Silica reinforced rubber composition and tire with tread thereof

Abstract: The present invention relates to a rubber composition containing silica reinforcement and to pneumatic tires having treads comprised of such rubber composition. A rubber composition comprises at least one elastomer, silica, carbon black and a silica coupler comprised of nicotinamide.

Description: Field This invention relates to rubber compositions which contain silica reinforcement and to tires having treads thereof. In one aspect, the rubber composition is comprised of rubber, particularly sulfur cured rubber, reinforced with a combination of silica, and optionally carbon black, and a nicotinamide coupling agent. Background For various applications utilizing rubber which requires high strength and abrasion resistance, particularly applications such as tires and various industrial products, sulfur cured rubber is utilized which contains substantial amounts of reinforcing fillers, often in a range of 35 to 85 parts by weight per 100 parts rubber. Carbon black is commonly used for such purpose and normally provides or enhances good physical properties for the sulfur cured rubber. Particulate silica is also often used for such purpose, particularly when the silica is used in conjunction with a coupling agent. In some cases, a combination of silica and carbon black is utilized for reinforcing fillers for various rubber products, including treads for tires. The use of such reinforcing fillers for elastomers, including sulfur curable elastomers, is well known to those skilled in such art. It is important to appreciate that, conventionally, carbon black is a considerably more effective reinforcing filler for rubber products, and particularly for rubber tire treads than silica if the silica is used without a coupling agent, or silica coupler or silica adhesion agent as it may be sometimes referred to herein. Such coupling agents may, for example, be premixed, or pre-reacted, with the silica particles or added to the rubber mix during a rubber/silica processing, or mixing, stage. If the coupling agent and silica are added separately to the rubber mix during the rubber/silica mixing, or processing stage, it is considered that the coupling agent then combines in situ with the silica. In particular, such coupling agents are sometimes composed of a silane which has a constituent component, or moiety, (the silane portion) capable of reacting with the silica surface and, also, a constituent component, or moiety, capable of reacting with the rubber, particularly a sulfur vulcanizable rubber which contains carbon-to-carbon double bonds, or unsaturation. In this manner, then the coupler acts as a connecting bridge between the silica and the rubber and thereby enhances the rubber reinforcement aspect of the silica. In one aspect, the silane of the coupling agent apparently forms a bond to the silica surface and the rubber reactive component of the coupling agent combines with the rubber itself. Usually the rubber reactive component of the coupler is temperature sensitive and tends to combine with the rubber during the final and higher temperature sulfur vulcanization stage and, thus, subsequent to the rubber/silica/coupler mixing stage and, therefore, after the silane group of the coupler has combined with the silica. However, partly because of typical temperature sensitivity of the coupler, some degree of combination, or bonding, may occur between the rubber-reactive component of the coupler and the rubber during an initial rubber/silica/coupler mixing stage[s] and, thus, prior to a subsequent vulcanization stage. The rubber-reactive group component of the coupler may be, for example, one or more of groups such as mercapto, amino, vinyl, epoxy, and sulfur groups, and is often a sulfur or mercapto moiety and more usually sulfur. Numerous coupling agents are taught for use in combining silica and rubber, such as, for example, silane coupling agents containing a polysulfide component, or structure, such as, for example, trialkoxyorganosilane polysulfides containing from 2 to 8 sulfur atoms in a polysulfide bridge such as, for example, bis-(3-triethoxysilylpropyl)tetrasulfide and/or trisulfide. Various U.S. patents relating to silicas and silica reinforced tire treads include, for example, US-A-3 451 458; 3 664 403; 3 768 537; 3 884 285; 3 938 574; 4 482 663; 4 590 052; 5 089 554 and GB-A-1 424 503. US-A-4 513 123 discloses a rubber composition utilizing dithiodipropionic acid with natural rubber, or blends of natural