PROPYLENE COMPOSITION, PROCESS FOR PREPARING THE SAME, POLYPROPYLENE COMPOSITION, AND MOLDED ARTICLES

Abstract: A polypropylene composition for the production of various molded articles which are excellent in moldability, mold shrinkage factor on molding, rigidity, flexibility, impact resistance, in particular low-temperature impact resistance, transparency, gloss, stress-whitening resistance, and the balance thereof; various molded articles having the above properties; a propylene composition which is suitable for a base resin for the polypropylene composition; and a process for the production thereof. The propylene composition comprises a propylene homopolymer and a propylene-ethylene copolymer, the intrinsic viscosity of the copolymer ([η] RC ) is in the range of 1.7 to 2.8 dl/g, the intrinsic viscosity ratio of the homopolymer to the copolymer ([η] RC /[η] PP ) is in the range of 0.7 to 1.2 and a product [ (W PP /W RC ) x ([η] RC /[η] PP ) ] of the weight ratio (W PP /W RC ) of the homopolymer to the copolymer and the intrinsic viscosity ratio thereof is in the range of 1.0 to 3.0.

Description: TECHNICAL FIELD OF THE INVENTION This invention relates uniaxially stretched and biaxially oriented films. BACKGROUND OF THE ART Polypropylene resins are relatively cheap and have good properties, and so have a widespread use such as various molded articles, e.g., injection molded articles such as sheets, containers, caps and those having a hinge structure; films; and blow molded articles such as air ducts. Films of polypropylene resins have been extensively employed as packaging materials for foods and fiber products, taking advantage of their mechanical, optical and thermal properties. In compliance with the properties required for the molding applications, there have been used polypropylene compositions, each based on propylene homopolymer; random copolymers of propylene and α-olefins, especially ethylene; and propylene homopolymer/propylene-α-olefin copolymer. In general, propylene homopolymer has high rigidity, good heat resistance, but insufficient flexibility, poor impact resistance, especially low-temperature impact resistance and poor tear strength when it is formed into films. Random copolymers of propylene and α-olefins have good transparency and good flexibility, but poor heat resistance and poor low-temperature impact resistance. Since known propylene compositions comprising a propylene homopolymer and a propylene-ethylene copolymer have good heat resistance and low-temperature impact resistance, they have been extensively employed in a wide variety of industrial fields including automobiles and appliances. However, they are inferior in transparency and gloss to homopolymer, but have high mold shrinkage factor like homopolymer, and also they are inferior in tear strength and flexibility to copolymers. In any case, a phenomenon of whitening is observed in said known compositions when impacting and bending, and their whitening resistance is insufficient. The methods to improve their insufficient properties include a method of modifying the properties of homopolymers, copolymers or compositions and a method using additives. For example, a general method has been employed wherein the mold shrinkage factor of the composition is improved by filling with inorganic materials, such as talc. However, the method requires a large quantity of inorganic materials such as talc to improve the mold shrinkage factor, which results in an increased weight of the molded article and a remarkably poor appearance. Further, a method has been employed wherein an ethylene content in the copolymer of the composition is lowered to improve the transparency and gloss. However, it is general that lowering the ethylene content in the copolymer contributes to an improvement in gloss, with the reduction in low-temperature impact resistance and rigidity. JP-A-60-28411 discloses a process of producing a high-rigidity ethylene-propylene copolymer, i.e., a propylene composition wherein propylene and ethylene are copolymerized in three consecutive stages with varying the ethylene content. The composition obtained by this process has high rigidity, good whitening resistance, good impact resistance and good heat resistance, but more improvements are required in the transparency, gloss, appearance of the molded articles and mold shrinkage factor on molding. JP-B-7-30145 discloses a propylene block copolymer, i.e., a propylene composition which comprises a crystalline polypropylene block and an ethylene-propylene random copolymer block, the content of the crystalline polypropylene component being 55-95 wt.%, the ratio of the intrinsic viscosities of both components ([η] EP /[η] PP ) being 0.5-2.0 and a glass transition temperature of the ethylene-propylene random copolymer being -30°C or lower. This composition has substantially the same range in respect of the content of the ethylene-propylene copolymer and the ratio of the intrinsic viscosity of the propylene homopolymer to that of the copolymer, has good mechanical properties such as impact resistance and rigidity, but more improvements are required in the transparency, gloss and appearance, especially stress-whitening resistance of the molded articles, and the mold shrinkage factor on molding. JP-A-6-93061 discloses a melt-kneaded polypropylene block copolymer obtained by polymerizing a monomer based on propylene to form a polymer comprising polypropylene (component A) in an amount of 60-80% by weight to the total polymer amount, and then polymerizing a mixture of ethylene and propylene to form an ethylene-propylene copolymer (component B) having an ethylene content of 20-50% by weight, and melt-kneading the resulting polypropylene block copolymer, wherein the intrinsic viscosity ([η B ]) of the ethylene-propylene copolymer is at least 2.0 dl/g and the ratio ([η] B /[η] A ) of the intrinsic viscosity of the component B to the component A is 1.8 or less. This composition has substantially the same range in respect of the content of the ethylene-propylene copolymer and the ratio of the intrinsic viscosity of the propylene homopolymer to the copolymer, has good low-temperature impact resistance, good blocking resistance and good appearance, but more improvements are required in mechanical properties such as rigidity and mold shrinkage factor on molding. JP-A-6-328640 discloses a multilayered film with a largely improved tear strength wherein a polypropylene resin layer is laminated on both surfaces of a straight chain low-density polyethylene layer. In the multilayered film, a compatibility of the laminating low-density polyethylene with polypropylene resin may be not substantially good, and so fish eye is easy to occur when the film is remelted and reused. JP-A-52-126450 discloses a blend of three components comprising an ethylene-α-olefin copolymer rubber, polypropylene or high-density polyethylene and paraffin or naphthene oil. This blend has good flexibility, but lower heat resistance. JP-A-4-282232 discloses a resin tubular body wherein a rigid portion produced from a rigid polyolefin resin and a flexible portion produced from a thermoplastic elastomer are connected in series with each other. This tubular body may be insufficient in the bonding strength between the rigid portion and the flexible portion. SUMMARY OF THE INVENTION The present inventors have studied the propylene type compositions to achieve the above-mentioned objects, and found that a propylene composition produced by subjecting propylene alone and then a mixture of propylene and ethylene to a continuous vapor phase polymerization in the presence of a catalyst for a stereoregular olefin polymerization comprising a titanium-containing solid catalyst component of a large particle size, is excellent in respect of impact resistance, especially low-temperature impact resistance, rigidity, transparency, stress-whitening resistance, mold shrinkage factor on molding as well as balance of said properties, when an intrinsic viscosity of the propylene-ethylene copolymer, an intrinsic viscosity ratio of both components and a product of the intrinsic viscosity ratio and the weight ratio of both components are in a certain range. The present invention relates to a uniaxially stretched or biaxially oriented film as defined in claims 1 to 10. Also disclosed is a process for the production of the propylene composition (A), which comprises conducting a first polymerization step wherein propylene is singly polymerized in a vapor phase in the presence of a catalyst for a stereoregular olefin polymerization which comprises a combination of (a) a titanium-containing solid catalyst component having an average particle size of 25-300 µm, (b) an organoaluminum compound of the formula AlR 1 m X 3-m wherein R 1 is a hydrocarbyl group of 1-20 carbons, X is a halogen atom and m is a positive number of 3≧m≧1.5, and (c) an organosilicon compound of the formula R 2 x R 3 y Si(OR 4 ) z wherein R 2 and R 4 are a hydrocarbyl group, R 3 is a hydrocarbyl group or a hydrocarbyl group containing a hetero atom, X, Y and Z have a relationship of 0≦X≦2, 1≦Y≦3, 1≦Z≦3, and X+Y+Z=4, to produce 78-60 wt.% of a propylene homopolymer (PP) on the total weight basis of the composition, and then conducting a second polymerization step wherein ethylene and propylene are copolymerized, to produce 22-40 wt.% of a propylene-ethylene copolymer (RC) having an ethylene unit of 25-55 wt.%, on the total weight basis of the composition. Also disclosed is a polypropylene composition (C) which comprises the above-mentioned propylene composition (A) as a main component and an additive to be added, if desired. EMBODIMENTS OF THE INVENTION In the propylene composition (A), the propylene homopolymer (PP) is a high crystalline, i.e., stereoregular polypropylene having an isotactic pentad (P) of not less than 0.95, preferably not less than 0.955. The isotactic pentad (P) of the propylene homopolymer (PP) has an effect on the mechanical properties of the molded articles (D) such as rigidity, heat resistance, etc. Higher pentad value provides higher rigidity and heat resistance. The propylene-ethylene copolymer (RC) is an ethylene-propylene random copolymer containing the ethylene polymeric unit of 25 to 55 wt.%, preferably 30 to 55 wt.