Process for producing styrenic polymer

Abstract: There is disclosed a process for producing a styrenic polymer, especially, syndiotactic polystyrene, which comprises polymerizing a styrenic monomer by the use of a (a) transition metal compound, a (b) coordination complex compound comprising an anion in which a plurality of racicals are bonded to a metal and a cation or a Lewis acid, a (c) alkylating agent (alkyl group-containing aluminum, magnesium or zinc compound) and a (d) reaction product between a straight-chain alkylaluminum having at least two carbon atoms and water (alkylaluminoxane). The above process is capable of simplifying the production process and producing high-performance styrenic polymer having a high degree of syndiotactic configuration in high catalytic activity without deteriorating the catalyst activity, increasing the amounts of residual metals in the objective polymer or leaving the decomposition products of the alkylaluminum therein, thereby curtailing the production cost of the objective polymer.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a process for producing a styrenic polymer having a high degree of syndiotactic configuration efficiently and inexpensively. 2. Description of the Related Arts In recent years, there has been proposed a process for producing a styrenic polymer having a syndiotactic configuration (hereinafter sometimes referred to as "SPS") by polymerizing a styrenic monomer by means of a catalyst comprising a transition metal compound as a primary ingredient, especially a titanium compound and methylaluminoxane (refer to Japanese Patent Application Laid-Open No. 187708/1987). There has also been proposed a process for efficiently producing such a styrenic polymer (SPS) by the use of a catalyst comprising a coordination complex compound composed of an anion in which a plurality of radicals are bonded to a metal and a cation, while dispensing with an aluminoxane which is expensive and is to be used in a large amount (refer to Japanese Patent Application Laid-Open Nos. 415573/1990, 415574/1990, etc.) In the case of polymerizing a styrenic monomer by the use of the above-mentioned catalyst, there has heretofore been employed an alkylaluminum as a chain transfer agent for the purpose of modifying the molecular weight of the objective polymer. However, this method involves the problems that the catalytic activity deteriorates resulting in an increase in the amounts of residual metals contained in the styrenic polymer thus produced, allowing the decomposed product of an alkylaluminum to remain in the objective polymer. Even in the case of raising the polymerization temperature, the deterioration of the catalytic activity increases the amount of residual metals in the objective polymer. The aforesaid situation calls for the development of a process capable of producing a styrenic polymer of high performance at a low cost, while enabling an decrease in the molecular weight of the resultant polymer and simplifying the process itself without deteriorating the catalytic activity. As a result of intensive research and investigation made by the present inventors under such circumstances, it has been found that in the case of polymerizing a styrenic monomer by the use of a certain transition metal compound, a coordination complex compound composed of an anion in which a plurality of radicals are bonded to a metal and a cation or a Lewis acid and an alkylating agent as principal components, the use of a reaction product between a straight-chain alkylaluminum having at least two carbon atoms and water can lower the molecular weight of the resultant polymer without deteriorating the catalytic activity. The present invention has been accomplished on the basis of the above-mentioned finding and information. SUMMARY OF THE INVENTION Specifically, the present invention provides a process for producing a styrenic polymer having a high degree of syndiotactic configuration as defined in claims 1 or 2, preferred embodiments of which are defined in claims 3 to 5. DESCRIPTION OF PREFERRED EMBODIMENT In the (a) transition metal compound to be used in the process of the present invention, M is a metal belonging to any of the groups 3 to 6 of the Periodic Table or a lanthanum series metal. As a metal belonging to any of the groups 3 to 6 of the Periodic Table or a lanthanum series metal as indicated by M, there are preferably employed the group 4 metals, especially titanium, zirconium and hafnium. As the