Method and equipment for the application of wear resistant coatings by high vacuum physical vapour deposition

Abstract: The present invention relates to a method for the plasma assisted high vacuum vapour coating of parts with wear resistant coatings where the method comprises at least the process steps heating and conditioning and where the process step conditioning comprises heating. A protective gas is used for the heating. It is circulated at a pressure of at least 0,01 bar. Significant advantages are realized over state of the art methods using radiation heating. The method is preferentially carried out in an equipment conceived for it, which comprises a blower (3), protective shields (8) and gas flow management sheets (9).

Description: The invention concerns a method for the plasma assisted high vacuum vapour coating of parts with wear resistant coatings comprising at least the process steps of conditioning and coating and where the process step conditioning comprises a conditioning step heating. It also concerns the equipment for carrying out this method. Many methods for the physical vapour deposition were proposed over the last 30 years. Many of them have found widespread application since (see E. Bergmann and E. Moll: plasma assisted PVD coating technologies published in Surface Coatings and Technologies volume 37 (1989), pages 483 ff.). All these methods can be described as a combination of three process steps: conditioning, deposition, deconditioning. Conditioning comprises in most cases several conditioning steps: cleaning, putting under high vacuum, heating and plasma etching. Deconditioning comprises in most cases the deconditioning steps: cooling, removing from high vacuum and conservation. This sequence of steps is used in almost all methods for the plasma assisted high vacuum physical vapour coating of parts with wear resistant coatings. Exceptions are of course the coating of temperature sensitive parts, where one skips heating. Parts are considered as temperature sensitive if they are not to be heated without damage to more than 650° K. The state of the art of conditioning for methods for the plasma assisted physical vapour coating of parts with wear resistant coatings has been described in the patents DE 3936550 and DE 104998. These two patents recommend putting under high vacuum and radiation heating. In the case of radiation, heating heat flows as a beam of infrared photons from a heater to the parts to be heated. A heater is a surface, whose temperature is higher than the temperature of the parts to be heated. The set point temperature is the temperature the parts should reach in the conditioning step. The different variants of plasma etching are not discussed being not a subject of this invention. All plasma etching methods used today are executed under high vacuum although one could conceive rough vacuum methods. Any physical vapour deposition can be considered as sequence of three processes, each of them being stationary in time, evaporation of components of the material that will form the coating in a suitable installation, called source, transport of these components that will form the coating and, if appropriate, gaseous components to the parts and conversion of these components on the surface of the parts to coatings with the required properties. Numerous forms of vapour sources are known and used today (see E. Bergmann and E. Moll op. cit. ). In the case of the physical vapour deposition of wear resistant coatings they are based either on sputtering or on arc evaporation. The evaporated components for forming the coating are transported to the parts by a free molecular flow or by means of an electrostatically and/or electromagnetically managed molecular flow. Thereby a mass flow of components of the material constituting the coating is formed. The following transport configurations have been realized so far, each being specific to a certain equipment and vapour source configuration: A flat source facing a flat part: Not suitable for wear protection coatings, where most parts are complex shaped. Mainly used in load-lock systems. Flat sources on a cylinder and a radial mass flow to the parts in the center of the cylinder. Moving point sources or rod sources in the center and radial mass flow towards the components on the cylinder surface. Point source in the center or on the bottom and radial flow to the substrates mounted onto the segment of a sphere. Flat sources are evaporation installations where the components of the material that will form the coating are emitted from an extended surface and where this surface is flat. Point sources are evaporation installations where the components of the material, that will form the coating, are emitted from a surface whose extension, typically in the range of 0,001 - 0,003 m, is very small compared to the vessel surface. Rod sources are evaporation installations where the components of the material, that will form the coating, are emitted from a rod. State of the art methods for the plasma assisted high vacuum physical vapour coating of parts with wear resistant coatings use transport configurations with either parallel heat and mass flows or heat and mass flows, that