POLYMERIZATION OF CYCLIC ETHERS USING SELECTED METAL COMPOUND CATALYSTS

Abstract: A process for polymerizing oxiranes, oxetanes, oxepanes, dioxolanes, trioxanes, and tetrahydrofurans to their respective polymers by contacting them with a selected metal compound and an accelerator which is a selected vinyl ester or a selected phosphorous compounds.

Description: TITLE POLYMERIZATION OF CYCLIC ETHERS USING SELECTED METAL COMPOUND CATALYSTS FIELD OF THE INVENTION This invention concerns the polymerization of oxiranes, oxetanes, oxepanes, 1,3-dioxolanes, 1,3,5-trioranes, and tetrahydrofurans to linear polyethers catalyzed by selected metal compounds together with selected accelerators. BACKGROUND OF THE INVENTION Cyclic ethers are polymerized by various means to give products of widespread utility. For instance, ethylene oxide is polymerized to polyethylene oxide which is useful, in lower molecular weight grades, for ceramics (as a binder), cosmetics, lubricants, polyurethanes; and in higher molecular weight grades, for packaging film, denture adhesives, lubricants, flocculation and for other articles and products. Tetrahydrofuran (THF) is polymerized to poly(tetra- methylene ether) glycol which is useful in the preparation of Spandex fibers; polyurethane resins which are useful in elasto eric parts; and thermoplastic elastomers which are useful for molding various mechanical parts. Therefore, improved methods of making these polymers are sought. U.S. Patent 3,842,019 describes the polymerization of oxiranes and other small ring compounds by a presumed cationic mechanism, using as the catalyst the decomposition products of metal perfluoroalkyl- sulfonates. These catalysts are described as "latent", that is no reaction occurs until the metal salt is decomposed. The reactions reported are relatively slow, even at elevated temperatures. U.S. Patents 5,084,586 and 5,124,417 describe the cationic polymerization of various monomers, including cyclic ethers, using onium cations, whose corresponding anions are fluororalkylsulfatometallates. Onium ion catalyzed cationic polymerizations are known, and there is no mention in these patents of the use of metal salts not containing onium ions, such as metal triflates, as catalysts for the polymerization of cyclic ethers. J. S. Hrkach, et al., Macromolecules, vol. 23, p. 4042-4046 (1990) describe the polymerization of tetrahydrofuran using trimethylsilyl trifluoromethane- sulfonate as the initiator. No mention is made of any other triflates as catalysts for this polymerization. G. A. Olah, et al., J. Appl . Polym. Sci., Vol. 45, 1355-1360 (1992) describe the use of boron, aluminum and gallium tristriflate to catalyze the polymerization of THF. S. L. Borkowsky, et al. , Organometal., Vol. 10, p. 1268-1274 (1991) report that certain zirconium complexes can initiate the polymerization of tetrahydrofuran. No mention is made of zirconium perfluoroalkylsulfonates, or of copolymers. I. Yamashita, et al., Kogyo Kagaku Zasshi, vol. 71, p. 1061-1064 (1968) describes the polymerization of tetrahydrofuran using a catalyst system consisting of a Lewis acid such as ferric chloride and a phosphorous compound such as triphenyl phosphite. The use of metal perfluoroalkylsulfonates is not mentioned. SUMMARY OF THE INVENTION This invention concerns a process for the polymerization of cyclic ethers, comprising, contacting one or more oxiranes, oxetanes, tetrahydrofurans, oxepanes, 1,3-dioxolanes or 1,3,5-trioxanes with a compound of the formula MZ s -Qt, and an accelerator which is a compound of the formula (R 3 O) 3 P, R 3 2 P-Xor wherein: R 1 is hydrogen, hydrocarbyl or substituted hydrocarbyl; R 2 is hydrogen, hydrocarbyl or substituted hydrocarbyl; each R 3 is independently hydrocarbyl or substituted hydrocarbyl; each X is independently chlorine, bromine or iodine; M is a metal selected from the group consisting