Liquid crystal compositions and liquid crystal display elements

Abstract: Liquid crystal compositions comprising (1) as a first component at least one of compounds of formula (I), (2) as a second component, at least one of benzonitrile liquid crystal compounds and (3) as a third component, other liquid crystal compounds, and having excellent voltage-transmittance characteristics (steepness) to meet a colorization and a high response rate and also having low viscosity, while satisfying various characteristics required for STN display mode.

Description: FIELD OF THE INVENTION This invention relates to a nematic liquid crystal composition comprising at least one chiral additive provided in a closed cell composed of two substrates having transparent electrodes, and to a liquid crystal display element using the composition. More particularly, it relates to a liquid crystal composition suitable for a supertwisted nematic mode, and to a liquid crystal display element using the composition. BACKGROUND OF THE INVENTION As a display mode for a liquid crystal display element (LCD), various modes have been proposed such as twisted nematic (TN) mode, supertwisted nematic (STN) mode, active matrix (AM-LCD) mode, etc., which have been put to practical use. Of these practical modes, the supertwisted nematic mode proposed by T. J. Scheffer, et al. (Appl. Phy. Lett., 45(10), 1021 (1984)), wherein the orientation of liquid crystal molecules in the upper and lower substrates is twisted at 180 - 270° , has been adopted for the LCD of personal computers, word processors, etc. A further improvement in various characteristics has been required in the STN mode. The liquid crystal composition used for the STN display element has been required to have the following characteristics: (1) The voltage-transmittance characteristics (steepness) should be steep in order to increase a contrast by liquid crystal display elements; (2) A phase transition temperature (clearing point) in a nematic isotropic phase should be higher for reducing changes in color development due to the temperature-dependency of the optical anisotropy (Δn); and (3) A viscosity (η) should be lower in order to reduce a response time as short as possible. Of these characteristics, the improvement of the above (1) and (3) has become important, as the measure for colorization and animation has been strongly required in recent years. Despite a continuing investigation of the liquid crystal composition having such characteristics, any further improvement is still desired. DETAILED DESCRIPTION OF THE INVENTION A primary object of this invention is to provide a liquid crystal composition having excellent voltage-transmittance characteristics (steepness) especially for meeting colorization and also having a low viscosity to meet a high response rate, while satisfying various characteristics required for the STN display mode. This invention provides a liquid crystal composition which comprises: (1) as a first component, at least one of compounds of formula (I) wherein R 1 represents an alkyl group of 1 - 10 carbons or an alkenyl group of 2 - 10 carbons, wherein one -CH 2 -group or two or more -CH 2 - groups not adjacent to each other may be substituted by -O-, and n represents an integer of 0 - 20; (2) as a second component, at least one of compounds of formula (II-a), (II-b) or (II-c) wherein R 2 represents an alkyl group of 1 - 10 carbons or an alkenyl group of 2 - 10 carbons, wherein one -CH 2 -group or two or more -CH 2 - groups not adjacent to each other may be substituted by -O-; Z 0 represents -COO- or -CH 2 CH 2 -, Z 1 represents -CH 2 CH 2 -, -COO- or a single bond; Q 1 represents H or F; A 1 represents trans-1,4-cyclohexylene, 1,4-phenylene or 1,3-dioxane-2,5-diyl (attached at the 2-position thereof to the cyanophenyl ring moiety); A 2 and A 3 independently represent trans-1,4-cyclohexylene or 1,4-phenylene; and p, q and m independently represent 0 or 1; and (3) as a third component, at least one of compounds of formula (III) or (IV) R 3 -(B)-Z 2 -(C)-R 4 wherein R 3 and R 4 independently represent an alkyl group of 1 - 10 carbons or an alkenyl group of 2 - 8 carbons, wherein one -CH 2 - group or two or more -CH 2 - groups may be substituted by -O-; B represents trans-1,4-cyclohexylene, pyrimidine-2,5-diyl (attached at the 2-position thereof to the group Z 2 ) or 1,4-phenylene; C represents trans-1,4-cyclohexylene or 1,4-phenylene; and Z 2 represents -C≡C-, -COO-, -CH 2 CH 2 -, -CH=CH-, -CF=CF- or a single bond; or R 5 -(D)-Z 3 -(E)-Z 4 -(G)-R 6 wherein R 5 represents an alkyl group of 1 - 10 carbons or an alkenyl group of 2 - 10 carbons, wherein one -CH 2 -group or two or more -CH 2 - groups not adjacent to each other may be substituted by -O-; R 6 represents an alkyl group, an alkoxy group or an alkoxymethyl group, each having 1 - 10 carbons; D represents trans-1,4-cyclohexylene or pyrimidine-2,5-diyl (attached at the 2-position thereof to the group Z 3 ); E represents trans-1,4-cyclohexylene or 1,4-phenylene wherein H is optionally substituted with F at one of the 2-, 3-, 5- and 6-positions thereof; G represents trans-1,4-cyclohexylene or 1,4-phenylene; Z 3 represents -CH 2 CH 2 - or a single bond and; Z 4 represents -C≡C-, -COO-, -CH=CH- or a single bond, with the proviso, that E and G do not represent 1,4-phenylene simultaneously when D represents trans 1,4-cyclohexylene and both Z 3 and Z 4 represent single bonds. In one embodiment of this invention, the first component comprises 3 - 50% by weight, the second component comprises 10 - 70% by weight and the third component comprises 10 - 70% by weight, based on a total weight of the liquid crystal composition. In another aspect of this invention, the liquid crystal composition further comprises as a fourth component, at least one of compounds of formula (V) or (VI) wherein R 7 represents an alkyl group of 1 - 10 carbons, Q 2 represents H or F; and k represents 0 or 1 or wherein R 8 represents an alkyl group of 1 - 10 carbons, J represents trans-1,4-cyclohexylene or 1,4-phenylene, Q 3 and Q 4 independently represent H or F; Z 5 and Z 6 independently represent -COO- or a single bond; and h represents 0, 1 or 2. In another embodiment of this invention, the fourth component comprises 0 - 50% by weight, based on a total weight of the liquid crystal composition. In further embodiment of this invention, the compounds of formula (III) are those wherein R 3 and R 4 independently represent an alkyl group, an alkoxy group or an alkoxymethyl group, each group having 1 - 10 carbons. In other embodiments of this invention, the compounds of formula (IV) are those wherein R 5 represents an alkyl group of 1 - 10 carbons, and R 6 represents an alkyl group or an alkoxy group, each group having 1 - 10 carbons. This invention also provides a liquid crystal display element which comprises the liquid crystal composition of the invention. For the compounds of formula (I) are preferable those of the following formulas: In the above formulas, R represents an alkyl group, an alkenyl group, an alkoxy group, an alkenyloxy group, alkoxymethyl group or an alkenyloxymethyl group, each group having 1-10 carbons. These compounds are known in Japanese Patent Kokai Hei 1-175947 and Japanese Patent Kokai Hei 1-308239 (EP 0325 796B). They have a weakly positive dielectric anisotropy and a low optical anisotropy (Δn), which are used mainly for lowering the viscosity and improving the steepness. For the second component, i.e., the compounds of formulas (II-a), (II-b) and (II-c) are preferable those of the following formulas: In the above formulas, R is an alkyl group or an alkenyl group and R' is an alkanediyl group or an alkenediyl group. Of these compounds, the compounds of the following formulas (II-a-1), (II-a-3), (II-a-6), (II-a-7), (II-b-1), (II-b-3), (II-b-5), (II-c-1), (II-c-4), (II-c-5), (II-c-6), (II-c-7), (II-c-10) and (II-c-11) are especially preferably used. These compounds of the second component have a positive dielectric anisotropy with particularly higher values, which are used mainly for reducing the threshold voltage and improving the steepness which is important as STN characteristics. As the compounds of formulas (III) and (IV) of the third component, preferred compounds are recited below. In the above formulas, R and R' independently represent an alkyl group or an alkenyl group, each group having 1 - 10 carbons. Of the compounds of formula (III), those of the following formulas (III-1, -2, -4, -5, -6, -7, -8, -13, -14, -18, -19 and -20) are especially preferably used. Of the compounds of formula (IV), those of the following formulas (IV-1, -2, -5, -9, -11, -12, -14 and -15) are especially preferably used. The compounds of formulas (III) and (IV) have a negative or weakly positive dielectric anisotropy. The compounds of formula (III) are used mainly for reducing the viscosity of the liquid crystal composition and/or for controlling Δn. The compounds of formula (IV) are used for broadening a nematic phase including an increase in a clearing point and/or for controlling Δn and viscosity. As the compounds of formulas (V) and (VI), preferred compounds are recited below. In the above formulas, R represents an alkyl group. Of the compounds of formula (V), the compounds of the following formulas (V-1, -2 and -3) are especially preferably used. Of the compounds of formula (VI), the compounds of the following formulas (VI-1, -5, -6, -7, -8, -9, -10, -11, -12, -13, -14, -15, -17 and -18) are especially preferably used. The compounds of formulas (V) and (VI) have a positive dielectric anisotropy, which are used particularly for reducing the threshold voltage and improving the temperature-dependency. They are also used for controlling the viscosity and Δn and for broadening a nematic range by increasing a clearing point. An amount of the first component used in this invention is preferably 3 - 50% by weight, more preferably 5 - 40% by weight, based on a total weight of a liquid crystal composition. With less than 3% by weight, it becomes difficult to attain the desired effects such as steepness and high response rate. With more than 50% by weight, a threshold voltage of the liquid crystal composition tends to be undesirably increased. An amount of the second component used is preferably 10 - 60% by weight, more preferably 15 - 60% by weight. With less than 10% by weight, a threshold voltage of the liquid crystal composition tends to be undesirably increased. With more than 60% by weight, a viscosity of the liquid crystal composition tends to be undesirably increased. An amount of the third component used is preferably 10 - 70% by weight, more preferably 15 - 60% by weight. With less than 10% by weight, a viscosity of the liquid crystal composition tends to be undesirably increased. With more than 70% by weight, a threshold voltage of the liquid crystal composition tends to be undesirably increased. An amount of the fourth component used is preferably up to 50% by weight, more preferably up to 40% by weight. Depending on the applications of the liquid crystal display element, the liquid crystal composition can contain, in addition to the compounds of the above formulas (I) - (VI), a suitable amount of other compounds within the range of not adversely affecting the object of this invention, for the purpose of controlling the threshold voltage, nematic range, Δn, dielectric anisotropy, viscosity and the like. Examples of such compounds include the following compounds: In the above formulas, R represents an alkyl group of 1 - 10 carbons. The liquid crystal composition of the invention is prepared by a conventional process. In general, a process has been employed wherein various components are dissolved in each other at an elevated temperature. The liquid crystal materials of the present invention are improved and optimized with any suitable additives, depending on the intended applications. Such additives are well known to a person of ordinary skill in the art and also disclosed in literatures. Usually, chiral dopants and others are added for inducing the helical structure of liquid crystals thereby to adjust necessary twist angle and prevent reverse twist of liquid crystal molecules. The present liquid crystal composition may be also used as a liquid crystal composition for guest-host (GH) mode by incorporating therein dichroic dyestuffs such as those of merocyanines, styryl derivatives, azo compounds, azomethines, azoxy compounds, quinophthalones, anthraquinones and tetrazine derivatives, etc. The liquid crystal composition of the present invention may be further used for NCAP prepared by micro-capsulating nematic liquid crystals or polymer-dispersion type display elements (PDLCD) represented