ANTIOXIDANTS CONTAINING PHENOL GROUPS AND AROMATIC AMINE GROUPS

Abstract: The invention relates to compounds of formula (I) in which R is C1-C18alkyl, C5-C8cycloalkyl, C7-C9phenylalkyl, -CH2-A-R2 or a group of formula (II), R1 is C1-C18alkyl, C5-C8cycloalkyl, C7-C9phenylalkyl or a group of formula (II), R2 is C4-C18alkyl, -(CH2)m-COOR5 or a group of formula (III), R3 is hydrogen, C5-C8cycloalkyl or C1-C12 alkyl, R4 is C1-C18alkyl, C5-C8cycloalkyl, C7-C9phenylalkyl or a group of formula (II) or (IV), A is S or SO, E is a direct bond, -CH2-, -CH2-O- or -CH2-NH-, G is -O- or -NR3-, Y is C1-C18alkyl, cyclohexyl, phenyl or alpha- or beta-naphthyl, R5 is C1-C18alkyl, and m is 1 or 2, with the provisos that either at least one of the radicals R and R4 conforms to a group of formula (II) or R is CH2-A-R2 and R4 is a group of formula (IV). The compounds are suitable for stabilizing organic material, in particular synthetic and natural rubber vulcanizates.

Description: Antioxidants containing phenol groups and aromatic amine groups The invention relates to compounds of the formula I described below, to compositions comprising these compounds, and to their use for stabilizing organic mateπals The stabilizers which have hitherto been incorporated into the molecular structure of the substrate to be stabilized are, for example, acrylates of the Ph-NH-C 6 H 4 -NH-CO-CH=CH 2 type The double bond participates in the polymeπzation or crosslinking of the substrate (US 3 975 414, US 4 743 657, D K Parker and G O Schulz, Rubber Chemistry and Technology 62,732, D E Miller et al , Rubber World 1989, 200(5), 13-16 and 18-23, and CA 112 140956x) The advantage of such stabilizers which can be incorporated is that losses due to leaching-out or diffusion can be avoided Stabilizers are already known, in particular for rubber, which conform to the formula (C 2 H 4 OCH 2 OC 2 K,SS) m C 2 H 4 OCH 2 OC 2 H 4 , R is t-C 4 -C 8 alkyl m is from 4 to 24 and R 3 is H or C C 18 alkyl (US 4 727 105) The invention relates to compounds of the formula I (I) in which R is C r C 18 alkyl, C 3 -C β cycloalkyl, C 7 -C 9 phenylalkyl, -CH 2 -A-R 2 or a group of the formula R, is C C^alkyl, C 5 -C β cycloalkyl, C 7 -C 9 phenylalkyl or a group of the formula (II), preferably methyl or tert-butyl, R 2 is C 4 -C 18 alkyl, -(CH 2 ) m -COOR 5 or a group of the formula III, preferably C„-C 12 alkyl, R 3 is hydrogen, C 3 -C B cycloalkyl or C,-C 12 alkyl, preferably hydrogen, 2-propyl, 2-(4-methylpentyl), 2-(5-methylpentyl), 2-octyl, cyclohexyl or 3-(5-methylheptyl), in particular H, R 4 is C^C^alkyl, C 3 -C 8 cycloalkyl, C 7 -C 9 phenylalkyl or a group of the formula II or IV, preferably methyl or t-butyl, A is S or SO, preferably SO, E is a direct bond, -CH 2 -, -CH 2 -O- or -CH 2 -NH-, preferably a direct bond or -CH 2 -, G is -O- or -NR 3 -, preferably -NR 3 -, Y is CrC^alkyl, cyclohexyl, phenyl or alpha- or beta-naphthyl, preferably phenyl or alpha- or beta-naphthyl, R 5 ιs C^C^alkyl, preferably C β -C 13 alkyl, and m is 1 or 2, preferably 2, with the provisos that either at least one of the radicals R and R « conforms to a group of the formula II or R is CH 2 -A-R 2 and R 4 is a group of the formula IV, where some of these compounds, which can be used as antioxidants, can be chemically incorporated into certain substrates Preference is given to compounds of the formula I described above in which R is Cι-C 8 alkyl, cyclohexyl, benzyl, -CH 2 -A-R 2 or a group of the formula II, R is Ci-Cβalkyl, cyclohexyl, benzyl or a group of the formula II, R., is C C 12 alkyl, cyclohexyl, benzyl or a group of the formula II or IV, R 2 is C 8 -C 12 alkyl or -(CH 2 ) m -COOR 5 , R 5 is C 8 -C 13 alkyl, and E is a direct bond or -CH 2 - Particular preference is given to compounds of the formula I described above in which R is C-ι-C 4 alkyl, -CH 2 -A-R 2 or a group of the formula II, R, is or a group of the formula II, R 4 is C 1 -C 4 alkyl or a group of the formula II or IV, R 2 is C 8 -C 12 alkyl, R 3 is hydrogen, C-ι-C 8 alkyl or cyclohexyl, E is a direct bond, Y is phenyl or alpha- or beta-naphthyl (C,-C 4 alkyl radicals here are preferably methyl or tert- butyl) A is particularly preferably SO Preference is furthermore given to compounds of the formula I in which R is -CH 2 -A-R 2 , Ri is Cι-C 18 alkyl, C 5 -C 8 cycloalkyl or C -C 8 phenylalkyl and R is a group of the formula IV; or in which R is a group of the formula II and R-> and R 4 , independently of one another, are C T -C^alkyl, C 5 -C 8 cycloalkyl or C -C 9 phenylalkyl, or in which R 4 is a group of the formula II and R and R,, independently of one another, are C C 18 a'kyl, C 5 -C 8 cycloalkyl or C -Cgphenylalkyl If the compounds of the formula I contain two or three groups of the formula II or IV, the groups E in the formula II are preferably identical to one another. Depending on the stated number of carbon atoms, alkyl is, for example, methyl, ethyl, n-propyl, isopropyl, n-, i-, sec- or t-butyl, pentyl, hexyl, heptyl, octyi, 2-ethylhexyl, i-octyl, decyl, nonyl, undecyl, dodecyl, tridecyl, quatrodecyl, quindecyl, sedecyl, heptadecyl or octadecyl. C 5 -C 8 Cycloalkyl is, for example, cyclopentyl, cyclohexyl, cycloheptyl or cyclooctyl. C -C 9 Phenylalkyl is, for example, benzyl, 1- or 2-phenylethyl, 3-phenylpropyl, α,α-dimethylbenzyl or 2-phenylisopropyl, preferably benzyl. The compounds of the formula I are suitable for stabilizing organic material, in particular polymers, specifically vulcanizates made from natural and/or synthetic rubber. As a consequence of their active groups, the compounds are effective as antioxidants both when incorporated and in free form Complete incorporation is not necessarily desired An incorporation rate of around 50 % is frequently regarded as advantageous The incorporation can take place via the SO group onto double bonds in the substrate. If A is sulfur, the incorporation can be preceded by oxidation by atmospheric oxygen. The incorporation into the substrate can also take place duπng use of the finished article at temperatures of, for example, around 80°C. In substrates which do not contain double bonds, the compounds of the formula I are in the form of conventional, admixed antioxidants. The invention thus also relates to compositions comprising an organic material which is sensitive to oxidative, thermal and/or photoinduced degradation and at least one compound of the formula I. Examples of organic materials to be stabilized are the following: 1 Polymers of monoolefins and diolefins, for example polypropylene, polyisobutylene, polybut-1-ene, poly-4-methylpent-1-ene, polyisoprene or polybutadiene, as well as polymers of cycloolefins, for example of cyclopentene or norbornene, furthermore polyethylene (which may optionally be crosslinked), for example high density polyethylene (HDPE), low density polyethylene (LDPE), linear low density polyethylene (LLDPE), branched low density polyethylene (BLDPE) Polyolefins, i e polymers of monoolefins exemplified in the preceding paragraph, in particular polyethylene and polypropylene, can be prepared by vaπous processes, especially by the following methods a) free-radical polymerization (normally under high pressure and