NONAQUEOUS LIQUID ELECTROLYTE SECONDARY CELL

Abstract: A negative electrode material for a secondary cell for anon-aqueous liquid electrolyte for realizing a high charging/discharging capacity and a high discharging efficiency, a method for producing such material and a non-aqueous liquid electrolyte secondary cell employing such material. The negative electrode material contains at least one carbonaceous material selected from the group consisting of coffee beans, tea leaves, cane sugar, corns, fruits, straws of cereals and husks of cereals, a carbonaceous material derived from a plant-origin high molecular material containing a sum total of 0.2 to 20 wt% of metal elements, phosphorus and sulphur calculated as elements or a carbonaceous material having a diffraction peak between 30° and 32° of the 2 diffraction angle in the X-ray (CuKα) powder diffraction pattern. For producing the negative electrode material, at least one carbonaceous material selected from the group consisting of coffee beans, tea leaves, cane sugar, corns, fruits, straws of cereals and husks of cereals, or crystalline or fibrous cellulose admixed with at least one of metal elements, phosphorus or sulphur, is sintered for carbonization. The negative electrode material is used for a non-aqueous liquid electrolyte secondary cell having a positive electrode formed of a lithium compound oxide and a negative electrode formed of a carbonaceous negative electrode material capable of doping and dedoping lithium ions as an active negative electrode material.

Description: This invention relates to a non-aqueous liquid electrolyte secondary cell. More particularly, it relates to a non-aqueous liquid electrolyte secondary call having a negative electrode material of a carbonaceous material capable of doping and dedoping lithium ions. With recent progress in electronics,a small-sized portable electronic equipment, such as a camera-integrated VTR, portable telephone or a lap-top computer, has been developed, and a strong demand has been raised for development of a small-sized and lightweight secondary cell with high energy density as a portable power source used for the equipment. Of the secondary cells, satisfying this demand, a. non-aqueous liquid electrolyte secondary cell of a high energy density, which is capable of generating a theoretically high voltage and which employs light metals, such as lithium, sodium or aluminum as an active material for the negative electrode, is most promising. In particular, the non-aqueous liquid electrolyte secondary cell in which lithium ion charging/discharging is done via a non-aqueous liquid electrolyte, is thought to be able to develop high output and high energy density as compared to the aqueous solution based liquid electrolyte secondary cell, such as nickel/cadmium cell or a lead storage cell. For this reason, investigations in this type of the non-aqueous liquid electrolyte secondary cell are proceeding briskly. If, in such non-aqueous liquid electrolyte secondary cell, light metals, such as lithium metal, are simply used as they are as the negative electrode material, lithium metals tend to be precipitated in a dendritic form in the negative electrode during charging. Since the current density becomes exceedingly high at the distal end of the dendrite, the cycle life is shortened due to decomposition of the liquid electrolyte. If the dendrite is grown excessively, internal shorting in the cell is likely to be produced. For assuring the operating time of the small-sized electronic equipment and the service life of power source packages, it has been strongly desired to develop a negative electrode material capable of realizing a high energy density cell. With this in view, for prohibiting precipitation of, for example, dendritic metals, such as metal lithium, for improving cyclic charging/discharging characteristics of the cell, it has been proposed to use a carbonaceous material capable of doping and dedoping lithium ions as the active materials for the negative electrode as a material for a negative electrode for a non-aqueous liquid electrolyte secondary cell (JP Patent Kokai Publication JP-A-62-90863). It is believed that, theoretically, lithium ions are electrochemically doped and dedoped in an interlayer space of the graphite-like layered structure of the carbonaceous material at a rate of one lithium atom per six carbon atoms. For such carbonaceous materials, cokes (such as pitch coke, needle coke or petroleum coke) or sintered organic high molecular compounds, such as furan resins or natural high molecular materials sintered and carbonized at a suitable temperature, as disclosed in JP-Patent Kokai Publication JP-A-4-308670, are mainly used in view of production cost and cyclic charging/discharging characteristics. For Example Ullmanns Encyclopädie der technischen Chemie, Vol. 14 (1977). p. 602 describes some characteristics values of coke. These cokes are all derived from fossile sources. However a coke obtained from high molecular plant-origin is not described. Further, Handbook of Battery Materials, Wiley-VCH (1999), p. 235, left column describes of carbonaceous materials like graphite and a variety of amorphous carbons such as carbon black, active carbon and glassy carbon. According to EP 0 700 105 A2 it is described the use of coconut shells for the production of a carbonaceous electrode material. In Example 5 the coconut shell char is used as a starting material which is obtained from a commercial source. In said example, before further carbonization, the char is leached with 35% hydrochloric acid at 55°C for one hour and then sufficiently washed with deionized water to obtain deashed char, i.e. the amount of impurities are reduced as much as possible. Of these carbonaceous materials, those produced by sintering crystalline cellulose, which is a natural high molecular material susceptible to fluctuations in the polymerization degree and hence in the properties of the sintered product to a lesser extent than synthetic high molecular material (JP-Patent Kokai publication JP-A-2-54866) is drawing the notice. This carbonaceous material is thought to be promising as a material of a negative electrode of a non-aqueous liquid electrolyte secondary cell in that it has a high charging capacity as compared to cokes. In distinction from a synthetic high molecular material prepared from fossil resources, cellulose is a regeneratable raw material and its re-utilization is thought to be desirable from the viewpoint of maintenance and improvement of earth environment. However, the crystalline cellulose based carbonaceous material, while having a higher charging capacity, undesirable has a low charging/discharging efficiency which is a ratio of the discharging capacity to charging capacity. Consequently, for producing a practically useful cell using the crystalline cellulose based carbonaceous material as a negative electrode material, it becomes necessary to use an active material for a positive electrode, such as oxides of lithium transition metals, in an amount that matches the charging capacity instead of the discharging capacity of the negative electrode, so that a considerably excess amount of the active material for the positive electrode as compared to the discharging capacity is used. Therefore, using the crystalline cellulose based carbonaceous material of low charging/discharging capacity as a material of a negative electrode of a non-aqueous liquid electrolyte secondary cell is not desirable in producing a high energy density cell under conditions of limited volume and weight. It has also been demanded to proceed further from using a vegetable high