Silicone pressure sensitive adhesive composition

Abstract: Silicone pressure sensitive compositions that combine high ultimate strength in a cured network with a lower modulus and improved adhesive strength at elevated temperatures are disclosed. These compositions are comprised of (A) a soluble, capped, organopolysiloxane resin containing less than 1.2 weight percent silicon-bonded hydroxyl groups based on the total weight of (A); (B) a diorganopolysiloxane polymer, each terminal group thereof containing at least two silicon-bonded hydrolyzable radicals said polymer having a viscosity at 25°C. of 20 to 100,000 mm 2 /s; and (C) a hydrolyzable silane.

Description: Adhesive compositions are typically comprised of a silicone resin such as an MQ resin and a polydiorganosiloxane fluid containing sufficient hydrolyzable/condensable functionality to crosslink and form a cured matrix. MQ resins which contain a significant level of Si-bonded hydroxyls, or whose surface has been rendered inert through an additional trimethylsilylation capping reaction, are useful for these types of adhesive sealants. Adhesive systems, containing MQ resin having a significant amount of reactive -SiOH, yield strong adhesive products which demonstrate the ability to provide an acceptable level of adhesive strength, not only at room temperature, but also at elevated temperatures (e.g. >120°C.). This is important for applications where the laminated part has to operate at temperatures of at least 120°C. In addition to providing sites for interaction with the fluid portion of the adhesive matrix, the hydroxyl content can also be a source of instability and abbreviated shelf life in the final product. Shelf life of these systems can be improved via the addition of reactive, hydrolyzable silanes. The degree of improvement in stability is dependent upon both the type and concentration of silane added to the mixture. Capped resins can also be used to produce high-strength, moisture curable adhesives. For example, Japanese Kokai Patent Publication No. 4/81487 discloses a pressure sensitive composition containing (1) an organosiloxane polymer resin having less than 0.7 wt% hydroxylsilyl radicals (2) a hydrolyzable group containing organopolysiloxane having a viscosity of 50 to 300,000 mm 2 /s and (3) a condensing catalyst. EP-A-0 315 333 discloses a composition and method for forming elastomeric pressure sensitive adhesives comprising a homogeneous mixture of: (A) a xylene-soluble resin copolymer of 0.6 to 0.9 triorganosiloxy units per Si0 4/2 unit and having less than 0.7 weight percent of silicon-bonded hydroxyl units, (B) a polydiorganosiloxane fluid endcapped with silicon-bonded hydroxyl groups and having a viscosity of from about 50 to 300,000 cP at 25 °C; (C) an organosilicon compound containing an average of more than two silicon-bonded alkoxy units per molecule; and (D) a condensation catalyst. EP-A-0 275 378 discloses a silicone composition for rendering surfaces stain resistant and water repellent comprising: (a) an organopolysiloxane resin selected from the group consisting of resins having R 3 S10 0.5 units and Si0 2 units, the ratio of R 3 Si 0.5 units to Si0 2 units ranging from about 0.2 to about 0.9:1 and resins having R 3 Si0 0.5 units, R 2 Si0 units and Si0 2 units, the ratio of R 3 Si0 0.5 units to SiO 2 units ranging from about 0.2 to about 0.9:1 and the ratio of R 2 Si0 units being up to about 0.1:1 where each R is independently selected from substituted or unsubstituted hydrocarbon radicals from 1 to about 8 carbon atoms; (b) alkyl-alkoxypolysiloxane resin; and (c) an effective amount of condensation catalyst. Although the compositions produced using capped resins are stable in the absence reactive silanes, they do not retain a sufficient amount of adhesive strength for service at elevated temperatures. It is an object of this invention to provide pressure sensitive adhesive compositions which are cured in the presence of moisture and that have high adhesive strength at elevated temperatures. The instant invention pertains to silicone pressure sensitive adhesive compositions comprising (A) 5 to 90 parts of a soluble, capped, organopolysiloxane resin consisting of R 3 SiO 1/2 siloxane units and SiO 4/2 siloxane units, wherein R is a monovalent hydrocarbon radical having 1 to 18 carbon atoms; there being from 0.5 to 1.5 R 3 SiO 1/2 units for every SiO 4/2 unit and containing less than 1.2 weight percent silicon-bonded hydroxyl groups based on the total weight of (A) solids as determined by Si 29 NMR; (B) 10 to 95 parts of a diorganopolysiloxane polymer, the terminal groups thereof containing at least two alkoxy radicals of the formula -ZSiR 1 x (OR 2 ) 3-x wherein R 1 is a monovalent hydrocarbon radical, R 2 is selected from alkyl radical or alkoxyalkyl radical, Z is selected from hydrocarbons, hydrocarbons containing one or more hetero atoms selected from oxygen, nitrogen and sulfur, siloxanes and combinations thereof, and the subscript x has a value of 0 or 1; said polymer having a viscosity at 25°C. of 20 to 100,000 mm 2 /s; wherein the amount of (A) and (B) equals 100 parts; and (C) 1 to 30 parts per 100 parts of resin (A) solids of a silane represented by monomers of the formula R 3 4-y SiX y or oligomeric reaction products thereof, in which R 3 is selected from hydrocarbon radicals or substituted hydrocarbon radical having 1-6 carbon atoms, X is a hydrolyzable group and y is 2 to 4; optionally (D) sufficient cure catalyst to