Method for the purification of reclaimed aqueous N-methylmorpholine N-oxide solution

Abstract: There is disclosed a method for purifying a used aqueous N-methylmorpholine N-oxide solution reclaimed from a spinning aqueous solution, which results from a coagulation solution into which a cellulose dope containing N-methylmorpholine N-oxide is extruded through a spinning die and from a washing solution for the coagulated cellulosic articles in manufacture processes for cellulose fibers or films, comprising adding an oxidant to the used aqueous N-methylmorpholine N-oxide solution to remove impurities therefrom through oxidizing N-methylmorpholine to N-methylmorpholine N-oxide and break down of the chromophores of the impurities. Utterly distinguished from conventional methods in the principle, the method is very simple and efficient as well as far superior to the conventional methods using ion exchange resin in the decoloration. In addition, it needs not suffer a loss of amine oxide as usual in the ion exchange resin. Further, the oxidant can achieve the decolorization without influence of the concentration of amine oxides. The amine oxide decolorized by the oxidant may be used to prepare the cellulose dope without any more purification. Provided that sequential use of the oxidant and the resin or active carbon, there are brought about much higher efficiency as well as much purer aqueous amine oxide solution.

Description: The present invention relates, in general, to regeneration of N-methylmorpholine N-oxide used to prepare a cellulose fiber or film and, more particularly, to a method for decolorizing a used aqueous N-methylmorpholine N-oxide solution through purification of coloring impurities of an aqueous solution after spinning. For cellulose fiber or film, a spinning cellulose dope containing N-methylmorpholine N-oxide as a solvent is usually extruded into an aqueous coagulation solution through a spinning die with the N-methylmorpholine N-oxide being eluted, and then subjected to washing. In this procedure, there is generation of an enormous quantity of spinning aqueous solution (a coagulating solution and a washing solution) in which N-methylmorpholine N-oxide is dissolved at a low content. The cellulose dope employing N-methyl morpholine N-oxide as a solvent is prepared at a high temperature, and the dope is heated when it is extruded through a spinning die. However, N-methylmorpholine N-oxide is apt to decompose due to the high temperature, generating coloring impurities. Consequently, the cellulose dope may be discolored by them. Most of the coloring impurities are eluted along with N-methyl morpholine N-oxide in the coagulating and the washing processes, but some remain unremoved even by further washing processes, coloring the final articles, such as fibers or films, ultimately. Therefore, a bleaching process is additionally required. In order to reclaim and reuse the N-methylmorpholine N-oxide which is dissolved in the spinning aqueous solution at a low content, concentration is performed, followed by purification. N-methylmorpholine N-oxide reclaimed but not purified is tinged with dark brown by the coloring impurities contained. In the case that the reclaimed N-methylmorpholine N-oxide is used to produce fibers or films without removing the coloring impurities, continuous accumulation of them comes to tinge the final articles with color, deleteriously affecting the final articles. As a basic solution for the discoloration problem, there is use of pure cellulose (commercially available wood pulp with little coloring organic materials) and highly purified N-methylmorpholine N-oxide. DD-A-259,863 discloses treatment with a cation exchange resin of sulfonized divinyl benzene-styrene copolymer at pH 5-8 (H 3 PO 4 ), thereby increasing purity of an aqueous N-methylmorpholine N-oxide solution obtained from oxidation of N-methylmorpholine. In many patents including EP-A-0 047 929, DE-A-3 034 685 (Akzo) and DE-A-41 06 029 (Lenzing A.