CARBOCATIONIC CATALYSTS AND PROCESS FOR USING SAID CATALYSTS

Abstract: A living carbocationic catalyst composition comprising an initiator of a tertiary alkyl halide, a tertiary aralkyl halide or polymeric halide a co-initiator of a methylaluminum or methylboron compound, and a solvent medium with a dielectric constant between 2.5 and 7 is used to produce narrow molecular weight distribution polymers particularly isobutylene polymers.

Description: CARBOCATIONIC CATALYSTS AND PROCESS FOR USING SAID CATALYSTS Field of the Invention This invention relates to the living polymerization of olefins using catalysts comprising alkylaluminum halides or alkyl boron halides. Background of the Invention: A variety of cationic catalysts are known to produce polymers out of olefin monomers in livi" * and nonhving polymerizations. In a living polymerization, each initiator molecul ; ates a growing polymer chain that does not undergo chain transfer or termr ι reactions while monom is present In some of these systems once th nomer is depleted the gπr g polymer chain undergoes an irreversible teπr. .tion reaction. In theory, th' jgh, if the chains did not terminate then addition of monomer would cause the polymer chain to grow regardless of the length of time between monomer additions. In reality however, this reversible termination has been difficult to produce for aluminum catalysts as later monomer additions grow unevenly to produce a broad molecular weight distribution. Such a distribution is the hallmark of a non-living system. Thus a living and termination system has heretofore not been strictly attained. It is an object of this inventio . .o provide such a terminationless living system with an alkyl aluminum catalyst Typical cationic catalysts such as titanium tetrachloride (TiCU), boron trichloride (BC13), tin tetrachloride(SnCl4), iron trichloride (FeCl3), aluminum trichloride (A1C13) systems and the like have been described in U.S. Patents 4,910,321 and 4,929,683, and EP-A-0341 012 for use in the living polymerization of olefins. The basic components of these systems include a Lewis acid, a tertiary alkyl imtiator molecule containing a halogen, ester, ether, acid or alcohol group and an electron done-' molecule such as ethyl acetate. The exact combination of the elements varies with each system. The tertiary alkyl initiators used in these systems are used for living and non-living carbocationic catalysts. The tertiary alkyl initiators are typically represented by the formula: wherein R\ , R2, and R3 are a variety of alkyl or aromatic groups or combinations thereof, n is the number of initiator (R3 R2 X) n molecules or initiator sites, typically 1 to 6, and X is the functional group which the Lewis acid ionizes to bring about the carbocationic initiating site. This group is typically a halogen, ester, ether, alcohol or acid group depending on the Lewis acid employed. One or two functional groups per initiator tend to lead to linear polymers while three or more tend to lead to star polymers. As discussed in U.S. 5,169,914, the chosen electron pair donor component of these systems direcdy relates to the ability of these catalysts to stabilize the carbocation formed and to generate living conditions. Electron pair donors have been defined as molecules capable of donating electron density to an electron deficient site. These molecules usually contain heteroatoms and heteroatomic functional groups including amides, ester, ethers, sulfoxides and the like. The electron donor number concept has been used to explain the activity of early catalyst systems which employ ether and ester initiators. It was believed that the formation of in situ electron pair donors were responsible for the catalyst characteristics. However, the role of the electron donor is still uncertain and has been challenged. See M Gyor, H. C. Wang, R. Faust J. Macromol. Sci. A2§, 639 (1992). Catalyst systems based on boron trichloride and titanium tetrachloride using various combinations of the above components typically have similar process characteristics. First, Lewis acid concentrations must exceed the concentration of initiator sites by 16 to 40 times in order to achieve 100 percent