of strontium, barium, scandium, yttrium, the rare earth metals, titanium, zirconium, hafnium, chromium, molybdenum, tantalum, rhenium, iron, cobalt, vanadium, niobium, tungsten, ruthenium, osmium, rhodium, iridium, palladium, platinum, silver, gold, zinc, cadmium, mercury, aluminum, gallium, indium, thulium, germanium, tin, lead, arsenic, antimony and bismuth; at least one of Z is an anion of the formula "SO3R 5 , wherein R 5 is perfluoroalkyl containing 1 to 12 carbon atoms or part of a fluorinated polymer wherein the carbon atoms alpha and beta to the sulfonate group are together bonded to at least four fluorine atoms, or tetraphenylborate, and the remainder of Z is oxo or one or more monovalent anions; s is 1 when M is silver; s is 2 when M is strontium, barium, cobalt, rhodium, iridium, palladium, platinum, chromium, zinc, cadmium or mercury; s is 3 when M is scandium, yttrium, a rare earth metal, arsenic, antimony, bismuth, gold, iron, ruthenium, osmium, aluminum, gallium, indium or thulium; s is 4 when M is titanium, zirconium, hafnium, molybdenum, germanium, tin, or lead; s is 5 when M is rhenium, vanadium, niobium or tantalum; s is 6 when M is tungsten; Q is a neutral ligand; t is 0 or an integer of 1 to 6; and provided that each oxo group present counts as two of s . DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS In the polymerization process described herein one or more cyclic ethers, oxiranes, oxetanes, 1,3-dioxo- lanes, 1,3,5-trioxanes, or tetrahydrofurans are polymerized to form a polyether. Oxirane (more commonly called epoxide) is herein given its usual structure, a saturated three membered ring containing two carbon atoms and one oxygen atom. Oxetane is also given its common meaning, a saturated four membered ring containing three carbon atoms and one oxygen atom. The term oxepane means a saturated seven membered ring containing six carbon atoms and one oxygen atoms. The term 1, 3-dioxolane means a saturated five membered ring which contains two oxygen atoms separated by 1 carbon atom. The term 1,3, 5-trioxane means a six membered ring containing 3 oxygen atoms in which the oxygen atoms and carbons atoms are alternated. All of these terms include compounds containing those ring systems which are substituted with hydrocarbyl or hydrocarbylene groups containing 1 to 20 carbon atoms. The hydrocarbylene groups may form carbocyclic rings, which include bicyclic, tricyclic, etc., systems. By a hydrocarbylene group herein is meant a divalent radical containing carbon and hydrogen which is part of a carbocyclic ring. Preferred cyclic ethers have the formula wherein n is 2 or 4 and each R 1 , R 2 , R 3 and R 4 is independently hydrogen or hydrocarbyl containing 1 to 20 carbon atoms. Some of these cyclic ethers polymerize to give repeat units of the formula -[CHR 1 (CR 2 R 3 ) n CHR 4 0]-. In a more preferred cyclic ether all of R 1 , R 2 , R 3 and R 4 are hydrogen. In another more preferred cyclic ether where n=2, R 1 , one of R 2 , both of R 3 and R 4 are hydrogen, and the remaining R 2 is alkyl containing 1-4 carbon atoms, especially preferably the remaining R 2 is methyl. By hydrocarbyl herein is meant a univalent radical containing carbon and hydrogen. The polymerization is run in the presence of an accelerator. Suitable accelerators include selected vinyl esters and selected phosphorous compounds. The vinyl ester accelerators have the formula O R 2 -C-O~CH=CHR 1 . In a preferred vinyl ester R 1 is hydrogen or alkyl, more preferably hydrogen or n-alkyl. In another preferred vinyl ester R 2 is alkyl, phenyl, or substituted phenyl, more preferably n-alkyl. In an especially preferred vinyl ester R 1 is hydrogen and R 2 is methyl. In the accelerators which are phosphorous compounds it is preferred if each R 3 is independently alkyl, phenyl, or substituted phenyl, more preferably n-alkyl containing 1, 2, 3 or 4 carbon