Viscosity conditioner

Abstract: A viscosity conditioner comprising a compound represented by the following formula (2) wherein R is a hydrocarbylene group; R' is a branched alkyl group of the following formula (4) where R 4 and R 5 are each a hydrocarbyl group having a carbon number of 4 or greater and R 6 is a hydrocarbylene group, or a secondary alkyl group of the following formula (5) where R 7 and R 8 are each a hydrocarbyl group having a carbon number of 4 or greater; R 1 is a hydrocarbyl group which may contain a urethane linkage; n ranges from 1 to 500; and h is not less than 1, is provided. The viscosity conditioner is conducive to reduced temperature dependence and hence constant viscosity in a certain range suited for all environmental conditions and good coatability throughout all seasons. An emulsion composition and an emulsion paint composition, each including the viscosity conditioner, are also provided.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention This invention relates to novel viscosity conditioners as well as to an emulsion composition and an emulsion paint composition utilizing such a viscosity conditioner. 2. Description of the Related Art A wide variety of viscosity builders are commonly known which are natural, semi-synthetic (for example, carboxymethyl cellulose) or synthetic in character. Also, there are many known reaction products obtained by reaction of polyoxyethylene glycol derivatives with aliphatic acid esters or epoxides. Various other viscosity builders are also known as disclosed for instance in Japanese Patent Publication No. 52-25840, Japanese Patent Laid-Open No. 58-213074, Japanese Patent Publication No. 1-55292, Japanese Patent Publication No. 3-9151, Japanese Patent Publication No. 3-52766 and Japanese Patent Publication No. 4-55471. US Patent No. 4079028 discloses latex compounds containing polyurethane thickeners. The compounds disclosed in this document differ from those of the present invention in the nature of the terminal hydrocarbyl groups hereinafter defined as R'. Such known viscosity builders, however, pose the problem that their viscosities are liable to change under ambient temperatures. For example, a paint formulated with a viscosity conditioner and a viscosity builder is necessarily susceptible, if by nature dependent on temperature, to varying viscosities at the time it is coated in summer and in winter. Especially in a geographical area like Japan where the four seasons are clearly vary, the maximum temperature difference is frequently 30 to 40 °C between winter and summer seasons, so such viscosity changes with the seasons cause problems in the workability of the paint. The present applicant's EP-A-761779, which was published after the filing date of the present application, discloses viscosity conditioners and compositions containing the same. The viscosity conditioners of the present invention fall within the general disclosure of this document. However, EP-A-761779 does not disclose the specific viscosity conditioners of the present invention. SUMMARY OF THE INVENTION The present invention, therefore, has for its primary object to provide a viscosity conditioner which is less dependent on temperature, and thus, is highly capable of maintaining a constant range of viscosities suited for all environmental conditions and is adequately coatable throughout the year. Another object of the invention resides in the provision of an emulsion composition and of an emulsion paint composition, each of which include the above viscosity conditioner. To cope with the foregoing problems of the prior art, the present inventors have as a result of intensive research, developed a unique viscosity conditioner that has reduced temperature dependence, constant viscosity in a certain range to suit all environmental conditions and excellent coatability all the year round, coupled with an emulsion composition and an emulsion paint composition which each include of such viscosity conditioner. In one aspect, the present invention provides a viscosity conditioner comprising a compound of the formula (2) wherein: R is a hydrocarbylene group; R' is a branched alkyl group of the following formula (4) where R 4 and R 5 are each a hydrocarbyl group having a carbon number of 4 or greater and R 6 is a hydrocarbylene group, or a secondary alkyl group of the following formula (5) where R 7 and R 8 are each a hydrocarbyl group having a carbon number of 4 or greater; R 1 is a hydrocarbyl group which may contain a urethane linkage; n ranges from 1 to 500; and h is not less than 1. In another aspect, the invention