Process for the production of reinforced slabs of stone material

Abstract: In the manufacture of slabs of stone material such as marble or granite, reinforced with reinforcing elements in particular made of steel and fixed to the rear surface of the slabs by a bonding resin of the hardening type, the resin is used to impregnate non-twisted strands of glass, preferably in the form of matting, in a percentage weight ratio of glass strands to resin of at least 50:50, with preference for a quantity by weight of glass strands greater than 50%.

Description: The present invention relates to improvements to materials for covering floors and lining the external and internal parts of buildings, in particular based on natural stones such as marble and granite. The use of these natural-stone materials for the abovementioned purposes is so well-known that no further comment is required. However, some problems and drawbacks, mainly linked to specific applications, have been and are partly still associated with their use. Firstly the thickness of the slabs obtained from processing of the blocks produced by quarry-mining has hitherto been limited, in the sense that it cannot be reduced to values of less then 10 mm, owing to the fact that slabs of a smaller thickness are unable to withstand the subsequent machining operations, such as sizing, smoothing, polishing, chamfering, etc. Secondly, natural stones usually do not possess homogeneous physical properties, in particular as regards their impact strength and flexural strength. Obviously these drawbacks create even more problems as regards the manufacture and use of stone products of limited thickness (namely, products in the form of slabs, tiles, etc.). Consequently, hitherto for most applications, the products have been of a considerable thickness if not more, resulting in problems associated with their weight and hence difficulties of transportation, handling and laying. Furthermore, in the case of large-size panels intended for the external facades of buildings, any breakage, due for example to gusts of wind, seismic tremors or even localized knocks, causes the detachment of fragments of a not insignificant size with the obvious dangers. In recent years much research has been carried out into the manufacture of thin products made of natural stone, in particular marble or granite, which do not have the aforementioned drawbacks and problems. In this connection, a very important part was also played by the increasingly widespread use of so-called suspended floors, namely floors supported at a certain height from the concrete layer forming the natural floor, so as to form an easily accessible cavity housing all the components of internal installations for the electricity supply, telephone connections and air-conditioning. This solution has proved to be particularly advantageous for commercial buildings and offices. Furthermore, a specific goal, on which the efforts of research technology have concentrated, but which hitherto has never been achieved, has been that of providing products made of natural stone material with a thickness comparable to that of ceramic products, so as to allow the replacement of ceramic with granite or marble even where the flooring is replaced, without the need for onerous adaptation work (such as dismantling of part of the thickness of the concrete support layer, trimming of the bottom edges of the doors, etc.). In the solutions proposed and tried hitherto it has been attempted to reinforce thin slabs of natural-stone material by applying to their rear face (namely the surface intended to remain out of sight) reinforcing elements, in the form of metal or glass-fibre or plastic grids, which are fixed to the aforementioned rear surface of the slab by means of a synthetic resin, for example epoxy or polyester resin. In Italian Patent Application No. TV2A000041 filed on 23 March 1992 in the name of the same Applicant a solution of this kind is proposed, by forming in the rear face of the slab of natural-stone material a regular grid formed by grooves or recesses having a depth less than the thickness of the starting slab and by anchoring therein a preferably metal reticular element by means of a binder, also preferably consisting of a synthetic resin, which fills the cavities and envelops the metal elements forming the grid. In turn, according to a subsequent patent application again in the name of the same Applicant (No. PD93A000099, filed on 6 May 1993), the rear face of the slabs have embedded in recesses, preferably framing the slabs or the tiles which will be formed from the latter, a reinforcing element consisting of synthetic resin, so as to define in the edges of each slab or tile a thickness of plastic material applied so as to reinforce the tile or slab precisely in the region of the parts which are most likely to be subject to deterioration or damage during subsequent machining operations. Furthermore, these inserts of plastic material also have the property of favouring cutting of the slabs into tiles or slabs of smaller dimensions