Hydrocarbylsiloxy-aluminoxane compositions

Abstract: Siloxy-aluminoxane compositions which are the reaction products of hydrocarbylsiloxanes and aluminoxanes and which have improved solubility and stability even at up to 60 weight percent when compared to the original aluminoxane. The compositions in combination with metallocenes of transition lathanide and actinide metals form catalysts which can be used in the polymerization of olefins such as ethylene.

Description: This process relates generally to soluble aluminoxane derivatives and more particularly to siloxy-aluminoxane compositions obtained by the reaction of hydrocarbylsiloxanes and aluminoxanes which, in the presence of metallocenes, form catalytically active compositions for olefin polymerization. U.S. Patent No. 3,740,384 discloses that the addition of dihydroxysiloxane to non-metallocene organozirconium catalyst systems in the absence of aluminoxanes gave improved catalyst activity in olefin polymerization. Likewise, U.S. Patent No. 4,945,076 describes the improved activity in olefin polymerization which is obtained by the addition of dihydroxysiloxane to a catalyst system consisting of a metallocene and an aluminoxane. The resulting ethylene polymer is said to have acquired a lower melt flow rate (MFR) than those produced without the silicon compound. U.S. Patent No. 5,034,549 discloses that a preformed catalyst component is obtained by the reaction of dihydroxysiloxane or silicon diol with a zirconocene. The patent further alleges that this catalyst component, when used in conjunction with methylaluminoxane, formed a good catalyst system for olefin polymerization. All the above mentioned disclosures describe the use of alkoxy-silanes having Si-O-C bonds, silicon diols having Si-OH bonds and dihydroxysiloxanes having both the Si-O-Si and Si-OH bonds. The reagents used in the present invention, namely hydrocarbylsiloxanes, have only the Si-O-Si bonds. The chemical reactivity of the hydrocarbylsiloxanes is significantly different from those of the silanols, silyl ethers, silyl esters and hydroxy disiloxanes ( 1 . Comprehensive Organometallic Chemistry , Vol. 2, Chap. 9; Pergamon Press, 1982: 2 . Comprehensive Organic Chemistry , Vol. 3, Chap. 13 Pergamon Press N.Y. 1979). Those skilled in the art would appreciate the fact that silicon compounds having Si-OH bonds generally undergo dehydration and condensation reactions. These reactions are rarely observed in the case of hydrocarbylsiloxanes. Thus, one could not anticipate any obvious similarity between the reactions of silanols, silyl ethers and silyl esters compared to hydrocarbylsiloxanes. In fact one would not expect to isolate under similar conditions, the same product described in U.S. Patent No. 5,034,549 by substituting an hydrocarbylsiloxane for the dihydroxysiloxane or silicon diol, as this would require the breaking of Si-O bond which is more difficult than breaking the SiO-H bond. Methylaluminoxane is the most important aluminoxane used as co-catalyst in polymerization reactions. It is usually obtained in aromatic solvents, in which it is only temporarily soluble. Methylaluminoxane solutions are usually plagued with instability with respect to gel formation or solid precipitation within a short period. Dilute toluene solutions of methylaluminoxane (10 weight percent or less) are reasonably stable to gel formation or solid precipitation for a couple of weeks at room temperature. However, the stability of methylaluminoxane solution drastically decreases as the concentration increases to about 20 weight percent or more. U.S. patent 5,391,529, relates to aiuminoxanes reacted with alkyldisiloxanes to form novel, soluble siloxy-aluminum compounds which, in combination with metallocenes, provide olefin polymerization catalysts having very high activity. Summary of the Invention In a first aspect the present invention relates to a siloxy-aluminoxane