Derivative of polyvinylpyridine

Abstract: A derivatized polymer is characterized by the repeating unit having the formula: wherein: P is phosphorus or arsenic; and n is 0 to 10.

Description: TECHNICAL FIELD The present invention pertains to stable electron acceptor compositions which have efficient and sustained photoinduced charge separation states. BACKGROUND OF THE INVENTION Solar energy can be used and stored by the efficient production of long-lived photo-induced charge separation - a state achieved in photosynthetic systems by the formation of a long-lived radical pair. A number of artificial systems have been reported that efficiently undergo photochemical charge transfer, unfortunately, the thermal back electron transfer often proceeds at an appreciable rate, limiting the utility of these systems. What is needed is a systems which has very efficient photoinduced charge transfer, and forms a charge-separated state which is long lived in air. The charge separation in these systems typically involves a redox reaction between a photo excited donor and a suitable acceptor, resulting in the production of radical ion pairs illustrated by the formula: (1a) D + hv → D * (1b) D * + A → A - + D + (2) D + + A → D + A The cation and anion generated in this way are better oxidants and reductants, respectively, than either of the neutral ground-state molecules. To harvest the light put into this system, the oxidizing and reducing power of the photo-generated species must be used before the electrons are transferred back (equation 2) generating the starting materials. It is desirable to control this photochemically unproductive thermal fast back electron transfer reaction. One method has been to incorporate the donors and acceptors into solid matrices. The individual components in the charge separated state have the appropriate potentials to carry out the reduction and oxidation of water. Unfortunately, these direct reactions are kinetically limited, such that catalysts are required to overcome the kinetic barriers. Colloidal platinum particles are ideal catalysts for the reduction of water to give H 2 .In systems used for photoreduction of water, the close contact of high potential radicals formed in the compounds and Pt particles is advantageous, because electron transfer from reduced viologen to Pt particles should compete effectively with back electron transfer. These platinum particles may be present in the reaction solution, incorporated into the structure of the compositions, or both. Compounds which can carry out reduction reactions, using hydrogen gas as their reducing equivalents, are useful as catalysts for the conversion of mixtures of hydrogen and oxygen to hydrogen peroxide. Hydrogen peroxide is a very large, volume chemical. The United States annual production is greater than 500 million lbs. Several processes have been patented for the production of hydrogen peroxide, which depend on the two following reactions. The goal is to promote reaction (3) and retard reaction (4): (3) H 2 + O 2 → H 2 O 2 (4) H 2 O 2 + H 2 → 2 H 2 O A number of catalysts for this conversion have been reported including both homogeneous and heterogeneous catalysts. The compositions of the present invention are capable of producing a sustained photoinduced charge separation state which renders the compositions useful in solar energy conversion and storage. In addition, the compositions permit reduction of various metal ions to produce the zero-valence metal in colloidal form entrapped in the matrices of the compositions. These latter matrices containing the zero-valence metal have a variety of uses such as in the decomposition of water to yield hydrogen gas and the sensing of oxygen. In addition, the zero-valence metal matrices can be used in catalysis, as for example in the production of hydrogen peroxide and the oligomerization of methane to form higher hydrocarbons. SUMMARY OF THE INVENTION The present invention relates to a derivatized polymer which has a repeating unit having the formula: Wherein: P is phosphorous or arsenic; and n is 0 to 10 BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic view of the highly ordered structure of a substrate and film. FIG. 2 is a schematic view of a solid composition incorporating "stalactite" and "stalagmite" ligands. FIG 3. is a schematic view of a solid incorporating metal Particles and "stalactite" and "stalagmite" ligands. DESCRIPTION