Process to prepare a blown film of a block copolymer composition

Abstract: The invention provides a process to prepare a blown film (27) of a vinyl aromatic hydrocarbon/conjugated diene block copolymer, comprising the steps of: i) providing a block copolymer composition comprising at least one block of a vinyl aromatic hydrocarbon and at least one block of conjugated block diene; ii) melting the block copolymer composition in an extruder (20); iii) passing the melted block copolymer composition from the extruder through a circular die (23) which comprises a circular outlet (12) and a tapered channel leading to the circular outlet, the circular outlet having an opening width in the range of from 2.28 10 -2 cm to 2.79 10 -2 cm, the taper being a linear taper of at least 2.54 cm length, the center of the linear taper being angled away from the center of the circular outlet at an angle of at least 10 degrees from a line normal to the circular outlet, and the die having a source of gas pressure (13) inside of the circular outlet; and iv) cooling the extruded composition that has been passed through the die with a cooling gas stream.

Description: The present invention relates to a process for preparing a blown film of a vinyl aromatic hydrocarbon/ conjugated diolefin block copolymer composition. Block copolymers of styrene and conjugated diolefins have long been known as useful as elastomeric thermolastics. These block copolymers are referred to as thermoplastic polymers because they may be processed by heating the polymer to above the polymer's melting temperature. Subsequently, the heated polymer may be further processed by such methods as vacuum forming, extrusion, compression molding, calendering or blow molding. These block copolymers have good tear resistance, flexibility, thermochemical stability and other properties. The thermoplastic properties of block copolymers of styrene and conjugated diolefins are the result of incompatibility between the polystyrene and the polyiolefin polymeric blocks which causes separate polymeric phases to exist. At service temperatures, the polydiolefin domains are rubbery and elastic, whereas the polystyrene domains are hard and glassy. The polystyrene domains serve as physical crosslinks between the rubbery polydiolefin blocks. This causes the polymer to behave much like a vulcanized rubber at temperatures that are below the polystyrene glass transition temperature. By heating the block copolymer to a temperature higher than the glass transition temperature of the polystyrene domains, the polymer may be processed as a melt and formed into useful shapes. US-A-4970259 relates to a process for extrusion blowing an elastomeric block copolymer composition into a film. The elastomeric block copolymer is a hydrogenated block copolymer comprising at least two blocks of a vinyl aromatic hydrocarbon and at least one block of conjugated diene. The elastomeric block copolymer is extrusion blown through a conventional die. An outlet opening of about 5 to about 120 mils (about 1.27 10 -2 cm to about 30.48 10 -2 cm) is considered acceptable, an outlet opening of about 10 to about 80 mils (about 2.54 10 -2 cm to about 20.32 10 -2 cm) is preferred and an outlet opening of about 20 to about 40 mils (about 5.08 10 -2 cm to about 10.16 10 -2 cm) is most preferred. Outlet openings of 5.08 10 -2 cm and larger are exemplified. Although US-A-4970259 states the object of blowing a film of 1 to 5 mils (2.54 to 12.7 10 -3 cm), in the examples of D3 only films with a thickness of 3 and 4 mils (7.62 to 10.16 10 -3 cm) are obtained. Blown films of about 2.54 10 -3 cm have not been commercially made from block copolymers of styrene and conjugated diolefins because blown films using typical blown film extruders and dies have resulted in films of about 5.08 10 -3 cm thickness or greater. Films of this thickness can be prepared by other processes that are simpler than blown film technology. It would, however, be desirable to have thinner blown films for many different uses, such as elastic gloves and baby diaper waist bands. Blown films of other materials can be made of 2.54 10 -3 cm thickness or less, but the elastomeric copolymers of block copolymers of styrene and conjugated diolefins have properties that make blown film extrusion very difficult. Previous attempts to blow-extrude films of these copolymers to thicknesses of about 2.54 10 -3 cm have been unsuccessful. It is therefore an objective of the present invention to provide a process to prepare blown films of block copolymers of vinyl aromatic hydrocarbons and conjugated diolefins wherein the blown films have a thickness of less than about 5.08 10 -3 cm. It is further object to provide such a method wherein commercially available blown film extruders can be used without significant modifications. The objectives of the present invention are accomplished by a process for preparing a blown film of a vinyl aromatic hydrocarbon/conjugated