composition comprising an aluminoxane which contains hydrocarbylsiloxane moieties which are free of Si-OH bonds, wherein the molar portion of aluminum to hydrocarbylsiloxane is from about 1:1 to 1000:1 and said hydrocarbylsiloxane moieties are derived from an aryldisiloxane, a linear or cyclic aryl polysiloxane, or a linear, branched or cyclic alkyl polysiloxane. Preferably said hydrocarbylsiloxane moieties are derived from a hydrocarbylsiloxane selected from the group consisting of octaphenylcyclotetrasiloxane, diphenyltetramethyldisiloxane, hexaphenyldisiloxane, tetraphenyldimethyldisiloxane, hexamethylcyclotrisiloxane, octamethylcyclotetrasiloxane, and octamethyltrisiloxane. In this case said aluminoxane is preferably methylaluminoxane. The composition may then contain up to about 60 weight percent of said methylaluminoxane, preferably from about 25-60 weight percent of said methylaluminoxane. In a second aspect the invention relates to an olefin polymerization catalyst comprising a metallocene of a transition, lathanide, or actinide metal and a siloxy-aluminoxane composition which comprises an aluminoxane which contains hydrocarbylsiloxane moieties which are free of Si-OH bonds, wherein the molar portion of aluminum to hydrocarbylsiloxane is from about 1:1 to 1000:1 and said hydrocarbylsiloxane moieties are derived from an aryldisiloxane, a linear or cyclic aryl polysiloxane, or a linear, branched or cyclic alkyl polysiloxane. Preferably said hydrocarbylsiloxane moieties are derived from a hydrocarbylsiloxane selected from the group consisting of octaphenylcyclotetrasiloxane, diphenyltetramethyldisiloxane, hexaphenyldisiloxane, tetraphenyldimethyldisiloxane, hexamethylcyclotrisiloxane, octamethyltrisiloxane and octamethylcyclotetrasiloxane and said hydrocarbylaluinoxane is methylaluminoxane. In a third aspect the present invention relates to a method of stabilizing an aluminoxane against gel formation and reducing its trimethylaluminum content comprising reacting said aluminoxane with a hydrocarbylsiloxane which is free of Si-OH bonds. It likewise relates to a method of stabilizing an aluminoxane by reacting hydrocarbylsiloxane with an aluminoxane solvent medium in which the molar ratio of aluminum to hydrocarbylsiloxane is from 1:1 to 1000:1, and wherein the hydrocarbylsiloxane used in the reaction is free of hydroxyl groups and is a hydrocarbyldisiloxane or a linear or cyclic polysiloxane. Preferably the reaction comprises: a) forming a solution of a siloxy-aluminoxane composition by mixing the hydrocarbylsiloxane with the aluminoxane in an organic solvent medium, and b) heating the solution of the siloxy-aluminoxane composition under reduced pressure to form a more concentrated solution. Detailed Description of the Invention It has now been found that the reaction products of aluminoxanes with other hydrocarbylsiloxanes, such as aryl, alkyl-aryl and cycloalkyl disiloxanes and polysiloxanes, including cyclic polysiloxanes, provide aluminoxanes containing hydrocarbylsiloxane moieties which impart stability to the aluminoxanes such that the aluminoxanes are not only more soluble in organic solvents but do not easily form gels during storage. For example, a concentrated MAO solution (20 weight percent or above) can be treated with cyclic or linear siloxane compounds to give solution stable, concentrated siloxy-methylaluminoxane compositions, which, after further solvent removal, produce 25-60 weight percent siloxy-methylaluminoxane solutions having enhanced solution stability. Alternatively, one can treat a dilute solution of the MAO solution with siloxanes to form stable siloxy-methylaluminoxane compositions which can optionally be further concentrated to give 25-60 weight percent siloxy-methylaluminoxane solutions. In accordance with this invention there is provided a siloxy-aluminoxane composition which comprises an aluminoxane which contains hydrocarbylsiloxane