Process for making a viscosity index improving copolymer

Abstract: There is provided a method for making a viscosity index improving copolymer which comprises polymerizing (meth)acrylate monomers and styrenic monomer(s) in an oil soluble diluent to form a solution of the copolymer in the oil soluble diluent, and wherein the solution includes less than or equal to 1000 parts by weight residual styrene monomer(s) per one million parts by weight solution.

Description: The present invention is concerned with viscosity index improving additives for lubricating oils and, more particularly, to a method for making a copolymer from alkyl (meth)acrylate monomers and vinyl aromatic monomer(s). Lubricating oil compositions for internal combustion engines typically include polymeric additives for improving the viscosity index of the lubricating composition, that is, modifying the relationship between temperature and the viscosity of the oil composition to reduce the temperature dependence of the viscosity and to lower the "pour point" of the composition, that is, to allow the composition to remain fluid at reduced temperature. Japanese Patent Publication JP-B-84020715 discloses an oil soluble copolymer obtained by reaction of 40 weight percent (wt%) to 75 wt% (meth) acrylate monomers composed of 0 parts by weight (pbw) to 80 pbw of a (meth)acrylate having a (C 8 -C 15 )alkyl group and 20 pbw to 100 pbw of a (meth)acrylate having a (C 16 -C 28 )alkyl group; and 25 wt% to 60 wt% of styrene or an alkyl styrene. While the properties of the copolymer disclosed in JP-B-84020715 are desirable, current environmental and health concerns dictate that the amount of residual styrenic monomer present in any commercial embodiment of the copolymer be reduced to a level below 1000 parts per million. Japanese Patent 84020715 is silent with respect to the amount of residual styrene monomer present in the copolymers disclosed in that patent. It is impractical to rely upon running the polymerization reaction to a sufficiently high monomer conversion so as to leave less than 1000 parts per million (ppm) nonreacted styrenic monomer in the copolymeric product, so that relatively costly processing steps as, e.g., stripping of the copolymeric product, may be required to remove residual styrenic monomer from the product copolymer. The present invention provides a method for making a viscosity index improving copolymer from monomers comprising (meth)acrylate monomers and styrenic monomer(s) that enables the above-noted difficulties to be overcome. According to the present invention there is provided a method for making a viscosity index improving polymer, which comprises: a). polymerizing a monomer mixture in an oil soluble diluent and in the presence of one or more polymerization initiator to form a polymerization intermediate, said monomer mixture comprising: from 5 parts by weight (pbw) to 70 pbw of one or more (meth)acrylate monomer having the structural formula (1): wherein: each R 1 is independently H or CH 3 ; and each R 2 is independently selected from (C 16 -C 24 )alkyl; from 5 pbw to 85 pbw of one or more (meth)acrylate monomer having the structural formula (2): wherein: each R 3 is independently H or CH 3 ; and each R 4 is independently selected from (C 7 -C 15 )alkyl; and from 5 pbw to 50 pbw of one or more styrenic monomer; and b). polymerizing from 2 pbw to 20 pbw, preferably from 2 pbw to 10 pbw, additional (meth)acrylate monomer(s) per 100 pbw of the combined (meth)acrylate monomers of formulae (1) and (2) of the monomer mixture, said additional (meth)acrylate monomer(s) comprising one or more (meth)acrylate monomer of formula (1), one or more (meth)acrylate monomer of formula (2), or a mixture thereof, in the presence of the polymerization intermediate, provided that the combined monomers of the monomer mixture and additional monomer(s) comprise from 5 wt% to 70 wt% of the (meth)acrylate monomer(s) of formula (1), from 5 wt% to 85 wt% of the (meth)acrylate monomer(s) of formula (2) and from 5 wt% to 50 wt% of the styrenic monomer(s), to provide a solution of from 30 weight percent to 90 weight percent of a viscosity index improving copolymer in the diluent, said solution including less than or equal to 1000 pbw residual styrene monomer(s) per 1,000,000 pbw solution. In one embodiment of the method of the invention the additional (meth)acrylate monomer(s) comprise(s) substantially the (meth)acrylate monomer(s) of formula (1), or comprise(s) substantially the (meth)acrylate monomer of formula (2). The limitation on the amount of residual styrenic monomer(s) in the product solution may, alternatively, be expressed on the basis of copolymer solids as less than or equal to 