EPOXY RESIN COMPOSITION FOR SEALING PHOTOSEMICONDUCTOR DEVICE

Abstract: An epoxy resin composition useful as a encapsulating material for photosemiconductor elements such as a photodetector or a light emittor and comprising an epoxy resin, a hardener and at least one compound represented by the following general formula (1) or (2). It can realize an excellent mold releasability from a forming die in transfer molding and the like and also give a encapsulating resin excellent in transparency. wherein Y 1 represents -H, -RCOOH, -COR' or -R' wherein R is a bivalent organic group and R' is an alkyl group whose carbon number is not more than 30; x represents a positive number of 8 to 200 and is a mean value; and n is set in such a manner that the weight ratio of the repeating unit n accounts for 25 to 95% by weight based on the whole compound. wherein R represents a bivalent organic group, Y 2 represents a metal atom having the valence of one or more, m represents a positive integer corresponding to the valence of Y 2 , x represents a positive number of 8 to 200 and is a mean value; and n is set in such a manner that the weight ratio of the repeating unit n accounts for 25 to 95% by weight based on the whole compound.

Description: FIELD OF THE INVENTION The present invention relates to an epoxy resin composition effective for encapsulating a photosemiconductor element with superior mold releasability and transparency. BACKGROUND OF THE INVENTION Heretofore, an epoxy resin composition has been used as a material for encapsulating photosemiconductor elements such as photodetector or a light emitter in view of superiority in transparency, moisture resistance and heat resistance. An earlier epoxy resin composition is described in US 4,628,080, which discloses a composition comprising an epoxy resin, a cationic curing agent and a surfactant, the surfactant added to increase the reproductability of cure rates of the cationic curing agent However, in spite of superiority in transparency, a conventional epoxy resin composition has a defect that mold releasability drastically deteriorates when forming a photosemiconductor device by transfer molding a photosemiconductor element and an epoxy resin composition in a forming die. For this reason, various kinds of troubles are caused. For example, a photosemiconductor device deforms, a package cracks, a photosemiconductor element and an encapsulating resin separate, or gold wires peel off by stress in mold releasing. Such troubles are distinctly identified by a variety of life tests for photosemiconductor devices, however, generally such photosemiconductor devices are judged as insufficient before they are subjected to such life tests and treated separately as defectives. For this reason, heretofore, countermeasures have been studied. For example, there is a method that a conventional mold releasing agent is preliminarily mixed in an epoxy resin composition as an encapsulating material. Addition of some kinds of the mold releasing agent to an epoxy resin composition makes it possible to produce a resin composition superior in transparency which is one of the important properties for a resin composition for encapsulating a photosemiconductor element. However, a resin composition superior both in transparency and mold releasability has not been developed. On the contrary, a resin composition for encapsulation superior in mold releasability can be produced by the addition of a mold releasing agent, which, however, causes a problem of deterioration in transparency. Thus, it is a current situation that an epoxy resin composition for encapsulation superior both in transparency and mold releasability has not been obtained. Object of the invention It is an object of the present invention to provide an epoxy resin composition for encapsulating a photosemiconductor element superior both in mold releasability from a forming die in transfer molding and