Method of polyimide resin preparation

Abstract: A polyimide resin having excellent storage stability which cures to give a highly adherent, heat-resistant, and moisture-resistant film is disclosed, said resin being prepared by reacting (A) a tetracarboxylic dianhydride and (B) a diamino-functional siloxane compound having the general formula in which each R 1 is independently selected from C 1 to C 20 monovalent hydrocarbon radicals, each R 2 is independently selected from C 1 to C 20 divalent hydrocarbon radicals, R 3 is selected from the group consisting of hydrogen and -SiR 1 3 wherein R 1 is defined as above, a is an integer from 1 to 20, b is an integer from 1 to 20, c is an integer from 0 to 20, and d is an integer from 1 to 20.

Description: This invention relates to polyimide resin and method for preparing that contains silicon-bonded hydrogen on organosiloxane in the main chain. More particularly, the present invention provides a polyimide resin that has excellent storage stability and that cures to a highly adherent, heat-resistant, and moisture-resistant cured film. Polyimide resins exhibit excellent heat resistance, mechanical properties, and electrical properties. As a result, they are used as heat-resistant films, molding resins, coatings, adhesives, alpha-radiation-shielding films, and the like. SiH-functional polyimide resins are already known from JP-A 6-80779 which discloses a polyimide resin whose terminals are capped by an SiH-containing tetrahydrophthalic anhydride derivative. Similarly JP-A 6-80783 claims a polyimide resin whose terminals are capped by an SiH-functional organic radical. These resins are starting materials for the synthesis of thermosetting resins through their reaction, in the presence of hydrosilylation catalyst, with olefinic group-containing polymers. The SiH is present at the terminal position in both of these polyimide resins (hereinafter terminal-SiH polyimide resin). Polyimide resin bearing SiH in the main chain (hereinafter main chain-SiH polyimide resin) is reported in Polymer Preprints, Japan, Volume 42, pp. 486, 487, 1496 (1993). There is also a report of main chain-SiH polyimide resin prepared by running a Diels-Alder reaction between dibutadienylsilane (synthesized from dichlorosilane and a grignard reagent of butadiene) and maleic anhydride to give a SiH-functional acid anhydride, which is then reacted with aromatic diamine. One drawback to the terminal-SiH polyimide resins is the narrow range from which their SiH content can be selected. While the introduction of SiH into the main chain of polyimide resins is a good strategy for broadening this range, the main chain-SiH polyimide resins present problems from a preparative standpoint. These problems include a multistep reaction sequence for synthesis of the intermediates and the necessity of a Grignard reaction step, which is associated with large amounts of by-products. An excellent storage stability is exhibited by the solutions of our instant polyimide resins as well as by the solutions of its precursor. Our polyimide resins also exhibit an excellent adherence to a variety of substrates. The present invention takes as its object the introduction of a novel polyimide resin that has silicon-bonded hydrogen on organosiloxane in the main chain. An additional object is a method for preparing said resin. Other objects of this invention are the introduction of a polyimide resin that has an excellent storage stability and that has high adherence to a variety of substrates. The polyimide resin of this invention is prepared by reacting (A) a tetracarboxylic dianhydride and (B) a diamino-functional siloxane compound having the general formula in which each R 1 is independently selected from C 1 to C 20 monovalent hydrocarbon radicals, each R 2 is independently selected from C 1 to C 20 divalent hydrocarbon radicals, R 3 is a hydrogen atom or an SiR 1 3 group wherein R 1 is defined as above, a is an integer from 1 to 20, b is an integer from 1 to 20, c is an integer from 0 to 20, and d is an integer from 1 to 20. This invention also relates to a method for the preparation of polyimide resin, wherein a polyamic acid intermediate is first synthesized by the reaction of the