with rational use of the initial slab area available. Finally, Patent Application No. M193A001462 of 6 July 1993 describes a process for manufacturing thin slabs of stone material reinforced on the rear face by means of a metal reticular element, for example a meshwork made of stretched metal or steel sheet, fixed to the aforementioned rear face by means of a bonding resin such as an epoxy resin. The tests carried out hitherto have shown, however, that the thin slabs obtained using the aforementioned technologies, while being satisfactory from the point of view of the desired mechanical strength together with the primary objective of a limited thickness, still have a drawback arising from the difference in the thermal expansion coefficient between the stone material and the resin used as a bonding agent. This is obviously a drawback which was not foreseen since it was difficult to imagine that a slab of granite could become warped on account of the difference in thermal expansion between the granite itself and the layer of resin adhering to its rear face. It has now been discovered, this discovery representing the main aspect of the present invention, that the aforementioned problem is totally eliminated by using a process for the production of reinforced slabs of stone material, wherein the rear face is reinforced by applying a reinforcing layer comprising a resin of a hardenable type and reinforcing material in the form of linear elements, characterized in that said reinforcing material consists of a plurality of fibers selected from the group of glass and carbon fibers, wherein said fibers are in the form of non-twisted stands impregnated with said hardenable resin with a percentage ratio of non-twisted strands to resin of at least 50:50. In the preferred embodiment of the present invention the glass-fibre strands are used in the form of matting. In the applications of the present invention two main situations are contemplated, namely: a) Production of reinforced thin slabs, with a thickness of less than 10 mm and preferably equivalent to 6-8 mm, in which the matting of non-twisted glass strands is impregnated with the bonding resin and applied to the rear face of the natural-stone slab, followed by hardening of the resin, for example by the action of a catalyst and/or heat. When a particularly marked reinforcing effect is required, instead of a single mat of glass strands two or more mats may be used, each impregnated with the bonding resin.It is moreover possible and envisaged to insert between the impregnated glass-strand matting and the rear face of the slab of stone material a separate reinforcing layer, for example consisting of steel in the form of a meshwork or stretched metal sheet, operating in the manner described in the already mentioned Italian Patent Application No. MI93A001462.In addition the bonding resin may be used to fix to the rear face of the slab of stone material a layer of fire-resistant or noise-insulating material, as envisaged in the last mentioned patent application. b) Production of slabs of stone material for use outside of buildings, both as flooring and as wall lining materials. In this case the solution illustrated and described in the aforementioned Italian Patent Application No. TV92A000041 is modified in the sense that, in addition to the conventional reinforcement consisting of linear elements or of a grid made of metal, in particular steel, in the grooves formed in the rear face of the slab of stone material, use is made of non-twisted strands of glass-fibre which are impregnated with the bonding resin in the proportions indicated above, preferably so as to envelop the linear metal reinforcing elements, anchoring them inside the grooves themselves. In this case the resin used to envelop the linear metal reinforcing elements may contain a mineral filler with a low thermal expansion coefficient, such as silica, for example, in a quantity of up to 70% by weight with respect to the resin. Alternatively, instead of the linear metal reinforcing members seated within the grooves and forming a grid use can be made of laid down glass fiber yarns, consisting of four 4800 TEX (19.6 g/m) threads laid down within the groove having 3 to 4 mm. deepress; the glass/resin ratio remains unchanged and the linear dilatation coefficent of this material is of 8 to 9 x 10 -6 , whereby it is consistent with the stone material. Another possible alternative is represented by circular cross-section reinforcing elements (rods) of extended fiber of glass and resin (68% glass, 32% resin by weight) of a diameter of 2 - 2,5 mm. with a linear dilatation coefficent of 7,5 x 10 -6 . These rods can be substituted for by bars having rectangular cross section. In the preferred embodiment of the invention, in both cases the percentage of resin used with respect to the non-twisted strands of glass, both as matting and as bundles of strands, is equivalent to 33% by weight with respect to the weight of glass strands; in the case of a thin slab reinforced with two mats there will be 1600 g/m2 of