AN ELECTRICALLY CONDUCTING POLYMER COMPOSITION, ITS PRODUCTION AND ITS USE

Abstract: The invention relates to an electrically conductive elastomer composition which comprises a thermoplastic polymer and a doped aniline polymer. A problem in the preparation of electrically conductive elastomer compositions is the lack of thermoplasticity of the electrically conductive component, making difficult the processing and the obtaining of a homogenous product. This problem has now been solved by having the doped aniline polymer be a substantially thermoplastic doped aniline polymer which is obtained by reacting with a functionalized protic acid a conjugated homo- or copolymer made up of at least unsubstituted and/or substituted aniline mers. The protic acid functionalizes the aniline polymer either on being heated together with the aniline polymer to a temperature of 80-250 DEG C or on being heated together with the aniline polymer and a solvent and on the solvent being evaporated. The elastomer composition is also composed of a plasticizer which plasticizes the doped aniline polymer and promotes its flow, preferably a metal compound with a plasticizing effect, such as a reaction product of zinc oxide and dodecylbenzenesulfonic acid.

Description: An electrically conducting polymer composition, its production and its use The invention relates to an electrically conductive thermoplastic elastomer composition which comprises a thermoplastic elastomer and a doped aniline polymer. The invention also relates to a method for the preparation of an electrically conductive elastomer composition, wherein a thermoplastic elastomer and a doped aniline polymer are contacted and are melt processed into the form of a granulate, powder, fiber, coating, film, sheet, laminate, foam, tube, hose, profile, blend, adhesivej sealant, composite, formed piece (e.g. extruded piece, molded piece) or other melt-processed product or structure. The invention also relates to a granulate, powder, coating, film, sheet, laminate, foam, tube, hose, profile, fiber, blend, adhesive, sealant, composite, formed piece (e.g. extruded piece, molded piece) or other elastomer product or structure which has been prepared from an elastomer mixture made up of a thermoplastic elastomer and a doped aniline polymer. Finally the invention relates to the use of the said electrically conductive elastomer composition, or a product made therefrom, for an ESD and/or EMI application, for an application which requires electrical conductivity and elasticity, for an application which requires the retaining of electrical conductivity on stretching, for an application which requires the dependence of the conductivity on the amount of elongation, for sensors in which electrically conductive thermoplastic elastomers are used, for elastomeric coatings, for elastomeric adhesive compositions, for elastomeric sealants, and for elastomeric sealing structures. Thermoplastic elastomers were launched on the market c. 1960. They have many physical properties typical of rubbers, such as softness, flexibility and resilience, but, in a manner deviating from conventional rubbers, they can be processed in the manner of thermoplastic resins. Rubbers have to be bridged irreversibly in order to achieve usable properties, whereas a thermoplastic elastomer is melt-processible and, when cooled, is rapidly and reversibly converted into a solid rubber-like product. Thermoplastic elastomers can be processed using a conventional plastics processing apparatus, such as an extruder, compounder, kneader or injection molder, the residues often being recycled. Owing to increased production and a lower price of the raw material, thermoelastic polymer materials constitute a considerable and increasing proportion of the total producti¬ on of plastics. Thermoelastic polymers are used mainly in fields in which thermal resistance and resistance to solvents are not required. Thermoelastic polymers are multi-phase compositions in which the phases are closely dispersed with each other. In many cases the phases are chemically bonded to each other by block polymerization or graft polymerization. In others, a fine dispersion suffices. At least one of the phases is made up of a material which is hard at room temperature but becomes liquid when heated. The other phase consists of a softer material, which is rubber-like at room temperature. A typical and simple structure is an A-B-A block polymer, in which A is the hard phase and B is the soft phase, i.e. the elastomer block. Most polymers are thermodynamically incompatible with other polymers, and their mixtures separate into two phases. This holds true even when the polymers are parts of the same molecule, as in these block polymers. The hard A end blocks form in the material separate three-dimensional areas which are dispersed in the continuous B-phase, i.e. the soft phase. At room temperature these A-block areas are hard and serve as physical bridges which bond together the soft chains into a three-dimensional network. This resembles the vulcanization structure of conventional rubbers, with the exception that in thermoplastic elastomers the hard A-block areas lose their strength when the material is heated or dissolved in solvents. For this reason the polymer is capable of flowing when heated or dissolved. When the material is then cooled or the solvent is evaporated, hard A-block areas and soft B-block areas are again formed and the elastic network is re¬ created. The most important thermoplastic elastomers (TPE) in 1991 were the following, and their proportions of world-wide sales are indicated after the polymer category: 1. styrene-type block polymers (SBC) 44 % 2. polyolefin-based elastomers (TPO/TPV) 29 % 3. polyurethane-based elastomers (TPU) 13 % 4. polyester-based elastomers (COPE) 5 % Recently, attention has begun to be paid to electrically conductive thermoplastic elasto¬ mers. Electrical conductivity is produced by mixing a fine-grained, electrically conductive powder with an elastomer matrix, the electrical conductivity of the created composite (moldable matrix + solid electrically conductive powder) being produced by contact between powder particles. In the case of thermoplastic elastomers this means that an electrically conductive elastomer is prepared by melt or solution processing, during which the electrically conductive powder remains in solid state. JP-63086781-A discloses an anisotropically conductive adhesive sheet which comprises a styrene/ethylene/butene/styrene block polymer, a coumarone-indene resin, an aliphatic petroleum resin, and an electrically conductive powder. The electrically conductive powder is preferably a metal powder or a metal-coated resin powder. The sheet obtained has high adhesiveness, high thermal resistance, and high resistance to moisture. It is used for making fine printed circuit boards. JP-62181379-A discloses an anisotropically conductive adhesive sheet of a similar type, intended for the connecting of circuits, the adhesive sheet comprising a styrene/butadie- ne/styrene block polymer, coumarone resin, terpene resin, and electrically conductive particles. The conductive particles are of metal, metal-coated resin, or metal-coated glass. The adhesive sheet has a high adhesiveness, and even when it is used for making fine- structured circuits, a reliable electrical conductivity is accomplished. In all of the publications cited above, an electrically conductive, non-melting material is blended with a non-conductive thermoplastic elastomer matrix. Such a multi-phase composite has the disadvantage that the electrical conductivity is dependent on mechanical contact between electrically conductive particles, in which case the minimum content which produces electrical conductivity, i.e. the percolation threshold, is high, and the