An easy-cleavage film and a method of producing the same

Abstract: An easy-cleavage film comprising a first layer, a second layer and a third layer which contain Nylon 6 (Ny 6), meta-xylylene adipamide (MXD 6) and polyamide elastomer (PAE), in which the film is defined as (1) a content of the components of each layer, (2) a layer ratio of each layer and (3) an orientation ratio, more specifically, (1) the first layer and the third layer being 60 to 85 % by weight of the Ny 6 content, 15 to 40 % by weight of the MXD 6 content and 0.1 to 10.0 % by weight of the PAE content, the second layer being 0 to 40 % by weight of the Ny 6 content, 60 to 100 % by weight of the MXD 6 content and 0.1 to 10.0 % by weight of the PAE content (but, each layer being Ny 6 + MXD 6 + PAE = 100 % by weight, further, the MXD 6 content in the second layer being larger than the MXD 6 content the first layer and the third layer), (2) the layer ratio of the first layer to the third layer being defined as 1:8:1 - 4:2:4, the layer ratio between the first layer (or the third layer) and the second layer being defined as 1:8 - 2:1, and the layer ratio between the first layer and the third layer being defined as 1:2 - 2:1, and (3) the orientation ratio of more than 2.8 times in both the direction of the movement of the film (a MD direction) and the direction of the width of the film (a TD direction).

Description: This invention relates to an easy-cleavage film and a method of producing the same, in which the produced easy- cleavage film can be used for, for example, the packing of foods, industrial materials, medicine, and so on. Conventionally, as a film having gas-barrier performance, a biaxial oriented nylon film coated with, for example, a vinylidene chloride resin is used. But, it is disadvantageous that the biaxial oriented nylon film produces a chloric gas when being burned damaging an incinerator or polluting the environment. Consequently, as the film having gas-barrier performance for which environmental consideration is unnecessary, namely, it is environmentally safe, an ethylene-vinyl-acetate copolymer saponification film (EVOH) is used in many cases. The EVOH film has good properties, but has an inferior point that its properties easily deteriorate under high temperature and high humidity, however to attain a high level of gas-barrier performance humidity is required. Furthermore, the EVOH film is accompanied with a limitation of uses by reason of produced disadvantages, such as the EVOH film changes color to misted white when undergoing a hot-water treatment (such as a retort treatment) when exceeding 100 °C. It is proposed that a multi-oriented film, such as Ny/EVOH/Ny and Ny/MXD 6/Ny, is prepared by using nylon (Ny) or meta-xylylene adipamide (MXD 6), resulting in a film which improves upon the aforementioned inferior points. However, these films have the utilitarian disadvantage that they are difficult to open by hand because of the deficiency of the easy-cleavage. Further, EVOH or MXD 6 both have high strength, so that there is a disadvantage that a pinhole is easily produced. As to the aforementioned easy-cleavage, lately, a multi-film laminated with a linear chain low-density polyethylene (L-LDPE) sealant has been increasingly used in order to facilitate protection of a substance enclosed in the film resulting in a product, however, an inferior opening performance is inversely proportional to the improved strength of the film, therefore, a compatible film with the easy-cleavage and strength is required. JP-A-6099493 and JP-A-6099492 disclose a film with easy tearing properties. The film is composed of first, second, and third layers containing nylon-6 (Ny-6) and meta-xylylene adipamide (MXD6). The Ny-6 contents of the first and the third layer are 60-95 parts by weight, and the MXD6 contents are 5-40 parts by weight. The Ny-6 content of the second layer is 40-85 parts by weight, and the MXD6 content is 15-60 parts by weight. For all of the layers, the total amount of NY-6 and MXD6 is 100 parts by weight. The MXD6 content of the second layer is higher than that of the first and the third layer. The layer thickness ratio of the first to the second to the third layer is 1:8:1-4:2:4. The layer thickness ratio of the first to the second layer is 1:8-2:1. The layer thickness ratio of the first to the third layer is 1:2-2:1. The film with easy tearing properties has a draw ratio in