Graphite layer material

Abstract: The present invention provides a graphite layer material to be used as an electrode material which exhibits excellent cell characteristics when used for a secondary cell. The graphite layer material of the present invention comprises highly oriented graphite layers of which a direction of crystalline orientation is adjusted to a planar direction, and an intercalant being inserted between the graphite layers.

Description: The present invention relates to a graphite layer material according to the preamble of claim 1. More particularly, it relates to a graphite layer material which is used for a graphite electrode in a secondary cell. Graphites are important as industrial materials because of their useful characteristics such as excellent heat and chemical resistances, high conductivity, etc., and have been widely used as electrode materials for secondary cells, heating elements, structural materials, gaskets, heat resistant sealing materials and the like. Examples of the conventional graphite to be used for these applications include the followings. (a) Graphite which is mainly composed of natural graphite: It is produced by mixing natural graphite powder or scale with a binder and molding the mixture, followed by sintering. The graphite is not only composed of graphite, but is a mixture of graphite and carbon. (b) Film graphite: It is produced by a so-called "expand process" wherein natural graphite is dipped in a solution mixture of concentrated sulfuric acid and concentrated nitric acid, and is then heated to expand an interlayer gap of the graphite, followed by rinsing to remove acid and subjecting to highpressure press molding to form film graphite. However, this film graphite is inferior to a single crystal graphite in various characteristics, and its film strength is also low. Further, there is a problem in that a large amount of the acid is required for the production and toxic gas (e.g. SOx, NOx, etc.) is generated. Also, there is a problem in that the acid used in the production is not completely removed and the remaining acid exudes when using the graphite to cause metal corrosion. The electrode for a secondary cell using the graphite or carbon is used by bringing lithium into contact with the graphite to form an interlayer compound which is obtained by inserting lithium between layers of the graphite to cause dedoping/doping to take electric current out. In this case, the cell characteristics are largely influenced by the properties of the graphite or carbon electrode and are not always good. Highly oriented graphite has recently been studied as novel graphite. One of them is a so-called "HOPG (Highly Oriented Pyrolytic Graphite)" which is obtained by depositing carbon atom on a substrate using a hydrocarbon gas by a CVD (Chemical Vapor Deposition) process, followed by annealing. The HOPG is one in which the crystal orientation is adjusted to one direction. Another highly oriented pyrogenic graphite which is obtained by a different production process is described in Japanese Laid-Open Patent Publication Nos. 3-75211 and 4-21508. The graphites can be produced in a short time and have a desired size and excellent physical properties approaching those of a homogeneous single crystal without creating problems due to the residual acid as described above in item (b). Regarding a secondary cell using conventional graphite and carbon, the cell characteristics are largely influenced by the properties of the graphite or carbon electrode. The cell is not superior in cell characteristics. It is the object of the present invention to provide a graphite layer material that overcomes the above outlined disadvantages. This object is attained by a graphite layer material as defined in claim 1. Suitably and preferred embodiments of this graphite layer material are described in the subclaims. The advantages of the present invention will become apparent to those skilled in the art from the following description with reference to the accompany drawing. Fig. 1 is a sectional view illustrating a lithium secondary cell using the graphite layer material of one embodiment of the present invention as a graphite electrode material for secondary cell. Fig. 2 is a sectional view illustrating a lithium secondary cell using the graphite layer material of another embodiment of the present invention as a graphite electrode material for secondary cell. It has been found that preferred characteristics can be obtained by using a highly oriented graphite having a crystal orientation adjusted to the planar direction. It has also been found that when an intercalant is inserted between the highly oriented graphite layers, most of the intercalant is inserted in a direction parallel to the direction of crystalline orientation through an interlayer gap at an end surface of the graphite, and a strong carbon skeleton disturbs the insertion of the intercalant from the direction perpendicular to the direction of crystalline orientation. It also becomes clear that it takes a long time to insert the intercalant between the highly oriented graphite layers because the intercalant is inserted between layers from approximately parallel direction to the orientation direction of the crystal. Further it become clear that the intercalant is inserted more rapidly, as it comes close to the end surface of the highly oriented graphite and, further, it takes a longer time to insert the intercalant as it goes away from the end surface and therefore the intercalant is not inserted, uniformly. Furthermore, it