Polycyclic spirophthalimide derivatives, process for their preparation and their use as fulgimides

Abstract: A fulgimide compound which reversibly changes from a colorless state into a colored state upon the action of light including ultraviolet-rays, and a photochromic composition containing the compound. The fulgimide compound is of formula (I), wherein the represents a divalent aromatic hydrocarbon or unsaturated heterocyclic group, R¹ represents a monovalent hydrocarbon or heterocyclic group and represents a norbornylidene group, bicyclo[3,3,1]nonylidene group or adamantylidene group and R² is perhalogenoalkyl, cyano, alkoxycarbonyl, alkylcarbonyl, arylcarbonyl, nitro ulfonyl, alkylsulfonyl, arylsulfonyl or aryloxycarbonyl.

Description: BACKGROUND OF THE INVENTION (Field of the Invention) The present invention relates to a fulgimide compound having photochromic action, to a composition containing the same compound and to the use thereof. More specifically, the invention relates to a fulgimide compound having excellent durability which changes from a colorless state into a colored state upon the action of light that contains ultraviolet rays such as of the sun light or the mercury lamps, the change being reversible, to a composition containing the same compound and to the use thereof. (Description of the Prior Art) Photochromism is a phenomenon which is drawing attention in these several years and is a reversible action exhibited by certain compounds. That is, a compound quickly changes its color when it is irradiated with the sun light or the light containing ultraviolet rays such as of a mercury lamp and returns to the original color when it is no longer irradiated with the light and is placed in a dark place. The compound having this property is called photochromic compound, and compounds having various structures have heretofore been synthesized and proposed without, however, any common skeleton among their structures. Under such circumstances, a fulgide compound or a fulgimide compound disclosed in Japanese Laid-Open Patent Publication No. 28154/1990 and represented by the following general formula exhibits no color and remains stable in a general state but readily develops color upon irradiation with the sun light or ultraviolet rays, returns to the colorless state when it is no longer irradiated with the light, and is, hence, a compound having excellent photochromic property making it possible to repeat these changes in color maintaining good durability. In the fulgide compound or fulgimide compound, stands for an aromatic hydrocarbon group or an unsaturated heterocyclic group, and R 1' stands for a hydrocarbon group or a heterocyclic group. Moreover, Y' stands for an oxygen atom, an imide group, or a group in which a hydrogen atom of the imide group is substituted by a group to which is bonded an electron-releasing group of an alkyl group or an aryl group or to which is bonded an electron-withdrawing group of a cyano group or an alkoxycarbonyl group via an alkylene group or an alkylidene group. Furthermore, represents a norbornylidene group or an adamantylidene group which may have a substituent. It has been considered that the fulgimide compound which has a rigid cage-like adamantylidene group or a norbornylidene group without distortion, weakens a single bond that constitutes a part of a six-membered ring, facilitates electron-cyclic ring cleavage upon irradiation with the light containing ultraviolet rays, and, as a result, assumes a color-producing form. As a maximum absorption wavelength is lengthened, however, these compounds develop a defect in that they have already been exhibiting yellowish color (hereinafter often referred to as initial coloring) before they are being irradiated with ultraviolet rays. When these compounds are used for a photochromic lens or the like, therefore, the lens at first exhibits a yellow color. In such circumstances, therefore, it has been urged to develop a photochromic compound suppressing the initial coloring despite a maximum absorption wavelength is lengthened. SUMMARY OF THE INVENTION The object of the present invention is to provide a novel fulgimide compound. Another object of the present invention is to provide a compound which changes from a colorless state into a colored state or a densely colored state upon irradiation with the light such as sun light or light containing ultraviolet-rays such as of a mercury lamp, the change being reversible. A further object of the present invention is to provide a fulgimide compound which suppresses initial coloring. A still further object of the present invention is to provide a highly practicable fulgimide compound. Yet further object of the present invention is to provide a process which is industrially advantageous for producing a fulgimide compound. Furthermore, the object of the present invention is to provide a high molecular composition containing a fulgimide compound. The above-mentioned objects of the present invention will become obvious from the following description. These objects of the present invention are accomplished by a novel fulgimide compound represented by the following formula (I), wherein: is an aryl group of 6 to 14 carbon atoms, a five-membered or six-membered mono-heterocyclic group comprising at least one heteroatom selected from nitrogen, oxygen and sulfur, or is a condensed heterocyclic group comprising said mono-heterocyclic group fused with a benzene ring or a cyclohexane or cyclohexene ring, and which aryl or heterocyclic group is unsubstituted or substituted by one to three substituents chosen from halogen, nitro, alkylthio of 1 to 4 carbon atoms, aryl of 6 to 10 carbon atoms, alkyl of 1 to 4 carbon atoms and alkoxy of 1 to 4 carbon atoms; is a norbornylidene group, a bicyclo [3,3,1]nonylidene group or an adamantylidene group which is unsubstituted or substituted by one or more substituents chosen from halogen, alkyl of 1 to 4 carbon atoms and alkoxy of 1 to 4 carbon atoms; R 1 is an alkyl group of 1 to 20 carbon atoms, an aryl group of 6 to 14 carbon atoms, a cycloalkyl group of 3 to 7 carbon atoms, or a five-membered or six-membered mono-heterocyclic ring group comprising at least one heteroatom selected from nitrogen, oxygen, and sulfur, and which group R 1 may be unsubstituted or substituted by one or more substituents as defined for the group (a); and R 2 is perhalogenoalkyl of 1 to 4 carbon atoms; cyano; alkoxycarbonyl of 2-5 carbon atoms unsubstituted or substituted by one or more substituents chosen from halogen and cyano; alkylcarbonyl of 2-5 carbon atoms unsubstituted or substituted by one or more substituents chosen from halogen and cyano; arylcarbonyl of 7-11 carbon atoms unsubstituted or substituted by one or more substituents chosen from halogen and cyano; nitro; sulfonyl; alkylsulfonyl of 1-4 carbon atoms unsubstituted or substituted by one or more substituents chosen from halogen and cyano; arylsulfonyl of 6-10 carbon atoms unsubstituted or substituted by one or more substituents chosen from halogen and cyano; or aryloxycarbonyl of 7-11 carbon atoms unsubstituted or substituted by one or more substituents