Transparent glass-ceramics

Abstract: The present invention is directed to the preparation of two groups of transparent glass-ceramics exhibiting high optical clarity and containing essentially only one crystal phase. The first group consists essentially, in cation percent, of SiO₂ 20-35 PbF₂ 19-23 AlO 1.5 10-20 YF₃ 3-7, CdF₂ 19-34 and the second group consists essentially, in cation percent, of SiO₂ 20-35 PbF₂ 15-25 AlO 1.5 10-20 YF₃ 3-7 CdF₂ 21-31 ZnF₂ 3-7 .

Description: Field of the Invention The field of the invention is the production of transparent glass-ceramic articles. More specifically, the field of the invention is the production of fluoride-containing, transparent glass-ceramic articles exhibiting properties rendering them suitable for use in fabricating amplifier and laser fibers. Background of the Invention It was first reported by M. Poulain and J. Lucas in "Verres Fluores au Tetrafluorure de Zirconium. Properties Optiques d'un Verre Dope au Nd 3+ ", Mat. Res. Bull. 10 , 243-246 (1975) that a transparent glass was formed from a ZrF 4 ·BaF 2 ·NaF mixture fused at 800°C, rather than a new crystalline laser host material, which had been the object of their research. Their finding aroused immediate widespread attention because this previously unknown fluoride-based glass system offered the only practical amorphous material with infrared transparency extending beyond 6 microns. This desirable optical property is founded in the nonoxide composition of the glass and has comprised the principal basis for extensive research and development to the present day. Investigators in the field appreciated that, because of the extended infrared transparency exhibited by the fluoride, they had the potential of forming optical fiber waveguides with losses of one to two orders of magnitude less than silica fibers. Furthermore, the low energy phonon spectra lead to relatively high quantum efficiencies for many rare earth metal transitions. Finally, when formulated with a sufficient content of rare earth metal ions, the glasses hold the promise of being attractive hosts for active fibers. Among the more potentially useful of the fluoride-based glasses is the system of heavy metal fluoride glasses termed ZBLAN, those glasses consisting essentially of ZrF 4 , BaF 2 , LaF 3 , AlF 3 , and NaF. U.S. Patent No. 4,674,835 (Mimura et al.) recites a representative formulation of ZBLAN expressed in terms of mole percent ZrF 4 50-55 AlF 3 2-4 BaF 3 16-24 NaF 16-24 LaF 3 3-5 wherein the sum of the components totals 100. Unfortunately, heavy metal fluoride glasses suffer certain undesirable attributes which have restricted their applications. Most notably, heavy metal fluoride glasses exhibit poor resistance to devitrification and Mimura et al. discuss the crystallization problems of ZBLAN and the light scattering problems resulting therefrom. The great susceptibility of ZBLAN glasses to devitrification also generates problems in forming large preforms. Crystallization at the interface between the core and cladding during the production of the preform causes problems in the most commonly used methods for preparing a ZBLAN optical fiber. That is, heavy metal fluoride glasses are quite prone to inhomogeneous nucleation, the consequence of which being crystallization at the core and cladding interfaces, particularly during the drawing of the optical fiber. The resulting fibers are subject to serious scattering losses due to crystals in the fibers. Devitrification of the glasses is aggravated when ions necessary to impart differences in indices of refraction to the core and cladding are added to the glass composition. Additional doping, for example with rare earth metal ions, also tends to reduce the stability of the glass. As a consequence of those problems, research has been continuous to find additives to the base ZBLAN composition which will reduce the tendency of the glass to devitrify and to increase the chemical stability thereof. Because that research has ameliorated the devitrification problem to a certain extent, but has not nearly eliminated it, other composition areas have been investigated wherein properties similar to those demonstrated by ZBLAN glasses can be secured, but where the problem of devitrification would be significantly reduced, most preferably totally eliminated. One area of such research is reported by Y. Wang and J. Ohwaki in "New Transparent Vitroceramics Codoped with Er 3+ and Yb 3+ for Efficient Frequency Upconversion", Applied Physics Letters , 63 (24), 3268-3270, December 