Process for producing 1-hexene

Abstract: A process for preparing 1-hexene which comprises trimerizing ethylene in a 1-hexene solvent in the presence of a catalyst system obtainable by contacting in a 1-hexene solvent the following components (A), (B), (C) and (D): (A) a chromium-containing compound represented by the general formula: CrXkYm wherein X in Xk is a residue of a carboxylic acid, a residue of a 1,3-diketone, a halogen atom or an alkoxyl group, k is an integer of 2 to 4, Y in Ym is an amine compound, a phosphine compound, a phosphine oxide compound, a nitrosyl group or an ether compound and m is an integer of 0 to 6, with the proviso that any two Y's may be same or different; (B) trialkylaluminum or dialkylaluminum hydride; (C) a pyrrole compound or a derivative thereof; (D) a group 13 (III B)-halogen compound represented by the general formula: MTtU3-t or a group 14 (IV B)-halogen compound represented by the general formula: M'Tt'U4-t' wherein M is an atom from the group 13 (III B), M' is an atom from the group 14(IV B), T is an alkyl group, an aryl group, an allyl group or a hydrogen atom, U is a halogen atom, t is a real number of 0 or more and less than 3 and t' is a real number of 0 or more and less than 4.

Description: The present invention relates to a process for producing 1-hexene. The following processes have been known as the processes for producing 1-hexene by trimerization of ethylene. Thus, US-A-4,668,838 discloses a process in which a chromium compound, a hydrocarbyl aluminum hydrolyzed with about 0.8 to about 1.1 mole of water per mole of the aluminum compound and a donor ligand were used as a catalyst. This process, however, had defects that the catalyst was insufficient in activity and selectivity and that maintenance of the activity of the catalyst was uneasy. EP-A-0 537 609 and EP-A-0 622 347 disclose processes in which a chromium complex and an aluminoxane were used as a catalyst. These processes were also unsatisfactory due to insufficient activity and selectivity of the catalyst. EP-A-0 611 743 discloses a process in which a chromium compound, an alkylaluminum compound and an amine or a metal amide were used as a catalyst. The process was also unsatisfactory due to insufficient activity and selectivity of the catalyst. Further, JP-A-6-157655 discloses a process in which a chromium compound, an aluminum compound and a pyrrole compound were used as a catalyst, and EP-A-608 447 discloses a process in which a chromium compound, an aluminum compound, a pyrrole compound and a halogen compound were used as a catalyst. These processes, however, had defects in that an apparatus and an excess of energy were required to separate the desired product 1-hexene from a solvent, which step was necessary because other solvents except 1-hexene were used. Thus, it is the object of the present invention to provide a process for producing 1-hexene which does not have the above disadvantages. This object has been achieved by the surprising finding that 1-hexene can be produced with excellent industrial efficiency, maintaining selectivity of the trimer C6-compound and purity of 1-hexene in the C 6 compound at a superior level, without requiring an apparatus and energy for separating the desired 1-hexene and a solvent, by trimerizing ethylene using a catalyst comprising a chromium-containing compound, an aluminum compound, a pyrrole compound and a group 13( B)-halogen compound or a group 14( B)-halogen compound and using the desired compound 1-hexene as a solvent. Accordingly, the present invention provides a process for producing 1-hexene which comprises trimerizing ethylene in a 1-hexene solvent in the presence of a catalyst system obtainable by contacting in a 1-hexene solvent the following components (A), (B), (C) and (D): (A) a chromium-containing compound represented by the general formula: CrX k L m wherein X is a residue of a carboxylic acid, a