POLYETHER PHOSPHATES

Abstract: A dispersant for aqueous mill-bases obtainable by reacting a polyethylene glycol with a molar excess of a hydroxycarboxylic acid containing from 4 to 17 carbon atoms or lactone thereof and/or with a C3-4-alkylene oxide to form a polymeric diol and phosphating the diol. The preferred hydroxycarboxylic acid or lactone is epsilon -caprolactone.

Description: POLYETHER PHOSPHATES The present invention relates to a compound for dispersing particulate solids in an aqueous medium, its method of preparation and compositions containing said compound and a particulate solid, including paints. Mill-bases for water-borne paints are conventionally prepared by subjecting an aqueous medium containing a water-insoluble particulate solid such as a pigment to a grinding operation in the presence of a dispersing agent in order to tiniformly distribute the finely divided solid throughout the medium. However, when such mill-bases are added to a paint, the dispersing agent can adversely effect the film-forming characteristics of the paint and/or its durability as a paint film. Some dispersing agents also adversely affect the gloss of the resulting paint film. Consequently, improved dispersing agents are required which are capable of dispersing greater amounts of particulate solid in the medium, and exhibiting increased stability of the dispersion and superior properties in the resulting paint film, especially higher gloss finish. EP 555,950 discloses aqueous mill bases containing a pigment and dispersant which is a polycyclic compound having a poly (C 2 . 4 -al yleneoxy) chain containing from 3 to 50 alkyleneoxy groups. Although the dispersant of the present invention also contains a polyal ylene chain it does not contain a terminal polycyclic group such as a naphthalene ring and the present dispersants have been found to provide a paint film with a much superior gloss. According to the present invention there is provided a dispersant obtainable by reacting a polyethylene glycol (hereinafter "PEG") with a molar excess of a hydroxycarboxylic acid containing from 4 to 17 carbon atoms or lactone thereof (hereinafter "HCA") and/or with a C 3 _ 4 -al ylene oxide (hereinafter "AO") to form a polymeric diol and phosphating the diol by reaction with a phosphating agent to give a phosphate ester. The dispersant may be in the free acid form or it may form a salt with an alkali metal, ammonia, an amine, alkanolamine or quaternary ammonium cation. The phosphate ester group may also be further partially esterified by reaction with an alcohol or may form a salt with an alkanolamine. Thus, in one aspect of the invention the dispersant is derived from a polymeric diol obtainable by reacting a PEG with a molar excess of a HCA. It is to be understood that the PEG includes block copolymers of ethylene oxide (EO) and propylene oxide (PO) wherein the latter constitutes a middle portion attached at each end to EO units and wherein the amount of PO is less than 50%, preferably less than 30% and more preferably less than 10% by weight relative to the total weight of PEG. It is especially preferred that the PEG consists essentially of EO units. In another aspect of the invention the dispersant is derived from a polymeric diol obtainable by reacting a PEG with a molar excess of a AO. In a still further aspect of the invention the dispersant is derived from a polymeric diol obtainable by reacting a PEG with a molar excess of a HCA and a AO wherein the reaction of the PEG with the HCA and the AO is carried out either simultaneously or sequentially. In all three aspects, the polymeric diol is a block co- polymer having terminal hydroxyl groups. In a preferred aspect of the invention the dispersant is obtainable from a polymeric diol of general formula (1) : H-A-O- [CH 2 CH 2 -0] n -A-H (1) wherein: 0 it A is the group - [0- or the group -[0-D-], B is C 4-17 -alkylene; D is C 3-4 -alkylene; m is from 2 to 50; and n is from 4 to 500 0 II Preferably, the repeat unit - [O-B-C] m - is derivable from 6-hydroxyhexanoic acid, ricinoleic acid, 12-hydroxystearic acid, 12-hydroxydodecanoic acid, 5-hydroxydodecanoic acid, 5-hydroxydecanoic acid, 4-hydroxydecanoic acid and e-caprolactone including mixtures thereof. It is especially preferred that B is -(CH 2 ) 5 - and that the repeat unit is