CALCIUM/OXYANION-CONTAINING PARTICLES FOR USE IN MEDICAL DIAGNOSTIC IMAGING

Abstract: The present invention provides new and structurally diverse particulates for use in magnetic resonance imaging and X-ray contrast imaging of body organs and tissues having the following general formula: CanMmXrYs, wherein M is a paramagnetic ion or stoichiometric mixture of metal ions having a valence of 2+ or 3+; X is a simple anion; Y is a tetrahedral oxyanion, or mixtures thereof; m is an integer greater than or equal to 1; n is an integer greater than or equal to 1; r and s are integers and are adjusted as needed to provide charge neutrality; and further comprising a polyalkoxy compound. Methods for using and making particles of the invention are also disclosed.

Description: TITLE RTT rτ ιFιff FOR USE τt MEPTCAII DIAGNOSTIC ΏJΆGIMS FIELD QF THE INVENTION The invention is in the field of imaging. In particular the invention relates to calcium/oxyanion-containing particles for use in medical diagnostic imaging, such as magnetic resonance imaging ("MRI") , ultrasound and X-ray. BACKGROUND QF THE INVENTION The use of contrast agents in diagnostic medicine is rapidly growing. In X-ray diagnostics, for example, increased contrast of internal organs, such as the kidneys, the urinary tract, the digestive tract, the vascular system of the heart (angiography) , and so forth, is obtained by administering a contrast agent which is substantially radiopaque. In conventional proton MRI diagnostics, increased contrast of internal organs and tissues may be obtained by administering compositions containing paramagnetic metal species which increase the relaxivity of surrounding protons. In ultrasound diagnostics, improved contrast is obtained by administering compositions having acoustic impedances different than that of blood and other tissues. Often it is desirable to image or treat a specific organ or tissue. Effective organ or tissue-specific diagnostic agents accumulate in the organ or tissue of interest. Copending patent application Serial No. 07/948,540, filed September 22, 1992, titled "Treated Apatite Particles for Medical Diagnostic Imaging, " which is incorporated herein by reference, discloses the preparation and use of apatite particles for medical diagnostic imaging. This patent application also describes methods for preparing apatite particles which provide organ or tissue-specific contrast. By carefully controlling the particle size and route of administration, organ specific imaging of the liver, spleen, gastrointestinal tract, or blood pool is obtained. A need continues to exist for new and structurally diverse compounds for use as imaging agents. There is a further need to develop highly stable complexes with good relaxivity characteristics that show improved specificity for particular organs and tissues. SUMMARY QF THE INVENTION The present invention provides new and structurally diverse particulates for use in magnetic resonance imaging and X-ray contrast imaging of body organs and tissues having the following general formula: Ca n M m X r Ys wherein M is a paramagnetic ion or stoichiometric mixture of metal ions having a valence of 2+ or 3+; X is a simple anion; Y is a tetrahedral oxyanion, or mixtures thereof; m is from 1-10; n is from 1-10; when M is a 2+ paramagnetic metal ion, then m + n = 10; when M is a 3+ paramagnetic metal ion, then m + l.5n = 10; r and s are adjusted as needed to provide charge neutrality; and further comprising a coating comprising polyethyleneglycols. DETAILED DESCRIPTION OF THE INVENTION Apatite particles are prepared by modifying conventional methods for preparing hydroxyapatite (sometimes referred to as "hydroxylapatite") . For example, stoichiometric hydroxyapatite, Ca 10 (OH) 2 (PO 4 ) 6 , can be prepared by adding an ammonium phosphate solution to a solution of calcium/ammonium hydroxide. Useful apatite particles may also be prepared by replacing calcium with paramagnetic metal ions. Other apatite derivatives are prepared by replacing the OH " with simple anions, including F", Br", I", or M[C0 3 2 "] . Various techniques for controlling the particle size for certain calcium phosphate-containing compounds (apatites) are disclosed in copending application Serial No. 07/948,540. For example, slower addition rates (introduction of the precipitating anion or cation) , faster stirring, higher reaction temperatures, and lower concentrations can result in smaller particles. In addition, sonication during precipitation, turbulent flow or impingement mixers, homogenization, and pH modification may be used to control particle size. Other means, such as computer controlled autoburets, peristaltic pumps, simultaneous mixing of reagents with or without syringes, may be used to control the mixing of precipitating ions to produce smaller particles. Due to the small size and nature of apatite particles, they tend to aggregate. Particle aggregation may be inhibited by coating the particles with