atoms or phenyl. It is also preferred if X is chlorine. By substituted hydrocarbyl (or substituted in substituted phenyl) is meant that the moiety may contain inert substituents (functional groups) . By inert is meant that they don't react with any of the starting materials or products nor interfere with the polymer¬ ization. Such substituents include (linear) ether, alkyl, aryl, and halo. An important consideration in the preparation of polyethers is the number average molecular weight (Mn) of the polyether and its molecular weight distribution. When the polyether is to be used as a monomer in the preparation of another polymer (usually in the diol form) , it is often preferred that the Mn of the polyether be in the range of about 400 to about 20,000, preferably about 500 to about 5,000. The catalyst may be yttrium or a rare earth compound of the formula MZ3 where M is a trivalent ion of yttrium, or one of the rare earths, lanthanum, cerium, praeseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium. Preferred metals, M, are strontium, scandium yttrium, the rare earth metals, titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, rhenium, iron, ruthenium, palladium, copper, gold, zinc, tin and bismuth. More preferred metals are yttrium, the rare earth metals, and scandium. Especially preferred metals are yttrium, ytterbium, dysprosium, erbium, neodymium, lanthanum, and scandium. Another preferred metal is "mischmetall" (sometimes also called "didymium") , which is a mixture of rare earth metals as obtained from the ore. It is currently believed monovalent anions that are relatively nonnucleophilic are useful as Z. Examples of such anions are tetraphenylborate, ~Sθ 3 R 5 , wherein R 5 is perfluoroalkyl, or wherein R 5 is part of a fluorinated polymer wherein the carbon atoms alpha and beta to a sulfonate group are together bonded to at least 4 fluorine atoms (as in -CF 2 CF 2 SO 3 ") . It is preferred if R5 is perfluoroalkyl. In a particularly preferred embodiment, R 5 is trifluoromethyl, and the anion is herein called "triflate". Generally speaking, any metallic compound in which the correct metal in the correct oxidation state (see above) is present and bonded to a triflate or similar anion will be a catalyst. Such a compound must of course be reasonably stable during the polymerization or decompose to another compound which is still a triflate (or similar anion) compound of the metal in the correct oxidation state. It has been found that, in general, the greater the number of triflate groups bonded to the metal cation, the more active the metal compound will be as a catalyst. It is preferred if half or more of the anions (Z) bound to each metal cation is triflate or a similar anion. The metal catalysts may optionally contain one or more neutral ligands coordinated to the metal. By a neutral ligand is meant a neutral compound that can coordinate with the catalysts, usually the metal cation. Neutral ligands include water, and ethers such as dimethyl ether and tetrahydrofuran. The metals catalysts may contain other anions than triflate and similar anions, and tetrafluoroborate, although at least one of triflate or tetrafluoroborate anions must be present. Some other useful anions are alkoxide, particularly lower alkoxide containing 1-4 carbon atoms, acetylacetonate, cyclopentadieneide, pentamethylcyclopentadieneide, t-butylacetylacetonate, and halide. It is preferred if all of the anions are triflate. In general, the higher the molar ratio of metal compound to cyclic ether monomer originally present, the lower the molecular weight of the resulting polyether will be. Similarly, the higher the ratio of accelerator (if present) to monomer originally present, the lower the molecular weight of the polyether will be. It is currently believed that the effects of these two ratios are cumulative. The polymerization may be run at