Semiconductor device and method of manufacturing the same

Abstract: A semiconductor device includes a substrate (211), an insulation film (215, 218, 222, 223) formed above the substrate (211) and containing silicon-fluorine bonds, and a titanium-based metal wiring layer (213, 217, 220) formed on the insulation film (215, 218, 222, 223), the titanium-based metal wiring layer (213, 217, 220) containing fluorine which is diffused from the insulation film (215, 218, 222, 223) and has a fluorine concentration of less than 1 × 10 20 atoms/cm 3 .

Description: The present invention relates to a semiconductor device having a titanium-based metal wiring layer on an insulation film and, more particularly, to a semiconductor device having improved adhesion properties between the wiring layer and the insulation film. In recent years, with the higher integration for integrated circuits, and demands for high-speed operations, suppression of a wiring capacitance in an integrated circuit has become a serious problem. When the wiring interval is on an order of submicrometers, the capacitance between interconnections abruptly increases to prolong the propagation delay of a signal. Particularly, in a high-speed logic circuit used for a CPU and the like, wiring on a chip is multi-layered. Extensive studies have been made for demanding an insulation film having a low dielectric constant suitable for an integrated circuit chip. As a conventional insulation film for an integrated circuit, a silicon oxide film (SiO 2 ) is widely used. The dielectric constant of a silicon oxide film formed by general CVD is about 4.2 to 5.0. To decrease this dielectric constant to a substantially half, an organic polymer (a dielectric constant of 2.0 to 3.1) is known. The organic polymer, however, has problems of insufficient thermal stability and difficult patterning. Recently, it is examined to form an insulation film (a dielectric constant of 3.0 to 3.6) containing Si-F bonds by adding fluorine (F) into a silicon oxide film and to decrease the dielectric constant of the insulation film. An insulation film containing Si-F bonds is a material which receives attention for its excellent burying properties in a multi-layered interconnection. By trapping fluorine into an oxide film, an insulation film having a low dielectric constant can be realized. This is reported in, e.g., "Reduction of Wiring Capacitance with New Low Dielectric SiOF Interlayer Film for High Speed/Low Power Sub-half Micron CMOS" (J. Ida et al., 1994 Symposium on VLSI (p. 59)). This reports that the propagation delay time (tpd) of a 0.35-fm CMOS 2NAND gate was improved 13% in an interconnection with an insulation film (a dielectric constant of 3.6) containing Si-F bonds in comparison with an interconnection with a normal CVD oxide film (a dielectric constant of 4.3). US-A-5 334 552 describes a method of fabricating a multi-layered interconnection structure which comprises the steps of: forming a first wiring layer on a silicon oxide film having a compressive stress; forming a chick (2 to 3.5 µm) fluorine-containing silicon oxide film at a temperature not higher than 200°C; etching back the fluorine-containing silicon oxide film to flatten the surface of the film; forming a silicon oxide film having a compressive stress; forming a through-hole in position; and forming a second wiring layer. The fluorine-containing silicon oxide film is used as part of an insulating film. EP-A-0 599 730 describes a semiconductor device and a method of producing the same. An Si oxide film is formed by plasma CVD with the use of a silicon compound gas containing fluorine, whereby the generation of particles can be suppressed to improve the quality of the device and the yield, the planarity of the Si oxide film functioning as an interlayer dielectric film or a passivation film can be improved, and higher speed operation in a semiconductor device can be accomplished. "A Room Temperature Chemical Vapor Deposition SIOF Film Formation Technology for the Interlayer in Submicron Multilevel Interconnections" by Tetsuya Homma et al., Journal of the Electrochemical Society, vol. 140, no. 3, March (1993), pp 687-692 describes an interlayer dielectric film formation technology for multilevel interconnection by catalytic chemical vapor deposition. This technique utilizes fluorotriethoxysilane [FSi (OC 2 H 5 ) 3 ] and water vapor as gas source. The films deposited at 25°C have remarkably good properties, such as tightly bonded Si-O networks with no OH radicals, large density value (2.20 g/cm 3 ), small residual stress (50 MPa), low leakage current, and small dielectric constant (3.7) although the film contains residual fluorine and carbon atoms with 5.3 x 10 21 and 2 x 10 21 atom/cm 3 , respectively. In this manner, an insulation film containing Si-F bonds has a low dielectric constant and an effect of decreasing a wiring capacitance. On the other hand, this insulation film has a drawback of insufficient adhesion properties with a refractory metal wiring layer to cause peel-off of the wiring layer. The situation will be described with reference to the accompanying drawing. FIG. 1 is a partial sectional view showing a semiconductor device having a two-layered interconnection formed on its surface. More specifically, a semiconductor element (not shown) is formed on the surface of a silicon substrate 111, and its entire upper surface is covered with a first insulation film 112 consisting of silicon oxide. A wiring underlayer 113a consisting of titanium (Ti) is formed on the surface of the first insulation film 112. A main wiring layer 113b made of Cu, Al-Si-Cu, or the like is stacked on the wiring underlayer 113a, and these stacked layers form a first metal interconnection 113. By adopting the two-layered structure in this manner, the mechanical strength with respect to disconnection and the like can be enhanced without increasing the electrical resistance of an interlayer. This first wiring layer is connected to the semiconductor element (not shown) formed on the substrate 111 through a via conductor (not shown). A second insulation film 115 of silicon dioxide (SiO 2 ) containing Si-F bonds is formed on the entire surface of the first metal interconnection 113. Via holes are partially formed on the first metal interconnection 113, and plugs 116 made of tungsten (W) are buried in these via holes. A second wiring underlayer 117a of titanium (Ti) and a second main wiring layer 117b of Cu, Al-Si-Cu, or the like are stacked on this second insulation film 115 to form a second metal interconnection 117. A third insulation film 119 consisting of silicon dioxide (SiO 2 ) is formed on this structure. In the semiconductor device manufactured in this manner, the second metal interconnection 117 on the surface may peel off from the second insulation layer 115 due to a residual thermal stress generated in the wiring layer and a mechanical impact during bonding. It is considered that this peel-off is caused by poor adhesion properties between the insulation