A novel ceramic substrate for bi-cuprate superconductors and a process for preparing the same

Abstract: A novel ceramic substrate useful for the preparation of superconductors, said substrate having the formula Ba 2 DyMO 5.5 where M represents at least one of the metals Zr, Sn and Hf and a process for the preparation of said ceramic substrate, which comprises (i)Reacting salts of dysprosium, barium and Zr, Sn or Hf in an organic medium, (ii) Pressing the resultant mixture in the form of pellets, (iii)Calcining the pellets by heating at a temperature in the range of 1000 to 1200°C, (iv)Repeating the calcination process for 30-45 h at temperature in the range of 1000- 1200°C until a highly homogenous mixture is formed, (v)Grinding the calcined material and pelletising at a pressure in the range of 3 to 4 tons/cm 2 , (vi) Sintering the resultant product at a temperature in the range of 1200 to 1600°C for a period of 10 to 30 h , and then furnace cooled to room temperature .

Description: Field of the Invention The invention relates to a novel ceramic substrate of formula Ba 2 DyMO 5.5 wherein M represents at least one of the metals Zr and Hf, a process for the preparation of said ceramic substrates for Bi-cuparate superconductors, Bi-cuparate superconductors and a process for the preparation of phase pure superconducting Bi(2223) and Bi(2223)-Ag thick films on these newly developed substrates. Prior art of the invention The immediate application of high T c superconductors is likely to be in the form of thick and thin films in electronic devices [Alford N. McN et al., Supercond. Sci. Technol. 4 (1991) 433; Pinto, R. et al., Applied Superconductivity 1 (1993) 1]. In the preparation of superconducting films, substrates play a vital role and the high chemical reactivity of Bi-cuprate superconductors imposes severe restrictions on the materials available for their use as substrates for Bi-cuprate superconductors [McGinnis, W.C. et al. J. Mater. Res. 7 (1992) 585]. Besides for microwave applications, the substrate should have a low dielectric constant and loss factor at Gh z frequencies [Preng, L.H. et al., Supercond. Sci. Technol. 3 (1990) 233]. To the best of our knowledge, MgO is the only substrate suitable for Bi-cuparate films for microwave applications. However, the Bi(Pb)SrCaCuO [BiSCCO] films developed on MgO contained mixed phases of both low T c , Bi(2212) ]T c(o) =80 K] and high Tc, Bi(2223) [T c(o) =110K] (McGinnis, W.C. et al., j. Mater. Res. 7 (1992) 585; Agarwal, A. et al., Supercond. Sci. Technol. 6 (1993) 670]. Other commercially available substrates such as Si, SiO 2 , Al 2 O 3 and SrTiO 3 etc. are either chemically reactive with BiSCCO superconductor or have high dielectric constant and loss factor which makes superconductor or have high dielectric constant and loss factor which makes them unsuitable or less attractive for microwave applications. PHYSICA C, 15 DEC. 1994, NETHERLANDS, vol. 234, no. 3-4, ISSN 0921-4534, pages 211-218, XP002029563 KOSHY J et al discloses that a new perovskite ceramic material, DyBa 2 SnO 5.5 , has been synthesised and sintered as single-phase material for its use as a substrate for both YBCO and BiSCCO superconductors. PHYSICA C, 10 JAN. 1996, ELSEVIER, NETHERLANDS, vol. 256, no. 3-4, ISSN 0921-4534, pages 312-318, XP002029562 KUMAR K S et al describes superconducting YBCO-Ag and Bi(2223)-Ag composite thick films fabricated on polycrystalline DyBa 2 SnO 5.5 by dip coating. We have now developed new substrate materials, Ba 2 DyMO 5.5 (M = Zr and Hf) which are found to be non-reacting with BiSCCO superconductor even at extreme processing conditions and have low dielectric constant and loss factors. We have produced phase pure Bi(2223) and Bi(2223) - Ag thick films with Tc (o) =110K and high critical current density (-10 4 A/cm 2 ) on these substrates. Objects of the invention Thus, the main objective of the present invention is to provide ceramic substrates of Ba 2 DyMO 5.5 (M=Zr, and Hf), a process for the preparation of said ceramic