Liquid crystalline compound and use thereof

Abstract: A process for producing a liquid crystalline compound represented by the following general formula (A):

Description: The present invention relates to a liquid crystalline compound and use thereof. More particularly, the present invention relates to a process for producing a novel liquid crystalline compound, which exhibits liquid crystallinity and, in addition, photoconductivity and fluorescence, and use of the liquid crystalline compound in a liquid crystalline charge transport material. Liquid crystalline compounds having various structures are known in the art and have been extensively used as a liquid crystal display material. Materials, wherein a charge transport molecule which serves as a charge transport site are dissolved or dispersed in a matrix material, such as a polycarbonate resin, or materials, wherein a charge transport molecule structure pends as a pendant on a polymer backbone, such as polyvinyl carbazole, are known in the art. These materials have been extensively used as materials for photoconductors in copying machines, printers and the like. For the above conventional charge transport materials, in the case of dispersive charge transport materials, that the charge transport molecule has high solubility in the polymer as a matrix is preferred from the viewpoint of improving the charge transport capability. In fact, however, bringing the charge transport molecule to a high concentration in the matrix leads to crystallization of the charge transport molecule in the matrix, and, for this reason, the upper limit of the concentration of the charge transport molecule is generally 20 to 50% by weight although it varies depending upon the kind of the charge transport molecule. This means that the matrix not having charge transport capability occupies not less than 50% by weight of the whole material. This in turn raises a new problem that the charge transport capability and response speed of a film formed from the material are limited by the excess matrix present in the material. On the other hand, in the case of the pendant type charge transport polymer, the proportion of the pendant having charge transport capability can be increased. This polymer, however, involves many practical problems associated with mechanical strength, environmental stability and durability of the formed film, film-forming properties and the like. In this type of charge transport material, the charge transport pendants are locally located in close proximity, and the local proximity portion serves as a stable site in hopping of charges and functions as a kind of trap, unfavorably resulting in lowered charge mobility. For all the above charge transport materials, electrical properties of such amorphous materials raise a problem that, unlike crystalline materials, the hopping site fluctuates in terms of space, as well as in terms of energy. For this reason, the charge transport depends greatly upon the concentration of the charge transport site, and the mobility is generally about 10 -6 to 10 -5 cm 2 /V.sec which is much smaller than that of the molecular crystal, 0.1 to 1 cm 2 /V.sec. Further, the amorphous materials have an additional problem that the charge transport properties depend greatly upon temperature and field strength. This is greatly different from the crystalline charge transport materials. A polycrystalline charge transport material is a promissing material in applications where a charge transport layer having a large area is necessary, because it can form an even charge transport film having a large area. The polycrystalline material, however, is inherently an uneven material from the microscopic viewpoint and involves a problem that a defect formed in the interface of particles should be inhibited. Accordingly, the present invention aims to solve the above problems of the prior art and to provide a novel charge transport material which simultaneously realizes advantages of the amorphous materials, that is, structural flexibility and evenness in a large area, and advantages of the crystalline materials having molecular orientation and is excellent in high-quality charge transport capability, thin film-forming properties, various types of durability. An object of the present invention is to provide a novel liquid crystalline compound which exhibits liquid crystallinity and, in addition, photoconductivity and fluorescence and a process for producing the same. Another object of the present invention is to provide a novel charge transport material which simultaneously realizes advantages of the amorphous materials, that is, structural flexibility and evenness in a large area, and advantages of the crystalline materials having molecular orientation and is excellent in high-quality charge transport capability, thin film-forming properties, various types of durability. According to one aspect of the present invention, there is provided a process for producing a liquid crystalline compound represented by the general formula (A) described below, comprising the steps of: reacting a compound represented by the general formula (1), described below, with a compound represented by the general formula (2) described below; brominating the reaction product to give a compound represented by the general formula (3) described below; and substituting the bromine atom with an R 2 group. According to another aspect of the present invention, there is provided a process for producing a liquid crystalline compound represented by the general formula (B) described below, comprising the step of: reacting a compound represented by the general