provides an emulsion composition including such viscosity conditioner. In a further aspect, the invention provides an emulsion paint composition including such viscosity conditioner. DETAILED DESCRIPTION OF THE INVENTION The viscosity conditioner according to the present invention is comprised of a compound represented by the formula (2) below. The formula (2) is as follows: where R is a hydrocarbylene group, R' is a branched alkyl group of formula (4), as defined above, or a secondary alkyl group of formula (5), as defined above, R 1 is a hydrocarbyl group which may have a urethane linkage, n ranges from 1 to 500, and h is not less than 1. The compound of the formula (2) according to the present invention can be obtained by reacting one or more mono- or poly-isocyanates of formula R 1 -(NCO) h and one or more polyether monoalcohols of formula R'-(O-R) n -OH. In such instance, the groups R, R' and R 1 in the formula (2) are determined by the compounds of formula R 1 -(NCO) h and of formula R'-(O-R) n -OH to be used. No particular restriction is imposed upon the mono- or poly-isocyanates of an h valence and of formula R 1 -(NCO) h for use in providing the viscosity conditioner of the present invention inasmuch as they have one or more isocyanate groups contained in their respective molecules. Here, the monoisocyanates and polyisocyanates include, for example, aliphatic monoisocyanates, aliphatic diisocyanates, aromatic monoisocyanates, aromatic diisocyanates, alicyclic monoisocyanates, alicyclic diisocyanates, biphenyl diisocyanates, phenylmethane diisocyanates, triisocyanates, and tetraisocyanates. Aliphatic monoisocyanates useful for the present invention may be suitably chosen from, for example, methyl isocyanate, ethyl isocyanate, butyl isocyanate, propyl isocyanate, hexyl isocyanate, octyl isocyanate, lauryl isocyanate and octadecyl isocyanate. Suitable alicyclic monoisocyanates include, for example, cyclohexyl isocyanate. Suitable aromatic monoisocyanates include, for example, phenyl isocyanate and tolylene isocyanate. Aliphatic diisocyanates used herein are chosen from, for example, methylene diisocyanate, dimethylene diisocyanate, trimethylene diisocyanate, tetramethylene diisocyanate, pentamethylene diisocyanate, hexamethylene diisocyanate, dipropylether diisocyanate, 2,2-dimethylpentane di-isocyanate, 3-methoxyhexane diisocyanate, octamethylene diisocyanate, 2,2,4-trimethylpentane diisocyanate, nona-methylene diisocyanate, decamethylene diisocyanate, 3-butoxyhexane diisocyanate, 1,4-butylene glycol dipropyl-ether diisocyanate, thiodihexyl diisocyanate, meta-xylylene diisocyanate, para-xylylene diisocyanate and tetramethylxylylene diisocyanate. Eligible aromatic diisocyanates include, for example, meta-phenylene diisocyanate, para-phenylene diisocyanate, 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, di-methylbenzene diisocyanate, ethylbenzene diisocyanate, isopropylbenzene diisocyanate, tolidine diisocyanate, 1,4-naphthalene diisocyanate, 1,5-naphthalene diisocyanate, 2,6-naphthalene diisocyanate and 2,7-naphthalene diisocyanate. Eligible alicyclic diisocyanates include, for example, hydrogenated xylylene diisocyanate and isophorone diisocyanate. Eligible biphenyl diisocyanates include, for example, biphenyl diisocyanate, 3,3'-dimethylbiphenyl diisocyanate and 3,3'-dimethoxybiphenyl diisocyanate. Phenylmethane diisocyanates used herein are exemplified by diphenylmethane-4,4'-diisocyanate, 2,2'-dimethyldiphenylmethane-4,4'-diisocyanate, diphenyldimethylmethane-4,4'-diisocyanate, 2,5,2',5'-tetramethyl-diphenylmethane-4,4'-diisocyanate, cyclohexylbis(4-isocyanato phenyl)methane, 3,3'-dimethoxydiphenylmethane-4,4'-diisocyanate, 4,4'-dimethoxydiphenylmethane-3,3'-diisocyanate, 4,4'-diethoxydiphenylmethane-3,3'-diisocyanate, 2,2'-dimethyl-5,5'-dimethoxydiphenylmethane-4,4'-diisocyanate, 3,3'-dichlorodiphenyldimethylmethane-4,4'-diisocyanate and benzophenone-3,3'-diisocyanate. Triisocyanates used herein are chosen from, for example, 1-methyl-benzene-2,4,6-triisocyanate, 1,3,5-trimethylbenzene-2,4,6-triisocyanate, 1,3,7-naphthalene triisocyanate, biphenyl-2,4,4'-triisocyanate, diphenylmethane-2,4,4'-tri-isocyanate, 3-methyldiphenylmethane-4,6,4'-triisocyanate, triphenylmethane-4,4',4"-triisocyanate, 1,6,11-undecane triisocyanate, 1,8-diisocyanate-4-isocyanate methyloctane, 1,3,6-hexamethylene triisocyanate, bicycloheptane tri-isocyanate and tris(isocyanate-phenyl)thiophosphate. The polyisocyanate compounds exemplified above may be by nature dimeric or trimeric (isocyanurate-linked), or in the form of a biuret derived from reaction with an