substrates, Bi-cuparate superconductors and a process for the preparation of single phase Bi(2223) and Bi(2223)-Ag thick films of Tc (O) =110K and high critical current density on these substrates. To meet these objectives, the present invention provides a novel ceramic substrate of formula Ba 2 DyMO 5.5 , a process for the preparation of superconducting Bi(2223) and Bi(2223)-Ag thick films on the new substrate and the superconductor produced by the process. Accordingly, one embodiment of the present invention relates to a process for producing new ceramic substrates of the formula Ba 2 DyMO 5.5 where M represents metals Zr and Hf, useful for the preparation of superconducting films thereon, which comprises : (i) mixing salts of dysprosium, barium and Zr and Hf in an organic medium, (ii) pressing the resultant mixture in the form of pellets, (iii) calcining the pellets by heating at a temperature in the range of 1000 to 1200°C, (iv) repeating the calcination process altogether not exceeding for 30 to 45 h, preferably 12 h for each calcination, at temperature in the range of 1000 to 1200°C till a highly homogeneous mixture is formed, (v) grinding the calcined material and pelletising at a pressure in the range of 3 to 4 tonns/cm 2 , and (vi) sintering the resultant product at a temperature in the range of 1200 to 1600°C for a period of 10 to 30 h preferably 20 h and then furnace cooled to room temperature. The salts of dysprosium, barium and other metals used may be selected from oxides, carbonates or nitrates. The purity of the salts may be of 99.9%. The organic medium used may be selected from organic solvents such as acetone, ethyl alcohol, isopropyl alcohol. Multiple calcinations (preferably three times) of the pellets may be conducted at temperature 1000 to 1200°C for a period ranging from 10 to 15 h preferably 12 h for each calcination. The sintering of the final product may be effected for a period of 10 to 30 h preferably for 20 h. In view of the suitability of Ba 2 DyMO 5.5 substrates, we have successfully screen-printed/dip-coated thick films of Bi(2223) and Bi(2223)-Ag with a zero resistivity superconducting transition at 110 K on these substrates. Thus, yet another aspect of the present invention relates to a process for the preparation of superconducting Bi(2223) and Bi(2223)-Ag thick films on new ceramic substrates of the formula Ba 2 DyMO 5.5 where M represents metals namely Zr and Hf, useful for the preparation of superconducting films, which comprises: (i) Mechanically polishing the ceramic substrate of the above said formula to get highly smooth and shining surfaces, (ii) Preparing thick films of Bi(2223) and Bi(2223)-Ag composites with 5-10 Vol% of Ag by known methods, (iii) (a) Screen printing Bi(2223) and Bi(2223)-Ag on said polished Ba 2 DyMO 5.5 substrates using a mesh size in the range of 325, or (b) Dip-coating Bi(2223) and Bi(2223)-Ag on said polished Ba 2 DyMO 5.5 using a suspension of the respective powder with an organic solvent, (iv) Drying the resultant films at a temperature in the range of 100 to 150°C, (v) Heating the dried films at a rate of 200 to 300°C/h upto 860-880°C and soaking at this temperature for 1 to 5 minutes, (vi) Cooling the film at a rate of 10°C/h to bring down the temperature to 845°C and keeping the films at this temperature for a period of 2-4 h, and (vii) Cooling the film at a rate of 200°C/h upto room temperature. All the above steps are being carried out in the presence of air or oxygen. The details of the invention are described in Example 1 given below and which is provided by way of illustration only and should not be constructed to limit the scope of the invention. Examples 2, 3, 4 and 5 provide technological background. Example 1 Preparation of ceramic substrates of the formula Ba 2 DyZrO 5.5 Ba 2 DyZrO 5.5 was prepared by solid state reaction method . Dy 2 O 3 , BaCO 3 and ZrO 2 (purity 99.9%) were taken in stoichiometric ratio, mixed thoroughly in acetone medium and calcined in air at 1150°C for 45 h with two intermediate