accelerate the cure of said composition; and optionally (E) up to 50 weight percent of a filler. The compositions of the instant invention combine high ultimate strength in a cured network with a lower modulus and have improved adhesive strength at elevated temperatures. Component (A) is a soluble, capped organopolysiloxane resin that consists of R 3 SiO 1/2 siloxane units and SiO 4/2 siloxane units. The term "soluble" means that the resin can be substantially dissolved, in either a hydrocarbon liquid such as benzene, toluene, xylene, heptane and the like or in a silicone liquid such as a low viscosity cyclic or linear polydiorganosiloxane. Our organopolysiloxane resins (A) contain no more than 1.2 weight percent silicon-bonded hydroxyl groups based on the total weight of (A), as determined by Si 29 NMR, and preferably contain no more than 1.0 weight percent. In the R 3 SiO 1/2 siloxane units, each R is individually a monovalent hydrocarbon radical having less than 18 carbon atoms, preferably having from 1 to 10 carbon atoms. Suitable R radicals include alkyl radicals, such as methyl, ethyl, propyl, pentyl, octyl, undecyl and octadecyl; alkenyl radicals, such as vinyl, allyl and 5-hexenyl; cycloaliphatic radicals, such as cyclohexyl or cyclohexenylethyl; and aryl radicals such as phenyl, tolyl, xylyl, benzyl and 2-phenylethyl. Preferably, at least one third, and more preferably substantially, of all R radicals are methyl radicals. Examples of preferred R 3 SiO 1/2 siloxane units include Me 3 SiO 1/2 , ViMe 2 SiO 1/2 , PhMe 2 SiO 1/2 and Ph 2 MeSiO 1/2 where Me denotes methyl and Ph denotes phenyl. The mole ratio of the R 3 SiO 1/2 siloxane units to SiO 4/2 siloxane unit of organopolysiloxane resin (A) has a value of from 0.5/1 to 1.5/1, preferably from 0.6/1 to 1.0/1. These mole ratios are easily measured by Si 29 nuclear magnetic resonance (NMR). Methods for producing capped organopolysiloxane resins are well known in the art. The capped organopolysiloxane resin (A) may be prepared by first making an untreated resin copolymer according to U.S. Patent 2,676,182. Thereafter, one would treat an organic solvent solution of the untreated resin copolymer with a suitable endblocking agent to reduce the amount of silicon-bonded hydroxyl units to less than about 1.2 weight percent, preferably less than 1.0 wt%, and more preferably less than 0.8 wt%, as determined by Si 29 NMR. Endblocking agents capable of providing endblocking by triorganosilyl units are commonly employed as silylating agents. A wide variety of agents are known and disclosed in U.S. Patents 4,584,355, 4,591,622 and 4,585,836. A single endblocking agent such as hexamethyldisilazane can be used or a mixture of such agents can be used. The procedure for treating the resin copolymer may be simply to mix the endblocking agent with a solvent solution of the resin copolymer and allowing the by-products to be removed. Preferably, an acid catalyst is added and the mixture is heated to reflux conditions for a few hours. Component (B) is a diorganopolysiloxane polymer, each terminal group thereof containing at least two alkoxy radicals of the formula -ZSiR 1 x (OR 2 ) 3-x wherein R 1 is a monovalent hydrocarbon radical, R 2 is selected from alkyl radical or alkoxyalkyl radical, Z is selected from hydrocarbons, hydrocarbons containing one or more hetero atoms selected from oxygen, nitrogen and sulfur, siloxanes and combinations thereof, and the subscript x has a value of 0 or 1. The repeat units of diorganopolysiloxane (B) are R 2 SiO 2/2 siloxy units wherein R is independently selected from the same hydrocarbon and halogenated hydrocarbon radicals delineated above for component (A). Component (B) can comprise a single diorganopolysiloxane or a mixture of two or more different diorganopolysiloxanes. Component (B) should have a viscosity at 25°C. of 20 to 100,000 mm 2 /s, preferably 350 to 60,000 mm 2 /s. It is preferred that at least 50%, and preferably at least 85%, of the organic radicals along the chain of component (B) are methyl radicals and that these radicals are distributed in any manner in the diorganopolysiloxane. Further, component (B) can contain siloxane branching sites provided it meets the above viscosity requirements. The side chains emanating from such branch points, of course, have terminal units which can also contain the described hydrolyzable radicals. The alkoxy radicals are represented by the formula -ZSiR 1 x (OR 2 ) 3-x wherein R 1 is a monovalent hydrocarbon radical, R 2 is selected from the group consisting of alkyl radical and alkoxyalkyl radical, Z is as defined in claim 1 and the subscript x has a value of 0 or 1. In the preceding formula, R 1 is a monovalent hydrocarbon radical having from 1 to 10, preferably 1 to 6 carbon atoms. R 1 is exemplified by alkyl radicals such as methyl, ethyl, propyl and isopropyl; alkenyl radicals such as vinyl; and aryl radicals such as phenyl. R 2 is a alkyl or alkoxyalkyl radical, preferably having less than 5 carbon atoms. R 2 is exemplified by methyl, ethyl, isopropyl, methoxyethyl or ethoxyethyl. R 2 is preferably methyl. hydrocarbons such as alkylene, for example, ethylene, propylene, isobutylene and phenylene; hydrocarbons containing one or more hetero atoms selected from oxygen, nitrogen and sulfur, for example, ether-, thioether-, ester- or amide-containing hydrocarbon; siloxanes, for example, polydimethylsiloxane and combinations thereof. Preferably, Z is selected from the group of radicals