Method for the preparation of organic solvent-soluble polytitanosiloxanes

Abstract: The invention is a method for preparing organic solvent-soluble polytitanosiloxanes that contain units with the formulas R¹ a R² (3-a) SiO 1/2 (M units), SiO 4/2 (Q units) and TiO 4/2 . Our method comprises hydrolyzing tetraalkyl titanate, or a partial hydrolyzate-condensate thereof, and tetraalkyl silicate, or a partial hydrolyzate-condensate thereof, using water in an amount which is less than 80% of the amount theoretically necessary for the hydrolysis of all the alkoxy groups, and reacting the cohydrolyzate-cocondensate with at least 1 silane with the formula R¹ a R² (3-a) SiOR³, where R¹ is hydrogen atom or a monovalent organic group, R² is a monovalent organic group, R³ is hydrogen atom or an acyl group having no more than 8 carbon atoms, and a is an integer with a value of 0 to 3.

Description: The invention relates to a method for the preparation of polytitanosiloxanes. The silicone industry uses the term "MQ resin" to designate organic solvent-soluble polyorganosiloxanes composed of siloxane units in which 3 organic groups are bonded on silicon, R 3 SiO 1/2 units also known as M units, and siloxane units free of organic groups, SiO 4/2 units known as Q units. MQ resin is used as a hard coating material and as a pressure sensitive adhesive, see for example, Kunio Itoh (ed.), Shirikon Handobukku [Silicone Handbook], Nikkan Kogyo Shinbunsha. Substances composed of Q and TiO 4/2 units, called "silica-titania", are known as low-expansion glasses in the field of inorganic materials. However, very few reports exist of silica-titania containing organic groups bonded to silicon. Otherwise, polytitanosiloxanes in which titanium atom substitution occurs in part of the polysiloxane are well known. They are described, for example, in Chapter 7 of Chemistry and Technology of Silicones, by W. Noll (Academic Press). Nevertheless, there is no report heretofore of organic solvent-soluble polytitanosiloxanes whose main structural elements are M, Q, and TiO 4/2 units. While a method for the preparation of similar compounds is suggested in JP-A 61-228919, the Q unit is not cited therein as an essential component, and, therefore, the corresponding examples are not described. Such a Q unit-free polytitanosiloxane lacks stability with regard to moisture and heat, which impairs its practical applications. Moreover, the preparative method of this published patent application uses the entire amount of water necessary for complete hydrolysis and condensation. This ultimately leads to the production of titania gel and makes it difficult to produce a transparent polymer. DE-A-3 407 087 discloses a process for the preparation of hard scratch-resistant coatings comprising coating and curing on a substrate a varnish prepared by a hydrolytic precondensation of a) 5 to 70 mole-% of at least a titanium or zirconium compound represented by a formula I MR 4 where M represents titanium atom or zirconium atom, and R represents a halogen atom, hydroxy, alkoxy, acyloxy or a chelating ligand, b) 30 to 95 mole-% of at least a monofunctional, difunctional or trifunctional organosilane represented by a formula (II) R' m (R''Y) n SiX (4-m-n) wherein R' represents alkyl or alkenyl, R'' represents alkylene or alkenylene, wherein theses groups can be interrupted by an oxygen atom or a sulfur atom or a -NH group, X represents hydrogen, halogen, hydroxy, alkoxy, acyloxy or a -NR''' 2 group, wherein R''' represents hydrogen or an alkyl group, Y represents halogen or an optionally substituted amino, amide, aldehyde, alkylcarbonyl, carboxy, mercapto, cyano, alkoxy, alkoxycarbonyl, sulfonic acid, phosphoric acid, acryloxy, methacryloxy, epoxy or vinyl group, m and n represent 0, 1, 2, or 3, and optionally c) 0 to 65 mole-% of at least one reaction medium-soluble, not easily volatile oxide of an element of the groups Ia to Va, IVb or Vb, with an amount of water which is lower than the amount necessary for a complete hydrolysis of all hydrolyzable groups optionally in the presence of a condensation catalyst and subsequently further condensing the composition with at least an amount of water necessary for a complete hydrolysis of all hydrolyzable groups. Our invention is a method for the preparation of an organic solvent-soluble polytitanosiloxane whose essential constituents are M, Q, and TiO 4/2 units. More specifically, the invention is a preparative method that suppresses titania gel formation while