Silicone containing water-in-oil emulsion

Abstract: A water-in-oil emulsion and a method of making said emulsion in which the emulsion includes 5 to 50 percent by weight of an organic oil; 44 to 94.5 percent by weight of water; and 0.5 to 5 percent by weight of a water-dispersible silicone wax. The emulsion is free of organic emulsifying agents. The water-dispersible silicone is a wax derived from the reaction of ≡SiH containing siloxane; (ii) a linear C₃₀+ organic alpha-olefin; and (iii) an unsaturated ethylene oxide polymer. Emulsions having a viscosity of 150,000 to 200,000 mm²/s (centistokes) are described.

Description: This invention is directed to a silicone terpolymer formed from three components: (i) an ≡SiH-containing siloxane; (ii) an organic alpha-olefin; and (iii) an unsaturated ethylene oxide polymer. Silicones containing long-chain organic substitution in the molecule which are waxes are not water-dispersible. Silicones containing polyether substitution in the molecule which are water-dispersible are not waxes. The problem solved by the present invention is to make a silicone which is a water-dispersible wax which can be used in the formation of water-in-oil emulsions without the need for any organic emulsifying agent. This problem is solved, according to the present invention, by forming a water-dispersible silicone wax which contains in its molecule both long-chain organic substitution and polyether substitution. Such a water-dispersible silicone wax may be prepared by chemically combining (i) an ≡SiH-containing siloxane polymer or copolymer; (ii) an high melting C 30+ organic alpha-olefin, blend or fraction; and (iii) an high melting unsaturated ethylene oxide polymer having the formula: H 2 C=CH-CH 2 -O(CH 2 CH 2 O) x H, in which x has a value of at least sixteen (16). The softening point of an high melting C 30+ organic alpha-olefin is about 60°C. The softening point of an high melting unsaturated ethylene oxide polymer is about 38°C. Depending upon the ratio of substitution, one skilled in the art would expect that a silicone containing in its molecule both an high melting C 30+ organic group and an high melting ethylene oxide group would have a softening point intermediate between the softening point of a silicone containing only the high melting C 30+ organic group (60°C) and a silicone containing only the high melting ethylene oxide group (38°C). However, it is surprising and unexpected that the water-dispersible silicone wax terpolymer of the present invention has a softening point higher (75°C) than either, and features a large percentage of substitution by the high melting C 30+ organic group (60°C) and a small percentage of substitution by the high melting ethylene oxide group (38°C). Because of these unique and unexpected characteristics, our water-dispersible silicone wax terpolymer possesses an utility as a water-in-oil emulsifying agent. It is also capable of producing stable, high viscosity emulsions which are free of any organic emulsifying agent. These emulsions have particular application in the personal care segment of the consumer market. It is an object of our invention to provide a water-dispersible silicone wax. It is also an object of this invention to provide a new silicone composition which has a softening point higher than would be expected of a silicone containing in its molecule a large percentage of substitution by an high melting C 30+ organic group and a small percentage of substitution by an high melting ethylene oxide group. It is a further object of the invention to form water-in-oil emulsions which are free of organic emulsifying agents. Our water-dispersible silicone wax is prepared by chemically combining three components. The first component is an ≡SiH-containing siloxane polymer or copolymer. This siloxane polymer can be in the form of a linear polymethylsiloxane such as Me 3 SiO(MeHSiO) x SiMe 3 . The siloxane can also be a linear polymethylsiloxane-polydimethylsiloxane copolymer such as Me 3 SiO(MeHSiO) x (Me 2 SiO) y SiMe 3 , in which the different units along the main backbone chain of the copolymer have a random distribution. In both formulaes, Me denotes the methyl radical and x and y denote integers. These siloxane polymers and copolymers are commercially available. However, to produce the water-dispersible silicone wax of this invention, the value of the integer x must be from twenty (20) to one hundred (100). In addition, the value of the integer y must be from one (1) to one hundred (100), with the proviso that the ratio of x/y is at least two to one (2:1) or above. Our second component is an high melting linear C 30+ organic alpha-olefin , blend or fraction. This material is available commercially as a chemical composition with an average of twenty-four or more carbon atoms, preferably thirty carbon atoms or more. Exemplary of such commercial products is a line of alkene chemicals manufactured and marketed under the trademark GULFTENE® by the Chevron Chemical Company, Houston, Texas, USA. One such product is GULFTENE® 24-28, which is an alpha-olefin fraction containing a blend