Process for producing nickel hydroxide from elementary nickel

Abstract: The invention provides a method of producing nickel hydroxide from elemental metal. Elemental nickel is first introduced into an aqueous ammonia or ammonia/ammonium salt solution capable of dissolving nickel. The potential, as measured by a standard calomel electrode, is allowed to reach a negative or reducing level. Oxygen is added to the aqueous solution at a rate that maintains the negative potential to facilitate the conversion of elemental nickel to nickel hydroxide. Nickel hydroxide may be readily precipitated from the aqueous solution.

Description: FIELD OF THE INVENTION This invention relates to a process for producing nickel hydroxide from nickel powders. In particular, this invention relates to conversion of nickel powder to nickel hydroxide in aqueous solutions containing ammonia and nickel ions. BACKGROUND OF THE INVENTION Nickel hydroxide is an important material in the manufacture of positive nickel electrodes for alkaline batteries and industrial applications. Essentially all known processes for making nickel hydroxide are based exclusively on caustic precipitation of nickel hydroxide from nickel salt solutions. For example, typical nickel salt solutions for forming nickel hydroxide include nickel sulfate, nickel chloride or nickel nitrate. Unfortunately, methods of production that rely upon caustic precipitation of nickel salts involve a number of operating steps and produce environmentally unacceptable effluents. The direct conversion of Ni powder into nickel hydroxide was first described in Australian Pat. No. 626,648 ('648). The process of the '648 patent disclosed the use of ammonia and oxygen under pressure to form nickel hydroxide from nickel powder in aqueous solutions. However, the '648 patent states that conversion of Ni powders into nickel hydroxide in ammonium hydroxide solutions can be achieved, at practical rates, only at elevated temperatures and oxygen partial pressures. At lower temperatures and oxygen partial pressures, the rate of Ni conversion is impractically slow. For example, only about 0.1% Ni dissolved from nickel powder in a 10 molar NH 3 solution at 55°C and 2 atmospheres oxygen partial pressure during 4 hours of batch reaction. It was later disclosed in EPO Pat. Publication No. 575,093 ('093) that when using nitric acid as an oxidant of nickel powder, atmospheric operations may be used to produce nickel hydroxide. However, the problem with the process of the '093 publication is that nitrate impurity levels exceed customer requirements for some applications. The use of nitric acid is believed to cause entrainment of nitrate in the nickel hydroxide. It is an object of this invention to provide a method for producing nickel hydroxide from nickel powder at atmospheric pressure conditions. It is a further object of this invention to provide a method of reducing nitrate impurities. It is a further object of this invention to control crystallinity of nickel hydroxide produced from nickel powder. DESCRIPTION OF THE DRAWING Figure 1 is a plot of potential as a function of time of nickel powders in 1N (NH 4 ) 2 , SO 4 solution at a pH of 8.8 and a temperature of 70°C; and Figure 2 is a plot of potential as a function of time of nickel powders in 1N(NH 4 ) 2 SO 4 solution at a pH of 9.1 and a temperature of 50°C. SUMMARY OF THE INVENTION The invention provides a method of producing nickel hydroxide from elemental metal. Elemental nickel is first introduced into an aqueous ammonia or ammonia/ammonium salt solution having the capability of dissolving nickel. The potential, as measured by a standard calomel electrode, is allowed to reach a negative or reducing level. Oxygen is added to the aqueous solution at a rate that maintains the negative potential to facilitate the conversion of elemental nickel to nickel hydroxide. Nickel hydroxide may be readily precipitated from the aqueous solution. DESCRIPTION OF PREFERRED EMBODIMENT It has been discovered that elemental nickel can be converted directly into nickel hydroxide in an aqueous solution at atmospheric pressure using a controlled rate of oxygen addition. Advantageously, the nickel is in the form of particulate or powder having a surface area of at least 0.2 m 2 /g. The oxygen addition is controlled to maintain a negative or reducing redox potential, with respect to a standard calomel electrode (S.C.E.). At negative redox potentials, the reactions responsible for nickel powder conversion into nickel hydroxide operate effectively at atmospheric oxygen partial pressures. The aqueous solution should contain free ammonia and be capable of dissolving nickel. (Unless the solution is capable of dissolving nickel, the reaction will not proceed.) A relatively small concentration of ammonium is inherently present in the ammonia-containing