Quantum splitting oxide phosphors and method of making same

Abstract: Quantum splitting oxide phosphors are described for use with VUV radiation. One oxide material has an atomic ratio, comprising: La 1-X Pr X MgB 5 O 10 ; where 0<X≦0.20. Another oxide material has an atomic ratio, comprising: Sr 1-X Pr X Al 12-X Mg X O 19 , where 0<X≦0.20 Both materials are stable and compatible for use as a phosphor with VUV radiation created by Hg vapor discharge.

Description: Field Of The Invention This invention relates generally to new oxide materials that have one application as a phosphor. More specifically, it comprises oxide phosphors doped with Pr 3+ that exhibits quantum splitting when irradiated with VUV (Vacuum Ultra-Violet) radiation. Most specifically, in a first embodiment it is a composition of matter of the form La I-X Pr X MgB 5 O 10 , where 0<X≤0.20; and a method of making this oxide, and in second embodiment it is a composition of matter of the form Sr X Pr 1-X Al 12-X Mg X O I9 , where 0<X≤0.20, and a method of making this oxide. Background of the Invention The conversion of a single ultraviolet photon into two visible photons with the result that the quantum efficiency of luminescence exceeds unity is termed quantum splitting. Quantum splitting materials are very desirable for use as phosphors for lighting applications, such as fluorescent lamps. A suitable quantum splitting material can in principle produce a significantly brighter light source. Quantum splitting has been demonstrated previously in fluoride-base materials. A material comprising 0.1% Pr 3+ in a matrix of YF 3 has been shown to generate more than one visible photon for every absorbed UV photon when excited with 185nm radiation. The measured quantum efficiency of this material was 145%±15%, and thus greatly exceeded unity. The critical conditions that yield quantum splitting by the Pr 3+ ion have only been achieved in fluoride-based materials. However, fluoride-base compounds do not have sufficient stability to permit their utilization as a phosphor in fluorescent lamps, because they are known to react with the Hg vapor that is used in such lamps to provide the UV radiation and form a material that does not exhibit quantum splitting. Therefore, it is desirable to develop materials that exhibit quantum splitting behavior, but that are also stable and suitable for use in current technology lamps (e.g. Hg-containing fluorescent lamps), such as metal oxides. Summary of the invention According to a first aspect of the invention, there is provided an oxide material having an atomic ratio, comprising: La 1-X Pr X MgB 5 O 10 ; where O<X<0.20. According to a second aspect of the invention, there is provided use of an oxide material having an atomic ratio, comprising: Sr 1-X Pr X Al 12-X Mg X O 19 ; where O<X<0.20 as a phosphor which shows quantum splitting behavior when iradicated with VUV. According to a third aspect of the invention, there is provided the method of claim 6, further comprising the step of washing the material in water to remove excess H 3 BO 3 . According to a fourth aspect of the invention, there is provided a lamp comprising an evacuated housing, a VUV radiation source located within the housing, and a phosphor that is located within the housing and adapted to be excited by the VUV radiation source, said phosphor comprising a boron oxide compound containing lanthanum, praseodymium, and magnesium in an atomic ratio La 1-x Pr x MgB 5 O 10 where 0<X<0.20, which phosphor exhibits quantum splitting when excited by VUV radiation from the VUV radiation source. According to a fifth aspect of the invention, there is provided a lamp comprising an evacuated housing, a VUV radiation source located within the housing, and a phosphor that is located within the housing and adapted to be excited by the VUV radiation source, said phosphor comprising an oxide of aluminum, strontium, praseodymium, and magnesium in an atomic ratio Sr 1-x Pr x A1 12-x Mg x O 19 ; where 0,x,0.20, which phosphor exhibits quantum splitting when excited by VUV radiation. Thus the invention includes an oxide phosphor doped with Pr 3+ that exhibits quantum splitting when irradiated with VUV radiation. It is also expected to feature the desired characteristic of being chemically stable in the presence of an Hg vapor discharge. In a first embodiment this invention comprises a composition of matter in the form of an oxide material having an atomic ratio, comprising: La 1- XPrxMgB 5 O 10 ; where O<X<0.20. The first embodiment of this invention may also be described as an oxide of boron, lanthanum, praseodymium, and magnesium that exhibits quantum splitting when excited by VUV radiation. The invention also may be described as a method of making La I-X Pr x MgB 5 O 10 material, where O<X<0.20, comprising the steps of: selecting a desired value of X so as to define a desired composition; forming a substantially homogeneous mixture from a quantity of each of the compounds La 2 (CO 3 ) 3 .8H 2 O,Pr 6 O II ,MgO and H 3 BO 3 that is sufficient to satisfy a stoichiometric requirement of the desired composition; and firing the mixture in a non-oxidizing atmosphere at a temperature and for a time sufficient to sinter the material and maintain the Pr state as Pr3 + . In a second embodiment, this invention comprises the use of a composition of matter in the form of an oxide material having an atomic ratio, comprising: Sr 1-x