conversion in 30 minutes (based upon a degree of polymerization equal to 890) at -75 to -80 ° C. These catalyst systems are also typically used with solvents. For example, the references above disclose methyl chloride as a preferred solvent and that a mixed solvent may be used to avoid side reactions or to keep the polymer in solution. Further the mixed solvent should provide some degree of polarity to maintain the polymerization rate. However, even in these circumstances, an electron pair donor must be present. For an industrially applicable process these catalysts and polymerization conditions fall short of commercial usefulness. Improvements in these systems would include elimination of boron and titanium based Lewis acids as they present handling and purification problems. In addition, living systems also tend to require expensive proton scavengers to suppress initiation from unwanted protons, such as those from water contamination. In a preferred embodiment this invention also provides a system that achieves living polymerization in the absence of a proton scavenger or an electron donor pair. Summary of the Invention In accordance with this invention, there is provided a living carbocationic polymerization catalyst system comprising an imtiator of one of a tertiary alkyl halide, a tertiary aralkyl halide or a tertiary polymeric halide, wherein each alkyl is indepenc dy a straight or branched chain alkyl and each aralkyl is substituted or unsubstit d, a co-initiator of a methylaluminum or a ■ lethylboron compound, and a solvent .edium having a dielectric constant between about 2.5 rnd about 7. -Another aspect of the invention comprises a process of using this . atalyst system for the polymerization of olefins and for producing narrow molecular weight distribution polymers. Brief Description of the Drawmg Figure 1 is a plot of the Mn vs. conversion (%C) for living isobutylene polymerizations at varied dimethylaluminum chloride concentrations. Description of Preferred Embodiments, This invention relates to a living carbocationic polymerization catalyst composition and process based upon a catalyst composition comprising: ' 1 ) an initiator of a tertiary alkyl halide, a tertiary aralkyl halide or a tertiary pol αeric halide, wherein each alkyl group is independently a straight or branched chain alkyl, preferably containing 1 to 15 carbon atoms, each aralkyl is substituted or unsubstituted and wherein the polymeric unit is an olefϊn polymer; (2) a co-initiator of a methylaluminum or a methylboron compound; and (3) a solvent medium with a dielectric constant between about 2.5 and about 7. In a preferred embodiment, this invention provides a living carbocationic polymerization catalyst composition and process based upon a catalyst composition comprising: (1) an initiator of a tertiary alkyl halide, a tertiary aralkyl halide or a tertiary polymeric halide, wherein each alkyl group is independently a straight or branched chain alkyl, preferably containing 1 to 15 carbon atoms, each aralkyl is substituted or unsubstituted and wherein the polymeric unit is an olefin polymer; (2) a co-initiator of dimethylaluminum halide or dimethylboron halide, preferably dimethylaluminum chloride; and (3) a solvent medium with a dielectric constant between about 2.0 and about 7 (as measured at 20 °C) and having a water content of about 1 x 10"*- * mol/L or less. Either the monomer or the co-initiator may be added last. However if the monomer is to be added last, it is preferred that an aging period of about three to about twenty minutes be utilized prior to the addition of the monomer. The addition of the last component begins the polymerization. Mn may be preselected by controlling the ratio of monomer to initiator concentrations, as in other living polymerization systems. In one embodiment, to make high Mn copolymers, the initiator concentration is typically about 1 x 10-3 m ol/L or less; the monomer concentration is typically 1 to 3 mol L, and the initiator and co-initiator are typically present at a molar ratio of 0.1 or more, preferably about 0.1 to about 20 (co-initiator to initiator). The catalyst systems described herein can be used, among other things, for