PROCESS FOR PRODUCING RUBBER MODIFIED RUBBER CEMENT

Abstract: A process for preparing a homogeneous asphalt product which is a two-member composition of distillation tower bottoms and ground tire rubber homogenized therein includes, in one embodiment, introducing distillation tower bottoms at a temperature of about 425 DEG -470 DEG F to a vessel through which air is flowing at about 6-15 psi pressure, introducing ground tire rubber to the vessel and bombarding the distillation tower bottoms and ground tire rubber with the air until the mixture is completely and stably homogenized, and recovering the homogenized asphalt composition. In another embodiment, the ground tire rubber is mixed directly with the distillation tower bottoms to form a wetted mixture which is bombarded with air at a temperature of about 350 DEG -485 DEG F at about 6-15 psi pressure until the mixture is completely and stably homogenized. The homogenized asphalt composition is then recovered.

Description: "PROCESS FOR PRODUCING RUBBER MODIFIED RUBBER CEMENT" Field of the Invention A process for preparing tire rubber modified asphalt cement systems by incorporating ground tire rubber into distillation tower bottoms using bombardment by air to make a homogeneous asphalt cement system, and products thereof. Background of the Invention Processes for incorporating ground tire rubber into bituminous material to make asphalt cement systems suitable for paving, roofing and other uses have hitherto been unduly complex and thus costly in use. Known processes use additional constituents of the composition and additional process steps in an attempt to provide a homogeneous system. Such attempts have not been successful. Duong et al., U.S. Patent No. 5,270,361, is directed to a process for making an asphalt composition which includes synthetic or natural rubber which may be in particles of up to one-half inch in thickness. Elemental selenium or an organo- selenium compound is added into the mixture to act as SDBSTΠUTESHEΠ ( ULE26) a substitute for the sulfur which is removed during the vulcanization process. The selenium or organo- selenium compound acts as a cross-linking agent. The composition is treated with pressurized air in a dehydrogenation reaction. In the dehydrogenation vessel, the dispersing device includes a pair of discs turning at 3600 rpm which promotes homogenization and acceleration of the dehydrogenation reaction. Elemental selenium or an organo-selenium compound is added into the homogenized composition and mixed in a static mixer. The asphalt composition is then recovered and stored in a container at about 150 to 175"C. Wilkes, U.S. Patent No. 4,609,696, describes a rubberized asphalt composition which is made by combining asphalt with a hydrocarbon oil to provide a homogenized asphalt-oil mixture or solution, combining the mixture with particulate rubber to provide a homogeneous gel and emulsifying the gel by passing the asphalt-rubber-oil gel, with water, through a colloid mill. Oliver, U.S. Patent No. 4,430,464, describes a pavement binder composition in which rubber particles are digested in a bituminous material. McDonald, U.S. Patent Nos. 4,069,182 and 3,891,585, describe an elastomeric pavement repair composition and a method for making the composition. Winters et al., U.S. SϋKWESEErp-126) Patent No. 3,919,148, also describes an elastomeric paving material. Pagen et al., U.S. Patent No. 4,588,634 describes a roofing material using bitumen and ground tire rubber together with mineral stabilizer and an elastomeric polymer composition. Air bombardment is not used. Summary of the Invention The invention provides a process for preparing homogenized tire rubber modified asphalt cement systems and products thereof which have only two components, distillation tower bottoms (DTB) and ground tire rubber (GTR) . No chemicals or special aromatic oils or additives are needed in this process. According to the process, a single stage of dehydrogenation accomplishes stable combination of the tire rubber and bituminous residue by bombarding with a high volume of air under pressure. The two components are combined into a new composite which is completely homogenized and is stable. The homogenized asphalt composition product does not separate or degrade even over a long period of time. The asphalt composition is useful in the paving and roofing industries. The process may be a one-stage process or a two stage process. The two components are combined into a new composite which is completely homogenized and is stable. The homogenized asphalt composition product does not separate or degrade even over a long period of time. The asphalt composition is useful in the paving and