Process for polymerizing monomers in fluidized beds

Abstract: The invention is directed toward polymerizing or copolymerizing alpha-olefins either alone or in combination with one or more other alpha-olefins in the presence of a metallocene catalyst in a gas phase reactor having a fluidized bed and a fluidizing medium such that the fluidizing medium entering the reactor comprises a gas and a liquid phase.

Description: FIELD OF THE INVENTION The present invention relates to a process for the gas phase polymerization of olefins in the presence of a metallocene catalyst in fluidized bed reactors. The present invention allows for substantial savings in energy and capital cost by significantly increasing the polymer production rate capacity of a given sized reactor. BACKGROUND OF THE INVENTION The discovery of the process for the production of polymers in fluidized beds has provided a means for the production of a diverse array of polymers. Using a gas fluidized bed polymerization process substantially reduces the energy requirements as compared to other processes and most importantly reduces the capital investment required to run such a process to produce polymers. Gas fluidized bed polymerization plants generally employ a continuous cycle. In one part of the cycle, in a reactor a cycling gas stream is heated by the heat of polymerization. This heat is removed in another part of the cycle by a cooling system external to the reactor. Generally in a gas fluidized bed process for producing polymers from alpha-olefin monomers a gaseous stream containing one or more monomers is continuously passed through a fluidized bed under reactive conditions in the presence of a catalyst. This gaseous stream is withdrawn from the fluidized bed and recycled back into the reactor. Simultaneously, polymer product is withdrawn from the reactor and new monomer is added to replace the reacted monomer. It is important to remove heat generated by the reaction in order to maintain the temperature of the gaseous stream inside the reactor at a temperature below the polymer and catalyst degradation temperatures. Further, it is important to prevent agglomeration or formation of chunks of polymer that cannot be removed as product. This is accomplished through control of the temperature of the gaseous stream in the reaction bed to a temperature below the fusion or sticking temperature of the polymer particles produced during the polymerization reaction. Thus, it is understood that the amount of polymer produced in a fluidized bed polymerization process is related to the amount of heat that can be withdrawn from a reaction zone in a fluidized bed within the reactor. Conventionally, heat has been removed from the gaseous recycle stream by cooling the stream outside the reactor. A requirement of a fluidized bed process is that the velocity of the gaseous recycle stream be sufficient to maintain the fluidized bed in a fluidized state. In a conventional fluidized bed reactor, the amount of fluid circulated to remove the heat of polymerization is greater than the amount of fluid required for support of the fluidized bed and for adequate mixing of the solids in the fluidized bed. However, to prevent excessive entrainment of solids in a gaseous stream withdrawn from the fluidized bed, the velocity of the gaseous stream must be regulated. Also, in a steady state fluidized bed polymerization process wherein the heat generated by the polymerization reaction is substantially proportional to the rate of polymer production, the heat generated is equal to the heat absorbed by the gaseous stream and lost by other means such that the bed temperature remains constant. For a time, it was thought that the temperature of the gaseous stream external to the reactor otherwise known as the recycle stream temperature could not be decreased below the dew point of the recycle stream. The dew point of the recycle stream is that temperature at which liquid condensate begins to form in the gaseous recycle stream. It was believed that introducing a liquid into a gas phase recycle stream in a fluidized bed polymerization process would inevitably result in plugging of the recycle stream lines, the heat exchanger, the area below the fluidized bed or the gas distributor plate. As a consequence of operating at a temperature above the dew point of the recycle stream to avoid the problems associated with liquid being in the gaseous recycle stream, production rates in commercial reactors could not be significantly increased without enlarging reactor diameters. In the past there was concern that excessive amounts of liquid in the recycle stream would disrupt the fluidization process to the extent that the fluidized bed would collapse resulting in the sintering of solid polymer particles into a solid mass causing the reactor to shut down. This widely held belief to avoid liquid in the recycle stream can be seen from the following: U.S. Patent Nos. 3,922,322, 4,035,560, 4,359,561 and 5,028,670 and European Patent Application Nos. 0 050 477 and 0 100 879. Contrary to this belief, it has been demonstrated, as disclosed by Jenkins, III, et al. in U.S. Patent No. 4,543,399 and related U.S. Patent No. 4,588,790 that a recycle stream can be cooled to a temperature below the dew point in a fluidized bed polymerization process resulting in condensing a portion of the recycle stream. The resulting stream containing entrained liquid is then returned to the reactor without the aforementioned agglomeration and/or plugging phenomena believed to occur when a liquid is introduced into a fluidized bed polymerization process. This process of purposefully introducing a liquid into a recycle stream or reactor is known in the industry as a "condensed mode" operation of a gas phase polymerization process. The above-mentioned U.S. patents to Jenkins, III, et al. disclose that when a recycle stream temperature is lowered to a point below its dew point in "condensed mode" operation, an increase in polymer production is possible, as compared to production in a non-condensing mode because of increased cooling capacity. Also, Jenkins, III, et al. found that a substantial increase in space time yield, the amount of polymer production in a given reactor volume, can be achieved by operating in "condensed mode" with little or no change in product properties. The liquid phase of the two-phase gas/liquid recycle stream mixture in "condensed mode" remains entrained or suspended in the gas phase of the mixture. The cooling of the recycle stream to produce this two-phase mixture results in a liquid/vapor equilibrium. Vaporization of the liquid occurs only when heat is added or pressure is reduced. The increase in space time yields achieved by Jenkins, III, et al. are the result of this increased cooling capacity of the recycle stream which, in turn, is due both to the greater temperature differential between the entering recycle stream and the fluidized bed temperature and to the vaporization of condensed liquid entrained in the recycle stream. Jenkins, et al. illustrate the difficulty and complexity of control in general and of trying to extend the stable operating zone to optimize the space time yield in a gas phase reactor. In Jenkins, et al. the recycle gas is cooled and added to the reactor at a temperature below the dew point so that condensed fluids evaporate inside the reactor. The cooling capacity of the recycle gas can be increased further while at a given temperature of the cooling heat transfer medium. One option described is to add non-polymerizing materials (isopentane) to increase the dew point. Because of greater cooling more heat can be removed and therefore higher space time yields are said to be possible. Jenkins, et al. recommends not exceeding 20 weight percent, preferably 2 to 12 weight percent, of condensed liquid in the recycle gas. Some of the potential hazards disclosed include the formation of "mud". maintaining a sufficiently high recycle gas speed or avoiding accumulation of liquid on a distributor plate. Jenkins, et al. is silent on where upper limits for non-polymerizable or polymerizable condensable materials lie and the question of how to optimize the space time yield using condensed mode. A gas fluidized bed reactor may be controlled to give the desired melt index and density for the polymer at an optimum production. Great care is generally taken to avoid conditions which can lead to formation of chunks or sheets or, in a worse case, an unstable fluidized bed which collapses, or causes polymer particles to fuse together. The control of a fluidized bed therefore has to be exercised to reduce chunking and sheeting and to prevent bed collapse or a need to terminate the reaction and shut down the reactor. This