Method for securing a thermoplastic insert

Abstract: Method for connection of thermoplastic inserts in structural sandwich panels. This connection is realized by ultrasonic welding. According to the invention the insert (1) is introduced in a through opening (9) in a sandwich panel (8) and welded to the opposed outer skins (6,7). Welding is realized by engagement of the insert by a welding apparatus at its frontal ends.

Description: Field of the Invention: This invention relates to the application of thermoplastic inserts in structural sandwich panels. More specifically this invention relates to a method of securing a thermoplastic insert in a structural sandwich panel which panel has two outer skins from thermoplastic material and an intermediate layer of foam or honeycomb material. This invention relates more specifically to securing a thermoplastic insert, placed in a hole in a structural sandwich panel, to the thermoplastic skins of said sandwich panel using ultrasonic welding. This invention is especially useful in aircraft floor panels. Background of the Invention : Structural sandwich panels are often used in aircraft, as floor and/or bulkhead panels. Traditionally a sandwich panel consists of a pair of relatively thin skin sheets, and an intermediate layer of foam or honeycomb material. Bonded together the result is a panel with a high strength-to-weight ratio, which makes it of interest for use in aircraft. Sandwich panels are very resistant to loads that are evenly distributed over a relatively large surface area. However when sandwich panels are subjected to loads where the force is applied to a point of the panel, the intermediate layer can be crushed locally and the skins can delaminate from the core. This characteristic of sandwich panels is a problem when the panels are to be used as floor panels and therefore have to be secured to a panel support structure. The fasteners such as e.g. screws, bolts, nails, often will crush the intermediate layer locally, when passed through the panel in order to secure the panel to the support structure. Therefore it is conventional in the art of securing sandwich panels to support members, to use inserts in the panel. The inserts have a hole through which the fastener may pass in order to attach the panel to the support members e.g. rails or studs. The insert then isolates the forces exerted by the fastener which are necessary to properly attach the panels to the support member. The method of securing the insert into a hole in the sandwich panel is of direct consequence to the amount of shear and compressive forces the panel in connection to the support member is able to withstand. The inserts used generally comprise a cylindrical body with a vertical cylindrical bore. The shape, size an form of the vertical cylindrical bore in the body is largely dependant on the fastener which is used to secure the panel to the support members. Bolts, screws, and the like exist in various forms and measurements which will require specifically shaped vertical cylindrical bores in the insert. The shape, size and form of the body part of the insert is largely dependant on the method of securing the insert into the panel. Most inserts also comprise a cylindrical head disc which is larger in diameter than the body portion. Because of the importance of good connection and stress relieve between panel, insert, fastener en support member, various methods for securing inserts in sandwich panels have been developed and are known in the prior art. US Patents 4,242,158 and 4,305,540 to Olson, disclose a method of securing an insert in a sandwich panel using an adhesive for one part of the insert and an anvil for forming the other part of the insert. The insert used in this method comprises a cylindrical head disc as top end of a cylindrical body. The length of the body portion is greater than the thickness of the panel. The insert is introduced in a hole in the panel with the cylindrical body, the head disc of the insert rests on top of the top skin of the panel. The bottom part of the cylindrical body of the insert protrudes below the bottom skin of the panel. The head disc of the insert is secured to the top skin of this panel using a suitable adhesive. The anvil presses against the bottom part of insert and this applied pressure causes this protruding portion to flare over and form a flange which secures the insert to the bottom skin. At the same time compressed air blows excess adhesive from the contacted surface from the insert. Sandwich panels with thermoplastic skin sheets allow the use of thermoplastic inserts. Until now the securing of thermoplastic inserts into the sandwich panel did not satisfy the structural requirements imposed by aircraft manufacturers. This is also stated by Worthing in his US Patent 4,817,264, column 2, line 27-45. Worthing consequently chooses to use a two part insert. This two part insert consisting of a metal flange member and a thermoplastic body portion. The method described in this patent uses an adhesive to secure the head disc to the top skin of the panel and ultrasonic energy to soften the protruding end of the insert and pressure to cause this portion to flare over and form a flange. Which flange forms a mechanic connection and is similar to the flange described in US Patents 4,242,258 and 4,305,540 to Olson. Above mentioned methods for securing inserts in sandwich panels are laborious and