LIGHT MODULATING DEVICE HAVING A MATRIX PREPARED FROM ALLYL REACTANTS

Abstract: In one aspect, an optionally responsive film that includes liquid crystal dispersed in a polymer matrix that is the reaction product of; (a) 5-60 % by weight of one or more allyl reactants; (b) 15-95 % by weight or one or more ene reactants other than an allyl; and (c) 0-20 % by weight of one or more thiol reactants. In a second aspect, the film is the reaction product of: (a) 5-50 % by weight of one or more allyl reactants; and (b) 2-25 % by weight of one or more methacrylate reactants.

Description: LIGHT MODULATING DEVICE HAVING A MATRIX PREPARED FROM ALLYL REACTANTS Background of the Invention Field of the Invention This invention relates to light modulating devices (e.g., a polymer-dispersed liquid crystal device hereinafter referred to as a "PDLC device") . Description of the Related Art Various types of light modulating devices are known. One type is the so-called PDLC device that includes an electrically responsive liquid crystal layer in which liquid crystal droplets are dispersed throughout a polymer matrix. One way to prepare the liquid crystal layer is by combining the liquid crystal material with a polymerizable matrix precursor and then subjecting the mixture to polymerization conditions. Polymerization causes phase separation of the liquid crystal material, resulting in the formation of liquid crystal droplets dispersed throughout the polymerized matrix. PDLC devices are translucent in the absence of an electric field due to light scattering and become transparent upon application of the field. Reverse mode PDLC devices are also known. These devices are transparent in the absence of an electric field and become translucent upon application of the field. Various PDLC matrices are known. They include the polymerization products of epoxy, isocyanate, and certain photo-curable vinyl monomers (e.g., acrylates or the reaction product of a multi-functional thiol with a multi-functional acrylate or a multi-functional allyl) . Summary of the Invention In a first aspect, the invention features an optically responsive film that includes liquid crystal dispersed in a polymer matrix that is the reaction product of (a) 5-60% by weight of one or more allyl reactants; (b) 15-95% by weight of one or more ene reactants other than an allyl; and (c) 0-20% by weight of one or more thiol reactants. As used herein, an "ene" is a reactant having a polymerizable carbon-carbon double bond. Weight percentages are calculated on the basis of matrix reactants plus initiator being equal to 100%. Examples of preferred non-allyl enes include mono- or multi-functional vinyl ethers, acrylates, methacrylates, acrylamides, methacrylamides, vinyl silanes, or combinations thereof, with vinyl ethers, acrylates, and methacrylates being particularly preferred. A "multi-functional" reactant is a reactant containing two or more groups that participate in the polymerization reaction by reacting with the carbon- carbon double bond(s) of the allyl reactant. A "mono- functional" reactant, in contrast, contains only one such group. In preferred embodiments, the film may be the reaction product of (a) 20-30% by weight of one or more allyl reactants; (b) 55-80% by weight of one or more ene reactants other than an allyl; and (c) 0-10% by weight of one or more thiol reactants. In one preferred embodiment, the amount of thiol is 0% by weight. In a second aspect, the invention features an optically responsive film that includes liquid crystal dispersed in a polymer matrix that is the reaction product of: (a) 5-50% by weight of one or more allyl reactants; and (b) 2-25% by weight of one or more methacrylate reactants. In one preferred embodiment of the second aspect of the invention, the film may be the reaction product of: (a) 30-45% by weight of one or more allyl reactants; and (b) 15-25% by weight of one or more methacrylate reactants. In another preferred embodiment, the film may be the reaction product of: (a) 5-50% by weight of one or more allyl reactants; (b) 2-25% by weight of one or more methacrylate reactants; and (c) one or more thiol reactants. In yet another preferred embodiment, the film may be the reaction product of: (a) 35-45% by weight of one or more allyl reactants; (b) 15-20% by weight of one or more methacrylate reactants; and (c) 25-35% by weight of one or more thiol reactants. In a third aspect, the invention features an optically responsive film that includes liquid crystal dispersed in a polymer matrix that is the reaction product of: (a) two or more ene reactants in which 5- 70% of all ene groups are allyl groups, and (b) one or more thiol reactants, the ratio of thiol groups to all ene groups being no greater than 0.2. As used herein, "all ene groups" refers to both allyl and non-allyl ene groups. In one preferred embodiment of the third aspect of the invention, 5-20% of all ene groups are allyl groups. In another preferred embodiment, the ratio of thiol groups to all ene groups is 0. In a fourth aspect, the invention features an optically responsive film that includes liquid crystal dispersed in a polymer matrix that is the reaction product of two or more ene reactants in which 10-90% of all ene groups are allyl groups and 5-30% of all ene groups are methacrylate groups. Preferably, 65-85% of all ene groups are allyl groups and 15-30% of all ene groups are methacrylate groups. The film may also include the reaction product of the two or more ene reactants and one or more thiol reactants, the ratio of thiol groups to all ene groups ranging from 0.65 to 0.75. The invention further features light modulating devices incorporating the above-described films. The invention provides optically responsive films exhibiting good physical and electro-optical properties. Other features and advantages of the invention will be apparent from the following description of the preferred embodiments thereof, and from the claims. Brief Description of the Drawings The invention will be more fully understood with reference to the following drawings in which: FIG. 1 is a schematic view, partially in cross- section, of a light modulating device according to the invention. FIG. 2 is a cross-sectional view of an extrusion die useful in preparing films according to the invention. FIG. 3 is an enlarged cross-sectional view of the die of FIG. 2. FIG. 4 is a cross-sectional view of an alternate extrusion die useful in preparing films according to the invention. Description of the Preferred Embodiments Referring to FIG. 1, there is shown a light modulating device 10 comprising an optically responsive film 12 having a multiplicity of discrete liquid crystal droplets 14 having diameters in the range from about 0.1 to 10 times the wavelength of light to be scattered dispersed in a polymeric matrix 16 that is the polymerization product of one or more allyl reactants, one or more non-allyl ene reactants, and, optionally, one or more thiol reactants. The allyl reactants may be