Thermoelectric device and a method of manufacturing thereof

Abstract: To provide a thermoelectric device (11) and a method of making thereof which is small, thin and capable of increasing a number of thermoelectric material chips (13, 14) per unit area. Respective thermoelectric material wafers (40) of P-type and N-type are bonded to substrates (42) for P-type and N-type provided with electrodes (43) each producing a gap therebetween. The thermoelectric material wafer bonded to the substrate is formed into the substrate bonded with thermoelectric material chips by cutting and eliminating unnecessary portions by utilising the gap. The substrates respectively bonded with P-type thermoelectric material chips and N-type thermoelectric material chips are opposed and distal ends of the chips and the electrodes on the substrate are bonded to thereby form PN junctions. Further, structures (44) are provided at surroundings of bonding portions on the substrate for positioning the bondings and for preventing a bonding material from oozing.

Description: The present invention relates to a thermoelectric device and a method of making thereof which make possible electric generation by temperature difference (thermal power generation) by Seebeck effect and thermoelectric cooling and heat generation by Peltier effect. A thermoelectric device, also known as a thermoelectric conversion element, is made by bonding a P-type thermoelectric material and a N-type thermoelectric material via an electrically conductive electrode such as a metal to thereby form a couple of PN junction. The thermoelectric device generates thermal electromotive force based on the Seebeck effect by a temperature difference applied between ends of the junction couple. Therefore, it has applications for a power generating device and conversely, a cooling device and a fine temperature control device utilising the so-called Peltier effect in which one side of a junction is cooled and the other side generates heat by making electric current flow in the device and the like. Generally, a thermoelectric device is used as a module in which a plurality of couples of PN junctions are connected in series to promote its function. In the structure of this module pieces of P-type and N-type thermoelectric materials (called thermoelectric material chip) having a shape of a rectangular parallelopiped of which size ranges from several hundreds µm to several mm are interposed between two sheets of electrically insulative substrates of alumina, aluminium nitride or the like, the P-type thermoelectric material chips and N-type thermoelectric material chips are PN-coupled by electrodes of an electrically conductive substance such as a metal formed on the substrates and at the same time the thermoelectric material chips are connected in series by these junctions. Figure 16 illustrates views showing an arrangement of electrodes of substrates and thermoelectric material chips at a section cut in a direction in parallel with the substrates and respective sections in a direction orthogonal to the substrates of a conventional thermoelectric device (hereinafter called a thermoelectric device including a module in which the above-mentioned plurality of thermoelectric chips are arranged) having such a structure. Figure 16A is a view showing an arrangement of electrodes and thermoelectric material chips on the substrate at a section in parallel with the substrates of the conventional thermoelectric device. In other words, it is a plan view for indicating the arrangement of the electrodes and the thermoelectric material chips from above the substrate. An electrode pattern shown by bold lines indicates an electrode 161 of a top substrate 160 whereas an electrode pattern shown by dotted lines indicates an electrode 162 of a bottom substrate 160. Further, a hatched quadrangle at the inside of a portion in which the electrode 161 of the top substrate intersects with the electrode 162 of the bottom substrate 160 indicates a portion in which a P-type thermoelectric material chip 163 or a N-type thermoelectric material chip 164 is disposed. Figures 16B, 16C and 16D are views showing respective longitudinal sections of Figure 16A taken along lines X1-X1', X2-X2' and Y1-Y1'. As is apparent from Figures 16, the arrangement of the thermoelectric material chips in the conventional thermoelectric device is in a lattice form arranged on the substrates and the P-type thermoelectric material chips and the N-type thermoelectric material chips are always arranged alternately in respective rows (X direction and Y direction in Figure 16A) constituting the lattice. An explanation will he given of a method of making the conventional thermoelectric device comprising a plurality of the thermoelectric material chips as follows. Figure 17 illustrates views showing an outline of working thermoelectric material in manufacturing the conventional thermoelectric device by longitudinal sections thereof. Figure 17A shows a section of a thermoelectric material 171 which has been worked in plate-like form or rod-like form. Layers 172 are formed for soldering by Ni etc. on both faces of the thermoelectric material to be bonded to the substrates by a plating method (Figure 17B). Next, P-type and N-type thermoelectric material chips 173 each having the layers 172 for soldering on both faces are formed by cutting the thermoelectric material (Figure 17C). Successively, each of the thermoelectric material chips made as above is disposed on a predetermined electrode on the substrate by using jigs or the like and a bonding is performed thereby forming the thermoelectric device. Figure 18 illustrates views showing a conventional method of manufacturing thermoelectric device by using the thermoelectric material chips and substrates provided with electrodes. Figure 18A shows relationship between the substrates 181 and thermoelectric material chips 182 before bonding. Electrodes 183 for forming PN junctions and bonding materials 184 for bonding the thermoelectric material chips 182 to surfaces of the substrates are formed on the substrates 181 in layers. Figure 18B shows a longitudinal sectional view in which a thermoelectric device 185 is formed by bonding the respective portions. Each thermoelectric material chip used for a thermoelectric device is a rectangular parallelopiped having sides with a size ranging from several hundreds µm to several mm. However in recent years, in an device used at around room temperature under a temperature difference of several tens degrees it has high function when its size and thickness ranges from several tens to several hundreds µm. For example, such a content is described in "The Transaction of the Institute of Electronics, Information and Communication Engineers C-II, Vol. J75-C-II, No. 8, pp. 416-424(JAPAN)" (in Japanese) and the like, while importance of design with respect to heat is set forth in the same paper. Further, the number of couples of thermoelectric material chips in one thermoelectric device has been several hundreds at most and its density has been approximately several tens couples/cm 3 . However, to increase the number of couples of thermoelectric material chips is one of very important factors in promoting its function and expanding its application. Especially, in power generation using a small temperature difference, generated electromotive force is in proportion to the number of couples of thermoelectric material chips and therefore, it is desirable to increase as many as possible the number of thermoelectric material chips connected in series in a thermoelectric device to generate a high voltage. Furthermore, also in case where a thermoelectric device is used as a cooling device or a temperature controlling device, electric current flowing in a device is enhanced when the number of thermoelectric material chips connected in series is small end it is necessary to enlarge wirings or to enlarge power sources. Accordingly, it is desirable to arrange as many thermoelectric material chips as possible in series. As stated above, miniaturising, thinning, thermal design and an increase in the number of the couples of the thermoelectric material chips connected in series in a single thermoelectric device amount to high function of the thermoelectric device and at the same time are becoming points of expanding its application. However, in making thermoelectric devices having the conventional structure shown in Figure 16 by the manufacturing method shown in Figure 17 and Figure 18, it is necessary to handle the thermoelectric material chips one by one and there is a limitation for reducing the size of chip and the size of device considering the operational performance and the working accuracy. Especially, thermoelectric materials having good function including Bi-Te series materials, Fe-Si series material and the like are substances having low mechanical strength. Therefore, in making a thermoelectric device in which the size of the thermoelectric material chip is no more than several hundreds µm or the number of chips is extremely large, the handling of the thermoelectric material is difficult and it is difficult to make thermoelectric device having the conventional structure by the conventional manufacturing method. Further, when a large number of thermoelectric elements are linked-up in series with one another, if there is a discontinuity even at just one part of the electrodes or the thermoelectric materials, the function of the device is impaired. This problem lowers the manufacturing yield and at the same time is considered important from the point of view of cost. EP 0506093A discloses a thermoelectric conversion module and method of making the same in which P-type and N-type thermoelectric semiconductor elements are alternately arranged in both the longitudinal and transverse directions. DE 4134685A discloses a thermoelectric device comprising two sheets of substrates, at least one of which is silicon, having a couple of P-type and N-type thermoelectric elements therebetween, the elements being PN-coupled via electrodes. WO 95/11583 discloses a thermoelectric module in which alternating bars of a first and a second thermoelectric material respectively are arranged parallel to each other and fixed into place on a first conductive pattern on a first substrate and a second conductive pattern on a second substrate, such that the bars are disposed between the substrates. It is an object of the present invention to provide a thermoelectric device which is small in scale and high in function and a method of making thereof by reducing the size of thermoelectric material chips and increasing the number of thermoelectric material chips per unit area (chip density). The present invention allows to adopt a new manufacturing method by improving the arrangement of thermoelectric material chips in the conventional thermoelectric device on substrates and provides a thermoelectric device in which the size of thermoelectric material chips is reduced and the chip density is enhanced. According to a first aspect of the present invention, there is provided a thermoelectric device comprising two sheets of substrates each having electrodes and at least one couple of P-type and N-type thermoelectric material elements interposed between the two sheets of substrates and PN-coupled via the electrodes, a sectional shape of each of the thermoelectric material elements cut in a plane parallel with the two sheets of substrates being quadrangular characterised in that the thermoelectric material elements and electrodes for PN junctions are arranged such that a straight line connecting centres of quadrangles of any adjacent, electrically coupled P-type and N-type thermoelectric material elements is not in an orthogonal or parallel relationship with any of the sides constituting the quadrangle that is the sectional shape of each thermoelectric material element forming a PN junction couple. According to a second aspect of the present invention, there is provided a method of making a thermoelectric device according to any one of the preceding claims comprising: a step of forming electrodes for performing a PN-coupling on each of the substrates (electrode forming step); a step of bonding either of P-type and N-type sheet-like thermoelectric materials to each of the two sheets of substrates (bonding step); a step of forming separate substrates bonded respectively with P-type and N-type thermoelectric material elements by cutting and eliminating portions of the bonded sheet-like thermoelectric materials in accordance with necessity (cutting and eliminating step); and a step of integrating the thermoelectric device by opposing the substrate bonded with the P-type thermoelectric material elements to the substrate bonded with the N-type thermoelectric material elements and bonding electrodes on the two sheets of substrates to distal ends of the thermoelectric material elements thereby forming couples of PN-junctions via the electrodes (integrating step). According to the method of making a thermoelectric device described above, after separately bonding the P-type and N-type thermoelectric material