Polyphenylene ether resin composition

Abstract: A resin composition with improved compatibility between polyphenylene ether (PPE) resin and thermoplastic polyester (PE) resin from which molded articles with high mechanical strength, especially impact resistance, can be obtained, comprises (A) 5 to 90 percent by weight of PPE resin and (B) 95 to 10 percent by weight of thermoplastic PE resin, and per total 100 parts by weight (A) and (B), (C) 0.01 to 30 parts by weight of a compound simultaneously having (A) a residue of a compound selected from among maleic acid esters, maleimide, maleinamic acid esters, and their derivatives and (B) residue of a compound selected from among oxazoline, oxazine, oxazolone, oxazinone, and their derivatives, and (D) 0.01 to 3 percent by weight of an organic peroxide which has a half life of one minute at temperatures ranging from 100 to 270°C.

Description: The present invention concerns a resin composition containing polyphenylene (sometimes abbreviated as PPE hereinbelow) and polyester resin (sometimes abbreviated as PE hereinbelow). PPE resin is heat resistant, and it has good mechanical strength, electrical properties, dimensional stability. However, it is susceptible to attack from aromatic hydrocarbon solvents such as benzene and halogenohydrocarbon solvents such as trichloroethane. Since PPE has poor moldability, PPE used alone has not found much use in molded articles. Blending polystyrene resin with PPE resin has therefore been proposed as a method for improving PPE's moldability. While this method does improve moldability, the resultant resin blends have poor solvent resistance, since polystyrene resin is also susceptible to attack by the above-mentioned solvents. Numerous alloys of PPE resin and polyamide resin have been proposed for the purpose of improving both solvent resistance and moldability (for example, Japan Examined Patent Application Kokoku No. Sho 45-997), but PPE-polyamide alloys lose mechanical strength, dimensional stability by absorbing moisture. Other inventors have considered adding thermoplastic polyester resins to PPE in order to improve the later's moldability and solvent resistance. However, PPE and polyester resins have poor compatibility, and molded articles made from them have low mechanical strength. The addition of various compatibilizers was proposed to remedy this situation. For example, it has been claimed that resin compositions providing molded articles that have good flexural elasticity, heat resistance, moldability, and water resistance can be obtained by adding compounds containing at least one from among carboxyl groups, acid anhydride groups, acid amide groups, imide groups, carboxylic acid ester groups, epoxy groups, amino groups, and hydroxyl groups (Kokoku No. Sho 63-350). It has also been proposed to obtain resin compositions providing molded articles that have excellent appearance, impact resistance, moldability, dimensional stability, and chemical resistance by adding a bifunctional epoxy compound (Kokoku No. Sho 63-39958). It is also known to improve the dispersion of PPE resin and polyester by adding a polymer obtained by reacting polyester and PPE with epoxy groups (Kokoku No. Sho 63-125569). The object of the present invention is to provide a resin composition in which the compatibility of PPE resin and thermoplastic polyester resin is improved and which provides molded articles with high mechanical strength, especially high impact resistance. As a result of intensive studies aimed at achieving this object, the present inventors discovered that specific compounds that are selectively reactive with PPE resin, specific compounds that are selectively reactive with thermoplastic polyester resin, and specific organic peroxides, when used in combination, act effectively as a compatibilizing agent, compatibilizing both resins well and causing the mechanical strength of molded articles made from them to be improved. Thus, the resin composition of the present invention contains (A) 5 to 90 percent by weight of polyphenylene ether resin; (B) 95 to 10 percent by weight of thermoplastic polyester resin, the composition also containing, per total 100 parts by weight of (A) and (B); (C) 0.01 to 30 parts by weight of a compound having (a) a residue of a compound selected from maleic acid esters or their