solution, since the ammonium/ammonia reaction is reversible. The solution optionally contains an anion. Advantageously, the anion arises from an ammonium salt, such as e.g. ammonium sulfate, acetate, chloride or formate. Ammonium salts may be added to increase solubility of nickel in the solution. Ammonium sulfate has been found to be particularly effective at increasing reaction rate. Initial tests with ammonium acetate have produced acceptable results that are comparable to additions of ammonium sulfate. However, recent tests have indicated that the reaction readily proceeds in solutions free of or substantially free of anions, e.g. other than hydroxide ions. Examples Example 1: Initially, 1.5 L of approximately 1.2 normal ammonium sulfate solution was placed into a 2 L reaction-vessel. The reaction vessel was equipped with four baffles, 6-blades radial turbine impeller, a pH electrode and a potential electrode. The reactor was opened to the atmosphere via a condenser. The pH of the solution was adjusted to 9 using 30% ammonium hydroxide and the mixture was then heated to 70°C. An addition of 225.7 g of INCO type 255 nickel powder was then reacted in the vessel over a period of about 15 minutes (INCO is a trademark of the Inco family of Companies.) At the end of this period, the solution potential was measured and showed a value of -750 mV with respect to a standard calomel electrode. (All potentials listed in this specification were measured with a standard calomel electrode.) Oxygen flow was introduced at this point into the suspension at the rate of 50 mL/minute. The potential of the reaction mixture remained unchanged after reacting for 2 h and 40 minutes. The reaction was allowed to proceed for a total of 20 h, at which point the potential increased to -15 mV. The resulting 1.2 L nickel hydroxide slurry was filtered and the filter cake washed with water. The filtration of nickel hydroxide was very good. The remaining about 300 mL of the nickel hydroxide slurry was saved as a seed material for the next test. Dry filter cake analyzed in mass %: 62.6 total Ni, 2.75 elemental nickel and 0.055 NH 3 and the filtrate contained in g/L: 31.2 Ni, 64.9 total ammonia and 48 sulfate. Example 2: The test of Example 1 was repeated using the filtrate and 300 mL of unfiltered slurry from the previous test (Example 1) as the feed solution. The potential of the suspension after the addition of type 255 nickel powder into the reactor was around -700 mV and remained unchanged for at least 4.5 h of reacting. The test was terminated after 23 h, at which point the potential increased to 0 mV. The nickel hydroxide produced analyzed in mass %: 0.37 element Ni, 62.0 total Ni and 0.058 NH 3 and the filtrate analyzed in g/L: 30.7 Ni, 59.5 total ammonia and 55.5 sulfate. Example 3: The test of Example 1 was repeated using the filtrate from the test of Example 2 and type 255 nickel powder. However, the oxygen addition at the rate of 50 mL/min. was initiated too soon, when the redox-potential was at only about -120 mV. No reaction was observed during 16 h of operation at which point the experiment was Example 4: Filtrate from the test of Example 3 was placed into the same reaction vessel and heated to 55°C, 225 g of Type 255 powder was then introduced into the reactor and allowed to agitate until the potential decreased to -670 mV, at which point the oxygen addition was started at the rate of 50 mL/min. The potential was followed and recorded versus time: Time, Min Potential, mV 0 -670 -- Oxygen addition started 10 -640 20 -596 55 -610 130 -220 180 -160 The reaction of nickel conversion into nickel hydroxide, which started as expected in view of Examples 1 and 2, having stopped after some 100 minutes of reaching, due to a too high a rate of oxygen addition at this operating temperature (55°C). Example 5: Potential of nickel suspension was measured as a function of time and temperature. Approximately 1N solution of ammonium sulfate was spiked with a concentrated aqueous ammonia to a pH of about 9. 750 mL of this solution was placed into an agitated vessel, which was temperature controlled. When the solution was heated to the desired temperature, 110 g of Type 255 nickel was added and the potential followed and recorded versus time. The result for two different temperatures are shown below: Time, (Min.) 50°C 70°C 0 0 0 0.5 -20 -200 1 -40 -490 1.5 -150 -540 2 -170 -560 3 -250 -585 4 -350 -610 5 -400 -620 6 -420 -620 8 -470 -620 10 -500 -630 It can be seen that the potential of the above nickel powder suspensions - is a very strong function of both the contact time and temperature.Similar tests were performed using other nickel powders (INCO type 123 powder and a sulfur activated powder). The results are shown diagrammatically in Figure 1 for 70°C and in Figure 2 for 50°C. It can be seen from the Figures that