Fluorine-containing elastomer composition

Abstract: A fluorine-containing elastomer composition, which comprises a terpolymer of tetrafluoroethylene, perfluoro(lower alkyl vinyl ether) or perfluoro(lower alkoxy-lower alkyl vinyl ether) and cross-linkable cyano group-containing (perfluorovinylether), and a bis(aminothiophenol) compound represented by the following general formula as a cross-linking agent: wherein A is an alkylidene group having 1 to 6 carbon atoms, a perfluoroalkylidene group having 1 to 10 carbon atoms, a SO₂ group, an O atom, a CO group or a carbon-carbon bond capable of directly bonding two benzene rings and one of X and Y is an amino group, while the other is a mercapto group, can produce cross-linked fluororubber moldings having an improved compression set.

Description: BACKGROUND OF THE INVENTION 1. FIELD OF THE INVENTION The present invention relates to a fluorine-containing elastomer composition, and more particularly to a cross-linkable composition of fluorine-containing elastomer having cyano groups as cross-linkable groups. 2. RELATED PRIOR ART JP-A-59-109546 discloses a fluorine-containing elastomer composition which comprises a terpolymer of tetrafluoroethylene, perfluoro(methyl vinyl ether) and cyano group-containing (perfluorovinylether) represented by the following general formula: CF 2 =CF[OCF 2 CF(CF 3 )]nO(CF 2 )mCN wherein n: 1∼2 and m: 1∼4 and a bis(aminophenyl) compound represented by the following general formula as a cross-linking agent: wherein A is an alkylidene group having 1 to 6 carbon atoms, a perfluoroalkylidene group having 1 to 10 carbon atoms, a SO 2 group, an O atom, a CO group or a carbon-carbon bond directly bonding the benzene rings, and X and Y are hydroxyl groups or amino groups. However, such use of bis-(diaminophenyl) compound or bis(aminophenol) compound still has a room for improvement in the compression set. SUMMARY OF THE INVENTION An object of the present invention is to provide a fluorine-containing elastomer composition capable of producing cross-linked fluororubber moldings having an improved compression set, which contains a bis(aminophenyl) compound as a cross-linking agent for a fluorine-containing elastomer having cyano groups as cross-linkable groups. According to the present invention, there is provided a fluorine-containing elastomer composition, which comprises a terpolymer of tetrafluoroethylene, perfluoro(C1-C5-alkyl vinyl ether) and cross-linkable cyano group-containing (perfluorovinyl ether) and a bis(aminothiophenol) compound represented by the following general formula as a cross-linking agent: wherein A is an alkylidene group having 1 to 6 carbon atoms, a perfluoroalkylidene group having 1 to 10 carbon atoms, a SO 2 group, an O atom, a CO group or a carbon-carbon bond directly bonding the benzene rings and one of X and Y is an amino group, while the other is a mercapto group. DETAILED DESCRIPTION OF THE INVENTION The terpolymer of tetrafluoroethylene, perfluoro(lower alkyl vinyl ether) and cyano group-containing (perfluorovinylether) for use in the present invention is a copolymer comprising 30 to 70% by mole of tetrafluoroethylene, 65 to 25% by mole of perfluoro(C1-C5-alkyl vinyl ether) and 0.1 to 5% by mole of cyano group-containing (perfluorovinylether) as a cross-linking site comonomer, the sum total of comonomers being 100% by mole. As the perfluoro(C1-C5-alkyl vinyl ether), perfluoro(methyl vinyl ether) is usually used. As the cyano group-containing (perfluorovinylether) capable of providing cross-linkable groups in the terpolymer, the following compounds are used: CF 2 =CFO(CF 2 ) n CN (n: 2∼12) [see: USP 3,546,186 and USP 3,114,778] CF 2 =CFO[CF 2 CF(CF 3 )O) n CF 2 CF(CF 3 )CN (n: 0∼4) [see: USP 3,852,326 and USP 3,933,767] CF 2 =CFO[CF 2 CF(CF 3 )O] m (CF 2 ) n CN (n: 1∼4 and m: 1∼2) [see: USP 4,138,426 and USP 4,281,092] The terpolymer can be further copolymerized with various fluoroolefins or vinyl compounds in such a degree as not to inhibit the copolymerization reaction and deteriorate physical properties of vulcanized products, for example, not more than 20% by mole on the basis of the terpolymer. Fluoroolefins for use in the present invention include, for example, vinylidene fluoride, monofluoroethylene, trifluoroethylene, trifluoropropylene, pentafluoropropylene, hexafluoropropylene, hexafluoroisobutylene, chlorotrifluoroethylene and dichlorodifluoroethylene. Vinyl compounds for use in the present invention include, for example, ethylene, propylene, 1-butene, isobutylene, methyl vinyl ether, ethyl vinyl ether, butyl vinyl ether, cyclohexyl vinyl ether, vinyl acetate, vinyl propionate, vinyl chloride, vinylidene chloride and trifluorostyrene. 0. 5 to 5 parts by weight, preferably about 1 to about 2 parts by weight, of bis(aminothiophenol) compound represented by the foregoing general formula is added to 100 parts by weight of the terpolymer. The fluorine-containing elastomer composition comprising the above-mentioned components as essential ones can further contain an inorganic filler such as carbon black and silica, an acid acceptor such as oxide, hydroxide or stearate of a divalent metal and litharge, a vulcanization aid such as crown ether, quaternary ammonium salt and quaternary phosphonium salt, and other additives, as desired. The composition can be prepared by kneading in rolls, kneader, Bambury mixer. Cross-linking of the composition is carried out by heating at about 160 to about 250°C for about 10 to about 60 minutes. Secondary vulcanization, when desired, is preferably carried out at about 150 to about 280°C for not more than about 30 hours in an inert atmosphere such as a nitrogen atmosphere. By using a bis(aminothiophenol) compound as a cross-linking agent for a fluorine-containing elastomer having cyano groups as cross-linkable groups, a fluorine-containing elastomer composition capable of producing cross-linked moldings having a largely improved compression set. PREFERRED EMBODIMENTS OF THE INVENTION The present invention will be described in detail below, referring to Examples. REFERENCE EXAMPLE 1 200ml of distilled water, 2.5g of ammonium perfluorooctanoate and 4.4g of Na 2 HPO 4 ·12H 2 O were charged into a stainless steel autoclave having a net capacity of 500ml, and then the inside gas was replaced with a nitrogen gas. Then the autoclave was subjected to pressure reduction and cooled to about -50°C. Then the following compounds were successively charged into the autoclave: Perfluoro(5-cyanopentyl vinyl ether) [FCVE] 6.4g Perfluoro(methyl vinyl ether) [FMVE] 68g Tetrafluoroethylene [TFE] 32g After heating the autoclave to 80°C, 25ml each of aqueous solutions cantaining 0.75g of sodium sulfite and 3.75g of ammonium persulfate, respectively, were charged into the autoclave to initiate polymerization reaction. After the polymerization reaction was continued for 20 hours, unreacted gases were purged from the autoclave and the resulting aqueous latex was taken out of the autoclave, salted out with an aqueous 10% sodium chloride solution and dried, whereby 44g of white rubbery terpolymer A was obtained. It was found by ultrared absorption analysis that the terpolymer A had a copolymer composition of 62.0% by mole of TFE, 37.0% by mole of FMVE and 1.0% by mole of FCVE (characteristic absorption of nitrile groups: 2268cm -1 ). REFERENCE EXAMPLE 2 Polymerization reaction was carried out in the same manner as in Reference Example 1 except that 9.1g of perfluoro(8-cyano-3,7-dioxanonene-1) [CNVE] was used in place of FCVE, whereby 35g of white rubbery terpolymer B was obtained. The terpolymer B had a copolymer composition of 61.0% by mole of TFE, 38.2% by mole of FMVE and 0.8% by mole of CNVE. EXAMPLES 1 TO 2 AND COMPARATIVE EXAMPLES 1 TO 2 The following components were kneaded in a double roll rubber mill and then subjected to primary vulcanization at 160 °C for 30 minutes and secondary vulcanization at 230°C for 22 hours in a nitrogen gas atmosphere: EXAMPLES 3 TO 4 AND COMPARATIVE EXAMPLES 3 TO 4 Operations were carried out in the same manner as in Examples 1 to 2 and Comparative Examples 1 to 2, except that the terpolymer B was used in place of the terpolymer A. Normal state physical properties of the vulcanized products obtained in Examples 1 to 4 and Comparative Examples 1 to 4 were measured according to JIS K-6301 and compression sets of O-rings thereof were determined. Results are shown in the following Table.

