Article comprising a dispersion-compensating optical waveguide

Abstract: Disclosed is dispersion compensating (DC) optical fiber having a refractive index profile designed such that the cut-off wavelength of the LP 11 mode is less than that of a further higher order mode, typically LP 02 , and less than λ op , such that the fiber does not support propagation of the LP 11 mode at λ op . The fiber furthermore is designed to have dispersion more negative than about-90 ps/nm·km and less negative than 150 ps/nm·km, all at λ op . The DC fiber typically has loss less than 0.5 db/km at λ op . Use of such fiber in optical fiber communication systems can result in lower overall system loss.

Description: Field of the Invention This invention pertains to dispersion-compensating (DC) optical waveguides, typically optical fiber, and to communication systems and other articles that comprise a DC optical waveguide. Background of the Invention It is well known that conventional SiO 2 -based single mode optical fiber generally has minimum loss at about 1.55µm and zero chromatic dispersion at about 1.3µm. Although it is possible to design optical fiber to have both minimum loss and zero chromatic dispersion at about 1.55µm (such fiber is generally referred to as "dispersion-shifted" fiber), most presently installed single mode fiber is of the conventional type and is operated at a signal wavelength of about 1.3µm, at or close to the zero chromatic dispersion wavelength of the fiber. Considerable advantages could be realized if already installed optical fiber systems could be operated at 1.55µm. These advantages include the possibility of increased distance between repeaters (due to the lower fiber loss), and the possibility of using Er-doped fiber amplifiers (EDFAs) instead of repeaters. However, straight-forward upgrade by changing operating wavelength is not practical, due to the significant amount (exemplarily about 17 ps/nm·km) of chromatic dispersion of conventional SiO 2 -based single mode fiber at 1.55µm. The dispersion typically would limit such a system to a bit rate of at most about 2 Gbit/sec for distances of order 500 miles. Several possible ways of dealing with the problem have recently been proposed. These can be divided into "active" and "passive" techniques. Herein we are only concerned with passive techniques, in particular, with techniques that involve use of dispersion-compensating (DC) fiber. U.S. patent 4,261,639 discloses dispersion compensation by catenation of single mode fibers of respectively positive and negative dispersion at the operating wavelength. DC fiber not only can advantageously be used to upgrade an existing fiber optic communication system but could also be used in new systems (e.g., transoceanic submarine systems that use dispersion-shifted fiber) that are designed to operate at 1.55µm, e.g., to ease manufacturing specifications on the dispersion-shifted fiber. C. D. Poole et al., (Optics Letters, Vol. 17(14), p. 985; see also coassigned U.S. patent 5,185,827) disclose a DC fiber designed to support, in addition to the lowest order mode (LP 01 ), also the lowest higher order mode (LP 11 ), and also designed to have a cut-off wavelength for the LP 11 (λ c11 ) mode just slightly above the operating wavelength (λ op ). Typically, at the upstream end of the DC fiber a mode converter is provided to convert the LP 01 mode into the LP 11 mode, and at the downstream end of the DC fiber another mode converter is provided to convert the LP 11 mode back into the LP 01 mode. The technique of Poole et al. is able to compensate both dispersion and dispersion slope and can yield desirably large values of negative dispersion (absolute value >100 or 150 ps/nm·km; exemplarily -228 ps/nm·km). However, the Poole et al. technique undesirably requires use of special components (mode converters and polarization rotators) which not only add cost but also typically introduce additional loss. Furthermore, typically only about 15-20% of the total power propagates within the core, owing to the proximity of λ op to λ c11 , typically resulting in relatively high loss. Still furthermore, the prior art technique typically requires slightly elliptical DC fiber to remove the four-fold degeneracy of the LP 11 mode. A. J. Antos, (Proceedings, Conference on Optical Fiber Measurements, National Institute of Science and Technology, Colorado, September 1992, p. 89) discloses DC fibers that are designed to support only the LP 01 mode and to have negative chromatic dispersion at 1.55µm. The disclosed DC fibers have relatively small negative chromatic dispersion (absolute value ≤100 ps/nm·km; exemplarily -65 ps/nm·km), necessitating the use of long lengths (e.g., 39 km of DC fiber to compensate the dispersion of 150 km of conventional fiber) of DC fiber. Furthermore, the Antos technique apparently is practical only for dispersion compensation, with dispersion