powder type also has a significant effect on the rate of developing a highly reducing potential of the nickel powder suspension. Example 6: The effect of solution pH on the potential of nickel powder suspensions was studied for two different powders using a similar procedure as that applied in Example 5, except that the temperature was kept at 50°C. The pH of the feed solution (1 N ammonium sulfate) was adjusted to the desired value, using 30% ammonia, prior to the nickel powder addition. The results are presented in Table 3 below: Potential [mV] Time, (Min.) Type 123 pH=7.0 Type 123 pH=7.5 Type 255 pH=8.5 Type 255 pH=9.0 0 +90 +45 1 -160 -270 -280 -40 2 -360 -460 -260 -170 3 -495 -530 -250 -250 4 -520 -560 -250 -350 5 -570 -260 -400 6 -560 -590 -260 -420 7 -595 8 -600 -390 -470 9 -610 10 -580 -615 -390 -500 12 -500 -525 15 -590 -624 -540 -550 20 -590 -625 -560 -560 25 -593 -628 -580 -570 30 -593 -630 -590 -580 40 -605 -600 50 -615 -610 60 -625 -625 The above Example illustrated that the rate of potential decrease (or the rate of nickel powder activation) increases with the solution pH for both Types 123 and 255 powders. The activation of Type 123 powder was are rapid than that of Type 255 powder (In spite of its greater surface area 0.68m 2 /g versus 0.34-0.44 m 2 /g for type 123.) Example 7: The effect of thiosulfate anion addition to the feed solution on the nickel powder activation was tested. Tests were performed in 1 N ammonium sulfate solution at pH=7 and 50°C in the absence and in the presence of 1 g/L sodium thiosulfate (Na 2 S 2 O 3 ) using Type 123 nickel powder. The results are shown in Table 4 below: Potential [mV] Time [min] Na 2 S 2 O 3 Absent 1 g/L Na 2 S 2 O 3 0 +90 +45 1 -160 -540 2 -360 -545 3 -495 -553 4 -520 -562 5 -572 6 -560 -580 8 -590 10 -580 -592 15 -590 -592 20 -590 -593 25 -593 -592 30 -593 -590 Table 4 illustrates that a small addition of thiosulfate anion enhances the rate of nickel powder activation quite substantially. Example 8: Potential of nickel powder suspensions was measured in three acidic solutions. 1.7 L of distilled water was placed into a an vessel, which was temperature controlled. After heating the contents to 50°C, a solution of approximately 1 M H 2 SO 4 was added until the desired pH was obtained. Then 256.9 g of INCO Type 123 powder were added into the vessel and automatic titrator was used to maintain the desired pH with the 1 M H 2 SO 4 solution. The potential of the nickel powder suspension was measured and recorded versus time. The results are presented in Table 5 below. Potential [mV] Time [min] pH=2.0 pH=4.0 pH=6.0 0 - - +120 1 -420 -450 -140 2 -430 -495 -180 3 - -510 -190 4 -430 -510 -190 5 -430 -510 -200 6 - -510 - 7 -420 -510 -210 8 - -510 - 10 - -510 -450 15 -420 -510 -510 20 -510 25 -550 30 -510 From Table 5 it was demonstrated that the potential of nickel powder suspensions may be readily reduced (or nickel powder activated) quite readily in acidic solutions, containing as little as around 0.000001 equivalents of H + per liter. The rate on nickel powder activation increases with the acid concentration and becomes quite rapid somewhere between 0.00001 and 0.0001 H + /L. Example 9: The potential of nickel powder suspension was measured at 53°C in 1 N ammonium acetate, adjusted to pH=9, with 30% ammonia, using Type 123 powder. The results are given below: Time [min] Potential [mV] 0 -91 1 -720 2 -760 3 -780 4 -792 5 -797 6 -800 8 -803 10 -803 15 -801 20 -800 25 -799 30 -797 The activation of nickel powder in ammonia acetate is also very rapid. Example 10: Feed solution for this test was made-up by mixing 102 g of concentrated ammonia (29% NH 3 ) with 1400 mL of distilled water. The ammonia concentration in the resulting solution was approximately 1.2 N and had a pH of 11.4 at 25°C. The test apparatus consisted of a 2 L resin kettle (glass cylindrical vessel) equipped with four baffles, a 5 cm diameter radial turbine impeller having 6 blades, a reflux condenser (to prevent ammonia-water losses during the tests), a redox combination electrode, an oxygen sparger and a heating mantle to maintain the desired temperature. The feed solution was heated to 60°C, at which temperature the pH meter indicated a pH of 9.9, and after reaching this temperature 170 g of Type 123 Ni powder were added. The redox potential decreased from a positive value to -710 mV in approximately 20 min. Then 170 g of Ni(OH) 2 seeds were added and after about 2 h the oxygen was started at a rate of 30 mL/min. The oxygen flow remained on for a total of 1430 minutes. After 1430 minutes, the redox was 0 mV and the test was terminated. The reacted slurry was then filtered and the cake washed with water and dried in an oven at 70°C. Mass of wet cake recovered was 433 g and mass of dry solids recovered was 350 g. Analysis - of the solids was 0.08 (mass %) elemental