Silicone coated base material and air bag base material

Abstract: A material in the form of polyamide fibers, polyester fibers, woven and non-woven fabric thereof, thermoplastic elastomer, and polyurethane sheet is coated with a silicone coating composition to a thickness of 5 to 20 µm, obtaining a silicone coated base material. The silicone coating composition contains (A) an organopolysiloxane having at least two alkenyl groups, (B) an organohydrogenpolysiloxane having at least two hydrogen atoms, (C) an organic silicon compound having at least one hydrogen atom and at least one epoxy and/or trialkoxysilyl group, (D) a carbon, NiO₂, FeO, FeO₂, Fe₂O₃, Fe₃O₄, CoO₂, CeO₂ or TiO₂ powder having a mean particle size of up to 20 µm, and (E) a platinum catalyst. The silicone coated base material is flame resistant and fully acceptable in practical use even though the silicone coating is as thin as 5 to 20 µm, namely less than about one-half of the conventional coating thickness.

Description: This invention relates to a silicone coated base material having a silicone coating formed on a base material. It also relates to an air bag base material. Most coating compositions used for automotive air bags in the prior art are chloroprene resin blends. The chloroprene resin blends are also used in treating fibrous base materials in the form of woven, knitted and non-woven fabrics of polyamide fibers e.g. by impregnation, coating or lamination. The resulting composite materials have excellent properties inherent to both the polyamide fibers and chloroprene resin and are useful in a variety of applications. However, these composite materials have some drawbacks. They tend to gradually lose their strength when they are allowed to stand above a certain temperature over a long term because the chloroprene resin releases hydrogen chloride which acts to scissor amide bonds of the polyamide fibers. Since the chloroprene resin is relatively hard, the resin excessively restrains polyamide fibers of the fibrous base material in the composite material, preventing free motion of the fibers. The composite materials therefore have relatively hard feel or suitability, and low tear strength. To overcome these drawbacks, it has been proposed to use coating compositions mainly comprising silicone resins, which are superior to chloroprene resins in heat resistance, weathering, and flexibility. Typical known compositions are blends of a heat vulcanizable silicone resin and a tackifier and blends of an addition - curing type silicone rubber and a tackifier. See e.g. EP-A-543 401 and EP-A-553 840. These silicone coating compositions are applied to base materials of air bags, particularly for automobiles or the like to form coatings thereon which are generally about 40 µm thick. However, to meet the demand for lightweight, compact and low cost products, it is desirable to reduce the coating thickness. As the coating thickness is reduced, the conventional coating compositions tend to increase in burn rate. When they are applied to air bags, e.g. for automobiles, thin coatings permit the air bags to puncture upon explosive expansion of an inflator. As a result, the air bags lose air tightness and are impractical. A general aim herein is to provide new and useful silicone-coated materials such as air bag substrate materials. One preferred aim is to provide a silicone coated base material which remains fully flame resistant even when the silicone coating is thin. Another preferred aim is to provide a silicone coated base material for use in air bags, particularly for automobiles, which maintains the air bag function upon explosive expansion of an inflator when the silicone coating is formed to a thickness of 5 to 20 µm. The invention uses a silicone coating composition comprising (A) 100 parts by weight of an organopolysiloxane having at least two alkenyl groups each directly bonded to a silicon atom in a molecule, (B) an organohydrogenpolysiloxane having at least two hydrogen atoms each bonded to a silicon atom (i.e. SiH groups) in a molecule, in a sufficient amount to give 0.5 to 4 silicon-bonded hydrogen atoms per alkenyl group in component (A), (C) 0.1 to 10 parts by weight of an organic silicon compound having in a molecule at least one hydrogen atom bonded to a silicon atom and at least one epoxy and/or trialkoxysilyl group bonded to a silicon atom through a carbon atom directly bonded to the silicon atom, for example through an alkylene group such as methylene, ethylene, and propylene group, (D) 0.1 to 100 parts by weight of at least one powder having a mean particle size of up to 20 µm selected from the group consisting of carbon, NiO 2 , FeO, FeO 2 , Fe 2 O 3 , Fe 3 O 4 , CoO 2 , CeO 2 , and TiO 2 , (E) a catalytic amount of a platinum