Ferritic stainless steel sheet having less planar anisotropy and excellent anti-ridging characteristics and process for producing same

Abstract: A ferritic stainless steel sheet having less planar anisotropy and excellent anti-ridging characteristics is disclosed. The sheet includes not more than about 0.02 wt% of C, about 0.01 - 1.0 wt% of Si, about 0.01 - 1.0 wt% of Mn, not more than about 0.08 wt% of P, not more than about 0.01 wt% of S, about 0.005 - 0.30 wt% of Al, about 11 - 50 wt% of Cr, about 0.1 - 5.0 wt% of Mo, not more than about 0.03 wt% N, with the contents of C and N satisfying the relations: about 0.005 wt% ≤ (C + N) ≤ about 0.03 wt%, and (C/N) < about 0.6. The sheet also includes Ti in an amount to satisfy the relation: about 5 ≤ Ti/(C + N) ≤ about 30. The balance of the sheet includes Fe and incidental impurities, with the sheet having an X-ray integral intensity ratio (222)/(310) of not less than about 35 in a plane parallel to a sheet surface at a depth of 1/4 of the sheet thickness from the sheet surface. This ferritic stainless steel sheet may be produced by a method which includes hot rolling said steel having the above-described composition at a final pass reduction ratio during rough rolling of not less than about 40% and at a final finish rolling temperature of not more than about 750°C. The hot rolled sheet is subsequently annealed, cold rolled, and finish annealed.

Description: Field of the Invention This invention relates to a ferrite stainless steel sheet appropriate for use in facing materials of buildings, kitchen utensils, chemical plants, and water storage tanks, and more particularly relates to a ferrite stainless steel sheet (including steel strip) having less planar anisotropy and excellent anti-ridging characteristics, the invention including a method of production. Description of the Prior Art Stainless steel sheets have a beautiful surface and excel in resistance to corrosion and, therefore, are commonly used as facing materials for buildings, kitchen utensils, chemical plants, and water storage tanks, for example. Particularly, austenitic stainless steel has been widely used in such applications because it is superior to ferritic stainless steel in terms of press formability, ductility, and anti-ridging characteristics. In recent years, steelmaking technology for high purity steel production has advanced to the point where product steels can exhibit enhanced formability, etc. Thus, the feasibility of applying highly corrosion resistant, high purity ferritic stainless steel in applications conventionally dominated by austenitic stainless steel such as SUS 304 and SUS 316 has been investigated. These studies have been prompted by ferritic stainless steel's advantageously low susceptibility to stress corrosion cracking and its lower cost due to the lack of Ni, an expensive substance typically present in austenitic stainless steels. Ferritic stainless steel, however, has rarely been considered for use as a durable consumable material for which corrosion resistance is of primary importance. For ferritic stainless steel to be used more frequently, it must exhibit adequate planar anisotropy and additional improvements in workability. For the purpose of improving the workability of ferritic stainless steel, a method which lowers the (C + N) content of the steel is known in the art. JP-A-56-123,327 discloses a technique for optimizing the draft distribution and the annealing condition for a ferritic stainless steel which has incorporated therein such a carbon and nitrogen stabilized element such as Nb. JP-A-03-264,652 discloses a technique for improving the forming properties of a ferritic stainless steel such as elongation and r value (Rankford value) by adding carbon and nitrogen stabilized elements like Ti and Nb to the stainless steel, thereby controlling the texture of aggregation and heightening the X ray integral intensity ratio (222)/(200). Further, JP-B-54-11,770 discloses a technique for improving the cold workability of a ferritic stainless steel by decreasing the C and N contents and, at the same time, adding Ti. These known techniques, however, are directed chiefly to improving the r value and the ductility. While they are apparently effective in improving these properties, the product ferritic stainless steels exhibit large planar anisotropy and do not possess satisfactory anti-ridging characteristics. In applications like stamping that demand deep drawing ferritic