METHOD OF PROTECTING THE SURFACE OF A FOIL, RELEASABLY ADHERING PROTECTIVE FILM AND FILM-COATED FOIL

Abstract: A method for protecting a substrate sheet (46) such as a conductive foil suitable for use in the manufacture of printed circuit boards involving applying a lamination mold-release layer (28) to one side of a protective film (12), and applying a preferably electron beam curable adhesive pressure-sensitive coating (42) to the other side of the film, curing the adhesive coating, and laminating the protective film to the foil (46) or other substrate sheet, which, in turn, may be laminated to other substrates such as dielectric sheets (60). The laminate product is a protected substrate sheet having a protective film laminated to one side of the sheet (or both), the film having a lamination mold-release layer on one side thereof and an electron beam cured pressure-sensitive adhesive coating on the other side thereof, said other side contacting but being releasably detachable from said substrate sheet. Where the substrate sheet is a foil or similar surface, protection is thus provided during handling and storage as well as during lamination, and the protective film is peelably detachable from the foil.

Description: METHOD OF PROTECTING THE SURFACE OF A FOIL, RELEASABLY ADHERING PROTECTIVE FILM AND FILM-COATED FOIL The present invention relates to the field of thin film plastic release layers or coatings for the lamination of thin sheet materials, including thin copper sheets as of the type used in printed circuit boards and similar devices, enabling the sheet materials to be laminated at high temperatures and high pressures with other substrates without damage to the surfaces) ofthe thin sheets and with subsequent removal ofthe pro¬ tective release layer(s) or coating(s), the invention being more particularly directed to the rendering of said protective layers or coatings adhesively attachable with high uniform surface attachment to, and releasable from, such sheets. The present invention relates also to methods for protecting the surfaces of sheet metal foils or other sheet materials, all herein sometimes generically referred to as "sheets" or "foils" and to resulting novel protected sheets and laminated sheet products. One such product is useful as an inteπnediate product in the manufacture of printed circuit boards and the like. More particularly, the present invention espe¬ cially relates to methods for protecting etchable conductive metal foil sheets or foil laminates (all hereinafter generically referred to as foils) using electron beam cured layers or coatings to protect the foils from damage during handling, shipping and storage, before and during and after processing into printed circuit boards and similar laminate structures. This application is a continuaύon-in-part of U.S. application Serial No. 278,871, filed July 8, 1994 for Sheets With High Temperature Stable Protection Coating. BACKGROUND QF THE INVENTION Printed circuit boards having a high density of electrical interconnections and circuitry have been developed from multilayer printed circuit board laminates to meet the needs for miniaturized electronic components. The multilayer printed circuit board laminates are made from suitable reinforced resin materials and thin metal foils, o particularly copper foils, which are processed together al high temperature and pres¬ sure, such laminates being used in the manufacture of printed circuit boards. A printed circuit board is made from a laminate by etching away portions of the conductive foils from the laminate surface to leave distinct patterns of conductive fines and formed elements on the surface ofthe etched laminate. Additional laminates 5 and or laminate materials are then packaged together with the etched product to form a multilayer circuit board package. Additional processing, such as hole drilling and component attaching, completes the printed circuit board package. While printed circuit boards are well known, printed circuit board technology continues to advance to provide higher density boards with smaller printed circuit ° lines. Miniaturization has advanced to the point, accordingly, that surface ∞ntamina- tion in storage and handling has now become a significant problem in addition to the problem of protecting the surfaces from the effects of high-temperature and high- pressure .amination processes. During the high-pressure and high-temperature lamination ofthe thin copper foils, thin plastic lamination mold release coating films or layers have been succesβ- fully temporarily interposed