Removal of an alkali metal compound from a polymer cement

Abstract: The invention provides a process for removing an alkali metal compound from a polymer cement comprising: i) washing the polymer cement with a weak acid to remove the alkali metal compound from the polymer cement; ii) removing the alkali metal compound from the acid; and iii) recycling the acid to wash more polymer cement.

Description: The present invention relates to a process for removing an alkali metal compound from a polymer cement. More specifically, the present invention relates to a process for removing an alkali metal compound from a low viscosity functionalised polymer cement. Acids are often used to remove catalyst residues and alkali metal compounds from polymer cements. Strong acids such as sulphuric and phosphoric acid are particularly effective at washing hydrogenation catalyst residues (nickel and aluminium) and alkali metal compounds (lithium) from polymer cements. If it is desired to recycle the acids, ion exchange is used, but it has been found that it is very difficult to remove lithium from the acids since most ion exchange resins have a very low selectivity for removing lithium. The process is even less effective if the wash step requires the use of a concentrated acid. Surprisingly, it has now been found that the selectivity of ion exchange processes for the removal of lithium from an acid can be improved when a weak acid such as citric acid or acetic acid is used in the wash step, instead of a strong acid. Accordingly, the present invention relates to a process for removing an alkali metal compound from a polymer cement comprising: i) washing the polymer cement with an acid having a pKa greater than 3 to remove the alkali metal compound from the polymer cement; ii) removing the alkali metal compound from the acid; and iii) recycling the acid to wash more polymer cement. It should be noted that in the context of the present invention an acid having a pKa of greater than 3 is considered a weak acid. Suitably, the weak acid has a pKa of less than 6. Preferably, the weak acid is selected from the group consisting of citric acid and acetic acid. A further improvement is established when in step ii) the weak acid is contacted with a first ion exchange resin functional to remove nickel and aluminium compounds from the acid; and the acid so obtained is then contacted with a second ion exchange resin functional to remove the alkali metal compound from the acid. The second ion exchange resin is more selective for removing the alkali metal compound from the acid than the first ion exchange resin is. Suitably, use is made of a solution of the weak acid. It also has been found that several ion exchange resins have a higher selectivity for removing lithium than others have. These are AMBERLYST 35 and AMBERLYST 15, (trademarks of Rohm and Haas for strong acid resins, H+ form), and BAYER OC 1501, (a trademark of Miles for a strong acid resin, H+ form). It has been found that lithium removal from an acid solution is improved in a process where nickel and aluminium are removed first on a resin such as AMBERLITE 200C (a trademark of Rohm and Haas for a strong acid resin) and lithium is removed next on one of the second ion exchange resins having a higher selectivity for removing lithium. The present invention is particularly applicable to low viscosity functionalised polymer cements (described hereinafter) and relates in particular to lithium removal post hydrogenation. The polymerisation process suitably uses a lithium initiator, which is preferably a protected functional initiator (PFI). PFI diols contain one mole of lithium per mole of polymer, and the termination step produces a lithium salt. The presence of the lithium salt may affect hydrogenation performance, although the magnitude of this impact is not yet fully understood. In cases where hydrogenation performance is acceptable, the lithium salt may be removed post hydrogenation in the same step used to remove the hydrogenation catalyst, which contains nickel and aluminium. As mentioned hereinbefore, removal of the lithium salts from the polymer cement post hydrogenation may be accomplished by washing the cement with a weak acid such as citric acid or acetic acid. This transfers the cations to the acid solution, which must then be treated to remove the salts before recycling. The AMBERLYST 35 resin is preferred and has higher capacity and selectivity for lithium than AMBERLITE 200C. A two bed configuration, in which a bed of AMBERLITE 200C is followed by a bed of AMBERLYST 35, achieves the best compromise between resin selectivity, capacity, and regenerability in a fixed bed process. The process is preferably run a temperature within the range of 21 to 77°C, preferably in the range of from 50 to 65°C. The acid is preferably citric acid in a concentration of 0.2 to 40%w or acetic acid in a concentration of 0.2 to 40%w, and the lithium salt at a concentration of 0.005 to 5%w. The process is preferably run at a velocity of 2 bed volumes per hour. Any alkali metal compound commonly found in a polymer cement when an alkali metal compound is used as the catalyst or initiator can be removed from the polymer cement. These include alkali metal hydrides, alkali metal alkoxides and alkali metal hydroxides. It will be understood that a polymer cement is the polymer solution resulting from a polymerisation reaction and normally comprises components such as polymer formed, organic solvent(s), non-converted monomer and polymerisation initiator, hydrogenation catalyst residues, etc. Low viscosity functionalised polymer cements can be made by anionic polymerisation of conjugated diene hydrocarbons with lithium initiators is well known (see for instance U.S. Patents Nos. 4,039,503 and Re. 27,145. Polymerisation commences with a monolithium, dilithium, or polylithium initiator which builds a living polymer backbone at each lithium site. Typical living polymer structures containing polymerised conjugated diene hydrocarbons are: X B Li X A B Li X A B A Li Li B Y B Li Li A B Y B A Li wherein B represents polymerised units of one or more conjugated diene hydrocarbons such as butadiene or isoprene. A represents polymerised units of one or more vinyl aromatic compounds such as styrene. X is the residue of a monolithium initiator such as sec butyllithium, and Y is the residue of a dilithium initiator such as the diadduct of sec butyllithium and m-diisopropenylbenzene. Some structures, including those