above described components, at a component (A) to component (B) molar ratio of 1:0.5 to 1:1.5, and is thereafter subjected to a cycloimidation reaction. The tetracarboxylic dianhydride (A) of the present invention comprises those tetracarboxylic dianhydrides known as precursors for polyimide resins. This component is exemplified by pyromellitic dianhydride, benzophenonetetracarboxylic dianhydride, 3,3',4,4'-biphenyltetracarboxylic dianhydride, or 2,2-bis(3,4-benzenedicarboxylic anhydride)perfluoropropane. These may be used individually or as mixtures of two or more. The diamino-functional siloxane compound (B) of the present invention has the following formula. Each R 1 is independently selected from monovalent hydrocarbon radicals having 1 to 20 carbons, and R 1 is exemplified by alkyl radicals such as methyl, ethyl, propyl, and butyl; or by aryl radicals such as phenyl, tolyl, xylyl, and naphthyl. Each R 2 is independently selected from divalent hydrocarbon radicals having 1 to 20 carbons, and R 2 is exemplified by alkylene radicals such as methylene, ethylene, propylene, butylene, heptylene, and hexylene; or by arylene radicals such as phenylene and tolylene. R 3 is the hydrogen atom or an SiR 1 3 group, wherein R 1 is defined as above. R 3 is specifically exemplified by the hydrogen atom, trimethylsilyl, and tert-butyldimethylsilyl. The subscript a is an integer having a value of 1 to 20; b is an integer having a value of 1 to 20; c is an integer having a value of 0 to 20; and d is an integer having a value of 1 to 20. This diamino-functional siloxane compound is exemplified by the following compounds, in which Me hereinafter denotes a methyl radical. and Various methods exist for the preparation of these diamino-functional siloxane compounds. One such example is provided by the following equation. Insofar as the objects of the present invention are not impaired, the present method contemplates the copolymerization of other diamino compounds with the aforementioned diamino-functional siloxane compound. Other diamino compounds are exemplified by aromatic diamines such as p-phenylenediamine, m-phenylenediamine, 4,4'-diaminodiphenyl ether, 4,4'-diaminodiphenylmethane, 4,4'-diaminodiphenylpropane, and 4,4'-diaminodiphenyl sulfone; aliphatic diamines such as ethylenediamine, hexamethylenediamine, and decamethylenediamine; or diamino-functional siloxane compounds with the following formulas. Polyimide resin according to the present invention is prepared by first synthesizing the polyamic acid intermediate by reacting the above-described tetracarboxylic dianhydride (A) with the above-described diamino-functional siloxane compound (B) and thereafter subjecting this polyamic acid intermediate to cycloimidation. The component (A) to component (B) molar ratio is from 1:0.5 to 1:1.5, and is preferably from 1:0.8 to 1:1.2. The use of solution polymerization methodologies will generally be advantageous for the synthesis of this polyamic acid intermediate. The solvent employed in this solution polymerization is exemplified by N,N-dimethylformamide, N,N-dimethylacetamide, N-methyl-2-pyrrolidinone, dimethyl sulfoxide, diethylene glycol dimethyl ether, dibutyl ether, toluene, xylene, and butyrolactone. These may be used singly or as mixtures of two or more. The temperature for synthesis of the polyamic acid intermediate generally ranges from -20°C to 150°C, and preferably ranges from -5°C to 100°C. Various methods are available for running the cycloimidation of the polyamic acid intermediate to give polyimide resin. One example is azeotropic dehydration. Therein, a solution of solvent-soluble polyimide is obtained by mixing an azeotropic dehydrating solvent, such as toluene or xylene, with the aforementioned polyamic acid solution, and then running an azeotropic dehydration on this mixture by heating at 80°C to 300°C, preferably at 120°C to 200°C. In addition, highly adherent polyimide resin can be produced on a substrate, such as a silicon wafer, or aluminum sheet, by coating thereon the polyamic acid solution, or polyimide solution, and by then curing by heating to 100°C to 300°C, and preferably 130°C to 250°C. The polyimide resin of this invention exhibits an excellent solution