Pneumatic tire and process for production thereof

Abstract: A pneumatic tire having an air permeation preventive layer comprising (A) a thin film of at least one aliphatic polyamide resin wherein at least part of the amide groups thereof are modified with alkoxyalkyl groups, (B) a thin film obtained from the curing a liquid composition containing (i) a multi component copolymer polyamide resin, (ii) a curable resin, and (iii) a curing agent for curing the curable resin, (C) a thin film obtained by coating and cross-linking a polymer composition containing (i) at least one aliphatic polyamide resin wherein at least part of the amide groups thereof are modified with alkoxyalkyl groups and/or groups having curable unsaturated bonds and (ii) at least one cross-linking agent and/or curable resin other than an acid, or (D) a thin film of a vinylidene chloride-acrylonitrile copolymer obtained by copolymerizing 5 to 50 molar % of acrylonitrile.

Description: The present invention relates to a pneumatic tire having a layer for preventing of air permeation which enables a reduction in the weight of the tire and is superior in bonding with a rubber layer, without detracting from the retention of air pressure in the tire and also relates to a process for the production of the same. The present invention further relates to a pneumatic tire having a layer for preventing of air permeation which enables a reduction in the weight of the tire, is superior in bonding with the rubber layer, and, in superior in water resistance, heat resistance, and, in some cases, durability, without detracting from the retention of air pressure in the tire and also relates to a process for the production of the same. The reduction of fuel consumption is one of the major technical problems to be solved in the automobile industry. There have been increasingly stronger demands for reduction of the weight of the pneumatic tires as part thereof. The inner surface of a pneumatic tire is provided with an inner liner layer composed of a low gas-permeable rubber such as halogenated butyl rubber so as to enable the tire air pressure to be kept constant. A halogenated butyl rubber, however, suffers from a large hysteresis loss. For this reason, when, after vulcanization of the tire, there are waves formed in the inner surface rubber of the carcass layer and the inner liner layer in the space between the carcass cords, the inner liner rubber layer deforms along with the deformation of the carcass layer. Thus there is the problem that the rolling resistance increases. Therefore, in general, the inner liner layer (e.g., halogenated butyl rubber) and inner surface rubber of the carcass layer are joined through a rubber sheet which is called a tie gum with a small hysteresis loss. Accordingly, in addition to the thickness of the inner liner layer of the halogenated butyl rubber, there is added the thickness of the tie gum and the layer as a whole becomes a thickness of over 1 mm (i.e., 1000 µm). As a result, this becomes one factor increasing the weight of the final tire product. Various proposals have been made for using various materials, in place of the low gas-permeable rubber such as butyl rubber, as the inner liner layer or other air permeation preventive layer of the pneumatic tire. For example, Japanese Examined Patent Publication (Kokoku) No. 47-31761 discloses the coating of the inner surface of a vulcanized tire from 0.1 mm or less of a solution or dispersion of a synthetic resin such as polyvinylidene chloride, a saturated polyester resin, or a polyamide resin having an air permeation coefficient (cm 3 (standard state)/cm·sec·mmHg)) of not more than 1.0 x 10 -12 or less at 30°C and of 5.0 x 10 -12 or less at 70°C. The techniques disclosed in this publication disclose to provide the inner surface of the carcass of a vulcanized tire or the inner surface of the inner liner with a coating of a synthetic resin having a specific air permeation coefficient and making the thickness of the synthetic resin coating 0.1 mm or less, but the pneumatic tire disclosed in the publication had a problem in the bonding between the rubber and synthetic resin and further had a defect that, when a polyamide resin was used as the inner liner layer, the heat resistance and moisture resistance (or water resistance) were poor. Note that this publication did not disclose the use of an alkoxyalkylated polyamide, multiple copolymer polyamide resin, alkoxyalkylated polyamide, etc. Several proposals have been made for using a vinylidene chloride resin for an air permeation preventive layer of a pneumatic tire. For example, Japanese Examined Patent Publication (Kokoku) No. 47-31761 proposes a tube-less tire which is coated with a synthetic resin such as a vinylidene chloride resin and discloses a vinylidene chloride-acryl ester copolymer. Further, Japanese Unexamined Patent Publication (Kokai) No. 5-278409 proposes to construct an inner liner layer by coating a thin film or solution