BONDING CURED ELASTOMER TO PLASTIC AND METAL

Abstract: The invention provides a method of directly bonding an elastomer, such as silicone rubber, to a plastic by separately ionizing a surface of the elastomer and ionizing a surface of the plastic and then immediately compressing the ionized surfaces together while applying pressure and heat. The invention further provides for an open top cap (10) in which a silicone rubber septum (20) is directly bonded to the flange (14) of an open top plastic cap (10).

Description: BONDING CURED ELASTOMER TO PLASTIC AND METAL TECHNICAL FIELD The present invention relates to bonding of a cured elastomer to a plastic or metal. More particularly, the present invention relates to a method of bonding cured silicone rubber to a plastic and plastic caps made by such a method. BACKGROUND OF THE INVENTION It is well known that silicone rubber is generally inert and is, therefore, particularly well suited for use in medical and scientific fields. For example, silicone rubber is often employed as part of a closure for bottles or containers intended to receive medical or scientific samples. Particularly useful in medical and scientific field is a container utilizing an open top cap, which is a cap with an aperture therein which is in turn sealed by a septum. Sealing the cap's aperture prevents contamination or loss of the sample yet allows a needle to be inserted through the septum of the cap and into the container in order to insert or withdraw the sample. Due to the generally inert nature of silicone rubber and its resealing properties it would be preferred that the septum be comprised, at least in part, of silicone rubber. The EPA has published standards under 40 C.F.R. §136 "Guidelines for Establishing Test Procedures for the Analysis of Pollutants" and 40 C.F.R. §141 "National Interim Primary Drinking Water Regulations: Control of Trihalomethanes in Drinking Water" which relate to acceptable testing procedures. These EPA standards specify a vial/cap/septum combination as well as detailed cleaning and sampling procedures which are designed to ensure that the sample is not contaminated or lost prior to analysis. These EPA regulations specify an open top cap and a septum comprised of silicone rubber laminated with polytetrafluoroethylene (Teflon) , such that the face of the Teflon lamination is exposed to the sample. Although use of a united cap and liner meeting the EPA specifications would be preferred, the industry has to date largely dealt with these requirements by using a separate septum unattached to the cap. Unfortunately, existing methods of attaching a silicone rubber septum to an open top cap are ill-suited for uses related to sampling of scientific or medical samples. The conventional method of attaching a liner or septum onto a cap utilizes some type of adhesive, which may come in contact with, and potentially contaminate, the sample. In this regard it should be noted that even minor contamination may make critical analytical analysis of pollutants difficult or untrustworthy, since tests are commonly directed towards the presence of pollutants at the level of ppm (part per million) or even ppb (part per billion) . Moreover, the EPA specification of a silicone rubber/Teflon septum presents further problems since many adhesives simply do not work well with silicone rubber. In addition, of those adhesives compatible with silicone rubber, many are thermoplastic adhesives which will not withstand common cleaning methods, such as those specified by the EPA cleaning standards. Other attempts to solve this problem have included curing of the silicone elastomer and a primer directly upon the surface of a polyolefin sheet. For example, in U.S. Patent No. 4,499,148 issued to Goodale et al. a thin film of polyolefin is corona discharge treated whereupon the uncured silicone is placed together with a primer therebetween. Pressure is then applied to force the materials together and then heat is applied in order to cure the silicone elastomer, thereby bonding the silicone elastomer to the polyolefin sheet as part of the curing process. Thereafter, circular sections of the polyolefin/silicone elastomer laminate are formed and inserted within a polyolefin cap having an aperture in the top. The polyolefin layer of the polyolefin/silicone elastomer laminate is then welded to the interior of the polyolefin cap by ultrasonic welding. However, this process taught in Goodale '148, as well as the resulting cap, suffers significant drawbacks. Often open top caps leave only a narrow flange, commonly about 3.8 mm or less, on the inside of the cap. Directing the welding energy onto such a narrow surface makes it difficult to consistently obtain a strong bond between the two polyolefin surfaces. Another drawback arises from the use of a polyolefin/silicone elastomer laminate, as opposed to a silicone elastomer alone. The inelasticity of the polyolefin layer makes penetration with a needle difficult and often causes the needle to bend or break, thereby creating significant health and safety concerns and interfering with the use of automatic sampling equipment. However, simply using a thinner polypropylene film in order to decrease the difficulty