Magnetic refrigerant compositions and processes for making and using

Abstract: There is provided a magnetic refrigerant composition comprising magnetic nonocrystalline metal oxide particles in an ion exchange matrix. The use of such composition in magnetic refrigerant processes is also provided. A process for making the composition is further provided. The composition can be used in xerographic copier or printing systems.

Description: The present invention relates to magnetic refrigeration compositins and processes for making magnetic refrigeration compositions and uses thereof. Magnetic refrigeration is a type of refrigeration which is accomplished generally by the cyclic operations of heat dissipation and heat absorption in the course of magnetization or demagnetization by adding or eliminating external magnetic fields applied to a magnetic substance. Magnetic refrigeration systems have been principally developed and used for achieving very low temperatures, for example in the milliKelvin range, for the purpose of investigating the physics of materials at low temperatures. These very low temperatures were achieved using, for example, an adiabatic magnetization and demagnetization process sequence with, for example, a paramagnetic salt, wherein the salt is magnetized during a first stage of cooling to low temperatures, by external means, followed by an adiabatic demagnetization of the salt to achieve a second stage of cooling and very low temperatures. In low temperature regions, such as below about 15 K, the lattice specific heat of magnetic materials for magnetic refrigeration becomes small compared to the magnetic specific heat, and a large magnetic entropy change may occur. The lattice specific heat values are negligible so that magnetic refrigeration can be accomplished in low temperature regions by using a magnetic refrigeration cycle of the reverse Carnot type. Paramagnetic substances are suitable materials for use in magnetic refrigeration in this low temperature region, especially in the region below about 20 K, for example gadolinium gallium garnet. In higher temperature regions, for example at or above 77 K the aforementioned lattice specific heat of the magnetic substance generally becomes larger than the magnetic specific heat so that a reverse Carnot type cycle is not usable and an Ericsson cycle and ferromagnetic and ferrimagnetic materials must be used. Furthermore, the heat disturbance energy of the magnetic moment also becomes greater for paramagnetic materials at these temperature and thus paramagnetic materials become unsuitable refrigerants at these temperatures. The use of magnetic fluids or ferrofluids as coolants is described in Magnetic Fluids Guidebook: Properties and Applications , V.E. Fertman, Hemisphere Publishing Corp., New York, 1990. Nanocomposite magnetic materials and their use in magnetic refrigeration are described in Nanostructured Materials. Vol. 1, 83-88, 1992, and Vol. 2, 205-211, 1993. However, these materials and systems are apparently limited in their application to refrigeration and are restricted to applications at or below about 25°K. US-A-5,362,417 discloses a method of forming a colloidal dispersion of submicron particles comprising: providing an ion exchange resin matrix; loading said resin matrix with an ion; and treating the resin to cause in-situ formation of submicron particles; and fluidizing said ion exchange resin and particles in an aqueous medium to form a stable colloid of said particles. EP-A-06 99 964 which is a document according to Article 54(3) and (4) EPC for all contracting states designated in the present application discloses a magnetic nanocomposite composition comprising from 0.001 to 60 weight percent of nanocrystalline particles of Fe 3 O 4 , and from 40 to 99.999 weight percent of a resin which is usually an ion exchange resin. Preferably, said resin is a sulfonated polystyrene resin. A long standing problem precluding the use of magnetic refrigeration systems at elevated temperatures has been the absence of suitable magnetic refrigerant materials and formulations which have a sufficiently large magnetocaloric effect at the elevated temperatures. There hence remains a need for magnetic materials which can be used in magnetic refrigeration processes at or above about 273 K and preferably above about 300 K. There also remains a need for magnetic materials which can increase the operating temperature range of magnetic refrigeration processes and also decrease the magnetic field requirements for magnetic refrigeration processes. Still further, there is a need for nanocomposite nanocrystalline particles that permit low cost, clean, and optionally dry micron and submicron polymeric composite particles that can be selected for use in a magnetic liquid formulation, and utilized as an active component in magnetic refrigeration heat transfer fluids. It is the object of the present invention to overcome the aforementioned problems. This object has been achieved by a magnetic refrigerant composition comprising a nanocomposite comprising from 0.001 to 60 weight percent of magnetic nanocrystalline metal oxide particles and from 40 to 99.999 weight percent of an ion exchange matrix, wherein the ion exchange matrix is selected from the group consisting of inorganic ion exchangeable metal oxide and mixed metal oxide compounds. Preferably, said composition comprises further a liquid carrier or heat