Inhibition of unsaturated monomers with 7-aryl quinone methides

Abstract: Ethylenically unsaturated monomers are protected from premature polymerization during manufacture and storage by the incorporation therein of an effective stabilizing amount of a 7-aryl quinone methide compound.

Description: The present invention relates to a compositions and a process for reducing premature polymerization of readily polymerizable unsaturated monomers during monomer manufacturing processes by incorporating therein an effective amount of a 7-aryl quinone methide compound. It is well known that ethylenically unsaturated monomers like vinyl aromatic compounds, such as styrene, α-methylstyrene, vinyltoluene or divinylbenzene or acrylic monomers, such as acrylic acid, methacrylic acid and their esters and amides, or unsaturated esters such as vinyl acetate or unsaturated polyesters have a strong tendency to polymerize when subjected to elevated temperatures. Manufacturing processes for such monomers typically include distillations or handling at elevated temperatures. To prevent the premature polymerization of vinyl aromatic monomers during the distillation purification process, various compounds have been disclosed as polymerization inhibitors. These include elemental sulfur and many classes of organic chemicals having varying degrees of success in industrial use. These compounds include among others nitrated phenol derivatives, C- and N-nitroso compounds, nitroxyl derivatives, diphenylamines, hydroxylamines, quinones, quinone oximes and quinone alkide derivatives. Known inhibitors of acrylic monomer polymerization include phenothiazine, hydroquinone monomethyl ether, and methylene blue. Phenothiazine, while unable to totally inhibit polymerization of acrylic monomers, is a commonly used co-additive. Recent patents claim phenylenediamines with soluble transition metal salts (U.S. 5,221,764) and aryl N-nitroso compounds (EP 0 522 709 A2) are active in acrylic monomer stabilization. However, there still remains a need for a compound to improve the stability of acrylic monomers during their distillation. The need exists for a stable polymerization inhibitor system which will effectively and safely prevent the premature polymerization of unsaturated monomers during distillation and purification processes, particularly if air is absent. United States Patent Nos. 4,003,800 and 4,040,911 disclose the use of quinone alkides in a styrene purification process. United States Patent No. 4,032,547 describes the preparation of quinone methides from phenols by a persulfate oxidation process mediated by ferricyanide. In the generic structure depicted above, groups A 4 and A 5 include phenyl and substituted phenyl, but such structures are not exemplified in U.S. 4,003,800 nor is any 7-aryl quinone methide derivative included among the 17 individually named compounds in U.S. 4,003,800. All 17 compounds have either no substituents or an alkyl substituent in the 7-position. The individually named compounds in U.S. 4,003,800 include six with unsubstituted 7-methylene groups, which are clearly too thermally unstable for practical use as industrial polymerization inhibitors in unsaturated monomers. In Kinet. Katal 1979, 20(1), 48-55 (CA, 1979, 90: 186075q) methylenquinones are described, particularly 4-benzylidene-2,6-di-.tert.-butyl-cyclohexa-2,5-dienone, as inhibitors of the liquid-phase oxidation of hydrocarbons. There is much convincing experimental evidence proving that quinone methides unsubstituted in the 7-position, i.e. compounds with an unsubstituted exomethylene group, are in fact too unstable to be even isolated at room temperature. These methylene derivatives can be prepared only as a very dilute 10-3 to 10-5 molar solutions which are stable only few days in the absence of light (See, e.g., P. Gruenanger in Houben-Weyl, Methoden der Organischen Chemie, Vol. 7/3B, p. 420). Quinone methides with 7-alkyl groups also lack thermal stability to be used efficiently in the present application. Surprisingly, quinone methides with 7-aryl substituents have now been found to be much more thermally stable than 7-alkyl derivatives. One object of this invention is to provide a composition protected from premature polymerization and a process for inhibiting the premature polymerization of ethylenically unsaturated monomers during the distillation and purification steps by incorporating therein at least one 7-aryl quinone methide derivative alone or in combination with another inhibitor. A further object of this invention is to provide new and novel 7-aryl quinone methide compounds suitable as stabilizers for the instant process and compositions. The instant invention is directed to the inhibition of the premature polymerization