ORGANO-TIN-CONTAINING COMPLEX STABILISER FOR SYNTHETIC RESIN COMPOSITIONS

Abstract: The invention relates to an organo-tin-containing complex stabiliser for synthetic resin compositions of the formula (I): M<2+>1-a-b(2+x)Al<3+>a[Sn(R)(2-x)]b<(2+x)+>(OH)<->2-b(2+x)A<n->a/n*mH2O wherein M<2+> stands for at least one divalent metal cation, R stands for a C1-12 linear or branched alkyl group, A<n-> stands for an n-valent anion or mixtures of anions, and the following conditions apply: 0<a<0.5; 0<b<0.1; 0</=x</=1; 0<a+b(2+x)<0.5; 0</=m</=2. The invention also relates to a method for the preparation of these stabilisers and their use in synthetic resin compositions, preferably halogen-containing synthetic resin compositions, or (co)polymers obtained by Ziegler Natta polymerization processes.

Description: ORGANO-TIN-CONTAINING COMPLEX STABILISER FOR SYNTHETIC RESIN COMPOSITIONS The invention relates to an organo-tin-containing complex stabiliser for synthetic resin compositions which comprises an aluminium cation and at least one divalent metal cation as well as organo-tin, and which is used for stabilising synthetic resin compositions, preferably halogen-containing synthetic resin compositions The invention also relates to a process for the preparation of these stabilisers Synthetic resin compositions, especially halogen-containing synthetic resm compositions, are subject to degradation under the influence of heat or light, such as loss of mechanical properties and/or discolouration. Therefore, it is the practice to incorporate compounds with a stabilising activity into the synthetic resin compositions Metal-containing stabilisers for this purpose have been known for quite some time. In the early days heavy metals such as cadmium and lead were present, but these are replaced nowadays by calcium, magnesium, and zinc compounds in demanding applications such as pipes, cables, and window profiles Then layered compounds comprising divalent and trivaient metal cations and, optionally, different anions were found to be a class of compounds with particularly good stabilisation properties. In the literature referred to, such stabilisers are frequently found under the name of hydrotalcite. To improve not only the stabilising activity, but also the initial colour and the avoidance of discolouration phenomena, the above-mentioned hydrotalcites are combined with other stabilisers. A frequently found combination is the one with organo-tin esters, since such compounds have proved to be excellent thermal stabilisers on the one hand, while on the other they have an extremely good effect on the initial colour and the transparency. Preferred organo-tin esters are alkyl-tin mercaptides, which use results in resins with improved thermostability and initial colour when compared to sulfur-free organo-tin esters. However these advantageous properties are countered by the drawback of odour problems resulting from the use of the organo-tin mercaptides. Moreover, the use of organo-mercaptides influences negatively the rheology and the Vicat softening temperature of the compositions. A combination of hydrotalcite containing two divalent metal cations and one trivaient metal cation with an organo-tin mercaptide has been descπbed in EP-A-0 189 899. EP-A-0 256 872 also discloses hydrotalcites in combination with magnesium oxide to stabilise synthetic resm compositions. However, these hydrotalcites have to be combined with either organo-tin stabilisers or with a mixture of beta- diketone and organic acid salts of zinc. Finally, in certain applications for synthetic resin compositions, such as cables, good electrical properties