transfer fluid in an amount of from 1 to 99 weight percent based on the weight of the nanocomposite. The present invention provides also a magnetic refrigeration process comprising: subjecting the above magnetic refrigerant composition to a magnetic field wherein the fluid is magnetized and the magnetized media absorbs the heat of magnetization; transferring the absorbed heat from the magnetized media to a heat sink; removing the magnetized media from the magnetic field, wherein the magnetic media undergoes spontaneous cooling to produce a cooled magnetic media; and providing heat to the cooled magnetic media from a heat source, and wherein said process is accomplished at above 275 K. The present invention is also directed to a process for making the above magnetic refrigerant composition comprising: providing the ion exchange matrix; loading said matrix with nanocrystalline metal oxide particles; treating the loaded matrix to cause in situ formation of magnetic particles or magnetic nanoclusters to form the magnetic refrigerant composition. Preferably, said process comprises further grinding the resulting magnetic particle impregnated ion exchange matrix; and/or drying the impregnated ion exchange matrix; and/or dispersing the impregnated ion exchange matrix in a liquid or solid medium. The present invention is also directed to the use of the above magnetic refrigerant composition in xerographic copier or printing systems. A solution to the above mentioned and related problems has been unexpectedly found in the use of a magnetic refrigeration material comprising a dispersion of magnetic nonocrystalline metal oxide particles in an ion exchange matrix that enables magnetic refrigeration processes at substantially elevated temperatures compared to those known in the art, for example, at about 0°C and above. The material typically has a large magnetic moment, is easily oriented in low magnetic fields and has an ordering temperature of about 0°C or above. The present invention provides magnetic refrigeration compositions for use in magnetic refrigeration processes at about room temperature and above. Figure 1 is an illustration of the magnetocaloric effect exhibited by a magnetic refrigeration composition of the present invention. The present invention provides, in embodiments, magnetic compositions suitable for use in heating and refrigeration processes which exhibit unexpected and superior magnetic refrigeration properties compared to those known in the art. The properties of the compositions enable improved magnetic refrigeration processes, for example, at and above ambient or room temperature, and which improvements are greater than would have been predicted based solely upon considerations of the chemical composition and magnetically active material content. Although not desired to be limited by theory, it appears that the improved magnetic refrigeration compositions and processes of the present invention are attributable in large part to the nanoscopic size and uniform distribution and disposition of the magnetic species within the ionic exchange matrix, and that the nanocomposites have a Curie temperature on the order of about 300°K. The present invention provides, in embodiments, magnetic refrigeration compositions which exhibit large isothermal field induced entropy changes ( Δ S ) in a magnetic field change. The magnetic refrigerant compositions of the present invention comprise: the magnetic or magnetizable nanoscopic metal oxide particles dispersed and stabilized within the ionic exchange resin; an optional immiscible or non-dissolving, with respect to the nanocomposite particles, aqueous or non aqueous carrier liquid, such as water, glycols, alcohols, tetrahydrofuran, toluene, and mixtures thereof; and optional additives, such as additives to control or enhance the heat transfer properties of the magnetic refrigerant composition, colorants, security taggants, fragrance or odorants, corrosion inhibitors, humectants and viscosity improvers. The nanocomposites and the magnetic refrigeration formulation are suitable as a principle constituent in ambient or room temperature magnetic refrigerant compositions, reference Figure 1 wherein there is graphically illustrated the relationship of the isothermal entropy changes over the indicated temperature range and demonstrates the magnetocaloric effect exhibited by a magnetic refrigeration composition of the present invention. The magnetic nanocomposite components of the present invention, in embodiments, enable a variety of viable magnetic refrigerant compositions and processes, as illustrated hereinafter. In embodiments, the compositions of the present invention are also useful as magnetic refrigerant compositions when disposed, for example, as solid-powder, liquid, colloid, suspension, slurry, and film forms. The compositions and process of the present invention are particularly useful in refrigeration applications such as heat management in, for example, xerographic copier or printing systems, such as fusing subsystems. The magnetic refrigeration compositions of the present invention typically exhibit magnetocaloric effects which are operable in the temperature range of from 290 to 310°K. The magnetic refrigerant compositions of the present invention also typically possess a Curie temperature of the order of about 300°K. An example of a magnetic refrigeration fluid composition of the present invention