Rechargeable lithium battery

Abstract: A rechargeable lithium cell comprising an anode, a separator, a cathode, and an electrolyte or an electrolyte solution, characterized in that said anode comprises (a) a metal capable of being alloyed with lithium and (b) a metal incapable of being alloyed with lithium, said anode contains lithium when charging is operated, and wherein an anode terminal is extended from a portion formed of said metal (b).

Description: The present invention relates to an improved rechargeable lithium battery . More particularly, the present invention relates to an improved rechargeable lithium battery which exhibits an excellent current collecting performance and is free of occurrence of dendrite (or branched tree-like protrusions) of lithium upon repetition of charging and discharging. It also concerns the anode prepared therefor. In recent years, heating of the earth because of the so-called greenhouse effect due to an increase of atmospheric CO 2 has been predicted. In the case of the steam-power generation, the amount of a fossil fuel represented by coal or petroleum to be consumed for power generation in order to comply with a societal demand for increased power supply has been continuously increased and along with this, the amount of exhaust fumes from the steam-power generation plants has been continuously increased accordingly to raise the content of gases to cause a greenhouse effect such as carbon dioxide gas in the air. This results in providing an earth-warming phenomenon. In order to prevent said earth-warming phenomenon from further developing, there is a tendency of prohibiting to newly establish a steam-power generation plant in some countries. Under this circumstance, there have been made a proposal of conducting so-called load leveling in order to effectively utilize the power generator, wherein rechargeable batteries are installed at general houses and a surplus power unused in the night, that is, a so-called dump power, is stored in said rechargeable batteries and the power thus stored is supplied in the daytime when the power demand is increased, whereby the power generator is leveled in terms the load therefor. By the way, there is an increased societal demand for developing a lightweight rechargeable battery with a high energy density for an electric vehicle which does not exhaust any air polluting substance such as CO x , NO x , SO x , hydrocarbon, and the like. Other than this demand, there are another increased societal demand for developing a miniature, lightweight, high performance rechargeable battery usable as a power source for portable instruments such as small personal computers, word processors, video cameras, and pocket telephones. As such rechargeable buttery, there has been proposed a rocking chair type lithium ion rechargeable battery in which a lithium intercalation compound is used as a cathode active material and carbon is used as an anode active material. However, as of the present time, there has not realized a practically usable lithium ion rechargeable battery having a sufficiently high energy density, which is considered could be attained by using a metallic lithium as the anode active material. The public attention has now focused on the rechargeable lithium battery in which metallic lithium is used as an anode, but as of the present time, there has not yet attained a practically usable, high capacity rechargeable lithium battery with an improved energy density. Particularly, as for the known rechargeable lithium battery, there is a problem in that lithium is often deposited in a dendritic state (that is, in the form of a dendrite) on the negative electrode (or the anode) upon the charging operation, wherein such dendritic deposition of lithium metal results in causing internal-shorts or self-discharge. As one of the reasons why such practically usable, high capacity rechargeable lithium battery as above described has not yet realized, there is a fact that a manner capable of preventing the occurrence of the above dendritic lithium deposition has not developed. Now, as above described, when the above lithium dendrite should be once formed, the dendrite is liable to gradually grow upon the charging, resulting in causing internal-shorts between the anode and the cathode. When the anode suffers from internal-shorts with the cathode as above described, the energy possessed by the battery is shortly consumed at the short-circuited portion to entail problems such that the battery is heated or the solvent of the electrolyte is decomposed by virtue of heat to generate gas, resulting in raising the inner pressure of the battery. These problems result in damaging the battery or/and shortening the lifetime of the battery. There has been proposed a manner of using a lithium alloy such as lithium-aluminum alloy as the anode for a rechargeable lithium battery in order to suppress the reactivity of the lithium so that a lithium dendrite is hardly generated. This manner is effective in preventing the generation of the lithium dendrite but is not effective in attaining a rechargeable lithium battery having a high energy density and which is long enough in cycle life. Particularly, Japanese Unexamined Patent Publication No. 13264/1988 (hereinafter referred to as document 1), No. 47381/1993 (hereinafter referred to as document 2) or No. 190171/1993 (hereinafter referred to as document 3) discloses a non-aqueous series rechargeable battery in which the anode is constituted by a lithium alloy. However, any of the rechargeable batteries disclosed in these documents 1 to 3 is problematic in that as the charging and discharging are repeated, the anode is repeatedly expanded and shrunk to often suffer from a crack, wherein the rechargeable battery eventually becomes poor in current collecting performance. Additionally, Japanese Unexamined Patent Publication No. 114057/1988 (hereinafter referred to as document 4) discloses a non-aqueous series rechargeable battery in which the anode is constituted by a basic constituent comprising a sintered body of a mixture composed of fibrous aluminum and fibrous metal incapable of being alloyed with lithium and a negative material comprising a lithium-aluminum alloy. However, the rechargeable battery disclosed in the document 4 is problematic in that as the charging and discharging are alternately repeated over a long period of time, expansion and shrinkage are liable to repeatedly occur at the fibrous aluminum to deteriorate its adhesion with the fibrous metal incapable of being alloyed with lithium or to cause a crack at the interface between the fibrous aluminum and the fibrous metal, wherein the rechargeable battery eventually becomes poor in current collecting performance. Further, Japanese Unexamined Patent Publication No. 234585/1993 (hereinafter referred to as document 5) discloses a non-aqueous series rechargeable battery in which the anode is constituted by a member made of lithium metal having powdery metal (which hardly forms an intermetallic compound with said lithium metal) uniformly deposited on the surface thereof. As for this rechargeable battery, the document 5 describes that it is slight in terms of the generation of a dendrite, high in charging and discharging efficiencies, and long in cycle life. However, the rechargeable battery disclosed in the document 5 is still problematic in that as the charging and discharging are alternately repeated, expansion and shrinkage are liable to repeatedly occur at the lithium metal member and as a result,the powdery metal deposited on the lithium metal member is often removed or a crack is often occurred at the lithium metal member, resulting in making it difficult to sufficiently prevent the occurrence of a dendrite and also in making the rechargeable battery to be poor in current collecting performance. Further in addition, Journal of Applied Electrochemistry, 22, 620-627 (1992) (hereinafter referred to as document 6) discloses a rechargeable lithium battery in which the anode (or the negative electrode) is constituted by an aluminum foil having a surface applied with etching treatment. However, the rechargeable lithium battery disclosed in the document 6 is problematic in that when the charging and discharging cycle is repeated as many as that practically conducted for the ordinary rechargeable battery, problems are liable to entail in that as the charging and discharging are alternately repeated, the aluminum foil is repeatedly expanded and shrunk to suffer from a crack, resulting in causing a reduction in the current collecting performance, wherein the growth of a dendrite is liable to occur. Hence, any of the rechargeable batteries disclosed in the documents 1 to 6 is still accompanied by some problems required to be solved. Accordingly, there is an increased demand for provision of an improved rechargeable lithium battery which is high in energy density and long enough in cycle life. US-A-4626335 discloses an anode for a battery cell wherein particles of a lithium alloy are compacted under pressure with particles of an inactive metal which binds the alloy particles together but does not alloy with them. EP-A-0323888 discloses an anode for a rechargeable lithium battery formed by an aluminum alloy containing fine particles of Ni, Fe or the like dispersed in aluminium. US-A-4690840 discloses an electrode comprising a layer of a host metal which can alloy with lithium, which layer is formed on a metallic sheet. The metallic sheet preferably comprises a good electronic conductor such as Cu, Ni, Al, Zn, Mo. A rechargeable lithium battery and an anode prepared therefor, each in accordance with the present invention, are defined respectively in claims 1 and 15 appearing hereinafter. In the accompanying drawings: FIG. 1 is a graph showing measured results for the surface of an anode for a rechargeable lithium battery by means of the tracer method, which were obtained as a result of the experimental studies by the present inventors. FIG. 2 is a known graph showing a typical relationship between (a) a difference between a height corresponding to a 1/2 of the maximum height Rmax for the surface roughness of an electrically conductive material disposed on the surface of an anode and a central line average roughness Ra for said surface roughness and (b) a given cycle life for the anode. FIG. 3 is a graph showing typical relationships between a value of the equation: 1 + (4nRa/L) (with Ra being a central line average roughness, L being a length measured, and n being the number of peaks present per the length L) and the cycle life of a given anode for a rechargeable lithium battery, which were obtained as a result of the experimental studies by the present inventors. FIGs. 4(a) through 4(h) are schematic cross-sectional views respectively for explaining examples and comparative examples of an anode for a rechargeable lithium battery according to the present invention. FIG. 5 is a schematic diagram illustrating the constitution of an example of a rechargeable lithium battery according to the present invention. FIG. 6 is a schematic cross-sectional view illustrating a single-layer system flat rechargeable battery. FIG. 7 is a schematic cross-sectional view illustrating a spiral-wound cylindrical rechargeable battery. The present invention is to eliminate the foregoing problems found in the known rechargeable lithium battery and to attain the above described objects. The present invention has been accomplished based on a finding obtained through experimental studies