at elevated temperature) b) catalytic polymerization using a catalyst that normally contains one or more metals of group IVb, Vb, Vlb or Vlll These metals usually have one or more ligands, such as oxides, halides, alcoholates, esters, ethers, amines, alkyls, alkenyls and/or aryls that may be either π- or σ-coordinated These metal complexes may be in the free form or fixed to supports, for example to activated magnesium chlonde, tιtanιum(lll) chloride, alumina or silicon oxide These catalysts may be soluble or insoluble in the polymenzation medium The catalysts can be active by themselves in the polymerization or further activators may be used, for example metal alkyls, metal hydrides, metal alkyl halides, metal alkyl oxides or metal alkyloxanes, the metals being elements of groups la, Ila and/or Ilia The activators may be modified, for example, with further ester, ether, amine or silyl ether groups These catalyst systems are usually termed Phillips, Standard Oil Indiana, Ziegler (-Natta), TNZ (DuPont), metallocene or single site catalysts (SSC) 2 Mixtures of the polymers mentioned under 1), for example mixtures of polypropylene with polyisobutylene, polypropylene with polyethylene (for example PP/HDPE, PP/LDPE) and mixtures of different types of polyethylene (for example LDPE/HDPE) 3 Copolymers of monoolefins and diolefins with each other or with other vinyl monomers, for example ethylene-propylene copolymers, linear low density polyethylene (LLDPE) and mixtures thereof with low density polyethylene (LDPE), propylene-but-1-ene copolymers, propylene-isobutylene copolymers, ethylene-but-1-ene copolymers, ethylene-hexene copolymers, ethylene-methylpentene copolymers, ethylene-heptene copolymers, ethylene- octene copolymers, propylene-butadiene copolymers, isobutylene-isoprene copolymers, ethylene-alkyl acrylate copolymers, ethylene-alkyl methacrylate copolymers, ethylene-vinyl acetate copolymers and their copolymers with carbon monoxide or ethylene-acrylic acid copolymers and their salts (ionomers) as well as terpolymers of ethylene with propylene and a diene such as hexadiene, dicyclopentadiene or ethylidene-norbornene, and mixtures of such copolymers with one another and with polymers mentioned under 1 ), for example polypropylene-ethylene-propylene copolymers, LDPE/ethylene-vmyl acetate copolymers, LDPE/ethylene-acrylic acid copolymers, LLDPE/ethylene-vinyl acetate copolymers, LLDPE/ethylene-acrylic acid copolymers and alternating or random polyalkylene-carbon monoxide copolymers and mixtures thereof with other polymers, for example polyamides 4 Hydrocarbon resms (for example C 3 -C 9 ) including hydrogenated modifications thereof (e g tackifiers) and mixtures of polyalkylenes and starch 5 Polystyrene, poly(p-methylstyrene), poly(α-methylstyrene) 6 Copolymers of styrene or α-methylstyrene with dienes or acrylic derivatives, for example styrene-butadiene, styrene-acrylonitπle, styrene-alkyl methacrylate, styrene-butadiene-alkyl acrylate, styrene-butadiene-alkyl methacrylate, styrene-maleic anhydride, styrene- acrylonitπle-methyl acrylate, high impact strength mixtures of styrene copolymers and another polymer, for example a polyacrylate a diene polymer or an ethylene-propylene- diene terpolymer, and block copolymers of styrene such as styrene-butadiene-styrene, styrene-isoprene-styrene, styrene-ethylene-butyleπe-styrene or styrene-ethylene-propylene- styrene 7 Graft copolymers of styrene or α-methylstyrene, for example styrene on polybutadiene, styrene on polybutadiene-styrene or polybutadiene-acrylonitπle copolymers, styrene and acrylonitrile (or methacrylonitnle) on polybutadiene, styrene, acrylonitrile and methyl methacrylate on polybutadiene, styrene and maleic anhydride on polybutadiene, styrene, acrylonitrile and maleic anhydnde or maleimide on polybutadiene, styrene and maleimide on polybutadiene, styrene and alkyl acrylates or alkyl methacrylates on polybutadiene, styrene and acrylonitnle on ethylene-propylene-diene teφolymers, styrene and acrylonitrile on polyalkyi acrylates or polyalkyi methacrylates, styrene and acrylonitrile on acrylate/butadiene copolymers, and mixtures thereof with the copolymers mentioned under 6), for example the copolymer mixtures known as ABS, MBS, ASA or AES polymers 8. Halogen-containing polymers such as polychloroprene, chlorinated rubber, chlorinated or chlorosulfonated polyethylene, copolymers of ethylene and chloπnated ethylene, epichlorohydrin homo- and copolymers, especially polymers of halogen-containing vinyl compounds, for example polyvinyl chloride, polyvinylidene chloride, polyvinyl fluoride, polyvinylidene fluoride; and copolymers thereof such as vinyl chloride-vinylidene chloride, vinyl chloride-vinyl acetate or vinylidene chloride-vinyl acetate. 9. Polymers derived from α,β-unsaturated acids and derivatives thereof, such as polyacrylates and polymethacrylates, polymethyl methacrylates, polyacrylamides and polyacrylonitriles, impact-modified with butyl acrylate. 10. Copolymers of the monomers mentioned under 9) with one other or with other unsaturated monomers, for example acrylonitrile-butadiene copolymers, acrylonitπle-alkyl acrylate copolymers, acrylonitrile-alkoxyalkyl acrylate copolymers, acrylonitπle-vinyl halide copolymers or acrylonitrile-alkyl methacrylate-butadiene teφolymers. 11. Polymers derived from unsaturated alcohols and amines or the acyl derivatives or acetals thereof, for example polyvinyl alcohol, polyvinyl acetate, polyvmyl stearate, polyvmyl benzoate, polyvinyl maleate, polyvinyl butyral, polyallyl phthalate or polyallylmelamine; and their copolymers with olefins mentioned in point 1 12. Homopolymers and copolymers of cyclic ethers, such as polyalkylene glycols, polyethylene oxide, polypropylene oxide or copolymers thereof with bisglycidyl ethers 13. Polyacetals such as polyoxymethylene and those polyoxymethylenes which contain comonomers, for example ethylene oxide; polyacetals modified with thermoplastic polyurethanes, acrylates or MBS. 14. Polyphenylene oxides and sulfides, and mixtures thereof with styrene polymers or polyamides. 15. Polyurethanes derived from hydroxyl-terminated polyethers, polyesters and polybutadienes on the one hand and aliphatic or aromatic polyisocyanates on the other, and precursors thereof. 