One-component, thermosetting resin composition for coating use

Abstract: A one-component, thermosetting resin composition curable through a Michael reaction between (a) a component having a plurality ofα , β -unsaturated carbonyl groups and (b) a component having a plurality of activated methylene or activated methyne groups is disclosed. The curing reaction is catalyzed with a quaternary ammonium, quaternary phosphonium or tertiary sulfonium salt in the presence of a five-membered cyclic carbonate compound independently added to the composition or covalently attached to either component (a) or component (b).

Description: FIELD OF THE INVENTION This invention relates to a one-component, thermosetting resin composition for coating use. More particularly, it relates to a resinous composition which cures through a Michael reaction. BACKGROUND OF THE INVENTION Michael reactions in which activated methylene is added to a polarized carbon-to-carbon double bond such as α , β -unsaturated carbonyl are utilized in the crosslinking of resinous compositions for coating use. These compositions are advantageous in that the Michael reaction gives a chemically stable crosslinking bond without forming any reaction by-product. Typical examples of prior art include the following patent literatures: U.S. Patent No. 4,408,018; U.S. Patent No. 5,017,649; U.S. Patent No. 5,084,536; EP-A-0448154 JP-A-01/121341 (EP-A-0310011); JP-A-01/204919 (EP-A-0326723); Michael reactions in general require a base catalyst for forming carboanions from active hydrogen sites such as activated methylene or methyne group. Most of the prior art compositions utilizing the Michael reaction for crosslinking employ a strong base such as alkali metal hydroxides, alkali metal alkoxides, quaternary ammonium hydroxides or carbonates, tertiary amines, guanidines, amidines and tertiary phosphines. Since such strong base catalysts may catalyze the Michael reaction even at ambient temperature, systems containing the strong base generally have to be formulated into a two component composition. The strong base catalyst may also hydrolyze or otherwise deteriorate resin components when remained in the films applied on substrates. For example, amines may cause yellowing of the cured films. Alkali metal based catalysts are hardly soluble in organic solvents conventionally used in coating compositions and, therefore, may result, when used, in cured films of unsatisfactory appearance. The present invention has its basis on the discovery that quaternary ammonium or like onium salts having no or little catalytic activity may exhibit an adequate activity on a Michael type crosslinking reaction in the presence of a five-membered cyclic carbonate component. The present invention may, therefore, achieve a number of advantages over the prior art compositions. The composition of the present invention may be formulated in an one-component or one-pot composition having a relatively long pot life while retaining an adequate curability upon heating. SUMMARY OF THE INVENTION The present invention provides a one-component, thermosetting resin composition for coating use comprising: (a) a component containing a plurality of α,β-ethylenically unsaturated carbonyl groups in the molecule; (b) a component containing a plurality of activated methylene groups or activated methyne groups in the molecule; (c) a quaternary ammonium salt, a quaternary phosphonium salt or a tertiary sulfonium salt, wherein the counter anion is a halide, a monobasic carboxylate, a polybasic carboxylate, nitrate, nitrite, a sulfonate, sulfate, sulfite, phosphate or an acid phosphate ester anion, the salt not having catalytic activity at ambient temperature when used alone; (d) a five-membered cyclic carbonate compound independently added to the composition or covalently attached to at least one of said component (a) and said component (b); wherein the proportions of component (a) and component (b) lie between 2:1 and 1:2, relative to the double bond and the active hydrogen to be added thereto, the proportion of component (c) ranges between 0.1 and 10.0 equivalent % based on the sum of component (a) and component (b), and the proportion of component (d) ranges between 0.5 and 100 equivalent % based on the sum of component (a) and component (b). The resin composition of the present invention may exhibit an adequate curability at elevated temperatures and has a relatively long pot life even when formulated into a one-component composition. Unlike amine catalysts, the onium salt will not cause yellowing or other deterioration in the resulting cured films. Furthermore, the solubility of the onium salt in the solvents commonly used in coating compositions may be increased by suitably selecting hydrocarbon