ANAEROBICALLY CURABLE COMPOSITION

Abstract: An anaerobically curable composition comprising an anaerobically curable base preparation and a fine particulate filler. The particles have an average dimension of less than 1 g/cm<3> while the base preparation comprises an ester of acrylic acid or of an alpha -substituted acrylic acid, a free radical catalyst and an agent to prevent premature curing.

Description: ANAEROBICALLY CURABLE COMPOSITION This invention relates to a sealant composition and to a method of sealing, in particular, pipeline leaks using such a composition. The leakage of gas from gas pipelines is a serious economic and, particularly, environmental problem. The gas leaks through pores in pipeline joints and/or corrosion defects. It is not economic to cure leakage by making an excavation at each joint and applying sealant externally but, despite much effort, no truly effective and economic method has been found of sealing pipelines internally. Hitherto, anaerobic sealants have been used in an endeavour to seal leaks. Anaerobically curing compositions comprise an anaerobic monomer, which is an ethylenically unsaturated compound which polymerises in the absence of oxygen and in the presence of a polymerisation initiator and a ferrous or other suitable metal. As well as the monomer and the initiator, anaerobic compositions normally contain an agent to prevent polymerisation of the composition when in storage. Anaerobically curing compositions based on acrylate or methacrylate systems are well known for sealing porosity in metals (GB 1297103 and GB 1547801). GB 1297103 and GB 1547801 describe compositions containing a major part of a monofunctional methacrylate ester (e.g. lauryl or butyl (methacrylate) and a minor pan of a polyfunctional methacrylate ester (e.g. triethylene glycol di methacrylate). The sealant of GB 1297103 comprises a peroxide initiator and is stabilised by aeration. The sealant of GB 1547801 comprises an inhibitor (e.g. hydroquinone) as well as a catalyst. The compositions described in the two British patents are used in the vacuum impregnation of porous articles. Such anaerobically curing compositions, which are stable in the presence of oxygen (air), penetrate into pores and cracks where they cure in anaerobic conditions to form polymeric material permanently blocking the pores and sealing the cracks. The concept has been more recently extended for sealing leaking flexible pipeline joints by the use of inflatable balloon or bladder devices (EP 0164907) and by direct spraying of leaking joints in gas mains (Anaerobic Spraying - a New South Eastern Development, British Gas, 1 1th January 1990). According to the latter method, leaking joints in gas pipelines are treated by internally spraying anaerobic sealant from a single excavation while the pipeline is carrying gas. Anaerobic spraying of gas pipelines realises considerable savings in excavation, reinstatement and time when a number of locations require treatment. It is possible to treat up to 140m of main from a single excavation in a fraction of the time taken using conventional external sealing techniques. The method results in a reduction in measured leakage but still leaves residual leakage from a pipeline. In anaerobic spraying the anaerobic composition is normally applied to the joint by low pressure "wash" spray which avoids formation of droplets in the gas stream. A large portion of the sprayed material, however, washes down the wall of the pipe and remains in liquid uncured state for a period of from minutes to hours depending on the nature and conditions of the pipe and gas flow. Therefore, conventional anaerobic spraying is not as effective as would be desirable in sealing leaks in the upper portion of pipelines. A representative anaerobic pipeline sealant comprises ethylhexyl methacrylate as the monomer, cu ene hydroperoxide as the polymerisation initiator and p-methoxyphenol as an inhibitor to prevent premature polymerisation. In addition, the sealant normally contains hydroxypropyl methacrylate or another hydroxy functional (meth)acrylate ester. Such a sealant formulation corresponds to the base preparation referred to hereinafter. The present invention provides an anaerobically curable composition comprising an anaerobically curable monomer, a curing initiator, and fine paniculate filler. In one embodiment the particles are closed, gas-containing particles. The gas may be air. In another embodiment the particles have an average particle density of less than lg/cm 3 . Thus, the invention resides in an anaerobically curable preparation characterised by containing such fine paniculate filler. The compositions will usually contain in