Novel pearl pigment and production method for same

Abstract: Disclosed are a novel pearl pigment which is excellent in discoloration resistance and in affinity (dispersibility) with resins, a production method for the same, and a resin composition, paint and ink into which the above pearl pigment is incorporated. The pearl pigment comprises a flake substrate, titanium oxide coated on the surface thereof, and a phosphoric acid metal compounds, or a phosphoric acid metal compounds and a metal oxides coated on the surface of particles coated with titanium oxide.

Description: FIELD OF THE INVENTION The present invention relates to a novel pearl pigment using a flake substrate as a base material, more specifically to a novel pearl pigment which is excellent in resistance to discoloration caused by light and heat, as well as in affinity (dispersibility) with resins, a production method for the same, and a resin composition, paint and ink into which the above pearl pigment is incorporated. BACKGROUND OF THE INVENTION There have so far been known and widely employed pearl pigments in which a flake substrate is coated with metal oxides having high refraction indices, for example, titanium dioxide and zirconium oxide to cause a pearlescent color to be revealed by an interference color generated by interference in a reflection of light, and pearl pigments in which colored metal oxides, for example, iron oxide and chromium oxide, or colored pigments and dyes are impregnated into this coating layer to cause colored pearlescence to be developed. Among them, with respect to white-color (including an interference color) pearl pigments, well known is a pearl pigment which is composed of a coating layer using titanium oxide as a base material. This titanium oxide is well known as an optically active material (refer to, for example, Susumu Okazaki, "Coloring Material", 60 [6], 333 to 341 (1987)), and it is reported that when this is mixed into paint and ink and kneaded into plastics, a resin component contacting this titanium oxide deteriorates (chalking; whiting) as time passes with light or heat energy as an initiator (refer to, for example, Susumu Okazaki, "Coloring Material", 60 [6], 333 to 341 (1987) and Hiroshi Tsubomura, "Optical Electrochemical and Energy Conversion", Tokyo Kagaku Dohjin (1980), P. 198). Further, it is said that when this titanium oxide is kneaded into a plastic comprising polyolefin, titanium oxide reacts with a phenol derivatives (for example, BHT and the like) or aniline-derivatives light stabilizer to form a coordination complex or a coordination compound, which causes discoloration (refer to, for example, D. A. Holzen, "TI-PURE" Technical Report, Du Pont Japan, No. 84-003 (1)). These kind of problems are similarly caused by using a pearl pigment in which titanium oxide is coated on the surface thereof. The present inventors have previously proposed a pearl pigment in which the defects described above are improved and which has a good dispersibility without causing discoloration and having coagulation of the particles (refer to JP-A-6-16964). This pearl pigment is prepared by using, as a raw material, a white pearl pigment prepared by coating titanium oxide in advance on mica particles and coating respective metal oxides (or hydrates) of silicon, aluminum and zinc in order on these white titanium oxide-coated mica particles (that is, on an outer layer) by a wet method, wherein it has been intended to reduce the exposure of titanium oxide to light and heat energies coming from the outside with the above outer layer and enhance the dispersibility of the pigment itself. However, this production method is required the repetition of the respective processing operations of a hydrolytic reaction twice and a dry processing (drying and calcination) and is a disadvantageous production method in terms of a production process. On the other hand, when a conventional pearl pigment in which metal oxides using titanium oxide as a base material are coated on a flake substrate is incorporated into a resin system, the pigment often moves to the surface of a resin composition, and this contaminates the surfaces of kneading rolls and calendar rolls in a molding machine to generate a phenomenon called plate out, which leads to causing differences in the quality by product and lot. In order to solve this problem of the plate out, proposed are a method in which blended components for a resin composition are improved (refer to, for example, JP-A-63-317557), and in addition to this, in case of a pearl pigment, a pigment in which the surface is treated with a specific polymer, such as, for example, a pearl pigment coated directly with a polyester-polyurethane block copolymer having a tertiary amino group (refer to JP-A-63-46266). However, the use of these pearl pigments has been problematic in that the kind of resins to be used is restricted. Further, there has been the problem