grindings. The resultant mixture was powdered and pressed at a pressure of 5 tons/cm 2 , in the form of circular pellets and sintered in air at 1450° C for 20 h. Example 2 Preparation of ceramic substrate of the formula Ba 2 DySnO 5.5 Ba 2 DySnO 5.5 was prepared by solid state reaction method . Dy 2 O 3 , BaCO 3 and SnO 2 (purity 99.9%) were taken in stoichiometric ratio, mixed thoroughly in acetone and calcined in air at 1100°C h with two intermediate grindings. The resultant mixture was powdered and pressed at a pressure of 4 tons/cm 2 in the form of circular pellets and sintered in air at 1360°C for 20 h. Structural determination The structure of the sintered material was examined by X-ray diffraction (XRD) method and it is found that all these materials are isostructural having a cubic perovskite structure as shown in the XRD patterns in fig 1(sheet No.1) of the drawings accompanying this specification for two typical samples Ba 2 DyZrO 5.5 (Example 1) and Ba 2 DySnO 5.5 (Example 2) . In table la and b, we have given the computerised XRD data for these materials . Dielectric properties The dielectric properties of the substrate materials were measured in the range 30 Hz to 13MHz frequencies and values of the dielectric constant (ε') and loss factor (tan δ) at 13 MHz, frequency are 12 and 10- 3 respectively at room temperature. At GHz frequencies the values of ε' and tan δ are found to be 10 and 10- 5 respectively, which are ideally suitable for microwave applications. Chemical compatibility of Ba 2 DyMO 5.5 with Bi(2223) superconductor The most important characteristics of a material to be used as a substrate for superconductors is its chemical non-reactivity with the superconductor at the processing temperature. The chemical reactivity between Ba2DyMO 5.5 and Bi(2223) was studied by mixing 1:1 vol% of Ba 2 DyMO 5.5 and Bi(2223 ) and annealing the present pellet at 850°C for 20 h . The XRD pattern of the annealed 1:1 vol% mixture of Ba 2 DySnO 5.5 and Bi(2223) is shown in fig.2 (sheet No.2) . The XRD pattern in the two phases in fig.2c is compared with those of pure Bi(2223) (fig.2a) and pure Ba 2 DySnO 5.5 (fig. 2b). fig.2 shows that there is no additional phase formed, not even Bi(2212) in the annealed composite sample other than those of Bi(2223) and Ba 2 DySnO 5.5 . This clearly indicates that there is no chemical reaction between Ba 2 DySnO 5.5 and Bi(2223), even at the extreme processing conditions. Detailed percolation studies carried on Ba 2 DySnO5 Bi(2223) composites confirmed that the Bi(2223) and Ba 2 DySnO 5.5 are found to remain as separated phases with their own charateristic even under severe heat treatment suggesting that Ba 2 DySnO 5.5 can be ideal substrate material for Bi(2223). Ba 2 DySnO 5.5 are insulating peovskite oxides with resistivity of the order of 10 ohm.cm . In view of the suitability of Ba 2 DySnO 5.5 substrates, we have successfully screen-printed/dip-coated thick films of Bi(2223) and Bi(2223)-Ag with Tc (o) =110 K on these substrates. The present process for fabrication of Bi(2223) and Bi(2223)-Ag by screen printing/dip coating thick films on Ba 2 DySnO 5.5 substrates is given below : Before screen-printing/dip-coating Bi(2223) and Bi(2223)-Ag, Ba 2 DySnO 5.5 substrates were mechanically polished to get highly smooth and shining surfaces. For screen printing thick film paste of Bi(2223) and Bi(2223)-Ag were made by mixing respective powder with an organic vehicle. Film thickness was controlled via viscosity control of the thick film paste. This thick film paste was then screenprinted on Ba 2 DySnO 5.5 substrates using a mesh size of 325. In the case of dip-coating the suspension of Bi(2223) and Bi(223)-Ag were prepared by mixing their respective fine powders separately in an organic medium and the viscosities were controlled by the addition of commercially available fish oil. Thick films of Bi(2223) and Bi(2223)-Ag were prepared by dipping polished Ba 2 DySnO 5.5 substrates into respective suspension. screen printed/dip-coated films were dried