transition metal compound of the component (a) to be used in the present invention, there is available at least one compound selected from the group consisting of the transition metal compounds having the constitution represented by the general formula (VIII) R'MX' p-1 L 1 q wherein R' is, as a π ligand, a fused polycyclic cyclopentadienyl group wherein at least one of many-membered rings to which cyclopentadienyl groups are fusedly bonded is a saturated ring, M is as previously defined, X' is a σ ligand, a plurality of X' may be the same or different and bonded to each other through an arbitrary group, L 1 is a Lewis base, p is the valency of M, q is 0, 1 or 2 and when L 1 is plural, each L 1 may be the same or different. The above-mentioned fused polycyclic cyclopentadienyl group is exemplified by that selected from those represented by any one of the general formulae (IX) to (XI) wherein R 15 , R 16 and R 17 are each a hydrogen atom, a halogen atom, an aliphatic hydrocarbon group having 1 to 20 carbon atoms, an aromatic hydrocarbon group having 6 to 20 carbon atoms, an alkoxyl group having 1 to 20 carbon atoms, an aryloxyl group having 6 to 20 carbon atoms, a thioalkoxyl group having 1 to 20 carbon atoms, a thioaryloxyl group having 6 to 20 carbon atoms, an amino group, an amide group, a carboxyl group or an alkylsilyl group and may be the same as or different from each other; and w, x, y and z are each an integer of 1 or greater. Of these, 4,5,6,7-tetrahydroindenyl group is preferable from the viewpoint of catalytic activity and the ease of its synthesis. Specific examples of R' include 4,5,6,7-tetrahydroindenyl group; 1-methyl-4,5,6,7-tetrahydroindenyl group; 2-methyl-4,5,6,7-tetrahydroindenyl group; 1,2-dimethyl-4,5,6,7-tetrahydroindenyl group; 1,3-dimethyl-4,5,6,7-tetrahydroindenyl group; 1,2,3-trimethyl-4,5,6,7-tetrahydroindenyl group; 1,2,3,4,5,6,7-heptamethyl-4,5,6,7-tetrahydroindenyl group; 1,2,4,5,6,7-hexamethyl-4,5,6,7-tetrahydroindenyl group; 1,3,4,5,6,7-hexamethyl-4,5,6,7-tetrahydroindenyl group; octahydrofluorenyl group; 1,2,3,4tetrahydrofluorenyl group; 9-methyl-1,2,3,4-tetrahydrofluorenyl group; and 9-methyl-octahydrofluorenyl group. M is a Group 3 to 6 metal or a lanthanoids metal and exemplified by titanium, zirconium, hafnium, lanthanoids, niobium and tantalum. Of these titanium is preferable from the viewpoint of catalytic activity. X' is a σ ligand and is exemplified by a hydrogen atom, a halogen atom, an aliphatic hydrocarbon group having 1 to 20 carbon atoms, an aromatic hydrocarbon group having 6 to 20 carbon atoms, an alkoxyl group having 1 to 20 carbon atoms, an aryloxyl group having 6 to 20 carbon atoms, a thioalkoxyl group having 1 to 20 carbon atoms, a thioaryloxyl group having 6 to 20 carbon atoms, an amino group, an amide group, a carboxyl group or an alkylsilyl group, and a plurality of X' may be the same or different and bonded to each other through an arbitrary group. Further, X' is specifically exemplified by hydrogen atom, chlorine atom, bromine atom, iodine atom, methyl group, benzyl group, phenyl group, trimethylsilylmethyl group, methoxy group, ethoxy group, phenoxy group, thiomethoxy group, thiophenoxy group, dimethylamino group and diisopropylamino group. L 1 is a Lewis base, p is the valency of M and q is 0, 1 or 2. As the transition metal compound represented by the general formula (VIII), there can preferably be employed a compound comprising R' and X' each arbitrarily selected from the above-exemplified groups. The transition metal compound represented by the general formula (VIII) is specifically exemplified by 4,5,6,7-tetrahydroindenyltitanium trichloride; 4,5,6,7-tetrahydroindenyltrimethyltitanium; 4,5,6,7-tetrahydroindenyltribenzyltitanium; 4,5,6,7-tetrahydroindenyltitanium trimethoxide; 1-methyl-4,5,6,7-tetrahydroindenyltitanium trichloride; 1-methyl-4,5,6,7-tetrahydroindenyltrimethyltitanium; 1-methyl-4,5,6,7-tetrahydroindenyltribenzyltitanium; 1-methyl-4,5,6,7-tetrahydroindenyltitanium trimethoxide; 2-methyl-4,5,6,7-tetrahydroindenyltitanium trichloride; 2-methyl-4,5,6,7-tetrahydroindenyltrimethyltitanium; 2-methyl-4,5,6,7-tetrahydroindenyltribenzyltitanium; 2-methyl-4,5,6,7-tetrahydroindenyltitanium trimethoxide; 1,2-dimethyl-4,5,6,7-tetrahydroindenyltitanium trichloride; 1,2-dimethyl-4,5,6,7-tetrahydroindenyltrimethyltitanium; 1,2-dimethyl-4,5,6,7-tetrahydroindenyltribenzyltitanium; 1,2-dimethyl-4,5,6,7-tetrahydroindenyltitanium trimethoxide; 1,3-dimethyl-4,5,6,7-tetrahydroindenyltitanium