of alpha-olefins with a weight distribution of mixed C 22 to C 30+ alkenes. This blend or fraction includes about one percent of C 22 alkenes, about thirty percent of C 24 alkenes, about thirty-nine percent of C 26+ alkenes, about twenty percent of C 28 alkenes and about ten percent of C 30+ alkenes. The average number of carbon atoms in this blend is twenty-four (24). Another and more preferred product is GULFTENE® C 30+ which is an alpha-olefin fraction containing a blend of alpha-olefins with a weight distribution of mixed C 28 to C 30+ alkenes. This blend or fraction includes about twenty-two percent of C 28 alkenes and about seventy-eight percent of C 30+ alkenes. The average number of carbon atoms in this blend is thirty (30). The third component is an high melting unsaturated ethylene oxide polymer having the formula H 2 C=CH-CH 2 -O(CH 2 CH 2 O) z H, in which z must have a value of at least sixteen. These waxy polyether materials are also commercially available. The softening point of such polyether waxes is 28°C when the degree of polymerization is sixteen, and reaches a maximum of 50°C when the degree of polymerization is twenty-eight (28) or more. Our silicone terpolymer is made by chemically combining stoichiometric amounts of the three components in the presence of a platinum catalyst such as chloroplatinic acid. Sufficient amounts of the ≡SiH-containing siloxane polymer or copolymer are employed to provide a slight excess of SiH. In the first step, the siloxane polymer and the alpha-olefin fraction are reacted in the presence of platinum. Additional amounts of the alpha-olefin fraction can be added following the first step. In the second step, the unsaturated ethylene oxide polymer is added and reacted. Additional amounts of the alpha-olefin fraction can be added following the second step. The reaction is carried out at temperatures in the range of 95 to 130°C. While chloroplatinic acid is the preferred catalyst, any suitable platinum-containing catalyst may be employed. Upon cooling, the wax reaction product can be used in the preparation of organic emulsifier free water-in-oil emulsions. These emulsions are formed from an oil phase and a water phase. Neither phase contains an organic emulsifying agent. The oil phase contains the water-dispersible silicone wax and one or more organic emollient oils. An electrolyte in the water phase may be required for the purpose of stabilization. Mixing, stirring, agitation or homogenization of the two phases yields a stable organic emulsifier free water-in-oil emulsion. A distinct advantage and benefit of our invention is that it enables one skilled in the art, by a simple means, to formulate high viscosity emulsions, without the need for complex equipment for reducing particle size or expensive thickening and gelling agents. Thus, water-in-oil emulsions having a viscosity in excess of 100,000 mm 2 /s (centistokes) can be produced and, more preferably, emulsions having a viscosity in excess of 150,000 mm 2 /s (centistokes). Water-in-oil emulsions which are most preferred according to our invention have a viscosity in the range of 150,000 to 200,000 mm 2 /s (centistokes) or more. Water-in-oil emulsions prepared according to this invention contain from 5 to 50 percent by weight of one or more organic oils as an emollient, from 44 to 94.5 percent by weight of water, from zero up to one percent by weight of an emulsion stabilizer which can be an electrolyte such as sodium chloride or ammonium chloride, and from 0.5 to 5 percent by weight of the water-dispersible silicone wax. Emollient oils which can be employed in our invention include mineral oil, peanut oil, sesame oil, avocado oil, coconut oil, cocoa butter, almond oil, safflower oil, corn oil, cotton seed oil, castor oil, olive oil, jojoba oil, paraffin oil, cod liver oil, palm oil, soybean oil, wheat germ oil, linseed oil and sunflower seed oil; fatty acid esters such as isopropyl myristate, isopropyl palmitate, isopropyl stearate, butyl stearate, cetyl stearate, diisopropyl adipate, isodecyl oleate, diisopropyl sebacate and lauryl lactate; fatty acids such as lauric, myristic, palmitic, stearic, oleic, linoleic and behenic acids; fatty alcohols such as lauryl, myristyl, cetyl, stearyl, isostearyl, oleyl, ricinoleyl, erocyl and 2-octyl dodecanol, alcohol; lanolin and its derivatives such as lanolin, lanolin oil, lanolin wax, lanolin alcohols, lanolin fatty acids, isopropyl lanolate, ethosylated lanolin and acetylated lanolin alcohols such as ACETULAN®, a trademark and product of Amerchol Corporation, Edison, New Jersey; and hydrocarbons such as petrolatum and squalane. Water-in-oil emulsions prepared according to the present invention are free of organic emulsifiers such as anionic, cationic and nonionic, surface-active agents. Instead, the water-dispersible silicone wax of this invention performs the function of holding together and compatibilizing the two otherwise immiscible phases. This is another distinct advantage and benefit of our emulsions when applied to consumer goods, since the presence of an organic emulsifying agent in a personal