in transparency. Disclosure of the invention In order to achieve the object mentioned above, the epoxy resin composition for encapsulating a photosemiconductor element in the present invention comprises the following components (A) to (C): (A) an epoxy resin; (B) a hardener; and (C) at least one compound represented by the following general formula (1) or (2). wherein Y 1 represents -H, -RCOOH, -COR' or -R' wherein R is a bivalent organic group and R' is an alkyl group whose carbon number is not more than 30; x represents a positive number of 17 to 200 and is a mean value; and n is set in such a manner that the weight ratio of the repeating unit n accounts for 25 to 95% by weight based on the whole compound. wherein R represents a bivalent organic group, Y 2 represents a metal atom having the valence of one or more, m represents a positive integer corresponding to the valence of Y 2 , x represents a positive number of 8 to 200 and is a mean value; and n is set in such a manner that the weight ratio of the repeating unit n accounts for 25 to 95% by weight based on the whole compound. The present invention further provides a photosemiconductor device made by encapsulating a photosemiconductor element with epoxy resin compositions according to the first aspect of the present invention. Namely, the inventors of the present invention have piled up a series of studies in order to obtain an epoxy resin composition for encapsulating a photosemiconductor element superior in both transparency and mold releasability. As a result of repeated tests by employing a variety of compounds to obtain good releasability without deteriorating transparency, it was found out that by employing at least either a specific compound represented by the general formula (1) or (2) as the component (C), an epoxy resin composition for encapsulating a photosemiconductor element superior in both transparency and mold releasability can be obtained, thus achieving the present invention. Particularly, by setting up the content of the above component (C) at 0.01 to 15% by weight (just abbreviated to % hereinafter) based on the whole epoxy resin composition for encapsulating a photosemiconductor element so as to prevent decrease in glass transition temperature or moisture Resistance reliability, sufficient mold releasability can be obtained. The epoxy resin composition, generally in a state of powder or a tablet made therewith, for encapsulating a photosemiconductor element of the present invention can be obtained by employing an epoxy resin (component A), a hardener (component B) and a specific compound (component C), and adding a hardening accelerator according to the case. As the epoxy resin (component A), there is no specific limitation so long as it has good transparency. For example, there are a bisphenol A type epoxy resin, a bisphenol F type epoxy resin, a phenol novolak type epoxy resin, a cresol novolak type epoxy resin, a cyclo aliphatic epoxy resin, cyclic epoxy resins containing nitrogen such as triglycidyl isocyanurate, a hydantoin epoxy resin and the like, a hydrogenated bisphenol A type epoxy resin, an aliphatic type epoxy resin, a glycidyl ether type epoxy resin, a bisphenol S type epoxy resin and the like. These are employed solely or in combination. Among the above various kinds of epoxy resins, it is preferable to employ a bisphenol A type epoxy resin, a bisphenol F type epoxy resin, a cyclo aliphatic epoxy resin or triglycidyl isocyanurate in view of resistance to discoloration of an encapsulating resin (hardened material) after encapsulating a photosemiconductor element. As a hardener (component B) employed together with the above epoxy resin (component A), there is no specific limitation so long as it has good transparency, however, it is preferable to employ a variety of acid anhydrides in view of less degree of discoloration of an encapsulating resin. Specifically, phthalic anhydride, maleic