Photoconductive imaging members containing metallophthalocyanine dimers

Abstract: Photoconductive imaging members comprised of an alkoxy-bridged metallophthalocyanine dimer as a charge generator material, wherein said dimer is of the formula C₃₂H₁₆N₈MOROMN₈H₁₆C₃₂ wherein M is a trivalent metal, and R is an alkyl group or an alkyl ether group.

Description: This invention is generally directed to photoconductive imaging members containing metallophthalocyanine dimers. The use of certain phthalocyanine pigments, such as metal free phthalocyanine, vanadyl phthalocyanine, titanyl phthalocyanine, chloroindium phthalocyanines, and others as photogenerator materials in photoresponsive devices is known. Layered photoresponsive imaging members have been described in a number of U.S. Patents, such as US-A-4,265,900, wherein there is illustrated an imaging member comprised of a photogenerating layer, and an aryl amine hole transport layer. Examples of photogenerating layer components include trigonal selenium, metal phthalocyanines, vanadyl phthalocyanines, and metal free phthalocyanines. Complex electrophotograhic properties, such as photosensitivity, dark decay, cyclic stability and environmental stability of photoconductive members, or electrophotographic photoreceptors, are, for example, dependent on the purity of the photogenerating pigment, dopant components and amounts, morphology, crystal defects, the photogenerating pigment selected, and analytical differences in the pigments. The differences in the electrophotographical properties of a pigment, often a particular polymorph, are usually traced to the processes by which the pigment was obtained. To obtain a phthalocyanine based electrophotographic photoreceptor having high sensitivity to near infrared light, it is believed necessary to control the synthesis and purification procedures in order to obtain a material with the desired purity, as well as to prepare the pigment in the correct crystal modification. GB-A-2,255,980 describes an electrophotoconductive photoreceptor comprising a hydroxy gallium phthalocyanine monomer as a charge generator material. DE-A-3,242,712 describes an electrophotoconductive photoreceptor comprising a polymeric or monomeric oxy-bridged metallophthalocyanine. It is an object of the present invention to provide photoconductive imaging members containing metallophthalocyanine dimers. According to the present invention there is provided A photoconductive imaging member comprised of a photogenerator layer comprising a charge generator material of the formula C 32 H 16 N 8 MOROMN 8 H 16 C 32 : wherein M is a trivalent metal and R is selected from the group consisting of an alkylene group; an alkylene-oxy-alkylene group ; a -[(CH 2 ) m -O-(CH 2 ) m ] r - group wherein r is a number from 1 to 4, and m is a number from 2 to 4; and a -[CH(CH 3 )CH 2 -O-CH 2 (CH 3 )CH] s - group wherein s is a number from 1 to 3. In embodiments, the bridged metallophthalocyanine dimers can be selected as photogenerator pigments in layered photoconductive imaging members. These photoconductive imaging members may contain separate charge transport layers, such as hole transport layers. The photoconductive imaging members with separate hole transport layers may contain hole transport molecules such as tertiary aryl amines, or hole transporting polymers. The aforementioned photoconductive imaging members can be negatively charged when the photogenerating layer is situated between the hole transport layer and the substrate, or positively charged when the hole transport layer is situated between the photogenerating layer and the supporting substrate. The layered photoconductive imaging members can be selected for a number of different known imaging and printing processes including, for example, electrophotographic imaging processes, especially xerographic imaging and other printing processes wherein negatively charged or positively charged images are rendered visible with toner compositions of the appropriate charge. The imaging members herein are sensitive in the wavelength regions of from about 500 to about 900 nanometers, therefore, diode lasers can be selected as the light source, especially diode lasers which emit light in the region of from 650 to 850 nanometers. The dimers can be prepared as illustrated in US-A-5,521,306, and which dimers are illustrated in US-A-5,466,796. The bridged metallophthalocyanine dimers of the present invention are considered novel phthalocyanine dimers (or diphthalocyanines), which have a bridge (-O-R-O-) linking the two metal atoms of the metallophthalocyanine rings. The structure between the two oxygen molecules of the bridge is determined by the diol used in the synthesis. The trivalent metal in the phthalocyanine dimer structure can be aluminum, gallium or indium, or trivalent transitional metals, such as Mn(III), Fe(III), Co(III), Ni(III), Cr(III), and the like. Photoconductive imaging members containing bridged metallophthalocyanine dimers of the present invention possess in embodiments excellent cycling properties when compared, for example, to Type V hydroxygallium phthalocyanine prepared from chlorogallium phthalocyanine. The bridged metallophthalocyanine dimers herein can be obtained by the reaction of ortho-phthalodinitrile or 1,3-diiminoisoindoline with a trivalent metal alkoxide in the presence of a diol. During the aforementioned reaction, the diol, which can also act as a solvent for the reaction, is chemically incorporated into the phthalocyanine product with the formation of a bridged metallophthalocyanine dimer of the formula C 32 H 16 N 8 MOROMN 8 H 16 C 32 as illustrated in Formula 1, wherein M is a trivalent metal and the bridge (O-R-O) contains the diol moiety (R). The bridged metallophthalocyanine dimers can also be obtained by the reaction of ortho-phthalodinitrile or 1,3-diiminoisoindoline with other complexes of trivalent metals, such as the acetates and acetylacetonates, in the presence of a diol. Alternatively, the bridged metallophthalocyanine dimers can be prepared by the reaction of hydroxy metallophthalocyanines of a trivalent metal,with a diol in the presence of excess diol or another solvent. Processes for the preparation of the dimers are described in US-A-5,466,796 and US-A-5,493,016. US-A-5,466,796 discloses bridged metallophthalocyanine dimers of the formula C 32 H 16 N 8 MOROMN 8 H 16 C 32 , or of the formula wherein M is a metal, and R is an alkyl or an alkyl ether; US-A-5,521,306 discloses a process for the preparation of