Method of introducing slightly tilting homeotropic orientation into liquid crystal, liquid crystal electro-optical device, and liquid crystal light valve

Abstract: An object of the invention is to provide a method of introducing slightly tilting homeotropic orientation into a liquid crystal layer by oblique evaporation of inorganic material by one step, and a further object is to apply this method to provide a reliable liquid crystal electro-optical device or a liquid crystal light valve. Fig. 1 shows an example of the method to introduce the slightly tilting homeotropic orientation into the liquid crystal layer by the one step of the oblique evaporation of the inorganic material. The orientation film is formed by the one step oblique evaporation. An incident angle is set from 45° to 70° relative to a parallel direction of the substrate, and a film thickness is set to 20nm through 500nm measured during the film deposition by a film thickness gauge disposed at an incident angle of 90° at the same distance from the evaporation source as the substrate. The orientation film is used in the liquid crystal electro-optical device or the liquid crystal light valve.

Description: The present invention relates to a method of introducing a slightly tilted homeotropic orientation into a liquid crystal. The liquid crystal layer having the homeotropic orientation is utilised as an optical modulation layer of an electro-optical device. Particularly, the present application is valuable when applied to a liquid crystal light valve used in an image projection apparatus and a high luminance image projection apparatus such as a video projector. The methods of introducing the homeotropic orientation into the liquid crystal include; a surface processing method by a silane coupling agent exemplified by octa-decyl tri-ethoxy (or methoxy) silane (ODS) and dimethyl octa-decyl [3-(tri-methoxysilil) propyl] ammonium chloride (DMOAP) having a long alkyl chain, a surface reaction method by a long chain alcohol or a long chain amine, and a coating method of a polymer material such as a polyamide and a polyamide having an alkyl side chain. These methods are common in that liquid crystal molecules are oriented in a direction of the long chain alkyl base by interaction between the long chain alkyl base exposed on the surface and the liquid crystal molecules. In realising the homeotropic orientation by means of these methods, it is necessary to introduce slight tilt into the liquid crystal alignment. For this, underlayer processing is carried out such that silicon monoxide or the like is obliquely evaporated, oxide material is obliquely sputtered, or oxide material is sputtered while a substrate is moved, before the surface is processed by a silane coupling agent or the surface is treated by the long chain alcohol or the long chain amine. Further, in the case using the polyamide, the polyamide having an alkyl side chain or the like, after forming the coating, rubbing process thereof is carried out by a cloth or buff, for example. A special method utilises an evaporation apparatus installed with a mechanism for rotating an obliquely set substrate. An angular velocity of the rotation is controlled to impart a weight to the incident direction. Such a rotation oblique evaporation method is capable of controlling a tilt of the liquid crystal molecules along a boundary over a wide range. It is reported that the tilt orientation close to the vertical direction can be realised, by a reference paper (K. Hiroshima Japanese journal of Applied Physics, 21, P761-P763(1982)). Further orientation films are known from EP-A-0 541 388 and from the article by G. Hanck, physica status solidi A, 70, P. K43-K46 (1982). The liquid crystal layer having the homeotropic orientation is applied to the liquid crystal electro-optical device used in colour display or else based on electrically controlled birefringence (ECB) effect. Further, as disclosed in the United States Patent 3592527 and others, the liquid crystal light valve is a device typically comprised of a photo-conductive layer, a light reflecting layer and a liquid crystal layer. A specific type of the liquid crystal light valve utilises the above noted ECB mode where the nematic liquid crystal is homeotropically oriented in the liquid crystal layer. This type achieves high contrast, and performs optical amplification utilised in a product of the high luminance image projection apparatus. In introduction of the homeotropic orientation into the liquid crystal, it is rather easy to obtain the perfect vertical orientation to the substrate according to the above mentioned conventional methods. However, if an electric field is applied to the liquid crystal layer of the perfect vertical alignment, distortion may occur in the liquid crystal layer due to torque by coupling between the electric field and the negative dielectric anisotropy of the liquid crystal molecules. A director of the liquid crystal molecules is not restricted, thereby causing a mixed state of plural domains having different molecule directors to generate a discrimination line along borders of the domains. This discrimination line may degrade the contrast of a directly viewed type of the display. Even worse, the discrimination line may seriously degrade resolution and contrast of the liquid crystal light valve used in the high luminance projector. Therefore, as described before, the slightly tilted homeotropic orientation is intoduced by the anisotropic treatment of the underlayer or by the after-treatment by rubbing. However, obviously complicated