Catalyst for purifying exhaust gas

Abstract: This invention relates to a catalyst for purifying an exhaust gas using a complex oxide having good heat-resistant and a purification performance which does not undergo degradation, particularly in a lean atmosphere at a high temperature of about 1,000°C, by using the complex oxide containing platinum and at least one member of element selected from the group from an alkaline earth metal element and the Group IIIA element and, furthermore, by using at least one member of platinum complex oxides selected from the group of those Pt complex oxides expressed by the chemical structural formulas X 4 PtO 6 (X = Ca, Sr, Ba, Mg), X' 2 Pt 2 O 7 (X' = Sc, La, Pr), SrX''PtO 6 (X'' = Co, Ni, Cu), Ba 2 ZPtO 6 (Z = Pr, Ce) and Ba 8 Y 3 Pt 4 O 17.5 .

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a catalyst for purifying exhaust gas which entraps platinum into a complex oxide and comprises a complex oxide having a good heat-resistance performance even in a lean combustion atmosphere at a high temperature of not lower than 1000°C. 2. Description of the Prior Art A catalyst for purifying an exhaust gas for automobiles, etc, according to the prior art uses a precious metal such as platinum, palladium and rhodium, either alone or in combination, as a catalytic component, and the catalytic component is generally supported by a catalytic support. Among them, however, rhodium is not abundant and is expensive. Palladium has better heat resistance than platinum but has remarkably lower resistance to poisoning by the lead in gasoline, or to phosphorus in a lubricating oil than platinum. Therefore, platinum which is more plentiful than rhodium becomes an essential component. However, platinum causes the problems in that it is oxidized in a high temperature lean atmosphere, and that its surface area drops due to sintering and its activity as a catalytic component then drops remarkably. Furthermore, an improvement in catalysts, for better heat resistance, has been required because the exhaust temperature has become higher so as to cope with stricter exhaust gas regulations such as the European step III regulations and the λ = 1 regulations. For existing Pt/Aℓ 2 O 3 system catalysts, purification performance drops remarkably in a high temperature lean atmosphere, and they cannot satisfy such regulations. It is assumed that the drop of purification performance, too, results from sintering of platinum. As a well-known technology in this field, the applicant of the present invention proposed a catalyst for purifying an exhaust gas which can prevent thermal degradation of Pt and its alloying and can improve the durability as well as the purification performance by using a perovskite type complex oxide between Pt and a lanthanoid element, or an alkaline earth metal element or its analogous complex oxide, as a catalyst for purifying an exhaust gas for an internal combustion engine, in Japanese Unexamined Patent Publication (Kokai) No. 62-277150. Although capable of drastically improving durability, etc, in comparison with the conventional catalysts, this catalyst is not free from the problem that the perovskite type complex oxide starts being decomposed in a region where the exhaust gas temperature exceeds 900°C. As described above, the exhaust gas temperature has drastically risen due to various kinds of exhaust gas regulations in recent years, and the development of a catalyst which can sufficiently purify the exhaust gas even in a region higher than 1,000°C is required. GB-A-1 568 370 discloses catalysts for purifying an exhaust gas of automobiles comprising a supported rhodium-platinum alloy catalyst. WO-A-92/01505 discloses catalysts which contain a perovskite type complex oxide. SUMMARY OF THE INVENTION The present invention is directed to provide a catalyst having good heat-resistance for purifying an exhaust gas which enables platinum to prevent or drastically restrict sintering even in a high temperature lean atmosphere by entrapping platinum into the crystal of the complex oxide. As a result of the efforts to prevent mutual sintering of the complex oxides having good heat-resistance, the present invention was found to be capable of providing a catalyst having good heat-resistance for purifying an exhaust gas and capable of restricting the decrease of a specific surface area of the complex oxide. Also, as a result of the examination of a complex oxide having better heat resistance than a perovskite structure, it is a further object of the present invention to provide a catalyst having good heat-resistance, for purifying an exhaust gas which can be produced by a sol-gel method. It is still another object of the present invention to provide a catalytic support which per se has good heat resistance and hardly reacts with the Pt complex oxide. On this point, it is believed that the reason why purification performance of the complex oxide having good heat resistance drops in the course of endurance running is because the alkaline earth element in the complex oxide reacts with the catalytic carrier, and forms complex oxides such as alkali earth metal-aluminates, silicates, etc, and