Claims: A fluorine-containing elastomer composition, which comprises a terpolymer of tetrafluoroethylene, perfluoro(C1-C5-alkyl vinyl ether) and cross-linkable cyano group-containing (perfluorovinylether), and a bis (aminothiophenol) compound represented by the following general formula as a cross-linking agent: wherein A is an alkylidene group having 1 to 6 carbon atoms, a perfluoroalkylidene group having 1 to 10 carbon atoms, a SO 2 group, an O atom, a CO group or a carbon-carbon bond directly bonding the benzene rings and one of X and Y is an amino group, while the other is a mercapto group. A fluorine-containing elastomer composition according to Claim 1, wherein the terpolymer is a copolymer comprising 30 to 70% by mole of tetrafluoroethylene, 65 to 25% by mole of perfluoro (C1-C5-alkyl vinyl ether) and 0.1 to 5% by mole of cyano group-containing (perfluorovinylether), the sum total of comonomers being 100% by mole. A fluorine-containing elastomer composition according to Claim 1, wherein the terpolymer contains not more than 20% by mole of other fluoroolefin or other vinyl compound on the basis of the terpolymer. A fluorine-containing elastomer composition according to Claim 1, wherein the bis(aminothiophenol) compound is: , or A fluorine-containing elastomer composition according to Claims 1, wherein 0.5 to 5 parts by weight of the bis(aminothiophenol) compound is used per 100 parts by weight of the terpolymer.

Inventors: ROMANOVICH POLISHCHUK VALERII, SAITO SATORU, SOLOMONOVICH GERMAN, TATSU HARUYOSHI, ROMANOVICH, POLISHCHUK VALERII, SAITO, SATORU, SOLOMONOVICH, GERMAN LEV, TATSU, HARUYOSHI
Applicants: NIPPON MEKTRON KK, NIPPON MEKTRON, LIMITED
Application year: 1995
Main classification: C08K5
IPC codes: C08F14, C08K5, C08F216, C08F214, C08L27, C08F16