Intergrated microstructures and a method of fabricating thereof

Abstract: The method includes the steps of: forming a sacrificial buried region of insulating material on a substrate (1); growing a semiconductor material layer (8) presenting a polycrystalline region (80) over the sacrificial buried region, and a monocrystalline region (81) elsewhere; selectively removing portions of the polycrystalline region (80) to form a trench (20) extending from the upper surface (11) Of the semiconductor material layer to the sacrificial buried region; and removing the sacrificial buried region via the trench (20). The portion (80') of the polycrystalline region (80) surrounded by the trench (20) thus forms a suspended structure separated and isolated thermally from the rest (80'', 81) of the semiconductor material layer. Using microelectronics processes, electronic components (12-14) are formed in the monocrystalline region (81), and dedicated regions (24) are formed at the suspended structure, so that the electronic components are integrated in the same chip with static, kinematic or dynamic microstructures (30).

Description: The present invention relates to a method of fabricating integrated microstructures of semiconductor material. As is known, micromachining, based on fabrication technologies typical of microelectronics, provides for fabricating microsystems such as microsensors, microactuators and special micromechanisms using the know-how and advantages typical of microelectronics processes. In the past, such microstructures have preferably been fabricated by bulk micromachining, whereby a silicon wafer is processed on both faces to exploit the excellent mechanical properties of monocrystalline silicon. Front-rear processing, however, and the need for particular handling of the wafers make bulk micromachining incompatible with current integrated circuit fabrication technology. Another microsystem fabrication technique employs etching solutions such as ethyldiaminapyrocatechol (EDP), and the structure is formed and separated from the substrate by etching the massive silicon from the front of the wafer using what is known as the "front bulk micromachining" technique. In the mid 80s, what is known as "surface micromachining" was proposed, whereby the sensitive element or micromechanism is formed of polycrystalline silicon, and which provides for forming suspended structures by depositing and subsequently removing sacrificial layers of different types, e.g. silicon oxide or nitride, porous silicon, aluminium, photoresist, polyimide, etc. An example of this technique is described in US-A-4 744 863. A general review of surface micromachining technology (as well as bulk micromachining and the characteristics of each) is to be found, for example, in the article entitled "Micromachining and ASIC technology" by Axel M. Stoffel, in Microelectronics Journal, 25 (1994), p. 145-156. Surface micromachined suspended structures, however, are characterized by poor flexural rigidity, and a tendency to collapse on to the underlying layer, thus impairing thermal or mechanical isolation. In the early 90s, a further microstructure fabrication technique, known as "silicon fusion bonding", was devised, whereby a cavity is formed in a monocrystalline silicon wafer onto which a further monocrystalline silicon wafer, in which the sensor is formed, is bonded. A similar microstructure fabrication technique employs dedicated or nondedicated SOI (silicon-on-Insulator) substrates. An example of this technique is described in US-A-5 369 544, to which the preambles of claims 1 and 12 refer. Other highly specialized techniques, such as "wafer dissolving", provide for forming silicon microstructures by means of dedicated processes which are totally incompatible with standard planar microelectronics technology. In a sense, these "ad hoc" processes simply consist in transferring on to silicon what is currently done using other materials, and only provide for fabricating the sensitive portion, so that the processing and control circuit must be formed on a separate chip. Yet another highly specialized technique is the LIGA method - a German acronym for Lithographie Galvanoformung Abformung - which comprises three processing steps: synchrotron x-ray lithography; galvanic deposition of metal films; and formation of plastic molds (see, for example, S.M.Sze's "Semiconductor Sensors", John Wiley & Sons, Inc., Chapter 2, p. 75-78). None of the above methods, however, provides for fabricating low-cost sensors comparable with those of microelectronics technology, using known, highly controllable, noncritical fabrication steps, and which may be integrated with the control electronics in one chip. It is an object of the present invention to provide a method of