derivatives represented by formula (i), where each R a and R b is independently selected from the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms, and R c is selected from the group consisting of alkyl groups containing 1 to 20 carbon atoms and aryl groups containing 6 to 14 carbon atoms; maleimide and its derivatives represented by formula (ii), where each R d and R e is independently selected from the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms; maleinamic acid esters and their derivatives represented by formula (iii), where each R f , R g and R i is independently selected from the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms, and R h is selected from among the group consisting of alkyl groups containing 1 to 20 carbon atoms and aryl groups containing 6 to 14 carbon atoms; and (b) a residue of a compound selected from oxazoline and its derivatives represented by formula (iv), where each R 1 , R 2 , R 3 and R 4 is independently selected from among the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms; oazines and their derivatives represented by formula (v), where each R 5 , R 6 , R 7 and R 8 is independently selected from the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms; oxazilone and its derivatives represented by formula (vi), where each R 9 and R 10 is independently selected from the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms; oxazinone and its derivatives represented by formula (vii), where each R 11 and R 12 is independently selected from the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms; and (D) 0.01 to 3 parts by weight of an organic peroxide which has a half life of one minute at a temperature within the range 100 to 270°C. PPE resins known in the art may be used as the PPE resin (A), for example. homopolymers or copolymers obtained by oxidative polymerization of at least one compound described by general formula (I) (where each R 1 , R 2 , R 3 , R 4 , and R 5 is independently selected from among hydrogen atoms, halogen atoms, hydrocarbon groups, or substituted hydrocarbon groups (for example, halogenohydrocarbon groups). Specific examples of the polymers include poly(2,6-dimethyl-1,4-phenylene) ether, poly(2,6-diethyl-1,4-phenylene) ether, poly(2-methyl-6-ethyl-1,4-phenylene) ether, poly(2-methyl-6-propyl-1,4-phenylene) ether, poly(2,6-dipropyl-1,4-phenylene) ether, poly(2-ethyl-6-propyl-1,4-phenylene) ether, poly(2.6-dimethoxy-1,4-phenylene) ether, poly(2,6-dichloromethyl-1,4-phenylene) ether, poly(2,6-dibromomethyl-1,4-phenylene) ether, poly(2,6-diphenyl-1,4-phenylene) ether, poly(2,6-ditrityl-1,4-phenylene) ether, poly(2,6-dichloro-1,4-phenylene) ether, poly(2.6-dibenzyl-1,4-phenylene) ether, and poly(2,5-dimethyl-1,4-phenylene ether. An especially preferred PPE resin is poly(2,6-dimethyl-1,4-phenylene) ether. An example of the polyphenylene ether copolymer is a copolymer containing some amount of an alkyl-3-substituted phenol, for example, 2,3,6-trimethylphenol, in the above-described polyphenylene ether repeating unit. Copolymers in which styrene is grafted to these polyphenylene ethers may also be used. Examples of polyphenylene ethers with grafted styrene compounds include copolymers obtained by graft-polymerizing styrene, α-methylstyrene, vinyltoluene, chlorostyrene, or the like to the above-described polyphenylene ethers. It is preferred that the PPE resins used in the invention have an intrinsic viscosity of 0.15 to 0.65 dL/g when measured at 30°C in a chloroform solvent, 0.30 to 0.60 dL/g being especially preferred. Compositions obtained from resins with an intrinsic viscosity of less than 0.15 dL/g tend to be brittle and have poor mechanical strength. PPE resins with an intrinsic viscosity exceeding 0.65 dL/g have too great a difference in viscosity with thermoplastic polyester and tend not to disperse well. The thermoplastic polyester resins used in the invention, which are known in the art, are polymers with ester linkages in the main chain of the molecule. Specific examples of them are polycondensed polyesters obtained by reacting dicarboxylic acid or a derivative thereof with a diol; polycondensed polyesters obtained by reacting dicarboxylic acid or a derivative thereof with a cyclic ether compound; polycondensed polyesters obtained by reacting a metal salt of dicarboxylic acid with a dihalide