mono-functional, multi¬ functional, or a combination thereof. Representative reactants of this class of materials include mono-, di- and triallyl compounds and allyl compounds containing an hydroxyl group reacted with a mono- or multi¬ functional isocyanate, e.g., triallyl isocyanurate, trimethylolpropane diallyl ether, allyl benzene, allylcyclohexane, diallyldiphenylsilane, and allyl- functional oligomers such as 9460 commercially available from Monomer-Polymer & Dajac Laboratories, Inc., Trevose, PA. Also suitable are allyl-functional siloxanes (e.g., the hydrolysis product of allyldimethylchlorosilane) , as well as allyl oligomers of polyurethanes, polyesters, polyols, alkylene oxides, polybutadienes, or epoxies. The non-allyl ene reactants may also be mono- functional, multi-functional, or a combination thereof. Examples of suitable ene reactants include mono- functional and multi-functional acrylates, methacrylates, acrylamides, methacrylamides , vinyl silanes, vinyl ethers, fumarates, maleates, and combinations thereof. Examples of mono-functional acrylates and methacrylates include acrylate and methacrylate esters of non-tertiary alkyl alcohols, the molecules of which have from 1 to about 14 carbon atoms. Included within this class of matrix reactants, are, for example, isooctyl acrylate, isononyl acrylate, 2-ethylhexyl acrylate, decyl acrylate, dodecyl acrylate, n-butyl acrylate, hexyl acrylate, isooctyl methacrylate, and lauryl methacrylate. Examples of multi-functional acrylates and methacrylates include 1,6 hexanedioldiacrylate, trimethylpropane triacrylate, propylene glycol dimethacrylate, pentaerythritol tetraacrylate, and 1,2- ethylene glycol diacrylate. Exa ples of mono-functional acrylamides and methacrylamides include N,N-dimethylacrylamide, N,N- diethylacrylamide, N-dodecylmethacrylamide, and N- ethylmethacrylamide. Examples of multi-functional acrylamides and methacrylamides include 1,6-hexamethylenebisacrylamide, N,N '-octamethylene-bisacryla ide, 1,6- hexamethylenebismethacrylamide, N,N-iso-valerylidene- bis-methacryla ide, and -xylene-bisacrylamide. Examples of mono-functional vinyl silanes include vinyltrimethylsilane, vinyltrimethoxysilane, vinyltris(trimethylsiloxy) silane, and siloxanes such as that commercially available from Hϋls America under the trade designation "PS408." Examples of multi-functional vinyl silanes include trivinylmethylsilane, 1,3-divinyltetramethyldisiloxane, 1,3-divinyl-l,3-diphenyl-dimethyldisiloxane, divinyldimethylsilane, divinyldiphenylsilane, 1,1,3,3- tetravinyldimethyldisiloxane, tetravinylsilane, and 1,3,5,7-tetravinyltetramethylcyclotetrasiloxane. Examples of suitable vinyl ethers include hydroxybutyl vinyl ether (HBVE, commercially available from International Specialty Products, Wayne, NJ) ; 1,4- cyclohexanedimethanol divinyl ether (CHVE, commercially available from International Specialty Products, Wayne, NJ) ; propenyl ether of propylene carbonate (PEPC, commercially available from International Specialty Products, Wayne, NJ) ; triethylene glycol divinyl ether (DVE-3, commercially available from International Specialty Products, Wayne, NJ) ; butanediol divinyl ether (commercially available from BASF, Parsippany, NJ) ; vinyl ethers commercially available from Allied- Signal Corp. , Morristown, NJ under the tradename "Vectomer" (e.g., Vectomer 2010, 2020, 4010, and 4020); vinyl ether-maleate mixtures commercially available from DSM Resins U.S., Inc., Elgin, IL under the tradename "Uralac" (e.g., Uralac 3004-102 and 3004- 300); and fluorinated vinyl ethers (e.g., C g F 17 S0 2 N(C 2 H 5 )CH 2 CH 2 OCH=CH 2 prepared according to the procedure described in U.S. Patent No. 3,078,245, hereby incorporated by reference) . Also suitable are ene-functional siloxanes such as acryloyl-functional siloxanes (e.g., l,3-bis[(p- acryloxymethyl)phenethyl]tetramethyldisiloxane) ; methacryloyl-functional siloxanes (e.g., l,3-bis(3- methacryloxypropyl)tetramethyldisiloxane and siloxanes such as that commercially available from Hϋls America under the trade designation "PS406") ; vinyl-functional siloxanes (e.g., 1,3-divinyltetramethyldisiloxane, 1,3- divinyl-1,3-diphenyl-dimethyldisiloxane, 1,1,3,3- tetravinyldimethyldisiloxane, and 1,3,5,7- tetravinyltetramethylcyclotetrasiloxane) ; and hexenyl- functional siloxanes (e.g., l,3-bis(6-hex-l- enyl)tetramethyldisiloxane, which is the hydrolysis product of 6-hex-l-enyldimethylchlorosilane) . Also useful are vinyl ether-functional and ( eth)acrylated oligomers of polyurethanes, polyesters, polyols, alkylene oxides, polybutadienes, or epoxies. An example of a suitable acrylated polybutadiene is SARTOMER CD 5000 (commercially available from Sartomer Co.). A useful acrylated polyester is SARTOMER 609 (from Sartomer Co. ) and a suitable acrylated polyurethane is SARTOMER 9610 (Sartomer Co.). Other useful acryl oligomers include those sold under the trade name "Ebecryl" by Radcure Specialties and the trade name "Photomer" from Diamond Shamrock. The allyl and ene reactants may be used in combination with reactants from one or more of the following classes of reactants: (1) Class I includes multi- and mono-functional thiols, with the proviso that the total thiol content of the matrix is no greater than about 20% by weight. Exa ples of suitable mono-functional thiols include isooctyl 3-mercaptopropionate. Preferred multi¬ functional thiols have the general formula Z[OCO(CH 2 ) n SH] m where Z is a polyvalent organic moiety which is a CHo. 3 group-containing nucleus of a tri- or tetravalent alcohol of the type of glycerol or pentaerythritol, m is 3 or 4, and n is an integer between 1 and 5, inclusive. Specific examples include trimethylolpropane tris(3-mercaptopropionate) and pentaerythritol tetra(3-mercaptopropionate) . Also useful are mercapto-functional siloxanes (e.g., poly(3-mercaptopropylmethylsiloxane) , or oligomers or copolymers thereof; 1,1,3,3-tetramethyl- 1,3-bis(3-mercaptopropyl)disiloxane; and siloxanes such as that commercially available from Hϋls America under the trade designation "PS405") . The thiols may be included as part of UV polymerizable systems based on thiol-ene chemistry in which one or more multi- or mono-functional enes (e.g., a mono- or multi-functional allyl, acrylate, methacrylate, or combination thereof) reacts with the thiol. Commercially available materials based upon thiol-ene chemistry include NOA 65 and NOA 68, each of which includes a photoinitiator and is available from Norland Products, Inc. New Brunswick, New Jersey, and compositions commercially available under the trade designation RCC-15C, RCC-15D, RCP-611, and WCC-2B from W.R. Grace & Co. , Atlanta, GA. (2) Class II includes multi- and mono-functional silicon hydrides. Examples of suitable mono-functional silicon hydrides include trimethylsilane and dimethylphenylsilane. Examples of suitable multi¬ functional silicon hydrides include dimethylsilane, diphenylsilane, and methylphenylsilane. Also suitable are hydrosiloxanes (e.g., 1,1,3,3- tetramethyldisiloxane; 