METHOD FOR TREATING WASTE WATER SLUDGE

Abstract: The invention relates to a method for treating waste water sludge comprising at least one metal originating from a waste water treatment coagulant, and phosphorus and heavy metals in order to recover said at least one metal and phosphorus and to discharge said heavy metals. In this method said waste water sludge is acidified to dissolve metals contained in the sludge thereby yielding an acidified sludge solution containing at least 1 % by weight of at least one metal to be recovered. In a first precipitation stage the pH of said acidified sludge solution is raised to precipitate at least one metal to be recovered as a phosphate, and thereafter the phosphate precipitate is separated, thereby leaving a solution comprising heavy metals. In a second precipitation stage the pH of said solution comprising heavy metals is raised and, if necessary, an appropriate chemical is added to precipitate heavy metals, and thereafter the precipitate is discharged.

Description: METHOD FOR TREATING WASTE WATER SLUDGE The invention relates to a method for treating waste water sludge comprising at least one metal, especially iron and possibly aluminium, originating from a waste water treatment coagulant, and phosphorus and heavy metals in order to recover said at least one metal and phosphorus and to discharge said heavy metals. In particular, the sludge is from a waste water purification process where waste water is chemically- precipitated i.e. by using coagulants containing iron and possibly aluminium. Dumping of the waste water sludge from a waste water purification plant is a major problem. This is partly due to the heavy metal content of the sludge. It is difficult to find suitable places for the waste and as standards rise landfilling is becoming more and more expensive. From this perspective the idea of recycling the waste water sludge is becoming increasingly important. Recycling involves treatment of the sludge to recover coagulant chemicals, particularly iron and aluminium, used in the water purification plant, and phosphorus. The first stage in a waste water purification process of the above kind is precipitation using Fe and possibly Al chemicals and sedimentation which yield a chemical sludge i.e. the precipitation sludge. One possible treatment procedure is first to dewater the sludge to a dry solids content of 15-25 % and then to compost, incinerate or transport the dewatered sludge to a dump. Another possible procedure is to acidify the precipitation sludge to dissolve metals. Insoluble substances are removed by filtering. The dissolved metals and phosphorus in the filtrate are precipitated and a sludge, which will be called a metal sludge, is obtained. The metal sludge contains the iron and aluminium of the used coagulant and, in addition, phosphorus and heavy metals. The procedure can also be performed at an elevated temperature to improve the filterability i.e. the dewatering properties of the sludge. The sludge to be treated can be a pre-precipitation sludge, a simul¬ taneous precipitation sludge, post-precipitation sludge or a mixture thereof. One additional alternative for treating the sludge is hydrolysis where the purpose is to hydrolyse organic material of the sludge into short-chained compounds to be util- ized in later stages of the waste water treatment process, especially as carbon sour in the denitrification stage. During hydrolysis, the metals of the raw sludge dissol in the hydrolysate solution. In the so-called thermal acid hydrolysis the temperatu is 150-160°C, and pH<2, preferably 1-1.5. After the hydrolysis, the insoluble p i.e. the organic sludge is separated, the sludge containing primarily fibres and pos ibly insoluble silicate minerals. The pH of the obtained solution is raised above t neutral level using a base so that the dissolved metals precipitate as hydroxides a phosphates. The precipitated sludge, which will hereinafter be called metal sludge then separated. The metal sludge contains iron and aluminium and also phosphor and heavy metals. The metal sludge can be dissolved in sulphuric acid or possibly in hydrochloric ac and the insoluble substances can be separated by filtering. Acidification nor hydrolysis of sludge is not commonly used in waste water purifi ation. One reason is