Tyre

Abstract: A tyre tread comprising an elongated strip of tyre tread compound of high resistivity having a transverse width (TR) characterised by within the transverse width (TR) a longitudinally extending conducting strip (3,6,7) of low resistivity tyre compound with a volume resistivity less than 10⁸ ohm cm said conducting strip extending from the top to the bottom surface of the tread strip.

Description: This invention relates to tyres having treads and in particular treads which are electrically conducting including those reinforced by Silica. The build-up of static electric charge in moving vehicles can have a potentially adverse effect on electronic circuitry and radio reception, as well as being a safety hazard should spark discharge occur during re-fuelling. Personal discomfort also occurs if charge is earthed through a driver or passenger. Charge is normally conducted to earth through the tyres, which requires that the tyres themselves have an acceptable level of conductivity - commonly described as anti-static. Such levels of conductivity are normally guaranteed by the use of tyre compounds containing significant proportions of carbon black as reinforcing filler. Carbon black reduces the resistivity of the intrinsically non-conductive rubber and so provides a leakage path for the static charge from the vehicle to earth. Anti-static rubber compounds generally require a volume resistivity below 10 8 ohm cm, which is usually achievable with approx 50phr or more carbon black in the compound. Such loadings are typical of carbon black-reinforced tyres, which are accordingly anti-static. If non-black fillers (e.g. silica) are used, or if the carbon black loading is significantly less than 50phr, anti-static properties are often not achieved. For example, with silica filler in place of carbon black, the volume resistivity is typically 10 13 ohm cm. Should such a compound be used in the tread of a tyre, for example to achieve a lower rolling resistance, the vehicle will effectively be insulated from the road and static charge will not be able to leak to earth. It is known that electrical conductivity may be improved by the addition of polar ingredients but the effect is generally of insufficient magnitude. Likewise special grades of superconductive carbon blacks may be added but these need to be present in moderately high loadings, e.g. 10-30phr, to be significantly effective, and since their other properties are not suited to tyre applications, road performance may deteriorate. A tyre according to the preamble of claim 1 is known from GB-A-544 757. According to one aspect of the present invention a tyre comprises an elongated main tread strip of high resistivity tread compound having a transverse width TR characterised by a sub-tread disposed in contact with the radially inner surface of the main tread strip and a longitudinally extending conducting strip of low resistivity tyre compound with a volume resistivity of less than 10 8 ohm-cm disposed within the transverse width TR of the main tread strip, the conducting strip extending from the radially outer surface of the main tread strip to its radially inner surface to contact the sub-tread, the sub-tread extending axially over the whole transverse width TR of the main tread strip. By high resistivity is meant tyre tread compounds having a volume resistivity greater than 10 8 ohm cm. Such compounds include for example tyre tread compounds having a silica filler in place of carbon black of which the volume of resistivity is typically 10 13 ohm-cm. Preferably the conducting strip is positioned at the centre of the tyre tread strip. Two or more longitudinally extending conducting strips may be provided. The width of the conducting strip is preferably in the range of 5-25% of the width of the tyre tread TR. The compound of the conducting strip more preferably has a volume resistivity of less than 10 6 ohm cm. Preferably the width of the conducting strip is greater than the width of the widest longitudinally extending tread groove to ensure that the conducting strip may contact the road when the tyre is completed and used on a vehicle. Further aspects of the present invention will become apparent from the following description, by way of example only, of two embodiments in conjunction with the attached diagrammatic drawings in which: Figure 1 is a transverse cross-sectional view of an extruded tyre tread strip according to the present invention; and Figure 2 shows the tyre tread strip of Figure 1 after tyre manufacture. Figure 1 shows the transverse cross-section of a longitudinally extended tyre tread strip comprising a main tyre tread compound region 1 and a tyre sub-tread region 2. This assembly is the standard one where an extruded tread compound strip of the required cross-section is brought into close contact with a flat strip or sheet of sub-tread compound to form a sub-assembly on later tyre manufacture. In this case however the first or main tyre tread strip region 1 is in three parts. Firstly a centre part 3 having a width of 15% of the tyre strip width TR and two main side regions 4. The centre region comprises a rubber compound having a volume resistivity of approximately 10 6 ohm-cm being reinforced by carbon black and having the following formulation. SBR 1712, styrene 23.5%, oil 27.3% 96 BR, 96% 1,4-cls 30 N234 Carbon Black 80 Silica Ultrasil VN3 - TESPT/N330 1:1 (X50-S) - Zinc Oxide 3 Stearic acid 2 Aromatic oil 10 CBS 1.5 DPG - Sulfur 1.5 The side regions 4 are of a rubber compound reinforced by silica having a volume of resistivity approximately 10 13 ohm-cm. The formulation of the side region tread compound is as follows. SBR 1712, styrene 23.5%, oil 27.3% 96 BR, 96% 1,4-cls 30 N234 Carbon Black - Silica Ultrasil VN3 80 TESPT/N330 1:1 (X50-S) 12.8 Zinc Oxide 3 Stearic acid 2 Aromatic oil 10 CBS 1.5 DPG 2 Sulfur 1.5 The tyre tread strip is fitted to tyre a carcass on top of a tread reinforcing breaker in the normal way and the tyre is vulcanised in a tyre curing press where the tyre tread pattern is formed. Figure 2 shows a short section of the tyre tread strip after such vulcanisation in a tyre mould and for simplicity is showing the three longitudinally extending zig-zag grooves as the tyre tread pattern. As can be seen the central region 3 having low resistivity has a large centre groove 5 formed therein but the width of the centre region 3 is such that there is still low resistivity compound at the tyre road contacting surface and the low resistivity material extends to the sub-tread so providing a path for charge to dissipate from the tyre to the road. The two side main grooves 5A do not have this low resistivity material but are formed in the silica, comparatively high resistivity, material. The formulation for the conducting or low volume resistivity components is given purely by way of example only and any of the normal low resistivity formulations known in the art may be used. Likewise the formulation of the non-conducting or high volume resistivity component is given purely by way of example only and any of the high resistivity formulations known in the art may be used. In the resultant tyre the properties of the silica reinforced tyre exist in full measure giving wear, wet grip, ice grip etc according to the silica compound formulation chosen. The disadvantage of silica compounds however in having too high a volume resistivity whereby static charge may be maintained on the vehicle so causing the problems mentioned above is overcome by the conducting paths of the low volume resistivity material provided in the tyre tread strip. A most important advantage of the construction of the present invention however is that the strips of low resistivity material comprise extrudable sections and the tyre tread strip can be manufactured using conventional extrusion techniques bringing the various components together to form a handlable tyre tread strip. The tyre tread strip may be spooled and used in continuous lengths or cut to the required length for each tyre to be manufactured.