moieties which are free of Si-OH bonds, wherein the molar portion of aluminum to hydrocarbylsiloxane is from 1:1 to 1000:1, and said hydrocarbylsiloxane moieties are derived from an aryldisiloxane, a linear or cyclic aryl polysiloxane or a linear, branched as cyclic alkyl polysiloxane. Also provided is an olefin polymerization catalyst comprising a metallocene of a transition, lathanide or actinide metal and a siloxy-aluminoxane composition which comprises an aluminoxane which contains hydrocarbylsiloxane moieties which are free of Si-OH bonds, wherein the molar portion of aluminum to hydrocarbylsiloxane is from 1:1 to 1000:1, and said hydrocarbylsiloxane is defined as above. The siloxy-aluminoxane compositions are obtainable by the reaction of an aluminoxane and a hydrocarbyldi- or polysiloxane such that the aluminoxane contains hydrocarbylsiloxane moieties which are chemically bonded thereto. Preferred aluminoxanes for use in making the siloxy-aluminoxane compounds are hydrocarbylaluminoxanes. Hydrocarbylaluminoxanes may exist in the form of linear or cyclic polymers with the simplest compounds being a tetraalkylaluminoxane such as tetramethylaluminoxane, (CH 3 ) 2 AlOAl(CH 3 ) 2 , or tetraethylaluminoxane, (C 2 H 5 ) 2 AlOAl(C 2 H 5 ) 2 . The compounds preferred for use in olefin polymerization catalysts usually contain about 4 to 20 of the repeating units: where R is C 1 -C 10 alkyl and especially preferred are methylaluminoxanes (MAO). The methylaluminoxanes can contain some higher alkyl groups to improve their solubility. Such modified methylaluminoxanes are described, for example, in U.S. Patent No. 5,157,008. The aluminoxanes can be prepared as known in the art by the partial hydrolysis of trialkylaluminum compounds. The trialkylaluminum compounds can be hydrolyzed by adding either free water or water containing solids, which can be either hydrates or porous materials which have absorbed water. Because it is difficult to control the reaction by adding water per se, even with vigorous agitation of the mixture, the free water is preferably added in the form of a solution or a dispersion in an organic solvent. Suitable hydrates include salt hydrates such as, for example, CuSO 4 •5H 2 O, Al 2 (SO 4 ) 3 •18H 2 O, FeSO 4 •7H 2 O, AlCl 3 •6H 2 O, Al(NO 3 ) 3 •9H 2 O, MgSO 4 •7H 2 O, ZnSO 4 •7H 2 O, Na 2 SO 4 •10H 2 O, MgCl 2 .6H 2 O, Na 3 PO 4 •12H 2 O, LiBr•2H 2 O, LiCl•1H 2 O, LiI•2H 2 O, LiI•3H 2 O, KF•2H 2 O, NaBr•2H 2 O and the like and alkali or alkaline earth metal hydroxides such as, for example, NaOH•H 2 O, NaOH•2H 2 O, Ba(OH) 2 •8H 2 O, KOH•2H 2 O, CsOH•1H 2 O, and LiOH•1H 2 O. Mixtures of any of the above hydrates can be used. The mole ratios of free water or water in the hydrate to total alkyl aluminum compounds in the mixture can vary widely, such as for example from 2:1 to 1:4 with ratios of from 4:3 to 1:3.5 being preferred. Such processes for preparing hydrocarbylaluminoxanes are described, for example, in U.S. Patent No. 4,908,463. The methylaluminoxanes contain varying amounts, of from 5 to 35 mole percent, of the aluminum value as unreacted trimethylaluminum. The hydrocarbylsiloxanes for use in the invention have hydrocarbyl groups which preferably contain from 1 to 30 carbon atoms and include linear and/or branched alkyl groups which contain from I to 24 carbon atoms, cycloalkyl groups which contain from 3 to 24 carbon atoms and alkylaryl or aryl groups which contain from 6 to 30 carbon atoms. The hydrocarbylsiloxanes are chosen from disiloxanes and linear or cyclic polysiloxanes The hydrocarbylsiloxanes contain the Si-O-Si bond and are substantially free of Si-OH bonds. The hydrocarbylsiloxanes can contain mixed hydrocarbyl groups. Non-limiting examples of hydrocarbylsiloxanes include hexaphenyldisiloxane, diphenyltetramethyldisiloxane, tetraphenyldimethyldisiloxane, hexamethylcyclotrisiloxane, octamethylcyclotetrasiloxane, octaphenylcyclotetrasiloxane, and