CHEMICAL MODIFICATION OF SHAPED HYDROGELS IN NON-AQUEOUS MEDIUM

Abstract: A method is described for the chemical modification of pre-shaped hydrogels in non-aqueous medium. The conditions permit the reaction of highly expanded, porous hydrogel particles, such as spherical beads, using pseudo homogeneous reaction conditions in the absence of water. The method involves a three step procedure in which the porous gels are solvent exchanged into a water-free solvent (step 1) with minimal change in gel dimension and porosity; followed by reaction under non-aqueous condition (step 2); and followed by solvent exchange into water (step 3). Many different types of reactions requiring non-aqueous conditions may be carried out using these conditions. The method has particularly been demonstrated for crosslinking fluorinating beads, and for esterifying beads in a reaction involving multifunctional free carboxylic acids in the presence of dicyclohexylcarbodiimide (DCC).

Description: CHEMICAL MODIFICATION OF SHAPED HYDROGELS IN NON-AQUEOUS MEDIUM DESCRIPTION BACKGROUND OF THE INVENTION Field of the Invention The invention is directed to a method of chemically modifying a cellulosic hydrogel as a sorptive support material such as a cellulose bead. More particularly, chemical modifications are done on solvent exchanged cellulose beads in a stringently non-aqueous environment. Description of the Prior Art Hydrogels are a class of organic substances capable of retaining and "immobilizing" water in a gel state having low solids content. Hydrogels usually consist of large organic macromolecules, and are hydroxy functional polymers capable of supporting a porous network structure. Porous hydrogels are useful materials in conjunction with sorption, flow, and separation processes involving aqueous solutions. Although hydrogels can be produced in various shapes and forms, such as films, fibers, and spherical "beads", they are most commonly used in bead form because of the ability to pack beads into continuous flow columns. Beaded hydrogels from such water-insoluble polysaccharides as dextrans and cellulose have gained practical importance in the separations industry. Cellulosic hydrogel beads have particularly attractive characteristics in terms of flow, strength, and pore (or network) dimensions. Polysaccharide gels are often materials with less than 25% solids content when drained of all free water; and solids content may be as low as 2% in the case of cellulosic beads. Hydrogels from polysaccharides are generated from solution state by crosslinking or precipitation in a non-solvent following such a shape formation procedure as atomization. Polysaccharidic hydrogels have excellent properties in terms of crush resistance when exposed to flowing streams of water. Owing to their network structure and/or porosity, they are capable of accommodating large macromolecules (e.g., MWs of 5-500,000) such as proteins and enzymes, in their pore structure. Shaped hydrogels from polysaccharides are limited by the fact that they lack specific bonding sites capable of separating and distinguishing • different water-soluble molecules on grounds of specific functionality. This apparent inactivity is usually overcome by the reaction of hydrogels in aqueous medium, usually in aqueous alkali, and in reactions usually producing ethers. Activation/functionalization of hydrogels from polysaccharides involving aqueous alkali represent state-of-the-art hydrogel modification techniques. Although this procedure prevents the complete desiccation of the solids leading to the formation of an amorphous glassy structure, this type of modification results in dimensional changes that alter the porosity and network dimensions of the activated gel structure. Not only is the chemical modification of pre-shaped hydrogels limited to aqueous medium, this also results in loss of porosity. No method exists today, or has been described in the state-of-art, that permits the modification of a pre-shaped hydrogel in non-aqueous medium without loss of gel structure. SUMMARY OF THE INVENTION It is an object of this invention to provide an improved method for chemically modifying cellulosic hydrogels. It is another object of this invention to provide a method to modify, by chemical reaction, an expanded hydrogel, formed in a shape desirable for its end use, in reactions requiring non-aqueous medium, while avoiding pore structure collapse. According to the invention, a pre-formed cellulose bead or other cellulosic support material that is present in hydrogel form is altered by replacing the water in the cellulosic support material with a non-aqueous solvent s ch' as tetrahydrofuran, benzene, toluene or the like. After the water is exchanged for a non-aqueous liquid, esterification, etherification, carbanilation (i.e., reaction with an isocyanate) or other reactions can be performed utilizing non- aqueous chemistry to make cellulose derivatives. By eliminating the water, competition with the hydroxy sites on the cellulose backbone by the water molecules is eliminated; thus, modification of the cellulose can proceed with reagents that would also react with water if it were present, such as acid anhydrides, acyl chlorides, isocyanates, etc. After the cellulose support material has been modified as desired, the non- aquous solvent is replaced with water. The invention has particular application in producing beads used for column chromotography, agglutinations, and Other separation techniques wherein a particular analyte in a b solution is bound to the particular functional groups which have been covalently bonded to the cellulose backbone via the modification procedure of this invention. In addition, depending upon the functional groups added to the cellulose backbone, the modified cellulose materials may be used as sorbents for separating chemicals in a waste stream. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION The invention addresses a method for solvent exchanging expanded hydrogels from water into a water-free solvent in which the desirable non-aqueous reaction is to be performed (step 1) ; followed by the reaction (step 2); followed by renewed solvent exchange from the non-aqueous solvent into water (step 3). Solvent exchange of expanded hydrogels makes it possible to perform reactions in pseudo homogeneous phase in non- aqueous medium which are not possible in aqueous medium. The method allows the modification of hydroxy sites on both the inside and outside of the hydrogel structure. Modification reactions may address such properties as hydrophobicity, crosslinking, activation, functionalization, and others. Scheme 1 shows the reaction processes of the present invention where an acid, an acyl chloride, an anhydride or an isocyanate is combined with cellulose and an optional catalyst to produce an ester or a urethane (carbanate) derivative. X= OH, Halogen, OCOR orotheractivating groups Y= N orC In the process, a solvent exchange of water into an organic such as tetrahydrofuran (THF) , followed by exchanged back into water following modification is used. Other organic solvents could be used in place of THF for affecting the non-aqueous reaction chemistry, including dioxane, benzene, toluene, xylene, and others. In case of solvents immiscible with water but miscible with alcohols, solvent exchange may proceed stepwise from water into methanol, and from methanol into the water- immiscible solvent such as benzene. The reaction process retains the dimensional characteristics of the shaped hydrogel. Data on the shaped hydrogels which have been derivatized according to the reaction scheme have demonstrated a retention of expanded shape in excess of 70% of the original. Thus, the solids content of the beads changes insignificantly during the process of water removal. Chemically modified cellulosic hydrogels in bead form are prepared by solvent exchanging never- dired beads with a water miscible, but non-aqueous solvent in which the reaction typically proceeds. Among qualifying reactions are esterifications- ith anhydrides or acyl chlorides in THF or dioxane. The reactions may also involve the free carboxylic acids in connection with such catalysts as dicyclohexylcarbodiimide (DCC) , 4- pyrrolidinopyridine (PP) , or tosyl chloride (TsCl) as described in the co-pending application having U.S. Serial No. to Glasser et al., entitled "Cellulose Derivatives with a Low Degree of Substitution", which is concurrently filed on even date with this application and is herein incorporated by reference. Another embodiment of this invention involves the use of NCO-functional chemical substances, isothyonates, capable of reacting with OH-functional cellulosic beads in the presence of such suitable catalysts as organic tin compounds . The modification reaction may involve complex reagent species with hyighly complex chemistries that target specific sorption tasks. Among these are carboxyl, sulfhydryl (mercapto-) metal chelating, etc., functionalities. By employing freshly cut potassium or sodium 5 metal as desiccant in the non-aqueous solvent being used for replacing water, all traces of moisture can rigorously be excluded from the cellulosic beads. The use of moisture indicators, such as benzophenone, may optionally assist in determining 0 conditions sufficiently anhydrous for reactions to proceed expediently and efficiently. These conditions are qualified to retain the expanded gel structure of the cellulosic hydrogel beads without destroying or significantly diminishing their 5 porosity. All solvents can be recovered once the modification reaction has been performed and the beads have exchanged back into aqueous medium. Solvents can efficiently be recycled by 0 distillation. Applications contemplated under this invention are chromatographic support media, sorbents for water purification, heavy metal concentration and removal, pesticide complexation, and many others. *5 EXAMPLE 1 Cellulosic beads are immersed in THF and allowed to exchange with the water inside the 0 beads. The THF was filtered away, and then replaced with a fresh batch of THF. The beads were then placed into a soxhlet extraction apparatus, which was fitted with a source for producing a dry nitrogen atmospher. In the sump flask, THF was refluxed over freshly cut potassium metal. Sodium metal could be used as a substitute for potassium. A tablespoon of benzophenone was added as a calorimetric indicator of dryness. The beads were dried until a blue color persisted and the resulting product was designated as "solvent exchanged beads" . EXAMPLE 2 The solvent exchanged beads of Example 1 were reacted with simple