HIGH-IMAGE-SHARPNESS RESIN-COATED METAL SHEET EXCELLENT IN ADHESION AFTER WORK

Abstract: In a resin-coated metal sheet, at least one surface of a metal sheet 10 as a base sheet is overlaid by a transparent polyester resin film A of 5 to 100 µm thickness, through a paint layer E, a modified olefin resin layer D of 5 to 100 µm thickness, a pattern or/and solid printing layer C and an adhesive layer B which layers are put one over another in order from the side of the metal sheet toward the transparent polyester resin film. Since the modified olefin resin layer which is provided in between the transparent polyester resin film and the metal sheet has the excellent adhesiveness against the printing layer, the paint layer and the polyester resin film, even if the resin-coated metal sheet is formed under the severe condition against the resin-coated metal sheet, for instance, by deep drawing, delamination does not occur so that the excellent workable adhesion strength is shown. Further, the roughness of the surface of the metal sheet, and unevenness of several component resin layers are absorbed by a modified olefin resin layer so that the excellent vivid relectivity for a resin-coated metal sheet can be obtained.

Description: The present invention relates to a resin-coated metal sheet with higher vivid reflectivity having excellent workable adhesion strength, in particular, to a resin-coated metal sheet with higher vivid refelectivity having excellent workable adhesion strength in which even if the resin-coated metal sheet is formed under severe conditions, for instance, by stretch-forming of the resin-coated metal sheet or by deep-drawing thereof, delamination does not occur so that excellent workable adhesion strength is shown. Recently, decorative design of a higher grade is being pursued, together with higher grade articles such as domestic electrical machinery and apparatus, audio, kitchen appliance, and interior finish materials. Decorative design of a higher grade is expressed by the decorativeness of the surface of packing materials, in particular, the higher vivid reflectivity. Further, decorative design can be expressed by the shape of package which is formed by stretch-forming of the resin-coated metal sheet or by deep-drawing thereof. Accordingly, the requirement for a decorative steel sheet with higher vivid reflectavity having a workable adhesion strength fit for stretch-forming of the resin-coated metal sheet or by deep-drawing thereof is increasing. In order to satisfy the requirement, various researches were made. For instance, there was proposed a method of laminating a colored metal sheet with a transparent thermosetting resin film or thermoplastic resin film of 5 to 100 µm and a thermoplastic resin film of 5 to 50 µm thickness having H to 7B hardness as disclosed in Japanese Patent Publication (Kokai) 55126 of 1991 (Heisei 2). EP-A-0,031,701 discloses laminated members comprising a metal foil or sheet and a thermoplastic resin film bonded together with an adhesive consisting of a carboxyl group-containing polyolefin. The thermoplastic resin film may be a single resin film of a thickness of 10 to 1,000 microns produced from polyester. The vivid refelectivity can be obtained by the above-mentioned method. However, since delamination occurs in the interface between two resin component layers or the interface between laminated resin layer and colored metal sheet, the workable shape of the decorative metal sheet is limited. Namely, in the prior art, it was extermely difficult to obtain a laminated metal sheet which has a workability fit for stretch-forming of the resin-coated metal sheet or by deep-drawing thereof whilst retaining the vivid reflectivity. It is an object of the present invention to provide a resin-coated metal sheet which has a workable adhesion strength fit for stretch-forming of the resin-coated metal sheet or by deep-drawing thereof, and excellent vivid reflectivity. 