residues attached to the onium atom so as to ensure uniform dissolution in the composition. DESCRIPTION OF THE PREFERRED EMBODIMENTS Component (a) Component (a) is a compound or polymer having a plurality of ethylenic unsaturations between carbon atoms at the α and β positions relative to the carbonyl group. Preferably, component (a) is a polyol poly(meth)acrylate resin, an unsaturated polyester resin, a polyester acrylate resin, an epoxy acrylate resin, a urethane acrylate resin, a polyether acrylate resin, an α,β-unsaturated carbonyl group-containing acrylic resin, or a silicone oligomer having (meth)acryloyl groups. Typical examples of such compounds are acrylic or methacrylic (hereinafter collectively referred to as "(meth)acrylic") esters of polyhydric alcohols such as ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, propylene glycol di(meth)acrylate, neopentyl glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate,glycerol tri(meth)acrylate, and pentaerythritol tetra(meth)acrylate. Acrylates or methacrylates of polyester polyols known as polyester acrylate resins fall within this class. Unsaturated polyesters containing an unsaturated dicarboxylic acid such as maleic or fumaric acid may also be used as component (a). Unsaturated polyesters are used in large quantities for molding various FRP products and may be synthesized, as is well-known, by the polycondensation reaction between an α,β-unsaturated dicarboxylic acid component such as maleic anhydride or fumaric acid optionally containing other polycarboxylic acids such as phthalic anhydride, isophthalic, terephthalic, adipic, sebacic or trimellitic acid and a polyol component such as ethylene glycol, diethylene glycol, propylene glycol, tetramethylene glycol, 1,6-hexanediol, neopentyl glycol, trimethylolpropane, glycerine or pentaerythritol. Other examples of component (a) include epoxy acrylate resins produced by reacting (meth)acrylic acid with an epoxy resin such as bisphenol or novolac type epoxy resins, and urethane acrylate resins produced by reacting a hydroxyl group-containing acrylic resin first with an organic polyisocyanate such as isophoronediisocyanate, tolylenediisocyanate, diphenylmethanediisocyanate, hexamethylenediisocyanate or a urethane prepolymer thereof and then with 2-hydroxyethyl (meth)acrylate. Acrylic resins containing a plurality of α, β-unsaturated carbonyl functions may be produced via the ring-opening reaction of an epoxy ring with (meth)acrylic acid or the acylation of a hydroxyl group with (meth)acrylic acid. For example, epoxy group-containing acrylic resins may be produced by copolymerizing an epoxy group-containing acrylic monomer such as glycidyl (meth)acrylate with an acrylic monomer free of the epoxy group and/or a nonacrylic ethylenically unsaturated monomer. Examples of copolymerizable acrylic monomers include alkyl (meth)acrylates such as methyl, ethyl, propyl, n-butyl, isobutyl, t-butyl, 2-ethylhexyl or lauryl (meth)acrylate; hydroxyalkyl (meth)acrylates such as 2-hydroxyethyl (meth)acrylate; aryl or aralkyl (meth)acrylates such as phenyl or benzyl (meth)acrylate; PLACCEL® FA1 or FM1 (adduct of 2-hydroxyethyl (meth)acrylate with polycaprolactone sold by Daicel Chemical Industries, Ltd.); and other acrylic monomers such as acrylamide, methylene-bis-acrylamide or acrylonitrile. Examples of copolymerizable non-acrylic monomers include styrene, α-methylstyrene, itaconic acid, maleic acid, and vinyl acetate. The epoxide function of the acrylic copolymer may then be opened with (meth)acrylic acid to introduce the α,β-unsaturated carbonyl function. Conversely, an epoxy group-containing acrylic monomer such as glycidyl (meth)acrylate may be reacted with an acrylic polymer containing a plurality of free carboxylic functions which may be produced by copolymerizing a carboxyl group-containing monomer such as acrylic, methacrylic or itaconic acid with a copolymerizable acrylic monomer and optionally with a non-acrylic monomer as discussed supra. Acryl polyols containing a plurality of hydroxyl groups may be modified to have a plurality of α,β-unsaturated carbonyl functions by the acylation reaction with acrylic or methacrylic acid or a reactive derivative thereof such as chloride, or the transesterification reaction with a lower alkyl (meth)acrylate such as methyl (meth)acrylate. Acryl polyols may be produced by copolymerizing a hydroxyl group-containing acrylic monomer such as 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth) crylate, 4-hydroxybutyl (meth)acrylate or PLACCEL® FM-1 with a copolymerizable acrylic and/or non-acrylic monomer as discussed supra. Further examples of component (a) include polyether acrylate resins such as polyethylene glycol di(meth)acrylate, and silicone oligomers