stability and cures to give a cured film that is highly adherent and strongly resistant to heat and moisture. These properties make our polyimide resin useful as a protective coating for electronic components where heat and moisture resistance are critical. Example 1 Pyromellitic dianhydride (6.3 g) and 34.8 g of a mixture of N,N-dimethylacetamide and xylene (mixture weight ratio = 95:5) were introduced under a nitrogen current into a four-neck flask equipped with a stirrer, addition funnel, and thermometer, and were then stirred. A diamino-functional siloxane compound (11.1 g) with the following formula and 34.8 g of a mixture of N,N-dimethylacetamide and xylene (mixture weight ratio = 95:5) were then added dropwise from the addition funnel over a period of 29 minutes, during which time the reaction temperature varied from 29°C to 37°C. The reaction was subsequently stirred for 3.5 hours at 37°C to 26°C. A Dean-Stark trap was then attached and an azeotropic dehydration was run for 8 minutes at 144°C to 146°C. Cooling to room temperature and filtration then gave 77.3 g of a solution of a polyimide with the following repeat units: The infrared absorption spectrum of this solution contained the SiH signal at 2130 cm -1 , and signals for the imide moiety were at 1780 cm -1 and 1720 cm -1 . When this polyimide solution was held for 6 months at room temperature, it remained homogeneous and was free of such changes as the development of gel or precipitate, an increase in viscosity, and the like. The prepared polyimide solution was also coated on a silicon wafer, glass plate, and aluminum sheet, and the respective polyimide films were prepared by an initial cure, accomplished by heating for 3 hours at 160°C in an oven. This was followed by a pressure cooker test for 20 hours at 121°C and 100% RH. Crosscut adhesion testing was run on each of the polyimide films, and these results are reported in Table 1. The instant polyimide resin exhibited an excellent adhesion for the various substrates. Example 2 Pyromellitic dianhydride (7.1 g) and 48.6 g of a mixture of N,N-dimethylacetamide and xylene (mixture weight ratio = 95:5) were introduced under a nitrogen current into a four-neck flask equipped with a stirrer, addition funnel, and thermometer, and were stirred. A diamino-functional siloxane compound (17.2 g) with the following formula and 48.6 g of a mixture of N,N-dimethylacetamide and xylene (mixture weight ratio = 95:5) were then added dropwise from the addition funnel over a period of 35 minutes, during which time the reaction temperature varied from 28°C to 36°C. The reaction was subsequently stirred for 3 hours at 36°C to 26°C. A Dean-Stark trap was then attached and an azeotropic dehydration was run for 9 minutes at 135°C to 142°C. Cooling to room temperature and filtration then gave 104.2 g of a solution of a polyimide with the following repeat units: The infrared absorption spectrum of this solution contained the SiH signal at 2130 cm -1 , and signals for the imide moiety were at 1780 cm -1 and 1720 cm -1 . When this polyimide solution was held for 6 months at room temperature, it also remained a homogeneous solution and was free of such changes as the development of gel or precipitate, an increase in viscosity, and the like. This polyimide solution was also subjected to crosscut adhesion testing as in Example 1, and these results are reported in Table 1. The instant polyimide resin exhibited an excellent adhesion for the various substrates. Example 3 Pyromellitic dianhydride (7.1 g) and 38.0 g of a mixture of N,N-dimethylacetamide and xylene (mixture weight ratio = 95:5) were introduced under a nitrogen current into a four-neck flask equipped with a stirrer, addition funnel, and thermometer and were stirred. A diamino-functional siloxane compound (11.2 g) with the following formula 0.7 g of 4,4'-diaminodiphenyl ether, and 38.0 g of a mixture of N,N-dimethylacetamide and xylene (mixture weight ratio = 95:5) were then added dropwise from the addition funnel over a period of 32 minutes, during which time the reaction temperature varied from 25°C to 29°C. The reaction was subsequently stirred for 4 hours at 29°C to 25°C followed by azeotropic dehydration. Cooling to room