METAL (III) COMPLEXES CONTAINING, NON-AROMATIC, ANIONIC, DIENYL GROUPS AND ADDITION POLYMERIZATION CATALYSTS THEREFROM

Abstract: Novel group 4, group 3 or lanthanide metal complexes wherein the metal is in the +3 formal oxidation state containing a cyclic or non-cyclic, non-aromatic, anionic, dienyl ligand group bound to M and having a bridged ligand structure, catalytic derivatives of such complexes; and the use thereof as catalysts for polymerizing addition polymerizable monomers are disclosed.

Description: METAL (III) COMPLEXES CONTAINING, NON-AROMATIC, ANIONIC, DIENYL GROUPS AND ADDITION POLYMERIZATION CATALYSTS THEREFROM This invention relates to certain Group 3, 4 and Lanthanide metal complexes comprising a cyclic, or noncyclic, non-aromatic, anionic, dienyl group wherein the metal of said complexes is in the + 3 formal oxidation state and further wherein the metal is also covalently bonded via a second ligand group to the cyclic or noncyclic, non-aromatic, anionic, dienyl ligand group. The invention also relates to techniques for preparing such complexes, catalyst systems comprising such complexes that are useful for polymerizing addition polymerizable monomers, and to such polymerization processes themselves. Metal complexes containing delocalized, π-bonded ligand groups and methods for their preparation are disclosed in EP-A-416,815; EP-A-468,651 ; EP-A-514,828: EP-A-520,732 and WO93/19104, US-A- 5,055,438, US-A- 5,057,475, US-A- 5,096,867, US-A- 5,064,802 and US-A-5, 132,380. Despite the advance in the art brought about by the foregoing metal complexes, new and improved catalytic compounds are still desired. According to the present invention there are provided metal complexes corresponding to the formula: Z — Y / / * « L X wherein : M is a Group 3, Group 4 or Lanthanide metal in the + 3 formal oxidation state; L is a group containing a cyclic or noncyclic, non-aromatic, anionic, dienyl ligand group bound to M and Z, said L group containing up to 60 nonhydrogen atoms, and being selected from the group consisting of 2,4- dimethylpentadienyl-, 1,5-dimethylpentadienyl-, silyl substituted pentadienyl-, silyloxy substituted pentadienyl-, hydrocarbyloxy substituted pentadienyl-, cyclohexadienyl-, cyclosilahexadienyl-, cycloheptadienyl-, cyclooctadienyl-, diphenyl-η5-methyl-, and di(1-cyclohexenyl)-η5-methyl- groups, and inertly substituted derivatives of such cyclohexadienyl-, cyclosilahexadienyl-, cycloheptadienyl-, cyclooctadienyl-, diphenyl-η- -methyl- and di(1- cyclohexenyl)-η->-methyl- groups; Z is a moiety covalently bound to both L and Y, comprising boron, or a member of Group 14 of the Periodic Table of the Elements, said moiety having up to 60 non-hydrogen atoms; Y is a moiety comprising nitrogen, phosphorus, sulfur or oxygen through which Y is covalently bound to both Z and M, said moiety having up to 20 nonhydrogen atoms; X' independently each occurrence is a Lewis base containing up to 40 nonhydrogen atoms; X is a monovalent anionic moiety having up to 20 non-hydrogen atoms, provided however that X is not an aromatic group that is π-bonded to M and optionally X and one or more X' groups may be bonded together thereby forming a moiety that is both covalently bound to M and coordinated thereto by means of Lewis base functionality; and q is a number from 0 to 3. Additionally according to the present invention there are provided processes for preparing such complexes comprising contacting a precursor Group 4 or Lanthanide metal compound containing 2 dispiaceable ligand groups with a source of a dianionic ligand, (L-Z-Y)-2, and optionally, if the precursor compound is in a higher formal oxidation state than the desired product, reducing the resulting complex. Further according to the present invention there is provided a catalyst system useful for polymerization of addition polymerizable monomers comprising: A) 1) one or more of the above metal complexes or the reaction product of the above described process, and 2) one or more activating cocatalysts; or B) the reaction product formed by converting one or more of the above metal complexes or the reaction product of the above described process to an active catalyst by use of an activating technique. The present invention also provides a polymerization process comprising contacting one or more addition polymerizable monomers with a catalyst comprising one or more of the above catalyst systems. The polymerization may be performed under solution, suspension, slurry, or gas phase process conditions, and the composition or individual components thereof may be used in a heterogeneous, that is, a supported state, or in a homogeneous state. The catalyst can be used in combination with one or more additional catalysts of the same or different nature either simultaneously in the same or separate reactor or sequentially in the same or separate reactors. Catalysts prepared from the complexes of the present invention possess improved catalytic properties compared to previously known dienyl based metal complexes. Surprisingly, the present complexes are stable under a wide variety of operating conditions and catalyst systems formed therefrom possess desirable operating features. For example, olefin polymer products formed from catalyst systems comprising complexes according to the present invention are relatively low in undesirable internal vinyl unsaturation thereby making such polymers more resistant to degradation. All reference to the Periodic Table of the Elements herein shall refer to the Periodic Table of the Elements, published and copyrighted by CRC Press, Inc., 1989. Also, any reference to a Group or Groups shall be to the Group or Groups as reflected in this Periodic Table of the Elements using the IUPAC system for numbering groups. Preferably, M is titanium or zirconium, most preferably titanium. By the term "non-aromatic" when used with reference to L groups is meant that the atoms contributing electrons to the π-system through which the anionic ligand is π-bonded to the metal do not form a cyclic, planar, π- system with 4n + 2 electrons, where n is an integer greater than or equal to 0. With respect to the methyldiphenyl group, that is : it should be noted that the group includes phenyl substituents but the π-system through which the ligand is bound to the metal is an η5 system, not ir 6 . Examples of aromatic ligand groups which are not included within the present definition of L include cyclopentadienyl ligands and substituted cyclopentadienyl ligands (including indenyl, fluorenyl, and hydrogenated derivatives thereof). By the term "divalent derivatives" is meant that L is bonded to both Z and M. Suitable inert substituents on L include hydrogen, hydrocarbyl, halocarbyl, halohydrocarbyl, silyl, germyl, halo, amino, phosphino, cyano, hydrocarbyloxy, siloxy and combinations thereof, each of said inert substituents having up to 20 nonhydrogen atoms, or optionally, two or more such substituents (except hydrogen, cyano or halo) together form a ring structure, particularly a fused ring structure. Desirably, such L groups contain up to 50 non-hydrogen atoms. Hydrogenated multiple ring ligand groups are specifically included within the above described L ligands. Dihydronaphthalenyl, hexahydro- naphthalenyl, dihydroanthracenyl, hexahydroanthracenyl, decahydro- anthracenyl groups, and such groups containing one or more of the foregoing hydrocarbyl, halocarbyl, halohydrocarbyl, silyl, germyl, halo, amino, phosphino, cyano, hydrocarbyloxy, siloxy groups or combinations thereof are specifically included within the above definition of L groups. Preferred L groups correspond to the following formulas: wherein : R' in each occurrence is a ligand that is independently selected from the group consisting of hydrogen, hydrocarbyl, silyl, germyl, siloxy, amino, hydrocarbyloxy, cyano, halo and combinations thereof, said R' having up to 20 non-hydrogen atoms, and optionally, two or more R' groups (where R' is not hydrogen, halo or cyano) may together form a divalent derivative of one of the foregoing ligands; and provided further that one R' comprises a covalent bond to Z. Especially suitable L groups are selected from the group consisting of divalent derivatives (as above defined with respect to L) of 2,4- dimethylpentadien-3-yl, cyclohexadienyl, cyclosilahexadienyl, cycloheptadienyl, or cyclooctadienyl groups; hydrocarbyl, silyl, hydrocarbyloxy and siloxy substituted derivatives of such groups; partially hydrogenated anthracenyl, or partially hydrogenated naphthalenyl groups; and hydrocarbyl, silyl, hydrocarbyloxy or siloxy substituted derivatives of such partially hydrogenated anthracenyl or partially hydrogenated naphthalenyl groups. The dienyl ligand group is bound to the metal atom by any suitable electronic interaction. In certain circumstances the exact form of electronic interaction may be indeterminate, because several equivalent isomeric configurations of the L ligand group may be generated, such as, η •-, η3-, and q5-bonded L ligands. This fact has been previously disclosed in the art, particularly in the teachings of R. D. Ernst, Chem. Rev., 88, 1255-1291 (1988), and R. D. Ernst, et al„ J. Am. Chem. Soc. 107, 5016-5018 (1985). Moreover it is further well understood that the dienyl ligand in an η- -bonded configuration may be depicted in several equivalent isomeric configurations, known as the "W", "U" and " S" configurations. Such isomeric forms are illustrated with the 2,4-dimethylpentadien-3-yl ligand in the following drawing: ι3" "η5-W" "η5-U" "η5-S" Such variants are not necessarily separately named herein nor are the carbon atoms contributing to the dienyl ligand's bonds always identified since the equivalence of such L groups is well recognized by the skilled artisan, as illustrated by the above cited Ernst and Ernst, et al. references. It is to be further understood that in naming the foregoing L groups, the original positions of the double bonds of the dienyl ligand need not be identified since in the final delocalized ligand group the original double bonds no longer exist, that is, the η5-1,3-pentadien-3-yl group is identical to the η5-1,4-pentadien-3-yl group. All such isomers are equivalent and may be referred to simply as η5- pentadien-3-yl. For purposes of the present invention it is to be understood that all possible isomeric forms of L