Process involving metal hydrides

Abstract: Metal hydrides are activated by an electrochemical procedure. In this procedure, a bulk sample of the corresponding metal is immersed in an aqueous electrolyte and contacted by a cathode. Current passed through the aqueous electrolyte causes electrolysis of the water and a concomitant reaction with the formation of metal hydride. As a result, the metal hydride is fractured and smaller particles result. Additionally, the resulting metal hydride has a substantial amount of absorbed hydrogen. A novel plating method, taking advantage of the reducing power of hydrogen absorbed in a metal hydride, is useful to encapsulate such metal hydride with a variety of metals. Therefore, such hydrides are uniformly coated by using plating solutions without the standard reducing agent and stabilizer.

Description: Background of the Invention 1. Field of the Invention This invention relates to metal hydrides, and in particular, to processes involving such hydrides. 2. Art Background Metal hydrides are used in a variety of industrial applications. Although there are many such applications, possibly the most prominent is the use of metal hydrides in batteries. For example, secondary nickel-metal hydride batteries employ lanthanum nickel hydride (or alloy modifications) or other intermetallic hydrides in the negative electrode. A variety of other uses involving energy storage and transfer have been described. Irrespective of the application, a crucial step in preparation is activation of the intermetallic. Activation is achieved, for example, by repeatedly reducing the metal such as LaNi 5 to the corresponding hydride with H 2 gas at high pressure and/or temperature followed by removal of hydrogen at lower pressures. This cyclic process, generally denominated activation, is believed to serve a number of purposes. Each reduction to the hydride 1) removes reducible surface oxides which tend to interfere with the functioning of the material in the ultimate desired application, 2) induces a reduction in particle size resulting from an increase in volume that causes fracture of the metal particles, and 3) changes the structure and/or composition of the material and/or surface of the metal. Any one or a combination of these three effects is generally employable to increase the rate of reversible hydrogen reaction and, thus, enhance the operation of the material for applications such as batteries or hydrogen storage. Methods of activation include I) hydriding with hydrogen gas at high temperatures and pressure; 2) hydriding with chemical hydriding agents; 3) etching with hot hydrofluoric acid or KOH; 4) pulsing the material between hydriding and dehydriding potentials in electrochemical cells; and 5) conventional battery cycling of metal hydride electrodes. However, activation of hydrides has most widely been performed by the first process, i.e., activation, at relatively high pressures (up to 1000 psi) and temperatures as high as 450°C, by subjecting the metal directly to hydrogen gas. Clearly, although such conditions are not prohibitive to commercial use, they require relatively large expenditures for suitable equipment Thus, an alternative to high pressure reaction of hydrogen gas with the corresponding metal would be quite desirable. Summary of the Invention The invention is defined in the claims. An advantageous method of producing hydrides with absorbed hydrogen is through the activation of metals, e.g., intermetallics such as LaNi 5 , using an electrochemical technique. In this technique, a metal to be activated is positioned at the cathode of an electrochemical cell such as shown at 9 in FIG. 1. An aqueous-based electrolyte is employed so that upon passing a current at a suitable voltage between cathodes and anodes through the electrolyte, electrolysis of the water present produces hydrogen. The resulting hydrogen interacts with the metal producing the hydride, and additionally, causes fracture of the metal into significantly smaller particles. If the cathode 5 in FIG. 1 is surrounded by a cage 8 of suitable mesh, this fracture continues until the particles are sufficiently small to fall through the mesh into the underlying anode compartment. Excessive hydrogen can be oxidized to reduce the hydrogen content of the hydride powder. Brief Description of the Drawings FIG. 1 is illustrative of equipment useful in one aspect of the invention, and FIGS. 2 and 3 are illustrative of results relating to the invention. Detailed Description Metals capable of forming stable metal hydrides are converted into their corresponding hydride, are activated, and are reduced to relatively small particles through an electrochemical process that, in one embodiment, produces