addition an agent to prevent premature curing and/or a rheology modifier to render the composition pseudoplastic. The invention includes an anaerobically curable composition, comprising: i) an anaerobically curable monomer; ii) a free radical catalyst; iii) an agent to prevent premature curing; iv) hollow inert particles preferably having one or more of the following properties: an average true panicle density of from about 0.02 to 0.6 g/cm 3 ; a cross sectional dimension of from about 5-200 μ ; a minimum % survival of 80 at a pressure of 500 psi (3.5 MPa) over ambient; a minimum volume % which floats in water of 90%; which hollow particles suitably do not promote premature curing of the composition and conveniently are in an amount of from 1-25% by weight of the composition; and v) fumed silica coated with a trimethylsilane or a silicone oil, the coated, fumed silica preferably being in an amount of from 2-15% by weight of the total composition. The inert particles are optionally glass particles or polymer microspheres or other particles having functionally equivalent properties to such glass or polymer particles. The coated fumed silica may be replaced by an alternative material which imparts substantially the same Theological properties and phase stability to the composition. Also provided by the invention is a composition for use as a premix for making a catalysed anaerobic composition whose curing will be initiated upon being placed in an anaerobic environment, comprising an anaerobically curable base preparation and a fine paniculate filler, the particles of which have an average density of less than 1 g/cm 3 , the composition being substantially free of active curing initiator. The composition may be free of any curing initiator or it may contain an inactive curing initiator e.g. one part of a two part initiator. An exemplary two part initiator is a hydroperoxide catalyst and a metal promoter. The invention further provides a method for sealing a wall, usually a pipeline wall, to control or prevent leakage through the wall, comprising applying to the wall a composition of the invention. Additional aspects and embodiments of the invention are stated in the claims. In one aspect, the invention comprises an anaerobic composition comprising a base preparation and a low density filler. The composition preferably contains in additional a rheology modifier. The Base Preparation T e base preparation may in principle be any anaerobically curable preparation compatible with the low density filler and any rheology modifier to form an anaerobically curable composition. Such preparations are well known to those skilled in the an. The base preparation normally comprises an ester of acrylic acid or an α-substituted acrylic acid, especially methacylic acid. A mixture of esters may of course be used. The base preparation preferably contains a hydrocarbyl methacrylate and optionally a hydroxy functional methacrylate. Other monomers may optionally be included to modify the physical and/or chemical properties of the composition. Preferred hydrocarbyl methacrylates useful in the invention are of the formula: Me I CH 2 =C-COOR where R is a hydrocarbon group optionally containing at least 8 and often at least 9 carbon atoms and optionally at least one ether linkage. R is preferably an aliphatic (e.g. alkyl), aromatic and cycloaliphatic group or comprises one of these groups substituted by another thereof, in either case optionally containing at least one ether linkage. Preferably, the hydrocarbon group does not contain more than 14 carbon atoms. More preferred R groups are alkyl groups, especially 8C - 14C alkyl groups, which may be straight chain or branched, such as nonyl, decyl, isodecyl. lauryl or myristyl for example. A suitable hydroxyfunctional methacrylate is hydroxypropyl or hydroxyethyl methacrylate, or another hydroxyalkyl methacrylate. Any hydroxyfunctional methacrylate is preferably wholly or predominantly a monohydroxy compound. Exemplary base preparations contain from 30 to 95% by weight or hydrocarbyl methacrylate and from 5 to 70% by weight of hydroxy functional methacrylate, the percentage total of all the constituents adding up to 100. In a preferred class of embodiments the hydrocarbyl methacrylate: hydroxyfunctional methacrylate weight ratio is 1.25: 1 to 0.75: 1, e.g. about 1:1. Among the other optional monomers which may be included in the base preparation are polyalkylene glycol monomethacrylates, e.g. polypropylene glycol monomethacrylate, which suitably contains an average of 5 propylene residues per molecule and is commonly used as a softener. The content of such other optional monomers is typically no more than 25% of