Preparation of triorganotin lithium compositions, the compositions and their use as initiators

Abstract: Solutions of triorganotin lithium are described having low residual concentrations (preferably less than 2,000 ppm) of halide. These are produced by a two-step process. Triorganotin halide is reacted with lithium to produce hexaorgano ditin and a precipitate of lithium halide. The lithium halide precipitate is removed by filtration and/or use of highly concentrated reaction conditions. Then the hexaorgano ditin is further reacted with lithium to form the triorgano substituted tin lithium. The lithium halide is less soluble in hot tetrahydrofuran (THF) and/or more concentrated solutions. THF is a preferred solvent for the reaction. The low-temperature reactions described result in low amounts of inactive and/or undesirable byproducts. These triorganotin lithium compounds are useful as anionic initiators that result in polymers with terminal tin compounds, e.g., triorganotin, attached to the terminal end of the polymer where initiation occurred. The polymers with terminal tin compounds have lower hysteresis in cured carbon black-filled elastomeric compounds. Low concentrations of residual halides in the initiators and consequently in the polymers has been associated with reduced amounts of volatile organotin compounds being generated during processing of polymers with organotin terminal groups.

Description: Preparation of a triorgano substituted-tin lithium solution having low residual lithium halide content made by a two step process is disclosed. The organotin lithium can be used to initiate the polymerization of anionically initiated elastomers such as polydienes and copolymers of dienes and vinyl aromatic monomers. The polymers initiated with this initiator have triorgano substituted-tin end groups which react with carbon black fillers. This reaction can give cured carbon black filled elastomers with lower hysteresis, higher rebound, and less heat build-up than in similar polymers made with butyl lithium initiators. U.S. Patent 3,426,006 discloses tin containing organo-metal initiators made by reactions from 1 mole of stannous chloride with 3 moles of alkyl lithium (column 5, lines 29-38). These initiators are then used to form colorless polymers. This initiator type has been shown by Tamborshi et al., Journal of Organic Chemistry , Vol. 28, page 237 (1963) to be predominantly an equilibrium mixture of dibutyltin and butyl lithium wherein the butyl lithium is the more active initiator and hence, only of a few of the polymer chains produced from its initiation actually contain tin atoms. U.S. Patent Application 07/636,961 filed June 2, 1991, which is published European Application 493839 of July 8, 1992, discloses several alternate ways to make triorgano substituted-tin lithium initiators and their use to make organotin terminated polymers with reduced hysteresis. The initiators disclosed therein had higher residual ionic chloride concentration than claimed herein or were made with a more expensive distillation process which results in undesirable tetrabutyltin and/or tributyltin hydride impurities. US-A-3699138 discloses the reaction of trialkyltin halide with molten sodium metal in order to produce a distannane. The reaction is carried between 100 and 220°C and no solvent is used. The paper entitled "Organic Sonochemistry. Ultrasound promoted coupling of chlorosilanes in the presence of lithium wire" (Tetrahedron 22 (1981), 381323814) discloses the use of ultrasound promoted coupling of chlorosilanes and the ultrasound promoted coupling of organo metal chlorides. In general terms, we propose a process in which triorgano-substituted tin halide is reacted with lithium, preferably with a (generally slight) excess of lithium, to give a hexaorgano-substituted ditin compound (and lithium halide, which is separated e.g. by filtration). The ditin compound can then be reacted in a further step with lithium to produce a triorgano-substituted tin lithium. High yields may be achieved. Lithium halide content in the product can be low. Good separation of lithium halide can be assisted by e.g. lower solubility of LiX in warmer THF solutions of the ditin product; low level of solvating solvent (e.g. THF) relative to the R 3 SnX reactant; e.g. 35-80wt% of the concentrated product before separation; use of non-solvating e.g. alkane-type solvents to wash hexaorgano ditin and other solvent off separated LiX. In a first aspect