Ultrasonic welding of metallized plastic

Abstract: A method for ultrasonically welding two plastic parts together. One part (30) has a weld joint feature (23) that is covered with a metal layer (27), and the other plastic part (25) has a complimentary weld joint feature. The two parts are joined together by ultrasonically welding the two weld joint features to each other. A force (40) is applied to the first and second plastic parts prior to the step of welding. The force is substantially in excess of that required to cause the two weld joint features to contact each other. This method creates an ultrasonic welded metallized plastic assembly. Each part of the assembly has a weld joint feature, at least one of which was covered with a metal layer prior to welding. Portions of the each of the two weld joint features are deformed to form a plastic weld joint through the metal coating.

Description: Technical Field This invention relates to a method of producing a composite article according to the precharacterising part of claim 1 and to a composite article according to the precharacterising part of claim 5. Background Ultrasonic welding allows accurate and precise application of energy to selectively melt or weld the desired portions of a plastic assembly. Ultrasonic assembly is suitable for most thermoplastic materials, and is widely used to weld thermoplastic parts in the automotive, packaging, electronic, and consumer industries. In practice, high-frequency (ultrasonic) mechanical vibrations are transmitted by the ultrasonic welding machine to mating plastic parts. At the joint or interface of the two parts, a combination of applied force and surface and/or intermolecular friction increases the temperature until the melting point of the thermoplastic is reached. The ultrasonic energy is then removed and a molecular bond or weld is produced between the two plastic parts. An ultrasonic welding system typically contains a high-frequency power supply (usually 20-40kHz). The high-frequency energy is directed into a horn which is a bar or a metal section, typically of titanium, aluminum, or hardened steel, dimensioned to be resident at the applied frequency. The horn contacts the workpiece and transmits the mechanical vibrations into it. A fixture or nest supports and aligns the two parts to be welded. It is generally made of aluminum or steel, and is sometimes lined with cast urethane or another material that is resilient. Proper joint design is essential for optimum welding results. Factors such as the type of material, part geometry, and requirements of the welded joint must be considered with determining the design. A joint should have a small, uniform initial contact area and some means of alignment to concentrate the ultrasonic energy for rapid localized energy dissipation. An energy director, the most commonly used design, consists of a small triangular bead of material on the part surface to be welded. In one type of weld, a sheer, or interference joint is used to obtain a high-strength hermetic seal. During welding, the interfaces melt and telescope together, producing a weld in the shear mode. Many types of thermoplastic polymers can be welded. Amorphous resins such as polystyrene, acrylonitrile-butadiene-styrene (ABS), polycarbonate, etc., are very energy efficient and are generally preferred for ultrasonic welding. They are characterized by a random molecular arrangement and a broad softening temperature range. This allow the material to flow easily without premature solidification. Resins that have higher levels of crystallinity require higher ultrasonic energy levels because of their highly-ordered molecular structure. Some dissimilar resins can be welded if their glass transition temperatures are similar (typically within about 40°F). And, they have somewhat similar molecular structures. Typical examples are ABS-to-acrylic, polycarbonate-to-acrylic, and polystyrene-to-polyphenyleneoxide. Many other factors, such as moisture content, fillers, and mold release agents, affect the ability to ultrasonically weld thermoplastic materials. Optimum welding typically requires that the plastic parts be dried prior to welding. Fillers are known to inhibit ultrasonic welding when levels of filling exceed 30-35%. Above these levels, strong welds cannot be assured because the joint areas contain insufficient fusible material. Also, fillers such as glass and minerals, can be abrasive and cause excessive horn wear at levels above 35%. Mold release agents lower the material's coefficient of friction and adversely affect the weld. Weld surfaces should preferably be cleaned with suitable cleaners to remove any surface contaminants prior to welding. The conventional wisdom in the art of ultrasonic welding has always indicated that the joint to be welded should be thoroughly cleaned and be free of foreign material. For this reason, it has been difficult and expensive to weld plastic parts that have metal plating on them. Metal plating in the area of the weld joint must be removed in order to assure a proper weld. This requires that plated plastic parts used, for example, as shielded RF shielded housings, must have the platings selectively masked off or removed prior to welding. Clearly it would be an advantageous improvement in the state of the art to be able to weld fully plated plastic parts. From patent publication CH-A-535 643 there is known a method for ultrasonic welding a sphere from two plastic parts, the interior of the sphere having a reflective coating that is a liquid sprayed through a number of nozzles or bores. However, this known method does not disclose a metal coating on the weld joint, nor welding through the metal coating