Curable coating composition including compound having carbamate and hydroxyl functionality

Abstract: A curable coating composition is described comprising (A) a compound comprising carbamate or urea and hydroxyl functional groups that is the reaction product of (1) a compound comprising a carbamate or urea group or a group that can be converted to a carbamate or urea group, and an active hydrogen group that is reactive with a lactone or a hydroxy carboxylic acid, and (2) a lactone or a hydroxy carboxylic acid, (B) a compound comprising at least one group that is reactive with carbamate and at least one group that is reactive with hydroxyl, or a plurality of groups that are reactive with both carbamate and hydroxyl.

Description: This invention relates to curable coating compositions, particularly to curable compositions utilizing a primary carbamate- or primary urea-functional compound as one of the components of the composition. Curable coating compositions such as thermoset coatings are widely used in the coatings art. They are often used for topcoats in the automotive and industrial coatings industry. Color-plus-clear composite coatings are particularly useful as topcoats where exceptional gloss, depth of color, distinctness of image, or special metallic effects are desired. The automotive industry has made extensive use of these coatings for automotive body panels. Color-plus-clear composite coatings, however, require an extremely high degree of clarity in the clearcoat to achieve the desired visual effect. High-gloss coatings also require a low degree of visual aberations at the surface of the coating in order to achieve the desired visual effect such as high distinctness of image (DOI). Such coatings are especially susceptible to a phenomenon known as environmental etch. Environmental etch manifests itself as spots or marks on or in the finish of the coating that often cannot be rubbed out. Curable coating compositions based on curable components having carbamate or urea functionality have been proposed have been described in the art to provide etch-resistant coatings, e.g., U.S. Patent 5,356,669 and WO 94/10211. In addition to resistance to environmental etch, a number of other characteristics can be desireable. For example, it may be desireable to provide a coating having a high degree of flexibility. This can be particularly advantageous if the substrate on which the coating is placed is itself flexible, as in the case of plastic, leather, or textile substrates. It is also desirable to reduce the amount of solvent required in coating compositions in order to reduce the volatile organic content (VOC), which is better for the environment. Finally, it is desirable to provide options of different types of carbamate- or urea-functional materials to provide coatings with a good combination of properties such as durability, hardness, and resistance to scratching, marring, solvents, and acids. Summary of the Invention According to the present invention, there is provided a coating composition comprising (A) a compound comprising primary carbamate or primary urea and hydroxyl functional groups that is the reaction product of (1) a compound comprising a primary carbamate or primary urea group or a group that can be converted to a primary carbamate or primary urea group, and an active hydrogen group that is reactive with (A) (2), and (2) a lactone or a hydroxy carboxylic acid, (B) a compound comprising at least one group that is reactive with carbamate and at least one group that is reactive with hydroxyl, or a plurality of groups that are reactive with both carbamate and hydroxyl. The present invention provides coatings having a good combination of properties such as durability, hardness, and resistance to scratching, marring, solvents, and acids. Coating compositions according to the invention can also provide low VOC levels, and can be used to prepare coatings having good flexibility for use over flexible substrates. Description of the Preferred Embodiments According to the present invention, compound (A) has primary carbamate or primary urea functionality and hydroxyl functionality, and is the reaction product of the compound having at least one primary carbamate or primary urea group (or a group that can be converted to primary carbamate or primary urea) and an active hydrogen group (A) (1) with the lactone or hydroxy carboxylic acid(A) (2). Primary carbamate groups can generally be characterized by the formula Primary urea groups can generally be characterized by the formula wherein R represents H or alkyl, preferably of 1 to 4 carbon atoms. The compound (A) can be formed by reacting a lactone or hydroxy carboxylic acid with a compound having an active hydrogen group capable of undergoing a condensation reaction with the acid group of the hydroxy carboxylic acid or ring-opening the lactone (e.g., hydroxyl, primary amine, acid) and a primary carbamate or primary urea group or a