Imidazolinyl-functional organo-siloxanes and method for preparation thereof

Abstract: Imidazolinyl-functional organosiloxanes, in which an aliphatically unsaturated monovalent hydrocarbon radical is bonded at the 2-position of the imidazoline ring, have from 2 to 1,100 siloxane units where at least one siloxane unit has an imidazolinyl radical of the following general formula bonded to silicon wherein R¹ is a C₁ to C₅₀ divalent hydrocarbon radicals, each R² is hydrogen atom or a C₁ to C₅₀ monovalent hydrocarbon radicals, and R³ is a C₂ to C₅₀ aliphatically unsaturated monovalent hydrocarbon radical. A method for the preparation thereof by a dehydration reaction of an amino-functional organosiloxane and an aliphatically unsaturated monocarboxylic acid is also described.

Description: This invention provides imidazolinyl-function-al organosiloxanes and a method for the preparation thereof. More particularly, this invention relates to imidazolinyl-func-tional organosiloxanes that carry an imidazolinyl radical substituted by an aliphatically unsaturated monovalent hydro-carbon radical at the 2 position of the imidazoline ring. These imidazolinyl-functional organosiloxanes are useful as additives for modifying the surfaces of cured products from room-temperature-curable (RTV) organopolysiloxane compositions. Organosiloxanes containing an imidazolinyl radical such as that of the following formula in the molecule where the nitrogen atom bonded to the radical is the 1-position, the carbon atom bonded to hydrogen atom and the double bond is the 2-position, the nitrogen atom bonded to the double bond is the 3-position, and going in a counter clockwise direction the remaining carbon atoms are the 4-position and the 5-position are known from U.S. Patents 3,373,137, and 4,797,439. Organosiloxanes containing imidazolinyl-functional radicals with monovalent hydrocarbon radicals which are free of aliphatic unsaturation substituted in the 2-position are known from U.S. Patent 3,440,261. However, imidazolinyl-functional organosiloxane in which the 2-position of the imidazoline ring is substituted by an aliphatically unsaturated monovalent hydrocarbon radical is unknown. We achieved the instant invention as the result of extensive investigations directed to the development of imidazolinyl-functional organosiloxanes in which the 2-position of the imidazoline ring is substituted by an unsaturated hydrocarbon radical. The present invention takes as its object the development of imidazolinyl-functional organosiloxanes in which an aliphatically unsaturated monovalent hydrocarbon radical is bonded at the 2-position of the imidazoline ring. Another object is a method for the preparation of these imidazolinyl-functional organosiloxanes. The present invention provides an imidazolinyl-functional organosiloxane comprising from 2 to 1,100 siloxane units where at least one siloxane unit has an imidazolinyl radical of the following general formula bonded to silicon wherein R 1 is a C 1 to C 50 divalent hydrocarbon radical, each R 2 is selected from hydrogen atom or a C 1 to C 50 monovalent hydrocarbon radical, and R 3 is a C 2 to C 50 monovalent hydrocarbon radical with aliphatic unsaturation. The imidazolinyl-functional organosiloxanes of the present invention contains from 2 to 1,100 siloxane units where at least one siloxane unit has a imidazolinyl radical with the following general formula bonded to silicon. The radical R 1 is a C 1 to C 50 divalent hydrocarbon radical and is exemplified by alkylene radicals such as methylene, ethylene, propylene, and butylene, and by arylene radicals such as phenylene, tolylene, and xylylene. R 1 is preferably a C 1 to C 8 divalent hydrocarbon radical. Each of the radicals R 2 is hydrogen atom or an independently selected C 1 to C 50 monovalent hydrocarbon radical is selected specifically. R 2 is preferably hydrogen or a C 1 to C 8 monovalent hydrocarbon radical which is exemplified by methyl, ethyl, and propyl R 3 is a C 2 to C 50 aliphatically unsaturated monovalent hydrocarbon radical and is exemplified by vinyl, allyl, butenyl, heptadecenyl, and heptadecadienyl. R 3 is preferably a C 10 to C 20 monovalent hydrocarbon radical. Organosiloxanes where R 3 is a mixture of such C 10 to C 20 monovalent hydrocarbon radicals is most preferred. The subject imidazolinyl-functional