procedure in required for the anisotropic treatment of the underlayer and the coupling process. Such a method suffers from various troubles in an industrial view. Further, the surface subjected to the coupling process has a seriously poor adhesion to an adhesive, thereby hindering reliability of the device. In the method of introducing the slight tilt by rubbing, the orientation film material importing the homeotropic orientation has a side chain of a long alkyl base. Therefore, the film is very soft and tends to create scratch by the rubbing. Quite severe condition is required for the rubbing. It is difficult to obtain a stable tilt. Further, the rubbing step itself suffers from drawbacks such as generation and adhesion of dust by the rubbing. The rotation evaporation method requires a quite special apparatus, where a rotation axis must coincide with a centre of the substrate. Therefore, only one substrate is treated by one evaporation step. Further, as the substrate size is made large, difference between the centre and the periphery becomes significant to thereby hinder uniformity of the orientation. Such a method is never industrial. In view of the above, the first and second methods of using the organic materials are practised; however, these methods have the manufacturing problems as noted above, and may suffer from poor reliability due to the used organic materials. Particularly, in the case where the liquid crystal light valve is applied to the high luminance image projection apparatus, an intensive reading light is required. However, the organic orientation film generally used to vertically align the liquid crystal has poor light resistance due to its organic nature. Therefore, in the high luminance image projection apparatus using the strong reading light, life of the liquid crystal valve is extremely shortened, thereby necessitating frequent replacing of the liquid crystal light valve at a short interval. As described before, the rotational oblique evaporation may ensure good light resistance; however, its application to the manufacture is quite difficult. In a first aspect, the invention provides a method of preparing an orientation film for introducing slightly tilting homeotropic orientation in a liquid crystal as recited in claim 1. In a second aspect, the invention provides a liquid crystal electro-optical device as recited in claim 5. In a third aspect, the invention provides a liquid crystal light valve as recited in claim 10. The film thickness gauge is disposed at an incident angle of 90° defined with reference to a direction parallel to the surface of the gauge. Therefore, according to the invention, the liquid crystal orientation film for introducing the homeotropic orientation is formed by vacuum-evaporating an inorganic material in a given direction tilted from a normal direction of the substrate under condition that an incident angle ψ is set in a range from 45° to 70° defined with reference to a direction parallel to the substrate and that a thickness d of the orientation film is set in a range from 20nm to 500nm measured by a film thickness gauge disposed at an incident angle of 90° defined with reference to a direction parallel to the gauge, at the same distance from the evaporation source as the substrate during the film forming. Preferably, the liquid crystal is a composition having a negative dielectric anisotropy and a nematic phase at a room temperature. Advantageously, the slightly tilted direction or director is substantially set opposite or parallel between the substrates. The inventive method carries out oblique evaporation only once in the same manner as the underlayer process of the coupling agent method, and is therefore remarkable to realise the slightly tilting homeotropic orientation. Further, the invention realises the liquid crystal electro-optical device having high reliability and using the above orientation method, and particularly realises the liquid crystal light valve applicable to the high luminance projector. Embodiments of the invention will now be described, by way of example only, with reference to the accompanying diagrammatic figures, in which; Fig. 1 is a schematic diagram showing an evaporation apparatus used for forming an orientation film according to the invention to introduce slightly tilting homeotropic orientation into liquid crystal. Fig. 2 is a graph plotting tilt angles measured when ψ is varied at 50°, 54° and 57°. Fig. 3 is a schematic diagram showing structure of the inventive liquid crystal electro-optical device. Fig. 4 is a graph plotting a voltage transmittance characteristic of the inventive liquid crystal electro-optical device. Fig. 5 is a schematic diagram showing construction of the inventive liquid crystal light valve. Fig. 6 is a diagram showing experiment results of homeotropic orientation performance while the incident angle of oblique evaporation and the film thickness are varied. The above described method can introduce the slightly tilting homeotropic orientation into the liquid crystal layer solely by the inorganic material by a single and simple step, thereby significantly improving the light resistance of the liquid crystal electro-optical device such as the liquid crystal light valve. This valve is applied to the high luminance image projection apparatus with less frequent replacement of the valve, thereby advantageously realising the highly reliable products. Conventionally, the evaporation angle range of 45° to 70° in the inventive oblique evaporation film is thought to provide homogeneous orientation or horizontal