sensitivity of the electrical conductivity to deformations of the composite is high. This problem of homogeneity associated with electrical conductivity is emphasized especially in thermoplastic elastomers, which even otherwise have hard bridging areas and soft elastomeric areas. Furthermore, a filler such as metal powder weakens specifically those mechanical properties of the composite which are required of an elastomer, i.e. softness, flexibility, stretchability, and elasticity. It is considered a great problem in the art that in- trinsically conductive polymers, such as aniline polymers, are usually not melt or solution processible, i.e. thermoplastic. Thus the blending of a conventional electrically conductive polymer with a thermoplastic elastomer will not solve this problem. The acidity of conductive polymers doped with protic acids also significantly complicates the use of conductive polymers in many applications. Acid products cause difficulties, for example, in the use of the apparatus for the preparation and processing of conductive polymers, since eroding and corrosion of the apparatus would become a problem. Furthermore, many conductive polymer applications presuppose neutral or nearly neutral materials, and thus the applications of the conductive material, which is good as such, remain few in practice. It is an object of the present invention to provide an electrically conductive thermoplastic elastomer composition combining high electrical conductivity and good mechanical properties, in particular softness, flexibility, stretchability, and elasticity. The aim is in particular to provide a material which comprises a thermoplastic elastomer and a doped aniline polymer, the conductivity-providing proportion of the aniline polymer, i.e. the percolation threshold, in the material being as low as possible. It is a further aim to achieve an elastomer composition the electrical conductivity of which, when a product made from the elastomer composition is stretched, will not behave in the same manner as when a non-melting conductive component is used. It is a specific aim that the electrical conductivity of the conductive elastomer composition will be retained maximally high when a piece made from the composition is stretched. It is also desirable that the inventi¬ on will provide an electrically conductive elastomer composition the melt processibility and solution processibility of which, with respect to all its components, can be exploited in the making of products such as a granulate, powder, coating, film, sheet, laminate, foam, long hose, profile, fiber, blend, adhesive, sealant, composite, formed piece, or other product. It is a further aim to produce a substantially neutral conductive elastomer material in which the acidity of the doping agent will not lower the quality of the material. By a substantially neutral acidity is meant in this context the pH range 3-8, preferably the pH range 4-7, and most preferably the pH range 5-7. The above objects have now been achieved with a new electrically conductive elastomer composition which is mainly characterized in that the elastomer will return substantially to its former shape (at least 85 %) after a 50 % stretching, the electrical conductivity of the elastomer will be retained at substantially the same level (reduced less than one de¬ cade) during the stretching, and the electrical conductivity of the elastomer will not, after the returning to its shape, be substantially weakened (reduced less than one decade). It is preferable that it comprises a) an amount approx. 10-99 % by weight of a thermoplastic elastomer and b) an amount of approx. 0.5-90 % by weight of an aniline polymer which is a conjugated homo- or copolymer which is made up of at least an unsubstituted and/or substituted aniline mer doped with a protic acid, the protic acid having a functionalizing effect in such a manner that the aniline polymer will be melt processible and solution processible. It is also preferable if it, in addition to components a) and b), comprises an amount of 0.5-40 % by weight of a plasticizer which will plasticize the thermoplastic doped aniline polymer and promote its flow. The elastomer composition may also be defined according to SFS standard 3551, which is incorporated herein by reference. It has thus been realized that an elastomer composition based on a thermoplastic elastomer and an electrically conductive polymer is superior if also the electrically conductive polymer is thermoplastic. Such a superior elastomer composition is produced by using a non-conventional thermoplastic, electrically conductive polymer which is obtained by reacting a conjugated homo- or copolymer, made up of at least unsubstituted and/or substituted aniline mers, at an elevated temperature with a protic acid which both dopes and functionalizes, i.e. plasticizes, the said conjugated homo- or copolymer. According to one embodiment, an elastomer composition according to the invention comprises a thermoplastic elastomer and a doped aniline polymer obtained by heating at an elevated temperature an undoped aniline polymer together with a protic acid which dopes and functionalizes it. It is preferable that the thermoplastic, doped aniline polymer is obtained by reacting a conjugated homo- or copolymer, made up of at least aniline mers and/or substituted aniline mers, with a protic acid which dopes it, at a temperature which is approx. 80-250 °C, preferably approx. 120-210 °C, most preferably approx. 150- 200 °C. The conductive component, i.e. the thermoplastic doped aniline polymer, of the electrical- ly conductive elastomer composition according to the invention is preferably obtained by reacting a conjugated homo- or copolymer, made up of at least unsubstituted and/or substituted aniline mers, together with a protic acid at a pressure which is approx. 1-10 4 kPa. The heating time required for the reacting may vary greatly and is 10 s - 20 min according to one embodiment. The conjugated homo- or copolymer made up of substituted or unsubstituted aniline mers is preferably reacted by means of shear forces with a protic acid which dopes and functionalizes it. By shear forces is meant shear forces of the same type as are used in the melt processing of plastics. In this case it is possible ad¬ vantageously to use common melt-processing apparatus for plastics, such as kneaders, screw blenders, and extruders. By using them, a plastic and homogenous thermoplastic doped aniline polymer is obtained at an elevated temperature. According to another embodiment, the said aniline polymer is protonated by heating it together with a functionalizing protic acid and a solvent, and by removing the solvent. The solvent is preferably a C,-Cι 0 alcohol such as ethanol. The doped aniline polymer component of the elastomer composition according to the invention is substantially thermoplastic, i.e. moldable in heat, and solution processible, and it is obtained by reacting a conjugated homo- or copolymer, made up of at least unsubstituted and/or substituted aniline mers, at an elevated temperature and/or in a solvent with a doping protic acid. Some typical such conjugated initial materials for an aniline polymer are polymers having in their polymer chains various quantities of phenylene amine and qiώione-imine type frame segments, and which include leuco- emeraldine, protoemeraldine, emeraldine, nigraline, and pernigraline. Dopable aniline- based homo- or copolymers usable in the present invention are listed, for example, in US patent publication 5 171 478, 5 281 363, and WO publication 90/10297 which are incorporated by reference in this application. According to one preferred embodiment, an unsubstituted polyaniline homopolymer, i.e. polyaniline, is used as the conjugated homo- or copolymer which is made up of at least unsubstituted and/or substituted aniline mers. As was already mentioned, it may be present in a leucoemeraldine, protoemeraldine, emeraldine, nigraline, or pernigraline form. The most preferred polyaniline form for use in the present invention is its emeraldi- SUBST1TUTE SHEET (RULE 26) ne form, i.e. emeraldine base form, which is in general depicted with the molecular formula where x is approx. 