are included in any reference to a specific isomer or electronic structure. The positional numbering of the L group herein is accomplished by identifying the carbons contributing to the bonds to M and Z or where no ambiguity is possible, merely identifying the total carbons contributing to such bonds with the symbol, η. In monocyclic systems the lowest ordinals in sequence are assigned to the carbons contributing to the bonds with the positions otherwise numbered so as to produce the lowest positional numbers for substituted carbon atoms. Thus, the trimethyl-substituted cyclohexadienyl ligand group derived from 1, 5, 5-trimethyl-1,3-cyclohexadiene and bound at what was the the 2-position (illustrated as follows) Cyclohexadiene compound ligand is named (2, 6, 6-trimethyl-η5-cyclohexadien-3-yl) rather than (4, 6, 6-trimethyl- η5-cyclohexadien-3-yl) or (2, 2, 4-trimethyl-η5-cyclohexadien-5-yl). The positional attachment of the Z group is indicated by identifying the carbon atom followed by -yl, that is, (η5-pentadien-1-yl) or (η5-pentadien-2-yl). Multicyclic systems are numbered using standard nomenclature so as to avoid confusion. Specifically, hydrogenated naphthalenyl and hydrogenated anthracenyl systems are specifically illustrated as follows: Hydrogenated positions of multicyclic systems are generally identified herein, however it is to be further understood that while various isomeric forms of such hydrogenated ligands are possible they are not necessarily named herein. Examples of the foregoing L groups include: (2,4-dimethyl-η5- pentadien-1-yl), (2,4-dimethyl-η5-pentadien-2-yl), (2, 4-dimethyl-η5.p e ntadien- 3-yl), (1,5-dimethyl-η5-pentadien-1-yl), (1 , 5-dimethyl-η5-ρentadien-2-yl), (1 , 5- dimethyl-η5-pentadien-3-yl), (1, 5-bis(trimethylsilyl)-η5-pentadien-3-yl), (η5- cyclohexadien-1-yl), (qδ-cyclohexadien-2-yl), (η5-cyclohexadien-3-yl), (6, 6- dimethyl-η5-cydohexadien-1-yl), (6, 6-dimethyl-q5-cyclohexadien-2-yl), (6, 6- dimethyl-η5-cyclohexadien-3-yl), (6,6-dimethyl-η5-6-sila-cyclohexadien-3-yl), (6- t-butyl-6-methoxy-η5-6-sila-cyclohexadien-3-yl), (6-methyl-6-fluoro-η5-6-sila- cyclohexadien-3-yl), (1, 2, 6, 6-tetramethyl-q5-cyclohexadien-4-yl), (1, 2, 4, 6, 6- pentamethyl-η5-cyclohexadien-3-yl), (1, 2, 4, 6, 6-pentamethyl-q5- cyclohexadien-5-yl), (1, 2, 5, 6, 6-pentamethyl-q5-cyclohexadien-4-yl), (1, 2, 4, 5, 6, 6-hexamethyl-q5-cyclohexadien-3-yl), (1, 2, 4, 5-tetramethyl- 6, 6- cyclotrimethylene-η5-cyclohexadien-3-yl), (2, 3, 4, 9, 10-η-1, 2-dihydronaphtha- len-1-yl), (2, 3, 4, 9, 10-η-1, 2-dihydronaphthalen-2-yl), (1, 1-dimethyl-2, 3, 4, 9, 10-11-1, 2-dihydronaphthalen-2-yl), (1, 1 -dimethyl-2, 3, 4, 9, 10-q-1, 2- dihydronaphthalen-4-yl), diphenylmethyl, di(1-cyclohexenyl)methyl, the equivalent ligands: (1, 1-dimethyl-2, 3, 4, 9, 10-η-1, 2, 5, 6, 7, 8- hexahydronaphthalen-4-yl), (1, 1-dimethyl-2, 3, 4, 9, 10-q-1, 4, 5, 6, 7, 8- hexahydronaphthalen-4-yl), and (1, 1-dimethyl-2, 3, 4, 9, 10-q-1 , 5, 6, 7, 8, 9- hexahydronaphthalen-4-yl), the equivalent ligands (1, 1, 2, 3-tetramethyl-2, 3, 4, 9, 10-q-1, 2, 5, 6, 7, 8- hexahydronaphthalen-4-yl), (1, 1, 2, 3-tetramethyl-2, 3, 4, 9, 10-q-1, 4, 5, 6, 7, 8- hexahydronaphthalen-4-yl), and (1, 1, 2, 3-tetramethyl-2, 3, 4, 9, 10-q-1, 5, 6, 7, 8, 9-hexahydronaphthalen-4-yl), (10, 11, 12, 13, 14-q-9, 10-dihydroanthracen-9-yl), (10, 11, 12, 13, 14-q-9,10- dihydroanthracen-1-yl), (9, 9-dimethyl-10, 11, 12, 13, 14-q-9, 10- dihydroanthracen-10-yl), (10, 11, 12, 13, 14-q-1, 2, 3, 4, 9, 10- hexahydroanthracen-9-yl), (10, 11, 12, 13, 14-q-1, 2, 3, 4, 9,10- hexahydroanthracen-1-yl), (10, 11, 12, 13, 14-q-1, 2, 3, 4, 9, 11-hexahydro- anthracen-9-yl), (10, 11, 12, 13, 14-q-1, 4, 5, 8, 9, 10-hexahydroanthracen-1-yl), (9, 9-dimethyl-10, 11 , 12, 13, 14-q-1, 4, 5, 8, 9, 10-hexahydroanthracen-10-yl), (9, 9-dimethyl-10, 11, 12, 13, 14-q-1, 4, 5, 8, 9, 10-hexahydroanthracen-2-yl), (8, 8- dimethyl-5, 6, 7, 13, 14-q-1, 4, 5, 8, 9,10-hexahydroanthracen-10-yl), the equivalent ligands: (10, 11 , 12, 13, 14-q-1, 2, 3, 4, 5, 6, 7, 8, 9,10- decahydroanthracen-9-yl) and (10, 11, 12, 13, 14-q-1, 2, 3, 4, 5, 6, 7, 8, 9,11 - decahydroanthracen-9-yl); and the equivalent ligands: (9, 9-dimethyl-10, 11 , 12, 13, 14-q-1 , 2, 3, 4, 5, 6, 7, 8, 9,10-decahydroanthracen-10-yl) and (9, 9-dimethyl-10, 11 , 12, 13, 14-q-1 , 2, 3, 4, 5, 6, 7, 8, 9,11-decahydroanthracen-10-yl) These groups are further illustrated in the following structures: 2-methyl-q5-cyclohexadien-3-yl), (6,6-dimethyl-q5-cyclohexadien-1-yl), CH, CH, (1 , 2, 4, 5, 6, 6-hexamethyl-q5- cyclohexadien-3-yl) CH 3 CH 3 CH 2 CH 2 (1, 2, 4, 5-tetramethyl- 6, 6- I cyclotetramethylene-q5- CH 2 CH 2 cyclohexadιen-3-yl) CH 3 CH, (6,6-dimethyl-q5-6-sila- cyclohexadien-3-yl) (6-t-butyl-6-methoxy-q5-6- sila-cyclohexadιen-3-yl) (2, 3, 4, 9, 10-q-1, 2-dihydronaphthalen- 2-yl)or(1,2, 3, 9,10-q-1,4- dihydronaphthalen-3-yl), (2,3,4,9, 10-q-1,2-dihydronaphthalen- 4-yl) or (1,2, 3, 9, 10-q-1, 4-dihydro- naphthalen-1-yl), 10-q-1, 2- ), 0-q-1, 4, thalen- l-2, 3, 4, 5, 10-q- phthalen-4-yl), (10, 11, 12, 13, 14-q-9,10-dihydro- anthracen-9-yl), (9,9-dimethyl-10, 11, 12, 13, 14-q-9,10- dihydroantnracen-10-yl), (1,1-dimethyl-2, 3, 4, 11, 12-q-1, 4, 5, 6, 7, 8, 9,10, 13, 14-decahydroanthracen-4-yl) or (1,1-dimethyl-2, 3, 4, 11, 12-q-1, 5, 6, 7, 8, 9, 10, 11, 13, 14-decahydroanthracen-4-yl), (9,9-dimethyl-10, 11, 12, 13, 14-q-1, 2, 3, 4, 5, 6, 7, 8, 9,10-decahydroanthracen-10-yl) or (9,9-dimethyl-10, 11, 12, 13, 14-q-1, 2, 3, 4, 5, 6, 7, 8, 9,11-decahydroanthracen-10-yl) Examples of X include chloro, hydrocarbyl, hydrocarbyloxy said X having up to 12 non-hydrogen atoms. Preferred examples of X groups are halide groups, allyl and methyl-substituted allyl stabilizing ligands. Preferred examples of X and X' groups taken together are di(hydrocarbyl)amino-, hydrocarbyloxy-, and di(hydrocarbyl)phosphino-substituted hydrocarbyl or silyl groups of up to 20 nonhydrogen atoms. Most preferred X groups are allyl. Most preferred X and X' groups taken together are dialkylaminobenzyl groups having from 1 to 4 carbons in each alkyl group. Preferred X' groups (when not bonded to X) include phosphines, phosphites, ethers, amines, carbon monoxide, salts of Group 1 or 2 metals, and mixtures of the foregoing X' groups. Examples of the foregoing especially include trimethylphosphine, triethylphosphine, trifluorophosphine, triphenyl- phosphine, bis-1,2-(dimethylphosphino)ethane, trimethylphosphite, triethylphosphite, dimethylphenylphosphite, tetrahydrofuran, diethy! ether, carbon monoxide, pyridine, bipyridine, tetramethylethylenediamine (TMEDA), dimethoxyethane (DME), dioxane, triethylamine, lithium chloride, and magnesium chloride. Preferred metal coordination complexes according to the present invention correspond to the formula: Z — Y / / L M X wherein: Y is -O-, -S-, -NR * -, -PR * -; Z is SiR * 2 , CR * 2 , SiR * 2 SiR * 2, CR* 2 CR * 2, CR * = CR * , CR * 2 SiR * 2 , CR * 2 CR* 2 CR * 2, CR * 2 SiR * 2 CR * 2 , SiR * 2 CR * 2 CR * 2 , SiR * 2 CR* 2 SiR * 2 , SiR * 2 SiR * 2 CR * 2 , SiR * 2SiR * 2SiR * 2, or GeR * 2," wherein: R * each occurrence is independently hydrogen, or a member selected from hydrocarbyl, silyl, halogenated alkyl, halogenated aryl, and combinations thereof, said R * having up to 18 non-hydrogen atoms, and optionally (when R * is not hydrogen), two R * groups from Z , or an R * group from Z and an R * group from Y form a ring system. M is titanium, scandium, yttrium or lanthanium in the + 3 formal oxidation state; L is a divalent derivative of a 2,4-dimethyl-q5-pentadien-3-yl, cyclohexadienyl, cyclosilahexadienyl, partially hydrogenated naphthalenyl, partially hydrogenated anthracenyl group or a hydrocarbyl or silyl substituted derivative of such cyclohexadienyl, cyclosilahexadienyl, partially hydrogenated naphthalenyl, partially hydrogenated anthracenyl group, each said hydrocarbyl or silyl substituent having up to 10 nonhydrogen atoms; and X is chloro, allyl or an N, N-dialkylamino substituted hydrocarbyl group, said X having up to 12 non-hydrogen atoms. Most highly preferred metal coordination complexes are amidosilane- or amidoalkanediyl- compounds corresponding to the formula: (ER" 2 ) -N-R'" L M X wherein : E is independently each occurrence silicon or carbon. R" is independently each occurrence hydrogen or C1-10 hydrocarbyl; R'" is an aryl, benzyl, hydrocarbyl substituted aryl, hydrocarbyl substituted benzyl, secondary or tertiary alkyl or tertiary silyl group of up to 12 nonhydrogen atoms; M is titanium in the + 3 formal oxidation state; m is an integer from 1 to 3; L is a (2,4-dimethylpentadien-3-yl), (6,6-disubstituted-q->- cyclohexadien-3-yl), (6,6-disubstituted-q5-cyclosilahexadien-3-yl), (1 , 2, 3, 4, 5-q- cyclohexadien-6-yl), (6-substituted-1, 2, 3, 4, 5-q-cyclohexadien-6-yl), (1, 2, 4, 5, 6, 6-hexasubstituted-q5-cyclohexadien-3-yl)-, (1 , 1-disubstituted-q5-hexahydro- naphthalen-4-yl), (1 , 1, 2, 3-tetrasubstituted-q5-hexahydronaphthalen-4-yl), or (9, 9-disubstituted-10, 11, 12, 13, 14-q-1 , 2, 3, 4, 5, 6, 7, 8, 9, 10- decahydroanthracene-10-yl), group said substituents independently each occurrence being hydrocarbyl, hydrocarbyloxy, silyl, siloxy or a mixture thereof of up to 10 nonhydrogen atoms each; X is chloro or allyl, and X' is THF or MgCI; or X and X' together is 2- (N,N-dimethylamino)benzyl. As a means of further illustration of the invention, specific metal complexes included therein are: Substituted pentadienyl complexes (N-tert-butylamido)(dimethyl)(2,4-dimethyl-q5-pentadien-1-yl)silane- titanium(lll) chloride . MgCI; (N-tert-butylamido)(dimethyl)(2,4-dimethyl-q5- pentadien-3-yl)silanetitanium (III) methyl .THF; (N-tert-butylamido)- (dimethyl)(2,4-dimethyl-q5-pentadien-3-yl)silanetitanium (lll) bis(trimethyl- silyl)methyl; (N-tert-butylamido)(diphenyl)(2,4-dimethyl-q5-pentadien-3- yl)silanetitanium (III) 2-(N,N-dimethylamino)benzyl; (N-benzylamido)- (dimethyl)(2,4-dimethyl-q5-pentadien-3-yl)silanetitanium (lll) (q3-propenyl); (N-tert-butylamido)(tetramethyl)(2,4-dimethyl-q5-pentadien-3- yl)disilanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(tetramethyl)(1,5-bis(trimethylsilyl)-2,4-dimethyl-q5-pentadien-1- yl)disilanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert-butylamido)(1, 1, 2, 2-tetramethyl)(1,5-bis(trimethylsilyl)-2,4-dimethyl-q5-pentadien-3- y disilanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert-butylamido)(1, 