pertaining to polylithium initiators or random units of styrene and a conjugated diene, generally have limited practical utility although known in the art. The anionic polymerisation of the conjugated diene hydrocarbons is typically controlled with structure modifiers such as diethylether or glyme (1,2-diethoxyethane) to obtain the desired amount of 1,4-addition. As described in Re 27,145, the level of 1,2-addition of a butadiene polymer or copolymer can greatly affect elastomeric properties after hydrogenation. Dilithium initiation with the diadduct of sec butyllithium (s BuLi)and m diisopropenylbenzene also requires presence of a non reactive coordinating agent such as diethyl ether, glyme, or triethyl amine, otherwise monolithium initiation is achieved. Ether is typically present during anionic polymerisation as discussed above, and the amount of ether typically needed to obtain specific polymeric structures has been sufficient to provide dilithium initiation. Alternatively, anionic polymerisation of conjugated dienes may be performed using protected functional initiators (PFI) as for instance described in U.S. Patents 5,391,663 and 5,146,168. Anionic polymerisation is often terminated by addition of water to remove the lithium as lithium hydroxide (LiOH) or by addition of an alcohol (ROH) to remove the lithium as a lithium alkoxide (LiOR). For polymers having terminal functional groups, the living polymer chains are preferably terminated with hydroxyl, carboxyl, phenol, epoxy or amine groups by reaction with ethylene oxide, carbon dioxide, a protected hydroxystyrene monomer, ethylene oxide plus epichlorohydrin, or the amine compounds listed in U.S. Patent 4,791,174, respectively. The termination of living anionic polymers to form functional end groups is for instance described in U.S. Patents 4,417,029, 4,518,753 and 4,753,991. Of particular interest for the present invention are terminal hydroxyl, carboxyl, phenol, epoxy and amine groups. Such polymers with number average molecular weights between 1000 and 20,000, as measured by gel permeation chromatography, are low viscosity functionalised polymers. Hydrogenation of at least 90%, preferably at least 95%, of the unsaturation in low molecular weight butadiene polymers is achieved with nickel catalysts as for instance described in U.S. Patents Re. 27,145 and 4,970,254. The preferred nickel catalyst is a mixture of nickel 2-ethylhexanoate and triethylaluminium. It is preferable to extract the nickel catalyst after hydrogenation by stirring the polymer solution with the weak acid. The invention will now be illustrated by means of the following Examples. EXAMPLES Example 1 Two column experiments were conducted to compare the effectiveness of lithium removal from two acids having the same normality but different acid strengths. Phosphoric acid and citric acid were selected for this comparison. The lithium, nickel and aluminium levels in both acids were similar. So were the process conditions such as temperature, flow rate, column dimensions, specific resin used, etc. In the experiment with 20%w phosphoric acid (2.2N), lithium breakthrough occurred after 2 bed volumes (BV) of acid had been treated. In the experiment with 36%w citric acid(2.2N), lithium breakthrough occurred at 16 bed volumes. Example 2 Two column experiments were carried out with 20%w phosphoric acid containing 280 ppm Li and 100 ppm of Ni and Al each. In the first experiment a 20cc bed of AMBERLITE 200C was used. In the second experiment, the bed consisted of 10cc of AMBERLITE 200C followed by 10cc of AMBERLYST 35. All other parameters such as flow rate, temperature, bed L/D, etc. were the same in both experiments. The results obtained in these tests show that using the two resins in series increased the volume of acid treated before lithium breakthrough from 2 bed volumes to 6 bed volumes. Example 3 The higher lithium selectivity of AMBERLYST 35, AMBERLYST 15, and BAYER OC 1501 was identified in isotherm tests. Screening experiments to select the best resins consisted of shake tests to equilibrate the resin or adsorbent with a 2%w phosphoric acid solution containing 230 ppm lithium. The acid to adsorbent weight ratio in these tests was 100:1 and the temperature was 22°C. After equilibration, the residual lithium in the acid solution was determined by ion chromatography. From these results, the most effective materials for lithium removal were identified. Testing included chelating resins, strong acid resins, a weak acid resin, a strong base resin with and without addition of chelating agents, an inorganic oxide, inorganic ion exchangers, several zeolites, alumina, acid activated carbon, and activated carbon impregnated with a crown ether. The results identified AMBERLYST 35, BAYER OC 1501, and AMBERLYST 15 as the most effective materials for lithium removal. It is not clear why these resins are particularly effective. It appears that one of the key factors is that these are strong acid resins in the H+ form. But even among strong acid resins in the H+ form, there seems to be some differences in effectiveness. It is suspected these are due to differences in structure (e.g. pore size) and/or acid strength.

Claims: A process for removing an alkali metal compound from a polymer cement comprising: i) washing the polymer cement with an acid having a pKa greater than 3 to remove the alkali metal compound from the polymer cement; ii) removing the alkali metal compound from the acid; and iii) recycling the acid to wash more polymer cement. A process according to claim 1, wherein the alkali metal is lithium. A process according to claim 1 or 2, wherein the alkali metal compound is removed from the acid by ion exchange. A process according to any one of claims 1 to 3, wherein the weak acid is selected from the group consisting of citric acid and acetic acid. A process according to any one of claims 1 to 4, wherein the polymer cement is a low viscosity functionalised polymer cement. A process according to any one of claims 1 to 5, wherein in step ii) the weak acid is contacted with a first ion exchange resin functional to remove the nickel and aluminium compounds from the acid; and the acid so obtained is then contacted with a second ion exchange resin functional to remove the alkali metal compound from the acid.

Inventors: DIAZ ZAIDA, WILKEY JOHN DAVID, DIAZ, ZAIDA, WILKEY, JOHN DAVID
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1996
Main classification: C08F6
IPC codes: B01J39, C08F6, C04B41, C08C2