Monovinyl aromatic block copolymer compositions for use in rotational moulding

Abstract: Block copolymer containing compositions, suitable for use in rotational moulding and comprising at least: (a) 100 parts by weight of a block copolymer containing at least two predominantly poly(monovinyl aromatic) blocks and at least one predominantly poly(conjugated diene) block, the poly(conjugated diene) block of which optionally being selectively hydrogenated (b) from 10 to 160 parts by weight poly(ethylene) or poly(propylene) or or copolymers of predominantly ethylene or propylene and minor amounts of other α-olefin comonomers, or poly(monovinylaromatic) polymers. (c) from 20 to 100 parts by weight by weight of a plasticizer.

Description: The present invention is relating to monovinylaromatic block copolymer containing compositions and microgranules and powders derived therefrom, to be used in rotational moulding and similar processes. More in particular the present invention is relating to compositions, comprising block copolymers of at least one monovinyl aromatic monomer such as styrene, alpha-methylstyrene, p-vinyl toluene, m-vinyl toluene, o-vinyl toluene, 4-ethylstyrene, 3-ethylstyrene, 2-ethylstyrene, 4-tert-butylstyrene; 2,4-dimethylstyrene or mixtures thereof, and at least one conjugated diene, such as 1,3-butadiene, isoprene, 2-ethyl-1,3-butadiene 2,3-dimethyl-1,3-butadiene and 1,3-pentadiene or mixtures thereof, and to microgranules and powders derived therefrom. Rotational moulding processes, using as starting materials elastomer containing compositions, were known from e.g. US patents nos. 5,308,700; 4,267,080 and 3,865,284. US patent no. 3,865,284 actually disclosed a dress form comprising a layered wall having the external form of a human torso and having an outer cellular layer and integral thereto an inner cellular layer; said outer cellular layer having an expansion ratio of from 2 to 20 and comprising a thermoplastic polymeric material, having an elastic modulus of 500 to 10 kg/cm 2 and preferably selected from the group consisting of ethylene-vinyl acetate copolymers, ethylene-acrylate copolymers and ethylene methacrylate copolymers; and (b) said inner layer comprising a thermoplastic polymeric material having a Young's modulus of 2,000 to 50,000 kg/cm 2 . Said dress form was mentioned to have been prepared by rotational moulding, using an expandable thermoplastic resin powder for the outer layer, having a preferred size from 70 to 400 µ and containing a blowing agent, having a higher decomposition temperature than the melting point or softening point of the polymeric material; and expandable thermoplastic polymeric beads or pellets, containing a blowing agent having a higher decomposition temperature than the melting point or softening point of said polymeric material. A mixture of said powder and beads or pellets was charged into a mould and the mould was rotated in an atmosphere heated at a temperature higher than the decomposition temperatures of the blowing agents. The heating caused that the powder, having a smaller particle size melts into a molten layer on the inner wall of the mould, and the bead or pellet, having a relatively larger particle size, melts and adheres to the inner surface of the molten layer of the powder to form an inner molten layer. Thereafter foaming took place in both molten layers by decomposition of the blowing agents. From US patent no. 4,267,080 it was known to produce articles of polymers of ethylene, having incorporated therein (1) 5-50 parts by weight of a rubber and/or an elastomer based on 100 parts by weight of the ethylene polymers, and in particular styrene-butadiene block copolymer elastomer, (2) a crosslinking agent selected from bis(tert-alkylperoxy)alkane or bis(tert alkylperoxy) benzene, and (3) 0.5-5 times by weight the amount of crosslinking agent specified under (2) of at least one crosslinking aid selected from 1,2-polybutadiene, triallyl cyanurate and triallyl isocyanurate; by rotational moulding. Such moulded articles were indicated to show good release characteristics as well as high impact strength and attractive surface lustre. The amount of the elastomer was prescribed to be in the range of from 5 to 50 parts by weight and preferably from 10 to 30 parts by weight per 100 parts by weight of the ethylene polymer. US patent No. 5,308,700 disclosed a thermoplastic elastomer powder for powder moulding, comprising a partially crosslinked type elastomer composition, from comprising a mixture of an ethylene-α-olefin copolymer rubber and a polyolefin resin, dynamically