slope compensation being considered "... not easily achieved in practice ..." by the author. Co-assigned European Patent Application 0 598 554 A1, published May 25, 1994, inter alia discloses a DC optical fiber, and contains relevant background and further technical information. The refractive index profile of the prior art fiber is designed such that the fiber supports the fundamental mode (LP 01 ), does not support the LP 11 mode but does support at least one higher order mode, typically LP 02 , all at the operating wavelength (λ op ) of the fiber, typically at 1.55µm. At λ op , LP 01 has dispersion that is more negative than -150 ps/nm·km and, in a preferred embodiment, LP 01 also has negative dispersion slope at λ op . The prior art DC fiber typically has a power law core refractive index profile, a refractive index "trench" surrounding the core, and a refractive index "ridge" surrounding the trench. A frequently used figure of merit for DC fiber is the ratio of the absolute value of the dispersion (|D DC |) to the fiber loss, both at λ op . It would be highly desirable to have available DC fiber that has a higher value of that figure of merit than is typically obtainable with the fiber of the '554 application, since installation of such fiber may result in lower overall system loss. This application discloses such fiber. Glossary and Definitions The "modes" LP µν are conventionally used in discussions of modal properties of optical fibers, although they are not true but only approximate solutions of the relevant wave equation. The fundamental LP mode is LP 01 . The lowest higher order LP mode is LP 11 . LP 0m is of higher order than LP 11 , with m = 2, 3, ..... The term "chromatic dispersion" is herein used in the conventional manner and refers to the sum of material dispersion and waveguide dispersion. A waveguide "supports" propagation of a given mode of radiation of wavelength λ op if the cut-off wavelength λ c of the mode is longer than λ op , and does not "support" propagation of a given mode if λ c of the mode is shorter than λ op . In conventional fiber designs the cut-off wavelength of the LP 11 mode is greater than that of the LP 02 mode. Brief Description of the Drawings FIGs. 1 and 4 schematically depict exemplary refractive index profiles of DC fiber according to the '554 application; FIGs. 2 and 5 show the dispersion of fiber of FIGs. 1 and 4, respectively, as a function of wavelength; and FIG. 3 schematically depicts an exemplary fiber communication system according to the invention. If the dispersion of the conventional waveguide is positive at λ op , then the DC fiber is designed to have negative dispersion at λ op . The Invention The invention is defined by the claims. In a broad aspect the invention is embodied in a novel optical waveguide and in articles that comprise the waveguide. Typically, but not necessarily, the optical waveguide is an optical fiber. Those skilled in the art will appreciate that the principles of the invention also apply to non-circular waveguides such as planar waveguides. However, the remainder of the discussion will be in terms of optical fiber. More particularly, the invention is typically embodied in an article that comprises a length L DC (not necessarily one continuous piece of fiber) of an optical fiber that is designed to support the propagation of radiation of wavelength λ op in the fundamental mode (LP 01 ). The DC fiber has a refractive index profile, and cut-off wavelengths respectively for a mode designated LP 11 and a given higher order mode other than LP 11 . The refractive index profile is selected such that the cut-off wavelength for the LP 11 mode is less than the cut-off wavelength for the given higher order mode, and also is less than λ op . The DC fiber thus does not support propagation of the LP 11 mode at λ op . Furthermore, the refractive index profile is selected such that the LP 01 mode has dispersion at λ op that is more negative than -90 ps/nm·km but less negative than -150 ps/nm·km. In a currently preferred embodiment, the optical fiber is a SiO 2 -based (i.e., containing everywhere more than 50 mole % SiO 2 ) optical fiber, λ op is about 1.55µm, and the fiber supports the propagation of LP 02 but not of LP 11 at λ op . Optionally the DC fiber also has a predetermined negative value of the dispersion slope (D' DC ) at λ op . FIG. 1 shows the nominal refractive index profile of an exemplary optical fiber according to the '554 application. Although the radius is expressed in arbitrary units, the profile can also be considered to be quantitative since 100 arbitrary radial units correspond, in a particular embodiment, to 1.9µm in the fiber. Those skilled in the art know that actual fiber profiles typically depart somewhat from the (ideal) nominal profiles that form the basis of design calculations. However, the properties of actual fibers typically closely