compound; and polycondensed polyesters obtained by ring-opening polymerization of a cyclic ester compound. Aliphatic or aromatic forms of dicarboxylic acid can be used. Examples of aliphatic dicarboxylic acids include unsaturated fatty acids such as oxalic acid, succinic acid, and adipic acid. Alicyclic dicarboxylic acids such as cyclohexanedicarboxylic acid can also be used. Examples of aromatic dicarboxylic acids include terephthalic acid, isophthalic acid, phthalic acid, and chlorophthalic acid. These acids may be used singly or in combinations of two or more. Aromatic dicarboxylic acids are preferred. with terephthalic acid, isophthalic acid. and phthalic acid being especially preferred. Examples of metal salts of dicarboxylic acids are alkali metal salts of the above-mentioned dicarboxylic acids. What is meant here by a derivative of a dicarboxylic acid is an anhydride, ester, salt, or similar derivative of a dicarboxylic acid. Aliphatic or aromatic diols may be used as the diol. Examples of aliphatic diols include dihydric alcohols such as ethylene glycol, propylene glycol, butane-1,4-diol, and hexamethylene glycol, with ethylene glycol or butane-1,4-diol being especially preferred. Examples of aromatic diols include bisphenol A and resorcinol. The diols may be used singly or in combinations of two or more. Examples of cyclic ether compounds include ethylene oxide and propylene oxide. The above-described diols in which two of the hydroxy groups have been substituted with halogens, for example, chlorine or bromine, can be used as dihalide compounds. ε-caprolactone can be used as the cyclic ester compound. The thermoplastic polyester resin used in the invention can be manufactured by any conventional method, using any of the above-mentioned raw materials. The preferred intrinsic viscosity, as an index of molecular weight, at least 0.50, at least 0.55 being especially preferred, when measured at 30°C in a 1:1 mixture (by weight) of the solvents phenol and tetrachloroethane. If the intrinsic viscosity of the thermoplastic polyester is less than 0.50, it is difficult to obtain molded articles having good mechanical properties from a melt-kneaded blend of polyester resin and PPE resin. The PPE resin (A) and thermoplastic polyester resin (B) are blended in amounts by weight of 5 to 90 parts of (A) per 95 to 10 parts of (B), preferably 20 to 50 parts of (A) per 80 to 50 parts of (B). If too much (A) is used, the resin composition will have poor moldability and solvent resistance, and if too much (B) is used, the composition will have poor dimensional stability and a low heat deflection temperature under loading. Component (C) in the resin composition of the invention is a compound simultaneously having (a) residues of compounds selected from among maleic acid esters, maleimide, maleinamic acid esters. and derivatives thereof and (b) residues of compounds selected from among oxazoline, oxazine, oxazolone, oxazinone, and derivatives thereof. The group (a) residues are discussed first. Residues of maleic acid esters or their derivatives are described by, for example, formula (i), hereinbelow (where each R a and R b is independently selected from the group consisting of hydrogen atoms, alkyl groups containing one to 20 carbon atoms, and aryl groups containing six to 14 carbon atoms, and R c is selected from the group consisting of alkyl groups containing one to 20 carbon atoms and aryl groups containing six to 14 carbon atoms). Residues of maleimide and its derivatives are described by, for example. formula (ii), hereinbelow (where each R d and R e is independently selected from the group consisting of hydrogen atoms, alkyl groups containing one to 20 carbon atoms, and aryl groups containing six to 14 carbon atoms). Residues of maleinamic acid esters and their derivatives are described by, for example, formula (iii), hereinbelow (where each R f , R g , and R i is independently selected from the group consisting of hydrogen atoms, alkyl groups containing one to 20 carbon atoms. and aryl groups containing six to 14 carbon atoms, and R h is selected from among the group consisting of alkyl groups containing one to 20 carbon atoms and aryl groups containing six to 14 carbon atoms). The alkyl groups containing one to 20 carbon atoms referred to here may be straight-chain or branched. It is preferred