SYNTHESIS OF CRYSTALLINE POROUS SOLIDS IN AMMONIA

Abstract: A process of preparing a crystalline porous solid selected from silicas and metallosilicates, such as, aluminosilicate zeolites or clathrasils. The process involves preparing a reaction mixture containing ammonia; water in a controlled concentration; a (hydrocarbyl)ammonium polysilicate hydrate salt; a mineralizer, such as ammonium fluoride; optionally, a source of a metal oxide, such as aluminum nitride; and optionally, a source of a charge-balancing cation or a structure directing agent; and maintaining the mixture at a temperature and for a time so as to produce the crystalline porous solid. A novel silica which is isostructural with zeolite P1 is prepared. Also prepared are a novel silica which is isostructural with zeolite beta and a novel TMA sodalite having a silica/alumina molar ratio between 12 and 20.

Description: SYNTHESIS OF CRYSTALLINE POROUS SOLIDS IN AMMONIA This invention relates to a process of synthesizing crystalline porous solids. More specifically, this invention relates to the synthesis of crystalline porous silicas and metallosilicates, such as silica molecular sieves, aluminosilicate zeolites, and for the purposes of this invention, clathrasils. In other aspects, this invention pertains to novel compositions of zeolite P 1 , zeolite beta, and sodalite. Crystalline porous silicas and metallosilicates find utility as supports for catalytic metals. Sodalite, for example, is useful as a catalyst support. Crystalline porous metallosilicates also have utility as heterogeneous catalysts in organic processes. For example, zeolite beta is useful as a catalyst in alkylating and transalkylating aromatic compounds and also useful as a catalyst in cracking, hydrocracking, and dewaxing hydrocarbons. Crystalline microporous solids are also employed as ion-exchangers and as sorbents for purifying gases. Zeolite beta, for example, is used as a sorbent for C 8 and C 10 alkylbenzene separations. Zeolite PI is used in the separation of linear and branched hydrocarbons. Crystalline porous solids are commonly prepared by hydrothermal methods. A typical preparation involves heating one or more nutrients, such as a source of silica, and optionally a source of a metal oxide, such as alumina, in water in the presence of a mineralizer and a structure directing agent until crystallization occurs. The mineralizer, which is typically hydroxide or fluoride, functions as a solubilizer of silica and metal oxides transporting them through the reactive solution or gel to nucleation sites. The structure-directing agent includes templates and stabilizers. The template, which may be a cation or neutral species, tends to favor the nucleation and growth of a particular zeolite. The stabilizer, often referred to as a pore filler, functions in a stabilizing role and may be required for a successful synthesis. Water and organic bases, such as primary, secondary, and tertiary aliphatic amines, and tetr aal ylammonium halides are common stabilizers. Additionally, the template or stabilizer may assist in controlling pH and/or may provide charge balance with a counteranion or the anionic framework. It is known that crystalline porous solids, such as MFI zeolites and zeolite ECR-5 of a cancrinite structure, can be synthesized in water to which dilute aqueous or liquid ammonia has been added. Typically, the ammonia/water molar ratio in the synthesis mixture is about 0.4, indicating a predominantly aqueous environment; but cancrinite products have been reported up to an ammonia/water molar ratio of 3. No crystalline products are taught to be recovered from liquid ammonia. U.S. patent 4,452,907 and U.S. patent 4,452,908 and U.S. patent 4,717,560 are representative of such teachings, as is the report of D.E.W. Vaughan and K. G. Strohmaier in the Proceedings of the 9* h International Zeolite Conference, Montreal, 1992, Eds. R. von Ballmoos etal., 1993, Butterworth-Heinemann. In hydrothermal syntheses the composition and structure of the products obtained are limited to those products whose precursor polysilicates and polymetallates are readily stabilized by water solvation. It would be desirable to have an alternative reaction environment for growing crystalline porous solids which stabilizes novel precursor polysilicates and polymetallates such that crystalline porous solids of novel composition and structure are formed. It would also be desirable to employ in the syntheses of crystalline porous solids novel reagents which form reactive intermediate species. In addition to the above, it would be advantageous to synthesize crystalline porous solids directly in an ammonium form, rather than a metal ion, for example, sodium, form. The advantage relies on the fact that usually the catalytically active form of these solids is the acid form. When the solid is synthesized as a metal ion salt, it must be ion-exchanged with aqueous acid solution to obtain the acid form. When, however, the solid is synthesized in the ammonium form, it need only be heated to drive off ammonia to obtain the acid form. Even though the advantages of alternative reaction environments are recognized, the prior art does not teach the synthesis of crystalline porous solids in concentrated ammonia. Instead, the disadvantages of working in ammonia are set forth. Chief among these disadvantages is the low solubility of common sources of reactive silica. In other aspects, zeolite Na-P1 is known having a silica/alumina molar ratio between 2 and 8, as exemplified by R. Szostak in Molecular Sieves: Principles of Synthesis and Identification, Van Nostrand Reinhold, New York, 1989, p. 64,-and by U. Hέkansson and L. Faith in Ada. Cryst., C46, 1363-1364 (1990).