as claimed in claim 1, the invention provides a process for producing a solution of triorgano-substituted-tin lithium comprising the steps of: (a) reacting triorgano-substituted-tin halide - wherein the organo groups are alkyl or cycloalkyl of 1 to 12 carbon atoms or aryl or alkyl substituted aryl having from 6 to 16 carbon atoms and the halide is chloride, iodide, or bromide - with lithium metal at a molar ratio of lithium metal to triorgano-substituted-tin halide of between 1.0 and 1.5, in the presence of solubilizing solvent with a mole ratio of said solubilizing solvent to said triorgano-substituted-tin halide of less than 3, forming a solution primarily of hexaorgano-substituted ditin and a lithium halide precipitate; (b) removing the lithium halide precipitate, and (c) combining the hexaorgano-substituted ditin solution with additional lithium metal and solubilizing solvent, at a mole ratio of lithium to hexaorgano-substituted ditin from 2 to 6, and reacting the hexaorgano-substituted ditin with the additional lithium metal forming triorgano-substituted-tin lithium in said solubilizing solvent, with a mole ratio of said solubilizing solvent to the triorgano-substituted-tin lithium of 3 or greater. A second aspect as claimed in claim 13 relates to the first reaction step described above, and is a process for producing a solution of hexaorgano-substituted ditin comprising: combining a triorgano substituted-tin halide with lithium metal with a molar ratio of lithium metal to triorgano-substituted-tin halide of between 1.0 and 1.5 to form lithium halide and a solution primarily of hexaorgano- substituted-ditin, in one or more solubilizing solvents in amounts such that the mole ratio of said solubilizing solvent to triorganotin halide is less than 3, and removing the lithium halide which precipitates from the hexaorgano-substituted-ditin, whereby the resulting hexaorgano-substituted-ditin contains less than 3000 ppm chloride based on the hexaorgano-substituted-ditin. The triorgano substituted-tin lithium products may then be used as initiators to make elastomers with one or more trialkyltin functionalized ends. These polymers with tin functionalized ends can be formulated with carbon black into rubber products having reduced hysteresis. See claim 12. The triorgano substituted-tin lithium initiators with low residual halide concentrations made by this process have low levels of organotin by-products such as tetrabutyltin. Polymers initiated with triorgano-substituted-tin lithium having high residual chloride, e.g. lithium chloride, levels are known to produce organotin chlorides during processing and compounding. These tetrabutyltins and organotin chlorides are volatile. The volatile organotin compounds are objectionable in the work place and are regulated and limited by the Occupational Safety and Health Act (OSHA). The two-step process offers an economically viable way to make triorgano substituted-tin lithium initiators with good activity and low residual halide concentrations. FURTHER EXPLANATIONS; OPTIONS AND PREFERRED FEATURES We find that the process can be used to produce a solution of triorgano substituted-tin lithium (R 3 SnLi) in a pure form at approximately 10-55 wt. % active initiator with less than about 3,500, desirably less than 3000; preferably less than 2500 or 2000, more preferably from 100 or 200 to less than 1500 ppm of halide ions (such as Cl - ) based on the active organo substituted-tin lithium. The chloride content can be measured by ion chromatography. The residual lithium halide concentration from prior art disclosures of tin lithium initiators made from triorgano substituted-tin chloride averages more than 4,000 ppm Cl - based on the active organotin. Desirably the triorgano substituted lithium or the hexaorgano ditin have low levels of tetraorganotin (e.g., less than 20, 15, 10, or 5% by wt. based on the active initiator wt.) and low levels of triorganotin hydride (e.g., less than 10, 6.0, or 4.0 by wt. based on the active initiator wt.). Desirably the R 3 SnLi species are 90 or 93 wt. % or more of all tin containing species present in the initiator. These tin lithium compounds are useful as anionic initiators that result in polymer (elastomer) chains where at least one terminal chain end (the terminus where the initiation of polymerization occurred) has a triorgano substituted-tin group (R 3 Sn)-. When the tin lithium disassociates to start polymerization, the triorgano substituted-tin