the polymerization of olefins, particularly the polymerization of one or more olefinic, α-olefinic, di-substituted olefinic or styrenic monomers. Monomers which may be polymerized by this system include any hydrocarbon monomer that is cationically polymerizable, i.e. capable of stabilizing a cation or propagating center because the monomer contains an electron donating group. Preferred monomers include one more of olefins, α-olefins, disubstituted olefins, isoolefins, styrenics and/or substituted styrenics. Preferably, the monomer contains 1 to 20 carbon atoms, more preferably 2 to 10, even more preferably 2 to 8 carbon atoms, and most preferably 2 to 6 carbon atoms. Examples of preferred olefins include styrene, para-alkylstyrene, para-methylstyrene, alpha-methyl styrene, isobutylene, 2-methylbutene, 2-methylpentene, isoprene, butadiene and the like. A particularly preferred monomer combination comprises isobutylene and para-methyl styrene. The system has the benefit of producing polymers with narrow molecular weight distribution, particularly narrow molecular weight distribution polyisobutylene that can incorporate additional monomer and still maintain a narrow molecular weight distribution. The block copolymers of the invention are produced from one or more of olefins, α-olefins, disubstituted olefins, isoolefins, styrenics and/or substituted styrenics, for example styrene, para-alkylstyrene, para-methylstyrene, para-t-butylstyrene and the like. Non limiting preferred block copolymers of the invention include polystyrene-polyisobutylene-polystyrene, poly-p-methylstyrene-polyisobutylene-poly-p-methylstyrene, poly-p-t- butylstyrene-polysiobutylene-poly-p-t-butylstyrene, and the like. Preferred initiators include tertiary alkyl or aralkyl halides represented by the formula below: wherein X is a halogen, preferably chloride and Rl, R2 and R3 are independently any straight or branched chain alkyls, aryls or aralkyls, preferably containing 1 to 15 carbon atoms, more preferably 1 to 8 carbr atoms, even more preferably 1 to 2 carbon atoms, n is the number of initiator and is a number greater than or equal to 1, Dreferably 1 to 6. The aralkyls may be substituted or unsubstituted. Preferred nples include 2-chloro-2,4,4-trimethyl pentane (TMPC1), 1,3,5 tri (1- chloro-l-mtuiyl ethyl) benzene and 5-tert-butyl-l,3-di( 1-chloro-l -methyl ethyl) benzene (TBDCC). Other suitable initiators can be found in U.S. Patent 4,946,899, which is herein incorporated by reference. For the purposes of this invention and any claims thereto, aralkyl is defined to mean a compound containing both aromatic and aliphatic structures. Another preferred initiator is a tertiary polymeric hahde, one of Rl , R2 or R3 is an olefin polymer and the remaining R groups are defined as above. Preferred oiefin polymers include polyisobutlyene and polypropylene. The polymeric initiator may have halogenated tertiary carbon positioned at the chain end or alo* >r with the backbone of the polymer When the olefin polymer has multiple ha. igen atθ'..s at tertiary carbons, either pendant to or within the polymer backbone, the product polymer may have a comb like structure and/or side chain branching depending on the number and placement of the halogen atoms in the olefin polymer. Likewise, the use of a chain end tertiary polymeric halide initiator provides a method for producing block copolymers. Monomer added to the polymeric initiator will form a second block. Successive blocks can be formed by sequential monomer addition. The preferred co-initiator is a dimethylaluminum halide or dimethylboron halide, preferably dimethylaluminum chloride or dimethylboron chloride. The solvent medium can be a single solvent or a mixture of solvents such that: (1) the polarity has been adjusted to match or resemble that obtained from a solvent mixture of 30 to 90 parts methyl cyclohexane to 70 to 10 parts methylene chloride, by volume; (2) has a calculated dielectric constant of between about 2.5 and about 7 units; or (3) has a measured dielectric constant between about 2.5 and about 7 plus or minus ten percent error. If the preferred embodiment utiUzing dimethylaluminum halide as a co-initiator is selected then