-Disadvantageously, the composition of zeolite P1 is limited to low Si0 2 /Al 2 0 3 molar ratios from 2 to 8. Zeolite beta is known having a Si0 /Al 0 3 molar ratio from as low as 5 to as high as 1500. Representative teachings are disclosed by R. Szostak in Molecular Sieves: Phnciples of Synthesis and Identification, op. cit, p. 64, and in U.S. patent 4,840,929. These references are silent with regard to an all-silica beta composition. In yet another aspect, zeolite sodalite can be prepared by hydrothermal methods. Normal sodalite crystallizes with a Si0 2 /Al 0 3 molar ratio of 2; however, a silica-rich sodalite is known having a Si0 2 /Al 2 0 3 molar ratio of 9.5. Representative references include R. M. Barrer and P. J. Denny, Journal of the Chemical Society, 971-982 and 983-1000 (1961); and R. M. Barrer and D. E. Mainwaring, Journal of the Chemical Society, Dalton, 2534-2546 (1972); and R. Aiello and R. M. Barrer in the Journal of the Chemical Society (A), 1470-1475 (1970). Disadvanta¬ geous^, the silica alumina molar ratio is limited to values of between 2 and 10. In one aspect, this invention is a process of preparing a crystalline porous solid selected from the group consisting of silicas and metallosilicates. The process comprises preparing a reaction mixture containing: (a) ammonia, (b) water in an amount such that the molar ratio of ammonia to water is between 4 and 26, (c) one or more nutrients comprising a (hydrocarbyl)ammonium polysilicate hydrate salt, and optionally, a source of a metal oxide which is reactive in the reaction mixture, and optionally, a source of an additional cation which is reactive in the reaction mixture, the nutrients being present in amounts sufficient to prepare the crystalline porous solid, and (d) a mineralizer in an amount sufficient to mineralize the nutrients, and thereafter maintaining the resulting mixture at a temperature and for a time sufficient to produce the crystalline porous silica or metallosilicate. For the purposes of this invention, a "crystalline porous solid" is defined as a solid which possesses a defined and ordered crystalline framework structure, in this case of silica or metallosilicate, extending in two or three dimensions and having within the framework an array of channels, pores, or cages. The channels or pores can be one, two, or three dimensional and can be distributed throughout the crystalline solid in a regular or irregular fashion. The two and three dimensional channels can be isolated or interconnected. The channels or pores may be classified as micropores or mesopores, wherein by definition a micropore ranges in size from 4 A to no greater than 20 A in cross-sectional dimension, and a mesopore ranges in size 'from greater than 20 A to 200 A in cross-sectional dimension. Alternatively, the pores or channels may be interlayered or interstitial spaces within the crystalline framework. If cages are present, they may be accessible via pores or channels. Alternatively, the cages may be isolated without interconnecting pores or channels, and therefore, inaccessible. Typically in the prior art, crystalline solids containing isolated cages are not considered to be porous. However, solids containing isolated cages can be made porous by thermal or chemical treatment. Such treatments introduce pores or channels which create accessibility to the cages. For the purposes of this invention, crystalline solids containing isolated cages will fall within the scope of the term "porous". The process of this invention provides a general method of preparing a crystalline porous solid in a reaction mixture containing predominantly ammonia. Surprisingly, the process of this invention produces novel crystalline porous solids unknown heretofore. Accordingly, the process of this invention offers the opportunity to develop novel compositions otherwise unavailable from hydrothermal methods. In addition, the process of this invention is suitable for growing crystalline porous solids of known composition. As an additional advantage, the ammonia can be removed from the reaction mixture by simple venting at room temperature. If desired, the vented ammonia can be recovered and recycled. Even more advantageously, the crystalline porous solids may be obtained directly in the ammonium form. Conversion to the active acid form is effected simply by heating; hence ion-exchange with aqueous acid solutions and its concomitant waste treatment problems may be avoided. In another aspect, this invention is a novel crystalline microporous silica, designated hereinafter as DCM-7, which is represented by the composition: Si0 2 : y (C 2 H 5 ) 3 N : n H 2 0 wherein y is a number ranging from 0 to 0.5 and n is a number ranging from 0 to 1. DCM-7 is isostructural with zeolite P1 , as determined by X-ray diffraction (XRD). The phrase "DCM-7 is isostructural with zeolite P1 " means that DCM-7 has the same crystalline structure, that is, the same XRD pattern, as zeolite P1. Unlike zeolite P1 which heretofore has been prepared with o Si0 2 /Al 2 0 3 molar ratios ranging only from 2 to 8, the aforementioned crystalline microporous silica of this invention contains less than 50 parts per million (ppm) by weight alumina. This low level of alumina corresponds to a Si0 2 /Al 2 0 3 molar ratio of greater than 34,000. DCM-7 is useful as a catalyst support and may be useful as a sorbent for the separation of branched and linear hydrocarbons. 5 In a third aspect, this invention is a novel crystalline microporous silica, hereinafter designated DCM-8, which is represented by the composition: Si0 2 : y' (CH 3 ) 3 N : n' H 2 0 wherein y' is a number ranging from 0 to 0.5 and n' is a number ranging from 0 to 1. DCM-8 is isostructural with zeolite beta, as determined by XRD. Unlike zeolite beta which heretofore 0 has been prepared with Siθ2/AI 2 θ3 molar ratios ranging from 20 to 1500, the novel zeolite beta of this invention contains less than 50 ppm by weight of alumina, likewise corresponding to a Si0 2 /AI 0 3 molar ratio of greater than 34,000. DCM-8 is useful as a catalyst support and as a sorbent. In a fourth aspect, this invention is a novel crystalline porous aluminosilicate, 5 hereinafter designated DCM-9, which is represented by the composition: x" Si0 2 : Al 2 0 3 : y" (CH 3 ) 4 N * : n" H 2 0 wherein x" is a number ranging from 12 to 20, y" is 2.0, and n" is a number ranging from 1 to 5. DCM-9 is isostructural with sodalite, as determined by XRD. Unlike sodalites which heretofore have been prepared with Si0 2 /AI 2 03 molar ratios ranging only from 2 to 10, the novel sodalite 0 of this invention has a Si0 2 /AI 2 θ3 molar ratio ranging from 12 to 20. Zeolite DCM-9 is useful as a catalyst support. The process of this invention provides a general method of preparing a crystalline porous solid in a reaction mixture that is predominantly ammonia. The solids are selected from the group consisting of silicas and metallosilicates. 