anhydride, trimellitic anhydride, pyromellitic anhydride, hexahydrophthalic anhydride, tetrahydrophtalic anhydride, methyl nadic anhydride, nadic anhydride, glutaric anhydride, methyl hexahydrophthalic anhydride, methyl tetrahydrophthalic anhydride and the like may be listed. These are employed solely or in combination. Among them, it is preferable to employ phthalic anhydride, hexahydrophthalic anhydride, tetrahydrophthalic anhydride or methyl hexahydrophthalic anhydride. Moreover, a conventional hardener, for example, amines, phenols or carboxylic acids such as hexahydrophthalic acids, tetrahydrophthalic acids, methyl hexahydro phthalic acids and the like may be employed solely or in combination other than the above acid anhydrides. As a mixing ratio of the above epoxy resin (component A) and the above hardener (component B), for example, when an acid anhydride is employed for the hardener, it is preferable to set up 0.5 to 1.5 for an acid anhydride equivalent per 1 equivalent of epoxy group in the above epoxy resin. Particularly, 0.7 to 1.2 is preferable. That is, when the acid anhydride equivalent of the above mixing ratio is below 0.5 equivalents, the hue of thus obtained epoxy resin deteriorates after hardening, in the meantime, when it is over 1.5 equivalents, moisture resistance tends to deteriorate. In addition, when the above mentioned amines, phenols or carboxylic acids are employed solely or in combination other than the acid anhydrides as a hardener (component B), the mixing ratio is set in accordance with the mixing ratio (equivalent ratio) when the acid anhydride is employed. A specific compound (component C) employed together with the components A and B is at least one compound represented by the following general formula (1) or (2). The addition thereof makes it easy to release a photosemiconductor device from a forming die when transfer molding with no damage in transparency of the encapsulating resin, which is the characteristic of this invention. CH 3 CH 2 (CH 2 -CH 2 ) x CH 2 -CH 2 -O (CH 2 -CH 2 -O) n Y 1 wherein Y 1 represents -H, -RCOOH, -COR' or -R' wherein R is a bivalent organic group and R' is an alkyl group whose carbon number is not more than 30; x represents a positive number of 17 to 200 and is a mean value; and n is set in such a manner that the weight ratio of the repeating unit n accounts for 25 to 95% by weight based on the whole compound. [CH 3 CH 2 (CH 2 -CH 2 ) x CH 2 -CH 2 -O (CH 2 -CH 2 -O) n RCOO ] m Y 2 wherein R represents a bivalent organic group, Y 2 represents a metal atom having the valence of one or more, m represents a positive integer corresponding to the valence of Y 2 , x represents a positive number of 8 to 200 and is a mean value; and n is set in such a manner that the weight ratio of the repeating unit n accounts for 25 to 95% by weight based on the whole compound. In the general formula (1), Y 1 is a hydrogen atom, - RCOOH (wherein R is a bivalent organic group), -COR' or -R' (wherein every R' is an alkyl group whose carbon number is not more than 30). Preferably, as Y 1 , there are hydrogen atom, -RCOOH wherein R is alkylene group having 30 carbons or below, or -COR' or -R' wherein R' is an alkyl group whose carbon number is 1 to 30. Further, as a metallic atom of Y 2 in the general formula (2), for example, zinc, calcium, barium, aluminium, magnesium, lead, potassium, sodium and the like can be listed. Particularly, in view of transparency, it is preferable to employ calcium, sodium or zinc for Y 2 . Still further, both in the general formulae (1) and (2), the repeating numeral x is within a range of 8 to 200 and the repeating unit n is set in such a manner that the weight ratio of the repeating unit n accounts for 25 to 95% based on the whole compound represented by the general formulae (1) and (2) respectively. More preferably, the repeating numeral x is a positive number of 13 to 28 and the weight ratio of the