16 Polyamides and copolyamides derived from diamines and dicarboxylic acids and/or from aminocarboxylic acids or the corresponding lactams, such as polyamide 4, polyamide 6, polyamide 6/6, 6/10, 6/9, 6/12, 4/6, 12/12, polyamide 11 , polyamide 12, aromatic polyamides starting from m-xylene, diamine and adipic acid, polyamides prepared from hexamethylenediamine and isophthalic and/or terephthalic acid and with or without an elastomer as modifier, for example poly-2,4,4-tπmethylhexamethylene terephthaiamide or poly-m-phenylene isophthalamide, block copolymers of the aforementioned polyamides with polyolefins, olefin copolymers, ionomers or chemically bonded or grafted elastomers, or with polyethers, e g with polyethylene glycol, polypropylene glycol or polytetramethylene glycol, or with polyamides or copolyamides modified with EPDM or ABS, and polyamides condensed during processing (RIM polyamide systems) 17 Polyureas, polyimides, polyamide-imides and polybenzimidazoles 18 Polyesters derived from dicarboxylic acids and diols and/or from hydroxycarboxyhc acids or the corresponding lactones, such as polyethylene terephthalate, polybutylene terephthalate, poly-1 ,4-dιmethylolcyclohexane terephthalate and polyhydroxybenzoates, and block polyether esters derived from hydroxyl-terminated polyethers, and also polyesters modified with polycarbonates or MBS 19 Polycarbonates and polyester carbonates 20 Polysulfones, polyether sulfones and polyether ketones 21 Crosslinked polymers derived from aldehydes on the one hand and phenols, urea or melamine on the other hand, such as phenol-formaldehyde resms, urea-formaldehyde resms and melamine-formaldehyde res s 22 Drying and non-drying alkyd resms 23 Unsaturated polyester resms derived from copolyesters of saturated and unsaturated dicarboxylic acids with polyhydric alcohols and vinyl compounds as crosslinkmg agents, and also halogen-containing modifications thereof of low flanimability 24 Crosslinkable acrylic resms derived from substituted acrylates, for example from epoxy acrylates, urethane acrylates or polyester acrylates 25 Alkyd resins, polyester resins and acrylate resins crosslinked with melamine resms, urea resms, polyisocyanates or epoxy resins 26 Crosslinked epoxy resins denved from polyepoxides, e g from bisglycidyl ethers or from cycloaliphatic diepoxides 27 Natural polymers such as cellulose, natural rubber, gelatin and chemically modified polymer-homologous derivatives thereof, for example cellulose acetates, cellulose propionates and cellulose butyrates, or the cellulose ethers such as methylcellulose, as well as rosins and derivatives 28 Blends of the aforementioned polymers (polyblends), for example PP/EPDM, poly- amide/EPDM or ABS, PVC/EVA, PVC/ABS, PVC/MBS, PC/ABS, PBTP/ABS, PC/ASA, PC/PBT, PVC/CPE, PVC/acrylates, POM/ther oplastic PUR, PC/thermoplastic PUR, POM/acrylate, POM/MBS, PPO/HIPS, PPO/PA 6 6 and copolymers, PA HDPE, PA/PP, PA/PPO 29 Aqueous emulsions of natural or synthetic rubbers, for example natural rubber latex or latices of carboxylated styrene-butadiene copolymers 30 Natural and synthetic organic substances which constitute pure monomer compounds or mixtures thereof, for example mineral oils, animal or vegetable fats oils and waxes, or oils, waxes and fats based on synthetic esters (e g phthalates, adipates phosphates or tπmellitates), and blends of synthetic esters with mineral oils in any desired ratios by weight, as are employed for example as spinning preparations, and the aqueous emulsions thereof Of these, preference is given to substances containing double bonds since this allows the advantage of chemical incorporation into the substrate to be utilized, in particular elastomers Examples of elastomers which can be present in the novel compositions are the following materials 1 Polydienes, for example polybutadiene, polyisoprene and polychloroprene, block polymers, for example styrene-butadiene-styrene, styrene-isoprene-styrene and acrylonitπle-butadiene copolymers Copolymers of monoolefins and diolefins with one another or with other vinyl monomers, for example ethylene-alkyl acrylate copolymers, ethylene-alkyl methacrylate copolymers, ethylene-vinyl acetate copolymers and terpolymers of ethylene with propylene and a diene, such as hexadiene, dicyclopentadiene or ethy denenorbornene Halogen-containing polymers, for example polychloroprene, chlorinated rubber, chlorinated or chlorosulfonated polyethylene, epichlorohydrin homopolymers and copolymers, chlorotπfluoroethylene copolymers, polymers of halogen-containing vinyl compounds, for example polyvinylidene chloride and polyvinylidene fluoride, and copolymers thereof, such as vinyl chloπde-viny dene chloπde, vinyl chloride-vinyl acetate and vinylidene chloride-vinyl acetate Polyurethanes derived from polyethers, polyesters and polybutadiene containing terminal hydroxyl groups on the one hand and aliphatic or aromatic polyisocyanates on the other hand, and precursors thereof 5 Natural rubber 6 Mixtures (polyblends) of the abovementioned polymers 7 Aqueous emulsions of natural or synthetic rubbers, for example natural rubber latex or latices of carboxylated styrene-butadiene copolymers These elastomers can, if desired, be in the form of latices and can be stabilized as such It is also possible for vulcanizates to be stabilized Preference is given to compositions in which the elastomer is a polydiene,. such as polybutadiene rubber The incorporation into the organic mateπals can take place, for example, by mixing-in the novel compounds or mixtures and, if desired, further additives by customary methods of the art Polymers, in particular synthetic polymers, can be incorporated before or during shaping or by applying the dissolved or dispersed compounds to the polymers if necessary with subsequent evaporation of the solvent In the case of elastomers, these can also be stabilized as latices A further, preferred way of using the novel compounds compnses addition thereof during the production of rubber mixtures together with the conventional other mixture constituents and ingredients by conventional techniques in, for example, Banbury mixers, on mixing rolls or in mixing extruders In particular, the presence of the compounds of the formula I duπng the mixing process and during subsequent shaping and the crosslinking reaction (vulcanization to give the finished rubber article) and dunng use of the finished article produces a chemical linkage to the elastomer/polymer This can be determined, for example, analytically from the higher residual content of additive - measured from residual nitrogen - compared with compounds which cannot be incoφorated The invention therefore relates in particular to compositions in which compounds of the formula I are incorporated into or chemically linked to an elastomer/polymer The novel compounds or mixtures can also be added to the plastics to be stabilized in the form of a masterbatch which comprises these compounds, for example, in a concentration of from 2 5 to 25 % by weight The novel polymer compositions can be used in various forms or converted into various products, for example as (to) films, fibres, tapes moulding compositions profiles or as binders for paints, adhesives or adhesive cements In addition to the novel compounds or mixtures, the novel compositions in particular if they comprise organic, preferably synthetic, polymers, can also comprise further conventional additives known to the person skilled in the art, for example 1 Antioxidants 1 1 Alkylated monophenols, for example 2,6-dι-tert-butyl-4-methylphenol, 2-butyl-4,6- dimethylphenol, 2,6-dι-tert-butyl-4-ethylphenol, 2,6-dι-tert-butyl-4-n-butylphenol, 2,6-dι-tert- butyl-4-ι obutylphenol, 2,6-dι-cyclopentyl-4-methylphenol, 2-(α-methylcyclohexyl)-4,6- dimethylphenol, 2,6-dιoctadecyl-4-methylphenol, 2,4,6-tπcyclohexylphenol, 2,6-dι-tert-butyl- 4-methoxymethylphenol, 2,6-dιnonyl-4-methylphenol, 2,4-dιmethyl-6-(1 '-methylundec-1 '-yl)- phenol, 2,4-dιmethyl-6-(1 '-methylheptadec-1'-yl)phenol, 2,4-dιmethyl-6-(1 -methyl tπdec-1 '-yl)phenol and mixtures thereof 1 2 Alkylthiomethylphenols, for