereby obtained. For example, when the polyester copolymer of the present invention is used as the core component in a sheath-core type conjugated fiber or sheath-core type conjugated hollow fiber, the ratio by weight of core/sheath is preferably 5/95 to 90/10, more preferably 7/93 to 50/50, still more preferably 10/90 to 30/70. The conjugating ratio can be optionally selected for applications with or without dyeing. The lower limit to the amount of the core is set for imparting sufficient hygroscopicity, and the upper limit is set having regard to maintaining desired spinnability and physical properties of the fiber. It is preferable that a hollow portion exists at the interface between the core and the sheath. If the hollow portion exists, it can ease and absorb the swelling power of the hygroscopic polymer, to prevent the sheath cracking when the core is hygroscopically swollen. The proportion of the hollow portion, in terms of its cross-sectional area and based on the cross sectional area of the fiber defined by the outer periphery of the fiber is preferably at least 1.4%, more preferably 1.8% or more, still more preferably 2.4% or more. Having regard to spinning stability, it is preferable that the hollow portion represents 70% or less of the total cross-sectional area. In an islands in a sea type conjugated fiber or a segmented type conjugated fiber, the conjugating ratio of the polyester copolymer (by weight) is preferably 5/95 to 90/10, more preferably 7/93 to 50/50, still more preferably 10/90 to 30/70. The conjugating ratio can be optionally selected for applications with or without dyeing. The lower limit of the conjugating ratio is set for imparting sufficient hygroscopicity, and the upper limit is set having regard to maintaining desired spinnability and physical properties of the fiber. Furthermore, the islands in a sea type conjugated fiber and the segment type conjugated fiber can also have a hollow portion at any optional place, but it is preferable that the hollow portion exists at the interface between sea and land or at the interface between the segment components stuck together. Again, for such islands in a sea or segment type conjugated fibers, the proportion of the hollow portion, in terms of its cross-sectional area, as described above, is at least 1.4%, more preferably 1.8% or more, still more preferably 2.4% or more and is preferably 70% or less. In order to maximize the practical comfort to the wearer, the ΔMR of the fiber is recommended to be as high as possible, preferably 1.0% or more, more preferably 1.5% or more, still more preferably 2.0% or more. In the present invention, the component which is conjugated or blended with the polymer capable of fiber formation may also contain, in addition to the polyester copolymer of the invention, another fibre forming polymer for example, a polyolefin, polyamide, polyester or polycarbonate, provided that the desired properties of the fiber are not seriously impaired. The polymer capable of fiber formation can, of course, contain a pigment such as titanium oxide or carbon black, and also any known antioxidant, anticoloring agent, light resisting material, antistatic agent, etc. as desired for a given application. In preparing a fiber of the present invention, especially a conjugated fiber consisting of a polymer capable of fiber formation and the polyester copolymer of the present invention, any known method can be employed. A typical method for preparing a sheath-core type conjugated fiber is described below. For example, in the case of a sheath-core type conjugated fiber, a polyester (sheath) and the polyester copolymer of the present invention (core) are separately rendered molten, and introduced into a spinning pack, to form a sheath-core conjugated flow in a die, which is spun out of a discharge opening to form a plurality of conjugated fibers. The resultant spun filament yarn is taken up at a predetermined speed, and once wound as a package, and the undrawn yarn obtained is drawn by a conventional drawing machine. For