carboxylic acids or carboxylic acids having secondary functionalities such as mercapto, or protected mercapto groups. Reaction with Benzoic Acid Solvent exchanged beads (3.8 g THF-wet weight, 0.774 g dry weight) was added to a THF (15 mL) solution of benzoic acid (1.75 g, 1 eq/OH) and dicyclohexylcarbodiimide (5.90 g, 2 eq/OH) . A catalytic amount of pyrrolidinopyridine (e.g., less than 0.1 eq/OH and preferably 0.01 eq/OH) was added to the solution and then the mixture was stirred at room temperature under a nitrogen atmosphere for 18 hr. The beads were then isolated by filtration on a sintered glass funnel. After washing with methanol and then with THF, the beads were stored in THF at 0°C. The amount of benzoyl groups on beads were determined as methyl benzoate by methanolysis/gas chromatrography. The procedure involved the treatment of 30 mg of dry beads with 1.0 M sodium methoxide/methanol (2 mL, with 3 mg/mL methyl-2-methyl benzoic acid as the internal standard) in a 3 mL vial at 50°C for 18 hr. The supernatant was passed through a disposable silica gel cartridge to remove NaOMe. A portion of the filtrate was injected into the gas chromatograph. The reaction yielded a material with a degree of substitution (DS) of 0.4. EXAMPLE 3 Reaction with S-protected Mercaptopropionic Acid Solvent exchanged beads (20.45 g THF-wet weight, 2.8 g of dry cellulose) was added to a solution of 3- (2-pyridyldithio)-propionic acid (1.86 g, 0.5 moles/anhydroglucose unit (sugar units in cellulose)), dicyclohexylcarbodiimide (3.72 g, 2 eq./acid) and 4-pyrrolidinopyridine (30 mg, catalytic amounts (0.01 eq/OH)) at room temperature under under nitrogen atmosphere. After a 24 hr reaction time, the beads were filtered in a sintered glass funnel and were washed with THF followed by methanol. The beads were stored in methanol at 0°C. The extent of derivatization was determined by treating beads with dithiothreatol (DTT) and spectrophotometric (UV) determination of liberated 2-thiopyridine. The activity for the beads thus calculated were 66.52 μmoles/mL, a value higher than what is available for similar commercial materials. For example, thiopropyl agarose available from Sigma Chemicals has an activity of 20-35 μmole/ir-L. Reaction Scheme 2 presents the reaction of Example 3. DTT = HSCH 2 CH (OH) CH (OH) CH 2 SH EXAMPLE 4 The solvent exchanged beads of Example 1 were transferred into a dry 250 mL round bottom flask. This flask was fitted with rubber septum, dry nitrogen atmosphere, and magnetic stir bar. Anhydrous THF, 20 mL, was added to the flask at an amount just enough to cover the beads. The flask was cooled to -70°C in a dry ice/acetone bath. Dimethyl amino sulfur trifluoride (me-DAST), 4.5 mL (46.1 mmoles), was added slowly to the flask while slowly stirring the beads which were warmed from SUBSTπUTtSHFfPll'F?^ -70°C to 0°C over a period of five hours. Subsequently, the beads were maintained between -20°C and 0°C for a period of 3.5 hours. The flask was then removed from the cooling bath, and allowed to warm to room temperature. Quickly, the beads were poured into 200 mL of ice water containing excess NaHC0 3 . At this time, the beads were still transparent and completely spherical. After remaining in bicarbonate solution over night, the beads were exchanged with a large amount of distilled water into aqueous environment. These beads were insoluble in all organic solvents including DMAc/LiCl; and they had a fluorine content of approximately 3%. While the invention has been described in terms of its preferred embodiments, those skilled in the art will recognize that the invention can be practiced with modification within the spirit and scope of the appended claims.

Claims: CLAIMS We claim: 1. A method for forming cellulose derivatives, comprising the steps of: replacing a first quantity of water from hydrogel cellulose support materials with an organic fluid; reacting a compound with hydroxy sites on cellulose polymers in said cellulose support materials; and replacing said organic fluid in said cellulose support materials after said first replacing step with a second quantity of water. 2. The method of claim 1 wherein said hydrogel cellulose support materials are selected from the group consisting of beads, films, and fibers. 3. The method of claim 1 wherein said hydrogel cellulose support materials have both an exterior surface and an internal dimension and wherein hydroxy sites on said cellulose polymers in said hygrogel cellulose support materials which are reacted during said reacting step are both inside said internal dimension and on said exterior surface. 4. The method of claim 1 wherein said a solids content and size dimension of said hydrogel cellulose support material after said second replacing step is within 30% of a solids content and size dimension of said hydrogel cellulose support material prior to said first replacing step, whereby said hydrogel cellulose support material remains intact without diminished porosity after said replacing and reacting steps.

Inventors: FRAZIER CHARLES E, GLASSER WOLFGANG G, SAMARANAYAKE GAMINI, FRAZIER, CHARLES, E., GLASSER, WOLFGANG, G., SAMARANAYAKE, GAMINI
Applicants: INNOVATIVE TECH CENTER, THE CENTER FOR INNOVATIVE TECHNOLOGY
Application year: 1995
Main classification: C08B3
IPC codes: C08B3, C08B5, C08B7, C08B11, C08B13