OF THE PREFERRED EMBODIMENT In general the invention relates to layered compositions comprising two or more adjacent metal layers, independently of the other, comprised of atoms of a divalent, trivalent, or tetravalent metal of Group III, IVA, IVB having an atomic number of at least 21 or atoms of a lanthanide, which form a cohesive layer. The metal layers are adjacently spaced and in substantially parallel relation to each other and to the substrate. Disposed between, and in substantially perpendicular relation to the metal layers, are organic pillars which are independently, one from the other, covalently joined to two of the adjacent metal layers and thus forming interstices between the pillars and the two adjacent metal layers. This layered composition can take the form of, for example, a thin film or a micro-crystalline solid. The organic pillars are illustrated by the formula: I . -(Y 1 O 3 -Z-Y 2 O 3 )- each of Y 1 and Y 2 , independently of the other, is phosphorous or arsenic; Z is an electron accepting divalent group containing two conjugated cationic centers which together have a negative E o red value, wherein Z is capable of alternating between a stable reduced form and a stable oxidized form; A sufficient number of anions are bound to the metal ions which make up the metal layers, such that the metal ions have an effective valence of from + 1 to + 6, preferably + 3 or + 4. A separate group of anions is present within the lattice formed by the pillars and metal atoms to counterbalance any residual charge in the composition. Additionally, the composition can comprise particles of at least one Group VIII metal at zero valance trapped in the interstices between the pillars and the adjacent metal layers. These particles may enhance the function of the composition, for example, by acting as a catalyst for reduction reactions. The compositions can also comprise organic ligands disposed between the metal layers and between the pillars which are independently, one from the other, covalently joined to one of the metal layers. The ligands are illustrated by the formula: II . - Y 3 O 3 -R 3 Y 3 is phosphorous or arsenic; and, R 3 is a non-reducible capping group. A first embodiment relates to a composite composition in which a film is disposed on a supporting substrate. In that form, the layer closest to the substrate is bound to the substrate by a linking means. The substrate can be, for example metals, glass, silicas, polymers, semiconductors (e.g., silicon, gallium arsenide), combinations thereof such as a gold layer on an aluminum base, and the like. The substrate can be in any form, for example sheets, foils, plates, films, electrodes, colloidal particles in suspension, polymer templates, high surface area supports, and the like. The film is composed of a pfurality of pillared metal complexes, each of the formula: in which: L is a linking means; each of Y 1 and Y 2 , independently of the other, is phosphorus or arsenic; Z is a divalent group which reversibly forms a stable reduced form and contains two conjugated cationic centers which together have a negative E o red value; X is anion; Me Y is Me 1 n W m , where Me 1 is a divalent, trivalent, or tetravalent metal of Group III, IVA, or IVB having an atomic number of at least 21 or a lanthanide; W is an anion, such as, but not limited to, halides or pseudohalides, or -OH; n is 1, 2, or 3; m is 0, 1, 2, 3, or 4; k has a value of from 1 to about 100; p has a value of 0, 1, 2, or 3; and q is the charge on the anion, where for each additional k value, another layer is added to the film. Me 1 can be, for example, a group IVA metal having an atomic number of at least 21 such as germanium, tin, or lead, a group IVB metal such as titanium, zirconium, or hafnium, a group IIIA metal having an atomic number of at least 21 such as gallium, indium, or thallium, a group IIIB metal such as scandium, yttrium, or a lanthanide as for example lanthanum, cerium, praseodymium, etc . Of these, titanium, zirconium, hafnium, germanium, tin, and lead are preferred with zirconium being particularly useful. Each of Y 1 and Y 2 is phosphorus or arsenic, preferably phosphorus, each of Y 1 O 3 and Y 2 O 3 thus being a phosphonato or arsenato group. The group Z is divalent, being bound to the phosphorus or arsenic atom of the phosphonato or arsonato group defined by Y 1 O 3 and Y 2 O 3 . In practice, the precise