Thermoplastic composition with filler and polyalkylene glycol

Abstract: The invention deals with compositions comprising (A) a resin selected from polycarbonates, polyestercarbonates, polyethylene terephthalate, polybutylene terephthalates, polycyclohexyl terephthalates, polyetheresters, polyesteramides, copolymers of any of the mentioned resins and mixtures of two or more of the mentioned resins or copolymers; (B) from 10-85% by weight of a filler, selected from zinc oxide, barium sulfate, zirconium oxide, zirconium silicate and mixtures of two or more of the mentioned fillers. It has been found that by incorporating a specific type of ingredient i.e. a polyalkylene glycol homopolymer or copolymer the surface properties of objects formed out of the compositions can be improved. In particular the cleanability can be improved and the tendency to marking and staining can be reduced.

Description: The present invention deals with a composition which comprises: (A) a resin selected from polycarbonates, polyestercarbonates, polyethylene terephthalates, polybutylene terephthalates, polycyclohexyl terephthalates, polyetheresters, polyesteramides, copolymers of any of the mentioned resins and mixtures of two or more of the mentioned resins or copolymers; (B) from 10-85% by weight of a filler, selected from zinc oxide, barium sulfate, zirconium oxide, zirconium silicate and mixtures of two or more of the mentioned fillers. Compositions comprising components A and B are known from EP-A-423 508; EP-A-423 509 and EP-A-423 510. The known compositions possess a unique combination of properties as indicated in above mentioned patent applications. The compositions described in above mentioned patent applications have been used for forming parts by injection molding or by extrusion. One application lies in the use of the known compositions for the extrusion of sheet products. It has been found that the surface quality of the objects formed out of the compositions according to the invention can be further improved by incorporating in the composition a polyalkylene glycol (C). By incorporating a component C the cleanability of the surface improved and the tendency to staining and marking can be reduced. By incorporating a component C the impact strength could also be improved. The invention thus relates to compositions which besides above mentioned components A and B further comprise: (C) from 0.1-4% by weight of a polyalkylene glycol homopolymer or copolymer, wherein all quantities have been calculated with respect to the total weight of components A, B and C. Detailed description of the invention. The composition of the invention comprises at least the following three types of constituents: A. a resin as indicated in claim 1, B. a filler as indicated in claim 1 and C. a polyalkylene glycol homopolymer or copolymer. A. Resin The composition of the invention comprises a resin selected from (A) a resin selected from polycarbonates, polyestercarbonates, polyethylene terephthalates, polybutylene terephthalates, polycyclohexylterephthalates, polyetheresters, polyesteramides, copolymers of any of the mentioned resins and mixtures of two or more of the mentioned resins or copolymers; The above mentioned resins are well known polymers which have been described extensively in the literature. Particularly suitable are the polycarbonates or polyestercarbonates derived from bisphenol A. A preferred resin A in the composition of the invention comprises a blend of a polyethylene terephthalate, a polybutylene terephthalate and a polycarbonate. B. Filler The composition of the invention comprises a filler chosen from: zinc oxide, barium sulfate, zirconium oxide, zirconium silicate and mixtures of two or more of the mentioned fillers. A preferred filler is barium sulfate. The quantity of the filler (B) is 10-85% by weight, more preferably between 15-40% by weight. C. Polyalkylene glycol homopolymer or copolymer. Polyalkylene glycol homopolymers and copolymers and processes for making them are known per se. Preferred polyalkylene glycols are polyalkylene glycols with or without special endgroups (such as methoxygroups), polyethylene glycol, polyethylene propylene glycol copolymers, polypropylene glycol, copolymers of a polyalkylene glycol and polydimethylsiloxanes or mixtures of two or more said polyalkylene glycols. A silicone oil has the same beneficial effect as the polyalkylene glycol. A combination of a polyalkylene glycol and a silicone oil is suitable. The quantity of the polyalkylene glycol is chosen between 0.1-4% by weight, more preferably 0.5-2.5% by weight. The composition according to the invention can further comprise components such as fillers others than the ones listed as component B (for example talc), non-reinforcing fibers such as pigmented short fibers and reinforcing fibers such as glass fibers, stabilizers, anti-oxidants, lubricants, release agents, silicone oils, agents to improve the impact, flame retardants, pigments. Materials suitable as an agent to improve the impact include SBR, AB and ABA block copolymers such as Kraton and Kraton-G; styrene-butadiene modified acrylics; core-shell acrylics. These and other impact modifiers are described in US 4,034,013; 4,096,202 and 4,180,494 and in Modern Plastics Encyclopedia, 1988 Edition, page 160. Effective amounts range from 1-20% by weight of the total composition. Example I; comparative Examples A, II In the preparation of a blend according to the invention and of a blend for comparative purposes the following ingredients were used: PBT: a standard polybutylene terephthalate resin. PC: a standard polycarbonate resin derived from bisphenol A. PET: a standard polyethylene terephthalate resin BaSO 4 barium sulfate filler PEG: polyethylene glycol end-capped with hydroxylgroups; with a number average molecular weight of 3350. SEBS: a styrene - ethylene/butylene - styrene triblock copolymer. The styrene blocks have a weight average molecular weight of 27,000; the e/b-block of 126,000. STAB: a standard stabilizer package Sil: a polydimethylsiloxane fluid The indicated ingredients were compounded into a twin-screw extruder. The compounded product was pelletized. The pellets were injection molded into plaques (about 3,5 mm thick). Another quantity of pellets were extruded into sheet (about 2,5 mm thick). The surface quality in particular the tendency to marking and ease of cleaning (cleanability) was tested as follows: The test samples were first finished by treatment with: 60 and 30 micron sanding pads, # 7445 and #7441 3M Scotch-Brite pads, and a 3M buffing pad (in the indicated order). Testing carried out was fingernail marking i.e. scratching the surface with fingernails, with visual judgment of surface performance by a five person panel. The compositions and the results are shown in Table A herebelow: Example A I II Composition (parts by weight) . PBT 17 17 17 . PC 27.8 26.2 26.2 . PET 9.8 9.8 9.8 . BaSO 4 37 37 37 . PEG - 1 - . SEBS 7.5 7.5 7.5 . Sil - - 1 . ZnPO 4 - 0.6 0.6 . STAB 0.9 0.9 0.9 Properties Marking cleanability . of injection molded plaques 2 1 1 . extruded sheet 2 1 2 As can be seen from the results in the above table the compositions according to the invention have less tendency to marking and possess improved cleanability which is of importance for many applications. Example III and comparative Example B. The compositions of Example I and A were made for a second time. (Examples III and B respectively). The products obtained were extruded into sheet. The Izod unnotched impact strength was determined in accordance with ASTM D256, the Dynatup multi-axial impact was determined in accordance with ASTM D3763. The values were as follows (Table B). Example III B (Comparative) Impact strength: . Izod (kJ/m) 2.0 1.5 . Dynatup (J) 24.4 17.6 Staining tests with tomato - ketchup and red chili sauce showed that the composition of the invention has an improved cleanability. As can be seen the composition of the invention has a better impact strength. It has also been found that the surface of objects made out of the compositions according to the invention can be better glued to a wooden surface.

