Plastic mirrors having enhanced thermal stability

Abstract: A mirror having improved resistance to heat distortion and loss of dimensional stability when exposed to heat radiation. The mirror has a substrate of glass or plastic having front and back surfaces which can be of similar or different shape, and is coated with similar or dissimilar low-emissivity reflective layers on both surfaces. Radiation is reflected by the back surface (away from the mirror) thereby reducing the amount of energy which is absorbed at the back surface of the mirror. This equalizes the temperature through the mirror and reduces thermally-induced warping of the mirror.

Description: Background of the Invention The present invention relates to the manufacture of mirrors, including inexpensive, lightweight mirrors having molded plastic substrates, and more particularly to increasing the thermal stability and resistance to distortion of such mirrors in the pressure at thermal variations and exposure to thermal radiation. Mirrors utilizing this invention can be used at any wavelength in particular for infrared application between 7 and 14 microns. Precision mirrors require a specified mirror shape, such as flat, spherical or other contoured shape, to be maintained to a high degree of accuracy. The degree of precision required varies depending on the application. For the present mirrors, accuracies of 0.1 to 20 wavelengths of HeNe Light (λ =.6328 microns) are typical. In order to beneficially use the energy incident on a mirror it must be reflected to the greatest degree practical. A mirror coating is used for this purpose. Requirements for reflectance typically vary from 85 to 99% depending upon the application and wavelength region. These coatings, by definition, have a low emissivity since emissivity can be no greater than 1-reflectivity. Since absorption and emissivity are related, a low reflectivity (no coating) surface would have a high emissivity and therefore be highly absorbing of incident energy. The reduction of this absorption provides the basis for the present invention. Absorbed radiative energy on the back (non mirror) side can generate thermal gradients caused by non-uniform heating resulting from the mismatch in energy being absorbed by the high emissivity (uncoated) back surface of the mirror substrate, of glass or molded plastic, and the low emissivity reflective coating on the front surface of the mirror substrate. Non-uniform heating can result in a thermal gradient which can warp the mirror substrate or cause a loss of dimensional stability, and thereby distort the mirror figure and reflected light. This effect can occur with any mirror substrate, including glass, but is particularly pronounced with molded plastic mirror substrates because they are particularly sensitive to thermal problems associated with a low thermal conductivity and a high temperature coefficient of expansion (CTE) as is inherent in most plastics. Therefore while molded plastic mirror substrates provide low cost, lightweight alternatives to glass mirror substrates, they are much more susceptible to warpage and distortion caused by thermal gradients and therefore have been unsatisfactory for use in precision mirrors, particularly those used in heat build-up or radiant energy conditions. JP-57096301 discloses a reflection mirror for an optical system comprising a substrate having a front and back surface upon which metallic film, consisting of aluminium, is vapor deposited. Summary of the Invention The present invention relates to the discovery that the application of a low emissivity reflective coating to the back surface of a mirror substrate, to compliment the primary reflective/low emissivity coating on the front (mirror) side of the mirror substrate of molded plastic including a filler material, provides a mirror which is more thermallystable in the presence of a radiative heat load, as claimed in claim 1 hereinafter. The back coating, which can be of the same or different reflective composition as applied to form the primary reflective mirror coating on the front surface of the substrate, typically reflects between 85.5% to 98.5% of the radiation incident on the surface. Since this energy would be largely absorbed by the back surface, heating of the back surface would result. Reflectance of this energy due to the coating reduces the heating of the back surface, and prevents the normal non-uniform heating of the substrate which normally occurs due to the mismatch in energy being absorbed by a high emissivity uncoated back surface of the substrate and the low emissivity surface on the coated mirror side. Such mismatch normally causes non-uniform heating of the front and back surfaces of the substrate, producing a thermal gradient which can warp or distort the substrate and the precision of the mirror properties, in the case of both contoured and flat mirrors. Detailed Description Precision mirrors are used as components of expensive scientific measuring and observation equipment and in low cost optical systems for commercial use, and their accuracy is essential to the results provided by such equipment. The precise shape of such mirrors, whether flat, convex or concave, can be produced from substrates of molded plastic composition but such precision is frustrated if the substrate warps or distorts during use due to poor thermal stability properties of the material. The major thermal property for the present mirror substrates injection molded from plastic compositions is their coefficient of thermal expansion (CTE). A low coefficient of expansion results in an optical assembly that is better able to maintain its performance over a wide temperature range. Based on the desire to achieve low thermal expansion, the coefficient of expansion for the plastic substrate including a filler material is in the range of 0.22 to 0.83 x 10 -5 cm/cm°C (0.4 to 1.5 x 10 -5 in/in°F). Thermal conductivity also plays an important role in the thermal stability of the substrate material. The larger the coefficient of thermal conductivity the more uniform the temperature of the substrate will be, and therefore, the more uniform the growth. In theory, uniform growth of the substrate due to temperature changes does not cause a reduction in optical performance (with the exception of a corresponding change in the focal length and an inverse change to the field of view). In order to achieve uniform growth due to thermal effects, the entire optical system preferably is made out of the same material. Attention to thermal conductivity is an important issue because plastics are very poor at conducting heat. Generally, plastic materials have coefficients of thermal conductivity between 15 and 100 times lower than aluminum. The need for a low coefficient of expansion is made all the more important by the low thermal conductivity of the plastic materials. A desired thermal conductivity of the mirrors may be achieved with a metalized exterior coating or by using additives to the material. Such additives are added to the plastic composition as filler material prior to molding. Filler materials are primarily used to add strength to molded plastic substrates. In additional, the coefficient of thermal expansion is generally reduced by the addition of filler materials. Filler materials are also used to enhance a number of other properties, such as resistance to flammability, lubricity, electrical conductivity, and flexibility. Carbon and glass fiber are two of the most common filler materials. Other filler materials such as graphite, cellulose, minerals, and metals are also used, but glass beads are preferred for smooth surface properties. The filler material is generally determinative of the molding process that is used, as well as the rate at which the material can be injected into a mold. The present invention improves the thermal stability of mirrors by balancing or approximating the radiationemissivity properties of the front and back surfaces of the mirror to prevent or substantially reduce any temperature differential between the front and back surfaces, such differential or temperature gradient can cause the mirror substrate to warp or undergo slight changes in shape which destroy the precision of the mirror. While glass substrates are susceptible to such changes when the front and back surfaces thereof are heated to different temperatures, molded clear polymeric substrates, such as of acrylic, polycarbonate, polystyrene, polyetherimide, polyphenylene sulfide, or other plastic molding compositions are more susceptible to such changes because plastic materials generally have a much lower thermal conductivity and a higher coefficient of thermal expansion (CTE) than glass. Thus, heat absorbed at the back surface of a plastic substrate remains localized to cause thermal expansion of the back surface relative to the front surface which can produce a change in the shape of the front (mirror) surface. The low emissivity coating applied to the back surface of the present mirror substrates can be identical in composition to the low emissivity reflective coating applied to the front surface or mirror side, and can be applied in identical manner and simultaneously if desired. Alternatively, the coating can be a totally different lower cost coating if desired. The typical preferred low emissivity reflective coatings for both the back and front surfaces of the present mirror substrates are conventional metallic mirror coatings. There are many suitable coating materials such as of aluminum and chromium, with additional special enhancement layers or protective coating layers. Metallic coatings have high thermal conductivity and equalize the heat uniformity over the entire coated surface. Also conventional thin metallic mirror coatings, as applied by vapor deposition processes, have high reflectivity properties so as to reflect away from about 85.0% to 98.5% of radiation directed thereagainst, including infrared heat energy, and thus permit only from about 1.5% to 15% of radiation directed thereagainst, including heat energy, to pass through the reflective surface and be absorbed to heat the back surface of the substrate. The low emissivity coatings preferably are applied simultaneously to both surfaces of the glass or plastic substrate by supporting the substrate within a vacuum deposition chamber and exposing both surfaces to vapors of a metal, such as aluminum. Alternatively the metal coatings may be applied by other conventional metallization processes such as sputtering, dipping, spraying or other such processes. It is not essential that the low emissivity coatings applied to the front and back surfaces of the substrate be of identical composition, or that they have identical low emissivity properties, although such identity is preferable for producing the greatest temperature stability. The rear surface coating may be of less expensive composition and may be applied by less expensive processes than the front mirror coating, for economy reasons, so long as it provides substantially lower emissivity than the absence of a back coating. As stated, maximum heat stabilization is obtained if the emissivity of the back coating matches that of the front coating exactly, but any back coating which reduces the emissivity of the rear surface of the substrate will increase the heat stability of the mirror, particularly in the case of plastic substrates with low thermal conductivity and high thermal expansion properties. It should be understood that the foregoing description is only illustrative of the invention. Various alternatives and modifications can be devised by those skilled in the art without departing from the invention. Accordingly, the present invention is intended to embrace all such alternatives, modifications and variances which fall within the scope of the appended claims.