1, 2, 2-tetramethyl)(q5-2,4-dimethylρentadien-3-yl)disilanetitanium (III) (q3- propenyl); (N-tert-butylamidomethylene)(dimethyl)(2,4-dimethyl-q5- pentadien-3-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(dimethyl)(2,4-dimethyl-q5-pentadien-3- ylmethylene)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(dimethyl)(2,4-dimethyl-q5-pentadien-3-yl)silanetitanium (III) 2 (N,N-dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(2,4-dimethyl-q5- pentadien-1-yl)silanetitanium (III) (q3-propenyl); (N-tert- butylamido)(dimethyl)(1,5-dimethyl-q--pentadien-3-yl)silanetitanium (lll)chloride • MgCI; (N-phenylamido)(dimethyl)(2,4-dimethyl-q5-pentadien-1- yl)silanetitanium(lll) (q3-propenyl); (N-cyclododecyl)(dimethyl)(2,4-dimethyl- q 5 -pentadien-3-yl)silanetitanium (III) methyl .THF; (N-tert- butylamido)(dimethyl)(1,5-bis(trimethylsilylmethyl)-q5-pentadien-3- yljsilanetitanium (III) methyl . THF; 1-(N-tert-butylamido)-2-(2,4-dimethyl-q 5 - pentadien-3-yl)ethane-1,2-diyltitanium (III) 2-(N, N-dimethylamino)benzyl; (N- tert-butylamido)(dimethyl)(1,5-di(trimethylsilyl)2,4-dimethyl-q 5 -pentadien-3- yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; and (N-tert- butylamido)(dimethyl)(1,5-bis(trimethylsilyl)-q5-pentadien-3-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl. Cyclohexadienyl and substituted cyclohexadienyl complexes (N-tert-butylamido)(dimethyl)(q5-cyclohexadien-1-yl)silanetitanium(lll) chloride . MgCI; (N-tert-butylamido)(dimethyl)(q5-cyclohexadien-1- y silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(dimethyl)(6,6-dimethyl-q5-cyclohexadien-1-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(6,6-dimethyl-q5- cyclohexadien-3-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(diphenyl)(6,6-dimethyl-q5-cyclohexadien-3-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert-butylamido)(1,1 ,2,2-tetramethyl)(6,6- dimethyl-q5-cyclohexadien-1-yl)disilanetitanium (III) 2-(N, N- dimethylamino)benzyl; (N-tert-butylamido)(1,1,2,2-tetramethyl)(6,6-dimethyl- q5-cyclohexadien-3-yl)disilanetitanium (III) 2-(N, N-dimethylamino)benzyl; ((N- tert-butylamido)methyl)(dimethyl)(6,6-dimethyl-q5-cyclohexadien-3- yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(dimethyl)((6,6-dimethyl-q5-cydohexadien-3- yl)methyl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(dimethyl)(2,4-dimethoxy-6,6-dimethyl-q5-cyclohexadien-3- y silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N- benzylamido)(dimethyl)(6,6-dimethyl-q5-cyclohexadien-3-yl)silanetitanium (lll) 2-(N, N-dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(1, 2, 4, 5, 6, 6- hexamethyl-q5-cyclohexadien-3-yl)silanetitanium (III) 2-(N, N- dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(1, 2, 6, 6-tetramethyl-q5- cyclohexadien-3-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(dimethyl)(6, 6-dimethyl-q5-cyc!ohexadien-3-yl)silanetitanium (!ll) methyl »THF; (N-tert-butylamido)(dimethyl)(q5-cyclohexadien-1- yl)silanetitanium (IV) (q3-propenyl); (N-tert-butylamido)(dimethyl)(6, 6- dimethyl-q5-cyclosilahexadien-3-yl)silanetitanium (III) chloride . MgCI; (N-tert- butylamido)(dimethyl)(q5-cyclohexadien-1-yl)silanetitanium (III) (q3-propenyl); (N-tert-butylamido)(dimethyl)(6, 6-dimethyl-q5-cyclohexadien-3- yl)silanetitanium (III) chloride • MgCI; (N-dodecyl)(dimethyl)(6, 6-dimethyl-q5- cyclohexadien-3-yl)silanetitanium (III) chloride • MgCI; (N-tert- butylamido)(dimethyl)(6, 6-dimethyl-q5-cyclohexadien-3-yl)silanetitanium (III) trimethylsilylmethyl; (N-tert-amylamido)(dimethyl)(6 t-butyl-6-methoxy-q5- cyclosilahexadien-3-yl)silanetitanium(lll) 2-(N, N-dimethylamino)benzyl; 1-(N- tert-butylamido)-2-(6, 6-dimethyl-q5-cyclohexadien-3-yl)ethanetitanium (III) 2- (N, N-dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(2, 3, 4, 9, 10-q-1,2- dihydronaphthalen-1-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N- tert-butylamido)(dimethyl)(1, 1-dimethyl-2, 3, 4, 9, 10-q-1,4- dihydronaphthalen-4-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N- tert-butylamido)(dimethyl)(2, 3, 4, 9, 10-q-1,2, 5, 6, 7, 8-hexahydronaphthalen- 1-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(dimethyl)(1,1-dimethyl-2, 3, 4, 9, 10-q-1,2, 5, 6, 7, 8-hexahydro- naphthalen-4-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(dimethyl)(9, 9-dimethyl-10, 11, 12, 13, 14-q-9,10- dihydroanthracen-10-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N- tert-butylamido)(dimethyl)(9,9-dimethyl-10, 11, 12, 13, 14-η-1 , 2, 3, 4, 9,10- hexahydroanthracen-10-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(9, 9-dimethyl-10, 11 , 12, 13, 14-q-1 , 2, 3, 4, 5, 6, 7, 8, 9,10-decahydroanthracen-10-yl)silanetitanium (III) 2-(N, N- dimethylamino)benzyl, and (N-tert-butylamido)(dimethyl)(9, 9-dimethyl-iθ, 11, 12, 13, 14-q-1, 2, 3, 4, 5, 6, 7, 8, 9,11-decahydroanthracen-10-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl. Higher cvcloalkadienyl and other complexes (N-tert-butylamido)(dimethyl)(q5-cydoheptadien-1-yl)silanetitanium(lll) chloride . MgCI; (N-tert-butylamido)(dimethyl)(q5-cyclooctadien-1- y silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(dimethyl)(q5-cyclooctadien-3-yl)silanetitanium (III) 2-(N, N- dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(6, 6, 7, 7-tetramethyl-q5- cycloheptadien-3-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(dimethyl)(6, 7, 8-trimethyl-q5-cyclooctadien-3-yl)silanetitanium (III) 2-(N, N-dimethylamino)ben7yl; (N-tert-butylamido)(1 , 1, 2, 2- tetramethyl)(6,6-dimethyl-q5-cycloheptadien-3-yl)disilanetitanium (III) 2-(N, N- dimethylamino)benzyl; (N-tert-butylamido)(1,1,2,2-tetramethyl)(6, 7, 8- trimethyl-q5-cyclooctadien-3-yl)disilanetitanium (III) 2-(N, N- dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(q5-di(1- cyclohexenyl)methyl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamidomethyl)(dimethyl)(q5-diphenylmethyl)silanetitanium (III) 2-(N, N- dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(q5-diphenylmethyl)- silanetitanium (III) chloride * MgCI; (N-tert-butylamido)(dimethyl)(q5- diphenylmethyl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert- butylamido)(dimethyl)(6, 6-dimethyl-q5-cyclosilahexadien-3-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(6-t-butyl-6- methoxy-q5-cyclosilahexadien-3-yl)silanetitanium (III) 2-(N, N- dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(6-methyl-6-methoxy-q 5 - cyclosilahexadien-3-yl)silanetitanium (III) 2-(N, N-dimethylamino)benzyl; and (N-tert-butylamido)(dimethyl)(6, 7, 7, 8-tetramethyl-q5-cyclooctadien-3- yl)silanetitanium (III) (q3-propenyl). The skilled artisan will recognize that additional members of the foregoing list include the corresponding Group 3 and Lanthanide containing derivatives, as well as complexes that are substituted as herein defined. Most highly preferred metal complexes according to the present invention comprise: (tert-butylamido)(dimethyl)(2,4-dimethyl-q5-pentadien-3- yQsilanetitanium (III) chloride • MgCI; (tert-butylamido)(dimethyl)(2,4-dimethyl- q 5 -pentadien-3-yl)silanetitanium (III) 2-(N,N-dimethylamino)benzyl; (tert-butyl- amido)(dimethyl)(2,4-dimethyl-q5-pentadien-3-yl)silanezirconium (III) methyl . THF; (tert-butylamido)(dimethyl)(2,4-dimethyl-q5-pentadien-1- yl)silanezirconium (III) methyl; (tert-butylamido)(dimethyl)(2,4-dimethyl-q5- pentadien-3-yl)silanezirconium (III) (q3-ρropenyl); (tert-butylamido)(dimethyl)- (2,4-dimethyl-q5-pentadien-3-yl)silanezirconium (III) 2-(N,N-dimethylamino)- benzyl; (tert-butylamido)(dimethyl)(1,5-bis(trimethylsilyl)-2,4-dimethyl-q5- pentadien-3-yl)silanetitanium (III) chloride * MgCI; (tert-butylamido)(dimethyl)- (1,5-bis(trimethylsilyl)-2,4-dimethyl-q5-pentadien-3-yl)silanetitanium (lll) 2- (N,N-dimethylamino)benzyl; (tert-butylamido)(dimethyl)(1,5-bis(trimethyl- silyl)-2,4-dimethyl-q5-pentadien-3-yl)silanezirconium (III) chloride . THF; (tert- butylamido)(dimethyl)(1,5-bis(trimethylsilyl)-2,4-dimethyl-q 5 -pentadien-3- yl)silanezirconium (III) 2-(N,N-dimethylamino)benzyl; (tert-butylamido)(di- methyl)(6,6-dimethyl-q5-cyclohexadien-3-yl)silanetitanium (III) chloride • MgCI; (tert-butylamido)(dimethyl)(6,6-dimethyl-q5-cyclohexadien-3-yl)silanetitanium (III) 2-(N N-dimethylamino)benzyl; (tert-butylamido)(dimethyl)(6,6-dimethyl- q5-cydosilahexadien-3-yl)silanetitanium (III) (q3-propenyl); (tert-butyl- amido)(dimethyl)(6,6-dimethyl-q5-cyclosilahexadien-3-yl)silanetitanium (lll) 2- (N,N-dimethylamino)benzyl; (tert-butylamido)(dimethyl)(6,6-dimethyl-q5- cyclohexadien-3-yl)silanezirconium (III) chloride * MgCI; (tert-butylamido)- (dimethyl)(6,6-dimethyl-q5-cyclohexadien-3-yl)silanezirconium (III) 2-(N,N- dimethylamino)benzyl, (tert-butylamido)(dimethyl)(6,6-dimethyl-q5- cyclosilahexadien-3-yl)silanezirconium (III) methyl *THF; (tert-butylamido)- (dimethyl)(6,6-dimethyl-q5-cyclosilahexadien-3-yl)silanezirconium (III) 2-(N,N- dimethylamino)benzyl, (N-tert-butylamido)(dimethyl)(2, 3, 4, 9, 10-q-1,2- dihydronaphthalen-4-yl)silanetitanium (III) 2-(N,N-dimethylamino)benzyl; (N- tert-butylamido)(dimethyl)(1,1-dimethyl-2,3,4,9,10-q-1,4-dihydronaphthalen- 4-yl)silanetitanium (III) 2-(N,N-dimethylamino)benzyl; (N-tert-butylamido)(di- methyl)(2, 3, 4, 9, 10-q-1,2, 5, 6, 7, 8-hexahydronaphthalen-4-yl)silanetitanium (III) methyl; (N-tert-butylamido)(dimethyl)(1,1-dimethyl-2, 3, 4, 9, 10-q-1 ,2, 5, 6, 7, 8-hexahydronaphthalen-4-yl)silanetitanium (III) 2-(N,N- dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(9, 9-dimethyl-10, 11, 12, 13, 14-q-9,10-dihydroanthracen-10-yl)silanetitanium (III) 2-(N,N-dimethyl- amino)benzyl; (N-tert-butylamido)(dimethyl)(9,9-dimethyl-10, 11, 12, 13, 14-q- 1, 2, 3, 4, 9,10-hexahydroanthracen-10-yl)silanetitanium (III) 2-(N,N- dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(9, 9-dimethyl-10, 11, 12, 13, 14-q-1, 2, 3, 4, 5, 6, 7, 8, 9,10-decahydroanthracen-10-yl)silanetitanium (III) 2-(N,N-dimethylamino)benzyl, and (N-tert-butylamido)(dimethyl)(9, 9- dimethyl-10, 11, 12, 13, 14-q-1, 2, 3, 4, 5, 6, 7, 8, 9,11-decahydroanthracen-10- y silanetitanium (III) (q3-propenyl). The complexes can be prepared in one embodiment by combining a precursor metal compound corresponding to the formula M(X)3X' q , wherein M, X, X' and q are as previously defined, with the added proviso that X in two occurrences is a monovalent anionic moiety having up to 20 non-hydrogen atoms capable of displacement by a dianion