time consuming. Specifically the time necessary to allow the adhesive to sufficiently harden, largely influence the production time and costs of such sandwich panels. The minimum time for hardening is generally several hours at room temperature. Also the use of adhesives requires more handling by personnel and is more fault sensitive. Also the use of adhesives adds weight to the panel and decrease the weight-to-strength ratio. Another drawback of the prior art is the protruding head disc and bottom flange of the insert when secured into the sandwich panel. One of the objects of this invention is to provide a method for securing a thermoplastic insert , which is placed inside a through hole in a sandwich panel, to vertical hole walls of the thermoplastic skins of said sandwich panel. Said insert for use with the new securing method comprises an essentially cylindrical body with a cylindrical through bore to receive a fastener. It is another object of the invention that ultrasonic energy is applied in order to secure the insert to the thermoplastic skins of the sandwich panel. Another object of the invention is to provide the thermoplastic insert with a concentric thermoplastic rim at the top and bottom of the body, which acts as sacrificial thermoplastic matter and is fused together with the thermoplastic material of top and bottom skins of the sandwich panel as a result of the appliance of ultrasonic energy. It is the object of this invention to provide a method for securing a thermoplastic insert to thermoplastic skins of a sandwich panel which takes not more than 10 seconds in time and results in a watertight connection. The connection between thermoplastic insert and thermoplastic skins of the panel is made by fusing thermoplastic sacrificial matter of the insert with the thermoplastic skin by applying ultrasonic energy. Summary of the invention: The method according to the invention, of securing a thermoplastic insert in a sandwich panel, comprises the steps of providing a sandwich panel with thermoplastic top and bottom skin sheets, drilling a through hole in said sandwich panel, providing a thermoplastic insert having integrally formed sacrificial thermoplastic material, providing an ultrasonic welding apparatus, placing said insert in said through hole, applying ultrasonic energy and pressure until said sacrificial thermoplastic material of said thermoplastic insert is fused to said thermoplastic top and bottom skin sheets of said sandwich panel forming a fused bond, cooling said fused bond before further handling said sandwich panel. The insert for use in this method is made of the same thermoplastic material as the skin sheets of the sandwich panel. Especially the top and bottom part of the inserts are to fit snugly to the through hole edges. Preferably the insert used with this method comprises an essentially cylindrical body with an axial through bore, which bore can receive a fastener with which the panel can be fastened to support members or the like in a structure. The sacrificial thermoplastic material of the insert is an integral part of said insert. Said sacrificial material has the form of a rim on the top and bottom plane of the insert, having a same outer diameter as the outer diameter of the body of the insert, and having a volume sufficient to fill the gap between insert and skin sheet and to form the fused bond between insert and skin sheet under influence of ultrasonic energy. Brief description of the drawings : Figures 1a-d depicts cross-sectional views of a number of preferred embodiments of a thermoplastic insert, prior to securing. Figure 2 is an exploded perspective view of the assembly according to the invention. Figure 3 is a cross-sectional enlarged view of the insert in combination with sandwich panel, prior to securing. Figures 4a-c are cross-sectional views depicting the sequential steps of securing the thermoplastic insert to the top and bottom thermoplastic skin sheets of the sandwich panel. Figure 5 is a cross-sectional view of a sandwich panel and thermoplastic insert secured therein in accordance with this invention. Description of the preferred embodiment : Reference will now be made in detail to the present preferred embodiments of the invention. Figures 1a-d depict a number of possible preferred embodiments of inserts 1 prior to assembly and securing in a hole in a sandwich panel. Insert 1 is designed specifically to enable securing with ultrasonic energy in a sandwich panel with thermoplastic skin sheets. For this reason the generic form of insert 1, according to the invention, comprises a essentially cylindrical body 12 and integrally formed axial thermoplastic sacrificial top and bottom rims 13 and 14. The outer diameter of top and bottom sacrificial rims 13 and 14 are equal to the outer diameter of body 12 of insert 1. In the currently preferred embodiment as shown in FIG.1a, insert 1 further comprises bore 10 with countersunk part 11. When mounting a sandwich panel which is equipped with a number of inserts according to FIG. 1a, fasteners e.g. bolts will be used, countersunk part 11 will then receive the head portion of the bolt while bore 10 will receive the shank portion. Use of inserts with a countersunk portion 11 will then after mounting of the panel on panel support members result in smooth top skin without protruding bolt heads. As shown in Figure 1a the cross-sectional view of rim 13 is rectangular