Trialkyl endcapped polyorganosiloxane emulsions

Abstract: A non-crosslinked endblocked polymer, comprising a preformed aqueous emulsion having a plurality of silanol-terminated polydiorganosiloxane particles, an endcapping silane having the formula R₃SiX where X is a hydrolyzable group, R is an alkyl group consisting of 1 to 7 carbon atoms, and an organotin catalyst. The composition unexpectedly results in a non-crosslinked polymer, unlike the polymers described in the prior art. It has been found that adding an endblocking silane having only one hydrolyzable group to a preformed polydiorganosiloxane emulsion surprisingly results in endblocked polydiorganosiloxane molecules free of crosslinks between the polydiorganosiloxane chains.

Description: The invention relates to a method of end-capping a polydiorganosiloxane molecule in emulsion with a trialkyl functional silane and the compositions resulting therefrom. U.S. Patent 2,755,194 teaches the preparation of polydiorganosiloxane emulsions by milling together a polyethylene glycol trimethylmonoether and alkylaryl polyether sulfate sodium salt, water and a siloxane polymer which have various functionalities. That patent does not teach an emulsification method but aims to teach a method to control the functionality of emulsion compositions. U.S. Patent 3,294,725 discloses a stable polydiorganosiloxane emulsion prepared by polymerizing R n SiO (4-2)/2 or HOR 2 SiQSiR 2 OH (where R is a hydrogen atom, hydrocarbon group or halohydrocarbon group, n is preferably 2 and Q is a divalent hydrocarbon or ether containing hydrocarbon radical) in aqueous medium using a surface active sulfonic acid catalyst such as C 12 H 25 C 6 H 4 SO 3 H. Example 3 of the patent uses hexamethyldisiloxane to produce a trimethyl end-capped polymer. However, it teaches only modification of the chain end during polymerization while the method of our invention claims the post modification of a polydiorganosiloxane emulsion. U.S. Patent 4,618,642 describes an aqueous silicone elastomeric emulsion that is obtained by mixing an anionic emulsion containing dispersed particles of hydroxyl endblocked polydiorganosiloxane, dialkyltindicarboxylate, silanes of the formula RSi(OR') 3 where R is a monovalent hydrocarbon radical of from 1 to 4 carbon atoms inclusive and R' is a lower alkyl radical of from 1 to 4 carbon atoms inclusive or a radical of the formula -N=CR 2 and inert, non-siliceous filler. Unlike that patent, the present invention does not use R'Si(0R') 3 in our compositions. U.S. Patent 4,782,112 provides a mixture of (A) a silicone water-based emulsion composed of water, emulsifying agent and diorganopolysiloxane having at least 2 silicone-bonded hydroxyl groups in each molecule, (B) a silicone water-based emulsion composed of water, emulsifying agent and organohydrogenpolysiloxane having at least 2 silicon-bonded hydrogen atoms in each molecule and (C) a curing catalyst. It is characterized by an excellent storage stability and by the formation on cure of a rubbery elastomeric film which has an excellent alkali resistance, water repellency, water-repellant sealability and durability of adhesion. The patent, however, does not teach the addition of a functionalizing silane to the polysiloxane as does our claimed invention. U.S. Patent 4,954,565 introduces a shelf-stable aqueous silicone emulsion which yields an elastomer upon removal of water. It is produced by combining a hydroxy endblocked polydiorganosiloxane, present as an emulsion of dispersed particles in water, a crosslinker and a tin catalyst. The tin catalyst is in the form of a divalent tin atom combined with organic radicals. The emulsion, after crosslinking of the polydiorganosiloxane, is reinforced with colloidal silica without affecting the shelf life of the reinforced emulsion. This patent, however, differs from the present invention because it does not include a monoalkoxy functionalizing silane. Moreover, that patent does not teach adding monohydrolyzable silanes to silanol functional polymers to form non-crosslinked polymers. The present invention provides a non-crosslinked emulsion polymer having trialkylsiloxy end groups, comprising (A) a preformed aqueous polydiorganosiloxane emulsion comprising water, a surfactant and a plurality of silanol-terminated polydiorganosiloxane molecules; (B) an endblocking silane having the formula R 3 SiX where X is a hydrolyzable group, R is the same or different alkyl radical having from 1 to 7 carbon atoms inclusive; and (C) an organotin catalyst. The above reactants of (A) are allowed to react for sufficient time to preform an end-blocked polymeric emulsion which is unlike the emulsion polymers described in the prior art. When our endblocking silane is added to the above polydiorganosiloxane emulsion in the presence of an organotin catalyst, an end-capped polymer results, which consists of a polydiorganosiloxane with a trialkylsiloxy endbocking group on