A method of recording information on a magneto-optical medium

Abstract: A magneto-optical recording medium which is adapted to realize a partial ROM with remarkable facility in providing software. The magneto-optical recording medium comprises a transparent substrate; a volatile magnetic recording layer formed on the transparent substrate and having a Curie temperature approximately equal to or lower than a temperature raisable in a recording/reproducing apparatus of a user; and a nonvolatile magnetic recording layer formed on the volatile magnetic recording layer and having a Curie temperature higher than the temperature raisable in the recording/reproducing apparatus of the user; wherein the nonvolatile magnetic recording layer is not initialized and is retained in a state immediately after manufacture of the medium.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates generally to a magneto-optical recording medium and, more particularly, to a recording medium having both a RAM part recordable, reproducible and erasable by a recording/reproducing apparatus of a user and a ROM part reproducible but not rewritable by such an apparatus. Description of the Related Art The problem of protecting the copyright of computer software is currently arising to be important. From the standpoint to provide such software, a variety of measures have been adopted on media in an attempt to prevent illegal use thereof with unauthorized duplication, and the recent trend generally seems that the software is provided in the form of ROM. In a CD-ROM which is an optical recording medium employed frequently of late due to its advantage that a large amount of information is recordable, the entire plane thereof serves as a read-only area, and discrimination between a regularly distributed medium and an illegally exploited one can be achieved with facility merely by deciding whether writing is possible or not. However, as viewed from the user's standpoint, a CD-ROM is disadvantageous because of its insufficient degree of freedom in practical use due to slow reproduction and nonexistence of a recordable/erasable user area. For this reason, there is currently proposed, in place of the above-described medium, a partial ROM which is a magneto-optical recording medium having both a reproduction-only area and recording/reproduction area. In the conventional partial ROM medium known heretofore, indented pits (ROM pits) are previously formed in a part of a substrate to define an area where changes of the reflectivity are applied as reproduced signals, whereby a partial ROM is achieved. According to this method, provision of read-only software is rendered possible by the technique substantially equal to that for the CD-ROM. Since a substrate of an optical disk is produced by a method of injection-molding a resinous material, a metallic stamper is first required to serve as a master in manufacture of a conventional partial ROM medium. Therefore, in providing new software, it is necessary to produce a stamper where new information has been recorded. Since highly advanced apparatus and techniques are required for producing such a stamper, any software provider having none of adequate equipment needs to request a third party for production of a stamper and a substrate as well when providing a conventional partial ROM medium. And there exists another disadvantage that, in case any inconvenience is found in a stage posterior to start of mass production, it has been impossible heretofore to debug such inconvenience in the conventional partial ROM medium. Also for prevention of copying or duplication of software, it may occasionally be desired to sell a medium with some specific information (such as manufacture number, serial number and so forth) readable by a recording/reproducing apparatus of a user. However, in the conventional partial ROM medium, it has been impossible heretofore to meet such requirements. SUMMARY OF THE INVENTION It is therefore an object of the present invention to provide a method of recording information on an ordinary magneto-optical recording medium, which is capable of executing a write-once nonvolatile recording in addition to the ordinary magneto-optical recording. In accordance with an aspect of the present invention, there is provided a method of recording information on a magneto-optical recording medium including a recording film having a perpendicular magnetization characteristic, comprising the step of: while irradiating a laser beam at a given power to said recording medium, rotating said medium at a peripheral velocity lower than that in forming a rewritable record mark, thereby forming a record mark whose direction of magnetization is uninvertibly changed in accordance with a record data. Preferably, the intensity of the laser beam to be irradiated is increased to be higher than that in forming a rewritable record mark. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a sectional view of a magneto-optical recording medium in a first embodiment of the invention; Fig. 2A graphically shows the waveform obtained by reproducing recorded data on the medium of the first embodiment; Fig. 2B graphically shows the reproduced waveform obtained after an erasing operation; Fig. 2C is similar to Fig. 2B but showing the reprduced waveform when a magnetic field applied thereto is reversed; Fig. 3 graphically shows the relationship between a recording laser power and the C/N of a reproduced waveform obtained at a fixed peripheral velocity; Fig. 4A shows a reproduced waveform obtained by an ordinary magneto-optical recording method; Fig. 4B is similar to Fig. 4A but showing a reproduced waveform obtaned by a recording method of the first embodiment; Fig. 5A shows a reproduced waveform and record mark obtained by the ordinary magneto-optical recording method; Fig. 5B is similar to Fig. 5A but showing a state obtained by the recording method of the first embodiment; DESCRIPTION OF THE PREFERRED EMBODIMENTS Fig. 1 shows an exemplary structure of a magneto-optical disk medium 2B used by a recording method in a first embodiment of the invention. The magneto-optical disk 2B has a laminated structure wherein a SiN protective layer 10, a DyFeCo recording layer 18, a SiN protective layer 14, an Al reflecting layer 16 and a resin coating layer 20 are superposed successively on a polycarbonate substrate 8 where ID signal pits and tracking grooves are formed. This magneto-optical disk 2B is a typical one used in general currently. In an ordinary mode of magneto-optically recording rewritable data, the magneto-optical disk 2B is rotated at a peripheral velocity of 9.0 m/sec, and a recording laser power of 10.5 mW is irradiated to the magneto-optical disk 2B while a recording magnetic field of 300 Oe is applied thereto. Under the conditions including a peripheral velocity of 10 m/sec, a recording laser power of 15.9 mW and a re cording magnetic field of 300 Oe, 8T signals (where T = clock period) modulated by a code (2, 7) RLL were recorded at pit positions with a density of 0.78 µm/mark. Fig. 