derived from e-caprolactone. Preferably, m is at least 3, more preferably at least 4 and especially at least 6. It is preferred that m is less than 40, more preferably less than 30 and especially less than 20. Preferably, n is at least 6, more preferably at least 8 and especially at least 10. It is also preferred that n is less than 400, preferably less than 300, more preferably less than 200 and especially less than 100. The ratio of the molecular weight of -A- and molecular weight of the group [-CH 2 -CH 2 -0]_- is preferably between 2.5:1 and 1:5 and especially between 1.5:1 and 1:3. The polymeric diol is preferably converted to the phosphate ester by reacting the diol with polyphosphoric acid, P 2 0 5 or P0C1 3 . Preferably, the ratio of the hydroxy groups of the diol to the phosphorus atom of the phosphating agent is from 3:1 to 1:1 and especially from 2:1 to 1:1. The reaction between the phosphating agent and the polymeric diol may optionally be carried out in the presence of an alcohol or alkanolamine or the phosphate ester of the polymer diol may be subsequently reacted with an alcohol or an alkanolamine. When the reaction involves an alcohol the phosphate end group(s) are partially further esterified. When the reaction involves an alkanolamine additional ester and/or amide groups and/or amine salts with the phosphated polymeric diol are formed. It is believed that the reaction product is mainly an amine salt. The alcohol or alkanolamine preferably has a molecular weight below 250 and especially below 100. Examples of suitable alkanolamines are ethanolamine, diethanolamine, 2-dimethylaminoethanol and 2-amino-2- methyl-1-propanol. The preferred dispersants are those derived from PEG having a molecular weight from 500 to 6000. It is also preferred that the HCA is derived from e-caprolactone. Preferably, the PEG is end-capped at each end with poly(5-hydroxy hexanoic acid) (PHHA) such that the ratio of the MW's of PHHA to PEG is from 1 to 10, more preferably from 1 to 5 and especially from 1 to 1. The polymeric diol can be made by reacting the PEG with the HCA at elevated temperatures optionally in the presence of an inert solvent. Preferably the two components are reacted together in the absence of a solvent, especially in the presence of a catalyst and more especially in an inert atmosphere such as nitrogen. Preferably the two components are reacted together at a temperature above 100°C, more preferably above 140°C and especially above 160°C. Preferably the temperature is below 250°C, more preferably below 200°C and especially below 180°C. Preferred catalysts are alkyl titanates, especially tetra- alkyl titanates such as tetrabutyltitanate. When the PEG is reacted with a AO to form the polymeric diol similar reaction conditions may be used except that the catalyst is normally an alkali metal hydroxide such as potassium hydroxide and the reaction vessel is preferably pressurised to prevent loss of the volatile AO. Consequently, the reaction,between the PEG and AO is preferably carried out a temperature below 100°C and in an inert atmosphere such as nitrogen. As noted hereinbefore the dispersants according to the present invention are suitable for iiniformly distributing a particulate solid in a liquid medium, especially an aqueous medium. Thus, according to a further aspect of the invention there is provided a composition comprising a dispersant as hereinbefore defined and a particulate solid. Preferably, the composition further comprises a liquid, especially one in which the dispersant is at least partially soluble and more especially is either water or an organic liquid which is miscible with water including mixtures thereof. Examples of suitable liquids include alcohols such as C 1-10 -aliphatic alcohols; glycols such as C 2-6 -alkylene glycols; alcohol ethers such as methoxy-, ethoxy-, propoxy- and butoxyethanol and methoxy-, ethoxy- and propoxypropanol; and glycol ethers such as diethylene glycol and propylene glycol. Generally, the liquid is selected to meet the requirements of the end-use to which the composition is put, especially compatibility with any medium with which it is to be diluted. Preferably, the liquid comprises at least 25%, more preferably at least 50% and especially at least 75% by weight water relative to the total weight of the