is the reason why commercial scale reactors are designed to operate well within proven stable operating zones, and why the reactors are used in a carefully circumscribed fashion. Even within the constraints of conventional, safe operation, control is complex adding further to the difficulty and uncertainty of experimentation if one wishes to find new and improved operating conditions. There are target values, determined by the polymer and the catalyst, for the operating temperature, the ratio of comonomer(s) to monomer and the ratio of hydrogen to monomer. The reactor and cooling system are contained within pressure vessels. Their contents are monitored, without unduly interfering with fluidization by measuring amongst others (1) the pressure at the top; (2) pressure differential at various heights along the bed, (3) temperature upstream of the bed; (4) temperature in the fluidized bed and temperature downstream of the bed as well as (5) the gas composition and (6) gas flow rate. These measurements arc used to control the catalyst addition, the monomer partial pressure and velocity of the recycle gas amongst others. Polymer removal is constrained in certain cases by the settled bulk density (non-fluidized) or the fluidized bulk density depending on plant design and these too must be watched as well as the ash level in the polymer. The plant is a closed system. In operation changes in the process of one or more of the measured values lead to consequential changes elsewhere. In the design of plant the optimization of capacity depends on the most restricting element in the overall design. There is no generally accepted view as to what causes chunking or sheeting. Obviously some fusing together of the polymer particles is involved, possibly because of insufficient heat transfer caused by inadequate fluidization in the fluidized bed. However, no clear correlations have thus far been found between individual settings and measurements and the occurrence of chunking and sheeting. The entirety of the measured values and controls is used therefore conventionally to stay within known, safe operating areas for a given plant design. Large scale gas phase plants are expensive and highly productive. Risks associated with experimentation in such plants are high because downtime is costly. Therefore it is difficult to explore design and operating boundaries experimentally in view of the costs and risks. It will be desirable to provide a method of determining a stable operating condition for gas fluidized bed polymerization to facilitate optimum design of the plant and the determination of desirable process conditions in a given plant design. It would also be desirable to provide a gas fluidized bed polymerization process giving a maximum reactor productivity. It is hence amongst the aims of the invention to help determine stable operating zones for a gas fluidized bed process and plant design, to find criteria for running a process safely with low risk of malfunction and at the same time high reactor productivities, and/or to avoid any constriction in the overall plant capacity due to the reactor productivity. SUMMARY OF THE INVENTION This invention relates to a process for polymerizing alpha-olefins in a gas phase reactor at significantly higher production rates than herefore envisaged. The invention is directed toward a process for polymerizing alpha-olefins in the presence of a metallocene catalyst in a gas phase reactor having a fluidized bed and a fluidizing medium where the level of liquid in the fluidizing medium is greater than 2 weight percent based on the total weight of the fluidizing medium as defined in claim 1. The invention is also directed toward a process for polymerizing alpha-olefins in the presence of a metallocene catalyst in a gas phase reactor having a fluidized bed and a fluidizing medium having a gas phase and a liquid phase entering the reactor as defined in claim 4. In a further embodiment the invention provides a continuous process for increasing reactor productivity of a gas phase polymerization reactor having a fluidizing medium and fluidized bed, said process comprising passing a gaseous stream comprising monomer through a reaction zone in the presence of a metallocene catalyst to produce a polymeric product, withdrawing said polymeric product, withdrawing said fluidizing medium comprising unreacted monomer from said traction zone, mixing said fluidizing medium with hydrocarbon and polymerizable monomer(s) to form a liquid and a gas phase, and recycling said fluidizing medium to said reactor as defined in claim 5. The foregoing objects, features, and advantages of this invention will become clearer and more fully understood when the following detailed description is read. DETAILED DESCRIPTION OF THE INVENTION This invention is not limited to any particular type or kind of polymerization or copolymerization reaction but is particularly well suited to the polymerization reactions involving the polymerization of one or more of the monomers, for example olefin monomers of ethylene, propylene, butene-1, pentene-1,4-methylpentene-1, hexene-1, octene-1 and styrene. Other monomers can include polar vinyl, conjugated and non-conjugated dienes, acetylene and aldehyde monomers. The catalysts employed in the improved process can include a metallocene component including single or multiple cyclopentadienyl components reacted with either a metal alkyl or alkoxy component or an ionic compound component. These catalysts can include partially and fully activated precursor compositions, those catalysts modified by prepolymerization or encapsulation and those catalysts supported on a carrier. Although, as previously stated, this present invention is not limited to any specific type of polymerization reaction, the following discussion of the operation of the improved process is directed to the gas phase polymerization of the olefin-type monomers, for example polyethylene, where this present invention has been found to be particularly advantageous. A significant increase in the reactor productivity is possible without an adverse effect on the product quality or properties. To achieve higher cooling capacities, and hence higher reactor productivity it may be desirable to raise the dew point of the recycle stream to permit a larger increase in the heat to be removed from the fluidized bed. For the purposes of this application, the terms "recycle stream" and "fluidizing medium" are interchangeable. The dew point of the recycle stream can be increased by increasing the operating pressure of the reaction/recycle system and/or increasing the percentage of condensable fluids and decreasing the percentage of non-condensable gases in the recycle stream in the manner disclosed by Jenkins, et al. U.S. Patent Nos. 4,588,790 and 4,543,399. The condensable fluid may be inert to the catalyst, reactants and the polymer product produced; it may also include comonomers. The condensable fluid can be introduced into the reaction/recycle system at any point in the system. For the purposes of this patent application the term condensable fluids include saturated or unsaturated hydrocarbons. Examples of suitable inert condensable fluids are readily volatile liquid hydrocarbons, which may be selected from saturated hydrocarbons containing from 2 to 8 carbon atoms. Some suitable saturated hydrocarbons are propane, n-butane, isobutane, n-pentane, isopentane, neopentane, n-hexane, isohexane, and other saturated C 6 hydrocarbons, n-heptane, n-octane and other saturated C 7 and C 8 hydrocarbons or mixtures thereof. The preferred inert condensable hydrocarbons are C 4 and C 6 saturated hydrocarbons. The condensable fluids may also include polymerizable condensable comonomers such as olefins, alpha-olefins, diolefins, diolefins containing at least one alpha-olefin or mixtures thereof including some of the aforementioned monomers which may be partially or entirely incorporated into the polymer product. In practicing the invention, the amount of gas in the recycle stream and the velocity of the recycle stream should be maintained at levels sufficient to keep the liquid phase of the mixture suspended in the gas phase until the recycle stream enters the fluidized bed, so that liquid does not accumulate in the bottom head of the reactor below the distributor plate. The velocity of the recycle stream must also be high enough to support and mix the fluidized bed within the reactor. It is also desirable that the liquid entering the fluidized bed be dispersed and vaporized quickly. Controlling the composition, temperature, pressure and superficial velocity of the gas in relation to the composition and physical characteristics of the polymer is important in maintaining