5 In one preferred embodiment, this invention is a process of growing a crystalline porous silica. The process comprises preparing a mixture containing (a) ammonia, (b) water , such that the ammonia water molar ratio ranges between 5 and 26, (c) a (hydro- carbyl)ammonium polysilicate hydrate salt, and (d) a mineralizer in an amount sufficient to mineralize the polysilicate salt. Thereafter, the resulting mixture is maintained at a temperature and for a time sufficient to produce the crystalline porous silica. In another preferred embodiment, this invention is a process of growing a crystalline porous alumino-silicate. The process comprises preparing a mixture containing (a) ammonia, (b) water such that the ammonia/water molar ratio ranges between 5 and 26, (c) nutrients comprising a (hydrocarbyl)-ammonium polysilicate hydrate salt, a source of alumina, and a source of a charge balancing cation, the nutrients being present in amounts sufficient to produce the crystalline porous solid, and (d) a mineralizer in an amount sufficient to mineralize the nutrients. Thereafter the mixture is maintained at a temperature and for a time sufficient to produce the crystalline porous aluminosilicate. In a more preferred embodiment, the source of alumina is aluminum nitride. In even more preferred embodiments, this invention is a process of growing a crystalline porous silica or aluminosilicate, as described hereinabove, wherein the mineralizer is fluoride. In a related aspect, this invention is a process of preparing a crystalline porous solid according to any of the above-identified methods wherein the synthesis mixture also contains one or more structure-directing agents In another related aspect, this invention is a process of preparing a crystalline porous solid according to any of the above-identified methods wherein the synthesis mixture further contains a secondary source of silica as described hereinafter. Any of the known crystalline porous silicas and metallosilicates can be prepared by the process of this invention. Non-limiting examples of suitable crystalline compounds containing isolated cages include clathrasils, such as dodecasil 3-C, dodecasil 3-T, dodecasil 1-H, and octadecasil. Other suitable crystalline porous compounds include silica molecular sieves, layered aluminosilicates, and aluminosilicate zeolites, non-limiting examples of which include felspars, such as pure silica sodalite and silicas of the pentasil family, such as silicalite and pure silica ferrierite; and aluminosilicate zeolites X, Y, mordenite, MCM-22, ferrierite, L, omega, beta, P1 , and the MFI (or ZSM) family, including ZSM-5, ZSM-11 , and ZSM-12. Analogous metallosilicates, including gallosilicates, titanosilicates, and borosilicates, can also be prepared by the process of this invention. Unexpectedly, novel crystalline porous silicas and metallo¬ silicates can also be prepared by the process of this invention, including, for example, a silica- rich sodalite and silicas which are isostructural with zeolite P1 and zeolite beta. The process of this invention com prises forming a reaction mixture containing ammonia, water, a (hydrocarbyl)ammonium polysilicate hydrate salt, a mineralizer, optionally, a reactive source of a metal oxide, and optionally a source of an additional cation, and maintaining the reaction mixture at a temperature and for a time sufficient to form the porous crystalline solid. The reaction mixture can be preferably represented by the following composition in terms of mole ratios of oxides: NH3/Si0 2 10 - 1000 NH3/H2O 4- 26 H 2 0/Si0 2 0.4- 250 Z Si0 2 0.04- 0.50 MOn/2/Si0 2 0 - 1 wherein Z represents the mineralizer, M0 n 2 represents the metal oxide, and n represents the valence of the metal M. At the amounts of metal oxide which are typically employed, the polysilicate hydrate salt can typically provide the necessary amount of charge-balancing cations. Typically, ammonia is supplied to the reaction mixture as an anhydrous liquid. The amount of ammonia which is employed can vary widely. Generally, the ratio of moles of ammonia to moles of silicon varies from 10 to 1000, and preferably, from 20 to 35. Ammonia possesses several properties which are especially advantageous for the formation of crystalline porous solids. Specifically, ammonia may act as a solvent or may act as a template or stabilizer. Accordingly, the addition of a separate template or stabilizer may not be required. Of course, in those instances where a template or stabilizer other than ammonia is required, that required compound may be added to the reaction mixture. As a further advantage, ammonia is a source of ammonium ions which may act as charge-balancing cations in the structure formed. As charge-balancing cations, ammonium ions have advantages over alkali or alkaline earth ions. When the as-synthesized form contains alkali or alkaline earth ions, the solid must be ion-exchanged with acid to obtain the active catalytic or sorbent form. By contrast, when the as-synthesized form contains ammonium ions, the solid need only be heated driving off ammonia to obtain the active acid form. A mineralizer is also required for the process of this invention. Mineralizers (or solubilizers) are well-known in the art to increase the solubility of nutrients in the reactive medium as well as to transport nutrients to nucleation sites, processes which are referred to as "mineralization". Mineralizers may be construed to be "catalysts" in that they are consumed on dissolution of the inorganic nutrients in the reactive media and usually regenerated when the crystalline porous solid is formed. Examples of suitable mineralizers include fluoride and hydroxide bases. If a hydroxide base in aqueous solution is used, then care must be taken to maintain an ammonia/water molar ratio within the range required of the process of this invention, as noted hereinbelow. The preferred mineralizer is fluoride. Any source of fluoride which is reactive in the reaction mixture is suitable for the process of this invention, including ammonium fluoride, hydrogen fluoride, sodium