by the present inventors that when an anode constituted by a composite material comprising a metal capable of being alloyed with lithium and another metal incapable of being alloyed with lithium is properly used, there can be attained an improved rechargeable lithium battery which is free of the generation of a dendrite which is found in the known rechargeable lithium battery, and which has a prolonged cycle life. A typical embodiment of the rechargeable lithium battery according to the present invention comprises an anode, a separator, a cathode, an electrolyte or an electrolyte solution, and a housing, and in which said anode comprises (a) a metal capable of being alloyed with lithium and (b) a metal incapable of being alloyed with lithium, said anode contains lithium when charging is operated, and wherein an outputting terminal on the side of said anode is extended from a portion formed of said metal (b). Particularly, in the secondary lithium cell according to the present invention, the anode is designed to have a collector portion comprised of a metal incapable of being alloyed with lithium. Because of this, the anode is always free from occurrence of the deposition or elution of lithium resulting in causing a crack at the anode upon repetition of the charging and discharging cycle, wherein the anode is always maintained in a stable state without being broken into fine particles. This situation makes the rechargeable battery stably exhibit an excellent current collecting performance without being deteriorated. In the present invention, the anode is designed such that the content of the metal incapable of forming an alloy with lithium is enhanced at the surface thereof which is contacted with the electrolyte or electrolyte solution and which is opposed to the cathode. The content of metal incapable of forming an alloy with lithium may also be enhanced at the collector portion in contact with the power output terminal. Now, in a rechargeable lithium battery in which the anode comprises a metal capable of being alloyed with lithium, there is a tendency for the anode to entail problems such that, upon charging, lithium is deposited to form an alloy wherein the anode is expanded and, upon discharging, lithium is eluted into the electrolyte solution wherein the anode is shrunk, whereby a crack occurs at the anode to break part of the anode into fine particles (this situation will be hereinafter referred to as "powdering"). This powdering most actively occurs at the anode's highly reactive surface where a metal capable of being alloyed with lithium is present. The portion wherein powdering has occurred is of a reduced conductivity and poor in current collecting performance. However, in the case where a metal incapable of being alloyed with lithium is incorporated at an enhanced content in the anode's surface which is contacted with the electrolyte solution and which is opposed to the cathode, a sufficient conductivity is maintained at the anode electrode through said metal incapable of being alloyed with lithium and because of this, the anode is prevented from being reduced in terms of the current collecting performance, even when powdering has occurred at a certain magnitude. In the present present invention, the anode comprising a metal (a) capable of being alloyed with lithium and a metal (b) incapable of being alloyed with lithium may be a composite formed by fixing a powdery material containing a metal capable of being alloyed with lithium to a material comprised of a metal incapable of being alloyed with lithium which can serve as an anode collector using a binding agent. Alternatively, the anode may be a sintered body obtained by subjecting said composite to sintering treatment. In any case, by constituting the anode for a rechargeable lithium battery by said composite or said sintered body, there are provided various advantages as will be described in the following. That is, first, the anode is free of the occurrence of a crack resulting in breaking the anode, which is caused when expansion due to the formation of an alloy with lithium upon charging and shrinkage due to the elution of lithium upon discharging are repeatedly carried out. And, since powdery material is used for the formation of the anode, an increase can be attained for the specific surface area of the anode wherein the area of the anode to be contacted with the electrolyte solution is increased, and this situation enables lithium ion to be readily diffused into the anode. Further, the specific surface area of the anode can be increased by way of - etching treatment for the surface of the anode formed as above described, wherein advantages are provided in that a dendritic deposition of lithium is prevented from growing upon charging, and both the charging efficiency and discharging efficiency are improved. In addition, the thickness of the anode, the content of each of the metal (a) capable of being alloyed with lithium and the metal (b) incapable of being alloyed with lithium in the anode may be easily controlled as desired. Now, in the case where the anode comprises a composite formed by fixing a powdery material (i) containing a metal capable of being alloyed with lithium to a material (ii) comprised of a metal incapable of being alloyed with lithium which can serve as an anode collector (or an anode current collector) using a binding agent wherein the composite is not subjected to sintering treatment, it is necessary for the powdery material (i) to be incorporated with an electrically conductive auxiliary such as powdery carbon or powdery metal in an amount of 1 to 25 wt.% so that the respective particles of the powdery material (i) possess an increased current collecting property. The powdery carbon or powdery metal as the electrically conductive auxiliary is desired to be of a small bulk density, wherein the anode becomes such that readily holds the electrolyte solution and has a reduced impedance. Specifically, the electrically conductive auxiliary is desired to be of a bulk density of 0.1 or less. As for the powdery carbon or powdery metal as the electrically conductive auxiliary, the smaller the mean particle size is, the more the effect is improved. In order to attain a desirable packing density while attaining a desirable current collecting property, it is preferable to use an electrically conductive auxiliary comprising a carbon or metal in the form of a sphere, acicular or flake shape. In the case where the anode comprises a sintered body obtained by subjecting the above described composite to sintering treatment, it is preferable to use, as-the binding agent, an inorganic material or an organic material which hardly generates a corrosive gas such as halogen gas under high temperature condition. Specific examples of such organic material are, for example, high-molecular compounds which can be readily carbonized. The sintering treatment is desired to be conducted under reduced pressure or in the presence of inert gas or reducing gas. Alternatively, it is possible for the anode to comprise an alloy of a metal capable of being alloyed with lithium and other metal incapable of being alloyed with lithium. In this case, an improvement is attained for the anode in that not only the exterior but also the inside is provided with a desirable current collecting property and the anode has a prolonged charging and discharging cycle life. As for the foregoing material (i) containing a metal capable of being alloyed with-lithium for the anode, it may comprise an alloy of two or more different metals each having a different etching speed and capable of being selectively etched. In this case, by subjecting the anode to selective etching treatment, the anode can be made such that it has a markedly increased specific surface area. In any case, in the present invention, it is desired to make the anode to have a large specific surface area by subjecting the foregoing constituent metal (a) capable of being alloyed with lithium or the foregoing constituent metal (b) incapable of being alloyed with lithium to selective etching treatment. In the case where the specific surface area of the anode is increased in this way, there are provided pronounced advantages in that the reactivity of the surface of the anode is increased to provide a reduction in the substantive current density, the charge and discharge reactions are made such that they effectively take place, and the cycle life is prolonged. In the case where protrusions are present at the surface of the anode which is provided with a plurality of irregularities such that it has an increased specific surface area, electric fields are centralized at the protrusions to provide an increase in the current density, resulting in a problem that the growth of a dendrite of lithium often occurs to cause internal-shorts between the anode and the cathode. In order to prevent occurrence of this problem, it is preferable for the anode to be designed such that the difference between (i) a height corresponding to a 1/2 of the maximum height Rmax (that is, a distance between the tip of the highest peak and the bottom point of the deepest valley) for the surface roughness of the electrically conductive material at the anode's surface which is contacted with the electrolyte solution and is opposed to the cathode and (ii) a central line average roughness Ra is 1/10 or less of the distance between the anode's surface and the cathode's surface. A pronounced effect is provided when the ratio of the electrical conductivity of the tip portion at the anode's surface (roughened surface) to the electrical conductivity of the valley portion at said anode's surface is 10 or less. Even if the above difference should be greater than 1/10 of the distance between the anode's surface and the cathode's surface, as long as the protrusions have an electrical resistance which is greater than that possessed by the flat portions, no electric line of force is centralized at the protrusions wherein the field intensity is not increased, and therefore, the growth of a dendrite of lithium does not occur at the protrusions when charging. Now, shown in FIG. 1 is an indication standard for the surface roughness of a material (see, N. Kinoshita, et al, Collection of Surface Polishing and Finishing Techniques, p.p. 217-219, published by Nikkei Gijitsu Tosho Kabushiki Kaisha, May 20, 1984). The present inventors made studies through experiments in order to examine the relationship between the surface roughness of a given material for the anode for a rechargeable lithium battery and the cycle life of the anode while referring to the indication standard shown in FIG. 1. That is, there were provided aluminum foils and copper foils each having a different surface roughness. As for the surface of each of these metal foils, the maximum height Rmax and the central line roughness Ra, which are described in FIG. 1, were measured by means of the tracer method. Using these metal foils, there were prepared a plurality of rechargeable lithium batteries by the conventional manner, wherein their anodes were formed using the aluminum foils or copper foils, and their cathodes were formed by applying a coating composition obtained by mixing lithium cobalt oxide (LiCoO 2 ), acetylene black, and polyvinylidene fluoride onto the surface of the aluminum foil. Then, as for each of the resultant rechargeable lithium batteries, charging and discharging were alternately repeated many times, wherein charging was operated under conditions of readily causing