Method for manufacturing electric-resistance-welded steel pipe

Abstract: A method for manufacturing an electric-resistance-welded steel pipe, comprises the steps of; (a) preparing a hot-rolled steel sheet consisting essentially of 0.005 to 0.2 wt.% C, 0.1 to 0.35 wt.% Si, 0.5 to 2 wt.% Mn, 0.01 wt.% or less P, 0.003 wt.% or less S, 0.001 to 0.1 wt.% Nb, and 0.001 to 0.006 wt.% Ca; (b) forming continuously an open pipe from the hot-rolled steel sheet using a multi-stage forming rolls; (c) heating both edges of the open pipe facing each other using electric resistance; and (d) pressure-welding both of the edges which were heated by electric resistance by applying irradiation of laser beam while controlling the upset using a set of squeezing rolls.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing an electric-resistance-welded steel pipe which is used under a wet hydrogen sulfide environment. 2. Description of the Related Arts Steel pipes which transfer petroleum and natural gas including hydrogen sulfide likely generate hydrogen-induced cracking (hereinafter referred to simply as "HIC") and sulfide stress corrosion cracking (hereinafter referred to simply as "SSCC"). The presumable mechanism of HIC generation is that, under an environment with the presence of hydrogen sulfide, hydrogen generated by the corrosion of steel surface becomes hydrogen atoms, which atoms easily penetrate into the steel body, and the atomic hydrogen generates bubbles in the vicinity of non-metallic inclusion in the steel, and that the pressure of generated bubbles induces cracks. The cracks further propagate through the non-uniform region such as segregated zone and ferrite-pearite interface to develop a large crack. Examined Japanese Patent Publication No. 57-16184 discloses a steel material having a good HIC resistance property which is used for a pipeline. The steel material consists essentially of 0.03 to 0.20 wt.% C, 0.01 to 0.50 wt.% Si, 0.03 wt.% or less P, 0.002 to 0.005 S, 0.01 to 0.10 wt.% Al, more than 1.2 wt.% and 2 wt.% or less Mn, oxygen which is inevitably contained in the steel material, 50 ppm or less Ca which is added in accordance with oxygen content [% O] and sulfur content [% S], and the balance being Fe and inevitable impurities. The oxygen content [% O], the sulfur content [% S] and the Ca content [% Ca] satisfy the following equation; [% Ca] x { 1 - 97 [% O] } / [% S] ≥ 1.0 Steel slab cast by continuous casting process or steel ingot of 400 mm or more in thickness, which has above-mentioned composition, is subjected to rolling. In this prior art, the shape control of inclusion by Ca addition prevents the inclusion becoming the starting point of cracks. On the other hand, SSCC is a cracking that occurs during the stress application, and the phenomenon differs from the mechanism of HIC. Both types of cracking are, however, common in that the hydrogen entered into the steel triggers the cracks from the point of non-metallic inclusion. Accordingly, reduction of non-metallic inclusion improves the SSCC resistance. For the hot-rolled steel sheet as the base material of electric-resistance-welded steel pipe, both the resistance to HIC and the resistance to SSCC are necessary to be improved by the above-described countermeasures. The characteristics of electric-resistance-welded steel pipe are, however, not improved solely by the improvement of base material. The presumable reason is that inclusion consisting mainly of fine oxide exists on a joining face at the electroseaming section and that hydrogen concentrates to the face to bring the inclusion as the starting point of cracks. Unexamined Japanese Patent Publication No. 63-241116 discloses a method for a electric-resistance welded steel pipe having a excellent SSCC resistance property. A steel strip is prepared. The steel strip consists essentially of 0.15 to 0.35 wt.% C, 0.1 to 0.8 wt.% Si, 0.2 to 0.5 wt.% Mn, 0.2 to 0.6 wt.% Cr, 0.05 to 0.25 wt.% Mo, 0.01 to 0.06 wt.% Al, at least one element selected from 0.01 to 0.15 wt.% Zr and 0.001 to 0.15 Hf, at least one element selected from the group consisting of 0.01 to 0.15 wt.% Nb, 0.01 to 0.15 wt.% V and 0.01 to 0.15 wt.% Ti, the balance being Fe and inevitable impurities. P and S are contained as impurities. The amount of P is 0.02 wt.% or less and the amount of S is 0.005 wt.% or less. A ratio of Mo wt.% to Cr wt.%, that is, Mo (wt.%) / Cr (wt.