Fire-resistant polycarbonate resin composition

Abstract: A fire-resistant polycarbonate resin composition contains A) 5-50 parts by weight of liquid crystal polymer B) 90-40 parts by weight of polycarbonate resin, C) 2-20 parts by weight of flame retardant, and D) 0.1-1.0 parts by weight of polytetrafluoroethylene. The composition is suitable for thin-wall application having high flow properties, high elastic modulus, high HDT, and superior surface appearance as well as a high flame retardance achieved by blending the specific flame retardant.

Description: The present invention pertains to a fire-resistant polycarbonate resin composition containing a polycarbonate and a liquid crystal polymer, and it further pertains to a fire-resistant polycarbonate resin composition having good flow properties, high impact resistance, and a high elastic modulus in comparison to standard polycarbonate resin compositions, and is suitable for thin-film housing applications. The above-mentioned composition includes a specific polycarbonate having a phenolic end group, and the solubility with the liquid crystal polymer can be improved by the phenolic end group; as a result, the above-mentioned fire-resistant polycarbonate resin composition with superior properties can be produced. Prior art Aromatic polycarbonate resins have high heat resistance, impact resistance, and mechanical strength and are widely used as high-performance resins, referred to as "engineering plastics." However, the process temperatures required for polycarbonates is high and the flow properties are poor. For this reason, blending with a liquid crystal polymer capable of providing good flow properties and a high elastic modulus is practiced. Blending of an aromatic polycarbonate (PC) with a liquid crystal polymer is disclosed in the patent literature (Japanese Patent Application No. Hei 4[1992]-359735), (Japanese Patent Application No. Hei 6[1994]-74017), etc., which are applications by the present applicant. In the contents disclosed in the above-mentioned existing technology, it is possible to produce a good balance among flow properties, high elastic modulus and high HDT, and products suitable for thin-wall housing applications such as notebook personal computers, pen recording computers, and handiphones are produced. However, there is room for improvement in the blending of polycarbonate and liquid crystal polymers for thin-wall housings and cases for small portable machines. Problems to be solved by the invention The objective of the present invention is to produce a fire-resistant polycarbonate resin composition suitable for thin-wall applications which has good flow properties, high elastic modulus, high HDT, and superior surface appearance, as well as high flame retardance, which is achieved by blending a specific flame retardant. Means to solve the problem The objective of the present invention can be achieved by a fire-resistant polycarbonate resin composition containing A) 5-50 parts by weight of liquid crystal polymer, B) 90-40 parts by weight of polycarbonate resin produced by hot-melt polymerization of an aromatic dihydroxy compound and a diester carbonate, having phenolic and nonphenolic end groups and having an equivalence ratio of phenolic end group (I) and nonphenolic end group (II), (I)/(II), which is greater than 1/19; C) 2-20 parts by weight of phosphate flame retardant wherein the total parts by weight of (A)+(B)+(C) is 100; and D) 0.1-1.0 part by weight per 100 parts of A)+(B)+(C) of polytetrafluoroethylene; For the liquid crystal polymer component (A) in the present invention, thermotropic liquid crystal polyesters can be used effectively, and 5-50 parts by weight, which is effective to improve the properties of the composition, are blended. Said material can be selected from the group of polyesters containing segments with the structure shown below. -O-R-O- -CO-R-CO- -O-R-CO- In this case, R can each be selected from the group shown below (Structure 1). Furthermore, the aromatic rings, aliphatic groups, alicyclic group, etc., represented by the above-mentioned R may be further substituted with the groups shown below (Structure 2). The polycarbonate resin of component (B) of the present invention is produced by hot-melt polymerization of an aromatic dihydroxy compound and a diester carbonate, and the equivalence ratio of phenolic end group (I) and nonphenolic end group (II) (I)/(II) is greater than 1/19, greater than 1/10 is further desirable, and greater than 