-G.), PCT W083/04415, US-A-4,581,072 (Courtaulds), and DD-A-229 708, DD-A-218 104 (VEB Chem) and DD-A-158 656 (ADW I.F.P.), there are described a variety of antioxidants to suppress oxidative thermal degradation of both cellulose and N-methylmorpholine N-oxide. EP-A-467,008 (Lenzing A. -G.) discloses that 0.01 - 2 % of H 2 O 2 along with a stabilizing additive is added to prepare a cellulose dope, thereby suppressing the oxidative thermal degradation of N-methylmorpholine N-oxide in the course of production and extrusion of the dope. However, even though highly pure raw materials are used and the antioxidants are added as mentioned above, perfect suppression of oxidative thermal degradation is impossible. In fact, alkaline bleaching (e.g. aqueous sodium hypochlorite solution or aqueous hydrogen peroxide/sodium hydroxide solution) is carried out for the colored article, followed by further processes such as neutralization and washing. According to PCT WO 92/14871 (Courtaulds), it is reported that the alkaline bleaching, however, causes fibrillation of fiber, leading to occurrence of defects which are fatal to dyeing property of fabric and to forming pills on its surface. An effort has been made to purify the aqueous N-methylmorpholine N-oxide solution reclaimed after the production of cellulose fiber or film. For example, DD-A-254 199 A1 (VEB Chem.) suggests a purification method comprising passing an aqueous solution containing 5 to 60 % by weight of amine oxide through an anion exchange resin of styrene-divinyl copolymer. According to this patent, the aqueous amine oxide solution is treated initially with a weak anion exchange resin with the amine group of -CH 2 N(CH 3 ) 2 and then with a resin with the tertiary ammonium group of -CH 2 [N(CH 3 ) 3 ] + OH - . After passing through the first resin column, the deep brown aqueous solution is purified into pale brown or yellow, which is further purified into pale yellow or colorless by the second resin column. The supra patent also says that the used resins can be regenerated by treatment with 3 wt% aqueous sodium hydroxide solution and 10 wt% aqueous sodium chloride solution. Such method can take off coloring impurities from the aqueous amine oxide solution, however, the regeneration of resin by strong alkali is unsatisfactory, so that the separation efficiency of the regenerated resin drops largely. In addition, EP-A-0 427 701 (Lenzing A. -G.) discloses use of a resin with -CH 2 [N(CH 3 ) 3 ] + X - or -CH 2 [N(CH 3 ) 2 (CH 2 OH)] + X - group, wherein X - is an anion of organic or inorganic acid. The resin is regenerated by a volatile acid, such as hydrochloric acid, carbonic acid, formic acid and acetic acid, which in turn is reclaimed by distillation. The resin regenerated is able to purify the aqueous amine oxide solution and thus, to give decolorized solution in a high efficiency. However, when strong inorganic acid, e.g. hydrochloric acid is employed, there is an disadvantage that apparatus is highly apt to be corroded because hydrochloric acid or a salt of Cl - is eluted along with the aqueous solution. Unlike two supra patents using either alkali or acid to regenerate the resin, PCT WO92/11287 (Courtaulds) suggests use of both alkali and acid stepwise to regenerate resin, thereby more efficiently removing the impurities adsorbed on the resin. According to the patent, an anion exchange resin with -CH 2 [N(CH 3 ) 3 ] + X - or -CH 2 [N(CH 3 ) 2 (CH 2 OH)] + X - group which has purified the reclaimed aqueous amine oxide solution is treated initially with an aqueous 1-10 wt % hydrochloric acid or sodium chloride solution to take off most of coloring impurities with the X - ions of resin being changed into Cl - ions, and then treated with an aqueous 1-10 wt% sodium hydroxide solution with X - ions of resin being changed into OH - ions. In the second treatment, sodium hydroxide is used in the same equivalent as the strong acid or in a little larger equivalent (mole ratio 1.0 - 1.1) to elute a neutralized solution containing only sodium chloride, thereby preventing the corrosion of apparatus. All the described methods using ion exchange resins can purify the aqueous amine oxide solution and thus give a decolorized solution, but generate a strong acidic solution, a strong alkaline solution or a salt solution containing coloring impurities during the regeneration of resin. To prevent the pollution by these waste solution, re-treatment processes such as concentration and incineration are required. In addition, since the resin is not lasting but has a life span of 2-3 years, equipment and its operation cost too much. Further, because amine oxide as well as the coloring impurities is well absorbed into the resin, the loss