by polymer net-work liquid crystal display element (PNLCD) having three-dimensional net-work polymer formed in liquid crystal. In addition, the present liquid crystal composition can be used as a liquid crystal material for electrically controlled birefringence (ECB) mode or dynamic scattering (DS) mode. This invention is further illustrated by the following examples and comparative examples, in which all parts and percentages (%) are by weight unless otherwise indicated. For evaluation on a 240° STN cell, a cell thickness d was selected so as to give Δn·d (i.e., the product of a cell thickness d and an optical anisotropy Δn) of approximately 0.85, while a chiral compound was added to the liquid crystal composition so as to provide a ratio of a cell thickness d to a pitch p of a liquid crystal composition (d/p) of approximately 0.5 and then the resulting mixture was poured into the cell. The cell evaluation was performed in a yellow mode and a voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz. A ratio of the voltage at a transmittance of 90% (V 90 ) and the voltage at a transmittance of 10% (V 10 ) was evaluated as the steepness (V 10 /V 90 ). As the chiral compounds are used the following compounds, but with no limitation thereto: Comparative Example 1 Composition A consisting of the following compounds was prepared: Composition A thus prepared had the following properties: Clearing point T NI = 72.4 (°C) Viscosity at 20°C η 20 = 27.0 (mPa · s) Optical anisotropy at 25°C Δn = 0.137 Dielectric anisotropy at 20°C Δε = 11.0 Threshold voltage at 20°C V th = 1.78 (V) Comparative Example 2 A liquid crystal composition was prepared by admixing 85 parts of Composition A obtained in Comparative Example 1 with 15 parts of the compound of the following formula included within the scope of formula (I): The liquid crystal composition thus prepared had the following properties: Clearing point T NI = 67.6 (°C) Viscosity at 20°C η 20 = 20.2 (mPa·s) Optical anisotropy at 25°C Δn = 0.123 Dielectric anisotropy at 20°C Δε = 9.6 Threshold voltage at 20°C V th = 1.74 (V) To 100 parts of the liquid crystal composition as obtained above was added 0.80 part of the chiral compound CM-33 to prepare a composition. This composition was poured into a 240 ° STN cell having a thickness of d=6.9 µm and the cell evaluation was performed in a yellow mode. The voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz, with the following results: V 90 = 1.95 (V), V 10 = 2.50 (V), steepness V 10 /V 90 = 1.282. Example 1 A liquid crystal composition consisting of the following compounds was prepared: The liquid crystal composition thus prepared had the following properties: Clearing point T NI = 86.7 (°C) Viscosity at 20°C η 20 = 13.4 (mPa·s) Optical anisotropy at 25°C Δn = 0.133 Dielectric anisotropy at 20°C Δε = 7.0 Threshold voltage at 20°C V th = 2.03 (V) To 100 parts of the liquid crystal composition as obtained above was added 0.85 part of the chiral compound CM-33 to prepare a composition. This composition was poured into a 240° STN cell having a thickness of d=6.4 µm. The cell evaluation was performed in a yellow mode. The voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz, with the following results: V 90 = 2.21 (V), V 10 = 2.38 (V), steepness V 10 /V 90 = 1.076 This liquid crystal composition had higher clearing point and lower viscosity as compared with the compositions of Comparative Examples 1 and 2. The steepness was greatly improved as compared with the composition of Comparative Example 2. Example 2 A liquid crystal composition consisting of the following compounds was prepared: The liquid crystal composition thus prepared had the following properties: Clearing point T NI = 85.0 (°C) Viscosity at 20°C η 20 = 15.8 (mPa·s) Optical anisotropy at 25°C Δn = 0.133 Dielectric anisotropy at 20°C Δε = 6.5 Threshold voltage at 20°C V th = 2.03 (V) To 100 parts of the liquid crystal composition as obtained above was added 0.80 part of the chiral compound CM-33 to prepare a composition. This composition was poured into a 240 ° STN cell having a thickness of d=6.4 µm. The cell evaluation was performed in a yellow mode. The voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz with the following results: V 90 = 2.24 (V), V 10 = 2.37 (V), steepness V 10 /V 90 = 1.054 This liquid crystal composition had higher clearing point and lower viscosity as compared with the compositions of Comparative Examples 1 and 2. The steepness was greatly improved as compared with the composition of Comparative Example 2. Example 3 A liquid crystal composition consisting of the following compounds was prepared: The liquid crystal composition thus prepared had the following properties: Clearing point T NI = 90.6 (°C) Viscosity at 20°C η 20 = 14.4 (mPa·s) Optical anisotropy at 25°C Δn = 0.154 Dielectric anisotropy at 20°C Δε = 6.0 Threshold voltage at 20°C V th = 2.29 (V) To 100 parts of the liquid crystal composition as obtained above was added 0.85 part of the chiral compound CM-33 to prepare a composition. This composition was poured into a 240 ° STN cell having a thickness of d=5.5 µm. The cell evaluation was performed in a yellow mode. The voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz, with the following results: V 90 = 2.45 (V), V 10 = 2.53 (V), steepness V 10 /V 90 = 1.034 This liquid crystal composition had higher clearing point and lower viscosity as compared with the compositions of Comparative Examples 1 and 2. The steepness was greatly improved as compared with the composition of Comparative Example 2. Example 4 A liquid crystal composition consisting of the following compounds was prepared: The liquid crystal composition thus prepared had the following properties: Clearing point T NI = 70.7 (°C) Viscosity at 20°C η 20 = 15.2 (mPa·s) Optical anisotropy at 25°C Δn = 0.171 Dielectric anisotropy at 20°C Δε = 5.5 Threshold voltage at 20°C V th = 2.01 (V) To 100 parts of the liquid crystal composition as obtained above was added 1.09 part of the chiral compound CM-33 to prepare a composition. This composition was poured into a 240 ° STN cell having a thickness of d=5.0 µm. The cell evaluation was performed in a yellow mode. The voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz, with the following results: V 90 = 2.11 (V), V 10 = 2.41 (V), steepness V 10 /V 90 = 1.142 This liquid crystal composition had lower viscosity as compared with those of Comparative Examples 1 and 2. The steepness was greatly improved as compared with the composition of Comparative Example 2. Example 5 A liquid crystal composition consisting of the following compounds was prepared: The liquid crystal composition thus prepared had the following properties: Clearing point T NI = 102.7 (°C) Viscosity at 20°C η 20 = 16.5 (mPa·s) Optical anisotropy at 25°C Δn = 0.134 Threshold voltage at 20°C V th = 2.00 (V) To 100 parts of the liquid crystal composition as obtained above was added 1.87 part of the chiral compound CN to prepare a composition. This composition was poured into a 240 ° STN cell having a thickness of d=6.4 µm. The cell evaluation was performed in a yellow mode. The voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz with the following results: V 90 = 2.19 (V), V 10 = 2.34 (V), steepness V 10 /V 90 = 1.068 This liquid crystal composition had higher clearing point and lower viscosity as compared with those of Comparative Examples 1 and 2. The steepness was greatly improved as compared with the composition of Comparative Example 2. Example 6 A liquid crystal composition consisting of the following compounds was prepared. The liquid crystal composition thus prepared had the following properties: Clearing point T NI = 102.0 (°C) Viscosity at 20°C η 20 = 15.7 (mPa·s) Optical anisotropy at 25°C Δn = 0.131 Threshold voltage at 20°C V th = 2.07 (V) To 100 parts of the liquid crystal composition as obtained above was added 1.74 part of the chiral compound CN to prepare a composition. This composition was poured into a 240° STN cell having a thickness of d=6.5 µm. The cell evaluation was performed in a yellow mode. The voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz, with the following results: V 90 = 2.19 (V), V 10 = 2.36 (V), steepness V 10 /V 90 = 1.078 This liquid crystal composition had higher clearing point and lower viscosity as compared with those of Comparative Examples 1 and 2. The steepness was greatly improved as compared with the composition of Comparative Example 2. Example 7 A liquid crystal