residue of a 1,3-diketone, a halogen atom or an alkoxyl group, k is an integer of 2 to 4, L is an amine group, a phosphine group, a phosphine oxide group, a nitrosyl group or an ether group and m is an integer of 0 to 6, with the proviso that any two L's may be same or different; (B) trialkylaluminum or dialkylaluminum hydride; (C) a pyrrole compound or a derivative thereof; (D) a group 13 ( B)-halogen compound represented by the general formula: MT t Z 3-t or a group 14 ( B)-halogen compound represented by the general formula: M'T t' Z 4-t' wherein M is an atom from the group 13 ( B), M' is an atom from the group 14( B), T is an alkyl group, an aryl group, an allyl group or a hydrogen atom, Z is a halogen atom, t is a real number of 0 or more and less than 3 and t' is a real number of 0 or more and less than 4. The present invention will be described in more detail in the following. The component (A) of the catalyst used in the present invention is a chromium compound represented by the general formula: CrX k L m . In the component (A), X is a residue of a carboxylic acid, a residue of a 1,3-diketone, a halogen atom or an alkoxyl group and k is an integer of 2 to 4. L is an amine group, a phosphine group, a phosphine oxide group, a nitrosyl group or an ether group and m is an integer of 0 to 6. It is to be noted that any two L's may be same or different. The residue of the carboxylic acid having 1 to 20 carbon atoms is preferred and includes, for example, residues of 2-ethylhexanoic acid, naphthenic acid, acetic acid, hydroxy-2-ethylhexanoic acid, dichloroethylhexanoic acid, butyric acid, neopentanoic acid, lauric acid, stearic acid and oxalic acid, wherein the residues of 2-ethylhexanoic acid and naphthenic acid are preferred. The residue of the 1,3-diketone having 5 to 20 carbon atoms is preferred and includes, for example, residues of acetylacetone, 2,2,6,6-tetramethyl-3,5-heptanedione, 1,1,1-trifluoroacetylacetone and benzoylacetone. The halogen atom includes chlorine, bromine, iodine and fluorine, wherein chlorine is preferred. The alkoxyl group having 1 to 20 carbon atoms is preferred and includes, for example, a t-butoxy group and an isopropoxy group. The amine group includes, for example, ammonia, ethylenediamine, diethylenetriamine, pyridine, pyridine derivatives, isoquinoline, isoquinoline derivatives and aniline. The pyridine derivatives include 4-dimethylaminopyridine, 4-cyanopyridine, 2-picoline, 3-picoline, 4-picoline, 2-ethylpyridine, 3-ethylpyridine, 4-ethylpyridine, 2-propylpyridine, 4-propylpyridine, 4-isopropylpyridine, 3-butylpyridine, 4-butylpyridine, 4-isobutylpyridine, 4-t-butylpyridine, 2-phenylpyridine, 3-phenylpyridine, 4-phenylpyridine, 2-benzylpyridine, 4-benzylpyridine, 4-phenylpropylpyridine, 4-(5-nonyl)pyridine, 3-(4-pyridyl)-1,5-diphenylpentane, 2-vinylpyridine, 4-vinylpyridine, 4-butenylpyridine, 4-(1-propenylbutenyl)pyridine, 4-pentenylpyridine, 4-(1-butenylpentenyl)pyridine, 2,6-lutidine, 2,4-lutidine, 2,5-lutidine, 3,4-lutidine, 3,5-lutidine, 2-methyl-4-ethylpyridine, 2-methyl-5-ethylpyridine, 3-methyl-4-ethylpyridine, 3-ethyl-4-methylpyridine, 3,4-diethylpyridine, 3,5-diethylpyridine, 2-methyl-5-butylpyridine, 2,6-dipropylpyridine, 2,6-di-t-butylpyridine, 2,6-diphenylpyridine, 2,3-cyclopentenopyridine, 2,3-cyclohexenopyridine, 2-methyl-6-vinylpyridine, 5-ethyl-2-vinylpyridine, 2,4,6-collidine, 2,3,5-collidine, 2-methyl-3-ethyl-6-propylpyridine and 2,6-di-t-butyl-4-methylpyridine. The isoquinoline derivatives include 1-methylisoquinoline, 3-methylisoquinoline and phenanthridine. The phosphine compound includes, for example, tributylphosphine and triphenylphosphine. The phosphine oxide compound includes tributylphosphine oxide and triphenylphosphine oxide. The ether group includes tetrahydrofuran. Specific examples of the component (A) include trichlorotris(ethylenediamine) chromium(III)x3.5 