ELECTRIC LAMP HAVING AN UNDERCOAT FOR INCREASING THE LIGHT OUTPUT OF A LUMINESCENT LAYER

Abstract: An electric lamp having a luminescent layer (17) on the lamp envelope (3) which produces visible light when impinged by ultraviolet radiation generated within the lamp. An undercoat for the luminescent layer (17) increases the luminous efficacy of the lamp. The undercoat comprises an agglomerated particulate material of predominantly gamma alumina having a primary crystallite size of less than about 0.05 mu m. The undercoat is effective to increase the luminous efficacy of certain fluorescent lamps so that they meet the minimum efficacy requirements of the Energy Policy Act of 1992.

Description: % Electric lamp having an undercoat for increasing the light output of a luminescent layer The invention pertains to an electric lamp, comprising: a. a lamp envelope having an inner surface; b. means within the lamp envelope for generating ultraviolet radiation; c. a luminescent layer adjacent the inner surface of the lamp envelope for generating visible light when impinged by said ultraviolet radiation; and d. a UV-reflecting layer, between the inner surface of the lamp envelope and the luminescent material layer, for reflecting ultraviolet radiation which has passed through the luminescent layer back into the luminescent layer for increasing the visible light output of the luminescent layer. Low pressure mercury vapor lamps, more commonly known as fluorescent lamps, have a lamp envelope with a filling of mercury and a rare gas and in which a gas discharge is maintained during lamp operation. The radiation emitted by the gas discharge is mostly in the ultraviolet region of the spectrum, with only a small portion in the visible spectrum. The inner surface of the lamp envelope has a luminescent layer, often of a blend of phosphors, which emits visible light when impinged by the ultraviolet radiation. Lighting accounts for approximately 20-25% of the electricity used annually in the United States. For stores, offices and warehouses, lighting may account for up to 50% of their electrical consumption. Lighting is a primary focus of The National Energy Policy Act (EPACT) of 1992, whose goal is to drastically reduce national energy consumption. This act mandates energy efficiency standards for various lamp types in terms of lamp efficacy and color rendering index. Luminous efficacy is a measure of the useful light output in relation to the energy input to the lamp, in lumens per watt. The EPACT standards for fluorescent lamps are listed in Table 1 below. Fluorescent lamps which do not meet these minimum standards cannot be sold in the United States beginning with certain dates in 1994. Fluorescent Lamp Standards * Lamp Nominal Minimum Minimum average lamp Lamp Power (W) CRI efficacy lm W 4-Foot >35 69 75.0 Medium BI-PIN ≤35 45 75.0 2-Foot >35 69 68.0 U-Bent ≤35 45 64.0 8-Foot >65 69 80.0 Slimline ≤65 45 80.0 8-Foot > 100 69 80.0 High Output ≤ IOO 45 80.0 Many fluorescent lamps on the market prior to 1994 do not meet these mandated minimum efficacy requirements. Such lamps include F96T12 and F40T12 CW (cool white), F96T12 and F40T12 Daylite, and F96T12 and F40T12 warm white. Herein th denotation Fp Td represents a fluorescent lamp having a nominal power of p W and an internal diameter of d/8 inch (=3.2 d mm). The efficacy of such lamps must be raised to th EPACT standards or they will no longer be allowed to be manufactured. Luminous efficacy is dependent on the efficiency at which the luminesce layer converts the ultraviolet radiation from the gas discharge into visible light, on electrode losses (specifically the cathode drop), thermal losses and losses in the column gas discharge. Lamp electrodes have already been highly optimized by the lamp industry for specific applications. Losses in the column discharge are primarily a function of lamp geometry. Thus, for fluorescent lamps of a given length, diameter and lifetime, a further reduction of losses at the electrodes and in the discharge would be extremely difficult to attain. The luminescent layer is the single most important contributing factor in determining the luminous efficacy of fluorescent lamps. Increasing lamp efficacy through development of new or improved phosphors, however, would be very time consuming, as well as expensive. Research and development in phosphors is accomplished primarily throu large numbers of experiments because results are not very predictable theoretically. Substitution