POLYESTER/POLYCARBONATE BLENDS HAVING ENHANCED PROPERTIES

Abstract: A PES/PC blend having enhanced properties as virgin material and as recyclate comprises a) at least one phosphite, b) at least one sterically hindered phenol, c) at least one compound promoting the reaction of an epoxy resin with a PES/PC blend, and d) at least one difunctional epoxy resin, 0.01 to 10 parts of component c) being used per 100 parts of PES/PC blend.

Description: Polvester/polycarbonate blends having enhanced properties The invention relates to polyester/polycarbonate blends having enhanced properties as well as to a process for enhancing the properties of polyester/polycarbonate blends. Polyester/polycarbonate blends (PES/PC) such as polybutylene terephthalate/PC blends (PBT/PC) or polyethylene terephthalate/polycarbonate blends (PET/PC), or ternary blends such as PBT/PC/ABS, are important engineering plastics. These blends unite the properties of the starting polymers, such as high impact strength at room temperature and at low temperature, high rigidity, low susceptibility to stress-cracking, good resistance to chemicals, in particular to fuel, and easy coatability. Because of these properties, PBT/PC blends are preferably used for lacquered parts of large dimensions, for example in the automotive industry for the production of car bumpers. Since the production of these parts demand relatively long cycle times at elevated temperature, efficient processing stabilisation is essential. The mechanical and physical properties of these blends furthermore depend essentially on the molecular weight of the polymer. During processing and use, however, the PES/PC blends are often damaged, resulting in reduced molecular weight. High-quality recycling of used PES/PC blends and of production waste therefore makes an increase of the molecular weight necessary. Accordingly, it is the object of the present invention to provide PES/PC blends, more particularly PBT/PC recyclates, having enhanced properties. In this context, enhancing the properties will be taken to mean in particular enhancing the processing stability and/or increasing the molecular weight. The molecular weight increase may relate either to a single component of the blend or to both or several components of the blend simultaneously. Surprisingly, a mixture of at least one phosphite, at least one sterically hindered phenol, at least one compound promoting the reaction of an epoxy resin with a PES/PC blend, and at least one difunctional epoxy resin, substantially enhances the properties of the blend. Accordingly, the invention relates to a PES/PC blend comprising a) at least one phosphite, b) at least one sterically hindered phenol, c) at least one compound promoting the reaction of an epoxy resin with a PES/PC blend, and d) at least one difunctional epoxy resin, 0.01 to 10 parts of component c) being used per 100 parts of PES/PC blend. In particular, the present invention relates to PES/PC blend recyclates, more particularly to PBT/PC or PET/PC and, very particularly, to PBT/PC recyclates. Such recyclates originate, for example, from industrial waste or useful material collections, production wastes or obligatory returnables. These recyclates may be obtained, for example, already as blend (for example in the case of car bumper materials), but may also be used as separate polymers for the preparation of the recyclate blend; e.g. PET from bottles and PC from rib-enforced sandwich panels of roof linings, or e.g. from returnable bottles. The recyclates may in particular be recyclates from car bumpers. Furthermore, according to this invention only one component of the blend can be in the form of scrap material, for example PET bottle recyclate in combination with PC virgin material. The polyesters may be homopolyesters or copolyesters that are derived from aliphatic, cycloaliphatic or aromatic dicarboxylic acids and diols or hydroxycarboxylic acids. The aliphatic dicarboxylic acids may contain from 2 to 40 carbon atoms, the cycloaliphatic dicarboxylic acids from 6 to 10 carbon atoms, the aromatic dicarboxylic acids from 8 to 14 carbon atoms, the aliphatic hydroxycarboxylic acids from 2 to 12 carbon atoms, and the aromatic as well as the cycloaliphatic hydroxycarboxylic acids from 7 to 14 carbon atoms. The aliphatic diols may contain from 2 to 12 carbon atoms, the cycloaliphatic diols from 5 to 8 carbon atoms and the aromatic diols from 6 to 16 carbon atoms. Aromatic diols will be taken to mean those in which two hydroxyl groups are bonded to one aromatic hydrocarbon radical or to different aromatic hydrocarbon radicals. The polyesters may also be branched with minor amounts, typically 0.1 to 3 moi %, based on the dicarboxylic acids, of more than difunctional monomers (e.g. pentaerythritol, trimellitic acid, l,3,5-tri(hydroxyphenyl)benzene, 2,4-dihydroxybenzoic acid or 2-(4-hydroxyphenyl)-2-(2,4-dihydroxyphenyl)propane). If the polyesters are based on at least 2 monomers, said monomers may be randomly distributed, or they may be block copolymers. Suitable dicarboxyhc acids are linear and branched saturated aliphatic dicarboxylic acids, aromatic dicarboxyhc acids and cycloaliphatic dicarboxylic acids. Suitable aliphatic dicarboxylic acids are those containing 2 to 40 carbon atoms, typically oxalic acid, malonic acid, dimethylmalonic acid, succinic acid, pimelic acid, adipic acid, trimethyladipic acid, sebacic acid, azelaic acid and dimer acids (dimerisation products of unsaturated aliphatic carboxylic acids such as oleic acid), alkylated malonic and succinic acids such as octadecylsuccinic acid. Suitable cycloaliphatic dicarboxyhc acids are: 1,3-cyclobutanedicarboxylic acid, 1,3-cyclopentanedicarboxylic acid, 1,3- and 1,4-cyclohexanedicarboxylic acid, 1,3- and l,4-(dicarboxylmethyl)cyclohexane, 4,4'-dicyclohexyldicarboxylic acid. Suitable aromatic dicarboxylic acids are: preferably terephthalic acid, isophthalic acid, o-phthalic acid, as well as 1,3-, 1,4-, 2,6- or 2,7-naphthalenedicarboxylic acid, 4,4-diphenyldicarboxylic acid, 4,4'-diphenylsulfonecar- boxylic acid, 4,4'-benzophenonedicarboxylic acid, l,l,3-trimethyl-5-carboxyl-3-(p-carbox- ylphenyl)indane, 4,4'-diphenyl ether dicarboxylic acid, bis-p-(carboxylphenyl)methane or bis-p-(carboxylphenyl)ethane. The aromatic dicarboxylic acids are preferred, including in particular terephthalic acid and isophthalic acid. Further suitable dicarboxylic acids are those that contain -CO-NH- groups and which are disclosed in DE-A 2 414349. Dicarboxylic acids that contain N-heterocyclic rings are also suitable, for example those that are derived from carboxylalkylated, carboxylphenyla- ted or carboxybenzylated monoamine-s-triazinedicarboxylic acids (q.v. DE-A 2 121 184 and 2533 675), mono- or bishydantoins, benzimidazolenes or halogenated benzimidazolenes or parabanic acid. The carboxyalkyl groups may contain from 3 to 20 carbon atoms. Suitable aliphatic diols are the linear and branched aliphatic glycols, preferably those containing 2 to 12, most preferably 2 to 6, carbon atoms in the molecule, typically including: ethylene glycol, 1,2- and 1,3-propylene glycol, 1,2-, 1,3-, 2,3- or 1,4-butanediol, pentyl glycol, neopentyl glycol, 1,6-hexanediol, 1,12-dodecanediol. A suitable cycloaliphatic diol is conveniendy 1,4-dihydroxycyclohexane. Further suitable aliphatic diols are typically l,4-bis(hydroxymethyl)cyclohexane, aromatic- aliphatic diols such as p-xylylene glycol or 2,5-dichloro-p-xylylene glycol, 2,2-(β-hydroxyethoxyphenyl)propane, as well as polyoxyalkylene glycols such as diethylene glycol, methylene glycol, polyethylene glycol or polypropylene glycol. The alkylene diols are preferably linear and preferably contain 2 to 4 carbon atoms. Preferred diols are the alkylene diols, 1,4-dihydroxycyclohexane and