Novel crystalline metal-organic microporous materials

Abstract: Novel metal-organic microporous materials are prepared in solution using mild reaction conditions from a metal or metalloid ion with a ligand containing multidentate functional groups in the presence of a templating agent. The resultant microporous materials are useful in the purification of liquids and gases.

Description: Introduction This invention is directed to the composition, method of preparation, and uses of new, novel crystalline microporous solids which are prepared in a solution reaction by admixing certain metal salts with an organic ligand containing multidentate functional groups or a mixture of organic ligands containing multidentate and monodentate functional groups in the presence of a templating agent. The materials may also be prepared in a viscous matrix whereby large crystals of the microporous solid can be advantageously prepared. Optionally, the materials may be advantageously prepared to contain voids by removing template materials after preparation. The resultant microporous materials are useful for the adsorption of molecules or ions of impurities from liquids and gases. Through the careful selection of metal ion, ligand, and templating agent, rigid and stable microporous materials can be prepared having desired pore size openings useful for particular tasks. BACKGROUND OF THE INVENTION The utility of microporous solids such as the zeolite-type aluminosilicates, aluminophosphates, and their metal substituted derivatives is well established in industrial processes involving ion-exchange, separation, and catalysis (U.S. Pat. No. 4,310,440, U.S. Pat. No. 4,440,871, and U.S. Pat. No. 4,500,651). The widespread application of these so called zeolitic materials is due to their ability to include molecules and ions in a selective and reversible fashion, a property conferred by the stability and rigidity of their porous frameworks. Although most of these frameworks are based on the oxide of the metal, a recent invention showed that similar materials can be produced from the sulfide and selenide of the metal (U.S. Pat. No. 4,880,761). While the syntheses of oxide zeolites and their sulfide and selenide analogues are well known, the capability of rationally designing the shape, size, and function of the pores of zeolites or microporous materials is lacking. In particular, the method for zeolite synthesis requires the mixing of an alkali metal hydroxide with aqueous solutions of silicate and aluminate anions to form a hydrated aluminosilicate gel of complex composition. Zeolitic solids are obtained by the subsequent heating of the gel (up to 200 °C) under water vapor pressure conditions in a closed vessel. The complexity of the gel precludes any possibility of controlling the structural organization of the zeolitic solid. Thus, zeolite synthesis has remained as much an art as a science (See A. Dyer, "An Introduction to Zeolite Molecular Sieves" John Wiley and Sons, New York (1988); R. M. Barrer, "Hydrothermal Chemistry of Zeolites" Academic Press, New York (1982); J. M. Newsam, "The Zeolite Cage Structure", Science, 231:1093 (1986)). An extensive amount of work has been done on the synthesis of metal-organic solids, though none of the resulting materials possess microporous properties comparable to those obtained through the use of this invention. For example, Toshitake Iwamoto, "Inclusion Compounds of Multi-Dimensional Cyanometal Complex Hosts" Inclusion Compounds , Vol. 5 (Eds.: J. L. Atwood, J. E. D. Davies, D. D. Macnicol), Oxford University Press (1991) p. 177, and references therein, provides a review on the Hoffmann-type compounds and their derivatives, where 1D, 2D and 3D frameworks are produced by linking one metal atom M to another M' to form M-CN-M' type solids. Other reports are B.F. Hoskins and R. Robson, "Design and Construction of a New Class of Scaffolding-Like Materials Comprising Infinite Polymeric Frameworks of 3D-Linked Molecular Rods. A Reappraisal of the Zn(CN) 2 and Cd(CN) 2 Structures and the Synthesis and Structure of the Diamond-Related Frameworks [N(CH 3 ) 4 ][Cu I Zn II (CN) 4 ] and Cu I [4,4',4'',4'''-tetracyanotetraphenylmethane]-BF 4 · x C 6 H 5 NO 2 ," J. Am. Chem. Soc., 112:1546 (1990); B.F. Hoskins and R. Robson, "Infinite Polymeric Frameworks Consisting of Three-Dimensionally Linked Rod-Like Segments," J. Am. Chem. Soc. 111:5962 (1989); S.R. Batten, B.F. Hoskins, and R. Robson, "3D Knitting Patterns. Two Independent, Interpenetrating Rutile-Related Infinite Frameworks in the Structure of Zn[C(CN) 3 ] 2 ," J. Chem. Soc., Chem. Commun. 445 (1991); B.F. Abrahams, B.F. Hoskins, D.M. Michall, and R. Robson, "Assembly of Porphyrin Building Blocks into Network Structures with Large Channels," Nature 369:727 (1994); G.B. Gardner, D. Venkataraman, J. S. Moore, and S. Lee, "Spontaneous Assembly of a Hinged Coordination Network," Nature 374:792 (1995); O. M. Yaghi, G. Li, and T. L. Groy, "Preparation of Single Crystals of Coordination Solids in Silica Gels: Synthesis and Structure of Cu II (1,4-C 4 H 4 N 2 ) (C 4 O 4 )(OH 2 ) 4 ," J. Solid State Chem., 256 (1995). O. M. Yaghi and G. Li, "Presence of Mutually Interpenetrating Sheets and Channels in the Extended Structure of Cu(4,4'-bipyridine)Cl," Angew . Chem., Int. Ed. Engl ., 207 (1995). All metal-organic solids prepared to date are either (a) one dimensional (1D), two dimensional (2D), or three dimensional (3D) dense solids having no porosity or (b) solids that are made by the formation of linkages between the metal, M, and a bifunctional, trifunctional, or tetrafunctional organic ligand, L, containing monodentate functional groups, around a templating agent, T. One possible structure, having a diamond-like framework, is shown as an example of the effect of the templating agent (Formula 1). Formula 1 below represents a schematic illustration of the assembly of a metal-organic framework in the presence of a templating agent, T. Here a fragment of a solid is shown with the small spheres representing a metal ion, M, capable of binding to four ligands in a tetrahedral geometry, while the dark rod represents a bifunctional organic ligand, L, capable of binding metal ions at its ends and encapsulating the templating agent within a pore. Metal-organic solids may assume other framework types, depending on the preferred coordination geometry of the metal ion and the organic ligand. Microporosity in the aforementioned metal-organic solids has not been demonstrated due to at least two problems. First, the templating agent interacts strongly with the metal-organic framework, thus making it impossible to remove the templating agent from the solid without altering or destroying the framework. In that way, the ability of the solid to adsorb another molecule, or readsorb the templating agent to yield the original material, is lost. So, it is desirable to keep the templating agent-framework interactions to a minimum while maximizing the strength of intra-framework bonding between the organic ligand and the metal ion. Secondly, for many metal-organic solids the pores are not occupied by templating agents, but with interpenetrated frameworks. Formula 2 below shows an example where one framework has interpenetrated another identical framework. Extensive framework interpenetration can cause the porous space of a single framework to be filled, resulting in a dense solid that will not adsorb molecules or ions. In Formula 2 below, two interpenetrated diamond-like frameworks (distinguished with light and dark shades) are shown. Each framework standing alone forms a porous structure. However, interpenetration in this case fills those pores. For a given solid, as the number of interpenetrating frameworks increases, the material becomes more densly packed, and thus, the channels and pores present in the material become smaller, perhaps to the extent that the material loses porosity to even the smallest adsorbing species. Attempts to rationally design microporous materials have resulted in nonporous solids due to interpenetration (see O. Ermer and L. Lindenberg, "Double-Diamond Inclusion Compounds of 2,6-Dimethylideneadamantane-1,3,5,7-tetracarboxylic Acid" Helv. Chim. Acta 74:825 (1991); O. Ermer, "Five-Fold Diamond Structure of Adamantane-1,3,5,7-tetracarboxylic Acid" J. Am. Chem. Soc. 110:3747 (1988); S.R. Batten, B.F. Hoskins, and R. Robson, "3D Knitting Patterns. Two Independent, Interpenetrating Rutile-Related Infinite Frameworks in the Structure of Zn[C(CN) 3 ] 2 ," J. Chem. Soc., Chem. Commun. 