structure of the group Z is of lesser importance than its electronic properties. Firstly, it must contain two conjugated cationic centers which together have a negative E o red value; i . e ., a reduction potential below that of hydrogen. Secondly, Z must be capable of existing both in a stable reduced form and reversibly in an oxidized form. The two conjugated cationic centers can be for example tetravalent nitrogen atoms which are conjugated ring members in an aromatic ring system. In one embodiment, each tetravalent nitrogen atom is a ring member in a separate aromatic ring system and two such ring systems, which can be of the same or different structure, are joined to one another directly through a covalent bond. Each such aromatic ring system can be a monocycle such as pyridine, pyrazine, or pyrimidine. Alternatively, each aromatic ring system can be a fused polycycle in which a pyridine, pyrazine, or pyrimidine ring is fused to one or more benzo or naphtho ring system, as for example quinolinium, isoquninolinium, phenanthridine, acridine, benz[ h ]isoquinoline, and the like. The two aromatic ring systems, which can be of the same or different structure, alternatively can be linked through a divalent conjugated system as for example diazo (-N=N-), imino (-CH=N-), vinylene, buta-1,3-diene-1,4-diyl, phenylene, biphenylene, and the like. In a further embodiment, the two conjugated cationic centers can be in a single aromatic system such as phenanthroline, 1,10-diazaanthrene, and phenazine. Typical dicationic structures suitable as Z thus include 2,2-bipyridinium, 3,3-bipyridinium, 4,4-bipyridinium, 2,2-bipyrazinium, 4,4-biquinolinium, 4,4-biisoquninolinium, 4-[2-(4-pyridinium)vinyl]pyridinium, and 4-[4-(4-pyridinium)phenyl]pyridinium. The aromatic systems in which the two conjugated cationic centers are located can be unsubstituted or substituted, as for example with alkyl of 1 to 6 carbon atoms or alkoxy of 1 to 6 carbon atoms. Such substitution can be inert or can have an effect on the reduction potentials of the cationic centers sterically or through induction. While the two cationic centers must be linked through conjugation, the entire system comprised by Z need not be conjugated. Thus Z can be joined to each of Y 1 O 3 and Y 2 O 3 through a conjugated or non-conjugated bridge. Hence one highly desirable structure for Z is characterized by the structure: IV -(R 1 ) n -Z'-(R 2 ) m - in which Z' is a divalent aromatic group containing at least two conjugated tetravalent nitrogen atoms; each of n and m, independently of the other, has a value of 0 or 1; and each of R 1 and R 2 , independently of the other, is a divalent aliphatic or aromatic hydrocarbon group. Typically each of n and m will be 1 and each of R 1 and R 2 , independently of the other, will be a straight or branched divalent alkane chain of six or less carbon atoms, as for example methylene, ethano, trimethylene, propane-1,2-diyl, 2-methylpropan-1,2-diyl, butane-1,2-diyl, butane-1,3-diyl, tetramethylene, and the like. The group X is an anionic group one or more of which (depending on the value of k and the charge of X) will balance the cationic charges of Z. and result in a net positive valence of Me Y being equal to (4-p*q). The precise nature of X is relatively unimportant and X can be for example a halogen anion such as chloride, bromide, iodide, a pseudohalide, sulfate, sulfonate, nitrate, carbonate, carboxylate, etc . The group W is an anionic group one or more of which (depending on the metal ion, Me 1 , used) will result in a net positive valence of Me Y being equal to (4-(p*q)). The precise nature of W is relatively unimportant and W can be for example a halide, a pseudohalide, hydroxy, etc. Each complex depicted by Formula III is bound to the substrate through the depicted linking means; the piurality of -L-Y 1 O 3 -Z-Y 2 O 3 Me Y units on the substrate, thereby produces a pillared structure. Each complex can contain one Z-containing unit ("pillar"), in which case k has a value of 1, but preferably k has a value in excess of 1 so that the unit -(Y 1 O 3 -Z-Y 2 O 3 )Me Y - becomes the monomer of the pillared polymeric complex in which k ranges from 2 to about 100, typically from about 5 to about 50. This multilayered structure can be illustrated by the formula: Such films can be prepared through sequential adsorption reactions analogously to those described by Rong et al., Coordination