Silane modified polyoxometalate anions

Abstract: Silane modified polyoxometalate anions, represented by the formula YZ(SiRR') n , were prepared by reacting a silane having two hydrolyzable groups with a lacunary polyoxometalate anion. In the above formula, Z is M 11 O 39 -12 , M 9 0 34 -14 or M 17 O 60 -20 , where M is tungsten or molybdenum; Y is As +5 , Si +4 , B +3 , Ge +4 , P +5 or Fe +3 ; when Z is M 11 O 39 -12 ; Y is Si +4 , Ge +4 , or P +5 when Z is M 9 0 34 -14 and Y is As 2 +10 or P 2 +10 when Z is M 17 O 61 -20 ; R is a monovalent hydrocarbon radical having from 1 to 24 carbon atoms; R' is hydrogen or R and n represents the number of (RR'Si) +2 groups bonding to the polyoxometalate anion which has a value from 1 to 3.

Description: This invention relates to the modification of inorganic metal oxide anions, referred to as polyoxometalate anions, by the reaction with silanes having two hydrolyzable groups. Although the vast majority of metal oxides are insoluble or have a limited solution chemistry, the chemical literature points out there is an important exception. This exception includes a class of oxides that are soluble in aqueous or nonaqueous solutions, charged and derived from polyvalent metals such as molybdenum, tungsten and less frequently vanadium, niobium or tantalum and/or mixtures thereof, in their highest oxidation states. These oxides are referred to in the literature as "isopolyanions" when only a polyvalent metal and oxygen are involved and are represented by the formula (M m O y ) p- . If an additional metallic or non-metallic element is present, these oxides are referred to as "heteropolyanions" and are represented by the formula (X x M m O y ) q- . Polyoxometalate anions fall into the latter category. In the above formulae, M is a polyvalent metal of the type already described, X is the "heteroatom" and is almost any element in the periodic table other than a noble gas; O is oxygen, x, m and y are integers where x << m, and p and q represent the charge on the anion. This anion charge is calculated by multiplying the valences of X, M and O by the value of the integer x, m and y associated with that atom and adding the products together. Although a majority of polyoxometalate anions have been formed in aqueous solution, nonaqueous syntheses have also been developed. A thorough discussion of polyoxometalate anions is found in a text by Michael Thor Pope entitled "Heteropoly and Isopoly Oxometalates" published in 1983 by Springer-Verlag. As discussed therein, these anions may generally be isolated from solution by addition of cations, typically alkali metals, NH 4 + or R 4 N + , where R represents a monovalent hydrocarbon. The type of cation will affect the chemical and physical properties of the polyoxometalate anion, including its solubility, and the properties of the reaction products of said polyoxometalate anion. The chemical literature also points out that the structures of polyoxometalate anions appear controlled by the electrostatic and radius-ratio principles seen for extended ionic lattices. Although there are a very large number of known polyoxometalate anions, investigators have found that most of these are characterized by relatively few structures. These structures consist of groups of MO 6 octahedra surrounding XO 4 tetrahedra that share edges, corners and occasionally faces with adjacent polyhedra. The structure of a number of polyoxometalate anions is discussed in the above referenced article by Pope, in a text by M. Pope and A. Muller in Angew. Chem., (International English Edition), 30 (1991) 34-48 and in an article entitled "Heteropoly Compounds of Molybdenum and Tungsten" by G. Tsigdinos that is part of a collection entitled Topics in Current Chemistry, 76 (1978) 1-64. The structure of a particular polyoxometalate anion, the heteropolyacid H 3 PW 12 O 40 *6H 2 O, is described by J.F. Keggin, in Nature, 131 (1933) 908-909. The acidic anion was determined to be a coordinated structure having a central PO 4 tetrahedron group surrounded by 12 WO 6 octahedra groups, linked together by shared oxygen atoms. Polyoxometalate anions having the polyhedron type structure are known as having a Keggin structure. Keggin structure anions of the formula (XM 12 O 40 ) n- , where M is molybdenum or tungsten and X is As +5 , Si +4 , B +3 , Ge +4 , P +5 , Fe +3 or Co +2 , have been reported in the literature. When X is silicon and M is tungsten or molybdenum, n is 4. Under mildly basic conditions, one or more of the MO groups from a polyoxometalate anion is removed to form a deficient or "lacunary" structure. The structure resulting from removal of one MO group is then represented by the formula (XM 11 O 39 ) n- . In the above example, when X is silicon and M is tungsten or molybdenum, n is 8. The vacancy left by the departing group is filled with other atoms or groups. Another common structure of polyoxometalate anions is referred to as a Dawson structure and is represented by the formula (X 2 M 18 O 62 ) n- . The heteroatom represented by X in this structure is P 5+ or As 5+ . A "lacunary" Dawson structure is formed by the removal of one or more MO groups. When one MO group is removed (which is the most common case), the "lacunary" Dawson structure is represented by the formula (X 2 M 17 O 61 ) n- . Reactions of the lacunary polyoxometalate anion W 11 SiO 39 8- with RSiCl 3 , where R is C 2 H 5 , C 6 H 5 , NC(CH 2 ) 3 or C 3 H 5 in an unbuffered aqueous solution have been reported by Knoth, J. Am. Chem. Soc., 1979, 101:3, 759-760. Knoth determined that the WO 4+ unit required for a complete, or "non-lacunary" structure, was replaced with (RSi) 2 O 4+ so the anion product corresponded to the composition (RSi) 2 W 11 SiO 40 4- . The structure Knoth postulated for this product, which was later confirmed, required that an oxygen atom bridge the two silicon groups that had been added to the polyoxometalate anion reactant. P. Judenstein et al., J. Chem. Soc., Dalton Trans., (1991) 1991-1997, disclosed the synthesis in water and acetonitrile of polyoxometalate salts or acids having the general formula [R] 4 [SiW 11 O 40 (SiR'') 2 ], where R= H + , K + , or NR' 4 + ; R'= methyl or butyl and R"= ethyl, vinyl, phenyl or decyl. The experiments described the reaction of W 11 SiO 39 8- with various R"SiX 3 compounds where X represented chlorine or ethoxy and R" was as described above. The resulting structure of the reaction products was determined to be as described by Knoth, such that an oxygen atom bridged the two silicon groups that were added. Judenstein, Chem. Mater. (1992) 4 , 4-7, shows the synthesis of negatively charged macromolecules by incorporating organically functionalized polyoxometalate anions in an organic polymeric backbone. The organically modified polyoxometalate anion was obtained by reacting W 11 SiO 39 8- with RSiCl 3 , where R was selected from vinyl, allyl and methacryl or RSi(OEt) 3 where R was styryl and the reaction products obtained therefrom were then reacted further using