Pr X Al 12-X Mg X O 19 ; where O<X<0.20, as a phosphor which exhibits quantum splitting when excited by VUV radiation. The invention also may be described as a method of making Sr 1-X Pr X Al 12-X Mg X O 19 material, where O<X<0.20, comprising the steps of: selecting a desired value of X so as to define a desired composition; forming a substantially homogeneous mixture from a quantity of each of the compounds SrCO 3 ,Pr 6 O II ,Al(OH) 3 and MgO that is sufficient to satisfy a stoichiometric requirement of the desired composition; and firing the mixture in a non-oxidizing atmosphere at a temperature and for a time sufficient to sinter the material and maintain the Pr state as Pr3 + . Brief Description of the Drawings The invention will now be described in greater detail by way of example, with reference to the file drawings, in which:- Figure 1 is a plot of measured values of emission intensity as a function of wavelength for a phosphor of the first embodiment of the present invention. Figure 2 is a plot of measured values of emission intensity as a function of wavelength for a phosphor of the second embodiment of the present invention. Figure 3 is a schematic illustration of a lamp incorporating either phosphor of the present invention. Detailed Description of the Invention In its first embodiment, this invention relates generally to a new oxide material comprising a complex oxide of boron, lanthanum, praseodymium and magnesium. In its second embodiment, this invention relates generally to a new oxide material comprising a complex oxide of aluminum, strontium, magnesium and praseodymium. Either material may be used as a phosphor, and is of particular interest because it has been observed to exhibit quantum splitting when it is excited by UV radiation in a VUV radiation environment. This material was empirically determined to be a quantum splitting material based upon observation of a characteristic peak or shift in the emission spectra of the material at 400nm when excited by VUV radiation, as shown in Figure 1 or Figure 2, respectively. This shift at 400nm is known to be a characteristic of quantum splitting materials, and examination of the intensity/wavelength emission spectra provides a convenient way of testing phosphors for quantum splitting behavior, as opposed to using the more time consuming quantum efficiency measurements for this purpose. Review of intensity/wavelength emission spectra for a number of complex oxides of boron, lanthanum, praseodymium and magnesium has led to the empirical determination that quantum splitting is particularly observed in oxides of the first embodiment of the present invention over the range of compositions represented by the atomic ratios: La 1-X Pr X MgB 5 O 10 ; where 0<X≤0.20. Review of intensity/wavelength emission spectra for a number of complex oxides of aluminum, strontium, magnesium and praseodymium has led to the empirical determination that quantum splitting is particularly observed in oxides of the second embodiment of the present invention over the range of compositions represented by the atomic ratios: Sr 1-X Pr X Al 12-X Mg X O 19 ; where 0<X≤0.20, Without limitation, the quantum splitting behavior is attributed to the UV excitation of the Pr 3+ ion within the oxide lattice. Therefore, oxides of the present invention should be processed so as to maintain Pr as a Pr 3+ ion within the oxide lattice. The quantum splitting oxide, Sr 1-X Pr X Al 12-X Mg X O 19 , where 0<X≤0.20, has been incorporated into a VUV fixture containing Hg, which was excited to serve as the UV source. This oxide continued to exhibit quantum splitting, even after about 100 hours of exposure to the Hg. Therefore, oxides of the first embodiment of the present invention are also expected to maintain quantum splitting in an Hg vapor environment. The oxides of the present invention characterized by quantum splitting behavior in VUV radiation and stability with regard to an Hg discharge environment may be utilized as a phosphor in a fluorescent lamp. Referring to Figure 3, lamp 50 comprises an evacuated housing means 60, a VUV radiation source 70 located within the housing means 60, and a phosphor 80 that is located within the housing and adapted to be excited by the VUV radiation source, said phosphor 80 comprising an oxide of boron, lanthanum, praseodymium, and magnesium that exhibits quantum splitting when excited by VUV radiation, or an oxide of aluminum, strontium, praseodymium, and magnesium that exhibits quantum splitting when excited by VUV radiation. In a preferred embodiment, lamp 50 is a fluorescent lamp and evacuated housing means 60 comprises an evacuated glass tube. The VUV radiation source 70 is a combination of Hg and an excitation means located within the glass tube that may be used to create an Hg vapor discharge to excite phosphor 80. Example 1 A sample of the oxide of the present invention designed to yield 50 grams of the final material was prepared by combining the following: La 2 (CO 3 ) 3 ·8H 2 O 37.78 Pr 6 O 11 1.1278 MgO 5.34 H 3 BO 3 41.4 g The starting materials were blended using a ball mill with ZrO 2 milling media. The blended materials were then fired in forming gas (1%H 2 -99%N 2 ) to avoid the oxidation of Pr to Pr 4+ , and maintain the Pr in the lattice as Pr 3+ state. The final composition of the material was La 0.95 Pr 0.05 MgB 5 O 10 . A general method for making the oxides of the first