COATING SYSTEM FOR GLASS STRENGTH RETENTION

Abstract: This invention provides an improved coating composition for glass substrates that comprises a poly(siloxane). The introduction of a poly(siloxane) in a coating composition for a glass substrate, and in particular an optical fiber, acts to delay the rate of deterioration of the glass or optical fiber due to moisture, and improves adhesion between the glass substrate and the coating composition. The introduction of a poly(siloxane) into a polymeric coating composition also improves the interlayer adhesion when more than one coating is applied to a glass substrate. This invention further relates to an outer primary coating composition or matrix material that comprises an acid functional ethylenically unsaturated monomer. This invention also provides an improved coated glass substrate having a decreased rate of deterioration due to moisture, improved adhesion between the glass substrate and the coating composition and between the various coatings, wherein the coating composition comprises a poly(siloxane).

Description: COATING SYSTEM FOR GLASS STRENGTH RETENTION Technical Field This invention relates to an improved coating composition for glass substrates and to glass substrates, such as optical fibers, coated with the composition. Background of the Invention It has long been known that glass substrates are weakened upon exposure to water. For example, moisture in air can cause weakening and the eventual breakage of glass. Typically, glass substrates have been coated with polymeric compositions for various reasons, such as to protect and preserve the strength of a glass object, to prevent damage during handling, and to prevent moisture from attacking the glass substrate. In addition, coatings have been applied to optical fibers to decrease the microbending of the optical fiber, which can reduce the transmission of electromagnetic radiation through the fiber. However, it has been found that many coating compositions are water permeable and therefore not very effective in protecting the glass substrate from moisture. In addition to causing the weakening of glass substrates, moisture can also cause polymeric compositions that have been applied to the glass substrate to break away, i.e., delaminate, from the glass surface. The delamination of a polymeric composition can result in a weakened glass substrate, as the polymeric coating no longer protects the glass from environmental stresses. Various coating compositions have been used to prevent the deterioration of glass substrates, and specifically optical fibers, to improve the useful life of the glass substrate to which it is applied. For example, U.S. Patent No. 5,000,541, issued to DiMarcello et al. teaches a method for hermetically sealing an optical fiber with carbon, which prevents water from contacting the optical fiber, and thus prolongs the useful life of the optical fiber. Similarly, U.S. Patent No. 4,849,462, issued to Bishop et al., teaches the incorporation of various organofunctional silanes into a coating composition to improve the adhesion between a coating composition for an optical fiber and the optical fiber, particularly in moist environments. Likewise, U.S. Patent No. 5,214,734, issued to Inniss et al., teaches the incorporation of particulate silica in a polymeric coating composition to increase the fatigue resistance of an optical fiber or glass to moisture. Many coating compositions have drawbacks that make them unsuitable for certain applications. For example, some of the compositions may be too expensive to use in the production of low cost optical fibers or glass objects, and the introduction of particulate matter into a coating composition as disclosed in the Inniss et al. patent can present problems such as scratching of the pristine optical glass fiber, resulting in breakage at low tensile loads; a turbid coating composition which has a tendency to gel; and other processing problems that are commonly encountered when working with particulate matter. Coatings which are modified with organofunctional silanes, such as the above referenced Bishop et al. patent, do improve the wet adhesion of a coating applied to an optical fiber substrate, but do not significantly improve the glass strength retention capability of the coating, when compared to this invention. Summary of the Invention This invention provides an improved coating composition for glass substrates, preferably silica-based optical fibers, wherein the composition comprises a poly(siloxane) having the formula: wherein Y and Z are independently selected from the group consisting of halogen, amino, alkyl and alkoxy; n is one or more and X-_ , X 2 , X 3 or X 4 is independently a hydrolyzable group that can be hydrolysed from the poly(siloxane) in the presence of water. Preferably, n is two or more, X is alkoxy and the coating composition is UV curable. Preferably, the poly(siloxane) is present in a radiation curable coating composition in an amount in the range of about 0.1% and about 50% by weight of the entire composition. More preferably, the poly(siloxane) is