Multi-layer structural body

Abstract: The present invention provides a multi-layer structural body, comprising: a first layer 1 of which oxygen permeability is less than 100cc/m²·day·atm (23°C, 100%RH) and which is resistant to gas permeation; a second layer 2 which comprises resin, of which the oxygen permeability coefficient is 200cc·0.1mm/m²·day·atm (23°C, 100%RH) or more, and a granular oxygen absorber, which is dispersed in the resin and which contains an oxygen absorber composition which exhibits a deoxidization reaction when moisture is supplied thereto, such second layer being laminated over the first layer 1 and having a deoxidizing property; and a third layer 3 of which oxygen permeability is 100cc/m²·day·atm (23°C, 100%RH) or more, which is laminated over the second layer 2, and which is permeable to air. This multi-layer structural body itself has an oxygen absorbing performance and is capable of actively and efficiently absorbing oxygen just like a conventional small bag which contains an oxygen absorber composition, without any special treatment such as heat treatment.

Description: The present invention relates to a multi-layer structural body which is obtained by forming and processing resin. More particularly, the present invention relates to a multi-layer structural body which has a superior oxygen absorbing function and superior resistance to gas permeation, and which can be used as a packing material, for example, for food and medicines. Moreover, the present invention relates to a method for manufacturing this multi-layer structural body, and to a container which is made of the multi-layer structural body. As the technology for preventing a substance to be preserved, such as food and medicine, from suffering, for example, oxidation, deterioration, discoloration, generation of molds, propagation of aerobic bacterium, and vermin damages, the method of placing the substance to be preserved, together with an oxygen absorber, in a package which is resistant to gas permeation has been used. A widely used type of oxygen absorber is an air-permeable, small bag containing an oxygen absorber composition in a powder or granular form. In this specification, the air-permeable, small bag containing the oxygen absorber composition may be called the "small bag containing the oxygen absorber composition" or simply the "small bag." The expression "resistance to gas permeation" or variant expressions thereof used in this specification of the present invention means the property of allowing no gas or a very small amount of gas to permeate through. However, if the small bag containing the oxygen absorber composition is placed in a package together with a substance to be preserved, the small bag will get mixed with the preserved substance. If the small bag is mixed with the preserved substance, there is a possibility that the small bag may be mistakenly cooked or eaten with the preserved substance. Moreover, such state of the small bag may give a user a strange feeling that some foreign stuff is mixed in, or a user may feel reluctant to use the preserved substance. Furthermore, if a user makes a mistake in handling the small bag and breaks it, the oxygen absorber composition running out of the small bag may contaminate the preserved substance. Therefore, recently, it has been attempted to construct a package made of a packing material which has a deoxidizing performance in order to give the oxygen absorbing performance to the package itself. As examples of the above-described construction, as disclosed in the official gazettes of the Japanese Patent (Kokoku) Publication No. SHO 62-1824, the Japanese Patent Laid-Open (Kokai) Publication No. SHO 57-146651, the Japanese Patent Laid-Open (Kokai) Publication No. HEI 4-45152, and the Japanese Patent Laid-Open (Kokai) Publication No. HEI 4-90848, there are films or sheets of multi-layer construction including a layer in which an oxygen absorber composition is dispersed in resin. Moreover, the official gazette of the Japanese Patent (Kokoku) Publication No. HEI 4-60826 discloses a packing container made of thermoplastic resin which is resistant to gas permeation and which contains an oxygen absorber composition sold on the market. The official gazette of the Japanese Patent (Kokoku) Publication No. HEI 4-62858 discloses a container including a material which exhibits its oxygen acquisition function only when it is exposed to high temperatures and high water vapor pressure in a retort treatment. These official gazettes of the Japanese Patent (Kokoku) Publication No. HEI 4-60826 and the Japanese Patent (Kokoku) Publication No. HEI 4-62858 disclose the technology for restraining the resistance to oxygen permeation of the gas-permeation-resistant resin from lowering at the time of a retort treatment, thereby preventing oxygen from leaking into the container from outside. However, compared to the prior art in which the small bag is placed together with the preserved substance in a package, the prior art in which the package itself is given the oxygen absorbing performance, is extremely inferior in its oxygen absorbing performance and there is a problem that oxygen existing in the package cannot be removed efficiently in a short period of time. As for the above-mentioned multi-layer structural body, if the oxygen-free absorber composition contained in the small bag is simply kneaded into resin, there exists resin between each component particle of the oxygen absorber composition and, therefore, it is very difficult for the particles of the oxygen absorber composition to directly contact each other. Moreover, oxygen and water, etc. which are involved in the oxygen absorption reaction cannot move to and from the particles of the oxygen absorber composition without passing through molecules of the resin. This is a material factor which hinders the progress of the oxygen absorption reaction, resulting in a problem that sufficient speed of the oxygen absorption reaction cannot be obtained. Also, since the composition cannot be dispersed well in resin, it is possible to blend the composition in a very large proportion to the amount of resin so that the composition will contact the resin sufficiently. However, this may cause many problems in the formation of the resin. It is necessary to try to enhance the oxygen absorbing capability of a multi-layer structural body by improving the blending of the oxygen absorber composition, the construction of the members of the multi-layer structural body, etc. However, if a multi-layer structural body with a strong oxygen absorbing capability is used, there is a problem that its oxygen absorbing capability will gradually lower during the storage period of a package (such as a container, lid, or bag) molded from the multi-layer structural body, before it is actually used. Of course, if the multi-layer structural body itself is stored in atmospheric air for a long time, not only the oxygen absorbing performance lowers, but also it results in the problem that when such multi-layer structural body is molded into a package by a thermoforming method such as sheet forming, vacuum forming, or pressure forming, the multi-layer structural body bubbles at the time of thermoforming and the surfaces of the multi-layer structural body become uneven. The above-described problems are caused because the oxygen absorption reaction requires moisture and the oxygen absorber composition tends to easily take in moisture which is essential to the reaction. There is another problem in that high oxygen absorbing performance cannot be acquired without using an oxygen absorber composition which easily takes in moisture and has a strong hygroscopic property. Accordingly, as the oxygen absorbing performance of the multi-layer structural body increases, the multi-layer structural body becomes capable of absorbing oxygen more easily. Hence, after the multi-layer structural body is molded into a final usage form, it absorbs oxygen even with a very small amount of moisture absorbed, thereby lowering the oxygen absorbing capability. As another cause for the moisture absorption of the multi-layer structural body, there is the factor that component members of the multi-layer structural body also absorb moisture, although the effect is less than in the case of the oxygen absorber composition. If ethylene-vinyl-alcohol-copolymer or various kinds of nylon films which have a hygroscopic property are used as gas-permeation-resistant