the dielectric constant is preferably from about 2 to about 7 plus or minus ten percent error. The dielectric constant is calculated or measured by the methods described in PCT publication WO 94/19380, published September 1, 1994,(wbich claims priority from USSN 08/020,850 and USSN 08/044,529), all of which are incorporated by reference herein for the purposes of U.S. law. Suitable solvents include hydrocarbons, especially hexanes and heptanes, halogenated hydrocarbons, especially chlorinated hydrocarbons and the like. Specific examples include but are not limited to methyl cyclohexane, ethyl cyclohexane, propyl cyclohexane, methyl chloride, methylene chloride, ethyl chloride, propyl chloride, butyl chloride, chloroform and the like. For the purposes of this invention and the claims thereto a proton scavenger is defined to be a composition capable of reacting irreversibly with free protons and not producing a new species of catalyst or if it does produce a new species of catalyst, that catalyst is substantially inactive when compared to the catalyst system of this invention. This invention is preferably used in the absence of proton scavenger. The co-initiator is preferably present in the polymerization feed at a mol ratio of up to about 20 times the number of initiator sites, preferably about 0.001 to about 20 times the number of initiator sites, even more preferably about 0.5 to about 8 times the number of initiator sites. In a preferred embodiment using dimethylaluminum halide as a co-initiator without the presence of a proton trap. the co-initiator may be present in a coinitiatoπinitiator ratio of about 0.1:1 or more, preferably a ratio of 0.1 : 1 of about 20: 1 or more. The concentration of the water in the system is calculated by the method described in PCT publication WO 94/19380 or measured by other means known in the art. This value is calculated for a batch of dried solvent or solvent mixture and then the value is used when that solvent is the reaction media. For the purposes of this invention it is assumed that the concentration of water in a given system of the same solvent batch does not vary in a statistically significant manner. (Even though the exact concentration may vary, the concentration is usually between 10-3 to lO" 4 M.) The polymerization reaction is typically run at or below about -30 °C preferably below about -75 °C. Typical monomers which may be polymerized by this system include one or more of: olefins, alpha olefins or disubstituted olefins. Preferred monomers include isobutylene, 2-methyl-butene, 2-methyl-pentene, and the like. The polymerization is typically performed in a solution phase reactor by methods known in the art The polymerization is typically complete in about 10 minutes, however, may run from less than one minute to about an hour. However, longer polymerization times are still within the scope of this invention. The polymers produced by this invention have a narrow molecular weight distribution (Mw/Mn), preferably less than about 2.0, even more preferably less than about 1.75. Polyisobutylene and other isobutylene based polymers having a narrow molecular weight distribution are preferred polymers produced by this catalyst system. Furthermore, when tertiary polymeric halide initiators with the tertiary carbon at the chain end or along or with in the polymer backbone are used, block copolymers and/or polymers with one or more side chain branches including comb copolymers are produced, respectively. Examples For the examples of this invention, the method described above was used to calculate the concentration of water in the solvents. For all the examples it is assumed that the water concentration was less than 1.0 x 10" mol/L. Once this concentration was determined as above, solvents from the same batch of dried solvents were used so as to minimize any variation in water concentration. Molecular weight (Mw and Mn) were measured by Gel Permeation Chromotography using a Waters 150 gel permeation chromatograph equipped with a differential refractive index (DRI) detector. The numerical analyses were performed using the commercially available standard Gel Permeation Software package. Example 1: In a nitrogen