the crystal structure of the complex oxide changes in the course of endurance running. The gist of the present invention will be described as follows. (1) A catalyst for purifying an exhaust gas which is characterized by a mixture of a complex oxide, comprising platinum and at least one member selected from the group consisting of alkaline earth metal elements and lanthanide elements which is produced by a sol-gel method, and a catalytic support oxide being a complex oxide comprising one member (M) selected from the group of alumina, silica, titania, and zirconia, and comprising further (X) an alkaline earth metal element or a lanthanide element,the mole ratio for (X) and (M) in the support being 1:0.3 ≥ X:M ≥ 1:20. (2) A catalyst for purifying an exhaust gas according to item (1), wherein said complex oxide having good heat-resistance comprises at least one member of a platinum complex oxide selected from the group of complex oxides expressed by chemical structural formulas X 4 PtO 6 (X = Ca, Sr, Ba, Mg), X' 2 Pt 2 O 7 (X' = Sc, La, Pr), SrX"PtO 6 (X" = Co, Ni, Cu), Ba 2 ZPtO 6 (Z = Pr, Ce) and Ba 8 Y 3 Pt 4 O 17.5 . (3) A catalyst for purifying an exhaust gas according to item (1), wherein the complex oxide having good heat-resistance further comprises Cu. (4) A catalyst for purifying an exhaust gas according to item 3), wherein the complex oxide having good heat-resistance comprises at least one member of platinum complex oxide selected from the group expressed by Ba 4 CuPt 2 O 9 , Ba 2 Y 2 CuPtO 8 , Ba 2 Y 2 Cu 2 PtO 10 , Ba 3 Y 2 Cu 2 PtO 10 , Ba 1.3 Sr 1.7 Y 2 Cu 2 PtO 10 , Ba 2 Ho 2 CuPtO 8 , Ba 3 Ho 2 Cu 2 PtO 10 , Ba 2 Er 2 CuPtO 8 , and Ba 2 Er 2 Cu 2 PtO 10 . (5) A process for producing a catalyst for purifying an exhaust gas according to any of items 1 to 4, wherein said process comprises the steps of calcining, drying and calcination. (6) A process for producing a catalyst for purifying an exhaust gas according to any of items 1 to 5, wherein the mixture of the complex oxide having good heat resistance and the catalytic support is prepared by powder addition of the catalytic support complex oxide or solution addition of the metal ions of the catalytic support complex oxide. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT According to the present invention, a catalyst for purifying an exhaust gas having good heat-resistance of not lower than 1,000°C can be accomplished by constituting the catalyst with a complex oxide comprising platinum and at least one element of alkaline earth metal element or a lanthanide element so as to entrap platinum into the crystal of the complex oxide. Preferably Mg, Ca, Sr and Ba are used as the alkaline earth metal element and La, Ce, Pr, etc. as the lanthanide element. Al 2 O 3 , SiO 2 , TiO 2 , ZrO 2 , are part of the catalytic support oxide, and the catalytic support oxide is mixed with the complex oxide having good heat-resistance and can thus prevent sintering of the complex oxides due to their mutual contact. As a result, the decrease of the specific surface area of the complex oxides can be restricted, and the drop of the catalysis can be prevented. Next, the technical features of the present invention will be explained below. First, the method of adding the catalytic support oxide is carried out by powder addition of oxide or by solution addition of the metal ions of the catalytic support complex oxide. These complex oxides are platinum complex oxides having good heat-resistance expressed by the following items (1) to (4) as the principal structures thereof. (1) X 4 PtO 6 (X = Ca, Sr, Ba, Mg), (2) X'Pt 2 O 7 (X' = Sc, La, Pr); in this case, Sc, La and Pr from a pyrochlore series (X'Pt 2 O 7 ). (3) SrX"PtO 4 (X" = Co, Ni, Cu); these compounds correspond to the compounds of Sr 4 PtO 6 whose one Sr is substituted. (4) Ba 2 ZPtO 6 (Z = Pr, Ce), (5) Ba 8 Y 3 Pt 4 O 17.5 . Next, the method of securing the specific surface area of the complex oxide having good heat-resistance according to the present invention will be explained. Since the specific surface area of this complex oxide is proportional to the number of Pt ions existing on the surface (that is, surface area), the greater the specific surface area of the complex oxide, the better. As a method of increasing this specific surface area, the present invention prepares all the complex oxides by a sol-gel method. A vapor phase decomposition method may be also used besides this sol-gel method. By the way, the object of the addition of the catalytic support oxide in the present invention is primarily directed to prevent sintering of the Pt complex oxide. In the inventions according to claim 2, Ba(Sr), Cu, Pt, X (X = Y, lanthanides, inclusive of the case where X does not exist), can be used as a Pt complex oxide having further improved durability for the Pt complex oxides Ba 4 PtO 6 , etc., described above. Further preferably, at least one of the platinum complex oxides expressed by Ba 4 CuPt 2 O 9 , Ba 2 Y 2 CuPtO 8 , Ba 2 Y 2 Cu 2 PtO 10 , Ba 3 Y 2 Cu 2 PtO 10 , Ba 1.3 Sr 1.7 Y 2 Cu 2 PtO 10 , Ba 2 Ho 2 CuPtO 8 , Ba 2 Ho 2 Cu 2 PtO 10 , Ba 2 Er 2 CuPtO 8 , Ba 3 Er 2 Cu 2 