to form the ultrasonic weld joint. Other methods for ultrasonic welding of plastic parts are known from patent publications DE-A-3530039, DE-A-3434687, JP-A-57047615 AND PUBLICATION 'ZENTRAL VERBAND DER ELEKTROTECHNISCHEN INDUSTRIE E.V.: "FUGEN VON FORMTEILEN UND HALBZEUGEN AUS THERMOPLASTISCHEN KUNSTSTOFFEN MIT ULTRASCALL", 1985, FACHVERBAND ELEKTROSCHWEISSG, FRANKFURT, DE XP002050902 12405'. Summary of the Invention Briefly, according to a first aspect of the invention, there is provided a method of producing a composite article by ultrasonically welding two plastic parts together, as claimed in claim 1. In one embodiment of the invention, a force is applied to the first and second plastic parts prior to the step of joining. The force is substantially in excess of that required to cause the two weld joint features to contact each other. In accordance with a second aspect of the invention there is provided a composite article made by the method according to claim 1 and as claimed in claim 5. Particular embodiments of the invention are the subject of the respective dependent claims. Embodiments of the present invention will now be described by way of example with reference to the accompanying drawings, in which: FIG. 1 is a schematic representation of ultrasonic welding in accordance with the invention. FIG. 2 is a cross-sectional view of two metallized plastic parts after welding in accordance with the invention. FIG. 3 is an illustration of the test procedure used to determine the effectiveness of the weld joint. Detailed Description of the Preferred Embodiment While the specification concludes with the claims defining the features of the invention that are regarded as novel, it is believed that the invention will be better understood from a consideration of the following description in conjunction with the drawing figures, in which like reference numerals are carried forward. Referring now to FIG. 1, ultrasonic welding is conventionally carried out as follows: 60 Hz alternating current (AC) line power is transformed to high (ultrasonic) frequency (20-40 KHz) AC power, which in turn is converted to mechanical vibrations of similar ultrasonic frequency through a piezoelectric transducer. These transformations take place in the portion of an ultrasonic welding machine commonly referred to as the generator/converter 10. The mechanical vibrations 12 are transmitted through the booster 15 and weld horn 20 to the plastic parts to be joined 25, 30. This assembly is collectively called the 'stack'. The geometries of the booster 15 and horn 20 define the degree of vibrational amplification which occurs in the stack, thereby defining the vibration 22 applied to the plastic parts 25, 30. The amplitude of vibration largely defines the amount of ultrasonic energy available. The weld horn 20 is custom-designed to mate with the first plastic part 25. The second plastic part 30 is constrained by a custom-designed fixture 35, which also serves to prevent its deformation. The mechanical vibrations 22 cause intermolecular vibration, thus frictional heat, within the plastic parts 25, 30. Through proper weld joint feature design, the intermolecular friction can be maximized locally, thereby selectively melting portions of the plastic parts, thus welding them together. The entire process is conducted under the application of a mechanical force 40 applied in a direction to cause the first plastic part 25 to touch the second plastic part 30, thus ensuring their intimate contact. This force is applied in two stages, one prior to the application of ultrasonic vibration 22, which is called the trigger force, and the second during the application of ultrasonic vibration, called the weld force. The trigger force is substantially in excess of that required to cause the two weld joint features to contact each other, thereby ensuring simultaneous melt initiation along the entire weld interface. Once this force is applied, the introduction of ultrasonic energy begins. The weld force, which is not necessarily identical to the trigger force, defines, to a large extent, the rate at which the two parts are joined. In one embodiment of the invention, the first and second plastic parts 25, 30 were comprised of injection molded test specimens. These test specimens have been referred to as modified I-Beams, and are distinctly different from the standard test specimens being developed by the American Welding Society G-1 Subcommittee on the Joining of Plastics and Composites in that they have an acute portion 23 on at least one area of at least one of the plastic parts. The first and second plastic parts were injection molded from polycarbonate, a thermoplastic material, and then covered with a coating 27 of copper and nickel via an electroless plating process. The plating thickness of the copper was measured to be approximately 1 µm thick. The plating thickness of the nickel was measured to be approximately 0.25 µm thick. Metal coatings in the range of 0.1 µm to 5 µm will be found to be useful, with the exact thickness being a function of the design requirements and the metal selected. However, the coating must not be formed too heavily, or it will be too strong and will not be overcome by the welding forces, thus a good weld joint will not be achieved. Other equivalent means of plating the plastic parts could also be used with success, such as vacuum depositing a coating (sputtering, evaporation, etc.), electroplating, flame spraying, coating with metallized paint, etc. In addition, other metals, such as aluminum, chrome, tin, or titanium may also be used. In contrast to the conventional art, the metal coating 27 is formed over the entire part, and is not selectively