Siloxane gels

Abstract: A gel suitable for use in various personal care applications is provided. The improved gel contains an amide-free gelator; a siloxane polyether for strengthening the gel and increasing its firmness, rigidity and adhesion to substrates; and a volatile methyl siloxane. Preferably, the gel includes 1 to 98.9 percent by weight of the siloxane polyether; 0.1 to 20 percent by weight of 12-hydroxystearic acid or metal salts of 12-hydroxystearic acid; and 1 to 98.9 percent by weight of a volatile methyl siloxane having a boiling point less than 250°C. and a viscosity of 0.65 to 5.0 centistokes (mm 2 /s).

Description: This invention is directed to a clear firm gel suitable for use in various personal care applications. This gel includes an amide-free gelator; a siloxane polyether for strengthening the gel and increasing its firmness, rigidity and adhesion to substrates and a methyl siloxane. Recent consumer trends have shifted in emphasis to a demand for clear products. These products range from fuels for automotive vehicles, to household and personal care products including dish washing and laundry detergents, as well as skin and hair care products in the form of lotions, solutions and gels. One is apt to find on store shelves consumer oriented products such as clear shampoos, clear sunscreens, clear bath oils, clear deodorants, clear antiperspirants and clear dentifrices. Since consumers tend to equate clarity with environmental friendliness and purity, the demand for clear products is likely to continue. It is difficult to produce a clear product. For stick type products, it is also difficult to produce a solid product with the appropriate rigidity. Not all ingredients necessary to formulate clear products lend themselves to clarity, or to firmness for that matter, particularly when they are combined with other ingredients for a successful formulated product. This is especially true in formulations found in the personal care arena. Thus, the problem sought to be solved by the present invention is the production of a gel product which is suitable for use as a base ingredient in personal care applications. This problem is solved according to our invention by combining only "certain" basic components into a formulation which meet "certain" criteria. The benefits and advantages derived from the invention are that a solid product, which is effective for use as a component in personal care products, is effectively produced that will meet consumer demands in the marketplace for clarity and rigidity. The invention provides a gel containing 1 to 98.9 percent by weight of a siloxane polyether having the formula as defined in the claim; 0.1 to 20 percent by weight of an amide-free gelator which is 12-hydroxystearic acid or the metal salts of 12-hydroxystearic acid; and 1 to 98.9 percent by weight of a volatile methyl siloxane (VMS) having the formula as defined in the claim. This VMS has a boiling point less than 250°C and a viscosity of 0.65 to 5.0 centistokes (mm 2 /s). While not bound by any particular theory, it is believed that the increase in strength of our gels, as well as their increase in clarity and adhesion to substrates, is due to interaction between the 12-hydroxystearic acid gelator and the siloxane polyether. Because our gelator is amide-free, this interaction is unhindered by the presence of any amide-type co-gelator, such as those of the prior art taught in the following related applications (US 0530671/EP 0 531 337/WO 93-23008). In the WO 93-23008 publication, a use is suggested of certain long-chain alkyl modified polysiloxane-polyoxyalkylene copolymers having a structure corresponding to MD x D' y D'' z M, by way of reference to EP 0 373 424/US 4980156. Surprisingly, the siloxane polyethers of the present invention have a structure of only MD'' z M, indicating a significantly different molecule, with a radically different structure, and obviously different properties. In addition, our siloxane polyethers differ from the molecules described in EP 0 373 424/US 4980156, in that these references do not suggest the use of a MD'' z M type siloxane polyether with an oxyalkylene segment consisting of only oxypropylene units -(C 3 H 