such as 3-methacryloyloxypropyl-terminated polydiorganosiloxanes. When component (a) is a resin, its molecular weight ranges between 400 and 100,000, preferably between 600 and 10,000, and the alkenyl equivalent weight ranges between 100 and 10,000, preferably between 100 and 1,000. The term "equivalent weight" as used herein refers to the molecular weight divided by the number of a function concerned. Component (b) Compounds or resins usable as component (b) have a plurality of activated methylene or methyne groups in the molecule. Typical examples of activated methylene compounds are acetoacetic acid, cyanoacetic acid, malonic acid and derivatives of these acids. Component (b) having a plurality of activated methylene groups may be prepared from these activated methylene carboxylic acids or derivatives thereof. Preferably component (b) is an ester of an activated methylene- or methynecarboxylic acid with a nonpolymeric or polymeric polyol, a reaction product of a polyamine with diketene, a polymer of an activated methylene group-containing acrylic monomer, or an adduct of an isocyanate compound with an activated methylene compound. For example, polyols may be reacted with a reactive derivative of acetoacetic, cyanoacetic or malonic acid to obtain component (b). Polyols may be a polyhydric alcohol used in the production of unsaturated polyesters as the polyol component thereof, or a polymeric polyol such as acryl polyols, polyester polyols, polyether polyols, epoxy polyols, polyurethane polyols or silicone polyols. Reactive derivatives of acetoacetic, cyanoacetic or malonic acid may be their lower alkyl esters or halides. Polyester resins having a plurality of activated methylene groups may be produced by polycondensating a polycarboxylic acid component containing dialkyl malonates and a polyol component discussed supra. Component (b) having a plurality of acetoacetamide groups may be produced by reacting diketene with a polyamine such as ethylenediamine, 1,3-diaminopropane, 1,4-diaminobutane, 1,6-hexanediamine, 1,12-diaminododecane, 1,2-diaminocyclohexane, phenylenediamine, piperazine, 2,6-diaminotoluene, diethyltoluenediamine, N,N'-bis (2-aminopropyl)-ethylenediamin, or N,N'-bis(3-aminopropyl)-1,3-propanediamine. Acrylic resins having a plurality of activated methylene groups may be produced by copolymerizing an acrylic monomer having an activated methylene group such as 2-acetoacetoxyethyl (meth)acrylate, 2-cyanoacetoxyethyl (meth)acrylate, N-(2-cyanoacetoxyethyl)acrylamide, N-(2-propionylacetoxybutyl)acrylamide, N-(4-acetoacetoxymethyl) benzylacrylamide, N-(2-acetoacetylaminoethyl)acrylamide or N-(2-acetoacetylaminoethyl)methacrylamide with an acrylic and/or nonacrylic monomer as discussed supra with regard to component(a). Component (b) having a plurality of activated methyne groups may be produced, as disclosed in EP-A-0310011, by the transesterification between a trialkyl methanetricarboxylate and a nonpolymeric or polymeric polyol, or by the addition reaction between an activated methylene compound and an isocyanate compound. As will be apparent, either one of the activated methylene and isocyanate reactants should be polyfunctional. For example, a polyisocyanate reactant produced by reacting a diisocyanate with a polyol at an NCO/OH ratio of greater than 1 may be reacted with a monofunctional activated methylene reactant such as dialkyl malonate. Alternatively, those compounds or resins having a plurality of activated methylene groups as discussed supra may be reacted with a monofunctional isocyanate. Component (b) may have both activated methylene and activated methyne groups in a mixture or in a single resin entity. For example, a copolymer of a monomer mixture containing an activated methylene-containing acrylic monomer and an activated methyne-containing acrylic monomer may be copolymerized optionally with other comonomers. When component (b) is a resin, its molecular weight ranges between 400 and 100,000, preferably between 600 and 10,000, and the active hydrogen equivalent weight ranges between 40 and 10,000, preferably between 80 and 5,000. Component (c) A variety of ammonium salts may be used. However, tetraalkyl and trialkylaralkyl type ammonium salts are preferred for economical reasons. Nitrogen-containing heterocyclic ammonium salts such as those derived from pyridine, piperidine, piperazine or morpholine may also be used. Specific examples of ammonium cations include tetraalkylammonium, such as tetrabutylammonium, tetramethylammonium, tetraethylammonium, tetrapropylammonium, tetrahexylammonium, tetraoctylammonium, tetradecylammonium, tetrahexadecylammonium, triethylhexylammonium, 2-hydroxyethyltrimethylammonium (choline), methyltrioctylammonium, cetyltrimethylammonium, 