a free radical polymerization. Ammari et al. New. J. Chem. (1991) 15 , 607-608, reveals the reaction of the trivacant W 9 SiO 34 10- with RSiCl 3 where R was alkyl or aryl in dry acetonitrile. In a prior work (EP-A 0 659 807), we provide organosiloxane compounds containing silicon-bonded polyoxometalate structures that are present as pendant groups and methods for their preparation. These methods include reacting a polysiloxane containing two or three hydrolyzable groups on the terminal silicon with a lacunary polyoxometalate anion and reacting a polyorganosiloxane containing at least one silicon-bonded hydrogen atom with the product of a lacunary polyoxometalate anion and a silane having two or three hydrolyzable groups. The materials found in the prior art have uses in coatings; electronics, for example as sensors; magnetic/electric storage devices; catalysts; ion exchange membranes in chromatography and as self-reinforced elastomers. One objective of this invention is to prepare silane modified polyoxometalate anions using silanes having two hydrolyzable groups. Another objective of this invention is the preparation of materials which are potentially used to catalyze stereospecific reactions or used as building blocks for organic-silicone-inorganic polymers. These materials are also potentially used as additives in polymers to perform specific functions, for example, electrical conductivity, photochromicity or electrochromicity. The aforesaid objects of the present invention are achieved by reacting a silane having two hydrolyzable groups with a polyoxometalate anion having a lacunary structure to form a silane modified polyoxometalate anion. One embodiment of this invention provides silane modified polyoxometalate anions represented by the formula YZ(SiRR') n where Z is selected from the group consisting of M 11 O 39 -12 , M 9 O 34 -14 and M 17 O 61 - 20 , where M is tungsten or molybdenum; Y is As +5 , Si +4 , B +3 , Ge +4 , P +5 or Fe +3 when Z is M 11 O 39 -12 ; Y is Si +4 , Ge +4 , or P +5 when Z is M 9 O 34 -14 ; and Y is As 2 +10 or P 2 +10 when Z is M 17 O 61 -20 ; and R is selected from monovalent hydrocarbon radical having from 1 to 24 carbon atoms, halogenated hydrocarbon or carbon radicals, epoxy radicals, amino radicals, mercapto radicals and methacrylo radicals; R' is selected from a hydrogen atom, monovalent hydrocarbon radicals having from 1 to 24 carbon atoms, halogenated hydrocarbon or carbon radicals, epoxy radicals, amino radicals, mercapto radicals and methacrylo radicals; and n represents the number of (SiRR') +2 groups bonding to the polyoxometalate anion and has a value from 1 to 3. The silane modified polyoxometalate products are anionic and therefore will associate with various cations. Some typical cations include hydrogen; alkali metals such as Li + , Na + , or K + ; alkaline earth metals such as Ba +2 , Mg +2 or Ca +2 ; or R 2 4 N + . Each R 2 represents a monovalent hydrocarbon radical that may or may not be identical to the other three R 2 radicals. The cation is preferably R 2 4 N + where the R 2 radicals are preferably identical and are preferably alkyl containing from 1 to 10 carbon atoms such as methyl, ethyl, iso-propyl, butyl, hexyl and decyl and is most preferably butyl. The type of cation will influence the solubility characteristics of the products. This invention also provides a method for preparing silane modified polyoxometalate anions, the method comprising reacting a silane having a general formula RR'SiX 2 where R is selected from monovalent hydrocarbon radicals having from 1 to 24 carbon atoms, halogenated hydrocarbon or carbon radicals, epoxy radicals, amino radicals, mercapto radicals and methacrylo radicals; R' is selected from hydrogen atom, monovalent hydrocarbon radicals having from 1 to 24 carbon atoms, halogenated hydrocarbon or carbon radicals, epoxy radicals, amino radicals, mercapto radicals and methacrylo radicals; and X is a hydrolyzable group; with a polyoxometalate anion represented by the formula YZ where Z is selected from the group consisting of M 11 O 39 -12 , M 9 0 34 -14 and M 17 O 61 -20 , where M is tungsten or molybdenum; Y is As +5 , Si +4 , B +3 , Ge +4 , P +5 or Fe +3 when Z is M 11 O 39 -12 ; Y is Si +4 , Ge +4 , or P +5 when Z is M 9 O 34 -14 and Y is As 2 +10 or P 2 +10 when Z is M 17 O 61 -20 . The polyoxometalate anion is represented by the formula YZ in the present invention. The letter Z describes various lacunary or deficient "isopolyanions," including M 11 O 39 -12 , M 9 O 34 -14 and M 17 O 61 -20 , where M is a polyvalent metal. The letter Y describes various "heteroatoms" which together with the isopolyanion forms "heteropolyanions" of which polyoxometalate anions are a part. In the present invention, M is preferably tungsten (W +6 ) or molybdenum (Mo +6 ) and most preferably is tungsten. Y is As +5 , Si +4 , B +3 , Ge +4 , P +5 or Fe +3 when Z is M 11 O 39 -12 , Si +4 , Ge +4 or P +5 when Z is M 9 0 34 -14 and As 2 +10 or P 2 +10 when Z is M 17 O 61 -20 . When Z represents M 11 O 39 -12 or M 9 0 34 -14 , Y is preferably Si +4 and P +5 and is most preferably Si +4 . When Z is M 17 O 61 -20 , Y is preferably P 2 +10 . Polyoxometalate anions have open valences and are therefore a charged species. The charge is determined by multiplying the valences of the atoms associated with Y and Z by the value of the integer associated with that atom and adding the products together. For the polyoxometalate anion YZ, where Y is Si +4 and Z is M 11 O 39 with M being tungsten or molybdenum, the charge is equal to the sum of the valence of silicon (+4), 11 times the valence of M (+6) and 39 times the valence of oxygen (-2), which totals -8. Since the polyoxometalate anion has a negative charge, it will associate with various cations. Some typical cations are hydrogen; alkali metals such as Li + , Na + , or K + ; alkaline earth metals such as Ba +2 , Mg +2 or Ca +2 ; or R 2 4 N + , where each R 2 represents a monovalent hydrocarbon that may or may not be identical to the other three R 2 radicals. The cation is preferably R 2 4 N + where the R 2 radicals are preferably identical and are preferably alkyl containing from 1 to 10 carbon atoms such as methyl, ethyl, iso-propyl, butyl, hexyl and decyl and is most preferably butyl. Methods for preparing lacunary polyoxometalate anions used as reactants for preparing the silane modified polyoxometalate anions of this invention are reported in the chemical literature, see, for example, Inorganic Syntheses; Ginsberg, A.P., Ed., John Wiley & Sons, Vol. 27, Chapter 3, 1990. Specific references include Teze et al., J. Inorg. Nucl. Chem. (1977) 39 , 999, for the preparation of the potassium salt of SiW 11 O 39 8- ; Herve et al., Inorg. Chem., (1977) 16 , 2115 for the synthesis of the sodium salt of SiW 9 O 34 10- and Contant, R., Inorganic Syntheses; Ginsberg, A.P., Ed., John Wiley & Sons, Vol. 27, Chapter 3, pp 104-107, 1990, for the synthesis of the potassium salt of (P 2 W 18 O 62 ) 6- . Non-lacunary or complete