a viable fluidized bed. A viable fluidized bed or a stable operating condition is defined as fluidized bed of particles that are suspended and well-mixed in a stable state under reactive conditions without the formation of significant quantities of agglomerates (chunks or sheets) which would disrupt the reactor or downstream process operations. In the one preferred embodiment more than 15 weight percent, preferably greater than 20 weight percent, of the recycle stream may be condensed, or be in a liquid phase without encountering disruption of the fluidization process provided that the safe operating boundaries of the stable operating zones determined with the help of fluidized bed bulk density measurements are not exceeded. During the polymerization process, a minor portion (typically less than about 10 percent) of the gaseous stream flowing upward through the fluidized bed reacts. The portion of the stream that does not react, i.e. the major portion, passes into a region above the fluidized bed called the freeboard zone which may be a velocity reduction zone. In the freeboard zone, the larger solid polymer particles which are projected above the bed by eruption of gas bubbles through the surface or entrained in the gas stream are allowed to fall back into the fluidized bed. The smaller solid polymer particles. known in the industry as "fines", are withdrawn along with the recycle stream because their terminal settling velocities are lower than the velocity of the recycle stream in the freeboard zone. The process operating temperature is set or adjusted to a temperature below the fusion or sticking temperature of polymer particles produced. Maintaining this temperature is important to prevent the plugging of the reactor by polymer chunks that grow rapidly if the temperature reaches high levels. These chunks of polymer can become too large to be withdrawn from the reactor as a polymer product and cause process and reactor failure. Also, chunks entering the downstream handling process of polymer product can disrupt, for example, transfer systems, drying units or extruders. The walls of the reactor can be treated in accordance with U.S. Patent No. 4,876,320. In one preferred embodiment of this invention, the entry point for the recycle stream is preferably below the lowest point of the fluidized bed so as to provide a uniform flow of the recycle stream throughout the reactor in order to maintain the fluidized bed in a suspended condition and to ensure uniformity of the recycle stream passing upwardly throughout the fluidized bed. In another embodiment of the present invention, the recycle stream can be divided into two or more separate streams, one or more of which can be introduced directly into the fluidized bed provided that the gas velocity below and throughout the fluidized bed is sufficient to keep the bed suspended. For example, the recycle stream can be divided into a liquid and a gas stream which can then be separately introduced into the reactor. In the practice of the improved process of this invention, the recycle stream comprising a mixture of a gas phase and a liquid phase within the reactor below the distributor plate can be formed by separately injecting a liquid and a recycle gas under conditions which will produce a stream comprising both phases. The advantages of this invention are not limited to the production of polyolefins. Thus, this invention can be practiced in connection with any exothermic reaction carried out in a gas fluidized bed. The advantages of a process operating in condensed mode over other processes generally increase directly with the nearness of the dew point temperature of the recycle steam to the reaction temperature within the interior of the fluidized bed. For a given dew point, advantages of the process may increase directly with the percentage of liquid in the recycle stream returned to the reactor. The invention allows high percentages of liquid to be used in the process. The present invention is well suited for any conventional fluidized bed reaction systems. A gas fluidized bed reactor which is particularly well suited to production of polymers by the process of the present invention comprises a reaction zone and a freeboard zone which in this instance is also a velocity reduction zone. The height to diameter ratio of the reaction zone can vary depending on the desired production capacity and residence time. The reaction zone includes a fluidized bed comprising growing polymer particles, existing formed polymer particles and small amounts of catalyst. The fluidized bed in the reaction zone is supported by a recycle stream or fluidizing medium generally made up from feed and recycle fluids. The recycle stream enters the reactor through a distributor plate 18 in the bottom section of the reactor which aids in the uniform fluidization and the support of the fluidized bed in the reaction zone. In order to maintain the fluidized bed of reaction zone in a suspended and viable state, the superficial gas velocity of the gas flow through the reactor generally exceeds the minimum flow required for fluidization. Polymer particles in the reaction zone help to prevent the formation of localized "hot spots" and entrap and distribute catalyst particles throughout the fluidized bed. On start up the reactor is charged with a base of polymer particles before the recycle stream flow is introduced. These polymer particles are preferably the same as the new polymer particles to be produced, however, if different, they are withdrawn with the newly formed first product after initiation of recycle and catalyst flows and establishment of reaction. This mixture is generally segregated from the later essentially new production for alternate disposition. The catalysts used in the improved process of this invention are usually sensitive to oxygen, therefore, the catalyst is preferably stored in a catalyst reservoir under a blanket of a gas, inert to the stored catalyst, such as, but not limited to nitrogen or argon. Metallocene catalysts, for example, are typically those bulky ligand transition metal compounds derivable from the formula: [L] m M[A] n where L is a bulky ligand; A is leaving group and or a ligand bonded to M and capable of inserting an olefin between the M-A bond, M is a transition metal and m and n are such that the total ligand valency corresponds to the transition metal valency. Preferably the catalyst is four co-ordinate such that the compound is ionizable to a 1 + charge state. Any two L and/or A ligands may be bridged to each other. The metallocene compound may be full-sandwich compounds having two or more ligands L, which may be cyclopentadienyl ligands, cyclopentadiene derived ligands or substituted cyclopentadienyl ligands, or half-sandwich compounds having one ligand L, which is a cyclopentadienyl ligand or heteroatom substituted cyclopentadienyl ligand or hydrocarbyl substituted cyclopentadienyl ligand such as an indenyl ligand, a benzindenyl ligand or a fluorenyl ligand and the like or any other ligand capable of η 5 bonding to a transition metal atom (M). One or more of these bulky ligands is π - bonded to the transition metal atom. Each L can be substituted with a combination of substituents, which can be the same or different including hydrogen or a linear, branched or cyclic alkyl, alkenyl or aryl radicals for example. The metal atom (M) may be a Group 4, 5 or 6 transition metal or a metal from the lanthanide and actinide series, preferably the transition metal is of Group 4 particularly, titanium, zirconium and hafnium in any formal oxidation state, preferably, +4. In one embodiment, the transition metal is zirconium and the ring is a cyclopentadienyl ring substituted by two or more alkyl radicals, preferably two different alkyl radicals. Other ligands may be bonded to the transition metal, such as a leaving group, such as but not limited to weak bases such as amines, phosphines and, ether. In addition to the transition metal, these ligands may be optionally bonded to A or L. The metallocene catalyst is at least one metallocene catalyst component or metallocene catalyst compound described above containing one of more cyclopentadienyl moiety in combination with a transition metal. The metallocene catalysts that can be activated by an activator, such as an alumoxane or derivative thereof, an ionizing activator, a Lewis acid, or a combination thereof, to form an active polymerization catalyst system that can be supported on a carrier, typically an inorganic oxide or chloride or a resinous material such as polyethylene. Nonlimiting examples of metallocene catalysts and types of catalyst systems are discussed in for example U.S. Patent Nos. 4,808,561, 5,017,714, 5,055,438, 