are coradial, coradial means being both in the radial direction of the same cylinder. The reasons for the restriction to these transport configurations are considered evident. Under high vacuum heat flow in the form of a photon beam as well as mass flow of the components, that will form the coating, in the form of a molecular flow are directed flows. This sequential combination requires therefore a parallel or coradial direction of heat flow and mass flow, to assure equal uniformity of exposure of the parts to both flows. Since heat transport in high vacuum is limited to photons, the state of the art is limited to radiation heating. The use of radiation heating brings many disadvantages in the practical application of these methods. Heat transport from the radiating surfaces to the core of the parts is poor, because it depends strongly on the surface finish of the parts and non-uniform temperatures can not be avoided: shading leaves some parts too cold, intensive irradiation overheats some parts. These problems arise from the fact that the heat flow associated with radiation depends very strongly on the temperature difference between heater and part to be heated. The heat flow is proportional to the 4th power of this temperature difference. Figure 1 shows the temperature evolution of three parts with different weight in different areas of an equipment with conditioning according to the state of the art. Curve (a) was measured with a twist drill made from H2 high speed steel, diameter 6 mm, fixed at half-height of the part carrier on a spindle at its periphery, loaded in a quiver executing a further rotation around its axis. Curve (b) was measured with a milling cutter, diameter 150 mm, length 200 mm, also fixed at half height of the part carrier on a spindle but free standing on a holder plate. Curve (c) was measured with a forming punch, diameter 300 mm, sitting in the center of the part carrier. The temperature of the heater was identical in all three experiments, namely 1270 °K. The target temperature for all three parts was 770 °K. The milling cutter reached this temperature after 2,5 hours. By that time the temperature of the twist drill had long exceeded his tempering temperature - 810 °K, the drill had softened and was scrap. The punch never reached his target temperature. This lower than specified temperature of the punch during the subsequent coating step affected the adhesion of the plasma assisted coating adversely. In this experiment a heater temperature largely exceeding the target temperature of the parts had been chosen. In this way the light parts, respectively the parts closer to the heater, did exceed the target temperature and had approached the temperature of the heater, while heavy parts, respectively parts at a larger distance from the heater had, remained significantly below the target temperature. If one sets a small difference between heater temperature and target temperature, the heat flow becomes very small and the heating time excessively long. These problems prevent currently the profitable coating of heavy parts with plasma assisted physical vapour deposition by job coaters. They also require from the operators of such equipment great skill in arranging mixed batches. The effect of the parallel or coradial arrangement of heat and mass flows leads to a heating of the part of similar non uniformity than the coating. The subject of the invention is a method for the plasma assisted high vacuum physical vapour coating of parts with wear resistant coatings characterized in that the sequence of steps following the closure of the chamber consists of: creation of fine or rough vacuum, creation of an atmosphere of protective gas at reduced pressure, this pressure being superior to the fine or rough vacuum created in the preceding step, and heating the parts to be coated by transporting said protective gas from heaters to the parts and back to the heaters by means for creating gas flows. The problems of the state of the art coating processes can be solved if instead of photons gas atoms and/or molecules are used as energy carriers. This requires a gas flow from the heaters to the parts. The principle is known since centuries in bakeries and was introduced in the baking stoves in households in the last two decades. A radiation stove can only bake breads of equal or similar size, a convection stove is suitable for the simultaneous baking of biscuits and cakes. But the high vacuum of the evaporation process has a low gas density, which would make heating by gas extremely inefficient. This problem is overcome with a novel procedure. The chamber with the parts to be coated is first pumped down to fine vacuum, then refilled with a protective gas to a rough vacuum, which will be used for the conditioning by heating. Only when heating is completed will the chamber be put under high vacuum and the coating process will be continued either by the conditioning step of plasma etching or by high vacuum deposition. In principle any gas that will not react with the parts at the target temperature can be used as a protective gas. Mixtures of noble gases, nitrogen and/or hydrogen have proven well suited, in particular, mixtures, where nitrogen