Method for inhibiting polymerization of (meth)acrylic acid and esters thereof

Abstract: Disclosed herein is a method for inhibiting polymerizable (meth)acryiic acid and esters thereof from polymerizing during their production, transportation and storage by using an inhibitor combination comprising an N-oxyl compound and at least one compound selected from the group consisting of manganese salt compounds, copper salt compounds, 2,2,6,6,-tetramethylpiperidine compounds and nitroso compounds. The N-oxyl compound is one or more kinds selected from 2,2,6,6,-tetramethylpiperidinooxyl, 4-hydroxy-2,2,6,6,-tetramethylpiperidinooxyl and 4, 4', 4''-tris-(2,2,6,6,-tetramethylpiperidinooxyl)phosphite. The combined use of the inhibitors provides superior inhibiting effect compared to the use of single inhibitors.

Description: The present invention relates to a method for inhibiting the polymerization of (meth)acrylic acid monomers and (meth)acrylate monomers (referred to as (meth)acrylic add and esters thereof hereinafter). It is well-known that (meth)acrylic acid and esters thereof have a strong tendency to spontaneous polymerization by light or heat. Hence, it is common practice to add one inhibitor or more in combination to inhibit polymerization during their storage. An example of the inhibitors which have so far been tried is N-oxyl compound which has N-oxyradicais, such as di-tert-butyl nitroxide and 2,2,6,6,-tetramethyl-4-hydroxypiperidinooxyl(2,2,6,6-tetramethyl-4-hydroxypiperidine-1-oxyl), as disclosed in GB-B-1,127,127. According to the disclosure, they are more effective than known inhibitors such as hydroquinone, phenothiazine, and cupric chloride, when they are used alone. The N-oxyl compound is also used as an inhibitor in the production of methacrylic acid from methacrolein by the aid of an oxygen-containing gas in an organic solvent. It includes 2,2,6,6-tetramethyl-4-hydroxypiperidinooxyl and 2,2,6,6-tetramethylpiperidinooxyl as disclosed in US-A-4,127,603. It also includes 2,2,5,5-tetramethyl-3-oxopyrrolidinooxyl and 2,2,6,6-tetramethyl-4-acetoxypiperidinooxyl as disclosed in Japanese Patent Publication No. 46496/1983. In addition, it is shown in Chinese Patent Laid-Open No. 1,052,847A that 2,2,6,6-tetramethyl-4-hydroxypiperidinooxyl effectively inhibits the polymerization of acrylic acid and acrylate when used alone or in combination with hydroquinone. Contrary to the foregoing, the present inventors have found that the N-oxyl compound used alone or in combination with hydroquinone does not work satisfactorily under specific conditions. In other words, the above-mentioned inhibitor used in an ordinary amount does not work in the production of (meth)acrylic acid by catalytic gas phase reaction, because polymerization of (meth)acrylic acid easily occurs while it is separated by azeotropic distillation from its aqueous solution containing acetic acid and aldehydes. Thus, there was a problem of the formation of popcorn polymers and sticky polymers in the distillation column during distillation, which prevents the continuous operation of the plant for a long period of time. Since a large amount of inhibitor was required to obtain effective inhibition, they didn't adapt for practical use. It is an object of the present invention to provide a method for inhibiting the polymerization of (meth)acrylic acid and esters thereof with small amount of inhibitor in the above-mentioned process. The gist of the present invention resides in a method for inhibiting the polymerization of (meth)acrylic add and esters thereof, the method comprising using, as the inhibitor of the polymerization, an N-oxyl compound and at least one further compound selected from the group consisting of manganese salt compounds, copper salt compounds, 2,2,6,6,-tetramethylpiperidine compounds and nitroso compounds by adding said two or more inhibitors to the (meth)acrylic acid or esters thereof. According to the more desirable embodiment of the present