comprises a nanocomposite comprising from 40 to 80 weight percent of magnetic nanocrystalline metal oxide particles, such as gamma-Fe 2 O 3 and from 40 to 99.999 weight percent of an ion exchangeable matrix being an ion exchangeable inorganic material, such as a zeolite or a molecular sieve, micas and hydrotalcites, and a liquid carrier or heat transfer fluid, such as methanol or ethylene glycol in admixture with for example, water, in an amount of from about 20 to about 60 weight percent based on the weight of the nanocomposite. The magnetic refrigeration media of the present invention are useful in magnetic heating or refrigeration processes comprising, for example, subjecting a magnetically susceptible media to a magnetic field wherein the media is magnetized and the magnetized media absorbs the heat of magnetization; transferring the absorbed heat from the magnetized media to a heat sink; removing the magnetized magnetic media from the magnetic field; wherein the magnetic media undergoes spontaneous cooling to produce a cooled magnetic media; and providing heat to the cooled magnetic media from a heat source. The process steps can be sequentially repeated indefinitely, for example, in excess of several million thermal cycles, with substantially no deterioration of: the compositional integrity of the magnetically susceptible media; the thermodynamic efficiency of the processes; or the magnetocaloric properties of the composition and process. The magnetic refrigeration process is carried out at temperatures above 275 K, for example from 275 K to 320 K, and preferably in the range of from 290 K to 310 K. The process can be conducted at an ambient or external temperature of above about 0°C, for example, from 0 to 50°C, and preferably from 10 to 40°C. The processes of the present invention, in embodiments, utilize a magnetic field for magnetizing the magnetic media. Suitable magnetic field strengths for magnetizing the magnetic media are from 5,000 to 35,000 Oersteds (Oe). In other embodiments there are provided magnetic refrigeration processes which utilize reduced magnetic field strengths of 10,000 Oersteds (1 Tesla) or less, and preferably less than 4,000 Oe. The magnetic field used to magnetize the nanocomposite particles can be provided by known magnetic devices, for example, a refrigerated electromagnet, a superconducting magnet, a switchable on/off electromagnet, a non-refrigerated electromagnet, and a permanent magnet or magnets, or combinations thereof. In embodiments of the present invention, the magnetically susceptible media has a magnetocaloric effect of 0.05 to 0.5 J/K-kg over a magnetic field change of about 30,000 Oe. In another embodiment of the present invention, when the preparative process is modified to minimize or eliminate separation steps, that is, for example, separating non-magnetic material for magnetic material, there results a magnetic product with an enhanced magnetocaloric effect or property of 0.5 to 50 J/K-kg over a magnetic field change of about 30,000 Oe. The improved magnetic refrigeration compositions of the present invention can in one aspect of the present invention be prepared by the processes including providing an ion exchange matrix; loading the matrix with an ion capable of forming a magnetic phase; treating the loaded matrix to cause in situ formation of magnetic particles or magnetic nanoclusters; optionally grinding the resulting magnetic particle impregnated ion exchange matrix; optionally drying the impregnated ion exchange matrix; and optionally dispersing the impregnated ion exchange matrix in a liquid or solid medium, to form the liquid or solid refrigerant composition, wherein the composition has an enhanced magnetocaloric effect in the temperature range of from about 275 to about 340 K. The magnetic compositions obtained thereby can be used in magnetic refrigeration processes with magnetic field strengths of less than about 1 Tesla. It is also apparent from an extensive magnetic analysis of a large number of intermediate samples obtained from a wide variety of processing steps and variations thereon that compositions obtained with minimal separation or manipulation, or samples that are obtained free of separation steps, for example, centrifugation and washing of intermediate fractions, possess the largest magnetocaloric effect. In the other process embodiments of the present invention the pH, the reaction temperature, the concentration of reactants, and other process variables can be varied without significant deterioration of the magnetocaloric properties of the resulting magnetic media. The magnetic refrigeration or heating processes, in embodiments of the present invention, are preferably conducted free of, or substantially without, phase separation or deterioration of the components of the magnetically susceptible media. Thus, the magnetic refrigeration compositions and processes of the present invention are robust and quite stable to extensive thermal cycling, for example, in excess of several million cycles. The magnetically susceptible media, in embodiments of the present invention, can be moved or transported during the refrigeration and heating process steps by mechanical means, non mechanical means, magnetic means or non-magnetic means. Mechanical means include known solid and liquid pumping devices adapted to handle magnetic or magnetically susceptible media. Other suitable transport or transfer