METHOD FOR DETERMINATION AND CONTROL OF THE AMOUNT OF NITROGEN DISSOLVED IN METALIC LIQUID PHASES AND DEVICE FOR ITS REALIZATION

Abstract: The present invention refers to a method for determination and control of the amount of nitrogen dissolved in metallic liquid phases and to a device permitting, when placed in the steel producing plant and for instance in the tundish or in the continuous casting mould, the determination of nitrogen content directly from the liquid phase. Such a device can point out possible nitrogen pick-up in real time, thus permitting to immediately intervene.

Description: METHOD FOR DETERMINATION AND CONTROL OF THE AMOUNT OF NITROGEN DISSOLVED IN METALLIC LIQUID PHASES AND DEVICE FOR ITS REALIZATION FIELD OF INVENTION The present invention refers to a method for determination and control of the amount of nitrogen dissolved in metallic liquid phases and to the device for its realization. The invention particularly refers to a device permitting a high measurement rate. STATE OF THE ART It is known that the in-line control of production processes actually has a direct positive influence both on production economy and on the quality of the end product. It is therefore important to have data acquisition systems able to give quick and reliable answers, to permit a real-time monitoring of a process and relevant timely adjustments, if necessary. In the iron and steel field, it is particularly needed the possibility of a continuous in-line monitoring of the concentration of such elements as nitrogen and hydrogen which are dissolved into the liquid steel from the gaseous environment and negatively influence the mechanical and physical characteristics of the end product. Particularly, nitrogen leads to hardening and fragility of ferrous alloys, thus being highly dengerous for steel products such as plates, gas pipes, deep-drawing sheets utilized in car bodies or domestic appliances production, for instance. The typical phase for nitrogen absorption from the atmosphere is during the steel transfer from the ladle to the mould, through the tundish . The determination of nitrogen content in liquid steel, directly in the steel shop, and preferably within the mould, could determine in real¬ time any rise in nitrogen concentration, thus permitting to timely intervene, in well known ways, to lower nitrogen pick-up and eliminate its excess from the metal bath. In the control of metallic materials production, particularly during the step in which such materials are in the liquid state, up to now the determination of dissolved chemical species, especially gases, was made through quickly solidified metal samples sent to the laboratory for analysis. Such a method, though accurate with errors within 5% , is not a satisfying one, due to excessive delay for the answer, tipically of 10-30 minutes, which does not allows for timely bath composition adjustments. A device for nitrogen determination in the liquid steel is available from Hereus-ElectroNite International N.V. The measurement method requires the immission into the liquid bath of an inert carrier gas, specifically helium. The nitrogen dissolved into the liquid steel is then divided, according to known laws, between metal and gas, and in the latter tends to a concentration, according to the Henry-Sieverts law, in equilibrium with, and proportional to, the one within the liquid bath. From the gas coming out from the bath, and containing all the chemical species extracted from the same, all the species interfering with the nitrogen analysis are eliminated through specific molecular sieves, and the purified gas is sent to the analysis made utilizing known apparatuses for thermal conductivity determination. The probe for introducing into the liquid bath a specific amount of helium, and for sampling it and send it to the analysis, is a disposable one and can give an answer in about 90 seconds, with a declared accuracy of 10$. It is possible to enhance this accuracy utilizing a well known artifice. After a first measure, a new extraction operation is started utilizing as carrier gas a mixture of helium and nitrogen in which the nitrogen content corresponds to the one previously determined, and the measure is repeated. If the new measure is identical to the previous one, the latter was correct; if a nitrogen content is determined higher than the previous one, the actual nitrogen content of the bath is higher than the one obtained in the previous measure, while if the newly determined content is lower, the bath has a lower nitrogen content. The above artifice permits to obtain an accuracy of about 5% - Such probes for the nitrogen determination, though representing an interesting progress with respect to the classic technique of laboratory analysis, still maintain even important drawbacks: - are of the disposable kind, allowing only a single determination at a time, thus not permitting a continuous monitoring; - it is practically impossible to introduce the probes into the mould with the necessary high cadence, first of all because it is forbidden to stay under the ladle during the casting and then because, even if it should be possible, the presence of casting powders and