Depolymerized natural rubber and process for preparation thereof

Abstract: A depolymerized natural rubber is disclosed, which is a liquid rubber having a number-average molecular weight of from 2,000 to 50,000 obtained by the depolymerization of a deproteinized natural rubber. A process for the preparation of a depolymerized natural rubber is also disclosed, which comprises dissolving a deproteinized natural rubber into an organic solvent so as to give a concentration of from 1 to 30 % by weight and then carrying out air oxidation of the resulting solution in the presence of a metallic catalyst. The depolymerized natural rubber can provide the same physical properties as ordinary vulcanized rubbers, exhibits no odor or color characteristic to natural rubbers and causes no immediate allergy induced by protein.

Description: The present invention relates to a depolymerized natural rubber useful as a raw material for adhesives, sealants, calking compounds, plasticizers or polyurethane and a process for the preparation thereof. A depolymerized natural rubber obtained by the depolymerization of a natural rubber is also called a liquid rubber. Because of its strong adhesivity and excellent crosslinking reactivity, the depolymerized natural rubber has found a wide application as a raw material for adhesives, sealants and calking compounds. It has also been used as a reactive plasticizer for improving the processing characteristics of solid rubbers such as compound rubber for tires. Further, as compared to the case where a solid rubber is used, the processing procedure to produce rubber products can be eased by using a liquid rubber, and thus it is advantageous in view of energy consumption. For these reasons, a liquid rubber have been drawing the attention in various industrial fields. However, since the prior art depolymerized natural rubber is made from a low purification natural rubber from which protein has not sufficiently been removed, it retains an odor characteristic to natural rubbers and causes coloration due to oxidation of protein, etc. Accordingly, the prior art depolymerized natural rubber is fatally disadvantageous in that it is hardly applied for an adhesive for familiar products such as household articles and nursing articles or observable articles such as an adhesive for a photographic album which needs to be colorless and transparent. Moreover, the prior art depolymerized natural rubber may cause immediate allergy induced by protein which has recently become a problem and thus cannot be applied to products which are used in contact with the human body. In general, a depolymerized natural rubber can be obtained by subjecting a natural rubber to mastication, pyrolysis, photodecomposition, chemical decomposition or the like treatment. However, these treatments have the following disadvantages. In the mastication process, a material rubber is subjected to processing by a roll mill or a closed mixer to break the rubber molecular chains by the mechanical and thermal action. During this process, a loosening agent such as a mercaptan is added to the rubber to prevent the recombination of the rubber molecules chain thus broken, thereby accelerating the reduction of the molecular weight of the rubber. The loosening agent is an organic compound which gives a plasticity to the rubber in a small amount, thereby reducing the mastication time; this is also referred to as "mastication accelerator". This process can provide a depolymerized rubber having a uniform number-average molecular weight. However, the distribution of molecules weight of the resulting depolymerized rubber is broad and the terminal structure of the resulting depolymerized rubber can hardly be controlled. The pyrolysis process is disadvantageous in that the reaction temperature is so high that not only decomposition but also crosslinking or recombination occurs, thus it is difficult to control the molecular weight distribution or the terminal structure. In the photodecomposition process, a molecular chain is broken by the energy of light such as ultraviolet rays. However, peroxides or the like at ketone ends produced by breaking the main chain act as a sensitizer whereby causing sequential decomposition, hence it makes difficult to control the terminal end, the molecular weight or its distribution. This process is also disadvantageous in that it facilitates isomerization reaction that transforms cis-1,4 structure into trans-1,4 structure. Known chemical decomposition processes include ozone degradation, oxidative degradation by an oxidizing agent such as hydrogen peroxide and phenylhydrazine, and oxidative degradation by a metallic ion catalyst. Ozone degradation should be effected at a low temperature. Further, since it is dangerous to use an ozone in