Chemistry Reviews, 97 , 237 (1990). The synthetic method and stoichiometry used can effect and detennine the resulting configuration and morphology of the compositions. A process uses a template of an organic polymer as a linking means for binding the compositions/films to the surfaces of hydrophobic substrates (e.g., quartz, silicon and metals). These polymer templates are derivatized with phosphonate or arsonate groups, for example, by treating epoxide groups pendant to the polymer backbone with phosphoric acid to yield pendant phosphates. The hydrophobic polymer template is adsorbed at the surface of the hydrophobic substrate leaving the hydrophilic phosphonate/arsonate groups free for cross-linking. These pendant phosphonate or arsonate groups are cross-linked with ions of the divalent, trivalent, or tetravalent metal of Group III, IVA, IVB having an atomic number of at least 21 or of a lanthanide which form a first metal layer. These polymer templates show good adhesion to the substrate surface, and a yield a highly porous structure (especially on metal substrates). The polymer can be any polymer having side chains which are capable of being derivatized with phosphonate or arsonate groups. A preferred polymer is polyvinylpyridine in which a fraction, preferably less than one half, of the pyridyl groups have been alkylated with X(CH 2 ) n PO 3 H 2 , where X is an anion and where n can be 0 to 10, preferably 2 to 4, (abbreviated PVP-C n P). A. polymer backbone which has pendent thiol groups, is preferred for enhanced binding to Au, Ag, and Pt substrates. In another process, the substrate can be the polymer template itself. Films grown on the polymer template are grown in solution. The hydrophobic properties of the polymer backbone cause the polymer in solution to aggregate into sheet form, with the pendant hydrophillic phosphonate or arsonate groups extending out into the solution, resembling lipid bilayers. This structure can be illustrated by the formula: Colloidal particles of a Group VIII metal, preferably platinum, can be present in the solution. The hydrophobic properties of the aggregate of the polymer backbone attracts the particles. The particles are then trapped within the hydrophobic environment between polymer backbones. This structure can be illustrated by the formula: In either case, the substrate, having a surface rich in phosphonate or arsonate groups then is treated with a reagent providing Me 3 ions, e.g ., zirconyl chloride. The metal ions bind to, and effectively cross-link, the phosphonate or arsonate groups, in turn producing an intermediate having a metal rich surface and characterized as "substrate-L'-Me 3 " in which L'-Me 3 corresponds to linking means, L, of Formula III, providing a means which ( I ) on the one hand binds to the substrate and ( ii ) on the other presents a metal Me 3 for further complexing. Formation of Layers The substrate-L is then separated from the reagent providing Me 3 ions, washed with water, and treated with a solution of a bisphosphonic acid or bisarsonic acid of the formula: XIII . H 2 Y 1 O 3 -Z-Y 2 O 3 H 2 •2X' in which Y 1 , Y 2 , Z, and X' are as defined above. This reaction is complete within a few hours, as for example about 4 to 5 hours, and can be accelerated through the use of moderate heat, as for example from about 80 to about 100°C. The deposition of this layer can be readily monitored spectrophotometrically at wavelengths of from about 260 to about 285 nm. For consistency, generally the range of 280-285 nm is employed. One of the -Y 1 O 3 H 2 and -Y 2 O 3 H 2 groups binds to the metal rich surface, while the other remains uncoordinated, thereby now producing an intermediate having a surface rich in phosphonate or arsonate groups. This intermediate can be depicted as: XIV . substrate-L'-Me 3 -Y 1 O 3 -Z-Y 2 O 3 H 2 •2X' The substrate-L'-Me 3 -Y 1 O 3 -Z-Y 2 O 3 H 2 •2X' is removed from the solution of the bisphosphonic acid or bisarsonic acid, rinsed thoroughly, and then treated with a reagent providing Me 1 ions to produce a complex of Formula III in which k is 1. The foregoing sequence of the last two synthetic steps, that is treatment with a bisphosphonic acid or bisarsonic acid followed by treatment with a reagent providing Me 1 ions, is repeated to produce complexes having higher k values. Absorbance, as for example at 280-285 nm. appears to increase linearly with the number