Surface treatment of an oxide LnBa2Cu3O7-x single crystal

Abstract: When a cuprate oxide LnBa 2 Cu 3 O 7-x (Ln=Y, Pr or Sm; 0.3≦ x≦1.0) single crystal is heated for growing a film epitaxially on the crystal or for recovering the single crystal damaged on surfaces, lots of tall protrusions occur on the surface of the oxide single crystal substrate or the film. The smooth surface of the oxides becomes rugged by the protrusions. The oxide substrate or the oxide superconductor film is heated in an atmosphere including oxygen of a partial pressure between 50 mTorr and 200 mTorr. The oxygen gas prevents the protrusions from originating on the surface of the heated oxides.

Description: This invention relates to a surface treatment of a cuprate oxide LnBa 2 Cu 3 O 7-x (Ln=Y, Pr, Sm) single crystal, in particular, to a method of giving a flat surface to the LnBa 2 Cu 3 O 7-x single crystal substrate or film by eliminating the protrusions appearing on the surface of the LnBa 2 Cu 3 O 7-x single crystal by heating. This application claims a priority based on Japanese patent application No.6-240622 (240622/'94) filed September 7th, 1994. Conventional oxide superconductors have been polycrystalline, because they have been made by sintering powder oxide material. Sintering method cannot make a single crystal superconductor. Polycrystalline oxide superconductors produced from powder material include a lot of grain boundaries and defects. The defects form potential barriers in the grain boundaries of the polycrystalline superconductors. The occurrence of the potential barriers degrades the conduction property of the superconductors. Oxide superconductors free from grain boundaries are desired ardently. There are many kinds of oxide superconductors. Here the problems are now explained by adopting YBa 2 Cu 3 O 7-x or more in general, LnBa 2 Cu 3 O 7-x (Ln = Y, Pr, or Sm) as examples. YBa 2 Cu 3 O 7-x is one of the most known rare earth oxides. YBa 2 Cu 3 O 7-x is sometimes written as "YBCO" in short. Recent technology has succeeded in making large bulk single crystals of the oxide superconductors. Single crystal superconductors exhibit good electrical properties, since single crystals have generally no grain boundaries and little defects. A bulk single crystal cannot make the devices by itself which have inherent functions. Production of devices still requires piling thin films on the bulk single crystal substrate. If a good oxide superconductor bulk single crystal is obtained, the surface of the bulk single crystal should be polished and thin films should epitaxially be deposited on the bulk single crystals in order to fabricating electronic devices. Both oxide superconductive substrates and oxide superconductive films have strong electric anisotropy. Thus the interface between the substrate and the film and the surface of the film must be smooth enough. Then the substrate is polished into a smooth surface. The substrate should be heated in order to grow thin films on the substrate epitaxially. In general, epitaxial growth never occurs on a substrate at room temperature. The growth of films requires a hot substrate. Pulse laser ablation method or sputtering method is generally used for the epitaxial growth of oxide superconductor films on a heated substrate. The pulse laser ablation method makes a film by the steps of heating the substrate to a pertinent temperature, introducing oxygen gas in the reaction chamber, irradiating a target containing the material for the film by pulsed ultraviolet rays of the laser, evaporating the film material from the target, conveying the film material to the substrate and piling the film on the hot substrate. The sputtering method produces a film by the steps of bombarding a target made of the material of the film by argon ion beams, carrying the moleculars of the material to the substrate and piling the material on the heated substrate. In any cases, the substrate is heated for growing oxide superconductor films on the oxide superconductor substrate. During heating, plenty of protrusions arise on the surface of the LnBa 2 Cu 3 O 7-x substrate. The protrusions are induced only by heating the LnBa 2 Cu 3 O 7-x substrate which has been perfectly smooth just before heating. Without etching, without sputtering, heating solely generates the rugged surface of the oxide superconductor substrate. Raising temperature invites the occurrence of lots of protrusions on the LnBa 2 Cu 3 O 7-x substrate. This is a new phenomenon found by the Inventors of the present invention