the base preparation. The constituents of the base preparation are not critical to the invention and, in principle, any anaerobically curably preparation may be used. However, the base preparation must be suitable for the intended use of the anaerobic composition. In the case of compositions to be pumped through a tube to the site of application it is preferable that the base preparation be of low viscosity, to facilitate pumping of the composition. Accordingly, the skilled person will select monomer(s) which provide low viscosity, suitable monomers being well known to those familiar with anaerobic sealant technology. It is preferred that the base preparation have a viscosity at 20° not exceeding about 100 cps, more preferably not exceeding about 20 cps. Exemplary preparations have a viscosity of no more than about 15 cps, e.g. about 10 cps. -Low viscosity may be obtained, as l nown, by using relatively low weight monomer, e.g. the preferred hydrocarbyl and hydroxyfunctional esters described above. Oligomeric methacrylate is undesirable. The base preparations when ready for use normally contain a free radical catalyst as curing initiator e.g. cumene hydroperoxide, diisopropylbenzene monohydroperoxide or another hydroperoxide or peroxide. The catalyst promotes anaerobic polymerisation when the composition has penetrated a pore or fissure, for example. Metal on the surface of the pipeline wall will promote hydroperoxide catalysts to decompose and release free radicals to initiate polymerisation. The base preparation may contain a redox initiator system comprising a combination of ingredients which produce an oxidation-reduction reaction resulting in the production of free radicals. Typically, such an initiator system comprises a peroxy compound and a tertiary amine or sulphimide or a hydroperoxide and a metal compound. The second component promotes decomposition of the peroxy or hydroperoxy compound. Activated peroxides may also be used with metal promoters. Suitable peroxy and hydroperoxy compounds are benzoyl peroxide and cumene hydroperoxide. Suitable decomposition promoters are tributyl amine. dimethylparatoluidine. benzoic sulphimide, copper octanoate or copper saccharin salt. Benzoyl peroxide/dimethylparatoluidine initiator systems are preferred. The base preparations also normally contain an agent to prevent premature curing, e.g. curing during storage. The curing prevention agent is not critical to the invention and may be hydroquinone or p-methoxyphenol, for example. If there is no curing prevention agent, the initiator or a component thereof is suitably added to the anaerobically curable composition immediately before use. Additionally or alternatively to an inhibitor, a metal chelator may be used as a stabiliser. If the low density filler contains metal capable of activating the catalyst, it will be essential to include a metal chelator to make a storage-stable composition. Suitable chelators are described in US 4416921 and may be any compound capable of forming coordination compounds with metal ions and compatible with the anaerobically curable composition. One class of chelating agents comprises those wherein all the ligand atoms are nitrogen. Typical examples of chelating agents in this case are dipyridyl, tripyridyl, phenanthroline, l,2-bis(2'-pryridyl-methyleneamino)ethane. Another class of chelating agents comprises those which possess a combination of oxygen and nitrogen ligand atoms, such as characterizes the α- and β-aminocarboxylates. Examples include the soluble carboxylated polyamines. such as the sodium derivatives of polycarboxylated alkylenediamines, e.g. tetra-sodium ethylenediamine tetraacetic acid. Other chelating agents of this type are o-aminophenol and 8-hydroxyquinoline. Another suitable chelator is diphosphonic acid. The proportion of the metal ion chelator in the base preparation is suitably 1 to 1000 ppm by weight of the base preparation, preferably 10 to 500 ppm. The anaerobically polymerisable base preparation may contain other optional ingredients in small quantities, for example other reactive monomers or oligomers, such as diallyl phthalate, or maleate or fumerate esters, for example. The Low Density Filler The low density filler comprises fine particles of low density, by which is meant closed gas-containing particles (e.g. hollow gas filled particles or paiticulate closed cell form) or particles having an average particle density of less than 1 g/cm 3 , preferably of less than 0.9 g/cm 3 and most preferably of no more than about 0.8 g/cm 3 . More usually, the particles have a density of no more than about 0.6 g/cm 3 . The minimum density of the filler particles is not critical but typically