formula (4), described below, with a compound represented by the general formula (5) described below. According to a further aspect of the present invention, there is provided a process for producing a liquid crystalline compound represented by the general formula (C) described below, comprising the step of: reacting two moles of a compound represented by the general formula (6), described below, with one mole of a compound represented by the general formula (7) described below. According to a yet further aspect of the present invention, there is provided a process for producing a liquid crystalline compound represented by the general formula (D) described below, comprising the step of: reacting two moles of a compound represented by the general formula (8), described below, with one mole of a compound represented by the general formula (9) described below. According to a yet further aspect of the present invention, there is provided a liquid crystalline charge transport material which exhibits smectic liquid crystallinity and has a reduction potential relative to a standard reference electrode (SCE) in the range of from - 0.3 to -0.6 (V vs. SCE). According to a yet further aspect of the present invention, there is provided a liquid crystalline charge transport material which exhibits smectic liquid crystallinity and has an oxidation potential relative to a standard reference electrode (SCE) in the range of from 0.2 to 1.3 (V vs. SCE). Figs. 1, 2, 3 and 4 are cross-sectional views of embodiments where the crystalline charge transport material according to the present invention has been applied to a charge transport layer in an image recording device: Fig. 5 is a cross-sectional view of an embodiment where the liquid crystalline charge transport material has been applied to a space light modulating device; and Fig. 6 is a cross-sectional view of an embodiment where the liquid crystalline charge transport material according to the present invention has been applied to a thin film transistor. Process for producing liquid crystalline compound The first aspect of the present invention relates to a process for producing a liquid crystalline compound represented by the general formula (A), comprising the steps of: reacting a compound represented by the general formula (1) with a compound represented by the general formula (2); brominating the reaction product to give a compound represented by the general formula (3); and substituting the bromine atom of the compound (3) with an R 2 group: wherein R 1 and R 2 represent (a) a cyano group, (b) a nitro group, (c) a fluorine atom, or (d) a C 1 - C 22 straight-chain or branched, saturated or unsaturated, alkyl or alkoxy group attached to the aromatic ring through an oxygen atom, or a sulfur atom, provided that at least one of R 1 and R 2 represents said alkyl or alkoxy group. The second aspect of the present invention relates to a process for producing a liquid crystalline compound represented by the general formula (B), comprising the step of: reacting a compound represented by the general formula (4) with a compound represented by the general formula (5): wherein R 1 and R 2 represent (a) a cyano group, (b) a nitro group, (c) a fluorin atom, or (d) a C 1 - C 22 straight-chain or branched, saturated or unsaturated, alkyl or alkoxy group attached to the aromatic ring through an oxygen atom, or a sulfur atom, provided that at least one of R 1 and R 2 represents said alkyl or alkoxy group; and X and Y are respectively groups which are reacted with each other to form Z selected from a -COO-, -OCO-, -N=N-, -CH=N-, -N=N-, - CH 2 S-, -CH=CH-, or acetylene group. The third aspect of the present invention relates to a process for producing a liguid crystalline compound represented by the general formula (C), comprising the step of: reacting 2 moles of a compound represented by the general formula (6) with one mole of a compound represented by the general formula (7): wherein R 1 is a C 1 - C 22 straight-chain or branched saturated or unsaturated alkyl or alkoxy group attached to the aromatic ring through an oxygen or sulfur atom. The fourth aspect of the present invention relates to a process for producing a liquid crystalline compound represented by the general formula (D), comprising the step of: reacting two moles of a compound represented by the general formula (8) with one mole of a compound represented by the general formula (9): wherein R 1 is a C 1 - C 22 straight-chain or branched saturated or unsaturated alkyl or alkoxy group attached to the aromatic ring through an oxygen or sulfur atom; and X and Y are respectively groups which are reacted with each other to form Z selected from a -COO-, -OCO-, -N-N-, -CH=N-, - N=N-, -CH 2 S-, -CH=CH-, or acetylene group. According to a specific one embodiment of the present invention, there is provided a process for producing a liquid crystalline compound represented by the following general formula (I), comprising the steps of: reacting a 4-alkoxybenzaldehyde with o-aminobenzenethiol to synthesize a 2-(4'-alkoxyphenyl)benzothiazole; brominating the 2-(4'-alkoxyphenyl)benzothiazole to synthesize a 2-(4'-alkoxyphenyl)-6-bromobenzothiazole; and reacting the resultant bromide with an alkanethiol: wherein R represents a C 4 - C 20 alkyl group; and R' represents a C 4 - C 20 alkyl group, provided that the total number of carbon atoms contained in R and R' is 10 or more. A further preferred embodiment of the production process will be described. According to the present invention, a 4-alkoxybenzaldehyde is reacted with 1 mole or more, preferably 1.1 to 1.5 moles or more, based on one mole of the 