on the foil to minimize deleterious effects upon the foil surfaces during such lamination, as described, for example, in Martin J. Wilheim, U.S. Patent 4,753,847 of common assignee ofthe present invention. Among such remov¬ able inteφosed layers have been sheets of polyvinyl fluoride and the like, such as those ofthe "Tedlar" type ofthe Dupont Company. As for protection during handling and otherwise before lamination, a clean environment can help or at least rnύώnize, contamination problems. Another way to avoid or minimize such problems is to use protective films as suggested in U.S. Patent 5,120,590, involving edge adhesive attachment of such films over the foil. The present invention, however, provides a vastly improved way to protect the surfaces of sheets from conUunination during each of handling, shipping, storage and lamination, remarkably to rninimize contamination problems in the manufacture of circuit boards and the like; and, at the same time, to resist damaging effects ofthe before-described high-temperature (about 350°F) and high pressure (about 500 to 1000 pounds/in 2 ) lamination to other substrates. This invention takes advantage, moreover, ofthe high temperature stability of bonding materials achieved by processing appropriate reactive pressure-intact adhe¬ sives to such plastic films, preferably by electron-beam airing. Thus, the present in- vention provides a foil laminate having a foil- protecting, electron beam-cured film or layer serving as a covering or coating which can be readily removed from the foil surface following the appropriate processing, and with no visible residue left on the foil. Furthermore, the adhesive coating used in this invention on these protective films can be applied with a high degree of uniformity across the entire surface ofthe film and then uniformly applied upon the foil, not just at edges or select regions, and without concern of film placement over the foil surface, nor ofthe effects of elevated temperature and pressure on the chemical structure of said adhesive, or any physical or chemical effects upon the foil surface By combining on one surface (outer) ofthe thin protective film covering or layer, the type of pressure-and temperature-resistive mold release-coating treatment described in before-mentioned U. S. Patent 4,753,847, for example, and, on the other surface inner or (bottom), a suitable releasably attached cured pressure-sensitive ad¬ hesive coating against the foil surface, an attached protective layer or coating for that foil is provided during each of handling, shipping and storage, and a mold-release layer for lamination protection, as well. SUMMARY OF INVENTION In summary, from one of its broader viewpoints, the invention embraces a protective film for releasable adhesion to a surface of a sheet and for providing sur- face protection during each of a) storage, shipping and handling ofthe sheet, b) the application of high pressure at high temperature to said surface to lami¬ nate the opposite surface ofthe sheet to a substrate, c) subsequent handling ofthe resulting laminate, and d) the ultimate release detachment ofthe film from said surface, the film having an outer surface treated to resist high pressure laminating con¬ ditions at high temperature to serve as a lamination mold-release layer, and an inner surface uniformly coated with a high-temperature, high-pressure- resistant pressure-sensitive adhesive layer for releasable attachment to said surface of the sheet, and inert to physical and chemical reaction with the sheet. Preferred and best mode techniques and designs are hereinafter more fully de¬ scribed. BRIEF DESCRIPTION OF THE DRAWING The invention will now be described in connection with the accompanying drawings in which Fig. 1 is a somewhat schematic view illustrating a preferred em- bodiment of the process of the present invention; Fig. 2 A is a fragmentary cross-section of a foil carrying a preferred form of protective film prepared by the process of Fig. 1 and applied on one surface ofthe foil and having a cured lamination-release coating on its outer surface and a cured pres¬ sure-sensitive adhesive on its inner surface against the foil; Fig. 2B is a similar view of the protected foil about to be laminated to a di¬ electric substrate, Fig. 2C is a similar view after lamination; Fig. 2D is again a similar view showing the releasing ofthe protective film from the laminate; Fig. 3 is a cross-sectional view similar to Fig. 2A, but with a protective film applied to both surfaces ofthe foil; and Fig. 4 is a view of a modified offset gravure