chosen from halogen and cyano. Fig.1 is an 1 H-NMR chart of a compound obtained in Example 1. Examples of the ring that forms the aromatic hydrocarbon ring of formula (a) include a benzene ring, naphthalene ring, phenanthrene ring, etc. Examples of ring forming heterocyclic groups include nitrogen-containing heterocyclic rings such as pyrrole ring, pyridine ring, quinoline ring, isoquinoline ring, and indole ring; oxygen-containing heterocyclic rings such as furan ring, benzofuran ring, pyran ring, and tetrahydrobenzofuran ring; and sulfur-containing heterocyclic ring such as thiophene ring, benzothiophene ring, and tetrahydrobenzothiophene ring. Examples of the substituents that may be possessed by the aromatic hydrocarbon group or the unsaturated heterocyclic group represented by the above-mentioned formula (a) include halogen atoms such as fluorine, chlorine, bromine and iodine; nitro groups; alkyl groups having 1 to 4 carbon atoms such as methyl group, ethyl group, propyl group and t-butyl group; alkoxy group having 1 to 4 carbon atoms such as methoxy group, ethoxy group and t-butoxy group; aryl groups having 6 to 10 carbon atoms such as phenyl group, naphthyl group and toluyl group; and alkylthio groups having 1 to 4 carbon atoms. These substituents may be the same or different, and there is no particular limitation in their positions. Where the group represented by the above-mentioned formula (a) is a condensed heterocyclic group, the heterocyclic ring group is preferably condensed with a benzene ring or a cyclohexene ring. It is further desired that the group represented by the above-mentioned formula (a) is a benzene ring, a five-membered or six-membered mono- heterocyclic ring having 1 to 3 hetero atoms, or a condensed heterocyclic ring of a form in which the above heterocyclic ring is condensed with a benzene ring or a cyclohexene ring. Preferably, these benzene ring, mono-heterocyclic ring or condensed heterocyclic ring contain 1 or 2 substituents that are mentioned above. Examples of R 1 include alkyl groups having 1 to 6 carbon atoms such as methyl group, ethyl group, propyl group and butyl group; aryl groups such as phenyl group, toluyl group, xylyl group and naphthyl group; and cycloalkyl groups such as cyclopropyl group, cyclobutyl group and cyclopentyl group and, particularly, cyclopropyl group. The heterocyclic group will preferably contain 1-3 hetero atoms of at least one kind. Preferred examples of the ring forming the heterocyclic group include nitrogen-containing unsaturated heterocyclic rings such as pyrrole ring, pyridine ring, etc.; oxygen-containing unsaturated heterocyclic rings such as furan ring, pyran ring, etc.; and sulfur-containing unsaturated heterocyclic rings such as thiophene ring, etc. It is also allowable to use saturated heterocyclic groups such as saturated piperidine ring, piperazine ring, morpholine ring, pyrrolidine ring, indoline ring and chroman ring. Concrete examples of the substituents for the groups represented by R 1 will be those substituents explained with reference to the formula (a), and the number thereof may be one or more. In the group represented by the formula (b), a preferred example of norbornylidene group is a 7-norbornylidene group represented by the following formula (c) a preferred example of bicyclo[3,3,1]nonylidene group is a bicyclo[3,3,1]9-nonylidene group represented by the following formula (d) and a preferred example of adamantylidene group is a 2-adamantylidene group represented by the following formula (e) The above formulas represent skeletal structures of the 7-norbornylidene group, bicyclo[3,3,1]9-nonylidene group or 2-adamantylidene group without having substituent. In the 7-norbornylidene group, bicyclo[3,3,1]9-nonylidene group or 2-adamantylidene group, a hydrogen atom in the above-mentioned formula may be substituted by one or more substituents which may be the same or different. When the group has a substituents, the kind, number and position thereof are selected from those listed above depending upon the object and application. As substituents for the 7-norbornylidene group, bicyclo[3,3,1]9-nonylidene group or 2-adamantylidene group, there can be exemplified alkoxy groups such as methoxy, ethoxy and tert-butoxy alkyl groups such as methyl, ethyl and t-butyl; and halogen atoms such as fluorine, chlorine and bromine. The R 2 groups are all electron-withdrawing groups. According to the present invention, a particular electron-withdrawing group is directly bonded to the imide group that constitutes the fulgimide compound, so that the initial coloring of the fulgimide compound is markedly decreased. Among the groups represented by R 2 , examples of the perhalogenoalkyl group include trichloromethyl group, trifluoromethyl group, pentafluoroethyl group, heptafluoropropyl group and nonafluorobutyl group; examples of the alkoxycarbonyl group include methoxycarbonyl group, ethoxycarbonyl group, propoxycarbonyl group, butoxycarbonyl group and t-butoxycarbonyl group; examples of the alkylcarbonyl group include methylcarbonyl group, ethylcarbonyl group, propylcarbonyl group, butylcarbonyl group and t-butylcarbonyl group; examples of the arylcarbonyl group include benzoyl group and 1-naphthylcarbonyl group; examples of the alkylsulfonyl group include methylsulfonyl group, ethylsulfonyl group, propylsulfonyl group and t-butylsulfonyl group; examples of the arylsulfonyl group include phenylsulfonyl group and naphthylsulfonyl group; and examples of the aryloxycarbonyl group include phenoxycarbonyl group, naphthoxycarbonyl group and the like. Furthermore, an R 2 group substituted by halogen atom is preferably one in which an alkoxy group, alkyl group or aryl group thereof is entirely substituted by halogen atoms. Examples of such groups include perhalogenoalkoxycarbonyl groups having 2 to 5 carbon atoms such as trichloromethoxycarbonyl group, trifluoromethoxycarbonyl group, pentafluoroethoxycarbonyl group, heptafluoropropoxycarbonyl group and nonafluorobutoxycarbonyl group; perhalogenoalkylcarbonyl groups having 2 to 5 carbon atoms such as trichloromethylcarbonyl group, trifluoromethylcarbonyl group, pentafluoroethylcarbonyl group, heptafluoropropylcarbonyl group, and nonafluorobutylcarbonyl group; and perhalogenoarylcarbonyl groups having 7 to 11 carbon atoms such as pentafluorobenzoyl group and the like. It is desired that the group represented by formula (b) is 7-norbornylidene, bicyclo[3,3,1]9-nonylidene or 2-adamantylidene which may have a substituent, and that R 2 is cyano, perhalogenoalkylcarbonyl or, alkylcarbonyl, which may have a substituent, arylcarbonyl which may have a substituent, and, particularly, cyano or arylcarbonyl which may have a substituent, from the standpoint of suppressing the initial coloring of the obtained compound. When R 2 is cyano , the fulgimide compound that is obtained can be used as a photochromic compound for developing color and extinguishing color reversibly and repetitively maintaining durability superior to that of other fulgimide compounds having a comparable maximum absorption wavelength at the time of developing color. Exemplified