0.5. In general, the number of repeat units in the aniline polymer to be doped is not critical and may vary greatly. Usable aniline polymers may be prepared by chemical or electrochemical synthesis methods. Polyaniline may be prepared, for example, by polymerizing aniline with ammonium persulfate in the presence of 1 M hydrochloric acid. This powder form of polyaniline is bluish green in color. It is electrically conductive and can be brought to a non-conductive form by treating it with an ethanol solution of ammonium hydroxide, whereby a non-conductive polyaniline form is obtained. In the invention, the doped aniline polymer is a substantially melt-processible doped aniline polymer obtained by reacting an aniline polymer, as defined above, with a protic acid which dopes the said aniline polymer to an electrical conductivity of at least approx. IO" 9 S/cm and which is a functionalizing protic acid so that it also plasticizes and com- patibilizes the polyaniline, whereupon it will be solution processible and melt processible together with a thermoplastic matrix polymer. Such protic acids include the compounds according to the following formula RXM wherein R is an organic group or amino, X is an anionic group such as PO 3 2* , PO 2 (Rι)", BO 2 2 ", SO 3 ", CO 2 ", PO 2 2" , PO(R " and/or SO 2 ", and M is one proton or cation or several protons or cations, provided that it includes at least one proton. Protic acids usable in the present invention are listed, for example, in US patent 5 281 363 which is incorporated by reference in this application. A protic acid according to the above formula is especially preferable when R is an aromatic ring or ring system. Typical usable aromatic protic acids are sulfonic acids, regarded as preferable, for example unsubstituted or substituted benzenesulfonic acids, benzenedisulfonic acids, naphthalenesulfonic acids, naphthalenedi- and trisulfonic acids, anthracenesulfonic acids, phenatrenesulfonic acids, biphenylmono- and disulfonic acids, etc. Benzenesulfonic acids substituted with a long al yl, such as dodecylbenzenesulfonic acid, have been found to be especially preferable in the invention. The thermoplastic doped aniline polymer for use in an elastomer composition according to the invention is preferably prepared in such a manner that the molar ratio of the undoped aniline polymer to the doping protic acid, to be reacted with each other, is in the heated reaction within a range of approx. 0.05-3.0, preferably approx. 0.1-1.0, and most preferably approx. 0.125-0.5. Other details relating to the method of preparing a doped aniline polymer can be obtained from, for example, EP patent application 545729 and the corresponding US patent 5,346,649, incorporated herein by reference. The present invention is thus based on the fact that both the thermoplastic elastomer and the doped aniline polymer of the elastomer composition according to the invention are in plastic form during melt or solution processing. In order to produce a melt-processible doped polyaniline, a plasticizer which will plasticize the doped aniline polymer may be added to the composition. The plasticizer used may be, for example, water, alcohols, ethers, ketones, urea compounds, phenols, substituted and unsubstituted aromatic com¬ pounds, amides and phosphorus amides, organic sulfur compounds, amines, esters, aromatic acids and their esters, aliphatic acids and their esters, including fatty acids and their esters, glycols and glycol derivatives, phosphates, silicates, borates, aromatic and aliphatic sulfonic acids and their derivatives, fluorinated carboxylic acids and fluorinated sulfonic acids, synthetic waxes, thermoplastic resins, etc. Examples of plasticizer belonging to these categories are presented in US patent publica- tion 5 171 478, which is incorporated herein by reference. Metal compounds having a plasticizing effect have been found to be especially preferable. This concerns quite particularly metal compounds the softening point of which is below approx. 300 °C. When a metal compound which has a plasticizing effect and which reacts with the doping protic acid is used, there is often also gained the advantage that the pH of an otherwise acidic doped aniline polymer, difficult to handle, is neutralized to the range 3-8. However, the above-mentioned preferable acidity limits (pH 3-8) achieved by using the method according to the invention can be further widened for certain special applications. Conductive plastics blends having a pH value even below 3 or above 8 can be used for certain purposes, and such plastics blends can be obtained by suitably selecting the matrix polymers to be blended with the conductive polymer material. According to one preferred embodiment, the metal in a metal compound suitable for use as a plasticizer is a metal belonging to any of groups 1-4 (IUPAC) of the Periodic Table of the Elements, such as zinc, copper, magnesium, barium, aluminum, calcium, titanium, zirconium, cadmium, lead, and/or stannium. In the present invention it is especially advantageous to use as the plasticizer metal compounds which are based on the metals zinc, copper, calcium, and/or magnesium. Plasticizing compounds based on zinc are especially preferable. According to one embodiment, the other component of the metal compound is a protic acid residue. The plasticizer is in that case a metal salt preferably of protic acid, more preferably of a non-oxidizing organic protic acid, even more preferably of an aromatic sulfonic acid, and most preferably of a long-chain alkarylsulfonic acid, such as dodecyl- benzenesulfonic acid. Even though it is not indispensable that the protic acid used in the plasticizer is the same as the doping and functionalizing protic acid used in the doped aniline polymer, it is, nevertheless, preferable if it is so. The plasticizing can thus be accomplished by using the doping protic acid in excess in proportion to the aniline polymer to be doped, and at least a stoichiometric amount of a metal compound reacting with the same protic acid, the metal compound thus reacting with the excess protic acid and forming a plasticizer deemed to be preferable in the invention. On the basis of the foregoing it is preferable if the plasticizer is a reaction product of a zinc compound and an aromatic sulfonic acid, obtained by causing zinc oxide or zinc hydroxide, preferably zinc oxide, and an alkylaromatic sulfonic acid, such as dodecyl- benzenesulfonic acid, to react with each other, for example by heating. When the plasticizer is prepared from a metal compound and protic acid, it is preferable to use a metal compound to protic acid ratio which is within the range 0.1»E - 10*E, where E stands for the valence ratio of the metal to the protic acid. When, for example, zinc oxide, ZnO, is used as the metal compound and dodecylbenzenesulfonic acid, DBSA, having one acid group, is used as the protic acid, one zinc atom will react with two acid molecules. As the valence of zinc is thus two and the valence of the acid is one, the ratio between their valences is 2. Thus their molar ratio is, on the basis of the above, 0.2-20. An especially preferable molar ratio is 0.5 E - 2 E, and the best is approx. 