a large amount as required in the degradation process, this process is used only as an analytical method and is not industrially valuable. Production of a depolymerized natural rubber by oxidative decomposition with hydrogen peroxide or phenylhydrazine has been industrialized. In this regard, "Polymer Digest", page 90, October (1981) discloses a molecular weight-reduced natural rubber latex. It is reported that this rubber latex is a product of the oxidative depolymerization of a natural rubber latex with hydrogen peroxide. However, this product is not sufficiently liquefied but rather it is a solid. Further, the ends of the molecular chain of this product are not substituted by functional groups. Similar examples can be seen in JP-A-58-152075 (The term "JP-A" as used herein means an "unexamined published Japanese patent application") wherein it is disclosed that a depolymerized natural rubber is obtained by adding hydrogen peroxide to a natural rubber latex, and then allowing the mixture to react while blowing oxygen thereinto, and which is a solid rubber having a break strength of 3.5 kg. On the other hand, "Rev. Gen. Caoutch Plast", vol. 61, No. 643, page 79 (1984) discloses a technique which comprises the depolymerization of a natural rubber latex with phenylhydrazine and air to obtain a depolymerized natural rubber having a molecular weight of from 3,000 to 20,000. As evident from "Makromol. Chem.", vol. 186, No. 12, page 2,441 (1985), such a depolymerized natural rubber is terminated by phenylhydrazine and thus exhibits no reactivity necessary for the extension of main chain. Further, it was reported in "Makromol. Chem. Rapid Commun.", vol 7, No. 3, page 159 (1986) that a liquid rubber having a molecular weight of 10,000 or less and a molecular weight distribution as narrow as 1.6 or 1.7 as calculated in terms of Mw/Mn has been produced by adding hydrogen peroxide and methanol or tetrahydrofuran to a toluene solution of a natural rubber and then irradiating the resulting mixture with ultraviolet rays. However, it was later reported in "Makromol. Chem.", vol. 189, No. 3, page 523 (1988) that a re-examination of the process has revealed that intramolecular epoxide group had been erroneously assumed as the terminal hydroxyl group. The present inventors' examination has also revealed that epoxidation and isomerization of main chain occurred in the depolymerization reaction by irradiation with ultraviolet rays under the same conditions as above. Further, it was found that no functional groups such as carbonyl group, carboxyl group and hydroxyl group was produced at the ends of the molecular chain. Moreover, the depolymerized natural rubber thus obtained had a molecular weight distribution as broad as 4 or more as calculated in terms of Mw/Mn (weight-average molecular weight/number-average molecular weight ratio), and the control thereof was difficult. If the foregoing depolymerized natural rubber which is not terminated by functional groups at its molecular ends is crosslinked with sulfur or peroxide, crosslinking reactions occur in the molecule rather than at the molecular ends, thereby providing a crosslinked rubber having many free-terminal chains. Since these free-terminal chains do not contribute to the physical properties or rubber elasticity of the crosslinked rubber but impair the dynamic properties of the crosslinked rubber, thus such a crosslinked rubber is not useful for the commercial products. In order to overcome these disadvantages, it is necessary to use a liquid rubber terminated by functional groups at both molecular ends and carry out crosslinking with the use of a hardening agent having a functionality of 3 or more or to use a liquid rubber containing functional groups at three positions, i.e., at the both molecular ends and at an intramolecular position, and carry out crosslinking with the use of a bifunctional hardening agent to form a three-dimensional network. In order to obtain a crosslinked rubber having a good rubber elasticity, it is preferred that its molecular weight distribution be as narrow as possible and its molecular chain be as flexible as possible, i.e., the depolymerized natural rubber maintain the original microstructure of the natural rubber as much as possible. This is because that a depolymerized natural rubber is to be applied for various uses on condition that it is able to exhibit physical properties equal to ordinal vulcanized rubbers by making it to have a three-dimensional network structure with the use of an appropriate hardening agent. GB-A-417 912 relates to the preparation of rubber derivatives by oxidation and there may be depolymerization and other chemical or physical change in the rubber. The oxidation of the rubber is performed in solution in the presence of a