wafer respectively and separately to the two sheets of substrates each of which is previously provided with predetermined electrode wirings for forming the PN junctions, predetermined portions of the bonded thermoelectric material wafers are cut and eliminated thereby forming thermoelectric material chips bonded to the substrates. At this instance, the electrodes to be bonded to the thermoelectric material chips of different types show up. The substrate in a state in which the P-type thermoelectric material chips are bonded thereto and the substrate in a state in which the N-type thermoelectric material chips are bonded thereto both formed thereby are opposed and bonded together at predetermined locations by which the thermoelectric device can be manufactured. According to the method of making a thermoelectric device described above, the method further comprises a step of forming bumps made of at least one material selected from solder, gold, silver, copper and nickel having a predetermined shape and an arrangement pattern on at least one of surfaces of the plate-like thermoelectric materials and bonding the substrates to the thermoelectric materials through the bumps during the bonding step. Other materials similar to those listed may also be used. The invention will now be described, by way of example only, with reference to the accompanying diagrammatic Figures, in which; Figure 1 is a view showing outlook of a thermoelectric device according to the present invention. Figures 2A-B illustrate views showing sections of major portions taken along lines A-A' and B-B' of Figure 1. Figure 3 is view showing a relationship between arrangement of thermoelectric material chips and electrodes of a thermoelectric device shown in EMBODIMENT-1 of the present invention. Figures 4A-E illustrate views showing outline of steps of manufacturing the thermoelectric device according to the EMBODIMENT-1 of the present invention. Figure 5 is a view showing a relationship between arrangement of thermoelectric material chips and electrodes of a thermoelectric device by way of illustrative example. Figures 6A-F illustrate views showing outline of steps of manufacturing a thermoelectric device according to EMBODIMENT-2 of the present invention. Figures 7A-E illustrate views showing outline of steps of manufacturing a thermoelectric device according to EMBODIMENT-3 of the present invention. Figure 8A-F illustrate views showing outline of steps of manufacturing a thermoelectric device according to EMBODIMENT-4 of the present invention. Figures 9A-B illustrate views showing sections-of the thermoelectric material wafer after a grooving step among steps of manufacturing the thermoelectric device according to EMBODIMENT-4 of the present invention. Figures 10A-B illustrate views showing sections of major portions after a cutting and eliminating step among steps for manufacturing the thermoelectric device according to EMBODIMENT-4 of the present invention. Figure 11 is a view showing a finished section of the thermoelectric device according to EMBODIMENT-4 of the present invention. Figure 12 is a sectional view of a thermoelectric device having the structure related to the thermoelectric device of EMBODIMENT-4 of the present invention. Figures 13A-E illustrate views showing outline of steps of manufacturing a thermoelectric device according to EMBODIMENT-5 of the present invention. Figures 14A-E illustrate views showing outline of steps of manufacturing a thermoelectric device according to EMBODIMENT-6 of the present invention. Figure 15 is a view showing a relationship between arrangement of thermoelectric material chips and electrodes of a thermoelectric device according to EMBODIMENT-7 of the present invention. Figures 16A-D illustrate views showing a relationship between arrangement of thermoelectric material chips and electrodes of a conventional thermoelectric device. Figure 17A-C illustrate views showing outline of working thermoelectric material in manufacturing the conventional thermoelectric device in its longitudinal sectional view. Figure 18A-B illustrate views showing a method of making the conventional thermoelectric device wherein the thermoelectric device is manufactured by using thermoelectric material chips and substrates provided with electrodes. A detailed explanation will be given of the present invention based on embodiments in reference to the drawings. EMBODIMENT-1 Figure 1 is a view showing appearance of a thermoelectric device according to the present invention. The basic structure of a thermoelectric device 11 shown in Figure 1 comprises substrates 12, P-type thermoelectric material chips 13, N-type thermoelectric material chips 14 and electrodes 15 for PN junction. Figure 2A and Figure 2B are views showing sections of major portions taken along lines A-A' and B-B' of Figure 1 showing appearance of the thermoelectric device, respectively. In the sectional views of Figure 2, in addition to the major portions of the thermoelectric device, structures 23 of the present invention are formed on the substrates 21 at the surroundings of bonding portions. In Figure 2A, that is a sectional view taken along the line A-A' of Figure 1, the P-type thermoelectric material chips and the N-type thermoelectric material chips are arranged alternately whereas in Figure 2B, that is a sectional view taken along the tine B-B' of Figure 1, only P-type thermoelectric material chips or N-type thermoelectric material chips are arranged. Figure 3 is a plan view showing an electrode pattern and a positional relationship among the thermoelectric material chips viewing the thermoelectric device of Figure 1 from above. (Appearance and concept are shown in Figure 1, Figure 2 and Figure 3 and dimensions, a number of the thermoelectric material chips and the like are determined in accordance with the purpose). In Figure 3, among lines showing electrodes, bold lines show electrode patterns 32 of a top substrate and dotted lines show electrode patterns 33 of a bottom substrate. Incidentally, the expression of top substrate or bottom substrate is for convenience of explanation and naturally, any substrate can be a top or bottom one in the thermoelectric device. Further, quadrangles having two kinds of hatched lines respectively show a P-type thermoelectric material chip 34 and an N-type thermoelectric material chip 35. An explanation will be given of a thermoelectric device and a method of making thereof according to the present invention having such a structure with respect to a small-scaled thermoelectric device in which the size of the thermoelectric material chip is 100µm. As thermoelectric material, a sintered body of Bi-Te series material that is excellent in properties around room temperature was used. As main characteristics of the thermoelectric material, in P-type, the Seebeck coefficient was 205µV/°C, the specific resistivity was 0.95 mΩ cm and the heat conductivity was 1.5 W/m °C whereas in N-type, the Seebeck coefficient was 170µV/°C, the specific resistivity was 0.75 mΩ cm and the heat conductivity was 1.5 W/m °C. As material for the substrate, a silicon wafer having the thickness of 300µm that was electrically insulated by thermally oxidising the surface was used. With respect to the size of the element and the like, the height of the thermoelectric material chip was 500µm, the shape of a section of the thermoelectric material chip in parallel with the substrate was a square having a length of a side of 100µm as mentioned above, a distance between nearest thermoelectric material chips of a same type in Figure 3 was 200µm (300µm in centre distance), a distance between nearest thermoelectric material chips of different types was 70µm (300/√2 = about 210µm in centre distance) and a number of element couples arranged in a single device in series was 125. Figure 4 illustrates views showing outline of steps for making the thermoelectric device of this embodiment. As shown in Figure 4, the method of making is grossly classified into five steps. An explanation will be given thereof in due order. In a bump forming step, Figure 4A, a photoresist having the thickness of 50µm was coated on both faces of respective thermoelectric material wafers 40 of P-type and N-type having the thickness of 500µm and made of Bi-Te series sintered bodies. A resist layer having circular openings each having the diameter of opening of 90µm, the arrangement of which was in a desired pattern, was formed by exposing and developing the photoresist. The desired pattern was determined based on the above dimensions to be conformed to the arrangement of the thermoelectric material chips specified in Figure 3. Next, after cleaning by an acid or the like, a nickel plating of 40µm was performed on the openings by an electric plating method to form so-called nickel bumps. Next, a solder plating was performed on the nickel layer similarly by an electric plating method to form a solder layer of 30µm. The solder plating was performed to form a solder of tin and lead having a composition ratio of 6:4. Next, after removing the photoresist, a resin group flux was coated on the solder-plated layer, and a reflow treatment was performed at 230°C by which spherical solder bumps 41 having the diameter of approximately 100µm could have been formed on both the faces of the thermoelectric material wafer 40. In an electrode forming step, Figure 4B, films of chromium, nickel and gold in that order from the substrate respectively having thicknesses of 0.1µm, 3µm and 1µm were formed by a sputtering method on the surface of a silicon wafer substrate 42 having the thickness of 300µm on which an oxide layer of 0.5µm was formed by thermal oxidation. Next, electrodes 43 were formed on the top and bottom substrates by photolithography conforming to the electrodes pattern of Figure 3. Further, two kinds of doughnut-shaped structures 44 of a polyamide group photoresist were formed by photolithography at the surroundings of portions thereof to which the P-type thermoelectric material and the N-type thermoelectric material were bonded through the solder bumps. With respect to the size of the structure 44 comprising the polyamide group photoresist, in the two sheets of substrates constituting the thermoelectric device, the inner diameter of the doughnut shape was 120µm, the outer diameter was 150µm and the height was 30µm at a position where the P-type thermoelectric material chip was disposed and the inner diameter was 140µm, the outer diameter was 170µm and the height was 30µm at a position where the N-type thermoelectric material chip was disposed in one substrate, whereas in the other substrate, the inner diameter was 140µm, the outer diameter was 170µm and the height was 30µm at a position where the P-type thermoelectric material chip was disposed and the inner diameter was 120µm, the outer diameter was 150µm and the height was 30µm at a position where the N-type thermoelectric material chip was disposed. In a bonding step, Figure 4C, each thermoelectric material wafer 40 having the bumps 41 formed in the bump forming step of Figure 4A was opposed to a respective substrate 42 having the electrodes 43 and the doughnut-shaped structures 44 in the vicinity of the bonding portions formed by the electrodes forming step of Figure 4B, predetermined positioning was performed and the thermoelectric material wafer 40 and the substrate 42 were bonded by melting the solder. Further, in the bonding of the P-type thermoelectric material wafer to the substrate, the solder bumps formed on the surface of the P-type thermoelectric material wafer were inserted into the inside of the smaller doughnut-type structures having the inner diameter of 120µm, the outer diameter of 150µm and the height of 30µm which had been formed on the substrate thereby positioning the thermoelectric material wafer 40 to the substrate 42. Similarly, in bonding the N-type thermoelectric material wafer to the substrate, the solder bumps formed on the surface of the N-type thermoelectric material wafer were inserted into the smaller doughnut-shaped structures having the inner diameter of 120µm, the outer diameter of 150µm and the height of 30µm which had been formed on the substrate thereby positioning the thermoelectric material wafer 40 to the substrate 42. In this procedure, smaller ones of the doughnut-shaped structures having two kinds of sizes which had been formed on the substrate in bonding the thermoelectric material wafer 40 to the substrate 42 to dispense with incorrect bonding positions and to promote mutual positioning accuracy. In a cutting and eliminating step, Figure 4D, portions of the thermoelectric material wafer 40 bonded to the substrate 42 were formed into thermoelectric material chips 45 bonded to the substrate 42 by cutting and eliminating other portions of the thermoelectric material wafer. At this instance, portions of the substrate 42 or the electrodes 43 might simultaneously be cut and eliminated in accordance with the necessity. In this embodiment, the cutting and eliminating step of Figure 4D was performed by using a dicing saw that was used in cutting silicon semiconductors and the like. A blade