fabricating microstructures of semiconductor material, designed to overcome the drawbacks typically associated with current technology. According to the present invention, there are provided an integrated microstructure and a method of fabricating integrated microstructures of semiconductor material, as claimed in claim 1 and in claim 12, respectively. In practice, according to the present invention, a buried silicon oxide region is formed on the starting wafer (substrate); the epitaxial layer for integrating the integrated circuit is grown; a polycrystalline silicon region for forming the sensitive element or micromechanism is formed over the buried region; and, after forming the electronic components, the buried region is etched via trenches in the polycrystalline silicon region to form a suspended region by which to form static, kinematic or dynamic microstructures. Two preferred, non-limiting embodiments of the present invention will be described by way of example with reference to the accompanying drawings, in which: Figures 1-5 show cross sections of a wafer of semiconductor material at successive steps in the fabrication method according to the present invention; Figures 6 and 7 show smaller-scale cross sections, as in Figures 1-5, at successive steps in the method according to the present invention; Figure 8 shows a top plan view of a portion of the Figure 7 wafer; Figure 9 shows a section, as in Figures 1-7, of a second embodiment of the fabrication method according to the present invention; Figures 10-14 show sections, as in Figures 1-7, of a third embodiment of the present invention. With reference to Figure 1, in the fabrication method according to the present invention, a silicon oxide layer 2 is formed, e.g. grown thermally, on a substrate 1 forming a monocrystalline silicon wafer; a silicon nitride layer 3 is deposited over oxide layer 2; a phototechnical and etching step are performed on the portion of the nitride in which the microstructure is to be formed; after removing of the resist masking layer the intermediate structure in Figure 1 is obtained in which nitride layer 3 presents a window 4. At this point, silicon oxide layer 2 and substrate 1, masked by nitride layer 3, are etched successively to obtain the intermediate structure shown in Figure 2 in which oxide layer 2 and part of substrate 1 present a recess 5, which is subsequently filled (Figure 3) with a thermally grown oxide region 6 (hereinafter also referred to as a buried oxide region). At this point, silicon nitride layer 3 is removed; an amorphous or polycrystalline silicon layer 7 is deposited, as shown in Figure 4; and, by means of a phototechnical and chemical etching step, polysilicon layer 7, with the exception of the portion over oxide region 6, and oxide layer 2 over substrate 1 are removed to obtain, over oxide region 6, a silicon region 7' representing the germ for the next step of growing the epitaxial layer. If called for in the process, doping species are implanted to form buried structures (such as buried layer 9 in Figure 6); and an epitaxial layer 8 is grown presenting a polycrystalline structure (polysilicon region 80) over buried oxide region 6, and a monocrystalline structure (epitaxial region 81) elsewhere, as shown in Figure 5. This is followed by standard integrated circuit fabrication steps. More specifically, as shown in Figure 6, P-type junction isolation regions 10, extending from surface 11 of epitaxial layer 8 to substrate 1, and an NPN transistor, presenting an N + type collector contact region 12, a P-type base region 13, and an N-type emitter region 14, are formed in N-type epitaxial layer 8. If necessary, diffused regions for implementing the microsensors, microactuators or micromechanisms provided for in the process may be formed simultaneously with the integrated circuit. For example, in known manner, when implanting the base region 13 of the NPN transistor, a heating element (not shown) may be formed in the case of a chemoresistive gas sensor, and piezoresistive elements (not shown) may be formed in the case of a pressure sensor. A dielectric layer 15 is then deposited and metal contacts 16 formed to obtain the structure shown in Figure 6, which also shows the N + type buried layer 9. At this point, the suspended structures are formed by means of a phototechnical and chemical etching step to remove portions of dielectric layer 15 and of polysilicon region 80 over buried oxide region 6, and so form a trench 20 extending from dielectric layer 15 (included) to buried oxide region 6 as shown in Figure 6. Trench 20 preferably extends in a closed line, e.g. along the sides of a rectangle (Figure 8) or along the circumference of a circle, so as to laterally define inner portions 80', 15' of polysilicon