DIAMOND COATED BODY AND METHOD OF ITS PRODUCTION

Abstract: According to the present invention there is now provided a body coated with at least one diamond layer on a substrate of cemented carbide or cermets. The substrate is before the diamond coating process provided with spotwise occurring particles containing an element either being any of W, Ta, Ti, Mo, Cr, V, Nb, Mg, Ca, Na, K or preferably any of B, Si, S, Al or P and in that said particles are dispersed at a density giving an average distance between two particles of 10 mu m or less, preferably 5 mu m or less.

Description: DIAMOND COATED BODY AND METHOD OF ITS PRODUCTION The present invention relates to a diamond coated body with good adherence of the diamond layer and a high resistance to wear. In particular, the invention relates to a cutting tool for cutting Al-alloys containing e.g. Si and Cu as alloying elements and the like. Production of thin layers of diamond directly from the gas phase by CVD or PVD technique is of great inte- rest for coating of cutting tools, drill bits, knives, etc. Gas phase deposition of diamond at useful deposi¬ tion rates has been subject for numerous researchers and a number of methods have evolved, all of which belong to plasma CVD methods . The commercialisation of diamond coated cutting tools has involved several years of research efforts, where the main problem has been achieving sufficient diamond layer adhesion onto the tool substrate material in a large-scale production method in order to make dia- mond coated cutting tools competitive from the economi¬ cal point of view. At this stage, these problems have been solved and diamond coated cutting tools are pro¬ duced and sold, see I.Reineck, M.E.Sjδstrand, J.Karner, M.Pedrazzini in "Proceedings of the 6th European Conf. on Diamond, Diamond-like and Related Materials", Barce¬ lona, Sept. 1995. Having reached this level of develop¬ ment, further focus on production cost related issues is of vital importance. The substrates of interest for diamond layers in cutting applications include cemented carbides and ce¬ ramics such as SiAlON and Si3 4 and the deposition of diamond on these categories of substrates is well known in the art. A standard method for achieving good diamond adhesion on cemented carbide substrates is to use dia- mond particles suspended in an ultrasonic bath wherein the tool substrates to be coated are treated prior to diamond deposition in order to scratch the tool surfaces to enhance the nucleation density. A high nucleation density is, however, not sufficient for achieving a good diamond layer adhesion - other parameters such as con¬ trolling the binder phase activity, in particular, that of cobalt, in a surface region is also important. Much work has been devoted to the enhancement of nucleation density for the diamond growth, see e.g. H.Liu and D.S.Dandy, Diam. Rel . Mat. 4 (1995) 1173, for a review. In B.Lux and R.Haubner, Diamond and Diamond-like Films and Coatings, Ed R.E.Clausing et al. , 1991, Plenum Press N.Y. polishing with AI2O3 (1 μm) is said not to enhance the nucleation density while this effect is ob- tained with diamond grits. In EP 445 305 electrolytic polishing of cemented carbide, optionally combined with subsequent scratching with diamond, cBN, AI2O3 or SiC is described. Diamond is the preferred scratching agent. The indication for good diamond layer adhesion is measured by means of a Rock¬ well indentation test where the layers are said to with¬ stand a load of 5-25 kg without flaking. It is therefore surprising to find that the flaking resistance as well as the wear resistance of a diamond layer deposited on a cemented carbide or ceramic body, in particular a cutting tool insert, can be reached to a level at least as good as that for diamond layers depos¬ ited onto tool bodies prepared by ultrasonic pretreat¬ ment with diamond particles. This is achieved through a combination of ultrasonic pretreatment with particles consisting of e.g. B4C, AI2O3 or SiC and the removal of binder material, e.g. cobalt, in a surface region of the tool substrate. In addition, the substrate surface should be prepared as to have either a certain surface roughness or to have pores in a surface region. Using particles other than diamond for the predeposition preparation is favourable from the view of production costs . According to the present invention the particles provided by the pretreatment can be stuck onto the sub¬ strate surface as can be seen by analysing the surface in an electron probe microanalyzer, see Fig 1. The dis¬ tribution of Al enriched particles should be compared to that of a substrate surface that is not treated accord- ing to the invention as shown in Fig 2. According to the present invention there is now pro¬ vided a body coated with at least one diamond layer. The surface of the body being in contact with the diamond layer is enriched with particles containing at least 20 wt-% of B, Al and/or Si such as carbides, oxides or ni¬ trides of these (e.g. B4C, BN, SiC or AI2O3), preferably Al-containing particles. Particles containing S and/or P can also be considered as well as metal containing par¬ ticles where the metal is at least one of W, Cr, Mo, Ta, Ti, Nb, V, Mg, Ca, Na or K. The average size of the particles is less than 5 μm, preferably less than 2 μm and most preferably less than 0.5 μm. Alternatively, the average size of the particles is 7-20 μm, preferably 10-15 μm. In yet an alternative a combination of small, <0.5 μm, and large particles, 10- 15 μm, is present at least 25% of each kind. The particle distribution is such that the average distance x m between two particles as analysed by elec¬ tron microprobe analysis is less than 10 μm, preferably less than 5 μm where x m = ∑xi/n where x^ are the indi¬ vidual distances between nearest neighbours of particles as defined in Fig 1 and n is the number of such pairs, n>5. The surface roughness of the body is l<R a <20 μm, preferably l<R a <10 μm. In an alternative embodiment, with a surface roughness R a l um, there are provided pores in a surface region of a depth <10 μm, preferably <5 μm. The size of the pores is 0.5-5 μm, preferably 0.5-2 μm. The bodies according to the present invention in¬ clude cemented carbides and cermets. Preferably, a ce¬ mented carbide body is depleted in the surface zone with respect to cobalt. This can, for example, be obtained by partly carburizing an eta-phase containing body as dis- closed in EP 464 012. According to the present invention there is also provided a method of preparing bodies suited for coating with diamond layers showing good adhesion. The bodies are first treated in order to get a surface roughness or creation of pores and/or depletion of cobalt, either through a sintering process with roughens the surface, or by etching the binder material to create pores in the surface region. Such methods are well known in the art. Subsequently, the bodies are treated in an ultrasonic bath containing the above mentioned particles in a con¬ centration of 2-50 g/l in water, oil or other suitable liquid for about 30-60 min. The average size of the par¬ ticles is less than 5 μm, preferably less than 2 μm and most preferably less than 0.5 μm. As an alternative method of treatment, particles of average size 7-20 μm, preferably 10-15 μm, are used. In a preferred method, the bodies are treated using particles of average size 10-15 μm and of average size less than 0.5 μm either si¬ multaneously in one treatment, using at least 25% of each kind, or separately in two consecutive treatments. As an alternative method of providing the particles to the surfaces of the substrates, a solution containing the desired elements can be used out of which particles are precipitated. After the body is treated to provide the particle- containing surface, a diamond layer is applied by con¬ ventional plasma CVD techniques known to the skilled ar¬ tisan. The invention has been described with reference to diamond layer in direct contact with a cemented carbide or cermet body. It is obvious that the invention can be applied also to the case when one or more intermediate layers are present between the body and the diamond layer. The invention can be applied to diamond coated cut¬ ting tools, tools for rock drilling and wear parts as well as to other superhard layers such as cBN layers de¬ posited by CVD or PVD methods. Example 1 Six C-6%Co cemented carbide inserts with a cobalt depleted surface zone and a surface roughness of R a = 2.0 μm were first treated in an ultrasonic bath contain- ing 1 g B4C-powder of grain size 5-15 μm in 200 ml oil as suspending medium. The treatment time was 30 min. The inserts were subsequently ultrasonically treated in a suspension consisting of AI2O3 powder of grain size <0.5 μm at a concentration of 1 g per 200 ml oil for another 30 min. The inserts were then cleaned in alcohol for 30 min in the ultrasonic bath. The AI2O3 - B4C pretreated inserts were analysed in an electron microprobe with respect to Al. Particles containing Al were found to exist at an average distance of 4 μm between each two particles . A set of reference WC-6%Co inserts were ultrasoni¬ cally pretreated in diamond grit powder of grain size 0- 2 μm suspended in oil. The treatment time as well as the cleaning procedure were the same as for the above men- tioned inserts. Subsequently, both types of inserts were diamond coated to a layer thickness of 7 μm using microwave plasma assisted CVD. The grain size of the layer was about 5 μm. The inserts were subjected to a turning flaking test in an Al-18%Cu alloy using the following cutting data: v = 300 m/min f = 0.1 mm a = 1 mm wet cutting The diamond coated set of inserts pretreated accord¬ ing to the invention lasted 6 min in this test until a wear zone of width of 0.1 mm was formed compared to the result for the set of inserts pretreated with diamond grit suspension which lasted only 4 min. Apart from the improvement in tool life, the