present in the coating composition in an amount in the range of about 0.1% to about 30% by weight of the entire composition and most preferred in the range of about 0.5 to about 10%. This invention also provides improved glass substrates that are coated with a composition that comprises a poly(siloxane). The resulting coated glass substrate has a decreased rate of deterioration due to moisture attack, improved adhesion between the glass substrate and the coating adjacent to the glass, and improved adhesion between coating layers if more than one coating layer containing a poly(siloxane) is applied to the glass substrate. Brief Description of the Drawings Figure 1 is a cross-sectional view of an optical fiber having two coatings. Figure 2 is a cross sectional view of an optical fiber having one coating. Detailed Description of the Preferred Embodiments The present invention contemplates a glass substrate, and specifically, a silica-based optical fiber that is coated with at least one polymeric coating composition. Most glass substrates, such as glass bottles, are usually coated with only one polymeric coating. An optical fiber substrate, however, usually has more than one coating. When a substrate has more than one coating, the various coating compositions may be the same or different. As used herein, the word "substrate" shall mean a glass object or a silica-based optical fiber. Some examples of glass objects include, but are not limited to, bottles, light bulbs, windows. In a preferred embodiment, the glass substrate is a silica-based optical fiber. The present invention is directed to an improved coating composition that comprises a poly(siloxane). Examples of hydrolyzable groups X lf X 2 , X 3 or X t in formula (1) include, but are not limited to, halogen (e.g. chlorine, fluorine and bromine), formyloxy, acetoxy, propyonoxy, valeryloxy, steaoryloxy, benzoyloxy, naphtoyloxy, toluyloxy, maleoyloxy, alkoxy, alkylthio, vinyloxy, allyloxy, vinyletherox , methacryloxy and acryloxy. These and other groups herein are defined according to the IUPAC Nomenclature Rules (1969). Preferably, in the poly(siloxane) according to formula (1), n is two or more and each X is alkoxy. Preferably the alkoxy group is a C- ^ -C^ alkoxy, more preferably a C^Cg alkoxy. Upon hydrolysis Ci-Cg alkoxy groups form volatile alcohols, which can escape from the coating composition by evaporation. Examples of such C- L -C 8 - alkoxy groups include, but are not limited to, methoxy, ethoxy, isopropoxy, n-butoxy, sec-butoxy, isobutoxy, tert- butoxy. Most preferably, the alkoxy groups are methoxy or ethoxy. The addition of a pol (siloxane) to the polymeric composition delays glass strength deterioration, provides excellent wet adhesion of the coating to a substrate and improves adhesion between adjacent coating layers that both contain a poly(siloxane) . Glass strength deterioration can typically be measured by industry standard static and/or dynamic fatigue tests. The poly(siloxane) may be added to various coating compositions that are known in the art. For example, U.S. Patent No. 5,112,658, to Skutnik et al., issued May 12, 1992, discloses coating compositions for glass containers. The Skutnik et al. patent is hereby incorporated by reference. Preferably, the substrates used in the present invention are mostly silicon-based. The addition of poly(siloxane) to a polymeric coating composition provides for better strength retention of the substrate coated therewith. When the hydrolyzable group contains ethylenic unsaturation, the ethylenic unsaturation may react with other ethylenically unsaturated compounds in the coating composition. Such hydrolyzable groups containing an ethylenic unsaturation include, but are not limited to, vinyloxy, allyloxy, vinyletheroxy, methacryloxy or acryloxy. It is contemplated that the siloxane main chain may be linear or branched. A branched structure results when some Xs in formula (1) are siloxane groups. Preferably the pol (siloxane) has the following general structure: wherein p is 2 or more. A particularly preferred methoxy functional poly(siloxane) is Dow Corning 1-6184. Preferably, the poly(siloxane) is a liguid so that it may be easily added to a coating composition. Alternatively, the pol (siloxane) may be a solid that is soluble in the polymeric coating composition. The improved coating compositions of the present invention may contain the poly(siloxane) or it may contain a mixture of poly(siloxane)s. Typically, the poly(siloxane) is present in the coating composition in an amount sufficient to delay deterioration of the substrate upon which the composition containing the poly(siloxane) is coated. Preferably, the poly(siloxane) is present in the coating composition in the range of about 0.1% to about 50% by weight of the entire composition. However, an effective amount of poly(siloxane) for a particular coating composition may vary and can be determined by trial and error. Glass substrates are typically coated with only one coating composition. An optical fiber substrate, however, may be coated with more than one coating composition. In a substrate