composition. The composition may comprise an intimate mixture of the dispersant and the particulate solid but preferably comprises a coating of the dispersant on a finely divided particulate solid. Preferably the particulate solid has a mean diameter of less than 15μ, more preferably less than 10ft, especially less than 5μ and most especially less than 3μ. The particulate solid can be any material which it is desired to stabilise in a finely divided state in a liquid medium. Examples of suitable solids are pigments and fillers for inks, paints and other surface coatings; magnetic metals or alloys and magnetic oxides, for use in the production of magnetic tapes, discs and memory devices; dirt and soil particles; biocides, agrochemicals and pharmaceuticals. The composition, whether dry or in the form of a dispersion, may contain other ingredients such as resins, binders, fluidising agents, anti- sedimentation agents, plasticisers, humectants, coalescents, co- solvents, thickeners and preservatives. These ingredients may be soluble in, partially soluble in, insoluble in, or dispersed in the liquid medium. If the solid is a pigment, it is preferably an inorganic pigment, a metallic pigment, or a metal salt of an organic dyestuff (sometimes referred to as a lake or toner) . It may come from any of the recognised classes of pigments described, for example, in the Third Edition of the Colours Index (1971) and subsequent revisions and supplements thereto, under the chapter headed "Pigments". Examples of inorganic pigments are titanium dioxide (including Anatase and Rutile forms, and high UV absorbing ultra-fine titanium dioxide) , zinc oxide, Prussian Blue, cadmium sulphide, iron oxides (including transparent iron oxides) , ultramarine, mica (including pearlescent pigments made by surface treating mica with, for example fine titanium dioxide) and the chrome pigments, including chromates, molybdates, and mixed chromates and sulphates of lead, zinc, barium, calcium and mixtures and modifications thereof which are commercially available as greenish-yellow to red pigments under the names of primrose, lemon, middle, orange, scarlet and red chromes. Examples of metallic pigments are aluminium flake, copper powder and copper flake. Examples of metal salts of organic dyestuffs are the azo metal salt pigments such as CI Pigment red 48 (also known as 2B Toner or Permanent Red 2B) , CI Pigment Red 53 (also known as Lake Red C or Red Lake C) , CI Pigment Red 52, CI Pigment Red 57 (also known as 4B Toner, Lithol Rubine, Rubine Toner or Permanent Red 4B) , CI Pigment Red 58, CI Pigment Red 247, CI Pigment Yellow 61, CI Pigment Yellow 62, CI Pigment Yellow 183 and CI Pigment Yellow 191. Examples of fillers are calcium carbonate, hydrated alumina, talc, quartz, silica (precipitated, pyrogenic and synthetic) , metal silicates, barium and calcium sulphate, china clay, antimony oxide, powdered slate, wollastonite and chopped glass fibre. The composition may be made by any method known to the art. Thus, it may be prepared by mixing together the dispersant and particulate solid and preferably then grinding the composition to obtain the desired particle size of the solid. Preferably, however, the dispersant may be added to the particulate solid in the presence of a liquid during the final preparation or finishing stages of the particulate solid. Generally, the composition is, however, prepared by mixing the dispersant, particulate solid and a liquid medium and then grinding or milling the composition to obtain the desired particle size of the particulate solid. The liquid medium may be water or an organic liquid in which the dispersant is preferably at least partially soluble. If the composition is required in dry form, the liquid medium is preferably volatile so that it may be readily removed from the particulate solid by simple separation means such as evaporation. It is preferred however that the composition comprises the liquid medium. If the dry composition consists essentially of the dispersant and the particulate solid, it preferably contains at least 0.2%, more preferably at least 0.5% and especially at least 1% by weight of dispersant based on the weight of the particulate solid. Preferably, the dry composition contains not greater than 100%, preferably not greater than 50%, more preferably