Sealed rechargeable battery

Abstract: A long-life sealed rechargeable battery employing a plastic battery container in use for electric vehicles and the like, wherein as least one tube having the bottom is formed under the cover, the pointed end of the tube is either brought as close as possible to the upper edge of the electrode group or put into direct contact with a lead tab of the positive or negative electrode, and a temperature sensor is inserted and fixed inside the tube in such a way that the temperature sensing part comes into direct contact with the inner surface of the pointed end of the tube, thereby capable of measuring from the outside temperature variation in the cell so as to control charge and discharge.

Description: II. BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a sealed rechargeable battery, particularly to a sealed rechargeable battery provided with a temperature sensor that measures temperature inside the cell. Description of the Prior Art Recently, exhaust gas emitted from automobile engines has been a matter of concern from a viewpoint of environmental pollution. As a countermeasure, the development and practical use of electric vehicles ( hereafter referred to as EV's ) have been vigorously carried out in major countries all the world over. The success in practical use of EV's depends on the availability of a good power supply battery which drives EV's. The requirements for EV batteries are: ( 1 ) high energy density, and small size and light weight ( 2 ) long charge-discharge cycle life, and high economical efficiency ( 3 ) easy maintenance A battery system which has been thus far mostly employed for the EV battery is, due to its comparatively low initial price, a lead-acid battery. In this lead-acid battery, the volume of electrolyte solution is starved so that in the over charge period gaseous oxygen produced at the positive electrode is absorbed by and disappears in the negative electrode, thereby facilitating hermetic seal and easy maintenance. However, no significant improvements have been seen in high energy density and long cycle life. Consequently, sealed alkaline rechargeable batteries based on a nickel-cadmium system that has an excellent output characteristics and a long cycle life and a nickel-metal hydride system that has as high output and as long cycle life as the nickel-cadmium system and has a high energy density have recently attracted much attention. For EV batteries of these systems, in order to practically prolong the driving distance per one charge, a series- and / or parallel-connection of a plurality of comparatively large single cells, or module batteries having a series-connection in monoblock structure of, for example, a nominal voltage of 6 V is used as an assembled battery of a desired nominal voltage and capacity. For these EV batteries, a battery container consisting a plastic case and cover that are made of polyethylene ( hereafter referred to as PE) or polypropylene ( hereafter referred to as PP ) or the like the main ingredient of which is polyolefin is mostly used because of its excellent mechanical strength such as shock-proof and vibrationproof, good chemicals-resistance, and high economical efficiency. In order to save maintenance operations such as supplying water for electrolyte, a sealed rechargeable battery is generally designed and manufactured in such a way that the negative electrode capacity is larger than the positive electrode capacity, so that in the time from the end of charge to over charge gaseous oxygen produced at the positive electrode is absorbed by and disappears at the negative electrode and consequently in the normal condition the internal pressure does not go up to a specified value. In order to prevent an abnormal increase of cell internal pressure, each cell is provided with a safety valve. The reaction during over charge wherein gaseous oxygen is absorbed by and disappears at the negative electrode, as described, above is a heat generating reaction, then the temperature inside the cell increases. Particularly in a nickel-metal hydride system that employs a hydrogen absorbing alloy for the negative electrode, the reaction wherein by means of charge hydrogen is absorbed into the hydrogen absorbing alloy to form a hydride is also a heat generating reaction and consequently the temperature increases much higher than in any other battery systems. Much higher temperature would make the rechargeable battery so deteriorated that it could not recover. In various sealed rechargeable batteries, therefore, several means are taken not to continue over charge unlimitedly, partly because of saving electric power. For example, in a lead-acid system, a constant current - constant voltage charging method is mostly employed wherein charge is carried out at an almost constant current until to a specified voltage, then when the charging voltage of the cell reaches a specified voltage, it is switched to a constant voltage charge thereby decreasing a charging current. On the other hand, in a nickel-cadmium system, in the case of a low rate of constant current charge such as over night charge, heat generation during charge time is not so vigorous that charge without control is generally employed. In the case of a quick charge by a high-rate equal to or more than 1 C, however, as charge proceeds, the cell voltage increases, and when it enters the over charge region it has been recommended to employ a - ΔV control system that makes use of the fact that the increased temperature in the cell, as previously described, allows the charge voltage to decrease. In this case, around the end of charge, when a voltage drop of about 5 mV / cell is observed after reaching a voltage peak, charge is either continued at a tricle current of about 1/20 C or stopped. In a nickel-metal hydride system, there