organosiloxanes are specifically exemplified by straight-chain organosiloxane with the general formula or by cyclic organosiloxane with the general formula wherein R 1 , R 2 , and R 3 are each defined as above. Each R 4 is independently selected from C 1 to C 50 monovalent hydrocarbon radicals. These are exemplified by alkyl radicals such as methyl, ethyl, and propyl or by aryl radicals such as phenyl, tolyl, and xylyl. R 4 is preferably a C 1 to C 8 monovalent hydrocarbon radical. Each R 5 is hydroxyl radical or an independent selection from C 1 to C 50 monovalent hydrocarbon radicals wherein said monovalent hydrocarbon radicals are exemplified by alkyl radicals such as methyl, ethyl, and propyl; by alkenyl radicals such as vinyl, allyl, and butenyl; and by aryl radicals such as phenyl, tolyl, and xylyl. R 5 is preferably hydroxyl radical or a C 1 to C 8 monovalent hydrocarbon radical. With regard to the subscripts, a and c each have values from 0 to 1,000, b and d each have values from 1 to 100, and c + d is from 3 to 1,100. The preferred cyclic organosiloxanes are those in which c is from 0 to 30, d is from 1 to 30, and c + d is from 3 to 30. The imidazolinyl-functional organosiloxanes are specifically exemplified by organosiloxanes with the following formulas: The method for preparing our imidazolinyl-functional organosiloxanes is a dehydration reaction between (A) an amino-functional organosiloxane and (B) an aliphatically unsaturated monocarboxylic acid. For example, straight chain imidazolinyl-functional organosiloxanes use as the starting siloxane, (A) an amino-functional organosiloxane of the general formula Cyclic imidazolinyl-functional organosiloxanes use as the starting siloxanes, (A) a cyclic amino-functional organosiloxane with the general formula In the preceding formulas R 1 , R 2 , R 4 , R 5 , a , b , c , and d are defined as above. The subject amino-functional organosiloxanes are synthesized, for example, by the alkali-catalyzed equilibration polymerization of such precursors as amino-functional cyclosiloxane and organo-cyclosiloxane using endblockers such as water and hexaalkyldi-siloxane where endblocking is desired. Amino-functional organosiloxanes of (A) encompass organosiloxanes exemplified by the following formulas: The carboxylic acid used as component (B) has the general formula R 3 COOH, wherein R 3 is a C 2 to C 50 aliphatically unsaturated monovalent hydrocarbon radical exemplified by vinyl, allyl, butenyl, heptadecenyl, and heptadecadienyl. The subject carboxylic acid is exemplified by acrylic acid, methacrylic acid, oleic acid, linoleic acid, linolenic acid, and ricinoleic acid; by drying oil fatty acids; and those obtained by the hydrolysis of a drying oil. Drying oil fatty acids are exemplified by soybean oil fatty acids, dehydrated castor oil fatty acids, tall oil fatty acids, linseed oil fatty acids, and tung oil fatty acids. The drying oil fatty acids are mixtures of carboxylic acids having the formula R 3 COOH and may also contain some saturated carboxylic acids as found in such drying oil hydrolysis products. The use of drying oil fatty acids is preferred when the imidazolinyl-functional organosiloxane of the present invention is used as an additive for modifying the surface of cured products from RTV organopolysiloxane compositions. The imidazolinyl-functional organosiloxanes are obtained by a dehydration reaction between components (A) and (B). Straight-chain amino-functional organosiloxanes are used as component (A) when straight-chain imidazolinyl-functional organosiloxanes are desired. Cyclic amino-functional organo-siloxanes are used as component (A) when cyclic imidazolinyl-functional organosiloxanes are used. The mixing ratio of components (A) and (B) in this method is preferably 0.5 mole of component (B) per 1 mole of amino group in component (A). Unreacted component (A) will remain when component (B) is used at less than 0.5 mole per 1 mole of amino group in component (A). While unreacted component (B) will remain when component (B) is used at more than 0.5 mole per 1 mole of amino group in component (A). The reaction temperature is preferably in the range from 100°C to 300°C, and more preferably in the range from 150°C to 250°C. The dehydration reaction does not go to completion at a reaction temperature below 100°C, which