molecular material, such as regeneratable crystalline cellulose as a raw material for the carbonaceous material for a negative electrode of a non-aqueous liquid electrolyte secondary cell, and to re-utilize the used waste material thereof as a regenerated material. It is an object of the present invention to provide a non-aqueous liquid electrolyte secondary cell using a negative electrode material for realizing a high charging/discharging capacity and a high charging/discharging efficiency. The negative electrode material being prepared from a raw material that is regeneratable and can be produced from an industrial waste material. As a result of perseverant researches, the present inventor has found that, by using a negative electrode prepared by sintering and carbonizing a specified plant origin high molecular material available as an industrial waste material, a high charging/discharging capacity can be achieved in a non-aqueous liquid electrolyte secondary cell. The present inventor has also found that such specified plant high molecular material, thus sintered and carbonized, contains metal elements, element phosphorus and element sulphur in higher proportions than the carbonaceous material derived from crystalline cellulose and consequently a high charging/discharging efficiency can be achieved in the non-aqueous liquid electrolyte secondary cell by using a negative electrode material formed of a co-carbonized material of the compound containing the above elements and the high molecular plant-origin material. The present inventor has also found that a material obtained on sintering and carbonizing a specified plant-origin high-molecular material has a peak in a specified range of 2 diffraction angle of an X-ray diffraction pattern, such peak being not observed in the case of a carbonaceous material derived from a high purity crystalline cellulose, and that not only the material obtained on sintering and carbonizing the specified plant-origin high-molecular material, but also the carbonaceous material having such peak, can achieve high charging/discharging capacity in the non-aqueous liquid electrolyte secondary cell as compared to the carbonaceous material not having such peak. The above information has led to completion of the present invention. It is therefore provided a non-aqueous liquid dectrolyte secondary cell having a positive electrode formed of a lithium compound oxide and a negative electrode formed of a carbonaceous negative electrode material capable of doping and dedoping lithium ions as an active negative electrode material, wherein the carbonaceousn egative electrode material is obtained by carbonizing in vacuum or in an inert gas atmosphere at 300 to 800°C a plant-origin high molecular material containing a sum total of 0.2 to 20 wt.-% of metal elements, phosphorus and sulfur calculated as elements, subsequently raising the temperature in vacuum or in an inert gas atmosphere at a temperature raising of not less than 1°C/ min up to a temperature of 700 to 3000°C and maintaining the temperature for 0 to 10 hours, wherein the thus obtained carbonaceous negative electrode material has a diffraction peak between 30° and 32° of the 2 diffraction angle in the X-ray (CuKα) powder diffraction pattern, the diffraction peak having an intensity in the corrected X-ray (CuKα) powder diffraction pattern of not less than 2% of the intensity of the (002) diffraction peak. A first embodiment of a non-aqueous liquid electrolyte secondary cell according to the present invention resides in that the plant-origin high molecular material is selected from the group consisting of coffee beans, tea leaves, cane sugar, corns, fruits, straws of cereals and husks of cereals. A negative electrode material for a negative electrode material for a non-aqueous liquid electrolyte secondary cell according to the present invention contains a carbonaceous material derived from a plant-origin high molecular material containing a sum total of 0.2 to 20 wt% of metal elements, phosphorus and sulphur calculated as elements. A second embodiment of the present invention resides in a non-aqueous liquid electrolyte secondary cell characterized in that the plant-origin high molecular material contains 0.01 to 0.5 wt% of Na calculated as element; a non-aqueous liquid electrolyte secondary cell characterized in that the plant-origin high molecular material contains 0.01 to 3 wt% of K calculated as element; a non-aqueous liquid electrolyte secondary cell characterized in that the plant-origin high molecular material contains 0.05 to 20 wt% of Ca calculated as element; a non-aqueous liquid electrolyte secondary cell characterized in that the plant-origin high molecular material contains 0.02 to 1 wt% of Mg calculated as element; a non-aqueous liquid electrolyte secondary cell characterized in that the plant-origin high molecular material contains 0.005 to 0.5 wt% of Al calculated as element; a non-aqueous liquid electrolyte secondary cell characterized in that the plant-origin high molecular material contains 0.04 to 3 wt% of phosphorus calculated as element; a non-aqueous liquid electrolyte secondary cell characterized in that the plant-origin high molecular material contains 0.03 to 0.5 wt% of sulphur calculated as element; and a non-aqueous liquid electrolyte secondary cell characterized in that the plant-origin high molecular material contains 0.01 to 1 wt% of Si calculated as element. The conditions of the embodiments may be taken into account independently. That is, it is only sufficient if one of the conditions, that is the sum total of the amounts of the respective elements and the amounts of the respective elements, is met. Of course, two or more of the conditions may be met. A non-aqueous liquid electrolyte secondary cell according to the present invention resides in that the negative electrode material contains a carbonaceous material having a diffraction peak between 30° and 32° of the 2 diffraction angle in the X-ray (CuKα) powder diffraction pattern. The negative electrodes of the above-described embodiments are highly suitable for a non-aqueous liquid electrolyte secondary cell. In particular, the negative electrode materials of the embodiments are highly suitable for a non-aqueous liquid electrolyte secondary cell having a positive electrode formed of a lithium compound oxide and a negative electrode formed of a carbonaceous negative electrode material capable of doping and dedoping lithium ions as an active negative electrode material. BRIEF DESCRIPTION OF THE DRAWING Fig.1 is a graph showing a corrected X-ray (CuKα) diffraction pattern of a negative electrode material of an Example F1. BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be explained beginning from a material of a negative electrode of a non-aqueous liquid electrolyte secondary cell. The material of a negative electrode of a non-aqueous liquid electrolyte secondary cell contains at least one carbonized material selected from the group consisting of coffee beans, tea leaves, sugar cane, corn, fruits, straws of cereals, or husks of cereals. it is possible with these carbonized materials to achieve a high charging/discharging efficiency as compared to the carbonaceous material derived from pure crystalline cellulose. Although the reason therefor is not apparent, the present inventor contemplates as follows: That is, in distinction from filter paper formed of substantially pure crystalline cellulose with a molecular weight of the order of 200,000, the coffee beans, tea leaves, sugar cane, corn, fruits, straws of cereals, or husks of cereals contain a larger amount of components other than such cellulose. For