66676.611 The present invention provides a resin-coated metal sheet comprising, in order, a metal sheet as a base sheet, a modified polyolefin resin layer of 5 to 100 µm thickness, an adhesive layer comprising polyester resin, epoxy resin, acrylic resin, melamine resin or urethane resin, and a transparent polyester resin film of 5 to 100 µm thickness, wherein one surface or both surfaces of the metal sheet is/are overlain by said modified polyolefin resin layer, adhesive layer and polyester resin film in order. Preferred embodiments may comprise a paint layer between the metal sheet and the modified polyolefin resin layer, and a printing layer, comprising at least one of a solid or a pattern, between the modified polyolefin resin layer and the adhesive layer. In a further preferred embodiment, the resin-coated metal sheet may comprise, in order, a paint layer and a printing layer comprising at least one of a solid or a pattern, between said metal sheet and said modified polyolefin resin layer. In another preferred embodiment, the resin-coated metal sheet comprises a paint layer between the metal sheet and the modified polyolefin resin layer. In these resin-coated metal sheets of the present invention, the paint layer is preferably formed as a top coat layer of the transparent polyester resin film. Further, in these resin-coated metal sheets of the present invention, the adhesive layer and/or the printing layer desirably includes aluminium pigment or mica pigment. Since the modified polyolefin resin layer which is provided in between the transparent polyester resin film and the metal sheet has the excellent adhesiveness against the printing layer, the paint layer and the polyester resin film, even if the resin-coated metal sheet is formed under severe conditions, for instance by deep drawing, delamination does not occur so that the excellent workable adhesion strength is shown. Further, the roughness of the surface of the metal sheet, and unevenness of several component layers (resin layers) are absorbed by the modified polyolefin resin layer so that the excellent vivid relectivity for a resin-coated metal sheet can be obtained. Further, since the paint layer is formed as the top coat layer (what is called "top coat") of the transparent polyester resin film, scratch resistance of the resin-coated metal sheet required when the resin-coated metal sheet is formed or handled can be improved. In the accompanying drawings: Figures 1 to 3 are sectional views showing the structure of one side of a resin-coated metal sheet according to the present invention. Embodiments of the present invention are explained in detail below. Figs 1 to 3 show the structures of one side of resin-coated metal sheets having resin coating layers formed on a metal sheet, respectively. In the present invention, resin coating layers may be provided on both sides of a metal sheet, or only on one side of a metal sheet. The first embodiment of the present invention is explained in which resin coating layers are provided on one side of a metal sheet. Fig. 1 corresponds to a resin-coated metal sheet which is an embodiment of the invention recited in claim 1, in which "A" denotes transparent polyester resin film, "B" denotes adhesive layer, "C" denotes pattern and/or solid printing layer, "D" denotes modified olefin resin layer, "E" denotes paint layer, and "10" denotes metal sheet. In the embodiment of the present invention shown in Fig. 1, transparent polyester resin film A is 5 to 100 µm thick, which forms the outside layer of the resin-coated metal sheet. The thickness of transparent polyester resin film A is preferably 15 µm to 80 µm. When the thickness of transparent polyester resin film A is less than 5 µm, vivid reflectivity of the whole of the resin-coated metal sheet is inferior, and besides handling of transparent polyolefin resin film A in laminating is difficult. When the thickness of transparent polyester resin film A is more than 100 µm, the workable adhesion strength of the resin-coated metal sheet is inferior. In order to improve scratch resistance of the resin-coated metal sheet in forming it or in handling it, transparent polyester resin film A is preferably coated with a top coat of thermosetting paint or ultraviolet irradiated resin paint such as silicone resin paint, fluoride resin paint, acrylic resin paint, melamine resin paint or urethane resin paint of 0.2 µm to 50 µm thickness, in which the thickness of the top coat is more preferably 0.5 µm to 30 µm. When the thicknes of the top coat is less than 0.2 µm, the interference color is noticeably seen, and besides cut resistance is inferior. On the other hand, when the thickness of the top coat is more than 50 µm, the workability thereof decreases, and besides the economical efficiency is inferior. Transparent polyester resin film A includes polyethylene terephthalate resin and copolymer thereof. Adhesive layer B contains resin