445 (1991)). Therefore, this invention details the first successful rational synthetic approach to the formation of crystalline metal-organic solids that show effective microporous activity, having (a) structural integrity preserved in the absence of a templating agent and (b) no or minimal amounts of interpenetrating frameworks so that channels and pores that can accomodate transfer and binding of molecules or ions exist within the solid. Given the great impact of zeolitic materials on the global economy, it would be a significant improvement in the art if a method existed for rationally designing crystalline microporous materials. The method of this invention provides to the art such a process. By the use of the subject invention, crystalline microporous materials can be prepared which have controlled pore distributions and sizes, and which are useful in a variety of industries. These materials form by the solution reaction of a metal ion selected from the group consisting of: Mg, Ca, Sr, Ba, Sc, Y, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, Au, Zn, Cd, Hg, Al, Ga, In, Tl, Si, Ge, Sn, Pb, As, Sb, and Bi, with a ligand having multidentate functional groups, and a templating agent. It is believed that the invention of the present application provides to the art a novel method for the preparation of microporous materials which are useful in industries such as catalysis, gas purification, ion-exchange, the removal of impurities from industrial aqueous streams, the removal of impurities from hydrocarbon streams, the removal of color from paper mill waste waters, the removal of metals from aqueous solutions, the removal of metals from hydrocarbon solutions, the removal of hydrocarbon contaminants from aqueous systems, the removal of hydrocarbon contaminants from hydrocarbon systems, filtration, and seperation materials, and the like. It is accordingly an object of this invention to provide to the art a method for the preparation of novel microporous materials. It is a still further object of this invention to provide to the art a method for the preparation of novel microporous materials in a simple straightforward manner which method would allow control over the resultant final product. It would be a further improvement in the art if the synthesis of microporous materials could be performed under room temperature or mild reaction conditions (relative to those used to synthesize oxide microporous materials). It would be a still further improvement in the art if the microporous materials could be prepared from simple metal salts and organic ligands. It would be an even further improvement in the art if the aforementioned synthetic method could result in the formation of crystalline microporous materials, having no pore or channel inhomogeneity. Further objects of this invention will appear hereinafter. Brief Description of the Drawings Fig. 1 is a thermal gravametric analysis trace of CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 •2/3 NC 5 H 5 . Fig. 2 is a FTIR spectrum of CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 with cyanobenzene absorbed into the framework. Fig. 3 is a FTIR spectrum of CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 with nitrobenzene absorbed into the framework. Fig.4 is an overlay of FTIR spectra of CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 and CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 with C 6 D 6 absorbed into the framework. Fig. 1-4 will be more fully explained in the examples contained herein. The Invention The basic process of the invention used for the preparation of the crystalline or microcrystalline microporous materials of this invention comprises the step of admixing: A. a solution containing one or more metal salts containing metal ions from the group consisting of: Mg 2+ , Ca 2+ , Sr 2+ , Ba 2+ , Sc 3+ , Y 3+ , Ti 4+ , Zr 4+ , Hf 4+ , V 4+ , V 3+ , V 2+ , Nb 3+ , Ta 3+ , Cr 3+ , Mo 3+ , W 3+ , Mn 3+ , Mn 2+ , Re 3+ , Re 2+ , Fe 3+ , Fe 2+ , Ru 3+ , Ru 2+ , Os 3+ , Os 2+ , Co 3+ , Co 2+ , Rh 2+ , Rh + , Ir 2+ , Ir + , Ni 2+ , Ni + , Pd 2+ , Pd + , Pt 2+ , Pt + , Cu 2+ , Cu + , Ag + , Au + , Zn 2+ , Cd 2+ , Hg 2+ , Al 3+ , Ga 3+ , In 3+ , Tl 3+ , Si 4+ , Si 2+ , Ge 4+ , Ge 2+ , Sn 4+ , Sn 2+ , Pb 4+ , Pb 2+ , As 5+ , As 3+ , As + , Sb 5+ , Sb 3+ , Sb + , and Bi 5+ , Bi 3+ , Bi + ; along with the corresponding metal salt counteranion with, B. one or more ligands, said ligands having at least one of: i. an alkyl group substructure, having from 1 to 10 carbon atoms; ii. an aryl group substructure, having from 1 to 5 phenyl rings; iii. an alkyl or aryl amine substructure, consisting of alkyl groups having from 1 to 10 carbon atoms or aryl groups having from 1 to 5 phenyl rings; said ligand having bound thereto at least one multidentate functional group "X", which is covalently bound to the substructure of the ligand, and wherein X is selected from the group consisting of: CO 2 H, CS 2 H, NO 2 , SO 3 H, Si(OH) 3 , Ge(OH) 3 , Sn(OH) 3 , Si(SH) 4 , Ge(SH) 4 , Sn(SH) 4 , PO 3 H, AsO 3 H, AsO 4 H, P(SH) 3 , As(SH) 3 ; CH(RSH) 2 , C(RSH) 3 , CH(RNH 2 ) 2 , C(RNH 2 ) 3 , CH(ROH) 2 , C(ROH) 3 , CH(RCN) 2 , C(RCN) 3 , wherein R is an alkyl group having from 1 to 5 carbon atoms, or an aryl group consisting of 1 to 2 phenyl rings; and, CH(SH) 2 , C(SH) 3 , CH(NH 2 ) 2 , C(NH 2 ) 3 , CH(OH) 2 , C(OH) 3 , CH(CN) 2 , and C(CN) 3 ; in the presence of; C. a templating agent, selected from the group consisting of: a. alkyl amines and their corresponding alkyl ammonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms (and their corresponding ammonium salts); b. aryl amines and their corresponding aryl ammonium salts having from 1 to 5 phenyl rings; c. alkyl phosphonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; d. aryl phosphonium salts, having from 1 to 5 phenyl rings; e. alkyl organic acids and the corresponding alkyl organic anions (and salts) containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; f. aryl organic acids and their corresponding aryl organic anions and salts, having from 1 to 5 phenyl rings; g. aliphatic alcohols, containings linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; h. aryl alcohols having from 1 to 5 phenyl rings; i. inorganic anions from the group consisting of: sulfate, nitrate, nitrite, sulfite, bisulfite, phosphate, hydrogen phosphate, dihydrogen phosphate, diphosphate, triphosphate, phosphite, chloride, chlorate, bromide, bromate, iodide, iodate, carbonate, bicarbonate, and the corresponding acids and salts of the aforementioned inorganic anions, j. ammonia, carbon dioxide, methane, oxygen, argon, nitrogen, ethylene, hexane, benzene, toluene, xylene, chlorobenzene, nitrobenzene, naphthalene, thiophene, pyridine, acetone, 1,2-dichloroethane, methylenechloride, tetrahydrofuran, ethanolamine, triethylamine, and trifluoromethylsulfonic acid. The invention described herein addresses the above by teaching a method for the synthesis of crystalline microporous materials by the appropriate combination of solutions of a metal salt(s), an organic ligand(s), and a templating agent, to give structurally stable and rigid materials having a desired pore shape, size, and function. Microporous materials hereunder can be obtained only by the appropriate choice of metal ion, organic ligand(s), and templating agent. The synthesis of the microporous materials described in this invention utilizes not only desirable properties (symmetry, rigidity, and functionality) of organic ligands and metal ions, but also it employs ligands that possess multidentate functional groups, which impart stability and rigidity to the resulting microporous metal-organic solids, while inhibiting the interpenetration of frameworks. The Ligands For the purposes of this invention, a multidentate functional group is defined as a moiety bound to an organic ligand or amine ligand substructure, L, and in which the moiety has the potential to have at least two