HALOGEN SCAVENGER FOR POLYMERS AND COPOLYMERS

Abstract: A solid solution is provided which is useful as a halogen-scavenging compound in polymer-containing formulations, where the polymer contains low levels of acid materials. The halogen scavenger is hydrotalcite-like composition, i.e., an aluminum magnesium hydroxy carbonate solid solution. The solid solution has a characteristic IR spectrum, which indicates bidentate coordination of carbonate, and has a crystallite size in the <003> direction of about 190 ANGSTROM to about 225 ANGSTROM .

Description: HALOGEN SCAVENGER FOR POLYMERS AND COPOLYMERS Field of the Invention The invention relates to hydrotalcite-like compositions useful as halogen scavengers in polymer formulations, and more specifically pertains to aluminum magnesium hydroxy carbonate solid solutions which may be compounded with plastics to neutralize residual catalyst. Background of the Invention Many synthetic polymers are prepared by catalyzed polymerization of monomers. Generally, the catalyst, or residue thereof, remains in the final product. Removal of the catalyst, which may be present at levels as low as ten parts per million, is commercially impractical. However, leaving the catalyst in the polymer, even at such low concentrations, often causes problems. The catalysts used to polymerize olefinic monomers are typically halogen-containing metallic or organometallic compounds, e.g., Ziegler-Natta catalysts containing titanium tetrachloride . It is reported that residual titanium chloride species in the polymers interfere with the functioning of stabilizers, e.g., antioxidants, that are typically compounded with the polymer. Residual catalyst may also catalyze polymer degradation reactions, and, particularly with halogen-containing catalyst residue, the halogens can promote corrosion of the equipment used to compound and process the polymer. It is commonly observed that polymers which have been compounded with thermal, and particularly light, stabilizers may exhibit a discoloration, i.e., they can develop a yellow or pinkish coloration. This has been attributed to the action of residual catalyst, and particularly halide ions, reacting with the stabilizers that have a phenol or a cruinone functional group. The halide may react with the phenol group to generate a colored phenolate anion. Most residual catalyst is acidic. Thus, one approach to overcoming the problems associated with residual catalyst is to add a basic material to the polymer, to thereby neutralize the residual catalyst. Such basic materials are known in the art, and are commonly referred to as neutralizer compounds or halogen-scavenging compounds. One class of halogen-scavenging compound is hydrotalcite and hydrotalcite-like materials. Hydrotalcite is the name given to a natural mineral having the chemical structure Al 2 Mg 6 OH 16 (C0 3 ) • 4 H-.0, which may also be written as Al 2 0 3 • 6 MgO • C0 3 • 12 H 2 0. Natural hydrotalcite is an example of a basic magnesium alumino-carbonate hydrate. As obtained from the earth, natural hydrotalcite is generally contaminated with other minerals such as penninite and muscovite, as well as various heavy metals. The impurity levels in natural hydrotalcite, as well as its scare occurrence around the world, have limited its commercial use. Pure, or nearly pure hydrotalcite has been prepared synthetically. For example, U.S. Patent No. 5,250,279 describes a method for the preparation of high purity synthetic hydrotalcite having a small platelet morphology. The method comprises reacting a mixture of a magnesium source, such as magnesium oxide, with an alkali metal bicarbonate, solid alumina trihydrate and an alkali metal aluminate under aqueous hydrothermal conditions at a temperature of about 160 - 200 °C. Other reports of the preparation of synthetic hydrotalcite having a composition which matches natural hydrotalcite may be found in, for example, U.S. Patent Nos. 3,650,704 and 3,539,306. The term "hydrotalcite" is often used genericaliy to refer to a large class of basic aluminum magnesium carbonate compounds or complexes having various lattice structures and compositions. These hydrotalcite-like materials, also referred to as hydrotalcite analogues, have been the subject of disclosed synthetic efforts. U.S. Patent No. 4,284,762 (the '762 patent) discloses a hydrotalcite of the formula Mg 1 ., c Al x (OH)-A x/n n --mH 2 0 wherein x is greater than 0 but less than or equal to 0.5, m is a positive number, and A n" represents an anion having a valence of n, or a product resulting from the surface- coating of said hydrotalcite with an anionic surface-active agent. The hydrotalcite has a BET specific surface area of not more than 20 m 2 /g, and a crystallite size, in the <003> direction of at least 600 A, and preferably at least 1,000 A.. U.S. Patent No. 4,299,759 (the '759 patent) discloses a hydrotalcite of the same composition as set forth in the '762 patent, but having a BET specific surface area of not more than 30 m /g. The '759 patent discloses that the surface treatment, i.e., the addition of sodium stearate to the hydrotalcite particle, can be achieved by adding an aqueous solution of sodium stearate to a suspension of the hydrotalcite powder to cause chemical adsorption of the surface-active agent to the surface of the solid powder. The surface treatment agent is preferably present at a loading of about 1 to about 10% by weight, based on the weight of the hydrotalcite. U.S. Patent No. 4,560,545 is directed to a process for preparing a basic aluminum magnesium carbonate of the formula Al,«Mg 6 -(OH) 1 -(C0 3 ) 2 -4H 2 0. The process comprises heating an aqueous slurry cf aluminum hydroxide, magnesium hydroxide and either ammonia or a water-soluble organic nitrogen-containing base, in the presence of carbon dioxide and at a temperature of between 70 and 100 °C at atmospheric pressure. The reaction time is from 1 to 12 hours, and the carbon dioxide is bubbled through the slurry during this time. The basic aluminum magnesium carbonate so produced may be used in pharmaceutical compositions. Hungarian Patent HU 30,453 (Abstract No. 101:43635g, prepared by the Chemical Abstracts Service) discloses a composition with the formula Al 2 «Mg 4 » (OH) 12 - (C0 3 ) « 2H 2 0. The composition is prepared by the reaction of MgCl, with Na 2 C0 3 and Na orthoaluminate or Al(OH) 3 in the presence of NaOH. U.S. 4,539,195 claims a crystalline basic aluminum magnesium carbonate of the formula: Al 2 (Mg) 5 (OH) 12 (C0 3 ) 3 • x(H 2 0) in which x ≥ 4 , obtainable by hydrothermal reaction of aluminum hydroxide with magnesium hydroxide or magnesium oxide in the presence of carbonate ions in stoichiometric amounts under the influence of gravitational forces at a temperature of 50 to 100°C. A basic magnesium aluminum carbonate of the formula Al 2 0 3 • xMgO • yC0 2 • zH 2 0 is described in British Patent 1,086,779, wherein x can be 0.15 to 1.5, y can be varied from 0.3 to 2.5, and z is not less than 2.5. U.S. Patent No. 4,675,356 discloses a hydrotalcite solid solution represented by the following formula wherein M : 2 * represents at least one divalent metal selected from the group consisting of Mg, Ca, Sr and Ba; M 2 2* represents at least one divalent metal cation selected frcm the group consisting of Zn, Cd, Pb and Sn; M 3* represents a trivalent metal cation, A ~ represents an anion having a valency of n, and x, yl, y2 and m are positive numbers represented by the following expressions 0 < x ≤ 0.5, 0 < yl, 0 < y2, 0.5 ≤ yl+y2 < 1, and 0 s m < 2; and to a resin composition comprising the above agent. The hydrotalcite cf the '356 patent may be surface treated with, for example, anionic surface-active agents such as sodium stearate. Reheis, Inc., Berkeley Heights, NJ, sells an aluminum magnesium hydroxy carbonate, trademark L55-R ® , having an analysis of 14-18% aluminum oxide, 25-29% magnesium oxide, 15-19% sodium stearate and 8.5-13.5% carbon dioxide. L55-R ® is a white, odorless powder having a bulk density of 0.19 - 0.35 g/cc and a particle size of 100% through 400 mesh (37 microns) and not less than 90% through 10 microns. While the prior art describes several hydrotalcite and hydrotalcite-like materials, there remains a need in the art for materials which can be added to polymeric materials, and mitigate the problems associated with residual catalyst and other halide-generating mechanisms. Summary of the Invention The present invention provides a solid solution having the formula Al 2 (Mg) a (OH) b (C0 3 ) c (G) d -eH 2 0 wherein 3 ≤ a ≤ 5.5; 8 ≤ b ≤ 14; 1.2 ≤ c ≤ 3 ; O ≤ d ≤ l; l ≤ e ≤ lO and G is a surface active agent. The solid solution has a crystallite size in the <003> direction of about 190 A to about 225 A, and has bidentate coordination for carbonate ion as shown by an infrared spectrum. Preferably, the surface active agent is a metal salt of a C 10 -C 22 saturated fatty acid, and more preferably is sodium stearate, zinc stearate or calcium stearate. In a preferred embodiment, the solid solution has the above formula wherein 4.1 ≤ a ≤ 5.3; 10 s b s 12; 1.3 ≤ c ≤ 3 ; 0.05 ≤ d ≤ 0.5; 3 s e s 9. That the solid solution has bidentate coordination for the carbonate ion can be seen by a split absorption band in the region of 1415-1480 cm "1 . The solid solution preferably has a BET specific surface area of about 25 m 2 /g to about 40 m 2 /g. The solid solution may be present in an aqueous slurry, however is preferably a dry powder. The dry powder has a tap density of about 0.1 g/cc to about 0.3 g/cc. The invention also provides for a method for inhibiting the corrosion-causing tendency and coloration of halogen-containing olefin polymers or copolymers. The method comprises incorporating about 0.01% to about 1% of the solid solution as described above into an olefin polymer or copolymer. The solid solution, having surface active agent, may be formed by a process wherein an aqueous slurry comprising an aluminum compound, preferably basic aluminum carbonate gel and/or aluminum hydroxide, and a magnesium compound, preferably basic hydrated magnesium carbonate and/or magnesium oxide, wherein the molar ratio of magnesium to aluminum is about 1.5 to 2.75, is heated to a temperature of about 70 °C to about 95 °C and for a reaction time "X" to provide a first slurry, where "X" is a period of time sufficient to achieve removal of substantially all free and loosely bound carbon dioxide from the aqueous slurry. Then at least one surface active agent is added to the first slurry, to provide a second slurry. The second slurry is heated to a temperature of about 125 °C to about 140 °C for a time sufficient for a suspension test to be passed. The suspension test is described later herein. When magnesium oxide is the magnesium compound in the above process, aluminum hydroxide is preferably the aluminum compound, and a stream of carbon dioxide gas is passed through the second slurry at a rate sufficient to produce a solid solution. When basic aluminum carbonate gel is the aluminum compound, it preferably has an Al 2 0 3 content of about 2% to about 20% by weight. When magnesium carbonate is the magnesium compound, it preferably has a MgO content of about 40% to about 43.5% by weight. The solid solution prepared as described above will be present as an aqueous slurry. To obtain a dry- powder of the solid solution, the water may be removed from said second slurry, and the resulting material may be micronized to provide particles having a particle size distribution wherein at least 99% of the particles are less than 44 microns in diameter, and at least 95% of the particles are less than 10 microns in diameter. The process need not be run in the presence of a surface active agent, in which case an aqueous slurry comprising an aluminum compound, preferably basic aluminum carbonate gel and/or aluminum hydroxide, and a magnesium compound, preferably basic hydrated magnesium carbonate and/or magnesium oxide, wherein the molar ratio of magnesium to aluminum is about 1.5 to 2.75, is heated to a temperature of about 70 °C to about 95 °C and for a reaction time "X" to provide a first slurry. The reaction time "X" is a period of time sufficient to achieve removal of substantially all free and loosely bound carbon dioxide from the aqueous slurry. The first slurry is then heated to a temperature of about 125 °C to about 140 °C for about 1 to about 4 hours. The solid solutions formed by the above processes preferably have an IR spectrum which displays a split absorption band in the region of 1415-1480 cm *1 , and preferably have a crystallite size in the <003> direction of about 190 A to about 225 A. Brief Description of the Drawing The foregoing summary, as well as the following detailed description of the preferred embodiments of the invention, will be better understood when read in conjunction with the appended drawing. In the drawing: Fig. 1 is an infrared spectrum of a solid solution of the invention. Description of the Preferred Embodiments As indicated above, this application is directed to a synthetic solid solution, and