Ink ribbon fabric foundation

Abstract: A fabric foundation for an ink ribbon comprising a woven fabric comprising warp yarns and weft yarns, and the woven fabric satisfying the following equation: K = 1.5 to 6 wherein K is the ratio of C₁/C₂; C₁ is a warp crimp rate; and C₂ is a weft crimp rate. The ink ribbon fabric foundation is hardly damaged under severe printing conditions such as high speed and strong striking force, offering an extended life.

Description: The present invention relates to a fabric foundation for an ink ribbon which is used for printing with being impregnated with a liquid ink, comprising a woven fabric having crimped warp yarns and crimped weft yarns, as know from JP-A-57 098 382. Ink ribbons impregnated with a liquid ink have been used in various impact printers such as wire dot printer and daisy wheel printer. The recent trend of such printers is toward higher printing speed. With these printers, printing is conducted with running an ink ribbon and, hence, a monentary rubbing between the ink ribbon and a printing paper, which is caused when striking with a print head, becomes violent with an increased printing speed. Further, the number of constituent sheets of duplicate chits or slips, and the like has be increased and a case has been increased where printing is conducted on such thick paper sheets as used in deposit passbooks, and the like. These cases require that a stronger striking power is exerted on the ink ribbon. Owing to such increased rubbing and striking force, ink ribbons are used under extremely severe conditions, resulting in damage to the ink ribbons in a short period of time. This tendency is marked with seamless ink ribbons because it is difficult to produce those having a large entire length. The seamless ink ribbon is fabricated by weaving a tubular fabric as shown in Fig. 3(A) according to an endless plain weaving method and cutting crosswise the tubular fabric to a desired width, yielding ring-like fabric foundations with no seam for the seamless ink ribbon as shown in Fig. 3(B). In Fig. 3(A), the longitudinal direction of the tube corresponds to the warp yarn direction, and the circumferential direction of the tube corresponds to the weft yarn direction. Fig. 3(C) is an enlarged partial plan view showing the thus obtained seamless ink ribbon fabric foundation, wherein numeral 1 denotes a warp yarn and numeral 2 denotes a weft yarn. In view of the foregoing, it is an object of the present invention to provide a fabric foundation for an ink ribbon, particularly for a seamless ink ribbon, which is hardly damaged under severe printing conditions such as high speed and strong striking force, offering an extended life. This and other objects of the present invention will become apparent from the description hereinafter, and are solved by a fabric foundation having the features of claim 1. Preferred improvements are subject matter of the dependent claims 2 and 3. The present invention provides a fabric foundation for an ink ribbon, comprising a woven fabric having warp yarns and weft yarns, the woven fabric being a plain weave fabric satisfying the following equation: K = 1.5 to 6 wherein K is the ratio of C 1 /C 2 ; C 1 is the warp crimp rate; and C 2 is the weft crimp rate. Herein, the terms "warp yarn" and "weft yarn" mean the warp yarn and the weft yarn on a loom, respectively. Accordingly, with the seamless ink ribbon, yarns in the transverse direction of the ribbon are warp yarns and yarns in the longitudinal direction of the ribbon are weft yarns. The warp crimp rate C 1 is defined by the following formula: Warp crimp rate C 1 (%) = L 10 -L 1 L 1 × 100 wherein L 1 is a given length of the ink ribbon fabric foundation in the warp yarn direction, and L 10 is the length of the warp yarns constituting the fabric foundation of the given length. The weft crimp rate C 2 is defined by the following formula: Weft crimp rate C 2 (%) = L 20 L 2 × 100 wherein L 2 is a given length of the ink ribbon fabric foundation, in the weft yarn direction, and L 20 is the length of the weft yarns constituting the fabric foundation of the given length. In the drawings fig. 1 is a schematic sectional view showing an example of the ink ribbon fabric foundation of the present invention, fig. 2 is a schematic sectional view illustrating an example of an endless plain weaving method, fig. 3(A) is a perspective view showing a tubular fabric woven by an endless plain weaving method; Fig. 3(B) is a perspective view showing a fabric foundation for a seamless ink ribbon obtained by cutting crosswise the tubular fabric; and Fig. 3(C) is an enlarged partial plan view showing the tissue of the seamless ink ribbon fabric foundation obtained by the endless plain weaving method, and fig. 4 is a schematic sectional view showing a conventional ink ribbon fabric foundation. The present inventors have examined conventional seamless ink ribbon fabric foundations and found that with the conventional seamless ink ribbon fabric foundations, the ratio K of the warp crimp rate C 1 to