are additionally required, such as resistance to water absorption. Accordingly, it is an object of the present invention to provide a stabiliser which, when compared to conventional hydrotalcite stabilisers, improves the thermal stability, improves the initial colour, gives no odour, and improves the resistance to water absorption of the resins in which they are incorporated. It is another object to provide a preparation process for such a stabiliser. Finally, it is an object of the present invention to provide synthetic resin compositions comprising the stabiliser of the present invention having the improved properties mentioned above. Surprisingly, it has been found that the stabilisers of the present invention even improve the thermostability of the compositions compared to the combination of hydrotalcite and organo-tin stabilisers mentioned above. The present invention comprises a organo-tin-containing complex stabiliser of the following formula I: 2+ .. a - b(2+) Al 3+ a [Sn(R) (2 . x) ] b (2+x)+ (OH)- 2 . b(2+x) A n - a/n * mH 2 0 (I) wherein M 2+ stands for at least one divalent metal cation, R stands for a C 12 linear or branched alkyl group, A n" stands for an n-valent anion or mixtures of anions, and the following conditions apply: 0<a<0.5; 0<b<0.1 : 0<x<1 ; 0<a+b(2+x)<0.5; 0<m<2. Preferably, the stabilisers of the present invention comprise two divalent cations. Examples of the divalent cation include Mg, Zn, Ca, Ba, Sr, and Sn. Preferably, the R group is selected from the group of methyl, butyl, octyl, and dodecyl groups. Examples of the anions include carbonate, hydrogen carbonate, sulphate, phosphate, nitrate, nitrite, chlorate, hydroxyl, acetate, salicylate, maleate, phthalate, acetylacetonate, and halogen, such as chloride, and mixtures thereof. Preferably, the following conditions apply: 0.25<a<0.5; 0<b<0.05; 0<x≤1 ; 0.25<a+b(2+x)<0.5; 0≤m≤1. Examples of the organo-tin-containing complex stabilisers are: Mgo .47 Zn 0 17 Al 0.33 [Sn(C 8 H 17 ) 1.5 ] 0 . 012 (OH) 1.97 (CO 3 ) 0 . 165 * 0.5H 2 O Mg 0.47 Zn 0 16 Al α33 [Sn(C 4 H 9 ) 2 ] 0 . 02 (OH) 1 96 (Cθ 3 )o .165 * 0.5H 2 O Mg 0.476 Zno 17 Al 0.33 [Sn(CH 3 ) 2 ] 0 . 012 (OH) 1 976 (CO 3 )o .165 * 0.5H 2 0 go. 65 Alo .3 [Sn(C 8 H 17 ) 1.5 ]o . oi 6 (OH) 1 . 96 (CO 3 )o. 15 * 0-5H 2 0 go .65 Alo. 3 [Sn(C 4 H 9 ) 2 ] 0 .o 25 (OH) 1 . 95 (C0 3 )o. 15 # 0.5H 2 0 gα 668 Alo. 3 [Sn(CH 3 ) 2 ] 0 . 016 (OH) l.968 (Cθ 3 ) 0 . l5 * 0.5H 2 0 The present invention also comprises a preparation process for the organo-tin- containing complex stabiliser. Hereto an organo-tin compound is introduced during the manufacturing process for the stabiliser. This process typically comprises a flrst step wherein primary particles are formed and a second step during which a more regular crystallization with change in form and size takes place. The organo-tin compound may be added at any point of the first step in the process. In a preferred process an organic tin salt is combined with at least one divalent metal cation source in an aqueous system at the beginning of said first reaction step, whereafter an aluminium source is added to form the primary particles of the organo-tin-containing complex stabiliser. The reaction is carried out at elevated temperatures, preferably between 50 and 200°C, more preferably between 60 and 160°C. The desired pH range is between 9 and 12. Preferably, the pH is between 10 and 12. When a basic aluminium compound is applied, the pH is set automatically. Otherwise, base compounds such as alkali hydroxide, e.g., sodium hydroxide, have to be present. The divalent metal cation compound is selected from the salts, oxides, hydroxides, and