of an ethylenically unsaturated monomer. It therefore pertains to a stabilized monomer composition which comprises (a) an ethylenically unsaturated monomer or mixture of monomers, and (b) a compound of formula I wherein R 1 and R 2 are independently alkyl of 4 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms or phenylalkyl of 7 to 15 carbon atoms, and R 3 is 2-, 3- or 4-pyridyl, 2- or 3-thienyl, 2- or 3-pyrryl, 2- or 3-furyl, aryl of 6 to 10 carbon atoms, or said aryl substituted by one to three alkyl of 1 to 8 carbon atoms, alkoxy of 1 to 8 carbon atoms, alkylthio of 1 to 8 carbon atoms, alkylamino of 1 to 8 carbon atoms, dialkylamino of 2 to 8 carbon atoms, alkoxycarbonyl of 2 to 8 carbon atoms, hydroxy, nitro, amino, cyano, carboxy, aminocarbonyl, chloro or mixtures of said substituents, with the proviso that R 3 is not phenyl if R 1 and R 2 are tert.-butyl. Alkyl of 4 to 18 carbon atoms is linear or branched and means, for example, n-, sec-, iso- or tert-butyl, n-, sec- iso- or tert-pentyl (amyl), hexyl, heptyl, octyl, tert-octyl, 2-ethylhexyl, nonyl, decyl, dodecyl, pentadecyl, hexadecyl or octadecyl. Alkyl of 1 to 8 carbon atoms is linear or branched and is, for example, methyl, ethyl, n- or iso-propyl,n-, sec-, iso- or tert-butyl, n-, sec- iso- or tert-pentyl (amyl), hexyl, heptyl, octyl, tert-octyl or 2-ethylhexyl. Tert-octyl is, for example, 1,1-dimethylhexyl, 2,2-dimethylhexyl, 3,3-dimethylhexyl, 4,4-dimethylhexyl, 5,5-dimethylhexyl, 1-ethyl-1-methylpentyl, 2-ethyl-2-methylpentyl, 3-ethyl-3-methylpentyl, 4-ethyl-4-methylpentyl, 1,1-diethylbutyl, 2,2-diethylbutyl, 3,3-diethylbutyl, 1-methyl-1-propylbutyl, 2-methyl-2-propylbutyl, 3-methyl-3-propylbutyl or 1,1-dipropylethyl. Cycloalkyl of 5 to 12 carbon atoms is, for example, cyclopentyl, cyclohexyl, cycloheptyl, cycloocytl, cyclodecyl or cyclododecyl, preferably cyclopentyl and cyclohexyl, especially cyclohexyl. Phenylalkyl of 7 to 15 carbon atoms is linear or branched in the alkyl-moiety and means, for example, benzyl, phenylethyl, α-methylbenzyl, 3-phenylpropyl, phenyl-2-methylethyl, phenyl-1-methylethyl, α,α-dimethylbenzyl, butylphenyl, hexylphenyl, octylphenyl or nonylphenyl, preferably benyzl, α-methylbenzyl or α,α-dimethylbenzyl, especially α-methylbenzyl or α,α-dimethylbenzyl. Aryl of 6 to 10 carbon atoms is phenyl or naphthyl, preferably phenyl. Aryl of 6 to 10 carbon atoms substituted one to three times is, for example, phenyl substituted in the 2-, 3-, 4-, 5-, 6- 2,6-, 2,4-, 2,5-, 3,5-, 2,4,6- or 2,3,6-position. Examples are tolyl, xylyl, ethylphenyl,propylphenyl, butylphenyl, dibutylphenyl, di-tert-butylphenyl, phenol, methoxyphenyl, cyanophenyl, dimethylaminobenzyl or dihydroxyphenyl. Alkoxy of 1 to 8 carbon atoms is linear or branched and is, for example, methoxy, ethoxy, n- or isopropoxy, n-, sec-, iso- or tert-butoxy, n-, sec- iso- or tert-pentoxy, hexyloxy, heptyloxy, octyloxy or 2-ethylhexyloxy. Alkylthio of 1 to 8 carbon atoms is linear or branched and is, for example, methylthio, ethylthio, n- or isopropylhtio, n-, sec-, iso- or tert-butylthio, n-, sec- iso- or tert-pentylthio, hexylthio, heptylthio or octylthio. Alkylamino of 1 to 8 carbon atoms is linear or branched in the alkyl moiety an is, for example, methylamino, ethylamino, propylamino, isopropylamino, butylamino, hexalymino or octylamino. Dialkylamino of 2 to 8 carbon atoms is linear or branched in the alkyl moiety, carries two identical or different alkyl groups and is, for example, dimethylamino, diethylamino, dipropylamino, dibutylamino, methylethylamino or methylbutylamino. Alkoxycarbonyl of 2 to 8 carbon atoms is linear or branched and is, for example, methoxycarbonyl, ethoxycarbonyl, n- or isopropoxycarbonyl, n-, sec-, iso- or tert-butoxycarbonyl, n-, sec- iso- or tert-pentoxycarbonyl, hexyloxycarbonyl or heptyloxycarbonyl. Preferably, in the compound of formula I, R 1 and R 2 are the same. Preferably, R 1 and R 2 are tert-butyl, tert-amyl, tert-octyl, cycloalkyl, α-methylbenzyl or α,α-dimethylbenzyl; most preferably R 1 and R 2 are tert-butyl, tert-amyl or tert-octyl. Preferably, in the compound of formula I, R 3 is phenyl or phenyl substituted by nitro, cyano, dimethylamino, methoxy, alkyl of 1 to 4 carbon atoms, hydroxy or mixtures of said substituents; most preferably R 3 is phenyl. The monomer of the instant invention is an aromatic vinyl compound or an acrylic monomer. The amount of the compound of formula I is from 1 to 2000 ppm, preferably at least 100 ppm, most preferably from 100 to 500 ppm, based on the weight of the monomer. Some preferred compounds of formula I are 2,6-di-tert-butyl-4-benzylidene-cyclohexa-2,5-dienone, 2,6-di-tert-butyl-4-(4-nitrobenzylidehe)-cyclohexa-2,5-dienone, 2,6-di-tert-butyl-4-(3-nitrobenzylidene)-cyclohexa-2,5-dienone, 