Type V hydroxygallium phthalocyanine which comprises the in situ formation of a bridged gallium phthalocyanine dimer, hydrolyzing said bridged gallium phthalocyanine dimer to hydroxygallium phthalocyanine, and subsequently converting the hydroxygallium phthalocyanine product obtained to Type V hydroxygallium phthalocyanine; a process for the preparation of Type V hydroxygallium phthalocyanine which comprises the formation of a bridged gallium phthalocyanine dimer by the reaction of an organic gallium complex with ortho-phthalodinitrile or 1,3-diiminoisoindoline and a diol; and US-A-5,493,016 discloses a process for the preparation of bridged metallophthalocyanine dimers by the reaction of a trivalent metal compound with ortho-phthalodinitrile or 1,3-diiminoisoindoline in the presence of a diol. The invention enables the provision of layered photoconductive imaging members containing bridged metallophthalocyanine dimers with near infrared photosensitivity. The present invention enables the provision of photoconductive imaging members with a photogenerator layer comprised of bridged metallophthalocyanine dimers. In one embodiment of the present invention there are provided photoconductive imaging members with an aryl amine hole transport layer, and a photogenerator layer comprised of bridged metallophthalocyanine dimers. In one embodiment of the present invention are provided photoconductive imaging members containing bridged metallophthalocyanine dimers of the formula C 32 H 16 N 8 MOROMN 8 H 16 C 32 , where the metal M is a trivalent metal such as aluminum, gallium, indium, or other metals in a trivalent form such as Fe(III), Cr(III), Co(III), Mn(III), Ni(III), or V(III); and R is an alkyl group or an alkyl ether. In another embodiment of the present invention to provide photoconductive imaging members containing bridged metallophthalocyanine dimers of the formula C 32 H 16 N 8 MOROMN 8 H 16 C 32 , where R is a moiety provided by the diol used in the preparation of the phthalocyanine dimer. In a further embodiment of the present invention there are provided photoconductive imaging members containing bridged gallium phthalocyanine dimers of the formula C 32 H 16 N 8 GaOROGaN 8 H 16 C 32 , where R is a moiety provided by the diol used in the preparation of the phthalocyanine dimer. It is another embodiment of the present invention to provide photoconductive imaging members containing bridged gallium phthalocyanine dimers of the formula C 32 H 16 N 8 GaOCH 2 CH 2 OGaN 8 H 16 C 32 , C 32 H 16 N 8 GaOCH(CH 3 )CH 2 OGaN 8 H 16 C 32 and C 32 H 16 N 8 GaOCH 2 CH 2 CH 2 OGaN 8 H 16 C 32 . Numerous different photoconductive imaging members can be provided with bridged metallophthalocyanine dimers, and specifically with alkoxy-bridged gallium phthalocyanine dimers. The photogenerating bridged galliumphthalocyanine dimers of the general formula as illustrated in Formula 3. with, for example, from 2 to about 10, and preferably about 2 to 6 carbon atoms in the alkoxy-bridge (O-R-O), and wherein M is a trivalent metal and R is an alkyl group or alkyl ether group, and which dimers can be obtained by the processes illustrated in US-A-5,466,796, US-A-5,521,306 and US-A-5,493,016, which dimers are selected as the photogenerating pigment for the photoconductive imaging members of the present invention. In embodiments of the present invention there are provided processes for the preparation of bridged gallium phthalocyanine dimers by the reaction of a gallium alkoxide with ortho-phthalodinitrile or 1,3-diiminoisoindoline and a selected diol. In further embodiments of the present invention, there are provided methods for the preparation of bridged gallium phthalocyanine dimers by the reaction of gallium acetate or gallium acetylacetonate with ortho-phthalodinitrile or 1,3-diiminoisoindoline, and a diol. The bridged gallium phthalocyanine dimer formed is of the the general formula C 32 H 16 N 8 MaOROMaN 8 H 16 C 32 with, for example, from 2 to about 10, and preferably about 2 to 6 carbon atoms in the alkoxy bridge (O-R-O). In preferred embodiments, gallium alkoxide can be prepared by reacting a gallium trihalide, especially the trichloride, with an alkali metal alkoxide, and thereafter reacting the resulting gallium alkoxide with, for example, ortho-phthalodinitrile or 1,3-diiminoisoindoline, and a dialcohol (diol) to form the alkoxy-bridged gallium phthalocyanine dimers. The diol may also serve as a reaction solvent, or an organic solvent may also be used, such as N-methylpyrrolidone; halonaphthalenes like 1-chloronaphthalene; quinoline, and the like. In preferred embodiments, the gallium alkoxide can be prepared by reacting gallium trichloride with a sodium alkoxide, such as methoxide or ethoxide, and thereafter reacting the resulting gallium alkoxide with, for example, ortho-phthalodinitrile or 1,3-diiminoisoindoline, and a dialcohol (diol) to form the alkoxy-bridged gallium phthalocyanine dimers. In another preferred embodiment, the gallium alkoxide can be prepared by reacting gallium trichloride with sodium methoxide, and thereafter reacting the resulting gallium methoxide with ortho-phthalodinitrile and 1,2-ethanediol (ethylene glycol) to form the bridged gallium phthalocyanine dimer with the formula C 32 H 16 N 8 GaOCH 2 CH 2 OGaN 8 H 16 C 32 , reference Formula 4. In another embodiment, the process of the present invention comprises the reaction of a metal trihalide like gallium trichloride with an alcohol like methanol, ethanol or butanol, and a base, such as ammonia, and subsequently reacting the resulting gallium alkoxide with, for example, ortho-phthalodinitrile or 1,3-diiminoisoindoline in the presence of a dialcohol (diol), which may also serve as a reaction solvent, to form the alkoxy-bridged gallium phthalocyanine dimers. Specific embodiments comprise initially preparing the trivalent metal alkoxide as indicated herein, which may then be separated from the byproduct or used in situ, followed by reaction of the metal alkoxide with ortho-phthalodinitrile or 1,3-diiminoisoindoline in a dialcohol (diol) solvent, to form the alkoxy-bridged metallophthalocyanine dimer. During the aforementioned reaction, some of the dialcohol solvent is chemically incorporated into the dimer product as a bridging unit between two metallophthalocyanine units. The resulting bridged metallophthalocyanine dimers, such as bridged gallium phthalocyanine dimers, can be selected for utilization in layered photoconductive imaging members, including those that possess infrared