for the first time. Since there has been no large oxide superconductor single crystal until recently, nobody never has been aware of such a strange fact. The protrusions appear only on a single crystal oxide superconductor substrate. The strange phenomenon does not arise in a polycrystalline superconductor substrate, even if the polycrystalline substrate is heated at a high temperature. There may be a large difference between a single crystal oxide superconductor and a polycrystalline oxide superconductor about the behavior against heating. The protrusions which appear on a single crystal oxide superconductor in heating are sometimes higher than 30 nm. These protrusions are pretty high. When a single crystal oxide superconductor is heated, such high protrusions arise overall on the surface of the single crystal superconductor and decrease the smoothness of the surface fatally. If a film is grown on the rough surface, the interface between the substrate and the film will have the roughness similar to the substrate, since the growing film transcribes the morphology of the surface of the substrate. If a superconducting device is produced on the film, the rough junction between the film and the substrate degrades the property of the device. Superconductor substrates are sometimes heated for another purpose except epitaxial growth. For example, substrates are annealed for the purpose of eliminating a damage from the surface. Annealing is often employed for other materials. For example, a part of a surface of wafers is removed by ion etching for eliminating a superficial degenerate layer in the case of semiconductors Si, GaAs or InP. The degenerate layer can be removed. The surface, however, is greatly damaged by ion etching. Then the wafers are often heated above 400 °C. The annealing recovers the substrate wafer from the superficial damage in general. In the case of a single crystal oxide superconductor, the annealing induces many protrusions on the surface of the substrate. Although the monocrystalline superconductor has been polished into a smooth surface, the surface is degraded into a rugged one by the annealing which aims at enhancing the quality of the substrate in general. Such a strange phenomenon never occurs in the case of ordinary semiconductors or metals. The phenomenon has been discovered by the Inventors of the present invention for single crystal oxide superconductors. The phenomenon turns out to appear in all single crystal oxide superconductors represented by LnBa 2 Cu 3 O 7-x for Ln = Y, Pr or Sm. The Inventors investigated the critical temperature at which the micro-protrusions originate on the surface, in the case of YBa 2 Cu 3 O 7-x . Heating the YBCO at 300°C does not invite the surface protrusions. When the YBCO single crystal is heated at 400 °C, micro-protrusions appear on the surface of the single crystal. There is no problem for heating the superconductor till a temperature below 300°C. Heat-treatment below 300°C can scarcely accomplish the purpose of the treatment. For example, heating the superconductor substrate at a temperature less than 300 °C is insufficient for a good epitaxial growth of the films. Similarly, heating the object at a temperature below 300°C is nearly ineffective for eliminating a damage from the surface. Almost all the heat-treatments demand a temperature higher than 400°C. Why do the protrusions originate on the monocrystalline oxide superconductor, when it is heated. The problem is why the high temperature yields the roughness of the surface. The roughness of the surface is generally induced by the contaminants or the degenerate layer in the cases of almost all materials except the present oxide superconductors. The micro-protrusions, however, originate even on a clean, smooth monocrystalline substrate which has been polished and wet-etched for eliminating the superficial degenerate layer. Thus the protrusions are not caused by the contamination or the surface degenerate layer. A purpose of the present invention is to provide a method of heating a flat, smooth oxide single crystal LnBa 2 Cu 3 O 7-x (Ln = Y, Pr or S) without introducing protrusions on the surface. Another purpose of the present invention is to provide a method of heating a smooth substrate LnBa 2 Cu 3 O 7-x (Ln = Y, Pr or S) for epitaxial growth of films without inviting roughness on the surface. Another purpose of the present invention is to provide a method of annealing a substrate LnBa 2 Cu 3 O 7-x (Ln = Y, Pr or S) having a superficial damage resulting from