A packaging material having a food grade barrier coating

Abstract: The invention concerns a packaging material comprising a substrate and a food grade coating which is resistant to water, humidity or fat, the coating comprises about 60 to 70% by weight of egg white, about 25 to 30% of plasticizer, about 5 to 10% of emulsifier and about 3 to 8% of water.

Description: This invention relates to a packaging material comprising a substrate and a food grade barrier coating based on egg white protein. The packaging material is suitable for packaging food stuffs. The invention also relates to a process of producing the packaging material. The coating of substrates with food grade films is already known. Japanese patent J54095749 describes a packing coating based on soybean protein and other proteins. There are several problems with this type of coating. First, the need to use several types of protein makes it more difficult and more expensive to manufacture this kind of coating. Further, the use of soybean protein in particular has several drawbacks: first a coating solution based on soybean protein takes some time to dry to form a coating; secondly the mechanical and thermal properties of soy protein based coatings are rather poor and the coating is not transparent; and thirdly this type of coating must be bound to a specific type of substrate. In particular the substrate must be a synthetic resin substrate which is active to soybean protein to obtain proper adhesion. Japanese J03198754 describes a type of substrate coating for food and drug packing which is water-proof. However it is only water-proof at room temperature or slightly above. According to this patent the film is thermally soluble and dissolves in 3 to 5 min. at 60 to 70°C if it is in contact with water. Furthermore the film appears to have rather poor mechanical properties since a three-layer structure is required to ensure acceptable physical strength. Also the film contains, among other components, pullulan which is not approved for food use, neither in Europe nor in the United States of America. Therefore there is a need for a packaging material having a food grade coating which is water and fat resistant, having good mechanical properties and is relatively simple to produce. In accordance with the present invention, a packaging material is provided which comprises a substrate and a food grade coating which is resistant to water, humidity or fat, the coating comprises about 60 to 70% by weight of egg white, about 25 to 30% of plasticizer, about 5 to 10% of emulsifier and about 3 to 8% of water. The substrate may be made of any suitable material, for example paper, cardboard, paperboard, metal, synthetic foam, plastic, linen or a combination thereof. Therefore the substrate has great versatility. For instance the substrate may be used for plates, backing pans, packing systems for frozen food like fish, vegetables, fruit, ice-creams, meat or pizza or other similar applications. It also may be used to pack sausages, hamburgers, French fries and other fast food items or as wrapping to prevent meat, fruit or vegetables from drying and keep them fresh as an alternative to wax paper or other similar applications. There are many advantages of the barrier coating. Primarily the use of egg white as source of protein avoids the need of soy protein and all the disadvantages of soy protein. Since only egg white is used as protein source for the film it is easier to manufacture. Furthermore the egg white in the coating coagulates almost instantly during a thermal treatment and this saves time and money in fixing the coating on the substrate. Also the egg white protein does not need any particular type of substrate to permit its adhesion on it since there is no active reaction between the coating and the substrate as needed in the prior art. In the packaging material according to the invention, the plasticizer is selected from polyethylene glycol, polypropylene glycol and glycerol, and mixtures thereof. The emulsifier is an acetylated monoglyceride. The coating further comprises up to 3% in weight of lecithin. The invention concerns further a process of producing a packaging material, the process comprising applying a coating solution comprising about 25 to 30% by weight of egg white powder, about 10 to 15% of plasticizer, about 2 to 5% of emulsifier and about 50 to 63% of water on a substrate, coagulating and drying the coating. The egg white provides the insoluble structure for the coating. It is to be considered that increasing the amount of protein in the solution increases the viscosity of the coating solution and makes it more difficult to form a thin layer on a chosen substrate. It has been observed that using about 25 to 30% of egg white powder is best for the coating composition. If a thin coating is desired on the substrate it is either possible to decrease the amount of egg white powder in the solution or it is possible to use rollers to spread the coating on the substrate. Water is preferably used to dissolve the egg white powder in order to form the basic solution for the film. To obtain an optimal solution about 50 to 63% of water is needed to get the good spreadability and short drying duration desired for the coating. Increasing the amount of water extends the drying period. To improve the water, humidity and fat barrier properties an emulsifier, for instance acetylated monoglyceride, is added to the coating solution. The emulsifier shows also a direct effect on the viscosity of the solution and on the homogeneity of the coating structure. It has been observed that increasing the amount of the emulsifier also increases the tendency to irregular coating and cracking. For best results, about 2 to 5 % of emulsifier is used. To ensure good mechanical properties a plasticizer, for instance polyethylene glycol, polypropylene glycol or glycerol, is added to the emulsifier in order to increase the elasticity of the coated substrate. Since the plasticizer reduces the water, humidity and fat barrier property, about 12 to 15% of glycerol have been found to be best for this type of coating although this amount can be extended to about 10 to 15% with acceptable results. After the plasticizer and the emulsifier have been mixed together, this solution is added to the previous egg white solution to obtain a homogeneous final solution that can be applied on the surface of the substrate. The final solution is characterized by a low viscosity well suited to be applied on a desired substrate in a way to form a uniform thickness. To obtain better homogeneity of the coating lecithin may be added to the egg white and water solution before adding the plasticizer and the emulsifier solution. Adding lecithin in small amounts, up to about 1%, avoids the formation of foam generated by egg white within the solution. The final solution can be applied on the surface of the substrate with a brush, by roller, by spraying or any other equivalent system. The amount of applied solution is about 80 to 120 g/m 2 in order to get a final coating after heating and drying of the order of 0.05 to 0.15 mm which is needed for good humidity, water and grease barrier properties. After the substrate has been coated, the coating is fixed by a thermal treatment. The thermal treatment consists of about 1 to 10 min. at a temperature of about 60 to 100°C in order to ensure the coagulation of the egg white contained within the coating. This operation can be done either in a heating tunnel for a continuous production or in an oven for a batch production. The thermal energy can be generated for instance by an I.R. radiator, by hot air, by vapor or by any equivalent equipment. After the drying of the coating on the substrate, the proportions of the coating components change according to the amount of liquid which has been evaporated. The remaining moisture after heating should be of the order of 6% which is best to ensure elasticity of the barrier material. While the amount of water decreases all other component proportions increase: the egg white proportion increases to about 60 to 70% by weight, the plasticizer quantity is about 25 to 30%, the emulsifier amount is of the order of 5 to 10% and there should be less than about 3% of lecithin within the dried coating. The properties of a substrate coated with the food grade coating described earlier in this document generate interesting possibilities: As it would be the case for any other food grade water, humidity and fat proof packaging material there is no need to use additional plastic bags or aluminum trays to separate the food and the substrate since the food is not directly in contact with the substrate but with its food grade coating; consequently no water, humidity or fat is able to migrate through the coating to the substrate and so no non edible component from the substrate to the food. Nevertheless compared to the known food grade coatings, this one is far more stable when exposed to heat or coldness or mechanical stress and it is transparent as well. This packaging material is elastic at room temperature and does not crack upon freezing as deep as-50°C. It withstands a temperature of 100°C without visible alterations and since there is no aluminum tray to contain the food, the packing system allows heating in a microwave oven so that the food can stay in its package until the cooking is done. To illustrate the description of the invention made above a couple of concrete examples which have been carried out are given. Example 1: The proposed barrier is to coat and to protect a cardboard substrate used as a frozen food carton for frozen pizzas which are supposed to be cooked directly in their package. The protective coating of the substrate is made out of the following amounts of components: 27.5% of egg white powder, 15% of glycerol, 2% of acetylated monoglyceride, 55.5% of water. First of all the egg white powder is to be dissolved in the water. Then glycerol and acetylated monoglyceride which have been mixed together is added to the dissolved egg white powder to obtain a homogeneous solution. Then 100 g/m 2 of solution are applied on a carton with a brush to form a thin and regular thick film to obtain a final thickness after heating of 0.1 mm which is enough to guaranty the water, humidity and fat barrier properties. After the solution has been spread on the substrate it is fixed by a thermal treatment. The thermal treatment is carried out in an oven using an I.R radiator as thermal energy source. Example 2: This example illustrates a coating of a fast-food paperboard tray for hamburgers to be sold as take-away food. The coating is made from a liquid solution containing the following proportions of components: 27.5% of egg white powder, 12% of glycerol, 5% of acetylated monoglyceride, 55% of water 0.5% of lecithin. The mixing of the components is done as in the previous example except that the lecithin is added to the egg white and water solution before the glycerol and acetylated monoglyceride solution is added to the dissolved egg white powder. After the mixing of the solution, a film of 120 g/m 2 of solution is spread on the substrate with a brush in order to get a final thickness of 0.15 mm. After coating the substrate the heating and drying operation is done in a heating tunnel using vapor as thermal energy source. Example 3: The last example relates to a coating of paper for wrapping fresh food like vegetables, fruit, meat, fish, cheese, etc. This paper is an alternative to the traditional wax paper used for the same purpose. The composition of the solution which is to be spread and later dried on the paper is the following: 27.5% of egg white powder, 10% of glycerol, 2% of acetylated monoglyceride, 60% of water 0.5% of lecithin. The preparation of the solution, the coating of the substrate and the drying is done as described in the procedure of the 2nd example.