the growth of a dendrite of lithium, and the charging and discharging cycle life of the rechargeable battery was examined. The examined results obtained are graphically shown in FIG. 2, in relation to values obtained by the equation: (the maximum height of the surface irregularities of the electrical conductive material at the anode's surface opposite the cathode)/2 - a central line average roughness/a distance between the anode's surface and the cathode's surface. From the results shown in FIG. 2, there were obtained findings. That is, there can be established a certain interrelation among (i) the difference between a value corresponding to a 1/2 of the maximum height Rmax of the surface irregularities of the electrical conductive material at the anode's surface opposite the cathode and the central line average roughness Ra for the surface irregularities at the anode's surface and (ii) the cycle life (that is, the charging and discharging cycle life) of the anode. And the cycle life of the anode is prolonged when the difference between a value obtained by the equation: [(the maximum height of the surface irregularities of the electrical conductive material at the anode's surface opposite the cathode) - (the minimum height of said irregularities)] x 1/2 and the central line average roughness of said irregularities is made to be 1/10 or less of the distance between the anode's surface and the cathode's surface. In addition, there was obtained a further finding as for the surface roughness of the electrically conductive material at the surface of the anode. That is, it is desired for the electrically conductive material at the surface of the anode to have a surface roughness satisfying the equation: 1 + (4nRa/L) ≧ 1.05, with Ra being a central line average roughness, L being a length measured, and n being the number of peaks present per the length L. Separately, the present inventors made studies of whether or not an improvement can be attained in the charging and discharging life of the anode for a rechargeable lithium battery by increasing the reactivity of the surface of the anode. That is, there were prepared a plurality of rechargeable lithium batteries by the conventional manner, wherein the anode of each rechargeable lithium battery was formed using an anode active material comprising aluminum as the metal capable of being alloyed with lithium and the resultant anode was subjected to etching treatment to roughen the surface thereof so as to have a different surface roughness in each case, the cathode thereof was formed using a cathode active material comprising lithium nickel oxide, and as the electrolyte solution, there was used an electrolyte solution obtained by dissolving lithium borofluoride in a mixed solvent of EC-DMC (ethylene carbonate-dimethyl carbonate) or PC-DEC (propylene carbonate-diethyl carbonate). As for each of the resultant rechargeable lithium batteries, the charging and discharging cycle life of the rechargeable battery was examined in the same manner as in the above. The examined results obtained are graphically shown in FIG. 3, in relation to values obtained by the equation: the equation: 1 + (4nRa/L), with Ra being a central line average roughness, L being a length measured, and n being the number of peaks present per the length L. Based on the results shown in FIG. 3, there was obtained a finding in that when the surface of the anode is roughened by the etching treatment, not only the reactivity of the anode's surface is increased but also the specific surface area thereof is increased, and as a result, the charging and discharging cycle life is prolonged accordingly. Particularly, as apparent from FIG. 3, it was found that when the surface of the anode is made such that the value obtained by the above equation is 1.05 or more, preferably 1.10 or more, more preferably 1.20 or more, the charging and discharging cycle life of the anode can be extended to be two times or more that of an anode having not subjected to surface roughening treatment. In the present invention, the anode may have a current collecting portion provided with an electrical conductor layer which has a higher coefficient of extension at room temperature than that of the metal capable of forming an alloy with lithium. In the present invention, the cathode active material for the cathode contains lithium. In this case, a deposition of lithium occurs first time when charging is first performed, wherein the lithium thus deposited causes the formation of an alloy with the metal capable of being alloyed with lithium which is contained in the anode. The incorporation of the lithium into the cathode active material provides a pronounced advantage in that it is not necessary to have a lithium alloy in advance prior to assembling a rechargeable lithium battery, the production process of the rechargeable lithium battery can be simplified. In addition to this advantage, there is provided another advantage in that since the lithium contained in the cathode releases therefrom and enters thereinto upon the repetition of the charging and discharging cycle, the cathode is hardly expanded or shrunk when the charging and discharging are repeated, wherein there is no occasion for the cathode active material to be removed, resulting in prolonging the charging and discharging cycle life. In the present invention, it is possible for the surface of the anode to be covered by an insulating film or a semiconductor film having a property of allowing lithium ion to pass through but prohibiting a lithium metal deposited upon the charging to pass through. In this case, the lithium deposited is prevented from directly contacting with the electrolyte solution. And in general, a reaction product produced as a result of the reaction of an active lithium often is liable not to contribute to the charging, but the active lithium is prevented from producing such reaction product. As a result, the charging and discharging cycle life is prolonged. Further, in this case, when the anode is formed of a powdery material, the foregoing surface coat prevents occurrence of a removal at the surface of the anode. In the following, the present invention will be described while referring to FIGs. 4(a) through 4(h). FIGS. 4(a), 4(c)-(e), 4(g) and 4(h) are schematic cross-sectional views respectively for illustrating embodiments of an anode usable in a rechargeable lithium battery. These embodiments are not according to the present invention. The rechargeable lithium battery according to the present invention comprises an anode shown in either of FIGs 4(b) and 4(f), and a cathode and a separator disposed above the anode such that they are opposite to the anode (not shown in the figures). FIG. 4(a) indicates a comparative anode comprising a member 102 constituted by a material containing a metal capable of being alloyed with lithium and a metal layer 101 as a collector portion, comprised of a metal incapable of being alloyed with lithium. In the case of the anode shown in FIG. 4(a), upon operating the charging, lithium ion contained in the electrolyte solution is reacted with the metal capable of being alloyed with lithium contained in the member 102 to cause a deposit in the form of an alloy, wherein the anode is expanded. Then, upon the discharging, lithium ion is released from the member 102 into the electrolyte solution, wherein the anode is shrunk. Due to the expansion and shrinkage occurred upon conducting the charging and discharging cycle, part of the member 102 often suffers from occurrence of a crack resulting in breaking part of the member into fine particles (this situation will be hereinafter referred to as powdering). But problems which will be caused by the powdering can be eliminated by the metal layer 101. That is, the metal layer 101 comprised of the metal incapable of being alloyed with lithium as the collector portion which is disposed next to the member 101 serves not only to prevent the current collecting performance from being reduced but also to prevent the member 102 from releasing its constituent into the electrolyte solution. The anode shown in FIG. 4(b) is a modification of the anode shown in FIG. 4(a) in which a plurality of small metallic materials 106 incapable of being alloyed with lithium are spacedly arranged on the surface of the anode shown in FIG. 4(a). The anode shown in FIG. 4(b) provides, in addition to the advantages provided by the anode shown in FIG. 4(a), a further advantage in that the small metallic materials 106 serve not only to prevent the anode's surface, which is most liable to readily break whereby causing the powdering, from causing a reduction in the current collecting performance in the plane direction but also to prevent the anode's surface from suffering from the powdering. The comparative anode shown in FIG.4(c) comprises a metal layer 101 comprised of a metal incapable of being alloyed with lithium as a current collecting portion and an active layer comprised of a mixture composed of a powdery material 103 containing a metal capable of being alloyed with lithium, an electrically conductive auxiliary 104 and a binding agent 105, wherein said active layer is fixed on the metal layer 101 by means of the binding agent 105. The comparative anode shown in FIG.4(c) provides advantages in that since the member containing the metal capable of being alloyed with lithium is formed using the powdery material, a stress which will be caused due to the expansion and shrinkage occurred upon conducting the charging and discharging cycle is desirably relaxed to prevent the anode from suffering from fatigue failure, and because of this, the charging and discharging cycle life is prolonged; and the area to be contacted with the electrolyte solution is increased to facilitate the reactions upon the charging and discharging to smoothly proceed. The comparative anode shown in FIG.4(d) is a modification of the configuration shown in FIG. 4(c), in which an additional active layer, which is the same as the active layer in the case of the anode shown in FIG. 4(c), is fixed to the remaining side of the metal layer 101 in the configuration shown in FIG. 4(c). In the case of using the anode shown in FIG. 4(d), a separator and a cathode may be arranged on each of the opposite sides of the anode. The comparative anode shown in FIG.4(d) is very effectively usable in the production of a spiral cylindrical type battery or a rectangular battery for the stacked type electrode, wherein there can be attained simplification for the production process, saving for the materials to be used, and an increase in the capacitance per a unit volume. Shown in FIG. 4(e) is a comparative modification of the configuration shown in FIG. 4(a), in which an electrically conductive layer 107 having a high coefficient of extension is interposed between the metal layer 101 as the collector portion and the member 102 of the configuration shown in FIG. 4(a). The anode shown in FIG. 4(e) provides advantages in that when the member 102 constituted by the material containing the metal capable of being alloyed with lithium is expanded and shrunk to suffer from occurrence of a crack of causing the powdering upon conducting the charging and discharging cycle, the electrically conductive layer 107 effectively follows said expansion and shrinkage to prevent the anode from deteriorating in terms of the current collecting performance; and the member 102 is prevented from releasing its constituent into the electrolyte solution. The anode shown in FIG. 