trichloride; 1,3-dimethyl-4,5,6,7-tetrahydroindenyltrimethyltitanium; 1,3-dimethyl-4,5,6,7-tetrahydroindenyltribenzyltitanium; 1,3-dimethyl-4,5,6,7-tetrahydroindenyltitanium trimethoxide; 1,2,3-trimethyl-4,5,6,7-tetrahydroindenyltitanium trichloride; 1,2,3-trimethyl-4,5,6,7-tetrahydroindenyltrimethyltitanium; 1,2,3-trimethyl-4,5,6,7-tetrahydroindenyltribenzyltitanium; 1,2,3-trimethyl-4,5,6,7-tetrahydroindenyltitanium trimethoxide; 1,2,3,4,5,6,7-heptamethyl-4,5,6,7-tetrahydroindenyititanium trichlorde; 1,2,3,4,5,6,7-heptamethyl-4,5,6,7-tetrahydroindenyltrimethyltitanium; 1,2,3,4,5,6,7-heptamethyl-4,5,6,7-tetrahydroindenyltribenzyltitanium; 1,2,3,4,5,6,7-heptamethyl-4,5,6,7-tetrahydroindenyltitanium trimethoxide; 1,2,4,5,6,7-hexamethyl-4,5,6,7-tetrahydroindenyltitanium trichloride; 1,2,4,5,6,7-hexamethyl-4,5,6,7-tetrahydroindenyltrimethyltitanium; 1,2,4,5,6,7-hexamethyl-4,5,6,7-tetrahydroindenyltribenzyltitanium; 1,2,4,5,6,7-hexamethyl-4,5,6,7-tetrahydroindenyltitanium trimethoxide; 1,3,4,5,6,7-hexamethyl-4,5,6,7-tetrahydroindenyltitanium trichloride; 1,3,4,5,6,7-hexamethyl-4,5,6,7-tetrahydroindenyltitanium trichloride; 1,3,4,5,6,7-hexamethyl-4,5,6,7-tetrahydroindenyltrimethyltitanium; 1,3,4,5,6,7-hexamethyl-4,5,6,7-tetrahydroindenyltribenzyltitanium; 1,3,4,5,6,7-hexamethyl-4,5,6,7-tetrahydroindenyltitanium trimethoxide; octahydrofluorenyltitanium trichloride; octahydrofluorenyltrimethyltitanium; octahydrofluorenyltribenzyltitanium; octahydrofluorenyltitanium trimethoxide; 1,2,3,4-tetrahydrofluorenyltitanium trichloride; 1,2,3,4-tetrahydrofluorenyltrimethyltitanium; 1,2,3,4-tetrahydrofluorenyltribenzyltitanium; 1,2,3,4-tetrahydrofluorenyltitanium trimethoxide; 9-methyl-1,2,3,4-tetrahydrofluorenyltitanium trichloride; 9-methyl-1,2,3,4-tetrahydrofluorenyltrimethyltitanium; 9-methyl-1,2,3,4-tetrahydrofluorenyltribenzyltitanium; 9-methyl-1,2,3,4-tetrahydrofluorenyltitanium trimethoxide; 9-methyl octahydrofluorenyltitanium trichloride; 9-methyloctahydrofluorenyltrimethyltitanium; 9-methyloctahydrofluorenyltribenzyltitanium; 9-methyloctahydrofluorenyltitanium trimethoxide; any of the above-mentioned compounds in which the titanium is replaced with zirconium or hafnium and a similar compound in which the transition metal element belongs to an other series or lanthanoids. Of these the titanium compounds are preferable from the viewpoint of catalytic activity. There are available various coordination complex compounds comprising an anion in which a plurality of radicals are bonded to a metal to be used as the component (b) in the present invention, and there is preferably usable such a coordination complex compound as represented by the following general formula (XII) or (XIII): ([L 1 -H] g+ ) h ([M 2 X 1 X 2 --- X n ] (n-m)- ) i or ([L 2 ] g+ ) q ([M 3 X 1 X 2 ---X n ] (n-m)- ) i wherein L 2 is M 4 , R 18 R 19 M 5 or R 20 3 C as hereinafter described; L 1 is a Lewis base; M 2 and M 3 are each a metal selected from Groups 5 to 15 of the Periodic Table; M 4 is a metal selected from Groups 8 to 12 of the Periodic Table; M 5 is a metal selected from Groups 8 to 10 of the Periodic Table; X 1 to X n are each a hydrogen atom, a dialkylamino group, an alkoxyl group, an aryloxyl group, an alkyl group having 1 to 20 carbon atoms, an aryl group, an alkylaryl group or an arylalkyl group, each having 6 to 20 carbon atoms, a substituted alkyl group, an organometalloid group or a halogen atom; R 18 and R 19 are each a cyclopentadienyl group, a substituted cyclopentadienyl group, an indenyl group or a fluorenyl group; R 20 is an alkyl group; m is the valency of each of M 2 and M 3 , indicating an integer of 1 to 7; n is an integer of 2 to 8; g is the ion valency of each of [L 1 -H] and [L 2 ], indicating an integer of 1 to 7; h is an integer of 1 or more; and j=hxg/(n-m). Specific examples of M 2 and M 3 include B, Al, Si, P, As, Sb in the form of atom; those of M 4 include Ag, Cu in the form of atom; and those of M 5 include Fe, Co, Ni in the form of atom. Specific examples of X 1 to X n include a dialkylamino group such as dimethylamino and diethylamino; an alkoxyl group such as methoxyl, ethoxyl and n-butoxyl; an aryloxyl group such as phenoxyl, 2,6-dimethylphenoxyl and naphthyloxyl; an alkyl group having 1 to 20 carbon atoms such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, n-octyl and 2-ethylhexyl; an aryl group, an alkylaryl group or an arylalkyl group each having 6 to 20 carbon atoms, such as phenyl, p-tolyl, benzyl, pentafluorophenyl, 