of se iliquid slag on the bath surface into the mould would make it highly difficult to correctly introduce the probe at the location and within the desired time; - the measure time of 90 seconds is still too long for some kind of intervention, and anyway it have to be strictly maintained: in fact, different residence times of the probe into the bath would make meaningless the measure; - in the nitrogen determination, it is necessary to utilize as carrier gas helium, which is very costly and usually not available in a steel shop. It is still unsolved the problem of the quick and accurate determination of the nitrogen content in liquid metal baths, in a continuous way or at least with a very short time interval from measure to measure. SUMMARY OF THE INVENTION It was now realized, and is part of present invention, a device permitting, when placed in the steel producing plant and for instance in the tundish or in the continuous casting mould, the determination of nitrogen content directly from the liquid phase. Such a device can point out possible nitrogen pick-up in real-time, thus permitting to immediately intervene. Another aspect of present invention is the method for the determination and control of the nitrogen content of metal baths through said device. Other objects of present invention shall be evident from the following detailed desctiption of the invention. BRIEF DESCRIPTION OF THE FIGURES Fig. 1 is a general scheme of the device according to present invention; Fig. 2 schematically shows the reactor according to Fig. 1 for the nitrogen oxidation; Fig. 3 is an enlarged schematic longitudinal section of a sensor particularly suited to measure the NO2 content in the gas. DETAILED DESCRIPTION OF THE INVENTION For a better understanding, present invention will be described starting from its realization method, which will make it simpler the following description and understanding of relevant device. To each phase of the process a part of the device is logically and operatively connected, as apparent from the following description. The method for the determination and control of nitrogen content in metal baths, according to present invention, comprises the following steps: - introducing into the liquid metal (in the following description also called metal bath or simply bath) a known quantity of inert carrier gas, for instance argon also mixed with other gases such as nitrogen, to promote a nitrogen exchange between the bath and the carrier gas; - withdrawing the carrier gas passed through the bath and containing nitrogen, adding to it a known quantity of oxygen and homogenizing the gas mixture thus obtained; - oxidizing the nitrogen contained in said gaseous mixture to nitrogen oxides, mainly NO2 and small quantities of NO; - measuring the NO2 content in said mixture and correlating it to the nitrogen content in the bath; - charging said analysys data in a computer and utilizing them control the nitrogen content in the metal bath. The carrier gas flow rate into the metal bath is comprised between 3 and 30 litres per hour. The oxygen flow rate to be added to the carrier gas passed through the bath is from 4θ to J0% of flow rate of carrier gas and the mixture is throughly homogenized and then treated to catalyze the nitrogen combustion to N0 2 , and small quantities of NO. Preferably, the homogenized gaseous mixture is subjected to electric sparks of between 3000 to 8000 V, to oxidize nitrogen to mainly N0 2 . The NO2 content of the thus obtained gaseous mixture is measured with known methods, and is correlated to the nitrogen content in the liquid metal bath, and the thus obtained concentration is utilized according to known methods to adjust, if necessary, the nitrogen content in the metal bath and hence to check and control the final quality of the products obtained from said metal bath. The production of small quantities of NO during the nitrogen combustion does not invalidate the method. In fact, the NO quantity is very small and its measure can be considered within the background noise, thus not significantly influencing the NO2 measure. To avoid "interpollution" of different measurements, the NO2 containing gas is sent to the analyzer in a non-continuous way, at regular time intervals as known volumes, utilizing an inert carrier gas, e.g. argon. Between a gas volume to be analyzed and the next one, the analyzer is fed with pure carrier gas, to purge any residual quantity of NU2- The gas volume to be analyzed, sent to the analyzer, is comprised between 0,3 amd 5 nil, while the carrier gas flow-rate during this step is between 5 and 20 1/h. With the utilized experimental apparatus, it is possible to perform quick measurements, typically a measure in 15-2 s, with an error lesser than 10%, improvable to less than % utilizing a double-measure system, as hereinafter specified. The measures cadence (2-4 measures per minute, instead of 0,6 measures per minute of known methods), though not permitting continuous measures, is however sufficiently quick to permit timely actions to control the nitrogen content in the liquid bath. The device according to present invention for the embodiement of the above method, comprises