prevents synthesis of the imidazolinyl-functional organosiloxane. Undesirable secondary reactions become a possibility at temperatures in excess of 300°C. Organic solvent and dehydrating reagent may also be used in this preparative method insofar as the object of the present invention is not impaired. Toluene and xylene, which are already known for azeotropic dehydration, are advantageously used as an organic solvent. They are used in an amount that gives a reaction temperature in the range specified above. The dehydrating reagent is exemplified by molecular sieves and dicyclohexylcarbodiimide. Because our imidazolinyl-functional organosiloxanes are miscible with organopolysiloxane to make RTV organopoly-siloxane compositions, they are useful as an additive for improving the physical properties of room-temperature curable organopoly-siloxane compositions. They are particularly useful as an additive for improving the surface of cured products obtained from room-temperature curable organopolysiloxane compositions. The aliphatic unsaturation of R 3 in the imidazolinyl radical provides the anti-staining property of any RTV silicone composition containing it as an additive. This anti-staining property is believed to be based on the ease of oxidation and hydrolytic cleavage attributed to R 3 which provides hydrophilicity to the surface of cured, RTV silicone-sealant compositions. This hydrophilicity is achieved by the hydrolytic cleavage of the oxidized aliphatically unsaturated monovalent hydrocarbon radical R 3 . If a saturated monovalent hydrocarbon radical were to replace R 3 and such a imidazolinyl-functional organosiloxane were used as an additive to an RTV silicone-sealant composition, a hydrophilic surface is not formed on the resulting cured, RTV silicone-sealant surface and a self-cleaning and anti-staining property is also not observed. EXAMPLE 1 While operating under a dry nitrogen current, 249.9 g of straight-chain amino-functional organosiloxane with the formula (amino value as NH = 0.89 wt %) and 37.1 g of xylene were introduced into a one-L flask equipped with stirrer, thermometer, and water-measurement tube fitted with a reflux condenser and stirred. The resulting mixture was then heated to reflux at 160°C. Separately, 20.7 g of mixed fatty acid, Hy-Diene™, containing 58 weight percent of conjugated linoleic acid, 27 weight percent nonconjugated linoleic acid, 7 weight percent oleic acid, 5 weight percent ricinoleic acid, weight percent palmitic acid, and 1 weight percent stearic acid (neutralization value = 198.3, Hy-Diene™ is from KF Trading Company, Tokyo, Japan) was weighed into an addition funnel, which was then installed on the one-L flask. This mixed fatty acid was subsequently added dropwise over 1.3 hours at 160°C into the mixture of amino-functional organosiloxane and xylene. After addition completion, the dehydration reaction was completed by stirring for 4.6 hours at 160°C to 179°C, after which interval 2.0 ml of water had distilled into the water-measurement tube. The resulting reaction mixture was then cooled to room temperature, combined with 20 g of filtration aid (Radiolite™ 900 from Showa Kagaku Kogyo Kabushiki Kaisha, Tokyo, Japan) and 146.3 g toluene, stirred for 30 minutes, and finally subjected to fine filtration. After filtration, the solvent in the filtrate was stripped off at 70°C and 4.0 kPa (30 mmHg) for 1 hour and then at 72°C and 1.1 kPa (8 mmHg) to 80°C and 1.3 kPa (10 mmHg) for 4 hours to give 238.9 g of a straight-chain imidazolinyl-functional organosiloxane of the following formula: The -C 17 H 31 - radical shown in the above formula represents the reacted residue from the Hy-diene™ acid mixture as determined from the molecular weight. Analysis of this organosiloxane by infrared absorption spectroscopy confirmed the presence of the imino group signal at 1,620 cm -1 , see see attached Figure 1 . Analysis of this organosiloxane by 13 C-nuclear magnetic resonance analysis ( 13 C-NMR) confirmed the presence of the signal for the imino group carbon in the imidazoline ring at 167.1 ppm, see Figure 2 . EXAMPLE 2 While operating under a dry nitrogen current, 11.6 g of straight-chain amino-functional organosiloxane with the formula (amino value as NH = 0.89 wt %) 1.68 g soybean oil fatty acid mixture, and 1 g of xylene were placed in