become clear that it is difficult to control the amount of the intercalant to be inserted at a desired amount. That is, the present invention provides a graphite layer material which comprises highly oriented graphite layers having a crystal orientation adjusted to the planar direction, with an intercalant being inserted between the graphite layers. The graphite layer material of the present invention comprises an intercalant inserted between highly oriented graphite layers, said layers having a crystal orientation adjusted to the planar direction. The intercalant to be used is preferably a donative intercalant, more preferably at least one selected from the group consisting of chloride and fluoride. It is preferred that the graphite layer material has been microperforated. It is preferred that the highly oriented graphite layer material is obtained by graphitizing polymer film. A preferred polymer film is made from at least one selected from the group consisting of polyoxadiazole, polybenzothiazole, polybenzobisthiazole, polybenzoxazole, polybenzobisoxazole, polyimide, polyamide, polyphenylenebenzoimidazole, polyphenylenebenzimidazole, polythiazole and polyparaphenylenevinylene. It is preferred that the graphitization is conducted by calcining said polymer film at a temperature of not less than 2000 °C. It is preferred that the highly oriented graphite planar material is flexible. A preferred intercalant is at least one selected from the group consisting of Li, K, Rb, Cs, Sr and Ba. Further, it is preferred that the size of the microperforation is 1 to 100 µm. Hereinafter, the present invention will be explained in detail. The highly oriented graphite layer material to be used for the graphite layer material of the present invention has a crystal orientation that is adjusted to the planar direction. Examples thereof include graphite materials obtained by depositing carbon atoms on a substrate by a CVD process using a hydrocarbon gas followed by annealing or graphite materials one which is obtained by graphitizing polymer film. Material obtained by graphitizing polymer film is preferably used because the intercalant can be inserted between the resulting graphite layers rapidly and uniformly. It is more preferred to use polymer film made from at least one selected from the group consisting of polyoxadiazoles (POD), polybenzothiazole (PBT), polybenzobisthiazole (PBBT), polybenzoxazole (PBO), polybenzobisoxazole (PBBO), polyimides (PI), polyamides (PA), polyphenylenebenzimidazole (PBI), polyphenylenebenzbisimidazole (PPBI), polythiazole (PT) and polyparaphenylenevinylene (PPV), because the intercalant can be inserted between the resulting graphite layers, rapidly and uniformly. Polyoxadiazoles include polyparaphenylene-1,3,4-oxadiazole and an isomer thereof. Polyimide include aromatic polyimides represented by the formula (1): wherein R 1 = and R 2 = Polyamide include aromatic polyamides represented by the formula (2): wherein Polyimides and polyamides to be used are not limited to those which have the above structure. The calcining conditions for graphitizing the polymer film are not specifically limited, but are preferably at a temperature of not less than 2000 °C, more preferably about 3000 °C to insert the intercalant between the resulting graphite layers rapidly and uniformly. Calcining is normally conducted in an inert gas. The thickness of the polymer film is preferably not less than 100 µm in order to inhibit the influence gas generated in the process of graphitization by adjusting a treating atmosphere to the atmospheric pressure at the time of calcining. The pressure at the time of calcining varies depending upon a film thickness, but is preferably within a range of 0.1 to 50 kg/cm 2 . When calcining at a maximum temperature of less than 2000 °C, the resulting graphite is hard and brittle and it is likely to become difficult to form an interlayer compound. After calcining, a sheeting treatment may be optionally conducted. The polymer film is graphitized , for example, by cutting the polymer film into pieces having a suitable size, introducing one cut film or a laminate of about 1000 cut films in a calcining furnace and heating to 3000 °C to graphitize the film or laminate. After calcining, the graphitized film or laminate may be optionally subjected to a sheeting treatment as described above. The highly oriented graphite planar material thus obtained may take any form such as film, sheet, plate and the like. Further, it may be flexible or hard with no flexibility. The highly oriented graphite layer material having flexibility is preferred so as to use the graphite layer material of the present invention as the electrode material in an integrated form. When using a film graphite as the electrode material, the thickness of the polymer film is preferably within the range of not more than 400 µm, more preferably 5 to 200 µm. When the thickness of the raw film exceeds 400 µm, the film changes into a degradated state by gas generated from the interior of film in the heat treatment process. It therefore becomes difficult to use it alone as a good quality electrode material. However, the graphite in the degradated state can be a useful electrode material if it is molded into a composite material with a fluorine resin such as polytetrafluoroethylene known as so-called "Teflon". Further, it is also possible to use the graphite by making it powder to mold into a composite material with a fluorine resin. In the case of composite material, the proportion (weight