Hemispherical fluid bearing

Abstract: A hemispherical fluid bearing and a manufacturing method thereof are provided. The hemispherical fluid bearing has a pair of inner rings (20), each having a spherical outer lubricating surface, which are fixed to a shaft (10) to face each other, and an outer ring (50) having a lubricating surface corresponding to the lubracating surfaces of the inner rings (20) for supporting the rotation of the inner rings (20). One of the inner rings (20) and the outer ring (50) has a first film coating of titanium or ceramic formed on the lubricating surface thereof. Therefore, abrasion due to solid friction when a motor starts or stops, is efficiently decreased.

Description: Background of the Invention The present invention relates to a bearing, and more particularly, to a hemispherical fluid bearing. In general, fluid bearings are used for supporting articles rotating at high speed. A conventional contact bearing such as a ball bearing or a roller bearing makes severe oscillation and noise, and rotates unstably, at high speed. On the contrary, a fluid bearing, which rotates at high speed in a non-contact manner, seldom oscillates and rotates stably. Therefore, the fluid bearing can find its applications in spindle motors of hard disk drives which must rotate rapidly, or a rotative multi-surfaced mirror driving motor used in laser printers or laser scanners. FIG. 1 is a sectional view of a conventional hemispherical bearing which is one of the fluid bearings (EP 0 376 647 A). As shown, the conventional hemispherical fluid bearing is comprised of an upper inner ring 20 and a lower inner ring 30, each having a hemispherical outer surface, which are fixed to a shaft 10 of a motor to be face-to-face with each other, an outer ring 50 fixed in a bearing housing 40, a ring 60 for keeping upper inner ring 20 and lower inner ring 30 from being detached from shaft 10, a spacer 70 disposed between upper inner ring 20 and lower inner ring 30 for maintaining clearance between outer ring 50 and upper inner ring 20, and between outer ring 50 and lower inner ring 30. Outer ring 50 supports upper inner ring 20 and lower inner ring 30 so that they can rotate. Since lubricant oil fills the clearance between outer ring 50 and inner rings 20 and 30 and generates fluid friction therebetween, upper inner ring 20 and lower inner ring 30 can rotate without making contact with outer ring 50. Therefore, a motor employing the hemispherical fluid bearing produces no oscillation and its rotation is stable. However, the conventional hemispherical fluid bearing exhibits a distinct drawback in that the contact surfaces of outer ring 50 and inner rings 20 and 30 abrade when the motor starts and stops. That is, solid friction occurs between outer ring 50 and upper inner ring 20, and between outer ring 50 and lower inner ring 30, at or below a threshold speed, thus accelerating the abrasion. As a result, the life span of the hemispherical fluid bearing decreases. Summary of the Invention The object of the present invention is to provide a hemispherical fluid bearing which can efficiently decrease abrasion caused by solid friction. To achieve the above object, there is provided a hemispherical fluid bearing comprising a pair of inner rings, each having a spherical outer lubricating surface, which are fixed to a shaft to face each other, and an outer ring having a lubricating surface corresponding to the lubricating surfaces of the inner rings, for supporting the rotation of the inner rings, wherein at least one of the inner rings and the outer ring has a first film coating of titanium or ceramic formed on the lubricating surface thereof, wherein there is a second film coating of a diamond-like carbon formed on the first film coating. The outer ring is preferably formed of ceramic. A predetermined groove is formed in the second film coating which extends to the first film coating. The first film coating is 5-20µm, and the second film coating is 5-10µm. Brief Description of the Drawings The above object and advantages of the present invention will become more apparent by describing in detail a preferred embodiment thereof with reference to the attached drawings in which: figure 1 is a sectional view of a conventional hemispherical fluid bearing; figure 2 is a sectional view of a hemispherical fluid bearing according to the present invention; and figure 3 is a sectional view taken along line A-A of figure 2. Detailed Description of the Invention Referring to figures 2 and 3, a hemispherical fluid bearing according to the present invention is comprised of an upper inner ring 20 and a lower inner ring 30, each having a hemispherical surface, which are fixed to a motor shaft 10 to be face-to-face with each other, an outer ring 50 fixed in a bearing housing 40, for supporting upper inner ring 20 and lower inner ring 30 so that they can rotate, a ring 60 for keeping upper inner ring 20 and lower inner ring 30 from being detached from shaft 10, and a spacer 70 disposed between upper inner ring 20 and lower inner ring 30 for maintaining clearance between outer ring 50 and upper inner ring 20, and between outer ring 50 and lower inner ring 30. Here, ring 60 may be forcibly fitted or be screw-combined with shaft 60. ,Upper inner ring 20 and lower inner ring 30 formed mainly of high carbon steel or WCo are coated with a 5-20 µ m thick titanium (Ti) film 21. Similarly, the lubricating surface of outer ring 50 is formed mainly of high carbon steel or WCo and is coated with a 5-20 µ m thick Ti film 51. Ti film coatings 21 and 51 can be replaced with a ceramic film coating, for example, an Al 2 O 3 film coating. In addition, upper inner ring 20, lower inner ring 30, and outer ring 50 may all be formed of ceramic. The film coating serves to alleviate the abrasion between outer ring 50 and upper inner ring 20, and between outer ring 50 and lower inner ring 30, which is caused by solid friction therebetween, when a motor starts or stops, namely, at or below a threshold speed. On the other hand, to further reduce the abrasion caused by the solid friction, a diamond-like-carbon (DLC) film of 5-10 µ m is coated on Ti film coating 21 of upper inner ring 20 and lower inner ring 30. Since DLC film coating 22 has a linear expansion coefficient similar to that of Ti film coating 21, there is no concern about flaking or a change of clearance. Further, the former is more resistant to friction than the latter, thus more efficiently alleviating the impact of the solid friction. A groove 23 is formed in DLC film coating 22. Groove 23 may reach Ti film coating 21 through DLC film coating 22 depending on the thickness of DLC film coating 22. Groove 23 lifts upper inner ring 20 and lower inner ring 30 away from outer ring 50 by generating oil pressure or air pressure when they rotate. Further, DLC film coating 22 and groove 23 may be provided to outer ring 50. An embodiment of a method for manufacturing the above hemispherical fluid bearing will be described, in detail. Upper inner ring 20 and lower inner ring 30 formed mainly of high carbon steel or WCo are lapping-machined to have an out-of-sphericity of 0.15-0.25 µ m, and their spherical surfaces are coated with a 5-20 µ m thick Ti film. Then, a 5-10 µ m thick DLC film is coated on the Ti film. A Ti ion beam projection method or a Ti gas deposition method can be used for the coating of the Ti film. The Ti film can be replaced with a ceramic film by the same method. The lubricating surface of outer ring 50 is coated with a Ti film or a ceramic film to a thickness of 5-20µm. Thereafter, groove 23 is formed in DLC film coating 22 by a chemical corrosion method or an electrical discharge machining method. As described above, the hemispherical fluid bearing according to the present invention can efficiently prevent abrasion caused by solid friction between an inner ring and an outer ring. Therefore, its longevity is approximately 500,000 start-stops, while the conventional bearing has a longevity of 100,000-200,000 start-stops.