atoms, X, from the general formula, A(RX) 2 , either (a) bound to a single metal ion, or (b) bound to two metal ions. A specific example of a multidentate functional group having the A(RX) 2 formula is CH(CH 2 OH) 2 , where A = CH, R = CH 2 , and X = O, as shown in Formulas 3a and 3b below: A multidentate functional group according to the above definition can also be represented by the formula AX 2 . A specific example of a multidentate functional group having the AX 2 formula is the carboxylate anion, CO 2 - . The carboxylate anion has the potential to bind to a metal ion in either a bidentate (a) or monodentate (b) fashion, as shown in Formula 4. It is not a requirement of this invention that multidentate functional groups always bind in a multidentate fashion to afford stable microporous materials. Rather, this invention teaches that the use of ligands that contain multidentate functional groups affords rigid and stable metal-organic microporous materials. For the purposes of this invention, an organic ligand or amine ligand substructure is defined as being an alkyl or cycloalkyl group, consisting of 1 to 20 carbon atoms, an aryl group, consisting of 1 to 5 phenyl rings, or an alkyl or aryl amine, consisting of alkyl or cycloalkyl groups having from 1 to 20 carbon atoms or aryl groups consisting of 1 to 5 phenyl rings, and in which multidentate functional groups are covalently bound to the substructure of the ligand. Some examples of organic ligand or amine ligand substructures are given in Formula 5 below: where X is a multidentate functionality selected from the group consisting of CO 2 H, CS 2 H, NO 2 , SO 3 H, Si(OH) 3 , Ge(OH) 3 , Sn(OH) 3 , Si(SH) 4 , Ge(SH) 4 , Sn(SH) 4 , PO 3 H, AsO 3 H, AsO 4 H, P(SH) 3 , As(SH) 3 , CH(RSH) 2 , C(RSH) 3 , CH(RNH 2 ) 2 , C(RNH 2 ) 3 , CH(ROH) 2 , C(ROH) 3 , CH(RCN) 2 , C(RCN) 3 , wherein R is an alkyl group having from 1 to 5 carbon atoms, or an aryl group consisting of 1 to 2 phenyl rings; and, CH(SH) 2 , C(SH) 3 , CH(NH 2 ) 2 , C(NH 2 ) 3 , CH(OH) 2 , C(OH) 3 , CH(CN) 2 , and C(CN) 3 . This invention further teaches that the cycloalkyl or aryl substructure may consist of 1 to 5 rings that consist either of all carbon or a mixture of carbon, with nitrogen, oxygen, sulfur, boron, phosphorous, silicon and aluminum atoms making up the ring. Some examples of such substructures are given in Formula 6 below: Preferred ligands of the invention are those that contain carboxylic acid functional groups. A preferred ligand of the invention is 1,3,5-benzenetricarboxylic acid (BTC), also called trimesic acid (Formula 8a). Examples given later in this invention detail how this trifunctional bidentate ligand has been used to synthesize rigid and stable metal-organic microporous materials using the metal ions cobalt(II) and zinc(II). Another aspect of this invention teaches that crystalline metal-organic microporous materials can be synthesized by the addition of a solution of a metal salt to a solution containing an appropriate blend of ligands, some of which contain multidentate functional groups, as defined previously, and others of which contain monodentate functional groups, in the presence of a suitable templating agent. For the purposes of this invention, a monodentate functional group is defined as a moiety bound to an organic ligand or amine ligand substructure, L, as defined previously, which can form only one bond to a metal ion. According to this definition, a ligand may contain one or more monodentate functional groups. For example, cyclohexylamine and 4,4'-bipyridine are ligands that contain monodentate functional groups, as shown in Formula 7, since each functional group is capable of binding to only one metal ion. According to this definition, cyclohexylamine is a monofunctional ligand containing a monodentate functional group and 4,4'-bipyridine is a difunctional ligand containing two monodentate functional groups. Specific examples of ligands containing monodentate functional groups are pyridine, which is a monofunctional ligand, hydroquinone, which is a difunctional ligand, and 1,3,5-tricyanobenzene, which is a trifunctional ligand. Examples of ligands having monodentate functional groups that can be blended with ligands that contain multidentate functional groups to make microporous materials in the presence of a suitable metal ion and a suitable templating agent are: A. Amines that contain alkyl or cycloalkyl groups, containing from 1 to 20 carbon atoms, or aryl groups, containing from 1 to 5 phenyl rings. Examples of monofuntional amines are methylamine, ethylamine, n-propylamine, iso-propylamine, n-butylamine, sec-butylamine, iso-butylamine, tert-butylamine, n-pentylamine, neo-pentylamine, n-hexylamine, pyrrolidine, 3-pyrroline, piperidine, cyclohexylamine, morpholine, pyridine, pyrrole, aniline, quinoline, isoquinoline, 1-azaphenanthrene, and 8-azaphenanthrene. Examples of difunctional and trifunctional amines are 1,4-diaminocyclohexane, 1,4-diaminobenzene, 4,4'-bipyridyl, imidazole, pyrazine, 1,3,5-triaminocyclohexane, 1,3,5-triazine, and 1,3,5-triaminobenzene. B. Alcohols that contain alkyl or cycloalkyl groups, containing from 1 to 20 carbon atoms, or aryl groups, containing from 1 to 5 phenyl rings. Examples of monofuntional alcohols are methanol, ethanol, n-propanol, iso-propanol, allyl alcohol, n-butanol, iso-butanol, sec-butanol, tert-butanol, n-pentanol, iso-pentanol, sec-pentanol, neo-pentanol, n-hexanol, cyclohexanol, phenol, benzyl alcohol, and 2-phenylethanol. Examples of difunctional and trifunctional alcohols are 1,4-dihydroxycyclohexane, hydroquinone, catechol, resorcinol, 1,3,5-trihydroxybenzene, and 1,3,5-trihydroxycyclohexane. C. Ethers that contain alkyl or cycloalkyl groups, containing from 1 to 20 carbon atoms, or aryl groups, containing from 1 to 5 phenyl rings. Examples of ethers are diethyl ether, furan, and morpholine. D. Thiols that contain alkyl or cycloalkyl groups, containing from 1 to 20 carbon atoms, or aryl groups, containing from 1 to 5 phenyl rings. Examples of monofuntional thiols are thiomethane, thioethane, thiopropane, thiocyclohexane, thiophene, benzothiophene, and thiobenzene. Examples of difunctional and trifunctional thiols are 1,4-dithiocyclohexane, 1,4-dithiobenzene, 1,3,5-trithiocyclohexane, and 1,3,5-trithiobenzene. E. Nitriles that contain alkyl or cycloalkyl groups, containing from 1 to 20 carbon atoms, or aryl groups, containing from 1 to 5 phenyl rings. Examples of monofuntional nitriles are acetonitrile, propanenitrile, butanenitrile, n-valeronitrile, benzonitrile, and p-tolunitrile. Examples of difunctional and trifunctional nitriles are 1,4-dinitrilocyclohexane, 1,4-dinitrilobenzene, 1,3,5-trinitrilocyclohexane, and 1,3,5-trinitrilobenzene. F. inorganic anions from the group consisting of: sulfate, nitrate, nitrite, sulfite, bisulfite, phosphate, hydrogen phosphate, dihydrogen phosphate, diphosphate, triphosphate, phosphite, chloride, chlorate, bromide, bromate, iodide, iodate, carbonate, bicarbonate, thiocyanide and isonitrile, and the corresponding acids and salts of the aforementioned inorganic anions. Formula 8 gives a specific example in which a metal ion, cobalt(II), a templating agent, pyridine, a ligand containing multidentate functional groups, BTC, and a ligand containing a monodentate functional group, pyridine, were combined to give a crystalline metal-organic microporous material. The reaction of BTC, L 1 , with Co 2+ , M, gave a material composed of Co-BTC 2D-sheets, with pyridine, L 2 , bound axially to the metal ion. Specific interactions between the pyridine ligands produce a strong interaction, resulting in a rigid 3D structure. The stacking of the Co-BTC sheets in the crystal produce alternating Co-BTC and pyridine layers leading to voids where templating agents, T, and other adsorbed species are accommodated. Therefore, in this example pyridine is used as a pillar or spacer between the Co-BTC sheets. In this specific embodiment of the invention, pyridine was used both as the monodentate ligand and the templating agent. The consideration of other possible coordination modes of BTC points to a large number of possible structural variations. In addition, one can take advantage of metal ion coordination geometries