catalyst, (F) up to 1 part by weight of benzotriazole and/or benzimidazole, and (G) 5 to 100 parts by weight of reinforcing silica. Note that components (F) and (G) are optional. This silicone coating composition is applied to a base material to form a coating from 5 to 20 µm thick on at least a portion of the base material. The base material may be selected from the group consisting of polyamide fibers, polyester fibers, woven and non-woven fabrics thereof, thermoplastic elastomers, and polyurethane sheets. In our work we find that even with thickness of about 5 to 20 µm, which is thinner than the conventional coatings about 40 µm thick, the resulting silicone coated base material is fully flame resistant and acceptable in practical use. Particularly when such silicone-coated base material is used in air bags, for example for automobiles, it can maintain the air bag function upon explosive expansion of an inflator. Therefore in one aspect we provide a silicone coated base material comprising a base material and a coating, 5 to 20 µm thick, formed thereon from a silicone coating composition comprising components (A) to (E), preferably further comprising components (F) and (G). In another aspect we provide an air bag base material having a coating of the composition. In the prior art we note that EP-A-553840 describes a solventless liquid silicone rubber coating composition for coating air bag fabric. The composition may include components corresponding to components (A), (B), (C), (E) above, and inorganic filler. The filler is for reinforcement, viscosity adjustment, improving heat resistance and flame retardancy. The listed fillers include titanium oxide and iron oxide of unspecified particle size. The examples used only silica filler, in coatings of conventional thickness. DETAILED DESCRIPTION In silicone coating compositions disclosed herein, component (A) is organopolysiloxane having at least two alkenyl groups each directly bonded to a silicon atom in a molecule. The organopolysiloxane (A) may have the following average compositional formula: R 1 n R 2 m SiO 4-n-m 2 wherein R 1 represents an unsubstituted or substituted monovalent hydrocarbon group not containing aliphatically unsaturated bonds, R 2 represents an alkenyl group, and letters n and m are positive numbers satisfying the relationship: 0.7 < n < 2.2, 0 < m ≦ 0.1 and 0.8 < m + n ≦ 2.2. It may take a straight chain, branched, network or three-dimensional resinous structure or a mixture thereof. The organopolysiloxane is preferably straight chain diorganopolysiloxane in which the main chain is composed basically of diorganosiloxane recurring units and end - blocked with triorganosilyl groups. The alkenyl groups are bonded to silicon atoms at molecule ends and/or in the intermediate portion of the main chain of the molecule. Preferably, alkenyl groups are bonded to silicon atoms at both molecule ends from the viewpoint of a curing rate and a cured product physical property. The alkenyl group, preferably having 2 or 8 carbon atoms, bonded to a silicon atom which are denoted by R 2 in the general compositional formula is exemplified by vinyl, allyl, 1-propenyl, isopropenyl, 1-butenyl, 3-butenyl, isobutenyl and hexenyl groups while the vinyl group is most preferred because of ease of synthesis and chemical stability. Organic groups bonded to a silicon atom other than the alkenyl group, which are denoted by R 1 in the general compositional formula include unsubstituted or substituted monovalent hydrocarbon groups not having aliphatic unsaturated bonds, and usually having 1 to 10 carbon atoms, for example, alkyl groups such as methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tert-butyl, hexyl, octyl and decyl groups, aryl groups such as phenyl, tolyl, xylyl and naphthyl groups, cycloalkyl groups such as cyclohexyl, aralkyl groups such as benzyl and phenylethyl groups, halogen-substituted or cyano-substituted such hydrocarbon groups, such as chloromethyl, bromoethyl, trifluoropropyl and cyanoethyl groups. Preferably all organic groups other than alkenyl groups are methyl groups or a mixture of methyl and phenyl groups because of ease of synthesis and chemical stability. The organopolysiloxanes preferably have a viscosity of at least 100, generally 100 to 10,000,000 centistokes at 25°C, more preferably at least 500, for example, 500 to 1,000,000 centistokes at 25°C. With a viscosity of less than 100 centistokes, a cured product may be weak and brittle and a coated base material may become hard. With a viscosity of more than 10,000,000 cs, workability may become lowered and a lot of diluting solvents may be required upon application by coating or screen printing. These siloxanes can be synthesized by conventional well - known processes. Component (B) in the