l,4-bis(hydroxy- methyl)cyclohexane. Ethylene glycol and 1,4-butanediol are especially preferred. Further suitable aliphatic diols are d e β-hydroxyalkylated, preferably β-hydroxyethylated, bisphenols such as 2,2-bis[4'-(β-hydroxyethoxy)phenyl]propane. Further bisphenols are mentioned hereinafter. A further group of suitable aliphatic diols comprises die heterocyclic diols disclosed in German Offenlegungsschrift specifications 1 812 003, 2 342432, 2 342 372 and 2453 326 Illustrative examples are: N,N'-bis(β-hydroxyedιyl-5,5-dimethyl)hydantoin, N,N'-bis(β-hydroxypropyl-5,5- dimethyl)hydantoin, methylenebis[N-(β-hydroxye±yl)-5-methyl-5-ethylhydantoin], methylenebis [N-(β-hydroxyethyl)-5 ,5-dimethylhydantoin] , N,N'-bis (β-hydroxy- ethylbenzylimidazolone, -(tetrachloro)benzimidazolone or -(tetrabromo)benzimidazolone. Suitable aromatic diols are mononuclear diphenols and, preferably, dinuclear diphenols which carry a hydroxyl group at each aromatic nucleus. By aromatic are meant preferably aromatic hydrocarbon radicals such as phenylene or naphdiylene. In addition to e.g. hydroquinone, resorcinol or 1,5-, 2,6- and 2,7-dihydroxynaphthaline, those bisphenols merit special mention tiiat may be illustrated by the following formulae: The hydroxyl groups may be in m-position, but are preferably in p-position. R' and R" in tins formula may be alkyl of 1 to 6 carbon atoms, halogen such as chloro or bromo and, in particular, hydrogen atoms. A may be a direct bond or O, S, SO 2 , CO, P(O)(C 1 -C 20 alkyl), unsubstituted or substituted alkylidene, cycloalkylidene or alkylene. Unsubstituted or substituted alkylidene is exemplified by: ethylidene, 1,1- or 2,2-propylidene, 2,2-butylidene, 1,1-isobutylidene, pentylidene, hexylidene, heptylidene, octylidene, dichloroethylidene, trichloroethylidene. Illustrative examples of unsubstituted or substituted alkylene are methylene, ethylene, phenylmethylene, diphenylmethylene, methylphenylmethylene. Illustrative examples of cycloalkyhdene are cyclopentylidene, cyclohexylidene, cycloheptyhdene and cyclooctylidene. Illustrative examples of bisphenols are: bis(p-hydroxyphenyl) ether or thioether, bis(p-hydroxyphenyl)sulfone, bis(p-hydroxy- phenyl)methane, bis(4-hydroxyphenyl)-2,2-biphenyl, phenylhydroquinone, methylhydro- quinone, trimethylhydroqinone, l,2-bis(p-hydroxyphenyl)ethane, l-phenyl-bis(p-hydroxy- phenyl)methane, diphenyl-bis(p-hydroxyphenyl)methane, diphenyl-bis(p-hydroxyphenyl)- methane, bis(3,5-dimethyl-4-hydroxyphenyl)sulfone, bis(3,5-dimethyl-4-hydroxy- phenyl)-p-diisopropylbenzene, bis(3,5-dimethyl-4-hydroxyphenyl)-m-diisopropylbenzene, 2,2-bis(3',5'-dimethyl-4'-hydroxyphenyl)propane, 1,1- or2,2-bis(p-hydroxyphenyl)butane, 2,2-bis(p-hydroxyphenyl)hexafluoropropane, 1,1-dichloro- or l,l,l-trichloro-2,2-bis- (p-hydroxyphenyl)ethane, l,l-bis(p-hydroxyphenyl)cyclopentane and, preferably, 2,2-bis- (p-hydroxyphenyl)propane (bisphenol A) and l,l-bis(p-hydroxyphenyl)cyclohexane (bisphenol C). Suitable polyesters of hydroxycarboxylic acids typically include polycaprolactone, polypivalolactone or the polyesters of 4-hydroxycyclohexanecarboxylic acid or 4-hydroxybenzoic acid. Also suitable are polymers containing mainly ester bonds, but also other bonds, such as polyester amides or polyester imides. Polyesters with aromatic dicarboxylic acids have achieved die greatest importance, in particular the polyalkylene terephthalates. Inventive moulding materials are therefore preferred in which the polyester is comprised of at least 30 moi %, preferably of at least 40 moi %, of aromatic dicarboxylic acids, and of at least 30 moi %, preferably of at least 40 moi %, of alkylenediols containing preferably 2 to 12 carbon atoms, based on the polyester. Especially in mis case the alkylenediol is linear and contains 2 to 6 carbon atoms and is exemplified by ethylene, trimethylene, tetramethylene or hexamethylene glycol and the aromatic dicarboxyhc acid is terephdialic and/or isophdialic acid. Particularly suitable polyesters are PET, PBT and corresponding copolymers. Polycarbonate (PC) is typically obtained from bisphenol A and phosgene or a phosgene analog such as trichloromethylchloroformate, triphosgene or diphenylcarbonate, in die last mentioned case by condensation, usually by addition of a suitable transesterification catalyst, such as a boron hydride, an amine such as 2-medιylimidazole or a quaternary ammomum salt. In addition to bisphenol A, otiier additional bisphenol components may be used, and also monomers which may be halogenated in me benzene nucleus. Particularly suitable bisphenol components that merit mention are: 2,2-bis(4'-hydroxyphenyl)propane (bisphenol A), 2,4'-dihydroxydiphenylmethane, bis(2-hydroxyphenyl)methane, bis- (4-hydroxyphenyl)methane, bis(4-hydroxy-5-propylphenyl)methane, 1 , l-bis(4'-hydroxy- phenyl)ethane, bis(4-hydroxyphenyl)cyclohexylmedιane, 2,2-bis(4'-hydroxyphenyl)-l- phenylpropane, 2,2-bis(3 ' ,5 '-dimethyl-4'-hydroxyphenyl)propane, 2,2-bis(3 ' ,5 '-dibromo- 4'-hydroxyphenyl)propane, 2,2-bis(3',5'-dichloro-4'-hydroxyphenyl)propane, 1,1-bis- (4'-hydroxyphenyl)cyclododecane, l,l-bis(3\5'-dimethyl-4'-hydroxyphenyl)cyclo- dodecane, l,l-bis(4'-hydroxyphenyl)-3,3,5-trimethylcyclohexane, l,l-bis(4'-hydroxy- phenyl)3,3,5,5-tetramethylcyclohexane, l,l-bis(4'-hydroxyphenyl)-3,3,5-trimethyl- cyclopentane and die bisphenols indicated above. Furthermore, the polycarbonates may also be branched by suitable amounts of more than difunctional monomers (examples are as indicated above). In addition to blends of PES and PC, i.e. in particular PBT/PC and PET/PC, suitable blends according to this invention are also ternary blends such as PBT/PC/ABS, PBT/PET/PC, PBT/PET/PC/ABS or PBT PC/ASA blends. The blends are prepared in customary manner from the starting polymers. The PES component is preferably PBT and die PC component is preferably a PC based on bisphenol A. The ratio of PES to PC is preferably from 95:5 to 5:95. Most preferred is a ratio in which one component constitutes at least 70%. The transesterification reactions result in all PES/PC blends containing a lesser or greater amount of block copolymer structures, i.e. one part of the blends is in die form of a PC/PES block copolymer. The inventive enhancement of the properties increases the compatibility of the polymers with one another. However, it is also possible to increase the compatibility with so-called compatibilisers. In the present case these may typically be polyester/polycarbonate copolymers, but also polyarylates (= aromatic polyesters). The PES/PC recyclates may also contain minor amounts of other polymers as impurities, for example polyolefms, polyurethanes, ABS or PVC. Furthermore, these recyclates may also contain standard impurities, such as dye residues, paint residues, metal traces, fuel residues and inorganic salts. The organic phosphites which may be used as component a) in accordance witii this invention are known as stabilisers for plastics. They are preferably used as processing stabilisers for polyolefms. The phosphites to be used according to tiiis invention are typically those of formula wherein R' l , R' 2 and R' 3 are each independendy of one anodier alkyl of 1 to 18 carbon atoms, alkyl of 1 to 18 carbon atoms which is substituted by halogen, -COOR}', -CN or -CONR 4 'R 4 , ; alkyl of 2 to 18 carbon atoms which is interrupted by -S-, -O- or -NR' 4 - ; cycloalkyl of 5 to 8 carbon atoms, phenyl or naphthyl; phenyl or naphthyl, each of which is substituted by halogen, 1 to 3 alkyl radicals or alkoxy radicals containing a total of 1 to 18 carbon atoms; 2,2,6,6-tetramethylpiperid-4-yl, N-allyl- or N-benzyl- or N-alkyl-2,2,6,6-tetramethyl- piperid-4-yl containing 1 to 4 carbon atoms in die alkyl moiety, or N-alkanoyl- 2,2,6,6-tetramethylpiperid-4-yl containing 1 to 4 carbon atoms in the alkyl moiety, or N-alkylene-2,2,6,6-tetramethylpiperidyl or N-alkylene-4-alkoxy-2,2,6,6-tetramethyl- piperidyl containing 1 to 3 carbon atoms in the alkylene moiety and 1 to 18 carbon atoms in the alkoxy moiety, each R' 4 is independently hydrogen, alkyl of 1 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms, or phenylalkyl containing 1 to 4 carbon atoms in the alkyl moiety, n' is 2, 3 or 4, A', if n' or q = 2, is alkylene of 2 to 12 carbon atoms, alkylene of 2 to 12 carbon atoms which is interrupted by -S-, -O- or -NR' 4 -, wherein R ' 4 has the given meaning, or a radical of formula A', if n' or q = 3, is a radical of formula -C f H^-r or ^( Α 2 . 