diene block copolymer comprising the steps of: i) providing a block copolymer composition comprising at least one block of a vinyl aromatic hydrocarbon and at least one block of a conjugated diene; ii) melting the block copolymer composition in an extruder; iii) passing the melted block copolymer composition from the extruder through a circular die which comprises a circular outlet and a tapered channel leading to the circular outlet, the circular outlet having an opening width in the range of from 2.28 10 -2 cm to 2.79 10 -2 cm, the taper being a linear taper of at least 2.54 cm length, the center of the linear taper being angled away from the center of the circular outlet at an angle of at least 10 degrees from a line normal to the circular outlet, and the die having a source of gas pressure inside of the circular outlet; and iv) cooling the extruded composition that has been passed through the die with a cooling gas stream. Dies with a tapered channel leading to the outlet opening are known from US-A-3223761 and US-A-4021170, relating to the extrusion blowing of polyvinylchloride and the extrusion of polyethylene and polyamide respectively. Such a tapered channel has, however, not been used before for the preparation of elastomeric films. The elastomeric films made according to the present invention can be made with a thickness of between 2.54 10 -3 cm and 5.08 10 -3 cm, which is desirable for many applications of elastomeric films. Previously, extruded films could be made only to thickness greater than 5.08 10 -3 cm, and blown extruded films could not be made less than 5.08 10 -3 cm thickness because of the lack of an appropriate die. With the novel die of the present invention, films of between 2.54 10 -3 cm and 5.08 10 -3 cm thickness can be prepared with excellent consistency and reliability. Thus, the present invention further provides a circular die comprising a circular outlet and a tapered channel leading to the circular outlet, the circular outlet having an opening width in the range of from 2.28 10 -2 to 2.79 10 -2 cm, the taper being a linear taper of at least 2.54 cm length, the center of the linear taper being angled away from the center of the circular outlet at an angle of at least 10 degrees from a line normal to the circular outlet, and the die having a source of gas pressure inside of the circular outlet. Preferably, the center of the linear taper is angled away from the center of the circular outlet at an angle of between 10 degrees and 30 degrees from a line normal to the circular outlet. Preferably, the circular outlet has an opening width in the range of from 2.33 10 -2 cm to 2.59 10 -2 cm. FIG. 1A shows a cross sectional view of a die suitable for use in the present process. FIG. 1B shows a cross sectional view of a die that is not according to the present invention. FIG. 2 shows a cross sectional and schematic view of an apparatus that can be used in accordance with the present invention. The block copolymers used in accordance with the present invention may be linear, branched, coupled or radial because the invention does not depend on any specific geometrical structure, but rather on the chemical constituents of each of the polymer blocks. The radial, or star, block copolymer may be symmetric or asymmetric. The polymer may also be a grafted block copolymer. The only requirement being that the blocks phase separate into aromatic and aliphatic domains and that at least a portion of the aliphatic blocks be surrounded by at least one aromatic block on each end of the aliphatic block. The block copolymer may be produced by any block polymerisation procedure including sequential addition of monomer techniques, incremental addition of monomer techniques, or various coupling techniques. Tapered copolymer techniques may also be used. Useful linear block copolymers include linear block copolymers such as those described in U.S. Patent Nos. 3,321,635; 3,265,765 and 3,322, 856. In general, linear and branched block copolymers include those that may be represented by the general formula: A-(B-A)y-Bx wherein: A is a linear or branched polymeric block comprising predominantly vinyl aromatic hydrocarbon monomer units (referred to as Block A); B is a linear or branched polymeric block containing predominately conjugated diolefin monomer units (referred to as Block B) ; x is equal to 0 or 1; and y is a whole number ranging from 1 to about 20. Radial block copolymers include polymers of the type as described in U.S. Patent Nos. 4,033,888; 4,077,893; 4,141,847; 4,391,949 and 4,444,953. Coupled and radial block copolymers include those that may be represented by the general formula: [B x (A-B) y -A] n -C-P n ' wherein: A, B, x, and y are as defined hereinbefore; n and n' are, independently, numbers from 1 to about 40 such that n + n' is greater than or equal to 3; C is the core of the coupled or radial polymer formed with a polyfunctional coupling agent having two or more functional