form of organohydrogenpolysiloxane is an essential component for forming a silicone cured product having practically acceptable strength by undergoing addition reaction (i.e. hydrosilylation reaction) with alkenyl groups in component (A) in the presence of component (E) for curing the silicone coating composition. Organohydrogenpolysiloxane (B) may accord with the average compositional formula: R 3 a H b SiO 4-a-b 2 wherein R 3 represents an unsubstituted or substituted monovalent hydrocarbon group, and letters a and b are positive numbers satisfying the relationship: 0.5 < a < 2.2, 0.002 ≦ b ≦ 1 and 0.8 < a + b ≦ 3. The organohydrogen-polysiloxane should have at least two, preferably at least three hydrogen atoms each bonded to a silicon atom (i.e. SiH group) in a molecule. The hydrogen atoms are directly bonded to silicon atoms at molecule ends and/or in the intermediate portion of the main chain of the molecule. Its molecular structure is not critical and any of commonly available organohydrogenpolysiloxanes, for example, of a straight chain, branched, cyclic or three-dimensional resinous structure may be used. Organic groups bonded to a silicon atom, which are denoted by R 3 in the general compositional formula include unsubstituted or substituted monovalent hydrocarbon groups, preferably not having aliphatic unsaturated bond, and having 1 to 10 carbon atoms, for example, alkyl groups such as methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tert-butyl, hexyl, octyl and decyl groups, aryl groups such as phenyl, tolyl, xylyl and naphthyl groups, cycloalkyl groups such as cyclohexyl, aralkyl groups such as benzyl and phenylethyl groups, halogen-substituted or cyano-substituted such hydrocarbon groups such as chloromethyl, bromoethyl, trifluoropropyl and cyanoethyl groups. Preferably all organic groups are methyl groups or a mixture of methyl and phenyl groups as in component (A). The organohydrogenpolysiloxanes preferably have a viscosity of up to 300, normally 0.1 to 300, more preferably 1 to 200 centistokes at 25°C. With a viscosity of more than 300 centistokes, compatibility with component (A) would sometimes be low. Component (B) is preferably used in such amount that the amount of silicon-bonded hydrogen atoms (i.e. SiH groups) in component (B) is 0.5 to 4 equivalents, preferably 1 to 3 equivalents per alkenyl group in component (A). With less than 0.5 equivalent, cured products may have low mechanical strength whereas an amount of more than 4 equivalents increases the likelihood of blowing upon curing. Component (C) in the form of organic silicon compound is a component for rendering silicone coatings adhesive to substrates e.g. polyamide fibers, polyester fibers, woven and non-woven fabrics thereof, thermoplastic elastomers, and polyurethane sheets. There may be used any of organic silicon compounds, for example organosilanes and linear, cyclic or branched organo(poly)siloxanes, having in a molecule at least one, preferably two or more hydrogen atom(s) each bonded to a silicon atom (i.e. SiH groups) and at least one epoxy and/or trialkoxysilyl group bonded to a silicon atom through a carbon atom (for example, through an alkylene group such as methylene, ethylene, propylene, etc.) directly bonded to the silicon atom. Examples of the epoxy and trialkoxysilyl groups bonded to a silicon atom through a carbon atom include: and wherein R 4 is an alkyl group or alkoxy-substituted alkyl group having 1 to 4 carbon atoms, and letter c is 1, 2, 3 or 4. Those having a linear or cyclic polysiloxane skeleton are preferred because of ease of synthesis. In the cyclic polysiloxane skeleton, siloxane rings constructed by 3 to 6 silicon atoms, more preferably 4 silicon atoms are preferred for ease of synthesis. In the case of linear polysiloxane skeletons, siloxane chains are preferably constructed by about 5 to 50 silicon atoms, though not limited thereto, because higher molecular weights lead to higher viscosity and are inconvenient to synthesize or handle. Component (C) may have an organic group bonded to a silicon atom in addition to the hydrogen atom bonded to a silicon atom (SiH group) and the trialkoxysilyl group and/or the epoxy group. The organic group bonded to a silicon atom is an unsubstituted or substituted monovalent hydrocarbon group having 1 to 10 carbon atoms and preferably not containing aliphatically unsaturated bonds, as exemplified for R 3 . Such organic silicon compounds may be prepared by effecting partial addition reaction of an organic compound having an alkenyl group and an epoxy and/or trialkoxysilyl group with an organohydrogenpolysiloxane having at least three hydrogen atoms each attached to a silicon atom in a molecule, in a conventional manner. The reaction mixture may be used simply after