poor profitability. An additional problem is the metal sludg which has no use. The metal sludge contains heavy metals, which makes the sludge harmful waste for the environment. The applicant has earlier proposed (PCT/FI94/00376) a method for recovering t coagulants and phosphorus from the acidic filtrate obtained by dissolving met sludge in sulphuric acid. The acidic filtrate typically contains at least 1% by weig of Fe. This method involves an extraction step, in which Fe and Al are separate followed by two successive precipitation stages for separating heavy metals a phosphorus. Although this process has given promising results so far, extraction m turn out to be problematic for several reasons. Use of organic solvents is expensiv Also the extraction process contains several steps, which makes the process diffic to control. Clean solutions are required and therefore the organic impurities in t solution must be removed before the extraction step. It has also been found that extra polishing precipitation may be needed after the extraction step to remove t remaining Fe from the solution. An inherent problem in extraction, particularly in t stripping stage, is that the solutions must have a relatively low concentration of F Extraction is not an effective method for concentrated Fe solution. Scott and Horlings have studied the removal of phosphates and metals from sewage sludges (Environmental Science & Technology, vol. 9, no. 9, 1975, pp. 849-855). Most of the metals and phosphorus in anaerobically digested sludges can be extrac¬ ted by acid. The acid extract is neutralized to yield a solid product low in organic material containing mostly iron and aluminium phosphates. By proper control of pH, it is possible to produce two solid products, one containing most of the iron and u inium and one containing most of the heavy metals. The above method cannot be used as such for a metal sludge, which typically has a much higher concentration of iron (and/or aluminium). Selective precipitation works fine in dilute solutions but in concentrated solutions there is a considerable overlap of the pH ranges at which various metals precipitate. Therefore, if the above method were applied to a typical metal sludge, the solid product containing Fe would also contain a considerable amount of heavy metals. The product could not be used as a raw material for coagu¬ lant chemicals. The objective of this invention is to provide a workable process, which solves the sludge problem in a waste water purification plant. The process must be able to re¬ move coagulant metals from solutions with relatively high concentration of iron and possibly aluminium. This objective can be achieved by the present invention, which provides a method for treating waste water sludge comprising at least one metal ori¬ ginating from a waste water treatment coagulant, and phosphorus and heavy metals in order to recover said at least one metal and phosphorus and to discharge said heavy metals, wherein said waste water sludge is acidified to dissolve metals con¬ tained in the sludge, thereby yielding an acidified sludge solution containing at least 1% by weight of at least one metal to be recovered, said method being primarily characterized in that it comprises a first precipitation stage comprising raising the pH of the acidified sludge solution and, if necessary, adding phosphate to precipitate at least one metal to be recovered as a phosphate, and thereafter separating the phos¬ phate precipitate, thereby leaving a solution comprising heavy metals, and a second precipitation stage comprising raising the pH of said solution comprising heavy metals and, if necessary, adding an appropriate chemical to precipitate heavy metals, and thereafter discharging the precipitate. The term "heavy metal" denotes metals of the following group: Cr, Ni, Cu, Zn, Cd, Pb and Hg. Preferably, the waste water sludge to be treated with the method of the present i vention comprises metal sludge obtained by subjecting waste water sludge from waste water treatment plant to acid treatment followed by precipitation and sepa ation of metal sludge from the filtrate. The acidified sludge solution obtained b dissolving metal sludge in an acid typically contains at least 1% and up to 6% b weight of each individual coagulant metal. The method