yielding polytitanosiloxane that is also stable to moisture and heat. Our polytitanosiloxane can be synthesized by hydrolysis and condensation of tetraalkyl titanate and tetraalkyl silicate using water in an amount which is less than 80% of the amount necessary for the hydrolysis and condensation of all the alkoxy groups on the tetraalkyl titanate and the tetraalkyl silicate. This is followed by subsequent reaction with at least 1 silane compound with the formula R 3 SiOR', where the radicals R, same or different, are selected from methyl, vinyl and phenyl and R' is selected from a hydrogen atom and an acyl group having no more than 8 carbon atoms. The alkyl group of the tetraalkyl titanate and tetraalkyl silicate is exemplified by methyl, ethyl, propyl, isopropyl, butyl, sec-butyl, tert-butyl, pentyl, hexyl, heptyl, and octyl. Substituents such as alkoxy and halogen may also be bonded to the alkyl group. For the titanate reactant, the alkyl group is preferably not methyl from the standpoint of solvent solubility, and preferably contains no more than 10 carbon atoms from the standpoint of hydrolyzability. For the silicate reactant, alkyl groups having no more than 6 carbon atoms are preferred from the standpoint of the hydrolysis rate. The hydrolyzate-condensate specified for the said titanate and silicate is the product yielded by the hydrolysis and condensation of the tetraalkyl titanate or tetraalkyl silicate using water in an amount less than that necessary for the hydrolysis and condensation of all the alkoxy groups on the tetraalkyl titanate and the tetraalkyl silicate. This product thus corresponds to an oligomer. There are absolutely no restrictions on the weight ratio between the tetraalkyl titanate and the tetraalkyl silicate. However, the Ti/Si ratio preferably falls between 1:100 to 100:1 from the standpoint of the properties of the polytitanosiloxane product. This ratio preferably falls between 1:10 to 10:1 to simultaneously obtain satisfactory optical properties and stability. A characteristic feature of the invention is that the tetraalkyl titanate and the tetraalkyl silicate are hydrolyzed and condensed using water in an amount which is less than 80% of the amount theoretically necessary for the hydrolysis and condensation of all the alkoxy groups on the tetraalkyl titanate and the tetraalkyl silicate. Said theoretically amount corresponds to 0.5 mole water per 1 mole alkoxy group. This characteristic feature is crucial for preventing gelation. When the amount of water is greater than or equal to 80%, a titania gel is frequently produced because the tetraalkyl titanate is ultimately completely hydrolyzed and condensed. The water quantity is preferably at least 10% of the theoretically necessary amount because lower values do not give a satisfactory production of polymer. The preferred water addition is at least 20%, but no more than 75% of the quantity necessary for the hydrolysis and condensation of all the alkoxy groups. The hydrolysis and condensation reaction can be run by introducing the tetraalkyl titanate and tetraalkyl silicate simultaneously or successively. In the latter case, hydrolysis and condensation of the tetraalkyl titanate may be carried out first using water in an amount which is less than 80% of the amount necessary for the hydrolysis and condensation of all the alkoxy groups on the tetraalkyl titanate and the tetraalkyl silicate This would be followed by addition of the tetraalkyl silicate and hydrolysis and condensation in the same manner. This order of addition can be reversed, and the reactants can be divided into any number of portions and added in alternation. The hydrolysis and condensation reaction will run in the absence of catalyst, but a catalyst may be used if desired. Any acidic, basic, or other catalyst generally used in the sol-gel method is satisfactory. The hydrolysis and condensation reaction can be run in a suitable solvent or may be run in the absence of solvent. Any solvent can be used that is capable of adequately dissolving the starting compounds and polymer product, and which does not adversely affect the reaction. The solvents are exemplified by aliphatic hydrocarbons such as pentane, hexane, heptane, and octane; aromatic hydrocarbons such as benzene, toluene, and xylene; ether solvents such as diethyl ether, dibutyl ether, diphenyl ether, dioxane, and tetrahydrofuran; ester solvents such as ethyl acetate and butyl acetate; ketone solvents such as acetone, methyl ethyl