amounts to a density of about 0.1 g/cm 3 . Preferably, at least 90% by volume of the filler particles will float in water. The filler functions to reduce the density of the anaerobic composition and modify its flow properties. In particular, it is effective to reduce slumping of the composition under its own weight. The quantity of filler used depends upon the properties desired of the anaerobic composition. The inventor has found that useful compositions can be made using the filler in an amount of from 1-20% by weight of the total composition. More preferably the filler is an amount of from 10-15 wt % for glass spheres. A content of about 1-5 wt % has been found very suitable for elastomeric spheres. If the filler absorbs organic compounds, it must not be used in an amount which absorbs substantially all the base preparation. The filler particles are fine particles which can be suspended in the anaerobic composition and entrained with the composition when it flows. The particle size is not critical and will be selected to achieve the desired properties of the anaerobic composition. A cross- sectional dimension of from 30-200um, more preferably 60-180 μm, has been found suitable. The filler is chosen to be compatible with the anaerobic composition. In particular, it must not cause premature polymerisation of the composition. Filler with excessive metal ions available to the surface is to be avoided. The filler functions to alter the properties of the base preparation during use of the preparation. The filler must therefore retain its low density and its inertness as a curing initiator until the anaerobic composition reaches its site of application. The filler may comprise hollow particles or spheres. In one class of embodiments the filler comprises hollow glass spheres. A suitable glass is sodalime borosilicate glass. If hollow particles are chosen as the filler, they must substantially resist rupturing during normal processing of the anaerobic composition. In cases when the composition is used as a pipeline sealant, the composition may conveniently be pumped along the pipeline . Such pumping subjects the pumped liquid to pressures significantly above ambient. It is thus desirable that hollow particles used in pipeline sealant substantially resist rupturing (e.g. minimum % survival of at least 80) at pressures of up to 300 psi (2 MPa) and preferably the hollow spheres should resist rupturing at pressures up to 1000 psi. One class of suitable glass spheres have an average true particle density of from about 0.1 to 0.6 ± 0.03 g/cm 3 as determined by the method of ASTM D2840 (1984 edition) and a size from about 70 to 180 μm (test method ASTM D1214, 10 g glass spheres: max weight percentage retained 5%); the glass spheres preferably have a minimum % survival of 80 at a test pressure of 300 psi (2 MPa) and more preferably a minimum % survival of 80 at a test pressure of 500 psi (3.5 MPa), % survival suitably being determined in accordance with 3M Test Method TM-2028. In this test method % survival is calculated from the change in density of a sample (mixed with talc) after exposure to dry nitrogen. Such glass spheres are available from 3M United Kingdom pic, 3M House, P.O. Box 1, Bracknell, Berkshire, RG12 IJU, United Kingdom under the trade mark "Scotchlite* Glass Bubbles". Fillers containing metal which would cause premature polymerisation must be treated to reduce to an acceptable level the metal ion concentration available to the base preparation. The treatment may comprise washing, application of a barrier coating or both. Thus, glass spheres may be washed by agitation in strong inorganic acid (e.g. 2M HC1), washed in a chelator (e.g. aqueous phosphonic acid) and finally rinsed in distilled water before being dried. Additionally or alternatively the filler may be coated with silicone oil or another substantially metal-free barrier. Another class of suitable filler comprises hollow thermo-plastic microspheres of density 0.02 to 0.08 g/cm 3 and size between 10 to 40 μm. The type of microspheres based on thermoplastic polymers are highly resistant to rupture when compounded into an anaerobic sealing composition because of their flexible and resilient nature. As an example of an organic filler the plastic microsphere known as EXPANCEL DE may be mentioned. EXPANCEL DE is sold by Boud Marketing Limited. The Rheology Modifier The rheology modifier helps to increase the rheological yield value of the anaerobic composition, i.e. to cause the composition to flow only when a high shear stress is applied. The viscosity of the flowing composition is not increased to the same extent, i.e. the rheology modifier renders the composition