GLASS FIBER SIZING AND SIZED GLASS FIBERS AND POLYOLEFIN REINFORCING ARTICLES

Abstract: An aqueous chemical treatment or size for silaceous fibers and fillers has a polyolefin compatible film forming polymer, organo functional coupling agent, and at least one stabilizer to produce a polyolefin reinforcing article. The stabilizer is one or more of the following: alkali metal and alkaline earth metal and ammonium, phosphinates, phosphites, hypophosphites, sulfites and bisulfites, organic phosphinates and/or phosphites and mixtures thereof and in combination with other types of antioxidants like hindered phenols, diarylamines, thiothers, wherein the amount of stabilizer is in an effective stabilizing amount. Optionally the size can have one or more partial esters of a branched carboxylic acid copolymer present.

Description: GLASS FIBER SIZING AND SIZED GLASS FIBERS AND POLYOLEFIN REINFORCING ARTICLES BACKGROUND OF THE INVENTION The present invention is directed to chemically treated glass fibers, strands or yarn where the fibers impart improved strength in reinforcing thermoplastics and in particular polyolefins. Glass fibers are produced by flowing molten glass via gravity through a multitude of small openings in a precious metal device, called a bushing. Typical formulations of glass fibers are disclosed in The Manufacturing Technology of Continuous Glass Fibres, Library of Congress Catalog Card Number 72-97429, by K. L. Loewenstein, Elsevier Scientific Publishing, 1973, at page 29. Glass fibers are, for example, those known as "E glass", "S glass", "D glass" and are typically between 3 and 30 microns in diameter. After the fibers have cooled very shortly after their issuance from the bushing and usually in close proximity to the the bushing, these fibers are treated with a chemical treating formulation usually referred to in the art as a sizing composition or size. The size serves to make the fibers more compatible with the material they will ultimately be used to reinforce and to make the fibers more easy to process. The aqueous size can be applied by sprayers, rollers, belts, metering devices or any similar application device. The sized glass fibers are gathered into bundles or strands comprising a plurality of individual fibers, generally from 200 to more than 3000. The sized glass fibers generally can have between about 0.01 and 5 percent of sizing composition based on the weight of the glass fiber. After their formation and treatment, the strands may be wound into a spool or "forming package" and/or may be chopped. The forming packages or chopped strands are usually dried in either an oven or at room temperature to remove some of the moisture from the fibers. The strands of treated fibers may be used to reinforce various materials such as thermoplastic polymers. Thermoplastics may be of different types including chemically coupled and non-chemically coupled thermoplastics. Particular types of strands of sized fibers have generally been directed to either chemically coupled or non-chemically coupled thermoplastics, such as polyalkylenes including polypropylenes. U.S. Patent 5,130,197 by Temple teaches a sizing having 1) an amino-silane coupling agent, 2) a carboxylic modified polyolefin resin, 3) an epoxy, urethane, or polyester resin or copolymer thereof, and 4) a binder stabilizer. These sized fibers are preferably used to reinforce non-chemically coupled polypropylene homopolymer. Also U.S. Patent 4,341,677 by Tamosauskas teaches a size having a film forming polymer, coupling agent and an oil-in-water emulsion of an antioxidant like hindered phenols and diarylamines. The fiber reinforced plastic industry continues to search for improvements in mechanical properties both initially and upon heat ageing. It is an object of the present invention to provide chemically treated or sized fibers and strands and bundles thereof resulting in improved initial mechanical strength and/or improved mechanical strength retention and/or color on heat ageing when used to reinforce either chemically coupled and/or non-chemically coupled thermoplastic polymers like polyalkylenes. SUMMARY OF THE INVENTION The objects of this invention are achieved by glass fibers which have been treated with a sizing having an organo functional inorganic coupling agent, a polyolefin compatible film forming polymer, one or more stabilizers that are effective against oxidizing phenomena, and a carrier for application of the size to the glass fibers. The stablizers are those like 1) alkali metal, alkaline earth metal, and ammonium, phosphinates, phosphites, hypophosphites, sulfites and bisulfites, organic phosphinates and/or phosphites and mixtures thereof; and 2) mixtures or combinations of the stabilizers of 1) with other types of stablizers, such as hindered phenols, diarylamines, thioethers and the like. Optionally the size can have a partial ester of a branched carboxylic acid copolymer as well as one or more other components like film forming polymers, coupling agents, fiber lubricants and the like. Another aspect of the invention is the polyolefin reinforcement comprised of a plurality of sized glass fibers having the aforementioned size. DETAILED DESCRIPTION OF THE INVENTION Any glass fiber suitable for reinforcing may suitably be treated in accordance with the present invention. Glass fibers such as soda lime glasses and borosilicate glasses like "E" glass and "621" type glass are particularly suited for this practice. Also "E" and "621" type glasses . formulated with lower amounts of or free