ratio) of the graphite in the fluorine resin is preferably within a range of 50:1 to 2:1. A donative intercalant is suitable and preferred as an electrode for a secondary cell. It is more preferred that the intercalant is at least one selected from the group consisting of chloride and fluoride. As the chloride and fluoride, there can be used chlorides and fluorides of any metal. When the intercalant is at least one selected from the group consisting of Li, K, Rb, Cs, Sr and Ba, the graphite layer material becomes an electrode material exhibiting excellent cell characteristics when used for a secondary cell. Interlayer compounds having a different layer structure can be obtained from the same intercalant substance depending on the reaction conditions. The interlayer compound is formed by interaction between a guest substance (intercalant) that is inserted between graphite layers as a host. The highly oriented graphite layer material is processed so that it has microperforations on its surface. By having the microperforation on the surface of the layer material, the intercalant can be inserted between the graphite layers rapidly and uniformly since the amount of the intercalant to be inserted is controlled. This leads to excellent cell characteristics when using the graphite layer material for the secondary cell. The method for providing the microperforation on the surface of the layer material is not specifically limited, for example,the microperforation may be created by subjecting the layer material to a perforation treatment using a press or a laser beam. The shape of the microperforation is not specifically limited, and it takes any form such as a circle ellipse, polygon and the like. The size of the microperforation is not specifically limited; for example, it is 1 to 100 µm. When the size is within this range, it becomes possible to precisely control the amount of the intercalant to be inserted and the intercalant is inserted between the layers of the highly oriented graphite more rapidly and uniformly. The size of the microperforation is preferably 2 to 50 µm, more preferably 5 to 20 µm microperforation may be arranged on the surface of the layer material regularly or irregularly. However to control the amount of the intercalant to be inserted, it is preferred that microperforation is arranged regularly in order to insert the intercalant between the graphite layers, uniformly. The method for inserting the intercalant between the graphite layers through the microperforation on the surface of the highly oriented graphite layer material is not specifically limited. Examples thereof include the vapor phase constant pressure reaction process, the liquid phase contact process, solid phase pressure process, the solvent process and the like. The intercalant is diffused between the graphite layers by an action such as capillary action through the microperforation on the surface of the highly oriented graphite layer material. Thus, by controlling the amount of the intercalant to be inserted, the intercalant can be inserted between the graphite layers rapidly and uniformly. As described above, a strong carbon skeleton does not disturb the insertion of the intercalant from the direction perpendicular to the direction of crystalline orientation and, therefore, the intercalant can be inserted between layers of the graphite from the direction perpendicular to the orientation of the crystal through the microperforation. Not only the intercalant is inserted between layers through the microperforation, but also it is sometimes inserted in the direction parallel to the crystal orientation through an interlayer gap between layers at the end surface of the graphite. The graphite layer material obtained by inserting the intercalant between graphite layers of the highly oriented graphite planar material thus obtained may be subjected to a dedoping treatment. The method for conducting the dedoping process is not specifically limited, for example, there can be used a method for conducting a heat treatment by washing with water or water vapor at elevated temperature. The graphite interlayer compound changes into the state where the interaction between layers is deteriorated by subjecting to the dedoping treatment, and excellent cell characteristics can be exhibited when using the graphite layer material as a cell material. The graphite layer material obtained according to the present invention is preferably used as an electrode material of a positive electrode of the secondary cell using particularly lithium as a negative electrode. The graphite layer material of the present invention can exhibit doping and dedoping actions, thereby exhibiting excellent cell characteristics, because the intercalant is inserted between layers of the highly oriented graphite layer material of which the crystal orientation is adjusted to the planar direction. Further, since the microperforation is provided on the surface of the highly oriented graphite planar material wherein the crystal orientation is adjusted to the planar direction, the intercalant can be inserted between layers through the microperforation. As described above, the graphite layer material of the present invention can be used as an electrode material exhibiting excellent cell characteristics when using for a secondary cell, because it comprises a highly oriented graphite layer material having a crystal orientation adjusted to a planar direction and an intercalant inserted between the graphite layers. It can be preferably used as an electrode for a