photosensitivity, for example from about 600 to about 900 nanometers, and wherein the dimer is selected as the photogenerating pigment. Alternatively, the bridged metallophthalocyanine dimer can be converted to the corresponding hydroxy metallophthalocyanine, which phthalocyanines may be selected as the photogenerating pigment. In embodiments, a trivalent metal alkoxide can be obtained from the reaction of the corresponding metal trihalide with an alkali metal salt of an alcohol, such as sodium ethoxide. The formed trivalent metal alkoxide can be separated from the alkali metal halide byproduct by filtration, or the mixture may be utilized in situ in the subsequent reaction to form the alkoxy-bridged metallophthalocyanine dimer. The trivalent metal alkoxide can also be obtained from the reaction of the corresponding metal trihalide with an alcohol in the presence of a base, such as ammonia. The formed trivalent metal alkoxide can be separated from the ammonium halide byproduct by filtration, or the mixture may be utilized in situ in the subsequent reaction to form the bridged metallophthalocyanine dimers. The trivalent metal alkoxide can thus be obtained from the reaction of the corresponding metal trihalide with an alkali metal alkoxide, such as sodium ethoxide. The alkali halide byproduct formed can be separated from the reaction mixture by filtration, or the mixture may be utilized as is (in situ) in the subsequent reaction to form the alkoxy-bridged metallophthalocyanine dimers. In embodiments, the gallium alkoxide can be prepared by reacting a gallium trihalide, especially the trichloride, and sodium methoxide, and thereafter reacting the resulting gallium methoxide with, for example, ortho-phthalodinitrile or 1,3-diiminoisoindoline in the presence of a dialcohol (diol), which may also serve as a reaction solvent to form the bridged gallium phthalocyanine dimer. A number of photoconductive imaging members with the novel bridged metallophthalocyanine dimer pigments illustrated herein can be fabricated. In embodiments, the layered photoresponsive imaging members are comprised of a supporting substrate, a charge transport layer, especially an aryl amine based hole transport layer, or a hole transporting aryl amine polycondensation polymer, and situated therebetween a photogenerator layer comprised of the alkoxy-bridged metallophthalocyanine dimer photogenerating pigment. Another embodiment of the present invention is directed to positively charged layered photoresponsive imaging members comprised of a supporting substrate, a charge transport layer, especially an aryl amine hole transport layer, and a top overcoating layer containing a bridged metallophthalocyanine dimer. Moreover, there is provided in accordance with the present invention a negatively charged photoresponsive imaging member comprised of a supporting substrate, a thin adhesive layer, a photogenerating layer containing bridged metallophthalocyanine dimer, such as an alkoxy-bridged gallium phthalocyanine dimer photogenerator dispersed in a polymeric resinous binder, such as a poly(vinyl butyral), a polycarbonate, or a styrene-vinylpyridine block copolymer, and as a top layer, aryl amine hole transporting molecules dispersed in a polymeric resinous binder such as polycarbonate, or a hole transporting aryl amine polycondensation polymer. Examples of specific dimer photogenerating pigments include 1,2-di(oxoaluminum phthalocyaninyl) ethane, 1,2-di(oxogallium phthalocyaninyl) ethane, 1,2-di(oxoindium phthalocyaninyl) ethane, 1,3-di(oxoaluminum phthalocyaninyl) propane, 1,3-di(oxogallium phthalocyaninyl) propane, 1,3-di(oxoindium phthalocyaninyl) propane, 1,2-di(oxoaluminum phthalocyaninyl) propane, 1,2-di(oxogallium phthalocyaninyl) propane, and 1,2-di(oxoindium phthalocyaninyl) propane. The photoconductive imaging members of the present invention can be prepared by a number of known methods, the type of coating process, the coating process parameters and the order of coating of the layers being dependent on the member desired. The photogenerating and charge transport layers of the imaging members can be coated as solutions or dispersions onto selective substrates by the use of a spray coater, dip coater, extrusion coater, roller coater, wire-bar coater, slot coater, doctor blade coater, gravure coater, and the like, and dried at from 40 to about 200°C for from 10 minutes to several hours under stationary conditions or in an air flow. The coating is accomplished to provide a final coating thickness of from 0.01 to about 30 µm (microns) after it has dried. The fabrication conditions for a given layer can be tailored to achieve optimum performance and cost in the final device. Imaging members of the present invention are useful in various electrostatographic imaging and printing systems, particularly those conventionally known as xerographic processes. Specifically, the imaging members of the present invention are useful in xerographic imaging and printing processes wherein the alkoxy-bridged metallophthalocyanine dimer absorbs light of a wavelength of from about 500 to about 900 nanometers, and preferably from about 650 to about 850 nanometers. In these known processes, electrostatic latent images are initially formed on the imaging member followed by development, and thereafter transferring the image to a suitable substrate. Substrate layers selected for the imaging members of the present invention can be opaque or substantially transparent, and may comprise any suitable material having the requisite mechanical properties. Thus, the substrate may comprise a layer of insulating material including inorganic or organic polymeric materials, such as MYLAR® a commercially available polyester, MYLAR® containing titanium, a layer of an organic or inorganic material having a semiconductive surface layer, such as indium tin oxide, or aluminum arranged thereon, or a conductive material inclusive of aluminum, chromium, nickel, brass or the like. The substrate may be flexible, seamless, or rigid and many have a number of many different configurations, such as for example a plate, a cylindrical drum, a scroll, an endless flexible belt and the like. In embodiments, the substrate is in the form of a seamless flexible belt. In some situations, it may be desirable to coat on the back of the substrate, particularly when the substrate is a flexible organic polymeric material, an anticurl layer, such as for example polycarbonate materials commercially available such as MAKROLON®. The photoconductive