such as polyester resin, epoxy resin, acrylic resin, melamine resin or urethane resin. Further, an adhesive assistant having an adhesive effect such as γ-glicidoxypropyl trimethoxysilane ( for instance, silane coupling agent made by Nippon Unicar Co., Ltd.) can be used as an ingredient in addition to the above-mentioned resin. The thickness of adhesive layer B is preferably 0.1 µm to 50 µ m, more preferably 0.5 µm to 30 µm. When the thickness of adhesive layer B is less than 0.1 µm, the boiling water resistance and the workable adhesion strength of the resin-coated metal sheet are inferior. On the other hand, when the thickness of the adhesive layer is more than 50 µm, disfigurement of the external appearance of resin-coated metal sheet is caused by residual solvent which adhesive has when the laminate film is heated for laminating. Thereby, the vivid reflectivity of resin-coated metal sheet becomes inferior. Adhesive layer B can contain pigment such as aluminium powder or mica powder too. In this case, the ratio of aluminium pigment to solid matter in adhesive is preferably 0.1 % by weight to 30 % by weight, more desirably 1 % by weight to 20 % by weight, because when the ratio of aluminium pigment to solid matter in adhesive is less than 0.1 % by weight, metallic luster cannot be given, and when the ratio of aluminium pigment to solid matter in adhesive is more than 30 % by weight, the adhesive layer becomes fragile and besides the vivid reflectivity of resin-coated metal sheet becomes inferior. The particle of aluminium pigment has a globelike shape or scalelike shape. The average particle size thereof is preferably 0.1 µm to 100 µm, more desirably 1 µm to 80 µm, in either globelike particles or scalelike particles, because when the average particle size is less than 0.1 µm, the decorativeness of resin-coated metal sheet is worsened, and when the average particle size is more than 100 µm, the vivid reflectivity of resin-coated metal sheet becomes bad. The ratio of mica pigment to solid matter in adhesive is preferably about 0.1 % by weight to 30 % by weight, more desirably 1 % by weight to 20 % by weight, because when the ratio of mica pigment to solid matter in adhesive is less than 0.1 % by weight. metallic luster cannot be achieved, and when the ratio of mica pigment to solid matter in adhesive is more than 30 % by weight, the adhesive layer becomes fragile. The particles of mica pigment have a globelike shape or scalelike shape. The average particle size thereof is preferably 0.1 µm to 100 µm, more preferably 1 µm to 80 µm, in either globelike particles or scalelike particles, because when the average particle size is less than 0.1 µm, the decorativeness of resin-coated metal sheet is worsened, and when the average particle size is more than 100 µm, the vivid reflectivity of resin-coated metal sheet is worsened. The pattern or/and solid printing layer C comprises a pattern printing layer and/or solid printing layer to give decoration to the resin-coated metal sheet. Resin for pattern or/and solid printing layer C includes polyester resin, epoxy resin, acrylic resin, melamine resin or urethane resin. Polyester resin is particularly preferable, since when polyester resin is used, the workable adhesion strength of the resin-coatad metal sheet is higher. When the printing layer is a pattern printing layer, the thickness of printing layer is preferably 1 µm to 5 µm, because when the thickness of printing layer is less than 1 µm, the printing pattern cannot come out well, and when the thickness of printing layer is more than 5 µm, solvent of printing ink remains in the printing layer C by which variations in the vivid reflectivity of resin-coated metal sheet are generated. When the printing layer C is a solid printing layer, the thickness of the printing layer is preferably 1 µm to 5 µm, because when the thickness of the printing layer is less than 1 µm, variations in coloring tone of the printing layer are generated, and when the thickness of the printing layer is more than 5 µm, variations in the vivid reflectivity of resin-coated metal sheet are generated, and besides it is not economical. The printing layer can contain aluminium pigment or mica pigment too, in which the ratio of pigment to solid matter in printing ink is preferably 0.1 % by weight to 30 % by weight, more desirably 1 % by weight to 20 % by weight, in the same manner as the above-mentioned ratio of pigment to