other than octahedral, such as tetrahedral, square planar, linear, trigonal and trigonal bipyramidal. It is understood that the ligands possessing multidentate functional groups bring with them corresponding counter cations, such as H + , Na + , K + , Mg 2+ , Ca 2+ , Sr 2+ , ammonium ion, alkylsubstituted ammonium ions, and arylsubstituted ammonium ions, or counter anions, such as F - , Cl - , Br - , I - , ClO - , ClO 2 - , ClO 3 - , ClO 4 - , OH - , NO 3 - , NO 2 - , SO 4 2- , SO 3 2- , PO 4 3- , and CO 3 2- . The Metal Ions The crystalline microporous materials of this invention can be synthesized using metal ions having distinctly different coordination geometries, in combination with a ligand possessing multidentate functional groups, and a suitable templating agent. Metal-organic microporous solids have been prepared using a metal ion that prefers octahedral coordination, cobalt(II), and a metal ion that prefers tetrahedral coordination, zinc(II), in the presence of the BTC ligand and a ligand containing a monodentate functional group. Therefore, it is reasonable to assume that stable metal-organic microporous materials can be made using metal ions from the following list: Mg 2+ , Ca 2+ , Sr 2+ , Ba 2+ , Sc 3+ , Y 3+ , Ti 4+ , Zr 4+ , Hf 4+ , V 4+ , V 3+ , V 2+ , Nb 3+ , Ta 3+ , Cr 3+ , Mo 3+ , W 3+ , Mn 3+ , Mn 2+ , Re 3+ , Re 2+ , Fe 3+ , Fe 2+ , Ru 3+ , Ru 2+ , Os 3+ , Os 2+ , Co 3+ , Co 2+ , Rh 2+ , Rh + , Ir 2+ , Ir + , Ni 2+ , Ni + , Pd 2+ , Pd + , Pt 2+ , Pt + , Cu 2+ , Cu + , Ag + , Au + , Zn 2+ , Cd 2+ , Hg 2+ , Al 3+ , Ga 3+ , In 3+ , Tl 3+ , Si 4+ , Si 2+ , Ge 4+ , Ge 2+ , Sn 4+ , Sn 2+ , Pb 4+ , Pb 2+ , As 5+ , As 3+ , As + , Sb 5+ , Sb 3+ , Sb + , and Bi 5+ , Bi 3+ , Bi + ; along with the corresponding metal salt counteranion. As used herein, the term metal ion refers to both metal and metalloid ions. Generally, the metal ions useful in this invention include: Sc 3+ , Ti 4+ , V 4+ ,V 3+ ,V 2+ ,Cr 3+ ,Mo 3+ ,Mn 3+ ,Mn 2+ ,Fe 3+ ,Fe 2+ ,Ru 3+ ,Ru 2+ ,Os 3+ ,Os 2+ ,Co 3+ , Co 2+ , Rh 2+ , Rh + , Ir 2+ , Ir + , Ni 2+ , Ni + , Pd 2+ , Pd + , Pt 2+ , Pt + , Cu 2+ , Cu + , Ag + , Au + , Zn 2+ , Cd 2+ , Al 3+ , Ga 3+ , In 3+ , Ge 4+ , Ge 2+ , Sn 4+ , Sn 2+ , Pb 4+ , Pb 2+ , Sb 5+ , Sb 3+ , Sb + , and Bi 5+ , Bi 3+ , Bi + ; along with the corresponding metal salt counteranion. A preferred group of metal ions for use in this invention includes: Sc 3+ ,Ti 4+ , V 4+ , V 3+ , Cr 3+ , Mo 3+ , Mn 3+ , Mn 2+ , Fe 3+ , Fe 2+ , Co 3+ , Co 2+ , Ni 2+ , Ni + , Cu 2+ , Cu + , Ag + , Zn 2+ , Cd 2+ , Al 3+ , Sn 4+ , Sn 2+ , and Bi 5+ , Bi 3+ , Bi + ; along with the corresponding metal salt counteranion. More preferably the metal ions useful in this invention are selected from the group consisting of: Mn 3+ , Mn 2+ , Fe 3+ , Fe 2+ , Co 3+ , Co 2+ , Ni 2+ , Ni + , Cu 2+ , Cu + , Ag + , Zn 2+ , Cd 2+ , along with the corresponding metal salt counteranion. Most preferably the metal ions useful in this invention are selected from the group consisting of: Fe 3+ , Fe 2+ , Co 3+ , Co 2+ , Ni 2+ , Ni + , Cu 2+ , Cu + ,Zn 2+ , along with the corresponding metal salt counteranion. An especially preferred group of metals for use in this invention is: Co 3+ , Co 2+ , Ni 2+ , Ni + , Zn 2+ , along with the corresponding metal salt counteranion, The Templating Agent The templating agents employed in this invention are added to the reaction mixture for the purpose of occupying the pores in the resulting crystalline metal-organic microporous materials. Examples of possible templating species are: a. alkyl amines and their corresponding alkyl ammonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; b. aryl amines and their corresponding aryl ammonium salts having from 1 to 5 phenyl rings; c. alkyl phosphonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; d. aryl phosphonium salts, having from 1 to 5 phenyl rings, e. alkyl organic acids and their corresponding salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; f. aryl organic acids and their corresponding salts, having from 1 to 5 phenyl rings; g. aliphatic alcohols, containings linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; h. aryl alcohols having from 1 to 5 phenyl rings; i. inorganic anions from the group consisting of sulfate, nitrate, nitrite, sulfite, bisulfite, phosphate, hydrogen phosphate, dihydrogen phosphate, diphosphate, triphosphate, phosphite, chloride, chlorate, bromide, bromate, iodide, iodate, carbonate, bicarbonate, and the corresponding acids and salts of said inorganic anions; j. ammonia, carbon dioxide, methane, oxygen, argon, nitrogen, ethylene, hexane, benzene, toluene, xylene, chlorobenzene, nitrobenzene, naphthalene, thiophene, pyridine, acetone,1,2-dichloroethane, methylenechloride, tetrahydrofuran, ethanolamine, triethylamine,and trifluoromethylsulfonic acid. The Process The synthesis of the rigid and stable microporous materials of this invention can be carried out under extremely mild reaction conditions. In most cases, the reagents are combined into a solution, either aqueous or nonaqueous, with synthetic reaction temperatures ranging from 0°C to 100°C (in an open beaker). In other cases, solution reactions are carried out in a closed vessel at temperatures from 25°C to 300°C. In either case, large single crystals or microcrystalline microporous solids are formed. In the preparation of the materials of this invention, the reactants are generally added in a mole ratio of 1:10 to 10:1 metal ion to ligand containing multidentate functional groups. Preferably, the metal ion to ligand containing multidentate functional groups is 1: 3 to 3:1, and most preferably from 1:2 to 2:1. The amount of templating agent is not critical, and in fact, templating agent can in some circumstances be employed as the solvent in which the reaction takes place. Templating agent can accordingly be employed in great excess without interfering with the reactions of this invention and the preparation of the microporous materials. When using a ligand containing monodentate functional groups in combination with the metal ion and the ligand containing multidentate functional groups, the, ligand containing monodentate functional groups can be utilized in great excess. In certain circumstances the ligand containing monodentate functional groups can be utilized as the solvent in which the reaction takes place. In addition, in certain circumstances the templating agent and the ligand containing monodentate functional groups may be identical. An example of a templating agent which is a ligand containing monodentate functional groups is pyridine. The preparation of the microporous materials of this invention is carried out in either an aqueous or non-aqueous system. The solvent may be polar or nonpolar as the case may be, and as stated earlier, the solvent may be the required templating agent, or the optional ligand containing a monodentate functional group. Examples of non-aqueous solvents include n-alkanes, such as pentane, hexane, benzene, toluene, xylene, chlorobenzene, nitrobenzene, cyanobenzene, aniline, naphthalene, naphthas, n-alcohols such as methanol, ethanol, n-propanol, isopropanol, acetone, 1,2,-dichloroethane, methylene chloride, chloroform, carbon tetrachloride, tetrahydrofuran, dimethylformamide, dimethylsulfoxide, thiophene, pyridine, ethanolamine, triethylamine, ethylenediamine, and the like. Those skilled in the art will be readily able to determine an appropriate solvent based on the starting reactants, and the choice of solvent is not believed to be critical in obtaining the microporous materials of this invention. To aid in the formation of large single crystals of microporous materials, suitable for single crystal x-ray structural characterization, the solution reaction is performed in the presence of viscous materials, generally polymeric additives. Specific additives include polyethylene oxide, polymethylmethacrylic acid, silica gels, agar, fats, and collogens, which aid in achieving high yields and pure crystalline products. The growth of large single crystals of microporous materials leads to unambiguous characterization of the microporous framework. Large single crystals of microporous materials may be useful for magnetic and electronic sensing applications. Examples