example, coffee or tea leaves contain hemicellulose with a molecular weight on the order of 20,000, low molecular weight caffeine or organic acids, while sugar cane or corn contains starch or sugar. The fruits contain hemicellulose, vitamins and minerals, while straws or husks of cereals contain metals, phosphorus or sulphur. It is contemplated that, if the raw material having such composition is carbonized, there is formed a matrix derived from crystalline cellulose and a structural or porous portion derived from other components, such as hemicellulose, starch or extraneous elements are intricately entangled with the matrix thus forming a low-crystalline structure. It may be presumed that the number of doping sites for light metal ions present in inter-layer portions of the graphite-like layered structure, such as lithium ions, is increased, while the number of sites that cannot be dedoped is decreased. Therefore, the negative electrode material is useful as a negative electrode that can dope and dedope light metal ions operating as an active material of a negative electrode of a non-aqueous liquid electrolyte secondary cell, such as lithium ions. The material of a negative electrode of a non-aqueous liquid electrolyte secondary cell is produced by sintering and carbonizing at least one selected from the group consisting of coffee beans, tea leaves, sugar cane, corn, fruits, straws of cereals, or husks of cereals. The carbonizing conditions, such as temperature raising rate, ultimate temperature (sintering temperature) or cooling conditions can be set appropriately. For example, sintering may be by previously carbonizing in vacuum or in an inert gas atmosphere, such as in nitrogen or argon atmosphere, at 300 to 800 °C, preferably 400 to 700°C, subsequently raising the temperature in vacuum or in an inert gas atmosphere, such as in nitrogen or argon atmosphere, at a temperature raising rate of not less than 1°C/min, preferably not less than 3°C/min and more preferably not less than 5°C/min, up to a temperature of 700 to 3000°C, preferably 800 to 2000°C and more preferably 90 to 1500°C and maintaining the temperature for 0 to 10 hours, preferably for 0 to 7 hours and more preferably for 0 to 5 hours. There is no particular limitation to the sorts or forms of the coffee beans, tea leaves, such as leaves of green tea or black tea, cane sugar, corns or fruits, such as oranges or bananas, and may be raw or processed such as by drying, fermentation, pulverization, baking or extraction. In particular, from the viewpoint of utilizing the industrial wastes as resources, used-up coffee beans, tea leaves, squeezed cane sugar, corn kernels, oranges or banana husks may preferably be used. These may be produced easily and in larger quantities from a food processing companies. The cereals of which the straws or husks are used are not placed under limitation and straws or husks of rice, wheat, wheat, ryes, barnyard millet or millet may be used. There is no limitation to the shape or from of the straws or husks such that raw or dried the straws or husks may be used. Those processed in many ways, such as by fermentation, baking or extraction in food or beverage processing, such as beer or foreign liquors, may also be used. In particular, the straws or husks obtained after threshing are preferably used for utilizing the industrial wastes as resources. The processed straws or husks may be easily obtained in larger quantities from the liquor producer or food companies. The material of a negative electrode of a non-aqueous liquid electrolyte secondary cell is composed of a carbonaceous material derived from a plant-origin high molecular material containing a sum total of 0.2 to 20 wt%, preferably 0.5 to 10 wt% and more preferably 1.0 to 5.0 wt% of metal elements, phosphorus and sulphur calculated as elements. Such carbonized material can achieve a higher charging/ discharging efficiency than is possible with the carbonaceous material derived from pure crystalline cellulose. Although the reason therefor is not apparent, it may be contemplated that, by containing at least one of metal elements, phosphorus and sulphur, the carbonaceous material is lowered in crystallinity and the number of doping sites for light metal ions present in inter-layer portions of the graphite-like layered structure, such as lithium ions, is increased, while the number of sites that cannot be dedoped is decreased. Therefore, the negative electrode material of the second embodiment is useful as a negative electrode that can dope and dedope light metal ions operating as an active material of a negative electrode of a non-aqueous liquid electrolyte secondary cell, such as lithium ions. If the content of metals, phosphorus and sulphur is less than 0.2 wt%, calculated as elements, the charging/discharging efficiency cannot be expected to be increased. If the content exceeds 20 wt%, crystallinity becomes too low and hence moldability is undesirably lowered. Examples of the metal elements may be enumerated by Na, K, Ca, Mg, Al and Si. The material of a negative electrode of a non-aqueous liquid electrolyte secondary cell may be produced by sintering and carbonizing a plant-origin high molecular material, containing at least one of metal ions, phosphorus and sulphur, in the same way as described above. As the plant-origin high molecular material, substantially pure crystalline cellulose may be employed, however, the plant-origin high molecular material containing metal containing vitamins, phosphorus compounds or sulphur compounds in the spontaneous growing state may preferably be employed. In particular, at least one carbonaceous material selected from coffee beans, tea leaves, sugar cane, corn, fruits, straws of cereals, or husks of cereals may preferably be used in view of re-utilization of the waste materials as resources and for increasing the charging/discharging efficiency. If crystalline cellulose is used as the plant-origin high molecular material, or if the content of particular elements is increased, various metals, phosphorus or sulphur are added to the plant-origin high molecular material as they are or in the form of hydroxides, oxides, inorganic salts, such as carbonates or phosphates, or organic salts, such as carboxylates. For adding these compounds to the plant-origin high molecular materials, powders may be directly admixed to the plant-origin high molecular materials, or added and mixed to the plant-origin high molecular material as a solvent dissolved in a suitable solvent. The addition may be made before or after preliminary carbonization. A further embodiment of the present invention is now explained. In the above-described embodiment, the present invention has been grasped from the viewpoint of the total content of metals, phosphorus and sulphur. In the further embodiment of the material of a negative electrode of a non-aqueous liquid electrolyte secondary cell, the present invention is grasped from the viewpoint of the content of each element. As for the amounts of the various elements in the carbonaceous material derived from the carbonaceous material plant origin high molecular material, the amount of Na is 0.01 to 0.5 wt%, that of K is 0.01 to 3 wt%, that of Ca is 0.05 to 20 wt%, that of Mg is 0.02 to 1 wt%, that of Al is 0.005 to 0.5 wt%, that of phosphorus is 0.04 to 3 wt%, that of sulphur id 0.03 to 0.5 wt% and that of Si is 0.01 to 1 wt%. At least one of these conditions should be met. As compared to the carbonaceous material derived from the pure crystalline cellulose, the above-defined carbonaceous material is capable of achieving a high charging/discharging efficiency. Although