Blends of poly(ethylene terephthalate) and monovinylarene/conjugated diene block copolymers

Abstract: A composition comprising (A) a monovinylarene/conjugated diene block copolymer, (B) a modified poly(ethylene terephthalate), and (C) a poly(ethylene terephthalate). A process for preparing the composition and articles manufactured from the composition are also provided.

Description: This invention relates to blends comprising monovinylarene/conjugated diene block copolymer, modified poly(ethylene terephthalate), and poly(ethylene terephthalate). BACKGROUND Monovinylarene/conjugated diene copolymers are known and useful for a variety of purposes. Polymers that can be formed into colorless, transparent articles having good physical properties are of particular interest. Such articles are useful in packaging such as blister packaging, and the manufacture of toys, window pieces, beverage containers and items of the like. It would therefore be desirable to develop useful polymer blends having a combination of good clarity, stiffness, and toughness. SUMMARY OF THE INVENTION It is an object of this invention to provide a polymer blend having a combination of good clarity, stiffness and toughness. It is another object of this invention to provide a process for preparing a polymer having good clarity and good mechanical properties. In accordance with this invention a polymer blend composition is provided, comprising (a) a monovinylarene/conjugated diene block copolymer present in an amount in the range of from 10 to 90 weight percent based on the total weight of the polymer blend, wherein monovinylarene is present in said monovinylarene/conjugated diene block copolymer in an amount in the range of from 55 to 95 weight percent, preferably from 60 to 95 weight percent, most preferably from 70 to 90 weight percent, each based on the weight of the monovinylarene/conjugated diene block copolymer, and wherein conjugated diene is present in said monovinylarene/conjugated diene block copolymer in an amount in the range of from 45 to 5 weight percent, preferably from 40 to 5 weight percent, most preferably from 30 to 10 weight percent, each based on the weight of the monovinylarene/conjugated diene block copolymer; (b) a modified poly(ethylene terephthalate), present in an amount in the range of from 5 to 85 weight percent based on the total weight of the polymer blend, wherein the modified poly(ethylene terephthalate) is modified by the inclusion of comonomers selected from diols, diacids, hydroxy acids and mixtures thereof; and (c) a poly(ethylene terephthalate) present in an amount in the range of from 5 to 85 weight percent based on the total weight of the polymer blend. In accordance with other aspects of this invention, a process for preparing the composition, comprising melt blending the components, and articles prepared therefrom are also provided. DETAILED DESCRIPTION OF THE INVENTION Any means known in the art is suitable to produce the polymers employed in the present invention. Many suitable polymers are commercially available. The component (A) monovinylarene/conjugated diene block copolymers useful in this invention are block copolymers having a melt flow greater than 0.1 g/10 min., preferably in the range of from 0.1 g/10 min. to 100 g/10 min. measured according to ASTM D-1238, Condition G. Preferably the monovinylarene/conjugated diene block copolymers will have a Notched Izod Impact Strength of greater than 16.01 N·m/m (0.3 ft lbs/in.) measured according to ASTM D-256. The monovinylarene/conjugated diene block copolymers are generally prepared by a solution process involving sequential polymerization of a monovinylarene monomer and a conjugated diene monomer. Optionally, a monovinylarene monomer/conjugated diene monomer mixture can be polymerized to form a monovinylarene/conjugated diene block. In some circumstances the polymer chains can be coupled to form multimodal block copolymers having a broad molecular weight distribution. The basic starting materials and polymerization conditions for preparing monovinylarene/conjugated diene block copolymer are disclosed in U.S. Pat. Nos. 4,091,053; 4,584,346; 4,704,434; 4,704,435; and 5,227,419. In a typical preparation method of these publications, a conjugated diene monomer and a monovinylarene monomer are copolymerized sequentially in the presence of an