in particular to a synthetic basic magnesium aluminocarbonate hydrate. The solid solution of the invention has the formula Al 2 (Mg) a (OH) b (C0 3 ) c (G) d -eH 2 0 wherein G is at least one surface active agent, and wherein the solid solution displays bidentate coordination for the carbonate ions as shown by an infrared spectrum, and wherein 3 ≤ a ≤ 5.5, 8 ≤ b ≤ 14, 1.2 ≤ c ≤ 3, O ≤ d ≤ l and 1 ≤ e ≤ 10. Techniques to determine the compositional formula of hydrotalcite and hydrotalcite- analogues, such as the solid solution set forth above, are well-known in the art. In a preferred embodiment, the hydrotalcite solid solution particles of the above formula comprise a surface- active agent. However, particularly in instances when the hydrotalcite is intended for use in aqueous coating compositions, or in antacids for pharmaceutical use, the surface active agent may not be present. Specific examples of the surface active agent include, without limitation, sodium stearate, potassium behenate, sodium montanate, potassium stearate, sodium oleate, potassium oleate, sodium palmitate, potassium palmitate, sodium laurate, potassium laurate, sodium dilaurylbenzenesulfonate, potassium octadecylsulfate, sodium laurylsulfonate, or disodium 2-sulfoethyl α-sulfostearate. Preferably, the surface active agent is a fatty acid salt of a metal, where the fatty acid should have at least about 10 carbon atoms, and may have as many as 20 or more carbon atoms. Fatty acids of greater than about 22 carbon atoms are not readily available at a low cost, and thus the fatty acids employed in the invention preferably have about 10 to about 22 carbon atoms. The fatty acid component is preferably a straight-chain fatty acid, however it may also have branching. The fatty acid component is preferably saturated, so as to be minimally reactive with, e.g., oxygen. A preferred fatty acid is stearic acid, which is a linear, C 1B fatty acid. A wide range of metal ions may constitute the metal ion component of the fatty acid salt, where exemplary, non-limiting examples of the metal ions include the ions of sodium, calcium, aluminum, magnesium, potassium and zinc. Sodium, zinc and calcium are preferred counterions. The molar ratio of fatty acid metal salt to aluminum in the solid solution is preferably not more than about 0.5:1. Preferably, the value of "d" in the formula for the solid solutions of the invention is greater than or equal to 0.05. On a weight basis, when the fatty acid salt is sodium stearate, the salt desirably contributes about 5.5 to about 15 weight percent of the solid solution, based on the total weight of the solid solution. When the level of fatty acid salt falls below the stated range, it is observed that the solid solution does not readily mix with polymers or copolymers, and thus is less effective as a halogen- scavenging compound. When the level of fatty acid salt exceeds the stated range, the solid solution does not have improved performance to offset the increased cost of such a formulation. A typical infrared spectrum of a solid solution cf the invention, having sodium stearate as the metal salt, is shown in Fig. 1. Salient features of the spectrum are set forth below in TABLE 1. TABLE 1. SELECTED ANALYSIS OF IR SPECTRUM IN FIG. 1 FUNCTIONAL FREQUENCY GROUP (cm '1 ) -OH Stretching 3430 H.O (molecular) 1620 C0 3 "2 stretching 1480 \ , ._ 1415> S P ll 1350 C0 3 "2 bending 790 .. ~ ) vibration 440 Mg-O' As seen in Fig. 1, the peak observed in the region of 1415-1480 cm -1 is actually split into two peaks. To the best knowledge of the inventors, this feature is unique to solid solutions of the invention, and is indicative of bidentate coordination for the carbonate ions. The solid solutions of the invention have a crystallite size in the <003> direction, as measured by x- ray diffraction, of about 190 A to about 225 A. This is considerably smaller than typical synthetic hydrotalcite- analogues, and is analogous to that found in naturally formed hydrotalcite. Control of the crystallite size in the < 003> direction may be achieved by careful control of the manufacturing process, and in particular the conditions cf a hydrothermal treatment, as illustrated, for example, in the Examples contained herein. An X-ray diffraction analysis of a typical solid solution according to the invention is shown in TABLE 2. The X-ray diffraction data indicate that the solid solutions of the invention are distinct from the solid solutions disclosed in, e.g., U.S. 4,539,195, the entire disclosure of which is incorporated herein by reference. TABLE 2. X-RAY DIFFRACTION ANALYSIS INTERPLANAR RELATIVE INTERPLANAR RELATIVE SPACING (A) INTENSITY SPACING (A) INTENSITY 8.4 7 2.27 7 7.6 100 2.15 7 6.3 3 1.93 53 5.75 7 1.714 10 4.45 2 1.619 8 4.18 7 1.519 24 3.76 56 1.488 22 2.89 10 1.450 5 2.84 3 1.409 5 2.8 5 1.378 2 2.56 61 1.306 3 2.52 8 1.263 7 2.35 7 1.247 5 The solid solutions of the invention preferably have a tap density of about 0.1 g/cc to about 0.3 g/cc, and more preferably about 0.15 g/cc to about 0.2 g/cc. Tap density may be measured by accurately transferring approximately 10 g of sample into a 250 mL flat-bottomed graduated cylinder, then placing the cylinder in an automatic tapper for one cycle (30 seconds, 1 second drop, 1 second lift, 1 inch drop) . The mass of the sample, divided by the volume in the cylinder after one cycle, is the tap density (g/cc) . The solid solutions of the invention preferably have a BET specific surface area of about 25 m 2 /g to about 40 m 2 /g. Again, control of the BET surface area may be achieved by careful control of the manufacturing conditions used to make the solid solution, and in particular by carefully controlling the conditions of a hydrothermal treatment step, as illustrated in the Examples set forth below. It is generally observed that precipitation of the solid solution will lead to very high BET specific surface areas, frequently in excess of 100 m 2 /g. As the temperature and time of a hydrothermal treatment is increased, it is generally observed that a lower BET specific surface area is achieved. Thermal analysis was performed on a typical solid solution of the invention. The results are shown in TABLE 3. TABLE 3. THERMAL ANALYSIS DTA Endotherm CO 265 28 318 81 384 .08 429 17 The endothermic peak due to elimination of the interlayer of water is observed at 265.28°C, where loss of moisture and carbonate occur. This indicates that there is a high binding force between anions and the basic layer in the solid solution. The second important endotherm