ketone, and methyl butyl ketone; and halogenated solvents such as carbon tetrachloride, chloroform, trichloroethane, trichloroethylene, and tetrachloroethylene; as well as dimethylformamide, dimethyl sulfoxide, and hexamethyltriamide phosphate. The preparative method of our invention must employ a procedure that leads to the formation of a cohydrolyzate-cocondensate from the tetraalkyl titanate and tetraalkyl silicate. In specific terms, care must be taken to avoid gel formation during the addition of water to the tetraalkyl titanate. Measures that can be taken are exemplified by very gradual dropwise addition of the water, for example, no more than 10 weight% of the total water addition per minute; addition of the water after its dilution in at least an equal volume of water-soluble organic solvent; addition of the water carried or adsorbed on a water-adsorptive solid such as silica gel, zeolite, calcium chloride, sodium sulfate, magnesium sulfate, aluminum oxide, aluminum hydroxide and particularly silica gel; and cooling the reactants during addition of the water, to 0°C to -100°C and preferably to -20°C to -90°C. However, any suitable measure may be used. After addition of the water and stabilization of the system, a process such as heating at reflux can be performed to complete the hydrolysis and condensation reaction. After water addition, the reaction mixture is reacted with at least 1 silane with the formula R 3 SiOR' to produce the desired polytitanosiloxane. The radicals R, same or different, are selected from methyl, phenyl, and vinyl. R' is selected from a hydrogen atom or an acyl group having 8 or fewer carbon atoms, and hydrogen and acetyl are preferred from a consideration of reactivity. Upon addition of silane, the alkoxy groups not consumed in the hydrolysis and condensation reaction undergo condensation with the silane, which completes compound, the synthesis of a stable and solvent-soluble polytitanosiloxane. When R' in the silane is hydrogen, alcohol is produced as a result of the condensation reaction, while a carboxylic acid ester is produced when R' is acyl. The reaction can be brought to completion by removal of the alcohol or ester by heating and/or a vacuum. Any number of different silane compounds may be added, and the silane compounds should be selected based on the type of organic groups desired in the polytitanosiloxane product. The quantity of the silane added is not critical, but the quantity preferably exceeds the number of moles of the residual alkoxy groups left unconsumed by the hydrolysis reaction. 1.5 to 5 moles of silane is preferably added for each mole of residual alkoxy groups. In some cases, it may be desired that alkoxy or hydroxyl remain bonded to the polytitanosiloxane molecule. Alkoxy- or hydroxy-functional polytitanosiloxane can be prepared by adjusting the type and/or quantity of addition of the silane. For example, because the silanol is generally more reactive than the acyloxysilane, survival of the alkoxy group can be facilitated through use of acyloxysilane as the silane. The invention is explained below in greater detail through the use of working examples. In the examples, the number average molecular weight is the value obtained by gel permeation chromatography (GPC) using polystyrene calibration. Structural determination was carried out using proton nuclear magnetic resonance spectroscopy, 29 Si nuclear magnetic resonance spectroscopy and atomic absorption spectroscopy. In addition, room temperature indicates 25°C and the following abbreviations are used: Me for methyl, Vi for vinyl, Ph for phenyl and THF for tetrahydrofuran. Example 1 To a solution consisting of a mixture of 5.27 g (15.5 mmol) titanium tetra-n-butoxide and 10 mL THF was added, over 20 minutes and at -78°C, a solution consisting of a mixture of 0.255 g (14 mmol) water and 5 mL THF. The reaction was subsequently allowed to return to room temperature and was stirred for 1 hour. After re-cooling to -78°C, 1.23 g of an already partially hydrolyzed and condensed ethyl orthosilicate (ethoxy group = 20 mmol, SiO 2 content = 40 weight%) was added and the reaction was stirred. This was followed by the dropwise addition of 0.255 g (14 mmol) water in 5 mL THF. The solution temperature was then allowed to return to room temperature and the reaction was stirred for another 30 minutes. A 45 g ether solution that contained 67 mmol vinyldimethylsilanol was added and the reaction was stirred for 30 minutes. The reaction was then developed