5,064,802, 5,124,418, 5,153,157 and 5,324,800. Fluidization of the fluidized bed in the reaction zone is achieved by the high rate at which the recycle stream flows into and through the reactor. Typically in operation, the rate of the recycle stream is approximately ten to fifty times the rate at which the feed is introduced into the recycle stream. This high rate of the recycle stream provides the superficial gas velocity necessary to suspend and mix the fluidized bed in the reaction zone in a fluidized state. The fluidized bed has a general appearance similar to that of a vigorously boiling liquid, with a dense mass of particles in individual motion caused by percolation and bubbling of gas through the fluidized bed. As the recycle stream passes through the fluidized bed in the reaction zone, there is a pressure drop. This pressure drop is equal to or slightly greater than the weight of the fluidized bed in the reaction zone divided by the cross-sectional area of the reaction zone, therefore making the pressure drop dependent on the reactor geometry. The make-up feed enters the recycle stream at, but not limited to, a point. A gas analyzer receives gas samples from the recycle stream line and monitors the composition of the recycle stream passing there through. The gas analyzer is also adapted to regulate the composition of the recycle stream line and the feed to maintain a steady state in the composition of the recycle stream in the reaction zone. The gas analyzer usually analyzes samples taken from the recycle stream line at a point between the freeboard zone and a heat exchanger, preferably, between a compressor and the heat exchanger. The recycle stream passes upward through the reaction zone adsorbing heat generated by this polymerization process. That portion of the recycle stream that does not react in the reaction zone exits the reaction zone and passes through the velocity reduction or freeboard zone. As previously described, in this region, the velocity reduction zone, a major portion of entrained polymer drops back into the fluidized bed in the reaction zone thereby reducing the carryover of solid polymer particles into the recycle stream line. The recycle stream once withdrawn from the reactor above the freeboard zone is then compressed in compressor and passes through the heat exchanger, where heat generated by the polymerization reaction and gas compression are removed from the recycle stream before returning the recycle stream back to the reaction zone in the reactor. The heat exchanger is conventional in type and can be placed within the recycle stream line in either a vertical or horizontal position. In an alternative embodiment of this invention, more than one heat exchanging zone or compression zone within the recycle stream line 16 may be included. The recycle stream upon exiting the heat exchanger returns to the bottom of the reactor. Preferably, a fluid flow deflector is positioned below the gas distributor plate. The fluid flow deflector prevents polymer from settling out into a solid mass and maintains entrainment of liquid and polymer particles within the recycle stream below the distributor plate. The preferred type of fluid flow deflector plate is annular disc in shape, for example, the type described in U.S. Pat. No. 4,933,149. Using an annular type disc provides both a central upward and outer peripheral flow. The central upward flow assists in the entrainment of liquid droplets in the bottom head and the outward peripheral flow assists in minimizing buildup of polymer particles in the bottom head. The distributor plate diffuses the recycle stream to avoid the stream entering the reaction zone in a centrally disposed upwardly moving stream or jet that would disrupt fluidization of the fluidized bed in the reaction zone. The temperature of the fluidized bed is set dependent on the particle sticking point but is basically dependent on three factors: (1) the catalyst activity and rate of catalyst injection which controls the rate of polymerization and the attendant rate of heat generation, (2) the temperature, pressure and composition of recycle and makeup streams introduced into the reactor and (3) the volume of the recycle stream passing through the fluidized bed. The amount of liquid introduced into the bed either with the recycle stream or by separate introduction as described previously especially affects the temperature because the liquid vaporizes in the reactor and serves to reduce the temperature of the fluidized bed. Usually the rate of catalyst addition is used to control the rate of polymer production. The temperature of the fluidized bed in the reaction zone in the preferred embodiment remains constant in a steady state by continuously removing the heat of reaction. A steady state of the reaction zone occurs when the amount of heat generated in the process is balanced with the amount of heat removed. This steady state requires that the total quantity of material entering the polymerization process is balanced by the amount of polymer and other material removed. Consequently, the temperature, the pressure, and the composition at any given point in the process is constant with time. There is no significant temperature gradient within most of the fluidized bed in the reaction zone, however, there is a temperature gradient in the bottom of the fluidized bed in the reaction zone in the region above the gas distributor plate. This gradient results from the difference between the temperature of the recycle stream entering through the distributor plate at the bottom of the reactor and temperature of the fluidized bed in the reaction zone. Efficient operation of the reactor requires good distribution of the recycle stream. Should growing or formed polymer and catalyst particles be allowed to settle out of the fluidized bed, fusion of the polymer can occur. This can result, in an extreme case, in the formation of a solid mass throughout the reactor. A commercial-sized reactor contains thousands of pounds or kilograms of polymer solids at any given time. The removal of a solid mass of polymer of this magnitude would entail great difficulty, requiring substantial effort and an extended downtime. By determining stable operating conditions with the help of fluidized bulk density measurement improved polymerization processes can be performed in which the fluidization and support of fluidized bed in the reaction zone within the reactor are maintained. In the preferred embodiment, variations in the fluidized bulk density for a given grade of polymer and/or catalyst composition are used to optimize process conditions and plant design. The fluidized bulk density is the ratio of the measured pressure drop upward across a centrally fixed portion of the reactor to the height of this fixed portion. It is a mean value which may be greater or less than the localized bulk density at any point in the fixed reactor portion. It should be understood that under certain conditions known to those skilled in the art, a mean value may be measured which is greater or less than the localized bed bulk density. Applicants have discovered that as the concentration of condensable component is increased in the gaseous stream flowing through the bed, an identifiable point may be reached beyond which there is danger of failure of the process if the concentration is further increased. This point is characterized by an irreversible decrease in the fluidized bulk density with an increase in condensable fluid concentration in the gas. The liquid content of the recycle stream entering the reactor may not be directly relevant. The decrease in fluidized bulk density generally occurs with no corresponding change in the settled bulk density of the final product granules. Thus, the change in fluidization behavior reflected by the decrease in fluidized bulk density apparently does not involve any permanent change in the characteristics of the polymer particles. The gas condensable fluid concentrations at which decreases in fluidized bulk density occur depend upon the type of polymer being produced and other process conditions. They may be identified by monitoring the fluidized bulk density as condensable fluid concentrations in the gas are increased for a given type of polymer and other process conditions. The fluidized bulk density (FBD) depends on other variables in addition to the condensable fluid concentration in the gas, including for example the superficial velocity of the gas flowing through the reactor, and the particle characteristics such as size, density and settled bulk density (SBD) as well as gas density, viscosity, temperature and pressure. Thus, in tests to determine changes in fluidized bulk density attributable to changes