removed or masked in the area or the weld joint feature. Prior to welding, the first plastic part 25 was oriented relative to the second plastic part 30 as shown. Appropriate fixturing 35 was used such that the two plastic parts' complementary weld joint features were appropriately aligned. In this representation of the embodiment, the second plastic part 30 contained a weld joint feature having an acute portion 23. The configuration of the weld joint features could also have been reversed between the two plastic parts. The acute portion 23 was found to be useful in creating a weak spot in the metal coating during the welding process. This weak spot aids the welding process by allowing the plastic to flow more readily and form a strong weld to the other plastic part. A trigger force of 245 N was applied to the first plastic part. The amplitude of vibration was 60 µm, and the weld force was set at 267 N. The parts were held together for 0.5 seconds under the application of the selected weld force after the cessation of the ultrasonic energy. Application of these process conditions allowed the complementary weld joint features in the two plastic parts to be locally heated in excess of polycarbonate's melting point. The molten plastic deformed, then resolidified into the weld joint after removal of the ultrasonic energy. Referring now to FIG. 2, after welding, the metal plating 27 is disrupted and has become dispersed throughout the weld joint, allowing the two plastic parts to flow together. Once complete, the process yielded a welded, metallized plastic assembly. Referring now to Fig. 3, the metallized plastic assembly 38 was placed in a fixture on an Instron Universal Testing machine and a force 50, 51 was applied as shown. The force was increased until it caused the two welded parts to be ultimately pulled apart, creating a failure. This testing was conducted in accordance with standard test procedures being developed by the American Welding Society G-1 Subcommittee on the Joining of Plastics and Composites. In short, these test procedures involve the determination of the force required to induce failure in standard welded test specimens as compared to the force required to induce failure in a molded, one-piece test specimen of identical geometry (the control specimen). The results of testing conducted with a variety of plastic parts are as follows: Material Average Strength One-piece, molded polycarbonate control 6352 N Welded, unplated polycarbonate 6325 N Welded, plated polycarbonate 6280 N The above results indicate that a metallized plastic assembly can be effectively created by joining two metal coated plastic parts using ultrasonic welding. An effective weld, equivalent to that obtained with unplated plastic, can be obtained on plastic parts that are completely plated with metal in the weld joint areas. While the preferred embodiments of the invention have been illustrated and described, it will be clear that the invention is not so limited. For example, differing trigger forces, metal platings, plastic compositions and weld joint configurations can be used. These and other modifications, changes, variations, substitutions and equivalents will occur to those skilled in the art without departing from the scope of the present invention as defined by the appended claims.

Claims: A method of producing a composite article, comprising the steps of: providing first (25) and second (30) parts made of thermoplastic material and having a metallised surface (27) and ; joining the first part to the second part by placing the first and second parts together and ultrasonically welding the first and second parts together; characterized in that the first and second parts have complementary shaped formations (23,27) each having a metallised surface at which formations the first and second parts are ultrasonically welded together through their metallised surfaces and wherein the unwelded surfaces of the first and second parts have a metallised coating such that the composite article formed by welding is coated substantially all over with a metallised coating. A method according to claim1 and wherein one of the complementary shaped formations has an acute portion (23). A method according to claim 1 or claim 2 and further comprising the step of: applying a force (40) to the first and second parts substantially in excess of that required to cause the two complementary shaped portions to contact each other prior to and during the step of joining. A method according to any one of the preceding claims and wherein the metallised coating on the first and second parts has a thickness in the range of 0.1µm to 5µm. A composite article made by the method according to claim 1 and comprising: first and second parts (25, 30) made of thermoplastic material and ultrasonically welded together; and characterized in that the first and second parts have been welded at complementary shaped formations (23,27) each having a metallised surface, the welding being through the metallised surfaces, and wherein the unwelded surfaces of the first and second parts have a metallised coating such that the composite article formed by welding is coated substantially all over with a metallised coating. A composite article according to claim 5 and wherein the metallised coating has a thickness in the range of 0.1µm to 5µm. A composite article according to claim 5 or claim 6 and wherein the metal of the metallised coating is selected from copper, nickel, aluminium, chromium, tin and titanium.

Inventors: GUZIK ANDRZEJ T, HUNT STEPHEN D, GUZIK, ANDRZEJ T., HUNT, STEPHEN D.
Applicants: MOTOROLA INC, MOTOROLA, INC.
Application year: 1995
Main classification: B29C65
IPC codes: B29C65