materials in the multi-layer structural body, there is the problem that the moisture absorbed during the storage period of the multi-layer structural body will hinder the thermoforming processing of the multi-layer structural body. As a measure for solving the above-described problems due to moisture absorption of the multi-layer structural body, it is possible to pack the multi-layer structural body by utilizing, for example, metallic can sealing technology, of which resistance to gas permeation is said to be perfect, or heat sealing technology with the use of a heat sealing bag with metallic foil layers. However, the films or sheets in the multi-layer structure are often stored, for example, in a wound roll which weighs hundreds of kilograms. Therefore, there are many problems in strength, workability, and the necessary facilities. Moreover, when the multi-layer structural body is formed in the shape of, for example, a container, it is bulky and, therefore, it may contain a large amount of air when it is packed, it is therefore inefficient. In addition, since the shape is complicated, there is the possibility that pin holes may be generated if the multi-layer structural body is packed in a gas-permeation-resistant bag. In addition, there are other problems such as bad workability and high cost. As another measure to solve the problems, it may be possible to place a desiccant such as silica gel or zeolite in a package together with the multi-layer structural body. However, in this case, this approach is not effective at all. The desiccant works effectively only when the substance to be placed in a package together with the desiccant has a much weaker hygroscopic property than that of the desiccant, or when moisture absorbed by the substance is absorbed again by the desiccant. In this case, however, the oxygen absorber composition has a strong hygroscopic property and the moisture, once absorbed, will be consumed in a chemical reaction. Therefore the desiccant does not work effectively. EP 0402217 discloses a multi-layer film including an oxygen absorbing material sandwiched between one layer that is oxygen impermeable and another layer that is oxygen permeable. EP 0466515 discloses an oxygen scavenger having an oxygen absorbent composition, an oxygen permeable film covering the oxygen absorbent composition and a back side laminate having gas barrier property. According to this European patent, the oxygen absorbent may contain other substances such as a catalyst, a water retentive agent and a hydrate. EP 0546903 discloses a multi-layer film comprising a plastic, gas-permeable sheet and an outer film having at least one layer impermeable to air. The internal layer and the film are bonded to one another by applying an adhesive layer containing an oxygen absorber to one face of one of the sheet or film and applying an adhesive layer containing an oxidation absorber activator to one face of the other of the sheet or film, and applying the two faces together. The present invention aims to solve the above-described problems. An objective of the invention is to provide a multi-layer structural body which has the function to absorb oxygen actively and efficiently just like a conventional small bag containing the oxygen absorber composition. Another objective of the invention is to provide a multi-layer structural body with improved thermoforming capability. A further objective of the invention is to provide a multi-layer structural body with improved preservability, which does not exhibit its oxygen absorbing capability until it is actually used. Still another objective of the invention is to provide a method of easily enabling the manufacture of the multi-layer structural body which attains the above-described objectives. Moreover, an objective of the invention is to provide a package made of the aforementioned multi-layer structural body. The present invention provides a multi-layer structural body, comprising a first layer which is resistant to gas permeation, a second layer which is laminated over said first layer and which has a deoxidizing property; and a third layer which is laminated over said second layer and which is permeable to oxygen, wherein the oxygen permeability of said first layer is less than 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH), wherein said second laver comprises resin of which the oxvgen permeability coefficient is 200cm 3 ·0.1mm/m 2 ·d·1.01x10 5 N/m 2 (cc•0.1mm/m 2 •day•atm) (23°C, 100%RH) or more, a granular oxygen absorber which is dispersed in the resin and which contains an oxygen absorber composition which exhibits a deoxidization reaction when moisture is supplied thereto, and calcium oxide as moisture absorber, and wherein the oxygen permeability of said third layer is 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH) or more. The present invention further provides a method for manufacturing a multi-layer structural body, comprising the step of simultaneously extruding a first material which is resistant to gas permeation, a second material which has a deoxidizing property, and a third material which is permeable to air, thereby forming a multi-layer laminated body in which layers are laminated in the order of a first layer made of the first material, a second layer made of the second material, and a third layer made of the third material, wherein said second material is manufactured by a method comprising the steps of kneading a granular oxygen absorber and calcium oxide as moisture absorber in resin, which oxygen absorber contains an oxygen absorber composition which exhibits a deoxidation reaction when moisture is supplied thereto. The present invention yet further provides a package made of a multi-layer structural body which comprises a first layer which is resistant to gas permeation, a second layer which is laminated over said first layer and which has a deoxidizing property, and a third layer which is air permeable and laminated to said second layer, wherein the oxygen permeability of said first layer is less than 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH), wherein said second layer comprises a resin having an oxygen permeability coefficient of at least 200cm 3 ·0.1mm/m 2 ·d·1.01x10 5 N/m 2 (cc•0.1mm/m 2 •day•atm) (23°C, 100%RH) , a granular oxygen absorber composition dispersed in the resin and including a deoxidization material undergoing a deoxidization reaction when exposed to moisture, and calcium oxide as moisture absorber dispersed in said resin, wherein the oxygen permeability of said third layer is at least 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH), and wherein said first layer forms the outside wall of the package, and said third layer forms the inside wall of the package. The inventors of the present invention made, as a form of the oxygen absorber composition to be mixed in the resin, all the components of the oxygen absorber composition, excluding moisture, contained in one grain of the oxygen absorber composition, thereby solving the aforementioned problems in the prior art. In accordance with the preferred embodiment the inventors of the present invention blended, as a form of the oxygen absorber composition to be mixed in the resin, all the oxygen absorbing components, which exhibit a deoxidation reaction when moisture is supplied thereto, in one grain of the oxygen absorber composition, thereby succeeding in making the oxygen absorption reaction progress without any obstacles and in obtaining a practical oxygen absorbing speed. Moreover, the hygroscopic property becomes stronger as the oxygen absorbing speed increases, which results in various problems such as bubbling, at the time of thermoforming, of the multi-layer structural body after being stored, and lowering of the oxygen absorbing function. The inventors of the present invention have solved these problems by adding calcium oxide as an alkaline earth metal oxide, thereby succeeding in enhancing the preservability of the multi-layer structural body. Furthermore, the inventors of the present invention discovered that formability under special thermoforming conditions can be improved by controlling the softening state of the resin. They also discovered a resin composition which makes the multi-layer structural body absorb oxygen faster and which also enhances its appearance. Accordingly, they remarkably improved the practical functions of the multi-layer structural body in a sheet form and resolved the