of a vinylidene chloride-vinyl chloride copolymer on the inner surface of a tire, followed by vulcanizing. A vinylidene chloride-vinyl chloride copolymer, however, has a Tg of 40°C or less and is inferior in long term heat resistance, and therefore, is not suitable for long term use at temperatures of, for example, about 80°C. A vinylidene chloride-vinyl chloride copolymer includes a large amount of chlorine, and therefore, easily degrades under heat. Further, most of them include up to 10% by weight of plasticizers for improving the workability or processability, but these plasticizers shift and the film hardens and the physical properties deteriorate. Thus there is the problem that they are not practical. Japanese Unexamined Patent Publication (Kokai) No. 5-330307 discloses to halogenate the inner surface of the tire (using a conventionally known chlorination solution, bromine solution, or iodine solution) and form on top of that a polymer coating (thickness of 10 to 200 µm) of methoxymethyl nylon, a copolymer nylon, a blend of polyurethane and polyvinylidene chloride, or a blend of polyurethane and polyvinylidene fluoride. This publication, however, discloses the use of an acid catalyst composed of an organic acid such as citric acid or tartaric acid as a cross-linking catalyst for curing the methoxymethylated nylon, but such an acid catalyst causes the problem of an inferior flex fatique due to deterioration after curing and of early cracking during use and it is difficult to say that the bondability is sufficient either. Further, the art disclosed in the publication suffers from the problem of a poor moisture resistance (or water resistance) or heat resistance of the air permeation preventive layer when an uncrosslinked or uncured polyamide resin is used, as the inner liner layer due to the non-crosslinking or curing thereof. Further, Japanese Unexamined Patent Publication (Kokai) No. 5-318618 discloses a pneumatic tire having a thin film of methoxymethylated nylon as an inner liner. According to this proposal, the inner surface of a green tire is sprayed or coated with a solution or emulsion of methoxymethylated nylon, then the tire is vulcanized or alternatively the inner surface of a vulcanized tire is sprayed or coated with a solution or emulsion of methoxymethylated nylon so as to produce a pneumatic tire. However, since there is no treatment for bonding between the rubber of the inner surface of the tire and the methoxymethylated nylon, when the tire is used at a high load, there are still the problem that the methoxymethylated nylon film peels off from the rubber of the inner surface of the tire and the problem that the resistance to humidity (or water resistance) and heat resistance of the inner liner layer are poor due to the fact the methoxymethylated nylon is not cross-linked or cured. Accordingly the object of the present invention is to provide a pneumatic tire using an air permeation preventive layer which enables the tire to be made lighter and which is bondable with a rubber layer, without detracting from the retention of air pressure by the tire and a process for production thereof. Another object of the present invention is to provide a pneumatic tire having an air permeation preventive layer which enables the tire to be reduced in weight and is superior in the bonding with the rubber layer and in the water resistance and heat resistance, without detracting from the retention of air pressure by the tire. In accordance with the present invention, there is provided a pneumatic tire having an air permeation preventive layer comprising a thin film of at least aliphatic polyamide resin wherein at least part of the amide groups thereof are modified with alkoxyalkyl groups, said air permeation preventive layer being laminated through an adhesive to the surface of a carcass layer or the surface of a rubber layer provided at the surface of the carcass layer. The present invention will now be better understood from the description set forth with reference to Fig. 1, which is a semi-cross-sectional view along the meridian direction showing the structure of an inner liner portion of a pneumatic tire of the present invention. The air permeation preventive layer of the pneumatic tire may be arranged at any location inside the tire, that is, at the inside or outside of the carcass layer or at the inside or outside of the rubber layer provided adjoining the carcass layer or any other location. The point is that there is no problem if it is arranged so as to prevent the permeation and dispersion of air from the inside of the tire and enable the air pressure inside the tire to be kept for a long period of time. Figure 1 is a semi-cross-sectional view along the meridian direction illustrating a typical example of the arrangement of an air permeation preventive layer of a pneumatic tire. In Fig. 1, a carcass layer 2 spans between the left and right bead cores 1 and 1. On the tire inner surface at the inside of