Article comprising exchange-coupled magnetic materials

Abstract: Articles according to the invention exemplarily comprise a magnetically hard oxide layer (e.g., 81) in contact with a magnetically soft oxide layer (e.g., 82), with spins in the latter at room temperature exchange-coupled to the (oriented) spins in the former. Exemplarily both materials are ferrimagnetic spinel-type oxides, e.g., CoFe 2 O 4 /(Mn, Zn)Fe 2 O 4 . Material combinations according to the invention can be advantageously used in high frequency circuit components such as inductors (e.g., 70), since the magnetically soft layer can be in a substantially single domain state even after exposure to a magnetic field of considerable strength, e.g., up to about 500 Oe.

Description: Field of the Invention This invention pertains to articles that comprise exchange-coupled magnetic materials. Background of the Invention Ferromagnetic or ferrimagnetic (collectively "FM") oxide materials have found widespread use in passive circuit components, e.g., in resonators or inductors, because the low conductivity of these materials eliminates eddy current losses. Typically the materials are used in bulk or thick film form, although their use in thin film form is not precluded. In prior art devices it is typically not possible to ensure that the FM oxide material contains a single magnetic domain, since readily encountered stray fields of only a few oersted can destroy a pre-existing single-domain state, thereby introducing domain walls into the material. However, the presence of domain walls results in power dissipation in an applied time-varying field, limiting the usefulness of prior art FM oxide circuit elements typically to frequencies of about 10 MHz or less. In view of the current rapid growth of the utilization of the frequency region of about 100 MHz-2 GHz for communication purposes (e.g., for cellular telephony), it would be highly desirable to have available circuit elements that comprise FM oxide material that can be single domain in substantially any stray magnetic field such a circuit element is likely to encounter, and that thus is not limited by dissipation due to domain wall motion. More specifically, it would be highly desirable to have available FM oxide-containing circuit elements that can be used at higher frequencies than prior art FM oxide elements, exemplarily including the range 100 MHz-2 GHz. This application discloses a technique for obtaining such elements, and elements produced thereby. It is well known that the quantum mechanical exchange interaction can lead to spin coupling across the interface between two magnetically ordered materials. The resulting interface energy leads to exchange anisotropy. See, for instance, A. Yelon, "Physics of Thin Films", Academic Press, New York 1971, Vol. 6, pp. 205-300. Exchange anisotropy has been observed at room temperature only in a relatively small number of material combinations (typically thin films), which are, to the best of our knowledge, either metal/metal or metal/oxide combinations. A particular metal/metal exchange coupled combination (MnFe/NiFe) has attained technological significance as the basis for a biasing scheme for magnetoresistive (MR) heads used in magnetic data storage. See, for instance, C. Tsang, IEEE Trans. Mag., Vol. 25, 3692 (1989). Note that MnFe is an antiferromagnet (AFM), and Ni 1-x Fe x (PERMALLOY) is a soft FM material. M-H loop offsets in the range 800-8000 A/m (10-100 Oe) are obtained in this system, with blocking temperatures (above which the exchange anisotropy is negligible) of about 250°C. K.I. Arai et al., IEEE Trans. Mag., Vol. 27,5337 (1991) report the application of YIG (yttrium iron garnet) to thin film inductors, with an external field applied to suppress domain-wall motion and consequent dissipation. For a brief discussion of some aspects of exchange anisotropy, see B.D. Cullity, "Introduction to Magnetic Materials", Addison-Wesley 1972, pp. 422-425. J.A. Borchers et al., J. Applied Physics, Vol. 73(10), page 6898, May 15, 1993, disclose neutron diffraction measurements on NiO/CoO superlattices with magnetic domains. J.A. Borches et al., J. Applied Physics, Vol. 73(10), May 15, 1993, pages 6898-6900 disclose propagation of antiferomagnetic order across paramagnetic layers in CoO/NiO superlattices; and V.V. Ustinov et al. (J. of Magnetism and Magnetic Materials, Vol.113 (1992), pages 1-7) disclose ferromagnetic resonance in epitaxial iron-garnet magnetically coupled layers. Summary of the Invention The invention is defined by claim 1. Preferred embodiments are defined in dependent claims 2 to 9. In a broad aspect the invention is embodied in an article (e.g., communication