roofing industries. The dehydrogenation is carried out in a reactor having a stationary air spider located at the bottom of the reactor. The base oil is distillation tower bottoms (DTB) which is the bituminous residue after vacuum distillation, atmospheric distillation, steam stripping of petroleum or other processes known to those skilled in the art. The ground tire rubber (GTR) is recycled rubber obtained from grinding scrap vulcanized rubber tires, tubes, etc. Ground tire rubber is loaded into the DTB in an amount ranging from 1% to 27%, preferably about 10-16%, and most preferably about 12%. The GTR may be sized from a powder grind (about 200 mesh or less) up to about 20 mesh. The air volume input through the stationary air distributing spider-shaped device may range from about 1600 to about 2800 cfm and from about 6 psi to about 15 psi, preferably about 2200 cfm at about 10 psi. SUBSTITUTE SEEF (RULE 26) In the one-stage process, the ground tire rubber and distillation tower bottoms are added into a converter and bombarded with air under increased temperature and pressure so that the ground tire rubber is abrasively absorbed into the distillation tower bottoms in the converter. The wetting process and dehydrogenation process takes place in a single step, using a two-component blend of distillation tower bottoms (DTB) and ground tire rubber (GTR) which are combined in a single stage which takes place in the converter. No special blending is needed prior to or following the process of dehydrogenation. The dehydrogenation is carried out by bombarding with air at about 2200 cfm at about 10 psi at a temperature of about 425-470°F. The total dehydrogenation time is about 2 to 8 hours. In the two-stage process, the process includes a wetting process and a dehydrogenation process, using a two-component blend of distillation tower bottoms (DTB) and ground tire rubber (GTR) . Like the one- stage process, no special blending is needed prior to or following the process of dehydrogenation. The dehydrogenation is carried out by bombarding with air at 2200 cfm at 10 psi with a beginning temperature of about 350"F and an ending temperature of about 485°F. The total dehydrogenation time is about 2 to 6 hours. Brief Description of the Drawings Figure 1 illustrates, schematically, apparatus used in a one-stage process of the invention. Figure 2 illustrates, schematically, apparatus used in a two-stage process of the invention. Detailed Description of the Preferred Embodiments The invention advantageously provides an asphalt composition which incorporates a bituminous residue, such as distillation tower bottoms (DTB) in a homogeneous mixture with ground tire rubber (GTR) for use in the roofing and paving industries or otherwise as will be apparent to one skilled in the art. The two-component asphalt composition produced is simple and economical to prepare. The product is a completely homogenized asphalt composition in which the ground tire rubber is fully incorporated into the distillation tower bottoms. The resulting composition is stable and does not separate out. No additives need to be used. Only distillation tower bottoms and ground tire rubber are used in preferred embodiments of the process. According to a one-stage process of the invention, compressed air is pumped into an empty converter, distillation tower bottoms are transferred from a storage vessel, where it is maintained at about 350°F., into the converter while the air is being pumped into the converter. After the distillation tower bottoms are in the converter, the ground tire rubber is pumped, pneumatically, into the converter. The air is constantly flowing throughout the entire process. The temperature in the converter is about 425-470°F., preferably about 450"F., and the distillation tower bottoms and ground tire rubber are bombarded by the compressed air in the converter to allow abrasive absorption of the asphaltic oils of the distillation tower bottoms into the ground tire rubber and complete digestion of the ground tire rubber into the distillation tower bottoms. The finished product is of a single composition and is a stable homogeneous product. The process is conducted in a closed system that is vented through a knockout tank with a liquid seal, followed by a dry tank, and the vapor recovery is concluded by incineration in an incinerator which is maintained at a minimum temperature of 1325°F. The finished product is transferred from the converter and shipped for storage or blended and incorporated into other products. The finished product and any blends thereof may be stored and handled at 350°F. In the converter, the ground tire rubber is "wetted" with the distillation tower