means include known magnetohydrodynamic or electrohydrodynamic means. Preferred transport means employ a minimal number of moving parts, and more preferably no moving parts. Minimizing or eliminating mechanical means or moving parts contributes to robustness and reliability of the process and reduces breakdown frequency and maintenance costs. The magnetic nanocrystalline metal oxide particles can be formed from magnetic metal ions selected, for example, from the group consisting of transition metal elements, such as iron, nickel, manganese, a lanthanide series element, and mixtures thereof. The aforementioned nanocomposite composition, in embodiments, can be optionally dispersed in a liquid carrier vehicle, for example, a water alcohol mixture, for facilitating material and thermal transport properties of the composition. The magnetic refrigerant compositions of the present invention preferably have a magnetic saturation moment of at least about 15 emu per gram. The magnetic refrigerant compositions of the present invention exhibit a pronounced magnetocaloric effect in the temperature range of from about 290 to about 310 K. The magnetic refrigerant composition can, in embodiments, be further comprised of at least one heat conducting additive selected from the group consisting of non-metallic particles, such as micron or preferably submicron polymeric particles or glass beads, and metallic filler particles, such as copper and silver. The magnetically susceptible media of the present invention includes magnetically susceptible solid nanocomposite particles dispersed in a compatible liquid or solid medium. The compatible solid can be selected from known materials such as binder resins other than the aforementioned ion exchange resins, rubbers, cellulosics, glasses, and the like solid vehicles. The solid vehicles are preferably friable under moderate to high or intense shear using mechanical means, such as roll and shot milling, while the solid vehicles are preferably resistant to degradation under the relatively low shear situation associated with the magnetic refrigeration transport and circulation conditions. Instead of conventionally known ion exchange polymer resins, such as those disclosed in EP-A-0 699 964, the ion exchange matrix is selected from inorganic ion exchangeable metal oxide and mixed metal oxide compound or compounds, for example, known natural and synthetic zeolites and molecular sieves, and inorganic layered compounds, such as hydrotalcites and mica. The resin matrix is preferably capable of withstanding, during nanocomposite preparation and in magnetic refrigeration process applications, repeated cycles of drying, swelling, and de-swelling and preferably will not decompose thermally below 120°C. The resin is preferably chemically unaffected by exposure to strong acids, bases or redox solutions with the exceptions of undergoing the desired ion exchange reactions. The resin may be of an analytical or an industrial grade. Aside from differences in cost and size, the industrial grade resins typically have more color than the analytical grades. Most of the color associated with industrial grade resins is temporary and is easily removed if desired by solvent washing, usually with water or alcohol or mixtures thereof. After washing, the industrial grade resin may retain a weak amber color similar to the analytical grade. Resin beads may be in embodiments, from 20 to 500 mesh and are preferably from 20 to 400 mesh size or between 850 and 38 µm (microns). More preferably, the resin beads are from 200 to 400 mesh or between 75 and 38 µm (microns). The larger size beads have two advantages over the smaller beads. First, the processing time is shorter when using the larger beads due to faster settling rates and ease of decanting. Second, the larger beads are mechanically weaker than the smaller bead due to greater osmotic shock effects during their manufacture. Thus, magnetic refrigerant material prepared from the larger beads crushes and presumably micronizes more easily than those made from the smaller beads. Despite its weaker mechanical strength, the lower cost larger resin retains its ion-exchange capability through and even beyond ten-cycles of loading. The resin selected may be submicron in size, for example, less than about 1 micron, from 0.01 to 1.0 µm (micron), and preferably from 0.05 to 0.5 µm (microns), so that no additional micronization step is necessary. Additional submicron resins appropriate for use in the present invention include any submicron resins which do not interfere with the characteristics of the desired material properties disclosed herein. Once a resin is selected, the resin matrix is next loaded with the precipitate precursor ion. In the case of the magnetic colloid this may be several different ions including, for example, ferrous or ferric ions in a manner described in US-A-4,474,866. The magnetic ion loaded resin is treated so as to cause an in-situ precipitation of the material desired for dispersion. Gamma-Fe 2 O 3 and Fe 3 O 4 , for example, may be precipitated in this manner. The nanometer size metal containing particles may be precipitated as compounds, for example as iron sulfide clusters, in their elemental forms, or preferably as the metal oxides, and which particles are preferably selected based on an empirical determination of their respective magnetocaloric effect. The nanocrystalline metal containing