of the invention is an obvious improvement compared to the metho which is based on extraction. Iron and phosphorus is first precipitated as ferric pho phate. This precipitate is processed in the subsequent process steps to produce a fe ric coagulant and a phosphate product. A preferred method of the invention is base on the following three conditions: (a) the precipitation is performed at a sufficientl low pH to provide pure product free of heavy metals, (b) Fe:P ratio is adjusted pri to precipitation and (c) a polishing precipitation of the coagulant metal phosphate i performed after the above precipitation. The method is suitable for solutions wit relatively high concentration of metals and phosphorus. Heavy metals of the metal sludge are separated by precipitation. The amount of th precipitate containing heavy metals is small so that dumping of the sludge is easi so that it does not cause any harm to environment. Preferably, the waste water sludge is prior to the first precipitation stage treated wit an oxidizer, such as hydrogen peroxide, to convert divalent iron to trivalent iron. According to a preferred embodiment, the molar ratio of the metal or metals to be r covered to phosphate is adjusted prior to the first precipitation stage by adding pho phoric acid to the dissolution stage, wherein the waste water sludge is acidified alternatively said molar ratio is adjusted prior to or during the first precipitation stag by adding a phosphate solution obtained from a later stage of the process. Said mol ratio is preferably adjusted to about 1 : 1. The solution obtained in the first precipitation stage can, prior to the second precip tation stage, be subjected to a further precipitation by raising the pH to precipitate further portion of at least one metal to be recovered as a phosphate. This phosphate precipitate can after separation be introduced into the dissolution stage, wherein the waste water sludge is acidified. According to one embodiment the pH in the first precipitation stage is raised to about 2 to 3 to precipitate ferric phosphate. The separated ferric phosphate precipitate can be treated with an alkali hydroxide, such as sodium hydroxide, thereby forming inso¬ luble ferric hydroxide and a solution comprising soluble alkali phosphate, whereafter the ferric hydroxide is separated. According to an other embodiment the pH in the first precipitation stage is raised to about 3 to 4 to precipitate ferric and aluminium phosphates. The separated ferric and aluminium phosphate precipitate can be treated with an alkali hydroxide, such as sodium hydroxide, thereby forming insoluble ferric hydroxide and a solution com¬ prising soluble alkali phosphate and aluminium hydroxide, whereafter the ferrichydr- oxide is separated. The above separated ferric hydroxide, optionally after a treatment with an alkali can be dissolved in hydrochloric acid to yield a ferric chloride solution or in sulphuric acid to yield a ferric sulphate solution or in nitric acid to yield a ferric nitrate sol- ution. These solutions are useful as coagulant chemicals. The above solution comprising soluble alkali phosphate can be subjected to a treat¬ ment to precipitate alkali phosphate, wherafter the precipitated alkali phosphate is separated, thereby leaving a solution comprising phosphate. Said phosphate solution can be used to adjust the molar ratio of the metal or metals to be recovered to phos¬ phate prior to or during the first precipitation stage. An alkaline earth metal hydroxide, such as calcium hydroxide, can be added to the above solution comprising soluble alkali phosphate and aluminium hydroxide to precipitate an alkaline earth metal phosphate complex, such as Ca5(OH)(Pθ4)3, whereafter the precipitate is separated, thereby leaving a solution comprising an al¬ kali aluminate. An acid, such as sulphuric acid, can be added to said solution com¬ prising alkali aluminate to lower the pH to a level, preferably between about 7 and 8, whereat aluminium hydroxide precipitates, whereafter the precipitate is separated. Preferably the second precipitation stage is carried out at a pH of about 7 to 9 in t presence of a heavy metal binder, such as hydrogen sulphide or a sulphide, e. sodium sulphide, sodium hydrogen sulphide or ferrous sulphide. If aluminium present in the second