3,5-di(trifluoromethyl)phenyl, 4-tert-butylphenyl, 2,6-dimethylphenyl, 3,5-dimethylphenyl, 2,4-dimethylphenyl and 1,2-dimethylphenyl; a halogen atom such as F, Cl, Br and I; and an organometalloid such as pentamethylantimony group, trimethylsilyl group, trimethylgermyl group, diphenylarsine group, dicyclohexylantimony group and diphenylboron group. Specific examples of substituted cyclopentadienyl group represented by any of R 18 and R 19 include methylcyclopentadienyl, butylcyclopentadienyl and pentamethylcyclopentadienyl. Specific examples of the anion in which a plurality of radicals are bonded to a metal include B(C 6 F 5 ) 4 - , B(C 6 HF 4 ) 4 - , B(C 6 H 2 F 3 ) 4 - , B(C 6 H 3 F 2 ) 4 - , B(C 6 H 4 F) 4 - , B(C 6 CF 3 F 4 ) 4 - , B(C 6 F 5 ) 4 - , BF 4 - , PF 6 - , P(C 6 F 5 ) 6 - and Al(C 6 HF 4 ) 4 - . Specific examples of the metallic cation include CpFe + , (MeCp) 2 Fe + , (tBuCp) 2 Fe + , (Me 2 Cp) 2 Fe + , (Me 3 Cp) 2 Fe + , (Me 4 Cp) 2 Fe + , (Me 5 Cp) 2 Fe + , Ag + , Na + and Li + , a nitrogen atom-containing compound such as pyridinium, 2,4-dinitro-N,N-diethylanilinium, diphenyl ammonium, p-nitroanilinium, 2,5-dichloroaniline, p-nitro-N,N-dimethylanilinum, quinolinium, N,N-dimethylanilinum and N,N-diethylanilinium; a carbenium compound such as triphenylcarbenium, tri(4-methylphenyl)carbenium and tri(4-methoxyphenyl)carbenium; an alkylphosphonium ion such as CH 3 PH 3 + , + C 2 H 5 PH 3 + , C 3 H 7 PH 3 + , (CH 3 ) 2 PH 2 + , (C 2 H 5 ) 2 PH 2 + , (C 3 H 7 ) 2 PH 2 + , (CH 3 ) 3 PH + , (C 2 H 5 ) 3 PH + , (C 3 H 7 ) 3 PH + , (CF 3 ) 3 PH + , (CH 3 ) 4 P + , (C 2 H 5 ) 4 P + and (C 3 H 7 ) 4 P + ; and an arylphosphonium ion such as C 6 H 5 PH 3 + , (C 6 H 5 ) 2 PH 2 + , (C 6 H 5 ) 3 PH + , (C 6 H 5 ) 4 P + , (C 2 H 5 ) 2 (C 6 H 5 )PH + , (CH 3 )(C 6 H 5 )PH 2 + , (CH 3 ) 2 (C 6 H 5 )PH + and (C 2 H 5 ) 2 (C 6 H 5 ) 2 P + . Among the compounds represented by the general formula (XII) or (XIII), specific examples of preferably usable compounds include, as the compound of the general formula (XII), triethylammonium tetraphenylborate, tri(n-butyl)ammonium tetraphenylborate, trimethylammonium tetraphenylborate, triethylammonium tetra(pentafluorophenyl)borate, tri(n-butyl)ammonium tetra(pentafluorophenyl)borate, triethylammonium hexafluoroarsenate, pyridinium tetra(pentafluorophenyl)borate, pyrrolinium tetra(pentafluorophenyl)borate, N,N-dimethylanilinium tetra(pentafluorophenyl)borate and methyldiphenylammonium tetra(pentafluorophenyl)borate, and as the compound of the general formula (XIII), ferrocenium tetraphenylborate, dimethylferrocenium tetra(pentafluorophenyl)borate, ferrocenium tetra(pentafluorophenyl)borate, decamethylferrocenium tetra(pentafluorophenyl)borate, acetylferrocenium tetra(pentafluorophenyl)borate, formylferrocenium tetra(pentafluorophenyl)borate, cyanoferrocenium tetra(pentafluorophenyl)borate, silver tetraphenylborate, silver tetra(pentafluorophenyl)borate, trityl tetraphenylborate, trityl tetra(pentafluorophenyl)borate, silver hexafluoroarsenate, silver hexafluoroantimonate and silver tetrafluoroborate. A Lewis acid may be used as the component (b) in addition to or in place of the coordination complex compound comprising an anion in which a plurality of radicals are bonded to a metal and a cation and is exemplified by an organoaluminum compound, a magnesium compound, zinc compound and lithium compound. Specific examples of the above-mentioned organoaluminum compound include the compound represented by the general formula (XIV) R 21 r Al(OR 22 ) s H t Z u wherein R 21 and R 22 independently of one another, are each an alkyl group having 1 to 8 carbon atoms and may be the same or different; Z is an halogen atom; r,s,t and u each satisfy the relations 0<rs≦3, 0<s≦3, 0≦t<3 and 0≦u<3 and r+s+t+u=3. In the organoaluminum compound represented by the general formula (XIV), the compound wherein t=u=0 and r=3 is exemplified by trimethylaluminum, triethylaluminum, triisopropylaluminum, triisobutylaluminum and trioctylaluminum. In the case of t=u=0 and 1.5≦r<3, the compound is exemplified by diethylaluminum ethoxide, dibutylaluminum butoxide, diethylaluminum sesquiethoxide and dibutylaluminum sesquibutoxide; as well as partially alkoxylated alkylaluminum. Examples of the compound corresponding to the case where s=t=0 include diethylaluminum dichloride and dibutylaluminum dichloride (r=2); ethylaluminum sesquichloride and butylaluminum sesquichloride (r=1.5); and ethylaluminum dichloride and butylaluminum