the combination in cooperation relationship of: - means for bubbling and picking-up a gas, enabling to inject an inert gas into a metal bath, thus realizing a nitrogen exchange between said bath and the injected gas, and to collect the obtained gas mixture; - means for extracting said gas mixture from said bubbling and picking-up means; - means for adding desired quantities of oxygen to said extracted mixture and means for homogenizing the gaseous mixture thus obtained; - means to subject the nitrogen contained in said homogenized gaseous mixture to a catalyzed oxidation; - means for measuring the NO2 content in said oxidated gaseous mixture; - means to acquire data relating to NO2 content in the oxidized gaseous mixture, transforming them in nitrogen content in the metal bath and utilizing them to monitor and modify, if necessary, the nitrogen content of the bath. The means for bubbling and picking-up a gas substantially comprise an element, for instance of an elongated tubular form, for picking-up the introduced gas, having a first conduit with a downwardly facing opening for the admission into said element of the gas to be bubbled through the bath, and a second conduit connected to said means for extracting the collected gas, for instance consisting in a rotary pump. The means for adding to the extracted gas known quantities of oxygen and for homogenizing the thus obtained mixture consist in an oxygen tank having means for controlling, measuring and purifying the outcoming oxygen flow, and in a conduit for admitting gas into a chamber, having openings for amitting and extracting gas, in which the extracted gas and oxygen are admitted. Said chamber is provided with a plurality of projections, for instance suitably located walls, to enhance the turbulence of the gases passing through said chamber and thus obtain a homogeneous gas mixture. Said means to oxidize the nitrogen in said homogenized gaseous mixture consist, for instance, in a reactor internally provided with means to subject the gaseous mixture containing nitrogen and oxygen to a catalytic oxidation reaction of the nitrogen, mainly to NO2. In said reaction, the oxidation efficiency of tne nitrogen (i.e. the ratio NO2/NO) is constant. Preferably, said means to subject the gas to a catalytic oxidation consist in at least a couple of electrodes, e.g. platinum ones, between which a tension is established sufficiently high to establish an electric arc. Said means for measuring the NO2 content in the gases coming out the reactor can be any sensor; preferably, said sensor comprises (i) a first conduit in which the gaseous mixture containing a component to be measured flows with laminar motion, (ii) a second conduit in which a carrier liquid, in which said component is soluble, flows with laminar motion, (iii) a membrane permeable only to said component and constituting a separating wall between said first and said second conduits, and (iv) a reference electrode and a measure electrode, sensing the concentration of said component, both placed in said second conduit. The linear speed of the carrier liquid on the semipermeable membrane is comprised between 10 and 10-- 5 m/s while the gas linear speed on the membrane is lesser than 5 m/s. The reference electrode is placed in said second conduit before said membrane, thus being always immersed in clean carrier liquid and therefore maintaining constant its potential, which is the reference potential. Said reference electrode has an wetted surface greater than the one of the measure electrode, preferably from 2 to 5 times greater. The semipermeable membrane is made with a porous hydrofobic polymer, with a mead pore dia etre of 1 micrometre. The gaseous mixture flows within the space between first and second conduits, and the carrier liquid flows within said second conduit in countercurrent with respect to the gaseous mixture, as a thin layer over the semipermeable membrane; its flow rate is comprised between 0,005 and 0,1 ml/s, preferably between 0,01 and 0,03 ml/s, its thickness being comprised between 2 and 0,05 mm, preferably between 1 and 0,1 mm. Said means to acquire data concerning the NO2 content in the gas and for correlating them to the nitrogen content in the metal bath comprise a computer provided with a standard program and with specific calibration curves, which can be obtained in any known way. It is to be noted that though the above device, particularly the sensor, is described only with reference to the analysis of NO ? , it can be easily utilized for the analysis of other species, of both acid and basic nature. Coming now to the enclosed Figures , the means for bubbling and picking-up the gas comprise a refractory collecting vessel (20) resistant to thermal shocks, preferably in silicon carbide, provided with a conduit (21), having flow controlling means (23) , for introducing a carrier gas and provided also with a second conduit { 22 ) to withdraw said gas from said vessel. The carrier gas, typically argon, flows within conduit { 22) coming from a tank (11), and its flovv rate is measured and controlled by a regulating flowmetre (13)- In operation, the vessel (20) s immersed into the metal bath with its