of known high performing phosphors for other, lower performing ones is often not feasible either. While certain phosphors, such as the so-called narrow band and rare earth phosphors, produce high luminous efficacy and excellent color rendering in lamps intended for the high end of the market, they would be too expensive for use in lamps intended for standard or low cost applications which presently employ the relatively low cost halophosphate phosphors. Furthermore, the thickness or coating weight of each type of phosphor has already been optimized for the greatest light output. In general, if a luminescent layer is too thin, some of the U. V. radiation from the discharge will pass through the layer without being converted into visible light. If the layer becomes too thick, however, the phosphor itself absorbs and/or reflects a portion of the visible light generated in the region of the layer near the discharge. Other types of lamps also include a luminescent layer for providing or improving their photometric parameters. These include high pressure discharge lamps, such as high pressure mercury vapor and certain metal halide lamps, which have an arc tube which at least partly emits U.V. radiation. Accordingly, it is an object of the invention to provide a cost effective mechanism of increasing the luminous efficacy of lamps having a luminescent layer. It is another object of the invention to increase the luminous efficacy of certain low pressure mercury vapor fluorescent lamps to meet the EPACT standards. Generally speaking, an electric lamp according to the invention includes a lamp envelope having an inner surface and means within the lamp envelope for generating ultraviolet radiation. A luminescent layer is adjacent the inner surface of the lamp envelope for generating visible light when impinged by the ultraviolet radiation. The lamp includes UV-reflecting layer, between the inner surface of the lamp envelope and the luminescent layer, for reflecting ultraviolet radiation which has passed through the luminescent layer of luminescent material back into the luminescent layer for increasing the visible light output of the luminescent layer. According to the invention the UV-reflecting layer comprises an agglomerated particulate material of predominantly gamma alumina having a primary crystallite size of less than about 0.05 μm. According to one embodiment, the UV-reflecting layer is a base, or pre- coat layer, disposed directly on the inner surface of the lamp envelope. In a favorable embodiment, the primary crystallite size was about 0.01 μm obtained from a commercially available source. For this particle size, the UV- reflecting layer preferably has a coating weight of between about 0.15 mg/cm 2 and about 0.3 mg/cm 2 for a lamp having a luminescent layer comprising a cool white phosphor. Above about 0.3 mg/cm 2 there is no further increase in the light output of the phosphor, so additional weight/thickness of the layer merely increases lamp cost without providing additional benefit. Below about 0.15 mg/cm 2 there is an insufficient design margin for meeting the EPACT standard with a standard cool white phosphor. Non-luminescent alumina-containing layers between the inner surface of the lamp envelope and the luminescent layer have been used in the industry for various purposes. These purposes include, for example, (i) layers for reducing chemical reactions between the soda-lime glass used in fluorescent lamps and the phosphor layer so as to improve lumen maintenance and (ϋ) ultraviolet radiation reflecting layers for reflecting U.V. radiation back into a phosphor layer through which it has already passed. U.S. Patent 5,008,789 (And et al) discloses a fluorescent lamp employing the relatively expensive rare earth phosphors. In order to reduce lamp cost, such lamps often used an additional but less costly halophosphate layer to reduce the quantity of the rare earth phosphor. However, while preserving luminous efficacy, the halophosphate layer was found to be detrimental to the color rendering properties associated with the rare earth phosphors because of the halophosphates' inferior visible emissions. Arai et al employs a non- luminescent layer in place of a halophosphate layer, which has the effect of reflecting U.V. radiation back into the rare earth phosphor layer. This was found to maintain luminous efficacy without adversely impacting the relatively high color rendering characteristics provided by the rare earth