Claims: A tyre comprising an elongated main tread strip (1) of high resistivity tread compound having a transverse width TR characterised by a sub-tread (2) disposed in contact with the radially inner surface of the main tread strip (1) and a longitudinally extending conducting strip (3) of low resistivity tyre compound having a volume resistivity of less than 10 8 ohm-cm disposed within the transverse width TR of the main tread strip (1), the conducting strip extending from the radially outer surface of the main tread strip (1) to its radially inner surface to contact the sub-tread (2), the sub-tread (2) extending axially over the whole transverse width TR of the main tread strip (1). A tyre according to claim 1, characterised in that the conducting strip (3) is substantially at the centre of the tread strip. A tyre according to claim 1, characterised in that two or more conducting strips are provided. A tyre according to any of claims 1, 2 or 3, characterised in that the width of the or each conducting strip is in the range of 5 to 25% of the width of the tyre tread. A tyre according to any of claims 1 to 4, characterised in that the conducting strip has a longitudinally extending tread groove formed therein. A tyre according to any of claims 1 to 5, characterised in that the conducting strip has a width greater than the width of the widest longitudinally extending tread groove. A tyre according to any of claims 1 to 6, characterised in that the volume resistivity of the compound of the conducting strip is less than 10 6 ohm cm. A tyre according to any of claims 1 to 7, characterised in that the high resistivity compound comprises silica as the major reinforcement or filler material.

Inventors: POWELL BRIAN DAVID WILLIAM, POWELL, BRIAN DAVID WILLIAM
Applicants: SUMITOMO RUBBER IND, SUMITOMO RUBBER INDUSTRIES LTD.
Application year: 1995
Main classification: B60C19
IPC codes: B60C19, B60C11, B60C1