METHOD FOR THE MANUFACTURE OF A ROLL FOR USE IN THE PRODUCTION OF PAPER, ROLL FOR USE IN THE PRODUCTION OF PAPER, AND COATING FOR A ROLL FOR USE IN THE PRODUCTION OF PAPER

Abstract: The invention concerns a method for the manufacture of a roll for use in the production of paper, in which method the roll is coated by means of thermal spraying. The method comprises the following steps: onto the coating (12) of the roll which has been produced by means of thermal spraying, a sealing-agent solution is spread to seal the pores (13) in the coating (12), the sealing-agent solution is allowed to be absorbed into the pores (13) in the coating (12), the roll is heated in order to eliminate the water from the sealing-agent solution, on elimination of the water, the sealing-agent solution crystallizes in the pores (13) in the coating (12), and the roll is allowed to cool. Further, the invention concerns a roll for use in the production of paper, which roll comprises a frame (10) and a roll coating (12), which coating (12) has been produced by means of thermal spraying. The coating (12) has been sealed by means of crystals formed out of a sealing-agent solution on elimination of water. Also, the invention concerns a coating for a roll for use in the production of paper, which coating (12) has been produced by means of thermal spraying, and in which coating (12) there are pores (13). In order to seal (12) the coating, a sealing agent (16) has been crystallized in the pores (13) in the coating (12).

Description: Method for the manufacture of a roll for use in the production of paper, roll for use in the production of paper, and coating for a roll for use in the production of paper The invention concerns a method for the manufacture of a roll for use in the production of paper, in which method the roll is coated by means of thermal spraying. Further, the invention concerns a roll for use in the production of paper, which roll comprises a frame and a roll coating, which coating has been produced by means of thermal spraying. Also, the invention concerns a coating for a roll for use in the production of paper, which coating has been produced by means of thermal spraying, and in which coating there are pores. As is well known, earlier the only alternative for the centre roll in the press section of a paper machine was a rock roll, which was made of granite. The popularity of granite was based on its surface properties, which produced controlled separation of the paper web from the rock face, and, moreover, granite tolerates the abrading effect of a doctor very well. However, granite has certain drawbacks. Being a natural material, its properties show variation, and internal flaws in granite and its tendency of cracking form a series obstacle for its use in some applications. This is why, to-day, as the centre roll of the press section of a paper machine, a coated roll is used very frequently, in particular a roll coated with an oxide coating. As is well known, in the production of paper, coated rolls are also used in a great variety of other applications, for example as press rolls, suction rolls, and as rolls of calenders and supercalenders. Onto the various rolls employed in the production of paper, the coating can be added in a number of different processes of manufacture. One important process for adding the coating onto a roll is thermal spraying, in which the problem has, however, occurred that a certain degree of porosity has tended to remain in the roll coatings. This tendency occurs in particular in coatings prepared from oxide ceramic by thermal spraying, because oxide materials are poorly melting. Oxide coatings are, however, highly suitable roll coatings for applications in which requirements are imposed concerning separation of the paper web, resistance to wear, resistance to corrosion, doctoring, and keeping clean. Such applications are, for example, the centre roll in a press section of a paper machine and the rolls in calenders. It has been one of the problems in thermally sprayed roll faces that the pores in the roll face are readily filled with contaminations occurring in connection with the manufacture of paper, for example pitch, or pastes contained in recycled pulps. When the pores in the roll coating are contaminated, the properties of the coating can be changed and, moreover, there is the risk that the contaminations/moisture break the boundary faces between the pores, in which case the coating is also worn by cracking and splitting. It is one prior-art application for sealing the pores in the coatings that so-called sealing agents are made to penetrate into the porous face. One prior-art application of such a sealing agent consists of thermosetting plastics which are composed of two or more components and which have a low viscosity when not solidified. In roll faces sealed in this way, problems have, however, arisen from the fact that the suitability for doctoring is deteriorated, because the plastic face tends to become smooth. Moreover, the smoothing may cause problems of runnability, because the properties of separation of paper are also changed. Thus, the object of the present invention is to suggest a solution which eliminates or at least minimizes the problems described above and arising from the porosity of the roll faces prepared by means of thermal spraying. In view of achieving the objectives stated above and those that will come out later, the method in accordance with the invention is mainly characterized in that the method comprises the following steps: onto the coating of the roll which has been produced by means of thermal spraying, a sealing-agent solution is spread to seal the pores in the coating, the sealing-agent solution is allowed to be absorbed into the pores in the coating, the roll is heated in order to eliminate the water from the sealing-agent solution, on elimination of the water, the sealing-agent solution crystallizes in the pores in the coating, and the roll is allowed to cool. On the other hand, the roll in accordance with the invention is mainly characterized in that the coating has been sealed by means of crystals formed out of a sealing- agent solution on elimination of water. Further, the roll coating in accordance with the invention is mainly characterized in that, in order to seal the coating, a sealing agent has been crystallized in the pores in the coating. According to the invention, the porous roll coating is sealed by means of a ceramic sealing agent, in particular by means of a phosphate sealing agent. According to the invention, the ceramic sealing, in particular phosphate sealing, can be carried out, for example, so that onto the coated roll Al(OH) 3 -H 3 PO 4 solution is spread. The solution is allowed to be absorbed into the pores in the coating during a certain period of time, for example twelve hours, after which the temperature of the roll is raised slowly and successively to a final temperature of 200...400 °C, during which heating water is eliminated from the solution. Owing to the elimination of water, the solution crystallizes