Oriented film

Abstract: An oriented thermoplastic film, comprising at least one layer comprising a thermoplastic polyolefin (TPO) exhibits improved memory properties compared with conventional PVC and shrink films. The films are preferably heat shrinkable, and may be multilayer films comprising a thermoplastic polyolefin (TPO) layer as a core layer.

Description: BACKGROUND OF THE INVENTION The present invention relates to thermoplastic films, more particularly to packaging films, especially films useful in packaging food products such as poultry. In the packaging of products, especially food products such as poultry, PVC (polyvinyl chloride) has been a traditional packaging material. PVC suffers from several deficiencies, including environmental concerns about possible migration of vinyl chloride monomer residuals, as well as plasticizer, into a food product packaged with PVC. PVC sometimes has lower abuse resistance and poorer memory than alternative packaging materials. More recently, olefinic materials such as SSD film and SES film provided by the Cryovac Division of W.R. Grace & Co.-Conn. have proven useful in packaging poultry. These olefinic materials have excellent physical properties, including good memory. By "memory" is meant the propensity of the packaging material, after being stretched over for example a trayed food product, to substantially return to its original dimensions after product settling. Also, it refers to the tightness of the trayed package during storage and distribution. Films with poor memory tend to show slackness or looseness in the packaging film overwrap of a trayed food package. It is desirable, especially when packaging "high profile" foods, i.e. foods that project above the edge of the tray, such as whole poultry, or poultry parts, to have films with even better memory. This would then allow for product settling while still substantially maintaining the tight package appearance. Flexible stretch/shrink films are disclosed in EP-A-0286430. The films comprise a core layer of very low density polyethylene, two adjacent intermediate layers of liner low density polyethylene and two outer layers of ethylene vinyl acetate or very low density polyethylene. SUMMARY OF THE INVENTION The present invention provides an oriented heat shrinkable thermoplastic coextruded multilayer film, comprising: a) a core layer comprising thermoplastic polyolefin (TPO) which comprises a continuous phase of isotactic polypropylene and a dispersed phase of ethylene propylene rubber; b) intermediate layers, adjacent each side of the core layer, comprising a polymeric adhesive; and c) two outer layers each bonded to a respective intermediate layer, comprising a polymeric material selected from; i) ethylene alpha olefin copolymer; ii) ethylene unsaturated ester copolymer; iii) ethylene acid copolymer; and iv) blends thereof. BRIEF DESCRIPTION OF THE DRAWINGS The invention may be further understood with reference to the drawings in which: FIG. 1 discloses a schematic cross section of a film in accordance with the invention; and DESCRIPTION OF THE PREFERRED EMBODIMENTS Referring to Fig. 1, an oriented film 10 of the present invention comprises a core layer 12, surface layers 14 and 16 and intermediate layers 18 and 20. The core layer 12 comprises a thermoplastic polyolefin (TPO). "Thermoplastic polyolefin" or "TPO" refers to a rubber modified isotactic polypropylene in which the "rubber" is a high ethylene content propylene-ethylene copolymer. A TPO may alternatively be defined as an impact modified polypropylene. These materials are typically made by melt compounding or, more recently by in-reactor polymerization ("reactor grade"). Commercial examples include those identified in Table 1 herein, as well as Adpro TM available from Genesis. The surface layers 14 and 16 are preferably of substantially the same composition. They preferably comprise an ethylene alpha olefin copolymer, an ethylene unsaturated ester copolymer, an ethylene acid copolymer, or any combination or blend thereof. Ethylene alpha olefin copolymers are preferably copolymers of ethylene with one or more comonomers selected from C 3 to C 10 alpha olefins. Both heterogeneous and homogeneous materials can be used. Examples of heterogeneous materials include LLDPE (linear low density polyethylene), VLDPE (very low density polyethylene), ULDPE (ultra low density polyethylene), and the like. Homogeneous materials can include metallocene catalyzed polymers (MCP) such as those available from Exxon under the EXACT trademark, and available from Dow under the AFFINITY trademark. Ethylene unsaturated ester copolymer refers to materials such as ethylene vinyl acetate copolymer (EVA), ethylene alkyl acrylate copolymers such as ethylene ethyl acrylate copolymer (EEA), ethylene methyl acrylate copolymer (EMA), and ethylene n-butyl acrylate copolymer (EnBA). It also refers to ethylene methyl methacrylate copolymer (EMMA). Ethylene acid copolymer refers to materials such as ethylene acrylic acid copolymer (EAA), and ethylene methacrylic acid copolymer (EMAA). Metal salt neutralized or partially neutralized versions of these materials, such as ionomer, are also included herein. Intermediate layers 18 and 20 can comprise any of the same materials as those disclosed for surface layers 14 and 16. They can also comprise a polymeric adhesive, such as acid or acid anhydride modified olefinic polymers or copolymers. These adhesive materials are available from DuPont under the Bynel trademark, from Mitsui under the Admer trademark, and from Quantum under the Plexar trademark. EXAMPLES Three films with thermoplastic polyolefin (TPO) cores were compared to each other and to a control film in a package tightness/looseness test. The results show all three had better tightness retention over the course of the study than the control. Example 3 had the highest mean score for tightness. The control film was the SES 320 film made by Cryovac Division of W.R. Grace & Co.-Conn. A "Package Tightness/Looseness Scoring Key" was developed by photographing tray overwrap packages of split breast chicken with varying levels of film tightness/looseness. The photographs were scored 1 to 5 with 1 being a very loose package and 5 being a very tight package. A photograph of a puffy package, where the film is domed above the chicken, was also included and scored "P". Chicken split breasts were put up in #6 trays on an Ossid 750 packaging machine using the four different films. Four packages of chicken were made with each film. The packages were shrunk in a hot air tunnel and then in a hot water tunnel. One package of each film was placed in the bottom of four boxes, and three layers of #6 trays containing two water bags each were piled on top of the chicken. The chicken was stored in a cooler for three days. Packages were then put in a refrigerated display case and coded for sensory evaluation. Ten panelists were asked to score each package for tightness/looseness with a number 1 to 5 corresponding to the photographs in the scoring key. Panelists were also instructed to mark a "P" for puffy next to the numerical score if necessary. The data was then entered into a program for statistical analysis of the different films' scores. RESULTS: Each of Examples 1-3 were significantly tighter than the control. Example 3 was significantly tighter than Example 2, but Example 1 was not significantly different from either Example 2 or Example 3. No one film scored significantly more "P"s for puffiness than any other film. The results are shown in Table 3. Table 1 identifies the polymers present in each of Examples 1-3 and the control. Table 2 identifies the structure of each of Examples 1-3 and the control. RESIN TRADENAME SOURCE TPO 1 Exxtral R 200.01 Exxon TPO 2 PPTR 134 Quantum TPO 3 KS-081 P Himont EAO 1 Dowlex 2045.04 Dow EAO 2 Dowlex 2037 Dow EUE 1 PE 1335 Rexene AB Kaopolite SF Kaopolite AB = antiblock; the Kaopolite SF is an anhydrous aluminum silicate; EAO 1 is an ethylene/octene copolymer with a density of 0.920 grams/cm 3 ; EAO 2 is an ethylene/octene copolymer with a density of 0.935 grams/cm -1 ; and EUE 1 is an ethylene vinyl acetate copolymer with a vinyl acetate content of 3.3%. EXAMPLE PACKAGE TIGHTNESS Control 2.5 1 3.5 2 3.2 3 3.9 Another film made in accordance with the present invention, and similar to the films of examples 1 to 3, showed memory characteristics superior to PVC. Those skilled in the art will understand that modifications to the present invention can be made after review of the disclosure. Such modifications are deemed to be within the scope of the invention as claimed. For example, although five-layer embodiments are disclosed, those in the art will readily understand that six, or more layers can be assembled into a multilayer film having the benefits described, when the TPO material is used. The examples were made by a tubular cast coextrusion process, well known in the art. However, flat cast coextrusion can also employed. These alternative processes are well known in the art. The examples were made by irradiating the extruded material prior to orientation. Films of the invention can be crosslinked by conventional means such as electronic or chemical crosslinking. Alternatively, the film can be post-irradiated, i.e. irradiated after orientation. Films of the present invention can also be made without. crosslinking. Orientation is accomplished by conventional means such as blown bubble or tenterframe. Orientation ratios can be at any suitable range or ratio, including 1:1 to 6:1 in either or both of the machine and transverse directions. Although the sample packages were made on an Ossid 750 machine, other equipment, including overwrap machines such as the Ossid 500 and the Ilapak Delta P machines, can also be used in combination with the film of the present invention. The films of the examples had a final thickness of about 60 gauge or 15µm (0.6 mils). The outermost layers and core layer each formed about 1/6 of the final film thickness; the intermediate layers each formed about 1/4 of the final film thickness. The relative thicknesses of each layer of multilayer embodiments of the present film can be chosen as appropriate. Preferred final film thicknesses are less than about 250 µm (10 mils), more preferably less than about 51 µm (2 mils), most preferably less than about 25 µm (1 mil).