not greater than 20% and especially not greater than 10% by weight dispersant based on the weight of the particulate solid. When the composition comprises a dispersant, particulate solid and a liquid medium, it preferably contains at least 5%, more preferably at least 20%, especially at least 40% and most especially at least 50% particulate solid based on the total weight of the composition. Preferably, the composition contains not greater than 90%, more preferably not greater than 80% and especially not greater than 75% by weight solid based on the total weight of the composition. The preferred amount of dispersant relative to the particulate solid is as defined hereinbefore for the dry composition. Some of the polymeric diols are new. Hence, as a further aspect of the invention there is provided a polymeric diol of formula 1 H-A-O- [CH 2 CH 2 -0] n -A-H ( 1 ) wwhheerreeiinn :: A is the group - [O-B- iC?] B is C 4-17 -alkylene; m is from 2 to 50; and n is from 4 to 500. The invention is further illustrated by the following examples in which all parts and percentages are by weight unless otherwise indicated. Intermediate diols for making Dispersants Intermediate 1 A mixture of polyethylene glycol (average molecular weight 1500, 45.00 parts), e-caprolactone (61.56 parts) and tetrabutyl titanate (0.21 parts) was stirred under nitrogen for 5 hours at 160-180°C. The reaction mass was then discharged and allowed to solidify to a waxy solid. Intermediate 2 A mixture of PEG 1500 (33.60 parts), e-caprolactone (66.40 parts) and tetrabutyl titanate (0.20 parts) was stirred under nitrogen for 5 hours at 160-180°C. The reaction mass was then discharged and allowed to solidify to a waxy solid. Intermediate 3 A mixture of PEG 1000 (32.77 parts), e-caprolactone (67.23 parts) and tetrabutyl titanate (0.20 parts) was stirred under nitrogen for 5 hours at 160-180°C. The reaction mass was then discharged and allowed to solidify to a waxy solid. Intermediate 4 A mixture of PEG 600 (39.68 parts), e-caprolactone (60.32 parts) and tetrabutyl titanate (0.20 parts) was stirred under nitrogen for 5 hours at 160-180°C. The reaction mass was then discharged and allowed to solidify to a waxy solid. Intermediate 5 A mixture of PEG 200 (20.00 parts), e-caprolactone (45.60 parts) and tetrabutyl titanate (0.10 parts) was stirred under nitrogen for 5 hours at 160-180°C. The reaction mass was then discharged and allowed to solidify to a waxy solid. Intermediate 6 A mixture of PEG 300 (30.00 parts), e-caprolactone (45.60 parts) and tetrabutyl titanate (0.15 parts) was stirred under nitrogen for 5 hours at 160-180°C. The reaction mass was then discharged and allowed to solidify to a waxy solid. Intermediate 7 A mixture of PEG 400 (30.00 parts), e-caprolactone (51.30 parts) and tetrabutyl titanate (0.16 parts) was stirred under nitrogen for 5 hours at 160-180°C. The reaction mass was then discharged and allowed to solidify to a waxy solid. Intermediate 8 A mixture of PEG 1500 (2.43 parts), 12-hydroxydodecanoic acid (3.50 parts) and tetrabutyl titanate (0.04 parts) was stirred under nitrogen for 5 hours at 160-180°C. The reaction mass was then discharged and allowed to solidify to a waxy solid. Intermediates 9 to 39 Intermediates 9 to 37 were all preferred by the method described for Intermediate 1 except that the amounts of PEG, e-caprolactone and tetrabutyl titanate (TBT) were varied as detailed in Table 1 below. In the case of intermediates 38 and 39, the PEG was also replaced by Synperonic PE L35 (an ethylene oxide/propylene oxide/ethylene oxide block co-polymer) and Pluronic 17R4 (a propylene oxide/ethylene oxide/propylene oxide block co-polymer) , respectively. Synperonic is a registered trade mark of ICI PLC and Pluronic is a registered trade mark of BASF. Intermediate 9 was obtained as a liquid. Intermediates 38 and 39 were obtained as pastes and the remainder were obtained as waxy solids. TABLE 1 Intermediate Diol Amount of Amount of Amount of Diol e-caprolactone TBT 9 PEG 200 20 22.8 0.1 10 PEG 600 70 26.6 0.5 11 PEG 600 30 91.2 0.5 12 PEG 1000 80 18.2 0.5 13 PEG 1000 50 57 0.5 14 PEG 1000 50 148.3 0.45 15 PEG 1500 80 12.2 0.5 16 PEG 1500 80 24.3 0.5 17 PEG 1500 100 76.1 1.05 18 PEG 1500 30 82.15 0.5 19 PEG 1500 25 95 0.5 20 PEG 2000 80 18.2 0.5 21 PEG 2000 100 76.1 1.05 22 PEG 2000 50 