having a thickness of 200µm was used in the cutting and eliminating. The thickness of the blade was selected under conditions wherein the length of the side of the thermoelectric material chip 45 in this embodiment was 100µm, the centre distance between the nearest thermoelectric material chips of a same type was 300µm and the thermoelectric material chips of different types were bonded in the positional relationship prescribed in Figure 3. The cutting and eliminating unnecessary portions of the thermoelectric material was performed at central portions between the solder bumps 41 and at the same time the height of the blade was adjusted so as not to destroy the electrodes 43 on the substrate by utilising a gap between the thermoelectric material wafer 40 and the substrate 42 comprising nickel bumps having the height of 40µm. With respect to the thermoelectric material of each type, the substrate 42 bonded substantially with 125 pieces of the thermoelectric material chip 45 was manufactured by longitudinally and transversely cutting and eliminating other portions by the blade of the dicing saw. With regard to the substrate 42 bonded substantially with 125 pieces of the thermoelectric material chips 45, the 125 pieces thereof were substantially related to PN junctions in view of their arrangement when the rectangular thermoelectric material wafer was used under the arrangement and the constitution of the thermoelectric material chips prescribed in Figure 3 and when the solder bumps were formed in 11 rows in the longitudinal direction by 12 rows in the transverse direction (132 pieces in total). In this case, with regard to unnecessary chips at outer peripheral portions, if any means of bonding was not provided, they were eliminated in the cutting and eliminating step resulting in no problem. However, they might be preserved by bonding them to the substrate by any means since mechanical reinforcement and electric reliability of the formed thermoelectric device could be promoted by preserving the unnecessary chips by bonding them to the substrate. In this case, when enhancing of strength of the formed thermoelectric device was aimed, the thermoelectric device could be manufactured with no hindrance in steps if bonding pads for electrically isolated dummy chips were previously formed on the substrate in forming the electrodes and bonded thereto as in the other bumps. Further, by bonding bumps of the unnecessary chips to the substrate in which pads wired to short-circuit near electrodes were previously formed, it was possible to preserve the chips and to achieve the mechanical reinforcement and the promotion of electric bonding reliability of the thermoelectric material chips at the outermost peripheral portions. In an integrating step, Figure 4E, two sheets of the substrates 42 respectively bonded with the thermoelectric material chips 45 of different types are opposed, the solder bumps formed on the distal ends of the respective chips and the electrodes 43 formed on the substrate were positioned to locations for bonding, the assembly was pressed and heated to melt the solder whereby the thermoelectric material chips 45 and the electrodes 43 on the substrate 42 were bonded thereby finishing the thermoelectric device having the PN junctions on the top and the bottom substrates. Further, positioning in bonding was performed by inserting the solder bumps 41 formed on the distal ends of the thermoelectric material chips 45 of respective types into the inside of the doughnut-shaped structures of the remaining larger ones (internal diameter; 140µm, outer diameter; 170µm height; 30µm) among the structures 44 formed on the substrate of different types to be bonded. Larger ones of the doughnut-shaped structures were selected in the positioning to facilitate the positioning of the thermoelectric material chips and the electrodes of the substrate and to prevent the solder from oozing in this embodiment, whereby their effect as well as that of the smaller doughnut-shaped structures in the bonding step of Figure 4C were sufficiently provided. With respect to the final outer dimensions of the thermoelectric device formed as above, the thickness was approximately 1.2 mm (as for the components of the thickness, the thickness of the thermoelectric material chip was 0.5 mm, the thickness of the top and the bottom substrates respectively was 0.3 mm, the heights of the bonding material and the nickel bump in sum at the top and the bottom bonding portion were respectively 0.05 mm), the size was 4 mm x 4 mm in the size of the lower substrate provided with input and output electrodes and electrically the internal resistance was 120Ω. The size of the thermoelectric device of this embodiment having the thermoelectric material chips and the positional and arranging relationships of the electrodes for PN bonding as shown by Figure 3 and manufactured by the method of making thereof, could not be achieved by the conventional manufacturing method in which the thermoelectric device was formed by forming the thermoelectric material chips and inserting them between the top and the bottom substrates. When lead wires were connected to input and output electrodes of the thermoelectric device and respective characteristics were investigated, the following results was provided. With respect to the power generation function based on the Seebeck effect, the open voltage between the substrates in a temperature difference of 2°C was 90 mV and an output of 80 mV -70 µA was obtained by attaching a load resistor of 1 KΩ to the outside when a temperature difference of 2°C was provided between the substrates. Further, when 16 pieces of the thermoelectric devices having 125 couples of PN junctions were connected in series and was carried by enclosing them in a quartz oscillator type electronic wrist watch, the watch could be driven at room temperature of 20°C. With respect to the function of a cooling and heat generating element based on the Peltier effect, when an aluminium radiating plate was adhered to the substrate on the heat generating side by a silicone adhering agent having high thermal conductivity and a voltage of 6 V was applied between input electrodes, electric current of approximately 50 mA flowed and a phenomenon was caused on the surface of the substrate on the heat absorbing side in which moisture in the air was instantaneously frozen by which it was proven that the function of the thermoelectric device as a Peltier device was very excellent. Illustrative example Figure 5 is a plan view viewing from a top substrate for explaining outline of electrodes and thermoelectric material chips on a substrate of a thermoelectric device by way of illustrative example. In Figure 5, among lines showing electrodes, bold lines indicate an electrode pattern 50 of a top substrate and dotted lines indicate electrode pattern 51 of a bottom substrate. Incidentally, the expression of top substrate or bottom substrate is for convenience of explanation and naturally, any substrate may be a top or bottom one in the thermoelectric device. Further, quadrangles provided with two kinds of hatched lines respectively indicate a P-type thermoelectric material chip 52 and a N-type thermoelectric material chip 53. Further, thermoelectric material chips provided at the outer peripheral portions of the thermoelectric device that are not related to PN junctions (hereafter called dummy chips), are bonded and fixed to the top substrate and the bottom substrate by dummy electrodes 54 of the top substrate and dummy electrodes 55 of the bottom substrate. In Figure 5, the dummy chip is connected to the dummy electrode on one substrate and connected to the electrode performing PN junction on the other substrate, however, there may be dummy electrodes connected to both of the substrates. In either case, the dummy chips perform mechanical reinforcement of the thermoelectric device comprising small-scaled thermoelectric material chips manufactured in this embodiment. As shown in figure 5, with regard to the arrangement of the thermoelectric material chips in the thermoelectric device of this embodiment, in viewing a certain row in X direction, only P-type thermoelectric material chips or only N-type thermoelectric material chips are arranged and the rows of the P-type thermoelectric material chips and the rows of the N-type thermoelectric material chips are alternately arranged. Meanwhile, in Y direction, in viewing a certain row, the P-type thermoelectric material chips and the N-type thermoelectric material chips are alternately arranged. In this embodiment, manufactured was the thermoelectric device having such a structure and the arrangement of the thermoelectric material chips in which the size of the thermoelectric material chip in a section in parallel with the substrates was 500µm, the height was 500µm, the centre distance between nearest thermoelectric material chips was 1,000µm and the number of the thermoelectric material chips (including dummy chips) was 64 pieces in sum of the P-type and N-type ones. As thermoelectric material, a sintered body of Bi-Te series material which was the same as that in EMBODIMENT-1 and of which function was excellent at around room temperature was used. As major characteristics of the thermoelectric material, in P-type, the Seebeck coefficient was 205µV/°C, the specific resistivity was 0.95 mΩ cm, the heat conductivity was 1.5 W/m °C, and in N-type, the Seebeck coefficient was 170µV/°C, the specific resistivity was 0.75 mΩ cm and the heat conductivity was 1.5 W/m °C. Alumina having the heat conductivity of 20 W/m °C was used as substrate material. Embodiment-2 Figure 6 is a view showing outline of steps for manufacturing a thermoelectric device in accordance with embodiment-2. An explanation will be given to respective steps in reference to Figure 6 as follows. In a bonding layer forming step, Figure 6A, a nickel plating was performed on both faces to be bonded to the substrate among surfaces of a thermoelectric material wafer 60 having the thickness of 500µm by a wet plating method by which a nickel layer 61 having the thickness of 10µm was formed. One of the faces on which the nickel layers were formed was masked, solder plating having the solder composition of tin:lead = 1:9 was performed on the other face by a wet plating method by which a solder layer 62 having the thickness of 30µm was formed. Next, the plating mask was stripped, the solder layer 62 having the solder composition of tin:lead = 1:9 was masked and a solder plating having the solder composition of tin:lead = 6:4 was performed on another nickel layer 61 by a wet plating method by which a solder layer 63 having the thickness of 30µm was formed, and by stripping the plating mask a thermoelectric material wafer having the solder layer 62 with the solder composition of tin:lead = 1:9 on one face and the solder layer 63 with the solder composition of tin:lead = 6:4 on the other face, was formed. Next, a rosin group flux was coated on the solder layer 62 and 63 on the both faces and the solder was reflowed at 350° C by which the solder layers were made uniform and the surfaces thereof were cleaned. Incidentally, in regard of steps, the reflow treatment may be performed after a grooving step that is successive to the bonding layer forming step. In a grooving step, Figure 6B, a dicing saw was used by which grooving was performed longitudinally and transversely on the side of the solder layer 62 having the solder composition of tin:lead = 1:9 up to the depth of 90µm from the surface of the solder layer 62 by a blade having the blade width of 1.5 mm. The feed of the blade between grooves was determined to be 2 mm such that an interval of a protrusion formed between the grooves became 0. 