polishing or etching without an occurrence of protrusions. Another purpose of the present invention is to provide a method for preventing protrusions from arising on the surface of the substrate LnBa 2 Cu 3 O 7-x (Ln = Y, Pr or S) when the substrate is heated for various objects. These purposes have been obtained with the methods according to claims 1-3. The origin of the protrusions is neither contamination nor degeneration of the substrate. The protrusions must be induced by a change of the structure of the single crystal LnBa 2 Cu 3 O 7-x itself. The Inventors consider that the structural change of the single crystal invites lots of protrusions on the oxide superconductor crystal. Why does the structural change occur in the single crystal superconductor? In general, any treatment is defined by the conditions including temperature, pressure, atmosphere and time change of the parameters. Temperature is, in many cases, determined by the object of heating of the treatment. Temperature is not a freely-controllable parameter. On the contrary, the kind of the atmospheric gas and the pressure of the atmospheric gas are the parameters which can freely be chosen. Then the oxide superconductors have been heated under various atmospheric pressures of various gases for examining the dependence of the occurrence of protrusions upon the atmospheric gas and the pressure. The atmospheric gas has been selected from rare gases, nitrogen gas, oxygen gas, halogen gases and mixture gases of them. The experiment has indicated that rare gases are ineffective for suppressing the protrusions from originating. Nitrogen gas is also in vain. Halogen gas cannot forbid the formation of the protrusions. The Inventors have discovered that only oxygen gas can prevent the protrusions from arising on the surface. Oxygen gas has turned out to be effective to maintain the smoothness of the surface of the oxide superconductors. Other gases except oxygen are all inept at suppressing the origination of the protrusions. Oxygen gas is the pertinent gas for the atmospheric gas of the heat treatment of monocrystalline oxide superconductors. In particular, 50 mTorr (6.6Pa) to 200 mTorr (26.6Pa) is the optimum partial pressure of oxygen gas. If the partial pressure of oxygen is less than 50 mTorr (6.6Pa), protrusions occur on the surface of the single crystal superconductors. On the contrary, more than 200 mTorr (26.6Pa) of oxygen atmosphere is still fully effective to hinder the protrusions from appearing on the substrate surface. The surface, however, becomes rough due to oxidization, when the oxygen partial pressure is higher than 200 mTorr. The roughness caused by oxidization is different from the ruggedness due to heating, since the height of the convexes induced by oxidization is several nanometers which are far lower than the protrusions owing to heating. However, the roughness by oxidization is also undesirable for the substrate crystal. Thus the optimum partial pressure of oxygen ranges from 50 mTorr (6.6Pa) to 200mTorr (26.6Pa). The occurrence of protrusions owing to heating has been a common fault for all oxide superconductor single crystals LnBa 2 Cu 3 O 7-x (Ln = Y, Pr, Sm). The method of this invention has turned out to be effective for all single crystal expressed by the formula LnBa 2 Cu 3 O 7-x (Ln = Y, Pr, Sm). In the formula LnBa 2 Cu 3 O 7-x , "x" means the defect number of oxygen from 7. The electric property depends on the defect number "x". Of course, x is less than 1. The oxide LnBa 2 Cu 3 O 7-x takes a value, in general, from 0 to 1 for x (0≦x≦1). When x = 0, the number of oxygen atoms in a molecule is 7. When x = 1, the oxygen atom number is 6. The samples having smaller number of oxygen atoms i.e. when x is nearly equal to 1, reduce the defect number x by absorbing oxygen atoms, when the sample is heated in oxygen gas. On the contrary, the other samples having bigger number of oxygen atoms will increase the number x by dispersing oxygen atoms when they are heated in anaerobic atmosphere, for example, in vacuum or in an inert gas. Big single crystal oxide superconductors which can be produced by the current technology have not enough oxygen atoms, since they have been grown at a high temperature. Thus at present, 0.3≦x≦1 is the scope for the value x of a superconducting LnBa 2 Cu 3 O 7-x (Ln = Y, Sm). PrBa 2 Cu 3 O 7-x is not superconductive for all values of x (0≦x≦1). Moreover a LnBa 2 Cu 3 O 7-x (Ln=Y, Sm) does not show superconductivity in the range of 0≦x≦0.3. However, these oxide single crystal