an advantageous level of absorbed hydrogen. Typical metals including elements, alloys, and intermetallic materials are employable in such electrochemical processes. Examples of such metals include Pd, LaNi 5 , MmNi 3.5 Al 0.8 Co 0.7 (Mm, mischmetal is a mixture or alloy of rare earth metals as described in Metals Handbook, 8th ed., ASM, pg. 25, 1961), Ti 2 Ni, Zr 0.5 Ti 0.5 V 0.69 Ni 1.22 Cr 0.22 , and ZrCrNi. Basically, for the inventive procedure, a metal should be capable of forming a hydride and should have the properties of absorbing hydrogen (more than 0.05% by wt.) inside the metal matrix. A particularly advantageous subset of such materials include metals corresponding to hydrides that produce an electromotive force when employed in a metal hydride battery. The hydrides are formed by reaction with hydrogen generated by electrolysis of an aqueous-based electrolyte, 15 in FIG. 1. For example, a useful electrolyte is formed by dissolving a suitable salt in water. Typical salts employed for such formation of electrolyte include potassium hydroxide and sodium hydroxide. Generally, salt concentrations in the range 0.5% to 50% by weight are employed. Concentrations greater than 50% are undesirable because of salt precipitation, while concentrations less than 0.5% lead to insufficient conductivity. Although the electrolytes should be aqueous based, presence of nonaqueous materials such as ethanol is not precluded. However, generally, concentrations of such nonaqueous materials should be limited to less than 10 volume %. As previously discussed, the current is passed through the electrolyte, 15, to induce electrolysis of water. Generally, a voltage of 1.23 volt or greater is required to induce such electrolysis. For typical metal compounds, voltages in the range 2 volt to 20 volt are useful. The rate of generation of hydrogen depends on the current. Typically, for a 2.5" inside dia and 4" long cylindrical barrel with a 200 micron size mesh screen wall, currents in the range 5 A to 15 A are usefully employed. Currents below 0.1 A, although not precluded, unduly prolong the process, while currents greater than 20 A induce excessive hydrogen evolution. For such exemplary conditions, typical metal loads are in the range 100 to 500 gms. The resulting hydrogen interacts with the metal 9 and induces activation of the corresponding hydride including fracture of the metal hydride into smaller particles. It is advantageous to have the cylinder 8 in FIG. 1 be made of mesh so that this fracture process continues until a desired particle size is reached resulting in particles, 25, falling through the mesh (which advantageously is rotated by motor, 11) and out of the reaction region. Particle fracture does not continue indefinitely once the particle falls through the barrel, and typically, mean fracture size is limited to a range between 6 µm and 200 µm. Such particle size is nevertheless advantageous for most uses including for applications in batteries. The composition of the electrodes is not critical. Typically, electrodes such as nickel and stainless steel are employed where the geometry of the anode, 7, is typically a mesh type and the cathode, 5, is a spherical dangler. Additionally, the size of the cell is also not critical, and typically, configurations such as a cylindrical barrel are employed. In the case where the metal hydride does not need to be coated by plating or where absorbed hydrogen is not used for such plating, the activated metal hydride is allowed after it passes through the mesh to contact an anode, any excess, absorbed hydrogen present is oxidized to form water. In this manner, any excessive accumulation of hydrogen is avoided, and thus, the activated material can be handled in air. The activated hydride particles from the inventive electrochemical process have a substantial level of absorbed hydrogen. The level of hydrogen in some exemplary metals is shown in Table 1. Hydrogen Storage Capacities of Metal Hydrides Metal Hydride Hydrogen Density (H/mL x 10 -22 ) Capacity (mAh/g) LaNi 5 H 6 7.4 372 CaNi 5 H 6 6.6 480 FeTiH 2 5.6 490 Mg 2 NiH 4 5.9 990 H 2 liquid 4.2 The concentration of hydrogen in liquid hydrogen is given as a comparison. As can be seen, the concentration of hydrogen in the activated metal hydrides is relatively high. This hydrogen is advantageously used as a reducing agent for the plating, such as electroless plating, of the metal hydrides. The following examples are illustrative of the invention. Example 1 About 400 grams of chunks of LaNi 5 (1-3cm size) were placed into a barrel plater (Model 24, Stirling Systems Sales Corp., St. Charles, IL). The barrel had a 200 micron size mesh made of polypropylene materials. The propylene tank (8" x 