PROCESS FOR THE PREPARATION OF ALUMINUM OXIDE FILM USING DIALKYLALUMINUM ALKOXIDE

Abstract: An aluminum oxide film is economically and conveniently deposited on a substrate by a process which comprises vaporizing a dialkylaluminum alkoxide compound at a temperature ranging from 0 to 25 DEG C and contacting the resulting vapor with said substrate heated to a temperature ranging from 300 to 600 DEG C.

Description: PROCESS FOR THE PREPARATION OF ALUMINUM OXIDE FILM USING DIALKYLALUMINUM ALKOXIDE Field of the Invention The present invention relates to a process for coating a suDstrate with an aluminum oxide film by chemical vapor deposition using a dialkylalummum alkoxide compound as an aluminum source. Background of the Invention There have hitherto been reported a number of chemical vapor deposition (CVD) methods for the preparation of an aluminum oxide film. These methods are well summarized in recent review by E. Fredπksson et al., "Chemical Vapour Deposition of Aluminum Oxides from Various Gas Mixture," ana J. Chemical Vapor Deposition, JL, 333-417 (1993) as well a^ in Korean translation of 'CVD Handbook' pp 665-689 (Bando Publishing Co., Seoul, Korea, 1993). Aluminum trichloride and triisopropoxide have been most commonly used as aluminum sources in the CVD of an aluminum oxide film due to their low cost and ready availability. These conventional aluminum sources have low vapor pressures and are usually heated to higher than 100 °C to generate a vapor stream to be used in a CVD process. Further, tπalkylaluminums have been used in the CVD of an aluminum oxide film, which are liquid at room temperature and have relatively high vapor pressure. However, such trialkylalummuiτis do not contain oxygen atoms, thus the use of an oxygen source such as 0 2 or N 2 0 is essential for the formation of an aluminum oxide film. Also trialkylalummums are pyropho ic when exposeα to air. U.S. Patent No. 4,675,089 discloses a plasma-assisted CVD method of depositing an amorphous thin film of aluminum oxide using d trialkylaluminum vapor and carbon dioxide. However, this method requires expensive equipments to produce plasma ana have lower throughput compared to a thermal CVD method, thus less suitable for use in a large-scale application. Summary of the Invention Accordingly, it is an ob ect of the present invention to provide an efficient and economical process for the preparation of an aluminum oxide film suitable for a large scale production of articles coated with aluminum oxide film. In accordance with one aspect of the present invention, there is provided a process for coating a substrate with an aluminum oxide film, which comprises contacting a vaporized dialkylalummum alkoxide compound with said substrate heated to a temperature ranging from 300 to 600 °C. Brief Description of the Drawings FIG. 1 represents an Auger electron spectrum of an aluminum oxide film deposited on SI(100) at 400 °C using diethylalum um isopropoxide accordance with Example 6 of the present invention; and FIG. 2 shows an Auger depth profile of the film obtamed m Example 6. Detailed Description of the Invention The present invention is characte izeα in that a dialkylalummum alkoxide s used as an aluminum source m the chemical deposition of an aluminum oxide film. Tne dialkylalummum alkoxide useful for practicing the present invention is a material which has a high vapor pressure sufficient to vaporize under an ambient condition, i.e. , 0.06 to 0.5 m Hg at a temperature ranging from 0 to 25 °C. The dialkylalummum alkoxide compound suitable for use m the present invention is represented by the following formul : R 1 2 A10R 2 wherein R and R 2 are each mdependently a C,_ 10 alkyl group. The dialkylalummum alkoxide compound according to the present invention may be prepared by reacting an alkylaluminum with an alcohol at a low temperature by a conventional method, e.g., as is described by Paul S. Coan, et al. Orqanometallics , 8 . , 