or helium are the main components. Furthermore, we found that configurations, where the heat flow is approximately orthogonal to the mass, flow lead to particularly good results. Heating and cooling can be made much more uniform for most shapes of parts. The fact, that the method claimed makes heating more uniform than coating is not a disadvantage. The heating with protective gases uses electrical energy and consists of a heater and a blower, that transports the protective gas from the heaters to the parts and back to the heaters. In the art of furnace design two variants of realization are known: In the case of external heating the blower sucks in the gas cooled down by the contact of the parts from the chamber and blows it over a heater, from where it again will flow across the chamber. Inlet and outlet fittings determine the heat flow. In the case of an internal heating, conditioning space and heater space are separated by sheets incorporated in the chamber. A blower sucks the protective gas cooled down by the contact with the parts from the conditioning space and blows it over the heater in the heater space, from where it flows back into the conditioning space. Both spaces are part of one same chamber. Both variants of realization are state of the art for sintering furnaces but have never been proposed for use in the high vacuum vapour coating of parts with wear resistant coatings probably because they did not seem compatible with methods for the deposition of wear resistant coatings onto parts under high vacuum with physical vapour deposition. In the case of an external heating with protective gases the fine dust created continuously in the methods for plasma assisted high vacuum vapour coating of parts with wear resistant coatings would settle partly on the valve seats thereby making the chamber quickly unsuitable for high vacuum operation. In the case of an internal heating, motors that run in the chamber are used, because it seemed not possible to design high vacuum rotary feed-through compatible with the high rotation speeds of efficient blowers. Slowly rotating blowers do not produce a controlled gas flow. However since these motors run in the vacuum chamber emit copious amounts of gases they can not be used with methods of plasma assisted high vacuum vapour coating of parts with wear resistant coatings. A further object of this invention is therefore a blower linked to a magnetic transmission, which is a preferred device for protective gas heating in processes of plasma assisted high vacuum vapour coating of parts with wear resistant coatings. Similar considerations are valid for cooling. In this case the heater should be replaced by a gas/gas or gas/water heat exchanger. It is therefore a further object of the present invention to use the wall of the high vacuum vessel as a gas/water heat exchanger. A further part of the invention is the use of movable gas flow management sheets. The equipment for carrying out the process must comprise means for creating gas flows, preferably a blower, which in the preferred embodiment is driven through a magnetic clutch. The equipment comprises gas flow management sheets, which in the preferred embodiment, also serve as heat flow barriers. They can be moved in a way to create a different gas flow during heating than during cooling. It was established that the process efficiency increases if the heaters are positioned close to the blower. Close means, for example a disposition within the range of 50 - 200 mm. It will not be possible to place all the heating elements in this range for every equipment and installed heating power. What matters above all is the installation in the proximity of the blower intake. This disposition is made easy by the use of the magnetic clutch. Since with a magnetic clutch there are no lubricated parts in the vicinity of the blower, a higher temperature of the blower body can be tolerated. The following is the preferred sequence of process steps for the method claimed. After closing the high vacuum coating equipment, a two stage mechanical pump creates a fine vacuum. During this process step no high vacuum pumps are used (the terms and definitions used correspond to W. Pupp, H. K. Hartmann Vakuumtechnik, Grundlagen und Anwendungen, Carl Hanser Verlag München 1991). A pressure of 5 - 10 Pascal is created. As soon as this pressure is reached, a valve is opened bleeding protective gas into the chamber. If the pumping unit does not have sufficient pumping power in the range of 5 - 20 Pascal the following process sequence can be taken as an alternative. One creates only a pressure in the range of 100 - 1000 Pa., this corresponds to a rough vacuum and provides ample rinsing of the equipment with protective gases, before the parts reach too high a temperature. In both versions a protective gas pressure of at least 0.01 bar is established. In the case, where one wants to coat ground shank type tools, a pressure in the range of 0,8 - 1 bar is used. If a more intense degassing of the parts is sought, for example with polished or honed tools, we found it advantageous to work at lower pressure at the expense of longer heat-up times. As soon as the target protective gas pressure