octamethyltrisiloxane. The siloxy-aluminoxane compositions can be prepared by reacting the aluminoxane and hydrocarbylsiloxane in an organic solvent medium in molar portions of aluminum in the aluminoxane to hydrocarbyldisiloxane of from 1:1 to 1000:1 and preferably from 1:1 to 50:1. Mixtures of aluminoxanes and/or hydrocarbylsiloxanes can be used in forming the compositions. Any inert organic solvent can be used as the reaction medium. Non-limiting examples of solvents include aliphatic hydrocarbons such as pentane, isopentane, hexane, cyclohexane, heptane, octane, decane, dodecane, hexadecane, and octadecane, with those having carbon numbers of 5 to 10 being preferred and aromatic hydrocarbons such as benzene, toluene, xylene, and cumene, with those having carbon numbers of 6 to 20 being preferred. Generally amounts of solvent to provide a total concentration of reactants of from 3 to 30 wt. percent are used. Reaction temperatures usually range from 0 to 200°C. Preferred reaction temperatures range from 25 to 150°C. The siloxy-aluminoxane compounds can be used in combination with metallocenes to provide olefin polymerization catalysts. Such metallocenes are well known in the art and non-limiting examples include the metallocenes described in U.S. Patent Nos. 4,892,851, 5,017,714, 5,026,798, 5,145,819, 5,296,434, 5,324,800 and 5,329,033. Illustrative examples of such metallocenes are bis-(cyclopentadienyl)-zirconium dimethyl, bis-(cyclpentadienyl)-zirconium dichloride, bis-(cyclopentadienyl)-monomethylmonochloride, bis-(cyclpentadienyl)-titanium dichloride, bis-(cyclopentadienyl)-titanium difluoride, cyclopentadienylzirconium tri-(2-ethylhexanoate), bis-cyclopentadienyl)-zirconium hydrogen chloride, and bis-(cyclopentadienyl)hafnium dichloride. The catalyst components are used in proportions to provide mole ratios of transition metal atom to aluminum atom of from 0.0002:1 to 0.2:1 and preferably 0.0005:1 to 0.02:1. The catalyst components can be used in solution or deposited on a solid support. The solid support can be any particulate solid, and particularly porous supports such as talc or inorganic oxides, or resinous support material such as polyolefins. Preferably, the support material is an inorganic oxide in finely divided form. Suitable inorganic oxide support materials which are desirably employed include Group IIA, IIIA, IVA or IVB metal oxides such as silica, alumina, silica-alumina and mixtures thereof. Other inorganic oxides that may be employed either alone or in combination with the silica, alumina or silica-alumina are magnesia, titania, and zirconia. Other suitable support materials are finely divided polyolefins such as finely divided polyethylene. The catalysts are effective to produce olefin polymers and especially ethylene polymers and ethylene/α-olefin copolymers. Examples of olefins that can be polymerized in the presence of the catalysts of the invention include α-olefins having 2 to 20 carbon atoms such as ethylene, propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, and 1-octadecene. Polymerization of ethylene or copolymerization with ethylene and an α-olefin having 3 to 10 carbon atoms is preferable. Such polymerizations may be performed in either the gas or liquid phase (e.g. in a solvent, such as toluene, or in a diluent, such as heptane). The polymerization can be conducted at conventional temperatures (e.g., 0° to 120°C.) and pressures (e.g., ambient to 50 kg/cm 2 ) using conventional procedures as to molecular weight regulations and the like. The invention is further illustrated by, but is not intended to be limited to, the following examples. The following examples were carried out under inert atmosphere conditions, using Schlenk glassware and vacuum line, in conjunction with a N 2 -drybox. Solvents were distilled using standard methods. Filtration and vacuum distillation were done inside a N 2 -drybox and distillates were