anion adds to the monomer unit to form a carbon anion while the lithium atom becomes the counter ion which associates with the growing chain end. When there are lithium halides present in the tin lithium initiator, they can be carried along in the anionic polymerization and will be present in the polymer and subsequently in the compounded elastomer. Lithium halides, especially lithium chloride, can further react with the triorgano substituted tin terminated polymer and carbon black to produce the original triorganotin chloride which has an undesirable odor. Furthermore, the produced R 3 SnCl, especially Bu 3 SnCl, is an environmental concern during processing of the compounded polymer stocks. Similar results are anticipated with potassium or sodium instead of lithium metal. Varying amounts of sodium metal can be used with lithium. The triorgano substituted-tin lithium compounds are made from the reaction of triorgano substituted-tin halides (R 3 SnX) with lithium metal (or optionally with partial substitution with sodium metal) in solvents inert towards the lithium metal. Examples of particularly effective solvating or solubilizing solvents are tetrahydrofuran (THF); ethers such as dimethyl ether, diethyl to diamyl ether, tetramethylene ethylene diamine; glymes such as monoglyme, ethyl glyme, diglyme, ethyl diglyme, triglyme, butyl diglyme, tetraglyme; or other diethers. THF is a highly preferred solvating or solubilizing solvent. Other solvents such as alkanes of 5-20 carbon atoms (such as hexane) may be used as a diluent. These alkane solvents are particularly beneficial to rinse useful reactants from the LiCl filter cake. Because LiCl is very insoluble in alkanes this rinse solvent minimizes the amount of LiCl carried forward from filtration steps. It is estimated that the LiCl filter cake may retain 10-15 wt. % of the active hexaorgano ditin prior to rinsing. These alkane solvents are not solubilizing solvents in this specification. The organo groups (R) of the tri, tetra and hexaorgano species can independently be alkyls including cyclic alkyls having from 1 to 12 carbon atoms or aryls or alkyl substituted aryls having from 6 to 15 carbon atoms. More desirably, the organo groups can be alkyls having from 2 to 8 carbon atoms, and most desirably, the organo groups are butyl groups. The halides (X) can be chloride, iodide, or bromide, (Cl - , I - , Br - ) and are more desirably chloride. The triorgano substituted-tin lithium (initiator) is desirably a solution. The concentration of the initiator can be from about 0.001% to about 58%, desirably from about 10 to about 50 or 55%, and preferably from about 20 or 30 to about 50 or 55% by weight of the solution. The process to produce triorgano substituted-tin lithium is desirably conducted in equipment inert to the lithium metal. Examples of suitable materials include polyethylene, polypropylene, stainless steel, and glass-lined materials. The reactions are desirably conducted under an atmosphere inert to lithium such as helium or argon gas, and preferably argon gas. Trace amounts of moisture from all components are minimized by drying procedures such as drying the THF over calcium hydride. The process to make triorganotin lithium is desirably conducted in two separate steps with a filtration step in between and optional further filtration after the last step. First Step In the first step, triorganotin chloride is reacted with a near stoichiometric amount of lithium metal to form a concentrated solution of hexaorgano ditin. It is desirable that the reaction proceed only to the hexaorgano ditin in the first step to facilitate removal of the Cl - ions. The molar ratio of lithium to the triorgano substituted-tin halide can be from about 1.0 to about 1.5, desirably from about 1.0 to about 1.20, and preferably from about 1.0 to about 1.10 in the first step. Only a trace of the triorganotin lithium is found when near stoichiometric amounts of lithium metal are added. Small amounts of Na in the lithium metal was found to increase the reaction rates. The lithium metal used may be excess or recycled lithium recovered from the second step. The solubilizing solvent is not essentially present during the first step to solubilize the reactants or the products but it is convenient to use it in small amounts and it may help keep the lithium metal surface clean and reactive. The mole ratio of solubilizing solvent: triorganotin halide is up to 3 and more desirably is from 0.5 to 