PtO 10 , etc., is used. When the Pt complex oxide described above and Aℓ 2 O 3 are mixed, the alkaline earth metal element in the complex oxide and Aℓ 2 O 3 react and form alkaline earth metal-aluminates. Therefore, Pt precipitates during the endurance running, but the claimed invention prevents this problem. This also means that the alkali earth metal-SiO 2 , TiO 2 and ZrO 2 complex oxides are formed in the cases of SiO 2 , TiO 2 and ZrO 2 , too. Since the catalyst of the present invention not only has good heat-resistance but contains in advance the alkaline earth metal element, it does not easily react with the alkaline earth metal element in itself. As a result, durability of the catalyst can be improved. According to the invention, the catalytic support itself comprises a complex oxide. Because the reaction between the alkaline earth metal element in the Pt complex oxide and the catalytic support can be restricted, durability of the catalyst for purifying an exhaust gas can be improved. The heat-resistance of the catalyst support itself can be improved, too. The catalytic support of complex oxide according to the present invention comprises Aℓ 2 O 3 , SiO 2 , TiO 2 or ZrO 2 and the alkaline earth metal element or the lanthanide element. Its composition ratio is X:M = 1:0.3 to 1:20 and preferably, X:M = 1:0.5 to 1:4 (X = alkaline earth metal, lanthanide,. M = Aℓ, Si, Ti, Zr). Hereinafter, the present invention will be explained in further detail with reference to Examples thereof. EXAMPLES Comparative Example 1 This Example relates to a Ba 4 PtO 6 /Aℓ 2 O 3 catalyst. The method of preparing the catalyst of this Example was as follows. First, 20g of PtCℓ 4 was dissolved in 200g of ethanol to prepare an Al solution. After 400g of an ethanol solution (10 wt%) of Na ethoxide C 2 H 5 ONa was added to this A1 solution, the mixed solution was refluxed for 5 hours in a nitrogen atmosphere to obtain a Pt alkoxide B1 solution. To this B1 solution was added 541g of an ethanol solution (10 wt%) of a Ba ethoxide Ba(OC 2 H 5 ) 2 so as to obtain a C1 solution. A gel-like precipitate was then obtained by adding 120g of water to this C1 solution. After centrifugal separation and washing were repeated, the reaction product was dried for twenty-four hours at 120°C and was calcined at 1100°C for 5 hours to obtain D1 powder. The catalyst of Comparative Example 1 was obtained by sufficiently mixing 2.7g of this D1 powder and 47.3g of γ-Al 2 O 3 powder. Comparative Example 2 This Example relates to a Ca 4 PtO 6 /Aℓ 2 O 3 catalyst. The method of preparing the catalyst in this Example was as follows. First, 37.3g of PtCℓ 4 was dissolved in 370g of ethanol to prepare an A2 solution, and 310g of an ethanol solution (10 wt%) of Na ethoxide C 2 H 5 ONa was added to this A2 solution. The mixed solution was refluxed in a nitrogen atmosphere for 5 hours to obtain a Pt alkoxide B2 solution. To this B2 solution was added 577g of an ethanol solution (10 wt%) of Ca ethoxide Ca (OC 2 H 5 ) 2 to obtain a C2 solution. Next, a gel-like precipitate was obtained by adding 239g of deionized water to this C2 solution. After centrifugal separation and washing were repeated, the reaction product was dried for twenty-four hours at 120°C and was calcined at 1100°C for 5 hours to obtain D2 powder. The catalyst of Comparative Example 2 was obtained by sufficiently mixing 1.45g of this D2 powder and 48.55g of γ-Al 2 O 3 powder. Comparative Example 3 This Example relates to La 2 Pt 2 O 7 /ZrO 2 catalyst. The method of preparing the catalyst of this Example was as follows. First, 43.1g of PtCℓ 4 was dissolved in 430g of ethanol to obtain an A3 solution. To this A3 solution was added 400g of an ethanol solution (10 wt%) of Na ethoxide C 2 H 5 ONa, and the mixed solution was refluxed for 5 hours in a nitrogen atmosphere to obtain a Pt alkoxide B3 solution. 350g of an ethanol solution (10 wt%) of La ethoxide La(OC 2 H 5 ) 3 was mixed with this B3 solution to obtain a C3 solution. A gel-like precipitate was then obtained by adding 160g of deionized water to this C3 solution. After centrifugal separation and washing were repeated, the reaction product was dried at 120°C for twenty-four hours and was then calcined at 1100°C for 5 hours to obtain D3 powder. The catalyst of Comparative Example 3 was obtained by sufficiently mixing 1.25g of this D3 powder and 48.75g of ZrO 2 powder. Comparative Example 4 This Example relates to Sr 3 NiPtO 6 /ZrO 2 catalyst. The method of preparing the catalyst of this Example was as follows. First, 27.5g of PtCℓ 4 and 10.6g of NiCℓ 2 were dissolved in 400g of ethanol to obtain an A4 solution. To this A4 solution was added 200g of an ethanol solution (10 wt%) of Na ethoxide C 2 H 5 ONa, and the mixed solution was refluxed for 5 hours in a nitrogen atmosphere to obtain a Pt alkoxide B4 solution. Next, 435g of an ethanol solution (10 wt%) of Sr ethoxide Sr(OC 2 H 5 ) 2 was added to this B4 solution to obtain a C4 solution. A gel-like precipitate was then obtained by adding 180g of deionized water to this C4 solution. After centrifugal separation and washing were repeated, the reaction product was dried at 120°C for