by gradually heating to 120°C while distilling the solvent. Removal of the solvent and low boilers at 120°C under reduced pressure ultimately yielded 3.60 g of a transparent light-yellow solid. This product was soluble in organic solvents such as THF, toluene, hexane, and carbon tetrachloride. Its nuber average molecular weight was 6.59 x 10 6 , and its index of refraction at 25°C was 1.561. The analytic results gave the following compositional formula: (TiO 4/2 ) 0.65 (SiO 4/2 ) 0.35 (ViMe 2 SiO 1/2 ) 0.52 Comparative Example 1 An experiment was run according to Example 1 using 0.56 g water in the first water addition instead of 0.255 g water. A solvent-insoluble gel was produced in the system. Comparative Example 2 An experiment was run according to Example 1 with the following modifications to the first water addition step: the temperature of the reaction system was maintained at 30°C and the water was added directly without dissolution in THF. This experiment produced a solvent-insoluble gel in the system. Comparative Example 3 An experiment was run according to Example 1 with the following modifications to the first water addition step: the temperature of the reaction system was maintained at 30°C and the water dissolved in THF was added within 1 second. This experiment produced a solvent-insoluble gel in the system. Comparative Example 4 An experiment was run according to Example 1 with the following modification: while maintaining the temperature of the reaction system at -78°C, the titanium tetra-n-butoxide, ethyl orthosilicate, and water (0.45 g in 10 mL THF) were mixed all at once. This experiment produced a solvent-insoluble gel in the system. Example 2 To a solution consisting of a mixture of 6.13 g (18.0 mmol) titanium tetra-n-butoxide and 10 mL THF, was added at -78°C a solution consisting of a mixture of 0.324 g (18 mmol) water and 4 mL THF. The reaction was subsequently allowed to return to room temperature and was stirred for 1 hour. After re-cooling to -78°C, 2.45 g (11.8 mmol) ethyl orthosilicate was added and the reaction was stirred. This was followed by the dropwise addition of 0.324 mg (18 mmol) water in 4 mL THF. The solution temperature was then allowed to return to room temperature and the reaction was stirred for another 30 minutes thereafter. A 50 mL ether solution that contained 70 mmol vinyldimethylsilanol and 50 mmol trimethylsilanol was added and the reaction was stirred for 30 minutes. The reaction was then developed by gradually heating to 120°C while distilling the solvent. Removal of the solvent and low boilers at 120°C under reduced pressure ultimately yielded 4.55 g of a transparent light-yellow solid. This product was soluble in organic solvents such as THF, toluene, hexane, and carbon tetrachloride. Its number average molecular weight was 8.40 x 10 5 , and its index of refraction at 25°C was 1.459. The analytic results gave the following compositional formula: (TiO 4/2 ) 0.6 (SiO 4/2 ) 0.4 (ViMe 2 SiO 1/2 ) 0.56 (Me 3 SiO 1/2 ) 0.44 Example 3 To a solution consisting of a mixture of 5.69 g (20 mmol) titanium tetraisopropoxide and 10 mL THF, was added at -78°C a solution consisting of a mixture of 0.36 g (20 mmol) water and 6 mL THF. The reaction was subsequently allowed to return to room temperature and was stirred for 1 hour. After re-cooling to -78°C, 1.97 g (12.9 mmol) ethyl orthosilicate was added and the reaction was stirred. This was followed by the dropwise addition of 0.36 g (20 mmol) water in 6 mL THF. The solution temperature was then allowed to return to room temperature and the reaction was stirred for another 30 minutes thereafter. A 70 mL ether solution that contained 40 mmol vinyldimethylsilanol and 60 mmol trimethylsilanol was added and the reaction was stirred for 30 minutes. The reaction was then developed by gradually heating to 100°C while distilling the solvent. Removal of the solvent and low boilers at 100°C under reduced pressure ultimately yielded 6.13 g of a transparent, highly viscous yellow liquid. This product was soluble in organic solvents such as THF, toluene, hexane, and carbon tetrachloride. Its number average molecular weight was 650, and its index of refraction at 25°C was 1.490. The analytic results gave the following compositional formula: (TiO 4/2 ) 0.41 (SiO 4/2 ) 0.39 (ViMe 2 SiO 1/2 ) 0.49 (Me 3 SiO 1/2 ) 0.56 Example 4 To a solution consisting of a mixture of 6.54 g (19.2 mmol) titanium tetra-n-butoxide and 10 mL THF, was added at -78°C a solution consisting