2 ^ 3 ~ , wherein r is 5 or 6, A', if n' = 4, is the radical of formula C(CH 2 ~ ) 4 ~ , R 5 and R 6 are each independendy of die other hydrogen or alkyl of 1 to 8 carbon atoms, B is a radical of formula -CH 2 -, -CHR' 4 -, -CR^R^-, -S- or a direct bond, wherein R and R' 4 are as indicated, p is 1 or 2, D', if p = 1, is metiiyl and, if p = 2, is -CT^OGE . R' 9 is metiiyl, and R' 10 has the meaning of R , q is 2 or 3, y is 1, 2 or 3, W, if y = 1, is alkyl of 1 to 18 carbon atoms, a radical of formula -OR' 16 , -NR' 17 R' 18 or fluoro, W, if y = 2, is a radical of formula -O-A"-O-, or W, if y = 3, is a radical of formula R 4 , or N(C 3 H 6 7 3 - . wherein R' 4 has the given meaning, R' 16 has the meaning of R , R' 17 and R _ are each independendy of d e other alkyl of 1 to 18 carbon atoms, benzyl, cyclohexyl, a 2,2,6,6-tetra- or l,2,2,6,6-pentamethylpiperid-4-yl radical, or R' 17 and R' 18 , taken togetiier, are butylene, pentylene, hexylene or the radical of formula -CH 2 CH 2 -O-CH 2 CH 2 -, A" has the meaning of A', if n' = 2, R' 19 is hydrogen or metiiyl, the substituents R'ι 4 are each independendy of one anodier hydrogen, alkyl of 1 to 9 carbon atoms or cyclohexyl, R' 15 is hydrogen or metiiyl, and Z is a direct bond, -CH 2 -, -C R'i 4 ) 2 - or -S- , wherein the substituents R' 1 are identical or different and have d e indicated meaning. Particularly suitable phosphites of formula (IE) are those, wherein R'_, R' 2 and R' 3 are each independendy of one another alkyl of 1 to 18 carbon atoms; phenyl; phenyl which is substituted by 1 to 3 alkyl radicals containing a total of 1 to 18 carbon atoms, or 2,2,6,6-tetramethylpiperid-4-yl and, more particularly, those, wherein R , R' 2 and R' 3 are each independendy of one another phenyl which is substituted by 1 to 3 alkyl radicals containing a total of 1 to 12 carbon atoms. Particularly suitable phosphites of formula (TV) are those, wherein A', if n' = 2, is preferably alkylene of 2 to 12 carbon atoms, -CH 2 CH 2 -O-CH 2 CH 2 -, -CH 2 CH 2 -O-CH 2 CH 2 O-CH 2 CH 2 - or -CH 2 CH 2 -NR CH 2 CH 2 - . C r A', if n * = 3, is N(CH 2 CH 2 3 " , wherein R' 4 is alkyl of 1 to 4 carbon atoms. Particularly suitable phosphites of formula (V) are those, wherein p is 1, D' is methyl, R' 9 is methyl and R' 10 is phenyl which is substituted by 1 to 3 alkyl radicals containing a total of 1 to 18 carbon atoms. Particularly suitable phosphites of formula (VII) are those, wherein W, if y = 1, is a radical of formula -OR'iβ, -NR' 17 R' 18 or fluoro, or W, if y = 2, is a radical of formula -O-CH 2 CH 2 -NR 4 -CH 2 CH 2 -O- , or W, if y = 3, is a radical of formula N(CH 2 CH 2 O-) 3 - , wherein R' 16 is alkyl of 1 to 18 carbon atoms, R' 17 and R' 18 are each independendy of the other alkyl of 1 to 18 carbon atoms, cyclohexyl or benzyl, or R' 17 and R' 18 , taken together, form a piperidyl, morpholinyl or hexamethylene-imino radical, and R' has die given meaning, Z is a direct bond, -CH 2 - or -CHCH 3 - , and die two substituents R'ι 4 are each independendy of die otiier alkyl of 1 to 4 carbon atoms and, more particularly, W, if y = 1, is 2-ethylhexyloxy or fluoro, R' 14 is tert-butyl, is hydrogen and Z is -CH 2 - or -CH(CH 3 )- , or W, if y = 2, is a radical of formula -O-CH 2 CH 2 -NCH 3 -CH 2 CH 2 -O-. Preferred phosphites are typically trilaurylphosphite, trioctadecylphosphite, distearyl pentaerythritol diphosphite or tristearyl sorbitol triphosphite. Aromatic phosphites are also preferred. By aromatic phosphites are meant those phosphites which contain an aromatic hydrocarbon radical such as a phenyl radical. Illustrative examples are triphenylphosphite, diphenylalkylphosphites, phenyldialkylphosphites and, specifically, tris(nonylphenyl)phosphite, tris(2,4-di-tert-butylphenyl)phosphite, bis(2,4-di-tert- butylphenyl)pentaerythritoldiphosphite and 2,2'-edιylidene-bis(4,6-di-tert-butylphenyl)- fluorophosphite. Of preeminent interest are phosphites containing as structural element die grouping P-O-Ar, wherein Ar is an aromatic radical, preferably an alkyl-substituted phenyl radical. Suitable alkyl substituents are C 1 -C 18 alkyl radicals or also C5-Cτcycloalkyl radicals. C 1 -C 4 Alkyl radicals and, more particularly, tert-butyl (represented in the formulae by ) are preferred. The following phosphites are particularly preferred: tris(2,4-di-tert-butylphenyl)phosphite; The use of tris(2,4-di-tert-butylphenyl)phosphite, very particularly preferred. It is preferred to use 0.01-2 parts, more particularly 0.01-1 part, of the phosphite, based on 100 parts of PES/PC blend. The sterically hindered phenols which may be used in accordance with this invention as component b) are likewise commonly known stabilisers against the thermal-oxidative ageing of plastics, in particular of polyolefins. Typically, the sterically hindered phenols contain at least one group of formula I wherein R' is hydrogen, metiiyl or tert-butyl; and R" is unsubstituted or substituted alkyl or unsubstituted or substituted alkylthioalkyl. A particularly suitable sterically hindered phenol is a compound of formula π, (H), wherein A is hydrogen, C- C^alkyl, C 5 -C 1 cycloalkyl, phenyl-C 1 -C 4 alkyl, phenyl or a group -CH 2 -S-R 25 or D is C 1 -C 2 alkyl, C 5 -C 12 cycloalkyl, phenyl-C r C alkyl, phenyl or a group -C^-S-R^, X is hydrogen, or one of the groups -C a H 2a -S q -R 26 , -C b H 2b -CO-OR 7 , -C b H 2b -CO-N(R 29 )(R 30 ), -CH 2 N(R 3 4)(R 35 ) , R is hydrogen or a group of formula -CO-CH=CH 2 , G* is hydrogen or C 1 -C 12 alkyl, R- 25 is C r C 18 alkyl, phenyl or a group -(CH 2 ) c -CO-OR 28 or -CH 2 CH 2 OR 33 , R 26 is hydrogen, Cι-C 18 alkyl, phenyl, benzyl or a group or -(CΗ. 2 ) c -CO-OR 28 or -CH 2 -CH 2 -OR 33 , R 27 is Cι-C 3 oalkyl or one of the groups -CHR 31 -CH 2 -S-R3 2 , or ] 3 , wherein Q is Qz- alkylene, C 4 -C 6 thiaalkylene or a group -CH 2 GH 2 (OCH 2 CH 2 ) d -, R 28 is C 1 -C 24 alkyl, R 2 is hydrogen, or cyclohexyl, R 30 is -Cjgalkyl, cyclohexyl, phenyl; Cj-C 18 alkyl-substituted phenyl, or one of the groups -C[(CH 2 ) r O-CO-C b H 2b — J— OH ] 3 , D or R 2 9 and R 30 , taken together, are C 4 -C 8 alkylene which may be interrupted by -O- or -NH-, R 31 is hydrogen, C 1 -C alkyl or phenyl, R 32 is C r C 18 alkyl, R 33 is hydrogen, C j -C^alkyl, phenyl, -Cjgalkanoyl or benzoyl, R 34 is C C 18 alkyl, cyclohexyl, phenyl, C r C 18 alkyl-substituted phenyl, or a group R 35 is hydrogen, C j -C^alkyl, cyclohexyl or a group R 34 and R 35 , taken together, are C 4 -C 8 alkylene which may be substituted by -O- or -NH-, a is 0, 1, 2 or 3, b is 0, 1, 2 or 3, c is 1 or 2, d is 1 to 5, f is 2 to 8, and q is 1, 2, 3 or 4. A preferred compound of formula II is that, wherein is hydrogen, -Cgalkyl, cyclohexyl, phenyl or a group -CH 2 -S-C 1 -C 18 alkyl or D is C j -Cgalkyl, cyclohexyl, phenyl or a group -CH 2 -S-C 1 -C 18 alkyl, X is hydrogen, Ci-Cgalkyl or one of the groups -C a H 2a -S q -R 26 , -C b H 2b -CO-OR 2 , -CH 2 N(R 34 )(R 35 ) , R 26 is C j -C^alkyl, phenyl or a group -(CH* 2 ) c -CO-OR 28 , R 27 is Ci-Cisalkyl or a group wherein Q is C 2 -C 8 alkylene, -CH 2 -CH 2 -S-CH 2 CH 2 or a group -CH 2 CH 2 (OCH 