5 mm that was the size of the thermoelectric material chip. The depth of grooving was determined to be 90µm from the surface of the solder layer such that contiguous protrusions 68 were not short circuited in a later bonding step and the grooves 67 produced a gap between the thermoelectric material wafer and the substrate that was necessary in a later step of chip formation by cutting and eliminating. In an electrode forming step, Figure 6C, a copper plate having the thickness of 0.1 mm on an alumina substrate 64 having the thickness of 0.5 mm was worked into electrodes 65 by photo etching constituting the top substrate or the bottom substrate pattern as shown in Figure 5. In a bonding step, Figure 6D, protrusions 68 of the thermoelectric wafer 60 and the electrodes 65 were positioned and the solder layer 62 having the composition of tin:lead = 1:9 of the protrusions was melted by which the electrodes 60 and the thermoelectric wafer were bonded. The bonding temperature at this instance was 340° C. In a cutting and eliminating step, Figure 6E, cutting and eliminating were performed by using a dicing saw with a blade having the blade width of 1.5 mm with respect to cutting in X direction specified in Figure 5 and with a blade having the blade width of 0.5 mm with respect to cutting in Y direction without destroying the electrodes 65 on the substrate 64 in which blade edges were disposed at grooves (recess) 67 formed in the grooving step of Figure 6B, thereby forming the thermoelectric material chips 66. In an integrating step, Figure 6F, two sheets of the substrates 64 respectively bonded with the thermoelectric material chips 66 of different types are opposed, the solder layer 63 having the solder composition of tin:lead = 6:4 formed on the distal ends of the respective chips and the electrodes 65 formed on the substrate 64 were positioned at locations at which the both were to be bonded, the assembly was heated while being pressed to melt the solder whereby the thermoelectric material chips 66 were bonded to the electrodes 65 on the substrates 64 by which the thermoelectric device having the PN junctions on the top and the bottom substrates could have been finished. Further, the temperature in bonding was determined to be 230° C at which the solder having the composition of tin:lead = 1:9 for the previous bonding was not molten. Accordingly, the integrating step could be performed without toppling or shifting the thermoelectric material chips even if structures were not provided around the bonding portions. The thermoelectric device of this embodiment was made by the manufacturing method essentially similar to that in making the thermoelectric device described in EMBODIMENT-1. Although the locations and arrangement of the thermoelectric material chips and the arrangement of the electrodes for PN bonding in EMBODIMENT-1 are preferable when the thermoelectric material chips are extremely small, the locations and arrangement of the thermoelectric material chips and the arrangement of the electrodes for PN bonding of this embodiment are preferable to enhance the density of the thermoelectric material chips in the thermoelectric device. Further, the thermoelectric device and the method of making thereof according to this embodiment are preferable to restrict the amount of the thermoelectric material to be removed in the cutting and eliminating step. With regard to the final outer dimensions of the thermoelectric device formed as above, the thickness was approximately 1.5 mm and the size was 9 mm x 8 mm in the size of the bottom substrate provided with input and output electrodes and electrically the internal resistance was 1Ω. Its function as a cooling and heat generating element based on the Peltier effect was investigated by connecting lead wires to input electrodes of the thermoelectric device. When an aluminium radiating plate was adhered to the substrate on the heat generating side by a silicone adhesive agent having high conductivity and when voltage of 1 V was applied between the input electrodes, current of approximately 1 A flowed and a rapid cooling was caused on the side of the heat absorbing substrate. A ratio of input power to an amount of heat absorbing, so called COP (coefficient of performance) was 0.55 at a temperature difference of 20°C which proved that this thermoelectric device has excellent function. EMBODIMENT-3 An explanation will be given of making a small-scaled thermoelectric device in which the size of thermoelectric material chips is 50µm with respect to a thermoelectric device having an electrode pattern similar to that in EMBODIMENT-1. As thermoelectric material, used was a sintered body of Bi-Te series material which was the same as that in EMBODIMENT-1 and was excellent in its function around room temperature. With regard to major characteristics of the thermoelectric material, in P-type, the Seebeck coefficient was 205µV/°C, the specific resistivity was 0.95 mΩ cm and the heat conductivity was 1.5 W/m °C and in N-type, the Seebeck coefficient was 170µV/°C, the specific resistivity was 0.75mΩ cm, and the heat conductivity was 1.5 W/m °C. As substrate material, a silicon wafer having the thickness of 300µm which was electrically insulated by thermally oxidising the surface was used. With regard to the size of the device and the like, the height of the thermoelectric chip was 500µm, the shape of a thermoelectric material chip at a section in parallel with the substrate was a square, the length of which side was 50µm as above, the distance between nearest thermoelectric material chips of a same kind was 100µm (150µm in centre distance), the distance between nearest thermoelectric material chips of different types was 35µm (150/√2 = about 110 µm in centre distance) and a number of element couples arranged in series in a single element was 51. Figure 7 is a view showing outline of steps for manufacturing the thermoelectric device of this embodiment. As shown in Figure 7, the manufacturing method is grossly classified into five steps. An explanation will be given thereto in due order. In a bump forming step, Figure 7A, a photoresist having the thickness of 20µm was coated on the both faces of thermoelectric material wafers 70 respectively of P-type and N-type having the thickness of 500µm each of which was made of a Bi-Te series sintered body. A pattern of the resist was formed by exposing and developing the photoresist such that circular openings each having the diameter of opening of 45µm were formed and their arrangement was in a desired pattern. The desired pattern was determined based on the above-mentioned dimensions such that the pattern conformed to the arrangement of the thermoelectric material chips in Figure 3. A nickel plating of 20 µm was firstly performed on the openings to form so-called nickel bumps by an electric plating method after cleaning them by an acid or the like. Next, a solder plating was performed on the nickel layer similarly by an electric plating method to form a solder layer of 30µm. Here, the solder plating was performed such that the ratio of tin:lead became 6:4. Next, when a rosin group flux was coated on the solder-plated layer after stripping the photoresist and a reflow treatment was performed thereon at 230°C, spherical solder bumps 71 having the diameter of approximately 50µm could be formed on the both faces of the thermoelectric material wafer 70. In an electrode forming step, Figure 7B, films of chromium, nickel and gold respectively having the thicknesses of 0.1µm, 2µm and 1µm in that order from the side of the substrate were formed by a sputtering method on the surface of a silicon wafer substrate 72 having the thickness of 300µm of which surface is provided with an oxide layer of 0.5µm by thermal oxidation. Next, electrodes 73 were formed on the top and bottom substrates by photolithography such that they conformed to the electrode patterns of Figure 3. Further, two kinds of structures 74 each having a bonding portion in a hollow cylindrical form around a portion of the electrode to be bonded to the P-type thermoelectric material or the N-type thermoelectric material through the solder humps were formed by photolithography using a thick film photoresist. With regard to the shape and the size of the structures 74 constituted by the thick film photoresist, in one substrate among two sheets of substrates constituting the thermoelectric device, the diameter of the cylinder at a location where the P-type thermoelectric material chip was disposed was 60µm, the diameter thereof at a location where the N-type thermoelectric material chip was disposed was 70µm and the other portions of the substrate was covered with the resist having the thickness of 40µm. In the other substrate, the diameter at a location where the P-type thermoelectric material chips was disposed was 70µm, the diameter at a location where the N-type thermoelectric material chip was disposed was 60µm and the other portion of the substrate was covered with the resist having the thickness of 40µm. Here, the thickness of the resist was determined to be 40µm to use the structures formed thereby to produce a gap in a successive step shown in Figure 7C of bonding the thermoelectric material wafer 70 to the substrate 72 and a step shown in Figure 7D successive to the step of Figure 7C of cutting and eliminating the thermoelectric material wafer 70. In EMBODIMENT-1, the gap was produced by the nickel bumps. In EMBODIMENT-4, the gap between the thermoelectric material wafer 70 and the substrate 72 necessary in the cutting and eliminating step of Figure 7D was 30µm or more. By contrast, in forming the bumps 71 on the thermoelectric material wafer 70 in the preceding step, it was difficult to render the height of the nickel bumps producing the gap to be 20µm or more due to a limitation of photolithography technology and plating technology. In a bonding step shown in Figure 7C, after performing a predetermined positioning between the thermoelectric material wafer 70 attached with the solder bumps 71 formed in the bump forming step of Figure 7A and the substrate 72 on which the electrodes 73 and the structures 74 in the vicinities of the bonding portions both were formed in the electrode forming step of Figure 7B, the solder was molten and the thermoelectric material wafer 70 was bonded to the substrate 72. Further, in bonding the P-type thermoelectric material wafer to the substrate, the positioning between the thermoelectric material wafer 70 and the substrate 72 was performed by inserting the solder bumps formed on the surface of the P-type thermoelectric material wafer into the inside of openings for bonding of the structures 74 having the diameter of 60µm that were formed on the substrate. Similarly, in bonding the N-type thermoelectric material wafer to the substrate, the positioning between the thermoelectric material wafer 70 and the substrate 72 was performed by inserting the solder bumps formed on the surface of the N-type thermoelectric material wafer into the inside of openings for bonding of the structure 74 having the diameter of 60µm that were formed on the substrate. The smaller ones of the openings for bonding of the two kinds of structures 74 that were formed on the substrate were used in bonding the thermoelectric material wafer 70 to the substrate 72 to dispense with wrong bonding locations and to promote the mutual positioning accuracy. In a cutting and eliminating step of Figure 7D, the thermoelectric wafer 70 bonded to the substrate 72 was transformed into thermoelectric material chips 75 bonded to the substrate 72 by cutting and eliminating portions of the thermoelectric material wafer. At this instance, portions of the substrate 72 might be cut and eliminated in accordance with the necessity. In this embodiment, the cutting and eliminating step of Figure 7D was performed by using a dicing saw that was used in cutting silicon semiconductors and the like. A blade having the thickness of 100µ m was used in the cutting and eliminating step. The thickness of the blade was selected under conditions in which the length of a side of a square of the thermoelectric material chip 70 in this embodiment was 50µm, the distance between nearest thermoelectric material chips of a same kind was 100µm and the thermoelectric material chips of different kinds were bonded in the positional relationship shown in Figure 3. The cutting and eliminating unnecessary portions of the thermoelectric material was performed at central portions between the solder bumps 71 and at the same time by adjusting the height of the blade so as not to destroy the electrodes 73 on the substrate by using a gap between the thermoelectric material wafer 70 and the substrate 72 formed by the structures 74 having the height of 40µm. The substrate 72 substantially bonded with 51 pieces of thermoelectric material chips 75 was manufactured with respect to the thermoelectric materials of respective types by longitudinally and transversely cutting and eliminating the portions by the blade of the dicing saw. Here, substantially 51 pieces of the thermoelectric material chips 75 were bonded to the substrate 72, in which, in case where a rectangular thermoelectric material wafer was used in the arrangement and the constitution of the thermoelectric material chips in Figure 3 and the solder bumps in 8 rows in the longitudinal direction by 7 columns in the transverse direction (56 pieces in sum) were formed, in regard of the arrangement, 51 pierces were substantially related to PN junctions. In this case, unnecessary portions of chips at outer peripheral portions were removed by the cutting and eliminating step resulting in no problem if no bonding measure was performed. However, the unnecessary chips might be connected to the substrates and preserved since the mechanical reinforcement and the electrical reliability could be promoted by bonding them to the substrate in preserving them. In this case, when the enhancement of the strength of the manufactured thermoelectric device was aimed, the thermoelectric device could be manufactured with no hindrance in steps if connecting pads for electrically isolated dummies are previously provided on the substrate in making the electrodes and bonded thereto as in the other bumps. Further, by short circuiting the pads to near electrodes at which unnecessary chips are bonded to the substrate, the chips could be preserved and the mechanical reinforcement and the electrical bonding reliability of the thermoelectric material chips at outermost peripheral portions