precipitation stage it co-precipitates with the heavy metals. The base used to raise the pH in the first and second precipitation stages is fo example an alkali hydroxide, such as NaOH, ammonia or a magnesium or calciu compound, such as MgO, Mg(OH)2, CaO or Ca(OH)2- The invention is described in more details in the following referring to the enclos drawings in which Fig. 1 shows an acidification process of precipitated sludge as a block diagra Fig. 2 shows a method according to the invention for treating a metal slud obtained from a waste water sludge as a block diagram, Fig. 3 shows the method for processing the ferric phosphate precipitate, Fig. 4 shows an alternative method for treating a metal sludge, Fig. 5 shows a first alternative method for treating the precipitate from the pr cess of Fig. 4, and Fig. 6 shows a second alternative method for treating the precipitate from t process of Fig. 4. Fig. 1 shows diagrammatically processing of a sludge from a waste water treatme plant. The metals in the sludge dissolve in the solution during acidification. The i soluble part i.e. the organic sludge is separated, the organic sludge containi primarily fibres and possibly insoluble silicate minerals. For neutralizing the soluti and precipitation of metals e.g. lime is added to the solution. In the separation sta subsequent to the neutralization stage, the metal sludge is separated. The filtrate led to later stages of the waste water treatment process. According to Fig. 2 the metal sludge is dissolved in sulphuric acid or possibly hydrochloric acid in the dissolving stage. Hydrogen peroxide or an other oxidati agent is added to make sure that iron is in ferric form. If the oxidation agent has be added in some prior stage its addition is not necessary at this stage. It may be neces ary to add phosphoric acid to adjust the Fe:Pθ4 mole ratio to 1.0. Addition of phos¬ phoric acid reduces the need of sulphuric or hydrochloric acid. After dissolution, the remaining insoluble substances are separated by filtering and disposed of. The filtrate contains Fe-phosphate/chloride/sulphate depending on the acids used in the dissolution stage. The filtrate naturally contains dissolved heavy metals and other soluble impurities. Instead of filtering other separation methods like centrifugation can be used as well. In the first precipitation stage, a base like NaOH or NH3 or a Mg/Ca compound is added to the acidic solution and pH is adjusted to about 2 whereat pure FeP04 pre¬ cipitates. The Pθ4^" addition for adjusting the mole ratio to 1 can also take place at this stage by adding Na3P04 solution, which is one end product of this process. The pH regulation is important because at higher pH values heavy metals may co-precipi- tate and reduce the purity of the product. The precipitate (FeP04) obtained is separ¬ ated from the solution and conveyed to further process stages, which will be de¬ scribed later. If the acidic filtrate contains Al and it is desired to separate the same from the solution, this can be carried out by raising the pH by 1 - 2 units i.e. to pH values 3 - 4, whereat AIPO4 precipitates. The pH of the filtrate solution is raised to about 3 to precipitate the remaining FeP04. The purpose of this second precipitation of FePθ4 is to minimize FePθ4 losses and thereby improve the yield of the process. The precipitate is returned to the beginning of the process and combined with the metal sludge. The final stage in the treatment process is the precipitation of heavy metals and alu¬ minium. Sodium sulphide is added to the solution and pH is gradually raised to about 7-9. The pH is raised by using a base like NaOH, NH3, Ca(OH)2, etc. It is also poss¬ ible to use other known heavy metal binders to make precipitation more efficient and to ensure very low concentration of heavy metals in the filtrate. The precipitate containing sulphides and hydroxides of heavy metals and aluminium is separated from the solution. The volume of this hurnful solid waste is small and it can be stored in a safe place. The filtrate water is returned to recycle. Fig. 3 shows the processing of the FePθ4 precipitate. The FePθ4 precipitate is fir dissolved at pH 12 and 60 °C. The pH is adjusted with NaOH. At this pH FeP dissolves and the ferric iron precipitates as Fe(OH)3. The solution is filtrated separate