IMPROVEMENTS IN METALLURGICAL CONVERSION

Abstract: The proposed improvements in metallurgical conversion according to the invention involve the production of a semi-finished product (a mixed blank) in the form of an ingot through casting in a mould of a casting facility from a solid filler, preferably an oxidizer, and liquid pig iron which is subsequently cooled. Action is taken during the process to prevent the solid filler in the liquid pig iron from flaring. This is done both by the application of a mechanical force which can be created by, for example, a cantilever (8) with a hollow roller (9) which acts on the mould (2), and a weighting unit (10), and by the selection of suitable relative dimensions of the solid filler pieces and of the pouring rate. The optimal conditions are disclosed for the use of the semi-finished article in metallurgical conversions in oxygen converters and electric arc furnaces.

Description: FIELD OF THE INVENTION The present invention relates to the field of ferrous metallurgy, more particularly to metal casting, namely to the casting of foundry pigs (that is to say metal casts intended for subsequent remelting), specifically to the manufacture of prepared blend materials for the steel-smelting production and also to machines for the casting of pigs primarily from pig iron with fillers. The present invention relates also to processing of metal (melt) in a liquid or viscous state in casting molds and namely in molding boxes of casting machines using the pressure, specifically using mechanical devices. More particularly, the present invention relates to processing of pig iron for the production of iron and steel effected both in converters and in electric furnaces, for example are furnaces. BACKGROUND OF THE INVENTION When performing metallurgical conversion, that is to say while converting pig iron into steel, including the addition of a scrap metal, by various known processes such as the open-hearth, the converter, the electro-smelting processes, a blend, that is to say, a mixture of materials necessary to provide a predetermined chemical composition of metal and slag obtained, is also charged into a corresponding melting furnace apart from pig iron and a scrap metal. As a rule, the blend includes primarily oxidizing agents needed for a chemical coupling and for removing from a bath the carbon and other unwanted ingredients of the melt, such as sulfur, phosphorus, manganese and the like. An important stage in the preparation of the blend resides in forming thereof, that is to say imparting a shape convenient both for transporting and storing and for charging into a corresponding melting furnace. Thus, granulation, agglomeration and briquetting of dispersed ingredients with the addition of binders have been widely used heretofore (M.A. Nechiporenko, "Pelletizing Fine Concentrates", Leningrad, 1958; L.A. Lurie, "Briquetting in Metallurgy", Moscow, The State Scientific and Technical Institute for Ferrous and Non-Ferrous Metallurgy, 1968; B.M. Ravig, "Briquetting Ores and Ore-Fuel Blends", Moscow, Nedra, 1968). In a number of cases, it is convenient to form the blend (the charge stock) in the form of pigs from iron-carbon alloys, as a rule from pig iron with the addition thereto of fillers of a required composition, in particular of iron-ore pellets (USSR Inventors' Certificate No. 985063) or ore-carbon pellets (USSR Inventors' Certificate No. 1250582 of August 15, 1986; Bulletin of Inventions No. 30, 1986) which in fact represent a semifinished item for metallurgical conversion. Such pigs are prepared in molding boxes of a casting machine filled with pellets from corresponding feeders and cast with pig iron. Here, cooling of a liquid pig iron is carried out at the expense of heating pellets, reducing oxides and heating a mould working surface being exposed to a pig (USSR Inventors' Certificate No. 1105273, which seems to be the closest prior art). Charging of various melting furnaces with such a stock, i.e. with pigs, appears to be extremely convenient and technologically effective. At the same time, there is a problem of achieving stability of a composition of a given semifinished item for metallurgical conversion, which is especially actual for low-volume smeltings, as well as for the preparation of section steels, in particular in oxygen converters and are furnaces, since the use of half-finished articles with unstable composition and thermal properties does not favour stability of steel-smelting procedures and techniques. GB-A-1458228 teaches a pig for manufacture of cast iron and in particular a moulded pig consisting of pig iron and, incorporated within the pig iron, other charge material for the production of cast iron. US patent no. 3,807,986 teaches a combination iron and iron oxide briquette and method of using. In particular, the invention