example 2,4-dιoctylthιomethyl-6-tert-butylphenol, 2,4- dιoctylthιomethyl-6-methylphenol, 2,4-dιoctylthιomethyl-6-ethylphenol, 2,6-dιdodecyl- thιomethyl-4-nonylphenol 1 3 Hvdroquinones and alkylated hydroquinones, for example 2,6-dι-tert-butyl-4- methoxyphenol, 2,5-dι-tert-butylhydroquιnone, 2,5-dι-tert-amylhydroquιnone, 2,6-dιphenyl-4- octadecyloxyphenol, 2,6-dι-tert-butylhydroquιnone, 2,5-dι-tert-butyl-4-hydroxyanιsole, 3,5-dι- tert-butyl-4-hydroxyanιsole, 3,5-dι-tert-butyl-4-hydroxyphenyl stearate, bιs(3,5-dι-tert-butyl-4- hydroxyphenyl) adipate 1 4 Tocopherols, for example α-tocopherol, β-tocopherol, γ-tocopherol, δ-tocopherol and mixtures thereof (vitamin E) 1 5 Hydroxylated thiodiphenyl ethers, for example 2,2'-thιobιs(6-tert-butyl-4-methylphenol), 2,2'-thιobιs(4-octylphenol), 4 4'-thιobιs(6-tert-butyl-3-methylphenol), 4,4'-thιobιs(6-tert-butyl- 2-methylphenol), 4,4'-thιobιs(3,6-dι-sec-amylphenol), 4,4'-bιs(2 6-dιmethyl-4-hydroxyphenyl) disulfide 1 6 Alkylidenebisphenols, for example 2,2'-methylenebιs(6-tert-butyl-4-methylphenol), 2,2'- methylenebιs(6-tert-butyl-4-ethylphenol), 2,2'-methylenebιs[4-methyl-6-(α-methylcyclohexyl)- phenol], 2,2'-methylenebιs(4-methyl-6-cyclohexylphenol), 2,2'-methylenebιs(6-nonyl-4- methylphenol), 2,2'-methylenebιs(4,6-dι-tert-butylphenol), 2,2'-ethylιdenebιs(4,6-dι-tert- butylphenol), 2,2'-ethylιdenebιs(6-tert-butyl-4-ιsobutylphenol), 2,2'-methylenebιs[6-(α- methylbenzyl)-4-nonylphenol], 2,2'-methylenebιs[6-(α,α-dιmethylbenzyl)-4-nonylphenol], 4,4'-methylenebιs(2,6-dι-tert-butylphenol), 4,4'-methylenebιs(6-tert-butyl-2-methylphenol), 1 ,1-bιs(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 2,6-bιs(3-tert-butyl-5-methyl-2- hydroxybenzyl)-4-methylphenol, 1 ,1 ,3-tπs(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 1 ,1- bιs(5-tert-butyl-4-hydroxy-2-methylphenyl)-3-n-dodecylmercaptobutane, ethylene glycol bιs[3,3-bιs(3'-tert-butyl-4'-hydroxyphenyl)butyrate], bιs(3-tert-butyl-4-hydroxy-5- methylphenyl)dιcyclopentadιene, bιs[2-(3'-tert-butyl-2'-hydroxy-5'-methylbenzyl)-6-tert-butyl- 4-methylphenyl] terephthalate, 1 ,1-bιs(3,5-dιmethyl-2-hydroxyphenyl)butane, 2,2-bιs(3,5-dι- tert-butyl-4-hydroxyphenyl)propane, 2,2-bιs(5-tert-butyl-4-hydroxy-2-methylphenyl)-4-n- dodecylmercaptobutane, 1 ,1 ,5,5-tetra-(5-tert-butyl-4-hydroxy-2-methylphenyl)pentane 1 7. O-, N- and S-benzyl compounds, for example 3,5,3', 5'-tetra-tert-butyl-4,4 - dihydroxydibenzyl ether, octadecyl 4-hydroxy-3,5-dιmethylbenzylmercaptoacetate, tπs(3,5- dι-tert-butyl-4-hydroxybenzyl)amme, bιs(4-tert-butyl-3-hydroxy-2,6-dιmethylbenzyl) dithioterephthalate, bιs(3,5-dι-tert-butyl-4-hydroxybenzyl) sulfide, isooctyl 3,5-dι-tert-butyl-4- hydroxybenzylmercaptoacetate 1 8 Hvdroxybenzylated malonates. for example dioctadecyl 2,2-bιs(3,5-dι-tert-butyl-2- hydroxybenzyl)malonate, dioctadecyl 2-(3-tert-butyl-4-hydroxy-5-methylbenzyl)malonate, di- dodecyl mercaptoethyl-2,2-bιs(3,5-dι-tert-butyl-4-hydroxybenzyl)malonate, dι-[4-(1 1 ,3,3- tetramethylbutyl)phenyl] 2,2-bιs(3,5-dι-tert-butyl-4-hydroxybenzyl)malonate 1 9 Aromatic hydroxybenzyl compounds, for example 1 ,3,5-tπs(3,5-dι-tert-butyl-4- hydroxybenzyl)-2,4,6-tπmethylbenzene, 1 ,4-bιs(3,5-dι-tert-butyl-4-hydroxybenzyl)-2, 3,5,6- tetramethylbenzene, 2,4,6-tπs(3,5-dι-tert-butyl-4-hydroxybenzyl)phenol 1 10 Triazine compounds, for example 2,4-bιsoctylmercapto-6-(3,5-dι-tert-butyl-4- hydroxyanιlιno)-1 ,3,5-tnazιne, 2-octylmercapto-4,6-bιs(3,5-dι-tert-butyl-4-hydroxyanιlιno)- 1 ,3,5-tπazιne, 2-octylmercapto-4,6-bιs(3,5-dι-tert-butyl-4-hydroxyphenoxy)-1 ,3 5-trιazιne, 2,4,6-tπs(3,5-dι-tert-butyl-4-hydroxyphenoxy)-1 ,2,3-tπazιne, 1 ,3,5-tπs(3,5-dι-tert-butyl-4- hydroxybenzyl) isocyanurate, 1 ,3,5-tπs(4-tert-butyl-3-hydroxy-2,6-dιmethylbenzyl) isocyanurate, 2,4,6-tπs(3,5-dι-tert-butyl-4-hydroxyphenylethyl)-1 ,3,5-trιazιne, 1 ,3 5-trιs(3,5-dι- tert-butyl-4-hydroxyphenylpropιonyl)hexahydro-1 ,3,5-tπazιne, 1 ,3,5-tπs(3,5-dιcyclohexyl-4- hydroxybenzyl) isocyanurate 1 11 Benzylphosphonates. for example dimethyl 2,5-dι-tert-butyl-4-hydroxybenzyl- phosphonate, diethyl 3,5-dι-tert-butyl-4-hydroxybenzylphosphonate, dioctadecyl 3,5-dι-tert- butyl-4-hydroxybenzylphosphonate, dioctadecyl 5-tert-butyl-4-hydroxy-3- methylbenzylphosphonate, the calcium salt of the monoethyl ester of 3,5-dι-tert-butyl-4- hydroxybenzylphosphonic acid 1 12 Acylaminophenols. for example 4-hydroxylauranιlιde, 4-hydroxystearanιlιde, octyi N-(3,5-dι-tert-butyl-4-hydroxyphenyl)ca rbamate 1 13 Esters of β-(3,5-dι-tert-butyl-4-hvdroxyphenyl)propιonιc acid with mono- or polyhydric alcohols, e g with methanol, ethanol, octanol, octadecanol, 1 ,6-hexanedιol, 1 ,9-nonanedιol, ethylene glycol, 1 ,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, tπethylene glycol, pentaerythritol, tris(hydroxyethyl) isocyanurate, N,N'-bis(hydroxyethyl)- oxalamide, 3-thιaundecanol, 3-thiapentadecanol, tπmethylhexanediol, trimethylolpropane, 4- hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane. 1.14. Esters of tH5-tert-butyl-4-hvdroxy-3-methylphenyl)propionic acid with mono- or polyhydric alcohols, e.g. with methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1 ,9- nonanediol, ethylene glycol, 1 ,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tπs(hydroxyethyl) isocyanurate, N,N - bis(hydroxyethyl)oxalamide, 3-thiaundecanol, 3-thιapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane. 1 15. Esters of β-(3,5-dicvclohexyl-4-hvdroxyphenyl)propionιc acid with mono- or polyhydric alcohols, e.g. with methanol, ethanol, octanol, octadecanol, 1 ,6-hexanediol, 1 ,9-nonanediol, ethylene glycol, 1 ,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tπs(hydroxyethyl) isocyanurate, N,N'-bis(hydroxyethyl)- oxalamide, 3-thιaundecanol, 3-thιapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-tπoxabιcyclo[2.2.2]octane. 1 16 Esters of 3, 5-dι-tert-butyl-4-hydroxyphenyl acetic acid with mono- or polyhydric alcohols, e g with methanol, ethanol, octanol, octadecanol, 1 ,6-hexanedιol, 1 ,9-nonanedιol, ethylene glycol, 1 ,2-propanedιol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tπs(hydroxyethyl) isocyanurate, N,N'-bιs- (hydroxyethyl)oxalamιde, 3-thιaundecanol, 3-thιapentadecanol, tπmethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-tπoxabιcyclo[2.2.2]octane. 1.17. Amides of f3-(3,5-di-tert-butyl-4-hvdroxyphenyl)propionic acid e.g. N,N , -bis(3,5-di-tert- butyl-4-hydroxyphenylpropionyl)hexamethylenedιamine, N,N'-bis(3,5-di-tert-butyl-4- hydroxyphenylpropionyl)trimethylenedιamine, N,N'-bιs(3,5-di-tert-butyl-4-hydroxyphenyl- propιonyl)hydrazιne. 