that when a metal oxide(titanium oxide)-coated flake substrate pigment itself is used as a raw material for ink as it is, raising the pigment content in order to emphasize pearlescence particularly in offset printing causes unevenness in printing as the number of printed sheets increases. This is because the affinity (dispersibility) of the pigment for an ink medium is low, and a phenomenon of so-called piling in which a pigment is separated from a medium and piles up on rolls, a plate and a blanket. The present invention is intended to solve the problems that conventional techniques pose. That is, an object of the present invention is to provide a pearl pigment which is improved in discoloration resistance, a reduction in plate-out in the production, and the printing characteristics of ink when the pearl pigment is used as mixed in with the paint and ink or as incorporated into plastics, a convenient production method for the same, and a resin, paint and ink compositions containing the pearl pigment obtained by the above production method. SUMMARY OF THE INVENTION Investigations repeated by the present inventors paying attention to the kinds of phosphoric acid compound, of metal oxide and combination thereof in order to achieve the objects described above have resulted in findings that show that the discoloration resistance of a pearl pigment, the affinity (dispersibility) thereof with a resin, and a printing aptitude in ink are notably improved by coating titanium oxide and a phosphoric acid metal compound, or titanium oxide, a phosphoric acid metal compound and other metal oxides in order on the surface of a flake substrate, while maintaining the intended pearlescence. That is, the present invention provides a novel pearl pigment comprising a flake substrate, titanium oxide coated on the surface thereof, and after coating titanium oxide on the surface of a flake substrate, a substance is coated thereon: wherein the amount of the phosphoric acid component constituting the phosphoric acid metal compound to be coated is in a proportion of 0.1 to 5 weight % in terms of P 2 O 5 based on titanium oxide (TiO 2 basis); the kinds of metals constituting the phosphoric acid metal compound and the metal oxide are Zn, Al and Si, and the metal compounds thereof are coated in order; and the amounts thereof are present in the proportions of 0.5 to 10 weight % in terms of ZnO 2 based on titanium oxide (TiO 2 basis), 0.5 to 10 weight % in terms of Al 2 O 3 based on titanium oxide (TiO 2 basis), and 0.5 to 5 weight % in terms of SiO 2 based on titanium oxide (TiO 2 basis), respectively. Further, the present invention provides: a method for producing a pearl pigment, as defined in claim 3. Further, the present invention provides a pearl pigment prepared by subjecting the pearl pigment thus obtained to a surface coating treatment with at least one selected from a silane coupling agent, an organosiloxane compound, and aliphatic carboxylic acid. In addition, the present invention provides paint, ink and resin compositions into which the pearl pigment of the present invention is blended. The novel pearl pigment according to the present invention is excellent in discoloration resistance, facility in kneading into resins, and printability when it is used for plastics, paint, and ink as a pearl pigment. Further, the production method according to the present invention is a very convenient and advantageous method in terms of production management and energy saving since after once preparing a suspension of a flake substrate, such intermediate process as drying and calcining in the middle of the process does not have to be carried out, and the reaction and treatment can be consistently carried out in succession in a suspension state (wet). DETAILED DESCRIPTION OF THE INVENTION The present invention will be explained below in detail. The flake substrate used in the present invention includes stratified clay minerals such as mica, kaolin, and talc, flake oxides of metals selected from titanium, aluminum, silicon, and iron, and glass flake. In particular, mica which is widely used as a flake substrate for a pearl pigment is preferably used since it is readily available. The size thereof is from 2 to 200 µ in terms of the average particle diameter and suitably selected within this range according to the applications thereof. For example, when it is used for ink, mica having an average particle diameter of as small as 10 µ or less is preferably used. Mica having a thickness of 2 µ or less, preferably 1 µ or less is suitable for revealing pearlescence. The amount of titanium oxide coated in the present invention can be optionally determined in the range of from 15 to 200 weight % (based on a flake substrate). Since the unit surface area is large when the diameter of a flake substrate is small, the coated amount is increased, and reversely, since the unit surface area is small when the