relates to certain changes in the steel making process in electric arc furnaces and more particularly refers to the use of a material which is made from particulate metallic iron and from iron oxide. SUMMARY OF THE PRESENT INVENTION It is, therefore, the principle object of the present invention to create a process for the preparation of a semifinished item for metallurgical conversion in the form of pigs formed in a molding box of a casting machine from a solid filler and a liquid iron-carbon alloy followed by cooling, which provides for stability of a composition of ingredients. It is another object of the present invention to create a casting machine for the preparation of a semifinished item for metallurgical conversion of a relatively stable composition. The above and other objects are accomplished according to the present invention in the preparation of a semifinished item for metallurgical conversion by forming thereof in a molding box of a casting machine from a solid filler and a liquid iron-carbon alloy followed by cooling in the form of a pig, provided the solid filler and a liquid iron-carbon alloy undergo, in the process of forming, an action which prevents the floating up of the solid filler in a liquid iron-carbon alloy. Such an action is required to achieve the aim of the present invention, since it has been discovered that heterogeneity of a composition of pigs obtained was associated with the fact that due to a difference in densities of the solid filler and the liquid iron-carbon alloy, the floating of the filler and its removal from a molding box occured in the process of pouring the filler with the alloy, wherein a low viscosity of said alloy in a hot state was insufficient to prevent this fact. In the case of pouring the filler with a solidifying alloy (according to an increased viscosity), the alloy was not able to fill in all the gaps between the filler pieces and, accordingly, it failed to bind the filler which led to the falling down of a part of the filler when discharging the pig from the molding box. In both cases, this resulted in an uncontrolled change of a composition of a semifinished item for metallurgical conversion. In the preparation of a semifinished item without the aforementioned action, the solid filler in the bulk of a molding box (a pig) is not uniformly distributed due to a difference between the apparent densities of iron-carbon alloy (for example, pig iron density is 7 g/cub. cm) and a filler (for example, a density is 3.7 g/cub. cm as to pellets). An upper part of the pig contains a very low proportion of iron-carbon alloy and a great deal of the filler; on the other hand, a lower part of the pig is almost wholly composed of iron-carbon alloy and contains little or no filler. In the upper part of the pig, particles of the filler are very weakly bonded by iron-carbon alloy and, when the pig falls down from the casting machine onto a flat-car, particles of the filler separate out from the pig thereby forming a mound which is nonmagnetic and not subjected to loading along with the pigs, when shipping to a consumer. As a result, the pigs contain an insufficient amount of the solid filler in comparison with an estimated one. This results, for example in that during a subsequent conversion, for example in an are furnace, an oxidizing period of steel smelting increases by 10 - 15 percent for the lack of oxygen introduced by pellets to oxidize pig iron admixtures. In practice, pig iron is used in most cases, however this fact should not be considered as a restriction of common conditions of the present invention. Within the scope of this text, the term "a solid filler" denotes any filler required to provide a predetermined chemical composition of metal obtained; among them and first of all, these may be solid oxidizing agents being a source of oxygen for a chemical bonding and removing carbon and other unwanted ingredients of the melt. In a preferred embodiment of the present invention, it is advisable that solid oxidizing agents be taken with a total amount of oxygen needed for the oxidation of 5 to 95 percent carbon and a total estimated oxidation of the remaining ingredients of iron-carbon alloy which possess an affinity to oxygen to a greater extent than carbon does. With the aforementioned total amount of oxygen when carrying out a subsequent conversion, one may simultaneously obtain a required degree of oxygen removal, an increased rate of metal dephosphorization and a sufficient slag frothing at the expanse of carbon oxide bubbles released by the reaction of carbon oxidation, which affords a slag protective effect, in particular in electric furnaces, that is to say are screening by the slag. If a total oxygen content is less than the amount needed for the oxidation of 5 percent carbon and for a total oxidation of other metal admixtures, then