layer 115 containing Si-F bonds and the titanium wiring underlayer 117a. As described above, in the semiconductor device having an insulation film containing Si-F bonds and a titanium wiring layer, the adhesion properties at the interface between the titanium wiring layer and the insulation film are degraded. Consequently, the metal wiring film is caused to peel off due to a thermal stress generated in the metal wiring film and a mechanical stress during bonding. It is an object of the present invention to provide a semiconductor device having high reliability without causing peel-off of a metal wiring film. In order to achieve the above object, according to the present invention, a semiconductor device comprising: a substrate having a first and a second region; a first insulating film made of silicon oxide and formed above said substrate and containing silicon-fluorine bonds, said first insulating film having a first thickness on said first region and having a second thickness greater than said first thickness on said second region; a metal interconnection formed on said first insulating film of said first region, the metal interconnection including a titanium-based underlayer on the first insulating film of said first region and a main wiring layer on the underlayer; and a second insulating film at least formed on said metal interconnection and having an opening for wire bonding on said metal interconnection above said first region of said substrate, wherein the fluorine concentration at the interface between the titanium-based underlayer and the first insulating film above said first region is less than 1 x 10 20 atoms/cm 3 . SIMS (Secondary Ion Mass Spectrometry) analysis is used for measurement of the fluorine concentration in the refractory metal. TiF is used as detection ions for quantitative analysis of fluorine in the titanium layer. A Model 6600 available from Perkin Elmer is used for the SIMS. The measurement is carried out under the condition wherein the ionization energy of Cs + ions is 5 keV. When a titanium-based refractory metal wiring layer is formed on an insulation film containing silicon-fluorine bonds directly or through another insulation film, fluorine in the insulation film is diffused to the titanium-based metal wiring layer in the sequential annealing step or the like. The diffused fluorine forms TiF, Ti x Fy, and at the same time forms Si x F y , Si x F y O z , Si x F y C z , and the like in the wiring layer or at the interface between the wiring layer and the insulation film. In addition, a reaction layer consisting of Ti x Si y O z is formed at the interface. These products degrade the adhesion properties between the insulation layer and the titanium-based wiring layer. Particularly, when the fluorine concentration in the titanium-based wiring layer is 1 × 10 20 atoms/cm 3 or more, or when the ratios of Ti to Si and O are higher in the reaction layer, the adhesion properties are greatly degraded. The composition of the reaction layer formed at the interface between the wiring layer for bonding wire connection and the insulation film after deposition of the insulation film may be set such that the element composition ratios of Ti to Si and O are 1 or less by suppressing the diffusion amount of F. With this operation, the adhesion properties at the interface can be greatly improved. This invention can be more fully understood from the following detailed description when taken in conjunction with the accompanying drawings, in which: FIG. 1 is a sectional view showing the main part of a semiconductor device according to the prior art for explaining peel-off of a metal interconnection; FIG. 2 is a graph showing the concentration profiles of constituent elements on a section taken along a line 2A - 2A' in FIG. 1; FIG. 3 is a sectional view showing the main part of a semiconductor device not forming part of the present invention; FIGS. 4A to 4D are sectional views of the semiconductor device showing a manufacturing method step by step for the device of Fig. 3; FIG. 5 is a graph showing the concentration profiles of constituent elements on a section taken along a line 5A - 5A' in FIG. 3; FIG. 6 is a sectional view showing the main part of another semiconductor device not forming part of the present invention; FIGS. 7A to 7D are sectional views of the semiconductor device showing a manufacturing method step by step for the device of Fig. 6; FIG. 8 is a graph showing the concentration profiles of constituent elements on a section taken along a line 8A - 8A' in FIG. 6; FIG. 9 is a graph showing a relationship between the fluorine concentration at the interface between titanium and a silicon oxide film and the bonding pad peel-off incidence in the device of Fig. 3; FIG. 10 is a sectional view showing the main part of a third semiconductor device not forming part of the present invention; FIGS. 11A and 11B are sectional views of the semiconductor device showing part of a manufacturing method for the device of Fig. 10; FIG.12 is a graph showing concentration profiles of constituent elements on a section taken along a line 12B - 12B' in FIG. 10; FIG. 13 is a sectional view showing the main part of a fourth semiconductor device not forming part of the present invention; FIGS. 14A and 14B are sectional views of the semiconductor device showing part of a manufacturing method for the device of Fig. 13; FIG. 15 is a graph showing concentration profiles of constituent elements on a section taken along a line 15B - 12B' in FIG. 13; FIG. 16 is a photomicrograph showing a reaction layer formed at the interface between an insulation layer and a metal wiring underlayer; FIG. 17 is a graph showing a relationship between the bonding strength and the thickness of a reaction layer; FIG. 18 is a graph showing the constituent ratios of main elements at the interface between an insulation layer and an underlayer in the device of Fig. 3; FIG. 19 is a graph showing the constituent ratios of main elements at the interface between an insulation layer and an underlayer in the prior art; FIG. 20 is a graph showing the ratios of Ti to Si and O at the interface between the insulation layer and the underlayer in the case where fluorine is removed in comparison with those in the prior art where no fluorine is removed; FIG. 21 is a sectional view showing the main part of a fifth semiconductor device not forming part of the present invention; FIGS. 22A and 22B are sectional views of the semiconductor device showing part of a manufacturing method for the device of Fig. 21; FIG. 23 is a sectional view showing the main part of a semiconductor device according to an embodiment of the present invention; and FIGS. 24A and 22B are sectional views of the semiconductor device showing part of a manufacturing method for the above embodiment of the present invention. The preferred embodiment will be described below with reference to the accompanying drawings. The same reference numerals denote the same parts throughout the following description, and a