4(f) comprises a member 102 constituted by a material containing a metal capable of being alloyed with lithium having a surface provided with a plurality of small metallic materials 106 spacedly arranged at said surface and a rear face provided with a plurality of small metallic materials 106 spacedly arranged at said rear face, and an electrically conductive layer 107 having a high coefficient of extension which is disposed so as to cover the rear face of the member 102, wherein the rear face of the member 102, which is provided with said plurality of small metallic materials 106, serves as collector portion. The anode shown in FIG. 4(f) provides advantages in that when the member 102 is expanded and shrunk to suffer from occurrence of a crack of causing the powdering upon conducting the charging and discharging cyle, the electrically conductive layer 107 effectively follows said expansion and shrinkage to prevent the anode from deteriorating in terms of the current collecting performance; and the member 102 is prevented from releasing its constituent into the electrolyte solution. Shown in FIG. 4(g) is a comparative modification of the configuration shown in FIG. 4(a), in which an electrically conductive layer 107 having a high coefficient of extension is disposed so as to cover the remaining face of the metal layer 101 as the collector portion of the configuration shown in FIG. 4(a). The anode shown in FIG. 4(g) provides advantages in that the current collecting performance of the metal layer 101 is effectively prevented from being deteriorated and the member 102 is prevented from releasing its constituent into the electrolyte solution. The comparative anode shown in FIG. 4(h) comprises an alloy 108 comprised of (a) a metal capable of being alloyed with lithium and (b) a metal incapable of being alloyed with lithium. The anode shown in FIG. 4(h) provides advantages in that it is possible for the metal (b) to be uniformly dispersed in the anode so that the anode always exhibits a desirable current collecting performance and there is no occasion for the anode to suffer from occurrence of a crack of causing the powdering. As for the alloy for the anode shown in FIG. 4(h), it is desired to contain the metal (a) in an amount of 50 wt.% or more in order to attain a sufficient utilization efficiency for lithium. Further, as for the alloy for the anode shown in FIG. 4(h), when the metal (a) and the metal (b) are different from each other in terms of the etching rate, selective etching can be conducted for the alloy, wherein by removing a part of either the metal (a) or the metal (b) by the selective etching, there can be attained a remarkably high specific surface area for the cathode. Using either of the anodes shown in FIGs.4(b) and 4(f), an appropriate cathode, an appropriate separator, and an appropriate electrolyte solution, there can be produced a rechargeable lithium battery according to the present invention, having such a configuration as shown in FIG. 5. In FIG. 5, reference numeral 202 indicates an anode comprising a collector portion 200 comprised of a metallic material incapable of being alloyed with lithium and a layer 201 comprised of a material containing a metal capable of being alloyed principally with lithium, reference numeral 203 a cathode, reference numeral 204 an electrolyte solution, reference numeral 205 a separator, reference numeral 206 an anode terminal, reference numeral 207 a cathode terminal, and reference numeral 208 a cell jacket. In this configuration, the anode 202 comprises either of the anodes shown in FIGs.4(b) and 4(f). As apparent from the foregoing description, the rechargeable lithium battery according to the present invention is provided with a specific anode comprising a specific member comprised of a material containing a metal capable of being alloyed with lithium and a specific collector portion comprised of a metallic material incapable of being alloyed with lithium, and because of this, the rechargeable lithium battery according to the present invention has pronounced advantages in that a desirable current collecting performance is always stably exhibited without the collector portion being deteriorated even when charging and discharging are alternately repeated over a long period of time, wherein the charging voltage upon the constant-current charging is effectively prevented from raising, a dendrite of lithium is effectively prevented from generating at the anode, and the charging and discharging cycle life of the anode is remarkably prolonged. In the following, description will be made of the rechargeable lithium battery according to the present invention and the production thereof. ANODE The anode disposed in a rechargeable lithium battery according to the present invention comprises at least a member comprised of a material containing a metal capable of being alloyed with lithium and a collector portion having a metal incapable of being alloyed with lithium, wherein an anode outputting terminal, is extended from said collector portion. In the present invention, the anode may take either of the configurations shown in FIGs. 4(b) and 4(f). Specifically, in a typical embodiment, the anode comprises a metallic material capable of being alloyed with lithium arranged on a plate-like or foil-like material containing a metal incapable of being alloyed with lithium which is capable of serving as an anode collector portion. In another typical embodiment, the anode comprises a layer formed of a powdery material containing a metal capable of being alloyed with lithium which is disposed on a metallic material incapable of being alloyed with lithium which is capable of serving as an anode collector portion. Any of these two anodes may be provided with a plurality of small metallic materials incapable of being alloyed with lithium such that they are spacedly arranged on the surface of the anode which is opposed to the cathode, in order to attain an improved current collecting performance. Alternatively, in any of the above two typical embodiments, either the metallic material capable of being alloyed with lithium or the layer formed of a powdery material containing a metal capable of being alloyed with lithium may be replaced by an alloy composed of a metal capable of being alloyed with lithium and a metal incapable of being alloyed with lithium. Further, the anode may be provided with a layer composed of an electrically conductive material, which exhibits a coefficient of extension which is greater than that of the metal capable of being alloyed with lithium at room temperature, such that said electrically conductive layer covers the collector portion, in order to prevent the anode from suffering from fatigue failure due to the expansion and shrinkage occurred when the charging and discharging are alternatively repeated. Description will be made of a manner of arranging a metallic material incapable of being alloyed with lithium (hereinafter referred to as arranging metal material) on an anode constituting member comprised of a metal capable of being alloyed with lithium (hereinafter referred to as anode base member). To arrange the arranging metal material either on a face of the anode base member to be situated to oppose the cathode or on a face thereof to be a collector portion may be conducted in the following manner. In the case where the metal capable of being alloyed with lithium (this metal will be hereinafter referred to as alloyable metal for the simplification purpose) has an ionization tendency which is higher than that of the metal incapable of being alloyed with lithium (this metal will be hereinafter referred to as non-alloyable metal for the simplification purpose), a member comprised of the alloyable metal is immersed in a solution of a salt of the non-alloyable metal. By this, part of the alloyable metal constituting said member can be substituted by the non-alloyable metal. The substituting amount may be controlled as desired by properly adjusting the time during which the member is immersed in the above solution, the content of the metal salt in the solution, or the temperature of the solution. Particularly, as the time during which the member is immersed in the above solution is prolonged, the substituting amount is increased accordingly. Similarly, as the content of the metal salt in the solution is increased or the temperature of the solution is heightened, the substituting amount is increased. Alternatively, to arrange the arranging metal material either a face of the anode base member to be situated to oppose the cathode or a face thereof to be a collector portion may be conducted by means of electro plating, non-electro (or chemical) plating, laser plating, sputtering, resistance heating evaporation, electron beam evaporation, cluster-ion beam evaporation, thermal-induced CVD, low pressure CVD, plasma CVD, or laser CVD, wherein a layer of the non-alloyable metal is deposited on the anode base member. Other than these, it may employ a manner of applying an ink or paste containing the non-alloyable metal on the anode base member by means of the screen printing process. Other than the above manners, it is possible to employ the following manner. That is, a member comprised of the non-alloyable metal capable of serving as an anode collector portion is provided, and on this member, a layer comprised of the alloyable metal is formed by means of sputtering, resistance heating evaporation, electron beam evaporation, cluster-ion beam evaporation, thermal-induced CVD, low pressure CVD, plasma CVD, or a coating process such as screen printing process. The member comprised of the non-alloyable metal in this case may be shaped in a plate-like form, foil-like form, punching metal form, expanded metal form, or mesh form. The group of the alloyable metals (that is, the metal capable of being alloyed with lithium) consists of Al, Mg, K, Na, Ca, Sr, Ba, Si, Ge, Sb, Pb, In, and Zn. Of these, Al, Mg, Ca and Pb are most appropriate. The group of the non-alloyable metals (that is, the metal incapable of being alloyed with lithium) consists of Ni, Ti, Cu, Ag, Au, Pt, Fe, Co, Cr, W, and Mo. Of these, Ni, Ti, Cu, Pt, and Fe are most appropriate. In order for the member comprised of the non-alloyable metal to function as the anode collector, it is a matter of course that the member may contain one of these metals. Alternatively, the member may comprise an alloy of two or more of these metals. Further, the member may comprise stainless steel. Description will be made of the anode having a layer formed of a powdery material containing the alloyable metal. The formation of the layer comprised of a powdery material containing the alloyable metal (that is, the metal capable of being alloyed with lithium) on the member comprised of the non-alloyable metal (that is, the metal incapable of being alloyed with lithium) serving as the collector portion (hereinafter referred to as collector member) may be conducted, for example, in the following manner. That is, a powdery material containing the alloyable metal or a powdery material of an alloy composed of the alloyable metal (that is, the metal capable of being alloyed with lithium) and the non-alloyable metal (that is, the metal incapable of being alloyed with lithium) is firstly provided. Any of these powdery materials is well mixed with a resin or a low fusion point glass as a binding agent. The resultant is well mixed with an organic solvent to obtain a paste having a predetermined viscosity. The paste thus obtained is