3,333 pbw residual styrene monomer(s) per 1,000,000 pbw copolymer solids. In a preferred embodiment, the method of the present invention provides a copolymer solution that includes less than or equal to 1,000 pbw, more preferably, less than or equal 500 pbw, residual styrene monomer(s) per 1,000,000 pbw copolymer solids. The terminology "(meth)acrylate" is used herein to generally refer to acrylate esters, methacrylate esters, and mixtures thereof. Commercially available alkyl (meth)acrylate monomers may be, and typically are, mixtures of esters. Such mixtures are typically referred to, and are referred to herein, using a contracted version of the names of the ester species predominating in the mixture, e.g., "lauryl-myristyl methacrylate", "cetyl-eicosyl methacrylate", "cetyl-stearyl methacrylate", "dodecylpentadecyl methacrylate". As used herein, (C 16 -C 24 )alkyl means any straight or branched alkyl group having 16 to 24 carbon atoms per group, e.g., stearyl, cetyl, heptadecyl, nonadecyl, eicosyl. Monomers having the structural formula (1) include, for example, stearyl acrylate, stearyl methacrylate, cetyl methacrylate, heptadecyl acrylate, heptadecyl methacrylate, nonadecyl methacrylate, eicosyl methacrylate and mixtures thereof, e.g., cetyl-stearyl methacrylate, cetyl-eicosyl methacrylate. In one embodiment of the present invention the monomer(s) of formula (1) is/are selected from the group consisting of stearyl methacrylate, cetyl methacrylate, heptadecyl methacrylate, nonadecyl methacrylate, eicosyl methacrylate, and mixtures of two or more of such monomers. As used herein, (C 7 -C 15 )alkyl means any straight or branched alkyl group having 7 to 15 carbon atoms per group, e.g., heptyl, octyl, nonyl, n-decyl, isodecyl undecyl, lauryl, tridecyl and myristyl. Monomers having the structural formula (2) include, for example, octyl acrylate octyl methacrylate, nonyl methacrylate, decyl acrylate, decyl methacrylate, isodecyl methacrylate, undecyl methacrylate, lauryl methacrylate, tridecyl methacrylate, myristyl methacrylate, pentadecyl methacrylate and mixtures thereof, e.g., lauryl-myristyl methacrylate. In one embodiment of the present inventin the monomer(s) of formula (2) is/are selected from the group consisting of heptyl methacrylate, octyl methacrylate, nonyl methacrylate, n-decyl methacrylate, isodecyl methacrylate, undecyl methacrylate, lauryl methacrylate, tridecyl methacrylate, myristyl methacrylate, pentadecyl methacrylate, and mixtures of two or more of such monomers. The term "styrenic monomer" means those polymerizable vinyl aromatic compounds having a single aromatic ring per molecule, and mixtures thereof, and includes, for example, styrene, alkyl-substituted styrenes such as α-methyl styrene, α-ethyl styrene, p-methyl styrene and vinyl xylene, halogenated styrenes such as chlorostyrene, bromostyrene and dichlorostyrene, and other vinyl aromatic compounds having a single aromatic ring per molecule and having one or more nonreactive substituents on the aromatic ring. In one embodiment of the present invention the styrenic monomer(s) is/are selected from the group consisting of styrene, alkyl-substituted styrenes and halogenated styrenes. In a preferred embodiment, the styrenic monomer is styrene. The copolymer of the present invention is made, e.g., by free radical polymerization of selected relative amounts of the above-disclosed monomers in an oil soluble hydrocarbon diluent in the presence of an effective amount of a polymerization initiator. In a preferred embodiment, the total monomer charge includes from about 20 wt% to about 50 wt%, more preferably about 25 wt% to about 35 wt%, (meth)acrylate monomer(s) of the structural formula (1), from about 20 wt% to about 50 wt%, more preferably about 25 wt% to about 40 wt%, (meth)acrylate monomer(s)of the structural formula (2), and from about 20 wt% to about 40 wt%, more preferably about 25 wt% to about 35 wt%, of the styrenic monomer(s). The diluent may be any inert oil soluble organic liquid and is preferably a hydrocarbon lubricating oil which is miscible with or identical to the lubricating oil base oil in which the additive is to be subsequently employed. In a preferred embodiment, the oil soluble diluent is a paraffinic or naphthenic neutral oil. In a preferred embodiment, the reaction mixture includes from about 15 to about 400 pbw diluent per 100 pbw total monomer charge and, more preferably, from about 50 to about 200 pbw diluent per 100 pbw total monomer charge. As used herein, the terminology "total monomer charge" means all monomers charged to the reaction vessel during the process of the present invention, i.e., the combined monomers of the monomer mixture and the additional (meth)acrylate monomer(s). Suitable polymerization initiators include those initiators which dissociate upon relatively mild heating, e.g., at temperatures in the range of 70°C to 140°C, to yield a free radical. The specific reaction temperature to be used in the polymerization reaction is selected in a known way, based on the composition of the initiator used in the reaction. Suitable initiators are known in the art and include, e.g., peroxides, hydroperoxides and related initiators such as benzoyl peroxide, tert-butyl hydroperoxide, cumene peroxide, acetyl peroxide, caproyl peroxide, tert -butyl perbenzoate, tert-butyl diperphthalate, methyl ethyl ketone peroxide, azo initiators such as, e.g., azo diisobutyronitrile, azo diisobutyramide, azobis(a, a-dimethylvaleronitrile), azobis(a-methylbutyronitrile) and dimethyl, diethyl or dibutyl azobis(methylvalerate), and mixtures thereof. The peroxide initiators are preferably used at a level of from about 0.01% to 3% by weight, based on the total monomer charge, and the azo initiators are preferably used at a level from about 0.01% to about 2% by weight, based on the total monomer charge. In a preferred embodiment, the reaction mixture includes from about 0.05 pbw to about 2.0 pbw polymerization initiator(s) per 100 pbw total monomers and, more preferably, from about 0.1 pbw to about 1.0 pbw polymerization initiator(s) per 100 pbw total monomer charge. The reaction mixture may, optionally, include a chain transfer agent. Suitable chain transfer agents include those conventional in the art, e.g., dodecyl mercaptan, ethyl mercaptan. Dodecyl mercaptan is preferred as the chain transfer agent. The selection of the amount of chain transfer agent to be used is based on the desired molecular weight of the polymer being synthesized in a manner conventional in the art. In a preferred embodiment, the reaction mixture includes from about 0.01 pbw to about 0.6 pbw chain transfer agent per 100 pbw total monomer charge, and more preferably includes from about 0.01 pbw to about 0.3 pbw chain transfer agent per 100 pbw total monomer charge. The method of the present invention may be carried out as follows:- (i). The diluent, an effective amount of first polymerization initiator(s), the styrenic monomer(s) and a first portion of the (meth)acrylate monomers are charged to a reaction vessel and heated with stirring, preferably under an inert, e.g., nitrogen, blanket to a temperature within a first reaction temperature range. A first reaction temperature range is selected based on the composition of the first initiator(s). The batch is then maintained at a temperature within the first reaction temperature range, with stirring, for a time period effective to allow copolymerization of the monomers in the reaction mixture, e.g., for about 2 hours to about 12 hours. In a preferred embodiment, a portion, e.g., from about 25% to about 60%, of the styrenic monomer(s) and the first portion of the (meth)acrylate monomers is initially charged to the reaction vessel and heated in the diluent in the presence of the polymerization initiator(s) to a temperature within the first reaction temperature range. The remaining portion of the styrenic monomer(s) and the first portion of the (meth)acrylate monomers is then fed into the reaction vessel with stirring and while maintaining the batch at a temperature within the first reaction temperature range over a time period of about 30 minutes to about 180 minutes. Following completion of the monomer addition, the batch is maintained at a temperature within the first reaction temperature range for a holding period of up to about 4 hours. (ii). A second portion of (meth)acrylate monomer(s) and a second amount of initiator(s) is then charged to the reactor. In a preferred embodiment, the second portion of (meth)acrylate monomer(s) comprises about 2 pbw to about 20 pbw (meth)acrylate monomer(s) per 100 pbw of the first portion of the (meth)acrylate monomers. More preferably, the second portion of (meth)acrylate monomer(s) comprises about 5 pbw to about 10 pbw (meth)acrylate monomer(s) per 100 pbw of the first portion of the (meth)acrylate monomer(s). In a highly preferred embodiment, the second portion of the (meth)acrylate monomer(s) comprises substantially either the (meth)acrylate monomer(s) of formula (1), i.e., the (C 16 -C 24 )alkyl (meth)acrylate monomer(s), or the (meth)acrylate monomer(s) of formula (2), i.e., the (C 7 -C 15 )alkyl (meth)acrylate monomer(s). In a very highly preferred embodiment, the second portion of the (meth)acrylate monomer(s) comprises substantially the (meth)acrylate monomer(s) of formula (2), i.e., the (C 7 -C 15 )alkyl (meth)acrylate monomer(s). The composition of the