repetitive description thereof will be omitted. FIG. 3 is a sectional view showing a metal interconnection portion of a,first semiconductor device. Referring to FIG. 3, a first insulation film (SiO 2 ) 212 is formed on an Si substrate 211, and a first metal interconnection 213 is partially formed on the surface of the first insulation film 212. This metal interconnection 213 is an interconnection of a multi-layered structure constituted by a titanium-based metal underlayer 213a and a main wiring layer 213b of, e.g., an Al-Cu-Si alloy. A second insulation film 215 is formed in the remaining region of the first insulation film 212. This insulation film 215 is an SiO 2 film containing Si-F bonds. Plugs 216 consisting of, e.g., tungsten (W) as a via conductor are formed on the metal interconnection 213, and electrodes are extracted to the surface of the second insulation film 215. A second metal interconnection 217 is formed on the insulation film 215, and part of the second metal interconnection 217 is connected to the plugs 216. This metal interconnection 217 is a titanium-based metal wiring layer of a multi-layered structure constituted by a titanium-based metal underlayer 217a and a main wiring layer 217b of, e.g., an Al-Cu-Si alloy. The insulation film 215 and the metal interconnection 217 are covered with a third insulation film (passivation film) 219 to form a surface metal interconnection portion. The above semiconductor device is manufactured according to the following method. First, as shown in FIG. 4A, an SiO 2 film as the first insulation film 212 is deposited to a thickness of 1,500 nm on the Si substrate 211 using TEOS (tetraethylorthosilicate) gas and oxygen (O 2 ) gas in a low-pressure plasma. In this case, O 3 gas may be used instead of the O 2 gas. With the O 3 gas, an SiO 2 film having more excellent self-planarization characteristics can be obtained. Next, Ti and TiN are sequentially deposited to thicknesses of 50 nm and 70 nm by sputtering for the refractory wiring underlayer 213a which constitutes the first metal interconnection. In this case, the CVD method can be used instead of the sputtering method. An Al-Cu-Si alloy for the main wiring layer 213b is deposited to a thickness of 600 nm on this wiring underlayer 213a by the sputtering method to form the metal wiring layer of the multi-layered structure. Note that examples of the material of the main wiring layer 213b may be Cu, a Cu alloy, W, and a W alloy. Subsequently, this metal wiring layer of the multi-layered structure is processed by the lithography technique and the RIE (Reactive Ion Etching) technique to form the first metal interconnection 213. Then, as shown in FIG. 4B, an SiO 2 film containing fluorine as the second insulation film 215 containing Si-F bonds is deposited to a thickness of 2,500 nm using TEOS gas, O 2 gas, and a nitrofluoride (NF x ) gas in a low-pressure plasma. As a film formation gas for the CVD SiO 2 film to be used here, inorganic SiH 4 or the like may be used instead of TEOS. In this case, a chlorofluoride (C x F y ), a siliconfluoride (Si x F y ), or the like may be used instead of the nitrofluorine. The second insulation film 215 contains Si-F bonds, multiple bonds such as Si-F-C bonds, and free fluorine having no bond radical. Thereafter, the surface of this insulation film is planarized by the resist etch-back RIE technique. In this case, the surface may be planarized using the CMP (Chemical Mechanical Polishing) technique. The obtained structure is introduced into a furnace in a nitrogen atmosphere at 450°C to anneal it for 15 minutes. A multiple bond in the second insulation film 215 has a lower bond energy than that of an Si-F bond and thus is in an instable bond state. As a result of this annealing, such polymer bonds, e.g., Si-F-C bonds are separated to generate CF x , and generated CF x and free fluorine are diffused outside the insulation film 215 (FIG. 4C). This removal process of free fluorine can be performed within a short period of time by, e.g., lamp annealing with an infrared lamp at 600°C for 20 seconds. Alternatively, this process may be performed by low-pressure plasma discharge at 200°C. In this case, oxygen gas, nitrogen gas, argon gas, or the like can be used for the atmosphere. Next, as shown in FIG. 4D, the via holes are opened for connecting the first metal interconnection to the second metal interconnection. Tungsten is selectively deposited in the via holes using WF 6 and SiH 4 gases to form the plugs 216. Similar to the first wiring underlayer, Ti and TiN for the second metal underlayer 217a are sequentially deposited to film thicknesses of 50 nm and 70 nm by the sputtering method. An Al-Cu-Si alloy for the main wiring layer 217b is deposited to a thickness of 1,200 nm on this wiring underlayer 217a by the sputtering method to form the metal wiring layer of the multi-layered structure. Note that examples of the material of the main wiring layer 217b may be Cu, a Cu alloy, tungsten, and a tungsten alloy. Subsequently, this metal wiring layer of the multi-layered structure is processed by the lithography technique and the RIE (Reactive Ion Etching) technique to form the second metal interconnection 217. The obtained structure is annealed in an annealing step at 450°C for 5 minutes. The third insulation film 219 is deposited to a thickness of 400 nm using TEOS and oxygen (O 2 ) gases in a low-pressure plasma at 400°C. An opening for connecting a lead wire or a bonding wire is formed by the lithography and RIE techniques. In this case, this opening may be formed using a chemical such as NH 4 F or the like. As a result, the surface metal interconnection portion is obtained as shown in FIG. 3 (note that the opening for lead wire connection is not illustrated). FIG. 5 shows the concentration distribution of constituent elements (Ti, F, C, and O x ) on a section indicated by a broken line 5A - 5A' near the interface between the second metal interconnection 217 and the second insulation film 215, which are obtained in the above manner. The abscissa in FIG. 5 represents the depth from 5A in the direction along the line 5A - 5A', and the ordinate represents the concentration of each constituent element. A region where titanium shows a high concentration is the underlayer 217a portion, while a region where carbon (C) shows a high concentration is the second insulation film 215 region. At the depth at which titanium contacts carbon (0.26 µm in this case; note that the absolute value is of no significance), the interface between the underlayer 217a and the second insulation layer 215 is present. It should be noted that the concentration of fluorine in a region sufficiently apart from the interface of the underlayer 217a (more specifically, a region of a titanium nitride film spaced apart by 50 nm or more) is about 5 × 10 17 atoms/cm 3 , which is extremely less than the fluorine concentration in the second insulation film (about 5 × 10 21 atoms/cm 3 ). Also, the fluorine concentration at the interface is as low as about 