collected in a trap at -78°C. Siloxanes were purchased from commercial sources and used without further purification. Aluminoxanes were obtained from stock solutions produced by Albemarle Corporation. Despite the enhanced solution stability of the siloxy-aluminoxane compositions, compared to regular aluminoxane solutions, the polymerization activity is not adversely affected. On the contrary, significant activity improvement is observed for certain siloxy-aluminoxane compositions. Example 1 Solid methylaluminoxane (MAO, 38 mmol Al) was suspended in hexane (50 mL). The mixture was stirred at room temperature (30 minutes). Hexamethyldisiloxane (HMDS, 4.7 mmol) was then slowly added via syringe. After stirring for 16 hours, the mixture was filtered. The hexane solution was then concentrated to dryness by vacuum distillation. The resulting solid siloxy-MAO product contained 65% of the initial aluminum value. Silicon-29 and proton NMR showed one sharp singlet each for the siloxy group. Additionally, H-1 NMR showed the usual broad peak for methylaluminoxane in the aluminum alkyl region. The sharp signals suggest a probable end capping environment of the siloxy group in the MAO structure. Example 2 An MAO solution in toluene (871g, 1446 mmol Al) was placed in a reaction bottle. Then, hexamethyldisiloxane (23.5g, 144.6 mmol), 10%) was added slowly at room temperature. After addition, the mixture was stirred at room temperature for about two hours. Then, the mixture was heated at 80°C (oil bath) for another two hours. On cooling to room temperature, the mixture was filtered through a medium frit to obtain a clear colorless solution product (884g). A portion of the liquid product (772g) was concentrated at 50°C/0.1 mm Hg to give a product which contains 32 weight percent MAO product. This product exhibits remarkable solution stability such that after 16 months no sign of gel formation or solid precipitation was observed, even at this high concentration. Furthermore, a drastic reduction in the TMA content of the original MAO solution was also observed. Thus, TMA content was reduced from the original 20 mole percent to 14 mole percent of the total aluminum content, which is about 30% reduction. This result is in sharp contrast to popular belief that excess TMA is required to improve MAO solubility and stability. Some of the product was also concentrated to dryness under reduced pressure to obtain a free flowing solid product. H-1 NMR of both the solid and liquid products showed Si-Me peaks and also revealed additional fine structures in the Al-Me region which are not observable in the corresponding spectra for regular untreated MAO. Example 3 A concentrated solution of MAO in toluene (232g, 1114 mmol Al) was placed in a reaction bottle. Hexamethyldisiloxane (18g, 111.4 mmol) was added and the mixture stirred at room temperature for 6 hours. Then the mixture was filtered through a coarse frit and then through a medium frit to give clear colorless liquid product. The siloxy-methylaluminoxane product contains 27 weight percent MAO product. The product was stored in a dry glass bottle inside a N2-drybox. This product started to show the first sign of gel formation after 5 weeks. Regular MAO solution of similar concentration usually takes less than 2 weeks to show gel formation. This product is drastically less stable compared to the product in Example 2. This, therefore, shows the importance of heating and removal of excess HMDS and gaseous byproducts as done in example 1. Example 4 A dilute solution of MAO in toluene (140g, 232 mmol Al) was placed in a reaction bottle. Octamethylcyclotetrasiloxane (6.9g, 23.2 mmol, 10%) was added slowly. The mixture was stirred at room temperature for 2 hours. A slight gas evolution with foaming was observed. Then, the mixture was heated at 90-100°C (oil bath) for about 4 hours. After filtration through a medium frit, a clear colorless liquid product