Method of and crucible for preparing compound semiconductor crystal

Abstract: Provided are a method of preparing a compound semiconductor crystal by forming a boron or boron compound containing layer on an inner surface of a crucible and heat treating the same thereby forming a B₂O₃ containing layer, and a crucible which is employed for preparing the compound semiconductor crystal. According to this method, it is possible to previously form a homogenous B₂O₃ film on the crucible surface while preventing the B₂O₃ film from incomplete coating and heterogeneous coating. Consequently, it is possible to prevent a raw material melt from wetting to a container and to suppress polycrystallization, thereby preparing a compound semiconductor single crystal in an excellent yield.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a method of and a crucible for preparing a compound semiconductor crystal, and more particularly, it relates to a method of and an apparatus for preparing a compound semiconductor crystal such as a group III-V compound semiconductor crystal of GaAs, GaP, GaSb, InP, InAs or InSb, or a group II-VI compound semiconductor crystal of CdTe, CdMnTe, CdZnTe, HgCdTe, ZnSe or ZnSSe. Description of the Background Art Typical conventional methods of preparing compound semiconductor bulk crystals are a horizontal Bridgman method, a gradient freezing method, a vertical Bridgman method, and a vertical gradient freezing method. In order to grow a single crystal by any of these methods, a seed crystal is first arranged on an end of a boat or a crucible and brought into contact with a raw material melt, and the temperature is gradually reduced from the seed crystal side to grow a single crystal. In such a method, however, the crystal is grown while being in contact with the container wall, and hence crystal defects are disadvantageously caused due to wetting of the melt and the container wall. It has generally been known in the art that crystal defects are caused in wet portions of the melt and the container wall, to result in polycrystallization. In order to solve this problem, the following countermeasure has been considered in general: A boat or a crucible is generally made of quartz or PBN (pyrolytic boron nitride). In relation to a boat or a crucible of quartz, it is known possible to reduce its wettability by roughening its surface by sandblasting. In relation to a crucible of PBN, on the other hand, it is known possible to prevent wetting by covering its inner surface with boron oxide (B 2 O 3 ) which is introduced therein with the raw material, for example. Fig. 5 is a sectional view showing an exemplary apparatus for preparing a GaAs single crystal by the vertical Bridgman method. Referring to Fig. 5, this apparatus comprises a stainless chamber 1, a heat insulator 2 which is arranged along its wall surface, heaters 3 to 12 which are arranged in its interior, and a quartz ampoule 14, supported by a lower shaft 13, which is mounted on its center. An arsenic pressure control part 15 is provided on a lower end of the ampoule 14 for controlling the temperature of this portion, thereby controlling the arsenic partial pressure in the ampoule 14. The arsenic partial pressure is controlled with solid arsenic 16. In the apparatus having the aforementioned structure, a GaAs crystal is prepared in the following manner: First, a crucible 17 is arranged in an upper portion of the ampoule 14. The lower portion of the crucible 17 is in the form of an inverted cone, so that a seed crystal 18 is mounted on its lower end. Then, GaAs raw material 19 and B 2 O 3 20 are charged on the seed crystal 18 which is arranged in the crucible 17. Thereafter the ampoule 14 is sealed, and heated by the heaters 3 to 12. In this heating, the B 2 O 3 20 is first softened to cover the inner surface of the crucible 17. Thereafter the temperature is further increased to melt the GaAs raw material 19, and temperature distribution is optimized, so that the lower shaft 13 is thereafter downwardly moved to move the ampoule 14 toward a lower temperature side, and the raw material 19 is solidified from the seed crystal 18 side, thereby growing a single crystal. The vertical gradient freezing method is carried out substantially similarly to the vertical Bridgman method shown in Fig. 5, except that the vertical position of the ampoule 14 is left intact and outputs of the heaters 3 to 12 are varied to gradually upwardly move the lower temperature portion so that the raw material 19 which is stored in the ampoule 14 is solidified from the seed crystal 18 side for growing a single crystal. When the vertical Bridgman method or the vertical gradient freezing method is employed, it is possible to alternatively grow a crystal in the atmosphere, without employing the stainless chamber 1. In this case, the heat insulator 2, the heaters 3 to 12 and the like must be formed to be employable in the atmosphere. In the aforementioned conventional method, however, it is not necessarily possible to completely cover the inner