of layers and provides a convenient method of monitoring the formation of multilaminar compositions. The foregoing procedure is readily and preferably modified to entrap atoms of at least one Group VIII metal, as for example platinum, palladium, iron, cobalt, nickel, ruthenium, rhodium, osmium, or iridium, at zero valence within the complexes. Thus following treatment with a bisphosphonic acid or bisarsonic acid but before treatment with a reagent providing Me 1 ions, the sample is immersed in an aqueous solution of a soluble anionic salt of the Group VIII metal. After a short time, the metal anion exchanges with some of the chloride anions in the sample. The stoichiometries of this exchange will depend upon the respective valences of the two anions. The platinum tetrachloride and platinum hexachloride anions, for example, each have a valence of -2 and if chloride were the starting anion, one anion of either of these metal anions would exchange for two chloride anions. Following this exchange, treatment with a reagent providing Me 1 ions then is performed as described above. As above, these reactions are repeated until the desired k value is attained. The composite is then simply exposed to hydrogen gas which reduces the metal anion to produce the metal in a zero valence state and colloidal form within the matrix of the composite. As noted previously, such materials are highly effective as catalysts in the production of hydrogen peroxide, the oligomerization of methane to form higher hydrocarbons, the decomposition of water to yield hydrogen gas, and the sensing of oxygen. The compositions also can be utilized to reduce various organic substrates. When growing the layered compounds on a polymer template as the substrate, the above processes are generally followed, however, the sequential treatment steps are separated by dialysis steps to remove unused reactants; not by rinsing. It is possible to utilize more than one Group VIII metal in any sample, either using soluble salts of different Group VIII metals in one or more exchanges or conducting one or more exchanges with a first Group VIII metal and subsequent exchanges with a different Group VIII metal. Thus created upon eventual reduction are unique compositions in which colloidal particles of two Group VIII metal having different chemical and electronic properties are entrapped in a single matrix. One preferred composition of these layered metal phosphonate compounds, where Z is a viologen, was found to be very efficient at collecting solar radiation and converting that into stored chemical energy. The active wavelengths for this process are in the ultraviolet portion of the spectrum. The energy storage reaction is evidenced by a deep blue color developing in the solid, which persists for long periods of time in the air. This blue color is due to a reduced viologen compound. Reduced viologen reacts rapidly with oxygen when prepared in solution, but is not reactive in the solid because it is trapped inside the dense solid. Oxygen and other external agents are unable to gain access to the reactive interior layers of the solid. The following examples will serve to further typify the nature of the invention but should not be construed as a limitation on the scope thereof which is defined solely by the appended claims. EXAMPLE 1 Diethyl 2-bromoethylphosphonate (25 g) and 4,4' bipyridine (7.35 g) in 125 mLs of water are refluxed for three days. An equal volume of concentrated hydrochloric acid is added and reflux continued for several hours. The solution is concentrated to 120 mLs by atmospheric distillation and 550 mL of isopropanol are added dropwise with stirring while chilling the mixture in an ice bath. The solid which forms is collected by vacuum filtration and washed with cold isopropanol to yield 1,1'-bisphosphonoethyl-4,4'-bipyridinium dichloride. ( 1 H NMR (D 2 O) 9.1(d), 8.5(d), 4.2(m), 2.0(m) ppm; 13 C NMR(D 2 O) 151, 147, 128, 58, 30 ppm; 31 P NMR(D 2 O) 17.8 (s) ppm; IR (KBr) 3112, 3014, 1640, 1555, 1506, 1443, 1358, 1281, 1175, 1112, 1020, 936, 816, 485 cm - 1.) In a similar fashion, utilizing 2.2-bipyridinium, 3,3-bipyridinium, 2,2-bipyrazinium, 4,4-biquinolinium, 4,4-biisoquninolinium, 4-[2-(4-pyridinium)vinyl]pyridinium, and 4-[4-(4-pyridinium)phenyl]pyridinium, there are respectively obtained 1,1'-bisphosphonoethyl-2,2-bipyridinium dichloride, 1,1'-bisphosphonoethyl-3,3-bipyridinium