the reason therefor is not apparent, it may be contemplated that, by the content of at least one of the above-mentioned elements in the specified range, the carbonaceous material is lowered in crystallinity and the number of doping sites for light metal ions present in inter-layer portions of the graphite-like layered structure, such as lithium ions, is increased, while the number of sites that cannot be dedoped is decreased. Therefore, the negative electrode material is useful as a negative electrode that can dope and dedope light metal ions operating as an active material of a negative electrode of a non-aqueous liquid electrolyte secondary cell, such as lithium ions. The material of a negative electrode of a non-aqueous liquid electrolyte secondary cell according to the further embodiment can be produced by sintering and carbonizing a plant-based high-molecular material containing Na, K, Ca, Mg, Al, phosphorus, sulphur or Si in the same way as when producing the material of a negative electrode of a non-aqueous liquid electrolyte secondary cell as described above. As the plant-based high molecular materials, the plant-based high molecular material similar to that explained may be used. This achieves higher charging/discharging capacity. The embodiment of the material of a negative electrode of a non-aqueous liquid electrolyte secondary cell grasps the present invention from the viewpoint of X-ray (CuKα) powder diffraction pattern characteristics. With such carbonaceous material, as compared to the crystalline cellulose based carbonaceous material not exhibiting the diffraction peaks, a high charging/discharging capacity may be achieved. Although the reason therefor is not apparent, it may be contemplated from the fact that crystalline cellulose fails to exhibit the diffraction peak that, if the carbonaceous material is lowered in crystallinity, the number of doping sites for light metal ions present in inter-layer portions of the graphite-like layered structure, such as lithium ions, is increased, while the number of sites that cannot be dedoped is decreased. Therefore, the negative electrode having such diffraction peak is thought to improve the charging/discharging capacity of the non-aqueous liquid electrolyte secondary cell. Therefore, the negative electrode material is useful as a negative electrode that can dope and dedope light metal ions operating as an active material of a negative electrode of a non-aqueous liquid electrolyte secondary cell, such as lithium ions. Meanwhile, such carbonaceous material have diffraction peaks between 30° and 32° of the 2 diffraction angle that the diffraction peak intensity between 30° and 32° of the 2 diffraction angle in the corrected X-ray (CuKα) powder diffraction pattern intensity is not less than 2% of the (002) diffraction peak intensity. It is noted that the correction of the X-ray powder diffraction pattern is the diffraction pattern intensity I() corrected by the squares of the polarization factor, absorption factor and the atomic scattering factor (which is a function of sin/λ but for which a coefficient of an analytic approximate equation on the carbon atom not in the valence state is used): polarizationfactor = 1 + cos 2 (2*)*cos 2 (2*α) 1 + cos 2 (2*α) [ for 0 < t < A / 2*cosec] absorptioncoefficient = ( sec  - t A *tan)*exp(-µ* t *(sec - 1)) [ for t ≥ A / 2* cosec2 ] absorptioncoefficient = A 2 t * cosec2 *exp(-µ* t *(sec - 1)) The intensity I() is arbitrary and may be the number of counts per second or simply the number of counts. In the above equations,  is the angle of diffraction, A is the width the X-rays impinges on the sample surface (= L*sin β, where L is the distance from an X-ray source to the sample and β is a scattering slit width), t is a sample thickness, µ is a line absorption coefficient of a sample which is equal to the product of a mass absorption coefficient of a sample (4.17) with the specific gravity), and α is one-half the diffraction angle of a monochrometer. If a CuKα ray and a graphite monochrometer, for example, are used, α is 13.3° which is one-half the (002) diffraction angle of graphite. Although the material of a negative electrode of a non-aqueous liquid electrolyte secondary cell may be a difficultly graphitizable carbon material or an easily graphatizable carbon material, the former is preferred in view of an increased volume. The difficultly graphitizable carbon material usually means a carbonaceous material which is not graphitized readily even after high-temperature heat treatment at elevated temperature of the order of 3000°C. In the present invention, it means such a carbonaceous material having a d (002) value of not less than 0.34 nm after heat treatment at 2600°C. The material of a negative electrode of a non-aqueous liquid electrolyte secondary cell can be prepared by sintering and carbonizing various carbon precursors in the same way as described above. These carbon precursors are enumerated by a natural organic substance, such as an organism of a living organism. The tissue of the living organism may be enumerated by coffee beans, tea leaves, sugar cane, corn, fruits, straws of cereals, or husks of cereals. The negative electrode materials is required to have specified diffraction peak, so that it is necessary to select and use the above-mentioned sintered precursors of the carbonaceous materials having the above-mentioned diffraction peak. The negative electrode materials according to the above embodiments are employed as conventionally as the negative electrode materials for a non-aqueous liquid electrolyte secondary cell. In particular, the negative electrode materials are used as the negative electrode of the non-aqueous liquid electrolyte secondary cell having a positive electrode formed of a lithium compound oxide and a negative electrode formed of a carbonaceous electrode material capable of doping and dedoping lithium ions as an active negative electrode material. In particular, the negative electrode suitable for a cell, in particular a non-aqueous liquid electrolyte secondary cell, may be prepared by pulverizing negative electrode materials of the above embodiments, heating the resulting powders at about 600°C if need be for removing surface adsorbed water, mixing the resulting powders with a binder, such as polyvinylidene fluoride and a solvent, such as dimethylamide to prepare a paste-like mixture and coating the resulting mixture on a current collector. The non-aqueous liquid electrolyte secondary cell, having the negative electrode, thus produced, is improved in charging/discharging capacity and charging/discharging efficiency. The positive electrode constituting the non-aqueous liquid electrolyte secondary cell may be formed by employing metal oxides, metal sulfides or specified polymers as active material depending on the sorts of the cell to be produced. For producing a non-aqueous liquid electrolyte lithium ion secondary cell, metal sulfides or oxides not containing lithium, such as TiO 2 , MoS 2 , NbSe 2 or V 2 O 5 , may be used as a positive electrode active material. For producing a cell of high energy density, it is desirable to employ a lithium composite oxide mainly composed of Li x MO 2 , where M denotes one or more transition metals, with 0.05 ≤ x ≤ 1.10. As the transition metals M making up the lithium compound oxide, Co, Ni or Mn is preferred. Examples of the lithium compound oxides include LiCoO 2 , LiNiO 2 and Li x Ni y Co 1-y O 2 , where x, y differ with the charging/discharging state of the cell and usually 0 < x < 1 and 0.7 < y < 1.2, and LiMn 2 O 4 . These lithium compound oxides may be prepared by pulverizing and mixing