particles are, in embodiments, from 1.0 to 100 nanometers in mean particle diameter, preferably from 1.0 to 50 nanometers, and more preferably from 1.0 to 10 nanometers. Once the composite material has been formed, the ion exchange process and subsequent formation of particles may then be repeated several times to achieve higher loading of magnetic species in the composite particles. As the number of particles increases or their size increases the crosslinked ion-exchange polymer matrix becomes stressed and eventually ruptures. In a typical ion exchange resin, sufficient stress may occur after the first loading. Rupture of the composite particles may be easily detected for example, texturally, visually or microscopically. Micronization, by for example, ball-milling of the composite product in a stable liquid or solid medium or vehicle will lead to the formation of the stable dispersion of the composite material in 30 to 180 minutes. A suitable vehicle is any vehicle which allows dispersion including, for example, water and water miscible materials and the like solvents, such as methanol and ethylene glycol. Examples of suitable liquid vehicles include known heat transfer fluids including water, alcohols, polyols, glycols, glycol ethers, ethers, and liquid metals, such as mercury, gallium, and mixtures thereof. Thus, in embodiments, the magnetic refrigerant composition may be formulated in water or methanol, or alternatively, a mixture of water and methanol. The vehicle may further include any material which will not adversely effect the desired magnetic, mechanical, electrical or optical properties of the nanocomposition or the refrigerant compositions, for example, water soluble polymers or surfactants. Micronization as used herein is defined as the formation of a liquid or solid mixture through mechanical comminution of the polymeric matrix containing the magnetic nanocrystalline particles. Micronization may be accomplished by attrition, air attrition followed by dispersion in water, shaking, milling, ball milling, shaking or ball milling directly in water. Shaking or ball milling are preferred. Coarse particles may be removed by filtration or centrifugation. The average micronization time is from 30 to 180 minutes. When using submicron resin particles, no micronization step is required to form a stable colloid. A micronization step may however, be used with a submicron resin if smaller submicron particles are desired. When a micronization step is selected, grinding or milling time is greatly reduced due to the friable nature of the nanocomposite. Submicron particles may be produced by growing or building from the molecular level rather than grinding larger particles down to form smaller particles. Thus, in embodiments, the ionic polymeric matrix can be formed using known submicron particle size polymerization techniques followed by in situ impregnation or formation of the magnetic nanocrystalline particles with the resulting submicron sized polymer matrix. In exemplary examples of submicron resins, diafiltration techniques can be used in place of conventional ion exchange techniques to process the resin because of the very small size of the resin beads. The submicron resin beads may be suspended in an aqueous colloidal form prior to incorporation of the precursor metal ions, thus resulting in a stable colloidal dispersion of the resin and magnetic nanocrystalline particles subsequent to appropriate chemical treatment. Alternatively, the resin beads may be removed from the dispersed condition and dried to form a dry nanocomposite. Ultrafiltration is a known pressure-activated membrane filtration process capable of performing a variety of selective molecular separations. In ultrafiltration, the process fluid flows across a membrane with pore diameters in the range of 100 to 2000 nm (10 to 200 Angstroms). Solvents and species whose molecular size and weight are below the molecular weight cut-off will permeate through the membrane and emerge as an ultrafiltrate, while rejected species are progressively concentrated in the retentate process stream. Ultrafiltration differs from reverse osmosis in that it employs a more "porous" membrane which will not retain low molecular weight species such as solvent molecules, rather the membrane separation application is based on particle size. Ultrafiltration covers the particle diameter range range of 10 -3 to 10 2 µm (microns). The composite resin beads as described above may be dried prior to micronization and then subsequently micronized to produce a dry powder composite for dispersion in a fluid or solid, for example, a polymer. This dispersion of crushed composite and fluid or solid may subsequently be used in magnetic refrigerant fluid formation as illustrated herein. The various additive or supplemental materials as disclosed above, particularly those materials which are bound to the ion exchange matrix, are stable toward settling and do not separate from the vehicle over extended thermal cycling in, for example, magnetic heating and cooling processes. In the following examples all amounts are by weight percent unless specified otherwise. Reference EXAMPLE I Preparation of Magnetic Refrigerant Composition. 