pseudoplastic. Pseudoplastic flow behaviour is characterised by a viscosity decrease with an accelerated shear rate or increased shear stress. "Thixotropy" is a term which is properly used to describe a non Newtonian flow behaviour that has a time dependent decrease in viscosity with increasing shear stress and shear rate. The so-called "thixotropic index" of a substance is in fact a viscosity ratio, defined herein as the ratio of viscosity when measured at a speed of 20 φm to the viscosity when measured at 2.5 φm (by a Brookfield viscometer). The index is a measure of pseudoplastic behaviour. The rheology modifier may function to make the composition thixotropic. although this is not necessary. The rheology modifier preferably acts also a phase stabiliser, that is it helps prevent separation of the filler panicles from the liquid phase and maintain a uniform blend. The rheology modifier must be compatible with the other components of the composition. A preferred rheology modifier is fumed silica coated with trimethylsilane. The trimethylsilane coated silica may be prepared, for example, by treating fumed silica with a methylchlorosilane, such as 3 dimethyl dichlorosilane or timethyl chlorosilane, or more preferably with hexamethyldisilazine. A preferred type of hexamethyldisilazine treated fumed silica is Aerosil R812 (TM of Degussa Limited) which is a hydrophobic silica having a BET surface area of 260 ±. 30 m 2 /gm and an ignition loss (2 hours at 1000 degrees °C) of 1-2.5%. Another preferred filler is fumed silica treated with silicone oil, which is available from Degussa Limited under the trade mark Aerosil R202. In one class of embodiments the filler has a specific surface area of at least 140 m 2 /g, e.g. of at least 200 m 2 /g, and optionally of at least 250 m-7g when measured by the method of DIN 66131. Alternatively, there may be used wax-based rheology modifiers. Suitable wax modifiers include low molecular weight such as polyethylene glycol wax with a melting point of about 60°C or low melting point (e.g. less than 100°C) stearic acid esters. Suitable commercial preparations are those sold under the trade marks THIXOMEN and TΗIXOTROL ST. The rheology modifier is incorporated in the composition in an amount suitable to impart the desired rheological properties to the composition. In one class of embodiments the rheology modifier is included in an amount of up to 15% by weight of the total composition and more preferably in an amount not exceeding 10 wt % . Fumed silica coated with timethylsilane or silicone oil is preferably used in an amount of no more than about 10% by weight of the total composition and more preferably in an amount of no more than about 8%, e.g. from 0.5-8 wt %. The Composition The filled, rheological ly modified, anaerobically curable compositions of the invention have a reduced density compared to conventional anaerobic sealant by virtue of the low density filler. The rheological properties are also altered by the rheology modifier, iln the result, the composition behaves like a paste or gel until a relatively high shear stress is applied and resists flowing under its own weight. Preferred compositions have a thixotropic index of at least 4, e.g. about 5. Preferred Theologically modified compositions will not move on a vertical glass plate when in the form of a bead having a height of from 4-8 mm or preferably more, e.g. 12 mm. Preferably the Theologically modified compositions have a viscosity at 20°C of at least 2000 cps, e.g. 2000-5000 cps, when measured at a shear rate of 10 s "1 . The polymer of the cured composition preferably has a low glass transition point of -5°C or below, so that the polymer does not pass through the glass transition point in ordinary use. The Use of the Composition The anaerobic composition is useful for sealing defects in a wall to control or prevent leakage through the wall, by applying the composition thereto. The properties of the composition make it particularly suitable for application to non-horizontal or downward facing wall surfaces, because its low density and, in preferred embodiments, pseudoplastic behaviour help the composition resist flowing or slumping under its own weight. The composition finds particular utility in sealing pipelines, especially fuel gas pipelines. The invention also contemplates the use of the composition to seal water pipelines. Extensive gas loss occurs from iron pipelines, through corrosion defects and imperfections in the joints. The inventive composition is applied to the internal wall of the pipeline in a region containing porosity and/or crack defects. Liquid, possibly containing entrained particles, enters pores or cracks in the