twenty-four hours and was then calcined at 1100°C for 5 hours to obtain D4 powder. The catalyst of Comparative Example 4 was obtained by sufficiently mixing 1.97g of this D4 powder and 48.03g of ZrO 2 powder. Comparative Example 5 This Example relates to a Ba 2 PrPtO 6 /ZrO 2 catalyst. The method of preparing the catalyst of this Example was as follows. First, 23.9g of PtCℓ 4 and 26.4g of PtCℓ 3 ·7H 2 O were dissolved in 500g of ethanol to obtain an A5 solution. To this A5 solution was added 338g of an ethanol solution (10 wt%) of Na ethoxide C 2 H 5 ONa, and the mixed solution was refluxed for 5 hours in a nitrogen atmosphere to obtain a Pt alkoxide B5 solution. Next, 322g of an ethanol solution (10 wt%) of Ba ethoxide Ba(OC 2 H 5 ) 2 to this B5 solution to obtain a C5 solution. A gel-like precipitate was obtained by adding 153g of deionized water to this C5 solution. After centrifugal separation and washing were repeated, the reaction product was dried at 120°C for twenty-four hours and was then calcined at 1100°C for 5 hours to obtain D5 powder. The catalyst of Comparative Example 5 was obtained by sufficiently mixing 2.26g of this D5 powder and 47.74g of ZrO 2 powder. Comparative Example 6 This Example relates to Ba 4 PtO 6 catalyst. The catalyst of Example 6 was D1 powder of Example 1 previously mentioned. Comparative Example 7 This Comparative Example relates to Pt/Aℓ 2 O 3 catalyst. The method of preparing the catalyst of this Comparative Example was as follows. First, 50g of γ-Aℓ 2 O 3 (specific surface area 150 m 2 /g) was placed into 313g of an aqueous dinitrodiamine Pt solution (0.2 wt% in terms of Pt), and the mixture was stirred. After water was evaporated, the reaction product was dried at 120°C for twenty-four hours and was then calcined at 500°C for 1 hour to obtain the catalyst of Comparative Example 7. Comparative Example 8 This Comparative Example 8 relates to LaCo 0.9 Pt 0.1 O 3 catalyst. The method of preparing the catalyst of this Comparative Example was as follows. First, 65.0g of La(NO 3 ) 3 ·6H 2 O was dissolved in 150 mℓ of deionized water, and 34.7g of Co(CH 3 COO) 2 ·4H 2 O was dissolved in 150 mℓ of deionized water. Next, 75.7g of citric acid was dissolved in 360 mℓ of deionized water. These three kinds of aqueous solutions were mixed and furthermore, 58.6g of an aqueous dinitrodiamine Pt solution (5 wt% in terms of Pt) was added and mixed. This mixed aqueous solution was evaporated, dried and solidified (for about 4 hours) over a bath at 80°C inside an evaporator under a reduced pressure. Next, while pressure reduction was being done using a vacuum pump, the reaction product was heated to 350°C and was then calcined at 750°C for 3 hours to obtain the catalyst of Comparative Example 8. When each catalyst of Comparative Examples 1 to 8 was analyzed by X-ray diffraction, the diffraction peak of the Pt metal could not be observed in all of the catalysts. Next, the method of evaluating performance of the catalysts of Comparative Examples 1 to 8 will be explained. After each of the catalysts was pressed by CIP (cold isostatic press), it was pulverized and was shaped to 1.7 to 1.0 mm. Before the performance evaluation, each testpiece was subjected to endurance treatment at 1,000°C for 10 hours. Table 1 represents the endurance treatment gas composition (corresponding to air-fuel ratio A/F = 16). O 2 CO C 3 H 6 NO CO 2 H 2 O N 2 1.50% 0.10% 0.057% 0.25% 14.5% 10% balance Next, the catalytic conversion efficiency was measured by using a normal pressure flow type reactor. Table 2 represents the composition of the measuring gas of catalytic conversion efficiency (corresponding to a stoichiometric composition) at this time. O 2 CO C 3 H 6 NO CO 2 H 2 O N 2 0.30% 0.20% 0.067% 0.20% 14.5% 10% balance The flow rate of the measuring gas of catalytic conversion efficiency at this time was 5 ℓ/min. The weight of the catalyst of Comparative Examples 1 to 7 was 2.0g. The weight of the catalyst of Comparative Example 8 was 6.17g so that the Pt weight contained in the catalyst became equal to that of Comparative Example 6. The catalyst bed temperature was set to 500°C, 450°C, 350°C, 300°C and 250°C, and the catalytic conversion efficiency under the steady state was measured at each of these temperatures. The definition of the catalytic conversion efficiency this time was as follows. catalytic conversion efficiency = [(inlet gas concentration - outlet gas concentration)/inlet gas concentration] × 100 Next, the temperature at which the catalytic conversion efficiency reached 50% (which will be hereinafter called "THC - T 50 " (C 3 H 6 component), "NO - T 50 " (NO component) was determined by plotting the catalyst bed temperature and the catalytic conversion efficiency. The results were altogether tabulated in Table 3. catalyst Pt amount HC-T 50 NO-T 50 Example 1 Ba 4 PtO 6 /Aℓ 2 O 3 1.25 wt% 399°C 388°C Example 2 Ca 4 PtO 6 /Aℓ 2 O 3 " 410°C 417°C Example 3 La 2 Pt 2 O 7 /ZrO 2 " 398°C 382°C Example 4 Sr 3 NiPtO 6 /ZrO 2 " 414°C 422°C Example 5 Ba 2 PrPtO 6 /ZrO 2 " 411°C 424°C Example 6 Ba 4 PtO 6 23.2 wt% 350°C 348°C Comp. Example 1 Pt/Aℓ 2 O 3 1.25 wt% 445°C 463°C Comp. Example 