of amine oxide is considerable at high concentration. For example, when an aqueous 62 wt% amine oxide solution is treated with anion exchange resin, an aqueous 43 wt% amine oxide solution is obtained after purification and decolorization. Furthermore, as the concentration of amine oxide is higher (e.g. not less than 40 %), the absorption efficiency of resin for the coloring impurities becomes low steepy. This is a main obstacle that restrains the resin from being used to purify an aqueous amine oxide solution with a high concentration. So, there is a troublesome problem that the resin should deal with more increased quantity of aqueous amine oxide solution diluted into a lower concentration. In general, active carbon rather than the ion exchange resins is frequently used to remove the coloring impurities because of its cheapness. It is well known that active carbon is used in two forms: bead and powder. Active carbon bead capacitates continuous work for taking off the coloring impurities. In addition, used active carbon bead can be regenerated, like the ion exchange resin. But, it is low in adsorption rate and has difficulty in yielding a high purity. On the other hand, active carbon powder is superior in adsorption rate and capable of purifying the aqueous amine oxide solution in high degrees in batch type. However, active carbon powder is uneconomical because the used cannot be regenerated. Further, active carbon powder does not allow continuous work. In purifying the aqueous amine oxide solution, active carbon bead can treat it successively and be used repetitively through regeneration. Active carbon bead, however, is remarkably low in decolorizing power as compared with the anion exchange resin. Especially, the coloring impurities contained in a high concentration of the aqueous amine oxide solution are not not readily absorbed into the active carbon bead relative to on the anion exchanger. By contraries, active carbon powder is much superior to the anion exchanger in decolorizing and purifying the reclaimed amine oxide at high content as well as at low content, even if it is less economical than active carbon bead. Meanwhile, it is reported in Cellulose Chem. Technol. 20, pp. 289-301 (1986) by H. Lang et al that when a cellulose dope containing N-methylmorpholine N-oxide is subjected to high temperature, both cellulose and N-methylmorpholine N-oxide are decomposed, mainly giving N-methylmorpholine, morpholine and carbon dioxide. It is also reported that N-methylmorpholine amounts up to 85 % of the decomposed products from N-methylmorpholine N-oxide. In "Das Papier" 40 (12), pp 615-619 (1986) F. A. Buijtenhuijs et al also report a similar result that the decomposed products of N-methylmorpholine N-oxide are mainly comprised of N-methylmorpholine and assert that, when cellulose/N-methylmorpholine N-oxide solution is heated at 120 °C for 16 hours, N-methylmorpholine N-oxide is decomposed in an amount of about 2 % by weight in the presence of propyl gallate, an antioxidant, and in an amount of about 5 % by weight in the absence of propyl gallate. They also report that metal ions such as copper and iron ions contained in a spinning dope catalyze the decomposition of amine oxide as well as the cellulose. According to Zh. Prikl. Khim. (Leningrad), 60(9) 2063-2067 (1987) and Zh. Prikl. Khim. (Leningrad), 61(1) 117-123 (1988), both by A. M. Bochek et al, a cellulose solution in amine oxides such as triethylamine N-oxide, N-methylmorpholine N-oxide and N,N-dimethylethanolamine N-oxide partially decompose at high temperatures, not only into N-methylmorpholine and morpholine with the N-O bond of amine oxide being broken down, but into olefins. It is well known that when amine oxides having beta-hydrogen are decomposed at high temperatures, hydroxyl amines and olefins are generated with the oxygen moiety of amine oxide catching the beta-hydrogen. Such reaction is widely utilized for a synthesis path for new olefins (reference, J. D. Roberts and M. C. Caserio, "Basic Principles of Organic Chemistry", W. A. Benjamin, Inc., New York, publ. 1964). There has been known no detailed and accurate information for the compositions and components of the coloring impurities resulting from the heat decomposition of N-methylmorpholine N-oxide. Nonetheless, it is believed that even little amount of the coloring impurities