temperature and filtration then gave 90.9 g of a solution of a polyimide with the following repeat units: and these units being present in a molar ratio of 9 to 1, respectively. The infrared absorption spectrum of this solution contained the SiH signal at 2130 cm -1 and signals for the imide moiety were at 1780 cm -1 and 1720 cm -1 . When this polyimide solution was held for 6 months at room temperature, it remained a homogeneous solution and was free of such changes as the development of gel or precipitate, an increase in viscosity, and the like. This polyimide solution was also subjected to crosscut adhesion testing as in Example 1, and these results are reported in Table 1. The instant polyimide resin exhibited an excellent adhesion for the various substrates. Comparative Example 1 Pyromellitic dianhydride (6.4 g) and 31.5 g of a mixture of N,N-dimethylacetamide and xylene (mixture weight ratio = 95:5) were introduced under a nitrogen current into a four-neck flask equipped with a stirrer, addition funnel, and thermometer and were stirred. A diamino-functional siloxane compound (9.4 g) with the following formula and 31.5 g of a mixture of N,N-dimethylacetamide and xylene (mixture weight ratio = 95:5) were then added dropwise from the addition funnel over a period of 14 minutes, during which time the reaction temperature varied from 26°C to 33°C. The reaction was subsequently stirred for 3 hours at 33°C to 25°C. A Dean-Stark trap was then attached and an azeotropic dehydration was run for 13 minutes at 140°C to 144°C. Cooling to room temperature and filtration then gave 64.6 g of a solution of a polyimide with the following formula repeat units: The infrared absorption spectrum taken on this solution contained signals for the imide moiety at 1780 cm -1 and 1720 cm -1 . The development of a white precipitate was observed on the second day as this polyimide solution was held at room temperature. This polyimide solution was also subjected to crosscut adhesion testing as in Example 1, and these results are reported in Table 1. For each substrate, the performance of this comparative polyimide resin was inferior to that of the SiH-functional polyimide resins of Examples 1 to 3. Results of crosscut adhesion testing on the polyimide films conditions after initial cure (160°C. 3 hours) after pressure cooker test (121°C, 100% RH. 20 hours) substrate: silicon wafer glass Al silicon wafer glass Al Example 1 0 0 0 0 3 0 Example 2 0 0 0 0 2 0 Example 3 0 2 1 0 4 4 Comparative Example 1 67 76 63 100 77 90

Claims: A method for preparing a polyimide resin comprising: (I) reacting (A) a tetracarboxylic dianhydride and (B) a diamino-functional siloxane compound having the general formula in which each R 1 is independently selected from C 1 to C 20 monovalent hydrocarbon radicals, each R 2 is independently selected from C 1 to C 20 divalent hydrocarbon radicals, R 3 is selected from hydrogen atom or -SiR 1 3 wherein R 1 is defined as above, a is an integer from 1 to 20, b is an integer from 1 to 20, c is an integer from 0 to 20, and d is an integer from 1 to 20, wherein said component (A) and said component (B) is reacted in a molar ratio of 1:0.05 to 1:1.5, thereby forming a polyamic acid; and (II) reacting the polyamic acid from step (I) to form a polyimide. The method according to claim 1, wherein R 1 is methyl. The method according to claim 2, wherein R 3 is hydrogen. The method according to claim 1, wherein said dianhydride (A) is selected from the group consisting of pyromellitic dianhydride, benzophenonetetracarboxylic dianhydride, 3,3',4,4'-biphenyltetracarboxylic dianhydride and 2,2-bis(3,4-benzenedicarboxylic anhydride)perfluoropropane. The method according to claim 1, wherein said diamino-functional siloxane compound (B) has a formula selected from the group consisting of and in which Me denotes a methyl radical. The method according to claim 1, wherein a = 1, b = 1 and c = 1. The polyimide resin obtainable by the method of claims 1-6.

Inventors: NAKASHIMA HISATAKA, NAKASHIMA, HISATAKA, Nakashima, Hisataka, Dow Corning Toray Silicone Co
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE CO., LTD.
Application year: 1995
Main classification: C08G73
IPC codes: C08G77, C08G73