of boron and flourine can be used. Examples of some suitable glass fibers are described at page 29 of The Manuf cturing Technology of Continuous Glass Fibers by K. L. Lowenstein, published in 1973 by Elsevier Scientific Publishing Company, Library of Congress Card Number 72-97429. The glass fibers to be treated according to this invention may typically be produced according to the teachings of U.S. Pat. No. 2,133,238. The glass fibers are formed by being drawn at a high rate of speed from molten cones of glass located at the tips of small orifices in one or more bushings of a glass melting device or furnace. Immediately after formation, the filaments are treated with with a chemical sizing prepared in the below-described manner. The application of the sizing to the filaments can occur while they are moving at a speed on the order of 1000 to 20,000 feet per minute (300 to 6100 meters/min) in the immediate vicinity of the hot bushings and the glass furnace in which the glass is melted. The application of sizing to glass fibers is well known in the art and may be accomplished by conventional methods such as a belt applicator, a "kiss-roll" applicator or by spraying. Details of a sizing applicator are shown in U.S. Patent No. 2,728,972. The amount of sizing deposited on the glass is around 0.01 to around 5 weight percent and preferably around 0.3 to around 2.5 to 3 weight percent of the treated glass fiber strand. After sizing, the glass fibers are gathered into bundles or strands of a plurality of fibers usually by a gathering shoe and/or a strand pulling device as illustrated in U.S. Pat. Nos. 3,292,013 and 4,248, 935. Additionally, or alternatively the fibers before or after collection into one or more strands may be attenuated by a chopper which cuts the fibers and/or collected strands into lengths from about a sixteenth (1.6 mm) to about 3 (76.2 mm) inches. The chopped strands can be deposited into a bag or box for ease in handling. The amount of moisture on the wet chopped glass fiber is generally in the range of up to about 20 weight percent. The glass may also be gathered into strands and collected as continuous glass fiber strand into a forming package and subsequently chopped in a remote wet chop process or after drying, in a dry chop process into lengths similar to those of the direct wet chop process . The forming package may be dried to remove residual moisture at room temperature or by oven heating. The sizing of this invention has, in addition to water, around 1 to around 50 weight percent solids which is on the basis of weight percent of nonvolatiles or of the dried film. Stated another way this is an amount of water of around 50 to around 99 weight percent of the size. Based on the weight percent of the non-volatiles the amounts of the nonaqueous components in the size are as follows: around 1 to around 30 weight percent of one or more organo-functional coupling agent, from around 50 to around 90 weight percent of the polyolefin compatible film forming polymer, and from around 1 to 25 weight percent of one or more stabilizers for the oxidizing phenomena. Optionally, but preferably, a partial ester of a branched carboxylic acid copolymer is present in an amount from around 1 to around 10 weight percent of the non-volatile components. Other components optionally added are present in minor amounts to that of the polyolefin compatible film forming polymer. The organo functional inorganic coupling agent useful in this invention can be an organo-functional silane compound used as a coupling agent between the predominantly organic size and the inorganic glass and any silane coupling agent known in the art may be used. Examples of organo-functional silane coupling agents useful in this invention are amino-functional silanes and epoxy-functional silanes. Commercially available silanes such as gamma-aminopropyltriethoxy silane and gamma-glycidoxypropyltrimethoxy silane are useful. These silanes are available from OSi specialties Company of Tarrytown New York as A-1100 and A-187, respectively, and from Dow Corning Corporation as Z-6011 and Z-6040, respectively. The amino functional silane is preferred and the silane may be hydrolyzed to some degree before use by reacting it with an effective amount of a suitable acid like a carboxylic acid such as acetic acid. Other coupling agents that can be used are the transition metal coupling agents such as the titanium and zirconium organofunctional coupling agents like the monoalkoxy, monoalkoxypyrophosphato, chelate, and coordinate types and the Werner coupling agents and the like. All of these provide the interfacial boundary area coupling between the glass inorganic surface and the organic matrix polymer. The polyolefin compatible film forming polymer is preferably an aqueous emulsion of a chemically-modified polyolefin. The term "chemically-modified polyolefins" refers to acid modified polyolefins either amorphous or crystalline in type such as those produced by the method explained in U.S. Patents 3,416,990 (Robinson); 3,437,550 (Paul) and 3,483,276 (Mahlman) . A discussion of these polyolefins, their modification and emulsification may be found in U.S. Patent 5,130,197. An example of a crystalline carboxylated polypropylene polymer that can be used in the emulsion to produce glass fibers of the present invention is the ® Hercoprime G type resin available from Hercules, Inc., Bloomington, Delaware. An example of the carboxylated amorphous polypropylene polymer that can be used in the sizing composition for preparing glass