occurs at 384.08°C. At this temperature, loss of water of crystallization and carbon dioxide evolution is believed to occur. The final endotherm at 429.17°C is due to decomposition of brucite-like layers in the solid solution. Another aspect of the invention is a solid solution formed by a process comprising the steps: (a) heating an aqueous slurry comprising an aluminum compound such as basic aluminum carbonate gel and/or aluminum hydroxide, and a magnesium compound such as basic hydrated magnesium carbonate and/or magnesium oxide, wherein the molar ratio of magnesium to aluminum is about 1.5 to 2.75, to a temperature of about 70 °C to about 95 °C for as long as necessary to remove all free or loosely bound carbon dioxide, which is typically at least about 1 hour, to form a first slurry; and (b) adding at least one surface active agent to said first slurry, to provide a second slurry; and (c) heating said second slurry to a temperature of about 125 °C to about 140 °C for a time sufficient for a suspension test (described below) to be passed. The aluminum hydroxide employed is preferably an active aluminum hydroxide, particularly a finely particulate, amorphous aluminum hydroxide gel which quickly dissolves in diluted acid. Such an aluminum hydroxide can be produced, for example, by precipitation from aluminum salt solutions by means of bases, particularly alkali carbonates. The magnesium compounds employed in the process of the present invention should likewise be present in their active form. Dead-burnt MgO, for example, is entirely unsuitable. The production of active magnesium oxides (hydratable) and basic magnesium carbonates is known. The basic aluminum carbonate preferably has an A1 2 0 3 content of about 2% to about 20%, and the magnesium compound is preferably a basic hydrated magnesium carbonate having a MgO content of about 40% to about 43.5%. The- aqueous slurry should be heated for a time and temperature sufficient to liberate most if not all of the free or loosely bound carbon dioxide from the aqueous slurry. This point can be determined based on the procedure provided in the General Procedures section, below. Typically, this can be accomplished by heating for at least one hour, preferably about 1.5 to about 2.5 hours, at a temperature of about 70 °C to about 95 °C, preferably about 85 °C to about 90 °C. The second slurry, which contains a surface active agent, should be heated for a time and temperature such that the solid solution contained therein passes the suspension test. The suspension test is described in the General Procedures section, below. Typically, this can be accomplished by heating for about 1.5 to about 4 hours, preferably for about 1.5 to about 2 hours, at a temperature of about 125 °C to about 140 °C, preferably about 130 °C to about 135 °C. In one embodiment of the invention, magnesium oxide can be used as the magnesium compound, and aluminum hydroxide is the aluminum compound. In this instance, carbonate ion must be provided to the reaction mixture, and this can be accomplished by passing a stream of carbon dioxide gas through the second slurry at a rate sufficient to produce the solid solution. If the solid solution is made free of surface active agent, then it will never pass the suspension test. In this case, a hydrothermal treatment should be conducted for about 1 to about 4 hours, at a temperature of about 125 °C to about 140 °C. Another aspect of the invention is a method for inhibiting the corrosion-causing tendency of halogen- containing olefin polymers or copolymers. The method comprises incorporating about 0.01% to about 1% of the solid solution of the invention into an olefin polymer or copolymer composition. The solid solution may be compounded with synthetic resins containing halogens and/or acidic substances derived from, for example, catalysts, monomers and post-treating agents. Examples of such synthetic resins include synthetic resins produced by using halogen- containing Ziegler-type catalysts, such as low-density to high-density pclyethylenes, polypropylene, polybutene-l, poly(4-methylpentene-l) , ethylene/propylene copolymer, ethylene/propylene/polyene copolymers, ethylene/butene-1 copolymer, polybutadiene rubber and polyisoprene rubber. Further exemplary synthetic resins, which may be produced using halogen-containing Friedel-Crafts catalysts, include, without limitation, polybutene, polyacetal, butyl rubber, liquid polyisobutylene, petroleum resins and polybenzil. Synthetic resins produced using acidic substances such as sulfuric acid, phos p horic acid and hydrochloric acid as catalysts, may also be employed, and include such resins as diallyl phthalate resin, phenolic resins, xylene resin and silicone resins. Synthetic resins derived from monomers containing halogens and/or acidic substances may also benefit from compounding with a solid solution of the invention. Exemplary polymers polyvinyl chloride, copolymers of vinyl chloride with at least one comonomer selected from olefinic monomers such as ethylene and propylene, vinylidene halide monomers such as vinylidene chloride and vinylidene fluoride, vinyl acetate, vinyl ether monomers such as lauryl vinyl ether, maleic anhydride, maleic acid esters such as butyl maleate, butadiene and styrene, polyvinylidene chloride, vinylidene chloride copolymers, polyvinyl acetate, vinyl acetate copolymers, polyorganosiloxanes, acrylic or methacrylic polymers or copolymers, epoxy chloroprenne rubber, fluorine rubber, polycarbonate resins, polyesters such as polyethylene terephthalate or polybutylene terephthalate, and polyurethane resins. The polymers and copolymers may be post- halogenated synthetic resins such as post-chlorinated olefinic resins ( e . g . , chlorinated polyethylene) post- chlorinated vinyl chloride-type resins (e.g. chlorinated polyvinyl chloride) , post-chlorosulfonated olefinic resins ( e . g. chlorosulfcnated polyethylene) and post-halogenated rubbers such ( e . g . , chlorinated or brominated butyl rubber) ; synthetic resins subjected to post-treatments (such as washing with acids) , such as sulfuric acid, phosphoric acid or hydrochloric acid, or neutralization, for example ABS resin and polystyrene resin; synthetic resins containing halogen-containing fire retardants or flame retardants such as tetrabromobisphenol A, decarbromodiphenyl oxide, or chlorinated paraffin; synthetic resins containing halogen- containing coloring agents or phenolic antioxidants such as isoindolinone or phthalocyanine green. There is no particular restriction