60 grams of Dowex 50X8-400 ion exchange resin, obtained from the Aldrich Chemical Co. (Milwaukee, WI), were washed clean batchwise with concentrated HCI, followed by successive washings with 0.1 N NaOH, deionized water, methanol and finally deionized water. The resin was then impregnated with iron ions in accordance with US-A-4,474,866 to afford magnetic impregnated resin nanocomposites comprising magnetic iron oxides or sulfides, such as Fe 2 O 3 , Fe 3 O 4 , Fe m S n , and the like species, and mixtures thereof. The resin loading procedure may be optionally repeated with additional batches of the same or different metal salt solutions, for example FeCl 2 solution, or alternatively a suitable equivalent metal salt, such as manganese salts, to produce mixed metal magnetic species, such as manganese ferrites. The mixture was then filtered and the impregnated resin washed with deionized water, first through a filter and then in batch until the filtrate tested negative for metal ions, as measured by, for example, electrochemical conductance methods. The mixture was filtered and washed clean with 2 liters, portionwise, of deionized water and then dried overnight at 110°C to afford the desired product of ultra-fine composite particles of nanocrystalline gamma-Fe 2 O 3 particles highly dispersed in the ion exchange resin. Transmission electron microscopy revealed that the magnetic iron oxide nanocrystals or particulate nanoclusters to be 5 to 15 nanometers (nm) in size and uniformly suspended or randomly dispersed in the resin. The product was then ground in water or suitable liquid vehicle to form a stable colloid. A dry powder sample was obtained by freeze drying the colloid. The aqueous colloid and the powder samples were evaluated as magnetic refrigerant materials as described below. Reference EXAMPLE II Magnetic Refrigerant Ferrofluid Preparation and Evaluation Twenty milliliters of a ferrofluid were prepared as described in Example I above and Example 3 of US-A-5,322,756. The ferrofluid was then concentrated using an Amicon® 8050 ultrafiltration cell under 207 kPa (30 psi) of dinitrogen using a cellulose membrane with an average pore size of 40 micrometers. The ferrofluid was concentrated to approximately 6 milliliters. Magnetization data as a function of temperature from 275 to 320°K were then obtained for the sample in applied magnetic fields of between 10,000 and 30,000 Gauss using a magnetic measuring device known as a SQUID magnetometer. The saturation magnetization of the sample, which was measured in electromagnetic units (emu), where one emu equals one erg per Gauss, showed a steady decline with temperature from 275 to 300 K characteristic of a ferromagnetic or ferrimagnetic material below its Curie temperature, that is, the temperature at which the saturation magnetization becomes zero and the material becomes paramagnetic. Over the temperature range of 275 to 300 K, the total magnetization of the sample as measured on the SQUID dropped by 0.04 emu in an applied field of 30,000 Gauss. Just before the Curie temperature was reached, however, the rate of change of the saturation magnetization with temperature became quite large and indicated that the Curie temperature of the material was being approached. In the present example, the saturation magnetization of the ferrofluid changed rapidly between 300 and 302 K. In this 2 K temperature range of 300 and 302 K, the saturation magnetization of the sample dropped 0.03 emu as compared to the drop of 0.04 emu over the 25 K in the temperature range of 275 to 300 K. At 302 K, the saturation magnetization of the sample immediately started to decrease at the previous slow rate to the limit of our measurement, 320 K. The precipitous drop in saturation magnetization at between 300 and 302 K was interpreted as an indication that a portion of the sample contained magnetic material with a Curie point at about room temperature. Next, the magnetization of the sample was measured as a function of magnetic field strength at constant temperature. This procedure was then repeated at several different temperatures between 275 and 300 K to generate a series of isothermal curves as described in Nanostructured Materials, Vol. 2, pp. 205-211, 1993. In this manner, the magnetocaloric effect was measured without calorimetry which would require measuring the change in temperature and heat capacity. The entropy variation of the sample, which is a quantitative measure of the magnetocaloric effect, was then obtained from the area enclosed by any two isotherms divided by the temperature difference between the isotherms. The entropy variation for the present sample as a function of temperature was highest in the range between approximately 295 and 300 K with a value of about 105 Joules per Kelvin degree-cubic meter (J/°K-m 3 ) at 295 K. The change in magnetic field strength (ΔH) was about 20,000 Gauss. Thus, the measured entropy variation, ΔS, for this stable magnetic colloid or ferrofluid, is large enough to indicate that this material may be used as a liquid magnetic refrigerant in the temperature range of approximately 290 to 300 K, and perhaps at temperatures just outside this range. Since the refrigerant in this situation is a liquid, it may be cycled rapidly through the refrigerator many times per minute thus making possible a magnetic refrigerator operating in the temperature range of approximately 290 to 300 K, and perhaps at temperatures outside this range, such as 305 to 345 K, or 250 to 280 K. Reference EXAMPLE III Magnetic Refrigerant Ferrofluid Preparation and Evaluation Thirty five milliliters of a ferrofluid were prepared as