Laser scribing on glass using Nd:YAG laser

Abstract: A method and an apparatus for inscribing a pattern into a surface (18a) of a substrate (18), such as a sheet of glass, are disclosed. The method includes the steps of providing a Nd:YAG laser (12) having a characteristic output wavelength at 1,06 micrometers, providing a glass substrate (18) that is substantially transparent to the characteristic output wavelength and applying a layer (16) of material, such as a layer of tape, to the surface (18a). The layer (16) of material is selected so as to strongly absorb the characteristic output wavelength. A next step focusses (14) an output (12a) of the laser (12) into a spot (12c) at or near to an interface between the layer (16) of material and the surface (18a) of the substrate (18). A further step translates (20) the surface (18a) relative to the spot (12c). The layer (16) of material absorbs the output of the laser (12) and is heated thereby to a temperature sufficient for inscribing the surface (18a) underlying the spot (12c). That is, the layer (16) of material enables the laser (12) to build a plasma state adjacent to the surface (18a) of the substrate (18), which in turn scribes the surface (18a) of the substrate (18).

Description: The present invention relates to a method for inscribing a pattern into a surface of a substrate, comprising the steps of providing a source of electromagnetic energy having a characteristic output wavelength, providing the substrate, temporarily applying a layer of material to the surface of the substrate, the layer of material being selected so as to strongly absorb the characteristic output wavelength, and translating the surface relative to an output of the source, wherein the layer of material absorbs the output of the source and is heated thereby to a temperature sufficient for inscribing the surface. Such a method is known from GB-A-2 126 956. This invention relates generally to the inscription of an image within a surface and, more particularly, to methods that use laser energy for permanently marking or inscribing a pattern into a surface of a material. Conventional techniques for inscribing an image into glass include mechanically abrading the surface of the glass with a pointed instrument, abrading the surface with a stream of particles (e.g., sand blasting), and chemically etching the surface. Each of these techniques has certain disadvantages and drawbacks, including a difficulty in accurately controlling the process, a requirement to perform an extensive cleanup of the workpiece, and the use of potentially harmful or toxic substances. Laser energy has been recognized as a suitable means for inscribing an image into the surface of glass, as evidenced by U.S. Patent No.: 5,298,717 by DeRossett, Jr., entitled "Method and Apparatus for Laser Inscription of an Image on a Surface". In the approach of DeRossett, Jr. a CO 2 or an excimer laser is translated relative to a workpiece, such as the window of an automobile, so as to etch a desired pattern, such as a VIN number, bar code, or decorative design, into the window. CO 2 and excimer lasers are used because glass is opaque to their output wavelengths. When using the CO 2 laser the preferred power is between 10 watts and 20 watts, with powers below 10 watts said to be inadequate for etching a glass surface. As can be appreciated, the technique of DeRossett, Jr. can be disadvantageous for some applications, as it requires that a laser be selected which is capable of outputting a beam to which the workpiece is opaque. The laser is also required to operate at significantly high power levels. From the above-mentioned document GB-A-2 126 956, a method of structuring the surface of materials which do not absorb laser radiation is known, wherein the surface to be structured is remote from the source of laser radiation and is brought into contact with a metal surface or the surface of another material which does absorb the laser radiation. Further, a laser beam machining method is known from Patent Abstracts of Japan, Vol. 010, No. 134 (M-479), May 17, 1986. When an scribing work is performed by radiating a laser beam on a soft glass, a film and an adhesive material are attached to the side of the soft glass to be scribed. The film consists of a rigid high molecule as of a wrapping material. The film and the adhesive material are evaporated only with consuming several percent of the energy of the irradiating laser beam and the remaining laser beam energy is used for the work of the soft glass. This method is said to prevent the generation of micro cracks in the brittle soft glass material. Further, US-A-3,701,880 discloses a method of achieving decorative effects in the case of glass lamp bulbs. The glass lamp bulbs are coated with a thin layer of a material different from the material of the lamp bulb, e.g. titanium dioxide. Desired patterns are laser-etched in said coating applied to the exterior surface of the bulb so as to produce a plurality of spaced cavities in the bulb surface and through the - opaque - coating so as to achieve the decorative effect. It is a first object of this