equipment that comprises an inductor or resonator) that comprises a quantity of a first magnetic material and a quantity of a second magnetic material in contact with the first magnetic material and having an interface therewith. Associated with each of the first and second magnetic materials is a spin orientation that can be a function of position in the material. The first and second magnetic materials are selected such that, over a temperature range that includes room temperature (20°C), the spin orientation in the second magnetic material is, in at least a portion of the second magnetic material that is adjacent to the interface between the first and second magnetic materials, a function of the spin orientation of the first magnetic material. Significantly, each of the first and second magnetic materials is a metal oxide magnetic material. Equivalently, the first and second magnetic materials are selected such that there is associated with the combination an interface anisotropy that provides substantial pinning of the second magnetic material spins at the interface, with the orientation of the pinned spins being a function of the spin orientation in the first magnetic material. Associated with the interface is an interface anistropy energy K int (defined as the magnetization of the second material times the measured offset field H ex divided by the thickness of the second layer) that is a measure of the strength of spin pinning. According to the invention, this energy is typically greater than about 10 -5 J/m 2 (10 -2 erg/cm 2 ) at room temperature. Combinations with interface anisotropy energy substantially below that value at room temperature are typically not of technological interest since the pinning strength would be too low to ensure maintenance of a single domain state in typical stray fields. A spin in the second magnetic material herein is considered to be "adjacent" to the interface if the spin is within the characteristic domain wall thickness of the second material to the interface. Although combinations according to the invention are not necessarily combinations of layers of magnetic materials, the discussion below will generally be in terms of layer structures. This is done for ease of exposition and definiteness, and is not intended to limit the scope of the invention. Magnetic oxide materials according to the invention typically are selected from the spinel-type oxides, the garnet-type oxides, and the cobalt Y-type hexaferrites, with spinel/spinel combinations currently most preferred. A given magnetic oxide can be a ferromagnet, ferrimagnet, antiferromagnet or compensated ferrimagnet at room temperature, with ferrimagnetic/ferrimagnetic combinations that comprise magnetically hard first material and magnetically soft second material currently most preferred. An exemplary combination comprises CoFe 2 O 4 first material, with second material selected from (Mn, Zn)Fe 2 O 4 , (Li, Fe)Fe 2 O 4 or (Ni, Zn) Fe 2 O 4 . In further exemplary combinations the first material is a spinel-or garnet-type magnetic oxide near compensation (e.g., with a compensation temperature in the range 20°C±50°C, exemplarily NiFeCrO 4 ). In currently preferred embodiments both the first and the second magnetic oxide material are thin films, the second material thin film typically being at most 1µm thick. The thin films are substantially single crystal thin films. Exemplarily the single crystal thin film is a magnetically hard first material thin film oriented such that an easy axis of the magnetic material lies in the plane of the film. The substantially single crystal thin film typically is grown on a single crystal substrate of appropriate composition, lattice structure and lattice constant. Optionally a buffer layer is interposed between the single crystal substrate and the single crystal magnetic oxide thin film. In currently most preferred embodiments both the first and the second magnetic oxide thin films are substantially single crystal thin films. In preferred embodiments of the invention the interface (exchange) anisotropy is of sufficient strength to return the second magnetic oxide material to a domain wall-free state after exposure to typically encountered stray magnetic fields, exemplarily to fields up to about 40 kA/m (about 500 Oe). Brief Description of the Drawings FIG. 1 schematically shows a general M-H loop; FIGs. 2 and 3 show the M-H loops of, respectively, a magnetically hard and a magnetically soft metal oxide material; FIG. 4 shows the major M-H loop of a combination of the magnetically hard and soft oxides of FIGs. 2 and 3; FIG. 5 shows a portion of the M-H loop of FIG. 4 with expanded scale of the magnetic field; FIG. 