5 × 10 19 atoms/cm 3 . Note that this concentration distribution was obtained by measurement in a state of FIG. 3, wherein the third insulation film 219 was formed. It was also confirmed that the same result was obtained on the section taken along a line 5A - 5A' in FIG. 4D, wherein the third insulation film 219 was not formed yet. The semiconductor device having such a concentration distribution and the semiconductor device described in the prior art (i.e., the semiconductor device described with reference to FIGS. 1 and 2) were subjected to an ultrasonic bonding test. A metal wire 25 µm in diameter was bonded between a bonding pad (50 × 80 µm) having the same arrangement as that of the second metal interconnection 217 on an IC chip and a terminal of a packaging part on which the IC chip is mounted with a predetermined ultrasonic output and a predetermined load. A tensile test was conducted on 100 bonding wires to check the presence of peel-off defects generated at the interface between the bonding pad and the insulation film 215. As a result, there was no peel-off defect. Consequently, it was apparent that the adhesion properties between the metal wiring underlayer 217a and the insulation film 215 could be increased by the fluorine concentration to less than 1 × 10 20 atoms/cm 3 in the range where a titanium-based metal had the highest concentration. If the diffusion of fluorine to the interconnection 217 is completely suppressed, the ideal condition can be realized. The lower limit of the fluorine concentration may be substantially 0. FIG. 6 is a sectional view showing a metal interconnection portion of a second semiconductor device. Referring to FIG. 6, a first insulation film (SiO 2 ) 212 is formed on a silicon substrate 211, and a first metal interconnection 213 is partially formed on the surface of the first insulation film 212. This metal interconnection 213 is an interconnection of a multi-layered structure constituted by a titanium-based metal underlayer 213a and a main wiring layer 213b of, e.g., an Al-Cu-Si alloy. A second insulation film 215 is formed in the remaining region of the first insulation film 212. This insulation film 215 is an SiO 2 film containing Si-F bonds 215a. The characteristic feature of this embodiment is that a third insulation film 218 is formed on this insulation film 215. In film formation, fluorine is not doped in this third insulation film 218. Plugs 216 consisting of, e.g., tungsten (W) as a via conductor are formed on the metal interconnection 213, and electrodes are extracted to the surface of the third insulation film 218 through the second insulation film 215 and the third insulation film 218. A second metal interconnection 217 is formed on the third insulation film 218, and part of the second metal interconnection 217 is connected to the plugs 216. This metal interconnection 217 is an interconnection of a multi-layered structure constituted by a titanium-based metal underlayer 217a and a conductor 217b of, e.g., an Al-Cu-Si alloy. The insulation film 215 and the metal interconnection 217 are covered with a fourth insulation film (passivation film) 219 to form a surface metal interconnection portion. The above semiconductor device is manufactured according to the following method. First, as shown in FIG. 7A, an SiO 2 film as the first insulation film 212 is deposited to a thickness of 1,500 nm on the silicon substrate 211 using TEOS and oxygen (O 2 ) gases in a low-pressure plasma. Next, Ti and TiN are sequentially deposited to film thicknesses of 50 nm and 70 nm by the sputtering method for the refractory wiring underlayer 213a, which constitutes the first metal interconnection. An Al-Cu-Si alloy for the main wiring layer 213b is deposited to a thickness of 600 nm on this wiring underlayer 213a by the sputtering method to form the metal wiring layer of the multi-layered structure. Subsequently, this metal wiring layer of the multi-layered structure is processed by the lithography and RIE techniques to form the first metal interconnection 213. Then, as shown in FIG. 7B, an SiO 2 film containing fluorine as the second insulation film 215 containing Si-F bonds is deposited to a thickness of 2,500 nm using TEOS gas, oxygen (O 2 ) gas, and a nitrofluoride (NF x ) gas in a low-pressure plasma, similar to the device of Fig.3. The second insulation film 215 contains Si-F bonds, multiple bonds such as Si-F-C bonds, and free fluorine having no bond radical. Thereafter, the surface of this insulation film is planarized by the resist etching back RIE technique. The obtained structure is introduced into a furnace in a nitrogen atmosphere at 450°C to anneal it for 15 minutes. A multiple bond in the second insulation film 215 has a lower bond energy than that of an Si-F bond and thus is in an instable bond state. As a result of this annealing, such polymer bonds, e.g., Si-F-C bonds are separated to generate CF x , and generated CF x and free fluorine are diffused outside the insulation film 215. Subsequently, as shown in FIG. 7C, the third insulation film 218 is deposited to a thickness of 300 nm using TEOS and oxygen (O 2 ) gases in a low-pressure plasma. As a film formation gas for the CVD SiO 2 film to be used here, inorganic SiH 4 may be used instead of TEOS. Further, O 3 gas may be used instead of the O 2 gas. Next,. as shown in FIG. 7D, via holes are opened for connecting the first metal interconnection to the second metal interconnection. Tungsten is selectively deposited in the via holes using WF 6 and SiH 4 gases to form the plugs 216. Similar to the first wiring underlayer, Ti and TiN for the second metal underlayer 217a are sequentially deposited to film thicknesses of 50 nm and 70 nm by the sputtering method. An Al-Cu-Si alloy for the main wiring layer 217b is deposited to a thickness of 1,200 nm on this wiring underlayer 217a by the sputtering method to form the metal wiring layer of the multi-layered structure. Subsequently, this metal wiring layer of the multi-layered structure is processed by the lithography and RIE techniques to form the second metal interconnection 217. The obtained structure is annealed in an annealing step at 450°C for 5 minutes. The fourth insulation film 219 is deposited to a thickness of 400 nm using TEOS and oxygen (O 2 ) gases in a low-pressure plasma at 400°C. An opening for connecting a lead wire or a bonding wire is formed by the lithography and RIE techniques. As a result, the surface metal interconnection portion is obtained as shown in FIG. 6 (note that the opening for lead wire connection is not illustrated). FIG. 8 shows the concentration distribution of constituent elements (Ti, F, C, and O x ) on a section indicated by a chain line 8A - 8A' near the interface between the second metal interconnection 217 and the third insulation film 218, which are obtained in the above manner. The abscissa in FIG. 8 represents the depth from 8A in the direction along the line 8A - 8A', and the ordinate represents the concentration of each constituent element. Like in