on the means of blending the synthetic resin with the hydrotalcite solid solution of the invention. For example, the synthetic resin and solid solution may be mixed as uniformly as possible with or without resin additives by the same means as conventionally used to mix resins with, for example, stabilizers fillers. Mixing may be carried out by using known mixing devices such as a ribbon blender, a high-speed mixer, a kneader, a pelle izer or an extruder. Alternatively, it is possible to use a method by which a suspension of the solid solution is added to a resin slurry immediately after polymerization, and the mixture is stirred and then dried. The following examples are set forth as a means of illustrating the present invention and are not to be construed as a limitation thereon. General Procedures Loose or Free Carbon Dioxide Determination According to the method, a sample is placed under vacuum such that free or loosely absorbed carbon dioxide is removed from the sample and captured in a bed of ascarite . The weight gain of the ascarite is proportional to the carbon dioxide level in the sample. Procedure : A single-necked flask is fitted with an adapter, which is connected through tubing to a bubbler containing cone, sulfuric acid. The bubbler exit is connected with tubing to a series of three, glass u-tubes which are connected in tandem by tubing. The u-tubes have stopcocks at each end, which allow control of the gas flow through the u-tubes. The last u-tube is connected to a vacuum source. The u-tube closest to the bubbler is filled with magnesium perchlorate (Mg(Cl0 3 ) 2 ) , the middle u-tube contains a plug of ascarite (mesh size 8-20) followed by a plug of magnesium perchlorate, and the third u-tube (closest to the vacuum source) contains a plug of magnesium chlorate followed by a plug of ascarite (20-30 mesh size) . Pinch clamps are placed on the pieces of tubing which flank the middle u-tube. Both stopcocks of the middle u-tube are closed, then the middle u-tube is disconnected from the tubing and weighed. The middle u-tube is replaced and the pinch clamps removed. All stopcocks are opened. About 1 to 2 grams of sample are accurately weighed into the single-necked flask. Then a slight vacuum is applied until about 3 bubbles/second come through the bubbler. The flask containing the sample is heated for about 10 minutes, then the heat is removed and the flask allowed to cool under vacuum for about 15 minutes . The vacuum is discontinued and the middle u-tube is reweighed as before. If the weight gain is not more than about 0.6 g, then substantially all of the free or loosely bound carbon dioxide has been removed from the solid solution. Suspension Test Combine 100 mL deionized water and about 0.5-0.6 g of solid solution, as a dry powder, into a 150 mL beaker. Add a magnetic bar and stir the suspension vigorously for five minutes. Allow the suspension to stand for five minutes. The absence of any settling of the powder indicates that additional thermal treatment is not necessary. In the Examples, average particle size was determined using a Microtrac SRA 50 particle measurement system from Leeds & Northrop Co., Palm Harbor, FL. BET surface area was measured using a Monosorb surface area analyzer from Quanta Chrome Corporation, Syosset, NY. Homogenization of the slurry was done using a Manton-Gaulin Homogenizer Model 15M from Gaulin Corporation, Everett MA, operated at 5000 psi. Homogenization pressures of about 3000 psi to about 8000 psi were found to be satisfactory, and a preferred pressure was about 5000-6000 psi. PREPARATIVE EXAMPLES Example 1 A slurry was prepared by blending 346 g basic aluminum carbonate gel (12.9% A1 2 0 3 , LIQUIGEL HO, Reheis Inc., Berkeley Heights, NJ) , 186 g USP grade heavy MgC0 3 powder (Whittaker, Clark & Daniels, South Plainfield, NJ) and 649 g water. The slurry was maintained at 85°C for 0.5 hour; then maintained at 70°C for 1 hour. To the slurry was added 18.5 g sodium stearate (Sodium Stearate EA, Food Grade, Witco Corporation, Oakland, NJ) . The slurry was transferred to a Parr bomb (Series 4500 Pressure Reactor, Parr Instrument Company, Moline, IL) , where it was heated at 145°C for 4 hours. The resulting slurry was processed through a spray dryer (Bowen Engineering Inc., Bridgewater, NJ) at an outlet temperature of 75°C to produce a fine, white powder which was then micronized in an air mill to an average particle size of 1.4 microns. The product was analyzed to have 14.9% Al 2 0 3 , 29.8% MgO, 16.4% C0 2 , and 7.04% sodium stearate for a formula of Al 2 0 (Mg) 5. - (OH) 1 - .1 (C0 3 ) 2 . 5S (Na Stearate) 0.16 ■ 6.69 (H,0) . The powder had a BET surface area of 25.0 m 2 /g, a tap density of 0.16 g/cc, and a Al/C0 3 molar ratio of 0.78. Example 2 Following the procedure of Example 1, a slurry was prepared blending 326 g of basic aluminum carbonate gel (13.8% A1 2 0 3 ) , 186 g USP grade heavy MgC0 3 powder and 669 g water. The resultant slurry was maintained at 85°C for 0.5 hour; then ' maintained at 70°C for 1 hour. To the slurry was added 18.5 g sodium stearate. The slurry was transferred to a Parr bomb, where it was heated at 130°C for 4 hours. The product was removed from the Parr bomb and homogenized to break down any agglomerates formed during the processing step into fine submicron- and micron-size particles. It may be noted that the primary precipitated particle is in the submicron range, and these particles agglomerate during the processing steps. The homogenized sample was then processed through a spray dryer at an outlet temperature of 75°C to produce a fine, white powder which was then micronized in an air mill to an average particle size of 1.4 microns. The product was analyzed to have 14.1% Al 2 0 3 , 29.4% MgO and 16.4% C0 2 . The powder had a BET surface area of 24.8 m 2 /g and a tap density of 0.24 g/cc. Example 3 Following the procedure of Example 1, a slurry was prepared by blending 326 g basic aluminum carbonate gel (13.8% Al 2 0 3 ) , 186 g USP grade heavy MgC0 3 powder and 669 g water. The resultant slurry was maintained at 85°C for 0.5 hour; then maintained at 70°C for 1 hour. To the slurry was added 18.5 g sodium stearate, and the mixture was homogenized to break down any agglomerates formed during the prior processing steps, into fine submicron- and micron-size particles. The slurry was then transferred to a Parr bomb and heated at 130°C for 4 hours. The resulting slurry was processed through a spray dryer at an outlet temperature of 75°C to produce a fine, white powder which was then