6 schematically shows the M-H loop of a combination according to the invention that comprises an antiferromagnetic (or compensated ferrimagnetic) biasing layer; and FIGs. 7 and 8 schematically depict an exemplary article according to the invention, namely, an inductor. Detailed Description of Some Preferred Embodiments "Exchange anisotropy" refers to the unidirectional anisotropy observed in heterogeneous magnetic systems due to coupling between two (or more) magnetic materials in contact with each other. The coupling is due to the same exchange processes that lead to ordered magnetic behavior in homogeneous systems (e.g., ferromagnetism, ferrimagnetism or antiferromagnetism). Because the exchange interaction is short-range, exchange anisotropy operates generally over a short length scale, typically less than 1µm. We have observed the existence of exchange anisotropy in magnetic metal oxide/magnetic metal oxide combinations (typically layer structures), and have discovered that such combinations can have magnetic properties that make them suitable for, e.g., high frequency circuit components such as inductors and resonators. The magnetic metal oxides are spinel-type, garnet-type, and cobalt Y-type hexaferrite metal oxides, with same-type combinations (e.g., spinel type/spinel type) currently preferred. A combination according to the invention generally comprises a metal oxide biasing layer in combination with a layer of magnetically soft oxide material. Multilayer (i.e., more than two layers) combinations that comprise interleaved biasing layers and magnetically soft oxide layers are also contemplated, as are non-thin-film combinations, e.g., a body comprising a mixture of first and second magnetic oxide particles, optionally together with a binder (e.g., epoxy), or particles of one type coated with material of the other type. The biasing layer will frequently comprise magnetically hard ferromagnetic or ferrimagnetic material, but biasing layers that comprise antiferromagnetic material or compensated ferrimagnetic material are also contemplated. Those skilled in the art will know that the latter two types of magnetic materials can be poled such that the spins are ordered, without providing macroscopic magnetization to the material. The terms "magnetically hard" and "magnetically soft" are well understood by those skilled in the art. The terms relate to characteristics of the magnetization loop (also referred to as the M-H loop) of a magnetic material. FIG. 1 shows an exemplary M-H loop, and defines such parameters as the coercive field H c , saturation magnetization M s , and remanent magnetization M r . See also, for instance, B. D. Cullity, "Introduction to Magnetic Materials", Addison-Wesley 1972, pp. 18-21, which illustrates the meaning of "major loop" and "minor loop". FIG. 2 shows the room temperature magnetization loop of an exemplary magnetically hard metal oxide material, namely, a (011)-oriented CoFe 2 O 4 film, with H applied in the easy (100) direction in the plane of the film, and FIG. 3 shows the room temperature magnetization loop of an exemplary magnetically soft material, namely a (011)-oriented Mn 0.5 Zn 0.5 Fe 2 O 4 film, with H also applied along the in-plane (100) direction. Exemplarily, a magnetically hard material herein has H c ≳ 40 kA/m (500 Oe), and a magnetically soft material has H c ≲ 4 kA/m (50Oe). The magnetically hard material will advantageously have H c ≲ 1.2 Ma/m (15 kOe), to facilitate poling of the material by conventional magnet means. However, materials with H c > 1.2 MA/m (15 kOe) can be poled in a pulse magnetic field and are not precluded. FIG. 4 shows the loop of an exemplary combination according to the invention, namely, a CoFe 2 O 4 film/Mn 0.5 Zn 0.5 Fe 2 O 4 film combination, oriented as specified for FIGs. 2 and 3. The films were substantially single crystal and epitaxial with each other. The data were taken at room temperature. The data are interpreted as follows: For large positive H (at portion 41 of the loop) the magnetization of both films is saturated and oriented parallel to the applied field. As the field strength is reduced towards zero, the magnetization remains substantially unchanged. Significant change in the magnetization occurs when the applied field has gone through zero and is small and negative (portion 42 of the loop). Under these conditions the magnetization of a portion of the soft layer reverses in direction. At portion 43 of the loop the magnetization of the soft layer substantially is parallel to the applied field, whereas the magnetization of the hard layer substantially is antiparallel to the applied field. Further increase in negative H results in reversal