1,3,5,7,9- pentamethylcyclopentasiloxane; phenyltris(dimethylsiloxy)silane; and 1,3,5,7- tetramethylcyclotetrasiloxane) . In choosing the amounts and identities of matrix reactants, several criteria generally apply. First, it is desirable to choose matrix reactants to adjust polymerization rate (and thereby optimize, e.g., haze, switching voltage, and droplet structure of the PDLC film 12, as well as allow the use of lower liquid crystal contents) . For example, allyls, vinyl silanes, vinyl ethers without maleates, and methacrylates tend to homopolymerize free-radically very slowly and therefore should preferably be used in combination with co-reactants that sustain and increase the polymerization rate. Such a combination will allow a high degree of conversion to be reached in a reasonable length of time. Examples of such co-reactants include acrylates, acrylamides, vinyl ether/maleate mixtures, and thiols. However, the amount of thiol is preferably limited (e.g., not to exceed about 20% by weight) and/or the functionality of the thiol is preferably high, resulting in conditions which minimize production of a matrix having a relatively low molecular weight and/or a relatively low degree of crosslinking. Low molecular weight or low crosslink density matrices are produced when the thiol concentration falls outside of these constraints because thiols are chain transfer agents that can terminate propagating polymer chains; and moreover, thiols do not readily homopolymerize. In addition, when a relatively high percentage of slow- reacting reactants (e.g., allyls, vinyl silanes, or methacrylates) is used, the slow-reacting reactants preferably should have relatively large equivalent weights (e.g., oligomers) and the rate sustaining co- reactants should be of relatively low equivalent weight (e.g., monomers) . A second criterion relates to the functionality of the reactants. Specifically, it is desirable that at least some of the allyl reactants and/or some of the ene reactants are multifunctional in order to produce a crosslinked matrix. Crosslinking increases the resistance to damage caused by extreme temperatures and further reduces "memory" effects. "Memory" refers to the change in zero-volt opacities before and after the device has been powered. Generally, the opacity difference (and thus the contrast between the on- and off-states) is greatest the first time the PDLC device is operated. On the other hand, too high a crosslinking level is undesirable because it shifts the switching voltage to higher voltages. The amount of multi-functional reactant(s) required will depend upon the structure and functionality of the particular reactant(s) . Low molecular weight and/or high functionality (i.e., low equivalent weight) reactants (e.g., hexanediol diacrylate) and reactants with more rigid backbones between functional groups (e.g., 1,4- cyclohexanedimethanol divinyl ether) are preferably used at lower levels than flexible and/or high equivalent weight reactants (e.g., triethylene glycol divinyl ether) . In addition, polar mono-functional reactants such as acrylic and methacrylic acid act as weak crosslinkers through hydrogen bonding. It has also been found that optical properties such as haze can be minimized by optimizing the refractive index of the matrix reactants relative to that of the liquid crystal material. For example, it has been found that optimizing the relative levels of isooctyl acrylate and 2-phenoxyethyl acrylate (i.e., replacing some of the isooctyl acrylate with 2- phenoxyethyl acrylate, or vice-versa) , minimizes haze in the powered PDLC device. To enhance the T-peel adhesion of optically responsive film 12, one or more copolymerizable acid reactants may copolymerized with the allyl, ene, and (optionally) thiol reactants. Examples of suitable acid reactants include unsaturated carboxylic acids (e.g., acrylic acid, methacrylic acid, crotonic acid, vinyl acetic acid, itaconic acid, maleic acid, fumaric acid, allylacetic acid, cinammic acid, and unsaturated acid-terminated polyester oligomers) ; mono-esters of unsaturated dicarboxylic acids (e.g., mono-esters of maleic, fumaric, and itaconic acid) ; mercapto- functional carboxylic acids (e.g., 3-mercaptopropionic acid); and combinations thereof. The amount of acid reactant preferably is not so high as to yield a brittle inflexible film with a relatively low T-peel strength and/or a film with a high degree of memory. Liquid crystal materials useful in forming the droplets 14 may be nematic or cholesteric. Furthermore, they may have either positive or negative dielectric anisotropy. Particularly preferred (in the case of light modulating devices for automotive and architectural applications) are nematic liquid crystals having positive dielectric anisotropy. Commercially useful examples of such liquid crystal materials include LICRISTAL E7, BL006, BL009, ML1005, ML1008, 17151, 17153, 17315, 17722 (sometimes available under the trade designation BL038) , and 17723 (sometimes available under the trade designation BL036) , all of which are available from EM Industries, Hawthorne, New York. Mixtures of these liquid crystal materials may also be used. Low birefringence liquid crystal mixtures may be used as well, e.g., to provide a wider viewing angle. Formation of an optically responsive film according to the invention is typically carried out in a phase separation process. Polymerization induced- phase separation has been found to be useful when the uncured polymer matrix material is miscible with a low molecular weight liquid crystal material. Liquid crystal droplets form when the solubility of the liquid crystal material in the polymer matrix material decreases as a result of an increase in the molecular weight of the matrix material that occurs when the matrix material polymerizes to form a continuous phase. As the solubility of the liquid crystal material decreases, it phase separates from the polymer matrix material and forms droplets. The droplets increase in size and/or purity until the polymer matrix material locks in the final droplet morphology. The polymerization is carried out in the presence of the liquid crystal material, thereby enabling tailoring of the polymer matrix in terms of molecular weight, crosslink density, liquid crystal compatibility, and/or adhesion. Although many polymer matrix material/liquid crystal combinations according to the invention form miscible mixtures at room temperature, in others it may be necessary to heat the combination slightly to form a homogeneous solution and prevent premature phase separation. Matrix 16 can be prepared by thermal-initiated polymerization of the polymer matrix material or, more preferably, by photo-initiated polymerization of the polymer matrix material using low intensity UV radiation. Generally, the amount of photoinitiator is from about 0.01 part to about 10 parts per 100 parts of polymer matrix material by weight. Useful photoinitiators and/or photocatalysts are preferably