fibers of the present invention is commercially available as Epolene ® E-43 available from the Tennessee Eastman Co. Another suitable example is an emulsion of the Epolene E-43 available from Byk-Cera under the trade designation of Aquacer 841 emulsion. This latter emulsion is the preferred polyolefin compatible film forming polymer which is present in sufficient quanitites to provide a predominant amount of the solids or non-volatiles of the aqueous size. An aqueous polyolefin emulsion can be prepared from either the carboxylated amorphous polyolefin such as the carboxylated amorphous polypropylene polymer or the crystalline carboxylated polyolefin such as the crystalline ® carboxylated polypropylene, Hercoprime G resin, or mixtures. Any surfactants or combination of surfactants known to those skilled in the art in emulsifying polyolefins can be used. A commercially available version of the aqueous polyolefin emulsion is the carboxylated amorphous polypropylene that is from National Starch, Procter Division, under the trade designation Protolube RL-5440 polypropylene emulsion. This product has a pH of about 9.5+0.5, a solids content of 32±1, a color ranging from tan to a grey emulsion and is slightly cationic and has a boiling point of approximately 100°C, a specific gravity of 0.98. An infrared spectraphotometric curve and differential scanning colorimeter curve of the RL-5440 emulsion product are presented as Figs. 3 and 4 of U.S. Patent 5,130,197 and the procedure for obtaining the curves is given therein. Another component of the chemical treating composition, which preferably is present, is one or more stabilizers against the oxidizing phenomenon. It has been discovered that particular types of stabilizers that may act as antioxidants provide particular benefits to the thermoplastic polymer such as polyolefins, polyamides, and polyesters (PBT and PET) that are reinforced with glass fibers or filled with siliceous material like glass flake and the like. These water emulsifiable, dispersible, or soluble stabilizers include inorganic and organic phosphinates, phosphites, and sulfites. These can be used alone or in mixtures with each other or in mixtures with any other emulsifiable, dispersible, or soluble antioxidant that is known to those skilled in the art for use with coatings and films on discrete surfaces such as fibers. For instance, the antioxidants of U.S. Patents 4,483,948; and 4,341,677 may be used and these patents are hereby incorporated by reference. A few examples of these other types of antioxidants include hindered phenols, diarylamines, thiothers, and the like. Examples of the phosphinates, phosphites, and sulfites that can be used include the water soluble alkali metal and alkaline earth metal and ammonium, phosphinates, phosphites, hypophosphites, hydrogen phosphites, sulfites, bisulfites, and hydrosulfites. Also the water dispersible or emulsifiable organic phosphinates and/or phosphites can be used. Another suitable type of stabilizer is the alkali metal phenyl phosphonates, an example of which is the sodium benzene phosphinate. This material is present in a similar amount as aforementioned and greater amounts can be used if additional benefits are required. An example of sodium benzene phosphonate is that available from Stauffer Chemical Company having the formula C 6 H6θ2PNa with a formula weight of 164. Other examples of antioxidant-type stabilizers include organic phosphites like diisodecyl pentaerythritol phosphite, trialkyl phosphites, like triisodecyl phosphite, tristearyl phosphite, trimethyl phosphite, tris- (2,4-di-tert- butyl-phenol) phosphite, tris- (2,4-ditnethylphenol) phosphite, alkylphenyl phosphites like isooctyl diphenyl phosphite, diisooctyl phenyl phosphite, hindered type organic phosphites like phosphorous acid cyclic neopentanetetrayl dioctadecyl ester, phosphorous acid and phosphorous cyclic neopentanetetrayl bis (alkylbutylphenyl) ester, and others as described in U.S. Patent 5,278,210 hereby incorporated by reference. A suitable example is Irgafos 168 which is tetrakis (2,4-di-tert-butylphenyl) 4,4'- biphenylylendiphosphonite. The preferred stabilizers are the water soluble inorganic hypophosphites and most preferably the sodium hypophosphite is the sole stabilizer present in a preferred amount of from around 3 up to around 10 weight percent of the aqueous chemical treating composition. A suitable sodium hypophosphite is that available from Fisher Scientific Company as solid sodium hypophosphite having the formula NaH2Pθ2-H2θ. This material is water soluble and when the carrier for the chemical treating composition is water, it is merely dissolved into the chemical treating composition or predissolved and added to the chemical treating composition. For the amount of the phosphite or phosphonate stabilizer, greater amounts can be used to provide even greater benefits in mechanical properties. The amount of the stabilizer that should not be exceeded is where the amounts of the other components are limited to the extent to deleteriously affect the overall performance of the size. The effective stabilizing amount of the stabilizer is that which improves the mechanical prperties of the glass fiber reinforced and/or siliceous filled thermoplastic polymeric matrix. Also, mixtures of these stabilizers are useful in the chemical treating composition and preferably a mixture is used. The mixture of stabilizers can be incorporated into the chemical treating composition or added in a secondary treatment after the chemical treatment