surface of the crucible with B 2 O 3 , although the raw material and B 2 O 3 are introduced into the crucible together and the ampoule is sealed so that B 2 O 3 is softened to cover the inner surface of the crucible. To this end, Japanese Patent Laying-Open No. 62-176998 (1987) proposes a method of previously spreading boron oxide powder or boric acid powder on an inner surface of a PBN boat. Further, each of Japanese Patent Laying-Open No. 62-176998 and U. S. Patent No. 4923561 proposes method of previously heating a PBN boat or a BN crucible in an oxygen atmosphere and oxidizing the same thereby previously forming a B 2 O 3 coat on the inner surface of the boat or the crucible, and thereafter introducing raw material into the same for growing a crystal. According to this method, the inner surface of the boat or the crucible is previously covered with B 2 O 3 , and hence it is conceivably possible to attain a higher effect of preventing polycrystallization caused by wetting, as compared with the conventional method of charging B 2 O 3 with the raw material. However, the aforementioned methods have the following problems respectively: First, the method of previously spreading boron oxide powder or boric acid powder on the inner surface of a PBN boat or crucible has the following problems: First, it is scarcely possible to attain adhesion of the boron oxide powder or the boric acid powder to the inner surface of the crucible by simply spreading the same. Therefore, the powder is disadvantageously easily separated from the crucible surface through contact with the raw material as introduced. Consequently, it is extremely difficult to homogeneously form a B 2 O 3 film. Second, the boron oxide powder or the boric acid powder has a high water content, and water-containing B 2 O 3 is extremely easy to scatter. Therefore, this B 2 O 3 is scattered before melting of the raw material, to break the film and expose the inner surface of the crucible. Consequently, it is extremely difficult to obtain a homogeneous film since B 2 O 3 is remarkably scattered particularly under a vacuum. On the other hand, the method of previously heating a PBN boat or a BN crucible in an oxygen atmosphere and oxidizing the same for previously forming a B 2 O 3 coat on the inner surface of the boat or the crucible has the following problems: First, it is generally necessary to form a thick B 2 O 3 film of about 50 µm, in order to effectively prevent polycrystallization caused by wetting. Due to the formation of such a thick B 2 O 3 film, therefore, the thickness of the crucible is remarkably reduced and hence its life is extremely reduced. Second, it is necessary to heat the inner surface of a crucible which is made of PBN (pyrolytic boron nitride) having a dense structure for a long time in order to oxidize the same, and hence the preparation cost is inevitably increased. Third, it is difficult to maintain a homogeneous flow of oxygen gas although the thickness of the B 2 O 3 depends on this flow, and B 2 O 3 is reduced in viscosity due to the high temperature heating and collected in the lower portion of the crucible. Thus, it is extremely difficult to form a homogeneous B 2 O 3 film. SUMMARY OF THE INVENTION An object of the present invention is to provide a method of and a crucible for preparing a crystal, which can solve the aforementioned problems by completely preventing wetting of a raw material melt with respect to a crucible and suppressing polycrystallization, for preparing a compound semiconductor single crystal in an excellent yield. According to an aspect of the present invention, a method of preparing a compound semiconductor crystal is provided. This method comprises the steps of previously forming a boron or oxygen-free boron compound containing layer on an inner surface of a crucible, heat treating the crucible which is provided with the boron or boron compound containing layer under an oxygen gas or oxygen mixed gas atmosphere thereby forming a boron oxide containing layer at least on a surface of the boron or boron compound containing layer, charging raw material in the crucible which is provided with the boron oxide containing layer, melting the charged raw material for forming a melt, and solidifying the melt from an end of the crucible thereby growing a crystal. The oxygen-free boron compound is preferably prepared from boron nitride, for example. In the oxygen mixed gas, gas to be mixed with oxygen is preferably prepared from that hardly reacting with oxygen and having small solubility with respect to B 2 O 3 , which is inactive with respect to the grown crystal. In more concrete terms, the oxygen mixed gas is preferably a mixed gas consisting of nitrogen gas or argon gas and oxygen gas, or air. A mixed gas consisting of helium gas, neon gas, krypton gas, xenon gas or carbon dioxide gas and oxygen gas can be employed. Further, the heat treatment is carried out at a temperature in the range of 700°C to 1800°C, preferably in the range of 800°C to 1500°C, more preferably in the range