dichloride, 1,1'-bis-phosphonoethyl-2,2-bipyrazinium dichloride, 1,1'-bisphosphonoethyl-4,4-biquinolinium dichloride, 1,1'-bisphosphonoethyl-4,4-biisoquninolinium dichloride, 1-phosphonoethyl-4-[2-(1-phosphonoethyl-4-pyridinium)vinyl]pyridinium dichloride, and 1-phosphonoethyl-4-[4-(1-phosphonoethyl-4-pyridinium)phenyl]pyridinium dichloride. Other cationic species, such as the corresponding dibromides or disulfates are obtained by substituting the corresponding acids, such as concentrated hydrobromic acid or sulfuric acid, for hydrochloric acid in the procedure of this example. EXAMPLE 2 Synthesis of phosphonate derivatized Polymer template: Diethyl-4-bromobutylphosphonate was made by the Michealis-Arbuzov Rearrangement of Br(CH 2 ) 4 Br with triethyl phosphite. 1, 4- dibromobutane (21.5 g, 100 mmol) and triethylphosphite (6.65 g, 40 mmol) were heated to 150°C for 6 hours. Unreacted 1,4-dibromobutane was removed by vacuum distillation. Poly(4-vinylpyridine) (PVP) was alkylated with diethyl 4-bromobutyl phosphonate to give polymers (PVP-C 4 P). PVP (1 g, 9.5 mmol) was dissolved in 60 mL N, N-dimethyl formamide (DMF) with 1.48 g (5.4 mmol) of diethyl-4-bromobutylphosphonate. The mixture was stirred at 60°C for two hours, and DMF was removed under vacuum. The remaining solid was washed with a 1:4 (v:v) mixture of methanol and diethyl ether, and then refluxed in ether for two hours. The solid sample was filtered and dried. The dried sample was then dissolved in 30 mL methylene chloride, 12 g of bmmotrimethylsilane was added and the mixture was stirred for 6 hours under an Ar atmosphere. H 2 O (80 mL) was added and the solution was stirred one more hour. The water phase was separated, and removed under vacuum to get yellow-brown solid (PVP-C 4 P). CHN analysis of PVP-C 4 P gave C : 55.76, H : 6.67, N : 8.20. This analysis is consistent with 25% of the pyridyl groups being alkylated. [C 7 H 7 N] 3 [C 11 H 17 NO 3 PBr]*3H 2 O would give a CHN analysis of C : 55.57, H : 6.41, N : 8.10. The NMR spectra of PVP-C 4 P consists of relatively broad lines, due to the polymeric nature of the material. Three broad appear in the 1H NMR spectrum in d6-DMSO/D 2 O at 8.2, 6.6 and 1.6 ppm, with integrated intensities of 1, 1, and 2.4. This ratio is consistent with the 25% derivitization if the two downfield peaks are assigned to pyridyl/pyridinium resonances and the peak at 1.6 ppm is assigned to all of the CH 2 groups except the one bound to nitrogen (based on model compounds the latter peak is expected to fall under HDO), since this should give a ratio of 1 : 1 : 2.3. EXAMPLE 3 Platinum colloids were prepared via reduction of hexachloroplatinate solution by sodium citrate. The reduction was similar to that described by Brugger, et. al., except that the temperature was held at 90°C in order to get uniform particle size (P. Brugger, P. Cuendet, M. Gatzel, J. Am. Chem. Soc., (1981), 103, page 2923.) K 2 PtCl 6 (40 mg) was dissolved in 300 mL distilled water and the solution was heated to 90°C. An aqueous solution of sodium citrate (30 mL, 1 % weight percent sodium citrate) was added and the solution stirred for 3 hours. After the colloid suspension was cooled to room temperature, Amberlite-MB-1 exchange resin was added and the mixture was stirred to remove the excess citrate until the conductivity of the solution was less than 5 m S/cm. EXAMPLE 4 Growth of zirconium viologen-bisphosphonate (ZrVP) on PVP-C 4 P: Polymer PVP-C 4 P (5 mg) was dissolved in 50 mL of the Pt colloid suspension described above. The weight ratio of Pt : polymer is 1 : 2.5. After the mixture was shaken for one hour to reach equilibrium, 0.3 gm of ZrOCl 2 • 8H 2 O was dissolved in the PVP-C 4 P/Pt suspension. The mixture was shaken at room temperature overnight in order to complete the reaction of Zr 4+ ions with phosphonate groups of the polymer . The mixture was then dialyzed against distilled water to remove free ions. The molecular weight cut of the dialysis tube used here was 12,000 - 15,000. Dialysis was carried out until conductivity of the water was less than 5 mS/cm. The suspension was poured back to a flask, 0.04 g viologen bisphosphonic acid was added and the mixture was shaken at 60°C overnight, a similar dialysis process was carried out to a conductivity of less than 5 mS/cm. The zirconium and bisphosphonate treatments were repeatedly performed up to five times in order to grow multiple layers