invention, the N-oxyl compound is one or more than one selected from 2,2,6,6,-tetramethyl-piperidinooxyl, 4-hydroxy-2,2,6,6,-tetramethyl-piperidinooxyl, and 4,4',4"-tris-(2,2,6,6,-tetramethylpiperidinooxyl)phosphite. The present inventors researched a series of methods for inhibiting polymerization of (meth)acrylic acid and esters thereof and already filed applications for the method of using a specific N-oxyl compound with phenol compounds and phenothiazine compounds in combination as inhibitors (EP-A-0 620 206) Then the inventors have invented another surprisingly effective method for inhibiting polymerization. The essential prerequisite of the present invention resides in using, as the inhibitor, the above-mentioned N-oxyl compound and one or more than one compound selected from the group consisting of manganese salt compounds, copper salt compounds, 2,2,6,6,-tetra-methylpiperidine compounds and nitroso compounds. Each compound can be used as an inhibitor by itself, but does not show sufficient effect. The present inventors have found that only when used together with an N-oxyl Compound, these compounds provide a remarkable synergistic effect for inhibiting the polymerization of (meth)acrylic acid and esters thereof, which they incompletely provide when used alone. The present invention is based on this finding. The present invention is described in detail hereinafter. In the present invention, N-oxyl compounds are used as an essential component of the inhibitor. There are no specific restriction on the N-oxyl compound used in the present invention. It is preferred to use one or more the one kind of the N-oxyl compound selected from 2,2,6,6-tetramethylpiperidinooxyl, 4-hydroxy-2,2,6,6-tetramethylpiperidinooxyl, and 4,4',4"-tris-(2,2,6,6-tetramethylpiperidinooxyl)phospite. In the present invention, the four components, manganese salt compound, copper salt compound, 2,2,6,6,-tetramethylpiperidine compound and nitroso compound have been found to provide an excellent inhibiting effect in combination with an N-oxyl compound, and at least one of these is to be used with the N-oxyl compound. One or more of them may be used together with the N-oxyl compound(s), and an inhibitor using more than three components provides a similar or even more excellent inhibiting effect. The manganese salt compound used in the present invention may include, for example, manganese di-alkyldithiocarbonate(the alkyl groups are selected from methyl, ethyl, propyl and butyl and may be same or different with each other), manganese diphenyldithiocarbamate, manganese formate, manganese acetate, manganese octanate, manganese naphthenate, potassium permanganate, manganese ethylendiaminetetraacetate, and the like. One or more kinds of them may be used. The manganese salt compound shows relatively inferior inhibiting effect when it is used alone, however, in using it with N-oxyl compounds or with a combination of the N-oxyl compound and other inhibitors according to the present invention, it provides an excellent inhibiting effect. The copper salt compound used in the present invention may include, for example, copper dialkyldithiocarbamate (the alkyl groups are selected from methyl, ethyl, propyl or butyl and may be same or different with each other), copper diphenyldithiocarbamate and the like, and one, two or more kinds may be used together. The 2,2,6,6,-tetramethylpiperidine compound used in the present invention may include, for example, 2,2,6,6-tetramethylpiperidine, 4-hydroxy-2,2,6,6-tetramethylpiperidine, 1-hydroxy-2,2,6,6,-tetramethylpiperidine, 1,4-dihydroxy-2,2,6,6,-tetramethylpiperdine and the like, and one or more of them may be used. The nitroso compound used in the present invention may include, for example, p-nitrosophenol, N-nitrosodiphenylamine, ammonium salt of N-nitrosophenylhydroxyamine and the like, and one, two or more kinds may be used together. According to the present invention, the above-mentioned at least two compounds, i.e. the