Use of biodegradable pour point depressants for industrial fluids derived from biodegradable base oil

Abstract: A process of depressing the pour point of an industrial fluid comprising at least one triglyceride, or improving the biodegradability or oxidation stability or hydrolytic stability of an industrial fluid comprising at leas one vegetable oil which process comprises adding to the industrial fluid as a pour point depressant one or more biodegradable polyalpha olefins.

Description: The present invention relates to the use of biodegradable polyalpha olefins as pour point depressants for industrial fluids comprising at least one triglyceride, including but not limited to natural or synthetic triglycerides or their esters. Preferred vegetable oils are rapeseed oil, soybean oil, and canola oil. Unfortunately, oils, hydraulic fluids, and other petroleum-based products almost inevitably leak onto pavement or other ground surfaces, eventually resulting in contamination of the environment. Much effort has been directed to avoiding such contamination. Since total containment of petroleum-based products may not be possible, efforts recently have focused on altering petroleum products to render those products less toxic to the environment. One promising approach has been to replace the base fluid--typically, a petroleum-derived hydrocarbon-- with a vegetable oil, such as a naturally occurring or synthetic triglyceride or ester thereof. Vegetable oils are biodegradable, and thus environmentally friendly. Unfortunately, triglycerides have poor low temperature viscometrics, and tend to congeal at temperatures below about -10°C (14°F). Many industrial fluids must have a pour point of less than -25°C (-13°F) and a Brookfield viscosity of 7500 to 110,000 centiPoise (cP) at -25°C (-13°F). In order for triglycerides to be used successfully as industrial base fluids, their low temperature viscometry must be improved. A number of compounds are known to improve the low temperature viscometrics of vegetable oils. These compounds are known as "pour point depressants" (PPD's). Known PPD's for triglycerides include, but are not limited to: modified carboxy containing interpolymers; acrylate polymers; nitrogen containing acrylate polymers; and methylene linked aromatic compounds. Unfortunately, known PPDs are not biodegradable. Therefore, the advantage in low temperature viscometry that is gained by using these PPD's is largely offset by the decrease in biodegradability of the resulting product. Also, manufacturing and environmental specifications limit the total amount of non-biodegradable material that can be used in a particular industrial fluid. WO 95/06700 discloses an extreme pressure industrial gear lubricant containing specific polyalphaolefins. WO 95/06700 teaches that the amount of polyalphaolefin in the composition can range from 20% by weight to 90% by weight. Biodegradable PPDs, which would meet the applicable specifications and not compromise the overall biodegradability of industrial fluids, are sorely needed. The invention involves the use of biodegradable polyalphaolefins ("PAOs") to treat biodegradable industrial fluids, such as lubricants, hydraulic fluids, fuel oils, and the like, to reduce their pour point. Accordingly, the present invention provides the use of a biodegradable polyalphaolefin comprising oligomerization and hydrogenation products of 1-alkenes having between 8 and 12 carbon atoms and having a kinematic viscosity of 1 to 3 centistokes for depressing the pour point of an industrial fluid comprising at least one triglyceride. A preferred industrial fluid is mixture of vegetable oil and branched alkane where the average molecular weight of the alkane is about 200-400, and the alkane additionally has a sufficient degree of branching to have a pour point of about -25°C or lower. Typical vegetable oils that may be used in the present invention include castor oil, olive oil, peanut oil, rapeseed oil, corn oil, sesame oil, cottonseed oil, soybean oil, canola oil, sunflower oil, safflower oil, hemp oil, linseed oil, tung oil, citicica oil, jojoba oil, meadowfoam oil, and the like. Such oils may be partially or fully hydrogenated, if desired. Suitable synthetic oils comprise the esters of dicarboxylic acids ( e.g ., phthalic acid, succinic acid, maleic acid, azelaic acid, suberic acid, sebacic acid, fumaric acid, adipic acid, mellitic acid, linoleic acid dimer) with a variety of alcohols ( e.g., butyl alcohol, hexyl alcohol, dodecyl alcohol, 2-ethylhexyl