has first been applied to the fibers of reinforcement. Examples of other antioxidants that can be used in stabilizer combinations with one or more of the phosphites, phosphonates and sulfites are the thioethers and polymers thereof. A nonexclusive example of these is di (tridecyl) thiodipropionate with a chemical formula of S (CH2CH2COOC13H27) 2 • A suitable thiodipropionate is that available from Grace from their Evans Chemetics Unit in Waterloo, New York, under the product name Evanstab 13. Another example is distearyldithiodipropionate (DSTDP) available from Eastman Chemical Company, Tennessee under the trade designation PA 49M. The amount of the mixture is generally in the aforestated range of amounts for the stabilizer. Optionally, but preferably the size also has carboxylic copolymer partial ester which may be used in this invention as an emulsifier and/or lubricant. It and its derivatives are polymers with pendant hydrocarbon and ethoxylated ester chains. A commercially available version of a suitable carboxylic copolymer partial ester is that from Akzo Chemie America, of Chicago, under the trade designation Dapral ® GE 202 partial ester. This material has an average molecular weight of about 20,000, a specific gravity of 1.05 at 25°C, a flash point of 178°C COC (Cleveland Open Cup) and is a yellowish, viscous liquid with little odor. This material is a partial ester of a branched carboxylic acid copolymer. This polymer has a comb-like structure and the main chain consists of carbon atoms only. The alkyl branches are hydrophobic and the ester and ether groups are hydrophilie. The sizing may optionally have other ingredients which are known to those skilled in the art to be useful in fiber glass sizing such as emulsifiers, antifoams, surfactants and the like. The sizing may be prepared by any method known to those skilled in the art, and applied to the fibers and/or fillers by any method known in the art. For instance when the glass fibers are produced by a dry chop method it is preferable to have an additional film forming polymer in the size to improve the strand integrity. The carrier for the chemical treating composition is any material known to those skilled in the art for applying the chemical treatment to fibers during their formation or after their formation or to other types of reinforcement during their formation. The carrier can be an organic solvent or water or a combination to produce foams and gels of the chemical treatment. Preferably water is the carrier to give an aqueous chemical treating composition. The carrier like water is present in effective amounts to give total solids (non-volatile content) in the range sufficient for a viscosity of the chemical treatments for application to the fibers for reinforcement or to the fillers. Generally, the water is present in an amount sufficient to give a total solids in the range of about 1 to about 50 weight percent and preferably about 5 to 20 weight percent. In any event the amount of the various components and the amount of water should be balanced so that the viscosity of the solution is not greater than around 150 centipoise at 20°C. Solutions having viscosities greater than 150 centipoise are difficult to apply as aqueous emulsion, dispersions or solutions to fibers during their formation, especially to glass fibers that are formed from molten streams of glass with standard type application equipment without causing the breakage of the continuity of the fibers . It is preferred that the viscosity of the aqueous chemical treating composition for application to glass fibers during their formation is in the range of about 20 to 60 centipoise at 20°C for best results. If the aqueous chemical treating composition is prepared with thixotropic agents to make it a foam or gel, then the viscosity will be that appropriate to such formulations and the application equipment will be appropriate for applying foams and gels to the fibers or reinforcement. The aqueous chemical treating composition can be prepared by addition of any of the components simultaneously or sequentially to each other, but the components can also be prediluted before they are combined and diluted with water into the aqueous size. This is to enhance their solubility, dispersibility or emulsifiability. Not only do the reinforcing fibers benefit from treatment with the aforementioned chemical treating composition, but also inorganic fillers sometimes used in reinforced composites would benefit from such treatment. Nonexclusive examples of such inorganic fillers include mica, wollastonite, talc, clay, flaked glass and novaculite. Contacting the fillers with the aqueous size is accomplished by spraying or dipping or the like as a convenient way of treating them. The dried fibers are used to reinforce polymeric matrices in any of the molding processes known to those skilled in the art utilizing either chopped strand, continuous strand or a mixture thereof. Preferably, the chopped fiber strands are mixed with the matrix polymer resin in a dry powder mixture to produce a homogeneous batch of matrix polymer. The batch can be compression or injection molded to produce the fiber reinforced polymeric part or shaped device. These sized glass fibers are used in molding the fiber reinforced polymers such as fiber reinforced polypropylenes, mixtures of polypropylenes and polyethylenes and polyalkylene terephthalates, including poly(ethylene terephthalate) and poly(butylene terephthalate) , polya ides, polyphenylene oxide, polystyrenics and other similar polar