groups; and each P is the same or a different polymer block or polymer segment having the general formula: B' x' -(A'-B'') y' -A'' wherein: A'' is a polymer block containing predominantly vinyl aromatic hydrocarbon monomer units which may be the same or different from A; B' is a polymer block containing predominantly conjugated diolefin monomer units which may be the same or different from B; A'-B'' is a polymer block containing vinyl aromatic hydrocarbon monomer units (A') and conjugated diolefin monomer units (B''), the A'-B'' monomer units may be random, tapered or block and when each of the A' and B'' is blocked, the A' block may be the same or different from A and B'' may be the same or different from B'; x' is equal to 0 or 1; and y' is a number from 0 to about 20, with the proviso that the sum of x', y' and z' is greater than or equal to 1. Blocks A and B may be either homopolymer, random or tapered copolymer blocks as long as each block predominates in at least one class of the monomers characterizing the block. Thus, blocks A may comprise styrene/alpha-methylstyrene copolymer blocks or styrene/butadiene random or tapered copolymer blocks as long as the blocks individually predominate in vinyl aromatics. The A blocks are preferably vinyl aromatic hydrocarbon homopolymeric blocks. The term "vinyl aromatic hydrocarbon" includes particularly those of the benzene series such as styrene and its analogs and homologs including alpha-methylstyrene and ring alkylated styrenes, particularly ring-methylated styrenes, and other vinyl polycyclic aromatic hydrocarbon compounds such as vinyl naphthalene. The preferred vinyl aromatic hydrocarbons are styrene and alpha-methylstyrene, and styrene is most preferred. The block B may comprise homopolymers of conjugated diene monomers, copolymers of two or more conjugated dienes, and copolymers of one of the dienes with a vinyl aromatics as long as the block B predominates in conjugated diene units. The conjugated dienes are preferably ones containing from 4 to 8 carbon atoms. Examples of suitable such conjugated diene monomers include: butadiene, isoprene, 2,3-dimethyl-1,3-butadiene, and piperylene, preferably butadiene and isoprene. Suitable block copolymers to be used in the process of the present invention comprise two or more vinyl aromatic hydrocarbon blocks separated by at least one conjugated diolefin block. These polymers form "networks" of connected vinyl aromatic domains which result in a composition having significant tensile strength. As used in connection with polymer block composition, "predominantly" means that the specified monomer type shall constitute at least 85 wt% of the total monomer content of that block. Anionic polymerisation methods that may be used to prepare the base block copolymers to be used in accordance with this invention are described in U.S. Patent Nos. 3,252,905; 3,390,207; 3,598,888; 4,219,627; 3,251,905; 3,265,765; 3,639,521; 4,208,356; 3,231,635; 3,322,856; 4,391,949; and 4,444,953. The block copolymers of conjugated dienes and vinyl aromatic hydrocarbons which may be utilized in this invention include polybutadiene block containing copolymers which have a polybutadiene 1,2-microstructure content in the range of from 7% to 100%, preferably in the range of from 25% to 65%, more preferably in the range of from 35% to 55%. These polymers have excellent elasticity due to the microstructure of the polybutadiene blocks. Block copolymers useful in this invention may contain various ratios of conjugated diene to vinyl aromatic hydrocarbon monomer units. The proportion of the vinyl aromatic hydrocarbon monomer units in these block copolymers will preferably be in the range of between 1 to 60 weight percent by weight and more preferably in the range of between 5 to 40 percent by weight. The number average molecular weights of the individual blocks may vary within certain limits. In most instances, the vinyl aromatic hydrocarbon blocks will have number average molecular weights of up to 125,000, and preferably in the range of between 1,000 to 60,000. Conjugated diolefin blocks will preferably have number average molecular weights in the range of from 10,000 to 450,000, and preferably from 10,000 to 150,000. These molecular weights are most accurately determined by gel permeation chromatography and/or low angle light scattering techniques. The block copolymer to be used in accordance with the present invention is preferably, but not necessarily, hydrogenated. Hydrogenation improves thermal, oxidative and U.V. stability of conjugated diolefin containing polymers. Selective hydrogenation refers to hydrogenation of the ethylenic unsaturation while the aromatic saturation remains unhydrogenated, and is preferred. Hydrogenation of the polymer may be accomplished using any of the methods known in the prior art. The hydrogenation will preferably be selective hydrogenation accomplished using a method such as those taught in U.S. Patent