of 900°C to 1300°C. Sputtering or vacuum deposition can be employed as a method of forming a boron nitride containing layer on the inner surface of the crucible. More preferably, a mixture of boron nitride powder and a solvent such as water, alcohol or acetone may be sprayed with gas such as butane gas, nitrogen gas, carbon dioxide gas or air, to form the boron nitride containing layer. More preferably, a mixture of boron nitride powder and a solvent such as water, alcohol or acetone may be sprayed by hand or through an automatic atomizer, or brushed, to form the boron nitride containing layer. More preferably, a mixed solution of boron nitride powder and a solvent such as water, alcohol or acetone may be charged in the crucible so that the residual mixed solution is discharged, thereby forming the boron nitride containing layer on the inner surface of the crucible. When the boron or boron compound containing layer is heat treated under the oxygen gas or oxygen mixed gas atmosphere, the crucible may be screened with a shielding material except the region provided with the boron oxide containing layer. This is because the crystal as grown strongly adheres to the crucible by boron oxide (B 2 O 3 ) and cannot be detached from the same and hence the amount of the boron oxide as formed is preferably minimized. In other words, it is preferable to minimize the area of the B 2 O 3 layer which is formed on the inner surface of the crucible, while it is most preferable to form the boron oxide containing layer limitedly to the portion of the inner surface of the crucible for growing the crystal. According to another aspect of the present invention, a method of preparing a compound semiconductor crystal is provided. This method comprises the steps of previously forming an oxygen-containing boron compound containing layer on an inner surface of a crucible, heat treating the crucible which is provided with the boron compound containing layer thereby forming a boron oxide containing layer at least on a surface of the boron compound containing layer, charging raw material in the crucible which is provided with the boron oxide containing layer, melting the charged raw material for forming a melt, and solidifying the melt from an end of the crucible thereby growing a crystal. The oxygen-containing boron compound is preferably prepared from orthoboric acid (H 3 BO 3 ), metaboric acid (HBO 2 ), tetraboric acid (H 2 B 4 O 7 ) or boron oxide (B 2 O 3 ), for example. When such an oxygen-containing boron compound is employed, it is not necessary to add oxygen to the atmosphere gas for the heat treatment. The heat treatment is carried out at a temperature in the range of 300°C to 1800°C, preferably in the range of 350°C to 1500°C, and more preferably in the range of 400°C to 1300°C. After the boron oxide containing layer is formed by the heat treatment, an additional step may be carried out to again increase the temperature to a level in the range of 1000°C to 1800°C, for adjusting the water content of boron oxide to not more than 0.5 percent by weight. In order to form the oxygen-containing boron compound containing layer on the inner surface of the crucible, employed is a method of dissolving or mixing the oxygen-containing boron compound in or with a solvent such as water, alcohol such as methyl alcohol, ethyl alcohol, propyl alcohol or butyl alcohol, or acetone, and applying or spraying the solution as formed onto the inner surface of the crucible. Alternatively, a solution or a mixed solution of the oxygen-containing boron compound may be charged in the crucible so that the solution or the mixed solution is thereafter discharged, thereby forming the oxygen-containing boron compound containing layer on the inner surface of the crucible. Further, a solid source of the oxygen-containing boron compound may be sputtered with argon or the like, or irradiated with an electron beam, so that the oxygen-containing boron compound containing layer is formed on the inner surface of the crucible. In addition, powder of the oxygen-containing boron compound may be charged in the crucible so that the residual powder is removed after the heat treatment, thereby forming the oxygen-containing boron compound containing layer on the inner surface of the crucible. According to the present invention, the boron oxide concentration in the boron oxide containing layer which is formed on the inner surface of the crucible by the heat treatment may be not less than 30 percent by weight, preferably not less than 40 percent by weight, and more preferably not less than 50 percent by weight, in order to effectively prevent wetting of the crystal and the crucible. According to the present invention, on the other hand, the boron oxide concentration is preferably minimized in a portion, which is in contact with the crucible, of the boron oxide containing layer formed by the heat treatment. This is because boron oxide (B 2 O 3 ) is solidified after the crystal growth, to damage the inner surface of the crucible by strongly adhering