51.3 0.4 23 PEG 2000 50 74.1 0.45 24 PEG 2000 50 102.6 0.45 25 PEG 2000 15 85.6 0.5 26 PEG 3000 50 34.2 0.45 27 PEG 3000 50 49.45 0.45 28 PEG 3000 50 68.4 0.5 29 PEG 3000 50 102.6 0.5 30 PEG 3000 25 83.6 0.5 TAB]_E 1 (continued) Example,1 Intermediate 1 (30.0 parts) was heated to 60°C, phosphorus pentoxide (0.80 parts) added and the mixture stirred -under nitrogen for 1 hour at 60°C. The temperature was raised to 85-90°C and held for a further 23 hours. The reaction mass was then discharged and allowed to solidify to a waxy solid. This product is hereinafter referred to as Dispersant 1. Example 2 Intermediate 2 (30.0 parts) was heated to 60°C, phosphorus pentoxide (0.64 parts) added and the mixture stirred under nitrogen for 1 hour at 60°C. The temperature was raised to 80-90°C and held for a further 23 hours. The reaction mass was then discharged and allowed to solidify to a waxy solid. This product is hereinafter referred to as Dispersant 2. Example 3 Intermediate 3 (30.0 parts) was heated to 60°C, phosphorus pentoxide (0.93 parts) added and the mixture stirred under nitrogen for 1 hour at 60°C. The temperature was raised to 80-90°C and held for a further 23 hours. The reaction mass was then discharged and allowed to solidify to a waxy solid. This product is hereinafter referred to as Dispersant 3. Example 4 Intermediate 4 (30.0 parts) was heated to 60°C, phosphorus pentoxide (1.88 parts) added and the mixture stirred under nitrogen for 1 hour at 60°C. The temperature was raised to 80-90°C and held for a further 23 hours. The reaction mass was then discharged and allowed to solidify to a waxy solid. This product is hereinafter referred to as Dispersant 4. Example 5 Intermediate 5 (30.0 parts) was heated to 30°C, phosphorus pentoxide (4.33 parts) added and the mixture stirred under nitrogen for 1 hour at 30°C. The temperature was raised to 60°C and held for 3 hours and then raised to 90-100°C for a further 20 hours. The reaction mass was then discharged and allowed to solidify to a waxy solid. This product is hereinafter referred to as Dispersant 5. Example 6 Intermediate 6 (30.0 parts) was heated to 30°C, phosphorus pentoxide (3.76 parts) added and the mixture stirred under nitrogen for 1 hour at 30°C. The temperature was raised to 60°C and held for 3 hours and then raised to 90-100°C for a further 20 hours. The reaction mass was then discharged and allowed to solidify to a waxy solid. This product is hereinafter referred to as Dispersant 6. Example 7 Intermediate 7 (30.0 parts) was heated to 30°C, phosphorus pentoxide (2.62 parts) added and the mixture stirred under nitrogen for 30 minutes at 30°C. The temperature was raised to 60°C and held for 3.. hours and then raised to 90-100°C for a further 20 hours. The reaction mass was then discharged and allowed to solidify to a waxy solid. This product is hereinafter referred to as Dispersant 7. Example 8 Intermediate 8 (5.93 parts) was heated to 60°C, phosphorus pentoxide (0.153 parts) added and the mixture stirred tinder nitrogen for 1 hour at 60°C. The temperature was raised to 90-100°C and held for a further 23 hours. The reaction mass was then discharged and allowed to solidify to a waxy solid. This product is hereinafter referred to as Dispersant 8. Example 9 Dispersant 1 (50.0 parts, Acid Value 27.36 mgs KOH/g) was heated until molten (60-70°C) and 2-amino-2-methyl-l-propanol (2.065 parts) added with stirring. The temperature was raised to 90-100°C and the mixture held with stirring for 1 hour. The reaction mass was then discharged and allowed to cool to a waxy solid. The product is hereinafter referred to as Dispersant 9. Exaπple 10 This was prepared in a similar manner to Dispersant Salt 1 but using Dispersant 1 (50.0 parts) and diethanolamine (2.43 parts) . The product is hereinafter referred to as Dispersant 10. Example 11 This was prepared in a similar manner to Dispersant Salt 1 but using Dispersant 1 (50.0 parts) and monoethanolamine (1.42 parts) . The product is hereinafter referred to as Dispersant 11. Example 12 This was prepared in a similar manner to Dispersant Salt 1 but using Dispersant 1 (50.0 parts) and 2-dimethylaminoethanol (2.065 parts) . The product is hereinafter referred to as Dispersant 12. Examples 13 to 51 and Comparative Examples A.B and C These examples were all prepared in analogous