Epoxy resin system

Abstract: An amine curing agent composition for an epoxy resin is provided having low volatility and good processability containing a) a polyamine curing agent and b) an aliphatic alcohol-alkylene oxide adduct. An epoxy resin-polyamine curing agent system containing an aliphatic alcohol-alkylene oxide adduct is also provided.

Description: This invention relates to diluent-containing amine curing agent and epoxy resin systems. In US-A-4,715,970 a composition comprising a polyamide formed from the reaction of a neoacid with a triamine, and a Neodol alcohol ethoxylate is disclosed. The polyamides are preferably prepared by a reaction of neoacid with a polyamine, which preferably includes 2 to 5 amino group. The alcohol-alkylene oxide adduct, Neodol 25-7, is the condensation product of a C 12 -C 15 linear alcohol and an average of 7 moles of ethylene oxide per mole of alcohol. Preferred Neodol in the compositions is Neodol 25-3. Preferred proportions of the components of the composition are 5 to 20% by weight of polyamide and 5 to 20% by weight of Neodol. Sodium sulfate may also be present in compositions as an accelerator. In US-A-4,668,758 a composition is disclosed, comprising an epoxy resin, a cationic curing agent, and a diarylamine. A specific example of diarylamine is the aromatic amine N,N'-diphenyl-p-phenylenediamine. The composition contains 0.01-20 wt% diarylamine based on the weight of epoxy resin. The composition further comprises a surfactant Neodol 91-6 in a concentration of 0.01-10 wt% based on the weight of epoxy resin. The epoxy resin is a polyglycidylether of a polyhydric alcohol and as specific examples of cationic curing agents HBF 4 and H 2 SO 4 are mentioned. In DE-A-2106320 are disclosed epoxy resin coating compositions, having an improved pot-life and good film-forming properties, which comprise a water dilutable epoxy resin dispersion which can be cured at ambient temperature, and a hardener, which consists of modified non-phenol containing compounds of amines and fatty acid derivatives. The epoxy resin composition and/or the hardener has been dispersed by two emulsifiers, one of which is water-dispersible and the other is water-soluble. The hardener dispersion is preferably consisting of polyalkylenepolyamines, which have been converted with monomeric, dimerized or trimerized fatty acids, whereby the amine numbers are between 83 and 400 and preferably between 200 and 300. On the other hand, typical epoxy resin systems for coatings and certain civil engineering applications such as in structural and flooring applications contain benzyl alcohol as diluent. Generally the diluent is added to the curing agent for the epoxy resin. Benzyl alcohol is used as a diluent to lower viscosity of the epoxy resin system for ease of processing. However, a large fraction of the diluent such as benzyl alcohol evaporates from a coating, or other exposed layer of epoxy resins during cure, and thereby behaves as a volatile organic compound (VOC). Environmentally it is desirable to have low VOC content. It is therefore an object of the present invention to provide a diluent-containing epoxy resin system which has lower volatility than benzyl alcohol-containing epoxy resin systems while retaining their ease of processing. It has been found that aliphatic alcohol-alkylene oxide adducts are effective diluents for amine curing agents and mixtures of these curing agents with epoxy resins. The amine curing agent composition and/or the curable epoxy resin composition of the invention has lower volatility and higher flash points than the corresponding composition containing the conventional benzyl alcohol diluent while having viscosity in the same range. Further, the aliphatic alcohol-alkylene oxide adduct does not react with aliphatic amine groups at room temperature at a rate high enough to threaten shelf stability when used as a diluent for epoxy curing agents containing amine groups. According to the present invention an amine curing agent composition is provided comprising: (a) a polyamine selected from the group consisting of aliphatic amines, cycloaliphatic amines, adducts of amines with epoxy resins, and amido amines, and having at least 2 nitrogen atoms and at least 2 amine hydrogen atoms; and (b) from 1 to 300 weight percent, based on the polyamine, of an aliphatic alcohol-alkylene oxide adduct having the formula: R 1 ―(O―CR 2 R 3 ―CR 4 R 5 ) n ―OH wherein R 1 is a hydrocarbyl group having 7 to 22 carbon atoms, R 2-5 are independently hydrogen or C 1-4 alkyl groups and n is a number having an average value of 1 to 15. Further, there is also provided a curable epoxy resin composition comprising: (a) an epoxy resin; (b) a polyamine selected from the group consisting of aliphatic amines, cycloaliphatic amines, adducts of amines with epoxy resins, and amidoamines, and having at least 2 nitrogen atoms and at least 2 amine hydrogen atoms; and (c) from 1 to 300 weight percent, based on the polyamine, of an aliphatic alcohol-alkylene oxide adduct having the formula: R 1 ―(O―CR 2 R 3 ―CR 4 R 5 ) n ―OH wherein R 1 is a hydrocarbyl group having 7 to 22 carbon atoms, R 2-5 are independently hydrogen or C 1-4 alkyl groups and n is a number having an average value of 1 to 15. The polyamine can be any nitrogen-containing curing agent useful in curing epoxy resins. These polyamines typically have at least 2 nitrogen atoms per molecule and at least two reactive amine hydrogen atoms per molecule. The nitrogen atoms are linked by divalent hydrocarbyl