stainless steel having improved planar anisotropy and anti-ridging characteristics would enhance the appearance and thus would advantageously reduce the polishing and other cosmetic work otherwise required. US-A-4 408 708 discloses ferritic stainless steels for preheater and reheater equipment applications. EP-A-0 675 206 describes ferritic stainless steel sheets having a small intra-face anisotropy and excellent anti-ridging characteristics. EP-A-0 727 504 describes a ferritic stainless steel sheet having a small planar anisotropy. SUMMARY OF THE INVENTION In light of these shortcomings of prior art ferritic stainless steels, an object of the present invention is to provide a ferritic stainless steel sheet having less planar anisotropy and excellent anti-ridging characteristics, as well as a method for producing the same. A further object of this invention is to provide a ferrite stainless steel sheet having a r value of not less than about 1.4, an elongation of not less than about 30%, a planar anisotropy, Δr, of not more than about 0.2 for the r value, a planar anisotropy, ΔEl, of not more than about 2.0% for the elongation, and an undulating height (which will be described below) of not more than about 10 µm, combined with excellent anti-ridging characteristics, and a method for producing the same. The present inventors have discovered that these objects are achieved by carefully controlling the chemical composition, rolling conditions, and annealing conditions of a ferritic stainless steel, thereby permitting the ferritic stainless steel to attain a unique texture of aggregation. To be specific, this invention has the following essential elements. A ferritic stainless steel sheet having less planar anisotropy and excellent anti-ridging characteristics in accordance with the invention comprises not more than 0.02 wt% of C, 0.01 - 1.0 wt% of Si, 0.01 - 1.0 wt% of Mn, not more than 0.08 wt% of P, not more than 0.01 wt% of S, 0.005 - 0.30 wt% of Al, 11 - 50 wt% of Cr, 0.1 - 5.0 wt% of Mo, not more than 0.03 wt% N, C and N satisfying the relations 0.005 wt% < (C + N) ≤ 0.03 wt% and (C/N) < 0.6. The ferritic stainless steel further comprises Ti in an amount which satisfies the relation 5 ≤ Ti/(C + N) ≤ 30, with the balance of the ferritic stainless steel being Fe and incidental impurities. The ferritic stainless steel has an X-ray integral intensity ratio (222)/(310) of not less than 35 in a plane parallel to the sheet surface at a depth of about 1/4 of the sheet thickness from a sheet surface. Preferably not less than 80% of the sheet in the thickness direction possesses an X-ray integral intensity ratio (222)/(310) within ±40% of the average X-ray integral intensity ratio (222)/(310) in the thickness direction. The invention also embodies a method of producing a ferritic stainless steel sheet, wherein a steel having the above-described composition is hot rolled with a final pass of the rough rolling reduction ratio of not less than 40% a final finish rolling temperature of not more than 750°C to produce a hot rolled sheet. The hot rolled sheet, which preferably possesses an X ray integral intensity ratio (222)/(310) of not less than 30 in a plane parallel to the sheet surface at a depth of about 1/4 of the sheet thickness from a sheet surface, is subsequently subjected to hot roll annealing, cold rolling, and finish annealing. Other elements and equivalents of this invention will become apparent from the following detailed description. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a graph showing the relation between planar anisotropy in terms of ΔEl and Δr and the C/N content ratio of the steel. Fig. 2 is a graph showing the relation between planar anisotropy in terms of ΔEl and Δr and the X-ray integral intensity ratio [α = (222)/(310)]. Fig. 3 is a graph showing the relation between the thickness proportion of the sheet which possesses an α [α = (222)/(310)] within about ±40% of the average α in the sheet thickness direction to the sheet thickness and planar anisotropy in terms of ΔEl and Δr. Fig. 4 is a diagram describing the method for determining the thickness proportion of the sheet which possesses an α [α = (222)/(310)] within about ±40% of the average α in the sheet thickness direction. DETAILED DESCRIPTION OF THE INVENTION This invention will be described more specifically below with reference to the contents of the components of the steel. C: Not more than 0.02 wt% C is an element which generally lowers