dichloride (r=1). Examples of the compound corresponding to the case in which s=u=0 include diethylaluminum hydride and diisobutylaluminum hydride (r=2); and ethylaluminum dihydride and butylaluminum dihydride (r=1). Examples of the above-mentioned magnesium compound include a Grignard compound such as methylmagnesium bromide, ethylmagnesium bromide, phenylmagnesium bromide and benzylmagnesium bromide, an organomagnesium compound such as diethoxymagnesium and ethylbutylmagnesium and an inorganic magnesium compound such as magnesium chloride, of which a Grignard compound is preferable. In addition, mention may be made of a zinc compound exemplified by an organozinc compound such as diethylzinc and of a lithium compound exemplified by an organolithium compound such as methyllithium. There are available various alkylating agents as the component (c), which are exemplified by the aluminum compound having an alkyl group represented by the general formula (XV) R 21 m' Al(OR 22 ) n' X 3-m'-n' wherein R 21 and R 22 are each an alkyl group having 1 to 8, preferably 1 to 4 carbon atoms, X is a hydrogen atom or a halogen atom, m' satisfies the relation 0<m'≦3, desirably m'=2 or 3, most desirably m'=3, and n' satisfies the relation 0≦n'<3, desirably n'=0 or 1; the magnesium compound having an alkyl group represented by the general formula (XVI) R 21 2 Mg wherin R 21 is as previously defined; the zinc compound having an alkyl group represented by the general formula (XVII) R 21 2 Zn wherin R 21 is as previously defined. The aforesaid compounds each having an alkyl group are preferably aluminum compounds each having an alkyl group, more desirably trialkylaluminium compounds and dialkylaluminum compounds, and specifically exemplified by trialkylaluminum such as trimethylaluminum, triethylaluminun, tri-n-propylaluminum, triisopropylaluminum, tri-n-butylaluminum, triisobutylaluminum and tri-tert-butylaluminum; dialkylaluminum halide such as dimethylaluminum chloride, diethylaluminum chloride, di-n-propylaluminum chloride, diisopropylaluminum chloride, di-n-butylaluminum chloride, diisobutylaluminum chloride and di-tert-butylaluinum chloride; dialkylaluminum alkoxide such as dimethylaluminum methoxide and dimethylaluminum ethoxide; dialkylaluminum hydride such as dimethylaluminum hydride, diethylalumium hydride and diisobutylaluminum hydride, dialkylmagnesium such as dimethylmagnesium, diethylmagnesium, di-n-propylmagnesium and diisopropylmagnesium; and dialkylzinc such as dimethylzinc, diethylzinc, di-n-propylethylzinc and diisopropylzinc. As described hereinbefore, the process according to the present invention comprises polymerizing a styrenic monomer by the use of the catalyst composed of the components (a), (b) and (c) and incorporating in the polymerization system, a (d) reaction product between a straight chain alkylaluminum having at least two carbon atoms in the alkyl group as represented by the general formula (XVIII) and water. R 0 3 Al wherein R 0 is a straight chain alkyl group having 2 to 10, preferably 2 to 6 carbon atoms. Specific examples of such alkylaluminum include triethylaluminum, tri-n-propylaluminum, tri-n-butylaluminum, tri-n-pentylaluminum, tri-n-hexylaluminum and tri-n-heptylaluminum. The water to be reacted with the straight chain alkylaluminum may be any of ice, water, steam, an organic solvent saturated with water and water of crystallization. The reaction product between such a straight chain alkylaluminum and water to be used in the present invention is obtained by reacting the above-mentioned straight chain alkylaluminum with water in a molar ratio of 1 : (1 to 2) at a temperature of -78 to 100°C in a organic solvent without active hydrogen atom, and is represented by the general formula (XIX) or (XX) wherin R 0 is as previously defined and n is an integer from 1 to 20. Specific examples of these compounds include ethylaluminoxane, propylaluminoxane, butylaluminoxane, pentylaluminoxane, hexylaluminoxane and heptylaluminoxane. The above-mentioned compound represented by the general formula (XIX) or (XX) has preferably n of 1 to 5 and may be used alone or in combination with at least one other one. In the case of carrying out the process of the present invention, the aforesaid components (a), (b), (c) and (d) may be added, separately one by one, to the monomer to be polymerized, or may be premixed with a solvent (aromatic hydrocarbon such as toluene, and ethylbenzene or aliphatic hydrocarbon such as hexane and heptane) prior