2-chloroethyltrimethylammonium, trialkylaralkylammonium, such as trimethylbenzylammonium, and alkylpyridinium, such as methylpyridinium. Onium cations of component (c) may also be tetraalkylphosphonium or trialkylsulfonium cations. Counter anions should be capable of forming a non-basic stable salt with the ammonium cations and include halides, monobasic carboxylates, polybasic carboxylates sulfonates, nitrate, nitrite, sulfate, sulfite, phosphate and acid phosphate esters. Specific examples thereof include acetate, laurate, glycolate, benzoate, salicylate, maleate, phthalate, chloride, bromide, iodide, methanesulfonate, p-toluenesulfonate, dodecylbenzene sulfonate, triflate, nitrate, sulfate, methosulfate, phosphate and acid t-dibutylphosphate. Quaternary phosphonium salts such as tetrabutylphosphonium bromide and tertiary sulfonium salts such as trimethylsulfonium iodide may also be used. Onium salts having above counter anions do not exhibit catalytic activity at ambient temperature when used alone but have catalytic activity only in the presence of component (d) under the conventional baking conditions. Accordingly, they are useful when a thermosetting, storage stable, one-component composition is desired. Component (d) The term "five-membered cyclic carbonate compounds" as used herein refers to 2-oxodioxolane otherwise known as ethylenecarbonate and its derivatives. They are produced by reacting phosgene with 1,2-alkylenediol such as ethylene glycol, 1,2-propylene glycol or 1,2-butylene glycol to form a cyclic carbonate structure. When glycerine is reacted with phosgene, glycerine carbonate, namely 2-oxo-4-hydroxymethyldioxolane is produced. Cyclic 1,2-alkylene carbonates or glycerine carbonate are examples of component (d) to be independently added to the composition of the present invention. Polymerizable five-membered cyclic carbonate monomers may be produced from glycerine carbonate using the remaining hydroxyl group. For example, a polymerizable unsaturated group may be introduced to glycerine carbonate by etherifying with a polymerizable alcohol such as allyl alcohol or 1-propenyl alcohol, esterifying with a reactive derivative of (meth)acrylic acid such as halide, or reacting with methacryloylisocyanate. Homo- or copolymers of these monomers may also be added independently to the composition of this invention as component (d). Alternatively, these monomers may be bound to component (a) or component (b) through a covalent bond. For example, when component (a) or component (b) is an acrylic polymer, the cyclic carbonate monomer may be added to the mixture of comonomers and copolymerized therewith. Component (b) having bound thereto a five-membered cyclic carbonate may be produced by copolymerizing the cyclic carbonate monomer with an acrylic monomer having an activated methylene group and other acrylic and/or non-acrylic monomers. Glycerine carbonate and its acrylate or methacrylate ester are preferable as component (d) when adding independently and when binding to component (a) or (b), respectively. At least one of component (a) and component (b) is preferably an acrylic resin or polymer, and component (d) is preferably glycerine carbonate (meth)acrylate copolymerized with said acrylic resin or polymer. Curable resin compositions The proportions of component (a) and component (b) in the curable resin composition of the present invention lie between 2:1 and 1:2, preferably between 1.5:1 and 1:1.5 relative to the double bond and the active hydrogen atom to be added thereto. The proportion of component (c) ranges between 0.1 and 10.0 equivalent %, preferably between 0.2 and 5.0 equivalent % based on the sum of component (a) and component (b). The proportion of component (d) ranges between 0.5 and 100 equivalent %, preferably between 5.0 and 40 equivalent % based on the sum of component (a) and component (b). When used as a coating composition, it may contain a variety of conventional additives such as solvents, extender pigments, coloring pigments, sag-preventing agents, and UV absorbers. After applying onto a substrate as a film, the composition may be cured by baking the film at a temperature between 100 °C and 250 °C, preferably between 140 °C and 220 °C. The curable resin composition may find use as a clear top coat composition to be applied on a color base coat. Further, the invention relates to a method of forming a multi-layer coating film on a substrate comprising the steps of applying onto the substrate a colored base coat composition, applying a clear top coat composition thereon wet-on-wet, and baking both coats simultaneously, wherein the clear top coat composition is a one-component, thermosetting resin composition according to the invention. The base coat composition may be solvent