4-alkoxybenzaldehyde, of o-aminobenzenethiol in a solvent suitable for a dehydration reaction (oxidative cyclization), preferably dimethylsulfoxide, at a temperature of 100°C or above, preferably 120 to 160°C, for about 30 min to 2 hr. In this reaction, the aldehyde group, the amino group, and the thiol group are combined together to form a thiazole ring, thus giving a 2-(4'-alkoxyphenyl)benzothiazole as an intermediate. This reaction can be easily achieved, and the intermediate is produced in a high yield of not less than 90%. The intermediate may be purified before use in the subsequent step or alternatively used in the subsequent step without purification. The 2-(4'-alkoxyphenyl)benzothiazole is then brominated. In the bromination, the 2-(4'-alkoxyphenyl)benzothiazole is dissolved in a suitable solvent, such as glacial acetic acid, and bromine in an equimolar or slightly excessive molar amount is dropwise added thereto. In this reaction, bromine is easily substituted in the 6-position of the benzothiazole ring to give a 2-(4'-alkoxyphenyl)-6-bromobenzothiazole, and the reaction under mild conditions with heating can give the bromide in a yield of not less than 60%. When this intermediate contains a dibromination product and/or a substance remaining unreacted as impurities, it is preferably purified by recrystallization before use in the subsequent step. Finally, the above bromide is reacted with an alkanethiol to give a liquid crystalline compound according to the present invention. Since this reaction is an aromatic nucleophilic displacement reaction by taking advantage of a thiolate anion, it is preferably performed in an alkaline atmosphere. For example, a liquid crystalline compound represented by the general formula (I) is produced by suspending an oil dispersion of sodium hydride in an ether, dropwise adding a corresponding alkanethiol to the suspension to produce a sodium salt of the alkanethiol, and reacting the sodium salt with the above bromide in a suitable solvent at a temperature of about 30 to 100°C for 30 min to 2 hr. According to the process of the present invention, the number of carbon atoms of the alkyl group in the 4-alkoxybenzaldehyde and the alkanethiol is important, and the number of carbon atoms of the alkyl group is preferably not less than 4, preferably 4 to 20 from the viewpoint of developing excellent liquid crystallinity. For the alkanethiol, the number of carbon atoms of the alkyl group is 4 or more, preferably 4 to 20. These alkyl groups may be somewhat branched. However, in order to develop excellent liquid crystallinity, the alkyl group is more preferably linear with the total number of carbon atoms of R and R' being 10 or more, preferably 12 to 40. Further, liquid crystalline compounds represented by the following general formula (II) also fall within the scope of the present invention: wherein R represents C 7 H 15 and R' represents C 6 H 13 , C 8 H 17 , C 10 H 21 or C 12 H 25 . The above liquid crystalline compounds according to the present invention can be produced in a high yield from a p-alkoxybenzaldehyde, for example, by the following reaction scheme: wherein R and R' are as defined above and DMI represents N,N'-dimethylimidazolidinone. The present invention provides a novel liquid crystalline compound which exhibits liquid crystallinity and, in addition, photoconductivity and fluorescence. The novel liquid crystalline compound is useful as a material for a liquid crystal display, a photosensitive material for electrophotography. In particular, the liquid crystalline compound of the present invention has strong fluorescence and, hence, when used as a material for a color liquid crystal display or used in combination with a dichroic dye, can effectively utilize an ultraviolet portion in a backlight source, offering a display image having excellent sharpness and brightness. Liquid crystalline charge transport material According to a further aspect of the present invention, there is provided a liquid crystalline charge transport material using the liquid crystalline compounds of the present invention which exhibits smectic liquid crystallinity and has a reduction potential relative to a standard reference electrode (SCE) in the range of from - 0.3 to -0.6 (V vs. SCE). According to a further aspect of the present invention, there is provided a liquid crystalline charge transport material using the liquid crystalline compounds of the present invention which exhibits smectic liquid crystallinity and has an oxidation potential relative to a standard reference electrode (SCE) in the range of from 0.2 to 1.3 (V vs. SCE). A liquid crystalline molecule, by virtue of its molecular structure, has self-orientation, and, in the case of charge transport utilizing this molecule as a hopping site, unlike the above molecule dispersive material, the spacial and energy scattering of the hopping site is inhibited, enabling a band-like transport property such as found in a molecular crystal to be realized. This enables a mobility of about 10 -3 to 10 -2 cm 2 /V.sec, that is, a larger mobility than that in the conventional molecular dispersive material, to be realized, and, in addition, the charge transport properties do not depend upon electric field. In order that the material serves as a hole transport material, the molecule should have a low ionization potential, and, hence, the oxidation potential should be in the range of from 0.2 to 1.3 (V vs. SCE) relative to a standard reference electrode (SCE). Further, in order that the material serves as an electron transport material, the molecule should have high electron affinity, and, hence, the reduction