13, 1993. The specific vitroceramic (also called glass-ceramic) described therein had a base composition within the general fluoroaluminosilicate system and consisted essentially, expressed in terms of mole percent, of SiO 2 30 CdF 2 20 AlO 1.5 15 YbF 3 10 PbF 2 24 ErF 3 1 . The glass produced from that composition was heat treated at 470°C to develop microcrystallites therewithin identified as Pb x Cd 1-x F 2 , which the authors stated did not reduce the transparency of the body. The authors posited that the Yb 3+ and Er 3+ ions were preferentially segregated from the precursor glass and dissolved into the microcrystals upon heat treatment. The size of the microcrystallites was estimated by the authors to range about 20 nm (200 Å, 002 µm); that size being so small that light scattering loss was minimal. (Our investigations of the materials indicated that not only were the crystals of very small size, but also the interparticle spacing of the crystals was very small.) The authors reported the upconversion efficiency of their products to be about 2 to 10 times as high as that measured on the precursor glass and other fluoride-containing glasses. Based upon those findings by the authors, we hypothesized that, if those glass-ceramics were as transparent as described, they might also be useful as hosts in amplifier and/or laser devices. Nevertheless, we realized that, if the glass-ceramic materials were to comprise viable hosts for 1.3 µm amplifier devices, Yb would have to be eliminated from the composition because Pr, which is customarily utilized in materials designed for such devices, readily transfers electrons to Yb, that action resulting in the efficiency of the device being reduced. Therefore, the principal objective of the present invention was to devise glass-ceramic materials comprising an improvement upon those described by Wang and Ohwaki. A specific objective of the subject invention was to develop such glass-ceramic materials which, when doped with Pr, would exhibit excellent behavior as hosts in 1.3 µm amplifiers. Another specific objective of the instant invention was to develop optical fiber waveguides comprising said glass-ceramic materials as the high refractive index core surrounded by a cladding of lower refractive index material. Summary of the Invention In our initial laboratory investigations, we discovered that, when YbF 3 was removed from the Wang et al. composition, the resultant glass did not, upon heat treatment, crystallize in situ properly to produce relatively uniformly-sized, homogeneously dispersed, very fine-grained crystals to yield a transparent material. That is, the resulting material did not exhibit the controlled crystallization constituting the hallmark of a glass-ceramic body. X-ray diffraction studies of the material found no crystalline peaks when the precursor glass was exposed to temperatures within the 450°-500°C range and further heat treatments did not yield a transparent glass-ceramic body. The occurrence of this phenomenon indicates that Yb plays a critical role in the formation of the crystal phase, a role not recognized by Wang et al. Further laboratory studies disclosed that YbF 3 could be replaced without changing the basic crystallization characteristics or the crystal phase itself of the Wang et al. glass by either a combination of YF 3 with CdF 2 concentrations greater than that in the glass of Wang et al., or by a combination of YF 3 and ZnF 2 . Founded upon those two discoveries, the two compositions listed below, expressed in terms of mole percent, were adopted as base glasses: Glass I (A) Glass II (B) SiO 2 30 PbF 2 22 SiO 2 30 PbF 2 17 AlO 1.5 15 YF 3 4 AlO 1.5 15 YF 3 4 CdF 2 29 CdF 2 29 ZnF 2 5 . The presence of at least 3 mole % YF 3 was determined to be required to assure the proper crystallization in situ to yield a transparent glass-ceramic material of optical clarity. Whereas both base glass compositions performed satisfactorily, the inclusion of ZnF 2 results in somewhat improved glass melting and crystallization behavior; hence, glasses containing ZnF 2 are preferred. In ZnF 2 -containing compositions the content of CdF 2 will range about 21-31 mole %. Where ZnF 2 is absent, CdF 2 will vary between about 19-34 mole %. In ZnF 2 -containing compositions the concentration of PbF 2 will range about 15-25 mole %, whereas in the absence of ZnF 2 , the PbF 2 content will be held between about 19-23 mole %. In order to determine whether additions and/or substitutions could be made to the base glasses, various composition