pipeline (whether at joints or in a pipe section) where it cures rapidly in the anaerobic conditions obtaining in the pores or cracks. The composition is preferably applied to form a layer of from 0.2 to 10 mm thick, where it cures and forms an impervious polymer lining firmly adhered to the pipe wall. The invention is not limited as to the manner of application of the composition to the wall to be treated. Pipeline sections of lengths of up to 140m may be treated from a single excavation by pumping the composition through a hose at low pressures of up to 1000 psi to an applicator head (using for example a positive displacement pump). An alternative pump type capable of applying greater pressures may be used to pump the composition through longer lengths of hose if the low density filler is capable of withstanding such higher pressures. In practice gear pumps are to be avoided because they may damage the filler panicles. An anaerobic composition containing both a free radical catalyst and a catalyst decomposition promoter will have a short shelf life. It is therefore preferable to use the composition in two-part form by making a premix composition substantially free of catalyst or decomposition promoter (or both) and to add the omitted component(s) shortly before use. A convenient technique is to make a premix to which copper is to be added as promoter and then to pump the premix to the application site through tubing in a region of which there is copper, e.g. a section of copper pipe. The copper may suitably be replaced by an alternative metal. Suitable applicator apparatus is described in GB 2226865. The apparatus described therein comprises a spray carriage movable in the interior of a pipeline. A spray head, located centrally within the pipeline, is mounted on the carriage and is fed with the sealant in a circumferential pattern. Such spray carriages are well known in the art. The spray head may be a conventional head or a spinning cup head, for example. As an alternative to spraying, a layer of sealant may be applied by a "pig", i.e. a somewhat plunger-like device between whose periphery and the pipeline wall a layer of sealant is layer down. Such devices are familiar to those skilled in the art. Exemplary devices are described in GB 2140530, GB 2133497, US 4582551 and GB 2131910. EXAMPLES Example 1 - Preparation of Hollow Glass Spheres Hollow glass spheres [Scotchlite* Glass Bubbles B23/500, having a particle density of 0.23 g/cm 3 and a minimum % survival of 80 at a test pressure of 500 psi (3.5 MPa)] were washed by vigorously shaking equal volumes in a separation funnel with 2 molar HC1. The mixture was allowed to stand for a period before removing the aqueous layer. This procedure was repeated 3 times followed by 2 washes of 0.1 molar diphosphonic acid followed by 3 distilled water washes. The slurry was oven dried before use. Example 2 - Preparation of Anaerobic Composition A base preparation was made comprising: Constituent Pans bv Weight πLauryl methacrylate 40 Hydroxypropyl methacrylate 40 Cumene hydroperoxide 1 Saccharin 1 Polypropyleneglycol monomethacrylate 15 Dimethyl paratoluidine 0.5 Stabiliser and other additives 1 The base preparation had a viscosity of 10 cps and uas blended with the treated glass spheres from Example 1 and with silicone oil-coated fumed silica (Aeorsil R202) as follows: Parts bv Weight Base preparation 80 Coated fumed silica 5 Treated glass spheres 15 The resultant composition had a viscosity of 15,000 cps (Brookfield T, Spindle A, 20°C, 20 φm). A bead 0.8 mm high did not slump on the vertical surface. When polymerised by the addition of small quantities of copper salts the polymer had a density of about 0.6 g/cm 3 and a Shore "A" hardness of 85-90. Polymers of lower modules can be prepared from compositions which yield polymers of lower glass transition temperature. Example 3 A base composition was made comprising: Constituent Parts bv Weight Hydroxypropyl methacrylate 20 Polypropyleneglycol monomethacrylate 35 Hyrdocarbyl methacrylate 31.5 Urethane methacrylate 5 Polymerisable surfactant 5 Saccharin 1 Cumene hyrdoperoxide 1 Dimethyl paratoluidene 0.5 Stabilisers 1 The base preparation had a viscosity of 20 cps and was blended and treated with the following composition: Constituent Parts bv Weight Glass spheres 5.0 (BHL lightweight glass microspheres, grade 23, Boud Marketing Limited) Expanded micro-spheres 1.5 (Expancel 091 -DE 80, Boud Marketing Limited) Coated fumed silica 4.0 (Aerosil R202) Coated fumed silica 1.2 (Aerosil R812) The resultant composition had a viscosity of 6000 cps (Brookfield T, Spindle A, 20°C, 20 φm) and a viscosity of 30,000 cps (Brookfield T, Spindle A, 20°C, 25 φm).