2.0 and preferably is from 0.8 to 1.5. The higher mole ratio of solubilizing solvent to tin chloride allow the solubilization of more LiCl. Therefore we keep the mole ratio of solvent to tin chloride low i.e. 3 or less to form hexaorgano substituted ditin in concentrated solutions with respect to the solubilizing solvent resulting in low concentrations of soluble LiCl. The reaction temperature can vary widely depending upon the amount of time available for the reaction. The rate of addition of the lithium metal to the triorganotin chloride or vice versa is limited by the cooling capacity of the reactor. Desirable reaction temperatures are from about 0 to about 65°C, desirably 5 to 40°C, and preferably from about 5 to about 15°C to minimize the occurrence of side reactions that may lower yields or result in other reaction products. Any triorganotin lithium formed is believed to react with additional triorganotin chloride to form hexaorgano ditin. The reaction desirably proceeds to 100% conversion of the triorganotin chloride producing hexaorgano substituted-ditin compounds (R 3 Sn-SnR 3 ) in about 90 to 100% yield along with lithium chloride. The insoluble lithium chloride results in crystals whose size can be optimized for filtration ease. The ditin solution can be up to 70 or 80 wt. % solids and is filtered to remove the lithium halide by-product. Several washes with heptane or other hydrocarbons may be used on the cake and the solvents included in the product. The lithium halide may be recycled to recover the lithium. The lithium halides (especially lithium chloride) were unexpectedly found to be less soluble in hot THF than cold THF. Thus, the amount of soluble halide can be limited by keeping the solvent temperature high immediately prior to and during filtration. Consequently, it is desirable to keep the ditin solution in THF from about 10 or 20 to 70°C and preferably about 30 to 65°C during the filtration to minimize the amount of soluble lithium halide carried forward into the second step of the reaction. The chloride:product ratios at this stage of the reaction are similar to the chloride:product ratios in the final product. The use of alkanes as partial replacement for the solubilizing solvents also minimizes the soluble LiCl. Second Step In the second step, the hexaorgano ditin which is typically present in concentrations up to 70 or 80 wt. % in the solution, is desirably added to a slurry of lithium metal in additional solvating solvent (preferably THF). This order of addition minimizes side reactions of the hexaorgano ditin. Total addition and reaction times desirably vary from 5 to 16 hours depending on the particular equipment and its limitations. Longer times tend to result in more undesired by products. This gives a concentration desirably of from about 10 to 50 wt. %, more desirably about 20 to 40 wt. % of active final product. Two moles of lithium react with one mole of hexaorgano ditin to form 2 moles of triorganotin lithium. An excess of from 10 to 105% of lithium helps to speed the reaction of hexaorgano ditin with lithium. The mole ratio of lithium to the ditin is from 2 to 6, more desirably from about 2.0 to 5.0, and preferably from about 2.0 to about 4.2. A Gilman titration can be used to determine the amount of active lithium present in the final product. Desirable reaction temperatures are from about 0 to about 65°C, more desirably from about 5 to about 40°C, still more desirably from about 5 to about 25, and preferably from about 10 to about 15°C. Lower temperatures during this reaction have been found to minimize the formation of organotin by-products such as tetrabutyltin and tributyltin hydride. The reaction product may be filtered to remove the unreacted lithium metal which can be used for a subsequent batch in the first step. The filtrate is a triorgano substituted-tin lithium initiator. The filter cake is rinsed with hydrocarbon solvent or solubilizing solvent and the rinse is optionally combined with product. The mole ratio of solubilizing solvent to organo substituted-tin lithium in this step and the final product is 3 or more and more desirably 3 to 6. These ratios are desirable in that they are sufficient to solubilize the tin species but are not unnecessarily dilute. The triorganotin lithium has utility for initiating the anionic polymerization of monomers capable of anionic polymerization. The triorganotin lithium is also useful as an intermediate in the synthesis of other