carbonates, nitrates, oxides or hydroxides of lithium with carbonates, nitrates, oxides or hydroxides of cobalt, manganese or nickel in desired proportions and sintering the resulting mixture in an oxygen atmosphere in a temperature range from 600°C to 1,000°C. The non-aqueous solvents constituting the non-aqueous liquid electrolyte secondary cell may be propylene carbonate, ethylene carbonate, diethyl carbonate, methyl ethyl carbonate, 1,2-dimethoxyethane, 1,2-diethoxyethane, γ-butyrolactone, tetrahydrofuran, 1,3-dioxolane, dipropyl carbonate, diethylether, sulforane, acetonitrile, propylnitrile, anisole, ester of acetic acid or esters of propionic acid. Two or more of these compounds may be used in combination. As the electrolytes dissolved in non-aqueous electrolytes, salts of light metals, such as lithium, sodium or aluminum may be employed. These electrolytes may be selected suitably depending on the sorts of the cells employing the non-aqueous liquid electrolytes. For constituting the non-aqueous liquid electrolyte secondary cell, lithium salts, such as LiClO 4 , LiAsF 6 , LiPF 6 , LiBF 4 , LiCF 3 SO 3 , LiN(CF 3 SO 2 ) 2 , may be employed as the electrolyte. As described above, by employing the material of a negative electrode of a non-aqueous liquid electrolyte secondary cell of the present invention in the non-aqueous liquid electrolyte secondary cell having the positive electrode formed of a lithium composite oxide and a negative electrode formed of a carbonaceous material capable of doping and dedoping lithium ions, it becomes possible to provide a non-aqueous liquid electrolyte lithium ion secondary cell having high energy density, high charging/discharging capacity and high charging/discharging efficiency. There is no particular limitation to the shape of the non-aqueous liquid electrolyte secondary cell which may be cylindrical, square, coin-shaped or button-shaped. If the cell is of the hermetically sealed type, a protection device may be provided for breaking the current with rise in pressure in the cell during failure such as excessive charging/discharging for assuring higher safety. The present invention will be explained with reference to more illustrative embodiments. Example A1 The coffee beans, washed with lukewarm water, were carbonized by heating at 500°C for five hours in a nitrogen stream. The resulting carbonized product was pulverized and 10 g of the resulting powders were charged into an alumina crucible and heated in a nitrogen stream of 1000 liters/ minute at a temperature rising rate of 5°C/minute up to an ultimate temperature of 1100°C. This temperature was maintained for one hour for sintering the material to a carbonized product. This produced a negative carbonaceous electrode material for a non-aqueous liquid electrolyte secondary cell. Example A2 A material of a negative electrode of a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example A1 except using an ultimate temperature of 1200°C. Example A3 A material of a negative electrode of a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example A1 except using leaves of green tea sufficiently washed with lukewarm water in place of coffee beans. Example A4 A material of a negative electrode of a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example A3 except using an ultimate temperature of 1200°C. Comparative Example a1 A material of a negative electrode of a carbonaceous material was produced in the same way as in Example A1 except using crystalline cellulose (manufactured by WAKO PURE CHEMICALS CO.LTD.) in place of coffee beans. Comparative Example a2 A material of a negative electrode of a carbonaceous material was produced in the same way as in Example A1 except using he ultimate temperature of 1200°C. Evaluation Using the negative carbonaceous electrode material obtained in Examples A1 to A4 and Comparative Examples a1 to a2, test cells were prepared as now explained for conducting negative electrode capacity tests. Preparation of Test Cells The respective negative carbonaceous electrode materials were pulverized in a mortar and classified in a mesh sieve for collecting powders with a diameter not larger than 38 µm. These powders were heated in an argon atmosphere at a temperature rising rate of 30 minute to an ultimate temperature of 600°C which was maintained for one hour. This removed water adsorbed on the surface of the powders. These powders were cooled to room temperature. After cooling, 90 parts by weight of the powders and 10 parts by weight of polyvinilydene fluoride (PVDF) as a binder and dimethyl formamide as a solvent were homogeneously mixed and dried to give a negative electrode mixture. 37 mg of the negative electrode mixture and a nickel mesh as a current collector with a nickel fiber diameter of 20 µm were used to prepare a pelle-t 15.5 mm in diameter as conventionally prepare a carbon electrode. Using the carbon electrode as a negative electrode, a coin-shaped test cell having a diameter of 20 mm and a thickness of 25 mm was prepared. The cell was made up of a counter electrode/ Li metal; separator/ porous film formed of polypropylene; liquid electrolyte/ solution obtained on dissolving LiClO 4 in a propylene carbonate dimethoxy ethane mixed solvent by 1:1 volume ratio at a ratio of 1 mol per liter; current collector/copper foil. Negative Electrode Capacity Test With the test cell, the following charging/discharging was carried out with the constant current of 1 mA (current density of 0.53 mA/cm 2 ). Meanwhile, the charging/discharging capacity (negative electrode) is based on the equilibrium potential as a reference thus reflecting characteristics proper to the material. The results obtained are shown in Table 1. Charging: Current supply for one hour and current interruption for two hours were recreated. By plotting the electrical voltage as shown with respect to minus 0.5 power of the current interruption time and extrapolation to infinite time, the equilibrium potential was estimated by the charging capacity (current supply/ current interruption charging/discharging method). The charging was discontinued when the equilibrium potential was 3 mV with respect to lithium. Discharging: Current supply for one hour and current interruption for two hours were recreated. Discharging was terminated at a time point when the test cell voltage in the current conducting state was lower than 1.5 V. The discharging capacity was divided by the carbon weight in the negative electrode to give a charging/discharging capacity of the negative electrode. raw materials used sintering temperature (°C) negative electrode capacity (mAh/g) volumetric increasing ratio (%) Ex.A1 coffee beans 1100 488 47 (to Comp. Ex.a1) Ex.A2 coffee beans 1200 407 32 (to Comp. Ex.a2) Ex.A3 green tea leaves 1100 412 24 (to Comp. Ex.a1) Ex.A4 green tea leaves 1200 368 19 (to Comp. Ex.a2) Comp. Ex.a1 cryst. cellulose 1100 332 - Comp. Ex.a2 cryst. cellulose 1200 308 - It is seen from Table 1 that the negative electrode materials of Examples A1 to A4, prepared using the coffee beans or green tea leaves as raw materials exhibited a high load capacity as compared to the negative electrode materials of Comparative Examples a1 and a2 obtained by sintering crystalline cellulose at the same temperature. Example B1 The cane sugar, washed with lukewarm water, was heated in a nitrogen stream at 500°C for 5 hours. The carbonized product was pulverized to powders, 10 g of which were charged into an alumina crucible and heated in a nitrogen stream of 10 liters/min at a temperature rising rate of 5°C/min to 1100°C (ultimate temperature) which was maintained for one hour for sintering and