this drawing, the spun yarn can be directly continuously drawn without being wound after having been taken up, or can be taken up at a high speed of 4000 m/min or more, to make, in one operation a yarn with desired performance characteristics, without the yarn being substantially drawn. For directly drawing after spinning, for example, the spun yarn can be taken up at 1000 to 5000 m/min and in succession drawn and thermally set at 3000 to 6000 m/min. The sectional form of the fiber of the present invention is not limited to a circle, and can also be a special form such as a triangle, flat or multi-leaf. Moreover, the fiber can be either a filament or staple fiber, which can be properly selected to suit each application. The fabric can be a woven fabric, knitted fabric or nonwoven fabric, etc. which can be properly selected to suit each application. Embodiments of the present invention will now be described below in more detail with reference to the following Examples. In the Examples, the values for respective properties of the polyesters and fibers containing them were obtained according to the following methods. A. Intrinsic viscosity [η] of polyester. Obtained for an o-chlorophenol solution at 25°C. B. Moisture absorption and release parameter (ΔMR) of polyester copolymer or fiber containing it. For a polymer, 1 g of a chip was cut into an about 2 mm cube to make a sample, and for a yarn, 1 to 3 g of a raw yarn or cloth was used as a sample. The absolute dry weight of the sample was measured. The sample was allowed to stand in a thermo-hygrostat (PR-2G produced by Tabai) at 20°C and 65% RH or at 30°C and 90% RH for 24 hours, and weighed. The coefficient of moisture absorption was obtained from the following formula: Coefficient of moisture absorption (%) = [(Weight after moisture absorption - Absolutely dry weight)/Absolutely dry weight] × 100 From the coefficient of moisture absorption measured after treatment at 20°C and 65% RH and that at 30°C and 90% RH (respectively expressed as MR1 and MR2), the moisture absorption coefficient difference ΔMR (%) = MR2 - MR1 was obtained. If the polyester copolymer is higher in ΔMR, the hygroscopicity of the yarn can, to advantage, be more efficiently enhanced. Accordingly, the following criterion was used: ΔMR ≥ 18 ... o 12 ≤ ΔMR < 18 ... Δ ΔMR < 12 ... x C. Melt viscosity of polyester copolymer. A polyester copolymer was dried in vacuum at 130°C for 12 hours, and the melt viscosity was measured by a melt indexer produced by Takara Kogyo, at a load of 325 g, 280°C and a shear rate of 50 cm -1 . D. Degree of hygroscopic swelling. A polyester copolymer chip was dried in vacuum at 130°C for 12 hours, accurately weighed, and put into a container filled with water. After 24 hours, the chip with water absorbed was weighed, and the ratio of the chip weight after water absorption to the chip weight before water absorption was obtained from the following formula as the degree of hygroscopic swelling. Degree of hygroscopic swelling = Chip weight after water absorption/Chip weight before water absorption E. Spinnability. Spinning was effected for 3 hours under the conditions stated in Example 1. The following criterion was used: No yarn breaking ... o Yarn breakage once ... Δ Yarn breakage two or more times ... x F. Strength and elongation. A Tensilon tensile testing machine produced by Toyo Baldwin Co., Ltd. was used, to obtain a stress-strain curve with the sample length as 20 cm at a tensile speed of 10 cm/min, and from the curve, the respective values were obtained. G. Change of yarn with the lapse of time. A drawing yarn was allowed to stand at 20°C and 70% RH for 1 month, and the strength-elongation characteristic stated in F was obtained, compared with that obtained immediately after drawing, and the deterioration in elongation measured. The following criterion was used: Elongation decreased by less than 8% ... o Elongation decreased by 8% to less than 16% (for example, if the elongation decreased from 40% to 32%, the proportional reduction is 8%) ... Δ Elongation decreased by 16% or more (for example, elongation decreased from 40% to 24% or less) ... x H. Proportion of hollow portion. A section of a fiber was photographed at about 100 times magnification, and each photo was further enlarged to twice the size. 10 single fibers were selected, and the cross-sectional area of the hollow portion as a proportion of the entire section was calculated from the following formula based on the cross-sectional area of the fiber defined by the external periphery of the fiber. Hollow portion area (%) = [(Area of hollow portion)/(Area of entire section)] × 100 Example 1 A flask was charged with 188 parts of terephthalic acid dimethyl ester, 124 parts of ethylene glycol, 7.6 parts of trimethyl trimellitate (TMTM) and 0.4 part of tetrabutyl titanate, and while methanol was distilled away at 140 to 230°C, ester interchange reaction was effected. Then, an ethylene glycol solution containing 0.08 part of phosphoric acid trimethyl ester, and 582 parts of polyethylene glycol (PEG) having a number average molecular weight of 6000, 1.2 parts of Irganox 1010 (produced by Ciba Geigy) as an antioxidant, 0.8 part of silicone as a defoaming agent, and 0.4 part of tetrabutyl titanate were added to the reaction product, and polymerization was effected at a reduced pressure of 1.0 mm Hg at 250°C for 4 hours, to obtain a polyester copolymer. The amount of polyethylene glycol copolymerized in the copolymer was 75 wt%. The ΔMR of the polyester copolymer obtained was 31.0% (M1 = 2.5%, M2 = 33.5%). Furthermore, the melt viscosity (280°C) of the polyester copolymer obtained was 1100 poises (110 Pa.s), and the degree of hygroscopic swelling was 2.8 times. The polyester copolymer as the core component and polyethylene terephthalate having an intrinsic viscosity of 0.70 as the sheath component were separately rendered molten, and discharged from concentric sheath-core conjugating dies at a ratio by weight of core/sheath = 15/85, to obtain an undrawn yarn. It was drawn and thermally treated to obtain a concentric sheath-core type conjugated yarn of 75 deniers and 24 filaments. The yarn was cylindrically knitted, and its ΔMR was measured and found to be 2.8%. It was also good in strength-elongation characteristic. It did not decrease in elongation with lapse of time. Examples 2 to 7, and Comparative Example 1 In Examples 2 to 6, polyester copolymers were obtained as in Example 1, with the proportional amount of polyethylene glycol copolymerized in the polyester copolymer kept constant, but with differing amounts of TMTM. In Example 7, a polyester copolymer was obtained as in Example 1, with the same composition, but for a shorter reaction time (3 hrs). The melt viscosity of the polymer was therefore comparatively low. The decrease in. elongation of the yarn was 10%. In Comparative Example 1, spinnability was poor, and among the properties of the yarn, the elongation decreased with lapse of time (Table 1). Examples 8 to 14, and Comparative Example 2 Polyester copolymers and polyester yarns were obtained as in Examples 1 to 7 and Comparative Example 1, except that bisphenol A ethylene oxide (EO) addition product (BPA) having a number average molecular weight of 6000 was used instead of polyethylene glycol in the polyester copolymer. In Comparative Example 2, spinnability was poor and the elongation decreased with lapse of time (Table 2). Examples 15 to 21, and Comparative Example 2 Polyester copolymers and yarns were obtained as in Examples 1 to 7 and Comparative Example 1, except that a bisphenol sulfone (S), having a number average molecular weight of 6000, /EO addition product (BPS) was used instead of polyethylene glycol in the polyester copolymer. In Comparative Example 3, spinnability was poor and the elongation decreased with lapse of time (Table 3). Examples 22 to 31, and Comparative Examples 4 and 5 Polyester copolymers were obtained as in Example 1, except that the amount of TMTM was kept constant at 3 mol% and that polyethylene glycol was changed in molecular weight or copolymerized