invention to provide an improved technique for inscribing an image into a transparent substrate that overcomes the foregoing and other problems. It is a second object of this invention to provide a method for inscribing an image into a transparent glass substrate with laser radiation, wherein the laser radiation may have an output wavelength that is not significantly absorbed by the glass substrate. It is a further object of this invention to provide a method for inscribing an image into a transparent glass substrate using a conventional Nd:YAG laser having an output wavelength of 1.06 micrometers. These objects are achieved by the method for inscribing a pattern into a surface of a substrate, mentioned at the outset, wherein the output of the source is focussed into a spot located at or adjacent to an interface between the layer of material and that surface of the substrate, which faces to the source. In general, the foregoing and other problems are overcome and the objects of the invention are realized by methods for inscribing a pattern into a surface of a substrate with electromagnetic radiation, wherein the substrate may be substantially transparent or reflective to the radiation. In one aspect of this invention there is provided a method for inscribing a pattern into a surface of a glass substrate. The method includes the steps of providing a Nd:YAG laser having a characteristic output wavelength of 1.06 micrometers; providing a glass substrate that is substantially transparent to the characteristic output wavelength; and applying a layer of material, such as tape, to a surface of the substrate. The layer of material is selected so as to strongly absorb the characteristic output wavelength. A next step focuses an output of the laser into a spot that is located preferably at or near an interface between the glass substrate and the layer of material. A further step translates the surface relative to the spot. The layer of material absorbs the output of the laser and is heated thereby to a temperature sufficient for inscribing the surface underlying the spot. That is, the layer of material enables the laser to build a plasma state adjacent to the surface of the substrate, which in turn scribes the surface of the substrate. The teaching of this invention eliminates the restriction to limit workpieces to only those that are opaque to the laser wavelength. Also, the disadvantages observed when using mechanical abrasion and chemical etching are avoided. Furthermore, the Nd:YAG output power is shown to be significantly less than the 10 to 20 Watt output power required when using the above-described CO 2 laser to inscribe glass. In addition, the shorter wavelength of the Nd:YAG laser (1.06 micrometers) versus the wavelength of a CO 2 laser (10.6 micrometers) provides for scribing the substrate with a finer resolution. The above set forth and other features of the invention are made more apparent in the ensuing Detailed Description of the Invention when read in conjunction with the attached Drawings, wherein: Fig. 1 is block diagram of a laser inscription system in accordance with this invention; and Fig. 2 is an elevational view of a glass substrate being laser inscribed in accordance with this invention. Reference is made to Figs. 1 and 2 for showing a presently preferred embodiment of a laser-based inscription system 10. A laser 12 delivers a collimated beam 12a to a focusing objective 14. The focusing objective 14 provides a focused beam 12b to a focal spot 12c. A workpiece 18 includes, in accordance with this invention, an overlying layer 16 of opaque material that strongly absorbs the wavelength output from the laser 12. That is, the layer 16 absorbs all or substantially all of the beam 12b. In a preferred embodiment of the invention the workpiece 18 is coupled to a multi-axis (x-y) translation stage 20. During operation the translation stage 20 controllably positions the workpiece 18 and overlying opaque material layer 16 relative to the focal spot 12c. The laser energy is absorbed within the material 16, which enables the laser energy to build a plasma state adjacent to surface 18a of the workpiece 18, which in turn scribes the surface 18a of the workpiece 18 as indicated by the characters 22 shown in Fig. 2. In a second, non-illustrated, embodiment of this invention the workpiece 18 is fixed in position and the laser 12 and/or the laser beam delivery system is moved relative to the surface 18a of the workpiece 18. The focal spot 12c is located at or adjacent to an interface between the surface 18a and the material 16. By example, the location of the focal spot 12c can be adjusted with a resolution of approximately 0.0254 mm [0.001 inch] or less, and the focal spot 12c is set so as to be within, by example, a few thousandths of 25.4 mm [an inch] of the interface between the surface 18a and layer of material 16. In accordance with this invention the workpiece 18 may be substantially transparent to the wavelength output by the laser 12. By example, the workpiece 18 may be a sheet of window glass, and the laser 12 may be a Nd:YAG laser having an output wavelength of 