compounds, particularly in the synthesis of pharmaceutical products. The monomers include compounds having at least one carbon-carbon double bond which is capable of polymerization through the double bond. Other monomers can include cyclic ethers and lactones that polymerize through ring opening reactions. Suitable monomers include dienes having from 4 to 12 carbon atoms (preferably conjugated dienes), monovinyl aromatic monomers having from 8 to 18 carbon atoms and trienes. In copolymers of dienes and monovinyl aromatics, the weight ratios of conjugated diene to aromatic vinyl monomers are desirably from 95-50:5-50, preferably 95-55:5-45. These triorgano substituted-tin lithium compounds can be used as initiators to make elastomeric polymers with one or more trialkyltin functionalized ends. These polymers with tin functionalized ends can be formulated with carbon black in elastomeric products with reduced hysteresis. One source of increased hysteresis in elastomers during flexing is the section of the polymer chain from the last crosslink of the vulcanizate to the end of the polymer chain. The free polymer chain end cannot elastically store energy. As a result, the energy transferred to this polymer chain end is lost as heat. One method to reduce this type of hysteresis energy loss is to create a polymer chain end with terminal tin groups. Tin has an affinity for carbon black reinforcing fillers and chemically reacts with the quinone functionality present on carbon black. This reaction of the tin-terminated polymer chain end with carbon black is believed to reduce hysteresis. This is further explained in an article in Rubber Chemistry and Technology, 1990, vol. 63, no. 1, by F. Tsutsumi et al. entitled "Structure and Dynamic Properties of Solution SBR Coupled with Tin Compounds" pp 8-22. . Cured carbon black filled polymer compositions are useful in many applications requiring low heat buildup during flexing. One such application is in tires where rolling resistance is reduced due to lower hysteresis. Polymerizations using these initiators are usually conducted in conventional hydrocarbon solvents for anionic polymerizations such as hexane, cyclohexane, benzene and the like. A polymerization terminating agent can be used to functionalize the chain end where termination occurs. Active terminating agents include compounds having abstractable hydrogen atoms such as water or alcohol. The growing chain ends can be functionalized or coupled to other species with compounds providing terminal functionality. These include tin tetrachloride, R 3 SnCl, R 2 SnCl 2 , RSnCl 3 , carbodiimides, N-methylpyrolidine, cyclic amides, cyclic ureas, isocyanates, Schiff bases, 4,4'-bis(diethyl amino) benzophenone, and other functionalizing agents well known to the art, wherein each R group is individually alkyls having from 1 to 20 carbon atoms, cycloalkyls having from 3 to 20 carbon atoms, aryls having 6 to 20 carbon atoms, or aralkyls having 7 to 20 carbon atoms. Preferred terminating or coupling agents for this application are various tin alkoxides of the formula R x Sn(OR) 4-x where x is from 0 to 3 and each R group can be the organo group described above and preferably the R groups are limited to lower alkyls (i.e., 1 to 8 carbon atoms). These tin containing compounds are preferred in that they help minimize the amount of chloride contaminants retained by the polymer. As previously explained, the chloride contaminants contribute to the production of volatile organotin by-products from the organotin terminated polymers. Anionic polymerizations using the triorgano substituted-tin lithium initiators can be conducted according to polymerization techniques well known to the art. The mole ratio of initiator to monomers limits the molecular weight in the absence of chain transfer or chain termination reactions. The monomer can be added batchwise or incrementally. Lower polymerization temperatures tend to minimize chain transfer and termination reactions. Polar coordinators may be added to control the vinyl content in diene polymerizations or to aid in randomization in copolymerizations. Amounts of polar coordinators may range from 0.001 to 90 or more equivalents per equivalent of lithium. Compounds useful as polar coordinators include tetrahydrofuran, linear and cyclic oligomeric oxolanyl alkanes such as 2,2'-di(tetrahydrofuryl) propane, di-piperidyl ethane, hexamethylphosphoramide, N,N'-dimethylpiperazane, diazabicyclooctane, dimethyl