groups. Other hydrocarbyl groups such as aliphatic, cycloaliphatic or aromatic groups may also be singly linked to some of the nitrogen atoms. These polyamines contain at least 2 carbon atoms per molecule. Preferably polyamines contain about 2 to about 6 amine nitrogen atoms per molecule, 2 to about 8 amine hydrogen atoms per molecule, and 2 to about 50 carbon atoms. Examples of the polyamines useful as a curing agent for epoxy resins include aliphatic polyamines such as ethylene diamine, diethylene triamine, triethylene tetramine, tetraethylene pentamine, pentaethylene hexamine, dipropylene triamine, tributylene tetramine, hexamethylene diamine, dihexamethylene triamine, 1,2-propane diamine, 1,3-propane diamine, 1,2-butane diamine, 1,3-butane diamine, 1,4-butane diamine, 1,5-pentane diamine, 1,6-hexane diamine, 2-methyl-1,5-pentanediamine, 2,5-dimethyl-2,5-hexanediamine and the like; cycloaliphatic polyamines such as isophoronediamine, 4,4'-diaminodicyclohexylmethane, menthane diamine, 1,2-diaminocyclohexane, 1,4-diaminocyclohexane, and diamines derived from "dimer acids" (dimerized fatty acids) which are produced by condensing the dimer acids with ammonia and then dehydrating and hydrogenating; adducts of amines with epoxy resins such as an adduct of isophoronediamine with a diglycidyl ether of a dihydric phenol, or corresponding adducts with ethylenediamine or m-xylylenediamine; araliphatic polyamines such as 1,3-bis(aminomethyl)benzene; aromatic polyamines such as 4,4'methylenedianiline, 1,3-phenylenediamine and 3,5-diethyl-2,4-toluenediamine; amidoamines such as condensates of fatty acids with diethylenetriamine, triethylenetetramine, etc.; and polyamides such as condensates of dimer acids with diethylenetriamine, triethylenetetramine, etc. Some commercial examples of polyamines include EPI-CURE Curing Agent 3140 (EPI-CURE is a trademark) (a dimer acid-aliphatic polyamine adduct), EPI-CURE Curing Agent 3270 (a modified aliphatic polyamine), EPI-CURE Curing Agent 3274 (a modified aliphatic polyamine), EPI-CURE Curing Agent 3295 (an aliphatic amine adduct), EPI-CURE Curing Agent 3282 (an aliphatic amine adduct), EPI-CURE Curing Agent 3055 (an amidoamine), EPI-CURE Curing Agent 3046 (an amidoamine) and EPI-CURE Curing Agent 3072 (modified amidoamine), and EPI-CURE Curing Agent 3483 (an aromatic polyamine) available from Shell Chemical Company. Mixtures of polyamines can also be used. In the aliphatic alcohol-alkylene oxide adduct of the general formula: R 1 ―(O―CR 2 R 3 ―CR 4 R 5 ) n ―OH R 1 is preferably a hydrocarbyl group having 8 to 18 carbon atoms, R 2-5 are preferably hydrogen and n is preferably a number having an average value of from 1 to 5. The hydrocarbyl group can optionally be substituted with groups inert to the amine curing agent such as, for example, other hydrocarbyl groups or alkoxy, aryloxy, alkylthio, arylthio, amino groups and the like. If the value of n is low such as 1, the adduct will tend to have poor solubility in epoxy resins, especially if the number of carbon atoms in R 1 is high such as greater than 22. If the value of n is high such as greater than 16, resin solubility of the adduct may be excellent but the adduct will have less power to reduce system viscosity. The preferred hydrocarbyl group is a linear alkyl group in which the substituent is bound to a primary carbon atom of the alkyl chain R 1 although aliphatic alcohol-alkylene oxide adducts in which the ether substituent is bound to a secondary carbon atom of the alkyl chain are also considered to be within the scope of this invention as well as any mixtures thereof. Aliphatic alcohol-alkylene oxide adducts in which branching occurs within the alkyl chain are also considered to be within the scope of the present invention. The preferred aliphatic alcohol-alkylene oxide adduct is an alcohol ethoxylate, an alcohol propoxylate or a mixture thereof. Some aliphatic alcohol ethoxylates useful in the present invention include, but are not limited to those described in U.S. Patent No. 4,474,678. The aliphatic alcohol-alkylene oxide adduct of formula II may be made by any conventional process known in the art including, but not limited to, the processes described in U.S. Patent No. 4,474,678. Such processes typically consist of the sequential addition of alkylene oxide to the corresponding alkanol (ROH) in the presence of a catalyst. Some commercial examples of the alcohol-alkylene oxide adduct include NEODOL alcohol ethoxylates (NEODOL is a trademark) (from Shell Chemical Company) such as NEODOL 91-2.5, NEODOL 91-6, NEODOL 45-2.25, NEODOL 45-7, NEODOL 45-13, NEODOL 25-3, NEODOL 25-9, NEODOL 25-12, NEODOL 1-5, NEODOL 23-3 and NEODOL 23-1 ethoxylates, NEODOL alkoxylates containing propoxylate groups such as NEODOL 375 propoxylate, DOBANOL alkoxylates (DOBANOL is a trademark of Shell International Petroleum Company, Ltd.), and Tergitol alcohol alkoxylates (Tergitol is a trademark) (Union Carbide). The aliphatic alcohol-alkylene oxide adduct is present in an amount effective to dilute the amine curing agent or the epoxy resin system to obtain a processable viscosity which is generally less than 50,000 centipoise or 50 Pa.s (at 25 °C), preferably within the range of 3000 centipoise to 10 centipoise. It can be appreciated that when the curing agent or the epoxy resin system is handled or processed at higher temperature the viscosity can be lower, which range is within the scope of the invention. The aliphatic alcohol-alkylene oxide adduct is typically present in an amount of