Process for production of rubber composition

Abstract: (i) A starting rubber (A) comprising a terminal-modified and/or coupled diene rubber and having an average glass transition temperature TgA (°C) is mixed with a specific amount of the reinforcing agent are mixed at a temperature of at least 135°C, followed by adding a starting rubber (B) comprising a terminal unmodified diene rubber and having a specific average glass transition temperature TgB (°C), and the remaining reinforcing agent and a softening agent; (ii) a starting diene rubber (A') having a specific weight average molecular weight Mw(A') and average glass transition temperature TgA' (°C) is contacted with a reinforcing agent, followed by adding a starting diene rubber (B') having a specific weight average molecular weight Mw(B) and average glass transition temperature TgB' (°C), and a softening agent to produce a rubber composition; or (iii) 100 parts by weight of a starting rubber comprising a starting rubber (A") comprising 20 to 100% by weight of a terminal-modified and/or coupled diene rubber and a starting rubber (B") comprising a terminal-unmodified and/or uncoupled rubber are mixed with a specific carbon black (X) in specific amounts at a temperature of at least 135°C, followed by adding the starting rubber (B") and the remaining carbon black and a softening agent.

Description: TECHNICAL FIELD The present invention relates to a process for producing a rubber composition superior in the tan 6 balance of the vulcanizate, more specifically a process for producing a rubber composition useful as a pneumatic tire. BACKGROUND ART Improvements have been proposed in the tan δ of tire tread rubber for reducing the fuel consumption of a vehicle. Specifically, separate mixing of ingredients and use of terminal-modified rubber have been proposed. For example, Japanese Examined Patent Publication (Kokoku) No. 5-1298 discloses a rubber composition further improving the impact resilience and tensile strength of a vulcanizate including a conjugated diene polymer having an aromatic tertiary amino group in the terminal portion of the conjugated diene polymer. On the other hand, Japanese Unexamined Patent Publication (Kokai) No. 55-10434 discloses, during the production of a rubber composition for a tire tread comprising blending a starting rubber composed of an amorphous 1,2-polybutadiene and natural rubber and/or polyisoprene rubber (or additionally including a partially conjugated diene rubber) with carbon black, first mixing a starting rubber containing at least 25% by weight of the 1,2-polybutadiene and the carbon black in a specific ratio, then adding and mixing the remaining starting rubber so as to improve the fuel economy and safety of a car. Further, Japanese Examined Patent Publication (Kokoku) No. 2-129241 proposes the improvement of the tensile strength and abrasion resistance of the vulcanizate by mixing a terminal-modified conjugated diene polymer with carbon black in an organic solvent. DISCLOSURE OF INVENTION EP 0 717 075 A describes a process for producing a rubber composition comprising (i) a total amount of 100 parts by weight of starting rubbers (A) and (B), including 30 to 90 parts by weight of the starting rubber (A) having a glass transition temperature (Tg) of -40 to 10 °C and 10 to 40 parts by weight of the starting rubber (B) which is viscoelastically incompatible with the starting rubber (A) and has a Tg of at least 20 °C lower than the Tg of the starting rubber (A) and (ii) 60 to 100 parts by weight of a reinforcing agent, wherein the starting rubber (A) and at least 80 % by weight of the total weight of the reinforcing agent are mixed in a heretic type mixer at 130 °C to 200 °C for at least 10 seconds, then the starting rubber (B) and the remaining reinforcing agent are added and mixed. This application also relates to a rubber composition and the use thereof for a tire tread. The above-mentioned method of separate mixture of ingredients, use of terminal-modified rubber, and other technologies, however, had problems such as the only slight effect in a formulation with a large oil and carbon black content and therefore improvements continued to be demanded. In the case of divided mixing, the technique was only effective for specific combinations of rubbers and the range of possible use are limited. Further, when adopting the method of first mixing the terminal-modified rubber and carbon black and then later adding the emulsion polymerized polymer, while the tan δ balance was improved, there was still the problem that the abrasion resistance fell. Accordingly, the objects of the present invention are to provide a rubber composition superior in the tan 6 balance of the vulcanizate and a process for producing a rubber composition for a tire tread giving a vulcanizate with a superior tan δ balance and improved abrasion resistance. In accordance with the present invention, there is provided a process for producing a rubber composition characterized by comprising first mixing 20 to 90 parts by weight of (A') a starting diene rubber having a weight average molecular weight Mw(A') in the range of 100,.000 to 1,200,000 with 50 to 120 parts by weight of a reinforcing agent, followed by