removing the unreacted compounds and addition reaction catalyst at the end of reaction. Desirably, the end product is isolated from the reaction mixture before use. Examples of the organic silicon compound used as component (C) are those cyclic or linear organopolysiloxanes having the following structures. The amount of component (C) is usually 0.1 to 10 parts, preferably 0.5 to 5 parts by weight per 100 parts by weight of component (A). On this basis, less than 0.1 part of component (C) may give insufficient adhesion whereas more than 10 parts of component (C) may cause blowing upon curing and result in cured products having low mechanical strength. Component (D) is to impart high-temperature resistance to the coated base material. It is carbon, NiO 2 , FeO, FeO 2 , Fe 2 O 3 , Fe 3 O 4 , CoO 2 , CeO 2 , TiO 2 or a mixture of two or more of them. It is in the form of finely divided powder particles having a mean particle size of up to 20 µm, normally of from 0.01 to 20 µm, preferably of from 0.02 to 10 µm, more preferably of from 0.02 to 1 µm. Particles with a mean particle size of more than 20 µm are inadequate for thin coatings which are as thin as 5 to 20 µm because the thin coatings become irregular on their surface. It may be difficult to obtain even particles having a mean particle size of less than 0.01 µm because agglomerates may not be so finely divided to give smaller size particles. The amount of component (D) is usually 0.1 to 100 parts, preferably 0.5 to 20 parts by weight per 100 parts by weight of component (A). On this basis, less than 0.1 part of component (D) may give insufficient high-temperature resistance whereas more than 100 parts of component (D) may adversely affect the physical properties of cured coatings, resulting in coated base materials having insufficient physical properties. A platinum catalyst is used as component (E) of the silicone coating composition and is selected from platinum and platinum compounds which are commonly used in hydrosilylation reaction. Examples are platinum black, chloroplatinic acid, alcohol modified chloroplatinic acid, complexes of platinum with olefins or aldehydes, and complexes of platinum with vinylsiloxanes. Component (E) is used in a catalytic amount which may be properly adjusted in accordance with a desired curing rate. Often the platinum catalyst is used in an amount of 0.5 to 200 ppm, preferably 1 to 100 ppm of platinum atom based on the weight of components (A), (B) and (C) combined. With less than 0.5 ppm of the catalyst, short curing may result or curing require a higher temperature and longer time. More than 200 ppm of the catalyst may make it difficult to control curing reaction and be costly. If desired, benzotriazole and/or benzimidazole is blended as component (F) in the silicone coating composition. It is effective for further improving the high - temperature resistance of a silicone coated base material It may be added in an amount of up to 1 part, normally 0.01 to 1 part, preferably of 0.05 to 0.5 part by weight per 100 parts by weight of component (A). Such minor amounts of the compound are fully effective for improving high-temperature resistance. More than 1 part of component (F) might however retard curing of a silicone coating composition which becomes less effective in working. A good and useful composition can be achieved without component (F) although addition of component (F) ensures further improved high-temperature resistance. It is also recommended to blend reinforcing silica as component (G) in the silicone coating composition. The reinforcing silica is added for enhancing the mechanical strength of cured coatings and may be selected from well-known ones commonly used in conventional silicone rubbers. Preferably, the reinforcing silica has a specific surface area of more than 50 m 2 /g, especially 50 to 500 m 2 /g by BET method. Examples include fumed silica, precipitated silica, fired silica, ground quartz, diatomaceous earth alone or in admixture of two or more. The reinforcing silica may be used as such. Preferably, it is treated with organic silicon compounds such as methylchlorosilanes, dimethylpolysiloxane, and hexamethyldisilazane for imparting smooth flow to a silicone coating composition. Component (G) is usually in an amount of up to 100 parts, preferably 5 to 100 parts, more preferably 10 to 70 parts by weight per 100 parts by weight of component (A). Less than 5 parts of silica is often less effective for reinforcement whereas more than 100 parts of silica often adversely affects the flow and workability of a silicone coating composition. In the silicone coating compositions disclosed herein, an adhesion promoter, reaction controller and other additives may be blended in addition to the above - mentioned