Method of improving the wear quality of ultra-high molecular weight polyethylene

Abstract: A method of improving the wear quality of ultra-high molecular weight polyethylene with a molecular weight greater than 1,000,000 which includes subjecting a workpiece to solid phase deformation in at least two directions to cause a preferred multi-axially orientation, said deformation in at least two directions, having a deformation ratio of 1.3 to 1.9.

Description: This invention relates to a method of improving the wear quality of ultra-high molecular weight polyethylene. In a paper published in PLASTICS AND RUBBER PROCESSING AND APPLICATIONS II (1982)(215-224) "The Production of Orientated Polymers by hydrostatic Extrusion" by B. Parsons and I.M. Ward there is a discussion on small and large scale hydro-static extrusion experiments on a range of polymers with particular reference to polyethylene and polyoxymetholene. Hydro-static extrusion is shown to be a viable forming process for polymeric material and considerable property enhancement is said to be achieved. In this paper it is stated to be known that appreciable improvements in the stiffness of polymers can be produced by a high degree of plastic deformation, for example by stretching. There is reference to synthetic fibres, such as Nylon (polyamide) or polyethylene terethphthlate (polyester) being treated with a draw ratio (the ratio of final stretch length of the filaments to the initial length) which is comparatively small (typically about 5). The paper goes on to state that it was considered that the draw ratio set a limitation to the degree of molecular alignment and corresponded to stretching the network of polymer molecules to some geometric limit - the "natural draw ratios" - after which fracture of the chains occurred. A process is described in which the polymer is extruded into a tube shaped product under hydro-static pressure, which involves passing material over a fixed mandrel and a semi-conical plug for the purpose of imposing some hoop expansion to part of the billet material. There is reference to the extruded materials showing a marked improvement in thermal properties and other advantages. Some of the advantages are said to be increased stiffness, reduction in creep. Improved chemical resistance, low permeability to gases, high melting temperature, reduced shrinkage, very low axial expansion coefficient and high axial thermal conductivity are found but it goes on to state that there may be possible defects one of which is said to be deterioration in dry wear properties. GB-2 060 469 relates to the deformation of thermoplastic polymers, to the solid phase deformation and concomitant orientation of orientatable thermoplastic polymers. There is reference to drawing an article through a die so as to induce a substantial degree of molecular orientation throughout the drawn article. There is also reference to a deformation ratio which is said to be the ratio of the cross-sectional area of the polymer billet to that of the extruder die orifice and in a discussion of UK Patent GB-1 480 479 there is reference to deformation ratios greater than about 8:1. GB-2 060 469 itself is related to a process for drawing the workpiece through the die so that its plastics strain is progressively increased during start up of the process. It is stated that the process produces a product with increased Young's modulus; resistance to creep; resistance to gas transport; enhanced deadfold; of enhanced axial thermal conductivity and it further states that the polymer should have a weight average molecular weight less than 1,000,000. The specification goes on to state that the die drawing process can be used as a forming process for polymers with higher molecular weight but that this will not produce the enhanced properties listed. In this specification, deformation ratio is used to define the ratio of the initial cross-sectional area of the workpiece to the final cross-sectional area of the product. In the description of Figure 1 it states that the polymer coating is drawn through a converging die and deformation of the polymer continues beyond the drawing block for some distance before it becomes frozen out. Thus, in this arrangement the molecular orientation is probably lengthwise in the product or parallel to the draw direction. The advantages of the process are defined in all the examples by referring to the Young's modulus of the material achieved. GB-2 156 733 relates to a process for solid phase deformation of tubular materials of an orientatable, thermoplastic polymer and to the orientated tubular material so produced. This invention is intended to provide improved mechanical properties, especially in the directions other than the machine direction, that is the drawing direction and there is reference to the drawing of a hollow workpiece through a die and simultaneously over an internally positioned former. Again, the specification states that when it is intended to produce a product with enhanced Young's modulus; resistance to creep; and resistance to gas transport; enhanced deadfold; or enhanced axial thermal conductivity then the workpiece should desirably comprise a polymer having a weight average molecular weight of less than 1,000,000. As in the previously referred to GB-2 060 469 the specification states that the process may be used as a forming process but not providing the enhanced properties listed above and it could, for example, be used with an ultra-high molecular weight polymer having a molecular weight of about 3,000,000. Very clear orientated polyester material is referred to using a nominal deformation ratio of at least 2:1 and preferably at least 3:1 and there is reference to the clarity of the workpiece. GB-2 225 551 refers to a similar process for producing a biaxially orientated tubular material in which the deformation is carried out in the absence of