phosphors. In one embodiment, the non-luminescent layer of Arai et al consists essentially of α(alpha)-alumina having an average grain size of between about 0.05 μm and 2 μm. Arai teaches that its UV-reflecting layer is effective for counteracting the loss of light output due to reduction in the thickness of the rare earth phosphor layer, but not for increasing the total light output of the lamp. It is disclosed that a slight reduction in lamp brightness may occur because of the increased light attenuation with increasing thickness and UV reflectance of its UV-reflecting layer. Furthermore, And specifically teaches (i) that o- alumina having a grain size of less than 0.05 μm is ineffectual at reflecting ultraviolet radiation because this grain size is smaller than the wavelength of the U.V. radiation and (ϋ) that higher luminous fluxes could not be obtained when 7(gamma)alumina was used instead of α-alumina. Accordingly, it was a surprise to find that the undercoat according to the invention increased lamp lumens as compared to a lamp with the identical phosphor layer an 5 no pre-coat. This was particularly surprising in view of the fact that (i) Applicants base consists of gamma alumina, which Arai teaches is ineffective for increasing light output, and (ϋ) the grain size according to the present invention is smaller than that which Arai teaches is effective. U.S. Patent 4,079,288 (Maloney et al) discloses a fluorescent lamp with another alumina undercoating of vapor formed spherical alumina particles having an individual particle size ranging from approximately 400 Angstroms to 5000 Angstroms in diameter (0.04 μm to 0.5 μm), and an average particle size of .135 μm. The alumina layer has light diffusion properties which scatters at least 99% of the visible radiation incident thereon from the adjacent phosphor layer. The alumina layer also functions to scatter U.V. radiation back into the phosphor layer to permit reduction in phosphor weight. The coating is applied by vaporizing, through rapid combustion, a pellet of solid aluminum isoproxide. While this technique may be practical for frosting a generally spherical incandescent lamp envelope as disclosed in Maloney's U.S. Patent 3,842,306, it would be difficult to achieve a uniform layer on the inner surface of a narrow, elongate tubular envelope of a fluorescent lamp in a very high speed manufacturing environment because of the long narrow geometry. Applicant is not aware of the presence of such a vapor deposited coating in commercially available fluorescent lamps. By comparison, the undercoating according to the invention can be applied by liquid suspension according to commonly employed techniques for applying phosphor layers on the interior surface of lamp envelopes. Additionally, it should be noted that Maloney's '306 patent discloses the introduction of a preformed minute crystalline alumina material, specifically Alon C powder, into the combustion process of the aluminum isoproxide. The resulting larger agglomerate of the Alon C becomes interspersed in the matrix of spherical alumina and helps hide the filament. Maloney did not disclose this minute crystalline material for use in the fluorescent lamp of the '288 patent. These and other features and advantages of the invention will be further described with reference to the following drawings, detailed description and claims. Figure 1 is a perspective view of a fluorescent lamp, partly in cross- section, partly broken away, having an undercoat according to the invention; Figure 2 is a graph of the light output in Lm verses the coating weight of the luminescent layer in mg/cm 2 for different coating weights in mg/cm 2 of the UV-reflecting layer according to the invention in a low-pressure discharge lamp; and Figure 3 is a perspective view, partly in cross-section, of a high-pressur mercury vapor lamp with the same UV-reflecting layer in accordance with the invention. Fig. 1 shows a low pressure mercury vapor fluorescent lamp 1 with an elongated lamp envelope 3. The lamp includes a conventional discharge electrode 5 at each end which includes a filament 6 supported on in-lead wires 7 and 9 which extend through a glass press seal 11 in a mount stem 10. The leads 7, 9 are connected to the pin-shaped contacts 13 of thdr respective bases 12 fixed at opposite ends of the lamp. The filling of an ionisable material in the envelope includes an inert gas such as argon, or a mixture of argo and other gases, at a low pressure in