2 CH 2 ) d -, R 28 is C r C 18 alkyl, R3 4 and R 35 are each independendy of the otiier hydrogen or C r C 12 alkyl, or R 34 and R 35 , taken together, are C 4 -C 8 alkylene which may be interrupted by -O- or -NH-, a is 1 or 2, b is 1 or 2, c is 1 or 2, and d is 1, 2 or 3. Illustrative examples of preferred sterically hindered phenols are: 2,6-di-tert-butyl-4-methylphenol, 2-tert-butyl-4,6-dimedιylphenol, 2,6-di-tert-butyl-4- ethylphenol, 2,6-di-tert-butyl-4-n-butylphenol, 2,6-di-tert-butyl-4-isobutylphenol, 2,6-dicyclopentyl-4-methylphenol, 2-(α-methylcyclohexyl)-4,6-dimedιylphenol, 2,6-di- octadecyl-4-methylphenol, 2,4,6- tricyclohexylphenol, 2,6-di-tert-butyl-4-methoxy- methylphenol, 2,6-dinonyl-4-methylphenol, 2,6-di-tert-butyl-4-methoxyphenol, 2,5-di- tert-butylhydroquinone, 2,5-di-tert-amyl-hydroquinone, 2,6-diphenyl-4-octadecyl- oxyphenol, 2,2'-thiobis(6-tert-butyl-4-methylphenol), 2,2'-thiobis(4-octylphenol), 4,4'-thiobis(6-tert-butyl-3-methylphenol), 4,4'-thiobis(6-tert-butyl-2-methylphenol), 2,2'-methylenebis(6-tert-butyl-4-methylphenol), 2,2'-methylenebis(6-tert-butyl- 4-ethylphenol), 2,2'-medιylenebis[4-medιyl-6-(α-methylcyclohexyl)-phenol], 2,2'- methylenebis(4-methyl-6-cyclohexylphenol), 2,2'-methylenebis(6-nonyl-4-methylphenol), 2,2'-methylenebis(4,6-di-tert-butylphenol), 2,2'-ethylidenebis(4,6-di-tert-butylphenol), 2,2'-edιylidenebis(6-tert-butyl-4-isobutylphenol), 2,2'-methylenebis[6-(α-methyl- benzyl)-4-nonylphenol] , 2,2'-methylenebis [6-(α,α-dimethylbenzyl)-4-nonylphenol] , 4,4'-methylenebis(2,6-di-tert-butylphenol), 4,4'-methylenebis(6-tert-butyl-2-methyl- phenol), l,l-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 2,6-bis(3-tert-butyl- 5-methyl-2-hydroxybenzyl)-4-methylphenol, 1 ,1 ,3-tris(5-tert-butyl-4-hydroxy-2-methyl- phenyl)butane, l,l-bis(5-tert-butyl-4-hydroxy-2-medιylphenyl)-3-n-dodecylmercapto- butane, ethylene glycol bis[3,3-bis(3'-tert-butyl-4'-hydroxyphenyl)butyrate], bis(3-tert- butyl-4-hydroxy-5-metiιylphenyl)dicyclopentadiene, bis[2-(3'-tert-butyl-2'-hydroxy-5'- methylbenzyl)-6-tert-butyl-4-methyl-phenyl]terephdιalate,l,3,5-tris(3,5-di-tert- butyl-4-hydroxybenzyl)-2,4,6-tr imethyl benzene, bis(3,5-di-tert-butyl-4-hydroxy- benzyl)sulfιde, isooctyl 3,5-di-tert-butyl-4-hydroxybenzylmercaptoacetate, bis(4-teιt- butyl-3-hydrox-2,6-dimethylbenzyl)did iolterephtha late, l,3,5-tris(3,5-di-tert-butyl-4- hydroxybenzyl)isocyanurate, l,3,5-tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)- isocyanurate, dioctadecyl 3,5-di-tert-butyl-4-hydroxybenzylphosphonate. Particularly preferred sterically hindered phenols are compounds containing at least one group of formula wherein R' is methyl or tert-butyl; and R" is unsubstituted or substituted alkyl or unsubstituted or substituted alkylthioalkyl. Illustrative examples of such sterically hindered phenols are: the esters of β-(3,5-di- tert-butyl-4-hydroxyphenyl)propionate and of β-(5-tert-butyl-4-hydroxy-3-methyl- phenyl)propionate with mono- or polyhydric alcohols, such as metiianol, octanol, octa- decanol, 1,6-hexanediol, neopentyl glycol, thiodietiiylene glycol, dietiiylene glycol, triethylene glycol, pentaerytiiritol, tris(hydroxyetiiyl)isocyanurate, N,N'-bis(hydroxy- ed yl)oxamide, as well as the amides of tiiese acids, such as N,N'-bis(3,5-di-tert-butyl- 4-hydroxyphenylpropionyl)hexamed ylenediamine, N,N'-bis(3,5-di-tert-butyl-4- hydroxyphenylpropionyl)trimethylenediamine and N,N , -bis(3,5-di-tert-butyl-4-hydroxy- *v phenylpropionyl)hydraziner Further particularly preferred compounds are: {2-(l,l-dimethylethyl)-6-[[3-(l,l-dimethylethyl)-2-hydroxy-5-methylphenyl]methyl]- 4-methylphenyl 2-propenoate}; CH 2 -CH 2 { 1,6-hexandiyl 3,5-bis(l,l-dimedιyl-edιyl)-4-hydroxyphenylpropanoate}; { 1 ,2-ethanediylbis(oxy-2, 1 -ethanediyl) 3-( 1 , 1 -dimethyletiιyl)-4-hydroxy-5-metiιyl- phenylpropanoate } ; {2-methyl-4,6-bis[(octylthio)medιyl]-phenol}; { 2,2'-edιylidenebis(4,6-di-tert-butylphenol) } ; {thiodi-2,l-edιanediyl 3,5-bis(l,l-dimedιyledιyl)-4-hydroxyphenylpropanoate}; { 4,4',4"-[(2,4,6-trimethyl- 1 ,3,5-phenyltriyl)-tris(methylene)] tris[2,6-bis(l , 1 -dimediyl- ethyl)phenol}; and 1 ,3,5-tris(3 ' ,5 '-di-tert.-butyl-4'-hydroxybenzyl)-isocyanurate. Very particularly preferred sterically hindered phenols are die pentaerythrityl, octyl and die octadecyl ester of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid. It is preferred to use 0.01-3 parts, more particularly 0.01-1 part, of the sterically hindered phenol, based on 100 parts of PES/PC blend. Furthermore, it is preferred to use component a) (phosphite) and b) (sterically hindered phenol) in the ratio from 1:10 to 10:1, most preferably in die ratio from 1:4 to 4:1. The compounds suitable for use as component c) in accordance witii this invention and which promote die reaction of an epoxy resin witii a PES/PC blend, belong to die group of the Lewis bases. Said compounds catalyse the reaction of an epoxy resin with a PES/PC blend. Suitable compounds may be selected from the following groups: Ci) metal oxides, metal hydroxides or metal carbonates; c 2 ) metal salts of organic acids; C 3 ) phosphates, phosphonates or phosphonites; c 4 ) tertiary amines, quarternary ammonium salts, polyamines or polyamides; c 5 ) silicates; C ) salts of sulfonic acids. If component c) is an inorganic compound of die series of the metal oxides, metal hydroxides or metal carbonates, then these are preferably metal oxides, metal hydroxides or metal carbonates of the elements of die 2nd main group and 2nd, 4th and 7th auxiliary groups. Further preferred metals are calcium, magnesium, zinc, titanium and manganese, the oxides such as CaO, MgO or ZnO, as well as calcium hydroxide and calcium carbonate, being particularly preferred. A mixture of different metal oxides, metal hydroxides or metal carbonates may also be used as component c). If component c) is a metal salt of an organic acid, tiien the metal is preferably an element of the 1st main group, die 2nd main or auxiliary group, aluminium or tin. Said metal salts are preferably zinc, magnesium, aluminium, tin or, more particularly, calcium salts of the series of the aliphatic saturated C 2 -C 22 carboxylates, the aliphatic olefinic C 3 -C 22 carboxylates, the aUphatic C^-C^carboxylates which are substituted by at least one OH group, die cyclic or bicyclic Cs-C^carboxylates, the aromatic C 7 -C 22 carboxylates, the aromatic C 7 -C 22 carboxylates which are substituted by at least one OH group, die phenylcarboxylates and die phenyl-C j -C j galkylcarboxylates, preferably stearates, laurates, behenates, laevulinates, lactates or thioglycolates. Examplary are also the salts of citric acid (e.g. sodium citrate), sodium benzoate or sodium naphd ate. Very particularly preferred metals soaps are calcium stearate, magnesium stearate, aluminium stearate, zinc stearate, calcium lactate or calcium laurate. It is also possible to use a mixture of different metal soaps for component c). Component c) may typically be a mixture of calcium laurate and calcium stearate, of zinc laurate and calcium stearate or of zinc stearate and calcium stearate. If component c) is a phosphate, phosphonate or phosphonite, then it is suitably e.g. calcium phosphate or aluminium phosphate, sodium pyrophosphate or calcium pyrophosphate, ammonium polyphosphate, triphenyl phosphate or tris(2,4-di-tert-butylphenyl)phosphate, as well as sterically hindered hydroxyphenylalkyl phosphonic acid esters or half-esters as disclosed, inter alia, in US 4,778,840. The hydroxyphenylalkyl phosphonic acid esters or half -esters may be illustrated by the following formula: wherein R ] is isopropyl, tert-butyl, cyclohexyl or cyclohexyl which is substituted by 1 to 3 C r C 4 alkyl groups; R 2 is H, C j -C 4 alkyl, cyclohexyl or cyclohexyl which is substituted by 1 to 3 C 