the MD (film movement), the TD (film width) direction of at least 2.8 times. The film is used for bags for food, chemicals, and industrial products. The film has easy tearing and linear cutting properties, and high impact resistance. In the production, the first, the second, and the third layers are melt extruded at the above layer thickness ratios and cooled. The resultant raw film is drawn at a draw ratio of at least 2.8 times in the MD direction and the TD direction. An easy-cleavage film of the first aspect of the present invention is characterized by having a first layer, a second layer and a third layer which contain Nylon 6 (Ny 6), meta-xylylene adipamide (MXD 6) and polyamide elastomer (PAE), in which the film is defined as (1) a content of the aforementioned component of each layer, (2) a layer ratio of each layer and (3) an orientation ratio as the following. (1) The first layer and the third layer are 60 to 85 % by weight of the Ny 6 content, 15 to 40 % by weight of the MXD 6 content and 0.1 to 10.0 % by weight of the PAE content, the second layer is 0 to 40 % by weight of the Ny 6 content, 60 to 100 % by weight of the MXD 6 content and 0.1 to 10.0 % by weight of the PAE content but, each layer is Ny 6 + MXD 6 + PAE = 100 % by weight, further, the MXD 6 content in the second layer is larger than the MXD 6 content in the first layer and the third layer. The aforementioned PAE is of a copolymer which is composed of a soft-segment required as the role of elastomeric properties and a hard-segment. As the soft-segment, polytetra methylene ether glycol, polypropylene-glycol or aliphatic polyesterdiol is used. While, as the hard-segment, Nylon 12, Nylon 6 or aromatic polyamide is used.When the MXD 6 content in each layer is below the aforementioned range, it is difficult to cut by hand for reason of having inferior easy-cleavage and linear cut performance. On the other hand, when the MXD 6 content is above the aforementioned range, an impact strength sharply decreases so as to greatly decrease the utility.When the PAE content in each layer is below the aforementioned range, improvement of a pinhole performance is insufficient. However, when the PAE content is above the aforementioned range, an optical character of the film is decreased so as to lower the value of the product.It is advisable for the first layer and the third layer to be 60 to 75 % by weight of the Ny 6 content and 25 to 40 % by weight of the MXD 6 content. Further, it is desirable for each layer to be 0.5 to 8% by weight of the PAE content. (2) The layer ratio of the first layer to the second layer to the third layer is defined as 1:8:1 - 4:2:4, the layer ratio between the first layer or the third layer and the second layer is defined as 1:8 - 2:1, and the layer ratio between the first layer and the third layer is defined as 1:2 - 2:1. Incidentally, it is advisable that the layer ratio of the first layer to the second layer to the third layer is defined as 1:2:1 - 2:1:2, the layer ratio between the first layer or the third layer and the second layer is defined as 1:2 - 2:1, and the layer ratio between the first layer and the third layer is defined as 1:1.5 - 1.5:1. (3) The film is oriented at a ratio of more than 2.8 times in both the direction of the movement of the film (a MD direction) and the direction of the width of the film (a TD direction). When the orientation ratio is smaller than 2.8 times, a disadvantage in utility is produced by having inferior linear cut performance and decreased impact strength. Incidentally, it is desirable that the orientation ratio is more than 3.0 times. The aforementioned easy-cleavage film can suitably contain therein necessary additives. It is possible to list an anti-blocking pill (such as inorganic filler), water repeller (such as ethylene-bis-stearate ester agent), lubricant (such as calcium stearate) and so on as the aforementioned additive. The second aspect of the present invention is a method of producing the easy-cleavage film having the first layer, the second layer and the third layer which contain Nylon 6 (Ny 6), meta-xylylene adipamide (MXD 6) and polyamide elastomer (PAE), which is characterized by defining the following: (1) a blended amount of the aforementioned raw materials for each layer, (2) the layer ratio of each layer and (3) the condition of the orientation. (1) The first layer and the third layer are a blend of 60 to 85 % by weight