the carcass layer 2 is provided with an inner liner layer 3. The inner liner layer 3 is composed from the cured or cross-linked first or second composition in the present invention. In Fig. 1, 4 shows a sidewall. According to the present invention, there is further provided a process for producing a pneumatic tire comprising spraying or coating an adhesive to the surface of a carcass layer of a green tire composed of unvulcanized rubber or the surface of a rubber layer provided at the surface of the carcass layer, then spraying or coating the adhesive surface with a liquid composition containing at least one aliphatic polyamide resin wherein at least part of the amide groups are modified by alkoxyalkyl groups, and then vulcanizing the green tire. According to the first aspect of the present invention, there is further provided a process for producing a pneumatic tire comprising spraying or coating an adhesive to the surface of a carcass layer of a vulcanized tire or the surface of a rubber layer provided at the surface of the carcass layer, then spraying or coating the adhesive surface with a liquid composition containing at least one aliphatic polyamide resin wherein at least part of the amide groups are modified by alkoxyalkyl groups. There is still further provided, as an air permeation preventive layer laminated through an adhesive, a pneumatic tire comprising a thin film of an aliphatic polyamide resin obtained from the cross-linking by heat treatment in the presence of an acid catalyst at least one aliphatic polyamide resin wherein at least part of the amide groups are modified with alkoxyalkyl groups. There is still further provided a process for producing a pneumatic tire comprising: spraying or coating an adhesive to the surface of a carcass layer of a green tire composed of unvulcanized rubber or the surface of a rubber layer provided at the surface of the carcass layer, then spraying or coating the adhesive surface with a solution composed of a liquid composition containing at least one aliphatic polyamide resin wherein at least part of the amide groups are modified by alkoxyalkyl groups and an acid catalyst, then vulcanizing the green tire. There is still further provided a process for producing a pneumatic tire comprising: spraying or coating an adhesive to the surface of a carcass layer of a vulcanized tire or the surface of a rubber layer provided at the surface of the carcass layer, then spraying or coating the adhesive surface with a solution comprising a liquid composition containing at least one aliphatic polyamide resin wherein at least part of the amide groups are modified with alkoxyalkyl groups and an acid catalyst. The modified aliphatic polyamide resin is one wherein at least part of the amide groups thereof are modified with an alkoxyalkyl group -R 1 -O-R 2 (wherein, R 1 is a C 1 to C 4 alkylene group, for example, a methylene, ethylene, propylene, or butylene group, R 2 is a C 1 to C 4 alkyl group, for example, methyl, ethyl, propyl, or butyl group) and/or a group having a curable unsaturated bond as mentioned below. Examples of the group having a curable unsaturated bond an N-methylol-acrylamide group, acryloyl group, methacrylol group, vinyl group or allyl group, these groups may be introduced by, for example, a reaction between an unsaturated acid chloride and >NH group of the amide group or a reaction with an N-methylol compound having an unsaturated bond. The alkoxyalkyl group may be introduced by the method of reacting methanol and para-formaldehyde with the >NH group of a polyamide in the presence of an alkali catalyst. Further, the alkoxyalkyl group and unsaturated bond may be simultaneously given. For example, they may be obtained by the method of reacting an unsaturated acid chloride to the >NH group of a polyamide to form a relatively stable >N-CO-bond, then alkoxyalkylating the remaining >NH groups or the method of effecting a dehydrogenation or dealcoholization reaction, that is, a condensation reaction, between the >NH group of the polyamide and an N-methylolate or N-alkoxyalkylate having an unsaturated bond having a good reactivity with polyamides to introduce an unsaturated bond in the side chain of the polyamide and further alkoxyalkylating the remaining >NH groups. As the polyamide, for example, linear polyamides, which are called ordinary nylons such as nylon 6, nylon 66, nylon 11, nylon 610, nylon 612, nylon 10, and nylon 6/66 and polymers having -NH 2 groups in the side chains thereof are extremely useful. Examples of the unsaturated acid chlorides are acrylic acid chloride, methacrylic acid chloride, crotonic acid chloride, and cinnamoyl chloride. Further, as the N-methylolate having the unsaturated bond are N-methylolacrylamide, N-methylolmethacryl-amide, etc. Further, examples of the N-alkoxyalkylate having an unsaturated bond are N-methoxymethylacrylamide, N-butoxymethylacrylamide, etc. Further, when alkoxyalkylating the remaining >NH groups or -NH 2 groups, the