are problems that the temperature increase due to over charge, whatever charge rate, makes the surface of hydrogen absorbing alloy powder of the negative electrode oxidized, thereby deteriorating its hydrogen absorption capability and forcing the gas pressure in the cell to increase by gaseous hydrogen. Over charge therefore has to be avoided as much as possible, but considering that in a nickel-metal hydride system no - ΔV effect is clearly observed as in a nickel-cadmium system and that even over charge during the action of the - ΔV control system gives rise to deterioration, a method has been employed that as soon as a temperature increase is sensed charge is stopped thereby avoiding over charge. The method that avoids over charge by temperature has so far been applied to other battery systems as well as the nickel-metal hydride system in order to improve reliability, and has been sometimes employed together with another control system. A sealed lead-acid rechargeable battery wherein a temperature sensor is provided being capable of measuring temperatures inside the cell from the outside to control charge is disclosed, for example, in Japanese Patent Application Open-Laying No. Sho 63-281367. Its specification describes that the sensing part of a temperature sensor is brought into contact with the central part of a group of electrode plates and separators, or a position capable of measuring in a correct way temperature variation, such as the main part of an electrode grid, and the portion of the cover through which its connecting lead wire passes through is hermetically sealed. However, when the cell container comprises a case and a cover that are made of plastics, the main ingredient of which is non-polar polyolefin, such as PE and PP, no appropriate adhesive agent is available and it is thus difficult to keep the state of hermetic seal for a long term. Taking into account these situation, some examples of a sealed nickel-metal hydride rechargeable battery wherein a temperature sensor is provided inside a single cell at the central part of a module battery at which place temperature is highest throughout inside the cell, or is provided on the outer surface of the case of the single cell are disclosed in Japanese Patent Application Open-laying No Hei 5-326024 and other examples wherein a temperature sensor is buried in the electrode terminal, or attached on the upper surface of the electrode terminal thereafter being covered with heat resisting material, or sealed in the PP tube disposed inside the case are disclosed in Japanese Patent application Open-laying No Hei 6-133468. In the case that a temperature sensor is provided on the surface of the case, although the state of hermetic seal is maintained, the fact that the thermal conductivity of the plastic case is low results in a slow response to temperature variation inside the cell, allowing a time lag in the measured values of temperature. In the case that a temperature sensor is fixed to the battery terminal, the fact that the metal electrode has a high thermal conductivity results in a significantly fast response to temperature variation, but the measured values of temperature is affected by the ambient temperature. This effect is avoided by covering it with heat insulating material, but giving rise to another problem that it constrains emission of heat produced inside the cell toward the outside. In the case that a temperature sensor is sealed inside a PP tube disposed inside the cell, it would give a good chemicals-resistance, but, as described perviously, it has a drawback that it would be difficult to liquid-tight seal between a lead wire connected to the temperature sensor and the PP tube. FR-A-2,589,008 discloses a rechargeable battery provided with a charging monitoring circuit which includes a temperature sensor depending into the interior of the battery casing and in contact with the liquid electrolyte. US-A-2,431,945 discloses a rechargeable battery that is designed so that it is feasible to assemble a thermal switch from the exterior of the battery below the normal level of the electrolyte and still not have the switch in contact with the electrolyte. This is achieved by forming the battery cover with a hollow member depending from the cover which constitutes a recess or well for housing the thermal switch. III Summary of the Invention The present invention provides a rechargeable battery comprising a plastics battery container having disposed therein: an electrode group having a first edge and comprising a plurality of alternating positive electrode plates and negative electrode plates, said positive and negative plates each having lead tabs connected to respective positive and negative poles, a plurality of separators disposed between each of said alternating positive and negative electrode plates and a volume of electrolyte, the battery further being provided with a temperature sensor for sensing an internal temperature of the battery characterised in that the battery is a sealed battery and the container is provided with a safety valve, and at least one tube receiving the temperature sensor, the tube having a closed second end which protrudes toward the electrode group such that the closed end contacts the electrode group or such that the distance between the closed end of the tube and the first edge of the electrode group is not larger than 2mm, the temperature sensor having a temperature sensing part in direct contact with the inner surface of the closed end of the tube. IV Brief Description of the Drawing Fig 1 is a perspective view, partly exposed, of a sealed rechargeable single cell according to the present invention. Fig 2 is a cross sectional view of the essential part of the single cell. Fig 3 shows the temperature variation in a test cell during low-rate charge at 25°C. Fig 4 shows the temperature variation in a test cell during low-rate charge at 0°C. Fig. 5 shows the temperature variation in a test cell during high-rate charge at 25 °C. Fig. 6 shows the capacity and weight changes of cells during charge-discharge cycle. Fig. 7 shows the temperature variations during charge as a parameter of the distance between the pointed end of the tube and the upper surface of the electrode group. V. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT A sealed rechargeable battery according to the present invention will be explained in detail with a nickel-metal hydride system as an example, referring to the drawings. Fig. 1 is a perspective view, partly exposed, of a sealed rechargeable single cell 1 based on nickel-metal hydride system according to the present invention. Fig. 2 is a cross sectional view of the essential part of the single cell 1. At first, a positive active material mixture mainly containing nickel hydroxide is filled in a high porous formed nickel sheet, and after drying the sheet is rolled and cut, thereby making positive electrode plates each of which having a capacity of 8 Ah. On the other hand, on both side of a nickel plated and punched steel sheet is pasted by a paste which is prepared by mixing hydrogen absorbing alloy powder represented by Mm Ni 3.6 Co 0.7 Mn 0.4 Al 0.3 ( Mm: misch metal ) with a binder solution, and after drying the sheet is rolled and cut, thus fabricating negative electrode plates each of which having a capacity of 12 Ah. Each of positive and negative electrode plates is inserted into a bag-shaped separator that is made with PP fiber non-woven cloth. Here, lead tabs have been welded to the positive and negative electrode plates beforehand. A plurality of positive and negative electrode plates each contained in a separator are piled up by turns to form an electrode group 2. Lead tabs 10 for the positive and negative electrodes are welded to nickel-plated steel positive and negative poles 7 and 8, respectively. This electrode group 2 is contained in a rectangular case 3 which is made of plastics containing PP as a main ingredient. The open upper edge portion of the case 3 is bonded with the fitting portion beneath a cover 4 which is made of the same material as the case 3 in a monoblock form by a thermal melting method and the like. In this state, the positive and negative electrode poles 7 and 8 are inserted through the cover 4, thereby being aligned. The mechanical strength of the bonded part 5 has at least 95 % of the strength of the parent material. Here, the strength of the parent material means the tensile strength of plastic form containing PP as a main ingredient. 170 cm3 of an electrolyte is injected via a through-hole provided for a safety valve 9 located on the center portion of the cover 4. The electrolyte used is 40 gram of lithium hydroxide crystal LiOH·H 2 O dissolved in 1.0 litre of 27 % potassium hydroxide aqueous solution. Although a little free electrolyte is noticed in the bottom of the cell immediately after injection, the discharge following the initial charge after the fabrication of the cell allows the electrolyte to be absorbed and immersed into the electrode group 2, the free electrolyte being thereafter not observed. After injection the positive and negative electrode poles 7 and 8 are fixed to the cover 4 in an gas-tight and liquid-tight way. Then, the cover 4 and the safety valve 9 that is made of the same material as the case 3 and the cover 4 are bonded together to form a monoblock by an ultrasonic melting method and the like to complete hermetic seal, a single cell being thus fabricated. Here, the poles 7 and 6 protruding above the cover 4 serves as terminals of the positive and negative electrodes, respectively, too. The safety valve 9 is a resealable type, and its operating pressure is set in the range from 0.20 to 0.78 M Pa (2.0 to 8.0 kgf·cm -2 ). At least one tube 6 having the bottom protruding toward the upper surface of the electrode group 2, located between the safety valve 9 and the positive electrode pole 7 or the negative electrode 8, are formed beneath the cover in a monoblock structure with the cover 4. The tube 6 and the cover 4 may be formed in a monoblock structure by an injection molding, or the open upper edge portions of the tube having the bottom prepared beforehand that are made of the same material as the cover 4 and the lower peripheral portions of pass through holes drilled at specified positions of the cover 4 may be bonded together in a monoblock structure by an ultrasonic method and the like. A thermistor or a thermo-couple is used for a temperature sensor that is to be inserted and fixed in the tube 6. In order to measure temperature variations of the electrode group, the temperature sensitive part of a temperature sensor primarily has to be inserted and fixed in the electrode group that serves as a heat source. However, if a temperature sensor, that is not associated with an electrochemical reaction brought about by charge and discharge and that could be regarded as a foreign substance, is inserted in the electrode group, then it would result in the breakdown of separators or a failure such as an ununiformal charge and discharge reaction. In one embodiment of the present invention, therefore, as shown in Fig. 2, the pointed end of the tube 6 having the bottom is brought as close as possible to the upper edge of the separators that is a little bit higher than the upper edge of the positive and negative electrode plates inside the electrode group 2. Test cells were subject to an initial charge at a constant current of 10 A and 25 °C followed by a discharge at a constant current of 20 A until to 1.0 V, then their standard capacities were measured. The discharge capacity of the test cells is 100 A being limited by the positive electrode capacity. 