below are fulgimide compounds represented by the above-mentioned formula (1) that can be preferably used in the present invention. (1) N-Cyano-4-cyclopropyl-6,7-dihydrospirobenzothiophene dicarboxyimide-7,2'-tricyclo[3.3.1.1 3,7 ]decane, (2) N-Acetyl-4-cyclopropyl-6,7-dihydrospirobenzothiophen edicarboxyimide-7,2'-tricyclo[3.3.1.1 3,7 ]decane, (3) N-Benzoyl-4-cyclopropyl-6,7-dihydrospirobenzothiophe nedicarboxyimide-7,2'-tricyclo[3.3.1.1 3,7 ]decane, (4) N-Acetyl-4-cyclopropyl-6,7-dihydro-2-methylspirobenz othiophenedicarboxyimide-7,2'-tricyclo[3.3.1.1 3,7 ]decane, (5) N-Cyano-6,7-dihydro-4-methyl-2-phenylspirobenzothiop henedicarboxyimide-7,2'-tricyclo[3.3.1.1 3,7 ]decane, (6) 5'-Chloro-6,7-dihydro-N-methyl-N'-methylsulfonyl-4-isopropylspiroindoledicarboxyimide-7,2'-tricyclo [3.3.1.1 3,7 ]decane, (7) 3',5'-Dichloro-3,4-dihydro-1-ethyl-7-methoxy-N-trichloromethylcarbonylspirodibenzo[5,6-b: d]thiophenedicarboxyimide-4,2'-tricyclo[3.3.1.1 3,7 ]decane, (8) N-Benzoyl-3,4-dihydro-5'-methyl-1-(p-methoxyph enyl)spirobenzo[5,6-b:d]furandicarboxyimide-4,2-tricyclo [3.3.1.1 3,7 ]decane, (9) 4-Cyclopropyl-5'-methoxy-N'-phenyl-N-trichloromethyl carbonylspirobenzo[b]indoledicarboxyimide-4,2'-tricyclo [3.3.1.1 3,7 ]decane, and (10) 1-Cyclopropyl-3,4-dihydro-N-phenylsulfonyl(6,7,8,9-tetrahydrodibenzo[5,6-b:d]thiophenedicarboxyimide-4,2'-tricyclo[3.3.1.1 3,7 ]decane. The fulgimide compound represented by the above-mentioned general formula (I) of the present invention usually exists as a pale-yellow solid at normal temperature, and can be confirmed by the following means (a) to (c). (a) The kind and number of protons present in the molecules can be learned by measuring a proton nuclear magnetic resonance spectrum ( 1 H-NMR). That is, a peak due to aromatic proton appears near δ 7 to 8 ppm and a broad peak appears near δ 1.2 to 2.5 ppm due to a group in which R 1 is a cycloalkyl group, and due to a norbornylidene group, a bicyclo[3.3.1]nonylidene group or adamantylidene group. By comparing their δ peak intensities, furthermore, it is allowed to know the number of protons in the bound groups. (b) Percentage by weight of carbon, hydrogen, nitrogen, sulfur and halogen can be found by elemental analysis. By subtracting the sum of the elements (% by weight) that is found from 100, furthermore, it is allowed to calculate the amount of oxygen (% by weight). It is therefore possible to determine the composition of the corresponding product. (c) By measuring the 13 C-nuclear magnetic resonance spectrum ( 13 C-NMR), it is allowed to know the kind of carbon present in the molecules. A peak appears near δ 27 to 52 ppm due to a group in which R 1 is a cycloalkyl group, and due to a norbornylidene group, a bicyclo [3.3.1]nonylidene group or an adamantylidene group, and a peak appears near δ 110 to 150 ppm due to carbon >C=0. The fulgimide compound of the above-mentioned general formula (I) of the present invention may be produced by any process, and no limitation is imposed on the kind of the process for its preparation. Described below, however, is a preferred and representative process to which only the present invention is in no way limited. The fulgimide compound can be produced by, for example, the following process A. Process A: According to this process A, a fulgimide compound represented by the above-mentioned general formula (I) is prepared by reacting an acid anhydride represented by the following general formula (II) wherein and R 1 are as defined in the above-mentioned general formula (I), with amines represented by the following formula (III) H 2 N-R 2 wherein R 2 is as defined in the above-mentioned general formula (I), followed by cyclization. It is desired that the reaction in this process A is carried out in a solvent which is a nonprotonic polar solvent such as N-methylpyrrolidone, dimethylformamide, tetrahydrofuran or 1,4-dioxane. In the method in which the acid anhydride of the above general formula (II) is reacted with the amine compound and is then cyclized, it is desired to effect the heating at, for example, 160 to 220 °C, or to effect this heating in combination with irradiation with ultraviolet rays, or to bring the reaction system into contact with a Lewis acid catalyst. As the Lewis acid catalyst, a known compound such as SnCl 4 , TiCl 4 , SbCl 5 or AlCl 3 can be used without any limitation. Though there is no particular limitation, it is desired to use the Lewis acid catalyst in an amount of usually from 0.001 to 1 mole per mole of the compound that is to be cyclized. In the process A, furthermore, when the acid anhydride of the general formula (II) is to be reacted with the amine compound, the reaction ratio may be selected over a wide range but is usually from 1:10 to 10:1 and, preferably, from 1:5 to 5:1 in terms of a molar ratio. The above reaction is carried out usually under the conditions of a temperature of from 25 to 160 °C and a time of from 1 to 24 hours. After the reaction, the solvent is removed, the reaction product is dehydrated with a dehydrating agent such as acetyl chloride or anhydrous acetic acid, and the obtained compound is subjected to the cyclization reaction under the above-mentioned conditions to obtain a fulgimide compound of the present invention. In the process A, the acid anhydride represented by the above-mentioned general formula (II) used as a starting material can be prepared by, for example, the following method. That is, a carbonyl compound represented by the following general formula (IIa) wherein and R 1 are as defined in the above-mentioned general formula (I), and a derivative of diester of succinic acid represented by the following general formula (IIb) wherein is as defined in the above-mentioned general formula (I), and R 3 and R 4 are the same or different alkyl groups having 1 to 6 carbon atoms, are subjected to the condensation reaction followed by the processing that will be described later, to obtain an acid anhydride represented by the above-mentioned general formula (II). In the above-mentioned condensation reaction, the reaction ratio of the carbonyl compound of the general formula (IIa) and the derivative of diester of succinic acid of the general formula (IIb) is selected from a wide range but is generally selected to be 1:10 to 10:1 and, preferably, 1:5 to 5:1. The reaction is usually carried out at 0 °C to 110 °C and, preferably, at 10 °C to 100 °C. It is desired that the reaction is carried out by using a solvent which may be a non-protonic solvent such as benzene, diethyl ether, toluene or tetrahydrofuran. The condensation reaction is usually carried out in the presence of a condensing agent such as sodium hydride, t-butoxide, sodium ethylate, etc. The condensing agent is used in an amount of usually from 0.1 to 10 moles per mole of the carbonyl compound of the above-mentioned general formula (IIa). After the reaction, the obtained diester of dicarboxylic acid is converted into a free dicarboxylic acid. This reaction is carried out under the conditions of a hydrolysis reaction in the presence of a base that has been widely known. The reaction is carried out by using, for example, a sodium