carbonization. This gave a negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell. Example B2 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example B1 except setting the ultimate temperature to 1200°C. Example B3 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example B2 except using corn washed with lukewarm water in place of the sugar cane. Example B4 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example B3 except setting the ultimate temperature to 1300°C. Comparative Example b1 The negative electrode carbonaceous material for comparison was produced in the same way as in Example B1 except using crystalline cellulose (manufactured by WAKO PURE CHEMICALS CO. LTD.) in place of the sugar cane. Comparative Example b2 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Comparative Example b1 except setting the ultimate temperature to 1200°C. Comparative Example b3 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Comparative Example b1 except setting the ultimate temperature to 1300°C. Evaluation Using the negative carbonaceous electrode material obtained in Examples B1 to B4 and Comparative Examples b1 to b3, test cells were prepared in the same way for conducting negative electrode capacity tests. The results are shown in Table 2. raw materials used sintering temperature (°C) negative electrode capacity (mAh/g) volumetric increasing ratio (%) Ex.B1 cane sugar 1100 425 28 (to Comp. Ex.b1) Ex.B2 cane sugar 1200 387 26 (to Comp. Ex.b2) Ex.B3 corn 1200 434 41 (to Comp. Ex.b1) Ex.B4 corn 1300 441 53 (to Comp. Ex.b3) Comp. Ex.b1 cryst. cellulose 1100 332 - Comp. Ex.b2 cryst. cellulose 1200 308 - Comp. Ex.b3 cryst. cellulose 1300 289 - It is seen from Table 2 that the negative electrode materials of Examples B1 to B4, prepared using the cane sugar or corn as raw materials exhibited a high load capacity as compared to the negative electrode materials of Comparative Examples obtained by sintering crystalline cellulose at the same temperature. Example C1 The skin of an orange, sufficiently washed with lukewarm water and ethanol, was heated in a nitrogen stream at 500°C for 5 hours. The carbonized product was pulverized to powders, 10 g of which were charged into an alumina crucible and heated in a nitrogen stream of 10 liters/min at a temperature rising rate of 5°C/min to 1100°C (ultimate temperature) which was maintained for one hour for sintering and carbonization. This gave a negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell. Example C2 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example C1 except setting the ultimate temperature to 1200°C. Example C3 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example C1 except using the skin of a banana washed sufficiently with lukewarm water and ethanol in place of the skin of an orange. Example C3 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example C1 except setting the ultimate temperature to 1200°C. Example C4 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example C1 except setting the ultimate temperature to 1200°C. Comparative Example c1 The negative electrode carbonaceous material for comparison was produced in the same way as in Example B1 except using crystalline cellulose (manufactured by WAKO PURE CHEMICALS CO. LTD. in place of the skin of an orange. Comparative Example c2 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Comparative Example c1 except setting the ultimate temperature to 1200°C. Evaluation Using the negative carbonaceous electrode material obtained in Examples C1 to C4 and Comparative Examples c1 and c2, test cells were prepared in the same way as in Examples A1 to A4 and Comparative Examples a1 and a2 for conducting negative electrode capacity tests. raw materials used sintering temperature (°C) negative electrode capacity (mAh/g) volumetric increasing ratio (%) Ex.C1 orange skin 1100 395 19 (to Comp. Ex.c1) Ex.C2 orange skin 1200 363 18 (to Comp. Ex.c2) Ex.C3 banana skin 1100 380 14 (to Comp. Ex.c1) Ex.C4 banana skin 1200 349 13 (to Comp. Ex.c2) Comp. Ex.c1 cryst. cellulose 1100 332 - Comp. Ex.c2 cryst. cellulose 1200 308 - It is seen from Table 3 that the negative electrode materials of Examples C1 to C4, prepared using the orange skin or banana skin as raw materials exhibited a high load capacity as compared to the negative electrode materials of Comparative Examples c1 and c2 obtained by sintering crystalline cellulose at the same temperature. Example D1 The husks of cereals, sufficiently washed with lukewarm water and ethanol, was heated in a nitrogen stream at 500°C for 5 hours. The carbonized product was pulverized to powders, 10 g of which were charged into an alumina crucible and heated in a nitrogen stream of 10 liters/min at a temperature rising rate of 5°C/min to 1100°C (ultimate temperature) which was maintained for one hour for sintering and carbonization. This gave a negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell. Example D2 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example D1 except setting the ultimate temperature to 1200°C. Comparative Example d1 The negative electrode carbonaceous material for comparison was produced in the same way as in Example B1 except using crystalline cellulose (manufactured by WAKO PURE CHEMICALS CO.LTD. for comparison. Comparative Example d2 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example D1 except setting the ultimate temperature to 1200°C. Evaluation Using the negative carbonaceous electrode material obtained in Examples D1 to D4 and Comparative Examples d1 and d2, test cells were prepared in the same way as in Examples A1 to A4 and Comparative Examples a1 and a2 for conducting negative electrode capacity tests. The results are shown in Table 4. raw materials used sintering temperature (°C) negative electrode capacity (mAh/g) volumetric increasing ratio (%) Ex.D1 husks of cereals 1100 447 35 (to Comp. Ex.d1) Ex.D2 husks of cereals 1200 398 29 (to Comp. Ex.d2) Comp. Ex.d1 cryst. cellulose 1100 332 - Comp. Ex.d2 cryst. cellulose 1200 308 - It is seen from Table 4 that the negative electrode materials prepared using the husks of cereals after threshing the cereals such as rice or wheat exhibits a high negative electrode capacity as compared to the negative electrode materials of Comparative Examples d1 and d2 obtained on sintering the crystalline cellulose at the same temperature. Example E1 As a raw material of the carbonaceous materials, 1 part by weight of potassium hydroxide and 8 parts by weight of ethyl alcohol were mixed to 99 parts by weight of crystalline cellulose resin (manufactured by WAKO PURE CHEMICALS CO.LTD. and the resulting mixture was heated in a nitrogen atmosphere at 500°C for 5 hours for carbonization. The carbonized product was pulverized and 1 g of the resulting powders was charged in an alumina crucible. The powders thus charged into the crucible were heated along with the crucible in a nitrogen stream of 3 liters/min to 1100°C or 1200°C (ultimate temperature) which was maintained for one hour for sintering and carbonization. Thus, a carbonaceous negative electrode material for a non-aqueous liquid electrolyte secondary cell could be produced. Example E2 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E1 except using a fibrous cellulose resin manufactured by SIGMA INC.in place of the crystalline cellulose resin. Example E3 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E1 except using sodium hydroxide in place of potassium hydroxide. Example 4 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E1 except using calcium hydroxide in place of potassium hydroxide. Example E5 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E1 