aforementioned conventional problems. The resin composing a second layer (the layer containing the oxygen absorber composition) itself is required to be permeable to oxygen (oxygen permeability coefficient: 200cm 3 ·0.1mm/m 2 ·d·1.01x10 5 N/m 2 (cc•0.1m/m 2 •day•atm) (23°C, 100%RH) or more) in order to allow the oxygen within the package to efficiently reach the oxygen absorber composition. When the multi-layer structural body is formed into the package in the shape of a container or bag, a first layer which forms the outside wall of the package is required to have the performance of preventing oxygen from penetrating into the package from outside. Moreover, the third layer which forms the inside wall of the package is required to have the performance of impeding the direct contact of the second layer with the preserved substance and of performing rapid and efficient oxygen permeation. Namely, the first layer is required to have as small an oxygen permeability as possible (oxygen permeability: less than 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH), while the third layer is required to have as large oxygen permeability as possible (oxygen permeability: 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH) or more). The construction of the first and third layers is not limited to a single layer construction, but can be a multi-layer construction including, for example, adhesive layers. Moreover, when an inside bag is additionally placed inside of the package, or when the package is further wrapped with a film or a case, it is necessary to determine the oxygen permeability of the first and third layers in consideration of the layer construction. The multi-layer structural body with the oxygen absorbing performance of the present invention in the above-described construction has a sufficient oxygen absorbing function and is capable of exhibiting its function without any special treatment such as high temperature treatment, just like when a conventional small bag containing the oxygen absorber composition is used. Even if heat sterilization, retort treatment, high temperature packing (hot bag) of the preserved substance, etc. are performed after the preserved substance is placed in the package formed of the multi-layer structural body, such performance does not hinder the preservation of the substance at all. Furthermore, if the environmental temperature rises, the speed of the oxygen absorption reaction and the oxygen permeability of the first and second layers also increases, thereby resulting in a more rapid oxygen absorbing function. The first layer forms the outermost layer of the package when the package is manufactured by using the multi-layer structural body of the present invention. This first layer consists of one or more layers. Regardless of the film thickness of each layer and the existence of adhesives, the first layer is required to have an oxygen permeability less than 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH). More preferably, it is desirable that the oxygen permeability of the first layer is 50cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH) or less. Namely, it is desirable to make the oxygen permeability of the first layer as low as possible within the allowable range concerning the processing steps, costs and other factors. When the package is manufactured by using the multi-layer structural body of the present invention, such small oxygen permeability of the first layer makes it possible to reduce the amount of oxygen permeating into the package from outside and to reduce the amount of oxygen absorber composition to be used. Moreover, the oxygen absorbing performance of the package can be maintained even longer. As examples of the resin which composes the first layer, the following types of resin can be preferably used: polyolefine such as polyethylene and polypropylene, and modified forms thereof; polyester such as polyethylene terephthalate; polyamide such as nylon 6, nylon 66, and MX nylon; and ethylene-vinyl-alcohol-copolymer, polyvinyl chloride, and polyvinylindene chloride. The first layer may be made in a single layer or in multiple layers in combination with layers made of the above-mentioned resin. Resin made by orientation processing may also be used. Moreover, it is possible to mix additives such as fillers, coloring agents, antistatic agents, and stabilizers in the first layer. Specifically, mixing coloring agents such as dyestuffs and pigments in the resin which composes the first or third layer conceals the second layer, makes the appearance of the package tidy and, therefore, is important because it makes the package marketable. The first layer can be formed in methods such as simultaneous extrusion, lamination, thermal shrink packaging, wrap packaging, and outside bag packaging. In the case of simultaneous extrusion, the first layer and the second layer may be extruded together. Moreover, the first layer and the second layer may be glued to each other via an adhesive layer. As examples of the oxygen absorber composition dispersed in the resin which forms the second layer, a granular reductive substance, which is the main component, of which surface is coated with catalysts or assistants, or a granular form of the mixture produced by mixing and then grinding the reductive substance, which is the main component, and all other components of the oxygen absorber composition, can be preferably used. As for the reductive substance, which is the main component, metal powder (such as iron powder, aluminum powder and silicon powder), inorganic salts (such as ferrous salt and dithionite), ascorbic acid and salt thereof, catechol, and glycerin, etc. are preferable. This main component is ground with other components and is used as the oxygen absorber composition in a granular form. Among others, it is preferable to use: metal powder with metal halide attached to the surface of the metal powder; granules of metal powder, metal halide and, if necessary, other additives, all of which granulated with a binder; and an inorganic carrier obtained by making it absorb an alkali aqueous solution of ascorbic acid and by drying it. As the aforementioned metal powder, metal iron is preferable. There are no special limitations, such as purity, on metal iron as long as it is capable of generating the aforementioned oxygen absorption reaction and can be dispersed in the thermoplastic resin. Even if a portion of the metal iron is already oxidized or if it is an alloy with other kind of metals, such metal iron is available. Preferable examples of the metal iron are: iron powder represented by reduced iron powder, atomized iron powder, and electrolytic iron powder; ground powder of various kinds of iron products, such as iron powder scattered, that is, turning, when manufacturing cast iron, cast iron, and powder of steel products; and ground articles. A preferable form of metal powder is a fine grain or fiber form. In the case of the metal iron in a fine grain form, when the metal iron grains are dispersed in the thermoplastic resin to form the second layer, a small size of grain is preferable because the film thickness of the second layer can be made thin and the surfaces can be made flat and smooth. Specifically, it is preferable to use metal iron grains with an average grain diameter of 200 µm or shorter, and more preferably of 50 µm or shorter. In the case of the metal iron in a fiber form, it is preferable to have the diameter of the metal iron fiber as short as possible because of the same reason as described above. A metal halide in the thermoplastic resin functions as a catalyst in the oxygen absorption reaction of the metal iron. As the metal, at least one of the following metals should be selected: alkali metal, alkaline earth metal, copper, zinc, aluminum, tin, iron, cobalt, or nickel. Specifically, lithium, potassium, sodium, magnesium, calcium, and barium iron are preferable. Examples of halogens are chlorine, bromine, and iodine, among which chlorine is specifically preferable. It is preferable to add the metal halide by methods such that the metal halide will not easily separate from the metal iron in the thermoplastic resin. For examples, the following methods are specifically preferable: the method of grinding and mixing the metal halide by using a machine such as a bowl mill or a speed mill, and of filling a recess on the surface of the metal iron with fine grains of the metal halide; the method of attaching fine