type or water-borne compositions containing metallic or solid color pigments. The base and top coats may conveniently be applied using so-called two coats-one bake method by applying the top coat on the base coat wet-on-wet and then baking both coats simultaneously. When the base coat is a water-borne system, it is preferable to subject the base coat to a preheating step at a temperature of 60-100 °C for 2-10 minutes before applying the top coat thereon. Base coat compositions useful in the above applications are disclosed, for example, in U.S. Patents Nos. 5,151,125 and 5,183,504. Particularly, a water-borne composition disclosed in Example 1 of U.S. Patent No. 5,183,504 may be used to advantage in combination with the composition of the present invention used as a top coat in order to give a multi-layer coating having satisfactory finish, appearance and other properties. It is very important for the top coat to be used for the above application particularly for finishing automobile bodies to have a satisfactory scratch resistance and acid rain resistance. The composition of the present invention is advantageous in these properties over conventional systems containing a melamine resin as a crosslinker. The following examples are intended to illustrate the present invention. All parts and per cents therein are by weight unless otherwise specified. Production Example 1 To a 4-necked flask charged with 360 parts of xylene was added dropwise a monomer mixture containing a polymerization initiator shown in Table 1 at 110°C over 3 hours. After the addition, the mixture was allowed to react at 110°C for 30 minutes. Then 2 parts of KAYAESTER® O (t-butylperoxyoctate sold by Nippon Kayaku Co., Ltd.) in 40 parts of xylene were added dropwise at 110 °C over 30 minutes and the mixture allowed to react at the same temperature for additional 90 minutes. An acrylic resin solution having 49.4 % nonvolatiles, a number average molecular weight Mn measured by the GPC method of 4,300, an activated methylene equivalent weight of 200, and a carbonate equivalent weight of 1002 was obtained. Production Examples 2-5 Production Example 1 was followed using a mixture shown in Table 1, respectively. Nonvolatile contents, Mn's and other data are also shown in Table 1. Production Example 6 To 394 parts of the acrylic resin solution of Production Example 5 (200 parts as solids) were added 0.1 parts of hydroquinone, 1.0 part of tetrabutylammonium bromide and 30 parts of methacrylic acid. The mixture was allowed to react at 120 °C until an acid number of less than 1 was reached. A resin solution having a nonvolatile content of 53.0 %, and an alkene equivalent weight of 630 was obtained. Production Example 7 A reactor was charged with 236 parts of 1,6-hexanediol, 78 parts of dimethyl phthalate, 230 parts of dimethyl maleate and 1 part of dibutyltin oxide. The mixture was heated gradually to 200°C while distilling off methanol formed by a transesterification reaction. Then the reaction was continued at 200 °C until no distillation of methanol was found. After cooling 250 parts of xylene were added. A resin solution having a nonvolatile content of 61.4 %, Mn of 1,700, and an alkene equivalent weight as solids of 480 was obtained. Production Example 8 A reactor was charged with 236 parts 1,6-hexanediol, 264 parts of dimethyl malonate and 1 part of dibutyltin oxide. The mixture was heated gradually to 200°C while distilling off methanol formed by a transesterification reaction. Then the reaction was continued at 200 °C until no distillation of methanol was found. After cooling 250 parts of xylene were added. A resin solution having a nonvolatile content of 58.8 %, Mn of 1,800 and an active hydrogen equivalent weight as solids of 184.2 was obtained. Example 1 405 parts of the resin solution of Production Example 1 (200 parts as solids), 80 parts of pentaerythritol triacrylate (PETA) and 2 parts of tetrabutylammonium bromide (TBABr) were thoroughly mixed to make a solution. The solution was applied on a tinplate using a #40 bar coater and heated in an oven at 160 °C for 20 minutes. The gel fraction of the resulting cured film was determined based on the difference of weight before and after soaking the film in a 1:1 mixture of acetone and methanol at room temperature for 48 hours. The result is shown in Table 2. Example 2 Example 1 was followed using 405 parts (200 parts as solids) of the resin solution of Production Example 2, 80 parts of PETA, 20 parts of glycerine carbonate and 2 parts of TBABr. The gel fraction of the cured film is shown in Table 2. Comparative Example 1 Examples 1 was followed except that 405 parts of the resin solution of Production Example 2 (200 parts as solids) were replaced for the resin solution of Production