and synthetic rubbers, 30-80 parts carbon black, sulfur and organo-cobalt compound for use as skim stock for brass-plated steel. It relates that the rubber composition can contain other additives such as fillers such as clays, silicas or calcium carbonate, process and extender oils, antioxidants, cure accelerators, cure activators, cure stabilizers and the like. The term "phr" if used herein, and according to conventional practice, refers to "parts of a respective material per 100 parts by weight of rubber, or elastomer". In the description of this invention, the terms "rubber" and "elastomer" if used herein, may be used interchangeably, unless otherwise prescribed. The terms "rubber composition", "compounded rubber" and "rubber compound", if used herein, are used interchangeably to refer to rubber which has been blended or mixed with various ingredients and materials and such terms are well known to those having skill in the rubber mixing or rubber compounding art. A reference to an elastomer's Tg refers to its glass transition temperature, which can conveniently be determined by a differential scanning calorimeter at a heating rate of 10°C per minute. Summary and Practice of the Invention In accordance with one aspect of this invention, a rubber composition is provided which comprises (A) 100 parts by weight of at least one diene-based elastomer, (B) 25 to 100, optionally 35 to 90, phr of filler composed of silica and carbon black, and (C) a silica coupler selected from (i) nicotinamide or (ii) a combination of 95 to 25, alternatively 90 to 55, weight percent nicotinamide and, correspondingly, 5 to 75, alternatively 10 to 45, weight percent of at least one of dithiodipropionic acid and bis-(3-trialkoxysilylalkyl) polysulfide containing from 2 to 8 sulfur atoms in the polysulfide bridge such as, for example, at least one of bis-(3-triethoxysilylpropyl)tetrasulfide and bis-(3-triethoxysilylpropyl)trisulfide; wherein the weight ratio of said silica coupler to silica is in a range of 0.01/1 to 0.2/1; wherein the weight ratio of silica to carbon black is at least 0.1/1, optionally at least 3/1 and optionally at least 10/1. In one aspect of the invention, such a rubber composition is provided which is comprised of (A) 100 parts by weight of at least one diene-based elastomer, (B) 25 to 90 phr particulate silica, (C) up to about 30 phr carbon black, and (D) a silica coupler which is collectively composed of 90 to 55 weight percent nicotinamide, 5 to 25 weight percent of at least one of bis-(3-triethoxysilylpropyl)tetrasulfide and bis-(3-triethoxysilylpropyl)trisulfide and 5 to 25 weight percent dithiodipropionic acid; wherein the weight ratio of said silica coupler to silica is in a range of 0.01/1 to 0.2/1; wherein the weight ratio of silica to carbon black is in a range of 3/1 to 30/1; wherein the silica is characterized by having a BET surface area in a range of 50 to 300 square meters per gram and a dibutylphthalate (DBP) absorption value in a range of 150 to 300. Thus, in one aspect of the invention, the rubber composition contains a combination of both silica and carbon black as elastomer reinforcing pigments. The rubber composition may contain a minor amount of silica in its silica/carbon black blend or it may be quantitatively reinforced with silica where carbon black is present in a minor amount. In another aspect of the invention, a tire is provided having a tread comprised of the said rubber composition of this invention. Where it is desired that the rubber composition is primarily reinforced with silica as the reinforcing pigment, it is preferable that the weight ratio of silica to carbon black is at least 3/1, preferably at least 10/1 and, thus, for example, in a range of 3/1 to 30/1. In one aspect of the invention, the silica coupler consists essentially of the nicotinamide. In another aspect, the silica coupler can be composed of a combination of nicotinamide and dithiodipropionic acid. While it is believed that dithiodipropionic acid may exist in isomer forms, such as the 3,3'- and 2,2'-forms, the 3,3'-dithiodipropionic acid form is preferred. In a further aspect, the silica coupler can be composed of a combination of the nicotinamide together with bis-(3-triethoxysilylpropyl)tetrasulfide and/or a blend of such tetrasulfide and bis-(3-triethoxysilylpropyl)trisulfide. In a still further aspect, the silica coupler can be composed of a combination of the nicotinamide, dithiodipropionic acid and bis-(3-triethoxysilylpropyl)tetrasulfide or blend of such