any external force acting in a direction which is perpendicular to the axis of the workpiece. In this specification there is reference to hoop draw ratio which is defined as a ratio of the final hoop dimension to the initial hoop dimension, (i.e. measured circumferentially) and the axial draw ratio is the ratio of the initial bulk cross-sectional area of the hollow workpiece to the final bulk cross-sectional area of the product. The specification states that for polymeric polyethylene the inner hoop draw ratio is at least 1.2 and more preferably at least 1.5 and most preferably at least 2 and the preferred axial draw ratio is at least 2 and preferably greater than 3. It also states that the outer draw ratio may be less than 1 but is preferably at least 1 and more preferably at least 1.5 or 2 and the ratio of the axial draw ratio to the inner hoop draw ratio is preferably at least 1 and less than 4, most preferably less than 2. The specification also refers to the use of polyethylene polymers having a weight average molecular weight of from 50,000 to 150,000 and also to polymers above 300,000. United States Patent No. 5,030,402 shows a method for producing an UHMWPE product with enhanced planar mechanical properties. A initial UHMWPE semicrystaline morphology is solid-state deformed under compression in a mould including a mould cavity with an unenclosed perimeter zone or a perimeter zone with a reservoir enabling flow-through for moulded material. In this method the deformation under compression is applied from one direction and the material is pressed flat. The general direction of forming is therefore in only one direction. EP-A-0 310 449 described a process for producing a polyethylene material for use in products required high mechanical strength and high elastic modulus. This process involves the use of a specific class of particulate polyethylenes having an intrinsic viscosity of 5 - 50 dl/g in decalin at 135°C and the steps of compression-moulding, solvent immersing, solid-phase extruding or rolling and finally drawing the material in that order. Although compressing, extruding and drawing are referred to there is no suggestion that the present Applicant's result can be achieved by the process as set forth. Ultra high molecular weight polyethylene is used as a bearing material for various Applications, for example in the bearing surfaces of the joints in prostheses. Various orthopaedic manufacturers have sought methods of improving the wear properties and reducing the amount of generated wear debris from the bearing surfaces of such joints. It has been the intention of these projects to explore "improved" polyethylenes especially those produced by post processing. A number of potential improvements have been seen in recent years on the market, some of which have already failed to fulfil clinical expectations, for example carbon reinforced polyethylene, and cross-linked polyethylene. The present invention therefore relates to a method of improving the wear quality of ultra-high molecular weight polyethylene with a molecular weight greater than 1,000,000. As will be seen from the discussion of the prior art investigation has been directed to means for orientating thermoplastic polymers but these have been basically directed to polymers with a weight average molecular weight less than 1,000,000 and it will also be seen that in the prior art it has been stated that although the die drawing process can be used as a forming process for polymers with high molecular weight this does not produce the enhanced properties which have been achieved with lower molecular weights and it has been stated that it was thought that the processes described do not enhance wear properties. It has now been found by experiment that the wear properties of ultra-high molecular weight polyethylene can be improved by subjecting a workpiece to certain influences. According to the present invention a method of improving the wear quality of ultra-high molecular weight polyethylene with a molecular weight greater than 1,000,000 includes subjecting a workpiece to solid phase deformation in at least two directions to cause a preferred multi-axially orientation, characterised by applying deforming forces in at least two directions to subject a workpiece to solid phase deformation in at least the longitudinal direction and the hoop direction by forming a tube by passing the polyethylene workpiece over a former of increasing diameter over its length, and/or by drawing the workpiece through a die to cause solid phase deformation in two directions to cause multi-axial deformation, said deformation in said two directions, to cause orientation of polyethylene chains in said two directions, said deformation in said two directions, having a deformation ratio of 1.3 to 1.9 The preferred deformation ratios in each direction are 1.5 to 1.6. The ultra-high molecular weight polyethylene preferably has a molecular weight greater than 4,000,000. The second deformation ratio can be greater than the first. In a preferred method the workpiece is hollow and is passed over a former of increasing cross-sectional area, the second deformation taking place in a hoop direction. In another method the workpiece is solid and can be square or of rectangular cross-section transverse to its length. The invention also includes a UHMWPE workpiece which has been treated by the method set forth above. The invention can be performed in various ways and some methods will now be described by way of example and with reference to the accompanying drawings in which : Figure 1 is a graph showing the relative density of drawn materials (B) according to the present invention relative to drawn isotropic source material (I); Figure 2 is a graph showing the relative crystallinity of the material (B) made according to the invention relative to isotropic source material (I); Figure 3 is a diagrammatic