at 100 ° to 150 °C for 2 to 3 h. Dried films were heated in a programmable furnace at a rate of 200° to 300°C h upto 860-880°C and soaked at this temperature for 11-5 min. The films were cooled down at a rate of 10°C/h and brought down to 845°c and kept at this temperature for 2-4 h and films were then cooled down to room temperature at a rate of 200°C . All the above processes were done in air. The structure of the films were examined by X-ray diffraction method and XRD patterns of these typical thick films of Bi(2223) on Ba 2 DySnO 5.5 are shown in Fig.3 (given on sheet Nos. 3,4&5). The XRD patterns of these(2223) thick films showed that except for the characteristic peaks of Ba 2 DySnO 5.5 substrates, all other peaks could be assigned to a phase pure Bi(2223) superconductor . The following examples illustrate the preparation of superconducting film employing the substrates. Example 3 Preparation of superconducting Bi(2223) thick film on ceramic substrate of formula Ba 2 DySnO 5.5 Highly polished polycrystalline Ba 2 DySnO 5.5 substrate was used for the fabrication of Bi(2223) thick films. Thick films paste of Bi(2223) was prepared by mixing Bi(2223) with n-butanol. The viscosity of the paste was controlled by the addition of commercially available fish oil. This paste was then screen printed on Ba 2 DySnO 5.5 substrate using a screen of 325 mesh size. The printed film was then dried in an oven at 200°C for 3 h. The film was then heated in a programmable furnace in air at a rate of 200°C/h upto 880°C and was kept at this temperature for two minutes . It was then cooled at a rate of 10°C/h upto 845°C and kept at this temperature for 3 h and finally furnace cooled to room temperature. Example 4 Preparation of superconducting Bi(2223) thick film on ceramic substrate of formula Ba 2 DySnO 5.5 The thick film suspension of Bi(2223) for dip-coating was prepared by mixing fine powder of Bi(2223) with n-butanol and the viscosity was controlled by the addition of fish oil. The thick film of Bi(2223) was prepared by dipping highly polished Ba 2 DySnO 5.5 substrate in the Bi(2223) suspension . The film is then dried in an electric oven at 150°C for 3 h. The dried film was then heated in a programmable furnace at a rate of 200°C/h upto 880°C and kept at this temperature for 3 min. The film was then cooled down upto 845°C at a rate of 10°C/h and kept at this temperature for 3 h. It was then cooled at a rate of 200°C /h to room temperature. The entire process was carried out in air. Example 5 Preparation of superconducting Bi(2223)-Ag thick film on ceramic substrate of formula Ba 2 DySnO 5.5 Thick film suspension of Bi(2223)-Ag for dip-coating was made by mixing superconducting Bi(2223)-Ag composite powder with n-butanol . Thick film of Bi(2223) -Ag composite having 7 vol% of Ag was fabricated by dipping highly polished Ba 2 DySnO 5.5 substrate in this suspension . The coated film was kept in an electric oven at 200°C for 3 h, to remove the organic solvent present in the film. The film was then heated in a programmable furnace in air at a rate of 300°C/h upto 870°C and kept at this temperature for 2 min and cooled at a rate of 10°C/h upto 845°C and kept at this temperature for 3 h. The film was then cooled at room temperature. The structure of the film was examined by X-ray diffraction technique. The XRD patterns of three typical thick films on Ba 2 DySnO 5.5 (example 3). Ba 2 DySnO 5.5 (example 4) and Ba 2 DySnO 5.5 (example 5) substrates are shown in Fig.3(a), (b) & (c) of the drawings (sheet Nos. 3,4 & 5) accompanying this specification. The XRD pattern of these Bi(2223) thick films showed that except for the characteristic peaks of Ba 2 DySnO 5.5 substrates, all other peaks could be assigned to a phase pure Bi (2223) superconductor. Superconductor in these Bi(2223) thick films on Ba 2 DySnO 5.5 substrates were studied by temperature-resistance measurements shown in Fig.4 (sheet No.6,7 & 8). The films show a metallic behavior in the normal state and give zero resistivity superconducting transition at 110 k. X-ray diffraction data of Ba 2 DyZrO 5.5 No. 2 d l/l o hkl 1 29.830 2.993 100 220 2 35.360 2.545 10 311 3 42.920 2.105 53 400 4 48.380 1.880 15 420 5 53.140 1.722 51 422 6 62.170 1.492 22 440 7 70.460 1.335 23 620 8 78.680 1.215 15 444 9 85.720 1.132 20 642 X-ray diffraction data of Ba 2 DySnO 5.5 No. 2  d l/l o hkl 1 17.480 5.069 9 111 2 29.720 3.004 100 220 3 34.900 2.569 7 311 4 36.560 2.456 7 222 5 42.530 2.124 25 400 6 52.690 1.736 32 422 7 61.660 1.503 15 440 8 69.930 1.344 13 620 9 77.650 1.229 9 444 10 85.470 1.135 12 642