manufacturing process step. DESCRIPTION OF THE PREFERRED EMBODIMENTS In Figs 1 and 2 A a copper foil 46, as for printed circuit board use or the like, is shown provided along its upper surface with a protective layer 12, as of polyester film or other materials later described. As explained in previously mentioned U. S. Patent 4,753,847, the electron- beam airing of suitable polymeric coatings on such a polyester film 12 inserted on top of a copper foil 46 to be laminated to, for example, a dielectric substrate 60, Figs. 2B and 2C, as for such printed circuit board applications and the like, produces a lamina¬ tion pressure mold-release coating 28 that protects and cushions the upper surface of the foil from the high lamination pressure and at the high temperatures involved in laminating the foil 46 as at L, Figs. 1 and 2B, to the dielectric or other substrate 60. Suitable polymeric films of polyester, nylon or cellulose acetate and the like are de¬ scribed in this patent and are well useable with the present invention; such being treated for promotion of resin adhesion in laminates and having cured coatings of acrylated oligomer resins and the like. In accordance with the present invention, a synergism is created for these and other additional functions, by actually adhering the film layer 12 to the copper foil 46 before lamination—the film 12 then being part ofthe foil and serving to protect the foil in storage, shipping and handling, even before lamination The film, however, must itself be ultimately peelably releasable from the foil, as indicated more particularly in Fig. 2D, and must not itself contaminate, mar or alter the foil surface. It has been discovered that such a result can be achieved through the uniform coating ofthe film, such as along the inner surface thereof, to be applied, for example, to the upper foil surface, with an appropriate high-temperature-high-pressure-resistant pressure-sensitive adhesive coating 42, preferably electron-beam curable and inert to any reaction, chemical or physical, with the surface ofthe foil 46. Suitable adhesives so applied include polyesters such as those having reactive unsaturated polymeric chain terminations, including the later-mentioned type Dynacoll A 2583 of Huls America, Inc., and or condensation products of terephthalic acid and ethylene glycol chemically treated on both sides to promote adhesion, such as "Mdinex 3'4" of ICI. Such adhesives are preferably coated on the polyester film inner surface with a uni¬ form layer ofthe order of 0.5 mil coating thinness throughout-such adhesive coatings containing chemical terminations responsive to electron beam (and in some cases ul¬ tra-violet) radiation, serving as reactive oligomers or pre-polymers, and inert to reac¬ tion with the foil 46. While, in prepared form, the lamination cushioning or pressure-release outer protective surface is provided by the cured polymer coating 28 on the film 12, other types of film covering, surfacing or treatment may be used to provide similar lamina¬ tion pressure-release functions. There are various techniques suitable for fabricating the novel protective films and composites of film-foil and film-foil laminate, etc., ofthe invention; but a pre¬ ferred process will now be described with reference to Fig. 1 ofthe drawings. Fig. 1 illustrates a preferred embodiment of a process ofthe present invention and shows a cross-section of a preferred product ofthe present invention. While the preferred embodiment ofthe present invention is described in terms of foil laminates used in making printed circuit boards, h will be appreciated by those skilled in the art that, broadly speaking, this invention is applicable to other products as well, includ¬ ing, as further illustrations, substrate sheets of glass, polycarbonate, acrylic, or other material . in accordance with the process of Fig. 1, d e before-described protective film 12, as of polyester sheet material, or the like, is unwound from roll 14 and is passed through offset gravure coating station 16. At offset gravure coating station 16, an electron beam-curable release coating material 18, such as the before-mentioned polymeric material, is taken up by roller 20, transferred to roller 22, and applied to one side of film 12 as a continuous coating 24, thereon. Film 12 with coating 24 is then passed through an electron beam curing apparatus 26 where an electron beam is applied to coating 24 which is thereby cured to form the before-mentioned cured coating 28, which serves as the previously described lamination-release layer or coat¬ ing, Figs. 