in shape, while rim 14 further comprises a countersunk portion 22. Figure 1b shows an embodiment of insert 1 without countersunk part 11, while rims 13 and 14 are the same as in the embodiment shown in Figure 1a. Figure 1c shows rim 14 in rectangular shape. In Figure 1d an embodiment is shown with recess 19 in body 12, this embodiment is suitable for use of a combination of two securing methods e.g. ultrasonic energy and potting resin. The method according to the invention of securing a thermoplastic insert in a sandwich panel, by fusing thermoplastic sacrificial material of the insert to the thermoplastic material of the skin sheets vertical hole walls of through hole using ultrasonic energy will now be described in general terms. As depicted in Figure 2 insert 1 is placed top side down on anvil 2, consequently hole 9 in top side down placed sandwich panel 4 is aligned with insert 1 and sandwich panel 4 is lowered, with top sheet 6 faced downward, on top of insert 1. Sandwich panel 4 is supported by table 3 in which anvil 2 is situated. Then horn 5 is placed on insert 1 and ultrasonic energy and pressure (of the weight of horn 5) are applied so as to form a fused bond between the thermoplastic material of top and bottom skin sheets 6, 7 and insert 1. Anvil 2 and welding horn 5 are part of the ultrasonic welding apparatus. Welding horn 5 can be moved relatively to table 3, while anvil 2 is fixedly attached in said table 3. In the currently preferred embodiment of the invention an ultrasonic apparatus of the 900-SERIES of manufacturer BRANSON ULTRASONIC CORP, Danburry, Conn. USA is used. Hole 9 in panel 4 is drilled in such a way as to result in a hole with vertical hole walls along the respective top and bottom skin sheets 6 and 7 without delaminations of said skin sheets. In order to attain this, it is preferred to place plates of PERSPEX-glass on top and bottom skin sheets 6, 7 of panel 4 prior to drilling and consequently drill a hole through the first layer of PERSPEX, through skin sheet 6, through core layer 8, through skin sheet 7 and through the second layer of PERSPEX. After the drilling operation the PERSPEX plates are removed. Along this way through hole 9 is formed. Fig. 3 shows a cross-sectional view of insert 1 as shown in Figure 1a, assembled in hole 9 prior to fusing. The figure shows in exaggerated size gap 17a between insert 1 and adjacent top skin hole wall 6a, gap 17b between insert 1 and adjacent bottom skin hole wall 7a and integral sacrificial thermoplastic rims 13 and 14 of insert 1. Rims 13 and 14 must be dimensioned as to provide sufficient sacrificial thermoplastic material to fill gaps 17a and 17b and thus provide the necessary volume for the fused bond between thermoplastic skin sheets and insert. In order to attain a properly fused bond, a glove-like fit for insert 1 in hole 9 is necessary. In the currently preferred embodiment of insert 1 rim 13 has a height of 0.25mm and a width of 0.50mm, and rim 14 has a height of 0.40 mm and a width of 0.50 mm. The height of skin hole wall 6a in the preferred embodiment is 0.75 mm and the height of bottom skin hole wall 7a is 0.5 mm. The glove-like fit of insert 1 in hole 9 is attained in the currently preferred embodiment by drilling hole 9 with a drill having a diameter of 0.2mm larger than the diameter of the insert. Figures 4a-4c show the steps of the method of securing the thermoplastic insert according to the preferred embodiment of the invention. Figure 4a depicts a cross sectional view of insert 1 in being assembled as practised by the invention. Insert 1 is turned top down, and bore 10 with countersunk portion 11 and sacrificial rim 13 facing anvil 2 of the ultrasonic welding apparatus is aligned with head portion 18 of anvil 2. Sandwich panel 4 is also turned top down, top skin sheet 6 facing table 3 and through hole 9 aligned with insert 1 and head portion 18 of anvil 2. Horn 5 of the ultrasonic welding apparatus is aligned with hole 9, insert 1 and anvil 2. Insert 1 is placed over head portion 18 of anvil 2, then panel 4 is placed over insert 1 as shown in Figures 4b and 3. Since rim 13 rests on lower part of head portion 18 of anvil 2, a part of insert 1 protrudes over skin sheet 7. The height of the protruding part is equal to the combined heights of rim 13 and rim 14. As shown in FIG 4b, horn 5 is lowered and rests with flat, solid base 21 on top of rim 14 of insert 1. Once ultrasonic energy is applied, the energy will cause both rims 13 and 14 to soften, flow into respectively gap 17a and 17b and fuse with the also under influence of the ultrasonic energy and friction between insert and hole wall thermoplastic material of respectively top skin sheet 6 and bottom skin sheet 7. Experiments with different forms and measures of the currently preferred embodiment of insert 1 as shown in Figure 1a have taught a minor influence of shape and form of head portion 18 of anvil 2 on the necessary measurements of rim 13. The thermoplastic sacrificial material of rim 13 is efficiently guided into gap 17a under influence of the specific form of head portion 18 of anvil 2. This results in a smaller necessary measurement of rim 13 in the preferred embodiment than rim 14. In effect the head portion of the ultrasonic welding apparatus can be tailor made to the shape, form and dimension of the bore and possible countersunk portion in any thermoplastic insert that is to be secured by use of