6 O) s -. Thus, in our invention, the siloxane polyethers function to increase the intermolecular forces between the VMS and the 12-hydroxystearic acid gelator, to control the size and number of microfibers which are formed and this in turn improves the strength and clarity of the gels. Furthermore, our siloxane polyethers function to increase the solubility of our amide-free 12-hydroxystearic acid gelator in the VMS. As a result, a large number of nucleation sites are formed during crystallization and these sites have the potential of producing a large number of microfibers. A high fiber density is thereby produced which causes the gels to become stronger and exhibit a higher modulus. Since these microfibers are of a very small size, they cause less light scattering and our gels are transparent. Gels of this invention contain 1 to 98.9 percent by weight of a siloxane polyether; 0.1 to 20 percent by weight of an amide-free gelator; and 1 to 98.9 percent by weight of a VMS. Preferably, our gels contain 1 to 10 percent by weight of the siloxane polyether; 0.1 to 4 percent by weight of the amide-free gelator; and 1 to 90 percent by weight of the VMS. The siloxane polyether of the present invention is a compound having the following formula: R a is an alkyl group of one to six carbon atoms; R b is the linking group -C m H 2m -; R c is a terminating radical which can be hydroxyl or alkoxy such as methoxy, ethoxy and propoxy; m has a value of two to eight; s has a value between one and thirty; and n has a value of one to forty. Methods of making siloxane polyether compounds are known in the art and are described in "Chemistry and Technology of Silicones", Walter Noll, Academic Press Inc., 1968, Pages 373-376. The oxyalkylene segment of the siloxane polyether consists of only oxypropylene units -(C 3 H 6 O) s -. The amide-free gelator is 12-hydroxystearic acid or a metal salt of 12-hydroxystearic acid. This acid has the formula CH 3 (CH 2 ) 5 CH(OH)(CH 2 ) 10 COOH. Metal salts of 12-hydroxystearic acid can also be employed as gelator. Such salts have the formula [C 6 H 13 -CH(OH)-(CH 2 ) 10 -COO] n M in which M indicates a metal such as Li+, Na+, K+, Rb+, Cs+, Mg(2+), Ca(2+), Sr(2+), Ba(2+), Mn(2+), Ni(2+), Cu(2+), Zn(2+), Cd(2+), Hg(2+), Co(2+) and Pb(2+); and the value of n is one for monovalent cations and two for divalent cations. An example of suitable metal salts for this invention are calcium 12-hydroxystearate and lithium 12-hydroxystearate. These metal salts are prepared by the direct neutralization of 12-hydroxystearic acid with a metal base such as sodium hydroxide or potassium hydroxide. The metal salts are also prepared by a metathesis reaction of a simple metal salt, such as sodium 12-hydroxystearate, with a metal sulfate salt or a metal chloride salt, such as zinc chloride or copper sulfate. The third component is a VMS which is a low viscosity silicone fluid which corresponds to the average unit formula (CH 3 ) a SiO (4-a)/2 in which a has an average value of two or three. The fluid contains siloxane units joined by Si-O-Si bonds. Representative units in the fluid molecule are the monofunctional unit (CH 3 ) 3 SiO 1/2 and the difunctional unit (CH 3 ) 2 SiO 2/2 . These units are present in molar amounts such that there is provided an average of from two to three methyl groups per silicon atom in the fluid. These fluids generally have a viscosity of less than ten centistokes (mm 2 /s). Representative VMS are cyclopolysiloxanes of the formula [(CH 3 ) 2 SiO] x and linear siloxanes of the formula (CH 3 ) 3 SiO[(CH 3 ) 2 SiO] y Si(CH 3 ) 3 , in which x has a value of three to six and y has a value of zero to five. These VMS have boiling points generally less than 250°C and the viscosity is typically from 0.65 to 5.0 centistokes (mm 2 /s). Some structures which are representative of VMS are shown below: or Structure I represents a linear VMS. Structure II represents a cyclic VMS. The values of x and y in Structures I and II are the same as noted previously. The cyclic VMS (II) has been assigned the International Nomenclature Cosmetic Ingredient (INCI) name "CYCLOMETHICONE" by The Cosmetics, Toiletries and Fragrance Association, Inc. (CTFA), Washington, D.C. The