hydrate, trichlorotris(4-dimethylaminopyridine) chromium(III), trichlorotripyridine chromium(III), trichlorotri(4-ethylpyridine) chromium(III), trichlorotri(4-isopropylpyridine) chromium(III), trichlorotri(4-t-butylpyridine) chromium(III), trichlorotri(4-phenylpyridine) chromium(III), trichlorotri(4-phenylpropylpyridine) chromium(III), trichlorotri(4-(5-nonyl)-pyridine) chromium(III), trichlorotri(3,5-lutidine) chromium(III), tribromotripyridine chromium(III), trifluorotripyridine chromium(III), dichlorobis(pyridine) chromium(II), dibromobis(pyridine) chromium(II), trichlorotriisoquinoline chromium(III), trichlorotrianiline chromium(III), trichlorotritetrahydrofuran chromium(III), chromium(III) tris(2-ethylhexanoate), chromium(II) bis(2-ethylhexanoate), chromium(III) tris(naphthenate), chromium(II) bis(naphthenate), chromium(III) tris(acetate), chromium(II) bis(acetate), chromium(III) tris(acetylacetonate), chromium(II) bis(acetylacetonate), chromium(III) tris(2,2,6,6-tetramethyl-3,5-heptadionate), chromium(IV) tetra(t-butoxide), dichlorodinitrosylbis(triphenylphosphineoxide)chromium, dichlorobis(triphenylphosphineoxide) chromium(II), dichlorodinitrosylbis(4-ethylpyridine) chromium , trichlorobis(tributylphosphine) chromium(III) dimer and trichloro(1,4,7-trimethyl-1,4,7-triazacyclononane chromium(III). In particular, trichlorotris(ethylenediamine) chromium(III)x3.5 hydrate, trichlorotris(4-dimethylaminopyridine) chromium(III), trichlorotripyridine chromium(III), trichlorotri(4-ethylpyridine) chromium(III), trichlorotri(4-isopropylpyridine) chromium(III), trichlorotri(4-t-butylpyridine) chromium(III), trichlorotri(4-phenylpyridine) chromium(III), trichlorotri(4-phenylpropylpyridine) chromium(III), trichlorotri(4-(5-nonyl)-pyridine) chromium(III), trichlorotri(3,5-lutidine)chromium(III), trichlorotriisoquinoline chromium(III) are preferred. As component (A) of the present invention, the components in which X is a halogen atom and k is 2 or 3 are particularly preferred. Component (B) of the catalyst used in the present invention includes trialkylaluminum or dialkylaluminum hydride. The alkyl group in component (B) is exemplified by a methyl group, ethyl group, propyl group, isopropyl group, butyl group, isobutyl group, hexyl group and octyl group. Specific examples of component (B) include trimethylaluminum, triethylaluminum, tripropylaluminum, tributylaluminum, triisobutylaluminum, trihexylaluminum, trioctylaluminum, diethylaluminum hydride and diisobutylaluminum hydride, wherein trialkylaluminum, especially triethylaluminum, is particularly preferred. Component (C) of the catalyst used in the present invention includes a pyrrole compound and derivatives thereof. Specific examples of component (C) include pyrrole, 2, 5-dimethylpyrrole, 2,5-diethylpyrrole, 2,5-dipropylpyrrole, 2-methylpyrrole, 2-ethylpyrrole, 3-methylpyrrole, 3-ethylpyrrole, 3-propylpyrrole, 3-butylpyrrole, 3-heptylpyrrole, 3-octylpyrrole, 3-ethyl-2,4-dimethylpyrrole, 2,3,4,5-tetramethylpyrrole, 4,5,6,7-tetrahydroindole, indole, carbazole, diisobutylaluminum-2,5-dimethylpyrrolide, diethylaluminum 2,5-dimethylpyrrolide, dimethylaluminum-2,5-dimethylpyrrolide, diisobutylaluminum pyrrolide, diethylaluminum pyrrolide and dimethylaluminum pyrrolide. Component (D) of the catalyst used in the present invention is a group 13( B)-halogen compound represented by the general formula: MT t Z 3-t or a group 14 ( B)-halogen compound represented by the general formula: M'T t' Z 4-t' . In the formula, M is an atom from the group 13 ( B) and M' is an atom from the group 14 ( B). T is an alkyl group, an aryl group, an allyl group or a hydrogen atom, Z is a halogen atom, t is a real number of 0 or more and less than 3 and t' is a real number of 0 or more and less than 4. The atom of the group 13 ( B) includes, for example, boron, aluminum, gallium, indium and thallium, wherein aluminum is particularly preferred. The atom of the group 14 ( B) includes, for