Example 1. The results are shown in Table 2. Example 3 Example 1 was followed using 395 parts (200 parts as solids) of Production Example 3, 60 parts of PETA and 4 parts of trimethylbenzylammonium chloride (BTMAC1). The gel fraction of the cured film is shown in Table 2. Comparative Example 2 Example 3 was followed except that 393 parts (200 parts as solids) of the resin solution of Production Example 4 were replaced for the resin solution of Production Example 3. The gel fraction of the cured film is shown in Table 2. Example 4 A blend of 395 parts of the resin solution of Production Example 3 (200 parts as solids), 150 parts of EPOXY ESTER® 3002A(reaction product of propylene oxide-bisphenol A adduct diglycidyl ester with acrylic acid sold by Kyoeisha Yushi Kagaku Kogyo) and 3 parts of tetrabutylammonium iodide (TBAI) was applied on a tinplate, baked at 160°C for 20 minutes, and tested for the gel fraction. The result is shown in Table 3. Comparative Example 3 Example 4 was followed except that 393 parts (200 parts as solids) of Production Example 4 were replaced for the resin solution of Production Example 3. The gel fraction of the cured film is shown in Table 3. Example 5 A blend of 405 parts (200 parts as solids) of the resin solution of Production Example 2, 100 parts of UA-306H (adduct of hexamethylenediisocyanate and pentaerythritol triacrylate at 1:2 moles sold by Kyoeisha Yushi Kagaku Kogyo K.K.), 20 parts of glycerine carbonate and 3 parts of cetylpyridinium chloride (CPC1) was applied on a tinplate, baked at 160 °C for 20 minutes, and tested for the gel fraction. The result is shown in Table 3. Comparative Example 4 Example 5 was followed using a blend of 405 parts (200 parts as solids) of the resin solution of Production Example 2, 100 parts of UA-306H and 3 parts of CPC1. The gel fraction is shown in Table 3. Example 6 A blend of 395 parts (200 parts as solids) of the resin solution of Production Example 3, 150 parts of NK ESTER A-400 (polyethylene glycol (n=9) diacrylate sold by Shin-Nakamura Kagaku Kogyo K.K.) and 2 parts of TBABr was applied on a tinplate, baked at 220°C for 1 minute, and tested for the gel fraction. The result is shown in Table 3. Comparative Example 5 Example 6 was followed except that 393 parts (200 parts as solids) of the resin solution of Production Example 4 were replaced for the resin solution of Production Example 3. The gel fraction is shown in Table 3. Example 7 A blend of 377 parts (200 parts as solids) of the resin solution of Production Example 6, 30 parts of ditrimethylolpropane tetraacetoacetate (DTMPTA), 20 parts of glycerine carbonate and 3 parts of TBABr was applied on a tinplate, baked at 160 °C for 20 minutes, and tested for the gel fraction. The result is shown in Table 4. Comparative Example 6 Example 7 was followed except that glycerine carbonate was not added. The gel fraction is shown in Table 4. Example 8 A blend of 326 parts (200 parts as solids) of the resin solution of Production Example 7, 70 parts of DTMPTA, 30 parts of glycerine carbonate and 4 parts of TBAI was applied on a tinplate, baked at 160°C for 20 minutes, and tested for the gel fraction. The result is shown in Table 4. Comparative Example 7 Example 8 was followed except that glycerine carbonate was not added. The gel fraction is shown in Table 4. Example 9 A blend of 377 parts (200 parts as solids) of the resin solution of Production Example 6, 127 parts of MACRYNAL® LH437 (polyfunctional methanetricarboxylic acid ester sold by Hoechst), 20 parts of glycerine carbonate and 3 parts of CPC1 was applied on a tinplate, baked at 160°C for 20 minutes, and tested for the gel fraction. The result is shown in Table 5. Comparative Example 8 Example 9 was followed except that glycerine carbonate was not added. The gel fraction is shown in Table 5. Example 10 A blend of 377 parts (200 parts as solids) of the resin solution of Production Example 6, 20 parts of 1,3-cyclohexane-bis(methylacetoacetamide) (HBA), 20 parts of glycerine carbonate and 3 parts of CPC1 was applied on a tinplate, baked at 160 °C for 20 minutes, and tested for the gel fraction. The result is shown in Table 5. Comparative Example 9 Example 10 was followed except that glycerine carbonate was not added. The gel fraction is shown in Table 5. Example 11 A blend of 405 parts (200 parts as solids) of the resin solution of Production Example 1, 80 parts of PETA, 40 parts of X-22-164B (methacrylate-modified polysiloxane at both terminals sold by Shin-Etsu Chemical Co., Ltd.) and 5 parts of tetrabutylammonium nitrate (TBANO) was applied on a tinplate, baked at 180°C for 20 minutes, and tested for the gel fraction. The result is shown in Table 6. Comparative Example 10 Example 11 was followed except that 405 parts (200 