adding 80 to 10 parts by weight of (B') a starting diene rubber having a weight average molecular weight Mw(B') of at least 400,000 and 20 to 80 parts by weight of a softening agent based upon 100 parts by weight of the total amount of the starting diene rubbers (A' ) and (B') to produce a rubber composition, wherein the weight average molecular weights are in the following relationship: 0.08 ≤ Mw(A' )/Mw(B' ) < 1 and wherein the average glass transition temperature TgA' (°C) of the starting rubber (A' ) and the average glass transition temperature TgB' (°C) of the starting rubber (B') are in the following relationship: TgA' + 20 > TgB' > TgA' - 20 According to the present invention, further, there is provided a rubber composition for a tire obtained using the above rubber composition. The present inventors found that the tan δ of a rubber composition had almost nothing to do with the rubber adsorption phase near the carbon black or other filler and that it was due to the matrix phase and succeeded in improving the tan δ balance by separating the surface of the carbon black from the matrix phase as much as possible. In the present invention, by using two types of starting diene rubber satisfying the above specific relationship (III) and mixing the starting diene rubber (A' ) and reinforcing agent, then mixing into this the starting diene rubber (B') and a softening agent, a rubber composition is obtained having an improved tan δ balance of the vulcanizate. Note that a ratio of Mw(A')/Mw(B' ) of less than 0.08 is not desirable since the reinforcement by the reinforcing agent falls, and therefore, the breakage properties and abrasion resistance fall. Conversely, when more than 1 is not preferred since the effect of the reinforcing agent in the matrix phase and the tan δ balance fall. According to the present invention, it is possible to produce a rubber composition having a good tan δ balance of the vulcanizate having a weight average molecular weight Mw(A' ) of a starting diene rubber (A') having a range of molecular weight of 100,000 to 1,200,000, preferably 120,000 to 900,000, and a weight average molecular weight Mw(B' ) of a starting diene rubber having a range of molecular weight of 400,000 or more, preferably 500,000 to 1,500,000 of the following relationship: 0.08 ≤ Mw(A' )/Mw(B') <1 preferably 0.1 ≤ Mw(A')/Mw(B') ≤ 0.8 and an average glass transition temperature TgA' (°C) of the starting rubber (A') and the average glass transition temperature TgB' (°C) of the starting rubber (B' ) of the following relationship: TgA' + 20 > TgB' > TgA' - 20 preferably TgA' + 20 > TgA' - 10 and 20 > TgA' > -45 by, first bringing 20 to 90 parts by weight, preferably 50 to 80 parts by weight, of the diene rubber (A) and 50 to 120 parts by weight, preferably 60 to 100 parts by weight, of a reinforcing agent (for example, carbon black, silica, etc.) into contact, then adding 80 to 10 parts by weight, preferably 50 to 20 parts by weight, of the starting diene rubber (B') and 20 to 80 parts by weight, preferably 35 to 70 parts by weight, per 100 parts by weight of a total weight of the starting diene rubber (A') and (B'), of a softening agent (for example, aromatic process oil, naphthene family process oil, etc. As the above starting rubber, a starting rubber dissolved in an organic solvent or a starting rubber made into an aqueous emulsion may be used. The present inventors succeeded in improving the abrasion resistance by causing the formation of a tight network composed of the polymer/carbon gel at the stage of premixing with the polymer under specific conditions using at least one type carbon black of a certain grade or higher. Therefore, by the first means, it is possible to provide a rubber composition containing carbon black used for obtaining a rubber composition for a tire tread superior in the tan δ balance of the vulcanized rubber by bringing a starting rubber containing a terminal-modified and/or coupled diene rubber having a high reactivity with carbon black into contact with the carbon black to cover the surface of the carbon black, then add a starting rubber composed of a diene rubber not terminal-modified and/or not coupled and having a low reactivity and, further, possible to obtain a rubber composition containing carbon black used for obtaining a composition for a tire tread improved in the abrasion resistance of the vulcanized rubber by setting the relationship of the content of the mixed starting rubber, carbon black, and softening agent to specific conditions. It is possible to add, to the rubber compositions of the present invention, in addition to the above polymers, reinforcing agents, and softening agents, sulfur, a vulcanization accelerator, an antioxidant, other fillers, a plasticizer, and other various additives generally blended into rubber compositions for automobile tire use. The amounts of these additives may be made the general amounts as well. For example, the amount of sulfur added may be at least 0.5 part by weight, more preferably 1.0 to 2.5 parts by weight, per 100 parts by weight of the rubber component. The vulcanization conditions also are in the general range. These additives are generally added after the completion of the first step