remaining groups are made to react with aldehydes, for example, formaldehyde, acetoaldehyde, etc. and alcohols, for example, methanol and ethanol. The cross-linkable elastic polyamide produced by these methods is used in an amount not detracting from the pliability suitable for a cross-linked article, that is, is made preferably 50% or less, further, more preferably 3 to 20%. Further, the flexibility given by the N-alkoxyalkylization must be stopped at the extent at which the physical properties are practical. It is preferable to use one with an N-substitution rate of 30 to 50%. The group having the unsaturated bond, for example, as disclosed in Japanese Unexamined Patent Publication (Kokai) No. 51-24677, page 2, left bottom column to right top column, is introduced into the polyamide resin by immersing a polyamide resin such as nylon 6 into an aqueous solution of N-methylol-acrylamide, ammonium chloride, and hydroquinone (or copper chloride), followed by drying and heat treating, washing with water and drying, then dissolving the reaction product in formic acid containing phenol therein, and adding thereto a formalin solution containing therein methanol, KOH, para-formaldehyde, or oxalic acid. The modified aliphatic polyamide resin is used dissolved in a solvent when to be coated. The solvent is not particularly limited so long as it is a solvent which dissolves the modified aliphatic polyamide resin. Examples of such a solvent are aliphatic alcohols such as methanol and ethanol and aromatic alcohols such as phenol and cresol Further, to these alcohol solvents, water, ethyl acetate, toluene, methyl ethyl ketone, benzene or chloroform, can be added. The concentration of the total amount of the modified aliphatic polyamide resin and cross-linking agent, curable resin, and curing agent for the curable resin is not particularly limited, but is preferably 5 to 30% by weight. Examples of the acid catalyst which may be used for cross-linking the modified aliphatic polyamide resin in the first aspect of the present invention are one or more acids selected from the group consisting of citric acid, tartaric acid, glutamic acid, lactic acid, itaconic acid, azelaic acid, succinic acid, glycolic acid, crotonic acid, hypophosphorous acid, lauric acid, chloroacetic acid, boric acid, maleic acid, oxalic acid, adipic acid, and malonic acid. An aromatic sulfonic acid may also be suitably used. Examples of such an aromatic sulfonic acid are one or more acids selected from the group consisting of p-toluenesulfonic acid, o-toluene-sulfonic acid, m-toluenesulfonic acid, benzenesulfonic acid, p-cresolsulfonic acid, o-cresolsulfonic acid, m-cresolsulfonic acid, naphthalenesulfonic acid, and dodecylbenzenesulfonic acid. The amount of the acid catalyst used may be as in the past, preferably is 3 to 5 parts by weight, based on 100 parts by weight of the modified aliphatic polyamide. Examples of the cross-linking agents other than acid catalysts which may be used for cross-linking the modified aliphatic polyamide resin in the first aspect of the present invention are sulfur alone, sulfur-releasing compounds (e.g., tetramethylthiuram disulfide, morpholine disulfide, tetraethylthiuram disulfide, tetrabutylthiuram disulfide, dipentamethylenethiuram pentamethylene, dimethyldiphenylthiuram disulfide), rubber vulcanization accelerators (e.g., thiazoles such as 2-mercaptobenzothiazole, dibenzothiazyl-disulfide, 2-mercaptobenzothiazole zinc salts, and dithio acid salts such as dichlorohexyl-benzothiazyl-sulfenamide, thiurams such as tetramethylthiuram disulfide, tetramethylthiuram monosulfide, tetraethylthiuram disulfide, and dipentamethylenethiuram tetrasulfide, and zinc dimethyldithiocarbaminate, guanidines such as diphenylguanidine, thioureas such as 1,3-diphenylthiourea) The thiurams may also be used jointly as vulcanization accelerators. The amount of these cross-linking agents used is not particularly limited as in the past, but preferably, depending on the type of the cross-linking agent used, is 0.1 to 10 parts by weight, more preferably 0.1 to 5 parts by weight, based on 100 parts by weight of the polymer. Note that in addition to the above-mentioned crosslinking agents, it is also possible to use peroxides such as dicumylperoxide (DCP). For the cross-linking agent, to smooth the cross-linking reaction, it is possible to use jointly an organic halogen donor (e.g., chlorosulfonated polyethylene or chloroprene) or an inorganic halogenated substance (e.g., stannous chloride, calcium chloride, iron chloride, aluminum chloride, zinc chloride, calcium fluoride, zinc bromide), in an amount of 0.1 to 5 parts by weight, based on 100 parts by weight of the polymer. Examples of the curable resin which may be used for curing the modified aliphatic polyamide resin in the first aspect of the present invention are epoxide compounds, which may be freely selected from glycidyl ethers, epoxyurethane resins, glycidyl ether-esters, glycidyl amine linear