from about 1 weight percent, preferably from 3 weight percent, more preferably from 5 weight percent to 300 weight percent, preferably to about 200 weight percent, more preferably to 150 weight percent, based on the polyamine. The polyamine and the aliphatic alcohol-alkylene oxide adduct are blended or mixed with any kind of blender, stirrer or mixer to give an intimate mixture. An accelerator can be included to increase the cure rate of the epoxy resin-curing agent system. Various amine-compatible accelerators can be used as long as they are soluble in the amine curing agents. Examples of accelerators include metal salts such as, for example, sulfonates, phosphonates, sulfates, tetrafluoroborates, carboxylates and nitrates of Groups IA, IIA and transition metal series of the Periodic Table (CAS version), preferably Mg, Ca, Zn and Sn salts, and complexes thereof; inorganic acids such as, for example, HBF 4 , H 2 SO 4 , H 2 NSO 3 H and H 3 PO 4 ; carboxylic acids, preferably hydroxy-substituted carboxylic acids such as, for example, salicylic, lactic, glycolic and resorcylic; phenolic compounds such as, for example, phenol, t-butylphenol, nonylphenol and bisphenol A; imidazoles; cyanamide compounds such as dicyandiamide and cyanamide; sulfonamides such as, for example p-toluenesulfonamide, methanesulfonamide, N-methylbenzenesulfonamide and sulfamide; and imides such as, for example, phthalimide, succinimide, perylenetetracarboxylic diimide and saccharin. When the cure rate at the desired temperature is suboptimal, it is preferable to include the accelerator. For example, for adhesive applications and civil engineering applications where application at low temperature is desired, it may be preferable to include the accelerator. It is particularly preferable to include the accelerator if the amine groups are hindered or the concentration of amine groups is low. The accelerators are typically present in an amount of from 0, preferably from 0.1 weight percent to 10 weight percent, preferably to 5 weight percent, based on the epoxy resin. More preferable accelerators for the invention include, for example, calcium alkylbenzenesulfonates, dicyandiamide, calcium nitrate, magnesium alkanesulfonates, tetrafluoroboric acid, salicylic acid, phenol, dichloroacetic acid, trifluoroacetic acid, and mercaptoacetic acid. The curable epoxy resin composition of the invention contains an epoxy resin, a polyamine, an aliphatic alcohol-alkylene oxide adduct and optionally an accelerator. The aliphatic alcohol-alkylene oxide adduct, the polyamines and the accelerators are described above. The epoxy resin can be any epoxy resin which can be cured by the amine curing agent. Generally, the epoxy resin can be any curable epoxy resin having a 1,2-epoxy equivalency greater than one and preferably, on the average, more than 1.5 epoxide groups per molecule. The epoxy resin can be saturated or unsaturated, linear or branched, aliphatic, cycloaliphatic, aromatic or heterocyclic, and may bear substituents which do not materially interfere with the curing reaction. Such substituents can include bromine. They may be monomeric or polymeric, liquid or solid, but are preferably liquid at room temperature. Suitable epoxy resins include glycidyl ethers prepared by reacting epichlorohydrin with a compound containing at least one hydroxyl group carried out under alkaline reaction conditions. Examples of epoxy resins suitable for use in the invention include polyglycidyl ethers of polyhydric compounds, epoxy novolacs or similar polyphenolic resins, polyglycidyl ethers of glycols or polyglycols, and polyglycidyl esters of polycarboxylic acids. Preferably the epoxy resin is a polyglycidyl ether of a polyhydric phenol. Polyglycidyl ethers of polyhydric phenols can be produced, for example, by reacting an epihalohydrin with a polyhydric phenol in the presence of an alkali. Examples of suitable polyhydric phenols include: 2,2-bis(4-hydroxyphenyl) propane (bisphenol-A); 2,2-bis(4-hydroxy-3-tert-butylphenyl) propane; 1,1-bis(4-hydroxyphenyl) ethane; 1,1-bis(4-hydroxyphenyl) isobutane; bis(2-hydroxy-1-naphthyl) methane; 1,5-dihydroxynaphthalene; 1,1-bis(4-hydroxy-3-alkylphenyl) ethane and the like. Suitable dihydric phenols can also be obtained from the reaction of phenol with aldehydes such as formaldehyde (bisphenol-F). Fusion products of these polyglycidyl ethers of polyhydric phenols with phenolic compounds such as bisphenol-A are also suitable as epoxy resins, such as those described in U.S. Patent Nos. 3,477,990 and 4,734,468. Commercial examples of preferred epoxy resins include, for example, EPON Resins DPL-862, 828, 826, 825 and 1001 available from Shell Chemical Company. The preferred epoxy resin systems of the invention for structural applications contain epoxy resins based on or containing diglycidyl ethers of dihydric phenols, a curing agent containing an aliphatic polyamine (modified or not), and an aliphatic alcohol-alkylene oxide adduct diluent. The preferred epoxy systems of the invention for coating applications contain diglycidyl ethers of dihydric phenols, and/or the fusion products of the diglycidyl ethers of dihydric phenols with bisphenols, a curing agent containing a polyamide or a polyamidoamine, and an aliphatic alcohol-alkylene oxide adduct diluent. The epoxy resin can be blended or mixed with the diluent-containing amine curing agent or blended with the polyamine, the aliphatic alcohol-alkylene oxide adduct and optionally the accelerator simultaneously or in any order at a temperature