of Ny 6, 15 to 40 % by weight of MXD 6 and 0.1 to 10.0 % by weight of PAE, the second layer is a blend of 0 to 40 % by weight of Ny 6, 60 to 100 % by weight of MXD 6 and 0.1 to 10.0 % by weight of PAE but, the blended amount of each layer is Ny 6 + MXD 6 + PAE = 100 % by weight, further, the blended amount of MXD in the second layer is larger than the blended amount of MXD 6 in the first layer and the third layer. (2) The layer ratio of the first layer to the second layer to the third layer is defined as 1:8:1 - 4:2:4, the layer ratio between the first layer or the third layer and the second layer is defined as 1:8 - 2:1, and the layer ratio between the first layer and the third layer is defined as 1:2 - 2:1. (3) The aforementioned raw materials for forming the first layer up to the third layer are melted and kneaded, further, laminated after extruding in a film state, and then the cooled original film is oriented at an orientation ratio which is more than 2.8 times in both the direction of the movement of the film (a MD direction) and in the direction of the width of the film (a TD direction). The aforementioned orientation is facilitated by using a simultaneous biaxial orientation, such as a tubular method. In the accompanying drawings : Fig. 1 is a sectional view of an easy-cleavage film according to a preferred embodiment of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT(S) EMBODIMENT 1 After mixing materials for making a first layer, a second layer and a third layer are respectively melted and kneaded in three extruders (40 mm in diameter) at 270°C, the melted substances are extruded from a multi-circular-die having a 90 mm diameter as a tubular three-layer film (ratio of layer, 1:1:1), and then an original film is made to be immediately cooled by water. The raw materials used for the aforementioned first layer is a blend of nylon 6 (Ny 6), meta-xylylene adipamide (MXD 6) and polyamide elastomer (PAE), respectively, at the ratio of 67 % by weight, 30 %, by weight and 3 to by weight. The raw materials used for the aforementioned second layer is a blend of Ny 6, MXD 6 and PAE, respectively, at the ratio of 0 % by weight, 97 % by weight and 3 % by weight. The raw materials used for the aforementioned third layer is a blend of Ny 6, MXD 6 and PAE, respectively, at the ratio of 67 % by weight, 30 % by weight and 3 % by weight. Nylon produced by UBE INDUSTRIES LIMITED (the tradename:UBE UBE NYLON 1023 FD, a relative viscosity η r = 3.6) is used as the aforementioned Ny 6, and meat-xylene adipamide produced by MISTUBISHI GAS CHEMICAL COMPANY INC. (the tradename: MX-NYLON 6007, a relative viscosity η r = 2.7) is used as the aforementioned MXD 6. Further, as the aforementioned PAE, polyamide elastomer produced by DAICEL-HULS CO., LTD. (the tradename: DI-AMIDE-PAE, X 40 (grade)) is used. The DI-AMIDE-PAE is a polyamide elastomer of a block-copolymer having a soft-segment, such as a polyether component, and a hard-segment, such as Nylon 12. After the original film is drawn into a pair of nip-rollers, it is heated by a heater while gas is fed by compression force into the inside, expanding the original film into a bubble by air blowing therein from an airing at a starting point of orientation, and then a simultaneous biaxial orientation to the MD direction and the TD direction by means of a tubular method by being pulled down with a pair of the nip-roller placed at the downstream side is carried out. The orientation ratio of both the MD direction and the TD direction is 3.0. Further, the oriented film is put into a heat treating furnace of a tenter type which is fixed at a temperature of 210 °C, whereby an easy-cleavage film according to the present invention is obtained. As is shown in Fig. 1, an easy-cleavage film 11 has a three-layer laminated structure, a first layer 12, a second layer 13 and a third layer 14. The obtained easy-cleavage film is measured by a tear strength and an impact strength (film-impact) and evaluated for easy-cleavage, linear cut performance, pinhole resistance, gas-barrier performance and optical character. The results are shown in Table 2. The measurement of the tear strength is facilitated by measuring Elmendorf spilt strength (kg/cm) following JIS-Z1702 in the direction of the orientation of the film. The aforementioned impact strength is measured by using a film-impact tester (produced by TOYO SEIKI CO. LTD.), in which the film is