tetrasulfide and trisulfide moiety thereof. The nicotinamide can also be referred to as niacinamide. It can conveniently be described as 3-pyridine carboxamide. In particular, it can be characterized by having the properties of melting point in a range of 130°C to 132°C; infrared spectrometric amide absorption band intensity in a range of 95% to 100% and pyridine absorption band intensity in a range of 95% to 98%. The nicotinamide is considered herein to be particularly advantageous for the practice of this invention because it has a very strong associative attraction to silica and high solubility in rubber which is considered to be a benefit to the exceptionally good dispersion of silica into the rubber. Historically, the more homogeneous the dispersion of rubber compound components into the rubber, the better the resultant cured properties of that rubber. The nicotinamide's strong association to silica and high affinity, or compatibility, with rubber is considered herein to lead to excellent silica dispersion. In one aspect, such a rubber composition can be provided as being sulfur cured. The sulfur curing is accomplished in a conventional manner, namely, by curing under conditions of elevated temperature and pressure for a suitable period of time. The dithiodipropionic acid may typically be characterized by having melting point in the range from 153°-159°C. Such melting point can conveniently be determined by a differential scanning calorimeter at a heating rate of 10°C/minute. In the practice of this invention, as hereinbefore pointed out, the rubber composition is comprised of at least one diene-based elastomer, or rubber. Thus, it is considered that the elastomer is a sulfur curable elastomer. Such elastomer, or rubber, may be selected, for example, from at least one of cis 1,4-polyisoprene rubber (natural and/or synthetic, and preferably natural rubber), 3,4-polyisoprene rubber, styrene/butadiene copolymer rubbers, styrene/isoprene/butadiene terpolymer rubbers, and cis 1,4-polybutadiene rubber. In one aspect the rubber is preferably of at least two diene based rubbers. Such diene based rubbers may, for example, be of homopolymers and copolymers of conjugated diene hydrocarbons and copolymers of at least one diene hydrocarbon with a vinyl aromatic compound. Such diene hydrocarbons may be, for example, selected from 1,3-butadiene and isoprene. Such vinyl aromatic compound may be, for example, styrene or alphamethylstyrene. For example, a combination of two or more rubbers is preferred such as at least two elastomers selected from cis 1,4-polyisoprene rubber (natural or synthetic, although natural is preferred), 3,4-polyisoprene rubber, isoprene/butadiene rubber, styrene/isoprene/butadiene rubber, emulsion and solution polymerization derived styrene/butadiene rubbers, cis 1,4-polybutadiene rubber, medium vinyl polybutadiene rubber having a vinyl content of from 30 to 50, high vinyl polybutadiene having a vinyl content of from 50 to 75, and emulsion polymerization prepared butadiene/acrylonitrile copolymers. In one aspect of this invention, an emulsion polymerization derived styrene/butadiene (E-SBR) might be used having a relatively conventional styrene content of 20 to 28 percent bound styrene or, for some applications, an E-SBR having a medium to relatively high bound styrene content, namely, a bound styrene content of 30 to 45 percent. The relatively high styrene content of 30 to 45% for the E-SBR can be considered beneficial for a purpose of enhancing traction, or skid resistance, of the tire tread. The presence of the E-SBR itself is considered beneficial for a purpose of enhancing processability of the uncured elastomer composition mixture, especially in comparison to a utilization of a solution polymerization prepared SBR (S-SBR). By emulsion polymerization prepared E-SBR, it is meant that styrene and 1,3-butadiene are copolymerized as an aqueous emulsion. Such are well known to those skilled in such art. The bound styrene content can vary, for example, from 5 to 50%. In one aspect, the E-SBR may also contain acrylonitrile to form a terpolymer rubber, as E-SBR, in amounts, for example, of 2 to 30 weight percent bound acrylonitrile in the terpolymer. Emulsion polymerization prepared styrene/butadiene/acrylonitrile copolymer rubbers containing 2 to 40 weight percent bound acrylonitrile in the copolymer are also contemplated as diene based rubbers for use in this invention. The solution polymerization prepared SBR (S-SBR) typically has a bound styrene content in a