below the cure temperature which is typically below 100 °C. The ratio of epoxy resin to polyamines is typically within the range of 10:90 to 90:10, more preferably 20:80 to 80:20 by weight percent. Further to facilitate handling or application or use in various environments, the amine curing agent or the epoxy resin system can be further diluted with minor amounts of aliphatic, aromatic or cycloaliphatic ketones or esters. The curable epoxy resin composition can be cured at a temperature within the range of from -40 °C, preferably from -10 °C, to 100 °C, preferably to 75 °C for a time effective to cure the epoxy resin. The epoxy resin composition of the invention may include other additives, such as fillers, elastomers, stabilizers, extenders, plasticizers, pigments, reinforcing agents, flow control agents and flame retardants depending on the application. The epoxy resin composition is useful for coatings and certain civil engineering applications such as for floor topping, grouts and adhesives. For coating applications, the curable epoxy resin composition can also contain pigments of the conventional type such as iron oxides, lead oxides, strontium chromate, carbon black, titanium dioxide, talc, barium sulfate, phthalocyanine blue and green, cadmium red, chromium green, lead silicate, silica, silicates and the like. Such pigments can be added to the polyamine curing agent component or the epoxy resin component prior to mixing them together. However, iron blue pigment, calcium carbonate and pigments considered reactive because of their basic nature are not compatible in the epoxy resin coating system when used in appreciable quantities. These normally are added to the curing agent component only. Defoamers, tints, slip agents, thixotropes, etc., are common auxiliary components to most coatings and may be employed in the epoxy resin composition of the present invention. It will be appreciated that another aspect of the present invention is formed by a substrate, coated with the curable epoxy resin composition as specified hereinbefore. The curable coating composition can be applied to a substrate by brush, spray, or rollers. One of the advantages of the coating system of the invention is the lower VOC content (i.e., from about 0 to about 20%) of the curable coating composition. For floor topping application, the curable epoxy resin composition can also contain a filler such as sand, other siliceous materials, iron or other metals. Small amounts of thixotropic agents, colouring agents, inert plasticizers, and levelling agents can also be incorporated in the curable epoxy resin composition if desired. These curable flooring compositions can be trowelled, sprayed or brushed onto a floor substrate. The following examples describe the process of the invention and are provided for illustrative purposes and are not meant as limiting the invention. Examples 1-5 demonstrate use of aliphatic alcohol-alkylene oxide adducts as diluents for amine curing agents, EPI-CURE-3140 curing agent (a condensate of dimerized fatty acid with an aliphatic polyamine from Shell Chemical Company), an adduct of isophoronediamine with EPON Resin 828 (from Shell Chemical Company), a cycloaliphatic amine curing agent, a modified araliphatic amine epoxy curing agent and a polyamide type epoxy curing agent, respectively, compared with benzyl alcohol as diluent. Examples 6 and 7 demonstrate use of aliphatic alcohol-alkylene oxide diluents with accelerators. Further, examples 2-7 demonstrate the epoxy resin systems of the invention. NEODOL alcohol ethoxylates mentioned in the examples below were obtained from Shell Chemical Company. NEODOL 91-2.5 alcohol ethoxylate (a linear alcohol ethoxylate mixture having an average of 2.7 ethoxylate groups and 9 to 11 carbon linear alcohol moiety). NEODOL 23-3 alcohol ethoxylate (a linear alcohol ethoxylate mixture having an average of 2.9 ethoxylate groups and 12 to 13 carbon linear alcohol moiety). TESTING METHODS Viscosity : Viscosities were measured at 25 °C using an Ubbelohde viscometer. Pot life : Pot life was determined in a Shyodu gel time apparatus using a 100 gram sample, starting at room temperature (approximately 20-22 °C). "Pot life" was time required for the probe to stop rotating. Gel Time : Gel time was determined in a thin film on a heated metal gel plate. An amount of resin (about 1 gram) was periodically touched with a wooden tongue depressor. "Gel time" was the time required for the curing mixture to stop being drawn up in fibrous strings when touched by the tongue depressor. Pencil Hardness : Pencil hardness was determined by ASTM D-3363 method. Direct Impact and Reverse Impact : Direct impact and reverse impact were determined by ASTM D-2794 method. Adhesion, Crosscut : Crosscut adhesion was determined by ASTM D-3359 method. Flexibility : Conical mandrel flexibility was determined by ASTM D-522 method. Dry Time : Dry time of films was determined by a Gardner circular dry time device with a probe moving through the coating as it dried overnight. Volatility (VOC CONTENT) : Volatility or VOC was determined by ASTM D-2369 method. Heat Distortion Temperature : Heat distortion temperature was determined by ASTM D-648 method. Tensile Strength, Modulus and Elongation : Tensile strength, modulus and elongation were determined by ASTM D-638 method. Flexural Strength and Modulus : Flexural strength and modulus were determined by ASTM D-790 method. Fracture Toughness : Fracture toughness was determined by ASTM E-399 method. Hardness : Hardness, shore "D" was determined by ASTM D-2240 method. EXAMPLE 1 Use of two aliphatic alcohol ethoxylates, NEODOL 91-2.5 ethoxylate and NEODOL 23-3 ethoxylate as diluents in comparison with benzyl alcohol for a dimer acid-aliphatic polyamine adduct curing agent, EPI-CURE 3140 curing agent, is demonstrated. EPI-CURE 3140 curing agent was blended with benzyl alcohol, NEODOL 91-2.5 and NEODOL 23-3 ethoxylates in the proportions indicated in Table 1 below. Kinematic viscosity of the mixtures was measured. EPI-CURE 3140 (parts) 50 50 50 50 50 50 Benzyl alcohol (parts) 5 10 NEODOL 91-2.5 (parts) 5 10 NEODOL 23-3 (parts) 5 10 Kinematic viscosity, (mm 2 /sec) 6750 3890 7350 4070 7050 4430 As can be seen from Table 1, the aliphatic alcohol ethoxylate diluents gave mixture kinematic viscosities almost as low as those provided by benzyl alcohol at equivalent diluent fraction. This was despite the fact that the kinematic viscosities of the aliphatic alcohol ethoxylates at 38 °C are 12 mm 2 /sec for NEODOL 91-2.5 ethoxylate and 13 mm 2 /sec for NEODOL 23-3 ethoxylate while the benzyl alcohol has a kinematic viscosity of 4.5 mm 2 /sec even at the much lower temperature of 30 °C. EXAMPLE 2 Use of NEODOL 91-2.5 and NEODOL 23-3 ethoxylates in comparison with benzyl alcohol as diluents in formulating a curing agent which is an adduct of isophoronediamine with EPON Resin 828 is demonstrated. A 1-litre, 4-neck round bottom flask was fitted with a paddle stirrer, an air condenser (topped by a connection to a nitrogen line through a Firestone valve), a thermocouple, and an addition funnel. To the flask were added 263.05 grams of isophoronediamine and 252.91 grams of the particular diluent used. To the addition funnel was added a mixture of 97.95 grams of EPON Resin 828 and 32.5 grams of the particular diluent used. The system was purged with nitrogen and the resin mixture was added to the amine mixture over approximately 30-45 minutes, with stirring. The mixture was heated to 82-90 °C and kept in this temperature range for 1 hour to bring the amine-epoxy reaction to near completion. The product was then poured into a glass bottle and stored for further characterization, as shown in Table 2 below. Diluent Benzyl Alcohol NEODOL 91-2.5 NEODOL 23-3 Diluent Properties : Kinematic viscosity (mm 2 /sec) 4.5(30 °C) 12(38 °C) 14(38 °C) Curing agent properties : Kinematic viscosity (mm 2 /sec) 328.5 472.2 500.7 Processing properties : Pot life, (min) 97.6 240.6 233.4 Thin film gel time (sec) 50 °C 3600 90 °C 570 1210 1250 120 °C 195 375 375 As can be seen from Table 2 above, the kinematic viscosity of the curing agents containing the alcohol ethoxylate diluents was not tremendously higher than that of the curing agent containing benzyl alcohol diluent. The alcohol ethoxylate containing systems were lower in reactivity than the benzyl alcohol-containing system, an advantage in some applications in which a long working life is needed. EXAMPLE 3 Use of NEODOL 23-3 ethoxylate in comparison with benzyl alcohol as diluent in a phenolic-accelerated formulated cycloaliphatic amine curing agent is demonstrated. A 1-litre, 4-neck round bottom flask was equipped as in Example 2. To the flask were added 221.40 grams of isophoronediamine. To the addition funnel were added 61.80 grams of EPON Resin 828. The system was purged with nitrogen and the resin was added to the amine over approximately 30-45 minutes, with stirring. The mixture was heated to 82-90 °C and kept in this temperature range for 1 hour to bring the amine-epoxy reaction to near completion. To the flask were added 144.00 grams of para-t-butylphenol and 172.80 grams of the particular diluent used. The mixture was heated to 82-90 °C and kept in this temperature range for 1 hour with stirring to yield a homogeneous mixture. The product was then poured into a glass bottle and stored for further characterization. The curing agents produced were characterized by using them to cure EPON Resin 828. For performance characterization, 1/8" (3.2 mm) thick castings were prepared in moulds formed from two pieces of 1/4" (6.4 mm) thick plate glass separated by a 1/8" (3.2 mm) thick polytetrafluoroethylene spacer. Film properties were visually characterized from 15 mil (0.38 mm) drawdowns cast over 1/4" (6.4 mm) thick plate glass. Results are shown in Table 3 below. Curing agent formulation: Isophoronediamine (pbw) 36.9 36.9 EPON Resin 828 (pbw) 10.3 10.3 NEODOL 23-3 (pbw) 28.8 Benzyl alcohol (pbw) 28.8 p-tert-Butylphenol (pbw) 24.0 24.0 Volatility, (% loss): Resin/curing agent blend 4.71 8.97 Curing agent 61.17 79.26 NEODOL 23-3 alone 23.52 Benzyl alcohol alone 99.31 Curing Agent properties: Viscosity (mPa.s) 1730 1340 Processing properties: Pot life (min) 35 23 Cured state properties: Heat distortion temperature (°C) 47 45 Tensile: Strength (MPa) 45 47 Modulus (GPa) 2.48 2.73 Elongation (%) 5.4 6.2 Flexural: Strength (MPa) 84 81 Modulus (GPa) 2.51 2.88 Fracture toughness (MPa-m 1/2 ) 0.64 0.70 Hardness (Shore "D") 69 72 Film properties: Film formation, 24 hr ambient cure Smooth film Smooth film Film clarity, 24 hr ambient cure Clear Clear Sweatout, 24 hr ambient cure None None Adhesion, 24 hr ambient cure Good Good Film clarity, 24 hr ambient cure plus 24 hour water soak Clear Clear Adhesion, 24 hr ambient cure plus 24 hour water soak Fair Good-Fair Solvent pickup (%) : Water, 24 hours 0.19 0.18 Water, 1 week 0.62 0.72 5% Acetic acid, 24 hours 0.47 0.31 5% Acetic acid, 1 week 1.39 0.91 Xylene, 24 hours 1.94 0.31 Xylene, 1 week 11.84 1.50 As can