alignment. This is mentioned in "liquid crystal device handbook" PP.242-247 edited by Nippon Gakujutsu Shinko-Kai 142-th section and published by Nikkankogyo Shinbun-Sha. However, as mentioned in a reference paper (W.A. Crossland et al., "Tilt angle measurements of nematic phases of cyano-biphenils aligned by obliquely evaporated films" J. Phys. D : Appl. Phys., Vol.9, 1976), these results are observed in a film thickness range lower than the inventive film thickness range. According to the invention, the thickness of the single layer oblique evaporation film is made great at the specified incident angle range which conventionally belongs to the homogeneous orientation range, to thereby realise the homeotropic orientation performance. Hereinafter, the invention is described in detail with reference to the drawings. Fig. 1 is a schematic diagram of an evaporation apparatus used for forming an orientation film effective to introduce the slightly tilting homeotropic alignment into the liquid crystal. The apparatus for forming the orientation film is an evaporation apparatus using a main pump 106 such as a diffusion pump, a turbo molecular pump and a cryopump. A vacuum chamber 101 contains therein at least an evaporation source 102, a mechanism 104 for supporting a substrate at a given angle, and a film thickness gauge 105. In the present embodiment, the main pump 106 is composed of an oil diffusion pump, the evaporation source 102 is composed of a resistance-heating boat having a slit opening, and the film thickness gauge 105 is composed of a quartz oscillator gauge. However, these components are not related to the gist of the invention, and therefore can be replaced by equivalent components without any trouble. A supporting holder 103 sets thereon a plurality of substrates so as to align surfaces thereof in the same plane, on which an orientation film is formed. Further, the supporting holder 103 is set to the holding mechanism 104 having a positioning and rotating mechanism so as to hold the surfaces at a given angle relative to a sputtering direction of evaporation particles from the evaporation source 102. According to an experiment in the present embodiment, condition of forming the orientation film is set such that the incident angle ψ is set variable at 54°, 57°, 60°, 69°, 78° and 87° defined relative to a direction parallel to the substrate, while the film thickness d (nm) is set variably at 20, 60, 100 and 140nm measured during the film deposition by the film thickness gauge disposed in a vertical direction at a distance equal between the evaporation source and the substrate. That is, the film thickness gauge is disposed so that the incident angle of the deposited material is 90° defined relative to a direction parallel to the gauge and the gauge is located at the same distance as the substrate from the evaporation source. The produced samples are assembled into a cell, an orientation state of which is observed. The experiment results are shown in Fig. 6. As can be seen from this, the homeotropic orientation is obtained by the vacuum evaporation of the single layer at a specified range of the incident angle ψ and the film thickness d. In the present embodiment, the results of which are indicated by Fig. 6, the evaporation source uses powder composed of silicon monoxide. The evaporation source can use various inorganic materials such as silicon oxide including silicon monoxide and silicon dioxide, oxide including titanium oxide, zirconium oxide and tantalum oxide, fluoride such as magnesium fluoride, sulfide such as zinc sulfide, and other materials of element, mixture or compound of element from group IV (four) of the periodic table, which includes, silicon and germanium, without any problem. Namely, slightly tilting homeotropic orientation is realised by the invention according to a surface structure obtained by the oblique evaporation at the specified condition of the film deposition. Practically, the invention can utilise almost all of the materials which can be evaporated to form the film. However, with regard to organic materials, the orientation state may be affected by polar interaction between the liquid crystal and the organic material, thereby failing to obtain the desired slight tilting. With regard to conductive materials such as metal, electric carriers flow along the surface to only enable whole on/off operation of the valve. Accordingly, the available materials are necessarily limited to an inorganic dielectric material and a semiconductor material. It is desired to select the above listed materials which are easily evaporated to produce a desired surface structure. The direction of the oblique evaporation is generally set opposite or parallel between a pair of the orientation film layers opposed to each other in the assembled cell. In the experiment of the present embodiment, the direction is set opposite. If the set direction is not opposite or parallel, twist distortion is created in the alignment of the liquid crystal molecules. It is difficult to obtain a desired phase modulation characteristic in response to an applied voltage. However, this does not negate the homeotropic orientation performance itself. If the set direction is opposite or antiparallel, the alignment state is almost free of distortion under non-application of voltage. If the set direction is parallel, the alignment contains only splay distortion. In both cases, the very stable state can be obtained. Further, in both cases, the liquid crystal molecules decline into a unique direction perfectly restricted by the application