the reactions of carbon and phosphorus oxidation proceed with difficulty. In this case, metal has an elevated phosphorus and carbon content. If a total oxygen content is in excess of the amount needed for the oxidation of 95 percent carbon and for a total oxidation of other elements, then the carbon content in a bath is unduly low and, on the contrary, the oxygen content is high, which is undesirable both for the reasons of conditions of a furnace output, a flow rate of deoxidizers, metal quality and for the reasons of a range of steel grades produced. In accordance with another preferred feature of the invention, a solid filler and iron-carbon alloy are subjected, in the process of forming to the action of force preventing the floating up of said solid filler in a liquid iron-carbon alloy, which action is effected mechanically, that is to say by distributing a force the magnitude of which in the direction perpendicular to the surface exceeds a maximum buoyant force acting upon said solid filler in said liquid iron-carbon alloy. Here, it is possible to form a semifinished item by casting a molding box with a liquid iron-carbon alloy, charging its surface with a solid filler and immersing said solid filler into a liquid phase under the action of a force the magnitude of which exceeds, in the optimal variant, by not less than 5 percent a maximum buoyant force acting upon said solid filler in iron-carbon alloy. According to Archimedes law, any body completely or partially submerged in a fluid (gas or liquid) at rest is acted upon by an upward, or buoyant, force the magnitude of which is equal to the weight of the fluid displaced by the body, which force is applied in the centre of gravity of the bulk of a body's submerged part. Accordingly, in order to immerse pellets and uniformly distribute thereof in the bulk of iron-carbon alloy (pig iron) prepoured into the molding box, it is necessary that the solid filler (pellets) be subjected to the action of a force exceeding the buoyant force. An excess rating (5 percent and more) has been determined experimentally. As a conveyer with molding boxes moves to a discharging end of the machine, a hard scum of pig iron becoming quickly solidified by all the mass of a semifinished item firmly keeps pellets in the bulk of pig iron. When approaching the discharging end, a mass of the semifinished item constitutes a strong unit composed of pellets firmly set by an already solidified pig iron. When a piece of such semifinished item comes against a flat-car bottom with a blow, the pellets do not run out therefrom but firmly hold out in a mass of the piece by means of a solid pig iron, since still at the stage of solidification the pellets were completely submerged in a mass of pig iron which at one stroke became solidified on a cold pellet surface. Solidification of pig iron in the semifinished item is accelerated by supplying water at an immersion device and also at a cooling zone directly toward a foundry pig present in the molding box. In this way, it is possible to form the semifinished item by charging a molding box with the solid filler, casting thereof with a liquid iron-carbon alloy and applying to a floating up filler a force the magnitude of which, in an optimal variant, is equal to 100 - 10,000 N/sq. m. In the latter case, depending on temperature and, hence, viscosity of iron-carbon alloy, it is advisable to apply said force in 1 - 60 seconds after the solid filler has been cast with a liquid iron-carbon alloy. An additional force exerted on the material in a molding box is necessary to immerse (drown) a floating up (because of a difference in densities of the filler and pig iron) material to a bottom part of the molding box, which provides a uniform distribution of the filler in the bulk of the foundry pig. The value of that force is determined by a depth of a material submerence in the molding box and by a weight of pig iron "squeezed-out" as a result of this, wherein said weight is referred to the surface of applying a force. For example, a material (pellets) is required to be submerged for a depth of 3 cm of the molding box. The area of applying a force, that is to say a lateral face of a roller cylindrical surface coming into contact with a heterogeneous system (pellets, pig iron) of the foundry pig, will be equal to 10 x 50 = 500 sq. m, where 10 cm - the length of the roller are coming into contact with a material in the molding box; 50 cm - the roller length. Pig iron density is 7 g/cub. cm. Pig iron volume squeezed-out by a force will be equal to 500 x 3 = 1500 cub. cm = 10.5 Kg = 105 N. Specific pressure will be equal to 105 : 500 = 0.20 N/sq. cm, or 2000 N/sq. m. The actual pressure must be over by a force directed to deform a metal scum formed. In cases where pig iron with an increased viscosity (pig iron having a