amount. Yarns were prepared as in Example 1, and the properties of the yarns are shown in Table 4. When the amount of PEG copolymerized was smaller than 40 wt% (Comparative Example 4), sufficient moisture absorbability could not be obtained. When the amount of PEG copolymerized was larger than 99 wt% (Comparative Example 5), moisture absorbability was low, and when the polyester copolymer was processed into a fiber, yarn breakage occurred very often, not allowing the intended conjugated fiber to be obtained, since the polyester copolymer was low in spinnability (Table 4). Examples 32 to 36 The polyester copolymer obtained as the core component in Example 1 and the same polyethylene terephthalate having an intrinsic viscosity of 0.70 used as the sheath component in Example 1 were separately rendered molten, and from concentric sheath-core conjugating dies, undrawn yarns were obtained at five different core-sheath conjugating ratios. They were drawn and heat-treated to obtain concentric sheath-core type conjugated yarns of 75 deniers and 24 filaments respectively. The properties of the yarns are shown in Table 5. According to the increase of the core-sheath ratio, ΔMR increased, but the strength and elongation decreased, while the elongation changed to some extent with lapse of time (Table 5). Examples 37 to 41 Sheath-core type conjugated hollow yarns (hollow portion area 6%) of 75 deniers and 24 filaments respectively were obtained as in Example 1, except that dies for forming a hollow portion at the interface between sheath and core were used. The properties of the yarns are shown in Table 6. According to the increase of the core-sheath ratio, ΔMR increased, but the strength and elongation decreased, while the elongation changed to some extent with lapse of time. The yarns were cylindrically knitted into fabrics which were dyed. They were good in fastness (Table 6). Examples 42 to 46 The polyester copolymer obtained in Example 1 as the land component (18 land pieces) and polyethylene terephthalate having in an intrinsic viscosity of 0.70 as the sea component were separately rendered molten, and from sea-land type conjugating dies, undrawn yarns were obtained at properly different land/sea ratios. They were drawn and heat-treated, to obtain sea-land type conjugated yarns of 75 deniers and 9 filaments respectively. The properties of the yarns are shown in Table 7. According to the increase of the core-sheath ratio, ΔMR increased, but the strength and elongation decreased, while the elongation changed to some extent with lapse of time (Table 7). Examples 47 to 49 The polyester copolymer (A) obtained in Example 1 and polyethylene terephthalate (B) having an intrinsic viscosity of 0.70 were separately rendered molten and from segment type conjugating dies, undrawn yarns were discharged at segment ratios (by weight) of A/B - 60/40, 50/50 and 40/60. They were drawn and heat-treated to obtain segment type conjugated yarns of 75 deniers and 24 filaments respectively. The properties of the yarns are shown in Table 8. They were high in ΔMR, strength and elongation (Table 8). Examples 50 to 54 The polyester copolymer (A) obtained in Example 1 and polyethylene terephthalate (B) having an intrinsic viscosity of 0.70 were rendered molten and mixed in an extruder at appropriate different ratios by weight, and from circular dies, undrawn yarns were discharged. They were drawn and heat-treated to obtain polyester yarns of 75 deniers and 24 filaments respectively. The properties of the yarns are shown in Table 9. With increase of the blending ratio, ΔMR increased, but the strength and elongation decreased while the elongation changed to some extent with lapse of time (Table 9). Composition and hygroscopic properties of copolymer Spinnability Properties of yarn Amount of PEG copolymerized (wt%) Amount of TMTM copolymerized (mol%) ΔMR (%) Evaluation Melt viscosity (poises) Strength (g/d) Elongation (%) ΔMR (%) Change over time Example 1 75 3 31.0 o 1100 o 4.2 40.2 4.2 o Example 2 75 1 30.6 o 1120 o 4.3 41.3 4.3 