%) is from 0.2 to 0.4. An electroseaming section of the strip is heated in a non-oxidizing atmosphere. The electroseaming section is electrically welded so that an upset or a difference between outer circumferential length of the pipe before and after welding may be from 25 to 125 % of wall thickness. Then the produced pipe is heated to a temperature of 920 to 1020 °C, quenched from the temperature and tempered. DE-A-3134532 describes a steel consisting of C ≤ 0.12%, 0,5-1,0 % Mn, 0.10 - 0,25 % Si, P ≤ 0,015 %, S ≤ 0,0020 %, Nb ≤ 0,050 % and 0,0010 - 0,0060 % Ca, the balance being iron and common impurities, and steel pipes obtained therefrom by electroseamed welding. This steel material is distinguished by a high resistance against hydrogen sulfide and acid gases containing other sulfur compounds. JP-A-05023867 discloses a manufacturing method of an electric resistance welded tube, wherein the oxygen concentration is lowered by gas shielding weld zone, the generated quantity of oxide is reduced and the weld zone in the course of high frequency heating is irradiated with a laser beam or plasma arc. Actually, however, there has not been developed a method that has an excellent shielding property and is durable for continuous operation. SUMMARY OF THE INVENTION It is an object of the present invention to provide a method for manufacturing an electric-resistance-welded steel pipe having an excellent HIC resistance property and SSCC resistance property under a wet hydrogen sulfide environment. To attain the aforementioned object, the present invention provides a method for manufacturing an electric-resistance-welded steel pipe, comprising the steps of; (a) preparing a hot-rolled steel sheet consisting of 0.005 to 0.2 wt.% C, 0.1 to 0.35 wt.% Si, 0.5 to 2 wt.% Mn, 0.01 wt.% or less P, 0.003 wt.% or less S, 0.001 to 0.1 wt.% Nb, and 0.001 to 0.006 wt.% Ca; optionally at least one element selected from the group of 0.05 to 0.5 wt.% Cu, 0.5 wt.% or less Ni, 0.5 wt.% or less Mo, 1 wt.% or less Cr, 0.001 - 0.1 wt.% V and 0.001-0,1 wt.% Ti; and the remainder being iron and inevitable impurities; (b) forming continuously an open pipe from the hot-rolled steel sheet using a multi-stage forming rolls, the open pipe having both edges which confront each other; (c) heating the both edges of the open pipe using heat by electric resistance; and (d) pressure-welding both of the edges which were heated by electric resistance by applying irradiation of laser beam and controlling the upset using a set of squeezing rolls, the upset being a difference between a coil width (mm) before pipe forming and a circumferencial length of pipe (mm), wherein the upset is controlled to bring a metal flow rise angle at electroseaming section to 45 degrees or less, the upset being from 0 to 4mm. BRIEF DESCRIPTION OF THE DRAWING FIGURE is a schematic drawing of welding simulator of Example. DESCRIPTION OF THE EMBODIMENT The reason of the limitation of the content of each component is described below. Carbon is necessary to add 0.005 wt.% or more for securing the strength of steel. From the view point of weldability and toughness, however, the upper limit is specified as 0.2 wt. %. Silicon is necessary to add 0.1 wt. % or more as a deoxidizer for steel. Excessive addition, however, results in a formation of brittle steel structure. So the upper limit is specified as 0.35 wt. %. Manganese is necessary to add 0.5 wt. % or more for securing the strength of steel. Excessive addition, however, deteriorates the toughness. So the upper limit is specified as 2 wt. %. Since P deteriorates the HIC resistance of steel, the upper limit is specified as 0.01 wt. %. Since S deteriorates the HIC resistance of steel, the upper limit is specified as 0.003 wt.%. Niobium is necessary to add 0.001 wt.% or more for securing the strength of steel. Excessive addition, however, deteriorates the toughness of steel. So the upper limit is specified as 0.1 wt.%. Calcium addition at an amount of 0.001 wt.% or more makes the shape of inclusion granule, and Ca may be added, at need, to improve the HIC resistance through the shape control. Excessive addition, however, deteriorates the toughness of steel. So the upper limit is specified as 0.006 wt.%. Copper addition at an amount of 0.05 wt.% or more prevents the diffusion of hydrogen through steel and improves the HIC resistance, it may be added at need. Excessive addition, however, deteriorates the hot-ductility of steel. So the upper limit is specified as 0.5 wt.%. Since Ni and Mo improve the HIC resistance of steel, they may be added at need. Excessive addition, however, deteriorates the SSCC resistance. So upper limit of each of them is specified as 0.5 wt.%. Chromium improves the resistance to carbon dioxide corrosion of steel. The addition of Cr above 1 wt.