Nos. 3,494,942; 3,634,549; 3,670,054; 3,700,633 and Re 27,145. Most preferably, selective hydrogenation will be accomplished using one of the processes taught in U.S. Patent No. 3,700,633. These hydrogenation processes involve the use of a suitable catalyst, particularly a catalyst or catalyst precursor comprising an iron group metal compound. In the methods described in the foregoing patent documents, the catalyst is prepared by combining an iron group metal, particularly a nickel or cobalt compound with a suitable reducing agent such as an aluminium alkyl. The preferred iron group metal compounds are carboxylates and alkoxides. The block copolymer is preferably selectively hydrogenated, thereby converting (hydrogenating) at least 80 percent and most preferably more than 98 percent of the initial ethylenic unsaturation. Preferably, less than 10 percent and most preferably less than 2 percent of the initial aromatic unsaturation is hydrogenated to obtain the maximum benefits of hydrogenation. Preferred block copolymers which have demonstrated utility in the present invention include those with the structure of polystyrene-hydrogenated polybutadiene-polystyrene. Suitability of polymeric compositions for blow extrusion is often determined by use of a Rheotens Melt Strength Tester. This tester is available from Goettfert Inc. of Rock Hill, S.C. A material's melt strength is determined using an apparatus comprising a plunger that forces a melt of the polymer through an orifice, and two rollers that pull a string of the melt that has been forces through the orifice at a rate that stretches the melt. Force required by the rollers to pull the melt is measured and plotted as a function of elongation ratio. The result of the test is a typically a parabolic curve starting at an elongation ration of one, and zero force and increasing force with elongation ratio until the string of the melt breaks. Although this apparatus determines the ability of the melt to stretch in one direction, whereas the blown extrusion process requires biaxial deformation, this test has been found to be a good predictor of the suitability of polymeric materials in a blown extrusion process. For elastomeric polymers such as a vinyl aromatic hydrocarbon/conjugated block copolymer, a high force at break (greater than 4 centiNewtons) generally results in strong bubbles whereas high elongation at break (generally greater than 6) is needed in order for a thin film to be made. Generally, the block copolymer composition of the present invention, at extrusion temperatures, will have a force at break of greater than 0.5 centiNewtons, and an elongation at break of at least 5. The die to be used in the present invention must meet certain criteria for a 2.54 10 -3 cm thickness film to be prepared. A melt of the block copolymer of the present invention is a visco-elastic material, and therefore has a "memory" of recent flow history. The melt will therefore tend to pull back into its previous form. The die therefore must be angled outward and tapered to a final die gap dimension to minimize abrupt shear deformation in the die. It is believed that memory of this shear deformation caused resistance to abrupt biaxial deformation imposed on the melt by bubble formation and therefore instability in the bubble unless a die such as the die shown in FIG. 1A is utilized. Referring now to FIG. 1A and 1B, two dies are shown. The die shown in FIG. 1A can be used in the process of the present invention. The die of FIG. 1B is a conventional die which is not in accordance with the present invention. The conventional die did not function effectively, making bubbles that were unstable, uneven, and that had to be made thicker to avoid failure of the bubble. The dies comprise inserts 10 that are supported by the die bodies 11, forming cavities 12 through which the melt flows. The conventional die has a gap, dimension a, of 0.0625 cm. The die of the present invention has dimension a of 0.0254 cm in order to blow extrude a film of 2.54 10 -3 cm to 5.08 10 -3 cm in final thickness. The cavities 12 through which the melt flows are circular, with the cavity of the die of the present invention being linearly tapered and pointed outward. The angle at which the cavity is pointed outward from vertical (or normal to the circular opening of the die) is at least 10 degrees, and preferably between 10 and 30 degrees. Having the cavity slanted outward in this fashion results in the melt leaving the gap and progressing more linearly as pressure from within the bubble causes the melt to expand. The cavity is tapered to provide a smooth acceleration of the melt as it progresses out the die. These feature have been found to be critical in forming a stable bubble when blow extruding the elastomeric block copolymers of the present invention to thicknesses in the range of from 2.54 10 -3 cm to 5.08 10 -3 cm. The cavity of the standard die has a cylindrical cavity leading to the