% on the weight basis of the copolymer (RC). The ethylene polymeric unit in the propylene-ethylene copolymer (RC) has an effect on the rigidity, flexibility, impact resistance, especially low-temperature impact resistance, and stress-whitening resistance of the molded articles (D). Higher ethylene polymeric unit provides more improved flexibility and impact resistance. However, excessive unit affects the dispersibility of propylene-ethylene copolymer (RC) in propylene homopolymer (PP), which results in lowering the transparency, gloss and stress-whitening resistance, etc. of the molded articles (D). For the propylene-ethylene copolymer (RC), the intrinsic viscosity ([η] RC ) as determined in tetralin at 135°C is in the range of 1.7 to 2.8 dl/g, and the ratio ([η] RC /[η] PP ) of the intrinsic viscosity ([η] RC ) of the copolymer to the intrinsic viscosity ([η] PP ) of propylene homopolymer as determined under the same condition is in the range of 0.7 to 1.2, preferably 0.8 to 1.2. Since the intrinsic viscosity ([η] RC ) of propylene-ethylene copolymer (RC) cannot be directly measured, it is derived from the intrinsic viscosity ([η] PP ) of propylene homopolymer (PP) which can be directly measured, the intrinsic viscosity ([η] WHOLE ) of the whole propylene composition (A) and the weight % (W RC ) of propylene-ethylene copolymer (RC), in accordance with the following equation. η RC = [ η ⁢ ] WHOLE - 1 - W RC / 100 [ η ⁢ ] PP / W RC / 100 The intrinsic viscosity ([η] RC ) of propylene-ethylene copolymer (RC) has an effect on the molding cycle of the polypropylene composition (C), the film-forming property when it is formed into film, and the mechanical properties of molded articles (D) such as rigidity, heat resistance, etc. The ratio [[η] RC /[η] PP ] of the intrinsic viscosity of propylene-ethylene copolymer (RC) to propylene homopolymer (PP) affects the dispersibility of propylene-ethylene copolymer (RC) in propylene homopolymer (PP). Higher intrinsic viscosity ([η] RC ) of propylene-ethylene copolymer (RC) provides more improved mechanical properties of molded articles (D), but lowers the molding cycle of the polypropylene composition. If the ratio [[η] RC /[η] PP ] of the intrinsic viscosity of said copolymer to that of propylene homopolymer (PP) is too high or too low, the low-temperature impact resistance and stress-whitening resistance of molded articles (D) become insufficient. Further, if it is too low, the flexibility of molded article (D) becomes insufficient. If it is too high, the improvement effect in the mold shrinkage factor of the polypropylene composition (C) and the transparency of the molded article (D) lowers, so that the desired properties cannot be obtained. The propylene-ethylene copolymer (RC) contains not less than 85 wt.% of a component soluble in xylene at 20°C, on the weight basis of the propylene-ethylene copolymer (RC). Since the weight % (CXS RC ) of the component soluble in xylene at 20°C in the propylene-ethylene copolymer (RC) cannot be directly measured, it is derived from the weight % (CXS PP ) of the component soluble in xylene at 20°C in the propylene homopolymer (PP), the weight % (CXS WHOLE ) of the component soluble in xylene at 20°C in the whole composition (A) and the weight % (W RC ) of the propylene-ethylene copolymer (RC), in accordance with the following equation. CXS RC = CXS WHOLE - 1 - W RC / 100 ⁢ CXS PP / W RC / 100 In the propylene composition (A) the weight ratio (W PP /W RC ) of propylene homopolymer (PP) to propylene-ethylene copolymer (RC) is such that a product [[η] RC /[η] PP ] x (W PP /W RC ) of said weight ratio (W PP /W RC ) and the intrinsic viscosity ratio [[η] RC /[η] PP ] of both components is in the range of 1.0 to 3.0. The product of the weight ratio and the intrinsic viscosity of both components is an index showing the mold shrinkage factor of the polypropylene composition (C). Lower product value provides more improved mold shrinkage factor as well as tear strength and weld strength of molded articles (D), but provides a great reduction in heat resistance and rigidity of molded article (D). On the other hand, higher product value lowers the stress-whitening resistance and does not provide the desired mold shrinkage factor as well as the improvement effects in tear strength and weld strength. More specifically, the propylene composition (A) comprises 22 to 40 wt.%, preferably 25 to 40 wt.% of propylene-ethylene copolymer (RC), on the weight basis of the composition (A). The propylene composition (A) has a narrow dispersing molecular-weight distribution wherein Q value (Mw/Mn) is not more than 5, preferably not more than 4.5. Wider molecular weight distribution lowers the gloss and weld strength of molded articles (D). The propylene composition (A) satisfying the above-mentioned various properties is suitably used as a base resin in the polypropylene composition (C) for the manufacture of molded articles having excellent mechanical properties such as mold shrinkage factor on molding and film-forming property, as well as transparency, gloss, rigidity, flexibility, impact resistance, especially low-temperature impact resistance, tear strength, weld strength, and excellent balance of the properties. The propylene composition (A) may be produced by any method, if it satisfies the above-mentioned properties. For example, the composition can be prepared by mixing propylene homopolymer (PP) and propylene-ethylene copolymer (RC) as produced separately, in a mixing equipment, but it can be suitably prepared by the processes of the present invention. The process for the production of the propylene composition (A) is characterized by producing the propylene homopolymer in a vapor phase in a first stage in the presence of a catalyst for a stereoregular olefin polymerization which comprises (a) a titanium-containing solid catalyst component, (b) an organoaluminum compound and (c) an organosilicon compound (first polymerization step) and successively producing the propylene-ethylene copolymer (second polymerization step). In the process as (a) the titanium-containing solid catalyst component can be used any known components, so long as they are titanium compounds supported on an inorganic carrier such as magnesium, silica and aluminum compounds, or an organic carrier such as polystyrene, and those supported on such carriers reacted with an electron donor compound such as ethers and esters, as is necessary. For example, the catalyst components (a) can include the titanium-containing solid catalyst components produced by spraying an alcohol solution of a magnesium compound, partially drying a solid component and treating the dry solid component with titanium halides and an electron donor compound ( JP-A-3-119003 ) and the titanium-containing solid catalyst component prepared by dissolving a magnesium compound in tetrahydrofuran/alcohol/ electron donor and treating magnesium precipitated by a TiCl 4 alone or a combination thereof with an electron donor, with titanium halides and electron donor compounds ( JP-A-4-103604 ). As the titanium-containing solid catalyst component (a) are used those having an average particle size of 25 to 300 µm, preferably 30 to 150 µm. If the average particle size of the titanium-containing solid catalyst component is not more than 25 µm, the flowability of the powder of the propylene composition (A) is remarkably lost, thus resulting in the contamination within the polymerization system by adhesion of the powders to the wall of the polymerization reactor and the agitating element, etc., and further resulting in difficulty in the transfer of the powders discharged from the polymerization reactor, which leads to a great hindrance to a steady operation. For the titanium-containing catalyst component (a) are preferable those having the uniformity of not more than 2.0 in the normal distribution. If the uniformity exceeds 2.0, the powder flowability of the propylene composition (A) get worse, so that the steady operation continuing the first polymerization step and the second polymerization step becomes difficult. As the organoaluminum compound (b) can be used the organoaluminum compounds of the formula AlR 1 m X 3-m wherein R 1 is a hydrocarbyl group of 1-20 carbons, X is a halogen atom and m is a positive number of 3≧m≧1.5. Specifically, the following compounds are recited; trimethylaluminum, triethylaluminum, tri-n-propylaluminum, tri-n-butylaluminum, tri-iso-butylaluminum, dimethylaluminum chloride, diethylaluminum chloride, methylaluminum sesquichloride, di-n-propylaluminum monochloride, ethylaluminum sesquichloride, ethylaluminum dichloride, diethylaluminum iodide, ethoxydiethylaluminum, etc. Preferably, triethylaluminum is used. These organoaluminum compounds may be used alone or in admixture with two or more kinds. As the organosilicon compound (c) can be used the organosilicon compounds of the formula R 2 X R 3 Y Si(OR 4 ) Z wherein R 2 and R 4 are a hydrocarbyl group, R 3 is a hydrocarbyl group or a hydrocarbyl group containing a hetero atom, X, Y and Z have the relationship of 0≦X≦2, 1≦Y≦3, 1≦Z≦3 and X+Y+Z=4. Specifically, the following compounds are recited, methyltrimethoxysilane, ethyltrimethoxysilane, n-propyltrimethoxysilane, phenylmethyldimethoxysilane, t-butyltrimethoxysilane, phenyltriethoxysilane, methylethyldimethoxysilane, methylphenyldiethoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane, diisopropyldimethoxysilane, diisobutyldimethoxysilane, di-t-butyldimethoxysilane, diphenyldimethoxysilane, trimethylmethoxysilane, cyclohexylmethyldimethoxysilane, trimethylethoxysilane, etc. Preferably, diisobutyldimethoxysilane, diisopropyldimethoxysilane, di-t-butyldimethoxysilane, cyclohexylmethyldimethoxysilane and diphenyldimethoxysilane are used. These organosilicon compounds may be used alone or in admixture with two or more kinds. In the process for the production of the propylene composition (A), it is preferable that the titanium-containing solid catalyst component (a) is preactivated by reaction with α-olefins in the presence of an organoaluminum compound (b') and, as is necessary, an organosilane compound (c'), prior to homopolymerization of propylene in the first polymerization step. For the preactivation of the titanium-containing solid catalyst component (a), the amount of the organoaluminum compound (b') used is not limited, but the compound (b') is usually used in the range of 0.1 to 40 mols, preferably 0.3 to 20 mols per mol of a titanium atom in the titanium-containing solid catalyst component, and it is reacted at 10-80°C over a period of 10 minutes to 48 hours with α-olefin in an amount of 0.1 to 100 grams, preferably 0.5 to 50 grams based on 1 g of the titanium-containing solid catalyst component. For the preactivation, the organosilane compound (c') may be previously used in the range of 0.01 to 10 mols, preferably 0.05 to 5 mols per mole of the organoaluminum compound. The organoaluminum compounds (b') used in the preactivation can include the above-illustrated organoaluminum compounds (b) used for the polymerization of propylene. As the organoaluminum compounds (b') can be used the kinds same as or different from the organoaluminum compound (b) used in the polymerization of propylene. Preferably, triethylaluminum is used. The organosilane compound (c') used in the preactivation as is necessary can include the same kinds as the above-recited organosilicon compounds (c). As the organosilane compounds (c') can be used the kinds same as or different from the organosilicon compound (c) used in the polymerization of propylene. Preferably, diisobutyldimethoxysilane, diisopropyldimethoxysilane, di-t-butyldimethoxysilane, cyclohexylmethyldimethoxysilane and diphenyldimethoxysilane are used. α-olefins used in the preactivation of the titanium-containing solid catalyst component (a) are ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene, 1-eicosene, 4-methyl-1-pentene, 3-methyl-1-pentene, etc. These olefins may be used alone or in admixture with two or more kinds. In the polymerization, a molecular weight modifier such as hydrogen can be used in combination to modify the