metallic oxidizing catalyst soluble in the rubber solvent or capable of being dispersed therein. The solvent is then evaporated. NL-A-66 07 905 describes the formation of a liquid rubber by thermally depolymerizing a synthetic isoprene rubber in a nitrogen atmosphere and then oxidizing with hydrogen peroxide or air for obtaining products containing bonded oxygen in an amount of 0.6 to 4.5 weight%. It is therefore an object of the present invention to provide a depolymerized natural rubber which provides the same physical properties as ordinary vulcanized rubbers, exhibits no odor or color characteristic to natural rubbers and causes no immediate allergy induced by protein and a process for the preparation thereof. It is another object of the present invention to provide a liquid depolymerized natural rubber containing functional groups at both ends thereof or at both ends thereof and in its molecule suitable for the production of a three-dimensional network structure with the use of an appropriate crosslinking agent (chain extender) and a process for the preparation thereof. The present inventors made extensive studies aiming at solving the foregoing problems. As a result, it was found that the use of a deproteinized and highly refined natural rubber as a raw material can prevent the production of odorous components or coloring due to the decomposition of proteins contained in natural rubber during the depolymerization reaction as well as the occurrence of complicated side reactions due to impurities. It was also found that the uniform contact of such a highly refined natural rubber with air in the presence of an appropriate catalyst enables an efficient depolymerization of a natural rubber main chain. Accordingly, it has attained to obtain a liquid depolymerized natural rubber which gives less odor, exhibits no color and causes no immediate allergy induced by protein. In addition, it has also attained to reduce side reactions such as epoxidation of main chain and isomerization, which cause the deterioration of rubber elasticity, to an extremely low level. Further, in favor of the reduction in the possibility of occurrence of complicated side reactions, it has attained to obtain a depolymerized natural rubber containing at its molecular ends a carbonyl group (>C=O) which can be modified to hydroxyl group or the like. A three-dimensional network structure can easily be formed by modifying the terminal carbonyl groups of the depolymerized natural rubber to hydroxyl groups and then carrying out crosslinking by a three functional crosslinking agent, though the carbonyl group itself can be used as a functional group. Moreover, it is attained to obtain a liquid depolymerized natural rubber having a narrow distribution of molecular weight. The depolymerized natural rubber according to the present invention is a liquid rubber having a number-average molecular weight of from 2,000 to 50,000 and a molecular weight distribution Mw/Mn (weight average molecular weight/number average molecular weight) of 3.0 or less, obtainable by the depolymerization of a deproteinized natural rubber having a nitrogen content of less than 0,02 % by weight. If the number-average molecular weight of the depolymerized natural rubber exceeds this range, the depolymerized natural rubber cannot become a liquid sufficiently. On the contrary, if the number-average molecular weight of the depolymerized natural rubber falls below this range, a uniform distribution of molecular weight can hardly be obtained, thus is not useful. The process for the preparation of a depolymerized natural rubber according to the present invention comprises dissolving a deproteinized natural rubber in an organic solvent so as to give a concentration of from 1 to 30 % by weight, based on the weight of the resulting solution, and then carrying out air oxidation of the resulting solution in the presence 0,05 to 5 % by weight of a metallic catalyst. In accordance with this process, depolymerization can efficiently proceed. The depolymerized natural rubber of the present invention contains one or less epoxy group produced by side reactions per one molecular chain and maintains the same high cis structure as in natural rubbers. Accordingly, rubber products obtained by crosslinking the depolymerized natural rubber of the present invention exhibit the physical properties equal to ordinary natural rubbers. The carbonyl group at the ends of the molecular chain produced by the depolymerization process according to the present invention easily undergoes aldol condensation, followed by water elimination reaction. Accordingly, the depolymerized natural rubber of the present invention comprises as a main component a telechelic liquid rubber wherein a C=C bond, one carbon atom of which is substituted