micronized in an air mill to an average particle size of 1.7 microns . The product was analyzed to have 17.0% Al 2 0 3 , 30.0% MgO and 11.5% CO-. The powder had a BET surface area of 23.1 m 2 /g, a tap density of 0.17 g/cc, and a crystallite size according to x-ray diffraction in the <003> direction of 225 A. Example 4 Following the procedure of Example 1, a slurry was prepared by blending 348 g basic aluminum carbonate gel (12.9% A1 2 0 3 ) , 186 g USP grade heavy MgC0 3 powder and 649 g water. The resultant slurry was maintained at 85°C for 0.5 hour; then maintained at 70°C for 1 hour. To the slurry was added 18.5 g of sodium stearate. The slurry was transferred to a Parr bomb and heated at 130°C for 4 hours. The resulting slurry was processed through a spray dryer at an outlet temperature of 75°C to produce a fine, white powder which was then micronized in an air mill to an average particle size of 2.9 microns. The product was analyzed to have 14.4% Al 2 0 3 , 29.3% MgO, 18% C0 2 and 5.39% sodium stearate for a formula of Al 2 0 (Mg) 5 21 (OH) X0.S7 (CO 3 ) 2 93 (Na Stearate) 0 13 ■ 7.86H 2 0. The powder had a BET surface area of 27.2 m 2 /g, and a tap density of 0.23 g/cc. The ratio of Al to C0 3 was 0.68. Example 5 Following the procedure of Example 1, a slurry was prepared by blending 344 g basic aluminum carbonate gel, 186 g USP grade heavy MgC0 3 powder and 649 g water. The resultant slurry was maintained at 85°C for 0.5 hour; then maintained at 70°C for 1 hour. To the slurry was added 18.5 g of sodium stearate. The slurry was transferred to a Parr bomb and heated at 130°C for 4 hours. The resulting slurry was processed through a spray dryer at an outlet temperature of 75°C to produce a fine, white powder which was then micronized in an air mill to an average particle size of 2.1 microns. The product was analyzed to have 13.6% A1 2 0 3 and 30.4% MgO. The powder had a BET surface area of 24.1 m 2 /g and a tap density of 0.19 g/cc. Example 6 Following the procedure of Example 1, a slurry was prepared by blending 360 lbs basic aluminum carbonate gel (9.0% A1 2 0 3 , LIQUIGEL NA, Reheis, Inc., Berkeley Heights, NJ) , 108 lbs USP grade heavy MgC0 3 powder and 600 lbs water in a pilot plant facility having a glass-lined reactor. The resultant slurry was maintained at 80-85°C for 2.5 hours. To the slurry was added 14 lbs of zinc stearate, and then the slurry was heated at 135°C for 1.5 hours. The resulting slurry was processed through a spray dryer at an inlet temperature 135-163°C and outlet temperature of 70-75°C to produce a fine, white powder which was then micronized in an air mill to an average particle size of 3.2 microns. The product was analyzed to have 16.7% Al 2 0 3 , 29.0% MgO, 10.0% C0 2 , and 9.67% zinc stearate for a formula of Al 2 . 0 (Mg) 4 . 36 (OH) 11-M (C0 3 ) x . 39 (Zn Stearate) 0 09 ■ 5.76H 2 0. The powder had a BET surface area of 29.7 m 2 /g and, according to x-ray diffraction, a crystallite size in the <003> direction of 205 A. The powder had a tap density of 0.21 g/cc. Example 7 Following the procedure of Example 1, a slurry was prepared by blending 242 lbs basic aluminum carbonate gel (9% A1 2 0 3 ) , 72 lbs USP grade heavy MgC0 3 powder and 450 lbs water. The resultant slurry was maintained at 80-85°C for 1.5 hours, then 11.3 lbs calcium stearate was added followed by additional heating at 132°C for 1.5 hours. The resulting slurry was processed through a spray dryer at an outlet temperature of 70-75°C to produce a fine, white powder which was then micronized in an air mill to an average particle size of 3.6 microns. The product was analyzed to have 17% Al 2 0 3 , 30.3% MgO, 11.8.% C0 2 , and 8.72% calcium stearate for a formula of Al 2 .o < M S) . .,- . (OH) ,-. 82 (C0 3 ) -..„ (Ca Stearate) 0 . 08S • 5.03H 2 O . The powder had a BET surface area of 29.7 m 2 /g and, according to x-ray diffraction, a crystallite size in the <003> direction of 201 A. The powder had a tap density of 0.23 g/cc. Example 8 Following the procedure of Example 1, a slurry was prepared by blending 270 lbs basic aluminum carbonate gel (8.86% Al 2 0 3 ) , 42.5 lbs basic aluminum carbonate gel (13.4% A1 2 0 3 ) , 134 lbs USP grade heavy MgC0 3 powder and 500 lbs water. The resultant slurry was maintained at 80-85°C for 1.5 hours, then 14.3 lbs sodium stearate were added followed by heating at 135°C for 1.5 hours. The resulting slurry was processed through a spray dryer at an outlet temperature of 55-60°C to produce a fine, white powder which was then micronized in an air mill to an average particle size of 2.6 microns . The product was analyzed to have 17.8% Al 2 0 3 , 30.2% MgO, 10.9% C0 2 , and 7.4% sodium stearate for a formula of Al 2 . 0 (Mg) 4 29 (OH) -- 71 (C0 3 ) 143 (Na Stearate) 0.14 • 4.91H 2 0. The powder had a BET specific surface area of 30.5 m 2 /g and, according to x-ray diffraction, a crystallite size in the <003> direction of 190 A. The powder had a tap density of 0.12 g/cc. PERFORMANCE EXAMPLES Example 9 and Comparative Example 1 A masterbatch containing 1% additive package and 99% HDPE (unstabilized reactor high density polyethylene, product 8412, Chevron Chemical, Orange, TX) was prepared by dry blending. The chloride concentration of the HDPE was determined to be 360 ppm (one determination) . The additives were 1000 ppm of a primary antioxidant (Irganox 1010, Batch No. 391204, Ciba-Geigy, Sufforn, NY) , 500 ppm of a secondary antioxidant (Irgafos 168, Batch No. AVA 382001, Ciba-Geigy) , and 300 ppm of solid solution prepared according to Example 8. The masterbatch was extruded and formed into discs as described below, to prepare Sample No. 9. A comparison composition was prepared as follows. The composition of Example 9 was duplicated, with the exception that DHT-4A (a hydrotalcite from Kyowa Chemical Industry Co., Ltd., Tokyo, Japan) was substituted for the solid solution of Example 8. The masterbatch was extruded and formed into discs as described below, to prepare Sample No. Cl. Extrusion Conditions: Sample Nos. 9 and Cl were first extruded through a Leistritz 34 mm co-rotating, intermeshing twin-screw 10-zone extruder, with an L/D of 40. Two volumetric feeders were used to feed the materials at about 20 lb/hr. The ratio of feed rates of each feeder was adjusted so that the additives were fed at the prescribed concentrations. Before starting, the extruder was purged with purging compound, followed by polypropylene and then 12 lb of each polymer-based formulation. Vacuum was not used. Each material was extruded through a strand