box having a water content below about 5 ppm, a test tube was charged with 3 microliters of 2-chloro-2,4,4-trimethylpentane (TMPC1), 4 ml of anhydrous methylene chloride, 6 ml of anhydrous hexane and 1.6 grams of isobutylene at -80 °C. Once the solution stabilized at -80 °C, 100 microliters of a 2.57 M solution of dimethylaluminum chloride in methylene chloride was added to begin the polymerization. After 25 minutes the polymerization was stopped with the addition of 3 ml of chilled methanol. Polymer was isolated by pouring the 10 reaction mixture into methanol with stirring. The data are reported in Table 1, Table 2 and Figure 1. Table 1 Run [DMAC] [TMPC1] [lb] (mol/L) (mol/L) (mol/L) 1 (-■-) 1.28xl0- 2 1.57xl0- 3 1.4 447.69+504.27 x R 2 =0.994 2 (-Δ-) 1.28xl0- 2 1.98x10-3 2.3 1749+669.95 x R 2 =0.997 3 (-D-) 2.57x10-2 1.98x10-3 3.2 336.38+937.53 x R 2 =0.998 4 (-0-) 3.85xl0- 2 1.98x10-3 3.2 590.5 + 904.97 x R 2 = 1.000 lb = isobutylene; TMPC1 = 2-chloro-2,4,4-trimethylpentane. Table 2 Run %C Mn %C Mn %C Mn %C Mn (-■-) (- ■ -) (-Δ-) (-Δ-) (-□-) (-□-) (-0-) (-0-) 1 0 0 0 0 0 0 0 0 2 7 2311 4 1441 5 2995 16 15773 3 4 2626 13 5347 26 24639 100 15773 4 22 8398 53 31981 78 75101 5 53 28425 100 66377 100 91526 6 100 49348 %C = percent conversion. Example 2: A solution is prepared at -90°C from 500 ml of hexane, 300 ml of methyl chloride, 2.3 ml (0.025 moles) of dimethylaluminum chloride (DMAC) and 3 ml (1.8 x lO'^moles) of a 0.06 mol/L stock solution of dimethyl phthalate in hexanes. This solution is aged two minutes before 110 ml (1.375 moles) of isobutylene (IB) is added. The solution is aged for two more minutes after this addition. Reaction is initiated by the addition of 235 milligrams (8 X 10" moles) of 5-tert-butyl-l,3-bis(l-chloro-l-methylethyl) benzene (TBDCC) which is dissolved into 2 ml of cold hexanes. Isobutylene is permitted to polymerize between 30 and 60 minute At the end of this time, 50 ml of a styrene stock solution is added This stock solution is prepared from 45 ml of styrene, 120 ml of hexane and lOυ ml of methyl chloride and is cooled to -90°C. Five minutes after the first addition, a second 50 ml aliquot of the styrene stock solution is added. A third aliquot of 50 ml is added after an additional five minutes. The remainder of the . tyrene solution is added nine minutes after the third aliquot addition. Polymerization is continued for 20 to 25 minutes before quenching with methanol. The block copolymer is isolated by devolatilization. The polymer is purified by dissolution into toluene, washing this solution with aqueous ammonium hydroxide, adding 1 wt% BHT (antioxidant) and finally precipitating the polymer into methanol. The material is further dried under vacuum. The data are reported in Table 3. The Mn (Mw/Mn) in Table 3 represents the respective values for the mid-segment polymer and the second value represents the whole polymer. The DTBP in Table 3 represents 2,6- di-tert-butyl-pyridine and DMP represents dimethyl phthalate. The block copolymers prepared from this invention are typically thermoplastic elastomers (TPEs). Thermoplastic elastomers retain all the properties of a vulcanized rubber, but also are capable of being melted like a thermoplastic. Operations suitable for use with a thermoplastic, like blow olding, extrusion and injection, are possible with the thermoplastic elastomers. Thus, the block copolymers in an embodiment of this invention are akin to meltable, IT sable butyl rubber. The uses of such materials encompass those normally fo: i for the vulcanized rubber (e.g., tire innerliners, sidewalls, medical enc sures) but also new applications such as those in vacuum forming operations (gloves, bottles) and as hot melt adhesives, modifiers and or compatibilizers with other polyolefins to name a few. All references, testing procedures and priority documents are incorporated by reference herein. As is apparent from the foregoing general description and the specific embodiments, while forms of the invention have been illustrated and described, various modifications can be made without departing from the spirit and scope of the invention. Accordingly, it is not intended that the invention be hmited thereby.