The following examples of this invention are meant as an illustration of the microporous materials that are obtained using the synthetic strategy defined by this invention, and are not meant to limit in any way the scope of the invention: EXAMPLE 1 This example describes the synthesis of a stable microporous material from an ethanol/1,2-dichloroethane solution matrix at room temperature by the simple combination of a cobalt(II) salt with two select ligands, BTC, which possesses multidentate functional groups, and pyridine, which possesses a monodentate functional group, in the presence of a templating agent, pyridine. Solids of Co(NO 3 ) 2 .6H 2 O (0.582 g, 2 mmol) and BTC (0.420 g, 2 mmol) were dissolved in 15 mL ethanol, then added to a 5 mL solution of polyethylene oxide (PEO) (0.250 g, MW = 100,000) in 1,2-dichloroethane. The mixture was stirred until a clear solution was obtained. This 20 mL reaction vessel was placed inside a larger vessel containing 1 mL of pyridine and the second vessel was closed. Gaseous,pyridine was diffused into the reaction solution for three days, resulting in large, pink, cubed-shaped crystals in the 20 mL reaction vessel. These were collected and washed successively with 1,2-dichloroethane, ethanol, and acetone, resulting in a yield of 0.85 g (89 % yield). The density of crystals of this material that were freshly isolated from their mother liquor was measured by the floatation method to give a value of 1.48± 0.01 g cm -3 . Elemental analysis done on crystalline samples of this material: found; C, 54.99; H, 3.82; N, 7.44; Co, 12.43%: Calculated for CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 ·2/3 NC 5 H 5 ; C, 56.11; H, 3.66; N, 7.82; Co, 12.33%. These crystals are insoluble in water and common organic solvents. The crystalline homogeneity of the microcrystalline product was confirmed by comparison of the observed (Table 1) and calculated (Table 2) x-ray powder diffraction patterns. The calculated x-ray powder diffraction pattern was produced using the single crystal data given below. An x-ray crystal analysis study was performed on a single crystal obtained from this reaction. The x-ray diffraction pattern data is given in Table 3 which revealed the presence of a porous solid represented by the formula, CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 ·2/3NC 5 H 5 . Single crystals of this material are at 20±1°C, hexagonal, space group P6 3 /mcm - D 3 / 6h (no. 193) with α = 16.711(4) Å, c = 14.189(2) Å, V = 3423(1) Å 3 , and Z = 6 {for x = 1, d calcd = 1.464 g cm -3 , µ a (MoKα - ) = 0.80 mm -1 }. A total of 1161 independent reflections having 2 (MoKα - ) < 50.7° (the equivalent of 0.8 limiting Cu Kα - spheres) were collected on a computer-controlled Nicolet autodiffractometer using full (0.90°-wide) ω scans and graphite-monochromatic MoKα - radiation. The structure was solved using "Direct Methods" techniques with the Siemens SHELXTL-PC software package as modified at Crystalytics Company. The resulting parameters have been refined to converge [ R 1 (unweighted, based on F) = 0.068 for 552 independent reflections having 2 (MoKα - ) < 50.7° and I > 3σ(I)]. Peak 2-Theta d-Space Intensity 1 12.360 7.1554 62.03 2 16.260 5.4469 10.33 3 18.420 4.8128 100.00 4 21.320 4.1642 16.75 5 22.180 4.0047 11.22 6 25.000 3.5590 73.79 7 27.340 3.2594 8.47 8 28.300 3.1510 11.52 9 29.000 3.0765 15.24 10 32.220 2.7760 10.69 11 33.660 2.6605 8.31 12 38.940 2.3110 7.40 13 41.100 2.1944 7.43 14 43.400 2.0833 8.66 h k l 2-theta d-spacing F multiplicity Lp-factor intensity -1 2 1 12.29 7.2028 219.09 12 173.5965 100.00 0 0 2 12.46 7.1055 253.49 2 168.9132 21.71 -1 3 0 16.20 5.4700 49.53 12 99.6912 2.94 -1 3 1 17.37 5.1049 39.78 24 86.6968 3.29 0 2 2 17.49 5.0699 82.02 12 85.4990 6.90 0 3 0 18.39 4.8240 374.83 6 77.3128 65.18 -1 3 2 20.49 4.3344 47.02 24 62.2186 3.30 -2 4 0 21.27 4.1778 100.05 6 57.7308 3.47 -1 2 3 21.56 4.1208 167.14 12 56.1408 18.82 -1 4 0 22.15 4.0139 67.59 12 53.2116 2.92 0 3 2 22.27 3.9911 98.57 12 52.5996 6.13 -2 4 2 24.72 3.6014 78.25 12 42.6381 3.13 0 0 4 25.06 3.5528 738.76 2 41.4670 45.26 -1 4 2 25.49 3.4948 43.16 24 40.0919 1.79 -2 5 0 26.85 3.3201 48.72 12 36.0848 1.03 -1 2 4 37.28 3.2695 143.98 12 34.9607 8.70 -1 5 0 28.26 3.1581 105.85 12 32.5500 4.38 -1 5 1 28.96 3.0829 107.47 24 30.9696 8.58 -1 3 4 29.99 2.9795 39.13 24 28.8585 1.06 -1 5 2 30.99 2.8859 40.46 24 27.0101 1.06 0 3 4 31.27 2.8607 80.76 12 26.5223 2.08 -3 6 0 32.14 2.7852 179.34 6 25.0865 4.84 -3 6 1 32.77 2.7332 74.43 12 24.1200 1.60 -1 2 5 33.30 2.6908 147.62 12 23.3457 6.11 0 5 2 33.43 2.6806 70.25 12 23.1607 1.37 -1 5 3 34.12 2.6277 74.85 24 22.2147 2.99 -3 6 2 34.59 2.5931 83.74 12 21.6064 1.82 -1 6 2 36.82 2.4411 54.56 24 19.0280 1.36 0 0 6 37.99 2.3685 467.56 2 17.8516 7.81 -2 7 0 38.86 2.3174 140.73 12 17.0444 4.05 -2 7 1 39.39 2.2872 89.58 24 16.5754 3.19 -1 2 6 39.55 2.2787 129.15 12 16.4450 3.29 -2 7 2 40.96 2.2032 114.47 24 15.3034 4.81 0 3 6 42.52 2.1261 128.33 12 14.1772 2.80 -1 5 5 42.80 2.1126 77.40 24 13.9848 2.01 -4 8 0 43.31 2.0889 175.7 6 13.6483 2.53 Cu-K(alpha) radiation, 5.00 <2-theta <50.00 Intensity = F*F*Lp*mult (scaled so that largest is 100) Only results having intensities greater or equal to 1.00 are listed Atomic Coordinates for Nonhydrogen Atoms in Crystalline CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 ·2/3NC 5 H 5 Obtained from Single Crystal x-ray analysis Atom Fractional Coordinates Eqiuvalent Isotropic Thermal Parameter, Type 10 4 x 10 4 y 10 4 z B. A 2 X 10 Co 3246(2) 0 2500 29(1) O 1 2477(7) 738(7) 2500 54(4) C 1 829(11) 0 2S00 22(6) C 2 0 -857(10) 2500 26(6) C 3 1779(15) 0 c 2500 34(6) O 2 4487(7) 1136(7) 2500 57(4) O 3 5643(6) 828(7) 2500 57(5) C 4 6023(10) 2394(10) 2500 27(5) C 5 5736(9) 3034(10) 2500 24(5) C 6 5307(8) 1370(10) 2500 29(5) N 1s 3240(10) 0 981(9) 80(10) C 1s 3557(32) -236(37) 456(26) 101(38) C 2s 3639(64) -136(126) -654(44) 156(29) C 38 3388(38) 397(32) 885(30) 94(21) C 4s 3058(30) 809(40) -444(37) 149(31) C 5s 3051(31) 752(30) 646(20) 101(22) Templating Agents Molecule 1 C 6s 455(7) 910(14) 0 125(32) Molecule 2 C 7s 6211(7) 3789(7) 0 171(388) C 8s 7122(7) 2878(7) 0 217(388) Using data from the x-ray single crystal analysis, a fragment of the structure of CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 ·2/3NC 5 H 5 was generated and shown in Formula 9 where three BTC units are coordinated to each of the Co(II) centers. Formula 9 shows a single layer of the extended porous network of CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 · 2/3 NC 5 H 5 . The hydrogen atoms on the pyridines and BTC units are omitted for clarity. The axial positions of the cobalt ions are occupied by pyridine molecules. In the crystal, the Co-BTC sheets stack along the z -axis to give alternating cobalt-carboxylate layers and pyridine layers as shown in Formula 10. Formula 10 shows a perspective drawing of the solid state structure of CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 ·2/3 NC 5 H 5 . The cobalt-carboxylate layers are shown anchored by pyridine ligands that are bound axially to cobalt. The pyridine templating agents (large spheres) reside in channels running between the layers. The cobalt-carboxylate layers are seperated by a distance of 7 Å with the bound pyridine ligands holding these layers tightly together. The remaining space between the sheets contains the pyridine templating agents which occupy the rectangular channels (7 × 10 Å). Since the layer-layer separation distance and the channel structure remain unaltered upon removal or inclusion of guests ( vide infra ), this compound is analogous to zeolites and not intercalation compounds. EXAMPLE 2 The material prepared in EXAMPLE 1, CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 . 