having the formula -D(Me 2 SiO) a (Me 2 SiC 2 H 4 ) b - wherein Me denotes methyl, D denotes oxygen (-O-) or -CH 2 CH 2 -, subscript a has a value of 0 to 2, preferably 1 and subscript b has a value of 0 to 6, preferably 0 or 1 and the sum of a+b≥0. Z is exemplified by -CH 2 CH 2 (OSiMe 2 )-, -O(Me 2 SiCH 2 CH 2 )-, -CH 2 CH 2 (OSiMe 2 )(Me 2 SiCH 2 CH 2 )-, -O(OSiMe 2 )(Me 2 SiCH 2 CH 2 )-, -CH 2 CH 2 (Me 2 SiCH 2 CH 2 )-, -CH 2 CH 2 -, -O(Me 2 SiO)- and -O-. Most preferably, Z contains an ethylene linkage bonded to the silicon containing the -OR 2 radicals. Specific examples of suitable curing radicals are (MeO) 3 SiCH 2 CH 2 -, (MeO) 3 SiO-, Me(MeO) 2 SiO-, (MeO) 3 SiCH 2 CH 2 Si(Me 2 )CH 2 CH 2 Si(Me 2 )O-, (MeO) 3 SiCH 2 CH 2 Si(Me 2 )O-, (MeO) 3 SiCH 2 CH 2 Si(Me 2 )OSi(Me 2 )OSi(Me 2 )O- and (MeO) 3 SiCH 2 CH 2 Si(Me 2 )OSi(Me 2 )CH 2 CH 2 -. A highly preferred diorganopolysiloxane (B) of the invention is a polydimethylsiloxane which is terminated with groups having the structures (MeO) 3 SiCH 2 CH 2 Si(Me) 2 O-, (MeO) 3 SiO-, (MeO) 3 SiCH 2 CH 2 Si(Me 2 )OSi(Me 2 )CH 2 CH 2 - or Me(MeO) 2 SiO-. The preparation of diorganopolysiloxane polymers having such alkoxy terminal groups is described in detail in EP-A1 0 529 841. Alkoxy functional groups having the representative formulae (MeO) 3 SiO- and Me(MeO) 2 SiO- can be introduced into a silanol-terminated diorganopolysiloxane by compounds having the formulae (MeO) 4 Si and Me(MeO) 3 Si, respectively, as is well known in the art. The hydrolyzable functional diorganopolysiloxane (B) may be also prepared from a hydroxyl-functional diorganopolysiloxane by reacting the latter with an hydrolyzable functional silane. This reaction is typically conducted in the presence of a suitable process catalyst such as an alkyl titanate. Heating of the mixture may be required for the reaction to proceed at a useful rate. Alternatively, a hydroxyl-functional diorganopolysiloxane can be capped in-situ by reacting it with an hydrolyzable functional silane in the presence of a solution of resin (A) and, preferably, also in the presence of a process catalyst such as stannous octoate, an amine, a base or tetrabutyltitanate. When the catalyst of the above described in-situ process is an Sn II salt, the catalyst is deactivated thermally or by an appropriate agent before further processing. Likewise, when the in-situ catalyst is a base such as potassium carbonate, this base is neutralized before further processing. The preferred diorganopolysiloxane (B) of the invention is a polydimethylsiloxane which is terminated with groups having the structure (MeO) 3 SiCH 2 CH 2 Si(Me 2 )OSi(Me 2 )CH 2 CH 2 -. The amount of diorganopolysiloxane polymer (B) 10 to 95 parts wherein the sum of (A) and (B) is 100 parts. Preferably component (B) is present from 30 to 60 parts, most preferably 35 to 45 parts wherein the sum of (A) plus (B) is 100 parts. Silane (C) of the present invention is represented by monomers of the formula R 3 4-z SiX z and oligomeric reaction products thereof, wherein R 3 is selected from hydrocarbon radicals or substituted hydrocarbon radicals having 1 to 6 carbon atoms. X is a hydrolyzable group, preferably selected from alkoxy radicals having 1 to 4 carbon atoms, ketoxime radicals, aminoxy radicals, acetamido, N-methylacetamido or acetoxy radicals and subscript z has a value of 2 to 4, preferably 3 to 4. The ketoxime groups are of the general form -ONC(R 4 ) 2 , wherein each R 4 independently represents an alkyl radical having 1 to 6 carbon atoms or a phenyl radical. Specific examples of preferred silanes include methyltrimethoxysilane, methyltriethoxysilane, propyltrimethoxysilane, tetramethoxysilane, tetraethoxysilane, phenyltrimethoxysilane, isobutyltrimethoxysilane, ethyltrimethoxysilane, glycidoxypropyltrimethoxysilane aminoethylaminopropyltrimethoxysilane 3-methacryloxypropyltrimethoxysilane, tetra (methylethylketoximo)silane, methyltris(methylethylketoximo)silane and vinyltris(methylethylketoximo)silane, methyltriacetoxysilane, and ethyltriacetoxysiane. It is preferred that the silane (C) be selected from alkoxy and oximosilanes. The amount of silane (C) present is from 1 to 30 parts per 100 parts of resin (A) solids, preferably from 2 to 10 parts per 100 parts of resin (A) solids. In general, small amounts of additional ingredients may be added to the compositions of this invention. For example, adhesion promoters, antioxidants, pigments, stabilizers, and fillers, may be added as long as they do not materially alter the requirements stipulated herein. Optionally, present in the instant composition is a cure catalyst (D), which can be used to accelerate the cure of the instant compositions upon exposure to moisture. The cure catalyst (D) may be selected from those compounds known in the art to promote the hydrolysis and subsequent condensation of the hydrolyzable groups on silicon. Suitable curing catalysts include metal salts of carboxylic acids, such as dibutyltin dilaurate and dibutyltin diacetate, stannous octanoate, ferrous octanoate, zinc napthenate, zinc octanoate, lead 2-ethylhexanoate; organotitanium compounds such as tetrabutyl titanate and 2,5-di-isopropoxy-bis(ethylacetate)titanium; and partially chelated derivatives of these salts with chelating agents such as acetoacetic acid esters and beta-diketones. A sufficient quantity of catalyst (D) may be added to accelerate the cure of the adhesive composition. This amount can readily be determined by the skilled