grains of the metal halide to the surface of the metal iron by using a binder; and the method of mixing and drying a metal halide aqueous solution and the metal iron and of attaching the fine grains of the metal halide to the surface of the metal iron. In order to confirm that the metal iron and the metal halide are not separated from each other in the thermoplastic resin, it is preferable to conduct an analysis with an electron photo-microanalyser. If component elements of both the iron and the metal halide exist as SEM images in a grain of the metal iron observed by the electron photo-microanalyser, the above-described objective can be considered to have been accomplished. A preferable amount of the metal halide to be added to 100 parts by weight of the metal iron is 0.1-20 parts by weight. When essentially the entire amount of the metal halide is attached to the metal iron, and when almost no metal halide is free in the thermoplastic resin, 0.1-5 parts by weight of the metal halide is enough for effective functioning. A granular oxygen absorber composition to be dispersed in the resin forming the second layer is a moisture-dependent type which exhibits a deoxidation reaction when moisture is supplied to it. A desirable initial content of moisture in the oxygen absorber composition is 0.2 wt% or less, and more preferably 0.1 wt% or less. As for the grain diameter, a preferable average grain diameter is 5-200 µm, and more preferably 5-50 µm. Moreover, it is possible to add, other than the oxygen absorber composition, the following additives in the second layer as needed: coloring agents such as organic or inorganic dyestuffs and pigments; dispersing agents such as those of silane or titanate type; water absorptive agents such as polyacrylic-type compounds; fillers such as clay, mica, silica, and starch; and gas absorber such as zeolite and activated carbon. As for the resin which forms the second layer and in which the granular oxygen absorber composition is dispersed, the following substances are preferable and resin mixtures of the following may also be used: polyolefin such as polyethylene, polypropylene, polybutadiene, and polymethyl pentene, and modified forms thereof; or thermoplastic resin such as graft polymer with silicon resin, ionomer, elastomer, polycarbonate, and polyurethane. A compounding ratio of the oxygen absorber composition in the second layer should preferably be 2-93 wt%, and more preferably 10-70 wt%. If the compounding ratio is too low, the oxygen absorbing performance lowers. On the other hand, if the compounding ratio is too high, the processibility of the multi-layer structural body lowers. It is desirable to make the film thickness of the second layer 1000 µm or less, and more preferably 500 µm or less. The third layer is the innermost layer of the package when the package is manufactured by using the multi-layer structural body of the present invention. The third layer consists of one or more layers. Regardless of the film thickness of each layer or the existence of adhesives, the third layer is required to have the oxygen permeability of 100 cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH) or more. More preferably, it is desirable to have an oxygen permeability of 200 cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH) or more. Namely, it is desirable to have the oxygen permeability of the third layer as high as possible within an allowable range concerning the processing steps, costs, and other factors. When a package is manufactured by using the multi-layer structural body of the present invention, and when a substance to be preserved is placed in the package, such high oxygen permeability makes it possible to make oxygen and moisture existing in the package penetrate through the third layer and reach the second layer rapidly, Accordingly, oxygen existing in the package can be efficiently and rapidly absorbed by the second layer. As examples of the resin which forms the third layer, the following substances can be preferably used: polyolefin such as polyethylene, polypropylene, polybutadiene, and polymethyl pentene, and modified forms thereof; or graft polymer with silicon resin; polyester such as polyethylene terephthalate; polyamide such as nylon 6 and nylon 66; and synthetic resin such as ionomer and elastomer. This third layer may be constructed in a single layer or multiple layers in combination with the aforementioned resin layers. Moreover, the third layer may be a mixed resin layer in which the aforementioned different kinds of resins are mixed together. Furthermore, a microporous film of the aforementioned resin on which micropores are formed, or nonwoven cloth may also be used as the third layer. It is also possible to mix additives such as fillers, coloring agents, antistatic agents, and stabilizers in the third layer. The third layer can be formed by methods such as simultaneous extrusion, lamination, inside bag packaging. In the case of simultaneous extrusion, the third layer may be extruded together with the second layer. If necessary, the third layer and the second layer may be glued to each other via an adhesive layer. When the multi-layer structural body of the present invention is thermoformed into a package in the shape of, for example, a tray or cup, if the heating temperature is set low in order to enhance the molding cycle, to maintain the appearance and transparency of the multi-layer structural body, and for other purposes, the third layer, which is the innermost layer of the package, sometimes becomes slightly uneven, depending on the heating method of the molding machine. This unevenness takes place because of the following reason: since in the second layer a large amount of the oxygen absorber composition, which has strong thermal conductivity, is dispersed in the resin, the resin existing adjacent to this oxygen absorber composition is rapidly heated; therefore, the resulting differences in the softening property of the resin existing adjacent to the oxygen absorber composition and the resin existing at other positions, the second layer becomes uneven and then the third layer which has already softened takes over the unevenness of the second layer. In many cases, the film thickness of the third layer is made thinner than that of the first layer because of air permeability. Therefore, the third layer tends to more easily receive adverse effects due to the generation of the above-described unevenness. In the present invention, preferably the resin forming the second layer is made to soften at lower molding temperatures, thereby the above-described phenomenon can be prevented. For example, if polypropylene is used as the main component of the sheet, it is preferable to use ethylene-propylene-random-copolymer for the second layer. Moreover, in the case of other kinds of sheets, it is preferable to use, for the second layer, a resin which has a softening temperature no higher than that of the main component resin which controls the moldability at the time of thermoforming. When the second layer is constructed by dispersing the oxygen absorber composition, which contains metal iron and metal halide, and calcium oxide as an alkaline earth metal oxide in thermoplastic resin, the first step of the oxygen absorption reaction caused by the metal iron can be expressed in the following reaction formulas: Fe → Fe 2+ + 2e - H 2 O + 1/2 O 2 + 2e - → 2 (OH) - Fe + H 2 O + 1/2 O 2 + 2e - → Fe 2+ + 2e - + 2(OH) - In this case, environmental pH is important. If the alkaline level becomes higher, electron transfer reactions of the above chemical formulas (1) and (2) are hindered, thereby making the reactions hardly progress. On the other hand, oxides of the alkaline earth metal easily react with water and become strong alkaline hydroxides of the alkaline earth metal. If the oxygen absorber composition contains calcium oxide as an alkaline earth metal oxide, water to be used in the oxygen absorption reaction is used in the reaction which changes the alkaline earth metal oxide into a hydroxide. As a result, it becomes difficult for the oxygen absorption reaction to take place. Moreover, due to the alkaline property of the alkaline earth metal hydroxide formed, the reaction becomes inactive and the oxygen absorber composition no longer serves as an oxygen absorber. In the present invention, the oxygen absorber composition and calcium oxide as the alkaline earth metal oxide are separated from each other when