temperature close to solidification) is used, it will take much more force to drown (immerse) the material in the molding box than it is required according to estimated values - up to 10,000 N/sq. m. If the value of a force acting on a material in the molding box is less than 100 N/sq. m, the effect of submergence of a solid oxidizing agent, that is to say pellets, will be negligible and the pellets will not be distributed uniformly in the pig bulk (pellets will be practically absent in the bottom part of the molding box). With the value of a force over 10,000 N/sq. m the mechanism of pellet submergence is complicated, overall dimensions of its units are enlarged, unfavourable conditions effect the machine on the whole, which complicates operation thereof. A time period from the moment of casting pig iron and the onset of applying a force for submersion (drowning) of a material in the molding box basically depends on the temperature of pig iron cast in the molding boxes. If the temperature of pig iron varies over the ranges close to solidification (1,200 - 1,260 °C) then, in order to drown a material in the molding box, one should apply a force practically immediately on termination of the casting process, i.e. in one second. After pig iron has become solidified in the molding box it is practically impossible to load a material thereto. If pig iron is cast being physically hot, a time period for applying a force to drown (immerse) the material deep in the molding box may be equal to one minute following termination of the pig casting. To change a time of applying a force in an effort to immerse (drown) it in the molding box, a pressing device (a roller with a cantilever and a weight) may be displaced, as the need arises, approaching or moving away from the place of casting pig iron in the molding boxes. To apply a force to the surface of a material in the molding box after expiration of one minute from the moment of termination of the molding box casting is not to the purpose, since this results in solidification of pig iron in the upper part of the foundry pig. In accordance with another embodiment of the present invention, an action, in the process of forming, on the solid filler and a liquid iron-carbon alloy which prevents the floating up of said solid filler in said liquid iron-carbon alloy, may be provided by using pieces having the size of 0.025 to 0.300 of the molding box height, and casting thereof with iron-carbon alloy in the ratio, of its average linear velocity to the linear velocity of the molding box movement equal to from 3 : 10 to 6 : 10. It seems that the last-mentioned parameter needs to be explained in more detail. It should be understood that "an average linear velocity" of iron-carbon alloy means a volume content of a liquid iron-carbon alloy entered into the molding box per unit of time (in a user-oriented literature, this value is called as a (volume) flow rate) reffered to a cross-section of the molding box. This ratio (cub. m/s : sq. m = m/s) having the dimension of velocity characterizes an average linear velocity of iron-carbon alloy movement along a cross-section of the molding box, since a cross-section of an iron-carbon flow itself is unknown and is difficult to be determined. This value is not a real speed of iron-carbon flow but represents a nominal velocity averaged by along a cross-section of the molding box while retaining a physical meaning of exactly a linear velocity of iron-carbon alloy movement. Casting of a liquid iron-carbon alloy into the molding boxes with the aforementioned ratio of linear velocities of iron-carbon alloy supply and molding box movement equal to from 3 : 10 to 6 : 10 provides for a uniform filtration of iron-carbon alloy in the bulk of the molding box filled with particles of a solid filler. At the same time, one may rule out a phenomenon of pouring-over of iron-carbon alloy into neighboring molding boxes which is caused by excess of the alloy casting speed over the speed of molding box movement, that is to say filling of spaces between particles of the solid filler. One may also rule out a local, nonuniform and incomplete filling of the molding boxes with iron-carbon alloy as well as solidification of iron-carbon alloy batches in the spaces between particles of the solid filler originating as a result of an insufficient feed rate of iron-carbon alloy into molding boxes, its fast cooling and solidification. The ratio of linear velocities of movement (casting) of iron-carbon alloy and molding boxes equal to from 3 : 10 to 6 : 10 is in compliance with the conditions for the preparation of moldings of blend materials with a stable ratio of iron-carbon alloy and a solid filler. It has been discovered that if this ratio exceeds 6 : 10, then iron-carbon alloy has not enough time to fill all spaces between particles of the solid