amine. In addition, urethane linkage-containing polyisocyanates can be used which result from reacting either one of the above listed polyisocyanates with a polyol. As polyols for use in that reaction, those of from divalence to octavalence are preferred and examples are selected from divalent alcohols such as ethylene glycol, propylene glycol, butylene glycol, hexamethylene glycol and neopentyl glycol, trivalent alcohols such as glycerin, trimethylolethane and trimethylolpropane, tetravalent alcohols such as pentaerythritol, pentavalent alcohols such as adonite, arabite and xylite, heptavalent alcohols such as dipentaerythritol, sorbite, mannite and idite, and octavalent alcohols such as sucrose, and oligomers thereof, adducts thereof with alkylene oxides, and adducts thereof with caprolactones. In preparing the viscosity conditioner of the formula (2) according to the present invention, the polyether monoalcohols of formula R'-(O-R) n -OH are not particularly restrictive insofar as they are polyethers induced from branched or secondary monovalent alcohols of formula (4') or (5') below. Such a compound can be derived from addition polymerization of a branched or secondary monovalent alcohol of formula (4') or (5') below with an alkylene oxide such as ethylene oxide, propylene oxide, butylene oxide, epichlorohydrin, or a styrene oxide. The branched alcohol stated above is represented by the following formula (4'). The above secondary alcohol is represented by the following formula (5'). It is noted, therefore, that the group R' denotes the residue formed by removing a hydroxyl group from each of compounds of formulae (4') and (5'). In the formulae (4) and (5), R 4 , R 5 , R 7 and R 8 are each a hydrocarbyl group having a carbon number of 4 or greater, selected for example from an alkyl group, an alkenyl group, an alkylaryl group, a cycloalkyl group and a cycloalkenyl group, and R 6 is a hydrocarbylene group, for example an alkylene group, an alkenylene group, an alkylarylene group, a cycloalkylene group or a cycloalkenylene group. Alkyl groups eligible for the present invention are chosen from, for example, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tertiary butyl, pentyl, isopentyl, neopentyl, tertiary pentyl, hexyl, heptyl, octyl, 2-ethylhexyl, nonyl, decyl, undecyl, dodecyl, tridecyl, isotridecyl, myristyl, palmityl, stearyl, eicosyl, docosyl, tetracosyl, triacontyl, 2-octyldodecyl, 2-dodecylhexadecyl, 2-tetra-decyloctadecyl and monomethyl branched isostearyl groups. Suitable alkenyl groups include, for example, vinyl, allyl, propenyl, isopropenyl, butenyl, isobutenyl, pentenyl, isopentenyl, hexenyl, heptenyl, octenyl, nonenyl, decenyl, undecenyl, dodecenyl, tetradecenyl and oleyl groups. Suitable alkylaryl groups include phenyl, tolyl, xylyl, cumenyl, mesityl, benzyl, phenetyl, styryl, cinnamyl, benzhydryl, trityl, ethylphenyl, propylphenyl, butylphenyl, pentylphenyl, hexylphenyl, heptylphenyl, octylphenyl, nonylphenyl, alpha-naphthyl and beta-naphthyl groups. Cycloalkyl and cycloalkenyl groups used herein are exemplified by cyclopentyl, cyclohexyl, cycloheptyl, methylcyclopentyl, methylcyclohexyl, methylcycloheptyl, cyclopentenyl, cyclohexenyl, cycloheptenyl, methyl-cyclopentenyl, methylcyclohexenyl and methylcycloheptenyl groups. In the formula (4), the group R 6 is a hydrocarbylene group such as, for example, an alkylene group, an alkenylene group, an alkylarylene group, a cycloalkylene group or a cycloalkenylene group. A -CH 2 - group is particularly suitable as the group R 6 since an alcohol branched at its 2-position is less dependent in viscosity on temperature. R' is a branched or secondary alkyl group of formula (4) or (5) above. The carbon number in the R' group totals preferably from 8 to 36, more preferably from 12 to 24. More specifically, each of the groups R 4 , R 5 , R 7 and R 8 in the formulae (4) and (5) have 4 or more carbon atoms, thereby rendering the viscosity of the resultant branched or secondary alcohol less dependent on temperature. The alkylene oxide or styrene oxide may be bonded by homopolymerization, or by random or block polymerization of two or more such oxides. In this instance, any known method is suitable. The polymerization degree n is in the range of 1 to 500, preferably of 1 to 200, more preferably of 10 to 200. The proportion of the ethylene group to be occupied in the group R is preferably from 50 to 100% by weight, more preferably from 65 to 100% by weight, based on the total weight of the group R, and strict observance of this proportion leads to enhanced performance in viscosity modification. The