4 test cells which have been subject to an initial charge followed by a complete discharge were prepared, then the same thermistor was used with different locations and different fixing methods to study difference in temperature variation in the test cells. The 4 test cells incorporating the thermistor are as follows: ( 1 ) Cell A according to the present invention: the thickness of the tube having the bottom is 1.0 mm, and the outer surface of the pointed end of the tube, the inner surface of the pointed end of that the temperature sensitive part is inserted to and fixed on, is put into contact with the upper edge of the separators in the electrode group. ( 2 ) Cell B according to a conventional means: the temperature sensing part is fixed on the outer surface of the case 30 mm from under the bonded part of the case and the cover. ( 3 ) Cell C according to another conventional means: the temperature sensing part is buried in the upper part of the positive electrode pole ( terminal ). ( 4 ) Cell D according to a still another conventional means: adjacent to the tube having the bottom and in the direction to the positive electrode pole, a hole is drilled, and the temperature sensing part is fixed so as to come into contact with the upper edge of the separators in the electrode group, thereafter the pass-through hole is sealed with blown-asphalt. Each cell was subject to charge at a constant current of 10 A for 10 h ( 100 Ah ) at 25 °C. The measurement result of the temperature variation versus charge time is shown in Fig. 3. Fig. 3 shows that both cell A according to the present invention and cell D according to a conventional means exhibit the similar temperature increase curve as is inferred from the fact that the temperature sensing part in both test cells is located almost in the same position. On the contrary, cell C according to a conventional means wherein the temperature sensing part is buried in the upper part of the electrode pole shows a slower temperature increase, presumably resulting from the radiation of heat by the effect of the ambient temperature. Cell B shows a still slower response, as is expected from the low thermal conductivity of the plastic case. After being completely discharged, each cell was charged at a constant current of 10 A and a temperature 0 °C for 10 h. The temperature variation versus charge time is shown in Fig. 4. As in the case of charge at 25 °C, Fig. 4 shows that both cell A according to the present invention and cell D according to a conventional means behave in a similar way, but cell C according to a conventional means exhibits no significant temperature increase. The reason is that the ambient temperature is so low that heat radiates efficiently, therefore it is concluded that fixing the temperature sensing part on the outside of the cell is not appropriate for detecting the temperature increase during charge in a good response. Furthermore, after being completely discharged, each cell was charged at 25 °C and a high rate of 100 A constant current for 0.8 h ( 80 Ah ). The temperature variation of each cell is shown in Fig. 5. Fig. 5 shows that the temperature increase of each cell is faster than in the case of low-rate charge. Cells A and D exhibit the similar curve. The effect of the ambient temperature in cell C as well as the low thermal conductivity of the plastic case in cell B is observed as in Figs. 3 and 4, therefore it can be understood that the conventional means thereby fixing the temperature sensing part on outside the cell is problematical. Cell A according to the present invention and cell D according to an conventional means, which exhibited an almost similar temperature characteristics in the experiments hitherto, were subject to a cycle life test wherein they were repeatedly charged at 25 °C and a constant current of 20 A either for 5.25 h ( 105 Ah ) or until reaching a cell internal pressure of 0.15 M Pa ( 1.53 Kgf cm -2 ) and thereafter discharged at a constant current of 50 A until to 1.0 V. Since the operating pressure of the safety valve was, as described before, fixed in the range from 0.20 to 0.78 M Pa, a cell internal pressure of 0.15 M Pa is decided so as to avoid the situation that the safety valve runs, gas inside the cell disperses and the electrolyte decreases. The cycle life test was continued until the capacity decreased to 60 % of the initial standard capacity of 100 Ah. The capacity and weight variations of each cell as a function of charge- discharge cycle are shown in Fig. 6. Fig. 6 shows that cell A according to the present invention loses weight less than cell D according to a conventional means and its cycle life exceeds 1000 cycles, while cell D according to a conventional means decreases in capacity as it loses weight and its life cycle is only 600 cycles. It is presumed that sealing of the pass-through hole of the cover provided for inserting the thermistor is not perfect in cell D, and for this reason, even though under lower than the operating pressure of the safety valve, gas leaks from the cell and the volume of the electrolyte decreases. In other words, cell A according to the present invention with its simple structure maintains the state of hermetic seal in high reliability and for a long time, thereby prolonging the cycle life. Next, a study was carried concerning the distance, from the pointed end of the tube having the bottom that is formed in a monoblock structure to the cover according to the present invention, to the upper edge of separators in the electrode group. The distance was varied from 0 ( in contact ), 1, 2, through 3 mm, and after being completely discharged, the cells were charged at 25 °C and a constant current of 10 A for 10 h (100 Ah ), and the thicknesses of the tubes were all 1.0 mm. The temperature variation as a function of distance