filler of an ore material with the result that a phenomenon of misrun of a molding box with iron-carbon alloy occurs. A part of the solid filler shall not be poured with iron-carbon alloy and shall pour out of the molding box, mass relation between iron-carbon alloy and the solid filler shall be violated as in the case of violation of the conditions for constancy of the molding composition. If the ratio of linear velocities is less than 3 : 10, then a blend material molding is overflowed with iron-carbon alloy, the latter pours over into neighboring molding boxes, which also results in violation of the conditions for constancy of the molding composition. It has also been discovered that the size of particles constituting a layer of the solid filler equal to from 0.025 to 0.300 to the molding box height is an optimal one for keeping a solid filler particle layer immovable in the molding box when the latter is poured (provided the aforementioned limitations on velocity are observed). If a particle size of iron-ore materials is less than 0.025 of the molding box height, then pouring of the molding box with pig iron is complicated, uniformity of mixing pig iron with an iron-ore material is infringed, stability of the pig iron - iron-ore material relationship is disordered, an increased dust escape of fine particles of an ironore material is observed, and foundry pigs noticeably differ by composition. If a particle size of an iron-ore material is more than 0.30 of the molding box height, then an upper particle layer, especially one disposed at the top of the molding box, is sluiced off by pig iron. This leads to the nonuniformity of distribution of an iron-ore material in the bulk of the molding box and to the violation of homogeneity of the composition thereof. The above and other objects are also accomplished in accordance with the present invention by providing a casting machine for the preparation of a semifinished item for metallurgical conversion comprising a frame adapted to assemble thereon units of the casting machine, a conveyer with molding boxes assembled on the frame, a pouring device to pour a liquid iron-carbon alloy into the molding boxes and a bin with a feeder to charge a solid filler into the molding boxes. This casting machine also comprises a device adapted to apply an action to said solid filler and liquid iron-carbon alloy, which action prevents the floating up of the solid filler in the liquid iron-carbon alloy. In a preferred embodiment, it is advisable that said machine be provided with atomizers connected to a pipe-line for supplying a cooling medium, said device for applying to said solid filler and liquid iron-carbon alloy an action preventing the floating up of the solid filler in the liquid iron-carbon alloy be made in the form of a cantilever with a hollow roller and a weighting material mounted on the cantilever with the possibility to move along its longitudinal axis, wherein said cantilever with its one end is mounted in supports on the frame and with another end, by means of a pivotably installed roller, rests on a molding box, the length of said hollow roller is from 0.80 to 0.95 of a working length of the molding box, an outside diameter of said roller is from 1.1 to 1.4 of the molding box width, the atomizers are located in the vinicity of said roller and oriented to its lateral face. The ratio of dimensions of the roller and the molding box is of a great significance to solve a problem formulated, i.e. to produce a uniform, heterogeneous system, that is to say, to uniformly distribute an oxidizing agent in the bulk of a pig iron matrix. If the lengh of the roller is less than 0.80 of a working lengh of the molding box, then the roller will bring pressure to bear upon the molding box walls and the process for immersing a material into a liquid pig iron will not be attained. Said ratios of an outside diameter of the roller and the molding box width have been determined experimentally when pouring metal into the molding boxes of different capacity. Moreover, if an outside diameter of the roller is less than 1.1 of the molding box width, a blend material and pig iron may be squeezed out of the molding box. If an outside diameter of the roller is more than 1.4 of the molding box width, this results in that the roller will start pressing the molding box walls, and a uniform, heterogeneous system will be absent in a lower part of the foundry pig. BRIEF DESCRIPTION OF THE DRAWING The present invention is explained in more detail herein-below with reference to the drawing which is a fragmented schematic illustration of one embodiment of a casting machine for metallurgical conversion in accordance with the present invention. BEST MODES FOR CARRYING OUT THE INVENTION A casting machine comprises chain conveyers 1 with molding boxes 2 fixed thereon, a pouring