example, carbon, silicon, germanium, tin and lead, wherein carbon, silicon, germanium and tin are particularly preferred. The alkyl group includes, for example, a methyl group, ethyl group, propyl group and a butyl group. The aryl group includes, for example, a phenyl group, tolyl group, xylyl group, indenyl group and a naphthyl group. The allyl group includes, for example, a 1-propenyl group. The halogen atom includes chlorine, bromine, iodine and fluorine, wherein chlorine and bromine are preferred. The group 13 ( B)-halogen compound includes aluminum halide compounds such as diethylaluminum chloride, diisobutylaluminum chloride, ethylaluminum dichloride, isobutylaluminum dichloride and ethylaluminum sesquichloride. The group 14 ( B)-halogen compound includes organic halogen compounds such as n-butyl bromide, isobutyl bromide, t-butyl bromide, n-hexyl bromide, n-octyl bromide, 1,4-dibromobutane, 1,6-dibromohexane, n-butyl chloride, isobutyl chloride, t-butyl chloride, n-hexyl chloride, n-octyl chloride, 1,4-dichlorobutane, 1,6-dichlorohexane, bromobenzene and chlorobenzene, germanium halide compounds such as germanium tetrachloride, tin halide compounds such as tin tetrachloride, silicon halide compounds such as trimethylchlorosilane. The ratio (molar ratio) (A)/(B)/(C)/(D) is usually 1/(1-100)/(1-50)/(1-50), preferably 1/(5-75)/(1-20)/(1-30) and more preferably 1/(5-50)/(1-10)/(1-10). If the amount of (A) is too small, the activity may be insufficient. If the amount of (B) is too small, again the activity may be insufficient. If the amount of (C) is too small, then the selectivity of 1-hexene may lower. When the components (A), (B), (C) and (D) are contacted, it is necessary to use 1-hexene as the solvent. This allows disuse of an apparatus and energy for separating the desired 1-hexene. When another solvent than 1-hexene, such as for example, butane, isobutane, pentane, hexane, heptane, 1-octene, toluene, xylene, chlorobenzene and dichlorobenzene is used, it will be necessary to recycle the solvent and to equip a recovering apparatus for economy purpose. In addition, a big pressure vessel for trimerization will be required corresponding to the volume of the solvent to be used. Furthermore, excess energy will be required in order to separate the desired 1-hexene from the solvent. Thus, the use of 1-hexene as the solvent lead to the advantages that both the fixed expense and the working expenses are minimized. For preparing the catalyst system used in the present invention, the components (A), (B), (C) and (D) are dissolved or suspended with stirring in 1-hexene as the solvent under an inert gas atmosphere such as nitrogen or argon or a reactant ethylene gas atmosphere. It is preferred that the components (A), (C) and (D) are charged first and thereafter the component (B) is added to the solution. The produced catalyst system may be used for trimerization reaction without removing 1-hexene as the solvent. The temperature for contacting the components (A), (B), (C) and (D) is 10 °C or below, preferably -100°C to 10°C and more preferably -20°C to 5 °C. If the temperature is too high, the selectivity of 1-hexene may lower. The period for contacting the components (A), (B), (C) and (D) may be suitably selected but is usually from 1 minute to 24 hours. Long-term contacting may create no problem but there is no economical merit. The trimerization reaction according to the present invention may be carried out in the following manner. Briefly, the above mentioned catalyst system and 1-hexene as the solvent are charged in a pressure reaction vessel and ethylene is introduced. The temperature is risen in order to initiate the reaction. The amount of the catalyst may be adjusted such that the concentration of chromium atom in the reaction mixture is preferably 0.000001 to 0.05 mole/l and more preferably 0.00001 to 0.01 mole/l. If the amount of the catalyst system is too small, the