ligand, (L-Z-Y)-2, wherein L, Z, and Y are as previously defined, with a metallated derivative of the dianion ligand (Z-L-Y) *2 , with a silyl-, especially a trialkylsilyl-, derivative of the dianion ligand (Z-L-Y) *2 , said silyl- or trialkylsilyl- group having from 1 to 20 nonhydrogen atoms, or with the neutral compound, H-(Z-L-Y)-H. The reaction may optionally be performed in the presence of a Lewis base, X'. The reaction is preferably conducted in an inert, organic, liquid at a temperature from -100 to 300°C, preferably from -78 to 150°C, most preferably from 0 to 125°C. The complex is optionally recovered from the reaction mixture. Suitable metallated derivatives especially include lithium, sodium, potassium, magnesium, or Grignard derivatives of the dianion ligand. Suitable trialkylsilyl derivatives especially include trimethylsilyl derivatives of the dianion ligand. The complexes can also be prepared by combining, in the presence of a reducing agent, a precursor metal compound corresponding to the formula M(X)4X' q# wherein M, X, X' and q are as previously defined, with the added proviso that X in two occurrences is a monovalent anionic moiety having up to 20 non-hydrogen atoms capable of displacement by a dianion ligand, (L- Z-Y)-2, wherein L, Z, and Y are as previously defined, with a metallated derivative of the dianion ligand (Z-L-Y) *2 , with a silyl-, especially a trialkylsilyl-, derivative of the dianion ligand (Z-L-Y) 2 , said silyl- or trialkylsilyl- group having from 1 to 20 nonhydrogen atoms, or with the neutral compound, H-(Z-L-Y)-H. The reaction may optionally also be performed in the presence of a Lewis base, X'. The reaction is preferably conducted in an inert, organic, liquid at a temperature from -100 to 300°C, preferably from -78 to 150°C, most preferably from 0 to 125°C. The complex is optionally recovered from the reaction mixture. Suitable metallated derivatives especially include lithium, sodium, potassium, magnesium, or Grignard derivatives of the dianion ligand. Suitable trialkylsilyl derivatives especially include trimethylsilyl derivatives of the dianion ligand. Suitable reducing agents especially include n-butyl lithium, lithium or magnesium metal. The dianionic ligand group is prepared using standard synthetic measures known to the skilled artisan or by use of procedures analogous to previously known routes. The ligands containing cyclosilahexadienyl functionality are prepared in a manner analogous to the techniques disclosed in Jutzi, et al, Chem. Ber., 117, 1885-95 (1984); J. Am. Chem. Soc, 103 6788-6789 (1981); and Zh. Oshch. Khim., 44, 226-227 (1979), modified according to EP-A- 563,365 as to the particular silane ligand utilized. Suitable reaction media for the formation of the complexes are aliphatic and aromatic hydrocarbons, ethers, and cyclic ethers. Examples include straight and branched-chain hydrocarbons such as isobutane, butane, pentane, hexane, heptane, octane, and mixtures thereof; cyclic and alicyclic hydrocarbons such as cyclohexane, cycloheptane, methylcyclohexane, methylcycloheptane, and mixtures thereof; aromatic and hydrocarbyl- substituted aromatic compounds such as benzene, toluene, xylene, and styrene, alkyl ethers having from 1 to 4 carbons in each alkyl group; C1-4 dialkyl ether derivatives of (poly)alkylene glycols, and tetrahydrofuran. Mixtures of the foregoing are also suitable. Preferred solvents include C5-10 alkanes, dialkyl ethers having from 1 to 4 carbons in each alkyl group, tetrahydrofuran, toluene, and mixtures thereof. Solvated adducts of the metal precursor complex may also be used if desired. Examples of solvated adducts include pyridine-, diethylether-, tetrahydrofuran- (THF), 1,2-dimethoxyethane- (DME), or tetramethyl-ethylenediamine- (TMEDA) containing adducts. The complexes according to the present invention are surprisingly stable and readily synthesized. They are active addition polymerization catalysts alone or when combined with an activating cocatalyst or used with an activating technique. Suitable activating cocatalysts for use herein include polymeric or oligomeric alumoxanes, especially methylalumoxane, triisobutyl aluminum modified methylalumoxane, or isobutylalumoxane; neutral Lewis acids, such as C1-30 hydrocarbyl substituted Group 13 compounds, especially tri(hydrocarbyl)aluminum- or tri(hydrocarbyl)boron compounds and halogenated (including perhalogenated) derivatives thereof, having from 1 to 10 carbons in each hydrocarbyl or halogenated hydrocarbyl group, more especially perfluorinated tri(aryl)boron compounds, and most especially tris(pentafluorophenyl)borane; nonpolymeric, compatible, noncoordinating, ion forming compounds (including the use of such compounds under oxidizing conditions), especially the use of ammonium-, phosphonium-, oxonium-, carbonium-, silylium- or sulfonium- salts of compatible, noncoordinating anions, or ferrocenium salts of compatible, noncoordinating anions; bulk electrolysis (explained in more detail hereinafter); and combinations of the foregoing activating cocatalysts and techniques. The foregoing activating cocatalysts and activating techniques have been previously taught with respect to different metal complexes in the following references: EP-A-277,003, US-A- 5,153,157, US-A-5,064,802, EP-A-468,651, EP-A-520,732, and WO93/03250. Combinations of neutral Lewis acids, especially the combination of a trialkyl aluminum compound having from 1 to 4 carbons in each alkyl group and a halogenated tri(hydrocarbyl)boron compound having from 1 to 10 carbons in each hydrocarbyl group, especially tris(pentafluorophenyl)borane, further combinations of such neutral Lewis acid mixtures with a polymeric or oligomeric alumoxane, and combinations of a single neutral Lewis acid, especially tris(pentafluorophenyl)borane with a polymeric or oligomeric alumoxane are especially desirable activating cocatalysts. Suitable ion forming compounds useful as cocatalysts in one embodiment of the present invention comprise a cation which is a Bronsted acid capable of donating a proton, and a compatible, noncoordinating anion, A-. As used herein, the term "noncoordinating" means an anion or substance which either does not coordinate to the Group 4 metal containing precursor complex and the catalytic derivative derived therefrom, or which is only weakly coordinated to such complexes thereby remaining sufficiently labile to be displaced by a neutral Lewis base. A noncoordinating anion specifically refers to an anion which when functioning as a charge balancing anion in a cationic metal complex does not transfer an anionic substituent or fragment thereof to said cation thereby forming neutral complexes. "Compatible anions" are anions which are not degraded to neutrality when the initially formed complex decomposes and are noninterfering with desired subsequent polymerization or other uses of the complex. Preferred anions are those containing a single coordination complex comprising a charge-bearing metal or metalloid core which anion is capable of balancing the charge of the active catalyst species (the metal cation) which may be formed when the two components are combined. Also, said anion should be sufficiently labile to be displaced by olefinic, diolefinic and acetylenically unsaturated compounds or other neutral Lewis bases such as ethers or nitriles. Suitable metals include, but are not limited to, aluminum, gold and platinum. Suitable metalloids include, but are not limited to, boron, phosphorus, and silicon. Compounds containing anions which comprise coordination complexes containing a single metal or metalloid atom are, of course, well known and many, particularly such compounds containing a single boron atom in the anion portion, are available commercially. Preferably such cocatalysts may be represented by the following general formula: wherein : L* is a neutral Lewis base; (L * -H) + is a Bronsted acid; Ad- is a noncoordinating, compatible anion having a charge of d-, and d is an integer from 1 to 3. More preferably A d* corresponds to the formula: [M' k + Q n .] d* wherein : k is an integer from 1 to 3; n' is an integer from 2 to 6; n'-k = d; M' is an element selected from Group 13 of the Periodic Table of the Elements; and Q independently each occurrence is selected from hydride, dialkylamido, halide, hydrocarbyl, hydrocarbyloxide, halosubstituted- hydrocarbyl, halosubstituted hydrocarbyloxy, and halo- substituted silyl¬ hydrocarbyl radicals (including perhalogenated hydrocarbyl- perhalogenated hydrocarbyloxy- and perhalogenated silylhydrocarbyl radicals), said Q having up to 20 carbons with the proviso that in not more than one occurrence is Q halide. Examples of suitable hydrocarbyloxide Q groups are disclosed in US-A-5,296,433. In a more preferred embodiment, d is one, that is, the counter ion has a single negative charge and is A-. Activating cocatalysts comprising boron which are particularly useful in the preparation of catalysts of this invention may be represented by the following general formula: [L * -H] + [BQ * wherein : L * is as previously defined; B is boron in a valence state of 3; and Q is a hydrocarbyl-, hydrocarbyloxy-, fluorinated hydrocarbyl-, fluorinated hydrocarbyloxy-, or fluorinated silylhydrocarbyl- group of up to 20 nonhydrogen atoms, with the proviso that in not more than one occasion is Q hydrocarbyl. Most preferably, Q is each occurrence a fluorinated aryl group, especially, a pentafluorophenyl group. Illustrative, but not limiting, examples of boron compounds which may be used as an activating cocatalyst in the preparation of the improved catalysts of this invention are tri-substituted ammonium salts such as: trimethylammonium tetraphenylborate, triethylammonium tetraphenylborate, tripropylammonium tetraphenylborate, tri(n-butyl)ammonium tetraphenylborate, tri(t-butyl)ammonium tetraphenylborate, N,N-dimethylanilinium tetraphenylborate, N,N-diethylanilinium tetraphenylborate, N,N-dimethyl-2,4,6-trimethylanilinium tetraphenylborate, trimethylammonium tetrakis(pentafluorophenyl) borate, triethylammonium tetrakis(pentafluorophenyl) borate, tripropylammonium tetrakis(pentafluorophenyl) borate, tri(n-butyl)ammonium tetrakis(pentafluorophenyl) borate, tri(sec- butyOammonium tetrakis(pentafluorophenyl) borate, N,N-dimethylanilinium tetrakis(pentafluorophenyl) borate, N,N-dimethylanilinium