a temperature of about -80°C to about 130°C. If this temperature is above the boiling point of the cyclic ether monomer, a pressure vessel may be used. A preferred temperature is ambient to the boiling point of the monomer, or 110°C, whichever is lower. An inert solvent such as di-n-butyl ether, diethyl ether or toluene may be used, but it is preferred if solvents are not present. Protic compounds such as water, methanol and ethanol should preferably not be present, and it is convenient to exclude them by drying the starting materials and keeping the process under an inert dry gas such as nitrogen. As in most chemical processes, the ingredients should be mixed at least initially. Continued agitation is preferred to assure that the process materials remain well mixed, and to avoid overheating. The polymerization is mildly exothermic. If the polymerization temperature goes up appreciably, refluxing of the monomer may be used to help cool the process. The polymerization process can be performed in a variety of ways known to those skilled in the art. It can be done by batch, semi-batch and continuous processes. Continuous processes include continuous stirred tank reactor(s) with one or more stages, and/or plug flow reactors. Other variations will be evident to those skilled in this art. In the polymerization process disclosed herein the catalyst may be recovered and reused. It may be recovered from the polymerization process by extracting the polymer formed with water. The recovered catalyst may be used again in the polymerization. The aqueous washings may be concentrated by removal of the water (as by evaporation) and the solid catalyst recovered. EXAMPLES In the following non-limiting Examples, the following abbreviations are used: GPC - gel permeation chromatography Mn - number average molecular weight Mw - weight average molecular weight PD - polydispersity, Mw/Mn PS - polystyrene RB - round-bottomed STD - standard THF - tetrahydrofuran EXAMPLE 1 Polymerization of THF with Diethvl Chlorophosphite and Ytterbium Triflate In a dry box, ytterbium triflate (2.00 g) was weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF (20.0 mL) and diethyl chlorophos¬ phite (1.00 mL) were added. After 17 hours the polymerization was terminated via the addition of water. THF and ether. The resulting organic phase was separated, concentrated at reduced pressure and then dried under vacuum affording 12.63 g of polymer. GPC analysis (PS STD.): Mn = 10200, Mw = 20100, PD = 1.96. EXAMPLE 2 Polymerization of THF with Diphenylphosphinic Acid and Ytterbium Triflate In a dry box, ytterbium triflate (2.00 g) and diphenylphosphinic acid (1.00 g) were weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF (20.0 mL) was added. After 17 hours the polymerization was terminated via the addition of water, THF and ether. The resulting white mixture was filtered through Celite. The resulting filtrate was washed with water, concentrated at reduced pressure and dried under vacuum affording 8.22 g of polymer. GPC analysis (PS STD.): Mn = 50900, Mw = 112000, PD = 2.21. EXAMPLE 3 Polymerization of THF with Diethvl Chlornphosphite and Erbium Triflate In a dry box, erbium triflate (2.00 g) was weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF (20.0 mL) and diethyl chlorophos- phite (2.00 mL) were added. After 17 hours the polymerization was terminated via the addition of water, THF and ether. The separated organic phase was again washed with water. The organic phase was concentrated at reduced pressure and then dried under vacuum affording 9.68 g of polymer. GPC analysis (PS STD.): Mn = 10800, Mw - 19600, PD = 1.82. EXAMPLE 4 Polymerization of THF with Diethyl Chlorophosphite and Neodvnium Triflate In a dry box, neodynium triflate (2.00 g) was weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF <20.0 mL) and diethyl chlorophos- phite (2.00 mL) were added. After 