Antiferroelectric liquid crystal composition

Abstract: An antiferroelectric liquid crystal composition having a chiralsmectic C A * phase composed by blending liquid crystal composition-constituting compounds having the same direction of inclination of optic axis produced by application of an electric field and/or comprised of a mixture of two enantiomers of a liquid crystal material; one having the stereosense (+) and the other having the stereosense (-). The stereosense is defined so that, when the molecule is viewed so that the bond between the core group and the asymmetric carbon is behind the asymmetric carbon atom, the stereosense is (+) if the remaining three groups (or atoms) are arranged clockwise in order of length of the groups (or, if the groups are the same length, in order of their volume), and the stereosense is (-) if the groups are arranged counter clockwise.

Description: 1. Field of the Invention This invention relates to a liquid crystal composition having an ability to indicate an antiferroelectric phase (chiralsmectic C A phase, hereinafter abbreviated to "SmC A * phase"). Further, this invention relates to a liquid crystal indication element comprising said antiferroelectric liquid crystal composition. 2. Description of the Related Art Recently, liquid crystal displays have become widely used as indication elements, due to their thin thickness, light weight, low electricity consumption etc. However, most of these displays use TN (Twisted Nematic) type displays comprising a nematic liquid crystal. Since the driving of the indication method of the TN type is based on the anisotropy of the dielectric constant of the liquid crystal, the speed of response is slow, and an improvement is required. In contrast, liquid crystal devices comprising the chiralsmectic C phase (hereinafter abbreviated as "SmC* phase") liquid crystal, which is ferroelectric and was discovered by Meyer et. al., has a high speed response and memory characteristics which are not attained by nematic liquid crystals. Thus, the application of ferroelectric liquid crystals to a ferroelectric liquid crystal display is being vigorously researched. However, the good orientation and memory characteristics required for this indication method are difficult to realize in a real cell. For example, the cell has the problems that it is not resistant to external shocks etc., and many problems must be solved. On the other hand, recently, an antiferroelectric phase (hereinafter abbreviated as "SmC A * phase") has been discovered which shows three stable states on the lower temperature side of said SmC* phase, by Chandani et. al. This antiferroelectric liquid crystal shows a thermodynamically stable phase wherein dipoles are arranged in antiparallel in every adjacent layer, and exhibits an electric field-induced phase transition between the antiferroelectric phase and the ferroelectric phase which is characterized by a clear threshold value and double hysteresis characteristics in response to an applied voltage. Research on a new indication method utilizing this switching behavior has already begun. EP-A-0 525 737 describes an antiferroelectric crystal composition comprising two kind of compounds to provide an antiferroelectric liquid crystal composition having improved temperature-dependency of the threshold electric field in the transition between SC A * phase and SC* phase, or provide a light-switching element having improved temperature characteristics of the driving threshold electric field. However, this document does not disclose guiding principles of how to select liquid crystal composition components in order to provide a liquid crystal composition having a quick response speed between an antiferroelectric phase and a ferroelectric phase, or provide a liquid crystal composition having a large VM (hereinafter defined). EP-A-0 582 519 discloses a liquid crystal composition having antiferroelectric phases at two temperature ranges and comprising liquid cystal-composition-constituting compounds of the same kind as in the present invention. LIQUID CRYSTALS, vol. 6, no. 2, 1989 LONDON, GB, pages 167-174, discloses that specific measures need to be taken in order to obtain a composition having a higher amount of R- or S- enantiomers. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a view showing states of inclinations of liquid crystal molecules when voltages are applied and not applied to a ferroelectric liquid crystal material. Fig. 2 is a graph showing the voltage-transmittance characteristics of a liquid crystal indication element. Fig. 3 is a view illustrating the stereoscopic sense of the liquid crystal of this invention. SUMMARY OF THE INVENTION The indication element of the liquid crystal composition having the SmC A * phase exhibits an antiferroelectric phase (AF) when an electric field is not applied, and exhibits a ferroelectric phase (F) when an electric field is applied, and presents a dark and bright state, respectively, as shown in Fig. 1. The response speed between the states [τr (AF - F), τd (F - AF)] is desired to be sufficiently high to obtain a good indication quality. In order to drive the liquid crystal element utilizing the double hysteresis characteristics in the voltage-transmittance characteristics of the indication element shown in Fig. 2, provided that the voltage which shows the transmittance of 10% is V1 and V4, and the voltage which shows the transmittance of 90% is V2 and V3 as shown in Fig. 2, it is required that (1) each of the threshold voltages is low, and that (2) the voltage width presented by V1 - V3 is wide, the voltage width presented by V2 - V1 is narrow, and the VM [= (V1 - V3)/(V2 - V1)] defined by the ratio of the above voltage widths is larger than 2. However, a guiding principle for accomplishing this is not clear. An object of this invention is to provide such guiding principle, to improve the liquid crystal characteristics. The inventors of this invention targeted the direction of inclination of an optic axis (tilt sense) of a liquid crystal composition-constituting compound (hereinafter referred to as "liquid crystal material" or "material") produced when an electric field is applied and the compound has made a transition to the ferroelectric phase, and have found that a high response speed liquid crystal composition is obtained by blending materials which have the same direction. That is to say, the antiferroelectric liquid crystal material cancel polarization components between adjacent layers and does not produce a spontaneous polarization, and the optic axis does not deviate from the layer normal direction. However, when a voltage is applied to the liquid crystal, the given outside electric field components interact, and the liquid crystal material transfers to the ferroelectric phase and the optic axis inclines. After detailed examination of the inclination directions of axes of several hundreds of materials, the present inventors have found that there is a material species that, when viewed from above, so that the bottom surface is defined to be at the standard voltage, inclines clockwise when a positive voltage is applied and counter clockwise when a negative voltage is applied (tilt sense +), and another material species that inclines counter clockwise when a positive voltage is applied and clockwise when a negative voltage is applied (tilt sense -). The main aspect of this invention relates to hysteresis characteristics. Accordingly the invention is directed to an antiferroelectric liquid crystal composition having a chiralsmectic C A * phase comprised of a mixture of two enantiomers; one having the stereosense (+) and the other having the stereosense (-); in which composition VM (Voltage Margin) [= (V1 - V3) (V2 - V1)] is larger than 2, V1 being the voltage which shows a transmittance of 10% and V2, V3 being the voltage which shows a transmittance of 90% in the double hysteresis characteristics in the voltage-transmittance characteristics of the antiferroelectric liquid crystal composition. The stereosense is defined so that, when the molecule is viewed so that the bond between the core group and the asymmetric carbon is behind the asymmetric carbon atom, the stereosense is (+) if the remaining three groups (or atoms) are arranged clockwise in order of length of the groups (or, if the groups are of the same length, in order of their volume), and the stereosense is (-) if the groups are arranged counter clockwise. The above "core" is an atomic group which is comprised of at least two cyclic groups, e.g. aromatic rings, heterocycles and cyclohexane rings which may have substituent(s), and combination groups connected to the cyclic rings e.g. -COO-, -O- and -CO- . In a specific embodiment of the above composition the proportion of the compound having the stereosense (+) is 1 to 99% and the proportion of the compound having the stereosense (-) is 1 to 99%. The present inventors focused on the peculiarity of the three dimensional configuration around the asymmetric carbon in the liquid crystal material and found that in order to achieve the above object, it is effective to select materials having different stereosenses and mix them, to form a composition. The above peculiarity of the three dimensional configuration does not mean the R and S enantiomers usually referred to in relation to the asymmetric carbon, but means two configurations with the same molecular formula, relating to the three atoms or three atomic groups other than the core connected to the asymmetric carbon of the liquid crystal material in the order of length (when two or more of the atoms or atomic groups have the same length, in the order of the volume of the atoms or atomic groups). The differences in configuration are considered to affect the spatial orientation of the liquid crystals at the time of mixing liquid crystal materials. As shown in Fig. 3, when the core is positioned in the opposite side, the case where the configuration of the remaining three substituents are in clockwise order has been defined as +, and the case