cyclic and linear methyl siloxanes are clear fluids and are essentially odorless, nontoxic, non-greasy and non-stinging. Cosmetically, the fluids are nonirritating to skin, spread easily when applied to the skin, and once applied, evaporate leaving behind no residue. The VMS leave substantially no residue after thirty minutes at room temperature when one gram of the fluid is placed at the center of No. 1 circular filter paper which has a diameter of 185 millimeters and which is supported at its perimeter in open room atmosphere. Some representative linear VMS are hexamethyldisiloxane which has a boiling point of 100°C and the formula Me 3 SiOSiMe 3 ; octamethyltrisiloxane which has a boiling point of 152°C and the formula Me 3 SiOMe 2 SiOSiMe 3 ; decamethyltetrasiloxane which has a boiling point of 194°C and the formula Me 3 SiO(Me 2 SiO) 2 SiMe 3 ; dodecamethylpentasiloxane which has a boiling point of 229°C and the formula Me 3 SiO(Me 2 SiO) 3 SiMe 3 ; tetradecamethylhexasiloxane which has a boiling point of 184°C and the formula Me 3 SiO(Me 2 SiO) 4 SiMe 3 ; and hexadecamethylheptasiloxane which has a boiling point of 184°C and the formula Me 3 SiO(Me 2 SiO) 5 SiMe 3 . Some representative cyclic VMS are hexamethylcyclotrisiloxane which has a boiling point of 133°C and the formula [(Me 2 )SiO] 3 ; octamethylcyclotetrasiloxane which has a boiling point of 171°C and the formula [(Me 2 )SiO] 4 ; decamethylcyclopentasiloxane which has a boiling point of 205°C and the formula [(Me 2 )SiO] 5 ; and dodecamethylcyclohexasiloxane which has a boiling point of 245°C and the formula [(Me 2 )SiO] 6 . Generally, the VMS may be used alone or mixed together. Mixtures of the fluids will result in a volatile material having an evaporating behavior different from any one of the individual fluids. A petition to the United States Environmental Protection Agency, filed in late 1992, is pending seeking exemption of these VMS from regulation as a volatile organic carbon (VOC). The basis for the petition is that the VMS do not contribute to, and in some cases actually inhibit, the formation of tropospheric ozone. Thus, the VMS have a lower ozone formation potential than ethane, which is the most reactive compound on a list of "exempt" VOC. Furthermore, these VMS have an atmospheric lifetime of between 10 to 30 days. Consequently, VMS compounds do not contribute significantly to global warming. These VMS have no potential to deplete stratospheric ozone due to their short atmospheric lifetimes so that they will not rise and accumulate in the stratosphere. VMS compounds also contain no chlorine or bromine atoms. VMS compounds neither attack the ozone layer nor do they contribute to tropospheric ozone formation (smog) and they have minimum GLOBAL WARMING potential. VMS compounds are hence unique in possessing these three attributes simultaneously. These VMS unexpectedly provide a viable solution to the problem of finding a suitable replacement for "outlawed" chemicals heretofore commonly used as components in personal care products. The procedure for making the clear, firm, gel according to this invention is simply a matter of combining and mixing together three components. The mixture is heated to dissolve the gelator. The gel is formed when the mixture is cooled or allowed to cool. Example 1 In a 29.6 ml (one ounce) glass vial, 3.1 grams of a mixture containing 75 percent by weight of decamethylcyclopentasiloxane and 25 percent by weight of dodecamethylcyclohexasiloxane, hereinafter VMS, was mixed with one gram of a siloxane polyether having the formula Me 3 SiO-[MeSi-(CH 2 ) 3 -(CH 2 CHCH 3 O) 2 OMe]-OSiMe 3 . This particular siloxane polyether is referred to hereinafter as siloxane polyether (I). To the resulting clear solution, 0.2 gram of 12-hydroxystearic acid was added and the mixture was heated mildly on a hot plate. The 12-hydroxystearic acid dissolved before reaching its melting temperature of 80-81°C. The clear solution was removed from the hot plate. Upon cooling and before reaching ambient temperature, a firm opaque gel was formed. The gelation rate was noted to be rapid. The gel was reheated and converted back to a clear solution. Upon cooling, a stiff