mixtures thereof. Examples include zinc sulphate, zinc oxide, magnesium chloride, magnesium oxide, magnesium carbonate, and basic magnesium carbonate (4MgC0 3 * Mg(OH) 2 * 4H 2 0). Aluminium is added in the form of reactive hydroxide, oxide or of its salt, e.g., aluminium sulphate or sodium aluminate. The organo-tin source is preferably selected from an alkyl tin trichloride or dialkyl tin dichloride or mixtures thereof, e.g., dimethyl tin dichloride, octyl tin chloride (a composition comprising octyl tin trichloride and dioctyl tin dichloride), and dibutyl tin dichloride. Preferably, a certain time period elapses before the aluminium source is added to the reaction mixture of the divalent metal source(s) and organo-tin salt. More particularly, the first adduct is aged during a time period ranging from 15 minutes to 5 hours before the aluminium source is added. The incoφoration of the anions is carried out in a simple manner through the use of the corresponding salts of the divalent metals, such as the above-mentioned carbonate, hydrogen carbonate, sulphate, phosphate, nitrate, nitrite, chlorate, hydroxyl, acetate, salicylate, maleate, phthalate, acetylacetonate, and halogen, such as chloride, and mixtures thereof, through the addition of the anions as alkali salt solution, such as the addition of NaHC0 3 , or by leading carbon dioxide through the suspension. If the organo-tin compound is incorporated in the flrst process step, the thereby obtained complex stabiliser will have a reduced average particle size. Typically, the addition of the organo-tin compound leads to primary particles with an average particle size of 100-200 nm, compared to about 500 nm when the organo-tin compound is not used. A correlation of the reduced primary particle size and improved performance of the stabiliser is likely, however, the Applicant does not want to be limited to such theory. The thus formed organo-tin-containing stabiliser complex is filtered and washed with water until it is free of salt and optionally subjected to a second process step, which is known in the art as a hydrothermal treatment, optionally under the corresponding vapour pressure. Subsequently, it may also be subjected to a surface treatment known in the art, applying a coating onto the complex. For the surface treatment, which is a preferred embodiment of the present invention, use may be made of known substances such as fatty acids, salts, and esters thereof, glycerin esters, and silanes. Examples include stearic acid, sodium stearate, zinc stearate, tetraalkoxy silane, and vinyl alkyloxy silane. The amount of coating compound to be added is in the range of 1 to 6 wt%, preferably 2 to 5 wt%, calculated on the prepared organo-tin-containing complex stabiliser. Without wishing to be so restricted, Applicant believes that the organo-tin containing complex stabiliser has a layered structure, e.g., a hydrotalcite structure. By reaction with a Grignard reagent and subsequent gaschromatographic analysis it was demonstrated that the organic groups of the organo-tin moiety of the stabiliser remained to be covalently bonded to the tin atom. The so-formed organo-tin-containing complex stabiliser is used in synthetic resin compositions, such as halogen-containing resin compositions, e.g., polyvinyl chloride, or polyolefin (co)polymers obtained by Ziegler Natta polymerizations. In these compositions costabilisers may be present as well as lubricants, plasticisers, fillers, and impact strength modifiers. The compositions of the present invention are applied, inter alia, in profiles, sheets, pipes, cables, and household articles. The