imaging member may optionally contain a charge blocking layer situated between the conductive substrate and the photogenerating layer. This layer may comprise metal oxides, such as aluminum oxide and the like, or materials such as silanes, or polymers such as polyesters. The primary purpose of this layer is to prevent charge injection from the substrate during and after charging. The charge blocking layer may be from about 0.01 to 0.2 µm (micron) thick and preferably from 0.02 to 0.08 µm (micron) thick. Intermediate adhesive layers between the substrate and subsequently applied layers may be desirable to improve adhesion. Typical adhesive layers include film forming polymers such as polyester, polyvinylbutyral, polyvinylpyrrolidone, polycarbonate, polyurethane, polymethyl methacrylate, and the like, and mixtures thereof. Since the surface of the substrate can be a metal oxide layer or an adhesive layer, the expression "substrate" as employed herein is intended to include in embodiments a metal oxide layer with or without an adhesive layer on a metal oxide layer. The adhesive layer may be from about 0.01 to 0.2 µm (micron) thick and preferably from 0.02 to 0.08 µm (micron) in thickness. In addition, the photoconductive imaging member may also optionally contain an adhesive interface layer situated between the hole blocking layer and the photogenerating layer. This layer may comprise a polymeric material such as polyester, polyvinyl butyral, polyvinyl pyrrolidone, and the like. The adhesive interface layer may be from about 0.01 to 0.2 µm (micron) thick and preferably from 0.02 to 0.08 µm (micron) in thickness. The photogenerator layer is preferably comprised of the alkoxy-bridged phthalocyanine dimer especially the gallium dimer dispersed in polymer binders. Generally, the thickness of the photogenerator layer depends on a number of factors, including the thicknesses of the other layers and the amount of photogenerator material contained in this layer. Accordingly, this layer can be of a thickness of from about 0.05 µm (micron) to about 10 µm (microns) when the bridged metallophthalocyanine dimer photogenerator is present in an amount of from about 5 percent to about 100 percent by volume. In embodiments, this layer is of a thickness of 0.01 to about 30, and preferably from about 0.10 µm (micron) to about 1 µm (micron)when the photogenerator composition is present in this layer in an amount of 30 to 75 percent by volume. The maximum thickness of this layer in an embodiment is dependent primarily upon factors, such as photosensitivity, electrical properties and mechanical considerations. The photogenerator layer can be fabricated by coating a dispersion of the alkoxy-bridged metallophthalocyanine dimer in a suitable solvent with or without an optional polymer binder material. The dispersion can be prepared by mixing and/or milling the bridged metallophthalocyanine dimer in equipment such as paint shakers, ball mills, sand mills and attritors. Common grinding media such as glass beads, steel balls or ceramic beads may be used in this equipment. The binder which can be present in an amount of from about 5 to 80 percent may be selected from a number of known polymers or resins suitable for this purpose such as poly(vinyl butyral), poly(vinyl carbazole), polyesters, polycarbonates, poly(vinyl chloride), polyacrylates and the like. In embodiments of the present invention, it is desirable to select a coating solvent that does not disturb or adversely affect the other previously coated layers of the device. Examples of components that can be selected for use as coating solvents for the photogenerator layer are ketones, alcohols, aromatic hydrocarbons, halogenated aliphatic or aromatic hydrocarbons, ethers, amines, amides, esters, and the like. Specific solvent examples are cyclohexanone, acetone, methyl ethyl ketone, methanol, ethanol, butanol, amyl alcohol, toluene, xylene, chlorobenzene, carbon tetrachloride, chloroform, methylene chloride, trichloroethylene, tetrahydrofuran, dioxane, dimethylformamide, dimethylacetamide, butyl acetate, ethyl acetate and methoxyethyl acetate, and the like. The coating of the photogenerator layer in embodiments of the present invention can be accomplished with spray, dip or wire-bar methods such that the final dry thickness of the photogenerator layer is from 0.01 to 30 µm (microns) and preferably from 0.1 to 15 µm (microns) after being dried at 40 to 150°C for 5 to 90 minutes. Illustrative examples of polymeric binder materials that can be selected for the photogenerator pigment are as illustrated herein and include those polymers as disclosed in U.S. Patent 3,121,006, the disclosure of which is totally incorporated herein by reference. The binder resin may be selected from a wide number of polymers such as polyesters, poly(vinyl butyral), poly(vinyl carbazole), polycarbonates, poly(vinyl chloride), polyacrylates and methacrylates, phenoxy resins, polyurethanes, poly(vinyl alcohol), polyacrylonitrile, polystyrene, copolymers and block copolymers of selected monomers such as styrene and vinylpyridine, and the like. The solvents used to dissolve these binders depend upon the particular resin. The charge transport layer is generally a nonphotoconductive material which supports the injection of photogenerated holes from the generator layer. The hole transporting layer is generally of a thickness of from about 5 µm (microns) to about 75 µm (microns), and preferably of a thickness of from about 10 µm (microns) to about 40 µm (microns). The charge transport layer may be a material comprising a hole transporting small molecule such as an aryl amine in an inactive, highly insulating and transparent polymer binder. Aryl amines selected for the hole transporting layer include molecules of the following formula wherein X is an alkyl group or a halogen, especially those substituents selected from the group consisting of Cl and CH 3 . Examples of specific aryl amines are N,N'-diphenyl-N,N'-bis(alkylphenyl)-1,1-biphenyl-4,4'-diamine wherein alkyl is selected from the group consisting of methyl, ethyl, propyl, butyl, hexyl, and the like; and N,N'-diphenyl-N,N'-bis(halophenyl)-1,1'-biphenyl-4,4'-diamine wherein the halo substituent is preferably a chloro substituent. Other known charge transport layer molecules can be selected, reference for example U.S. Patents 4,921,773 and 4,464,450, the disclosures of which are totally incorporated herein by reference. Charge transporting polymers, such as aryl amine polycondensation polymers