device 3, a frame 4, a bin 5 with a feeder to supply solid fillers, a pipe-line 6 for supplying a cooling medium being connected to atomizers 7, a cantilever 8 with a hollow roller 9 and a weighting material 10 mounted on the cantilever with the possibility to move along its longitudinal axis. The cantilever with its one end is hinged in supports on the frame and with another end, by means of a pivotably installed roller, rests on a molding box. The casting machine operates as follows. A laddie with a liquid pig iron is fed to the casting machine while pellets are fed to the bin with the feeder. The feeder gates open up and the pellets get into ingot molds. A travel speed bears a directly proportional relationship to the pellet flow rate. Ingot molds filled with the pellets are conveyed and poured with pig iron. In 1 - 60 seconds after pig iron has been cast, a material in the molding box is subjected to an additional action of a force the magnitude of which is equal to 100 - 10,000 N/sq. m. A time interval from the moment of finishing the pig iron casting to the moment of applying said force is mentioned above as is an intensity of the force applied depending on the conditions of pouring. Example 1 Tests of the present method for the preparation a semifinished item were carried out on a pilot-plant casting machine in the variant of applying a mechanical force and a casting machine therefore using different intensities of said force on the surface of a material in a molding box and time periods for applying said force and in different ratios of a roller length to a working length of the molding box and an outside diameter of the roller to the molding box width. The results of these tests are presented in Table 1. Test Nos. Iron temperature, °C Force apply delay, sec. Force intensity, N/sq.m Roller diame-ter- Mold box width ratio Roler length - Mold box length ratio Pig weight, Kg Filler distribution uniformity in the pig, Numbers Priorart 1380 - - - - 27.5 1 1 1260 1 1000 1.4 0.80 26.0 4 2 1380 20 100 1.35 0.85 25.5 3 3 1300 50 10000 1.25 0.90 27.0 5 4 1400 60 7500 1.1 0.95 26.0 4 5 1280 70 9000 1.9 0.7 25.0 2 6 1360 30 10000 1.5 1.0 27.5 1 The analysis of tests performed has showed that the claimed method and casting machine therefore enable to prepare foundry pigs of a semifinished item for metallurgical conversion having a uniform, heterogeneous composition with a uniform distribution of pellets in the bulk of a pig (4 numbers according to a five-number evaluation system). Example 2 A method in accordance with the present invention was carried out on a casting machine, 35 m in length and 5.8 m in width, having two conveyers each comprising 292 molding boxes. The casting machine was equipped with a device for a measured loading of a lumpy iron-ore material into the molding boxes of both conveyers. Molds were prepared in the molding boxes having 12.5 m in height and 318 sq. cm in cross-section wherein their travel speed was equal to 10 cm/sec. As an iron-ore material, roasted oxidized iron-ore pellets and a sinter-cake with the size of pieces equal to from 0.3 to 3.8 cm, that is to say in the range of from 0.025 to 0.300 of the molding box height, were used. A pig ron casting rate referred to a molding box cross-section and to a conveyer travel speed was controlled in the range of (3- 6) : 10. It was noted that with the ratio of linear velocities of a pig iron casting and a molding box movement exceeding 6 : 10, pig iron had not enough time to fill all spaces between solid particles of an iron-ore material, and molds prepared were porous with a nonuniform distribution of pig iron in the bulk of the mold. A part of solid particles was not seized by pig iron and was poured out of the molding boxes, which resulted in the preparation of poor-quality molds. If the ratio of linear velocities was less than 3 : 10, then a blend material mold was overflowed with pig iron, the latter poured over into neighboring molding boxes, which resulted in violation of the conditions for constancy of the molding composition and in an increase of the mold weight. In the tests performed, more than 1,500 tons of a molded blend material for steel-making furnaces were produced. Molds were of 31 - 33 Kg each and contained 20 - 25 percent by weight of an iron-ore material, the rest being pig iron. A molded blend material produced was remelted into steel in 3-, 6-, and 100-ton electric furnaces and in a 65-ton open-hearth furnace. In all cases, a positive effect was produced: a melting time was reduced by 30 - 50 percent, a fuel consumption - by 14 - 25 percent, a refractory material consumption - by 1 - 2 Kg per ton of steel, steel net costs were cut in comparison with steel produced from a conventional blend: scrap and metallized pellets. Example 3 In metallurgical reservoirs for charging a converter, a