initiator. Optionally, a monovinylarene monomer/conjugated diene monomer mixture can be polymerized to form a monovinylarene/conjugated diene block. The initiators can be any of the organomonoalkali metal compounds known for such purposes. Preferably the initiator is provided in at least three charges. Small amounts of polar organic compounds, such as ethers, thioethers, and tertiary amines can be employed in the hydrocarbon diluent to improve the effectiveness of the initiator and to randomize at least part of the monovinylarene monomer in a mixed monomer charge. The polymerization process is carried out in a hydrocarbon diluent at any suitable temperature in the range of from -100°C to 150°C, at pressures sufficient to maintain the reaction mixture substantially in the liquid phase. Each monomer charge or monomer mixture charge is polymerized under solution polymerization conditions such that the polymerization of each monomer charge or monomer mixture is substantially complete before charging a subsequent charge. A coupling agent can be added after polymerization is complete. Conjugated dienes having 4 to 12 carbon atoms per molecule are suitable and can be used in the copolymers of the present invention. Those having 4 to 8 carbon atoms are preferred. Examples of such suitable compounds include 1,3-butadiene; 2-methyl-1,3-butadiene;2-ethyl-1,3-butadiene;2,3-dimethyl-1,3-butadiene;1,3-pentadiene; 3-butyl-1,3-octadiene; and mixtures thereof. 1,3-Butadiene and isoprene are preferred dienes; and 1,3-butadiene is most preferable. Suitable monovinylarene compounds which can be used in the copolymers include those having 8 to 18 carbon atoms per molecule, preferably 8 to 12 carbon atoms. Examples of such suitable compounds include styrene; alphamethylstyrene; 2-methylstyrene; 3-methylstyrene; 4-methylstyrene; 2-ethylstyrene; 3-ethylstyrene; 4-ethylstyrene; 4-n-propylstyrene; 4-t-butylstyrene; 2,4-dimethylstyrene; 4-cyclohexylstyrene; 4-decylstyrene; 2-ethyl-4-benzylstyrene; 4,(4-phenyl-n-butyl)styrene; 1-vinylnaphthalene; 2-vinylnaphthalene; and mixtures thereof. Styrene is the preferred monovinylarene compound. Generally, the monovinylarene/conjugated diene block copolymer will contain monovinylarene monomer in an amount in the range of from 55 weight percent to 95 weight percent based on the total weight of the final block copolymer, preferably in the range of from 60 weight percent to 95 weight percent, and more preferably in the range of from 70 weight percent to 90 weight percent. Generally the conjugated diene monomer will be present in the final block copolymer in an amount in the range of from 45 weight percent to 5 weight percent based on the total weight of the final block copolymer, preferably in the range of from 40 weight percent to 5 weight percent, and more preferably in the range of from 30 weight percent to 10 weight percent. Preferably, the monovinylarene/conjugated diene block copolymer exhibits a refractive index of 1.56 to 1.58 measured according to ASTM 542. Polymers of component (B), modified poly(ethylene terephthalate), are high molecular weight polymers made by condensing ethylene glycol with terephthalic acid or dimethylterephthalate and comonomers or modifying agents, regardless of how prepared. The poly(ethylene terephthalate) is modified by the inclusion of comonomers or modifying agents selected from the group consisting of diols, diacids, hydroxyacids, and mixtures thereof. Generally a comonomer or modifying agent is present in an amount in the range of 5 weight percent to 20 weight percent based on the total weight of the modified poly(ethylene terephthalate). Such comonomers or modifying agents include various diols such as 1,4-butanediol; 1,4-cyclohexanedimethanol; diethylene glycol; hydrolyzed polyalkylene oxides; neopentyl glycol; butylene glycol, 1,3-propanediol; and mixtures thereof. Likewise, such comonomers or modifying agents can include various diacids such as isophthalic acid, adipic acid, sebacic acid, 2,6-naphthalene dicarboxylic acid, hydroxy acids such as p-hydroxy benzoic acid, and mixtures thereof. Mixtures of modified poly(ethylene terephthalate) can be used. Suitable modified poly(ethylene terephthalate) is commercially available. Of the suitable modifying agents, diols are preferred. Modified poly(ethylene terephthalate) wherein the modifying agent contains at least 50 mole percent ethylene glycol and 20 to 50 mole percent 1,4-cyclohexanedimethanol is especially preferred. The modified poly(ethylene terephthalate) employed herein generally has an inherent viscosity of at least 0.2, preferably in the range of from 0.2 to 10.0 as measured by ASTM D-2857. Inherent viscosity is measured in a 3:1 volume ratio of methylene chloride and trifluoroacetic acid at 30°C. Preferably the refractive index of the modified poly(ethylene terephthalate) is similar to the refractive index of the monovinylarene/conjugated diene employed, i.e. in the range of 1.56 to 1.58 measured according to ASTM 542. Polymers of component (C) , poly(ethylene terephthalate), are high molecular weight polymers made by condensing ethylene glycol with terephthalic acid or dimethylterephthalate regardless of the preparation steps involved. The polymers are not further modified with the modifying agents listed above or their equivalents. The poly(ethylene terephthalate) employed herein generally has an inherent viscosity of at least 0.2, preferably in the range of from 0.5 to 5.0 as measured utilizing the same procedure as was used above for the modified poly(ethylene terephthalate). Preferably, the poly(ethylene terephthalate) exhibits a refractive index of about 1.57 measured according to ASTM 542. The composition of the polymer blend can vary broadly. Generally component (A), the monovinylarene/conjugated diene block copolymer, is present in an amount in the range of from 10 weight percent to 90 weight percent based on the total weight of the polymer blend, preferably from 10 weight percent to 80 weight percent, more preferably from 15 weight percent to 60 weight percent. Component (B), the modified poly(ethylene terephthalate), is generally present in an amount in the range of from 5 weight percent to 85 weight percent based on the total weight of the polymer blend, preferably from 10 weight percent to 50 weight percent, more preferably from 20 weight percent to 40 weight percent. Generally component (C) is present in an amount in the range of from 5 weight percent to 85 weight percent based on the total weight of the polymer blend, preferably from 10 weight percent to 50 weight percent, more preferably from 20 weight percent to 40 weight percent. Polymer blends of the present invention as described above exhibit a combination of desirable characteristics. The polymer blends exhibit haze of less than 10 percent, measured with a Gardner Hazemeter according to ASTM 1003, using test specimens of 1.27 nm (50 mil) thickness, preferably less than 6 percent, most preferably 5.75 percent or less. The polymer blends exhibit Shore D Hardness of greater than 70 measured according to ASTM D-2240. Preferably, the Flexural Modulus of the polymer blends, measured according to ASTM D-648, will be greater than 1.55 . 10 9 N/m 2 (225 kilopounds per square inch (ksi)). The polymer blends will exhibit a Notched Izod Impact Strength of greater than 64.05 N·m/m (1.20 ft·lbs/inch). Blending can be accomplished by any method known in the art. Preferably the polymers are melt blended employing any desired means such as a Banbury mixer, a hot roll, or an extruder. More preferably the polymers are melt blended employing extruder blending techniques. Single or twin screw extruders can be utilized. The polymers can be dry blended prior to the melt blending. The blending conditions depend upon the blending technique and polymers employed. If an initial dry blending of the polymer is employed, the blending conditions may include temperatures from room temperature up to just under the melting temperature of the polymer, and blending times in the range of a few seconds to hours, e.g. 2 seconds to 30 minutes. During the melt blending, the temperature at which the polymers are combined in the blender will generally be in the range between the highest melting point of the polymers employed and up to 100°C above such melting point. The time required for the melt blending can vary broadly and depends on the method of blending employed. The time required is the time sufficient to thoroughly mix the components. Generally, the individual polymers are blended for a time of 5 seconds to 15 minutes. The polymer blends can contain additives such as stabilizers, anti-oxidants, anti-blocking agents, mold release agents, dyes, and pigments, flame retardants, as