molecular weight of the polymer. The inert solvents used in the preactivation of the titanium-containing solid catalyst component (a) are those which do not give a remarkable effect on the polymerization reaction, including liquid saturated hydrocarbons such as hexane, heptane, octane, decane, dodecane and liquid paraffin and a silicone oil having a dimethylpolysiloxane structure. These inert solvents may be a single solvent or a mixed solvent of two or more kinds. It is preferable to use these inert solvents after removal therefrom of impurities adversely affecting the polymerization, such as water and sulfur compounds. In the process for the production of the propylene composition (A) there are successively carried out the first polymerization step wherein propylene is polymerized in a vapor phase in the presence of the preactivated titanium-containing solid catalyst component (a) to produce a propylene homopolymer (PP) and then the second polymerization step wherein ethylene and propylene are copolymerized to produce a propylene-ethylene copolymer (RC). The first polymerization step is not limited to a vapor phase polymerization, and may use a slurry polymerization and a bulk polymerization. The subsequent second polymerization step is preferably a vapor phase polymerization. Therefore, the first polymerization step also preferably uses a vapor phase polymerization. In case where slurry and bulk polymerizations are used as the second polymerization step, the propylene-ethylene copolymer (RC) dissolves out in the solution, which results in the difficulty in the continuation of a stable operation. The polymerization conditions for the propylene homopolymer (PP) are varied depending on a polymerization process. For the vapor phase polymerization process, propylene is polymerized at a polymerization temperature of 20 to 120°C, preferably 40 to 100°C and a polymerization pressure of from atmospheric pressure to 9.9 MPa, preferably 0.59 to 5.0 MPa in the presence of a stereoregular catalyst comprising (a) a titanium-containing solid catalyst component which has been preactivated by mixing and agitating prescribed amounts of powders, (b) an organoaluminum component and (c) an organosilicon compound, to produce a propylene homopolymer (A). The ratio, Al/Ti of (b) the organoaluminum compound used to (a) the titanium-containing solid catalyst component used is 1-500 (molar ratio), preferably 10-300. In this case, the number of mols of (a) the titanium-containing solid catalyst component refers to substantially the number of g atoms of Ti in (a) the titanium-containing solid catalyst component. The ratio, b/c of (c) the organosilicon compound used to (b) the organoaluminum component used is 1-10 (molar ratio), preferably 1.5-8. If the molar ratio of b/c is too high, the crystallizability of propylene homopolymer (PP) lowers, resulting in insufficient rigidity of (D) a molded article. If the molar ratio of b/c is too low, the polymerization activity lowers remarkably, resulting in lowered productivity. To modify the molecular weight of propylene homopolymer (PP), a molecular weight modifier such as hydrogen can be used upon polymerization. It is performed so that the intrinsic viscosity of propylene homopolymer (PP) can meet the requirements for the present invention. After the propylene homopolymer (PP) was polymerized, a part of the resultant powders is taken out and used for the measurement of the intrinsic viscosity ([η] PP ), melt flow rate (MFR PP ), amount of a soluble component in xylene at 20 °C, isotactic pentad (P) and polymerization yield per weight of catalyst. Subsequently to the homopolymerization of propylene in the first polymerization step, the second polymerization step is carried out wherein a mixed monomer of ethylene and propylene is copolymerized at a polymerization temperature of 20 to 120°C, preferably 40 to 100°C and a polymerization pressure of from atmospheric pressure to 9.9 MPa, preferably 0.59 to 5.0 MPa, to produce a propylene-ethylene copolymer (RC). The ethylene content in the propylene-ethylene copolymer (RC) is adjusted so as to provide 25 to 55 wt.%, by controlling a gas molar ratio of an ethylene monomer to a propylene monomer in the comonomer gas. The weight of the propylene-ethylene copolymer (RC) relative to the weight of the propylene homopolymer (PP) is adjusted so as to provide 22 to 40 wt.%, by controlling the polymerization time and using an agent for regulating the polymerization activity of the catalyst such as carbon monoxide and hydrogen sulfide. Further, the molecular weight of the propylene-ethylene copolymer (RC) is regulated so that the intrinsic viscosity of the propylene-ethylene copolymer (RC) can meet the requirements for the propylene composition (A), by adding a molecular weight modifier such as hydrogen upon the polymerization of the propylene-ethylene copolymer. Hydrogen is fed so that the Q value (Mw/Mn) of the propylene composition (A) can meet the requirements for the propylene composition (A). The polymerization system may be any of batch, semi-continuous and continuous systems, but a continuous polymerization is industrially preferable. After completion of the second polymerization step, the monomer can be removed from the polymerization system to prepare a particulate polymer. The resultant polymer is used for the measurement of the intrinsic viscosity ([η] WHOLE ), amount of the soluble component in xylene at 20°C, Q value (Mw/Mn), ethylene content and polymerization yield per weight of the catalyst. The polypropylene composition (C) is the composition comprising said propylene composition (A) as a base resin in which a desired additive component is incorporated in compliance with the required properties for the molded article and the molding method. The polypropylene composition (C) may usually contain, within the range that would not adversely affect the object of the invention, various types of additives commonly employed for polyolefin compositions, such as antioxidants, for example, phenol-, thioether- or phosphorous antioxidants; dispersing agents or neutralizing agents, for example, higher aliphatic acid salts (metal soaps), e.g., calcium stearate; light stabilizers; heavy metal inactivators (copper pollution inhibitors); crystal nucleating agents; lubricants such as stearic acid amides; antistatic agents such as aliphatic acid esters, e.g., glycerol monostearate; anti-fogging agents; flame retardants; auxiliaries for flame retardants; pigments; halogen scavengers; organic or inorganic antibacterial agents; inorganic fillers and anti-blocking agents; for example, talc, mica, clay, wollastonite, zeolite, kaolin, bentonite, perlite, diatomaceous earth, asbestos, calcium carbonate, magnesium carbonate, aluminum hydroxide, magnesium hydroxide, hydrotalcite, basic aluminum lithium hydroxycarbonate hydrate, silicon dioxide, titanium dioxide, zinc oxide, magnesium oxide, calcium oxide, barium sulfate, magnesium sulfate, calcium silicate, aluminum silicate, glass fibers, potassium titanate, carbon fibers, carbon black, graphite and metallic fibers; coupling agents, e.g., silane-, titanate-, boron-, aluminate- or zircoaluminate- coupling agents, as well as inorganic or organic fillers surface-treated with any of said coupling agents, for example, wood flours, pulps, wastepapers, synthetic fibers, natural fibers. In general, phenolic antioxidants and/or phosphorus antioxidants, and calcium stearate as neutralizing agents (dispersants) are incorporated in the polypropylene composition (C). The polypropylene compositions (C) having conventional additives incorporated in the above-mentioned polyolefins can be used as such suitably as a polypropylene composition for injection molding (Ci), a polypropylene composition for sheet forming (Cs) and a polypropylene composition for film forming (Cf). Increased rigidity and more improved low-temperature impact resistance of the injection molded articles can be achieved by incorporating in the polypropylene composition (Ci) 0.0001 to 1 part by weight, preferably 0.001 to 0.8 part by weight of an α-crystal nucleating agent based on 100 parts by weight of the propylene composition (A). The α-crystal nucleating agents can include inorganic compounds such as talc, alum, silica, titanium oxide, calcium oxide, magnesium oxide, carbon black, clay minerals; carboxylic acids excluding aliphatic monocarboxylic acids such as malonic acid, succinic acid, adipic acid, maleic acid, azelaic acid, sebacic acid, dodecanic diacid, citric acid, butanetricarboxylic acid, butanetetracarboxylic acid, naphthenic acid, cyclopentanecarboxylic acid, 1-methylcyclopentanecarboxylic acid, 2-methylcyclopentanecarboxylic acid, cyclopentanecarboxylic acid, cyclohexanecarboxylic acid, 1-methylcyclohexanecarboxylic acid, 4-methylcyclohexanecarboxylic acid, 3,5-dimethylcyclohexanecarboxylic acid, 4-butylcyclohexanecarboxylic acid, 4-octylcyclohexanecarboxylic acid, cyclohexanecarboxylic acid, 4-cyclohexane-1,2-dicarboxylic acid, benzoic acid, toluic acid, xylic acid, ethylbenzoic acid, 4-t-butylbenzoic acid, salicylic acid, phthalic acid, trimellitic acid or pyromellitic acid; normal salts or basic salts of said non-aliphatic monocarboxylic acids such as lithium, sodium, potassium, magnesium, calcium, strontium, barium, zinc or aluminum; dibenzylidenesorbitol compounds such as 1.3,2.4-dibenzylidenesorbitol, 1.3-benzylidene-2.4-p-methylbenzylidenesorbitol, 1.3-benzylidene-2.4-p-ethylbenzylidenesorbitol, 1.3-p-methylbenzylidene-2.4-benzylidenesorbitol, 1.3-p-ethylbenzylidene-2.4-benzylidenesorbitol, 1.3-p-methylbenzylidene-2.4-p-ethylbenzylidenesorbitol, 1.3-p-ethylbenzylidene-2.4-p-methylbenzylidenesorbitol, 1.3,2.4-bis(p-methylbenzylidene)sorbitol, 1.3,2.4-bis(p-ethylbenzylidene)sorbitol, 1.3,2.4-bis(p-n-propylbenzylidene)sorbitol, 1.3,2.4-bis(p-i-propylbenzylidene)sorbitol, 1.3,2.4-bis(p-n-butylbenzylidene)sorbitol, 1.3,2.4-bis(p-s-butylbenzylidene)sorbitol, 1.3,2.4-bis(p-t-butylbenzylidene)sorbitol, 1.3-(2'.4'-dimethylbenzylidene)-2.4-benzylidenesorbitol, 1.3-benzylidene-2.4-(2'.4'-dimethylbenzylidene)sorbitol, 1.3,2.4-bis(2',4'-dimethylbenzylidene)sorbitol, 1.3,2.4-bis(3',4'-dimethylbenzylidene)sorbitol, 1.3,2.4-bis(p-methoxybenzylidene)sorbitol, 1.3,2.4-bis(p-ethoxybenzylidene)sorbitol, 1.3-benzylidene-2.4-p-chlorobenzylidenesorbitol, 1.3-p-chlorobenzylidene-2.4-benzylidenesorbitol, 1.3-p-chlorobenzylidene-2.4-p-methylbenzylidenesorbitol, 1.3-p-chlorobenzylidene-2.4-p-ethylbenzylidenesorbitol, 1.3-p-methylbenzylidene-2.4-p-chlorobenzylidenesorbitol, 1.3-p-ethylbenzylidene-2.4-p-chlorobenzylidenesorbitol and 1.3,2.4-bis(p-chlorobenzylidene)sorbitol; arylphosphate compounds such as lithium bis(4-t-butylphenyl)phosphate, sodium bis(4-t-butylphenyl)phosphate, lithium bis(4-cumylphenyl)phosphate, sodium bis(4-cumylphenyl)phosphate, potassium bis(4-t-butylphenyl)phosphate, calcium mono(4-t-butylphenyl)phosphate, calcium bis(4-t-butylphenyl)phosphate, magnesium mono(4-t-butylphenyl)phosphate, magnesium bis(4-t-butylphenyl)phosphate, zinc mono(4-t-butylphenyl)phosphate, zinc bis(4-t-butylphenyl)phosphate, aluminum dihydroxy-(4-t-butylphenyl)phosphate, aluminum hydroxy-bis(4-t-butylphenyl)phosphate, aluminum