dispersed in the resin. Therefore, even if the alkaline earth metal oxide becomes an alkaline earth metal hydroxide, ions hardly pass through the resin. Accordingly, the oxygen absorber composition itself does not become alkaline, and suffers almost no hinderance of the oxygen absorption reaction. Furthermore, this calcium oxide restrains the oxygen absorber composition from absorbing water while the multi-layer structural body is stored, that is, after the multi-layer structural body is molded in a final usage form and until it is actually used. Therefore, the oxygen absorber composition never exhibits its oxygen absorbing performance during the above-described storage period. Surprisingly, however, this invention prevents the oxygen absorber composition from absorbing water when the oxygen absorber composition is stored, and what is more, it never hinders the oxygen absorption reaction, which requires moisture, when the substance to be preserved is actually preserved. This is because the amount of moisture permeating into the multi-layer structural body is different during when the multi-layer structural body is stored and when it is actually used. Materials of the multi-layer structural body of the present invention, even when they are molded by an extrusion method, exhibit a moisture removal function in a cylinder of an extrusion molding machine. Accordingly, even if a little moisture or crystal water exist in the thermoplastic resin or in the oxygen absorber composition, the extrusion molding can be conducted without any trouble such as bubbling. Therefore, it is possible to enhance the preservability of the multi-layer structural body at the level of raw materials, that is, before it is actually used. The alkaline earth metal oxide to be mixed in the second layer is calcium oxide which has easy availability and good reactivity. It is also desirable to use this oxide in a grain form. Calcium oxide with 2-200 µm of average grain diameter is preferable, and 5-50 µm of average grain diameter especially preferable. Moreover, in order to make the film thickness of the second layer of the present invention thin, it is preferable to use calcium oxide with an average grain diameter equal or shorter than that of the metal iron. On the other hand, if the grain diameter is too short, there is a possibility that its hygroscopic property may be too strong, degrading the preservability and easiness in handling, and that the calcium oxide may be attached to the metal iron even in the thermoplastic resin. The second layer of the present invention can be obtained by mixing, kneading, and dispersing the oxygen absorber composition, which contains the aforementioned metal iron and metal halide, and the calcium oxide in the above-described thermoplastic resin. A preferable content of the metal iron in the second layer is 2-93 wt%. If the percentage content of the metal iron is low, sufficient oxygen absorbing capability cannot be obtained. On the other hand, if the percentage content of the metal iron is high, there is a tendency to lower the mechanical strength and formability of the second layer. Therefore, it is specifically preferable to utilize the metal iron in a proportion of 10-70 wt% in the second layer. Moreover, it is preferable that the second layer contains the calcium oxide in a proportion of 0.1-5 wt% (against the entire layer). If the percentage content of the calcium oxide is too low, a sufficiently improved effect of preservability cannot be obtained. On the other hand, if the percentage content of the calcium oxide is too high, there is a tendency to give an adverse effect to the oxygen absorbing performance when the multi-layer structural body is used. In order to mix the oxygen absorber composition and the calcium oxide in the thermoplastic resin, mixing or kneading can be performed by using an agitating-vane-type mixer, biaxial extrusion machine, etc. However, other methods may be chosen for the above purpose. It is also possible to select a master batch method of previously dispersing the oxygen absorber composition and the calcium oxide in the thermoplastic resin at high concentration and then kneading and extruding them, if necessary, with additional thermoplastic resin, by using a single axial extrusion machine or other similar machines. In the second layer, it is preferable that the oxygen absorber composition and the calcium oxide are isolated from each other by the thermoplastic resin. A preferable condition can be obtained relatively easily if the second layer is extruded by using an extrusion machine which provides sufficient dispersibility. However, attention should be paid to the mixing method when the percentage content of the oxygen absorber composition is high, and when a previously prepared mixture of the oxygen absorber composition and the calcium oxide is kneaded with the thermoplastic resin. As for the third layer which becomes an inside wall when a package is formed out of the multi-layer structural body of the present invention, the third layer should isolate the preserved substance to be placed in the package from the second layer and should have high air permeability. For this purpose, it is desirable that materials of the third layer are adhesive enough to be extruded together with materials of the second layer, and that the third layer is a thin single layer. In order to meet the above-described conditions, the resin forming the second layer should preferably contain either polyethylene or polypropylene in a proportion of 50% or more, and more preferably in a proportion of 60% or more. On the other hand, it is desirable that, when the resin forming the third layer is extruded together with the resin forming the second layer, the resin forming the third layer is a mixture of polyolefin (polyethylene, polypropylene, ethylene-propylene-copolymer, or a mixture thereof) which can be adhered to the resin forming the second layer, and poly-4-methyl-pentene-1 or resin which contains poly-4-methyl-pentene-1 as a main component. Poly-4-methyl-pentene-1 is a kind of polyolefin which is superior in gas permeability such as oxygen and vapor. This is advantageous to the enhancement of the air permeability of the third layer, while there is the disadvantage that it has poor adhesiveness with other resins. However, in the present invention, poly-4-methyl-pentene-1 is mixed with polyolefin such as polyethylene and polypropylene in certain proportion and, therefore, remarkably strong adhesiveness with other resins can be obtained. When the percentage content of poly-4-methyl-pentene-1 is 10-80 wt%, the miscibility of poly-4-methyl-pentene-l with polyolefin is poor. Therefore, the matrix obtained is lustrous like a pearl and has a high-grade appearance. At the same time, efficient enhancement of the oxygen permeability can be observed, which seems to be attributable to a morphological structure of the matrix, which structure consists of dispersed phases and continuous phases. When the percentage content of poly-4-methyl-pentene-1 is 50 wt% or less, its adhesiveness with the second layer containing polyethylene or polypropylene as a main component can be secured. In the present invention, the third layer may be composed of a mixture of two or more kinds of polyolefin, which mixture contains poly-4-methyl-pentene-1 or resin containing poly-4-methyl-pentene-1 as its main component in the proportion of 50 wt% or less. Thus the adhesiveness of the third layer with the second layer is secured, thereby enhancing the air permeability remarkably and realizing a third layer with a good appearance in a single layer construction. It is more preferable to compose the third layer of a mixture of two or more kinds of polyolefin , which mixture contains poly-4-methyl-pentene-1 or resin containing poly-4-methyl-pentene-1 as its main component in a proportion of 10-40 wt%. The thinner the film thickness of the third layer is, the more the air permeability of the third layer increases. However, as the third layer becomes thinner, its molding processibility and covering power lower, and the isolated condition of the second layer from the preserved substance becomes worse. Therefore, it is desirable to make the third layer 10-100 µm thick. It is possible to add dyestuffs or pigments to the third layer in order to cover or color the third layer, or to add various kinds of additives to the third layer in order to enhance its heat sealing property, etc. There are two ways