well as fillers and reinforcing agents, such as glass fibers as long as the amounts and types do not interfere with the objectives of this invention. The polymer blends prepared according to the invention are useful for the production of articles prepared by milling, extrusion, injection molding, or blow molding. EXAMPLE The following example is presented to further illustrate the invention. This example demonstrates the combination of clarity and mechanical properties of various polymer blends. Styrene/butadiene block copolymer (SB), modified poly(ethylene terephthalate) (PETG), and an unmodified, poly(ethylene terephthalate) (PET) were blended employing a Werner & Pfleiderer ZSK-30 twin screw extruder. The styrene/butadiene block copolymer (SB) was prepared employing a sequential solution polymerization and three initiator charges according to the process described in U.S. 4,584,346. Polymerization was allowed to continue to completion after each monomer charge. The sequence of styrene (S), butadiene (B), initiator (i), and coupling agent (CA) charges was as follows: S, i, i, S, B, i, S, B, CA. Polymerization temperature ranged from 38° to 110°C and pressure ranged from 0.014 to 0.41 MPa gauge (2 psig to 60 psig). The weight ratio of styrene to butadiene in the styrene-butadiene block copolymer designated KR03 in Table 1 was 75/25. Following completion of the sequential polymerizations, Vikoflex 71710, (a coupling agent comprising epoxidized soybean oil sold by Viking Chemical Co.) was charged to the reactor. The styrene/butadiene block copolymers (KR03) were stabilized with Irganox 1076 and tris(nonylphenyl) phosphite. The KR03 exhibited melt flows in the range of from 5 g/10 min. to 15 g/10 min. measured according to ASTM D-1238, Condition G. The KR03 exhibited a Notched Izod Impact Strength greater than 16.01 N·m/m (0.3 ft·lbs/in.) measured according to ASTM D-256. The modified poly(ethylene terephthalate) (PETG) employed was ethylene,1,4-cyclohexylenedimethylene terephthalate copolymer, Kodar 6763, from Eastman chemical. The PETG exhibited a refractive index of 1.567, a Notched Izod Impact Strength of 43.77 N·m/m (0.82 ft·lbs/in.) measured according to ASTM D-256, and Haze of 0.5% measured according to ASTM 1003. The poly(ethylene terephthalate) (PET) employed was Ektar 9921 from Eastman Chemical. The PET (amorphous state) exhibited a refractive index of 1.575 measured according to ASTM 542, Notched Izod Impact Strength of 19.75 N·m/m (0.37 ft·lbs/in.) and Haze of 2.8% measured according to ASTM 1003. PET and PETG were dried in a desiccant oven for 4 hrs. Components of the runs were dry blended and samples were extruded. The results are summarized in Table 1. Run Composition Weight % Flexural Modulus (ksi) 10 9 ·N/m 2 Notched Izod (ft • lb/in) N·m/m Hardness Shore D Haze % 101 KR03 (214) 1.48 (0.43) 22.95 65 2.6 102 PET (316) 2.18 (0.37) 19.75 75 2.80 103 PETG (286) 1.97 (0.82) 43.77 75 0.50 104 33PET/67PETG (306) 2.11 (0.74) 39.50 76 0.90 105 67PET/33PETG (320) 2.21 (0.46) 24.55 76 1.06 106 33KR03/67PET (253) 1.75 (0.47) 25.09 73 14.6 107 67KR03/33PET (215) 1.48 (1.01) 53.91 69 10.8 108 33KR03/67PETG (234) 1.61 (2.66) 141.99 73 116 109 67KR03/33PETG (218) 1.50 (1.3) 69.39 69 14.6 110 40KR03/40PETG/20PET (234) 1.61 (1.36) 72.60 72 5.72 111 40KR03/20PETG/40PET (239) 1.65 (1.22) 65.12 73 4.62 112 20KR03/40PETG/40PET (265) 1.83 (5.45) 290.92 74 3.94 KR03: K-Resin, 75:25 Styrene-Butadiene copolymer, Phillips Petroleum PETG: Poly(ethylene terephthalate) copolymer, Kodar 6763, Eastman Chemical PET: Poly(ethylene terephthalate), Ektar 9921, Eastman Chemical Haze in percent was measured according to ASTM 1003. Hardness (Shore D) was measured according to ASTM D-2240. Flexural Modulus in N/m 2 (ksi) was measured according to ASTM D-648. Notched Izod Impact Strength in N·m/m (ft·lb/in) was measured according to ASTM D-256. Table 1 demonstrates that polymer blends of either KR03 and PETG, or KR03 and PET , (Runs 106-109), exhibit unacceptably poor Haze characteristics and range from very poor to acceptable toughness (Notched Izod). When PET was blended with PETG, although good Haze characteristics were observed, very poor toughness was present. Nonetheless, when the 3 components (KR03/PETG/PET) were blended together, the blend exhibited significantly improved toughness as well as improved Haze characteristics.