repeating unit n is 35 to 85% both in the general formulae (1) and (2) respectively. Most preferably, the repeating numeral x is a positive number of 17 to 23 and the repeating unit n accounts for 45 to 70% both in the general formulae (1) and (2) respectively. In addition, when there are several kinds of compounds represented by the general formulae (1) and (2) respectively, the repeating numeral x is a mean value of every repeating numeral x respectively. Moreover, the weight ratio (%) of the repeating unit n is a value calculated from the following formula. (molecular weight of the repeating unit n) [molecular weight of compound represented by the general formula (1) or (2)] ×100 In this way, as the compounds represented by the general formulae (1) and (2), those whose mean molecular weight is in the range of 300 to 300,000 are employed. Preferably, it is 600 to 12,000. More preferably, it is 900 to 5,000. The compound represented by the general formula (1) can be obtained, for example, by adding ethylene oxide into higher alcohol. Preferably, at least one compound (component C) represented by the general formula (1) or (2) is mixed so as to account for 0.01 to 15% based on the whole epoxy resin composition. More preferably, the mixing ratio is 0.1 to 5% and most preferably, 0.5 to 3%. Namely, with lower mixing ratio of the component C, sufficient mold releasability from a forming die cannot be obtained when transfer molding, while with over mixing ratio, there is a possibility that a glass transition temperature or moisture resistance reliability may decrease. Further, a hardening accelerator, a dye, a pigment, a modifier, an antioxidant, a coupling agent, a mold releasing agent and the like may appropriately be mixed in the epoxy resin composition for encapsulating a photosemiconductor element of the present invention other than the above components (A) to (C) within a range so as not to damage transparency. As the above hardening accelerator, there is no specific limitation and any conventional type can be employed. For example, tertiary amines, imidazoles, quaternary ammonium salts and organometallic salts, and phosphorus compounds, 1,8-diazabicyclo [5,4,0]undec-7-ene and their derivatives can be listed. These are employed solely or in combination. Among these hardening accelerators, it is preferable to employ tertiary amines or imidazoles. The mixing ratio of the hardening accelerator is preferably set within a range of 0.01 to 8 parts by weight (just abbreviated to part hereinafter) based on 100 parts of the epoxy resin (component A), more preferably, 0.1 to 3 parts. Namely, the mixing ratio below 0.01 parts thereof does not bring about a sufficient effect in hardening acceleration, while that over 8 parts may cause a possibility of discoloration in the encapsulating resin (hardened material). As the above modifier, conventional types such as glycols, silicones and the like can be listed. As the above antioxidant, conventional types such as phenol compounds, amine compounds, organic sulfur compounds, phosphinic compounds and the like can be listed. As the above coupling agent, conventional types such as silanes, titanates and the like can be listed. As the above mold releasing agent, conventional types such as long linear carboxylic acids such as stearic acid, behehic acid and montan acid, and their metallic salts, higher alcohols such as stearyl alcohol, amides such as stearyl bis amide, carnauba, esters such as phosphoric ester, paraffin wax and the like can be listed. The mixing ratio of such a mold releasing agent is generally said to be not more than 3% based on the whole resin composition, however, this is not critical so long as no deterioration in transparency may be caused as mentioned above. Besides, when light dispersion property is required, a filler may be mixed in addition to the above components. As the filler, mineral fillers such as fused quartz