diameter of a flake substrate is large, the coated amount is decreased. The optical thickness has to be fundamentally increased when an interference color is revealed, and the coated amount is increased by more than the coated amount in case of a silver color tone. Accordingly, the coated amount of titanium oxide is suitably determined according to an intended color tone. With respect to the method for coating titanium oxide hydrate on a flake substrate according to the present invention, there can be employed known methods, for example, either a method by neutralized hydrolysis in which a titanium salt aqueous solution and an alkali solution are added at the same time while maintained (at about pH 2), or a method using heat hydrolysis in which a titanium salt compound is added in advance and heat is then applied. In this case, a rutilizing agent, for example, a tin salt can be used in order to convert titanium oxide crystal to a rutile type. Titanium tetrachloride, titanium trichloride, and titanyl sulfate are preferably used because of easier availability thereof. After this hydrolytic reaction (coating titanium oxide hydrate), phosphoric acid or a phosphate compound and a desired metal salt are added to a system of the suspension to form a phosphoric acid metal compound. In this case, phosphoric acid or the phosphate compound includes phosphoric acid, condensed phosphoric acid, and the alkaline metal salts thereof. To be concrete, used are phosphoric acid, disodium phosphate, monosodium phosphate, dipotassium phosphate, monopotassium phosphate, potassium pyrophosphate, sodium pyrophosphate, potassium tripolyphosphate, and sodium tripolyphosphate. Phosphoric acid, disodium phosphate, and dipotassium phosphate are preferably used from the viewpoint of easy availability and cost. The amount of this phosphoric acid or phosphate compound is used in a proportion of 0.1 to 5 weight %, preferably 1 to 4 weight % in terms of P 2 O 5 based on the amount of titanium oxide in the finished product. The amount less than the above level provides lower effect, and even if the amount is increased more than this level, the degree of an increase in a discoloration resistance effect is small. In this case, if pH increases more than 3 after adding the phosphate compound, the reaction is preferably carried out after pH is once lowered to 3 or less with acid such as hydrochloric acid in a range in which the metal salt to be added subsequently is not hydrolyzed. In the method described above, employed is a method in which in order to improve the discoloration resistance and prevent the particles from coagulating by sintering in the production and calcination, an Al salt and an Si salt are coated in order in the amounts of from 0.5 to 10 weight % in terms of Al 2 O 3 based on titanium oxide (as TiO 2 ), and from 0.5 to 5 weight % in terms of SiO 2 based on titanium oxide (as TiO 2 ), respectively. The use of this Al salt contributes particularly to a coagulation reduction effect of the product attributable to a sintering prevention action in calcination. The amount of 0.5 weight % or less in terms of the metal oxide (Al 2 O 3 ) greatly reduces the effect thereof, and the amount of 10 weight % or more not only does not increase the effect thereof but also causes a reduction in the pearl gloss of the pigment. The more preferred amount of it to be used, though this is influenced by the unit surface area of the flake substrate, is usually from 1 to 4 weight %. The use of the Si salt improves the discoloration resistance effect, and the preferred amount thereof, though it is still influenced by the unit surface area of the flake substrate, is from 1 to 3 weight % in terms of the metal oxide (SiO 2 ). A decrease in this amount does not enhance the discoloration resistance effect, and an increase in the amount causes sintering in calcination which leads to coagulation and does not provides a pigment with satisfactory dispersibility, which leads to a reduction in the pearlescence. As described above, "the phosphoric acid metal compound" and "the phosphoric acid metal compound and the metal oxide" described in the present invention mean the final state that the hydrolysis products of phosphoric acid or a phosphate compound and various metal salts are adhered on a flake substrate, dried and calcined, whereby they are formed, and the analysis thereof is not necessarily made. However, it is considered that they reside in the state that they are composed of a phosphoric acid metal salt, the mixture of a phosphoric acid metal salt and a metal oxide, the mixture of P 2 O 5 and other metal oxides, and the composite of P 2 O 5 and other metal oxides according to the ratio of the amounts of phosphoric acid (or a phosphate compound) to a metal salt to be used. The production method according to the present invention will be explained in more detail. The first step: coating titanium oxide hydrate A suspension