secondary cell when the intercalant is a donative intercalant. It is more preferred that the intercalant is at least one sort selected from the group consisting of chloride and fluoride. When the highly oriented graphite planar material is provided with a microperforation there can be provided a graphite layer material exhibiting excellent cell characteristics when using it for a secondary cell by inserting an intercalant between layers of the highly oriented graphite rapidly and uniformly to control the amount of the intercalant to be inserted. When the highly oriented graphite planar material is obtained by graphitizing polymer film, a donative intercalant can be inserted between layers of the graphite more rapidly and uniformly. When the polymer film is made from at least one selected from the group consisting of polyoxadiazole, polybenzothiazole, polybenzobisthiazole, polybenzoxazole, polybenzobisoxazole, polyimide, polyamide, polyphenylenebenzoimidazole, polyphenylenebenzbisimidazole, polythiazole and polyparaphenylenevinylene and the graphitization is conducted by calcining at a temperature of not less than 2000°C, a donative intercalant can be inserted between layers of the graphite, more rapidly and uniformly. When the highly oriented graphite planar material is flexible, it becomes possible to use the graphite layer material of the present invention as an electrode material in an integrated form. When the intercalant is at least one sort selected from the group consisting of Li, K, Rb, Cs, Sr and Ba, it becomes an electrode material exhibiting excellent cell characteristics when using it for a secondary cell. When the size of the fine pore is 1 to 100 µm, it becomes possible to insert an intercalant between layers of the graphite more rapidly and uniformly to precisely control the amount of the intercalant to be inserted. EXAMPLES The following Examples and Comparative Examples further illustrate the present invention in detail but are not to be construed to limit the scope thereof. Example 1 A polyparaphenylene-1,3,4-oxadiazole film having a thickness of 50 µm was subjected to a preliminary heat treatment by heating it to 1000 °C at a rate of 10 °C/minute in a nitrogen gas using an electric furnace (model LTF-8, manufactured by Sankyo Denro Co. Ltd.) and maintaining it at 1000 °C for one hour. Then the resulting carbonaceous film was set stretchably in a graphite cylindrical container and heated at a rate of 20 °C/minute using an ultrahigh temperature furnace (model 46-5, manufactured by Shinsei Denro Co. Ltd.). The film was calcined so that the maximum temperature was 2000, 2500 and 3000 °C, respectively, to obtain three graphites. For comparison, a graphite (Comparative Example) was obtained by calcining at a maximum temperature of 1800 °C which is lower than 2000°C. The calcining was conducted in an argon gas under pressure (0.2 kg/cm 2 ). The graphitized film thus obtained exhibited flexibility. After this film was set in a pyrex glass container so that it could contact directly with lithium metal and sodium metal, the container was sealed under vacuum and subjected to a heat treatment at 150 °C. A regular micro (10 µm) was achieved on the surface of a separate graphitized film having flexibility obtained above, by means of a press. After the film having the microperforation was set in a pyrex glass container so that it could contact directly with lithium metal and sodium metal, the container was sealed under vacuum and subjected to a heat treatment at 150 °C. In the case of a graphite calcined at a temperature of not less than 2000 °C in the respective Examples, an interlayer compound at the second stage could be obtained. However, in the case of a graphite calcined at 1800 °C in the Comparative Example, no interlayer compound could be obtained. A lithium secondary cell of a structure as shown in Fig. 1 was prepared by using the resulting graphite layer material as a positive electrode 1 of an electrode material and subjecting the positive electrode to pressure molding in an inert gas, together with a polypropylene separator 3 having a porous structure and a lithium metal as a negative electrode 2 . As an electrolyte solution, a solution comprising propylene carbonate containing lithium perchlorate and 1,2-dimethoxyethane is used. This secondary cell has excellent charging/discharging characteristics. On the other hand, in case of a graphite of the Comparative Example, no satisfactory characteristics were obtained because no interlayer compound was formed. Further, the calcining temperature and charging/discharging characteristics are mutually related. The higher the calcining temperature, the more the characteristics were improved. It became clear that the characteristics are improved when the microperforation exists. Example 2 The graphite layer material of Example 1 as the electrode material was allowed to stand in air for 24 hours, subjected to a dedoping treatment by treating with boiling distilled water and then dried before subjecting it to pressure molding in an inert gas together with polypropylene having a porous structure and lithium metal. Then, according to the same manner as that described in Example 1, a secondary cell was prepared and the charging/discharging characteristics of the secondary cell were examined. The secondary cell of Example 2 had excellent charging/discharging characteristics, similar to Example 1. On the other hand, in case of graphite of the Comparative Example, no satisfactory characteristics were obtained because no interlayer