hydroxide solution containing 10% of ethanol at a temperature of from 0 to 80 °C. The thus obtained dicarboxylic acid is converted into an acid anhydride according to a method that has been widely known; i.e., the acid anhydride of the above-mentioned general formula (II) is thus obtained. The reaction for obtaining the acid anhydride is carried out by using a widely known reagent such as anhydrous acetic acid or acetyl chloride. Process B: According to this process B, a fulgimide compound represented by the above-mentioned general formula (I) is prepared by reacting an imide compound represented by the following general formula (IV) wherein and R 1 are as defined in the above-mentioned general formula (I), with an alkali metal, followed by the reaction with a halogen compound represented by the following formula (V) A-R 2 wherein R 2 is as defined in the above-mentioned formula (I), and A is a halogen atom. The alkali metal used in this process B may be a metal sodium, a metal potassium or a metal lithium. The reaction ratio of the alkali metal is usually selected over a range of from 1.0 to 10 moles per mole of the imide compound represented by the above-mentioned general formula (IV). It is further desired that the reaction ratio of the halogen compound is selected over a range of from 0.5 to 10 moles per mole of the compound that is obtained by reacting an alkali metal. The solvent used in this reaction is the one which is the same as the one that was described with reference to the above-mentioned process A. Preferably, the reaction temperature is usually from 0 to 100 °C. The fulgimide compound of the above-mentioned general formula (I) of the present invention can be obtained by either the above-mentioned process A or the process B or by a modification thereof. The fulgimide compound of the above-mentioned general formula (I) of the present invention usually exhibits orange to bluish color tone when it develops color. When a desired color is not obtained from this compound that is used as a photochromic compound, therefore, it is desired to use it being mixed with a photochromic compound having other color tone. In such a case, a chromene compound can be favorably used as the other photochromic compound. That is, the chromene compound usually develops orange to yellowish color tone. By mixing it to the fulgimide compound of the above-mentioned general formula (I), therefore, there can be obtained such colors as grey, amber, brown, as well as various other intermediate color tones. The chromene compound has a chromene skeleton. Any widely known compound having photochromic property can be used without any limitation. In particular, a chromene compound represented by the following general formula (VI) can be favorably used, wherein R 5 , R 6 , R 7 and R 8 may be the same or different and are hydrogen atoms, hydrocarbon groups, substituted amino groups, aromatic hydrocarbon groups, unsaturated heterocyclic groups or saturated heterocyclic groups which may have a substituent, and R 7 and R 8 in combination may form a ring, and is an aromatic hydrocarbon group or an unsaturated heterocyclic group which may have a substituent, respectively. It is desired that in the above formula (VI), R 5 , R 6 , R 7 and R 8 are hydrogen atoms, alkyl groups, aryl groups, substituted amino groups or saturated heterocyclic ring groups. Here, the alkyl group and aryl group may be those described with reference to the aforementioned formula (I), the substituted amino group may be the one in which at least one hydrogen atom is substituted in the alkyl group and in the aryl group, and the saturated heterocyclic ring group may be a monovalent group derived from a five- to six-membered ring that contains one to two nitrogen atoms, oxygen atoms or sulfur atoms such as of pyrrolidine ring, imidazoline ring, piperidine ring, piperazine ring or morpholine ring, as ring-constituting atoms. In the above formula (VI), a ring formed by R 7 and R 8 in combination will be a norbornylidene group, a bicyclo(3.3.1)nonylidene group, etc. In the above formula (VI), furthermore, the aromatic hydrocarbon groups or the unsaturated heterocyclic ring groups represented by are the same as the groups described in the above-mentioned formula (I). Though there is no particular limitation, the substituent of these groups will be, for example, a halogen atom such as chlorine, bromine or iodine; an alkyl group having 1 to 20 carbon atoms such as methyl group or ethyl group; an alkoxy group having 1 to 20 carbon atoms such as methoxy group or ethoxy group; an aryl group having 6 to 10 carbon atoms such as phenyl group, tolyl group or xylyl group; an amino group; a nitro group; a cyano group and the like group. Among the chromene compounds represented by the above-mentioned general formula (VI), preferred compounds are those in which R 5 and R 6 are both hydrogen atoms, R 7 and R 8 are alkyl groups, respectively, or in combination are forming a bicyclo(3.3.1)nonylidene group or a norbornylidene group, and is a naphthalene ring which may be substituted, from the standpoint of photochromic property. Concretely described below are the chromene compounds that can be favorably used in the present invention. Chromene compounds: (1) Spiro(norbornane-2,2'-(2H)benzo(h)chromene), (2) Spiro(bicyclo[3.3.1]nonane-9,2'-(2H)benzo(h)-chromene) (3) 7'-Methoxyspiro(bicyclo(3,3,1)nonane-9,2'-(2H)benzo(h)chromene), (4) 7'-Methoxyspiro(norbornane-2,2'-(2H)benzo(f)-chromene), (5) 2,2-Dimethyl-7-octoxy(2H)benzo(h)chromene), (6) 4'-Methylspiro(bicyclo(3,3,1)nonane-9,2'-(2H)-benzo(h)chromene), (7) 3'-Methylspiro(bicyclo(3.3.1)nonane-9,2'-(2H)-benzo(h)chromene), (8) Spiro(tricyclo[3.3.1.13.7]decane-2,2'-(2H)-benzo(h)chromene), (9) 4'-Piperidinospiro(bicyclo(3.3.1)nonane-9,2'-(2H)benzo(h)chromene), (10) 2,2-Dimethyl-6-octoxy(2H)benzo(h)chromene), (11) Spiro(norbornane-2,2'-(2H)naphtho-(1,2-h)chromene), (12) 2,2-Dimethyl-7-(ethylthiohexyl)oxy(2H)benzo (h)chromene), (13) 6-Chloro-2,2-dimethyl-7-(diisopropylphosphorohexyl) oxo(2H)benzo(h)chromene, (14) 2,2-Dimethyl(2H)pyrido(2,3-h)chromene, (15) 7-Methoxy-2,2-dimethyl(2H)benzo(h)chromene, and (16) 7-(Diethylaminooctyl)-2,2-dimethyl(2H)benzo (h)chromene. According to the present invention, the fulgimide compound and the chromene compound can be mixed at any ratio depending upon the desired color tone. To obtain such a color tone as grey, brown, amber, etc., it is usually desired that the chromene compound is used in an amount of 0.01 to 10000 parts by weight, preferably, 1 to 1000 parts by weight and, more preferably, 10 to 500 parts by weight per 100 parts by weight of the fulgimide compound. The fulgimide compound and the chromene compound may be added in two or more kinds, respectively. It is further allowable to blend the photochromic composition with a spiro-oxazine compound to adjust such color tone as grey, brown, amber, etc. Any widely known spiro-oxazine compound can be used without any limitation provided it has a spiro-oxazine skeleton and photochromic property. The spiro-oxazine compounds represented by the following formula (VII) can be preferably used wherein R 9 , R 