bottoms while being bombarded with a high volume of air which causes intimate mixing of the rubber molecules and bituminous molecules causing dehydrogenation of the rubber and complete and stable homogenization of the resulting composition. Lower hydrocarbon oils are driven off and a completely homogenized asphalt composition which is the product of the process remains in the dehydrogenation vessel. In the two-stage process of the invention, the ground tire rubber is "wetted" with the distillation tower bottoms and passed into a dehydrogenation vessel in which the wetted mixture is bombarded with a high volume of air which causes intimate mixing of the rubber molecules and bituminous molecules causing dehydrogenation of the rubber and complete and stable homogenization of the resulting composition. Lower hydrocarbon oils are driven off and a completely homogenized asphalt composition which is the product of the process remains in the dehydrogenation vessel. Figure 1 illustrates the one-stage process of the invention, schematically. Distillation tower bottoms (DTB) are stored in vessel 2. A charge of DTB is pumped directly into converter 4 together with a charge of ground tire rubber (GTR) fed from hopper 6. The GTR may be sized from a powder grade (about 200 mesh or less) up to about 20 mesh. In a typical application, the GTR is present in a ratio of 1:99 to 27:33 with respect to DTB, preferably in a ratio of 10:90 to 16:84 and most preferably about SUB§K SIET(RULE26) 12:88 with respect to DTB. Pressurized air is fed from air compressor 8 at 1600 to 2800 cfm and a pressure of 6 to 15 psi through conduit 10 and stationary spider device 12 which allows the pressurized air to enter the bottom of converter 4, in which dehydrogenation takes place. In a preferred embodiment, the air is pumped into converter 4 through the stationary spider device 12 at 2200 cfm and 10 to 15 psi. As the air bombards the mixture in converter 4, a dehydrogenation process takes place. The dehydrogenation process takes place by injecting air at, for example, 2200 cfm into the bottom of the vessel through the stationary air spider and maintaining the air flow at 10 psi throughout the process. The temperature in the converter is held at about 425-470° F during the process. The temperature and airflow are maintained until the targeted softening point is achieved. The material may be sampled every 30 minutes, or as otherwise known to one skilled in the art. The duration of the process may be about 2 to 14 hours for reaching the targeted softening point. Once the targeted softening point is reached, the air and heat are shut off and the finished product, which is completely homogeneous is transferred through conduit 14 using a finished product pump (not shown) to the finished product storage. Hydrocarbons released in the dehydrogenation tank are passed to a hydrocarbon collection and vapor recovery area through conduit 16 to knockout tank 18 and dry tank 20. The vapor recovery system takes place through conduits 22, 24, 26. In one example, any remaining uncondensed hydrocarbons are burned in incinerator 28 using a gas fired burner at a temperature of about 1325°F, minimum. Throughput of the process may be 100 to 500 tons per day using one converter or otherwise as known to one skilled in the art. Other equipment may be used to achieve a similar result. The examples describe preferred embodiments. A typical sample of DTB may have the following properties: Viscosity at 140°F (poises) 15-50 ps ASTM 2171 Softening point of flint 40-70°F ASTM D113 Flash point, °F, min. COC 560°F ASTM D92 Example 1 - PAVING GRADE, 15% CONCENTRATE A full volume of air, 2200 cfm at 10 psi, was initiated into a reactor. The reactor was then charged with 70.5 tons of DTB, at 350°F. The air volume and pressure was maintained and the air flow continued at 2200 cfm at 10 psi throughout the entire process. After the desired amount (70.5 tons) of DTB was transferred, GTR was pneumatically pumped into the liquid level of the DTB in the reactor. The agitation action of the air into the materials provided an excellent mixture of the GTR and DTB. To charge 12.44 tons of GTR into 70.5 tons DTB takes approximately 80 minutes. The reactor is heated to no more than 470°F and no less than 425 β F. Once the desired temperature is achieved samples are pulled every hour until the desired softening point of 230°F is achieved. Once the targeted softening point is achieved, the air and heat are shut off and the process is completed. The targeted softening point was achieved after 12 hours and 30 minutes. The finished material is pumped into a vessel for downblending and polymer modification process. Once downblended