Claims: A ceramic substrate useful for the preparation of superconductors, said substrate having the formula Ba 2 DyMO 5.5 where M represents at least one of the metals Zr and Hf. A process for the preparation of ceramic substrates useful for the preparation of superconducting Bi-cuprate films, said substrate having the formula Ba 2 DyMO 5.5 where M represents at least one of the metals Zr and Hf, which comprises: (i) Reacting salts of dysprosium, barium and Zr or Hf in an organic medium, (ii) Pressing the resultant mixture in the form of pellets, (iii) Calcining the pellets by heating at a temperature in the range of 1000 to 1200 °C, (iv) Repeating the calcination process for 30-45 h, preferably 12 h for each calcination, at temperature in the range of 1000- 1200°C until a highly homogenous mixture is formed, (v) Grinding the calcined material and pelletising at a pressure in the range of 3 to 4 tons/cm 2 , and (vi) Sintering the resultant product at a temperature in the range of 1200 to 1600°C for a period of 10 to 30 h, and then furnace cooled to room temperature. A process as claimed in claim 2 wherein the salts of dysprosium, barium and other metals used are selected from oxides, carbonates or nitrates and the like. A process as claimed in claim 2 wherein the purity of the salts is about 99.9%. A process as claimed in claim 2 wherein the organic medium used is an organic solvent such as acetone, alcohol or the like. A process as claimed in claim 2 wherein the multiple calcination of the pellets is effected for a period ranging from 30 to 45 h, preferably 12 h, for each calcination. A process as claimed in claim 2 where in the sintering of the final product is effected for a period of 10 to 30 h, preferably for 20 h. Bi-cuprate superconductor comprising a ceramic substrate having the formula Ba 2 DyMO 5.5 where M represents at least one of the metals Zr and Hf, which is coated with at least one layer of superconducting Bi(2223) and Bi(2223)-Ag thick film. A process for the preparation of superconducting Bi(2223) and Bi(2223)-Ag thick films on a ceramic substrate as defined in claim 1, said process comprising: (i) Mechanically polishing the ceramic substrate to give a highly smooth and shining surface, (ii) Preparing a thick film of Bi(2223) and Bi(2223)-Ag composites having Ag 5 vol% by known methods, (iii)(a) screen-printing Bi (2223) and Bi (2223)-Ag on the substrate using a mesh size in the range of 325, or (iii)(b)Dip-coating Bi(2223) and Bi(2223)-Ag on the substrate using suspensions of respective powders with organic solvents, (iv) Drying the resulting film at a temperature in the range of 100 to 150°C, (v) Heating the dried film at a rate of 200 to 300°C/h upto 860-880°C and soaking at this temperature for 1 to 5 minutes, (vi) Cooling the film at a rate 10°C/h to bring down the temperature to 845°C and keeping the film at this temperature for a period of between 2 and 4 h, and (vii) Cooling the film at a rate of 200°C/h to room temperature, all of the above steps being carried out in the presence of air or oxygen.

Inventors: DAMODARAN ALATHUR DAMODARAN, JOHN MARY ASHA, JOSE RAJAN, KOSHY JACOB, KUMAR KRISHNAN SUDERSAN, KURIAN JOSE, SAJITH POO KODAN, DAMODARAN, ALATHUR DAMODARAN, JOHN, MARY ASHA, JOSE, RAJAN, KOSHY, JACOB, KUMAR, KRISHNAN SUDERSAN, KURIAN, JOSE, SAJITH, POO KODAN
Applicants: COUNCIL SCIENT IND RES, COUNCIL OF SCIENTIFIC AND INDUSTRIAL RESEARCH
Application year: 1996
Main classification: H01L39
IPC codes: H01L39