substrates LnBa 2 Cu 3 O 7-x (Ln=Y, Sm or Pr; 0≦x≦1) is useful for the substrates for the growth of the superconductor films LnBa 2 Cu 3 O 7-x (Ln= Y, Sm; 0.3≦x≦1). Then if the oxide superconductors are heated in oxygen atmosphere, the Inventors have thought, the oxide crystal will change the crystal structure by absorbing oxygen atoms. Then the structural change will make the surface of the crystal rough. Otherwise, the Inventors have considered that no structural change will be induced in the oxide single crystal, when it is heated in vacuum. The Inventors have thought that if the oxide superconductor is heated in vacuum, no structural change will occur. Then no change of the structure and no dissociation of the crystal should arise, when the oxide superconductor crystal is heated up to 400°C in a vacuum of about 10 -6 Torr (1.3 x 10 -4 Pa). On the surface some parts of lattice structure should be dissolved due to the imperfection of lattice even at such a low temperature and should be converted into alien parts of different components. Then the alien parts should grow as protrusions. Namely, the imperfection of the lattice should allow oxygen atoms to dissociating from the surface and should induce the growth of the protrusions which are alien parts produced by the escape of oxygen atoms. Thus this invention heats oxide superconductors under the atmosphere of oxygen for preventing oxygen atoms from escaping out of the surface. The Inventors have confirmed that no protrusion happens on the surface, if the escape of oxygen atoms is suppressed. Then the reason which causes the occurrence of the protrusions has been solved. Conventionally, thin films of the oxide superconductor have been produced by preparing a single crystal MgO or a single crystal SrTiO 3 as a substrate, heating the substrate in vacuum and depositing oxide superconductor films on the heated substrate. For example, the films were produced on a MgO or SrTiO 3 substrate after being heated in a vacuum of 10 -5 Torr to 10 -6 Torr (1.3 x 10 -3 Pa to 1.3 x 10 -4 Pa). This invention denies vacuum as the atmosphere for heating a superconductor single crystal substrate. On the contrary, this invention adopts a non-vacuum atmosphere including oxygen with a partial pressure between 50 mTorr(6.6Pa) and 200 mTorr(26.6Pa). The requirement for the atmosphere is only (he partial pressure of oxygen. Thus the atmosphere can include other gases except oxygen, although other gases have no function for suppressing the ruggedness of the surface. Oxygen atoms do not dissociate from the lattice structure of the substrate crystal, since the substrate is heated under the atmosphere of oxygen gas in the present invention. Then no protrusion originates on the surface, because the protrusions have been caused by the dissociation of oxygen atoms from the surface. This invention has succeeded in suppressing the protrusions from occurring to perfection, even if the oxide superconductor is heated up to a high temperature between 400°C and 800°C. The atmosphere for heating an LnBa 2 Cu 3 O 7-x single crystal substrate has not been investigated in detail. Generally, it is considered that heating the oxygen deficient LnBa2Cu307-x (0.3≦x≦1) oxygen atmosphere caused oxidization. Then this invention which heats the oxide in such a high oxygen pressure of 50 mTorr (6.6 Pa) sharply contradicts the common sense which has adhered to the in-vacuum heating of the oxide superconductors. The Inventors, however, have confirmed that the oxide superconductors are not oxidized by heating in oxygen gas of 50mTorr (6.6Pa). Furthermore, the Inventors have verified the fact that the protrusions arise due to the escape of oxygen, when the oxide is heated under the oxygen partial pressure less than 50 mTorr (6.6Pa). By contrast, if a YBa 2 Cu 3 O 7-x crystal is heated in an oxygen atmosphere of 1 atm (760 Torr, 0.1MPa), the surface of the crystal is oxidized and the lattice of surface is distorted by oxidization. The surface is rugged by the distortion of the lattice structure. The oxygen pressure less than 1000 mTorr (133Pa) enables the oxide superconductors to avoid both the occurrence of the protrusions and the oxidization on the surface. The surface of LnBa 2 Cu 3 O 7-x , however, is gradually oxidized to some extent in oxygen gas of a pressure between 200 mTorr (26.6Pa) and 1000 mTorr(133Pa). Thus the optimum range of the partial pressure of oxygen is 50 mTorr to 200 mTorr.