prepared by dispersing a flake substrate having a desired particle size in water is heated to 70°C or higher, and an aqueous solution of a titanium salt in which the concentration is adjusted is added to this suspension to adjust the pH to about 2. Further, the aqueous solution of the titanium salt is subsequently added under stirring together with an alkali solution while maintaining the pH at the above level. After adding the prescribed amount, the suspension is further stirred for about 10 minutes. The second step: adding phosphoric acid or a phosphate compound and a metal salt and coating the hydrolysis products thereof: Added are phosphoric acid or a phosphate compound in an amount corresponding to from 0.1 to 5 weight % in terms of P 2 O 5 based on the amount of titanium oxide calculated from the amount of the titanium salt added in the first step, and a Zn salt in an amount corresponding to 0.5 to 10 weight % in terms of the oxide thereof based the amount of titanium oxide calculated above, wherein stirring is carried out for about 10 minutes without specifically controlling the pH. In the case where the phosphate compound used in this step is, for example, disodium phosphate or sodium tripolyphosphate, the pH increases to some extent. When the pH increases to 3 or higher, it is once lowered to 3 or lower with mineral acids such as hydrochloric acid. Then, an alkali solution is gradually added dropwise to this suspension to raise the pH up to 5.5. An Al metal compound aqueous solution is added in an amount corresponding to from 0.5 to 10 weight % in terms of Al 2 O 3 based on the amount of titanium oxide simultaneously with the alkali solution while maintaining the pH at 5.5. Then, an aqueous solution of a silicate compound is gradually added in an amount corresponding to from 0.5 to 5 weight % in terms of SiO 2 based on the amount of titanium oxide without controlling the pH. After completing the addition, stirring is further carried out for 10 minutes. Third step: after-treatment step The suspension obtained in the second step is filtered, and soluble free salts are removed by washing with water. After drying, the pigment thus obtained is calcined at from 700 to 1200°C to thereby obtain the intended pearl pigment. The present invention further includes pigments obtained by subjecting the pearl pigments obtained through the respective third steps described above to a surface treatment with surface treating agents such as a silane coupling agent, an organosiloxane compound and aliphatic carboxylic acid. These surface treatments increase the both the affinity for resins and a discoloration resistance. In this case, alkyl trimethoxysilanes having an aliphatic chain with 8 or more carbon atoms are preferably used as the silane coupling agent. Also, methyl hydrogenpolysiloxane is preferably used as organosiloxane. Employed as the method for these surface treatments used in the present invention are a method in which the pearl pigment obtained through the third step in the production method is charged into a stirring mixer such as a Henshell mixer and a high-speed blender mixer manufactured by Worling Co., Ltd. and mixed with a surface treating agent added while stirring, or a method in which the components are charged in one lot and mixed, wherein employed is such a means that a heat treatment is provided through stirring according to necessity or a surface treating agent is mixed in advance into an organic solvent and added, followed by heating to remove the solvent. Next, the present invention will be more concretely explained with reference to examples, comparative examples and various test examples. However, the present invention will not be restricted by these examples. Example 6 (a-1) Muscovite (particle diameter: from about 10 to 60 µm) in an amount of 80 g was suspended in demineralized water of 1 liter, and the suspension was heated to 75°C while stirring. A titanium tetrachloride aqueous solution in which titanium tetrachloride of 414 g per liter was dissolved was added to this suspension, and the pH was adjusted to 2.2, followed by maintaining it, for 5 minutes. Then, the titanium tetrachloride aqueous solution described above was further added dropwise gradually while maintaining the pH at 2.2 with a 32 % sodium hydroxide aqueous solution. The titanium tetrachloride aqueous solution of 188 ml was added in total, whereby a suspension of titanium hydroxide-coated mica having a gloss of a silver color was obtained. (b-1) 85% phosphoric acid of 1.1 g and zinc chloride of 2.0 g were added to the suspension thus obtained and maintained for 10 minutes while stirring. Then, a 32% sodium hydroxide aqueous solution was slowly added dropwise to adjust the pH to 5.5, and subsequently, a 6% aluminum chloride 6 hydrate aqueous solution of 94.8 g was dropped for 30 minutes while maintaining the pH at 5.5 with a sodium hydroxide aqueous solution. Then, further