N-oxyl compound and at least one compound selected from the group consisting of manganese salt compound, copper salt compound, 2,2,6,6,-tetramethylpiperidine compound and nitroso compound, produce a pronounced inhibiting effect. Further, other known inhibitors may be used together with the above compounds. Such known inhibitors may include, for example, hydroquinone, p-methoxyphenol(methoquinone), cresol, t-butylcatechol, diphenyl-amine, phenothiazin, tetraalkylthiuramdisulfide (the alkyl groups mean the same as the above), Methylene Blue and the like. If necessary, they may also be used in combination with molecular oxygen to enhance the inhibiting effect and to provide the continuous operation of the plant for a long period of time. The inhibiting method of the present invention may be favorably applied to (meth)acrylic acid and esters thereof which are particularly liable to polymerize among vinyl compounds. Examples of the acrylic esters include methyl acrylate, ethyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, 2-hydroxyethyl acrylate, and 2-hydroxypropyl acrylate. Examples of the methacrylic ester include methyl methacrylate, butyl methacrylate, 2-hydroxyethyl methacrylate, and 2-hydroxypropyl methacrylate. According to the inhibiting method of the present invention, the inhibitors can be added to (meth)acrylic acid, e.g. in all distillation processes, at various locations, such as rectification column, separation column from solvent, separation column from low-boiling fractions such as acetic add, and stripper of low-boiling acrolein and methacrolein, for instance in the case where (meth)acrylic acid is produced by the catalytic gas phase reaction. The inhibitors can also be used to stabilize the transportation and storage of (meth)acrylic acid. When producing the present invention one is adding the above-mentioned two or more inhibitor compounds to the (meth)acrylic acid or ester(s) thereof. The inhibitors may be added in the form of a solid or powder or in the form of an aqueous solution or solvent solution. The inhibitors may be added all at once (in the form of solution for example) or one after another. If the inhibitor is to be added during the distillation process in the production of (meth) acrylic acid or esters thereof, it may be dissolved in the feed or reflux. The amount of the inhibitors to be used is not specifically limited, depending on the operating conditions. Usually, it may be 3-650 ppm (by weight) of the amount of evaporated monomer (or (meth)acrylic acid and esters thereof). The preferred amount of the individual inhibitors based on the amount of evaporated monomer is as follows: N-oxyl compound: 1-100 ppm Manganese salt compound : 1-50 ppm Copper salt compound : 1-50 ppm 2,2,6,6,-tetramethylpiperidine compound : 1-500 ppm Nitroso compound : 1-500 ppm In case of the storage of the monomer the above-mentioned figures are based on the total amount of (meth)acrylic acid and esters thereof. The amount of evaporated monomer means the total amount of monomer vapor which is generated in the reboiler in proportion to the amount of heat fed to the reboiler. The total amount of the monomer vapor can be easily calculated and the calculated numeral is an important factor to determine the amount of the inhibitors to be added. The optional molecular oxygen component may be added to (meth)acrylic acid and esters thereof directly by bubbling or indirectly by dissolution in solvents. Bubbling may be easily accomplished by introducing oxygen gas to the distillation column or stripper from their bottom and/or from the reboiler. The amount of molecular oxygen should preferably be 0.1-1.0 vol% of the amount of evaporated monomer. Thus the method of the present invention provides the uninterrupted operation of the plant for a long period and stable transportation and storage of (meth)acrylic acid and esters thereof. To further illustrate the invention, and not by way of limitation, the following examples are given. (Unit ppm in the following examples and comparative examples is based by weight) Example 1 Pure acrylic acid was prepared from commercial one by distillation to remove inhibitors. 