where the configuration of the remaining three substituents are in counter clockwise order has been defined as -, which has been designated as stereosense. The inventors have found that in contrast to mixing of liquid crystal materials having the same stereosense, mixing of liquid crystal materials having different stereosense generally causes a decrease of the threshold voltage and an increase of VM due to a decrease of V3. The reason for this is thought to be that, by mixing liquid crystal materials having different stereosenses, a change occurs in the interactions among liquid crystal materials, so that, in comparison with the ferroelectric phase, the antiferroelectric phase becomes unstable. According to this feature, VM is made at least 2. In a preferred embodiment the present liquid crystal composition is further characterized by comprising liquid crystal composition-constituting compounds having the same direction of inclination of optic axis (hereinafter the direction of inclination of the optic axis will be referred to as "tilt sense") produced by application of an electric field and wherein the proportion of the liquid crystal composition-constituting compound having the same tilt sense is not less than 70 wt%. In a further preferred embodiment the present liquid crystal composition has a saturation value of spontaneous polarization of not less than 200 nC/cm 2 . Examples of a compound having a tilt sense (+) include hydrocarbon system chiral side chain materials and fluorohydrocarbon system chiral side chain materials, having an absolute configuration of S modification, more concretely S enantiomers of the compounds having the following chemical constitution formulae 1 to 15. In the above formulae 1 to 15, n is the integer 4, 5, 6, 7, 8, 9, 10, 11, 12, 13 or 14, and m is the integer 2, 3, 4, 5, 6,7, 8, 9, 10, 11, 12, 13 or 14. Preferably, n is an integer from 5 to 12, and m is an integer from 4 to 12. Examples of the compound having tilt sense (-) include hydrocarbon system chiral side chain materials and fluorohydrocarbon system chiral side chain materials, having an absolute configuration of R modification, more concretely R modification of the compounds having the above chemical constitution formulae 1 to 15. Examples of the compound having stereosense (+) include fluorohydrocarbon system chiral side chain materials having an R absolute configuration and hydrocarbon system chiral side chain materials having an S absolute configuration, more concretely R configuration of the compounds having the following chemical formulae 16 to 25 and S modification of the compounds having the following chemical formulae 26 to 30. In these formulae 16 to 30, n is the integer 4, 5, 6, 7, 8, 9, 10, 11, 12, 13 or 14, and m is the integer 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13 or 14, provided that in formula 30, m is the integer 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13 or 14. Examples of compounds having stereosense (-) include S enantiomers of the compounds represented by the above formulae 16 to 25 and R enantiomers of the compounds represented by the above constitutional formulae 26 to 30. Using compounds No. 1 to 6 shown in Table 1, liquid crystal compositions shown in the examples shown below were prepared. The liquid crystal compositions were injected into liquid crystal cells having gaps of 2 µm. After the injection, the cell was heated to a temperature at which the liquid crystal became an isotropic liquid, and thereafter cooled to room temperature at a rate of 2°C/min, to obtain an antiferroelectric liquid crystal element. The response speed was determined by applying a rectangular wave of 50V. The hysteresis characteristics were determined by measuring an intensity variance of the transmitted light under a crossed Nicols by applying a chopping wave of 50V-1 Hz to the cell. Example 1 (Reference Example) From the compounds shown in Table 1, compound Nos. 1, 2 and 5 were selected and used to prepare composition Nos. I and II as shown in Table 2. In composition No. I, the components were selected so that the tilt senses of all compounds were the same (-). On the other hand, in composition No. II, some of the compounds was selected to have different tilt senses from the others, to prepare a material with a blend of tilt senses. The results of response speed of the compositions are also shown in the Table 2. Composition No. I, wherein the tilt senses are the same, exhibited superior response characteristics for τr and τd (both measured at 40°C). Incidentally, the tilt sense reverses in a compound having the same chemical constitution by changing the absolute configuration. Composition No. Compound No. Blend Ratio (wt%) Absolute Configuration Tilt Sense τr (µs) τd (µs) Ps (nC/cm 2 ) I 2 16 R - 5 68 R - 26 105 220 1 16 R - II 2 16 R - 5 68 R - 126 208 170 1 16 S + Example 2 From the compounds shown in Table 1, compound Nos. 2, 3, 4, 5 and 6 were selected and used to prepare composition Nos. VIII and IX as shown in Table 3. In composition No. IX , the components were selected so that the tilt senses of all compounds was the same (-). On the other hand, in composition No. VIII,the compound No. 2 was selected so that it consisted of materials, with different stereosenses, to prepare a material with a mixture of stereosenses. The results (determined at 30°C) of the threshold voltage and VM of the compositions are also shown in the Table3 . The composition No. VIII exhibited a low threshold voltage and a sufficiently large VM. Incidentally, the stereosense reverses in a compound having the same chemical constitution by changing the absolute configuration. Composition No. Compound No. Blend Ratio (wt%) Absolute Configuration Stereo-Sense V1 V2 V3 V4 VM VIII 2 10 S - 3 6 R + 4 4 R + 33 39 10 2 3.8 5 53 R + 6 27 R + IX 2 10 R + 3 6 R + 4 4 R + 33 42 17 3 1.8 5 53 R + 6 27 R + Example 3 From the compounds shown in Table 1, compound Nos. 1, 2 and 5 were selected and used to prepare composition Nos. I and II as shown in Table 4, in the same manner as in Example 1. The blend ratios were the same as in Example 1. In composition No. I, the components were selected so that the tilt senses of all compounds were the same (-) and some of the materials had opposite stereosenses from the others to form a blended material with a mixture of stereosenses. Composition No. I apparently shows a good response speed (ref. Example 1), hysteresis characteristics (threshold value (determined at 40°C) and VM, ref. Table 4 shown below). Composition No. Compound No. Blend Ratio (wt%) Absolute Configuration Stereo-Sense V1 V2 V3 V4 VM I 2 16 R + 5 68 R + 25 31 11 3 2.3 1 16 R - II 2 16 R + 5 68 R + 35 47 25 3 0.8 1 16 S + The liquid crystal composition according to this invention exhibits excellent hysteresis characteristics (low threshold value and high driving margin) and in some cases also high speed response characteristics, so that it can be used to manufacture a practically excellent liquid crystal element.

Claims: An antiferroelectric liquid crystal composition having a chiralsmectic C A * phase comprised of a mixture of two enantiomers of a liquid crystal material; one having the stereosense (+) and the other having the stereosense (-), the stereosense being defined so that, when the molecule is viewed so that the bond between the core group and the asymmetric carbon is behind the asymmetric carbon atom, the stereosense is (+) if the remaining three groups (or atoms) are arranged clockwise in order of length of the groups (or, if the groups are of the same length, in order of their volume), and the stereosense is (-) if the groups are arranged counter clockwise, the said core group being an atomic group which is comprised of at least two cyclic groups including aromatic rings, heterocycles and cyclohexane rings which may have substituent(s), and combination groups connected to the cyclic rings including -COO-, -O- and -CO-; in which composition the voltage margin VM [= (V1 - V3)/(V2 - V1)] is larger than 2, V1 being the voltage which shows a transmittance of 10% and V2, V3 being the voltage which shows a transmittance of 90% in the double hysteresis characteristics in the voltage-transmittance characteristics of the antiferroelectric liquid crystal composition. The composition according to claim 1, wherein the proportion of the compound having the stereosense (+) is 1 to 99 wt% and the proportion of the compound having the stereosense (-) is 1 to 99 wt%. The composition according to claim 1 or 2, wherein the compound having the stereosense (+) is selected from the R enantiomers of the following constitutional formulae No. 16 to 25 and S modifications of the following formulae No. 26 to 30, and the compound having the stereosense (-) is selected from the S enantiomers of the following formulae No. 16 to 25 and R modifications of the following formulae No. 26 to 30, wherein n is an integer selected from 4 to 14 and m is an integer selected from 2 to 14, provided that in formula 30, m is an integer selected from 3 to 14: The antiferroelectric liquid crystal composition according to claim 1, characterized by comprising liquid crystal composition-constituting compounds having the same direction of inclination of optic axis (hereinafter the direction of inclination of the optic axis will be referred to as "tilt sense") produced by application of an electric field and wherein the proportion of the liquid crystal composition-constituting compound having the same tilt sense is not less than 70 wt%. The antiferroelectric liquid crystal composition according to claim 1, wherein the composition has a saturation value of spontaneous polarization of not less than 200 nC/cm 2 . A liquid crystal indication element comprising the liquid crystal composition according to any of claims 1 to 5.

Inventors: HAYASHI HITOSHI, KIKUCHI KATSUHIDE, TAKEUCHI AKIRA, TAKIGAWA KENJI, HAYASHI, HITOSHI, KIKUCHI, KATSUHIDE, TAKEUCHI, AKIRA, TAKIGAWA, KENJI
Applicants: NIPPON SOKEN, NIPPON SOKEN, INC.
Application year: 1995
Main classification: C09K19
IPC codes: C09K19