in gas condensable fluid concentration, significant changes in other conditions should be avoided. Therefore, it is within the scope of this invention to monitor these other variables from which fluidized bulk density can be determined, which affect bed instabilities. For the purposes of this application monitoring or maintaining fluidized bulk density includes monitoring or maintaining those variables described above that affect fluidized bulk density or are used to determine fluidized bulk density. While some modest drop in fluidized bulk density may be accommodated without the loss of control, further changes in gas composition or other variables which also increase the dew point temperature may be accompanied by an irreversible decrease in the fluidized bulk density, development of "hot spots" in the reactor bed, formation of fused agglomerates and eventual shutdown of the reactor. Other practical consequences directly related to the reduction of the fluidized bulk density include a reduced polymer capacity of a fixed-volume reactor discharge system and reduced polymer/catalyst reactor residence time at constant polymer production rate. The latter may. for a given catalyst, reduce the catalyst productivity and increase the level of catalyst residues in the product polymer. In a preferred embodiment it is desirable to minimize the condensable fluid concentration in the gas for a given target reactor production rate and associated cooling requirement. Using such fluidized bulk density variations, stable operating conditions can be defined. Once a suitable composition has been identified, the composition may be used to achieve much higher cooling capacities for the recycle stream (without encountering bed instabilities) by cooling that composition to a greater degree. Condensable, non-polymerizable materials may be added in appropriate amounts for a particular grade to achieve high tractor productivity whilst preserving good conditions in the fluidized bed by staying within the so determined stable operating zone. High reactor productivity can be achieved in a process or, in terms of plant design, a large capacity plant can be designed with a relatively small reactor diameter or existing reactors can be modified to provide increased capacity without changing the reactor size, see U.S. Patent No. 5,352,749, and US Patent 5 462 999. At higher reactor productivities it has been found that, staying within the boundaries defined by the acceptable fluidized bulk density changes, levels of condensed liquid well over, typically greater than 2%, 5%, 10%, 12%, 15%, 18%, 20%, 22%, 25%, 27%, 30% or even 35% can be accommodated whilst avoiding significant levels of chunking or sheeting resulting from fluidized bed disruption. The levels of condensed liquid based on the total weight of the recycle stream or fluidizing medium is in the range of between 2 to 50 weight percent, preferably greater than 10 to 50 weight percent and even more preferably 15 to 40 weight percent, still even more preferably 20 to 40, and most preferably 25 to 40 weight percent. Preferably the fluidized bulk density is observed by using a pressure difference measurement from a part of the fluidized bed not prone to disturbances over the distributor plate. Whereas, conventionally, fluidized bulk density variations in the lower part of the bed can be taken to be indicative of bed disruption over the distributor plate, with the upper fluidized bulk density measured remote from the distributor plate being used as a stable reference, it has now surprisingly been found that the changes in the upper fluidized bulk density correlate to change in the composition of the stream and can be used to find and define stable operating zones. The bulk density function (Z) is defined as wherein ρ bf is the fluidized bulk density, ρ bs is the settled bulk density, ρ g is the gas density, and ρ s is the solid (resin) density. The bulk density function (Z) can be calculated from process and product measurements. In the present invention, disruption of fluidization is avoided by maintaining the bulk density function (Z) value above about the minimum or limit values shown in the following Tables A and B based on the calculated values for X and Y. For the purposes of this patent specification and appended claims X and Y are defined according to the following equations: wherein d p is the weight average particle diameter, g is the gravity acceleration (9.805 m/sec 2 ). U o is the gas superficial velocity, and µ is the gas viscosity. For the purposes of this patent specification and appended claims the calculated limit of the bulk density function is based on the values for X and Y function as calculated using the formulas set forth above. The calculated limit is the number determined from Tables A and/or B using the calculated values for X and Y. Table A are the values for the calculated limit of the bulk density function for ranges for X and Y. Table B are the values for the calculated limit of the bulk density function for preferred ranges for X and Y. While the Tables A and/or B represent only selected point values for X and Y. one of ordinary skill in the art will recognize that it will generally be necessary to interpolate the values X and Y to obtain a corresponding limit Z value. In a preferred embodiment the bulk density function (Z) is maintained at a value greater than or equal, more preferably greater than, to the value provided in Tables A and/or B using the values for X and Y. In yet another embodiment the bulk density function (Z) is maintained at a level greater than 1% above the limit of the bulk density function value determined from Tables A and B and more preferably greater than above 2%, even more preferably greater than above 4% and most preferably greater than above 5%. The particle diameter (d p ) can be in the range of from 100 to 3000 microns 1 micron = 1 micrometer, preferably from 500 to 2500 microns, more preferably from 500 to 2000 microns, most preferably from 500 to 1500 microns. The gas viscosity (µ) can be in the range of from 0.01 to 0.02 centipose (cp), preferably 0.01 to 0.18 cp and most preferably 0.011 to 0.015 cp (1 centipoise = 1 mPa·s). The settled bulk density (SBD) or (ρ bs ) can be in the range of from 10 to 35 lb/ft 3 (160.2 to 561 kg/m 3 ), preferably from 12 to 35 lb/ft 3 (193 to 561 kg/m 3 ), more preferably from 14 to 32 lb/ft 3 (224.3 to 513 kg/m 3 ) and most preferably from 15 to 30 lb/ft 3 (240.3 to 481 kg/m 3 ). The gas density (ρ g ) can be in the range of from 0.5 to 4.8 lb/ft 3 (8 to 77 kg/m 3 ), preferably from 1 to 4 lb/ft 3 (16 to 64.1 kg/m 3 ). more preferably from 1.1 to 4 lb/ft 3 (17.6 to 64.1 kg/m 3 ) and most preferably from 1.2 to 3.6 lb/ft 3 (19.3 to 57.9 kg/m 3 ). The solid resin density (ρ s ) can be in the range of 0.86 to 0.97 g/ml, preferably in the range of 0.87 to 0.97 g/ml, more preferably in the range of 0.875 to 0.970 g/ml and most preferably in the range of 0.88 to 0.97 g/ml. The reactor temperature can be between 60 and 120°C, preferably 60 to 115°C and most preferably in the range of 70 to 110°C. The reactor pressure can be 100 to 1000 psig (689.5 to 6895 kPag), preferably 150 to 600 psig (1034 to 4137 kPag), more preferably 200 to 500 psig (1379 to 3448 kPag) and most preferably between 250 to 400 psig (1724 to 2758 kPag). LIMIT BULK DENSITY FUNCTION Y 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5 6.0 6.5 7.0 7.5 8.0 X 0.3 0.411 0.4 0.403 0.5 0.393 0.6 0.381 0.7 0.367 0.460 0.8 0.351 0.450 0.9 0.332 0.437 1.0 0.311 0.422 0.522 1.1 0.289 0.404 0.510 1.2 0.265 0.384 0.496 1.3 0.239 0.361 0.480 1.4 0.214 0.336 0.460 0.561 1.5 0.188 0.309 0.438 0.546 1.6 0.281 0.413 0.529 1.7 0.252 0.386 0.508 0.598 1.8 0.223 0.355 0.484 0.582 1.9 0.324 0.457 0.563 2.0 0.291 0.427 0.541 0.620 2.1 0.258 0.394 0.516 0.602 2.2 0.226 0.360 0.487 0.581 2.3 0.324 0.455 0.557 0.633 2.4 0.288 0.421 0.529 0.614 2.5 0.252 0.384 0.497 0.590 2.6 0.346 0.462 0.563 0.635 2.7 0.307 0.425 0.533 0.614 2.8 0.270 0.385 0.499 0.588 2.9 0.339 0.461 0.559 0.628 3.0 0.299 0.422 0.526 0.605 3.1 0.261 0.381 0.490 0.577 0.641 3.2 0.339 0.451 0.546 0.619 3.3 0.298 0.410 0.511 0.593 3.4 0.259 0.368 0.473 0.564 0.631 3.5 0.325 0.433 0.531 0.608 3.6 0.284 0.391 0.494 0.580 0.643 3.7 0.245 0.348 0.455 0.549 0.621 3.8 0.306 0.413 0.514 0.595 0.653 3.9 0.266 0.371 0.476 0.566 0.633 4.0 0.328 0.435 0.532 0.609 4.1 0.287 0.393 0.496 0.581 4.2 0.247 0.350 0.456 0.550 4.3 0.308 0.415 0.515 4.4 0.267 0.372 0.477 4.5 0.329 0.436 4.6 0.288 0.394 PREFERRED RANGE LIMIT BULK DENSITY FUNCTION Y 4.00 4.25 4.50 4.75 5.00 5.25 5.50 5.75 6.00 6.25 6.50 6.75 7.00 X 2.00 0.541 0.584 2.05 0.529 0.574 2.10 0.516 0.562 2.15 0.502 0.550 0.592 2.20 0.487 0.537 0.581 2.25 0.472 