nickel and 63.8 (mass %) total nickel. The conversion of Ni powder into nickel hydroxide was essentially complete. Example 11: This Example was carried out in a similar way as Example 10, except that the feed solution was approximately 2 N ammonia and the operating temperature was 80°C. Also the ammonia concentration was kept constant during the test by adding a concentrated aqueous ammonia on demand to maintain a constant pH of 11.2. The initial potential, following the activation was -780mV. Oxygen flow was started at this point at a rate of 50 mL/min. The test was terminated after 1040 minutes (when the potential became positive). The reacted slurry was filtered, the cake washed with water, dried in an oven at 70°C and analyzed. The dried cake contained 63.6% Ni and 0.04% NH 3 , indicating essentially complete conversion of Ni powder into nickel hydroxide. From the above examples, a continuous process for making nickel hydroxide can be formulated in which nickel powder and a recycled ammonia / ammonium sulfate (or other ammonium salt) aqueous solution are introduced into the reaction system, comprising a single reactor or a number of reactors in series. It is recognized that elemental nickel may be used in any form. Advantageously, elemental nickel is added as nickel powder due to its simplified handling characteristics, commercial availability and relatively large surface area. The reactor apparatus, which operates at atmospheric pressure, is supplied with oxygen, ammonia, nickel and optionally an ammonium salt at controlled rates for continuous operations. Oxygen is added at a controlled rate in order to maintain the reducing potential of the reaction mixture, to cause an oxidative nickel dissolution, which leads to the precipitation of the desired nickel hydroxide product. Oxygen may alternatively be added from a donor source or from an oxygen-containing gas. During operation, oxygen diffusion appears to control the reaction rate. In fact, under normal operating conditions, the steps of dissolution of nickel to formation of nickel hydroxide appear to occur instantaneously. Since oxygen diffusion rate appears to control the reaction, it is preferred to add oxygen in substantially pure form. Elemental nickel containing a passive film may be activated by several separate methods at pH levels from less than 0 to as high as 14. For purposes of this specification, activated nickel is defined as nickel capable of dissolving in an ammonia-containing solution at atmospheric pressure in the presence of oxygen. First, nickel may be activated by contacting the feed powder with recycled process solution in a separate agitating tank with the resulting suspension being fed into a reactor. Second, the powder may be activated in a separate solution such as dilute acid and transferring the activated nickel after a separation operation into the reactor. Third, the nickel may be activated by introducing it directly into a reactor maintained at a redox-potential below about -200mV as measured with respect to a standard calomel electrode. Finally, any suitable reducing agent such as hydrogen gas may be used to reduce any passive oxygen film surrounding the nickel to effectively activate the nickel. Using a separate vessel for activation provides the advantage of improved pH control. Alternatively, the first and second activation steps may be preformed in batch operations. After a reaction has initiated, the reaction continues to operate effectively even when the temperature decreases or the potential increases. Advantageously, potentials below about -100 mV with respect to S.C.E., are maintained to facilitate the conversion of nickel powder into nickel hydroxide. Advantageously, potential is maintained between about -100 mV and -600 mV for effective conversion. Most advantageously, potential is maintained within the range of -200mV to -500mV. Advantageously, pH of the solution is maintained between 8.5 and 12 during conversion to nickel hydroxide. Most advantageously, pH of the solution is maintained between 9 and 12 during conversion to nickel hydroxide. Prior to their introduction into the reaction apparatus the recycled feed solution and the nickel feed powder may optionally be contacted for a suitable period of time to reduce the supsension's potential to the desired level. Experimentation has indicated that the operating temperature may be between room temperature and the boiling temperature. For purposes of this specification, room temperature is defined as being about 20°C. However, it has been found that nickel hydroxide powders produced at temperatures close to the boiling temperature are more crystalline and less amorphous than nickel hydroxide powders produced at lower temperatures. The end-use of nickel hydroxide would dictate the operating temperature. For example, a general purpose, more