the device of Fig. 3, the fluorine concentration in a region sufficiently apart from the interface of the underlayer 217a (more specifically, a region of a titanium nitride film spaced apart by 50 nm or more) is about 5 × 10 17 atoms/cm 3 , and that at the interface is as low as about 5 × 10 18 atoms/cm 3 . It should be noted that the fluorine concentration at a portion corresponding to the third insulation film 218 (a region where the carbon (C) concentration shows a value of about 1 × 10 20 atoms/cm 3 ) is less than that of the second insulation film 215 (a region where the C concentration shows a value of about 1 × 10 21 atoms/cm 3 ). This is because fluorine is not originally doped in the third insulation film 218, and the third insulation film 218 contains only fluorine which is diffused from the second insulation film 215 during annealing and remains in the third insulation film 218. Note that this concentration distribution was obtained by measurement in a state of FIG. 6, wherein the fourth insulation film 219 was formed. It was also confirmed that the same result was obtained on a section taken along the line 8A - 8A' in FIG. 7D, wherein the fourth insulation film 219 was not formed yet. In the multi-layered structure constituted in this manner, the fluorine concentration at the interface between the second metal interconnection 217 and the third insulation film 218 can be changed by changing the annealing conditions and the film formation conditions of the fluorine-doped insulation film. FIG. 9 is a graph showing a relationship between the fluorine concentration on this interface and the pad peel-off incidence during wire bonding. This relationship was examined by changing the fluorine concentration at this interface. The conditions for wire bonding are completely the same as those in the device of Fig.3. As is apparent from FIG. 9, pad peel-off does not occur at all if the fluorine concentration is less than 1 × 10 20 atoms/cm 3 in the range where a Ti-based metal had the highest concentration. In this manner, pad peel-off can be avoided by controlling the fluorine concentration at the interface. Note that SIMS (Secondary Ion Mass Spectrometry) analysis was used for measurement of the fluorine concentration in the refractory metal. TiF was used as detection ions for quantitative analysis of fluorine in the titanium layer. A Model 6600 available from Perkin Elmer was used for the SIMS. The measurement was carried out under the condition wherein the ionization. energy of Cs + ions was 5 keV. The above effect can also be obtained in a metal interconnection portion having a structure having a larger number of layers. Next, an example of a multi-layered interconnection will be described with reference to FIG. 10. This exemplifies the case wherein one more metal interconnection is stacked on the second metal interconnection of the device of Fig. 3. That is, a third 215 is formed on a second metal interconnection 217, and plugs 226 consisting of tungsten or the like are formed in predetermined portions of the second metal interconnection. On the upper portion, a third metal interconnection 220 is formed like the second metal interconnection. Further, a second insulation layer 224 covers the resultant structure. This multi-layered metal interconnection portion is manufactured as shown in FIGS. 11A and 11B. First, the same procedure as in the device of Fig. 3 is performed to form up to the second metal interconnection 217. In this stage, the concentration distribution of each constituent element along a line 5A - 5A' in FIG. 11A is the same as that in FIG. 5. Then, in the same step as for the second insulation film 215, the third insulation film 222 doped with fluorine is formed to a film thickness of 2,500 nm. The surface of this insulation,film 222 is planarized by the resist etch-back RIE technique. Subsequently, this substrate is introduced into a furnace in a nitrogen atmosphere at 450°C anneal it for 15 minutes. As a result, CF x and free fluorine are diffused outside the insulation film 222. Next, as shown in FIG. 11B, via holes are opened for connecting the second metal interconnection to the third metal interconnection. Tungsten is selectively deposited in the via holes using WF 6 and SiH 4 gases to form the plugs 226. Similar to the first wiring underlayer, Ti and TiN for a third wiring underlayer 220a are sequentially deposited to film thicknesses of 50 nm and 70 nm by the sputtering method. An Al-Cu-Si alloy for a main wiring layer 220b is deposited to a thickness of 1,200 nm on this wiring underlayer 220a by the sputtering method to form the metal wiring layer of the multi-layered structure. Subsequently, this metal wiring layer of the multi-layered structure is processed by the lithography and RIE techniques to form the third metal interconnection 220. The obtained structure is annealed in an annealing step at 450°C for 5 minutes. The second insulation film 224 is deposited to a thickness of 400 nm using TEOS and oxygen (O 2 ) gases in a low-pressure plasma at 400°C. An opening for connecting a lead wire or a bonding wire is formed by the lithography and RIE techniques. As a result, the three-layered metal interconnection portion is obtained as shown in FIG. 10 (note that the opening for lead wire connection is not illustrated). At this time, the concentration distribution of each constituent element on a section taken along a line 12B - 12B' in FIG. 10 showed the same result as in the device of Fig. 3. The surface metal interconnection formed in this manner was subjected to a bonding test, like in the device of Fig. 3. It was confirmed that there was no pad peel-off defects caused by bonding. FIG. 13 exemplifies the case wherein one more metal interconnection is stacked on the second metal interconnection of the second embodiment. That is, a third insulation film 222 similar to a second insulation film 215 is formed on a second metal interconnection 217, and a fourth insulation film 223 is further stacked thereon. Plugs 226 consisting of tungsten are formed in predetermined portions of the second metal interconnection. On the upper portion, a third metal interconnection 220 is formed like the second metal interconnection. Further, a second insulation layer 224 covers the resultant structure. This multi-layered metal interconnection portion is manufactured as shown in FIGS. 14A and 14B. First, the same procedure as in the second embodiment is performed to form up to the second metal interconnection 217. The concentration distribution of each constituent element along a line 8A - 8A' in FIG. 14A becomes the same as that in FIG. 8. Then, in the same step as for the second insulation film 215, the third insulation film 222 doped with fluorine is formed to 2,500 nm. The surface of this insulation film 222 is planarized by the resist etch-back RIE technique. Subsequently, this substrate is introduced into a furnace in a nitrogen atmosphere at 450°C to anneal it for 15 minutes. As a result, CF x and free fluorine are