to a 5% GTR concentrate, using AC-5 and modified with synthetic rubber, the final material is transferred to a holding vessel for shipment. The physical characteristics of the downblended material are shown in Table 1. TABLE 1 AC-15-5TR PAVING GRADE ASPHALT CEMENT Dse in Chip Seal Applications TESTS RESULTS ASTM METHOD Viscosity @ 140"F, Poises 3700 ps ASTM D2171 SUBSTTTUTE SHEET (P.ULE 26) TESTS RESULTS ASTM METHOD Viscosity § 275°F, Poises 6.5 ps Texas Item 300 Penetration § 77°F lOOg, 5 sec, dmm 116 ASTM D5 Softening Point, °F 126°F ASTM D36 Flash Point, °F, COC 555°F ASTM D92 Ductility @ 39.2°F 5 cm/min, cm 44.0 cm ASTM D113 Storage Stability 48 hrs § 325°F Softening Point difference between Top and Bottom 0.5% Texas Item 300 Example 2 - PAVING GRADE 15% CONCENTRATE A full volume of air, 2200 cfm at 10 psi, was initiated into a reactor. The reactor was then charged with 75.6 tons of DTB, at 350°F. The air volume and pressure is maintained and continues to flow throughout the entire process. After the desired amount of DTB was transferred, the GTR was pneumatically pumped into the liquid level of the DTB in Reactor 2. The agitation action of the air into the materials provided an excellent mixture of the GTR and DTB. To charge 13.34 tons of GTR takes approximately 90 minutes. The reactor is heated to no more than 470°F and no less than 425°F. Once the desired temperature is achieved samples are pulled every hour until the desired softening point of 230°F is achieved. Once the targeted softening point is achieved, the air and heat are shut off and the process is completed. The targeted softening point was achieved after 13 hours and 10 minutes. The finished material is pumped into a vessel in preparation for the downblending and polymer modification process. Once downblended to a 5% GTR concentrate, using AC-20 and modification with synthetic rubber, the downblended material is transferred to a holding vessel for shipment. The physical characteristics of the downblended material are shown in Table 2. TABLE 2 AC-45-5TR PAVING GRADE ASPHALT CEMENT Use in Hot Mix Applications TESTS RESULTS ASTM METHOD Viscosity @ 140°F, Poises 5664 ps ASTM D2171 Viscosity § 275°F, Poises 11.0 ps Texas Item 300 Penetration @ 77°F lOOg, 5 sec, dmm 70 ASTM D5 Softening Point, °F 127°F ASTM D36 Flash Point, °F, COC 559°F ASTM D92 TESTS RESULTS ASTM METHOD Ductility @ 39.2°F 5 cm/min, cm 21.5 cm ASTM D113 Storage Stability 48 hrs @ 325°F Softening Point difference between Top and Bottom 0.75% Texas Item 300 Example 3 - ROOFING COATING GRADE @ 5% CONCENTRATE A full volume of air, 2200 cfm at 10 psi, was initiated into a reactor. The empty reactor was then charged with 28.5 tons of DTB, at 350°F. The air volume and pressure is maintained and continues to flow throughout the entire process. After the desired amount of DTB is transferred, the GTR is pneumatically pumped into the liquid level of the DTB in the reactor. The agitation action of the air into the materials provided an excellent mixture of the GTR and DTB. To charge 1.5 tons of GTR takes aprox. 20 minutes. The reactor is heated to no more than 470"F and no less than 425°F. Once the desired temperature is achieved samples are pulled every hour until the desired softening point of 200°F is achieved. Once the targeted softening point is achieved, the air and heat are shut off and the process is completed. The targeted softening point was achieved after 8 hours and 15 minutes. The SUBSTITUTE Sii (Ptl)LE 26) material is transferred to a holding vessel for shipment. The physical characteristics of the material are shown in Table 3. TABLE 3 TRMAC COATING ROOFING GRADE ASPHALT CEMENT Use in Manufacturing of Roofing Shingles and Roll Goods TESTS RESULTS ASTM METHOD Viscosity § 400 β F, Poises 2.68 ps Florida 336-1 Penetration θ 77°F lOOg, 5 sec, dmm 20 ASTM D5 Softening Point, °F 200°F ASTM D36 Flash Point, °F, COC 570°F ASTM D92 Ductility @ 77°F 1 cm/min, cm 6.0 cm ASTM D113 The product of each of the three examples described above is a stable, heat resistant product. The same two-step process was used for each example, with different volumes. The dehydrogenation is achieved without incorporating any chemicals or additional aromatic oils or additives. The process yields material suitable for use in both roofing and paving industries. The different materials have a different proportion of GTR loading in the DTB and a different time of dehydrogenation processing to achieve the different properties required in the final materials. About 1-5% of polymer material such as synthetic rubber is capable of being incorporated together with the GTR into the DTB. Examples of synthetic materials are styrene-butadiene-styrene (SBS) , styrene-butadiene-rubber (SBR) , polyethylene, polyisoprene, polybutylene, polychloroprene (neoprene) , nitrile rubber (acrylonitrile butadiene) , butyl rubber (copolymer of isobutylene and isoprene) polyacrylonitrile and other materials known to one skilled in the art. Use of excess amounts of synthetic rubbers would cause degradation of the synthetic rubber. If an insufficient quantity of air is used or if the residence time in the air bombardment vessel is insufficient, the product is unstable and/or not properly homogeneous and thus is liable to separate out. Figure 2 illustrates a two-stage process of the invention, schematically. Distillation tower bottoms (DTB) are stored in vessel 32. A charge of DTB is pumped by charge pump 34 into wetting vessel 36 together with a charge of ground tire rubber (GTR) fed from hopper 38. The GTR may be sized from a powder grade (about 200 mesh or less) up to about 20 mesh. The DTB and GTR are thoroughly mixed together using stirrer 40, thoroughly wetting the GTR with DTB. In a typical application, the GTR is present in a ratio of 1:99 to 27:33 with respect to DTB, preferably in a ratio of 10:90 to 16:84 and most preferably about 12:88 with respect to DTB. The mixture from wetting vessel 26 is pumped to dehydrogenation vessel 42 using reactor feed pump 44. Pressurized air is fed by pump 46 at 1600 to 2800 cfm and a pressure of 6 to 15 psi through conduit 48 and stationary spider device 50 which allows the pressurized air to enter the bottom of dehydrogenation vessel 42. In a preferred embodiment, the air is pumped into dehydrogenation vessel 42 through the stationary spider device 50 at 2200 cfm and 10 to 15 psi. As the air bombards the mixture in vessel 42, a dehydrogenation process takes place. The dehydrogenation process takes place by injecting air at, for example, 2200 cfm into the bottom of the vessel through the stationary air spider and maintaining the air flow at 10 psi throughout the process. The process starts with a dehydrogenation reactor temperature of 300 to 375°F and the temperature is increased to 485°F during the process. The temperature and airflow are maintained until the targeted softening point is achieved. The SUBSK SfiET(K26) material may be sampled every 30 minutes, or as otherwise known to one skilled in the art. The duration of the process may be about 2 to 6 hours for reaching the targeted softening point. Once the targeted softening point is reached, the air and heat are shut off and the finished product, which is completely homogeneous is transferred using the finished product pump 52 to finished product storage 54. Hydrocarbons released in the dehydrogenation tank are passed to a hydrocarbon collection and vapor recovery area through conduit 56 to knockout tank 58 and condensate tank 60. In one example, any remaining uncondensed hydrocarbons are burned in incinerator 62 using gas fired burner 64 at a temperature of 1500"F. Throughput of the process may be 300 to 400 tons per day using one reactor and one wetting vessel or otherwise as known to one skilled in the art. Other equipment may be used to achieve a similar result. The examples describe preferred embodiments. A typical sample of DTB may have the following properties: Viscosity at 140°F (poises) 15-50 ps ASTM 2171 Softening point of flint 40-70°F ASTM D113 Flash point, °F, min. COC 560°F ASTM D92 Example 4 In laboratory size equipment, 807.5 g DTB is heated to 350° F, 42.5 g GTR is added to the DTB and stirred for one minute until all the dry GTR is incorporated into the DTB. The total mixture is poured into a lab size reactor. 30 Cfm of air at 2 psi is injected into the reactor through a stationary air spider located at the bottom of the vessel. The reactor is heated and maintained at 485°F. Samples are pulled every 30 minutes after the air inflow is initiated. At a targeted 130°F softening point, the air and heat are shut off. The material is drained into a sample can and tested. The physical characteristics of the material produced are shown in Table 1, below. TABLE 4 - PAVING TESTS RESULTS ASTM METHOD Softening Point, °F 131°F ASTM D36 Penetration at 77°F lOOg, 5 sec, dm 68 ASTM D5 Flash point °F, COC 585°F ASTM D92 Viscosity at 140°F (poises) 8500 ps ASTM D2171 Ductility at 39.2°F 5cm/min, cm 6.5 cm ASTM D113 SUBSTπUTESHEET(RULE26) TESTS RESULTS ASTM METHOD Storage Stability 48 hrs at 325°F Softening Point difference between Top and Bottom 1.5% Texas Item 300 Brookfield Viscosity, at 325°F (poises) 3.25 ps Florida 336-1 Storage Stability Long Term, 30 days at 325°F difference between Top and Bottom 3.0% Texas Item 300 Example 5 2550 g DTB is heated to 350° F. 850 g GTR is added to the DTB and stirred for 2 minutes until the GTR is completely wetted and incorporated into the DTB. The mixture is poured into a large lab size reactor. 