having more than one coating composition, such as an optical fiber, the various coatings may have the same composition or the coatings may have different compositions. For example, some of the coatings may contain a poly(siloxane) and some of the coatings may not. The compositions according to the present invention may be used as an inner primary coating. When used as an inner primary coating the composition is preferably formulated such that, when cured, the composition results in a coating having a T g below about 23°C and a modulus in the range of about 0.1 to about 50 MPa. More preferably, the T g is below 0°C and the modulus is in the range of 0.1 to 10 MPa. In certain applications, it is desirable to use a matrix composition to hold a plurality of optical fibers together, and various matrices and their use are known to those skilled in the art. For example, a matrix composition can be the same as the outer primary coatings exemplified herein. It is contemplated that a poly(siloxane) may be incorporated into the matrix composition. Also contemplated are optical fiber ribbons, which are known to those skilled in the art, that comprise a matrix material that comprises the poly(siloxane) . Preferably, the outer primary coating composition, when cured, results in a coating having a T g above 23°C and a modulus in the range of about 100 to about 3,000 MPa. Most preferably, the outer primary coating composition, when cured, results in a coating having a T g above 40°C and a modulus in the range of about 300 to about 2,000 MPa. Figure 1 illustrates a coating configuration that is available in the optical fiber industry. The central substrate labeled 1 is a glass substrate, in this case, a silica-based optical fiber. The coating layer 2, which is directly adjacent to the glass, is typically termed the inner primary coating or innermost layer. The coating layer 3 that surrounds the inner primary coating is typically termed the outer primary coating. As used herein, the term "inner primary coating" is any coating directly adjacent to a silica-based optical fiber, while the term "outer primary coating" will apply to any coating or coatings which overcoats the inner primary coating, including an ink. Figure 2 illustrates another coating configuration for glass substrates, which is also available in the optical fiber industry. The central substrate labeled 4 is the glass substrate, in this case, a silica-based optical fiber. The sole coating layer labeled 5 is generally termed a single coat and is characterized by the fact that it is the only coating layer present on the glass substrate. As used herein, the term "single coat" is any coating adjacent to a glass optical fiber substrate that is not immediately overcoated. It is understood that any or all of the coating layers described including the inner primary, outer primary and matrix, may independently contain a poly(siloxane) to obtain the glass strength retention benefit. In one embodiment of the present invention, the outer primary coating contains a poly(siloxane) to obtain the strength retention benefit. The addition of the poly(siloxane) to the inner primary coating, in addition to obtaining the glass strength retention benefit, has the additional desired benefit of improving the adhesion of the coating to the glass under high humidity conditions. A coating composition of the present invention may be prepared by combining curable oligomers, monomers and/or polymers along with other components and the selected pol (siloxane). For example, the oligomers useful in the compositions of the present invention may be the reaction product of a hydroxy functional monomer containing ethylenic unsaturation and an isocyanate that is then further reacted with a hydroxy functional polyether that contains branched, oxyalkylene repeating units. The branched, oxyalkylene repeating units have about 2 to about 6 carbon atoms. The resulting oligomers have molecular weights that are generally in the range of about 700 to about 20,000, and preferably about 1000 to about 10,000. They are also substantially free of isocyanate functionality. These end-capped oligomers can be combined with reactive diluents, photoinitiators, antioxidants and light stabilizers to form the curable compositions of the present invention. Any of a wide variety of organic polyisocyanates, alone or in admixture, can be reacted with the hydroxy functional monomer containing ethylenic unsaturation. The reaction product of the isocyanate and the hydroxy functional monomer is then further reacted with the polyether containing branched chain, oxyalkylene repeating units to form polyether oligomers. Representative diisocyanates include isophorone diisocyanate (IPDI), toluene diisocyanate (TDI), diphenylmethylene diisocyanate, hexamethylene diisocyanate, cyclohexylene diisocyanate, methylene dicyclohexane diisocyanate, 2,2,4-trimethyl hexamethylene diisocyanate, m-phenylene diisocyanate, 4-chloro-l,3- phenylene diisocyanate, 4,4 '-biphenylene diisocyanate, 1,5-naphthylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, 1,10- decamethylene