1/5 is especially desirable. When said ratio is less than 1/19, it is not possible to improve the solubility with the thermotropic liquid crystal polyester and delamination occurs, and the mechanical strength becomes poor; therefore, it is not desirable. Furthermore, it is desirable when the above-mentioned phenolic end group (I) is represented by the formula shown below: and the nonphenolic end group (II) is represented by the formula shown below: In both of the above-mentioned formulas, R 1 and R 2 each represent a hydrogen atom, a linear or branched, alkyl group with less than 20 carbons that may be substituted with halogen atoms, preferably, fluorine, chlorine, or bromine. The adjustment of the equivalence ratio of the above-mentioned polycarbonate end groups can be easily performed by changing the molar ratio of the aromatic dihydroxy compound and diester carbonate raw materials at the time of manufacturing the polycarbonate by means of hot-melt polymerization. For example, when bisphenol A is used for the aromatic dihydroxy compound, and diphenylcarbonate is used as the diester carbonate, the end group of the polycarbonate is a phenolic residue based on the bisphenol A and the phenyl group based on diphenylcarbonate, and when the molar ratio of the bisphenol A is increased, the equivalence ratio of the phenolic end group (I) and nonphenolic end group (II), (I)/(II) of the polycarbonate produced increases. Furthermore, the polycarbonate of the present invention may be a branched type. The branched polycarbonate can be produced by the reaction of a polyfunctional aromatic compound with a diphenol and/or carbonate precursor as a branched thermoplastic resin random branched carbonate. In a polycarbonate used for standard application, especially, a polycarbonate produced by the reaction (especially, by interfacial polymerization method) of an aromatic dihydroxy compound such as bisphenol A and carbonyl chloride, the equivalence ratio of phenolic end group (I) and nonphenolic end group (II), (I)/(II) is less than 1/19, and it is not desirable. The method used for manufacturing the polycarbonate of the present invention itself is a known method in which a polycarbonate is synthesized by a transesterification reaction of the aromatic dihydroxy compound and a diester carbonate under hot-melt conditions. The aromatic dihydroxy compound used is not especially limited, and many known materials can be used. For example, compounds shown in the formula below: (In this case, R a and R b each represent a halogen or univalent hydrocarbon group, X represents -C(R c ) (R d )-, -C(=R e )-, -O-, -S-, -SO-, or -SO 2 -, R c and R d each represent an atomic hydrogen or univalent hydrocarbon group, and R e represents a divalent hydrocarbon group, p and q each represent an integer in the range of 0-4.) for example, bis(hydroxyaryl)alkanes such as bis(4-hydroxyphenyl)methane, 1,1-bis(4-hydroxyphenyl)ethane, 2,2-bis(4-hydroxyphenyl)propane, 2,2-bis(4-hydroxyphenyl)butane, 2,2-bis(4-hydroxyphenyl)octane, bis(4-hydroxyphenyl)phenylmethane, 2,2-bis(4-hydroxy-1-methylphenyl)propane, 1,1-bis(4-hydroxy-t-butyl phenyl)propane, and 2,2-bis(4-hydroxy-3-bromophenylpropane, bis(hydroxyaryl)cycloalkanes such as 1,1-bis(4-hydroxyphenyl)cyclopentane, and 1,1-(4-hydroxyphenyl)cyclohexane, dihydroxyaryl ethers such as 4,4'-dihydroxydiphenyl ether, and 4,4'-dihydroxy-3,3'-dimethylphenyl ether, dihydroxydiaryl sulfides such as 4,4'-dihydroxydiphenyl sulfide, and 4,4'-dihydroxy-3,3'-dimethylphenyl sulfide, dihydroxydiaryl sulfoxides such as 4,4'-dihydroxydiphenyl sulfoxide, 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfoxide, and dihydroxydiaryl sulfones such as 4,4'-dihydroxydiphenyl sulfone, 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfone, etc., can be mentioned, but it is not limited to these compounds. Among those described above, 2,2-bis(4-hydroxyphenyl)propane is especially desirable. In addition to the above-mentioned compounds, compounds shown in the general formula below: (In this case, R f represents a hydrocarbon group with 1-10 carbons, or halogen compound or halogen atom thereof, and m is an integer in the range of 0-4.) for example, resorcinal, and substituted resorcinols such as 3-methyl resorcinol, 3-ethyl resorcinol, 3-propyl resorcinol, 3-butyl resorcinol, 3-t-butyl resorcinol, 3-phenyl resorcinol, 3-cumyl resorcinol, 2,3,4,6-tetrafluororesorcinol, and 2,3,4,6-tetrabromo resorcinol, catechol, hydroquinone and substituted hydroquinones such as 