potential should be in the range of from -0.3 to -0.6 (V vs. SCE). The above requirements are the same as the well known requirements for a charge transport molecule used in the conventional molecule dispersive material. Preferred liquid crystalline charge transport materials of the present invention will be listed in Tables 1 and 2. The liquid crystalline charge transport materials according to the present invention are useful for various applications such as photosensors, electroluminescence devices, photoconductors, space modulating devices, and thin film transistors. The liquid crystalline charge transfer materials according to the present invention can realize high-speed mobility and inhibition of the creation of structural traps. Therefore, high-speed response photosensors may be mentioned as the first application thereof. Next, by virtue of excellent charge transport properties, the liquid crystalline charge transfer materials according to the present invention can be used as a charge transfer layer in electroluminescence devices. Further, since electric field orientation and photoconductivity can be simultaneously switched, they can be used in image display devices. The application to image display devices will be described as a representative example. In an image display device, when a device comprising a transparent substrate, such as glass, a transparent electrode, such as ITO (indium-tin-oxide), a charge generating layer capable of generating carriers according to exposure, the liquid crystalline charge transport material of the present invention, and a counter electrode (such as a gold electrode) laminated in that order is subjected to imagewise exposure (input image) through the bottom of the device as shown in the schematic diagram, the liquid crystalline charge transport material is aligned according to the exposure, resulting in flow of carriers in the counter electrode (gold electrode). The input image can be reproduced by optical reading of the alignment of the liquid crystal. The larger the smectic properties of the liquid crystal, the longer the storage time of the alignment of the liquid crystal and the longer the storage time of the input information. Figs. 1 to 3 are explanatory diagrams of embodiments where the liquid crystalline charge transport material according to the present invention has been applied to a charge transport layer in an image recording device. Fig. 1 is a schematic view of a photosensor, an embodiment where the liquid crystalline charge transport material according to the present invention has been applied to a charge transport layer. Use of the photosensor will be described in more detail. As shown in Fig. 3, the device is subjected to pattern exposure from the direction of the above in the drawing while applying a voltage across the upper and lower electrodes 15. Carriers are generated in a pattern form in 14', and charges transported by a charge transport layer 14'' are discharged in a space 19 and reach the surface of an information recording layer 11. The information recording layer is, for example, a liquid crystal/polymer composite layer formed of a composite of a smectic liquid crystal and a polymer. The liquid crystal is aligned in a pattern form in an electric field of accumulated charges and accumulated, enabling optical recording to be performed. In the embodiment shown in Fig. 4, exposure with a voltage being applied may be carried out in the same manner as described above in connection with the embodiment shown in Fig. 3. The generated charges (image) are accumulated on the top surface of a dielectric layer 20, and the liquid crystal is aligned in a pattern form in an electric field of charges accumulated in the same manner as described above in connection with the embodiment shown in Fig. 3 and accumulated, enabling optical reading to be performed. Further, the liquid crystalline charge transport material according to the present invention can be used also in a pace optical light modulating device schematically shown in Fig. 5. Furthermore, the liquid crystalline charge transport materials of the present invention can also be used as an active layer of a thin film transistor. For example, as shown in Fig. 6, the liquid crystalline material may be disposed on a substrate having thereon source, drain, and gate electrodes. Thus, the liquid crystalline charge transport materials according to the present invention are useful for various applications such as photosensors, electroluminescence devices, photoconductors, space modulating devices, and thin film transistors. Example A1 44.6 g (0.34 mol) of 4-cyanobenzaldehyde and 54.4 g (0.64 mol) of o-aminobenzenethiol were dissolved in 300 ml of dimethyl sulfoxide, and the temperature of the solution was raised to 140°C. The produced water and the dimethyl sulfoxide were distilled off. After heating for one hr, the residue was cooled, water was added thereto, and the resultant precipitate was collected by filtration and washed with ethanol. The crude crystal thus obtained was recrystallized from ethyl acetate to give 2-(4'-cyanophenyl)benzothiazole. 