bifluoride, ammonium hexafluorosilicate, and hydrocarbylammonium fluorides, such astetramethyl- ammonium fluoride, tetraethylammonium fluoride, benzyltrimethylammonium fluoride, dipropylammonium fluoride, and isopropylammonium fluoride. Alternatively, alkali metal fluoride salts, such as sodium fluoride, can be used provided that such salts are reactive in the reaction mixture. Preferably, the source of fluoride is ammonium fluoride, hydrogen fluoride, sodium fluoride, sodium bifluoride, or ammonium hexafluorosilicate. More preferably, the source of fluoride is ammonium fluoride. As a general procedure, ammonia is added to a mixture of the nutrients, the mineralizer, and optionally the charge-balancing cation, the structure-directing agent, and water, and then the mixture is maintained at a temperature and for a time sufficient to form the crystalline porous solid. It will be apparent to those skilled in the art that the nutrients employed will depend upon the specific crystalline porous solid desired. For example, silicas will require a source of silica; whereas, metallosilicates will require a source of silica, a source of o metal oxide, and a source of a charge-balancing cation. Prior art sources of silica, such as alkali silicates and silica gels, are not readily mineralized in solutions containing predominantly ammonia. Unexpectedly, it has now been discovered that (hydrocarbyl)ammonium polyhedral polysilicate hydrates, can be mineralized in solutions containing predominantly ammonia, and therefore these salts provide a suitable source of reactive silica. The identification and preparation of (hydrocarbyl)ammonium polysilicate hydrate salts are described by D. Hoebbel et al. in Z. anorg. allg. Chem., 384, 43-52 (1971); /b.d, 465, 15 (1980); ibid..494. 31-42 (1982). Among the polysilicate ions described therein are SiεOis- 6 , Siβ0 2 o" 8 / and Siιo0 2 5" 1 °. Preferably, the polysilicate ion is SiβO-s- 6 or Siβ0 2 o" 8 . These ions are prepared with tetra(hydrocarbyl)ammonium cations, such as, tetra- 0 methylammonium, tetraethylammonium, tetrapropylammonium, tetrabutylammonium, and benzyltrimethylammonium. Preferably, the counterion istetramethylammonium, tetraethylammonium, or benzyltrimethylammonium. The polysilicate is generally obtained as a hydrate. For example, ( R 4 )6Si6θι 5 can be crystallized with 19.5 moles water of hydration. The polysilicate (NR 4 )βSi8θ 2 o crystallizes with 20-30 moles of water when NR 4 * istetramethyl- 5 ammonium and with 9-18 moles of water when NR 4 * is benzyltrimethylammonium. It has also been found that common sources of silica may be employed in the reaction mixture along with the (hydrocarbyl)ammonium polysilicate hydrate. Non-limiting examples of these secondary sources of silica include amorphous silicas, porous and dense phase silicas, alkali metasilicates, amorphous aluminosilicates, crystalline dense phase alumino- 0 silicates, crystalline porous aluminosilicates, modified zeolites and molecular sieves, as well as, analogous other metallosilicates. In addition, silicon alkoxides, silicon nitrides, and silicon alkyls are also suitable. Preferred among these secondary sources of silica are zeolites X, Y, A, mordenite, ferrierite, and beta, and their corresponding acid forms. Secondary sources of silica are employed in an amount ranging from 1 to 20 weight percent based on the total weight of 5 polysilicate hydrate and alumina sources present. It is noted that the crystalline porous solid produced in the process of this invention will possess a crystalline structure which is different from the structure of the secondary source of silica. For example, if zeolite Y is used as a secondary source of silica, the product produced will have a structure different from zeolite Y. Likewise, if a metallosilicate, such as an aluminosilicate, is used as a source of metal oxide, such as alumina, the structure of the product produced will differ from the structure of the metallosilicate. The mineralization of the source of silica depends upon the ratio of mineralizer to silica in the reaction mixture. Generally, this ratio ranges between 0.04 and 0.50, more preferably, between 0.06 and 0.20. Above the upper ratio of 0.5, when the mineralizer is fluoride, the predominant species formed is hexafluorosilicate ion which may precipitates from the reaction mixture. Below the lower ratio of 0.04, mineralization of the silica may be slow. As noted hereinbefore, a metal oxide may be required in the process of this invention. Non-limiting examples of suitable metal oxides include the metal oxides of Groups 2 through 14 of the Periodic Table of the Elements, published and copyrighted by CRC Press, Inc., 1994. Preferably, the metal oxide is selected from the group consisting of the metal oxides of aluminum, gallium, titanium, zirconium, vanadium, magnesium, boron, iron, nickel, cobalt, phosphorus, and mixtures thereof. More preferably, the metal oxide is an oxide of aluminum, boron, gallium, or titanium. Most preferably, the metal oxide is alumina. Any source of metal oxide is acceptable for the process of this invention provided that the source is reactive in the reaction mixture. Suitable sources of metal oxide include the elemental metals, metal nitrides, metal hydrides, metal alkoxides, metal halides, metal phosphates, amorphous and crystalline metal oxides, and metallosilicates, as well as organometallic compounds, such as metal alkyls. For the most preferred metal oxide, which is alumina, suitable sources include aluminum nitride, aluminum metal, aluminum hydride, aluminum alkoxides, aluminum halides, aluminum phosphates, amorphous and crystalline aluminas, aluminates, and aluminosilicates. Preferably, the source of alumina is aluminum nitride or porous aluminosilicates. More preferably, the source of alumina is aluminum nitride, heretofore unknown as a reagent for the production of crystalline porous solids. The amount of metal oxide employed in the process of this invention can vary widely. Specifically, the molar ratio of metal oxide to silica in the reaction mixture, derived from the source of silica and the source of metal oxide, can range from 0 to 1. (The corresponding silica to metal oxide molar ratio ranges from 1 to infinity.) When