(6.6Pa to 26.6Pa). The advantages of the present invention are explained. This invention enables various heat treatments to heat LnBa 2 Cu 3 O 7-x single crystals without the occurrence of protrusions. The single crystals can be heated without becoming rough by the present invention. If the present invention is applied to the annealing for eliminating the inner strain of the oxide superconductors, no protrusion is borne on the surface of the oxides. This invention allows the annealing treatment to make a crystal with flat, smooth surfaces immune from protrusions. If the present invention is applied to the epitaxial growth of the thin films of superconductors on a superconductor LnBa 2 Cu 3 O 7-x single crystal substrate, no protrusion is generated both on the substrate and on the films even at a high temperature. The epitaxy succeeds in producing extremely flat, smooth films on the oxide superconductor substrates owing to the oxygen atmosphere proposed by the present invention. The invention will be more fully understood from the following description given by way of example only with reference to the several figures of the accompanying drawings in which, Fig.1(a) is an assembly of lines showing the heights in a direction of a part 3µm×3µm of the surface of a YBa 2 Cu 3 O 7-x single crystal observed by an AFM (atomic force microscope) which has been annealed at a temperature of 500°C in vacuum according to the conventional annealing in order to eliminating the damage induced by the ion etching. Fig.1(b) is a graph showing the distribution of the heights of the surface in a direction indicated by an arrow in Fig.1(a). The abscissa is the distance (µm) in the line on the surface. The ordinate is the heights (nm) of the surface on the line. Fig.2(a) is an assembly of lines showing the heights in a direction of a part 3 µm × 3 µm of the surface of a YBa 2 Cu 3 O 7-x single crystal observed by an AFM which has been annealed at a temperature of 500°C in oxygen gas of a pressure of 100 mTorr (13.3Pa) according to the teaching of the present invention in order to removing the damage induced by the ion etching. Fig.2(b) is a graph of the distribution of the heights of the surface in a direction indicated by an arrow in Fig.2(a). The abscissa is the distance (µm) in the line on the surface. The ordinate is the heights (nm) of the surface on the line. Fig.3 is a graph showing the time-dependence of the temperature in the film formation of a YBa 2 Cu 3 O 7-x film on a YBa 2 Cu 3 O 7-x single crystal substrate in vacuum of 10 -6 Torr (1.3 x 10 -4 Pa) by the conventional sputtering method. Fig.4 is a graph showing the time-dependence of the temperature in the film formation of a YBa 2 Cu 3 O 7-x film on a YBa 2 Cu 3 O 7-x single crystal substrate in oxygen of a pressure of 90 mTorr (11.9Pa) by tne conventional sputtering method modified by the present invention. Fig.5(a) is an assembly of lines showing the heights in a direction of a part 3 µm × 3 µm of the surface of a YBa 2 Cu 3 O 7-x single crystal film (sample D) observed by an AFM (atomic force microscope) which has been epitaxially grown on a YBa 2 Cu 3 O 7-x single crystal substrate which had been treated with the heating process in vacuum of 10 -6 Torr (1.3 x 10 -4 Pa) according to the conventional method. Fig.5(b) is a graph showing the distribution of the heights of the surface in a direction indicated by an arrow in Fig.5(a). The abscissa is the distance (µm) in the line on the surface. The ordinate is the heights (nm) of the surface on the line. Fig.6(a) is an assembly of lines showing the heights in a direction of a part 3 µm × 3 µm of the surface of a YBa 2 Cu 3 O 7-x single crystal film (sample C) observed by an AFM (atomic force microscope) which has been epitaxially grown on a YBa 2 Cu 3 O 7-x single crystal substrate which had been treated with the heating process in oxygen of a pressure of 90 mTorr (11.9Pa) by the sputtering method modified by the present invention. Fig.6(b) is a graph showing the distribution of the heights of the surface in a direction indicated by an arrow in Fig.6(a). The abscissa is the distance (µm) in the line on the surface. The ordinate is the heights (nm) of the surface on the line. To achieve the foregoing objects and in accordance with the purpose of the invention, embodiments will be broadly descried herein.; [EMBODIMENT 1 ○: Heating for recovering from a damaged state] A smooth-polished YBa 2 Cu 3 O 7-x single crystal was etched by ion beams. The single crystal was damaged by the bombardment of the ion beams. The RHEED patterns (reflective high energy electron beam diffraction) vanished