Keggin structures of polyoxometalate anions corresponding to the formula YM 12 O 40 , are prepared by adding an acid to an aqueous solution of sodium tungstate or sodium molybdate in the presence of a solubilized compound, such as an alkali metal silicate, containing the heteroatom represented by Y in the general formula for the polyoxometalate anion. Another method for preparing non-lacunary polyoxometalate anions utilizes a phase transfer procedure described by Katsoulis and Pope, J. Am. Chem. Soc., (1984) 106 , 2737. This procedure converts a water soluble polyoxometalate salt, such as an alkali metal polyoxometalate salt, to a salt that is soluble in non-polar organic solvents, such as a tetraalkylammonium polyoxometalate salt. In this instance, the nitrogen-bonded radicals contain more than four carbon atoms and preferably six or seven carbon atoms. In the present invention, lacunary polyoxometalate anions are reacted with silanes having two hydolyzable groups. The lacunary structures are generated during preparation of the polyoxometalate anion, by using the appropriate ratio of tungsten or molybdate salt to heteroatom compound corresponding to the formula of the desired structure and by maintaining the pH of the reaction mixture at no lower than 4.8. Alternatively, a complete polyoxometalate anion structure is changed to a lacunary structure by hydrolysis under basic conditions. Specific reactants and conditions for preparing polyoxometalate anions are described in the literature so that a complete discussion of the subject is not required in this specification. The preparation of preferred polyoxometalate anions is described in the accompanying examples. The silane reactants used for modifying the polyoxometalate anions in the present invention are represented by the general formula RR'SiX 2 . The letter X represents hydrolyzable groups bonded to silicon and R and R' represent other groups which may, or may not, be identical and which may, or may not, contain functionality also bonded to the silicon atom. Hydrolyzable groups include any group attached to silicon which is hydrolyzed by water at room temperature. Suitable hydrolyzable groups that are represented by X include, but are not limited to, halogen atoms such as chlorine, bromine, fluorine or iodine; groups of the formula -OT when T is any hydrocarbon or halogenated hydrocarbon group such as methyl, ethyl, iso-propyl, octadecyl, allyl, hexenyl, cyclohexyl, phenyl, benzyl, beta-phenylether, 2-chloroethyl, chlorophenyl, 3,3,3-trifluoropropyl or bromocyclohexyl; any hydrocarbon ether radical such as 2-methoxyethyl, 2-ethoxyisopropyl, 2-butoxyisobutyl, p-methoxyphenyl or -(CH 2 CH 2 O) 2 CH 3 ; any acyl radical such as acetyl, propionyl, benzoyl, cyclohexoyl, acrylyl, methacrylyl, stearyl, naphthoyl, trifluoroacetyl, chlorobenzoyl or bromopropionyl; any acyloxy group such as acetoxy, benzoyloxy, propionoxy, or acryloxy; or any N,N-amino radical such as dimethylamino, diethylamino, ethylmethylamino, diphenylamino or dicyclohexylamino. X is also any amino radical such as NH 2 , dimethylamino, diethylamino, methylphenylamino or dicyclohexylamino; any ketoxime radical of the formula -ON=CL 2 or -ON=CL' in which L is any monovalent hydrocarbon or halogenated hydrocarbon as those shown for T above and L' is any divalent hydrocarbon radical both valences of which are attached to the carbon, such as hexylene, pentylene or octylene; ureido groups of the formula -N(L)CONL" 2 in which L is defined above and L" is hydrogen or any of the L radicals; carbamate groups of the formula -OOCNLL'' in which L and L" are defined above; or carboxylic amide radicals of the formula -NLC=O(L") in which L and L" are defined above. X is also the sulfate group or the sulfate ester groups of the formula -OSO 2 (OL) where L is as defined above; the cyano group; the isocyanate group; and the phosphate or phosphate ester groups of the formula -OPO(OL) 2 , where L is as defined above. Halogen atoms, particularly chlorine, alkoxy groups containing from 1 to 4 carbon atoms, particularly methoxy and acyloxy groups containing 2 to 6 carbon atoms, particularly acetoxy are preferred based on cost and the nature of the byproducts generated during reaction with the polyoxometalalate anion. Examples of suitable monovalent hydrocarbon radicals, including organofunctional radicals, that are represented by R and R', include but are not limited to, alkyl radicals such as methyl, ethyl, isopropyl, hexyl, octadecyl or myricyl; alkenyl radicals such as vinyl, allyl or hexenyl; alkynal radicals such as propargyl, cycloaliphatic radicals such as cyclopentyl, cyclohexyl or cyclohexenyl; aromatic hydrocarbons such as phenyl, tolyl, xylyl, xenyl, naphthyl or anthracyl; aralkyl hydrocarbon radicals such as benzyl, beta-phenylethyl, beta-phenylpropyl or gamma-tolylpropyl; halogenated hydrocarbon or carbon radicals such as 3,3,3-trifluoropropyl, tridecafluoro-1,1,2,2-(tetrahydrooctyl)-1-methyl or perfluoroalkyl; epoxy radicals such as 2,3-epoxypropyl, epoxyethyl, 2-(3,4 epoxycyclohexyl) or 3,4 epoxybutyl; amino radicals such as aminoethyl, aminoethylaminopropyl, 2-aminobutyl, 3-aminopropyl or methyl aminopropyl; mercapto radicals such as 3-mercaptopropyl or mercaptomethyl; and methacrylo radicals such as 3-methacryloxypropyl In addition, R' may be represented by hydrogen. R and R' are preferably ethyl, methyl, vinyl, 1-hexenyl, phenyl or 1,1,1,2,2,3,3,4,4-nonafluorohexyl, epoxy or amino. Most preferably, one or both of the groups on R or R' is a functional group which is capable of further reaction such as vinyl, hexenyl, epoxy or amino. If R and R' are not identical, the silicon atom is chiral and stereoisomers can form. This chirality creates the potential for designing stereospecific reactions using the present invention. These types of reactions are particularly utilized by the pharmaceutical industry in the production of drugs. Methods for preparing silanes containing two hydrolyzable groups and various hydrocarbon groups or hydrogen are described in the art and do not need to be further described here. The preferred silanes used in the examples are all commercially available. Silane modified polyoxometalate anions having the general formula YZ(RR 1 Si) n are prepared by reacting a silane containing two hydrolyzable groups with a lacunary polyoxometalate anion. The cation associated with the polyoxometalate anion is typically an alkali metal or tetralkyl ammonium. The reaction between the polyoxometalate anion and the silane is conducted in a homogeneous reaction or a heterogeneous reaction. The molar ratio of silane to polyoxometalate anion, used in either type reaction, is from 0.5 to 3 moles but preferably is greater than 1 and is more preferably 2:1. In a homogeneous reaction, the silane and polyoxometalate anion are placed in a solvent in which both are soluble and allowed to stir for some time. If, for example, a chlorosilane is used in the presence of water, there is no need for the addition of another