2,6-di-tert-butyl-4-(4-cyanobenzylidene)-cyclohexa-2,5-dienone, 2,6-di-tert-butyl-4-(4-dimethylaminobenzylidene)-cyclohexa-2,5-dienone, 2,6-di-tert-amyl-4-benzylidene-cyclohexa-2,5-dienone, 2,6-di-tert-butyl-4-(4-methoxybenzylidene)-cyclohexa-2,5-dienone, and 2,6-di-tert-butyl-4-(3,5-di-tert-butyl-4-hydroxybenzylidene)-cyclohexa-2,5-dienone; It is emphasized that the instant compounds of formula I differ significantly from the structurally related compounds of United States Patent No. 4,003,800 in that the instant compounds are thermally stable and the compounds of U.S. 4,003,800 are not. The thermal stability of the instant compounds allows them to be used practically as polymerization inhibitors unlike the compounds of the prior art. The instant invention also pertains to a process for inhibiting the premature polymerization of an ethylenically unsaturated monomer which comprises adding thereto a compound of formula I. The instant invention especially pertains to a stabilized monomer composition which comprises (a) an ethylenically unsaturated monomer or mixture of monomers, and (b) a mixture of (i) at least one compound of formula I wherein R 1 and R 2 are independently alkyl of 4 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms or phenylalkyl of 7 to 15 carbon atoms, and R 3 is 2-, 3- or 4-pyridyl, 2- or 3-thienyl, 2- or 3-pyrryl, 2- or 3-furyl, aryl of 6 to 10 carbon atoms, or said aryl substituted by one to three alkyl of 1 to 8 carbon atoms, alkoxy of 1 to 8 carbon atoms, alkylthio of 1 to 8 carbon atoms, alkylamino of 1 to 8 carbon atoms, dialkylamino of 2 to 8 carbon atoms, alkoxycarbonyl of 2 to 8 carbon atoms, hydroxy, nitro, amino, cyano, carboxy, aminocarbonyl, chloro or mixtures of said substituents, and (ii) at least one stable nitroxyl compound. The relative concentrations of component (i) is 5 to 95 percent by weight and of component (ii) is 95 to 5 percent by weight based on the combined total weight of components (i) and (ii) and wherein the amount of the mixture of components (i) and (ii) is 1 to 2000 ppm, preferably at least 100 ppm, most preferably from 100 to 500 ppm, based on the total weight of the monomer of component (a). The instant invention also pertains to a process of inhibiting premature polymerization of an ethylenically unsaturated monomer which comprises adding thereto a mixture as described above. The monomers in the instant process are processed at a temperature from 50°C to 150°C. The synergistic mixture of the instant invention is added continuously or added intermittently upstream to the points where polymerization inhibition is required. In another variation of the instant invention, the components (i) and (ii) of the mixture are added separately at different entry points into the process stream in the processing train. Some preferred embodiments of component (i) are 2,6-di-tert-butyl-4-benzylidene-cyclohexa-2,5-dienone, 2,6-di-tert-butyl-4-(4-nitrobenzylidene)-cyclohexa-2,5-dienone, 2,6-di-tert-butyl-4-(3-nitrobenzylidene)-cyclohexa-2,5-dienone, 2,6-di-tert-butyl-4-(4-cyanobenzylidene)-cyclohexa-2,5-dienone, 2,6-di-tert-butyl-4-(4-dimethylaminobenzylidene)-cyclohexa-2,5-dienone, 2,6-di-tert-amyl-4-benzylidene-cyclohexa-2,5-dienone, 2,6-di-tert-butyl-4-(4-methoxybenzylidene)-cyclohexa-2,5-dienone, and 2,6-di-tert-butyl-4-(3,5-di-tert-butyl-4-hydroxybenzylidene)-cyclohexa-2,5-dienone. Some preferred embodiments of component (ii) are 1-oxyl-2,2,6,6-tetramethylpiperidine, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-ol, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-one, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl acetate, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl 2-ethylhexanoate, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl stearate, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl benzoate, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl 4-tert-butylbenzoate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) succinate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) adipate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) sebacate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) n-butylmalonate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) phthalate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) isophthalate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) terephthalate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) hexahydroterephthalate, N,N'-bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)adipamide, N-1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl-caprolactam, N-1 -oxyl-2,2,6,6-tetramethylpiperidin-4-yl-dodecylsuccinimide, 2,4,6-tris-[N-butyl-N-(1-oxyl-2,2,6,6-tetramethylpiperidin-4 -yl]-s-triazine, 