artisan through routine experimentation and is typically 0.01 to 3 percent based on the combined weight of (A) and (B). The compositions of this invention may be prepared by combining the organopolysiloxane resin (A) and silane (C), preferably in the presence of a solvent and thereafter adding to the mixture the diorganopolysiloxane polymer (B). The composition may be applied from the solvent or the solvent may then be stripped off to provide an essentially solvent-free composition. Catalyst (D) is then optionally added to the solvent based or stripped product. The stripping (devolatilization) of the adhesive compositions are effectively accomplished by heating the mixture under vacuum, for example, at 90°C. to 150°C. and less than 14.6 kPa (100 millimeters) of mercury in a batch operation. The removal of solvent can also be accomplished by any of the known techniques, such as contact with a stream of inert gas, evaporation, distillation, thin film stripping. Excessively high temperatures should be avoided when all the components are being devolatilized. A temperature of 200°C., and preferably 150°C., should not be exceeded. In addition to the above components, a filler (E) may be optionally added to our compositions. The filler may be added in an amount up to 80 wt%, preferably up to 35 wt%. Fillers useful in this invention are exemplified by inorganic materials such as pyrogenic silica, precipitated silica and diatomaceous silica, ground quartz, aluminum silicates, mixed aluminum and magnesium silicates, zirconium silicate, mica powder, calcium carbonate, glass powder and fibers, titanium oxides of the pyrogenic oxide and rutile type, barium zirconate, barium sulphate, barium metaborate, boron nitride, lithopone, the oxides of iron, zinc, chrome, zirconium and magnesium, the different forms of alumina (hydrated or anhydrous), graphite, conducting or nonconducting lamp blacks, asbestos and calcined clay and organic materials such as the phthalocyaniines, cork powder, sawdust, synthetic fibers and synthetic polymers (polytetrafluoroethylene, polyethylene, polypropylene, polystryene and polyvinyl chloride). The filler may be of a single type or mixtures of several types. The above methods for producing the composition of the instant invention are preferably carried out in the presence of a solvent. The solvent is preferably the same one used to prepare the resin component, for example, a hydrocarbon liquid such as benzene, toluene, xylene, heptane and a silicone liquid such as cyclic or linear polydiorganosiloxanes. In the preparation of our compositions, a process catalyst (F) may be optionally added to facilitate the reaction of the hydroxyl groups on the resin (A) with the hydrolyzable groups on the silane (C). Catalysts known in the art for facilitating a reaction between the hydroxyl and hydrolyzable groups are useful in the instant invention. Suitable catalysts are amines, tin salts such as dibutyltin dilaurate, dibutyltin diacetate and stannous octanoate and titanates such as tetra n-butyl titanate or 2,5-diisopropoxy-bis(ethylacetate)titanium. A sufficient quantity of catalyst (F) is added facilitate the reaction between the hydroxyl groups and the silane. Typically, 0.01 to 2 weight percent is added based on the combined weight of (A) and (C). Preferably from 0.025 to 1.0 weight percent is added. The process catalyst is de-activated by an appropriate agent after the resin (A) and silane (C) have been reacted. It is, of course, understood that the above procedures are to be carried out in the absence of moisture to prevent premature curing of the compositions. This also applies to subsequent storage of the compositions. So that those skilled in the art can understand and appreciate the invention taught herein, the following examples are presented. RESIN 1 is a 72% solution in xylene of a solid MQ resin consisting of trimethylsiloxane units and SiO 4/2 units in a molar ratio of 0.8:1 and having a silicon-bonded hydroxyl content of 2.6 weight percent based on FTIR and a number average molecular weight (Mn) of 5,000. RESIN 2 is a 62% solution in xylene of Resin 1 wherein the resin has been capped with trimethylsiloxy groups so as to provide a residual silicon-bonded hydroxyl content of 1.0 wt% based on solids as determined by Si 29 NMR. FLUID A is a polydimethylsiloxane fluid having a viscosity of approximately 450 mm 2 /s terminated with the units of the formula -CH 2 CH 2 Si(Me) 2 OSi(Me) 2 CH 2 CH 2 Si(OMe) 3 . FLUID B is a polydimethylsiloxane fluid having a viscosity of approximately 2,000 mm 2 /s terminated with the units of the formula -CH 2 CH 2 Si(Me) 2 OSi(Me) 2 CH 2 CH 2 Si(OMe) 3 . FLUID C is a triethoxysilyl-capped polydimethylsiloxane fluid having a viscosity of 2,000 mm 2 /s. TBT is tetra n-butyl titanate. TDIDE is 2,5-di-isopropoxy-bis(ethylacetate)-titanium. SLURRY A is a mixture of 6 parts TBT, 17 parts of diisopropoxy di(ethoxyacetoacetyl)titanate in a mixture of approximately 70 parts of methyltrimethoxysilane, 3 parts of aminoethylaminopropyltrimethoxysilane and 3 parts of 3-mercaptopropyltrimethoxysilane. The Mn of the above resins was determined by gel-permeation chromatography (GPC) using Varian™ TSK 4000 + 2500 columns at 35°C., a chloroform mobile phase at 1 mL/min and an IR detector set at 9.1 micrometers to detect Si-O-Si. The GPC was calibrated using narrow fractions of similar resins as standards. The Mn values reported herein exclude any neopentamer, (Me 3 SiO) 4 Si, present in the