parts as solids) of the resin solution of Production Example 2 were replaced for the resin solution of Production Example 1. The gel fraction is shown in Table 6. Example 12 A blend of 340 parts (200 parts as solids) of the resin solution of Production Example 8, 200 parts of KAYARAD® DPCA-120 (dipentaerythritol (1 mole)/caprolactone (12 moles) adduct hexaacrylate sold Nippon Kayaku Co., Ltd.), 40 parts of glycerine carbonate and 4 parts of tetrabutylammonium phthalate (TBAPA) was applied on a tinplate, baked at 140 °C for 20 minutes, and tested for the gel fraction. The result is shown in Table 6. Production Example 9 Production Example 1 was followed using the following monomer mixture. Material Parts 2-Acetoacetoxyethyl methacrylate 191 n-Butyl methacrylate 88 Methyl methacrylate 171 n-Butyl acrylate 50 KAYAESTER® O 15 An acryl resin solution having a nonvolatile content of 60.4 %, Mn(GPC) of 6,000, and active hydrogen equivalent weight of 281 was produced. Example 13 A blend of 947 parts of the resin solution of Production Example 9, 100 parts of PETA, 16 parts of glycerine carbonate and 16 parts of TBABr was produced. To this were dispersed 28 parts of MITSUBISHI CARBON MA-100 (carbon black sold by Mitsubishi Chemical Corp.) in a paint shaker until a particle size of less than 30 µm was reached. This composition was applied on a tinplate, baked at 220 °C for 2 minutes, and tested for the gel fraction as in Example 1. The gel fraction was greater than 95 %. The composition was stable upon storage at 40°C for 10 days. Example 14 Use in two coat-one baking coating Step A A zinc phosphate-treated steel plate having a thickness of 0.8 mm was coated with a cationic electrodeposition paint (POWER TOP PU-50 sold by Nippon Paint Co., Ltd.) electrically to a dry film thickness of 25 microns and then with a mid-layer paint (ORGA P-2 SEALER sold by Nippon Paint Co., Ltd.) using an air spray gun to a dry film thickness of 40 microns. The coated plate was then baked at 140 °C for 30 minutes. Step B 1. Base Coat Formulation ALPASTE 7160 N 10 parts Acrylic varnish 50 parts CYMEL 202 10 parts CYMEL 327 10 parts Isopropyl alcohol 7 parts 2. Top Coat Formulation Acrylic resin varnish of Pro.Ex.2 405 parts PETA 80 parts TBABr 2 parts Glycerine carbonate 20 parts TINUVIN 900 6 parts SANOL LS-292 3 parts Onto the steel plate substrate prepared in Step A was applied the above base coat composition to a dry film thickness of 16 microns by air spraying and allowed to set for 7 minutes. Then, the above top coat composition adjusted to Ford cup #4 viscosity of 30 seconds at 20 °C was applied electrostatically on the base coat wet-on-wet to a dry film thickness of 40 microns, allowed to set for 7 minutes, and baked together with the base coat at 160°C for 25 minutes. The resulting multi-layer film was evaluated for various items. The results are shown in Table 7. Comparative Example 11 Example 14 was followed except that the top coat composition used was a conventional acrylic-melamine based composition of the following formulation. The results are shown in Table 7. Top Coat Formulation for Comparison DIANAL HR-554 58.3 parts ACR-461 63.6 parts YUBAN 20N-60 50.0 parts TINUVIN 900 2.0 parts SANOL LS-292 1.0 parts n-Butanol 1.3 parts SOLVESSO 100 5.0 parts Item Ex. 12 Comp.Ex. 11 SVS, % 1) 56.2 49.0 Pencil hardness 2) HB F Scratch resistance 3) Good Fair Acid resistance 4) Good Not Good Evaluation method 1) Volumetric nonvolatile content (SVS): The composition was adjusted to a Ford cup #4 viscosity at 30 sec. at 20 °C. A 0.5g aliquot was taken precisely, diluted with 3 ml of toluene, baked at 110°C for 1 hour to determine the nonvolatile content by weight followed by the conversion into the volumetric nonvolatile content. 2) Pencil hardness: The method of JIS K5400 8-4-2 was followed. 3) Scratch resistance: One gram of a 50 % aqueous dispersion of a commercial cleanser (NEW HOME CLEANSER sold by Kao Corporation) was applied on a flannel fabric of 2 cm x 2 cm size. This fabric was attached to the reciprocating head of a Gakushin type dyeing fastness tester (Daiei Kagaku Seiki K.K.). The test specimen was rubbed with the head under a load of 500g at 20 reciprocations and per cents retention of 20 ° gloss was determined. The scratch resistance was evaluated according to the following schedule. Very good greater than 85 % Good 70-85 % Fair 40-70 % Not good less than 40 % 4) Acid resistance: One drop (0.5 ml) of 0.1 N H 2 SO 4 was pipetted on the specimen and allowed to stand at 75 °C for 30 minutes. Then the change in appearance was observed visually. Judgment was made by the following schedule. Very good No trace was observed. Good Slight trace was observed. Fair Remarkable trace was observed. Not good Film was partly eroded.