powder, talc, silica powder, alumina powder and calcium carbonate can be listed. As a suitable combination of each component for the epoxy resin composition for encapsulating a photosemiconductor element, in view of superior transparency and mold releasability, a bisphenol A type epoxy resin, triglycidyl isocyanurate, a novolak type epoxy resin or a cyclo aliphatic epoxy resin as an epoxy resin (component A), tetrahydrophthalic anhydride or phthalic anhydride as a hardener (component B), tertiary amines or imidazols as a hardening accelerator of the other additive are employed together with compounds (component C) represented by the foregoing general formulae (1) and/or (2). At that time, each repeating numeral x in the formulae (1) is preferably a positive number of 17 to 28, in the formula (2) preferably a positive number of 13 to 28, and each repeating unit n preferably accounts for 35 to 85% based on the whole compound. Among these combinations, the especially preferable combination is in view of a better effect to prevent discoloration of a hardened resin, a bisphenol A type epoxy resin or triglycidyl isocyanurate as an epoxy resin (component A), tetrahydrophthalic anhydride as a hardener (component B) and imidazoles as a hardening accelerator of the other additive are employed together with the compound (component c) represented by the general formulae (1) and/or (2) wherein the repeating numeral x is a positive number of 17 to 23 and the repeating unit n accounts for 45 to 70% based on the whole compound. For example, the epoxy resin composition for encapsulating a photosemiconductor element of the present invention can be produced by the following manner. First, the above components (A) to (C), and according to the case, a hardening accelerator, a dye, a pigment, a modifier, an antioxidant, a coupling agent, a mold releasing agent, a filler and the like are blended at a specific ratio. The mixture is then mixed and kneaded by adopting a dry blend method or a fusion blend method appropriately in accordance with the usual way. Consecutively, it is cooled and cracked, and further tableted as needed, thus obtaining the epoxy resin composition. A method for encapsulating a photosemiconductor element by employing such epoxy resin composition is not critical, and for example, a conventional mold method such as a transfer molding is available. Thus obtained photosemiconductor device is superior in both transparency of the encapsulating resin and mold releasability when transfer molding, resulting in no bad effects due to inferior mold releasability heretofore on the photosemiconductor device. Besides, in the present invention, as a hardened material of the encapsulating resin, preferably, light transmittance at 600nm wave length is not less than 70% on a hardened material in 1mm thickness, more preferably not less than 80% in accordance with a measurement of a spectrophotometer. The invention will further be described in examples with reference to comparative examples. EXAMPLES First, compounds a to 1 shown in the following table 1 were prepared prior to examples. In addition, the compounds a to i are compounds represented by the above mentioned general formula (1), wherein the last symbol Y 1 is a hydrogen atom. Besides, in addition to the compounds a to 1, compounds m to o shown in the following table 2 were prepared prior to examples. The compounds m to o are compounds represented by the above mentioned general formula (1). Further, in addition to the compounds a to o, compounds p to r shown in the following table 3 were prepared. The compounds p to r are compounds represented by the general formula (2). Then, epoxy resins A to D, hardeners E to G, hardening accelerators H to I and antioxidants J to L were prepared. [Epoxy resin A] Bisphenol A type epoxy resin (epoxy equivalent: 650, melting point; 83 °C) [Epoxy resin B] Tris (2,3-epoxypropyl) isocyanurate (epoxy equivalent: 