group that can be converted to primary carbamate or primary urea. When a compound having an active hydrogen group and a group that can be converted to primary carbamate or primary urea is used to react with the lactone or hydroxy carboxylic acid, conversion of the group to a primary carbamate or primary urea can be accomplished during or after the ring-opening reaction. Compounds having a primary carbamate or primary urea group and an active hydrogen group are known in the art. Hydroxypropyl carbamate and hydroxyethyl ethylene urea, for example, are well known and commercially available. Amino carbamates are described in U.S. Patent 2,842,523. Hydroxyl ureas may also be prepared by reacting an oxazolidone with ammonia or a primary amine or by reacting ethylene oxide with ammonia to form an amino alcohol and then reacting the amine group of that compound or any other amino alcohol with hydrochloric acid, then urea to form a hydroxy urea. Amino ureas can be prepared, for example, by reacting a ketone with a diamine having one amine group protected from reaction (e.g., by steric hindrance), followed by reaction with HNCO (i.e., the product of the thermal decomposition of urea), and then water. Alternatively, these compounds can be prepared by starting with a compound having an active hydrogen and a group that can be converted to primary carbamate or primary urea as described below, and then converting that group to the primary carbamate or primary urea prior to commencement of the reaction with the lactone or hydroxy carboxylic acid. Groups that can be converted to primary carbamate include cyclic carbonate groups, epoxy groups, and unsaturated bonds. Cyclic carbonate groups can be converted to primary carbamate groups by reaction with ammonia, which ring-opens the cyclic carbonate to form a β-hydroxy primary carbamate. Epoxy groups can be converted to carbamate groups by first converting to a cyclic carbonate group by reaction with CO 2 . This can be done at any pressure from atmospheric up to supercritical CO 2 pressures, but is preferably under elevated pressure (e.g., 60-150 psi). The temperature for this reaction is preferably 60-150°C. Useful catalysts include any that activate an oxirane ring, such as tertiary amine or quaternary salts (e.g., tetramethyl ammonium bromide), combinations of complex organotin halides and alkyl phosphonium halides (e.g., (CH 3 ) 3 SnI, Bu 4 SnI, Bu 4 PI, and (CH 3 ) 4 PI), potassium salts (e.g., K 2 CO 3 , KI) preferably in combination with crown ethers, tin octoate, calcium octoate, and the like. The cyclic carbonate group can then be converted to a primary carbamate group as described above. Any unsaturated bond can be converted to carbamate groups by first reacting with peroxide to convert to an epoxy group, then with CO 2 to form a cyclic carbonate, and then with ammonia to form the primary carbamate. Other groups, such as hydroxyl groups or isocyanate groups can also be converted to primary carbamate groups to form a compound (A) (1). However, if such groups were to be present on the compound (A) (1) and then converted to primary carbamate after the reacting with the lactone or hydroxy carboxylic acid, they would have to be blocked so that they would not react with the lactone, the hydroxy carboxylic acid, or with the active hydrogen groups. When blocking these groups is not feasible, the conversion to primary carbamate or primary urea would have to be completed prior to reaction with the lactone or hydroxy carboxylic acid. Hydroxyl groups can be converted to primary carbamate groups by reaction with cyanic acid (which may be formed in situ by thermal decomposition of urea). This reaction preferably occurs in the presence of a catalyst as is known in the art. A hydroxyl group can also be reacted with phosgene and then ammonia to form a compound having primary carbamate group(s). Another approach is to react an isocyanate with a compound such as hydroxyalkyl primary carbamate to form a primary carbamate-capped isocyanate derivative. For example, one isocyanate group on toluene diisocyanate can be reacted with hydroxypropyl carbamate, followed by reaction of the other isocyanate group with an excess of polyol to form a hydroxy carbamate. Finally, carbamates can be prepared by a transesterification approach where hydroxyl group reacted with an alkyl carbamate (e.g., methyl carbamate, ethyl carbamate, butyl carbamate) to form a primary carbamate group-containing compound. This reaction is performed under heat, preferably in the presence of a catalyst such as an organometallic catalyst (e.g., dibutyltin dilaurate). Other techniques for preparing carbamates are also known in the art and are described, for example, in P. Adams & F. Baron, "Esters of Carbamic Acid", Chemical Review, v. 65, 1965. Groups such as oxazolidone can also be converted to urea after reaction with the lactone or hydroxy carboxylic acid. For example, hydroxyethyl oxazolidone can