2724 (1989), or by reacting an alkylaluminum with an aluminum alkoxide in a molar ratio of 2:1 at room temperature. The preferred dialkylalummum alkoxide compounα an practicing the present invention may be dimethylalummum isopropoxide, diethylalummu lsopropoxide, dimethylalum uπ t-butoxide and a mixture thereo . Under an ambient condition, dimethylalummum isopropoxide is a liquid, whereas diethylalummum isopropoxide and dimethylalummum t butoxide are gel-like solids. In accordance with the present invention, the dialkylalummum alkoxide compound is vaporized at an ambient temperature ranging from 0 to 20 °C and the vapor thereof is then contacted with the surface of a substrate heated at a temperature ranging from 300 to 600 °C to deposit an aluminum oxide film thereon. The vaporization of dialkylalummum alkoxide compound may be carried out m a reactor which is preferably maintained at an internal pressure of 10 to 50 mbar. The substrate which may be used in practicing tne present invention is an inorganic solid which is stable under the CVD condition and examples thereof mclude glass, quartz, silicon, gallium arsenide, sapphire, alkali metal niobate, alkaline earth metal titanate, gallium nitride, niobium nitride and the like, among which silicon smgle crystal is preferred when the coated substrate is mtended for electronic applications. The following Preparatives and Examples are provided foi the purposes of illustrating certain aspects of the present invention only; they are not to be construed as limiting the scope of the present invention any way. Preparative 1: Synthsis of dimethylalummum t-butoxide To 2.07 g (28.7 mmol) oi trimethyl aluminum dissolveα in 30 ml of dry ethyl ether was added 2.13 g (28.7 mmol) of t-butanol at -70 °C, and the resulting mixture was warmed to room temperature while stirring and the solvent was evaporated off under a reduced pressure. The residue was sublimed to obtain 2.16 g (16.6 mmol, 58 % yield) of the title compound in the form of a gel-like solid. 1 r; NMR analysis benzene-d 6 of the compound obtamed showed peaks at δ -0.42(s, A1(CH 3 ) 2 , 6H) and 1.15(s, OC(CH 3 ) 3 , 9H) . Preparative 2: Synthsis of dimethylalummum isopropoxide To 2.75 g (38.1 mmol) of trimethyl aluminum was added 3.90 g (19.1 mmol) of aluminum isopropoxide which was previously purified by distillation unαer a reduced pressure to obtam 12.52 g (108 mmol, 87 % yield) of the title compound in the form of a colorless liquid that boils at a temperature ranging from 68 to 72 °C at 10 mHg. 1 H NMR in benzene-d 6 analysis of the compound obtained showed peaks at δ -0.47(s, A1(CH 3 ) 2 , 6H), 0.99(d, OCH(CH 3 ) 2 , 6H) and 3.84(heptet, OCH(CH 3 ) ? , IH). Preparative 3: Synthsis of diethylalummum isopropoxide To 1.21 g (10.6 mmol) of triethyl aluminum (93 I purity, Aldrich Chemical Co. ) was added 1.08 g (5.3 mmol) of aluminum triisopropoxide which was previously purified by distillation under a reduced pressure, and the resulting mixture was stirred for 24 hours and the mixture was sublimed to obtain 1.89 g (13.5 mmol, 85 yield as diethylalummum isopropamide) of the title compound the form of a gel-like solid. Example 1 0.05 g of dimethylalummum t-butoxide prepared Preparative 1 was vaporized at 0 °C and the vapor thereof was conveyed to a Sι(100) substrate preheated to 400 °C to conduct the chemical vapor deposition for 3 hours. The X- ray photoelectron spectrum of the deposited film showed peaks corresponding to oxygen and aluminum as well as carbon, but not the peaks for silicon. This observation shows that the surface of the silicon substrate is completely covered by an aluminum oxide film. Example 2 The procedure of Example 1 was repeated except that the Sι(100) substrate was preheated to 300 °C and the chemical vapor deposition was carried out for 1 hour. The X-ray photoelectron spectrum of the deposited f lm showed peaks corresponding to oxygen and aluminum as well as carbon, but