2 LaCo 0.9 Pt 0.1 O 3 7.52 wt% 404°C 421°C It can be understood clearly from Comp. Examples 1 to 6 that these catalysts had a lower THC purification temperature and a lower NO purification temperature after endurance treatment than the conventional catalyst according to Comparative Example 7. In the catalyst according to the Comparative Example 7, the higher the durability temperature, the more its sintering was promoted. Sintering was particularly remarkable in the high temperature oxidizing atmosphere, and it was extremely difficult to prevent this sintering. As an example of measurement of the Pt particle size of this catalyst of Comparative Example 1 after endurance treatment, it was as great as about 55 nm when measured by a half value width method of X-ray diffraction described already. On the other hand, the perovskite type complex oxide of the afore-mentioned reference such as the catalyst of Comparative Example 8 is expressed by the general formula ABO 3 , where A is a member selected from the group consisting of the lanthanoid elements and the alkaline earth metal elements, and B is platinum alone or a mixture of platinum and a transition metal. Further, the catalytic component includes complex oxides having a so-called "perovskite type structure analogous structure" such as an ilmenite type, a BaNi-O 3 type, a K 2 NiF 4 type, and so forth. In these complex oxides, too, Pt is entrapped into the structure. However, at a temperature of 900°C, the structure itself of these complex oxides is decomposed, so that Pt is extruded and can no longer exist stably. Example 1 This example relates to Ba 4 PtO 6 /BaO-Aℓ 2 O 3 (Ba:Aℓ = 1:2) catalyst. First, 26.9g of Ba(OC 3 H 7 ) 3 and 80g of Aℓ(OC 3 H 7 ) 3 were dissolved in 350g of isopropanol and the mixed solution was heated and refluxed at 70°C for 3 hours over a water bath to prepare an A7 solution. While the A7 solution was being stirred, 56g of deionized water was added little by little to obtain a B7 precipitate. After being aged at 70°C for 5 hours, the B7 precipitate was dried under reduced pressure. The dried product was treated at 500°C for 1 hour in a nitrogen stream. Subsequently, the product was treated at 1,100°C for 5 hours to obtain C7 powder of a complex oxide. An E7 solution was prepared by dissolving 20g of PtCℓ 4 in 200g of ethanol. After 400g of an ethanol solution (10 wt%) of C 2 H 5 ONa was added to the E7 solution described above, the mixture was refluxed for 5 hours to obtain a F7 solution. Next, 541g of an ethanol solution (10 wt%) of Ba(OC 2 H 5 ) 2 was added to the F7 solution to obtain a G7 solution. 120g of deionized water was added to the G6 solution to obtain a gel-like precipitate. After centrifugal separation and washing were repeated, the precipitate was dried at 120°C for twenty-four hours, and was treated at 1,000°C for 5 hours in air to obtain H7 powder. The catalyst of Example 1 was obtained by sufficiently mixing 47.3g of C7 powder and 2.7g of H7 powder. Example 2 This Example relates to Ba 4 PtO 6 /BaO-Aℓ 2 O 3 (Ba:Aℓ = 1:12) catalyst. First, 8.9g of Ba(OC 3 H 7 ) 3 and 80g of Aℓ(OC 3 H 7 ) 3 were dissolved in 507g of isopropanol, and the mixture was heated and refluxed at 70°C for 3 hours over a water bath to prepare an A8 solution. While the A8 solution was being stirred, 89g of deionized water was added little by little to obtain a B8 precipitate. After being aged at 70°C for 5 hours, the B8 precipitate was dried under reduced pressure. The dried product was treated at 500°C for 1 hour in a nitrogen stream. Subsequently, the product was treated at 1,100°C for 5 hours in air to obtain C8 powder of a complex oxide. The catalyst of Example 2 was obtained by sufficiently mixing 47.3g of C8 powder and 2.7g of H7 powder. Example 3 This Example relates to Sr 3 CoPtO 6 /BaO-Aℓ 2 O 3 (Ba:Aℓ = 1:2) catalyst. First, 27.5g of PtCℓ 4 and 10.6g of CoCℓ 2 were dissolved in 400g of ethanol to prepare an E9 solution. Next, 200g of an ethanol solution (10 wt%) of C 2 H 5 ONa was added to the E9 solution and the mixed solution was refluxed for 5 hours in a nitrogen atmosphere to prepare a F9 solution. A G9 solution was prepared by mixing 435g of an ethanol solution (10 wt%) of Sr(OC 2 H 5 ) 2 to the F9 solution. Next, 180g of deionized water was added to the G9 solution to obtain a precipitate. After centrifugal separation and washing were repeated, the precipitate was dried at 120°C for twenty-four hours and was then calcined at 500°C for 3 hours to obtain H9 powder. The catalyst of Example 3 was obtained by sufficiently mixing 48.05g of C7 powder and 1.95g of H9 powder. Example 4 This Example relates to Ba 4 PtO 6 /MgO-Aℓ 2 O 3 (Mg:Aℓ = 1:2) catalyst. First, 8.5g of Mg(OC 3 H 7 ) 3 and 144g of Aℓ(OC 3 H 7 ) 3 were dissolved in 633g of isopropanol and the mixed solution was heated and refluxed at 70°C for 3 hours over a water bath to prepare an A10 solution. While the A10 solution was being stirred, 101g of deionized water was added little by little to obtain a B10 precipitate. After being aged at 70°C for 5 hours, the B10 precipitate was dried under reduced pressure. The dried product was then treated at 500°C for