coating agents. The agglomerated particles may also be disrupted by mechanical or chemical means and then coated with a coating agent having an affinity for the apatite. One preferred method of obtaining small, uniformly sized, manganese-doped apatite particles is to dropwise add a degassed solution of (NH 4 ) 2 HP0 4 and NH 4 OH into a rapidly stirring degassed solution of Ca(N0 3 ) 2 *»4H 2 0 and Mn(N0 3 ) 2 *»6H 2 0. The resulting apatite particles are then reacted with a solution of a coating agent containing a diphosphonate group. The smaller particles are separated from larger particles by repeated centrifuging and collection of the supernatant. The particles are then washed to remove base and saits by centrifuging at a higher rpm, discarding the supernatant, resuspending the solid pellet in water, and recentrifuging. In another preferred method the particles are prepared by rapidly mixing two solutions, one containing Mn(N0 3 ) 2 , Ca(N0 3 ) 2 and H 3 P0 4 and another containing enough NHapOH to generate a final pH between about 4 and about 10. The resulting suspension is coated with a polyethyleneglycol derivative chemically coupled to a diphosphonate. The present invention provides calcium/oxyanion- containing particles, including apatites and apatite precursors, especially hydroxyapatite. Calcium/oxyanion-containing particles, include calcium phosphate minerals, apatites, and apatite precursors of the general formula Ca n M n X r Y,, where M is a paramagnetic metal ion, radiopaque metal ion, radioactive metal ion, or stoichiometric mixture of metal ions, X is a simple anion, Y is an oxyanion including tetrahedral oxyanions, carbonate, or mixtures thereof, m is from 0 to 10, n is from 1 to 10, s is ≥ 1, and r is adjusted as needed to provide charge neutrality. Apatite precursors include compounds within the scope of the above general formula having one or more amorphous phases which, when sintered, may become crystalline apatites. Paramagnetic metal ions which can be used in the calcium/oxyanion-containingparticles of the present invention include: chromium(III) , manganese(II) , iron(II), iron(III), praseodymium(III) , neodymium(III) , samarium(III) , ytterbium (III) , gadolinium ( III) , terbium (III) , dysprosium(III) , holmium(III) , erbium(III) , or mixtures of these with each other or with alkali or alkaline earth metals. Certain radiopaque heavy metals, such as bismuth, tungsten, tantalum, hafnium, lanthanum and the lanthanides, barium, molybdenum, niobium, zirconium, and strontium may also be incorporated into particles to provide X-ray contrast. The radiopaque metals are incorporated into the calcium/oxyanion- containing particles in the same manner as paramagnetic metal ions. Typical simple anions which can be used in the calci¬ um/oxyanion-containing particles of the present invention include: OH " , F", Br" I " , *$[C0 3 2 "], or mixtures thereof. The tetrahedral oxyanions used in the present invention may optionally include radiopaque metals or radioactive metals. Suitable tetrahedral oxyanions are nonoxidizing and stable to hydrolysis. Examples of suitable tetrahedral oxyanions for use in the present invention include: P0 4 3 ", As0 4 3 ", W0 4 2 ", Mo0 4 2 " , V0 4 3* , Si0 4 4 ", and Ge0 4 4 ". Phosphate is a currently preferred tetrahedral oxyanion. By controlling particle size, organ specific imaging or therapy of the liver or gastrointestinal tract is obtained. When apatite particles having a size in range from about 5 nm to about 5 μm are injected into the vascular system, the particles collect in the liver or spleen (the RES system) because a normal function of these organs is to purify the blood of foreign particles. Once the particles have collected in the liver or spleen, these organs may be imaged by the desired medical diagnostic imaging technique. Depending on the diagnostic imaging technique, calci- um/oxyanion containing particles are treated to be paramag¬ netic, radiopaque, or echogenic. For example, paramagnetic metal species may be incorporated into the particles to improve magnetic resonance contrast, and radiopaque species may be incorporated to provide X-ray contrast. Particle density, and corresponding echogenic characteristics, can be controlled to impart low or high acoustic impedance relative to blood. The calcium/oxyanion-containing particles may also be fluorinated to form stable, nontoxic compositions useful for 19 F imaging. The presence of a paramagnetic metal species in these particles may reduce 19 F and proton relaxivity, thereby enhancing MRI, MRS, or MRSI. Antioxidants, such as gentisic acid and ascorbic acid, added during or after apatite particle synthesis may be used to prevent metal ion oxidation. Reducing agents, such as NaBH 4 , have been found to reduce metal ions that are unintentionally oxidized during apatite particle synthesis. Paramagnetic particles may also be prepared by adsorbing paramagnetic metal ions onto the particle. For example, manganese