region 80 and dielectric layer 15, and separate them from respective outer portions 80", 15", with the exception of connecting and supporting arms 22 extending between inner portions 80', 15' and respective outer portions 80", 15". Trench 20 advantageously extends close to the periphery of buried oxide region 6. Subsequently, buried oxide region 6 is removed using hydrofluoric acid to form an opening also called air gap 21 beneath inner polysilicon portion 80' (Figure 7). The inner polysilicon portion 80 thus forms a suspended region, that may be used to form structures isolated thermally or mechanically from the substrate (static structures such as chemoresistive gas or piezoresistive pressure sensors), movable structures able to detect external signals due to their movement (kinematic structures such as flow or motion sensors), or mechanical structures (dynamic structures such as micromotors or microactuators. Before or after buried oxide region 6 is removed, regions or layers are formed according to the type of structure to be fabricated. For example, before forming trench 20, a tin oxide film 24 may be deposited and defined over inner polysilicon portion 80' and respective inner dielectric portion 15' to form a chemoresistive gas sensor shown schematically by 30 in the Figure 8 plan view, in which the dotted line 25 indicates the edge of opening 21, and which shows trench 20 separating inner and outer dielectric portions 15' and 15". According to a further embodiment of the invention, the buried oxide region is grown directly by local oxidation, without forming recess 5 beforehand, thus eliminating etching of oxide layer 2 and substrate 1. According to this variation, shown in Figure 9, the intermediate structure in Figure 1, masked by nitride layer 3, is oxidized locally to form an oxide region 6' at window 4, and typical "beaks" beneath nitride layer 3; at which point, nitride layer 3 is removed, silicon layer 7 is deposited as shown in Figure 4, and the successive steps shown in Figures 5-8 are performed. According to a third embodiment shown in Figures 10-14, the buried oxide region is formed by depositing and defining an oxide layer. More specifically, a silicon oxide layer 60 is formed, e.g. grown thermally, on substrate 1 (Figure 10); by means of known photolithographic techniques, oxide layer 60 is defined to form a region 60' (Figure 11); amorphous or polycrystalline silicon layer 7 is deposited (Figure 12); layer 7 is etched and removed, except for the portion over buried oxide region 60' (Figure 13, which shows the remaining portion 7' of silicon layer 7); the epitaxial layer is grown to give the structure in Figure 14 corresponding to Figure 5, and showing polysilicon region 80 and epitaxial region 81; and the steps described above with reference to Figures 6 and 7 are then performed. The advantages of the fabrication method described are as follows. In particular, suspended region 80' is thicker, and therefore presents better mechanical characteristics and fewer signal processing problems as compared with deposited films. In the event the suspended structure is used to form a pressure sensor, this is more sensitive as compared with similar types formed using deposited films. Being formed by means of an epitaxial layer, the suspended structure presents a high degree of flexural rigidity, is therefore highly unlikely to collapse and adhere to the substrate, and therefore presents better mechanical characteristics as compared with surface micromachined structures. The suspended structure may be integrated with electronic control components on one chip; and may be formed using only three additional masks as compared with standard analog/digital fabrication processes, i.e. for defining buried oxide region 6, 6', 60', defining deposited polysilicon layer 7, and etching trench 20. The method described is extremely low-cost as compared with those involving the use of SOI or silicon-fusion-bonded substrates. Finally, the structure may be formed to the desired degree of flatness. That is, the embodiment in Figures 2 and 3 may be used in cases requiring a highly flat chip; and the Figure 9 and Figure 10-14 embodiments when flatness is not particularly essential. Clearly, changes may be made to the method as described and illustrated herein without, however, departing from the scope of the present invention. In particular, isolation regions 10 in epitaxial layer 8 may be of a type other than that shown, e.g. dielectric as opposed to junction; the electronic components integrated in the same chip may be both bipolar and MOS types; the conductivity of the various regions may be other than as shown; and the structure may be used for any sensor or mechanism employing suspended regions of the type described.