one hour in a nitrogen stream. Subsequently, the product was treated at 110°C for 5 hours in air to obtain C10 powder of a complex oxide. The catalyst of Example 4 was obtained by sufficiently mixing 47.3g of C10 powder and 2.7g of H7 powder. Example 5 This Example relates to La 2 Pt 2 O 7 /La 2 O 3 -Aℓ 2 O 3 (La:Aℓ = 1:1) catalyst. First, 64.1g of La(OC 2 H 5 ) 3 and 47.8g of Aℓ(OC 3 H 7 ) 3 were dissolved in 280g of isopropanol and the mixed solution was heated and refluxed at 70°C for 3 hours over a water bath to prepare an A11 solution. While the A11 solution was being stirred, 51g of deionized water was added little by little to obtain a B11 precipitate. After being aged at 70°C for 5 hours, the B11 precipitate was dried under reduced pressure. The dried product was treated at 500°C for 1 hour in a nitrogen stream. Subsequently, the product was treated at 1,100°C for 5 hours in air to obtain C11 powder of a complex oxide. 43.1g of PtCℓ 4 was dissolved in 430g of ethanol to prepared an E11 solution, and 400g of an ethanol solution (10 wt%) of C 2 H 5 ONa was added to this E11 solution. The mixed solution was refluxed for 5 hours to prepare a F11 solution. Further, 350g of an ethanol solution (10 wt%) of La(OC 2 H 5 ) 3 was mixed with this F11 solution to prepare a G11 solution. Next, 160g of deionized water was added to the G11 solution to obtain a precipitate. After centrifugal separation and washing were repeated, the precipitate was dried at 120°C for twenty-four hours and was then calcined at 500°C for 3 hours to obtain H11 powder. The catalyst of this Example 5 was obtained by sufficiently mixing 48.75g of C11 powder and 1.25g of H11 powder. Example 6 This Example relates to an Sr 3 CoPtO 6 /CaO-SiO 2 (Ca:Si = 1:0.3) catalyst. First, 85.5g of Ca(OC 2 H 5 ) 2 and 45.6g of Si(OC 2 H 5 ) 4 were dissolved in 526g of isopropanol, and the mixed solution was heated and refluxed at 70°C for 3 hours over a water bath to prepare an A12 solution. While the A12 solution was being stirred, 79g of deionized water was added little by little to obtain a B12 precipitate. After being aged at 70°C for 5 hours, the precipitate was dried under reduced pressure. The dried product was treated at 500°C for 1 hour in a nitrogen stream. Subsequently, the product was treated at 1,100°C for 5 hours in air to obtain C12 powder of a complex oxide. The catalyst of Example 6 was obtained by sufficiently mixing 48.05g of C12 powder and 1.95g of H9 powder. Example 7 This Example relates to Sr 3 CoPtO 6 /BaO-TiO 2 (Ba:Ti = 1:1) catalyst. First, 48.7g of Ba(OC 2 H 5 ) 2 and 48.9g of Ti(OC 2 H 5 ) were dissolved in 257g of isopropanol, and the mixed solution was heated and refluxed at 70°C for 3 hours over a water bath to prepare an A13 solution. While the A13 solution was being stirred, 47g of deionized water was added little by little to obtain a B13 precipitate. After being aged at 70°C for 5 hours, the precipitate was dried under reduced pressure. The dried product was treated at 500°C for 1 hour in a nitrogen stream. Subsequently, the product was treated at 1,100°C for 5 hours to obtain C13 powder of a complex oxide. The catalyst of Example 7 was obtained by sufficiently mixing 48.0g of C13 powder and 1.25g of H9 powder. Example 8 This Example relates to Sr 3 CoPtO 6 /SrO-ZrO 2 (Sr:Zr = 1:1) catalyst. First, 39.1g of Sr(OC 2 H 5 ) 2 and 59.8g of Zr(OC 2 H 5 ) 4 were dissolved in 257g of isopropanol, and the mixed solution was heated and refluxed at 70°C for 3 hours to prepare an A14 solution. While the solution was being stirred, 47g of deionized water was added little by little to obtain a B14 precipitate. After being aged at 70°C for 5 hours, the precipitate was dried under reduced pressure. The dried product was treated at 500°C for 1 hour in a nitrogen atmosphere. Subsequently, the product was treated at 1,100°C for 5 hours in air to obtain C14 powder of a composite oxide. The catalyst of Example 8 was obtained by sufficiently mixing 48.05g of C14 powder and 1.25g of H9 powder. Comp. Example 11 This Comp. Example relates to Sr 3 CoPtO 6 /Aℓ 2 O 3 catalyst. The catalyst of Comp. Example 11 was obtained by sufficiently mixing 48.05g of γ-Aℓ 2 O 3 and 1.95g of H9 powder. Comp. Example 12 This Comp. Example relates to Sr 3 CoPtO 6 /SiO 2 catalyst. The catalyst of Comp. Example 12 was obtained by sufficiently mixing 48.05g of SiO 2 and 1.95g of H9 powder. Comp. Example 13 This Comp. Example 11 relates to Sr 3 CoPtO 6 /TiO 2 catalyst. The catalyst of Comp. Example 13 was obtained by sufficiently mixing 48.05g of TiO 2 and 1.95g of H9 powder. Comp. Example 14 This Comp. Example 12 relates to Sr 3 CoPtO 6 /ZrO 2 catalyst. The catalyst of Comp. Example 14 was obtained by sufficiently mixing 48.05g of ZrO 2 and 1.95g of H9 powder. Performance evaluation of the catalysts of Examples 1 to 8 and Comparative Examples 9 - 12 was subjected in the same way as in Comp. Examples 1 to 8. The results were altogether tabulated in Table 4. The following is obvious from Table 4 for Examples 1 to 8. When the complex oxide according to the present invention is used as the catalytic support of the precious metal complex oxide