WATER-BASED ADHESIVE FORMULATION HAVING ENHANCED CHARACTERISTICS

Abstract: Adhesive formulations are blends of aqueous polymer dispersions and a hydrophobic plasticizer. The blended dispersed polymers include at least one hard sulfonated polyester urethane, at least one soft non-sulfonated polyester urethane, and at least one polar non-polyurethane water-based polymer or copolymer. A high molecular weight elastomeric non-sulfonated polyurethane polymer and a crosslinker are optional further components in the blend. The formulations are useful as non-heat activating, one-component adhesive s which generate excellent green strength, water and heat resistant bonds.

Description: WATER-BASED ADHESIVE FORMULATION HAVING ENHANCED CHARACTERISTICS Background of the Invention Field of the Invention This invention relates to a new water-based adhesive formulation. Specifically, a formulation having enhanced characteristics such as excellent adhesion without heat activation. More specifically, it relates to a one-component aqueous sulfonated polyurethane adhesive formulation having enhanced properties for use in applications where use of heat for activation is undesirable or unavailable. Description of the Prior Art Aqueous polyurethane dispersions have received a great deal of attention recently. These dispersions arc compatible with many other water-based polymers, and adhesives made from them usually exhibit improved performance. Examples of these activities can be found in JP 57030776 and JP 83046277. These patents disclose heat curing, water-resistant and stable adhesive compositions comprising dispersions of partially saponified polyvinyl acetate, aqueous solutions of polyurethanes and dispcrsable polyisocyanatc compounds. The adhesive properties of these compositions are generated with a heat curing cycle. JP 6256749 discloses another adhesive composition prepared by adding polyisocyanatc crosslinking agents to a blend of aqueous polyurethane resins and polyvinyl latex. -This polyurethane based adhesive composition is reported to exhibit high adhesion, and excellent heat and water resistance. German Utility Model patent no. 9304018 discloses an adhesive comprising at least a two component polyurethane dispersion having a pot life of 12 hours. This water-based formulation describes a polymer blend of polyurethane dispersions, EVA's or mcthacrylic derivatives, characterized in that it comprises one essentially non-hydrophobic plasticizer. A draw back for these prior art compositions is the need for heat activation, making them unsuitable for use where heat for activation is either unavailable or destructive to the substrates or parts being bonded together. - o . The present inventors have now discovered a one-component sulfonated aqueous polyurethane dispersion based adhesive formulation having excellent adhesive properties, good green strength, solvent resistance, and capable of forming moisture and heat resistant bonds without heat activation. Summary of the Invention The present invention is directed to a novel adhesive formulation comprising plasticizcd aqueous polyurethane dispersion blends. The formulations of the invention provide excellent adhesion properties upon pressurized joining of coated substrates. This adhesion property, without heat activation, and the unexpected heat resistant properties of the resulting bonds on aging, are believed to be unique properties for polyurethane dispersion adhesive formulations. The inventive adhesive formulations have properties superior to polychloroprene (e.g. Neoprcnc ® ) based contact adhesives, have good green strength and moisture resistance and can be spray-coagulated with acids (e.g. by HYDROpHUSE™ process). The preferred formulations of the invention, when used with a crosslinker, have very long pot-lives, in some cases up to a month or more after addition of the crosslinker. Surprisingly, such formulations even after a month exhibit excellent green strength characteristics without heat activation. This allows formulations containing crosslinking additives to be shipped by the manufacturer as one-component compositions, and provides a substantially improved convenience to the end user. The applied adhesive films have a useful life or "open time" (time