can be adsorbed to hydroxyapatite particles by taking a slurry of hydroxyapatite and adding Mn(N0 3 ) 2 with stirring. Applying energy, such as ultrasonic power or heat, to the resulting mixture may also facilitate the reaction. The resulting mixture can be separated by either centrifugation and decantation or by filtration. Any excess manganese may be removed by washing with large amounts of water. The manganese adsorbed particles can then be stabilized against oxidation and particle agglomeration with a suitable coating agent. The same procedure may be used with other paramagnetic cations. The amount of manganese adsorbed onto the particle surface, as a percentage of the total calcium in the particle, is in the range from about 0.1% to about 50%. Such particles exhibit very high relaxivities and rapid liver enhancement in magnetic resonance imaging studies. Stabilized calcium/oxyanion-containing particles, including apatites and apatite precursors, are desirable for in vivo use as medical diagnostic imaging agents. ' Such particles tend to aggregate. Although the reasons calci¬ um/oxyanion-containing particles aggregate is not fully understood, it has been found that several different coating agents are able to inhibit particle aggregation. For example, these particles may be stabilized by treatment with coating agents such as di- and polyphosphonate-containing compounds or their salts, such as 1-hydroxyethane-1,1-diphosphonate (HEDP) , pyrophosphate, aminophosphonates; or any of these moieties attached to a long polymeric chain carboxylates and polycarboxylate-containing compounds such as oxalates and citrates; alcohols and polyalcohol-containing compounds; compounds containing one or more phosphate, sulfate, or sulfonate moiety; and biomolecules such as peptides, proteins, antibodies, and lipids all of which may or may not have been attached to a long polymeric chain. Such coating agents can stabilize the small particles by reducing further particle growth and promoting particle suspension. Coatings for use with this invention include polymeric alkoxy derivatives that have been coupled to some group capable of making a tight binding to the surface of the particle. coatings derived from poly(ethylene glycol), poly(propylene glycol) and co-polymers of propylene and ethylene glycol are examples of the polymeric alkoxy derivatives. The number of ethylenegylcyol and/or propyleneglycol units is between 2 and 1000. The polymeric alkoxy derivatives may have one end capped with an alkyl group. Coupling can be done through any chemically and biologically compatible coupling group such as amide, ether, or ester linkages. The length of chain between the polymer and binding group is 1-5 atoms. This chain can be made up of C,N,0,S or P atoms. Where appropriate, the atoms may contain branching groups such as OH, C0 2 H, PH 3 H 2 , S0 3 H, alkyl or substituted alkyl groups, F, Cl, Br, I, NR2 (R=alkyl 3 , OH or H) . Examples of groups that may be coupled to the polymeric alkoxy derivative include groups containing free di- or polyphosphonates, polycarboxylates, di- or polyphosphates or mixtures of phosphonates, carboxylates and phosphates. Other groups such as alcohols, thiols or ethers may also be included. The general form of the coating agent will be R 2 I R 1 -C-X-R 4 I R 3 with one to three R groups being a polymeric alkoxy group and one to three R groups being the group containing the particle binding moiety, the remainder of the R groups are chains of 1- 5 atoms made up of C,N,0,S or P atoms and, where appropriate, the atoms may contain branching groups such OH, C0 2 H, P0 3 H 2 , S0 3 H, alkyl or substituted alkyl groups, F, Cl, Br, I, NR2 (R-=alkyl, OH or H) and X is a coupling moiety. It is believed coated agents are not recognized by opsonizing agents in the body that would, without the PEGs, direct agents very rapidly towards the liver. The significantly increased blood residence time is believed due to the PEGs making these particles look more like "natural" materials thereby going undetected by the normal mechanisms that clear particles from the blood. When used in magnetic resonance imaging, particle relaxivity is enhanced by allowing more water accessible to the particle surface. By limiting particle size and increasing the available surface area, relaxivity may be improved. In addition to the coating agents identified above, conventional particle coating techniques may also be used in the manufacturing processes of the present invention. Typical coating techniques are identified in International Publication Numbers WO 85/02772, WO 91/02811, and European Publication Number EP 0343934, which are incorporated by reference. For instance, agglomerated particles may be disrupted by mechanical or chemical means and then coated with apatite coating agents is their ability to modify the particle surface charge, or zeta potential. One such mechanical disrupter is referred to as a microfluidizer. It will be