diffused outside the insulation film 222. Next, via holes are opened for connecting the second metal interconnection to the third metal interconnection. Tungsten is selectively deposited in the via holes using WF 6 and SiH 4 gases to form the plugs 226. Similar to the first wiring underlayer, Ti and TiN for a third wiring underlayer 220a are sequentially deposited to film thicknesses of 50 nm and 70 nm by the sputtering method. An Al-Cu-Si alloy for a main wiring layer 220b is deposited to a thickness of 1,200 nm on this wiring underlayer 220a by the sputtering method to form the metal wiring layer of the multi-layered structure. Subsequently, this metal wiring layer of the multi-layered structure is processed by the lithography and RIE techniques to form the third metal interconnection 220. The obtained structure is annealed in an annealing step at 450°C for 5 minutes. The second insulation film 224 is deposited to a thickness of 400 nm using TEOS and oxygen (O 2 ) gases in a low-pressure plasma at 400°C. An opening for connecting a lead wire or a bonding wire is formed by the lithography and RIE techniques. As a result, the three-layered metal interconnection portion is obtained as shown in FIG. 13 (note that the opening for lead wire connection is not illustrated). At this time, the concentration distribution of each constituent element on a section taken along a line 15B - 15B' in FIG. 13 showed the same result as in the device of Fig. 6. The surface metal interconnection formed in this manner was subjected to a bonding test, like in the device of Fig. 6. It was confirmed that there was no pad peel-off defects caused by bonding. The formation method for a multi-layered interconnection is not limited to the above examples, and various modifications may be effected. For example, it is possible to manufacture an insulation layer between the first and second layers of a three-layered interconnection by the same method as for the device of Fig. and to manufacture an insulation layer between the second and third layers by the method used for the device of Fig. 6. As described above, the adhesion strength of a multi-layered interconnection, which uses a titanium-based metal formed on an Si-F-containing insulation film as an underlayer, is improved by paying attention to the concentration of fluorine contained in the underlayer. A further analysis of the adhesion mechanism between the underlayer and the insulation film reveals the following fact. When the boundary between the metal wiring underlayer and the insulation film represented by a circle 16 in FIG. 3 is enlarged, a reaction layer 230 several nm thick interposes therebetween, as shown in a photomicrograph of FIG. 16. It is considered that the reaction layer 230 is constituted such that SiO 2 contained in the insulation film 215 reacts with Ti of the underlayer to form a reaction product of Ti x Si y O z . The constituent elements of the reaction layer obtained in the device of Fig. 3 and those of the reaction layer obtained in the prior art, in which no fluorine removal process was performed, were analyzed with the EDX (Energy Dispersed X-ray spectrometer), thereby obtaining the following results shown in Table 1. Constituent Element Content (atomic%) Embodiment 1 Prior Art Ti 7.15 38.08 Si 41.99 43.77 F 0 0.64 O 50.86 15.48 N 0 0 C 0 2.03 The ratio of Ti to Si and that of Ti to O were calculated from Table 1, and the results are shown in Table 2. Embodiment 1 Prior Art Ti/Si 0.17 0.87 Ti/O 0.14 2.46 From Table 2, it is found that the ratio of Ti to Si in the reaction layer obtained in the first embodiment is as very low as 0.2 or less (Ti/Si < 0.2), and the ratio of Ti to O is also as very low as 0.2 or less (Ti/O < 0.2). On the other hand, both the ratios are as very high as 0.8 or more in the reaction layer of the prior art, in which no fluorine removal process is performed. An examination of a relationship between the bonding strength and the thickness of the reaction layer. reveals the following results shown in FIG. 17. The strength of 3g or more, which is considered to be in a good bonding state, is obtained in a reaction layer 3.5 nm or less thick. The ratios of constituent elements of a reaction layer corresponding to a bonding strength of 7.5 g were analyzed·with the EDX, and the results are shown in FIG. 18. It is found that the Ti amount in the reaction layer is 100% or less with respect to Si and O . The ratios of constituent elements of a reaction layer corresponding to a bonding strength of 1.5 g were analyzed with the EDX, and the results are shown in FIG. 19. It is found that the Ti amount in the reaction layer greatly exceeds the amounts of Si and O except for a part. Note that, in FIGS. 18 and 19, each abscissa indicates not actual distances but a schematic positional relationship of measurement points. The thickness of the reaction layer 230 is 2 to 3 nm in FIG. 18, and 4 to 6 nm in FIG. 19. FIG. 20 shows a comparison between fluorine removal and the prior art, in which no fluorine removal process is executed, by calculating Ti/Si and Ti/O values. At least on the central portion of a reaction layer in a direction of film thickness, the two ratios of elements are 1.0 or less in the present invention, while those ratios are 1.0 or more in the prior art. That is, the characteristic relationship becomes apparent in which the adhesion strength in the reaction layer having small ratios of Ti to Si and O is superior to the adhesion strength in the prior art. Although this mechanism has not been clarified yet, it is considered that diffusion of F to the Ti layer greatly involves in this phenomenon. From the above finding, it was supposed that an increase in adhesion strength of the underlayer could be realized by preventing diffusion of F to the reaction layer. To achieve this prevention of F diffusion, the device of Fig. 21 described below and an embodiment of the invention described thereafter are both proposed from a viewpoint different from that of the devices of Figs. 3 to 13. FIG. 21 is a sectional view showing a metal interconnection portion of a fifth semiconductor device not forming part of the present invention. Referring to FIG. 21, a first insulation film (SiO 2 ) 212 is formed on an Si substrate 211, and a first metal interconnection 213 is partially formed on the surface of the first insulation film 212. This metal interconnection 213 is an interconnection of a multi-layered structure constituted by a titanium-based metal underlayer 213a and a main wiring layer 213b of, e.g., an Al-Cu-Si alloy. A second insulation film 215 is formed in the remaining region of the first insulation film 212. This insulation film 215 is an SiO 2 film containing Si-F bonds. The characteristic feature of this embodiment is that a first fluorine diffusion suppression film 231 is formed on this insulation film 215. This fluorine diffusion suppression film 231 may be an insulation film or a conductive film. In the case of an insulation film, an SiN film, an SiH 4 -SiO 2 film formed