2A graphically shows the waveform obtained by reproducing such recorded data at a peripheral velocity of 9.0 m/sec and a reproducing laser power of 1.0 mW, with the record track pattern obtained thereat. A magnetization inverted area (hatched area: S-side magnetized portion) is formed on an erased record track, and an area (black area: record mark) with a change of the magnetization characteristics (where the Kerr effect is no further existent due to the loss of perpendicular magnetic anisotropy) is formed in a high-temperature region substantially at the center of the hatched area, so that the reproduced signal waveform becomes a pattern of repeated Ms. Fig. 2B graphically shows the reproduced waveform obtained after an erasing operation on the data-recorded magneto-optical disk under the conditions including a peripheral velocity of 9.0 m/sec, an erasing laser power of 10.5 mW and an erasing magnetic field of 300 Oe, with the record track pattern obtained thereat. It is seen from this graph that the formed record marks are not erased even by such erasing operation, hence verifying proper performance of nonvolatile recording. Fig. 2C graphically shows the reproduced waveform obtained after an erasing operation performed under the same erasing conditions as the above with the exception that the applied magnetic field is directionally inverted, with the record track pattern obtained thereat. It is seen from this graph that the data once recorded is not erased even by inverting the applied magnetic field. Whether any unerasable record mark is formed or not is concerned with the amount of the irradiation energy, so that there exists a mutual relationship between the peripheral velocity of the disk and the recording laser power. Fig. 3 graphically shows the C/N characteristics of the reproduced waveform obtained by first recording the data while setting the peripheral velocity fixedly to 1.0 m/sec and changing the recording laser power, and then performing an erasing operation under the above conditions. Supposing now that the peripheral velocity of the disk is 9.0 m/sec for example, it is impossible to perform nonvolatile recording if the recording laser power is lower than 15.9 mW. However, in case the peripheral velocity of the disk is 1.0 m/sec, nonvolatile recording can be performed with a recording laser power of 12 mW or more. Thus, the lower the peripheral velocity of the disk, the lower the recording laser power required for nonvolatile recording. Figs. 4A and 4B graphically show the reproduced waveforms of 3T signals modulated by a code (2, 7) RLL and recorded at pit positions with a recording density of 0.78 µm/mark by the ordinary magneto-optical recording method and the recording method of this embodiment, respectively. The C/N representing the signal quality is 46 dB in ordinary magneto-optical recording as shown in Fig. 4A but is 41 dB in the recording method of this embodiment as shown in Fig. 4B. However, it is still possible to sufficiently achieve satisfactory reproduction, and properly reproduced signals can be obtained as in an ordinary reproduction mode for magneto-optically recorded signals. The difference between the C/N of the reproduced signal by the ordinary magneto-optical recording method and that of the reproduced signal by the recording method of this embodiment is derived from the fact that, as shown in Figs. 5A and 5B, the amplitude of the reproduced signal obtained by the recording method of this embodiment is approximately 1/2 of the amplitude of the reproduced waveform by the ordinary magneto-optical recording method. In the ordinary recording, the polarization angle becomes +k or -k depending on the direction of magnetization as shown in Fig. 5A. The record mark formed by the method of this embodiment is such that the magnetic Kerr effect is lost in the mark portion and the change of the polarization therein is substantially zero, so that the amplitude of the reproduced waveform is reduced to be approximately 1/2 as shown in Fig. 5B. When the medium portion recorded by the method of this embodiment is reproduced according to a light amount change signal, substantially none of reproduced signal is obtained. It is considered therefore that the recording layer is not crystallized by a recording power which is adequate to perform nonvolatile recording by the method of this embodiment. It is obvious from the above that, in the recording method of this embodiment, nonvolatile data recording is not performed according to a structural change (crystallization or amorphization) of the recording layer but is performed according to a change of the magnetic characteristics of the recording layer. It is further considered that the perpendicular magnetic anisotropy is decreased and the change of the polarization angle based on the magnetic Kerr effect due to the perpendicular magnetization is reduced approximately to zero. Although DyFeCo is selectively employed to compose the recording layer in this embodiment, GdFeCo may be employed as well. Since the method of this embodiment performs nonvolatile recording at a lower peripheral velocity and/or a higher recording laser intensity than those in the ordinary magneto-optical recording, it is also possible to execute a write-once nonvolatile recording function in addition to the ordinary magneto-optical magnetic recording function. Furthermore an exclusive write-once recording layer need not be provided in particular, so that a nonvolatile data recording operation can be performed without the necessity of any specific process on a commercially available ordinary magneto-optical disk medium. As nonvolatile data is recordable merely by changing the peripheral velocity and/or the laser power in the recording mode, the required recording/reproducing system is the same as for rewritable data. Therefore a nonvolatile data recording/reproducing operation can be performed with remarkable simplicity and facility, whereby the nonvolatile data recording area can be set to any desired dimensions.

Claims: A method of recording information on a magneto-optical recording medium including a recording film having a perpendicular magnetization characteristic, comprising the step of: while irradiating a laser beam at a given power to said recording medium, rotating said medium at a peripheral velocity lower than that in forming a rewritable record mark, thereby forming a record mark whose direction of magnetization is uninvertibly changed in accordance with a record data. The method according to claim 1, wherein the intensity of the laser beam to be irradiated is increased to be higher than that in forming a rewritable record mark. A magneto-optical recording medium having nonvolatile recorded date recorded by the method according to claim 1 or 2.

Inventors: IZUMI HARUHIKO, TAGUCHI MASAKAZU, IZUMI, HARUHIKO, TAGUCHI, MASAKAZU, IZUMI, HARUHIKO, C/O FUJITSU LIMITED, TAGUCHI, MASAKAZU, C/O FUJITSU LIMITED
Applicants: FUJITSU LTD, FUJITSU LIMITED
Application year: 1995
Main classification: G11B11
IPC codes: G11B19, G11B11