resulted. A part of the product was concentrated under reduced pressure to give 25 weight percent MAO product solution, which did not show any visible sign of gel formation over a six month period. Example 5 A concentrated solution of MAO in toluene (60g, 264 mmol Al) was placed in a reaction bottle. Octamethylcyclotetrasiloxane (1.5g, 5 mmol, 2%) was added, followed by heating at 80°C (oil bath) for 2 hours. On cooling, the mixture was filtered through a medium frit. The product was further concentrated to remove some volatiles. The resulting solution contains 25 weight percent product. Example 6 To solution of MAO in toluene (800g, 1360 mmol Al) was added octaphenylcyclotetrasiloxane (2.2g, 2.72 mmol, 0.2%). The reaction was carried out as described in Example 5. Lots of foaming was observed during and after filtration. The product was further concentrated to give 35 weight percent MAO product solution. Example 7 MAO solution (93g, 418 mmol Al) was allowed to react with hexamethylcyclotrisiloxane (1.9g, 8.4 mmol, 2%) as described in Example 5. A foamy but clear and colorless liquid product was obtained after filtration. The product was further concentrated to give 36 weight percent MAO product solution. Example 8 A solution of MAO in toluene (86g, 361 mmol Al) was treated with tetraphenyldimethyldisiloxane (1.5g, 3.6 mmol, 1%) and the reaction carried out as described in Example 5. The product was further concentrated under reduced pressure to give 31 weight percent solution. Example 9 MAO solution (85g, 357 mmol Al) was treated with tetraphenyldimethyldisiloxane (0.15g, 0.36 mmol, 0.1%) as described in Example 5. The experiment was designed to determine the minimum amount of siloxane required to provide enhance solution stability for concentrated MAO solution. The product was further concentrated to obtain 36 weight percent solution. Example 10 To a solution of MAO in toluene (91g, 410 mmol Al) was added diphenyltetramethyldisiloxane (5.9g, 20.5 mmol, 5%). The reaction was carried out as described in Example 5. After filtration, the product was further concentrated to give 45 weight percent solution. Polymerization Ethylene polymerization was conducted in a Part reactor (600 mL) equipped with a cooling coil, magnetic stirrer, pressure gauge and a gas inlet. The catalyst system, siloxy-MAO and zirconocene dichloride, are dissolved in toluene (300 mL). The loading was done in a dry-box after which the reactor was assembled in a well vented hood. Ethylene was passed into the reactor at 4.2 kg/cm 2 (60 psi) for 10 minutes while the temperature was maintained at about 90°C. After cooling down to room temperature, the reactor contents were poured into a beaker where an equal volume of methanol was added to destroy the catalyst system. The polyethylene was collected by filtration and then dried in a vacuum oven. Examples 11 A solid sample obtained from Example 1 was separately employed in conjunction with zirconocene dichloride to conduct ethylene polymerization tests as described above. Results are shown in Table 1. Examples 12 to 14 Siloxy-aluminoxane compositions obtained from Examples 4, 5 and 6 were separately used in the presence of zirconocene dichloride to polymerize ethylene as described above. Results indicate that alkyl and aryl cyclic polysiloxanes are also useful in forming soluble siloxy-methylaluminoxane compositions which are polymerization active. Comparison A comparative polymerization was carried out using regular methylaluminoxane (MAO) solution in toluene (9.4 wt. % Al) in conjunction with zirconocene dichloride without the addition of disiloxane. The results are shown in Table 1. Table 1 shows that no significant additional activity was gained as the molar ratio of HMDS was increased. However, the data in this table show a notable increase (about 50%) in the activity of the siloxy-MAO derivatives as compared to the regular MAO under similar conditions.