second amount of initiator(s) may differ from the initiator(s) present in the initial reaction mixture. A second reaction temperature range is selected based on the composition of the second amount of initiator(s). Following completion of the addition of the second portion of (meth)acrylate monomer(s) and second portion of initiator(s), the batch is maintained at a temperature within the second reaction temperature range for a second holding period of up to about 4 hours. In a preferred embodiment, a third portion of initiator(s), e.g. in an amount of about 0.05 pbw to about 1.0 pbw polymerization initiator per 100 pbw total monomer charge, is added to the reaction mixture subsequent to the second holding period. A third reaction temperature range is selected based on the composition of the third amount of initiator. The reaction mixture is held within the third reaction temperature range for a time period of about 30 minutes to about 180 minutes subsequent to the addition of the third portion of polymerization initiator(s) to complete the polymerization reaction. A viscous solution of the copolymer in the diluent, wherein the copolymer has substantially the same relative composition as the above described total monomer charge and the solution includes less than 1000 ppm, preferably less than 500 ppm, and most preferably less than 300 ppm, residual styrenic monomer(s) is obtained as the product of the polymerization process of the present invention. The polymer solids content of the solution may, optionally, be further adjusted, i.e., by further dilution, on the basis of the viscosity of the copolymer to provide a tractable fluid. In a preferred embodiment of the present invention, the copolymer exhibits a weight average molecular weight, determined, e.g., by gel permeation chromatography, from about 20,000 to about 500,000, more preferably from about 150,000 to about 400,000. In a preferred embodiment of the present invention, the copolymer exhibits a polydispersity factor, i.e., the ratio of the number average molecular weight of the copolymer to weight average molecular weight of the copolymer, of about 1.5 to about 10, more preferably from about 1.5 to about 5. Optionally, the copolymer may be synthesized, using the method of the present invention, at a molecular weight that is higher than desired for the intended end use and then be mechanically or thermally degraded to adjust the molecular weight of the copolymer into the desired range, in a manner known in the art. The polymer solution formed in the method of the present invention is useful as an additive composition for improving the viscosity of a lubricating oil and includes from about 30 weight percent to about 90 weight percent, more preferably from about 40 weight percent to about 80 weight percent, polymer solids dissolved in an oil soluble diluent. The copolymer, made by the method of the present invention, may be added, typically in the form of the above-disclosed additive composition, to a lubricating oil base stock, e.g., a paraffinic solvent neutral oil, to provide a lubricating oil composition having the desired viscometric properties. Suitable lubricating oil base stocks include paraffinic and naphthenic neutral oils. The present invention also provides an additive for improving the viscosity index of a lubricating oil, which comprises from 30 weight percent to 90 weight percent of the copolymer, and from 10 weight percent to 70 weight percent of an oil soluble diluent. The present invention also provides a lubricating oil composition, which comprises from 2 pbw to 20 pbw, more preferably from about 5 pbw to about 15 pbw, of the copolymer (on the basis of polymer solids) per 100 pbw lubricating oil base stock. The following Examples are presented to illustrate various embodiments of the present invention. Example 1 A copolymer was made by the process of the present invention. A styrenic monomer (styrene (165 g)) and a polymerization initiator (74 % benzoyl peroxide (0.95 g)) were mixed in a closed vessel at room temperature to form a homogeneous solution of the initiator in the styrenic monomer. A first alkyl methacrylate monomer (isodecyl methacrylate (112.5 g)), a second alkyl methacrylate monomer (stearyl methacrylate (192.5 g)), a polymerization initiator (t-butyl perbenzoate (0.10 g)) and a chain transfer agent (n-dodecyl mercaptan (0.39 g)) were then added to the solution and stirred for 10 minutes to form a "monomer mixture". A 1 liter reaction vessel was fitted with a thermometer, a temperature controller, a purge gas inlet, a water-cooled reflux condenser with purge gas outlet, a stirrer, and an addition funnel. A portion of the monomer mixture (120 g) and a diluent (a