diisocyanate, 1,4-cyclohexylene diisocyanate, and polyalkyloxide and polyester glycol diisocyanates such as polytetramethylene ether glycol terminated with TDI and polyethylene adipate terminated with TDI, respectively. Preferably, the isocyanates are TDI and IPDI. The isocyanate is reacted with the hydroxy functional ethylenically unsaturated monomer. These hydroxy functional ethylenically unsaturated monomers are preferably acrylates, vinyl ethers, maleates, fumarates or other unsaturated functional groups. In the reaction between hydroxy and isocyanate groups, it is preferred to employ a stoichiometric balance between hydroxy and isocyanate functionality and to maintain the reactants at a reaction temperature of at least about 25°C. The hydroxy functionality should be substantially consumed. The mole ratio of the isocyanate to the hydroxy functional ethylenically unsaturated monomer is in the range of about 3:1 to about 1.2:1, and preferably about 2:1 to about 1.5:1. The hydroxy functional ethylenically unsaturated monomer attaches to the isocyanate via an urethane linkage. The reaction product of the isocyanate and the ethylenically unsaturated monomer is further reacted with the polyether containing branched, oxyalkylene repeating units. The resulting polyether oligomer is end-capped with the reaction product from the isocyanate/ethylenically unsaturated monomer reaction. By "end-capped" it is meant that a functional group caps each of the two ends of the polyether. Suitable monomers that are useful to endcap the polyether with the desired (meth)acrylate functional groups include hydroxy functional acrylates such as 2- hydroxyethyl acrylate, 2-hydroxypropyl acrylate and the like. Suitable monomers which will endcap the polyether with the desired vinyl ether functional groups include 4- hydroxybutyl vinyl ether, and triethylene glycol monovinyl ether. Suitable monomers which will endcap the polyether with the desired maleate functional group, include maleic acid and hydroxy functional maleates. As stated above, the product of the reaction of the isocyanate and ethylenically unsaturated hydroxy functional monomer is reacted with a polyether that contains branched, oxyalkylene repeating units. These branched, oxyalkylene repeating units preferably contain about 2 to about 6 carbon atoms. Polyether copolymers that contain both branched and non-branched oxyalkylene repeating units are also suitable. Preferably, the polyether contains at least 20 percent by weight of the above-described branched, oxyalkylene repeating units. The preferred polyethers are pol (oxyisopropylene) , marketed by Union Carbide, Danbury, Connecticut, and poly(oxymethyltetramethylene). Poly(oxymethyltetramethylene) is preferably the polymerization product of 3-methyltetrahydrofuran, which has undergone a ring opening polymerization. If the polyether contains repeating units in addition to the branched, oxyalkylene repeating units described above, these repeating units are preferably oxyalkylene repeating units with about 2 to about 5 carbon atoms. A polyether which is the polymerization product of 20 percent by weight of 3-methyltetrahydrofuran and 80 percent by weight of tetrahydrofuran, both of which have undergone a ring opening polymerization, is an example of a suitable polyether containing both branched and non- branched oxyalkylene repeating unit. This polyether copolymer is marketed as PTGL 1000 by the Hodogaya Chemical Company of Japan. The isocyanate/hydroxy functional monomer reaction product attaches to the polyether containing branched, oxyalkylene repeating units via an urethane linkage. The urethane reaction by which this linkage is formed takes place in the presence of a catalyst. Catalysts for the urethane reaction, such as diazabicyclooctane crystals and the like, are suitable for this purpose. The mole ratio of the isocyanate/hydroxy functional monomer reaction product to the polyether with branched, oxyalkylene repeating units is in the range of about 3:1 to about 1.2:1 preferably about 2:1 to about 1.5:1. Unreacted isocyanate groups can be present in the end-capped polyether oligomer, but are preferably minimized to less than about 0.1 percent by weight to provide an oligomer which contains substantially no free isocyanate groups. It is preferred that there be no detectable isocyanate present. The endcapped polyether oligomer is then combined with a reactive diluent and a photoinitiator to form a curable coating composition of the present invention. The endcapped polyether oligomer is about 10 weight percent to about 80 weight percent of the coating composition of the present invention and preferably about 15 to about 50 weight percent of the coating composition. While polyether oligomers are extensively discussed herein, it is understood that any conventional coating composition can be modified as taught herein. Other coating compositions may include, but are not limited to, compositions containing oligomers based on polyolefins, e.g., polybutadienes (saturated or unsaturated), polycarbonates, polyesters and combinations thereof. In the polyether oligomers