o Example 3 75 5 32.2 o 1080 o 4.2 40.4 4.1 o Example 4 75 12 31.2 o 1800 o 3.8 38.4 3.8 o Example 5 75 25 31.4 o 2120 Δ 3.4 36.5 3.8 o Example 6 75 40 30.2 o 2400 Δ 3.0 33.4 3.7 o Comparative example 1 75 0 30.3 Δ 200 × 4.2 42.0 3.8 × Example 7 75 3 29.0 Δ 310 Δ 4.2 41.2 3.9 Δ Molecular weight of PEG: 6000 Composition and hygroscopic properties of copolymer Spinnability Properties of yarn Amount of BPA copolymerized (wt%) Amount of TMTM copolymerized (mol%) ΔMR (%) Evaluation Melt viscosity (poises) Strength (g/d) Elongation (%) ΔMR (%) Change over time Example 8 75 3 30.2 o 1120 o 4.2 40.2 4.1 o Example 9 75 1 31.6 o 1140 o 4.3 41.3 4.3 o Example 10 75 5 30.9 o 1080 o 4.2 40.4 4.2 o Example 11 75 12 31.7 o 1700 o 3.8 38.4 3.9 o Example 12 75 25 31.4 o 2180 o 3.4 36.5 3.8 o Example 13 . 75 40 31.2 o 2360 Δ 3.0 33.4 3.7 o Comparative example 2 75 0 30.0 Δ 220 × 4.2 41.0 4.0 × Example 14 75 3 29.0 Δ 360 Δ 4.0 39.0 3.9 Δ Molecular weight of BPA: 6000 Composition and hygroscopic properties of copolymer Spinnability Properties of yarn Amount of BPS copolymerized (wt%) Amount of TMTM copolymerized (mol%) ΔMR (%) Evaluation Melt viscosity (poises) Strength (g/d) Elongation (%) ΔMR (%) Change over time Example 15 75 3 29.0 o 1050 o 4.1 39.2 4.2 o Example 16 75 1 30.2 o 1100 o 4.2 40.3 4.3 o Example 17 75 5 31.2 o 1050 o 4.1 40.1 4.1 o Example 18 75 12 31.8 o 1850 o 3.7 38.4 3.7 o Example 19 75 25 30.4 o 2020 o 3.3 36.5 3.7 o Example 20 75 40 29.2 o 2520 Δ 3.0 31.4 3.7 o Comparative example 3 75 0 29.8 Δ 270 × 4.1 40.0 4.1 × Example 21 75 3 29.0 Δ 390 Δ 4.2 40.6 3.9 Δ Molecular weight of BPS: 6000 Composition and property Properties of yarn Molecular weight of PEG Amount of PEG copolymerized (wt%) ΔMR (%) Evaluation Strength (g/d) Elongation (%) ΔMR (%) Change over time Comparative example 4 6000 35 10.5 × 4.1 40.4 1.4 o Example 22 6000 45 12.8 Δ 4.3 41.3 2.0 o Example 23 6000 55 24.7 o 4.1 40.6 3.7 o Example 24 6000 70 30.3 o 4.2 41.5 4.5 o Example 25 6000 93 28.6 o 4.2 40.2 4.2 Δ Comparative example 5 6000 99.5 8.6 × - - - - Example 26 400 75 12.3 Δ 4.2 40.1 1.9 Δ Example 27 1000 75 23.6 o 4.2 41.2 2.7 o Example 28 3000 75 26.1 o 4.2 40.5 4.2 o Example 29 5000 75 28.4 o 4.3 41.3 3.3 o Example 30 8000 75 30.0 o 4.2 40.4 1.9 o Example 31 24000 75 12.1 Δ 4.2 41.0 1.8 o TMTM 3 mol% Properties of yarn Core-sheath conjugating ratio Strength (g/d) Elongation (%) ΔMR (%) Change over time Example 32 7/93 4.6 38.4 2.1 o Example 33 10/90 4.3 41.0 2.8 o Example 34 25/75 3.8 41.2 8.2 o Example 35 50/50 2.6 27.3 14.1 Δ Example 36 90/10 1.3 22.1 26.1 Δ Properties of yarn Core-sheath conjugating ratio Strength (g/d) Elongation (%) ΔMR (%) Change over time Example 37 7/93 4.5 41.4 2.2 o Example 38 10/90 4.3 40.6 2.7 o Example 39 25/75 3.6 39.6 8.4 o Example 40 50/50 2.5 28.5 14.0 Δ Example 41 90/10 1.2 22.4 25.6 Δ Properties of yarn Land/sea conjugating ratio Strength (g/d) Elongation (%) ΔMR (%) Change over time Example 42 7/93 4.5 39.4 2.0 o Example 43 10/90 4.2 40.7 2.8 o Example 44 25/75 3.8 39.5 8.3 o Example 45 50/50 2.7 28.8 14.6 Δ Example 46 90/10 1.3 21.4 26.5 Δ Properties of yarn A/B conjugating ratio Strength (g/d) Elongation (%) ΔMR (%) Change over time Example 47 60/40 3.4 37.4 15.0 o Example 48 50/50 3.7 40.0 13.8 o Example 49 40/60 3.7 39.5 11.2 o Properties of yarn A/B blending ratio Strength (g/d) Elongation (%) ΔMR (%) Change over time Example 50 7/93 4.2 40.4 1.9 o Example 51 10/90 3.8 41.0 2.8 o Example 52 20/80 3.5 35.3 5.2 o Example 53 35/65 2.4 24.3 9.1 Δ Example 54 70/30 1.2 20.0 18.5 Δ Polyester copolymers embodying the present invention have very high hygroscopicity, and yarns obtained from them have sufficient hygroscopicity to ensure wearing comfort. The yarns also have a dry touch, softness and high color fastness and light fastness. Fibers embodying the present invention are suitable for underwear, shirts, blouses, intermediate wear, sports wear, slacks, outer wear, interlinings, curtains, wall paper, and furthermore, are highly practical for bed sheets, bedquilt covers, fillings, etc.