that the alkyl groups contain one to three carbon atoms. Preferred examples of alkyl groups include methyl, ethyl, and propyl groups. Specific preferred examples of aryl groups containing six to 14 carbon atoms include phenyl groups, benzyl groups, tolyl groups, xylyl groups, and trityl groups. It is preferred to select R a and R b in formula (i), hereinabove, from among hydrogen atoms, methyl groups, and ethyl groups and R c from among methyl groups and ethyl groups. It is preferred to select R d and R e in formula (ii). hereinabove, from among hydrogen atoms, methyl groups, and ethyl groups. It is preferred to select R f , R g , and R i in formula (iii), hereinabove, from among hydrogen atoms, methyl groups, and ethyl groups and R h from among methyl groups and ethyl groups. The group (b) residues are discussed hereinbelow. Oxazoline, oxazine, oxazolone, oxazinone, and their derivatives may have free valance at any position. These compounds have at least two possible resonance structures, and they may have any structure in the invention. Preferred residues of oxazoline and its derivatives are described by, for example, formula (iv), hereinbelow (where each R 1 , R 2 , R 3 , and R 4 is independently selected from among the group consisting of hydrogen atoms, alkyl groups containing one to 20 carbon atoms, and aryl groups containing six to 14 carbon atoms.) The oxygen, nitrogen, and carbon atoms in the oxazines may occupy any position. and the oxazines may be orthooxazine, metoxazine, and para-oxazine. A preferred residue of oxazines and their derivatives is metoxazine described by, for example, formula (v), hereinbelow (where each R 5 , R 6 , R 7 , and R 8 is independently selected from the group consisting of hydrogen atoms, alkyl groups containing one to 20 carbon atoms, and aryl groups containing six to 14 carbon atoms.) Preferred residues of oxazilone and its derivatives are described.by, for example, formula (vi) hereinbelow (where each R 9 and R 10 is independently selected from the group consisting of hydrogen atoms, alkyl groups containing one to 20 carbon atoms. and aryl groups containing six to 14 carbon atoms.) Preferred residues of oxazinone and its derivatives are described by, for example, formula (vii), hereinbelow (where each R 11 and R 12 is independently selected from the group consisting of hydrogen atoms, alkyl groups containing one to 20 carbon atoms, and aryl groups containing six to 14 carbon atoms.) The alkyl groups containing one to 20 carbon atoms referred to here may be straight-chain or branched. It is preferred that the alkyl groups contain one to three carbon atoms. Preferred examples of alkyl groups include methyl, ethyl, and propyl groups. Specific preferred examples of aryl groups containing six to 14 carbon atoms include phenyl groups, benzyl groups, tolyl groups, xylyl groups, and trityl groups. It is preferred that R 1 to R 4 in formula (iv), hereinabove, be selected from among hydrogen atoms, methyl groups, and ethyl groups. It is preferred that R 5 to R 8 in formula (v), hereinabove, be selected from among hydrogen atoms, methyl groups, and ethyl groups. It is preferred that R 9 and R 10 in formula (vi), hereinabove. be selected from among hydrogen atoms, methyl groups, and ethyl groups. It is preferred that R 11 and R 12 in formula (vii), hereinabove, be selected from among hydrogen atoms, methyl groups, and ethyl groups. Component (C) may contain any combination of one or more residues each from group (a) and group (b). Preferred examples of the compound designated component (C) include 2-ricinol-2-oxazoline maleate described by the following formula These compounds may be used singly or in combinations of two or more. 2-Ricinol-2-oxazoline maleate is preferred. Examples of methods for preparing component (C) can be found in European Patent Application No. 315,856 (1989), European Patent Application No. 394,854 (1990), and H. Moellard et al. Fat. Sci. Tchnol. 