alcohol, ethylene glycol). Specific examples of these esters include dibutyl adipate, di(2-ethylhexyl) adipate, didodecyl adipate, di(tridecyl) adipate, di(triisodecyl) adipate, di(2-ethylhexyl) sebacate, dilauryl sebacate, di-n-hexyl fumarate, dioctyl sebacate, diisooctyl azelate, diisodecyl azelate, dioctyl phthalate, didecyl phthalate, di(eicosyl) sebacate, and 2-ethylhexyl diester of linoleic acid dimer, the mixed nonyl/undecyl ester of phthalic acid, and the complex ester formed by reacting one mole of sebacic acid with two moles of tetraethylene glycol and two moles of 2-ethylhexanoic acid. Other esters which may be used include those made from C 3 -C 18 monocarboxylic acids and polyols and polyol ethers such as neopentyl glycol, trimethylolpropane, pentaerythritol and dipentaerythritol. Trimethylolpropane tripelargonate, trimethylolpropane trinonanoate, pentaerythritol tetracaproate, the ester formed from trimethylolpropane and a mixture of octanoic and decanoic acids, the ester formed from trimethylolpropane, caprylic acid and sebacic acid, and the polyesters derived from a C 4 -C 14 dicarboxylic acid and one or more aliphatic dihydric C 3 -C 12 alcohols such as derived from azelaic acid or sebacic acid and 2,2,4-trimethyl-1, 6-hexanediol, serve as examples. Preferred forms of these oils are high oleic forms, such as high oleic rapeseed oil, high oleic safflower oil, high oleic corn oil, high oleic sunflower oil, high oleic soybean oil, high oleic cottonseed oil, and high oleic palm olein. A preferred vegetable oil is high oleic rapeseed oil, which may be obtained from a number of sources. The rapeseed. oil used herein was "RISSO FOR CHEFS," and may be obtained form Van de Moortele, in either Oudenbosch, Holland, or Ghent, Belgium. Typically, therefore, the triglyceride comprises rapeseed oil. As used herein, the term "triglyceride" shall refer to a naturally occurring and synthetic biodegradable triglyceride or an ester thereof. Triglycerides that are useful in the present invention generally have the following formula: wherein R 1 , R 2 , and R 3 are independently selected from aliphatic hydrocarbyl groups preferably having at least 60 percent monounsaturated character and containing from about 6 to about 24 carbon atoms. As used herein, the term "hydrocarbyl group" denotes a radical having a carbon atom directly attached to the remainder of the molecule, and includes: (1) aliphatic hydrocarbon groups: alkyl groups, such as heptyl, nonyl, undecyl, tridecyl, and heptadecyl groups; alkenyl groups containing a single double bond, such as heptenyl, nonenyl, undecenyl, tridecenyl, heptadecenyl, heneicosenyl groups; and, alkenyl groups containing 2 or 3 double bonds, such as 8,11-heptadecadienyl and 8,11,14-heptadecatrienyl groups. All isomers of the foregoing are acceptable, but straight chain groups are preferred; (2) Substituted aliphatic hydrocarbon groups: groups containing non-hydrocarbon substituents which, in the context of the present invention, do not alter the predominantly hydrocarbon character of the group. Persons skilled in the art will be aware of suitable substituents, examples being hydroxy, carbalkoxy (especially lower carbalkoxy), and alkoxy (especially lower alkoxy) groups, the term "lower" denoting groups containing not more than 7 carbon atoms; (3) Hetero groups: groups which, while predominantly aliphatic hydrocarbon in character in the context of this invention, contain atoms other than carbon present in a chain or ring otherwise composed of aliphatic carbon atoms. Suitable hetero atoms will be apparent to those skilled in the art and include, for example, oxygen, nitrogen, and sulfur. Regardless of the source of the triglyceride, the fatty acid moieties preferably should be such that the triglyceride has a monounsaturated character of at least 60 percent, preferably at least 70 percent, and most preferably at least 80 percent. For example, a triglyceride comprising exclusively an oleic acid moiety has an oleic acid content of 100% and consequently a monounsaturated content of 100%. Where the triglyceride is made up of acid moieties that are 70% oleic acid, 10% stearic acid, 5% palmitic acid, 7% linoleic acid, and 8% hexadecanoic acid, the monounsaturated content is 78%. Preferably, the monounsaturated character is derived from an oleyl radical, i.e., is the residue of oleic acid. Preferred triglycerides are high oleic acid (at least 60 percent) triglyceride oils. Polyalphaolefins are known to have high oxidation and hydrolytic stability; therefore, to