1 -C 4 alkyl groups; R 3 is Ci-C^o- kyl, or unsubstituted or substituted phenyl or naphdiyl; R 4 is M 2+ /2, C j -C^o-alky-. . or unsubstituted or substituted phenyl or naphthyl; M + is a divalent metal cation, and n is 1 to 6. Substituents defined as alkyl containing up to and including 8 carbon atoms are suitably radicals such as metiiyl, ethyl, propyl, butyl, pentyl, hexyl, octyl, stearyl or lauryl as well as the corresponding branched isomers. C 2 -C Alkyl is preferred. Suitable substituents of the phenyl or naphdiyl radicals are typically C r C 4 alkyl groups. Suitable divalent metal cations are typically Zn, Ba, Ca and Mg. Calcium is particularly preferred. Preferred compounds of formula (VIII) are those that contain at least one tert-butyl group as R j or R . Compounds in which Rj and R 2 are tert-butyl (in the formulae: 1 — ) are very particularly preferred. Preferably n is 1 or 2 and, most preferably, 1. Sterically hindered hydroxyphenylalkyl phosphonic acid ester or half-ester is very particularly preferably: If component c) is a tertiary amine, a quarternary ammonium salt, a polyamine or a polyamide, men it is suitably trimethylbenzylammonium chloride or trimethylbenzylammonium bromide, N,N-dimethyl-4-aminopyridine, diediylaminopropylamine, tetramethylguanidine, 2-ethyl-4-medιylimidazol, dimetiiylbenzylamine or dicyandiamide. If component c) is a silicate, then it is suitably e.g. a dehydrotalcite such as DHT-4A®, an alcamizer or a calcium silicate hydrate (Xonodit®). If component c) is a salt of a sulfonic acid, tiien it may suitably be e.g. sodium perfluorobutanesulfonate or a p-toluene sulfonic acid salt (e.g. sodium salt). It is also possible to use mixtures of the components c_ to c 6 . 0.01-10 parts, preferably 0.05-1 part, of component c) are used per 100 parts of PES/PC blend. The difunctional epoxy resins which may be used as component d) according to mis invention may have an aliphatic, aromatic, cycloaliphatic, araliphatic or heterocyclic structure. They contain epoxy groups as side groups or tiiese groups form part of an ali- cyclic or heterocycUc ring system. The epoxy groups are preferably Unked to die residual molecule as glycidyl groups dirough ether or ester bonds, or tiiey are N-glycidyl deri¬ vatives of heterocyclic amines, amides or imides. Epoxy resins of diese types are commonly known and commercially available. The epoxy resins contain two epoxy radicals, typically those of formula X O — CH- (CH 2 )- C - N CH f (χ) R 1 R 2 R 3 which radicals are linked direct to carbon, oxygen, nitrogen or sulfur atoms, wherein R j and R 3 are botii hydrogen, R 2 is hydrogen or metiiyl, and n = 0, or wherein R- and R 3 , taken together, are -CH 2 -CH 2 - or -CH 2 -CH 2 -CH 2 -, in which case R 2 is hydrogen and n = 0 or 1. Illustrative examples of epoxy resins are: I) Diglycidyl and di(β-methylglycidyl) esters which are obtainable by reacting a compound containing two carboxyl groups in the molecule and epichlorohydrin or glycerol dichlorohydrin or β-methyl epichlorohydrin. The reaction is conveniendy carried out in the presence of a base. Compounds containing two carboxyl groups in the molecule may suitably be aUphatic dicarboxylic acids. Exemplary of tiiese dicarboxyUc acids are glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid or dimerised or trimerised linoleic acid. Cycloaliphatische dicarboxyUc acids may also be used, for example tetrahydrophthaUc acid, 4-methyltetrahydrophdιaUc acid, hexahydrophdiaUc acid or 4-methylhexahydro- phthaUc acid. Aromatic dicarboxylic acids may also be used, including phtiialic acid or isophmalic acid. II) Diglycidyl or di(β-methylglycidyl) ethers which are obtainable by reacting a compound containing two free alcoholic hydroxyl groups and or phenolic hydroxyl groups in the molecule with a suitably substituted epichlorohydrin under alkaline conditions or in die presence of an acid catalyst and subsequent treatment with an alkali. Eti ers of tiiis type are typically derived from acycUc alcohols such as ethylene glycol, di- ethylene glycol and higher poly(oxyethylene) glycols, 1,2-propanediol, or poly(oxy- propylene) glycols, 1,3-propanediol, 1,4-butanediol, poly(oxytetramethylene) glycols, 1,5-pentanediol, 1,6-hexanediol, sorbitol, as well as from polyepichlorohydrins. They may also be derived from cycloaliphatic alcohols such as 1,3- or 1,4-dihydroxy- cyclohexane, bis(4-hydroxycyclohexyl)methane, 2,2-bis(4-hydroxycyclohexyl)propane or l,l-bis(hydroxymethyl)cyclohex-3-ene, or they contain aromatic nuclei, such as N,N-bis(2-hydroxyetiιyl)aniUne or p,p'-bis(2-hydroxyedιylamino)diphenylmemane. The epoxy resins may also be derived from mononuclear phenols, as from resorcinol, 1,2-benzenediol or hydroquinone, or tiiey are based on polynuclear phenols such as 4,4'-dihydroxybiphenyl, bis(4-hydroxyphenyl)medιane, 2,2-bis(4-hydroxyphenyl)propane, 2,2-bis(3,5-dibromo-4-hydroxyphenyl)propane, 4,4 '-dihydroxydiphenylsulfone, or 9,9-bis- (4-hydroxyphenyl)fluorene, or on condensates of phenols with formaldehyde which are obtained under acid conditions, for example phenol novolaks. IH) Bis(N-glycidyl) compounds, obtainable typically by dehydrochlorination of the reaction products of epichlorohydrin with amines which contain two amino hydrogen atoms. These amines are typically aniUne, toluidine, n-butylamine, bis(4-amino- phenyl)methane, m-xylylenediamine or bis(4-methylaminophenyl)methane. The bis(N-glycidyl) compounds, however, also include N,N' -diglycidyl derivatives of cycloalkylene ureas such as ethyleneurea or 1,3-popyleneurea, and N,N'-diglycidyl derivatives of hydantoins, typically of 5,5-dimethylhydantoin. IV) Bis(S-glycidyl) compounds, typically bis(S-glycidyl) derivatives diat are derived from didiiols such as 1,2-ethanedithiol or bis(4-mercaptomethylphenyl) edier. V) Epoxy resins containing a radical of formula X, wherein R 1 and R 3 together are -CH 2 -CH 2 - and n is 0, typically bis(2,3-epoxycyclopentyl) ether, 2,3-epoxycyclopentyl- glycidyl etiier or l,2-bis(2,3-epoxycyclopentyloxy) ethane. Epoxy resins containing a radical of formula X, wherein Rj and R 3 together are -CH 2 -CH 2 - and n is 1, is typically 3,4-epoxy-6-methylcyclohexyl-3',4'-epoxy-6'-metiιylcyclohexanecarboxylate. By reason of the preparative process, the above-mentioned difunctional epoxy resins may contain minor amounts of mono- or trifunctional groups. Furthermore, trifunctional or higher-functional epoxy resins may also be used, typically triglycidyl isocyanurate, triglycidyl trimellate or Diglycidyl compounds of aromatic structure are mainly used. It is also possible to use a mixture of epoxy resins of different structure. Particularly preferred difunctional epoxy resins are diglycidyl etiiers of bisphenols, typically 2,2-bis(4-hydroxyphenyl)propane (bisphenol A), bis(4-hydroxyphenyl)sulfone (bisphenol S) or mixtures of bis(ortho-/para-hydroxyphenyl)metiιane (bisphenol F). Epoxy resins of the diglycidyl etiier of bisphenol A type (especially having a softening temperature higher than 25°C) are very particularly preferred, e.g. Araldit® GT 6071, GT 6084, GT 7071, GT 7072, GT 6097 and GT 6099. Further compounds which are particularly preferred are, besides the diglycidyl ediers of bisphenol A, diglycidyl terephtiialate, diglycidyl etiier of bisphenol F, e.g. Araldit® GY 281 and PY 306, diglycidyl isophtiialate, triglycidyl trimeUate and Based on 100 parts of PES/PC blend, 0.01-5 parts, more particularly 0.02-2 parts and, most preferably, 0.05- 1 part, of me difunctional epoxy resins are used. To 100 parts of PES/PC blend are usually added 0.01 to 2 parts, preferably 0.01 to 1 part, of component a), 0.01 to 3 parts, preferably 0.01 to 1 part, of component b), 0.01 to 10 parts, preferably 0.05 to 1 part, of component c) and 0.01 to 5 parts, preferably 0.02 to 2 parts, of component d). The amount of the components a), b), c) and d) is determined in this case by the starting molecular weight of the polymer and by die desired final molecular weight, or whetiier a processing stability is desired. In addition to components a), b), c) and d) further stabilisers may be added to die PES/PC blend. These further stabilisers are known to the skiUed person and are selected according to die specific demands made of die end product In particular, it is possible to add light stabilisers or also antioxidants or additional antioxidants ("Plastics Additives Handbook", Ed. R. Gachter and H. Mϋller, Hanser Verlag, 3rd edition, 1990; in particular pages 88/89, 92/94, 251/252 and 258/259). Likewise it is possible to add further modifiers, such as slip agents, impact strength improvers, mould release agents, fiUers or reinforcing agents, such as glass fibres, flame retardants, antistatic agents and, especially for PBT/PC, modifiers mat prevent transesterification during processing, for example aromatic phosphates. 