measured by the impact strength needed to puncture the film when a semi-tubular pendulum (a diameter; 1.27 cm (1/2 inch), weight; 30 kg) is struck on the fixed ring-likely film. The measured value I of the impact strength is defined as ○ for I ≧ 5,000 kg · cm/cm and as × for I < 5,000 kg · cm/cm. In I < 5,000 kg · cm/cm, the efficiency as a base material for the surface is lowered, therefore, utility as a base material for packaging liquid becomes inferior. The aforementioned easy-cleavage is evaluated as the value E of the aforementioned Elemendorf spilt strength and defined as ○ for E ≦ 7 kg/cm, Δ for 7 kg/cm < E < 9 kg/cm and × for E ≧ 9 kg/cm. When E is more than 9 kg/cm, the easy-cleavage is conspicuously decreased, more particularly, the linear cut performance is immediately inferior. The aforementioned linear cut performance is evaluated in the following way. More specifically, after the film is torn along a rift which is made for a predetermined distance W s , for example, for a distance of 2 cm, on the film with a width of 20 cm, a width W e of the other end of the film piece is measured, and then deviation α with the original distance W s is calculated as follows. α = [(W s - W e )/W s ] × 100 The aforementioned measurement is conducted on 10 sheets of the film, in which the average deviation α(%) evaluated as less than ± 10 % is indicated with o ○ (the linear cut performance is excellent), as ±10 % ≦ α ≦ ±30 % is indicated with ○ (the linear cut performance is good), and as more than ±30 % is indicated with × (the linear cut performance is insufficient). Further, more than 80 % of the examined films are ±10 % ≦ α ≦ ±30 %, and almost 20 % are ±30 % ≦ α ≦ ±40 %, which are evaluated as Δ (the linear cut performance is slightly unstable). When α(%) exceeds 30 %, it becomes difficult to cut the film on the straight. The aforementioned pinhole resistance is evaluated with a bending resistance by using a Gerbo-tester of a MIL standard. The laminated film of the easy-cleavage film of the embodiment and a linear chain low-density polyethylene (L-LDPE, 50 µm) is used as a sample, in which after the laminated film is bent at 23 °C, 50 %RH, the number of produced through-holes are measured by using a liquid for detecting the pinholes. The measured evaluation is indicated with ○ for less than five through-holes, Δ for 6 to 19 and × for more than 20. Evaluation of the optical character is measured by following ASTM D-1003 and indicated with ○ for the cases of less than 7 % and with × for the cases of more than 7 %. Evaluation of the gas-barrier performance is measured by the degree oxygen-gas transferred in less than 60 %RH by using a gas-transmission tester produced by MOCON CO., LTD., in which ○ shows the cases of less than 15 cc/m 2 , 24Hr, and × shows the cases of more than 15 cc/m 2 , 24Hr. The total evaluation is defined as ○ for the film absent of the evaluation × as to the tear strength, the impact strength, the easy-cleavage, the linear cut performance, the pinhole resistance, the gas-barrier performance and the optical character, and as × for the film which has at least one of these evaluations ×. EMBODIMENTS 2 TO 14 The easy-cleavage film relating to each embodiment is obtained like Embodiment 1. But, the percentage of the blend of the materials, the ratio of the layers and the orientation ratio are differed from each embodiment as shown in Table 1. Incidentally, PAE used in Embodiments 2 to 13 is the DI-AMIDE-PAE(the tradename), X 40 (grade), and PAE used in Embodiment 14 is the DI-AMIDE-PAE (the tradename), X 4442 (grade). The easy-cleavage films of these embodiments are, like Embodiment 1, measured by the tear strength and the impact strength and evaluated for easy-cleavage, linear cut performance and so on. These results are illustrated in Table 2. COMPARATIVE EXAMPLES 1 TO 7 A film relating to each comparative example is obtained like Embodiment 1. But, the component of the layers, a percentage of the blend of the materials and the orientation ratio are differed from each comparative example as shown in Table 3. The easy-cleavage films of these comparative examples are, like Embodiment 1, measured by the tear strength and the impact strength and evaluated for easy-cleavage, linear cut performance and so on. These results are illustrated in Table 4. Raw Material Composition (% by weight) Layer Ratio Orientation Ratio 1 ○ 2 ○ 3 ○ PAE Ny MX Ny Mx Ny MX 1 ○ 2 ○ 3 ○ MD TD E m b o d i m e n t s 1 67 30 0 97 67 30 3 1 1 1 3.0 3.0 2 67 30 0 97 67 30 3 2 1 2 3.0 3.0 3 69 30 0 99 69 30 1 2 1 2 3.0 3.0 4 60 30 0 90 60 30 10 2 1 2 3.0 3.0 5 67 30 17 80 67 30 3 1 1 1 3.0 3.0 6 67 30 37 60 67 30 3 1 1 1 3.0 3.0 7 67 30 37 60 67 30 3 1 1 1 3.0 3.0 8 77 20 17 80 77 20 3 1 1 1 3.0 3.0 9 82 15 37 60 82 15 3 1 1 1 3.0 3.0 10 67 30 37 60 67 30 3 1 2 1 3.0 3.0 11 67 30 37 60 67 30 3 1 1 1 2.8 2.8 12 69.9 30 0 99.9 69.9 30 0.1 1 1 1 3.0 3.0 13 69.5 30 0 99.5 69.5 30 0.5 1 1 1 3.0 3.0 14 69.5 30 0 99.5 69.5 30 0.5 1 1 1 3.0 3.0 Tear Strenght (kg/cm) Easy-Cleavage Linear Cut Performance Impact Strenght (kg/cm) Pinhole Resistance Gas-Barrier Performance Optical Character Total Evaluation MT TD E m b o d i m e n t s 1 6.5 6.5 ○ o ○ 6,500 ○ o ○ ○ ○ ○ 2 6.0 6.0 ○ o ○ 7,000 ○ o ○ ○ ○ ○ 3 6.0 6.0 ○ o ○ 7,000 ○ ○ ○ ○ ○ 4 6.0 6.0 ○ ○ 7,200 ○ 30 ○ Δ ○ 5 6.3 6.2 ○ o ○ 7,500 ○ 30 ○ ○ ○ 6 6.0 6.0 ○ o ○ 7,500 ○ 30 ○ ○ ○ 7 5.5 5.5 ○ o ○ 7,500 ○ 30 ○ ○ ○ 8 6.5 6.5 ○ o ○ 7,800 ○ 20 ○ ○ ○ 9 7.0 7.0 ○ o ○ 8,000 ○ 15 ○ ○ ○ 10 6.5 6.5 ○ o ○ 7,000 ○ 30 ○ ○ ○ 11 7.0 7.0 ○ ○ 5,500 ○ 30 ○ ○ ○ 12 6.5 6.5 ○ o ○ 6,500 ○ Δ ○ ○ ○ 13 6.5 6.5 ○ o ○ 6,500 ○ ○ ○ ○ ○ 14 6.5 6.5 ○ o ○ 6,500 ○ Δ ○ ○ ○ Raw Material Composition (% by weight) Layer Ratio Orientation Ratio 1 ○ 2 ○ 3 ○ PAE Ny MX Ny MX Ny MX 1 ○ 2 ○ 3 ○ MD TD 1 97 0 - - - - 3 1 0 0 3.0 3.0 2 87 10 - - - - 3 1 0 0 3.0 3.0 3 97 0 0 97 69 0 3 1 1 1 3.0 3.0 4 100 0 0 100 100 0 0 1 1 1 3.0 3.0 5 67 30 57 40 67 30 3 1 1 1 2.5 2.5 6 0 100 - - - - 0 1 0 0 3.0 3.0 7 0 97 - - - - 3 1 0 0 3.0 3.0 Tear Strength (kg/cm) Easy-Cleavage Linear Cut Performance Impact Strength (kg·cm/cm) Pinhole Resistance Gas-Barrier Performance Optical Character Total Evaluation MD TD 1 1 8.5 8.5 Δ × 8,000 ○ ○ × ○ × 2 7.0 7.5 Δ × 8,000 ○ ○ × ○ × 3 8.0 8.0 Δ × 7,000 ○ ○ ○ ○ × 4 8.0 8.0 Δ × 7,000 ○ × ○ ○ × 5 9.0 9.0 × × 5,000 ○ × × ○ × 6 6.5 6.5 ○ × 3,000 × × ○ ○ × 7 6.7 7.0 ○ × 3,500 × × ○ ○ × From Tables 1 and 2, it is understood that the easy-cleavage film has the first layer, the second layer and the third layer which contain Ny 6, MXD 6 and PAE, in which (1) the content of the aforementioned component of each layer, (2) the layer ratio of each layer and (3) the orientation ratio are within the predetermined range according to the present invention, so that the easy-cleavage film is sufficient in the easy-cleavage, the linear cut performance, the pinhole resistance, the gas-barrier performance and the optical character. Further, the easy-cleavage film according to the present invention does not contain a chlorine-type resin, so that there is no concern of producing a chloric gas when burning, and it is environmentally safe. On the other hand, from Tables 3 and 4, it is understood that, in the comparative example 1, the film is composed of only the Ny 6 layer containing PAE, therefore the film is inferior in the linear cut performance and the gas-barrier performance. In the comparative example 2, the film is composed of only one layer containing Ny 6 and MXD 6, in which, in addition, the amount of MXD 6 is only 10 %, therefore the film is inferior in the linear cut performance and the gas-barrier performance. Although the comparative example 3 has the first layer to the third layer each containing PAE, however the amounts of PAE, Ny 6 and MXD 6 contained in each layer are not of the ratios according to the present invention, whereby the film is inferior in the linear cut performance. Although the comparative example 4 has the first layer to the third layer, Ny 6 and MXD 6 contained in each layer are not of the ratios according to the present invention, whereby the film is inferior in the linear cut performance, and further, PAE is not added to each layer, whereby the film is inferior in the pinhole resistance. Although the comparative example 5 has the first layer to the third layer, the orientation ratio is low, two and a half times, whereby the film is inferior in the easy-cleavage, the linear cut performance, the pinhole resistance and the gas-barrier performance. The comparative example 6 has only the first layer containing MXD 6, whereby the film is inferior in the linear cut performance, the impact strength and the pinhole resistance. The comparative example 7, also, has only the first layer containing MXD 6 blended with PAE, whereby the film is inferior in the linear cut performance, the pinhole resistance and the impact strength.