by the damage due to the bombardment. The extinction of the RHEED patterns means random disorder of the lattice structures on the surface. The single crystal was annealed in a vacuum chamber for recovering the crystal from the damage. One sample (sample A) was heated in oxygen gas of 100 mTorr (13.3Pa) up to 500°C according to the teaching of the present invention. The other YBa 2 Cu 3 O 7-x sample (sample B) was heated in vacuum of 10 -6 to 10 -5 Torr (1.3 x 10 -4 Pa to 1.3 x 10 -3 Pa) up to 500°C according to the conventional annealing. Both samples were kept at 500 °C for a certain time. Then the samples were cooled and taken out of the chamber. Then the samples were examined by the RHEED method. The RHEED patterns with streaks appear in both samples A and B. The appearance of the RHEED patterns means the recovery of the regular order of the lattice structure. Sample A and sample B were tantamount to each other till then. The recovery of the lattice order does not necessarily mean the recovery of the smoothness of the surface of the crystal. Then the samples A and B were observed by the AFM (atomic force microscope). Fig.1 shows the result of the observation of sample B (vacuum annealing). Fig.1(a) indicates the changes of heights of the surface in a 3µm×3µm square by an assembly of 50 lines stretching in X-direction with a spacing of 60 nm. The ordinate denotes the distance (µm) in X-direction. The abscissa indicates the heights (nm). Fig.1(b) shows the heights on the line indicated by the arrow in Fig.1(a). Sample B which had been heated in vacuum exhibited a lot of protrusions randomly distributed on the surface. Some protrusions have a broadness less than 60 nm. The other protrusions have a broadness more than 60 nm which appears at the same distance in two neighboring lines. The heights of the protrusions ranged from 10 µm to 30 µm. The protrusions were so high that the crystal could not be adopted as a substrate for film formation. The number of the protrusions was too much. The section of Fig.1(b) had seven protrusions in a 3 µm length. This meant that the protrusions happened at a higher frequency. The vacuum-annealing resulted in producing a lot of high protrusions on the surface. Fig.2(a) indicates the changes of the heights of the surface in a 3 µm × 3 µm square of sample A by an assembly of 50 lines stretching in X-direction with a spacing of 60 nm. The ordinate denotes the distance (µm) in X-direction. The abscissa indicates the heights (nm). Fig.2(b) shows the heights on the line indicated by the arrow in Fig.2(a). Sample A which had been annealed in oxygen of 100 mTorr (13.3Pa) had a very smooth surface. There was no protrusion in the square of 3 µm × 3 µm of the surface of sample A. Fig.2(b) shows no disorder on the surface in X-direction. The surface was quite flat and smooth without protrusions. Sample A and sample B were annealed in the same conditions except the atmosphere. Sample B was heated in vacuum. Sample A was heated in oxygen gas. The conspicuous difference of the surfaces was caused by the existence or the non-existence of oxygen. These experiments verified the effectiveness of the present invention. [EMBODIMENT:2 ○ Heating for epitaxial growth of films] Single crystal oxide superconductor films were grown on YBa 2 Cu 3 O 7-x single crystal substrate by the sputtering method. The heating for the epitaxy may cause the protrusions on the films. The sample made by the method of the present invention (in oxygen) is named sample C. The other sample made by the conventional method (in vacuum) is named sample D. Fig.3 indicates a graph showing the time-dependent change of the temperature of the conventional sputtering. The abscissa is the time. The ordinate is the temperature. The chamber is kept to be vacuous (10 -6 Torr) (1.3 x 10 -4 Pa). The epitaxy consists of only three steps of a temperature-rising process (1), a sputtering process (2) and a temperature-falling process (3). The substrate was heated up to 650°C in vacuum of 10 -6 Torr (1.3 x 10 -4 Pa) in process (1). Then a mixture gas including oxygen gas of 90 % and argon gas of 10% was introduced into the reaction chamber. The total pressure was adjusted at 200 mTorr. The gas was excited into plasma. The target made of the oxide superconductor material was bombarded by the plasma. Then a YBa 2 Cu 3 O 7-x film was deposited on the heated substrate in process (2). Then the substrate was cooled to room temperature in process (3). Fig.4 denotes a graph showing the processes of the sputtering by