a one-half L flask equipped with stirrer, thermometer, and water-measurement tube fitted with a reflux condenser and stirred. A dehydration reaction was run by heating for 3 hours under reflux at 144°C to 155°C, after which interval 0.1 mL of water had distilled into the water-measurement tube. The reaction mixture was then cooled to room temperature, combined with 5 g of filtration aid (Radiolite 900™) and 10 g of toluene, stirred for 30 minutes, and finally subjected to fine filtration. After filtration, the solvent in the filtrate was stripped off at 70°C and 4.0 kPa (30 mmHg) for 1 hour and then at 72°C and 1.1 kPa (8 mmHg) to 80°C and 1.3 kPa (10 mmHg) for 2 hours to give 11.1 g of a straight-chain imidazolinyl-functional organosiloxane with the following formula: The -C 17 H 31 - radical shown in the above formula represents the reacted residue from the soybean fatty acid mixture as determined from the molecular weight. Analysis of the obtained organosiloxane by infrared absorption spectroscopy confirmed the presence of the imino group signal at 1,610 cm -1 , see Figure 3 . Analysis of the obtained organosiloxane by 13 C-NMR confirmed the presence of the signal for the imino group carbon in the imidazoline ring at 168 ppm, see Figure 4 . EXAMPLE 3 While operating under a dry nitrogen current, 103.8 g of cyclic amino-functional organosiloxane of the formula (amino value as NH = 18.2 wt %) and 41.5 g of xylene were introduced into a 0.3 L flask equipped with stirrer, thermometer, and water-measurement tube fitted with a reflux condenser and stirred. The resulting mixture was then heated to reflux at 145°C. Separately, 140.9 g of Hy-Diene™ was weighed into an addition funnel, which was then installed on the 0.3-L flask. This mixed fatty acid was subsequently added dropwise over 2.2 hours at 145°C to 154°C into the mixture of cyclic amino-functional organosiloxane and xylene. After addition completion, the dehydration reaction was completed by stirring for 5.3 hours at 154°C to 190°C, after which interval 18.0 mL of water had distilled into the water-measurement tube. The resulting reaction mixture was then cooled to room temperature, combined with 20 g filtration aid (Radiolite 900™) and 122.8 g of toluene, stirred for 30 minutes, and finally subjected to fine filtration. After filtration, the solvent in the filtrate was stripped off at 70°C and 4.0 kPa (30 mmHg) for 1.5 hours and then at 70°C and 1.1 kPa (8 mmHg) to 80°C and 1.3 kPa (10 mmHg) for 4 hours to give 207.1 g of a cyclic imidazolinyl-functional organosiloxane with the following formula: Analysis of he organosiloxane by infrared absorption spectroscopy confirmed the presence of the imino group signal at 1,610 cm -1 , see Figure 5 . Analysis of this organosiloxane by 13 C-NMR confirmed the presence of the signal for the imino group carbon in the imidazoline ring at 166.1 ppm, see Figure 6 . APPLICATION EXAMPLE 1 The following were mixed to homogeneity to give a room-temperature curable organopolysiloxane composition: 15 g of the imidazolinyl-functional organosiloxane prepared in Example 1, 85 g of alpha,omega-dihydroxypolydimethylsiloxane with a viscosity at 25°C of 18 Pa.s, 100 g of precipitated calcium carbonate, 0.3 g of dibutyltin octoate, 1 g of surfactant, and 16.3 g of methyltris(methyl ethyl ketoxime)silane. This organopolysiloxane composition was filled into a joint (width = 20 mm, and depth = 10 mm) formed by abutting 2 white ceramic boards. Curing at 25°C for 5 days then yielded a test panel. This test panel was thereafter held outdoors at an inclination of 75° with the joint on the upper side, and the development of staining on the ceramic board in the vicinity of the joint was examined over a 2-month period. Almost no staining was observed even after the 2 months had elapsed. In addition, the room-temperature curable organopolysiloxane composition itself was held for 3 months at 25°C and its appearance was then inspected: no separation or sedimentation was observed. For purposes of comparison, another room-temperature-curable organopolysiloxane composition was prepared as above, but omitting the 15 g imidazolinyl-functional organosiloxane from Example 1. The postcure behavior of this organopolysiloxane composition was evaluated as above, and staining was observed on the ceramic board after 1 week.