invention will be further illustrated by the following examples. Example? A) Preparation of complex stabilisers containing two divalent metal cations Example 1 In 1500 ml of deionised water were suspended with stirring 14.5 g ZnS0 4 * 7H 2 0, 28.0 g MgCI 2 * 6H 2 0, 13.0 g NaOH (solid), and 30.0 g NaHC0 3 , and the whole was heated to 80°C. After continuous stirring for 30 minutes 1.30 g of octyl tin chloride (Sn content 31.8%, monooctyl:dioctyl molar ratio 1 :1) were added dropwise at 80°C within 2 minutes. The suspension was stirred for 2 hours. Subsequently, 29.0 g of a solution of AI 2 (S0 4 ) 3 * 14H 2 0 in 250 ml of deionised water were dosed within 10 minutes. After 4 hours, the product was hot filtered and washed with 2 I of deionised water to make the product salt-free. Next, the filter cake was suspended in 1 I of deionised water and subjected to a hydrothermal treatment, firstly for 2 hours at 90°C and then for 5 hours at 160°C at the corresponding vapour pressure. After this the product was cooled down to 90°C and coated with 1.2 g of sodium stearate. After 10 minutes the solid matter was filtered off hot and dried at 110°C to constant weight. After milling the average particle diameter was 0.99 μm and the specific surface area was 16 m 2 /g. The yield was 25.3 g. Analysis of the material yielded the following result: 13.2 of Mg 12.9% of Zn 10.5% of Al 1.6% of Sn This result is indicative for a complex stabiliser of the formula: Mgo 47 Zno 17 Al 0 . 33 [Sn(C 8 H 17 ) 1.5 ]o.oι 2 (OH) 1 97 (CO 3 ) o l65 * 0.5H 2 0 Example 2 Into 1500 ml of deionised water were stirred 66.0 g of basic magnesium carbonate, i.e. 4MgC0 3 * Mg(OH) 2 " r 4H 2 O, and 20.0 g of ZnO, and the whole was heated to 85°C. After 30 minutes, 9.2 g of dibutyl tin dichloride (Sn content 39.06%) were added dropwise at 85°C within 10 minutes. The suspension was stirred for 1 hour, whereupon at 85°C 138.0 g of a 29.9% solution of sodium aluminate (Al 2 0 3 content 18.6%) were added within 10 minutes. After 4 hours the solid matter was filtered off hot and washed salt-free with 1 I of deionised water. The filter cake was subsequently suspended in 1.5 I of deionised water and subjected to a hydrothermal treatment, firstly at 95°C for 4 hours and then for 4 hours at 140°C at the corresponding vapour pressure. Next, the product was cooled down to 90 β C and coated with 3.0 g of stearic acid. The solid matter was filtered off hot and dried at 110 β C to constant weight. After milling the average particle diameter was 1.04 μm and the specific surface area was 15 m 2 /g. The yield was 133.1 g. Analysis of the material yielded the following result: 12.9% of Mg 12.0% of Zn 10.0% of Al 2.6% of Sn This result is indicative for a complex stabiliser of the formula: Mg 0 47 Zn 0 16 AI 0 33 [Sn(C 4 H 9 ) 2 ] 0.02 (OH) 1 96 (CO 3 ) 0 165 * 0.5H 2 O Example 3 Example 1 was repeated, except that 1.30 g of octyl tin chloride was replaced by 0.75 g of dimethyl tin dichloride. After milling the average particle diameter was 1.02 μm and the specific surface area was 13 m 2 /g. The yield was 25.3 g. Analysis of the material yielded the following result: 13.1% of Mg 12.9% of Zn 10.4% of Al 1.6% of Sn This result is indicative for a complex stabiliser of the formula: Mgo .476 Zn 0 17 Al 0.33 [Sn(CH 3 ) 2 ] 0. o 12 (OH) 1.976 (C0 3 ) 0.165 * 0.5H 2 0 Comparative Example A In 1500 ml of deionised water were suspended with stirring 14 5 g ZnS0 4 * 7H 2 0, 31.0 g MgCI 2 * 6H 2 0, 12.0 g NaOH (solid), and 30.0 g NaHC0 3 , and the whole was heated to 80°C. The suspension was stirred for 2 hours. Subsequently, 29.0 g of a solution of AI 2 (S0 4 ) 3 * 