added was the step in which a sodium silicate (SiO 2 : 36 %) solution of 1.67 g was diluted with water to 11.1 g, and this solution was added dropwise thereto for about 10 minutes. (c-1) Further, the coated pigment was filtered off from this suspension, and after washing with demineralized water and drying, the pigment was calcined at 900°C, whereby a pearl pigment having a gloss of a silver color was obtained. Example 7 (a-2) Muscovite (particle diameter: from about 5 to 20 µm) in an amount of 60 g was suspended in demineralized water of 1 liter, and the suspension was heated to 75°C while stirring. A titanium tetrachloride aqueous solution in which 414 g per liter of titanium tetrachloride were dissolved was added to this suspension, and the pH was adjusted to 2.2, followed by maintaining it for 5 minutes. Then, the titanium tetrachloride aqueous solution described above was further dropwise added gradually while maintaining the pH at 2.2 with a 32 % sodium hydroxide aqueous solution. The titanium tetrachloride aqueous solution of 211 ml was added in total, whereby a suspension of titanium hydroxide-coated mica having a gloss of a silver color was obtained. (b-2) 85% phosphoric acid in an amount of 1.3 g and zinc chloride of 2.3 g were added to the suspension thus obtained and maintained for 10 minutes while stirring. Then, a 32% sodium hydroxide aqueous solution was slowly added dropwise to adjust the pH to 5.5. Next, a 6 % aluminum chloride 6 hydrate aqueous solution of 124 g was added dropwise thereto for about 30 minutes while maintaining the pH at 5.5. Then, an aqueous solution prepared by diluting a sodium silicate (SiO 2 : 36 %) of 2.2 g with water to 14.7 g was added dropwise for about 10 minutes and maintained for about 10 minutes. (c-2) Further, the pigment was filtered off from this suspension, and after washing with demineralized water and drying, the pigment was calcined at 930°C, whereby a pearl pigment having a gloss of a silver color was obtained. Example 8 (a-3) Muscovite (particle diameter: from about 5 to 20 µm) in an amount of 60 g was suspended in demineralized water of 1 liter, and the suspension was heated to 75°C while stirring. An aqueous solution of 22.6 ml in which tin tetrachloride 5 hydrate in an amount of 414 g per liter was dissolved as a rutilizing agent was prepared, and this aqueous solution was gradually added dropwise while maintaining the pH at 2.0 with a 32% sodium hydroxide aqueous solution. After maintaining for 15 minutes while stirring, a solution containing titanium tetrachloride in an amount of 414 g per liter was gradually added dropwise while maintaining the pH at 2.0 with a 32% sodium hydroxide aqueous solution. The titanium tetrachloride aqueous solution of 220 ml was added, whereby a suspension of titanium hydroxide-coated mica having a gloss of a silver color was obtained. (b-3) 85% phosphoric acid in an amount of 1.3 g and zinc chloride in an amount of 2.3 g were added to the suspension thus obtained and maintained for 10 minutes while stirring. Then, a 32% sodium hydroxide aqueous solution was slowly added dropwise to adjust the pH to 5.5. Next, 127 g of a 6% aluminum chloride 6 hydrate aqueous solution were added dropwise for about 30 minutes while maintaining the pH at 5.5. Then, an aqueous solution prepared by diluting 2.2 g a sodium silicate (SiO 2 : 36 %) with water to 14.7 g was added dropwise for about 10 minutes and maintained for about 10 minutes. (c-3) Then, the same operation as that in the step (c-2) of Example 7 was carried out, whereby a pearl pigment was obtained. Comparative Example 1 After carrying out the same operation as that in the step (a-1) of Example 6, the operation of the step (c-1) in Example 6 was carried out to thereby obtain a titanium oxide-coated pigment. Comparative Example 2 After carrying out the same operation as that in the step (a-2) of Example 7, the operation of the step (c-2) in Example 7 was carried out to thereby obtain a titanium oxide-coated pigment. Comparative Example 3 After carrying out the same operation as that in the step (a-3) of Example 8, the operation of the step (c-2) in Example 7 was carried out to thereby obtain a rutile-type titanium oxide-coated pigment. Example 12 The pearl pigment of 98 g obtained in Example 6 and SH1107 (manufactured by Toray Dow Corning Co., Ltd.) of 2 g as the organosiloxane compound were put into a mixer (high speed blender mixer manufactured by Worling Co., Ltd.) having a volume of 1200 ml and mixed by stirring. Further, the suspension was subjected to a heat treatment at 130°C, whereby a surface-treated pearl pigment having a good powder fluidity was obtained. Example 13 The pearl pigment in an amount of 98 g obtained in Example 6 and stearic acid of 2 g were put into the mixer (high speed blender mixer manufactured by Worling Co., Ltd.) having a volume of 1200 ml and mixed by stirring while heating at 70°C, whereby a