1.18. Dihvdroquinoline derivatives, for example polymerized 2,2,4-trimethyl-1 ,2- dihydroquinoline 1.19 Diphenylamines and other diarylamine derivatives, for example di(octylphenyl)amine 1 20 p-Phenylenedιamιnes. for example N-phenyl-N'-isopropyl-p-phenylenediamine, N-phenyl-N'-(1 ,3-dιmethylbutyl)-p-phenylenedιamιne and N,N'-dιphenyl-p-phenylenedιamιne 1 21 Further antioxidants. for example 2-mercapto-4(S)-methylbenzιmιdazole, 2-mercaptotoluιmιdazole, and their zinc salts 1 22 Naphthylammes, for example N-phenyl-α-naphthylamme and N-phenyl-β- naphthylamme (PBNA) 2 UV-absorbers and light stabilizers 2 1 2-(2'-Hvdroχyphenyl)benzotπazoles, for example 2-(2'-hydroxy-5'-methylphenyl)- benzotπazole, 2-(3',5'-dι-tert-butyl-2'-hydroxyphenyl)benzotπazole, 2-(5'-tert-butyl-2'- hydroxyphenyl)benzotπazole, 2-(2'-hydroxy-5'-(1 ,1,3,3-tetramethylbutyl)phenyl)- benzotπazole, 2-(3',5'-dι-tert-butyl-2'-hydroxyphenyl)-5-chlorobenzotrιazole, 2-(3'-tert-butyl- 2'-hydroxy-5'-methylphenyl)-5-chlorobenzotπazole, 2-(3'-sec-butyl-5'-tert-butyl-2'- hydroxyphenyl)-benzotπazole, 2-(2'-hydroxy-4'-octoxyphenyl)benzotπazole, 2-(3',5'-dι-tert- amyl-2'-hydroxyphenyl)benzotπazole, 2-(3',5'-bιs(α,α-dιmethylbenzyl)-2'-hydroxyphenyl)- benzotπazole, a mixture of 2-(3'-tert-butyl-2'-hydroxy-5'-(2-octyloxycarbonylethyl)phenyl)-5- chlorobenzotπazole, 2-(3 -tert-butyl-5'-[2-(2-ethylhexyloxy)carbonylethyl]-2'-hydroxyphenyl)- 5-chlorobenzotnazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-methoxycarbonylethyl)phenyl)-5- chlorobenzotπazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-methoxycarbonylethyl)phenyl)- benzotnazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-octyloxycarbonylethyl)phenyl)benzotnazole, 2-(3'-tert-butyl-5'-[2-(2-ethylhexyloxy)carbonylethyl]-2'-hydroxyphenyl)benzotπazole, 2-(3'- dodecyl-2'-hydroxy-5'-methylphenyl)benzotπazole, and 2-(3'-tert-butyl-2'-hydroxy-5'-(2- ιsooctyloxycarbonylethyl)phenylbenzotπazole, 2,2'-methylenebιs[4-(1 ,1 ,3,3-tetramethylbutyl)- 6-benzotπazol-2-ylphenol], the transesteπfication product of 2-[3'-tert-butyl-5'-(2-methoxy- carbonylethyl)-2'-hydroxyphenyl]benzotπazole with polyethylene glycol 300, [RCH 2 CH 2 COO(CH 2 ) 3 - — where R = 3'-tert-butyl-4'-hydroxy-5'-2H-benzotrιazol-2-ylphenyl 2 2 2-Hydroxybenzophenones. for example the 4-hydroxy, 4-methoxy, 4-octoxy, 4-decyloxy, 4-dodecyloxy, 4-benzyloxy, 4,2',4'-tnhydroxy and 2'-hydroxy-4,4'-dιmethoxy derivative 2.3. Esters of substituted or unsubstituted benzoic acids, for example 4-tert-butyl-phenyl salicylate, phenyl salicylate, octylphenyl salicylate, dibenzoylresorcinol, bιs(4-tert- butylbenzoyl)resorcιnol, benzoylresorcmol, 2,4-di-tert-butylphenyl 3,5-di-tert-butyl-4- hydroxybenzoate, hexadecyl 3,5-di-tert-butyl-4-hydroxybenzoate, octadecyl 3,5-di-tert-butyl- 4-hydroxybenzoate, 2-methyl-4,6-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxybenzoate. 2.4. Acrylates, for example ethyl α-cyano-β,β-diphenylacrylate or isooctyl α-cyano-β,β- diphenylacrylate, methyl α-carbomethoxycinnamate, methyl α-cyano-β-methyl-p-methoxy- cinnamate or butyl α-cyano-β-methyl-p-methoxycinnamate, methyl α-carbomethoxy-p- methoxycmnamate and N-(β-carbomethoxy-β-cyanovinyl)-2-methylιndolιne 2.5. Nickel compounds, for example nickel complexes of 2,2'-thio-bιs-[4-(1 ,1 ,3,3- tetramethylbutyl)phenol], such as the 1 :1 or 1 :2 complex, with or without additional ligands such as n-butylamine, triethanolamine or N-cyclohexyldiethanolamme, nickel dibutyldithiocarbamate, nickel salts of monoalkyl esters, such as of the methyl or ethyl ester, of 4-hydroxy-3,5-di-tert-butylbenzylphosphonιc acid, nickel complexes of ketoximes, e.g. of 2-hydroxy-4-methylphenyl undecyl ketoxime, nickel complexes of 1-phenyl-4-lauroyl-5- hydroxypyrazole, with or without additional ligands 2 6 Sterically hindered amines, for example bιs(2,2,6,6-tetramethylpιpeπdyl) sebacate, bιs(2,2,6,6-tetramethylpιpeπdyl) succinate, bιs(1 ,2,2,6,6-pentamethylpιperιdyl) sebacate, bιs(1 ,2,2,6,6-pentamethylpιperιdyl) n-butyl 3,5-dι-tert-butyl-4-hydroxybenzylmalona.e, the condensate of 1-hydroxyethyl-2,2,6,6-tetramethyl-4-hydroxypιpendιne and succinic acid, the condensate of N,N'-bis(2,2,6,6-tetramethyl-4-pιpeπdyl)hexamethylenedιamιne and 4-tert- octylamino-2,6-dichloro-1 ,3,5-s-triazine, tris(2,2,6,6-tetramethyl-4-pιpeπdyl) nitπlotπacetate, tetrakis(2,2,6,6-tetramethyl-4-piperidyl) 1 ,2,3,4-butanetetraoate, 1 ,1 '-(1 ,2-ethanedιyl)- bis(3,3,5,5-tetramethylpiperazinone), 4-benzoyl-2,2,6,6-tetramethylpιperidιne, 4-stearyloxy- 2,2,6,6-tetramethylpiperidine, bis(1,2,2,6,6-pentamethylpipeπdyl) 2-n-butyl-2-(2-hydroxy-3,5- di-tert-butylbenzyl)malonate, 3-n-octyl-7,7,9,9-tetramethyl-1 ,3,8-tπazaspiro[4.5]decan-2,4- dione, bis(1-octyloxy-2,2,6,6-tetramethylpiperidyl) sebacate, bιs(1-octyloxy-2,2,6,6-tetra- methylpiperidyl) succinate, the condensate of N,N'bis(2,2,6,6-tetramethyl-4-piperidyl)- hexamethylenediamine and 4-morpholino-2,6-dichloro-1 ,3,5-tπazine, the condensate of 2-chloro-4,6-di(4-n-butylamιno-2,2,6,6-tetramethylpiperidyl)-1 ,3,5-tπazιne and 1 ,2-bis(3- aminopropylamino)ethane, the condensate of 2-chloro-4,6-di(4-n-butylamino-1 ,2,2,6,6- pentamethylpiperidyl)-1 ,3,5-triazιne and 1 ,2-bis(3-aminopropylamino)ethane, 8-acetyl-3- dodecyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]decane-2,4-dιone, 3-dodecyl-1 -(2,2,6,6- tetramethyl-4-piperidyl)pyrrolidine-2,5-dione, 3-dodecyl-1-(1 ,2,2,6,6-pentamethyl-4- piperidyl)pyrrolιdιne-2,5-dione. 2.7. Oxalamides, for example 4,4'-dioctyloxyoxanilide, 2,2'-diethoxyoxanilide, 2,2'-dioctyloxy- 5,5'-di-tert-butyloxanilide, 2,2'-didodecyloxy-5,5'-di-tert-butyloxanilide, 2-ethoxy-2'- ethyloxanilide, N,N'-bis(3-dimethylaminopropyl)oxalamide, 2-ethoxy-5-tert-butyl-2'- ethyloxanilide and its mixture with 2-ethoxy-2'-ethyl-5,4'-di-tert-butyloxanilide and mixtures of o- and p-methoxy disubstituted oxanilides and mixtures of o- and p-ethoxy disubstituted oxanilides 2.8. 2-(2-Hydroxyphenyl)-1 ,3.5-triazines. for example 2,4,6-tris(2-hydroxy-4-octyloxyphenyl)- 1 ,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1 ,3,5-triazine, 2-(2,4-dihydroxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1 ,3,5-tπazιne, 2,4-bis(2-hydroxy-4- propoxyphenyl)-6-(2,4-dimethylphenyl)-1 ,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6- bis(4-methylphenyl)-1 ,3,5-triazine, 2-(2-hydroxy-4-dodecyloxyphenyl)-4,6-bis(2,4- dιmethylphenyl)-1 ,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-butyloxypropyloxy)phenyl]-4,6- bιs(2,4-dιmethylphenyl)-1 ,3,5-triazιne, 2-[2-hydroxy-4-(2-hydroxy-3-octyloxypropoxy)- phenyl]-4,6-bis(2,4-dimethylphenyl)-1 ,3,5-triazine. 3 Metal deactivators. for example, N,N'-diphenyloxalamιde, N-salicylal-N'-sa cyloyl hydrazine, N,N'-bιs(salicyloyl)hydrazιne, N,N'-bιs(3,5-dι-tert-butyl-4-hydroxyphenyl- propιonyl)hydrazιne, 3-salιcyloylamino-1 ,2,4-tπazole, bιs(benzylιdene)oxalyl dihydrazide, oxanihde, isophthaloyl dihydrazide, sebacoyl bisphenylhydrazide, N,N'-dιacetyladιpoyl dihydrazide, N,N'-bis(salicyloyl)oxalyl dihydrazide, N,N'-bιs(salιcyloyl)thιopropιonyl dihydrazide. 