opaque gel was again formed. Ten additional grams of the VMS were added to the gel and the mixture was heated. Upon cooling, a translucent gel was obtained. The concentration of 12-hydroxystearic acid in the gel was 1.4 weight percent. At this low concentration, the gel was still stiff enough, that it would not break down by either vigorous vortexing on a Thermolyne™ Maxi Mix II mixer, nor by vigorous shaking by hand. Example 2 Another gel was prepared in a manner analogous to that described in Example 1, by mixing together twenty grams of VMS, 0.88 grams of the siloxane polyether (I) and 0.2 gram of 12-hydroxystearic acid. The mixture was heated and a clear solution was obtained. Upon cooling, an opaque firm gel was formed. Vigorous vortexing did not disrupt the gel. One gram of absolute ethanol was added to the formulation and by applying a slight amount of heat, the gel was converted to a clear solution. Upon cooling and the elapse of two hours, only a small portion of the solution had formed traces of a weak gel. Most of the mixture remained in liquid form, with some cloudy specks believed to be precipitated 12-hydroxystearic acid, which were clearly visible. This indicated that the gelator was very soluble in an alcohol, the presence of which prevents the gelation process. Example 3 Another gel was prepared by combining ten grams of VMS, one gram of the siloxane polyether (I) that contained fifty weight percent of unreacted propylene oxide and 0.2 gram of 12-hydroxystearic acid. The method described in Example 1 was again followed. The gel was opaque and firm and did not break down by vortexing. An amount of 0.44 gram of absolute ethanol was added to the gel and upon heating and vortexing, an opaque liquid was obtained. When cooled, the mixture again gelled. This gel was breakable with vortexing, but it reformed within an hour by standing at room temperature. Example 4 The following gel formulation was prepared by the method of Example 1, by mixing together eighty-eight weight percent of VMS, ten weight percent of the siloxane polyether (I) and two weight percent of 12-hydroxystearic acid. The resulting gel was firm and translucent. The gel was not disrupted by vortexing, shaking by hand or by a Brinkman™ mechanical shaker set at maximum. Example 5 Three (3) gels analogous to the gel of Example 4 were prepared gels analogous to the gel of Example 4 were prepared using the siloxane polyethers shown below. In the formulas, "Me" indicates the methyl group -CH 3 . The gel formed with siloxane polyether (I) is described in the previous Example 4. Polyether Formula (A) MDDM Me 3 SiO(Me 2 SiO) 103 (MeQSiO) 9.5 -SiMe 3 in which Q is -(CH 2 ) 3 (OCH 2 CH 2 ) 18 (OCH 2 CHCH 3 ) 18 OCOCH 3 (B) MDDM Me 3 SiO(Me 2 SiO) 8.6 (MeQSiO) 3.6 SiMe 3 in which Q is -(CH 2 ) 3 (OCH 2 CH 2 ) 12 OH (I) MDM Me 3 SiO-[MeSi-(CH 2 ) 3 -(CH 2 CHMeO) 2 OMe]-OSiMe 3 . The formulations for each of the gels were heated to dissolve the gelator. All of the mixtures formed hazy solutions. Gels were formed on cooling. Example 5A Another formulation containing 89.5 weight percent of VMS, ten weight percent of the siloxane polyether (I) and 0.5 weight percent of 12-hydroxystearic acid, formed a translucent gel. This gel could be disrupted by shaking for a few seconds with a Brinkman™ shaker set at 100. Example 6 - Comparison Two gels analogous to the gel made by the procedure of Example 4, were prepared using siloxane polyethers (A) and (B). The formulas for these two siloxane polyethers are set forth in Example 5. Siloxane polyethers (A) and (B) are of the type MDDM, in comparison to the siloxane polyether (I) of the invention, which corresponds to the type MDM, as shown in Example 5. Cloudy mixtures containing the siloxane polyethers (A) and (B) were heated on a hot plate at a temperature in excess of 80° C. Gel (B) which was formed with siloxane polyether (B), phase separated and required mixing prior to reaching the gel point, to obtain a "uniform-like" gel. Gels (A) and (B) were each shaken on a Brinkman™ wrist shaker operating at maximum speed. Gel (B) broke down first. Gel (A) was more resistant to breakage, although it began thinning after a time. Upon standing for one hour at