1.06 micrometers. The layer 16 of opaque material can be embodied in a length of 0.051 mm [0.002 inch] thick amber colored Kapton™ tape that is available from 3M, part number 5413. The amber-colored tape is selected for strongly absorbing the 1.06 micrometer radiation output by the laser 12, and is ablated by same. The ablation of the tape results in the generation of a localized region of high temperature which is sufficient for scribing the surface 18a. In the absence of the tape the laser energy would pass substantially unabsorbed through the glass sheet, and a desired pattern would not be inscribed into the surface. Another suitable tape is a bluish-colored reticle tape that was obtained from Nitto Semiconductor Equipment, number 18074-6, Roll Plastic Blue, Medium Tack. This tape is useful in that it leaves little residue on the substrate after removal. However, the above-described amber-colored tape was preferred for use in that the repeatability was found to be better. The objective lens 14, in a preferred embodiment of the invention, is embodied in a 60 millimeter, three element apoachromat focusing objective that is available from the U.S. Laser Company, part no. 3440. The translation stage 20 is a computer controlled system that includes a character generator sub-system, and is available from Anarad as an Anomatic III system, model 2414. Example: A glass substrate was etched with a Nd:YAG laser 12 having a 1.06 micrometer, 2.3 Watt output with a 1.3 kilohertz pulse repetition frequency (PRF). The glass substrate was moved at 0.05 inch/second by the translation stage 20 during the etching process. The glass substrate had a layer of the above-described amber-colored tape applied to the surface into which a pattern was permanently etched. The tape was removed after the desired pattern was etched into the surface of the glass substrate. It can be appreciated that the teaching of this invention overcomes the problems that are inherent in the prior art. For example, it is not necessary to limit the workpieces to only those that are opaque to the laser wavelength. Also, the disadvantages observed when using mechanical abrasion and chemical etching are avoided. Furthermore, the 2.3 Watt Nd:YAG output power is significantly less than the 10 to 20 Watt output power required when using a conventional CO 2 laser to inscribe glass, and the significantly shorter wavelength of the Nd:YAG laser provides superior resolution. Although described in the context of a system for scribing glass, it should be further realized that a number of different materials can be laser inscribed in accordance with the invention. By example, the substrate may be comprised of sapphire. Also be example, the substrate can be a mirror, which would tend to reflect a significant portion of the laser light in the absence of the overlying layer of absorptive material. Further by example, the layer of absorptive material can be sprayed or painted on, and then subsequently removed after inscribing the desired pattern. The teaching of this invention is also not limited for use with an apoachromat focussing objective, in that a number of different optical lens types, and also reflector types, can be employed for providing a localized region of high intensity electromagnetic radiation at or near to the surface to be scribed.

Claims: A method for inscribing a pattern into a surface (18a) of a substrate (18), comprising the steps of: providing a source (12) of electromagnetic energy having a characteristic output wavelength; providing the substrate (18); temporarily applying a layer of material (16) to the surface (18a) of the substrate, the layer of material (16) being selected so as to strongly absorb the characteristic output wavelength; and translating the surface (18a) relative to an output of the source (12), wherein the layer of material (16) absorbs the output of the source (12) and is heated thereby to a temperature sufficient for inscribing the surface (18a), characterized by focussing the output of the source (12) into a spot (12c) located at or adjacent to an interface between the layer of material (16) and that surface (18a) of the substrate (18), which faces to the source (12). The method of claim 1, characterized in that the step of providing a source of electromagnetic energy includes a step of providing an Nd:YAG laser (12), and that the characteristic wavelength is 1,06 micrometers. The method of claim 1 or 2, characterized in that the step of focussing includes a step of applying a collimated output (12a) of the source to a focussing objective (14). The method of claim 3, characterized in that the focussing objective (14) is an apoachromat focussing objective. The method of any of claims 1-4, characterized in that the substrate (18) is substantially transparent to or reflective of the characteristic wavelength. The method of any of claims 1-5, characterized in that the layer (16) of material is composed from a tape.

Inventors: RICHMAN JOHN A, RICHMAN, JOHN A.
Applicants: RAYTHEON CO, RAYTHEON COMPANY
Application year: 1996
Main classification: B23K26
IPC codes: H01S3, B23K26, G02B27, B41M5