combination with a small quantity of mercury to sustai an arc discharge during lamp operation. The inner surface 15 of the outer envdope 3 is provided with a UV-reflecting layer 16 of 7(gamma) alumina having a primary crystallite size of less than about 0.05 μm. A luminescent layer 17 is disposed over the undercoat 16. Both layers 16, 17 extend the full length of the envdope 3, completely circumferentially around the inner surface of the envelope. To better illustrate the improvement in light output characteristics obtain for a fluorescent lamp having the above undercoat, a number of lamps were fabricated having a discharge vessd with a length of 1.20 m and an internal diameter of 38 mm. Various weights of the above UV-reflecting layer with a primary crystallite size of about 0.01 μm were utilized. The initial (100 hr) lumen output for these lamps at a power of 40 are reported in Table I bdow: TABLE I In the table, m, and φ represent the coating weight in mg/cm 2 of the standard cool white halophosphate phosphor used and the light output in lm respectively. The cool white phosphor was Cas(F, Cl) (PQJj. S b :M,. The heading at the top of each column is the coating wdght m* in mg/cm 2 per lamp of the above-mentioned 0.01 μm γ (Gamma) alumina base coat. The data of Table I is illustrated graphically in Figure 2. The UV- reflecting layer with a coating wdght of 0.22 mg/cm 2 provided the highest light output. Fo a 40W lamp having a discharge vessd with a length of 1.20 m and an internal diameter of mm (ιj), a light output of 3000 lm (illustrated by the dashed line) corresponds to an efficac of 75 lm/W, which is the minimum value that the EPACT standard prescribes for that type of fluorescent lamp. From Fig. 2 it can be seen that this efficacy is met for a coating wdg of the base coat of 0.22 mg/cm 2 and of 0.15 mg/cm 2 and is significantly higher than the 72. lm/W obtained without the base coat. While the minimum coating wdght of the luminescen layer for attaining 75 lm/W is lower for a higher base coat wdght (about 4.6 mg/cm 2 for base coat of 0.22 mg/cm 2 and about 5.0 mg cm 2 for a base coat of 0.15 mg/cm 2 , at the present time the standard cool white halophosphate phosphor is significantly less costly than the Aluminum oxide C material, so lamp cost is lowest with the lowest sufficient base coat weight. It should be noted that a lamp of the type F40T12 was used as a test vehicle for demonstrating the increase in light output using the base coat according to the invention. Although the efficacy has been sufficiently raised, an F40T12 with the specified cool white phosphor will not meet the minimum color rendering (CRI>69) for this lamp type specified by EPACT. However, the effect is transferable to other lamps when weight per lamp is converted to weight/unit area. From Figure 2, a minimum effective coating weight of about 0.15 mg/cm 2 was found to provide the necessary percent increase in light output. Though not shown in Figure 2, it was found that at above about 0.3 mg/cm 2 no additional increase in light output was found, so additional coating weight of the UV- reflecting lamp merely increased lamp cost without a further improvement in light output. Base coats having a coating weight within this range were employed in an F96T12 CW lam having a discharge vessel with a length of 2,40 m and were effective to increase its lumino efficacy from 77-78 lm/W to above the minimum EPACT standard of 80 lm/W. The minimum EPACT CRI for this lamp is only 45, so the lamp meets both EPACT requirements with the cool white phosphor and a UV-reflecting layer according to the invention. The inner surface area of a lamp of this type is about 2800 cm 2 . The data in Table I was fitted to the curve described by the following equatio θ = A - Be- 0 * - DW where θ represents the light output in lm, W represents the weight of the cool white phosphor (mg/cm 2 ) and A, B, C an D are constants. The constants A, B, C and D are listed in Table π bdow: TABLE π Constant Control Control Control Control 0.0 mg/cm 2 0.075 mg/cm 2 0.15 mg/cm 2 0.22 mg/cm 2 A 2.97e+003 3.39e+003 3.18e+003 3.64e+003 B 3.95e+004 1.99e+003 1.30e+004 3.24e+003 C l.oe+OOO 4.54e-001 1.16e-000 5.78e-001 D 1.18e+001 4.61e+001 2.87e+001 9.03e+001 Base Coat Preparation/ Application The base coats mentioned above were prepared from dispersions of colloidal alumina commercially available from Degussa as Aluminum Oxide C. This material is made by the so-called aerosol process. The resulting