4,4'-ethylenebis(1-oxyl-2,2,6,6-tetramethylpiperazin-3-one) and di-tert-butyl nitroxyl. A most preferred embodiment of the instant invention is where component (i) is 2,6-di-tert-butyl-4-benzylidene-cyclohexa-2,5-dienone, and component (ii) is bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) sebacate. The term unsaturated monomers as used in this application includes any readily polymerizable vinyl aromatic monomer, e.g., styrene, α-methylstyrene, vinyltoluene, divinylbenzene and structural isomers, derivatives and mixtures thereof or acrylic monomer, such as acrylic acid, methacrylic acid or their esters and amides and mixtures thereof or unsaturated esters such as vinyl acetate and unsaturated polyesters and mixtures thereof. The amount of the hindered 7-aryl quinone methide polymerization inhibitor may vary over a wide range depending upon the particular ethylenically unsaturated monomer and the conditions of distillation and/or storage. Preferably, the total amount of a quinone methide is from 1 ppm to about 2000 ppm (based upon the weight of the monomer being inhibited). For most applications the inhibitor system is used in the range of 5 to 1000 ppm, preferably at least 100 ppm, most preferably from 100 to 500 ppm. As the temperature increases, greater amounts of inhibitor are required. It has also been found that the hindered 7-aryl quinone methides show strong synergistic effect when used with stable hindered nitroxyl free radicals. Another object of the invention is therefore a stabilizer mixture comprising (i) at least one compound of formula I wherein R 1 and R 2 are independently alkyl of 4 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms or phenylalkyl of 7 to 15 carbon atoms, and R 3 is 2-, 3- or 4-pyridyl, 2- or 3-thienyl, 2- or 3-pyrryl, 2- or 3-furyl, aryl of 6 to 10 carbon atoms, or said aryl substituted by one to three alkyl of 1 to 8 carbon atoms, alkoxy of 1 to 8 carbon atoms, alkylthio of 1 to 8 carbon atoms, alkylamino of 1 to 8 carbon atoms, dialkylamino of 2 to 8 carbon atoms, alkoxycarbonyl of 2 to 8 carbon atoms, hydroxy, nitro, amino, cyano, carboxy, aminocarbonyl, chloro or mixtures of said substituents, and (ii) at least one stable nitroxyl compound. Surprisingly effective inhibition of ethylenically unsaturated monomer polymerization is thus obtained using combinations of hindered 7-aryl quinone methides with a wide variety of free nitroxyl radical derivatives, for example compounds such as: 1-oxyl-2,2,6,6-tetramethylpiperidine, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-ol, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-one, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl acetate, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl 2-ethylhexanoate, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl stearate, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl benzoate, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl 4-tert-butylbenzoate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) succinate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) adipate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) sebacate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) n-butylmalonate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) phthalate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) isophthalate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) terephthalate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl) hexahydroterephthalate, N,N'-bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)adipamide, N-1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl-caprolactam, N-1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl-dodecylsuccinimide, 2,4,6-tris-[N-butyl-N-(1-oxyl-2,2,6,6-tetramethylpiperidin-4 -yl]-s-triazine, 4,4'-ethylenebis(1-oxyl-2,2,6,6-tetramethylpiperazin-3-one) and di-tert-butyl nitroxyl. The relative concentrations of nitroxyl radical and hindered 7-aryl quinone methide compound used in the instant invention are generally in the range of about 5 to 95 weight percent nitroxyl radical and 95 to 5 weight percent hindered 7-aryl quinone methide, based on the total combined weight of these components. In preferred embodiments, the concentrations generally fall in the range of about 10 to 90 weight percent nitroxyl radical and 90 to 10 weight percent hindered 7-aryl quinone methide based on the total combined weight of these components. The polymerization inhibitor compositions can be introduced into the monomer to be protected by any conventional method. It may be added as a concentrate solution in suitable solvents just upstream of the point of desired application by any suitable means. Suitable solvents, for example, are the monomer itself, ethylbenzene or