thermoplastic polymers, copolymers, blends and alloys. Preferred Embodiment The preferred embodiment utilizes glass fibers that are processed by an after dried wet chop method having a dried residue of the size where the fibers have a length of around 1/8" to 1/2". The fibers have conventional filament diameters that can range from around 1 micron to greater than 30 microns but are preferably in the diameter of around 10 to around 16 microns. The aqueous size preferably has the formulation with ranges of preferred amounts for the components as shown in Table A. : TABLE A COMPONENT WEIGHT PERCENT OF THE SOLIDS Gamma Aminopropyltriethoxysilane 7.5-to-23.5 Polypropylene emulsion 64-to-84 sodium hypophosphite 3.0-to-15 carboxylic copolymer partial ester 0.3-to-2.3 The fibers of this invention may be used to reinforce thermoplastics which are chemically coupled. The term "chemically coupled" means a thermoplastic such as polypropylene to which has been added an acid modified polyolefin which provides chemical moieties for reaction with the components of the sizing. This acid modified polyolefin chemical coupler is added to the thermoplastic as a physical mixture prior to compounding with the fibers and may be, for example, polypropylene with pendant carboxylic acid groups. These pendant carboxylic acid groups are believed to react with the basic amino groups of the amino silane to create a strong bond between the glass to which the silane is attached and the polyolefin compatible chemical coupler. An example of a suitable chemically coupled polyolefin for use with the fibers of this invention is commercially available as PCO-72 from Himont. PCO-72 is a mixture of unmodified polypropylene homopolymer and a small amount of modified polypropylene homopolymer. The fibers of this invention may also be used to reinforce thermoplastics which are not chemically coupled. In this type of thermoplastic, the chemical coupler mentioned above is not added to the thermoplastic. An example of a suitable non-chemically coupled thermoplastic is commercially available as Profax ® 6523 polypropylene from Himont and is a polypropylene homopolymer. The sized fibers of this invention provide generally good results in both chemically coupled and non-chemically coupled thermoplastics. The following is an example of one method of preparation of the sizing of this invention. About 24 kilograms (Kg.)of polypropylene emulsion were added to about' to 20 liters of deionized water at room temperature in a large tank with gentle stirring. It is important to avoid air entrainment and foam generation in the mixture. In a separate tank, about 3.1 Kgs. of gamma-aminopropyl- triethoxy silane were added to about 37 liters of deionized water having 1 Kg of acetic acid at room temperature. After gentle stirring for about 10 minutes, it was added to the prior mixture with moderate stirring. The aforementioned amount of the sodium hypophosphite is dissolved in water and added to the mix. In a separate tank about 150 grams of Dapral ® partial ester were added to about 5 liters of deionized water at 25°C. After stirring for about 10 minutes, it was added to the prior mixture. Glass fibers were sized with a roller applicator and chopped in a wet condition. The fibers were dried and compounded with a commercially available chemically coupled homopolymeric polypropylene (CCHP) using a counter-rotating extruder at a 30 weight percent glass content. The compounded glass and polypropylene mixture was molded in a 200 ton injection molding unit in a method known in the art and then tested for strength. The fibers were also compounded and molded with a commercially available non-chemically coupled homopolymeric polypropylene (HP) in the same manner. The size formulations of Table 1 were prepared in a manner similar to that for the preferred embodiment which is further described at Example 2 in Table 1. The sizings of Table 1 were each applied to a plurality of glass fibers to prepare a strand construction having 800 filaments per strand where the filaments had a fiber diameter of 13 microns. The strands for each example were wound into separate forming packages. A number of forming packages for each example, between 2 and 12, but preferably 4 were unwound and combined into a strand which passes over an applicator to apply additional moisture and/or sizing before chopping in a wet condition. Usually it is preferred to chop a multitude of strands, usually in the range of around 10 to 15 per chopper. The chopped strand can be either dried directly after chopping or collected and dried by a fluidized bed continuous process dryer. In Table 1 the second batch of sizing formulations were prepared and along with these another Illustrative Example 1 (Illustrative Example IB)and another Example 2 (Example 2) were also prepared. These additional formulations are listed as Illustrative Example IB, Example 2B, and Examples 3-6 in Table 1 and they all employ sodium hypophosphite as the stabilizer or antioxidant. The sizings were applied to glass fibers formed in strand constructions and chopped compounded, molded and tested in homopolymer polypropylene and chemically coupled polypropylene in a similar manner to that for Examples 1 and 2 and 7-9 for initial mechanical properties. TABLE 1 Sizing Formulations f% of Total Solids) 111. 