%, however, deteriorates the weldability of steel so that the upper limit is specified as 1 wt.%. Vanadium and Ti increase the strength of steel when each of them is added as a rate of 0.001 wt.% or more. Excessive addition, however, deteriorates the toughness of steel. So the upper limit of each of them is specified as 0.1 wt.%. That is the reason why each of the added element is limited. The working method is described in the following. The reason why the conventional method for manufacturing electric-resistance-welded steel pipe gives poorer resistance to HIC and SSCC at the electroseamed portion than that of base material is that the inclusion generated during electroseaming stage and consisting mainly of oxides and being left on the joining face is exposed on the bead face by the machining of welded bead, which exposed inclusion then becomes the starting point of hydrogen cracks. At the electroseamed section, normally a strong aggregate structure appears by upset application after heating stage. The structure is observed under a microscopic photograph of a bead section as the metal flow rise. That type of structure is a cause of deterioration in the mechanical properties of the electric-resistance-welded steel pipe, and the structure is also not desirable from the standpoint of SSCC resistance. Nevertheless, prior art unavoidably applies a strong upset to discharge the oxides which were generated on the joining face. As a result, a strong aggregate structure occurred in the prior art. The upset is defined as follows. Upset (mm) = Coil width (mm) before pipe forming - Circumferencial length of pipe (mm) In addition to the conventional application of electrical heating, the irradiation of laser beam fuses the oxides generated on the joining face and finely disperses the fused oxides to avoid providing a starting point of the crack. Consequently, the HIC resistance and SSCC resistance are improved. In the present invention, no increased upset is necessary. By reducing the upset degree to prevent the generation of agglomerated structure specific to the electroseamed steel pipe, the mechanical properties and SSCC resistance at the electroseamed section are improved. The metal flow rise angle is an index of the aggregated structure at the electroseamed section. If the angle exceeds 45 degree, the deterioration of SSCC resistance at the electroseamed section becomes significant. Therefore, the angle is selected at 45 degrees or less. According to the present invention, the hot-rolled steel sheet having composition described before is subjected to laser beam irradiation immediately before squeezing by squeezing rolls in a conventional facility for manufacturing the electroseamed steel pipes, and to compression welding thereof. EXAMPLE Steels having chemical composition listed in Table 1 were melted in vacuum in a laboratory equipment to cast 50 kg ingots. Each of the ingot was heated to 1200 °C and rolled to form a sheet having 50 mm thickness, then the sheet was cooled by air. The sheet types A through E in Table 1 have the composition within the range of the present invention. The sheet type F does not include Ca and the composition is outside of the range of the present invention. A strip of 50 x 150 x 400 mm was cut from each of the sheet, which strip was rolled to a thickness of 12 mm by heating up to 1200 °C, and to 820 °C of end point. Immediately after the rolling, a mist spray was applied to cool the rolled sheet to 550 °C at a cooling rate of about 10 °C/sec. Then the sheet was inserted into a furnace which was heated to 550 °C in advance for cooling thereof. The procedure was a simulated pattern of actual hot-rolling process. A specimen having a size of 12 x 35 x 2000 mm was cut from each of the sheet which was cooled to room temperature. The specimen was welded by an electroseaming simulator. The simulator is illustrated in FIGURE. Two steel sheets 1 are fed to multistage forming rolls, and the steel sheet edges facing each other are heated by resistance induced by high frequency current supplied from the contact chip 2. Then the edges are processed by compression welding using the squeezing rolls 3. The simulator further enables to irradiate carbon dioxide gas laser beam 4 to the edge joining section. The welding conditions were 10 m/min. of welding speed, 700 kW of applied power supplied from the contact chip, and 0 to 4 mm of variable upset. The laser output was 5 kW, and the beam diameter at focusing point was 0.5 mm. The irradiation was conducted from vertical upward of the steel sheet while focusing on the edge joining