opening facing downwardly, to a level comprised from 100 to 300 mm, and valve (23) is opened, allowing the carrier gas to bubble within the bath, activating the nitrogen exchange between bath and gas. The gas coming out of the bath and enriched w th nitrogen is then sent, by means of a pump (not shown), and of conduit (22 ) to the mixer/homogenizer (30) into which is mixed with oxygen coming from tank (31) through conduit (32) with a desired flow rate, measured and controlled by flowmetre (33)- The mixer/homogenizer (30) comprises a sealed chamber internally provided with deflecting walls, helical paths and the like permitting to homogenize the gaseous mixture consisting of argon, nitrogen and oxygen which is then sent to the reactor (-40) . The latter (Giggs 1 and 2) comprises a tubular chamber, containing at least a pair of electrodes (*42) facing to each other; between said electrodes and port (*45) for the immission of the homogenized gaseous mixture into chamber ( O ) a narrowing ( h ) is RECTIFIED SHEET (RULE 91} ISA / EP placed, preferably having a conical form, to send the gaseous mixture flow exactly in the space existing between the electrodes (-42) , in which an electric sparks are generated through a generator (4l), as described with reference to the embodiment method. Thus, the energy of the electric sparks catalyzes the nitrogen combustion, mainly to NO2. The generation of NO during the above process does not impair the validity of the measures, in that NO concentration is very small and the NO2/ O ratio is practically constant. During the measures the NO2 containing mixture, thus obtained, is sent to the analysis device (53) . which can be of the kind illustrated in Fig. 3- This device (100) comprises: (i) a first conduit (200) having an inlet opening (210) and a discharge opening (220), (ii) a second conduit (300) also having an inlet opening (310) and a discharge opening (320), and comprising a membrane (400) semipermeable to gases the extremities (350, 36O) of which are connected to metallic tubular elements containing (iii) a pair of reference (330) and measure (3^0) electrodes. Conduit (300) is internal and coaxial to conduit (200), and its metallic extremities, preferably made in stainless steel, comprise a first oxidized and stabilized zone (330), acting as reference electrode, and a second oxidized and stabilized zone (3*^0), acting as measure electrode. Cables (510, 520) respectively connect electrodes (330) and (3^0) to a measure instrument (500), in this case a millivoltmeter. The oxidized gaseous mixture is periodically sent to the analyzer as constant and known volumes controlled by a flowmetre (56) and by a four-ways cock (52), utilizing a carrier gas, argon for instance, erogates at a constant rate by a reservoir (50) through a flowmetre (5D. An important advantage of the device according to present invention is that vessel (20) can be permanently placed into the liquid bath, e.g. into the continuous casting mould, where can work during the entire casting process. This means that vessel (20) can be put in place before starting the casting operations (then easily and in complete safety for the operators) and continuously works for many hours without modifying the operating conditions of the plant. The device according to the invention can pinpoint on the line and within 1 -2 seconds any unduly high nitrogen content into the bath, allowing to timely operate to reduce said nitrogen content thus avoiding a downgrading of the end product. The device according to the invention can measure O2 contents even smaller than 1 ppm, on very small gas volumes. According to the present invention, the measure error of the nitrogen content in the metal bath is around 10%, depending on the uncertainties introduced by bath temperature variations and bath content of such elements as sulphur and oxygen, which can influence the exchange cinetics of nitrogen between metal bath and gas. It is possible to improve such figures utilizing a double-analysis technique, according to which after a first measure, obtained as above described, a second one is made, passing through the bath a nitrogen- argon mixture in which the nitrogen, coming from tank (10) and measured by flowmeter (15). has a content corresponding to the one in equilibrium with the nitrogen in the bath, known from the first measure; the mixture is homogenized in the mixer (1*4). If in said second measure the nitrogen content in the mixture passed through the bath is really in equilibrium with the bath, there will be no change in the nitrogen content in the gaseous mixture, and the measure will remain unchanged. On the other hand, should the measured concentrations be different, it is possible to desume, in a known way, the nitrogen concentration in equilibrium with the bath through solution of systems of differential cynetics equations. From this value, the Henry-Sieverts law allows to obtain the real concentration of nitrogen in the bath. It is thus possible to enhance the accuracy of the measures, at the expense of a doubling of the time necessary for each measure; however, a cadence of less than 50 seconds can be considered acceptable in most cases.