manner to that described for example 1 except that the Intermediate 1 and amount was replaced by the diol listed in Table 2 below and the amount of phosphorus pentoxide (PO) was varied as indicated in the table or replaced by polyphosphoric acid (PPA) as indicated. The physical form of the dispersant obtained in also indicated in Table 2. The dispersants obtained from these examples all bear the exaπple legend hereinafter. Thus, Dispersant 13 is the product from example 13 and Comparative Dispersant A is the product from Comparative Example A. TAB&E 2 Ex Diol Amount of Amount Amount of Appearance Diol of PO PPA 13 Intermediate 9 30 6.63 - paste 14 Intermediate 10 94 11 - oil 15 Intermediate 11 121 2.4 - wax 16 Intermediate 12 95 7.6 - wax 17 Intermediate 13 104 4.73 - wax 18 Intermediate 14 198 4.74 - wax 19 Intermediate 15 90 5.05 - wax 20 Intermediate 16 100 5.05 - wax 21 Intermediate 17 177 7.43 - wax TABLE 2 (continued) Ex Diol Amount of Amount of Amount Appearance Diol PO of PPA 22 Intermediate 18 112 1.9 - wax 23 Intermediate 19 116 1.57 - wax 24 Intermediate 20 96 3.79 - wax 25 Intermediate 21 158 5.57 - wax 26 Intermediate 22 101 2.37 - wax 27 Intermediate 23 120 2.37 - wax 28 Intermediate 24 150 2.37 - wax 29 Intermediate 25 95 0.71 - wax 30 Intermediate 26 80 1.58 - wax 31 Intermediate 27 95 1.58 - wax 32 Intermediate 28 115 1.58 - wax 33 Intermediate 29 150 1.58 - wax 34 Intermediate 30 109 0.79 - wax 35 Intermediate 31 73 0.32 - wax 36 Intermediate 32 121 1.39 - wax 37 Intermediate 33 125 1.18 - wax 38 Intermediate 34 101 1.26 - wax 39 Intermediate 35 130 1.25 - wax 40 Intermediate 36 95 0.95 - wax 41 Intermediate 37 124 0.59 - wax A PEG 1500 100 6.3 - wax B PEG 2000 100 4.73 - wax C Synperonic 100 - 3.84 oil PE L64 TABLE 2 (continued) Ex Diol Amount of Amount of Amount Appearance Diol O of PPA 42 Intermediate 38 81 - 3 paste 43 Pluronic 10R5 100 - 5.66 oil 44 Pluronic 17R4 100 - 4.12 oil 45 Pluronic 25R4 100 - 2.93 oil 46 Intermediate 39 71 - 2.06 paste 47 Pluronic 10R8 100 - 2.23 wax 48 Pluronic 17R8 100 - 1.31 wax 49 Pluronic 25R5 100 - 2.23 wax 50 Pluronic 25R8 100 - 0.89 wax 51 Pluronic 31R4 100 - 2.16 wax Examples 52 - 59 The following examples having the formulations described in Table 3 below were prepared by ball milling the ingredients on a laboratory shaker with 3mm glass beads for 17 hours. In each case the total weight was made up to lOg with water. All were fluid dispersions. TABLE 3 Example Amount Dispersant & Resin (a) Antifoam Rutile Ti0 2 Amount 52 6.5g Disp. 1 0.73g 0.05g 0.33g 53 6.5g Disp. 2 0.73g 0.05g 0.33g 54 6.5g Disp. 3 0.73g 0.05g 0.33g 55 6.5g Disp. 4 0.73g 0.05g 0.33g 56 7.0g Disp. 6 - - 0.14g 57 7.0g Disp. 7 - - 0.14g 58 7.0g Disp. 1 - 0.05g 0.42g 59 7.0g Disp. 8 - 0.05g 0.14g (a) Footnote to Table 3 The resin used was a 45% solids wholly acrylic emulsion polymer of pH 9 ± 0.5 supplied by ICI Resins, Waalwijk, Holland under the trade name NEOCRYL XK90. The antifoam was supplied by Henkel-Nσpco under the trade name DEHYDRAN 1293. Examples 60 to 62 Details of the millbase and letdown formulations for the water based paint system employed in Examples 60-62 are given in Table 4. The millbases were prepared by ball milling the ingredients in a high energy ball mill with 3mm glass beads for 30 minutes. After milling the millbase was converted into a usable paint by the addition of the letdown emulsion. TABLE 4 Example Example Example £__ 51 f___ Dispersant 1 2.8 Dispersant 2 2.8 Dispersant 3 2.8 Water 13.87 13.87 13.87 NEOCRYL XK90 4.51 4.51 4.51 DEHYDRAN 1293 0.32 0.32 0.32 TIOXIDE TR92 39.94 39.94 39.94 Letdown NEOCRYL XK90 94.51 94.51 94.51 Propylene Glycol 3.80 3.80 3.80 Footnote to Table 4 Aqueous solutions of Dispersants 1 to 3 are acidic so their pH was raised to 9 ± 1 with ammonia solution prior to the addition of the resin. Test panels were prepared by coating aluminiiim and primed steel panels using a mechanised wire wound K bar draw down system supplied by RK Print-Coat Instruments Ltd. ,Royston, Herts., England. The K bar was calibrated to leave a wet film thickness of 100 microns. The paint films were allowed to dry at ambient temperature for 90 minutes and then baked at 120°C for 30 minutes. The average gloss of each panel was calculated from the mean of 5 readings taken over the panel surface. These results