is reached, the blower is put in operation creating a strong flow of protective gas. The flow of protective gas is taken in through heaters placed in the vicinity of the blower. A heat flow from the heaters to the parts is created. The direction of the heat flow corresponds to the direction of the gas flow. Very unexpectedly indeed, we found that it is very advantageous if, during heating in the space where the parts are loaded, the heat flow is essentially orthogonal to the mass flow, which will take place during high vacuum coating. By orthogonality of the two flows we mean that the vector of the total gas flow 17 and the vector of the total mass flow 18 form an angle, that is essentially a right angle. Figure 2 explains how this rule must be applied. Because of flow deviations by the parts and whirls, the gas flow and therefore the heat flow may of course have locally 14 another even an opposite direction. But the majority of the flow lines 15 and therefore the macroscopic flow 17 will have a single and unique direction whose meaning is evident for a skilled person. Similar deviations have to be taken into account for the mass flow of the plasma assisted high vacuum evaporation processes. In these processes the mass flows are essentially directed 16 pointing away from the vapour sources. Since part of the vapour will be ionized, some electrostatic deviation will occur. Despite these deviations, the application of the rule will be evident to anybody skilled in the art: It is a clear rule for the disposition of vapour sources, parts to be coated, and the disposition of blower and gas flow direction sheets. The details depend on the vapour sources selected and will be further detailed by the following two examples. If one chooses planar magnetrons and a cylindrical vessel, one will incorporate the vapour sources in the cylinder side wall and reserve the chamber center for the parts just the way described e.g. in US 4 877 505. In this case one should use the faces of the cylinder for the blowing (sucking) blower respectively the protective gas recirculation (feed) device. If one chooses a rod as vapour source as described in EP 508612, one will dispose the parts around this rod. In this case one will either use the two lateral walls of a rectangular chamber or two facing cylinder segments of a cylindrical chamber for blower and protective gas recirculation (feed) device. The reasons for this unexpected effect of improvement with orthogonal flows appear to be the following- although no completely satisfactory answer has been found so far. Shank type tools, which constitute the bulk of parts to be coated. are usually loaded with their axis of revolution normal to the mass flow. If then the heat flow is parallel or coradial, the heat intake of the parts is limited to the cylindrical half-face exposed to the heat flow. With an optimally tuned heating, the surface of this half-face will immediately reach the target temperature. Heat will then diffuse from this surface to the bulk of the tool. The form of the shank type tools will cause an orthogonal heat flow to be taken in on the whole cylinder face, whose surface will reach immediately the target temperature with an optimally tuned heating. In the framework of the validity of this simple model, one gets half the heating time for orthogonal flow when compared with parallel or coradial flow. When the parts have reached the target temperature for the parts, the conditioning step heating is terminated. The energy input into the heaters is shut off. After that, the blower drive is shut down. All the plasma etching steps currently used are carried out under high vacuum (see E. Bergmann und E. Moll op. cit.). Under these circumstances the bleeding gas inlet will be closed after the shut down of the blower and the chamber will be pumped down to high vacuum with the high vacuum pumping device. High vacuum pumping devices are usually of the three stage type. A significant advantage of the method claimed when compared with state of the art methods is the fact that, for a given high vacuum pumping device, the time that elapses until high vacuum is reached is considerably shortened. In the state of the art methods the equipment is first pumped down to high vacuum before the conditioning step heating is started. In this case high vacuum must be produced in a cold or warmed up chamber. Usual high vacuum evaporation practice consists in warming the chamber up to 45 ° C with water. The installation for this conditioning of the walls is significant (usually 10 - 20 % of the equipment costs). But this practice ignores the fact that equipment for the plasma assisted high vacuum coating with wear resistant coatings is run in a different way than other high vacuum coaters. The thickness of the coatings deposited is relatively high, in the range of 2 - 10 µm for each batch. Since the parts are usually shank type or complex shaped, this coating thickness on the parts corresponds to a coating thickness deposited on the walls of 6 - 30 µm per batch. The usual applications of high vacuum deposition processes, from which the state of the art practice had been taken, deposit 0,1 µm on flat parts. The pump down in a high vacuum