the metal oxide/silica ratio is 0, a siliceous material is obtained containing less than 1000 ppm metal oxide. On the other hand, the presence of metal oxide in the reaction mixture does not ensure that the corresponding metal will be incorporated into the crystalline porous solid which is formed. In those cases where the metal oxide is a desired part of the product, the molar ratio of metal oxide to silica in the reaction mixture preferably ranges between 0.01 and 0.25. Additional cations may also be added to the reaction mixture. The cations may function in a charge-balancing capacity or as structure-directing agents. Non-limiting examples of additional cations include the alkali (Group 1), alkaline earth (Group 2), and transition metal ions of the Periodic Table. Any source of these additional cations may be employed provided that the source can be solubilized in the reaction mixture. Suitable sources of these cations include the carbonate, halide, sulfate, nitrate, acetate, silicate, aluminate, phosphate, oxalate, and carboxylic salts. Other charge-balancing or structure-directing agents may also be added to the reaction mixture. Ammonia, itself, can act as a template or stabilizer and a source of charge- balancing ammonium ions. Alternatively, ammonium ions can be introduced into the reaction mixture as the silicate, aluminate, phosphate, halide, sulfate, nitrate, acetate, oxalate, or carboxylate salt. Other suitable sources include alkylammonium salts, such as the halides, preferably wherein each alkyl group contains from 1 to 20 carbon atoms, and more preferably, from 1 to 6 carbon atoms. Illustrative of these cations are tetramethylammonium, tetraethylammonium, isopropylammonium, dipropylammonium, tetrapropylammonium, tetrabutylammonium, benzyltrimethylammonium, typically available as the halides. Another source of structure-directing agents and charge-balancing ions includes alkylamines, which can serve as precursors to the in situ formation of alkylammonium ions. Any amount of structure-directing agent is suitable provided that a crystalline porous solid is formed. Typically, the molar ratio of structure-directing agent to total framework-forming elements excluding oxygen (silicon and metal, for example, aluminum) ranges in the reaction mixture from 0 to 2, more preferably, from 0.5 to 2.0. Charge-balancing cations should be added in an amount sufficient to provide overall charge neutrality in the crystalline porous solid. While the intention of this invention is to grow crystalline porous solids in a reaction medium which is predominantly ammonia, the presence of water in the reaction medium is not excluded. For the purposes of this invention the molar ratio of ammonia to water must be equal to or greater than 4. Preferably, the ammonia/water molar ratio is greater than 5, more pre erably, greater than 6, even more pre erably, greater than 7. Preferably, the ammonia/water molar ratio is no greater than 26. Most preferably, the ammonia/water molar ratio ranges between 7 and 26 corresponding to an ammonia concentration between 88 and 96 mole percent, based on the total moles of ammonia and water. By contrast, saturated aqueous ammonium hydroxide contains between 25 and 30 mole percent ammonia, based on the total moles of ammonia and water. It is noted that the ammonia/water molar ratio measures the water which is added to the reaction mixture either as free water or as combined water, such as water of crystallization or water adsorbed on the reagents. Once the reaction mixture is prepared, however, it is usually not known whetherthe water remains as free water or combined water or whether the water is removed by reaction with one of the reagents. If desired, a seed crystal may be added prior to closing the reactor. Seed crystals are employed in the reaction mixture in an amount ranging from 0.01 to 20 weight percent based on the total weight of other silica and alumina sources. Seed crystals direct the synthesis of a composition which is identical to the seed crystal. The nutrients, mineralizer, optional charge-balancing cation and structure- directing agent, any additional water, and seed crystals can be mixed in any order provided that a crystalline porous solid is later produced. The order of addition of the components may determine the crystalline product formed. For example, when a mixture containing polysilicate ions and a lesser amount of zeolite Y is added to a mixture containing ammonium fluoride and aluminum nitride, and then anhydrous ammonia is added, an all-silica beta zeolite is formed. If the polysilicate is first added to aluminum nitride, then zeolite Y is added, and thereafter o ammonium fluoride and anhydrous ammonia are sequentially added, zeolite PI is formed. After the nutrients and other components are added to the reactor, the reactor is cooled to a temperature between -60°C and -30 C C, and liquid ammonia is transferred into the reactor. Thereafter, the reactor is maintained at a temperature and pressure sufficient to effect nucleation and precipitation of the crystalline porous solid. Reactor contents are usually 5 not stirred or agitated. Any reactor designed to withstand high pressure is suitable for the process of this invention, including stainless steel, Hastaloy™, or teflon-lined reactors. The temperature of the process can vary from the boiling point of ammonia (-30°C) to any higher temperature, so long as the reactor can handle the pressure generated. As a general rule, the temperature ranges between 0°C and 200°C, preferably between 100°C 0 and 180°C, and more preferably, between 130°C and 160°C. Pressure is autogenous, and typically ranges from several hundred to several thousand psig. Below 130°C anhydrous ammonia is in the liquid phase, while above 130°C anhydrous ammonia is a supercritical fluid. In the process of this invention the supercritical transition temperature will vary depending upon the specific composition of the reaction mixture. Since the pressure curve in the 5 supercritical phase increases dramatically with small increases in temperature, pressure vessels should be rated accordingly. Crystallization times range from 1 to 15 days, and preferably, from 2 to 9 days. The products of the process of this