1. Suitable further antioxidants are also chroman derivatives of formula , wherein R is (O)-Z, and Z is orR" are hydrogen, metiiyl or tert-butyl, e.g. α-tocopherol, β-tocopherol, γ-tocopherol, δ-tocopherol and mixtures thereof (vitamin E). 2. UV absorbers and light stabilisers 2.1. 2-(2 , -Hvdroxyphenyl)benzotriazoles, for example 2-(2'-hydroxy-5'-methylphenyl)- benzotriazole, 2-(3 ' ,5 ' -di-tert-butyl-2 '-hydroxyphenyl)benzotriazole, 2-(5 ' -tert-butyl-2 ' - hydroxyphenyl)benzotriazole, 2-(2'-hydroxy-5'-(l,l,3,3-tetramethylbutyl)phenyl)benzo- triazole, 2-(3 ' ,5 '-di-teπ-butyl-2'-hydroxyphenyl)-5-chloro-benzotriazole, 2-(3 '-teπ-butyl- 2'-hydroxy-5'-medιylphenyl)-5-chloro-benzotriazole, 2-(3'-sec-butyl-5'-tert-butyl-2'- hydroxyphenyl)benzotriazole, 2-(2'-hydroxy-4'-octyloxyphenyl)benzotriazole, 2-(3 ',5 '- di-tert-amyl-2'-hydroxyphenyl)benzotriazole, 2-(3',5'-bis-(α,α-dimethylbenzyl)-2'- hydroxyphenyl)benzotriazole, mixture of 2-(3'-tert-butyl-2'-hydroxy-5'-(2-octyloxycar- bonylethyl)phenyl)-5-chloro-benzottiazole, 2-(3'-tert-butyl-5'-[2-(2-ethylhexyloxy)-car- bonyledιyl]-2'-hydroxyphenyl)-5-chloro-benzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2- methoxycarbonylethyl)phenyl)-5-chloro-benzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2- methoxycarbonyledιyl)phenyl)benzotriazole, 2- (3 '-tert-butyl-2 '-hydroxy-5 '- (2-octyl- oxycarbonylethyl)phenyl)benzotriazole, 2-(3'-tert-butyl-5'-[2-(2-ethylhexyloxy)carbonyl- ethyl]-2'-hydroxyphenyl)benzottiazole, 2-(3'-dodecyl-2'-hydroxy-5'-methylphenyl)benzo- triazole, and 2-(3 , -tert-butyl-2'-hydroxy-5 , -(2-isooctyloxycarbonylethyl)phenylbenzotri- azole, 2,2'-methylene-bis[4-( 1 , 1 ,3,3-tetramethylbutyl)-6-benzotriazole-2-ylphenol] ; the transesterification product of 2-[3'-tert-butyl-5'-(2-methoxycarbonylethyl)-2'-hydroxy- phenyl]-2H-benzotriazole with polyethylene glycol 300; [R-<_-Η 2 CT 2 -COO(CH 2 ) 3 t 2 — . where R = (3 , -tert-butyl-4'-hydroxy-5'-2H-benzotriazol-2-yl)phenyl. 2.2. 2-Hvdroxybenzophenones, for example the 4-hydroxy, 4-metiιoxy, 4-octyloxy, 4-de- cyloxy, 4-dodecyloxy, 4-benzyloxy, 4,2',4'-trihydroxy and 2'-hydroxy-4,4'-dimethoxy derivatives. 2.3. Esters of substituted and unsubstituted benzoic acids, as for example 4-tert-butyl- phenyl salicylate, phenyl salicylate, octylphenyl salicylate, dibenzoyl resorcinol, bis(4- tert-butylbenzoyl) resorcinol, benzoyl resorcinol, 2,4-di-tertbutylphenyl 3,5-di-tert-butyl- 4-hydroxybenzoate, hexadecyl 3,5-di-tert-butyl-4-hydroxybenzoate, octadecyl 3,5-di-tert- butyl-4-hydroxybenzoate, 2-methyl-4,6-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxy- benzoate. 2.4. AcTylates, for example ethyl α-cyano-β,β-diphenylacrylate, isooctyl α-cyano-β,β-di- phenylacrylate, methyl α-carbomethoxycinnamate, methyl α-cyano-β-methyl-p-metiioxy- cinnamate, butyl α-cyano-β-methyl-p-methoxy-cinnamate, methyl α-carbomethoxy-p- methoxycinnamate and N-(β-carbomethoxy-β-cyanovinyl)-2-methylindoline. 2.5. Nickel compounds, for example nickel complexes of 2,2'-thiobis[4-(l,l,3,3-tetra- methylbutyl)phenol], such as the 1:1 or 1:2 complex, witii or without additional ligands such as n-butylamine, triethanolamine or N-cyclohexyldiethanolamine, nickel dibutyldi- thiocarbamate, nickel salts of die monoalkyl esters, e.g. the methyl or etiiyl ester, of 4- hydroxy-3,5-di-tert-butylbenzylphosphonic acid, nickel complexes of ketoximes, e.g. of 2-hydroxy-4-methylphenyl undecylketoxime, nickel complexes of l-phenyl-4-lauroyl-5- hydroxypyrazole, with or without additional ligands. 2.6. Sterically hindered amines, for example bis(2,2,6,6-tetramethyl-piperidyl)sebacate, bis(2,2,6,6-tetramethyl-piperidyl)succinate, bis( 1 ,2,2,6,6-pentamethylpiperidyl)sebacate, bis(l,2,2,6,6-pentamethylpiperidyl) n-butyl-3,5-di-tert-butyl-4-hydroxybenzylmalonate, the condensate of l-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine and succi¬ nic acid, the condensate of N,N'-bis(2,2,6,6-tetramemyl-4-piperidyl)hexamethylenedi- amine and 4-tert-octylamino-2,6-dichloro-l,3,5-triazine, tris(2,2,6,6-tetramethyl-4-piperi- dyl) nitrilotriacetate, tetrakis(2,2,6,6-tetramethyl-4- piperidyl)- 1,2,3 ,4-butane-tetracar- boxylate, l, -(l,2-ethanediyl)bis(3,3,5,5-tetramethylpiperazinone), 4-benzoyl-2,2,6,6- tetramethylpiperidine, 4-stearyloxy-2,2,6,6-tetramethylpiperidine, bis( 1 ,2,2,6, 6-penta- methylpiperidyl)-2-n-butyl-2-(2-hydroxy-3,5-di-tert-butylbenzyl)malonate, 3-n-octyl- 7,7,9,9-tetramethyl-l,3,8-triazasprio[4.5]decane-2,4-dione, bis(l-octyloxy-2,2,6,6-tetra- methylpiperidyl)sebacate, bis(l-octyloxy-2^,6,6-tetramethylpiperidyl)succinate, the condensate of N,N'-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-mor- pholino-2,6-dichloro-l,3,5-triazine, the condensate of 2-chloro-4,6-bis(4-n-butylamino- 2,2,6,6-tetramethylpiperidyl )-l,3,5-triazine and l,2-bis(3-aminopropylamino)etiιane, the condensate of 2-chloro-4,6-di(4-n-butylamino- 1 ,2,2,6,6-pentamethylpiperidyl)- 1,3,5-triazine and l,2-bis(3-aminopropylamino)ethane, 8-acetyl-3-dodecyl-7,7,9,9-tetra- methyl- 1 ,3,8-triazaspiro[4.5]decane-2,4-dione, 3-dodecyl- 1 -(2,2,6,6-tetramethyl-4-piperi- dyl)pyrrolidine-2,5-dione, 3-dodecyl- 1 -( 1 ,2,2,6,6-pentamemyl-4-piperidyl)pyrrolidine- 2,5-dione. 2.7. Oxamides, for example 4,4'-dioctyloxyoxanilide, 2,2'-dioctyloxy-5,5'-di-tert-butox- anilide, 2,2'-didodecyloxy-5,5'-di-tert-butoxaniUde, 2-edιoxy-2'-ethyloxanilide, N,N'- bis(3-dimemylaminopropyl)oxamide, 2-ethoxy-5-tert-butyl-2'-ethoxanilide and its mix¬ ture with 2-ethoxy-2'-ethyl-5,4'-di-tert-butoxanilide and mixtures of ortho- and para- methoxy-disubstituted oxanilides and mixtures of o- and p-etiioxy-disubstituted oxani- lides. 2.8. 2-(2-Hvdroxyphenyl)-l,3,5-triazines, for example 2,4,6-tris(2-hydroxy-4-octyloxy- phenyl)- 1 ,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)- 1 ,3,5-triazine, 2-(2,4-dihydroxyphenyl)-4,6-bis(2,4-dimetiιylphenyl)- 1 ,3,5-triazine, 2,4-bis(2-hydroxy-4-propyloxyphenyl)-6-(2,4-dimethylphenyl)-l,3,5-triazine, 2-(2-hy- droxy-4-octyloxyphenyl)-4,6-bis(4-methylphenyl)-l,3,5-triazine, 2-(2-hydroxy-4-dodecyl- oxyphenyl)-4,6-bis(2,4-dimethylphenyl)- 1 ,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy- 3-butyloxy-propoxy)phenyl]-4,6-bis(2,4-dimetiιyl)- 1 ,3,5-triazine, 2-[2-hydroxy-4-(2- hydroxy-3-octyloxy-propyloxy)phenyl]-4,6-bis(2,4-dimedιyl)-l,3,5-triazine. 3. Metal deactivators, for example N-N'-diphenyloxamide, N-salicylal-N'-salicyloyl hydrazine, N,N'-bis(salicyloyl) hydrazine, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenyl- propionyl) hydrazine , 3-salicyloylamino-l,2,4-triazole, bis(benzylidene)oxalyl di¬ hydrazide, oxaniUde, isophti aloyl dihydrazide, sebacoyl bisphenylhydrazide, N,N'-di- acetyladipoyl dihydrazide, N,N'-bis(salicyloyl)oxalyl dihydrazide, N,N'-bis(salicyloyl)- thiopropionyl dihydrazide. 