care product can often be responsible for potential skin irritation. The following examples are set forth for the purpose of illustrating the invention in greater detail. Example I A mixture of 15.7 grams of a linear polymethylsiloxane having a molecular weight of about 3600 and containing 0.25 equivalent of Si-H; 4.22 grams (0.008 mole) of a C 30+ olefin fraction; and 0.02 gram (1 ppm Pt) of an one percent solution of H 2 PtCl 6 in isopropanol was heated to 95°C. The mixture exothermed to 106°C. After five minutes, 86.15 grams (0.16 mole) of a C 30+ olefin fraction were added over a period of forty-five minutes, the addition being accompanied by heating at 110-120°C. Nine grams of isostearyl alcohol were added to the mixture as a compatibilizer; this was followed by the addition of 11.67 grams (0.012 mole) of an allyl-initiated polyetylene glycol having a molecular weight of 938 and the formula: H 2 C=CH-CH 2 -O-(CH 2 CH 2 O) 20 H, and of 0.10 gram (4 ppm Pt) of an one percent solution of H 2 PtCl 6 in isopropanol. The temperature was raised to 130°C and the mixture was heated for thirty minutes. The final step in the synthesis was the addition of 27.63 grams (0.07 mole) of a C 30+ olefin fraction followed by heating at 130°C for one hour. Upon cooling, a product was recovered which was a white wax having a softening point of 72-75°C. Reheating of the product above its softening point produced a clear highly viscous fluid. Residual Si-H in the product was analysed to be 130 ppm. Example II A water-in-oil emulsion was prepared as follows. First, an oil phase was formed by combining nineteen percent by weight of mineral oil, six percent by weight of sunflower oil and two percent by weight of the white wax product from Example I. The mineral oil, sunflower oil and the white wax product fromExample I were mixed together and heated to 75°C to melt the wax. A water phase was then formed with seventy-two percent by weight of deionized water containing one percent by weight of sodium chloride as a stabilizing agent for the emulsion. The water phase was mixed and heated to 75°C. The water phase was added very slowly to the oil phase, and the two phases were mixed together to uniformity. The resulting mixture was then cooled to room temperature. The resulting product was a white, thick oil-in-water emulsion having a "fluffy" texture and a pH of 6.7. The viscosity of the emulsion was 190,000 mm 2 /s (centistokes) as determined with an RVT-D viscometer rotating at 2.5 rpm for sixty seconds. Example III The emulsion of Example II was evaluated and found to be an effective skin conditioner in the maintenance of skin smoothness and softness and in protecting the skin from dryness. When applied to the skin, the emulsion had a dry, smooth feel.

Claims: A water-in-oil emulsion comprising from 5 to 50 percent by weight of an organic oil; from 44 to 94.5 percent by weight of water; and from 0.5 to 5 percent by weight of a water-dispersible silicone wax, the water dispersible silicone wax being derived from the reaction of (i) an ≡SiH-containing siloxane having a formula selected from Me 3 SiO(MeHSiO) x SiMe 3 and Me 3 SiO(MeHSiO) x (Me 2 SiO) y SiMe 3 , in which Me is the methyl radical and x and y are integers, the value of the integer x being from twenty to one hundred and the value of the integer y being from one to one hundred, with the proviso that the ratio of x/y is at least two to one or above; (ii) a linear C 30+ organic alpha-olefin; and (iii) an unsaturated ethylene oxide polymer having the formula: H 2 C=CH-CH 2 -O(CH 2 CH 2 O) z H, in which z has a value of at least sixteen, the emulsion being free of organic emulsifying agents. An emulsion according to claim 1, in which the emulsion has a viscosity in excess of 100,000 mm 2 /s (centistokes). An emulsion according to claim 1 or claim 2, in which the emulsion has a viscosity in the range of from 150,000 to 200,000 mm 2 /s (centistokes). An emulsion according to any of claims 1 to 3, in which the organic oil is present in the form of a mixture of two different organic oils. An emulsion according to any of claims 1 to 4, in which the emulsion includes up to one percent by weight of an emulsion stabilizer in the form of an electrolyte selected from sodium chloride and ammonium chloride. A method of softening skin comprising applying to the skin a water-in-oil emulsion according to claim 1 which includes 5 to 50 percent by weight of an organic oil; 44 to 94.5 percent by weight of water; and 0.5 to 5 percent by weight of a water-dispersible silicone wax. A method according to claim 6, in which the organic oil is present in the form of a mixture of two different organic oils. A method according to claim 6 or claim 7, in which the emulsion includes up to one percent by weight of an emulsion stabilizer in the form of an electrolyte selected from sodium chloride and ammonium chloride.

Inventors: GLOVER DAVID ALLAN, LEGROW GARY EDWARD, GLOVER, DAVID ALLAN,, LEGROW, GARY EDWARD
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1995
Main classification: A61K7
IPC codes: A61K8, C08J3, C08L83, A61Q19, C08G77