experienced with inserting the needle causes an increase in welding problems and is not a viable alternative. Therefore, there exists a need for a cap having an inert elastomer bonded directly to the interior of the cap without the use of adhesives or thin layers of plastic. There further exists a need for such a cap which is capable of withstanding the cleaning procedures required by standard scientific and medical sampling techniques. There likewise exists a need for a cap which will prevent pockets of trapped fluid or air from forming during sampling and cleaning procedures. Moreover, there exists a need for a cap which when utilized to hold medical or scientific samples will not contaminate such samples, allow leakage of such samples or allow the formation of air bubbles within the container. In addition, there exists a need for a method for forming a durable and water resistant bond between inert elastomers, such as silicone rubber, and other materials commonly used in caps and vials. Furthermore, there likewise exists a need for a method for making a durable cap with a septum bonced thereto having the characteristics discussed above. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a top view of a screw cap having an open top and septum. Fig. la is a cross-sectional side view of the screw cap of fig. 1 taken at A-A 1 . DESCRIPTION OF THE INVENTION The present invention encompasses a method of bonding an elastomer to a plastic or metal comprising ionizing a surface upon the elastomer thereby forming a first activated area; ionizing a surface upon the plastic thereby forming a second activated area; placing the first and second activated areas in contact with one another and applying pressure thereto thereby forming a direct bond between the elastomer and the plastic. The present invention also encompasses a sealing element comprising a plastic cap having an opening therein which is defined by a flange; a septum in direct physical contact with the interior of said flange thereby occluding the opening within the cap and whereby there is no layer of material between the septum and the flange; and wherein the septum comprises an elastomer. The plastic may be treated with a flame, corona or plasma discharge as well as by radiation or high intensity UV light. This treatment ionizes the surface of the material intended to be bonded with the rubber. As used throughout, the term plastic refers to both ther osetting and thermoplastic materials, examples being phenolics and polyolefines. Preferably, the surface area of the plastic intended to be bonded with the elastomer is ionized by exposure to a corona electrode having approximately 0.3 to 0.7 milliamps of current passing therethrough at a distance of approximately 2.5 cm or less from the plastic's surface, for less than a second. The elastomer may be shaped to the desired form, although preferably the surface to be bonded is substantially flat such that it will lie flush upon the plastic. Examples of elastomers include, but are not limited to, silicone rubber, SBR rubber, butyl rubber and viton rubber. The surface of the elastomer intended to be bonded with the plastic may similarly be ionized by treating the surface of the rubber with flame, corona or plasma discharge as well as by ionizing radiation or with high intensity UV light. When utilizing a corona discharge electrode at 0.3 to 0.4 milliamps current, the preferred treatment takes less than a second with the electrode approximately 2.5 cm from the surface of the elastomer. Preferably the electrode is placed from about 6 mm to about 38 mm from the surface to be treated. As soon as possible after the corona treatment of the elastomer surface, the activated area of the elastomer may be placed in contact with the activated surface of the plastic. Pressure in the amount of approximately 3.5 kg/cm 2 may be applied at the areas in contact for 1 to 2 minutes thereby achieving a bond between the two materials. Optional surface treatments may be applied to the plastic after ionization of the surface, and before contact, in order to enhance the resulting bond. Examples of such surface treatments or primers include silane coupling agents and reactive silanes. The use of these materials to modify adhesive bonding is discussed in "Silane Coupling Agents" by E.P. Pluedde ann, Q.D.412 S6P5 1982 ISBN 0-306-40957-7. However, this work covers the use of such agents in bonding of inorganic materials, such as glass fibers, in a matrix of thermoset or uncured resin. A preferred primer includes approximately 1/4 - 2% isopropanol solution of an aminosilane of formula: (CH 3 0) 3 Si(CH 2 ) 3 NHCH 2 CH 2 NH 2 or N-(2-aminoethyl) -3-aminopropyltrimethoxysilane It is believed that the primer enhances the bond strength and increases the time allowed for bonding after ionization of the surface. Utilization of the primer is preferred when more than 1 hour will elapse between ionization of the plastic and contact with the activated surface of the elastomer. It is believed that the silane occupies the reactive sites on the surface of the plastic and provides a more stable reactive species for later reaction with the surface of the activated elastomer. Similarly, it is also