by an SiH 4 -based gas, an SiON film doped with oxygen during SiN film formation, or the like can be used. In the case of a conductive film, a polysilicon film, a W-, Ti-, Co- or Ni-based metal silicide film, an Al- or Cu-based metal film, or a multi-layered structure of these films can be employed. The fluorine diffusion suppression film 231 is processed so as to be selectively arranged under a portion serving as an interconnection region for bonding wire connection (bonding pad). Thereafter, a third insulation film 218 is formed of, e.g., SiO 2 on the fluorine diffusion suppression film 231 and the second insulation film 215. A plug 216 consisting of, e.g., tungsten (W) as a via conductor is formed on the metal interconnection 213. Electrodes are extracted to the surface of the third insulation film 218 through the second insulation film 215 and the third insulation film 218. A second metal interconnection 217 is formed on the insulation film 218, and part of the second metal interconnection 217 is connected to the plug 216. This metal interconnection 217 is an interconnection of a multi-layered structure constituted by a titanium-based metal underlayer 217a and a main wiring layer 217b of, e.g., an Al-Cu-Si alloy. The insulation film 218 and the metal interconnection 217 are covered with a fourth insulation film (passivation film) 219 to form a surface metal interconnection portion. The above semiconductor device is manufactured by the following method. Following the same procedures as in the device shown in FIGS. 4A and 4B, the first insulation film 212, the first metal interconnection 213, and the. second insulation film 215 are formed on the substrate 211. Then, as shown in FIG. 22A, e.g., an SiN insulation film as the fluorine diffusion suppression film 231 is deposited to a thickness of 200 nm on the second insulation film 215 containing Si-F bonds by the low-pressure plasma CVD method. Subsequently, the SiN film is etched by the lithography technique and the CDE or RIE technique so as to leave the SiN film only in the region under the pad portion for bonding wire connection to be formed. The same procedure is performed for use of an SiH 4 -SiO 2 film, an SiON film, a polysilicon film, or a metal film as this fluorine diffusion suppression film 231. Each film is etched by the lithography technique so as to be selectively arranged in the region under the bonding pad. The third insulation film 218 is deposited to a thickness of 300 nm using TEOS and oxygen (O 2 ) gases in a low-pressure plasma. Next, as shown in FIG. 22B, a via hole is opened for connecting the first metal interconnection to the second metal interconnection. Tungsten is selectively deposited in the via hole using WF 6 and SiH 4 gases to form the plug 216. Similar to the first wiring underlayer, Ti and TiN for the second metal underlayer 217a are sequentially deposited to film thicknesses of 50 nm and 70 nm by the sputtering method. An Al-Cu-Si alloy for the main wiring layer 217b is deposited to a thickness of 1,200 nm on this wiring underlayer 217a by the sputtering method to form the metal wiring layer of the multi-layered structure. Subsequently, this metal wiring layer of the multi-layered structure is processed by the lithography and RIE techniques to form the second metal interconnection 217. The obtained structure is annealed in an annealing step at 450°C for 5 minutes. The fourth insulation film 219 is deposited to a thickness of 400 nm using TEOS and oxygen (O 2 ) gases in a low-pressure plasma at 400°C. An opening for a bonding pad 232 is formed by the lithography and RIE techniques. As a result, the surface metal interconnection portion is obtained as shown in FIG. 21. The vicinity of the interface between the second metal interconnection 217 and the third insulation film 218, which were obtained in this manner, was analyzed. As a result, formation of a reaction layer 230 as shown in FIG. 16 was confirmed. The thickness of the reaction layer was 2.6 nm on a section taken along a broken line C - C' line in FIG. 22B, and 4.1 nm on a section taken along a broken line D - D' line. The ratios of constituent elements in the reaction layer were analyzed with the EDX. The constituent ratios Ti/Si and Ti/O were as low as about 0.3 in the central portion of the reaction layer in a direction of film thickness along the line C - C', while those were higher than 1 in the reaction layer along the line D - D'. That is, it was confirmed that the content of Ti was small in the region (bonding pad region) where the adhesion properties between Ti and SiO 2 were to be enhanced. The fluorine concentrations in the Ti underlayer 217a and the reaction layer 230 were examined to be less than 1 × 10 20 atoms/cm 3 . The semiconductor device having such a concentration distribution was subjected to an ultrasonic bonding test. A metal wire 25 µm in diameter was bonded between a bonding pad (50 × 80 µm) having the same arrangement as that·of the second metal interconnection 217 on an IC chip and a terminal of a packaging part on which the IC is mounted with a predetermined ultrasonic output and a predetermined load. A tensile test was conducted on 100 bonding wires to check the presence of peel-off defects generated at the interface between the bonding pad and the insulation film 218. As a result, there was no peel-off defect. Consequently, it was apparent that the properties between the metal wiring underlayer 217a and the insulation film 218 could be increased using the technique by which the constituent ratios Ti/Si and Ti/O became less than 1.0. (Embodiment of the Invention) FIG. 23 is a sectional view showing a metal interconnection portion of a semiconductor device according to an embodiment of the present. invention. Referring to FIG. 23, a first insulation film (SiO 2 ) 212 is formed on a silicon substrate 211, and a first metal interconnection 213 is partially formed on the surface of the first insulation film 212. This metal interconnection 213 is an interconnection of a multi-layered structure constituted by a titanium-based metal underlayer 213a and a main wiring layer 213b of, e.g., an Al-Cu-Si alloy. A second insulation film 215 is formed in the remaining region of the first insulation film 212. This insulation film 215 is an SiO 2 film containing Si-F bonds. The characteristic feature of this embodiment is to partially remove this insulation film 215. Part or all of the insulation film 215 at a portion serving as an interconnection region for bonding wire connection where the adhesion properties between Ti and SiO 2 are to be enhanced is selectively removed by the lithography technique, the CDE or RIE technique, and the like. For example, when the insulation film 215 has a normal thickness of 800 nm, it is removed by a thickness of 600 nm in the region under the bonding pad 232. Although it is considered to thin the overall thickness of the insulation film 215, the capacitance between the interconnections formed on different two layers increases to degrade a