crystalline, hydroxide can be produced at higher temperatures (close to the boiling point), while nickel hydroxide destined for batteries should preferably be made at lower temperature, e.g. 50°C. Advantageously, "amorphous" nickel hydroxides are produced at temperatures between 20° and 70°C. Most advantageously, "amorphous" nickel hydroxides are produced at temperatures between 30°C and 60°C. Optionally, the crystallinity may be reduced by the addition of a suitable crystal habit modifier(s) into the reactor system. After formation of nickel hydroxide, reacted nickel hydroxide slurry exiting the reaction system is most advantageously subjected to a magnetic separation to remove and recycle any unreacted nickel powder back to the reactor. Initial tests have demonstrated that magnetic separation is a highly effective method for ensuring elemental powder does not contaminate the nickel hydroxide. Furthermore, nickel hydroxide slurry is most advantageously subjected to a solid-liquid separation to obtain the desired nickel hydroxide product and the aqueous ammonia or ammonia/ammonium sulfate solution for recycling. Advantageously, nickel hydroxide is filtered and washed. If desired, the water washed cake may be contacted with an alkaline solution (NaOH, KOH, etc.) in order to reduce the concentration of anionic impurities, which have entered the structure of Ni(OH) 2 during its crystallization. During this contact, an anion exchange process occurs whereby anion impurities (e.g. sulfate, acetate) in the solids phase are exchanged by an equivalent quantity of hydroxyl group from the aqueous solution. The filter cake may then be dried in a suitable dryer to form the final product. Alternatively, the nickel hydroxide may be classified into a coarse fraction and a fine fraction to control ultimate size of nickel hydroxide particulate. Most advantageously, the fine fraction from the classification step is recycled into a nickel hydroxide precipitation apparatus to provide seed for the growing of coarse nickel hydroxide. It is apparent from the above that the instant process can be conveniently set up as a closed loop process in which the ammonia or ammonia/ammonium salt reaction medium is recycled and no liquid effluent, containing reaction by-products is generated. The pH of the recycling solution should be checked and adjusted if necessary to be above 8. There is illustrated and described herein specific embodiments of the invention. Those skilled in the art will understand that changes may be made in the form of the invention covered by the claims.

Claims: A method of producing nickel hydroxide from elemental nickel, which method comprises forming a mixture of the elemental nickel and an aqueous solution of ammonia and adding oxygen to the said mixture whilst maintaining the redox potential of the mixture at a potential that is negative with respect to a standard calomel electrode, to convert said nickel into said nickel hydroxide. The method of claim 1 including the additional step of filtering nickel hydroxide from said aqueous solution. The method of claim 1 or claim 2 wherein said aqueous solution has a pH between about 8.5 and 12 during said converting of said dissolved nickel to nickel hydroxide. The method of any one of claims 1 to 3 wherein said aqueous solution has a temperature between about 20°C and 70°C for forming amorphous nickel hydroxide during said conversion of the nickel to nickel hydroxide. The method of any one of claims 1 to 4 wherein said negative potential of said mixture of elemental nickel and said aqueous solution is between about - 100mV and -600mV during said conversion of the nickel to nickel hydroxide. The method of any one of claims 1 to 5 wherein said negative potential of said mixture of said elemental nickel particles and said aqueous solution is between about -200mV and -500mV during said conversion of nickel to nickel hydroxide. The method of any one of claims 1 to 6 wherein said aqueous solution is recycled after removal of nickel hydroxide for converting additional elemental nickel into nickel hydroxide. The method of any one of claims 1 to 7 wherein said aqueous solution is substantially free of anions (other than hydroxide ions). The method of any one of claims 1 to 8 wherein said nickel hydroxide is precipitated and is classified by size into a coarse fraction and a fine fraction and said fine fraction of the said nickel hydroxide is recycled to seed precipitation of said coarse nickel hydroxide. The method of any one of claims 1 to 9 wherein said nickel particulate is activated in a separate vessel prior to introduction into said aqueous solution.

Inventors: BABJAK JURAJ, ETTELL VICTOR ALEXANDER, BABJAK, JURAJ, ETTELL, VICTOR ALEXANDER
Applicants: INCO LTD, INCO LIMITED
Application year: 1995
Main classification: C01G53
IPC codes: C01G53