the hydroxide precipitate from the liquid phase, which contains Na3Pθ4 soluble form. On cooling the solution, Na3Pθ4 forms crystals, which are separat from the solution to yield a very pure phosphate product for use as a raw material detergent industry, for example. The basic solution is returned to the beginning of t process i.e. to the stage, in which the FePθ4 precipitate is dissolved in NaOH. The Fe(OH)3 precipitate can be further treated with alkali as shown in Fig. 3. NaO is added to the precipitate and the Fe(OH)3 precipitate is filtered. The purpose of th alkali treatment is to remove any remaining phosphorus from the precipitate. The a kali filtrate is returned to the beginning of the FePθ4 process. The ferric hydroxi precipitate is dissolved in hydrochloric acid to yield a FeCl3 solution or in sulphu acid to yield a Fe2(Sθ4)3~solution. Both of these alternative solutions can be used a coagulant chemical in a water purification plant. It is also possible to use nit acid. Ferric nitrate can be used in special situations wherein nitrogen or oxygen the nitrate is needed. Fig. 4 shows the method of the invention in case the sludge contains a significa amount of aluminium. Precipitation of FePθ4 and AIPO4 take place simultaneous at the pH range 3-4. The precipitate is separated by filtering, the filtrate containi heavy metals. Since all FePθ4 is likely to precipitate at this pH, no additional pr cipitation stage is needed as in Fig. 2. Therefore, the filtrate goes to the subseque step for precipitation of heavy metals from the solution. Sodium sulphide is added the solution and pH is gradually raised to about 7-9. The pH is raised by using a ba like NaOH, NH3, Ca(OH)2, etc. It is also possible to use other known heavy met binders to make precipitation more efficient and to ensure very low concentration heavy metals in the filtrate. The precipitate containing sulphides and hydroxides heavy metal is separated from the solution. The filtrate water can be recycled in t process. Fig. 5 shows a first alternative for further treating the precipitate, which contai bom FePθ4 and AIPO4 to recover Al, Fe, and phosphorus. The precipitate is fir dissolved at pH 12 and 60 °C. The pH is adjusted with NaOH. At this pH, FeP and AIPO4 dissolve and the ferric iron precipitates as Fe(OH)3, whereas Al remains in the solution. The solution is filtrated to separate the hydroxide precipitate from the liquid phase, which contains aluminium and Na3Pθ4 in soluble form. Adding Ca(OH)2 to this solution results in precipitation of calcium phosphate in the form of Ca5(OH)(Pθ4)3, which is separated from the solution in the subsequent filtration step. The filtrate, which contains sodium aluminate, can be used as such or it can be further processed in a manner shown in Fig. 6. Fig. 6 shows a second alternative for further treating the precipitate, which contains both FePθ4 and AJPO4 to recover Al, Fe, and phosphorus. This alternative is the same as that of Fig. 5 except that sulphuric acid is added to the filtrate solution con¬ taining aluminium in soluble form to lower pH to about 7-8. At this pH, Al(OH)3 precipitates. The precipitate is separated by filtration, and it can be used as raw ma¬ terial for an Al-coagulant. The filtrate contains mainly Na2Sθ4. EXAMPLE 1. Metal sludge was acidified and filtrated. A volume of 3 litres of the filtrate was taken for further tests. To oxidize all Fe into ferric form, 60 ml of H2O2 was added in small amounts while mixing the batch on a magnetic mixer. H3PO4 was added to adjust the mole ratio P:Fe to 1. Table 2 shows the chemical analysis of the acidic fil¬ trate before the addition of P. Table 1. Conditions during precipitation and filtration. The precipitate was washed twice. The weight of solid precipitate is the weight of the wet cake. Test Precipitation Wash Solid Filtrate g g pH °C min water ml 1 2.5 60 60 2* 100 104 632 2 2.8 60 60 2*90 78 486 3 2.5 23 60 2*90 107 473 4 2.3 60 60 2*90 82 438 5 2.0 23 30 2* 100 141 621 6 2.0 23 30 2*100 126 654 Six precipitation tests (1...6) were made using the above filtrate with the exceptio that in test 6 the mole ratio P:Fe was intentionally adjusted to 0.8. The tests wer performed in the following way. A 500 ml volume of the filtrate was heated to th desired temperature (see Table 1). While heating