excursions were tested. The general approach adopted comprised substituting fluorides for fluorides and oxides for oxides, thereby maintaining a relatively constant anion ratio. Satisfaction of the following two fundamental criteria was required: (1) the glass will crystallize in situ to a glass-ceramic containing essentially one crystal phase which, most preferably, is capable of accepting some rare earth metal doping; and (2) the glass-ceramic will display high optical clarity. Those excursions illustrated that B 2 O 3 , GeO 2 , P 2 O 5 , and, to a lesser extent, TiO 2 can be substituted into the oxide composition without encountering adverse effects upon the crystallization behavior of the glass. GaF 3 , HfF 4 , and InF 3 can be substituted into the fluoride composition area. Alkali metal and alkaline earth metal oxides and fluorides caused the glass melt to devitrify as it cooled. Compositions containing LaF 3 did not melt well, even at temperatures as high as 1200°C. Other rare earth metals demonstrated varying effects. For example, LuF 3 and DyF 3 satisfied the above two criteria in amounts up to 11 mole %; GdF 3 -containing compositions crystallized in situ with two crystal phases; and CeF 3 -containing melts devitrified spontaneously during cooling. Finally, some CdS can be substituted for CdF 2 . As a result of our laboratory investigations, we have determined that precursor glasses essentially free from ZnO capable of being crystallized in situ to glass-ceramic materials displaying high optical clarity and containing essentially one crystal phase can be prepared from compositions consisting essentially, expressed in terms of mole percent, of SiO 2 20-35 PbF 2 19-23 AlO 1.5 10-20 YF 3 3-7 . CaF 2 19-34 Where the precursor glass contains 3-7 mole % ZnF 2 , glass-ceramic materials exhibiting high optical clarity and containing essentially one crystal phase can be prepared from compositions consisting essentially, expressed in terms of mole percent, of SiO 2 20-35 PbF 2 15-25 ALo 1.5 10-20 YF 3 3-7 CdF 2 21-31 ZnF 2 3-7 . By the expression "essentially free from", it is meant that the glass does not contain sufficient ZnF 2 to alter the chemical and/or physical characteristics of the glass. Preferably, ZnF 2 will be absent altogether, but this is not always possible because the glass batch materials (including cullet added to the batch materials) may contain it as an impurity. By the expression "essentially one crystal phase", it is meant that the glass-ceramic does not contain a sufficient amount of a second crystal phase to alter the chemical and/or physical characteristics of the glass-ceramic, most particularly the optical clarity thereof. Again, most preferably, no amount of a second crystal phase will be present. Where rare earth metal ions are included as substitutes for yttrium, they will be present in the crystal phase(s). In the present specification and claims, the expressions "consisting essentially of" and "consist essentially of" are intended to permit the inclusion of minor amounts of inorganic components which do not detrimentally affect the characteristics of the precursor glass and/or those of the final glass-ceramic. In both of the above composition intervals, up to 17 mole % total of the following components in the indicated proportions selected from the group consisting of 0-7% BO 1.5 , 0-12% GeO 2 , 0-7% PO 2.5 , 0-3% TiO 2 , 0-7% GaF 3 , 0-7% HfF 4 , 0-7% InF 3 , 0-11% LuF 3 , 0-11% DyF 3 , 0-3% CdCl 2 , and 0-5% CdS may be present. Differential scanning calorimetry (DSC) measurements of the inventive glasses have indicated a transition temperature in the vicinity of 400°C and a sharp crystallization peak above 450°C for most compositions. The temperature of the heat treatment required to convert the precursor glass to a glass-ceramic was determined after first observing the position of the crystallization peak from the DSC curve, and then exposing the glass to temperatures in the vicinity of that peak. The length of the exposure was dependent upon the temperature employed relative to the peak crystallization temperature, it being well known that crystallization occurs more rapidly at higher temperatures. Thus, the period of exposure could be as short as a few minutes at elevated temperatures to many hours at temperatures below the peak crystallization temperature. Nevertheless, because crystal growth can be more closely controlled at lower temperatures to assure uniformly very fine-grained crystals, heat treatments of 2-8 hours, desirably about 4 