2/3NC 5 H 5 , was also prepared in the absence of the viscous medium, PEO. Solids of Co(NO 3 ) 2 .6H 2 O (0.30 g, 1 mmol) and BTC (0.21 g, 1 mmol) were dissolved in a 20 mL reaction vessel using10 mL of ethanol. This 20 mL reaction vessel was placed inside a larger vessel containing 1 mL of pyridine and the second vessel was closed. Gaseous pyridine was allowed to diffuse into the reaction solution for three days, resulting in pink, cubed-shaped crystals in the 20 mL reaction vessel. These were collected and washed successively with ethanol and acetone, and air dried, resulting in a yield of 0.26 g (56 % yield). The x-ray powder diffraction data collected for the product of this reaction, were identical to that from the product obtained in EXAMPLE 1, CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 ·2/3NC 5 H 5 , confirming that the same crystalline microporous material was prepared regardless of the presence of the viscous PEO medium. EXAMPLE 3 The stacking of the pyridine ligands axially coordinated to the cobalt metal centers in the microporous material described in EXAMPLE 1, CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 ·2/3 NC 5 H 5 , has significant implications on the three-dimensional rigidity and stability of the material. Thermal gravimetric analysis, shown in Fig.1, performed on a crystalline sample of CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 ·2/3 NC 5 H 5 showed cleanly a weight loss of 11.7% at 190 °C, corresponding to the loss of the pyridine templating agents (2/3 NC 5 H 5 per formula unit). Decomposition of the material did not occur until 350°C, as evidenced by another weight loss of a total 45.5% corresponding to the remaining pyridine molecules bound to the cobalt metal centers (2 remaining NC 5 H 5 per formula unit). This material does not lose its crystallinity or become altered to a different framework structure upon removal of the pyridine templating agents. The material was shown to remain intact up to 200°C for as long as four hours, as confirmed by x-ray powder diffraction data. Table 4 shows that the positions of the most intense lines are unchanged from those of the unheated sample (compare with Table 1). Elemental analysis of the material heated to 200°C confirms the absence of pyridine templating agents and the retention of the axially bound pyridines (found; C, 52.38; H, 3.46; N, 6.84%: Calculated for CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 ; C, 53.66; H, 3.32; N, 6.59). Peak 2-Theta d-Space Intensity 1 10.56 8.3707 11.14 2 12.34 7.1670 55.65 3 16.54 5.3553 12.84 4 18.40 4.8179 100.00 5 21.32 4.1642 16.17 6 22.32 3.9799 10.58 7 24.90 3.5730 63.27 8 27.28 3.2665 12.34 9 28.24 3.1576 13.61 10 29.02 3.0744 13.21 11 32.16 2.7811 14.25 12 33.74 2.6544 10.27 13 34.76 2.5788 11.54 14 38.98 2.3088 10.75 15 43.40 2.0833 9.71 EXAMPLE 4 Based on infrared data and elemental analysis, solid samples of the template-free material discussed in EXAMPLE 2, CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 , selectively adsorb aromatic molecules such as benzene, nitrobenzene, cyanobenzene, and chlorobenzene, in the presence of acetonitrile, nitromethane, or dichloroethane. Such experiments were performed by suspending CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 in a solvent mixture containing an aromatic and an aliphatic component, such as C 6 H 5 CN/CH 3 CN, for approximately 30 minutes, followed by filtration and air drying. Fig. 2 shows results for the case of C 6 H 5 CN/CH 3 CN, in which the FT IR spectrum of the resulting solid showed a peak at 2236 cm -1 corresponding to the ν CN of C 6 H 5 CN, with no peak appearing at 2260 or 2300 cm -1 , where acetonitrile ν CN peaks appear. The small peaks between 2300-2400 cm -1 are due to atmospheric carbon dioxide. Fig. 3 shows results from an analogous experiment done using the C 6 H 5 NO 2 /CH 3 NO 2 mixture. In this case, the FT IR spectrum of the resulting solid showed peaks at 1526, 1354, 854, and 685 cm -1 , corresponding to that of C 6 H 5 NO 2 , with no peaks appearing at 1570, 1406, 1386, 1103, or 662 cm -1 , where nitromethane peaks appear. Fig. 4 shows results from the inclusion of benzene into CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 . Fig. 4 shows an overlay of FTIR spectra, with the thinly traced FTIR spectrum being that of CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 , and the more boldly traced FTIR spectrum being that of the material after about 30 minutes of submersion in benzene solvent. The peaks at 2282, 2268, 1332, 814 and 498 cm -1 are consistent with benzene adsorption into the microporous material. Alternatively, the pyridine templating agents can be exchanged by suspending a crystalline sample of CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 ·2/3 NC 5 H 5 at 60 °C for one day in the aromatic solvent to be adsorbed, as evidenced from the FTIR spectrum. The solid remains intact and is rigid, as evidenced from the x-ray powder diffraction pattern, which is similar to that of the original starting material. EXAMPLE 5 This example describes the synthesis of a stable microporous material in an ethanol/1,2-dichloroethane solution matrix by the simple combination of a zinc(II) salt with select ligands, BTC, which possesses multidentate functional groups, nitrate, which possesses a monodentate functional group, and triethylamine as solvent. Solids of Zn(NO 3 ) 2 .6H 2 O (0.60 g, 2 mmol) and BTC (0.21 g, 1 mmol) were dissolved in ethanol. This solution was added to a 2 mL 1,2-dichloroethane solution containing polyethylene oxide (0.12 g, MW = 100,000). Upon stirring, the solution became clear and a gel was formed. This reaction vessel was placed inside a larger vessel containing 1mL of triethylamine and the second vessel was closed. After 2-3 days, colorless cubic crystals appeared. The solid was collected and washed successively with ethanol and was air dried to give 0.30 g of product (70 % yield). Elemental analysis done on crystalline samples of this material found: C, 24.40; H, 3.20; N, 2.91: calculated for Zn 2 (C 9 H 3 O 6 )•NO 3 (H 2 O) 1 (C 2 H 5 OH) 5 ; C, 24.71; H, 2.70; N, 2.88. X-ray diffraction studies perfomed on single crystals obtained from this reaction revealed the existence of a crystalline microporous material composed of Zn 2 (C 9 H 3 O 6 )•NO 3 (H 2 O) 1 (C 2 H 5 OH) 5 . Single crystals of this material are at 20±1 °C, cubic, space group P2(1)3, with a = 14.720(2)Å. Table 5 shows the atomic coordinates for the material which were obtained from single crystal x-ray analysis. The structure of Zn 2 (C 9 H 3 O 6 )•NO 3 (H 2 O) 1 (C 2 H 5 OH) 5 is constructed from the units shown in Formula 11a, which form large rings of zinc(II) and BTC, that are fused together (Formula 11b) to give the channel network (Formula 11c). The nitrate is bound to zinc and is pointing toward the center of the channels. The templating agent, ethanol, occupies the remaining space in the channels. The ethanol templating agents and the hydrogens on the carbon atoms of the BTC ligand are omitted for clarity. Atom Fractional Coordinates Type 10 4 x 10 4 y 10 4 z ZN1 -0.18741 -0.18741 -0.18741 ZN2 -0.04685 -0.04685 -0.04685 O1 -0.20588 -0.17977 -0.05145 O2 -0.15931 -0.05261 0.02219 C1 -0.21400 -0.12517 0.00715 C2 -0.29040 -0.12700 0.07924 C3 -0.34760 -0.20374 0.07023 H3 -0.33996 -0.24655 0.02163 O1E -0.32779 -0.17555 -0.20343 C1E -0.38780 -0.06827 -0.19122 H1EA -0.44421 -0.08243 -0.22073 H1EB -0.35775 -0.02266 -0.22687 C2E -0.42678 -0.06280 -0.08996 O1S -0.55566 0.20844 -0.35979 C2S -0.46465 0.17157 -0.29759 C3S -0.45398 0.21116 -0.22956 O2S -0.56675 0.18980 -0.22085 O3S -0.56571 0.16314 -0.31344 O3 0.0494 0.0494 0.0494 EXAMPLE 6 The material prepared in EXAMPLE 5, Zn 2 (C 9 H 3 O 6 )•NO 3 (H 2 O) 1 (C 2 H 5 OH) 5 was also prepared in the absence of the viscous medium, PEO. Solids of Zn(NO 3 ) 2 .6H 2 O (0.30 g, 1 mmol) and BTC (0.105 g, 0.5 mmol) were dissolved in a 20 mL reaction vessel using 10 mL of ethanol. In another 5 mL vessel, 2 mL of triethylamine were added. The vessels were placed side-by-side in a larger container, which was then closed. Gaseous triethylamine was allowed to diffuse into the 10 mL reaction solution for one day, resulting in colorless crystals in the 20 mL reaction vessel. After three days these were collected and washed successively with ethanol and acetone, resulting in a yield of 0.18 g (80 % yield). Due to the large pore sizes in this microporous material, solvent molecules in the pores were lost very quickly, with a 30% weight loss occurring in one day. The x-ray diffraction data collected for the product of this reaction were identical to that from the product obtained in EXAMPLE 5, Zn 2 (C 9 H 3 O 6 )•NO 3 (H 2 O) 1 (C 2 H 5 OH) 5 .