130 cfm of air at 2 psi is injected into the reactor via a stationary air spider located at the bottom of the vessel. The reactor is heated and maintained at 475° F. Samples are pulled every 30 minutes after initiating the air flow. After the mixture is homogenized and the GTR is dissolved in the DTB, the process is shutdown. The material is drained into a sample can and tested. The physical characteristics are as follows. SUBSTITUTE SHEt (RULE 26) TABLE 5 - ROOFING TESTS RESULTS ASTM METHOD Softening Point, °F 240 β F ASTM D36 Penetration at 77°F lOOg, 5 sec, dmm 18 ASTM D5 Flash point °F, COC 585°F ASTM D92 Viscosity at 140°F (poises) N/A ASTM D2171 Ductility at 39.2°F 5cm/min, cm 1.0 cm ASTM D113 Storage Stability 48 hrs at 400 β F Softening Point difference between Top and Bottom 1.0% Texas Item 300 Brookfield Viscosity, at 400°F, poises 81.45 ps Florida 336-1 Storage Stability Long Term, 30 days at 400 F difference between Top and Bottom 1.0% Texas Item 300 Example 6 70.4 tons DTB is heated to 350 β F. 9.6 tons GTR is added to the DTB through a wetting vessel. GTR is added into the top of the vessel using a top mounted tank mixer to pull the dried GTR into the DTB. The wetting process takes approximately 1.5 hours until the entire amount of GTR is incorporated into the DTB. The mixture is transferred into a dehydrogenation reactor. 2200 cfm of air at 10 psi is injected into the bottom of the reactor via a stationary air spider located at the bottom of the vessel. The air volume and pressure is maintained throughout the entire process. The vapor recovery incinerator is maintained at 1500°F throughout the entire process. The reactor is heated and maintained at 470°F. Samples are pulled every 30 minutes after the process has been operating for two hours. At a targeted 130*^ softening point, the air and heat are shut off and the process is completed. The softening point is achieved after 3 hours and 25 minutes. The finished material is pumped into a holding vessel for shipment and tested. The physical characteristics of the final material are shown in Table 3. TABLE 6 - PAVING TESTS RESULTS ASTM METHOD Softening Point, °F 135°F ASTM D36 Penetration at 77°F lOOg, 5 sec, dmm 62 ASTM D5 Flash point °F, COC 585°F ASTM D92 Viscosity at 140°F, Poises 8600 ps ASTM D2171 Ductility at 39.2 β F 5cm/min, cm 4.5 cm ASTM D113 TESTS RESULTS ASTM METHOD Storage Stability 48 hrs at 325°F Softening Point difference between Top and Bottom 1.5% Texas Item 300 Brookfield Viscosity, at 325°F (poises) 6.75 ps Florida 336-1 Storage Stability Long Term, 30 days at 325"F difference between Top and Bottom 2.0% Texas Item 300 The product of each of the three examples described above is a stable, heat resistant product. The same two-step process was used for each example, with different volumes. The dehydrogenation is achieved without incorporating any chemicals or additional aromatic oils or additives. The process yields material suitable for use in both roofing and paving industries. The different materials have a different proportion of GTR loading in the DTB and a different time of dehydrogenation processing to achieve the different properties required in the final materials. About 1-5% of polymer material such as synthetic rubber is capable of being incorporated together with the GTR into the DTB. Examples of synthetic materials are styrene-butadiene-styrene (SBS) , styrene-butadiene-rubber (SBR) , polyethylene, UBSπfUTE SHEET RUU26 polyisoprene, polybutylene, polychloroprene (neoprene) , nitrile rubber (acrylonitrile butadiene) , butyl rubber (copolymer of isobutylene and isoprene) polyacrylonitrile and other materials known to one skilled in the art. Use of excess amounts of synthetic rubbers would cause degradation of the synthetic rubber. If an insufficient quantity of air is used or if the residence time in the air bombardment vessel is insufficient, the product is unstable and/or not properly homogeneous and thus is liable to separate out. While the invention has been described above with respect to certain embodiments thereof, it will be appreciated by one skilled in the art that variations and modifications may be made without departing from the spirit and scope of the invention. SUBSTTΠJTE SHEET (RULE 26)