equipment is determined by two different processes (Pupp und Hartmann op. cit.). Pumping down to fine vacuum is achieved by removing the gas filling the volume of the chamber. The transition from fine vacuum to high vacuum requires the removal of the gas adsorbed on the walls and surfaces. This leads to problems particular for equipment for plasma assisted high vacuum deposition of wear resistant coatings because of the large coating build-up on the walls involved. Since the kinetics of gas desorption are governed by Arrhenius' law, an economic operation requires for this application a transition from fine vacuum to high vacuum under high temperature. This fact was overlooked in the state of the art methods derived from the practice of high vacuum coating of other parts. The choice of a high temperature for the transition from fine vacuum to high vacuum, which is a subject of the present invention, solves another problem which is characteristic for processes where the heating step is carried out under protective gas. Chambers for such processes are equipped with protection shields between the chamber walls and the parts for reasons that will be detailed in the section of this patent description, where the equipment is discussed in detail. This requirement multiplies the surfaces covered with gas and would therefore handicap the economic operation of the equipment subject of the present invention, had we not found a method where the transition from fine vacuum to high vacuum takes place out under high temperature. When high vacuum has been achieved, the selected plasma etching process is carried out followed by the selected high vacuum vapour deposition process. Figure 1 shows the heat-up of three different parts and the comparison with the state of the art, whose results have already been discussed. Curve (d) was measured with a twist drill, diameter 6 mm, mounted on the periphery of a rotating plate at half the height of the substrate carrier. Curve (e) shows the result for an end mill, diameter 150 mm, length 200 mm, also loaded on the periphery of the substrate carrier, but standing on the carrier plate. Curve (f) was measured with a forming punch, diameter 300 mm, loaded on the center of the substrate carrier. The temperatures of the heaters were the same in all three cases, namely 1170 °K. The target temperature for the parts was 770 ° K. After 40 minutes even the most heavy part had reached the target temperature. None of the parts was overheated. After the high vacuum vapour deposition process(es), the parts are subjected to a further conditioning step, the cooling. Cooling is a conditioning step by which the temperature of the parts is brought down from the temperature after the coating step to another target temperature, the venting temperature. In the process of the present invention protective gas is used again for the heat transport in this conditioning step. For this purpose the chamber is back-filled again with protective gas up to a pressure between 0,5 and 1 bar. Following this, the blower is again put into operation and brought up to a rotating speed of at least 500 revolutions per minute, preferably to a rotation speed of 2000 - 2500 revolutions per minute. This is also the preferred rotation speed for heating. A change in the gas flow management device will now direct the flow along the chamber wall. As a consequence the chamber wall cools down the gas to the temperature close to the chamber wall cooling water. This cooled down gas is then blown or sucked over the parts by the blower. During this pass the gas cools down the parts picking up heat. To avoid overheating of the chamber cooling water during this process step, the blower rotational speed is regulated at least part of the time in the following way: A temperature sensor measures continuously the temperature of the chamber cooling water and transmits a corresponding signal, the actual value, to the regulating unit. This unit compares the signal with the set value, that corresponds to a threshold of the temperature. This threshold temperature will depend on the design of the chamber water cooling unit. It will be in the range of 60 - 95 °C. When the signal reaches the threshold value, the regulating unit will reduce the rotation speed of the blower. When the signal is inferior to the threshold by a value corresponding to 5°C, the regulating unit starts increasing the rotation speed of the blower, until either the signal reaches again the threshold value or the rotation speed the set maximum. When the parts reach the venting temperature, the chamber is brought back to atmospheric pressure by opening the nitrogen bleeding valve followed by an opening of the air venting valve or simply by opening the air venting valve. Figure 2 shows a preferred embodiment of the invention. The vacuum vessel 1 is a cylindrical chamber 21 having for dimensions a diameter of 600 mm and a height of 800 mm. The relation between height and diameter reflects in the usual way the dimensions and quantities of the parts to be coated. On the chamber wall several rectangular cathodic arc evaporators 13 are mounted. The cathodic arc evaporators are of the externally mounted type of the state of the