be used to react with the lactone or hydroxy carboxylic acid, followed by reaction of ammonia or a primary amine with the oxazolidone to generate the urea functional group. Other groups, such as amino groups or isocyanate groups can also be converted to urea groups to form a compound (A) (1). However, if such groups were to be present on the compound (A) (1) and then converted to urea after reaction with the lactone or hydroxy carboxylic acid, they would have to be blocked so that they would not react with the lactone, the hydroxy carboxylic acid, or with the active hydrogen groups. When blocking these groups is not feasible, the conversion to carbamate or urea would have to be completed prior to the reaction with the lactone or hydroxy carboxylic acid. Amino groups can be converted to urea groups by reaction with a monoisocyanate (e.g., methyl isocyanate) to form a secondary urea group or with cyanic acid (which may be formed in situ by thermal decomposition of urea) to form a primary urea group. This reaction preferably occurs in the presence of a catalyst as is known in the art. An amino group can also be reacted with phosgene and then ammonia to form a compound having primary urea group(s), or by reaction of an amino group with phosgene and then a primary amine to form a compound having secondary urea groups. Another approach is to react an isocyanate with a hydroxy urea compound to form a urea-capped isocyanate derivative. For example, one isocyanate group on toluene diisocyanate can be reacted with hydroxyethyl ethylene urea, followed by reaction of the other isocyanate group with an excess of polyol to form a hydroxy carbamate. One preferred class of compounds having an active hydrogen group and a group that can be converted to primary carbamate is the hydroxyalkyl cyclic carbonates. Hydroxyalkyl cyclic carbonates can be prepared by a number of approaches. Certain hydroxyalkyl cyclic carbonates like 3-hydroxypropyl carbonate (i.e., glycerine carbonate) are commercially available. Cyclic carbonate compounds can be synthesized by any of several different approaches. One approach involves reacting an epoxy group-containing compound with CO 2 , under conditions and with catalysts as described hereinabove. Epoxides can also be reacted with β-butyrolactone in the presence of such catalysts. In another approach, a glycol like glycerine is reacted at temperatures of at least 80°C with diethyl carbonate in the presence of a catalyst (e.g., potassium carbonate) to form a hydroxyalkyl carbonate. Alternatively, a functional compound containing a ketal of a 1,2-diol having the structure: can be ring-opened with water, preferably with a trace amount of acid, to form a 1,2-glycol, which is then further reacted with diethyl carbonate to form the cyclic carbonate. Cyclic carbonates typically have 5-6-membered rings, as is known in the art. Five-membered rings are preferred, due to their ease of synthesis and greater degree of commercial availability. Six-membered rings can be synthesized by reacting phosgene with 1,3-propane diol under conditions known in the art for the formation of cyclic carbonates. Preferred hydroxyalkyl cyclic carbonates used in the practice can be represented by the formula: where R (or each instance of R if n is more than 1) is a hydroxyalkyl group of 1-18 carbon atoms, preferably 1-6 carbon atoms, and more preferably 1-3 carbon atoms, which may be linear or branched and may have subsituents in addition to the hydroxyl (which itself may be primary, secondary, or tertiary), and n is 1 or 2, which may be substituted by one or more other substituents such as blocked amines or unsaturated groups. More preferably, R is -C m H 2m OH where the hydroxyl may be primary or secondary and m is 1 to 8, and even more preferably, R is -(CH 2 ) p -OH where the hydroxyl is primary and p is 1 to 2. Lactones that can be ring opened by an active hydrogen are well-known in the art. They include, for example, ε-caprolactone, γ-caprolactone, β-butyrolactone, β-propriolactone, γ-butyrolactone, α-methyl-γ-butyrolactone, β-methyl-γ-butyrolactone, γ-valerolactone, δ-valerolactone, γ-nonanoic lactone, γ-octanoic lactone, and pentolactone. In one preferred embodiment, the lactone is ε-caprolactone. Lactones useful in the practice of the invention can also be characterized by the formula: wherein n is a positive integer of 1 to 7 and R is one or more H atoms, or substituted or unsubstituted alkyl groups of 1-7 carbon atoms. The lactone ring-opening reaction is typically conducted under elevated temperature (e.g., 80-150°C). The reactants are usually liquids so a solvent is not necessary. However, a solvent may be useful in promoting good conditions for the reaction even if the reactants are liquid. Any non-reactive solvent may be used, including both polar and nonpolar organic solvents. Examples of useful solvents include toluene, xylene, methyl ethyl ketone, methyl isobutyl ketone, and the like. A