LASER WAVEGUIDE

Abstract: A laser waveguide is made by sputter-depositing an alloy of mainly aluminium and a little dopant e.g. Cr, in an oxidising atmosphere, onto a heated quartz substrate, and annealing to form ruby, which is then encased in a silica cladding.

Description: LASER WAVEGUTDF. . This invention relates to a laser waveguide and to a method of making it. One of the most useful solid state lasers produced in recent years is the very broad band tunable laser using titanium doped sapphire (Ti:Al2θ3). This has up to 20% conversion efficiency when pumped with an argon laser lamp but needs some 10W of argon power. It has therefore been proposed to make the Ti:Al2θ3 in the form of a planar or channel waveguide. This should reduce the pump threshold power by factors of up to 100 (i.e. a pump power down to say 100 mW). Since diode lasers exist at the few watt level one may then be able to drive the tunable laser via a diode with a second harmonic crystal to reach the ideal pump wavelength. However it would be desirable to improve the economy, performance, reproducibility and ease of production of such a material. According to the invention, a laser waveguide is made by sputter-depositing an alloy of aluminium and dopant onto a waveguide substrate in an oxidising atmosphere, e.g. oxygen. The dopant may be a transition metal, e.g. Ti, Cr, Co, Fe, and may be present in a proportion of 1 mole.K to 10^ moles aluminium. The substrate may be any material having transparency, a lower refractive index than the oxidised alloy, and a similar coefficient of expansion to the oxidised alloy. Quartz has proved suitable. The waveguide may be used when made as set forth above, for example for the ruby waveguide laser. Preferably, however, it is annealed, for example in the temperature range 800 to 1,400°C in an oxidising atmosphere in the case of the ruby but alternatively in a reducing atmosphere (particularly hydrogen) in the case of the titanium sapphire. Addition of hydrogen to control the valence state of the titanium impurities may alternatively be controlled by ion implantation of hydrogen following an annealing stage. To reduce surface scatter losses, the waveguide may be encased (for example by sputter coating) in any material that would be suitable as a cladding, e.g. an overlayer of silica may be applied. During the sputter deposition, the waveguide substrate is preferably maintained at a predetermined temperature, for example 400-C to 700°C more preferably 450-650°C e.g. 500°C or 600°C or at a temperature around midway (from one-third to two-thirds of the way) between room temperature and the annealing temperature, such a temperature both helping to minimise the differential expansion between the substrate and the deposited film during annealing on the one hand and during use at room temperature on the other hand, and allowing local diffusion during deposition to improve homogeneity of the deposited film. It is postulated that the deposited film is amorphous and remains so during annealing, which step encourages homogenisation and densification. In this case, the deposited film would as a necessary consequence be completely non-epitaxial with the substrate. The invention will now be described by way of example with reference to Figures 1 and 2, showing results from Examples 1 and 2 respectively. Examples of deposition conditions which produce waveguides with strong ruby or titanium emission arc as follows. General preparation conditions: a chamber base pressure of 6 x 10"" torr. The operating gas is introduced to a pressure of up to 3 x 10"^ torr typically as a mixture of 10 to 30% oxygen and 90 to 70% argon. 10 O 2 :90 A and 30 O :70 A both worked, the latter slightly better. An RF plasma has successfully been used but the deposition rate is slow and for more rapid film growth a combination of an RF with DC biased plasma w » used, giving a thirtyfold improvement in speed. The sputter source was an alloy made of the required metals, for example 99.6% Al with 0.4% Ti. The alloy composition determines the dopant level in the sapphire film. In the examples, the films were deposited on quartz at room temperature. However, a higher temperature can be used, and the phase transition of quartz at 573 β C (and in suitable cases that to form tridymite) may be exploited to advantage. Major improvements in quality are observed by depositing at 500°C or at 600°C. The luminescence performance has been monitored by cathodoluminescence and compared with single crystal luminescence ofruby and titanium sapphire samples. After the annealing treatments the thin film samples produce comparable spectra and luminescence intensity to that of bulk crystals for the same excitation conditions, even for non-optimised samples. These spectra are characteristic of the upper regions of the film and are independent of the substrate. Example 1 Figure 1 shows the ruby line spectra for a Cr/Ti doped 1.9 micron thick film sputter-deposited onto a quartz substrate as above and after annealing in oxygen at l,200 o C for 2 hours. In this example where chromium was introduced as a contaminant, the chromium line contribution was approximately 80% as intense as from a commercial bulk ruby. The titanium was 0.4%, the AI2O3 99.6 mole %. The spectrum was obtained from a 10 kV 0.3 μA beam at room temperature and was attenuated by a 6.2% filter. Example 2 Figure 2 is the corresponding spectrum for a 1.55 micron thick film of titanium sapphire deposited on quartz. After deposition the film was heat treated in a hydrogen furnace at 1 ,200°C for 4 hours. In this example the trace impurity, Cr, has been suppressed by the processing. The spectral response is as for bulk titanium sapphire and in this example the intensity was 95% that of the commercial crystals. The Ti was 0.4% and AI2O3 99.6 mole %. The spectrum was obtained from a 10 kV 0.5 μA beam at room temperature and was attenuated by a 6.2% filter.

Claims: CLAIMS 1. Making a laser waveguide by sputter-depositing an alloy of aluminium and dopant onto a waveguide substrate in an oxidising atmosphere. 2. Making a laser waveguide according to Claim 1, wherein the dopant is a transition metal. 3. Making a laser waveguide according to Claim 1 or 2, wherein the dopant is present in a proportion of 1 mole: 10^ to 10^ moles aluminium. 4. Making a laser waveguide according to any preceding claim, wherein, during sputter-deposition, the waveguide substrate is maintained at from 400°C to 700°C. 5. Making a laser waveguide according to any preceding claim, further comprising annealing the waveguide in an atmosphere which controls the oxidation state of the dopant to a desired value. 6. Making a laser waveguide according to any of Claims 1 to 4, further comprising annealing the waveguide and thereafter ion-implanting hydrogen to control the oxidation state of the dopant. 7. Making a laser waveguide according to Claim 5 or 6, wherein, during sputter-deposition, the waveguide substrate is maintained at a temperature from one-third to two-thirds of the way between room temperature and the annealing temperature. 8. Making a laser waveguide according to any preceding claim, further comprising * encasing it in a cladding overlayer of silica.

Inventors: MEEK PHILIP RONALD, NUNN PATRICIA JEAN THOMSON, TOWNSEND PETER DAVID, MEEK, PHILIP, RONALD, NUNN, PATRICIA, JEAN, THOMSON, TOWNSEND, PETER, DAVID
Applicants: BRITISH TECH GROUP, MEEK PHILIP RONALD, NUNN PATRICIA JEAN THOMSON, TOWNSEND PETER DAVID, BRITISH TECHNOLOGY GROUP LIMITED, MEEK, PHILIP, RONALD, NUNN, PATRICIA, JEAN, THOMSON, TOWNSEND, PETER, DAVID
Application year: 1995
Main classification: H01S3
IPC codes: H01S3