of preparing a package of the multi-layer structural body of the present invention. One way is to first form the multi-layer structural body of the present invention and then mold it into a package. The other way is to directly form a package from the multi-layer structural body. In either way, known methods can be applied to the formation of the package, and various conventional means used in resin processing and container processing can be applied. For example, the package can be formed directly by utilizing known resin molding technology and processing, including extrusion molding with a T die or circular die, injection molding, direct blow molding, and orientation blow molding. It is also possible to form the package by using sheets, tubes, and parison obtained in the above-described methods and by performing vacuum forming, pressure forming, plug assist forming, bulge forming, or blow forming to form the package. Moreover, it is possible to form the main portion first, and then to combine it with other molded articles, or to perform various kinds of lamination such as heat lamination, dry lamination, extrusion lamination, or hot melt lamination, or to perform laminated processing such as coating. Furthermore, shrink packaging, shrink label packaging, or outside or inside packaging by using a.case or bag can be applied. Examples of the package which can be formed in the above-described methods are a tray, cup, tube, bottle, case, or bag. It is also possible to use a sheet of the multi-layer structural body of the present invention as a top film to cover a gas-permeation-resistant container such as a tray or cup. As for the usage form of the multi-layer structural body, it is eventually necessary to seal the package hermetically in order to prevent oxygen from permeating into the package from outside. As a method of hermetical sealing, a closure means, top film, outside package or other conventional technology can be applied. Embodiments of the present invention will now be described by way of example only with reference to the accompanying drawings, in which: Figure 1 is a sectional view of the multi-layer structural body of the present invention. Figure 2 is a sectional view of a container made of the multi-layer structural body of this invention. Figure 3 is a sectional view of the container of this invention in which a preserved substance is placed and which is hermetically sealed. Figure 4 is a sectional view of a wide-mouthed bottle made of the multi-layer structural body of this invention. Figure 5 is a sectional view of another wide-mouthed bottle made of the multi-layer structural body of this invention. Figure 6 is a sectional view of a container which is covered with a lid made of the multi-layer structural body of this invention. Figure 7 is a sectional view of a still another wide-mouthed bottle made of the multi-layer structural body of this invention. Figure 1 shows a multi-layer structural body to be produced in accordance with the invention. Iron powder (median diameter on a weight basis: 35 µm) was put in a vacuum mixing dryer with a heat jacket, and was heated and dried at a temperature of 130°C under 10 mmHg of reduced pressure. At the same time, a mixed aqueous solution of calcium chloride, sodium chloride, and water, which was mixed in the proportion of calcium chloride : sodium chloride water = 0.5 : 0.5 : 2.5 (parts by weight), was sprayed to 100 parts by weight of the iron powder. Accordingly, the mixed solution was attached to the surface of the iron powder, thereby obtaining an oxygen absorber composition. Then polypropylene and the oxygen absorber composition were mixed and kneaded in a weight ratio of polypropylene : oxygen absorber composition = 2 : 3 by using a biaxial extrusion machine (45 mm) which rotates in a unilateral direction. The kneaded mixture was cooled by using a net belt with a blower and was made to go through a pelletizer, thereby obtaining oxygen absorber composition pellets. Subsequently, a multi-layered sheet molding device was used, which consist of first through fourth extrusion machines, feed blocks, T dies, cooling rolls, and sheet take-off machines, and which forms a six-layer construction from four groups of materials. The first extrusion machine was provided with polypropylene with white pigments added. The second extrusion machine was provided with the oxygen absorber composition pellets. The third extrusion machine was provided with ethylene-vinyl-alcohol-copolymer. The fourth extrusion machine was provided with maleic anhydride modified polypropylene. These materials were extruded from the respective extrusion machines, thereby obtaining the multi-layer structural body as shown in Figure 1. This multi-layer structural body comprises: a third layer 3 of polypropylene with white pigments added; a second layer 2 of the oxygen absorber composition pellets, which is laminated over the third layer 3; and a first layer 1. The first layer consists of: layer 13 of maleic anhydride modified polypropylene, which is laminated over the second layer 2; layer 14 of ethylene-vinyl-alcohol-copolymer, which is laminated over layer 13; layer 15 of maleic anhydride modified polypropylene, which is laminated over layer 14; and layer 16 of polypropylene with white pigments added, which is laminated over layer 15. In the present invention, film thickness of the respective layers is set as follows: the third layer at 100 µm; the second layer at 100 µm; layer 13 at 15 µm; layer 14 at 20 µm; layer 15 at 15 µm; and layer 16 at 250 µm. Then, the multi-layer structural body was molded into a tray-shaped container (length 150 mm x width 100 mm x depth 30 mm, and about 350 cm 3 (cc) of content volume) with the third layer 3 being the innermost layer, as shown in Figure 2, by a plug assist forming method by using a vacuum forming machine at a temperature of about 180°C. Boiled pasta (200g) was placed in the tray-shaped container 50 obtained, and then nitrogen replacement was conducted by using a cup sealer with a nitrogen blow device so that the oxygen content within the tray-shaped container became about 5%. A top film 10 was then hermetically sealed to the tray-shaped container by heat, as shown in Figure 3, in order to hermetically seal the tray-shaped container with the above-mentioned oxygen content. Although not shown in Figure 3, this top film 10 is in a five-layer structure which consists of: a layer of polypropylene which is 50 µm in film thickness; a layer of maleic anhydride modified polypropylene which is 5 µm in film thickness and which is laminated over the above first layer; a layer of ethylene-vinyl-alcohol-copolymer which is 10 µm in film thickness and which is laminated over the above second layer; a layer of maleic anhydride modified polypropylene which is 5 µm in film thickness and which is laminated over the above third layer; and a layer of nylon which is 20 µm in film thickness and which is laminated over the above fourth layer. Figure 4 shows a multi-layer structural body in the form of a bottle to be produced in accordance with the invention. 100 parts by weight of iron powder (median diameter on a weight basis: 20 µm or shorter), 1 part by weight of calcium chloride, 2 parts by weight of yellow iron oxide, 0.5 parts by weight of powdered activated carbon, and 3 parts by weight of polypropylene (granulated to be 10 µm or shorter in a median diameter on a weight basis) were mixed by using a Henschel mixer. The mixture obtained was formed into tablets (diameter: 9 mm) by using a rotary tablet machine. These tablets were ground by a speed mill and then were screened, thereby obtaining an oxygen absorber composition which was made in a dust size of 100-250 mesh. Subsequently, polypropylene and the above-mentioned oxygen absorber composition were mixed and kneaded in the weight ratio of polypropylene : free oxygen absorber composition = 1 : 1 by using a biaxial extrusion machine (45 mm) which rotates in a unilateral direction. The kneaded mixture was extruded from a strand die, and the extruded mixture was cooled by using a net belt with a blower and was made to go through a pelletizer, thereby obtaining pellets containing the oxygen absorber composition. By using a blow molding device which consists of first and second extrusion machines, multi-layer circular dies, and mold dies for blow molding, a wide-mouthed bottle (mouth diameter: 40 mm; diameter of the body portion: 60 mm; height: 95 mm; and volume: about 180 ml) was formed. As shown in Figure 4, the wide-mouthed bottle is constructed by laminating layers in the following order from the innermost layer to the outermost layer: a third layer of polyethylene (50 µm in film thickness) ; a second layer of polyethylene (200 µm in film thickness) in which the oxygen absorber composition is dispersed; and a first layer of polyethylene (450 µm in film thickness of the body portion). As shown in Figure 5, the body portion of the same wide-mouthed bottle was covered with a barrier shrink film ("BDF 2001"™ made by CRYOVAC) which was in a cylindrical shape (diameter: 65 mm; height 80 mm) and in the laminated structure of polyolefin and ethylene-vinyl-acetate-copolymer. This barrier shrink film was made to shrink with hot air and thereby made to closely contact the body portion of the bottle, thereby obtaining the wide-mouthed bottle shown in Figure 5. Namely, the first layer of Figure 5 consists of polyethylene (450 µm in film thickness) and the barrier shrink film. EXAMPLE 1 EXAMPLE 1 of the present invention is hereinafter explained. 