Claims: CLAIMS: I claim: 1. A carbocationic catalyst composition comprising: an initiator of one of a tertiary alkyl halide, a tertiary aralkyl halide or a tertiary polymeric halide; a co-initiator which is one of a methylaluminum or a methylboron compound; and a solvent medium having a dielectric constant between about 2.5 and about 7. 2. A polymerization process for comprising contacting under polymerization conditions one or more olefinic, alpha olefinic, di-substituted olefinic or styrenic monomers with a carbocationic catalyst composition comprising: an initiator of a tertiary alkyl halide, tertiary aralkyl halide or tertiary polymeric halide; a co-initiator of an methylaluminum or methylboron compound; and a solvent medium with a dielectric constant between 2.5 and 7. 3. A process for producing block copolymers comprising sequentially contacting different monomers selected from the group consisting of alpha-olefins, olefins, di-substituted olefins, styrenics and mixtures thereof under polymerization conditions with: an initiator of a tertiary polymeric halide; a co-initiator of an methylaluminum halide or a methylboron halide; and a solvent medium having a dielectric constant of about 2.5 to about 7. 4. A carbocationic catalyst composition comprising: an initiator of one of a tertiary alkyl halide, a tertiary aralkyl halide or a tertiary polymeric halide; a co-initiator which is one of a dimethylaluminum halide or a dimethylboron halide; and a solvent medium having a dielectric constant between about 2.0 and about 7 and having a water content of about 1 x 10"3 mol L or less. 5. A living polymerization process comprising: contacting under polymerization conditions one or more olefinic, α-olefinic, di-substituted olefinic or styrenic monomers with a catalyst composition comprising: an initiator of a tertiary alkyl halide, tertiary aralkyl halide or tertiary polymeric halide; a co-initiator of an dimethylaluminum hahde or dimethylboron hahde; and a solvent medium with a dielectric constant between 2.0 and 7 having a water content of about 1 x 10"3 mol/L or less. 6. The carbocationic catalyst composition of claim 1 wherein the co- initiator is dimethylaluminum halide or dimethylboron hahde or dimethylaluminum chloride. 7. The carbocationic catalyst composition of any preceding claims wherein each alkyl or aralkyl group of the initiator has 1 to 8 carbon atoms, preferably an alkyl group having 1 or 2 carbon atoms. 8. The carbocationic catalyst composition of any preceding claims wherein the initiator is represented by the formula: wherein Rl, R2 and R3 are independently a Cl to Cl5 straight or branched chain alkyl, aryl or aralkyl group, X is a halogen and n is a number greater than or equal to 1, preferably n is 1 to 6. 9. The composition of any preceding claim, wherein a proton scavenger is absent 10. The carbocationic catalyst composition of any preceding claims wherein the catalyst is utilized at a temperature less than about -30°C or less than about -70°C. 11. The carbocationic catalyst composition of any preceding claims wherein the ratio of number of moles of co-initiator to the number of initiator sites is up to about 20: 1 , preferably the ratio of number of moles of co-initiator to the number of initiator sites 0.001 : 1 to about 20: 1. 12. The carbocationic catalyst composition of any preceding claims wherein the ratio of number of moles of co-initiator to the number of initiator sites is from about 0.5: 1 to about 8: 1. 13. The process of claim 2 wherein the ratio of the number of moles of co-initiator to the number of initiator sites is between about 0.001 : 1 to about 20: 1. 14. The process of claim 2 wherein the co-initiator is dimethylaluminum chloride, and the initiator is a tertiary alkyl halide or tertiary aralkyl halide wherein each alkyl or aralkyl independently has 1 to 8 carbon atoms. 15. The process of any preceding claims 2-14 wherein the monomer comprises isobutylene. 16. The system of claim 4 wherein the molar concentration ratio of co- initiator to initiator sites is 0.1 : 1 or more and/or the molar concentration ratio of co-initiator to initiator sites is between about 0.1 : 1 to about 20: 1. 17. The process of claim 5 wherein the monomer is added to a solution of initiator, co-initiator and solvent at least about 3 minutes after the addition of the co-initiator.

Inventors: BAHADUR MANEESH, SHAFFER TIMOTHY DANIEL, BAHADUR, MANEESH, SHAFFER, TIMOTHY, DANIEL
Applicants: EXXON CHEMICAL PATENTS INC, EXXON CHEMICAL PATENTS INC.
Application year: 1995
Main classification: C08F
IPC codes: C08F2, C08F4, C08F10, C08F12, C08F110, C08F297