invention are crystalline porous solids, preferably crystalline microporous and mesoporous solids, suitable examples of which are 0 noted hereinabove. Among the products produced are novel compositions including an all- silica microporous solid designated DCM-7 and represented by the molar composition: Si0 2 : y (C 2 H5)3N : n H2θ wherein y is a number ranging from 0 to 0.5 and n is a number ranging from 0 to 1. DCM-7 exhibits an XRD pattern whose characteristic reflections for Cu-Kα radiation are listed in Table 5 1 * Table 1-X-rav Diffraction Pattern of DCM-7, (Cu-Kα) Relative D-Spacing Intensity (l l 0 ) 7.09 ± 0.2 50.0 4.97 ± 0.2 33.8 4.07 ± 0.2 36.0 3.51 ± 0.2 25.5 3.18 ± 0.2 100.0 2.97 ± 0.2 28.2 2.68 ± 0.2 28.9 2.45 ± 0.2 9.6 2.36 ± 0.2 8.8 2.25 ± 0.2 8.0 2.09 + 0.2 7.8 2.05 ± 0.2 11.8 1.98 ± 0.2 11.9 1.96 ± 0.2 11.3 1.78 ± 0.2 16.9 1.72 ± 0.2 15.9 The pattern shown in Table 1 is essentially identical tothe pattern given for zeolite P1 by R. von Ballmoos and J. B. Higgins, eds., in Zeolites: Collection of Simulated X-Ray Diffraction Powder Patterns for Zeolites, Butterworth-Heineman, Stoneham, MA, 1990, p. 406S. The water and triethylamine (TEA) molecules occupy the void spaces within the crystalline structure and can be removed by heating. Another novel product of the process of this invention is a crystalline microporous solid designated DCM-8 represented by the molar composition: Si0 2 : y' (CH 3 ) 3 N : n' H 2 0 wherein y' is a number ranging from 0 to 0.5 and n' is a number ranging from 0 to 1. DCM-8 exhibits an XRD pattern whose characteristic reflections for Cu-Kα radiation are listed in Table 2. Table 2-X-ray Diffraction Pattern of DCM-8, (Cu Kα) The XRD pattern shown in Table 2 is essentially identical to the pattern listed for zeolite beta by R. Von Ballmoos and J. B. Higgins, eds., in Zeolites: Collection of Simulated X-Ray Powder Patterns for Zeolites, op. cit., p. 514S. The aluminum concentration of the novel composition is less than 50 ppm, as determined by X-ray fluorescence. Upon calcination, the trimethylamine is lost and the composition reduces to: Si0 2 : n' H 2 0 wherein n' ranges from Oto 0.05. A third novel product of the process of this invention is a crystalline microporous solid designated DCM-9 represented in the as-synthesized form by the molar composition: x" Si0 2 : Al 2 0 3 : y" (CH 3 ) 4 N * : n" H 2 0 wherein x" is a number ranging from 12 to 20, y" is 2.0, and n" ranges from 1 to 5. DCM-9 exhibits an XRD pattern whose characteristic reflections for Cu-Kα radiation are listed in Table 3. Table 3-X-ray Diffraction Pattern of DCM-9 , (Cu Kα) Relative Relative D-Spacing Intensity D-Spacing Intensity (Cont.) (l/lo) (l/lo) (Cont.) 0 6.28 ± 0.2 33 2.38 ± 0.2 3 4.45 ± 0.2 40 2.23 ± 0.2 6 3.96 ± 0.2 8 2.10 ± 0.2 10 3.63 ± 0.2 100 1.90 ± 0.2 8 2.82 ± 0.2 14 1.75 ± 0.2 17 5 2.57 ± 0.2 19 The XRD pattern shown in Table 3 is essentially identical to the pattern listed for TMA-sodalite by R. Von Ballmoos and J. B. Higgins, eds., in Zeolites: Collection of Simulated X-Ray Powder Patterns for Zeolites, op. cit., p.479S. The following examples are illustrative of the process and compositions of this 0 invention, but should not be construed to be limiting thereof. Preparation of tetraethylammonium polysilicate hydrate of composition [(C, HQ-,N Si.;Oι*-l nH,0 A solution comprising 35 weight percent tetraethylammonium hydroxide 5 (TEAOH, 1 L) was heated to 80-90°C, and fumed silica (144 g, Aerosil* grade) was added with vigorous stirring. The mixture was stirred for several hours until clear, then cooled to ambient temperature, and refrigerated. A large mass of waxy solid was collected by filtration. The solids were dried over calcium sulfate in a desiccator for 3 weeks, and then ground into a powder to yield [(C 2 H 5 )4N] 6 [Si6θιs] nH 2 0. The degree of hydration was determined by thermal Q gravimetric analysis (TGA). Example 1 - Synthesis of Crystalline Porous Silica DCM-7 A reaction mixture was prepared by mixing tetraethylammonium polysilicate (TEADDR) hydrate of composition (193 g; 0.125 mole TEADDR; 2.44 moles H 2 0), synthesized as described hereinabove, with ammonium fluoride (4.6 g. 0.124 mole). The mixture was transferred to a stainless steel autoclave (1 L) and cooled to -50°C. To 5 the mixture, liquid ammonia (383 g, 22.5 moles) was added, and the contents were well mixed. The reactor was sealed, removed from the cold bath, and left standing for 2 hr. The NH3 H2O molar ratio was 9.2 corresponding to 90 mole percent ammonia. Thereafter, the reactor was heated to 150°C over a 3 hr period, and allowed to stand at that temperature for 5 days. The internal pressure to 1500 psig over the course of the reaction. The reactor was then cooled to ambient temperature, the ammonia was vented, and the reactor was purged with nitrogen. A dry powder was removed from the reactor, washed with water, and dried at 85°C. Analysis by XRD (Cu Kα radiation), as set forth in Table 1 , showed that the solid was isostructural with zeolite Na-P1. The molar composition of the product, as synthesized, is: Siθ2 : 0.1 (C 2 H s )3N : 0.6 H 2 O The water and triethylamine molecules comprised 13.1 wt percent and 11.9 wt percent, respectively, of the product, as determined by TGA, and occupied the void spaces within the crystalline structure. Water desorption occurred at about 100°C and removal of triethylamine was achieved by calcination above 400°C. Preparation of tetramethylammonium polysilicate hydrate of composition f(CH /tNl s fSi a Q ? nl nH 7 0 A 2.0 M solution of tetramethylammonium hydroxide (TMAOH) was prepared by diluting a 25 weight percent solution of TMAOH (729.2 g) with deionized water to 1 L volume. The solution was heated to between 80 to 90°C, and fumed silica (120 g, Aerosil ® grade) was added in portions with strong stirring. The resulting cloudy solution was stirred for several hours at temperature until clear. The solution was cooled to ambient and refrigerated. Crystallization produces a large mass of colorless needles. The needles were collected by filtration, and the mother liquor was concentrated to two-thirds of the original volume by heating. A second crop of colorless crystals was collected, and the mother liquor was discarded. The crystals