grade 90, solvent neutral mineral oil having a bromine index less than 12 (50 g)) were charged to the reaction vessel. The contents of the reaction vessel were then heated to 120 °C over a time period of 30 minutes with stirring and with a nitrogen sparge of 50 cubic cm per minute. When the reactor contents reached 120 °C, the remaining monomer mixture was fed to the kettle at a substantially constant rate over a time period of about 2.5 hours. At the end of the monomer feed, the reactive mixture was maintained at 120 °C for a time period of 30 minutes and then an additional amount of polymerization initiator (t-butyl peroctoate (0.75 g)) and an additional amount of diluent (a grade 90, solvent neutral mineral oil having a bromine index less than 20 ( 58 g)) were quickly added to the reaction vessel. The contents of the reaction vessel were then maintained at 120 °C for a first holding time period of 30 minutes. Following the first holding time period, an additional amount of the first alkyl methacrylate monomer (isodecyl methacrylate (25 g)) and an additional amount of polymerization initiator (t-butyl peroctoate (0.75 g)) were charged to the reaction vessel. The contents of the reaction vessel were then maintained at 120°C for a second holding time period of 30 minutes. Following the 30 minute second holding time period, an additional amount of polymerization initiator (t-butyl peroctoate (0.75 g)) and an additional amount of diluent (a grade 90, solvent neutral mineral oil having a bromine index less than 20 ( 58 g)) were charged to the reaction vessel. The contents of the reaction vessel were then heated from 120°C to 130°C over a time period of 30 minutes, then maintained at 130°C for a time period of 30 minutes and finally allowed to cool to ambient temperature. The above described process produced a viscous solution of a copolymer in the diluent. The solution was further diluted with additional diluent (a grade 90, solvent neutral mineral oil having a bromine index less than 20 (324 g)). The copolymer solution of Example 1 exhibited a polymer solids content of 73 wt% and a viscosity of 22,239 mm 2 /s (22,239 centiStokes (cSt)) at 100°C measured according to ASTM D445-88. Conversion of monomer to copolymer was calculated to be 98%. The product solution included 170 pbw nonreacted styrene monomer per one million pbw solution (227 pbw nonreacted styrene monomer per one million pbw copolymer), as determined by headspace gas chromatography. Example 2 A further copolymer solution was made by the method of Example 1, using the same relative amounts of the respective monomers. The copolymer solution of Example 2 exhibited a polymer solids content of 74 wt% and a viscosity of 25,300 mm 2 /s (cSt) at 100°C measured according to ASTM D445-88. Conversion of monomer to copolymer was calculated to be 99%. The product solution included 80 pbw nonreacted styrene monomer per one million pbw solution (160 pbw nonreacted styrene monomer per one million pbw copolymer), as determined by headspace gas chromatography. The copolymer of the solution of Example 2 exhibited a weight average molecular weight of 240,000, measured by gel permeation chromatography using a polystyrene calibration standard, and a polydispersity of 4.5. Example 3 The concentrated copolymer solution of Example 2 was diluted with 150 neutral oil (viscosity index of 92, pour point of -9°C) to provide the lubricating oil composition of Example 3. The lubricating oil composition of Example 3 included 8.7 wt% copolymer solids and exhibited a kinematic viscosity of 13.94 mm 2 /s (cSt) at 100°C, measured according to ASTM D445-88. The lubricating oil composition exhibited a kinematic viscosity of 85.67 mm 2 /s (cSt) at 40°C, measured according to ASTM D445-88, and a viscosity index of 168. The lubricating oil composition exhibited a sonic shear index (SSI) of 28 and viscosity loss of 17.4 %, determined according to Comite Europeen de Coordination (CEC) L 14 A 88 (30 cycles). The lubricating oil composition exhibited a pour point of -39°C, measured according to ASTM D97-87. The process of the present invention provides viscosity index improving and pour point lowering copolymeric additive for lubricating oils that is derived from alkyl (meth)acrylate monomers and styrenic monomer(s) and that includes less than or equal to about 1000 ppm residual styrenic monomer(s). The process of the present invention provides an oil additive solution that includes a copolymer having repeating units derived from styrenic monomer(s) but that exhibits a very low residual styrenic monomer(s) content and avoids such costly process steps as, e.g., stripping of the copolymeric product to remove unreacted styrenic monomer(s).