of voltage to thereby avoid generation of discrimination lines. The tilt direction is not limited to the perfect opposite direction or parallel direction. A deviation of degrees does not affect optical and electric performance in the industrial application. As seen from Fig. 6, according to the experimental condition of the present embodiment, the homeotropic orientation is obtained in the range where the incident angle ψ is not more than 69° and the film thickness is not less than 20nm. However, in an extremely low incident angle range, only a small tilt is introduced into the alignment of the liquid crystal molecules. Therefore, when an electric field is applied to the liquid crystal, the director of the liquid crystal molecules is not controlled when distortion is created within the liquid crystal layer by torque due to coupling between the electric field and the negative dielectric anisotropy of the liquid crystal molecules. This causes a mixed state of plural domains having different molecule directors to thereby generate discrimination lines along borders of the domains. This discrimination line degrades the contrast in the directly viewed type of the display. Consequently, the incident angle ψ should be set equal to or more than 45°. The description is given for this with reference to Fig. 2. Fig. 2 is a graph plotting tilt angles while ψ is varied at 50°, 54° and 57°. In this measurement, the orientation film has a thickness d of 60 and 100 nm. The cell is assembled such that the incident angles of the evaporation are set in the opposite relation to each other between the substrates in which the liquid crystal is sandwiched. The measurement is conducted by crystal rotation method to determine a mean director of the molecules within the liquid crystal layer. As extrapolation value obtained from Fig. 2, it is understood that the slight tilt is not introduced into the alignment unless the incident angle ψ is not less than 45°. Further, it is not preferable to form an extremely thick evaporation film in an industrial view of increase in throughput. For this, practically, the film thickness is set not more than 500nm. As the results, the liquid crystal orientation film to introduce the homeotropic alignment is formed by vacumm-evaporating an inorganic material in a direction tilted from the normal direction of the substrate under the condition that the incident angle ψ is set from 45° to 70° measured relative to a direction parallel to the substrate and that the film thickness d is set from 60nm to 500nm measured during the film deposition by the film thickness gauge disposed at an incident angle of 90° measured relative to a direction parallel to the gauge and at the same distance from the evaporation source as the substrate. By such a manner, the oblique evaporation is carried out only once in the same manner as the underlayer process in the method of using coupling agent so as to realise the slightly tilting homeotropic orientation. The inventive method is a remarkable one to introduce the slight tilting homeotropic orientation into the liquid crystal layer by one step of quite simple film forming. The orientation film is composed solely of the inorganic material to improve the reliability, particularly, the light resistance. The inventive method can significantly improve the reliability of the liquid crystal electro-optical device such as the liquid crystal light valve used in the highly luminant projector and the like. Hereinafter, the description is given for the liquid crystal electro-optic device and the liquid crystal light valve utilising the inventive method. Fig. 3 is a schematic diagram showing a construction of the inventive liquid crystal electro-optical device. A pair of substrates 301a and 301b are provided to sandwich liquid crystal molecules, and are each composed of a transparent glass plate having a thickness of 1.1mm. A pair of Indium Tin Oxide (ITO) transparent electrode layers 302a and 302b are formed on respective surfaces of the substrates 301a and 301b. These substrates have orientation films 303a and 303b formed on the respective transparent electrodes 302a and 302b. Then, the substrates are joined to each other through a spacer 304 to sandwich a liquid crystal layer 305. The orientation films 303a and 303b are formed according to a condition selected from the range specified in the embodiment 1. In this embodiment, the evaporation source uses powder of silicon monoxide, the incident angle ψ is set to 54° relative to the direction parallel to the substrate, and the film thickness d is set to 100nm measured during the film deposition by the film thickness gauge disposed at an incident angle of 90% at the same distance from the evaporation source as the substrate. However, as mentioned in the embodiment 1, the film forming condition of the inventive orientation film is not limited to those selected in the present embodiment, but may be altered to satisfy the given condition. The used spacer is composed of an adhesive containing silicon dioxide particles (commercial product called "Shinshikyu SW" made by Shokubai Kasei Co., Ltd.) having a mean diameter of 5.0µm to determine a gap between the pair of the substrates. The liquid crystal filled in the gap is composed of ZLI-4788-100 provided by Merk. However, the liquid crystal material is not limited to the used one, but may have various electric characteristics, optical characteristics and visco-elastic characteristics as long as the material is a composition having a negative dielectric anisotropy. Further, the gap is not limited