the extent that the PAO is present in the vegetable oil, the PAO also should increase the oxidation and hydrolytic stability performance of the vegetable oil. PAO's that are biodegradable are formed by (a) oligomerization of 1-alkene hydrocarbons having between 8 and 12 carbon atoms, and (b) hydrogenation of the resultant oligomer. Preferably, the polyalphaolefin comprises branched alkanes with an average molecular weight of 200 to 400 and a sufficient degree of branching to reduce the pour point of the industrial fluid to -25°C or lower. By "biodegradable" is meant that the PAO in question has a biodegradability when tested and reported in accordance with the well known test method CEC L-33-T-82 of at least 20%, preferably at least 30%, and more preferably at least 40%. Not all hydrogenated 1-alkene hydrocarbon liquid oligomers are "biodegradable." To verify that a particular PAO is biodegradable, recourse should be had to the CEC L-33-T-82 test procedure to determine the % biodegradability of the oligomer under consideration. Some unhydrogenated or partially unsaturated forms of PAO may possess the desired biodegradability. Generally, the polyalphaolefin comprises hydrogenated liquid oligomers of linear 1-alkenes containing at least 50% dimer, trimer, and/or tetramer species of the oligomers. Such oligomers can be formed using a water or alcohol promoted Friedel-Crafts catalyst. They tend to possess the requisite biodegradability, and thus are preferred. Particularly preferred polyalphaolefins are those comprising hydrogenated liquid oligomers of linear 1-alkenes comprising at least 80 or 90% dimer and/or codimer species of the oligomers. Such 1-alkenes should be linear (i.e., substantially free of branching and cyclization). Typically, the polyalphaolefin comprises oligomerization and hydrogenation products of 1-decene having a kinematic viscosity of 2 centistokes. Methods for producing substantially biodegradable polyalphaolefins are known, and reported in the literature. Examples are U.S. Patent Nos. 3,763,244; 3,780,128, 4,172,855 and 4,218,330, incorporated herein by reference. Additionally, PAO's are available commercially, for example, Ethyl Petroleum Additives, Inc. as HITEC® 162, HITEC® 164, HITEC® 166 AND HITEC® 168. Preferred PAO's are 1-decene oligomers having a high ratio of dimer content, as opposed to trimer or tetramer content. A most preferred PAO is a 2 centistoke polyalpha olefin available from Ethyl Petroleum Additives, Inc. under the trademark HITEC® 162. Suitable PAO's also may be available from other suppliers. The preferred hydrogenated oligomers of this type have little, if any, residual ethylenic unsaturation. Preferred oligomers are formed using (a) a Friedel-Crafts catalyst (especially boron trifluoride promoted with water or a C 1-20 alkanol), followed by (b) catalytic hydrogenation of the resulting oligomer using procedures such as those described in the foregoing U.S. Patents. Other suitable catalyst systems include Zeigler catalysts, such as ethyl aluminum sesquichloride with titanium tetrachloride, aluminum alkyl catalysts, chromium oxide catalysts on silica or alumina supports, and a system in which a boron trifluoride catalyst oligomerization is followed by treatment with an organic peroxide. Mixtures or blends of PAOs also can be used as a pour point depressant in the present invention, provided that the overall blend possesses the requisite biodegradability. The PAO's of the present invention preferably should be used without adding other, non-biodegradable pour point depressants to the triglyceride. The PAO may be added in any desired quantity. In most applications, the PAO--alone--would be a functional industrial fluid. However, vegetable oils such as rapeseed oil are much less expensive than PAO's. Therefore, it is desirable to minimize the amount of PAO that is used in the industrial fluid. In order to adequately suppress the pour point of a triglyceride-based fluid, the PAO preferably should be added in a range of about 12 - 20 wt%, most preferably 15 wt%. Other well known additives also may be added to the base fluid, provided that these additives are miscible with the vegetable oil and the PAO, and do not substantially interfere with the biodegradability of the overall composition. Such additives include wear inhibitors, detergents, viscosity index improvers,. friction modifiers, fuel economy additives, antioxidants or thermal stabilizers, dispersants, extreme pressure agents, tackiness additives, rust