by formyl group (-CHO) produced by the aldol condensation, is contained per one molecular chain and the both ends of the molecular chain are terminated by ketone groups. A series of reaction processes from the oxidative decomposition of natural rubber through the formation of a telechelic liquid rubber will be described hereinafter. In order to minimize the distribution of the molecular weight, it is preferred that the air oxidation of the deproteinized natural rubber is effected while vigorously shaking the solution so that the contact of the depolymerized natural rubber with air is increased. The deproteinized natural rubber to be used as a raw material in the present invention can be prepared in accordance with a process as disclosed, for example, in JP-A-6-56902 (corresponding to EP-A-0 584 597). This process comprises adding a protease to a latex such as field latex and ammonia-treated latex to decompose a protein, and then repeatedly washing the latex with a surfactant to purify it. The washing is preferably effected by centrifugal separation. The protease to be used for the deproteinization is not specifically limited. The protease may be one derived from bacteria, fungi or yeast. Among them, one derived from bacteria is preferred. In general, the decomposition by the protease may be carried out by adding the protease to a natural rubber latex in an amount of from 0.01 to 10 % by weight and then allowing the resulting mixture to stand, or stirring, it for from several minutes to one week. The proteolysis treatment by protease is effected at a temperature of preferably from 5 to 90°C, more preferably from 20 to 60°C. The foregoing surfactant may be added to the system during or after the proteolysis treatment. The surfactant may be an anionic surfactant and/or a nonionic surfactant. Examples of the anionic surfactant include carboxylic acid surfactants, sulfonic acid surfactants, sulfuric ester surfactants, and phosphoric ester surfactants. Examples of the nonionic surfactant include polyoxyalkylene ether surfactants, polyoxyalkylene ester surfactants, polyhydric alcohol aliphatic ester surfactants, sugar fatty acid ester surfactants, and alkyl polyglycoside surfactants. The surfactant is preferably added in an amount from 0.001 to 10 % by weight based on the amount of the natural rubber latex. The deproteinized natural rubber obtained by the foregoing purification has at least a nitrogen content of less than 0.02 % by weight, i.e., being substantially free from any protein. In the deproteinized natural rubber having a nitrogen content of the range specified above, not only water-soluble proteins but also proteins bonded to natural rubber molecules have been decomposed and removed away by protease. It is also preferred that the deproteinized natural rubber is deproteinized to such a level that a raw rubber film prepared therefrom exhibits no absorption at a wavelength of 3,280 cm -1 in the infrared absorption spectrum, which is characteristic to polypeptides. The protein content in a natural rubber has normally been represented by 6.3 times the nitrogen content (N %) determined by Kjeldahl method. In the case of a fresh natural rubber latex (field latex), it is normally from about 3 to 5 % by weight (about 0.5 to 0.8 % by weight as N %) based on the solid content. In the case of a commercially available purified latex and raw rubber (smoked sheet rubber), it is about 2 % by weight or more (about 0.3 % by weight as N %). It has been revealed that, in the case of highly purified natural rubbers, the protein content thereof cannot be accurately estimated based on the nitrogen content thereof. This is because of the fact that there are proteins that bond to rubber molecules and, even when these proteins have been hydrolyzed, amino acid residues or short chain peptide molecules remain bonding to the rubber molecules. In general, it is known that a natural rubber is a mixture of a high molecular component having a molecular weight of from 1,000,000 to 2,500,000 and a low molecular component having a molecular weight of from 100,000 to 200,000. It is assumed that the low molecular components are bound with each other via abnormal groups contained in the natural rubber and branched, thereby forming the high molecular components. When an amino acid molecule (i.e., a nitrogen atom of an atomic weight of 14) is bound to one molecule of a low molecular weight rubber molecule of a molecular weight of 100,000 which has been seemingly formed by the inherent biosynthesis, the nitrogen content becomes 0.014 %. It is therefore considered that the nitrogen content corresponding to this amount is not eliminated but remains. Accordingly, it is understood that even a natural rubber from which proteins have completely been eliminated