tris(4-t-butylphenyl)phosphate, sodium 2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate, sodium 2,2'-ethylidene-bis(4,6-di-t-butylphenyl)phosphate, sodium 2,2'-methylene-bis(4-cumyl-6-t-butylphenyl)phosphate, lithium 2,2'-methylene-bis(4, 6-di-t-butylphenyl )phosphate, lithium 2,2'-ethylidene-bis(4,6-di-t-buthylphenyl)phosphate, lithium 2,2'-methylene-bis(4-cumyl-6-t-butylphenyl)phosphate, sodium 2,2'-ethylidene-bis(4-i-propyl-6-t-butylphenyl)phosphate, lithium 2,2'-methylene-bis(4-methyl-6-t-butylphenyl)phosphate, lithium 2,2'-methylene-bis(4-ethyl-6-t-butylphenyl)phosphate, sodium 2,2'-butylidene-bis(4,6-di-methylphenyl)phosphate, sodium 2,2'-butylidene-bis(4,6-di-t-butylphenyl)phosphate, sodium 2,2'-t-octylmethylene-bis(4,6-di-methylphenyl)phosphate, sodium 2,2'-t-octylmethylene-bis(4,6-di-t-butylphenyl)phosphate, sodium 2,2'-methylene-bis(4-methyl-6-t-butylphenyl)phosphate, sodium 2,2'-methylene-bis(4-ethyl-6-t-butylphenyl)phosphate, sodium (4,4'-dimethyl-6,6'-di-t-butyl-2,2'-biphenyl)phosphate, sodium 2,2'-ethylidene-bis(4-s-butyl-6-t-butylphenyl)phosphate, sodium 2,2'-methylene-bis(4,6-di-methylphenyl)phosphate, sodium 2,2'-methylene-bis(4,6-di-ethylphenyl)phosphate, potassium 2,2'-ethylidene-bis(4,6-di-t-butylphenyl)phosphate, calcium bis(2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate, magnesium bis[2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate], zinc bis[2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate], aluminum tris[2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate], calcium bis[2,2'-methylene-bis(4-methyl-6-t-butylphenyl)phosphate], calcium bis[2,2'-ethylidene-bis(4,6-di-t-butylphenyl)phosphate], calcium bis[2,2'-thiobis(4-methyl-6-t-butylphenyl)phosphate], calcium bis[2,2'-thiobis(4-ethyl-6-t-butylphenyl)phosphate, calcium bis[2,2'-thiobis(4,6-di-t-butylphenyl)phosphate], magnesium bis[2,2'-thiobis(4,6-di-t-butylphenyl)phosphate], magnesium bis[2,2'-thiobis(4-t-octylphenyl)phosphate], barium bis[2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate, calcium bis[(4,4'-dimethyl-6,6'-di-t-butyl-2,2'-biphenyl)phosphate], magnesium bis[2,2'-ethylidene-bis(4,6-di-t-butylphenyl)phosphate], barium bis[2,2'-ethylidene-bis(4,6-di-t-butylphenyl)phosphate], aluminum tris[2,2'-ethylidene-bis(4,6-di-t-butylphenyl)phosphate], aluminum dihydroxy-2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate, aluminum dihydroxy-2,2'-methylene-bis(4-cumyl-6-t-butylphenyl)phosphate, aluminum hydroxy-bis[2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate], aluminum hydroxy-bis[2,2'-methylene-bis(4-cumyl-6-t-butylphenyl)phosphate], titanium dihydroxy-bis[2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate], tin dihydroxy-bis[2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate], zirconium oxy-bis[2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate, aluminum dihydroxy-2,2'-methylene-bis(4-methyl-6-t-butylphenyl)phosphate, aluminum hydroxy-bis[2,2'-methylene-bis(4-methyl-6-t-butylphenyl)phosphate], aluminum dihydroxy-2,2'-ethylidene-bis(4,6-di-t-butylphenyl)phosphate or aluminum hydroxy-bis[2,2'-ethylidene-bis(4,6-di-t-butylphenyl)phosphate]; mixtures of cyclic polyvalent metal aryl phosphate compounds among the said aryl phosphate compounds with alkali metal salts of aliphatic monocarboxylic acids such as lithium, sodium or potassium salts of aliphatic monocarboxylic acids, for example, acetic acid, lactic acid, propionic acid, acrylic acid, octanoic acid, isooctanoic acid, nonanoic acid, decanoic acid, lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid, linoleic acid, linolenic acid, 12-hydroxystearic acid, ricinolic acid, behenic acid, erucic acid, montanoic acid, melissic acid, stearoyllactic acid, β-N-laurylaminopropionic acid, β-N-methyl-N-lauroylaminopropionic acid, or basic aluminum lithium hydroxycarbonate hydrate; polymeric compounds such as poly(3-methyl-1-butene), poly(3-methyl-1-pentene), poly(3-ethyl-1-pentene), poly(4-methyl-1-pentene), poly(4-methyl-1-hexene), poly(4,4-dimethyl-1-pentene), poly(4,4-dimethyl-1-hexene), poly(4-ethyl-1-hexene), poly(3-ethyl-1-hexene), polyallylnaphthalene, polyallylnorbornane, atactic polystyrene, syndiotactic polystyrene, polydimethylstyrene, polyvinylnaphthalene, polyallylbenzene, polyallyltoluene, polyvinylcyclopentane, polyvinylcyclohexane, polyvinylcycloheptane, polyvinyltrimethylsilane or polyallyltrimethylsilane. Particularly preferable are talc; aluminum hydroxy-bis(4-t-butylbenzoate); 1.3,2.4-dibenzylidenesorbitol, 1.3,2.4-bis(p-methylbenzylidene)sorbitol, 1.3,2.4-bis(p-ethylbenzylidene)sorbitol, 1.3,2.4-bis(2',4'-dimethylbenzylidene)sorbitol, 1.3,2.4-bis(3',4'-dimethylbenzylidene)sorbitol, 1.3-p-chlorobenzylidene-2.4-p-methylbenzylidenesorbitol, 1.3,2.4-bis(p-chlorobenzylidene)sorbitol; mixtures of aliphatic monocarboxylic acid alkali metal salts with cyclic polyvalent metal arylphosphate compounds such as sodium bis(4-t-butylphenyl)phosphate, sodium 2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate, calcium 2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate, aluminum 2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate, aluminum dihydroxy-2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate or aluminum hydroxy-bis[2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate]; poly(3-methyl-1-butene); polyvinylcyclohexane and polyallyltrimethylsilane. The α-crystal nucleating agent may be used alone or in combination with two or more kinds. The crystalline propylene homopolymer (PHP) to be incorporated is the propylene homopolymer having the density of 0.91 to 0.89 g/cm 3 and the melt flow rate ratio (MFR WHOLE /MFR Ph ) of the propylene composition (A) to the crystalline propylene homopolymer (PHP) ranging from 0.5 to 2, preferably 0.8 to 1.2. The radical generator causes the compound to be highly fluidized and remarkably improves the moldability. For the radical generator, it is desirable that the decomposition temperature is not too low to obtain a uniform composition, and the temperature for obtaining a half-life period of 10 hours is 70°C or higher, preferably 100°C or higher. For example, the following organic peroxides are recited: benzoyl peroxide, t-butylperbenzoate, t-butylperacetate, t-butylperoxyisopropylcarbonate, 2,5-di-methyl-2,5-di-(t-benzoylperoxy)hexane, 2,5-di-methyl-2,5-di-(t-benzoylperoxy)hexyne-3,t-butyl-diperadipate, t-butylperoxy-3,5,5-trimethylhexanoate, methyl ethyl ketone peroxide, cyclohexanone peroxide, di-t-butyl peroxide, dicumyl peroxide, 2,5-di-methyl-2,5-di-(t-butylperoxy)hexane, 2,5-di-methyl-2,5-di-(t-butylperoxy)hexyne-3, 1,3-bis-(t-butylperoxyisopropyl)benzene, t-butylcumyl peroxide, 1,1-bis-(t-butylperoxy)-3,3,5-trimethylcyclohexane, 1,1-bis-(t-butylperoxy)cyclohexane, 2,2-bis-(t-butylperoxybutane), p-methane hydroperoxide, diisopropylbenzene hydroperoxide, cumene hydroperoxide, t-butyl hydroperoxide, p-cymene hydroperoxide, 1,1,3,3-tetramethylbutyl hydroperoxide and 2,5-di-methyl-2,5-di-(hydroperoxy)hexane. In particular, 2,5-di-methyl-2,5-di-(t-butylperoxy)hexane, 2,5-di-methyl-2,5-di-(t-butylperoxy)hexyne-3 and 1,3-bis-(t-butylperoxyisopropyl)benzene are preferable. The radical generators can be used alone or in combination with two or more kinds. The polypropylene composition (C) having conventional additives incorporated in the above-mentioned olefin can be used as the polypropylene composition (Cb) for the formation of blow molded articles. The polypropylene composition (Cb) can be incorporated with 5 to 20 parts by weight of a plasticizing component based on 100 parts by weight of the propylene composition (A) to provide the molded article with flexibility. The plasticizing components (Ps) can include an ethylene homopolymer and ethylene-α-olefin copolymer which are generally called "low-density polyethylene", having the density of 0.910 to 0.930 g/cm 3 , the crystalline melting point (Tm) of 100 to 115°C and the melt flow rate (MFR: 190 °C; 21.18 N) of 0.1 to 5 g/10 min, preferably 0.1 to 1 g/10 min, and an ethylene-vinyl acetate copolymer having the density of 0.92 to 0.935 g/cm 3 , the crystalline melting point (Tm) of 90 to 108°C, and the melt flow rate (MFR: 190°C; 21.18 N) of 0.1 to 5 g/10 min, preferably 0.1 to 1 g/10 min. Since the incorporation of the plasticizing component provides the molded article with flexibility, the polypropylene composition (Cb) is suitable for the formation of films. Sheets can be produced by any of the known sheet molding methods, but are preferably produced by extrusion molding or calendering because of their good productivity. Specifically, the sheets are molded by T-die extrusion method using an apparatus equipped with extruder, T-die, polishing roll (cooling roll), guide roll, take-off roll, trimming cutter, masking, cutter for cutting in desired lengths, stacker and the like (T-die sheet molding machine), or using an apparatus (calendering machine) equipped with Banburry mixer, mixing roll, warming roll, extruder, calender roll, trimming cutter, masking, cutter for cutting in desired lengths, winder and the like. More preferably, the polypropylene compositions (C), preferably the polypropylene compositions (Cs) similar to those mentioned for the injection molding are molded by the method for producing the sheets according to the present invention, namely by the T-die method, by extruding at a resin temperature of from 180 to 300 °C and a cooling roll temperature in the range of 5 to 80°C while setting the temperature difference between the resin temperature and the cooling roll temperature not less than 120°C, and at a sheet speed of 0.1 to 100 m/min. If the resin temperature is in the range of from 180 to 300°C, the polypropylene compositions (Cs) melt sufficiently without thermal deterioration, whereby the melt tension of the sheets will be maintained to provide a good moldability, and the surface of the resulting sheet will not exhibit shark skin pattern to give sheets with an excellent appearance. If the cooling roll temperature is not less than 5°C, spot patterns are not formed on the sheet surface because moisture condensation does not occur on the cooling roll. If it is not higher than 80°C, the sheets can be sufficiently cooled and will not have a linear pattern when the sheet is unrolled, whereby sheets with a good appearance are provided. Because the sheet is weekly molecular-oriented end a difference in heat shrinkage between the longitudinal direction and transverse direction is small, the sheets having an excellent moldability can be obtained by maintaining the following relation between the resin temperature and the cooling roll temperature: Resin temperature - Cooling roll temperature ≧ 120 ⁢ °C If the sheet line speed is not less than 0.1 m/min., sheets with a uniform thickness and a low fraction defective can be obtained with a satisfactory production speed. If it is not more than 100 m/min., the sheets can be sufficiently cooled and linear pattern generation will be prevented upon unrolling, thereby sheets with a good appearance can be obtained. Films according to the present invention produced by molding the above-mentioned polypropylene composition (C), preferably polypropylene composition (Cf) in which conventional additives