METHOD OF FORMING DIAMOND-LIKE CARBON FILM (DLC), DLC FILM FORMED THEREBY, USE OF THE SAME, FIELD EMITTER ARRAY AND FIELD EMITTER CATHODES

Abstract: The present invention relates to a method for forming substantially hydrogen-free DLC layers, wherein DLC layer of thickness about 1 to 100 nanometers is deposited over a sample substrate or a field emitter array and subsequently exposed to etching plasma comprising fluorine gas, wherein during the latter step, hydrogen contained in the substrate is eliminated by chemical etching reaction with fluorine, wherein steps to form the hydrogen-free DLC layer can be repeated to obtain a predetermined thickness of a DLC film.

Description: METHOD OF FORMING DIAMOND LIKE CARBON FILM(DLC), DLC FILM FORMED THEREBY, USE OF THE SAME, FIELD EMITTER ARRAY AND FIELD EMITTER CATHODES TECHNICAL FIELD The present invention relates to a method of forming Diamond-Like Carbon("DLC") film, particularly substantially hydrogen free DLC film, using the Plasma Enhanced Chemical Vapor Deposition ("PECVD") method, and the DLC film formed thereby .The present invention also relates to use ofthe same as field emission cathodes of a field emission display as well as to a field emitter array coated with the DLC film and field emitter cathodes comprising the DLC film. BACKGROUND ART In general, DLC without incorporated hydrogen has considerable interest, due to its higher sp 3 fraction compared to its hydrogenated counterpart; see, for example, V S Veerasamy et al.,Solid-State Elec.37,319 (1994); D.R.Mckenzie et al.,Thin Solid Films 206, 198(199 l);and K.K.Chan et al, Thin Solid Films 212,232(1992). DLC film possessing negative electron affinity("NEA") characteristics, have great potential in their application as electron emitters in vacuum microelectronics and have, as such, attracted extensive studies; see, for example, M.W.Geis et.al, IEEE ED Lett. 12,456(1991); N.S.Xu et al., Electron. Lett., 29, 1596(1993). The interest for the DLC as an emission material results from its unique emission properties; low-field cold emission and emission stability. In addition, the excellent thermal conductivity of the DLC anticipates high maximum currents to be obtained from the DLC film coated emitters. As could be known from these references, DLC film is typically used as an field emitter material for a Field Emission Display("FED"). In general, FED comprises emission cathodes and a glass face plate coated with phosphors on transparent conducting oxide. In operation, the face plate is held at a high positive voltage. When a color element is addressed, electrons from a cold cathode array bombard the corresponding phosphor element to produce a bright light in the same manner as in a conventional television picture tube. At the present time, diamond, DLC and, crystalline Si, metals such as Mo are mostly adopted as materials for the FED tip. However, using of metals or Si as tip material has the problems such as low durability, high driving voltage due to high work function compared with DLC or diamond Further, dispersion of electron and particles causes difficulty in maintenance of high vacuum below IO "7 Torr, as well as oxidization of the tip The chemical inertness, the hardness, and especially the low work function ofthe DLC make it an excellent electron emitting material for the FED. Cold cathode electron emitters obtained by depositing diamond films on Si tips, Mo tips, or W tips are also widely discussed The field strength needed for electron emission has been reduced to less than 3 x 1 O^V/cm, which is substantially lower than the field strength required in the conventional metal tips Field Emission Array("FEA"), as > 1 X 10 6 V/cm Heretofore, the DLC film deposited by PECVD method has higher hydrogen content, typically higher than 20 at %, see, A Dekempeneer et al., Thin Solid Films 217,56(1992). The incorporated hydrogen reduces sp 3 fraction in the film, resulting in reduction of film hardness Hydrogen free DLC can be obtained by filtered vacuum arc deposition or by ion beam deposition, see for example, S.Aisenberg et al., Appl.Phys.42,2953(1971). Mckenzie et al., deposited hydrogen free DLC with more than 85% sp 3 fraction by a filtered vacuum arc deposition, see, Mckenzie et al.,Phys.Rev.Lett 67,773(1991). A typical