described in Example 2 of US-A-5,322,756 with the exceptions that cesium hydroxide was used in the preparation instead of sodium hydroxide and the ferrofluid vehicle, water, was not allowed to evaporate as described in the example. The ferrofluid instead, was concentrated using a Amicon® 8050 stirred ultrafiltration cell under 220 kPa (32.psi) of dinitrogen using a filter with a molecular weight cut-off of 20,000. The ferrofluid was concentrated to approximately 3 milliliters. Magnetization data as a function of temperature from 275 to 320 K were then obtained for the sample as described in Example II above. The stable water-based ferrofluid showed a practical magnetocaloric effect in the temperature range between approximately 290 and 300 K. At 295 K, the change in entropy and thus the value of the magnetocaloric effect was measured to be approximately 38 J/K-m 3 . The change in magnetic field strength (ΔH) was about 10,000 Gauss. Thus, the measured entropy variation, Δ S, for this stable magnetic colloid or ferrofluid, was sufficiently large to indicate that this material may be used as a liquid magnetic refrigerant in the temperature range of approximately 290 to 300 K. Since the refrigerant in this case is a liquid, it may be cycled rapidly through the refrigerator many times per minute thereby making possible a magnetic refrigerator operating in the temperature range of about 290 to about 300 K, and perhaps at temperatures outside this range. Reference EXAMPLE IV Magnetic Refrigerant Ferrofluid Preparation and Evaluation Sixty three milliliters of a stable, water-based ferrofluid were prepared as described in Example 3 of US-A-5,322,756 This ferrofluid was then concentrated to 8.5 milliliters using an Amicon® 8200 ultrafiltration cell in a manner described above. Magnetization data as a function of temperature from 275 to 320 K were then obtained for the liquid sample as described in Example II above. The stable water-based ferrofluid thus generated and measured, showed a practical magnetocaloric effect in the temperature range between approximately 290 and 300 K. At 295 K, the change in entropy and thus the value of the magnetocaloric effect was measured to be approximately 165 J/K-m 3 or approximately 4.3 times greater than that in Example III and about 1.6 times greater than the liquid sample in Example II. The change in magnetic field strength (ΔH) was about 10,000 Gauss. Thus, the measured entropy variation, Δ S, for this stable magnetic colloid or ferrofluid, is large enough to indicate that this material may be used as a liquid magnetic refrigerant in the temperature range of about 290 to 300 K, and perhaps at temperatures just below and just above this range as well. Since the refrigerant in this case is a liquid, it may be cycled rapidly through the refrigerator many times per minute thus making possible a magnetic refrigerator operating in the temperature range of approximately 290 to 300 K, and perhaps at temperatures below and above this range, such as 305 to 345°K, or 250 to 285 K. Reference EXAMPLE V Magnetic Refrigerant Ferrofluid Powder Preparation and Evaluation Ten milliliters of the stable, water-based ferrofluid prepared in Example IV above were freeze dried under vacuum using a standard Labconco® Freeze Dry / Shell Freeze System. The resulting dry, magnetic powder was then subjected to magnetization measurements as described in the previous examples over the temperature range from 275 to 320 K. The dried magnetic powder obtained showed a practical magnetocaloric effect in the temperature range between approximately 290 and 300°K. At 295 K, the change in entropy and thus the value of the magnetocaloric effect was measured to be approximately 320 J/K-m 3 or about 1.9 times greater than that in Example IV Thus, a solid magnetic powder consisting of nano-scale iron oxide particles dispersed in a sulfonated polystyrene polymer is obtained that shows a substantial and practical magnetocaloric effect at ambient room temperature. Thus, the measured entropy variation, Δ S, for this nanocomposite material, is large enough to indicate that this material may be used as a magnetic refrigerant in the temperature range of approximately 290 to 300 K, and perhaps at temperatures just outside this range. The magnetic refrigeration industry standard and commonly used solid paramagnetic refrigerant is gadolinium gallium garnet (GGG), Gd 3 Ga 5 O 12 , which is useful in the temperature range between approximately 7 to 15°K is limited to this temperature range and lacking the advantage of the present sample which is useful in the range of approximately 290 to 300 K, and perhaps at temperatures just below and above this range. A Δ S value, in units of J/K-kg, for the present sample measures the same order of magnitude as that for the aforementioned GGG sample, 0.21 at Δ H of 30,000 Gauss versus 0.70 at Δ H of 10,000 Gauss, respectively. In the present sample, only about 1% of the total magnetic material is the refrigerant. Thus, the present material, containing higher concentrations of magnetic refrigerant will equal or surpass the magnetocaloric effect of GGG when compared at the same Δ H. The present material does not possess a remanent magnetization and therefore no hysteretic losses during field cycling. These same properties of no remanent magnetization and no hysteretic losses are also possessed by the ferrofluids in Examples II, III and IV above.