described in U.S. Patents 4,806,443 and 5,028,687, the disclosures of which are totally incorporated herein by reference, can also be selected. Examples of the highly insulating and transparent polymer binder material for the transport layers include materials such as those described in U.S. Patent 3,121,006, the disclosure of which is totally incorporated herein by reference. Specific examples of polymer binder materials include polycarbonates, acrylate polymers, vinyl polymers, cellulose polymers, polyesters, polysiloxanes, polyamides, polyurethanes and epoxies, as well as block, random or alternating copolymers thereof. Preferred electrically inactive binders are comprised of polycarbonate resins having a molecular weight of from about 20,000 to about 100,000 with a molecular weight of from about 50,000 to about 100,000 being particularly preferred. Generally, the transport layer contains from about 10 to about 75 percent by weight of the charge transport material, and preferably from about 35 percent to about 50 percent of this material. Also, included within the scope of the present invention are methods of imaging and printing with the photoconductive devices illustrated herein. These methods generally involve the formation of an electrostatic latent image on the imaging member, followed by developing the image with a toner composition, reference U.S. Patents 4,560,635; 4,298,697 and 4,338,390, the disclosures of which are totally incorporated herein by reference, subsequently transferring the image to a suitable substrate, and permanently affixing the image thereto. In those environments wherein the device is to be used in a printing mode, the imaging method involves the same steps with the exception that the exposure step can be accomplished with a laser device or image bar. The xerographic electrical properties of the imaging members can be determined by known means, including as indicated herein electrostatically charging the surfaces thereof with a corona discharge source until the surface potentials, as measured by a capacitively coupled probe attached to an electrometer, attains an initial value V 0 of about -800 volts. After resting for 0.5 second in the dark, the charged members attain a surface potential of V ddp , dark development potential. Each imaging member is then exposed to light from a filtered Xenon lamp with a XBO 150 watt bulb, thereby inducing a photodischarge which results in a reduction of surface potential to a V bg value, background potential. The desired wavelength and energy of the exposed light can be determined by the type of filters placed in front of the lamp. The monochromatic light photosensitivity is determined by using a narrow band-pass filter. The dark decay in volts per second was calculated as (V 0 -V ddp )/0.5. The photosensitivity of the imaging members is provided in terms of the amount of exposure energy in ergs/cm 2 , designated as E 1/2 , required to achieve 50 percent photodischarge from the dark development potential. E 800-100V , which is the amount of exposure energy causing reduction of the V ddp from 800 volts to 100 volts, was also determined. The higher the photosensitivity is indicated by the smaller the E 1/2 and E 800-100V values. Cyclic stability is determined by performing cycling tests. Devices were charged with a corotron to about -800 volts. They were exposed with 775 nanometers of light with an intensity of about 7 ergs/cm 2 and erased with white light of about 60 ergs/cm 2 . The dark development (V ddp ) and background (V bg ) potentials were measured and recorded while the testing was performed for 10,000 cycles. After the cycling test had been completed, the devices remained in the dark for about 20 hours. After charging the device to about -800 volts with a corotron, they were exposed with 775 nanometers of light with an intensity of 3 ergs/cm 2 and erased with white light of about 200 ergs/cm 2 . The dark development and background potentials were measured and recorded while the testing was performed for 5,000 cycles. The significantly higher erase light intensity, used in this second test compared to the standard test, accelerates the cycledown (decrease in the dark development potential) in the photogenerator material and is thus considered a stress test. The smaller values of the voltage loss of both the dark development (V ddp ) and background (V bg ) potentials represent the better cyclic stability. For a better understanding of the present invention and further features thereof, reference is made to the following detailed description of various preferred embodiments wherein: Figure 1 represents an infrared plot of the bridged gallium phthalocyanine dimer of the formula C 32 H 16 N 8 GaOCH 2 CH 2 OGaN 8 H 16 C 32 prepared as described in Example I. Figure 2 represents a plot of 1 H NMR spectroscopy (in TFA-d/CDCl 3 solution) of the bridged phthalocyanine dimer prepared as described in Example I. Figure 3 represents an X-ray powder diffraction trace for the bridged gallium phthalocyanine dimer (Type I polymorph) prepared as described in Example I. Figure 4 is an infrared plot of the chlorogallium phthalocyanine prepared as described in Example II. Figure 5 is an X-ray powder diffraction trace for the chlorogallium phthalocyanine (Type I polymorph) prepared as described in Example II. Figure 6 is an infrared plot of the Type I hydroxygallium phthalocyanine prepared as described in Example III. Figure 7 is an X-ray powder diffraction trace for the Type I hydroxygallium phthalocyanine prepared as described in Example III. Figure 8 is an X-ray powder diffraction trace for the bridged gallium phthalocyanine dimer (Type I polymorph with a low level of crystallinity) prepared as described in Example IV. Figure 9 is an infrared plot of the Type V hydroxygallium phthalocyanine prepared as described in Comparative Example I. Figure 10 is an X-ray powder diffraction trace for the Type V hydroxygallium phthalocyanine prepared as described in Comparative Example 1. The following Examples are intended to be illustrative only, and the invention is not intended to be limited to the materials, conditions, or process parameters recited therein, percentages are by weight unless otherwise indicated. Comparative Examples and data are also provided. EXAMPLE I Alkoxy-bridged Gallium Phthalocyanine Dimer Synthesis Using Gallium Methoxide Obtained From Gallium Chloride and Sodium Methoxide In Situ: To a 1 liter round bottomed flask were added 25 grams of GaCl 3 and 300 milliliters of