catalyst is preferably present. Useful catalysts include proton acids (e.g., octanoic acid, Amberlyst® 15 (Rohm & Haas)), and tin catalysts (e.g., stannous octoate). Alternatively, the reaction can be initiated by forming a sodium salt of the hydroxyl group on the molecules to react with the lactone ring. The lactone ring-opening reaction provides chain extension of the molecule if sufficient amounts of the lactone are present. The relative amounts of the primary carbamate or primary urea compound (A) (1) and the lactone (A) (2) can be varied to control the degree of chain extension. The opening of the lactone ring with a hydroxyl or amine group results in the formation of an ester or amide and an OH group. The OH group can then react with another available lactone ring, thus resulting in chain extension. The reaction is thus controlled by the proportion of lactone in the relative to the amount of initiator compound (A) (1). In the practice of the present invention, the ratio of equivalents of lactone from (A) (2) to equivalents of active hydrogen groups on (A) (1) is preferably from 0.1:1 to 10:1, and more preferably from 1:1 to 5:1. When the lactone is opened with with an acid, the resulting compound has an acid group, which can then be converted to a hydroxyl group by well-known techniques such as reaction with ethylene oxide. A compound (A)(1) having a hydroxyl active hydrogen group can also be reacted with a hydroxy carboxylic acid to form the carbamate- or urea-functional compound (A). Useful hydroxy carboxylic acids include dimethylhydroxypropionic acid, hydroxy stearic acid, tartaric acid, lactic acid, 2-hydroxyethyl benzoic acid, and N-(2-hydroxyethyl)ethylene diamine triacetic acid. The reaction can be conducted under typical transesterification conditions, e.g., temperatures from room temperature to 150°C with transesterification catalysts such as such as calcium octoate, metal hydroxides (e.g., KOH), Group I or II metals (e.g., Na, Li), metal carbonates (e.g., K 2 CO 3 ) which may be enhanced by use in combination with crown ethers, metal oxides (e.g., dibutyltin oxide), metal alkoxides (e.g., NaOCH 3 , Al(OC 3 H 7 ) 3 ), metal esters (e.g., stannous octoate, calcium octoate, or protic acids (e.g., H 2 SO 4 ), MgCO 3 , or Ph 4 SbI. The reaction may also be conducted at room temperature with a polymer-supported catalyst such as Amberlyst-15® (Rohm & Haas) as described by R. Anand, Synthetic Communications, 24(19), 2743-47 (1994), the disclosure of which is incorporated herein by reference. The reaction is preferably performed with an excess of compound (A) (1) to minimize self-condensation of the hydroxy carboxylic acid. The composition of the invention is cured by a reaction of the primary carbamate- or primary urea-functional compound (A) with a component (B) that is a compound having a plurality of functional groups that are reactive with the primary carbamate or primary urea groups on component (A). Such reactive groups include active methylol or methylalkoxy groups on aminoplast crosslinking agents or on other compounds such as phenol/formaldehyde adducts, siloxane or silane groups, and anhydride groups. Examples of (B) compounds include melamine formaldehyde resin (including monomeric or polymeric melamine resin and partially or fully alkylated melamine resin), urea resins (e.g., methylol ureas such as urea formaldehyde resin, alkoxy ureas such as butylated urea formaldehyde resin), N-methylol acrylamide emulsions, isobutoxy methyl acrylamide emulsions, polyanhydrides (e.g., polysuccinic anhydride), and siloxanes or silanes (e.g., dimethyldimethoxy silane). Aminoplast resin such as melamine formaldehyde resin or urea formaldehyde resin are especially preferred. Also preferred are aminoplast resins where one or more of the amino nitrogens is substituted with a carbamate group for use in a process with a curing temperature below 150°C, as described in U.S. patent 5,300,328. A solvent may optionally be utilized in the coating composition used in the practice of the present invention. The coating composition according to the present invention can be applied without solvent, especially if the degree of chain extension for component (A) is limited. However, in many cases, it is desirable to use a solvent in the coating composition as well. This solvent should act as a solvent with respect to both the carbamate- or urea-functional compound (A) as well as the component (B). In general, depending on the solubility characteristics of components (A) and (B), the solvent can be any organic solvent and/or water. In one preferred embodiment, the solvent is a polar organic solvent. More preferably, the solvent is a polar aliphatic solvent or polar aromatic solvent. Still more preferably, the solvent is a ketone, ester, acetate, aprotic amide, aprotic sulfoxide, or aprotic amine. Examples of useful solvents include methyl ethyl ketone, methyl isobutyl ketone, amyl acetate, ethylene