0.524 0.569 2.30 0.455 0.509 0.557 0.598 2.35 0.438 0.493 0.543 0.587 2.40 0.420 0.477 0.529 0.574 2.45 0.402 0.460 0.513 0.561 0.602 2.50 0.384 0.442 0.497 0.547 0.590 2.55 0.424 0.480 0.532 0.577 2.60 0.405 0.462 0.515 0.563 0.605 2.65 0.386 0.444 0.499 0.548 0.592 2.70 0.425 0.481 0.533 0.579 2.75 0.405 0.463 0.516 0.564 0.601 2.80 0.385 0.444 0.499 0.549 0.588 2.85 0.424 0.480 0.533 0.574 0.609 2.90 0.404 0.461 0.515 0.559 0.397 2.95 0.384 0.442 0.497 0.543 0.583 3.00 0.422 0.478 0.526 0.568 0.605 3.05 0.401 0.459 0.509 0.553 0.591 3.10 0.381 0.439 0.490 0.536 0.577 0.612 3.15 0.418 0.471 0.519 0.562 0.599 3.20 0.398 0.451 0.501 0.546 0.585 3.25 0.377 0.431 0.482 0.529 0.571 0.607 3.30 0.410 0.462 0.511 0.555 0.593 3.35 0.389 0.442 0.493 0.539 0.579 0.613 3.40 0.422 0.473 0.521 0.564 0.601 3.45 0.401 0.453 0.503 0.548 0.587 3.50 0.379 0.433 0.484 0.531 0.572 0.608 3.55 0.412 0.464 0.513 0.556 0.594 3.60 0.391 0.444 0.494 0.540 0.580 3.65 0.423 0.475 0.522 0.565 3.70 0.402 0.455 0.504 0.549 3.75 0.381 0.434 0.485 0.532 3.80 0.413 0.465 0.514 3.85 0.392 0.445 0.495 3.90 0.424 0.476 3.95 0.403 0.456 4.00 0.382 0.435 Advantageously the recycle stream is cooled and passes at a velocity through the reactor such that the cooling capacity is sufficient for a reactor productivity expressed in pounds (lbs) of polymer per hr/ft 2 of reactor cross-sectional area exceeding 500 lb/hr-ft 2 (2441 kg/hr-m 2 ), especially 600 lb/hr-ft 2 (2929 kg/hr-m 2 ) involving an eathalpy change of the recycle stream from the reactor inlet conditions to the reactor outlet conditions of at least 40 Btu/lb (21.62 cal/g), preferably 50 Btu/lb (27.03 cal/g). Preferably, the liquid and gaseous component of the stream are added in a mixture below a reactor distributor plate. This reactor productivity is equal to the space time yield multiplied by the height of the fluidized bed. In the preferred embodiment of the present invention, the liquid introduced into the reactor 10 is vaporized in order to achieve the increased reactor cooling capacity benefits of this polymerization process. High levels of liquid in the bed may promote the formation of agglomerates which cannot be broken up by mechanical forces present in the bed, thus leading potentially to defluidization, bed collapse and reactor shutdown. In addition, the presence of liquids can influence local bed temperatures and affect the capability of the process to produce polymer having consistent properties, since this requires an essentially constant temperature throughout the bed. For these reasons, the amount of liquid introduced into the fluidized bed under a given set of conditions should not materially exceed the amount that will vaporize in the lower region of the fluidized bed, where mechanical forces associated with entry of the recycle stream through the distributor plate are sufficient to break up agglomerates formed by liquid-particle interaction. It has been discovered in this invention that, for given composition and physical characteristics of the product particles in the fluidized bed and otherwise given or related reactor and recycle conditions, by defining boundary conditions related to the composition of the gas flowing through the bed, a viable fluidized bed can be maintained at high cooling levels. While not wishing to be bound by any theory, applicants suggest that the observed decrease in fluidized bulk density may reflect an expansion of the dense particulate phase and change in bubble behavior within the fluidized bed. A catalyst activator, if required depending on the catalyst utilized, is generally added downstream from the heat exchanger . The catalyst activator may be introduced from a dispenser into the recycle stream. However, the improved process of this present invention is not limited to the location of the insertion of the catalyst activator or any other required components such as catalyst promoters. The catalyst from the catalyst reservoir can be injected either intermittently or continuously into the fluidized bed reaction zone at a preferred rate at a point which is above the gas distributor plate. In the preferred embodiment as described above, the catalyst is injected at a point where mixing with polymer particles within the fluidized bed is best accomplished. Because some catalysts are very active, the preferred injection into the reactor should be above the gas distributor plate not below. Injection of catalyst in the area below the gas distributor plate, may result in the polymerization of product in this area, which would result eventually in the plugging of the gas distributor plate. Also, introducing the catalyst above the gas distributor plate aids in the uniform distribution of catalyst throughout the fluidized bed and, therefore, helps to preclude the formation of "hot spots" resulting from high local catalyst concentrations. Injection is preferably into the lower portion of the fluidized bed in the reaction zone to provide uniform distribution and to minimize catalyst carryover into the recycle line where polymerization may lead to eventual plugging of the recycle line and heat exchanger. A variety of techniques for catalyst injection may be utilized in the improved process of this present invention, for example the technique described in U.S. Pat. No. 3,779,712. An inert gas such as nitrogen or an inert liquid that readily volatilizes under reactor conditions is preferably used to carry the catalyst into the fluidized bed reaction zone. The catalyst injection rate and monomer concentration in the recycle stream determines the rate of polymer production in the fluidized bed reaction zone. It is possible to control the production rate of the polymer produced by simply adjusting catalyst injection rate. In the preferred operating mode of the reactor utilizing the improved process of this present invention, the height of the fluidized bed in reaction zone is maintained by the withdrawal of a portion of the polymer product at a rate consistent with the formation of the polymer product. Instrumentation for detecting any temperature or pressure changes throughout the reactor and recycle stream are useful to monitor changes in the condition of the fluidized bed in the reaction zone. Also, this instrumentation allows for either the manual or automatic adjustment of the rate of catalyst injection and/or the temperature of the recycle stream. In operation of the reactor, the product is removed from the reactor through a discharge system. The discharge of polymer product is preferably followed by separating fluids from the polymer product. These fluids may be returned to the recycle stream line as a gas at point and/or as a condensed liquid at point. The polymer product is routed to downstream processing at point. In accordance with the present invention, a process is provided for increasing the reactor productivity of polymer production in a fluidized bed reactor employing an exothermic polymerization reaction by cooling the recycle stream to below its dew point and returning the resultant recycle stream to the reactor. The recycle stream containing greater than 15, preferably greater than 20 weight percent liquid can be recycled to the reactor to maintain the fluidized bed at a desired temperature. In the processes of the invention, the cooling capacity of the recycle stream or fluidizing medium may be significantly increased by both the vaporization of the condensed liquids entrained in the recycle stream and as a result of the greater temperature differential between the entering recycle stream and the fluidized bed temperature. In the preferred embodiment the polymers, homopolymers or copolymers, produced are selected from a film grade resin having a MI from 0.01 to 5.0, preferably 0.5 to 5.0 and a density of 0.900 to 0.930; or a molding grade resin having a MI of from 0.10 to 150.0, preferably 4.0 to 150.0 and a density of from 0.920 to 0.939; or a high density resin having a MI of from 0.01 to 70.0, preferably 2.0 to 70.0 and a density of from 0.940 to 0.970; all density units being in a g/cm 3 and the melt index being in g/10 min determined according to ASTM-1238 condition E. Depending on the target resin different recycle conditions may be adopted providing reactor productivity levels not previously envisaged. Firstly, there may be produced for example a film grade resin in which the recycle stream has a butene/ethylene mole ratio of from 0.001 to 0.60, preferably 0.30 to 0.50 or a 4-methyl-pentene-1/ethylene mole ratio of from 0.001 to 0.50, preferably 0.08 to 0.33 or a hexene/ethylene mole ratio of from 0.001 to 0.30, preferably 0.05 to 0.20; or an octene-1/ethylene mole ratio of from 0.001 to 0.10, preferably 0.02 to 0.07: a hydrogen/ethylene mole ratio