toluene, and the mixture was stirred for 10 minutes to form a solution. Then, 98 milliliters of a 25 weight percent sodium methoxide solution (in methanol) were added while cooling the flask with an ice bath to keep the contents below 40°C. Subsequently, 250 milliliters of ethylene glycol and 72.8 grams of o-phthalodinitrile were added. The methanol and toluene were quickly distilled off over 30 minutes while heating from 70 to 135°C, and then the phthalocyanine synthesis was performed by heating at 195°C for 4.5 hours. The alkoxy-bridged gallium phthalocyanine dimer product formed was isolated by filtration at 120°C. The product was then washed with 400 milliliters of DMF at 100°C for 1 hour and filtered. The product was then washed with 600 milliliters of deionized water at 60°C for 1 hour and filtered. The product was then washed with 600 milliliters of methanol at 25°C for 1 hour and filtered. The product was dried at 60°C under vacuum for 18 hours. The bridged gallium phthalocyanine dimer, 1,2-di(oxogallium phthalocyaninyl) ethane, was isolated as a dark blue solid in 77 percent yield. The dimer product was characterized by elemental analysis, infrared spectroscopy, 1 H NMR spectroscopy and X-ray powder diffraction. Elemental analysis showed the presence of only 0.10 percent chlorine. Infrared spectroscopy: major peaks at 573, 611, 636, 731, 756, 775, 874, 897, 962, 999, 1069, 1088, 1125, 1165, 1289, 1337, 1424, 1466, 1503, 1611, 2569, 2607, 2648, 2864, 2950, and 3045 cm -1 (Figure 1); 1 H NMR spectroscopy (TFA-d/CDCl 3 solution, 1:1 v/v, tetramethylsilane reference): peaks at (δ, ppm ± 0.01 ppm) 4.00 (4H), 8.54 (16H), and 9.62 (16H) (Figure 2); X-ray powder diffraction pattern: peaks at Bragg angles (2Θ ± 0.2°) of 6.7, 8.9, 12.8, 13.9, 15.7, 16.6, 21.2, 25.3, 25.9, and 28.3, with the highest peak at 6.7 degrees 2Θ (Figure 3). EXAMPLE II Chlorogallium Phthalocyanine Synthesis Using Gallium Trichloride in 1-Chloronaphthalene: To a 5 liter round bottomed flask equipped with stirring and a nitrogen purge atmosphere were added 200 grams of GaCl 3 plus 582 grams of o-phthalodinitrile and 2.75 liters of 1-chloronaphthalene. The phthalocyanine synthesis was performed at 200°C for 4 hours. The phthalocyanine was filtered at 120°C and then washed in the filter with 350 milliliters of DMF. The product was then washed in a beaker with 1.5 liters of DMF at 22°C for 30 minutes and filtered. The product was then washed in a beaker with 1.5 liters of DMF at 100°C for 1 hour and filtered. The product was then washed again at 22°C for 30 minutes in a beaker with 1.5 liters of DMF and filtered. The product was then washed in a beaker with 1.5 liters of methanol at 65°C for 1 hour and filtered. The product was then washed again at 22°C for 30 minutes in a beaker with 1.5 liters of methanol and filtered. The resulting wet cake was dried at 60°C under vacuum for 18 hours resulting in 271 grams of chlorogallium phthalocyanine (39 percent yield). The product pigment hydroxygallium phthalocyanine Type V was characterized by elemental analysis, infrared spectroscopy and X-ray powder diffraction. Elemental analysis showed the presence of 5.60 percent chlorine (theoretical value for ClGaPc is 5.74 percent). Infrared spectroscopy: major peaks at 432, 507, 573, 638, 718, 754, 779, 866, 897, 947, 995, 1067, 1088, 1125, 1169, 1288, 1339, 1424, 1468, 1484, 1507, 1589, 1607, 1638, 1680, 1732, 1810, 1848, 1891, 1929, 1967, 2197, 2237, 2269, 2388, 2426, 2577, 2612, 2652, 2783, 2824, 2861, 2914, 2857, 3013, 3030, 3053 and 3084 cm -1 (Figure 4); X-ray diffraction pattern: peaks at Bragg angles of 7.3, 9.1, 10.9, 13.4, 18.6, 20.3, 27.0, 28.8 and 33.1, with the highest peak at 27.0 degrees 2Θ (2 theta +/- 0.2°) (Figure 5). EXAMPLE III Hydrolysis of Chlorogallium Phthalocyanine to Hydroxygallium Phthalocyanine: The hydrolysis of chlorogallium phthalocyanine synthesized in Example II above to hydroxygallium phthalocyanine was performed as follows. Sulfuric acid (94 to 96 percent, 125 grams) was heated to 40°C in a 125 milliliter Erlenmeyer flask and then 5 grams of the chlorogallium phthalocyanine were added. Addition of the solid was completed in approximately 15 minutes, during which time the temperature of the solution increased to about 48°C. The acid solution was then stirred for 2 hours at 40°C, after which it was added in a dropwise fashion to a mixture comprised of concentrated (about 30 percent) ammonium hydroxide (265 milliliters) and deionized water (435 milliliters), which had been cooled to a temperature below 5°C. The addition of the dissolved phthalocyanine was completed in approximately 30 minutes, during which time the temperature of the solution increased to about 40°C. The reprecipitated phthalocyanine was then removed from the cooling bath and allowed to stir at room temperature for 1 hour. The resulting phthalocyanine was then filtered through a porcelain funnel fitted with a Whatman 934-AH grade glass fiber filter. The resulting blue solid was redispersed in fresh deionized water by stirring at room temperature for 1 hour and filtered. This process was repeated at least three times, until the conductivity of the filtrate was <20 µS. The filtercake was oven dried overnight at 50°C to provide 4.75 grams (95 percent) of Type I HOGaPc, identified by infrared spectroscopy and X-ray powder diffraction. Infrared spectroscopy: major peaks at 507, 573, 629, 729, 756, 772, 874, 898, 956, 984, 1092, 1121, 1165, 1188, 1290, 1339, 1424, 1468, 1503, 1588, 1611, 1757, 1835, 1951, 2099, 2207, 2280, 2384, 2425, 2570, 2608, 2652, 2780, 2819, 2853, 2907, 2951, 3049 and 3479 (broad) cm -1 (Figure 6); X-ray diffraction pattern: peaks at Bragg angles of 6.8, 13.0, 16.5, 21.0, 26.3 and 29.5, with the highest peak at 6.8 degrees 2Θ (2 theta +/- 0.2°) (Figure 7). EXAMPLE IV Synthesis of Alkoxy-bridged Gallium Phthalocyanine Dimer From Hydroxygallium Phthalocyanine at 120°C: To a 500 milliliter round bottomed flask were added 6.0 grams of hydroxygallium phthalocyanine and 200 milliliters of ethylene glycol. The mixture was stirred while heating at 120°C for 5 hours. The alkoxy-bridged gallium phthalocyanine dimer was isolated by filtration and then twice washed with 200 milliliters of methanol. The product was dried at 60°C under vacuum for 18 hours. The alkoxy-bridged gallium phthalocyanine dimer, 1,2-di(oxogallium phthalocyaninyl) ethane, was isolated as a dark blue solid in 90 percent yield. The dimer product was characterized by infrared spectroscopy, 1 H NMR spectroscopy and