catalyst, both the THC purification temperature and the NO purification temperature can be lowered more greatly than those of the oxides (Aℓ 2 O 3 , SiO 2 , TiO 2 , ZrO 2 ) according to the prior art. A preferred composition ratio capable of reducing the THC purification temperature and the No purification temperature after endurance treatment is X:M = 1:0.5 to 1:4 (where X is the alkaline earth metal or the lanthanides and M is Aℓ, Si, Ti and Zr). In the catalysts according to the present invention, the diffraction peak of the Pt metal cannot be observed by X-ray diffraction even after endurance treatment at 1,000°C, and the catalysts keep stably the form of the complex oxides. This presumably improves extremely highly durability performance of the catalysts of the present invention. In the cases of Comp. Examples 1 and 11 to 14, the existence of the Ba-aluminates, the Sr-aluminates, the Sr-silicates, etc., can be observed by XRD analysis after endurance treatment. These compounds are formed as the result of the reaction between the precious metal complex oxide and the catalytic support oxide. As a result, the precious metal complex oxide becomes unstable and presumably becomes more likely to be sintered or to suffer structural break-down. In other words, in the complex oxide catalytic support according to the present invention, those metal elements which are likely to be entrapped into the catalytic support oxides according to the prior art are in advance made complex. In consequence, the reaction between the precious metal complex oxide and the catalytic support oxide can be restricted, so that durability can be improved. Comp. Example 15 This Example relates to a Ba 8 Y 3 Pt 4 O 17.5 /Aℓ 2 O 3 catalyst. First, 37.5g of Ba(OC 2 H 5 ) 2 , 13.9g of Y(OC 2 H 5 ) 3 and 32.4g of Pt(C 5 H 8 O 2 ) 2 were dissolved in 370g of isopropanol, and the mixed solution was refluxed at 70°C for 3 hours on a water bath to prepare an A21 solution. While this A21 solution was being stirred, 31g of deionized water was added little by little to obtain a B21 precipitate. After being aged at 70°C for 5 hours, the B21 precipitate was dried under reduced pressure. The resulting dried product was treated at 500°C for 1 hour in a nitrogen stream. Subsequently, the product was treated at 1,000°C for 5 hours in air to obtain C21 powder of complex oxide. The catalyst of Comp. Example 15 was obtained by sufficiently mixing 1.95g of C21 powder and 48.05g of γ-Aℓ 2 O 3 . Comp. Example 16 This Example relates to Ba 4 CuPt 2 O 9 /Aℓ 2 O 3 , catalyst. First, 39.6g of Ba(OC 2 H 5 ) 2 , 11.4g of Cu(C 5 H 8 O 2 ) 2 and 34.3g of Pt(C 5 H 8 O 2 ) 2 were dissolved in 366g of isopropanol, and the mixed solution was refluxed at 70°C for 3 hours over a water bath to prepare an A22 solution. While the A22 solution was being stirred, 28g of deionized water was added little by little to obtain a B22 precipitate. After being aged at 70°C for 5 hours, the B22 precipitate was dried under reduced pressure. The dried product was treated at 500°C for 1 hour in a nitrogen stream. Subsequently, the product was treated at 1,000°C for 5 hours in air to obtain C22 powder of complex oxide. The catalyst of Comp. Example 16 was obtained by sufficiently mixing 1.84g of C22 powder and 48.26g of γ-Aℓ 2 O 3 . Comp. Example 17 This Example relates to Ba 2 Y 2 CuPtO 8 /Aℓ 2 O 3 catalyst. First, 27.1g of Ba(OC 2 H 5 ) 2 , 26.7g of Y(OC 2 H 5 ) 3 , 15.6g of Cu(C 5 H 8 O 2 ) 2 and 23.4g of Pt(C 5 H 8 O 2 ) 2 were dissolved in 429g of isopropanol, and the mixed solution was refluxed at 70°C for 3 hours over a water bath to prepare an A23 solution. While the A23 solution was being stirred, 34g of deionized water was added little by little to obtain a B23 precipitate. After being aged at 70°C for 5 hours, the B23 precipitate was dried under reduced pressure. The dried product was treated at 500°C for 1 hour in a nitrogen stream. Subsequently, the product was treated at 1,000°C for 5 hours in air to obtain C23 powder of complex oxide. The catalyst of Comp. Example 17 was obtained by sufficiently mixing 2.68g of C23 powder and 48.32g of γ-Aℓ 2 O 3 . Comp. Example 18 This Example relates to a Ba 1.3 Sr 1.7 Y 2 Cu 2 PtO 10 /Aℓ 2 O 3 catalyst. First, 23.0g of Ba(OC 2 H 5 ) 2 , 15.3g of Sr(OC 2 H 5 ) 2 , 22.7g of Y(OC 2 H 5 ) 3 , 26.5g of Cu(C 5 H 8 O 2 ) 2 and 19.9g of Pt(C 5 H 8 O 2 ) 2 were dissolved in 486g of isopropanol, and the mixed solution was refluxed at 70°C for 3 hours over a water bath to prepare an A24 solution. While the solution was being stirred, 37g of deionized water was added little by little to obtain a B24 precipitate. After being aged at 70°C for 5 hours, the B24 precipitate was dried under reduced pressure. The dried product was treated at 500°C for 1 hour in a nitrogen stream. Subsequently, the product was treated at 1,000°C for 5 hours to obtain complex oxide C24 powder. The catalyst of Comp. Example 18 was obtained by sufficiently mixing 3.16g of C24 powder and 46.84g of γ-Aℓ 2 O 3 . Comp. Example 19 This Example relates to a Ba 2 Ho 2 CuPtO 8 /Aℓ 2 O 3 catalyst. First, 22.9g of Ba(OC 2 H 5 ) 2 , 13.2g of Cu(C 5 H 8 O 2 ) 2 and 19.8g of Pt(C 