Process for the solid state polycondensation of polyester resins

Abstract: Process for the solid state polycondensation of polyester resins, where an inert gas is circulating in a moving bed of polymer at a temperature between 180° and 230°C, characterized by the fact that the ratio by weight between the gas rate of flow per hour and that one of the discharged polymer is lower than 0.6.

Description: The present invention relates to a process for the solid state polycondensation of polyester resins. The aromatic polyester resins, particularly three of them, the polyethyleneterephthalate (PET), the copolymers of the terephthalic acid with minor proportions of isophthalic acid and polybuthyleneterephthalate find wide application both in the fibres and the films area, or as molding material. While for fibres and films the intrinsic viscosity of the resin is in general between 0.6-0.75 dl/g, for the molding material are necessary higher values, which with difficulty are directly obtainable by the polycondensation process of the resin. The intrinsic viscosity is increased to the required values (in general higher than 0.75 dl/g) by means of SSP processes of the resin, at a temperature in general between 190° and 230°C. The starting resin used for the SSP process is in the amorphous state; it is necessary to take it to a sufficient degree of crystallinity before it is submitted to the SSP process. The crystallisation is necessary in order to avoid polymer chips stocking in the polycondensation reactor that is in general formed by a vertical moving bed where the polymer filled from the top is passed through by an inert gas stream which removes the volatile residual products of the polycondensation reaction (ethylene glycol and acetaldehyde in the case of polyethyleneterephthalate). The products removal of the polycondensation reaction is a fundamental requisite for the development of the same reaction. Various reactions occur during the polycondensation. The main reaction, that leads to the increase of the PET molecular weight is the removal of ethylene glycol: Other reactions lead to the esterifications of carboxylic end-groups and to the formation of acetaldehyde. The polycondensation and esterification reactions are reversible while the reactions leading to the acetaldehyde formation are irreversible and of various type. They include the degradation reaction of the polymeric chain with the formation of a vinylester end-group, which reacting with an OH end-group eliminates acetaldehyde; the reaction of the vinylester group with a COOH end group with formation of an anhydride group and acetaldehyde removal; the degradation reaction of hydroxyethylic end groups with acetaldehyde formation. The acetaldehyde removal from the polymer at levels lower than few ppm is a fundamental requisite in the case of PET for the production of items for food uses, such as mineral water bottles. As already indicated, the residual products of the polycondensation reaction are eliminated by passing an inert gas stream equi- or countercurrently with the feeding of polymer coming from the crystallisation stage. The polycondensation reaction is in general carried out in a tubular reactor with moving bed, wherein the polymer enters from the top and comes out from the bottom and an inert gas stream is passed over the polymer. In US patent No. 4 064 122 there are described process of this type, where the granular polymer is crystallized up to a degree of density of at least 1.390 g/cm 3 , operating in crystallizers with forced movement at a temperature between 220° and 260°C and effecting then the polycondensation reaction in a reactor with moving bed, operating at temperatures equal or lower than those used in the crystallization step. The temperature in the crystallization step is in general between 230° and 245°C and the process is carried out till to obtain crystallinity values corresponding to 1.403-1.415 g/cm 3 density. A temperature between 230° and 245°C is used in the polycondensation step to obtain an optimal value of the reaction speed combined with a low degree of polymer degradation. An inert gas, preferably nitrogen, is used to remove the residual products formed in the polycondensation stage. The gas is recycled after by-products purification. The polymer undergoes hydrolysis decompositions when the water content exceeds that one above indicated. The reaction speed is influenced negatively, when the glycol content exceeds the above indicated one. High contents of oxygen and acetaldehyde cause discoloring