diethylbenzene. In addition, these compounds may be injected separately into the distillation train along with the incoming feed, or through separate entry points providing efficient distribution of the inhibitor composition. Since the inhibitor is gradually depleted during operation, it is generally necessary to maintain the appropiate amount of the inhibitor in the distillation apparatus by adding inhibitor during the course of the distillation process. Such addition may be carried out either on a generally continuous basis or it may consist of intermittently charging inhibitor into the distillation system if the concentration of inhibitor is to be maintained above the minimum required level. A further subject of the invention is the use of a compound of formula I for the stabilization of an ethylenically unsaturated monomer or mixture of monomers against premature polymerization wherein R 1 and R 2 are independently alkyl of 4 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms or phenylalkyl of 7 to 15 carbon atoms, and R 3 is 2-, 3- or 4-pyridyl, 2- or 3-thienyl, 2- or 3-pyrryl, 2- or 3-furyl, aryl of 6 to 10 carbon atoms, or said aryl substituted by one to three alkyl of 1 to 8 carbon atoms, alkoxy of 1 to 8 carbon atoms, alkylthio of 1 to 8 carbon atoms, alkylamino of 1 to 8 carbon atoms, dialkylamino of 2 to 8 carbon atoms, alkoxycarbonyl of 2 to 8 carbon atoms, hydroxy, nitro, amino, cyano, carboxy, aminocarbonyl, chloro or mixtures of said substituents. The polymerization inhibiting compositions of this invention are also well suited for protecting the reboiler sections of a distillation column. The following examples are meant for illustrative purposes only and are not to be construed as limiting the instant invention in any manner whatsoever. In the Examples, styrene is used as a representative vinyl aromatic monomer and the mixture acrylic acid-octyl acrylate serves as a test monomer for acrylate monomers. Example 1: 2,6-Di-tert-butyl-4-benzylidene-cyclohexa-2,5-dienone This compound is prepared according to the method described by B. Koutek et al., Synth. Commun. 6 (4), 305 (1976). Example 2: 2,6-Di-tert-butyl-4-(4-nitrobenzylidene)-cyclohexa-2,5-dienone (A) 2,6-Di-tert-butyl-4-[4-nitro-α-(piperidin-1-yl)benzyl]phenol A mixture of 2.1 g (0.01 mol) of 2,6-di-tert-butylphenol, 1.51 g (0.01 mol) of 4-nitrobenzaldehyde and 0.9 g (0.0105 mol) of piperidine is refluxed under nitrogen in 15 ml n-butanol for 24 hours. The solution is then evaporated in vacuo. The residue is then chromatographed on silica gel with hexane:ethyl acetate (4:1). The pure fractions are recrystallized from acetonitrile to give 1.0 g of the title compound as pale yellow crystals, melting at 147-148°C. 1 H-NMR (CDCl 3 , 500 MHz): 1.25 s (2x t-Bu), 1.30-1.60 m (3x CH 2 ), 2.10-2.25 m (2x CH 2 ), 4.20 s (CH), 5.05 s (OH), 7.03 s (2 ArH), 7.52 d (2 ArH, J=8.3 Hz), 8.06 d (2 ArH, J=8.3 Hz). (B) 2,6-Di-tert-butyl-4-(4-nitrobenzylidene)-cyclohexa-2,5-dienone A mixture of 4.24 g (0.01 mol) of the compound made in Example 2(A) and 3.0 g (0.024 mol) of dimethyl sulfate is refluxed in 15 ml acetonitrile for one hour. An additional 0.8 g (0.006 mol) of dimethyl sulfate is added and refluxing is continued for another hour. The solution is then evaporated in vacuo and the residue chromatographed on silica gel with toluene. The pure fractions are recrystallized from acetonitrile to give 2.7 g of the title compound as orange crystals, melting at 162-163°C. 1 H-NMR (CDCl 3 , 300 MHz): 1.26 s (t-Bu), 1.30 s (t-Bu), 6.98 d (1 ArH, J=2.8Hz), 7.11 s (CH), 7.33 d (1 ArH, J=2.8Hz), 7.55 d (2 ArH, J=8.4Hz), 8.28 d (2 ArH, J=8.4Hz). Example 3: 2,6-Di-tert-butyl-4-(3-nitrobenzylidene)-cyclohexa-2,5-dienone (A) 2,6-Di-tert-butyl-4-[3-nitro-α-(piperidin-1-yl)benzyl]phenol Using the same procedure as described in Example 4, 30.2 g (0.2 mol) of 3-nitrobenzaldehyde, 37.4 g (0.44 mol) of piperidine and 39.2 g (0.19 mol) of 2,6-di-tert-butylphenol are allowed to react in xylene to give 48.4 g of the title compound as yellow crystals, melting at 157°C. Analysis: Calcd. for C 26 H 36 N 2 O 3 C, 73.55; H, 8.55; N, 6.60. Found C, 73.65; H, 8.53; N, 6.65. (B) 2,6-Di-tert-butyl-4-(3-nitrobenzylidene)-cyclohexa-2,5-dienone The compound prepared in Example 3(A), 17.0 g (0.04 mol) is heated in 60 ml acetic anhydride at 80°C for 45 minutes. The mixture is then poured into 150 ml water and extracted with toluene. The toluene layer is washed three times with water, evaporated in vacuo, and recrystallized from methanol to give 9.7 g of the title compound as an orange solid, melting at 118°C. Analysis: Calcd for C 21 H 25 NO 3 C, 74.3; H, 7.4; N, 4.1. Found C, 74.1; H, 7.4; N, 4.1. Example 4 : 2,6-Di-tert-butyl-4-(4-cyanobenzylidene)-cyclohexa-2,5-dienone (A) 2,6-Di-tert-butyl-4-[4-cyano-α-(piperidin-1-yl)benzyl]phenol 2,6-Di-tert-butylphenol (4.12 g, 0.02 mol), 2.62 g (0.02 mol) of 4-cyanobenzaldehyde and 1.7 g (0.02 mol) of piperidine are refluxed under nitrogen in 25 ml of xylene for 24 hours. The solution is then evaporated in vacuo and the residue chromatographed on silica gel with toluene/ ethyl acetate (9:1) to give 6.2 g of a practically pure title compound. A 5 g portion of said compound is recrystallized twice from acetonitrile to give 1.0 g of a pure sample as colorless crystals, melting at 139-140°C. 1 H-NMR (CDCl 3 , 300 MHz): 1.36 s (2x t-Bu), 1.35-1.60 m (3x CH 2 ), 2.10-2.30 m (2x CH 2 ), 4.15 s (CH), 5.05 s (OH), 7.04 s (2 ArH), 7.46-7.55 m (4 ArH). (B) 2,6-Di-tert-butyl-4-(4-cyanobenzylidene)-cyclohexa-2,5-dienone The compound of Example 4(A) (1.2 g, 0.003 mol) and 1.1 g (0.009 mol) of dimethyl sulfate are refluxed in 20 ml of acetonitrile for one hour. The solution is then evaporated in vacuo and the residue chromatographed on silica gel with toluene. The pure fractions are recrystallized from acetonitrile to give 0.3 g of the title compound as yellow crystals, melting at 147-148°C. 1 H-NMR (CDCl 3 , 300 MHz): 1.25 s (t-Bu), 1.29 s (t-Bu), 6.96 d (1 ArH, J=2.2Hz), 7.08 s (CH), 7.32 d (1 ArH, J=2.2Hz), 7.50 d (2 ArH, J=8.3Hz), 7.70 d (2 ArH, J=8.3Hz). Example 5: 2,6-Di-tert-butyl-4-(4-dimethylaminobenzylidene)-cyclohexa-2,5-dienone (A) 2,6-Di-tert-butyl-4-[4-dimethylamino-α-(piperidin-1-yl)benzyl]phenol To 30.4 g (0.2 mol) of 4-dimethylaminobenzaldehyde in 100 ml of xylene, 39.1 g (0.46 mol) of piperidine is added dropwise over a period of six minutes. The mixture is heated at reflux using a Dean-Stark trap until the separation of water is complete. To the cooled reaction mixture 40.3 (0.2 mol) of 2,6-di-tert-butylphenol in 70 ml of xylene is added rapidly. The mixture is then heated at reflux for five hours. The title compound is isolated as an almost white solid by evaporation of the solvent and recrystallization from toluene-hexane.The yield is 66.3 g of the title compound, melting at 184-185°C. Analysis: Calcd for C 28 H 42 N 2 O C, 79.6; H, 10.0; N, 6.6. Found C, 79.7; H, 10.1; N, 6.4. (B) 2,6-Di-tert-butyl-4-(4-dimethylaminobenzylidene)-cyclohexa-2,5-dienone The compound prepared in Example 5(A) (21.1 g. 0.05 mol) is heated in 100 ml acetic acid at 110°C for 15 minutes. The reaction mixture is poured into 200 ml of water and then taken up in 200 ml of toluene. Evaporation of the solvent and recrystallization of the residue from methanol affords 10.7 g of the title compound as a red powder, melting at 175°C. Analysis: Calcd for C 23 H 31 NO C, 81.8; H, 9.3; N, 4.1. Found C, 81.7; H, 9.2; N, 4.1. Example 6: 2,6-Di-tert-amyl-4-benzylidene-cyclohexa-2,5-dienone 6.0 g (0.026 Mol) of 2,6-di-tert-amylphenol, 2.75 g (0.026 mol) of benzaldehyde and 4.37 g (0.051 mol) of piperidine are refluxed under nitrogen in 50 ml of heptane on a Dean-Stark trap for 24 hours. The solution is then evaporated in vacuo and the residue chromatographed twice on silica gel with hexane and then with hexane:ethyl acetate (9:1) to give 3.5 g of the title compound as a thick yellow oil. 1 H-NMR (CDCl 3 , 300 MHz): 0.66 t (CH 3 , J=7.3Hz), 0.68 t (CH 3 , J=7.3Hz), 1.24 s (CH 3 ), 1.28 (CH 3 ), 1.83 q (CH 2 , J=7.3 Hz), 1.87 q (CH 2 , J=7.3 Hz), 6.98 d (1 ArH, J=2.1Hz), 7.19 s (CH), 7.36-7.45 m (1 ArH), 7.45-7.52 m (5 ArH). Example 7: 2,6-Di-tert-butyl-4-(4-methoxybenzylidene)-cyclohexa-2,5-dienone This compound is prepared according to the method described by L. Jurd et al., J. Agric. Food Chem., 27 , 1007 (1979). Example 8: 2,6-Di-tert-butyl-4-(3,5-di-tert-butyl-4-hydroxybenzylidene)-cyclohexa-2,5-dienone This compound is prepared according to the method described by A. G. Liakumovich et al., Izobreteniya, 37 , 87 (1992). Example 9: Inhibition of the Polymerization of Styrene Monomer (A) Series of 7-aryl quinone methides Commercial grade styrene is freed of tert-butyl catechol storage stabilizer by washing with 1 N sodium hydroxide, water and subsequent distillation under reduced pressure. A 300 mL 3-necked flask equipped with thermometer, condenser, rubber septum and magnetic stirrer bar is charged with 100 g of purified styrene and 20.0 mg of experimental inhibitor or 20 mg of a mixture of inhibitors, yielding styrene with 200 ppm of total inhibitors. An oxygen-free atmosphere is established by five consecutive evacuations and backfilling with nitrogen, followed by sparging the styrene solution with pure nitrogen for 15 minutes. The vessel is then immersed into a mechanically stirred and thermostatically controlled oilbath at 120°C and heated for 45 minutes. The amount of polystyrene formed is then determined by refractive index measurements, calibrated