agglomerated paniculate material has a primary crystallite size of 0.01 μm and is predominantly gamma alumina. A small amount of chloride ion and moisture is also present in the material. The dispersions are most conveniently prepared using water to which various ingredients may also be added without substantially changing the benefits of the base coat. These additives may include various nonionic and or cationic surfactants and/or dispersants, such as organic and inorganic salts of aluminum or other metals or cations and/or binders such as are in common use in aqueous phosphor suspension systems. For increasing viscosity, binders of polyvinyl alcohol were found particularly useful and at the low concentrations employed were easily removed during lehring. A notable exception to the above is that alumina dispersions in general are colloidally incompatible with anionic surfactants, dispersants and binders. The density and viscosity of aqueous dispersions produced for casting layers of alumina of the desired wdght is a function of the rate of drying and the amount of binder found convenient to employ. The alumina layer can also be cast from organic solvent based dispersions if an adequate amount of shear is applied. Surfactants useful in that case should ideally behave as ionic dispersants as the strongly repulsive potentials experienced by alumina in water under the appropriate conditions are substantially absent in organic solvents. If a binder is desired any in common use in organic media could be used. 10 The dispersion is applied to the interior of a clean fluorescent tube in a manner known to the art. The way the applied dispersion is dried does not seem to influenc the usefulness of the invention. However, the weight of the resulting alumina layer has a direction influence on the lamp output (as discussed above) and is a function of both the rat of drying and the density and viscosity of the dispersion employed. The UV-reflecting layer may be lehred before the application of the luminescent layer. However, no advantages were found from this step, though no disadvantages were uncovered dther. It has been found experimentally that the alumina particles of the UV- reflecting layer 16 are not dislodged in the application of the luminescent layer if the aqueo dispersion contains any typical combination of surfactants, dispersants and binden or wheth the base coat layer is lehred or not. It is advisable to lehr layers cast from organic binders they are likely to be dislodged or dissolved by a subsequent coating of either an aqueous or non-aqueous suspension of the phosphor. The luminescent layer is applied in a manner known to the art directly o the lehred or unlehred alumina base coat. The traction rate of the phosphor suspension is diminished by the presence of the base coat. The weight of the phosphor contained in the luminescent layer is found to bear a relationship proportional to the weight in the base coat. The lamp envdope coated as above is then lehred and finished into a la in the manner known to the art. The presence of the alumina base coat was not found to adversely influence any of the further lamp processing if the limit of weight per unit area a described above is observed. Other Lamps The alumina base coat according to the invention is useful for other lam with a phosphor coating and U.V. emitting light source as well. Referring to Fig. 3, there i shown a high-pressure mercury vapor lamp 20 comprising a discharge vessel 21 enclosed within an outer glass envelope 23 provided with a screw base 24. The lamp envelope 23 is preferably of a conventional hard glass, such as borosilicate glass. The discharge vessel 21 indudes quartz arc tube 22 provided with main dectrodes 25 and 26 at each end, with an auxiliary dectrode 27 bdng located adjacent to the main electrode 25. The filling in the arc tube 22 comprises a measured amount of mercury which is completely vaporized during operation in combination with an inert starting gas such as argon, all of which is conventional in such lamps. The arc tube is supported within the outer jacket by a frame including side rods 28, metal straps 29 and resistor-bridge assembly 30. The lower side rod 28 serves as a conductor between electrode 25 and die base shell. Field wire 31 connects the other dectrode 26 to the center contact of the base. Starting dectrode 27 is connected to main dectrode 26 at the opposite end of the arc tube by the resistor assembly 30. A conventional luminescent