has a residual nitrogen content of less than 0.02 %. In order to confirm the removal of protein more accurately, an analytical method by the infrared absorption spectrum is preferred. Based on the measurement of the infrared spectra of natural rubbers from which proteins have been eliminated at various levels with the use of a Fourier transform infrared spectrometer and comparison of the results thereof with the infrared absorption spectra of peptides reported by Nakamura et al. (as disclosed in Biopolymers, 26, 795), it has been clarified that after eliminating proteins, an absorption at 3280 cm -1 assignable to polypeptides disappears, though an absorption at 3315 to 3320 cm -1 assignable to the group of >N-H in short-chain peptides or amino acids binding to rubber molecules remains. In the present invention, a metallic catalyst is used to accelerate the air oxidation of the deproteinized natural rubber. Preferred examples of metal species of the catalyst include cobalt, copper and iron. These metal species may be used in the form of chloride or salt or complex with an organic compound. Among them, cobalt catalysts such as cobalt chloride, cobalt acetyl acetonate and cobalt naphthenate are preferred. The organic solvent to be used in the present invention may be any organic solvent so long as it does not react with the rubber, is hardly oxidized and dissolves the rubber therein. For example, various hydrocarbon solvents, aromatic hydrocarbon solvents and organic halogen solvents. may preferably be used. Examples of the hydrocarbon solvent include hexane, and gasoline. Examples of the aromatic hydrocarbon solvent include toluene, xylene, and benzene. Examples of the organic halogen solvent include chloroform, and dichloromethane. Among them, aromatic hydrocarbon solvents such as toluene is preferred. These organic solvents may be used in admixture with an alcohol. The deproteinized natural rubber is dissolved into an organic solvent so as to give a concentration of from 1 to 30 % by weight, preferably from 1 to 10 % by weight, more preferably from 2 to 5 % by weight, based on the weight of the resulting solution, and the resulting solution is subjected to oxidation reaction. If the concentration of the deproteinized natural rubber falls below the range specified above, it is economically disadvantageous. On the contrary, if the concentration of the deproteinized natural rubber exceeds the range specified above, the viscosity becomes too high, which makes difficult to bring the deproteinized natural rubber into uniform contact with air. The metallic oxidation catalyst may be used by dissolving or dispersing into the solution of the deproteinized natural rubber. The addition amount of the metallic oxidation catalyst is from 0.05 to 5 % by weight, preferably from 0.1 to 1 % by weight, based on the weight of the deproteinized natural rubber. If the addition amount of the metallic oxidation catalyst falls below the range specified above, the rate of air oxidation is too low, thus not practical. On the contrary, if the addition amount of the metallic oxidation catalyst exceeds the range specified above, it causes another difficulties such as the difficulty of the catalyst removal after the reaction. The oxidation reaction is preferably carried out in such a manner that the solution is brought into uniform contact with air. The method for bring the solution into uniform contact with air is not specifically limited. For example, it may easily be accomplished by shaking the solution in a shaking flask. The air oxidation is normally effected at a temperature of from room temperature to 100 °C. However, the reaction, temperature is not specifically limited. The reaction is normally completed within 1 to 3 hours. After the reaction, the reaction product is separated from the reaction solution for purification. Since the metallic oxidation catalyst remains in the reaction solution even after the reaction, it is preferred that the reaction solution is poured into an alcohol (e.g., methanol) solution containing an acid (e.g., hydrochloric acid) in a large excess amount against the metallic ions, whereby only the rubber content is precipitated and thus purified. The present invention will be further described in the following examples. EXAMPLES 1-11 To 50 mℓ of a 2 % (W/V) toluene solution of a deproteinized natural rubber which has a nitrogen content of 0.01 % and wherein a film obtained therefrom exhibits no absorption at a wavelength of 3,280 cm -1 in the infrared absorption spectrum was added a metallic oxidation catalyst specified in Table 1 in an amount (% by weight) specified in Table 1. The resulting mixture was charged into a 300-mℓ shaking flask, and then shaken in a shaking constant-temperature water bath at 65°C at a