could be promoted. In an integrating step, Figure 7E, two sheets of the substrates 72 respectively bonded with the thermoelectric material chips 75 of different types were opposed, the solder bumps 71 formed on the distal ends of the respective chips and the electrodes 73 formed on the substrates were positioned to locations to be bonded, the assembly was heated while being pressed to melt the solder, whereby the thermoelectric material chips 15 and the electrodes 73 of the substrate 72 were bonded by which the thermoelectric device having the PN junctions on the top and the bottom of the substrates could have been finished. Further, the positioning in bonding was performed by inserting the solder bumps 71 formed on the distal ends of the thermoelectric material chips 75 of respective types into the inside of the remaining larger ones (70 µm in diameter) among the openings for bonding of the structures 74 formed on the substrates of different types to be bonded. The larger ones of the openings for bonding of the structures 74 were selected in positioning to facilitate the positioning of the thermoelectric material chips and the substrate electrodes and to prevent the solder from oozing and in this embodiment, the effect as well as that of the smaller openings for bonding of the structure 74 in the bonding step of Figure 7C were sufficiently provided. With respect to the final outer dimensions of the thermoelectric device manufactured as above, the thickness was approximately 1.2mm, the size was 2mm x 2mm in the size of the bottom substrate provided with input and output electrodes and electrically the internal resistance was 180Ω. When lead wires were connected to the input and output electrodes of the thermoelectric device and respective properties were investigated, the following result was provided. With regard to the power generating function based on the Seebeck effect, the open voltage between the substrates in a temperature difference of 2°C was 35mV and an output of 30mV - 30µA was provided when a load resistor of 1KΩ was attached to the outside and a temperature of 2°C was given between the substrates. Further, when 49 pieces of the thermoelectric device having 51 couples of the PN junctions were connected in series and the assembly was carried in a wrist watch, the watch could be driven at room temperature of 20°C. With respect to the function as a cooling and heat generating element based on the Peltier effect, an aluminium irradiating plate was adhered to the substrate on the heat generating side of the substrate by a silicone adhesive agent having high thermal conductivity and a voltage of 2V was applied between the input electrodes, current of approximately 10 mA flowed and a phenomenon in which moisture in the air was instantaneously frozen on the surface of the substrate at the heat absorbing side was caused by which it was proved that the function of the thermoelectric device as a Peltier device was very excellent. EMBODIMENT-4 As explanation will be given of making a small-scaled thermoelectric device having structure in which the sectional shape of a thermoelectric material chip is thick (70µm) on the side of one substrate and thin (50µm) on the side of the other substrate in a thermal device having structure of electrodes as in EMBODIMENT-1. As thermoelectric material, a sintered body of Bi-Te series material was similarly used. As substrate material, a silicon wafer having the thickness of 300µm that was electrically insulated by thermally oxidising its surface was used. With respect to the size of the element and the like, the height of thermoelectric material chips was 500µm, the shape of the thermoelectric material chip at sections in parallel with the substrate was a square, the length of the side of the square at a section was 50µm as mentioned above and that at a section proximate to one bonding portion was 70µm. The centre distance between nearest thermoelectric material chips of a same kind arranged as in Figure 3 was 270µm, the centre distance between nearest thermoelectric material chips of different types was 270/√2 = about 190µm and a number of element couples arranged in a single element in series was 51. (The calculation of distance was performed with the size of the chip as 70µm). Figure 8 illustrates views showing outline of steps for manufacturing the thermoelectric device of EMBODIMENT-4. As shown in Figure 3, the manufacturing method is grossly classified into 6 steps. An explanation will be given thereto in due order. In a bump forming step, Figure 8A, a photoresist having the thickness of 10µm was coated on both faces of respective thermoelectric material wafers 40 of P-type and N-type each comprising a Bi-Te series sintered body having the thickness of 500µm. A resist layer having circular openings of which diameter of opening was 40µm on one face, of which diameter of opening was 60µm on the other face and the arrangement of which is in a desired pattern, was formed by exposing and developing the photoresist. Further, the desired pattern was determined based on the above dimensions such that the pattern conformed to the arrangement of the thermoelectric material chips in Figure 3. Next, a nickel plating of 10µm was performed firstly on the both faces of the openings by an electric plating method after cleaning them by an acid or the like by which so-called nickel bumps were formed. Next, a solder plating was performed on the nickel layer similarly by an electric plating method to form a solder layer of 30µm. The solder plating was performed such that a ratio of tin to lead was 6:4. Next, when a rosin group flux was coated on the solder plated layer after removing the photoresist and a reflow treatment was performed at 230°C, spherical solder bumps 81 having the diameter of approximately 50µm on one face and the diameter of 70µm on the other face could be formed on both the faces of each thermoelectric material wafer 80. In a grooving step, Figure 8B, different grooving operations were performed on the P-type thermoelectric material wafer 90 and the N-type thermoelectric material wafer 92. Figure 9 illustrates views showing the width and the depth of the grooving in the grooving step of this embodiment. As shown in Figure 9A, firstly, grooving of the depth of 150µm was longitudinally and transversely performed at central portions between the solder bumps by a dicing saw attached with a blade having the blade width of 160µm on surfaces on which the solder bumps having the diameter of 70µm were formed with respect to the P-type thermoelectric material wafer 90. Thereby, grooves having the width of 160µm and the depth of 150µm could be formed and therefore, the P-type thermoelectric material wafer 90 in which the solder bumps having the diameter of approximately 70µm were formed on protrusions having the length of a side of 70µm and the height from the bottom of the groove of 150µ m could be formed. As shown in Figure 9B, grooving of the depth of 350µm was performed longitudinally and transversely at central portions between the bumps by a dicing saw attached with a blade having the blade width of 180µm on surfaces on which the solder bumps having the diameter of 50µm were formed with respect to the N-type thermoelectric material wafer 92. Thereby, grooves having the width of 180µm and the depth of 350µm could be formed and therefore, the N-type thermoelectric material wafer 92 in which the solder bumps having the diameter of approximately 50µm were formed on protrusions having the length of a side of 50µm and the depth from the bottom of the groove of 350µm could be formed. The reason of the grooving formed in such a way was that in addition to forming a gap between the thermoelectric material wafer and the substrate that is necessary in a bonding step shown in Figure 8B and in a cutting and eliminating step shown in Figure 8E that are later steps, by changing the sectional shape of the thermoelectric material chip in direction orthogonal to the substrates, in case where the manufactured thermoelectric device was used as a Peltier element, Joule heat by flowing current was to be generated as much as possible on the side of a heat radiating substrate and heat flow to the side of a heat absorbing substrate was to be prevented. In an electrode forming step, in Figure 8C, films of chromium, nickel and gold in that order from the substrate respectively having the thicknesses of 0. 1µm, 1µm and 0.1µm were formed by a sputtering method on the surface of a silicon wafer substrate 82 having the thickness of 300µm and provided with an oxide layer of 0.5µm on its surface by thermal oxidation. Next, electrodes 83 were formed to conform to the electrode pattern specified in Figure 3. On one of the substrates, doughnut-shaped structures 84 having the internal diameter of 80µm, the outer diameter of 110µm and the height of 30 µm were formed by photolithography using a cured thick film photoresist at the surroundings of portions to be bonded by the solder bumps. On the other one of the substrates, doughnut-shaped structures 84 having the internal diameter of 60µm, the outer diameter of 90µm and the height of 30µm were formed by photolithography using a thick film photoresist at the surroundings of portions to be bonded by the solder bumps. In a bonding step, Figure 8D, the thermoelectric material wafer 80 attached with the solder bumps 81 formed by the bump forming step of Figure 8A and the substrate 82 formed with the electrodes 83 and the doughnut-shaped structure 84 in the vicinity of the bonding portions which had been made in the electrode forming step of Figure 8C were positioned at predetermined locations and thereafter, the solder was molten by which the thermoelectric material wafer 80 and the substrate 82 were bonded. In the bonding, the solder bumps on the surface of the thermoelectric material wafer 80 on which the grooving had been performed and the doughnut-shaped structures 84 on the substrate 82 were positioned at predetermined locations and heating and bonding were performed while pressing the substrate 82 from outside. The P-type thermoelectric material wafer was bonded to the substrate in which the structures having the internal diameter of 80µm, the outer diameter of 110µm and the height of 30µm were formed by the solder bumps having the diameter of 70µm which had been formed on the surface on which the grooving had been performed and the N-type thermoelectric material wafer was bonded to the substrate on which the structures having the inner diameter of 60µm, the outer diameter of 90µm and the height of 30µm were formed by the solder bumps having the diameter of 50µm formed on the surface on which the grooving had been performed. In a cutting and eliminating step, Figure 8E, the thermoelectric material wafer 80 bonded to the substrate 82 was formed into thermoelectric material chips 85 bonded to the substrate 82 by cutting and eliminating portions of the thermoelectric material wafer. At this instance, portions of the substrate 82 might simultaneously be cut and eliminated in accordance with the necessity. As in EMBODIMENT-1, also in this embodiment, the cutting and eliminating step of Figure 8E was performed by using a dicing saw that was used in cutting silicon semiconductors and the like. With respect to a blade used in the cutting and eliminating, a blade having the blade thickness of 180µm was used in cutting and eliminating portions of the P-type thermoelectric material wafer 90 and a blade having the blade thickness of 160µm was used in cutting and eliminating portions of the N-type thermoelectric material wafer 92. In the P-type thermoelectric material wafer 90, the grooves having the width of 160µm had been cut by 150µm from the side of the substrate in the grooving step and therefore, in the cutting and eliminating step of Figure 8E, the cutting and eliminating was performed by a blade having the blade thickness of 180µm and up to the depth of 350µm from the surface of the remaining portion of the thermoelectric material wafer 90 on the opposite side thereof wherein the grooves having the width of 160µm and the depth of 150µm had been cut. In the N-type thermoelectric material wafer 92, the grooves having the width of 180µm had already been cut by 350µm from the side of the substrate in the grooving step and therefore, in the cutting and eliminating step of Figure 8E, the cutting and eliminating was performed by the blade of 160µm from the surface of the remaining portion of thermoelectric material wafer 92 having the thickness of 150µm on the opposite side thereof wherein the grooves having the width of 180µm and the depth of 350µm had been cut. Figure 10 illustrates sectional views of the substrates to which the thermoelectric material chips made by this operation had been bonded in a direction orthogonal to the substrates. As shown in Figure 10, in the P-type thermoelectric material chip 100, the size of a side is 70µm up to 150µm from the substrate and the size is 50µm for the remaining portion of 150µm to 500µm therefrom and in the N-type thermoelectric material chip 105, the size is 50µm up to 350µm from the substrate and the size