of the free radical type. Examples of suitable free- radical photoinitiators include the benzoin ethers, substituted benzoin ethers such as benzoin methyl ether or benzoin isopropyl ether, substituted acetophenones such as 2,2-diethoxy-acetophenone, and 2,2-dimethoxy-2- phenyl-acetophenone, substituted alpha-ketols such as 2-methyl-2-hydroxypropiophenone, aromatic sulphonyl chlorides such as 2-naphthalene sulphonyl chloride, and photoactive oximes such as l-phenyl-l,l-propanedione-2- (O-ethoxycarbonyl) oxime. Other suitable free radical polymerization initiating systems which may be used to effect the polymerization include 2,4-bistrichloro- methyl-6-substituted-s-triazines, and benzophenone with an a ine, for example, benzophenone and p-(N,N- diethyla ino) ethyl benzoate. Low intensity UV lamps with different spectral responses are commercially available and may be used. The lamp should be selected such that the maximum output of the lamp is near the maximum absorption of the initiator. Fluorescent lamps (e.g., F40T12-350BL lamps commercially available from Osram Sylvania, Danvers, MA) in which the intensity of each lamp bank is in the range of about 0.25 to 10 mW/cm 2 (more preferably in the range of about 0.5 to 5 mW/cm 2 ) are suitable for this application. The total radiation to which the polymer matrix material is exposed preferably is in the range of about 100 to 1500 mJ/cm 2 as measured through the electrode substrate. The particular radiation intensity and total energy exposure requirements will vary depending on the liquid crystal, initiator, and polymer matrix materials. Preferably, the liquid crystal material and the polymer matrix material are provided in approximately equal parts by weight, although the parts by weight of the liquid crystal material can vary from 10-90% by weight, even more preferably from 25-75% by weight. The optimum liquid crystal content is within 5% by weight of the concentration in which a further 5% by weight increase in liquid crystal content would yield a film in which the color of transmitted white light would change from slightly red to white. Referring again to FIG. 1, although the optically responsive film 12 may be provided in free-standing form, in many applications it will be desirable to provide a sandwichlike construction in which the film 12 is interposed between a pair of first and second substrates 18 and 20, respectively. The thickness of the film preferably ranges from about 5 to 25 microns, more preferably in the range of about 10 to 25 microns, and most preferably in the range of about 15 to 21 microns. It will be understood that the device 10 may be provided with only a single substrate if, for example, the device is to be applied to a motor vehicle sunroof or an architectural window in which case the sunroof or the window have a function analogous to that of the second substrate. At least one of the substrates 18 and 20 is at least partially transparent to allow incident visible light to pass therethrough. One of the substrates (preferably the one which light first impinges) may be modified to have selective light transmission characteristics, for example, to selectively transmit light of a wavelength corresponding to a certain color of the visible spectrum, ultraviolet light, or infrared light. Materials suitable for the substrates 18 and 20 include glass (which may be tempered) and plastics such as polyethylene terephthalate, polyethylene naphthalate, or other polyester or copolyester materials, polyethersulfone, polyimide, poly(methyl methacrylate) , and polycarbonate. The substrates may be treated so as to enhance their abrasion and scratch resistance. The substrates are typically about 25 to 50 microns thick for flexible, durable constructions, although they may range in thickness from 1 microns to greater than 250 microns. If glass is employed for at least one of the substrates, the thickness may be in excess of 250 microns. With continued reference to FIG. 1, in order to induce a change in the orientation of the liquid crystal droplets so as to cause the optically responsive film 12 to switch between the translucent off-state and the transparent on-state, it is necessary to apply an electric field across the film 12 (the film 12 may also be switched by applying a magnetic field across the same or by raising the temperature of the film above the clearing point temperature of the encapsulated liquid crystal) . Accordingly, the device 10 may further comprise first and second electrodes 22 and 24, respectively, which are positioned intermediate the substrates 18 and 20 and the optically responsive film 12. The electrodes 22 and 24 are connected to, respectively, first and second leads 26 and 28 (e.g., using the connector described in PCT International application No. PCT/US93/12128, entitled "Electrical Connector" which, in turn, are electrically connected to a variable power supply 30, preferably of the alternating current type (e.g., a zero-cross power supply) . Preferably, the frequency of the alternating field should be in the range of 40 to 100 Hz. The field should alternate sufficiently rapidly so that a human observer of the device cannot perceive flickering. Thus, upon application of an electric field across the film 12, the optic axes of the liquid crystal droplets become aligned. If the refractive indices of the liquid crystal material and the polymer matrix have been closely matched, the film 12 will switch between the translucent off-state and the transparent on-state. The electrodes 22 and 24 may be formed of various materials including chromium, indium oxide, tin oxide, stainless steel, indium tin oxide, gold, silver, copper, aluminum, titanium, cadmium stannate, transition metal oxides, and mixtures and alloys thereof. With the use of oxidizable electrode materials (e.g., silver) it may be desirable to environmentally protect the same with a thin passivating dielectric layer. The use of such a protective layer may enhance the ability of the electrode to resist thermal, chemical, moisture and/or ultraviolet-induced degradation. The electrodes must be capable of receiving an electrical input from the leads 26 and 28 and transmitting the same so as to apply an electric field across the film 12. Preferably the electrodes 22 and 24 are positioned adjacent to opposite sides or surfaces of the film 12 and extend over, across and parallel to the same. At least one of the electrodes 22 and 24 preferably is at least partially transparent to visible light, although electrodes which provide preferential light transmission characteristics, such as color tint or ultraviolet or infrared filter, may be used. The electrodes 22 and 24 need not be equally transparent. At least one of the electrodes should provide a visible light transmission of at least 1%, preferably at least 10%, and more preferably at least 50%. The electrode coating should have a conductivity greater than 0.001 mhos per square. The electrode material may be coated or otherwise applied