to mixing with the monomer, in which the components (c) and (d) may totally or partly be added to the monomer. The addition of the aforesaid components (a), (b), (c) and (d) to the monomer can be carried out at a temperature of 0 to 100°C, needless to say, at a polymerization temperature. The above-described catalyst along with the chain transfer agent exhibit a high activity in the production of a styrenic polymer having a high degree of syndiotactic configuration. The molecular weight of the resultant polymer can be lowered by the addition of the component (d), but the amount thereof to be added is not specifically limited, since it varies depending on the type of each of the components (a), (b), (c) and (d), the monomer species and polymerization conditions such as polymerization temperature. In the production of a styrenic polymer by the process according to the present invention, a styrenic monomer or monomers or a styrenic derivative or derivatives is homopolymerized or are copolymerized in the present of a catalyst composed mainly of the components (a), (b) and (c) and chain transfer agent of the component (d). As the styrenic monomer, there is preferably used a compound represented by the general formula (XXI) wherein R 23 is hydrogen atom, a halogen atom or a hydrocarbon group having 1 to 20 carbon atoms, m' is an integer from 1 to 3 and , when m' is 2 or greater, a plurality of R 23 may be the same or different. Examples of the compound of the general formula (XXI) include styrene; alkylstyrenes such as p-methylstyrene; m-methylstyrene; o-methylstyrene; 2,4-dimethylstyrene; 2,5-dimethylstyrene; 3,4-dimethylstyrene; 3,5-dimethylstyrene; and p-tertiary-butylstyrene; polyvinylbenzenes such as p-divinylbenzene; m-divinylbenzene; and trivinylbenzene; halogenated styrenes such as p-chlorostyrene; m-chlorostyrene; o-chlorostyrene; p-bromostyrene; m-bromostyrene; o-bromostyrene; p-fluorostyrene; m-fluorostyrene; o-fluorostyrene and o-methyl-p-fluorostyrene; alkoxystyrenes such as methoxystyrene; ethoxystyrene; and tert-butoxystyrene; and a mixture of at least two of them. The polymerization of the styrenic monomer or monomers may be carried out by means of bulk polymerization or solution polymerization by the use of an aliphatic hydrocarbon solvent such as pentane, hexane or heptane, an alicyclic hydrocarbon solvent such as cyclohexane or an aromatic hydrocarbon solvent such as benzene, toluene or xylene. The polymerization temperature is not specifically limited, but is usually in the range of 20 to 120°C, preferably 20 to 90°C. In addition, the polymerization reaction may be carried out in the presence of hydrogen in order to modify the molecular weight of the styrenic polymer to be produced. The styrenic polymer thus obtained possesses a high degree of syndiotactic configuration in its polymerization chain of the styrenic monomer. Here, the styrenic polymer having a high degree of syndiotactic configuration in its polymerization chain of the styrenic monomer means that its stereochemical structure is mainly of syndiotactic configuration, i.e. the stereostructure in which phenyl groups or substituted phenyl group as side chains are located alternately at opposite directions relative to the main chain consisting of carbon-carbon bonds. Tacticity is quantitatively determined by the nuclear magnetic resonance method ( 13 C-NMR method) using carbon isotope. The tacticity as determined by the 13 C-NMR method can be indicated in terms of proportions of structural units continuously connected to each other, i.e., a diad in which two structural units are connected to each other, a triad in which three structural units are connected to each other and a pentad in which five structural unit are connected to each other. "The styrenic polymers having a high degree of syndiotactic configuration" as mentioned in the present invention means polystyrene, poly(alkylstyrene), poly(halogenated styrene), poly(alkoxystyrene), poly(vinylbenzoate), the mixtures thereof, and copolymers containing the above polymers as main components, having such a syndiotacticity that the proportion of racemic diad is at least 75%, preferably at least 85%, or the proportion of racemic pentad is at least 30%, preferably at least 50%. The poly(alkylstyrene) include poly(methylstyrene), poly(ethylstyrene) poly(isopropylstyrene), poly(tert-butylstyrene), poly(halogenated styrene) include, poly(chlorostyrene), poly(bromostyrene), and poly(fluorostyrene). The