2ml each of the pure acrylic acid were placed in a test tube and incorporated with inhibitors in the compositions and the amounts as shown in Table 1 and 2. (The amounts are the figures after the compound abbreviations in the following tables and they are expressed by ppm values based on the amount of the added acrylic acid.) Experiments Nos. 1-10 are for comparison. The test tube was kept under reduced pressure and immersed in an oil bath at 100°C. The time till the starting of a white turbidity by the polymerized products (induction period) was measured by visual inspection. The results are shown in Table 1 and 2. Compounds are abbreviated as follow hereinafter. PO: 2,2,6,6-tetramethylpiperidinooxyl 4H-PO: 4-hydroxy-2,2,6,6-tetramethylpiperidinooxyl T-PO: 4,4',4"-tris-(2,2,6,6-tetramethylpiperidinooxyl)phosphite MnAc: manganese acetate CB: copper dibutyfdithiocarbamate 4HTMP: 4-hydroxy-2,2,6,6,-tetramethylpiperidine DHTMP: 1,4-dihydroxy-2,2,6,6,-tetramethylpiperidine PNP: p-nitrosophenol NNDPA: N-nitrosodiphenylamine NPH: ammonium salt of N-nitrosophenylhydroxyamine Run No. Inhibitors (ppm) Induction period (min) N-oxyl compound Mn salt compound Cu salt compound Piperidine compound Nitroso compound 1 4H-PO 5 19 2 4H-PO 10 36 3 MnAc 5 5 4 MnAc 10 5 5 CB 5 10 6 CB 10 18 7 DHTMP 5 6 8 DHTMP 10 7 9 NNDPA 5 7 10 NNDPA 10 8 11 4H-PO 5 MnAc 5 >240 12 PO 5 MnAc 5 >240 13 T-PO 5 MnAc 5 >240 14 4H-PO 5 CB 5 110 15 4H-PO 5 DHTMP 5 103 16 4H-PO 5 4HTMP 5 101 17 4H-PO 5 NNDPA 5 128 18 4H-PO 5 PNP 5 115 19 4H-PO 5 NPH 5 103 20 4H-PO 4 MnAc 3 CB 3 >240 21 4H-PO 4 MnAc 3 DHTMP 3 >240 22 4H-PO 4 MnAc 3 NNDPA 3 >240 23 4H-PO 3 MnAc 3 CB 2 DHTMP 2 210 24 4H-PO 3 MnAc 3 CB 2 NNDPA 2 230 25 4H-PO 2 MnAc 2 CB 2 DHTMP 2 NNDPA 2 190 26 4H-PO 4 CB 3 DHTMP 3 101 27 4H-PO 4 CB 3 NNDPA 3 105 28 4H-PO 3 CB 3 DHTMP 2 NNDPA 2 92 29 4H-PO 4 DHTMP 3 NNDPA 3 125 Run No. Inhibitors (ppm) Induction period (min) N-oxyl compound Mn salt compound Hydroquinone Methoquinone Phenothiazine 30 4H-PO 4 MnAc 3 3 >240 31 4H-PO 4 MnAc 3 3 >240 32 4H-PO 4 MnAc 3 3 >240 33 4H-PO 3 MnAc 3 2 2 180 34 4H-PO 3 MnAc 3 2 2 200 From Table 1, it is dear that the inhibiting effect is inferior in comparison experiments Nos. 1-10 where the inhibitor was used alone, when compared to the present invention experiments Nos. 11-29 where 2-5 inhibitors were used together, since the comparison examples showed shorter induction periods. Though the total amount(100 ppm) of the used inhibitors of the present invention was same as that of comparison examples Nos.2,4,6,8 and 10 in which the inhibitors were used alone, there seems a great difference concerning their induction periods. Thus, a synergistic effect by using the inhibitor combination of the present invention clearly appears. Especially in the case, where a manganese salt compound is used together with the N-oxyl compound, the synergistic effect is highly significant. Additionally, from Table 2, it is clear that a similar inhibiting effect was obtained when other known inhibitors (examples Nos. 30-34) were added to the inhibitor-pair according to this invention (example No. 11). Example 2 The inhibiting effect was evaluated in azeotropic separation of acrylic acid from its aqueous solution (containing 30 wt% water and 2.5 wt% acetic acid) resulting from the catalytic gas phase reaction of propylene. The azeotropic separation was carried out using a packed column with a feed pipe in the middle and a condenser at the top and also using methyl isobutyl ketone as reflux, with the pressure being 160 mmHg and the temperature being 49°C at the top and 97°C at the bottom. Each of the inhibitors shown in Table 3 was added to the reflux (which was fed to the column) and oxygen gas was fed to the bottom of the column. The amounts of the inhibitors and