to the first and second substrates 18 and 20. Where only one of the substrates and one of the electrodes is transparent, the transparent substrate and transparent electrode should be on the same side of the device. In operation, a user of the device 10 applies an electric field across the film 12 using power supplied by power supply 30, thereby rendering the device transmissive to light. Whether the light modulating device is supplied as a free-standing film, with one substrate, or with two substrates, the device may be applied to a surface such as a motor vehicle sunroof, a motor vehicle side window, or an architectural window with, for example, suitable adhesive; preferably, the adhesive is optically transparent. As the device switches between the translucent off-state and the transparent on-state (in the case of nematic liquid crystal material having positive dielectric anisotropy) , the device preferably has a uniform, even appearance. The invention will be more fully understood with references to the following examples which are not to be construed as limiting the scope of the invention. EXAMPLES The following examples describe the preparation of light modulating devices based upon optically responsive PDLC films. In Examples 19-22 the device was prepared by first degassing an unpolymerized composition of matrix reactant(s) and liquid crystal and then pumping the composition to a coating die through which the composition was extruded onto the electrode side of an approximately 51 micron thick indium-tin oxide (ITO)-coated polyester film (90/10 indium/tin, 80 ohms/square, commercially available from Southwall Technologies, Palo Alto, CA) according to the process described in greater detail in Vesley et al., PCT International application No. (Attorney Docket No. 50778PCT5A) entitled "Precision Coating Process for Preparing Polymerizable Films" filed concurrently with, and assigned to the same assignee as the present application. The coating die 40 is shown in Figure 2. The unpolymerized composition 44 was supplied by a pump 46 to the die 40 for application in the form of a continuous coating bead to the moving iTO-coated polyester film 48, supported by a backup roll 50. The backup roll 50 was a pacer roll driven by a Torquer Tachometer precision motor (available from Inland Motor Division, Bradford, VA) . The temperatures of the die and backup roll were controlled by circulating a temperature controlled fluid through them. Where indicated in the examples, vacuum was applied to vacuum chamber 42 to stabilize the coating bead. The unpolymerized composition 44 was supplied through a channel 52 to a manifold 54 for distribution through a slot 56 and coating onto the moving film 48. The height of slot 56 was controlled by means of a U-shaped shim 41 (typically made of brass or stainless steel) . Referring to Figure 3, die 40 consisted of an upstream bar 64 and a downstream bar 66. The lip of the upstream bar was formed as a curved land 68 and the lip of the downstream bar was formed as a substantially straight sharp edge 70 having an edge radius no greater than 10 microns. The radius of the curved land 68 was equal to the radius of the backup roll 50 plus a minimal, and non-critical, 0.13 mm allowance for coating gap and film thickness. The length L, of the curved land 68 on the upstream bar 64 was 12.7 mm and the length 1^ of land 82 was 12.7 mm. The edge angle A ! of the downstream bar 66 was 50- 60°. The die attack angle A 2 between the downstream bar 66 surface of the coating slot 56 and the tangent plane P through a line on the film 48 surface parallel to, and directly opposite, the sharp edge 70 was 95°. The coating gap G, is the distance between the sharp edge 70 and the film 48. Slot height H is the distance between upstream bar 64 and downstream bar 66, and was controlled by controlling the thickness of shim 41. The slot height used in the examples was 0.152 mm. Overbite O is a positioning of the sharp edge 70 of the downstream bar 66, with respect to the downstream edge 72 of the curved land 68 on the upstream bar 64, in a direction toward the film 48. Convergence C is a counterclockwise, as shown in Figure 3, positioning of the curved land 68 away from a location parallel to the film 48, with the downstream edge 72 being the center of rotation. In the examples, convergence was 0.57°. Vacuum land gap G 2 was 152 microns. Figure 4 is cross-sectional view of the extrusion die used to prepare films according to the invention and shows an alternate configuration where the vacuum bar 74 is isolated from the bottom die bar 65 by a flexible metal seal 88. This configuration allows adjustment of the coating gap G, and convergence C without affecting the vacuum land gap G 2 . The width of the coating produced by a given die was reduced where indicated by "deckling" the die and the vacuum chamber by concurrently incorporating a) shaped plugs to reduce the widths of the die cavity manifold 54 and vacuum chamber 42 to the deckling width and b) a shim into the die that has a shim slot width corresponding to the deckling width. A second ITO-coated polyester film was unwound from a second unwind roll and passed around a 2.54 cm diameter sintered metal laminator bar where the second film was laminated to the coated face of the first film according to the procedure described in Vesley et al., PCT International application No. (Attorney Docket No. 50777PCT7A, entitled "Lamination Process for Coating" filed concurrently with, and assigned to, the same assignee as the present application. The laminator bar was located approximately 12 cm downstream from the backup roll such that the coated film was not in contact with the backup roll or other idler or takeup rolls at the point of lamination, and positioned so that the uncoated first substrate was depressed below the plane defined by the first film as it passed over the backup roll and the idler roll; the extent of depression is hereinafter referred to as "interference." Air pressure (approximately 2.4 bar) through the air bar laminator was adjusted to provide a cushion of air between the air bar laminator and the second film. The uncured laminate construction was cured by passing the construction through a cooled curing chamber constructed of ultraviolet transparent Acrylite™ OP-4 (available from Cyro Industries, Mt. Arlington, NJ) , extending approximately 61 cm (2 feet) into a cure chamber equipped with two banks of fluorescent black lights (F20T12-350BL, available from Osra Sylvania, Danvers, MA) , one bank positioned on each side of the laminate. Air temperature in the cooling chamber was monitored by a thermocouple mounted in the chamber under the second fluorescent bulb and controlled at the indicated temperature by introducing temperature controlled air. Each side of the laminate construction was exposed to approximately 250-600 mJ/cm 2 of radiation calculated from light intensities measured through a conductive electrode using a UVIBRITE radiometer (model number