die and quenched in cold water. High velocity air was used to blow off water from the extruder strand, after which it was pelletized in a Killion Pelletizer. Each of the two formulations was then extruded four additional times in a Killion 1" single screw 5-zone extruder, with an L/D of 20 and a general purpose screw. Between each run about 1 lb. of formulated material was used to purge the machine. The extruded material was quenched and pelletized as described above. TABLE A reports the extrusion conditions for each of the five runs. Sample Preparation: Discs, 1/8" thick and 3.1" in diameter, were prepared from the extruded material by compression molding. The HDPE samples were prepared at 175°C as follows: l min preheating pellets, 2 min melting at 1000 lbs, 3 min cooling at 5000 lbs. Testinσ: Color data for the discs prepared above was obtained using the combination of a Macbeth Color Ξye ® spectrophotometer Model M2090 PL and an I3M personal computer. Color measurement was done in a reflectance mode. From reflectance data, the tristimulus values were computed to generate yellow-blue ("Blue" in TABLE B) and red-green ("Green" in TABLE B) indices. Oven-aging conditions were 110°C for 22 hrs. The color data appears in TABLE B. TABLE B. Color Data Pass Sample No. No. Blue Green Halogen- scavenger 1 l 5.37 7.21 DHT-4A 1 9 5.78 7.66 Ex. No. 8 1 Cl (Aged) 5.10 7.15 DHT-4A 1 9 (Aged) 5.64 7.66 Ex. No. 8 3 l 4.47 6.45 DHT- A 3 9 5.38 7.36 Ex. No. 8 5 Cl 3.96 6.06 DHT-4A 5 9 5.95 7.18 Ex. No. 8 The data in Table B indicates that the solid solution from Example No. 8 is a superior halogen-scavenge : the color of Sample No. 9 was more consistent throughout five extrusion passes, and was slightly whiter in color than Sample No. Cl. Yellowness Index: Yellowness index (ASTM D-1925) was also measured on discs molded after one, three, and five passes, and oven-aged discs produced after one pass. Oven- aging conditions were 110°C for 22 hrs. Average results for two discs are shown in TABLE C. Two measurements per each side of each of the discs were made. The results indicate that, in HDPE, the solid solution prepared in Example No. 8 yields a less yellow polymer composition, after 5 passes through an extruder, than is achieved using DHT-4A under the same conditions. TABLE C. YELLOWNESS INDEX OF HDPE FORMULATIONS Pass Sample Color Pass Sample Color No. No. Index No. No. Index 1 9 9.20 1 Cl 8.73 1 9 (Aged) 9.94 1 Cl (Aged) 9.71 3 9 10.7 3 Cl 12.1 5 9 11.7 5 Cl 13.4 Example 10 and Comparative Example 2 A masterbatch containing 1% additive package and 99% unstabilized polypropylene (PP) (Fortilene PP 9600, Solvay, Deer Park, TX) was prepared by dry blending. The additives were 1000 ppm of a primary antioxidant (Irganox 1010, Ciba-Geigy, Batch #391204) , 500 ppm of a secondary antioxidant (Sandostab P-EPQ) , and 300 ppm of solid solution prepared according to Example 8. The masterbatch was initially extruded through a W&P ZSK30 co-rotating intermeshing twin screw extruder with an L/D of 40. The extrudate was then extruded four times through a Killion 1" single-screw extruder with an L/D of 20. Discs, denoted Sample No. 10, and each having a 0.077 inch thickness, were prepared by compression molding at 195 °C as follows: 2 min. pre-heating of pellets, 2 min. melting at 5,000 lbs, and 3 min. cooling at 5,000 lbs. To prepare Comparative Example 2, the composition of Example 10 was duplicated, with the exception that DHT-4A was substituted for the solid solution of Example 8. The masterbatch was extruded, and discs prepared, as described above, to prepare Sample No. C2. The Yellowness Index according to ASTM D-1925 was determined for Samples Nos. 10 and C2 as shown in TABLE D. Results indicate superior performance for Sample No. 10. TABLE D . YELLOWNESS INDEX 07 PP FORMULATIONS Pass Sample Color Pass Sample No . Color No . No . Index No . Index 1 10 6 . 4 1 C2 8 . 2 1 10 (Aged) 6 . 2 1 C2 (Aged) 6 . 5 3 10 11 . 2 3 C2 14 . 5 5 10 130 . 0 5 C2 16 . 1 Example 11: Corrosion Test The corrosion inhibition performance of the halogen scavenger of the invention was measured using the following procedure. Compounded formulations of minimally stabilized polymer and halogen scavenger, as set forth in Table F, were placed between polished (15 cm x 10 cm) steel plates. Three weighted plates, total weight 350 g, were placed on the sample test plates and the assembly was placed in a circulating air oven at 250°C, where it was heated for thirty minutes. The assembly was removed and, being careful not to touch the test surface of the test plate, it was stripped away from the resin sample. The test plate was allowed to stand in a humidity saturated chamber at 25°C for 12 hours. No part of the test plate actually touched water while in the humidity chamber. The corrosivity of the polymer was classified as none, slight, medium, high, or very high according to the appearances set forth in TABLE E. TABLE E Corrosivity Plate Appearance Classification None Glossy surface or no rust removed when wiped with a clean white paper towel . Slight Some small rust spots or slight streaking. The rust may be apparent only when wiped with a clean white towel. (The rust will appear very lightly on the towel.) Medium One or more clear rust spots . (These spots are clearly visible and wiping is not necessary. ) High All of the surface is covered with clear rust spots. Very High The rust is present over essentially the entire test area of the test plate. In TABLE F, "Ex. No. 6" refers to the solid solution prepared according to the procedure provided in Example No. 6, above. "Ex. No. 8" and "Ex. No. 3" have the corresponding meanings. TABLE F. CORROSION TEST RESULTS Polymer Halogen Concentration Corrosion Tested scavenger ppm Test Results Tested Virgin linear None 0 High low density Ex. No. 6 500 None Lot #ER 3003Z Ex. No. 8 500 Slight (Chevron) Ex. No. 3 500 Slight Polypropylene None 0 Medium Fortilene Ex. No. 6 500 None Lot# 9600 Ex. No. 8 500 None (Solvay) Ex. No. 3 500 None The data in TABLE F shows that each of the halogen scavengers tested was able to mitigate the corrosion properties of the two polymers tested. It will be appreciated by those skilled in the art that changes could be made to the embodiments described above without departing from the broad inventive concept thereof. It is understood, therefore, that this invention is not limited to the particular embodiments disclosed, but it is intended to cover modifications within the spirit and scope of the present invention as defined by the appended claims.