the r value, represses elongation and weakens corrosion resistance. The upper limit of the content of C is 0.02 wt% because these adverse effects become conspicuous above the content. Preferably, C content is not more than about 0.005 wt%. Si: Between 0.01 and 1.0 wt% Si is an element which promotes deoxidation, when the Si content is not less than 0.01 wt%. The upper limit of the Si content, however, is 1.0 wt%. Contents in excess of 1.0 wt% can impair cold workability and degrade ductility. Preferably, the Si content is in the range of about 0.03 - 0.5 wt%. Mn: Between 0.01 and 1.0 wt% Mn is useful for separating S from steel and fixing the separated S and to maintain hot workability, when the Mn content is not less than 0.01 wt%. The upper limit of Mn content is 1.0 wt% because additional quantities lower cold workability and degrade corrosion resistance. Preferably, the Mn content is in the range of about 0.1 - 0.5 wt%. P: Not more than 0.08 wt% P is a harmful element which not only degrades hot workability but also deteriorates mechanical properties. The upper limit of P content is 0.08 wt% because the adverse effects of this element become conspicuous when the content exceeds 0.08 wt%. Preferably, P content is not more than about 0.04 wt%. S: Not more than 0.01 wt% S is a harmful element which couples with Mn to form rust-promoting MnS and, at the same time, segregates in the grain boundary and promotes the embrittlement of grain boundary. The upper limit of the S content, therefore, is 0.01 wt% because the adverse effects of this element become conspicuous when the content exceeds 0.01 wt%. Preferably, S content is not more than about 0.006 wt%. Al: Between 0.005 and 0.30 wt% Al is an element which promotes deoxidation, when the Al content is not less than 0.005 wt%. The upper limit of Al content is 0.30 wt% because additional quantities of this element promote Al-based inclusions which induce surface flaws. The Al content is preferably in the range of 0.005 - 0.10 wt%. Cr: Between 11 and 50 wt% Cr is an element which is indispensable to the improvement of corrosion resistance. The Cr content is in the range of 11 - 50 wt% because sufficient corrosion resistance will not be realized if the content is less than 11 wt%, while hot and cold workability will be degraded if the content exceeds 50 wt%. The Cr content preferably is in the range of 11 to 35 wt%. Mo: Between 0.1 and 5.0 wt% Mo is an element which improves corrosion resistance and anti-ridging characteristics, when the Mo content is not less than 0.1 wt%. The upper limit of the Mo content is 5.0 wt% because the corrosion and rusting resistance effects are saturated, and precipitation of the σ phase and the χ phase is promoted to degrade corrosion resistance and workability when the Mo content exceeds 5.0 wt%. Mo content is preferably not less than 0.1 wt% to ensure the beneficial effects described above. N: Not more than 0.03 wt% N, like C, is harmful to corrosion resistance because it lowers the r value, represses elongation, and forms a Cr-removing layer through the formation of a Cr nitride. The upper limit of the N content is 0.03 wt% because the adverse effects of the element become conspicuous when the N content exceeds 0.03 wt%. Preferably, the N content is not more than about 0.01 wt%. 0.005 wt% ≤ (C+N) ≤ 0.03 wt%, (C/N) < 0.6 C and N, as described above, both have adverse effects on the r value, elongation, and corrosion resistance. If the total content of C and N exceeds 0.03 wt%, these negative effects will become conspicuous. Conversely, if the combined content of C and N is less than 0.005 wt%, a preferential growth of crystal grains will be promoted, controlling the aggregation texture becomes difficult, and anti-ridging characteristics is degraded. The C content and the N content, therefore, must satisfy the expression, 0.005 wt% ≤ (C + N) ≤ 0.03 wt%. We have also discovered that the weight ratio of C and N, (C/N), has a large effect on the aggregation texture. If (C/N) is less than 0.6, the numerical value of the X-ray integral intensity ratio (222)/(310) will increase, the r value and the elongation will be improved, and the magnitude of planar anisotropy will decrease. The C content and the N content, therefore, must also satisfy the relation, (C/N) < 0.6. Fig. 1 shows the relation between planar anisotropy (to be determined by the method which will be described herein below) and C/N, obtained from various species of steel sheets having the C + N in the range of 0.0080 - 0.0200 wt%, Ti/(C + N) in the range of 10 - 19, and the other elements in accordance with the present invention. Fig. 1 shows that the C/N must be less than 0.6 to decrease the planar anisotropy as required. 