UBM365MO, available from Electronic Instrumentation and Technology, Inc. , Sterling, VA) equipped with a glass filter responsive between 300 and 400 nm, with a maximum transmission at 365 nm. The radiometer was specially calibrated to read in absolute intensity. In the case of Examples 1-18, the devices were prepared using a modified version of the procedure described in PCT International application No. PCT/US92/00173. A puddle of unpolymerized liquid crystal/matrix composition was placed on the moving surface of an ITO-coated polyester film measuring 51 microns thick just prior to the nip gap of the precision coater, where a second ITO-coated PET film entered to form a laminate in which the ITO-coated surfaces were in a facing relationship. The temperature of the nip rolls was maintained at 27°C by circulating a cooling solution from a constant temperature bath through the rolls. The nip gap was typically set between 0.11 - 0.14 mm to accommodate the thickness of the electrode materials and to allow for the desired PDLC matrix thickness. After exiting the nip rolls, the sandwichlike construction was cured by transporting it into a temperature-controlled cure chamber where it was irradiated with long wavelength UV light for approximately 3 minutes. The intensity of the UV light was measured by a EIT UVIBRITE radiometer model number UBM365MO as described above. The resulting light modulating devices prepared according to either of the two methods were characterized by measuring the electro-optical response (Test Procedure A) and haze (Test Procedure B) . Test Procedure A The electro-optical responses of the PDLC devices were characterized using a computer-controlled test stand consisting of an IBM personal computer interfaced with Kepco 125-1KVA-3T power supply, a Dyn-Optics Optical Monitor 590, and a Valhalla Scientific 2300 Series Digital Power Analyzer. The optics of the Dyn- Optics Optical Monitor were adjusted such that the specular transmission of photopically-filter light at an approximate 6° collection half angle was measured relative to an open beam. A sample of a PDLC film/electrode sandwich measuring several square centimeters was attached to the leads of the power supply using a connector such as that described in the aforementioned Engfer et al. application. A 60 Hz voltage ranging from zero to 120 volts AC (VAC) was applied to the sample in 5 VAC increments and the specular transmission recorded. Test Procedure B The haze of the powered (120 VAC, 60 Hz) PDLC devices was measured using a Pacific Scientific Gardner XL-835 Colorimeter according to the manufacturer's instructions. Example 1 A PDLC device was prepared using the "modified Miller procedure" described above from a fluid containing (a) 55 parts BL036 liquid crystal mixture (EM Industries, Hawthorne, NY) and (b) 45 parts of the following mixture; 2.2 wt.% Esacure KB-1 photoinitiator (Sartomer, West Chester, PA), 27.4 wt.% 9460 allyl aliphatic urethane (Monomer Polymer & Dajac, Trevose, PA), 26.9 wt.% isooctyl acrylate, 10.0 wt.% 2- phenoxyethyl acrylate (Sartomer, West Chester, PA), 9.0 wt.% trimethylolpropane tris(3-mercaptopropionate) (Aldrich, Milwaukee, WI) , and 24.5 wt.% 1,6-hexanediol diacrylate (Sartomer, West Chester, PA) . The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 23°C to produce a PDLC film approximately 15 microns thick. The PDLC device exhibited on- and off-state transmissions of 73.8% and 1.3% respectively and a haze of 5.6%. A PDLC device was prepared as described in Example 1 from a fluid containing (a) 40 parts BL036 liquid crystal mixture and (b) 60 parts of the following mixture; 2.5 wt.% Esacure KB-1 photoinitiator, 30.0 wt.% RCC-15C obtained without initiator and with 50% less thiol (W.R. Grace, Atlanta, GA) , 5.0 wt.% acrylic acid (Aldrich, Milwaukee, WI) , 17.5 wt.% isooctyl acrylate, 10.0 wt.% 2-phenoxyethyl acrylate, and 35.0 wt.% Uralac 3004-102 (DSM Resins, U.S., Inc., Elgin, IL) . The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 24°C to produce a PDLC film approximately 18 microns thick. The PDLC device exhibited on- and off-state transmissions of 74.2% and 1.1% respectively and a haze of 3.9%. Example 3 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 45 parts BL036 liquid crystal mixture and (b) 55 parts of the following mixture; 2.8 wt.% Esacure KB-1 photoinitiator, 8.5 wt.% RCC-15C prepared without initiator and with 50% less thiol, 34.1 wt.% isooctyl acrylate, 17.1 wt.% 2- phenoxyethyl acrylate, 20.4% diethyl fumarate (Aldrich, Milwaukee, WI) , and 17.1 wt.% divinyl ether of triethylene glycol (International Specialty Products, Wayne, NJ) . The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 23°C to produce a PDLC film approximately 20 microns thick. The PDLC device exhibited on- and off-state transmissions of 58.6% and 1.1% respectively. Example 4 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 55 parts BL036 liquid crystal mixture and (b) 45 parts of the following mixture; 2.5 wt.% Esacure KB-1 photoinitiator, 7.5 wt.% acrylic acid, 15.0 wt.% isooctyl acrylate, 5.0 wt.% 2- phenoxyethyl acrylate, 30.0 wt.% Uralac 3004-102, 29.9 wt.% Uralac 3004-300 (DSM Resins, U.S., Inc., Elgin, IL) , and 10.0 wt.% trimethylolpropane mono-ally1 ether (Monomer-Polymer & Dajac, Trevose, PA) . The laminate was prepared as described above and cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 23°C to produce a PDLC film approximately 18 microns thick. The PDLC device exhibited on- and off-state transmissions of 72.0% and 1.9% respectively and a haze of 8.2%. Example 5 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 45 parts BL036 liquid crystal mixture and (b) 55 parts of the following mixture; 2.5 wt.% Esacure KB-1 photoinitiator, 60.0 wt.% 9460 allyl aliphatic urethane, 10.0 wt.% isooctyl acrylate, 17.5 wt.% 2-phenoxyethyl acrylate, and 10.0 wt.% Uralac 3004-102. The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 26°C to produce a PDLC film approximately 21 microns thick. The PDLC device exhibited on- and off-state transmissions of 73.8% and 1.4% respectively. Example 6 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 50 parts BL036 liquid crystal mixture and (b) 50 parts of the following mixture; 2.5 wt.% Esacure KB-1 photoinitiator, 20.0 wt.% 9461 allylated bisphenol A glycidyl ether oligomer (Monomer-Polymer & Dajac, Trevose, PA), 35.0 wt.% isooctyl acrylate, 10.0 wt.% 2-phenoxyethyl acrylate, and 32.5 wt.% Uralac 3004-102. The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 24°C to produce a PDLC film approximately 28 microns thick. The PDLC device exhibited on- and off-state transmissions of 74.0% and 1.6% respectively. Example 7 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 45 parts BL036 liquid crystal mixture and (b) 55 parts of the following mixture; 2.5 wt.% Esacure KB-1 photoinitiator, 30.0 wt.% 9461 allylated bisphenol A glycidyl ether oligomer, 25.9 wt.% isooctyl acrylate, 6.7 wt.% 2- phenoxyethyl acrylate, and 35.0 wt.