n-butyltris(pentafluorophenyl) borate, N,N-dimethylanilinium benzyltris(pentafluorophenyl) borate, N,N-dimethylanilinium tetrakis(4-(t-butyldimethylsilyl)-2, 3, 5, 6- tetrafluorophenyl) borate, N,N-dimethylanilinium tetrakis(4-(triisopropylsilyl)-2, 3, 5, 6-tetrafluorophenyl) borate, N,N-dimethylanilinium pentafluorophenoxytris(pentafluorophenyl) borate, N,N-diethylanilinium tetrakis(pentafluorophenyl) borate, N,N-dimethyl-2,4,6- trimethylanilinium tetrakis(pentafluorophenyl) borate, trimethylammonium tetrakis(2,3,4,6-tetrafluorophenyl)borate, triethylammonium tetrakis(2,3,4,6-tetrafluorophenyl) borate, tripropylammonium tetrakis(2,3,4,6-tetrafluorophenyl) borate, tri(n-butyl)ammonium tetrakis(2,3,4,6-tetrafluorophenyl) borate, dimethyl(t-butyl)ammonium tetrakis(2,3,4,6-tetrafluorophenyl) borate, N,N-dimethylanilinium tetrakis(2,3,4,6-tetrafluorophenyl) borate, N,N-diethylanilinium tetrakis(2,3,4,6-tetrafluorophenyl) borate, and N,N-dimethyl-2,4,6-trimethylanilinium tetrakis(2,3,4,6-tetrafluorophenyl) borate; dialkyl ammonium salts such as: di-(i-propyl)ammonium tetrakis(pentafluorophenyl) borate, and dicyclohexylammonium tetrakis(pentafluorophenyl) borate; tri -substituted phosphonium salts such as: triphenylphosphonium tetrakis(pentafluorophenyl) borate, tri(o-tolyl)phosphonium tetrakis(pentafluorophenyl) borate, and tri(2,6-dimethylphenyl)phosphonium tetrakis(pentafluorophenyl) borate; di-substituted oxonium salts such as: diphenyloxonium tetrakis(pentafluorophenyl) borate, di(o-tolyl)oxonium tetrakis(pentafluorophenyl) borate, and di(2,6-dimethylphenyl)oxonium tetrakis(pentafluorophenyl) borate; di-substituted sulfonium salts such as: diphenylsulfonium tetrakis(pentafluorophenyl) borate, di(o-tolyl)sulfonium tetrakis(pentafluorophenyl) borate, and di(2,6-dimethylphenyl)sulfonium tetrakis(pentafluorophenyl) borate. Preferred [L*-H] + cations are N,N-dimethylanilinium and tributylammonium. Another suitable ion forming, activating cocatalyst comprises a salt of a cationic oxidizing agent and a noncoordinating, compatible anion represented by the formula: (Oχe + ) d (A<--) e wherein: Oχe + is a cationic oxidizing agent having a charge of e + ; e is an integer from 1 to 3; and Ad- and d are as previously defined. Examples of cationic oxidizing agents include: ferrocenium, hydrocarbyl-substituted ferrocenium, Ag + , or Pb + 2. Preferred embodiments of Ad- are those anions previously defined with respect to the Bronsted acid containing activating cocatalysts, especially tetrakis(pentafluorophenyl)borate. Another suitable ion forming, activating cocatalyst comprises a compound which is a salt of a carbenium ion and a noncoordinating, compatible anion represented by the formula : © + A- wherein: © + is a C1-20 carbenium ion; and A- is as previously defined. A preferred carbenium ion is the trityl cation, that is triphenylmethylium. A further suitable ion forming, activating cocatalyst comprises a compound which is a salt of a silylium ion and a noncoordinating, compatible anion represented by the formula: R 3 Si(X') q + A wherein: R is C1-10 hydrocarbyl, and X', q and A- are as previously defined. Preferred silylium salt activating cocatalysts are trimethylsilylium tetrakispentafluorophenylborate, triethylsilylium tetrakispentafluoro- phenylborate and ether substituted adducts thereof. Silylium salts have been previously generically disclosed in J. Chem Soc. Chem.Comm., 1993, 383-384, as well as Lambert, J. B., et al., Orqanometallics, 1994, 13, 2430-2443. Certain complexes of alcohols, mercaptans, silanols, and oximes with tris(pentafluorophenyl)borane are also effective catalyst activators and may be used according to the present invention. Such cocatalysts are disclosed in USP 5,296,433. The technique of bulk electrolysis involves the electrochemical oxidation of the metal complex under electrolysis conditions in the presence of a supporting electrolyte comprising a noncoordinating, inert anion. In the technique, solvents, supporting electrolytes and electrolytic potentials for the electrolysis are used such that electrolysis byproducts that would render the metal complex catalytically inactive are not substantially formed during the reaction. More particularly, suitable solvents are materials that are: liquids under the conditions of the electrolysis (generally temperatures from 0 to 100°C), capable of dissolving the supporting electrolyte, and inert. "Inert solvents" are those that are not reduced or oxidized under the reaction conditions employed for the electrolysis. It is generally possible in view of the desired electrolysis reaction to choose a solvent and a supporting electrolyte that are unaffected by the electrical potential used for the desired electrolysis. Preferred solvents include difluorobenzene (all isomers), dimethoxyethane (DME), and mixtures thereof. The electrolysis may be conducted in a standard electrolytic cell containing an anode and cathode (also referred to as the working electrode and counter electrode respectively). Suitable materials of construction for the cell are glass, plastic, ceramic and glass coated metal. The electrodes are prepared from inert conductive materials, by which are meant conductive materials that are unaffected by the reaction mixture or reaction conditions. Platinum or palladium are preferred inert conductive materials. Normally an ion permeable membrane such as a fine glass frit separates the cell into separate compartments, the working electrode compartment and counter electrode compartment. The working electrode is immersed in a reaction medium comprising the metal complex to be activated, solvent, supporting electrolyte, and any other materials desired for moderating the electrolysis or stabilizing the resulting complex. The counter electrode is immersed in a mixture of the solvent and supporting electrolyte. The desired voltage may be determined by theoretical calculations or experimentally by sweeping the cell using a reference electrode such as a silver electrode immersed in the cell electrolyte. The background cell current, the current draw in the absence of the desired electrolysis, is also determined. The electrolysis is completed when the current drops from the desired level to the background level. In this manner, complete conversion of the initial metal complex can be easily detected. Suitable supporting electrolytes are salts comprising a cation and a compatible, noncoordinating anion, A * . Preferred supporting electrolytes are salts corresponding to the formula G + A-; wherein : G + is a cation which is nonreactive towards the starting and resulting complex, and A- is as previously defined. Examples of cations, G + , include tetrahydrocarbyl substituted ammonium or phosphonium cations having up to 40 nonhydrogen atoms. Preferred cations are the tetra-n-butylammonium- and tetraethylammonium- cations. During activation of the complexes of the present invention by bulk electrolysis the cation of the supporting electrolyte passes to the counter electrode and A- migrates to the working electrode to become the anion of the resulting oxidized product. Either the solvent or the cation of the supporting electrolyte is reduced at the counter electrode in equal molar quantity with the amount of oxidized metal complex formed at the working electrode. Preferred supporting electrolytes are tetrahydrocarbylammonium salts of tetrakis(perfluoroaryl) borates having from 1 to 10 carbons in each hydrocarbyl or perf luoroaryl group, especially tetra-n-butylammonium tetrakis(penta- fluorophenyl) borate. A further recently discovered electrochemical technique for generation of activating cocatalysts is the electrolysis of a disilane compound in the presence of a source of a noncoordinating compatible anion. Preferably disilanes, such as hexamethylsilane are electrolyzed, in the presence of an ammonium salt of tetrakis(pentafluorophenyl)borate. The foregoing activating techniques and ion forming cocatalysts are also preferably used in combination with a tri(hydrocarbyl)aluminum or tri(hydrocarbyl)borane compound having from 1 to 4 carbons in each hydrocarbyl group, an oligomeric or polymeric alumoxane compound, or a mixture of a tri(hydrocarbyl)aluminum compound having from 1 to 4 carbons in each hydrocarbyl group and a polymeric or oligomeric alumoxane. The molar ratio of catalyst cocatalyst employed preferably ranges from 1 : 10,000 to 100: 1, more preferably from 1 :5000 to 10: 1, most preferably from 1 : 10 to 1 : 1. In a particularly preferred embodiment of the invention the cocatalyst can be used in combination with a tri(hydrocarbyl)aluminum compound having from 1 to 10 carbons in each hydrocarbyl group or an oligomeric or polymeric alumoxane. Mixtures of activating cocatalysts may also be employed. It is possible to employ these aluminum compounds for their beneficial ability to scavenge impurities such as oxygen, water, and aldehydes from the polymerization mixture. Preferred aluminum compounds include trialkyl aluminum compounds having from 2 to 6 carbons in each alkyl group, especially those wherein the alkyl groups are methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl, pentyl, neopentyl, or isopentyl, and methylalumoxane, modified methylalumoxane (that is, methylalumoxane modified by reaction with triisobutyl aluminum) (MMAO) and isobutylalumoxane. The molar ratio of metal complex to aluminum compound is preferably from 1 : 10,000 to 100: 1, more preferably from 1 : 1000 to 10: 1, most preferably from 1 :500 to 1 : 1. A most preferred activating cocatalyst comprises both a strong Lewis acid and an alumoxane, especially tris(pentafluorophenyl)borane and methylalumoxane, modified methylalumoxane, or diisobutylalumoxane. The catalysts may be used to polymerize ethylenically and/or acetylenically unsaturated monomers having from 2 to 100,000 carbon atoms either alone or in combination. Preferred monomers include the C2-20 α-olefins especially ethylene, propylene, isobutylene, 1-butene, 1-pentene, 1-hexene, 3- methyl-1-pentene, 4-methyl-1-pentene, 1-octene, 1-decene, long chain, macromolecular α-olefins, and mixtures thereof. Other preferred monomers include styrene, C._ 4 alkyl substituted styrene, tetrafluoroethylene, vinylbenzocyclobutane, ethylidenenorbornene, 1, 4-hexadiene, 1, 5-hexadiene, 1,7-octadiene, vinylcyclohexane, 