except using magnesium hydroxide in place of potassium hydroxide. Example E6 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E1 except using aluminum hydroxide in place of potassium hydroxide. Example E7 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E1 except using silicic acid in place of potassium hydroxide. Example E8 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E1 except using phosphoric acid in place of potassium hydroxide. Example E9 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E1 except using sulfuric acid in place of potassium hydroxide. Example E10 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E1 except using 100 parts by weight of coffee beans washed with lukewarm water in place of 99 parts by weight of crystalline cellulose resin without using coffee beans washed with lukewarm water. Example E11 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E10 except using non-washed coffee beans in place of coffee beans washed with lukewarm water. Example E12 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E10 except using black tea leaves washed with water and ethyl alcohol in place of coffee beans washed with lukewarm water. Example E13 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E10 except using green tea leaves washed with water and ethyl alcohol in place of coffee beans washed with lukewarm water. Example E14 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E10 except using oranges washed with water and ethyl alcohol in place of coffee beans washed with lukewarm water. Example E15 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E10 except using sugar cane washed with water and ethyl alcohol in place of coffee beans washed with lukewarm water. Comparative Example e1 A carbonaceous negative electrode material was produced in the same way as in Comparative Example e1 except using fibrous cellulose resin in place of the crystalline cellulose resin. Evaluation Using the negative carbonaceous electrode material obtained in Examples E1 to E4 and Comparative Examples e1 and e2, test cells were prepared in the same way as in Examples A1 to A4 and Comparative Examples a1 and a2 for conducting negative electrode capacity tests. The results are shown in Tables 5 and 6. The amounts of metals, phosphorus and sulphur contained in each negative electrode material sintered at 1200°C were measured by phosphorescent X-ray analyses (qualitative and quantitative analyses employing Rigaku X-Ray Spectrometer RIX3000. The results are shown in Tables 7, 8 and 9. raw materials used additives sintering temperature (°C) charging/discharging efficiency (%) Ex. E1 cryst. cellulose resin potassium hydroxide (1 wt%) 1100 78.6 1200 77.2 Ex. E2 fibrous cellulose resin potassium hydroxide (1 wt%) 1100 78.1 1200 76.9 Ex. E3 cryst. cellulose resin sodium hydroxide 1100 77.9 1200 80.2 Ex. E4 cryst. cellulose resin calcium hydroxide 1100 76.9 1200 81.1 Ex. E5 cryst. cellulose resin magnesium hydroxide 1100 72.9 1200 74.3 Ex. E6 cryst. cellulose resin aluminum hydroxide 1100 78.8 1100 79.5 Ex. E7 cryst. cellulose resin silicic acid 1200 72.5 1100 77.4 Ex. E8 cryst. cellulose resin phosphoric acid 1200 81.5 1100 81.9 Ex. E9 cryst. cellulose resin sulfuric acid 1200 76.6 1100 77.3 elements Ex.13 Ex.14 Ex.15 Comp. Ex. e1 Comp. Ex. e2 Na 0.0748 0.0333 0.3438 0.0094 0.0086 K 2.2666 2.449 2.709 0.0053 0.0067 Ca 2.8426 14.779 0.5197 0.0197 0.0174 Mg 0.5147 0.3862 0.2418 0.0132 0.0151 Al 0.2077 0.3862 0.2418 0.0132 0.0151 Rb 0.0013 0.0023 0.0073 - - Sr 0.0023 0.1134 0.0011 - - Si 0.1435 0.0398 0.7054 0.0037 0.0049 P 2.0986 0.4735 0.3479 0.0234 0.0301 S 0.1181 0.1046 0.417 0.0168 0.0211 total 8.36391 18.389 5.3055 0.0963 0.1061 The numerals in Table 9 denote wt%. It is seen from the results of Tables 5 to 9 that the negative electrode materials of Examples E1 to E15 exhibit a higher charging/discharging efficiency than that of the negative electrode materials of Comparative Examples e1 and e2 obtained on sintering crystalline cellulose or fibrous cellulose at the same temperature. In particular, the negative electrode materials of Examples E10 to E15, employing plant-origin high molecular materials, such as coffee beans, black tea, green tea, cane sugar and oranges, as the raw carbonaceous materials, exhibit higher charging/discharging capacity than that of the negative electrode materials of Comparative Examples e1 and e2. It is seen that, with the plant-origin high molecular materials used in Examples E10 to E15, namely the coffee beans, black tea, green tea, cane sugar and oranges, inherently contain metals, phosphorus and sulphur as ingredients, certain amounts of these elements may be maintained without using additives, such as KOH. Example F1 The coffee beans, sufficiently washed with lukewarm water, were carbonized by heating in a nitrogen stream at 500°C for five hours. The carbonized product was pulverized and 10 g of the resulting powders was charged in an alumina crucible. The powders thus charged into the crucible were heated along with the crucible in a nitrogen stream of 10 liters/min to 1100°C (ultimate temperature) which was maintained for one hour for sintering and carbonization. Thus, a carbonaceous negative electrode material for a non-aqueous liquid electrolyte secondary cell was produced. Example F2 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example F1 except setting the ultimate temperature to 1200°C. Example F3 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example F1 except using green tea leaves sufficiently washed with lukewarm water in place in place of coffee beans. Example F4 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example F3 except setting the ultimate temperature to 1200°C. Example F5 As a raw material of the carbonaceous materials, 1 part by weight of potassium hydroxide and 8 parts by weight of ethyl alcohol were mixed to 99 parts by weight of crystalline cellulose resin (manufactured by WAKO PURE CHEMICALS CO. LTD. and the resulting mixture was heated in a nitrogen atmosphere at 500°C for 5 hours for carbonization. The carbonized product was pulverized and 1 g of the resulting powders was charged in an alumina crucible. The powders thus charged into the crucible were heated along with the crucible in a nitrogen stream of 3 liters/min to 1100°C or 1200°C (ultimate temperature) which was maintained for one hour for sintering and carbonization. Thus, a carbonaceous negative electrode material for a non-aqueous liquid electrolyte secondary cell could be produced. Example F6 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example F5 except using sodium hydroxide in place of potassium hydroxide. Example F7 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example F5 except using calcium hydroxide in place of potassium hydroxide. Example F8 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E1 except using magnesium hydroxide in place of potassium hydroxide. Example F9 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example F5 except using aluminum hydroxide in place of potassium hydroxide. Example F10 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example F5 except using silicic acid in place of potassium hydroxide. Example F11 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example E1 except using phosphoric acid in place of potassium hydroxide. Example F12 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Example F5 except using sulfuric acid in place of potassium hydroxide. Comparative Example f1 The negative electrode carbonaceous material for comparison was produced in the same way as in Example F1 except using crystalline cellulose (manufactured by