filtered vacuum arc discharge method is characterized in depositing carbon ions formed by arc discharge by applying magnetic field and electric field to said carbon ions. However, it is not easy to get a uniform deposition in large area by this method. FIG. 1 shows a prior art process for DLC layer forming by using PECVD method. Deposition plasma comprising methane (other carbon hydrides gases can also be used), hydrogen and helium is used in this method. However, in this method, radicals containing hydrogen are formed in the course of decomposing the methane which is included in the deposition plasma, causing a subject sample to inevitably contain hydrogen DISCLOSURE OF INVENTION Therefore, it is an object of the present invention to provide a method to form uniform substantially hydrogen free DLC deposition on a large area In the present invention, the substantially hydrogen free DLC layer is formed by depositing a thin DLC layer and subsequently exposing its surface to etching plasma This will be referred to as layer-by-layer deposition method hereinafter According to the present invention, the DLC layer of thickness about 1 to 100 nanometers is first deposited over a sample substrate Then the surface of said DLC layer is exposed to etching plasma During the latter step, hydrogen contained in the substrate is eliminated by chemical annealing (or etching) This results in a substantially hydrogen free DLC layer The characteristics ofthe DLC layer can advantageously be changed by altering its exposure time to the etching plasma Any plasma with chemical etching reaction can be used as the etching plasma The etching plasma can preferably comprise fluorine, more preferably carbon fluorides According to another respect of the present invention, the DLC layer is formed over Metal tips BRIEF DESCRIPTION OF THE DRAWINGS The object and advantages of the present invention will be more clearly understood to those skilled in the art with reference to the accompanying drawings in which FIG 1A-1B show a prior art process for forming DLC layer using PECVD method, FIG 2A-2I show a process for forming DLC layer according to the present invention, FIG 3 shows a Fourier Transform-Infrared absoφtion (FR-IR) spectra for the deposited DLC films, FIG 4 shows the optical band gap ofthe DLC film obtained from the Tauc's plot, FIG 5 shows the temperature dependency of dark conductivity ofthe DLC film, FIG 6 shows the I-E (current-electric field) characteristics ofthe DLC film, FIG 7 shows changes in characteristics of the DLC films with varied exposure time, FIG 8 is a top view SEM picture of DLC layer coated Mo FEAs, FIG 9 is a cross-sectional SEM picture of the DLC layer coated Mo tip; FIG. 10 shows I-V characteristics of the DLC layer coated Mo tips and Mo tips FEA; FIG. 1 1 shows Fowler-Nordheim plots of the DLC layer coated Mo tips and Mo tips FEA, FIG. 12 shows emission current fluctuation of pure Mo FEAs and the DLC layer coated Mo FEAs. BEST MODE FOR CARRYING OUT THE INVENTION Fig. 2A shows a substrate exposed to deposition plasma to coat it with DLC layer. Fig. 2B shows a DLC layer(l 1) formed by said deposition. Fig. 2C shows exposing a DLC layer( l 1) to etching plasma comprising fluoride gas after the deposition of the DLC layer. The characteristics ofthe sample substrate can advantageously be changed by altering the exposure time to the etching plasma in this step. Fig. 2D shows a first layer( 12) of substantially hydrogen free DLC formed by said process. Subsequently, another layer of conventional DLC of thickness about 1 to 100 nanometers is grown(Fig. 2E and Fig 2F). The step of exposing the sample substrate under the etching plasma to obtain the second substantially hydrogen free DLC layer is shown in the Fig.2G. The second DLC layer is thus obtained (Fig. 2H). Fig.2I shows the tenth layer of DLC layer subject to the etching plasma. Steps are repeated to obtain a predetermined number of DLC layers, which in all form a DLC film. In an example where plasma comprising CF 4 is used as the etching plasma, the layer-by-layer deposition method according to the present invention was used to deposit substantially hydrogen free a-Si:H and microcrystalline Si films. In this case, deposition plasma comprising hydrogen was exposed on a thin a-Si:H layer for