reagent because it will hydrolyze very quickly generating HCl which assists in the coordination of silane to polyoxometalate anion. When a silane other than a halosilane is used, for example an alkoxy silane, one will need to add a catalyst to assist in the hydrolysis/coordination reaction. In most cases, this is an acid or basic catalyst, preferably HCl. The amount of catalyst used ranges from 0 to 2.5 equivalents per silane, with 2 equivalents per silane being preferred. The reaction takes place at temperatures ranging from 0°C. to the boiling point of the solvent, and are preferably conducted at ambient temperatures. Depending on temperature, the time for reaction ranges from minutes to hours, and at ambient temperatures the reaction time is preferably 2-3 hours. In a heterogeneous reaction, a polyoxometalate salt is brought into contact with a silane, dissolved usually in an organic solvent such as acetonitrile or mixtures of acetonitrile/toluene and allowed to stir for several hours. As in the homogeneous reaction, it is preferred that the silane hydrolyze, which assists in the coordination of silane to polyoxometalate anion. Therefore, when a silane other than a halosilane is used, for example, an alkoxy silane, one will need to add a catalyst to assist in the hydrolysis/coordination reaction. In most cases, this is an acid or basic catalyst, preferably HCl. The amount of catalyst used ranges from 0 to 3 equivalents per silane, with 2 equivalents per silane being preferred. A large excess of acid will convert the lacunary polyoxometalate anion to the "complete" Keggin structure thereby reducing the reaction yield. The reaction takes place at temperatures ranging from 0°C. to the boiling point of the solvent and is preferably conducted at ambient temperatures. Depending on temperature, the time for reaction ranges from 3 to 36 hours and at ambient temperatures the reaction time is preferably 24 hours. Whether the reaction is conducted in a heterogeneous manner or a homogeneous manner, the products are isolated in similar ways. One method is simply by evaporating the solvent. This method is used if the reaction is carried out using a polyoxometalate salt that is soluble in a nonpolar solvent such as toluene or methylene chloride. Another method to isolate the product is by adding a solvent that reduces the products' solubility; for example, from a water solution one could add ethanol, acetone or acetonitrile. If acetonitrile is the reaction solvent, one adds water and the product will precipitate. The preferred method to isolate the products is to add another cation to the silane modified polyoxometalate product mixture, which will then exchange with the cation that was initially added as the polyoxometalate salt, to form another salt. This new salt will either precipitate out of the solvent used, if it is insoluble in such solvent, or it can be precipitated out of solution by the addition of a different solvent. For example, if the solvent used is water, one can add organic cations, such as tetrabutylammonium or inorganic cations such as Ba +2 , Ca +2 and Cs +1 , and easily precipitate the product which is now associated with the new cation. If the solvent used is acetonitrile, one can add organic cations such as tetrabutylammonium bromide. In this case, the product associated with the new cation may not precipitate if it is soluble in in acetonitrile. However, one can easily get this product to precipitate by the addition of water or other solvent which the product associated with the new cation does not have solubility. In this invention, it is preferable to prepare the silane modified polyoxometalate anion in acetonitrile by reacting an alkali metal salt of the polyoxometalate anion with a silane by adding tetrabutylammonium bromide to provide the tetrabutylammonium salt of the silane modified polyoxometalate anion and, if necessary, by adding water to precipitate this salt out of solution. The silane modified polyoxometalate salts are stable in the absence of strong acids or bases in aqueous and nonaqueous environments. Lacunary polyoxometalate anions such as SiW 11 O 39 8- have a vacancy or "hole" where a WO 4+ has been removed from a complete polyoxometalate anion such as SiW 12 O 40 4- . The chemical literature has shown that when this lacunary polyoxometalate anion is reacted with silanes containing three hydrolyzable groups, two silane groups bond to the four oxygens in the polyoxometalate anion and an oxygen bridge connects the two silane groups. The silane modified polyoxometalate anion resulting from the reaction of SiW 11 O 39 8- with RR'SiX 2 has a valence of 4-, i.e., SiW 11 O 39 O(RR'Si) 2 4- . This valence is determined by adding the 2+ charge of each silane group to the charge of 8- of the lacunary polyoxometalate anion (2 x (2+) + (8-)). When a lacunary polyoxometalate anion is reacted with silanes containing two hydrolyzable groups, an oxygen bridge connecting the two silane groups does not typically result. However, experiments have shown that, if any of the R groups oxidize during the synthesis of the silane modified polyoxometalate anion, an oxygen bridge can be be observed in some of the reaction products as described in our Examples 12, 13 and 14. It has also been determined that in some instances, reaction products may contain mixtures such that there are products containing two silane groups bonded to the polyoxometalate anion and products having only one silane group bonded to the polyoxometalate anion. When only one silane group bonds to the lacunary polyoxometalate anion, two oxygen atoms remain with open valences and the resulting silane modified polyoxometalate anion has a valence which differs from the reaction product having two silane groups bonded to it. These two products are separable on the basis of overall negative charge. These results may be explainable as due to steric hindrance, i.e. larger R or R' groups on silicon restrict how many groups will bond to the available oxygens. In addition, it has been observed that increasing the molar concentration of the silane reactant may result in an increase in the monosubstituted reaction product. If, in the silane reactant RR'SiX 2 , R and R' are not identical, the silicon atoms are chiral and give rise to the formation of stereoisomers. The physical properties of the silane modified polyoxometalate anions depend upon a number of variables including the cation associated with it. The cation will also determine the solvents that are used as the reaction medium. Silane modified polyoxometalate anions having functional groups bonded to the silicon atoms serve as building blocks for the synthesis of silicone-polyoxometalate hybrid polymer systems, with potential applications as coatings, electronic or protonic conductors, electronic or optical storage devices and supported catalysts. If the silane modified polyoxometalate anions do not have functional groups bonded to the silicon, these materials still have various potential uses, for