composition consisting of the following compounds was prepared. The liquid crystal composition thus prepared had the following properties: Clearing point T NI = 78.7 (°C) Viscosity at 20°C η 20 = 12.6 (mPa·s) Optical anisotropy at 25°C Δn = 0.133 Dielectric anisotropy at 20°C Δε = 6.5 Threshold voltage at 20°C V th = 1.93 (V) To 100 parts of the liquid crystal composition as obtained above was added 0.82 part of the chiral compound CM-33 to prepare a composition. This composition was poured into a 240 ° STN cell having a thickness of d=6.4 µm. The cell evaluation was performed in a yellow mode. The voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz, with the following results: V 90 = 2.15 (V), V 10 = 2.30 (V), steepness V 10 /V 90 = 1.070 Example 8 A liquid crystal composition consisting of the following compounds was prepared. The liquid crystal composition thus prepared had the following properties: Clearing point T NI = 76.6 (°C) Viscosity at 20°C η 20 = 19.1 (mPa·s) Optical anisotropy at 25°C Δn = 0.120 Dielectric anisotropy at 20°C Δε = 7.2 Threshold voltage at 20°C V th = 1.79 (V) To 100 parts of the liquid crystal composition as obtained above was added 0.80 part of the chiral compound CM-33 to prepare a composition. This composition was poured into a 240 ° STN cell having a thickness of d=7.0 µm. The cell evaluation was performed in a yellow mode. The voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz, with the following results: V 90 = 1.92 (V), V 10 = 2.09 (V), steepness V 10 /V 90 = 1.089 Example 9 A liquid crystal composition consisting of the following compounds was prepared. The liquid crystal composition thus prepared had the following properties: Clearing point T NI = 76.1 (°C) Viscosity at 20°C η 20 = 18.0 (mPa·s) Optical anisotropy at 25°C Δn = 0.111 Dielectric anisotropy at 20°C Δε = 7.8 Threshold voltage at 20°C V th = 1.70 (V) To 100 parts of the liquid crystal composition as obtained above was added 0.78 part of the chiral compound CM-33 to prepare a composition. This composition was poured into a 240 ° STN cell having a thickness of d=7.5 µm. The cell evaluation was performed in a yellow mode. The voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz, with the following results: V 90 = 1.86 (V), V 10 = 2.03 (V), steepness V 10 /V 90 = 1.091 Example 10 A liquid crystal composition consisting of the following compounds was prepared. The liquid crystal composition thus prepared had the following properties: Clearing point T NI = 85.0 (°C) Viscosity at 20°C η 20 = 23.7 (mPa·s) Optical anisotropy at 25°C Δn = 0.124 Dielectric anisotropy at 20°C Δε = 11.4 Threshold voltage at 20°C V th = 1.39 (V) To 100 parts of the liquid crystal composition as obtained above was added 0.80 part of the chiral compound CM-33 to prepare a composition. This composition was poured into a 240 ° STN cell having a thickness of d=6.9 µm. The cell evaluation was performed in a yellow mode. The voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz, with the following results: V 90 = 1.46 (V), V 10 = 1.60 (V), steepness V 10 /V 90 = 1.096 Example 11 A liquid crystal composition consisting of the following compounds was prepared: The liquid crystal composition thus prepared had the following properties: Clearing point T NI = 81.2 (°C) Viscosity at 20°C η 20 = 24.5 (mPa·s) Optical anisotropy at 25°C Δn = 0.113 Dielectric anisotropy at 20°C Δε = 8.1 Threshold voltage at 20°C V th = 1.54 (V) To 100 parts of the liquid crystal composition as obtained above was added 1.50 part of the chiral compound CN to prepare a composition. This composition was poured into a 240° STN cell with a thickness of d=7.5 µm. The cell evaluation was performed in a yellow mode. The voltage-transmittance characteristics (V-T characteristics) were determined with a square wave at 70 Hz, with the following results: V 90 = 1.67 (V), V 10 = 1.82 (V), steepness V 10 /V 90 = 1.090 As apparent from the above examples, the present invention can provide the liquid crystal compositions having excellent voltage-transmittance characteristics (steepness), especially to meet colorization and also having a lower viscosity to meet a high response rate, while satisfying various characteristics required for the STN display mode.