3-methylhydroquinone 3-ethylhydroquinone, 3-propylhydroquinone, 3-butylhydroquinone, 3-t-butylhydroquinone, 3-phenylhydroquinone, 3-cumylhydroquinone, 2,3,5,6-tetramethylhydroquinone, 2,3,5,6-tetra-t-butylhydroquinone, 2,3,5,6-tetrafluorohydroquinone, 2,3,5,6-tetrabromohydroquinone, in addition, 2,2,2',2'-tetrahydro-3,3,3',3'-tetramethyl-1,1'-spiro-b-[1H-indene]-7,7'-diol shown in the formula below: etc., can be used as aromatic dihydroxy compounds. The above-mentioned dihydroxy compounds may be used independently, or in combination of two or more compounds. Also, diester carbonates are not especially limited, for example, diphenyl carbonate, ditolyl carbonate, bis(chlorophenyl)carbonate, m-cresyl carbonate, dinaphthyl carbonate, bis(diphenyl)carbonate, diethyl carbonate, dimethyl carbonate, dibutyl carbonate, dicyclohexyl carbonate, etc., can be mentioned, but it is not limited to these compounds. In particular, diphenyl carbonate is further desirable. The above-mentioned diester carbonates may be used independently, or in combination of two or more compounds. The above-mentioned diester carbonates may include dicarboxylic acids or dicarboxylic acid esters. For examples of dicarboxylic acids and dicarboxylic acid esters, aromatic dicarboxylic acids such as terephthalic acid isophthalic acid, diphenylterephthalate, and diphenylisophthalate, aliphatic dicarboxylic acids such as succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, decanedioic acid, dodecanedioic acid, diphenyl sebacate, diphenyldecanedioic acid, diphenyldodecanedioic acid, alicyclic dicarboxylic acids such as cyclopropanedicarboxylic acid, 1,2-cyclobutanedicarboxylic acid, 1,3-cyclobutanedicarboxylic acid, 1,2-cyclopentanedicarboxylic acid, 1,3-cyclopentanedicarboxylic acid, 1,2-cyclohexanedicarboxylic acid, 1,3-cyclohexanedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, diphenylcyclopropanedicarboxylate, 1,2-cyclobutanediphenyldicarboxylate, 1,3-cyclobutanediphenyldicarboxylate, 1,2-cyclopentanediphenyldicarboxylate, 1,3-cyclopentanediphenyldicarboxylate, 1,2-cyclohexanediphenyldicarboxylate, 1,3-cyclohexanediphenyldicarboxylate, and 1,4-cyclohexanediphenyldicarboxylate, can be mentioned. The above-mentioned dicarboxylic acids and dicarboxylic acid esters may be used independently, or as a combination of two or more compounds. The amount of the dicarboxylic acid or dicarboxylic acid ester included is preferably less than 50 mol% for the above-mentioned diester carbonates, and an amount of less than 30 mol% is further desirable. In addition to an aromatic dihydroxy compound and diester carbonate, polyfunctional compounds containing at least three functional groups in a single molecule can be further included in manufacturing the polycarbonate. For said polyfunctional compounds, compounds containing a phenolic hydroxy group or carboxyl group, and a compound containing three phenolic hydroxy groups is especially desirable. For examples of desirable compounds, 1,1,1-tris(4-hydroxyphenyl)ethane, 2,2'2''-tris(4-hydroxyphenyl)di-isopropylbenzene, α-methyl-α,α',α'-tris(4-hydroxyphenyl)-1,4-diethylbenzene, α,α',α''-tris(4-hydroxyphenyl)-1,3,5-triisopropylbenzene, fluoroglycin. 4,6-dimethyl-2,4,6-tri(4-hydroxyphenyl)-heptane-2,1,3,5-tri(4-hydroxyphenyl)benzene, 2,2-bis(4,4-(4,4'-dihydroxyphenylcyclohexyl)propane, trimellitic acid, 1,3,5-benzene tricarboxylic acid, pyromellitic acid, etc., can be mentioned. Among those described above, 1,1,1-tris(4-hydroxyphenyl)-ethane, α,α',α''-tris(4-hydroxyphenyl)-1,3,5-triisopropylbenzene, etc., are further desirable. The amount of the polyfunctional compound used is preferably less than 0.03 mol for 1 mol of aromatic dihydroxy compound, and less than 0.001-0.02 mol is further desirable, and less than 0.001-0.01 mol is especially desirable. Also, a compound capable of introducing at least one end group shown in the formula below: (In this case, the aromatic ring or chromanyl group may be substituted with a halogen or an alkyl group with 1-9 carbons.) to the polycarbonate produced may be further included. For the compound capable of introducing the hydroxy group shown in the formula (1), diol compounds such as bisphenol A can be mentioned. For the compound capable of introducing the phenoxy group shown in the formula (2), phenol, diphenyl carbonate, etc., can be mentioned; for the compound capable of introducing the p-t-butylphenoxy group shown in the formula (3), p-t-butyl phenol, p-t-butylphenylcarbonate, p-t-butylphenylcarbonate, etc., can