appreciated that the calcium phosphate- containing particles within the scope of the present invention may be coated before, during, or after passage through a microfluidizer. When coated during passage through the microfluidizer, one fluid stream is the coating agent, while the other fluid stream is the particulate stream. The currently preferred mechanical means for reducing particle size is icrofluidization, but other means such as heating, sonication, other forms of particle energization, such as irradiation, and chemical means, such as pH modifi¬ cation or combinations of these types of treatment, such as pH modification combined with sonication may be used. The calcium/oxyanion-containing particles of this invention may be formulated into diagnostic compositions for parenteral administration. For example, parenteral formulations advantageously contain a sterile aqueous solution or suspension of treated apatite or apatite precursor particles according to this invention. Various techniqu * es for preparing suitable pharmaceutical solutions and suspensions are known in the art. Such solutions also may contain pharmaceutically acceptable antioxidants, optionally, electrolytes such as sodium chloride or agents to increase the toxicity of the solution. Parenteral compositions may be injected directly or mixed with a large volume parenteral composition for systemic administration. The diagnostic compositions of this invention are used in a conventional manner in medical diagnostic imaging procedures such as magnetic resonance, X-ray, and ultrasound imaging. The diagnostic compositions are administered in a sufficient amount to provide adequate visualization, to a warm-blooded animal either systemically or locally to an organ or tissues to be imaged, then the animal is subjected to the medical diagnostic procedure. Such.doses may vary widely, depending upon the diagnostic technique employed as well as the organ to be imaged. The compositions of the invention can be formulated into therapeutic or diagnostic compositions for enteral or parenteral administration. These compositions contain an effective amount of the paramagnetic ion-containing particle along with conventional pharmaceutical carriers and excipients appropriate for the type of administration contemplated. For example, parenteral formulations advantageously contain a sterile aqueous solution or suspension of from about 0.05 to about 1.0M of a paramagnetic ion-containing particle according to this invention. Parenteral compositions may be injected directly or mixed with a large volume parenteral composition for systemic administration. Preferred parenteral formulations have a concentration of paramagnetic ion complex of about 0.1M to about 0.5M. Such solutions also may contain pharmaceutically acceptable antioxidants, buffers and, optionally, electrolytes such as sodium chloride or agents to increase the toxicity of the solution. Formulations for enteral administration may vary widely, as is well-known in the art. In general, such formulations are liquids which include an effective amount of the paramagnetic ion particle in suspension. Such enteral compositions may optionally include buffers, surfactants, thixotropic agents, antioxidants and the like. Compositions for oral administration may also contain flavoring agents and other ingredients for enhancing their organoleptic qualities. The diagnostic compositions are administered in doses effective to achieve the desired enhancement of the image. Such doses may vary widely, depending upon the particular paramagnetic ion complex employed, the organs or tissues which are the subject of the imaging procedure, the imaging procedure, the imaging equipment being used, and the like. In general, parenteral dosages will range from about 0.001 to about 1.0 mMol of paramagnetic ion complex per kg of patient body weight. Preferred parenteral dosages range from about 0.01 to about 0.5 mMol of paramagnetic ion complex per kg of patient body weight. Enteral dosages generally range from about 0.5 to about 100 mMol, preferably from about 1.0 to about 10 mMol, more preferably from about 1.0 to about 10.0 mMol of paramagnetic ion complex per kg of patient body weight. The diagnostic compositions of the invention are used in the conventional manner. The compositions may be administered to a patient, typically a warm-blooded animal, either systemically or locally to the organ or tissue to be imaged, and the patient then subjected to the imaging procedure. Protocols for imaging and instrument procedures are found in texts such as Stark, D.D. ,* Bradley, w.G. Magnetic Resonance Imaging,- Mosby Year Book: St. Louis, MO, 1992. X-ray contrast Imaging Procedures are found in Albert A. Moss, M.D., Gordon Gamsu, M.D., and Harry K. Genant, M.D., Computed Tomography of the. Body. (W.B. Saunders Company, Philadelphia, Pennsylvania 1992) and M. Sovak, Editor, Radiocontrast Agents. (Springer-Verlag, Berlin 1984) . The following examples