100, melting point: 110 °C) [Epoxy resin C] Cresol novolak type epoxy resin (epoxy equivalent: 215, softening point: 92°C) [Epoxy resin D] Cyclo aliphatic epoxy resin represented by the following general formula (3) (epoxy equivalent: 187, softening point: 73 °C) wherein R 1 represents trimethylolpropane residual group and A represents [Hardener E] Tetrahydrophthalic anhydride [Hardener F] Diaminodiphenyl methane [Hardener G] Phenol novolak type resin (hydroxyl group equivalent: 105, softening point: 72 °C) [Hardening accelerator H] 2-ethyl-4-methylimidazole [Hardening accelerator I] Dimethylbenzyl amine [Antioxidant J] 2,6-di-tert-butyl-hydrotoluene represented by the following structural formula (4) [Antioxidant K] Triphenyl phosphite represented by the following structural formula (5) [Antioxidant L] 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide REFERENTIAL EXAMPLES 1 to 3, EXAMPLES 4 TO 27 AND COMPARATIVE EXAMPLES 1 TO 6 Each component shown in tables 4 to 8 was mixed at a specified ratio shown therein. The mixture was fusion-kneaded at 80 to 130 °C by a mixing roller. After being cured, the mixture was cooled at room temperature and crushed, thus obtaining powdery epoxy resin composition as an object. (parts) EXAMPLES 1 2 3 4 5 6 7 EPOXY RESIN A 72.5 72.5 72.5 72.5 80 80 80 B 27.5 27.5 27.5 27.5 20 20 20 C - - - - - - - D - - - - - - - HARDENER E 55.2 55.2 55.2 55.2 44.2 44.2 44.2 F - - - - - - - G - - - - - - - HARDENING H 0.4 0.4 0.4 0.4 0.4 0.4 0.4 ACCELERATOR I - - - - - - - ANTIOXIDANT J 1.0 1.0 1.0 1.0 1.0 1.0 1.0 K 1.0 1.0 1.0 1.0 1.5 1.5 1.5 L - - - - - - - COMPOUND a 1.6 - - - - - - b - 1.6 - - - - - c - - 8.3 - - - - d - - - 1.6 4.5 - - e - - - - - 0.44 0.74 CONTENT OF COMPOUND (%) 1.0 1.0 5.0 1.0 3.0 0.3 0.5 (parts) EXAMPLES 8 9 10 11 12 13 14 15 EPOXY RESIN A 80 80 100 - 55 60 80 80 B 20 20 - - - - 20 20 C - - - 100 45 - - - D - - - - - 40 - - HARDENER E 44.2 44.2 - - 46.2 37.2 44.2 44.2 F - - 7.6 - - - - - G - - - 50 - - - - HARDENING H 0.4 0.4 - 0.4 - - 0.4 0.4 ACCELERATOR I - - - - 0.8 0.8 - - ANTIOXIDANT J 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 K 1.5 1.5 - - - - 1.5 1.5 L - - 1.0 1.0 1.0 1.0 - - COMPOUND a - - - - - - - - b - - - - - - - - c - - - - - - - - d - - - - - - - - e 4.5 7.7 3.4 4.7 4.6 4.3 16.4 - f - - - - - - - 0.15 CONTENT OF COMPOUND (%) 3.0 5.0 3.0 3.0 3.0 3.0 10.0 0.1 (parts) EXAMPLES 16 17 18 19 20 21 22 23 EPOXY RESIN A 80 80 80 80 80 80 80 80 B 20 20 20 20 20 20 20 20 C - - - - - - - - D - - - - - - - - HARDENER E 44.2 44.2 44.2 44.2 44.2 44.2 44.2 44.2 F - - - - - - - - G - - - - - - - - HARDENING H 0.4 0.4 0.4 0.4 0.4 0.4 0.4 0.4 ACCELERATOR I - - - - - - - - ANTIOXIDANT J 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 K 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 L - - - - - - - - COMPOUND m 3.0 - - - - - - - n - 0.3 - - - - - - o - - 3.0 - - - 0.15 7.7 p - - - 3.0 - - - - q - - - - 3.0 - - - r - - - - - 3.0 - - CONTENT OF COMPOUND (%) 2.0 0.2 2.0 2.0 2.0 2.0 0.1 5.0 (parts) EXAMPLES 24 25 26 27 28 29 EPOXY RESIN A 80 80 80 80 80 80 B 20 20 20 20 20 20 C - - - - - - D - - - - - - HARDENER E 44.2 44.2 44.2 44.2 44.2 44.2 F - - - - - - G - - - - - - HARDENING H 0.4 0.4 0.4 0.4 0.4 0.4 ACCELERATOR I - - - - - - ANTIOXIDANT J 1.0 1.0 1.0 1.0 1.0 1.0 K 1.5 1.5 1.5 1.5 1.5 1.5 L - - - - - - COMPOUND e - - - - 1.5 1.5 q 0.15 7.7 - - 1.5 - r - - 0.15 7.7 - 1.5 CONTENT OF COMPOUND (%) 0.1 5.0 0.1 5.0 2.0 2.0 (parts) COMPARATIVE EXAMPLES 1 2 3 4 5 6 EPOXY RESIN A 80 80 80 80 80 80 B 20 20 20 20 20 20 C - - - - - - D - - - - - - HARDENER E 44.2 44.2 44.2 44.2 44.2 44.2 F - - - - - - G - - - - - - HARDENING H 0.4 0.4 0.4 0.4 0.4 0.4 ACCELERATOR I - - - - -- - ANTIOXIDANT J 1.0 1.0 1.0 1.0 1.0 1.0 K 1.5 1.5 1.5 1.5 1.5 1.5 L - - - - - - COMPOUND g 4.5 - - - - - h - 4.5 - - - - i - - 4.5 - - - j - - - 3.0 - - k - - - - 4.5 - 1 - - - - - 0.74 CONTENT OF COMPOUND (%) 3.0 3.0 3.0 2.0 3.0 0.5 As mentioned