be seen from Table 3 above, substitution of NEODOL 23-3 ethoxylate for benzyl alcohol in the curing agent formulation produces a large decrease in the volatile organic compound fraction of the resin-curing agent mixture. There is little change in cured casting or film properties except for xylene pickup after long exposure. EXAMPLE 4 The use of NEODOL 91-2.5 ethoxylate and NEODOL 23-3 ethoxylate in comparison with benzyl alcohol as modifiers in the synthesis of modified araliphatic amine epoxy curing agents is demonstrated. To a four-necked flask equipped with a stirrer, a temperature controller, and a condenser, 2266.86 grams of meta-xylylenediamine (MXDA) and 896.3 grams of deionized water were charged under a nitrogen blanket. Acrylic acid (622.5 g) was metered into the reaction mixture at 43-46 °C over 90 minutes. The reaction temperature was maintained at 43-46 °C over the next two hours to complete the Michael addition reaction between MXDA and acrylic acid. The reaction mixture was then heated to 199 °C (heated slowly through the range 93-107 °C to facilitate the condensation reaction between the acid functionality of the acrylic acid and the residual amine functionality MXDA) to complete the condensation reaction. The base curative, was characterized to have the properties summarized in Table 4. Amine value (mg KOH/g) 495 Acid value (mg KOH/g) 1.88 Viscosity (Ubbelohde, Pa.s at 25 °C) 18.96 Colour (Gardner) <1 The base curative was cooled to 93 °C. The base curative (80 parts by weight) was blended with 20 parts by weight of benzyl alcohol, NEODOL 91-2.5 ethoxylate and NEODOL 23-3 ethoxylate respectively. These three modified araliphatic amine curative analogs were characterized to have the properties summarized in Table 5. As can be seen from the results in Table 5, the aliphatic alcohol-alkylene oxide adduct containing polyamine curing agents have lower volatile organic compound (VOC) content than the corresponding benzyl alcohol containing polyamine curing agent. Diluent Benzyl Alcohol NEODOL 91-2.5 NEODOL 23-3 Amine value (mg KOH/g) 394 397 396 Acid value (mg KOH/g) 0.65 0.74 0.80 Viscosity (Ubbelohde, Pa.s at 25 °C) 1.99 2.97 3.75 Volatility (% loss) 31.71 21.93 19.58 Colour (Gardner) <1 <1 <1 Gel time 27.3 40.5 37.1 Density (g/cm 3 ) 1.13 1.09 1.09 The curing agents produced were characterized by using them to cure EPON Resin 828. The EPON Resin 828, in amounts indicated in Table 6 below, was initially diluted with a 50:40:10 (by weight) mixture of xylene:methyl isobutyl ketone (MIBK):methyl n-amyl ketone (MnAK). The curing agent was then added to the diluted resin, followed by the 3M FC-430 flow control agent. After thorough mixing, the mixture was then diluted further with an amount of a 70:30 (by weight) mixture of xylene:n-butanol in order to achieve a Gardner-Holdt viscosity of D. The diluted mixture of resin and curing agent was then allowed to stand for a 10 minute induction period at room temperature. The mixture was then coated onto a set of 15 cold-rolled steel panels (prerinsed with isopropyl alcohol and then with methyl ethyl ketone) with a #25 drawdown bar. The resultant films were allowed to cure under ambient conditions and cured properties of the films (shown in Table 6 below) were determined after 24 hours and again after 7 days. Dry time was determined by a Gardner circular dry time device with a probe moving through the coating as it dried overnight. Dry time results are shown in Table 6 below. EPON Resin 828, grams 30 30 30 50 xylene: 40 MIBK: 10 MnAK, grams 5.76 5.76 5.76 Diluent in curing agent Benzyl alcohol NEODOL 91-2.5 NEODOL 23-3 Curing agent, grams 16.2 16.2 16.2 3M FC-430 (levelling agent), grams 0.115 0.115 0.115 70 xylene:30 n-butanol, grams 5.0 5.0 5.0 Film properties : Dry time (Gardner circular), hours: Channel formation begins 0.5 0.25 Clear channel (bare metal) 1.5 0.5 3.0 End of clear channel 3.0 1.0 4.0 End of surface rupture 4.5 2.0 End of surface scratching 5.5 4.0 18.0 Properties after 24 hours: Visual appearance Clear hard film Clear hard film Clear hard film Film thickness, mm 0.030-0.043 0.025-0.038 0.020-0.028 Pencil hardness (ASTM D-3363) 3H 2H 2H Properties after 7 days: Pencil hardness (ASTM D-3363) 3H 3H 3H Direct impact, J (ASTM D-2794) 3.2 3.6 2.7 Reverse impact, J (ASTM D-2794) 0.5 0.2 0.2 Adhesion, crosscut (ASTM D-3359) 5A 5A 5A Flexibility, conical mandrel (ASTM D-522), % elongation 32 32 32 Methyl isobutyl ketone resistance >120 min. pass/pencil #H >120 min. pass/pencil #H >120 min. pass/pencil #H As can be seen from the results in Table 6 above, cure behaviour (with the exception of Gardner circular dry time for the system modified with NEODOL 23-3 ethoxylate) and cured properties after 24 hours and 7 days are similar for the three systems, with no major differences due to the substitution of linear alcohol ethoxylates for benzyl alcohol. EXAMPLE 5 The use of NEODOL 91-2.5 ethoxylate and NEODOL 23-3 ethoxylate in comparison to benzyl alcohol as modifiers in the synthesis of a polyamide type epoxy curing agent is demonstrated. To a four-necked flask equipped with a stirrer, a temperature controller and a condenser, 469.2 grams of Z 4-1/4 dimer acid (dimerized fatty acid) and 869.1 grams of a crude mixture of monomeric and dimerized acids were charged under a nitrogen blanket. The monomer-dimer acid mixture was pre-warmed to 40 °C before charging. The reaction mixture was heated to 100 °C with moderate agitation. Triethylenetetramine (TETA) (561.6 grams) was metered into the reaction