Claims: A method of fabricating integrated microstructures of semiconductor material comprising the sequential steps of: forming a sacrificial buried region (6, 6', 60') of insulating material on a substrate (1) of monocrystalline semiconductor material; epitaxially growing a first semiconductor material layer (8) on said substrate (1); said first semiconductor material layer consisting of a polycrystalline region (80) over said sacrificial buried region, and a monocrystalline region (81) over the monocrystalline portion of said substrate; and said substrate and said first semiconductor material layer surrounding said sacrificial buried region (6, 6', 60'); selectively removing portions of said polycrystalline region (80) to form a trench (20) extending from a surface (11) of said first semiconductor material layer to said sacrificial buried region (6, 6', 60'); and removing said sacrificial buried region (6, 6', 60') via said trench (20). A method as claimed in Claim 1, characterized in that said step of forming a sacrificial buried region comprises the steps of: masking said substrate (1) with a mask (3) of nonoxidizable material presenting a window (4); and thermally growing said sacrificial buried region (6) at said window. A method as claimed in Claim 2, characterized in that said step of masking said substrate (1) comprises the steps of: forming an oxide layer (2) over said substrate (1); depositing a nitride layer (3) over said oxide layer; and defining said nitride layer to form said mask. A method as claimed in Claim 3, characterized by the steps of: removing a portion of said oxide layer (2) at said window (4) following said step of masking said substrate (1); and removing a portion of said substrate (1) at said window to form a recess (5) in the substrate; and in that said thermally growing step comprises the step of growing said sacrificial buried region (6) to fill said recess (5). A method as claimed in Claim 2 or 3, characterized in that said thermally growing step comprises the step of locally oxidizing (6') said substrate (1) at said window (4). A method as claimed in Claim 1, characterized in that said step of forming a sacrificial buried region comprises the steps of: growing an oxide layer (60) over said substrate (1); and lithographically defining (60') said oxide layer (60). A method as claimed in any one of the foregoing Claims, characterized in that said step of growing a first semiconductor material layer (8) is preceded by the steps of: depositing, on said substrate (1), a second semiconductor material layer (7) covering said sacrificial buried region (6, 6', 60'); and selectively removing said second semiconductor material layer (7) to form a germ region (7') over said sacrificial buried region (6, 6', 60'). A method as claimed in Claim 7, characterized in that said second semiconductor material layer (7) consists of amorphous silicon. A method as claimed in Claim 7, characterized in that said second semiconductor material layer (7) consists of polycrystalline silicon. A method as claimed in any one of the foregoing claims, characterized in that said step of selectively removing portions of said polycrystalline region is preceded by the steps of: forming, in said first semiconductor material layer, regions of opposite conductivity (12-14) defining integrated electronic components; forming a dielectric layer (15) over said first semiconductor material layer (8); and forming electric contact regions (16) of electrically conductive material. A method as claimed in Claim 10, characterized in that said step of forming electric contact regions (16) is followed by a step of forming regions (24) of a microstructure (30). An integrated microstructure of semiconductor material, comprising a substrate (1) of monocrystalline semiconductor material and a semiconductor material layer (8) over said substrate, said semiconductor layer including a monocrystalline portion (81), an opening (21) being located between facing portions of said substrate (1) and of said semiconductor layer (8); characterized in that said monocrystalline portion (81) directly contacts said substrate (1), that said semiconductor material layer (8) includes a polycrystalline portion (80) overlying said opening (21) and supporting integrated microsensors and microsystems (30) and that a trench (20) extends between an outer surface (11) of the polycrystalline portion of said semiconductor material layer (8) and said opening (21). A microstructure as claimed in Claim 12, characterized in that said trench (20) defines an inner portion (80') of said polycrystalline region (80) except for connecting and supporting portions (22) extending between said inner portion (80') of said polycrystalline region and outer regions (80") of said semiconductor material layer (8).

Inventors: FERRARI PAOLO, FORONI MARIO, VIGNA BENEDETTO, VILLA FLAVIO, FERRARI, PAOLO, FORONI, MARIO, VIGNA, BENEDETTO, VILLA, FLAVIO
Applicants: ST MICROELECTRONICS SRL, STMICROELECTRONICS S.R.L.
Application year: 1996
Main classification: H01L21
IPC codes: H01L29, G01L1, H01L21, G01L9, G01P15, B81C1, B81B3, B81B7