2 A and 2B Film 12 with the now cured coating 28 thereon is wound onto roll 30. Roll 30 is then turned over as indicated at arrow 32 and the film 12 with hs cured coating 28 thereon is unwound from roll 30 and an electron beam-curable adhe¬ sive coating material 34 is applied by a "knife over roll" applicator 36 to the previ¬ ously uncoated side of film 12. Film 12 with adhesive coating 38 is then passed through electron beam curing apparatus 40 and an electron beam is applied to cure the adhesive material 34 on film 12 to form the before-described cured pressure- o sensitive adhesive coating 42, Figs. 1 and 2 Film 12 is then rewound onto roll 44 and the adhesive side thereof is applied to a copper foil sheet laminate 46 between rolls 48 and 50. The now protected foil sheet laminate 52 is cut at station 54 to pro¬ vide sheets 56, Figs. 1 and 2 A, which are heated and pressed at press 58 to bond or laminate at L with a dielectric sheet 60, and thus to form laminate 62, as shown in 5 Fig. 2C. Finally, laminate 62 is allowed to cool. Laminate 62 is then fiirther proc¬ essed by suitable conventional processes such as drilling at 64 and cutting at 66 to provide a circuit board laminate 68 as is well known. Film 12 is then removed as shown at 70, Figs. 1 and 2D. Instead of a "knife-over-roll'' application technique, an offset gravure ° technique may be used as shown in Fig. 4, as may other well-known techniques be employed. In Fig. 4, the coating is applied by a gravure cylinder from a reservoir, so- labeled, under doctor blade control, to an applicator roll cooperating with a chrome roll or the like, as is well known. EXAMPLE 1 A polyester film (92ga-0.00092" thin-Melinex 314, ICI Resins) was installed in a coating machine equipped with an electron processor, manufactured by Energy Sciences, Inc. An electron beam curable release coating, such as that disclosed in said U. S. Patent 4,753,847, was applied by an offset gravure application station to one side ofthe polyester film at a coating weight of approximately 3 lbs. per 3000 sq. ft. and cured by electron beam at a dose of 3 megarads The film was turned over, and the before-mentioned Dynacoll A 2583 polymeric coating, heated to suitable applica¬ tion viscosity (about 100°C), was uniformly applied by a "knife over roll" applicator to the other side ofthe polyester film, and cured at a dose of 4 megarads at 165KVs. The resulting pressure-adhesive side ofthe resulting roll of film was found to be easily releasable from the opposite side lamination release layer as in the roll and was ap¬ plied to a copper foil sheet laminate, and pressed uniformly thereto at 350° F. at 500 psi for 90 minutes. Following the press cycle, the sample was allowed to cool, and subsequently the protective film was found to be easily removed by peeling from the copper sheet, as illustrated in Fig. 2D. There was no visible evidence of any surface contamination on the copper foil . It has been found, furthermore, particularly where extremely thin metal foils are increasingly coming into use, that the protective film(s) ofthe invention, as above described, may also synergistically provide a useful measure of stiffening to the foil, desirable for its handling and support. EXAMPLE 2 A roll of 48ga polyester film chemically treated on one side (ICI type 813) was converted in a commercial vacuum metallizer for the deposition of aluminum onto the untreated side of he film to an aluminum thickness of about 3 ohms per square. The metallized polyester was then converted in accordance with Example 1 with Dynacoll A 2583 adhesive from a "lαiife-over-rolT device to the opposite side, i e the treated side, ofthe polyester film, and cured by electron beam radiation at a dose of 4 megarads. The cured adhesive released from the metallized surface which itself then served as a lamination release layer. While the invention has thus far been described with the protective film ap¬ plied to one surface ofthe foil, a protective film may also be applied to the other side ofthe film as well, as shown in Fig. 3, such providing additional handling, shipping and storage protection; and, where appropriate, the optional selection ofthe side to which the lammation press is to be applied ln some instances, the mold-release layer may be separate from the film, though it is preferred to integrate the same into the film outer surface as above described. Further modifications will also occur to those skilled in this art and such are considered to fall within the spirit and scope ofthe invention as defined in the ap¬ pended claims.