17 hours the polymerization was terminated via the addition of water, THF and ether. The separated organic phase was again washed with water. The organic phase was concentrated at reduced pressure and then dried under vacuum affording 4.73 g of polymer. GPC analysis (PS STD.): Mn - 12200, Mw = 22600, PD - 1.85. EXAMPLE S Polymerization of THF with Diethyl Chlorophosphite and Dysprosium Triflate In a dry box, dysprosium triflate (2.00 g) was weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF (20.0 mL) and diethyl chlorophos¬ phite (2.00 mL) were added. After 17 hours the polymerization was terminated via the addition of water, THF and ether. The separated organic phase was again washed with water. The organic phase was concentrated at reduced pressure and then dried under vacuum affording 9.80 g of polymer. GPC analysis (PS STD.): Mn - 14100, Mw = 27900, PD = 1.98. EXAMPLE 6 Polymerization of THF with Diethyl Chlorophosphite and Tin Triflate In a dry box, tin triflate (2.00 g) was weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF (20.0 mL) and diethyl chlorophos¬ phite (2.00 mL) were added. After 17 hours the polymerization was terminated via the addition of water, THF and ether. The separated organic phase was again washed with water. The organic phase was concentrated at reduced pressure and then dried under vacuum affording 14.93 g of polymer. GPC analysis (PS STD.): Mn = 2680, Mw = 5520, PD = 2.06. EXAMPLE 7 Polymerization of THF with Diethyl Chlorophosphite and Bismuth Triflate In a dry box, bismuth triflate (2.00 g) was weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF (20.0 mL) and diethyl chlorophos¬ phite (2.00 mL) were added. After 17 hours the polymerization was terminated via the addition of water, THF and ether. The separated organic phase was again washed with water. The organic phase was concentrated at reduced pressure and then dried under vacuum affording 7.99 g of polymer. GPC analysis (PS STD.): Mn = 3050, Mw = 6600, PD - 2.16. EXAMPLE 8 Polymerization of THF with Diethvl Chlorophosphite and Lanthanum Triflate In a dry box, lanthanum triflate (2.00 g) was weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF (20.0 mL) and diethyl chlorophos¬ phite (2.00 mL) were added. After 15 hours the polymerization was terminated via the addition of water, THF and ether. The separated organic phase was again washed with water. The organic phase was concentrated at reduced pressure and then dried under vacuum affording 7.03 g of polymer. GPC analysis (PS STD.): Mn = 14500, Mw = 30300, PD = 2.08. EXAMPLE 10. Polymerization of THF with Phosphonitrilic Trimer and Ytterbium Triflate In a dry box, ytterbium triflate (2.00 g) and phosphonitrilic trimer (1.00 g) were weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF (20.0 mL) was added. After 16 hours the polymerization was terminated via the addition of water, THF and ether. The separated organic phase was again washed with water. The organic phase was concentrated at reduced pressure and then dried under vacuum affording 7.78 g of polymer. GPC analysis (PS STD.): Mn = 6710, Mw = 28500, PD - 4.25. EXAMPLE 11 Polymerization of THF with Vinvl Acetate and Ytterbium Triflate In a dry box, ytterbium triflate (2.00 g) was weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF (20.0 mL) and vinyl acetate (1.00 mL) were added. After 17 hours the polymerization was terminated via the addition of water, THF and ether. The resulting organic phase was separated, washed with water, concentrated at reduced pressure and then dried under vacuum affording 7.66 g of polymer. GPC analysis (PS STD.): Mn - 184000, Mw = 335000, PD - 1.82. EXAMPLE 12 Polymerization of THF with Vinyl 2-Ethylhexanoate and Ytterbium Triflate In a dry box, ytterbium triflate (2.00 g) was added to each of four 100 mL RB flasks equipped with stirring bars . The flasks were sealed with rubber septa and removed from the dry box. After the attachment of nitrogen bleeds THF (20.0 mL) was added to each flask. Vinyl 2-ethylhexanoate (1.0. 