111. Ex. 1 Ex. 1 Ex. 2 Ex. IB Ex. 2B Ex. 3 Ex. 4 Ex. 5 Ex. 6 Ex. 7 Ex. 8 Ex. 9 A-1100 gamma- aminopropyltriethoxysilane 21.1 21.2 21.2 21.1 21.2 15.0 15.7 7.8 19.9 21.2 21.3 21.4 Polypropylene Emulsion 77.2 66.7 66.6 77.2 66.6 82.5 79.9 78.9 70.0 72.1 67.1 61.9 Dapral GE 202 Partial Ester Carboxylic Acid Copolymer 1.7 1.3 1.3 1.7 1.3 1.3 1.3 1.3 1.3 1.3 1.3 1.3 Sodium Benzene Phosphinate -- 10.8 -- -- -- -- -- -- -- -- -- -- Sodium Hypophosphite -- -- 10.8 -- 10.8 8.7 3.0 11.9 8.7 -- -- -- Organic Phosphite Irgasfos 168 Emulsion 3.6 3.6 3.6 ^1 Hindered Phenol I Irganox 1010 Emulsion __ _- 1.8 1.8 1.8 Thioester Antioxidant - DSTOP -- -- -- -- -- -- -- -- -- -- 4.9 9.9 LOI 1.00 0.80 0.98 -- -- -- -- -- -- 0.97 -- -- Grams of Fuzz 0 0 0.03 0 0 0 0 0 0 0 0 0.03 The chopped strands for each example were compounded, molded and tested separately in a similar manner in homopolymer polypropylene (12 Mf Himont F30S) and chemically coupled polypropylene (addition of 2.5 percent Exxelor POX1 1015 to the base polypropylene resin) . Compounding was performed to make fiber reinforced polypropylene plastic (FRP) samples by extruding the chopped glass fiber strands with pellets of the matrix polypropylene polymer in a Werner Pfleiderer ZSK 30 (millimeter) twin-screw extruder. The chopped strands were fed downstream using a vibratory glass strand feeder. The pellets of the matrix polymer and any additional polymer additives were dry blended prior to feeding into the extruder. The screw speed for the extruder was 300 rpm and the vacuum was full. Injection molding was performed with a Battenfeld CD750 machine and the screw speed was 100 rpm and the clamp pressure was 100 bar and the back pressure was 35 bar. The samples were molded using an ISO family mold. The compounds for each example were tested for initial mechanical properties and color. They were also tested for retention of mechanical properties and color after heat-aging at 150°C for a total of 13 days. The initial mechanical property results are listed in Table 2 and the heat-aging mechanical property results for various times during the 13-day period are listed in Tables 3 and 4. The tests were conducted in accordance with the following methods for the stated test: Tensile: on a Zwick 1476 machine according to ISO 527 with a 100 kiloNewton load at 2 millimeter (mm) /minute for measurement of modulus and 5 mm/minute for strength measurements for the crosshead speed, where the sample was held by mechanical wedge grips; Flexural: on A Zwick Model 1474 according to ISO 178 at 2 mm/minute for modulus and 5 mm/minute for strength with a 3 KiloNewton load with a three-point bending configuration and with a 64 mm span; Impact: with a Zwick impact tester (pendulum type) according to ISO standard 179 (Charpy) and ISO standard 180 (Izod) ; color: Dr. Lange Colorimeter; and glass content: by burning off broken test specimens. The units in the following tables are SI units utilizing the following abbreviations: MPa = (megapascals) ; GPa = (gigapascals) ; J/m = (joules/meter) ; and kJ/meter2 = kilojoules/ square meter; (mm) = millimeters; (μm) = microns; (g/cm3) = grams per cubic centimeter; whiteness index is the opposite of the yellow index. The yellow and whiteness indices are related in that a low value for yellow or high value for whiteness are indicative of better performance. In the first part of Table 2 the Illustrative Example 1 was conducted with examples 1-2 and 7-9. In the second part of Table 2, Table 2(B) the Illustrative Example IB was conducted with examples 2b and 3-6. The formulation of Example 2 as shown in Table 2 resulted in increased mechanical properties in homopolymer relative to the illustrative example. Although the glass content was slightly higher, the tensile strength was 23 percent higher, the flexural strength was 20 percent higher, the unnotched charpy was 30 percent higher and the unnotched Izod was 59 percent higher. The color values indicated a whiter product (higher L value) and less yellow (lower b value) . All of the Examples 1-9 gave comparable or higher initial mechanical properties. The results of the mechanical properties in Table 2 for Examples 2B and 3-6 and Illustrative Example IB show a connection between the amount of sodium hypophosphite in the sizing formulation and the level of mechanical properties. Example 4 had the lowest amount of sodium hypophosphite and also had the lowest level of mechanical properties. Example 5 had the highest amount of sodium hypophosphite and had the highest level of mechanical properties. The mechanical properties for most of the size formulations of Examples 2-9 of Table 1 as shown in Table 2 resulted in equivalent mechanical properties to those obtained for the Illustrative Example 1 formulation. As shown in Table 3, the specimens were taken from heat-aging at 150°C at the first, third, sixth, ninth and thirteenth days and tested for tensile and impact properties. Examples 2 and 8 had significantly better heat aging results than the illustrative example without the antioxidant. The product from Example 9 had good results up until the 13th day and then failed to the extent that it was not measurable due to oxidation. The heat-aging properties for the product of Example 9 are in the most part similar to those for Example 8 until the 13th day. Given the similarities in the formulation and the data through nine days, the 13th day value may be suspect. The impact properties (unnotched charpy and unnotched Izod) in homopolymer polypropylene are listed in Table 3. All the examples with antioxidant or stabilizer have superior properties to those of Illustrative Example 1. In unnotched Izod, both the product of Example 8 and Example 2 stood out as being significantly better. The