compound of the formula (2) may be prepared as is usually done with the reaction of a polyether with an isocyanate, for example, at 80 to 90°C for 1 to 3 hours. The viscosity conditioner of the present invention, comprised of a compound of the formula (2), provides those physical properties which have not been achieved with the foregoing viscosity builders of the prior art. For example, the viscosity conditioner of the invention is by nature nonionic, and though relatively low in molecular weight, it shows good viscosity increase even when added in a smaller amount to aqueous systems. It is moreover stable to water and to alcohol. In particular, upon application to emulsion paints, such viscosity conditioner is highly capable not only of bringing about a sufficient viscosity increase, but also of contributing in most cases to excellent fluidity and leveling properties and to outstanding performance of viscosity modification under both low- and high-sheared conditions. Also, the viscosity conditioner of the present invention advantageously offers a specific property of temperature sensitivity that the prior art viscosity builders have failed to gain. Owing to the temperature sensitivity, the viscosity conditioner is less dependent on temperature, fully constant in a certain range of viscosities held for all environmental conditions and adequately coatable in all seasons. These advantages are peculiar to the present invention and due to the fact that the group R' in the formula (2) is specifically defined as a branched or secondary alkyl group of formula (4) or (5) above, namely, to the fact that a branched or secondary alcohol of formula (4') or (5') is selectively used as a starting material in providing the group R' of the formula (2). The viscosity conditioner of the present invention is applicable to aqueous systems such as emulsions, latexes and dispersible fluids (such as suspensions and dispersions). Polymeric emulsions of a vinyl acetate type are chosen for example from homopolymer emulsions of a vinyl acetate monomer, and copolymer emulsions of a vinyl acetate monomer with a comonomer such as ethylene, vinyl chloride, acrylic acid, acrylate ester, methacrylic acid, methacrylate ester, beova, maleic acid or maleate ester. Suitable polymeric emulsions of an acrylic type include homopolymer emulsions of a monomer such as acrylic acid, acrylate ester, methacrylic acid, methacrylate ester or acrylonitrile, copolymer emulsions of two or more such monomers, and copolymer emulsions of one such monomer with styrene. Suitable polymeric emulsions of a vinylidene type include homopolymer emulsions of a vinylidene chloride monomer, and copolymer emulsions of a vinylidene chloride monomer with a comonomer such as acrylic acid, acrylate ester, methacrylic acid, methacrylate ester, acrylonitrile or vinyl chloride. Included in other suitable polymeric emulsions are urethane resin emulsions, silicone resin emulsions, epoxy resin emulsions and fluorine resin emulsions. Eligible latexes are exemplified for example by SBR latex, SB latex, ABS latex, NBR latex, CR latex, VP latex, BR latex, MBR latex and IR latex. When dissolved or dispersed in water, the viscosity conditioner of the present invention can produce its effects of viscosity modification and may be used usually in an amount of 0.01 to 10%, preferably of 0.01 to 5%, based on the solid content of a given polymeric emulsion or on the total weight of a given latex. To the emulsion or latex may be added the viscosity conditioner as it is, or after it is diluted to a suitable viscosity with water or solvent. For use in emulsion paints, the viscosity conditioner of the invention may be incorporated as an aqueous solution in ethyl alcohol at a kneading stage or at a modifying stage of such an emulsion paint, whereby workability is facilitated with the viscosity conditioner added in an amount of 0.01 to 5%. The polymeric emulsions stated above can be prepared by the use of one or more anionic, cationic or nonionic emulsifiers. Two or more emulsifiers may be employed as admixed with one another irrespective of their types. The amount of the emulsifier to be used is from about 0.1 to 6% by weight based on the total weight of a selected monomer and may in some cases be larger than 6% by weight. Frequently, where an initiator of a persulfate salt type is employed, no emulsifiers may be needed. The average molecular weights of those emulsion polymers are generally from 1x10 5 to 1x10 7 and mostly above 5x10 5 . The viscosity conditioner of the present invention is nonionic in nature and thus effective also