2.0, 3.0 and 4.0 mL) was added to each flask. After 17 hours the polymerizations were terminated via the addition of water, THF and ether. The separated organic phases were again washed with water, separated, concentrated at reduced pressure and then dried under vacuum. Polymer yields and GPC analyses: Vinyl 2-Ethyl¬ Polymer Yield Mn hexanoate (mL) (g) (PS STD.) Mw PD 1.0 1.47 435000 774000 1.78 2.0 1.85 429000 681000 1.59 3.0 2.28 410000 622000 1.52 4.0 3.07 253000 543000 2.15 EXAMPLE Polvmerization of THF with Vinvl Acetate and Bisfn- -cvcloDentadienvlltetrahvdrofuran- j .s (trifluoromethanesulfonatoi zirconium (Cp2Zr[(0 3 SCF 3 )2] (THF)) In a dry box, bis (n-cyclopentadienyl)tetrahydro- furan-bis (trifluoromethanesulfonato) zirconium (Cp2Zr[ (03SCF 3 ) 2 ] (THF) ) (2.00 g) was weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF (20.0 mL) and vinyl acetate (2.00 mL) were added. After 17 hours the polymerization was terminated via the addition of water, THF and ether. The resulting organic phase was separated, washed with water, concentrated at reduced pressure and then dried under vacuum affording 12.17 g of polymer. GPC analysis (PS STD.): Mn = 60100, Mw = 126000, PD - 2.10. EXAMPLE 14 Polymerization of THF with Vinyl Acetate and Yttrium Triflate In a dry box, yttrium triflate (2.00 g) was weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF (20.0 L) and vinyl acetate (3.00 mL) were added. After 19.5 hours the polymerization was terminated via the addition of water, THF and ether. The resulting organic phase was separated, washed with water, concentrated at reduced pressure and then dried under vacuum affording 3.15 g of polymer. GPC analysis (PS STD.): Mn = 100000, Mw = 194000, PD = 1.94. EXAMPLE 15 Polymerization of THF with Vinyl Acetate and Erbium Triflate In a dry box, erbium triflate (2.00 g) was weighed in an oven dried 100 mL RB flask equipped with a stirring bar. The flask was sealed with a rubber septum and removed from the dry box. After the attachment of a nitrogen bleed, THF (20.0 mL) and vinyl acetate (3.00 mL) were added. ' After 17 hours the polymerization was terminated via the addition of water, THF and ether. The resulting organic phase was separated, washed with water, concentrated at reduced pressure and then dried under vacuum affording 0.54 g of polymer. GPC analysis (PS STD.): Mn = 222000, Mw = 396000, PD = 1.76. Although particular embodiments of the present invention have been described in the foregoing description, it will be understood by those skilled in the art that the invention is capable of numerous modifications, substitutions and rearrangements without departing from the spirit or essential attributes of the invention. Reference should be made to the appended claims, rather than the foregoing specification, as indicating the scope of the invention.

Claims: WHAT IS CLAIMED IS: 1. A process for the polymerization of cyclic ethers, comprising, contacting one or more oxiranes, oxetanes, tetrahydrofurans, oxepanes, 1,3-dioxolanes or 1,3,5-trioxanes with a compound of the formula MZ a -Qt, and an accelerator which is a compound of the formula O O o R 2 -C-O-CH=CHR 1 , R 3 2 P-OH, R 3 2 P-X, (R 3 O) 3 P, R 3 2 P-X σr wherein: R 1 is hydrogen, hydrocarbyl or substituted hydrocarbyl; R 2 is hydrogen, hydrocarbyl or substituted hydrocarbyl; each R 3 is independently hydrocarbyl or substituted hydrocarbyl; each X is independently chlorine, bromine or iodine; M is a metal selected from the group consisting of strontium, barium, scandium, yttrium, the rare earth metals, titanium, zirconium, hafnium, chromium, molybdenum, tantalum, rhenium, iron, cobalt, vanadium, niobium, tungsten, ruthenium, osmium, rhodium, iridium, palladium, platinum, silver, gold, zinc, cadmium, mercury, aluminum, gallium, indium, thulium, germanium, tin, lead, arsenic, antimony