WAKO PURE CHEMICALS CO. LTD. in place of coffee beans for comparison. Comparative Example f2 The negative electrode carbonaceous material for a non-aqueous liquid electrolyte secondary cell was produced in the same way as in Comparative Example f1 except setting the ultimate temperature to 1200°C. Evaluation Using the negative carbonaceous electrode material obtained in Examples F1 to F12 and Comparative Examples f1 and f2, test cells were prepared in the same way as in Examples A1 to A4 and Comparative Examples a1 and a2 for conducting negative electrode capacity tests. The results are shown in Table 4. On the other hand, X-ray diffraction of powders of respective negative electrode materials was measured under the conditions of an X-ray source of CuKα (wavelength λ of 0.15418 nm); a scattering slit width (DS) of 0.5°(β); a sampling interval of 0.05°; a scanning speed of 1°/min; a scanning width of 10° to 40°; and a distance from the X-ray source to a sample of 185 mm (L). The corrected X-ray diffraction pattern of powders of the negative electrode material of Example F1 is shown in Fig.1, where a solid line curve represents a fitting curve. The graph was obtained by dividing the intensity I() of the diffraction pattern by squares of the deflection factor, absorption factor and atomic scattering factor for correction. The as-corrected pattern Icorr () exhibited a locally minimum value near 2 of approximately 35°. This locally minimum value and the angle 2 giving the locally minimum value were read as Ia and as 1, respectively. For avoiding the effects of the noise in the signal, 15 to 35 point smoothing was carried out in a 2 range of from 30° to 40°. From the smoothed value of Icorr () was subtracted Ia to give an intensity which was then multiplied with sin 2  to give an as-corrected pattern. In the corrected diffraction pattern, with a (002) peak top intensity I max in the vicinity of 25° of the 2 value, the closest 2 angle having an intensity of I max /2 towards the low-angle side from the peak top position was read as 0. The corrected pattern from e0 to 1 was fitted with two Gauss peaks, that is the (002) peak and a sub-peak lying between the angles of 30° and 32°. The area intensity of the sub-peak lying between 30° and 32° was divided by the area intensity of the produced (002) peak to find a relative intensity (%). The results are shown in Table 10. Similarly, X-ray diffraction was measured of the negative electrode materials of Examples F2 to F12 and Comparative Examples f1 and f2. With the negative electrode materials of Examples F2 to F12. sub-peaks were observed between 30° and 32° of the 2 diffraction angle, while no such sub-peak was observed with the negative electrode materials of Comparative Examples f1 and f2. In addition, with the negative electrode materials of Examples F2 to F12, the relative intensity of the sub-peak between 30° and 32° of the 2 diffraction angle was found, as in Example F1. The results are also shown in Table 10. raw materials used additives sintering temperature (°C) negative electrode capacity (mAh/g) Ex. F1 coffee beans - 1100 488 Ex. F2 green tea leaves - 1200 407 Ex. F3 green tea leaves - 1100 412 Ex. F4 cryst. cellulose resin - 1200 368 Ex. F5 cryst. cellulose resin potassium hydrixide 1100 330 1200 305 Ex. F6 cryst. cellulose resin sodium hydroxide 1100 335 1200 304 Ex. F7 cryst. cellulose resin calcium hydroxide 1100 341 1200 300 Ex. F8 cryst. cellulose resin magnesium hydroxide 1100 421 1200 369 Ex. F9 cryst. cellulose resin aluminum hydroxide 1100 338 1200 327 Ex. F10 cryst. cellulose resin silicic acid 1100 383 1200 346 Ex. F11 cryst. cellulose resin phosphoric acid 1100 324 1200 299 Ex. F12 cryst. cellulose resin sulfuric acid 1100 381 1200 369 Ex. f1 - 1100 332 Ex. f2 - 1200 308 It is seen from Table 10 that, with the negative electrode materials of Examples F1 to F12having a diffraction peak between 30° and 32° of the 2 diffraction angle in the X-ray (CuKα) diffraction pattern, the negative electrode capacity is significantly increased as compared with the negative electrode materials of Comparative Examples f1 and f2 not exhibiting relevant diffraction peaks.

Claims: A non-aqueous liquid electrolyte secondary cell having a positive electrode formed of a lithium compound oxide and a negative electrode formed of a carbonaceous negative electrode material capable of doping and dedoping lithium ions as an active negative electrode material, wherein the carbonaceous negative electrode material is obtained by carbonizing in vacuum or in an inert gas atmosphere at 300 to 800°C a plant-origin high molecular material containing a sum total of 0.2 to 20 wt.-% of metal elements, phosphorus and sulfur calculated as elements, subsequently raising the temperature in vacuum or in an inert gas atmosphere at a temperature raising of not less than 1°C/min up to a temperature of 700 to 3000°C and maintaining the temperature for 0 to 10 hours, wherein the thus obtained carbonaceous negative electrode material has a diffraction peak between 30° and 32° of the 2 diffraction angle in the X-ray (CuKα) powder diffraction pattern, the diffraction peak having an intensity in the corrected X-ray (CuKα) powder diffraction pattern of not less than 2% of the intensity of the (002) diffraction peak. A non-aqueous liquid electrolyte secondary cell according to claim 1. wherein the plant-origin high molecular material is selected from the group consisting of coffee beans, tea leaves, cane sugar, corns, fruits, straws of cereals and husks of cereals. A non-aqueous liquid electrolyte secondary cell according to claim 1, wherein the metal elements comprise at least one of Na, K, Ca. Mg. Al and Si. A non-aqueous liquid electrolyte secondary cell according to claim 1, wherein the plant-origin high molecular material is crystalline cellulose or fibrous cellulose. A non-aqueous liquid electrolyte secondary cell according to claim 1, wherein the plant-origin high molecular material contains 0.01 to 0.5 wt.-% of Na calculated as element. A non-aqueous liquid electrolyte secondary cell according to claim 1. wherein the plant-origin high molecular material contains 0.01 to 3 wt.-% of K calculated as element. A non-aqueous liquid electrolyte secondary cell according to claim 1, wherein the plant-origin high molecular material contains 0.05 to 20 wt.-% of Ca calculated as element. A non-aqueous liquid electrolyte secondary cell according to claim 1. wherein the plant-origin high molecular material contains 0.02 to 1 wt.-% of Mg calculated as element. A non-aqueous liquid electrolyte secondary cell according to claim 1, wherein the plant-origin high molecular material contains 0.005 to 0.5 wt.-% of Al calculated as element. A non-aqueous liquid electrolyte secondary cell according to claim 1, wherein the plant-origin high molecular material contains 0.04 to 3 wt.-% of phosphorus calculated as element. A non-aqueous liquid electrolyte secondary cell according to claim 1, wherein the plant-origin high molecular material contains 0.03 to 0.5 wt.-% of sulfur calculated as element. A non-aqueous liquid electrolyte secondary cell according to claim 1, wherein the plant-origin high molecular material contains 0.01 to 1 wt.-.% of Si calculated as element.

Inventors: ADACHI MOMOE, AKASHI HIROYUKI, AZUMA HIDETO, IMOTO HIROSHI, KITAMURA KENICHI, SASAKI TERUE, TANAKA KOHICHI, YAMADA SHINICHIRO, ADACHI, MOMOE, AKASHI, HIROYUKI, AZUMA, HIDETO, IMOTO, HIROSHI, KITAMURA, KENICHI, SASAKI, TERUE, TANAKA, KOHICHI, YAMADA, SHINICHIRO, AZUMA, Hideto Sony Corporation
Applicants: SONY CORP, SONY CORPORATION
Application year: 1996
Main classification: H01M4
IPC codes: H01M4