glycol butyl ether-acetate, propylene glycol monomethyl ether acetate, xylene, N-methylpyrrolidone, or blends of aromatic hydrocarbons. In another embodiment, the solvent can be water or a mixture of water with co-solvents. The coating composition used in the practice of the invention may include a catalyst to enhance the cure reaction. For example, when aminoplast compounds, especially monomeric melamines, are used as component (B), a strong acid catalyst may be utilized to enhance the cure reaction. Such catalysts are well-known in the art and include, for example, p-toluenesulfonic acid, dinonylnaphthalene disulfonic acid, dodecylbenzenesulfonic acid, phenyl acid phosphate, monobutyl maleate, butyl phosphate, and hydroxy phosphate ester. Other catalysts that may be useful in the composition of the invention include Lewis acids, zinc salts, and tin salts. Although a solvent may be present in the coating composition in an amount of from about 0.01 weight percent to about 99 weight percent, it is preferably present in an amount of less than 30%, more preferably less than 20% and most preferably less than 10%. The coating composition preferably has a VOC (VOC is defined herein as VOC according to ASTM D3960) of less than 3.0 lbs/gal, more preferably less than 2.0 lbs/gal, and most preferably less than 1.0 lbs/gal. Coating compositions can be coated on the article by any of a number of techniques well-known in the art. These include, for example, spray coating, dip coating, roll coating, curtain coating, and the like. For automotive body panels, spray coating is preferred. One advantage that can be achieved with coating compositions according to the invention is that coatings with a high degree of flexibility can be prepared. Accordingly, in a preferred embodiment, the substrate onto which the coating is applied is flexible, such as plastic, leather, or textile substrates. Any additional agent used, for example, surfactants, fillers, stabilizers, wetting agents, dispersing agents, adhesion promoters, UV absorbers, HALS, etc. may be incorporated into the coating composition. While the agents are well-known in the prior art, the amount used must be controlled to avoid adversely affecting the coating characteristics. In one preferred embodiment, the coating composition according to the invention is preferably utilized in a high-gloss coating and/or as the clearcoat of a composite color-plus-clear coating. High-gloss coatings as used herein are coatings having a 20° gloss (ASTM D523-89) or a DOI (ASTM E430-91) of at least 80. In other preferred embodiments, the coating composition may be utilized to prepare high-gloss or low-gloss primer or enamel coatings. When the coating composition of the invention is used as a high-gloss pigmented paint coating, the pigment may be any organic or inorganic compounds or colored materials, fillers, metallic or other inorganic flake materials such as mica or aluminum flake, and other materials of the kind that the art normally names as pigments. Pigments are usually used in the composition in an amount of 2% to 350%, based on the total weight (not including solvent) of components A and B (i.e., a P:B ratio of 0.02 to 3.5). When the coating composition according to the invention is used as the clearcoat of a composite color-plus-clear coating, the pigmented basecoat composition may any of a number of types well-known in the art, and does not require explanation in detail herein. Polymers known in the art to be useful in basecoat compositions include acrylics, vinyls, polyurethanes, polycarbonates, polyesters, alkyds, and siloxanes. Preferred polymers include acrylics and polyurethanes. In one preferred embodiment of the invention, the basecoat composition also utilizes a carbamate-functional acrylic polymer. Basecoat polymers are preferably crosslinkable, and thus comprise one or more type of cross-linkable functional groups. Such groups include, for example, hydroxy, isocyanate, amine, epoxy, acrylate, vinyl, silane, and acetoacetate groups. These groups may be masked or blocked in such a way so that they are unblocked and available for the cross-linking reaction under the desired curing conditions, generally elevated temperatures. Useful cross-linkable functional groups include hydroxy, epoxy, acid, anhydride, silane, and acetoacetate groups. Preferred cross-linkable functional groups include hydroxy functional groups and amino functional groups. Basecoat polymers may be self-cross-linkable, or may require a separate cross-linking agent that is reactive with the functional groups of the polymer. When the polymer comprises hydroxy functional groups, for example, the cross-linking agent may be an aminoplast resin, isocyanate and blocked isocyanates (including isocyanurates), and acid or anhydride functional cross-linking agents. The coating compositions described herein are preferably subjected to conditions so as to cure the coating layers. Although various