Claims: An oriented heat shrinkable thermoplastic coextruded multilayer film comprising: a) a core layer comprising thermoplastic polyolefin (TPO) which comprises a continuous phase of isotactic polypropylene and a dispersed phase of ethylene propylene rubber; b) intermediate layers, adjacent each side of the core layer, comprising a polymeric adhesive; and c) two outer layers each bonded to a respective intermediate layer, comprising a polymeric material selected from; i) ethylene alpha olefin copolymer; ii) ethylene unsaturated ester copolymer; iii) ethylene acid copolymer; and iv) blends thereof. A film according to claim 1 which comprises an outer ethylene alpha olefin copolymer layer comprising: i) homogeneous ethylene alpha olefin copolymer; or ii) heterogeneous ethylene alpha olefin copolymer. A film according to claim 1 which comprises an outer ethylene unsaturated ester copolymer layer comprising: i) ethylene vinyl acetate copolymer; or ii) ethylene alkyl acrylate copolymer. A film according to claim 1 which comprises an outer ethylene acid copolymer layer comprising: i) ethylene acrylic acid copolymer; ii) ethylene methacrylic acid copolymer; or iii) ionomer. A film according to any one of the preceding claims which is cross-linked. A film according to any one of the preceding claims having a thickness of less than 250 µm (10 mils). A film according to claim 6 having a thickness of less than 25µm (1 mil). A package made from a film as claimed in any one of the preceding claims.

Inventors: WILBURN DANIEL S, WILBURN, DANIEL S.
Applicants: CRYOVAC INC, CRYOVAC, INC.
Application year: 1995
Main classification: B32B27
IPC codes: B32B27, B32B7, B65D1