4. Phosphites and phosphonites. for example triphenyl phosphite, diphenyl alkyl phosphites, phenyl dialkyl phosphites, tris(nonylphenyl) phosphite, trilauryl phosphite, trioctadecyl phosphite, distearyl pentaerythritol diphosphite, tris(2,4-di-tert-butylphenyl)phosphite, diisodecyl pentaerythritol diphosphite, bis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite, bis(2,6-di-tert-butyl-4-methylphenyl)pentaerythritol diphosphite, bisisodecyloxypentaerythritol diphosphite, bis(2,4-di-tert-butyl-6-methylphenyl)pentaerythritol diphosphite, bis(2,4,6-tri-tert- butylphenyl)pentaerythritol dipnosphite, tristearyl sorbitol triphosphite, tetrakis(2,4-di-tert- butylphenyl) 4,4'-biphenylene diphosphonite, 6-isooctyloxy-2,4,8,10-tetra-tert-butyl-12H- dibenzo[d,g]-1 ,3,2-dioxaphosphocin, 6-fluoro-2 ,4,8, 10-tetra-tert-butyl-12-methyl- dιbenzo[d,g]-1,3,2-dιoxaphosphocιn, bιs(2,4-dι-tert-butyl-6-methylphenyl) methyl phosphite, bιs(2,4-dι-tert-butyl-6-methylphenyl) ethyl phosphite 5 Peroxide scavengers, for example esters of β-thiodipropionic acid, for example the lauryl, stearyl, mynstyl or tridecyl esters, mercaptobenzimidazole or the zinc salt of 2-mercapto- benzimidazole, zinc dibutyldithiocarbamate, dioctadecyl disulfide, pentaerythritol tetrakιs(β- dodecylmercapto)propιonate 6 Polyamide stabilizers, for example copper salts in combination with iodides and/or phosphorus compounds and salts of divalent manganese 7 Basic co-stabilizers, for example melamine, polyvinylpyrrolidone, dicyandiamide, triallyl cyanurate, urea deπvatives, hydrazine deπvatives, amines, polyamides, polyurethanes, alkali metal salts and alkaline earth metal salts of higher fatty acids, for example calcium stearate, zinc stearate, magnesium behenate, magnesium stearate, sodium ricinoleate, and potassium palmitate, antimony pyrocatecholate or tin pyrocatecholate 8 Nucleating agents, for example 4-tert-butylbenzoιc acid, adipic acid and diphenylacetic 9 Fillers and reinforcing agents, for example calcium carbonate, silicates, glass fibres, asbestos, talc, kaolin, mica, barium sulfate, metal oxides and hydroxides, carbon black, graphite 10 Other additives, for example plasticizers, lubricants, emuisifiers, pigments, optical brighteners, flameproofing agents, antistatic agents and blowing agents 11 Benzofuranones and indolinones, for example those described in US-A-4 325 863, US-A-4 338 244, US-A-5 175 312, US-A-5 216 052, US-A-5 252 643, DE-A-4 316 611 , DE- A-4 316 622, DE-A-4 316 876, EP-A-0 589 839 or EP-A-0 591 102 or 3-[4-(2-acetoxy- ethoxy)phenyl]-5,7-dι-tert-butyl-benzofuran-2-one, 5,7-dι-tert-butyl-3-[4-(2-stearoyloxy- ethoxy)-phenyl]benzofuran-2-one, 3,3'-bιs[5,7-dι-tert-butyl-3-(4-[2-hydroxyethoxy]phenyl)- benzofuran-2-one], 5,7-dι-tert-butyl-3-(4-ethoxyphenyι)benzofuran-2-one, 3-(4-acetoxy-3,5- dιmethylphenyl)5,7-dι-tert-butyl-benzofuran-2-one, 3-(3,5-dιmethyl-4-pιvaloyloxyphenyl)-5,7- dι-tert-butyl-benzofuran-2-one 12. Crosslinking agents, for example organic peroxides, sulfur, sulfur-containing vulcanization accelerators, zinc oxide and vulcanization activators. The compounds of the formula I can be prepared by or analogously to known processes. Starting materials for A' (T - S) are the compounds of the formulae C and D: The methyl ester C (Z = OCH 3 ) is synthesized, for example, by the methods described in Patent Specifications US-A 4 759 862 and US-A 4 857 572 by thioalkylation of the corresponding, known 3'-substituted methyl 3-(4'-hydroxyphenyl)propionates D (for example methyl 3-(3'-t-butyl- -hydroxyphenyl)propionate). The acid chloride C (Z = Cl) is prepared from the corresponding acid (Z = OH) by processes known from the literature. Starting materials for B and B' are the compounds of the formulae E and E': E' The methyl esters E and E' (L = OCH 3 and E = direct bond or -CH 2 -) are synthesized, for example, analogously to the synthesis of C, starting from the corresponding 2,4- or 2.6-dιsubstιtuted phenols, formaldehyde and methyl thioglycolate or 3-thιopropιonate The compounds F and F' (Q = CH 2 -O and CH 2 -NH respectively) F' can be prepared analogously to the compounds described in US-A 4 759 862 and US-A 4 857 572. a) Preparation of the compounds A ' (T - SO), B and B' (A - SO) The sulfoxides A' (T = SO, E = direct bond), B and B' (A = SO) are prepared by oxidation of the corresponding thioethers A' (T = S), B and B' (A = S), as described in EP 473 549. Examples of oxidants which can be used are H 2 0 2 , t-butyl hydroperoxide and cumyl hydroperoxide. Suitable solvents are hydrocarbons, ethers and, for example, acetone. b) Variant for E = direct bond or CH 2 : by reacting activated acid derivatives G, H and H' with the aromatic amine or phenol Ar-NH-C 6 H 4 -G-H (W) (G = O or NR 3 ), see c). G, H and H' are prepared as described above by oxidation of the corresponding thioethers C, E and E' (see above). Depending on the conditions, side reactions of the sulfoxide group must also be expected here (Pummerer reaction). c) Variant for E = CH 2 0 or CH 2 NH-: Reaction of the sulfoxides J or J' J with the activated derivative aryl-NH-C 6 H 4 -NR 3 -C(=0)-Q (W) (Q = halogen or another activating group) d) Preparation of the compounds A', B and B' (A = S) where E - CH 2 -0 or CH 2 NH The urethanes or ureas B and B' (E = O or NH, G = NR 3 ) can be synthesized by reacting a compound aryl-NH-C 6 H 4 -NR 3 -C(=O)-Q (W') (Q = halogen or another activating group) with the corresponding alcohol or amino derivative F or F' (E = CH 2 -O or CH 2 -NH). e) Preparation of the compounds A, B and B' (A = S) where E = direct bond or CH 2 By substitution of a suitable [activated] acid derivative C, E or E' with an aromatic amine or phenol of the formula Ar-NH-C 6 H 4 -G-H (G = O or NR 3 ) (W), where Z is, inter alia, OCH 3 , halogen or OH. The reaction is generally carried out without solvent or catalyst or in an inert solvent and/or using a catalyst or an auxiliary, which can be employed in a molar excess of up to five-fold. The reaction temperatures are in the range from 0°C to 250°C. If Z = halogen, a tertiary amine is preferably used as acid scavenger. In the case of polyfunctionalized compounds an at least two-fold molar excess of W or W is used correspondingly The examples below serve to illustrate the invention in greater detail. In the examples and in the remainder of the description and in the claims, parts and percentages are by weight, unless stated otherwise. Example 1 : Methyl 3-(3'-t-butyl-4'-hydroxy-5-octylthιomethylphenyl)propιonate 29.94 g (0.127 mol) of methyl 3-(3'-t-butyl-4-hydroxyphenyl)propionate, 20.39 g (0.139 mol) of octanethiol, 7 61 g (0.253 mol) of paraformaldehyde and 0.285 g of dimethylamine are refluxed for 15 hours in 30 ml of DMF. Evaporation of the solvent and drying at 60°C/0.015 mbar gives a yellow oil (51 g), which can be further purified by distillation (b.p. 80-90°C/0.06 mbar) and flash chromatography Analysis for C 23 H 38 O 3 S: calc. C 70.01 ; H 9.71 ; S 8.12 %; found C 69.92; H 9.64; S 8.15 %. Example 2: Methyl 3,5-di-t-butyl-2-hydroxybenzylthioacetate 50.96 g (0.247 mol) of 2,4-di-t-butylphenol, 28.84 g (0.272 mol) of methyl thioglycolate, 14.83 g (0.494 mol) of paraformaldehyde and 3.41 g of dimethylamine (33 % in ethanol) are refluxed for 18 hours in 50 ml of DMF. The crude product (85.3 g) can, after working-up as described above, be further purified by flash chromatography. m.p. 55.0-55.5°C. Analysis for C 18 H 28 SO 3 : calc. C 66.63; H, 8.70; S 9.88 %; found C 66.65; H 8.79; S 9.88 %. Example 3: 3-(3'-t-Butvl-4'-hvdroxv-5-octvlthiomethvlphenvl)-4'-phenvlaminopropιonanilide (compound of the formula I in which R is CH 2 -S-n-octyl, R, is tert-butyl and R 4 is a group of the formula III where m = 2, R 3 = H and Y = phenyl) 20 g (50.7 mmol) of the compound from Example 1 , 9.34 g (50.7 mmol) of 4-aminodiphenyl- amine and 50 mg of phenothiazine are heated at 180°C for 2 hours. The brown, viscous crude product is purified by flash chromatography. IR (KBr): 3375 and 3300 (OH and NH), 1654 (amide I), 1508 (aromatic), 1515 (amide II). Analysis for C^H^N^S: calc. C 74.68; H 8.48; N 5.12; S 5.86 %; found C 74,74; H 8.67; N 4.96; S 5.65 %. Example 4: 3,5-Di-t-butyl-2-hydroxybenzylthio-4'-phenylaminoacetanilide (compound of the formula I in which R and R, are t-butyl and R 4 is a group of the formula II where A = S, E = direct bond, G = direct bond and Y = phenyl. 