and the second step, but the invention is not limited to this. EXAMPLES The present invention will be further illustrated by, but is by no means limited to, the following Examples. Examples I-1 to I-2 and Comparative Examples I-1 to I-4 Example I-1 and Comparative Examples I-1 to I-2 evaluate the vulcanizate properties in the case of use of SBR-1 (terminal-modified/coupled solution polymerized styrene-butadiene copolymer having glass transition temperature of -30°C, bound styrene content of 20%, vinyl content of 65%, weight average molecular weight of 350,000) and SBR-2 (33.3% oil-extended emulsion polymerized styrene-butadiene copolymer having glass transition temperature of -21°C, bound styrene content of 45%, vinyl content of 12%, and weight average molecular weight of 1,200,000) as starting rubbers and blending in the other ingredients shown in Table I-1. The results are shown in Table I-1 as well. The vulcanizate property (tan δ) was measured as described below. A Toyo Seiki Seisakusho Rheograph Solid was used to measure the viscoelasticity at an initial stress of 10%, a dynamic stress of 2%, and a frequency of 20Hz (sample width of 5 mm and temperatures of 0°C and 40°C) Note that in the vulcanizate properties, the higher than tan 6 at 0°C, the greater the frictional force on wet road surfaces (the higher the grid of the tire), while the lower the tan δ at 40°C, the smaller the energy loss in fixed energy deformation (the smaller the rolling resistance of the tire). In the present invention, the evaluation is by the value of the tan δ (0°C)/tan δ (40°C) (shown in the Table as (a)/(b)). The larger this value, the better the tan δ balance (that is, a high grip of the tire and small rolling resistance). Comparative Example I-1 (Standard Example) uses the same rubber compositions in both steps. Example I-1 charged all of the oil-extended emulsion polymerized SBR in the second step. The tan δ at 40°C fell about 10%, the temperature gradient of the tan δ increased, and it was possible to maintain the tire grip and reduce the fuel consumption. On the other hand, Comparative Example I-2 charged 30 parts by weight of the modified solution polymerized SBR in the second step. In contrast to Example I-1, the temperature gradient of the tan 6 deteriorated. Example I-2 and Comparative Examples I-3 to I-4 are Examples of use of 70 parts by weight of SBR-1 (terminal-modified/coupled solution polymerized styrene-butadiene copolymer having glass transition temperature of -30°C, bound styrene content of 20%, vinyl content of 65%, weight average molecular weight of 350,000) and 30 parts by weight of SBR-2 (33.3% oil-extended emulsion polymerized styrene-butadiene copolymer having glass transition temperature of -36°C, bound styrene content of 33%, vinyl bond content of 13%, and weight average molecular weight of 720,000) as the starting rubbers. In these Examples as well, like the above Examples, Example I-2 of the present invention showed an effect of improvement of the tan δ compared with Comparative Example I-3 (Standard Example) and Comparative Example I-4. Examples I-3 to I-4 and Comparative Examples I-5 to I-8 Comparative Example I-5 (Standard Example) and Comparative Example I-6 are Examples of use of 70 parts by weight of the above SBR-1 and 30 parts by weight of BR-1 (solution polymerized butadiene polymer having cis content of 30%, vinyl content of 13%, and weight average molecular weight of 300,000) formulated as shown in Table II. The difference of Tg of these starting rubbers was 60°C and the requirements of the present invention were not satisfied. Even if the non-modified oil extended emulsion polymerized SBR is charged in the second step, no effect of improvement in the tan δ can be recognized. Examples I-3 to I-4 and Comparative Example I-7 (Standard Example) and Comparative Example I-8 are Examples of use of 60 parts by weight of SBR-4 (terminal-modified/coupled solution polymerized styrene-butadiene polymer having glass transition temperature of -25°C, bound styrene content of 15%, vinyl content of 80%, and weight average molecular weight of 350,000) and 40 parts by weight of the above SBR-2 as the starting rubbers for formulation as shown in Table I-2. Comparative Example I-7 (Standard Example) had all of the starting rubber charged in the first step, while Comparative Example I-8 (Standard Example) used the same rubber composition in step 1 and step 2. Looking at the effects of the differences in mixing methods of the two components, as shown in Table I-2, in the method for additionally adding the starting rubber in step 2, an effect of reduction of the tan δ at 40°C arose, but the tan δ at 0°C falls and no improvement was observed in the temperature gradient of the tan δ. On the other hand, in Examples I-3 and I-4 of the present invention, as shown in Table I-2, the tan δ at 40°C fell and the temperature gradient of the tan δ was improved. Example I-3 is an Example of SBR-1 (terminal-modified/coupled solution polymerized styrene-butadiene polymer having glass transition temperature of -30°C, bound styrene content of 20%, vinyl content of 65%, and weight average molecular weight of 350,000), SBR-2 (33.3% oil extended emulsion polymerized styrene-butadiene