95 (1993) 2, p 51-57. Component (C) is used in amounts, by weight, of at least 0.01 parts, preferably at least 0.5 parts, and no more than 30 parts, preferably no more than 10 parts, per 100 parts total of (A) and (B). If (C) is used in too small amounts, it does not compatibilize (A) and (B); if it is used in too large amounts, mechanical and thermal properties are compromised. Examples of component (D), an organic peroxide with a half-life of 1 min at 100°C to 270°C, include diallylperoxydicarbonate, t -butyl peroxyallylcarbonate, 2,5-dimethyl-2,5-di(peroxybenzoyl)hexene-3, 2,5-dimethyl-2,5-di(peroxybenzoyl)hexyne-3, 2.5-dimethyl-2,5-di( t -butylperoxy)hexene-3, 2,5-dimethyl-2,5-di( t -butylperoxy)hexyne-3, t -butylperoxyisopropylene carbonate, 1,1,3,3-tetramethylperhydroxybutylene-3, 1,1,3,3-tetramethylperhydroxypentene-4, 2,2-bis( t -butylperoxy)octene-1, 2,2-bis( t -butylperoxy)heptene-1, methyl ethyl ketone peroxide, cyclohexanone peroxide, 2,2-bis( t -butylperoxy)octane, 2,2-bis( t -butylperoxy)butane, cumene hydroperoxide, di- t -butyl peroxide, dicumyl peroxide, t -butyl cumylperoxide, t -butyl peroxylaurate, and 1.3-bis( t -butylperoxyisopropyl)benzene. They may be used singly or in combinations of two or more. Preferably, component (D) is selected from among 1,3-bis( t -butylperoxyisopropyl)benzene, t -butyl cumylperoxide, dicumyl peroxide, and 2,5-dimethyl-2,5-d( t -butylperoxy)hexyne-3. It is preferred to blend component (D) in amounts, by weight, of at least 0.01 parts, preferably at least 0.05 parts, and no more than 3 parts, preferably no more than 1 part, per total 100 parts of the above-mentioned (A) and (B). If there is too little (D), (A) and (B) are not compatibilized, and if there is too much (D), the mechanical and thermal properties of the composition are compromised. Other conventional additives may be added, as desired, to the resin composition of the invention when the resin is mixed or molded, provided that the properties of the composition are not compromised. Examples include coloring agents (pigments and dies), reinforcing agents (glass fibers, carbon fibers, etc.), fillers (carbon black, silica, titanium oxide, etc.) agents for imparting heat resistance, antioxidants, antiweathering agents, lubricants, parting agents, crystal-nucleating agents, plasticizers, flame retardants, flowability enhancers, impact resistance enhancers, and antistatic agents. There are no particular restrictions on the manufacturing method for the resin composition of the invention; conventional methods are satisfactory. However, a melt-mix method is generally preferred. Small amounts of solvent may be used, but they are generally not necessary. Examples of equipment that may be used include Banbury mixers, rolls, and kneaders, which may be used in a batchwise or continuous manner. There are no particular restrictions on the mixing order for the components. Examples The present invention is described in further detail hereinbelow by means of working examples. The following compounds were used in the working and comparative examples. Component (A) PPE: Poly(2,6-dimethyl-1,4-phenylene) ether with an intrinsic viscosity of 0.46 dUg (chloroform. 30°C). made by G.E. Plastics Japan. Ltd. Component (B) Polyester: Poly(butylene terephthalate) (PBT), trade name VALOX 315, made by G.E. Plastics Japan. Ltd. Component (C) C-1: 2-Ricinol-2-oxazoline maleate (VEP8-5515, made by Henkle Shiramizu K.K.) C-2 (Used in the comparative examples): 2-Ricinol-2-oxazoline (VEP8513, made by Henkle Shiramizu K.K.) Component (D) P-14: 1,3-Bis( t -butylperoxyisopropyl)benzene with a half-life of 1 min at 183°C. Trade name Percadox 14, made by Kayaku Akuzo K.K. Working Examples 1-6 and Comparative Examples 1-4 The components in Table 1 were melt-kneaded for 5 min in the amounts shown (parts by weight), using a Brabender [sic] at a temperature setting of 260°C. Morphology was observed by scanning electron microscopy (SEM, magnification: 1,000 ×). The PPE particles dispersed in the composition were classified as being one of three sizes: fine (> 2 µm), intermediate (2-4 µm), and large (>4 µm). The results are shown in Table 1. Working Example 7 and Comparative Example 5 Pellets were made by extruding the components in Table 2 in the amounts shown (parts by weight) with a vented twin screw extruder at a temperature setting of 260°C and screw speed of 300 rpm. The pellets were injection-molded with an injection molder at a cylinder temperature of 260°C and mold temperature of 60°C and then subjected to the following battery of tests. The results are shown in Table 2. (1) Izod Impact Strength Izod impact strength was measured in accordance with ASTM D256, using unnotched 1/8-inch test