example, silane modified polyoxometalate anions containing R groups with long carbon chains will provide surfactant-like properties and therefore are useful to modify solvent properties. The following examples describe preferred embodiments of the present silane modified polyoxometalate anions, the properties of these materials and methods for preparing them. Preparation of Salts of Preferred Polyoxometalate Anions A. K 8 SiW 11 O 39 The salt of the polyoxometalate anion was prepared, either by the method of Teze et al., J. Inorg. Nucl. Chem (1977) 39 , 999 or by simple modifications thereto. Into a flask equipped with a stirrer, addition funnel and Claisen "Y" adapter, fitted with a condenser and thermometer, were charged 900 mL of deionized water, 546 g (1.66 moles) of sodium tungstate, Na 2 WO 4 *2H 2 0 and 33 g (0.155 moles) of sodium metasilicate, Na 2 SiO 3 *5H 2 O. The mixture was heated at 95°C. until the solids dissolved and then 585 mL (2.34 moles) of 4N aqueous hydrochloric acid were added over 3 hours. The heating was continued for another 15 minutes after all the HCl was added, and then the solution was filtered hot through a set of #5 and #3 Whatman filters in a nitrogen pressurized filter funnel. A first white precipitate weighing 0.059 g was collected. The clear first filtrate was transferred to a beaker, kept hot at 80°C. and 225 g (2.98 moles) of potassium chloride, KCl, were added. The solution was stirred for another 20 minutes during which time a second white precipitate formed. This second precipitate was filtered as described above, washed three times with 100 mL cold deionized water and dried for 24 hours at 110°C. to produce a powder giving a 65% yield of K 8 SiW 11 O 39 based on Na 2 WO 4 *H 2 O. As the second filtrate cooled, more of the second precipitate appeared. This additional second precipitate was gravity filtered through a #1 Whatman paper, transferred to a fritted glass Buchner funnel fitted with a 1.2 µm membrane filter, washed well with cold deionized water and dried to a constant weight, first for 24 hours at 115°C. and then for 28 hours at 125°C., giving a final yield of K 8 SiW 11 O 39 of 42.5 g or 81% based on Na 2 WO 4 *H 2 O. The product was identified by its infrared spectra and by the use of 29 Si nuclear magnetic resonance spectroscopy (NMR) and 183 W NMR. B. Na 7 PW 11 O 39 *nH 2 O This salt was prepared by the method of Brevard et al., J. A. Chem. Soc. (1983), 105 , 7059. An amount of 72.5 g (0.22 moles) of Na 2 WO 4 *2H 2 O and 2.87 of anhydrous Na 2 HPO 3 (0.02 moles) were dissolved in approximately 200 mL of deionized water. The solution was heated to 80-90°C. and titrated to pH 4.8 using 21.8 mL of concentrated HNO 3 . The volume of the solution was reduced to half and the polyoxometalate salt was separated in a dense lower layer by liquid-liquid extraction with 90 mL of acetone. The extraction was repeated two more times and only a small amount of lower layer was separated. The solid sodium salt was obtained as the hydrate by evaporating the acetone extract to dryness (approximately 10 days in air). The material was characterized by IR and NMR spectroscopy. Preparation of the Tetrabutylammonium Salt of Silane Modified Polyoxometalate Anions Unless otherwise specified, the reactions were conducted at ambient temperature and all yield percentages in the examples are by weight. The method to prepare silane modified polyoxometalate anions described by Judenstein, Chem. Mater. (1992) 4 ,4, has been used in the present invention, with some modifications. Example 1 In a flask equipped with a magnetic stirrer and containing 450 mL of acetonitrile, CH 3 CN, 15 g (5x10 -3 moles) of K 8 SiW 11 O 39 , dried overnight at 115 - 117°C., were added and allowed to stir for 2 hours. To that mixture, 0.73 g (9.2x10 -3 moles) of pyridine, C 5 H 5 N, was added. An amount of 1.20 g (9.3x10 -3 moles) of dimethyldichlorosilane, (CH 3 ) 2 SiCl 2 , dissolved in 17 g of CH 3 CN, was then added over a 16 minute period. An additional 6.7 mL of CH 3 CN, used to rinse the addition funnel, were added to the flask and the mixture stirred another 22 hours. A first precipitate consisting of unreacted K 8 SiW 11 O 39 and potassium chloride was separated by centrifuging and filtering through a 0.22 µm nylon membrane filter. To the clear first filtrate, 48.55 g (0.15 moles) of tetrabutylammonium bromide, (C 4 H 9 ) 4 NBr, were added and the mixture stirred for 15 minutes. A second precipitate formed and was separated as before. To the second filtrate, 450 mL of deionized water were added and a third precipitate formed. This third precipitate was isolated by centrifuging and decanting the liquid part, washing the precipitate twice with 100 mL portions of deionized water and air drying. Analysis by 29 Si NMR and 183 W NMR showed the third precipitate consisted of the mixed adduct [(C 4 H 9 ) 4 N] (8-2n) SiW 11 O 39 [(CH 3 ) 2 Si] n where n = 1 or 2. The mole ratio of K 8 SiW 11 O 39 to (CH 3 ) 2 SiCl 2 added initially was 1:1.84 and the mole ratio of isolated adduct n=1:n=2, estimated from 29 Si NMR data, was 1.6:1. Yield of the product was 7.99 g. This yield was estimated as 40% based on K 8 SiW 11 O 39 and the adduct ratio. Example 2 In a flask equipped with a stirrer and containing 450 mL of acetonitrile, CH 3 CN, 15 g (5x10 -3 moles) of K 8 SiW 11 O 39 , dried overnight at 115 - 117°C., were added and allowed to stir for 2 hours. An amount of 0.774 g (6x10 -3 moles) of (CH 3 ) 2 SiCl 2 dissolved in 10 g of CH 3 CN, was added to the flask and the mixture stirred another 40 hours. A first precipitate consisting of unreacted K 8 SiW 11 O 39 and potassium chloride was separated by centrifuging and filtering through a 0.22 µm nylon membrane filter. To the first clear filtrate, 48.35 g (0.15 moles) of tetrabutylammonium bromide, (C 4 H 9 ) 4 NBr, were added and the mixture stirred for 15 minutes. A second precipitate formed and was separated as before. To the second filtrate, 400 mL of deionized water were added and a third white precipitate formed. This third precipitate was recovered by centrifuging, decanting, filtering, washing several times with deionized water and drying under a nitrogen purge for 72 hours. Analysis by 29 Si NMR and 183 W NMR showed the third precipitate consisted of the mixed adduct [(C 4 H 9 ) 4 N] (8-2n) SiW 11 O 39 [(CH 3 ) 2 Si] n where n = 1 or 2. The mole ratio of K 8 SiW 11 O 39 to (CH 3 ) 2 SiCl 2 added initially was 1:1.20 and the mole ratio of isolated adduct n=1:n=2, estimated from 29 Si NMR data, was 2.3:1. Yield of the product was 10.17 g. This yield was estimated as 54% based on K 8 SiW 11 O 39 and the adduct ratio. Example 3 This preparation followed the same general procedure as in Example 2 except the amount of (CH 3 ) 2 SiCl 2 added was 1.2 g (9.3x10 -3 moles). Analysis by 29 Si NMR and 183 W NMR showed the third precipitate consisted of the mixed adduct[(C 4 H 9 ) 4 N] 8-2n SiW 11 O 39 [(CH 3 ) 2 Si] n where n = 1 or 2. The mole ratio of K 8 SiW 11 O 39 to (CH 3 ) 2 SiCl 2 added initially was 1:1.86 and the mole ratio of isolated adduct n=1:n=2, estimated from 29 Si NMR data, was 3.8/1. Yield of the product was 14.95 g. This yield was estimated as 73% based on K 8 SiW 11 O 39 and the adduct ratio. Example 4 This preparation followed the same general procedure as in Example 2 except the amount of (CH 3 ) 2 SiCl 2 added was 1.55 g (1.2x10 -2 moles). Analysis by 29 Si NMR and 183 W NMR showed the third precipitate consisted of the mixed adduct [(C 4 H 9 ) 4 N] (8-2n) SiW 11 O 39 [(CH 3 ) 2 Si] n where n = 1 or 2. The mole ratio of K 8 SiW 11 O 39 to (CH 3 ) 2 SiCl 2 added initially was 1:2.4 and the mole ratio of isolated adduct n=1:n=2, estimated from 29 Si NMR data, was 17.8:1. Yield of the product was 15.32 g. This yield was estimated as 74% based on K 8 SiW 11 O 39 and the adduct ratio. Example 5 In a flask equipped with a stirrer and containing 450 mL of acetonitrile, CH 3 CN, 15 g (5x10 -3 moles) of K 8 SiW 11 O 39 dried overnight at 115°C. was added and allowed to stir for 2 hours. An amount of 1.91 g (0.01 moles) of (CH 3 )C 6 H 5 SiCl 2 , dissolved in 1.5 g CH 3 CN, was added dropwise over one minute and the mixture stirred 22 hours. A first precipitate was separated by centrifuging and filtering through a 0.22 µm nylon membrane filter. To the first clear filtrate, 48.65 g (0.15 moles) of tetrabutylammonium bromide, (C 4 H 9 ) 4 NBr, were added and the mixture stirred for 15 minutes. A second precipitate formed and was separated as before. To the second filtrate, 500 mL of deionized water were added and a third precipitate formed. This third precipitate was recovered by centrifuging, decanting, filtering, washing several times with deionized water and drying under a nitrogen purge. Analysis by 29 Si NMR and 183 W NMR showed the third precipitate consisted of the mixed adduct [(C 4 H 9 ) 4 N] 8-2n Si*W 11 O 39 [(CH 3 )C 6 H 5 Si] n where n = 1 or 2 and with the Si* being a chiral center. Two monosubstituted stereoisomers were present and a disubstituted isomer was also found. The mole ratio of K 8 SiW 11 O 39 to (CH 3 )C 6 H 5 SiCl 2 added initially was 1:2. Yield of the product was 17.51 g. This yield was estimated as 82% based on K 8 SiW 11 O 39 . Example 6 In a flask equipped with a stirrer and containing 450 mL of CH 3 CN, 18.08 g (8.1x10 -3 moles) of K 8 SiW 11 O 39 dried for 24 hours at 115°C. were added and the milky suspension stirred for 2 hours. An amount of 1.72 g (0.0122 moles) of methylvinyldichlorosilane, ViCH 3 SiCl 2 , was added and allowed to stir for 23 hours. The mixture was centrifuged, a first precipitate isolated and the clear supernatant solution decanted to a clean flask. An amount of 58.22 g (0.181 moles) of tetrabutylammonium bromide was added to this first filtrate and the mixture stirred for 15 minutes. A second fluffy white precipitate formed and was isolated by filtering through a 0.22 µm nylon membrane. To the remaining clear, slightly yellow filtrate, 600 mL of deionized water were added and a third precipitate formed. This third precipitate was isolated by centrifuging and decanting the liquid part, washing the precipitate with deionized water and drying under nitrogen. Analysis by 29 Si NMR and 183 W NMR showed the third precipitate consisted of two isomers of the adduct [(C 4 H 9 ) 4 N] 6 Si*W 11 O 39 [CH 3 SiVi], with the Si* being a chiral center. The 183 W NMR spectrum was more helpful than the 29 Si NMR spectrum for determining the relative amounts of each isomer. A 22 line spectrum was obtained which corresponded to two sets of 11 equivalent lines. Based on the equivalent amounts of the two isomers present in the mixture, it was concluded that the preference was statistical. The mole ratio of K 8 SiW 11 O 39 to (CH 3 )ViSiCl 2 added initially was 1:1.5. Yield of the reaction product was 10.98 g. This yield was estimated as 43.2% based on K 8 SiW 11 O 39 . Example 7 In a flask equipped with a stirrer and containing 450 mL of acetonitrile, CH 3 CN, 15 g (5x10 -3 moles) of K 8 SiW 11 O 39 , dried overnight at 115°C., were added and allowed to stir for 2 hours. An amount of 1.88 g (0.01 moles) of (CH 3 )ViSi(O 2 CCH 3 ) 2 was added and the mixture stirred 24 hours. A considerable amount of K 8 SiW 11 O 39 remained undissolved, so 2.02 g (0.02 moles) of concentrated HCl were added dropwise into the mixture over a period of 4 minutes and the stirring was continued for another 20 hours. A first precipitate was separated by centrifuging and filtering through a 0.22 µm nylon membrane filter. To the first clear filtrate, 48.65 g (0.15 moles) of tetrabutylammonium bromide, (C 4 H 9 ) 4 NBr, were added and the mixture stirred for 15 minutes. A second precipitate formed and was separated as before and the weight of the dry powder was 6.05 g. To the second filtrate, 500 mL of deionized water were added and a third precipitate formed. This third precipitate was recovered by centrifuging, decanting, filtering, washing several times with deionized water and drying under a nitrogen purge. Final weight of the third precipitate was 12.86 g. Analysis by IR indicated that the second and third precipitates were identical. Analysis by 29 Si NMR and 183 W NMR showed the second and third precipitates consisted of two isomers of the adduct [(C 4 H 9 ) 4 N] 6 Si*W 11 O 39 [CH 3 SiVi], the Si* being a chiral center, the same compounds as described in Example 6. The mole ratio of K 8 SiW 11 O 39 to (CH 3 )ViSi(O 2 CCH 3 ) 2 added initially was 1:2. Yield of the product based on the second and third precipitates was 12.86 g. This yield was estimated as 92% based on K 8 SiW 11 O 39 . Example 8 In a flask equipped with a stirrer and containing 450 mL of acetonitrile, CH 3 CN, 15 g (5x10 -3 moles) of K 8 SiW 11 O 39 , dried overnight at 115°C., were added and allowed to stir for 2 hours. An amount of 2.48 g (0.01 moles) of dissolved in 3.98 g of CH 3 CN, were added to the mixture. An amount of 1.97 g (0.02 moles) of concentrated HCl were added dropwise into the mixture and the stirring continued for another 22 hours. A first precipitate was separated by centrifuging and decanting. To the first clear filtrate, 48.65 g (0.15 moles) of tetrabutylammonium bromide, (C 4 H 9 ) 4 NBr, were added and the mixture stirred for 15 minutes. A second precipitate formed and was separated by filtering through a 0.22 µm nylon membrane. To the second filtrate, 800 mL of deionized water were added and a third precipitate formed. This third precipitate was recovered by centrifuging, decanting, filtering, washing several times with deionized water and drying under a nitrogen purge. Analysis by 29 Si NMR and 183 W NMR showed the third precipitate consisted of two isomers of the adduct ,the Si* being a chiral center. Both the 183 W NMR and the 29 Si NMR data were very similar to that received in analyzing the hexenyl silane modified polyoxometalate described in Example 9. The mole ratio of K 8 SiW 11 O 39 to added initially was 1:2. Yield of the product based on the third precipitate was 