of the ZrVP materials. EXAMPLE 5 Photochemical Hydrogen Generation: Photochemical hydrogen generation was carried out by irradiating samples of the polymer templated ZrVP on Pt colloids (Example 34) in EDTA solutions. The suspension was held in a 1 cm square cell kept at 20°C throughout the photochemical experiment. A mixture of 4 mL of the sample suspension and 1 mL of 0.1 M NaEDTA (sacrificial reducing agent) were thoroughly degassed by bubbling N 2 through the suspension prior to photolysis. The sample was then irradiated with a 200 Watt Hg/Xe arc lamp. Levels of hydrogen were measured by GC. Photolysis of a suspension sample with 11 mg ZrPV(CI) in 0.05 M NaEDTA by a 200-w Hg/Xe lamp leads to a hydrogen production rate 0.25 mL/hr for the first hour. EDTA is used as a sacrificial reductant to turn the system over. The rate of hydrogen production gradually decrease on longer irradiation time. This is similar to that on multi layer thin films grown on silica surface. Passing the light through a 260 nm cutoff filter decreases the rate of hydrogen production by about 50%, but produces about 20% more hydrogen in longer period of time. The wave length dependence for photoproduction of hydrogen in this system correlates well with that observed in forming charge-separated state in both microcrystalline and thin film sample of ZrPV(Cl). EXAMPLE 6 Sample and substrate preparation.. Polymer PVP-C 4 P (molecular weight = 100,000) was synthesized from poly(4-vinylpyridine) and diethyl,4-bromobutyl-phosphonate by the method described in Example 32. H 2 O 3 PCH 2 CH 2 (bipyridinium)CH 2 CH 2 PO 3 H 2 Cl 2 (V2P) was prepared as described in Example 1. Single-crystal polished silicon wafers and microscopic fused silica (quartz) slides (∼ 1x3 cm 2 ) and 0.05 - 0.1 mm thick gold, platinum and palladium foil (∼1x0.5 cm 2 ) were each used as substrates. They were cleaned before use with a mixture of concentrated H 2 SO 4 and 30% H 2 O 2 (v/v 3:1), rinsed thoroughly with distilled water and heated at 500°C overnight to provide a dehydroxylated surface. Surface initialization procedure. A silicon wafer, quartz slide or metal foil strip was dipped into an aqueous 0.5% (w/w) solution of PVP-C 4 P. After 5 minutes, the slide was removed from the solution and dried by blowing pure N 2 . A thin layer of 80 mM solution of ZrOCl 2 was applied to the surface of the slide to achieve the cross-linking of phosphonic acid residues of polymer , and the film was air-dried. To make sure that the polymer was fully cross-linked with Zr 4+ ions, the process was repeated twice. The slide was then washed with distilled water to remove extra ions from surface. Film growth. Multilayers of ZrPV(CI) compound were produced on the zirconium rich surfaces by repeated dipping of the initialized substrate in 10 mM V2P aqueous solution at 80°C for 4 hours (step 1), then in 60 mM ZrOCl 2 aqueous solution at room temperature for 2 hours (step 2). The surface was thoroughly rinsed with distilled water between dippings (step 3). Steps 1-3 constituted one cycle of treatment. Various films were made by repeating up to 15 cycles. In the last cycle step 2 was usually omitted. EXAMPLE 7 Atomic force microscopic (AFM) images were obtained with NanoScope III Scanning Probe Microscope (Digital Instruments). Surface was imaged in a tapping mode with silicon cantilevers (typical F o 320-360 kHz). AFM images (0.5x0.5 µm2) of the samples reveal their finer features and demonstrate that the structure and thickness of the films prepared in the same way depends on the nature of the substrate. All of the samples showed a significant increase in RMS roughness on film growth. Examination of the AFM images shows that in all case the materials growing on the surface consist of microcrystallites. It is in contrast to the growth of Zn and Cu alkanebisphosphonate mutlilayer films (Yang, H. C., K. Aoki, H.-G. Hong, D. D. Sackett, M. F. Arendt, S.