aliphatic epoxy resins, aliphatic epoxy resins As the curing agent for the curable resin, it is possible to use various types of curing agents such as aromatic amines, acid anhydrides, polyamides, aliphatic amines, latent curing agents but generally meta-phenylenediamine, diaminodiphenylmethane, anhydrous maleic acid, pyromellitic acid anhydrides, hexahydro anhydrous phthalic acid, and other phthalic acid anhydrides, hexamethylene diamine, and also sebacic acid dehydrazide, dicyandiamide, piperadine sebacic acid salts, may be used. The curable resin, while differing depending on the combination with the curing agent, is preferable present in an amount of 60 parts by weight or less, based on 100 parts by weight of the cross-linkable elastic polyamide. To cross-link the modified aliphatic polyamide resin, it is possible to further use an alkylphenol formalin resin or alkylresorcinol formalin resin such as described, for example, in Japanese Unexamined Patent Publication (Kokai) No. 51-18756, page 3, top left column to page 4, top right column. The first production process of the pneumatic tire will be explained with reference to the case where the inner liner layer 3 is arranged at the inside of the carcass layer 2, as shown in Fig. 1, the inner surface of the carcass layer of a green tire comprising unvulcanized rubber is coated with an adhesive, then the top thereof is sprayed or coated with at least one aliphatic polyamide resin wherein at least part of the amide groups are modified with alkoxyalkyl groups, then the green tire is vulcanized by an ordinary method, whereby the desired light weight pneumatic tire is produced. Note that the same procedure may be followed when providing the inner liner layer at the outer circumference of the carcass layer. On the other hand, when the air permeation preventive layer is arranged at the surface (that is, the inner circumference) of the carcass layer of a vulcanized tire in accordance with the present invention, the surface of the vulcanized carcass layer which has been vulcanized by an ordinary method is coated with an adhesive, then the top thereof is sprayed or coated with at least one aliphatic polyamide resin wherein at least part of the amide groups have been modified with alkoxyalkyl groups and the assembly is heated, whereby the desired light weight pneumatic tire is produced. In the production of the pneumatic tire it is possible to halogenate the surface of the carcass layer or the rubber layer on top of the same by an ordinary method. This halogenation treatment may be performed, for example, using a chlorine solution, bromine solution, iodine solution, for halogenation of general rubber. As such a solution, it is possible to use an aqueous solution including chlorine, bromine, or iodine or a dilute aqueous solution of 12N hydrochloric acid. Further, it is preferable to use a dilute solution of a compound containing -N(X)C(O)- groups (wherein X is a halogen) in an organic solvent. Specific examples of such compounds are trichloro, dichloro, or monochloro isocyanuric acid. Use of a solution of 2 to 20% by weight of trichloroisocyanuric acid in an organic solvent (for example a solution of a ketone organic solvent such as methyl ethyl ketone or a solution of an ester organic solvent such as ethyl acetate) is most preferred. Examples of the adhesive to be coated on the surface of the carcass layer in the production process of a pneumatic tire are those which undergo a bonding reaction and self-curing reaction with the rubber of the carcass layer and the resin of the air permeation preventive layer during the vulcanization by the heat of vulcanization, such as a phenol resin adhesive, a chlorinated rubber adhesive, or an isocyanate adhesive. Preferable examples of these adhesives are phenol resin types (e.g., Chemlock 234B made by LORD Co.), chlorinated rubber types (e.g., Chemlock 205 made by LORD Co.), isocyanate type (e.g., Chemlock 402 made by LORD Co.). The material of the rubber layer for bonding with the air permeation preventive layer according to the first aspect of the present invention is not particularly limited. Any rubber material which has been generally used as a rubber material for a tire in the past may be used. Examples of such a rubber are rubber compositions composed of diene rubbers such as NR, IR, BR, and SBR, halogenated butyl rubbers, ethylene-propylene copolymer rubbers, styrene elastomers, to which have been added blending agents such as carbon black, process oil, and vulcanization agents. The inner liner layer has a melting point of 80 °C or more, preferably 100 °C or more and an air permeation coefficient, measured according to JIS k7126, 25 x 10 -12 cc•cm/cm 2 •sec•cmHg (at 30°C) or less, preferably 5 x 10 -12 cc•cm/cm 2 •sec•cmHg (at 30°C) or less. When the air permeation coefficient is 25 x 10 -12 cc•cm/cm 2 •sec•cmHg (at 30°C) or less, the thickness of the inner liner layer can be made to 1/2 or less of the thickness of the conventional