be mentioned, and for the compound capable of introducing the p-cumylphenoxy group (p-phenylisopropylphenoxy group) shown in the formula (4), p-cumylphenol, p-cumylphenylphenyl carbonate, p-cumylphenyl carbonate, etc., can be mentioned. For the chromanylphenoxy group shown in the above-mentioned formula (5), chromanylphenoxy groups such as those shown in the formula below can be mentioned : For the compound capable of introducing the group shown in (5-1)[sic], 2,2,4-trimethyl-4-(4-hydroxyphenyl)chroman, 2,2,4,6-tetramethyl-4-(3,5-dimethyl-4-hydroxyphenyl)chroman, 2,3,4-trimethyl-2-ethyl-4-(3-nonyl-4-hydroxyphenyl)-7-nonylchroman, 2,2,4-trimethyl-4-(3,5-diethyl-4-hydroxyphenyl)-6-ethylchroman, 2,2,4,6,8-pentamethyl-4-(3,5-dimethyl-4-hydroxyphenyl)chroman, 2,2,4-triethyl-3-methyl-4-(4-hydroxyphenyl)chroman, 2,2,4-trimethyl-4-(3-bromo-4-hydroxyphenyl)chroman, 2,2,4-trimethyl-4-(3-bromo-4-hydroxyphenyl)-6-bromochroman, 2,2,4-trimethyl-4-(3,5-dibromo-4-hydroxyphenyl)-6-bromochroman, 2,2,4-trimethyl-4-(3,5-dibromo-4-hydroxyphenyl)-6,8-dibromochroman, etc., can be mentioned, and among those listed above, 2,2,4-trimethyl-4-(4-hydroxyphenyl)chroman is further desirable; for the compound capable of introducing groups shown in (5-2), 2,2,3-trimethyl-3-(4-hydroxyphenyl)chroman, 2,2,3,6-tetramethyl-3-(3,5-dimethyl-4-hydroxyphenyl)chroman, 2,3,4-trimethyl-2-ethyl-3-(3-nonyl-4-hydroxyphenyl)-7-nonylchroman, 2,2,3-trimethyl-3-(3,5-diethyl-4-hydroxyphenyl)-6-ethylchroman, 2,2,3,6,8-pentamethyl-3-(3,5-dimethyl-4-hydroxyphenyl)chroman, 2,2,3-triethyl-3-methyl-3-(4-hydroxyphenyl)chroman, 2,2,3-trimethyl-3-(3-bromo-4-hydroxyphenyl)-6-bromochroman. 2,2,3-trimethyl-3-(3,5-dibromo-4-hydroxyphenyl)-6-bromochroman, 2,2,3-trimethyl-3-(3,5-dibromo-4-hydroxyphenyl)-6,8-dibromochroman, etc. can be mentioned, and among those listed above, 2,2,3-trimethyl-3-(4-hydroxyphenyl)chroman is further desirable, for the compound capable of introducing the group shown in (5-3), 2,4,4-trimethyl-2-(2-hydroxyphenyl)chroman, 2,4,4,6-tetramethyl-2-(3,5-dimethyl-2-hydroxyphenyl)chroman, 2,3,4-trimethyl-4-ethyl-2-(3,5-dimethyl-2-hydroxyphenyl)-7-nonyl-chroman, 2,4,4-trimethyl-2-(3,5-dimethyl-2-hydroxyphenyl)-6-ethylchroman, 2,4,4,6,8-pentamethyl-2-(3,5-dimethyl-2-hydroxyphenyl)-6-ethylchroman, 2,4,4-trimethyl-2-(3-bromo-2-hydroxyphenyl)chroman, 2,4,4-trimethyl-2-(3-bromo-2-hydroxyphenyl)-6-bromochroman, 2,4,4-trimethyl-2-(3,5-dibromo-2-hydroxyphenyl)-6-bromochroman, 2,4,4-trimethyl-2-(3,5-dibromo-2-hydroxyphenyl)-6,8-dibromochroman, etc., can be mentioned, and among those listed above, 2,4,4-trimethyl-2,2-(hydroxyphenyl)chroman is further desirable, for the compound capable of introducing the group shown in (5-4), 2,4,4-trimethyl-2-(4-hydroxyphenyl)chroman, 2,4,4,6-tetramethyl-2-(3,5-dimethyl-4-hydroxyphenyl)chroman. 2,4,4-triethyl-2-(4-hydroxyphenyl)chroman, 2,3,4-trimethyl-4-ethyl-2-(3,5-dimethyl-4-hydroxyphenyl)-7-nonylchroman, 2,4,4-trimethyl-2-(3,5-dimethyl-4-hydroxyphenyl)-6-ethylchroman, 2,4,4,6,8-pentamethyl-2-(3,5-dimethyl-4-hydroxyphenyl)-6-ethylchroman, 2,4,4-trimethyl-2-(3-bromo-4-hydroxyphenyl)chroman, 2,4,4-trimethyl-2-(3-bromo-4-hydroxyphenyl)-6-bromochroman, 2,4,4-trimethyl-2-(3,5-dibromo-4-hydroxyphenyl)-6-bromochroman, 2,4,4-trimethyl-2-(3,5-dibromo-4-hydroxyphenyl)-6,8-dibromochroman, etc., can be mentioned, and among those listed above, 2,4,4-trimethyl-2-(4-hydroxyphenyl)chroman is especially desirable. The above-mentioned aromatic ring or aliphatic ring may be further substituted with a halogen or an alkyl group with 1-9 carbons. The above-mentioned compounds may be used independently, or as a combination of two or more compounds. The amount of the above-mentioned compounds used is 1.00-1.30 mol for 1 mol of aromatic dihydroxy compound, and 1.01-1.20 diester carbonate is used and a reaction is performed for the two in the presence of a catalyst. For the catalyst, for example, compounds being suggested in the specification of Japanese Kokai Patent Application No. Hei 4[1992]-175368 by the present inventors can be used. For example, it is desirable to use (a) organic acid salts, inorganic acid salts, oxides, hydroxides, hydrides, alcoholates of metals such as alkali metals and alkaline-earth metals. For specific examples of the above-mentioned compounds, sodium hydroxide, potassium hydroxide, lithium hydroxide, sodium hydrogencarbonate, potassium hydrogencarbonate, lithium hydrogencarbonate, sodium carbonate, potassium carbonate, lithium carbonate, sodium