34.03 g (0.105 mol) of the compound from Example 2 and 19.34 g (0.105 mol) of 4-aminodiphenylamine are heated at 180°C for 8 hours. The brown, viscous crude product is purified by flash chromatography and recrystallization. Recrystallization from toluene/cyclohexane gives a crystalline product of m.p. 143.0-143.5°C Analysis for C 29 H 36 N 2 O 2 S: calc. C 73.07; H 7.61 ; N 5.88; S 6.73 %; found C 73 00; H 7.63; N 6.09; S 6.67 %. Example 5: 3-(3'-t-Butyl-4'-hydroxy-5'-octylsulfinylmethylphenyl)-4"-phenylamιno- propionanilide (compound from Example 3 where R = CH 2 -SO-n-octyl) 4.5 g (8.23 mmol) of the compound from Example 3 are refluxed for 48 hours with 6.51 g (86.4 mmol) of 30 % H 2 O 2 in 40 ml of acetone. The mixture is then diluted at 20-25 c C with 50 ml of hexane. Turbidity is removed by filtration. Evaporation of the filtrate gives 1.8 g of a pale brown crystalline product. Recrystallization from hexane/acetone at -20°C gives 3.15 g of a white powder of m.p. 114.5-116°C. IR (KBr): 3300 (OH, NH), 1655 (amide I), 1597 (aromatic), 1514 (amide II). MS: 562. Analysis for calc. C 72.56; H 8.24; N 4.98; S 5.70 %; found C 72.14; H 8.13; N 4.60; S 5,45 %. Example 6 3,5-Dι-t-butvl-2-hvdroxvbenzylsulfιnvl-4'-phenvlamιnoacetanιlιde (compound from Example 4 where A = SO) 17 64 g (37 mmol) of the compound from Example 4 and 33 56 g (296 mmol) of 30 % hydrogen peroxide are refluxed for 48 hours in 250 ml of methanol Work-up as in the above example and recrystallization from hexane/acetone give a yellowish powder of m p 134°C IR (KBr) 3300 (broad, NH, OH), 1652 (amide I), 1597 (aromatic), 1515 (amide II) MS 492 (calc for C 29 H 36 N 2 O 3 S calc C 70 70, H 7 37, N 5 69, S 6 51 %, found C 70 18, H 7.27, N 5 30 S 6 16 % Example 7 Methyl 3,5-dιmethyl-2-hydroxybenzylthιoacetate 1) (intermediate) Preparation analogous to Example 3 (using 3,5-dιmethylphenol instead of 3,5-dι-t- butylphenol) m p 47 0-47 5 β C Analysis for C 12 H 16 S0 3 calc C 59 98 H 6 71 , S 13 34 %, found C 59 96, H 6 73, S 13 01 % Example 8 3,5-Dιmethyl-2-hydroxybenzylthιo-4'-phenylamιnoacetanιlιde 2 Preparation analogous to Example 4 using the compound described in Example 7 m p 137 5-138°C (toluene) IR (KBr) 3335 (OH/NH) 1644 (amide I) 1593 (aromatic), 1514 (amide II) Analysis for C 23 H 24 N 2 O 2 S calc C 70 38 H 6 16, N 7 14, S 8 17 %, found C 69 90, H 6 27 N 7 07, S 8 18 % NH- Ph Example 9: 3,5-Dιmethyl-2-hydroxybenzylsulfinyl-4'-phenylamιnoacetaniiιde 3 Preparation analogously to Example 6 from the compound described in Example 8. m.p. 176.5-177.5°C (acetonitrile). IR (KBr): 3310 (OH/NH), 1653 (amide I), 1597 (aromatic), 1515 (amide II). Analysis for C 23 H 24 N 2 O 3 S: calc. C 67.62; H 5.92; N 6.86; S 7.85 %; found C 67.70; H 5.91 ; N 6.86; S 7.69 %. Example 10: Methyl 2-{3-t-butyl-4-hydroxy-5-([methoxycarbonylmethyl]thιomethyl)- benzylthio}acetate 4) (intermediate) Preparation from 274.6 g (2.587 mol) of methyl thioglycolate, 194.32 g (1.293 mol) of 2-t- butylphenol, 155.4 g (5.17 mol) of paraformaldehyde, 5.83 g of dimethylamine and 195 ml of DMF: the mixture of the above components is boiled for 3 hours under nitrogen in a flask fitted with mechanical stirrer and reflux condenser. The internal temperature is 110 C C. The crude product is taken up in ethyl acetate and washed with 100 ml of water Evaporation of the organic phase gives 476.7 g of a brown-red oil (95.3 %). 1 H NMR(CDCI 3 ) 7.15 and 6.95 (d, J = 2.5Hz), 3.86 and 3.72 (2s, Ar-S-CH 2 ), 3.75 and 3.70 (2s, MeO), 3 16 and 3 08 (2s, CO-CH 2 -S), 1.39 (t-butyl). Analysis for C 18 H 26 S 2 O 5 : calc. C 55.93, H 6 78, S 16 59 %; found C 55 95; H 6 99; S 16.69 % 10: R'=t-Bu, 12: R' = Me, Example 11 : 2-{3-t-Butvl-4-hvdroxv-5-f(2-oxo-2-(4-phenvlaminophenvl)ethvl)thιomethvN- benzylthio} (4-phenylaminophenyl)acetamide 5) Preparation analogously to Example 3 from the dimethyl ester from Example 10 and two equivalents of 4-aminodiphenylamine. M.p. 82-84°C. IR (KBr): 3375, 3323 (OH and NH); 1654 (amide I), 1597 (aromatic), 1515 (amide II). Analysis for C 40 H 42 N 4 O 3 S 2 : calc. C 69.54; H 6.13; N 8.11 ; S 9.28 %; found C 70.08; H 6.44; N 8.08; S 8.90 %. Example 12: Methyl 2-{3-methyl-4-hydroxy-5-([methoxycarbonylmethyl]thiomethyl)- benzylthio}acetate ) (intermediate) Preparation analogously to Example 10 using o-cresol. m.p. 63.0-64.5°C (toluene), IR (film). 1732 (C=O, ester). Analysis for C 15 H 20 S 2 O 5 : calc. C 52.31 ; H 5.85; S 18.62 %; found C 52.49; H 5.95; S 18.58 %. Example 13: 2-(3-methyl-4-hvdroxy-5-f (2-oxo-2-,4-phenvlamιnophenvl ,ethvl .thiomethvπ- benzylthιo}-N-(4-phenylamιnophenyl)acetamιde 5> Preparation analogously to Example 11 m.p 133.5-134 5°C (acetonitrile) IR (film) 3310 (NH, OH), 1654 (amide I), 1597 (aromatic), 1516 (amide II) Analysis for C 37 H 36 N 4 O 3 S 2 : calc. C 68 49, H 5 59, N 8.64, S 9.88 %, found C 68 43. H 5.64. N 8.64; S 9.79 % Examples 11 and 13 1 1 : R'=t-Bu,R=H 13: R'=Me, R=H Example 14: Methyl 3-(3'-t-butyl-4'-hydroxy-5'-(methoxycarbonylmethyl)thiomethylphenyl)- propionate 6 ' Preparation analogously to Example 1 ; viscous, colourless oil. IR (film): 1730 (C=O, ester). Analysis for C 17 H 26 O 5 S: calc. C 52.31 ; H 5.85; S 18.62 %; found C 52.49; H 5.95; S 18.58 %. Example 15: 3-{3-Methyl-4-hydroxy-5-[(2-oxo-2-(4-phenylaminophenyl)ethyl)thiomethyl]}-4- phenylaminopropionanilide 7 ' Preparation analogously to Example 11 ; m p. 168°C (toluene/acetone), IR (KBr): 3318 (OH), 1653 (amide I), 1597 (aromatic), 1515 (amide II). Analysis for C 40 H 42 N 4 O 3 S: calc. C 72.92; H 6.43; N 8.50 %; S 4.87 %; found. C 72.71 ; H 6.31 ; N 8.30 %; S 4.76 %. NH-Ph Example A1 Incorporation into a rubber substrate and oven ageing Crude rubber (polybutadiene) is mixed in a Brabender mixer with sulfur, ZnO, stearic acid, the vulcanization accelerator (Vulkacit ZDBC) and (I) the compounds from Example 5 and 6 or (it) the conventional stabilizer Vulcanox PAN The mixture is vulcanized, and samples of the vulcanizate are treated with acetone After drying, the residual nitrogen content is determined Values Nitrogen content (additive) Additive Before acetone After acetone treatment treatment in ppm in ppm in % of initial value Comp from Example 5 590 336 57 Comp from Example 6 680 492 72 Vulkanox PAN 879 9 1 The different initial nitrogen values result from the different nitrogen contents of the additives It is found that the novel compounds are leached out to the extent of less than 55 %, whereas the sample containing the conventional additive is leached out to the extent of more than 95 % Oven ageing After the samples have been oven aged at 100°C for 5 weeks, the samples stabilized in accordance with the invention still have rubber elasticity and flexibility, whereas a stabilizer- free sample is brittle like glass and the sample containing PAN is hard and agile Example A2: Incorporation