were dried over several days exposed to ambient or controlled humidity atmosphere. The dry, opaque/white solids were ground to a fine powder to yield [(CH 3 ) 4 N]8[Siβθ2o] nH 2 0. The degree of hydration, determined by TGA, was varied by controlling the relative humidity of the atmosphere during drying. Example 2 - Preparation of Zeolite P1 A reaction mixture was prepared by mixing tetramethylammonium polysilicate (TMADVR) hydrate of composition C32H 96 N 8 Si 8 θ2o-30 H 2 0 (125 g; 0.0745 mole TMADVR; 2.23 g H 2 0), synthesized as described hereinabove, with aluminum nitride (12.2 g, 0.3 mole). To this mixture zeolite HY (15.4 g, Conteka CBV-720, 95 wt percent Si0 2 , 5 wt percent Al 2 θ3) was added, and thereafter ammonium fluoride (1.8 g, 0.048 mole) was added. The mixture was transferred into a stainless steel autoclave (1 L), cooled to -50°C, and liquid ammonia (305 g, 17.9 moles) was added. The reactor contents were well mixed, and the reactor was sealed. The NH3/H2O molar ratio was 7.8 corresponding to 89 mole percent ammonia. After about 2 hr, the reactor was heated to 150°C over a 3-4 hr period with the internal pressure rising to near 1800 psig. After 5 days the reactor was cooled to ambient, the ammonia vented, and the reactor purged with nitrogen. A solid was collected, washed with an excess of water, and dried at 85°C. The solid was identified by XRD as zeolite P1, a crystalline porous aluminosilicate having a Si0 2 /AI 2 θ3 molar ratio of 4.8. As synthesized, the zeolite was in the tetramethylammonium form. Preparation of benzyltrimethylammonium polysilicate hydrate of composition r(C 7 H7)(CH,),N- R rSi R 0 ? nl-nH,0 A 1.2 M solution of benzyltrimethylammonium hydroxide (BTMAOH) was prepared by diluting 40 weight percent BTMAOH solution (500 g) with deionized water to 1 L volume. The solution was heated to 80-90°C, and fumed silica (72 g, Aerosil ® grade) was added in portions while stirring vigorously. The mixture was stirred for about 40 min until clear, and then cooled to approximately 40°C. The solution was filtered, and the filtrate was o concentrated to two-thirds volume by heating. After cooling to ambient and overnight refrigeration, a large mass of colorless plate-like crystals was obtained. The crystals were collected by filtration, and the mother liquor was concentrated to two-thirds volume by heating. A second crop of colorless crystals was collected, and the mother liquor discarded. The crystals were dried over several days exposed to ambient atmosphere, and then the dry, 5 opaque/white solids were ground to a fine powderto yield [( 7 H 7 )(CH3)3 ] 8 [Si8θ2ol nH 2 0. The degree of hydration was determined by TGA. Example 3 - Preparation of Dodecasil 3C A reaction mixture was prepared in an autoclave (1 L) by mixing benzyltrimethylammonium polysilicate (BTMADVR) hydrate of composition 0 CβoH βNβSiβOzo-lβ H 2 0 (145.7 g; 0.07 mole BTMADVR; 1.3 moles H 2 0), synthesized as described hereinabove, with ammonium fluoride (3.4 g, 0.09 mole). The mixture was cooled to -50°C, and liquid ammonia (286 g, 16.8 moles) was added. The contents were mixed, and the reactor was sealed. The NH3/H 2 0 molar ratio was 13 corresponding to 93 mole percent ammonia. After about 30 min., the reactor was heated to 150°C overa 1.5 hr period. Internal 5 pressure rose to between 1500 and 1600 psig. After 9 days the reactor was cooled, the ammonia vented, and the reactor purged with nitrogen. A white solid was recovered, washed with water, and dried at 85 C C. The solid was identified by XRD as dodecasil 3C, a polyhedral cage-containing silica. Example 4 - Preparation of Dodecasil 3C 0 A reaction mixture was prepared in an autoclave (1 L) by mixing ammonium fluoride (3.2 g, 0.09 mole) with water (26.3 g, 1.46 moles). To the mixture was added benzyltrimethylammonium polysilicate (BTMADVR) hydrate of composition C 8 oHi2 8 8 Si 8 θ2o 9 H 2 0 (125 g; 0.065 mole BTMADVR; 0.59 moles H 2 0), synthesized as described hereinabove. The mixture was cooled to -50°C, and liquid ammonia (266 g, 15.6 moles) was added. The 5 contents were mixed, and the reactor was sealed. The NH3/H2O molar ratio was 7.6 corresponding to 88 mole percent ammonia. The reactor was heated to 150°C. Internal pressure rose to about 1200 psig. After 7 days the reactor was cooled, the ammonia vented, and the reactor purged with nitrogen. A white solid was recovered, washed with water, and dried at 85°C. The solid was identified by XRD as dodecasil 3C, a polyhedral cage-containing silica. Example 5 - Preparation of Crystalline Porous Silica DCM-8 A first reaction mixture was prepared in an autoclave (1 L) by mixing tetramethylammonium polysilicate (TMADVR) hydrate of composition C3 2 Hg6N8Si8θ2o 28 H 2 0 (125 g, 0.0763 mole TMADVR, 2.1 moles H 2 0) with zeolite HY (15.4 g, Conteka CBV-720, 95 wt percent Siθ2, 5 wt percent AI2O3). Aluminum nitride (12.5 g, 0.3 mole) and ammonium fluoride (1.9 g, 0.05 mole) were mixed together and then added to the first reaction mixture. The combined mixture was cooled to -50°C, and liquid ammonia (312 g, 18.31 moles) was added. The NH3/H2O molar ratio was 8.4 corresponding to 89 mole percent ammonia. The contents were mixed, and the reactor was sealed. The reactor was heated to 150°C. Internal pressure rose to nearly 2500 psig. After 5 days the reactor was cooled, the ammonia vented, and the reactor purged with nitrogen. The solid product was washed with water and dried at 85°C. The XRD pattern is set forth in Table 2. The data in Table 2 are consistent with DCM-8 being isostructural with zeolite beta. Elemental analysis indicates a composition comprising Si0 2 : 0.1 (CH 3 ) 3 N : 0.04 H 2 0 The aluminum concentration was less than 50 ppm by weight, as determined by X-ray fluorescence. Upon calcination at 550°Cthe composition reduced to Siθ2 : 0.05 H 2 0. The composition was stable in air at 800°C. Example 6 - Preparation of Crystalline Porous Solid: DCM-9 A reaction mixture was prepared by mixing tetramethylammonium polysilicate (TMADVR) hydrate of the composition C3 2 H9 6 N 8 Si8θ2o 28 H 0 (143 g, 0.0875 mole TMADVR, 2.4 mole H 2 0), synthesized as described hereinabove, with ammonium fluoride (4.6 g, 0.12 mole). Then, aluminum nitride (3.1 g, 0.076 mole) and HY zeolite (15 g, Conteka CBV-720, 95 wt percent Si0 2 , 5 wt percent AI2O3) were added. The mixture was transferred to a stainless steel autoclave (1 L), and cooled to -50 β C. Liquid ammonia was added (384 g, 22.5 moles), and the contents were mixed and the reactor sealed. The NH3/H 2 0 molar ratio was 9.1 corresponding to 90 mole percent ammonia. After about 30 min the reactor was heated to 150 C C over a 1.5 hr period with the internal pressure rising to near 1400 psig. After 5 days the reactor was cooled, the ammonia vented, and the reactor purged with nitrogen. A powder was collected, washed with excess water, and dried at 85°C. The powder exhibited the XRD pattern shown in Table 3 and was identified as TMA-sodalite, a clathrasil cage-containing alumino¬ silicate having the composition: 16.9 Si0 2 : Al 2 0 3 : 2.2 (CH 3 ) 4 N + : 1.7 H 2 0 The Si0 2 /AI θ3 molar ratio was 16.9. Example 7 - Preparation of Octadecasil A reaction mixture was prepared by mixing tetramethylammonium polysilicate (TMADVR) hydrate of the composition C32Hg 6 N 8 Si 8 θ2o 31 H 2 0 (160 g, 0.094 mole TMADVR, 2.9 mole H 2 0), synthesized as described hereinabove, with ammonium fluoride (4.6 g, 0.124 mole). The mixture was transferred to a stainless steel autoclave (1 L), and cooled to -50 C C. Liquid ammonia was added (384 g, 22.5 moles); the contents were mixed, and the reactor was sealed. The NH3/H2O molar ratio was 7.8 corresponding to 88 mole percent ammonia. After about 30 min, the reactor was heated to 150°C over a 1.5 hr period with the internal pressure rising to near 1200 psig. After 9 days the reactor was cooled, the ammonia vented, and the reactor purged with nitrogen. A powder was collected, washed with excess water, and dried at 85°C. The powder was identified by XRD as octadecasil, a polyhedral cage-containing silica. Example 8 - Preparation of Zeolite Na-1 Tetramethylammonium polysilicate hydrate of composition [(CH3) 4 N] 8 [Si 8 θ2o] 23H 2 0 (8.0 g), ammonium fluoride (0.12 g), and sodium fluoride (0.14 g) were loaded into an autoclave and cooled to -50°C. Liquid ammonia was added (21 g), the contents were mixed, and the reactor was sealed. The NH3/H 2 0 molar ratio was 6. The reactor was heated to 150°C and maintained for 3 days. Thereafter, the reactor was cooled, and the ammonia was vented. A powder was collected and identified by XRD as zeolite Na-1 , a clathrasil.

Claims: WHAT IS CLAIMED IS: 1. A process of preparing a crystalline porous solid selected from the group consisting of silicas and metallosilicates, the process comprising preparing a mixture containing: (a) ammonia, (b) water in an amount such that the molar ratio of ammonia to water is greater than 4 and less than 26, (c) one or more nutrients comprising a (hydrocarbyl)polysilicate hydrate salt, and o optionally, a source of a metal oxide which is reactive in the reaction mixture, and optionally, a source of an additional cation which is reactive in the reaction mixture, the relative amounts of the nutrients being sufficient to form the crystalline porous solid, and (d) a mineralizer in an amount sufficient to mineralize the nutrient(s); 5 and maintaining the resulting mixture at a temperature and for a time sufficient to produce the crystalline porous silica or metallosilicate. 2. The process of Claim 1 wherein the crystalline porous solid is selected from the group consisting of clathrasils, felspars, layered aluminosilicates, aluminosilicate molecular sieves, and silica molecular sieves. 0 3. The process of Claim 1 wherein the molar ratio of ammonia to silicon ranges between 10 and 1000, wherein the molar ratio of mineralizer to silica ranges between 0.04 and 0.50, and wherein the temperature ranges between 0°C and 200°C. 4. The process of Claim 1 wherein the mineralizer is fluoride and the fluoride is obtained from a source of fluoride selected from the group consisting of ammonium 5 fluoride, hydrogen fluoride, sodium fluoride, sodium bifluoride, and ammonium hexafluoro¬ silicate. 5. The process of Claim 1 wherein the polysilicate ion is selected from the group consisting of SiβOi s *6 , Si 8 θ2o" 8 and Siιo0 2 5" 10 and wherein the metal oxide is selected from the group consisting of the oxides of aluminum, gallium, titanium, magnesium, boron, 0 iron, nickel, cobalt, vanadium, zirconium, phosphorus, and mixtures thereof. 6. The process of Claim 5 wherein the metal oxide is alumina which is obtained from a source of alumina selected from the group consisting of aluminum metal, aluminum nitride, aluminum hydride, aluminum alkoxides, aluminum halides, aluminum phosphates, amorphous and crystalline aluminas, aluminates, and aluminosilicates. 5 7. The process of Claim 1 wherein a source of an additional cation is employed as a charge-balancing cation or as a structure-directing agent; or wherein a secondary source of silica is present and is selected from the group consisting of crystalline and amorphous silicas, porous and dense phase crystalline silicas, alkali metasilicates, amorphous aluminosilicates, crystalline dense phase aluminosilicates, and aluminosilicate molecular sieves; or wherein a seed crystal is added to the reaction mixture. 8. A crystalline microporous silica having a composition represented by Si0 2 : y (C 2 H 5 ) 3 N : n H 2 0 wherein y is a number ranging from 0 to 0.5 and n is a number ranging from 0 to 1 , the silica being isostructural with zeolite P1 as determined by X-ray diffraction. 9. A crystalline microporous silica having a composition represented by Si0 2 : y' (CH 3 ) 3 N : n' H 2 0 wherein y' is a number ranging from 0 to 0.5 and n' is a number ranging from 0 to 1 , the silica being isostructural with zeolite beta as determined by X-ray diffraction. 10. A crystalline microporous aluminosilicate having a composition represented by: x" Si0 2 : Al 2 0 3 : y" (CH 3 ) 4 N * : n" H 2 0 wherein x" is a number ranging from 12 to 20, y" is-2.0 and n" ranges from 1 to-5, the aluminosilicate being isostructural with sodalite as determined by X-ray diffraction.

Inventors: GARCES JUAN M, HOWARD KEVIN E, MILLAR DEAN M, GARCES, JUAN, M., HOWARD, KEVIN, E., MILLAR, DEAN, M.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1995
Main classification: C01B37
IPC codes: C01B33, C01B37, C01B39