for polymeric emulsions of an alkaline class. Such viscosity conditioner may be added to such an emulsion together with a defoamer, a pigment dispersant and a surfactant. The viscosity conditioner may also contain or may subsequently be mixed with various other additives such as antioxidants, ultraviolet absorbers, water-proofing agents, anti-septic agents, bactericides, dispersants, anti-foaming agents, deodorizers, perfumes, extenders, dyes and pigments. Other aqueous systems suitable for the viscosity conditioner of the present invention are aqueous paint compositions for use in the paper, leather and textile industries, detergents, adhesives, waxes, polishing agents, cosmetics and toiletry goods, pharmaceuticals, agricultural chemicals and agricultural compositions. As discussed hereinabove, a novel viscosity conditioner, an emulsion composition and an emulsion paint composition each including of such viscosity conditioner are provided in accordance with the present invention. EXAMPLES With reference to Production Examples 1 to 9 and Examples 1 to 4 of the viscosity conditioner represented above by the formula (2), the present invention will be described below in greater detail. Production Example 1 Into a 4-necked flask of 1,000 ml in volume equipped with a thermometer, a nitrogen inlet and a stirrer was charged 660 parts by weight of an adduct of the formula formed by reaction of a branched alcohol of the formula with 20 mols of ethylene oxide (EO). The reactive system was dehydrated in vacuo (below 10 mm Hg) at 90 to 100°C for 3 hours until the moisture in the system was reduced to 0.03%. On subsequent cooling of the system to 80°C, 47.0 parts by weight of hexamethylene diisocyanate (HMDI) was placed in the flask. Reaction was then effected in a nitrogen stream at 80 to 90°C for 2 hours, after which the isocyanate content was confirmed to be nil. Thus, a reaction product of the invention was obtained which was a pale yellowish solid at normal temperature. This product is hereunder called Viscosity Conditioner 1 (R: ethylene group; R': 2-decyltetradecyl group; R 1 : hexamethylene group; h=2; n=20). Production Example 2 The process for Production Example 1 was followed except that 690 parts by weight of an adduct of a secondary alcohol of 11 to 14 carbon atoms with 100 mols of EO, and 10.5 parts by weight of tetramethylene diisocyanate were used. Thus, a pale yellowish solid product was obtained. This product is called Viscosity Conditioner 2 (R: ethylene group; R': mixture of the formula R 1 : tetramethylene group; h=2; n=100). Production Example 3 The process for Production Example 1 was followed except that 133 parts by weight of an adduct of the formula formed by reaction of a branched alcohol of the formula with 50 mols of EO, and 20.4 parts by weight of HMDI were used. Thus, a pale yellowish solid product was obtained. This product is called Viscosity Conditioner 3 (R: ethylene group; R 1 : hexamethylene group; h=2; n=50). Production Example 4 The process for Production Example 1 was followed except that 167 parts by weight of an adduct of the formula formed by reaction of a branched alcohol of the formula with 10 mols of EO, 504 parts by weight of an adduct of a secondary alcohol of 11 to 14 carbon atoms with 100 mols of EO, and 36.5 parts by weight of tolylene diisocyanate (TDI) were used. Thus, a pale yellowish solid product was obtained. This product is called Viscosity Conditioner 4 (R: ethylene group; R': mixture of 2-decyltetradecyl group and same group as in Production Example 2; R 1 : tolylene group; h=2; n=10). Production Example 5 The process for Production Example 1 was followed except that use was made of 656 parts by weight of an adduct of the formula formed by reaction of a branched alcohol of formula with 100 mols of EO, and 48.0 parts by weight of a triisocyanate derived by reacting 1 mol of trimethylolpropane and 3 mols of TDI. Thus, a pale yellowish solid product was obtained. This product is called Viscosity Conditioner 5 (R: ethylene group; R': 2-decyltetradecyl group; R 1 : tri-methylolpropane-TDI moiety; h=3; n=100). Production Example 6 The process for Production Example 1 was followed except that 625 parts by weight of an adduct of the formula formed by reaction of a branched alcohol of the formula with 100 mols of EO, and 12.7 parts by weight of tolylene isocyanate were used. Thus, a pale yellowish solid product was obtained. This product is called Viscosity Conditioner 6 (R: ethylene group; R': 2-decyltetradecyl group; R 1 : toluyl group; h=1; n=100). Production Example 7 The process for Production Example 1 was