art design as it is described e.g. in DE 126040. The parts 12 are the parts to be coated by plasma assisted high vacuum physical vapour deposition. The holders carrying the parts consist of a carrying plate 11 with a feed-through 23 and a drive for the carrying plate which is not shown. Further details concerning the substrate holder can be taken from US 4 485 759. The vessel is evacuated through a pumping port 2. It is fed with protective gas, a mixture of 10 volume % of hydrogen and 90 volume % of nitrogen through the valves 5. The admission duct for the protective gas and the reactive gases for the plasma assisted high vacuum vapour deposition process is designated by 6. The chamber lid is equipped with an axial blower 3, connected to a motor 20 by an axis 19 and a magnetic clutch 4. Details of the magnetic clutch are shown in figure 3. The heating elements are disposed in the immediate neighbourhood of the blower. They heat up the protective gas before it is sucked in by the blower. The preferred embodiment allows the placing of the heating element in the top of the chamber in a space, where the distance to the fan ranged from 30 to 300 mm. The gas management sheets 9 and 8 direct the gas heated or cooled by the parts from the chamber bottom back to the chamber top. In the embodiment shown the lower gas management sheet was simply a dumb bell shaped vessel cylinder face of diameter 550 mm and 2 mm thickness. The two vertical sheets are cylinders with rectangular openings in the sections where the evaporator(s) is(are) fitted into the chamber wall. In the embodiment shown, their diameters were respectively 560 and 510 mm. The protection sheet 8 consists of a stack of three sheets. The chamber described therefore contained a total of five protection sheets between the parts and the chamber wall. One of the gas flow management sheets 8 can be moved to two positions opening or closing the channel 25 formed by sheets 8 and 9 to the protective gas flow. This is achieved by the shut off device 26. It is linked to a linear feed-through 10 connected to a lever 27, whose action produces a movement of the sheet 8 during the transition from the conditioning step heating to high vacuum or during the transition from high vacuum to the deconditioning step cooling or any time in between these two transitions. Other designs like chain drives or pneumatic cylinders are of course equally suitable. Other movements like rotations or opening or closing of traps can replace the lifting. During the conditioning step heating, the gas management sheets are positioned in a way to produce a preferred flow of the protective gas between sheets 8 and 9 through the heating channel 25. During the deconditioning step cooling, the two gas management sheets are in a position, that forces the protective gas flow through the cooling channel 24 formed by the chamber wall 21 and the gas management sheet 8. This cooling channel 24 can be equipped with cooling fins 22 to enhance the heat exchange between the chamber wall 21 and the protective gas. A preferred embodiment of the magnetic clutch is shown in figure 3. A pot with crossbeams 38 carrying two rolling bearings 29 is connected to a chamber flange 36. The pot contains the driven part of the clutch. The bearings support the blower shaft 19 which carries firmly linked to it a plate 33 separated from the chamber flange surface by a gap not exceeding 3 mm but superior to 0,2 mm. The periphery of this plate is connected to a ring 31, the driven ring. This ring consists either of permanent magnet material which is magnetized axially or of bars and fins of permanently magnetic material mounted in an appropriately designed yoke. The other side of the chamber flange is connected through a seal 37 with a pot 34, which carries the driving part of the clutch. The pot is equipped with at least one rolling bearing 29, whose inner ring is riveted to or coinciding with the shaft 28 of the motor, which is not shown. The shaft carries a yoke made from soft iron or another appropriate ferromagnetic material like a nickel or cobalt alloy. The yoke is linked to a ring of permanently magnetized material 30 which is designed in the same way as the driven ring 31. The design of the whole ensemble is executed in a way to maximize the attractive force between the driving and the driven parts of the clutch. In a preferred embodiment the yokes and the shapes of the permanent magnet material are such that the gap of 0,2 - 3 mm between the flange and the plate 33 and the thickness of the flange correspond essentially to the total air gap of the magnetic circuit. The mechanical design of the flange should be such that the thickness of the membrane 39 in the gap does not exceed 2 mm. This thin membrane has to be properly supported to withstand the pressure of 1 bar. A preferred realization of the invention uses rings made from permanently magnetic material that are alloys of rare earths with cobalt or iron. A further preference in the realization of the embodiment of the invention uses alloys made essentially from the elements neodymium, iron and boron. The pot 34 is closed by a membrane made from stainless steel 39, whose thickness must not exceed 2 mm.