is shown in Fig. 7. Fig. 7 shows that as far as the distances are not longer than 2 mm, their measured values of temperature were almost alike. If the distance is 3 mm, there arises a delay in the measured values of temperature, suggesting a slow response. Therefore it is understood that it is preferable that the pointed end of the tube is positioned within 2 mm from the upper edge of separators in the electrode group or is brought as close as possible to that. The thicknesses of the tubes thus far are all 1.0 mm, but it is essentially preferable that they are kept as thin as possible. However, this thickness should be decided from the standpoint of mechanical strength which affects easy-to-handle in fabrication and easy-to-form of the tube, and more of less 0.5 mm in thickness is practically appropriate. The tube according to the embodiment of the present invention are, as described in detail, formed in a monoblock structure between the safety valve and the electrode poles under the cover and the pointed end of the tube is brought as close as possible to the central upper edge of the electrode group, but the pointed end may be put into direct contact with rigid body such as lead tabs of the positive and negative electrodes because such body by no means leads to breakdown of the separators. There was no significant difference in measured temperature values whether the tube is located between the safety valve and the positive electrode pole or between the safety valve and the negative electrode pole. Analysis by a thermograph method of temperature distribution in the cell during charge and discharge confirmed that there is no significant difference in temperature between the lead tabs of the positive and negative electrodes and the upper edge of the electrode group. Heat generation during charge is caused not by an electrochemical reaction but mainly by Joule' heat of ohmic resistance, and on these measuring locations just described the temperature measurement can be carried out in a reproducible way. According to the present invention, a temperature sensor has to be preferably provided to each cell. If a temperature sensor is to be fixed to a particular cell in a module battery or an assembled battery, it has to be located in a cell in the central position that undergoes less heat radiation. When reaching a specified temperature during charge, a charge current is to be stopped. When exceeding a specific temperature, the cell is to be cooled down by an air or water cooling method, thereby maintaining a good cycle life even in a high rate discharge as in EV and enabling a continuous discharge. A rectangular sealed rechargeable battery based on nickel-metal hydride system was thus far described in detail, but the application of the present invention is not restricted to that battery system, but also includes a sealed rechargeable battery employing a plastic battery container based on, for example, nickel-cadmium system and the like. The present invention can be, furthermore, applied to a cylindrical cell that forms the electrode group in such a way that a piece of positive electrode plate and a piece of negative electrode plate therebetween inserted with a separator are spirally rolled, with the pointed end of the tube having the bottom under the cover being brought as close as possible to the central upper edge of that electrode group that where temperature increases fastest. As above detailed, the present invention provides a long-life sealed rechargeable battery that has a simple structure, maintains the state of hermetic seal for a long time and in high reliability, and facilitates measuring temperature in the cell from the outside in a good response thereby controlling charge and discharge.

Claims: A rechargeable battery comprising a plastics battery container having disposed therein: an electrode group (2) having a first edge and comprising a plurality of alternating positive electrode plates and negative electrode plates, said positive and negative plates each having lead tabs (10) connected to respective positive and negative poles (7,8), a plurality of separators disposed between each of said alternating positive and negative electrode plates and a volume of electrolyte, the battery further being provided with a temperature sensor for sensing an internal temperature of the battery characterised in that the battery is a sealed battery and the container is provided with a safety valve (9), and at least one tube (6) receiving the temperature sensor, the tube (6) having a closed second end which protrudes toward the electrode group (2) such that the closed end contacts the electrode group (2) or such that the distance between the closed end of the tube (6) and the first edge of the electrode group (2) is not larger than 2mm, the temperature sensor having a temperature sensing part in direct contact with the inner surface of the closed end of the tube. A rechargeable battery comprising a plastics battery container according to claim 1, wherein the battery container has a case (3) and a cover (4) made of a polyolefin. A rechargeable battery comprising a plastics battery container according to claim 2, wherein the polyolefin is polyethylene or polypropylene. A rechargeable battery comprising a plastics battery container according to claim 2 or 3, wherein the tube (6) is formed together with the cover (4) in an integral structure. A rechargeable battery comprising a plastics battery container according to claim 2 or 3 wherein the tube (6) is joined to the cover (4) and axially in line with a hole through the cover.

Inventors: HAMADA SHINJI, IKOMA MUNEHISA, INOUE HIROSHI, OKAMOTO MIHO, HAMADA, SHINJI, IKOMA, MUNEHISA, INOUE, HIROSHI, OKAMOTO, MIHO
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1996
Main classification: H01M10
IPC codes: H01M10, H01M2