scrap metal and a semifinished item comprising 20 percent of pellets and 80 percent of iron-carbon alloy (pig iron) were prepared. A solid blend for a 160-ton converter contained 25 tons of scrap and 12 tons of the semifinished item; a liquid pig iron was poured in the converter in the amount of 135 tons. A flow rate of slag-forming constituents was identical to that when using only scrap as a solid blend: lime, 12 tons; cand, 0.2 ton; ore pellets, 0.8 ton. Blowing a heat was carried out according to a conventional practice in line with operating instructions. Smelting proceeded smoothly, without any deviation from slag and thermal conditions and a required chemical composition. Steel produced was of C T 20 carbon steel grade. Following termination of the blow, deoxidizing agents were introduced into a liquid bath, the metal was tapped into a laddie which was transferred to a continuous casting machine. The yield of a liquid metal was at a level of conventional smeltings when performed using only scrap in a metal blend, and equaled to 87.4 percent. Pilot-plant smeltings using a semifinished item instead of a scrap metal as a quenching medium showed the effectiveness of said change, at the same time providing required slag and thermal conditions of smelting, the reduction of the copper content by 25 percent, the nickel content by 29 percent in comparison with smeltings when performed using only scrap as a solid blend. Example 4 Table 2 illustrates the effect of applying an action in the form of a mechanical load exceeding a buoyant force by 10 percent, on the stability of a composition of a semifinished item (a foundry pig) for metallurgical conversion and accordingly on smelting performance. Nos. Pellet content, % wt. Oxygen deficit as a result of pellet mound, Kg per 100 Kg semifinished item Oxidation period rise, Minutes in semifinished item mound Planed Actual without loading 1. 25 17 8 2.10 8 2. 25 15 10 2.60 10 3. 25 18 7 1.80 7 on load 4. 25 25.0 - - absent 5. 25 24.7 0.3 0.06 absent 6. 25 25.0 - - absent 7. 25 25.0 - - absent 8. 25 24.8 0.2 0.04 absent Example 5 Pilot-plant smeltings were performed in 100-ton are furnaces. Electric anisotropic steel was produced. Scrap (crop ends, defective slabs, amortization scrap) and a charge stock in various ratios therebetween were used in a metal blend composition. A blend comprising a charge stock and scrap was loaded in layers into a bucket and charged into a furnace. The charge was also furnished with lime, 1.5 - 4 tons; a sinter cake, 2 - 4 tons; and, during separate smeltings, with cand in the amount of 300 - 50 tons per each smelting. After melting a charge stock, a bucket was added with a charge stock above scrap. Steel making was performed using a crown tuyere for oxygen lancing. In the process of melting, a sinter cake and cand were added, if required. To produce a charge stock, conversion pig iron and iron-ore pellets were used in a (81 - 84) : (19 - 16) ratio therebetween. On melting of the blend in sample 1, the metal with the following chemical composition (on a weight percentage basis) was produced: C = 0.18 - 1.00; Mn = 0.10 - 0.20; P = 0.009 - 0.016; S = 0.005 - 0.027; Cr = 0.03 - 0.09; Ni = 0.05 - 0.09; Cu = 0.05 - 0.13. After refining and preliminary deoxidizing, the metal was tapped into a laddle. Technical-and-economic performance of electro-smelting of electric steel produced in accordance with the present method are presented in Table 3 in comparison with smeltings of the current manufacture (on the average with respect to 20 smeltings). Nos Number of batches. Charge stock content(% by weight of furnace burden Charge stockmetal scrap ratio (in parts) Power con sump-tion per each smelting (kilowatt-hour) Smelt duration (hour,min) Comparative 1 50 1:1.0 51838 3-08 1 2 2 1:30 51120 3-02 2 2 3 1:20 49800 2-55 3 2 10 1:5.4 48240 2-53 4 2 20 1:0.8 47100 2-49 5 2 30 1:0.2 46800 2-45 6 2 32 1:0.1 47460 2-51 7 2 34 1:0.007 49830 2-57 As one can see from the Table, the proposed method for steel-making in an are furnace provides for improvement of technical-and-economic performance of smelting at the expense of reducing a duration of the melting period by 7 - 12 percent, and a specific power consumption by 4 - 10 percent. It is to be understood that the invention is not limited to the illustrations described and shown herein, which are deemed to be merely illustrative of the best modes of carrying out the invention, and which are susceptible of modification of form, size, arrangement of parts and details of operation. The invention rather is intended to encompass all such modifications which are within the scope as defined by the attached claims. It is also to be understood that the semi-finished product itself and its use in a steelmaking process represents background art which is useful for understanding the invention .