oxygen given in Table 3 are based on the amount of evaporated acrylic acid. It was found that the bottom product in the steady state was composed of 97 wt% acrylic acid and 0.5 wt% acetic acid, with the remainder being 2.5 wt%. After continued operation for 8 hours, with recycled oil phase as the reflux, the amount of polymers formed in the column was determined through suction drying to obtain constant weight. The results are shown in Table 3. Run No. Inhibitors (ppm) Amount of oxygen (vol%) Amount of polymer formed (g) 4H-PO MnAc CB DHTMP NNDPA 35 3.3 0.21 10.4 36 3.3 0.21 53.8 37 3.3 0.21 41.8 38 3.3 0.21 38.5 39 3.3 0.21 25.1 40 3.3 3.3 0.21 1.2 41 3.3 3.3 0.21 2.5 42 3.3 3.3 0.21 2.3 43 3.3 3.3 0.21 1.9 From Table 3, it is clear that the amount of the formed polymer was very small in experiments Nos. 40 - 43 (pertaining to present invention) and that therefore the inhibitor combinations of the present invention perform an excellent effect compared to experiments Nos. 35-39. Example 3 Pure methacrylic acid was prepared from commercial one by distillation to remove inhibitors. 2ml each of pure methacrylic acid were placed on a test tube and incorporated with inhibitor combinations in the compositions; the amounts of the inhibitors are shown in Table 4 (the ppm values are based on the amount of added methacrylic acid). Experiments Nos. 44-48 are for comparison. The test tube was kept under reduced pressure and immersed in an oil bath at 130°C. Induction period was measured by visual inspection. The results are shown in Table 4. Run No. Inhibitors (ppm) Induction period (min) 4H-PO MnAc CB DHTMP NNDPA 44 10 65 45 10 7 46 10 19 47 10 8 48 10 25 49 5 5 > 240 50 5 5 > 240 51 5 5 > 240 52 5 5 > 240 53 4 3 3 > 240 54 4 3 3 > 240 55 4 3 3 > 240 56 3 3 2 2 > 240 57 3 3 2 2 > 240 58 2 2 2 2 2 220 59 4 3 3 > 240 60 4 3 3 > 240 61 3 3 2 2 > 240 62 4 3 3 > 240 From Table 4, it is clear that examples Nos. 49-62 showed a synergistic inhibiting effect of the present invention, since they showed longer induction period though the used amount of the inhibitors was the same as that of comparison examples Nos.44-48. Example 4 Four pure acrylates (methyl acrylate (AM), ethyl acrylate (AE), butyl acrylate (AB), and octyl acrylate (AO)) were prepared from commercial ones by distillation to remove inhibitors. 30ml each of the pure acrylate were placed in a test tube and incorporated with inhibitors in the compositions and the amounts as shown in Table 5 (the ppm values are based on the amount of the added acrylate). The test tube was kept under reduced pressure and immersed in an oil bath at 70°C for AM, 90°C for AE, and 120°C for AB and AO. The time till starting heat polymerization generation was measured as induction period. The results are shown in Table 5. Run No. Inhibitors (ppm) Induction period (min) 4H-PO MnAc CB DHTMP NNDPA AM AE AB AO 63 10 55.0 50.5 35.5 100.5 64 10 5.5 5.0 4.0 15.5 65 10 11.5 10.5 8.5 25.0 66 10 6.0 5.5 7.0 14.5 67 10 48.0 44.5 30.5 77.5 68 5 5 > 240 > 240 > 240 > 240 69 5 5 > 240 > 240 > 240 > 240 70 5 5 > 240 > 240 > 240 > 240 71 5 5 > 240 > 240 > 240 > 240 From Table 5, it is dear that examples Nos. 68-71 where inhibitors were used in pairs according to the present invention showed an excellent inhibiting effect for any of the acrylate. Example 5 Two pure methacrylates (methyl methacrylate (MMA) and butyl methacrylate (BMA)) were prepared from commercial ones by distillation to remove inhibitors. 30ml each of the pure methacrylate were placed in a test tube and incorporated with inhibitors in different compositions and amounts as shown in Table 6 (the ppm values are based on the added methacrylate). The test tube was kept under reduced pressure and immersed in an oil bath at 90°C for MMA and 120°C for BMA. Induction period was measured in the same manner as in Example 4. The results are shown in Table 6. Run No. Inhibitors (ppm) Induction period (hr) 4H-PO MnAc CB DHTMP NNDPA MMA BMA 72 10 62.0 33.5 73 10 2.5 1.5 74 10 7.0 6.0 75 10 7.5 5.5 76 10 55.0 21.0 77 5 5 > 240 > 240 78 5 5 > 240 > 240 79 5 5 > 240 > 240 80 5 5 > 240 > 240 From Table 6, it is clear that examples Nos. 77-80 (pertaining to the present invention) where the inhibitors were used in pairs show an excellent inhibiting effect against any of the methacrylate. Example 6 Four pure (meth)acrylates (listed below) were prepared from commercial ones by distillation to remove inhibitors. 