1.0 E. When the plasticizer is combined with the principal components of the elastomer composi¬ tion according to the invention, which are a thermoplastic elastomer and a thermoplastic doped aniline polymer, the proportion of the plasticizer may vary widely within the range 0.5-40 % by weight, and there is no critical limit considering the function of the plasticizer. It has, however, been observed that an especially preferable molar ratio of the repeat units of the doped aniline polymer to the molecules of the plasticizer is approx. 0.20-20, preferably approx. 0.3-10. Additional information regarding the metal compound plasticizing the doped aniline polymer can be found in EP application publication 582 919 or US patent 5,340,499, which is incorporated herein by reference. The principal component of the electrically conductive elastomer composition according to the invention and the source of its typical mechanical properties is the thermoplastic elastomer component. As was pointed out in the preamble, by a thermoplastic elastomer is meant a multi-phase composition in which the phases are closely dispersed. The phases are usually chemically bonded to each other by block or graft polymerization, although the protective scope of the invention also covers elastomer components and mixtures which, without chemical bonds, together form a thermoplastic elastomer composition. In the elastomer composition according to the invention, preferably a block polymer is used in which the elastomer chain lengths, i.e. blocks, are made up, on the one hand, of a plurality of mers, i.e. monomer units, of a hard elastomer and, on the other hand, of a plurality of mers of a soft elastomer. Such block polymers include A-B-A-type and (A- SUBSnTUTE SHEET (RULE 26) B) n -type block polymers, in which the A-block is the so-called hard phase and the B-block is the so-called soft, i.e. elastomer, phase. Thus, in a thermoplastic elastomer component according to the invention, A may be any block of a polymer classifiable as a hard ther¬ moplastic, such as a block of polystyrene, polymethyl metacrylate, polypropylene, etc., and B may be any block of a polymer normally classifiable as a soft resin or elastomer, such as polyisoprene, polybutadiene, polyisobutylene, polydimethyl siloxane, polyethyle- ne/alkene, etc. Typical thermoplastic elastomers usable in the invention, having a block¬ like structure, include poly(styrene block - butadiene block - styrene block), poly(styrene block - isoprene block - styrene block), poly(α-methylstyrene block - butadiene block - a- methylstyrene block), poly(o--methylstyrene block - isoprene block - α-methylstyrene block), poly (styrene block - ethylene-cobutene block - styrene block), poly(ethylene block - ethylene-cobutene block - ethylene block), poly(styrene block - dimethylsiloxane block - styrene block), poly(α-methylstyrene block - dimethylsiloxane block - o--methylstyrene block), poly(c--methylstyrene block - dimethylsiloxane block) n , poly(sulfone block - dimethylsiloxane block) n , poly(silfenylenesiloxane block - dimethylsiloxane block) n , poly(urethane block - ester block),., poly(urethane block - ether blocks, poly(ester block - ether blocks, poly(carbonate block - dimethylsiloxane block) n , and poly(carbonate block - ether block!.. Preferred block polymers for use as the thermoplastic elastomer component of the present invention include poly (styrene block - elastomer block - styrene block) (SBC, 44 %), polyolefin-based elastomers (TPO/TPV, 29 %), polyurethane-based elastomers (TPU, 13 %), and polyester-based elastomers (COPE, 5 %). Especially preferable are linear poly(styrene block - ethylenebutene block - styrene block), linear poly(styrene block - butadiene block - styrene block), and branched poly (styrene block - butadiene blocks. Additional information regarding thermoplastic elastomers suitable for an electrically conductive elastomer composition according to the invention can be obtained, for example, from the series Encyclopedy of Polymer Science and Engineering, 2nd edition, 1986, volume 5, pp. 416-430, and from the series Kirk-Othmer, Encyclopedia of Chemical Technology, 3rd edition, volume 6, pp. 626-640. As was pointed out, an electrically conductive thermoplastic elastomer composition according to the invention comprises principally two components, i.e. a thermoplastic elastomer component and a doped plasticized aniline polymer, the latter component possibly containing a plasticizer. According to one preferred embodiment, the proportion of the doped aniline elastomer, or the entity made up of it and the plasticizer, in the total elastomer composition is approx. 1-70 % by weight, more preferably approx. 1.5-50 % by weight, and most preferably approx. 3-30 % by weight. The proportion of the thermoplastic elastomer in the total elastomer composition is preferably approx. 20-99 % by weight, more preferably approx. 50-98 % by weight, and most preferably approx. 70- 95 % by weight. The proportion of plasticizer in the total elastomer composition is preferably approx. 1-35 %, most preferably approx. 2-20 % by weight. An electrically conductive elastomer composition according to the invention may also contain other components. In fact it is clear that it is possible to add to the composition additional components and auxiliaries of thermoplastic elastomers, known in the art, as well as additives and components of doped polymers, and in particular of aniline polymers. Ac¬ cording to one embodiment, the electrically conductive elastomer composition according to the invention contains, in addition to the two components mentioned above, one or more elective plastics components, preferably thermoplastic. The electrical conductivity of the conductive elastomer composition according to the invention depends on the application in a given case. The conductivity may be as low as IO "9 S/cm in the case of antistatic applications, whereas conductivity higher than 0.1 S/cm is required for EMI shielding applications. In addition to an electrically conductive elastomer composition, the present invention also relates to a method for the preparation of an electrically conductive elastomer composi- tion, wherein a thermoplastic elastomer and a doped aniline polymer are contacted and are melt processed into the form of a granulate, powder, fiber, coating, film, sheet, laminate, foam, hose, profile, blend, adhesive, sealant, composite, formed piece, or other melt- processed product or structure. The method according to the invention is characterized that the following components are contacted with each other and melt processed: a) an amount of approx. 10-99 % by weight of a thermoplastic elastomer, b) an amount of approx. 0.5-90 % by weight of a thermoplastic doped aniline polymer which has been obtained by reacting a conjugated homo- or copolymer made up of at least unsubstituted and/or substituted aniline mers with a protic acid functionalized to render the aniline polymer processible. The functionalization is carried out by heating the protic acid together with the aniline polymer to a temperature of 80-250 °C or by heating it together with the aniline polymer and a solvent and by evaporating the solvent. According to one embodiment there is also melt processed: c) an amount of approx. 