embodiment comprises selecting a desired value of X so as to define a desired composition; forming a substantially homogeneous mixture from a quantity of each of the compounds La 2 (CO 3 ) 3 ·8H 2 O,Pr 6 O 11 ,MgO and H 3 BO 3 that is sufficient to satisfy a stoichiometric requirement of the desired composition; and firing the mixture in a non-oxidizing atmosphere at a temperature and for a time sufficient to sinter the material and maintain the Pr state as Pr 3+ . The material was irradiated with 185nm radiation in a VUV instrument. The resulting emission was monitored from 300-500nm, and is shown as Figure 1. Example 2 A sample of the oxide of the present invention designed to yield 50 grams of the final material was prepared by combining the following: SrCO 3 9.77 g Pr 6 O 11 0.59 g Al(OH) 3 64.94 g MgO 0.14 g The starting materials were blended using a ball mill with ZrO 2 milling media. The blended materials were then fired in air in an available furnace for 5 hours at 1,500°C to sinter the material, however, firing in air is generally undesirable because it tends to oxidize the Pr to Pr 4+ , rather than Pr 3+ . Therefore, in this example, the sintered sample was remilled and fired at 1,200°C for an additional 5 hours in forming gas (1%H 2 -99%N 2 ) to reduce the Pr to Pr 3+ . The final composition of the material was Sr 0.95 Pr 0.05 Al 11.95 Mg 0.05 O 19 . A general method for making the oxides of the second embodiment of the present invention comprises selecting 100 a desired value of X so as to define a desired composition; forming 110 a substantially homogeneous mixture from a quantity of each of the compounds SrCO 3 ,Pr 6 O 11 ,Al(OH) 3 and MgO that is sufficient to satisfy a stoichiometric requirement of the desired composition; and firing the mixture in a non-oxidizing atmosphere at a temperature and for a time sufficient to sinter the material and maintain the Pr state as Pr 3+ . The material was irradiated with 185nm radiation in a VUV instrument. The resulting emission was monitored from 300-500nm, and is shown as Figure 2. In addition to the shift at 400nm, a shift was also observed in the visible spectrum at approximately 480nm.

Claims: An oxide material having an atomic ratio, comprising: La I-X Pr x MgB 5 O 10 ; where O<X<0.20. The ceramic oxide material of claim 1, wherein the ceramic oxide material exhibits quantum splitting behavior when excited by VUV radiation. The ceramic oxide material of claim 2, wherein the VUV radiation results from an Hg vapor discharge in the presence of the ceramic oxide material. Use of an oxide material having an atomic ratio, comprising: Sr 1-X Pr X Al 12-X Mg x O 19 ; where O<X<0.20 as a phosphor which shows quantum splitting behavior when irradiated with VUV. Use of an oxide material as claimed in claim 2, wherein the VUV radiation results from an Hg vapor discharge in the presence of the ceramic. A method of making La I-X Pr x MgB 5 O 10 material, where O<X<0.20, comprising the steps of selecting a desired value of X so as to define a desired composition; forming a substantially homogeneous mixture from a quantity of each of the compounds La 2 (CO 3 ) 3 .8H 2 O,Pr 6 O II ,MgO and H 3 BO 3 that is sufficient to satisfy a stoichiometric requirement of the desired composition; and firing the mixture in a non-oxidizing atmosphere at a temperature and for a time sufficient to sinter the material and maintain the Pr state as Pr 3+ . The method of claim 6, further comprising the step of washing the material in water to remove excess H 3 BO 3 . A method of making Sr 1-x PrXAl 12-X Mg X O 19 material; where O<X<0.20 comprising the steps of: selecting a desired value of X so as to define a desired composition; forming a substantially homogeneous mixture from a quantity of each of the compounds SrCO 3 ,Pr 6 O II ,Al(OH) 3 and MgO that is sufficient to satisfy a stoichiometric requirement of the desired composition; and firing the mixture in a non-oxidizing atmosphere at a temperature and for a time sufficient to sinter the material and maintain the Pr state as Pr 3+ . The method of claim 8, wherein the non-oxidizing atmosphere is a forming gas atmosphere. A lamp comprising an evacuated housing, a VUV radiation source located within the housing, and a phosphor that is located within the housing and adapted to be excited by the VUV radiation source, said phosphor comprising a boron oxide compound containing lanthanum, praseodymium, and magnesium in an atomic ratio La 1-x Pr x MgB 5 O 10 where 0<X<0.20, which phosphor exhibits quantum splitting when excited by VUV radiation from the VUV radiation source. A lamp comprising an evacuated housing, a VUV radiation source located within the housing, and a phosphor that is located within the housing and adapted to be excited by the VUV radiation source, said phosphor comprising an oxide of aluminum, strontium, praseodymium, and magnesium in an atomic ratio Sr 1-x Pr x Al 12-x Mg x O 19 ; where 0,x,0.20, which phosphor exhibits quantum splitting when excited by VUV radiation. The lamp of claim 10 or 11, wherein the VUV radiation source is Hg that is adapted to be excited by an excitation means so as to create an Hg vapor discharge.

Inventors: BEERS WILLIAM WINDER, SRIVASTAVA ALOK MANI, BEERS, WILLIAM WINDER, SRIVASTAVA, ALOK MANI
Applicants: GEN ELECTRIC, GENERAL ELECTRIC COMPANY
Application year: 1995
Main classification: C09K11
IPC codes: C09K11, C01B35, H01J61, C04B35