Claims: An easy-cleavage film comprising a first layer, a second layer and a third layer which contain Nylon 6 (Ny 6), meta-xylylene adipamide (MXD 6) and polyamide elastomer (PAE), in which said film is defined as (1) a content of said components of each layer, (2) a layer ratio of each layer and (3) an orientation ratio as the following, (1) said first layer and said third layer being 60 to 85 % by weight of said Ny 6 content, 15 to 40 % by weight of said MXD 6 content and 0.1 to 10.0 % by weight of said PAE content, said second layer being 0 to 40 % by weight of said Ny 6 content, 60 to 100 % by weight of said MXD 6 content and 0.1 to 10.0 % by weight of said PAE content but, each layer being Ny 6 + MXD 6 + PAE = 100 % by weight, further, said MXD 6 content in said second layer being larger than said MXD 6 content in said first layer and the third layer, (2) said layer ratio of said first layer to said second layer to said third layer being defined as 1:8:1 - 4:2:4, the layer ratio between said first layer or said third layer to said second layer being defined as 1:8 - 2:1, and the layer ratio between said first layer to said third layer being defined as 1:2 - 2:1, (3) said orientation ratio is more than 2.8 times in both the direction of the movement of said film (a MD direction) and the direction of the width of said film (a TD direction). A method of producing an easy-cleavage film, which said easy-cleavage film has a first layer, a second layer and a third layer containing Nylon 6 (Ny 6), meta-xylylene adipamide(MXD 6) and polyamide elastomer(PAE), wherein (1) a blended amount of the raw materials for each layer is a blend of 60 to 85 % by weight of Ny 6, 15 to 40 % by weight of MXD 6 and 0.1 to 10.0 % by weight of PAE in the first layer and the third layer, and of 0 to 40 % by weight of Ny 6, 60 to 100 % by weight of MXD 6 and 0.1 to 10.0 % by weight of PAE in the second layer but, the blended amounts of each layer are Ny 6 + MXD 6 + PAE = 100 % by weight, further, said blended amount of MXD 6 in the second layer is larger than said blended amount of MXD 6 in the first layer and the third layer; (2) the layer ratio of each layer is defined as 1:8:1 - 4:2:4 in the first layer to the second layer to the third layer, as 1:8 - 2:1 between the first layer or the third layer and the second layer, and as 1:2 - 2:1 between the first layer and the third layer; and (3) said raw materials for forming the first layer up to the third layer are melted and kneaded, further, laminated after extruding in a film state, and then said cooled original film is oriented at an orientation ratio which is more than 2.8 times in both in the direction of the movement of said film (a MD direction) and in the direction of the width of said film (a TD direction).

Inventors: HAYASHI TAKEO, IWAMOTO TAKEHIRO, TAKASHIGE MASAO, HAYASHI, TAKEO, IWAMOTO, TAKEHIRO, TAKASHIGE, MASAO, Hayashi, Takeo, c/o Idemitsu Petrochem. Co, Ltd, Iwamoto, Takehiro, c/o Idemitsu Petrochem. Co, Ltd, Takashige, Masao, c/o Idemitsu Petrochem. Co., Ltd
Applicants: IDEMITSU PETROCHEMICAL CO, IDEMITSU PETROCHEMICAL CO., LTD.
Application year: 1995
Main classification: B32B27
IPC codes: B32B27