with authentic polystyrene in styrene solutions of known concentration. The lower the amount of polystyrene formed, the more effective is the inhibitor compound. Without any added inhibitor 6.2% polystyrene is formed. Polymer levels obtained with inhibitors are listed in the table below. Compound of Example Percent Polymer after 45 Minutes 1 0.48 2 0.32 3 0.32 4 0.32 5 1.13 6 0.48 7 0.65 8 0.48 Each of these 7-aryl quinone methides is quite effective as a polymerization inhibitor for styrene monomer. (B) Effect of Oxygen When the compound of Example 1 is used in the presence of 0.66% oxygen or in the presence of only nitrogen, the amount of polymer formed after 45 minutes is the same, namely 0.48 %. (C) Mixture of compounds of the formula I with stable hindered nitroxyl free radicals The blends of hindered 7-aryl quinone methides with stable hindered nitroxyl free radicals inhibitors are found to be considerably more effective in reducing the amount of polymer formed than is either component by itself at the same total inhibitor concentration. This synergistic effect is demonstrated in the table below with the 7-aryl quinone methide compound of Example 1. Inhibitor Concentration Percent Polymer after 45 Minutes Compound of Example 1 200 ppm 0.48 Nitroxyl 200 ppm 1.37 Compound of Example 1 + Nitroxyl 100 ppm + 100 ppm 0.16 It is clear that there is a synergistic effect obtained when a nitroxyl free radical is used in conjunction with the instant 7-aryl quinone methide. Example 10: Inhibition of Acrylate Monomers A screening test that involves the radical polymerization of acrylate is developed to test polymerization inhibitors. The procedure involves the radical induced polymerization of a 3:1 mixture of acrylic acid and octyl acrylate in a low molecular weight carboxylic acid solvent. Free radicals are generated by the thermal decomposition of azo-bis-isobutyronitrile (AIBN) at 60°C. The degree of polymerization is determined by periodically measuring the solution viscosity, and comparing it to the initial viscosity. A four-fold increase in viscosity is considered failure. The higher the time to achieve four-fold increase in viscosity, the more effective is the tested inhibitor compound. Unless otherwise noted, all reagents and solvents are used as received. A solution of acrylate (3:1 weight ratio of acrylic acid to octyl acrylate) in propionic acid (0.1g/mL) containing AIBN (recrystallized from methanol) and the inhibitor additive to be tested (2% and 400 ppm, respectively, with respect to acrylate) is prepared. When determining interaction with a coadditive, phenothiazine is present at 250 ppm (with respect to acrylate). To a Canon-Fenske viscometer is added 10mL of the test solution, which is then purged with nitrogen (>99.995%) for 5 minutes before being heated in a 60°C oil bath. After an additional purge for 5 minutes, drop times are automatically measured (10 minute intervals, with a 1 minute gas purge before each measurement) using a Design Scientific automated viscometer. The results are summarized in the table below. Time (min) to 4-Fold Viscosity Increase Inhibitor (ppm) None 45 Compound of Example 1 (400) 69 Phenothiazine (250) 57 Phenothiazine (250) plus Compound of Example 1 (400) 73 The combination of an instant 7-aryl quinone methide plus phenothiazine provides superior polymerization inhibition compared to either inhibitor alone.

Claims: A stabilized monomer composition which comprises (a) an ethylenically unsaturated monomer or mixture of monomers, and (b) a compound of formula I wherein R 1 and R 2 are independently alkyl of 4 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms or phenylalkyl of 7 to 15 carbon atoms, and R 3 is 2-, 3- or 4-pyridyl, 2- or 3-thienyl, 2- or 3-pyrryl, 2- or 3-furyl, aryl of 6 to 10 carbon atoms, or said aryl substituted by one to three alkyl of 1 to 8 carbon atoms, alkoxy of 1 to 8 carbon atoms, alkylthio of 1 to 8 carbon atoms, alkylamino of 1 to 8 carbon atoms, dialkylamino of 2 to 8 carbon atoms, alkoxycarbonyl of 2 to 8 carbon atoms, hydroxy, nitro, amino, cyano, carboxy, aminocarbonyl, chloro or mixtures of said substituents, with the proviso that R 3 is not phenyl if R 1 and R 2 are tert.