Claims: A packaging material comprising a substrate and a food grade coating which is resistant to water, humidity or fat, the coating comprises 60 to 70% by weight of egg white, 25 to 30% of plasticizer, 5 to 10% of emulsifier and 3 to 8% of water. A packaging material as in claim 1 wherein the substrate is selected from paper, paperboard, cardboard, plastic, synthetic foam, metal, linen or a combination thereof. A packaging material as in claim 1 or 2 wherein the coating further comprises up to 3% in weight of lecithin. A packaging material as in any of claims 1 to 3 in which the plasticizer is selected from polyethylene glycol, polypropylene glycol and glycerol, and mixtures thereof. A packaging material as in any of claim 1 to 4 in which the emulsifier is an acetylated monoglyceride. A process of producing a packaging material according to any of claims 1 to 5 comprising applying a coating solution comprising 25 to 30% by weight of egg white powder, 10 to 15% of plasticizer, 2 to 5% of emulsifier and 50 to 63% of water on a substrate, coagulating and drying the coating. A process as in claim 6 wherein the coating solution is prepared by dissolving the egg white powder in water prior to adding a plasticizer and emulsifier mix. A process as in claim 6 or 7 wherein the egg white and water solution is furthermore mixed with up to 1% of lecithin. A process as in any of claims 6 to 8 wherein the coating solution is applied on the substrate by means of a brush, a roller or by spraying. A process as in any of claims 6 to 9 wherein the coating is coagulated and dried in a heating tunnel or an oven. A process as in any of claims 6 to 10 wherein the heating conditions are of the order of 1 to 10 min. at a temperature of about 60 to 100°C.

Inventors: WISSGOTT ULRICH, WISSGOTT, ULRICH
Applicants: NESTLE SA, SOCIETE DES PRODUITS NESTLE S.A.
Application year: 1996
Main classification: D21H19
IPC codes: D21H19, D06M13, D06M15, B32B9, B65D65, D21H27, C09D189