Claims: A one-component, thermosetting resin composition for coating use comprising: (a) a component containing a plurality of α,β-ethylenically unsaturated carbonyl groups in the molecule; (b) a component containing a plurality of activated methylene groups or activated methyne groups in the molecule; (c) a quaternary ammonium salt, a quaternary phosphonium salt or a tertiary sulfonium salt, wherein the counter anion is a halide, a monobasic carboxylate, a polybasic carboxylate, nitrate, nitrite, a sulfonate, sulfate, sulfite, phosphate or an acid phosphate ester anion, the salt not having catalytic activity at ambient temperature when used alone; (d) a five-membered cyclic carbonate compound independently added to the composition or covalently attached to at least one of said component (a) and said component (b); wherein the proportions of component (a) and component (b) lie between 2:1 and 1:2, relative to the double bond and the active hydrogen to be added thereto, the proportion of component (c) ranges between 0.1 and 10.0 equivalent % based on the sum of component (a) and component (b), and the proportion of component (d) ranges between 0.5 and 100 equivalent % based on the sum of component (a) and component (b). The composition according to claim 1, wherein said component (a) is a polyol poly(meth)acrylate, an unsaturated polyester resin, a polyester acrylate resin, an epoxy acrylate resin, a urethane acrylate resin, a polyether acrylate resin, an α,β-unsaturated carbonyl group-containing acrylic resin, or a silicone oligomer having (meth)acryloyl groups. The composition according to claims 1 or 2, wherein said component (b) is an ester of an activated methylene- or methynecarboxylic acid with a nonpolymeric or polymeric polyol, a reaction product of a polyamine with diketene, a polymer of an activated methylene group-containing acrylic monomer, or an adduct of an isocyanate compound with an activated methylene compound. The composition according to any of the preceding claims, wherein the onium cation of said component (c) is a tetraalkylammonium, trialkylaralkylammonium, alkylpyridinium, tetraalkylphosphonium or trialkylsulfonium cation. The composition according to any of the preceding claims, wherein said component (d) is a cyclic 1,2-alkylenecarbonate or glycerine carbonate independently added to the composition. The composition according to any of the preceding claims, wherein at least one of said component (a) and said component (b) is an acrylic resin or polymer, and wherein said component (d) is glycerine carbonate (meth)acrylate copolymerized with said acrylic resin or polymer. A method of forming a multi-layer coating film on a substrate comprising the steps of applying onto the substrate a colored base coat composition, applying a clear top coat composition thereon wet-on-wet, and baking both coats simultaneously, wherein said clear top coat composition is the composition of any one of claims 1 to 6.

Inventors: AOKI KEI, IRIE TAKASHI, MORIMOTO HIDEO, SAWADA HARUHIKO, AOKI, KEI, IRIE, TAKASHI, MORIMOTO, HIDEO, SAWADA, HARUHIKO
Applicants: NIPPON PAINT CO LTD, NIPPON PAINT CO., LTD.
Application year: 1996
Main classification: C09D4
IPC codes: B05D7, C09D4, B05D1, C09D175, C08F290, C09D7, C09D133