correspond to the computed properties of the corresponding models that use nominal fiber profiles, and it is common practice to base new fiber designs on computer simulations. The profile of FIG. 1 comprises core 11, first cladding region (trench) 12, second cladding region (ridge) 13, and third cladding region 14. The exemplary profile of FIG. 1 corresponds to a fiber having a core diameter of 3.8 µm, a maximum core Δ of about 0.019, an outer trench radius of 5.7µm, a trench Δ of about -0.004, an outer ridge radius of 7.6µm, a ridge Δ of about 0.004, and a third cladding region wherein Δ = 0. The third cladding region extends to the fiber surface. The parameter Δ is defined in the conventional manner, namely Δ(r) = (n(r) - n o )/n o , where n o is the refractive index of pure vitreous SiO 2 . The ridge is selected to support the LP 02 mode. Generally speaking, if it is desired that a DC fiber support the LP 0m mode, then the fiber exemplarily can have m-1 appropriately placed ridges. A further exemplary refractive index profile is shown in FIG. 4. The core has a power law profile, with α = 2.2, and 300 arbitrary (radial) units correspond to 5 µm in the fiber. Typically, DC fiber according to the invention will comprise the above referred to core and first-third cladding regions. The first cladding region will be immediately adjacent to the core and have a refractive index that is lower than the refractive index of any region outside of the first cladding region. The refractive index of the second cladding region will have a value between the maximum core refractive index and the first region refractive index, and the position of the second cladding region will be selected such that the desired higher order mode (e.g., LP 02 ) is excited before LP 11 . Finally the third cladding region will have a refractive index of value between that of the first and second cladding regions. Frequently the third cladding region will comprise nominally pure silica. Exemplarily, a fiber according to the invention typically will have a generic power-law core profile. The fibers of FIGs. 1 and 4 can be made by conventional means. The core typically will be Ge-doped, the trench down-doped with F, the ridge lightly up-doped with Ge, and region 14 typically will be undoped SiO 2 . The fiber of FIG. 1 has λ c02 of about 1.600 µm, and λ c11 of about 1.565 µm. Although FIG. 1 shows an approximately triangular (power-law exponent α = 1.5) core profile; this is not a necessary requirement, and other core profiles such as parabolic or step profiles could be used. FIGs. 2 and 5 show the (computed) dispersion of the fibers of FIGs. 1 and 4, respectively, as a function of wavelength. As can be seen, the exemplary fibers have quite large (negative) dispersion (e.g., -260 ps/nm·km at 1550 nm), making them effective DC fibers. Exemplarily, the dispersion of 50 km of conventional single mode fiber (dispersion 17 ps/nm·km at 1.55µm) could be compensated with a mere 3.3 km of the exemplary fiber of FIG. 1. Fiber according to the invention can be joined directly, without intermediate mode converter, to conventional single mode transmission fiber. Most of the optical power that is coupled into the inventive fiber will continue to propagate in the LP 01 mode, with only a minor portion of the power in the LP 02 mode. Due to the proximity of λ op to λ c02 , the LP 02 mode is quite susceptible to bending loss. This will typically be an advantage, since it facilitates removal of LP 02 mode power by simple means, e.g., coiling the length of DC fiber. Thus, it can be readily arranged that at the downstream end of the DC fiber essentially all of the optical power is in the LP 01 mode, facilitating direct joining to conventional single mode transmission fiber or other conventional components. Furthermore, waveguides according to the invention not only can compensate chromatic dispersion but also the dispersion slope at a given system operating wavelength. By "dispersion slope" (designated herein D') at a wavelength λ op we mean the value of the first derivative of the chromatic dispersion with respect to wavelength at λ op . Exemplarily, appropriate choice of fiber profile makes it possible to compensate the dispersion slope of standard single mode fiber such that the system can exhibit very low chromatic dispersion over a significant spectral region, e.g., have less than about 1.5 ps/nm·km dispersion over a wavelength range of at least 50 nm width in the 1.55µm wavelength region. This feature can be advantageously used in wavelength division multiplexed (WDM) systems. Those skilled in the art will know that the dispersion slope of an optical fiber is proportional to the negative of the second derivative of the propagation constant with respect to the V-number of the fiber. Typically, conventional single mode fiber has a positive dispersion slope at 1.55µm. In order to compensate the