at all. The completed cell is disposed in crossed Nicols, while an electric field is applied to measure variation of transmittance. Fig. 4 shows the results of the measurement. The white light is used in the measurement. As seem from Fig. 4, the liquid crystal electro-optical device oriented by the inventive method exhibits quite good sharpness and high contrast. Further, the inventive device can achieve display of quite high quality free of discrimination lines which would be frequently observed in the general liquid crystal device of the homeotropic orientation type and which would degrade the contrast. In the liquid crystal electro-optical device produced in the present embodiment, the ITO electrode of the respective substrates is not divided so that the device may be used as a plane shutter or the like. The contrast is over 100 : 1 to thereby realise a quite high performance shutter. The device of the embodiment utilises the ECB effect so that the device is also utilised as a wave front modulator and a colour filter. Further, the inventive orientation method can realise the ECB cell having the quite good sharpness. The ITO electrode of each substrate is divided to sufficiently enable matrix driving. However, the cell can be combined to the active matrix drive. As described above, the inventive method realises the ECB cell of good sharp threshold characteristic. Therefore, the colour display of the matrix type can be realised in combination with the active matrix driving. The thus produced liquid crystal electro-optical device is formed with the orientation film layer composed of pure inorganic material to thereby improve the light resistance. The device can be produced by steps simpler than the conventional homeotropic orientation technology to thereby increase the adhesion strength of the seal to improve the reliability. Next, the description is given for an embodiment where the inventive orientation technology is applied to a liquid crystal light valve. Fig. 5 is a schematic diagram showing construction of the inventive liquid crystal light valve. The valve has a pair of substrates 501a and 501b each composed of a transparent glass plate having a thickness of 5mm and being polished at a parallel flatness of λ/5 (λ indicates He-Ne laser wavelength) so as to sandwich liquid crystal molecules. ITO electrodes 502a and 502b are provided on surfaces of the respective substrates. A photo-conductive layer 506 composed of hydrized amorphous silicon (a-Si H) is formed at a thickness of 5µm on the transparent electrode layer 502a of the optical writing side. A mirror layer composed of a dielectric multi-layered mirror 507 is formed on the photo-conductive layer. Alternatively, the mirror layer may have a structure having metal films isolated from one another. After forming orientation films 503a and 503b on the mirror layer 507 and the transparent electrode 502b, respectively, the pair of the substrates are joined by a spacer 504 to sandwich a liquid crystal layer 505 in a gap between the substrates. The orientation films 503a and 503b are formed in manner similar to the embodiment 2, hence detailed description is omitted. The used spacer 504 is composed of an adhesive containing silicon dioxide particles (commercial product ShinShiKyu SW, Shokubai Kasei Co., Ltd.) having a mean diameter of 5.0µm to determine the gap. The liquid crystal held in the gap is composed of ZLI-4788-100 produced by Merk. However, the liquid crystal material is not limited to the above, but may be selected from compositions having various electric, optic, and visco-elastic characteristics as long as the compositions have the negative dielectric anisotropy. The gap dimension is not limited to the above at all. The assembled cell is disposed in a projection optical system of crossed Nicols to undertake projection experiment. The device achieves very good resolution and high contrast over 3000 : 1 was measured. Further, the device can achieve the display of the very high quality free of discrimination lines which would be frequently observed in the general liquid crystal device of the homeotropic orientation type and which would degrade the contrast. The thus constructed liquid crystal light valve uses the orientation film layer composed of the pure inorganic material, which is free of damage when exposed to strong reading light in contrast to general organic orientation film, thereby improving optical resistance. Further, the device can be produced by steps simpler than the general homeotropic orientation technology to improve adhesion strength of the seal and to improve the reliability. The liquid crystal light valve of the present embodiment is applied to a liquid crystal projector featuring good reliability, durability and high luminance. The liquid crystal light valve is easily produced to thereby reduce the cost of the highly luminant liquid crystal projector. The present invention can introduce the slightly tilting homeotropic orientation into the liquid crystal layer through a single and simple step by the pure inorganic film. Accordingly, the optical resistance of the liquid crystal electro-optical device such as the liquid crystal light valve is significantly improved. This device is applied to the high luminance image projection apparatus, thereby featuring less frequent replacement of the valve and high reliability. The aforegoing description has been given by way of example only and it will be appreciated by a person skilled in the art that modifications can be made without departing from the scope of the present invention.