ether, diethyl ether, tributylamine and the like. The linear and cyclic oligomeric oxolanyl alkane modifiers are described in U.S. Patent No. 4,429,091, which is hereby incorporated by reference. Other polar coordinators include compounds having an oxygen or nitrogen heteroatom and a non-bonded pair of electrons. Examples include dialkyl ethers of mono and oligo alkylene glycols; "crown" ethers; tertiary amines such as tetramethylene diamine (TMEDA); tetrahydrofuran (THF), THF oligomers, alkylated versions of THF and the like. The polymers produced with a triorganotin lithium initiator as described herein as the sole initiator are found to have essentially one or more organo substituted-tin group per polymer chain with said essentially one group being derived from the initiator. If an organo substituted-tin terminating agent or a coupling agent is used, the molar ratio of triorganotin to polymer chains can be above 1.60:1, desirably above 1.80:1, and preferably above 1.95:1. The triorganotin compound (R 3 Sn-) is the first unit of the polymer chains initiated by these initiators. The growing polymer chain thus has the structure R 3 Sn-(repeat unit)-Li+. The growing anionic chain end can then be functionalized as described above. The residual halogen in the polymer is less than 3500 ppm; and preferably less than about 2500 or 2,000 ppm; and more preferably from about 100 or 200 to 1500 ppm based on the wt. of the triorganotin groups due to the low concentration of residual halogen, desirably Cl - ' in the initiator of this invention. We find that triorgano substituted-tin lithium initiators made as described are very stable to loss of initiator activity with storage. Butyl lithium stored in THF in a sealed glass ampoule loses activity as an initiator during storage. The triorganotin lithium initiators dissolved in THF and stored in glass ampoules at temperatures from 20°C up to 35°C maintain their activity without measurable losses for periods of six months or more. We find that triorgano substituted-tin compounds made as described have low amounts of organotin by-products due to the mild reaction conditions used, such as low temperatures. One example of such effect is that the initial tributyl substituted-tin lithium produced had from 8 to 10 mole % tetrabutyltin as a contaminant in the product. This contaminant contributes to the volatile organotin in the air and doesn't function as an initiator. By controlling the reaction conditions, tributyl substituted-tin lithium samples can be made having only 2 or 3 mole percent of tin in the tetrabutyl tin form. It is anticipated that distilling the hexaorgano ditin would result in substantial amounts of tetrabutyltin relative to the hexaorgano ditin made in the first step. The polymers initiated with the triorganotin lithium initiators find use in compounded rubber stocks. The organotin groups on the ends of the polymer can chemically react with function groups such as quinones on the carbon black used in many rubber stocks. This chemical reaction between the polymer chain ends and the carbon black reduces hysteresis in the cured rubber stock. In applications such as tire applications where there is a constant flexing of the rubber, this can reduce rolling resistance and minimize heat buildup. EXAMPLE 1 The above process may be better understood by the following example. 6.89 kg of tri-n-butyltin chloride was reacted in 1.8 kg of tetrahydrofuran (THF) with 0.187 kg of lithium metal. A finely divided or powdered lithium metal reacts more quickly than large solid portions. This reaction takes about 2 hr. with stirring at 15-35°C. The insoluble lithium halide in the reaction product (present as a precipitate) is removed by hot filtration, e.g. 55°C from the solution of hexa-n-butyl-di-tin in THF. The LiCl can be washed free of tin (Sn) compounds with pentane or heptane and then recycled to recover the Li. The filtered solution of hexa-n-butyl-di-tin is gradually added to a reactor containing enough THF (about 3.6kg) to have a 3:1 mole ratio of solvent to triorganotin lithium and 0.35 kg of lithium metal. This reacts for about 4 hours at a temperature of 25-50°C to form a solution of lithium tri-n-butyl tin in THF. This is filtered again to remove any excess lithium metal present and any non-soluble tin containing by-products. EXAMPLE 2 First Step A stirred tank reactor is purged with argon charged with 5.9 kg (13 pounds) (1.87 lb-moles) lithium metal dispersion and 77.1 kg (170 lbs) (2.36 lb-moles) tetrahydrofuran (THF). (The lithium metal contained 0.5% sodium metal.) The lithium metal dispersion may either be a fresh charge or the excess metal filtered from the second reaction step and recycled to the first step. The stirred slurry is maintained at 10-15°C while 259 kg (570 pounds) of tri- n -butyltin chloride (1.75 lb-moles) is added over a period of 8-10 hours. The reaction is noticeably exothermic and proceeds rapidly. (The rate of addition is a function of the cooling capacity of the reactor.) After the addition is completed, the reaction mass is stirred an additional hour before allowing the temperature to rise to room temperature over a two hour period. It may then be filtered. The reaction slurry is then filtered to remove the lithium chloride which formed in the reaction. The filter cake is washed twice with heptane to remove the residual hexabutyl ditin and THF. These washings are combined with the THF filtrate containing hexabutyl ditin to provide the feed for the second step reaction. The yield to the hexabutyl ditin product is about 85 to 95%. The chloride content of the solution is less than 2000 ppm with a hexabutyl ditin concentration of about 70-80% by weight. Second Step A stirred tank reactor is purged with argon and charged with 10 kg (22 pounds) of lithium metal (0.5% wt. sodium) and 152 kg (334 pounds) of THF. The stirred slurry is cooled to 5-15°C and maintained at this temperature while the combined filtrate from the first step is added over 6-8 hours. The reaction is mildly exothermic during the first half of the reaction. The reaction slurry is stirred an additional four hours after the addition is complete at 10-15°C. The reaction slurry is then allowed to warm up to ambient temperature over two hours and then stirred several additional hours. The product slurry is then filtered and the filter cake washed with heptane which is combined with the product solution. The final product solution contains about 30-35% lithium tri- n -butyltin at an overall yield of 76-80%. The filter cake consisting primarily of lithium metal can be recycled to be the lithium charge for step one. EXAMPLE 3 Since there is a concern about the volatile organotin compounds that may be generated during compounding and curing of the polymers made using triorgano substituted-tin lithium initiator, an experiment was set up to determine the effect of Cl - in a tributyl substituted-tin lithium (TBTL) on the amount of extractable Bu 3 SnCl in a cured rubber sample. The experimental procedure is described below and the data is summarized in Table I. To a 2 gal. (7.6 1) stainless steel reactor was added 2.02 lbs. (916 g) of 33% styrene in hexane and 7.00 lbs. (3.18 kg) of 24.5% butadiene in hexane. After cooling to 55°F (13°C) from 1.0 to 1.5 millimoles of 2,2'-ditetrahydrofuryl propane and 8.7 to 10.9 millimoles of an approximately 50 wt. % tributyltin lithium (TBTL) in THF were added. The temperature was held at 55°F (13°C) for 1.5 hrs. before increasing to 70°F (21°C) and then every 15 minutes increasing another 10°F (5.6°C) until 120°F (49°C) was reached. A 4.0 lbs. (1.8 kg) sample was removed and terminated with isopropyl alcohol and dibutyl para-cresol (DBPC) was added an antioxidant. The polymer was analyzed for its ML 4 @ 212°F (100°C), % styrene, % vinyl PBD and Tg which are listed in the attached Table I. Polymer Sample # ppm Cl - in TBTL initiator Bu 3 SnAm ppm ML 4 100°C Styrene % PBD %V Tg (°C) 1 6325 819 57.4 20.7 61.2 -36.2 2 3770 450 10.3 21.8 78.4 -18.8 3 2425 466 27.3 28.4 57.9 -29.9 4 2425 645 9.4 30.7 55.8 -31.3 5 830 90.1 78.4 27.4 63.4 -21.4 6 830 128 23.6 30.1 55.7 -24.1 7 830 185 26.9 31.1 56.4 -23.2 8 40 55.0 30.5 30.0 56.0 -26.3 9 40 114 16.2 29.2 56.0 -26.4 10 40 55.4 82.2 29.5 54.5 -26.6 Test plaques were produced by compounding 100 parts of this rubber in a Brabender with 50 phr carbon black, 3 phr zinc oxide, 1 phr antioxidant, 1-8 phr sulfur, 2 phr stearic acid, and 1 phr of accelerator and then curing for 30 min. at 300°F (149°C). Extraction with hexane, treatment of the extract with amyl magnesium bromide (AmMgBr) and analysis by GC using a flame photometric detector and a tetrapropyltin (Pr 4 Sn) internal standard allowed the determination of extractable tributyltin chloride (Bu 3 SnCl) measured as Bu 3 SnAm. Table I shows lower concentrations of Bu 3 SnCl were formed when the concentration of Cl - was less than 2000 ppm based on the weight of the initiator.