-butyl. A composition according to claim 1 where in the compound of formula I, R 1 and R 2 are the same. A composition according to claim 2 wherein R 1 and R 2 are tert-butyl, tert-amyl, tert-octyl, cycloalkyl, α-methylbenzyl or α,α-dimethylbenzyl. A composition according to claim 1 where in the compound of formula I, R 3 is phenyl or phenyl substituted by nitro, cyano, dimethylamino, methoxy, alkyl of 1 to 4 carbon atoms, hydroxy or mixtures of said substituents. A composition according to claim 1 wherein the monomer of component (a) is an aromatic vinyl compound or an acrylic monomer. A composition according to claim 1 wherein the amount of a compound of formula I is from 1 to 2000 ppm, based on the weight of the monomer of component (a). A stabilized monomer composition for which comprises (a) an ethylenically unsaturated monomer or mixture of monomers, and (b) a mixture of (i) at least one compound of formula I wherein R 1 and R 2 are independently alkyl of 4 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms or phenylalkyl of 7 to 15 carbon atoms, and R 3 is 2-, 3- or 4-pyridyl, 2- or 3-thienyl, 2- or 3-pyrryl, 2- or 3-furyl, aryl of 6 to 10 carbon atoms, or said aryl substituted by one to three alkyl of 1 to 8 carbon atoms, alkoxy of 1 to 8 carbon atoms, alkylthio of 1 to 8 carbon atoms, alkylamino of 1 to 8 carbon atoms, dialkylamino of 2 to 8 carbon atoms, alkoxycarbonyl of 2 to 8 carbon atoms, hydroxy, nitro, amino, cyano, carboxy, aminocarbonyl, chloro or mixtures of said substituents, and (ii) at least one stable nitroxyl compound. A composition according to claim 7 where in the compound of formula I, R 1 and R 2 are the same. A composition according to claim 8 wherein R 1 and R 2 are tert-butyl, tert-amyl, tert-octyl, cycloalkyl, α-methylbenzyl or α,α-dimethylbenzyl. A composition according to claim 7 where in the compound of formula I, R 3 is phenyl or phenyl substituted by nitro, cyano, dimethylamino, methoxy, alkyl of 1 to 4 carbon atoms, hydroxy or mixtures of said substituents. A composition according to claim 7 wherein the monomer of component (a) is an aromatic vinyl compound or an acrylic monomer. A composition according to claim 7 wherein the relative concentrations of component (i) is 5 to 95 percent by weight and of component (ii) is 95 to 5 percent by weight based on the combined total weight of components (i) and (ii) and wherein the effective inhibiting amount of the synergistic mixture of components (i) and (ii) is 1 to 2000 ppm based on the total weight of the monomer of component (a). A stabilizer mixture comprising (i) at least one compound of formula I wherein R 1 and R 2 are independently alkyl of 4 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms or phenylalkyl of 7 to 15 carbon atoms, and R 3 is 2-, 3- or 4-pyridyl, 2- or 3-thienyl, 2- or 3-pyrryl, 2- or 3-furyl, aryl of 6 to 10 carbon atoms, or said aryl substituted by one to three alkyl of 1 to 8 carbon atoms, alkoxy of 1 to 8 carbon atoms, alkylthio of 1 to 8 carbon atoms, alkylamino of 1 to 8 carbon atoms, dialkylamino of 2 to 8 carbon atoms, alkoxycarbonyl of 2 to 8 carbon atoms, hydroxy, nitro, amino, cyano, carboxy, aminocarbonyl, chloro or mixtures of said substituents, and (ii) at least one stable nitroxyl compound. A process of inhibiting premature polymerization of an ethylenically unsaturated monomer which comprises adding thereto a compound of the formula I according to claim 1 or a stabilizer mixture according to claim 13. A process according to claim 14 wherein the monomers are processed at a temperature from 50°C to 150°C. A process according to claim 14 wherein the compound of the formula I or the stabilizer mixture is added continuously or added intermittently upstream to the points where polymerization inhibition is required. A process of inhibiting premature polymerization of an ethylenically unsaturated monomer wherein the components (i) and (ii) of the stabilizer mixture according to claim 13 are added separately at different entry points into the process stream in the processing train. Use of a compound of formula I for the stabilization of an ethylenically unsaturated monomer or mixture of monomers against premature polymerization wherein R 1 and R 2 are independently alkyl of 4 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms or phenylalkyl of 7 to 15 carbon atoms, and R 3 is 2-, 3- or 4-pyridyl, 2- or 3-thienyl, 2- or 3-pyrryl, 2- or 3-furyl, aryl of 6 to 10 carbon atoms, or said aryl substituted by one to three alkyl of 1 to 8 carbon atoms, alkoxy of 1 to 8 carbon atoms, alkylthio of 1 to 8 carbon atoms, alkylamino of 1 to 8 carbon atoms, dialkylamino of 2 to 8 carbon atoms, alkoxycarbonyl of 2 to 8 carbon atoms, hydroxy, nitro, amino, cyano, carboxy, aminocarbonyl, chloro or mixtures of said substituents.

Inventors: EVANS SAMUEL DR, GANDE MATTHEW EDWARD, NESVADBA PETER DR, VON AHN VOLKER HARTMUT, WINTER ROLAND ARTHUR EDWIN, EVANS, SAMUEL, DR., GANDE, MATTHEW EDWARD, NESVADBA, PETER, DR., VON AHN, VOLKER HARTMUT, WINTER, ROLAND ARTHUR EDWIN
Applicants: ONDEO NALCO ENERGY SERV LP, ONDEO NALCO ENERGY SERVICES, L.P.
Application year: 1996
Main classification: C07B63
IPC codes: C07C7, C07B63, C07D307, C07C225, C07C49, C07D333, C08F4, C07D211, C07C205, C07C67, C07D207, C07D401, C07C255, C08F2