point. The HIC test was applied at the welded section and the base material. The test was conducted in accordance with NACE TM0284-87 except for a change of test solution. The specimen was cut along the welded direction with a size of 10 x 20 x 100 mm. The whole surface of the specimen was wet-polished to #320. The test solution was 5% NaCl + 0.5% CH 3 COOH aqueous solution saturated with hydrogen sulfide at 1 atm. The specimen was immersed into the test solution at 25 °C for 96 hrs. Then, the specimen was cut to four equal pieces along the longitudinal direction. The three cut sections were observed for checking crack generation, and an evaluation was given by a crack sensitivity rate. The SSCC test was carried out using a tension type tester confirming to NACE TM0177-90 Method A. The specimen was a round rod tensile test specimen which was cut lateral to the welding direction, having a size of 3.81 mm of diameter at the parallel section, 25 mm of length at parallel section, and being wet-polished to #600. The specimen was applied with a specified stress in the test solution having the same composition with that used in HIC test. The applied stress level was changed to determine the minimum stress (σth) which does not generate crack during the testperiod of 720 hrs. The SSCC resistance was evaluated from a ratio of σth to σys, where σys is the yield stress obtained by a tensile test in air. The test result is given in Table 2. The table shows that the electroseamed steel pipes produced from the steels having the composition range of the present invention and formed under the laser beam irradiation give a favorable crack sensitivity rate (CSR) and a good ratio of the minimum stress (σth) to the yield stress (σys), (σth/σys). Furthermore, for the case of metal flow rise angle of 45 degree or less, these figures become more preferable level. Steel tested Laser irradiation Upset (mm) Metal flow rise angle CRS (%) σth /σys (%) Remark A not applied 2.1 65° 8.0 50 Comparative Example A applied 0.4 2° 1.5 75 Example A applied 1.9 42° 1.0 75 Example A applied 2.3 55° 1.5 75 Comparative Example A applied 3.2 67° 1.5 75 Comparative Example B not applied 1.2 43° 9.5 60 Comparative Example B applied 0.6 5° 1.5 80 Example B applied 1.3 18° 1.5 80 Example B applied 2.0 48° 2.0 80 Comparative Example C not applied 1.5 50° 15.0 50 Comparative Example C applied 0.3 0° 3.0 70 Example C applied 1.8 40° 3.5 70 Example C applied 4.2 82° 4.5 70 Comparative Example D not applied 1.6 44° 8.5 50 Comparative Example D applied 1.6 40° 2.0 75 Example E not applied 2.0 51° 10.0 55 Comparative Example E applied 2.0 48° 2.5 75 Comparative Example F not applied 1.8 47° 25.5 45 Comparative Example F applied 1.8 44° 18.5 55 Comparative Example

Claims: A method for manufacturing an electric-resistance-welded steel pipe, comprising the steps of; (a) preparing a hot-rolled steel sheet consisting of 0.005 to 0.2 wt.% C, 0.1 to 0.35 wt.% Si, 0.5 to 2 wt.% Mn, 0.01 wt.% or less P, 0.003 wt.% or less S, 0.001 to 0.1 wt.% Nb, and 0.001 to 0.006 wt.% Ca; optionally at least one element selected from the group of 0.05 to 0.5 wt.% Cu, 0.5 wt.% or less Ni, 0.5 wt.% or less Mo, 1 wt.% or less Cr, 0.001 - 0.1 wt.% V and 0.001-0,1 wt.% Ti; and the remainder being iron and inevitable impurities; (b) forming continuously an open pipe from the hot-rolled steel sheet using a multi-stage forming rolls, the open pipe having both edges which confront each other; (c) heating the both edges of the open pipe using heat by electric resistance; and (d) pressure-welding both of the edges which were heated by electric resistance by applying irradiation of laser beam and controlling the upset using a set of squeezing rolls, the upset being a difference between a coil width (mm) before pipe forming and a circumferencial length of pipe (mm), wherein the upset is controlled to bring a metal flow rise angle at electroseaming section to 45 degrees or less, the upset being from 0 to 4mm.

Inventors: ISHIZAWA YOSHIICHI, NAGAHAMA YUTAKA, ODAKE TAKAYUKI, TAKAMURA TOSHIHIRO, ISHIZAWA, YOSHIICHI                            T., NAGAHAMA, YUTAKA                               T., ODAKE, TAKAYUKI                                ., TAKAMURA, TOSHIHIRO                            T., Ishizawa, Yoshiichi, c/o Intellect.Property Dept., Nagahama, Yutaka, c/o Intellectual Property Dept., Odake, Takayuki, c/o Intellectual Property Dept., Takamura, Toshihiro, c/o Intellect.Property Dept.
Applicants: NIPPON KOKAN KK, NKK CORPORATION
Application year: 1995
Main classification: C22C38
IPC codes: B21D5, B23K26, C22C38, B21C37, B23K11