each chain end. By "endblocking group", it is meant a non-reactive group that will not undergo further conventional chemical reactions. The method of this invention allows for specific placement of the endblocking silane at the chain end. This result is unexpectedly achieved by selecting a certain endblocking silane having one hydrolyzable group and by then adding this silane to the preformed emulsion in the presence of a tin catalyst. The endblocked polyorganosiloxane emulsions of our invention have the physical characteristics of a gum or fluid, once the water is removed. Our resulting endblocked polydiorganosiloxane emulsions are used for slip additives, lubricants, antifoam additives, release agents and hydrophobing fabric treatments. The polydiorganosiloxane emulsions of this invention are in contrast to systems known in the prior art, in which the trialkyl functionality is attached to the chain end during polymerization. Such systems do not easily produce high molecular weight polymers. Our method also differs from those of the prior art which employ a tin catalyst in that we use a trialkyl silane having a single hydrolyzable group rather than a crosslinking trialkoxy silane. When a trialkoxy silane is used, the resulting compositions consist of elastomeric polydiorganosiloxanes, which upon removal of water, will produce elastomeric films that are insoluble in solvent whereas, in contrast, the present invention consists of non-crosslinked polydi-organosiloxane emulsions which form tacky, gum-like or fluid-like films that are soluble in solvent when water is removed. Our invention introduces a non-crosslinked endblocked emulsion polymer, comprising (A) a preformed aqueous polydiorganosiloxane emulsion comprising water, a surfactant and a plurality of silanol-terminated polydiorganosiloxane molecules; (B) an endblocking silane having the formula R 3 SiX where X is a hydrolyzable group, R is the same or different alkyl radical having 1 to 7 carbon atoms inclusive; and (C) an organotin catalyst. The aqueous emulsion having a plurality of particles of silanol-terminated polydiorganosiloxane is prepared by conventional methods known in the art. In addition to polydiorganosiloxane and water, this component also contains at least one surfactant which stabilizes the dispersed polydiorganosiloxane particles in the emulsion. The polydiorganosiloxane particles of this emulsion should have an average size of 0.1 to 10 micrometers, preferably from 0.5 to 1 micrometer. It is preferred that the above emulsion have a solids content ranging from 20 to 70 weight percent, most preferably about 65 weight percent. These emulsions are well known in the art and may be prepared by methods wherein cyclic or linear oligomeric diorganosiloxanes are dispersed in an aqueous continuous phase with the aid of the above surfactant and are thereafter emulsion polymerized by the introduction of an acid or base catalyst. These methods are illustrated by the disclosures of U.S. Patents 3,294,725 and U.S. Patent 2,891,920. In preferred embodiments, the surfactant employed is an anionic type, such as sodium lauryl sulfate or ammonium lauryl sulfate, and the catalyst is dodecylbenzene sulfonic acid, the latter also acting as a surfactant in the system. The emulsions taught in U.S. Patents 4,618,642 and 4,954,565, may also be used in the present invention. The polydiorganosiloxane emulsion can also be prepared by direct emulsification. In this process, a mixture of water, polydiorganosiloxane and one or more surfactants is processed under high shear conditions using either conventional mixing equipment or high shear devices such as a homogenizer. Methods for preparing these emulsions are demonstrated in U.S. Patent 4,177,177. The organic groups pendant from the backbone of the polydiorganosiloxane molecule are independently selected from hydrocarbon or halogenated hydrocarbon radicals such as alkyl and substituted alkyl radicals containing from 1 to 20 carbon atoms; cycloalkyl radicals such as cyclohexyl; and aromatic hydrocarbon radicals such as phenyl, benzyl and tolyl. Preferred organic groups are lower alkyl radicals containing from 1 to 4 carbon atoms, phenyl, and halogen-substituted alkyl such as 3,3,3-trifluoropropyl. Thus, the polydiorganosiloxane can be a homopolymer, a copolymer or a terpolymer containing such organic groups. Examples include systems comprising dimethylsiloxy units and phenylmethylsiloxy units; dimethylsiloxy units and diphenylsiloxy units; and dimethylsiloxy units, diphenylsiloxy units and phenylmethylsiloxy units, among others. Most preferably, the polydiorganosiloxane is a polydimethylsiloxane which is terminated with a silanol group at each end of its molecule. Component (B), the endblocking silane, is a silane having the following formula R 3 SiX, R is the same or different alkyl radical containing 1 to 7 carbon atoms inclusive. These groups are exemplified by