the batch, NaOH was graduall added to adjust the pH to the desired value. After reaching the intended temperatur and pH, mixing was continued for 1 h. The solution was then filtered (Buchner filter) and washed with water twice. The wash water was added to the filtrate, whic was then analyzed. The analytical results are presented in Table 2. The precipitation yields are presented in Table 3. The results show clearly that Fe-> precipitates well as FePθ4 in the pH range 2-2.5. Cr and Al co-precipitate less lower pH. Table 2. Chemical analysis of the oxidized acidic filtrate (second column) and th filtrate obtained after the precipitation of FePθ4 in tests 1-6. ) pH in precipitation Table 3 Precipitation yield in tests 1-6. The yield values in Table 3 show that almost a complete recovery of Fe and P was in tests 1-4. The filtrate of test 6 was processed further. A precipitate had formed in the filtrate. The filtrate with the precipitate was filtered with a fibreglass filter. The precipitate on the filter was washed with a small amount of water and dried for 24 h at 50 °C. The dry precipitate constituted 0.1 1% by weight of the original filtrate. The precipi¬ tate was amorphous, and the main component was Fe with a concentration of over 10% as deduced by semiquantitative XRF analysis. The liquid portion was neutral¬ ized from pH 2.05 to 8.9 with lime. A precipitate with a dry weight of 15.57 g was obtained with the following concentration of heavy metals: Cd 3.1 ppm, Cu 130 ppm, Ni 25 ppm, Pb < 10 ppm and Zn 1700 ppm. EXAMPLE 2. A 15 g amount of dry FePθ4 cake (24% Fe, 12% P, 0.0048% Cr) was mixed with 560 g of water. The pH of the suspension was raised from 2.4 to 12 by adding 25.96 g of NaOH (50%). The temperature was maintained all the time (2 h) at 50 °C. The solution was then passed through a filter and the precipitate was washed three times with 20 ml of water. The amount of dry precipitate (ferric hydroxide) was 7.2 g and it had the following analysis: 50% Fe, 2.2% P, 0.01 1% Cr. Based on this analysis the yield of Fe was 100%. A sub-sample of 3.26 g of the filtrate (40.5 g) was taken and diluted with 50 ml water and this was analyzed to contain < 0.0015% Fe, 2.6% P a < 0.0015% Cr. The above filtrate was maintained for several days at about +10°C whereupon yello crystallites were formed. The crystals (3.97 g) were separated from the solution an they were analyzed by XRD. The crystals were pure Na3Pθ4 (< 0.0025% F 10.70% Na). The filtrate contained Na 5.4%, P 1.80% and Cr < 0.0001%. The ferric hydroxide precipitate was further treated with NaOH to remove pho phorus remaining in the precipitate. A 2.4 g amount of the precipitate was graduall added to 9.6 g of water containing 0.105 g NaOH (100%). The pH of the solutio rose to 12.7. The temperature of the batch was maintained at 50 °C for 2 h. T solution was then filtered giving 2.28 g of precipitate with 48.3% Fe and 1.60% P.

Claims: Claims 1. A method for treating waste water sludge comprising at least one metal originating from a waste water treatment coagulant, and phosphorus and heavy metals in order to recover said at least one metal and phosphorus and to discharge said heavy metals, wherein said waste water sludge is acidified to dissolve metals contained in the sludge thereby yielding an acidified sludge solution containing at least 1% by weight of at least one metal to be recovered, characterized in that the method comprises: - a first precipitation stage comprising raising the pH of the acidified sludge solution and, if necessary, adding phosphate to precipitate at least one metal to be recovered as a phosphate, and thereafter separating the phosphate precipitate, thereby leaving a solution comprising heavy metals, and - a second precipitation stage comprising raising the pH of said solution comprising heavy metals and, if necessary, adding an appropriate chemical to precipitate heavy metals, and thereafter discharging the precipitate. 2. A method of claim 1, characterized in that the metal or metals to be recovered comprise either iron or iron and aluminium. 