solid matter in the adhesive layer. Modified polyolefin resin layer D is 5 µm to 100 µm thick, which is the essential element of the present invention for providing the excellent workable adhesion strength and the high vivid reflectivity to the resin-coated metal sheet. The modified polyolefin resin is produced by blending propylene copolymer having a carboxyl group within a molecule with polypropylene in the following ratio: polypropylene copolymer 100 parts by weight to 20 parts by weight, and polypropylene 100 parts by weight to 0 parts by weight. The thickness of modified polyolefin resin layer D is preferably 10 µm to 80 µm, more preferably 20 µm to 70 µm. When the thickness of modified polyolefin resin layer D is less than 5 µm, the vivid reflectivity of the whole of resin-coated metal sheet is lowered, and when the thickness of modified polyolefin resin layer D is more than 100 µm, the surface hardness and the workable adhesion strength of the whole of resin-coated metal sheet is lowered. The modified polyolefin resin includes polyolefin polymer having at least one functional group selected from the group consisting of hydroxyl group, hydrolyzable group, carboxyl group, and acid anhydrous group within the molecule, or a mixture of the polyolefin polymer with other polyolefin polymer. One or more kinds of pigment may be mixed in the modified polyolefin resin layer. Further, it is preferable to apply an anchor coat on an upper side or a bottom side or both sides of the modified polyolefin resin layer by using silane coupling agent and others in order to improve adhesive strength of between resin layers. The above mentioned transparent polyester resin film A, adhesive layer B, printing layer C and modified polyolefin resin layer D are together called a "Laminate film". Paint layer E shown in Fig. 1 is provided for forming a color layer which is directly formed on a metal sheet as a design. Resin for paint includes polyester resin, acrylic resin, urethane resin, epoxy resin or melamine resin as chief ingredients. it is preferable that polyester resin is used as chief ingredients in particular, because the workable adhesion strength is extremely good. The thickness of the paint layer is preferably 1 µm to 50 µm, more preferably 5 µm to 30µm. Further, paint layer E includes a paint layer formed of two or more layers. Namely, the paint layer E may include a laminate formed of plural layers having an under coating including rust preventing pigment. For instance, a first layer as an under coating layer may be formed of color paint, and a second layer laid on the under coating layer may be formed of clear paint. The metal sheet 10 as a base sheet shown in Fig. 1 includes steel sheets, stainless steel sheet, and surface treated steel sheets such as galvanized sheet iron, composite galvanized sheet iron, nickel-plated steel sheet and tin-free steel. Further the metal sheet 10 may include nonferrous metal sheets such as aluminium sheet and copper sheet. The thickness of the metal sheet 10 is preferably 0.2 mm to 1.2 mm. When one side of the metal sheet 10 is coated with resin, a bottom layer of the metal sheet 10 (namely, a side of the metal sheet 10 which is not coated with resin) is favorably coated with rust proofing paint of 0.1 µm to 50 µm thickness, and further the bottom layer is preferably coated with polyvinyl chloride for rust proofing. Paint resin including, as a principal component, resin such as polyester resin, acrylic resin, polyurethane resin, epoxy resin, or melamine resin is suitable. Fig. 2 corresponds to the invention as claimed in claim 4. "A" is transparent polyester resin film, "B" is adhesive layer, "C" is pattern or/and solid printing layer, "D" is modified olefin resin layer, "E" is paint layer, and "10" is metal sheet. This embodiment differs from the first embodiment shown in Fig. 1 in that pattern or/and solid printing layer C and modified polyolefin resin layer D are exchanged with each other in the order of laminating. Namely, in the resin-coated metal sheet as described in Claim 4, printing layer C is formed between paint layer E and modified polyolefin resin layer D. In this case, transparent modified polyolefin resin layer is used as modified polyolefin resin layer D so as to give vivid reflectivity to a design of printing layer C formed thereunder so that pattern of printing layer C can be seen from outside. Fig. 3 corresponds to an invention as described