discussed herein above, as well as in oligomers based on polymers other than polyethers, the above mentioned urethane linkages may be replaced with linkages based on urea, thiourea, or any other linking moiety. The examples of polymeric coating compositions set forth above are intended to be illustrative of the coating compositions that may be employed in the present invention. It is recognized that any coating composition in which a pol (siloxane) may be incorporated falls within the scope of this invention. Other components that may be present in the composition include, but are not limited to, light sensitive and light absorbing components, catalysts, initiators, lubricants, wetting agents, organofunctional silanes, antioxidants, and stabilizers. As an example, a curable coating composition according to the invention may generally be comprised of: 0-80 % of a urethane acrylate oligomer, 0-80 % of a monomer, 0.1-10 % of a photoinitiator, 0.1-10 % of a stabilizer/antioxidant and 0.1-50 % of a poly(alkoxysiloxane) , all percentages being weight percentages relative to the total weight of the composition. A good example of a specific inner primary coating composition that may be used in the present invention is described in U.S. Patent No. 4,682,851 to Ansel, issued July 28, 1987, which is hereby incorporated by reference. A suitable inner primary polymeric composition for application to an optical fiber should have an appropriate viscosity for application, should be fast curing, should be compliant enough at low temperatures to limit optical loss, and should be resistant to penetration from most chemicals or solvents that the fibers are likely to encounter in practical use. A good example of a specific outer primary coating composition that may be used in the present invention is described in U.S. Patent No. 4,472,019, to Bishop et al., issued September 18, 1994, which is hereby incorporated by reference. An outer primary coating should have an appropriate viscosity for application, should be fast curing, should be tough enough to protect the fiber from mechanical handling, should adhere to the inner primary coating well enough to allow complete and easy removal of all coatings from the optical fiber, and should be resistant to penetration from most chemicals or solvents that the fibers are likely to encounter in practical use. A good example of a specific single coat composition that may be used in the present invention is described in U.S. Patent No. 4,932,750, to Ansel et al., issued June 12, 1990, which is hereby incorporated by reference. In the case of an optical fiber, a suitable single coat composition for application should have an appropriate viscosity for application, should be fast curing, should be compliant enough at low temperatures to limit optical loss, should be tough enough to limit abrasion, and should protect the optical fiber from exposure to most chemicals or solvents. A good example of a specific glass substrate coating composition that may be used in the present invention is described in U.S. patent No. 5,112,658, to Skutnik, et al., issued on May 12, 1992, which is hereby incorporated by reference. In the case of a generic glass coating, a suitable coating composition for application to non-optical fiber glass substrates should have an appropriate viscosity for application, should be tough enough to limit abrasion, and should be fast curing. In producing a coated substrate, a liquid coating composition is applied to a substrate and subsequently cured. Typically, the cure is affected using ultraviolet or visible radiation. However, other methods are available. For example, thermal curing, usually in the presence of an initiator, may be used. Alternatively, the coating can be cured by electron beam irradiation where no catalyst is required. More than one coating may be applied. Typically, a first coating is applied and cured followed by a second coating and so on until the desired number of coatings have been applied. Alternatively, the layers can be applied on top of each other as liquids, described herein as a wet-on-wet process, with one final curing step at the end. In many applications involving optical fibers, it is desirable to have more than one coating layer, e.g., at least one inner and one outer primary coating, which are easily removed or stripped as a unit without leaving any coating residue on the glass fiber. To further enhance the strippability and enhance glass strength retention, the inner primary coatings may both be modified with poly(siloxane)and any outer primary coatings may be modified with a strong acid functional ethylenically unsaturated monomer such as phosphonic acid monoacrylate. The strong acid functional ethylenically unsaturated monomer is a monomer comprising an ethylenic unsaturation and a strong acid group. The ethylenically unsaturated group may be a vinyl, allyl, vinylether or (meth)acrylate-group. A non-functional alkyl chain may connect the ethylenic unsaturation to the strong acid group. The strong acid group may be any acid group that completely dissociates in water. Examples of such