Claims: A hemispherical fluid bearing comprising a pair of inner rings, each having a spherical outer lubricating surface, which are fixed to a shaft to face each other, and an outer ring having a lubricating surface corresponding to said lubricating surfaces of said inner rings for supporting the rotation of said inner rings, wherein at least one of said inner rings and said outer ring has a first film coating of one of titanium and ceramic formed on the lubricating surface thereof, and wherein a second film coating of a diamond-like-carbon is formed on said first film coating. A hemispherical fluid bearing as claimed in claim 1, wherein said outer ring is formed of ceramic. A hemispherical fluid bearing as claimed in claim 1 or 2 wherein a predetermined groove is formed in said second film coating. A hemispherical fluid bearing as claimed in claim 3, wherein said groove extends to said first film coating. A hemispherical fluid bearing as claimed in any preceding claim, wherein said first film coating is 5-20µm thick. A hemispherical fluid bearing as claimed in any preceding claim, wherein said second film coating is 5-10µm. A hemispherical fluid bearing as claimed in claim 3, wherein said second film coating is 5-10µm.

Inventors: HONG MIN-PYO, HONG, MIN-PYO
Applicants: SAMSUNG ELECTRONICS CO LTD, SAMSUNG ELECTRONICS CO., LTD.
Application year: 1995
Main classification: F16C33
IPC codes: F16C33, F16C23, F16C17