surface-treated pearl pigment having a good powder fluidity was obtained. Discoloration resistance test: (1) Evaluation with n-propyl gallate n-Propyl gallate which is a kind of a phenol derivatives stabilizer discolored by contact with titanium oxide was used for evaluating a discoloring property to compare and evaluate the pigments of the present invention described in the examples and the pigments described in the comparative examples. [Preparation of test samples] A: The pigments in an amount of each 1 g obtained in the examples and the comparative examples and an ink medium (VS Medium manufactured by Dainichi Seika Co., Ltd.) in an amount of 9 g were put into a beaker and mixed sufficiently to homogeneity by stirring. B: The pigments in an amount of each 1 g obtained in the examples and the comparative examples and an ink medium (VS medium manufactured by Dainichi Seika Co., Ltd.) in an amount of 9 g containing n-propyl gallate (Extra Pure manufactured by Kanto Chemical Co., Ltd.) in a proportion of 1 % were put into a beaker and mixed sufficiently to homogeneity by stirring. [Test method] The samples of A and B were coated on a black and white masking test paper with a bar coater No. 20. After drying, these two b values (yellow) were measured with a color meter (CR-200 manufactured by Minolta Camera Co., Ltd.). The difference Δb value (the b value of the sample B - the b value of the sample A) between these b values were then calculated. The results thereof are shown in Table 1. Sample Δb Example 6 +0.3 Example 7 +0.4 Example 8 +0.3 Comp. Example 1 +5.9 Comp. Example 2 +6.7 Comp. Example 3 +4.8 As shown in Table 1, it has been observed that all of the pigments according to the present invention have small Δb values and therefore is excellent in discoloration resistance. (2) Evaluation by black lamp The light resistance was evaluated with a black lamp having its main light source in the ultraviolet region. [Preparation of test pieces] A sample pigment of 1 g and an anti-oxidation agent (BHT, Yoshinox manufactured by Yoshitomi Pharmaceutical Co., Ltd.) of 0.1 g were added to the substance prepared by blending HDPE (Hizex 2100J manufactured by Mitsui Petrochemical Co., Ltd.) of 98.8 g with a wetting agent (liquid paraffin, Hi-White manufactured by Nippon Petroleum Co., Ltd.), and mixed well. This mixture was molded by injection to prepare a test piece with a height of 14.8 cm, a width of 7.5 cm and a thickness of 0.2 cm. [Evaluating method] A light cabinet equipped with one black lamp (20 W, manufactured by Nippo Co., Ltd.) with emission in the ultraviolet region as a light source was prepared, and the test piece described above, which was separated by 20 cm from the light source, was left irradiated at room temperatures for 2 weeks. The b values were measured with a color-difference meter before and after the irradiation, and the difference thereof was calculated in terms of the Δb value. The results thereof are shown in Table 2. Sample Δb Example 2 +1.7 Example 6 +0.7 Example 7 +0.7 Example 8 +1.1 Iriodine 100 +5.1 Iriodine 120 +5.4 As apparent from the results summarized in Table 2, it has been observed that the pearl pigments of the present invention have small Δb values and therefore are excellent in discoloration resistance as compared with Iriodine 100 (Pearl pigment composed of 29 wt% titanium dioxide coated on mica with particle size of from 10 to 60 µ) and Iriodine 120 (Pearl pigment composed of 38 wt% titanium dioxide coated mica with particle size of from 5 to 20 µ). (3) Evaluation by light irradiation and bedewing cycle Cycle test using by UV rays and bedewing (wetting) was carried out. [Preparation of test pieces] Test pieces were prepared in the same manner as that described above, except that Hizex 6200B (manufactured by Mitsui Petrochemical Co., Ltd.) was substituted for HDPE (Hizex 2100J). [Evaluating method] A cycle test of irradiating and bedewing was carried out with a weather meter (dew panel light control weather meter manufactured by Suga Testing Machine Co., Ltd.) using a UV ray fluorescent lamp as a light source, wherein the test piece was set and exposed for 200 hours; and the b values before and after the exposure were measured with a color meter to calculate the Δb values. The results thereof are shown in Table 3. Sample Δb Example 6 +2.3 Example 7 +2.6 Example 8 +1.0 Iriodine 100 +5.3 Iriodine 120 +6.7 It is observed from the results summarized in Table 3 that all of the pigments according to the present invention have low levels of discoloration resistance. (4) Exposure evaluation in an ammonia gas atmosphere The test pieces were irradiated with a fluorescent lamp in an ammonia gas atmosphere in order to evaluate them. [Preparation of test pieces] HDPE (Hizex 2100J manufactured by Mitsui Petrochemical Co., Ltd.) in an amount of 980 g and the pigment of 20 g were charged into a Henshell mixer and mixed thoroughly. This mixture was