16.18 g. This yield was estimated as 75% based on K 8 SiW 11 O 39 . Example 9 In a flask equipped with a stirrer and containing 450 mL of CH 3 CN, 15.0 g (5.0x10 -3 moles) of K 8 SiW 11 O 39 , dried for 24 hours at 115°C., were added and the milky suspension stirred for 2 hours. An amount of 1.98 g (0.01 moles) of 1-hexenylmethyldichlorosilane, CH 2 =CH(CH 2 ) 4 (CH 3 )SiCl 2 , was added and the solution stirred for an additional 21 hours. The mixture was centrifuged and a clear supernatant solution was separated from a first precipitate by decanting it to a clean flask. An amount of 48.35 g (0.146 moles) of tetrabutylammonium bromide was added to the supernatant solution and the mixture stirred for 15 minutes. A second fluffy white precipitate formed and was isolated by filtering through a 0.22 µm nylon membrane. To the remaining clear, slightly yellow filtrate, 500 mL of deionized water were added and a third precipitate formed. This third precipitate was isolated by centrifuging and decanting the liquid part, washing the precipitate three times with 170 mL of deionized water and drying under nitrogen. Analysis by 29 Si NMR and 183 W NMR showed the third precipitate consisted of two isomers of the adduct [(C 4 H 9 ) 4 N] 6 Si*W 11 O 39 [CH 3 Si(CH 2 ) 4 CH=CH 2 ], the Si* being a chiral center. The 183 W NMR spectrum was more helpful than the 29 Si NMR spectrum for determining the relative amounts of each isomer. A 22 line spectrum was obtained with relative intensities of 1:0.6. This suggests that the composition of the mixture is approximately 63:37; however, we were not able to determine which isomer corresponded to which set of resonances. The mole ratio of K 8 SiW 11 O 39 to CH 2 =CH(CH 2 ) 4 (CH 3 )SiCl 2 added initially was 1:2. Yield of the reaction product was 16.34 g. This yield was estimated as 76.5% based on K 8 SiW 11 O 39 . Example 10 In a flask equipped with a stirrer and containing 450 mL of CH 3 CN, 15.0 g (5.0x10 -3 moles) of Na 7 PW 11 O 39 , dried for 24 hours at 115°C. and ground in a mortar and pestle, were added and the milky suspension stirred for 2.5 hours. An amount of 2.08 g (0.01 moles) of 1-hexenylmethyl-dichlorosilane, CH 2 =CH(CH 2 ) 4 (CH 3 )SiCl 2 , dissolved in CH 3 CN, was added and the solution stirred for an additional 22 hours. The mixture was centrifuged and a slightly yellow supernatant solution was separated from a first precipitate by decanting it to a clean flask. An amount of 51.26 g (0.146 moles) of tetrabutylammonium bromide was added to the supernatant solution and the mixture stirred for 15 minutes. A second precipitate formed and was isolated by filtering through a 0.22 µm nylon membrane. To the remaining clear, slightly yellow filtrate, 500 mL of deionized water were added and a third precipitate formed. This third precipitate was isolated by centrifuging and decanting the liquid part, washing the precipitate three times with 170 mL of deionized water and drying under nitrogen. Analysis by 31 P NMR, 29 Si NMR and 183 W NMR showed the third precipitate consisted of two monosubstituted isomers of the type described in Example 9. The mole ratio of Na 7 PW 11 O 39 to CH 2 =CH(CH 2 ) 4 (CH 3 )SiCl 2 added initially was 1:2. Yield of the product was 15.88 g. This yield was estimated as 75% based on Na 7 PW 11 O 39 . Example 11 In a flask equipped with a stirrer and containing 450 mL of CH 3 CN, 15.0 g (5.0x10 -3 moles) of K 8 SiW 11 O 39 , dried for 24 hours at 115°C., were added and the milky suspension stirred for 2 hours. An amount of 3.58 g (0.01 moles) of CF 3 (CF 2 ) 3 CH 2 CH 2 (CH 3 )SiCl 2 , dissolved in 1.97 g of CH 3 CN, were added and the solution stirred for an additional 24 hours. The mixture was centrifuged and the supernatant solution was separated from a first precipitate by decanting it to a clean flask. An amount of 48.35 g (0.15 moles) of tetrabutylammonium bromide was added to the supernatant solution and the mixture stirred for 15 minutes. A second precipitate formed and was isolated by filtering through a 0.22 µm nylon membrane. To the remaining clear, slightly yellow filtrate, 500 mL of deionized water were added causing the product to precipitate slowly. This third precipitate was isolated by centrifuging and decanting the liquid part, washing the precipitate three times with 540 mL of deionized water and drying under nitrogen. Analysis by 29 Si NMR and 183 W NMR showed the third precipitate consisted of the mixed adduct [(C 4 H 9 ) 4 N] 8-2n Si*W 11 O 39 [CF 3 (CF 2 ) 3 CH 2 CH 2 (CH 3 )Si] n where n = 1 or 2 and the Si* being a chiral center. Two monosubstituted stereoisomers were present and two disubstituted isomers were also found. The mole ratio of K 8 SiW 11 O 39 to CF 3 (CF 2 ) 3 CH 2 CH 2 (CH 3 )SiCl 2 added initially was 1:2. Yield of the product was 18.76 g. This yield was estimated as 86.5% based on K 8 SiW 11 O 39 and the adduct ratio. The product was very soluble in CH 3 CN (60 weight percent), DMSO and (CH 3 ) 2 CO. Example 12 In a flask equipped with a stirrer and containing 450 mL of acetonitrile, CH 3 CN, 15 g (5x10 -3 moles) of K 8 SiW 11 O 39 , dried overnight at 115 to 117°C., were added and allowed to stir for 2 hours. An amount of 1.15 g (0.01 moles) of methylhydrogendichlorosilane, HCH 3 SiCI 2 , dissolved in 17 g of CH 3 CN, was then added over an 8 minute period. An additional 6 mL of CH 3 CN, used to rinse the addition funnel, were added to the flask and the mixture stirred another 21 hours. A first precipitate consisting of unreacted K 8 SiW 11 O 39 and potassium chloride was separated by centrifuging and filtering through a 0.22 µm nylon membrane filter. To the clear first filtrate, 48.35 g (0.15 moles) of tetrabutylammonium bromide, (C 4 H 9 ) 4 NBr, were added and the mixture stirred for 27 minutes. A second precipitate formed and was separated as before. To this second filtrate, 450 mL of deionized water were added and a third precipitate formed. This third precipitate was isolated by centrifuging and decanting the liquid part, washing the precipitate twice with 100 mL portions of deionized water and drying under nitrogen. Analysis by 29 Si NMR and 183 W NMR showed the third precipitate consisted of three isomers of the adduct [(C 4 H 9 ) 4 N] 4 Si*W 11 O 39 [CH 3 SiH] 2 , the Si* being a chiral center. In addition, it appears that a large portion of the Si-H of the silane starting material oxidized during the synthesis of the silane modified polyoxometalate and produced a material having the formula SiW 11 O 39 O[SiCH 3 ] 2 -4 . Approximately 50% of the product was an oxidized material and the isomers comprised the remaining 50%. The mole ratio of K 8 SiW 11 O 39 to (CH 3 )HSiCl 2 added initially was 1:2. Yield of the product was 2.85 g. This yield was estimated as 15% based on K 8 SiW 11 O 39 . Example 13 In a flask equipped with a stirrer and containing 450 mL of CH 3 CN, 15.0 g (5.0x10 -3 moles) of Na 7 PW 11 O 39 , dried for 24 hours at 115°C. and ground in a mortar and pestle, were added and the milky suspension