-L. Yau, C. M. Bell, T. E. Mallouk J. Am. Chem. Soc. 1993, 115, 11855-11862.) which results in the smoothing of surface roughness. The crystals are smaller in the case of quartz and silicon substrates and larger in the case of metals. There seems to be no direct correlation between the overall roughness of the film and the crystal size, as well as between the roughness of the bare substrate and of the film on it. The films on quartz consist of small crystals uniformly distributed on the surface. Films on gold and platinum are made up of somewhat larger crystals than those on quartz, but they are still uniformly distributed on gold and tend to aggregate into larger clusters on platinum. Growth of films on Pd leads to large crystals, which appear clustered into even larger islands. In contrast, films on silicon consist of very small particles, which also cluster into large islands. No differences were observed in the AFM images of untreated and PVP-C 4 P treated substrates. EXAMPLE 8 Cyclic voltammograms (CV) were registered at Au, Pt and Pd electrodes (working surface area ∼ 0.3 cm 2 ) covered with ZrPV(Cl) films as described above in Examples 36-37. PAR Potentiostat/Galvanostst Model 283 was used. A counter electrode (Pt wire) was separated from the working aqueous 0.1 M KCl solution by a porous glass frit. The reference was a saturated calomel electrode (SCE). Oxygen was removed from the working solution by bubbling with argon gas of high purity. Cyclic volmmmograms of the ZrPV(CI) films at the Au, Pt and Pd electrodes show broad peaks with reduction potentials (E o / surf =(E p.c + E p,a )/2, where E p.c and E p.a are the cathodic and anodic peak potentials, respectively) close to -0.77 V, with peak-to-peak separations (ΔE) of 120 - 200 mV. ΔE is slightly affected by the number of treatments on gold and platinum but shows no change for palladium. This large ΔE increasing as the experimental time scale is shortened (at higher potential scan rates) indicates the kinetic limitations for charge transfer which are more serious for anodic processes and for Pt and Pd electrodes. Integration of the reduction peaks at the cyclic voltammograms confirm that the amount of ZrPV(Cl) accumulated at the surface after the same number of treatments is different for different substrates. Much more material is being accumulated at Pt and Pd than at Au. These results are consistent with the AFM data indicating that films at Pt and Pd are more rough than at Au. Estimates based on the integrals obtained from the cyclic voltammograms indicate that every cycle of treatment results not in a single layer coating but adds 3-6 layers depending on substrate. The E o / surf values are 100 mV more negative than E o for the one-electron reduction of V2P in aqueous solution which we found to be -0.67 V (ΔE = 70 mV), which is close to the redox potential reported for the methylviologen dication/cation radical redox couple (-0.69 V). The 100 mV shift of E o / surf to the more negative values in films as compared to V2P in solution is not significantly affected by the number of times the substrate is treated with the Zr 4+ and viologen bisphosphonate. EXAMPLE 3 Blue color due to photochemical charge separation is observed on the layered ZrPV(Cl) with polysoap template, if the sample is photolyzed with a 200 w Hg/Xe lamp in vacuum or under N 2 . Five minute photolysis leads to the formation of both reduced viologen monomer and dimmer on the irradiated sample. Electron spectra show the decreasing band of 270 nm, and appearance of bands at 405, 605 nm and 380, 540 nm, which are correspond to monomer and dimmer respectively. The electronic spectra of the ZrPV(CI) with polysoap template, as well as the air sensitivity of the photoreduced sample suggest that this multilayered compound is not as tightly packed as microcrystalline samples of ZrPV(CI). Treating of a photoreduced suspension sample of layered ZrPV(CI) with template with air leads to complete bleaching within a matter of seconds, while the microcrystalline samples require hours to days. Oxygen appears to freely diffuse through the more open lattice of the compound. This is probably related to the flexible blanket-like feature of the materials with template.

Claims: A derivatized polymer characterized by the repeating unit having the formula: wherein: P is phosphorus or arsenic ; and n is 0 to 10.

Inventors: JOSHI VIJAY, SNOVER JONATHAN LEE, TANG XIAOZHANG, THOMPSON MARK E, VERMEULEN LORI ANN, JOSHI, VIJAY, SNOVER, JONATHAN, LEE, TANG, XIAOZHANG, THOMPSON, MARK, E., VERMEULEN, LORI, ANN
Applicants: JOSHI VIJAY, SNOVER JONATHAN LEE, TANG XIAOZHANG, THOMPSON MARK E, UNIV PRINCETON, VERMEULEN LORI ANN, JOSHI, VIJAY, SNOVER, JONATHAN LEE, TANG, XIAOZHANG, THE TRUSTEES OF PRINCETON UNIVERSITY, THOMPSON, MARK E., VERMEULEN, LORI ANN
Application year: 1995
Main classification: C08F8
IPC codes: C08F8, B01J31, C01B15, C08F30