is 70µm for the remaining portion of 350µm to 500µm therefrom. In an integrating step, in Figure 8F, two sheets of the substrates 82 respectively bonded with the thermoelectric material chips 85 of different types were opposed, the solder bumps 81 formed on the distal ends of the respective chips and the electrodes 83 formed on the substrates were positioned at locations to be bonded and the assembly was heated while being pressed to melt the solder whereby the thermoelectric material chips 85 were bonded to the electrodes 83 on the substrates 82 by which the thermoelectric device having the PN junctions on the top and the bottom substrates could have been finished. Further, the positioning in this bonding was performed by the structures 84 formed on the substrates of different types to be bonded to the solder bumps 81 which had been formed on the distal ends of the thermoelectric material chips 85 of respective types. Figure 11 is a view indicating outline of the thermoelectric device made by the above series of steps. Although the constitution of the device is similar to the device manufactured in EMBODIMENT-1, the sectional shapes of the P-type thermoelectric material chip 110 and the N-type thermoelectric material chip 111 are not in a single rectangular form and those in both of the P-type and the N-type are thick on the side of one substrate 116 and thin on the side of the other substrate 113. To investigate the function of the thermoelectric device of EMBODIMENT-4, thermoelectric devices respectively having sizes of thermoelectric material chips of 50µm and 70µm and having the same number of PN junctions and outer dimensions were manufactured and the function as a Peltier element was compared among the three devices. Then, the device of this embodiment indicated a value of the COP (coefficient of Performance) superior to those of the respective comparison samples by approximately 10% showing the most excellent function. In a Peltier device, Joule heat is generated by flowing current in addition to heat generation on the side of a radiating substrate caused by the transfer of heat by the Peltier effect. As is well known, in the Joule heat generation, in case where the section of a substance in which current flows is uniform, a central portion thereof is mostly heated and generates heat. In the thermoelectric device of this embodiment, by making current flow such that the substrate having the thinner thermoelectric material chips became a heat radiating substrate, the Joule heat generation was caused centring on the portions in which the thermoelectric material chips are thinned. Therefore, the generated heat was smoothly transferred from a nearer substrate, that is, the heat radiating substrate and accordingly, heat could be prevented from flowing to a heat absorbing substrate on the opposite side by which the thermoelectric device was provided with high function. Further, although the sectional view showing of the outline of the thermoelectric device in EMBODIMENT-4 is illustrated in Figure 11, considering the easiness of manufacturing a thermoelectric device, especially the positioning or the bonding of the thermoelectric material chips to the substrate in the integrating step, a sectional shape shown in Figure 12 is also effective. EMBODIMENT-5. An explanation will given of an embodiment of manufacturing a small-scaled thermoelectric device in which thermoelectric material and substrates are bonded by a method other than the solder bump method in a thermoelectric device having an electrode pattern similar to that in EMBODIMENT-1. The size of thermoelectric material chips, a number of couples of PN junctions, used material and the like are the same as those in EMBODIMENT-1. Figure 13 illustrates views showing outline of steps for manufacturing a thermoelectric device of this embodiment. As shown in Figure 13, the manufacturing method is grossly classified into five steps. An explanation will be given thereto in due order. In a protruded electrode forming step, Figure 13A, a photoresist having the thickness of 50µm was coated on both faces of respective thermoelectric material wafers 130 of P-type and N-type each comprising a Bi-Te series sintered body having the thickness of 500µm. A resist layer having circular openings of which diameter of opening was 90µm and the arrangement of which was in a desired pattern was formed by exposing and developing the photoresist. The desired pattern was determined based on the above-mentioned dimensions such that it became the arrangement of thermoelectric material chips specified in Figure 3. Next, a nickel plating of 50µm was performed on the openings by an electric plating method after cleaning them by an acid or the like thereby forming a protruded nickel layer. Next, a gold plating was performed on the nickel layer similarly by an electric plating method thereby forming a gold layer of 1µm. Next, the protruded electrodes 131 comprising nickel-gold was formed by removing the resist. Here, the gold layer was provided to prevent the surface of nickel from being oxidised and to facilitate soldering in a later step and therefore, the gold layer was not always necessary if there was no concern of oxidation. In an electrode forming step, Figure 13B, films of chromium, nickel and gold in that order from the side of a substrate respectively having the thicknesses of 0.1µm, 3µm and 1µm were formed by a sputtering method on a silicon wafer substrate 132 having the thickness of 300µm on the surface of which an oxide layer of 0.5µm had been provided by thermal oxidation. Next, electrodes 133 were formed on each of top and bottom substrates by photolithography to form the electrode pattern specified in Figure 3 and a solder paste was printed on the electrodes 133 thereby finishing the electrode wirings. In a bonding step, Figure 13C, the thermoelectric material wafer 130 having the protruded electrodes 131 formed in the protruded electrode forming step of Figure 13A and the substrate 132 on which the electrodes 133 had been formed in the electrode forming step of Figure 13B, were positioned at predetermined locations and solder was molten whereby the thermoelectric material wafer 130 and the substrate 132 were bonded. (Incidentally, top or bottom is for convenience of expression as mentioned above and there is no top or bottom in the substrates of this thermoelectric device). In a cutting and eliminating step, Figure 13D, the thermoelectric material wafer 130 bonded to the substrate 132 was formed into thermoelectric material chips 134 bonded to the substrate 132 by cutting and eliminating portions of the thermoelectric material wafer 130. At this instance, portions of the substrate 132 might simultaneously be cut and eliminated in accordance with the necessity. In this embodiment, the cutting and eliminating step of Figure 13D was performed by using a dicing saw used in cutting silicon semiconductors and the like. A blade used in the cutting and eliminating had the thickness of 200µm. The thickness of the blade was selected under conditions in which the length of a side of the square thermoelectric material chip 134 in this embodiment was 100µm, the centre distance of nearest thermoelectric material chips of a same type was 300µm and the thermoelectric material chips of different types were bonded conforming to the positional relationships specified in Figure 3. Unnecessary portions of the thermoelectric material were cut and eliminated at central portions between the protruded electrodes 131 and the height of the blade was adjusted by using a gap between the thermoelectric material wafer 130 and the substrate 132 produced by the protruded electrodes 131 having the height of 50µm so as not to destroy the electrodes 133 on the substrate. The substrate 132 substantially bonded with 125 pieces of the thermoelectric material chips 134 was made for respective type of the thermoelectric material by longitudinally and transversely cutting and eliminating using the blade of a dicing saw. In an integrating step, Figure 13E, two sheets of the substrates 132 respectively bonded with the thermoelectric material chips 134 of different types were opposed and the protruded electrodes 131 respectively formed on the distal ends of the chips and the electrodes 133 formed on the substrates and comprising solder layers were positioned at locations to be bonded and the assembly was heated while being pressed to melt the solder whereby the thermoelectric material chips 134 and the electrodes 133 on the substrates 132 were bonded by which the thermoelectric device having PN junctions on the top and the bottom substrates could have been finished. With respect to the final outer dimensions of the thermoelectric device manufactured as above, the thickness was approximately 1.2 mm, the size was 4 mm x 4 mm in the size of the bottom substrate having input and output electrodes, electrically the internal resistance was 120Ω and the basic characteristics thereof were the same as those in the thermoelectric device manufactured in EMBODIMENT-1. EMBODIMENT-6 An explanation will be given of an embodiment of manufacturing a small-scaled thermoelectric device in which thermoelectric material and substrates are bonded by the solder bump method and a method using an electrically conductive adhesive agent in a thermoelectric device having an electrode pattern similar to that in EMBODIMENT-1. The size of a thermoelectric material chip, a number of couples of PN junctions, used material and the like are the same as those in EMBODIMENT-1. Figure 14 illustrates views showing outline of steps in manufacturing a thermoelectric device of this embodiment. As shown in Figure 14, the manufacturing method is grossly classified into five steps. An explanation will be given thereto in due order. In a bump forming step, Figure 14A, a photoresist having the thickness of 50µm was coated on one face of each of thermoelectric material wafers 140 of P-type and N-type respectively comprising a Bi-Te series sintered body having the thickness of 500µm. A resist layer having circular openings of which diameter of opening was 90µm and the arrangement of which was in a desired pattern was formed by exposing and developing the photoresist. The desired pattern was determined based on the above dimensions to conform to the arrangement of thermoelectric material chips specified in Figure 3. A plating resist was coated on the other face not coated with the photoresist. Next, firstly, a nickel plating of 40µm was coated on the openings by an electric plating method after cleaning them by an acid or the like to form so-called nickel bumps. Next, a solder plating was performed on the nickel layer similarly by an electric plating method to form a solder layer of 30µm. In the solder plating, a ratio of tin to lead was 6:4. Next, after removing the photoresist and the plating resist, a rosin group flux was coated on the solder-plated layer and a reflow treatment was performed at 230°C whereby spherical solder bumps 141 having the diameter of approximately 100µm were formed on the one face of the thermoelectric material wafer 140. In an electrode forming step, Figure 14B, films of chromium, nickel and gold in that order from the side of a substrate respectively having the thicknesses of 0. 