components. Another type of organopolysiloxane may be further blended. Such additives which can be additionally blended include adhesion promoters, which are typically organosilane compounds (often referred to as silane coupling agent) having two or three alkoxy groups and a functional group (e.g. alkenyl group, acryloxy group, methacryloxy group, glycidoxy group, etc.), such as vinyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-acryloxypropyltrimethoxysilane, and 3 - glycidoxypropyltrimethoxysilane, reaction controllers such as methylvinylcyclopolysiloxane, acetylene alcohols, and triallylisocyanurate, plasticizers such as non-functional dimethylpolysiloxane, and viscosity modifiers. Also silicone resins consisting basically of SiO 2 and R 3 SiO 1/2 units optionally also comprising R 2 SiO 2/2 or RSiO 3/2 units (wherein R is a monovalent hydrocarbon group as defined in R 2 ), containing at least one alkenyl group such as vinyl group in a molecule and soluble in silicone oil may be used as a mechanical strength enhancer. These additives may be added in any desired amount as long as the basic function of the composition is not impaired. The silicone coating composition may start curing when all the components, especially components (A), (B) and (E), are mixed, because component (E) promotes reaction between components (A) and (B). Therefore, it is recommended to add an effective reaction inhibitor, for example, triallylisocyanurate and acetylene alcohols or to keep the composition in two separate portions, that is, a major component group and a curing agent group so that all the components are uniformly mixed on use. The division into two groups is not particularly limited provided that components (A), (B) and (E) are not present in a common group. For example, the composition is divided into a main group of (A) to (D) and a group of (E) or into a main group of part of (A) + (D) + (E) and a curing agent group of (B) + (C). The silicone coating composition may be used in a solventless system, an aqueous emulsion system or a system diluted with an organic solvent such as toluene. In any case, the composition is usually adjusted to a viscosity of 1 to 50,000 centipoise, preferably 10 to 30,000 centipoise at 25°C before it is applied to a base material (or substrates) selected from the group consisting of polyamide fibers, polyester fibers, woven and non - woven fabrics thereof, thermoplastic elastomers, and polyurethane sheets.A coating is formed, preferably to a dry thickness of about 5 to 20 µm. For the application purpose, coating, impregnation and spraying techniques are used. If the viscosity of the composition exceeds 50,000 centipoise, it is difficult to form a uniform coating of 5 to 20 µm thick. After application, the coating is generally cured by heating at 60 to 180°C for 1/10 to 10 minutes. In this way, there is obtained a silicone coated base material (or substrates) in which a base material (or substrates) desirably selected from the group consisting of polyamide fibers, polyester fibers, woven and non-woven fabrics thereof, thermoplastic elastomers, and polyurethane sheets which is entirely or partially covered with a coating of the silicone coating composition to a thickness of 5 to 20 µm. Uniqueness resides in a composite combination of the above-defined silicone coating composition with various base materials (or substrates), typically fibrous base materials in the form of polyamide fibers, polyester fibers, woven and non - woven fabrics thereof. More particularly, coatings of silicone coating composition which are 5 to 20 µm thick, stand alone, will often readily burn. By combining such coatings with the above-mentioned base materials (or substrates), especially fibrous base materials, quite unexpectedly, a flame propagating rate and length can be reduced. There are obtained practically fully acceptable coated base materials although their coating thickness may be less than about one - half of the conventional coating thickness. Therefore, the silicone coated base materials as described herein in which a coating of the silicone coating composition is formed on a fibrous base material are advantageously used as an air bag base material. When the fibrous base material is used to form an air bag, a silicone coating is normally formed on the entire surface of the fibrous base material, but may sometimes be formed on only that region of the fibrous base material which comes in contact with explosion residues of an inflator. There has been described a silicone coated base material which is flame resistant and fully acceptable in practical use even though a coating of a silicone coating composition on a base material (or substrates) is as thin as 5 to 20 µm or less than about one-half of the conventional