Claims: A method for making a viscosity index improving polymer, which comprises: a). polymerizing a monomer mixture in an oil soluble diluent and in the presence of one or more polymerization initiator to form a polymerization intermediate, said monomer mixture comprising: from 5 parts by weight to 70 parts by weight of one or more (meth)acrylate monomer having the structural formula: wherein: each R 1 is independently H or CH 3 ; and each R 2 is independently selected from (C 16 -C 24 )alkyl; from 5 parts by weight to 85 parts by weight of one or more (meth)acrylate monomer having the structural formula: wherein: each R 3 is independently H or CH 3 ; and each R 4 is independently selected from (C 7 -C 15 )alkyl; and from 5 parts by weight to 50 parts by weight of one or more styrenic monomer; and b). polymerizing from 2 parts by weight to 20 parts by weight additional (meth)acrylate monomer(s) per 100 parts by weight of the combined (meth)acrylate monomers of formulae (1) and (2) of the monomer mixture, said additional (meth)acrylate monomer(s) comprising one or more (meth)acrylate monomer of formula (1), one or more (meth)acrylate monomer of formula (2), or a mixture thereof, in the presence of the polymerization intermediate, provided that the combined monomers of the monomer mixture and the additional monomer(s) comprise from 5 weight percent to 70 weight percent of the (meth)acrylate monomer(s) of formula (1), from 5 weight percent to 85 weight percent of the (meth)acrylate monomer(s) of formula (2), and from 5 weight percent to 50 weight percent of the styrenic monomer(s), to provide a solution of from 30 weight percent to 90 weight percent of a viscosity index improving copolymer in the diluent, said solution including less than or equal to 1000 parts by weight residual styrene monomer(s) per one million parts by weight solution. A method as claimed in claim 1, wherein the additional (meth)acrylate monomer(s) comprise(s) substantially the (meth)acrylate monomer(s) of formula (1), or comprise(s) substantially the (meth)acrylate monomer of formula (2). A method as claimed in claim 1 or claim 2, wherein the (meth)acrylate monomer(s) of formula (1) is/are selected from the group consisting of stearyl methacrylate, cetyl methacrylate, heptadecyl methacrylate, nonadecyl methacrylate, eicosyl methacrylate, and mixtures of two or more of such monomers. A method as claimed in any preceding claim, wherein the (meth)acrylate monomer(s) of formula (2) is/are selected from the group consisting of heptyl methacrylate, octyl methacrylate, nonyl methacrylate, n-decyl methacrylate, isodecyl methacrylate, undecyl methacrylate, lauryl methacrylate, tridecyl methacrylate, myristyl methacrylate, pentadecyl methacrylate, and mixtures of two or more of such monomers. A method as claimed in any preceding claim, wherein the styrenic monomer(s) is/are selected from the group consisting of styrene, alkyl-substituted styrenes and halogenated styrenes. A method as claimed in any preceding claim, comprising polymerizing from 2 parts by weight to 10 parts by weight additional (meth)acrylate monomer(s) per 100 parts by weight of the combined (meth)acrylate monomers of formulae (1) and (2) of the monomer mixture. An additive for improving the viscosity index of a lubricating oil, which comprises from 30 weight percent to 90 weight percent of a viscosity index improving polymer prepared by a method as claimed in any preceding claim, and from 10 weight percent to 70 weight percent of an oil soluble diluent. A lubricating oil composition, which comprises from 2 parts by weight to 20 parts by weight of a viscosity index improving polymer, prepared by a method as claimed in any of claims 1 to 6, per 100 parts by weight of lubricating oil base stock.

Inventors: SCHAUBER CLAUDE CHARLES, SCHAUBER, CLAUDE CHARLES
Applicants: ROHM & HAAS, ROHM AND HAAS COMPANY
Application year: 1995
Main classification: C08F220
IPC codes: C10M143, C10M145, C10M147, C08F220, C08F212, C08F2, C10N70, C10N30, C10N40