Claims: CLAIMS 1 A protective film for releasable adhesion to a surface of a sheet and for providing surface protection during each of a) storage and handling ofthe sheet, b)the application of high pressure at high temperature to said surface to larni- nate the opposite surface ofthe sheet to a substrate, c) subsequent handling of the resulting laminate, and d) the ultimate release detachment ofthe film from said surface, the film having an outer surface treated to resist high pressure laminating con¬ ditions at high temperature to serve as lamination mold-release layer, and an inner surface uniformly coated with a high-temperature, high-pressure- resistant pressure-sensitive adhesive layer for releasable attachment to said surface of the sheet, and inert to physical and chemical reaction with the sheet 2. A protective film as claimed in claim I and in which the film is a thin poly¬ meric sheet and the lamination mold-release layer comprises a radiation-cured poly- meric coating upon the plastic sheet. 3. A protective film as claimed in claim 1 and in which the film is a thin poly¬ meric sheet and the adhesive layer comprises a radiation-cured pressure-sensitive ad¬ hesive coating upon the polymeric sheet. 4. A protective film as claimed in claim 3 and in which the adhesive coating is an electron-beam-cured polyester pressure-sensitive adhesive. 5. A protective film as claimed in claim 1 and in which the film is a thin polyester sheet, the lamination mold-release layer comprises a radiation-cured polymeric coat¬ ing upon the polyester sheet, and the adhesive layer comprises a radiation-cured pres¬ sure-sensitive adhesive coating. 6. A protective film as claimed in claim 5 for application to a surface of a copper foil 7. A protective film as claimed in claim 6 and in which the film is of sufficient thickness to impart a measure of stiffening to the foil. 8 A protective film as claimed in claim 6 and in which the adhesive layer is of o the order of 0.5 mils in thinness and the film is ofthe order of 92ga. 9. A protective film as claimed in claim 1 for application to a surface of a sheet selected from the group consisting of metal foil as for printed circuit use, glass, poly¬ carbonate and acrylic. 10. A protective film releasably adherable to a surface of a sheet, the film having 5 an outer surface treated to resist high pressure laminating conditions at high tem¬ perature to serve as a lamination mold-release layer, and an inner surface uniformly coated with a high-temperature-high-pressure-resistant pressure-sensitive adhesive layer adherable to the sheet surface but peelably releasable therefrom, and inert to re¬ action with the sheet. 0 11 A protective film as claimed in claim 10 and in which the sheet comprises a metal foil, the film is a thin polyester sheet, the lamination mold-release layer com- prises a radiation-cured polymeric coating upon the film, and the adhesive layer com¬ prises a radiation-cured pressure-sensitive adhesive coating. 12. A protective film as claimed in claim 11 and in which the film is of sufficient thickness to provide some stiffening support for the foil, and the film serves as its own release strip for releasably peeling the film from the foil. 13. A composite of a protective film releasably adhered to a surface of a sheet, the film having an outer surface treated to resist high pressure laminating conditions at high temperature to serve as a lamination mold-release layer, and an inner surface uniformly coated with a high-temperature, high-pressure pressure-sensitive adhesive o layer adhered to the sheet surface but releasable therefrom by peeling off the film, the adhesive being inert to reaction with the sheet. 14. A composite serving as an intermediate of a printed circuit board as claimed in claim 13 and in which the sheet comprises a thin copper foil, the film is a thin polyes¬ ter sheet, the lamination mold-release layer comprises a radiation-cured polymeric 5 coating upon the film, and the adhesive layer comprises a radiation-cured pressure- sensitive adhesive coating. 15. A composite as claimed in claim 14 and in which the film is of sufficient thick¬ ness to provide not only sufficient cushioning for lamination pressure protection for the foil, but some stiffening for the foil, and to serve as its own release strip for re- 0 leasably peeling the film from the foil. 16. A composite as claimed in claim 15 and in which an additional film is adhered to the opposite surface ofthe foil. 17 A composite as claimed in claun 15 and in which a dielectric substrate is lami¬ nated to the opposite surface ofthe foil. 18. A method of protecting the outer surfaces of sheets from handling, storage and high pressure lamination damage and the like, that comprises, preparing a protec- tive plastic film for at least one ofthe outer surfaces of a sheet by treating one ofthe film surfaces to provide a high-pressure, high-temperature resistant lamination mold- release layer therealong and uniformly coating the opposite film surface with a high- temperature, high-pressure pressure-sensitive adhesive layer, inert to reaction with the sheet, and applying the film to said outer surface ofthe sheet with the pressure- sensitive adhesive layer adhered uniformly against and along said outer surface ofthe sheet to serve as a protective film therefor, but with the film being releasably peelable from the sheet. 