between the making of said films and the using of said films to form the bonded structure) ranging from about an hour to a few hours, depending on the composition of the dispersion and the crosslinkers chosen. The invention is also directed to the use of the inventive formulations as adhesives and to an adhesively bonded structure comprising said formulation as the adhesive. The inventive adhesive formulations comprise: a) at least one hydrophobic plasticizer, for instance a member of the group consisting of alkyl and aryl sulfonamides, benzoate esters, phthalatc esters, adipatcs, citrates, and mixtures thereof; and b) an aqueous polyurethane dispersion blend comprising: 1) at least one hard sulfonated polyester urethane; 2) at least one soft non-sulfonated polyester urethane; and 3) at least one polar non-polyurcthane water-based polymer or copolymer. A high molecular weight non-sulfonated polyurethane polymer and/ or a crosslinker, such as a dispensable polyisocyanatc crosslinker, are optional components employed in preferred embodiments of the invention. The invention also relates to a polyurethane dispersion based adhesive formulation containing an interpenetrating network having crosslinkcd matrixes for improved heat, moisture and solvent resistance, and to the process of manufacture and use of the same. Detailed Description of the Invention In the inventive adhesive formulations an aqueous polyurethane dispersion blend is employed which includes at least one "hard" sulfonated polyester urethane, at least one "soft" non-sulfonated polyester urethane; and at least one polar non-polyurcthane water-based polymer or copolymer. The "hard" sulfonated polyester polyurethane is a relatively high molecular weight anionic sulfonated polyester urethane polymer which is characterized by a shear storage modulus (G') having a value of from about 10" to about 10 10 dynes/cm- at 25°C and a frequency of 10 radians/sec. The relatively high molecular weight, polyurethane useful as the hard polyurethane in the aqueous polyurethane dispersion blends of the present invention can be linear aliphatic, cyclic aliphatic, or aromatic sulfonated polyester urethanes, preferably formed from at least one sulfonated polyaminc or polyol and one or more diisocyanates. A suitable example of such a sulfonated polyester polyurethane dispersion is Dispercoll™ KA-8464, sold by Mobay Corporation. Pittsburgh, Pennsylvania. The hard polyurethane dispersion solids may comprise from about 15 parts to about 35 parts, preferably from about 20 parts to about 30 parts, based on 100 parts total solids. The "soft" non-sulfonated polyurethane component of the inventive blends is a relatively low molecular weight polyurethane polymer characterized by a shear storage modulus (G') having a value of from about 10 f> dynes/cm 2 to about 10 x dynes/cm 2 at 25°C and 10 radians/sec. It can be formed from linear aliphatic, cyclic aliphatic, or aromatic non-sulfonated polyester urcthanes, preferably formed from diisocyanatcs such as isophoronc diisocyanate (IPDI), hexamcthylcnc diisocyanate (HDI), tetramelhylxylylenc diisocyanate (TMXDI), and mixtures thereof. Such polymers arc tacky and give the final adhesive composition added tack and improved initial green strength characteristics. The soft polyurethane dispersion solids arc present from about 15 parts to about 35 parts and preferably from about 20 parts to about 30 parts, based on 100 parts total solids. The blended dispersion also includes a polar, non-polyurethane water-based polymer or copolymer component. Addition of at least one such polar, water-based polymer or copolymer can improve the sprayability of the dispersion. Examples of these polymers or copolymers include vinyl acclatc-ethylene copolymers, acrylic polymers, vinyl acetate polymers and other vinyl polymers. The polar, non-polyurethane water-based polymer or copolymer solids comprise from about 5 parts to about 40 parts, and preferably from about 5 parts to about 15 parts, based on 100 parts total solids. The inventive formulations also include a hydrophobic plasticizcr. The hydrophobic plasticizers enhance the water resistance properties of the adhesive. They can be selected from the group consisting of alkyl and aryl sulfonamides, benzoate