die, and does not include an angled cavity leading to the gap, nor a tapered cavity leading to the gap. The angled and tapered cavity of the present invention is preferably at least 3.05 cm long. Both the standard die and the die of the present invention include an air ring 14 to direct cooling air at the melt of the block copolymer. The air ring 14 provides a circular opening 15 through which a cooling gas such as air travels. The lower boundary of the cooling gas path is defined by a plate 16. The plate 16 in both figures has a height above the gap, dimension b, of 1.50 cm. The plates 16 differ in their distance from the gap. The elastomeric nature of the block copolymer of the present invention causes a greater expansion above the gap (bubble sagging), and so a greater distance c between the gap and the plate 16 is required in order to prevent the bubble from contacting the plate. Dimension c of FIG. 1A is 2.39 cm whereas dimension c of the die of FIG 1B is 1.32 cm. Angle  of the die useful in the practice of the present invention is therefore 32 degrees or less. This angle allows for expansion of the bubble without contact with the air ring. Within the dies, conduits 13 are provided for supplying pressure to within the bubble to maintain the bubble in an expanded state. The pressure is typically applied by supplying air, but any gas could be used. The dies useful in the practice of the present invention are typically heated dies with at least one thermocouple to provide a control temperature for control of a band heater around the die. The present invention requires stable temperature control to obtain a smooth and uniform film. To ensure that the film does not exhibit rough surface appearance as a result of the relatively small die gap of the present invention the die temperature is preferably maintained at a higher level than the extruder temperature to reduce the melt viscosity and consequently lower the shear stress in the thinner gap. Referring now to FIG. 2, a schematic cutaway view of an extruder-blower useful in the practice of the present invention is shown. An extruder 20 is fed pellets of block copolymer from a hopper 21 into a low pressure feed section 26 from which an screw compresses and heats pellets of the block copolymer into a high pressure section 22, from which a melt of pressurized polymer exits into a die 23. The die defines a flow path for the block copolymer melt to a circular gap of about 10 mils width. Pressurized air is forced through a channel 24 through the die to maintain a bubble of the block copolymer at the outlet of the gap. Air ring 25 provides a stream of cooling air, and directs the stream of cooling air to the melt of block copolymer exiting the die through the gap. Air inlet 30 is in communication with circular chamber 31. The circular chamber 31 contains vertical baffles 32 and 33 to provide for distribution of the air around the circumference of a cooling air opening 34 that directs cooling air at the bubble of melt. Air ring bottom plate 35 contains a lip 36 to direct the cooling air at the bubble at an appropriate height above the die gap. The melt of block copolymer is cooled to become an elastomeric film tube 27 by the cooling gas stream. The tube of elastomeric film is collapsed by rollers 28 and collected on a spool 29. The composition of the present invention may, of course, further comprise additives and components known to be useful in elastomeric block copolymer compositions. These other components include non-reactive homopolymers or copolymers of alpha olefins or aromatics. The amount of non-reactive polymer is 100 parts by weight or less and preferably in the range of from 1 to 50 parts by weight. Fillers, reinforcing materials such as silica, carbon black, glass fibers, organic fibers, calcium carbonate and the like, lubricants, pigments, extender oils, stabilized inhibitors of oxidative, thermal and ultraviolet light degradation, antioxidants, flame retardants, mold release agents and/or crosslinking agents, colorants including dyes and pigments and nucleating agents may also be included. Example Two compositions of block copolymers of styrene and butadiene were blow extruded to films having thicknesses of less than 5.08 10 -3 cm using a die such as that shown in FIG. 1A having a outer diameter of the gap of 5.18 cm. Composition A included 40 parts by weight of a styrene-hydrogenated butadiene-styrene triblock copolymer having a number average molecular weight of 52,000 and 30 percent by weight of styrene and 60 parts by weight of a styrene-hydrogenated butadiene-styrene triblock copolymer having a number average molecular weight of 70,000 and 29 percent by weight of styrene along with components listed below in Table 1. The hydrogenated mid-blocks were than 98% hydrogenated. COMPOSITION A parts weight/100 parts block copolymer component/source 45 PENRECO 4434 (Penzoil) paraffinic extending oil 20 PICOLASTIC D-150 (Hercules) low