in the shaped article and high contents of acetaldehyde are not allowed in the shaped articles for food use. To limit the purification costs of the gas recycling and the energy costs for the maintenance of the gaseous flow, the ration by weight between the gas rate of flow per hour and the rate of flow per hour of the polymer leaving the reactor has to be maintained between 0.7:1 and 3:1 preferably between 1:1 and 2:1. By using values lower than 0.7 (0.5 and 0.3 in the examples) and operating in the conditions set forth in US patent No. 4 064 112 patent (crystallization temperature 235°C and polycondensation temperature 230°C) the intrinsic viscosity of the polymer does not increase significantly. By using ratios lower than 0.7, there is an increase of the temperature difference through the reactor section. US patent No. 4 161 578, describes a solid state crystallization/polycondensation process where the polymer in chips is crystallized in an equipment with forced movement, acting at temperatures between 180° and 235°C till to obtain a crystallinity degree corresponding to at least 1.385 g/cm 3 of density and subsequently fed to a polycondensation moving bed reactor, where the polymer is heated to temperatures higher than those used in the crystallization step. Nitrogen is circulated in the polycondensation reactor in countercurrent with the polymer feed with a ratio by weight between the rates of flow comprised from 0.7 to 3.5 kg N 2 /kg PET. It has been unexpectedly found that even using ratios R between the rate of flow per hour by weight of inert gas fed to the polycondensation reactor and the rate of flow per hour by weight of the polymer coming out of the reactor lower than those considered till now as limit values, below which interesting results could not be obtained, it is possible to effectively remove the by-products of the polycondensation reaction, thus obtaining high reaction kinetics. The present invention is as defined by present Claim 1. It has furthermore been unexpectedly found that the exothermic heat of the reaction decreases using low R ratios; this allows to better control the thermal profile in the SSP reactor and to improve also the plant operability. The usable R ratio is lower than 0.6 and preferably comprised between 0.2 and 0.5. The use of such low ratios allows considerable energy savings in the gas blowing operation. In the invention process the polycondensation reaction is carried out at temperatures between about 180°C-220°C. The polymer to subject to the SSP reaction has a crystallinity degree comprised between 40 and 50% by weight and it is fed as chips. Preferably, the crystalline organization of the polymer is such that the pre-melting peak appearing in the DSC curve is shifted toward temperatures higher than those used in the reaction. Results of this type are obtainable by operating, according to the crystallization process described in the Applicant's European application EP-A-0712703.0 In the process described in the application, the chips of the amorphous polymer are at first submitted to a crystallization process carried out in a fluidized bed and then to crystallization processes in two mechanical mixers, the first working at a temperature between 10° and 30°C higher than that of the fluidized bed and the second one at a temperature corresponding to that used in the next SSP reactor. The inert gas stream coming out from the SSP reactor is submitted to purification processes for the removal of the organic products impurities therein present. The process is described in W095/02446 application. The average residence times in the SSP reactor are such as to obtain an increase of the polymer intrinsic viscosity of at least 0.1 dl/g; they are in general comprised between 5 and 20 hours. The kinetics of the intrinsic viscosity increase can be considerably increased if the polymer is blended in the molten state, in a step previous to that of crystallization, with a polyfunctional compound containing two or more groups capable of reacting with condensation or addition reaction with the OH and COOH end groups of the polyester. The pyromellitic anhydride, and in general the dianhydrides of tetracarboxylic aromatic or aliphatic acids are examples of such compounds. These compounds are used in a quantity comprised in general between 0.1 and 2% by weight on the polymer. The pyromellitic anhydride is the preferred compound. The use of these compounds is described in the European patent 422 282 and in US patents No. 5 243 020, 5 334 669 and 5 338 808 whose