inhibitors, wax modifiers, foam inhibitors, copper passivators, sulfur scavengers, seal swell agents, color stabilizers, and like materials. Where such additives are used, the PAO may be included in the additive, for example, as a biodegradable processing oil. The invention will be more clearly understood with reference to the following examples: Example 1 In this example, "RISSO FOR CHEFS" rapeseed oil, obtained form Van de Moortele, was mixed with 15% by weight HITEC® 162, obtained from Ethyl Petroleum Additives, Inc.. The mixture was stirred and heated to about 50°C (122°F), and the pour point was determined using the Institute of Petroleum test method IP-15. The results, which demonstrate the operability of the invention, are shown in Table I: COMPONENT % (wt) % (wt) % (wt) % (wt) % (wt) % (wt) H162 - 1.0 2.0 5.0 10.0 15.0 Rapeseed oil 100.0 99.0 98.0 95.0 90.0 85.0 Pour point (°C/°F) -21°C/-5.8°F -21°C/-5.8°F -21°C/-5.8°F -21°C/-5.8°F -24°C/-11.2°F -36°C/-32.8°F Example 2 In the following experiment, the same procedures as given in Example 1 were used with the same PAO and the same triglyceride; however, a second, non-biodegradable pour point depressant also was added. The non-biodegradable PPD was HITEC® 623 ("H623"), a polymethacrylate product obtained from Ethyl Petroleum Additives, Inc. The results, which demonstrate a correlation between pour point and the amount of PAO added, are given in Table II: COMPONENT % (wt) % (wt) % (wt) % (wt) H162 2.0 5.0 10.0 15.0 Rapeseed oil 97.0 94.0 89.0 84.0 H623 1.0 1.0 1.0 1.0 Pour Point °C/°F -33°C/-27.4°F -33°C/-27.4°F -36°C/-32.8°F -36°C/-32.8°F Example 3 The procedures of Example 1 were followed to test the PAO alone, and in combination with several different non-biodegradable PPDs, including HITEC® 623, tested in Example 2, and HITEC® 672, a styrene acrylate obtained from Ethyl Petroleum Additives, Inc. The comparative results are shown in Table III: COMPARISON COMPARISON COMPARISON COMPARISON INVENTION Component % (wt) % (wt) % (wt) % (wt) % (wt) H162 - - - 2.0 15.0 H672 - - 1.0 1.0 - H623 - 1.0 - - - Rapeseed oil 100 99.0 99.0 97.0 85.0 Pour Point °C/°F -21°C/-5.8°F -30°C/-22°F -33°C/-27.4°F -33°C/-27.4°F -36°C/-32.8°F The foregoing results demonstrate that non-biodegradable PPD's, alone, lowered the pour point of rapeseed oil, and that the addition of PAO in association with these non-biodegradable PPDs did not alter the pour point further. However, as also seen in Examples 1 and 2, the use of larger amounts of PAO, alone, lowered the pour point as effectively as the non-biodegradable PPDs, alone. In this manner, the methods and compositions of the present invention can be used to treat biodegradable industrial fluids, such as lubricants, hydraulic fluids, fuel oils, and the like, to: (a) reduce their pour point; (b) improve their oxidation stability performance; and/or, (c) improve their hydrolytic stability performance.

Claims: Use of a biodegradable polyalphaolefin comprising oligomerization and hydrogenation products of alkenes having between 8 to 12 carbon atoms and having a kinematic viscosity of 1 to 3 centistokes for depressing the pour point of an industrial fluid comprising at least one triglyceride. Use according to claim 1 wherein the polyalphaolefin is present in an amount of 12 to 20% by wt of the industrial fluid. Use according to claim 1 or claim 2 wherein the polyalphaolefin comprises hydrogenated liquid oligomers of linear 1-alkenes comprising at least 50% dimer, trimer, and tetramer species of the oligomers. Use according to any one of claims 1 to 3 wherein the polyalphaolefin comprises hydrogenation liquid oligomers of linear 1-alkenes comprising at least 80% diner and codimer species of the oligomers. Use according to any one of claims 1 to 4 wherein the polyalphaolefin comprises oligomerization and hydrogenation products of 1-decene having a kinematic viscosity of 2 centistokes. Use according to any one of claims 1 to 5 wherein the triglyceride has at least 60 percent monounsaturated character. Use according to any one of claims 1 to 6 wherein the triglyceride comprises rapeseed oil. Use according to any one of claims 1 to 7 wherein the polyalphaolefin comprises branched alkanes with an average molecular weight of 200 to 400 and a sufficient degree of branching to reduce the pour point of the industrial fluid to -25°C or lower.

Inventors: MACPHERSON IAN, MACPHERSON, IAN
Applicants: ETHYL CORP, ETHYL CORPORATION
Application year: 1996
Main classification: C10M169
IPC codes: C10L1, C10M169, C10M111