acetate, potassium acetate, lithium acetate, sodium stearate, potassium stearate, lithium stearate, borosodium hydroxide, borolithium hydroxide, borosodium phenylide, sodium benzoate, potassium benzoate, lithium benzoate, disodium hydrogenphosphate, dipotassium hydrogenphosphate, dilithium hydrogenphosphate, disodium salt, dipotassium salt, and dilithium salt of bisphenol A, sodium salt, potassium salt, and lithium salt of phenol, potassium hydroxide, barium hydroxide, magnesium hydroxide, strontium hydroxide, calcium hydrogencarbonate, barium hydrogencarbonate, magnesium hydrogencarbonate, strontium hydrogencarbonate, calcium carbonate, barium carbonate, magnesium carbonate, strontium carbonate, calcium acetate, barium acetate, magnesium acetate, strontium acetate, strontium stearate, etc. can be mentioned, but it is not limited to these compounds. The above-mentioned compounds may be used independently, or as a combination of two or more compounds. The amount of the above-mentioned alkali metal compounds and/or alkaline-earth metal compounds included is preferably 10 -8 to 10 -3 mol for 1 mol of the aromatic dihydroxy compound, 10 -7 to 10 -6 mol is further desirable, and 10 -7 to 8 x 10 -7 mol is especially desirable. Furthermore, in addition to above-mentioned alkali metal compounds and/or alkaline-earth metal compounds, (b) basic compounds may be used as a catalyst. For examples of basic compounds, for example, nitrogen compounds, in specific terms, ammonium hydroxides containing alkyl, aryl, alaryl groups such as tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetrabutylammonium hydroxide, and trimethylbenzylammonium hydroxide, tertiary amines such as trimethylenamine, triethylamine, dimethylbenzylamine, and triphenylamine, secondary or primary amines containing alkyl groups such as methyl group and ethyl group, aryl groups such as phenyl group, and toluyl group, ammonia, and basic salts such as tetramethylammonium borohydride, tetrabutylammonium borohydride, and tetramethylammonium borohydride, etc., can be mentioned, but it is not limited to these compounds. Among those listed above, ammonium hydroxides are especially desirable. The above-mentioned compounds may be used independently, or in combination of two or more compounds. In the component (B) of the present invention, a polycarbonate with a high molecular weight can be produced at a high polymerization activity level when a combination consisting of the above-mentioned (a) an alkali metal compound and/or alkaline-earth metal compound, and (b) a nitrogen-containing basic compound is used as a catalyst. Furthermore, a combination consisting of (a) an alkali metal compound and/or alkaline-earth metal compound, (b) a nitrogen-containing basic compound, and (c) at least one selected from boric acid or boric acid ester as a catalyst. When a catalyst comprised of the above-mentioned combinations is used, it is desirable to use (a) an alkali metal compound and/or alkaline-earth metal compound in the amount described above, and 10 -6 to 10 -1 mol, preferably 10 -5 to 10 -2 mol, of (b) a nitrogen-containing basic compound for 1 mol of aromatic dihydroxy compound. For boric acid or boric acid ester (c), the compounds shown in the general formula shown below: B(OR 3 ) n '(OH) 3-n ' (In this case, R 3 represents a hydrogen atom, an aliphatic hydrocarbon group, alicyclic hydrocarbon group, or aromatic hydrocarbon group, and n' is an integer in the range of 1-3.) are desirable, and for examples, boric acid, trimethylborate, triethylborate, tributylborate, trihexylborate, triheptylborate, triphenylborate, tritolylborate, trinaphthylborate, etc., can be mentioned. Among those listed above, triphenylborate is further desirable. When the above-mentioned boric acid or boric acid esters (c) are used as catalysts along with the above-mentioned compounds (a) and (b), the amount included is in the range of 10 -6 to 10 -1 mol for 1 mol of aromatic dihydroxy compound, and 10 -5 to 10 -2 mol is especially desirable. The conditions such as temperature and pressure, etc. used for the hot-melt polymerization reaction are not especially limited, and conditions commonly used for this purpose can be used as well. Specifically, the first stage reaction is carried out at a temperature of 80-250°C, preferably 100-230°C, and especially 120-190°C, for 0-5 h, preferably 0-4 h, and especially 0.25-3 h, at ambient pressure. Subsequently, the reaction temperature is slowly increased while the pressure of the