applied on the collector member, followed by subjecting to drying or sintering treatment. The resin (that is, the binder resin) is desired to be a resin which is stable for the electrolyte solution. Specific examples of such binder resin are polytetrafluoroethylene, polyvinylidene fluoride, polyethylene, polypropylene, ethylene-propylene copolymer, ethylene-propylene-diethane polymer, and silicone resin. Other than these, polymers capable of being highly crosslinked are also usable. In the case where these binder resins are selectively used as the binding agent, there is a tendency that the current collecting performance is gradually decreased as the charging and discharging are alternately repeated, although the active material is slightly released. In order to prevent occurrence of this problem, it is desired to incorporate an appropriate electrically conductive auxiliary into any of the foregoing powdery materials. By this, an improvement can attained for the powdery material layer. Such electrically conductive auxiliary can include carbon blacks such as ketjen black (trademark name) and acetylene black, and graphite in a powdery form. Of these, graphite is the most appropriate. Particularly in the case where flake-like graphite having a form of being large in the direction parallel to the crystal plane and being small in the direction perpendicular to the crystal plane and having a bulk density of 0.1 or less is used as the electrically conductive auxiliary, pronounced advantages are provided in that because the flake-like graphite is high in electrical conductivity, an improved current collecting performance is attained while providing an improvement in the retention of the electrolyte solution, and a reduction is attained for the anode comprised of the powdery material in terms of the impedance. As for the foregoing collector member, it is necessary for the surface thereof to be composed of an electrically conductive material comprised of the non-alloyable metal. The collector member may be shaped in a plate-like form, foil-like form, mesh form, porous form-like sponge form, punching metal form, or expanded metal form. Specific examples of the non-alloyable metal (that is, the metal incapable of being alloyed with lithium) by which the collector member is constituted are Ni, Ti, Cu, Ag, Au, Pt, Fe, or stainless steel. Description will be made of the electrically conductive layer having a high coefficient of extension. The electrically conductive layer having a high coefficient of extension may be formed by means of sputtering, resistance heating evaporation, electron beam evaporation, cluster-ion beam evaporation, thermal-induced CVD, low pressure CVD, plasma CVD, laser CVD, electro plating, non-electro (or chemical) plating, or laser plating. Other than these, it may employ a manner of applying an ink containing a given electrically conductive material having a high coefficient of extension by means of the screen printing process. The electrically conductive layer having a high coefficient of extension may be formed of a metal or alloy such as Sn, Sn-Bi alloy, Sn-Pb alloy, Zn-Al alloy, Cu-Zn alloy, or Cd-Zn alloy. If necessary, the electrically conductive layer may be formed of a metal or alloy selected from Au, Ag, Al, and alloys of these metals. Further, the electrically conductive layer may be formed of an electrically conductive ink comprising a mixture of fine particles of an electrically conductive material and an organic polymer material as a binding agent. In this case, the electrically conductive layer is usually formed by means of the screen printing process. The above organic polymer material contained in the electrically conductive ink can include fluorine-containing resin, polyolefin, silicone resin, and other polymers capable of being highly crosslinked. In a preferred embodiment, the above organic polymer material as the binding agent is desired to be such that the glass transition temperature thereof is less that the lowest temperature of the temperature range practically used, specifically, it is - 30 °C or less for example. Description will be made of the case where the surface of the anode is made to have an increased surface area by subjecting the surface of the anode to etching treatment. As above described, the anode comprising a member comprised of a material containing the alloyable metal (that is, the metal capable of being alloyed with lithium) and a collector member comprised of the non-alloyable metal (that is, the metal incapable of being alloyed with lithium) according to the present invention can be made to have an increased surface area by subjecting the surface of the anode to etching treatment. The etching treatment in this case may be conducted by way of chemical etching, electrochemical etching, or plasma etching. The chemical etching is conducted in a manner wherein the surface of an object is etched by reacting it with an etching solution of an acid or alkali. As the acid usable for etching a member comprised of Al as the alloyable metal (that is, the metal capable of being alloyed with lithium), there can be mentioned phosphoric acid, sulfuric acid, hydrochloric acid, nitric acid, acetic acid, hydrofluoric acid and mixtures of two or more of these. Similarly, as the alkali, there can be mentioned potassium hydroxide, sodium hydroxide, lithium hydroxide, and mixtures of two or more of these. As the etching solution usable for etching a member comprised of Mg as the alloyable metal, there can be mentioned solutions of one or more acids selected from nitric acid, sulfuric acid and hydrochloric acid. Other than these, solutions of ammonium salts of these acids are also usable. As the etching solution usable for etching a member comprised of Ni as the non-alloyable metal (that is, the metal incapable of being alloyed with lithium), there can be mentioned solutions of dilute acids such as nitric acid. As the etching solution usable for etching a member comprised of Cu as the non-alloyable metal, there can be mentioned solutions of one or more acids selected from sulfuric acid, hydrochloric acid, nitric acid and acetic acid. Other than these, a solution of cupric chloride or ferric chloride and aqueous ammonia are also usable. As the etching solution usable for etching a member comprised of Ti as the non-alloyable metal, there can be mentioned solutions of one or more acids selected from hydrofluoric acid and phosphoric acid. In any case wherein the chemical etching is conducted, it is desired to selectively use an appropriate etching solution having a selectively etching property such that that the etching rate for the alloyable metal (the metal capable of being alloyed with lithium) is different from that for the non-alloyable metal (the metal incapable of being alloyed with lithium). The electrochemical etching is conducted in a manner wherein an electric field is applied between an object to be treated and a counter electrode in an electrolyte solution to electrochemically release metal ions from the object into the electrolyte solution. As the electrolyte solution usable for electrochemically etching an Al-member, there can be used a solution of phosphoric acid, sulfuric acid or chromic acid. Other than these, solutions of mixtures of these acids are also usable. As the electrolyte solution usable for electrochemically etching a Cu-member, there can be used a solution of phosphoric acid. The plasma etching is conducted in a manner wherein a plasma is generated from an etching gas to produce a reactive ions or radicals, wherein an object to be treated is reacted with said reactive ions or radicals whereby etching said object. As the etching gas usable, there can be mentioned tetrachloromethane, tetrafluoromethane, chlorine gas, trichloromonofluoromethane, dichlorodifluoromethane, and chlorotrifluoromethane. Description will be made of the surface coating for the anode in the present invention. As previously described, in the present invention, it is possible for the surface of the anode to be covered by an insulating film or a semiconductor film having a property of allowing lithium ion to pass through but prohibiting a lithium metal deposited upon the charging to pass through. In this case, there are provided advantages such that lithium deposited is prevented from directly contacting with the electrolyte solution, active lithium is prevented from reacting to produce such a reaction product of not contributing to the charging, and as a result, the charging and discharging cycle life is prolonged. Further, in this case, when the anode is formed of a powdery material, the foregoing surface coat prevents occurrence of a removal at the surface of the anode. As the material by which the surface of the anode is coated, there is used a material having a porous structure or a molecular structure capable of allowing lithium ion to pass through. As the material having such molecular structure, there can be mentioned high-molecular compounds such as large-ring ether structure-bearing compounds, cupulate cyclic compounds having a plurality of phenol units, and ether bond-bearing high-molecular compounds. As for the material having such porous structure, it can be formed by a manner wherein an appropriate material such as an electrolyte salt or the like capable of being eluted after the formation of a coating film is contained in a coating liquid to be applied or a manner wherein a foaming agent or a material capable of being readily thermally decomposed is contained in a coating liquid to be applied. Description will be made of the anode terminal in the present invention. As previously described, the anode terminal for outputting or inputting a power is extended from the collector portion of the anode. The formation of the anode terminal may be conducted by a manner of electrically connecting an electrically conductive material to the collector portion by means of laser welding, spot welding or solder jointing. In the case where a collector portion is interposed between two members, it is desired to previously form an outputting portion capable of being electrically connected to a power outputting or inputting terminal at the collector portion. CATHODE The cathode is constituted by a cathode collector, a cathode active material containing lithium, an electrically conductive auxiliary, and a binding agent. Particularly, the cathode is formed by disposing a mixture of a cathode active material, an electrically conductive auxiliary and a binding agent on a member capable of serving as a cathode collector. The electrically conductive auxiliary can include carbon blacks such as ketjen black (trademark name) and acetylene black, and graphite in a powdery form or a fibrous form. The binding agent is desired to be stable for the electrolyte solution. Specific examples of such binding agent are polytetrafluoroethylene, polyvinylidene fluoride, polyethylene, polypropylene, ethylene-propylene copolymer, and ethylene-propylene-diethane polymer. The cathode collector serves to supply an electric current so that said electric current can be efficiently consumed for the electrode reaction upon conducting the charging and discharging cycle or it serves to collect an electric current generated. The cathode collector is therefore desired to be constituted by a material which has a high electrical conductivity and is inactive to the battery reaction. The material by which the cathode collector is constituted can include Ni, Ti, Cu, Al, Pt, V, Au, Zn, alloys of two or more of these