property retention in unnotched charpy and unnotched Izod were slightly different. The unnotched charpy impact test demonstrated with Examples 1-2 and 7-9 significantly better property retention after 13 days than that for Illustrative Example 1. However, the results for Example 2 were slightly better than the others. The unnotched Izod was more differentiating, and Examples 8 and 2 were significantly better than those for Illustrative Example 1 and the other size formulations. The properties of tensile strength and elongation for chemically coupled polypropylene after heat-aging are listed in Table 4. In chemically coupled polypropylene, three examples, 2, 8 and 9, were significantly better than the results for Illustrative Example 1. Impact retention of the chemically coupled polypropylene with heat-aging is also shown in Table 4. Similar results are observed where the results for Examples 2, 8 and 9 providing the best results on heat aging. From the data in Tables 1-4, the size and sized glass fibers and polypropylene reinforcement articles of the present invention provides significant improvement in heat aging for the reinforced polypropylene and significant improvements in homopolymer mechanical properties of the polypropylene and significant improvement in color of both the homopolymer and chemically coupled polypropylene in terms of higher L values (more white) and lower b values (less yellow) . 1 BLE---2. Mechanical and Color Properties 111. Ex. Ex. 1 Ex. 2 Ex. 7 Ex. 8 Ex. 9 1 Himont F3C )s Homopolymer Polypropylene 12 Melt Flow Tensile Strength (MPa) 66 73 81 70 71 68 Tensile Elongation (%) 1.5 1.6 1.9 1.5 1.5 1.5 Flexural Strength 86 97 103 91 93 89 (MPa) Flexural Modulus (GPa) 5.3 5.7 5.6 5.5 5.7 5.5 Unnotched Charpy 11.4 11.4 14.8 10.7 11.4 10.9 (kJ/m 2 ) Unnotched Izod (kJ/m 2 ) 19.5 20.9 31.1 21.0 18.7 18.7 Glass Content (%) 30.6 31. "6 31.9 31.0 31.8 30.6 Color Values L 57.8 62.6 59.7 59.8 59.1 60.1 Color Values a -2.5 -2.4 -2.5 -2.5 -2.2 -2.5 Color Values j -, 5.5 5.9 2.6 6.2 6.2 6.3 Himont F30s Plus 2.5% Exxelor 1015-(Chemically Coupled) Tensile Strength (MPa) 101 100 96 102 103 101 Tensile Elongation (%) 2.9 2.8 3.0 3.0 3.0 3.0 Flexural Strength 143 139 134 145 144 141 (MPa) Flexural Modulus (GPa) 5.8 6.0 5.8 5.9 5.9 5.8 Unnotched Charpy 32.7 30.9 30.2 33.6 32.8 33.3 (kJ/m 2 ) Unnotched Izod (kJ/m 2 ) 59.9 56.8 57.2 60.8 63.9 63.3 Glass Content (%) 31.3 31.9 28.2 31.5 31.7 30.8 Color Values L 56.6 58.4 57.4 57.4 55.8 55.0 Color Values a -2.3 -2.8 -2.4 -2.2 -2.7 -2.5 Color Values j -, 6.7 5.5 2.3 7.1 6.9 6.4 TABLE 2 (B) Mechanical and Color Properties 111. Ex. IB Ex. 2B Ex. 3 Ex. 4 Ex. 5 Ex. 6 Himont F30s Homopolymer Polypropylene 12 Melt Flow Tensile Strength (MPa) 70 80 81 76 82 79 Tensile Elongation (%) 1.6 2.0 1.8 1.7 1.8 1.7 Flexural Strength 92 107 108 99 109 105 (MPa) Flexural Modulus (GPa) 5.4 5.4 5.6 5.6 5.6 5.6 Unnotched Charpy 11.1 16.1 13.9 12.2 13.8 13.3 (kJ/m 2 ) Unnotched Izod (kJ/m 2 ) 20.2 29.1 26.2 22.8 27.5 27.1 Glass Content (%) 30.7 31.7 31.3 31.6 31.4 31.1 Color Values L 58.63 58.0 59.3 59.6 57.8 60.4 Color Values a -2.5 -2.2 -2.1 -2.3 -2.0 -2.4 Color Values j -, 4.9 1.6 2.6 3.9 2.0 2.7 Himont F30s Plus 2.5% Exxelor 1015 (Chemically Coupled Tensile Strength (MPa) 102 94 99 103 96 101 Tensile Elongation (%) 3.0 3.0 2.9 2.9 2.7 3.0 Flexural Strength 140 132 137 141 132 138 (MPa) Flexural Modulus (GPa) 5.5 5.7 5.7 5.6 5.6 5.6 Unnotched Charpy 32.3 29.1 31.0 31.5 26.6 31.7 (kJ/m 2 ) Unnotched Izod (kJ/m 2 ) 63.6 57.4 60.3 58.8 50.5 63.4 Glass Content (%) 31.4 31.4 31.7 32.1 31.8 31.7 Color Values L 55.3 56.5 56.2 56.2 56.7 56.1 Color Values a -2.1 -2.1 -2.0 -2.2 -2.2 -2.2 Color Values ] _, 5.6 1.9 2.3 3.7 1.8 2.4 lAJ-iE_3- Heat Aging Tensile Strength Retention of Homopolymer PP after Exposure to 150°C Tensile Strength (MPa) 111. Example E . 7 Ex. 8 Ex. 9 Ex. 1 Ex. 2 Initial 66 70 71 68 73 81 1 Day 58 62 62 60 63 68 3 Days 58 61 61 60 63 66 6 Days 46 60 61 60 61 65 9 Days 35 54 60 60 51 64 13 Days 20 33 60 -- 33 64 Tensile Elongation (%) Initial 1.5 1.5 1.5 1.5 1.6 1.9 1 Day 1.5 1.4 1.4 1.4 1.3 1.4 3 Days 1.6 1.4 1.4 1.4 1.3 1.3 S Days 0.7 1.4 1.4 1.4 1.3 1.3 9 Days 0.5 1.1 1.4 1.4 0.9 1.3 13 Days 0.4 0.6 1.4 -- 0.6 1.4 Heat Aging Unnotched Charpy and Izod Impact Retention of Homopolymer PP After Exposure to lSp g C Unnotched Charpy (kJ/m 2 ) Initial 11.4 10.7 11.4 10.9 11.4 14.8 1 Day 10.5 9.9 10.1 9.6 10.0 10.5 3 Days 10.3 10.1 10.1 10.2 10.2 10.5 6 Days 10.9 10.ϊ 9.8 10.1 10.2 10.6 9 Days 9.9 10.4 9.9 11.0 9.9 10.2 13 Days 4.0 8.7 9.9 10.3 8.7 11.0 Unnotched Izod (kJ/m 2 ) Initial 19.5 21.0 18.7 18.7 20.9 31.1 1 Day 19.5 18.8 18.4 17.7 17.1 21.9 3 Days 18.1 17.3 17.6 19.4 15.8 21.6 6 Days 18.0 17.7 17.7 16.8 17.2 21.0 9 Days 14.6 18.8 17.6 18.5 15.8 19.0 13 Days 3.7 7.3 17.4 8.1 6.7 20.2 TABLE 4 Heat Aging Tensile Strength Retention of Chemically Coupled PP after Exposure to lSQ Q C Tensile Strength (MPa) 111. Ex. 1 Ex. 7 Ex. 8 Ex. 9 Ex. 1 Ex. 2 Initial 101 102 103 101 100 96 1 Day 95 97 99 97 96 95 3 Days 86 90 92 91 92 91 6 Days 80 85 88 87 89 89 9 Days 60 71 85 82 65 88 13 Days 15 28 82 79 47 82 Tensile Elongation (%) Initial 2.9 3.0 3.0 3.0 2.8 3.0 1 Day 2.2 2.2 2.2 2.2 2.2 2.3 3 Days 1.9 1.9 2.0 2.0 2.0 2.1 6 Days 1.7 1.8 1.9 1.9 1.9 2.1 9 Days 1.2 1.4 1.8 1.6 1.2 2.0 13 Days 0.3 0.7 1.7 1.7 0.8 1.8 Heat Aging Properties Unnotched Charpy and Izod Chemically Coupled PP 150°C Unnotched Charpy (kJ/m 2 ) Initial 32.7 33.6 32.8 33.3 30.9 30.2 1 Day 25.1 25.4 26.2 26.5 25.6 25.8 3 Days 22.6 23.2 22.1 23.9 21.2 24.2 6 Days 20.4 22.2 20.6 21.6 20.4 23.6 9 Days 9.3 18.9 19.1 19.7 19.0 21.8 13 Days 4.4 7.1 19.2 20.6 15.6 19.9 Unnotched Izod (kJ/m 2 ) Initial 59.9 60.8 63.9 63.3 56.8 57.2 1 Day 44.6 47.3 45.1 48.1 45.6 46.4 3 Days 42.1 40.5 42.6 44.0 42.1 44.2 6 Days 34.0 39.3 39.7 38.8 38.5 40.3 9 Days 23.2 33.4 34.2 30.0 33.6 39.0 13 Days 5.2 9.1 32.7 34.0 16.9 36.4