for polyolefins are added to the propylene compositions (A). The films are uniaxially stretched and biaxially oriented films. Unstretched films can be produced by the T-die method or inflation method which are usually used for production of polyolefin films, and the uniaxially stretched films or biaxially oriented films can be produced by stretching the thus obtained unstretched films by way of uniaxial stretching with a tentering method, or by succesive biaxial orienting or by simultaneous biaxial orienting with a tubular method, respectively. These films are excellent in low-temperature impact resistance, thermal resistance and tear resistance due to the use of the polypropylene compositions (C) containing as a base resin the propylene compositions. Another embodiment of the films is a multi-layered film wherein a functional polymer layer is laminated on one or both of the surface(s) of the above-mentioned films. The multi-layered films are not specially restricted as long as a polymer layer which can provide a special function is laminated on a film comprising the polypropylene composition (C), but have at least a heat sealing layer. As the heat sealing layer can be suitably used propylene homopolymers having the density of 0.89 to 0.91 g/cm 3 and the crystalline melting point of 165 to 160°C and/or propylene-α-olefin copolymers having the density of 0.89 to 0.91 g/cm 3 and the crystalline melting point of 159 to 110°C. The melt flow rate (230°C; 21.18 N) of the polymers used for the heat sealing layer is 0.1 to 50 g/10 min., preferably 1 to 20 g/10 min. from the viewpoints of moldability on molding of the film and appearance of the resulting films. Examples of the α-olefins to be copolymerized with propylene can include ethylene, butene-1, pentene-1, etc. The propylene-α-olefin copolymers can include ethylene-propylene copolymers containing 0.2 to 10% by weight of ethylene component and ethylene-propylene-butene-1-copolymers containing 0.2 to 10% by weight of ethylene component and 0.4 to 5% by weight of butene-1 component. The crystalline melting point of the propylene homopolymer is 165 to 160°C in order to give a multi-layered film having excellent gloss, hardness and rigidity. The crystalline melting point of the propylene-α-olefin copolymer is 159 to 110°C, preferably 140 to 110°C, in order to give a multi-layered film having an excellent heat-sealing property. These propylene homopolymers and propylene-α-olefin copolymers can be produced by conventional polymerization methods through homopolymerization of propylene or copolymerization of propylene and an α-olefin using a catalyst formed from a composite containing at least magnesium, titanium and a halogen, an organometal compound of Groups 1 to 3 metals in periodic table and an electron donor. The multi-layered films are unstretched, uniaxially stretched or biaxially oriented multi-layered films having a layer of the polypropylene composition and the above-mentioned functional polymer layer. The layer configuration of the multi-layered films can include two components-two layers, i.e. functional polymer layer/polypropylene composition layer, and two components-three layers or three components-three layers such as functional polymer layer/polypropylene composition layer/functional polymer layer. Among them, a multi-layered film consisting of propylene homopolymer layer/polypropylene composition layer/propylene-α-olefin copolymer layer is preferred in view of thermal resistance and heat-sealing property of the resulting multi-layered film. The thickness of the multi-layered film is not specially restricted, but is preferably 10 to 100µ, more preferably 15 to 70µ in view of the moldability of the film. The thickness of each layer in the multi-layered film is not specially restricted, but the ratio of the thickness of the propylene composition layer to the total thickness of the film is 30 to 90%, preferably 50 to 90%, in view of low-temperature impact resistance, thermal resistance and tear strength of the multi-layered film. The methods for production of the multi-layered films can include a multi-layer extrusion molding method, a dry laminating method, an extrusion laminating method and the like. The multi-layer extrusion molding methods can include a T-die or inflation method which is usually used for production of polyolefin films. The stretching methods include successive biaxial orienting by a tentering method and simultaneous biaxial orienting by a tubular method. When the multi-layered films are produced according to conventional methods, there is no special restriction in melt flow rates (MFR) of the polypropylene composition and the functional polymer constituting each layer. However, the MFR ratio of the polypropylene composition to the functional polymer is from 0.1 to 10, preferably 0.5 to 2, in view of the moldability of the film and appearance of the film product. The multi-layered films can be produced by laminating the functional polymer layer onto a transparent base film such as BOPP film, PET film, nylon film or Eberl film through an adhesive by the methods such as dry lamination. The films and multi-layered films can be further subjected to surface treatments such as corona discharge treatment, flame treatment, plasma treatment, etc. by using usual industrially-applicable methods for the purpose of providing printability, lamination adaptability and metallizing property. EXAMPLE The present invention will be explained below more in detail by way of the examples and comparative examples. A. Synthesis of propylene composition (A) 1) Measurement of physical properties During synthesis of the propylene compositions, the physical properties of the intermediate products and the final products were measured according to the following methods. Conditions for the synthesis and the results of the measurements are shown in Tables 1 and 2. a) Average particle size (µm) of titanium-containing solid catalyst component (a): Calculated from a particle distribution measured by using Master sizer (manufactured by MALVERN Corporation). b) Degree of uniformity of titanium-containing solid catalyst component (a): Calculated by dividing the particle size in 60% undersize by that of 10% undersize which are obtained from the particle distribution measured by using Master sizer (manufactured by MALVERN Corporation). c) Amount of polymer produced per unit weight of catalyst: Measured by induction bonded plasma spectral analysis (IPC method) of Mg in a sample. d) Isotactic pentad in the polypropylene molecular chain (P): Measured by means of 13 C-NMR according to Macromolecules 8687 (1975). e) Ethylene unit content (% by weight): Measured by Infrared absorption spectroscopy. f) Intrinsic viscosity (dl/g): Measured in a solvent, tetralin (tetrachloronaphthalene), at 135°C by using automatic viscometer (AVS2-type, manufactured by MITSUI TOATSU CHEMICALS, INC.). g) Melt flow rate (g/10 min.): Measured according to JIS K 6760. h) Average molecular weight Q value (Mn/Mw): Measured on a sample dissolved in ortho-dichlorobenze at 135°C by using GPC apparatus (Gel Permeation Chromatograph, Model 150C, manufactured by Waters Corporation, column: TSK GEL GMH6-HT). i) Amount of a soluble component in xylene at 20°C (% by weight): Measured according to ISO/DIS 1873-1. j) Powder flowability: Compressibility of powders was calculated according to the following equation: Compressibility = ( Apparent compact density - Apparent loose density ) × 100 Apparent compact density Higher compressibility provides lower flowability of the powder. 2) Preparation of titanium-containing solid catalyst component (a) a) Titanium-containing solid catalyst component: a-1 In a stainless steel autoclave purged with nitrogen were charged anhydrous MgCl 2 (95.3 g) and absolute EtOH (352 ml), and the mixture was heated at 105°C with stirring and dissolved. After stirring was continued for one hour, the resulting solution was introduced to a two-fluids spray nozzle with a pressurized nitrogen gas (1.1 MPa) heated at 105°C. The flow rate of the nitrogen gas was 38 liters/min. Cooling liquid nitrogen was introduced into the spray tower in which the temperature was maintained at -15°C. The product was collected in cooled hexane introduced at the bottom of the tower to give 256 g of the product. The analysis of the product showed that the composition of the carrier was MgCl 2 · 6EtOH, which was the same as the starting solution. For using as a carrier, 205 g of spherical carrier having the particle size of 45 to 212 µm were taken out by sieving. The carrier was dried by introducing nitrogen gas at the flow rate of 3 liters/min. at room temperature for 181 hours to give a dry carrier composed of MgCl 2 ·1.7 EtOH. The dry carrier (20 g), titanium tetrachloride (160 ml) and purified 1,2-dichloroethane (240 ml) were blended in a glass flask, and heated to 100°C with stirring. Then di-isobutylphthalate (6.8 ml) was added. After heating the mixture for additional 2 hours at 100°C, a liquid layer was removed by decantation. Again, titanium tetrachloride (160 ml) and purified 1,2-dichloroethane (320 ml) were added and the resulting mixture was maintained at 100°C by heating for one hour. A liquid layer was removed by decantation, and the residue was washed with purified hexane and dried to give a titanium-containing solid catalyst component: a-1. The average particle size of the titanium-containing solid catalyst component: a-1 was 115 µm, and the analytical values were as follows: Mg; 19.5% by weight, Ti; 1.6% by weight, Cl; 59.0% by weight, di-isobutylphthalate; 4.5% by weight. b) Titanium-containing solid catalyst component: a-2 In a stainless steel autoclave purged with nitrogen were charged purified kerosine (1,050 ml), anhydrous MgCl 2 (15 g), absolute ethanol (36.3 g) and a surfactant (trade name: EMASOLE 320, produced by KAO ATLAS Co. Ltd.) (4.5 g), and the resulting mixture was elevated with stirring at 800 rpm and maintained at 120°C for 30 minutes. The molten mixture was transferred to a 3,000 ml flask equipped with a stirrer containing 1,500 ml of purified kerosine cooled to -10°C, using a teflon tube of 5 mm inner diameter while stirring the mixture at a high speed. The product was filtered and then thoroughly washed with hexane to obtain a carrier. The carrier (15 g) was suspended in titanium tetrachloride (300 ml) at room temperature, di-isobutylphthalate (2.6 ml) was added, and the resulting suspension was raised to 120°C. After stirring and mixing the suspension at 120°C for two hours, a solid was filtered off and suspended again in titanium tetrachloride (300 ml). After the suspension was stirred and mixed at 130°C for 2 hours, a solid was filtered off and thoroughly washed with purified hexane to give titanium-containing solid catalyst component: a-2. The resulting titanium-containing solid catalyst component: a-2 had an average particle size of 72 µm and the following analytical values: Mg; 21.1% by weight, Ti; 2.4% by weight, Cl; 64.15% by weight, di-isobutylphthalate; 5.3% by weight. c) Titanium-containing solid catalyst component: a-3 A mixture of magnesium ethoxide (300 g), 2-ethylhexanol (550 ml) and toluene (600 ml) was stirred at 93°C for 3 hours in a carbon dioxide atmosphere of 0.20 MPa. Additional toluene (800 ml) and n-decane (800 ml) were added to obtain a magnesium carbonate solution. Toluene (800 ml), chlorobenzene (60 ml), tetraethoxysilane (18 ml), titanium tetrachloride (17 ml) and Isopal G (isoparaffin hydrocarbon having an average carbon number of 10, boiling point: 156-176°C)(200 ml) were stirred at 30°C for 5 minutes, and then the magnesiun carbonate solution prepared above was added. After additionally stirring the mixture for 5 minutes, tetrahydrofuran (44 ml) was added, and the resulting mixture was stirred at 60°C for one hour. After stirring was ceased and a supernatant was removed, the resulting solid was washed with toluene (100 ml), chlorobenzene (200 ml) and titanium tetrachloride (200 ml) were added, and the mixture was stirred at 135°C for one hour. After stirring was ceased and a supernatant was removed, chlorobenzene (500 ml), titanium tetrachloride (200 ml) and d-n-butylphthalate (4.2 ml) were added, and the mixture was stirred at 135°C for 1.5 hours. The supernatant was removed and the solid was washed successively with toluene (1,200 ml), Isopal G (1,600 ml), and hexane (800 ml) to obtain titanium-containing solid catalyst component: a-3 for comparison. The resulting titanium-containing solid catalyst component: a-3 had an average particle size of 18.5 µm, with the following analytical values: Mg; 17.0% by weight, Ti; 2.3% by weight, Cl; 55.0% by weight, di-isobutylphthalate; 7.5% by weight. 