polymer having glass transition temperature of -21°C, bound styrene content of 45%, vinyl content of 12%, and weight average molecular weight of 1,200,000), and SBR-5 (33.3% oil extended emulsion polymerized styrene-butadiene polymer having glass transition temperature of -36°C, bound styrene content of 35%, vinyl content of 14%, and weight average molecular weight of 820,000). Comparative Example I-9 is an Example where all of the ingredients except for the vulcanization system are added in the first step, while Comparative Examples I-10 and I-11 are Examples where, opposite to the present invention, the modified solution polymerized SBR is added in the second step. As shown in Table I-3, Example I-5 of the present invention, compared with Comparative Example I-9, showed a higher tan δ at 0°C and a lower tan δ at 40°C, a larger tan δ gradient, and both a maintained tire grip and a lower fuel consumption. Further, compared with Comparative Example I-10, where the modified solution polymerized SBR was added in the second step, in Comparative Example I-9, the tan δ at 0°C fell and the tan δ at 40°C rose so deterioration was shown. The same was true for Example I-6 and Comparative Example I-11. Note that the ingredients shown in Tables I-1 to I-3 were as follows: SBR-1: A terminal-modified and coupled solution polymerized styrene-butadiene copolymer having a glass transition temperature of -30°C, a bound styrene content of 20%, a vinyl content of 65%, a weight average molecular weight of 350,000 SBR-2: A 33.3% oil-extended emulsion polymerized styrene-butadiene copolymer having a glass transition temperature of -21°C, a bound styrene content of 45%, a vinyl content of 12%, and a weight average molecular weight of 1,200,000 SBR-3: A 33.3% oil-extended emulsion polymerized styrene-butadiene copolymer having a glass transition temperature of -36°C, a bound styrene content of 33%, a vinyl content of 13%, and a weight average molecular weight of 720,000. SBR-4: A terminal-modified/coupled solution polymerized styrene-butadiene copolymer having a glass transition temperature of -25°C, a bound styrene content of 15%, a vinyl content of 80%, and a weight average molecular weight of 350,000. SBR-5: A 33.3% oil-extended emulsion polymerized styrene-butadiene copolymer having a glass transition temperature of -36°C, a bound styrene content of 35%, a vinyl content of 14%, and a weight average molecular weight of 820,000. BR-1: A solution polymerized butadiene polymer having a glass transition temperature of -90°C, a cis content of 30%, a vinyl content of 13%, and a weight average molecular weight of 300,000. Carbon black 1: Nitrogen adsorption specific area of 117 m 2 /g and DBP oil absorption of 112 ml/100 g. Carbon black 2: Nitrogen adsorption specific area of 150 m 2 /g and DBP oil absorption of 127 ml/100 g. Zinc white: Zinc White No. 3 Stearic acid: Industrial stearic acid Antioxidant 6C: N-phenyl-N'-(1,3-dimethylbutyl)-p-phenylenediamine Aromatic oil: Aromatic process oil Powdered sulfur: 5% oil treated powdered sulfur Vulcanization accelerator CZ: N-cyclohexyl-2-benzothiazylsulfenamide Vulcanization accelerator DPG: Diphenylguanidine INDUSTRIAL APPLICABILITY As explained above, according to the present invention, it is possible to obtain the effects of an improvement in the tan δ balance, a reduction in the fuel consumption using a general use HPT type tire tread in which the effect of use was not sufficient with conventional end-modified SBR, and the tan δ can be reduced to a level of solution polymerization using an inexpensive emulsion polymerization SBR.

Claims: A process for producing a rubber composition characterized by comprising first mixing 20 to 90 parts by weight of (A') a starting diene rubber having a weight average molecular weight Mw(A') in the range of 100,000 to 1,200,000 with 50 to 120 parts by weight of a reinforcing agent, followed by adding 80 to 10 parts by weight of (B') a starting diene rubber having a weight average molecular weight Mw(B') of at least 400,000 and 20 to 80 parts by weight of a softening agent based upon 100 parts by weight of the total amount of the starting diene rubbers (A') and (B') to produce a rubber composition, wherein the weight average molecular weights are in the following relationship: 0.08 ≤ Mw (A')/Mw(B') < 1 and wherein the average glass transition temperature TgA' (°C) of the starting rubber (A') and the average glass transition temperature TgB' (°C) of the starting rubber (B') are in the following relationship: TgA' + 20 > TgB' > TgA' - 20 A process for producing a rubber composition as claimed in claim 1, wherein the average glass transition temperature TgA' (°C) of the starting rubber (A') is in the following range: 20 > TgA' > -45 A rubber composition for a tire obtainable by a production process according to any one of claims 1 or 2.

Inventors: KAIDO HIROYUKI, KAWAZURA TETSUJI, YATSUYANAGI FUMITO, KAIDO, HIROYUKI, KAWAZURA, TETSUJI, YATSUYANAGI, FUMITO, Kaido, Hiroyuki, Hiratsuka Factory, Kawazura, Tetsuji, Hiratsuka Factory, Yatsuyanagi, Fumito, Hiratsuka Factory
Applicants: YOKOHAMA RUBBER CO LTD, THE YOKOHAMA RUBBER CO., LTD.
Application year: 1996
Main classification: C08L15
IPC codes: C08L15