Claims: CLAIMS 1 1. Method for the measure and the control of the nitrogen content in 2 metal baths, characterized in that it comprises in a cooperation 3 relationship the following steps: 4 - introducing into the liquid metal a known quantity of inert carrier 5 gas, for instance argon also mixed with other gases such as nitrogen, 6 and letting it to bubble through the bath to promote a nitrogen 7 exchange between the bath and the carrier gas, and then collecting the 8 gas; 9 - withdrawing the collected gas, adding to it a known quantity of 0 oxygen and homogenizing the gas mixture thus obtained; 1 - oxidizing the nitrogen contained in said gaseous mixture to 2 nitrogen oxides, mainly NO2 and small quantities of NO; 3 - measuring the NO2 content in said mixture and correlating it to the *4 nitrogen content in the bath; 5 - charging said analysis data in a computer and utilizing them 6 control the nitrogen content in the metal bath. 1 2. Method according to clain 1, characterized in that the carrier gas 2 flow rate into the metal bath is comprised between 3 and 30 litres per 3 hour. 1 3- Method according to any one of the above claims, characterized in 2 that the oxygen flow rate to be added to the carrier gas passed *4 through the bath is from to 10% of flow rate of carrier gas and the 5 mixture is thoroughly homogenized. 1 k . Method according to any one of the preceding claims, characterized 2 in that the homogenized gaseous mixture comprising nitrogen and oxygen 3 is treated to catalyze the nitrogen combustion mainly to NO2. 5> Method according to claim 4, characterized in that the homogenized gaseous mixture is subjected to electric sparks of between 3000 to 8000 V, to catalyze the oxidation of nitrogen to mainly N0 2 - 6. Method according to any one of the preceding claims, characterized in that the gaseous mixture containing NO2 is sent to an analyzer for the determination, according to known ways, the NO2 which, in turn, is correlated to the nitrogen content in the liquid metal bath, and the thus obtained concentration is utilized according to known methods to adjust the nitrogen content in the metal. 7- Device for the embodiement of the above method, characterized in that it comprises the combination in cooperation relationship of: - means (20, 21, 23) for bubbling and picking-up a gas, enabling to inject an inert gas into a metal bath, thus realizing a nitrogen exchange between said bath and the injected gas; - means (22) for extracting said gas mixture from saig bubbling and picking-up means; - means (31. 32, 33) for adding desired quantities of oxygen to said extracted mixture and means (30) for homogenizing the gaseous mixture thus obtained; - means (40, 4l, 42) to oxidize mainly to NO2 the nitrogen contained in said homogenized gaseous mixture; - means (53. 100) for measuring the NO2 content in said oxidated gaseous mixture; - means (54, 55) for processing the above acquire data and relating them to the nitrogen content in the bath. 8. Device according to claim 7. characterized in that the means for bubbling and picking-up a gas substantially comprise an elongated element (20) provided with an internal space and having a first opening at one of its extremities, a first conduit (21) for the admission into said space of the inert gas and of a second opening provided with said means (22) for extracting the gas, consisting in a second conduit and means to control the gas flow. 9- Device according to claims 7 and 8, characterized in that said means for adding to the extracted gas known quantities of oxygen and for homogenizing the thus obtained mixture consist in an oxygen tank (31) having means (33) for controlling and measuring the outcoming oxygen flow, and in a chamber (30) , having openings for amitting and extracting gas, in which the extracted gas and oxygen are admitted, said chamber is provided with a plurality of suitably located projections to enhance the turbulence of the gases passing through said chamber and thus obtain a homogeneous gas mixture. 10. Device according to any of claims from 7 to 9. characterized in that said means to oxidize the nitrogen in said homogenized gaseous mixture comprise a tubular reactor (40) internally provided with means (42) to subject the gaseous mixture containing nitrogen and oxygen to a catalytic oxidation reaction of the nitrogen, mainly to NO2. 11. Device according to claim 10, characterized in that said means (42) to subject the gas to a catalytic oxidation consist in at least a couple of electrodes between which a tension is established sufficiently high to establish an electric arc. 12. Device according to any one of claims from 7 to 11, characterized in that said means (53. 100) for measuring the NO2 content in the gases coming out the reactor comprise (i) a first conduit (200) in which the gaseous mixture containing a component to be measured flows with laminar motion, and provided with an inlet opening (210) and a discharge opening (220); (ii) a second conduit (300), adjacent to the first one, through which a carrier liquid, in which said component is soluble, flows with laminar motion in countercurrent with said gaseous mixture, said second conduit having an inlet opening (310) and a discharge opening (320); (iii) a membrane (400) in a hydrophobic polymer permeable only to said component and constituting a separating wall between said first and said second conduits, and (iv) a couple of reference (330) and measure (340) electrodes, respectively, placed in said conduit (300) at the extremities of membrane (400) . 13- Device according to any one of claims from 7 to 12, characterized in that said second conduit (300) comprises stainless steel zones, carrying a reference electrode (33) consisting of a first oxidized and stabilized surface part, and a measure electrode (3^0) consisting of a second oxidized and stabilized surface part, said measure electrode (340) being from 20% to 50% longer than the reference one (330), from 2 to 5 times greater. RECTIFIED SHEET (RULE 91) ISA/ EP

Inventors: BORGIANNI CARLO, DI DONATO ANTONELLO, PISTELLI MARIA ILARIA, BORGIANNI, CARLO, DI DONATO, ANTONELLO, PISTELLI, MARIA, ILARIA
Applicants: BORGIANNI CARLO, DONATO ANTONELLO DI, PISTELLI MARIA ILARIA, SVILUPPO MATERIALI SPA, BORGIANNI, CARLO, CENTRO SVILUPPO MATERIALI S.P.A., DI DONATO, ANTONELLO, PISTELLI, MARIA, ILARIA
Application year: 1996
Main classification: C21C5
IPC codes: C21C5, G01N33