ultrasonic energy to skin sheets of a sandwich panel. In the currently preferred embodiment insert 1 as shown in FIG 1a comprises countersunk portion 11 in through bore 10, and anvil 2 is shaped to fit. This specifically shaped form of anvil 2 has a guiding effect on the sacrificial thermoplastic material of top rim 13 during the appliance of the ultrasonic energy. Flat, solid base 21 of horn 5 has no such guiding effect, resulting in the necessity to provide more sacrificial material in the bottom rim 14, in order to fill gap 17b and form a fused bond. It stands to reason that if the base 21 of horn 5 could also be tailor made to the shape, form and dimension of the bore of insert 1, without adversely effecting the ultrasonic wave pattern, undoubtedly bottom rim 14 could be of less volume. Figure 4c depicts insert 1 of the preferred embodiment as shown in Figure 1a secured in panel 4, prior to removing the ultrasonic work station formed by table 3, anvil 2 and horn 5. Figure 5 shows a cross sectional view of sandwich panel 4, with insert 1 secured therein. Areas 15a and 15b depict the circumferential fused bond insert and top skin sheet 6 of the panel 4. In area's 16a and 16b the fused bond is depicted between insert and bottom skin sheet 7 of the panel 4. As the thermoplastic material of the insert 1 is the same as the thermoplastic material of the skin sheets 6, 7 of the panel 4, the bond between insert 1 and skin sheets 6, 7 consists of fused thermoplastic material and no clear bond line is visible. This is shown in by indicating the thermoplastic material with continuous shading in top skin sheet 6, body 12 of insert 1 and bottom skin sheet 7, without bond lines between skin sheets 6, 7 and insert 1. It is desirable to use the same thermoplastic material for insert and skin sheets in order to get a proper fused bond. The use of fibre reinforcements is optional. E.g. in the currently preferred embodiment. Polyetherimide (PEI)-inserts were bonded to PEI-fibre reinforced skin sheets. Also PEI-fibre reinforced inserts were bonded to PEI-fibre reinforce skin sheets. Fused bonds between polyether-etherketone (PEEK) inserts and PEEK skin sheets, fibre reinforced PEEK skin sheets and non-fibre reinforced PEEK inserts are also possible. It will be apparent to those skilled in the art that various modifications and variations could be made to the described invention of securing thermoplastic inserts to the thermoplastic skin sheets of a sandwich panel using ultrasonic energy, without departing from the scope of the invention.

Claims: A method for securing a thermoplastic insert (1), placed in a through hole (9) in a sandwich panel (4) of the type comprising top and bottom fiber reinforced thermoplastic skin sheets (6, 7) and an intermediate core layer (8), to said top and bottom skin sheets (6, 7) of said sandwich panel (4), comprising the steps of: providing a thermoplastic insert (1) having integrally formed sacrificial thermoplastic material; placing said insert (1) in said through hole (9) in said panel (4); providing and positioning an ultrasonic appartus comprising a horn (5) and an anvil (2); characterized by applying ultrasonic energy until said sacrificial thermoplastic material of said thermoplastic insert (1) is fused to the hole walls (7a, 7b) of thermoplastic top and bottom skin sheets (6, 7) of said sandwich panel (4) forming a fused bond. A method as described in claim 1, wherein: said integrally formed sacrificial thermoplastic material of said insert (1) comprises cylindrical top rim (13), with outer diameter equal to outer diameter of said insert (1). A method as described in claim 1, wherein: said integrally formed sacrificial thermoplastic material of said insert (1) comprises a cylindrical bottom rim (14), with outer diameter equal to outer diameter of said insert (1). A method as described in claim 1, 2 or 3, wherein: said thermoplastic insert (1) further comprising a through bore (10) for receiving fastener means. A method as described in claim 4, wherein: said anvil (2) of said ultrasonic welding apparatus comprises a protruding head portion (18) which fits snugly into said vertical bore (10) of said thermoplastic insert (1). A method as described in claim 1, wherein: a table (3) is provided for supporting said sandwich panel (4) during the process of securing of said thermoplastic insert (1) to said thermoplastic top and bottom skins sheets (6, 7) of said sandwich panel (4). A method as described in claim 1, wherein: said insert (1) is placed on said anvil (2) and subsequently said sandwich panel (4) is placed on said anvil (2) and table (3) facing said top sheet (8) down in such a way as to inserting said insert (1) in said through hole (9) of said sandwich panel (4). A method according to claim 1, wherein: said insert material corresponds to the material of the skins sheets (6, 7) of the panel (4). A method according to claim 1, wherein said insert (1) comprises a fiber reinforced plastic material. A method as described in claim 9, wherein: said thermoplastic insert (1) is made of PEI with 30% glass. A method as described in claim 1, wherein: said thermoplastic skin sheets (6, 7) comprises PEI fiber reinforced material.

Inventors: OFFRINGA ARNT RINSE, TEUNISSEN JOHN, OFFRINGA, ARNT RINSE, TEUNISSEN, JOHN
Applicants: FOKKER SPECIAL PRODUCTS, FOKKER SPECIAL PRODUCTS B.V.
Application year: 1995
Main classification: B29C65
IPC codes: B29C65