methods of curing may be used, heat-curing is preferred. Generally, heat curing is effected by exposing the coated article to elevated temperatures provided primarily by radiative heat sources. Curing temperatures will vary depending on the particular blocking groups used in the cross-linking agents, however they generally range between 93°C and 177°C. The coating composition according to the present invention is curable even at relatively low cure temperatures. Thus, in a preferred embodiment, the cure temperature is preferably between 115°C and 150°C, and more preferably at temperatures between 115°C and 138°C for a blocked acid catalyzed system. For an unblocked acid catalyzed system, the cure temperature is preferably between 82°C and 99°C The curing time will vary depending on the particular components used, and physical parameters such as the thickness of the layers, however, typical curing times range from 15 to 60 minutes, and preferably 15-25 minutes for blocked acid catalyzed systems and 10-20 minutes for unblocked acid catalyzed systems. The invention is further described in the following examples. Preparation 1 - Compound (A) A clean 5-liter three-necked round bottomed flask was equipped with an agitator, condenser, thermocouple, and nitrogen line. To this apparatus was added 1735.0 g ε-caprolactone, 761.9 g hydroxypropyl carbamate, 234 g xylene, and 4.4 g stannous octoate. The mixtured was stirred under nitrogen atmosphere and heated to a temperature of 130°C. Temperature was maintained for a period of 6 hours to complete the synthesis, and then cooled. Example 1 - Coating Composition A clearcoat composition was prepared by mixing 1000 g of Preparation 1, 337.4 g monomeric fully metholated melamine, and 6.1 g dodecylbenzyl sulfonic acid. This composition was spray-applied to a variety of substrates using a conventional air atomization siphon gun. Both rigid and flexible substrates were coated. A portion of the panels were applied wet on wet over conventional high solids basecoat. For these systems, the basecoat (an industry standard high-solids OH acrylic/melamine system) was applied, followed by a 10-minute ambient flash, at which point the above-described coating composition was applied. After an additional 5 minutes ambient flash, the panels were baked at 121.1°C (250°F) for 30 minutes. The coating composition of the Example resulted in a contiguous cured hard clear film. The measured VOC of the clearcoat mixture was found to be 143.8 g/l (1.2 lbs/gal).

Claims: A curable coating composition comprising (A) a compound comprising primary carbamate or primary urea and hydroxyl functional groups that is the reaction product of (1) a compound comprising a primary carbamate or primary urea group or a group that can be converted to a primary carbamate or primary urea group, and an active hydrogen group that is reactive with (A)(2), and (2) a lactone or a hydroxy carboxylic acid, (B) a compound comprising at least one group that is reactive with carbamate and at least one group that is reactive with hydroxyl, or a plurality of groups that are reactive with both carbamate and hydroxyl. A coating composition according to claim 1 wherein the active hydrogen group on compound (A)(1) is a hydroxyl group. A coating composition according to claim 1 wherein the active hydrogen group on compound (A)(1) is an amino group. A coating composition according to claim 1 wherein said compound (A) comprises primary carbamate and hydroxyl functional groups. A coating composition according to claim 1 wherein said compound (A) comprises primary urea and hydroxyl functional groups. A coating composition according to claim 1 wherein compound (A) (1) is a hydroxyalkyl carbamate or a hydroxyalkyl cyclic carbonate. A coating composition according to claim 1 wherein compound (A)(1) is a β-hydroxy carbamate that is a product of a ring-opened cyclic carbonate. A coating composition according to claim 1 wherein the compound (A) (2) is a lactone. A coating composition according to any of claims 1 to 8 wherein the ratio of equivalents of lactone from (A)(2) to equivalents of active hydrogen groups on (A)(1) is from 0.1:1 to 10:1. A coating composition according to any of claims 1 to 9 wherein compound (B) is an aminoplast. A coating composition according to claim 10 wherein said aminoplast is a melamine resin. A coating composition according to any of claims 1 to 11 that is a clear coating composition. A coating composition according to any of claims 1 to 11, further comprising a pigment. An article comprising a substrate having thereon a cured coating derived from a coating composition according to any of claims 1-13.

Inventors: BAMMEL BRAIN D, MCGEE JOHN D, MENOVCIK GREGORY C, OHRBOM WALTER H, BAMMEL, BRAIN D., MCGEE, JOHN D., MENOVCIK, GREGORY C., OHRBOM, WALTER H.
Applicants: BASF CORP, BASF CORPORATION
Application year: 1996
Main classification: C09D201
IPC codes: C09D201, C09D167, C09D161, C08G71