shaking amplitude of 2 cm and a shaking frequency of 135 times/min. for a predetermined period of time. The reaction product was then poured into a cool methanol containing hydrochloric acid in a 10-times amount of the metallic ion to separate the rubber content therefrom. The rubber content thus separated was then dissolved in toluene and the resulting toluene solution was poured into a cool hydrochlorically-acidified methanol for reprecipitating and purifying the rubber content. Thus a depolymerized natural rubber was obtained. COMPARATIVE EXAMPLE 1 To 50 mℓ of a 2 % (W/V) toluene solution of the same deproteinized natural rubber as used in Examples 1 to 11 was added 10 mg (1% by weight based on the rubber content) of cobalt acetylacetonate. The mixture was charged into a 200-mℓ round flask installed in a constant-temperature water bath at 65°C. The mixture was then allowed to react while minute air bubbles were being blown thereinto at a rate of 1 ℓ/min. through a porous glass nozzle located in the mixture for a period of time specified in Table 1. The reaction product was then subjected to purification in the same manner as in Example 1 to obtain a depolymerized natural rubber. COMPARATIVE EXAMPLE 2 To 50 mℓ of a 2 % (W/V) toluene solution of a commercially available pale crepe having a nitrogen content of 0.38 % was added 10 mg (1 % by weight based on the rubber content) of cobalt acetylacetonate. The mixture was charged into a 300-mℓ shaking flask and then shaken in a shaking constant-temperature water bath at 65°C at a shaking amplitude of 2 cm and a shaking frequency of 135 times/min. for a predetermined period of time. The reaction product was then poured into a cool methanol containing hydrochloric acid in a 10-times amount of the metallic ion to separate the rubber content. The rubber content thus separated was then dissolved in toluene and the resulting toluene solution was poured into a cool hydrochlorically-acidified methanol for reprecipitating and purifying the rubber content. Thus a depolymerized natural rubber was obtained. COMPARATIVE EXAMPLE 3 A depolymerized natural rubber was prepared in the same manner as in Comparative Example 2 except that a commercially available deproteinized natural rubber having a nitrogen content of 0.07 % was used instead of the pale crepe. COMPARATIVE EXAMPLE 4 To 200 mℓ of a 5 % (W/V) toluene solution of the same deproteinized natural rubber as used in Examples 1 to 11 were added 50 mℓ of methanol and 10 mℓ of a 30 % aqueous hydrogen peroxide. The volumetric ratio of toluene/methanol/aqueous hydrogen peroxide was 20/5/1. The mixture was then irradiated with ultraviolet rays from a 100-W high voltage mercury vapor lamp. The reaction was effected at 10°C, which was controlled by passing cool water of 10°C through a cooling jacket. The reaction product was then subjected to purification in the same manner as in the Examples to obtain a depolymerized natural rubber. EVALUATION TEST The depolymerized natural rubbers thus obtained were visually observed for form. Further, these depolymerized natural rubbers were measured for [η], Mn, Mw and Mw/Mn. The results are set forth in Table 1. All the depolymerized natural rubbers obtained in the Examples were almost colorless and odorless liquid rubbers having a nitrogen content of 0.01 % or less. On the contrary, neither Comparative Example 2 nor Comparative Example 3 gave a liquid rubber. Comparative Example 4 gave a liquid rubber. However, C 13 NMR analysis of the product showed that cis-1,4 chain units constituting the main chain had been isomerized to trans-1,4 structure in a proportion of 1 per 290 units and had been epoxidized in a proportion of 1 per 40 units. It was made clear from C 13 NMR analysis that the liquid rubbers of the present invention obtained in the Examples had cis-1,4-chain units epoxidized in a proportion of 1 per about 80 units, approximately half that of Comparative Example 4. These liquid rubbers had a number-average molecular weight Mn of 6,600 as determined by gel permeation chromatography (GPC) and thus were pentanonacontamers. It can thus be judged that these liquid rubbers each contain epoxy groups in a proportion of about 1 per one molecular chain. As a result of C 13 NMR of these liquid rubbers, no isomerization had been found in the isoprene chain, demonstrating that a high cis structure characteristic of natural rubbers had been maintained. The examples of the present invention were essentially different from the Comparative Examples for the following points of view. Namely, the depolymerized natural rubbers obtained in the Examples of the present invention were confirmed to contain formyl group bonded to one carbon in C=C bond in the molecular chain. This means that the air oxidation has caused the