Claims: A liquid crystal composition which comprises: (1) as a first component, at least one of compounds of formula (I) wherein R 1 represents an alkyl group of 1 - 10 carbons or an alkenyl group of 2 - 10 carbons, wherein one -CH 2 - group or two or more -CH 2 - groups not adjacent to each other may be substituted by -O-, and n represents an integer of 0 - 20; (2) as a second component, at least one of compounds of formula (II-a), (II-b) or (II-c) wherein R 2 represents an alkyl group of 1 - 10 carbons or an alkenyl group of 2 - 10 carbons, wherein one -CH 2 - group or two or more -CH 2 - groups not adjacent to each other may be substituted by -O-; Z° represents -COO- or -CH 2 CH 2 -, Z 1 represents -CH 2 CH 2 -, -COO- or a single bond; Q 1 represents H or F; A 1 represents trans-1,4-cyclohexylene, 1,4-phenylene or 1,3-dioxane-2,5-diyl (attached at the 2-position thereof to the cyanophenyl ring moiety); A 2 and A 3 independently represent trans-1,4-cyclohexylene or 1,4-phenylene; and p, q and m independently represent 0 or 1; and (3) as a third component, at least one of compounds of formula (III) or (IV) R 3 -(B)-Z 2 -(C)-R 4 wherein R 3 and R 4 independently represent an alkyl group of 1 - 10 carbons or an alkenyl group of 2 - 8 carbons, wherein one -CH 2 - group or two or more -CH 2 - groups may be substituted by -O-; B represents trans-1,4-cyclohexylene, pyrimidine-2,5-diyl (attached at the 2-position thereof to the group Z 2 ) or 1,4-phenylene; C represents trans-1,4-cyclohexylene or 1,4-phenylene; and Z 2 represents -C≡C-, -COO-, -CH 2 CH 2 -, -CH=CH-, -CF=CF- or a single bond; or R 5 -(D)-Z 3 -(E)-Z 4 -(G)-R 6 wherein R 5 represents an alkyl group of 1 - 10 carbons or an alkenyl group of 2 - 10 carbons, wherein one -CH 2 - group or two or more -CH 2 - groups not adjacent to each other may be substituted by -O-; R 6 represents an alkyl group, an alkoxy group or an alkoxymethyl group, each having 1 - 10 carbons; D represents trans-1,4-cyclohexylene or pyrimidine-2,5-diyl (attached at the 2-position thereof to the group Z 3 ); E represents trans-1,4-cyclohexylene or 1,4-phenylene wherein H is optionally substituted with F at one of the 2-, 3-, 5- and 6-positions thereof; G represents trans-1,4-cyclohexylene or 1,4-phenylene; Z 3 represents -CH 2 CH 2 - or a single bond and, Z 4 represents - C≡C-,-COO-, -, -CH=CH- or a single bond, with the proviso, that E and G do not represent 1,4-phenylene simultaneously when D represents trans 1,4-cyclohexylene and both Z 3 and Z 4 represent single bonds. The liquid crystal composition as claimed in claim 1 wherein the first component comprises 3 - 50% by weight, the second component comprises 10 - 70% by weight and the third component comprises 10 - 70% by weight, based on a total weight of the liquid crystal composition. The liquid crystal composition as claimed in claim 1 or 2 which further comprises as a fourth component, at least one of compounds of formula (V) or (VI) wherein R 7 represents an alkyl group of 1 - 10 carbons; Q 2 represents H or F; and k represents 0 or 1 or wherein R 8 represents an alkyl group of 1 - 10 carbons; J represents trans-1,4-cyclohexylene or 1,4-phenylene; Q 3 and Q 4 independently represent H or F; Z 5 and Z 6 independently represent -COO- or a single bond; and h represents 0, 1 or 2. The liquid crystal composition as claimed in claim 3 wherein the fourth component comprises up to 50% by weight, based on a total weight of the liquid crystal composition. The liquid crystal composition as claimed in any of claims 1 - 4 wherein R 3 and R 4 in formula (III) independently represent an alkyl group, an alkoxy group or an alkoxymethyl group, each group having 1 - 10 carbons. The liquid crystal composition as claimed in any of claims 1 - 5 wherein R 5 in formula (IV) represents an alkyl group of 1 - 10 carbons, and R 6 represents an alkyl group or an alkoxy group, each group having 1 - 10 carbons. A liquid crystal display element which comprises a liquid crystal composition as claimed in any of claims 1 - 6.

Inventors: NAKAGAWA ETSUO, SAWADA SHINICHI, NAKAGAWA, ETSUO, SAWADA, SHINICHI
Applicants: CHISSO CORP, CHISSO CORPORATION
Application year: 1995
Main classification: C09K19
IPC codes: C09K19, G02F1