4. Peroxide scavengers, for example esters of β-thiodipropionic acid, for example the lauryl, stearyl, myristyl or tridecyl esters, mercaptobenzimidazole or the zinc salt of 2-mercaptobenzimidazole, zinc dibutyldidiiocarbamate, dioctadecyl disulfide, penta- erythritol tetrakis(β-dodecylmercapto)propionate. 5. Polyamide stabilisers, for example, copper salts in combination with iodides and/or phosphorus compounds and salts of divalent manganese. 6. Basic co-stabilisers, for example, melamine, polyvinylpyrroUdone, dicyandiamide, tri- allyl cyanurate, urea derivatives, hydrazine derivatives, amines, polyamides, polyure- thanes. 7. Nucleating agents, for example, 4-tert-butylbenzoic acid, adipic acid, diphenylacetic acid, sodium benzoate and aluminium-bis-4-(l,l-dimethylethyl)benzoatehydroxide. 8. Fillers and reinforcing agents, for example, siUcates, glass fibres, talc, kaolin, mica, barium sulfate, metal oxides and hydroxides, carbon black, graphite. 9. Other additives, for example, plasticisers, lubricants, emulsifiers, pigments (such as titanium dioxide), optical brighteners, flameproofing agents, antistatic agents, blowing agents, adhesion promoters, dyes. 10. Benzofuranones and indolinones, for example those disclosed in US-A-4 325 863, US-A-4 338 244 or US-A-5 175 312, US-A-5 216 052, US-A-5 252 643, DE-A-4 316 611, DE-A-4 316 622, DE-A-4 316 876, EP-A-0 589 839 or EP-A-0 591 102, or 3-[4-(2-acet- oxyethoxy)phenyl]-5,7-di-tert-butyl-benzofuran-2-one, 5,7-di-tert-butyl-3-[4-(2-stearoyl- oxyethoxy)phenyl]benzofuran-2-one, 3,3'-bis[5,7-di-tert-butyl-3-(4-[2-hydroxyetiιoxy]- phenyl)benzofuran-2-one] , 5,7-di-tert-butyl-3-(4-ethoxyphenyl)benzofuran-2-one, 3-(4- acetoxy-3,5-dimethylphenyl)-5,7-di-tert-butyl-benzofuran-2-one, 3-(3,5-dimethyl-4-piva- loyloxyphenyl)-5,7-di-tert-butyl-benzofuran-2-one. The preferred light stabilisers are those of the classes 2.1, 2.6 and 2.7 such as light stabilisers of the Chimassorb 944, Chimassorb 119, Tinuvin 234, Tinuvin 312, Tinuvin 622 or Tinuvin 770 type. If the polyester/polycarbonate blend is a recyclate, then d e blend can also be used in admixture with virgin material or together with virgin material, for example in a coextrusion process. These mixtures will be understood as comprising mixtures of, for example, a polyester recyclate with PC virgin material or polyester virgin material and PC recyclate, or the addition of PC virgin material or polyester virgin material to a polyester/PC recyclate blend. Further modifiers tiiat merit mention are the compounds usually employed for curing epoxy resins. Such modifiers include in particular: amides, amines, urea, urethanes, isocyanates, mercaptanes, alcohols, phenols, acids, acid anhydrides, silanes or silanols; typical examples thereof are: 4,4'-diaminodiphenylsulfone, dicyandiamide, N-phenyl-N-butyl-4-methylbenzenesulfonamide, 4,4'-methylenebis(phenylcyanamide), N,N'-dicyanopiperazine, toluene-2,4-diisocyanate, polyglycoldiamine, tris(mercaptoethyl)trioxane, hexahydrophdialic anhydride, pyromelUtic dianhydride and trimethylchlorosilane. The addition of photoinitiators such as diazonium salts and triarylsulfonium salts also merits mention. The present invention also relates to the use of a mixture comprising a) at least one phosphite, b) at least one sterically hindered phenol, c) at least one compound promoting the reaction of an epoxy resin with a PES/PC blend, and d) at least one difunctional epoxy resin, for enhancing the properties of PES/PC blends and, more particularly, of PES/PC recyclates, 0.01 to 10 parts of component c) being used per 100 parts of PES/PC blend. The preferred embodiments of die use correspond to tiiose of the PES/PC blend. The invention also relates to a process for enhancing the properties of PES/PC blends or of PES/PC recyclates, which comprises heating the PES/PC blend, witii die addition of a) at least one phosphite, b) at least one sterically hindered phenol, c) at least one compound promoting the reaction of an epoxy resin with a PES/PC blend, and d) at least one difunctional epoxy resin, to above the melting point of the PES/PC blend, 0.01-10 parts of component c) being used per 100 parts of PES/PC blend. The preferred embodiments of me process correspond to those of die PES/PC blend. The process can be carried out in any heatable container equipped with a stirrer. The process is preferably carried out in an extruder or in a kneader. It is immaterial whetiier processing takes place in an inert atmosphere or in the presence of oxygen. The PES/PC blend to be heated and die components a), b), c) and d) are usually put into the apparatus when heating is started. However, a later addition is also possible, either by adding the component mixture or the individual components in any order. For this addition, the components a), b), c) and d) may be each independently of one anodier in the forni of powder, Uquid, granules or in compacted form or also on a substrate such as silica gel, or together with a polymer powder or wax, e.g. a polyethylene wax, but also in die form of a masterbatch. Heating to above die melting point is usually effected with stirring, until the components are homogenised. The temperature is governed by the PES/PC blend employed. Processing is preferably carried out in the temperature range from melting point to c. 50°C above the melting point. A suitable temperature range for PBT/PC is typically from 220 to 300°C, preferably from 230 to 280°C. Furthermore, where there is a PET component present, processing will preferably be carried out in the upper temperature range by reason of its higher melting point The invention is iUustrated by the following non-limitative Examples in which and in the remainder of die description, unless otherwise stated, parts and percentages are by weight. Examples 1-2: (Table 1) A PBT/PC blend (scrap material from lacquered car bumpers) is kneaded at 235°C over a period of 15 min at 30 rpm in an oil-heated mixing chamber W 50 (Brabender) and the melt flow rate (MFR) is then determined at 250°C/2.16 kg in accordance witii ISO 1133. Examples 3-5: (Table 2) PBT/PC virgin material (Pocan KV 1-7916/2, sold by Bayer, DE) is kneaded at 235°C over a period of 15 min at 40 rpm in an oil-heated mixing chamber W 50 (Brabender) and die melt flow rate (MFR) is then determined at 250°C/2.16 kg in accordance witii ISO 1133. Examples 6-9: (Table 3) A PBT/PC blend (production waste of form of a grinding stock) is kneaded at 235°C over a period of 15 min at 40 rpm in an oil-heated mixing chamber W 50 (Brabender) and die melt flow rate (MFR) is then determined at 250°C/2.16 kg in accordance witii ISO 1133. Table 1: Table 2: υ. Table 3: The compounds used in the Examples are: Araldit® GT 6071 (ciba; CH): diglycidyl ether of bisphenol A having an epoxy value of 2.15-2.22 eq/kg and a softening temperature from 70 to 75°C Araldit GY 281 (ciba; CH): liquid diglycidyl etiier of bisphenol F Araldit PY 306 (ciba; CH): diglycidyl ether of bisphenol F Irgafos® 12 (ciba; CH): Irgafos 168 (ciba; CH): tris(2,4-di-tert-butylphenyl)phosphite Irganox® 1010 (ciba; CH): pentaerythrityl ester of β- (3 ,5-di-teιt-butyl-4-hydroxyphenyl)propionic acid Irganox 1330 (ciba; CH): Irganox 1425 (ciba; CH): HO -i VCH Irganox 3114 (ciba; CH): l,3,5-tris(3',5'-di-tert.-butyl-4'-hydroxybenzyl)-isocyanurate Irganox B 225 (ciba; CH): 1:1 mixture of the pentaerythrityl ester of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid and tris(2,4-di-tert-butylphenyl)phosphite Irganox B 561 (ciba; CH): 1:4 mixture of the pentaerythrityl ester of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid and tris(2,4-di-tert-butylphenyl)phosphite Irganox B 900 (ciba; CH): 1:4 mixture of the octadecyl ester of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid and tris(2,4-di-tert-butylphenyl)phosphite Xonodit: calcium silicate hydrate