poly(alkoxystyrene) include, poly(methoxystyrene), poly(ethoxystyrene). The most desirable styrenic polymers are polystyrene, poly(p-methylstyrene), poly(m-methylstyrene), poly(p-tert-butylstyrene), poly(p-chlorostyrene), poly(m-chlorostyrene), poly(p-fluorostyrene), and the copolymer of styrene and p-methylstyrene. As described hereinbefore, the process according to the present invention makes it possible to attain a high activity in the production of a styrenic polymer having a high degree of syndiotactic configuration, decrease the amount of the residual metals in the resultant styrenic polymer without deterioration of the catalytic activity by the use of a reaction product between the specific straight chain alkylaluminum and water, and at the same time, to simplify the production process of the styrenic polymer and curtail the production cost thereof. In the following, the present invention will be described in more detail with reference to comparative examples and examples. Reference Example 1 (1) Synthesis of ethylaluminoxane In a 5 liter (hereinafter abbreviated to "L") vessel which had been dried and purged with nitrogen was placed 178 milliliter (hereinafter abbreviated to "mL") of 0.5 mol/L solution of triethylaluminum in 112 mL of toluene. To the resultant mixture was gradually added dropwise under sufficient stirring at room temperature, 1.67L solution in toluene (H 2 O; 430.7x10 -6 g/mL) which had been adjusted in water content by means of ion-exchanged water. After the completion of the dropwise addition, the toluene was distilled away to form 8.5g of product. (2) Polymerization of styrene In a 50 mL vessel which had been dried and purged with nitrogen were successively placed 0.4mL of 2 moles/L of triisobutylaluminum in 39.3 mL of toluene, 64mg of dimethylanilinium tetra(pentafluorophenyl)borate, and 0.32 mL of 250 mmol of pentamethylcyclopentadienyltitanium trimethoxide to prepare a preliminary mixed catalyst. In a 30 mL vessel which had been dried and purged with nitrogen were placed 10 mL of styrene and 45 µL of 0.28 mol/L of ethylaluminoxane with heating to 70°C and 250 µL of the preliminary mixed catalyst as prepared above to polymerize the styrene for 1 hour. After the completion of the reaction, the reaction product was dried to afford 2.99g of a polymer. The resultant polymer was cut into slices of at most 1 mm in thickness, which were subjected to Soxhlet extraction for 6 hours by the use of methyl ethyl ketone (MEK) as the solvent to produce MIP (MEK-insoluble portion). As a result, objective SPS having a molecular weight of 310,000 was obtained in a yield of 2.83g with a raffinate (MIP) rate of 94.8% and an activity for SPS of 118 kg/g-Ti. Reference Example 2 The procedure in Example 1 (2) was repeated to obtain 2.87g of a polymer except that the addition amount of 0.28 mol/L of ethylaluminoxane was set on 90 µL in place of 45 µL. The resultant polymer was subjected to Soxhlet extraction for 6 hours by the use of methyl ethyl ketone (MEK) as the solvent to produce MIP. As a result, objective SPS having a molecular weight of 240,000 was obtained in a yield of 2.80g with a raffinate (MIP) rate of 97.6% and an activity for SPS of 117 kg/g-Ti. Reference Example 3 The procedure in Example 1 (2) was repeated to obtain 2.87g of a polymer except that there was used n-butylaluminoxane which had been prepared in the same manner as in Example 1 (1) in place of ethylaluminoxane. The resultant polymer was subjected to Soxhlet extraction for 6 hours by the use of methyl ethyl ketone (MEK) as the solvent to produce MIP. As a result, objective SPS having a molecular weight of 350,000 was obtained in a yield of 2.81g with a raffinate (MIP) rate of 97.9% and an activity for SPS of 117 kg/g-Ti. Reference Example 4 The procedure in Example 1 (2) was repeated to obtain a polymer except that there was used n-propylaluminoxane which had been prepared in the same manner as in Example 1 (1) in place of ethylaluminoxane. The resultant polymer was subjected to Soxhlet extraction for 6 hours by the use of methyl ethyl ketone (MEK) as the solvent to produce MIP. As a result, objective SPS having a molecular weight of 340,000 was obtained with a raffinate (MIP) rate of 95% and an activity for SPS of 120 kg/g-Ti. Reference Example 5 The procedure in Example 1 (2) was repeated to obtain a polymer except that there was used ferrocenium tetra(pentafluorenyl)borate in place of dimethylanilinium tetra(pentafluorenyl)borate. The resultant polymer was