5 H 8 O 2 ) 2 were dissolved in 363g of isopropanol, and the mixed solution was refluxed at 70°C for 2 hours to prepare an A25 solution. While the A25 solution was being stirred, 22.3g of Ho(NO 3 ) 3 ·5H 2 O was added, and the mixed solution was refluxed at 70°C for 2 hours over a water bath to prepare a D25 solution. Next, 29g of deionized water was added little by little to the D25 solution to obtain a B25 precipitate. After being aged at 70°C for 5 hours, the precipitate was dried under reduced pressure. The dried product was treated at 500°C for 1 hour in a nitrogen stream. Subsequently, the product was treated at 1,000°C for 1 hour in air to obtain complex oxide C25 powder. The catalyst of Camp. Example 19 was obtained by sufficiently mixing 3.18g of C25 powder and 46.82g of γ-Aℓ 2 O 3 . Comp. Example 20 This Example relates to a Ba 2 Er 2 CuPtO 8 /Aℓ 2 O 3 catalyst. First, 20.6g of Ba(OC 2 H 5 ) 2 , 11.9g of Cu(C 5 H 8 O 2 ) 2 and 17.8g of Pt(C 5 H 8 O 2 ) 2 were dissolved in 435g of isopropanol, and the mixed solution was refluxed at 70°C for 2 hours over a water bath to prepare an A26 solution. While the A26 solution was being stirred, 41.8g of Er(NO 3 ) 3 6H 2 O was added, and the mixed solution was refluxed at 70°C for 2 hours over a water bath to prepare a B26 solution. Next, 33g of deionized water was added little by little to the D26 solution to obtain a C26 precipitate. After being aged at 70°C for 5 hours, the C26 precipitate was dried under reduced pressure. The dried product was treated at 500°C for 1 hour in a nitrogen stream. Subsequently, the product was treated at 1,000°C for 5 hours to obtain complex oxide D26 powder. The catalyst of Comp. Example 20 was obtained by sufficiently mixing 3.53g of D26 powder and 46.47g of γ-Aℓ 2 O 3 . Next, performance evaluation of the catalysts of Comp. Examples 15 to 20 and Comparative Example 21 was subjected in the same way as in Comparative Examples 1 to 8. The results were altogether tabulated in Table 5. catalyst Pt amount HC-T 50 NO-T 50 Comp. Ex. 15 Ba 2 Y 3 Pt 4 O 17.5 /Aℓ 2 O 3 1.25wt% 393°C 382°C Comp. Ex. 16 Ba 4 CuPt 2 O 9 /Aℓ 2 O 3 " 414°C 405°C Comp. Ex. 17 Ba 2 Y 2 CuPtO 8 /Aℓ 2 O 3 " 402°C 391°C Comp. Ex. 18 Ba 1.3 Sr 1.7 Y 2 Cu 2 PtO 10 /Aℓ 2 O 3 " 398°C 388°C Comp. Ex. 19 Ba 2 Ho 2 CuPtO 8 /Aℓ 2 O 3 " 407°C 399°C Comp. Ex. 20 Ba 2 Er 2 CuPtO 8 /Aℓ 2 O 3 " 404°C 396°C Comp. Example 21 Pt/Aℓ 2 O 3 " 445°C 463°C The following is obvious from Table 5 for Comp. Examples 15 to 21. When the complex oxide is used for the precious metal complex oxide catalyst, the THC purification temperature and the NO purification temperature after durability use can be lowered more greatly than the oxides (Aℓ 2 O 3 , SiO 2 , TiO 2 , ZrO 2 ) according to the prior art. Since the catalyst for purifying exhaust gas according to the present invention achieves high temperature stability by entrapping platinum into the crystal of the complex oxide, it has durability capable of withstanding the use at a temperature not lower than 1,000°C. Further, sintering due to the mutual contact of the complex oxides having good heat resistance can be prevented by mixing the catalytic support oxide with the complex oxide having good heat resistance, and the decrease of the specific surface area of the complex oxide having good heat resistance can be restricted. Accordingly, durability can be further improved.

Claims: A catalyst for purifying an exhaust gas characterized by a mixture of a complex oxide comprising platinum and at least one member selected from the group consisting of alkaline earth metal elements and lanthanide elements which is produced by a sol-gel method, and a catalytic support oxide being a complex oxide comprising one member (M) selected from the group of alumina, silica, titania, and zirconia, and comprising further (X) an alkaline earth metal element or a lanthanide element, the mole ratio for (X) and (M) in the support being 1 : 0.3 ≥ X : M ≥ 1 : 20. A catalyst for purifying an exhaust gas according to claim 1, wherein said complex oxide having good heat-resistance comprises at least one member of a platinum complex oxide selected from the group of complex oxides expressed by chemical structural formulas X 4 PtO 6 (X = Ca, Sr, Mg), X' 2 Pt 2 O 7 (X' = La, Pr), SrX"PtO 6 (X" = Co, Ni, Cu), Ba 2 ZPtO 6 (Z = Pr, Ce) and Ba 8 Y 3 Pt 4 O 17.5 . A catalyst for purifying an exhaust gas according to claim 1, wherein said complex oxide having good heat-resistance further comprises Cu. A catalyst for purifying an exhaust gas according to claim 3, wherein said complex oxide having good heat-resistance comprises at least one member of platinum complex oxide selected from the group expressed by Ba 4 CuPt 2 O 9 , Ba 2 Y 2 CuPtO 8 , Ba 2 Y 2 Cu 2 PtO 10 , Ba 3 Y 2 Cu 2 PtO 10 , Ba 1.3 Sr 1.7 Y 2 Cu 2 PtO 10 , Ba 2 Ho 2 CuPtO 8 , Ba 3 Ho 2 Cu 2 PtO 10 , Ba 2 Er 2 CuPtO 8 and Ba 2 Er 2 Cu 2 PtO 10 .

Inventors: MURACHI MIKIO, SUGIYAMA MASAHIKO, YAMASITA KOITI, MURACHI, MIKIO, SUGIYAMA, MASAHIKO, YAMASITA, KOITI
Applicants: TOYOTA MOTOR CO LTD, TOYOTA JIDOSHA KABUSHIKI KAISHA
Application year: 1996
Main classification: B01J23
IPC codes: B01D53, B01J23