22.4 g (0.095 mol) of the compound was dissolved in 250 ml of acetic acid, and 18.6 g (0.116 mol) of bromine was dropwise added thereto. As soon as bromine was added, a yellow bromine adduct was produced. Subsequently, 150 ml of water was added, and the mixture was stirred at 80°C for 2 hr. It was then cooled, and the resultant precipitate was collected by filtration and washed with ethanol. The crude product thus obtained was recrystallized from ethyl acetate. A 60 % by weight dispersion of 0.8 g (0.02 mol) of sodium hydride in an oil was suspended in 50 ml of ether, 3.22 g (0.022 mol) of 1-octanethiol was dropwise added thereto, and the mixture was refluxed for 30 min. Thereafter, the ether was distilled off, 50 ml of N,N-dimethylimidazolidinone was added to the residue, and the temperature of the system was raised to 60°C. 0.01 mol of 2-(4'-cyanophenyl)-6-bromobenzothiazole was added to the solution, and stirring was continued for one hr. The solution was cooled, water was added thereto, and the resultant precipitate was collected by filtration and washed with ethanol. The product thus obtained was recrystallized from a hexane/ethyl acetate mixed solution to give a compound represented by the following formula: Example A2 1.31 g (0.01 mol) of 4-cyanobenzaldehyde, 2.5 g (0.01 mol) of 2-amino-6-hexyloxybenzothiazole, and 30 ml of ethanol were heated at 70°C for 2 hr. The reaction mixture was then cooled to room temperature, and the resultant solid matter was collected by filtration and recrystallized from ethanol to give a compound represented by the following formula: Example A3 2.21 g (0.01 mol) of 2,5-diamino-1,4-benzenedithiol/dihydrochloric acid adduct, 5.34 g (0.024 mol) of 4-hexyloxybenzoic acid, 3 g of phosphorus pentaoxide, and 50 ml of methanesulfonic acid were allowed to react at 90°C for one hr and then heated at 80°C for 5 hr. The resultant product was collected by filtration and recrystallized from N-methylpyrrolidone to give a compound represented by the following formula: Example A4 2.56 g (0.01 mol) of 2,6-dimercaptobenzo(1,2-d: 5,6-d')bisthiazole, 4.54 g (0.02 mol) of 4-hexyloxybenzyl chloride, 1.2 g of potassium carbonate, and 15 ml of N-methylpyrrolidone were heated at 80°C for 3 hr. The reaction mixture was poured into water, and the resultant solid matter was collected by filtration and washed with water, methanol, and chloroform. It was then recrystallized from benzene to give a compound represented by the following formula: wherein R=CH 3 (CH 2 ) 5 O. Example A5 The procedure of Example A1 was repeated to prepare liquid crystalline compounds represented by the general formula (A) wherein R 1 and R 2 represent the following groups. The liquid crystalline compounds thus obtained had the same properties as the liquid crystalline compound prepared in Example A1. Example R 1 R 2 A5-1 CH 3 (CH 2 ) 9 O CN A5-2 CH 3 CH 2 C*H(CH 3 )CH 2 O CN A5-3 CH 3 (CH 2 ) 5 O O(CH 2 ) 9 CH 3 A5-4 NO 2 S(CH 2 ) 7 CH 3 A5-5 NO 2 O(CH 2 ) 7 CH 3 A5-6 F O(CH 2 ) 9 CH 3 Example A6 The procedure of Example A2 was repeated to prepare liquid crystalline compounds represented by the general formula (B) wherein R 1 and R 2 represent the following groups. The liquid crystalline compounds thus obtained had the same properties as the liquid crystalline compound prepared in Example A2. Example R 1 R 2 Z A6-1 NO 2 O(CH 2 ) 9 CH 3 CH=N A6-2 CH 3 (CH 2 ) 5 O O(CH 2 ) 5 CH 3 COO A6-3 CH 3 CH 2 C*H(CH 3 )CH 2 O O(CH 2 ) 7 CH 3 CH=CH A6-4 CN O(CH 2 ) 8 CH 3 CH=CH A6-5 CH 3 (CH 2 ) 9 O O(CH 2 ) 3 CH 3 C≡C A6-6 CH 3 (CH 2 ) 5 O O(CH 2 ) 5 CH 3 N=N Example A7 The procedure of Example A3 was repeated to prepare liquid crystalline compounds represented by the general formula (C) wherein R 1 represents the following groups. The liquid crystalline compounds thus obtained had the same properties as the liquid crystalline compound prepared in Example A3. Example R 1 A7-1 CH 3 (CH 2 ) 9 O A7-2 CH 3 (CH 2 ) 9 A7-3 CH 3 (CH 2 ) 9 S A7-4 CH 3 (CH 2 ) 5 S A7-5 CH 3 (CH 2 ) 8 S A7-6 CH 3 CH 2 C*H(CH 3 )CH 2 O Example A8 The procedure of Example A3 was repeated to prepare liquid crystalline compounds represented by the general formula (D) wherein R 1 represents the following group. The liquid crystalline compounds thus obtained had the same properties as the liquid crystalline compound prepared in Example A4. Example R 1 Z A8-1 CH 3 (CH 2 ) 5 O COO A8-2 CH 3 (CH 2 ) 5 O CH=N A8-3 CH 3 CH 2 C*H(CH 3 )CH 2 O CH=CH A8-4 CH 3 (CH 2 ) 5 S CH=N A8-5 CH 3 (CH 2 ) 3 O N=N A8-6 CH 3 (CH 2 ) 9 O COO According to the present invention, novel liquid crystalline compounds are provided which exhibit liquid crystallinity and, in addition, photoconductivity and fluorescence. The novel liquid crystalline compounds are useful as materials for liquid crystal displays, photosensitive materials for electrophotography and the like. Example B [Synthesis of 2-(4'-heptyloxyphenyl)benzothiazole] 74.2 g (0.34 mol) of 4-heptyloxybenzaldehyde and 54.4 g (0.46 mol) of o-aminobenzenethiol were dissolved in 300 ml of dimethyl sulfoxide, and the temperature of the solution was raised to 140°C. The produced water and the dimethyl sulfoxide were distilled off. After heating for one hr, the residue was cooled, water was added thereto, and the resultant precipitate was collected by filtration and washed with ethanol. The crude crystal thus obtained was recrystallized from ethyl acetate. The yield was 90%. The above compound exhibited the following peaks in NMR spectrum: 1 H NMR (CDCl 3 ) δ = 0.90 (3H, t, J = 6.6 Hz), 1.25-1.47 (8H, m), 1.81 (2H, quint, J = 6.6 Hz), 4.01 (2H, t, J = 6.5 Hz), 6.97 (2H, d, J = 8.5 Hz), 7.33 (1H, d, J = 8.9 Hz), 7.45 (1H, t, J = 8.5 Hz), 7.86 (1H, d, J = 7.9 Hz), 8.01 (1H, d, J = 8.9 Hz), 8.02 (2H, d, J = 8.5 Hz) Further, it exhibited the following peaks in IR (KBr disc) spectrum: 506, 568, 622, 648, 698, 730, 968, 1010, 1037, 1300, 1316, 1394, 1417, 1441, 1470, 1483, 1520, 1603, 2852, 2912 cm -1 [Synthesis of 2-(4'-heptyloxyphenyl)-6-bromobenzothiazole] 31.0 g (0.095 mol) of 2-(4'-heptyloxyphenyl)benzothiazole was dissolved in 250 ml of acetic acid, and 18.6 g (0.116 mol) of bromine was dropwise added thereto. As soon as bromine was