esters, phthalate esters, adipatcs, citrates, and mixtures thereof. Particularly preferred are alkyl sulfonamides, aryl sulfonamides, alkylenc glycol benzoates, dialkylene glycol benzoates, and mixtures thereof. The amount of plasticizer present in the adhes 'e composition can vary from about 1 part to 40 parts, and preferably from about 20 parts to about 40 parts, based on 100 parts total solids. The sulfonated polyester urcthanes contain ionomcrs capable of strong hydrogen bonding and ionic dipole interactions. These strong intermolecular forces give the polymers improved heat and water resistance, as well as good adhesive properties. These same high inter-molecular forces also oppose plasticization. This is well known in the art. The documentation can be found in the proceedings of the Plasticization and Plaslicizcr Processes symposium sponsored by the Division of Industrial and Engineering Chemistry at the 147th meeting of the American Chemical Society, Philadelphia, Pa., April 6-7, 1964. The adhesive compositions of the present invention surprisingly possess good adhesive properties without heat activation, using hydrophobic plasticizers. Λ preferred embodiment can comprise : a) at least one hydrophobic plasticizer selected from the group consisting of alkyl and aryl sulfonamides, bcnzoate esters, phthalate esters, adipates, citrates, and mixtures thereof; and b) an aqueous polyurethane dispersion comprising 1 ) at least one high molecular weight sulfonated polyester urethane; 2) at least one high molecular weight non-sulfonated polyester urethane; 3) at least one tacky non-sulfonated polyester urethane; and 4) at least one polar non-polyurcthane water-based polymer or copolymer. In this embodiment the non-sulfonated high molecular weight polyester urcthanes can be crystalline or semi-crystalline linear aliphatic, cyclic aliphatic, or aromatic polyester urethanes, preferably also formed from diisocyanatcs such as isophorone diisocyanate (IPDI), hexamethylenediisocyanate (HDI), and mixtures thereof. Preferably this component has clastomcric properties. It may comprise from about 10 parts to about 30 parts, preferably from about 15 parts to about 25 parts, based on 100 parts total solids. The adhesive compositions of the present invention may include a water dispersable crosslinker. Conventional water-dispcrsiblc polyfunctional chemically activatable crosslinking agents arc useful for the present invention. These crosslinking agents include dispersable formulations of polyfunctional aziridines, isocyanates, mclamine resins, cpoxics, oxazolincs, carbodiimides and other polyfunctional crossl inkers. Typically, the crosslinking agents are added at a level of about 1 to about 20 parts, preferably from about 5 parts to about 15 parts based on 100 parts total solids. It is surmised that when crosslinking agents arc added to the polyurethane dispersion adhesive composition, an interpenetrating or interconnected network having crosslinked matrixes is formed which link the blended polymers with covalcnt and/or non-covalent linkages. The crosslinked network gives the adhesive composition further improved heat, moisture and solvent resistance. A surprising feature of preferred embodiments of the invention is that the crosslinker can be added to the adhesives at least a month before use without destabilizing (gelling or high sedimentation) the system. Therefore the crosslinked compositions can be prepared by the supplier before shipping to the end user. The crosslinked or uncrosslinked adhesives of the invention, in some cases, can be applied to one or both substrates and subsequently successfully bonded, with pressure but without heat, as long as several hours later and still give adhesive strength properties which are similar to those obtained when the substrates arc joined promptly after application and drying or coagulation of the adhesive. This is a further significant advance in the art of aqueous dispersion adhesives since it allows for separation of the adhesive application and bonding steps so that the adhesive can be prcapplicd, for instance in a batch process and then bonded assemblies can be subsequently prepared on a batch basis. An especially preferred embodiment of the invention is an