4-vinylcyclohexene, allylbenzene, divinylbenzene, 2,5-norbornadiene, and mixtures of such other preferred monomers with C2-20 α-olefins. In general, the polymerization may be accomplished at conditions well known in the prior art for Ziegler-Natta or Kaminsky-Sinn type polymerization reactions, that is, temperatures from 0-250°C and pressures from atmospheric to 10,000 atmospheres (0.1 to 1000 MPa). Suspension, solution, slurry, gas phase or other process conditions may be employed if desired. A support, especially silica, modified silica (silica modified by calcining, treatment with a trialkylaluminum compound having from 1 to 10 carbons in each alkyl group, or treatment with an alkylalumoxane), alumina, or a polymer (especially polytetrafluoroethylene or a polyolefin) may be employed, and desirably is employed when the catalysts are used in a gas phase or slurry polymerization process. The support is preferably employed in an amount to provide a weight ratio of catalyst (based on metal):support from 1 : 100,000 to 1 : 10, more preferably from 1 :50,000 to 1 :20, and most preferably from 1 : 10,000 to 1 :30. In most polymerization reactions the molar ratio of catalyst: polymerizable compounds employed is from 10 12 : 1 to 10 1 : 1, more preferably from 10 *12 : 1 to 10 *5 : 1. Suitable solvents or diluents for polymerization are noncoordinating, inert liquids. Examples include C4-10 straight and branched- chain hydrocarbons , especially butane, isobutane, pentane, isopentane, hexane, heptane, octane, and mixtures thereof; cyclic and alicyclic hydrocarbons such as cyclopentane, cyclohexane, cycloheptane, methylcyclohexane, methylcycloheptane, and mixtures thereof; perfluorinated hydrocarbons such as perfluorinated C 4 . 10 alkanes, and aromatic and alkyl- substituted aromatic compounds such as benzene, toluene, and xylene (all isomers). Suitable solvents also include liquid olefins or other monomers or mixtures thereof as previously mentioned. The catalysts may also be utilized in combination with at least one additional homogeneous or heterogeneous polymerization catalyst in the same or separate reactors connected in series or in parallel to prepare polymer blends having desirable properties. An example of such a process is disclosed in WO 94/00500. One such polymerization process comprises: contacting, optionally in a solvent, one or more α-olefins with a catalyst according to the present invention comprising one or more metal complexes according to the present invention in one or more continuous stirred tank or tubular reactors, or in the absence of solvent, optionally in one or more fluidized bed gas phase reactors, connected in series or in parallel, and recovering the resulting polymer. In another such polymerization process, in one or more of the foregoing reactors, one or more α-olefins are also contacted with one or more catalyst compositions comprising one or more metal complexes according to the present invention in admixture with a catalyst composition comprising one or more homogeneous metallocene complexes other than a complex according to the present invention, said catalyst composition also comprising one or more cocatalyst activators. In yet another process an ethylene /α-olefin interpolymer composition is prepared by: (A) contacting ethylene and at least one other α-olefin under polymerization conditions in the presence of a homogeneous catalyst composition of the present invention comprising a metal complex of the present invention with at least one of the aforementioned activating cocatalysts in at least one reactor to produce a first interpolymer or optionally a solution of a first interpolymer, (B) contacting ethylene and at least one other α-olefin under polymerization conditions at optionally a different, preferably a higher, polymerization reaction temperature than used in step (A) in the presence of a heterogeneous Ziegler catalyst in at least one other reactor to produce a second interpolymer optionally in solution, and (C) combining the first interpolymer and second interpolymer to form an ethylene/α-olefin interpolymer blend composition, and (D) recovering the ethylene/α-olefin interpolymer blend composition. Preferably the heterogeneous Ziegler catalyst comprises: (i) a solid support component comprising magnesium halide, silica, modified silica, alumina, aluminum phosphate, or a mixture thereof, and (ii) a transition metal component represented by the formula : TrX" u (X'") v -u, or TrX" u O(X'")v-u-2 wherein: Tr is a Group 4, 5, or 6 metal, O is oxygen, X" is halogen, X'" is independently selected from hydrocarbyl, silyl, hydrocarbyloxy or siloxy having up to 10 non-hydrogen atoms, u is a number from 0 to 6 that is less than or equal to v, and v is the formal oxidation number of Tr. These polymerizations are generally carried out under solution conditions to facilitate the intimate mixing of the two polymer-containing streams. The foregoing technique allows for the preparation of ethylene/α- olefin interpolymer compositions having a broad range of molecular weight distributions and composition distributions. Preferably, the heterogeneous catalyst is also chosen from those catalysts which are capable of efficiently producing the polymers under high temperatures, especially, temperatures greater than or equal to 180°C under solution process conditions. In a still further embodiment, there is provided a process for preparing an ethylene/α-olefin interpolymer composition, comprising : (A) polymerizing ethylene and at least one other α-olefin in a solution process under suitable solution polymerization temperatures and pressures in at least one reactor containing a catalyst composition comprising the metal complex of the present invention with at least one of the aforementioned activating cocatalysts to produce a first interpolymer solution, (B) passing the interpolymer solution of (A) into at least one other reactor containing a heterogeneous Ziegler catalyst, in the presence of ethylene and optionally one other α-olefin under solution polymerization conditions to form a solution comprising the ethylene/α-olefin interpolymer composition, and (C) recovering the ethylene/α-olefin interpolymer composition. Preferably the heterogeneous Ziegler catalyst comprises: (i) a solid support component comprising a magnesium halide, silica or modified silica, including calcined silica, and (ii) a transition metal component represented by the formula : TrX" u (X"V u , or TrX" u O(X'")v-u-2 wherein: Tr, X", X'", O, u, and v are as previously defined. The foregoing technique also allows for the preparation of ethylene/α-olefin interpolymer compositions having a broad range of molecular weight distributions and composition distributions. Particularly desirable α-olefins for use in the foregoing processes are C3-8 α-olefins, most desirably 1-octene. The skilled artisan will appreciate that the invention disclosed herein may be practiced in the absence of any component which has not been specifically disclosed. The following examples are provided as further illustration thereof and are not to be construed as limiting. Unless stated to the contrary all parts and percentages are expressed on a weight basis. Example 1 (N-t-butylamido)(dimethyl)(6,6-dimethyl-r|5-cvclohexadien-3-yl)silanetitanium (III) chloride 1. Preparation of 5,5-dimethyl-l ,3-cyclohexadiene/ 3,3-dimethyl-1 ,4- cyclohexadiene isomeric mixture In a glass flask under nitrogen atmosphere, 50.0 g (0.357 mol) 5,5- dimethyl-1,3-cyclohexanedione (dimedone) was slurried in about 500 mL of diethyl ether. After cooling the slurry in an ice bath, 13 g (0.342 mol) of LiAIHή was slowly added. The reaction mixture was allowed to warm to room temperature and was stirred for 2 hours, after which 14 g (0.369 mol) of additional LiAIH4 was added. The reaction mixture was refluxed for 2 hours, then stirred overnight. Workup occurred as follows: After the reaction mixture was cooled in an ice bath, 27 mL of water was slowly added, followed by 27 mL of 15 weight percent, aqueous NaOH solution, then 81 mL of water. The resulting solids were filtered off and washed with diethyl ether. The combined ether solutions were concentrated by evaporation. To the resulting pale yellow product was added 10 mL of 9 M aqueous H2SO4. The product was collected after distillation using a short path distillation column up to a pot temperature of 145 °C. Additional H2SO4 was added and a second distillation was performed. After washing with 10 weight percent, aqueous Na2 O3, then with water, the product was dried with anhydrous MgSO4- The product was fractionally distilled, with fractions boiling up to about 100°C being collected. The yield was 12 g. of the isomeric mixture depicted as follows: 2. Preparation of potassium 6,6-dimethylcyclohexadienide To 14.0 g (0.111 mol) of potassium t-amylate (KOC(CH 3 ) 2 C2H 5 ) in 200 mL of pentane was added 44.4 mL of 2.5 M (0.111 mol) butyl lithium in hexane with formation of a small amount of brownish insoluble material. To this was added 12.0 (0.111 mol) of the dimethylcyclohexadiene isomeric mixture. A bright orange product resulted. After stirring overnight, the color became brownish orange. The product was filtered, washed several times with pentane, then dried under reduced pressure. The yield of orange powder was 11.8 g, 72.7 percent. 3. Preparation of (N-t-butylamino)(dimethyl)(4,4-dimethyl-2,5- cyclohexadien-1-yl)silane To a solution of 5.46 g (32.9 mmol) of CISi(CH3)2NHC(CH3)3 (obtained according to the technique of EP-A-563,365) in tetrahydrofuran (THF) was slowly added 4.50 g (30.8 mmol) of solid potassium 6,6-dimethylcyclohexadienide. After stirring overnight, the reaction mixture was filtered and the solvent was removed under reduced pressure. The residue was extracted with pentane, the resulting slurry was filtered and the solvent was removed from the filtrate. Purification by Kugelrohr distillation gave 3.58 g of product, 49.0 percent yield. 