ambient temperature, gels (A) and (B) were partially reformed, although gel (A) broke down again upon inversion of the vial and gel (B) was noted to contain some non-gelled fluid. Example 7 - Comparison Two gels were prepared by the method described in Example 1. Gel (A) contained 9.8 grams of VMS and 0.2 gram of 12-hydroxystearic acid. Gel (A) did not contain a siloxane polyether and is not according to our invention. Gel (B) contained 15.2 grams of the VMS, 4.4 grams of siloxane polyether (I) and 0.4 gram of the gelator 12-hydroxystearic acid. Gel (B) is according to this invention. The mixture used to prepare gel (B) was clear when the solution was hot. The solution used to prepare gel (A) on the other hand, contained visible droplets of melted 12-hydroxystearic acid when it was heated. The hot solutions were each cast in a round stainless steel mold used on Rheometrics™ Inc., rheometers for measuring the strength of gels. Gels were formed on cooling. Gel (B) was less hazy than gel (A). Gel (B) was found to adhere to a greater extent on metal and Teflon substrates than gel (A). Strain sweep curves were determined for each of the gels (A) and gel (B). Figure 1 is a graphical representation of these strain sweep curves measured at 5 radians per second (48 revolutions per minute). Curve A represents Gel (A) prepared while Curve B represents Gel (B) also prepared in Example 7. Gel (B) represents the present invention, while Gel (A) does not represent our invention. The figure shows that the storage modulus, G', of Gel (B) is higher than that of Gel (A). This indicates that the consistency of Gel (B) is firmer than that of Gel (A). Thus, the siloxane polyether used to prepare Gel (B) of the invention functions to increase the compatibility of the 12-hydroxystearic acid gelator with the VMS when hot. Upon cooling, a large number of nucleation sites are thereby formed, which create a high density of microfibers and thus a firmer Gel (B). In comparison, Gel (A) did not contain the siloxane polyether according to the invention and was inferior. This improvement is believed to be due to the fact that the siloxane polyethers of the type MDM increase the compatibility of the gelator with the VMS when the solution is hot. Example 7A - Comparison Another gel was prepared by mixing four weight percent of 12-hydroxystearic acid and 96 weight percent of the VMS. Again, no siloxane polyether was used to prepare the gel. Upon shaking, this comparison gel easily broke down. Example 8 Five (5) gels were prepared by combining the VMS, the siloxane polyether (I) and the 12-hydroxystearic acid gelator, according to the method described in Example 1. The amounts of the three ingredients used to prepare these five gels are shown in Table I. Gel wt.% VMS wt.% (I) wt.% 12-OH stearic acid Comments A 79 20 1 weak gel B 84 15 1 firmer than A C 89 10 1 complete gel D 88.5 10 1.5 gelled E 88.25 10 1.75 gelled While gels (D) and (E) could be mechanically disrupted, they reformed on standing for about one day. The foregoing examples illustrate that better gels are obtained using the siloxane polyethers of the invention which are MDM type ethers, in comparision to the longer chain ethers of the prior art such as the ethers of the types MDDM or MDDDM.

Claims: A gel comprising (A) 1 to 98.9 percent by weight of a siloxane polyether having the formula wherein R a is an alkyl group of one to six carbon atoms; R b is the linking group -C m H 2m -; R c is hydroxy or alkoxy; m has a value of two to eight; s has a value between one and thirty; and n has a value of one to forty; (B) 0.1 to 20 percent by weight of an amide-free gelator selected from 12-hydroxystearic acid or metal salts of 12-hydroxystearic acid; and (C) 1 to 98.9 percent by weight of a volatile methyl siloxane having a boiling point less than 250 °C and a viscosity of 0.65 to 5.0 centistoke (mm 2 /s), the volatile methyl siloxane having a formula selected from or in which x has a value of three to six and y has a value of zero to five.

Inventors: KATSOULIS DIMITRIS ELIAS, KATSOULIS, DIMITRIS ELIAS
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1995
Main classification: A61K7
IPC codes: C08K5, A61K8, C08L83, A61Q19, A61Q5