adhesive composition which comprises : a) at least one hydrophobic plasticizcr selected from the group consisting of alkyl and aryl sulfonamides, benzoate esters, phlhalate esters, adipates, citrates, and mixtures thereof; and b) an aqueous polyurethane dispersion comprising 1) at least one high molecular weight sulfonated polyester urethane; 2) at least one high molecular weight non-sulfonated polyester urethane; 3) at least one tacky non-sulfonated polyester urethane; and 4) at least one polar non-polyurethane water-based polymer or copolymer; and c) at least one polyfunctional crosslinking agent selected from the group consisting of chemically activatable crosslinkers. To prepare the adhesive formulations of the invention the aqueous polymer dispersions are blended together with mild agitation and then the hydrophobic plasticizer is added. Crosslinkers arc added last. Application of the adhesive formulations of the invention can be accomplished in either one-side mode or two-side mode. In the one-side mode the adhesive is applied to one of two substrates to be joined and dried, coagulated with acid or spray coagulated (acid added in spray droplet) for instance by the HYDROpHUSE™ process. The second substrate is then brought into contact with the adhesive coated substrate with pressure. In the two-side mode the adhesive is applied to both substrates to be joined and then the substrates are brought together with pressure. The fact that heat activation is not required to accomplish bonding gives the formulations the characteristics of contact adhesives, a unique characteristic for polyurethane dispersion adhesives. It is especially surprising that even the crosslinked adhesive compositions possess good adhesive properties without heat activation. These adhesives can be used either in the aqueous dispersion form, or in the form of a cast film, to bond both porous and non-porous substrates, for applications in the automotive, aerospace, and others where regular heat activatablc and/or heat curing polyurethane dispersion adhesive formulations are being used. They are especially useful in applications where the use of heat for activation is either not available or destructive to the substrates. Such applications can include film to film lamination. Although not necessary to obtain good bonding, substrates coated with formulations of the invention can also be bonded with heat activation if desired. The present invention is further illustrated by the following non- limiting examples. All parts are by weight unless otherwise specified. Examples In the following examples the following test methods were used. Test 1. Peel Adhesion (Non-porous Substrates) The samples for testing were prepared in the following manner. The adhesive formulations were coated on two 15.2 cm by 17.8 cm sheets of polyvinyl chloride (PVC) using a #40 Meyer rod. The substrates were then dried at room temperature and pressed together using a Seminal Heat sealer at room temperature for 30 sec. at 206.8 kPa (30 psi) nip pressure. After aging at ambient conditions for 72 hours, the sheets were cut into 2.5 cm by 17.8 cm strips and tested for peel adhesion on the Twing Albert 500. Test 2. Peel Adhesion Failure Temperatures (Porous Substrates) The samples for testing were prepared and tested in the same manner as Test 1 , except that the substrates used were 2.5 cm by 2.5 cm samples of canvas which were bonded in a T-peel configuration and placed in the Tenney oven. The T-pecls were ubjected to a 25 °C increase in temperature each hour until bond failure, and the temperatures and the times were recorded by the Tenney sensing unit. Test 3. Peel Adhesion (Mixed Non-porous Substrates) The samples for testing were prepared and tested in the same manner as Test 1 , except that one substrate was ΛBS (acrylonitrile-butadicne-styrcnc block copolymer) and the other substrate was PVC. Bonds were assembled with a pressure of 206.8 kPa (30 psi) 30 sec. at room temperature and at 82°C (180°F). Bonded assemblies were prepared as in Test 1 and tested for green strength promptly after bonding and then after aging the bond for 3 weeks. In the formulations described below, component quantities arc given in parts by weight. Examples 1 -4 Blended formulations were