5 ≤ Ti/(C + N) ≤ 30 Ti is a carbon and nitrogen stabilized element which is useful for repressing the precipitation at the grain boundaries of Cr carbides and/or nitrides during the course of welding or heat treatment. Ti also improves corrosion resistance, fixes the solid solution of C and N in steel in the form of a carbides and/or nitrides, controls the texture of aggregation, and improves ductility and workability. These effects will not be obtained if the weight ratio of Ti to (C + N), i.e. Ti/(C + N), is less than 5. Conversely, if this ratio exceeds 30, these properties will be degraded. Thus, Ti and C and N must satisfy the relation, 5 ≤ Ti/(C + N) ≤ 30. The composition of the ferritic stainless steel of this invention may also include, besides the elements mentioned above, at least one member of at least one group selected from the following three groups: (1) Ca: 0.0005 - 0.0050 wt%, (2) Nb: 0.001 - 0.0100 wt%, B: 0.00020 - 0.0020 wt%, (3) Cu: 0.01 - 2.0 wt%, Ni: 0.01 - 2.0 wt%. Ca: Between 0.0005 and 0.0050 wt% Ca effectively represses the nozzle clogging caused by Ti-based inclusions during the casting of steel, when the Ca content is not less than about 0.0010 wt%. The Ca content, however, must have its upper limit of 0.0050 wt% because excess addition of this element can induce rusting, with a Ca-based inclusions acting as the starting point, and consequently promote fracture by embrittlement. The Ca content is preferably in the range of about 0.0010 - 0.0030 wt%. Nb: Between 0.001 - 0.0100 wt% Nb is a carbon and nitrogen stabilising element which effectively enhances corrosion resistance and workability and, in particular, enhances planar anisotropy for improved mechanical characteristics, when the Nb content is not less than 0.001 wt%. If Nb is added in an amount exceeding 0.0100 wt%, however, the effect mentioned above will be saturated and the workability will be degraded as the temperature of recrystallization rises. The upper limit of Nb content, therefore, is 0.0100 wt%. For the purpose of manifesting the effect of producing minute carbide particles in steel, refining crystal grains, and improving planar anisotropy, it is preferred that Nb content is between about 0.003 and 0.008 wt%. B: Between 0.00020 and 0.0020 wt% B is a useful element which precipitates in the crystal grain boundaries and improves the secondary work embrittlement of steel, when the B content is not less than 0.00020 wt%. The upper limit of B content is 0.0020 wt% because contents in excess of 0.0020 wt% impair workability. Preferably, B content is in the range of about 0.0003 - 0.0010 wt%. Cu: Between 0.01 and 2.0 wt% Cu is a useful element which improves resistance to corrosion, caused by acid, and the crevice corrosion resistance, when the Cu content is not less than 0.01 wt%. The element is also effective in restraining the growth of pits destined to become initial rusting points, thereby improving the corrosion resistance. Cu is useful for imparting improved corrosion resistance to such consumer articles as building materials and kitchen utensils, for example. The upper limit of the Cu content is 2.0 wt% because Cu contents exceeding 2.0 wt% will bring about adverse effects like cracking at high temperatures. Preferably, Cu content is in the range of 0.1 - 2.0 wt%. Ni: Between 0.01 and 2.0 wt% Ni is also a useful element which improves the resistance to corrosion, caused by acid, and the crevice corrosion resistance, when the Ni content is not less than 0.01 wt%. The element is also effective in restraining the growth of pits destined to become initial rusting points, thereby improving the corrosion resistance. Ni is useful for imparting improved corrosion resistance to such consumer articles as building materials and kitchen utensils, for example. The upper limit of Ni content nevertheless is 2.0 wt% because Ni contents in excess of 2.0 wt% will bring about adverse effects such as cracking at high temperatures. Preferably, Ni content is in the range of 0.1 - 2.0 wt%. For the purpose of improving the corrosion resistance, it is preferred that the total content of Cu and Ni is not less than 0.01 wt%. X-ray integral intensity ratio: (222)/(310) (hereinafter expressed as "α") An