range of 5 to 50, preferably 9 to 36, percent. The S-SBR can be conveniently prepared, for example, by organo lithium catalyzation in the presence of an organic hydrocarbon solvent. A purpose of using S-SBR is for improved tire rolling resistance as a result of lower hysteresis when it is used in a tire tread composition. The 3,4-polyisoprene rubber (3,4-PI) is considered beneficial for a purpose of enhancing the tire's traction when it is used in a tire tread composition. The 3,4-PI and use thereof is more fully described in US-A-5 087 668. The Tg refers to the glass transition temperature which can conveniently be determined by a differential scanning calorimeter at a heating rate of 10°C per minute. The cis 1,4-polybutadiene rubber (BR) is considered to be beneficial for a purpose of enhancing the tire tread's wear, or treadwear. Such BR can be prepared, for example, by organic solution polymerization of 1,3-butadiene. The BR may be conveniently characterized, for example, by having at least a 90% cis 1,4-content. The cis 1,4-polyisoprene and cis 1,4-polyisoprene natural rubber are well known to those having skill in the rubber art. The vulcanized rubber composition should contain a sufficient amount of silica, and carbon black reinforcing filler(s) to contribute a reasonably high modulus and high resistance to tear. The combined weight of the silica and carbon black, as hereinbefore referenced, may be as low as 30 parts per 100 parts rubber, but is preferably from 35 or 45 to 90 parts by weight. The commonly employed siliceous pigments used in rubber compounding applications can be used as the silica in this invention, including pyrogenic and precipitated siliceous pigments (silica), although precipitate silicas are preferred. The siliceous pigments preferably employed in this invention are precipitated silicas such as, for example, those obtained by the acidification of a soluble silicate, e.g., sodium silicate. Such silicas might be characterized, for example, by having a BET surface area, as measured using nitrogen gas, preferably in the range of 40 to 600, and more usually in a range of 50 to 300 square meters per gram. The BET method of measuring surface area is described in the Journal of the American Chemical Society , Volume 60, page 304 (1930). The silica may also be typically characterized by having a dibutylphthalate (DBP) absorption value in a range of 100 to 400, and more usually 150 to 300. The silica might be expected to have an average ultimate particle size, for example, in the range of 0.01 to 0.05 micron as determined by the electron microscope, although the silica particles may be even smaller, or possibly larger, in size. Various commercially available silicas may be considered for use in this invention such as, only for example herein, and without limitation, silicas commercially available from PPG Industries under the Hi-Sil trademark with designations 210, 243, etc; silicas available from Rhone-Poulenc, with, for example, Zeosil 1165MP and silicas available from Degussa AG with, for example, designations VN2 and VN3, etc. It is readily understood by those having skill in the art that the rubber composition would be compounded by methods generally known in the rubber compounding art, such as mixing the various sulfur-vulcanizable constituent rubbers with various commonly used additive materials such as, for example, curing aids, such as sulfur, activators, retarders and accelerators, processing additives, such as oils, resins including tackifying resins, silicas, and plasticizers, fillers, pigments, fatty acid, zinc oxide, waxes, antioxidants and antiozonants, peptizing agents and reinforcing materials such as, for example, carbon black. As known to those skilled in the art, depending on the intended use of the sulfur vulcanizable and sulfur vulcanized material (rubbers), the additives mentioned above are selected and commonly used in conventional amounts. Typical amounts of reinforcing type carbon blacks(s), for this invention, if used, are hereinbefore set forth. It is to be appreciated that the silica coupler may be used in conjunction with a carbon black, namely, pre-mixed with a carbon black prior to addition to the rubber composition, and such carbon black is to be included in the aforesaid amount of carbon black for the rubber composition formulation. Typical amounts of tackifier resins, if used, comprise 0.5 to 10 phr, usually 1 to 5 phr. Typical amounts of processing aids comprise 1 to 50 phr. Such processing aids can include, for