0.5-40 % by weight of a plasticizer which plasticizes the thermoplastic, doped aniline polymer and promotes its flow. The melt processing is thus carried out while the thermoplastic, doped aniline polymer is in a substantially molten state. The invention is thus based on the fact that, in addition to the thermoplastic elastomer, also the doped aniline polymer behaves thermoplastically, in which case the melt processing concerns two components in molten state and the product will be more homogenous and stronger than previously. The aniline polymer used in the process according to the invention is obtained by causing a conjugated homo- or copolymer, made up of at least unsubstituted and/or substituted aniline mers, to react with a functionalizing protic acid which dopes and at the same time thermoplasticizes the said conjugated homo- or copolymer. In this case the melt proces¬ sing takes place while the doped aniline polymer is in a substantially molten or plastic state. One embodiment of the invention is based on the realization that an electrically conductive elastomer composition can be prepared more easily if the electrically conductive doped aniline polymer used in it is prepared by heating an undoped aniline polymer together with a dopant to a relatively high temperature, whereby the protic acid is functionalized and the behavior of the forming doped aniline polymer will be thermoplastic, in a manner deviating from the previous. It is especially preferable if the said undoped aniline polymer is heated together with the protic acid which dopes it at a temperature of approx. 120- 210 °C, most preferably approx. 150-200 °C. The other characteristics of the method according to the invention are also evident from the above description of the electrically conductive elastomer composition according to the invention. When, in accordance with the present invention, a thermoplastic elastomer, a doped aniline polymer, and possibly a plasticizer are melt processed together, this preferably takes place by means of heat, pressure and shear forces, as in conventional processing of thermoplastics. The apparatus used may be any thermoplastics-processing apparatus, and the temperature is preferably within a range of approx. 80-300 °C. In another embodiment of the invention, an electrically conductive doped polyaniline is plasticized in a suitable solvent, such as ethanol, together with a protonating acid, whereafter the solvent is removed. In this method, also, a protic acid is used which functionalizes polyaniline in such a manner that it plasticizes and compatibilizes the aniline polymer, whereupon it can be melt processed together with some thermoplastic matrix polymer. In the melt-processing method according to the invention for the preparation of an electrically conductive elastomer composition it is also possible to use one or more plasticizers suitable for the plasticizing of the doped aniline polymer component. Such a plasticizer may be a plasticizer presented above in connection with the description of the elastomer composition, and is preferably a metal compound, more preferably a compound of a metal belonging to any of groups 1-4 (IUPAC) of the Periodic Table of the Elements, and most preferably a reaction product of an aromatic sulfonic acid, such as dodecylben- zenesulfonic acid, and a zinc compound, such as zinc oxide or zinc hydroxide. The invention also relates to a method for the preparation of an electrically conductive elastomer composition, wherein a thermoplastic elastomer and a doped aniline polymer are dissolved, at least in part, in an organic solvent, the obtained solution is brought into the desired form, and the solvent is removed, whereupon there remains an electrically conductive elastomer composition which is in a suitable form and is made up of a thermoplastic elastomer and a doped aniline polymer. This solution-processing method is characterized in what is stated in Claim 27, i.e. that the doped aniline polymer is substantially thermoplastic in its properties, i.e. at least in part soluble in an organic solvent, in which case it is obtained by causing a conjugated homo- or copolymer made up of at least unsubstituted and/or substituted aniline mers to react in a solvent with a functionalizing protic acid, which both dopes and plasticizes the said conjugated homo- or copolymer to an electric conductivity of at least approx. 10 " * S/cm. In the dissolving, the doped aniline polymer thus obtained substantially dissolves in the solvent or swells therein. In the solution-processing method the thermoplastic elastomer may be any thermoplastic elastomer referred to above in the discussion of the electrically conductive elastomer composition according to the invention, and the same applies to the doped aniline polymer. The selection of the solvent is not critical in terms of the success of the invention, since an expert in the art will be capable of finding suitable solvents, either with the aid of literature or through empirical experimentation. The essential point is that thermoplasticity, so rare in conductive elastomers, is exploited in the melt-processing method according to the present invention. In the solution-processing method according to the invention it is preferable to use the same components and the same component proportions as in the electrically conductive elastomer composition described above. In addition to a thermoplastic elastomer and a doped aniline polymer, preferably also a plasticizer which plasticizes the doped aniline polymer and is analogous to any of the plasticizer listed above in connection with the elastomer composition is dissolved in an organic solvent. As stated above, an especially preferred plasticizer is a metal compound having a plasticizing effect, preferably a plasticizing compound of a metal belonging to any of groups 1-4 (IUPAC) of the Periodic Table of the Elements. Most preferably the plasticizing compound is a reaction product, with plasticizing effect, of an aromatic sulfonic acid, such as dodecylbenzenesulfonic acid, and a zinc compound, such as zinc oxide or zinc hydroxide. The present invention relates not only to an electrically conductive elastomer composition and a melt-processing method and a solution-processing method for its preparation, but also to any products or structures made from an electrically conductive elastomer composition according to the invention and/or by the above-mentioned methods. Accor¬ ding to one embodiment, the invention thus relates to a granulate, powder, coating, film, sheet, laminate, foam, tube, hose, profile, fiber, blend, adhesive, sealant, composite, formed piece (e.g. extruded piece, molded piece), or other plastics product or structure which has been made from an elastomer mixture made up of a thermoplastic elastomer and a doped aniline polymer and characterized in what is stated in the characterizing clause of Claim 33. The properties and material proportions of the basic components of a completed elastomer product according to the invention are briefly described above in connection with the electrically conductive elastomer composition. The methods of making products according to the invention are also discussed above. For an expert in the art it is also clear that in products according to the invention it is possible to use additives, such as fillers, lubri¬ cants and fluidizers, stabilizers and other anti-aging agents, flame retardants, pigments, foaming agents, bridging agents, and UV-shield agents, etc. It is also clear that an expert in the art will know how to use correct additives in correct proportions. We mention the book Brydson, J.A., Plastics Materials, 4th edition, 1982, pp. 114-145, which is incorpo- rated herein by reference. A product according to the invention also contains a plasticizer which plasticizes the doped aniline polymer component, the plasticizer preferably being a metal compound having a plasticizing effect, more preferably a compound of a metal belonging to any of groups 1-4 (TUPAC) of the Periodic Table of the Elements, most preferably a reaction product of an aromatic sulfonic acid, such as dodecylbenzenesulfonic acid, and a zinc compound, such as zinc oxide or zinc hydroxide. The invention further relates to the use of an electrically conductive elastomer composition described above, or an elastomer product made therefrom, for highly varied purposes, such as an ESD and/or EMI application, an application requiring electrical conductivity and elasticity, an application requiring the retaining of electrical conductivity