crosslinked in the presence of a crosslinking agent, wherein said elastomer composition has a complex dynamic viscosity η*(1) as measured at frequency of 1 radian/sec in dynamic viscoelasticity measurement at 250°C, of 1.5 x 10 5 poise or less, a Newtonian viscosity index n calculated from the following equation by using the complex dynamic viscosity η*(1) at a frequency of 1 radian/sec and the complex dynamic viscosity η* (100) at a frequency of 100 radian/sec of 0.67 or less and a hardness (shore D) of 45 or less: n = { log η*(1) - log η*(100)}/2 As ethylene-α-olefin copolymer rubber preferably ethylene-propylene-non conjugated diene copolymer rubber was used, while the polyolefin resin component of the powder was polypropylene or a copolymer of propylene and an α-olefin. No reference was made to styrenic block copolymers at all. The hereinbefore discussed publications have all in common, that a thermoplastic material in the form of very fine powder having a particle size of 300 µm is used for rotational moulding, wherein a fused thermoplastic material flows and spreads to form a fused thermoplastic layer on the inner surface of a mould. Moreover in order to reach a thermoplastic material of enhanced flow characteristics low molecular weight materials had to be used which provided rotational moulded articles being poor in impact strength and environmental stress cracking resistance, and thus in service life. It was generally known that particle sizes of starting powder for such rotational moulding processes, derived from low melt viscosity styrenic block copolymer containing compositions, of lower than 400 µm could be obtained by cryogenic milling at temperatures of -40°C or lower and preferably -70°C or lower, and that a dusting agent had to be added to said powder in order to reach powder compositions of a sufficiently good flow behaviour under a low shear rate and low pressure, i.e. powder compositions which do not block or cake by uncontrolled reagglomeration during storage and processing. Rotational moulding can be regarded as one of the oldest and simplest thermoplastic processing techniques in the polymer industry. Such rotational moulding process normally consists of three steps and distinguishes a loading/unloading station, a heating station and a cooling station. A cold mould was up to now filled with a measured weight of a thermoplastic powder (station 1). Then he mould was moved into an oven (station 2) and started to rotate biaxially at a low speed (from 2-20 rpm). The powder in contact with the hot inner surface of the mould fused and adhered to the mould surface, finally producing an even coating over the inside of the mould. After fusion had been completed the mould was moved into a cooling chamber (station 3) to be cooled by air or water jet. Subsequently the mould was returned to its original position (station 1) where the article was removed as soon as its shape was sufficiently stable. It was an object of the present invention to improve the properties of products of rotational moulding and similar process, while a decrease of the product price is aimed at too, due to lower manufacturing costs by using microgranules instead of powder and a lower cost of starting composition. As a result of extensive research and experimentation styrenic block copolymer compositions which meet the processing requirements as specified hereinbefore, surprisingly were found. Accordingly, the present invention is relating to monovinylaromatic block copolymer containing compositions which are to be used in rotational moulding and consisting essentially of: a) 100 parts by weight of a main block copolymer containing at least two predominantly poly(monovinyl aromatic) blocks and at least one predominantly poly(conjugated diene) block, optionally mixed with a minor amount of terminated diblock copolymer of the same monomers, from which the main block copolymer was derived by coupling, and wherein the poly(conjugated diene) block of which optionally being selectively hydrogenated b)from 5 to 160 parts by weight of poly(styrene), poly(alpha-methylstyrene), copolymer of styrene and alpha-methylstyrene, optionally toughened with elastomer, or poly(ethylene) or poly(propylene) or copolymers of ethylene or propylene and other alpha-olefin comonomers, having a melt index (ASTM D 1238) in the range of from 5 to 75 and a density in the range of from 0.91 to 0.95 g/cm 3 c) from 20 to 100 parts by weight of a plasticizer, which block copolymer-containing compositions may contain in addition to the components (a) to (c) a minor amount of auxiliaries comprising