Claims: A method for the preparation of microporous materials characterized by the steps of: admixing a solution containing one or more metal ions from the group consisting of: Mg 2+ , Ca 2+ , Sr 2+ , Ba 2+ , Sc 3+ , Y 3+ , Ti 4+ , Zr 4+ , Hf 4+ , V 4+ , V 3+ , V 2+ , Nb 3+ , Ta 3+ , Cr 3+ , Mo 3+ , W 3+ , Mn 3+ , Mn 2+ , Re 3+ , Re 2+ , Fe 3+ , Fe 2+ , Ru 3+ , Ru 2+ , Os 3+ , Os 2+ , Co 3+ , Co 2+ , Rh 2+ , Rh + , Ir 2+ , Ir + , Ni 2+ , Ni + , Pd 2+ , Pd + , Pt 2+ , Pt + , Cu 2+ , Cu + , Ag + , Au + , Zn 2+ , Cd 2+ , Hg 2+ , Al 3+ , Ga 3+ , In 3+ , Tl 3+ , Si 4+ , Si 2+ , Ge 4+ , Ge 2+ , Sn 4+ , Sn 2+ , Pb 4+ , Pb 2+ , As 5+ , As 3+ , As+, Sb 5+ , Sb 3+ , Sb+, and Bi 5+ , Bi 3+ , Bi+; along with the corresponding metal salt counteranion, with one or more ligands having at least one of: an alkyl group substructure, having from 1 to 10 carbon atoms; an aryl group substructure, having from 1 to 5 phenyl rings; or, an alkyl or aryl amine substructure, consisting of alkyl groups having from 1 to 10 carbon atoms or aryl groups having from 1 to 5 phenyl rings, said ligand substructure having bound thereto multidentate functional groups, X, which are covalently bound to the substructure of the ligand, wherein X is a functional group selected from the groups consisting of: CO 2 H, CS 2 H, NO 2 , SO 3 H, Si(OH) 3 , Ge(OH) 3 , Sn(OH) 3 , Si(SH) 4 , Ge(SH) 4 , Sn(SH) 4 , PO 3 H, AsO 3 H, AsO 4 H, P(SH) 3 , As(SH) 3 ; CH(SH) 2 , C(SH) 3 , CH(NH 2 ) 2 , C(NH 2 ) 3 , CH(OH) 2 , C(OH) 3 , CH(CN) 2 , C(CN) 3 , CH(RSH) 2 , C(RSH) 3 , CH(RNH 2 ) 2 , C(RNH 2 ) 3 , CH(ROH) 2 , C(ROH) 3 , CH(RCN) 2 , C(RCN) 3 , wherein R is an alkyl group having from 1 to 5 carbon atoms, or an aryl group consisting of 1 to 2 phenyl rings, in the presence of a templating agent, selected from the group consisting of: a. alkyl amines and their corresponding alkyl ammonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; b. aryl amines and their corresponding aryl ammonium salts having from 1 to 5 phenyl rings; c. alkyl phosphonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; d. aryl phosphonium salts, having from 1 to 5 phenyl rings, e. alkyl organic acids and their corresponding salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; f. aryl organic acids and their corresponding salts, having from 1 to 5 phenyl rings; g. aliphatic alcohols, containings linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; h. aryl alcohols having from 1 to 5 phenyl rings; i. inorganic anions from the group consisting of sulfate, nitrate, nitrite, sulfite, bisulfite, phosphate, hydrogen phosphate, dihydrogen phosphate, diphosphate, triphosphate, phosphite, chloride, chlorate, bromide, bromate, iodide, iodate, carbonate, bicarbonate, and the corresponding acids and salts of said inorganic anions; j. ammonia, carbon dioxide, methane, oxygen, argon, nitrogen, ethylene, hexane, benzene, toluene, xylene, chlorobenzene, nitrobenzene, naphthalene, thiophene, pyridine, acetone, 1,2-dichloroethane, methylenechloride, tetrahydrofuran, ethanolamine, triethylamine,and trifluoromethylsulfonic acid. The method of claim 1 characterized in that the templating agent is selected from pyridine or ethanol. The method of claim 1 characterized in that the ligand is selected from benzene-1,3,5-tricarboxylic acid, benzene-1,4-dicarboxylic acid, benzene-1,2, 4, 5-tetracarboxylic acid, adamantane-1,3,5,7-tetracarboxylic acid, and 1,1',1'',1'''-methanetetracarboxylic acid. The method of claim 1 characterized in that the microporous materials are prepared in the presence of a ligand containing one or more monodentate functional groups said ligand selected from the group consisting of: a. alkyl amines containing at least one alkyl group containing 1 to 10 carbon atoms; b. aryl amines containing from 1 to 5 phenyl rings; c. alkyl alcohols containing at least one alkyl group having from 1 to 10 carbon atoms; d. aryl alcohols containing from 1 to 5 phenyl rings; e. alkyl thiols containing at least one alkyl group having from 1 to 10 carbon atoms; f. aryl thiols containing from 1 to 5 phenyl rings; g. alkyl cyanides containing at least one alkyl group having from 1 to 10 carbon atoms; h. aryl cyanides containing from 1 to 5 phenyl rings; and i. inorganic anions from the group consisting of: sulfate, nitrate, nitrite, sulfite, bisulfite, phosphate, hydrogen phosphate, dihydrogen phosphate, diphosphate, triphosphate, phosphite, chloride, chlorate, bromide, bromate, iodide, iodate, carbonate, bicarbonate, thiocyanide, and isonitrile, and the corresponding acids and salts of said inorganic anions. The method of claim 4 characterized in that the ligand containing one or more monodentate functional groups is selected from the group consisting of: pyridine, 4,4'-bipyridine, ethylenediamine, propylenediamine, 2-aminoethanol, 3-aminopropanol, trimethylamine, triethylamine, tripropylamine, 2-aminopropane, triethanolamine, ethylbutylamine, piperidine, cyclohexylamine, 2-methylpyridine, N,N-dimethylbenzylamine, N,N-dimethylethanolamine, N,N'-dimethylpiperazine, N-methyldiethanolamine, N-methylethanolamine, N-methylpiperidine, 3-methylpiperidine, 4-methylpyridine, 1,4-diaminocyclohexane, morpholine, aniline, 1,4-diaminobenzene, 1,3,5-triaminobenzene, 1,3,5-triazine, imidazole, pyrazine, methanol, dihydroxymethane, trihydroxymethane, tetrahydroxymethane, ethanol, ethylene glycol, 1,1,2,2-tetrahydroxyethane, 1-propanol, 2-propanol, propylene glycol, 1,3-propanediol, glycerol, 1,1,3,3-tetrahydroxypropane, allyl alcohol, n-butanol, secbutanol, iso-butanol, tert-butanol, 1,4-butanediol, 1,3-butanediol, 1,1,4,4-tetrahydroxybutane, n-pentanol, sec-pentanol, iso-pentanol, tert-pentanol, 1,5-pentanediol, 1,4-pentanediol, 1,3-pentanediol, 1,3,5-trihydroxypentane, n-hexanol, sec-hexanol, iso-hexanol, tert-hexanol, 1,6-hexanediol, 1,5-hexanediol, 1,4-hexanediol, 1,3-hexanediol, 1,3,6-trihydroxyhexane, cyclohexanol, 1,4-dihydroxycyclohexane, 1,3,5-trihydroxycyclohexane, phenol, benzyl alcohol, hydroquinone, catechol, resorcinol, 1,3,5-trihydroxybenzene, 1,2,4-trihydroxybenzene, 1,2,3-trihydroxybenzene, 1,2,4,5-tetrahydroxybenzene, thiomethane, thioethane, thiopropane, thiocyclohexane, thiobenzene, 1,3-dithiopropane, 1,4-dithiobutane, 1,4-dithiobenzene, and 1,3,5-trithiobenzene, 1,4-dicyanobenzene, and 1,3,5-tricyanobenzene. The method according to claim 1 in characterized in that the reaction mixture containing the microporous material product is heated from 30°C to 500°C to partially or completely remove the templating agent. A method for removing impurities from a gas or liquid which is characterized by contacting the gas or liquid containing such impurities with an effective adsorbing amount of a microporous material for a period of time sufficient to remove such impurities and then removing said microporous material from contact with said gas or liquid, said microporous material having been prepared by the steps of admixing a solution containing one or more metal ions from the group consisting of: Mg 2+ , Ca 2+ , Sr 2+ , Ba 2+ , Sc 3+ , Y 3+ , Ti 4+ , Zr 4+ , Hf 4+ , V 4+ , V 3+ , V 2+ , Nb 3+ , Ta 3+ , Cr 3+ , Mo 3+ , W 3+ , Mn 3+ , Mn 2+ , Re 3+ , Re 2+ , Fe 3+ , Fe 2+ , Ru 3+ , Ru 2+ , Os 3+ , Os 2+ , Co 3+ , Co 2+ , Rh 2+ , Rh + , Ir 2+ , Ir + , Ni 2+ , Ni + , Pd 2+ , Pd + , Pt 2+ , Pt + , Cu 2+ , Cu + , Ag + , Au + , Zn 2+ , Cd 2+ , Hg 2+ , Al 3+ , Ga 3+ , In 3+ , Tl 3+ , Si 4+ , Si 2+ , Ge 4+ , Ge 2+ , Sn 4+ , Sn 2+ , Pb 4+ , Pb 2+ , As 5+ , As 3+ , As+, Sb 5+ , Sb 3+ , Sb+, and Bi 5+ , Bi 3+ , Bi+; along with the corresponding metal salt counteranion, with one or more ligands having at least one of: an alkyl group substructure, having from 1 to 10 carbon atoms, an aryl group substructure, having from 1 to 5 phenyl rings, or, an alkyl or aryl amine substructure, consisting of alkyl groups having from 1 to 10 carbon atoms or aryl groups having from 1 to 5 phenyl rings, said ligand substructure having bound thereto multidentate functional groups, X, which are covalently bound to the substructure of the ligand, wherein X is a functional group selected from the groups consisting of: CO 2 H, CS 2 H, NO 2 , SO 3 H, Si(OH) 3 , Ge(OH) 3 , Sn(OH) 3 , Si(SH) 4 , Ge(SH) 4 , Sn(SH) 4 , PO 3 H, AsO 3 H, AsO 4 H, P(SH) 3 , As(SH) 3 ; and, CH(SH) 2 , C(SH) 3 , CH(NH 2 ) 2 , C(NH 2 ) 3 , CH(OH) 2 , C(OH) 3 , CH(CN) 2 , C(CN) 3 , CH(RSH) 2 , C(RSH) 3 , CH(RNH 2 ) 2 , C(RNH 2 ) 3 , CH(ROH) 2 , C(ROH) 3 , CH(RCN) 2 , C(RCN) 3 , wherein R is an alkyl group having from 1 to 5 carbon atoms, or an aryl group consisting of 1 to 2 phenyl rings, in the presence of a templating agent, selected from the group consisting of: a. alkyl amines and their corresponding alkyl ammonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; b. aryl amines and their corresponding aryl ammonium salts having from 1 to 5 phenyl