inner liner layers. On the other hand, the Young's modulus is 1 to 500 MPa, preferably 10 to 300 MPa, and the thickness is 0.01 to 1.0 mm, preferably 0.02 to 0.5 mm. When the Young's modulus is less than 1 MPa, wrinkles will form at the time of forming the tire, whereby handling will become difficult, while when more than 500 MPa, it is not possible for the film to follow the deformation of the tire during use. The present invention will now be further illustrated by the following Examples. Examples I-1 to I-24 and Comparative Examples I-1 to I-3 Examples I-1 to I-11 are Examples of coating an alkoxyalkylated aliphatic polyamide resin before vulcanization of the tire. The inner surface of a green tire molded by an ordinary method and composed of unvulcanized rubber is spray-coated by an adhesive, dried at room temperature for 30 minutes, then spray-coated with a solution composed of a mixed solvent of 70% by weight of methanol and 30% by weight of methyl ethyl ketone in which has been dissolved an alkoxyalkylated aliphatic polyamide resin in a proportion of 20% by weight. This is blown on by hot air of 80°C for 2 minutes, then vulcanized by a tire vulcanizer at 185°C for 15 minutes at a pressure of 2.3 MPa. Examples I-12 to I-24 and Comparative Example I-3 are examples of coating an adhesive in the same way on the inner surface of a tire vulcanized by an ordinary method under the same type of vulcanization conditions as above, followed by spray-coating with a solution prepared in the same way as mentioned above and cross-linking or curing in accordance with the cross-linking and curing conditions shown in Table II. Comparative Examples I-1 to I-2 are examples of not coating an adhesive, but halogenating the inner surface of an unvulcanized green tire or vulcanized tire (brush-coating a 3.3% solution of trichloroisocyanuric acid in ethyl acetate and drying for 2 hours). The vulcanization conditions were similar to those mentioned above. Further, the standard Example of a tire used a butyl rubber composition of the following formulation as an inner liner layer: Formulation of Butyl Rubber Compound (Unit: Parts by Weight) Br-IIR 100 Carbon black (GPF) 60 Stearic acid 1 Petroleum based hydrocarbon resin 10 Paraffinic process oil 10 Zinc oxide 3 DM 1 Sulfur 0.6 The methods of evaluation used in the following Examples were as follows: Method of Preparation of Alkoxyalkylated Aliphatic Polyamide Resin Solution Used in Tire The polymers, cross-linking agents, and other additives shown in the following formulations 1 to 8 were dissolved in a mixed solvent of 30% by weight of methyl ethyl ketone and 70% by weight of methanol to give polymer concentrations of 30% by weight. The formulations used were as shown in the following formulations 1 to 3 and formulation 8: Formulation 1 Formulation 2 Formulation 3 Formulation 8 Polymer A 100 100 100 - Polymer B *2 - - - 100 Sulfur 1.5 - - 1.5 Peroxide (di- - 1.0 - - cumylperoxide) Sulfur-releasing-agent (tetramethylthiuram disulfide) - - 1.5 - DM 3.0 - - 3.0 M 2.0 - - 2.0 MZ 2.0 - - 2.0 SnCl 2 1.0 - - 1.0 A 500 parts amount of nylon 6 and 2000 parts of formic acid were placed in a reactor provided with a reflux cover and were fully stirred to make a homogeneous solution. 3 parts of phenol and 10 parts of N-methylolacrylamide were added and the stirring continued for 30 minutes while holding the temperature at 70°C. During this process, the N-methylolacrylamide and >NH groups included in the nylon 6 molecule engaged in a dehydrogenation condensation reaction. Separately, 10 parts of KOH were added to 3000 parts of methanol held at 60°C and a homogeneous solution made, then 2500 parts of para-formaldehyde were added to cause complete dissolution. The N-methoxymethylation reaction was completed, while gradually adding this to the above nylon 6 formic acid solution. At this time, the temperature of the reaction system became 60 to 64°C. Further, the time until the end of the addition of the methanol-para-formaldehyde solution was made 10 to 15 minutes and the reaction was made to complete in 60 minutes from the start of the addition. The resultant reaction solution was poured into water and the target substance was removed. This was fully washed with water, then dried. The result was a flexible substance having a good elasticity. *2 : Polymer B: Polymer B was synthesized as follows (parts are all parts by weight). A 500 parts amount of nylon 66 and 2000 parts of formic acid were placed in a reactor provided with a reflux cover and were fully stirred to make a homogeneous solution. A 3 parts amount of phenol and 10 parts of N-methylolacrylamide were added and the stirring continued for 30 minutes, while holding the temperature at 70°C. During this process, the N-methylolacrylamide and >NH groups contained in the nylon 66 molecule caused a dehydrogenation condensation reaction. Formulation 4 Formulation 5 Luckamide 5003 100 100 Epicoat #828 15 30 (epoxide group) Sebacic acid dihydrazide (curing agent) 3.5 7.5 Formulation 6 Formulation 7 Luckamide 5003 100 100 Hitanol 1502 12 - Takkirol 250-1 - 20 Zinc oxide 3 3 Boric acid 1 - Preparation of Film Sample Solutions of alkoxyalkylated aliphatic polyamide resin of the formulations of Examples and Comparative Examples dissolved in a proportion of 20% by weight in a mixed solvent of 70% by weight of methanol and 30% by weight of methyl ethyl ketone were formed into films by the film casting method (uniformly casting a polymer solution on an endless belt, continuously drying it by blowing hot air of 60 to 90°C, then peeling to form a film). After drying, these were allowed to stand in a 130°C heater for 15 minutes for a cross-linking or curing reaction. (Film: thickness of approximately 100 µm) Method for Measurement of Melting Point A differential scan calorimeter (DSC) was used, the temperature raised at 10°C/min, and the endothermic peak temperature caused by the melting point was read or, when the peak was unclear, a thermal mechanical analysis (TMA) apparatus was used, a compression test was performed at a load of 5g, and the melting point was read from the temperature of the point of inflexion. Measurement of Air Permeation Coefficient of Air Permeation Preventive Layer According to JIS K7126 "Test Method of Gas Permeability of Plastic Films and Sheets (Method A)". Test piece: Samples of films prepared in the examples used. Test gas: Air (N 2 :O 2 = 8:2) Test temperature: 30°C Method for Measurement of Young's Modulus of Film According to JIS K6251 "Tensile Test Method of Vulcanized Rubber". Test piece: The film samples prepared above were punched into JIS No. 3 dumbbell shapes in parallel to the direction of flow of the solution (direction of flow of endless belt). A tangent was drawn to the curve of the initial strain area of the resultant stress-strain curve and the Young's modulus was found from the inclination of the tangent. Method for Measurement of Peeling Strength of Air Permeation Preventive Layer/Carcass Layer According to JIS K6258 "Test Method of Bonding of Vulcanized Rubber". Test piece: A finished tire was disassembled and short strips of a width of 25 mm were punched out in the direction of arrangement of the carcass cord. Test temperature: 20°C Test: The inner liner layer and carcass layer of a sample were partially peeled apart in advance. The layers of the sample were gripped in the chucks of a tensile tester and were peeled apart at the following tensile rate: 50.0±5.0 mm/min Method for Testing Long Term Durability A 165SR13 steel radial tire (rim 13 x 4 1/2-J) was used, was mounted on a 1500 cc class passenger car at an air pressure of 200 kPa, was subjected to a load corresponding to four passengers (65 kg/person), and was run on actual roads for 20,000 km. After use, the tire was removed from the rim and the liner layer at the inside surface of the tire was visually examined. Liner layers with cracks, visible wrinkles, or peeled or blistered liner layers were judged as failing and those without them as passing. The test was designed to evaluate as a whole the deterioration of strength, deterioration of bonding, etc. of the liner layer by actual cars. Method for Testing Long Term Water Resistance and Resistance to Moisture Absorption A 165SR13 steel radial tire (rim 13 x 4 1/2-J) was used and run on a 1707 mm drum at a speed of 80 km/h at an air pressure of 200 kPa, a load of 5.5 kN, and a room temperature of 38°C. After 10,000 km, the inside surface of the tire was visually examined. Liner layers with cracks, visible wrinkles, or peeled or blistered liner layers were judged as failing and those without them as passing. Note that just before the test run, the tire was allowed to stand for 10 days at a relative humidity of 98% and a room temperature of 70°C. Method for Testing Tire Air Leakage Performance A 165SR13 steel radial tire (rim 13 x 4 1/2-J) was used, allowed to stand at an initial pressure of 200 kPa under no-load conditions at room temperature 21°C for 3 months, and measured as to pressure every four day interval. When the measured pressure is Pt, the initial pressure is Po, and the number of days elapsed is t, the value α is found by recurrence of the function: Pt/Po = exp (-αt) The α obtained is used and t=30 substituted in the following formula to obtain β : β = [1-exp(-αt)] x 100 This value β is considered the rate of reduction of pressure per month (%/month). Formulation of Rubber for Tire Carcass Ingredient Parts by weight Natural rubber 80.0 SBR 1502 20.0 FEF carbon black 50.0 Stearic acid 2.0 Zinc oxide 3.0 Sulfur 3.0 Vulcanization accelerator (NS) 1.0 Aromatic oil 2.0 The results for the evaluation are shown in Table I-1 and Table I-2. As explained above, it is possible to obtain a pneumatic tire having an air permeation preventive layer which enables the weight of the tire to be reduced while maintaining an excellent air pressure retention in the tire and which is superior in bonding with a rubber layer.