1µm, 3µm and 1µm were formed on the surface of a silicon wafer substrate 142 having the thickness of 300µm the surface of which was provided with an oxide layer of 0.5µm by thermal oxidation. Next, electrodes 143 were formed on the top and the bottom substrates by photolithography to form the same electrode pattern as in Figure 3. Further, two kinds of doughnut-shaped structures 144 were formed at the surroundings of portions to which a P-type thermoelectric material and a N-type thermoelectric material were to be bonded through solder bumps by photolithography using a polyamide group photoresist. The structures 144 comprising the polyamide group photoresist were provided with a doughnut shape having the internal diameter of 120µm, the outer diameter of 150µm and the height of 30µm at locations to which the P-type thermoelectric material chips were disposed and the internal diameter of 150µm, the outer diameter of 170µm and the height of 30µm at locations to which the N-type thermoelectric material chips were disposed in one of two sheets of the substrates constituting the thermoelectric conversion element and in the other substrate, they were provided with a doughnut shape having the inner diameter of 150µm, the outer diameter of 170µm and the height of 30µm at locations to which the P-type thermoelectric material chips were disposed and the internal diameter of 120µm, the outer diameter of 150µm and the height of 30µm at locations to which the N-type thermoelectric material chips were disposed. In a bonding step, Figure 14C, the thermoelectric material wafer 140 and the substrate 142 in which the electrodes 143 and the doughnut-shaped structures in the vicinities of bonding portions formed in the electrode forming step of Figure 14B were opposed at predetermined locations and the solder was molten whereby the thermoelectric material wafer 140 and the substrate 142 were bonded. Further, in bonding the P-type thermoelectric material wafer and the substrate, the positioning of the thermoelectric material wafer 140 and the substrate 142 was performed by inserting the solder bumps formed on the surface of the P-type thermoelectric material wafer into the inside of the smaller doughnut-shaped structures 144 having the inner diameter of 120µ m, the outer diameter of 150µm and the height of 30µm formed on the substrate. Similarly, in bonding the N-type thermoelectric material wafer and the substrate, the positioning of the thermoelectric wafer 140 and the substrate 142 was performed by inserting the solder bumps formed on the surface of the N-type thermoelectric material wafer into the inside of the smaller doughnut-shaped structures 144 having the inner diameter of 120µm, the outer diameter of 150µm and the height of 30µm formed on the substrate. Here, the smaller structures among the doughnut-shaped structures having two sizes formed on the substrate were used in bonding the thermoelectric material wafer 140 and the substrate 142 to dispense with wrong bonding locations and to enhance mutual positioning accuracy. In a cutting and eliminating step, Figure 14D, the thermoelectric material wafer 140 bonded to the substrate 142 were formed into thermoelectric material chips 145 bonded to the substrate 142 by cutting and eliminating portions of the thermoelectric material wafer. At this instance, portions of the substrate 142 might simultaneously be cut and eliminated in accordance with the necessity. In this embodiment, the cutting and eliminating step of Figure 14D was performed by using a dicing saw used in cutting silicon semiconductors and the like. A blade used in the cutting and eliminating had the thickness of 200µm. The thickness of the blade was selected under conditions in which the length of a side of the square thermoelectric material chip 145 of this embodiment was 100µm, the centre distance between nearest thermoelectric material chips of a same kind was 300µm and the thermoelectric material chips of different kinds were bonded in the positional relationship specified in Figure 3. Unnecessary portions of the thermoelectric material were cut and eliminated at central portions between the solder bumps 141 and at the same time the height of the blade was adjusted by utilising a gap between the thermoelectric material wafer 140 and the substrate 142 produced by the nickel bumps having the height of 40µm so as not to destroy the electrodes 143 on the substrate. The substrate 142 substantially bonded with 125 pieces of the thermoelectric material chips 145 was made for each type of the thermoelectric materials by longitudinally and transversely cutting and eliminating thereof by the blade of a dicing saw. In an integrating step, Figure 14E, an electrically conductive adhesive agent 146 having silver particles and epoxy resin as major components was adhered to distal ends of the thermoelectric material chips 145 by stamping in. Two sheets of the substrates respectively bonded with the thermoelectric material chips 145 of different types were opposed, the distal ends of the thermoelectric material chips 145 and the electrodes 143 formed on the substrates 142 were positioned at locations to be bonded and the assembly was heated while being pressed whereby the electrically conductive adhesive agent was cured and the thermoelectric material chips 145 and the electrodes 143 on the substrates 142 were bonded by which the thermoelectric device having PN junctions on the top and the bottom substrates could have been finished. Further, the bonding was performed at the insides of the remaining doughnut-shaped structures 144 and the electrically conductive adhesive agent could be prevented from oozing in bonding by using the doughnut-shaped structures 144. With regard to the final outer dimensions of the thermoelectric device manufactured as above, the thickness was approximately 1.2 mm, the size was 4 mm x 4 mm in the size of the bottom substrate having input and output electrodes, electrically the internal resistance was 120Ω and its basic characteristics were the same as those in the thermoelectric device manufactured in EMBODIMENT-1. In this embodiment, in the step of forming the bumps on the thermoelectric material, the plating resist was not formed on the both faces by photolithography and therefore, there was no need of coating a photoresist on the both faces and using both a face aligner and exposure device which could simplify apparatuses and steps. EMBODIMENT-7 The present invention will now be described on the basis of one embodiment thereof and with reference to the accompanying drawings. Fig. 15 is a view showing only a metal wiring part of a thermoelectric device produced by sandwiching between two alumina substrates a PN junction comprising a P-type thermoelectric material and an N-type thermoelectric material connected through a metal, with the view being taken from above one of the substrates. In Fig. 15, solid line parts 152 show an electrode pattern for the PN junctions provided on the top substrate and dashed lines 151 show electrode patterns for the PN junction provided on the bottom substrate. The P-type thermoelectric materials chips 153 and the N-type thermoelectric materials chips 154 are mutually disposed at the parts where these continuous lines and dashed lines cross and are linked in series between two input/output electrodes 155 (hereinafter, between two electrodes will be referred to as between electrodes). Electrodes 156 are provided at the outer periphery of the wiring on the bottom substrate as device repair and inspection electrodes for the present invention. The existence of defects such as disconnections existing between the electrodes 156 (for example, between the electrodes 156-a and 156-b in Fig. 15) can be investigated by providing a number of electrodes 156 and by connecting with inspection probe electrodes between the electrodes. Also, if a defect exists between the electrodes 156, the defective part can be electrically isolated by making electrical connections between the electrodes and a device can be formed just using nondefective parts. For example, if there is a disconnection at the point A in Fig. 15, the device can be made to function by electrically making a short-circuit between the electrode 156-a and the electrode 156-b. In Fig. 15several tens thermoelectric material chips are sandwiched between the substrates but this diagram is for simplifying the explanation. The inventor carried out experiments for a heat difference power generator comprised of 50 rows in the X-direction of Fig. 15 and 10 rows in the Y direction so that a disconnection at one place results in the elimination of two rows (10 pairs of elements) in the X-direction, and the reduction of the power-generating performance is proportional to the ratio of the number of elements eliminated. Reductions in performance change depending on the purpose of the device but with devices where the object is temperature difference power generation or refrigeration where the number of elements has been made large a reduction in the number of elements of a few to 10% is not a problem. However, this problem can be resolved by anticipating the number of defective elements beforehand and increasing the number of elements by this portion. In the case of a device having the kind of wiring structure in Fig. 15, the ratio of the number of elements which do not operate with respect to the overall number of elements upon the occurrence of defects such as discontinuities, can be made small, by adopting a wiring structure where the number of elements in the Y direction in the drawing is reduced to as great an extent as possible and the number of elements in the X direction is increased. As explained above, according to the inventions described in embodiments, a thermoelectric material wafer and PN bonding electrodes on a substrate are bonded under a positional relationship of thermoelectric material chips and the PN bonding electrodes, the thermoelectric material chips bonded to the substrate are formed by cutting and eliminating unnecessary portions of thermoelectric material, the substrates respectively bonded with the thermoelectric material chips of different types are opposed and PN junctions are formed by bonding distal ends of the thermoelectric material chips and the PN bonding electrodes on the substrate. Therefore, there is an effect capable of manufacturing a thermoelectric device in which the size of the thermoelectric material chip is small and the density of a number of the thermoelectric material chips per unit area is high. Further, according to the present inventions, by forming electrodes as wiring on a substrate of a thermoelectric device, inspection of the thermoelectric device can be carried out and it is possible to investigate defects such as disconnections or defective connections. Further, when defects exist, the functioning of a thermoelectric device can still be exhibited by connecting electrodes so as to exclude the defective portion. As a result of this, the device construction yield rate is markedly increased and costs are reduced. Further, each thermoelectric device manufactured as above which is small and thin and is provided with a number of couples of PN junctions of the thermoelectric material chips, achieves a considerable effect in power generating in a small temperature difference. In EMBODIMENT-1, an example has been shown in which an electronic wrist watch was driven by using the thermoelectric devices each having couples of PN junctions of a number capable of outputting approximately 1 V or more. However, the number of devices can considerably be decreased when a step-up circuit is attached thereto or CMOS-ICs are driven at a low voltage and therefore, the thermoelectric device is applicable not only to the electronic wrist watch but to many carried electronic instruments. Further, in using the small-scaled thermoelectric device manufactured by the present invention as a cooling device an enormous effect is provided. For example, when the current density per thermoelectric material chip is made constant to equalise cooling function, the cooling capacity can be enhanced by increasing voltage since the sectional area of the thermoelectric material chip can be small and many thermoelectric material chips can be arranged in series. For example, the cooling function is determined by power inputted to a thermoelectric device and in a conventional thermoelectric device, power supply causes low voltage and high current since the sectional area of a thermoelectric material chip is large. By contrast, with regard to the thermoelectric device of the present invention, power can be supplied at low current since the sectional area of the thermoelectric material chips can be reduced. Thereby, it is not necessary to make thick wirings for inputting and outputting and to provide a large current-type power source for use. Further, a multi-stage element called a cascade type can easily be manufactured since electric wirings can be made thin by which an extremely low temperature can be achieved. Further, although the size of the thermoelectric material chip was 500µm or less in the embodiments, with respect to the size, the present invention is naturally applicable to the size of several hundred µm to mm order that is a general size. Although the description has been given of making individual thermoelectric devices in the embodiments, it is possible to manufacture a plurality of devices in one operation by using large-scaled substrates and thermoelectric material wafers. Therefore, the present invention achieves an enormous effect in manufacturing small-scaled thermoelectric devices in view of the production cost. As stated above, although the explanation has been given to the present invention with respect to the embodiments, the present invention is not restricted to the above embodiments and a broad application is conceivable. For example, although the sintered body of a Bi-Te series thermoelectric material was used in the respective embodiments as thermoelectric material, the present invention is naturally not restricted to this thermoelectric material and various thermoelectric materials of Fe-Si series material, Si-Ge series material, Co-Sb series material and the like are applicable. Further, although the description has been given to small-scaled thermoelectric devices and their methods of making in the respective embodiments, according to the thermoelectric device and the method of making thereof of the present invention, the present invention is also applicable to a comparatively large thermoelectric device which is manufactured by the conventional method in which thermoelectric material chips are interposed between two sheets of substrates after they have been formed. The aforegoing description has been given by way of example only and it will be appreciated by a person skilled in the art that modifications can be made without departing from the scope of the present invention as defined by the accompanying claims.