dispersion slope D' SM of a given length L SM of conventional single mode fiber at, e.g., 1.55µm with a length L DC of DC fiber, the index profile of the DC fiber is selected such that, at the V-number that corresponds to λ = 1.55µm, the above referred-to second derivative is positive and of magnitude such that the dispersion slope of the DC fiber (D' DC ) is substantially equal to (D' SM )(L SM /L DC ). The selection can readily be made by computer modeling, using well known techniques. For instance, the fiber of FIG. 4 has dispersion at 1.55 µm more negative than 150 ps/km·nm, and has dispersion slope of about -0.8 ps/km·nm 2 at 1.55µm. Thus, about 4.4 km of that fiber can compensate the dispersion slope of 50 km of a single mode fiber having dispersion slope at 1.55µm of 0.07 ps/km · nm 2 , a typical value. Those skilled in the art will appreciate that an optical fiber communication system according to the invention can take many forms, and all such embodiments are contemplated. For instance, in order to upgrade a conventional (1.3µm) system, each regenerator can be replaced by an EDFA with associated length L DC of DC fiber according to the invention. Although it will generally be appropriate to insert a single length of DC fiber into each fiber span, this is not necessarily so. At least in principle it is possible to insert shorter pieces of DC fiber at several points of a span, or to insert all of the required DC fiber at a single location, e.g., at the receiver location or even at the transmitter. Since there is signal attenuation associated with DC fiber according to the invention, it will at times be appropriate to dope the core of the DC fiber with appropriate rare earth ions (e.g., Er 3+ ), and to provide an appropriate pump radiation source. In this manner a length of DC fiber can be made to appear substantially loss-less for signal radiation. Of course, DC fiber could also be rare earth-doped such that the fiber provides net gain, advantageously serving both as dispersion compensator and optical amplifier. FIG. 3 schematically depicts an exemplary optical fiber communication system according to the invention, wherein numeral 32 refers to signal radiation emitted by transmitter 31 which is guided in transmission fiber 33 to optical amplifier/dispersion compensator 34, is then typically guided through further lengths of transmission fiber and further amplifiers/compensators (not shown) to receiver 36. Exemplarily the amplifier/compensator comprises a length of DC fiber 37 and EDFA 38. Pump radiation 39 is provided to combination 34, to be coupled into the EDFA. It will be appreciated that the functions of compensation and amplification could be performed by rare earth-doped DC fiber. A frequently used figure of merit for DC fiber is the ratio of the absolute value of the dispersion (|D DC |) to the fiber loss, both at the relevant wavelength, typically 1.55µm. We have found that, at least under some circumstances, a fiber that has |D DC | of only 100 ps/nm·km or even somewhat less (typically |D DC | > 90 ps/nm·km) can have a higher value of that figure of merit than a fiber of |D DC | of, e.g., 150 ps/nm·km, since attainment of such large values of dispersion frequently requires quite high core doping levels, which in turn can cause relatively high loss. For instance, core deltas of about 2% were desirable for obtaining dispersions of about -175 to -200 ps/nm·km, resulting in fiber having a loss of about 3 dB/km. On the other hand, it is possible to attain dispersion of about -100 ps/nm·km with fiber having a core delta of about 1.5% and a loss of less than about 0.5 dB/km. Thus, from a systems design point of view, it will frequently be preferable to install DC fiber that has less than the highest attainable dispersion value, since installation of lower dispersion fiber may result in lower overall system loss. A further advantage of fiber that has somewhat lower dispersion (e.g., about -100 ps/nm·km) is that such fiber can have lower bend loss than analogous fiber of higher dispersion, making possible use of more compact dispersion compensation packages. We have also found that it may at times be advantageous to design a DC fiber such that the cut-off wavelength for the at least one higher order mode is in the approximate range 1.35 - 1.60µm. Thus, for λ op of about 1.55µm, the relevant higher order mode (typically LP 02 may actually be gradually lost from the installed fiber, thereby eliminating the need of stripping the higher order mode from the fiber prior to signal detection. In all cases, however, the fiber is designed to not support the propagation of the LP 11 mode, and the cut-off wavelength of LP 11 is less than the cut-off wavelength of the relevant higher order mode, typically LP 02 . In some preferred embodiments, the slope of the dispersion as a function of wavelength is negative. Exemplarily, a DC fiber