main chain to be decomposed to a carbonyl group at one end and a formyl group at the other but the formyl group has then been re-bonded to the main chain due to aldol condensation reaction. From the fact that no formyl group has been found at the ends of the product and the amount of the aldol-condensed group is 1 per molecular chain of liquid rubber, it can be judged that the reaction product according to the present invention mainly composed of a telechelic liquid rubber terminated by ketone at both ends thereof. Under the conditions where the rubber solution is vigorously shaken so as to bring the rubber solution into uniform contact with air, liquid rubbers having a molecular weight distribution as narrow as 3 or less as calculated in terms of Mw/Mn, which have not been attained in the prior art technique, had attained. The molecular weight distribution of the rubber of Comparative Example 1 was higher than that of the present invention. As mentioned above, the depolymerized natural rubber of the present invention is free of odor or color characteristic to natural rubbers and causes no immediate allergy induced by protein. Thus, the depolymerized natural rubber of the present invention is suitably applied for articles used closely to the human body such as an adhesive and for transparent products. Further, the depolymerized natural rubber of the present invention contains about one epoxy group per one molecular chain and its isoprene chain maintains a high cis structure which is the same as in natural rubbers. Thus, the depolymerized natural rubber of the present invention can be provided with the same physical properties as ordinary vulcanized rubbers. Moreover, the depolymerized natural rubber of the present invention comprises as a main component a telechelic liquid rubber containing a C=C bond, one carbon atom of which is substituted by formyl group, produced by aldol condensation, per one molecular chain, and the both ends of the molecular chain are terminated by ketone groups. Thus, the depolymerized natural rubber of the present invention can be formed into a three-dimensional network structure with the use of an appropriate crosslinking agent (chain extender). In accordance with the process for the preparation of a depolymerized natural rubber according to the present invention, a deproteinized natural rubber is dissolved in an organic solvent and then carrying out air oxidation in the presence of a metallic catalyst, whereby making it possible to easily and efficiently prepare a depolymerized natural rubber having excellent physical properties as mentioned above.

Claims: A depolymerized natural rubber, which is a liquid rubber having a number-average molecular weight of from 2,000 to 50,000 and a molecular weight distribution Mw/Mn (= weight average molecular weight/number average molecular weight) of 3.0 or less, obtainable by the depolymerization of a deproteinized natural rubber having a nitrogen content of less than 0.02 % by weight. The depolymerized natural rubber of claim 1 which contains not more than one epoxy group per molecular chain and maintains a high cis structure characteristic to a natural rubber. The depolymerized natural rubber of claim 1 or 2 which comprises a telechelic liquid rubber wherein a C=C bond, one carbon atom of which is substituted by formyl group (-CHO) produced by aldol condensation, is contained per one molecular chain and the both ends of the molecular chain are terminated by ketone groups. A process for the preparation of a depolymerized natural rubber, as defined in any one of the claims 1 to 3, which comprises dissolving a deproteinized natural rubber in an organic solvent so as to give a concentration of from 1 to 30 % by weight and then carrying out air oxidation of the resulting solution in the presence of 0.05 to 5 % by weight of a metallic catalyst. The process of claim 4 wherein said organic solvent is an aromatic hydrocarbon. The process of any one of the claims 4 and 5, wherein said metallic catalyst is a cobalt catalyst. The process of any one of the claims 4 to 6, wherein said air oxidation is carried out by shaking said solution of the deproteinized natural rubber.

Inventors: HAYASHI MASAHARU, KANAMARU EIJI, KAWASAKI ATSUKO, SAKAKI TOSHIAKI, SHIBATA KAZUHIKO, TANAKA YASUYUKI, HAYASHI, MASAHARU, KANAMARU, EIJI, KAWASAKI, ATSUKO, SAKAKI, TOSHIAKI, SHIBATA, KAZUHIKO, TANAKA, YASUYUKI, Hayashi, Masaharu, c/o Kao Corporation, Kanamaru, Eiji, c/o Fuji Latex Co., Ltd., Shibata, Kazuhiko, c/o Nitto Denko Corporation
Applicants: FUJI LATEX CO, KAO CORP, NITTO DENKO CORP, SUMITOMO RUBBER IND, FUJI LATEX CO., LTD, KAO CORPORATION, NITTO DENKO CORPORATION, SUMITOMO RUBBER INDUSTRIES LTD.
Application year: 1995
Main classification: C08C19
IPC codes: C08C19, C08F8, C08C1