X-ray powder diffraction. Infrared spectroscopy: major peaks at 573, 611, 636, 731, 756, 775, 874, 897, 962, 999, 1069, 1088, 1125, 1165, 1289, 1337, 1424, 1466, 1503, 1611, 2569, 2607, 2648, 2864, 2950, and 3045 cm -1 (identical to Figure 1); 1 H NMR spectroscopy (TFA-d/CDCl 3 solution, 1:1 v/v, tetramethylsilane reference): peaks at (δ, ppm ± 0.01 ppm) 4.00 (4H), 8.54 (16H), and 9.62 (16H) (identical to Figure 2); X-ray powder diffraction pattern: peaks at Bragg angles (2Θ ± 0.2°) of 6.7, 8.9, 12.8, 13.9, 15.7, 16.6, 25.9, and 28.3, with the highest peak at 6.7 degrees 2Θ (Figure 8). EXAMPLE V Alkoxy-bridged Gallium Phthalocyanine Dimer Synthesis From Hydroxygallium Phthalocyanine at 190°C: To a 500 milliliter round bottomed flask were added 6.0 grams of hydroxygallium phthalocyanine and 200 milliliters of ethylene glycol. The mixture was stirred while heating at 190°C for 5 hours. The alkoxy-bridged gallium phthalocyanine dimer was isolated by filtration and then twice washed with 200 milliliters of methanol. The product was dried at 60°C under vacuum for 18 hours. The alkoxy-bridged gallium phthalocyanine dimer, 1,2-di(oxogallium phthalocyaninyl) ethane, was isolated as a dark blue solid in 90 percent yield. The dimer product was characterized by infrared spectroscopy, 1 H NMR spectroscopy and X-ray powder diffraction. Infrared spectroscopy: major peaks at 573, 611, 636, 731, 756, 775, 874, 897, 962, 999, 1069, 1088, 1125, 1165, 1289, 1337, 1424, 1466, 1503, 1611, 2569, 2607, 2648, 2864, 2950, and 3045 cm-1 (identical to Figure 1); 1 H NMR spectroscopy (TFA-d/CDCl 3 solution, 1:1 v/v, tetramethylsilane reference): peaks at (δ, ppm ± 0.01 ppm) 4.00 (4H), 8.54 (16H), and 9.62 (16H) (identical to Figure 2); X-ray powder diffraction pattern: peaks at Bragg angles (2Θ ± 0.2°) of 6.7, 8.9, 12.8, 13.9, 15.7, 16.6) 21.2, 25.3, 25.9, and 28.3, with the highest peak at 6.7 degrees 2Θ (identical to Figure 3). COMPARATIVE EXAMPLE 1 Conversion of Type I Hydroxygallium Phthalocyanine to Type V: The Type I hydroxygallium phthalocyanine pigment obtained in Example III above was converted to Type V HOGaPc as follows. The Type I hydroxygallium phthalocyanine pigment (3.0 grams) was added to 25 milliliters of N,N-dimethylformamide in a 60 milliliter glass bottle containing 60 grams of glass beads ((0.25 inch) 6.3 mm in diameter). The bottle was sealed and placed on a ball mill overnight (18 hours). The solid was isolated by filtration through a porcelain funnel fitted with a Whatman GF/F grade glass fiber filter, and washed in the filter using several 25 milliliter portions of acetone. The filtercake was oven dried overnight at 50°C to provide 2.8 grams of Type V HOGaPc which was identified by infrared spectroscopy and X-ray powder diffraction. Infrared spectroscopy: major peaks at 507, 571, 631, 733, 756, 773, 897, 965, 1067, 1084, 1121, 1146, 1165, 1291, 1337, 1425, 1468, 1503, 1588, 1609, 1757, 1848, 1925, 2099, 2205, 2276, 2384, 2425, 2572, 2613, 2653, 2780, 2861, 2909, 2956, 3057 and 3499 (broad) cm -1 (Figure 9); X-ray diffraction pattern: peaks at Bragg angles of 7.4, 9.8, 12.4, 12.9, 16.2, 18.4, 21.9, 23.9, 25.0 and 28.1, with the highest peak at 7.4 degrees 2Θ (2 theta +/- 0.2°) (Figure 10). EXAMPLE VI The bridged gallium phthalocyanine dimers prepared in Examples IV and V, and the Type V HOGaPc prepared in Comparative Example 1 were utilized as a photogenerating layer or a photogenerating pigment in a layered photoconductive imaging member prepared by the following procedure. An aluminized MYLAR® substrate, about 4 mil in thickness, was first coated with a blocking layer of a silane/zirconium alkoxide solution prepared by mixing 6.5 grams of acetylacetonate tributoxy zirconium (ZC540), 0.75 gram of (aminopropyl)trimethoxysilane (A1110), 28.5 gram of isopropyl alcohol, and 14.25 gram of butanol using a number 5 wire wound rod applicator. The blocking layer was dried at 140°C for 20 minutes; the final thickness was measured to be 0.1 µm (micron). A dispersion was prepared by combining 0.5 gram of C 32 H 16 N 8 GaOCH 2 CH 2 OGaN 8 H 16 C 32 prepared as described in Examples IV and V, and 0.26 gram of poly(vinyl butyral) in 25.2 grams of chlorobenzene in a 60 milliliter glass jar containing 70 grams of 0.8 millimeter glass beads. The dispersion was shaken on a paint shaker for 2 hours and then coated onto the above silane/zirconium layer using a number 6 wire wound rod applicator. The alkoxy-bridged gallium phthalocyanine dimer photogenerating layer so formed was dried at 100°C for 10 minutes to a final thickness of about 0.2 µm (micron). A hole transporting layer solution was prepared by dissolving 5.4 grams of N,N'-diphenyl-N,N-bis(3-methyl phenyl)-1,1'-biphenyl-4,4'-diamine, and 8.1 grams of polycarbonate in 61.5 grams of chlorobenzene. The solution was coated onto the alkoxy-bridged gallium phthalocyanine dimer photogenerator layer using a 10 mil film applicator. The charge transporting layer thus obtained was dried at 115°C for 60 minutes to provide a final thickness of about 28 µm (microns). A dispersion was prepared by combining 0.5 gram of Type V HOGaPc prepared as described in Comparative Example 1, and 0.26 gram of poly(vinyl butyral) in 25.2 grams of chlorobenzene in a 60 milliliter glass jar containing 70 grams of 0.8 millimeter glass beads. The dispersion was shaken on a paint shaker for 2 hours and then coated onto the above silane/zirconium layer using a number 6 wire wound rod applicator. The alkoxy-bridged gallium phthalocyanine dimer photogenerating layer formed was dried at 100°C for 10 minutes to a final thickness of about 0.20 µm (micron). A hole transporting layer solution was prepared by dissolving 5.4 grams of N,N'-diphenyl-N,N-bis(3-methyl phenyl)-1,1'-biphenyl-4,4'-diamine, and 8.1 grams of polycarbonate in 61.5 grams of chlorobenzene. The solution was coated onto the alkoxy-bridged gallium phthalocyanine dimer photogenerator layer using a 10 mil film applicator. The charge transporting layer thus obtained was dried at 115°C for 60 minutes to provide a final thickness of about 28 microns. The xerographic electrical properties of photoresponsive imaging members prepared as described above were determined by electrostatically charging the surface thereof with a corona discharge source until the surface potential, as measured by a capacitatively coupled probe attached to an electrometer, attained an initial dark value, V 0 , of -800 volts. After resting for 0.5 second in the dark, the charged member reached a surface potential, V