illustrate the specific embodiments of the invention described in this document. As would be apparent to skilled artisans, various changes and modifications are possible and are contemplated within the scope of the invention described. EXAMPLES Example 1 Preparationof the Bis(te-xa-n-butylaπmaniurn) salt of 1-amino- 3-hrydrcoςypιrcpan^ acid. l-Amino-3-hydroxypropane-l,1-diphosphonicacid (76.3g,324 mmol) was mixed with 425.5 mL of an aqueous 40% tetra-n-butyl ammonium hydroxide solution (649 mmol) , and the mixture stirred at 60°C until a clear solution was obtained. The water was then removed by vacuum distillation, and the resulting gummy residue dried in vacuo at 40°C for 18 hr. The residue was taken up in methylene chloride (750 mL) , the cloudy suspension dried over anhydrous sodium sulfate, filtered, and the solvent removed in vacuo to give 226.9g(97% yield) of the bis(tetra-n-butylammonium) salt of l-amino-3-hydroxypropane- 1,1-diphosphonic acid. Example 2 Preparation of [methyl(polyoxyetbylene)]αxyacetyl chloride A magnetically-stirred 2-L round-bottomed flask was charged with oxalyl chloride (700 mL, 8.0 mol) . The vessel was cooled in an ice-water bath to below 10°C. Methyl (polyoxyethylene)]oxyacetic acid (avg. mol. wt. ca. 2000) (277.7g, ca. 135 mmol) was added in portions over a 30 min. period, followed by dropwise addition of N,N- dimethylformamide over a 60 min. period, maintaining the temperature below 10°C. The ice-water bath was removed, and the vessel was slowly heated. At ca. 32°C, a vigorous reaction ensued, and the heat source was removed, when the reaction subsides, heating was continued, and the solution was heated at gentle reflux for 15 hr. After cooling to room temperature (20-25°C) , the oxalyl chloride was removed in vacuo. Dry methylene chloride (200 mL) was added, then removed in vacuo. the methylene chloride treatment was repeated, the residue was taken up again in dry methylene chloride (500 mL) , concentrated in vacuo, and heated at 40°C under vacuum for 16 hr. to obtain 299g of crude [methyl(polyoxyethylene)]oxyacetyl chloride as a wax. Example 3 Preparation of l-hyό-roxy-3-{I^IΛyl(polyoxyethylene)] ooyacetamido}-prqpane*-l y 1-diphosphonic acid The bis(tetra-n-butylammonium) salt of l-amino-3- hydroxypropane-1,1-diphosphonic acid (138g,192 mmol) was mixed with toluene (700 mL) and the mixture dried by azeotropic distillation with a Dean-stark trap. After cooling to room temperature, the toluene was removed in vacuo, and the " residue dissolved in anhydrous acetonitrile (250 mL) . To this was a d d e d a s o l u t i o n o f t h e c r u d e [methyl(polyoxyethylene)]oxyacetyl chloride (299g) in anhydrous acetonitrile (250 mL) , followed by dry triethylamine (138 mL, 100 g, 990mmol) . The solution was heated and stirred at 70°C for 4 days, after which time the solvent was removed in Vacuo. The residue was dissolved in water (600 mL) and eluted through 500 mL of Amberlite IR-120 resin (H*form) . The brown eluent was collected, the water removed in vacuo, and the waxy residue redissolved in water (800 mL) . The product solution was loaded onto a column containing 3.5L of Amberlite IRA-68 resin, and eluted with 0.25 M acetic acid, followed by 10 L of 0.5 M acetic acid, collecting 2-L fractions. Portions of each fraction were concentrated and analyzed by X H and 31 P- NMR. Fractions containing product ( 31 P resonance at ca 19 ppm downfield from 85% H 3 P0 4 ) were combined, concentrated in vacuo, and re-chromatographed on 1 L of fresh IRA-68 resin, eluting with a sodium acetate gradient (0-25 mM) . The purest fractions were combined, eluted through Amberlite IR-120 resin (H*form) to remove sodium ions, the solvent removed in vacuo, and the product dried in vacuo to give 18 g of l-hydroxy-3- { [methyl (polyoxyethylene) ] oxyacetamido} -propane-1, 1- diphosphonic acid as a waxy solid. Example 4 Synthesis of 15% 13nHA//20%dαphosphαnate for blood pool METALS AND PHOSPHATE: A metal ion solution was prepared by mixing 0.26g of Mn(N03)2.4.5H20, or 1 mmole; 1.33g of Ca(N0 3 ) 2 .4H 2 0, or 5.66 mmole; 0.46g of NH 4 H 2 P0 4 , or 4mmole; and 0.2ml of 1M H 3 P0 4 3 together with water to a final volume of 20ml. This solution was deaerated prior to use. BASE: Aqueous ammonia (11 ml. 1M) was diluted to 20ml for use. STABILIZING AGENT: 4.0g of PEG(2000-APD) was dissolved in 20ml of water and the pH was adjusted to 9 with 1M aqueous ammonia. PARTICLES: The metal and base were mixed rapidly and stirred for 30 min. The pH at this state is -8. The stabilizing agent was then added and stirred for an extra 1 hr. The slurry was microfluidized at 15,000 psi to break up aggregates and the product was purified of small ions and unbound stabilizing agent by tangential flow filtration until the conductivity of the effluent dropped to -200 uS (this typically required -12 volume-equivalents of effluent) . PRODUCT: Approximately 70ml of product is obtained with [Mn] of -lOmM, diameter <50nm, Rl between 