thereto. For example, the life of a PBN crucible is reduced since its surface layer is disadvantageously delaminated. When the boron oxide concentration is reduced in the portion which is in contact with the crucible, therefore, it is possible to reduce the damage on the crucible and to increase its life. In more concrete terms, the boron oxide concentration in the portion which is in contact with the crucible may be not more than 70 percent by weight, preferably not more than 60 percent by weight, and more preferably not more than 50 percent by weight, so that it is possible to reduce damage of the crucible caused by strong adhesion of boron oxide. According to the present invention, as hereinabove described, the boron oxide concentration is reduced in the portion which is in contact with the crucible in the boron oxide containing layer formed by the heat treatment as compared with that on the surface, so that it is possible to effectively prevent wetting of the crystal and the crucible and to reduce damage of the crucible caused by strong adhesion of boron oxide. According to the inventive method, it is possible to freely adjust the compounding ratio of B 2 O 3 by adjusting the degree of oxidization and the content of the boron compound. While it is also possible to adjust the B 2 O 3 concentration by controlling the temperature and the time for oxidization, a layer having higher density than the surface may be introduced into the boron or boron compound containing layer which is formed on the inner surface of the crucible. This is because oxidization hardly progresses inwardly beyond the layer having high density, and hence it is possible to readily reduce the boron oxide concentration in the portion which is in contact with the crucible as compared with that on the surface. As to a method of adjusting the boron oxide concentration, it is also effective to further mix at least one substance which is selected from the group consisting of a group III element, a group IV element, a group V element, a compound of the group III element, a compound of the group IV element and a compound of the group V element to the boron or boron compound containing layer. The group III element is preferably prepared from Al, for example, while the compound of the group III element is preferably prepared from an Al compound, i.e., an Al oxide or an Al nitride in more concrete terms, for example. Further, the group III element is also preferably prepared from Ga, and the compound of the group III element is also preferably prepared from a Ga compound, i.e., a Ga oxide or a Ga nitride in more concrete terms, for example. The group IV element is preferably prepared from Si, for example, while the compound of the group IV element is preferably prepared from a Si compound, i.e., a silicon oxide, silicon nitride or silicon carbide in more concrete terms, for example. Further, it is possible to effectively form the boron oxide containing layer on the surface by reducing concentration of Al or the Al compound, Ga or the Ga compound and Si or the Si compound on the surface of the boron or boron compound containing layer which is formed on the inner surface of the crucible as compared with the interior of the layer and increasing the content of boron or the boron compound on the surface. According to the present invention, the boron oxide containing layer is preferably be formed only on a portion which is in contact with the raw material melt. After the boron oxide containing layer is formed on the inner surface of the crucible, the crucible is cooled to the room temperature in a pressure reduction or dry gas atmosphere. According to the present invention, further, the crucible is preferably cooled to the room temperature in the pressure reduction or dry gas atmosphere, so that the water concentration of the boron oxide containing layer as formed is not more than 0.5 percent by weight, preferably in the range of 0.001 to 0.1 percent by weight, and more preferably in the range of 0.001 to 0.02 percent by weight. This is because boron oxide is scattered with water under a high temperature to damage homogeneity of the film, if the water concentration of the boron oxide containing layer exceeds 0.5 percent by weight. In particular, a thin film of B 2 O 3 readily absorbs water due to its large specific surface area. After formation of the B 2 O 3 containing layer, therefore, it is preferable to prevent the B 2 O 3 containing layer from water absorption by cooling the crucible to the room temperature under the reduced pressure or dry gas atmosphere. According to the present invention, it is necessary to carry out the heat treatment at a high temperature in order to obtain a B 2 O 3 film having low water concentration, while the thickness of the B 2 O 3 film is readily heterogenized as the temperature is increased since B 2 O 3 flows down toward the lower portion of the crucible due to reduction of its viscosity. Therefore, it is preferable to carry out the process of forming the B 2 O 3 film by heat