description is herewith incorporated by reference. The polyester resins used in the crystallization process of the invention comprise the polycondensation products of C 2 -C 20 diols such as ethylene glycol butylene glycol, 1,4 cyclohexandimethyol with aromatic bicarboxylic acids, such as terephthalic acid, 2,6 naphthalene bicarboxylic acid or their reactive derivatives such as the lower alkyl esters such as for example, dimethyl terephthalate. Polyethyleneterephthalate is the preferred resin. Besides the terephthalic units also units deriving from other bicarboxylic acids such as the isophthalic acid and the naphthalendicarboxylic acids can be present in a quantity of about 0.5-20% by weight, preferably 1-20% by or of isophtalic acid units. The following examples are given to illustrate but not to limit the invention. Example 1 A polycondensation test in the solid state was carried out in a continuous reactor with moving bed and with a rate of flow of solid of 50 kg/h. The used resin is a copolyethyleneterephthalate containing a percentage by weight of isophthalic acid of 2.2%. The starting intrinsic viscosity was 0.60 dl/g and the acetaldehyde content of 35 ppm. A polymer with a final intrinsic viscosity of 0.80 dl/g was produced keeping constant the average temperature of the reactor and changing only the inert gas quantity fed (nitrogen) (changing therefore the R ratio). The average residence time was 12 hours. The fed nitrogen contained less than 10 ppm of organic compounds expressed as methane equivalent. The obtained results are shown in Table 1. Example 2 By using the same reactor, the same polymer and the same inert gas, as in example 1, some tests were carried out using different temperatures of inert gas. The obtained results are shown in Table 2. Comparative Example 1 The test of example 1 was repeated using an R ratio of 1, keeping constant the average chips temperature at 210.1°C and the residence time at 12h. The intrinsic viscosity of the obtained polymer was of 0.80 dl/g. Test No. 1 2 3 4 5 Nitrogen quantity kg/h 5 10 15 20 25 R Nitrogen/chips 0.1 0.2 0.3 0.4 0.5 Average temperature °C 210.1 210.1 210.2 210.3 210.4 Max. Temp. chips °C 210.5 210.5 210.7 210.8 211.0 IV final 0.800 0.800 0.801 0.799 0.802 IV Max. 0.803 0.803 0.805 0.803 0.806 IV Min. 0.797 0.796 0.798 0.795 0.799 Test No. 1 2 3 4 Nitrogen quantity kg/h 10 10 10 10 Gas temperature °C 200 220 180 160 R Nitrogen/chips 0.2 0.2 0.2 0.2 Mid. Temp. of chips °C 210.1 210.3 210.1 210.0 Max. Temp. of chips °C 210.5 210.6 210.5 210.4 IV end 0.800 0.801 0.799 0.799

Claims: Continuous process for the solid state polycondensation of crystallised aromatic polyester resins, wherein the resin is fed from the top of a moving bed reactor and discharged from bottom, an inert gas is circulated countercurrent or equicurrent with the resin, with resin average residence time enough to obtain an increase of polymer intrinsic viscosity of at least 0.1 dl/g and a ratio R by weight between the gas rate of flow per hour and the rate of flow per hour of the polymer discharged from reactor lower than 0.6, characterised in that said resins have a degree of crystallisation from 40 to 50% and are obtained by crystallisation at first in a fluidised bed at temperatures from 210° to 225°C, then in mechanical mixers first at temperatures 10° to 30°C higher than the temperature in the fluidised bed and finally at a temperature corresponding to that used in the solid state polycondensation reactor, the temperature in said reactor being kept between 180° and 220°C. Process according to claim 1, where R ratio is comprised between 0.2 and 0.5. Process according to claims 1 and 2, where the temperature in the reactor is comprised between 190° and 210°C. Process according to claims 1, 2 or 3, where the inert gas is nitrogen. Process according to claim 4, where the nitrogen is circulating in equicurrent with the polymer. Process according to the previous claims, where the polyester resin is polyethyleneterephthalate or copolyethyleneterephthalate containing from 1 to 20% of isophtalic acid units. Process according to the previous claims, where the nitrogen is recycled to the reactor after having been submitted to a purification process of the organic impurities till to obtain values lower than 10 ppm expressed as methane equivalent.

Inventors: AL GHATTA HUSSAIN ALI KASHIF, GIORDANO DARIO, AL GHATTA, HUSSAIN ALI KASHIF, GIORDANO, DARIO
Applicants: UOP SINCO S R L, UOP SINCO S.R.L.
Application year: 1995
Main classification: C08G63
IPC codes: C08G63