% Uralac 3004-102. The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 26°C for 5 minutes to produce a PDLC film approximately 30 microns thick. The PDLC device exhibited on- and off-state transmissions of 67.6% and 5.4% respectively. Example 8 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 50 parts BL036 liquid crystal mixture and (b) 50 parts of the following mixture; 2.5 wt.% Esacure KB-1 photoinitiator, 20.1 wt.% of the oligomer contained in RCC-15C (W.R. Grace, Atlanta, GA) , 7.5 wt.% acrylic acid, 35.0 wt.% isooctyl acrylate, 20.0 wt.% 2-phenoxyethyl acrylate, and 15.0 wt.% poly(methylvinylsiloxane) (Hϋls America, Piscataway, NJ) . The laminate was prepared as described above and cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 24°C to produce a PDLC film approximately 18 microns thick. The PDLC device exhibited on- and off-state transmissions of 73.8% and 1.4% respectively. Example 9 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 45 parts BL036 liquid crystal mixture and (b) 55 parts of the following mixture; 2.5 wt.% Esacure KB-1 photoinitiator, 40.0 wt.% of the oligomer contained in RCC-15C, 23.1 wt.% isooctyl acrylate, 4.4 wt.% 2-phenoxyethyl acrylate, and 30.0 wt.% Uralac 3004-102. The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 24°C to produce a PDLC film approximately 23 microns thick. The PDLC device exhibited on- and off-state transmissions of 75.3% and 2.0% respectively. Example 10 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 55 parts BL036 liquid crystal mixture and (b) 45 parts of the following mixture; 2.5 wt.% Esacure KB-1 photoinitiator, 50.0 wt.% triallyl-1,3,5-triazine-2,4,6-(1H,3H,5H)-trione (Aldrich, Milwaukee, WI) , and 47.5 wt.% isooctyl acrylate. The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 24°C to produce a PDLC film approximately 18 microns thick. The PDLC device exhibited on- and off-state transmissions of 75.5% and 1.5% respectively. Example 11 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 59.8 parts BL036 liquid crystal mixture and (b) 40 parts of the following mixture; 2.4 wt.% Esacure KB-1 photoinitiator, 9.5 wt.% triallyl-1,3,5-triazine-2,4,6-(1H,3H,5H)-trione, 5.1 wt.% mono-2-ethylhexyl itaconic acid (Monomer-Polymer & Dajac, Trevose, PA), 49.9 wt.% isooctyl acrylate, 19.0 wt.% 2-phenoxyethyl acrylate, and 14.3 wt.% Uralac 3004-102. The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 24°C to produce a PDLC film approximately 20 microns thick. The PDLC device exhibited on- and off-state transmissions of 75.5% and 7.3% respectively. Example 12 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 60.1 parts BL036 liquid crystal mixture and (b) 40.1 parts of the following mixture; 2.4 wt.% Esacure KB-1 photoinitiator, 9.5 wt.% triallyl-1,3,5-triazine-2,4,6-(1H,3H,5H)-trione, 5.1 wt.% mono-2-ethylhexyl maleic acid (Monomer-Polymer & Dajac, Trevose, PA), 49.8 wt.% isooctyl acrylate, 19.0 wt.% 2-phenoxyethyl acrylate, and 14.2 wt.% Uralac 3004-102. The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 24°C to produce a PDLC film approximately 19 microns thick. The PDLC device exhibited on- and off-state transmissions of 75.1% and 1.0% respectively. Example 13 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 60 parts BL036 liquid crystal mixture and (b) 39.9 parts of the following mixture; 2.4 wt.% Esacure KB-1 photoinitiator, 9.5 wt.% triallyl-1,3,5-triazine-2,4,6-(1H,3H,5H)-trione, 5.1 wt.% 2-hexenoic acid (Aldrich, Milwaukee, WI) , 49.8 wt.% isooctyl acrylate, 19.0 wt.% 2-phenoxyethyl acrylate, and 14.3 wt.% Uralac 3004-102. The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 24°C to produce a PDLC film approximately 20 microns thick. The PDLC device exhibited on- and off-state transmissions of 72.6% and 4.1% respectively. Example 14 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 70 parts BL036 liquid crystal mixture and (b) 30 parts of the following mixture; 2.5 wt.% Esacure KB-1 photoinitiator, 10.0 wt.% triallyl-1,3,5-triazine-2,4,6-(1H,3H,5H)-trione, 57.5 wt.% isooctyl acrylate, 10.0 wt.% ethylene glycol dimethacrylate (Aldrich), and 20.0 wt.% 2-phenoxyethyl acrylate. The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 24°C for 5 minutes to produce a PDLC film approximately 19 microns thick. The PDLC device exhibited on- and off-state transmissions of 76.3% and 2.2% respectively. Example 15 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 50 parts BL036 liquid crystal mixture and (b) 50 parts of the following mixture; 2.0 wt.% Esacure KB-1 photoinitiator, 80.4 wt.% RCC-15C prepared without initiator, 2.0 wt.% methacrylic acid (Aldrich, Milwaukee, WI) , and 15.7 wt.% isooctyl acrylate. The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 23°C to produce a PDLC film. The PDLC device exhibited on- and off-state transmissions of 70.5% and 1.1% respectively. Example 16 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 45 parts BL036 liquid crystal mixture and (b) 55 parts of the following mixture; 2.0 wt.% Esacure KB-1 photoinitiator, 80.4 wt.% RCC-15C prepared without initiator, and 17.6 wt.% lauryl methacrylate (Rohm Tech, Inc., Maiden, MA). The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 23°C to produce a PDLC film approximately 24 microns thick. The PDLC device exhibited on- and off-state transmissions of 74.2% and 1.2% respectively and a haze of 6.4%. Example 17 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 40 parts BL036 liquid crystal mixture and (b) 60 parts of the following mixture; 2.0 wt.% Esacure KB-1 photoinitiator, 80.4 wt.% RCC-15C obtained without initiator, and 17.6 wt.% isooctyl methacrylate. The laminate was cured by exposure to UV light (intensity approximately 2.0 mW/cm 2 ) at about 23°C to produce a PDLC film approximately 24 microns thick. The PDLC device exhibited on- and off-state transmissions of 73.6% and 1.3% respectively and a haze of 6.0%. Example 18 A PDLC device was prepared as described in Example 1 from a fluid containing (a) 42.5 parts BL036 liquid crystal mixture and (b) 57.5 parts of the following mixture; 2.0 wt.% Esacure KB-1 photoinitiator, 80.4 wt.% RCC-15C prepared without initiator, 3.9 wt.% methacrylic acid, and 13.7 wt.% lauryl methacrylate. The laminate was cured by exposure to UV light (intensity approximately 1.7 mW/cm 2 ) at about 23°C for 7 minutes to produce a PDLC film approximately 22 microns thick. The PDLC device exhibited on- and off-state transmissions of 73.1% and 1.2% respectively. Example 19 A PDLC device was prepared as described in the precision coating method above from a fluid containing (a) 55 parts of a mixture consisting of 30.0 wt.% RCC- 15C curable matrix mixture obtained without initiator and with 50% less thiol, 7.5 wt.% acrylic acid, 30.0 wt.% isooctyl acrylate, 15.0 wt.% 2-phenoxyethyl acrylate, 15.0 wt.% divinyl ether of triethylene glycol, and 2.5 wt.