compound was formed. Further, the calcining temperature and charging/discharging characteristics are mutually related. The higher the calcining temperature, the more the characteristics were improved. It became clear that the characteristics are improved when the microperforation exists. Example 3 According to the same manner as that described in Example 1 except that a laminate of one thousand polyparaphenylene-1,3,4-oxadiazole films having a thickness of 50 µm was calcined, a graphitized plate was obtained. This plate had a flexibility. Then, according to the same manner as that described in Example 1, a secondary cell as shown in Fig. 2 was prepared and the charging/discharging characteristics of the secondary cell were examined. The secondary cell of Example 3 had excellent charging/discharging characteristics, similar to Example 1. Further, the calcining temperature and charging/discharging characteristics are mutually related. The higher the calcining temperature, the more the characteristics were improved. Further, a regular microperforation (10 µm) was created on the surface of the graphitized plate having a flexibility obtained above by using a laser beam. Then, according to the same manner as that described in Example 1, a secondary cell as shown in Fig. 2 was prepared and the charging/discharging characteristics of the secondary cell were examined. The secondary cell of Example 3 had excellent charging/discharging characteristics, similar to Example 1. Further, the calcining temperature and charging/discharging characteristics are mutually related. The higher the calcining temperature, the more the characteristics were improved. Example 4 According to the same manner as that described above except that polyimide films (Capton H film, manufactured by Du Pont Co.) having a thickness of 125, 25, 50 and 75 µm were used, respectively, and the maximum temperature at the time of calcining was 2800 °C, a graphitized interlayer compound was prepared, respectively. Further, it was subjected to a dedoping treatment and the cell characteristics were examined according to the same manner as that described above. As a result, any film exhibited excellent cell characteristics, similar to Example 1. Example 5 According to the same manner as that described above except that respective films (PI, POD, PBT, PBBT, PBO, PBBO, PPA, PBI, PPBI, PT and PPV) having a thickness of 50 µm was used and calcined at the maximum temperature of 3000 °C under pressure of 2.0 kg/cm 2 and, at the same time, potassium was inserted between layers using a vapor phase constant pressure reaction process (Two-buib process), a graphitized interlayer compound was formed, respectively. Further, it was subjected to a dedoping treatment and the cell characteristics were examined according to the same manner as that described above. As a result, any film exhibited excellent cell characteristics, similar to Example 1. Incidentally, the potassium-side temperature and graphite-side temperature were set at 250 and 300 °C, respectively when an interlayer compound is formed to obtain an interlayer compound at the first stage. Example 6 According to the same manner as that described in Example 1, POD and PI films having a thickness of 400 µm were subjected to a heat treatment. Although the films are in the degradated state, a graphite interlayer compound was obtained according to the same manner as that described in Example 1. Further, the compound was subjected to a dedoping treatment to prepare a composite material of a graphite material and Teflon®. The weight ratio of the graphite material to Teflon® was 10:1. Then, the cell characteristics were examined according to the same manner as that described in Example 1. As a result, the resulting cell exhibited excellent cell characteristics.

Claims: A graphite layer material comprising highly oriented graphite layers having a crystal orientation adjusted to the planar direction, wherein an intercalant is inserted between the graphite layers, charcaterized in that said graphite layer material has been microperforated. The graphite layer material of claim 1, wherein said intercalant is donative. The graphite layer material of claim 1 or 2, wherein said intercalant is at least one selected from the group consisting of chlorides and fluorides. The graphite layer material of any one of claims 1 to 3, wherein said graphite layers have been obtained by graphitizing polymer film. The graphite layer material of claim 4, wherein said polymer film is made from at least one selected from the group consisting of polyoxadiazole, polybenzothiazole, polybenzobisthiazole, polybenzoxazole, polybenzobisoxazole, polyimide, polyamide, polyphenylenebenzoimidazole, polyphenylenebenzimidazole, polythiazole and polyparaphenylenevinylene. The graphite layer material of claim 4 or 5, wherein the graphitization has been conducted by calcining said polymer film at a temperature of not less than 2000 °C. The graphite layer material of any one of claims 1 to 6, wherein said highly oriented graphite layers are flexible. The graphite layer material of any one of claims 1 to 8, wherein said intercalant is at least one selected from the group consisting of Li, K, Rb, Cs, Sr and Ba. The graphite layer material of any of claims 1 to 8, wherein said microperforations has a diameter of 1 to 100 µm.

Inventors: IKEDA JUNJI, INOUE TAKAO, NISHIKI NAOMI, IKEDA, JUNJI, INOUE, TAKAO, NISHIKI, NAOMI
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1995
Main classification: H01M4
IPC codes: C01B31, H01M4, H01M10