activity may be insufficient. The reaction temperature is usually 20 to 200°C and preferably 20 to 150 °C. When the reaction temperature is too low, the activity of the catalyst may also be low, and when, on the contrary, the reaction temperature is too high, the selectivity of the desired 1-hexene may lower. The pressure is usually from the atmospheric pressure to 1961.33 N/cm 2 (200 Kg/cm 2 ) and preferably 98.07 to 980.67 N/cm 2 (10 to 100 Kg/cm 2 ). When the pressure is too low, the activity may be insufficient. The reaction period is usually from 0.1 to 8 hours and preferably 0.5 to 7 hours. When the reaction period is too short, the reactivity may be low. The recovery of the desired 1-hexene from the reaction mixture of the present invention may be accomplished by, for example, distillation. The catalyst system used in the present invention may be used as above or in the form of a carrier-bound catalyst carried on or over an inorganic carrier such as silica, alumina, silica-alumina, zeolite or aluminum phosphate or an organic carrier such as an ion-exchange resin, polystyrene or polyvinylpyridine. In the present invention, 1-hexene is used as the solvent for carrying out the trimerization reaction as described above. The solvent 1-hexene may be used in one portion from the time of preparing the catalyst system or alternatively may be added thereafter to the solvent used for preparing the catalyst system. It is the characteristic of the present invention that the solvent for preparing the catalyst and for carrying out the trimerization is limited to 1-hexene. The reason for the limitation is described above. When the catalyst is prepared using the components (A), (B), (C) and (D) stored in a solvent other than 1-hexene, a small amount of such solvent other than 1-hexene may be contaminating the catalyst system or trimerization reaction, but such contamination does not cause trouble insofar as the contamination of said other solvent is not more than 5 % by weight of, for example, 1-hexene as the solvent for trimerization reaction. Example 1 Under an argon atmosphere, 20 ml of degassed and dried 1-hexene as the solvent was cooled to 2 to 3 °C in an ice-water bath and 13.4 mg (0.026 m mole) of trichlorotris(4-dimethylaminopyridine) chromium(III) (A1), 7.2 mg (0.076 m mole) of 2,5-dimethylpyrrole (C1) (9.5 % by weight solution in heptane) and 14.7 mg (0.069 m mole) of germanium tetrachloride (D1) (0.8 mole/l solution in heptane) were added while stirring to form a suspension. Then, under an ethylene atmosphere, the above suspension, 85.5 mg (0.75 m mole) of triethylaluminum (B1) (1.0 mole/l solution in heptane) and 140 ml of 1-hexene as the solvent were charged into a pressure reaction vessel with an inner volume of 0.5 liter, previously cooled to 10°C or below in an ice-water and ethylene was introduced up to a pressure of 245.17 N/cm 2 (25 Kg/cm 2 G). The trimerization reaction was carried out by rising temperature while stirring. The reaction temperature was 100°C, the reaction pressure 392.27 N/cm 2 (40 Kg/cm 2 G), the reaction period 2 hours, and ethylene was supplied as required. Solid and liquid phases in the reaction mixture were separated and the amount of the polymer product was calculated from the weight of the solid phase and analysed by gas chromatography of the liquid phase. The reaction conditions and results are shown in Table 1 and 2. Example 2 The procedure of Example 1 was repeated except that 10.5 mg (0.026 m mole) of trichlorotris(ethylenediamine) chromium(III)x3.5 hydrate (A2) was used as the chromium compound in place of trichlorotris(4-dimethylaminopyridine) chromium(III) (A1). The reaction conditions and the results are shown in Table 1 and 2. Example 3 The procedure of Example 1 was repeated except that 12.3 mg (0.026 m mole) of chromium(III) tris(2-ethylhexanoate) (A3) (0.8 % by weight solution in heptane) was used as the chromium