blowing agents, stabilisers, antistatic agents, mould release agents and/or fillers, wherein the block copolymer-containing compositions show a melt viscosity at low shear rate (≤ 0.2 sec -1 ) of a value lower than 2000 Pa.s at 190 degrees C. The block copolymers to be used as component (a) may be linear triblock copolymers or multiarmed or star shaped symmetrical or unsymetrical block copolymers as main ingredient. It will be appreciated that these main block copolymers may be optionally mixed with minor amounts of diblock copolymers (<20 wt%) relative to the block copolymer weight, which served as initially prepared, intermediate living block copolymers, which were coupled into the triblock copolymers or multiarmed or star shaped block copolymers. Preferably block copolymers are used as component (a), containing blocks predominantly derived from styrene and predominantly derived from butadiene and/or isoprene respectively. The poly(conjugated diene) blocks may optionally have been hydrogenated up to a substantial degree, i.e. more than 80% of the original ethylenic unsaturation has been hydrogenated. According to a preferred embodiment of the present invention, the poly(conjugated diene) blocks have been hydrogenated up to a residual ethylenic unsaturation (RU) of at most 10% and more preferably less than 5%. With the term "predominantly derived from" is meant that the main monomer of the respective individual blocks optionally may be mixed with minor amounts of another comonomer and more in particular with minor amounts of the main monomer of the other blocks. Examples of the mono vinyl aromatic monomers may be selected from styrene, ∝-methylstyrene, p-methylstyrene, m-methylstyrene, o-methylstyrene, p-tert-butylstyrene, dimethylstyrene, vinylnaphthalene and the like and mixtures thereof and conjugated diene monomers may be selected from butadiene, isoprene, 2-ethyl-1,3 butadiene 2,3 dimethyl-1,3-butadiene 1,3-pentadiene, 2,4-hexadiene, 3-ethyl 1,3-pentadiene and the like, and mixtures thereof. Of these monomers styrene and butadiene or isoprene or mixtures thereof are preferred. Most preferably block copolymers have been found to be used, which only contain substantially pure poly(styrene) blocks and substantially pure poly(butadiene) or poly(isoprene) blocks. Examples of such block copolymers which can be suitably used are KRATON D and G block copolymers (KRATON is a trade mark) and more preferably KRATON D 1118, KRATON D 1102, KRATON D 4271, KRATON G 1652, KRATON G 1726 block copolymers are used. It will be appreciated that also mixtures of hydrogenated and non-hydrogenated or partially hydrogenated block copolymers can be used as starting ingredients for the block copolymer composition, in addition to individual grades of hydrogenated block copolymers or non-hydrogenated block copolymers or partially hydrogenated block copolymers. However, the use of block copolymers, having poly(conjugated diene) blocks which have been substantially hydrogenated (RU ≤5%) is preferred. The terminal poly(monovinyl aromatic) blocks in the optionally selectively hydrogenated block copolymers have usually apparent molecular weights, ranging from 3,000 to 100,000 and preferably from 5,000 to 20,000, and the internal, optionally selectively hydrogenated poly(conjugated diene) blocks usually have apparent molecular weights in the range of from 10,000 to 300,000 and preferably from 30,000 to 100,000. The initially prepared poly(conjugated diene) blocks usually contain from 5 to 50 mol%, relative to the conjugated diene molecules, of vinyl groups originating from 1,2 polymerization and more preferably from 5 to 15% in case of use of non-hydrogenated block copolymers and from 25-40% in case of use substantially completely hydrogenated block copolymers. The complete block copolymer to be used according to the present invention, is normally containing bound monovinyl aromatic in an amount of from 20 to 60% by weight and preferably from 25 to 45% by weight. The apparent molecular weight of the total block copolymer will normally be in the range of from 20,000 to 350,000 and preferably in the range of from 40,000 to 200,000 and more preferably in the range from 40,000 to 150,000. The components (b) have a melt index (measured according to ASTM D 1238) in the range of from 5 to 75 and preferably from 20 to 75, and a density in the range of from 0.91 to 0.95 g/cm 3 . A preferred poly(monovinylaromatic) resin is poly(styrene) such as TPS476L from BASF and a preferred poly(ethylene) is linear low density poly(ethylene). A preferred copolymer of styrene and