in claim 5, in which "A" is transparent polyester resin film, "B" is adhesive layer, "C" is modified olefin resin layer, "D" is paint layer, and "10" is metal sheet. This embodiment differs from the second embodiment of Fig. 2 in that printing layer C does not exist in the laminate film. In this case, the appearance of paint layer D can be observed from above of transparent polyester resin film A. A method of producing a resin-coated metal sheet (1) Production of painted steel sheet Coating of galvanized sheet iron with resin paint is made by roll coating one time or two times, in which when the thickness of paint layer is needed to be increased, further times of painting are increased. (2) Production of a laminate film An instance of production of a laminate film shown in Fig. 1 is explained below. First, adhesive is painted on polyester resin film by roll coating to form an adhesive layer. After drying, a pattern is printed on the adhesive layer. Further according to demand, solid printing is made thereon. Or there is a case where patten printing is omitted and only solid printing is made. Modified polypropylene resin layer is formed over the printing layer by extrusion coating to form a laminate film. (3) Overlay After the painted steel sheet is heated, the painted steel sheet is overlain by the laminate film by means of a laminating roll, and then the painted steel sheet overlain by a laminate film is further heated, and pressed by means of a mirror roll. Thereafter the painted steel sheet overlain by the laminate film is cooled. In this time, the suitable roll pressure of the laminating roll is 1 kg/cm 2 to 80 kg/cm 2 , and more desirably 5 kg/cm 2 to 60 kg/cm 2 . When the roll pressure is less than 1 kg/cm 2 , the laminate film cannot be brought into close contact with the painted steel sheet uniformly over the width of the painted steel sheet so that the variations in the apprearance ( vivid reflectivity ) can be found. On the other hand, when the roll pressure is more than 80 kg/cm 2 , the abrasion of the roll occurs heavily so that the exchange of laminating roll should be made frequently, therefore, the productivity being decreased. (Example 1) (Production of painted steel sheet) Polyester copolymer paint including white pigment was painted on Galvanized sheet iron having 0.5 mm thickness, 10 g/m 2 galvanizing amount, 0.05 mg/dm 2 chromate film layer (as amount of chromium ) and average surface roughness Ra of 0.3 µ m, with thickness 15 µm and made thermoset to form a painted steel sheet. (Production of a laminate film) Polyester resin adhesive was painted on a transparent polyethylene terephthalate film of 25 µm thickness which was previousely top-coated with polyester resin of 5 µm thickness ( film-protective layer ), with thickness 1 µm, and then a grain pattern was printed thereon by using polyester resin ink, with thickness 1 µm. Thereafter, transparent modified polypropylene resin layer ( consisting of a mixture of 100 parts by weight of polypropylene copolymer with 100 parts by weight of polypropylene) of 20 µm thickness was formed on the printed side of the polyethylene terephthalate film by extrusion coating to form a laminate film. (Overlay) The painted steel sheet was overlaid by the laminate film in an atmosphere of 200 °C, under the roll pressure of 20 kg/cm 2 . As a result, the numerical value indicating the vivid reflectivity of the resin-coated metal sheet was 0.8 and good, and workable adhesion strength thereof was excellent. (Comparative example 1) A painted steel sheet was produced in the same manner as in Example 1, and then overlaid by the following laminate film. Namely, polyester resin adhesive was painted on transparent polyethylene terephthalate film of 25 µm thickness, with thickess 1 µm, and then a grain pattern was printed on the adhesive layer, with thickness 1 µm by using polyester resin ink to form a laminate film. Then, the painted steel sheet was overlaid by the laminate film to form a resin-coated metal sheet in the same manner as in Example 1. As a result, the workable adhesion strength of the resin-coated metal sheet was good, however the numerical value indicating the vivid reflectivity thereof was 0.1, bad and poor. (Example 2) A painted steel sheet produced in the same manner as in Example 1, and then overlaid by the following laminate film. Namely, polyester resin adhesive was painted on one side of transparent polyethylene