upon stretching, an application requiring dependence of the electrical conductivity on the extent of elongation, sensors in which electrically conductive rubbers are used, elastomeric coatings, elastomeric adhesive compositions, elastomeric sealants, and elastomeric sealing structures. Below, a number of embodiment examples are presented, their sole purpose being to illustrate the invention. Embodiment examples Process steps Step l In all of the experiments, the polyaniline, metal compound, calcium compound and dodecylbenzenesulfonic acid were first mixed together. The solidification of the polymer complex was carried out advantageously by running the mixture through a screw blender in one or several heating sequences. In terms of operatii-g technology, the same procedure was used in the solidification as is described in previous EP patent applications 545729, 582919 and FI-932578. Thereafter the plasticized PANI complex was dry mixed with the elastomer material (in weight ratios indicated below) in a Buss laboratory compounder MDK E 46, the temperature being 140-170 °C and the rate of feed being 3 kg/h. Elec¬ trical conductivity was measured from the prepared conductive polymer complex, in either tape-like or granulate form. Step 2 The blended granulates were either injection molded or compression molded. Injection molding into ISO 527 test pieces was carried out by using an Engel ES200/50HL apparatus at 170 °C, the mold temperature being 60 °C. The quantity of granulates used for compression molding was 1.5 g, the mold was 60 x 60 x 0.2 mm 3 , compressive force 2 tonnes, preheating time 3 min at 160 °C, compression time 3 min at 160 °C, and cooling to 135 °C. The granulates were compressed into films 0.2 mm thick. Step 3 Electrical conductivity was measured by the 4-probe method from an ISO 527 tensile test piece in unstretched state, and also by the same method from a film in unstretched and in stretched state. Step 4 ISO 527 tensile test pieces were tested mechanically by using an Instron tension apparatus with a tension rate of 500 mm/min. The results are described using tension-elongation functions. The mechanical testing was carried out according to the standard ISO/R 527. Shore A hardness was measured according to the standard ISO 868. Elastomer materials Three types of elastomers were used in the method: S-EB-S A linear triblock polymer, poly(styrene block - (ethylenebutene) block - styrene), type Shell Kraton G 1651 was used. Represents a hydrogenated linear block polymer which does not have double bonds in the soft phase. Polystyrene 32 % (Mw 30,000) Polyfethylenebutene) 68 % (Mw 122,000) S-B-S A linear triblock polymer, poly (styrene block - butadiene block - styrene), type Shell Cariflex TR 1101 was used. A material corresponding to S-EB-S, but contains double bonds in the soft phase. Polystyrene 30 % Butadiene 70 % (S-B-) n A branched poly(styrene block - butadiene block - styrene) (Shell Cariflex TR 1186). Corresponds to linear S-B-S, but the elastomeric phase contains branched chains. Polystyrene 30 % Butadiene 70 % Method Ml The conductive polymer used in the experiments was an emeraldine base form of polyaniline, EB, which was prepared according to the method disclosed in the publication Y. Cao, A. Andreatta, AJ. Heeger and Smith, Polymer, 30 (1989) 2305. Exceptionally, however, sulfuric acid H 2 SO 4 is used in this method instead of hydrochloric acid HC1. The product was dried to a dry matter content of 49.1 %. The doping agent (i.e. counter ion) used was a dodecylbenzenesulfonic acid (DBSA) by the trade name Sulfosoft. The following initial materials (amounts in per cent by weight) were used for the prepara- tion of the polymer complex: EB 6.2 % DBSA Sulfosoft 83.4 % ZnO 8.9 % CaCO 3 1.5 % The materials were mixed together, and a completely plasticized conductive polymer complex was obtained by a conventional screw solidification process. Method M2 Preparation of polyaniline An emeraldine base form of polyaniline, EB, was prepared as in method Ml, but the protic acid now used was HC1. The product was dried to a dry matter content of 95 %. Preparation of PANI(DBSA) 0 . 5 complex by "EB ethanol protonation" A mixture of 8 g of EB (as in method Ml) and 14.4 g of DBSA (Tokyo Kasei) was added to 110 ml of water-free ethanol, which was then stirred and heated at 78 °C for 1 h. Thereafter the ethanol was boiled off under vacuum at 60 °C. When most of the ethanol had evaporated, the remaining powder was dried under vacuum at 50 °C for 24 h. Preparation of Zn(DBS) 2 0.4 kg of zinc oxide ZnO and 1.5 1 ethanol (industrial quality) were stirred for 20 minutes in a Burger reactor. Thereafter 3.21 kg of DBSA (Sulfosoft) was added under stirring, and the mixture was heated to 70 °C. The ethanol was boiled off under vacuum in the course of 24 h at 110 °C, whereafter the mixture was ground by means of dry ice. Blending PANI(DBSA)o. 5 , Zn(DBS) 2 and elastomer powder were crushed and mixed mechanically in a mortar. The produced dry mixture was blended by using a clockwise-rotating conical twin-screw blender at a temperature of 190 °C at 100 rpm (when the elastomer material used was S-EB-S) or at 180 °C at 250.5 rpm (the elastomer being S-B-S or (S-B-)„). The product made was a tape. Compression molding into a film was carried out at 190 °C, preheating 15 s, compression 15 s, whereafter a rapid cooling was carried out between brass plates. EXAMPLES Example 1 By using method Ml, a mixture was prepared from a PANI complex prepared by the procedure described above and an elastomer copolymer S-EB-S (Shell Kraton G 1651) at the mass ratio PAN S-EB-S 10 :90% The properties obtained as a result were as follows: Conductivity Elongation Strength (S/cm) (%) (MPa) Buss tape 1,8 IO "3 ISO 527 9,5 IO "5 166 2,8 Film 0,077 The conductivity of this elastomer mixture was also examined as a function of the elongation, and the results are shown in Figure 1. The vertical axis in the figure rep¬ resents the ratio of the conductivity of stretched film to that of unstretched film, σ/σ(o), and the horizontal axis represents the elongation (%). The figure shows that the electrical conductivity of the elastomer mixture increases only to approx. 1.5-fold at an elongation of approx. 100-200 % , and still at an elongation of 400 % the conductivity is the same as that of an unstretched mixture. Example 2 In accordance with method Ml, a mixture was prepared from a PANI complex and an elastomer copolymer S-EB-S (Shell Kraton G 1651) at the mass ratio PANI:S-EB-S 20%:80%. On this elastomer mixture, the change in electrical conductivity upon the reversal of the elongation was examined. In the experiment the mixture was stretched 50 %, and the elongation was allowed to reverse while the conductivity of the film was being measured. These results are shown in Figure 2. The vertical axis in the figure represents the ratio of the conductivity of stretched film to that of unstretched film, σ/σ(o), and the horizontal axis represents the time (s) from the reversal of the elongation. This figure shows that the conductivity of the elastomer mixture is increased to only approx. 