increase in the X-ray integral intensity ratio: α = (222)/(310) (which will be described specifically herein below) in a plane of a rolled steel sheet parallel to the sheet surface serves reflects a decrease in the ratio of planar anisotropy such as for Δr and ΔEl without negatively affecting the r value and the elongation. To secure this advantageous effect, the ratio of α in a plane of a hot rolled sheet parallel to the sheet surface at a depth of about 1/4 of the thickness of the sheet is controlled to a level exceeding 30. When a hot rolled sheet having an aggregation texture controlled as described above is subjected to hot rolled sheet annealing, cold rolling, and cold rolled sheet annealing, a ferritic stainless steel sheet having the ratio of α at depth of about 1/4 of the thickness of the sheet in a plane parallel to the sheet surface will ultimately exhibit an α exceeding 35. Fig. 2 represents the relation between planar anisotropy (to be determined by the method which will be described herein below) and the ratio of α at the depth of about 1/4 of the thickness of rolled sheet, obtained from cold rolled steel sheets manufactured by subjecting various species of steels having C + N total percentages in the range of 0.0080 - 0.0200 wt%, the Ti/(C + N) ratio in the range of 10 - 19, and the other elements in accordance with the invention to hot rolling, annealing, and cold rolling performed under varied conditions. Fig. 2 shows that the ratio of α in a cold rolled sheet must be controlled to a level of not less than 35, preferably to a level of not less than about 75, for the purpose of lowering both the elongation planar anisotropy ΔEl and the r value planar anisotropy Δr. The depth of about 1/4 of the thickness in the direction of sheet thickness is adopted as the position for the determination of the X-ray integral intensity ratio α, because it has a good relation with the planar anisotropy and is most representative of the numerical values of α existing throughout the entire body of the steel sheet. It has been discovered that the degree to which the reduction in both types of planar anisotropy ΔEl and Δr is retained increases as the ratio of the X-ray integral intensity ratio α increases, and also increases in proportion to improved uniformity in the ratio of α in the sheet thickness direction. The data of Fig. 3 were obtained by preparing steel sheets whose ratio of α at a depth of 1/4 of the sheet thickness in a cold rolled sheet were in the range of 50 - 130, measuring the ratio of α in the direction of sheet thickness at various depths, calculating the average α in the thickness direction, then calculating the thickness proportion of the sheet which possesses an α within ±40% of the average α in the sheet thickness direction. The relation between the proportions mentioned above and both types of planar anisotropy ΔEl and Δr is shown in Fig. 3. The method for specifically calculating the ratio of the X-ray integral intensity ratio α mentioned above is schematically shown in Fig. 4. First, a distribution curve in the direction of sheet thickness is found by measuring the ratio of α at varying positions either separated at intervals of not more than 100 µm or selected at not less than 30 points, integrating this distribution curve in the direction of sheet thickness, and dividing the results of this integration by the sheet thickness B to thereby calculate the average of the ratio α of the X-ray integral intensity ratio in the direction of sheet thickness. Then, the lengths in the direction of sheet thickness (the total length of the line segment, A1+A2, in the diagram) in the area existing within about ±40% of the average are found and the ratio of the lengths to the sheet thickness {(A1+A2)/B} x 100(%) are calculated. Fig. 3 shows that the planar anisotropy can be decreased by controlling the thickness proportion of the sheet having an α within about ±40% of the average α in the sheet thickness direction to not less than about 80%. A method for producing a steel sheet in accordance with the invention comprises melting a steel having a composition specified above in, e.g., a converter or an electric furnace, forming slabs from the melt by a continuous casting method or a molding method, and subjecting the slabs sequentially to the steps of hot rolling, annealing of hot rolled sheet, pickling, cold rolling, and finish annealing. These steps are described in detail below. Hot rolling The reduction ratio