mixture at 100-120 °C over 1 hour. The reaction mixture was heated slowly to 210 °C with nitrogen sparging after onset of the condensation reaction between the acid and the amine. At 210 °C, the pressure inside the flask was gradually decreased from atmospheric to 13 kPa in order to increase the imidazoline content of the curative to a target value. The base curative was characterized to have the properties summarized in Table 7. Amine value (mg KOH/g) 336 Acid value (mg KOH/g) 1.2 Viscosity (Ubbelohde, Pa.s at 25 °C) 20.03 Colour (Gardner) 8-9 The base curative was cooled to 71 °C. The base curative (63.08 parts by weight) was blended with 31.93 parts by weight of benzyl alcohol, NEODOL 91-2.5 ethoxylate and NEODOL 23-3 ethoxylate respectively. Each of the above modified curatives was adducted with 5 parts by weight of EPON Resin 828 at 80 °C over 2 hours. The EPON Resin 828 was added to the reaction mixture at 40-50 °C and heated to 80 °C after a mild exotherm up to 60 °C. These three curative analogs were characterized to have the properties summarized in Table 8. As can be seen from the results in Table 8, the aliphatic alcohol-alkylene oxide adduct containing polyamine curing agents have lower volatile organic compound (VOC) content than the corresponding benzyl alcohol containing polyamine curing agent. Diluent Benzyl alcohol NEODOL 91-2.5 NEODOL 23-3 Amine value (mg KOH/g) 211 210 210 Acid value (mg KOH/g) 1.27 1.33 0.92 Viscosity (Ubbelohde, Pa.s at 25 °C) 3.88 5.85 7.10 Volatility (% loss) 32.85 12.90 8.90 Colour (Gardner) 7-8 7-8 7-8 Gel time 158 356 359 Density (g/cm 3 ) 1.003 0.962 0.961 The curing agents produced were characterized by using them to cure EPON Resin 1001 from Shell Chemical Company. The EPON Resin 1001 was used as EPON Resin 1001-CX-75, a 75% by weight solids solution of EPON Resin 1001 in a 65:35 (by weight) mixture of methyl isobutyl ketone (MIBK):xylene. This solution was further diluted with the amount indicated in Table 9 below of a 50:40:10 (by weight) mixture of xylene:methyl isobutyl ketone (MIBK):methyl n-amyl ketone (MnAK). The curing agent was then added to the resin solution, followed by the 3M FC-430 flow control agent. The diluted mixture of resin and curing agent was then allowed to stand for a 10 minute induction period at room temperature. The mixture was then diluted further with an amount of a 70:30 (by weight) mixture of xylene:n-butanol in order to achieve a Gardner-Holdt viscosity of D. The mixture was then coated onto a set of 15 cold-rolled steel panels (prerinsed with isopropyl alcohol and then with methyl ethyl ketone) with a #35 drawdown bar. The resultant films were allowed to cure under ambient conditions and cured properties of the films (shown in Table 9 below) were determined after 24 hours and again after 7 days. Dry time was determined by a Gardner circular dry time device with a probe moving through the coating as it dried overnight. Dry time results are also shown in Table 9 below. EPON Resin 1001-CX-75 (grams) 40 40 40 50 xylene:40 MIBK:10 MnAK (grams) 13.4 13.4 13.4 Diluent in curing agent Benzyl alcohol NEODOL 91-2.5 NEODOL 23-3 Curing agent (grams) 21 21 21 3M FC-430 (levelling agent) (grams) 0.254 0.254 0.254 70 xylene:30 n-butanol (grams) 14 16 16 Film properties : Dry time (Gardner circular), hours: Channel formation begins 0.5 1.0 0.75 Clear channel (bare metal) 1.0 2.0 3.5 End of clear channel 4.0 4.0 5.25 End of surface rupture 5.5 7.5 7.5 End of surface scratching 8.0 9.0 8.25 Properties after 24 hours: Visual appearance Clear hard film Clear hard film Clear hard film Film thickness, mm 0.025-0.030 0.030-0.036 0.025-0.033 Pencil hardness F HB HB Properties after 7 days: Pencil hardness 3H HB 2H Direct impact (J) ≥ 18.1 ≥ 18.1 17.2 Reverse impact (J) ≥ 18.1 ≥ 18.1 ≥ 18.1 Adhesion, crosscut 5A 5A 5A Flexibility, conical mandrel (% elongation) 32 32 32 Methyl isobutyl ketone resistance Failed at 15 minutes Failed at 15 minutes Failed at 15 minutes As can be seen from Table 9 above, cure behaviour and cured properties (with the exception, to some degree, of hardness) after 24 hours and 7 days are similar for the three systems, with no major differences due to the substitution of linear alcohol ethoxylates for benzyl alcohol. EXAMPLE 6 Use of a calcium sulfonate accelerator with NEODOL 91-2.5 ethoxylate in comparison with benzyl alcohol as diluent in formulating a curing agent which is an adduct of isophoronediamine with EPON Resin 828 is demonstrated. A 1-litre, 4-neck round bottom flask was equipped as in Example 2. To the flask were added 263.05 grams of isophoronediamine, 187.81 grams of NEODOL 91-2.5 ethoxylate and 65.2 grams of Ninate 401 (a product of Stepan Chemical, a liquid mixture of 65% calcium sulfonates (corresponding approximately to calcium dodecylbenzenesulfonate) and 35% of a solvent mixture). To the addition funnel was added a mixture of 97.95 grams of EPON Resin 828 and 32.5 grams of NEODOL 91-2.5 ethoxylate. The system was purged with nitrogen and the resin mixture was added to the amine mixture over approximately 30-45 minutes, with stirring. The mixture was heated to 82-90 °C and kept in this temperature range for 1 hour to bring the amine-epoxy reaction to near completion. The product was then poured into a glass bottle and stored for further characterization, as shown in Table 10 below. Curing agent formulation : Mixture from Example text above (pbw) 100 50 25 NEODOL 91-2.5 mixture from Table 2 (pbw) 50 75 100 Benzyl alcohol mixture from Table 2 (pbw) 100 Curing