of the magnetization of the hard layer (portion 44) and saturation of the magnetization of the combination (portion 45). Sweeping the applied field from large negative values through zero to large positive values traces the remaining portion of the M-H loop. An important aspect of the magnetic behavior of combinations according to the invention is the pinning of the spins of the magnetically soft material at the interface by the spins of the bias layer, resulting in magnetization asymmetry. This is more clearly shown in FIG. 5, which was obtained from the combination of FIG. 4. The M-H loop of FIG. 5 was obtained by first applying a field of + 800 kA/m (+10 kOe), and then tracing a (minor) loop over the range +40 to -80 kA/m (+500 to -1000 Oe). M s of the magnetically hard layer was subtracted from the data, with FIG. 5 showing the M-H loop of only the magnetically soft layer. The asymmetry in shape and the offset with regard to H=0 are due to exchange coupling between the magnetically hard and soft layers. The offset is approximately 8 kA/m (100 Oe), and is referred to as H ex . It is important to note that although the M-H loop is a minor loop for the overall layer combination, it is effectively a major loop for the magnetically soft layer, since this layer is driven from positive saturation to negative saturation and back. As those skilled in the art will recognize, in combinations according to the invention the biasing layer provides asymmetry, somewhat akin to the asymmetry provided by an applied static magnetic field. This asymmetry can insure that the magnetically soft layer returns to the single-domain state for a significant range of applied magnetic fields (including stray magnetic fields), and thus eliminates energy dissipation due to domain wall motion in the magnetically soft layer under typical operating conditions of circuit elements that comprise the combination. Such circuit elements thus are substantially not subject to a major shortcoming of corresponding prior art circuit elements (namely, dissipation due to domain wall motion), and can be used at higher frequencies than the prior art components. In currently preferred embodiments the biasing layer is a hard ferromagnetic or ferrimagnetic material. In this case the spins in the magnetically soft layer adjacent to the interface will typically be pinned in parallel orientation (although other orientations such as antiparallel are not excluded) to the spins in the biasing layer, assuming that the spins in the biasing layer are ordered. Such ordering of course is readily achieved by application of a field of strength sufficient to produce magnetization saturation in the biasing layer. The magnetically hard biasing layer is advantageously selected to have relatively high crystal anisotropy (e.g., greater than about 10 kJ/m 3 (10 5 ergs/cm 3 )) and coercive force (e.g., greater than about 40 kA/m (500 Oe)) in the plane of the layer, with the layer typically poled in an easy magnetization direction in the plane of the film. FIGs. 4 and 5 are exemplary of the M-H loops of combinations according to the invention that comprise a ferromagnetic or ferrimagnetic biasing layer. FIG. 6 shows a schematic M-H loop of a combination that comprises a ferro- or ferrimagnetic magnetically soft layer and a compensated ferrimagnetic or antiferromagnetic biasing layer. As those skilled in the art will appreciate, in the case exemplified by FIG. 6 the biasing layer does substantially not contribute to the magnetization of the combination, but does serve to pin the soft material spins adjacent to the interface, assuming the biasing layer is appropriately poled. Such poling can be achieved, for instance, by cooling of the combination through the Neel temperature in the presence of a magnetic poling field. Desirably, the easy axis of the biasing layer lies in the plane of the layer. The magnetically soft layer of combinations according to the invention typically is a ferromagnetic or ferrimagnetic material, desirably such a material having relatively low crystal anisotropy (e.g., less than 100/m 3 (10 3 ergs/cm 3 )), low coercive force (e.g., ≲ 4 kA/m (50Oe)), and high magnetization (M s ≳ 20 emu/cm 3 ). Preferred embodiments of the invention comprise a substantially single crystal biasing layer, oriented such that an easy axis lies in the plane of the layer. Currently most preferred are combinations that furthermore comprise a substantially single crystal magnetically soft layer that is epitaxial with the biasing layer. By "substantially single crystal" we mean herein material having χ min < 20%. The RBS ratio χ min is a conventional measure of crystalline perfection in thin films, using 