are given in Table 5. TABLE 5 Averaσe 20° Gloss Example vwninium Panel Primed Panel 60 56.06 51.02 61 60.02 58.60 62 52.52 53.38 The moisture resistance of each paint was tested by immersing the aluminium panel in water at 80°C for 24 hours. In all cases none of the paints showed signs of blistering, shrinkage, or loss of adhesion. Examples 63 to 65 The paint formulation employed in these examples were prepared by the method described in examples 52 to 59 which were then coated, dried and tested in an identical manner to those set out in Examples 60 to 62. The only difference is the omission of resin from the millbase. Details of the formulations are given in Table 6 in which all quantities are in grammes. The results of the gloss measurements are given in Table 7. TABLE 6 Example Example Example Millbases SI ___. ≤__ Dispersant 1 1.29 Dispersant 7 1.29 Dispersant 8 0.86 Water 7.76 7.76 8.19 DEHYDRA 1293 0.16 0.16 0.16 TIOXIDE TR92 21.50 21.50 21.50 Letdown NEOCRYL XK90 53.10 53.10 53.10 Propylene Glycol 2.20 2.20 2.20 Footnote to Table 6 Aqueous solutions of Dispersants 1, 7 & 8 are acidic so their pH was raised to 9 ± 1 with ammonia solution prior to the addition of the other ingredients. TABLE 7 Average 20° Gloss Example Aluminium Panel Primed Panel 63 58.86 52.36 64 45.52 41.44 65 53.58 49.92 None of the paints applied to the aluminium panels showed signs of blistering, shrinkage or loss of adhesion on immersion in water at 80°C for 24 hours. Examples 66 to 102 and Comparative Examples D.E. F and G Mill bases were prepared by adding the dispersants (4.8 parts) listed in Table 8 below to water (37.6 parts) and 2-amino-2- methylpropanol (0.6 parts) and adjusting the pH to between 10 and 10.2 with 2-amino-2methylpropanol. The water dispersant mix was warmed on a steam bath to fully dissolve the dispersant. The aqueous solution of the dispersant was then cooled, poured into a dispermat pot and titanium dioxide (Tioxide TR92, 79.84 parts) added with stirring followed by 1mm diameter glass beads (180 parts) again with stirring. The mill bases were then milled at a speed of 3000 rmp on a Dispermat Fl disperser (VMA Getzmann, West Germany) for 30 minutes with no water running through the cooling jacket. The temperature during milling rose to between 30 and 40°C. The mill bases were then allowed to cool and the paints filtered from the glass beads. These paints were then let down to final volume by adding Neocryl XK90 resin and propylene glycol in the amounts given by the formulae Weight of Neocryl resin = Y x 212.4 122.84 Weight of propylene glycol = Y x 8.8 122.84 where Y is the yield of millbase. The let-down paints were allowed to stand overnight (16 hours) to de-aerate and were then coated onto primed and bare aluminium panels using a No 8 K-bar on an automatic coater (KCC 202, Zeneca Ltd) to give a wet film thickness of lOOμm. The film was air-dried for 90 minutes and then cured in an oven by baking at 120°C for 30 minutes. The 20° gloss of the dried paint film was finally measured using a Novo- gloss Meter (Rhopoint Instrumentation, UK) . A mill base using β-naphthol 10E0 was prepared in identical manner except that no 2-amino-2-methylpropanol was used and the amount of water was increased from 37.6 to 38.2 parts. The results are given in Table 8 below. TABEE 9 Average 20° Gloss Example Dispersant Aliiπtinium Panel Primed Panel 66 4 43.8 47.9 67 5 33.2 24.2 68 6 22.6 23.5 69 13 38.9 35.9 70 14 43.4 33.0 71 15 49.9 40.7 72 16 50.8 45.0 73 17 57.6 48.9 74 18 30.2 30.9 75 19 46.8 41.0 76 20 56.4 49.0 77 21 49.6 27.8 78 22 48.4 43.9 79 23 24.4 23.7 80 24 50.8 45.4 81 25 37.9 29.0 82 26 59.3 53.0 83 27 56.5 51.2 84 28 59.9 49.9 85 29 39.7 32.6 86 30 48.5 41.6 87 31 52.9 47.2 88 32 58.3 50.8 TABLE 8 (continued) Average 20° Gloss Exaπple Dispersant uminium Panel Primed Panel 89 33 56.4 47.5 90 34 49.2 39.3 91 35 NT NT 92 36 48.6 44.5 93 37 57.3 51.7 94 38 46.0 39.7 95 39 35.7 35.5 96 40 17.0 14.3 97 41 55.3 45.0 D A 34.1 37.0 E B 31.5 33.8 F C 23.9 19.4 98 42 57.2 50.8 99 43 54.3 48.2 100 44 56.4 50.4 101 45 52.1 49.6 102 46 37.3 30.2 103 47 32.5 32.8 104 48 39.5 35.1 105 49 38.7 35.3 106 50 38.4 32.5 107 51 42.8 38.3 G BNE 34.1 34.72 Footnote to Table 8 NT = Not tested, dispersant not sufficiently soluble. BNE = β naphthol-10-ethoxylate as disclosed in GB 2,060,715.