3) Pre-activation of titanium-containing solid catalyst component (a) A 15 liters stainless steel reaction vessel equipped with slant vanes was purged with nitrogen gas, and then charged with a saturated hydrocarbon solvent having a dynamic viscosity of 7.3 centistokes at 40°C (CRYSTOL-52, manufactured by Esso Sekiyu Co., Ltd.)(8.3 liters), triethyl aluminum (525 mmol), di-isopropyl-di-methoxysilane (80 mmol) and the titanium-containing solid catalyst component as prepared above (700 g) at room temperature. The mixture was warmed to 40°C and reacted for 7 hours at a propylene partial pressure of 0.15 PMa to pre-activate the catalyst. The result of the analysis indicated that 3.0 g of propylene was reacted per 1 g of the titanium-containing solid catalyst component. 4) Synthesis of propylene homopolymer (PP): first polymerization step Referring to the flow sheet shown in Fig. 3 , a horizontal polymerization reactor equipped with stirring vanes 1 (L/D=6, inside volume: 100 liters) was fed continuously with the pre-activated titanium-containing solid catalyst component at the rate of 0.5 g/hr, triethyl aluminum as the organoaluminum compound (b) and di-isopropyl-di-methoxysilane as the organosilicon compound (c) in such a ratio as to give the Al/Si molar ratio shown in Tables 1 and 2. Propylene was continuously fed to maintain the conditions of the reaction temperature at 70°C, the reaction pressure at 2.5 MPa and the stirring speed at 40 rpm, and hydrogen gas was continuously fed through circulation pipe 2 to adjust the molecular weight of the resulting propylene homopolymer and the intrinsic viscosity of the propylene homopolymer was controlled with the hydrogen concentration in the vapor phase within the reactor. Reaction heat was removed by evaporation of the starting propylene supplied through piping 3. Unreacted gases discharged from the polymerization reactor was cooled and condensed outside the reaction system via piping 4 and returned to polymerization reactor 1. The propylene homopolymer obtained in the polymerization reactor 1 was continuously taken out from said reactor 1 via piping 5 so that the retention level of the polymer occupies 50% volume of the reactor and then introduced into polymerization reactor 10 in the second polymerization step. A part of the propylene homopolymer was intermittently taken out from piping 5 to give a sample for measuring the isotactic pentad (P), amount of a soluble component in xylene at 20°C, intrinsic viscosity ([η]pp) and yield of the polymer per unit weight of the catalyst. 5) Synthesis of propylene-ethylene copolymer (RC): second polymerization step Into a horizontal polymerization reactor equipped with stirring vanes 10 (L/D=6, inner volume: 100 liters), the propylene homopolymer from the first polymerization step and ethylene-propylene mixed gases were continuously fed to copolymerize ethylene and propylene. Reaction conditions were as follows; stirring speed: 40 rpm, temperature: 60°C and pressure: 2.1 MPa. The gas composition in the vapor phase was controlled to give ethylene/propylene and hydrogen/ethylene molar ratios as shown in Tables 1 and 2. Carbon monoxide was supplied as a polymerization inhibitor to control the polymerized amount of the resulting propylene-ethylene copolymer and hydrogen gas was supplied to control the molecular weight of the resulting propylene-ethylene copolymer, both from piping 7. Reaction heat was removed by evaporation of the starting liquid propylene supplied from piping 6. Unreacted gases discharged from the polymerization reactor were cooled and condensed outside the reaction system via piping 8 and returned to the copolymerization step. The propylene composition (A) produced in the copolymerization step was taken out from polymerization reactor 10 via piping 9 so that the retention level of the polymer occupies 50% volume of the reactor. Production rate of the propylene composition (A) was 8 to 12 kg/hr. Monomers were removed from the propylene composition (A) taken from the reactor 10, a part was subjected to the measurement of intrinsic viscosity ([η] WHOLE ), Q value (Mw/Mn), amount of a soluble component in xylene at 20°C, ethylene content of the propylene-ethylene copolymers by infrared spectrum and polymerization ratio of the propylene-ethylene copolymers. The flowability of the powder of the propylene composition (A) was evaluated. By varying the type of the titanium-containing solid catalyst component (a), Al/Si and hydrogen/propylene molar ratios in the first polymerization step, and ethylene/propylene and hydrogen/ethylene molar ratios in the second polymerization step, there were obtained samples A-1 to A-14 of the present invention and comparative samples cA-1 to cA-14. The reaction conditions and the measured results of the physical properties are shown in Tables 1 and 2. Table 1 shows the production conditions and physical properties of the propylene compositions according to the present invention and Table 2 shows those of the comparative propylene compositions. B. Polypropylene compositions (Ci) for injection molding and injection molded articles 1) Polypropylene compositions Each of the powders of the propylene compositions A-1 to A-6 and the comparative compositions cA-1 to cA-7 was incorporated with various additives and mixed at room temperature for 5 to 10 minutes using a high speed stirring mixer (Henschel mixer), and each of the mixtures was pelletized into pellets by an extruding pelletizer with a screw diameter of 40 mm while setting the cylinder temperature at 230°C. Tables 3 and 4 show the additive components and the amounts thereof for the injection molding polypropylene compositions Ci-1 to Ci-12 and Ci-13 to Ci-18 of the present invention, and Tables 5 and 6 show those of comparative compositions cCi-1 to cCi-7 and cCi-13. The additive components and abbreviations appearing in the tables are shown below. Propylene homopolymer PHP 1: a crystalline propylene homopolymer having a melt flow rate MFR PHP of 1 and a melting point of 163°C, which was produced by homopolymerization of propylene using titanium-containing solid catalyst-component a-1 under the following conditions; Al/Si molar ratio: 2, hydrogen/propylene molar ratio: 0.03, polymerization pressure: 2.5 MPa and polymerization temperature: 70°C. PHP 2: a crystalline propylene homopolymer having a melt flow rate MFR PHP of 1.9 and a melting point of 164°C, which was produced by homopolymerization of propylene using titanium-containing solid catalyst component a-1 under the following conditions; Al/Si molar ratio: 2, hydrogen/propylene molar ratio: 0.01, polymerization pressure: 2.5 MPa, and polymerization temperature: 70°C. PHP 3: a comparative crystalline propylene homopolymer having a melt flow rate MFR PHP of 6 and a melting point of 164°C, which was produced by homopolymerization of propylene using titanium-containing solid catalyst component a-1 under the following conditions; Al/Si molar ratio: 2, hydrogen/propylene molar ratio : 0.055, polymerization pressure: 2.5 MPa, and polymerization temperature: 70°C. Antioxidants Ph-1: phenolic thermal stabilizer Ph-2: tetrakis(methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate)methane α-crystal nucleating agents α-1: aluminum hydroxy-bis(4-t-butylbenzoate) α-2: 1.3,2.4-bis(p-methylbenzylidene)sorbitol α-3: sodium 2,2'-methylene-bis(4,6-di-t-butylphenyl)phosphate Radical generator: 1,3-bis(t-butyl-peroxyisopropyl)benzene Neutralizer: calcium stearate Table 4 Composition for injection molding and injection molded article (II) Example No. for injection molding 13 14 15 16 17 18 Polypropylene composition (Ci) No. Ci-13 Ci-14 Ci-15 Ci-16 Ci-17 Ci-18 Propylene composition (A) No. A-1 A-1 A-1 A-5 A-5 A-5 part by weight 100 50 50 100 50 50 Propylene homopolymer type -- PHP-1 PHP-1 -- PHP-2 PHP-2 part by weight -- 50 50 -- 50 50 α-crystal nucleating agent type -- -- -- -- -- -- part by weight -- -- -- -- -- -- Radical generator part by weight 0.02 -- 0.02 0.01 -- 0.01 Antioxidant type Ph-1 Ph-1 Ph-1 Ph-1 Ph-1 Ph-1 part by weight 0.02 0.02 0.02 0.02 0.02 0.02 Neutralizer, calcium stearate 0.02 0.02 0.02 0.02 0.02 0.02 part by weight Physical properties Melt flow rate (MFR) g/10 min. 10 1 11 12 2.3 14 Molding shrinkage % 0.96 1.23 1.2 0.75 1.12 1.1 Flexural modulus MPa 670 850 825 590 820 810 Impact resistance (-20°C) J/m -- -- -- -- -- -- ( 23°C) J/m NB 90 70 NB 100 70 Izod impact strength (-30°C) J/m -- -- -- -- -- -- Haze % 48 60 59 57 63 65 Gloss % 84 87 87 83 86 85 Stress-whitening resistance ○ ○ ○ ○ ○ ○ Table 5 Comparative composition for injection molding and injection molded article (I) Comparative Example No. for injection molding 1 2 3 4 5 6 7 Polypropylene composition (Ci) No. cCi-1 cCi-2 cCi-3 cCi-4 cCi-5 cCi-6 cCi-7 Propylene composition (A) No. cA-1 cA-2 cA-3 cA-4 cA-5 cA-6 cA-7 part by weight 100 100 100 100 100 100 100 Propylene homopolymer type -- -- -- -- -- -- -- part by weight -- -- -- -- -- -- -- α-crystal nucleating agent type -- -- -- -- -- -- -- part by weight -- -- -- -- -- -- -- Radical generator part by weight -- -- -- -- -- -- -- Antioxidant type Ph-1 Ph-1 Ph-1 Ph-1 Ph-1 Ph-1 Ph-1 part by weight 0.1 0.1 0.1 0.1 0.1 0.1 0.1 Neutralizer, calcium stearate 0.1 0.1 0.1 0.1 0.1 0.1 0.1 part by weight Physical properties of molded article Molding shrinkage % 1.08 1.42 1.41 0.98 1.38 1.56 0.62 Flexural modulus MPa 800 900 1100 710 750 770 370 Impact resistance (-20 °C) J/m 70 70 45 400 120 140 NB ( 23°C) J/m -- -- -- -- -- -- -- Izod impact strength (-30°C) J/m -- -- -- -- -- -- -- Haze % 50 75 65 57 66 58 53 Gloss % 88 96 90 85 93 96 77 Stress-whitening resistance Δ × ○ Δ × × ○ Table 6 Comparative composition for injection molding and injection