4 He ions at 2 MeV. The layers can be deposited on a substrate in arbitrary order, with the order selected to meet given requirements. If it is desired that the first-deposited layer is a substantially single crystal layer, then the substrate has to be a single crystal substrate, of suitably chosen composition, lattice structure and lattice constant. Growth of a heteroepitaxial layer on a single crystal substrate is well known and does not require detailed discussion. In some cases it may be desirable to grow a buffer layer on the single crystal substrate, and to form the first layer of the combination according to the invention on the buffer layer. Use of a buffer layer in aid of epitaxial growth is also known to those skilled in the art. For technological applications it is clearly of considerable importance that combinations according to the invention exhibit exchange anisotropy over a temperature range that includes room temperature, thereby avoiding the expense and inconvenience of cooling devices according to the invention. Our discovery of suitable combinations of magnetic oxides thus is considered a significant aspect of the invention. FIGs. 7 and 8 schematically depict an exemplary device according to the invention, namely, an inductor that is suitable for high frequency use. Reference numeral 71 refers to a composite body that comprises single crystal substrate 80, biasing layer 81, and soft layer 82 and optionally comprises a buffer layer (not shown) between substrate and biasing layer. On the magnetically soft layer is disposed conductive material in form of a spiral. Pads 73 and 74 facilitate electrical contact with the inductor. Optional spacers to separate crossing conductive paths are conventional and are not shown. The arrow in FIG. 7 exemplarily indicates the biasing layer poling direction. Among currently preferred magnetic metal oxides for use in combinations according to the invention are spinel ferrites. These materials typically have moderately high resistivities (e.g., 10-10 6 Ω·cm), moderately high magnetizations (e.g., 300-400 emu/cm 3 ), and moderately low ferromagnetic resonance (FMR) linewidths (e.g., 0.16-16 kA/m (2-200 Oe) at ∼10 GHz). For further detail on spinel ferrites and garnet ferrites see, for instance, W. H. von Aulock, "Handbook of Microwave Ferrite Materials", Academic Press, New York, 1965. Exemplary spinel ferrites for use as the second (i.e., magnetically soft) material are (Mn,Zn)Fe 2 O 4 , Li 0.5 Fe 2.5 O 4 , and (Ni, Zn)Fe 2 O 4 . Exemplary magnetically hard spinel ferrites are CoFe 2 O 4 , and (Mn, Ti)Fe 2 O 4 , with the former having a high bulk crystal anisotropy constant of about 3 x 10 6 erg/cm 3 and being currently most preferred. The notation such as (Mn, Zn)Fe 2 O 4 is conventional, being short-hand for (Mn x Zn 1-x )Fe 2 O 4 . The value of x is selected to yield desired properties (e.g., coercivity) for a given application, and is generally between 0 and 1. Single crystal MgAl 2 O 4 has lattice constant of about 0.818 nm and can advantageously be used as substrate for spinel ferrites, which typically have lattice constants in the range 0.830-0.840 nm. The moderate mismatch can be alleviated by use of an appropriate lattice-matching buffer layer. Paramagnetic CoCr 2 O 4 and NiMnO 4 can advantageously serve as a buffer layer, and other buffer layer materials can be readily identified. We have used buffer layers that were about 50 nm thick. We annealed the buffer layers at 1000°C in air for 30 minutes to improve crystallinity. Spinel ferrites are not the only magnetic materials that are potentially useful in the practice of the invention. Among other potentially useful magnetic metal oxides are garnets (e.g., Y 3 Fe 5 O 12 ), and cobalt Y-type hexaferrites (e.g., Ba 2 Co 2 Fe 12 O 22 . Example A (110) oriented crystal MgAl 2 O 4 substrate was provided, and a 100 nm thick epitaxial CoCr 2 O 4 buffer layer was formed thereon by laser deposition (substrate at 600°C 133 mPa (1 mT) of 1% O 2 , 99% N 2 ; KrF (248 nm) laser at 10 Hz, about 3J/cm 2 energy density). The buffer layer was annealed in air at 1000°C for 30 minutes, followed by formation of a 150 nm thick epitaxial Mn 0.5 Zn 0.5 Fe 2 O 4 layer on the buffer layer by KrF laser deposition (substrate at 400°C; 133 mPa (1 mT) O 2 ; laser at 10 Hz, energy density about 4J/cm 2 ). This was followed by deposition of a 160 nm thick epitaxial layer of CoFe 2 O 4 by laser deposition, using the same deposition conditions. The resulting layer combination was substantially single crystal, with the FWHM rocking curve line width of the (440) reflection being 0.6°. Magnetic measurements of the combination yielded the results shown in FIG. 4.