Claims: A thermoplastic composition which comprises: (A) a resin selected from polycarbonates, polyestercarbonates, polyethylene terephthalate, polybutylene terephthalates, polycyclohexyl terephthalates, polyetheresters, polyesteramides, copolymers of any of the mentioned resins and mixtures of two or more of the mentioned resins or copolymers; (B) from 10-85% by weight of a filler, selected from zinc oxide, barium sulfate, zirconium oxide, zirconium silicate and mixtures of two or more of the mentioned fillers wherein the composition further comprises: (C) from 0.1-4% by weight of a polyalkylene glycol homopolymer or copolymer, wherein all quantities have been calculated with respect to the total weight of components A, B and C. Composition of claim 1, wherein the polyalkylene glycol (C) is chosen from a polyalkylene glycol which has been provided which special endgroups, polyethylene glycol, polyethylene propylene glycol copolymers, polypropylene glycol, copolymers of a polyalkylene glycol and polydimethylsiloxanes or mixtures of two or more said polyalkylene glycols. Composition of claim 1, wherein component A comprises of a blend of a polyethylene terephthalate, a polybutylene terephthalate and a polycarbonate. Composition of claim 1, wherein constituent B is bariumsulfate. Composition of claim 1, wherein the composition further comprises an agent to improve the impact strength. Composition of claim 1 wherein the composition further comprises a silicone oil. Extruded sheet made out of the composition of any of the previous claims.

Inventors: FONTANA LUCA PIETRO, SACHARIAS ANTONIUS LEONARDUS, VAN DE GRAMPEL HENDRIK THEODOR, FONTANA, LUCA PIETRO, SACHARIAS, ANTONIUS LEONARDUS, VAN DE GRAMPEL, HENDRIK THEODORUS
Applicants: GEN ELECTRIC, GENERAL ELECTRIC COMPANY
Application year: 1995
Main classification: C08K3
IPC codes: C08K3, C08L77, C08L67, C08L71, C08L101, C08L69