3. A method of claim 2, characterized in that the waste water sludge prior to the first precipitation stage is treated with an oxidizer, such as hydrogen peroxide, to convert divalent iron to trivalent iron. 4. A method of any of the previous claims, characterized in that the molar ratio of the metal or metals to be recovered to phosphate is adjusted prior to the first precipitation stage by adding phosphoric acid to the dissolution stage, wherein the waste water sludge is acidified. 5. A method of any of claims 1 to 3, characterized in that the molar ratio of the metal or metals to be recovered to phosphate is adjusted prior to or during the first precipitation stage by adding a phosphate solution. 6. A method of claim 4 or 5, characterized in that said molar ratio is adjusted to about 1: 1. 7. A method of any of claims 1 to 6, characterized in that the solution obtained the first precipitation stage is prior to the second precipitation stage subjected to further precipitation by raising the pH to precipitate a further portion of at least o metal to be recovered as a phosphate, and thereafter the precipitate is separated. 8. A method of claim 7, characterized in that said separated phosphate precipita is introduced into the dissolution stage, wherein the waste water sludge is acidified. 9. A method of any claims 2 to 8, characterized in that in the first precipitati stage the pH is raised to a level of about 2 to 3 to precipitate ferric phosphate. 10. A method of claim 9, characterized in that the ferric phosphate precipita separated in the first precipitation stage is treated with an alkali hydroxide, such sodium hydroxide, thereby forming insoluble ferric hydroxide and a solution co prising soluble alkali phosphate, whereafter the ferric hydroxide is separated. 11. A method of any of claims 2 to 8, characterized in that in the first precipitati stage the pH is raised to a level of about 3 to 4 to precipitate ferric and aluminiu phosphates. 12. A method of claim 1 1, characterized in that the ferric and aluminium pho phate precipitate separated in the first precipitation stage is treated with an alk hydroxide, such as sodium hydroxide, thereby forming insoluble ferric hydroxi and a solution comprising soluble alkali phosphate and aluminium hydroxid whereafter the ferric hydroxide is separated. 13. A method of claim 10 or 12, characterized in that the separated ferric hyd oxide optionally after a treatment with an alkali is dissolved in hydrochloric acid yield a ferric chloride solution in sulphuric acid to yield a ferric sulphate solution in nitric acid to yield a ferric nitrate solution, said solutions being useful as coagula chemicals. 14. A method of claim 10, characterized in that said solution comprising solub alkali phosphate is subjected to a treatment to precipitate alkali phosphate, wheraft the precipitated alkali phosphate is separated, thereby leaving a solution comprising phosphate. 15. A method of claim 14, characterized in that said solution comprising phos- phate is used to adjust the molar ratio of the metal or metals to be recovered to phosphate prior to or during the first precipitation stage. 16. A method of claim 12, characterized in that an alkaline earth metal hydroxide, such as calcium hydroxide, is added to said solution comprising soluble alkali phos- phate and aluminium hydroxide to precipitate an alkaline earth metal phosphate complex, such as Ca5(OH)(Pθ4)3, whereafter the precipitate is separated thereby leaving a solution comprising an alkali aluminate. 17. A method of claim 16, characterized in that an acid, such as sulphuric acid, is added to said solution comprising alkali aluminate to lower the pH to a level, pref¬ erably between about 7 and 8, whereat aluminium hydroxide precipitates, whereafter the precipitate is separated. 18. A method of any of claims 1 to 9, characterized in that the second precipit- ation stage is carried out at a pH of about 7 to 9 in the presence of a heavy metal binder, such as hydrogen sulphide or a sulphide, e.g. sodium sulphide, sodium hydrogen sulphide or ferrous sulphide. 19. A method of any of the previous claims, characterized in that said waste water sludge comprises metal sludge obtained by subjecting waste water sludge from a waste water treatment plant to acid treatment followed by precipitation and separ¬ ation of metal sludge from the filtrate.

Inventors: JOKINEN SIMO, JOKINEN, SIMO
Applicants: JOKINEN SIMO, KEMIRA CHEMICALS OY, JOKINEN, SIMO
Application year: 1995
Main classification: C02F11
IPC codes: C02F9, C02F11