above, by employing thus obtained powdery epoxy resin composition in examples and comparative examples, a photosemiconductor element was transfer molded (molding conditions: 150°C × 4 minutes), and subsequently after-cured at 150°C for 3 hours so as to produce photosemiconduct or devices. Thus obtained photosemiconductor devices were evaluated in view of mold releasability from a forming die. The evaluation of the mold releasability was conducted on every fourth shot's photosemiconductor device consecutively molded by transfer molding after cleaning molding with a melamine formaldehyde resin (Nippon Carbide Industries; Nikalet ECR, Grade AA). When a photosemiconductor device (package size: 19.8mm× 13.9mm × 2.8mm thickness) could be taken out from a forming die (a cavity) with working an ejector pin only, the evaluation iso ○. When being taken out with an ejector pin and air blasting, the evaluation is ○. When not being taken out with an ejector pin, air blasting and the like and being taken out additionally with mechanical force, resulting in deformation or cracking of the package, the evaluation is ×. The results are shown in the following tables 9 to 13. Moreover, by employing each of the above epoxy resin composition, a hardened material in 1mm thickness was molded (hardening conditions: 150°C × 4 minutes + 150°C x 3 hours (after cure)]. Light transmittance at 600nm wave length was measured on thus obtained hardened material by a spectrophotometer (Shimadzu Corporation; UV-3101PC). The results are shown in the following tables 9 to 13. (parts) EXAMPLES 1 2 3 4 5 6 7 MOLD RELEASABILITY ○ ○ ○ ○ o ○ ○ ○ LIGHT TRANSMITTANCE (%) 82.4 84.6 81.0 88.3 72.3 92.9 94.4 (parts) EXAMPLES 8 9 10 11 12 13 14 15 MOLD RELEASABILITY o ○ o ○ ○ ○ ○ ○ ○ ○ LIGHT TRANSMITTANCE (%) 95.2 95.6 78.0 91.3 94.0 94.8 96,0 73.0 (parts) EXAMPLES 16 17 18 19 20 21 22 23 MOLD RELEASABILITY ○ ○ ○ ○ ○ ○ ○ ○ LIGHT TRANSMITTANCE (%) 90.0 70.0 91.0 88.0 78.0 81.2 93.0 79.0 (parts) EXAMPLES 24 25 26 27 28 29 MOLD RELEASABILITY ○ o ○ ○ o ○ o ○ o ○ LIGHT TRANSMITTANCE (%) 85.0 72.0 90.0 73,0 85.0 88.0 (parts) COMPARATIVE EXAMPLES 1 2 3 4 5 6 MOLD RELEASABILITY o ○ o ○ o ○ × o ○ × LIGHT TRANSMITTANCE (%)1.0> 1.0> 1.0> 98.8 1.0> 91.0 From results of the above tables 9 to 13, it is found out that all examples were high in light transmittance and superior in mold releasability. This shows that the examples are superior in both transparency and mold releasability. On the other hand, comparative examples 1 to 3 and 5 were good in mold releasability, however, very bad in light transmittance. Further, comparative examples 4 and 6 were high in light transmittance, however, very bad in mold releasability. In this way, comparative examples were good in either of light transmittance or mold releasability and bad in the other one. There were no comparative examples which showed satisfactory results in both properties. EFFECTS OF THE INVENTION As mentioned above, the epoxy resin composition for encapsulating a photosemiconductor element in the present invention contains at least one specific compound (component C) represented by the general formula (1) or (2). For this reason, the encapsulating resin by the epoxy resin composition retains high transparency and is also superior in mold releasability from a forming die when transfer molding and the like. Particularly, by setting up the content of the above component (C) in the range of 0.01 to 15% based on the whole epoxy resin composition for encapsulating a photosemiconductor element, sufficient mold releasability can be obtained together with prevention of reduction in glass transition temperature or moisture resistance reliability. Therefore, when encapsulating a photosemiconductor element with this epoxy resin composition, a photosemiconductor device with high reliability can be obtained without being handled as defects due to damages caused by bad mold releasability.