8" x 8") contained About 7 liters of 30 wt. % KOH aqueous solution. There were two vertical nickel anodes (3" x 4") placeD about 0.25" away from the barrel. The cathodic current was passed through the chunks of LaNi 5 by using a spherical dangler inside the barrel. The rotational speed was set to about 5 rpm. The current was set at 10 amperes and the cell voltage was about 7 volts. After 8.5 hours, 82 grams of LaNi 5 were reduced to sizes below 200 µm and fell through the barrel to the bottom of the tank. During the next 10 hours, additional 110 grams of LaNi 5 fell through the barrel. Additional experiments were carried out to determine the dependence of powder formation on the electrolytic current passed and the rotational speed of the plating barrel. FIG. 2 shows the amount of powder formed as a function of the current passed. The rate of powder formation was higher at higher current: 12.5 g/hr, 21 g/hr, and 35 g/hr at 5A, 10A, and 15A respectively with a rotational speed of 20 rpm. FIG. 3 shows the amount of powder formed as a function of the rotational speed of the plating barrel while passing a current of 10 amperes. At 20 rpm or higher, the rate of powder formation was about 20 g/hr. At 7 rpm, the rate dropped to 13 g/hr. Example 2 Pd wires (1 mm diameter) were charged with hydrogen by electrolysis in 1 M KOH for about 18 hours at a current density of approximately 20 mA/cm 2 . After a quick rinse in de-ionized water, the Pd hydride wires were immersed for about 15 min. into the plating solution held at 50°C. The thickness of the metal coating was measured by X-ray fluorescence and cross-section microscopy. The plating solutions used and the thickness of the metal coating are listed in Table 2. Metal Hydride Plated Metal Plating Solution Average Thickness (microns) PdH x Cu 0.1M CuSO 4 , 0.05M H 2 SO 4 2.0 PdH x Cu 0.02M CuSO 4 , 0.065M triisopropanolamine 0.5 PdH x Ag 0.01M AgCN, 0.1MKCN, 0.1M KOH 3.6 Pd(no H 2 ) Ag 0.01M AgCN, 0.1MKCN, 0.1M KOH 0.1 Copper is plated in both acidic and basic solutions. The copper coating plated in the acidic solution is thicker than the basic solution, possibly due to the higher throwing power in the lower pH. About 3.6 microns of Ag was plated on the hydrided Pd wire in the silver cyanide solution Since it is possible to plate Ag on Pd by displacement plating, a Pd wire with no hydrogen charging was placed in the same solution and the Ag plated by displacement was found to be negligible. Example 3 Nickel and Cu were plated on representative intermetallic alloys that can be hydrided, such as LaNi 5 , Ti 2 Ni, Ti 2 Ni 0.8 Mn 0.2 and ZrCrNi. A 1 gram ingot of LaNi 5 was converted to hydride in 1M KOH for approximately 4 hours at a current density of 20mA/cm 2 . After a quick rinse in de-ionized water it was immersed in an alkaline ammoniacal solution (0.2M NiSO 4 , approximately 1.2M NH 4 OH to pH 12) at room temperature for 15 min. Another LaNi 5 sample plus ingots of Ti 2 Ni and Ti 2 Ni 0.8 Mn 0.2 were charged and washed as described above and then immersed for 15 min. in an alkaline copper plating solution (0.02M CuSO 4 ,0.065M triisopropanolamine, 0.2M NaOH, pH 12) at 50°C. A ZrCrNi sample was treated in a similar fashion but no Cu plating was realized. The sample was pulse activated prior to immersion in the Cu plating solution and a coating of about 2.5 microns was obtained. The average thickness of all the coatings is listed in Table 3. Metal Hydride Plated Metal Average Thickness (microns) LaNi 5 Ni 0.5 LaNi 5 Cu 3.0 Ti 2 Ni Cu 3.0 Ti 2 Ni 0.8 Mn 0.2 Cu 2.0 ZrCrNi Cu 2.5

Claims: A process for activating a metal, comprising the steps of: providing an electrochemical cell comprising an aqueous electrolyte a cathode, and an anode; contacting a metal positioned at the cathode and capable of forming a metal hydride with the aqueous electrolyte and passing a current through the aqueous electrolyte between the cathode and the anode to produce hydrogen, such that the metal both interacts with the hydrogen to produce a metal hydride and fractures, the resultant fractured metal exhibiting an increased rate of reversible hydrogen reaction. The process of claim 1, wherein the fractured metal passes through a mesh located in the electrochemical cell. The process of claim 1, wherein the metal comprises a material chosen from the group consisting of Pd, LaNi 5 , MmNi 3.5 Al 0.8 Co 0.7 , Ti 2 Ni, Zr 0.5 Ti 0.5 V 0.69 Ni 1.22 Cr 0.22 , and ZrCrNi. The process of claim 1, wherein the aqueous electrolyte comprises an aqueous solution of a hydroxide salt.

Inventors: HON LAW HENRY, VYAS BRIJESH, HON LAW, HENRY, VYAS, BRIJESH
Applicants: AT & T CORP, AT&T IPM CORP.
Application year: 1996
Main classification: H01M4
IPC codes: H01M4, C23C18, C01B6