hours, at temperatures slightly below the peak crystallization temperature were employed. X-ray diffractive analyses have indicated the presence of a crystal phase which has not been positively identified. The crystal structure has been tentatively identified as a derivative of either M (1-x) (Y,Ln) x F 2+x , wherein M comprises Pb and/or Cd, or (Pb, Cd)LnF 3+x , each of which is a cubic fluorite-like crystal. (Ln refers to a rare earth metal of the lanthanide series.) In either case it indicates the site of the rare earth metal ion in the crystal. X-ray diffraction analyses also indicated the size of the crystals to be about 100-300 Å (10-30 nm, 0.01-0.03 µm) and the crystal content of the material to be about 25-30% by volume. Those values were confirmed via transmission electron micrography. The linear coefficients of thermal expansion of the inventive glass-ceramic materials over the temperature range of 25°-300°C have been measured between about 95-112x10 -7 /°C. The densities of the glass-ceramics range about 5.7-5.9 g/cm 3 and their refractive indices between about 1.74-1.76. Where doped with Pr, fluorescence lifetimes in excess of 100 microseconds are the norm with some examples measuring up to about 160 microseconds, that value being more than 50% longer than exhibited by Pr 3+ -doped ZBLAN. Prior Art A. A. Kaminskii et al. in "Stimulated IR Emission of Nd 3+ Ions in Nonstoichiometric Cubic Fluorides", Izvestiya Akademii Nauk SSSR, Neorganicheskie Materialy , Vol. 21, No. 5, pages 702-705, May 1985, describe three methods for improving the energy characteristics of the stimulated emission of solid state inorganic materials with Ln 3+ ions; viz., the growth of multi-center disordered crystals based on structurally ordered compounds, increasing the concentration of the activator, and/or introducing sensitizing ions into active media of the types just described. The authors indicated that the first two methods had already been used to obtain M 1-x (R,Ln) x F 2+x solid solutions with a fluorite structure with Nd 3+ ions on the basis of MF 2 (where M is Ca, Sr, and/or Ba), the trifluorides RF 3 (where R is Y and/or Sc), and LnF 3 , where Ln is La, Ce, Nd, Gd, and/or Lu). The work of the authors described in this paper was directed to the stimulated emission spectroscopy of Nd 3+ ions in the infrared region of the radiation spectrum in disordered fluorite phases based on CdF 2 and the trifluorides of gadolinium and lutecium, i.e., Cd 1-x Ln x -F 2+x . There is no mention by the authors of a glass-ceramic article or of precursor glass compositions suitable for heat treatment to produce transparent glass-ceramic articles. They were dealing with conventional ceramic materials to grow single crystals. This paper and the literature article authored by Wang et al. discussed above are believed to constitute the most pertinent prior art. Description of Preferred Embodiments Table I below records a number of glass compositions expressed in terms of mole percent illustrating the present invention resulting from our laboratory investigations. Batches in 25 gram lots were prepared from pure oxides, fluorides, chlorides, and sulfides, hand tumbled to mix the components together, and then charged into 30 cm 3 platinum crucibles. Each batch was doped with 200 ppm PrF 3 . The crucibles were moved into a furnace operating at temperatures between 1000°-1200°C for 0.5 hour. All compounding, mixing, and melting were carried out in a glove box under dry nitrogen. Although these glasses do not require melting under inert conditions, safety concerns because of the high concentrations of cadmium led to the practice of confining the melts. After melting, most compositions appeared to be clear, moderately fluid, quiescent liquids. When poured onto a steel block, the resultant slabs tended to break up into small fragments, the cause of the fragmentation being conjectured to be due to the formation of a few crystals therein. Larger bars having dimensions of 5 X 1 X 1 cm, could be cast without shattering, this capability being theorized to be due to a partial anneal received during cooling because of the larger volume of the article. A more thorough anneal was required when the material was to be cut and polished for testing. As was observed above, the crystallization heat treatment applied to each glass sample was determined after the position of the crystal-lization peak had been located from a DSC curve. The glass sample was heated to a temperature in the vicinity of the peak, the time of exposure being dependent