100 Kg of reduced iron powder (median diameter on a weight basis: 30 µm) was put in a vacuum mixing dryer with a heat jacket. While the reduced iron powder was heated and dried at a temperature of 140°C and under reduced pressure of 10 mm Hg, 7 Kg of 20 wt% calcium chloride aqueous solution was sprayed on the reduced iron. The reduced iron powder with the calcium chloride solution sprayed thereon was dried and screened, and grains larger than 300 mesh were removed, thereby obtaining an oxygen absorber composition. By using a unilateral rotary biaxial extrusion machine (45 mm) with vents and a quantitative feeder, ethylene-propylene-copolymer and the above oxygen absorber composition were mixed and kneaded in the proportion of ethylene-propylene-copolymer : oxygen absorber composition = 2 : 3. The kneaded mixture was extruded from a strand die, and the extruded mixture was air-cooled and crushed, thereby obtaining a master batch A. Then by using the above-mentioned extrusion machine, calcium oxide (median diameter on a weight basis: 20 µm) and ethylene-α-olefine-copolymer were mixed and kneaded in a weight ratio of 1 : 1, and a master batch B was obtained by the same operations as described above. Subsequently, a multi-layer structural body having the structure shown in Table 1 was prepared by using a sheet extrusion device which consists of the first through fifth extrusion machines, feed blocks, T dies, cooling rolls, sheet take-off machines, slitters, and winders, and which forms a six-layer construction from five groups of materials. Extrusion Machine Extruded Compositions Corresponding Layers 1st Extrusion Machine Ethylene-propylene-copolymer: 90 wt% Isolating layer Titanium oxide pigment: 10 wt% 2nd Extrusion Machine Master batch A: 98 wt% Oxygen absorber layer Master batch B: 2 wt% 3rd Extrusion Machine Nylon MXD6 Gas-permeation-resistant layer 4th Extrusion Machine Maleic anhydride modified polypropylene Adhesive layer 5th Extrusion Machine Ethylene-propylene-copolymer: 95 wt% Strength-retaining layer Titanium oxide pigment: 5 wt% The multi-layer structural body in the construction shown in Table 1 consists of: a first layer which consists of three kinds of layers, that is, a layer of nylon MXD6 (20 µm in film thickness), a layer of maleic anhydride modified polypropylene (15 µm in film thickness), and a layer of a mixture of ethylene-propylene-copolymer and titanium oxide pigments (250 µm in film thickness); a second layer (140 µm in film thickness) which consists of a mixture of ethylene-propylene-copolymer, master batch A, and master batch B; and a third layer of ethylene-propylene-copolymer (60 µm in film thickness). The layer of nylon MXD6 gives resistance to gas permeation, the layer of maleic anhydride modified polypropylene gives adhesiveness, and the layer of the mixture of ethylene-propylene-copolymer and titanium oxide pigments gives retaining strength. COMPARATIVE EXAMPLE 1 A multi-layer structural body of the same construction as that used in EXAMPLE 1 was prepared in the same manner as in EXAMPLE 1, except that the composition of the master batch B was not used among the compositions extruded from the second extrusion machine used in EXAMPLE 1, and that the content of ethylene-propylene-copolymer was changed to 12 wt%. As a result of observation of this multi-layer structural body, the surface of the third layer became uneven and was no longer flat. Moreover, bubbles were generated in the second layer. COMPARATIVE EXAMPLE 2 A multi-layer structural body of the same construction as that used in EXAMPLE 1 was prepared in the same manner as in COMPARATIVE EXAMPLE 1, i.e. master batch B was not added to the composition extruded from the second extrusion machine to form the oxygen absorber layer, except that the oxygen absorber composition was dried for one hour at a temperature of 300°C under a nitrogen gas atmosphere by using an electric furnace. According to observations of this multi-layer structural body, the surfaces of the multi-layer structural body were deemed flat and smooth and in good condition as in EXAMPLE 1. EXAMPLE 2 The multi-layer structural body (50 m long) obtained in EXAMPLE 1 was wound around a vinyl chloride pipe (76 mm (3 inches) in inside diameter) ), and then was wrapped with a moisture-proof film made of aluminum-foil-laminated polypropylene. The wrapped multi-layer structural body was sealed with tape. The wrapped multi-layer structural body was put in a bag made of laminated films of nylon coated with vinylidene chloride and of polyethylene. The mouth of the bag was hermetically sealed by heat, and the bag was preserved indoors. This multi-layer structural body was opened after 2-month preservation, and a formed tray (content volume: 270cm 3 (cc)) formed in a vacuum forming method at a temperature of 185°C by using a vacuum forming machine (capable of forming 15 trays, each 130 mm x 90 mm x depth 25 mm). According to observations, the formed condition of the formed tray was deemed good. COMPARATIVE EXAMPLE 3 The multi-layer structural body obtained in COMPARATIVE EXAMPLE 2 was preserved in the same wrapped form as in EXAMPLE 2. The wrapped multi-layer structural body was opened after a 2-month preservation, and was then formed into a formed tray in a vacuum forming method under the same conditions as in EXAMPLE 2. According to observations of the formed condition of the tray, bubbles were generated in the tray, which destroyed the appearances of the tray, the third layer was partly broken and the second layer was exposed. Therefore, the formed tray was not usable as a tray. EXAMPLE 3 The formed tray obtained in EXAMPLE 2 with 250 cm 3 (cc) of boiling water poured inside was covered with a top film of laminated layers of polyester, aluminum foil, and polypropylene, and was hermetically sealed by heat. This sealed tray was placed and left at room temperature, and the oxygen content within the tray was analyzed by gas chromatography after a 24-hour preservation and a 2-month preservation. The results obtained are shown in Table 2. EXAMPLE 4 The formed tray obtained in EXAMPLE 2 was put in a bag of nylon-laminated polyethylene, and the mouth of the bag was tied with a rubber band. The formed tray was then left indoors, and after a 2-month preservation, the oxygen content was measured in the same manner as in EXAMPLE 3. The results obtained are shown in Table 2. COMPARATIVE EXAMPLE 4 For the formed tray obtained in COMPARATIVE EXAMPLE 2, the oxygen content within the tray was analyzed by gas chromatography under the same conditions as in EXAMPLE 3. The results obtained are shown in Table 2. COMPARATIVE EXAMPLE 5 The oxygen content within the tray was analyzed by gas chromatography under the same conditions as in EXAMPLE 4 except that the formed tray obtained in COMPARATIVE EXAMPLE 2 was used instead of the formed tray obtained in EXAMPLE 2 The results obtained are shown in Table 2. Oxygen Content after 24 Hours Oxygen Content after 2 Months Before Preservation EX. 3 2.2% 0.1% or less EX. C-E 4 2.4% 0.1% or less After Preservation ER. 4 2.3% 0.1% or less EX. C-E 5 4.7% 0.1% or less The multi-layer structural body of the present invention can be used, other than as a container such as a tray or bottle, as a lid 201 of a container 200 as shown in Figure 6. Moreover, as shown in Figure 7, only a part of the container 200 may be in a three-layer structure.