strong acid functional groups include, but are not limited to, phosphoric acid, sulphuric acid and sulfonic acid groups etc. Most preferably, the strong acid functional groups are phosphoric acid groups. An example of a strong acid functional ethylenically unsaturated monomer includes, but is not limited to, phosphoric acid monoacrylate, commercially available as Ebecryl 170 through Radcure Specialties in Atlanta, Georgia. Other such strong acid functional ethylenically unsaturated monomers are also suitable. Another example is 2-acrylamido-2-methylpropanesulfonic acid, commercially available as Lubrizol* 2401 through the Lubrizol Corporation in Wickliffe, Ohio. The strong acid functional ethylenically unsaturated monomer is preferably present in the range of about 0.1% to about 10%, more preferably in the range of about 0.1% to about 5% by weight of the entire outer primary coating composition. To further enhance the strippability and enhance glass strength retention, the inner and outer primary coatings may both be modified with poly(siloxane) . The polysiloxane is preferably present in each coating in the range of about 0.1% to about 30% by weight in the entire coating compositions in which the poly(siloxane) is found. In one of the preferred embodiments at least the inner coating contains a poly(siloxane) and at least one of the outer primary coatings contains a poly(siloxane) . In certain applications, it is desirable to use a matrix composition to hold a plurality of optical fibers together, and various matrices and their use are known to those skilled in the art. For example, a matrix composition can be the same as the outer primary coatings exemplified herein. It is contemplated that a poly(siloxane) or a strong acid functional ethylenically unsaturated monomer may be incorporated into the matrix composition to obtain the strength retention benefit. It is also recognized that in a plurality of optical fibers employing a matrix, that the poly(siloxane) or the strong acid functional ethylenically unsaturated monomer may be independently found in the outer primary coating, any other coating, for instance an ink, or the matrix, or in any combination thereof. Also contemplated are optical fiber ribbons, which are known to those skilled in the art, that comprise a matrix material that comprises a poly(siloxane) and/or an acid function ethylenically unsaturated monomer. An inner primary coating could, for example, comprise 30-80 wt% (meth)acrylate oligomer, 0-70 wt% (meth)acrylate monomer, 0-3 wt% antioxidant, 0.5-10 wt% photoinitiator, 0-30 wt% organofunctional silane and 0.1- 30 wt% poly(siloxane) . As an example, but without being limited thereto, such a coating could comprise about 60 wt% oligomer, obtained by reacting hydroxyethyl acrylate, a diisocyanate such as toluene diisocyanate and a polyoxyalkylene diol, such as polypropylene glycol, about 33 wt% phenoxyethyl acrylate as a monomer, about 1 wt% thiodiethylene bis (3,5-di-tert-butyl-4-hydroxy) hydrocinnamate as an antioxidant, about 3 wt% 1- hydroxycyclohexyl phenyl ketone as a photoinitiator, and about 3 wt% Dow Corning 1-6184. As another example of an inner primary coating, but without being limited thereto, could comprise about 60 wt% oligomer, obtained by reacting hydroxyethyl acrylate, a diisocyanate such as isophorone diisocyanate and a polyalkylenediol, such as hydrogenated 1,2-polybutadiene diol, about 13 wt% nonyl phenol acrylate as a monomer, about 10 wt% lauryl acrylate as a comonσmer, about 1 wt% thiodiethylene bis(3,5-di-tert-butyl-4 hydroxy) hydrocinnamate as an antioxidant, about 3 wt% 1- hydroxycyclohexyl phenyl ketone as a photoinitiator, and about 3 wt% Dow Corning 1-6184. An outer primary coating could, e.g., comprise 30-80 wt% ( eth)acrylate oligomer, 0-70 wt% (meth)acrylate monomer, 0-3 wt% antioxidant, 0.5- 10 % photoinitiator, and 0.1-30 wt% pol (siloxane). An example of an outer primary coating, but without being limited thereto, could comprise about 40 wt% oligomer, obtained by reacting hydroxyethyl acrylate, a diisocyanate such as isophorone diisocyanate and a hydrophobic polyester diol, such as polycaprolactone diol, about 25 wt% bisphenol A diglycidyl ether diacrylate as a monomer, about 10 wt% trimethylolpropane triacrylate as a monomer, about 18 wt% phenoxyethyl acrylate as a monomer, about 1 wt% thiodiethylene bis (3,5-di-tert-butyl-4 hydroxy) hydrocinnamate as an antioxidant, about 3 wt% 1- hydroxycyclohexyl phenyl ketone as a photoinitiator, and about 3 wt% Dow Corning 1-6184. The following examples are intended to illustrate particular embodiments of the invention, and are not intended to limit the claims or the any part of the specification in any way. Example Example 1 Example of a curable coating composition with poly(siloxane) * This oligomer is the reaction product of 2-hydroxy ethyl acrylate (HEA) , isophorone diisocyanate (IPDI), and Permanol KM 10-1733, produced by Permuthane (a carbonic acid polymer with alkane diol). The composition of example 1, when applied to glass, after curing shows good wet adhesion and good glass strength retention.