1.7-fold at an elonga¬ tion of 50 %, and after the reversal of the elongation the conductivity rapidly returns to the same level as that of an unstretched mixture. Example 3 By using method M2 in the manner described above, 0.063 g of PANI(DBSA)o 5 , 0.182 g of Zn(DBS) 2 and 3.255 g of an elastomer copolymer S-EB-S (Shell Kraton G 1651) were blended. The obtained conductivity was 3.4 10" 4 S/cm. After a stretching of 50 %, the permanent elongation of the product made from the mixture was less than 15 %. Example 4 In accordance with method Ml, a mixture of a PAJNI complex and an elastomer copoly¬ mer S-B-S (Shell Cariflex TR 1101) was prepared at the mass ratio PAN S-B-S 10% :9- 0%. After a stretching of 50 %, the permanent elongation of the product made from the mixture was less than 10 %. Example 5 In accordance with method Ml, a mixture of a PANI complex and an elastomer copoly¬ mer S-B-S (Shell Cariflex TR 1101) was prepared at the mass ratio PAN S-B-S 20%:8- 0%. After a stretching of 50 %, the permanent elongation of the product made from the mixture was less than 15 %. Example 6 In accordance with method Ml, a mixture of a PANI complex and an elastomer copoly¬ mer (S-B-) n (Shell Cariflex TR 1186) was prepared at the mass ratio PANI^S-B , 10%:90%. After a stretching of 50 %, the permanent elongation of the product made from the mixture was less than 10 %. Example 7 In accordance with method Ml, a mixture of a PANI complex and an elastomer copoly¬ mer (S-B-) n (Shell Cariflex TR 1186) was prepared at the mass ratio PAN φ-BL. 20%:80%. After a stretching of 50 %, the permanent elongation of the product made from the mixture was less than 15 % . Table 1 Ex. PAN elastom. Test piece Conductivity Elongation Stregth No. % by weight (S/cm) (%) (MPa) 1 10:90 S-EB-S Buss tape 1,8 IO "3 ISO 527 9,5 IO "5 166 2,8 Film 0,077 2 20:80 S-EB-S Buss tape 9,9 IO "3 ISO 527 4,4 IO *4 171 2,97 Film 0,235 3 7:93 S-EB-S Film 3,4 IO "4 50 4,2 4 10:90 S-B-S Buss tape < 10 '9 ISO 527 < 10 "9 812 9,48 Film < ισ 9 5 20:80 S-B-S Buss tape 4,7 IO "4 ISO 527 7,2 IO 4 654 5,2 Film 1,9 IO "4 6 10:90 (S-B-) n Buss tape 3,6 IO "8 ISO 527 < 10 "9 918 6,15 Film < ιo- 9 7 20:80 (S-B-) n Buss film 1.7 IO "4 ISO 527 6.8 IO "5 244 2,74 Film 2,6 IO "3

Claims: Claims 1. An electrically conductive, thermoplastic elastomer composition which comprises a thermoplastic elastomer and a doped aniline polymer, characterized in that the elastomer returns substantially to its former shape (at least 85 %) after a stretching of 50 %, the electrical conductivity of the elastomer remains at substantially the same level during the stretching (decreases less than one decade), and upon the returning to its shape of the elastomer its electrical conductivity does not weaken substantially (decreases less than one decade). 2. An electrically conductive, thermoplastic elastomer composition according to Claim 1, characterized in that it comprises a) an amount of approx. 10-99 % by weight of a thermoplastic elastomer and b) an amount of approx. 0.5-90 % by weight of an aniline polymer which is a conjuga- ted homo- or copolymer made up of at least an unsubstituted and/or substituted aniline mer which is doped with a protic acid, the protic acid functionalizing it in such a way that the aniline polymer is melt-processible or solution-processible. 3. An electrically conductive, thermoplastic elastomer composition according to Claim 2, character-zed in that it additionally comprises c) an amount of approx. 0.5-40 % by weight of a plasticizer which plasticizes the doped aniline polymer and promotes its flow. 4. A composition according to any of the above claims, characterized in that the plasticizer which plasticizes the doped aniline polymer and promotes its flow is a metal compound the softening point of which is below approx. 300 °C and/or which adjusts the pH of the doped aniline polymer to the range 3-8. 5. An electrically conductive, thermoplastic elastomer composition according to any of the above claims, characterized in that the said aniline polymer is protonated by heating it together with the said functionalizing protic acid to a temperature of approx. 80-250 °C, preferably to a temperature of approx. 120-210 °C, most preferably to a temperature of approx. 150-200 °C. 6. An electrically conductive, thermoplastic elastomer composition according to Claim 5, characterized in that the said aniline polymer is protonated by heating it, together with a protic acid which functionalizes it, by using blending shear forces of the type used in the melt processing of plastics, preferably by using an apparatus designed for the melt processing of plastics. 7. An electrically conductive, thermoplastic elastomer composition according to any of Claims 1-4, characterized in that the said aniline polymer is protonated by heating it, together with a protic acid which functionalizes it, in a solvent and by removing the solvent by evaporation. 8. An electrically conductive, thermoplastic elastomer composition according to Claim 7, characterized in that the solvent is a C,-C 10 alcohol, preferably ethanol. 9. A composition according to any of Claims 2-8, characterized in that the doping protic acid is a non-oxidizing organic protic acid, preferably an aromatic sulfonic acid, and most preferably dodecylbenzenesulfonic acid. 10. A composition according to any of Claims 5-9, characterized in that the molar ratio of the conjugated homo- or copolymer made up of at least unsubstituted and/or substituted aniline mers to the protic acid which dopes it is in the heated reaction within a range of approx. 0.05-3.0, preferably within a range of approx. 0.1-1.0, and most preferably within a range of approx. 0.125-0.5. 11. A composition according to any of Claims 4-10, characterized in that the metal in the metal compound with a plasticizing effect is a metal belonging to any of groups 1-4 (IUPAC) of the Periodic Table of the Elements, preferably zinc. 12. A composition according to any of Claims 4-11, characterized in that the plasticizer is a metal salt of a protic acid, preferably a non-oxidizing organic protic acid, more preferably an aromatic sulfonic acid, and most preferably dodecylbenzenesulfonic acid. 13. A composition according to any of Claims 4-12, characterized in that the plasticizer is a reaction product of a zinc compound and an aromatic sulfonic acid, the reaction product being preferably obtained by contacting zinc oxide or zinc hydroxide with dodecylbenzenesulfonic acid at an elevated temperature. 14. A composition according to any of Claims 3-13, characterized in that the molar ratio of the repeat units of the thermoplastic doped aniline polymer to the molecules of the plasticizer is within a range of approx. 0.20-20, preferably approx. 0.3-10. 15. A composition according to any of the above claims, characterized in that the thermoplastic elastomer is a block polymer of a monomer of one or several types, forming a hard polymer, and a monomer of one or several types, forming a soft polymer, preferably a block copolymer of styrene and a monomer which forms a soft polymer, more preferably a polystyrene block - conjugated diene block - styrene block) or poly (styrene block - (ethylene-1-alkene block) - styrene block) copolymer, most preferably a poly(styrene block - butadiene block - styrene block) or poly(styrene block - (ethylene¬ butene) block - styrene block) copolymer, or a combination or mixture thereof. 16. A composition according to any of the above claims, characterized in that the proportion of the thermoplastic elastomer in the total elastomer composition is approx. 20- 99 % by weight, preferably approx. 50-98 % by weight, most preferably approx. 70- 95 % by weight. 17. A composition according to any of the above claims, characterized in that the proportion of the melt-processible, doped aniline polymer in the total elastomer composi- tion is approx. 1-70 % by weight, preferably approx. 1.5-50 % by weight, and most preferably approx. 3-30 % by weight. 18. A composition according to any of Claims 3-17, characterized in that the proportion of the plasticizer in the total elastomer composition is approx. 1-35 % by weight, preferably approx. 2-20 % by weight. 19. A composition according to any of the above claims, characterized in that it addi¬ tionally contains one or more elective plastics components, preferably thermoplastic. 