Claims: An imidazolinyl-functional organosiloxane comprising from 2 to 1,100 siloxane units where at least one siloxane unit has an imidazolinyl radical of the following general formula bonded to silicon wherein R 1 is a C 1 to C 50 divalent hydrocarbon radical, each R 2 is selected from hydrogen atom or a C 1 to C 50 monovalent hydrocarbon radical, and R 3 is a C 2 to C 50 monovalent hydrocarbon radical with aliphatic unsaturation. The imidazolinyl-functional organosiloxane according to claim 1 where the organosiloxane has the following general formula wherein R 1 , R 2 , and R 3 are as defined in claim 1, each R 4 is a C 1 to C 50 monovalent hydrocarbon radical, each R 5 is selected from hydroxyl radical or a C 1 to C 50 monovalent hydrocarbon radical, a is from 0 to 1,000, and b is from 1 to 100. The imidazolinyl-functional organosiloxane according to claim 2 in which R 1 is a C 1 to C 8 divalent hydrocarbon radical, R 2 is hydrogen atom, R 3 is a C 10 to C 20 monovalent hydrocarbon radical with aliphatic unsaturation or a mixture thereof, R 4 is a C 1 to C 8 monovalent hydrocarbon radical, and R 5 is a hydroxyl radical or a C 1 to C 8 monovalent hydrocarbon radical. The imidazolinyl-functional organosiloxane according to claim 3 in which R 1 is-C 3 H 6 -, R 3 is -C 17 H 31 -, R 4 and R 5 is methyl radicals. The imidazolinyl-functional organosiloxane according to claim 1 where the siloxane has the following general formula wherein R 1 , R 2 , and R 3 are as defined in claim 1, each R 4 is a C 1 to C 50 monovalent hydrocarbon radical, c is from 0 to 1,000, d is from to 100, and c + d is from 3 to 1,100. The imidazolinyl-functional organosiloxane according to claim 5 in which R 1 is a C 1 to C 8 divalent hydrocarbon radical, R 2 is hydrogen atom, R 3 is a C 10 to C 20 monovalent hydrocarbon radical with aliphatic unsaturation or a mixture thereof, R 4 is a C 1 to C 8 monovalent hydrocarbon radical, c is 0 to 30, d is 3 to 30, and c + d is from 3 to 30. The imidazolinyl-functional organosiloxane according to claim 5 in which R 1 is-C 3 H 6 -, R 3 is -C 17 H 31 -mixture, R 4 is methyl radical, and R 5 is methyl radical. A method for preparation of an imidazolinyl-functional organosiloxane comprising a dehydration reaction between (A) an amino-functional organosiloxane with the general formula wherein R 1 is a C 1 to C 50 divalent hydrocarbon radical, each R 2 is selected from hydrogen atom or a C 1 to C 50 monovalent hydrocarbon radical, each R 4 is a C 1 to C 50 monovalent hydrocarbon radical, each R 5 is selected from hydroxyl radical or a C 1 to C 50 monovalent hydrocarbon radical, a is from 0 to 1,000, and b is from 1 to 100 or an amino-functional organosiloxane with the general formula wherein R 1 , R 2 , and R 4 are defined above, c is from 0 to 1,000, d is from 1 to 100, and c + d i s from 3 to 1,100 and (B) a carboxylic acid with the general formula R 3 COOH wherein R 3 is a C 2 to C 50 monovalent hydrocarbon radical with aliphatic unsaturation.

Inventors: NAKASHIMA HISATAKA, NAKASHIMA, HISATAKA, Nakashima, Hisataka, Dow Corning Toray Sil. Co.Ltd
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE COMPANY LTD.
Application year: 1995
Main classification: C08G77
IPC codes: C08G77, C07F7