Claims: A polymer blend composition comprising (a) a monovinylarene/conjugated diene block copolymer present in an amount in the range of from 10 to 90 weight percent based on the total weight of the polymer blend, wherein monovinylarene is present in said monovinylarene/conjugated diene block copolymer in an amount in the range of from 55 to 95 weight percent, preferably from 60 to 95 weight percent, most preferably from 70 to 90 weight percent, each based on the weight of the monovinylarene/conjugated diene block copolymer, and wherein conjugated diene is present in said monovinylarene/conjugated diene block copolymer in an amount in the range of from 45 to 5 weight percent, preferably from 40 to 5 weight percent, most preferably from 30 to 10 weight percent, each based on the weight of the monovinylarene/conjugated diene block copolymer; (b) a modified poly(ethylene terephthalate), present in an amount in the range of from 5 to 85 weight percent based on the total weight of the polymer blend, wherein the modified poly(ethylene terephthalate) is modified by the inclusion of comonomers selected from diols, diacids, hydroxy acids and mixtures thereof; and (c) a poly(ethylene terephthalate) present in an amount in the range of from 5 to 85 weight percent based on the total weight of the polymer blend. The composition of claim 1, wherein said monovinylarene/conjugated diene block copolymer (A) is present in an amount in the range of from 10 to 80 weight percent, preferably from 15 to 60 weight percent, each based on the total weight of the polymer blend; said modified poly(ethylene terephthalate) (B) is present in an amount in the range of from 10 to 50 weight percent, preferably from 20 to 40 weight percent, each based on the total weight of the polymer blend; and said poly(ethylene terephthalate) (C) is present in an amount in the range of from 10 to 50 weight percent, most preferably from 20 to 40 weight percent, each based on the total weight of the polymer blends. The composition of claim 1 or 2, wherein said monovinylarene in monovinylarene/conjugated diene block copolymer is styrene. The composition of any of claims 1 to 3, wherein said conjugated diene in said monovinylarene/conjugated diene block copolymer is butadiene. The composition of any of the preceding claims, wherein said modifying agent in component (B) is a diol. The composition of any of the preceding claims, wherein said monovinylarene/conjugated diene copolymer exhibits a refractive index of 1.56 to 1.58 measured according to ASTM 542. The composition of any of the preceding claims, wherein said modified poly(ethylene terephthalate) exhibits a refractive index of 1.56 to 1.58 measured according to ASTM 542. The composition of any of the preceding claims, wherein said poly(ethylene terephthalate) exhibits a refractive index of about 1.57 measured according to ASTM 542. The composition of any of the preceding claims, which exhibits haze of 6 percent or less, preferably of 5.75 percent or less, each measured with a Gardner Hazemeter according to ASTM 1003, using test specimens of 1.27 mm (50 mil) thickness. The composition of any of the preceding claims, which exhibits Shore D Hardness of 70 or greater measured according to ASTM D-2240, Flexural Modulus of 1.55 · 10 9 N/m 2 (225 kilopounds per square inch) or greater, measured according to ASTM D-648, and a Notched Izod Impact Strength of 64.05 N·m/m (1.20 ft·lbs/inch) or greater, measured according to ASTM D-256. An article made from the composition of any of the preceding claims. A process for preparing a polymer blend comprising melt blending the components comprising (A) a monovinylarene/conjugated diene block copolymer present in an amount in the range of from 10 to 90 weight percent based on the total weight of the polymer blend, wherein said monovinylarene is present in an amount in the range of from 55 to 95 weight percent, preferably from 60 to 95 weight percent, each based on the weight of the monovinylarene/conjugated diene block copolymer, and wherein said conjugated diene is present in an amount in the range of from 45 to 5 weight percent, preferably from 40 to 5 weight percent, each based on the weight of the monovinylarene/conjugated diene block copolymer; (B) a modified poly(ethylene terephthalate) present in an amount in the range of from 5 to 85 weight percent based on the total weight of the polymer blend, wherein the modified poly(ethylene terephthalate) is modified by the inclusion of comonomers selected from diols, diacids, hydroxy acids and mixtures thereof; and (C) a poly(ethylene terephthalate) present in an amount in the range of from 5 to 85 weight percent based on the total weight of the polymer blend.

Inventors: HANES MARK D, HANES, MARK D.
Applicants: PHILLIPS PETROLEUM CO, PHILLIPS PETROLEUM COMPANY
Application year: 1996
Main classification: C08L53
IPC codes: C08L67, C08L53