α-methylstyrene is Hercures A150. As component (c) various plasticizing oils are useful in the compositions to be used according to the present invention. Plasticizing oils which have been found useful include petroleum derived oils, olefin oligomers and low molecular weight polymers, as well as vegetable and animal oil and their derivatives. The petroleum derived oils which may be employed are relatively high boiling materials, containing only a minor proportion of aromatic hydrocarbons preferably less than 20 percent and more preferably less than 15 percent by weight of the oil most preferably the oil may be totally non-aromatic. The oligomers may be polypropylene, polybutenes, hydrogenated polyisoprene, hydrogenated polybutadiene, polypiperylene and copolymers of piperylene and isoprene, having average molecular weights between 350 and 10,000. Vegetable and animal oils include glyceryl esters of the usual fatty acids and polymerization products thereof. Examples of a preferred paraffinic oil are PRIMOL 352 (PRIMOL is a trade mark) CATENEX SM 925, CATENEX SM 956 (CATENEX is trade mark) and the NAPVIS and HYVIS (trade marks) polyolefins, having a molecular weight in the range of from 500 to 6,000. The block copolymer containing compositions may contain in addition to the components (a) - (c) minor amounts of one or more usual auxiliaries, such as blowing agents, stabilisers, (eg. Irganox UV stabilisers), antistatic agents, mould release agents, fillers such as calcium carbonate (Durcal). The hereinbefore specified styrenic block copolymer containing compositions can be used in the form of particles, having an average size in the range of from 200 to 1100µm. The average particle size D m is calculated according to the equation D m = Σ (Pi x Di/100 wherein pi = the weight percentage of the material retained on sieve i. Di = average particle size in µm of material on sieve i. Preferably the average particle sizes are in the range of from 200 µm to 800µm and more preferably from 300 to 700µm. It will be appreciated that a preferred embodiment of the present invention is formed by microgranules, having an average particle size of from 300 to 1100µm, and preferably from 300 to 900µm and more preferably from 500-700µm and derived from the hereinbefore specified block copolymer compositions. Another aspect of the present invention is formed by a process for the manufacture of microgranules, having an average particle size of from 200 to 1100µm. Said process comprises feeding the respective ingredients at the same or different places into an extruder, extrusion of the homogeneous melt through a die with micro holes and subsequent pelletising resulting in microgranules with an hereinbefore specified average particle size. Such a process was known in principle from e.g. Plastics World, November 1994, page 20, "Micropellets:Little things means a lot", J.J. Callari. It will be appreciated that a surprising advantageous aspect of the present invention is formed by the found enablement to use said microgranules for fusing them at very low or zero shear by applying heat, allowing the use of processing techniques such as rotational moulding, to convert the microgranules into elastomeric layers with a broad range of properties instead of the conventional fine powder compositions which are significantly more expensive due to higher manufacturing costs. Another aspect of the present invention is formed by a specific process for the manufacture of formed articles by rotational moulding of the hereinbefore specified particles of the block copolymer composition. Specific oven temperatures which provided formed articles of an acceptable quality are in the range of from 260 to 300°C and preferably in the range of from 260 to 280°C, while the maximum internal air temperature is in the range of from 170 to 225°C and preferably from 190°C to 215°C, using an aluminium mould thickness of from 5 to 10 mm, a moulded part thickness of from 0.5 to 3 mm while the mould may be internally coated to enable the easy release of the product ROTOSPEED or CACCIA (trademarks) equipment can be suitably applied. The invention is further illustrated by the following examples. Example 1-3 Microgranules were prepared as described hereafter, from the following listed compositions, having the specified properties: 1 2 3 KRATON G-1652 70 100 100 KRATON G-1726 30 - - CATENEX SM925 50 80 70 NOVOLEN 1100 UCX - - 50 TPS 476L - 20 - HERCULES A 150 20 20 110 DURCAL 5 100 70 50 IRGANOX 1010 0.2 1 1 Melt viscosity, Pa.s 1600 690 1300 190°C, 0.2 sec -1 Drop point °C 225 216 233 MFR 190°C/2.16kg