Claims: WE CLAIM : 1. A sizing composition for glass fibers comprising: at least one organo-functional silane coupling agent; a polyolefin compatible film former, at least one stabilizer selected from the group comprised of 1) alkali metal and alkaline earth metal and ammonium, phosphinates, phosphites, hypophosphites, sulfites and bisulfites and organic phosphinates and/or phosphites,and mixtures thereof and mixtures with other types of antioxidants selected from the group consisting of hindered phenols, diarylamines, thiothers, in an effective stabilizer amount and; carrier in an effective application amount. 2. The sizing composition of Claim 1, wherein the stabilizer is selected from the group consisting of sodium hypophosphite, potassium hypophosphite, ammonium hypophosphite, and sodium benzene phosphonate. 3. The sizing composition of Claim 1, wherein the organofunctional silane coupling agent is an amino organosilane coupling agent selected from the group consisting of gamma-aminopropyltrimethoxy silane, polyaminoalkyl alkoxysilanes and their hydrolyzed derivatives. 4. The sizing composition of Claim 1, which includes a partial ester of a branched carboxylic acid copolymer. 5. The size of claim 1 further comprising a carboxylic acid in an amount sufficient to hydrolyze said silane and the carrier is water. 6. The size of claim 1 wherein the polyolefin compatible film forming polymer is a acid modified polypropylene present in an oil-in-water emulsion where the emulsion is present in an amount sufficient to yield and amount of polymer from 50 to around 90 weight percent of the solids of size. 7. The size of claim 1 wherein the stabilizer is selected from the group consisting of a mixture of organic phosphite and hindered phenol stabilizer and a mixture of organic phosphite and hindeered phenol and thioether stabilizers in an amount from around 2 to 20 weight percent of the nonaqueous components of the size. 8. The size of claim 1 which is present on glass fibers in a moisture reduced amount of between 0.3 and 3 weight percent of the glass as measured on a loss on ignition basis. 9. An aqueous sizing composition for glass fibers comprising, in addition to water: at least one coupling agent selected from the group consisting of hydrolyzed silanes and non-hydrolyzed silanes, and mixtures thereof present in an amount between about 5 and 25 weight percent on a non-aqueous basis; a polypropylene compatible film former present in an amount between about 50 and 90 weight percent on a non-aqueous basis, at least one stabilizer selected from the group comprised of 1) alkali metal and alkaline earth metal and ammonium, phosphinates, phosphites, hypophosphites, sulfites and bisulfites and mixtures thereof and in admixture with other types of antioxidants selected from the group consisting of hindered phenols, diarylamines, thiothers, organic phosphinates and/or phosphites, and the like; and 2) organic phosphinates and/or phosphites in combination with other types of antioxidants like hindered phenols, diarylamines, thiothers, wherein the amount of stabilizer is in the range of from about 2 to about 15 weight percent of the solids of the size; and a partial ester of a branched carboxylic acid copolymer present in an amount between about 1 and 10 weight percent on a non-aqueous basis. 10. The aqueous sizing composition of Claim 9, wherein the stabilizer is selected from the group consisting of sodium hypophosphite, potassium hypophosphite, ammonium hypophosphite, and sodium benzene phosphonate. 11. The aqueous sizing composition of Claim 9, wherein the organofunctional silane coupling agent is an amino organosilane coupling agent selected from the group consisting of gamma-aminopropyltrimethoxy silane, polyaminoalkyl alkoxysilanes and their hydrolyzed derivatives. 12. The size of claim 9 further comprising a carboxylic acid in an amount sufficient to hydrolyze said silane. 13. The size of claim 9 wherein the polyolefin compatible film forming polymer is a maleonated polypropylene present in an oil-in-water emulsion where the emulsion is present in an amount sufficient to yield from 50 to around 90 weight percent of the polymer in the solids of the size. 14. The size of claim 9 wherein the stabilizer is selected from the group consisting of a mixture of organic phosphite and hindered phenol stabilizer and a mixture of organic phosphite and hindered phenol and thioether stabilizers in an amount from around 2 to 20 weight percent of the nonaqueous components of the size. 15. The size of claim 1 which is present on glass fibers in a moisture reduced amount of between 0.3 and 3 weight percent of the glass as measured on a loss on ignition basis. 16. A polyolefin reinforcing glass fiber bundle wherein each glass fiber has a portion of its surface covered with a thin film of the sizing composition of Claim 15. 17. A polyolefin reinforcing glass fiber bundle of claim 16 herein the bundle is a chopped polypropylene reinforcing glass fiber bundle.

Inventors: MEESTERS LAURA A, SCHELL PHILIP L, MEESTERS, LAURA, A., SCHELL, PHILIP, L.
Applicants: PPG INDUSTRIES INC, PPG INDUSTRIES, INC.
Application year: 1995
Main classification: C03C25
IPC codes: C03C25, C08J5