added, a yellow bromine adduct was produced. Subsequently, 150 ml of water was added, and the mixture was stirred at 80°C for 2 hr. It was then cooled, and the resultant precipitate was collected by filtration and washed with ethanol. The crude product thus obtained was recrystallized from ethyl acetate. The yield was 68%. The above compound exhibited the following peaks in NMR spectrum: 1 H NMR (CDCl 3 ) δ = 0.90 (3H, t, J = 6.6 Hz), 1.33-1.50 (8H, m), 1.81 (2H, quint, J = 6.6 Hz), 4.03 (2H, t, J = 6.6 Hz), 6.98 (2H, d, J = 8.6 Hz), 7.55 (1H, dd, J1 = 2.0 and J2 = 8.6 Hz), 7.85 (1H, d, J = 8.6 Hz), 7.98 (1H, d, J = 2.0 Hz), 7.99 (2H, d, J = 8.6 Hz) Further, it exhibited the following peaks in IR (KBr disc) spectrum: 520, 563, 622, 666, 695, 723, 748, 859, 1015, 1040, 1090, 1115, 1224, 1393, 1438, 1474, 1488, 1520, 1541, 2855, 2922, 2937 cm -1 [General process for synthesizing 2-(4'-alkoxyphenyl)-6-alkylthiobenzothiazole derivatives] A 60 % by weight dispersion of 0.8 g (0.02 mol) of sodium hydride in an oil was suspended in 50 ml of ether, 0.022 mol of a corresponding alkanethiol was dropwise added thereto, and the mixture was refluxed for 30 min. Thereafter, the ether was distilled off, 50 ml of N,N'-dimethylimidazolidinone was added to the residue, and the temperature of the system was raised to 60°C. 0.01 mol of 2-(4'-heptyloxyphenyl)-6-bromobenzothiazole was added to the solution, and stirring was continued for one hr. The solution was cooled, water was added thereto, and the resultant precipitate was collected by filtration and washed with ethanol. The crude product thus obtained was recrystallized from hexane. 2-(4'-alkoxyphenyl)-6-alkylthiobenzothiazole, having the same R (heptyl group) and different R', had the following properties. [2-(4'-heptyloxyphenyl)-6-hexylthiobenzothiazole] (yield 65%): 1 H NMR (CDCl 3 ) δ = 0.89 (3H, t, J = 6.6 Hz), 0.90 (3H, t, J = 6.6 Hz), 1.27-1.47 (14H, m), 1.67 (2H, quint, J = 7.2 Hz), 1.82 (2H, quint, J = 6.6 Hz), 2.98 (2H, t, J = 7.2 Hz), 4.02 (2H, t, J = 6.6 Hz), 6.98 (2H, d, J = 8.6 Hz), 7.43 (1H, dd, J1 = 1.7 and J2 = 8.3 Hz), 7.82 (1H, d, J = 1.7 Hz), 7.91 (1H, d, J = 8.3 Hz), 7.99 (2H, d, J = 8.6 Hz) IR (KBr disc) 520, 570, 621, 701, 727, 966, 1010, 1040, 1112, 1276, 1306, 1396, 1418, 1441, 1474, 1485, 1520, 1543, 1575, 1606, 2855, 2956 cm -1 Heating: Cryst (80.5°C) - SmA (103.7°C) - iso (2°C/min) Cooling: Iso (103.2°C) - SmA (83.9°C) - Cryst (5°C/min) [2-(4'-heptyloxyphenyl)-6-octylthiobenzothiazole] (yield 54%): 1 H NMR (CDCl 3 ) δ = 0.87 (3H, t, J = 6.9 Hz), 0.90 (3H, t, J = 6.6 Hz), 1.18-1.47 (18H, m), 1.67 (2H, quint, J = 7.3 Hz), 1.81 (2H, quint, J = 6.6 Hz), 2.97 (2H, t, J =7.3 Hz), 4.02 (2H, t, J = 6.6 Hz), 6.98 (2H, d, J = 8.9 Hz), 7.42 (1H, dd, J1 = 1.6 and J2 = 8.6 Hz), 7.81 (1H, d, J = 1.6 Hz), 7.90 (1H, d, J = 8.6 Hz), 7.98 (2H, d, J = 8.9 Hz) IR (KBr disc) 520, 570, 621, 702, 727, 774, 843, 967, 1017, 1041, 1112, 1176, 1276, 1306, 1396, 1441, 1474, 1486, 1520, 1543, 1575, 1607, 2855, 2956 cm -1 Heating: Cryst (94.0°C) - SmA (102.0°C) - iso (2°C/min) Cooling: Iso (100.3°C) - SmA (89.8°C) - Sm? (78.2°C) - Cryst (5°C/min) [2-(4'-heptyloxyphenyl)-6-decylthiobenzothiazole] (yield 63%): 1 H NMR (CDCl 3 ) δ = 0.87 (3H, t, J = 6.9 Hz), 0.90 (3H, t, J = 6.6 Hz), 1.25-1.47 (22H, m), 1.66 (2H, quint, J = 7.3 Hz), 1.81 (2H, quint, J = 6.6 Hz), 2.96 (2H, t, J = 7.3 Hz), 4.02 (2H, t, J = 6.6 Hz), 6.97 (2H, d, J = 8.9 Hz), 7.43 (1H, dd, J1 = 2.0 and J2 = 8.6 Hz), 7.81 (1H, d, J = 2.2 Hz), 7.89 (1H, d, J = 8.6 Hz), 7.98 (2H, d, J = 8.9 Hz) IR (KBr disc) 570, 812, 842, 967, 1018, 1041, 1112, 1177, 1306, 1393, 1441, 1474, 1485, 1519,1575, 1607, 2853, 2957 cm -1 Heating: Cryst (95.5°C) - SmA (100.9°C) -iso (2°C/min) Cooling: Iso (100.6°C) -SmA (93.1°C) -Cryst (5°C/min) [2-(4'-heptyloxyphenyl)-6-dodecylthiobenzothiazole] (yield 67%): 1 H NMR (CDCl 3 ) δ = 0.87 (3H, t, J = 7.0 Hz), 0.90 (3H, t, J = 6.6 Hz), 1.28-1.46 (26H, m), 1.62(2H, quint, J = 7.6 Hz), 1.78 (2H, quint, J = 7.6 Hz), 2.97 (2H, t, J = 7.6 Hz), 4.02 (2H, t, J = 6.6 Hz), 6.97 (2H, d, J = 8.6 Hz), 7.42 (1H, dd, J1 = 2.0 and J2 = 8.6 Hz), 7.81 (1H, d, J = 2.0 Hz), 7.90 (1H, d, J = 8.6 Hz), 7.98 (2H, d, J = 8.6 Hz) IR (KBr disc) 571, 812, 841, 967, 1018, 1111, 1178, 1306, 1395, 1474, 1486, 1519, 1607, 2852, 2920, 2956 cm -1 Heating: Cryst (90.0°C) - SmA (98.0°C) - iso (2°C/min) Cooling: Iso (96.1°C) -SmA (85.7°C) - Cryst (5°C/min) UV - VIS λmax = 327 nm (10 -6 M in CCl 3 ) PL (He - Cd Laser 324 nm) λmax = 420, 438 nm Example C Synthesis Example 1 of Intermediate [Synthesis of 2-(4'-heptyloxyphenyl)benzothiazole] 74.2 g (0.34 mol) of 4-heptyloxybenzaldehyde and 54.4 g (0.46 mol) of o-aminobenzenethiol were dissolved in 300 ml of dimethyl sulfoxide, and the temperature of the solution was raised to 140°C. The produced water and the dimethyl sulfoxide were distilled off. After heating for one hr, the residue was cooled, water was added thereto, and the resultant precipitate was collected by filtration and washed with ethanol. The crude crystal thus obtained was recrystallized from ethyl acetate. The yield was 90%. The above compound exhibited the following peaks in NMR spectrum: 1 H NMR (CDCl 3 ) δ = 0.90 (3H, t, J = 6.6 Hz), 1.25-1.47 (8H, m), 1.81 (2H, quint, J = 6.6 Hz), 4.01 (2H, t, J = 6.5 Hz), 6.97 (2H, d, J = 8.5 Hz), 7.33 (1H, d, J = 8.9 Hz), 7.45 (1H, t, J = 8.5 Hz), 7.86 (1H, d, J = 7.9 Hz), 8.01 (1H, d, J = 8.9 Hz), 8.02 (2H, d, J = 8.5 Hz) Further, it exhibited the following peaks in IR (KBr disc) spectrum: 506, 568, 622, 648, 698, 730, 968, 1010, 1037, 1300, 1316, 1394, 1417, 1441, 1470, 1483, 1520, 1603, 2852, 2912 cm -1 Synthesis Example 2 of Intermediate [Synthesis of 2-(4'-heptyloxyphenyl)-6-bromobenzothiazole] 31.0 g (0.095 mol) of 2-(4'-heptyloxyphenyl)benzothiazole was dissolved in 250 ml of acetic acid, and 18.6 g (0.116 mol) of bromine was dropwise added thereto. As soon as bromine was added, a yellow bromine adduct was produced. Subsequently, 150 ml of water was added, and the mixture was stirred at 80°C for 2 hr. It was then cooled, and the resultant precipitate was collected by filtration and washed with ethanol. The crude product thus obtained was recrystallized from ethyl acetate. The yield was 68%. The above compound exhibited the following peaks in NMR spectrum: 1 H NMR (CDCl 3 ) δ = 0.90 (3H, t, J = 6.6 Hz), 1.33-1.50 (8H, m), 1.81 (2H, quint, J = 6.6 Hz), 4.03 (2H, t, J = 6.6 Hz), 6.98 (2H, d, J = 8.6 Hz), 7.55 (1H, dd, J1 = 2.0 and J2 = 8.6 Hz), 7.85 (1H, d, J = 8.6 Hz), 7.98 (1H, d, J = 2.0 Hz), 7.99 (2H, d, J = 8.6 Hz) Further, it exhibited the following peaks in IR (KBr disc) spectrum: 520, 563, 622, 666, 695, 723, 748, 859, 1015, 1040, 1090, 1115, 1224, 1393, 1438, 1474, 1488, 1520, 1541, 2855, 2922, 2937 cm -1 Examples C1 to C4 [General process for synthesizing 2-(4'-alkoxyphenyl)-6-alkylthiobenzothiazole derivatives] A 60 % by weight dispersion of 0.8 g (0.02 mol) of sodium hydride in an oil was suspended in 50 ml of ether, 0.022 mol of a corresponding alkanethiol was dropwise added thereto, and the mixture was refluxed for 30 min. Thereafter, the ether was distilled off, 50 ml of N,N'-dimethylimidazolidinone was added to the residue, and the temperature of the system was raised to 60°C. 0.01 mol of 2-(4'-heptyloxyphenyl)-6-bromobenzothiazole was added to the solution, and stirring was continued for one hr. The solution was cooled, water was added thereto, and the resultant precipitate was collected by filtration and washed with ethanol. The crude product thus obtained was recrystallized from hexane. 2-(4'-alkoxyphenyl)-6-alkylthiobenzothiazole, having the same R (heptyl group) and different R', had the following properties. Example C1 [2-(4'-heptyloxyphenyl)-6-hexylthiobenzothiazole] (yield 65%): 1 H NMR (CDCl 3 ) δ = 0.89 (3H, t, J = 6.6 Hz), 0.90 (3H, t, J = 6.6 Hz), 1.27-1.47 (14H, m), 1.67 (2H, quint, J = 7.2 Hz), 1.82 (2H, quint, J = 6.6 Hz), 2.98 (2H, t, J = 7.2 Hz), 4.02 (2H, t, J = 6.6 Hz), 6.98 (2H, d, J = 8.6 Hz), 7.43 (1H, dd, J1 = 1.7 and J2 = 8.3 Hz), 7.82 (1H, d, J = 1.7 Hz), 7.91 (1H, d, J = 8.3 Hz), 7.99 (2H, d, J = 8.6 Hz) IR (KBr disc) 520, 570, 621, 701, 727, 966, 1010, 1040, 1112, 1276, 1306, 1396, 1418, 1441, 1474, 1485, 1520, 1543, 1575, 1606, 2855, 2956 cm -1 Heating: Cryst (80.5°C) - SmA (103.7°C) - iso (2°C/min) Cooling: Iso (103.2°C) - SmA (83.9°C) - Cryst (5°C/min) Example C2 [2-(4'-heptyloxyphenyl)-6-octylthiobenzothiazole] (yield 54%): 1 H NMR (CDCl 3 ) δ = 0.87 (3H, t, J = 6.9 Hz), 0.90 (3H, t, J = 6.6 Hz), 1.18-1.47 (18H, m), 1.67 (2H, quint, J = 7.3 Hz), 1.81 (2H, quint, J = 6.6 Hz), 2.97 (2H, t, J =7.3 Hz), 4.02 (2H, t, J = 6.6 Hz), 6.98 (2H, d, J = 8.9 Hz), 7.42 (1H, dd, J1 = 1.6 and J2 = 8.6 Hz), 7.81 (1H, d, J = 1.6 Hz), 7.90 (1H, d, J = 8.6 Hz), 7.98 (2H, d, J = 8.9 Hz) IR (KBr disc) 520, 570, 621, 702, 727, 774, 843, 967, 1017, 1041, 1112, 1176, 1276, 1306, 1396, 1441, 1474, 1486, 1520, 1543, 1575, 1607, 2855, 2956 cm -1 Heating: Cryst (94.0°C) - SmA (102.0°C) - iso (2°C/min) Cooling: Iso (100.3°C) - SmA (89.8°C) - Sm? (78.2°C) - Cryst (5°C/min) Example C3 [2-(4'-heptyloxyphenyl)-6-decylthiobenzothiazole] (yield 63%): 1 H NMR (CDCl 3 ) δ = 0.87 (3H, t, J = 6.9 Hz), 0.90 (3H, t, J = 6.6 Hz), 1.25-1.47 (22H, m), 1.66 (2H, quint, J = 7.3 Hz), 1.81 (2H, quint, J = 6.6 Hz), 2.96 (2H, t, J = 7.3 Hz), 4.02 (2H, t, J = 6.6 Hz), 6.97 (2H, d, J = 8.9 Hz), 7.43 (1H, dd, J1 = 2.0 and J2 = 8.6 Hz), 7.81 (1H, d, J = 2.2 Hz), 7.89 (1H, d, J = 8.6 Hz), 7.98 (2H, d, J = 8.9 Hz) IR (KBr disc) 570, 812, 842, 967, 1018, 1041, 1112, 1177, 1306, 1393, 1441, 1474, 1485, 1519,1575, 1607, 2853, 2957 cm -1 Heating: Cryst (95.5°C) - SmA (100.9°C) -iso (2°C/min) Cooling: Iso (100.6°C) -SmA (93.1°C) -Cryst (5°C/min) Example C4 [2-(4'-heptyloxyphenyl)-6-dodecylthiobenzothiazole] (yield 67%): 1 H NMR (CDCl 3 ) δ = 0.87 (3H, t, J = 7.0 Hz), 0.90 (3H, t, J = 6.6 Hz), 1.28-1.46 (26H, m), 1.62(2H, quint, J = 7.6 Hz), 1.78 (2H, quint, J = 7.6 Hz), 2.97 (2H, t, J = 7.6 Hz), 4.02 (2H, t, J = 6.6 Hz), 6.97 (2H, d, J = 8.6 Hz), 7.42 (1H, dd, J1 = 2.0 and J2 = 8.6 Hz), 7.81 (1H, d, J = 2.0 Hz), 7.90 (1H, d, J = 8.6 Hz), 7.98 (2H, d, J = 8.6 Hz) IR (KBr disc) 571, 812, 841, 967, 1018, 1111, 1178, 1306, 1395, 1474, 1486, 1519, 1607, 2852, 2920, 2956 cm -1 Heating: Cryst (90.0°C) - SmA (98.0°C) - iso (2°C/min) Cooling: Iso (96.1°C) -SmA (85.7°C) - Cryst (5°C/min) UV - VIS λmax = 327 nm (10 -6 M in CCl 3 ) PL (He - Cd Laser 324 nm) λmax = 420, 438 nm Examples C5 to C10 Liquid crystalline compounds represented by the above general formula wherein R and R' represent the following groups were prepared in the same manner as in the above examples and comparative examples. All the liquid crystalline compounds thus obtained had the same properties as those prepared in Examples C1 to C4. Example R R' Example C5 Hexyl group Heptyl group Example C6 Octyl group Nonyl group Example C7 Hexyl group Undecynyl group Example C8 Decyl group Tetradecyl group Example C9 Amyl group Tridecyl group Example C10 Dodecyl group Heptyl group According to the present invention, novel liquid crystalline compounds which exhibit liquid crystallinity and, in addition, photoconductivity and fluorescence. The novel liquid crystalline compounds are useful as materials for liquid crystal displays, photosensitive materials for electrophotography.