subjected to Soxhlet extraction for 6 hours by the use of methyl ethyl ketone (MEK) as the solvent to produce MIP. As a result, objective SPS having a molecular weight of 320,000 was obtained with a raffinate (MIP) rate of 95% and an activity for SPS of 122 kg/g-Ti. Reference Example 6 The procedure in Example 1 (2) was repeated to obtain a polymer except that there was used tri-n-butylaluminum in place of triisobutylaluminum. The resultant polymer was subjected to Soxhlet extraction for 6 hours by the use of methyl ethyl ketone (MEK) as the solvent to produce MIP. As a result, objective SPS having a molecular weight of 310,000 was obtained with a raffinate (MIP) rate of 95% and an activity for SPS of 119 kg/g-Ti. Comparative Example 1 The procedure in Example 1 (2) was repeated to obtain a polymer except that ethylaluminoxane was not used. The resultant polymer was subjected to Soxhlet extraction for 6 hours by the use of methyl ethyl ketone (MEK) as the solvent to produce MIP. As a result, objective SPS having a molecular weight of 871,000 was obtained in a yield of 2.69g with a raffinate (MIP) rate of 95.5% and an activity for SPS of 112 kg/g-Ti.

Claims: A process for producing a styrenic polymer having a high degree of syndiotactic configuration which comprises polymerizing a styrenic monomer by the use of (a) a transition metal compound represented by the general formula R'MX' p-1 L 1 q wherein R' is, as a π ligand, a fused polycyclic cyclopentadienyl group wherein at least one of many-membered rings to which cyclopentadienyl groups are fusedly bonded is a saturated ring, M is a metal belonging to any of the groups 3 to 6 of the Periodic Table or a lanthanum series metal, X' is a α ligand, a plurality of X' may be the same or different and bonded to each other through an arbitrary group, L 1 is a Lewis base, p is the valency of M, q is 0, 1 or 2 and when L 1 is plural, each L 1 may be the same or different; (b) a coordination complex compound comprising an anion in which a plurality of radicals are bonded to a metal and a cation; (c) an alkylating agent; and (d) a reaction product between a straight-chain alkylaluminum having at least two carbon atoms in the alkyl group as represented by the general formula XVIII and water: R o 3 Al wherein R o is a straight-chain alkyl group having 2 to 10 carbon atoms. A process for producing a styrenic polymer having a high degree of syndiotactic configuration which comprises polymerizing a styrenic monomer by the use of (a) a transition metal compound represented by the general formula R'MX' p-1 L 1 q wherein R' is, as a π ligand, a fused polycyclic cyclopentadienyl group wherein at least one of many-membered rings to which cyclopentadienyl groups are fusedly bonded is a saturated ring, M is a metal belonging to any of the groups 3 to 6 of the Periodic Table or a lanthanum series metal, X' is a σ ligand, a plurality of X' may be the same or different and bonded to each other through an arbitrary group, L 1 is a Lewis base, p is the valency of M, q is 0, 1 or 2 and when L 1 is plural, each L 1 may be the same or different; (b) a Lewis acid; (c) an alkylating agent; and (d) a reaction product between a straight-chain alkylaluminum having at least two carbon atoms in the alkyl group as represented by the general formula XVIII and water: R o 3 Al wherein R o is a straight-chain alkyl group having 2 to 10 carbon atoms, proviso that a compound belonging to the component (b) is different from a compound belonging to the component (c). The process according to Claim 1 or 2 wherein the reaction product as the component (d) is a compound represented by the general formula wherein R 0 is a straight-chain alkyl group having 2 to 10 carbon atoms and n is an integer of 1 to 20. The process according to Claim 1 or 2 wherein the reaction product as the component (d) is at least one member selected from the group consisting of ethylaluminoxane, propylaluminoxane, butylaluminoxane, pentylaluminoxane, hexylaluminoxane and heptylaluminoxane. The process according to Claim 1 or 2 wherein the alkylating agent as the component (c) is at least one member selected from the group consisting of alkyl group-containing aluminum compounds, alkyl group-containing magnesium compound and alkyl group-containing zinc compound.

Inventors: AOYAMA YOSHIAKI, TOMOTSU NORIO, AOYAMA, YOSHIAKI, TOMOTSU, NORIO
Applicants: IDEMITSU KOSAN CO, IDEMITSU KOSAN CO., LTD.
Application year: 1995
Main classification: C08F12
IPC codes: C08F12