Claims: A process for producing a solution of triorgano-substituted-tin lithium comprising the steps of: (a) reacting triorgano-substituted-tin halide - wherein the organo groups are alkyl or cycloalkyl of 1 to 12 carbon atoms or aryl or alkyl substituted aryl having from 6 to 16 carbon atoms and the halide is chloride, iodide, or bromide - with lithium metal at a molar ratio of lithium metal to triorgano-substituted-tin halide of between 1.0 and 1.5, in the presence of solubilizing solvent with a mole ratio of said solubilizing solvent to said triorgano-substituted-tin halide of less than 3, forming a solution primarily of hexaorgano-substituted ditin and a lithium halide precipitate; (b) removing the lithium halide precipitate, and (c) combining the hexaorgano-substituted ditin solution with additional lithium metal and solubilizing solvent, at a mole ratio of lithium to hexaorgano-substituted ditin from 2 to 6, and reacting the hexaorgano-substituted ditin with the additional lithium metal forming triorgano-substituted-tin lithium in said solubilizing solvent, with a mole ratio of said solubilizing solvent to the triorgano-substituted-tin lithium of 3 or greater. A process according to claim 1 wherein the halide precipitate is removed by a filtering step. A process according to claim 2 wherein the filtering step is carried out at a temperature from 10 to 70°C. A process according to claim 3 wherein the filtering step is carried out at from 30 to 65°C and said solubilising solvent is tetrahydrofuran. A process for producing a solution of triorgano-substituted-tin lithium according to any one of claims 1 to 4 wherein said solubilizing solvent of said solution is primarily tetrahydrofuran, and wherein the halide is chloride. A process according to any one of claims 1 to 5 in which the reaction temperature in step (c) is from 5 to 40°C. A process according to claim 6 in which the reaction temperature in step (c) is from 5 to 25°C. A process according to any one of the preceding claims wherein in step (a) said mole ratio of solubilising solvent to tin halide is from 0.5 to 2.0. A process according to any one of claims 2 to 8 in which after the filtering step the filter cake of lithium halide is rinsed with hydrocarbon solvent to recover hexaorgano ditin product for inclusion with the rest. A process for producing a solution of triorgano-substituted-tin lithium according to any one of the preceding claims, further including a step of filtering said triorgano-substituted-tin lithium solution to remove unreacted lithium and insoluble tin compounds. A process according to any one of the preceding claims wherein the organo groups are alkyl of 2-8 carbon atoms. A process for anionically polymerizing a polymer to be compounded as a carbon black-filled elastomer, said process comprising: preparing a solution of triorgano-substituted tin lithium initiator by a process according to any one of claims 1 to 11, and reacting the triorgano-substituted-tin lithium initiator with at least one diene monomer and optionally monovinyl aromatic monomer, forming a polymer with triorgano-substituted-tin groups on at least one end, wherein said diene has from 4 to 12 carbon atoms and said monovinyl aromatic monomer if present has from 8 to 18 carbon atoms. A process for producing a solution of hexaorgano-substituted ditin comprising: combining a triorgano substituted-tin halide with lithium metal with a molar ratio of lithium metal to triorgano-substituted-tin halide of between 1.0 and 1.5 to form lithium halide and a solution primarily of hexaorgano-substituted-ditin, in one or more solubilizing solvents in amounts such that the mole ratio of said solubilizing solvent to triorganotin halide is less than 3, and removing the lithium halide which precipitates from the hexaorgano-substituted-ditin, whereby the resulting hexaorgano-substituted-ditin contains less than 3000 ppm chloride based on the hexaorgano-substituted-ditin. A process according to claim 13 wherein the lithium halide is removed by filtering. A process according to claim 14 wherein the solution is filtered at a temperature from 10 to 70°C. A process according to claim 15 wherein during the filtration step the solution is at from about 20 to 65°C. A process according to any one of claims 13 to 16 wherein said one or more solubilizing solvents is tetrahydrofuran, the organo groups of the triorgano substituted-tin lithium are individually alkyls or cycloalkyls of from 1 to 12 carbon atoms, and said hexaorganotin has less than 2000 ppm chloride after filtration. A process according to claim 17 wherein the organo groups are alkyls of 2-8 carbon atoms.

Inventors: HERGENROTHER WILLIAM L, MURATORE ANTHONY JOSEPH, NEMETH MARK TIMOTHY, SIGLE JAY C, SMITH WILLIAM NOVIS, HERGENROTHER, WILLIAM L., MURATORE, ANTHONY JOSEPH, NEMETH, MARK TIMOTHY, SIGLE, JAY C., SMITH, WILLIAM NOVIS
Applicants: BRIDGESTONE CORP, CYPRUS FOOTE MINERAL, BRIDGESTONE CORPORATION, CYPRUS FOOTE MINERAL COMPANY
Application year: 1995
Main classification: C07F7
IPC codes: C08F36, C07F7, C08F4, C08F236