Claims: A process for the preparation of a semi-finished metallurgical product for use in metallurgical melting processes, the semi-finished product comprising a liquid iron-carbon alloy and a solid filler of lesser density than the iron-carbon alloy, the process comprising forming of said product in a molding box of a casting machine from a solid filler and a liquid iron-carbon alloy followed by cooling, characterized in that in the process of forming the semi-finished product said solid filler and iron-carbon alloy are subjected to the action of a distributed mechanical force of a magnitude which in a direction perpendicular to an upper surface of the liquid iron-carbon alloy is at least equal to a maximum buoyant force acting upon said solid filler in said liquid iron-carbon alloy, whereby floating of the solid filler in said liquid iron-carbon alloy is prevented. A process according to Claim 1, characterized in that forming of said semi-finished metallurgical product is carried out by pouring a molding box with a liquid iron-carbon alloy, charging its surface with a solid filler and immersing said solid filler into a liquid phase under the action of a mechanical force the magnitude of which exceeds a maximum buoyant force acting upon said solid filler in said iron-carbon alloy by not less than 5 percent. A process according to Claim 1, characterized in that said mechanical force has a magnitude of 100-10,000N/sq.m. A process according to Claim 3, characterized in that said force is applied in 1-60 seconds after said solid filler has been cast with a liquid iron-carbon alloy. A process according to Claim 1, characterized in that solid oxidizing agents are used as the solid filler and taken with a total amount of oxygen needed for the oxidation of 5 to 95 percent carbon and a total estimated oxidation of the remaining ingredients of iron-carbon alloy which affinity for oxygen is greater than for carbon. A process according to Claim 1, characterized in that pig iron is used as said iron-carbon alloy. A process according to Claim 1, characterized in that charging of said solid filler is carried out with pieces having the size of 0.025 to 0.300 of the molding box height, pouring with iron-carbon alloy is effected in the ratio of its average linear velocity to the linear velocity of the molding box movement equal to from 3:10 to 6:10. A casting machine for the preparation of a semi-finished metallurgical product for use in metallurgical melting processes comprising a conveyor with molding boxes, a pouring device adapted to pour a liquid iron-carbon alloy into the molding boxes, and a bin with a feeder to charge a solid filler into the molding boxes, the machine additionally comprising a device adapted to apply a mechanical action to said solid filler and liquid iron-carbon alloy, which action prevents floating of the solid filler in the liquid iron-carbon alloy. A casting machine according to Claim 5, comprising atomizers connected to a pipe-line for supplying a cooling medium, wherein said device for applying said mechanical action to said solid filler and liquid iron-carbon alloy comprises a cantilever having a longitudinal axis and a pivotably installed hollow roller, and a weighting material mounted on the cantilever with a capability of moving along the longitudinal axis, a first end of the cantilever hinged on a frame, the frame disposed such that said roller rests on at least one of said molding boxes, the length of said hollow roller is from 0.80 to 0.95 of a working length of the molding box, an outside diameter of said roller is from 1.1 to 1.4 of the molding box width, the atomizers are located in the vicinity of said roller and oriented to a lateral face of the roller.

Inventors: AFONIN SERAFIM ZAKHAROVICH, DOROFEEV GENRIKH ALEXEEVICH, IVASHINA EVGENY NEKTARIEVICH, MAKUROV ALEXANDR VLADIMIROVICH, PANFILOV ALEXANDR NIKOLAEVICH, RYABOV VYACHESLAV VASILIEVICH, SHAKHPAZOV EVGENY KHRISTOFOROV, SITNOV ANATOLY GEORGIEVICH, TSEITLIN MARK ARONOVICH, UTKIN JURY VIKTOROVICH, ZUBAREV ALEXEI GRIGORIEVICH, AFONIN, SERAFIM ZAKHAROVICH, DOROFEEV, GENRIKH ALEXEEVICH, IVASHINA, EVGENY NEKTARIEVICH, MAKUROV, ALEXANDR VLADIMIROVICH, PANFILOV, ALEXANDR NIKOLAEVICH, RYABOV, VYACHESLAV VASILIEVICH, SHAKHPAZOV, EVGENY KHRISTOFOROVICH, SITNOV, ANATOLY GEORGIEVICH, TSEITLIN, MARK ARONOVICH, UTKIN, JURY VIKTOROVICH, ZUBAREV, ALEXEI GRIGORIEVICH
Applicants: AKTSIONERNOE OBSCHESTVO ZAKRYT, AKTSIONERNOE OBSCHESTVO ZAKRYTOGO TIPA " INTERMET-SERVICE & CO."
Application year: 1995
Main classification: B22D3
IPC codes: C21C5, B22D5, B22D3, C21B11, B22D27, C21B5, C21C1, C21C3