reaction system is being reduced, and a reaction is performed for the aromatic dihydroxy compound and diester carbonate; it is desirable to carry out the final reaction for the aromatic dihydroxy compound and diester carbonate under a pressure of 0.05-5 mm Hg at a temperature of 240-320°C. The above-mentioned reaction of the aromatic dihydroxy compound and diester carbonate may be carried out by the continuous method or the batch method. The reactor used to perform the above-mentioned reaction may be a tank, a tube, or tower reactor. For the mixing ratio of the polycarbonate in the flame retardant polycarbonate resin composition of the present invention, 90-40 parts by weight, as indicated above, is desirable as a range capable of achieving the objective. Furthermore, manufacturing of the final product of the resin compositions of the present invention can be achieved by standard fabrication methods such as injection molding, extrusion molding, blow molding, and compression molding. Furthermore, in addition to the additives described above, known additives, for example, reinforcing materials such as glass fibers, carbon fibers, and metal whiskers, fillers such as carbon blacks, calcium carbonate, and glass beads, lubricants such as paraffin waxes, and silicone oils, antioxidants such as hindered phenols, weather-resistant agents such as epoxy type monomers, and triazine, etc., can be further included in the fire-resistant polycarbonate resin composition of the present invention. Furthermore, polymers such as polycarbonates, polybutylene terephthalates, polyethylene terephthalates, polyethylenes, and polyethylenepropylene copolymers other than those mentioned above may be used in combination. For the flame-retardant component (C) used in the fire-resistant polycarbonate resin composition of the present invention, 2-20 parts by weight of a phosphate flame retardant, halogen flame retardant, or a brominated compound flame retardant can be used. When the amount used is less than 2 parts by weight, the improvement in the flame-retardant properties is inadequate, and when greater than 20 parts by weight is used, properties of the composition may be lost. For the phosphate flame retardants, phosphate compounds shown in the formula below: (In this case, R 1 , R 2 , R 3 , and R 4 each represents a hydrogen atom, or an organic group, but excludes the case of R 1 = R 2 = R 3 = R 4 = H. X' represents an organic group greater than divalent, p is either 0 or 1, q is an integer greater than 1, for example, 30, and r is an integer above 0.) can be mentioned. But it is not limited to said compounds. In the above-mentioned formula, "organic group" means alkyl groups, cycloalkyl groups, and aryl groups that may not be substituted. When the group is substituted, for example, alkyl groups, alkoxy groups, alkylthio groups, halogens, aryl groups, aryloxy groups, arylthio groups, halogenated aryl groups, etc., can be mentioned for substituents; furthermore, combinations of the above substituents (for example, arylalkoxyalkyl group, etc.), the above-mentioned substituents bonded with an oxygen atom, a sulfur atom, or nitrogen atom, etc. (for example, arylsulfonylaryl group, etc.) can be used as substituents. "Organic groups greater than divalent" means groups greater than divalent produced by removing at least one of the hydrogen atoms bonded to carbon atoms in the above-mentioned organic groups. For example, those derived from alkylene groups, and preferably, (substituted) phenylene groups, polynuclear phenols, for example, bisphenols, can be mentioned, and the relative locations of the free valence greater than 2 is not limited. In particular, hydroquinone, resorcinol, diphenylolmethane, diphenyloldimethylmethane, dihydroxydiphenyl, p,p'-dihydroxydiphenyl sulfone, dihydroxynaphthalene can be mentioned as suitable groups. For specific examples of phosphate compounds, trimethyl phosphate, triethyl phosphate, tributyl phosphate, trioctyl phosphate, tributhoxyethyl phosphate, triphenyl phosphate, tricresyl phosphate, cresylphenyl phosphate, octyldiphenyl phosphate, diisopropylphenyl phosphate, tris(chloroethyl)phosphate, tris(dichloropropyl)phosphate, tris(chloropropyl)phosphate, bis(2,3-dibromopropyl)-2,3-dichloropropylphosphate, tris(2,3-dibromopropyl)phosphate, bis(chloropropyl)monooctyl phosphate, bisphenol A bisphosphate, hydroxybisphosphate, resorcinol bisphosphate, trioxybenzene triphosphate, in which R 1 -R 4 is represented by an alkoxy, for