agent properties : Kinematic viscosity (mm 2 /sec) 1128 710.5 573.5 472.2 328.5 Processing properties : Kinematic viscosity (mm 2 /sec) 2700 1700 1600 1500 1350 Viscosity doubling time (min) 10 16 33 41 20 Pot life (min) 37.1 91.2 149.1 240.6 97.6 Thin film gel time (sec) 50 °C 2750 3575 6100 3600 90 °C 380 610 860 1210 570 120 °C 100 158 240 375 195 Volatility (% loss) : Resin/curing agent blend 2.4% 7.4% Cured properties : Shore D hardness (20 gram casting, 17 hours after mixing) 40-45 60-65 Thin film appearance (17 hours after mixing) Glossy but somewhat opaque Glossy and clear Thin film hardness (2 days after mixing) HB-H 2H As can be seen from Table 10 above, the curing agent with slightly over one-fourth of the NEODOL 91-2.5 ethoxylate replaced by Ninate 401 gave reactivity with EPON Resin 828 considerably higher than that of the curing agent containing benzyl alcohol, although the viscosity of the Ninate 401 blend was much higher. When the Ninate 401 concentration was cut in half, the reactivity of the resultant curing agent with EPON Resin 828 was about the same as that of the unaccelerated curing agent containing benzyl alcohol. Although the kinematic viscosity of the resultant curing agent containing NEODOL 91-2.5 ethoxylate and Ninate 401 was more than twice that of the unaccelerated curing agent containing benzyl alcohol, there was only a small difference in kinematic viscosity (1350 versus 1700 mm 2 /sec) between mixtures of the two curing agents with EPON Resin 828. EXAMPLE 7 Use of dicyandiamide accelerator with NEODOL 91-2.5 ethoxylates in comparison with benzyl alcohol as diluent in formulating a curing agent which is an adduct of isophoronediamine with EPON Resin 828 is demonstrated. To 1-pint bottles were added the proportions indicated in Table 11 below of isophoronediamine and dicyandiamide. The bottles were held in an 82 °C oven for approximately one hour to dissolve most of the dicyandiamide in the amine; placing the bottles on rollers overnight at room temperature completed the dissolution. To the resultant mixtures were added the proportions indicated in Table 11 below of EPON Resin 828 and NEODOL 91-2.5. The bottles were shaken until the mixtures were homogeneous (slight warming occurred as a result of the reaction exotherm). The mixtures were then allowed to stand at room temperature for 3 to 5 days. The curing agent products were then characterized as shown in Table 11 below. Curing agent formulation : Isophoronediamine (pbw) 40.47 40.47 40.47 40.47 EPON Resin 828 (pbw) 15.07 15.06 15.07 15.07 NEODOL 91-2.5 (pbw) 37.84 39.85 43.91 Benzyl alcohol (pbw) 43.91 Dicyandiamide (pbw) 6.07 4.05 Curing agent properties : Kinematic viscosity (mm 2 /sec) 1668 472.2 328.5 Amine value (mg KOH/g) 271.9 272.3 Processing properties : Kinematic viscosity (mm 2 /sec) 1500 1350 Viscosity doubling time (min) 41 20 Pot life, 100 gram mass (min) 74.9 101.0 240.6 97.6 Thin film gel time (sec) 50 °C 4410 5150 3600 90 °C 760 775 1210 570 120 °C 200 200 375 195 As can be seen from Table 11 above, dicyandiamide is also a relatively effective accelerator which can be used to give the curing agent diluted with NEODOL 91-2.5 ethoxylate a reactivity similar to that diluted with benzyl alcohol, at least in terms of pot life in a 100-gram mass. Dicyandiamide has an additional advantage of not increasing the colour of the curing agent.

Claims: An amine curing agent composition comprising: (a) a polyamine selected from the group consisting of aliphatic amines, cyclo aliphatic amines, adducts of amines with epoxy resins, and amido amines, and having at least 2 nitrogen atoms and at least 2 amine hydrogen atoms, and (b) from 1 to 300 weight percent, based on the polyamine, of an aliphatic alcohol-alkylene oxide adduct having the formula: R 1 ―(O―CR 2 R 3 ―CR 4 R 5 ) n ―OH wherein R 1 is a hydrocarbyl group having 7 to 22 carbon atoms, R 2-5 are independently hydrogen or C 1-4 alkyl groups and n is a number having an average value of 1 to 15. The composition of claim 1 wherein R 1 is a hydrocarbyl group having 8 to 18 carbon atoms. The composition of claim 1 or 2 wherein R 1 is a linear alkyl group. The composition of any of claims 1-3 wherein n is a number having an average value of 1 to 5. The composition of any of claims 1-4 wherein R 2-5 are all hydrogen. The composition of claim 1 further comprising an accelerator. A curable epoxy resin composition comprising: (a) an epoxy resin, (b) a polyamine selected from the group consisting of aliphatic amines, cyclo aliphatic amines, adducts of amines with epoxy resins, and amido amines, and having at least 2 nitrogen atoms and at least 2 amine hydrogen atoms, and (c) from 1 to 300 weight percent, based on the polyamine, of an aliphatic alcohol-alkylene oxide adduct having the formula: R 1 ―(O―CR 2 R 3 ―CR 4 R 5 ) n ―OH wherein R 1 is a hydrocarbyl group having 7 to 22 carbon atoms, R 2-5 are independently hydrogen or C 1-4 alkyl groups and n is a number having an average value of 1 to 15. The composition of claim 7 wherein the epoxy resin is a polyglycidyl ether of a polyhydric phenol. A substrate coated with the curable epoxy resin composition of claim 7.

Inventors: CORLEY LARRY STEVEN, GHOSH KALYAN, HUNTER JOE MICHAEL, KINCAID DEREK SCOTT, MEILUS LEO, WEINMANN DANIEL JAMES, CORLEY, LARRY STEVEN, GHOSH, KALYAN, HUNTER, JOE MICHAEL, KINCAID, DEREK SCOTT, MEILUS, LEO, WEINMANN, DANIEL JAMES
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1995
Main classification: C08L63
IPC codes: C08G59, C08L71, C08L63, C08L77