20. A method for the preparation of an electrically conductive, thermoplastic elastomer composition, wherein a thermoplastic elastomer and a doped aniline polymer are contacted and are melt processed into the form of a granulate, powder, fiber, coating, film, sheet, laminate, foam, tube, hose, profile, blend, adhesive, sealant, composite, formed piece (e.g. extruded piece, molded piece), or other melt-processed product or structure, characterized in that a) an amount of approx. 10-99 % by weight of a thermoplastic elastomer, b) an amount of approx. 0.5-90 % by weight of a thermoplastic doped aniline polymer which is obtained by reacting a conjugated homo- or copolymer, made up of at least unsubstituted and/or substituted aniline mers, are contacted and melt processed with a protic acid which has a functionalizing effect so that the aniline polymer is melt processi¬ ble, the melt processing taking place while the thermoplastic doped aniline polymer is in substantially molten state. 21. A method according to Claim 20, characterized in that in addition to components a) and b), also c) an amount of approx. 0.5-40 % by weight of a plasticizer which plasticizes the thermoplastic doped aniline polymer and promotes its flow is contacted and processed. 22. A method according to Claim 21, characterized in that the plasticizer which plasticizes the doped aniline polymer and its flow is a metal compound which has a softening point below approx. 300 °C and/or which adjusts the pH of the doped aniline polymer to the range 3-8. 23. A method according to Claim 20, characterized in that the plasticizer is a metal compound, preferably a compound of a metal belonging to any of groups 1-4 (IUPAC) of the Periodic Table of the Elements, most preferably a reaction product of an aromatic sulfonic acid, such as dodecylbenzenesulfonic acid, and a zinc compound, such as zinc oxide or zinc hydroxide. 24. A method according to any of Claims 20-23, characterized in that a thermoplastic elastomer and a doped aniline polymer are melt processed into the said electrically conductive elastomer composition at a temperature of 80-300 °C. 25. A method according to any of Claims 20-24, characterized in that the said aniline polymer is heated, together with a protic acid which functionalizes it, to a temperature of approx. 80-250 °C, preferably to a temperature of approx. 120-210 °C, most preferably to a temperature of approx. 150-200 °C. 26. A method according to any of Claims 20-24, characterized in that the said aniline polymer is heated, together with a protic acid which functionalizes it, in a solvent and the solvent is evaporated off. 27. A method for preparing an electrically conductive thermoplastic composition, wherein a thermoplastic elastomer and a doped aniline polymer are dissolved, at least in part, in an organic solvent, the obtained solution is brought to the desired form, and the solvent is removed, whereupon there is left an electrically conductive elastomer composition in a suitable form, made up of a thermoplastic elastomer and a doped aniline polymer, characterized in that a) an amount of approx. 10-99.5 % by weight of a thermoplastic elastomer, b) an amount of approx. 0.5-90 % by weight of a thermoplastic doped aniline polymer which is obtained by reacting a conjugated homo- or copolymer, made up of at least unsubstituted and/or substituted aniline mers, are dissolved together with a protic acid which has a functionalizing effect so that the aniline polymer is solution processible, the doped aniline polymer substantially dissolving in the solvent or swelling therein. 28. A method according to Claim 27, characterized in that in addition to components a) and b), also c) an amount of approx. 0.5-40 % by weight of a plasticizer which plasticizes the thermoplastic doped aniline polymer and promotes its flow is dissolved. 29. A method according to Claim 28, characterized in that the plasticizer which plasticizes the doped aniline polymer and promotes its flow is a metal compound the softening point of which is below approx. 300 °C and/or which adjusts the pH of the doped aniline polymer to the range 3-8. 30. A method according to any of Claims 27-29, characterized in that the plasticizer is a metal compound with a plasticizing effect, preferably a plasticizing compound of a metal belonging to any of groups 1-4 (IUPAC) of the Periodic Table of the Elements, most preferably a reaction product of an aromatic sulfonic acid, such as dodecylbenzenesulfonic acid, and a zinc compound, such as zinc oxide or zinc hydroxide. 31. A method according to any of Claims 27-29, characterized in that the said aniline polymer is heated, together with a protic acid which functionalizes it, to a temperature of approx. 80-250 °C, preferably to a temperature of approx. 120-210 °C, most preferably to a temperature of approx. 150-200 °C. 32. A method according to any of Claims 27-29, characterized in that the said aniline polymer is heated, together with a protic acid which functionalizes it, in a solvent and the solvent is evaporated off. 33. A granulate, powder, coating, film, sheet, laminate, foam, tube, hose, profile, fiber, blend, adhesive, sealant, composite, formed piece (e.g. extruded piece, molded piece) or other elastomer product or structure which is made from an elastomer mixture made up of a thermoelastic polymer and a doped aniline polymer, characterized in that the elastomer mixture comprises a) an amount of approx. 10-99.5 % by weight of a thermoplastic elastomer, b) an amount of approx. 0.5-90 % of a thermoplastic doped aniline polymer which is obtained by reacting a conjugated homo- or copolymer, made up of at least unsubstituted and/or substituted aniline mers, with a protic acid which has functionalizing effect so that the aniline polymer is solution processible and melt processible. 34. A product according to Claim 33, characterized in that in addition to components a) and b) it also comprises c) an amount of approx. 0.5-40 % by weight of a plasticizer which plasticizes the thermoplastic doped aniline polymer and promotes its flow. 35. A product according to any of Claims 33-34, characterized in that the plasticizer is a metal compound with a plasticizing effect, preferably a compound of a metal belonging to any of groups 1-4 (IUPAC) of the Periodic Table of the Elements, most preferably a reaction product of an aromatic sulfonic acid, such as dodecylbenzenesulfonic acid, and a zinc compound, such as zinc oxide or zinc hydroxide. 36. A product according to any of Claims 33-35, characterized in that the said aniline polymer is heated, together with a protic acid functionalizing it, to a temperature of approx. 80-250 °C, or it is heated together with the said aniline polymer and a solvent and the solvent is evaporated off. 37. The use of a composition according to any of Claims 1-19 or a granulate, powder, coating, film, sheet, laminate, foam, tube, hose, profile, fiber, blend, adhesive, sealant, composite, formed piece (e.g. extruded piece, molded piece) or other plastics product or structure according to any of Claims 33-35 for an ESD and/or EMI application, for an application requiring electrical conductivity and elasticity, for an application requiring the retaining of electrical conductivity upon stretching, for an application requiring the dependence of the electrical conductivity on the amount of elongation, for sensors in which electrically conductive thermoplastic elastomers are used, for elastomeric coatings, for elastomeric adhesive compositions, for elastomeric sealants, and for elastomeric sealing structures.

Inventors: IKKALA OLLI, KIRMANEN PAULI, SAVOLAINEN ESKO, VIRTANEN ESA, IKKALA, OLLI, KIRMANEN, PAULI, SAVOLAINEN, ESKO, VIRTANEN, ESA
Applicants: IKKALA OLLI, KIRMANEN PAULI, NESTE OY, SAVOLAINEN ESKO, VIRTANEN ESA, IKKALA, OLLI, KIRMANEN, PAULI, SAVOLAINEN, ESKO, VIRTANEN, ESA
Application year: 1995
Main classification: H01B1
IPC codes: C08L79, H01B1