Claims: A siloxy-aluminoxane composition comprising an aluminoxane which contains hydrocarbylsiloxane moieties which are free of Si-OH bonds, wherein the molar portion of aluminum to hydrocarbylsiloxane is from about 1:1 to 1000:1 and said hydrocarbylsiloxane moieties are derived from an aryldisiloxane, a linear or cyclic aryl polysiloxane, or a linear, branched or cyclic alkyl polysiloxane. The composition of claim 1 wherein said hydrocarbylsiloxane moieties are derived from a hydrocarbylsiloxane selected from the group consisting of octaphenylcyclotetrasiloxane, diphenyltetramethyldisiloxane, hexaphenyldisiloxane, tetraphenyldimethyldisiloxane, hexamethylcyclotrisiloxane, octamethylcyclotetrasiloxane, and octamethyltrisiloxane. The composition of claim 2 wherein said aluminoxane is methylaluminoxane. The composition of claim 3, which contains up to about 60 weight percent of said methylaluminoxane. The composition of claim 4 wherein said composition contains from about 25-60 weight percent of said methylaluminoxane. An olefin polymerization catalyst comprising a metallocene of a transition, lathanide, or actinide metal and a siloxy-aluminoxane composition which comprises an aluminoxane which contains hydrocarbylsiloxane moieties which are free of Si-OH bonds, wherein the molar portion of aluminum to hydrocarbylsiloxane is from about 1:1 to 1000:1 and said hydrocarbylsiloxane moieties are derived from an aryldisiloxane, a linear or cyclic aryl polysiloxane, or a linear, branched or cyclic alkyl polysiloxane. The catalyst of claim 6 wherein said hydrocarbylsiloxane moieties are derived from a hydrocarbylsiloxane selected from the group consisting of octaphenylcyclotetrasiloxane, diphenyltetramethyldisiloxane, hexaphenyldisiloxane, tetraphenyldimethyldisiloxane, hexamethylcyclotrisiloxane, octamethyltrisiloxane and octamethylcyclotetrasiloxane and said hydrocarbylaluminoxane is methylaluminoxane. A method of stabilizing an aluminoxane against gel formation and reducing its trimethylaluminum content comprising reacting said aluminoxane with a hydrocarbylsiloxane which is free of Si-OH bonds. A method of stabilizing an aluminoxane by reacting hydrocarbylsiloxane with an aluminoxane solvent medium in which the molar ratio of aluminum to hydrocarbylsiloxane is from 1:1 to 1000:1 and wherein the hydrocarbylsiloxane used in the reaction is free of hydroxyl groups and is a hydrocarbyldisiloxane or a linear or cyclic polysiloxane. The method of claim 9, wherein the reaction comprises: a) forming a solution of a siloxy-aluminoxane composition by mixing the hydrocarbylsiloxane with the aluminoxane in an organic solvent medium, and b) heating the solution of the siloxy-aluminoxane composition under reduced pressure to form a more concentrated solution. The method of claim 10, by which a more concentrated solution containing 25-60 weight percent of the siloxy-aluminoxane composition is obtained. The method of claim 10, by which a dry solid siloxy-aluminoxane composition is formed in step b). The method of one of claims 9 to 12, wherein the aluminoxane is a methylaluminoxane formed by partial hydrolysis of trimethylaluminum. The method of any of claims 9 to 13, wherein the organic solvent medium is a hydrocarbon solvent. The method of claim 14, wherein the aromatic hydrocarbon solvent is toluene. The method of any of claims 9 to 15, wherein the hydrocarbylsiloxane used in the reaction is an aryldisiloxane, a linear or cyclic arylpolysiloxane, or a linear, branched, or cyclic alkylpolysiloxane. The method of claim 16, wherein the polysiloxane is octaphenylcyclotetrasiloxane, hexamethylcyclotrisiloxane, octamethyltrisiloxane, diphenyltetramethyldisiloxane, hexaphenyldisiloxane, tetraphenyldimethyldisiloxane or octamethylcyclotetrasiloxane.

Inventors: SANGOKOYA SAMUEL A, SANGOKOYA, SAMUEL A.
Applicants: ALBEMARLE CORP, ALBEMARLE CORPORATION
Application year: 1996
Main classification: C07F7
IPC codes: C08F4, C08L83, C08F10, C07F7, C07F5