into crude rubber Crude rubber (polybutadiene) is compounded in a tarn compounder (Brabender) for 15 minutes at 150°C und 40 rpm together with 1.5 % of the additives. The rubber, in the form of 1 mm test sheets, is then extracted with acetone. The nitrogen content is measured before and after extraction. Results: Additive Nitrogen content before extraction after extraction ppm in ppm in % of initial value Comp. from Example 5 830 443 53.4 Comp. from Example 6 920 583 63.4 Example A3: Action under processing conditions Crude rubber (polybutadiene) is compounded in a tarn compounder (Brabender) at 160°C and 60 φm together with 0.25 % of the additives until an increase in the torque/time diagram is clearly evident The time for a 1 Nm rise is defined as the induction time and is a measure of the effectiveness of the additives in delaying oxidative crosslinkmg of the rubber Results. Additive Induction time (min) Vulkanox 4020 NA 6.4 Comp. from Example 5 27.4 Example A4: Action under storage conditions In each case, 0.25 % of the additives are mixed into the crude rubber at 60°C on mixing rolls. 10-mm sheets are pressed out of the rubber and then aged at 80°C in a fan-assisted oven. A sample is taken once a week and the gel content (insoluble content in toluene at 20°C) is determined. An increasing gel content indicates oxidative crosslinking, i.e. the longer the time taken for the gel content to rise to values >1 %, the better the protective action of the additive Results Additive Time in weeks to a gel content of >1 % Control < 2 Comp from Example 5 > 11 Comp from Example 6 10 Example A5: Incorporation of the additives into carbon black-filled vulcanizates and effectiveness after extraction The following mixture constituents are mixed at 60°C in a Werner & Pfleiderer LH1 Banbury- type mixer Parts by weight Polybutadiene (Taktene 1220/Bayer) 40 0 Natural rubbers MR 5CV 60 0 Carbon black N 330 55 0 Aromatic oil (Ingralen 450/Fuchs) 6 0 Zinc oxide 5 0 Stearic acid 2 0 Antιlux 1 1 1 2 0 Vulkanox HS 1 5 The following vulcanization assistants and the additive to be tested are then admixed on the mixing rolls Struktol SU 109 (75 %)/sulfur preparation 2.67 Vulkazit MOZ 0.6 Additive 2 5 From the finished mixtures, sheets with a thickness of 2 mm are vulcanized in a hot press at 150°C for 20 minutes Extraction The vulcanized sheets are extracted with acetone for 48 hours at room temperature Determination of the nitrogen content The nitrogen content of the samples is determined by X-ray spectrometry before and after extraction, and the amounts originating from the additives to be tested are calculated by taking the difference between the respective values of the control (contains extractable and non-extractable nitrogen compounds from other formulation constituents, such as carbon black and accelerator) Ageing ISO S2 rods are stamped out of the extracted sheets, and the tensile strength and elongation at break are determined before and after ageing at 80°C. Results: 1 Additive coφoration/nonextractable additive amounts Additive Nitrogen content of the additive after extraction in % of the value before extraction Control none Vulkanox 4010 NA 0 Comp from Example 5 50 Comp from Example 9 45 Comp from Example 13 41 2 Effectiveness during oven ageing at 80°C after extraction Additive Br ;ιng strer lgth (MPa) Elongation at break (%) fresh after 2 weeks after 2 weeks Control 23 2 6 9 97 Vulkanox 4010 NA 23 9 7 9 1 12 Comp from Example 5 23 7 13 8 205 Comp from Example 9 25 0 14 1 205 Comp from Example 13 23 6 12 5 195

Claims: WHAT IS CLAIMED IS 1. A compound of the formula I (I) in which R is C,-C 18 alkyl, C 5 -C 8 cycloalkyI, C 7 -C 9 phenylalkyl, -CH 2 -A-R 2 or a group of the formula II, R, is C,-C 18 alkyl, C 5 -C 8 cycloalkyl, C 7 -C 9 phenylalkyl or a group of the formula (II), R 2 is C 4 -C, B alkyl, -(CH 2 ) m -COOR 5 or a group of the formula III, R 3 is hydrogen, C 5 -C B cycloalkyl or C,-C, 2 alkyl, R 4 is C^C^alkyl, C 5 -C 8 cycloalkyl, C 7 -C 9 phenylalkyl or a group of the formula II or IV, E is a direct bond, -CH 2 -, -CH 2 -O- or -CH 2 -NH-, Y is C^C^alkyl, cyclohexyl, phenyl or alpha- or beta-naphthyl, R 5 ιs C C^alkyl, and with the provisos that either at least one of the radicals R and R 4 conforms to a group of the formula II or R is CH 2 -A-R 2 and R 4 is a group of the formula IV. 2. A compound according to claim 1 , in which R is d-Cβalkyl, cyclohexyl, benzyl, -CH 2 -A-R 2 or a group of the formula II, Ri is Cι-C 8 alkyl, cyclohexyl, benzyl or a group of the formula II, R 4 is C C 12 alkyl, cyclohexyl, benzyl or a group of the formula II, R 2 is C 8 -C 12 alkyl or -(CH 2 ) m -COOR 5 , R 5 is C 8 -C 13 alkyl, and E is a direct bond or -CH 2 3. A compound according to claim 1 , in which R is C Calkyl, -CH -A-R 2 or a group of the formula II, R is Crdalkyl or a group of the formula II, R 4 is Cι-C 4 alkyl or a group of the formula II or IV, R 2 is C 8 -C 12 alkyl, R 3 is hydrogen, C C 8 alkyl or cyclohexyl, E is a direct bond, Y is phenyl or alpha- or beta-naphthyl 4 A compound according to cairn 1 , in which A is SO or a direct bond 5. A compound according to claim 1 , in which R is -CH 2 -A-R 2 , R* is C C 18 alkyl, C 5 -C 8 cycloalkyl or C 7 -C 9 phenylalkyl and R 4 is a group of the formula IV 6. A compound according to claim 1 , in which R is a group of the formula II, and R and R 4 , independently of one another, are d-C^alky!, C 5 -C 8 cycloalkyl or C 7 -C 9 phenylalkyl 7 A compound according to claim 1 , in which R 4 is a group of the formula II,, and R and R^ independently of one another, are C C 18 alkyl, C 5 -C 8 cycloalkyl or C 7 -C 9 phenylalkyl sind 8 A composition comprising an organic material which is sensitive to oxidative, thermal and/or photoinduced degradation and at least one compound of the formula I according to claim 1 9 A composition according to claim 8, in which the organic mateπal is an organic, preferably synthetic, polymer. 10 A composition according to claim 9, in which the organic material is an elastomer 11 A composition according to claim 9, in which the compound of the formula I is chemically linked to the elastomer 12. A process for stabilizing organic material which is sensitive to oxidative, thermal and/or photoinduced degradation, which comprises adding a compound of the formula I as described in claim 1 to this material 13 A process according to claim 12, where the organic mateπal is a polymer 14. A process according to claim 12, where the organic material is a synthetic or natural rubber vulcanizate 15 The use of a compound of formula I according to claim 1 as a stabilizer in an organic material which is sensitive to oxidative, thermal and/or photoinduced degradation 16 The use according to claim 15, in which the organic material is a polymer 17. The use of a compound according to claim 15, in which the organic material is an elastomer

Inventors: KNOBLOCH GERRIT, MEIER HANS RUDOLF, KNOBLOCH, GERRIT, MEIER, HANS, RUDOLF
Applicants: CIBA GEIGY, KNOBLOCH GERRIT, MEIER HANS RUDOLF, CIBA SPECIALTY CHEMICALS HOLDING INC., KNOBLOCH, GERRIT, MEIER, HANS, RUDOLF
Application year: 1996
Main classification: C07C323
IPC codes: C07C317, C07C323, C08K5, C09K15