terephthalate film of 100 µm thickness, with thickness 5 µm. Then transparent modified propylene resin layer of 100 µm thickness was formed on the painted side of the polyethylene terephthalate by extrusion coating. And then the grain pattern printing and the solid pattern printing were made in order on the modified propylene resin layer with each thickness 5 µm by using polyester resin ink to form a laminate film. Then, the painted steel sheet used in Example 1 overlaid by the laminate film in an atmosphere of 200 °C under the roll pressure of 20 kg/cm 2 , by which a resin-coated metal sheet having the vivid reflectivity was formed. This resin-coated metal sheet had the vivid reflectivity of 1.0 and the excellent workable adhesion strength. (Comparative example 2) A painted steel sheet was produced in the same manner as in Example 1, and then overlaid by the following laminate film. Namely, polyester resin adhesive was painted on a transparent polyethylene terephthalate film of 100 µm thickness, with thicness 5 µm. Then, a transparent polypropylene resin layer of 100 µm thickness was formed on the polyethylene terephthalate film by extrusion coating. Then the grain pattern printing and the solid printing were made in order on the propylene resin layer, with each thickness 5 µm, by using polyester resin ink to form a laminate film. Then the painted steel sheet was overlaid by the laminate film in the same manner as in Example 1 to form a resin-coated metal sheet. As a result, the numerical value of the vivid reflectivity of the resin-coated metal sheet was 0.8 and good. However, the workable adhesion strength thereof was bad and poor. (Comparative example 3) A painted steel sheet was produced in the same manner as in Example 1, and overlaid by the following laminate film. Namely, silane coupling agent was painted on one side of a transparent polyethylene terephthalate film of 12 µm thickness, with thickness 0.5 µm. Then, solid printing was made thereon by using polyester resin ink including mica pigment, with thickness 4 µ m. Transparent propylene resin layer of 5 µm thickness is formed on the printed side of the polyethylene terephthalate film by exrusion coating to form a laminate film. Then the painted steel sheet was overlaid by the laminate film in the same manner as in Example 1 to form a resin-coated metal sheet. As a result, the numerical value indicating the vivid reflectivity of the resin-coated metal sheet was 0.7, and good. However, the workable adhesion strength was bad and poor. (Example 3) A painted steel sheet was produced in the same manner as in Example 1, and then overlaid by the following laminate film. Namely, Polyester resin adhesive including aluminium pigment was painted on one side of a transparent polyethylene terephthalate film of 50 µm thickness, with thickness 50 µm. Then transparent modified polypropylene resin of 50 µm thickness was formed thereon by extrusion coating to form a laminate film. Then, the painted steel sheet used in Example 1 was overlaid by the laminate film in an atmosphere of 200°C, under the roll pressure of 20 kg/cm 2 to form a resin-coated metal sheet with vivid refelectivity. The numerical value indicating the vivid reflectivity of the resin-coated metal sheet was 0.7, and the workable adhesion strength was excellent. (Comparative example 4) A painted steel sheet was produced in the same matter as in Example 1, and then overlaid by the following laminate film. Namely, polyester resin adhesive including aluminium pigment was painted on one side of a transparent polyethylene terephthalate film of 50 µm thickness, with thickness 50 µm. Then, a transparent polypropylene resin layer of 50 µm thickness was formed thereon by extrusion coating to form a laminate film. Then, the painted steel sheet was overlaid by the laminate film in the same manner as in Example 1 to form a resin-coated metal sheet. As a result, the numerical value indicating the vivid reflectivity of the resin-coated metal sheet was 0.7 and good. However the workable adhesion strength thereof was bad and poor. (Method of valuation) (Vivid reflectivity) The vivid reflectivity of the resin-coated metal sheet of the present invention was measured by the following method. Namely, the vivid reflectivity of reflected image, namely the vivid reflectivity of normal reflected image on decorative surface of resin-coated metal sheet was measured by means of a portable distinctness