10 and R 11 may be the same or different, and are alkyl groups, cycloalkyl groups, alkoxy groups, alkyleneoxyalkyl groups, alkoxycarbonyl groups, alkoxycarbonylalkyl groups, aryl groups, aralkyl groups, aryloxy groups, alkylenethioalkyl groups, acyl groups, acyloxy groups or amino groups, and R 10 and R 11 together may form a ring, R 9 , R 10 and R 11 may have a substituent, respectively, and thesubstituent may be halogen atom, nitro group, cyano group or heterocyclic group in addition to being the above-mentioned groups. Moreover, the group is an aromatic hydrocarbon group or an unsaturated heterocyclic group that may have a substituent, respectively, and the group is an aromatic hydrocarbon group or an unsaturated heterocyclic group that may have a substituent, respectively. The substituents may be the same ones as represented by R 9 , R 10 and R 11 above. Among them, a group represented by wherein R 12 and R 13 are alkyl groups, alkoxy groups or aryl groups that may have a substituent, and R 12 and R 13 may be bonded together, cyclized, or may form a nitrogen-containing heterocyclic ring, is preferably used. Among the spiro-oxazine compounds represented by the above-mentioned formula (VII), it is desired to use those compounds in which R 9 is an alkyl group or an alkoxycarbonylalkyl group, R 10 and R 11 are cycloalkyls which together are forming a ring, is an aromatic hydrocarbon group which may be partly or entirely substituted with halogen atoms and, particularly, with fluorine, and is an aromatic hydrocarbon group that may have a substituent and is, particularly, a naphthalene ring substituted with amino group. Concretely described below are the spiro-oxazine compounds that can be favorably used in the present invention. Spiro-oxazine compounds: (1) 1',5'-Dimethyl-6'-fluoro-6"-morpholinodispiro (cyclohexane-1,3'-(3H)indole-2'-(2'H),3"-(3H)naphtho(3,2-a)(1,4)oxazine, (2) 6'-Fluoro-1'-methoxycarbonylethyl-8"-methoxy-6"-piperazinodispiro(cyclohexane-1,3'-(3H)indole-2'-(2'H), 3"-(3H)naphtho(3,2-a)(1,4)oxazine, (3) 1'-(2-(Dioxazine-2-il)ethyl)-6'-fluoro-6"-(4-methylpiperazino)dispiro(cyclohexane-1,3'-(3H)indole-2'-(2H),3"-(3H)naphtho(3,2-1)(1,4)oxazine, (4) 5',7'-Difluoro-1'-methyl-6"-morpholinodispiro (cyclohexane-1,3'-(3H)indole-2'-(2H),3"-(3H)naphtho(3,2-a)(1,4)oxazine, and (5) 1'-Isobutyl-5'-methyl-6'-fluro-6"-morpholinodispiro (cyclohexane-1,3'-(3H)indole-2'-(2H),3"-(3H)naphtho(2,3-a)(1,4)oxazine. According to the present invention, the photochromic composition and the spiro-oxazine compound can be mixed at any ratio depending upon the desired color tone. To obtain such a color tone as grey, brown, amber, etc., it is usually desired that the spiro-oxazine compound is used in an amount of 0.01 to 10000 parts by weight, preferably, 0.1 to 1000 parts by weight and, more preferably, 1 to 500 parts by weight per 100 parts by weight of the photochromic composition which comprises a fulgimide compound represented by the above-mentioned formula (I) and the chromene compound. The spiro-oxazine compounds may be added in two or more kinds. The fulgimide compound of the present invention may be dispersed in an organic solvent to obtain a photochromic fluid that can be used for ornamental applications and the like applications. The fulgimide compound of the present invention may further be dispersed in a polymer such as a thermosetting resin or a thermoplastic resin obtained by polymerizing a polymerizable monomer to obtain molded articles such as photochromic lenses and the like. In this case, the fulgimide compound represented by the above-mentioned formula (I) or the photochromic composition comprising the fulgimide compound and other photochromic compound such as chromene compound or spiro-oxazine compound, is added in an amount of 0.001 to 20 parts by weight and, preferably, 0.01 to 10 parts by weight per 100 parts by weight of the polymerizable monomer or per 100 parts by weight of the thermoplastic resin. Any widely known thermosetting resin can be used without any limitation provided it permits a photochromic compound to be uniformly dispersed therein. Examples of the thermosetting resin that can be preferably used include polyhydric acrylic acid and polyhydric methacrylic ester compound such as ethylene glycol diacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, ethylene glycol bisglycidylmethacrylate, bisphenol A dimethacrylate, 2,2-bis(4-methacryloyloxyetho xyphenyl) propane, and 2,2-bis(3,5-dibromo-4-methacryloyl oxyethoxyphenyl) propane; polyhydric allyl compounds such as diallyl phthalate, diallyl terephthalate, diallyl isophthalate, dially tartarate, diallyl epoxysuccinate, diallyl fumarate, diallyl chlorendate, diallyl hexaphthalate, diallyl carbonate, allyl diglycol carbonate and trimethylolpropanetriallyl carbonate; polyhydric thioacrylic acid and polyhydric thiomethacrylic esters such as 1,2-bis(methacryloyl thio)ethane, bis(2-acryloylthioethyl)ether, and 1,4-bis(methacryloylthiomethyl)benzene; methacrylate compounds or acrylate compounds such as glycidyl acrylate, glycidyl methacrylate, β-methylglycidyl methacrylate, bisphenol A-monoglycidylether methacrylate, 4-glycidyloxy methacrylate, 3-(glycidyl-2-oxyethoxy)-2-hydroxypropyl methacrylate, 3-(glycidyloxy-1-isopropyloxy)-2-hydroxypropyl acrylate, and 3-(glycidyloxy-2-hydroxypropyloxy)-2-hydroxypropyl acrylate; and a thermosetting resin obtained by polymerizing a radically polymerizable polyfunctional monomer such as divinyl benzene and the like. There can be further exemplified thermosetting resins obtained by copolymerizing the above-mentioned radically polymerizable polyfunctional monomers with radically polymerizable monofunctional monomers like unsaturated carboxylic acids such as acrylic acid, methacrylic acid and maleic anhydride; acrylic and methacrylic ester compounds such as methyl acrylate, methyl methacrylate, benzyl methacrylate, phenyl methacrylate, and 2-hydroxyet hyl methacrylate; fumaric ester compounds such as diethyl fumarate and di[henyl fumarate; thioacrylic and thiomethacrylic ester compounds such as methylthioacrylate, benzylthioacrylate and benzylthiomethacrylate; or vinyl compounds such as styrene, chlorostyrene, methylstyrene, vinylnaphthalene, α-methylstyrene dimer and bromostyrene. There can be further exemplified an addition copolymer of a polyhydric thiol compound such as ethanedithiol, propanetriol, hexanedithiol, pentaerythritol tetrakisthioglycolate or di(2-mercaptoethyl)ether and the above-mentioned radical polymerizable polyfunctional monomer; and a thermoplastic resin obtained by the addition polymerization of a polyhydric isocyanate compound such as diphenylethane diisocyanate, xylylene diisocyanate or p-phenylene diisocyanate and a polyhydric alcohol compound such as ethylene glycol, trimethylolpropane, pentaerythritol or bisphenol A or the above-mentioned thiol compound. These polymerizable monomers can be used in a single kind or being mixed together in two or more kinds. The photochromic compound can be dispersed in the thermosetting resin in a generally employed method without any limitation. For instance, there can be employed a method