example, methoxy, ethoxy, or propoxy, or (substituted) phenoxy, for example, phenoxy, methyl (substituted) phenoxy, and triphenyl phosphate, can be mentioned, and different kinds of bisphosphates are further desirable. Furthermore, polytetrafluoroethylene (referred to as to as PTFE hereinafter) of the component (D) in the present invention is a typical polymer that belongs to fluoro. resins produced by performing a polymerization for tetrafluoroethylene. The chemical resistance of said polymer is high, and long-term application at a temperature of about 260°C is possible, and friction is low. When said polytetrafluoroethylene is used in the above-mentioned mixing ratio of 0.1-1.0 part by weight, synergistic effect with the above-mentioned flame retardant is achieved, and the objective can be achieved. When the mixing ratio is less than 0.1 part by weight, the effect is insignificant. On the other hand, when greater than 1.0 part by weight, properties of the composition may deteriorate. Application examples In the following, the present invention is further disclosed with application examples. It should be noted that "parts" in application examples represents parts by weight. Materials used for production of the thermoplastic resin composition of the present invention are those described below. For the liquid crystal polymer LCP (1), Rodrun [transliteration] LC5000 (trademark, product of Unitika (Ltd.)) was used. For LCP (2), VECTRA A950 (trademark, product of Polyplastic (Ltd.)) was used. For polycarbonate PC (60), LX polycarbonate which has 60% phenolic end groups, with bottom-end sealed (product name; product of Nippon G. E. Plastics (Ltd.)) was used. For the phosphate flame retardant used as FR (1) phenyl resorcinol polyphosphate CR733 (trademark: Daihachi Chemical Co., Ltd.) was used. Furthermore, for brominated compound flame retardant, a brominated epoxy, Platherm EP-16 (trademark: product of Dainippon Ink Chemical Ind. (Ltd.)) was used for FR (2), and a brominated polycarbonate (Br = 25 wt%: product of GE Plastics (USA)) was used as FR (3). For the first polytetrafluoroethylene PTFE (1), Teflon 30J (trademark: product of Mitsui Du Pont Fluorochemicals (Ltd.) was used. For the second PTFE (2), 20 wt% of PTFE mixed with polycarbonate (product of GE Plastics (USA)) was used. However, the present invention is not limited by these material used. Each of the above-mentioned materials was used, and extrusion was performed from the biaxial extruder of Toshiba Machines (Ltd.) under the extrusion conditions of the screw rotation of 200 rpm, and a barrel temperature of 270-280°C, and [the extruded material] was cut to a prescribed length to produce a pellet. The above-mentioned pellet produced was used, and a sample piece for a flame-retardance test was produced by the 80-t injection molder of Toyo Machines and Metals (Ltd.). The molding conditions were set at a barrel temperature of 260°C and a die temperature of 50°C. The flame-retardant test was performed by the method specified in UL 94/V0. VI, and VII. The test was performed for five test pieces according to the test method specified in Bulletin 94 of Underwriters Laboratory Incorporated, "Flame Retardance Test for Material Classification" (referred to as to as UL-94, hereinafter) at a thickness of 1.59mm (1/16 inch). Based on the test method, the sample materials were evaluated for UL-94, V-0, V-1, and V-II based on the results of the five samples. Each of the UL-94 V standards is briefly explained below. V-0: The average flame retention time after removal of the burning flame is less than 5 sec, and none of the samples drop burning material that ignites the cotton. V-I: The average flame retention time after removal of the burning flame is less than 25 sec, and none of the samples drop burning material that ignites the cotton. V-II: The average flame retention time after removal of the burning flame is less than 25 sec, and samples drop burning material that ignites the cotton. Furthermore, the tensile test was performed by the standard method specified in ASTM method. The ratio of the components used, and the test results are as shown in Tables I-VI. In Table I, the phosphate flame retardant FR (1) was used as the flame retardant, PTFE (2), and polycarbonate were mixed in the ratios shown below; as a result, compositions with high flame retardance, high tensile elongation properties, and superior flow properties were produced. Comparative Example Application Example 1 Application Example Component