resin component. The trimethylsiloxy/SiO 4/2 /SiO 4/2 ratio of the resins was determined by 29 Si NMR and, in this case, the reported results include any neopentamer component present in the resin. The hydroxyl content of the resins was measured by an FTIR procedure based on ASTM E-168. This method comprises comparing the absorbance of a specific band in the infrared spectrum of the resin with the absorbance of the same band in a reference spectrum of known concentration. The strength of adhesive compositions was determined as a function of cure time under ambient conditions using a plastic box construction. The box construction comprised four integrally-formed side walls and a detachable, form-fitting bottom plate. The box had a generally rectangular cross-section measuring 3.5 cm wide x 6 cm long, had a wall height of 1.5 cm and had a wall thickness of 5 mm. Each side wall had a 3 mm wide recessed step along its bottom interior edge for receiving said bottom plate such that the exterior surface of the latter was flush with said edges when seated on said step. In a typical adhesion evaluation, the plate was detached and a thin bead of molten adhesive was extruded from a heated metal cartridge (approximately 150°C.) along the 3 mm wide step. The bottom plate was pressed into place to contact the adhesive on the step and thereby provide a box having an open top. The box additionally had external protrusions in two of its opposite walls which allowed it to be constrained in a special jig while the bottom plate was pushed out with the ram of an arbor press apparatus, the apparatus having been modified to measure the applied force. The force necessary to push the bottom plate out of the wall section was recorded and the test repeated on identical box constructions at various storage times at ambient conditions to evaluate adhesion and its improvement with cure. 172 grams of Resin 1 were combined with 47.6 grams of isobutyltrimethoxy silane and 1 gram of TBT. The mixture was allowed to sit overnight in a loosely capped jar. After 24 hours, 76.0 grams of Fluid B were added to the mixture in a flask and put onto a rotovap. Bath temperature was increased from room temperature to 60°C. while the flask rotated. After 2 hours, the bath temperature was increased to 90°C. and the mixture was stripped to less than 1.33 kPa (10 mm Hg). 1.0 g of TBT and 1.0 g of isobutyltrimethoxy silane were added and blended at 95°C. without vacuum. The resulting composition was transferred to an aluminum cartridge for application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as described above. After 2 weeks at room temperature the assembly was placed in a 150°C. oven for 30 minutes. The assembly was removed from the oven and immediately tested for the amount of force required to delaminate the lid from the box assembly. 44.5 Newtons (N) were required to delaminate the lid. Another box was placed in a 130°C. oven for 30 minutes. 53.4 N were required to delaminate the lid. The tests were repeated after 6 weeks cure at room temperature. An average of 35.6 N were required to delaminate the lid at 133°C. and 311.46 N at room temperature. 28 grams of Fluid C were combined with 10.75 grams of methyltrimethoxysilane and 0.35 grams TBT in a 3-neck reaction flask. 58.3 grams of Resin 1 were then added to the flask. The resultant mixture was heated to 60°C. and maintained at that temperature for approximately one hour, followed by devolatilization at reduced pressure of less than 1.33 kPa (10 mm Hg) at a ramped temperature up to 150°C. Once devolatilized, the system was restored to 101.3 kPa (1 atmosphere) and 0.35 gram of TDIDE was dispersed into the molten product. The material was then transferred to a metal cartridge for future application. The material was later applied to the inside rim of a plastic PBT box using a hot melt gun as above. Short term adhesive strength was monitored as a function of time. CURE TIME (room temp) FORCE (N) 20 min 151.2 1 hr 222.4 5 hr 364.7 1 day 471.5 7 days 507.1 After approximately 2 weeks cure at room temperature the assembly was then placed in a 150°C. oven for 30 minutes. The assembly was removed from the oven and immediately tested for the amount of force required to delaminate the lid from the box assembly. 44.5 N were required to delaminate the lid. COMPARATIVE EXAMPLE 3 67.4 grams of Resin 2 were combined with 28 grams of Fluid C followed by devolatilization at reduced pressure of less than 1.33 kPa (10 mm Hg) at a ramped temperature up to 150°C. Once devolatilized, the system was restored to 101.3 kPa (1 atmosphere) and 0.2 gram of TBT was dispersed into the molten product. The material was later applied to a metal cartridge for future application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as described above. Short term adhesive strength was monitored as a function of time. CURE TIME (room temp) FORCE (N) 20 min 111.2 1 hr 129.0 5 hr 284.7 1 day 373.6 7 days 431.5 After approximately 2 weeks cure at room temperature, the assembly was then placed in a 150°C. oven for 30 minutes. The assembly was removed from the oven and immediately tested for the amount of force required to delaminate the lid from the box assembly. 