Claims: CLAIMS 1. An anaerobically curable composition, comprising an anaerobically curable base preparation and a fine paniculate filler. ~> A composition of claim 1 in which the particles have an average density of less than 1 g/cm 3 . 3. A composition of claim 1 or claim 2, wherein the base preparation comprises an ester of acrylic acid or of an α-substituted acrylic acid, a free radical catalyst and an agent to prevent premature curing. 4. A composition of claim 3, which further comprises a promoter for the catalyst. 5. A composition of claim 3 or claim 4, wherein the ester is a hydrocarbyl ester of acrylic or methacrylic acid, the hydrocarbyl moiety containing at least 8 carbon atoms and optionally containing at least one ether linkage. 6. A composition of claim 5, wherein the hydrocarbyl moiety is an alkyl group optionally containing an ether linkage. 7. A composition of any of claims 3 to 6, wherein the base preparation further contains hydroxypropyl methacrylate, hydroxyethyl methacrylate or another hydroxy functional methacrylate in an amount of from 5-70% by weight of the base preparation, and optionally one or more additional (meth)acrylate esters in an amount of no more than 45 % by weight of the base preparation, the percentage total of the constituents of the preparation being 100. 8. A composition of any claims 3 to 7, wherein the agent to prevent premature curing comprises a metal ion chelator and/or a free radical quencher. 9. A composition of claim 8, wherein the metal ion chelator comprises diphosphonic acid. 10. A composition of any of claims 1 to 9, wherein the filler particles have an average panicle density of no more than about 0.8 g/cm 3 . 11. A composition of claim 10, wherein the filler panicles have an average particle density of no more than about 0.6 g/cm 3 . 12. A composition of claim 10 or claim 11, wherein the filler particles have an average particle density of at least 0.02 g/cm 3 . 13. A composition of any of claims 1 to 12, wherein the filler particles have a cross sectional dimension of from 5 to 200 μm. 14. A composition of any of claims 1 to 13, wherein at least 90% by volume of the filler particles float in water. 15. A composition of any of claims 1 to 14, wherein the filler particles substantially resist breaking at pressures of up to 300 psi (2MPa) over ambient. 16. A composition of claim 15, wherein the filler particles substantially resist breaking at pressures of up to 500 psi (3.5 MPa) over ambient. 17. A composition of any of claims 1 to 16, wherein the filler comprises hollow particles or paniculate closed cell foam. 18. A composition of claim 17, wherein the filler comprises hollow glass particles or other hollow inorganic particles. 19. A composition of claim 18. wherein the inorganic particles are coated with an inert, substantially metal-free barrier and/or are pretreated to reduce the concentration of metal ions available to the base preparation. 20. A composition of claim 19, wherein the pretreatment includes washing with a strong inorganic acid and washing in phosphonic acid or another metal ion chelator. 21. A composition of any of claims 1 to 20 which further includes a rheology modifier such that the composition possesses pseudoplastic character. 22. A composition of claim 21 , wherein the rheology modifier additionally functions to resist phase separation. 23. A composition of claim 21 or claim 22, a bead of which having a height of 3 mm does not move on a vertical face of a glass plate. 24. A composition of any of claims 21 to 23, wherein the rheology modifier is in an amount of up to 15% by weight of the total composition. 25. A composition of claim 24, wherein the rheology modifier is in an amount of up to 10% by weight of the total composition. 26. A composition of any of claims 20 to 25, wherein the rheology modifier comprises fumed silica coated with a trimethylsilane or with a silicone oil. 27. A composition of claim 26, wherein the coated, fumed silica is in an amount of up to 8% by weight of the total composition. 28. A composition of any of claims 20 to 25, wherein the rheology modifier comprises a low melting point wax. 29. An anaerobically curable composition, comprising: i) an anaerobically curable monomer; ii) a free radical catalyst; iii) an agent to prevent premature curing; iv) hollow inert panicles; and v) fumed silica coated with a trimethylsilane or a silicone oil. 30. A composition of claim 29, wherein the particles have an average particle density of from about 0.02 to 0.6 g/cm 3 . 31. A composition of claim 29 or claim 30, wherein the particles have a cross- sectional dimension of from about 5 to 200 mm. 32. A composition of any one of claims 29 to 31 , wherein the particles have a minimum % survival of 80 at a pressure of 500 psi (3.5 MPa) over ambient. 