ratio PC (60) 90 86 84 LCP (1) 10 10 10 Flame retardant FR (1) 4 6 PTFE (2) 1.0 1.0 1.0 Properties UL 94, 1.6 mm HB VI V0 UL 94, 0.8 mm HB VII V0 FM, 1.6 mm 40150 41300 41500 MI, 1.2 kg, 300°C 15.1 17.2 19.3 In Table II, the brominated epoxy flame retardant FR (2) was used as the flame retardant, PTFE (2), and polycarbonate were mixed at the ratios as shown below; as a result, compositions with a very high flame retardance, high tensile elongation properties, and relatively high flow properties were produced. Comparative Example 2 Application Examples 3 Application Examples 4 Component ratio PC (60) 90 86 84 LCP (1) 10 10 10 Flame retardant FM (2) 4 6 PTFE (2) 1.0 1.0 1.0 Properties UL 94, 1.6 mm HB V0 V0 UL 94, 0.8 mm HB VII VI FM, 1.6 mm 40150 40230 40210 MI, 1.2 kg, 300°C 15.1 14.9 14.8 In Table III, the brominated polycarbonate flame retardant FR (3) was used as the flame retardant, PTFE (1), and polycarbonate were mixed at the ratios as shown below; as a result, compositions with high flame retardance, high tensile elongation properties, and superior flow properties as well as superior HDT were produced. Comparative Example 5 Application Example 6 Application Example 7 Application Example 8 Component ratio PC (60) 90 86 84 81 LCP (1) 10 10 10 10 Flame retardant FM (3) 4 6 9 PTFE (1) 0.5 0.5 0.5 0.5 Properties UL 94, 1.6 mm HB VI V0 V0 UL 94, 0.8 mm HB VII VI V0 FM, 1.6 mm 40150 40170 40230 40180 HDT, 18.6 kg/cm 2 141 141 141 141 In Table IV, for the phosphate flame retardant FR (1) used as the flame retardant, PTFE (1), and polycarbonate mixed at the ratios as shown below, LCP (2) with a different structure than that of the liquid crystal polymer LCP (1) was mixed at the ratio shown below; as a result, compositions with high flame retardance, high tensile elongation properties, and superior HDT were produced. Comparative Example 9 Application Example 10 Application Example 11 Component ratio PC (60) 90 86 84 LCP (2) 10 10 10 Flame retardant FR (1) 4 6 PTFE (2) 1.0 1.0 1.0 Properties UL 94, 1.6 mm HB VI V0 UL 94, 0.8 mm HB VII V0 FM, 1.6 mm 37860 38230 39650 MI, 1.2 kg, 300°C 15.6 17.3 19.5 Compared with conventional products, the properties of the mold produced from the fire-resistant polycarbonate resin composition of the present invention show higher flame retardance, impact resistance, and high tensile strength as well. Because of the above-mentioned superior propeties, in particular, a high rigidity, the product can be phones, and PHP (personal handiphones).

Claims: A fire-resistant polycarbonate resin composition comprising: A) 5-50 parts by weight of liquid crystal polymer, B) 90-40 parts by weight of polycarbonate resin produced by hot-melt polymerization of an aromatic dihydroxy compound and a diester carbonate, having phenolic and nonphenolic end groups and having an equivalence ratio of phenolic end group (I) and nonphenolic end group (II), (I)/(II), which is greater than 1/19; C) 2-20 parts by weight of phosphate flame retardant wherein the total parts by weight of (A)+(B)+(C) is 100; and D) 0.1-1.0 part by weight per 100 parts of A)+(B)+(C) of polytetrafluoroethylene; The composition of claim 1 wherein the phenolic end group (I) has the formula and the nonphenolic end group (II) has the formula wherein R 1 and R 2 each represent a hydrogen atom, a linear or branched alkyl group with less than 20 carbons, unsubstituted or substituted with halogen atoms. The composition of claim 1 wherein the liquid crystal polymer is a thermotropic liquid crystal polyester. The composition of claim 3 wherein the polyester contains segments with the structure -O-R-O-, -CO-RCO- or -0-R-CO- wherein R is selected from and wherein the aromatic rings, aliphatic groups or alicyclic groups of R are unsubstituted or substituted with -Br, -Cl, -COOH, -CONH 2 , -CH 3 , -C(CH 3 ) 3 , or combinations thereof. The composition of claim 1 wherein the equivalence ratio is greater than 1/10. The composition of claim 5 wherein the equivalence ratio is greater than 1/5. The composition of claim 1 wherein the polycarbonate resin comprises a branched polycarbonate. The composition of claim 1 wherein the diester carbonate is diphenyl carbonate. The composition of claim 1 wherein the aromatic dihydroxy compound is 2,2-bis(4-hydroxyphenyl)propane.

Inventors: ITOI HIDEYUKI, LIU CHANG FENG, ITOI, HIDEYUKI, LIU, CHANG FENG
Applicants: GEN ELECTRIC, GENERAL ELECTRIC COMPANY
Application year: 1995
Main classification: C08L69
IPC codes: C08L69, C08L67, C08K5, C08L27