methyl, ethyl, propyl, isopropyl, butyl, t-butyl, cyclohexyl, phenyl, hexyl or combinations thereof. The most preferred R radical is methyl. X is any hydrolyzable group. The term "hydrolyzable group" means any group attached to the silicon which is hydrolyzed by water at room temperature. The hydrolyzable group X includes hydrogen atom, halogen atoms such as F, Cl, Br or I; groups of the formula -OY when Y is any hydrocarbon or halogenated hydrocarbon group such as methyl, ethyl, isopropyl, octadecyl, allyl, hexenyl, cyclohexyl, phenyl, benzyl, beta-phenylethyl, any hydrocarbon ether radical such as 2-methoxyethyl, 2-ethoxyisopropyl, 2-butoxyisobutyl, p-methoxyphenyl or -(CH 2 CH 2 O) 2 CH 3 ; or any N,N-amino radical such as dimethylamino, diethylamino, ethylmethylamino, diphenylamino or dicyclohexylamino. X is also any amino radical such as NH 2 , dimethylamino, diethylamino, methylphenylamino or dicyclohexylamino or any ketoxime radicals of the formula -ON=CM 2 or -ON=CM'. M is any monovalent hydrocarbon or halogenated hydrocarbon radical such as those shown for Y above and M' is any divalent hydrocarbon radical both valences of which are attached to the carbon, such as hexylene, pentylene or octylene. X can be ureido groups of the formula -N(M)CONM" 2 in which M is defined as above, hydrocarbon radicals such as those shown for Y above and M" is hydrogen atom or any of the M radicals. X is further carboxyl groups of the formula -OOCMM" in which M and M" are as defined above or a halogenated hydrocarbon radical as illustrated for Y above, or carboxylic amide radicals of the formula -NMC=O(M") in which M and M" are as defined above. X can also be the sulfate group or sulfate ester groups of the formula -OSO 2 (OM) where M is defined as above, hydrocarbon or halogenated hydrocarbon radicals illustrated for Y; the cyano group; the isocyanate group; and the phosphate group or phosphate ester groups of the formula -OPO(OM) 2 in which M is defined as above. The most preferred hydrolyzable groups of the invention are alkoxy groups. Illustrative examples are methoxy, ethoxy, propoxy, butoxy, isobutoxy, pentoxy, hexoxy and 2-ethylhexoxy; alkoxy radicals such as methoxymethoxy or ethoxymethoxy; and alkoxyaryloxy such as ethoxyphenoxy. The most preferred alkoxy groups are methoxy or ethoxy. The organotin catalyst, Component (C), is an organic salt of tin and may be illustrated by tin (II) carboxylates, such as stannous oleate and stannous naphthenate; dialkyl tin (IV) carboxylates, such as dibutyltin diacetate and dibutyltin dilaurate; and tin (IV) stannoxanes, as exemplified by the structure (Bu) 2 SnCl-O-(Bu) 2 OH, in which Bu denotes a butyl radical, as taught in U.S. Patent 5,034,455. In preferred embodiments, the catalyst is stannous octoate. To prepare the composition of the present invention, an organotin curing catalyst and an endblocking silane are added to the preformed aqueous polydiorganosiloxane emulsion in a first step. The endblocking silane migrates into the particles of the polyorganosiloxane where it condenses with the silanol groups on the ends of the polydimethylsiloxane molecules in the presence of the organotin catalyst. Unlike the prior art, no crosslinking occurs between our polyorganosiloxane molecules because the endblocking silane contains only one hydrolyzable group and therefore is incapable of cross-linking. This surprisingly contrasts with the silanes taught in the prior art, in which three or more hydrolyzable groups at the silicon atom of the silane lead to a cross-linked polyorganosiloxane emulsion which has the physical characteristics of an elastomer upon the removal of water. The non-crosslinked polyorganosiloxane emulsions of the present invention therefore have the physical characteristics of a gum or fluid upon removal of water. Although the order of addition is not considered critical, it is preferred to first add from 0.05 to 2 parts by weight, preferably from 0.3 to 0.6 parts, of the catalyst to 100 parts by weight of the silanol-terminated polydiorganosiloxane in emulsion. From 0.1 to 10 parts by weight, preferably about 1 part, of the endblocking silane is then added to this mixture for each 100 parts by weight of the polydiorganosiloxane and the resultant emulsion is allowed to age in a second step. Usually the aging process requires from one half hour to four hours at room temperature. When the endblocking silane content is less than 0.1 part, incomplete endcapping is observed; when this component exceeds 10 parts, the by-products formed when the hydrolyzable group X is reacted can destabilize the emulsion. During the aging process, which can take place at room temperature as well as at elevated temperatures, the pH of the emulsion should be maintained between 4 and 10.5. The following examples are presented to further illustrate the compositions of this invention. All parts and percentages in the examples are on a weight basis and all measurements were obtained at 25°C., unless indicated to the contrary. Example 1 A silanol functional polydimethylsiloxane emulsion was prepared by adding 4.0 g of sodium lauryl sulfate to 200 g of water followed by 200 g of a silanol end-blocked polydimethylsiloxane with an average degree of polymerization of approximately 50. The mixture was stirred for 15 minutes and the resulting dispersion was homogenized by passing it twice through a Microfluidics™ Microfluidizer at 55.2 MPa (8000 psi). The resulting emulsion contained 50 wt% polydimethylsiloxane having an average particle size of 310 nm. To 50 g of this polydimethylsiloxane emulsion, 0.17 g of stannous octoate was added. The latex was stirred and 1.50 g of trimethylmethoxysilane was added dropwise. 