% KB-1 photoinitiator, and (b) 45 parts BL036 liquid crystal mixture having a solution viscosity of 42 cps (measured on a Brookfield viscometer using a #3 spindle operating at 60 rpm) . The fluid, which was degassed under vacuum for approximately 2 minutes at ambient temperature, was applied as a 15.2 cm (6 inch) wide strip to the electrode surface of an ITO-coated polyester film (90/10 indium/tin ratio, 80 ohms/square, 51 microns (2 mil) thick PET, available from Southwall Technologies, Palo Alto, CA) at a rate of approximately 152.4 cm/min (5 ft/minute) using an 88.9 cm die similar to that illustrated in Figure 4 which was deckled to produce a narrower coating and configured with a 152 micron shim, a coating land having a length (L,) of 12.7 mm, a vacuum land having a length Lj of 12.7 mm, a 0.57° convergence, a 33 micron overbite, a vacuum land gap G 2 of 0.152 mm, a die attack angle A 2 of 95°, and a coating gap of 102 microns. The convergence of the vacuum bar was 0° and no vacuum was applied to the vacuum chamber during coating. Both the die and back-up roll were temperature controlled at 21°C. A pressure of 1.7 bar was maintained to the sintered metal bar during lamination and the lamination bar was adjusted to provide an interference of 3.6 mm. The resulting laminate was cured by exposure to UV light (intensity approximately 1.1 mW/cm 2 ) at about 21°C to produce a PDLC film approximately 24±1 microns thick. The PDLC device had on- and off-state transmissions of 73.1% and 1.2%, respectively, and a haze of 5.8%. Example 20 A PDLC device was prepared as described in Example 19 except that the fluid contained (a) 220 parts of BL036 liquid crystal mixture and (b) 180 parts of the following mixture; 2.5 wt.% Esacure KB-1 photoinitiator, 30.0 wt.% 9460 allyl aliphatic urethane, 7.5 wt.% acrylic acid, 25.0 wt.% isooctyl acrylate, 20.0 wt.% 2-phenoxyethyl acrylate, and 15.0 wt.% Uralac 3004-102. The die was configured with an overbite of 51 microns and a coating gap set at 76 microns. A vacuum of 0.9 mm Hg was applied to the vacuum chamber during coating. An air pressure of 1.7 bar was maintained to the laminator bar which was adjusted to provide an interference of 3.8 mm. The resulting laminate was cured by exposure to UV light (intensity approximately 1.9 mW/cm 2 ) at about 22°C to produce a PDLC film approximately 13-14 microns thick. The PDLC device had on- and off-state transmissions of 73.8% and 1.2%, respectively, and a haze of 4.8%. Example 21 A PDLC device was prepared as described in Example 19 except that the fluid contained (a) 333 parts of BL036 liquid crystal mixture and (b) 267 parts of the following mixture; 2.5 wt.% Esacure KB-1 photoinitiator, 20.0 wt.% 9460 allyl aliphatic urethane, 5.0 wt.% acrylic acid, 30.0 wt.% isooctyl acrylate, 20.0 wt.% 2-phenoxyethyl acrylate, and 22.5 wt.% Uralac 3004-102. The die was configured to coat an 88.9 cm wide strip, with an overbite of 41 microns. A vacuum of 1.9 mm Hg was applied to the vacuum chamber during coating. An air pressure of 3.4 bar was maintained to the laminator bar which was adjusted to provide an interference of 3.8 mm. The resulting laminate was cured by exposure to UV light (intensity approximately 1.8 mW/cm 2 ) at about 21°C to produce a PDLC film approximately 15 microns thick. The PDLC device had on- and off-state transmissions of 74.8% and 1.2%, respectively, and a haze of 4.7%. Example 22 A PDLC device was prepared as described in Example 19 using a fluid containing (a) 45 parts of a mixture consisting of 20.0 wt.% of the oligomer contained in RCC-15C, 2.5 wt.% acrylic acid, 40.0 wt.% isooctyl acrylate, 25.0 wt.% 2-phenoxyethyl acrylate, 10.0 wt.% Uralac 3004-102, and 2.5 wt.% KB-1 photoinitiator, and (b) 55 parts BL036 liquid crystal mixture having a solution viscosity of 42 cps (measured on a Brookfield viscometer using a #3 spindle operating at 60 rpm) . The fluid was applied to the electrode substrate at a rate of approximately 4.6 m/min using a die configured with a 3.8 micron overbite. A vacuum of 3.7 mm Hg was applied to the vacuum chamber during coating. Both the die and back-up roll were temperature controlled at 20°C. A pressure of 3.4 bar was maintained to the sintered metal bar during lamination and the lamination bar was adjusted to provide an interference of 3.8 mm. The laminate was cured at 21°C by exposure to 244 mJ/cm 2 UV light at an average intensity of approximately 2.0 mW/cm 2 to produce a PDLC film approximately 19 microns thick. The PDLC device had on- and off-state transmissions of 74.3% and 1.0%, respectively, and a haze of 4.0%. Other embodiments are within the following claims.

Claims: WHAT IS CLAIMED IS: 1. An optically responsive film comprising liquid crystal dispersed in a polymer matrix comprising the reaction product of: (a) 5-60% by weight of one or more allyl reactants; (b) 15-95% by weight of one or more ene reactants other than an allyl; and (c) 0-20% by weight of one or more thiol reactants. 2. The optically responsive film of claim 1 wherein said film comprises the reaction product of: (a) 20-30% by weight of one or more allyl reactants; (b) 55-80% by weight of one or more ene reactants other than an allyl; and (c) 0-10% by weight of one or more thiol reactants. 3. The optically responsive film of claim 1 wherein said ene comprises a mono- or multi-functional vinyl ether, acrylate, methacrylate, acrylamide, methacrylamide, vinyl silane, or combination thereof. 4. A light modulating device comprising an optically responsive film according to claim 2 to which an electric field is applied through a pair of electrodes. 5. An optically responsive film comprising liquid crystal dispersed in a polymer matrix comprising the reaction product of: (a) 5-50% by weight of one or more allyl reactants; and (b) 2-25% by weight of one or more methacrylate reactants; and (c) optionally, one or more thiol reactants. 6. A light modulating device comprising an optically responsive film according to claim 5 to which an electric field is applied through a pair of electrodes. 7. An optically responsive film comprising liquid crystal dispersed in a polymer matrix comprising the reaction product of: (a) two or more ene reactants in which 5-70% of all ene groups are allyl groups, and (b) one or more thiol reactants, the ratio of thiol groups to all ene groups being no greater than 0.2. 8. A light modulating device comprising an optically responsive film according to claim 7 to which an electric field is applied through a pair of electrodes. 9. An optically responsive film comprising liquid crystal dispersed in a polymer matrix comprising the reaction product of two or more ene reactants in which 10-90% of all ene groups are allyl groups and 5- 30% of all ene groups are methacrylate groups. 10. A light modulating device comprising an optically responsive film according to claim 9 to which an electric field is applied through a pair of electrodes.

Inventors: NERAD BRUCE A, VESLEY GEORGE F, NERAD, BRUCE, A., VESLEY, GEORGE, F.
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1995
Main classification: C09K19
IPC codes: C08F290, C08J5, C08L29, C08L33, C08L101, C09K19, G02F1