an option to apply heat at about 120°C while pressure is applied to the activated surface of the elastomer and the activated surface of the plastic or other material. Application of heat is not necessary when the activated elastomer and activated plastic material are brought into pressurized contact immediately after treatment. However, application of heat during the pressurized contact is preferred, particularly when a significant delay is experienced between ionization and pressurized contact. In addition, the method described above may be utilized to bond elastomers to other materials, examples being metals, such as aluminum. However, when bonding the elastomers to materials such as metals it is unnecessary to treat the metal surface to form an activated area. After treatment of the elastomer, the active area of the elastomer may be bonded directly to a metal surface previously wetted with a primer such as a silane coupling agent. As used throughout, the term cap refers to a device capable of encapsulating or sealing an opening of a container. The caps may form a seal with the containers by means well known in the art, examples include screw caps/threaded caps, snap-on caps, crimp caps, as well as other means known in the art for attaching a cap to a container. Example 1 A 24 mm 24-400 polypropylene cap 10 (as seen in reference to figs. 1 and la) having a 14mm hole 12 in the top defined by a flange 14 (having a 3.8mm inch flange 15 on the inside portion of the cap) is provided. A thin layer of Teflon 21 is bonded to a sheet of silicone rubber 22 by standard means, such as pressing and curing the rubber upon an etched and primed Teflon film. Sections of the silicone rubber/Teflon laminate are cut in order to form a septum 20, which is sized to tightly fit within the interior of the cap 10, having a diameter of approximately 22mm. The interior portion of the flange 15 of the cap is treated by corona discharge treatment by an electrode having approximately 0.3 to 0.7 milliamps at a distance of approximately 2.5 cm from the electrode for approximately 3/4 of a second. A 1% solution of a inosilane of formula N-(2-aminoethyl) -3-aminopropyltrimethoxysilane in isopropanol is applied to the inner surface of the cap's flange 15 and air dried. The septum 20 is then treated on the surface of the silicone rubber 22 by corona discharge treatment employing a corona electrode, having 0.3 to 0.4 milliamps of current, 2.5 cm from the surface for approximately 3/4 second. The treated septum 20 is then immediately inserted into the cap 10 and approximately 3.5 kg/cm 2 (about 50 psi) is applied to the septum 20 from its opposite face (the side having the Teflon layer 20) and heated to about 120°C. The pressure is removed and the cap 10 is allowed to cool to room temperature whereupon the septum 20 is bonded directly to the interior flange 15 of the polypropylene open top cap 10, which fully occludes the aperture 12 of the cap 10 and creates a durable liquid tight seal. Example 2 Wetting the interior surface of an aluminum crimp cap, such as used on analytical vials and injectable drugs and which has a hole in the top, with 1% silane coupling agent and allowing the same to air dry. A natural rubber/F.E.P. laminate, which may be sized to comprise a septum, may be treated on the natural rubber surface with corona discharge treatment by an electrode having 0.3 to 0.7 milliamps at a distance of about 1 inch for approximately 3/4 of a second. The activated area of the elastomer and the aluminum are pressed together under 3.5 kg/cm 2 and at a temperature of about 120°C to form a bond therebetween. Example 3 The interior surface of the flange of a phenolic thermoset open top cap, such as those used for autoclavable bottles for growth media, is treated by corona discharge treatment by an electrode having approximately 0.3 to 0.7 milliamps at a distance of approximately 2.5 cm from the electrode for approximately 3/4 of a second. The interior surface of the cap is then wetted with a 1% solution of N-(2- aminoethyl) -3-aminopropyltrimethoxysilane in isopropanol and allowed to dry. Sections of the silicone rubber/Teflon laminate may be cut in order to form a septum sized to tightly fit within the interior of the cap. The septum is then treated on the silicone rubber surface by corona discharge treatment employing a corona electrode, having 0.3 to 0.4 milliamps of current, 2.5 cm from the surface for approximately 3/4 second. The treated septum is then immediately inserted into the cap and approximately 3.5 kg/cm 2 (about 50 psi) is applied to the septum from its opposite face (the side having the Teflon layer) and heated to about 120°C. The pressure is removed and the cap is allowed to cool to room temperature whereupon the silicone rubber septum is bonded directly to the flange of the phenolic plastic cap, which fully occludes the aperture of the cap and creates a durable liquid tight seal. While the present invention has been particularly shown and described with reference to preferred embodiments thereof, it will be understood to those skilled in the art that various changes in form and details may be made therein without departing from the spirit and the scope of the invention.