example, aromatic, napthenic, and/or paraffinic processing oils. Typical amounts of antioxidants comprise 1 to 5 phr. Representative antioxidants may be, for example, diphenyl-p-phenylenediamine and others, such as, for example, those disclosed in the Vanderbilt Rubber Handbook (1978), pages 344-346. Typical amounts of antiozonants comprise 1 to 5 phr. Typical amounts of fatty acids, if used, which can include stearic acid comprise 0.5 to 3 phr. Typical amounts of zinc oxide comprise 2 to 5 phr. Typical amounts of waxes comprise 1 to 5 phr. Often microcrystalline waxes are used. Typical amounts of peptizers comprise 0.1 to 1 phr. Typical peptizers may be, for example, pentachlorothiophenol and dibenzamidodiphenyl disulfide. The vulcanization is conducted in the presence of a sulfur vulcanizing agent. Examples of suitable sulfur vulcanizing agents include elemental sulfur (free sulfur) or sulfur donating vulcanizing agents, for example, an amine disulfide, polymeric polysulfide or sulfur olefin adducts. Preferably, the sulfur vulcanizing agent is elemental sulfur. As known to those skilled in the art, sulfur vulcanizing agents are used in an amount ranging from 0.5 to 4 phr, or even, in some circumstances, up to 8 phr, with a range of from 1.5 to 2.5, sometimes from 2 to 2.5, being preferred. Accelerators are used to control the time and/or temperature required for vulcanization and to improve the properties of the vulcanizate. In one embodiment, a single accelerator system may be used, i.e., primary accelerator. Conventionally and preferably, a primary accelerator(s) is used in total amounts ranging from 0.5 to 4, preferably 0.8 to 1.5, phr. In another embodiment, combinations of a primary and a secondary accelerator might be used with the secondary accelerator being used in smaller amounts (of 0.05 to 3 phr) in order to activate and to improve the properties of the vulcanizate. Combinations of these accelerators might be expected to produce a synergistic effect on the final properties and are somewhat better than those produced by use of either accelerator alone. In addition, delayed action accelerators may be used which are not affected by normal processing temperatures but produce a satisfactory cure at ordinary vulcanization temperatures. Vulcanization retarders might also be used. Suitable types of accelerators that may be used in the present invention are amines, disulfides, guanidines, thioureas, thiazoles, thiurams, sulfenamides, dithiocarbamates and xanthates. Preferably, the primary accelerator is a sulfenamide. If a second accelerator is used, the secondary accelerator is preferably a guanidine, dithiocarbamate or thiuram compound. The presence and relative amounts of sulfur vulcanizing agent and accelerator(s) are not considered to be an aspect of this invention which is more primarily directed to the use of silica as a reinforcing filler in combination with dithiodipropionic acid as a coupling agent. The presence and relative amounts of the above additives are not considered to be an aspect of the present invention which is more primarily directed to the utilization of specified blends of rubbers in rubber compositions, in combination with silica and dithiodipropionic acid, or blends of dithiodipropionic acid and bis-(3-triethoxysilylpropyl)tetrasulfide as well as, optionally, carbon black, for the reinforcement of the rubber. The mixing of the rubber composition can be accomplished by methods known to those having skill in the rubber mixing art. For example, the ingredients are typically mixed in at least two stages, namely, at least one non-productive stage followed by a productive mix stage. The final curatives are typically mixed in the final stage which is conventionally called the "productive" mix stage in which the mixing typically occurs at a temperature, or ultimate temperature, lower than the mix temperature(s) in the preceding non-productive mix stage(s). The rubber, silica and silica coupler, and carbon black if used, are mixed in one or more non-productive mix stages. The terms "non-productive" and "productive" mix stages are well known to those having skill in the rubber mixing art. The rubber composition of this invention can be used for various purposes. For example, it can be used for various tire compounds. Such tires can be built, shaped, molded and cured by various methods which are known and will be readily apparent to those having skill in such art. The invention may be better understood by reference to the following examples in which the