in the pores in the coating as phosphate compounds of aluminum, for example AlPO 3 , AlPO 4 , etc. It is a second, alternative mode of penetration of the phosphate sealing agent into the porous coating that, in stead of the Al(OH) 3 -H 3 PO solution mentioned above, a mixture of phosphoric acid, for example 85-% orthophosphoric acid H 3 PO 4 and finely divided ceramic powder or powders of a particle size, for example, smaller than 3 μm, is used. Materials suitable for this purpose are, for example, Al 2 O 3 and Cr 2 O 3 . The ceramic powder is dissolved into the phosphoric acid, whereby a solution is formed, which is made to penetrate into the porous face of the roll by absorbing during a period of time long enough, after which water is eliminated during heating, whereby aluminum phosphate and/or chromium phosphate is/are formed. After the treatment of the coating mentioned above, any extra phosphate that may remain on the roll face is wiped away, for example, with silicon carbide paper. The good properties of the phosphate sealing are based on the fact that the sealing agent blocks the pores and, moreover, the phosphoric acid that is included reacts with the oxide material in the coating and "glues" said material together, as a result of which the wear by means of cracking and splitting is also excluded. The applicant has carried out experiments in order to find out the advantages of the sealing described above, and in the experiments that were carried out the following advantages were established: Sealing of the roll coating with aluminum oxide increased the microhardness of the coating by about 250 HV03 units (Vickers hardness measurement with a weight of 0.3 kilogram), and sealing with chromium oxide by about 300 HV03 units, and with zirconium oxide by about 300 HV03 units. The increased microhardness and the ("gluing") effect of phosphoric acid increase the wear resistance of the coating. In an abrasive wear test, the wear resistances of the coatings were improved with aluminum oxide even to ten-fold, with chromium oxide to five-fold, and with zirconium oxide to eight-fold. Moreover, in electrochemical corrosion tests it was noticed that the capacity of corrosion protection of the coating was improved by up to five decades. Moreover, the sealing increases the resistance of the coating to delamination as well as the property of remaining clean, because contaminations cannot penetrate into the pores in the coating. Besides the exemplifying embodiments described above, for sealing it is also possible to use, for example, a mixture of phosphoric acid and very finely divided oxide ceramic, the finely divided oxide ceramic being partly dissolved in the phosphoric acid, and the sealing of the roll coating is carried out by means of the methods described above. In the following, the invention will be described in more detail with reference to the figures in the accompanying drawing, wherein Figure A is a schematic sectional view in part of a prior-art roll provided with a roll coating, and Figure 1 is a schematic sectional view in part of a roll coated and sealed in accord¬ ance with the present invention. As is shown in Fig. A, the roll frame 10a is provided with an adhesion layer Ila, onto which the ceramic layer 12a has been applied. The face of the ceramic includes pores 13a and cavities 14a between them. In such a case, it is possible that the roll coating splits along a crack 15a that is formed. Fig. 1 is a schematic sectional view in part of a sealed roll coating in accordance with the invention, and in the figure the roll frame is denoted with the reference numeral 10, an adhesion layer, if any, with the reference numeral 11, and the coating layer with the reference numeral 12. The pores 13 in the coating have been sealed with a sealing agent 16, as a result of which contaminations cannot penetrate into the pores 13 and a crack cannot proceed along the cavities between the pores. In the method in accordance with the present invention, the roll coating 12, which has been applied onto the roll frame, either onto an adhesion layer 11 or directly onto the roll frame 10, by means of thermal spraying, is sealed so that a ceramic sealing agent, which is in the form of a solution of an acid, is made to penetrate into the roll coating. The solution of sealing agent is absorbed into the pores in the coating during a certain period of time, for example twelve hours. After this the temperature of the roll is raised slowly and successively to a final temperature of about 200...400 °C. Owing to this heating, water is eliminated out of the solution, in which connection the solution crystallizes in the pores in the coating as com¬ pounds of the ceramic, and the accompanying acid glues the ceramic material together. After this the roll is allowed to cool, whereupon any extra material is wiped away from the roll face by means of a suitable method. The roll coating 12 may be an oxide coating, for example Y 2 O 3 , Al 2 O 3 , Cr 2 O 3 , ZrO 2 , SiO 2 , MgO, TiO 2 , CeO 2 , or any other roll coating prepared by thermal spraying, for example a mixture of oxide and carbide or of oxide and nitride. As the ceramic sealing agent, preferably phosphate sealing agents are used, and also fluorophosphoric acid (H 2 PO 3 F) and chromic acid are suitable for sealing agents. According to a preferred exemplifying embodiment of the invention, the thermally sprayed roll coating is sealed by means of a phosphate sealing agent, in which connection Al(OH) 3 -H 3 PO solution is spread onto the coated roll. The solution is allowed to be absorbed into the pores in the coating for twelve hours, and after this the temperature of the roll is raised slowly and successively to a final temperature of 200...400 °C, during which process water is eliminated from the solution. As a result of the elimination of water, the solution crystallizes in the pores in the coating as phosphate compounds of aluminum (AlPO 3 , AlPO , etc.). According to a second preferred exemplifying embodiment of the invention, in stead of the Al(OH) 3 -H 3 PO 4 solution, a mixture of phosphoric acid, for example 85-% orthophosphoric acid H 3 PO and finely divided ceramic powder or powders of a particle size, for example, smaller than 3 μm, is used. Materials suitable for this purpose are, for example, Al 2 O 3 and Cr 2 O 3 . Out of the phosphoric acid and the ceramic powder/powders, a solution is formed, which is absorbed into the pores in the coating. When the roll is heated slowly and successively to a temperature of 220...280 °C, water is eliminated from the solution. Owing to the elimination of water, the solution crystallizes in the pores in the coating as phosphate compounds of aluminum and/or chromium. Above, the invention has been described with reference to some preferred exemplify¬ ing embodiments of same only, and the invention is, however, not supposed to be strictly confined to the details of said embodiments. Many variations and modif ica- tions are possible within the scope of the inventive idea defined in the following patent claims.