1 H NMR (C 6 D 6 ) δ 5.69 (d, 10.2 Hz, 2H), 5.45 (d, 9.9 Hz, 2H), 2.30 (s, 1 H), 1.13 (s, 3H), 1.12 (s, 3H), 1.07 (s, 9H), 0.12 (s, 6H). The structure of the product is depicted as follows: 4. Preparation of dilithium(N-t-butylamido)(dimethyl)(4,4-dimethyl- n5-cyclohexadien-1-yl)silane To 3.58 g (15.1 mmol) of (N-t-butylamino)(dimethyl)(4,4-dimethyl-2,5- cyclohexadien-1-yl)silane in 75 mL of diethyl ether was added 12.6 mL of 2.52 M n-butyl lithium in hexane. The resulting yellow reaction solution was stirred for several days, during which time a large amount of precipitate had formed. The reaction mixture was refluxed for several hours, then it was filtered. The solid was washed with hexane and then dried under reduced pressure. The yield of the pale yellow powder was 2.01 g, 53.5 percent yield. 5. Preparation of (N-t-butylamido)(dimethyl)(6, 6-dimethyl-n5. cyclohexadien-3-yl)silanetitanium (III) chloride 0.320g Of TiCl3(THF) 3 (1.40 mmol) was dissolved in 25 mL of THF. To this solution 0.350g of dilithium ((N-t-butylamino)(dimethyl)(4,4-dimethyl-1,3- cyclohexadien-1-yl)silane) (1.40 mmol) was added and the solution stirred for 20 minutes. The reaction mixture changed color indicating formation of the desired product but recovery was not attempted. Instead, the product was converted to the corresponding 2-(dimethylamino)benzyl complex in Example 2. Example 2 (N-t-butylamido)(dimethyl)(6,6-dimethyl-n5-cyclohexadien-3- vQsilanetitanium (III) 2-(dimethylamino)benzyl 0.198 g of 2-dimethylaminobenzyl lithium (1.40 mmol) was added to the reaction mixture of Example 1 and the solution was stirred for 20 minutes. After this time period the solvent was removed under reduced pressure and the residue extracted with pentane and filtered. The filtrate was concentrated and kept at -35 °C overnight to give 0.080 g (14 percent yield) of the desired product. The structure of the resulting product is as follows: Polymerization A two liter stirred reactor was charged with 800 g of toluene solvent and 50 g of 1-octene. The reactor was heated to 140 °C and saturated with ethylene at 3.4 MPa (500 psi). Catalyst and cocatalyst were mixed in a dry box by combining 0.2 mL of a 0.005M toluene solution of (N-t-butylamido)(dimethyl)(6,6- dimethyl-q5-cyclohexadien-3-yl)silanetitanium (III) 2-(dimethylamino)benzyl (1.0 μmole) and 1.0 μmole of ferrocenium tetrakis(pentafluorophenyl)borate also in toluene. The resulting solution was transferred to a catalyst addition tank and injected into the reactor. The polymerization was allowed to proceed with ethylene being added on demand. After 10 minutes the polymer solution was removed from the reactor. A hindered phenol antioxidant (lrganox™ 1010 available from Ciba Geigy Corp.), 100 mg, was added. Volatiles were removed under reduced pressure in an oven at about 130 °C for approximately 18 hours. Yield was 2.0 g of ethylene/ 1-octene copolymer. Example 3 (N-t-butylamido)(dimethyl)(1 ,1-dimethyl-2, 3, 4, 9, 10-n-1 ,2- dihydronaphthalen-4-yl)silanetitanium (III) chloride 1. Preparation of potassium 4,4-dimethyldihydronaphthalide A mixture of 4,4-dimethyl-3,4-dihydronaphthalene and 4,4-dimethyl-1,4- dihydronaphthalene (83: 17 ratio, 6.00 g, 37.9 mmol) was dissolved in approximately 200 mL of hexane in a 250 mL flask. To the flask was added potassium amylate (4.91 g, 38.9 mmol) followed by n-BuLi (16.1 mL, 2.48 M, 39.8 mmol). Immediate formation of an orange solid resulted. After stirring for 1 hour, the slurry was filtered and the solid washed four times with 20 mL of hexane each time. The solid was transferred to a flask which was evacuated to remove any volatiles. The desired product was recovered as a powdery orange solid. Yield was 6.91 g, 93 percent. 2. Preparation of (dimethyl)(N-t-butylamino)(4,4-dimethyldihvdro- naphthalen-1-yl)silane A 500 mL flask was charged with dimethyl(t-butylamino)chlorosilane (CISiMe 2 NHtBu) (5.81 g, 35.1 mmol) and approximately 80 mL of THF. A constant addition funnel was attached containing the potassium 4,4- dimethyldihydronaphthalide complex of step 1 (4.00 g, 20.4 mmol) dissolved in about 120 mL of THF. The flask was cooled to -78 °C and the orange solution added dropwise over a 3 hour period. The bath was removed and the mixture allowed to warm to 25 °C during which the color changed from tan to yellow. The solvent was removed under reduced pressure and the residue triturated once with 80 mL of hexane. The residue was taken up in hexane and filtered through Celite™ brand diatomaceous earth filter aid. The solids were washed once with 20 mL of hexane and the combined filtrates were concentrated. Stirring overnight under reduced pressure resulted in a yellow oil. Yield was 4.72 g, 80 percent. 3. Preparation of dilithium(dimethyl)(N-t-butylamido)(4,4- dimethyldihvdronaphthalen-l-vQsilane A 250 mL flask was charged with the (dimethyl)(N-t-butylamino)(4,4- dimethyldihydronaphthalenyl)silane mixture of step 2 (4.72 g, 16.4 mmol) and 120 mL of diethylether. To this solution was added sec-BuLi (25.9 mL, 1.3 M, 33.6 mmol) in small aliquots via syringe through a septum at 25 °C. The yellow- orange mixture was stirred overnight. The reaction mixture was filtered though Celite™ brand diatomaceous earth filter aid, the ether was removed and the residue triturated with hexane three times and discarded. The hexane was removed by evaporation and diethylether was added. This mixture was stirred overnight during which time a solid formed. The yellow solid flocculent material was isolated by filtration and dried in vacuo. Yield was 0.66 g, 13 percent. 4. (dimethyl)(N-t-butylamido)(1 ,1-dimethyl-2, 3, 4, 9, 10-n-1 ,2- dihvdronaphthalen-4-yl)silane titanium (III) chloride A 250 mL glass flask was charged with TiCl3(THF)3 (495 mg, 1.34 mmol) and 120 mL of THF. To this was added via pipet a THF solution of dilithium ((N-t- butylamido)(dimethyl)(4,4-dimethyl-1, 2, 3, 9, 10-q-1,2-dihydronaphthalen-1- yl)silane) (400 mg, 1.34 mmol). The solution turned brown opaque. PbCl2 (672 mg, 2.42 mmol) was added as a solid. The mixture was stirred for 2 hours at 25 °C and then filtered through Celite™ brand diatomaceous earth filter aid to give a brown solution. Concentration of the solution under reduced pressure and cooling to -25 °C produced brown crystals which were isolated via filtration. Yield was 120 mg, 22 percent. ESR analysis showed the product to be the above complex. Example 4 (N-t-butylamido)(dimethyl)(2,4-dimethyl-n 5 -pentadien-1-yl)silanetitanium (III) chloride 1 - Preparation of (N-t-butylamido)(dimethyl)(2,4-dimethyl-q 5 - pentadien-1-yl)silanetitanium (III) chloride (THF adduct) A reaction mixture was formed by combining 0.862 g (2.77 mmol) of dilithium (N-t-butylamido)(dimethyl)(2,4-dimethyl-2,4-pentadien-1-yl)silane and 1.35 g (3.63 mmol) of TiCl3*3THF in 50 mL of THF. After stirring overnight, the solution was filtered, the solvent was removed under reduced pressure, the residue was extracted with pentane, the dark solution was filtered and then concentrated and chilled in a -35°C freezer. The brown solid product was isolated. Example 5 (Dimethyl)(N-t-butylamido)(diphenylmethyl)silane titanium (III) chloride Preparation of diphenylmethyl potassium To a solution of 18.3 g (109 mmol) of diphenylmethane in 400 mL of hexane were added 11.99 g (109 mmol) of potassium t-a my late. To the resulting pale yellow solution were added 68.75 mL of 1.60 M (110 mmol) butyl lithium. The thick, bright orange slurry was stirred overnight. The solids were collected on a filter, washed three times with 100 mL, then twice with 50 mL of hexane, then dried under reduced pressure. The yield of bright orange powder was 18.23 g, 81.2 percent. Preparation of (N-t-butylamino)(dimethyl)(diphenylmethyl)silane To a solution of 4.1 g (24.7 mmol) of CISiMβ2NHCMe3 in 80 mL of THF were added 3.735 g (18.1 mmol) of solid diphenylmethyl potassium. The orange color of the diphenylmethyl potassium disappeared instantly and precipitate formed rapidly. The reaction mixture was stirred for several days. The solvent was removed under reduced pressure and the residue was extracted with hexane and the solvent was removed under reduced pressure. The yellow liquid product was subjected to vacuum pumping to remove the excess CISiMe2NHCMβ3. The yield was 4.786 g, 88.9 percent. 1 H NMR, (CDCI3) δ 7.33 - 7.06 (br, m, 10H), 3.57 (s, 1 H), 1.22 (s, 1 H), 1.06 (s, 9H), 0.08 (s, 6H). 13C NMR, (CDCI3) δ 142.8, 128.9, 128.0, 124.8, 49.6, 47.4, 33.8, 1.3. Preparation of dilithium(N-t-butylamido)(dimethyl)(diphenylmethyl)silane To a solution of 4.786 g (16.1 mmol) of (N-t-butylamino)(dimethyl)- (diphenylmethyl)silane in 50 mL of ether were added 14.1 mL of 2.285 M (32.2 mmol) of n-butyl lithium in hexanes. There was vigorous gas evolution and the reaction solution darkened to an orange-red color. The reaction mixture was stirred overnight. The bright orange precipitate which had formed was filtered off, washed with hexane, then dried under vacuum. The yield of bright orange powder was 2.213 g, 44.5 percent. Additional butyl lithium solution (2 - 3 mL) was added to the filtrate, which was then stirred for several days. More precipitate gradually formed. It was isolated as above to give 0.916 g additional product. Total yield was 3.13 g, 62.9 percent. Preparation of (N-t-butylamido)(dimethyl)(diphenylmethyl)silanetitanium (III) chloride Solid dilithium(N-t-butylamido)(dimethyl)(diphenylmethyl)silane (0.712 g, 2.30 mmol) was mixed with 0.853 g (2.30 mmol) of solid TiCl3* 3THF in a flask to which 50 mL of THF was then added. A color change in the solution was noted. The reaction product was subsequently utilized to prepare (N-t-butylamido)- (dimethy (diphenylmethyl)silanetitanium (IV) dichloride by metal center oxidation using PbCl2 oxidant which was subsequently used for a polymerization reaction. Polymerization A two liter stirred reactor was charged with 750 g of Isopar E™ solvent and 110 g of 1-octene. The reactor was heated to 140 °C and saturated with ethylene at 3.4 MPa (500 psi). Catalyst and cocatalyst were mixed in a dry box by combining 0.6 mL of a 0.005M toluene solution of (N-t-butylamido)(dimethyl)- (diphenylmethyl)silanetitanium (IV) dichloride (3.0 μmole) and 2.0 mL of a 1.5 M toluene solution of methylalumoxane (3000 μmole). The resulting solution was transferred to a catalyst addition tank and injected into the reactor. The polymerization was allowed to proceed with ethylene being added on demand. After 10 minutes the polymer solution was removed from the reactor. A hindered phenol antioxidant (Irganox™ 1010 available from Ciba Geigy Corp.), 100 mg, was added. Volatiles were removed under reduced pressure in an oven at about 130 °C for approximately 18 hours. Yield was 1.1 g of ethylene/ 1-octene copolymer.