44.5 N were required to delaminate the lid. COMPARATIVE EXAMPLE 4 97.4 grams of Resin 2 were combined with 40 grams of Fluid A followed by devolatilization at reduced pressure of less than 1.33 kPa (10 mm Hg) at a ramped temperature up to 150°C. Once devolatilized, the system was restored to 101.3 kPa (1 atmosphere) and 1.0 gram of TBT was dispersed into the molten product. The material was then transferred to a metal cartridge for future application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as above. Short term adhesive strength was monitored as a function of time. After one month cure at room temperature, the force to delaminate the lid was 120.0 N at room temperature, 155.7 N at 130°C. and 75.6 N at 150°C. COMPARATIVE EXAMPLE 5 93.6 grams of Resin 2 were combined with 40 grams of Fluid A followed by the addition of 0.05 grams of Sn(Oct) 2 . The mixture was heated to 60°C. and held for 30 minutes. The mixture gelled during the heating step. EXAMPLE 1 93.6 grams of Resin 2 were combined with 4.1 grams of isobutyltrimethoxy silane and 0.05 grams of Sn(Oct) 2 in a flask and place on the rotovap. Bath temperature was raised to 70°C. and the flask was rotated in the bath for 1 hours. 0.5 gram of mercaptopropyltrimethoxysilane was added to the mixture to neutralize the catalyst. After 30 minutes, 2.5 grams were removed for analysis and then 39 grams of Fluid A were added to the remainder. The bath temperature was raised to 90°C. while rotating and the mixture was devolatilized to 1.33 kPa (10 mm Hg). 1 gram of TBT was added and allowed to mix for 5 minutes. The resulting composition was transferred to an aluminum cartridge for application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as described above. Short term adhesive strength was monitored as a function of time. After approximately 2 weeks cure at room temperature, one assembly was then placed in a 150°C. oven for 30 minutes and another was placed in a 130°C. oven for 30 minutes. Another assembly was tested after 30 minutes in a 130°C. oven after 6 weeks cure at room temperature. The assemblies were removed from the oven and immediately tested for the amount of force required to delaminate the lid from the box assembly. CURE TIME FORCE (N) 1 min @RT 35.6 24 hr @RT 444.8 2 wk @RT 756.2 @130°C(2wk) 169.0 @150°C 133.4 6 wk @RT 747.3 130°C (6 wk) 142.3 EXAMPLE 2 187.2 grams of Resin 2 were combined with 8.2 grams of isobutyltrimethoxy silane in a flask and place on the rotovap. Bath temperature was raised to 70°C. and the flask was rotated in the bath for 1 hour. 78 grams of Fluid A were added to the remainder. The bath temperature was raised to 90°C. while rotating and the mixture was devolatilized to 1.33 kPa (10 mm Hg). 2 grams of TBT were added and allowed to mix for 5 minutes. The resulting composition was transferred to an aluminum cartridge for application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as above. The force required to delaminate the lid after 6 weeks was 769.5 N at room temperature and 142.3 N at 130°C. EXAMPLE 3 151 grams of a mixture, prepared by blending 225 grams of Resin 2 with 9.6 grams of isobutyltrimethoxy silane, were combined with 60.0 grams of Fluid A followed by the addition of 0.08 grams of Sn(Oct) 2 . The mixture was heated to 50°C. and held there for 30 minutes. 0.75 gram of mercaptopropyltrimethoxysilane was added to the mixture to neutralize the catalyst. After 20 minutes, the mixture was devolatilized and 1.50 grams of TBT were added to the devolatilized product at room temperature. The resulting composition was transferred to an aluminum cartridge for application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as above. The force required to delaminate the lid after 6 weeks was 738.4 N at room temperature and 164.6 N at 130°C. EXAMPLE 4 133.7 grams of a mixture, prepared by blending 125.9 grams of Resin 2 with 9.1 grams of methyltri(ethylmethylketoxime)silane; were combined with 51.6 grams of Fluid A followed by the addition of 0.07 gram of Sn(Oct) 2 . The mixture was heated to 50°C. and held there for 30 minutes. 0.65 gram of mercaptopropyltrimethoxysilane was added to the mixture to neutralize the catalyst. After 30 minutes, the mixture was devolatilized and 1.29 grams of TBT were added to the devolatilized material. The resulting composition was transferred to an aluminum cartridge for application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as described above. The force required to delaminate the lid after 6 weeks was 890+ N at room temperature and 244.6 N at 130°C. EXAMPLE 5 93.6 grams of Resin 2 were combined with 4.1 grams of isobutyltrimethoxy silane and 0.025 gram of Sn(Oct) 2 in a flask and place on the rotovap. Bath temperature was raised to 70°C. and the flask was rotated in the bath for 1 hours. 0.25 gram of mercaptopropyltrimethoxysilane was added to the mixture to neutralize the catalyst. After 30 minutes, 39 grams of Fluid A were added to the remainder. The bath temperature was raised to 90°C. while rotating and the mixture was devolatilized to 1.33 kPa (10 mm Hg). 1 gram of TBT was added and allowed to mix for 5 minutes. The resulting composition was transferred to an aluminum cartridge for application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as above. The force required to delaminate the lid after 6 weeks was 609.4 N at room temperature and 75.6 N at 130°C. EXAMPLE 6 97.4 grams of Resin 2 and methyltri(ethylmethylketoxime)silane (amounts given in Table 1) were combined. The mixture was heated to 60°C. and held there for 30 minutes. 