Claims: A process for producing a liquid crystalline compound represented by the general formula (A), comprising the steps of: reacting a compound represented by the general formula (1) with a compound represented by the general formula (2); brominating the reaction product to give a compound represented by the general formula (3); and substituting the bromine atom of the compound (3) with an R 2 group to obtain the liquid crystalline compound (A): wherein R 1 and R 2 represent (a) a cyano group, (b) a nitro group, (c) a fluorine atom, or (d) a C 1 - C 22 straight-chain or branched, saturated or unsaturated, alkyl or alkoxy group attached to the aromatic ring through an oxygen atom, or a sulfur atom, provided that at least one of R 1 and R 2 represents said alkyl or alkoxy group. A process for producing a liquid crystalline compound represented by the general formula (B), comprising the step of: reacting a compound represented by the general formula (4) with a compound represented by the general formula (5) to obtain the liquid crystalline compound (B): wherein R 1 and R 2 represent (a) a cyano group, (b) a nitro group, (c) a fluorine atom, or (d) a C 1 - C 22 straight-chain or branched saturated or unsaturated, alkyl or alkoxy group attached to the aromatic ring through an oxygen atom, or a sulfur atom, provided that at least one of R 1 and R 2 represents said alkyl or alkoxy group; and X and Y are respectively groups which are reacted with each other to form Z selected from a -COO-, -OCO-, -N=N-, -CH=N-, -N=N-, -CH 2 S-, -CH=CH-, or -C≡C- group. A process for producing a liquid crystalline compound represented by the general formula (C), comprising the step of: reacting 2 moles of a compound represented by the general formula (6) with one mole of a compound represented by the general formula (7) to obtain the liquid crystalline compound (C): wherein R 1 is a C 1 - C 22 straight-chain or branched saturated or unsaturated alkyl or alkoxy group attached to the aromatic ring through an oxygen or sulfur. A process for producing a liquid crystalline compound represented by the general formula (D), comprising the step of: reacting two moles of a compound represented by the general formula (8) with one mole of a compound represented by the general formula (9) to obtain the liquid crystalline compound (D): wherein R 1 is a C 1 - C 22 straight-chain or branched saturated or unsaturated alkyl or alkoxy group attached to the aromatic ring through an oxygen or sulfur group; and X and Y are respectively groups which are reacted with each other to form Z selected from a -COO-, -OCO-, -N=N-, -CH=N-, - N=N-, -CH 2 S-, -CH=CH-, or -C≡C- group. A process for producing a liquid crystalline compound represented by the following general formula (I), comprising the steps of: reacting a 4-alkoxybenzaldehyde with o-aminobenzenethiol to synthesize a 2-(4'-alkoxyphenyl)benzothiazole; brominating the 2-(4'-alkoxyphenyl)benzothiazole to synthesize a 2-(4'-alkoxyphenyl)-6-bromobenzothiazole; and reacting the resultant bromide with an alkanethiol to obtain the liquid crystalline compound (I): wherein R represents a C 4 - C 20 alkyl group; and R' represents a C 4 - C 20 alkyl group, provided that the total number of carbon atoms contained in R and R' is 10 or more. A liquid crystalline compound represented by the following general formula (II): wherein R represents C 7 H 15 and R' represents C 6 H 13 , C 9 H 17 , C 10 H 21 or C 12 H 25 . A liquid crystalline charge transport material using the liquid crystalline compounds obtained by the process according to any one of claims 1 to 5, wherein the material exhibits smetic liquid crystallinity and has a reduction potential relative to a standard reference electrode (SCE) in the range of from -0.3 to -0.6 (V vs. SCE). A liquid crystalline charge transport material using the liquid crystalline compounds obtained by the process according to any one of claims 1 to 5, wherein the material exhibits smetic liquid crystallinity and has an oxidation potential relative to a standard reference electrode (SCE) in the range of from 0.2 to 1.3 (V vs. SCE). An image display device comprising the material according to claim 7 or 8 in a drive path. An electroluminescence device comprising the material according to claim 7 or 8 in a drive path. A photoconductor comprising the material according to claim 7 or 8 in a drive path. A space light modulating device comprising the material according to claim 7 or 8 in a drive path. A thin film transistor comprising the material according to claim 7 or 8 in a drive path.

Inventors: AKADA MASANORI, ANDO MASAYUKI, FUNABASHI MASAHIRO, HANNA JUNICHI, KOSAKA YOZO, AKADA, MASANORI, ANDO, MASAYUKI, FUNABASHI, MASAHIRO, HANNA, JUNICHI, KOSAKA, YOZO, Akada, Masanori, c/o Dai Nippon printing Co., Ltd., Ando, Masayuki, c/o Dai Nippon Printing Co., Ltd., Kosaka, Yozo, c/o Dai Nippon Printing Co., Ltd.
Applicants: DAINIPPON PRINTING CO LTD, DAI NIPPON PRINTING CO., LTD.
Application year: 1996
Main classification: C07D277
IPC codes: C09K11, C07D277, C09K19, G11C13