of a mixture of 0.35 g (19 mmol) water and 6 mL THF. The reaction was subsequently allowed to return to room temperature and was stirred for 1 hour. After re-cooling to -78°C, 2.35 g (ethoxy group = 38 mmol, SiO 2 content = 40 weight%) of an already partially hydrolyzed and condensed ethyl orthosilicate was added and the reaction was stirred. This was followed by the dropwise addition of 0.35 g (19 mmol) water in 6 mL THF. The solution temperature was then allowed to return to room temperature and the reaction was stirred for another 30 minutes thereafter. A 50 mL ether solution that contained 60 mmol phenyldimethylsilanol was added and the reaction was stirred for 30 minutes. The reaction was then developed by gradually heating to 120°C while distilling the solvent. Removal of the solvent and low boilers at 120°C under reduced pressure ultimately yielded 6.35 g of a transparent, highly viscous yellow liquid. This product was soluble in organic solvents such as THF, toluene, hexane, and carbon tetrachloride. Its number average molecular weight was 3.66 x 10 5 , and its index of refraction at 25°C was 1.572. The analytic results gave the following compositional formula: (TiO 4/2 ) 0.55 (SiO 4/2 ) 0.45 (PhMe 2 SiO 1/2 ) 0.50 Example 5 To a solution consisting of a mixture of 5.27 g (15.5 mmol) titanium tetra-n-butoxide and 10 mL THF, was added at 5°C silica gel to which 0.27 g water (15 mmol) had been adsorbed. The reaction was subsequently allowed to return to room temperature and was stirred for 3 hours. Ethyl orthosilicate (3.33 g, 16 mmol) was added and the reaction was stirred. This was followed by the addition of silica gel on which 0.28 g water (16 mmol) had been adsorbed, and stirring for 6 hours at 60°C. The solution temperature was then allowed to return to room temperature. 18 mmol vinyldimethylacetoxysilane and 35 mmol trimethylacetoxysilane were added and the reaction was stirred for another 30 minutes. The reaction was then developed by gradually heating to 120°C while distilling the solvent. Removal of the solvent and low boilers at 120°C under reduced pressure ultimately yielded 3.71 g of a transparent, highly viscous and light-brown liquid. This product was soluble in organic solvents such as THF, toluene, hexane, and carbon tetrachloride. Its number average molecular weight was 3.94 x 10 4 . The analytic results gave the following compositional formula: (TiO 4/2 ) 0.49 (SiO 4/2 ) 0.51 (ViMe 2 SiO 1/2 ) 0.16 (Me 3 SiO 1/2 ) 0.29 (C 2 H 5 O 1/2 ) 0.25 (C 4 H 9 O 1/2 ) 0.06 A polytitanosiloxane prepared using our preparative method does not contain gel, is stable with respect to moisture and heat, and is soluble in organic solvents. These attributes are surprising and unexpected. They produce a polytitanosiloxane which is extremely useful, for example, as an antireflection coating.

Claims: A method for preparation of organic solvent-soluble polytitanosiloxanes, the method comprising: (1) adding water simultaneously or successively to a tetraalkyl titanate and a tetraalkyl silicate, in the absence of a catalyst and while cooling the reactants during addition of the water to 0°C to -100°C so that a cohydrolyzate-cocondensate forms, in an amount which is less than 80 % of the amount theoretically necessary for the hydrolysis and condensation of all alkoxy groups on the tetraalkyl titanate and the tetraalkyl silicate in a way so as to avoid gel formation by using a measure selected from the group consisting of a) very gradual dropwise addition of the water in a rate of no more than 10 weight% of the total water addition per minute; b) addition of the water after its dilution in at least an equal volume of a water-soluble organic solvent; and c) addition of the water carried or adsorbed on a water-adsorptive solid and (2) reacting the cohydrolyzate-cocondensate with at least one silane with a formula R 3 SiOR' where the radicals R, same or different, are selected from methyl, vinyl and phenyl, and R' is selected from a hydrogen atom and an acyl group having no more than 8 carbon atoms. The method of Claim 1, wherein R' is selected from a hydrogen atom and an acetyl group.

Inventors: KUSHIBIKI NOBUO, SUGATA YOKO, SUZUKI TOSHIO, KUSHIBIKI, NOBUO, SUGATA, YOKO, SUZUKI, TOSHIO, KUSHIBIKI, NOBUO, DOW CORNING ASIA, LTD., SUGATA, YOKO, DOW CORNING ASIA, LTD., SUZUKI, TOSHIO, DOW CORNING ASIA, LTD.
Applicants: DOW CORNING ASIA LTD, DOW CORNING ASIA, LTD.
Application year: 1995
Main classification: C08G77
IPC codes: C08G77, C08G79