molded article (II) Comparative Example No. for injection molding 8 9 10 11 12 13 Polypropylene composition (Ci) No. cCi-8 cCi-9 cCi-10 cCi-11 cCi-12 cCi-13 Propylene composition (A) No. cA-2 cA-2 cA-2 cA-2 cA-2 cA-2 part by weight 100 100 100 100 50 50 Propylene homopolymer type -- -- -- -- PHP-3 PNP-3 part by weight -- -- -- -- 50 50 α-crystal nucleating agent type α-1 α-2 α-3 -- -- -- part by weight 0.15 0.3 0.2 -- -- -- Radical generator part by weight -- -- -- 0.005 -- 0.005 Antioxidant type Ph-2 Ph-2 Ph-2 Ph-1 Ph-1 Ph-1 part by weight 0.1 0.1 0.1 0.02 0.02 0.02 Neutralizer, calcium stearate 0.1 0.1 0.1 0.02 0.02 0.02 part by weight Physical properties Melt flow rate (MFR) g/10 min. -- -- -- 30 7 35 Molding shrinkage % 1.4 1.4 1.5 1.42 1.46 1.45 Flexural modulus MPa 1150 1070 1100 900 1000 1050 Impact resistance (-20°C) J/m -- -- -- -- -- -- (23°C) J/m -- -- -- 120 80 50 Izod impact strength (-30°C) J/m 101 101 98 -- -- -- Haze % 91 91 91 96 70 70 Gloss % 66 60 63 75 77 78 Stress-whitening resistance -- -- -- × × × 2) Injection molding Each of the pellets as prepared above was molded into a JIS type test piece and a test piece for measuring physical properties, using an injection molding machine in which the molten resin temperature was set at 230°C and the mold temperature at 50°C. The test pieces were conditioned in a chamber kept at a humidity of 50% and at room temperature 23°C for 72 hours, and measured for the physical properties according to the following methods: a) Molding shrinkage: 100 times of the ratio of the length obtained by subtracting the whole length of the tensile test piece (JIS K 7113 No. 1 tensile test piece) from the whole length of the mold of the molding machine to the whole length of the mold, which is calculated from the following equation: Molding shrinkage = ( Whole length of the mold - Whole length of test piece ) × 100 Whole length of the mold b) Flexural modulus (MPa): Measured according to JIS K 7203. c) Impact resistance (J/m): Measured at -20°C or 23°C according to JIS K 7110. d) Izod impact strength (J/m): Measured at -30°C according to JIS K 7110. e) Haze: Measured on a plate-like 25 x 50 x 1 mm test piece according to ASTM D 1003. f) Gloss: Measured at an indication angle of 60 degrees according to ASTM D 523 specular gloss method. g) Stress-whitening resistance: Using a test piece having a hinge structure, a degree of whitening on folding at the hinge portion was visually observed and evaluated according to the following three standards: ○: color at the hinge portion is equivalent to that at the other portions. Δ: color at the hinge portion is slightly whiter than that at the other portions. ×: color at the hinge portion is remarkably whiter than that at the other portions. The measured results are shown in Tables 3 to 6. "NB" in the impact test data means that the test piece did not break under the given conditions. Regarding the inventive samples Ci-1 to Ci-6 and the comparative samples cCi-1 to cCi-6, Fig. 1 shows the relation between a product of the intrinsic viscosity ratio and the weight ratio of the propylene homopolymer to the propylene-ethylene copolymer and the molding shrinkage and Fig. 2 the relation between said product and bending modulus. C. Preparation of sheet molding polypropylene composition (Cs) and sheet 1) Polypropylene composition Each of the powders of the propylene compositions A-1 to A-6 and comparative compositions cA-1, -3, -5 and -7 was incorporated with various additives and mixed at room temperature for 5 to 10 minutes using a high speed mixer (Henschel mixer), and each of the mixtures was granulated into pellets by an extruding granulator with a screw diameter of 40 mm while setting the cylinder temperature at 230°C. Tables 7 and 8 show the additive components and the amounts added to the polypropylene compositions Cs-1 to Cs-6 of the present invention and the comparative compositions cCs-1 to cCs-4. The additive components and abbreviations thereof appearing in the tables are indicated below. Antioxidant P-1: phosphorus thermal stabilizer P-2: tris(2,4-di-t-butylphenyl)phosphite Neutralizer: the same as the above. Table 8 Comparative composition for sheet molding and sheet Comparative Example No. for sheet molding 1 2 3 4 Polypropylene composition (Cs) No. cCs-1 cCs-2 cCs-3 cCs-4 Propylene composition (A) No. cA-1 cA-5 cA-3 cA-7 part by weight 100 100 100 100 Antioxidant type P-2 P-2 P-2 P-2 part by weight 0.1 0.1 0.1 0.1 Neutralizer, calcium stearate 0.1 0.1 0.1 0.1 part by weight Molding conditions Resin temperature °C 230 230 230 230 Cooling roll temperature °C 60 60 60 60 Line speed m/min. 5 5 5 5 Physical properties of sheet Tensile strength at yield point (50°C) MPa 18.6 17.3 22.2 12.1 Young's modulus (23°C) MPa 510 480 617 208 Punching impact resistance (0°C) J ≥3 ≥3 -- -- Whitening on folding mmφ 15 20 -- -- Printability ○ ○ ○ × 2) Sheet molding Each of the compositions as prepared above was molded into a sheet of 5 mm thick by a sheet molding machine equipped with a T-die and a polishing roll at the cylinder temperature, cooling roll temperature and line speed as shown in Tables 9 and 10. The molded sheet was conditioned in a chamber at a humidity of 50% and room temperature 23°C for 72 hours, and measured for the following physical properties. Molding conditions and the measured results of the physical properties are shown in Tables 7 and 8. a) Tensile strength at yield point (MPa): Measured according to ASTM D 882 after allowing to stand in a constant temperature bath at 50°C for 30 minutes or more. b) Young's modulus (MPa): Measured according to ASTM D 882 after allowing to stand in a chamber at 23°C for 48 hours or more. c) Punching impact strength (J): Measured according to ASTM D 781. d) Whitening on folding (mmφ): A sheet of 10 mm in width and 120 mm in length was used as a punching test piece. The both ends of the test piece were gradually allowed to come near to each other to fold the piece and the curvature of the curved portion at the time where a whitening generated thereon was measured. A diameter of the circle corresponding to this curvature was calculated to evaluate a whitening on folding, which was used as an indication of stress-whitening resistance. e) Printing property: Using a gravure printing machine, three color-printing was carried out at a drying temperature of 50°C and a printing speed of 5m/min., and printing shear was visually observed. ○: no shear in printing ×: apparent shear in printing Molding conditions and the measured results of the physical properties are shown in Tables 7 and 8. D. Preparation of polypropylene composition for film (Cf) and its films 1) Polypropylene composition Each of the propylene compositions A-7 to 14, -2, -4 and -5 and the comparative propylene compositions cA-8 to 14, -5 and -6 was incorporated with various additives and mixed using Henshel mixer (trade name), and the mixture was molten kneaded and granulated into pellets by a single screw extruder (bore diameter: 40 mmφ) to obtain polypropylene compositions Cf-1 to Cf-12 for film and comparative compositions cCf-1 to cCf-9 for film. The polypropylene compositions and the comparative compositions are shown in Tables 9 and 10. The additive components used and abbreviations thereof in the tables are indicated below. Antioxidant Ph-2: tetrakis[methylene(3,5-di-t-butyl-4-hydroxyphenyl)propionate]methane P-2: tris(2,4-di-t-butylphenyl)phosphite Neutralizer: calcium stearate Anti-blocking agent: silica Lubricant: oleic amide 2) Molding of single-layer film a) Unstretched film The compositions Cf-1 to Cf-8 and cCf-1 to cCf-7 were extruded using a single-layer extruder (bore diameter: 65 mmφ) equipped with a T-die at an extruding temperature of 230°C, and rapidly cooled by an air chamber and a cooling roll with a surface temperature of 30°C to obtain an unstretched film of 25 µm thick. b) Biaxially oriented film The compositions Cf-9 to Cf-11 and cCf-8 and -9 were extruded using a single-layer extruder (bore diameter: 40 mmφ) equipped with a T-die at an extruding temperature of 230°C, and rapidly cooled and solidified by an air knife and a cooling roll with a surface temperature of 30°C to mold an unstretched sheet of 2.0 mm thick. Then the resulting unstretched sheet was biaxially oriented (5.0 times in the extruding direction and 8.0 times in the transverse direction) using a batch type biaxially orienting machine at a stretching temperature of 157°C to obtain a biaxially oriented film of 50 µm thick. c) Uniaxially stretched film The compositions Cf-9 to Cf-11 and cCf-8 and -9 were extruded using a single-layer extruder (bore diameter: 40 mmφ) equipped with a T-die at an extruding temperature of 230°C, and rapidly cooled and solidified by an air knife and a cooling roll with a surface temperature of 60°C to mold an unstretched sheet of 0.25 mm thick. Then the resulting unstretched sheet was uniaxially stretched 5.0 times in the extruding direction using a batch type uniaxially stretching machine at a stretching temperature of 120°C to obtain a uniaxially stretched film of 50 µm thick. 3) Molding of multi-layered film a) Unstretched film Using the polypropylene compositions Cf-2 and -4, the comparative compositions cCf-1 and -6, as well as the following polyolefin compositions, an unstretched film of two components-three layers or three components-three layers was prepared. Polyolefin composition PO-1: A composition in the form of pellets obtained by incorporating 99.49% by weight of a propylene homopolymer having the density of 0.90 g/cm 3 , the crystalline melting point of 163°C and the melt flow rate (MFR) of 7.0 g/10 min., with 0.03% by weight of tetrakis[methylene(3,5-di-t-butyl-4-hydroxyphenyl)propionate]methane, 0.08% by weight of tris(2,4-di-t-butylphenyl)phosphite, 0.1% by weight of calcium stearate, 0.2% by weight of silica (anti-blocking agent) and 0.1% by weight of oleic amide (lubricant), and mixing by Henschel mixer (trade name), melt-kneading using a single screw extruder (bore diameter: 40 mmφ), and molding the mixture into pellets. PO-2: A composition in the form of pellets obtained by incorporating 99.49% by weight of a propylene-ethylene-butene-1 copolymer having the density of 0.90 g/cm 3 , the crystalline melting point of 132°C and the melt flow rate (MFR) of 6.0 g/10 min., with 0.03% by weight of tetrakis[methylene(3,5-di-t-butyl-4-hydroxyphenyl)propionate]methane, 0.08% by weight of tris(2,4-di-t-butylphenyl)phosphite, 0.1% by weight of calcium stearate, 0.2% by weight of silica (anti-blocking agent), and 0.1% by weight of oleic amide (lubricant), and mixing by Henschel mixer (trade name), melt-kneading using a single screw extruder (bore diameter: 40 mmφ), and molding the mixture into pellets. Using an extruder for molding a film of three components-three layers, equipped with a multi-layer T-die (including one single screw extruder for intermediate layers having a bore diameter of 65 mmφ, and two single screw extruders for surface layers having a bore diameter of 50 mmφ), the polypropylene composition was fed to the single screw extruder for intermediate layers, and the polyolefin composition was fed to the single screw extruders for surface layers, and