Claims: WHAT IS CLAIMED IS: 1. A metal complex corresponding to the formula : z — Y / / x x' < L M X wherein: M is a Group 3, Group 4 or Lanthanide metal in the + 3 formal oxidation state; L is a group containing a cyclic or noncyclic, non-aromatic, anionic, dienyl ligand group bound to M and Z, said L group containing up to 60 nonhydrogen atoms, and being selected from the group consisting of 2,4- dimethylpentadienyl-, 1,5-dimethylpentadienyl-, silyl substituted pentadienyl-, si lyloxy substituted pentadienyl-, hydrocarbyloxy substituted pentadienyl-, cyclohexadienyl-, cyclosilahexadienyl-, cycloheptadienyl-, cyclooctadienyl-, diphenyl-q5-methyl-, and di(1-cyclohexenyl)-q5-methyl- groups, and inertly substituted derivatives of such cyclohexadienyl-, cyclosilahexadienyl-, cycloheptadienyl-, cyclooctadienyl-, diphenyl-q5-methyl- and di(1- cyclohexenyl)-q5-methyl- groups; Z is a moiety covalently bound to both L and Y, comprising boron, or a member of Group 14 of the Periodic Table of the Elements, said moiety having up to 60 non-hydrogen atoms; Y is a moiety comprising nitrogen, phosphorus, sulfur or oxygen through which Y is covalently bound to both Z and M, said moiety having up to 20 nonhydrogen atoms; X' independently each occurrence is a Lewis base containing up to 40 nonhydrogen atoms; X is a monovalent anionic moiety having up to 20 non-hydrogen atoms, provided however that X is not an aromatic group that is π-bonded to M and optionally X and one or more X' groups may be bonded together thereby forming a moiety that is both covalently bound to M and coordinated thereto by means of Lewis base functionality; and q is a number from 0 to 3. 2. A metal complex according to Claim 1 wherein L corresponds to the formula: wherein: R' in each occurrence is a ligand that is independently selected from the group consisting of hydrogen, hydrocarbyl, silyl, germyl, siloxy, amino, hydrocarbyloxy, cyano, halo and combinations thereof, said R' having up to 20 non-hydrogen atoms, and optionally, two or more R' groups (where R' is not hydrogen, halo or cyano) may together form a divalent derivative of one of the foregoing ligands; and provided further that one R' comprises a covalent bond to Z. 3. A metal complex according to Claim 1 wherein L is selected from the group consisting of divalent derivatives of 2,4-dimethylpentadien-3- yl, cyclohexadienyl, cyclosilahexadienyl, cycloheptadienyl, and cyclooctadienyl groups; hydrocarbyl, silyl, hydrocarbyloxy and siloxy substituted derivatives of such groups; partially hydrogenated anthracenyl, and partially hydrogenated naphthalenyl groups; and hydrocarbyl, silyl, hydrocarbyloxy or siloxy substituted derivatives of such partially hydrogenated anthracenyl and partially hydrogenated naphthalenyl groups. 4. A metal complex according to claim 1 corresponding to the formula: z — Y / / L M X wherein : Y is -O-, -S-, -NR * -, -PR * -; Z is SiR * 2 , CR* 2 , SiR* 2 SiR * 2 , CR * 2 CR * 2 , CR * = CR*, CR * 2 SiR * 2 , CR * 2 CR * 2 CR * 2, CR* 2 SiR * 2 CR * 2 , SiR * 2 CR * 2 CR * 2 , SiR * 2 CR * 2 SiR * 2 , SiR * 2 SiR * 2 CR * 2 , SiR*2SiR*2SiR*2, or GeR*2," wherein: R * each occurrence is independently hydrogen, or a member selected from hydrocarbyl, silyl, halogenated alkyl, halogenated aryl, and combinations thereof, said R* having up to 18 non-hydrogen atoms, and optionally (when R* is not hydrogen), two R * groups from Z , or an R* group from Z and an R* group from Y form a ring system. M is titanium, scandium, yttrium or lanthanium in the + 3 formal oxidation state; L is a divalent derivative of a 2,4-dimethyl-q- -pentadien-3-yl, cyclohexadienyl, cyclosilahexadienyl, partially hydrogenated naphthalenyl, partially hydrogenated anthracenyl group or a hydrocarbyl or silyl substituted derivative of such cyclohexadienyl, cyclosilahexadienyl, partially hydrogenated naphthalenyl, partially hydrogenated anthracenyl group, each said hydrocarbyl or silyl substituent having up to 10 nonhydrogen atoms; and X is chloro, allyl or an N, N-dialkylamino substituted hydrocarbyl group, said X having up to 12 non-hydrogen atoms. 5. A metal complex according to claim 1, corresponding to the formula: (ER" 2 ) m -N-R'" M wherein: E is independently each occurrence silicon or carbon. R" is independently each occurrence hydrogen or CMO hydrocarbyl; R'" is an aryl, benzyl, hydrocarbyl substituted aryl, hydrocarbyl substituted benzyl, secondary or tertiary alkyl or tertiary silyl group of up to 12 nonhydrogen atoms; M is titanium in the + 3 formal oxidation state; m is an integer from 1 to 3; L is a (2,4-dimethylpentadien-3-yl), (6,6-disubstituted-q5- cyclohexadien-3-yl), (6,6-disubstituted-q->-cyclosilahexadien-3-yl), (1, 2, 3, 4, 5-q- cydohexadien-6-yl), (6-substituted-1, 2, 3, 4, 5-q-cyclohexadien-6-yl), (1 , 2, 4, 5, 6, 6-hexasubstituted-q- -cyclohexadien-3-yl)-, (1, 1-disubstituted-q5-hexahydro- naphthalen-4-yl), (1, 1, 2, 3-tetrasubstituted-q5-hexahydronaphthalen-4-yl), or (9, 9-disubstituted-10, 11, 12, 13, 14-q-1, 2, 3, 4, 5, 6, 7, 8, 9, 10- decahydroanthracene-10-yl), group said substituents independently each occurrence being hydrocarbyl, hydrocarbyloxy, silyl, siloxy or a mixture thereof of up to 10 nonhydrogen atoms each; X is chloro or allyl, and X' is THF or MgCI; or X and X' together is 2- (N,N-dimethylamino)benzyl. 6. A metal complex according to claim 5 selected from the group consisting of : (tert-butylamido)(dimethyl)(2,4-dimethyl-q5-pentadien-3- yOsilanetitanium (III) chloride • MgCI; (tert-butylamido)(dimethyl)(2,4-dimethyl- q 5 -pentadien-3-yl)silanetitanium (III) 2-(N,N-dimethylamino)benzyl; (tert-butyl- amido)(dimethyl)(2,4-dimethyl-q5-pentadien-3-yl)silanezirconium (III) methyl • THF; (tert-butylamido)(dimethyl)(2,4-dimethyl-q5-pentadien-1- yOsilanezirconium (III) methyl; (tert-butylam!do)(dimethy!)(2,4-dimethyl-q5- pentadien-3-yl)silanezirconium (III) (q3-propenyl); (tert-butyl- amido)(dimethyl)(2,4-dimethyl-q5-pentadien-3-yl)silanezirconium (III) 2-(N,N- dimethylamino)benzyl; (tert-butylamido)(dimethyl)(1,5-bis(trimethylsilyl)-2,4- dimethyl-q--pentadien-3-yl)silanetitanium (III) chloride • MgCI; (tert-butyl- amido)(dimethyl)(1,5-bis(trimethylsilyl)-2,4-dimethyl-q5-pentadien-3- yOsilanetitanium (III) 2-(N,N-dimethylamino)benzyl; (tert-butyl- amido)(dimethyl)(1 ,5-bis(trimethylsilyl)-2,4-dimethyl-q5-pentadien-3- yOsilanezirconium (III) chloride . THF; (tert-butylamido)(dimethyl)(1 ,5- bis(trimethylsilyl)-2,4-dimethyl-q5-pentadien-3-yl)silanezirconium (III) 2-(N,N- dimethylamino)benzyl; (tert-butylamido)(dimethyl)(6,6-dimethyl-q5- cyclohexadien-3-yl)silanetitanium (III) chloride • MgCI; (tert-butyl- amido)(dimethyl)(6,6-dimethyl-q5-cyclohexadien-3-yl)silanetitanium (III) 2- (N,N-dimethylamino)benzyl; (tert-butylamido)(dimethyl)(6,6-dimethyl-q5- cyclosilahexadien-3-yl)silanetitanium (III) (q3-propenyl); (tert-butyl- amido)(dimethyl)(6,6-dimethyl-q5-cyclosilahexadien-3-yl)silanetitanium (III) 2- (N,N-dimethylamino)benzyl; (tert-butylamido)(dimethyl)(6,6-dimethyl-q5- cyclohexadien-3-yl)silanezirconium (III) chloride • MgCI; (tert-butyl- amido)(dimethyl)(6,6-dimethyl-q5-cyclohexadien-3-yl)silanezirconium (III) 2- (N,N-dimethylamino)benzyl, (tert-butylamido)(dimethyl)(6,6-dimethyl-q5- cyclosilahexadien-3-yl)silanezirconium (III) methyl .THF; (tert-butyl- amido)(dimethyl)(6,6-dimethyl-q5-cyclosilahexadien-3-yl)silanezirconium (III) 2- (N,N-dimethylamino)benzyl, (N-tert-butylamido)(dimethyl)(2, 3, 4, 9, 10-q-1,2- dihydronaphthalen-4-yl)silanetitanium (III) 2-(N,N-dimethylamino)benzyl; (N- tert-butylamido)(dimethyl)(1, 1-dimethyl-2, 3, 4, 9, 10-q-1,4- dihydronaphthalen-4-yl)silanetitanium (III) 2-(N,N-dimethylamino)benzyl; (N- tert-butylamido)(dimethyl)(2, 3, 4, 9, 10-q-1,2, 5, 6, 7, 8-hexahydronaphthalen- 4-yl)silanetitanium (III) methyl; (N-tert-butylamido)(dimethyl)(1,1-dimethyl-2, 3, 4, 9, 10-q-1,2, 5, 6, 7, 8-hexahydronaphthalen-4-yl)silanetitanium (III) 2-(N,N- dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(9, 9-dimethyl-10, 11, 12, 13, 14-q-9,10-dihydroanthracen-10-yl)silanetitanium (III) 2-(N,N- dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(9,9-dimethyl-10, 11, 12, 13, 14-q-1 , 2, 3, 4, 9,10-hexahydroanthracen-10-yl)silanetitanium (III) 2-(N,N- dimethylamino)benzyl; (N-tert-butylamido)(dimethyl)(9, 9-dimethyl-10, 11, 12, 13, 14-q-1, 2, 3, 4, 5, 6, 7, 8, 9,10-decahydroanthracen-10-yl)silanetitanium (III) 2-(N,N-dimethylamino)benzyl, and (N-tert-butylamido)(dimethyl)(9, 9- dimethyl-10, 11, 12, 13, 14-q-1, 2, 3, 4, 5, 6, 7, 8, 9,11-decahydroanthracen-10- yOsilanetitanium (III) (q3-propenyl). 7. A catalyst composition comprising a metal complex according to any one of claims 1 to 6 and an activating cocatalyst selected from the group consisting of polymeric or oligomeric alumoxanes; neutral Lewis acids; nonpolymeric, compatible, noncoordinating, ion forming compounds; and combinations thereof. 8. A polymerization process comprising contacting an addition polymerizable monomer with a catalyst under polymerization conditions characterized in that the catalyst comprises a catalyst composition according to claim 7.

Inventors: KRUPER W JACK JR, NEITHAMER DAVID R, NICKIAS PETER N, WILSON DAVID R, KRUPER, W., JACK, JR., NEITHAMER, DAVID, R., NICKIAS, PETER, N., WILSON, DAVID, R.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1995
Main classification: C07F7
IPC codes: C07F5, C07F7, C07F13, C07F17, C08F4, C08F10