representation of the method used according to one aspect of the present invention; Figure 4 is a diagrammatic perspective view of a material produced according to the invention; Figure 5 is a graph showing typical engineering stress strain curves; Figure 6 is a graph showing strain energy to failure and elastic modulus of material made according to the invention in comparison with isotropic materials; Figure 7 is a graph showing stress strain curves for materials made according to the invention relative to isotropic materials; Figure 8 is a graph showing wear test results; Figure 9 is another graph showing wear test results; Figure 10 is a diagrammatic view of a pin used for testing; Figure 11 is a diagrammatic view of a plate used for testing; Figure 12 is a diagrammatic perspective view of another method according to the invention; and, Figure 13 is a diagrammatic side elevation of a third method of applying the invention. The present invention is focused on biaxial orientation of ultra high molecular weight polyethylene to enhance its properties in at least two directions, and establishes conditions, where the strain energy to failure of the modified material is maintained and the proof or yield stress of the material is increased. The invention demonstrates for the first time successful die drawing of GUR412 (MW 4.5 million) UHMWPE in both uniaxial and biaxial forms. The drawn materials had similar density and crystallinity as shown in Figures 1 and 2 to the isotropic source material. The molecular orientation of the drawn material was confirmed by X-ray diffraction. The material was intended for use as polymer components in artificial joints which undergo complex loading regimes, stress field and wear patterns, it was considered preferable to enhance the properties of the UHMWPE in two directions, by using biaxial drawing methods. Figure 3 shows a method used for biaxial orientation of a thick walled tube 1, by drawing a material 2 over a mandrel 3 which is of increasing diameter over its length in the direction of draw indicated by reference numeral 4. Such a method of drawing polyethylene material to produce solid phase deformation is described in GB 2 225 551, but the effects produced by the present invention were unexpected considering the information set out, for example in the prior art documents referred to above. This method produced orientation in both the longitudinal direction indicated by arrow 5 and hoop direction indicated by arrow 6, as shown in Figures 3 and 4, with a higher draw deformation ration and orientation near the internal surface of the tube 7 than the outside 8 in the hoop direction 5. Material was produced such that the draw ratios close to the internal surface 7 were similar in magnitude in both the hoop 6 and longitudinal direction 5. Figure 5 shows typical engineering stress strain curves taken in tension in the longitudinal direction for the isotropic or standard material (A) and biaxially orientated material (B) with a draw ratio of 1.5 in each direction. This shows that the drawn material had a reduction in the strain to failure, approximately similar strain energy to failure and a higher proof stress and working stress range compared to the isotropic material. Increasing the draw ratio further adversely affected both the strain and strain energy to failure, producing a much more brittle material as shown in the curve for the highly drawn uniaxial material with a ratio of 4 to 1 as shown in Figure 5. Biaxially drawn material with a draw ratio of approximately 1.5 in each direction was considered to produce the most appropriate change in properties with a statistically significant increase in proof stress and working stress range while maintaining a similar strain energy to failure and elastic modulus to the isotropic material as shown in Figure 6. A detailed examination of the stress strain curve for the two material sat low strains shows clearly the improved characteristics of the biaxially orientated material as shown in Figure 7. Seven one metre long lengths of thick walled tube were produced from three different 75 mm thick slabs of GUR412 UHMWPE. The final dimensions of the drawn tube produced a wall thickness of between 10 and 15 mm with an outside diameter of 63 mm. The drawn material was found to have some dimensional instability when machined components were taken from the drawn tube, due to the release of inbuilt strains. Two types of wear tests were carried out, a polymer pin on a metal plate with reciprocating motion, and a spherical ended metal pin on polymer plate under reciprocating motion. The first test configuration maybe considered more appropriate for hip joint applications, while the second test may be considered more suited to knee joint applications. The polymer pins and plates were taken with their wear surfaces close to the internal diameter of the drawn tube, where the draw ratio was approximately 1.5 in each direction such a pin 9 and a plate 10 are shown in Figure 4. Each test consisted of a direct comparison between the biaxial material and the isotropic control material. Tests were carried out for sliding distances greater than 250 km (greater than 10 years equivalent), with more than 15 measurements in each test to allow statistical analysis. Tests were run in bovine serum as a lubricant, and the wear rate was expressed as a normalised wear factor K when, Wear factor = Wear Volume Load and Sliding Distance The results of five sets of polymer pin 9 on plate tests are shown in Figure 8. The specific conditions for each of the tests are set out below. POLYMER PIN ON PLATE WEAR TESTS 1 200N LOAD 2 160N LOAD 3 160N LOAD 4 80N LOAD 5 80N LOAD (ROUGH COUNTERFACE) In each of the tests the biaxial material has a lower wear rate than the isotropic control material. The differences were statistically significant at the 20 % level in Tests 2 and 3. Overall, the