prepared as shown in Table 1 below. After formulation of the blended adhesive, the formulations were subjected to Peel Adhesion testing under the conditions specified above for Tests 1 and 2 above. Results arc shown in Table 1 below. Table Example Components 1 2 j -> 4 Hard Sulfonated Polyester Polyurethane 36.57 34.74 36.57 34.74 (Dispcrcoll -8464, Miles Inc.) High Mol. Wt. Non-Sulfonatcd Polyurethane 12.29 1 1.67 12.29 1 1.67 ( eorcz R-9630, Zcneca Resins) Soft Tacky Non-Sulfonatcd Polyurethane 26.13 24.84 26.13 24.84 (Neorez R-9320, Zeneca Resins) Hydrophobic Sulfonamide Plasticizer 15.49 14.71 — — (Uniplex 108, Unitcx Chemical) Hydrophobic Benzoalc Plasticizer (Bcnzollcx — — 15.49 14.71 50) Vinyl acetate cthylcnc copolymer emulsion 9.52 9.04 9.52 9.04 (Airflcx 320, Air Products Inc.) Polyisocyanatc crosslinker (Dcsmondur DΛ, — 5.00 — 5.00 Miles Inc.) Test Results Test 1 ( kg/cm) 3.24 2.93 2.40 2.69 Test 2 (°C) 46 79 60 101 Examples 5-7 Formulations were prepared as shown in Table 2 below in the same manner as described for Examples 1 -4. Testing was the same as for Examples 1-4 except that the Example 7 formulation was also subjected to Test 3, described above. Test results are also given in Table 2. Example 5 is a comparative formulation which does not include the hydrophobic plasticizer component of the inventive formulations. Table 2 Example Comparative Invention 5 6 7 Hard Sulfonated Polyester Polyurethane 43.27 36.57 34.82 (Dispercoll -8464) High Mol. Wt. Non-Sulfonatcd 30.91 26.13 24.88 Polyurethane (Ncorcz R-9630) Soft Tacky Non-Sulfonatcd Polyurethane 14.54 12.29 1 1.70 (Ncorcz R-9320) Hydrophobic Plasticizer (N-ethyl-toluenc — 15.49 14.76 sulfonamide mixture Hydrophilic Plasticizer (Triacctin) — — — Vinyl acetate ethylcne copolymer emulsion 1 1.28 9.52 9.07 (Airflex 320) Polyisocyanatc crosslinker (Dcsmondur — — 4.77 DA) Test Results Test 1 ( kg/cm) 0. 1 1 3.24 2.93 Test 2 (°C) 61 46 79 Test 3 (kg/cm) - Immediately Room Temp 2.50 [82°C] 0.95 Test 3 (kg/cm) - Aged 3 weeks Room Temp 1.72 [82°C] 0.91 Example 8 A formulation was prepared as in Example 1 using the following components: Dispercoll K-8464 35.4 Neorez R-9630 25.3 Neorez R-9320 1 1.9 Uniplex 108 15.0 Airflex 320 9.2 Desmondur DA 5.0 The adhesive was applied with a paint brush to chrome leather, SBR rubber sheet and suede leather samples and allowed to dry. Contact bonds were formed at room temperature with hand pressure between adhesive coated samples of chrome leather and SBR sheet and between adhesive coated SBR rubber sheet and suede leather. When pulled apart, both samples failed by substrate failure of the leather substrate indicating that the adhesive bond was stronger than the substrate, and demonstrating the utility of the adhesive as a cold contact shoe adhesive. The same adhesive was applied with a paint brush to ponderosa pine blocks 7.5 cm x 7.5 cm square, allowed to dry for 10-15 minutes and then contact bonded with hand pressure at room temperature. The samples produced immediate strength which could not be broken by hand shear or torsion forces. When pried apart with a hammer and chisel the bond broke by wood failure, demonstrating the utility of the adhesive as a cold contact wood adhesive. Example 9 An adhesive formulation as described in the previous example was tested for carpct-to-fiberglass (glass fiber/polyester laminate) wet and dry peel strength. The samples were prepared for testing by spray application to both surfaces at a dry spread rate of 54 g/nr (5 g/ft 2 ). The adhesive were spray- coagulated (HYDROpHUSE™) with a Mattson Crossfire™ spray gun using a dilute solution of citric acid as the acid which is mixed in the spray process. Carpet laminations were made on both the gel coat and the rough side of marine fiberglass. The coated substrates were immediately joined with a 2.3 kg (5 lb) hand roller. 