of from 0.00 to 0.4, preferably 0.1 to 0.3; and an isopentane level of from 3 to 20 mol% or an isohexane level of from 1.5 to 10 mol% and in which the cooling capacity of the recycle stream is at least 40 Btu/lb (21.62 cal/g), preferably at least 50 but/lb (27.03 cal/g) or the weight percent condensed is at least 15, preferably greater than 20. Secondly, the process may be used to yield a molding grade resin in which the recycle stream has a butene-1/ethylene mole ratio of from 0.001 to 0.60, preferably 0.10 to 0.50 or a 4-methyl-pentene-1/ethylene mole ratio of from 0.001 to 0.50, preferably, 0.08 to 0.20 or a hexene/ethylene mole ratio of from 0.001 to 0.30, preferably 0.05 to 0.12 or an octene-1/ethylene mole ratio of from 0.001 to 0.10, preferably 0.02 to 0.04; a hydrogen/ethylene mole ratio of from 0.00 to 1.6, preferably 0.3 to 1.4; and an isopentane level of from 3 to 30 mol% or an isohexane level of from 1.5 to 15 mol% and in which the cooling capacity of the recycle stream is at least 40 Btu/lb (21.62 cal/g) preferably at least 50 Btu/lb (27.03 cal/g) or the weight percent condensed is at least 15, preferably greater than 20. Also, high density grades of resins may be made by a process in which the recycle stream has a butene-ethylene mole ratio of 0.001 to 0.30, preferably 0.001 to 0.15 or a 4-methyl-pentene-1/ethylene mole ratio of from 0.001 to 0.25, preferably 0.001 to 0.12 or a hexene/ethylene mole ratio of 0.001 to 0.15, preferably 0.001 to 0.07 or an octene-1/ethylene mole ratio of from 0.001 to 0.05, preferably 0.001 to 0.02; a hydrogen to ethylene mole ratio of 0.00 to 1.5, preferably 0.3 to 1.0; and an isopentane level of from 10 to 40 mol% or an isohexane level of from 5 to 20 mol% and in which the cooling capacity of the recycle stream is at least 60 Btu/lb (32.4 cal/g) preferably greater than 73 Btu/lb (39.42 cal/g), and most preferably greater than at least about 75 Btu/lb (40.5 cal/g) of the weight percent condensed is at least 12, preferably greater than 20. EXAMPLES In order to provide a better understanding of the present invention including representative advantages and limitations thereof, the following examples are offered as related to actual tests performed in the practice of this invention. EXAMPLE 1 A fluidized gas phase reactor was operated to produce a copolymer of ethylene and hexene-1. The metallocene catalyst was prepared from silica dehydrated at 600 °C. The catalyst was a commercial scale catalyst prepared in a mixing vessel with and agitator. An initial charge of 1156 pounds(462 Kg) toluene was added to the mixer. This was followed by mixing 925 pounds (421Kg) of 30 percent by weight methyl aluminoxane in toluene. This was followed with 100 pounds(46 Kg)of 20 percent by weight bis(1,3-methyl-n-butyl cyclopentadienyl) zirconium dichloride in toluene (20.4 pounds (9.3Kg) of contained metallocene). An additional 144 pounds (66Kg) of toluene was added to the mixer to rinse the metallocene feed cylinder and allowed to mix for 30 minutes at ambient conditions. This was followed by 54.3 pounds (25 Kg) of an AS-990 in toluene, surface modifier solution, containing 5.3 pounds (2.4 Kg) of contained AS-990. An additional 100 pounds (46Kg) of toluene rinsed the surface modifier container and was added to the mixer. The resulting slurry was vacuum dried at 3.2 psia (70.6kPa) at 175 °F (79 °C) to a free flowing powder. The final catalyst weight was 1093 pounds (497Kg). The catalyst had a final zirconium loading of 0.40% and an aluminum loading of 12.0%. The polymerization was conducted in a commercial scale continuous gas phase fluidized bed reactor. The fluidized bed is made up of polymer granules. The gaseous feed streams of ethylene hydrogen are introduced below the reactor bed into the recycle gas line. Hexene comonomer is introduced below the reactor bed in a separate line to the recycle gas line. An inert hydrocarbon such as isopentane is also introduced to the reactor in the recycle gas line. The isopentane is added to provide additional heat capacity to the reactor recycle gases. The individual flow rates of ethylene, hydrogen and comonomer were controlled to maintain fixed composition targets. The ethylene concentration was controlled to maintain a constant hydrogen to ethylene ratio. The concentration of the gases were measured by an on-line gas chromatograph to ensure relatively constant composition in the recycle gas stream. Tri-ethyl aluminum (TEAL) as 20 percent by weight solution in isopentane carrier solvent was introduced into the fluidized bed for about 2 hours and 40 minutes at a rate of 32 lb/hr (14.5 kg/h) prior to the introduction of the catalyst. Once the catalyst feed began, TEAL introduction continued as above for about 1 hour and then was stopped. The total TEAL on bed was 122 ppm. The solid catalyst was injected directly into the fluidized bed using purified nitrogen. The catalyst rate was adjusted to maintain a constant production rate. The reacting bed of growing polymer particles is maintained in a fluidized state by a continuous flow of the make up feed and recycle gas through the reaction zone. The reactor was operated at a total pressure of 310 psig (2138kPa). To maintain a constant reactor temperature, the temperature of the recycle gas in continuously adjusted up or down to accommodate any changes in the rate of heat generation due to the polymerization. The fluidized bed was maintained at a constant height by withdrawing a portion of the bed at a rate equal to the formation of the particulate product. The product is removed semi-continuously via a series of valves into a fixed volume vessels. These fixed volume vessels are vented back to the reactor through a recycle gas compressor which recovers reactor gases. The product is transferred to a purger vessel to remove entrained hydrocarbons and treated with humidified nitrogen to deactivate the residual catalyst. Table 1, Run 1, is polymerization data from an actual operation. The data in Run 2 and 3 of Table 1 were prepared by extrapolating information from actual operation, Run 1, by using thermodynamic equations well known in the art to project target conditions. The fluidized bulk density function (Z) is not shown in Runs 2 and 3 for the reasons stated above, however, the calculated limit of the bulk density function is shown. Time (Hours) 1 2 3 Resin Melt Index (dg/10 min) 3.42 3.42 3.42 3.42 Resin Density (g/cc) 0.9179 0.9179 0.9179 0.9179 Recycle Stream Compositions: -- -- -- -- Ethylene 46.3 46.3 46.3 46.3 Butene-1 -- -- -- -- Hexene-1 0.9 0.9 0.9 0.9 Hydrogen (ppm) 250 250 250 250 Isopentane 11.5 15.0 18.0 18.0 C 6 Saturated Hydrocarbons Nitrogen 39.9 36.4 33.4 33.4 Ethane 0.3 0.3 0.3 0.3 Methane -- -- -- -- C 8 Saturated Hydrocarbons -- -- -- -- Recycle Gas Dew Point (°F) 137.7 152.7 163.7 163.7 Recycle Gas Dew Point (°C) 58.7 67.1 73.2 73.2 Reactor Inlet Temperature (°F) 113.6 100.0 100.0 100.0 Reactor Inlet Temperature (°C) 45.3 37.8 37.8 37.8 Liquid in Recycle gas (wt%) 10.4 22.5 29.0 29.0 Reactor Temperature (°F) 175.3 175.3 175.3 175.3 Reactor Temperature (°C) 79.6 79.6 79.6 79.6 Reactor Pressure (psig) 312.7 312.7 312.7 312.7 Reactor Pressure (kPag) 2156.0 2156.0 2156.0 2156.0 Reactor Superficial Gas Velocity (ft/sec) 2.12 2.12 2.12 2.50 Reactor Superficial Gas Velocity (m/sec) 0.65 0.65 0.65 0.76 Reactor Bed Height (ft) 43.4 43.4 43.4 43.4 Reactor Bed Height (m) 13.2 13.2 13.2 13.2 Resin Settled Bulk Density (lb/ft 3 ) 25.7 25.7 25.7 25.7 Resin Settled Bulk Density (kg/m 3 ) 411.7 411.7 411.7 411.7 Reactor Bed Fluidized Bulk Density (lb/ft 3 ) 19.2 -- -- -- Reactor Bed Fluidized Bulk Density (kg/m 3 ) 307.5 -- -- -- Space Time Yield (lb/hr-ft 3 ) 8.6 14.8 18.1 20.8 Space Time Yield (kg/hr-m 3 ) 137.5 236.5 289.3 333.1 Production Rate (klb/hr) 61.5 105.8 129.4 149.0 Production Rate (Tons/hr) 27.9 48.0 58.7 67.6 Reactor Productivity (lb/hr-ft 2 ) 373 641 784 902 Reactor Productivity (kg/hr-m 2 ) 1819 3129 3827 4406 Recycle Stream Enthalpy Change (Btu/lb) 37 58 66 66 Recycle Stream Enthalpy Change (cal/g) 20 32 37 37 Gas Density lb/ft 3 1.73 1.88 1.98 1.98 Gas Density kg/m 3 27.7 30.2 31.6 31.6 Gas Viscosity (cp) 0.014 0.013 0.013 0.013 Particle Size (inches) 0.042 0.042 0.042 0.042 Particle Size (microns) 1054 1054 1054 1054 X Function 3.13 3.20 3.22 3.29 Y Function 5.81 5.91 5.93 5.93 Density Function (Z) 0.70 -- -- -- Table A and B Limits 0.54 0.53 0.53 0.50 It is within scope of this invention to utilize a catalyst of increased activity to increase the rate of production or reduce the temperature of a recycle stream by employing refrigerator units. For this reason, then, references should be made solcly to the appended claims for purposes of determining the true scope of the present invention.