metals such stainless steel and the like. The cathode collector member may be shaped in a plate-like form, foil-like form, mesh form, porous form-like sponge form, punching metal form, or expanded metal form. As a cathode active material which is to contain lithium, there is usually used a compound selected from the group consisting of transition metal oxides and transition metal sulfides. The metals of these transition metal oxides and transition metal sulfides can include metals partially having a d-shell or f-shell. Specific examples of such metal are Sc, Y, lanthanoids, actinoids, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Tc, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag and Au. Of these, Ti, V, Cr, Mn, Fe, Co, Ni and Cu are most appropriate. The cathode active material is desired to be comprised of any of the above transition metal oxides and transition metal sulfides which is incorporated with lithium. Since a lithium-containing cathode active material is used, there is provided an advantage in that it is not necessary to prepare a lithium-containing anode in advance and because of this, the battery production process can be simplified. The lithium-containing cathode active material may be prepared by a manner of obtaining a transition metal oxide or transition metal sulfide using lithium hydroxide or lithium salt. Alternatively, it may be prepared by a manner of providing a mixture of a given transition metal oxide or transition metal sulfide and lithium hydroxide, lithium nitrate, or lithium carbonate capable of being readily thermally decomposed and subjecting said mixture to heat treatment. SEPARATOR The separator is disposed between the anode and cathode, and it serves to prevent the cathode and anode from suffering from occurrence of internal-shorts between them. In addition, the separator also serves to retain the electrolyte solution. The separator is required to have a porous structure capable of allowing lithium ion to pass therethrough and it is also required to be insoluble into and stable to the electrolyte solution. The separator is usually constituted by a nonwoven fabric or a membrane having a micropore structure made of glass, polypropylene, polyethylene, fluorine-containing resin, or polyamide. Alternatively, the separator may be constituted by a metal oxide film or a resin film combined with a metal oxide, respectively having a plurality of pores. In a preferred embodiment, the separator is constituted by a multilayered metal oxide film. In this case, the separator effectively prevent a dendrite from passing therethrough and because of this, occurrence of internal-shorts between the cathode and anode is desirably prevented. In another preferred embodiment, the separator is constituted by an incombustible fluorine-containing resin, glass or metal oxide film. In this case, an improvement can be attained in terms of the safety. ELECTROLYTE In the present invention, there can be used an appropriate electrolyte as it is, a solution of said electrolyte dissolved in a solvent, or a material of said solution having immobilized using a gelatinizing agent. However, an electrolyte solution obtained by dissolving an appropriate electrolyte in an solvent is usually used in a way that said electrolyte solution is retained on the separator. The higher the electrical conductivity of the electrolyte, the better. Particularly, it is desired to use such an electrolyte or an electrolyte solution that the electrical conductivity at 25 °C is preferably 1 x 10 -3 S/cm or more or more preferably, 5 x 10 -3 S/cm or more. The electrolyte usable in the present invention can include inorganic acids such as H 2 SO 4 , HCl and HNO 3 ; salts of Li + (lithium ion) with Lewis acid ion such as BF 4 - , PF 6 - , ClO 4 - , CF 3 SO 3 - , or BPh 4 - (with Ph being a phenyl group); and mixtures of two or more of said salts. Other than these supporting electrolytes, salts of the above described Lewis acids ions with cations such as sodium ion, potassium ion, tetraalkylammonium ion, or the like are also usable. In any case, it is desired that the above salts are used after they are subjected to dehydration or deoxygenation, for example, by way of heat treatment under reduced pressure. The solvent in which the electrolyte is dissolved can include acetonitrile, benzonitrile, propylene carbonate, ethylene carbonate, dimethyl carbonate, diethyl carbonate, demethylformamide, tetrahydrofuran, nitrobenzene, dichloroethane, diethoxyethane, 1,2-dimethoxyethane, chlorobenzene, γ-butyrolactone, dioxolan, sulfolan, nitromethane, dimethyl sulfide, dimethyl oxide, methyl formate, 3-methyl-2-oxazolydinone, 2-methyltetrahydrofuran, 3-propylsydnone, sulfur dioxide, phosphoryl chloride, thionyl chloride, sulfulyl chloride, and mixtures of two or more of these. As for these solvents, it is desired for them to be subjected to dehydration using activated alumina, molecular sieve, phosphorus pentaoxide, or calcium chloride, prior to their use. Alternatively, it is possible for them to be subjected to distillation in an atmosphere composed of inert gas in the presence of an alkali metal, wherein moisture and foreign matters are removed. In order to prevent leakage of the electrolyte, it is desired for the electrolyte to be gelatinized using an appropriate gelatinizing agent. The gelatinizing agent usable in this case can include polymers having a property such that it absorbs the solvent of the electrolyte solution to swell. Specific examples of such polymer are polyethylene oxide, polyvinyl alcohol, and polyacrylamide. SHAPE AND STRUCTURE OF SECONDARY LITHIUM CELL There is no particular limitation for the shape of the rechargeable lithium battery according to the present invention. The rechargeable lithium battery according to the present invention may be in the form of a flat round shape (or a coin-like shape), a cylindrical shape, a prismatic shape, or a sheet-like shape. In the case where the rechargeable lithium battery is shaped in a spiral-wound cylindrical form, the anode, separator and cathode are arranged in the named order and they are spriral-wound. By this, there are provided advantages such that the battery area can be increased as desired and a high electric current can be flown upon conducting the charging and discharging cycle. In the case where the rechargeable lithium battery is shaped in a prismatic form, there is provided an advantage in that the space of a device for housing the rechargeable lithium battery can be effectively utilized. As for the structure of the rechargeable lithium battery according to the present invention, it can optionally made to be of a single layer structure or a stacked structure. FIG. 6 is a schematic cross-sectional view illustrating an example of a single-layer structure type flat rechargeable lithium battery according to the present invention. FIG. 7 is a schematic cross-sectional view illustrating an example of a spiral-wound cylindrical rechargeable lithium battery according to the present invention. In FIGs. 6 and 7, each of reference numerals 300 and 400 indicates an anode collector, each of reference numerals 301 and 401 an anode, each of reference numerals 303 and 403 a cathode, each of reference numerals 305 and 405 an anode terminal (or an anode cap), each of reference numerals 306 and 406 a cathode can, each of reference numerals 307 and 407 a separator and an electrolyte, each of reference numerals 310 and 410 an insulating packing, and reference numeral 411 an insulating plate. The fabrication of a rechargeable battery of the configuration shown in FIG. 6 or FIG. 7 is conducted, for example, in the following manner. That is, a combination comprising the separator (307, 407) interposed between the anode (301, 401) and the cathode (303, 403) is positioned in the cathode can (306, 406). Thereafter, the electrolyte is introduced thereinto. The resultant is assembled with the anode cap (305, 405) and the insulating packing (310, 410), followed by subjecting to caulking treatment. Thus, there is obtained the rechargeable battery. The preparation of the constituent materials for the rechargeable battery and the fabrication of the rechargeable battery are desired to be conducted in a dry air atmosphere free of moisture or a dry inert gas atmosphere free of moisture. As the constituent of the insulating packing (310, 410), there can be used fluorine-containing resin, polyamide resin, polysulfone resin, or various rubbers. The sealing is typically conducted using a gasket such as the insulating packing, as shown in FIGs. 6 and 7. Other than this, it can be conducted by means of glass sealing, adhesive sealing, welding or soldering. As the constituent of the insulating plate 411 shown in FIG. 7, there can be used organic resins and ceramics. Any of the cathode can (306, 406) and the anode cap (305, 405) can be constituted by stainless steel, titanium clad steel, copper clad steel, or nickel-plated steel. In any of the configurations shown in FIGs. 6 and 7, the cathode can (306, 406) is designed to serve also as a battery casing. In the case where a battery casing is independently used, the battery casing can be constituted by a metal such as zinc, an alloy such as stainless steel, a plastic such as polypropylene, or a composite of a metal or glass fiber with plastic. Although this is not shown in any of FIGs. 6 and 7, but it is possible to employ an appropriate safety valve in any of the configurations shown in FIGs. 6 and 7. In the following, the present invention will be described in more detail with reference to examples, which are only for illustrative purposes but not intended to restrict the scope of the present invention to these examples. Reference Example 1 There was prepared a rechargeable lithium battery of the configuration shown in FIG. 6 in the following manner. Formation of anode: There was firstly provided a foil composed of a Ti-Al alloy containing the Ti in an amount of 50% and the Al in an amount of 50% (the Ti belonging to the metal incapable of being alloyed with lithium). The Ti-Al alloy was subjected to surface polishing treatment to obtain a 50 um thick Ti-Al alloy foil having a ground surface. The Ti-Al alloy foil was then immersed in a 5% potassium hydroxide aqueous solution for 5 minutes, wherein the surface of the Ti-Al alloy foil was etched. The Ti-Al alloy foil thus treated was washed with pure water, followed by drying. Thus, there was obtained an anode. In the above, as for the surface of the Ti-Al alloy foil to be opposed to a cathode, its surface roughness measured by the tracer method was adjusted to be 0.6 µm or less in central line average roughness and 3.8 µm or less in maximum height Rmax through the surface polishing treatment and the etching treatment, wherein the number of roughened peaks for the measured length L of 80 µm was 7. Formation of cathode: Electrolytic manganese dioxide was mixed with lithium carbonate with a mixing ratio of 1 : 0.4, followed by subjecting heat treatment at 800 °C, to there by obtain a lithium-manganese oxide. With the resultant lithium-manganese oxide, 3 wt.% of powdery acetylene black and 5 wt.% of powdery polyvinylidene fluoride were mixed. The resultant was mixed with N-methyl-2-pyrrolidone to obtain a paste-like product. The resultant paste-like product was applied onto the surface of an aluminum foil, followed by subjecting to drying. Thus, there was obtained a cathode. Preparation of electrolyte solution: There was provided a moisture-free mixed solvent composed of ethylene carbonate (EC) and methoxy carbonate (DMC) with an equivalent mixing ratio. 