Claims: A thermoelectric device (11) comprising two sheets of substrates (12, 64, 132) each having electrodes (15, 32, 33, 50, 51,65, 133, 151, 152) and at least one couple of P-type (13) and N-type (14) thermoelectric material elements interposed between the two sheets of substrates and PN-coupled via the electrodes, a sectional shape of each of the thermoelectric material elements cut in a plane parallel with the two sheets of substrates being quadrangular characterised in that the thermoelectric material elements and electrodes for PN junctions are arranged such that a straight line connecting centres of quadrangles of any adjacent, electrically coupled P-type and N-type thermoelectric material elements is not in an orthogonal or parallel relationship with any of the sides constituting the quadrangle that is the sectional shape of each thermoelectric material element forming a PN junction couple. A thermoelectric device according to claim 1, wherein a shortest distance between the centres of quadrangles of P-type and N-type thermoelectric material elements respectively which are disposed mostly closed is ranged from a half to equal a shortest distance between the centres of quadrangles of same type elements which are disposed mostly closed. A thermoelectric device according to claim 1 or claim 2, wherein said straight line connecting centers of respective adjacent, electrically coupled P-type and N-type thermoelectric material elements and a straight line connecting diagonally opposite corners of the respective quadrangles are the same straight line. A thermoelectric device according to any one of claims 1 to 3, wherein, except ones at outermost portions among the thermoelectric material elements constituting the thermoelectric device, an arbitrarily selected one of the thermoelectric material elements is arranged inside of a second quadrangle formed by connecting the corner most close to the arbitrarily selected thermoelectric material element of each of four of the thermoelectric material elements of a different type to and most close to the arbitrarily selected thermoelectric material element. A thermoelectric device according to any one of the preceding claims, wherein the thermoelectric material elements interposed between the two sheets of substrates include thermoelectric material elements bonded to the two sheets of substrates and electrically isolated from the device. A thermoelectric device according to any one of preceding claims, wherein the thermoelectric device has electrodes (54, 55) each of which is connected with a plurality of elements of a same type among the thermoelectric material elements interposed between the two sheets of substrates. A thermoelectric device according to any one of the preceding claims, wherein a sectional area of each of the thermoelectric material elements is changed in a height direction of the thermoelectric material elements. A thermoelectric device according to any one of the preceding claims, wherein structures (23) are provided where the thermoelectric material elements and the substrate are bonded via an electrode on at least one of the surfaces of the two sheets of substrates. A thermoelectric device according to claim 8, wherein sizes of the structures provided on the substrates are different at portions of at least one of the two sheets of substrates at which the P-type thermoelectric material elements and the N-type thermoelectric material elements are arranged depending on types thereof. A thermoelectric device according to claim 8 or claim 9, wherein the structures are provided on each of the two sheets of substrates respectively and the size or shape of a structure provided for a selected thermoelectric material element on a first of said sheets is different to the size or shape of a structure provided for the selected thermoelectric material element on a second of said sheets. A thermoelectric device according to any one of claims 8 to 10, wherein the structures provided on the two sheets of substrates are made of a high polymer material. A thermoelectric device according to any one of claims 8 to 11, wherein the structures provided on the two sheets of substrates comprise a cured photosensitive resin. A thermoelectric device according to any one of the preceding claims, wherein at least one of the two sheets of substrates is made of silicon. A thermoelectric device according to claim 13, wherein a surface of silicon constituting the substrate is covered with an insulating layer. A thermoelectric device according to any one of the preceding claims, wherein compositions of bonding materials (62, 63) for bonding thermoelectric material elements to electrodes formed on the two sheets of substrates in bonding thereof on at least one of the two sheets of substrates are different respectively depending on a difference in types of the thermoelectric material elements. A thermoelectric device according to any one of the preceding claims, wherein the thermoelectric material elements and electrodes formed on the two sheets of substrates are bonded through protruded electrodes (131). A thermoelectric device according to claim 16, wherein the protruded electrodes for bonding the thermoelectric material elements to the electrodes formed on the two sheets of substrates are formed on the thermoelectric material elements. A thermoelectric device according to claim 16 or claim 17, wherein the protruded electrodes for bonding the thermoelectric material elements to the electrodes formed on the two sheets of substrates are provided with a solder bump structure formed on each of the thermoelectric material elements. A thermoelectric device according to any one of the preceding claims, wherein the device has electrodes (156) capable of being wired other than with thermoelectric material junctions. A thermoelectric device according to claim 19, wherein electrodes (156) which are different from a pair of electrodes (155) for input/output of the device capable of electrical connection from outside of the thermoelectric device are attached to the electrodes positioned at the outer periphery. A method of making a thermoelectric device according to any one of the preceding claims comprising: a step of forming electrodes (43) for performing a PN-coupling on each of the substrates (42) (electrode forming step); a step of bonding either of P-type and N-type sheet-like thermoelectric materials (40) to each of the two sheets of substrates (bonding step); a step of forming separate substrates bonded respectively with P-type and N-type thermoelectric material elements (13, 14, 45) by cutting and eliminating portions of the bonded sheet-like thermoelectric materials in accordance with necessity (cutting and eliminating step); and a step of integrating the thermoelectric device by opposing the substrate bonded with the P-type thermoelectric material elements to the substrate bonded with the N-type thermoelectric material elements and bonding electrodes on the two sheets of substrates to distal ends of the thermoelectric material elements thereby forming couples of PN-junctions via the electrodes (integrating step). A method of making a thermoelectric device according to claim 21, wherein a gap is left between the substrate and the thermoelectric material after bonding the substrate to the sheet-like thermoelectric material (bonding step). A method of making a thermoelectric device according to claim 21 or claim 22, former comprising a step of forming predetermined electrodes on surfaces of the substrates, a step of forming bumps (41, 71, 81, 141) made of at least one material selected from solder, gold, silver, copper and nickel having a predetermined shape and an arrangement pattern on at least one of surfaces of the sheet-like thermoelectric materials and bonding the substrates to the thermoelectric materials through the bumps during the bonding step. A method of making a thermoelectric device according to any one of claims 21 to 23, wherein a gap is produced between the substrate and the thermoelectric material by bumps (41, 71, 81, 141) formed on a surface of the thermoelectric material in bonding the substrate to the sheet-like thermoelectric material in the bonding step. A method of making a thermoelectric device according to claim 21, wherein a gap is produced between the substrate and the thermoelectric material by structure (44, 74, 84, 144) formed on the substrate in bonding the substrate to the sheet-like thermoelectric material in the bonding step. A method of making a thermoelectric device according to claim 21, further comprising a step of forming bumps on one of the surfaces of the thermoelectric materials not bonded to the substrate after bonding the substrate to the sheet-like thermoelectric material in the bonding step. A method of making a thermoelectric device according to claim 21, further comprising a step of working a total or portions of a surface of a thermoelectric material wafer to be bonded to the substrate to protrude bonding portions thereof for bonding to the substrate. A method of making a thermoelectric device according to claim 21 or claim 27, further comprising a step of grooving a total or portions of at least one of the surfaces of the sheet-like thermoelectric material for bonding to the substrate before bonding. A method of making a thermoelectric device according to any one of claims 21, 27 or 28, further comprising a step of producing protruding portions (68) for bonding to the substrate by grooving a total or portions of at least one of the surfaces of the sheet-like thermoelectric material on which a bonding material layer for bonding to the substrate or a layer for assisting the bonding is formed before bonding. A method of making a thermoelectric device according to any one of claims 21, 23 or 25, further comprising a step of grooving at least one of the surfaces of the sheet-like thermoelectric material on which bumps are formed for bonding to the substrate before bonding wherein the grooving is performed between the bumps. A method of making a thermoelectric device according to claim 21, further comprising a step of grooving at least one of the surfaces of the sheet-like thermoelectric material before bonding wherein a width of grooves formed by the grooving differs from a width of cutting and eliminating in the step of cutting and eliminating unnecessary portions of the thermoelectric material which is a later step.

Inventors: KISHI MATSUO, NEMOTO HIROHIKO, OKANO HIROSHI, KISHI, MATSUO, NEMOTO, HIROHIKO, OKANO, HIROSHI, KISHI, MATSUO, C/O SEIKO INSTRUMENTS INC., NEMOTO, HIROHIKO, C/O SEIKO INSTRUMENTS INC., OKANO, HIROSHI, C/O SEIKO INSTRUMENTS INC.
Applicants: SEIKO INSTR INC, SEIKO INSTRUMENTS INC.
Application year: 1995
Main classification: H01L35
IPC codes: H01L35