Claims: A hygroscopic conjugated fibre comprising a conjugated fibre forming polyester component and a conjugated hygroscopic polyester copolymer component, which polyester copolymer comprises units derived from (i) an acid component and a glycol component capable of forming a polyester; (ii) a hydrophilic compound (A) selected from polyoxyalkylene compounds, polyoxazolines, polyacrylamide and derivatives thereof, polysulfoethyl methacrylate, polyacrylic and polymethacrylic acid and salts thereof, polyhydroxyethyl acrylate and methacrylate, polyvinyl alcohol and polyvinyl pyrrolidone; and (iii) a cross-linking agent (B) which is a polyfunctional compound represented by the following formula (II); (R 4 O) n R 3 (COOR 5 ) m where R 3 is a trivalent to hexavalent organic residue; R 4 is a hydrogen atom or acetyl group; R 5 is a hydrogen atom or alkyl group; and 3 ≤ m + n ≤ 6; the hydrophilic compound (A) being present in the polyester copolymer in an amount of 40 to 99 wt% based on the total weight of the polyester copolymer; which polyester copolymer has a release parameter ΔMR of at least 12%, where the release parameter ΔMR is the difference between the respective coefficients of moisture absorption MR(%) at 30°C and 90% RH (MR2) and at 20°C and 65% (MR1) and wherein the coefficient of moisture absorption MR is given by MR(%) = 100 (weight after moisture absorption - absolute dry weight) absolute dry weight A hygroscopic conjugated fibre according to claim 1, wherein the hygroscopic polyester copolymer has a release parameter (ΔMR) of from 12 to 80%. A hygroscopic conjugated fibre according to claim 1 or claim 2, wherein the number average molecular weight of the hydrophilic compound (A) is 600 to 20000. A hygroscopic conjugated fibre according to claim 1, claim 2 or claim 3, wherein the hydrophilic compound (A) is a polyoxyalkylene compound. A hygroscopic conjugated fibre according to claim 4, wherein the hydrophilic compound (A) is a polyoxyalkylene compound with a crystallinity inhibitor component. A hygroscopic conjugated fibre according to claim 5, wherein the polyoxyalkylene compound with a crystallinity inhibitor component is a polyethylene glycol derivative represented by the following formula (I); where X is -CR 1 R 2 - (R 1 and R 2 are each, independently of one another, a hydrogen atom or alkyl group), -SO 2 , -O-, -S- or -C(O)-; and n and m are given by 10 ≤ n + m ≤ 450. A hygroscopic conjugated fibre according to any preceding claim, wherein the cross-linking agent (B) is present in the polyester copolymer in an amount of 0.01 to 30 mol% based on the total acid content of the entire copolymer, which total acid content includes (when the cross-linking agent (B) is an acid) that of the cross-linking agent (B). A hygroscopic conjugated fibre according to any preceding claim, wherein the melt viscosity of the hygroscopic polyester copolymer, measured at 280°C at a shear rate of 50 cm -1 , is 50 to 500 Pa.s (500 to 5000 poises). A hygroscopic conjugated fibre according to any preceding claim, wherein the degree of hygroscopic swelling in 20°C water of the hygroscopic polyester copolymer is from 1.2 to 3.2 times. A hygroscopic conjugated fibre according to any preceding claim, which is of a sheath-core type comprising, as a sheath component thereof, a polymer formable into a fibre and, as a core component thereof, the said hygroscopic polyester copolymer. A hygroscopic conjugated fibre according to claim 10, wherein the core/sheath conjugating ratio (wt%) is 5/95 to 90/10. A hygroscopic conjugated fibre according to claim 10 or claim 11, additionally having a hollow portion provided therein and in contact with the core component. A hygroscopic conjugated fibre according to claim 12, wherein the core/sheath conjugating ratio (wt%) is 5/95 to 90/10. A hygroscopic conjugated fibre according to claim 12 or claim 13, wherein the hollow portion provides from 1.4% to 70% of the cross-sectional area of the conjugated fibre. A hygroscopic conjugated fiber according to any one of claims 1 to 9, which is of an islands in a sea-type comprising, as a sea component thereof, a polymer formable into a fibre and, as island component thereof, the said hygroscopic polyester copolymer. A conjugated fiber according to claim 15, wherein the sea/islands conjugating ratio (wt%) is 5/95 to 90/10. A hygroscopic conjugated fibre according to any one of claims 1 to 9, which is of a segment type comprising from 95 to 10 wt% of a polymer formable into a fibre and from 5 to 90 wt% of the said hygroscopic polyester copolymer. A hygroscopic conjugated fiber according to any preceding claim, wherein the fiber forming polymer is a polyester. A hygroscopic conjugated fiber according to any preceding claim, wherein ΔMR of the fiber is at least 1.0%.

Inventors: HARASHINA YUKO, HIGUCHI TETSUNORI, MATSUMURA YOSHITAKA, SASAMOTO TAI, HARASHINA, YUKO, HIGUCHI, TETSUNORI, MATSUMURA, YOSHITAKA, SASAMOTO, TAI
Applicants: TORAY INDUSTRIES, TORAY INDUSTRIES, INC.
Application year: 1996
Main classification: D01F8
IPC codes: D01F8, D01F6, C08G63