m. wt. polystyrene 1 IRGANOX 1010 (Ciba Geigy) antioxidant 0.5 DLDTP (Cytech Industries) antioxidant Composition B was prepared using 150 parts by weight of a compound of a styrene-butadiene-styrene triblock copolymer having a number average molecular weight of 111,000 and 30 percent by weight of styrene. This polymer compound is provided with 50 parts weight based on 150 parts by weight of the copolymer compound of plasticizer oil. Table 2 below lists the other components of Composition B. COMPOSITION B parts weight/100 parts block copolymer component/source 7 PENRECO 4434 (Penzoil) paraffinic extending oil 21 DP-210 (Huntsman Chemical) polystyrene 25 ELVAX 250 (DuPont) polyethyl vinyl acetate 20 ATTANE 4601 (Dow Chemicals) linear low density polyethylene 0.4 IRGANOX 1010 (Ciba Geigy) antioxidant 0.6 DLDTP (Cytech Industries) antioxidant Blown films were prepared from the two block copolymer compositions using a 1¼" Brabender extruder, along with a die assembly, air ring, and a take-up device, all attached to a frame. For comparison, and to demonstrate that thinner films have acceptable properties, films of composition A were prepared with 1.016 10 -2 cm thickness, and 3.81 10 -3 cm thickness. The only difference between the apparatuses of the two runs was that a gap of 5.08 10 -3 cm was used to prepare the 1.016 10 -2 cm film, whereas a die having a gap of 2.54 10 -2 cm was used to prepare the 3.81 10 -3 cm thickness film. Operating conditions and film properties are summarized in TABLE 3 shown below. Thick Film Thin Film OPERATING CONDITIONS Melt Temp °C 260 260 Thickness, cm 1,016 10 -2 3.81 10 -3 Layflat width, cm 16.51 17.78 RPM 42 40 Feet/Minute 12 19 PROPERTIES Tb @MD, psi 2189 1990 Tb @TD, psi 1904 1961 Eb @MD, % 730.6 676.0 Eb @TD, % 695.2 621.4 100% Modulus @MD, psi 134.7 153.4 100% Modulus @TD, psi 153.7 154.1 SR60, % 7.3 10.3 In Table 3, Tb is tensile stress at break; Eb is ultimate elongation, MD is machine direction, TD is transverse direction, and SR60 is the stress relaxation with 150% strain. Results of this example demonstrate that films of about 2.54 10 -3 cm thickness can be prepared, and when compared to thicker films, these low thickness films do not exhibit significantly impaired physical properties.

Claims: A process for preparing a blown film of thickness of less than about 5.08 10 -3 cm from a block copolymer composition comprising the steps of: i) providing a block copolymer composition comprising at least one block of a vinyl aromatic hydrocarbon and at least one block of a conjugated diene; ii) melting the block copolymer composition in an extruder (20); iii) passing the melted block copolymer composition from the extruder (20) through a die(23); and iv) cooling the extruded composition that has been passed through the die (23) with a cooling gas stream, characterized in that the die (23) is a circular die which comprises a circular outlet and a tapered channel (12) leading to the circular outlet, the circular outlet having an opening width in the range of from 2.28 10 -2 cm to 2.79 10 -2 cm, the taper being a linear taper of at least 2.54 cm length, the center of the linear taper being angled away from the center of the circular outlet at an angle (α) of at least 10 degrees from a line normal to the circular outlet, and the die (23) having a source of gas pressure inside of the circular outlet. A process according to claim 1 wherein the cooling gas stream is directed at the extruded composition from an opening (15) that is below a 35 degree angle from the circular outlet relative to the plane of the circular outlet. A process according to claim 1 or 2, wherein the block copolymer composition is a hydrogenated block copolymer composition. A process according to any one of claims 1 to 3, wherein the vinyl aromatic hydrocarbon is styrene and the conjugated diene is selected from the group consisting of butadiene, isoprene and a combination thereof. A process according to any one of claims 1 to 4, wherein the center of the linear taper is angled away from the center of the circular outlet at an angle in the range of between 10 and 30 degrees from a line normal to the circular outlet. A circular die for preparing a blown film of thickness of less than about 5.08 10 -3 cm from a block copolymer composition, which comprises a circular outlet and a tapered channel (12) leading to the circular outlet, and having a source of gas pressure inside of the circular outlet, characterized in the circular outlet having an opening width in the range of from 2.28 10 -2 cm to 2.79 10 -2 cm, the taper being a linear taper of at least 2.54 cm length, and the center of the linear taper being angled away from the center of the circular outlet at an angle (α) of at least 10 degrees from a line normal to the circular outlet.

Inventors: RASTOGI AMIT, YANG BING, RASTOGI, AMIT, YANG, BING
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1996
Main classification: B29C47
IPC codes: B29C47