upon the heat treatment temperature utilized vis-a-vis the peak crystallization temperature. In Table I the glass compositions are founded in base glasses A and B with various substitutions of constituents being recorded in terms of mole percent. As noted above, the crystallization heat treatment comprises a range of temperatures centered about the peak crystallization temperature. Because each change in composition can shift both the Tg and peak crystallization temperature of a glass, the thermal processing of each material varies. The heat treatment range for each composition, expressed in terms of °C, encompasses the temperature interval between the onset of the crystallization peak to its terminus. The breadth of the heat treatment ranges for some of the compositions is reported in Table I. Finally, whether the crystallized product (Product) exhibited the demanded optical clarity and whether it contained extremely fine-grained crystals of a single phase are also recorded (yes/no). A chemical analysis was conducted on base glass B. The batch therefor was melted for 30 minutes at 1000°C in a platinum crucible. Element Batched, Weight % Melted, Weight % Si 6.9 5.3 Al 3.3 3.6 Cd 26.7 28.9 Pb 28.9 30.6 Y 2.9 3.3 Zn 2.7 3.0 F 17.8 12.8 Those data suggest that essentially only Si and F were lost during melting. Inasmuch as the F/Si ratio loss approximates 4, it is believed logical to conclude that SiF 4 comprises the principal volatilization product under the present melting conditions. The great resistance of the inventive glasses to devitrification permits the production of large preforms. Thus, crystallization at the interface between the core and cladding during the production of the preform is avoided in the most commonly used methods in preparing an optical fiber waveguide. That attribute led to investigations to discover cladding glasses exhibiting lower refractive indices than the inventive glass-ceramics, but demonstrating linear coefficients of thermal expansion, transition temperatures, and viscosity characteristics compatible with the inventive precursor glasses and glass-ceramics, so as to permit the fabrication of optical fiber waveguides. We have found a family of glasses in the K 2 O-PbO-B 2 O 3 -SiO 2 system which exhibit the necessary properties. Thus, they display refractive indices between 1.67-1.73, linear coefficients of thermal expansion over the temperature range of 25°-300°C of 98-110x10 -7 /°C, transition temperatures between 390°-425°C, and softening points between 475°-525°C. The composition ranges of operable glasses are set out below, expressed in terms of weight percent on the oxide basis, of SiO 2 23-30 B 2 O 3 1-10 Al 2 O 3 0-3 PbO 49-60 Li 2 O 0-1 Na 2 O 0-2 K 2 O 5-11 BaO 0-8 Examples of operable glass compositions, expressed in terms of weight percent on the oxide basis, are listed below in Table II. Also listed are the refractive index (η), the linear coefficient of thermal expansion (Exp) over the temperature range 25°-300°C expressed in terms of x10 -7 /°C, and the softening point (S.P.) and transition temperature (Tg) expressed in terms of °C. The batch ingredients were compounded in 1000 gram lots, thoroughly blended together in a turbula mixer, and charged into platinum crucibles. The crucibles were moved into a furnace operating at 1200°C and the batches melted for three hours. The melts were cocktail mixed and then poured onto a steel plate to form glass patties having dimensions of about 6" x 6" x 0.5" (∼15 x 15 x 1.25 cm). Finally, the patties were annealed at 400°C. 1 2 3 4 5 6 SiO 2 26.0 25.5 24.4 29.2 27.2 26.0 PbO 58.0 52.3 50.6 54.0 54.0 58.0 K 2 O 9.0 10.3 11.4 7.7 7.7 8.0 B 2 O 3 3.0 3.0 3.0 6.0 8.0 2.0 Li 2 O -- -- -- 0.5 0.5 -- BaO -- 4.9 6.6 -- -- 2.0 Al 2 O 3 3.0 3.0 3.0 -- -- 2.0 Na 2 O -- -- -- 1.6 1.6 -- Sb 2 O 3 1.0 1.0 1.0 1.0 1.0 1.0 η 1.722 1.713 1.713 1.699 1.701 1.7175 Exp 97-109 97-113 103-118 98-116 95-110 92-104 S.P. -- -- -- 504 502 550 Tg 425 423 426 399 398 421 Sb 2 O 3 was included in the glasses to perform its conventional function as a fining agent. As can be appreciated, other fining agents such as As 2 O 3 , halides, and sulfates could be substituted therefor. As can be seen, minor amounts of Li 2 O and/or Na 2 O can be substituted for K 2 O. Such substitutions can improve the chemical durability of the glasses. Likewise, a minor amount of BaO can be substituted for PbO to modify the refractive index of the glass. The most preferred transparent glass-ceramic consists of Glass B doped with 200 ppm PrF 3 .