the weft crimp rate C 2 ( K=C 1 /C 2 ) (hereinafter, the ratio K is referred to as "crimp rate ratio") usually ranges from 8 to 9. A microscopic observation of the conventional seamless ink ribbon fabric foundations reveals that the warp yarn 1 is a little slackened and the weft yarn 2 is a little tightened, as shown in Fig. 4. Further, it has been, found that when printing is conducted with use of an ink ribbon in such a condition, on the printing paper side, the warp yarns of the fabric foundation mainly strike the printing paper when striking with a printing head, resulting in deterioration of the warp yarns due to the rubbing and impact, and on the printing head side, the warp yarns are also deteriorated by direct striking with the thermal head, so that the fabric foundation is damaged in a short period of time. The present inventors have made intensive researches on the basis of these findings and succeeded in fabricating a fabric foundation having an extended life by specifying the crimp rate ratio K to the range of from 1.5 to 6. When the crimp rate ratio of the fabric foundation is within the range of from 1.5 to 6, the warp yarns and the weft yarns strike the printing paper to the same degree, resulting in an extremely extended life. The present invention will be explained by taking a fabric foundation for a seamless ink ribbon as an example. Fig. 1 is a schematic sectional view showing an example of a fabric foundation for a seamless ink ribbon according to the present invention. As illustrated in Fig. 1, with the fabric foundation satisfying the crimp rate ratio prescribed in the present invention, the warp yarns 1 are tightened as compared to the warp yarns of the conventional fabric foundation and the weft yarns 2 are slackened as compared to the weft yarns of the conventional fabric foundation, and, hence, the warp yarns 1 and the weft yarns 2 appear to the same degree on the surface of the fabric foundation. When printing is conducted with use of an ink ribbon using such a fabric foundation, the warp yarns 1 and the weft yarns 2 strike a printing paper to the same degree when striking with the printing head, whereby deterioration of only the warp yarns encountered with the conventional ink ribbon is prevented to provide a largely extended life. For example, as shown in comparative tests mentioned below, the life (expressed in terms of the number of characters printed till the ink ribbon is damaged) of a conventional fabric foundation having a crimp rate ratio K of 8.7 is 90 × 10 4 characters, while the life of a fabric foundation having a crimp rate ratio of 6 according to the present invention is 150 × 10 4 characters which is 1.7 times the value 90 × 10 4 characters. Thus, a large extension of the life of a seamless ink ribbon can be achieved by the present invention. When the crimp rate ratio K is larger than 6, the warp yarns 1 become a little slackened and, hence, the degree to which the warp yarns 1 strike the printing paper when striking with the printing head is greater than that to which the weft yarns 2 strike the printing paper. Consequently, the warp yarns 1 are violently deteriorated, resulting in reduction of life of the fabric foundation. When the crimp rate ratio K is smaller than 1.5, conversely the weft yarns 2 become a little slackened, and, hence, the weft yarns 2 mainly strike the printing paper when striking with the printing head, resulting in reduction of life of the fabric foundation. Further, stable production of a fabric foundation having a crimp rate ratio of smaller than 1.5 is difficult under the present condition. Usable as the warp yarn or the weft yarn in the present invention are yarns obtained from one or more of synthetic fibers, regenerated fibers and natural fibers, inclusive of polyamide fibers such as nylon 6 and nylon 66, polyester fibers, rayon fiber, silk fiber and cotton fiber. Yarns each of about 20 to about 70 deniers are preferably used. Usually, there are used yarns obtained by gathering a plurality of single fibers (monofilaments) each of about 0.8 to about 3 deniers or a plurality of spun yarns (of natural fiber such as silk fiber or cotton fiber) each of about 0.8 to about 3 deniers, and preferably subjecting the resultant to a soft twist to give yarns each having a thickness within the above-mentioned range. With use of the aforesaid warp yarns and weft yarns, a tubular fabric is preferably woven by an endless plain weaving method. Fig. 2 is a schematic sectional view showing an example of the endless plain weaving method. As shown in Fig. 2, a weft yarn 2 is moved to and fro through group G 1 of warp yarns and group G 2 of warp yarns arranged above and below in two rows to weave a tubular fabric. In Fig. 2, numeral 10 denotes a shuttle, and numerals 11 and 12 denote pins for supporting the ends of the weft yarn 2 between which the weft yarn 2 is moved to and fro. The crimp rate ratio of the resulting fabric can be controlled by adjusting the tensile force exerted on the warp yarn 1 and the tensile force exerted on the