Claims: A magnetic refrigerant composition comprising a nanocomposite comprising from 0.001 to 60 weight percent of magnetic nanocrystalline metal oxide particles and from 40 to 99.999 weight percent of an ion exchange matrix, wherein the ion exchange matrix is selected from the group consisting of inorganic ion exchangeable metal oxide and mixed metal oxide compounds. The composition according to claim 1, further comprising a liquid carrier or heat transfer fluid in an amount of from 1 to 99 weight percent based on the weight of the nanocomposite. The composition according to claim 1 or 2, wherein the magnetic nanocrystalline metal oxide particles are formed from magnetic metal ions selected from the group consisting of a transition metal element, a lanthanide series element, and mixtures thereof. The composition according to any of claims 1 to 3, wherein the refrigerant composition has a magnetic saturation moment of greater than about 15 emu per gram and a maximum magnetocaloric effect in the temperature range of from 290 to 310° K. The composition according to claim 4, further comprising at least one heat conducting additive selected from the group consisting of non-metallic and metallic filler particles. A magnetic refrigeration process comprising: subjecting a magnetic refrigerant composition according to any of claims 1 to 5 to a magnetic field wherein the fluid is magnetized and the magnetized media absorbs the heat of magnetization; transferring the absorbed heat from the magnetized media to a heat sink; removing the magnetized media from the magnetic field, wherein the magnetic media undergoes spontaneous cooling to produce a cooled magnetic media; and providing heat to the cooled magnetic media from a heat source, and wherein said process is accomplished at above 275 K. The magnetic refrigeration process according to claim 6, wherein the process is accomplished at from 275 K to 320 K and wherein the process is conducted at an ambient or external temperature of 0 to 50°C. The process in accordance with claim 6 or 7 wherein the magnetic field is of a strength of 5,000 to 35,000 Oersteds (Oe). The process in accordance with any of claims 6 to 8 wherein the magnetically susceptible media has a magnetocaloric effect of 0.05 to 0.5 J/K-kg over a magnetic field change of about 30,000 Oe. A process for making a magnetic refrigerant composition according to any of claims 1 to 5 comprising: providing the ion exchange matrix; loading said matrix with nanocrystalline metal oxide particles; treating the loaded matrix to cause in situ formation of magnetic particles or magnetic nanoclusters to form the magnetic refrigerant composition. The process according to claim 10, further comprising: grinding the resulting magnetic particle impregnated ion exchange matrix; and/or drying the impregnated ion exchange matrix; and/or dispersing the impregnated ion exchange matrix in a liquid or solid medium. Use of a magnetic refrigerant composition according to any of claims 1 to 5 in xerographic copier or printing systems.

Inventors: KROLL ELIZABETH C, PALACIOS JAVIER TEJADA, ZHANG XIXIANG, ZIOLO RONALD F, KROLL, ELIZABETH C., PALACIOS, JAVIER TEJADA, ZHANG, XIXIANG, ZIOLO, RONALD F.
Applicants: XEROX CORP, XEROX CORPORATION
Application year: 1996
Main classification: H01F1
IPC codes: H01F1, G03G21, F25B21