rings c. alkyl phosphonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; d. aryl phosphonium salts, having from 1 to 5 phenyl rings, e. alkyl organic acids and their corresponding salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; f. aryl organic acids and their corresponding salts, having from 1 to 5 phenyl rings; g. aliphatic alcohols, containings linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; h. aryl alcohols having from 1 to 5 phenyl rings; i. inorganic anions selected from the group consisting of: sulfate, nitrate, nitrite, sulfite, bisulfite, phosphate, hydrogen phosphate, dihydrogen phosphate, diphosphate, triphosphate, phosphite, chloride, chlorate, bromide, bromate, iodide, iodate, carbonate, bicarbonate, and the corresponding acids and salts of said inorganic anions; j. ammonia, carbon dioxide, methane, oxygen, argon, nitrogen, ethylene, hexane, benzene, toluene, xylene, chlorobenzene, nitrobenzene, naphthalene, thiophene, pyridine, acetone,1,2-dichloroethane, methyl-enechloride, tetrahydrofuran, ethanolamine, triethylamine, and trifluoromethylsulfonic acid. A method for the adsorption of aromatic molecules from the group consisting of: benzene, nitrobenzene, cyanobenzene, chlorobenzene, toluene, ethylbenzene, aniline, o-xylene, m-xylene, p-xylene, styrene, chlorostyrene, phenol, catechol, resorcinol, biphenyl, trans-stilbene, cis-stilbine, phenylacetylene, benzoic acid, nitrotoluene, toluenesulfonic acid, phthalic acid, isophthalic acid, teraphthalic acid, benzylbromide, and benzylchloride from industrial waters and hydrocarbon streams is characterized by treating such waters and hydrocarbon streams with an effective adsorbing amount of CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 •2/3NC 5 H 5 . A method for the absorbtion of aromatic molecules from the group consisting of benzene, nitrobenzene, cyanobenzene, and chlorobenzene from industrial waters and hydrocarbon streams which is characterized by treating such waters and hydrocarbon streams with an effective adsorbing amount of CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 •2/3NC 5 H 5 . The method of claim 1 characterized in that the metal ion is added to the reaction in the form of Zn(NO 3 )•6H 2 O, the templating agent is ethanol, the ligand containing multidentate functional groups is benzene-1,3,5-tricarboxylic acid, the ligand containing monodentate functional group is nitrate, and triethylamine and ethanol are cosolvents, and said reaction is carried out in a polyethylene oxide gel at room temperature to give large colorless crystals of Zn 2 (C 9 H 3 O 6 )• NO 3 (H 2 O) 1 (C 2 H 5 OH) 5 . The method of claim 1 characterized in that the metal ion is added to the reaction in the form of Zn(NO 3 )•6H 2 O, the templating agent is ethanol, the ligand containing multidentate functional groups is benzene-1,3,5-tricarboxylic acid, the ligand containing monodentate functional group is nitrate, and triethylamine and ethanol are cosolvents, and said reaction is carried out at room temperature to give colorless crystals of Zn 2 (C 9 H 3 O 6 )•NO 3 (H 2 O) 1 (C 2 H 5 OH) 5 . The method of claim 1 characterized in that the metal ion is added as Co(NO 3 ) 2 •6H 2 O, the ligand containing multidentate functional groups is benzene-1,3,5-tricarboxylic acid, and pyridine is the ligand containing monodentate functional group and the templating agent, and wherein the reaction is carried out in an ethanol/1,2-dichloroethane solution in the presence of a polyethylene oxide gel to give CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 •2/3NC 5 H 5 . The method of claim 1 characterized in that the metal ion is added as Co(NO 3 ) 2 •6H 2 O, the ligand containing multidentate functional groups is benzene-1, 3, 5-tricarboxylic acid, and pyridine is the ligand containing monodentate functional group and the templating agent, and said reaction is carried out in ethanol to give CoC 6 H 3 (COOH 1/3 ) 3 (NC 5 H 5 ) 2 •2/3NC 5 H 5 . A method for removing impurities from a gas or liquid characterized by contacting the gas or liquid containing such impurities with an effective adsorbing amount of a microporous material for a period of time sufficient to remove such impurities and then removing said microporous material from contact with said gas or liquid, said microporous material having been prepared by the steps of admixing a solution containing one or more metal ions from the group consisting of: Sc 3+ , Ti 4+ , V 4+ , V 3+ , V 2+ , Cr 3+ , Mo 3+ , Mn 3+ , Mn 2+ , Fe 3+ , Fe 2+ , Co 3+ , Co 2+ , Ni 2+ , Ni + , Cu 2+ , Cu + , Ag + , Zn 2+ , Cd 2+ , Al 3+ , Sn 4+ , Sn 2+ , and Bi 5+ , Bi 3+ , Bi + ; along with the corresponding metal salt counteranion, with one or more ligand substructures being at least one of: methane, tetraphenylmethane, ethylene, benzene, naphthylene, adamantane, and squarane; said ligand substructure having bound thereto multidentate functional groups, X, which are covalently bound to the substructure of the ligand, wherein X is a functional group selected from the groups consisting of: COOH, CSSH, CH(RSH) 2 , CH(RNH 2 ) 2 , CH(ROH) 2 , and CH(RCN) 2 , wherein R is H or methyl or an aryl group consisting of one phenyl ring; in the presence of a templating agent, selected from the group consisting of: a. alkyl amines and their corresponding alkyl ammonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; b. aryl amines and their corresponding aryl ammonium salts having from 1 to 5 phenyl rings; c. alkyl phosphonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; d. aryl phosphonium salts, having from 1 to 5 phenyl rings, e. alkyl organic acids and their corresponding salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; f. aryl organic acids and their corresponding salts, having from 1 to 5 phenyl rings; g. aliphatic alcohols, containings linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; h. aryl alcohols having from 1 to 5 phenyl rings; i. sulfate, nitrate, nitrite, sulfite, bisulfite, phosphate, hydrogen phosphate, dihydrogen phosphate, diphosphate, triphosphate, phosphite, chloride, chlorate, bromide, bromate, iodide, iodate, carbonate, bicarbonate, and the corresponding acids and salts of the aforementioned inorganic anions; j. ammonia, carbon dioxide, methane, oxygen, argon, nitrogen, ethylene, hexane, benzene, toluene, xylene, chlorobenzene, nitrobenzene, naphthalene, thiophene, pyridine, acetone, 1,2-dichloroethane, methylenechloride, tetrahydrofuran, ethanolamine, triethylamine,and trifluoromethylsulfonic acid. A method for removing impurities from a gas or liquid characterized by contacting the gas or liquid containing such impurities with an effective adsorbing amount of a microporous material for a period of time sufficient to remove such impurities and then removing said microporous material from contact with said gas or liquid, said microporous material having been prepared by the steps of admixing a solution containing one or more metal ions from the group consisting of: Fe 3+ , Fe 2+ , Co 3+ , Co 2+ , Ni 2+ , Ni + , Zn 2+ , along with the corresponding metal salt counteranion, with one or more ligand substructures being at least one of: benzene and adamantane, said ligand substructure having bound thereto carboxylic acid functional groups; in the presence of a templating agent, selected from the group consisting of: a. alkyl amines and their corresponding alkyl ammonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; b. aryl amines and their corresponding aryl ammonium salts having from 1 to 5 phenyl rings; c. alkyl phosphonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; d. aryl phosphonium salts, having from 1 to 5 phenyl rings, e. alkyl organic acids and their corresponding salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; f. aryl organic acids and their corresponding salts, having from 1 to 5 phenyl rings; g. aliphatic alcohols, containings linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; h. aryl alcohols having from 1 to 5 phenyl rings; i. inorganic anions from the group consisting of: sulfate, nitrate, nitrite, sulfite, bisulfite, phosphate, hydrogen phosphate, dihydrogen phosphate, diphosphate, triphosphate, phosphite, chloride, chlorate, bromide, bromate, iodide, iodate, carbonate, bicarbonate, and the corresponding acids and salts of said inorganic anions; j. ammonia, carbon dioxide, methane, oxygen, argon, nitrogen, ethylene, hexane, benzene, toluene, xylene, chlorobenzene, nitrobenzene, naphthalene, thiophene, pyridine, acetone, 1,2-dichloroethane, methylenechloride, tetrahydrofuran, ethanolamine, triethylamine,and trifluoromethylsulfonic acid.

Inventors: YAGHI OMAR M, YAGHI, OMAR M.
Applicants: NALCO CHEMICAL CO, NALCO CHEMICAL COMPANY
Application year: 1996
Main classification: C07F19
IPC codes: C07F3, B01J31, C07F15