1 . A method as claimed in claim 18 and in which the film-covered sheet is lami¬ nated with a substrate by applying laminating pressure along the mold-release layer of the film. 20 A method as claimed in claim 18 and in which the sheet comprises a thin cop¬ per foil, the treating ofthe said one film surface is effected by radiation-curing a polymeric mold-release coating thereupon, and the pressure-sensitive adhesive layer coating upon the opposite film surface is also radiation-cured thereupon. 21. A method as claimed in claim 20 and in which the film is selected from the group consisting of polyester, nylon and cellulose acetate, the radiation-cured poly- meric coating is of an acryiated oligomer resin, and the pressure-sensitive adhesive layer is a radiation-curable polyester adhesive. 22 A method as claimed in claim 21 and in which the film is of the order of about 92ga in thinness, and the pressure-sensitive adhesive is apphed in a thinness ofthe or- der of about 0.5 mils. 23. A method for protecting a substrate sheet such as a conductive foil suitable for use in the manufacture of printed circuit boards, comprising the steps of: (A) providing a release coating on one side of a protective film; (B) applying an electron beam curable adhesive coating to the o other side of the protective film; (C) curing said adhesive coating; and (D) laminating said protective film substrate to a substrate sheet. 24 The method of claim 23 wherein said release coating is provided by applying an electron beam curable release coating to one side of said film and curing said re- 5 lease coating. 25 The method of claim 23 wherein said substrate sheet is a copper foil laminate. 26. The method of claim 25 wherein said substrate sheet is processed to form a printed circuit board. 27. The method of claim 25 wherein said film is a polyester film. 0 28. The method of claim 26 wherein said laminating of step (D) is carried out un¬ der heat and pressure and said substrate sheet is a dielectric. 29. The method of claim 23 wherein said substrate sheet is polycarbonate 30. The method of claim 23 wherein said substrate is acrylic. 31. A protected sheet laminate comprising: (A) a substrate foil sheet; and (B) a protective film laminated to said substrate sheet, said film having a release coating on one side and an electron beam-cured adhesive coating on the other side, said other side being in adhesive contacting relationship with said substrate sheet 32. A sheet as in claim 31 wherein said release coating is an electron beam-cured o polymeric release coating. 33. A βheet as in claim 31 wherein said substrate sheet is a copper foil laminate 34. A method of protecting the outer surface(s) of a sheet from handling and stor¬ age and from high pressure lamination damage when laminated by a lamination pres¬ sure surface to a substrate, that comprises, preparing a protective plastic film for an 5 outer surface of a sheet by uniformly coating one surfece of the film with a high- temperature, high-pressure pressure-sensitive adhesive layer, inert to reaction with the sheet; applying the coated film surface uniformly against and along said outer surface ofthe sheet to serve as a protective film therefor, but with the coating enabling the film to be releasably peelable from the sheet; placing the opposite surface ofthe sheet o against a substrate with which it is to be laminated by the application of a lamination pressure surface against the film-covered sheet; and interposing between the film and the lamination pressure surface a high-pressure, high-temperature resistant lamination mold-release layer. 35. A method as claimed in claim 34 and in which the mold-release layer com¬ prises a radiation-cured coating upon the film. 36. A method as claimed in claim 34 and in which the mold-release layer is a sepa¬ rate layer interposed between the film and the lamination pressure surface. 37. A method as claimed in claim 34 and in which the adhesive layer is applied to the film with a knife over roll application. 38. A method as claimed in claim 34 and in which the adhesive layer is applied to the film with an offset gravure apphcation.

Inventors: KEOUGH ALLEN H, WILHEIM MARTIN J, KEOUGH, ALLEN, H., WILHEIM, MARTIN, J.
Applicants: KEOUGH ALLEN H, METALLIZED PRODUCTS INC, WILHEIM MARTIN J, KEOUGH, ALLEN, H., METALLIZED PRODUCTS INC., WILHEIM, MARTIN, J.
Application year: 1996
Main classification: B32B31
IPC codes: H05K3