according to the invention has a refractive index profile substantially as shown in FIG. 1, except that the core is a power law graded index core with exponent 6, the core has a diameter of 3.5µm and a delta of 1.4%, cladding region 12 has delta of -0.6% and width 3.5 µm, and cladding region 13 has delta of 0.5% and width 3.5 µm. The fiber has loss less than 0.5 dB/km and dispersion of about -136 ps/nm·km at 1.55µm, with the dispersion slope being about -0.767 ps/nm 2 ·km over the range 1530-1560 nm. The cut-off wavelengths for LP 11 and LP 02 are, respectively, 1.02µm and 1.50µm. Those skilled in the art will realize that the amount of dispersion compensation will frequently depend on such systems aspects as data rate and span length, and that exact compensation of total span dispersion may frequently not be necessary. For instance, in a 10 Gbit/s system with span length of 120 km, it may frequently be sufficient to compensate for the dispersion of only about 100 km of the single mode fiber. In general, we contemplate compensation of at least about 80% of the span length. In other words, we contemplate systems wherein up to about 20% of the span dispersion remains uncompensated, i.e., wherein L DC ·D DC ( λ op ) + (L SM ·D SM (λ op ) < 0.2 L SM ·D SM (λ op ). In this expression, L DC and L SM are the lengths of DC and single mode fiber, respectively, and D SM is the dispersion of the single mode fiber. Furthermore, we contemplate a system wherein the DC fiber has a profile selected such that, in addition to the above condition, the condition (L DC ·D DC (λ) + L SM ·D SM (λ))/(L DC + L SM ) < 1.5 ps/nm·km is satisfied for all wavelengths λ in a wavelength range that is greater than 50 nm and includes λ op .

Claims: An article comprising a length L DC of optical fiber (37), said fiber to be hereinafter designated "DC" fiber, designed to support propagation of radiation (32) of wavelength λ op in a fundamental mode, the DC fiber having a refractive index profile, and cut-off wavelengths respectively for a mode designated LP 11 and a given higher order mode other than LP 11 ; wherein said refractive index profile is selected such that the cut-off wavelength for the LP 11 mode is less than λ op and less than the cut-off wavelength for said given higher order mode, such that the DC fiber does not support propagation of said LP 11 mode at λ op ; and wherein the DC fiber has a core (11) having normalized maximum refractive index difference Δ c > 0, the core contactingly surrounded by a cladding comprising, in outwardly directed sequence, a first cladding region (12) having normalized refractive index difference Δ 1 < 0, a second cladding region (13) having normalized refractive index difference Δ 2 selected such that 0 < Δ 2 < Δ c , and a third cladding region having normalized refractive index difference Δ 3 < Δ 2 ; CHARACTERIZED IN THAT the refractive index profile furthermore is selected such that the radiation in the fundamental mode has dispersion D DC at wavelength λ op that is more negative than about -90ps/nm·km but is less negative than -150ps/nm·km, and Δ c is less than 1.5%. The article of claim 1, wherein said given higher order mode is the LP 02 mode, the cut-off wavelength for the LP 02 mode is in the wavelength range 1.35µm to 1.60µm, and λ op is about 1.55µm. The article of claim 2, wherein the cut-off wavelength of the LP 02 mode is less than λ op . The article of any of claims 1-3, wherein the article is an optical fiber communication system that comprises a source (31) of radiation of wavelength λ op , detector means (36) for detecting radiation of wavelength λ op that are spaced from said source of radiation, and an optical fiber transmission path that radiation-transmissively links said source and said detector means, with said optical fiber transmission path comprising said length of DC fiber, and further comprising a length L SM of single mode optical fiber having chromatic dispersion D SM (λ op ) at λ op , with L DC and L SM selected such that L DC ·D DC (λ op ) + L SM ·D SM (λ op ) is less than 0.2 (L SM ·D SM (λ op )). The article of claim 4, wherein the refractive index profile is further selected such that the absolute value of (L DC ·D DC (λ) + L SM ·D SM (λ))/(L DC + L SM ) is less than about 1.5ps/nm·km for all wavelengths λ in a wavelengths range that is greater than 50 nm and includes λ op . The article of claim 1, wherein the DC fiber comprises at least one rare earth species capable of stimulated emission at the wavelength λ op , and wherein the article comprises means for coupling pump radiation of wavelength <λ op into the DC fiber. The article of claim 6, wherein λ op is about 1.55µm and the rare earth species is Er.

Inventors: VENGSARKAR ASHISH M, WALKER KENNETH L, VENGSARKAR, ASHISH M., WALKER, KENNETH L.
Applicants: AT & T CORP, AT&T CORP.
Application year: 1995
Main classification: G02B6
IPC codes: G02B6