g/10' 40 89 45 Onset melttemp. °C 220 180 195 Hardness, 0 sec, ShA 61 49 74 30 sec, ShA 58 46 70 Preblends were prepared in a PAPENMEIER (trademark) dry blender from the ingredients mentioned above. The blends were extruded through a die with circular holes having a diameter in the range of from 360 to 500 µm in an underwater pelletiser, processing parameters which have been listed in Table 2, and providing microgranules, having a particle size distribution as listed in Table 3. Extruder settings APV twin screw extruder, 65 mm Barrel temperatures °C 50-40 Die temperature °C 200 Die pressure bar 48-79 Throughput kg/h 100-150 Extruder screw speed rpm 500 Granulator shaft speed rpm 3600 Die set-up 240 x 0.5 mm holes Granulator water temperature °C 55 - 65 Number of granulating knives 6 Micropellets paricle size distribution ASTM D 1921 91.263 %w > 2000 µm 0.5 > 1180 µm 30.7 > 710 µm 68.8 > 300 µm 0 The obtained microgranule compositions were subjected to rotational moulding processing, the details of which have been listed in Tables 4 and 5. Equipment Characteristics ROTOSPEED CACCIA Oven temperature (°C) 270 270 Fan Speed 3000 Cooling Air only air only mould Bladder Test mould Shotweight (g) 400/300 1000 Moulding conditions Composition Example 1 Composition Example 2 oven temperature 270°C 270° mould thickness 8-10 mm alum 8-10 mm alum part thickness ≈ 2.5 mm ≈ 2.5 mm maximum internal air 215-220°C 205-210°C temperature From these particles, formed articles could be prepared in several well rounded moulds.

Claims: Block copolymer-containing compositions, suitable for use in rotational moulding and consisting essentially of: a)100 parts by weight of a main block copolymer containing at least two predominantly poly(monovinyl aromatic) blocks and at least one predominantly poly(conjugated diene) block, optionally mixed with a minor amount of terminated diblock copolymer of the same monomers, from which the main block copolymer was derived by coupling, and wherein the poly(conjugated diene) block of which optionally being selectively hydrogenated b) from 5 to 160 parts by weight of poly(styrene), poly(alpha-methylstyrene), copolymer of styrene and alpha-methylstyrene, optionally toughened with elastomer, or poly(ethylene) or poly(propylene) or copolymers of ethylene or propylene and other alpha-olefin comonomers, having a melt index (ASTM D 1238) in the range of from 5 to 75 and a density in the range of from 0,91 to 0.95 g/cm 3 c) from 20 to 100 parts by weight of a plasticizer, which block copolymer-containing compositions may contain in addition to the components (a) to (c) a minor amount of auxiliaries comprising blowing agents, stabilisers, antistatic agents, mould release agents and/or fillers, wherein the block copolymer-containing compositions show a melt viscosity at low shear rate (≤ 0.2 sec -1 ) of a value lower than 2000 Pa.s at 190 degrees C. Block copolymer containing composition according to claim 1 , characterised in that the block copolymer is derived from styrene and butadiene and/or isoprene. Block copolymer-containing composition according to claims 1-2, characterised in that the poly(conjugated diene) blocks have been hydrogenated up to a residual unsaturation of less than 5%. Block copolymer containing compositions according to claims 1-3, characterised in that the poly(monovinyl aromatic) blocks have apparent molecular weights in the range of from 5,000 to 20,000 and that the poly(conjugated diene) blocks have apparent molecular weights in the range of from 30,000 to 100,000. Block copolymer containing compositions according to claims 1-4, characterised in that they are in the form of particles having an average size in the range of from 200µm to 1100µm. Use of block copolymer compositions according to claims 1-5, to produce formed articles by rotational moulding. Use of block copolymer compositions according to claim 6, characterised that a maximum internal air temperature is used in the range of from 170 to 225°C. Process for the preparation of microgranules derived from the block copolymer composition according to claims 1-5 having an average particle size in the range of from 200 to 1100µm, comprising feeding the respective ingredients into an extruder, extruding the homogeneous melt through a die with microholes and subsequent pelletising.

Inventors: MAES CAROLINE RITA NICOLE, MIGCHELS PETER, MAES, CAROLINE RITA NICOLE, MIGCHELS, PETER
Applicants: KRATON POLYMERS RES BV, KRATON POLYMERS RESEARCH B.V.
Application year: 1996
Main classification: C08L53
IPC codes: B29B9, C08L51, C08L53, C08J3, C08L25, B29C41, C08L23