tinge the aqueous amine oxide solution reclaimed with dark brown and they are in close relation with the olefin compounds generated on heat decomposition of N-methylmorpholine N-oxide. It is, therefore, an object of the present invention to provide a method for purifying an aqueous N-methylmorpholine N-oxide solution reclaimed from a used aqueous solution after spinning. The method is superior in decolorizing the solution. It is another object of the present invention to provide a method for purifying an aqueous N-methylmorpholine N-oxide solution reclaimed from a used spinning aqueous solution, profitable in economy and high in efficiency. It is a further object of the present invention to provide a method for purifying an aqueous N-methylmorpholine N-oxide solution reclaimed from a used spinning aqueous solution, capable of decoloration without influence of the concentration of amine oxide. Based on the intensive study by the present inventors, the present invention is designed in the idea that addition of a small amount of oxidant into the reclaimed aqueous N-methylmorpholine N-methylmorpholine, N-oxide solution can oxidize methylmorpholine, a main heat decomposition product, into N-oxide and remove the coloring tinge through oxidation of the chromophore of the coloring impurities. In accordance with the present invention, the above objects could be accomplished by a provision of a method for purifying a used aqueous N-methylmorpholine N-oxide solution reclaimed from a spinning solution, which results from a coagulation solution into which a cellulose dope is extruded through a spinning die and from a washing solution for the coagulated cellulosic articles in manufacture processes for cellulose fibers or films, comprising addition of an oxidant into the used aqueous N-methylmorpholine N-oxide solution to remove impurities therefrom through oxidation N-methylmorpholine into N-methylmorpholine N-oxide and break down of the chromophores of the impurities. These and other objects and advantages of the present invention will become more apparent as the following description proceeds. In accordance with an aspect of the present invention, an oxidant is added into an aqueous N-methylmorpholine N-oxide solution reclaimed from a used spinning aqueous solution including a coagulation solution and a washing solution which are generated when a cellulose dope containing N-methylmorpholine N-oxide as a solvent is extruded into the coagulation solution through a spinning die and then washed. The aqueous N-methylmorpholine N-oxide solution reclaimed from the used spinning aqueous solution usually contains N-methylmorpholine N-oxide in amounts ranging from approximately 5 to approximately 75 % by weight. Typically, the reclaimed N-methylmorpholine N-oxide solution is tinged with dark brown. Depending on the colored extent of the reclaimed aqueous N-methylmorpholine N-oxide solution, the oxidant is added in an amount of approximately 0.1 to approximately 10 % by weight with a range of approximately 1 to approximately 5 % by weight being preferred. Maintenance of the colored, aqueous N-methylmorpholine N-oxide solution added with the oxidant at a temperature ranging from approximately 20 to approximately 100 °C, preferably approximately 60 to approximately 80 °C allows the solution to be decolorized gradually and to be changed into reusable one finally. The time for the decolorization is dependent on the colored extent of the aqueous N-methylmorpholine N-oxide solution, and the kind and amount of the oxidant. Usually, high temperature promotes the decoloration. For example, it takes several days at room temperature for the dark brown solution to be decolorized to pale yellow, whereas it takes about 30 minutes at 70 °C to yellow and only additional 30 minutes at the same temperature to pale yellow or almost colorless. According to the present invention, aqueous hydrogen peroxide and aqueous peroxides of volatile organic acids, such as HCO 3 H, CH 3 CO 3 H, and CH 3 CH 2 CO 3 H, may be used as the oxidant. Such peroxides of volatile organic acid, however, are disadvantageous in that their organic acids remain in the aqueous amine oxide solution. Thus, aqueous hydrogen peroxide is more preferable. In accordance with another aspect of the present invention, the resulting aqueous N-methylmorpholine N-oxide solution