weft yarn 2 to adjust the warp crimp rate C 1 and the weft crimp rate C 2 . In view of ensuring general requirements for ink ribbon fabric foundations, such as strength, capacity for containing ink and clearness of print images, it is preferable to adjust the crimp rate ratio K to the range of 1.5 to 6, provided that the following conditions are satisfied: Warp yarn density = 47 to 75 yarns/cm (120 to 190 yarns/inch), Weft yarn density = 47 to 67 yarns/cm (120 to 170 yarns/inch), Warp crimp rate C 1 = 7 to 15 %, and Warp crimp rate C 2 = 1 to 6 %. The thus obtained tubular fabric is cut crosswise to a desired length into rings, which are subjected to post-treatments such as washing and scouring to give the desired fabric foundations for a seamless ink ribbon. The fabric foundation is impregnated with a liquid ink composition to give a seamless ink ribbon. In the foregoing, the present invention has been explained by taking the fabric foundation for the seamless ink ribbon as an example. However, the present invention is also preferably applicable to a fabric foundation for an endless ink ribbon with a seam, which is obtained by cutting off a strap from a plain weave fabric and joining both ends of the strap. With the endless ink ribbon fabric foundation, usually, the longitudinal direction of the ribbon corresponds to the warp yarn direction, and the transverse direction of the ribbon corresponds to the weft yarn direction. The present invention will be more fully described by way of Examples. Examples 1 to 4 and Comparative Examples 1 to 2 A yarn of 40 deniers which was obtained by gathering 34 nylon 66 monofilaments each of 1.2 deniers and subjecting the resultant to a soft twist, was used as warp yarn, and a yarn of 40 deniers which was obtained by gathering 34 nylon 66 monofilaments each of 1.2 deniers and subjecting the resultant to a soft twist, was used as weft yarn. The warp yarn and the weft yarn were woven with adjusting the tensile forces of the warp yarn and weft yarn according to the endless plain weaving method as shown in Fig. 2 to give a tubular fabric with a circumferential length of 1.6 m having yarn density, crimp rate and crimp rate ratio as shown in Table 1. The tubular fabric was cut crosswise to a width of 8 mm into rings, which were subjected to scouring treatment to give fabric foundations for a seamless ink ribbon. The fabric foundation was impregnated with a liquid ink having the following formula to give a seamless ink ribbon. Ink formula Component Parts by weight Nigrosine Base 20 Carbon black 5 Oleic acid 30 Sorbitan 20 Motor oil 25 With use of each of the thus obtained seamless ink ribbons on a wire dot printer equipped with a printing head having 24 pins, LQ (letter quality) printing was conducted on a paper for business form 55 kg made by Toppan Moore Co., Ltd. to determine the life (the number of characters printed till the ink ribbon is damaged) of the ink ribbon fabric foundation. The results are shown in Table 1. Crimp rate ratio (K) Yarn density yarns/cm (yarns/inch) Crimp rate (%) Life (Number of characters) Warp Weft Warp (C 1 ) Weft (C 2 ) Com. Ex. 1 1.2 57,5 (146) 58 (148) 7.0 6.0 100 × 10 4 Ex. 1 1.6 57,5 (146) 58 (148) 8.0 5.0 160 × 10 4 Ex. 2 3.0 57,5 (146) 58 (148) 10.0 3.3 200 × 10 4 Ex. 3 4.0 57,5 (146) 58 (148) 10.0 2.5 180 × 10 4 Ex. 4 6.0 57,5 (146) 58 (148) 12.0 2.0 150 × 10 4 Com. Ex. 2 8.7 57,5 (146) 58 (148) 13.0 1.5 90 × 10 4 In addition to the materials and ingredients used in the Examples, other materials and ingredients can be used in Examples as set forth in the specification to obtain substantially the same results. As described above, the ink ribbon fabric foundation of the present invention wherein the ratio K of the warp crimp rate C 1 to the weft crimp rate C 2 is specified to the range of from 1.5 to 6 provides an extremely extended life for use with an impact printer wherein printing is performed at a high speed and a strong striking force.

Claims: Fabric foundation for a ink ribbon, comprising a woven fabric having warp yarns (1) and weft yarns (2), characterized in that the woven fabric is a plain weave fabric satisfying the following equation: K = 1.5 to 6, wherein K is the ratio of C 1 /C 2 ; C 1 is the crimp rate of the warp and C 2 is the crimp rate of the weft. The fabric foundation of Claim 1, characterized in that the plain weave fabric is in the form of a seamless ring. The fabric foundation of Claim 1 or 2, characterized in that the plain weave fabric satisfies the following conditions: Warn yarn (1) density = 47 to 75 yarns/cm (120 to 190 yarns/inch), Weft yarn (2) density = 47 to 67 yarns/cm (120 to 170 yarns/inch), Warp crimp rate C 1 = 7 to 15 %, and Weft crimp rate C 2 = 1 to 6 %.

Inventors: CAI ZHENG IONG, TSUBOI SEIJI, CAI, ZHENG IONG                                D, TSUBOI, SEIJI, CAI, ZHENG IONG, C/O TECHN. CENT. FUJICOPIAN LTD, TSUBOI, SEIJI, C/O TECHN. CENT. FUJICOPIAN LTD.
Applicants: FUJI KAGAKU SHIKOGYO, FUJICOPIAN CO., LTD.
Application year: 1995
Main classification: B41J31
IPC codes: B41J31