Claims: What is claimed is: 1. A process for preparing a homogeneous asphalt composition consisting essentially of the steps of: introducing distillation tower bottoms at a temperature of about 350°-485°F into a vessel; introducing ground tire rubber into the vessel; passing air at about 6-15 psi pressure through the vessel, thereby bombarding the ground tire rubber and distillation tower bottoms in the vessel with the air under pressure to incorporate the ground tire rubber into the distillation tower bottoms; obtaining a stable homogeneous, incorporated asphalt composition of ground tire rubber and distillation tower bottoms. recovering the incorporated asphalt composition. 2. A process according to claim 1, wherein the steps are carried out in the following sequence: passing the air through the vessel; introducing the distillation tower bottoms into the vessel; introducing the ground tire rubber into the vessel in which the distillation tower bottoms are being bombarded with air. SUBSIITiITES!-EEr(-tII]126 3. A process according to one of claims 1 or 2, comprising the following sequential steps: injecting air at about 6-15 psi pressure at a rate of about 1600-2800 cfm for about 2-14 hours through a stationary spider-shaped device mounted in the vessel; introducing about 86-90% distillation tower bottoms at a temperature of about 350°-485°F into the vessel for bombarding with the injected air; and introducing about 10-14% ground tire rubber into the vessel; bombarding the distillation tower bottoms and ground tire rubber in the vessel with the injected air. 4. A process according to claim 1, wherein the steps are carried out in the following sequence: mixing the ground tire rubber with distillation tower bottoms to form a wetted mixture of the ground tire rubber and the distillation tower bottoms; introducing the wetted mixture into the vessel; bombarding the wetted mixture with air at a temperature of about 350°-485"F at about 6-15 psi pressure. 5. A process according to one of claims 1 or 4, comprising the following sequential steps: mixing about 10-14% ground tire rubber with about 86-90% distillation tower bottoms to form a wetted mixture of the ground tire rubber with the distillation tower bottoms; injecting air at a temperature of about 350°-485"F at a flow rate of about 1600-2800 cfm and about 6-15 psi pressure for about 2 to 14 hours through a stationary spider-shaped device mounted in the vessel; bombarding the wetted mixture of ground tire rubber and distillation tower bottoms with the injected air. 6. A process according to one of claims 1, 2 or 4, wherein about 1-27% ground tire rubber is mixed into about 73-99% distillation tower bottoms. 7. A process according to one of claims 1, 2 or 4, wherein about 10-15% ground tire rubber is mixed into about 85-90% distillation tower bottoms. 8. A process according to one of claims 1 to 5, wherein after the ground tire rubber is mixed with the distillation tower bottoms, the temperature of the process is maintained at a temperature of about 425°-475 β F. 9. A process according to one of claims 1, 2 or 4, wherein the air bombardment is carried out for about 2-14 hours. 10. A process according to one of claims 1, 2 or 4, wherein the air bombardment is carried out at about 1600-2800 cfm. 11. A process according to one of claims l to 5, wherein the air bombardment is carried out at about 2000-2400 cfm. 12. A process according to one of claims 1, 2 or 4, wherein the air for bombarding the wetted mixture is injected through a stationary spider- shaped injector device. 13. A process according to claims 1, 2 or 4, wherein the ground tire rubber includes rubber selected from natural rubber and synthetic rubber. 14. A process according to one of claims 1 to 5, wherein the air bombardment is carried out for about 2-6 hours. 15. A homogenized asphalt composition made by a process according to claim 1. SUBSTITUTE SHEET (ROLE 26) 16. A homogenized asphalt composition made by a process according to one of claims 2 or 3. 17. A homogenized asphalt composition made by a process according to one of claims 4 or 5. 18. A homogenized asphalt composition made by a process according to one of claims 6 to 14. 19. A homogenized asphalt composition consisting essentially of about 1-27% ground tire rubber incorporated into about 73-99% distillation tower bottoms. 20. A homogenized asphalt composition according to claim 19 consisting essentially of about 10-14% ground tire rubber incorporated into about 86-90% distillation tower bottoms. 21. A homogenized asphalt composition according to claim 19 consisting essentially of about 12% ground tire rubber and about 88% distillation tower bottoms. 22. A homogenized asphalt composition according to claim 19, wherein the ground tire rubber includes synthetic rubber.

Inventors: FLANIGAN THEODORE P, FLANIGAN, THEODORE, P.
Applicants: NESTE WRIGHT ASPHALT PRODUCTS, NESTE/WRIGHT ASPHALT PRODUCTS CO.
Application year: 1995
Main classification: C08J11
IPC codes: C08J11, C08L95