layer 32 is applied over the gamma alumina undercoat 34 at the inner surface 35. Instead of a high pressure mercury arc tube, a metal halide arc tube may be used, which in addition to the mercury and inert starting gas, would contain vaporizable metal halides such as sodium, thallium and scandium. Accordingly, Applicants have discovered that contrary to certain prior art teachings, a base coat consisting predominantly of γ (gamma) alumina particles is effective for increasing the light output of a luminescent layer. The increased light output occurs at particle sizes significantly smaller than that previously thought possible. The effect was demonstrated in an F40T12 cool white lamp using commercially available Aluminum oxide C with primary particle size of about 0.01 μm. It should be noted that this is the only known commercially available source of gamma alumina in the claimed size range, so additional tests with primary particle sizes above and bdow 0.01 μm could not be conducted. However, similar improvements in the size range less than 0.05 μm are expected based on the results of the 0.01 μm. Suitable base coat weights for use with other phosphors or fluorescent lamp types to meet the EPACT efficacy standards can be readily experimentally determined based on Applicant's teachings. The difference between α-alumina and γ-alumina is in the distribution of the aluminum and oxygen in the oxide matrix. In α-alumina the distribution of the aluminum relative to the oxygen is very predse, whereas in γ-alumina there are significantly more errors. The mechanism by which gamma alumina arid/or the much smaller particle size produces an increased light output is not understood at this time, but the effect is demonstrated in the above-tests. While preferred embodiments of the invention have been shown and described, various other embodiments and modifications thereof will become apparent to those of ordinary skill in the art, and will fell within the scope of the invention as defined by the appended claims. Accordingly, the specification is to be considered to be illustrative only and not limiting.

Claims: CLAIMS: 1. The invention pertains to an dectric lamp (1; 20), comprising: a. a lamp envdope (3;23) having an inner surface (15;35); b. means within the lamp envdope (3; 23) for generating ultraviolet radiation; c. a luminescent layer (17; 32) adjacent the inner surface (15; 32) of the lamp envdope (3; 23) for generating visible light when impinged by said ultraviolet radiation; and d. a UV-reflecting layer (16; 34), between the inner surface (15; 32) of the lamp envelope (3; 23) and the luminescent material layer (17; 32), for reflecting ultraviolet radiation which has passed through the luminescent layer (17; 32) back into the luminescent layer for increasing the visible light output of the luminescent layer, characterized in that th UV-reflecting layer comprises an agglomerated particulate material of predominantly gamma alumina having a primary crystallite size of less than about 0.05 μm. 2. A lamp according to claim 1, characterized in that the UV-reflecting laye (16; 34) is a base layer disposed directly on the inner surface (15; 32) of the lamp envdope. 3. A lamp according to claim 2, characterized in that the material of the U reflecting layer has a primary crystallite size of about 0.01 μm. 4. A lamp according to claim 3, characterized in that the UV-reflecting laye (16; 34) has a coating weight of between about 0.15 mg/cm 2 and about 0.30 mg/cm 2 . 5. A lamp according to claim 1, 2 or 4, characterized in that the luminescen layer (17; 32) comprises a halophosphate phosphor. 6. A lamp according to claim 1, 2, 3, 4 or 5, characterized in that the mean for generating ultraviolet radiation is comprised by an arc tube (21) disposed within the lam envelope (23), the arc tube (21) including a filling of an ionizable material and a rare gas an a pair of discharge dectrodes (25,26) between which a discharge takes place during lamp operation. 7. A lamp according to claim 1, 2, 3, 4 or 5, characterized in that the mea for generating ultraviolet radiation comprises a filling of an ionizable material and a rare ga within said lamp envdope and a pair of discharge electrodes (5) each adjacent a respective sealed end of said lamp envdope (3).

Inventors: TRUSHELL CHARLES, TRUSHELL, CHARLES
Applicants: PHILIPS ELECTRONICS NV, PHILIPS NORDEN AB, PHILIPS ELECTRONICS N.V.
Application year: 1995
Main classification: H01J61
IPC codes: H01J9, H01J61