14H 2 0 in 250 ml of deionised water were dosed within 10 minutes. After 4 hours, the product was hot filtered and washed with 2 I of deionised water to make the product salt-free. Next, the filter cake was suspended in 1 I of deionised water and given a hydrothermal treatment, firstly for 2 hours at 90°C and then for 5 hours at 160°C at the corresponding vapour pressure After this the product was cooled down to 90°C and coated with 1 2 g of sodium stearate. After 10 minutes the solid matter was filtered off hot and dried at 110°C to constant weight. After milling the average particle diameter was 1.11μm and the specific surface area was 15 m 2 /g. The yield was 25.2 g. Analysis of the material yielded the following result: 14.4% of Mg 13.1 % of Zn 10.6% of Al This result is indicative for a complex stabiliser of the formula. Mg 05 Zn 0 17 AI 0 33 (OH) 2 (CO 3 ) 0 165 * 0.5H 2 O B) Preparation of complex stabilisers containing one divalent metal cation Example 4 In 1500 ml of deionised water were suspended with stirring 41.8 g MgCI 2 * 6H 2 0, 18.0 g NaOH (solid), and 27 0 g NaHC0 3 , and the whole was heated to 80°C After continuous stirring for 30 minutes 1 9 g of octyl tin chloride (Sn content 31 8%, mono-di ratio 1 1) were added dropwise at 80 C C within 2 minutes The suspension was stirred for 2 5 hours Subsequently, 29 0 g of a solution of AI 2 (S0 4 ) 3 * 14H 2 0 in 250 ml of deionised water were dosed within 10 minutes After 4 hours, the product was hot filtered and washed with 2 I of deionised water to make the product salt-free Next, the filter cake was suspended in 1 I of deionised water and given a hydrothermal treatment, firstly for 2 hours at 90°C and then for 5 hours at 160°C at the corresponding vapour pressure After this the product was cooled down to 90°C and coated with 1.2 g of sodium stearate After 10 minutes the solid matter was filtered off hot and dried at 110°C to constant weight After milling the average particle diameter was 3 41 μm and the specific surface area was 16 m 2 /g The yield was 25.4 g Analysis of the material yielded the following result: 19.8% of Mg 10.2% of Al 2.4% of Sn This result is indicative for a complex stabiliser of the formula: Mg 066 AI 0 3 [Sn(C 8 H 17 ) 1 s OH), 96 . CO 3 ) 0 15 * 0.5H 2 O Example 5 In 1500 ml of deionised water were suspended with stirring 41.3 g MgCI 2 * 6H 2 0, 18.0 g NaOH (solid), and 27.0 g NaHC0 3 , and the whole was heated heated to 80°C. After continuous stirring for 30 minutes 2.4 g of dibutyl tin dichloride (Sn content 39.06%) were added dropwise at 80°C within 3 minutes. The suspension was stirred for 1 hour. Subsequently, 29.0 g of a solution of AI 2 (SO 4 ) 3 * 14H 2 O in 250 ml of deionised water were dosed within 10 minutes. Subsequent steps are the same as described in Example 4. After milling the average particle diameter was 3.16 μm and the specific surface area was 13 m 2 /g. The yield was 25.6 g. Analysis of the material yielded the following result: 19.5% of Mg 10.1 % of Al 3.6% of Sn This result is indicative for a complex stabiliser of the formula: Mg 065 AI 0 3 [Sn(C 4 H 9 ) 2 3o . o 25 (OH) 1 . 