Claims: Method for the plasma assisted high vacuum vapour coating of parts with wear resistant coatings comprising at least the process steps of conditioning and coating and where the process step conditioning comprises a conditioning step heating characterised in that the sequence of steps following the closure of the chamber consists of: creation of fine or rough vacuum, creation of an atmosphere of protective gas at reduced pressure, this pressure being superior to the fine or rough vacuum created in the preceding step, and heating the parts to be coated by transporting said protective gas from heaters to the parts and back to the heater by means for creating gas flows. Method according to claim 1, characterised in that protective gas is used for the heat transport in the conditioning step heating. Method according to claim 1, comprising, after the process step high vacuum vapour coating, the deconditioning step cooling, characterised in that a protective gas is used for the heat transport in the conditioning step cooling. Method according to any one of the preceding claims, characterised in that heat and mass flow are essentially orthogonal one to each other. Method according to any one, of the claims 1 to 3 characterised in that a protective gas circulation is achieved with a blower. Method according to claim 1, characterised in that the conditioning step heating is followed either by a further conditioning step carried out under fine or rough vacuum, or that high vacuum is created in the chamber after the conditioning step heating. Method according to any one of the claims 1 to 3, characterised in that the pressure of the atmosphere of protective gas is superior to 0,01 bar. Method according to any one of the preceding claims, characterised in that the protective gas is helium or nitrogen. Method according to claim 1, characterised in that during conditioning step heating the protective gas is repeatedly renewed. Method according to claim 5, characterised in that the blower is rotated with a speed exceeding 500 revolutions/minute. Method according to claim 5, characterised in that the blower is rotated with a speed exceeding 2000 revolutions/minute. Equipment for the plasma assisted high vacuum vapour coatinq of parts with wear resistant coatings which comprises at least a high vacuum chamber, evaporation sources, substrate holders for the creation of a gas flow and characterised by means for transporting a protective gas from heaters to the parts to be coated and back to the heaters. Equipment according to claim 12, characterised in that said means for transporting a protective gas contain a blower (3). Equipment according to claim 12, characterised in that at least one or several protective shields (8) is disposed in the space between chamber wall (21) and the parts (12) to be coated. Equipment according to claim 12, characterised in that it is equipped with gas flow management sheets (9). Equipment according to claims 14 and 15, characterised in that at least part of the protective shields do also form gas flow management sheets. Equipment according to claim 15, characterised in that the position of the gas flow management sheets can be changed. Equipment according to claim 13, characterised in that the blower (3) is linked to its driving motor by a magnetic clutch (4), whose driven part is separated from the driving part by the high vacuum chamber wall (21). Equipment according to claim 12, characterised in that heating elements are disposed in a space adjacent to the blower. Equipment according to claim 18, characterised in that the chamber wall is exclusively used to cool the protective gas. Equipment according to claim 18, comprising driving and driven subassemblies, characterised in that one of the two subassemblies is closed vacuum tight by a membrane (39) made from stainless steel. Equipment according to claim 21, characterised in that the thickness of the membrane does not exceed 2 mm.

Inventors: BERGMANN ERICH, BERGMANN, ERICH
Applicants: BERGMANN ERICH, BERGMANN, ERICH
Application year: 1996
Main classification: C23C14
IPC codes: C23C14, H01J37