16-20mM "1 sec" 1 , and R2 between 20-24 mM" 1 sec" 1 . Example 5 Preparation of [methyl(polyoxyethylene)]σxyacetyl chloride A magnetically-stirred 1-L round-bottomed flask fitted with a Dean-Stark trap and a reflux condenser was charged with methyl (polyoxyethylene) ]oxyacetic acid (avg. mol. wt. ca. 2000) (135 g, ca. 65 mmol) and toluene (500 mL) . The resulting solution was dried azeotropically by heating at reflux and collecting the distillate in a Dean-Stark trap until the distillate was clear and water no longer separated out (ca. 2 hours) . The toluene was removed in vacuo, and oxalyl chloride was added. The reaction vessel was fitted with a reflux condenser connected to a gas bubbler, and the resulting solution was heated at reflux until gas evolution ceased, allowed to cool to room temp. (20-25°C) , and the excess oxalyl chloride removed in vacuo to give the acid chloride as a waxy solid. Example f, Preparation of l-hydroxy-3-{bnethyl(polyoxyethylene)] oxyacetjrrnido}-propaTift-l,1-diphosphonic acid [Methyl(polyoxyethylene)]oxyacetyl chloride (prepared above) was dissolved in toluene (300 mL) and added dropwise, over 2 hours, to a vigorously stirred solution of 3-amino-l- hydroxypropane-l,l-diphosphonic acid (15 g, 64 mmol) in IN aqueous sodium hydroxide (330 mL, 330mmol) . The reaction mixture was stirred at room temp, for 18 hours, the toluene removed in vacuo, and the resulting aqueous solution eluted through 330 mL of Amberlite IR-120 cation exchange resin (H+ form) , followed by 500 mL of water. The total eluent was evaporated to dryness in vacuo, then redissolved in water (1 L) and purified by preparative HPLC on 450 g of SynChrom Synchroprep AX-300 resin in a stainless steel column. After applying the product mixture to the column, the column was eluted (at a flow rate of 50 mL/min) with water (2L) , followed by a step gradient of aqueous sodium acetate (20 mM per step, 500 mL between steps) , collecting 500 mL fractions. The fractions containing pure product were combined, concentrated, eluted through Amberlite IR-120 cation exchange resin (H+ form) to remove sodium, and evaporated to dryness. The resultant waxy solid was redissolved in water, titrated with IN aqueous NaOH to pH 7.1, evaporated to a gummy solid, redissolved in absolute ethanol, and evaporated to a solid to give 40 g of l-hydroxy-3-{ [methyl(polyoxyethylene)] oxyacetamido}-propane-l,1-diphosphonic acid as its trisodium salt. Although the invention has been described with respect to specific modifications, the details thereof are not to be construed as limitations, for it will be apparent that various equivalents, changes and modifications may be resorted to without departing from the spirit and scope thereof, and it is understood that such equivalent embodiments are to be included therein.

Claims: CLAIMS What is claimed is: 1. A diagnostic agent comprising a compound of the general formula: Ca n M ra X r Y s wherein M is a paramagnetic ion or stoichiometric mixture of metal ions having a valence of 2+ or 3+,* X is a simple anion; Y is a tetrahedral oxyanion, or mixtures thereof; is ≥l; n is ≥l ; r and s are integers and adjusted as needed to provide charge neutrality; and further comprising a coating comprising a polymeric alkoxy compound. 2. The diagnostic agent of claim 1 wherein the polymeric alkoxy compound is of the general formula: R-Z-R R wherein R is present or not, and is the same or different, and is a polymeric alkoxy group, particle binding group, H, OH, a biomolecule, C0 2 H, P0 3 H 2 , S0 3 H, alkyl of about 1 to about 5 carbons, substituted alkyl, F, Cl, Br, I, or N(R*) 2 wherein R 1 is alkyl, polymeric alkoxy, biomolecule, substituted alkyl, OH or H; Z is present or not, and is a chain made up of about 10 atoms of C, N, 0, S, P, or combinations thereof; provided at least one R is a polymeric alkoxy group and at least one R is a particle binding group. 3. The diagnostic agent of claim 2 wherein the polymeric alkoxy compound is comprised of ethylene glycol and/or propylene glycol units with the total number of units being between about 2 and about 1000. 4. The diagnostic agent of claim 3 wherein the polymeric alkoxy derivative is poly(ethylene glycol) . 5. The diagnostic agent of claim 4 wherein the poly(ethylene glycol) comprises between about 2 and about 200 units of ethylene glycol. 6. The diagnostic agent of claim 4, in which the paramagnetic metal is chromium (III), manganese (II), iron (II), iron (III), praseodymium (III), neodymium (III), samarium (III), ytterbium (III), gadolinium (III), terbium (III), dysprosium (III), holmium (III), erbium (III), or mixtures thereof, with or without alkali or alkaline earth metals. 7. The diagnostic agent of claim 4 wherein X is OH " , F " , Br " I " , 1/2[C0 3 2" ], or mixtures thereof. 8. The diagnostic agent of claim 4 wherein Y is phosphate, arsenate, tungstate, molybdate, vanadate, silicate, germanate, or mixtures thereof. 