the present invention. The sputtering consists of three steps of a temperature-rising process (1), a sputtering process (2) and a temperature-falling process (3). The profile of the time-dependent change of the temperature is similar to the conventional one of Fig.3. The temperature of sputtering was also the same to the conventional method. The target (YBa 2 Cu 3 O 7-x polycrystal) was also common to the conventional one. What was different was only the atmosphere in the reaction chamber in the temperature-rising process (1). The conventional method raised the temperature in vacuum. The present invention raised the temperature in the atmosphere of 100 mTorr (13.3Pa) having argon gas of 10%and oxygen gas of 90 %. The partial pressure of oxygen in process (11) was 90 mTorr (11.9Pa). The partial pressure of argon gas in the same process was 10 mTorr (1.3Pa). The total pressure was doubled at the turning point from process (1) to process (2). The partial pressure of oxygen was 180 mTorr (23.9Pa) in process (2). The partial pressure of argon was 20 mTorr (2.6Pa) in process (2). The components and the ratio were kept constant for process (1), process (2) and process (3). The reason why argon gas is included in the atmospheric gas was that the sputtering requires argon gas. Thus, argon gas was not necessary for process(1). It was more convenient to adopt a mixture gas also for the temperature-rising process (1), since there is no need to change the components of the gas at the turning point from process (1) to process (2). Only the partial pressure of oxygen gas plays the role of suppressing the oxygen atoms from escaping out of the lattices and preventing the protrusions from arising on the surface. Partial pressures of other gases are irrelevant to the suppression of the occurrence of protrusions. The other gases do not facilitate the origination of the protrusions. Therefore, other gases can freely be contained in the atmospheric gas. In this case argon gas was added in the gas for inducing the sputtering. Fig.5 shows the result of the AFM (atomic force microscope) observation of a part of 3µm×3µm of the film surface of sample D which was made by the conventional method. The distributions of the heights in X-direction are denoted by an assembly of continual lines. Fifty lines are arranged with a common spacing of 60nm. The abscissa is the distance (µm) in XY plane. The ordinate is the height (nm) of the surface. Many high protrusions were produced on the surface. The heights were distributed from 50 nm to 90 nm. In particular, there were many protrusions of about 70 nm height. The protrusions on the films of Fig.5 were far wider and taller than the protrusions on the substrate shown in Fig.1. The protrusions were so wide that a plurality of neighboring lines corresponded with the same peaks. The reason why the protrusions on the films were bigger and wider than the protrusions on the substrate of Fig. 1 is that the temperature (650°C) for the film formation was higher than the temperature (500°C) for the annealing. Such high protrusions will make a lot of defects at the junction which will be formed on the rough films and make it impossible to produce a good junction. By contrast, the density of the film protrusions (Fig.5) is lower than the density of the substrate protrusions (Fig.l). The smaller density may be caused by unification of protrusions. Fig.5(b)indicates the line of heights in X-section indicated by an arrow in Fig.5(a). The line has four peaks which were about 60 nm in height. Fig.6 shows the result of the AFM observation of the epitaxial film (sample C) produced by the teaching of the present invention. Fig.6(a) indicates the 2-dimensional distribution of the heights in a part of 3µm×3µm of the epitaxial film. Fig.6(b) shows the 1-dimensional distribution in X-direction denoted by an arrow in Fig.6(a). The surface was very smooth. The differences between peaks and valleys were lower than 5 nm. No protrusion was formed. The heights of the protrusions of the epitaxial film were less than the heights of the protrusions of the substrate of Fig.2 (sample A). Sample C and sample D differed from each other only with regard to the fact whether the atmosphere gas included oxygen gas or not. The result of the experiment verifies the fact that oxygen gas effectively prevents the protrusions from originating on the single crystal oxide superconductors. Thus this invention succeeds in making good oxide superconductor films and junctions which excel in the smoothness and flatness.