1.5 g of the emulsion was inverted into tetrachloroethylene by adding the emulsion to a slurry of anhydrous ammonium sulfate in tetrachloroethylene. The silanol content of the polydimethylsiloxane was determined by measuring the absorption of infrared light at 3693 cm -1 using a Perkin Elmer™ Model 1640 FTIR. Another portion of the emulsion was inverted into toluene and the molecular weight was measured by gel permeation chromatography (GPC). The endcapping efficiency, or the fraction of chain-ends that were capped by the trimethylmethoxysilane, was determined by dividing the number of silanol chain-ends determined by FTIR with the number of total chain-ends calculated for the GPC molecular weight and then subtracting this number from one. After 16 hours, eighty-five percent of the chain-ends were capped with trimethyl groups and after 4 days ninety-three percent of the chain-ends were capped with trimethyl groups. Example 2 An endcapping reaction was carried out similar to Example 1 except 0.15 g of dibutyltin diacetate (DBTDA) was used in lieu of stannous octoate. The endcapping efficiency was then determined using the FTIR technique of Example 1. After 16 hours, seventy-two percent of the polymer chain-ends were capped with trimethyl groups and after 4 days ninety-three percent of the end-groups were capped with trimethyl groups. Example 3 An aqueous, anionically stabilized emulsion of silanol ended PDMS having a solids content of approximately 62% by weight, a mean particle size of approximately 420 nm and a polymer weight average molecular weight of approximately 300,000 was prepared according to the method described in U.S. Patent 4,618,642. Next, 0.6 g of stannous octoate was added to the emulsion and stirred for 3 minutes. This was followed by 1.0 g of trimethylmethoxysilane which was added dropwise to the emulsion with continued stirring. After 10 minutes, the stirring was discontinued and the emulsion was allowed to remain undisturbed for an additional hour. The endcapping efficiency was then determined using the same FTIR technique described in Example 1. After 48 hours, 93% of the end-groups were capped with trimethyl. Example 4 An endcapping reaction was carried out as in Example 1, except 0.6 g of dibutyltin diacetate (DBTDA) was used in lieu of the stannous octoate. The endcapping efficiency was then determined using the same FTIR technique described in Example 1. After 4 days, 100% of the end-groups were capped with trimethyl.

Claims: A polymeric emulsion comprising (A) a preformed aqueous polydiorganosiloxane emulsion comprising water, a surfactant, and a plurality of silanol-terminated polydiorganosiloxane molecules; (B) an endblocking silane having the formula R 3 SiX where X is a hydrolyzable group, R is the same or different alkyl radical containing 1 to 7 carbon atoms inclusive; and (C) an organotin catalyst. The composition according to claim 1, wherein said polydiorganosiloxane is a polydimethylsiloxane which is terminated with silanol groups. The composition according to claim 1 wherein said organo tin catalyst is selected from the group consisting of a tin (II) carboxylate and a dialkyl tin (IV) carboxylate. The composition according to claim 1 wherein said endblocking silane is trimethylmethoxy silane. The composition according to claim 1 wherein the composition contains a filler. The composition of claim 1 wherein the water has been removed. A method for preparing an end-blocked polymeric emulsion comprising the steps of (I) adding an endblocking silane and an organotin catalyst to a preformed aqueous polydiorganosiloxane emulsion comprising water, a surfactant and a plurality of silanol-terminated polydiorganosiloxane molecules, wherein said endblocking silane has the formula R 3 SiX where X is a hydrolyzable group and R is the same or different alkyl radical containing 1 to 7 carbon atoms inclusive; and (II) allowing the reactants of (I) to react for sufficient time to form an end-blocked polymeric emulsion.

Inventors: LILES DONALD TAYLOR, MURRAY DAVID LOGAN, LILES, DONALD TAYLOR, MURRAY, DAVID LOGAN
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1995
Main classification: C08J3
IPC codes: C08G77, C08K5, C08F2, C08L83, C08J3