high-speed operation. For this reason, it is desirable to thin the insulation film 215 only under the bonding pad 232. A thickness of the insulation film under the bonding pad may be preferably 100 to 600 nm, more preferably 200 to 500 nm. The above semiconductor device is manufactured by the following method. Following the same procedures as in the device shown in FIGS. 4A and 4B, the first insulation film 212, the first metal interconnection 213, and the second insulation film 215 are formed on the substrate 211. Note that, in this embodiment, the thickness of the second insulation film 215 is set to be 800 nm. Then, as shown in FIG. 24A, the insulation film 215 at a portion under the region where the bonding pad is to be formed is selectively removed by a thickness of 600 nm according to the lithography technique, the CDE or RIE technique, and the like. Subsequently, a third insulation film 218 is deposited to a thickness of 300 nm using TEOS and oxygen (O 2 ) gases in a low-pressure plasma. Next, as shown in FIG. 24B, a via hole is opened for connecting the first metal interconnection to the second metal interconnection. Tungsten is selectively deposited in the via hole using WF 6 and SiH 4 gases to form a plug 216. Similar to the first wiring underlayer, Ti and TiN for a second metal underlayer 217a are sequentially deposited to film thicknesses of 50 nm and 70 nm by the sputtering method. An Al-Cu-Si alloy for a main wiring layer 217b is deposited to a thickness of 1,200 nm on this wiring underlayer 217a by the sputtering method to form the metal wiring layer of the multi-layered structure. Subsequently, this metal wiring layer of the multi-layered structure is processed by the lithography and RIE techniques to form a second metal interconnection 217. The obtained structure is annealed in an annealing step at 450°C for 5 minutes. A fourth insulation film 219 is deposited to a thickness of 400 nm using TEOS and oxygen (O 2 ) gases in a low-pressure plasma at 400°C. An opening for a bonding pad 232 is formed by the lithography and RIE techniques. As a result, a surface metal interconnection portion is obtained as shown in FIG. 23. The vicinity of the interface between the second metal interconnection 217 and the third insulation film 218, which were obtained in this manner, was analyzed. As a result, formation of a reaction layer 230 as shown in FIG. 16 was confirmed. The thickness of the reaction layer was 2.7 nm on a section taken along a chain line E - E' in FIG. 23, and 4.0 nm on a section taken along a chain line F - F'. The ratios of constituent elements in the reaction layer were analyzed with the EDX. The constituent ratios Ti/Si and Ti/O were as low as about 0.3 in the reaction layer along the line E - E', while those were higher than 1 in the reaction layer along the line F - F'. That is, it was confirmed that the content of Ti was small in the region where the adhesion properties between Ti and SiO 2 were to be enhanced. The semiconductor device having such a concentration distribution was subjected to an ultrasonic bonding test. A metal wire 25 µm in diameter was bonded between a bonding pad (50 × 80 µm) having the same arrangement as that of the second metal interconnection 217 on an IC chip and a terminal of a packaging part on which the IC is mounted with a predetermined ultrasonic output and a predetermined load. A tensile test was conducted on 100 bonding wires to check the presence of peel-off defects generated at the interface between the bonding pad and the insulation film 218. As a result, there was no peel-off defect. Consequently, it was apparent that the adhesion properties between the metal wiring underlayer 217a and the insulation film 218 could be increased by decreasing the thickness of the insulation film 215 containing Si-F bonds. This is because the content of fluorine, which is the diffusion source, is originally small in the thin layer. In a multi-layered interconnection having three or more layers, the method of manufacturing the device of Fig. 21 and the described embodiment is used only for a surface layer, and the method of manufacturing the devices of Figs. 3 to 13 or the prior art is used ror the remaining lower layers. In the manufacturing method of the device of Fig. 21 and of the described embodiment, the insulation film 218 not containing Si-F radicals-is interposed between the insulation film 215 containing Si-F bonds and the metal interconnection 217, but this insulation film 218 can be omitted. Note that, to reliably suppress diffusion of fluorine to the metal interconnection 217, it is desirable to interpose the insulation film 218 not containing Si-F bonds. In the above-described embodiments, silicon substrates are used for the substrates for the present invention. However, the substrates are not limited to silicon substrates. Any substrate material generally used for a semiconductor device can be used for the present invention. As has been described above, according to the present invention, the following process is performed on an insulation film containing Si-F bonds. That is, the thickness of the insulation film is decreased. Thereafter, a metal interconnection containing Ti is formed on this insulation film. The adhesion properties between the insulation film and the Ti-based metal wiring layer is enhanced by setting the fluorine concentration at the interface between Ti and the insulation film to less than 1 × 10 20 atoms/cm 3 . Therefore, the semiconductor device having high reliability wherein no peel-off occurs between Ti and the insulation film can be realized.

Claims: A semiconductor device comprising: a substrate (211) having a first and a second region; a first insulating film (215, 218) made of silicon oxide and formed above said substrate (211) and containing silicon-fluorine bonds, said first insulating film (215, 218) having a first thickness on said first region and having a second thickness greater than said first thickness on said second region; a metal interconnection (217) formed on said first insulating film (215, 218) of said first region, the metal interconnection including a titanium-based underlayer (217a) on the first insulating film of said first region and a main wiring layer (217b) on the underlayer; and a second insulating film (219) at least formed on said metal interconnection (217) and having an opening for wire bonding on said metal interconnection (217) above said first region of said substrate (211), wherein the fluorine concentration at the interface between the titanium-based underlayer and the first insulating film above said first region is less than 1 x 10 20 atoms/cm 3 . A device according to claim 1, wherein a film thickness of said first insulating film (215, 218) above said first region falls in a range from 100 to 600 nm.

Inventors: MATSUNO TADASHI, MATSUNO, TADASHI, Matsuno, Tadashi, Kabushiki Kaisha Toshiba
Applicants: TOSHIBA KK, KABUSHIKI KAISHA TOSHIBA
Application year: 1995
Main classification: H01L23
IPC codes: H01L23, H01L21