purified is preferably deprived of metal ions in an ordinary manner. Since metal ions, especially, iron or copper ions, promote the decomposition of amine oxides at high temperatures, they should not be accumulated in recycling amine oxides. Metal ions contained in the aqueous amine oxide solution may result from metal apparatuses such as metal vessels used during the total procedure as well as from a trace amount of metals captured by the cellulose or amine oxides. Therefore, a cation exchange resin may be used to remove the metal ions, especially, iron or copper ions. Alternatively, chitosan may preferably be used for the same purpose. Chitosan is very fast in absorbing and detaching the metal ions. In case of using chitosan, the metal ions absorbed into chitosan are taken off therefrom in a conventional manner, for example, using ethylenediamine tetraacetic acid (EDTA). Thereafter, the chitosan can be recycled. With regard to order of the removal of metal ions, it may be carried out, prior to the decoloration as done in conventional methods. To the contrary, in the present invention, the metal ions are more preferably removed by means of cation exchange resin or chitosan, subsequent to the decoloration by the oxidant. The reason is as follows. In conventional methods, the coloring ingredients are removed by absorption of anion exchange resins, whereas, in the present invention, they disappear by oxidation of the chromophores thereof, so that even trace amount of the oxidized ingredients may be left in the reclaimed solution. Thus, the removal of metal ions by chitosan or cation exchange resin subsequent to the decoloration by oxidation can be accompanied by the elimination of the oxidized products of the coloring ingredients through adsorption. As described hereinbefore, the method according to the present invention is advantageous in many aspects. On one hand, let us compare it with conventional and known methods using ion exchange resin. The conventional and known methods using ion exchange resin are complicated because the reclaimed aqueous N-methylmorpholine N-oxide solution is purified by absorbing the coloring heat-decomposition products into an anion exchange resin, which is subjected to regeneration by alkali and/or acid, according to them. In addition, the conventional methods are uneconomical because they require immense cost for equipment and its maintenance and the life span of resin is short. Further, the conventional methods are problematic in that pollution is caused by the waste solution generated during the regeneration of resin. On the contrary, the present method is utterly distinguished from the conventional methods in the principle that the presence of a small amount of oxidant in the reclaimed aqueous N-methylmorpholine N-oxide solution oxidizes N-methylmorpholine, amounting up to 85 % of the heat-decomposition products, into N-methylmorpholine N-oxide and removes trace amount of the coloring impurities through oxidation of the chromophores, to decolorize the solution. So, the present method is very simple and efficient. In addition, it is far superior to the conventional methods using ion exchange resin in the decoloration and needs not suffer a loss of amine oxide as usual in the ion exchange resin. Further, distinguished from the ion exchange resin of conventional methods, the oxidant according to the present invention can achieve the decoloration without influence of concentration of amine oxide. On the other hand, with relation to active carbon bead, whenever used amine oxide is reclaimed, it must be purified. Its purification by either active carbon bead or ion exchange resins requires immense cost for maintenance. In case of active carbon powder, its decolorizing capacity is far better than that of the resin or active carbon bead, but there is such a disadvantage that active carbon powder is difficult to regenerate. The amine oxide decolorized by the oxidant according to the present method may be used to prepare the cellulose dope without any more purification. However, provided that amine oxides are recycled many times, anion exchange resin or active carbon bead or powder may additionally be used subsequent to the purification of the present invention. In this case, in comparison to the conventional methods using either only anion exchange resin or active carbon, the