specimens. (2) Tensile Strength and Tensile Elongation Measured in accordance with ASTM D638. using ASTM No. 4 dumbbells. (3) Flexural Strength and Flexural Modulus Measured in accordance with ASTM D790. using 1/4-inch thick test specimens. (4) Heat Deflection Temperature (HDT) Measured in accordance with ASTM D648, using 1/4-inch thick test specimens. (5) Melt Index (MI) Measured in accordance with ASTM D1238 at 250°C under a load of 10 kg. (6) Morphology Morphology was observed by scanning electron microscopy (SEM, magnification: 1,000 ×). The PPE particles dispersed in the composition were classified as being one of three sizes: fine (> 2 µm), intermediate (2-4 µm), and large (> 4 µm). Working Example 7 Comparative Example 5 Components (Parts by Weight) (A) PPE 30 30 (B) PBT 70 70 (C) C-1 2 0 (D) P-14 0.2 0 Evaluative Tests Izod impact strength (Kg·cm/cm) 39 15 Tensile strength (Kg/cm 2 ) 465 340 Tensile elongation (%) 5 4 Flexural strength (Kg/cm 2 ) 870 580 Flexural modulus (Kg/cm 2 ) 24,800 24,600 Heat deflection temperature (°C) 174 187 MI (g/10min) 35 24 Morphology Particle size of dispersed PPE Fine Large Scanning electron microscopy revealed extremely good compatibility between the PPE and PBT in moldings of the composition of the invention, and the moldings therefore have excellent mechanical strength. Brief Description of the Figures Figure 1 A scanning electron micrograph of the particle structure on a cross-section of a molding obtained in Working Example 7. Figure 2 A scanning electron micrograph of the particle structure on a cross-section of a molding obtained in Comparative Example 5.

Claims: A resin composition comprising: (A) 5 to 90 percent by weight of polyphenylene ether resin; (B) 95 to 10 percent by weight of thermoplastic polyester resin, the composition also containing, per total 100 parts by weight of (A) and (B); (C) 0.01 to 30 parts by weight of a compound having (a) a residue of a compound selected from maleic acid esters or their derivatives represented by formula (i), where each R a and R b is independently selected from the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms, and R c is selected from the group consisting of alkyl groups containing 1 to 20 carbon atoms and aryl groups containing 6 to 14 carbon atoms; maleimide and its derivatives represented by formula (ii), where each R d and R e is independently selected from the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms; maleinamic acid esters and their derivatives represented by formula (iii), where each R f , R g and R i is independently selected from the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms, and R h is selected from among the group consisting of alkyl groups containing 1 to 20 carbon atoms and aryl groups containing 6 to 14 carbon atoms; and (b) a residue of a compound selected from oxazoline and its derivatives represented by formula (iv), where each R 1 , R 2 , R 3 and R 4 is independently selected from among the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms; oazines and their derivatives represented by formula (v), where each R 5 , R 6 , R 7 and R 8 is independently selected from the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms; oxazilone and its derivatives represented by formula (vi), where each R 9 and R 10 is independently selected from the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms; oxazinone and its derivatives represented by formula (vii), where each R 11 and R 12 is independently selected from the group consisting of hydrogen atoms, alkyl groups containing 1 to 20 carbon atoms, and aryl groups containing 6 to 14 carbon atoms; and (D) 0.01 to 3 parts by weight of an organic peroxide which has a half life of one minute at a temperature within the range 100 to 270°C. A resin composition according to claim 1, wherein component (C) is 2-ricinol-2-oxazoline maleate. A resin composition according to claim 1 or claim 2, wherein component (D) is selected from 1,3-bis(t-butylperoxyisopropyl)benzene, t-butyl cumylperoxide, dicumyl peroxide and 2,5-dimethyl-2,5-di( t -butylperoxy)hexyne-3.

Inventors: ISHIDA HIROMI, OSHIMA AKIFUMI, SHINOHARA TOSHIHIKO, ISHIDA, HIROMI, OSHIMA, AKIFUMI, SHINOHARA, TOSHIHIKO
Applicants: GEN ELECTRIC, GENERAL ELECTRIC COMPANY
Application year: 1996
Main classification: C08L67
IPC codes: C08K5, C08L71, C08L67