parts and percentages are by weight unless otherwise indicated. EXAMPLE I In this Example, nicotinamide was evaluated as an alternative for a relatively commonly used silica coupling agent, bis-(3-triethoxysilylpropyl) tetrasulfide, on a carbon black as a carrier, in a silica reinforced rubber composition. The rubber compositions containing the materials set out in Table 1 were prepared in a BR Banbury rubber mixer using three separate, sequential stages of addition (mixing), namely, two non-productive mix stages and one final productive mix to temperatures of 160°C, 160°C and 120°C and times of 4 minutes, 4 minutes and 2 minutes, respectively. The amount of coupler is listed as being "variable" in Table 1 and is more specifically set forth in Table 2. It is clearly evident that utilization of the coupling agent appears to be necessary to obtain suitable cured properties in a silica containing rubber composition, or compound. Such properties include tensile strength at break, the 100 and 300% modulus values, rebound hardness, Rheovibron E' and particularly DIN abrasion resistance (lower indicate less, or better, abrasion values). Samples 2 and 3, when compared to Sample 1, which was prepared in the absence of utilization of the silica coupling agent, clearly show the advantage of the coupling agents. The properties of Sample 3, which contains the silica coupler utilized in this invention are at least equivalent or somewhat better than those exhibited by Sample 2 which contains the conventional silane coupling agent. In particular, this Example shows that the nicotinamide, as utilized in Sample 3, can provide significant improvements in modulus, rebound, hardness and abrasion when compared to control Sample 1 which does not contain coupling agent. Furthermore, these properties compare favorably to those of Sample 2 which contains the conventional silane coupling agent. EXAMPLE II In this Example, nicotinamide was evaluated as a partial replacement for the bis-(3-triethoxysilylpropyl)tetrasulfide (an organosilane tetrasulfide) or in combination with dithiodipropionic acid in a rubber composition which contains carbon black and silica particulate reinforcement. The rubber compositions containing the materials set out in Table 3 were prepared in a BR Banbury according to the mixing procedures described in Example I. The variations in the recipes are indicated in Table 4 along with the cure behavior and cured properties. Again, it is evident that a coupling agent is considered herein in a silica containing rubber compound to achieve optimum cured rubber properties. The combination of nicotinamide with the organosilane tetrasulfide (Sample 5) or dithiodipropionic acid (Sample 6) gave properties somewhat similar to Sample 7 which contained only the organosilane tetrasulfide coupling agent. The overall properties of Samples 5 and 6 are clearly superior to those of Sample 4 which lacks the presence of a coupling agent. EXAMPLE III In this Example, nicotinamide was evaluated as a coupling agent in a rubber composition which contained a quantitative amount of silica reinforcement and, thus, is considered herein as being highly silica loaded. Rubber compositions containing the materials set out in Table 5 were prepared in a BR Banbury according to the mixing procedures described in Example 1. The cure behavior and cured properties for this composition are indicated in Table 6. 1st Non-Productive NAT 2200 100.00 Carbon Black 35.00 Processing Oil 5.00 Zinc Oxide 5.00 Fatty Acid 2.00 Antioxidant 2.00 2nd Non-Productive Silica 15.00 Bis-(3-triethoxysilylpropyl) tetrasulfide 4 variable Dithiodipropionic Acid Nicotinamide variable variable Productive Sulfur 1.40 Accelerator, sulfenamide type 1.00 Sample # 1 2 3 X50S (Degussa AG) 0 3 0 Nicotinamide 0 0 2 Rheometer (150°C) Max. Torque 27.5 31.0 37.4 Min. Torque 8.7 8.0 8.3 Delta Torque 18.8 23.0 29.1 T 90 , minutes 22.5 19.5 13.8 Stress-Strain Tensile Strength, MPa 15.8 19.1 21.3 Elongation at Break, % 638 604 616 100% Modulus, MPa 1.08 1.58 1.72 300% Modulus, MPa 4.75 7.47 7.73 Rebound 100°C, % 55.4 61.6 59.1 Hardness Shore A, 100°C 45.5 51.0 55.8 Rheovibron E' at 60°C, MPa 7.94 9.11 12.72 Tan Delta at 60% .114 .104 .085 DIN Abrasion 252 156 137 1st Non-Productive NAT 2200 100.00 Carbon Black 35.00 Processing Oil 5.00 Zinc Oxide 5.00 Fatty Acid 2.00 Antioxidant 2.00 2nd Non-Productive Silica 3 15.00 Bis-(3-triethoxysilylpropyl) tetrasulfide variable Nicotinamide variable Dithiodipropionic Acid variable Productive Sulfur 1.40 Accelerator, sulfenamide