not the peaks for silicon. Examp l e 3 0.1 g of dimethylalummum isopropoxide prepared in Preparative 2 was vaporized at room temperature and the vapor thereof was transported to a Si(100) substrate preheated to 350 °C to conduct the chemical vapor deposition for 5 hours. The X-ray photoelectron spectrum of the deposited film showed peaks corresponding to oxygen and aluminum as well as carbon, but not the peaks for silicon. Example 4 0.1 g of diethylalummum isopropoxide prepared in Preparative 3 was vaporized at room temperature and the vapor thereof was brought into contact with a Si (100) substrate preheated to 350 °C to conduct the chemical vapor deposition for 2 hours. The X-ray photoelectron spectrum of the deposited film showed peaks corresponding to oxygen and aluminum as well as carbon, but not the peaks for silicon. Example 5 0.1 g of dimethylalummum isopropoxide prepared in Preparative 2 was vaporized at room temperature and the vapor thereof was carried to a Si(100) substrate preheated to 600 °C to conduct the chemical vapor deposition for 5 hours. The X-ray photoelectron spectrum of the deposited film showed peaks corresponding to oxygen and aluminum as well as carbon, but not the peaks for silicon. Example 6 0.1 g of diethylalummum isopropoxide prepared in Preparative 3 was vaporized at room temperature and the vapor thereof was transported to a Si (100) substrate preheated to 400 °C to conduct the chemical vapor deposition for 10 hours. The Auger electron spectrum of the deposited film obtamed after sputtering for 6 seconds with 3.5 keV Ar + ion beam is shown in FIG. 1. And Auger depth profile of the same film is shown in FIG. 2. These data clearly indicate that the film is εtoichimetric with no appreciable carbon incorporation and the composition is constant through the bulk of the film. The thickness of the aluminum oxide film is estimated at 0.23 μm, assuming an etch rate of 0.83 nm/s. In accordance with the present invention as described above, an aluminum oxide film can be conveniently and effectively deposited on a substrate by way of using a dialkylalummum alkoxide compound as an aluminum source. The inventive process has the advantage that gas phase mixing can be completely avoided because no additional oxygen source is necessary, thus a large-scale production of aluminum oxide films is possible using simple equipments under much simplified conditions. While the invention has been described with respect to the specific embodiments, it should be recognized that various modifications and changes may be made by those skilled in the art to the invention which also fall within the scope of the mvention as defmed by the appended claims .

Claims: What is claimed is: 1. A process for coating a substrate with an aluminum oxide film, which comprises contacting a vaporized dialkylalummum alkoxide compound of formula (I) with said substrate: R 1 2 A10R 2 wherein R 1 and R 2 are each independently a C 1 10 alkyl group. 2. The process of claim 1 wherein the substrate is heated to a temperature ranging from 300 to 600 °C. 3. The process of claim 1 wherein tne vaporization of dialkylalummum alkoxide compound is conducted at a temperature ranging from 0 to 25 °C. 4. The process of claim 2 wherein the dialkylalummum alkoxide compound is selected from the group consisting oi dimethylalummum isopropoxide, diethylalummum isopropoxide, dimethylalummum t-butoxide and a mixture thereof. 5. The process of claim 4 wherein the dialkylalummum alkoxide compound is dimethylalummum isopropoxide. 6. The process of claim 1 wherein the substrate s a silicon smgle crystal.

Inventors: KIM YUN SOO, KOH WON YONG, KU SU JIN, KIM, YUN, SOO, KOH, WON, YONG, KU, SU, JIN
Applicants: KIM YUN SOO, KOH WON YONG, KOREA RES INST CHEM TECH, KU SU JIN, KIM, YUN, SOO, KOH, WON, YONG, KOREA RESEARCH INSTITUTE OF CHEMICAL TECHNOLOGY, KU, SU, JIN
Application year: 1996
Main classification: C23C16
IPC codes: C23C16, C30B29