30ml each of the pure (meth)acrylate were placed in a test tube and incorporated with inhibitors in the amounts as shown in Table 7 (the ppm values are based on the added (meth)acrylate). The test tube was kept under reduced pressure and immersed in an oil bath at 100°C. The time till starting heat polymerization generation was measured as induction period. The results are shown in Table 7. HEA: 2-hydroxyethyl acrylate HPA: 2-hydroxypropyl acrylate HEMA: 2-hydroxyethyl methacrylate HPMA: 2-hydroxypropyl methacrylate Run No. Inhibitors (ppm) Induction period (hr) 4H-PO MnAc CB DHTMP NNDPA HEA HPA HEMA HPMA 81 10 89.5 210.0 152.0 98.5 82 10 1.5 10.0 7.5 5.5 83 10 10.0 19.5 15.0 11.0 84 10 2.5 15.5 10.5 9.0 85 10 71.0 134.5 99.5 68.0 86 5 5 > 480 > 480 > 480 > 480 87 5 5 > 480 > 480 > 480 > 480 88 5 5 > 480 > 480 > 480 > 480 89 5 5 > 480 > 480 > 480 > 480 From Table 7, it is clear that the inhibiting effect of the inhibitor combinations of the present invention (runs nos. 86 to 89) is excellent in comparison to that of runs nos. 81 to 85. The method of the present invention for inhibiting polymerization has been described above. The inhibitor combination consists of an N-oxyl compound and at least one compound selected from the group consisting of manganese salt compounds, copper salt compounds, 2,2,6,6-tetramethylpiperidine compounds and nitroso compounds. The combinated use of the above inhibitors provides superior inhibiting effect compared to the use of only one inhibitor. It has now become possible to prevent (meth)acrylic acid and esters thereof from polymerizing even under the condition that occurs their polymerization very easily. Thus, the method of the present invention provides the uninterrupted operation of the plant for a long period and stable transportation and storage of (meth)acrylic acid and esters thereof.

Claims: Use of an N-oxyl compound and at least one compound selected from manganese salt compounds, copper salt compounds, 2,2,6,6-tetramethylpiperidirie compounds and nitroso compounds, for inhibiting the polymerization of (meth)acrylic acid and esters thereof, by adding said two or more inhibitors to the (meth)acrylic acid or esters thereof. Use according to claim 1 wherein the N-oxyl compound is at least one selected from 2,2,6,6-tetramethylpiperidinooxyl, 4-hydroxy-2,2,6,6-tetramethylpiperidinooxyl and 4, 4', 4"-tris (2,2,6,6-tetramethylpiperidinooxyl) phosphite. Use according to claim 1 or 2, wherein the composition comprises one or more manganese salt compounds. Use according to claim 1 or 2, wherein the composition comprises one or more copper salt compounds. Use according to claim 1 or 2, wherein the composition comprises one or more 2,2,6,6-tetramethylpiperidine compounds. Use according to claim 1 or 2, wherein the composition comprises one or more nitroso compounds. Use according to any of claims 1 to 6, wherein at least one further inhibitor from the group consisting of hydroquinone, p-methoxyphenol (methoquinone), cresol, t-butylcatechol, diphenylamine, phenothiazin, tetraalkylthiuramidsulfide and Methylene Blue is employed. Use according to any of claims 1 to 7, wherein the inhibitors are employed in combination with molecular oxygen.

Inventors: AKAZAWA YOJI, BABA MASAO, SAKAMOTO KAZUHIKO, TAKEDA TAKAHIRO, UEOKA MASATOSHI, AKAZAWA, YOJI, BABA, MASAO, SAKAMOTO, KAZUHIKO, TAKEDA, TAKAHIRO, UEOKA, MASATOSHI
Applicants: NIPPON CATALYTIC CHEM IND, NIPPON SHOKUBAI CO., LTD.
Application year: 1995
Main classification: C07C57
IPC codes: C07C51, C07C67, C07C57