Claims: A process for polymerizing alpha-olefin(s) in the presence of a metallocene catalyst in a gas phase reactor having a fluidized bed and a fluidizing medium wherein the fluidizing medium servers to control the cooling capacity of said reactor, the process comprising employing in the fluidizing medium a level of liquid of staturated and/or unsaturated hydrocarbons entering the reactor which is greater than 2 weight percent and less than 50 weight percent based on the total weight of the fluidizing medium and calculating and maintaining the bulk density function (Z) at a value equal to or greater than the calculated limit of the bulk density function in Table A herein, in which X and Y in Table A are calculated according to the following equations: wherein ρ bf is the fluidized bulk density, ρ bs is the settled bulk density, ρ g is the gas density, and ρ s is the solid (resin) density and wherein d p is weight average particle diameter, g is the gravity accelaration (9.805 m/sec 2 ), U o is the gas superficial velocity, and µ is the gas viscosity. The process according to claim 1 in which the level of liquid is greater than 20 wt % based on the total weight of the fluidized medium. The process according to claim 1 or claim 2 in which the level of liquid is in the range from 25 to 40 wt % based on the total weight of the fluidizing medium. A process for polymerizing alpha-olefins in the presence of a metallocene catalyst in a gas phase reactor having a fluidized bed and a fluidizing medium having a gas phase and a liquid phase entering the reactor, said process comprising: a) controlling the cooling capacity of said fluidizing medium by controlling the ratio of said gas phase to said liquid phase: b) calculating the bulk density function limit; c) maintaining or monitoring the bulk density function (Z); and d) adjusting the bulk density function (Z) to maintain the bulk density function (Z) at a value greater than or equal to the calculated bulk density function limit wherein the bulk density function (Z) is calculated from the equation: limit and the limit of the bulk density function in as set out in Table A herein, in which X and Y in Table A are calculated according to the following equations: in which in the equations ρ bf is the fluidized bulk density, ρ bs is the settled bulk density, ρ g is the gas density, and ρ s is the solid (resin) density and wherein dp is weight average particle diameter, g is the gravity accelaration (9.805 m/sec 2 ), U o is the gas superficial velocity, and µ is the gas viscosity; A continuous process for increasing reactor productivity of a gas phase polymerization reactor having a fluidizing medium and fluidized bed, said process comprising passing a gaseous stream comprising monomer through a reaction zone in the presence of a metallocene catalyst to produce a polymeric product, withdrawing said polymeric product, withdrawing said fluidizing medium comprising unreacted monomer from said reaction zone, mixing said fluidizing medium with hydrocarbon and polymerizable monomer(s) to form a liquid and a gas phase, and recycling said fluidizing medium to said reactor, the process comprising: a) introducing said hydrocarbon into said fluidizing medium to permit an increase in the cooling capacity of the fluidizing medium above at least 40 Btu/lb (21.62 cal/g); b) increasing the rate of withdrawal of polymer product to above at least 500 lb/hr-ft 2 (2441 kg/hr-m 2 ); c) calculating the bulk density function limit (as herein defined); and d) maintaining a bulk density function (Z) value greater than or equal to the calculated limit of the bulk density function in Table A herein, in which X and Y in Table A are calculated according to the following equations: wherein ρ bf is the fluidized bulk density, ρ b s is the settled bulk density, ρ g is the gas density, and ρ s is the solid (resin) density and wherein d ρ is weight average particle diameter, g is the gravity acceleration (9.805 m/sec 2 ), U o is the gas superficial velocity, and µ is the gas viscosity; The process according to claim 5 in which the level of liquid is in the range of from 15 to 50 wt % based on the total weight of the fluidizing medium. The process according to claim 5 or claim 6 in which the level of liquid is in the range from 20 to 40 wt % based on the total weight of the fluidizing medium. The process in accordance with any of the preceding claims 5 to 7 wherein polymer product is withdrawn at a rate greater than 500 lb/hr-ft 2 (2441 kg/hr-m 2 ), preferably greater than 600 lb/hr-ft 2 (2929 kg/hr-m 2 ). The process in accordance with any of the preceding claims wherein the bulk density function (Z) is greater than 1 %, preferably 2 %, above the calculated limit of the bulk density function. The process in accordance with any of the preceding claims wherein said fluidizing medium comprises: i) butene-1 and ethylene at a molar ratio of from 0.001 to 0.60 or 4-methyl-pentene-1 and ethylene at a molar ratio of from 0.001 to 0.50 or hexene-1 and ethylene at a molar ratio of from 0.001 to 0.30 or octene-1 and ethylene at a molar ratio of from 0.001 to 0.10; ii) a condensable fluid comprising from 1.5 to 20 mole percent of the fluidizing medium, or i) butene-1 and ethylene at a molar ratio of from 0.001 to 0.60 or 4-methyl-pentene-1 and ethylene at a molar ratio of from 0.001 to 0.50 or hexene-1 and ethylene at a molar ratio of from 0.001 to 0.30 or octene-1 and ethylene at a molar ratio of from 0.001 to 0.10; ii) a condensable fluid comprising from 1.5 to 30 mole percent of the fluidizing medium, or i) butene-1 and ethylene at a molar ratio of from 0.001 to 0.30 or 1-methyl-pentene-1 and ethylene at a molar ratio of from 0.001 to 0.25 hexene-1 and ethylene at a molar ratio of from 0.001 to 0.15 or octene-1 and ethylene at a molar ratio of from 0.001 to 0.05; ii) a condensable fluid comprising from 5 to 40 mole percent of the fluidizing medium. The process in accordance with any of the preceding claims wherein the gas phase enters the reactor separate, and apart from the liquid phase and/or wherein the liquid phase enters the reactor below the distributor plate. The process in accordance with any of the preceding claims 5 to 11 wherein the ratio of the fluidized bulk density to settled bulk density is less than 0.59. The process in accordance with any of the preceding claims wherein the bulk density function (Z) is greater than or equal to (0.59-ρ g / ρ bs )/ (1-ρ g /ρ s ), wherein ρ bf is the fluidized bulk density, ρ bs is the settled bulk density, ρ g is the gas density, ρ s is the solid (resin) density. The process in accordance with any preceding claims wherein where the fluidizing medium passing through the fluidized bed comprises a dew point increasing component in an amount greater than 2.0 mole percent, the ratio of the fluidized bulk density to settled bulk density is not above 0.59.

Inventors: DECHELLIS MARC LOUIS, GRIFFIN JOHN ROBERT, MUHLE MICHAEL ELROY, DECHELLIS, MARC LOUIS, GRIFFIN, JOHN ROBERT, MUHLE, MICHAEL ELROY
Applicants: EXXONMOBIL CHEM PATENTS INC, EXXONMOBIL CHEMICAL PATENTS INC.
Application year: 1995
Main classification: C08F10
IPC codes: C08F210, C08F10, C08F4, C08F2