Claims: A method of heating an oxide LnBa 2 Cu 3 O 7-x single crystal (Ln=Y, Pr or Sm; 0.3≦x≦1) without introducing protrusions on the surface thereof, comprising heating the LnBa 2 Cu 3 O 7-x single crystal at a temperature higher than 400°C in an atmosphere including oxygen gas of a partial pressure between 50 mTorr and 200 mTorr (6.6Pa to 26.6Pa). A method of heating an oxide LnBa 2 Cu 3 O 7-x single crystal (Ln=Y, Pr or Sm; 0.3≦x≦1) which has a damaged surface without introducing protrusions on the surface thereof, comprising heating the damaged LnBa 2 Cu 3 O 7-x single crystal at a temperature between 400°C and 800°C in an atmosphere including oxygen gas of a partial pressure between 50 mTorr and 200 mTorr (6.6Pa to 26.6Pa). A method of depositing a LnBa 2 Cu 3 O 7-x film (Ln = Y, Pr or Sm) epitaxially on an oxide LnBa 2 Cu 3 O 7-x single crystal (Ln=Y, Pr or Sm; 0.3≦x≦1) without introducing protrusions on the surface of said single crystal, comprising the steps of: heating the LnBa 2 Cu 3 O 7-x single crystal at a temperature between 400°C and 800°C in an atmosphere including oxygen gas of a partial pressure between 50 mTorr and 200 mTorr and; depositing a LnBa 2 Cu 3 O 7-x film (Ln=Y, Pr or Sm) epitaxially on the heated LnBa 2 Cu 3 O 7-x single crystal in an atmosphere including oxygen gas.

Inventors: ENOMOTO YOUICHI, FUKE HIROYUKI, KONISHI MASAYA, SHIOHARA YUH, TANAKA SHOJI, ENOMOTO, YOUICHI, FUKE, HIROYUKI, KONISHI, MASAYA, SHIOHARA, YUH, TANAKA, SHOJI, Enomoto, Youichi, c/o Superconductivity Res. Lab., Fuke, Hiroyuki, c/o Superconductivity Res. Lab., Konishi, Masaya, c/o Superconductivity Res. Lab., Shiohara, Yuh, c/o Superconductivity Res. Lab., TANAKA, SHOJI, C/O SUPERCONDUCTIVITY RES. LAB.
Applicants: INT SUPERCONDUCTIVITY TECH, SUMITOMO ELECTRIC INDUSTRIES, TOSHIBA KK, INTERNATIONAL SUPERCONDUCTIVITY TECHNOLOGY CENTER, KABUSHIKI KAISHA TOSHIBA, SUMITOMO ELECTRIC INDUSTRIES, LIMITED
Application year: 1995
Main classification: C30B33
IPC codes: C01G1, C30B29, H01L21, C30B33, C01G3