of hot rolling is closely related to the separation of a ferrite band which is thought to be an important factor in ridging. In particular, we have discovered that when the final pass reduction ratio during rough rolling exceeds about 40%, separation of the ferrite band is ensured, strain in the sheet thickness direction is made uniform, and the refinement of crystal grains by static recrystallization is effectively promoted. Further, the final temperature of the finish rolling has effects similar to the reduction ratio in the rough rolling mentioned above. The degree with which the uniformity, refinement, and isotropy of the crystal grains in the direction of sheet thickness are promoted by the residue of the rolling strain of increases as the final temperature of the finish rolling lowers. The upper limit of the final finish rolling temperature is set at 750°C because the effects mentioned above are large by lowering the final temperature below 750°C. If the final temperature is less than about 600°C, surface defects will occur easily and the productivity will be degraded. Therefore, the lower limit of the final temperature is preferably about 600°C. The application of a lubricant to the place between the sheet and work rolls during hot rolling in the low temperature range mentioned above for the purpose of imparting uniform strain in the direction of sheet thickness is advantageous because the lubrication promotes static recrystallization caused by accumulation of strain. Annealing of hot rolled sheet The annealing conditions for the hot rolled sheet affect ridging. If the annealing temperature of the hot rolled sheet is too low, ridging will occur in the form of a band. If this temperature is too high, the surface of the rolled steel sheet will exhibit a rough skin. The range of this annealing temperature, therefore, is 900 - 1100°C, preferably about 975 - 1050°C. The annealing time is preferably in the range of about 5 seconds - 4 minutes. Cold rolling The reduction ratio of the cold rolling affects ridging, the r value, and planar anisotropy. The r value and anti-ridging characteristics are improved and planar anisotropy is decreased when the reduction ratio of the cold rolling is increased. In view of these points, the reduction ratio of the cold rolling should exceed about 60%. These characteristics are degraded, however, when the reduction ratio exceeds about 95%. The reduction ratio of the cold rolling, therefore, is preferably in the range of 60 - 95%. Finish annealing The finish annealing of the cold rolled sheet is essential for the isotropy and uniformity of crystal grains and for the purpose of securing good mechanical properties. Preferably, the range of finish annealing temperature is 830 - 950°C, and the retention time is in the range of about 3 seconds - 1 minute. EXAMPLES The invention will now be described through illustrative examples. The examples are not intended to limit the scope of the appended claims. Species of steel differing in chemical composition as shown in Table 1 (part 1-(a) to part 3-(b) were each melted and refined in a converter, cast in the shape of a slab, then heated to 1250°C, and hot rolled under production condition No. 1 shown in Table 2 by four passes of rough rolling and seven passes of finish rolling. The hot-rolled sheets were annealed (retention time: 1 minute), pickled, then cold rolled, and finish annealed (retention time: 30 seconds) to obtain cold-rolled steel sheets having a thickness of 0.6 mm. In each of the cold-rolled steel sheets obtained by the method described above, the X-ray integral intensity ratio α was found by the X-ray diffraction method at a depth of 1/4 of the sheet thickness to determine elongation (El), deep-drawing formability (r value), ΔEl, Δr, anti-ridging characteristics, and biaxial stretch forming (Erichsen value). By the method described above, the thickness proportion of the sheet which possesses an α within about ±40% of the average α in the sheet thickness direction was calculated. To study the aggregation texture in a hot-rolled sheet, the ratio of α was determined at a depth of 1/4 of the sheet thickness. The results are shown in Table 3. Some of the steels shown in Table 1 were combined as shown in Table 4 under production conditions shown in Table 2 and processed in the same manner as described above to produce cold-rolled steel sheets, 0.6 mm in thickness. These steel sheets were similarly tested. The results are shown in Table 