Claims: What is claimed is: 1. A method of bonding a cured elastomer to a plastic, comprising: ionizing a surface upon said cured elastomer, thereby forming a first activated area; ionizing a surface upon said plastic, thereby forming a second activated area; placing said first activated area in contact with said second activated area; applying pressure to the first and second activated areas in contact thereby forming a bond directly between said elastomer and said plastic. 2. A method of claim 1 wherein said first and second activated areas are placed in contact immediately after formation of said first activated area. 3. A method of claim 1 further comprising: adding a primer to said second activated area prior to placing said first and second activated areas in contact. 4. A method of claim 4 further comprising: drying said second activated area after adding said primer and prior to placing said first and second activated areas in contact. 5. A method of claim 3 wherein said primer comprises approximately a 1% solution of an aminosilane. 6. A method of claim 6 wherein said aminosilane is selected from the group of: ( CH 3 0 ) 3 Si ( CH 2 ) 3 NHCH 2 CH 2 NH 2 or N-(2-aminoethyl)-3-aminopropyltrimethoxysilane 7. A method of claim 1 wherein ionization of said elastomer and said plastic is achieved by treatment selected from the group of flame, corona or plasma discharge treatment. 8. A method of claim 8 wherein said ionization is achieved by exposing said elastomer and said plastic to a corona discharge electrode. 9. A method of claim 1 wherein said first and second activated areas are placed in contact under a pressure of approximately 3.5 kg/cm 2 . 10. A method of claim 10 wherein heat is applied to said first and second activated areas placed in contact during said application of pressure. 11. A method of claim 1 wherein said plastic comprises a polyolefin. 12. A method of claim 1 wherein said plastic comprises a phenolic plastic. 13. A method of claim 1 wherein said plastic comprises a derivative of urea compounds. 14. A method of claim 1 wherein said elastomer comprises a rubber. 15. A method of claim 14 wherein said rubber comprises silicone rubber. 16. A sealing element comprising: a plastic cap having an opening therein, the opening of said cap being defined by a flange; a septum in direct physical contact with the interior of said flange thereby occluding the opening in said cap and whereby there is no layer of material between said septum and said flange; said septum comprising an elastomer. 17. The sealing element of claim 16 wherein said plastic comprises polyolefin. 18. The sealing element of claim 16 wherein said elastomer comprises silicone rubber. 19. The sealing element of claim 18 wherein said septum further comprises a layer of polytetrafluoroethylene opposite the side of the septum in direct physical contact with the interior of said flange. 20. The sealing element of claim 16 wherein the septum has a substantially concave shape extending away from said flange. 21. A sellable container, comprising: - a container; a plastic cap adapted to releasably attach to said container wherein a liquid-tight seal is formed when the cap is attached to the container; said plastic cap having an opening therein defined by a flange; said cap having a septum in direct physical contact with the interior of said flange thereby occluding the opening in said cap whereby there is no layer of material between said septum and said flange; said septum comprising an elastomer. 22. A sealing element comprising: a metal cap having an opening therein, the opening of said cap being defined by a flange; a septum in direct physical contact with the interior of said flange thereby occluding the opening in said cap and whereby there is no layer of material between said septum and said flange; said septum comprises an elastomer. 23. The method of claim 22 wherein said metal comprises aluminum. 24. The method of claim 22 wherein said cap is a crimp cap. 25. A method of bonding a cured elastomer to a metal surface, comprising: wetting said metal with an aminosilane coupling agent; ionizing a surface upon said cured elastomer, thereby forming a first activated area; placing said first activated area in contact with said metal surface; applying pressure and heat to the areas in contact, thereby forming a bond directly between said elastomer and said metal. 26. The method of claim 25 wherein said metal is aluminum and said elastomer is selected from the group of silicone rubber, styrene butadiene rubber, butyl rubber, natural rubber and viton rubber.

Inventors: DELANRY WILLIAM R, GEE ALAN R, PETROSINO PAUL M, DELANRY, WILLIAM, R., GEE, ALAN, R., PETROSINO, PAUL, M.
Applicants: INTEGRATED LINER TECHNOLOGIES, INTEGRATED LINER TECHNOLOGIES, INC.
Application year: 1995
Main classification: B65D39
IPC codes: B29C59, B29C65, B32B7, B32B25, B65D39, B65D51, C08J5, C08J7