followed except that use was made of 662 parts by weight of an adduct of the formula formed by reaction of a branched alcohol of the formula with 100 mols of EO, and 30.0 parts by weight of a triisocyanate prepared by reacting 1 mol of trimethylolpropane and 3 mols of HMDI. Thus, a pale yellowish solid product was obtained. This product is called Viscosity Conditioner 7 (R: ethylene group; R': 2-decyltetradecyl group; R 1 : tri-methylolpropane-HMDI moiety; h=3; n=100). Production Example 8 The process for Production Example 1 was followed except that use was made of 634 parts by weight of an adduct of a secondary alcohol of 11 to 14 carbon atoms with 50 mols of EO, and 55.4 parts by weight of a tetravalent isocyanate prepared by reacting 1 mol of pentaerythritol and 4 mols of TDI. Thus, a pale yellowish solid product was obtained. This product is called Viscosity Conditioner 8 (R: ethylene group; R': same group as in Production Example 2; R 1 : penta-erythritol-TDI moiety; h=4; n=50). Production Example 9 The process for Production Example 1 was followed except that use was made of 665 parts by weight of an adduct of the formula formed by reaction of a branched alcohol of the formula with 100 mols of EO and also with 20 mols of propylene oxide (PO), and 25.7 parts by weight of a hexavalent isocyanate derived by reacting 1 mol of dipentaerythritol and 6 mols of xylylene diisocyanate. Thus, a pale yellowish solid product was obtained. This product is called Viscosity Conditioner 9 (R: ethylene group, propylene group; R 1 : dipentaerythritol-xylylene diisocyanate moiety; h=6; n=100, 20). Comparative Production Example 1 Into a 4-necked flask of 1,000 ml in volume equipped with a thermometer, a nitrogen inlet and a stirrer was charged 668 parts by weight of an adduct of lauryl alcohol with 50 mols of EO. The reactive system was dehydrated in vacuo (below 10 mm Hg) at 90 to 100 °C for 3 hours until the moisture in the system was lowered to 0.03%. On cooling of the reactive system to 80°C, 23.5 parts by weight of HMDI was put into the flask. Reaction was then effected in a nitrogen stream at 80 to 90 °C for 2 hours, after which the isocyanate content was confirmed to be nil. Thus, a comparative reaction product was obtained which was a pale yellowish solid at normal temperature. This product is hereunder called Comparative Product 1. Comparative Production Example 2 The process for Comparative Production Example 1 was followed except that use was made of 665 parts by weight of an adduct of nonylphenol with 100 mols of EO, and 30.6 parts by weight of a triisocyanate derived by reacting 1 mol of tri-methylolpropane and 3 mols of HMDI. Thus, a pale yellowish solid product was obtained. This product is called Comparative Product 2. Comparative Production Example 3 The process for Comparative Production Example 1 was followed except that 655 parts by weight of an adduct of decyl alcohol with 50 mols of EO, and 37.8 parts by weight of TDI were used. Thus, a pale yellowish solid product was obtained. This product is called Comparative Product 3. An amount of 40 parts by weight of each of Viscosity Conditioners 1 to 9 representative of the present invention and of Comparative Products 1 to 3 was uniformly mixed with 10 parts by weight of butyl cellosolve and 50 parts by weight of water so that there was provided a transparent liquid composition, namely each of Compositions 1 to 9 and of Comparative Composition 1 to 3. The viscosities of these test compositions are indicated below. (1 cPs = 1m Pa.s) Composition 1 about 2,000 cPs Composition 2 about 4,000 cPs Composition 3 about 2,500 cPs Composition 4 about 2,000 cPs Composition 5 about 6,000 cPs Composition 6 about 3,500 cPs Composition 7 about 5,500 cPs Composition 8 about 4,500 cPs Composition 9 about 7,500 cPs Comparative Composition 1 about 4,000 cPs Comparative Composition 2 about 6,000 cPs Comparative Composition 3 about 2,000 cPs Example 1: Evaluation with Emulsions Formulation: emulsion (for gloss coating; acrylate ester type; commercially available) 100.0 g viscosity conditioner (each of inventive and comparative products; aqueous solution of 10% in solid content) 0.5 g anti-foaming agent (Adekanate B-940; mineral oil type; Asahi Denka Kogyo K.K.) 0.2 g The above formulation was hand-stirred for 5 minutes, followed by mechanical stirring (at 1,000 rpm). After being allowed to stand for 2 hours at each of certain selected temperatures (5, 25 and 40°C), the viscosities of the resulting emulsion compositions, inventive compositions 1 to 9 and comparative compositions 1 to 3, were measured. The measurements