95 (C0 3 ) 0.15 * 0.5H 2 0 Example 6 In 1500 ml of deionised water were suspended with stirring 44.4 g MgC. 2 * 6H 2 0, 18.0 g NaOH (solid), and 27.0 g NaHC0 3 , and the whole was heated to 80°C. After continuous stirring for 30 minutes 1.15 g of dimethyl tin dichloride (Sn content 54%) were added dropwise at 80°C within 2 minutes. The suspension was stirred for 1 hour. Subsequently, 29.0 g of a solution of AI 2 (S0 4 ) 3 * 14H 2 0 in 250 ml of deionised water were dosed within 10 minutes. Subsequent steps are the same as described in Example 4. After milling the average particle diameter was 3.40 μm and the specific surface area was 15 m 2 /g. The yield was 25.1 g. Analysis of the material yielded the following result: 20.5% of Mg 10.5% of Al 2.4% of Sn This result is indicative for a complex stabiliser of the formula: go .668 Alo. 3 [Sn(CH 3 ) 2 ]o . oi 6 (OH) 1.968 (C0 3 )o .15 * 0.5H 2 0 Comparative Example B In 1500 ml of deionised water were suspended with stirring 46.0 g MgCI 2 * 6H 2 O, 17.0 g NaOH (solid), and 27.0 g NaHC0 3> and the whole was heated to 80°C. The suspension was stirred for 2 hours. Subsequently, 29.0 g of a solution of AI 2 (S0 4 ) 3 *14H 2 O in 250 ml of deionised water were dosed within 10 minutes. After 4 hours, the product was hot filtered and washed with 2 I of deionised water to make the product salt-free. Next, the filter cake was suspended in 1 I of deionised water and given a hydrothermal treatment, firstly for 2 hours at 90°C and then for 5 hours at 160°C at the corresponding vapour pressure. After this the product was cooled down to 90°C and coated with 1.2 g of sodium stearate. After 10 minutes the solid matter was filtered off hot and dried at 110°C to constant weight. After milling the average particle diameter was 3.53 μm and the specific surface area was 17 m 2 /g. The yield was 24.9 g. Analysis of the material yielded the following result: 22.0% of Mg 10.6% of Al This result is indicative for a complex stabiliser of the formula: Mgo 7 AI 0 3 (OH) 2 (C0 3 )o 15 * 0.5H 2 0 C) Performance tests The organo-tin-containing complex stabilisers according to the invention and the comparative complex stabilisers prepared above were tested for their performance in PVC resin. Profile Recipe A 100 parts PVC K 68 - graft copolymer 1 phr acrylic processing aid 3 phr titianium dioxide 3 phr calcium carbonate 0.2 phr zinc laurate 0.2 phr calcium stearate 0.1 phr stearoyl benzoyl methane 0.3 phr tris(2-hydroxyethyl)isocyanurate 0.2 phr polyethylene wax 0.6 phr distearyl phthalate 0.3 phr bis(2,4-di-t.butylphenyl) pentaerythritol diphosphite phr = parts by weight per hundred parts (by weight) of resin Into this recipe complex stabilisers as prepared according to Examples 1 to 6 and Comparative Examples A and B were incorporated. When the complex stabilisers of the comparative examples were applied, an alkyl tin (2-ethylhexyl) thioglycolate stabiliser (alkyl TTG) was also incorporated into the PVC composition. The alkyl TTG is typically a mixture of dialkyl tin di(2-ethyl hexyl) thioglycolate and monoalkyl tin tris(2-ethyl hexyl) thioglycolate. Table 1 lists the compositions. Table 1 Example Stabiliser Alkyl TTG 1A 1.2 phr ex. 1 2A 1.2 phr ex. 2 3A 1.2 phr ex. 3 AA 1.2 phr comp. ex. A AAO 1.2 phr comp. ex. A 0.13 phr octyl TTG (15% Sn) AAB 1.2 phr comp. ex. A 0.17 phr butyl TTG (18% Sn) AAM 1.2 phr comp. ex. A 0.09 phr methyl TTG (21% Sn) 4A 1.2 phr ex. 4 5A 1.2 phr ex. 5 6A 1.2 phr ex. 6 BA 1.2 phr comp. ex. B BAO 1.2 phr comp. ex. B 0.19 phr octyl TTG (15% Sn) BAB 1.2 phr comp. ex. B 0.24 phr butyl TTG (18% Sn) BAM 1.2 phr comp. ex. B 0.14 phr methyl TTG (21% Sn) Octyl TTG and butyl TTG were supplied by Akcros Chemicals GmbH as Tinstab® OTS 17 MS and Tinstab® BTS 70, respectively. Methyl TTG was supplied by Morton International as Advastab® TM-181-FS. The compositions were tested for thermostability, odour, and initial colour. The thermostability was measured in accordance with the Congo-Red method (DIN 53381 method D) at 190°C. To this end, sheets of 0.4 mm thick were prepared on a two-roil mill at a temperature of 175°C. The odour of the resin was determined by analyzing