of image glossmeter PGD-4 type ( made by Japan Color Research Institute ). The higher the measured value is, the higher the vivid reflectivity is. A method of measurement was as follows. Namely, a resin-coated metal sheet of 10 cm × 10 cm was pushed against the glossmeter horizontally, and scale of the glossmeter was read with naked eyes as the vivid reflectivity. (Workable adhesion strength) In the present invention, valuation of workable adhesion strength was made by taking the following two measurements and judging the results thereof synthetically. (1) Erichsen test Checkered cuts reaching a base metal are made in a resin-coated surface of resin-coated metal sheet by a cutter knife, and 8 mm stretch-forming of the resin-coated metal sheet was made from the backside of the resin-coated metal sheet by Erichsen tester. Thereafter, the extent of delamination was valuated by heating continuousely the resin-coated metal sheet at 100 °C for one hour and thereafter observing the existing of delamination. In Table No. 1, the mark " o ○ " designates "no delamination", and the mark " × " designates "delamination". (2) Cup-deep drawing test Deep drawing of a resin-coated metal sheet into a cup was made by Yamada-way deep drawing tester, with drawing ratio r = 2.2. Checkered cuts reaching the base metal were made in a resin surface of the resin-coated metal sheet formed into a cylindrical part of cup, with a space of 5 mm. Thereafter, the extent of delamination was evaluated by heating continuously the resin-coated metal sheet formed into a cup by deep drawing and thereafter observing the existence of delamination. In Table 1, the mark " o ○" designates "no delamination", and the mark "×" designates "delamination". As apparent from Table 1 and 2, since modified polyolefin resin layer included in a laminate film has excellent adhesion strength with printing layer, paint layer, polyester resin film and others, even if severe work such as deep drawing is made, delamination between layers does not occur. Therefore, the resin-coated metal sheet of the present invention has excellent workable adhesion strength. Further, since surface roughness and convex and concave parts of each layer ( resin layer ) are absorbed by modified polyolefin resin layer, resin-coated metal sheet of the present invention has excellent vivid reflectivity for a resin-coated metal sheet.

Claims: A resin-coated metal sheet comprising, in order, a metal sheet as a base sheet, a modified polyolefin resin layer of 5 to 100 µm thickness, an adhesive layer comprising polyester resin, epoxy resin, acrylic resin, melamine resin or urethane resin, and a transparent polyester resin film of 5 to 100 µm thickness, wherein one surface or both surfaces of the metal sheet is/are overlain by said modified polyolefin resin layer, adhesive layer and polyester resin film in order. A resin-coated metal sheet as claimed in claim 1 further comprising a top-coat on said transparent polyester resin film, said top-coat comprising thermosetting paint or ultraviolet irradiated resin paint. A resin-coated metal sheet as claimed in claim 1 or claim 2 comprising a paint layer between said metal sheet and said modified polyolefin resin layer, and a printing layer, comprising at least one of a solid or a pattern, between said modified polyolefin resin layer and said adhesive layer. A resin-coated metal sheet as claimed in claim 1 or claim 2 comprising, in order, a paint layer and a printing layer comprising at least one of a solid or a pattern, between said metal sheet and said modified polyolefin resin layer. A resin-coated metal sheet as claimed in claim 1 or claim 2 comprising a paint layer between said metal sheet and said modified polyolefin resin layer. A resin-coated metal sheet as claimed in any of claims 1 to 5, wherein the adhesive layer includes aluminium pigment. A resin-coated metal sheet as claimed in any of claims 1 to 6, wherein the adhesive layer includes mica pigment. A resin-coated metal sheet as claimed in any of claims 1 to 5, wherein the printing layer includes aluminium pigment. A resin-coated metal sheet as claimed in any of claims 1 to B, wherein the printing layer includes mica pigment.

Inventors: MINAMIGI TAKASHI, NAKAMOTO TETSUO, SUGIMOTO YOSHIYUKI, MINAMIGI, TAKASHI, NAKAMOTO, TETSUO, SUGIMOTO, YOSHIYUKI
Applicants: TOYO KOHAN CO LTD, TOYO KOHAN CO., LTD
Application year: 1995
Main classification: B32B15
IPC codes: B32B15