Claims: An article comprising a layer of a first magnetic oxide material (the "first material") and a layer of a second magnetic oxide material (the "second material") that differs in composition from the first material and is in contact with the layer of the first material and forms an interface therewith, with cach of said layers being a substantially single crystal layer, CHARACTERIZED IN THAT a) both the first and second material are selected from magnetic oxides having a spinel crystal structure, the magnetic oxides having a garnet crystal structure, and the magnetic oxides having a cobalt Y hexaferrite crystal structure; b) the first and second materials are selected such that, at 20°C, the interface has an interface anisotropy energy K greater than 10 -5 Joules/m 2 (10 -2 erg/cm 2 ); c) the first and second materials are further selected such that, at 20°C, the layer of the second material has an asymmetric M-H loop such that the spins of the layer of second material are substantially pinned at the interface and the layer of second material is substantially free of magnetic domain boundaries. An article according to claim 1, wherein each of the first and second materials has the spinel crystal structure, or has the garnet crystal structure, or has the cobalt Y hexaferrite crystal structure. An article according to claim 1, wherein the first material is a ferromagnetic or ferrimagnetic oxide material having coercivity H c > 4x10 4 A/m (500Oe) at 20°C, and the second material is a ferromagnetic or ferrimagnetic oxide material have coercivity H c < 4x10 3 A/m (500e) at 20°C. An article according to claim 3 wherein the first magnetic oxide material is selected from the group consisting of CoFe 2 O 4 and (Mn, Ti)Fe 2 O 4 , and wherein the second magnetic oxide material is selected from the group consisting of (Mn, Zn)Fe 2 O 4 , Li 0.5 Fe 2.5 O 4 , and (Ni, Zn)Fe 2 O 4 . An article according to claim 1, wherein the first material is selected from the group consisting of the ferrimagnetic oxides having spinel crystal structure and the ferrimagnetic oxides having a garnet crystal structure and having a compensation temperature in the range 20°C ± 50°C. An article according to claim 5, wherein the first material is NiFeCrO 4 . An article according to claim 4, wherein the first material is CoFe 2 O 4 . An article according to claim 1, further comprising a patterned metal layer disposed on said second material. An article according to claim 8, wherein the patterned metal layer comprises a metal spiral adapted for use an inductor.

Inventors: GYORGY ERNST MICHAEL, PHILLIPS JULIA MAE, SUZUKI YURI, VAN DOVER ROBERT BRUCE, GYORGY, ERNST MICHAEL, PHILLIPS, JULIA MAE, SUZUKI, YURI, VAN DOVER, ROBERT BRUCE
Applicants: LUCENT TECHNOLOGIES INC, LUCENT TECHNOLOGIES INC.
Application year: 1996
Main classification: H01F10
IPC codes: H01F10, H01F17