1 M (mol/l) of tetrafluoro lithium borate was dissolved in the mixed solvent. Thus, there was obtained an electrolyte solution. Formation of separator: A nonwoven fabric made of polypropylene, a polypropylene membrane film provided with a number of small pores, and another nonwoven fabric made of polypropylene were laminated in the named order to obtain a composite having a thickness of 50 µm. Thus, there was obtained a separator. Fabrication of rechargeable lithium battery: The fabrication of a rechargeable lithium battery was conducted in a dry argon atmosphere. The separator was interposed between the cathode and the anode, and the resultant was inserted into a cathode can made of titanium clad steel. Then, the electrolyte solution was injected into the cathode can. The resultant was sealed using an anode cap made of titanium clad steel and an insulating packing made of fluoro rubber. Thus, there was obtained a rechargeable lithium battery. Example 2 There was prepared a rechargeable lithium battery of the configuration shown in FIG. 6 in the same manner as in Example 1, except that the anode was formed in the following manner, and as the separator a 25 µm thick polypropylene membrane film provided with a number of small pores was used. The anode was formed in the following manner. That is, there was firstly provided a 30 µm thick aluminum foil. The aluminum foil was immersed in a 5 % potassium hydroxide aqueous solution for 5 minutes, wherein the surface of the aluminum foil was etched. The aluminum foil thus treated was washed with pure water, followed by drying. The resultant aluminum foil was then immersed in a 20% nickel chloride aqueous solution maintained at 50 °C for 5 minutes, whereby the opposite surfaces of the aluminum foil were partially substituted by nickel (belonging to the metal incapable of being alloyed with lithium). The aluminum foil thus treated was washed with pure water, followed by subjecting to vacuum drying at 150 °C. In this case, as for the surface of the aluminum foil to be opposed to the cathode, its surface roughness measured by the tracer method was adjusted to be 0.4 µm or less in central line average roughness and 2.0 µm or less in maximum height Rmax, wherein the number of roughened peaks for the measured length L of 80 µm was 8. Example 3 There was prepared a rechargeable lithium battery of the configuration shown in FIG. 6 in the same manner as in Example 2, except that the treated face of the aluminum foil on the current collecting side was applied with an electrically conductive ink obtained by fine particles of Ag were dispersed in an epoxy resin of - 30 °C in glass transition temperature by means of the screen printing process, followed by subjecting to heat treatment at 150 °C and under reduced pressure condition to crosslink and harden, whereby forming an electrically conductive layer on said face. Example 4 There was prepared a rechargeable lithium battery of the configuration shown in FIG. 6 in the same manner as in Example 1, except that the anode was formed in the following manner. That is, there was firstly provided a 30 um thick aluminum foil having a ground surface. The aluminum foil was immersed in a 5 % hydrofluoric acid aqueous solution for 5 minutes, wherein the surface of the aluminum foil was etched. The aluminum foil thus treated was washed with pure water, followed by drying. The resultant aluminum foil was then immersed in an aqueous solution containing copper sulfate and sulfuric acid, wherein the opposite surfaces of the aluminum foil were copper-plated at a thickness of 50 nm (the copper belonging to the metal incapable of being alloyed with lithium). The aluminum foil thus treated was washed with pure water, followed by subjecting to vacuum drying at 150 °C. Then, the surface of the aluminum foil on the current collecting side was deposited with a Sn-Bi alloy at a thickness of 500 nm by means of the sputtering process to thereby form an electrically conductive layer. Thus, there was obtained an anode. In this case, as for the surface of the aluminum foil to be opposed to the cathode, its surface roughness measured by the tracer method was adjusted to be 0.3 µm or less in central line average roughness and 1.7 µm or less in maximum height Rmax through the surface polishing treatment and the etching treatment, wherein the number of roughened peaks for the measured length L of 80 µm was 8. Example 5 There was prepared a rechargeable lithium battery of the configuration shown in FIG. 6 in the same manner as in Example 1, except that the anode was formed in the following manner. That is, powdery aluminum of 300 mesh in mean particle size, ultra fine powdery nickel of less than 0.1 in mean particle size, and methyl cellulose as a binding agent were mixed with a weight mixing ratio of 90 : 5 : 5. The resultant mixture was mixed with xylene to obtain a paste-like product. The resultant paste-like product was applied on the surface of a nickel-plated iron punching metal foil of 35 um in thickness. The thickness of the coat formed on the surface of the foil was made to be uniform by means of a roll press machine, followed by subjecting to drying at 100 °C. The resultant was subjected to sintering treatment at 700 °C under reduced pressure condition. Thereafter, the resultant obtained was immersed in a 20% nickel chloride aqueous solution maintained at 50 °C for 5 minutes, wherein the powdery aluminum of the coat formed on the foil was partially substituted by nickel, followed by subjecting to washing with pure water, then followed by subjecting to vacuum drying at 150 °C, to thereby obtain a 60 µm thick anode. Example 6 There was prepared a rechargeable lithium battery of the configuration shown in FIG. 6 in the same manner as in Example 1, except that the anode was formed in the following manner. That is, powdery Ni-Al alloy (with a mixing rate of 40% : 60%) having a mean particle size of 250 mesh and methyl cellulose as a binding agent were mixed with a weight mixing ratio of 90 : 10. The resultant mixture was mixed with xylene to obtain a paste-like product. The resultant paste-like product was applied on the surface of an expanded nickel metal foil of 35 µm in thickness. The thickness of the coat formed on the surface of the foil was made to be uniform by means of a roll press machine, followed by subjecting to drying at 100 °C. The resultant was subjected to sintering treatment at 700 °C under reduced pressure. Thereafter, the resultant obtained was-immersed in a 5% potassium hydroxide aqueous solution for 5 minutes, wherein the surface of the coat formed on the foil was etched, followed by subjecting to washing with pure water, then followed by subjecting to vacuum drying at 150 °C, to thereby obtain a 50 µm thick anode. Comparative Example 1 There was prepared a rechargeable lithium battery of the configuration shown in FIG. 6 in the same manner as in Example 1, except that the anode was replaced by a conventional aluminum foil of 30 µm in thickness. As for the surface of the aluminum foil to be opposed to the cathode, its surface roughness measured by the tracer method was found to be 0.15 µm or less in central line average roughness and 0.7 µm or less in maximum height Rmax, wherein the number of roughened peaks for the measured length L of 80 µm was found to be 6. Comparative Example 2 There was prepared a rechargeable lithium battery of the configuration shown in FIG. 6 in the same manner as in Example 1, except that the anode was replaced by a 100 µm thick aluminum foil having an etched surface (produced by Nihon Chikudenki Kogyo Kabushiki Kaisha). Comparative Example 3 There was prepared a rechargeable lithium battery of the configuration shown in FIG. 6 in the same manner as in Example 1, except that the anode was formed in the following manner. That is, powdery graphite obtained by subjecting natural powdery graphite to heat treatment in an argon gas atmosphere at 2000 °C, acetylene black, and powdery polyvinylidene fluoride were mixed with a weight mixing ratio of 82 : 3 : 5. The resultant mixture was mixed with N-methyl-2-pyrrolidone to obtain a paste-like product. The resultant paste-like product was applied on the surface of a copper foil of 35 µm in thickness. The thickness of the coat formed on the surface of the foil was made to be uniform by means of a roll press machine, followed by subjecting to drying at 150 °C under reduced pressure. Thus, there was obtained a 110 µm thick anode. Evaluation As for each of the rechargeable lithium batteries obtained in the above Examples 1 to 6 and the above Comparative Examples 1 to 3, evaluation was conducted with respect to battery characteristics through the charging and discharging cycle test. The charging and discharging cycle test was conducted in the following manner. That is, each rechargeable lithium battery was placed in a charging and discharging device HJ-106M (produced by Hokuto Denko Kabushiki Kaisha), wherein charging and discharging were alternately repeated under conditions of 0.5 C (electric current of 0.5 time the electric capacity per an hour based on the electric capacity calculated from the anode active material of each rechargeable lithium battery) for the charging and discharging, 4.5 V for the cut-off voltage upon the charging, 30 minutes for the rest, and 2.5 V for the cut-off voltage upon the discharging. The cut-off voltage upon the charging was determined so as to prevent the solvent of the electrolyte solution from decomposing. The charging and discharging cycle test was initiated by operating the charging. In the charging and discharging test, as for each rechargeable lithium battery, there were observed its battery capacity (that is, an energy density, namely, a discharge energy density) per a unit volume of the rechargeable lithium battery) and its charging and discharging cycle life. The battery capacity was based on the service capacity after the third repetition of the charging and discharging cycle. And the charging and discharging cycle life was based on the number of the charging and discharging cycle having been repeated until the charge voltage became 4.5 V. The observed results obtained are collectively-shown in Table 1. In Table 1, the values with respect to the energy density as for the rechargeable lithium batteries obtained in Examples 1 to 6 and Comparative Examples 2 and 3 are relative values to the energy density of the rechargeable lithium battery obtained in Comparative Example 1, which is set at 1.0. Similarly, the values with respect to the cycle life as for the rechargeable lithium batteries obtained in Examples 1 to 6 and Comparative Examples 2 and 3 are relative values to the cycle life of the rechargeable lithium battery obtained in Comparative Example 1, which is set at 1.0. Based on the results shown in Table 1, there were obtained the following facts. That is, the rechargeable lithium batteries obtained in Examples 1 to 6 belonging to the present invention surpass the rechargeable lithium batteries obtained in Comparative Examples 1 to 3 in terms of the total battery characteristics. Particularly, as for the energy density, the rechargeable lithium batteries obtained in Examples 1 to 6 are apparently superior to the rechargeable lithium batteries obtained in Comparative Examples 1 to 3. As for the charging and discharging cycle life, the rechargeable lithium batteries obtained in Examples 1 to 6 are apparently superior to the rechargeable lithium batteries obtained in Comparative Examples 1 and 2, although the rechargeable lithium batteries obtained in Examples 1 to 6 are similar to the rechargeable lithium battery obtained in Comparative Example 3 which is, however, apparently inferior in terms of the energy density. discharge energy density charging and discharging cycle life the rechargeable lithium battery in Reference Example 1 1.4 2.9 the rechargeable lithium battery in Example 2 1.6 3.2 the rechargeable lithium battery in Example 3 1.5 3.7 the rechargeable lithium battery in Example 4 1.6 3.5 the rechargeable lithium battery in Example 5 1.4 3.6 the rechargeable lithium battery in Example 6 1.4 3.4 the rechargeable lithium battery in Comparative Example 1 1.0 1.0 the rechargeable lithium battery in Comparative Example 2 1.1 1.3 the rechargeable lithium battery in Comparative Example 3 1.0 4.2