chemical annealing. Then, CF. plasma was exposed on a thin DLC layer to remove weak bonds, predominantly C-H-, bonds and graphite C-C bonds. Conventional PECVD method, in which rf power was applied to the substrate holder was used. CH 4 /H 2 /He and CF He were introduced for the deposition of DLC layer and the surface treatment, respectively. Table below depicts the layer-by-layer conditions for the example. Condition Deposition Plasma Etching RF power(W) 100 100 Pressure(mbar) 0.4 0.45 Flow rate(sccm) He 50 50 H 2 5 0 CH 4 1 0 v-.l 4 c Time(s) 100 0~200 The flow rates of He and CF 4 was fixed at 50 seem and 30 seem, respectively for the etching plasma treatment. The thickness of each layer of the DLC and the CF 4 plasma exposure time were the two most important parameters to obtain a good quality DLC layer. In the example, the thickness of each layer was fixed at 5 nm and the CF 4 plasma exposure time was varied from 0 to 200s. The measured self-bias voltage ofthe example was found to be -120 V at a fixed rf power of 100 W. The self-bias voltage depends strongly on the gas pressure and rf power. Fig. 3 shows the FT-IR transmittance spectra of the DLC films. The absorption peaks at 2870 cm "1 , 2925 cm "1 and 2960 cm "1 corresponding respectively to sp 3 CH 3 (symmetrical), sp 3 CH 2 (asymmetrical) and sp 3 CH 3 (asymmetrical) modes, appear in the FT-IR spectrum for the conventional DLC layer. C-H,, vibration intensity disappears completely when the CF 4 plasma exposure time is 200s. This confirms that, it is possible to deposit a substantially hydrogen free DLC layer by PECVD method using the layer-by- layer deposition method according to the present invention. Fig.4 shows the optical band gap (E g opI ) ofthe DLC film obtained from the Tauc's plot. The optical band gap increases from 1.2 eV to 1.4 eV with increasing CF 4 plasma exposure time. The increase in optical band gap appears to be caused by the preferential etching of graphite phase in the DLC layer by CF 4 plasma exposure. Note that the bond energy of C-C sp 3 bond(8.68 eV) is higher than that of C-C sp 2 (6.33 eV). Therefore, bonding and anti-bonding states of C-C sp 2 lie in the inner side of those of C-C sp 3 . The removal of the sp 2 bonds, therefore, results in widening of band gap of DLC. Fig 5 shows temperature dependence of dark conductivity for the DLC films The conductivity ofthe DLC film shows an activated form and the activation energy increases from 0 25 eV to 0 55 eV with increasing CF plasma exposure time up to 200s This means that the Fermi level moves toward the midgap after the CF 4 plasma exposure because optical band gap ofthe substantially hydrogen free DLC layer is 1 4 eV, which is higher than 2 times of conductivity activation energy The conventional DLC layer shows characteristics of a p-type behavior and activation energy of conductivity around 0 2 eV This DLC film according to the present invention indicates relative high value (0 55 eV) of activation energy Fig 6 shows the I-E characteristics ofthe DLC films The area and thickness of the DLC films were 0 9 cm 2 and 100 nm, respectively Conventional DLC film shows non- emission up to 22 V/μm However, layer-by-layer deposited DLC film shows an effective electron emission the onset field for emission was found to be 18 V/μm and the emission currents were described by the Fowler-Nordheιm(F-N) formula The barrier energy for electron emission for the substantially hydrogen-free DLC, calculated from the slope of F-N plot , is 0 06 eV This indicates that the DLC films has low barrier energy for electron emission Layer-by-layer deposition was carried out under different deposition and etching plasma exposure conditions The flow rates of CH 4 and H 2 were 6 seem and 3 seem, respectively for the DLC deposition and the CF 4 flow rate was fixed at 20 seem for etching plasma treatment. Fig 7 shows the I-E characteristics of the DLC films according to the present invention with various CF 4 plasma exposure time The area of the DLC films in the example was fixed at 0 3 cm 2 The emission current of the DLC film increases with the CF 4 plasma exposure time, together with decrease in emission threshold field The onset field could be decreased by further optimization of the growth of DLC by using the method according