Claims: An epoxy resin composition comprising the following (A) to (C) for encapsulating a photosemiconductor element: (A) an epoxy resin; (B) a hardener; (C) at least one compound represented by the following general formula (1) or (2) CH 3 CH 2 -(-CH 2 -CH 2 -)- x -CH 2 -CH 2 -O-(-CH 2 -CH 2 -O-)- n - Y 1 wherein Y 1 represents -H, -RCOOH, -COR' or -R' wherein R is a bivalent organic group and R' is an alkyl group whose carbon number is not more than 30; x represents a positive number of 17 to 200 and is a mean value; and n is set in such a manner that the weight ratio of the repeating unit n accounts for 25 to 95% by weight based on the whole compound, [CH 3 CH 2 -(-CH 2 -CH 2 -)- x - CH 2 -CH 2 -O-(-CH 2 -CH 2 -O-)- n - RCOO-] m - Y 2 wherein R represents a bivalent organic group, Y 2 represents a metal atom having the valence of one or more, m represents a positive integer corresponding to the valence of Y 2 , x represents a positive number of 8 to 200 and is a mean value; and n is set in such a manner that the weight ratio of the repeating unit n accounts for 25 to 95% by weight based on the whole compound. An epoxy resin composition for encapsulating a photosemiconductor element according to claim 1, wherein the repeating numeral x is a positive number of 17 to 28 and the repeating unit n is set in such a manner that the weight ratio of n accounts for 35 to 85% by weight based on the whole compound in the formulae (1) and/or (2). An epoxy resin composition for encapsulating a photosemiconductor element according to claim 1, wherein the repeating numeral x is a positive number of 17 to 23 and the repeating unit n is set in such a manner that the weight ratio of n accounts for 45 to 70% by weight based on the whole compound in the formulae (1) and/or (2). An epoxy resin composition for encapsulating a photosemiconductor element according to any of claims 1 to 3, wherein content of the component (C) is arranged so as to account for 0.01 to 15% by weight based on the whole epoxy resin composition. An epoxy resin composition for encapsulating a photosemiconductor element according to any of claims 1 to 3, wherein content of the component (C) is arranged so as to account for 0.01 to 5% by weight based on the whole epoxy resin composition. An epoxy resin composition for encapsulating a photosemiconductor element according to any one of claims 1 to 3, wherein content of the component (C) is arranged so as to account for 0.5 to 3% by weight based on the whole epoxy resin composition. An epoxy resin composition for encapsulating a photosemiconductor element according to any of claims 1 to 6, wherein the component (A) is at least one epoxy resin selected from the group consisting of a bisphenol A type epoxy resin, triglycidyl isocyanurate, a novolak type epoxy resin and a cyclo aliphatic epoxy resin, the component (B)is at least one of tetrahydrophtalic anhydride or phtalic anhydride, the component (C) is at least one compound represented by the formula (1) or (2) in which the repeating numeral x is a positive number of 17 to 28 and the repeating unit n accounts for 35 to 85% by weight based on the whole compound, and further a hardening accelerator comprising at least one of tertiary amines or imidazoles are mixed with the components (A) to (C). An epoxy resin composition for encapsulating a photosemiconductor element according to any of claims 1 to 6, wherein the component (A) is at least one of a bisphenol A type epoxy resin or triglycidyl isocyanurate, the component (B) is tetrahydrophtalic anhydride, and the component (C) is at least one compound represented by the formula (1) or (2) in which the repeating numeral x is a positive number of 17 to 23 and the repeating unit n accounts for 45 to 70% by weight based on the whole compound, and further imidazoles are mixed with the components (A) to (C) as a hardening accelerator. A photosemiconductor device made by encapsulating a photosemiconductor element with the epoxy resin composition of any of the preceding claims. A photosemiconductor device according to claim 9 wherein content of the component (C) is set within 0.01 to 15% by weight based on the whole epoxy resin composition.

Inventors: HARADA TADAAKI, KOUYAMA HIROKATSU, MARUHASHI TAKAHIKO, SHIMADA KATSUMI, TANIGAWA SATOSHI, UENISHI SHINJIROU, HARADA, TADAAKI, KOUYAMA, HIROKATSU, MARUHASHI, TAKAHIKO, SHIMADA, KATSUMI, TANIGAWA, SATOSHI, UENISHI, SHINJIROU
Applicants: NITTO DENKO CORP, NITTO DENKO CORPORATION
Application year: 1995
Main classification: C08L63
IPC codes: C08G59, C08L71, H01L31, H01L23, H01L33, C08L63