4. The properties mentioned above were measured by the following methods. El, ΔEl, r value, and Δr From a given steel sheet, test pieces in accordance with No. 13B of JIS (Japanese Industrial Standard) were taken in a direction of 45° relative to the direction of rolling and in a direction of 90° relative to the direction of rolling. The test pieces were subjected to a tensile test to determine elongation at rupture. From the test results, El and ΔEl were calculated based on the following formulas: El = (El L + 2El D + El T )/4 ΔEl = (El L - 2El D + El T )/2. In the formulas, El L represents elongation at rupture in the rolling direction, El D represents elongation at rupture in a direction 45° relative to the rolling direction, and El T represents elongation at rupture in a direction 90° relative to the rolling direction. Test pieces in accordance with No. 13B of JIS, taken in varying directions in the same manner as described above, were uniaxially stretched to 5 - 15%. From the ratio of lateral strain and strain in the direction of sheet thickness thusly obtained, the Rankford values were determined in the relevant directions and the r value and the Δr were calculated based on the following formulas: r = (r L + 2r D + r T )/4 Δr = (r L - 2r D + r T )/2. In the formulas, r L represents Rankford value in the rolling direction, r D represents the Rankford value in a direction 45° relative to the rolling direction, and r T represents the Rankford value in a direction 90° relative to the rolling direction. Erichsen value This was determined in accordance with method 2247 of JIS, using a sample coated with graphite grease. Undulating height (irregularities in ridging) The undulating height was measured by producing a ridge in a sample through a tensile test, measuring irregularities perpendicular to the stretching direction by the use of a roughness meter, and calculating the average of the differences in wave heights from the results of the measurement mentioned above. The undulating height was determined by polishing one surface of a tensile test piece prepared in accordance with No. 5 of JIS until a wet 600 finish was attained, then stretching the test piece by 20% at room temperature, evaluating the produced ridge by measuring perpendicular to the stretching direction by the use of a roughness meter, and calculating the average of the measurements. As seen from the tabulated results, a ferritic stainless steel sheet having an El of not less than 30%, a ΔEl of not more than 2.0%, a r value of not less than 1.4, a Δr of not more than 0.2, an Erichsen value of not less than 10, and an undulating height of not more than 10 µm, possessing satisfactory formability, manifesting less planar anisotropy, and excelling in anti-ridging characteristics can be produced by adjusting the steel composition and the production conditions and controlling the α value of the cold-rolled sheet in accordance with the invention. As described above, this invention enables the production of a ferritic stainless steel sheet possessing satisfactory formability and, at the same time, exhibiting less planar anisotropy and excelling in anti-ridging characteristics. By this invention, a ferritic stainless steel sheet having an elongation of not less than 30%, a r value of not less than 1.4, a planar anisotropy of elongation, ΔEl, of not more than 2.0%, a planar anisotropy of r value, Δr, of not more than 0.2, and a anti-ridging characteristics of not more than 10 µm in undulating height can be produced. The ferritic stainless steel sheets produced according to this invention, therefore, can be useed in various applications which have heretofore required the use of austenitic stainless steel sheets. As a result, this invention has very high commercial value. It should be understood that the scope of the invention is not limited to the particular illustrative embodiments shown and described herein, but that various equivalent elements and method steps may be substituted without departing from the scope of the invention defined in the appended claims.