compound in place of trichlorotris(4-dimethylaminopyridine) chromium(III) (A1) and the reaction temperature was changed to 80°C. The reaction conditions and the results are shown in Tables 1 and 2. Example 4 The procedure of Example 1 was repeated except that 18.6 mg (0.075 m mole) of ethylaluminum sesquichloride (D2) (1.0 mole/l solution in heptane) was used as the halogen compound in place of germanium tetrachloride (D1) and the reaction period was changed to 3 hours. The reaction conditions and the results are shown in Tables 1 and 2. Example 5 The procedure of Example 4 was repeated except that 12.3 mg (0.026 m mole) of chromium(III) tris(2-ethylhexanoate) (A3) (0.8 % by weight solution in heptane) was used as the chromium compound in place of trichlorotris(4-dimethylaminopyridine) chromium(III) (A1). The reaction conditions and the results are shown in Tables 1 and 2. Comparative Example 1 The procedure of Example 2 was repeated except that germanium tetrachloride (D1) was not used. The reaction conditions and the results are shown in Tables 1 and 2. Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Com. Ex. 1 Catalyst Component Kind (A) A1 A2 A3 A1 A3 A2 (B) B1 B1 B1 B1 B1 B1 (C) C1 C1 C1 C1 C1 C1 (D) D1 D1 D1 D2 D2 - Composition (A) 1 1 1 1 1 1 (B) 29 29 30 29 29 29 (C) 3 3 3 3 3 3 (D) 3 3 3 3 3 - Temperature for catalyst preparation(°C) <10 <10 <10 <10 <10 <10 Amount of catalyst 0.16 0.16 0.16 0.16 0.16 0.16 Reaction temperature (°C) 100 100 80 100 100 100 Reaction Pressure N/cm 2 392.27 392.27 392.27 392.27 392.27 392.27 (Kg/cm 2 G) 40 40 40 40 40 40 Reaction Period (hr) 2 2 2 3 3 2 Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Com. Ex. 1 Results Activity g/g-Cr 58440 55672 57922 92649 64074 26020 g/g-Cr/hr 29220 27836 28961 30883 21358 13010 Selectivity % C 6 -compound 79.8 74.8 70.9 76.4 60.6 28.3 1-hexene 78.8 73.3 69.6 75.4 58.8 22.7 C 4 -compound 0.1 0.2 0.2 0.2 1.1 7.0 C 8 -compound 0.4 0.7 0.8 0.5 2.1 6.3 C 10 -compound 17.3 20.9 22.4 19.4 26.4 42.2 Polymer <0.1 0.1 0.5 <0.1 0.1 0.2 Purity of 1-hexene 98.6 98.1 98.2 98.7 97.1 80.2

Claims: A process for producing 1-hexene which comprises trimerizing ethylene in a 1-hexene solvent in the presence of a catalyst system obtainable by contacting in a 1-hexene solvent the following components (A), (B), (C) and (D): (A) a chromium-containing compound represented by the general formula: CrX k L m wherein X is a residue of a carboxylic acid, a residue of a 1,3-diketone, a halogen atom or an alkoxyl group, k is an integer of 2 to 4, L is an amine group, a phosphine group, a phosphine oxide group, a nitrosyl group or an ether group and m is an integer of 0 to 6, with the proviso that any two L's may be same or different; (B) trialkylaluminum or dialkylaluminum hydride; (C) a pyrrole compound or a derivative thereof; (D) a group 13 ( B)-halogen compound represented by the general formula: MT t Z 3-t or a group 14 ( B)-halogen compound represented by the general formula: M'T t' Z 4-t' wherein M is an atom from the group 13 ( B), M' is an atom from the group 14( B), T is an alkyl group, an aryl group, an allyl group or a hydrogen atom, Z is a halogen atom, t is a real number of 0 or more and less than 3 and t' is a real number of 0 or more and less than 4. The process according to Claim 1, wherein X in the component (A) is a halogen atom. The process according to Claim 1 or 2, wherein the component (B) is trialkylaluminum. The process according to any of claims 1 to 3, wherein the catalyst system is obtainable by first adding the components (A), (C) and (D) to the solvent and then adding the component (B).

Inventors: ITO YOSHIAKI, IWANAGA KIYOSHI, TAMURA MITSUHISA, UCHIDA KENSHI, ITO, YOSHIAKI, IWANAGA, KIYOSHI, TAMURA, MITSUHISA, UCHIDA, KENSHI
Applicants: SUMITOMO CHEMICAL CO, SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1995
Main classification: C07C11
IPC codes: C07C11, C07B61, C07C2, B01J31