wherein the photochromic compound is dissolved in the polymerizable monomer and, then, a polymerization catalyst is added thereto to effect the polymerization with the heat or light to disperse it in the resin, or a method which permits the photochromic compound to stay on the surface of the thermosetting resin. Furthermore, any thermoplastic resin can be used without any limitation provided it permits the photochromic compound to be uniformly dispersed therein. Optically desired examples thereof include methyl polyacrylate, ethyl polyacrylate, methyl polymethacrylate, ethyl polymethacrylate, polystyrene, polyacrylonitrile, polyvinyl alcohol, polyacrylamide, poly(2-hydroxyethyl methacrylate), polydimethyl siloxane, polycarbonate, etc. The photochromic compound can be dispersed in the thermoplastic resin by a generally employed method without any limitation. For instance, there can be employed a method in which the thermoplastic resin and the photochromic compound are melted and kneaded at a temperature higher than the melting temperature of the thermoplastic resin. The composition of the present invention blended with an ultraviolet-ray stabilizer features an improved durability in exhibiting photochromic property. As the ultraviolet-ray stabilizer, any widely known ultraviolet-ray stabilizer added to various plastics can be used without any limitation. In an attempt to improve durability of the compound of the present invention, a singlet oxygen extinguishing agent and a hindered amine photo stabilizer can be preferably used among various ultraviolet-ray stabilizers. The fulgimide compounds of the present invention can be used over a wide range of fields as various recording materials, copying materials, potosensitive materials for printing, recording materials for cathode-ray tubes and as photosensitive materials for laser applications to substitute for silver salt photosensitive materials. Moreover, the fulgimide compounds of the present invention can be used as materials for photochromic lenses, for optical filters, as display materials, as actinometers and as ornamental materials. When the fulgimide compound is used for a photochromic lens, any method can be employed without limitation provided it makes it possible to obtain a uniformdimming property. Concretely speaking, there can be employed a method by which a polymer film in which the fulgimide compound of the present invention is uniformly dispersed is sandwiched at the center of the lens, a method by which the fulgimide compound and a photo initiator are dissolved in a polymerizable monomer by heating, and the polymer is then cured by a predetermined method, and a method by which the fulgimide compound of the present invention is dissolved in, for example, a silicone oil, applied to the lens surfaces at 150 to 200 °C over a period of 10 to 60 minutes, and the surfaces are coated with a curable material to obtain a photochromic lens. It can be further contrived to obtain a photochromic lens by applying the polymer film onto the lens surfaces which are then coated with a curable material. In the fulgimide compound of the general formula (I) of the present invention in which a particular electron attractive group is directly introduced to the imide moiety thereof, development of color is favorably suppressed in an initial state of not developing color, and the effect of lengthening the wave is obtained. By using the fulgimide compound which is blended with a chromene compound and a spiro-oxazine compound, it is allowed to develop such colors as grey, brown, amber as well as a variety of intermediate colors from its no-color state. Among the fulgimide compounds, furthermore, those in which R 2 is a cyano group feature superior durability for reversibly repeating developing of color and extinction of color to that of other fulgimide compounds having a comparable maximum absorption wavelength for developing color. The invention will now be described in detail by way of Examples. (Example 1) 10.0 Grams (0.066 mols) of a 3-cyclopropylthienyl ketone and 20.0 g (0.065 mols) of a diethyl 2-adamantylid enesuccinate of the following formula were dissolved in 200 cc of toluene to prepare a solution. This toluene solution was added to a solution of 200 cc of toluene in which 5.6 g of sodium hydride was dispersed, and the mixture solution was vigorously stirred maintaining a temperature of not higher than 0 °C for 10 hours. The solution was hydrolyzed with an excess of 10 % alcoholic potassium hydroxide solution. Then, a dicarboxylic acid obtained by the acidification with hydrochloric acid was treated with 100 cc of acetyl chloride and was purified by chromatography on silica gel to obtain 11.5 g of a fulgide compound of the following formula, The obtained compound was dissolved in 100 cc of acetone, and to which was dropwisely added 5.5 g (0.131 mols) of cyanamide, followed by stirring for two hours. After the reaction, the solvent was removed, and the reaction product was dissolved in acetyl chloride and was refluxed for one hour to cyclize it. The obtained compound was refluxed in an O-dichlorobenzene for one hour to rearrange it into a fulgimide compound (1) mentioned below. By using chloroform and hexane as eluents, this compound was purified by chromatography on the silica gel, and was recrystallized from toluene and isopropyl alcohol in the form of pale-yellow needle crystals maintaining a yield of 15%. The elemental analysis of this compound was C 70.79%, H 5.72%, N 7.15%, O 8.20%, S 8.23%, which was in very good agreement with C 70.74%, H 5.68%, N 7.17%, O 8.19%, S 8.21% that was calculated from C 23 H 22 N 2 O 2 S. Measurement of a proton nuclear magnetic resonance spectrum indicated a peak 2H near δ 7.0 to 7.5 ppm due to proton of a thiophene ring, a peak 1H near δ 3.7 ppm due to proton that is 1.5-shift, and a peak 19H of protons near δ 1.3 to 2.5 ppm due to a cyclopropyl group and a 2-adamantylidene group. Furthermore, measurement of a 13 C-nuclear magnetic resonance spectrum ( 13 C-NMR) indicated a peak near δ 27 to 70 ppm due to carbon of the 2-adamantylidene group, a peak near δ 10.2 ppm due to carbon of the cyclopropyl group, a peak near δ 110 to 160 ppm due to carbon of the thiophene ring, and a peak near δ 160 to 170 ppm due to carbon of a bond >C=O. From the above results, it was confirmed that the product that was isolated was a fulgimide compound (1) represented by the following structural formula, (Example 2) A fulgimide compound of the following structural formula was obtained in the same procedure as in Example 1 but using NH 3 instead of the cyanamide of Example 1. 