present method is much higher in efficiency as well as gives a much purer aqueous amine oxide solution. The preferred embodiments of the present invention will now be further described with reference to the following specific examples. In the following examples, there were used N-methylmorpholine N-oxide solutions that were reclaimed after the preparation of cellulose dope was carried out at higher temperature and for longer time than those in a commercial process of the cellulose dope and fiber manufacture suggested in Korean Patent Application No. 93-18018. Using a UV-spectrophotometer, the concentration of impurities tingeing the aqueous amine oxide solution with color was measured, and its results were represented in amine oxide optical density (AOOD) of a solution containing 1 % by weight of the amine oxide. COMPARATIVE EXAMPLE 1 Into 100 mL of a reclaimed spinning solution A containing 30 % by weight of N-methylmorpholine N-oxide, ion exchange resin (Amberlite IRA 416), active carbon powder (Junsei Chemical, purity 1 class) and active carbon bead (Samcheonli Chemical Co., coal) were separately added in a predetermined amount and then gently stirred at room temperature for 2 hours. The resin, the active carbon powder and the active carbon bead were filtered off, and AOOD values for the resulting filtered solutions were measured. The results are shown in the following Table 1. Solution Kind UV Spectrophotometry 350 nm 400 nm 450 nm AOOD % AOOD Drop AOOD % AOOD Drop AOOD % AOOD Drop Spinning Sol'n A (100 mL) 0.0940 - 0.0467 - 0.0280 - Amberlite IRA 416 2 g 0.0330 64.9 0.0124 73.4 0.0084 70.0 5 g 0.0302 67.9 0.0117 74.9 0.0083 70.4 10 g 0.0275 70.7 0.0107 77.1 0.0082 70.7 Active Carbon Powder 2 g 0.0055 94.1 0.0014 97.0 0.0004 98.6 5 g 0.0014 98.5 0.0003 99.4 0.0001 99.6 Active Carbon Bead 2 g 0.0399 57.6 0.0158 66.2 0.0117 58.2 COMPARATIVE EXAMPLE 2 Into 100 mL of a reclaimed spinning solution B containing 57.6 % by weight of N-methylmorpholine N-oxide, 2 g of each ion exchange resin (Amberlite IRA 416), active carbon powder (Junsei Chemical, purity 1 class) and active carbon bead (Samcheonli Chemical, coal) was added respectively and then gently stirred at room temperature for 2 hours. The resin, the active carbon powder and the active carbon bead were filtered off, and AOOD values for the resulting filtered solutions were measured. The results are shown in the following Table 2. Solution Kind UV Spectrophotometry 350 nm 400 nm 450 nm AOOD % AOOD Drop AOOD % AOOD Drop AOOD % AOOD Drop Spinning Sol'n B 0.04549 - 0.01840 - 0.00868 - Amberlite IRA 416 0.02474 45.6 0.00912 50.4 0.00421 51.5 Active Carbon Powder 0.02193 51.8 0.000860 53.3 0.00439 49.4 Active Carbon Bead 0.04211 7.4 0.01667 9.4 0.00772 11.1 EXAMPLE 1 Into 100 mL of a spinning solution A containing 30 % by weight of N-methylmorpholine N-oxide, aqueous hydrogen peroxide was added in an amount of 3 % by weight of hydrogen peroxide based on the total weight of the solution and then, kept at 70 °C for a predetermined time. AOOD values for this solution were measured. After reacting with the aqueous hydrogen peroxide from 120 to 360 minutes, the solution was mixed with each of active carbon powder and Amberlite IRA 416 in an amount of 2g/100 mL. Subsequently, the resulting solution was gently stirred at room temperature for 1 hour, and the resin and the active carbon powder were filtered off. AOOD values for the resulting filtered solutions were measured. The results of measurement are shown in the following Table 3. Solution Kind UV Spectrophotometry 350 nm 400 nm 450 nm AOOD % AOOD Drop AOOD % AOOD Drop AOOD % AOOD Drop Spinning Sol'n A 120 min. 0.0067 92.9 0.00130 97.2 0.00033 98.8 240 min. 0.0047 95.0 0.00067 98.6 0.00017 99.4 360 min. 0.0040 95.7 0.00033 99.3 0.00003 99.9 Active Carbon Powder 0.0001 99.9 0 100 0 100 Amberlite IRA 416 0.0013 98.6 0 100 0 100 EXAMPLE 2 Into 100 mL of the same spinning solution as that of Example 1 reacted with aqueous hydrogen peroxide for 360 minutes, 2 g of each Amberlite IRA 416, cation exchange resin (Amberlite IR 120 transformed into H-form) and chitosan was added respectively and then, gently stirred. Filtration was carried out to remove the Amberlite IRA 416, the cation exchange resin and the chitosan. Each of the filtered solutions was investigated to measure the amount of iron and copper ions. The