40 grams of Fluid B were added to the mixture. The mixture was devolatilized and 1.0 gram of TBT was added to the devolatilized material. The resulting composition was transferred to an aluminum cartridge for application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as above. The tests at the elevated temperatures were conducted after at least one month's cure at room temperature. A B C D Amt. Ketoxime Silane (g) 6.8 4.9 2.4 0.0 Force to delaminate (N) 20 min @ RT 40.0 53.4 80.1 84.5 24 hr @ RT 573.8 556.0 462.6 302.5 1 week @ RT 880.7 814.0 769.5 498.2 1 month @ RT 702.8 680.5 631.6 400.3 130°C 355.8 338.0 204.6 106.8 150°C 289.1 271.3 115.6 102.3 EXAMPLE 7 97.4 grams of Resin 2, isobutyltrimethoxysilane (amount given in Table 2) and 0.05 gram of Sn(Oct) 2 were combined. The mixture was heated to 75°C. and held there for 30 minutes. 0.5 gram of mercaptopropyltrimethoxysilane was added to the mixture to neutralize the catalyst. The mixture was held at 75°C. for 30 minutes. 40 grams of Fluid B were added to the mixture. The mixture was devolatilized and 1.0 gram of TBT was added to the devolatilized material. The resulting composition was transferred to an aluminum cartridge for application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as above. The tests at the elevated temperatures were conducted after at least one month cure at room temperature. A B C D Amt. Methoxy Silane (g) 4.3 2.9 1.4 0.0 Force to delaminate (N) 20 min @ RT 102.3 133.4 115.6 84.5 24 hr @ RT --- --- --- 302.5 1 week @ RT 382.5 462.6 409.2 498.2 1 month @ RT 471.5 471.5 600.5 400.3 130°C 177.9 195.7 97.9 106.8 150°C 177.9 137.9 129.0 102.3 EXAMPLES 8-9 97.4 grams of Resin 2, 4.1 grams of isobutyltrimethoxy silane and 40.0 grams of Fluid A were combined followed by the addition of 0.05 gram of DBTDL. The mixture was heated to 50°C. (Example 8), 100°C. (Example 9) and held there for 30 minutes. 0.5 gram of mercaptopropyltrimethoxysilane was added to the mixture to neutralize the catalyst. After 30 minutes, each mixture was devolatilized and 1.0 gram of TBT was added to each devolatilized product. The resulting compositions were transferred to aluminum cartridges for application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as above. The force required to delaminate the lid after one month was 711.7 N (Example 8), 747.3 N (Example 9) at room temperature; 195.7 N (Example 8), 320.3 N (Example 9) at 130°C., 124.5 N (Example 8) and 373.6 N (Example 9) at 150°C. EXAMPLE 10 6.97 grams of methyltri(ethylmethylketoxime) silane were combined with 96.6 grams of Resin 2 and reacted for an hour at 60°C. 40 grams of Fluid A were then added and thoroughly mixed with resin/silane mixture. The system was devolatilized and 1.0 gram of TBT and 0.5 gram of a reaction product of 73.5 wt% glycidoxypropyltrimethoxysilane and 26.5 wt% aminopropyltrimethoxysilane were added to the. molten mixture. The resulting composition was transferred to an aluminum cartridge for application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as above. The force required to delaminate the lid after one month was 756.2 N at room temperature; 240.2 N at 130°C. and 177.9 N at 150°C. EXAMPLE 11 The following silanes were used in this example: Silane A: glycidoxypropyltrimethoxysilane Silane B: aminoethylaminopropyltrimethoxysilane Silane C: 3-methacryloxypropyltrimethoxysilane Silane D: phenyltrimethoxysilane In these examples, 97.4 grams of Resin 2 were combined with the silane (See Table 3) and 40.0 grams of Fluid A. 0.05 gram of DBTDL was added and the mixture was heated to 100°C. and held there for 30 minutes. 0.5 gram of mercaptopropyltrimethoxysilane was added to the mixture to neutralize the catalyst. After 30 minutes, the mixture was devolatilized and 1.0 gram of TBT was added to the molten material. The resulting composition was transferred to an aluminum cartridge for application. The material was then transferred to the inside rim of a plastic PBT box using a hot melt gun as above. Results are given in Table 3. Silane A B C D Amt. Silane (g) 7.5 7.1 5.7 6.3 Force to delaminate (N) 20 min @ RT 17.8 53.4 26.7 26.7 1 hr @ RT 22.2 102.3 44.5 62.3 1 day @ RT 222.4 160.1 275.8 209.1 1 week @ RT 800.6 667.2 862.9 774.0 1 month @ RT >890 756.2 849.6 802.9 130°C 489.3 133.4 253.5 282.4 150°C 542.7 124.5 240.2 255.8 EXAMPLE 12 250 grams of Resin 2 were combined with 19 grams of isobutyltrimethoxysilane and reacted for 4 hours at 100°C. in the presence of stannous octoate. 0.2 gram of mercaptopropyltrimethoxysilane was then added to neutralize the catalyst and the system was reacted for another 30 minutes. The resulting resin was cooled to room temperature. To 104.8 grams of this resin were added 72 grams of mixture of approximately 53 wt% of a dimethylsiloxane fluid terminated with (CH 3 O) 3 SiCH 2 CH 2 Si(CH 3 ) 2 O- groups and having a viscosity of approximately 65,000 mm 2 /s; 37 wt% CaCO 3 (ppt, stearate); 5 wt% calcium carbonate treated with stearic acid; 1 wt% lampblack and 4 wt% of Slurry A. The resulting mixture was allowed to blend for 2 hours at 100°C. The mixture was devolatilized by heating at 130°C. at less than 1.33 kPa (10 mm Hg) pressure and then maintained for an additional 15 minutes at that condition. The system was then restored to atmospheric pressure and the product was recovered. EXAMPLE 13 97.4 grams of Resin 2 were combined with 8.79 grams of methyl tri(methylethylketoximo)silane) and blended at room temperature for 30 minutes. To this resin were added 72.0 grams of mixture of approximately 53 wt% of a dimethylsiloxane fluid terminated with (CH 3 O) 3 SiCH 2 CH 2 Si(CH 3 ) 2 O- groups and having a viscosity of approximately 65,000 mm 2 /s; 37 wt% CaCO 