ddp , or dark development potential. The member was then exposed to filtered light from a Xenon lamp. A reduction in surface potential from V ddp to a background potential, V bg , due to the photodischarge effect was observed. The dark decay in volts per second was calculated as (V 0 -V ddp )/0.5. The half exposure energy, that is E 1/2 is the amount of exposure energy causing reduction of the V ddp to half of its initial value, was determined. E 800-100V , which is the amount of exposure energy causing reduction of the V ddp from -800 volts to -100 volts, was also determined. The wavelength of light selected was 780 nanometers. In a cycling test, the above prepared devices or photoconductive imaging members were charged with a corotron to about -800 volts. They were exposed with 775 nanometers of light with an intensity of about 7 ergs/cm 2 and erased with white light of about 60 ergs/cm 2 . The dark development (V ddp ) and background (V bg ) potentials were measured and recorded while the testing was performed for 10,000 cycles. After the cycling test had been completed, the devices remained in the dark for about 20 hours. After charging the device to about -800 volts with a corotron, they were exposed with 775 nanometers of light with an intensity of 3 ergs/cm 2 and erased with white light of about 200 ergs/cm 2 . The dark development and background potentials were measured and recorded while the testing was performed for 5,000 cycles. The significantly higher erase light intensity used in this second test compared to the standard test accelerates the cycledown (decrease in the dark development potential) in the photogenerator material, and is thus considered a stress test. The imaging member prepared with the alkoxy-bridged gallium phthalocyanine dimer prepared in Example IV had a dark decay of 36.2 volts per second, E 1/2 = 1.66 ergs/cm 2 , and an E 800-100V = 3.87 ergs/cm 2 . In cycling tests, the device had a cycle down of -24 volts after 10,000 cycles and a cycle down of -32 volts after 5,000 cycles in the more stressful test. The imaging member prepared with the alkoxy-bridged gallium phthalocyanine dimer prepared in Example V had a dark decay of 25.6 volts per second, E 1/2 = 1.69 ergs/cm 2 , and an E 800-100V = 4.01 ergs/cm 2 . In cycling tests, the device had a cycledown of -28 volts after 10,000 cycles and a cycledown of -37 volts after 5,000 cycles in the more stressful test. The imaging member prepared with the Type V HOGaPc prepared in Comparative Example 1 had a dark decay of 22.2 volts per second, E 1/2 = 1.54 ergs/cm 2 , and an E 800-100V = 3.84 ergs/cm 2 . In cycling tests, the device had a cycledown of -47 volts after 10,000 cycles and a cycledown of -90 volts after 5,000 cycles in the more stressful test. From the information summarized in the Table, it is evident that the bridged gallium phthalocyanine dimer of this invention enabled imaging members, and improved cyclic stability (smaller voltage loss) when compared to Type V hydroxygallium phthalocyanine obtained from a chlorogallium phthalocyanine precursor. Comparative Electrical Properties of Phthalocyanine Photogenerators Device # P/G Material P/G from Example No. Dark Decay Volts /Sec. E 1/2 erg/cm 2 E 800-100v erg/cm 2 Cycle-Down 10k Volts Cycle-Down 5k Stress Test Volts 1 Dimer IV 36.2 1.66 3.87 -24 -32 2 Dimer V 25.6 1.69 4.01 -28 -37 3 HOGaPc from ClGaPc Comparative Example 1 22.2 1.54 3.84 -47 -90

Claims: A photoconductive imaging member comprised of a photogenerator layer comprising a charge generator material of the formula: wherein M is a trivalent metal and R is selected from the group consisting of an alkylene group; an alkylene-oxy-alkylene group; a -[(CH 2 ) m -O-(CH 2 ) m ] r - group wherein r is a number from 1 to 4, and m is a number from 2 to 4; and a -[CH(CH 3 )CH 2 -O-CH 2 (CH 3 )CH] s - group wherein s is a number from 1 to 3. A photoconductive imaging member as claimed in claim 1, including a supporting substrate and a charge transport layer. An imaging member as claimed in claim 1 or claim 2, wherein the trivalent metal in the charge generator material is aluminum, gallium, indium, or a trivalent metal of Mn(III), Fe(III), Co(III), Ni(III), Cr(III), or V(III). An imaging member as claimed in any one of claims 1 to 3, wherein R in the charge generator material is selected from the group consisting of: -(CH 2 ) n - wherein n is a number of from 2 to 12; wherein p a number of from 0 to 4; wherein q is a number of from 0 to 4. An imaging member as claimed in any one of claims 1 to 4, wherein the charge generator material is an alkoxy-bridged gallium phthalocyanine dimer of the formula C 32 H 16 N 8 GaOROGaN 8 H 16 C 32 . An imaging member as claimed in any one of claims 1 to 5, wherein said charge generator material is 1,2-di(oxogallium phthalocyaninyl) ethane of the formula C 32 H 16 N 8 GaOCH 2 CH 2 OGaN 8 H 16 C 32 ; 1,3-di(oxogallium phthalocyaninyl) propane of the formula C 32 H 16 N 8 GaOCH 2 CH 2 CH 2 OGaN 8 H 16 C 32 ; or 1,2-di(oxogallium phthalocyaninyl) propane of the formula C 32 H 16 N 8 GaOCH(CH 3 )CH 2 OGaN 8 H 16 C 32 . An imaging member as claimed in claim 1 or claim 2, wherein the charge generator material is dispersed in a resinous binder in an amount of from 5 percent to 95 percent by weight and preferably from 25 to 75 percent by weight. An imaging member as claimed in claim 2, wherein the charge transport layer is comprised of aryl amines of the formula dispersed in a highly insulating polymer in an amount of from 20 to 60 percent, and preferably from 30 to 50 percent, wherein X is an alkyl group or a halogen. An imaging member as claimed in claim 2, wherein the supporting substrate is overcoated with a polymeric adhesive layer of a a polyester of a thickness of from 0.01 to 1 µm (micron). An imaging method which comprises the formation of a latent image on a photoconductive imaging member as claimed in any one of claims 1 to 9, developing the image with a toner composition comprised of resin and pigment, transferring the image to a substrate and fixing the image thereto.

Inventors: BURT RICHARD A, DAIMON KATSUMI, GARDNER SANDRA J, HSIAO CHENG-KUO, IGARASHI RYOSAKU, KEOSHKERIAN BARKEV, LIEBERMANN GEORGE, MURTI DASARAO K, SAKAGUCHI YASUO, BURT, RICHARD A., DAIMON, KATSUMI, GARDNER, SANDRA J., HSIAO, CHENG-KUO, IGARASHI, RYOSAKU, KEOSHKERIAN, BARKEV, LIEBERMANN, GEORGE, MURTI, DASARAO K., SAKAGUCHI, YASUO
Applicants: XEROX CORP, XEROX CORPORATION
Application year: 1995
Main classification: G03G5
IPC codes: G03G5, C09B47