Claims: A method of preparing an orientation film for introducting slightly tilting homeotropic orientation into liquid crystal in a liquid crystal (305) sandwiched by a pair of substrates (301a, 301b) wherein the orientation film (303a, 303b) is formed on one of the substrates so as to be in contact with a layer of the liquid crystal, characterised in that the orientation film is formed by vacuum evaporating an inorganic material in a given direction tilted from a normal direction of the substrate, under condition where an incident angle ψ is set from 45° to 70° defined with reference to a direction parallel to the substrate and a thickness d of the orientation film is set to be in excess of 60nm up to and including 500nm measured by a film thickness gauge (105) disposed at an incident angle of 90° at the same distance from an evaporation source (102) as the substrate during the forming of the orientation film. A method of introducing slightly tilting homeotropic orientation into liquid crystal according to claim 1, further characterised in that the liquid crystal is a composition having a negative dielectric anistropy and a nematic phase at room temperature. A method of introducing slightly tilting homeotropic orientation into liquid crystal according to claim 1 or claim 2, further characterised in that the orientation film is formed of a silicon oxide including a silicon monoxide or a silicon dioxide, an oxide including a titanium oxide, a zirconium oxide or a tantalum oxide, a fluoride including a magnesium fluoride, or a sulfide including a zinc sulfide. A method of introducing slightly tilting homeotropic orientation into liquid crystal according to claim 1 or claim 2, further characterised in that the orientation film is formed of a raw material composed mainly of an element, a mixture or a compound containing an element of group IV of the periodic table. A liquid crystal electro-optical device composed of a liquid crystal (305) sandwiched by a pair of substrates (301a, 301b) and an orientation film (303a, 303b) disposed on one of the substrates so as to be in contact with a layer of the liquid crystal, characterised in that the orientation film is obtainable by the method as claim 1 and introduces a homeotropic orientation such that molecules of the liquid crystal have a slightly tilted director along the surface between the orientation film and the liquid crystal. A liquid crystal electro-optical device according to claim 5, further characterised in that the slightly tilted director of the liquid crystal molecules is substantially opposite or parallel between the pair of the substrates. A liquid crystal electro-optical device according to claim 5 or claim 6, further characterised in that the orientation film is composed of a silicon oxide including a silicon monoxide or a silicon dioxide, an oxide including a titanium oxide, a zirconium oxide or a tantalum oxide, a fluoride including a magnesium fluoride, or a sulfide including a zinc sulfide. A liquid crystal electro-optical device according to claim 5 or claim 6, further characterised in that the orientation film is formed of a raw material composed mainly of an element, a mixture or a compound containing an element of group IV of the periodic table. A liquid crystal electro-optical device according to any one of claims 5 to 8, further characterised in that a respective orientation film is provided on each substrate and the film thickness d thereof is different between the two orientation films. A liquid crystal light valve having optical writing means, optical reading means, voltage applying means, a glass substrate (501a) formed with a photo-conductive layer (506) and a mirror layer (507) over a transparent electrode (502a), another glass substrate (501b) formed with a transparent electrode (502b), the pair of glass substrates being opposed to each other, opposed surfaces of the pair of glass substrates being formed with respective liquid crystal orientation films (503a, 503b), and a liquid crystal composition (505) sealed therebetween to form a liquid crystal optical modulation layer, characterised in that each of the liquid crystal orientation films is obtainable by the method of claim 1 and thereby introduces a slightly tilting homeotropic orientation into the liquid crystal optical modulation layer. A liquid crystal light valve according to claim 10, further characterised in that the liquid crystal composition used to form the liquid crystal layer is a composition having a negative dielectric anisotropy and a nematic phase at a room temperature, and the slightly tilted direction is substantially set opposite or parallel between the substrates. A liquid crystal light valve according to claim 10 or claim 11, further characterised in that the orientation film is composed of a silicon oxide including a silicon monoxide or a silicon dioxide, an oxide including a titanium oxide, a zirconium oxide or a tantalum oxide, a fluoride including a magnesium fluoride, or a sulphide including a zinc sulphide. A liquid crystal light valve according to claim 10 or claim 11, further characterised in that the orientation film is formed of a raw material composed mainly of an element, a mixture or a compound containing an element of group IV of the periodic table. A liquid crystal light valve according to claim 10, characterised in that the film thickness d is different between the opposed orientation films.

Inventors: IWAKI TADAO, KATO NAOKI, SEKURA RIEKO, IWAKI, TADAO, KATO, NAOKI, SEKURA, RIEKO
Applicants: SEIKO INSTR INC, SEIKO INSTRUMENTS INC.
Application year: 1995
Main classification: G02F1
IPC codes: G02F1