3 (ppt, stearate); 5 wt% calcium carbonate treated with stearic acid; 1 wt% lampblack; and 4 wt% of Slurry A. The resulting mixture was allowed to blend for 2 hours at 100°C. The mixture was de-volatilized by heating at 130°C. at less than 1.33 kPa (10 mm Hg) pressure and then maintained for an additional 15 minutes at that condition. The system was then restored to atmospheric pressure and the product was recovered. EXAMPLE 14 To 97.4 grams of Resin 2 were added 72.0 grams of mixture of approximately 53 wt% of a dimethyl siloxane fluid terminated with (CH 3 O) 3 SiCH 2 CH 2 Si(CH 3 ) 2 O- groups and having a viscosity of approximately 65,000 mm 2 /s; 37 wt% CaCO 3 (ppt, stearate); 5 wt% calcium carbonate treated with stearic acid; 1 wt% lampblack; and 4 wt% of Slurry A. The resulting mixture was allowed to blend overnight. The mixture was devolatilized by heating at 130°C. at less than 1.33 kPa (10 mm Hg) pressure and then maintained for an additional 15 minutes at that condition. The system was then restored to atmospheric pressure and the product was recovered. EXAMPLE 15 To 89.3 grams of Resin 2 were added 81.0 grams of mixture of approximately 53 wt% of a dimethyl siloxane fluid terminated with (CH 3 O) 3 SiCH 2 CH 2 Si(CH 3 ) 2 O- groups and having a viscosity of approximately 65,000 mm 2 /s; 37 wt% CaCO 3 (ppt, stearate); 5 wt% calcium carbonate treated with stearic acid; 1 wt% lampblack; and 4 wt% of Slurry A. The resulting mixture was allowed to blend overnight. The mixture was de-volatilized by heating at 130°C. at less than 1.3 kPa (10 mm Hg) pressure and then maintained for an additional 15 minutes at that condition. The system was then restored to atmospheric pressure and the product was recovered. EXAMPLE 16 The adhesives prepared in Examples 12 - 15 were cast as films on 0.051 mm (2 mil) Mylar™ sheets which had been treated with a fluorosilicone release coating and cured at room temperature for approximately 2 weeks. Tensile bars having a width and gauge length of 6.4 and 22.9 mm (0.25 and 0.90 inches), respectively, were stamped from the resultant coated sheets; isolated as free films; and evaluated for tensile and elongation characteristics. Samples were tested using an Instron™, Table Model 1122, a crosshead speed of 5.1 cm/min (2 inches/min.) and a load cell sufficient to accurately measure loads ranging from 454 to 4,540 g (one to ten pounds). For comparison, a film was prepared from a mixture of approximately 53 wt% of a dimethyl siloxane fluid terminated with (CH 3 O) 3 SiCH 2 CH 2 Si(CH 3 ) 2 O- groups and having a viscosity of approximately 65,000 mm 2 /s; 37 wt% CaCO 3 (ppt, stearate); 5 wt% calcium carbonate treated with stearic acid; 1 wt% lampblack; and 4 wt% of Slurry A. Results are reported in Table 4. Tensile @ Break (MPa) Elongation @ Break (%) Comparison 2.165 400 Example 12 0.996 1200 Example 13 1.903 720 Example 14 1.662 952 Example 15 2.489 999

Claims: A pressure sensitive adhesive composition comprising (A) 5 to 90 parts of a hydrocarbon or silicone liquid soluble, capped, organopolysiloxane resin consisting of R 3 SiO 1/2 siloxane units and SiO 4/2 siloxane units, wherein R is a monovalent hydrocarbon radical having 1 to 18 carbon atoms; there being from 0.5 to 1.5 R 3 SiO 1/2 units for every SiO 4/2 unit; said resin containing less than 1.2 weight percent of silicon-bonded hydroxyl groups based on the total weight of (A) solids as determined by Si 29 NMR; (B) 10 to 95 parts of a diorganopolysiloxane polymer, each terminal group thereof containing at least two alkoxy radicals of the formula -ZSiR 1 x (OR 2 ) 3-x wherein R 1 is a monovalent hydrocarbon radical, R 2 is selected from alkyl radical or alkoxyalkyl radical, Z is selected from hydrocarbons, hydrocarbons containing one or more hetero atoms selected from oxygen, nitrogen and sulfur, siloxanes and combinations thereof, and the subscript x has a value of 0 or 1; said polymer having a viscosity at 25°C. of 20 to 100,000 mm 2 /s; wherein the amount of (A) and (B) equals 100 parts; and (C) 1 to 30 parts per 100 parts of resin (A) solids of a silane represented by monomers of the formula R 3 4-y SiX y or oligomeric reaction products thereof, in which R 3 is selected from hydrocarbon radicals or substituted hydrocarbon radicals having 1-6 carbon atoms, X is a hydrolyzable group and y is 2 to 4. The composition as claimed in claim 1 wherein X is selected from alkoxy radicals having 1 to 4 carbon atoms, ketoxime radicals, aminoxy radicals, acetamido radicals, N-methylacetamido radicals and acetoxy radicals. The composition as claimed in claim 1 wherein silane (C) is selected from the group consisting of methyltrimethoxysilane, methyltriethoxysilane, propyltrimethoxysilane, tetramethoxysilane, tetraethoxysilane, phenyltrimethoxysilane, isobutyltrimethoxysilane, ethyltrimethoxysilane, glycidoxypropyltrimethoxysilane, aminoethylaminopropyltrimethoxysilane, aminopropyltriethoxysilane and 3-methacryloxypropyltrimethoxysilane. The composition as claimed in claim 1 wherein there is additionally (D) sufficient cure catalyst to accelerate the cure of said composition. The composition as claimed in claim 1 wherein there is additionally (E) up to 80 weight percent filler.

Inventors: CIFUENTES MARTIN ERIC, STRONG MICHAEL RAYMOND, VANWERT BERNARD, CIFUENTES, MARTIN ERIC, STRONG, MICHAEL RAYMOND, VANWERT, BERNARD
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1995
Main classification: C09J183
IPC codes: C08L83, C09J183, C08K5, C08K3