the sheets when they were taken from the two-roll mill during the preparation of specimen for the thermostability test. Measurement of the initial colour was carried out with a multispectral measurement technique using the CIE 1976 standard. To this end, 2 mm thick sheets were prepared on the roll mill at 190°C. The diffus reflectance of the sheets was observated under 10° observer angle by subjecting the sheets to daylight D65 under an angle of 8°. The characteristic of the yellow colouration is the Cielab b * -value. Table 2 Example Thermostability Initial colour (min) (b*-value) AA 44.7 17.1 AAO 47.0 15.9 1A 50.8 15.4 AAB 46.3 16.0 2A 50.0 15.6 AAM 46.0 16.2 3A 52.5 15.3 BA 36.2 23.2 BAO 38.9 21.1 4A 40.0 20.3 BAB 37.0 22.9 5A 38.6 20.9 BAM 38.1 22.0 6A 42.7 20.0 All alkyl-TTG containing samples had a mercaptan-like smell. This smell was absent in the samples comprising a stabiliser according to the invention. The organo-tin-containing complex stabilisers of the present invention were also tested in Cable Recipe B, a plasticiser-containing recipe. They were tested for thermostability and water absorption. Cable i Recip e B 100 parts PVC K 70 50 phr calcium carbonate 40 phr dioctyl phthalate 0.65 phr zinc laurate 0.2 phr Bisphenol A 0.2 phr natural paraffin Into this recipe the complex stabilisers prepared according to Examples 1 to 6 or Comparative Examples A and B were incorporated. When the complex stabilisers of Comparative Examples A and B were applied, alkyl TTG was also incorporated into the resin composition. Table 3 lists the resulting compositions. Table 3 Example Stabiliser Alkyl TTG 1B 3.0 phr ex 1 - 2B 3.0 phr ex. 2 - 3B 3.0 phr ex. 3 - AB 3.0 phr comp. ex. A - ABO 3.0 phr comp. ex. A 0.32 phr octyl TTG (15% Sn) ABB 3.0 phr comp. ex. A 0.43 phr butyl TTG (18% Sn) ABM 3 0 phr comp. ex. A 0.23 phr methyl TTG (21% Sn) 4B 3.0 phr ex 4 - 5B 3.0 phr ex. 5 - 6B 3.0 phr ex. 6 - BB 3.0 phr comp. ex. B - BBO 3.0 phr comp. ex. B 0 48 phr octyl TTG (15% Sn) BBB 3.0 phr comp. ex. B 0.60 phr butyl TTG (18% Sn) BBM 3.0 phr comp. ex. B 0.34 phr methyl TTG (21% Sn) The compositions were tested for thermostability as described above, except for the temperature being changed from 190° to 200°C Again the alkyl-TTG containing samples smelled bad while the compositions according to the invention did not. Water absorption for the cable compositions was tested by subjecting 40x40x0.4 mm sheets to deionised water at a temperature of 70°C for 20 days. The increase in weight in percentage terms was then measured on the dried sheets. Table 4 It is clear from Tabies 2 and 4 that the organo-tin-containing complex stabilisers according to the present invention provide improved colour resistance, a better smell, and a better resistance to water absorption together with improved thermostability as compared with the stabiliser compositions according to the prior art.

Claims: CLAIMS 1. A organo-tin-containing complex stabiliser of the following formula I: M 2+ 1-a . b(2 . x) Al 3+ a [Sn(R) (2 . x) ] b (2*x)+ (OH)- 2-b(2+x) A n - a/n * mH 2 0 (I) wherein M + stands for at least one divalent metal cation, R stands for a C 1-12 linear or branched alkyl group, A π" stands for an n-valent anion or mixtures of anions, and the following conditions apply: 0<a<0.5: 0<b<0.1 ; O≤x≤l ; 0<a+b(2+x)<0.5; 0≤m≤2. 2. A stabiliser according to claim 1 , characterised in that comprises two divalent cations. 3. A stabiliser according to either of the preceding claims, characterised in that the divalent cation is selected from Mg, Zn, Ca, Ba, Sr, and Sn. 4. A stabiliser according to any one of the preceding claims, characterised in that the R group is selected from the group of methyl, butyl, octyl, and dodecyl groups. 