glass-strand component and 800 grammes per square metre of resin. Among the resins which can be used in the present invention, epoxy resins of the type bisphenol A or bisphenol A/C are preferred, while as a hardener a polyamine or polyamide compound of the well-known type is used. As a result of experimental tests performed in the laboratory on thin slabs of granite reinforced with two mats of non-twisted glass strands impregnated with 33% by weight of epoxy resin, it has been possible to ascertain firstly that the linear expansion coefficient of the mat + resin combination is between 15 and 30 x 10 -6 per °C, i.e. very close to that of granite. The mechanical characteristics of the slabs thus obtained also proved to be excellent, as can be seen from the following table which shows the corresponding values for non-reinforced granite: Granite slab (thickness 8 mm) Granite slab reinforced with 2 mats (thickness 8mm) Flexural strength 14,7 MPa (150 kg/cm2) 191,1 MPa (1950 kg/cm2) Impact strength (1 kg sphere) material breaks when H=20 cm When H = 60-90 cm: imprint remains but material does not break When H < 60 cm: no effect, with no cracks or imprints Concentrated loading test with 25x25 mm punch With P=150 kg and camber = 2.5 mm, tile breaks With P=600 kg and camber = 7 mm, granite disintegrates, but backing remains attached In the description above reference has been made to the impregnation of non-twisted glass strands, preferably in the form of matting, but it is obvious that this must not be regarded as limiting since other materials may be used with similar results, such as, for example, carbon fibres. Likewise, instead of preliminary impregnation of the glass strands, it is possible to carry out a process consisting in arranging the layer or mat of glass strands and then casting the resin so as to coat and impregnate the glass strands. For further details regarding the process for manufacturing reinforced slabs which are both thin and have grooves containing the metal reinforcing elements, either linear or in the form of a meshwork, reference should be made to the Italian patent applications indicated above.

Claims: Process for the production of reinforced slabs of stone material, wherein the rear face is reinforced by applying a reinforcing layer comprising a resin of a hardenable type and reinforcing material in the form of linear elements, characterized in that said reinforcing material consists of a plurality of fibers selected from the group of glass and carbon fibers, wherein said fibers are in the form of non-twisted strands impregnated with said hardenable resin with a percentage ratio of non-twisted strands to resin of at least 50:50. Process according to claim 1, characterized in that said non-twisted strands are in form of a matting. Process according to claim 1, characterized in that the amount of non twisted strands is prevailing in comparison with that of the hardenable resin. Process according to claim 1, characterized in that the percentage weight ratio of resin to non twisted strand is 33:66. Process according to claim 1, characterized in that said slabs of stone material have a thickness not greater than 10 mm. Process according to claim 5, characterized in that said slabs of stone material have a thickness of 6-8 mm. Process according to claim 1, characterized in that linear metal reinforcing elements are inserted between said reinforcing layer and the rear face of the slabs. Process according to claim 7, characterized in that said metal is steel. Process according to claim 7, characterized in that said linear metal reinforcing elements are housed in grooves or recesses formed in the said rear face of the slab. Process according to claim 9, characterized in that said grooves or recesses form a grid. Process according to claim 9, characterized in that between said reinforcement and the rear face of the slab linear reinforcing elements are inserted consisting of laid down glass fiber yarns, seated within the grooves. Process according to claim 11, characterized in that said linear reinforcing elements consists of rods or bars of glass and resin. Process according to claim 12, characterized in that said linear rods or bars have a diameter of 2 to 2.5 mm. Process according to claim 12, characterized in that said rods or bars consists of 68% glass and 32% resin, the percentages being expressed by weight. Reinforced slab of stone material having a reinforcement layer applied to the rear surface thereof comprising a resin of the hardenable type and reinforcing material in the form of linear elements characterized in that said reinforcing material consists of a plurality of fibers selected from the group of glass and carbon fibers, wherein said fibers are in the form of non-twisted strands impregnated with said hardenable resin with a percentage ratio of non-twisted strands to resin of at least 50:50.

Inventors: TONCELLI MARCELLO, TONCELLI, MARCELLO
Applicants: TONCELLI MARCELLO, TONCELLI, MARCELLO
Application year: 1995
Main classification: B32B9
IPC codes: E04C2, B32B9, B29C67, E01C5