9. The diagnostic agent of claim 6 wherein Y is phosphate, X is OH" or r is zero, and M is Mn. 10. The diagnostic agent of claim 9 wherein the percent of Mn to total metal is between about 5 and about 25 percent. 11. The diagnostic agent of claim 11 wherein the polymeric alkoxy compound has an average molecular weight of about 1500 to about 5500. 12. The diagnostic agent of claim 11 wherein the coating agent is l-hydroxy-3-{ [methyl(polyoxyethylene) ] oxyacetamido}-propane-1,1-diphosphonic acid of average molecule weight of about 2100. 13. The diagnostic agent of claim 12 wherein the average particle size is greater than or equal to about 1 nm but less than about 5 μm. 14. A diagnostic agent comprising a compound of the general formula: Ca n M ar X r Y s wherein M is a radiopaque heavy metal; X is a simple anion; Y is a tetrahedral oxyanion, or mixtures thereof; m is ≥l ; n is ≥l ; r and s integers and adjusted as needed to provide charge neutrality; and further comprising a coating comprising a polymeric alkoxy compound. 15. The diagnostic agent of claim 14 wherein the polymeric alkoxy compound is of the general formula: R R-Z-R R wherein R is present or not, and is the same or different, and is a polymeric alkoxy group, particle binding group, H, OH, a biomolecule, C0 2 H, P0 3 H 2 , S0 3 H, alkyl of about 1 to about 5 carbons, substituted alkyl, F, Cl, Br, I, or NIR'lj wherein R 1 is alkyl, polymeric alkoxy, biomolecule, substituted alkyl, OH or H; Z is present or not, and is a chain made up of about 10 atoms of C, N, 0, S, P, or- combinations thereof; provided at least one R is a polymeric alkoxy group and at least one R is a particle binding group. 16. The diagnostic agent of claim 15 wherein the polymeric alkoxy compound is comprised of ethylene glycol and/or propylene glycol units with the total number of units being between about 2 and about 1000. 17. The diagnostic agent of claim 16 wherein the polymeric alkoxy derivative is poly(ethylene glycol) . 18. The diagnostic agent of claim 17 wherein the poly(ethylene glycol) comprises between about 2 and about 200 units of ethylene glycol. 19. The diagnostic agent of claim 17, in which the radiopaque heavy metal is bismuth, tungsten, tantalum, hafnium, lanthanum, barium, molybdenum, niobium, zirconium, or strontium. 20. The diagnostic agent of claim 17 wherein X is OH", F", Br " , I", 1/2[C0 3 2 "], or mixtures thereof. 21. The diagnostic agent of claim 17 wherein Y is phosphate, arsenate, tungstate, molybdate, vanadate, silicate, germanate, or mixtures thereof. 22. The diagnostic agent of claim 21 wherein Y is phosphate, X is OH " or r is zero, and M is bismuth. 23. The diagnostic agent of claim 22 wherein the percent of Mn to total metal is between about 5 and about 25 percent. 24. The diagnostic agent of claim 23 wherein the polymeric alkoxy compound has an average molecular weight of about 1500 to about 5500. 25. The diagnostic agent of claim 24 wherein the polymeric alkoxy compound is l-hydroxy-3-{ [methyl(polyoxyethylene) ] oxyacetamido}-propane-1,1-diphosphonic acid of average molecule weight of about 2100. 26. The diagnostic agent of claim 25 wherein the average particle size is greater than or equal to about 1 nm but less than about 5 um. 27. A method of imaging comprising administering to a patient a compound of the general formula: Ca n M B X r Y, wherein M is a paramagnetic ion or stoichiometric mixture of metal ions having a valence of 2+ or 3+; X is a simple anion; Y is a tetrahedral oxyanion, or mixtures thereof; m is ≥l; n is ≥l; r and s are integers and adjusted as needed to provide charge neutrality; and further comprising a coating comprising a polymeric alkoxy compound. 28. The method of claim 27 wherein the polymeric alkoxy compound is of the general formula: R I R-Z-R I R wherein R is present or not, and is the same or different, and is a polymeric alkoxy group, particle binding group, H, OH, a biomolecule, C0 2 H, P0 3 H 2 , S0 3 H, alkyl of about 1 to about 5 carbons, substituted alkyl, F, Cl, Br, I, or N(R 1 ) 2 wherein R 1 is alkyl, polymeric alkoxy, biomolecule, substituted alkyl, OH or H; Z is present or not, and is a chain made up of about 10 atoms of C, N, 0, S, P, or combinations thereof; provided at least one R is a polymeric alkoxy group and at least one R is a particle binding group. 29. The method of claim 28 wherein the polymeric alkoxy compound is comprised of ethylene glycol and/or propylene glycol units with the total number of units being between about 2 and about 1000. 30. The method of claim 29 wherein the polymeric alkoxy derivative is poly(ethylene glycol) . 31. The method of claim 30 wherein the poly(ethylene glycol) comprises between about 2 and about 200 units of ethylene glycol. 32. The method of claim 30, in which the paramagnetic metal is chromium (III), manganese )II), iron (II), iron (III), praseodymium (III), neodvmiu (III), samarium (III), ytterbium (III) , gadolinium (III) , terbium (III) , dysprosium (III), holmium (III), erbium (III), or mixtures thereof, with or without alkali or alkaline earth metals. 