are made under the set of conditions given below: viscometer: BM viscometer rotor: No. 4 revolution: 12 rpm The test results are shown in Table 1. viscosity conditioner 5°C (cPs) 25 °C (cPs) 40 °C (cPs) 40°C/5°C Composition 1 8,100 7,800 7,600 0.94 Composition 2 3,300 2,900 2,800 0.85 Composition 3 9,000 8,800 8,500 0.94 Composition 4 5,200 4,800 4,600 0.88 Composition 5 7,000 6,500 6,100 0.87 Composition 6 8,200 8,000 8,000 0.98 Composition 7 11,500 10,300 10,100 0.88 Composition 8 5,800 5,800 5,400 0.93 Composition 9 3,100 2,700 2,400 0.77 Comparative Composiiton 1 4,000 2,800 800 0.20 Comparative Composition 2 6,300 2,100 630 0.10 Comparative Composition 3 8,200 3,800 1,100 0.13 The above testing was repeated except that use was made of a different emulsion for use in elastic coating (styrene-acrylate ester type; commercially available) and a different grade of anti-foaming agent (Adekanate B-190; silicone type; Asahi Denka Kogyo K.K.). The results are listed in Table 2. viscosity conditioner 5°C (cPs) 25 °C (cPs) 40 °C (cPs) 40°C/5°C Composition 1 15,000 14,500 13,300 0.89 Composition 2 12,000 11,300 11,000 0.92 Composition 3 20,000 19,800 19,600 0.98 Composition 4 18,000 17,800 16,800 0.93 Composition 5 25,000 23,500 23,100 0.92 Composition 6 31,000 30,800 30,000 0.97 Composition 7 41,000 39,800 38,500 0.94 Composition 8 33,000 31,600 31,600 0.96 Composition 9 53,100 53,100 52,500 0.99 Comparative Composiiton 1 19,900 10,800 5,500 0.28 Comparative Composition 2 40,300 20,300 5,900 0.15 Comparative Composition 3 38,500 16,000 6,800 0.18 Example 2: Evaluation with Elastic Paints Formulation: water 90 parts by weight viscosity conditioner (each of inventive and comparative products) 70 parts by weight pigment dispersant (25% polycarboxylic acid type) 10 parts by weight anti-freeze agent (ethylene glycol) 20 parts by weight anti-foaming agent (Adekanate B-940; Asahi Denka Kogyo K.K.) 2 parts by weight titanium oxide 140 parts by weight calcium carbonate 160 parts by weight The mixture thus formulated was stirred for 24 hours and eventually used as a mill base. This base was then formulated as below. Formulation: mill base 493 parts by weight emulsion (for elastic coating; styrene-acrylate ester type; available in commerce) 410 parts by weight anti-foaming agent (Adekanate B-190) 3 parts by weight Stirring was done for 5 hours, and each of the finished paints was let to stand for 2 hours at three different temperatures (5, 25 and 40°C) and then checked for viscosities under the following set of conditions: viscometer: BM viscometer rotor No. 4 revolution: 30 rpm The results are shown in Table 3. viscosity conditioner 5°C (cPs) 25 °C (cPs) 40 °C (cPs) 40°C/5°C Composition 1 25,600 24,500 22,900 0.89 Composition 2 18,700 17,500 16,300 0.87 Composition 3 35,200 33,300 32,000 0.91 Composition 4 18,700 16,500 15,000 0.80 Composition 5 35,000 34,000 33,600 0.96 Composition 6 53,300 53,300 51,800 0.97 Composition 7 62,800 62,300 62,300 0.99 Composition 8 48,500 48,000 47,800 0.99 Composition 9 73,300 73,300 73,300 1.00 Comparative Composiiton 1 28,800 15,700 9,400 0.33 Comparative Composition 2 17,800 8,500 1,300 0.07 Comparative Composition 3 53,600 21,100 5,800 0.11 As is clear from Examples 1 and 2 above, Viscosity Conditioners 1 to 9 according to the present invention have proved to provide emulsions which are less susceptible to viscosity changes with temperature. The reason behind this benefit is that such viscosity conditioners were produced by the use of a selected class of branched or secondary alcohols as starting materials with consequential bonding of a branched chain or a secondary hydrocarbon chain to the group R'. On the other hand, Comparative Products 1 to 3 in common use revealed marked changes in the viscosities with temperatures since the products were derived from use of straight alcohols as starting materials and hence were so structured as to be terminated by a straight hydrocarbon chain. Example 3: Color Toning and Water Resistance with Emulsions Subsequently, the following testing was conducted to evaluate the performance of the viscosity conditioner of the present invention as applied to a certain emulsion paint. Formulation: emulsion (acrylate ester type) 40.0 g black pigment 0.8 g anti-foaming agent (Adekanate B-940) 0.1g Hand mixing of this formulation was done for 1 minute, followed by homogenization through mechanical stirring with a large turbine impeller for 10 to 20 minutes at 1,000 to 2,000 rpm. The resultant emulsion was coated over a slate plate. Color toning was adjudged in respect of any appreciable color changes