coating thickness. EXAMPLE Examples of the present invention are given below by way of illustration and not by way of limitation. All parts are by weight. Example 1 A blend was prepared by uniformly kneading 54 parts of a dimethylpolysiloxane of the following average molecular formula (i) end-blocked with vinyldimethylsilyl groups at both molecule ends, and having a viscosity of 10,000 centistokes at 25°C, 16 parts of finely divided silica having a specific surface area of 300 m 2 /g (by BET method), and 3 parts of hexamethyldisilazane, followed by heat treatment. This blend, 70 parts, was mixed with 30 parts of a dimethylpolysiloxane end - blocked with vinyldimethylsilyl groups at both molecule ends, and having a viscosity of 5,000 centistokes at 25°C, 2.0 parts of an epoxy-containing methylhydrogenpolysiloxane of the following molecular formula (ii), 2.0 parts of a methylhydrogenpolysiloxane of the following average molecular formula (iii) having a viscosity of 12 centistokes at 25°C, 10 parts of acetylene black having a mean particle size of 0.03 µm, and 0.2 part of a solution of platinum/vinylsiloxane complex in a both end vinyl - blocked dimethylpolysiloxane with platinum atom content of 1% by weight as a platinum catalyst, obtaining a mixture having a viscosity of 280 poise at 25°C. The mixture was coated to a 23.3 tex (210 denier) nylon 66 fabric as a fibrous base material. For the coating purpose, a knife coater was used with a spacing of 20 µm set between the coater's knife edge and the fabric surface. The coating was vulcanized at 150°C for 1 minute. The resulting coating was uniform and had a thickness of 18 µm. wherein letter n is such an integer that the organopolysiloxane has the viscosity defined above (or below). Comparative Example 1 A blend was prepared by uniformly kneading 54 parts of a dimethylpolysiloxane of average molecular formula (i) end-blocked with vinyldimethylsilyl groups at both molecule ends, and having a viscosity of 10,000 centistokes at 25°C, 16 parts of finely divided silica having a specific area of 300 m 2 /g (BET method), and 3 parts of hexamethyldisilazane, followed by heat treatment. This blend, 70 parts, was mixed with 30 parts of a dimethylpolysiloxane end-blocked with vinyldimethylsilyl groups at both molecule ends, and having a viscosity of 5,000 centistokes at 25°C, 2.0 parts of an epoxy-containing methylhydrogenpolysiloxane of molecular formula (ii), 2.0 parts of a methylhydrogenpolysiloxane of average molecular formula (iii), and 0.2 part of a solution of platinum/vinylsiloxane complex in a both end vinyl - blocked dimethylpolysiloxane with platinum atom content of 1% by weight as a platinum catalyst, obtaining a mixture having a viscosity of 280 poise at 25°C. The mixture was coated to a 23.3 tex (210 denier) nylon 66 fabric as a fibrous base material. For the coating purpose, a knife coater was used with a spacing of 50 µm set between the coater's knife edge and the fabric surface. The coating was vulcanized at 150°C for 1 minute. The resulting coating was uniform and had a thickness of 45 µm, which is corresponding to those thickness of air - bag coatings in the prior art. Comparative Example 2 The same mixture as in Comparative Example 1 was coated to a 23.3 tex (210 denier) nylon 66 fabric. For the coating purpose, a knife coater was used with a spacing of 20 µm set between the coater's knife edge and the fabric surface. The coating was vulcanized at 150°C for 1 minute. The resulting coating was uniform and had a thickness of 18 µm. Example 2 A blend was prepared by uniformly kneading 80 parts of a dimethylpolysiloxane of average molecular formula (i) end - blocked with vinyldimethylsilyl groups at both molecule ends, and having a viscosity of 10,000 centistokes at 25°C, 20 parts of finely divided silica having a specific surface area of 300 m 2 /g (BET method), and 3 parts of hexamethyldisilazane, followed by heat treatment. This blend, 100 parts, was mixed with 2.0 parts of a trimethoxysilyl-containing and epoxy - containing methylhydrogenpolysiloxane of the following molecular formula (iv), 2.0 parts of an methylhydrogenpolysiloxane of average molecular formula (iii), 5 parts of Fe 2 O 3 having a mean particle size of 0.16 µm, 0.2 part of benzimidazole, and 0.2 part of a solution of platinum/vinylsiloxane complex in a both end vinyl - blocked dimethylpolysiloxane with platinum atom content of 1% by weight as a platinum catalyst. To the resulting mixture was added 120 parts of toluene. Uniform dissolution yielded a mixture having a viscosity of 80 poise at 25°C. The mixture was spray coated to a 210-denier nylon 66 fabric as a fibrous base material. The coating was heated at 80°C for 5 minutes for evaporating off the solvent and then heat cured at 150°C for 