Claims: 1. A dispersant obtainable by reacting a polyethylene glycol with a molar excess of hydroxycarboxylic acid containing from 4 to 17 carbon atoms or lactone thereof and/or with a C 3-4 -alkylene oxide to form a polymeric diol and phosphating the diol to form a phosphate ester including its salt thereof with an alkali metal, ammonia, amine, alkanolamine or quaternary ammonium compound. 2. A dispersant as claimed in claim 1 wherein the phosphate ester is further partially esterified by reaction with an alcohol. 3. A dispersant as claimed in either claim 1 or claim 2 wherein the polyethylene glycol consists essentially of ethylene oxide units. 4. A dispersant as claimed in any one of claims 1 to 3 wherein the polymeric diol is of formula (1) H-A-0-[CH 2 -CH 2 -0] n -A-H (1) wherein O A is the group -[0-B-C] m - or the group -[0-D-J-; B is C 4-17 -alkylene,- D is C 3-4 -alkylene; m is from 2 to 50; and n is from 4 to 500. 5. A dispersant as claimed in claim 4 wherein the repeat unit O -[0-B-CJ m - is derivable from e-caprolactone. 6. A dispersant as claimed in either claim 4 or claim 5 wherein the ratio of the molecular weight of -A- and molecular weight of the group [-CH_CH 2 -0] n - is between 1.5:1 and 1:3 7. A dispersant as claimed is any one of claims 1 to 6 wherein the polyethylene glycol has a MW from 500 to 6000. 8. A dispersant as claimed in any one of claims 5 to 7 wherein the ratio of the MW's of poly(5-hydroxy hexanoic acid) derived from e- caprolactone and polyethylene glycol is from 1 to 1. 9. A process for making a dispersant as claimed in claim 1 which comprises reacting a polyethylene glycol with a molar excess of a hydroxycarboxylic acid containing from 4 to 17 carbon atoms or lactone thereof and/or with a C 3-4 -alkylene oxide to form a polymeric diol and phosphating the diol to form a phosphate ester. 10. A process as claimed in claim 9 wherein the polyethylene glycol is reacted with the hydroxycarboxylic acid or lactone thereof in the presence of an alkyl titanate. 11. A composition ^ comprising a dispersant as claimed in any one of claims 1 to 8 and a particulate solid. 12. A composition as claimed in claim 11 wherein the solid is a pigment. 13. A composition as claimed in either claim 11 or claim 12 which additionally comprises a liquid. 14. A composition as claimed in claim 13 wherein the liquid is water. 15. The use of a composition as claimed in claim 12 in an aqueous paint. 16. A polymeric diol of formula 1 H-A-0-[CH 2 CH 2 -0] n -A-H (1) wherein: 0 A is the group -[0-B-C] m ; B is - 17 -alkylene; m is from 2 to 50; and n is from 4 to 500.

Inventors: SCHOFIELD JOHN DAVID, THETFORD DEAN, SCHOFIELD, JOHN, DAVID, THETFORD, DEAN
Applicants: SCHOFIELD JOHN DAVID, THETFORD DEAN, ZENECA LTD, SCHOFIELD, JOHN, DAVID, THETFORD, DEAN, ZENECA LIMITED
Application year: 1995
Main classification: C08G65
IPC codes: B01F17, C08G63, C08G65, C08K3, C08L67, C08L71, C09D171