180° peel tests were completed after aging of the resulting bonded assembly for 7 days at ambient conditions. The test instrument was a 3M90 peel tester run at 30 cc/min, 30 sec. peel. Bonded and aged assemblies prepared in the same manner as described in the previous paragraph were placed in 22°C water for 24 hours after which peel strengths were measured in the same manner. In addition to the formulation of Example 8 with citric acid coagulation, a competitive water based adhesive 3M Fastbond™ 2000 NF, spray- coagulated with Fastbond™ zinc sulfate, and a commercial SBR solvent cement, spray applied, were tested in the same manner. It was noted that the diisocyanate crosslinker employed in the formulation of Example 8 could not be satisfactorily added to the Fastbond 2000 NF formulation because the pot-life was too short in the high pM system of that adhesive. Results are given in Table 3 where all values arc kg/cm. Table 3 Dry Wet Product Gel Coat Side Rough Side Gel Coat Side Rough Side Example 8 2.1 1.4 2.1 1.0 SBR solvent cement 0.8 1.0 0.7 0.1 3M Fastbond 2000 0.9 0.5 0.9 0.2 NF

Claims: - I J - CLAIMS What is claimed is: 1. An adhesive formulation comprising a dispersion in an aqueous media of: 5 a) at least one hydrophobic plasticizer, and b) a blended mixture of dispersed polymers, the mixture comprising: 1) at least one hard sulfonated polyester urethane; 2) al least one soft non-sulfonated polyester urethane; and 3) at least one polar non-polyurcthane water-based polymer 0 or copolymer. 2. An adhesive as in claim 1 wherein the hard sulfonated polyester polyurethane is an anionic sulfonated polyester urethane polymer which is characterized by a shear storage modulus (G') having a value of from about 10 y to 15 about 10 10 dynes/cm 2 at 25°C and a frequency of 10 radians/sec. 3. An adhesive as in claim 1 wherein the hard sulfonated polyester polyurethane is a linear aliphatic, cyclic aliphatic, or aromatic sulfonated polyester urethane. 0 4. An adhesive as in claim 3 wherein the hard sulfonated polyester polyurethane is from al least one sulfonated polyester polyol. al least one aliphatic diol, and at least one diisocyanate. 25 5. An adhesive as in claim 4 wherein said diisocyanate is isophorone diisocyanate (IPDI), hexamcthylcncdiisocyanatc (HDI), or a mixtures thereof. 6. An adhesive as in claim 1 wherein the hard sulfonated polyester polyurethane is a high molecular weight crystallizing sulfonated polyurethane. J 0 7. An adhesive as in claim 1 wherein the hard sulfonated polyurethane solids comprise from about 15 parts to about 35 parts, based on 100 parts total solids. 8. An adhesive as in claim 1 wherein the soft polyurethane is characterized by a shear storage modulus (C) having a value of from about 10" dynes/cm 2 to about 10 s dynes/cm 2 at 25°C and 10 radians/sec. 9. An adhesive as in claim 8 wherein said soft polyurethane is a low molecular weight tacky, polymer formed from at least one linear aliphatic, cyclic aliphatic, or aromatic non-sulfonated polyester and al least one diisocyanate. 10. An adhesive as in claim 9 wherein said diisocyanate is isophorone diisocyanate (IPDI), hcxamethylcnediisocyanale (I IDI), and mixtures thereof. 1 1. An adhesive as in claim 1 wherein said soft polyurethane is present in an amount of from about 15 parts to about 35 parts, based on 100 parts total solids. 12. An adhesive as in claim 1 wherein the polar, non-polyurcthane water-based polymer or copolymer is a member of the group consisting of vinyl acetate polymers and copolymers, acrylic polymers, and epoxy polymers. 13. An adhesive as in claim 1 wherein the polar, non-polyurcthane water-based polymer or copolymer is present in an amount of from about 5 parts to about 40 parts, based on 100 parts total solids. 14. An adhesive as in claim 1 wherein the hydrophobic plasticizer is selected from the group consisting of alkyl and aryl sulfonamides, benzoate esters, phthalate esters, adipates, citrates, and mixtures thereof. 15. An adhesive as in claim 1 wherein the hydrophobic plasticizer is present in the adhesive composition in an amount of from about 20 part to 40 parts by weight, based on 100 parts total solids. 16. An adhesive as in claim 1 further comprising at least one high molecular weight non-sulfonated polyester urethane. 17. An adhesive as in claim 16 wherein said one high molecular weight non-sulfonated polyester urethane is formed from at least one linear aliphatic, cyclic aliphatic, or aromatic non-sulfonated polyester and at least one diisocyanate. 18. " Λn adhesive as in claim 17 wherein said diisocyanate is isophorone diisocyanate (IPDI), hcxamethylenediisocyanatc (HDI), and mixtures thereof. 