1 minute. The resulting coating was uniform and had a thickness of 5 µm. Example 3 A 23.3 tex (210 denier) nylon 66 fabric was impregnated with the same mixture as in Example 2. The impregnated fabric was heated at 80°C for 5 minutes for evaporating off the solvent and then heat cured at 150°C for 1 minute. The resulting silicone coating was uniform and had a thickness of 10 µm. Example 4 By repeating the procedure of Example 2 except that the benzimidazole was omitted, a mixture having a viscosity of 80 poise at 25°C was obtained. The mixture was spray coated to a 23.3 tex (210 denier) nylon 66 fabric as a fibrous base material. The coating was heated at 80°C for 5 minutes for evaporating off the solvent and then heat cured at 150°C for 1 minute. The resulting coating was uniform and had a thickness of 5 µm. Next, the silicone coated base materials of the foregoing Examples and Comparative Examples were subject to a burning test according to the U.S. Federal Motor Vehicle Safety Standards "FVMS-302". As a control (Comparative Example 3), the nylon fabric used in the Examples, but without a coating was subject to the same burning test. The results are shown in Table 1. E1 E2 E3 E4 CE1 CE2 CE3 Coating thickness 18 µm 5 µm 10 µm 5 µm 45 µm 18 µm 0 Flame propagating time (sec.) 20 18 22 25 33 107 205 Flame propagating length (mm) 3 4 4 10 5 92 170 Burn rate (mm/sec.) 9 13 11 24 9 52 50 Note that the burn rate is defined by the following equation. Burn rate = 60 × (flame propagating length/flame propagating time) As seen from Table 1, the uncoated fabric of Comparative Example 3 burned as if it melted and partially dripped. The coated fabric of Comparative Example 2 did not drop molten drips as in Comparative Example 3, but instead, continued burning for a longer time. Examples 1 to 4 exhibited a combustion level comparable to Comparative Example 1 having a conventional coating thickness. Although some preferred embodiments have been described, many modifications and variations may be made thereto in the light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described.

Claims: A silicone-coated base material comprising a base material, selected from polyamide fibres, polyester fibres, woven and non-woven fabrics thereof, thermoplastic elastomers, and polyurethane sheets, and a coating formed on at least a portion of said base material to a thickness in the range 5 to 20 µm, said coating being a cured coating of a silicone coating composition comprising (A) 100 parts by weight of organopolysiloxane having per molecule at least two alkenyl groups each directly bonded to silicon atom; (B) organohydrogenpolysiloxane having per molecule at least two hydrogen atoms bonded to silicon atom, in a sufficient amount to give 0.5 to 4 equivalents of silicon-bonded hydrogen atom per equivalent of alkenyl group in component (A), (C) 0.1 to 10 parts by weight of organic silicon compound having per molecule at least one hydrogen atom bonded to silicon atom and at least one epoxy and/or trialkoxysilyl group bonded to silicon atom through one or more carbon atoms directly bonded to the silicon atom, (D) 0.1 to 100 parts by weight of at least one powder having a mean particle size of up to 20 µm and selected from carbon, NiO 2 , FeO, FeO 2 , Fe 2 O 3 , Fe 3 O 4 , CoO 2 , CeO 2 and TiO 2 powders, and (E) a catalytic amount of platinum catalyst. A silicone-coated base material according to claim 1 wherein said silicone coating composition contains reinforcing silica, at up to 100 parts by weight. A silicone-coated base material according to claim 2 in which said silicone coating composition includes from 10 to 70 parts by weight of the reinforcing silica. A silicone-coated base material according to any one of claims 1 to 3 in which said powder (D) has a mean particle size in the range 0.02 to 10 µm. A silicone-coated base material according to any one of the preceding claims in which said powder (D) is included in the coating composition at from 0.5 to 20 parts by weight. A silicone-coated base material according to any one of the preceding claims in which the silicone coating composition contains benzotriazole and/or benzimidazole, at up to 1 part by weight. An air bag base material which is a silicone-coated base material in accordance with any one of claims 1 to 6, the base material being a fibrous base material selected from said polyamide fibres, polyester fibres and woven and non-woven fabrics thereof.

Inventors: FUJIKI HIRONAO, TANAKA MIYUKI, FUJIKI, HIRONAO, TANAKA, MIYUKI, FUJIKI, HIRONAO, C/O SILICONE-ELEC. MAT. LAB., TANAKA, MIYUKI, C/O SILICONE-ELEC. MAT. LAB.
Applicants: SHINETSU CHEMICAL CO, SHIN-ETSU CHEMICAL CO., LTD.
Application year: 1995
Main classification: D06M15
IPC codes: D06M11, B60R21, D06N3, D06M15, C09D183