5. A stabiliser according to any one of the preceding claims, characterised in that the anion is selected from the group of carbonate, hydrogen carbonate, sulphate, phosphate, nitrate, nitrite, chlorate, hydroxyl, acetate, salicylate, maleate, phthalate, acetylacetonate, and halogen, such as chloride, and mixtures thereof. 6. A stabilizer according to any one of the preceding claims, characterised in that the following conditions apply: 0.25<a<0.5; 0<b<0.05; 0≤x<1; 0.25<a+b(2+x)<0.5; 0≤m<1. 7. A stabiliser according to claim 6, characterised in that the stabiliser is selected from: g 047 Zn 0.17 AI 033 [Sn(C 8 H 17 ) 1.5 ] 0012 (OH) 1 97 (C0 3 )o .165 * 0.5H 2 0 Mg 047 Zn 0 16 AI 033 [Sn(C 4 H 9 ) 2 ] 002 (OH) 1 96 (CO 3 ) 0 165 * 0.5H 2 O Mg 0476 Zn 0 .7 Al 0.33 _Sn(CH 3 ) 2 ] 0 0.2 (OH), 976 (CO 3 ) 0.165 * 0.5H 2 O Mg 066 AI 0 3 [Sn(C 8 H 17 ) 1.5 ] 0.016 (OH) 1.96 (CO 3 ) 0 15 * 0.5H 2 O Mg 0.65 Al 0 3 [Sn(C 4 H 9 ) 2 ] 0025 (OH) 1 . 95 (CO 3 ) 0 15 * 0.5H 2 O g 0668 Alo .3 [Sn(CH 3 ) 2 ] 0 o 16 (OH) 1 96β (CO 3 ) 0 15 * 0.5H 2 O 8. A stabiliser according to any one of the preceding claims, characterised in that the stabiliser has a coating of 1 to 6 wt% coating compound based on the weight of the stabiliser. 9. A stabiliser according to any one of claims 1-8, characterised in that it is odour free. 10. A stabiliser according to any one of claims 1-9, characterised in that the primary particles of the stabiliser have an average particle size of less than 250 nm. 11. An organo-tin-containing complex stabiliser obtainable by a process comprising a first step in an aqueous system in which at least one divalent metal cation source is reacted with an organo-tin compound, whereafter an aluminium source is added, the process being carried out at a temperature between 50° and 200°C and the pH ranges from 9 to 12. 12. A process for the preparation of the organo-tin-containing complex stabiliser according to claims 1 to 10, characterised in that in an aqueous system in a first step at least one divalent metal cation source is reacted with an organo-tin compound, whereafter an aluminium source is added, the process being carried out at a temperature between 50° and 200°C and the pH ranges from 9 to 12 13 A process according to claim 12, characterised in that a certain time period elapses before the aluminium source is added, i e. 15 minutes to 5 hours 14 A process according to claims 12 and 13, characterised in that the stabiliser is subsequently subjected to a hydrothermal treatment, optionally under the corresponding vapour pressure 15 A process according to claims 12 to 14, characterised in that the stabiliser is subjected to a surface treatment applying a coating onto the complex 16. A synthetic resm composition comprising the stabiliser according to claims 1 to 11 17 An article comprising the synthetic resin according to claim 16

Inventors: HENNE PETER, HORN VOLKER, KLAESS PETER, MELLOR MALCOLM THOMAS JOHN, ORCHISON JACK JAMES ANGUS, SCHMETS GERARD HUBERT FRANS, HENNE, PETER, HORN, VOLKER, KLAESS, PETER, MELLOR, MALCOLM, THOMAS, JOHN, ORCHISON, JACK, JAMES, ANGUS, SCHMETS, GERARD, HUBERT, FRANS
Applicants: AKCROS CHEM, HENNE PETER, HORN VOLKER, KLAESS PETER, MELLOR MALCOLM THOMAS JOHN, ORCHISON JACK JAMES ANGUS, SCHMETS GERARD HUBERT FRANS, AKCROS CHEMICALS, HENNE, PETER, HORN, VOLKER, KLAESS, PETER, MELLOR, MALCOLM, THOMAS, JOHN, ORCHISON, JACK, JAMES, ANGUS, SCHMETS, GERARD, HUBERT, FRANS
Application year: 1996
Main classification: C08K5
IPC codes: C01B13, C01F7, C07F7, C08K3, C08K5, C08K9, C08L27