6.5 Grams (0.015 mols) of this compound was dissolved in tetrahydrofurane, with which metal potassium was reacted at room temperature to obtain 5.4 g of imidopotassium of the following formula, By reacting this compound with 0.79 grams (0.01 mols) of acetyl chloride in dimethylformamide, the following fulgimide compound (2) was obtained. By using chloroform and hexane as eluents, this compound was purified by chromatography on silica gel, and was recrystallized from toluene and isopropyl alcohol in the form of yellow needle crystals maintaining a yield of 42%. The elemental analysis of this compound was C 71.61%, H 6.02%, N 3.36%, O 11.47%, S 7.70%, which was in very good agreement with C 71.57%, H 6.01%, N 3.34%, O 11.44%, S 7.64% that was calculated from C 25 H 25 NO 3 S. Measurement of a proton nuclear magnetic resonance spectrum indicated a peak 2H near δ 7.0 to 8.0 ppm due to aromatic proton, a peak 1H near δ 3.7 ppm due to proton that is 1-5 shift, and a peak 22H near δ 1.0 to 2.2 ppm due to a cyclopropyl group and a 2-adamantylidene group. Furthermore, measurement of a 13 C-nuclear magnetic resonance spectrum ( 13 C-NMR) indicated a peak near δ 27 to 52 ppm due to carbon of the 2-adamantylidene group, a peak near δ 9.7 ppm due to carbon of the cyclopropyl group, a peak near δ 25 to 35 ppm due to carbon of the acetyl group or methyl group, a peak near δ 110 to 160 ppm due to carbon of a thiophene ring and a peak near δ 160 to 170 ppm due to carbon of a bond >C=O. From the above results, it was confirmed that the product that was isolated was a fulgimide compound (2) represented by the following structural formula, (Example 3) 3.3 Grams (0.01 mols) of a fulgimide compound of the following formula, was dissolved in a tetrahydrofuran and was reacted with 1 g of metal potassium at room temperature to obtain 3.0 g of imidopotassium of the following formula, This compound was reacted with 1.41 g (0.01 mols) of benzoyl chloride in dimethylformamide to obtain the following fulgimide compound (3). By using chloroform and hexane as eluents, this compound was purified by chromatography on silica gel, and was recrystallized from toluene and isopropyl alcohol in the form of pale-yellowi sh crystals maintaining a yield of 55%. The elemental analysis of this compound was C 72.40%, H 5.88%, N 3.27%, O 7.15%, S 7.45%, which was in very good agreement with C 72.36%, H 5.84%, N 3.25%, O 11.12%, S 7.43% that was calculated from C 26 H 25 NO 3 S. Measurement of a proton nuclear magnetic resonance spectrum indicated a peak 7H near δ 7.0 to 7.5 ppm due to proton of a thiophene ring and a benzene ring, a peak 1H near δ 3.7 ppm due to proton that is 1-5 shifted,and a peak 19H near δ 1.3 to 2.5 ppm due to protons of a cyclopropyl group and a 2-adamantylidene group. Furthermore, measurement of a 13 C-nuclear magnetic resonance spectrum ( 13 C-NMR) indicated a peak near δ 27 to 70 ppm due to carbon of the 2-adamantylidene group, a peak near δ 10.2 ppm due to carbon of the cyclopropyl group, a peak near δ 110 to 160 ppm due to carbon of a thiophene ring and benzene ring, and a peak near δ 160 to 170 ppm due to carbon of a bond >C=O. From the above results, it was confirmed that the product that was isolated was a fulgimide compound (3) represented by the following structural formula, (Examples 4 to 33) A variety of fulgimide compounds were synthesized using starting materials shown in Table 1 in the same procedure as in Examples 1 to 3. The obtained compounds were subjected to the elemental analysis and were measured for their proton nuclear magnetic resonance spectrum and 13 C-nuclear magnetic resonance spectrum in the same procedure as in Examples 1 to 3. It was confirmed that the compounds were those represented by the structural formulas (4) to (33) shown in Table 1. Table 2 shows elemental analyses of these compounds, values calculated from the structural formulas of the compounds, and characteristic proton nuclear magnetic resonance spectra. (Examples 34 to 66) 0.04 Parts of fulgimide compounds shown in Table 3, 70 parts of tetraethyleneglycol dimethacrylate, 15 parts of triethyleneglycol dimethacrylate, 10 parts of glycidyl methacrylate, 5 parts of 2-hydroethyl methacrylate and 1 part of perbutyl ND as a polymerization catalyst, were sufficiently mixed together until they were completely dissolved. The mixture solution was poured into a mold constituted by a glass plate and a gasket of an ethylene/vinyl acetate copolymer, and its temperature was elevated in an air oven from 35 °C to 90 °C over a period of 20 hours to effect the polymerization. After the polymerization, the polymer was taken out from the glass mold. The obtained polymer plate was irradiated with xenon light by using a Xenon Long-Life Fade Meter FAL-25AX-HC (output: 2.5 KW, source of light: xenon long-life arc lamp) manufactured by Suga Shikenki Co., in order to measure a maximum absorption wavelength in a state of developing color. The initial color tone was observed by eyes, and YI of the samples was measured by using a color-difference meter (Model SM-4) manufactured by Suga Shikenki Co. The wear life (T1/2) was also measured in compliance with JIS L0843 and JIS B7754. T1/2 is defined to be the time until the color density decreases down to one-half the initial value when the polymer plate is irradiated with light by using the fade meter. For the purpose of comparison, the fulgimide compounds represented by the following formulas (A) to (I) were also used to prepare polymer plates to measure their properties in the same procedure as described above. (Examples 67 to 93) Photochromic polymer plates were prepared in the same procedure as in Example 5 but by using fulgimide compounds and chromene compounds shown in Table 4 in amounts shown in Table 4 instead of using fulgimide compounds of Examples 34 to 66. The obtained polymer plates were irradiated with the sun light for 10 minutes and color tone at that moment was observed by eyes. The samples were also measured for their YI by using the color-difference meter (Model SM-4) manufactured by Suga Shikenki Co. The results were as shown in Table 4. The following chromene compounds were used. (Examples 94 to 110) Photochromic polymer plates were prepared in the same procedure as in Examples 67 to 93 but by using fulgimide compounds, chromene compounds and spiro-oxazine compounds shown in Table 5 in amounts shown in Table 5 instead of using fulgimide compounds and chromene compounds of Examples 67 to 93, in order to measure their properties. The following spiro-oxazine were used. (Examples 111 to 120) The fulgimide compounds and chromene compounds shown in Table 5 were mixed in amounts as shown in Table 5 into 100 parts of a polycarbonate resin, so that they were adsorbed on the surfaces of the resin. By using an injection molding machine, the resin was injection molded into a plate having a thickness of 2 mm. The molding was carried out a temperature of 270 °C. The obtained molded plates were evaluated in the same manner as in Examples 67 to 93. The results were as shown in Table 3. It will be understood that throughout, alkyl includes straight or branched alkyl for example, methyl, ethyl, n , propyl, i -propyl, n -butyl, s -butyl and t -butyl. This shall be taken to include alkyl group present as a part of a larger functional group such as alkyl groups in alkoxy, alkoxycarbonyl, alkylcarbonyl, alkylsulfonyl, alkylthio, alkylamino, dialkylamino, alkyleneoxyalkyl, alkoxycarbonylalkyl, and alkylenethioalkyl groups. It will further be understood that cycloalkyl groups may generally contain from 3 to 7, preferably 5, most preferably 6 carbon atoms in the ring.