benefit of using a cheaper pretreatment agent compared to the diamond grit is de¬ monstrated. Example 2 Six WC-4%Co inserts with a cobalt depleted surface zone and a porous surface layer of 5 μm with pore size 1 μm, were pretreated in an ultrasonic suspension contain¬ ing B4C powder of grain size distribution 0-5 μm. The treatment time was 30 min. The inserts were then ultra¬ sonically cleaned in alcohol for 30 min. A set of refer¬ ence inserts was prepared similar to Example 1. The in¬ serts were coated with a 10 μm thick diamond layer using a DC arc plasma CVD method. Prior to diamond coating the B4C treated inserts were analysed in an electron icroprobe with respect to boron. Boron containing particles were found with an average distance of 4 μm between two individual par¬ ticles . The inserts were subjected to a milling flaking test in an Al-9%Si alloy using the following cutting data: v = 2000 m/min f = 0.5 mm/tooth a = 1 mm wet cutting The diamond coated set of inserts pretreated accord¬ ing to the invention lasted 100 passes in this test without any visible damage. This result was also achieved for the diamond grit treated set of inserts . Hence, a similar performance can be achieved by using a B4C treatment instead of the more expensive diamond grit treatment. Example 3 Six C-4%Co inserts with a cobalt depleted surface zone and a surface roughness of R a =5 μm were treated in an ultrasonic bath containing 1 g B4C of grit size 10 μm in 200 ml oil for 30 min. The inserts were subsequently treated in an aqueous AI2 (304)3 solution (10%) for 5 min. An alkaline solution of 2% NaOH was then added into the Al2(Sθ4)3 solution, still being stirred in the ul¬ trasonic bath. The inserts were treated in this bath for another 25 min. Then the inserts were ultrasonically cleaned in alcohol during 15 min. Reference inserts were prepared according to Example 1 above. All inserts were diamond coated in a DC plasma activated CVD process to a diamond layer of thickness 10 μm. Prior to diamond coating the AI2 (SO4) 3-treated in¬ serts were analysed in an electron microprobe with re¬ spect to aluminium. Aluminium containing particles were found at an average distance of 5 μm between each two individual particles. The inserts were subjected to a turning flaking test in an Al-18%Cu alloy using the following cutting data: v = 700 m/min f = 0.05 mm a = 1 mm wet cutting The diamond coated set of inserts pretreated accord- ing to the invention lasted 4 min in this test compared to the result for the set of inserts pretreated with diamond grit suspension which was 2 min. Again, an im¬ provement in tool life is demonstrated, together with the benefit of using a cheaper pretreatment agent com- pared to the diamond grit powder.

Claims: Claims 1. Body of cemented carbide or cermets coated with at least one diamond layer characterised in that be¬ tween said body and diamond layer is present spotwise occurring particles containing at least one element either being any of W, Ta, Ti, Mo, Cr, V, Nb, Mg, Ca, Na, K or preferably any of B, Si, S, Al or P and in that said particles are dispersed at a density giving an ave¬ rage distance between two particles of 10 μm or less, preferably 5 μm or less. 2. Body according claim 1 characterised in that said body is a cemented carbide with a cobalt depleted surface zone. 3. Body according to any of the preceding claims characterised in that said body has a surface rough¬ ness of 1 μm < R a < 20 μm, preferably 1 μm < R a < 10 μm. 4. Body according to any of the claims 1-3 characterised in that the body has a porous surface zone of <10 μm, preferably <5 urn. 5. Method for producing a diamond coated body characterised in that the body is first treated to get a suitable structure of their surface region and depletion of cobalt, either through a sintering process with roughens the surface, or by etching the binder a- terial to create pores in the surface region whereafter the bodies are treated in an ultrasonic bath containing particles containing at least one element either being any of the metals W, Ta, Ti, Mo, Cr, V, Nb, Al, Mg, Ca, Na, K or any of the metalloids B, Si, S or P in a con- centration of 2-50 g/l in water, oil or other suitable liquid for about 30-60 min whereby the average size of the particles is less than 5 μm, preferably less than 2 μm or 7-20 μm, preferably 10-15 μm. 6. Method according to claim 5 characterised in that the bodies are treated using particles of average size 10-15 μm and of average size less than 0.5 μm either simultaneously in one treatment, using at least 25% of each kind, or separately in two consecutive treatments . 7. Method according to claim 5 characterised in that the body is treated in a solution containing the desired elements out of which solution the desired par¬ ticles precipitate.

Inventors: NORDIN MARIA, REINECK INGRID, NORDIN, MARIA, REINECK, INGRID
Applicants: SANDVIK AB, SANDVIK AB; (PUBL)
Application year: 1996
Main classification: C23C16
IPC codes: C23C16