molded by injection to prepare test pieces in the same manner as described above. [Evaluating method] The test pieces were set and tightly closed in a desiccator (diameter of the middle plate: 210 mm) into which 500 ml of 28% aqueous ammonia were placed. A lamp was adjusted so that the illuminance on the surface of the test pieces became 2000 lux, and the test pieces were irradiated with a fluorescent lamp at room temperature for 100 hours. The b values before and after the irradiation were measured with a color meter to calculate the Δb values. The results thereof are shown in Table 4. Sample Δb Example 7 +1.0 Example 8 +1.0 Iriodine 100 +5.4 Iriodine 120 +7.8 It has been observed from the results summarized in Table 4 that all of the pigments according to the present invention have low levels of discoloration resistance. Evaluation test for a plate out resistance: The plate-out of a pigment which is problematic when it is incorporated into plastics and processing was evaluated according to the following method. [Preparation of test samples] A compound prepared by blending a pigment of 5 parts with a soft polyvinyl chloride compound (containing DOP of 80 parts per 100 parts of PVC) in an amount of 100 parts was kneaded for 3 minutes with two rolls heated to 150°C. A sheet wound round the roll was removed, and the soft polyvinyl chloride compound was further kneaded at the same temperature for 3 minutes. The pigment (plate out pigment) adhered on the surface of the roll was removed and processed into a sheet with a thickness of about 1.5 mm. This sheet was separated from a roll face and processed again into a sheet with a thickness of 0.5 mm in the press conditions of 170°C and 20 kg/cm 2 , whereby a sample for evaluation was prepared. [Evaluation of plate-out property] The number of pigments distributed at optional 12 points in the sample prepared for evaluation was counted under a metallurgical microscope at a magnification of 100, and a plate-out amount was defined by an average of the number. The smaller this value is, the more excellent the plate out resistance is. The results thereof are shown in Table 6. Sample Plate out amount Example 6 122 Example 12 39 Example 13 102 Comp. Example 1 338 It has been observed from the results summarized in Table 6 that all of the pigments according to the present invention have small plate out amounts and are therefore excellent in plate-out resistance.

Claims: A pearl pigment comprising a flake substrate coated with titanium oxide having thereon phosphoric acid metal compounds and metal oxides, wherein the amount of a phosphoric acid component constituting said phosphoric acid metal compound is in a proportion of from 0.1 to 5 weight % in terms of P 2 O 5 based on titanium oxide; the kinds of metals constituting the phosphoric acid metal compound and the metal oxide are Zn, Al and Si, and the metal compounds thereof are coated in order; and the amounts thereof are in the proportion of from 0.5 to 10 weight % in terms of ZnO based on titanium oxide, from 0.5 to 10 weight % in terms of Al 2 O 3 based on titanium oxide, and of from 0.5 to 5 weight % in terms of SiO 2 based on titanium oxide, respectively. A pearl pigment as described in claim 1, wherein said pearl pigment is subjected to a surface coating treatment with at least one selected from a silane coupling agent, an organosiloxane compound, and aliphatic carboxylic acid. A method for producing a pearl pigment, comprising: preparing an aqueous suspension of a flake substrate, coating titanium oxide hydrate prepared by a hydrolysis of a titanium salt on the surface of the substrate, adding phosphoric acid or a phosphoric acid salt compound in an amount corresponding to from 0.1 to 5 weight % in terms of P 2 O 5 based on the amount of titanium oxide calculated from the amount of said titanium salt and a Zn salt to a coated particle surface to form a hydrolysis product of the Zn salt and the phosphoric acid metal salt thereof with alkali, the amounts thereof are in the proportions of from 0.5 to 10 weight % in terms of ZnO based on titanium oxide, then using an Al salt and alkali to form a neutralized hydrolysis product thereof, the amount thereof is in the proportion of from 0.5 to 10 weight % in terms of Al 2 O 3 based on titanium oxide, further adding a silicate compound to form a hydrolysis product thereof, the amount thereof is in the proportion of from 0.5 to 5 weight % in terms of SiO 2 based on titanium dioxide, and coating them in order, and filtrating and washing the coated particles, followed by drying and calcining them. A resin composition, paint and ink containing the pearl pigment described in claims 1 and 2.

Inventors: NISHIMAGI ATUKO, NITTA KATUHISA, YAZAWA MASAHIKO, NISHIMAGI, ATUKO, NITTA, KATUHISA, YAZAWA, MASAHIKO
Applicants: MERCK PATENT GMBH
Application year: 1996
Main classification: C09C1
IPC codes: C08K3, C09C3, C08K9, C09C1, C09D11, C09D5