Claims: A multi-layer structural body, comprising: a first layer which is resistant to gas permeation; a second layer which is laminated over said first layer and which has a deoxidizing property; and a third layer which is laminated over said second layer and which is permeable to oxygen, wherein the oxygen permeability of said first layer is less than 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH), wherein said second layer comprises: resin of which the oxygen permeability coefficient is 200cm 3 ·0.1mm/m 2 ·d·1.01x10 5 N/m 2 (cc•0.1mm/m 2 •day•atm) (23°C, 100%RH) or more; a granular oxygen absorber which is dispersed in the resin and which contains an oxygen absorber composition which exhibits a deoxidization reaction when moisture is supplied thereto; and calcium oxide as moisture absorber, and wherein the oxygen permeability of said third layer is 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH) or more. A multi-layer structural body according to claim 1, wherein the moisture amount of said oxygen absorber composition is 0.2 wt% or less. A multi-layer structural body according to claim 1 or claim 2, wherein said first layer consists of one or more layers of at least one kind of the following groups: polyolefin such as polyethylene and polypropylene; polyester such as polyethylene terephthalate; polyamide such as nylon 6, nylon 66, and MX nylon; and synthetic resin such as ethylene-vinyl-alcohol-copolymer, polyvinyl chloride, or polyvinylidene chloride, wherein said second layer consists of a layer of at least one kind of the following groups: polyolefin such as polyethylene, polypropylene, polybutadiene, or polymethyl pentene, and modified forms thereof; and thermoplastic resin such as graft polymer with silicone resin, ionomer, elastomer, polycarbonate, or polyurethane, and mixed resin thereof, and wherein said third layer consists of one or more layers of at least one kind of the following groups: polyolefin such as polyethylene, polypropylene, polybutadiene, or polymethyl pentene, and modified forms thereof; graft polymer with silicone resin; polyester such as polyethylene terephthalate; polyamide such as nylon 6, nylon 66; or synthetic resin such as ionomer or elastomer. A multi-layer structural body according to any one of claims 1 to 3, wherein said second layer consists of ethylene-propylene-random-copolymer, and said first and third layers mainly consist of polypropylene. A multi-layer structural body according to any ones of claims 1 to 4, wherein the compounding ratio of the oxygen absorber composition in said second layer is 2-93 wt%. A multi-layer structural body according to any one of claims 1 to 5, wherein film thickness of said second layer is 1000 µm or less. A multi-layer structural body according to any one of claims 1 to 6, wherein the median diameter on a weight basis of said oxygen absorber composition is 5-200 µm. A multi-layer structural body according to any one of claims 1 to 7, wherein said second layer softens much faster than said third layer. A multi-layer structural body according to claim 8, wherein the softening temperature of the resin composing said second layer is no higher than that of the resin which is the main component of said first and third layers. A multi-layer structural body according to any one of claims 1 to 9, wherein said oxygen absorber composition contains metal iron and metal halide. A multi-layer structural body according to any one of claims 1 to 10, wherein said calcium oxide is dispersed in said thermoplastic resin as separate grains from said oxygen absorber composition. A multi-layer structural body according to any one of claims 1 to 11, wherein the compounding ratio of said calcium oxide to the resin composing said second layer is 0.1-5 wt%. A multi-layer structural body according to any one of claims 1 to 12, wherein said first layer contains a coloring agent. A multi-layer structural body according to claim 1, wherein said third layer is made of a mixture of a first resin, which can be adhered to the second layer, and a second resin, which has poor miscibility with the first resin. A multi-layer structural body according to claim 14, wherein both the resin composing said second layer and the first and second resin composing said third layer are polyolefin, the oxygen permeability of said second resin is higher than that of said first resin, and the second resin does not hinder adhesion to the second layer. A multi-layer structural body according to claim 15, wherein said third layer is made of a mixture of two or more kinds of polyolefin, which mixture contains poly-4-methyl-pentene-1 or resin containing poly-4-methyl-pentene-1 as a main component in a proportion of 50 wt% or less. A multi-layer structural body according to claim 16, being made of a mixture of two or more kinds of polyolefin, which mixture contains poly-4-methyl-pentene-1 or resin containing poly-4-methyl-pentene-1 as a main component in a proportion of 10-40 wt%. A multi-layer structural body according to any one of claims 1 to 17, wherein film thickness of said third layer is 10-100 µm. A method for manufacturing a multi-layer structural body, comprising: the step of simultaneously extruding a first material which is resistant to gas permeation, a second material which has a deoxidizing property, and a third material which is permeable to air, thereby forming a multi-layer laminated body in which layers are laminated in the order of a first layer made of the first material, a second layer made of the second material, and a third layer made of the third material, wherein said second material is manufactured by a method comprising the steps of kneading a granular oxygen absorber and calcium oxide as moisture absorber in resin, which oxygen absorber contains an oxygen absorber composition which exhibits a deoxidation reaction when moisture is supplied thereto. A method of manufacturing a multi-layer structural body according to claim 19, comprising the step of laminating a fourth layer which is resistant to heat and to gas permeation, over the first layer of said multi-layer laminated body. A method of manufacturing a multi-layer structural body according to claim 19 or claim 20, wherein the resin composing said first layer is polyolefin, said second layer is a second polyolefin in which the oxygen absorber composition containing metal iron grains is dispersed, and the resin composing said third layer is a third polyolefin. A package made of a multi-layer structural body which comprises: a first layer which is resistant to gas permeation; a second layer which is laminated over said first layer and which has a deoxidizing property; and a third layer which is air permeable and laminated to said second layer, wherein the oxygen permeability of said first layer is less than 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH), wherein said second layer comprises: a resin having an oxygen permeability coefficient of at least 200cm 3 ·0.1mm/m 2 ·d·1.01x10 5 N/m 2 (cc•0.1mm/m 2 •day•atm) (23°C, 100%RH) ; a granular oxygen absorber composition dispersed in the resin and including a deoxidization material undergoing a deoxidization reaction when exposed to moisture; and calcium oxide as moisture absorber dispersed in said resin, wherein the oxygen permeability of said third layer is at least 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH) , and wherein said first layer forms the outside wall of the package, and said third layer forms the inside wall of the package. Use of calcium oxide as a moisture absorber in a multi-layer structural body comprising: a first layer which is resistant to gas permeation; a second layer which is laminated over said first layer and which has a deoxidizing property; and a third layer which is laminated over said second layer and which is permeable to oxygen, wherein the oxygen permeability of said first layer is less than 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH) , wherein said second layer comprises: resin of which the oxygen permeability coefficient is 200cc•0.1mm/m 2 •day•atm (23°C, 100%RH) or more; a granular oxygen absorber which is dispersed in the resin and which contains an oxygen absorber composition which exhibits a deoxidization reaction when moisture is supplied thereto; and the moisture absorber, and wherein the oxygen permeability of said third layer is 100cm 3 /m 2 ·d·1.01x10 5 N/m 2 (cc/m 2 •day•atm) (23°C, 100%RH) or more for the purpose of restraining the oxygen absorber composition from absorbing water during storage of said multi-layer structural body.

Inventors: HATAKEYAMA HIDETOSHI, ITO YOSHIKI, HATAKEYAMA, HIDETOSHI, ITO, YOSHIKI, HATAKEYAMA, HIDETOSHI, MITSUBISHI GAS CHEM. CO., ITO, YOSHIKI, MITSUBISHI GAS CHEM. CO.,INC.
Applicants: MITSUBISHI GAS CHEMICAL CO, MITSUBISHI GAS CHEMICAL COMPANY, INC.
Application year: 1995
Main classification: B32B27
IPC codes: B32B27, B65D81