Claims: CLAIMS 1. A solid solution having the formula Al 2 (Mg) a (OH) b (C0 3 ) c (G) d -eH 2 0 and a crystallite size in the <003> direction of about 190 A to about 225 A, and having bidentate coordination for carbonate ion as shown by an infrared spectrum, and wherein 3 ≤ a ≤ 5.5; 8 __ b ≤ 14; 1.2 ≤ c ≤ 3 ; 0 ≤ d ≤ 1; 1 ≤ e ≤ 10 and G is a surface active agent. 2. A solid solution according to claim 1, wherein G is a metal salt of a C. 0 -C 22 saturated fatty acid. 3. A solid solution according to claim 2, wherein said metal salt of a C 10 -C 22 saturated fatty acid is selected from the group consisting of the sodium stearate, zinc stearate and calcium stearate. 4. A solid solution according to claim 1 having an infrared spectrum that displays a split absorption band in the region of 1415-1480 cm "1 . 5. A solid solution according to claim 1 having a tap density of about 0.1 g/cc to about 0.3 g/cc. 6. A solid solution according to claim 1 having a BET specific surface area of about 25 m 2 /g to about 40 πr/g. 7. A solid solution according to claim 1 wherein 4.1 ≤ a s 5.3; 10 . b s 12; 1.3 ≤ c s 3 ; 0 s d ≤ 0.5; 3 ≤ e ≤ 9. 8 . A method for inhibiting the corrosion-causing tendency and coloration of halogen-containing olefin polymers or copolymers , comprising incorporating about 0 . 01% to about 1% of the solid solution of claim 1 into an olefin polymer or copolymer. 9. A solid solution formed by a process comprising the steps: (a) heating an aqueous slurry comprising an aluminum compound selected from the group consisting of basic aluminum carbonate gel and aluminum hydroxide, and a magnesium compound selected from the group consisting of basic hydrated magnesium carbonate and magnesium oxide, wherein the molar ratio of magnesium to aluminum is about 1.5 to 2.75, to a temperature of about 70 °C to about 95 °C and for a reaction time "X" to provide a first slurry, where "X" is a period of time sufficient to achieve removal of substantially all free and loosely bound carbon dioxide from the aqueous slurry; (b) adding at least one surface active agent to said first slurry, to provide a second slurry; (c) heating said second slurry to a temperature of about 125 °C to about 140 °C for a time sufficient for a suspension test to be passed, where the suspension test takes an aliquot of said second slurry, removes the water therefrom to provide about 0.5 to about 0.6 g of dry solid solution in powdered form, combines the dry solid solution with about 100 mL deionized water to provide a suspension, and stirs the suspension vigorously for about five minutes, where the failure of the suspension to exhibit appreciable settling after stirring is completed indicates that the suspension test has been passed. 10. A solid solution according to claim 9 having an infrared spectrum that displays a split absorption band in the region of 1415-1480 cm "1 . 11. A solid solution according to claim 9, having a crystallite size in the <003> direction of about 190 A to about 225 A. 12. A solid solution according to claim 9 having a BET specific surface area of about 25 m 2 /g to about 40 2 /g. 13. A solid solution according to claim 9, wherein magnesium oxide is the magnesium compound, aluminum hydroxide is the aluminum compound, and a stream of carbon dioxide gas is passed through the second slurry at a rate sufficient to produce the solid solution. 14. A solid solution according to claim 9, wherein said surface active agent is a metal salt of a C 10 - C 22 saturated fatty acid. 15. A solid solution according to claim 14, wherein said surface active agent is selected from the group consisting of the sodium stearate, zinc stearate and calcium stearate . 16. A solid solution according to claim 9, wherein the basic aluminum carbonate gel has an Al 2 0 3 content of about 2% to about 20% by weight. 17. A solid solution according to claim 9, wherein said magnesium carbonate has a MgO content of about 40% to about 43.5% by weight. 18. A solid solution according to claim 9, wherein said aqueous slurry is heated for at least about 1 hour. 19. A solid solution according to claim 18, wherein said aqueous slurry is heated at a temperature of about 85 °C to about 90 °C for about 1.5 hours to about 2 hours . 20. A solid solution according to claim 9, wherein said second slurry is heated to a temperature of about 130 °C to about 135 °C for about 1.5 hours to about 2 hours . 21. A solid solution according to claim 9, further comprising the step of removing the water from said second slurry to provide a dry solid solution, and then micronizing said dry solid solution to provide particles having a particle size distribution wherein at least 99% of the particles are less than 44 microns in diameter, and at least 95% of the particles are less than 10 microns in diameter. 22. A solid solution according to claim 21, wherein the average particle size of the dry solid solution is about 4 microns to about 5 microns. 23. A solid solution according to claim 21 having a tap density of about 0.1 g/cc to about 0.3 g/cc. 24. A solid solution formed by a process comprising the steps: (a) heating an aqueous slurry comprising an aluminum compound selected from the group consisting of basic aluminum carbonate gel and aluminum hydroxide, and a magnesium compound selected from the group consisting of basic hydrated magnesium carbonate and magnesium oxide, wherein the molar ratio of magnesium to aluminum is about 1.5 to 2.75, to a temperature of about 70 °C to about 95 °C and for a reaction time "X" to provide a first slurry, where "X" is a period of time sufficient to achieve removal of substantially all free and loosely bound carbon dioxide from the aqueous slurry; (b) heating said first slurry to a temperature of about 125 °C to about 140 °C for about 1 to about 4 hours . 25. A solid solution according to claim 24, having an IR spectrum which displays a split absorption band in the region of 1415-1480 cm "1 . 26. A solid solution according to claim 24, having a crystallite size in the <003> direction of about 190 A to about 225 A.

Inventors: DESAI RAJANIKANT D, PAREKH JAWAHAR C, DESAI, RAJANIKANT, D., PAREKH, JAWAHAR, C.
Applicants: REHEIS INC, REHEIS, INC.
Application year: 1995
Main classification: C08K3
IPC codes: C07F5, C08K3, C08K5, C08L27