Patterned heat welding rod for seaming resilient flooring

Abstract: The welding rod (13) is a laminate structure in which a print layer (10) is disposed between a first thermoplastic layer (12) and a second transparent thermoplastic layer (11). Preferably the welding rod (13) is in the form of an elongated element having a half-round cross-sectional shape. The welding rod is used to join two pieces of thermoplastic sheeting, particularly flooring, together. If the welding rod has a pattern similar to the printed pattern of the sheeting the resulting surface covering looks seamless.

Description: The invention relates to a rod made of thermoplastic material for joining two pieces of thermoplastic surface covering sheetings together to create a seam for the surface covering with the same unique visual. It has been very desirable to achieve new and unique visuals in floor covering products, and many end-users find it desirable to heat weld flooring seams in an effort to prevent dirt and bacteria from entering the seams. One such method has been to heat weld seams with a solid-colored welding rod. This has become a popular practice in the healthcare industry where sanitation requirements are extremely important. Not only have flooring manufacturers provided welding rods for seam sealing, but many wall systems are also being marketed with seam welding or seam sealing materials. The end users and job specifiers also often employ seam welding rods as an option to offer a decorative styling element to the specified job. They can add a solid colored welding rod that compliments the color of the patterned floor, or they can use an "accent" color that contrasts sharply with the floor to create a bold new look. GB 2 283 937 A discloses a through-colored, patterned welding rod of the generic kind which matches the color and design of the floor covering pattern. This heat welding rod uses methods which create a through-color visual which extends all the way from the surface down through the entire depth of the composition in an uninterrupted fashion. The pattern is limited to a multi-colored, chip- or granule-image. It is the object of the invention to provide a rod of the generic kind that could be readily matched to any pattern and/or design with relative ease. This objcet is achieved in that the rod of the generic kind comprises a laminate consisting of a first thermoplastic layer, at least one second transparent thermoplastic layer and a print layer disposed between the first layer and the second layer and having a print corresponding to the image of the surface covering. Further embodiments of the rod according to the invention are subjects of the subclaims 2 to 5. The welding rod of the present invention having a distinct, repeatable pattern can be produced by laminating a 0.15 cm printed, calendered PVC film to several overlying layers of 0.51 cm clear calendered films. The print image which matches the floor covering design is printed by any conventional means and could be done in a way that would create a realistic image. Lithographic printing and rotogravure printing techniques were found to be satisfactory. In fact, some printed film from a vendor was purchased for use in a flooring structure, and then, the same film was used to make a welding rod to match the flooring structure. The welding rod thickness is preferably 2.0 to 2.3 cm. The final structure was a sandwich-type structure. The bottom layer was a 0.15 cm printed film. To this print image layer, four successive layers of 0.51 cm clear calendered PVC films were laminated. The lamination could be done in either a hot/cold press type of operation or one could employ other methods. Multiple film laminations were produced simultaneously on an Auma machine. Also, two films were laminated using a regular calender/laminator on a roll press consolidation line. In any case, once the films have been laminated, they are die-cut into pieces/sheets that could be placed into a hot/cold press and molded into the half-round configuration of the final product welding rod. Subsequent testing revealed that the product had adequate bond strength. Naturally, the conditions and test results would vary if one opted to use different chemical compositions for the product/process structure. The invention is made by printing a desired image on one layer of film and laminating successive layers of clear films to create the same unique visual as the surface covering. Gauge variation can be minimized by using calendered films. The calendered films are then preferably molded into half-round cross-sectional welding rods. In the preferred embodiment, the printed image is protected by at least 0.76 cm of clear film, i.e., PVC or otherwise. Thus, as the product surface wears away, the underlying print does not change. In an effort to create a new flooring structure via a lamination process, heat welding rods were produced having a appearance similar to the flooring sheets. Different sandwich type structures were laminated using printed and clear PVC films. Such welding rods are more cost effective and would speed up introduction of surface covering patterns for commercial introduction, because the process merely relies on photographing the image of the surface covering structure to reproduce the visual for the welding rod. The printed film used to create the new laminated flooring structure were used to produce the patterned weld rod in a separate process. The composition of the laminates are well known in the art. This new process offers a visual that could be readily matched to any pattern and/or design with relative ease. By merely photographing and printing the design, one could laminate the printed film and create a patterned welding rod. The patterned welding rod, when welded between two pieces of similarly patterned polyvinyl chloride (PVC) resilient sheet flooring, disguises the joined area and forms a water-tight, sealed assembly. The pattern may be any multicolored design or image, including wood grain, marble or fanciful. The welding rod is preferably directed to use with resilient floor covering sheets which have a transparent wear layer of significant thickness, and more particularly to laminated floor covering sheets. Figure 1 is a schematic representation of a method to form the welding rod of the present invention. Figure 2 is a schematic representation of the present welding rod after being molded and prior to being separated into individual welding rods. Referring to Figure 1, the preferred method is to laminate several layers of clear film 1 on top of a 0.15 cm printed film 2 and then pressing them into a molded 1/2-round weld rod shape configuration. Alternatively, the lamination was done on a flat-bed press. All of the films were "pinned" (or perforated) to allow entrapped air to be released. A 0.15 cm printed polyvinyl chloride (PVC) base film was placed on the bottom press platen with the printed surface up and with a cork pad and three pieces of duct cloth disposed between the platen and the base film. Four 0.51 cm clear films were placed over the printed base film, followed by a top release paper or felt. The layers were pressed for one-half minute at 0.56 kg/cm 2 and then for one half minute at 5.6 kg/cm 2 . The temperature of the top and bottom platens was 148.9°C (300°F). The laminate was then cooled for 3 minutes under the 5.6 kg/cm 2 pressure. The laminated sheet was pressed into welding rods by placing a half-round embossing mold 3 on the bottom press platen 4, stripping the release paper/felt from the laminate and placing it onto the mold. The bottom platen was then pre-heated for 2 minutes to 162.8°C (325°F). The top press platen 5 was then lowered onto the laminate with a top release paper, release felt or ferro-chrome plate 6 disposed between the top platen and the laminate. The laminate was pressed for one and a half minutes at 0.28 kg/cm 2 and cooled for 3 minutes under the 0.28 kg/cm 2 pressure. The laminates were placed onto the mold with the backside of the printed film against the cutting edges of the mold. Thus, after pressing, the print image was facing upward as shown in Figure 2. The print layer 10 is disposed between the film 11 on which the print layer is adhered and the calendered clear film 12. The individual welding rods 13 are then separated. The structure of the welding rods 13 do not resemble the homogeneous, round weld rods or the uniformly distributed chip, half-round weld rods of the prior art. The product could also be made by multiple film laminations, using a continuous process to laminate the various layers. As such, either the films could be pre-heated and laminated to a heated/warm substrate, or one could pre-heat a substrate and then wrap the films around a cold laminator roll to consolidate the two layers. The technique depends on the thickness of the films being used, as well as their chemical composition. To minimize plasticizer migration, the welding rod formulation, especially the plasticizer system, must be balanced with the surface covering formulation. The plasticizer content and type should be similar between the welding rod and surface covering. Flooring is typically installed at temperatures between 12.8°C (55°F) to 29.4°C (85°F). Therefore, flexibility and ease of cutting must be maintained even near the lower end of the range. This is done by the addition of a low temperature plasticizer such as dioctyl adipate. Preferably the glass transition temperature, T g , of the plasticized chips is no greater than -1.1°C (30°F), more preferably no greater than -3.9°C (25°F), and most preferably no greater than -5.6°C (22°F). Thermoplastic materials which can be used to make the thermoplastic welding rods include polyvinyl chloride, acrylonitrile/butadiene/styrene, polypropylene, polyethylene, and thermoplastic polyurethane. Other thermoplastic resins that can be plasticized and used include polyvinyl acetate, cellulose acetate, polystyrene, ethyl cellulose, polyvinylidene chloride, polyurethane, nylon, acrylic, and polyphenylene oxide. The following thermoplastic resins have been used to make welding rods of the present invention: polyvinyl chloride homopolymers and copolymers with acetate functionality, and mixtures thereof. Polyvinyl chloride homopolymers are preferred. Plasticizers which can be used include butyl cyclohexyl phthalate, tri(butoxyethyl) phosphate, trioctyl phosphate, 2-ethylhexyl diphenyl phosphate, dibutyl phthalate, diisobutyl adipate, epoxidized di(2-ethylhexyl) tetrahydrophthalate, di(2-ethylhexyl) phthalate, diisooctyl phthalate, dioctyl adipate, diisononyl phthalate, di(2-ethylhexyl) hexahydrophthalate, n-octyl,n-decyl phthalate, tricresyl phosphate, butyl benzyl phthalate, dicapryl phthalate, di(3,5,5-trimethylhexyl) phthalate, diisodecyl phthalate, di(2-ethylhexyl) adipate, butyl epoxy stearate, epoxidized soya oil, epoxidized octyl tallate, dimethyl phthalate, hexyl epoxy stearate, cresyl diphenyl phosphate, di(2-ethylhexyl) isophthalate, n-octyl,n-decyl adipate, di(2-ethylhexyl) azelate, epoxidized octyl oleate, di(2-ethylhexyl) sebacate, tetraethylene glycol/di(2-ethyhexoate), diisodecyl adipate, and triethylene glycol/di(2-ethylhexoate). Total plasticizer concentration should be between 35 and 60 parts per hundred of resin (phr), preferably between 40 and 55 phr, and most preferably between 45 and 50 phr. Combinations of plasticizers are preferred.