and bismuth; at least one of Z is an anion of the formula "S0 3 R 5 , wherein R 5 is perfluoroalkyl containing 1 to 12 carbon atoms or part of a fluorinated polymer wherein the carbon atoms alpha and beta to the sulfonate group are together bonded to at least four fluorine atoms, or tetraphenylborate, and the remainder of Z is oxo or one or more monovalent anions; s is 1 when M is silver; s is 2 when M is strontium, barium, cobalt, rhodium,, iridium, palladium, platinum, chromium, zinc, cadmium or mercury; s is 3 when M is scandium, yttrium, a rare earth metal, arsenic, antimony, bismuth, gold, iron, ruthenium, osmium, aluminum, gallium, indium or thulium; s is 4 when M is titanium, zirconium, hafnium, molybdenum, germanium, tin, or lead; s is 5 when M is rhenium, vanadium, niobium or tantalum; s is 6 when M is tungsten; Q is a neutral ligand; t is 0 or an integer of 1 to 6; and provided that each oxo group present as part of Z is considered to account for two of s. 2. The process as recited in Claim 1 wherein said cyclic ether is one or more of said tetrahydrofurans, oxepanes, 1,3-dioxolanes or 1,3, 5-trioxanes. 3. The process as recited in Claim 2 wherein M is a metal selected from the group consisting of strontium, barium, scandium, yttrium, the rare earth metals, titanium, zirconium, hafnium, chromium, molybdenum, tantalum, rhenium, iron, ruthenium, osmium, rhodium, iridium, palladium, platinum, silver, gold, zinc, cadmium, mercury, germanium, tin, lead, arsenic, antimony and bismuth. 4. The process as recited in Claim 3 wherein said cyclic ether comprises the formula wherein : each R 1 , R 2 , R 3 and R 4 is independently hydrogen or hydrocarbyl containing 1 to 20 carbon atoms; and n is 2 or 4. 5. The process as recited in Claim 4 wherein n is 2 and R 1 , R 4 and all of R 2 and R 3 are hydrogen. 6. The process as recited in Claim 4 wherein n is 2 and R 1 and R 4 are each hydrogen, one of R 2 is hydrogen, the other R 2 is methyl, and both R 3 are hydrogen. 7. The process as recited in Claim 3 wherein R 5 is trifluoromethyl or perfluoroalkyl. 8. The process as recited in Claim 5 wherein M is strontium, scandium, yttrium, the rare earth metals, titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, rhenium, iron, ruthenium, palladium, copper, gold, zinc, tin, bismuth or mischmetall. 9. The process as recited in Claim 1 carried out at a temperature of about -80°C to about 130°C. 10. The process as recited in Claim 1 wherein said accelerator is a compound of the formula O R 2 -C-O-CHSCHR 1 . 11. The process as recited in Claim 10 wherein R 1 is hydrogen or alkyl, and R 2 is alkyl, phenyl, or substituted phenyl. 12. The process as recited in Claim 10 wherein R 1 is hydrogen and R 2 is methyl. 13. The process as recited in Claim 5 wherein said accelerator is O R 2 -C-O-CH=CHR 1 , and R 1 is hydrogen or alkyl, and R 2 is alkyl, phenyl, or substituted phenyl. 14. The process as recited in Claim 5 wherein said accelerator is O R2_ C _O-CH=CHR 1 , and R 1 is hydrogen and R 2 is methyl. 15. The process as recited in Claim 1 wherein said accelerator is O O R 2 P-OH, R 3 2 P-X, (R 3 O) 3 P, R 3 2 P-Xor 16. The process as recited in Claim 15 wherein each R 3 is independently alkyl, phenyl, or substituted phenyl, and X is chlorine. 17. The process as recited in Claim 15 wherein each R 3 is n-alkyl containing 1, 2, 3 or 4 carbon atoms or phenyl. 18. The process as recited in Claim 5 wherein said accelerator is O O R 2 P-OH, R 3 2 P-X, (R 3 O) 3 P, R 3 2 P-Xor and each R 3 is independently alkyl, phenyl, or substituted phenyl, and X is chlorine.

Inventors: DRYSDALE NEVILLE EVERTON, DRYSDALE, NEVILLE, EVERTON
Applicants: DU PONT, E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1995
Main classification: C08G65
IPC codes: B01J31, C08G65