Claims: What is claimed is: 1. A polyester/polycarbonate blend (PES/PC blend), comprising a) at least one phosphite, b) at least one sterically hindered phenol, c) at least one compound promoting the reaction of an epoxy resin with a PES/PC blend, and d) at least one difunctional epoxy resin, 0.01 to 10 parts of component c) being used per 100 parts of PES/PC blend. 2. A PES/PC blend according to claim 1, which is a PES/PC recyclate. 3. A PES/PC blend according to eitiier claim 1 or claim 2, wherein component a) is a phosphite of one of the formulae R , R' 2 and R' 3 are each independendy of one anod er alkyl of 1 to 18 carbon atoms; alkyl of 1 to 18 carbon atoms which is substituted by halogen, -COOR 4 ', -CN or -00^4^4'; alkyl of 2 to 18 carbon atoms which is interrupted by -S-, -O- or -NR' - ; cycloalkyl of 5 to 8 carbon atoms, phenyl or naphthyl; phenyl or naphdiyl, each of which is substituted by halogen, 1 to 3 alkyl radicals or alkoxy radicals containing a total of 1 to 18 carbon atoms; 2,2,6,6-tetramethylpiperid-4-yl, N-allyl- or N-benzyl- or N-alkyl-2,2,6,6-tetramethyl- piperid-4-yl containing 1 to 4 carbon atoms in the alkyl moiety, or N-alkanoyl- 2,2,6,6-tetramethylpiperid-4-yl containing 1 to 4 carbon atoms in the alkyl moiety, or N-alkylene-2^,6,6-tetramethylpiperidyl orN-alkylene-4-alkoxy-2,2,6,6-tetramethyl- piperidyl containing 1 to 3 carbon atoms in the alkylene moiety and 1 to 18 carbon atoms in die alkoxy moiety, each R' 4 is independently hydrogen, alkyl of 1 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms, or phenylalkyl containing 1 to 4 carbon atoms in the alkyl moiety, n' is 2, 3 or 4, A', if n' or q = 2, is alkylene of 2 to 12 carbon atoms, alkylene of 2 to 12 carbon atoms which is interrupted by -S-, -O- or -NR' -, wherein R' has the given meaning, or a radical of formula A', if n' or q = 3, is a radical of formula - H^-r or N(CH 2 CH * 7 3 — , wherein r is 5 or 6, A', if n' = 4, is the radical of formula C(CH 2 "7 " , R 5 and R 6 are each independendy of die otiier hydrogen or alkyl of 1 to 8 carbon atoms, B is a radical of formula -CH 2 -, -CHR' 4 -, -CR^R , -S- or a direct bond, wherein R and R' 4 are as indicated, p is 1 or 2, D", if p = 1, is metiiyl and, if p = 2, is -CH 2 OCH 2 - > R' 9 is methyl, and R'ι 0 has the meaning of R^, q is 2 or 3, y is 1, 2 or 3, W, if y = 1, is alkyl of 1 to 18 carbon atoms, a radical of formula -OR' 16 , -NR' 17 R' 18 or fluoro, W, if y = 2, is a radical of formula -O-A"-O-, or W, if y = 3, is a radical of formula R^C^O^ , N(C 2 H 4 Oi 3 - or N(C 3 H 6 Cτ7 3 — , wherein R' has the given meaning, R' 16 has the meaning of R , R' 17 and R' j are each independently of the otiier alkyl of 1 to 18 carbon atoms, benzyl, cyclohexyl, a 2,2,6,6-tetra- or l,2,2,6,6-pentamethylpiperid-4-yl radical, or R' 17 and R' 18 , taken together, are butylene, pentylene, hexylene or the radical of formula -CH 2 CH 2 -O-CH 2 CH 2 -, A" has the meaning of A', if n' = 2, R' 19 is hydrogen or methyl, the substituents R' 1 are each independently of one anotiier hydrogen, alkyl of 1 to 9 carbon atoms or cyclohexyl, R'_ 5 is hydrogen or methyl, and Z is a direct bond, -CH 2 -, -C(R' 14 ) 2 - or -S- , wherein the substiments R'^ are identical or different and have die indicated meaning. 4. A PES/PC blend according to either claim 1 or claim 2, wherein component a) is a phosphite selected from die group consisting of tris(2,4-di-tert-butylphenyl)phosphite; 5. A PES/PC blend according to eitiier claim 1 or claim 2, wherein component b) is a sterically hindered phenol of formula π, wherein A is hydrogen, phenyl or a group -CH 2 -S-R 25 or D is C j -C^alkyl, -C^cycloalkyl, phenyl-C 1 -C 4 alkyl, phenyl or a group -CH^S-R^, X is hydrogen, -C b H 2b -CO-OR 2 , -C b H 2b -CO-N(R 29 )(R3o). -CH 2 N(R34)(R 3 5) , R is hydrogen or a group of formula -CO-CH=CH 2 , G* is hydrogen or Ci-C^alkyl, R 25 is C r C 18 alkyl, phenyl or a group -(CH 2 ) c -CO-OR 28 or -CH 2 CH 2 OR 33 , R 26 is hydrogen, C r C 18 alkyl, phenyl, benzyl or a group OH or -(CH 2 ) c -CO-OR 28 or -CH 2 -CH 2 -OR 33 , R 7 is C j ^oal yl or one of the groups -CHR 31 -CH 2 -S-R 32 , OH ] 3 , wherein Q is C 2 -Cgalkylene, C 4 -C 6 thiaalkylene or a group -CH 2 CH 2 (OCH 2 CH 2 ) d -, R 28 is C 1 -C 24 alkyl, R 29 is hydrogen, C j -C j galkyl or cyclohexyl, R 30 is C 1 -C 18 alkyl, cyclohexyl, phenyl; C r C 18 alkyl-substituted phenyl, or one of the or R 29 and R 30 , taken together, are C 4 -C 8 alkylene which may be interrupted by -O- or -NH-, R 31 is hydrogen, C 1 -C alkyl or phenyl, R 32 is C r C 18 alkyl, R 33 is hydrogen, C 1 -C 24 alkyl, phenyl, C 2 -C 18 alkanoyl or benzoyl, R 34 is C r C 18 alkyl, cyclohexyl, phenyl, C r C 18 alkyl-substituted phenyl, or a group R 35 is hydrogen, C 1 -C 18 alkyl, cyclohexyl or a group R 34 and R 35 , taken together, are C 4 -C 8 alkylene which may be substituted by -O- or -NH-, a is 0, 1, 2 or 3, b is 0, 1, 2 or 3, c is 1 or 2, d is 1 to 5, f is 2 to 8, and q is 1, 2, 3 or 4. 6. A PES/PC blend according to either claim 1 or claim 2, wherein component c), which promotes the reaction of an epoxy resin with a PES/PC blend, is selected from one of the foUowing groups consisting of: Cj) metal oxides, metal hydroxides or metal carbonates; c 2 ) metal salts of an organic acid; c 3 ) phosphates, phosphonates or phosphonites; c ) tertiary amines, quartemary ammonium salts, polyamines or polyamides; c 5 ) siUcates; and c 6 ) salts of sulfonic acids. 7. A PES/PC blend according to eitiier claim 1 or claim 2, wherein componente d) is an epoxy resin of the diglycidyl etiier of bisphenol A, diglycidyl terephthalate, diglycidyl etiier of bisphenol F, diglycidyl isophtiialate or triglycidyl trimeUate type, or 8. A PES/PC blend according to either claim 1 or claim 2, comprising 0.01 to 2 parts of component a), 0.01 to 3 parts of component b), 0.01 to 10 parts pf component c) and 0.01 to 5 parts of component d) per 100 parts of PES/PC blend. 9. A PES/PC blend according to eidier claim 1 or claim 2, comprising 0.01 to 1 part of component a), 0.01 to 1 part of component b), 0.05 to 1 part of component c) and 0.02 to 2 parts of component d) per 100 parts of PES/PC blend. 10. A PES/PC blend according to either claim 1 or claim 2, wherein the PES/PC blend is based on PBT/PC, PBT/PC/ABS or PBT/PC/ASA. 11. A PES/PC blend according to either claim 1 or claim 2, wherein the PES/PC blend is a PBT/PC blend. 12. Use of a mixture comprising a) at least one phosphite, b) at least one stericaUy hindered phenol, c) at least one compound promoting the reaction of an epoxy resin with a PES/PC blend, and d) at least one difunctional epoxy resin, for enhancing the properties of PES/PC blends and, in particular, of PES/PC recyclates, and which comprises using 0.01 to 10 parts of component c) per 100 parts of PES/PC blend. 13. A process for enhancing the properties of PES/PC blends, which comprises heating a PES/PC blend with the addition of a) at least one phosphite, b) at least one sterically hindered phenol, c) at least one compound promoting the reaction of an epoxy resin with a PES/PC blend, and d) at least one difunctional epoxy resin, to above the melting point of the PES/PC blend, 0.01 to 10 parts of component c) being used per 100 parts of PES/PC blend. 14. A PES/PC blend obtainable in accordance witii the process according to claim 13.

Inventors: HERBST HEINZ, HOFFMANN KURT, PFAENDNER RUDOLF, HERBST, HEINZ, HOFFMANN, KURT, PFAENDNER, RUDOLF
Applicants: CIBA GEIGY AG, HERBST HEINZ, HOFFMANN KURT, PFAENDNER RUDOLF, CIBA-GEIGY AG, HERBST, HEINZ, HOFFMANN, KURT, PFAENDNER, RUDOLF
Application year: 1995
Main classification: C08K5
IPC codes: C08K3, C08K5, C08L63, C08L67, C08L69, C08L77, C08L79