Claims: A pneumatic tire having an air permeation preventive layer comprising a thin film of at least one aliphatic polyamide resin wherein at least part of the amide groups thereof are modified with alkoxyalkyl groups, said air permeation preventive layer being laminated through an adhesive to the surface of a carcass layer or the surface of a rubber layer provided at the surface of the carcass layer. A process for producing a pneumatic tire as defined in claim 1, comprising: spraying or coating an adhesive to the surface of a carcass layer of a green tire comprising unvulcanized rubber or the surface of a rubber layer provided at the surface of the carcass layer, then spraying or coating the adhesive surface with a liquid composition containing at least one aliphatic polyamide resin wherein at least part of the amide groups thereof are modified by alkoxyalkyl groups, and then vulcanizing the green tire. A process for producing a pneumatic tire as defined in claim 1, comprising: spraying or coating an adhesive to the surface of a carcass layer of a vulcanized tire or the surface of a rubber layer provided at the surface of the carcass layer, then spraying or coating the adhesive surface with a liquid composition containing at least one aliphatic polyamide resin wherein at least part of the amide groups thereof are modified with alkoxyalkyl groups. A pneumatic tire comprising, as an air permeation preventive layer laminated through an adhesive, a thin film of an aliphatic polyamide resin obtained by cross-linking by heat treatment in the presence of an acid catalyst at least one aliphatic polyamide resin wherein at least part of the amide groups thereof are modified with alkoxyalkyl groups. A process for the production of a pneumatic tire according to claim 4, comprising: spraying or coating an adhesive to the surface of a carcass layer of a green tire comprising unvulcanized rubber or the surface of a rubber layer provided at the surface of the carcass layer, then spraying or coating the adhesive surface with a solution comprising a liquid composition containing at least one aliphatic polyamide resin wherein at least part of the amide groups thereof are modified with alkoxyalkyl groups and an acid catalyst, and then vulcanizing the green tire. A process for producing a pneumatic tire according to claim 4, comprising: spraying or coating an adhesive to the surface of a carcass layer of a vulcanized tire or the surface of a rubber layer provided at the surface of the carcass layer, then spraying or coating the adhesive surface with a solution comprising a liquid composition- containing at least one aliphatic polyamide resin wherein at least part of the amide groups thereof are modified with alkoxyalkyl groups and an acid catalyst. A pneumatic tire as claimed in any one of the claims 1 to 6, wherein the air permeation preventive layer has a melting point of at least 80°C, an air permeation coefficient, measured according to JIS k7126, of 25 x 10 -12 cc•cm/cm 2 •sec•cmHg (at 30°C) or less, and a Young's modulus of 1 to 500 MPa. The process according to the claims 2, 3, 5 or 6, wherein the air permeation preventive layer has a melting point of at least 80°C, an air permeation coefficient measured according to JIS K 7126 of 25 x 10 -12 cc•cm/cm 2 •sec•cmHg (at 30°C) or less, and a Young's modulus of 1 to 500 MPa.

Inventors: OZAWA OSAMU, SUGA KAZUO, TAKEYAMA HIDEKAZU, YAMAKAWA KAZUTO, OZAWA, OSAMU, SUGA, KAZUO, TAKEYAMA, HIDEKAZU, YAMAKAWA, KAZUTO, Ozawa, Osamu, c/o Yokohama Rubber Co., Ltd., Suga, Kazuo, c/o Yokohama Rubber Co., Ltd., Takeyama, Hidekazu, c/o Yokohama Rubber Co., Ltd., Yamakawa, Kazuto, c/o Yokohama Rubber Co., Ltd.
Applicants: YOKOHAMA RUBBER CO LTD, THE YOKOHAMA RUBBER CO., LTD.
Application year: 1996
Main classification: B60C1
IPC codes: B60C1, C08G69, C08L77, B60C5