33. The method of claim 30 wherein X is OH " , F " , Br " , I " , 1/2 [C0 3 2" ], or mixtures thereof. 34. The method of claim 30 wherein Y is phosphate, arsenate, tungstate, molybdate, vanadate, silicate, germanate, or mixtures thereof. 35. The method of claim 32 wherein Y is phosphate, X is OH " or r is zero, and M is Mn. 36. The method of claim 35 wherein the percent of Mn to total metal is between about 5 and about 25 percent. 37. The method of claim 37 wherein the polymeric alkoxy compound has an average molecular weight of about 2000 to about 5000. 38. The diagnostic agent of claim 11 where the coating agent is l-hydroxy-3-{ [methyl(polyoxyethylene) ] xyacetamido}-propane-1,1-diphosphonic acid of average molecule weight of about 2100. 39. The method of claim 38 wherein the average particle size is greater than or equal to about 1 nm but less than about 5 urn. 40. A method of imaging comprising administering to a patient a compound of the general formula: CaJΛJZ-Y. wherein M is a radiopaque heavy metal; X is a simple anion; Y is a tetrahedral oxyanion, or mixtures thereof; m is ≥l; n is ≥l; r and s integers and adjusted as needed to provide charge neutrality; and further comprising a coating comprising a polymeric alkoxy compound. 41. The method of claim 40 wherein the polymeric alkoxy compound is of the general formula: R-Z-R R wherein R is present or not, and is the same or different, and is a polymeric alkoxy group, particle binding group, H, OH, a biomolecule, C0 2 H, P0 3 H 2 , S0 3 H, alkyl of about 1 to about 5 carbons, substituted alkyl, F, Cl, Br, I, or N(R l ) wherein R 1 is alkyl, polymeric alkoxy, biomolecule, substituted alkyl, OH or H; Z is present or not, and is a chain made up of about 10 atoms of C, N, 0, S, P, or combinations thereof; provided at least one R is a polymeric alkoxy group and at least one R is a particle binding group. 42. The method of claim 41 wherein the polymeric alkoxy compound is comprised of ethylene glycol and/or propylene glycol units with the total number of units being between about 2 and about 1000. 43. The method of claim 42 wherein the polymeric alkoxy derivative is poly(ethylene glycol) . 44. The method of claim 43 wherein the poly(ethylene glycol) comprises between about 2 and about 200 units of ethylene glycol. 45. The method of claim 42, in which the radiopaque heavy metal is bismuth, tungsten, tantalum, hafnium, lanthanum, barium, molybdenum, niobium, zirconium, or strontium. 46. The method of claim 42 wherein X is OH " , F " , Br", I", 1/2[C0 3 2" ], or mixtures thereof. 47. The method of claim 42 wherein Y is phosphate, arsenate, tungstate, molybdate, vanadate, silicate, germanate, or mixtures thereof. 48. The method of claim 47 wherein Y is phosphate, X is OH" or r is zero, and M is bismuth. 49. The method of claim 48 wherein the percent of bismuth to total metal is between about 5 and about 25 percent. 50. The method of claim 49 wherein the polymeric alkoxy compound has an average molecular weight of about 2000 to about 5000. 51. The method of claim 50 wherein the polymeric alkoxy compound is l-hydroxy-3-{ [methyl(polyoxyethylene) ] oxyacetamido}-propane-1,1-diphosphonic acid of average molecular weight of about 2100. 52. The method of claim 51 wherein the average particle size is greater than or equal to about 1 nm but less than about 5 urn. 53. A method for making compounds of the general formula: Ca π M π r r Ys wherein M is a paramagnetic ion or stoichiometric mixture of metal ions having a valence of 2+ or 3+; X is a simple anion; Y is a tetrahedral oxyanion, or mixtures thereof; m is ≥l; n is ≥l; r and s are integers and adjusted as needed to provide charge neutrality; and further comprising a coating comprising a polymeric alkoxy compound of the general formula: R-Z-R wherein R is present or not, and is the same or different, and is a polymeric alkoxy group, particle binding group, H, OH, a biomolecule, C0 2 H, P0 3 H 2 , S0 3 H, alkyl of about 1 to about 5 carbons, substituted alkyl, F, Cl, Br, I, or N(R X ) 2 wherein R 1 is alkyl, polymeric alkoxy, biomolecule, substituted alkyl, OH or H; Z is present or not, and is a chain made up of about 10 atoms of C, N, 0, S, P, or combinations thereof; provided at least one R is a polymeric alkoxy group and at least one R is a particle binding group. 54. The method of claim 53 wherein base is added separately. 55. The method of claim 53 wherein base and coating are added separately. 56. The method of claim 53 wherein coating is added last. 57. The method of claim 53 further comprising the addition of simple anions and/or alkaline earth metals.

Inventors: ADZAMLI KOFI, KLIBANOV ALEXANDER L, NEMA SANDEEP, NOSCO DENNIS, ADZAMLI, KOFI, KLIBANOV, ALEXANDER, L., NEMA, SANDEEP, NOSCO, DENNIS
Applicants: MALLINCKRODT MEDICAL INC, MALLINCKRODT MEDICAL, INC.
Application year: 1996
Main classification: A61B5
IPC codes: A61B5, A61B8, A61K49, G01R33