wear factor for the biaxial material was reduced by 22% compared to the isotropic material. The results for the polymer plate 10 on a pin test are shown in Figure 9. The isotropic material showed a higher wear factor than the biaxial material and this was statistically significant at the 5% level. The biaxial drawing of the material was predicted to produce a 25 % reduction in the wear rate of this test. Figures 10 and 11 are intended to illustrate what is thought to be the lines of molecular orientation on the test pieces. Thus, Figures 10 shows the work surface 9a on the end of the pin 9. The general direction of the molecular orientation is shown to be in two directions by arrows A and B. The point from which the pin has been taken is shown in Figure 4 and it will be seen that the lines of orientation are substantially at right angles to each other across the surface. In Figure 11 the lines of orientation are again shown in two directions C and D on one face 11a of the plate 10. It will be seen that the lines of orientation are at right angles on this face. On the face 11b however, although the lines of orientation C and D are again at right angles the lines D exhibit their ends towards the face and on the face 11c the lines of orientation D extend across the face but the lines C again exhibit their ends. It will be appreciated that the above Figures only show assumed lines of orientation and are meant to be interpreted in general terms. From the experimental results set forth above it is assumed that the best wear qualities are obtained when the lines are at right angles across the face, as shown in Figures 10, although this assumption may be only the result of the two different types of experiments applied. As will be seen from the above the mechanical properties of ultra high molecular weight polyethylene have been enhanced by biaxial drawing and a significant increase in proof stress and working stress range has been achieved, while maintaining the strain energy to failure. Wear tests have shown that this can produce a 22 to 25 % reduction in the wear rate of the biaxially drawn materials compared to the isotropic UHMWPE. An alternative method of causing solid phase deformation in at least two directions to ultra high molecular weight polyethylene (UHMWP) can be applied by a slot type drawing method. As shown in Figure 12 a rectangular or square strip of pre-machined UHMWP 12 is drawn through a slot 13 of a slot-type die 14 having an entry opening 15 and a discharge opening 16. The direction of draw is indicated by arrow 17 and the transverse width of the slot 13 is equivalent to the transverse width of the strip 12 at entry. With this arrangement there is solid phase deformation in the draw direction 17 and at an angle thereto, indicated by arrow 18 in the die slot, thus causing solid phase deformation in two directions to cause the preferred multi-axial orientation. The deformation ratios, that is the draw ratio and in effect the compression ratio in the slot, are both between 1.3 to 1.9. Figure 13 shows a method similar to that described and shown in Figure 3 and the same reference numerals are used to indicate similar parts but in this method the tube of material also passes through a control die 20. Other methods of producing solid phase deformation in at least two directions will be apparent to those skilled in the art, for example rolling and drawing, the governing factor being that the deformation ratios are between 1.3 to 1.9 to produce the preferred multi-axial orientation. In the method described with regard to Figures 1 to 9 the material produced is described as being intended for bearing elements in prosthetic joints but it will be appreciated that there are many other applications for the material produced.

Claims: A method of improving the wear quality of ultra-high molecular weight polyethylene with a molecular weight greater than 1,000,000 which includes subjecting a workpiece (1) to solid phase deformation in at least two directions to cause a preferred multi-axially orientation, characterised by applying deforming forces in at least two directions to subject a workpiece (1) to solid phase deformation in at least the longitudinal direction (5) and the hoop direction (6) by forming a tube by passing the polyethylene workpiece (1) over a former (3) of increasing diameter over its length, and/or by drawing the workpiece (1) through a die (14)(20) to cause solid phase deformation in two directions to cause multi-axial deformation, said deformation in said two directions, to cause orientation of polyethylene chains in said two directions (5,6), said deformation in said two directions (5,6), having a deformation ratio of 1.3 to 1.9 A method as claimed in claim 1 characterised in that said deformation ratios in each direction are 1.5 to 1.6. A method as claimed in claim 1 or claim 2 characterised in that the ultra-high molecular weight polyethylene has a molecular weight greater than 4,000,000. A method as claimed in claims 1 to 3 characterised in that the second deformation ratio is greater than the first. A method as claimed in any one of preceding claims characterised in that the workpiece (1) is hollow and passed over a former (3) of increasing cross-sectional area, the second deformation taking place in a hoop direction (6). A method as claimed in any one of preceding claims characterised in that the workpiece (1) is solid. A method as claimed in claim 8 characterised in that the workpiece (1) is of square or rectangular cross-section transverse to its length. A UHMWP workpiece (1)(12) which has been treated by the method set forth in any one of preceding claims 1 to 11.

Inventors: DOYLE CHRISTINA DR, DOYLE, CHRISTINA, DR.
Applicants: HOWMEDICA INTERNAT S DE R L, HOWMEDICA INTERNATIONAL S. DE R.L.
Application year: 1996
Main classification: B29C55
IPC codes: A61F2, B29K23, B29C55, C08J5, A61L27