Method for heating glass sheets to be tempered or heat-strengthened

Abstract: The invention relates to a method for heating glass sheets to be tempered or heat-strengthened, in which method glass sheets are heated in a preheating furnace (1) by applying a hot-air blast and convection heating produced thereby to the opposite sides of a glass sheet and the preheated glass sheet is transferred from the preheating furnace (1) into a radiation heating furnace (2) for heating the glass sheet to a tempering temperature. During the convection heating of a glass sheet, the rotating speed of a hot-air fan (5) is increased while adjusting the heating effect of heating resistances (6) so as to maintain the temperature of blasted air substantially constant. Thus, the diminishing temperature difference between glass and air is compensated for by controlling the coefficient of heat transfer.

Description: The present invention relates to a method for heating glass sheets to be tempered or heat-strengthened, in which method glass sheets are heated in a preheating furnace by applying a hot-air blast and convection heating produced thereby to the opposite sides of a glass sheet and the preheated glass sheet is transferred from the preheating furnace into a radiation heating furnace for heating the glass sheet to a tempering temperature. In such prior known tempering furnaces, a drawback involved in preheating is that the heating efficiency deteriorates as the glass temperature rises. Thus, the preheating station is not capable of reaching a very high temperature or, alternatively, the heating time increases unacceptably. EP-A-592862 discloses a method and a furnace for bending glass sheets. Glass sheets are heated to a bending temperature by supporting them on a ring mold and carrying them from one heat station to another. In the heat and bending station, the glass sheet is heated for effecting a desired bending partially or entirely through the action of gravity. During the bending operation, the temperature distribution of radiation heat is adjusted. In at least one of the heating stations for preheating, prebending or bending, the glass sheet is subjected to the action of convection blasting (forced convection) in addition to the radiant heat from electric resistance heaters mounted above the glass sheet. Consequently, the disclosure of EP592862 relates to a bending furnace rather than a tempering furnace. Heat recovery sections are disclosed, wherein air is circulated for convection heating and preheating sections, where radiation heating is assisted by forced convection. US-A-5,085,580 discloses a preheater for preheating flat glass sheets prior to further heating to a higher temperature within a furnace in preparation for further processing, such as bending and tempering or other similar processing. In the disclosed tempering, a bending furnace having a preheating furnace, the heating is effected by hot air convection heating. There is no disclosure of adjusting the rotating speed of the hot air blowers. An object of the invention is to improve this type of tempering method, such that the preheating can be intensified and expedited even though the air temperature is maintained substantially constant. This object is achieved on the basis of the characterizing features set forth in the annexed claim 1. The invention will now be described in more detail by way of an example with reference made to the accompanying drawing, in which fig. 1 is a schematic vertical section, showing a tempering furnace for implementing a method of the invention and fig. 2 shows schematically a detail in the preheating station of the furnace. The furnace comprises a preheating furnace 1 operating on the convection heating principle, a radiation heating furnace 2, and a cooling station 3 for tempering or heat-strengthening. The radiation heating furnace 2 is provided with resistance elements 10 on either side of a roll conveyor or just above a roll conveyor. The chilling station 3 is provided,with nozzle boxes 11 above and below a roll conveyor. The method may concern the tempering or heat-strengthening of flat glass or bent glass. Above and below a conveyor consisting of rolls 7, the pre-heating furnace 1 includes nozzle boxes 4 which are fitted with fans 5 for circulating hot air between the furnace interior and nozzles located adjacent to the surface of a glass sheet. The nozzle boxes 4 are provided with heating resistances 6 between the fan 5 and nozzle orifices. A temperature sensor 12 measuring the air temperature of furnace 1 uses a control device 13 for regulating the power received by the resistances 6, such that the air temperature in the furnace remains substantially constant at a certain set value. The air temperature is maintained within a range of 400-500°C, preferably at about 450°C. This temperature is about 100°C higher than in conventional preheating furnaces operating on the convection principle. An essential feature in the invention is that the temperature difference between the glass and the furnace air diminishing upon the heating of glass is compensated for by controlling the coefficient of heat transfer of convection blast. According to the invention, this control of the coefficient of heat transfer is effected by increasing the rotating speed of fans 5 included in nozzle boxes 4 as the glass is heating. The rotating speed may increase to about 6-fold during the course of preheating. The primary reason why the air temperature must be maintained constant is to prevent the heat expansion of furnace structures. The preheating must not involve at any stage too high a coefficient of heat transfer since the temperature difference between the core and the surface of glass must be maintained smaller than the temperature difference at which the glass breaks. Typically, this temperature difference is less than 50°C. A method of the invention enables the maintenance of a coefficient of heat transfer throughout the preheating process at an optimally high level, such that it is not too high at the start and ineffectively low at the end. An additional advantage gained by the invention is that, when preheating coated and reflecting glasses, the coefficients of heat transfer for both surfaces can be adjusted separately by adjusting separately the rotating speeds of hot-air fans blasting to the opposite surfaces of the glass so as to produce different coefficients of heat transfer for the opposite surfaces of the glass. The inverter operation of fan motors 8 controls automatically the rise of rotating speed, whereby a controller 9 can be used for setting the rotating-speed rising rates adapted to various glass thicknesses.

Claims: A method for heating glass sheets to be tempered or heat-strengthened, in which method glass sheets are heated in a preheating furnace (1) by applying a hot-air blast and convection heating produced thereby to the opposite sides of a glass sheet and the preheated glass sheet is transferred from the preheating furnace (1) into a radiation heating furnace (2) for heating the glass sheet to a tempering temperature, characterized in that , in view of adjusting the coefficient of heat transfer for convection heating, the rotating speed of a hot-air fan (5) is increased for increasing the volume flow of blast as the glass temperature rises. A method according to claim 1, characterized in that , during the convection heating of a glass sheet, the rotating speed of a hot-air fan (5) is increased while adjusting the heating effect of heating resistances (6) so as to maintain the temperature of blasted air substantially constant. A method as set forth in claim 1 or 2, characterized in that , the temperature of blasted air is maintained within the range of 400 - 500°C, preferably at about 450°C. A method as set forth in any of claims 1 to 3, characterized in that , a fan motor (8) is controlled by means of an inverter (9) which is adapted to increase the rotating speed according to a preset program depending on the glass thickness. A method as set forth in any of claims 1 to 3, characterized in that , the rotating speeds of the hot-air fans (5) blasting to the opposite glass surfaces are adjusted separately for producing, if necessary, different coefficients of heat transfer for the opposite glass surfaces.

Inventors: LEHTO ESKO, VEHMAS JUKKA, VITKALA JORMA, LEHTO, ESKO, VEHMAS, JUKKA, VITKALA, JORMA
Applicants: TAMGLASS ENG OY, TAMGLASS ENGINEERING OY
Application year: 1995
Main classification: C03B29
IPC codes: C03B29, C03B27