Claims: Rod made of thermoplastic material for joining two pieces of thermoplastic surface covering sheetings together to create a seam for the surface covering with the same unique visual, characterized in that the rod comprises a laminate of a first thermoplastic layer (11), at least one second transparent thermoplastic layer (12) and a print layer (10) disposed between the first layer (11) and the second layer (12) and having a print corresponding to the image of the surface covering. Rod according to claim 1, characterized in that the second transparent layer (12) is substantially colorless. Rod according to claim 1 or 2, characterized in that the first layer (11) and the second layer (12) comprise a polymer selected from the group consisting of polyvinyl chloride or polyester. Rod according to one of the preceding claims, characterized in that the print layer (10) is a film (2) printed to the first thermoplastic layer (10) wherein on top of the printed film (2) several layers (1) of clear film (1) are laminated, which several layers (1) form the second layer (12). Rod according to one of the preceding claims characterized in that the rod has a half-round cross-sectional shape. Surface covering comprising at least two thermoplastic sheetings welded together with at least one rod according to one of the claims 1 to 5.

Inventors: BALMER RICHARD H, KURTZ DONALD L, BALMER, RICHARD H., KURTZ, DONALD L.
Applicants: ARMSTRONG WORLD IND INC, ARMSTRONG WORLD INDUSTRIES, INC.
Application year: 1996
Main classification: B29C65
IPC codes: B32B27, B29C37, B29C43, B29L31, B29K27, B29C65