these compositions were molten at 230°C, subjected to multi-layers (two components-three layers or three components-three layers) co-extrusion, and then cooled and solidified in an air chamber and a cooling roll with a surface temperature of 30°C to obtain an unstretched film of two components-three layers or three components-three layers. The layer configuration is shown in Tables 11 and 12. b) Biaxially oriented film Using the three components-three layers extruder equipped with a multi-layer T-die (including one single screw extruder for intermediate layers having a bore diameter of 65 mmφ, and two single screw extruders for surface layers having a bore diameter of 50 mmφ), the polypropylene composition Cf-12 or cCf-8 was fed to the single screw extruder for intermediate layers, and the polyolefin composition was fed to the single screw extruders for surface layers, and these compositions were molten at 230°C, subjected to multi-layers (two components-three layers) co-extrusion, and then cooled and solidified by an air knife and a cooling roll with a surface temperature of 30°C to obtain an unstretched sheet of two components-three layers of 2.0 mm thick (thickness ratio: 1/18/1). Then the resulting unstretched sheet was biaxially oriented (5.0 times in the extruding direction and 8.0 times in the transverse direction) using a batch type biaxially orienting machine at a stretching temperature of 157°C to obtain a biaxially oriented film of 50 µm thick. The layer configuration is shown in Tables 11 and 12. Table 11 Multi-layered film (Example) Example No. for film molding 13 14 15 16 17 18 Layer configuration Intermediate layer, Cf-2 Cf-4 Cf-2 Cf-4 Cf-12 Cf-12 polypropylene composition (Cf) Skin layer 1, polyolefin composition PO-2 PO-2 PO-1 PO-1 PO-1 PO-2 Skin layer 2, polyolefin composition PO-2 PO-2 PO-2 PO-2 PO-1 PO-2 Physical properties of unstretched multi-layer film Transparency (haze) % 2.2 1.8 2.3 1.8 -- -- Gloss % 115 119 116 119 -- -- Tear strength in extruding 40 23 38 23 -- -- direction N/mm Cold resistance temperature °C -25 -20 -20 -15 -- -- Heat resistance °C 135 140 140 145 -- -- Heat-sealing temperature °C -- -- 130 130 -- -- Physical properties of biaxially oriented film Transparency (haze) % -- -- -- -- 0.2 1.8 Tensile strength at fracture -- -- --- -- 150 130 in extruding direction MPa Heat-sealing temperature °C -- -- -- -- -- 130 Table 12 Multi-layered film (Comparative Example) Comparative Example No. for film molding 10 11 12 13 14 Layer configuration Intermediate layer, cCf-1 cCf-6 cCf-6 cCf-8 cCf-8 polypropylene composition (Cf) Skin layer 1, polyolefin composition PO-2 PO-2 PO-1 PO-1 PO-2 Skin layer 2, polyolefin composition PO-2 PO-2 PO-2 PO-1 PO-2 Physical properties of unstretched multi-layer film Transparency (haze) % 4.2 6.7 6.8 -- -- Gloss % 90 81 80 -- -- Tear strength in extruding 10 8 8 -- -- direction N/mm Cold resistance temperature °C -25 -25 -20 -- -- Heat resistance °C 135 135 140 -- -- Heat-sealing temperature °C -- -- 130 -- -- Physical properties of biaxially oriented film Transparency (haze) % -- -- -- 12.7 10.4 Tensile strength at fracture -- -- -- 110 90 in extruding direction MPa Heat-sealing temperature °C -- -- -- -- 130 4) Physical properties of films The single layer films and the multi-layered films were evaluated with regard to the following physical properties. a) Transparency (%): Haze of the film was measured according to ASTM D 1003, and used as a standard of transparency. b) Gloss (%): Gloss of the film was measured at an angle of 20° according to ASTM D 523. c) Tear strength (N/mm): Elmendorf tear strength of the film was measured according to ASTM D 1922. d) Tensile strength at break (MPa): Tensile strength at break of the film was measured according to ASTM D 882. e) Tensile elongation at break (MPa): Tensile elongation at break of the film was measured according to ASTM D 882. f) Cold resistance temperature (°C): After retaining a film in a bath at a constant cold temperature for 15 minutes, an impact strength of the film was measured according to ASTM D 781. When the film which had been retained in the bath at a cold temperature had an impact strength of not less than 0.5 J, the temperature of the bath at that time was expressed as a cold resistance temperature. g) Heat resistance (°C): A sample of 10 x 100 mm strip which had been cut out from the film was retained in a silicone oil bath set at a predetermined temperature for 10 minutes, and measured for the length in longer direction. When the length of the sample is decreased by more than 2% based on its initial length, the temperature of the oil bath in which the sample was retained was expressed as a heat resistance. h) Heat sealing temperature (°C): The film was dry laminated with a biaxially oriented polypropylene film (20 µ) by using an adhesive, and the laminated film was heat-sealed over 10 mm width at a sealing pressure of 2 MPa for 0.5 second at sealing temperatures ranging from 130°C to 190°C with a temperature difference of 5°C (8 temperature conditions in total). Using a 15 mm wide strip sample cut out from the film, a peel test was carried out at the different sealing temperatures on the sealed part of the sample at 90°C by measuring the peel strength by means of a tensile machine at a tensile speed of 300 mm/min. When the sealed part had a peel strength not less than 0.5 N/15 mm, the corresponding minimum sealing temperature was expressed as the heat sealing temperature. The results of the evaluation on the single-layer films are shown in Tables 9 and 10, and those on the multi-layered films are shown in Tables 11 and 12. EFFECT OF THE INVENTION The propylene compositions are suitably used as a base resin of the polypropylene compositions for producing various molded articles which are excellent in moldability, molding shrinkage, rigidity, flexibility, impact resistance, particularly low-temperature impact resistance, transparency, gloss and stress-whitening resistance, and which are well balanced in these properties. The single-layer films molded from the polypropylene compositions including as a base resin the propylene compositions provide biaxially oriented and uniaxially stretched films which are excellent in transparency and heat resistance and which are well balanced in mechanical properties such as tear strength, tensile strength at break, tensile elongation at break and low-temperature impact resistance, as shown in Tables 9 and 10. The multi-layered films of the polypropylene compositions and the polyolefin compositions have an excellent heat sealing property while maintaining the properties of the above-mentioned single-layer films, as shown in Tables 11 and 12. These films are suitable as various packaging films including those for foods. BRIEF EXPLANATION OF DRAWINGS Fig. 1 shows a curve representing a molding shrinkage relative to the product ([η] RC /[η] PP ) x (W PP /W RC ) of the intrinsic viscosity ratio and the weight ratio of the propylene homopolymers (PP) to the propylene-ethylene copolymers (RC). Fig. 2 shows a curve representing a bending modulus relative to the product ([η] RC /[η] PP ) x (W PP /W RC ) of the intrinsic viscosity ratio and the weight ratio of the propylene homopolymers (PP) to the propylene-ethylene copolymers (RC). Fig. 3 is a flow sheet of the continuous polymerization apparatus for the propylene compositions used in the examples. Explanation on symbols 1, 10: polymerization reactor, 2: piping for hydrogen, 3: piping for starting propylene, 4, 8: piping for unreacted gases, 5, 9: piping for removing polymers, 6: piping for starting mixed gases.

Claims: A uniaxially stretched or biaxially oriented film made from a polypropylene composition comprising a propylene composition comprising a propylene homopolymer and 22-40 wt.% of a propylene-ethylene copolymer, on the weight basis of the propylene composition the propylene-ethylene copolymer containing 25-55 wt.%.of an ethylene unit on the weight basis of the propylene-ethylene copolymer, characterized in that the propylene-ethylene copolymer contains not less than 85 wt.% of a component soluble in xylene at 20 °C on the weight basis of the propylene-ethylene copolymer and that the intrinsic viscosity ([η] RC ) of the propylene-ethylene copolymer is in the range of 1.7 to 2.8 dl/g, the ratio ([η] RC /[η] PP ) of the intrinsic viscosity of the propylene-ethylene copolymer to the intrinsic viscosity of the propylene homopolymer is in the range of 0.7 to 1.2 and the product [(W pp /W RC )x([η] RC /[η ] pp )] of the weight ratio (W pp /W RC ) of the propylene homopolymer to the propylene-ethylene copolymer and the intrinsic viscosity ratio ([η] RC /[η] pp ) thereof is in the range of 1.0 to 3.0 as a base resin. The film of claim 1 wherein the polypropylene composition comprises an antioxidant and a neutralizer. The film of claim 2, wherein the antioxidant is a phenolic heat stabilizer and/or a phosphorus heat stabilizer, and the neutralizer is calcium stearate. The film of any of claims 1-3, wherein the polypropylene composition further comprises 0.0001-1 wt.% of an α-crystal nucleating agent. The film of Claim 4 wherein the α-crystal nucleating agent is talc, metal aromatic carboxylates, dibenzylidene sorbitol compounds, metal aromatic phosphates, poly(3-methyl-1-butene), polyvinylcyclohexane, polyallyltrimethylsilane or a mixture thereof. The film of any of claims 1-5, wherein the polypropylene composition, further comprises a radical generator. The film of Claim 6 wherein the radical generator is an organic peroxide. The film of any of claims 1-7, wherein the polypropylene composition, further comprises 10-95 wt.%, on the basis of the resin, of propylene homopolymer having a density of 0.91-0.89 g/cm 3 and a melt flow rate ratio of the homopolymer to the propylene composition being in the range of 0.5-2. The film of any of claims 1-8, wherein the polypropylene composition, further comprises 5-20 parts by weight of a flexibilizing component based on 100 parts by weight of the polypropylene composition. The film of Claim 9 wherein the flexibilizing component is an ethylene homopolymer or an ethylene-α-olefin copolymer having the density of 0.910-0.930 g/cm 3 and the crystalline melting point (Tm) of 100-115°C and/or an ethylene-vinyl acetate copolymer having the density of 0.92-0.935 g/cm 3 , the crystalline melting point (Tm) of 90-108°C and the vinyl acetate unit of 1-10 wt.%.

Inventors: GOUDA KUNIO, ISHII HIROHISA, KAWANO SHOUJI, KIMURA KAZUHIRO, KIMURA MASAMI, MOCHIZUKI YASUHIRO, NAKAGAWA YASUHIKO, NAKASHIMA TAKANORI, OKAYAMA CHIKASHI, SAITO NORIAKI, SUGIMOTO MASATAKA, WAKATA MAYUMI, YAMAMOTO TOSHIKI, YOKOTA JUNICHIRO, GOUDA, KUNIO, ISHII, HIROHISA, KAWANO, SHOUJI, KIMURA, KAZUHIRO, KIMURA, MASAMI, MOCHIZUKI, YASUHIRO, NAKAGAWA, YASUHIKO, NAKASHIMA, TAKANORI, OKAYAMA, CHIKASHI, SAITO, NORIAKI, SUGIMOTO, MASATAKA, WAKATA, MAYUMI, YAMAMOTO, TOSHIKI, YOKOTA, JUNICHIRO, NAKAGAWA, Yasuhiko Chisso Petrochemical Corp., SUGIMOTO, Masataka C/O Chisso Petrochemical Corp.
Applicants: CHISSO CORP, CHISSO CORPORATION
Application year: 1996
Main classification: C08F297
IPC codes: C08L53, C08F297, C08L51, B29K23, C08F210, B32B27, C08L23, C08F110, C08F255, C08J5