type 1.00 Sample # 4 5 6 7 X50S (Degussa AG) 0 2 0 3 Nicotinamide 0 1 1 0 Dithiodipropionic Acid 0 0 1 0 Rheometer (150°C) Max. Torque 26.0 37.3 36.3 33.0 Min. Torque 4.0 4.7 6.3 5.0 Delta Torque 22.0 32.6 30.0 28.0 T 90 , minutes 22.3 14.5 20.0 18.8 Stress-Strain Tensile Strength, MPa 14.3 21.5 21.2 19.1 Elongation at Break, % 632 581 588 624 100% Modulus, MPa 1.10 2.15 2.23 1.67 300% Modulus, MPa 4.53 9.46 9.11 7.55 Rebound 100°C, % 51.7 59.0 60.5 57.9 Hardness Shore A, 100% 43.8 57.9 59.0 52.6 Rheovibron E' at 60°C, MPa 8.16 17.4 19.9 10.9 Tan Delta at 60°C .115 .086 .074 .096 DIN Abrasion 254 120 145 130 1st Non-Productive SBR 1712 68.75 BUD 1207 15.00 NAT 2200 35.00 Carbon Black 20.00 Silica 40.00 Zinc Oxide 3.00 Fatty Acid 3.00 Antioxidant 2.00 Processing Aid 10.00 Nicotinamide 3.00 2nd Non-Productive Silica 4 30.00 Productive Sulfur 2.50 Accelerator, sulfenamide type 3.00 Diphenylguanidine 2.00 Sample # 8 Rheometer, 150°C Max. Torque 50.5 Min. Torque 10.0 Delta Torque 40.5 T 90 , minutes 11.8 Stress-Strain Tensile Strength, MPa 9.50 Elongation at Break, % 326 100% Modulus, MPa 3.35 Rebound 100°C, % 53.0 Hardness Shore A, 100°C 65.6 DIN Abrasion 168

Claims: A rubber composition characterized by being comprised of (A) 100 parts by weight of at least one diene-based elastomer, (B) 25 to 100 phr of filler composed of particulate, precipitated silica and carbon black, and (C) a silica coupler selected from (i) nicotinamide or from (ii) a combination of 95 to 25 weight percent nicotinamide and, correspondingly, 5 to 75 weight percent of at least one of bis-(3-trialkoxysilylalkyl) polysulfide, which contains from 2 to 8 sulfur atoms in its polysulfide bridge, and dithiodipropionic acid; wherein the weight ratio of said silica coupler to silica is in a range of 0.01/1 to 0.2/1; wherein the weight ratio of silica to carbon black, is at least 0.1/1. The rubber composition of claim 1 characterized in that the said silica coupler consists essentially of nicotinamide. The rubber composition of claim 1 characterized in that the said silica coupler is a combination of 95 to 25 weight percent nicotinamide and, correspondingly, 5 to 75 percent of at least one of bis-(3-triethoxysilylpropyl) tetrasulfide and bis-(3-triethoxysilylpropyl) trisulfide. The rubber composition of claim 1 characterized in that the said silica coupler is a combination of 95 to 25 weight percent nicotinamide and, correspondingly, 5 to 75 weight percent dithiodipropionic acid. The rubber composition of claim 4 characterized in that said dithiodipropionic acid is 3,3'-dithiodipropionic acid. The rubber composition of any of claims 1-5 characterized in that the diene based elastomer is selected from at least one of cis 1,4-polyisoprene rubber, 3,4-polyisoprene rubber, styrene/butadiene copolymer rubbers, isoprene/butadiene rubber, styrene/isoprene/butadiene terpolymer rubbers, cis 1,4-polybutadiene rubber, medium vinyl polybutadiene rubber, high vinyl polybutadiene rubber and emulsion polymerization prepared styrene/butadiene/acrylonitrile terpolymer rubber and butadiene/acrylonitrile copolymer rubber. The rubber composition of any of claims 1-6 characterized in that the silica has a BET surface area in a range of 50 to 300 square meters per gram and a dibutylphthalate (DBP) absorption value in a range of 150 to 300. A rubber composition characterized by being comprised of (A) 100 parts by weight of at least one diene-based elastomer, (B) 25 to 90 phr particulate silica, (C) up to 30 phr carbon black, and (D) a silica coupler which is collectively composed of 90 to 55 weight percent nicotinamide, 5 to 25 weight percent of at least one of bis-(3-triethoxysilylpropyl)tetrasulfide and bis-(3-triethoxysilylpropyl)trisulfide and 5 to 25 weight percent dithiodipropionic acid; wherein the weight ratio of said silica coupler to silica is in a range of 0.01/1 to 0.2/1; wherein the weight ratio of silica to carbon black is in a range of 3/1 to 30/1; wherein the silica has a BET surface area in a range of 50 to 300 square meters per gram and a dibutylphthalate (DBP) absorption value in a range of 150 to 300. A tire characterized by having a rubber tread wherein said tread is comprised of the rubber composition of any of the preceding claims.

Inventors: SANDSTROM PAUL HARRY, WIDEMAN LAWSON GIBSON, SANDSTROM, PAUL HARRY, WIDEMAN, LAWSON GIBSON
Applicants: GOODYEAR TIRE & RUBBER, THE GOODYEAR TIRE & RUBBER COMPANY
Application year: 1996
Main classification: C08K5
IPC codes: C08L21, C08K5, C08L9, C08K3, B60C1