Claims: A fulgimide compound of the formula (I), wherein: is an aryl group of 6 to 14 carbon atoms, a five-membered or six-membered mono-heterocyclic group comprising at least one heteroatom selected from nitrogen, oxygen and sulfur, or a condensed heterocyclic group comprising a said mono-heterocyclic group fused with a benzene ring or a cyclohexane ring or cyclohexene, and which aryl or heterocyclic group is unsubstituted or substituted by one to three substituents chosen from halogen, nitro, alkylthio of 1 to 4 carbon atoms, aryl of 6 to 10 carbon atoms, alkyl of 1 to 4 carbon atoms and alkoxy of 1 to 4 carbon atoms; is a norbornylidene group, a bicyclo [3,3,1]nonylidene group or an adamantylidene group which is unsubstituted or substituted by one or more substituents chosen from halogen, alkyl of 1 to 4 carbon atoms and alkoxy of 1 to 4 carbon atoms; R 1 is an alkyl group of 1 to 20 carbon atoms, an aryl group of 6 to 14 carbon atoms, a cycloalkyl group of 3 to 7 carbon atoms, or a five-membered or six-membered mono-heterocyclic ring group comprising at least one heteroatom selected from nitrogen, oxygen, and sulfur, and which group R1 may be unsubstituted or substituted by one or more substituents as defined for the group (a); and R 2 is perhalogenoalkyl of 1 to 4 carbon atoms; cyano; alkoxycarbonyl of 2-5 carbon atoms unsubstituted or substituted by one or more substituents chosen from halogen and cyano; alkylcarbonyl of 2-5 carbon atoms unsubstituted or substituted by one or more substituents chosen from halogen and cyano; arylcarbonyl of 7-11 carbon atoms unsubstituted or substituted by one or more substituents chosen from halogen and cyano; nitro; sulfonyl; alkylsulfonyl of 1-4 carbon atoms unsubstituted or substituted by one or more substituents chosen from halogen and cyano; arylsulfonyl of 6-10 carbon atoms unsubstituted or substituted by one or more substituents chosen from halogen and cyano; or aryloxycarbonyl of 7-11 carbon atoms unsubstituted or substituted by one or more substituents chosen from halogen and cyano. A process for preparing a fulgimide compound as claimed in claim 1, which process comprises: (A) reacting an acid anhydride of the formula (II), wherein and R 1 are as defined in claim 1 with an amine of formula (III), H 2 N-R 2 wherein R 2 is as defined in claim 1, followed by cyclization; or (B) reacting an imide compound of the formula (IV) wherein and R 1 are as defined in claim 1, with alkali metal, followed by reaction with a halogen compound of formula (V), A-R 2 wherein R 2 is as defined in claim 1. A photochromic mixture comprising 100 parts by weight of a fulgimide compound as claimed in claim 1 and 0.01 to 10,000 parts by weight of a chromene compound. A mixture according to claim 3, wherein the chromene compound is of formula (VI), wherein R 5 , R 6 , R 7 and R 8 may be the same or different, and each is hydrogen or a hydrocarbon, substituted amino, aromatic hydrocarbon, unsaturated or saturated heterocyclic group which group may be unsubstituted or substituted, or where R 7 and R 8 together form a ring, and the group is an aromatic hydrocarbon or unsaturated heterocyclic group which group may be unsubstituted or substituted. A mixture according to claim 3 or 4 , further comprising 0.01 to 10,000 parts by weight of a spiro-oxazine compound. A mixture according to claim 5, wherein the spiro-oxazine compound is of formula (VII), wherein R 9 , R 10 and R 11 may be the same or different, each is hydrogen, or an alkyl, cycloalkyl, alkoxy, alkyleneoxyalkyl, alkoxycarbonyl, alkoxycarbonylalkyl, aryl, aralkyl, aryloxy, alkylenethioalkyl, acyl, acyloxy or amino group which may be unsubstituted or substituted, the group is an aromatic hydrocarbon or unsaturated heterocyclic group which may be unsubstituted or substituted, the group is an aromatic hydrocarbon or unsaturated heterocyclic group which may be unsubstituted or substituted and the group is an aromatic hydrocarbon or unsaturated heterocyclic group which may be unsubstituted or substituted. A photochromic composition comprising 0.001 to 20 parts by weight of (a) a fulgimide compound as claimed in claim 1 , or (b) a photochromic mixture as claimed in any one of claims 3 to 6, and 100 parts by weight of a polymerizable monomer. A photochromic composition containing 0.001 to 2U parts by weight of (a) a fulgimide compound as claimed in claim 1 , or (b) a photochromic mixture as claimed in any one of claims 3 to 6 , and 100 parts by weight of a thermoplastic resin. A photochromic lens comprising a polymer obtainable by polymerizing a photochromic composition according to claim 7. A photochromic lens comprising a photochromic composition according to claim 8.

Inventors: KOBAYAKAWA TAKASHI, TANIZAWA TSUNEYOSHI, KOBAYAKAWA, TAKASHI, TANIZAWA, TSUNEYOSHI, KOBAYAKAWA, TAKASHI, C/O TOKUYAMA CORP., TANIZAWA, TSUNEYOSHI, C/O TOKUYAMA CORP.
Applicants: TOKUYAMA CORP, TOKUYAMA CORPORATION
Application year: 1995
Main classification: C07D209
IPC codes: C07D491, G03C1, C07D209, C07D487