19. An adhesive as in claim 16 wherein said high molecular weight non- sulfonated polyester urethane is an elastomer. 20. Λn adhesive as in claim 16 wherein said high molecular weight non-sulfonated polyester urethane is present in an amount of from about 10 parts to about 30 parts, based on 100 parts total solids. 21. An adhesive as in claim 1 further comprising at least one water dispersable polyfunctional crosslinking agent. 22. An adhesive as in claim 21 wherein said crosslinking agent is selected from the group consisting of polyfunctional aziridincs, isocyanatcs, melaminc resins, cpoxics, oxazolincs and carbodiimides. 23. An adhesive as in claim 21 wherein the crosslinking agent is present in the adhesive in an amount of from about 1 to about 20 parts, based 100 parts total solids. 24 A method of bonding a pair of substrates comprising applying an adhesive dispersion as in claim 1 to at least one of said substrates, drying or coagulating said dispersion and then joining the two substrates together with pressure. 25 A method as in claim 24 wherein said substrates are joined without heat activation. 26. A method as in claim 24 wherein said substrates are joined with heat activation. 27. A method as in claim 24 wherein said adhesive dispersion further comprises a crosslinker provided to the dispersion prior to said applying step and said joining step is performed more than 24 hours after said crosslinker is provided to the adhesive dispersion. 28. A method as in claim 24 wherein said adhesive is dried before said joining step. 29. A method as in claim 24 wherein said adhesive is coagulated before said joining step. 30. A method as in claim 24 wherein said coagulation step is accomplished by spray coagulating with a co-sprayed acid. 31. A bonded assembly comprising a pair of substrates adhesively bonded wherein said adhesive is a dried or coagulated dispersion of an adhesive dispersion as in claim 1. 32. An bonded assembly as in claim 31 wherein at least one of said substrates is a member of the group consisting of leather, rubber, synthetic polymers and wood. 33. A bonded assembly as in claim 31 wherein said assembly is a shoe. 34. Λn adhesive formulation comprising a dispersion in an aqueous media of: a) at least one hydrophobic plasticizer selected from the group consisting of alkyl and aryl sulfonamides, benzoate esters, phthalate esters, adipates, citrates, and mixtures thereof; and b) an aqueous polyurethane dispersion comprising 1 ) at least one anionic sulfonated polyester urethane polymer which is characterized by a shear storage modulus (G') having a value of from about 10 v to about 10'" dynes/cm 2 at 25°C and a frequency of 10 radians/sec; 5 2) at least one high molecular weight clastomcric non- sulfonated polyester urethane; 3) at least one tacky non-sulfonated polyester urethane which is characterized by a shear storage modulus (G') having a value of from about 10'' dynes/cm 2 to about 10 s dynes/cnr at 0 25°C and 10 radians/sec; and c) at least one polar non-polyurcthane polymer selected from the group consisting of vinyl acetate polymers and copolymers, acrylic polymers, and epoxy polymers. 15 35. An adhesive as in claim 34 further comprising at least one polyfunctional crosslinking agent selected from the group consisting of polyfunctional aziridines, isoeyanates, melamine resins, epoxies, oxazolines and carbodiimidcs. 0 36. An adhesive as in claim 35 wherein the component solids arc present in respective relative amounts by weight as follows: hydrophobic plasticizer 20 - 40 parts; anionic sulfonated polyester urethane polymer 15 - 35 parts; high molecular weight clastomcric 25 non-sulfonated polyester urethane 10 - 30 parts; tacky non-sulfonated polyester urethane 5 - 15 parts; polar non-polyurethane water-based polymer 5 - 40 parts. crosslinking agent 1 - 20 parts. J 0 37. An adhesive as in claim 35 wherein said crosslinking agent is a dispersable polyisocyanatc

Inventors: DOCKNIAK MICHAEL, HAIDER GARY, JANNUSCH LEONARD, MAKSYMKIW MIKE, WADE PAUL, DOCKNIAK, MICHAEL, HAIDER, GARY, JANNUSCH, LEONARD, MAKSYMKIW, MIKE, WADE, PAUL
Applicants: FULLER H B LICENSING FINANC, H.B. FULLER LICENSING & FINANCING, INC.
Application year: 1996
Main classification: C08G18
IPC codes: C09J175