stirred for 2 hours. An amount of 1.22 g (0.01 moles) of H(CH 3 )SiCl 2 , dissolved in CH 3 CN, were added and the solution stirred for an additional 20 hours. The mixture was centrifuged and a slightly yellow supernatant solution was separated from a first precipitate by decanting it to a clean flask. An amount of 51.26 g (0.146 moles) of tetrabutylammonium bromide was added to the supernatant solution and the mixture stirred for 15 minutes. A second precipitate formed and was isolated by filtering through a 0.22 µm nylon membrane. To the remaining clear, yellow filtrate, 500 mL of deionized water were added and a third precipitate formed. This third precipitate was isolated by centrifuging and decanting the liquid part, washing the precipitate with deionized water and drying under nitrogen. Analysis by 29 Si NMR and 183 W NMR showed the third precipitate consisted of entirely of an oxidized product. The mole ratio of Na 7 PW 11 O 39 to H(CH 3 )SiCl 2 added initially was 1:2. Yield of the product was 15.14 g. This yield was estimated as 80.9% based on Na 7 PW 11 O 39 . Example 14 In a flask equipped with a stirrer and containing 450 mL of acetonitrile, CH 3 CN, 14.65 g (5x10 -3 moles) of K 8 SiW 11 O 39 , dried overnight at 115 to 117°C., were added and allowed to stir for 2 hours. An amount of 1.26 g (0.01 moles) of ethylhydrogendichlorosilane, H(CH 3 CH 2 )SiCl 2 , dissolved in 1 g of CH 3 CN, was then added and the stirring continued for 23.5 hours. After centrifugation, a first precipitate was separated from the supernatant liquid by decanting. To the clear first filtrate, 48.65 g (0.146 moles) of tetrabutylammonium bromide, (C 4 H 9 ) 4 NBr, were added, a second precipitate was formed and was separated by filtering through a 0.22 µm nylon membrane and washing with approximately 10-15 mL of CH 3 CN. This second precipitate was dried under nitrogen and the yield was 17.79 g. To the second filtrate, 500 mL of deionized water were added and a very small amount of a third precipitate formed. This third precipitate was isolated by centrifuging and decanting the liquid part, washing with deionized water and drying under nitrogen. The weight of the dried, third precipitate was 0.79 g. IR analysis indicated that the second and third precipitates were identical. Analysis by 29 Si NMR and 183 W NMR of the second precipitate showed that it consisted of two isomers of the adduct [(C 4 H 9 ) 4 N] 4 Si*W 11 O 39 [CH 3 CH 2 SiH] 2 , the Si* being a chiral center. In addition, it appears that approximately 30% of the Si-H of the silane starting material oxidized during the synthesis of the silane modified polyoxometalate and produced a material having the formula SiW 11 O 39 O[SiCH 2 CH 3 ] 2 -4 . Based on the equivalent amounts of the two isomers present in the mixture, it was concluded that the preference was statistical. The mole ratio of K 8 SiW 11 O 39 to (CH 3 CH 2 )HSiCl 2 added initially was 1:2. Yield of the product was 17.79 g. This yield was estimated as 96.26% based on K 8 SiW 11 O 39 and assuming 100% pure adduct.

Claims: A silane modified polyoxometalate anion represented by the formula YZ(SiRR') n where Z is selected from the group consisting of M 11 O 39 -12 , M 9 0 34 -14 and M 17 O 61 -20 , where M is tungsten or molybdenum; Y is As +5 , Si +4 , B +3 , Ge +4 , P +5 or Fe +3 when Z is M 11 O 39 -12 ; Y is Si +4 , Ge +4 , or P +5 when Z is M 9 0 34 -14 and Y is As 2 +10 or P 2 +10 when Z is M 17 O 61 -20 ; R is a monovalent hydrocarbon radical having from 1 to 24 carbon atoms; halogenated hydrocarbon or carbon radicals, epoxy radicals, amino radicals, mercapto radicals and methacrylo radicals; R' is selected from a hydrogen atom, monovalent hydrocarbon radicals having from 1 to 24 carbon atoms, halogenated hydrocarbon or carbon radicals, epoxy radicals, amino radicals, mercapto radicals and methacrylo radicals; and n represents the number of (=SiRR') +2 groups bonding to the polyoxometalate anion and has a value from 1 to 3. The anion according to claim 1 and further comprising an associated cation selected from an alkali metal or tetralkylammonium. The anion according to claim 1 wherein R and R' are not identical. The anion according to claims 1 or 2, wherein Z is M 11 O 39 -12 where M is tungsten, Y is Si +4 and n has a value from 1 to 2. The anion according to claims 2 or 4, wherein R and R' are monovalent hydrocarbon radicals having from 1 to 10 carbon atoms, halogenated hydrocarbon or carbon radicals, epoxy radicals, amino radicals, mercapto radicals and methacrylo radicals; or R' is hydrogen atom. A method for preparing a silane modified polyoxometalate anion, the method comprising reacting a silane having a general formula RR'SiX 2 where R is selected from monovalent hydrocarbon radicals having from 1 to 24 carbon atoms, halogenated hydrocarbon or carbon radicals, epoxy radicals, amino radicals, mercapto radicals and methacrylo radicals; R' is selected from hydrogen atom, monovalent hydrocarbon radicals having from 1 to 24 carbon atoms, halogenated hydrocarbon or carbon radicals, epoxy radicals, amino radicals, mercapto radicals and methacrylo radicals; and X is a hydrolyzable group; with a polyoxometalate anion represented by the formula YZ where Z is selected from the group consisting of M 11 O 39 -12 , M 9 0 34 -14 and M 17 O 61 -20 , where M is tungsten or molybdenum; Y is As +5 , Si +4 , B +3 , Ge +4 , P +5 or Fe +3 when Z is M 11 O 39 -12 ; Y is Si +4 , Ge +4 , or P +5 when Z is M 9 0 34 -14 and Y is As 2 +10 or P 2 +10 when Z is M 17 O 61 -20 ; to form a silane modified polyoxometalate anion represented by the formula YZ(SiRR') n where M, R, R', Y, and Z are as defined above and n represents the number of (=SiRR') +2 groups bonding to the polyoxometalate anion and has a value from 1 to 3. The method according to claim 6 where a first cation associated with the silane modified polyoxometalate anion is exchanged in an additional step with a second cation selected from an alkali metal or tetralkyl ammonium. The method according to claim 6 wherein R and R' are not identical. The method according to claim 6 wherein X is selected from a halogen atom or an alkoxy radical having from 1 to 4 carbon atoms. The method according to claim 9 wherein Z is M 11 O 39 -12 , where M is tungsten, Y is Si +4 and n has a value from 1 to 2. The method according to claim 10 wherein R and R' are selected from monovalent hydrocarbon radicals having from 1 to 10 carbon atoms, halogenated hydrocarbon or carbon radicals, epoxy radicals, amino radicals, mercapto radicals and methacrylo radicals; or R' is hydrogen. The method according to claim 6 wherein between 0.5 and 3 moles of silane per mole of polyoxometalate anion are reacted in an organic solvent at a temperature from 0°C. to the boiling point of said solvent.

Inventors: KATSOULIS DIMITRIS ELIAS, KERYK JOHN ROBERT, KATSOULIS, DIMITRIS ELIAS, KERYK, JOHN ROBERT
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1995
Main classification: C07F11
IPC codes: C07F11, C07F7