Claims: A ferritic stainless steel sheet having less planar anisotropy and excellent anti-ridging characteristics, comprising: C not more than 0.02 wt% Si 0.01 - 1.0 wt% Mn 0.01 -1.0 wt% P not more than 0.08 wt% S not more than 0.01 wt% Al 0.005 - 0.30 wt% Cr 11 - 50 wt% Mo 0.1 - 5.0 wt% N not more than 0.03 wt% the content of C and N further satisfying the relations: 0.005 wt% ≤ (C + N) ≤ 0.03 wt% and (C/N) < 0.6, said sheet further comprising Ti in an amount which satisfies the relation: 5 ≤ Ti / (C + N) ≤ 30, said sheet optionally comprising at least one member of at least one group selected from the following three groups: (1) Ca: 0.0005 - 0.0050 wt%, (2) Nb: 0.001 - 0.0100 wt%, B: 0.00020 - 0.0020 wt%, (3) Cu: 0.01 - 2.0 wt%, Ni: 0.01 - 2.0 wt% the balance of the sheet being Fe and incidental impurities, wherein said sheet has an X-ray integral intensity ratio (222)/(310) of not less than 35 in a plane parallel to a sheet surface at a depth of about ¼ of the sheet thickness from said sheet surface. The ferritic stainless steel sheet according to claim 1, further comprising an X-ray integral intensity ratio (222)/(310) over at least 80% of said sheet thickness within ± 40% of an average X-ray integral intensity ratio (222)/(310) in the sheet thickness direction. A method of producing a ferritic stainless steel sheet having less planar anisotropy and excellent anti-ridging characteristics, comprising the steps of: preparing a steel comprising: C not more than 0.02 wt% Si 0.01 - 1.0 wt% Mn 0.01 - 1.0 wt% P not more than 0.08 wt% S not more than 0.01 wt% Al 0.005 - 0.30 wt% Cr 11 - 50 wt% Mo 0.1 - 5.0 wt% N not more than 0.03 wt% the content of C and N further satisfying the relations: 0.005 wt% ≤ (C + N) ≤ 0.03 wt% and (C/N) < 0.6, said steel further comprising Ti in an amount which satisfies the relation: 5 ≤ Ti / (C + N) ≤ 30, wherein said step of preparing said steel further optionally comprises the incorporation of at least one member of at least one group selected from the following three groups: (1) Ca: 0.0005 - 0.0050 wt%, (2) Nb: 0.001 - 0.0100 wt%, B: 0.00020 - 0.0020 wt%, (3) Cu: 0.01 - 2.0 wt%, Ni: 0.01 - 2.0 wt% the balance of said steel being Fe and incidental impurities; hot rolling said steel to a hot-rolled sheet, said hot rolling including final pass reduction ratio during rough rolling of not less than 40% and at a final finish rolling temperature of not more than 750°C and subsequently subjecting said hot-rolled sheet to hot roll annealing, cold rolling, and finish annealing. A method of producing a ferritic stainless steel sheet having less planar anisotropy and excellent anti-ridging characteristics, comprising the steps of: preparing a steel comprising: C not more than 0.02 wt% Si 0.01 - 1.0 wt% Mn 0.01-1.0 wt% P not more than 0.08 wt% S not more than 0.01 wt% Al 0.005- 0.30 wt% Cr 11 - 50 wt% Mo 0.1 - 5.0 wt% N not more than 0.03 wt% the content of C and N further satisfying the relations: 0.005 wt% ≤ (C + N) ≤ 0.03 wt% and (C/N) < 0.6, said steel further comprising Ti in an amount which satisfies the relation: 5 ≤ Ti / (C + N) ≤ 30, wherein said step of preparing said steel further optionally comprises the incorporation of at least one member of at least one group selected from the following three groups: (1) Ca: 0.0005 - 0.0050 wt%, (2) Nb: 0.001 - 0.0100 wt%, B: 0.00020 - 0.0020 wt%, (3) Cu: 0.01 - 2.0 wt%, Ni: 0.01 - 2.0 wt% the balance of said steel being Fe and incidental impurities; hot rolling said steel to a hot-rolled sheet, said hot rolling including final pass reduction ratio during rough rolling of not less than 40% and at a final finish rolling temperature of not more than 750°C; wherein a hot-rolled sheet having a X-ray integral intensity ratio (222)/(310) of not less than 30 in a plane parallel to a sheet surface at a depth of about ¼ of the sheet thickness from said sheet surface; and subsequently subjecting said hot-rolled sheet to annealing, cold rolling, and finish annealing. The method according to claim 3 or 4, wherein said annealing is conducted at a temperature in the range of 900 - 1100°C, said cold rolling is effected with a reduction ratio in the range of 60% - 95%, and said finish annealing is performed at a temperature in the range of 830 - 950°C.

Inventors: KASAI MASAYUKI, KOBAYASHI MAKOTO, KUMAZAWA SHINTARO, SATOH SUSUMU, UJIRO TAKUMI, YAZAWA YOSHIHIRO, KASAI, MASAYUKI, KOBAYASHI, MAKOTO, KUMAZAWA, SHINTARO, SATOH, SUSUMU, UJIRO, TAKUMI, YAZAWA, YOSHIHIRO, Kasai, Masayuki, c/o Technical Research Center, KOBAYASHI, MAKOTO, C/O CHIBA WORKS, Kumazawa, Shintaro, c/o Chiba Works, Satoh, Susumu, c/o Technical Research Laboratories, Ujiro, Takumi, c/o Technical Research Laboratories, Yazawa, Yoshihiro, c/o Technical Research Lab.
Applicants: KAWASAKI STEEL CO, KAWASAKI STEEL CORPORATION
Application year: 1996
Main classification: C21D8
IPC codes: C21D8, C22C38