Claims: Claims 1. A method for the manufacture of a roll for use in the production of paper, in which method the roll is coated by means of thermal spraying, characterized in that the method comprises the following steps: onto the coating (12) of the roll which has been produced by means of thermal spraying, a sealing-agent solution is spread to seal the pores (13) in the coating (12), the sealing-agent solution is allowed to be absorbed into the pores (13) in the coating (12), the roll is heated in order to eliminate the water from the sealing-agent solution, on elimination of the water, the sealing-agent solution crystallizes in the pores (13) in the coating (12), and the roll is allowed to cool. 2. A method as claimed in claim 1, characterized in that, in the method, any extra sealing agent that has remained on the face of the roll is wiped away. 3. A method as claimed in claim 1, characterized in that a phosphate sealing agent is used as the sealing-agent solution. 4. A method as claimed in claim 3, characterized in that Al(OH) 3 -H 3 PO solution is used as the phosphate sealing agent. 5. A method as claimed in claim 3, characterized in that a mixture of phosphoric acid and ceramic powder/powders is used as the phosphate sealing-agent solution. 6. A method as claimed in claim 5, characterized in that, as the phosphoric acid, 85-% orthophosphoric acid is used, and as the ceramic powder Al 2 O 3 and/or Cr 2 O 3 materials are used. 7. A method as claimed in any of the preceding claims, characterized in that the roll is heated to a temperature of 200...400 °C. 8. A method as claimed in any of the preceding claims, characterized in that, in the method, the coating of the roll takes place onto an adhesion layer (11) placed on the roll frame (10). 9. A method as claimed in any of the preceding claims, characterized in that the roll is coated with an oxide ceramic material. 10. A roll for use in the production of paper, which roll comprises a frame (10) and a roll coating (12), which coating (12) has been produced by means of thermal spraying, characterized in that the coating (12) has been sealed by means of crystals formed out of a sealing-agent solution on elimination of water. 11. A roll as claimed in claim 10, characterized in that the sealing-agent solution consists of a phosphate sealing agent. 12. A roll as claimed in claim 11 , characterized in that the phosphate sealing agent is a mixture of phosphoric acid and ceramic powder/powders. 13. A roll as claimed in claim 12, characterized in that the particle size in the ceramic powder/powders is smaller than 3 μm. 14. A roll as claimed in claim 11, characterized in that the phosphate sealing agent consists of Al(OH) 3 -H 3 PO 4 solution. 15. A roll as claimed in any of the preceding claims, characterized in that the coating (12) consists of a ceramic material. 16. A roll as claimed in any of the preceding claims, characterized in that aluminum phosphate and/or chromium phosphate has/have crystallized in the pores in the coating (12). 17. A roll as claimed in any of the preceding claims, characterized in that there is an adhesion layer (11) between the roll frame and the coating (12). 18. A coating for a roll for use in the production of paper, which coating (12) has been produced by means of thermal spraying, and in which coating (12) there are pores (13), characterized in that, in order to seal (12) the coating, a sealing agent (16) has been crystallized in the pores (13) in the coating (12). 19. A coating for a roll as claimed in claim 18, characterized in that ceramic compounds have been crystallized in the pores in the coating (12). 20. A coating for a roll as claimed in claim 18 or 19, characterized in that phosphate compounds (16) of aluminum and/ or chromium have been crystallized in the pores (13) in the coating (12).

Inventors: TELAMA ARI, TELAMA, ARI
Applicants: VALMET CORP, VALMET CORPORATION
Application year: 1996
Main classification: D21F3
IPC codes: B05D7, C23C4, D21F3