result was that 20 ppm/11 ppm of iron/copper ion was reduced into 4.4 ppm/3 ppm, 1.3 ppm/0.9 ppm and 3.5 ppm/0.7 ppm in Amberlite IRA 416, Amberlite IR 120 and chitosan, respectively. EXAMPLE 3 Into 100 mL of a reclaimed spinning solution C containing 30 % by weight of N-methylmorpholine N-oxide, aqueous hydrogen peroxide was separately added in an amount of 3 % by weight and 5 % by weight of hydrogen peroxide. The two resulting solutions were kept at a temperature of 60 and 90 °C, respectively. With the lapse of reaction time, AOOD values for the solutions were measured. The results are shown in the following Table 4. wt% H 2 O 2 /°C Temp. Reac.Time Min. UV Spectrophotometry 350 nm 400 nm 450 nm AOOD % AOOD Drop AOOD % AOOD Drop AOOD % AOOD Drop Spinning Sol'n C 0.12000 0.06367 0.03067 3/60 60 0.06400 46.7 0.02367 62.8 0.00967 68.7 3/60 120 0.04800 60.0 0.01733 72.8 0.00800 73.9 3/60 260 0.02967 75.3 0.00900 85.7 0.00333 89.1 5/90 15 0.04467 62.8 0.01600 74.9 0.00733 76.1 5/90 30 0.01733 85.6 0.00500 92.1 0.00200 93.5 5/90 60 0.01333 88.9 0.00333 94.8 0.00167 94.6 5/90 95 0.01133 90.6 0.00300 95.3 0.00133 95.7 EXAMPLE 4 In 100 mL of the same spinning solution as that of Comparative Example 2 containing 57.6 % by weight of N-methylmorpholine N-oxide, aqueous hydrogen peroxide water was separately added in an amount of 1 and 3 % by weight of hydrogen peroxide based on the total weight of the solution and then, kept at 70 °C. With the lapse of reaction time, AOOD values for the solutions were measured. The results are shown in the following Table 5. wt% H 2 O 2 Reac.Time Min. UV Spectrophotometry 350 nm 400 nm 450 nm AOOD % AOOD Drop AOOD % AOOD Drop AOOD % AOOD Drop 1 120 0.02257 50.4 0.00764 58.5 0.00278 68.0 1 240 0.01875 58.8 0.00712 61.3 0.00226 74.0 1 360 0.01563 65.6 0.00521 71.7 0.00208 76.0 3 120 0.01389 69.5 0.00469 74.5 0.00191 78.0 3 240 0.01042 77.1 0.00295 84.0 0.00122 85.9 3 360 0.00903 80.1 0.00243 86.8 0.00104 88.0 Other features, advantages and embodiments of the invention disclosed herein will be readily apparent to those exercising ordinary skill after reading the foregoing disclosures. In this regard, while specific embodiments of the invention have been described in considerable detail, variations and modifications of these embodiments can be effected without departing from the spirit and scope of the invention as described and claimed.

Claims: A method for purifying a used aqueous N-methylmorpholine N-oxide solution reclaimed from a spinning aqueous solution, which results from a coagulation solution into which a cellulose dope containing N-methylmorpholine N-oxide is extruded through a spinning die and from a washing solution for the coagulated cellulosic articles in manufacture processes for cellulose fibers or films, comprising addition of an oxidant into the used aqueous N-methylmorpholine N-oxide solution to remove impurities therefrom through oxidizing N-methylmorpholine to N-methylmorpholine N-oxide and break down of the chromophores of the impurities. Amethod according to Claim 1, wherein said oxidant is aqueous hydrogen peroxide. A method according to claim 1 or 2, wherein said oxidant is added in an amount of approximately 0.1 to approximately 10 % by weight of hydrogen peroxide based on the total weight of the used aqueous solution. A method according to any one of Claims 1 to 3, wherein said oxidant is reacted at temperatures ranging from about 20 to about 100 °C. A method according to any one of Claims 1 to 4, wherein said used aqueous N-methylmorpholine N-oxide solution reclaimed from said spinning solution contains N-methylmorpholine N-oxide in an amount of approximately 5 to approximately 75 % by weight. A method according to any one of Claims 1 to 5, further comprising purifying the aqueous N-methylmorpholine N-oxide solution deprived of impurities by said oxidant with active carbon or anion exchange resin. A method according to any one of Claims 1 to 5, further comprising treating the aqueous N-methylmorpholine N-oxide solution deprived of impurities by said oxidant with cation exchange resin or chitosan, to remove metal ions therefrom.

Inventors: CHONG SOO PARK, SEONG MU JO, WHA SEOP LEE, YONG KEUN HONG
Applicants: KOREA INST SCIENCE TECHNOLOGY, KOREA INSTITUTE OF SCIENCE AND TECHNOLOGY
Application year: 1995
Main classification: D01F13
IPC codes: D01F2, D01F13