to the present invention In another example, Mo tips field emitter array (FEA) is DLC coated by the layer- by-layer method according to the present invention The Mo tips were deposited on silicon substrate using E-beam evaporator into 1.5μm diameter holes spaced on lOμm centers, which included sequential growing of SiO 2 , Mo, and Al layers The height ofthe tip relative to the gate is determined by the diameter ofthe hole and the thickness ofthe insulating layers. During deposition of the DLC layers, the substrate temperature was adjusted to room temperature under a pressure of 20 mTorr. A thin DLC layer of about 5 nm thickness was grown and then CF 4 plasma was exposed on the surface. The DLC deposition and CF 4 plasma exposure were repeated to obtain substantially hydrogen free DLC layer of 20 nm thickness. Especially, substantially hydrogen free DLC layer can be grown by layer-by-layer deposition method; i.e. deposition of 5 nm DLC layer and subsequent 200 seconds of CF 4 plasma exposure on each layer of 5 nm DLC layer. Electron emission characteristics ofthe tips were measured using triode geometry. An anode plate was placed at 1 mm above the gate and was biased at 300 V. The variation ofthe anode and the gate current with the gate-to-cathode bias was measured under 1 X 10 '8 Torr vacuum environment. The current -voltage and current fluctuation tests can be controlled by a computer. For all the tests, the device is configured in a common emitter configuration with the emitter grounded, the anode at a positive voltage and the gate driven positive to turn the device on. The morphologies of the substantially hydrogen free DLC coated Mo tips are shown in Fig. 8. The cross-sectional view ofthe substantially hydrogen free DLC coated Mo tips, shown in Fig. 9 reveals that the tips are typically 1.8μm high and the gate aperture is 1 5μm wide. The thermal SiO 2 dielectric layer is around 1.6μm in thickness and the thickness of the substantially hydrogen free DLC coated on the Mo tips is about 20 nm. Fig.10 shows the emission current voltage characteristics for the DLC coated Mo tips FEA of 900 tips and the Mo tips FEA. The turn-on voltage was measured 80 V for the Mo tips FEA and 65 V for the DLC coated Mo tips FEA. In addition to the decrease in the turn-on voltage, the maximum anode current available also increased from 140 A to 320μA. And an anode current of about 0. 1 μA per emitter is achieved at 87 V in the DLC coated Mo tips FEA, while the same current level is obtained at 107 V in the Mo tips FEA. This indicates that the operating voltage can be remarkably reduced just by adopting this fabrication process ofthe DLC coating on the Mo tips. By contrast, the gate current monotonously increased with the applied gate voltage and was not significantly altered because ofthe DLC coating. It should be noted that these Mo and the DLC coated Mo tips were grown on the same wafers under the same condition. The modification on the current-voltage property can, thus, be completely attributed to the enhancement on the electron emission behavior due to the substantially hydrogen free DLC coating Fig 1 1 shows the Fowler-Nordheim plots of the DLC coated Mo tips FEA and Mo tips FEA The electron emission characteristics of the tips were further evaluated using the Fowler-Nordheim Equation, that is, log(I/V 2 ) = log A - B x (1000/V), where I is the emission current, V is the gate to cathode voltage, log A is the intersection with vertical axis, and B the slope of the F-N plot which is proportional to φ 3 2 The effective work-function(φ), and turn-on voltage estimated from the slop ofthe F-N plots and the intercepts of this plot with the abscissa, respectively The field enhanced factor for these tips was first obtained by comparing φ value calculated from the slope of the F-N plots of the Mo tips with the work-function reported for Mo metal (4 5 eV) The effective φ value thus calculated for the DLC coated tips is 2 60 eV These observations illustrated the significant effect of the substantially hydrogen free DLC coating on lowering the work-function required for emitting the electrons The emission current fluctuations of Mo tips FEA and the substantially hydrogen free DLC coated Mo tips FEA with variable gate voltage are shown in Fig 12 A and Fig 