Claims: A rechargeable lithium battery, in an as prepared state prior to being subjected to first charging, comprising at least an anode (202), a separator (205), a cathode (203), an electrolyte (204) or an electrolyte solution, an anode terminal (206) electrically connected to said anode (202), said anode (202) and said cathode (203) being electrically contacted with said electrolyte (204) or electrolyte solution; wherein said anode (202) comprises (a) a collector (101, 200) and (b) a layer (102, 201) in contact with said collector, said collector (101,200) comprising metal incapable of being alloyed with lithium upon charging, comprising one or more metals selected from the group consisting of Ni, Ti, Cu, Ag, Au, Pt, Fe, Co, Cr, W and Mo; said anode (202) has a surface region in said layer (102,201), said surface region being in contact with said electrolyte (204) or electrolyte solution and opposed to said cathode (203); said anode terminal (206) is extended from said collector (101,200), and said cathode (203) comprises a cathode active material containing lithium; characterised in that : said layer (102,201) comprises (i) metal (106) incapable of being alloyed with lithium upon charging and (ii) metal capable of being alloyed with lithium upon charging, wherein said layer (102,201) contains said metal (106) such that said metal (106) is enriched on the surface thereof and said layer (102,201) contains no lithium before charging is performed, said metal (106) comprising one or more metals selected from the group consisting of Ni, Ti, Cu, Ag, Au, Pt, Fe, Co, Cr, W and Mo, and said metal (ii) comprising one or more metals selected from the group consisting of Al, Mg, K, Na, Ca, Sr, Ba, Si, Ge, Sb, Pb, In and Zn. A rechargeable lithium battery according to claim 1, wherein the layer (102,201) has a member containing the metal (ii) in particulate form, and the collector (101,200) comprises a collector member comprising a metal incapable of being alloyed with lithium, comprising one or more metals selected from the group consisting of Ni, Ti, Cu, Ag, Au, Pt, Fe, Co, Cr, W and Mo, and a constituent other than the metal incapable of being alloyed with lithium, wherein said member of the layer (102,201) containing the metal (ii) is fixed to the collector (101,200) with a binding agent (105). A rechargeable lithium battery according to claim 1 or 2, wherein the layer (102,201) comprises an alloy containing at least the metal (i) and the metal (ii). A rechargeable lithium battery according to claim 1 or 2, wherein the layer (102,201) has a surface formed by selectively etching a surface of a member containing the metal (ii) and other metal having an etching rate different from that of the metal (ii). A rechargeable lithium battery according to claim 1, wherein the layer (102,201) has an increased surface area obtained by selectively etching the metal (i) or the metal (ii) contained in said layer (102,201). A rechargeable lithium battery according to claim 1, wherein the surface region in the layer (102,201) has surface irregularities, and the surface region is contacted with an electrolyte (204) or electrolyte solution, is opposed to a cathode (203), and is roughened such that a difference between a value corresponding to a ½ of the maximum height Rmax of the surface irregularities and a central line average roughness Ra is 1/10 or less of the distance between the anode and the cathode. A rechargeable lithium battery according to any of claims 1 to 6, wherein the layer (102,201) has a surface having a roughness which satisfies the equation below: 1 +(4nRa/L) ≧ 1.05, with Ra being a central line average roughness, L being a length measured, and n being the number of peaks per the length L. A rechargeable lithium battery according to any of claims 1 to 7, wherein the anode (202) has a portion provided with an electrically conductive layer (107) having a coefficient of extension at room temperature which is greater than that of the metal (ii). A rechargeable lithium battery according to any of claims 1 to 8, wherein the anode (202) has a collector portion provided with an electrically conductive layer (107) having a coefficient of extension at room temperature which is greater than that of the metal (ii). A rechargeable lithium battery according to claim 9 wherein the electrically conductive layer (107) comprises one or more materials selected from the group consisting of Sn-Bi alloy, Sn-Pb alloy, Zn-Al alloy, Cu-Zn alloy, Cd-Zn alloy, and an electrically conductive ink comprising electrically conductive particles fixed with a material substantially unreactive with an electrolyte or electrolyte solution, said material being an organic polymer material. A rechargeable lithium battery according to claim 10, wherein the organic polymer material is selected from the group consisting of fluorine-containing resins, polyolefins, silicone resins and other polymers capable of being highly crosslinked. A rechargeable lithium battery according to any of claims 1 to 7, wherein the anode (202) has a surface coating comprising an insulating film or a semiconductor film incapable of being dissolved in the electrolyte (204) or electrolyte solution and having a property of allowing a lithium ion to pass through but prohibiting a lithium metal deposited upon battery charging to pass through. A rechargeable lithium battery according to claim 1, wherein the layer (102,201) comprises an alloy comprising the metal (i) and the metal (ii), said alloy containing the metal (ii) at a content ratio of 50% or more. An anode (202) usable as the anode in the fabrication of a rechargeable lithium battery comprising at least an anode (202), a separator (205), a cathode (203), the active material thereof containing lithium, an electrolyte (204) or electrolyte solution, and an anode terminal (206) electrically connected to said anode (202), said anode (202) and said cathode (203) being electrically contacted with said electrolyte (204) or electrolyte solution, said anode (202) comprising (a) a collector (101, 200) and (b) a layer (102, 201) in contact with said collector, said collector (101,200) comprising metal incapable of being alloyed with lithium upon charging, comprising one or more metals selected from the group consisting of Ni, Ti, Cu, Ag, Au, Pt, Fe, Co, Cr, W and Mo; characterised in that : said layer (102,201) comprises (i) metal (106) incapable of being alloyed with lithium upon charging and (ii) metal capable of being alloyed with lithium upon charging, wherein said layer (102,201) contains said metal (106) such that said metal (106) is enriched on the surface thereof and said layer (102,201) contains no lithium before charging is performed, said metal (106) comprising one or more metals selected from the consisting of Ni, Ti, Cu, Ag, Au, Pt, Fe, Co, Cr, W and Mo, and said metal (ii) comprising one or more metals selected from the group consisting of Al, Mg, K, Na, Ca, Sr, Ba, Si, Ge, Sb, Pb, In and Zn. An anode according to claim 14, wherein the layer (102,201) has a member containing the metal (ii) in particulate form, and the collector (101, 200) comprises a collector member comprising a metal incapable of being alloyed with lithium, comprising one or more metals selected from the group consisting of Ni, Ti, Cu, Ag, Au, Pt, Fe, Co, Cr, W and Mo and a constituent other than the metal incapable of being alloyed with lithium, wherein said member of the layer (102,201) containing the metal (ii) is fixed to the collector ( 101, 200 ) with a binding agent (105). An anode according to claim 14 or 15, wherein the layer (102,201) comprises an alloy containing at least the metal (i) and the metal (ii). An anode according to claim 14 or 15, wherein the layer (102,201) has a surface formed by selectively etching a surface of a member containing the metal (ii) and other metal having an etching rate different from that of the metal (ii). An anode according to claim 14, wherein the layer (102,201) has an increased surface area obtained by selectively etching the metal (i) or the metal (ii) contained in said layer (102,201). An anode according to any of claims 15 to 18, wherein the layer (102,201) has a surface having a roughness which satisfies the equation 1 +(4nRa/L) ≧ 1.05, with Ra being a central line average roughness, L being a length measured, and n being the number of peaks per the length L. An anode according to any of claims 14 to 19, wherein the anode (202) has a portion provided with an electrically conductive layer (107) having a coefficient of extension at room temperature which is greater than that of the metal (ii). An anode according to claim 20, wherein the electrically conductive layer (107) comprises one or more materials selected from the group consisting of Sn-Bi alloy, Sn-Pb alloy, Zn-Al alloy, Cu-Zn alloy, Cd-Zn alloy, and an electrically conductive ink comprising electrically conductive particles fixed with a material substantially unreactive with electrolyte or electrolyte solution, said material being an organic polymer material. An anode according to claim 21, wherein the organic polymer material is selected from the group consisting of fluorine-containing resins, polyolefins, silicone resins and other polymers capable of being highly crosslinked. An anode according to any of claims 14 to 19, wherein the anode (202) has a surface coating comprising an insulating film or a semiconductor film incapable of being dissolved in electrolyte (204) or electrolyte solution and having a property of allowing lithium ions to pass through but prohibiting lithium metal, deposited in use upon battery charging, to pass through. An anode according to claim 14, wherein the layer (102,201) comprises an alloy comprising the metal (i) and the metal (ii), said alloy containing the metal (ii) at a content ratio of 50% or more. A process for producing a rechargeable lithium battery, the process comprising: (a) providing a rechargeable lithium battery according to one of claims 1 to 13, and (b) subjecting the rechargeable lithium battery to charging. A process for producing a rechargeable lithium battery, the process comprising: (a) fabricating a rechargeable lithium battery using an anode according to one of claims 14 to 24, and (b) subjecting the rechargeable lithium battery to charging.

Inventors: ASAO MASAYA, KAWAKAMI SOICHIRO, KOBAYASHI NAOYA, MISHINA SHINYA, ASAO, MASAYA, KAWAKAMI, SOICHIRO, KOBAYASHI, NAOYA, MISHINA, SHINYA, ASAO, MASAYA, C/O CANON K.K., KAWAKAMI, SOICHIRO, C/O CANON K.K., KOBAYASHI, NAOYA, C/O CANON K.K., MISHINA, SHINYA, C/O CANON K.K.
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1995
Main classification: H01M4
IPC codes: H01M6, H01M4, H01M10