Claims: A transparent glass-ceramic exhibiting high optical clarity and containing essentially only one crystal phase consisting essentially, expressed in terms of mole percent, of (a) SiO 2 20-35 PbF 2 19-23 AlO 1.5 10-20 YF 3 3-7 CdF 2 19-34 or (b) SiO 2 20-35 PbF 2 15-25 AlO 1.5 10-20 YF 3 3-7 CdF 2 21-31 ZnF 2 3-7 . A glass-ceramic according to claim 1 also containing up to 17 mole percent total of at least one component in the indicated proportion selected from the group consisting of 0-7% BO 1.5 , 0-12% GeO 2 , 0-7% PO 2.5 , 0-3% TiO 2 , 0-7% GaF 3 , 0-7% HfF 4 , 0-7% InF 3 , 0-11% LuF 3 , 0-11% DyF 3 , 0-3% CdCl 2 , and 0-5% CdS. An optical fiber waveguide comprising a core consisting of a transparent glass-ceramic essentially free from ZnO exhibiting high optical clarity and containing essentially only one crystal phase consisting essentially, expressed in terms of mole percent, of SiO 2 20-35 PbF 2 19-23 AlO 1.5 10-20 YF 3 3-7 CdF 2 19-34 and a cladding consisting of a transparent glass consisting essentially, expressed in terms of weight percent on the oxide basis, of SiO 2 23-30 B 2 O 3 1-10 Al 2 O 3 0-3 PbO 49-60 Li 2 O 0-1 Na 2 O 0-2 . K 2 O 5-11 BaO 0-8 An optical fiber waveguide comprising a core consisting of a transparent glass-ceramic exhibiting high optical clarity and containing essentially only one crystal phase consisting essentially, expressed in terms of mole percent, of SiO 2 20-35 PbF 2 15-25 AlO 1.5 10-20 YF 3 3-7 CdF 2 21-31 ZnF 2 3-7 and a cladding consisting of a transparent glass consisting essentially, expressed in terms of weight percent on the oxide basis, of SiO 2 23-30 B 2 O 3 1-10 Al 2 O 3 0-3 PbO 49-60 Li 2 O 0-1 Na 2 O 0-2 . K 2 O 5-11 BaO 0-8 An optical fiber waveguide according to claim 3 or 4 wherein said glass-ceramic also contains up to 17 mole percent total of at least one component in the indicated proportion selected from the group consisting of 0-7% BO 1.5 , 0-12% GeO 2 , 0-7% PO 2.5 , 0-3% TiO 2 , 0-7% GaF 3 , 0-7% HfF 4 , 0-7% InF 3 , 0-11% LuF 3 , 0-11% DyF 3 , 0-3% CdCl 2 , and 0-5% CdS. A glass-ceramic according to claim 1 further containing PrF 3 as a dopant. A glass-ceramic according to claim 6 containing 200 ppm PrF 3 as a dopant.

Inventors: BORRELLI NICHOLAS FRANCIS, CORNELIUS LAUREN KAY, NEWHOUSE MARK ANDREW, TICK PAUL ARTHUR, BORRELLI, NICHOLAS FRANCIS, CORNELIUS, LAUREN KAY, NEWHOUSE, MARK ANDREW, TICK, PAUL ARTHUR, BORRELLI, NICHOLAS FRANCIS, CORNING INCORPORATED, CORNELIUS, LAUREN KAY, CORNING INCORPORATED, NEWHOUSE, MARK ANDREW, CORNING INCORPORATED, TICK, PAUL ARTHUR, CORNING INCORPORATED
Applicants: CORNING INC, CORNING INCORPORATED
Application year: 1995
Main classification: C03C10
IPC codes: C03B32, C03C10, G02B6, C03C4, C03C3, H01S3, C03C13