Claims: C L I M S 1. A radiation curable coating composition for a glass substrate, said composition comprising at least one component selected from the group consisting of radiation curable polymers, oligomers and monomers, characterized in that said composition comprises a poly(siloxane) having the formula: wherein Y and Z are independently selected from the group consisting of halogen, amino, alkyl and alkoxy; n is one or more and X lf X 2 , X 3 or X 4 is independently a hydrolyzable group that can be hydrolysed from the poly(siloxane) in the presence of water. 2. A radiation curable coating composition according to claim 1, characterized in that the composition comprises a UV radiation curable eth lenically unsaturated oligomer. 3. A curable coating composition according to claim 2, characterized in that the UV curable ethylenically unsaturated oligomer is the reaction product of a hydroxy functional monomer containing ethylenic unsaturation, an isocyanate that is than further reacted with a hydroxy functional polyether. 4. The composition according to any one of claims 1-3, characterized in that the hydrolyzable groups X lf X 2 , X 3 and X 4 are independently halogen (e.g. chloro), formyloxy, acetoxy, propyonyl-oxy, valeryloxy, steaoryloxy, benzoyloxy, naphtoyloxy, toluyloxy, maleoyloxy, alkoxy, alkyl-thio, vinyloxy, allyloxy, vinyletheroxy, methacryloxy or acryloxy. 5. The composition according to claim 4, characterized in that the hydrolyzable groups X lf X 2 , X 3 and X 4 are independently an alkoxy group or a group containing an ethylenic unsaturation. 6. The composition according to any of claims 1-5, characterized in that the poly(siloxane) is present in an amount in the range of 0.1% to 30% by weight of the entire composition. 7. The composition according to claim 6, characterized in that the pol (siloxane) is present in an amount in the range of 0.5% to 10% by weight of the entire composition. 8. The composition according to claim 5, characterized in that the alkoxy groups are methoxy or ethoxy groups. 9. A glass substrate characterized in that it is coated with at least one composition in accordance any one of claims 1-8. 10. A coated optical fiber coated with more than one layer of coating, characterized in that at least the innermost layer comprises the pol (siloxane) as defined in claim 1, and wherein at least one of the other layers comprises an acid functional monomer. 9. A coated optical fiber coated with more than one layer of coating, characterized in that the innermost layer comprises the pol (siloxane) as defined in claim 1, and wherein at least one of the other layers comprises the pol (siloxane) as defined in claim 1. 10. A matrix material characterized in that it comprises a composition according to any of claims 1-8. 11. An optical fiber ribbon comprising at least one coated optical fiber embedded in a cured matrix material, characterized in that the matrix material comprises a poly(siloxane) having the formula wherein Y and Z are independently selected from the group consisting of halogen, amino, alkyl and alkoxy; n is one or more and X lf X 2 , X 3 or X 4 is independently a hydrolyzable group that can be hydrolysed from the poly(siloxane) in the presence of water.

Inventors: SZUM DAVID M, SZUM, DAVID, M.
Applicants: DSM NV, DSM N.V.
Application year: 1995
Main classification: C03C25
IPC codes: C03C17, C03C25, C09D4, C09D175, C09D183, G02B6