Claims: A mirror operable to reflect incident radiation, said mirror having a substrate of a first material having a front and a back surface, and a high reflectance low emissivity layer overlying said front surface for providing a mirror surface, said mirror further comprising a high reflectance low emissivity layer covering the back surface of the substrate to reduce or prevent warpage of the substrate, said layer covering the back surface of the substrate being made from a material different to said first material; and said back surface layer reflecting in the range of 85.5% to 98.5% of said incident radiation; characterised in that : said substrate is molded from a polymeric composition, includes a filler material which reduces the coefficient of thermal expansion CTE of the substrate, and has a coefficient of expansion in the range of 0.22 to 0.83 x 10 -5 cm/cm°C (0.4 to 1.5 x 10 -5 inch/inch °F). The mirror according to claim 1, said mirror having improved resistance to the loss of dimensional stability in the presence of a thermal heat load, wherein said layer covering the back surface of the substrate is for reducing the amount of heat energy which is absorbed by the back of the substrate, and wherein, said layers covering the front and back surfaces of the substrate are of the same composition, and the front surface layer reflects in the range of 85.5% to 98.5% of said incident radiation. A mirror according to claim 2, in which the reflective layers applied to both the front surface and the rear surface of the substrate have similar low emissivity properties. A mirror according to any preceding claim, in which said reflective layers comprise vapor-deposited metallic layers. A mirror according to any preceding claim, in which said substrate made of a first material having a front and a back surface comprises an acrylic, polycarbonate, styrene, polyetheirimide or polyphenylene sulfide.

Inventors: TAYLOR CHRISTOPHER D, TAYLOR, CHRISTOPHER D.
Applicants: RAYTHEON CO, RAYTHEON COMPANY
Application year: 1996
Main classification: G02B5
IPC codes: B29D11, G02B7, B29K25, G02B5, B29K69