at three points of the emulsion, i.e., (1) wet-on-wet coating, (2) coated surface texture upon finger rubbing and (3) coat sagging, as compared to the coated surface obtained with a single coating. Water resistance was determined by inspecting the state of the coat after being immersed in a warm water of 50°C for 24 hours. The results are listed in Table 4 in which the symbol "o" is taken as "not different", "_" as "slightly different" and "×" as "largely different". viscosity conditioner color tone water resistance point 1 point 2 point 3 Composition 1 ○ ○ ○ not different Composition 2 ○ ○ ○ not different Composition 3 ○ ○ ○ not different Composition 4 ○ ○ ○ not different Composition 5 ○ ○ ○ not different Composition 6 ○ ○ ○ not different Composition 7 ○ ○ ○ not different Composition 8 ○ ○ ○ not different Composition 9 ○ ○ ○ not different Comparative Composition 1 - × × slightly blistered Comparative Composition 2 - ○ × greatly blistered Comparative Composition 3 × - ○ greatly blistered Example 4: Color Toning and Water Resistance with Paints Formulation: paint used in Example 2 40.0 g black pigment 0.8 g anti-foaming agent (Adekanate B-940) 0.1 g Hand mixing of this formulation was done for 1 minute, followed by homogenization through mechanical stirring with a large turbine impeller for 10 to 20 minutes at 1,000 to 2,000 rpm. The resultant emulsion was coated over a slate plate. Color toning was adjudged in respect of any appreciable color changes at three points of the emulsion, i.e., (1) wet-on-wet coating, (2) coated surface texture upon finger rubbing and (3) coat sagging, as compared to the coated surface obtained with a single coating. Water resistance was determined by inspecting the state of the coat after being immersed in a warm water of 50°C for 24 hours. The results are listed in Table 5 in which the symbol "o" is taken as "not different", "_" as "slightly different" and "×" as "largely different". viscosity conditioner color tone water resistance point 1 point 2 point 3 Composition 1 ○ ○ ○ not different Composition 2 ○ ○ ○ not different Composition 3 ○ ○ ○ not different Composition 4 ○ ○ ○ not different Composition 5 ○ ○ ○ not different Composition 6 ○ ○ ○ not different Composition 7 ○ ○ ○ not different Composition 8 ○ ○ ○ not different Composition 9 ○ ○ ○ not different Comparative Composition 1 × - ○ slightly blistered Comparative Composition 2 ○ × - slightly blistered Comparative Composition 3 × × - greatly blistered As demonstrated by Examples 3 and 4 above, Viscosity Conditioners 1 to 9 of the present invention have excellent physical properties suited for use as viscosity conditioners for emulsion paints.

Claims: A viscosity conditioner comprising a compound represented by the following formula (2) wherein: R is a hydrocarbylene group; R' is a branched alkyl group of the following formula (4) where R 4 and R 5 are each a hydrocarbyl group having a carbon number of 4 or greater and R 6 is a hydrocarbylene group, or a secondary alkyl group of the following formula (5) where R 7 and R 8 are each a hydrocarbyl group having a carbon number of 4 or greater; R 1 is a hydrocarbyl group which may contain a urethane linkage; n ranges from 1 to 500; and h is not less than 1. The viscosity conditioner according to claim 1, wherein the group R' is a residue remaining after an isocyanate group or groups have been removed from a mono- or polyisocyanate of formula R 1 -(NCO) h , wherein R 1 and h are as defined in claim 1. The viscosity conditioner according to claim 2, wherein the polyisocyanate of formula R 1 -(NCO) h is derived from the reaction of a divalent to hexavalent polyol and a divalent to tetravalent polyisocyanate and has a urethane linkage in its molecule. The viscosity conditioner according to claim 1, wherein the group R is an alkylene group having 2 to 4 carbon atoms. The viscosity conditioner according to claim 1, wherein R 6 is -CH 2 -. A viscosity conditioner resulting from the reaction of at least one mono- or polyisocyanate of formula R 1 -(NCO) h and at least one polyether monoalcohol of formula R'-(O-R) n -OH, where R 1 , R', R, h and n are as defined in claim 1. An emulsion composition comprising, as an essential component, the viscosity conditioner of any one of claims 1 to 6. An emulsion paint composition comprising, as an essential component, the viscosity conditioner of any one of claims 1 to 6.

Inventors: KAORU KOMIYA, TOYOTARO YOSHIOKA, KAORU, KOMIYA, TOYOTARO, YOSHIOKA
Applicants: ASAHI DENKA KOGYO KK, ASAHI DENKA KOGYO KABUSHIKI KAISHA
Application year: 1996
Main classification: C09D7
IPC codes: C08G18, C09D7