12B, respectively It was confirmed that, in the measurement of midterm current fluctuation, the emission current ofthe substantially hydrogen free DLC coated Mo tips FEA is more stable than that ofthe conventional pure Mo tips FEA So the performance ofthe DLC coated Mo-tips FEA is better than that ofthe Mo tips FEA Electron emission characteristics ofthe Mo tips and the substantially hydrogen free DLC coated Mo tips FEA have been examined using triode geometry, DLC coatings are observed to have markedly enhance the emission of electrons The turn-on voltage is reduced from 80 to 65 V, while the maximum anode current increased from 140 to 320μA, due to DLC coating on Mo tips And the emission current for the substantially hydrogen free DLC coated Mo tips is more stable than that ofthe conventional pure Mo tips FEA Considering the above, the substantially hydrogen free DLC film formed by method according to the present invention provides a promising cathode material especially for FED, due to its characteristics of hardness, chemical inertness, the excellent thermal conductivity, large area capability, low-field cold emission and emission stability Obviously, numerous modifications and variations of the present invention are possible in light ofthe above teaching. It is therefore to be understood that the invention may be practiced otherwise than as specifically described herein.

Claims: WHAT IS CLAIMED IS: 1 A method of forming a DLC film on a substrate comprising steps of ( l)growιng a DLC layer having a predetermined thickness on the substrate, and (2)exposmg the surface ofthe DLC layer to a etching plasma after the growth of the DLC layer 2 The method according to claim 1, characteπzed in that the steps of growing and exposing are repeated in that order over the pre-formed DLC layer to obtain a predetermined thickness ofthe DLC film 3 The method according to claim 1, characterized in that the etching plasma comprises fluorine gas 4 The method according to claim 3, characterized in that the fluorine gas is carbon fluoride 5 The method according to claim 4, characterized in that the carbon fluoride is CF 4 6 The method according to claim 1, characterized in that the thickness ofthe DLC layer is 1 to 100 nanometers 7 The method according to claim 1, characterized in that the thickness ofthe DLC layer is 5 to 20 nanometers 8 The method according to claim 1, characterized in that the DLC layer is exposed to the etching plasma for 1 to 200 sec 9 The method according to claim 1, characterized in that the DLC layer is exposed to the etching plasma for 50 to 100 sec 10 The method according to claim 1, characterized in that the DLC layer is grown by PECVD method using deposition plasma 1 1 The method according to claim 10, characterized in that the deposition plasma for the growing ofthe DLC layer comprises CH 4 , H, and He 12 The method according to claim 10, characterized in that the etching plasma comprises CF 4 and He 13 A DLC film formed by the method of claim 1 14 A DLC film according to claim 13, comprising one or more DLC layers formed on the surface of the pre-formed DLC layer 15 A use ofthe DLC film according to claim 13 as field emission cathodes of field emission display 16 A field emitter array comprising a DLC film formed on the suiface ofthe array by the method of claim 1 17 The field emitter array according to claim 16, characterized in that one or more DLC layers are formed on the surface of the pre-formed DLC layer to obtain a predetermined thickness ofthe DLC film 18 The field emitter array according to claim 16, characterized in that the field emitter array is a Mo tips field emitter array for a field emission display 19 Field emission cathodes of a field emission display comprising a DLC film formed by the method of claim 1 20 The field emission cathodes according to claim 19, characterized in that one or more DLC layers are formed on the surface ofthe pre-formed DLC layer to obtain a predetermined thickness ofthe DLC film.

Inventors: JANG JIN, PARK KYU CHANG, JANG, JIN, PARK, KYU, CHANG
Applicants: JANG JIN, ORION ELECTRIC CO LTD, PARK KYU CHANG, JANG, JIN, ORION ELECTRIC CO., LTD., PARK, KYU, CHANG
Application year: 1996
Main classification: C23C16
IPC codes: C01B31, C23C14, C23C16, C23F4, C30B25, C30B29, H01J9, H01L21