33. A composition of any one of claims 29 to 32, wherein the particles have a minimum volume % which floats in water of 90%. 34. A composition of any one of claims 29 to 33, wherein the particles do not promote premature curing of the composition. 35. A composition of any one of claims 29 to 34, wherein the particles are in an amount from 0.5 to 20% by weight of the composition. 36. A composition of any one of claims 29 to 35, wherein the coated, fumed silica is in an amount of up to 15% by weight of the total composition. 37. A composition of any one of claims 29 to 36, wherein the hollow inert particles are hollow glass particles. 38. A composition of any one of claims 29 to 37, wherein a bead having a height from 3 to 12 mm does not move on a vertical face of a glass plate. 39. A composition as claimed in any one of claims 29 to 38, wherein the monomer comprises an alkyl methacrylate and optionally one or both of a hydroxylalkyl methacrylate and a polyalkyleneglycol monomethacrylate. 40. A composition as claimed in any one of claims 29 to 39, wherein the catalyst comprises a peroxy or a hydroperoxy compound and optionally a metal salt or other promoter for the catalyst. 41. A composition as claimed in any one of claims 29 to 40, wherein the curing prevention agent comprises phosphonic acid or another metal chelator and optionally a free radical quencher. 42. A modification of a composition of any of claims 29 to 41, wherein the hollow inert particles are hollow glass panicles or other particles possessing substantially functionally equivalent properties to such glass particles. 43. A modification of a composition of any of claims 29 to 42, wherein the coated, fumed silica is replaced by an alternative material which imparts substantially the same rheological properties and phase stability to the composition. 44. A composition for use as a premix for making a catalysed anaerobic composition whose curing will be initiated upon being placed in an anaerobic environment, comprising an anaerobically curable base preparation and a fine paniculate filler, the composition being substantially free of active curing initiator. 45. A composition of claim 44, wherein the particles have an average density of less than 1 g/cm 3 . 46. A composition of claim 44 or claim 45, which contains a free radical catalyst but is substantially free of promoter therefor. 47. A composition of claim 46, wherein the catalyst is a peroxy or hydroxy compound. 48. A composition of claim 44, which is substantially free of free radical catalyst. 49. A composition of any of claims 44 to 48, wherein: i) the base preparation comprises a monomer or monomers as defined in any of claims 3, 5, to 7 or 39 to 41; and/or ii) the composition further includes the specific feature(s) of one or more of claims 3 or 8 to 28. 50. A method for sealing a wall to control or prevent leakage therethrough, comprising applying to the wall an anaerobic composition of any of claims 1 to 49. 51. A method of claim 50, wherein the composition is applied by spraying or by a P-g* 52. A method of claim 50 or claim 51, wherein the wall is a metal pipeline wall to the internal surface of which the composition is applied. 53. A method of any of claims 50 to 52, wherein the composition is applied in a layer of from 0.2 to 10 mm thick. 54. A method of any of claims 50 to 53, which includes combining a free radical catalyst and/or a catalyst promoter with a prebland substantially free of such substance(s) to prepare the anaerobic composition prior to its application to the wall. 55. A method of claim 54, in which the combining step comprises contracting the premix with copper as the preblend flows through tubing. 56. A method of maldng a catalytically active composition of any one of claims 1 to 43, comprising combining a premix as defined in any of claims 43 to 49 with a free radical catalyst and/or a promoter for the catalyst to prepare composition containing catalyst and promoter. 57. A method of claim 56, wherein the combining step is as defined in claim 55. 58. A method of claim 56 or claim 57, which further includes applying the resultant composition to a substrate. 59. An anaerobically curable composition, which preparation optionally is substantially free of active curing initiator, characterised in that it contains fine, closed gas-containing particles. 60. A composition of claim 59, wherein at least 90% by volume of the particles float in water. 61. An anaerobically curable composition substantially as hereinbefore described with reference to the Examples. 62. A method for sealing a wall to control or prevent leakage therethrough substantially as hereinbefore described.

Inventors: COOKE BERNARD, COOKE, BERNARD
Applicants: BRITISH GAS PLC, COOKE BERNARD, COOKE, BERNARD
Application year: 1995
Main classification: C09J4
IPC codes: C08F2, C08F20, C08F220, C08K3, C08L33, C08L101, C09D4, C09J4, C09K3