treating boron or the boron compound at a relatively low temperature of not more than 1000°C over a considerably long time, while adjusting the water concentration of the film at a high temperature of not less than 1000°C in a short time. Due to such heat treatment, it is possible to form a homogeneous B 2 O 3 film. The inventive method is applicable to any method such as the horizontal Bridgman method, the vertical Bridgman method, the horizontal gradient freezing method and the vertical gradient freezing method, so far as the method is adapted to prepare a compound semiconductor crystal by solidifying the melt from an end of the crucible. Further, the shape of the crucible as employed is not limited either and any shape is employable so far as the crucible or a boat is applied to the aforementioned method of preparing a compound semiconductor crystal. Further, heating means for carrying out the heat treatment is not restricted to an annular furnace but any means is employable so far as the same can heat the crucible to a target temperature. According to still another aspect of the present invention, a crucible for preparing a compound semiconductor crystal is provided. This crucible is adapted to prepare a compound semiconductor crystal by melt solidification, and is characterized in that the same is provided on its inner surface with a boron oxide containing layer having water concentration of not more than 0.5 percent by weight, preferably in the range of 0.001 percent by weight to 0.1 percent by weight, more preferably in the range of 0.001 percent by weight to 0.02 percent by weight. The material for the crucible can be prepared from boron nitride, graphite, pyrolytic boron nitride (PBN), pyrolytic graphite (PG), glassy carbon, alumina, zirconia, silicon nitride, silicon carbide or quartz, for example. As hereinabove described, the present invention is adapted to prepare a compound semiconductor crystal not by spreading boron oxide powder or boric acid powder onto an inner surface of a crucible or oxidizing a PBN boat or a BN crucible itself but by forming a boron or boron compound containing layer on an inner surface of a crucible and heat treating the same thereby forming a B 2 O 3 layer. Dissimilarly to the conventional method of growing a crystal by introducing raw material and solid B 2 O 3 into a crucible, therefore, it is possible to previously form a homogeneous B 2 O 3 film on the inner surface of the crucible while preventing the B 2 O 3 film from incomplete or heterogeneous coating. Thus, it is possible to prevent the raw material melt from wetting with the container and to remove the possibility for polycrystallization. When a boron or oxygen-free boron compound containing layer is formed in the present invention, it is possible to form a B 2 O 3 containing film on the inner surface of the crucible by heating the same in oxygen-containing gas. For example, a B 2 O 3 film is formed by oxidizing boron nitride, along a chemical reaction in the following formula (A): 4BN + 3O 2 → 2B 2 O 3 + 2N 2 When an oxygen-containing boron compound containing layer is formed in the present invention, further, oxygen is not inevitably necessary but a B 2 O 3 film can be formed on the inner surface of the crucible also by thermal decomposition. For example, a B 2 O 3 film is formed by thermal decomposition of orthoboric acid (H 3 BO 3 ), along a chemical reaction in the following formula (B): 2H 3 BO 3 → B 2 O 3 + 3H 2 O On the other hand, it is impossible to attain adhesion to the crucible by merely applying boron compound containing powder which is mixed with a solvent. In this case, the film of the powder as applied is disadvantageously stripped when the raw material is stored in the crucible. According to the present invention, therefore, B 2 O 3 which is formed by the reaction of the formula (A) or (B) is softened at a temperature of not less than 300°C by the heat treatment, so that particles thereof adhere to the crucible wall. Consequently, it is possible to obtain a B 2 O 3 film having high adhesion, which is not stripped when the raw material is stored in the crucible. The foregoing and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a conceptual diagram of an apparatus for preparing a crystal, which is employed for carrying out the inventive method; Fig. 2 is an enlarged view showing a crucible employed in Fig. 1, which is provided on its inner surface with a boron or boron compound containing film; Fig. 3 is adapted to illustrate an exemplary situation of heat treating a boron or boron compound containing layer which is provided on an inner surface of a crucible; Fig. 4 is adapted to illustrate another exemplary situation of heat treating a boron or boron compound containing layer which is provided on an inner surface of a crucible; and Fig. 5 is a conceptual diagram of a conventional apparatus for preparing a crystal. DESCRIPTION OF THE PREFERRED EMBODIMENTS Fig. 1 is a conceptual diagram of an apparatus for preparing a crystal, which is employed for carrying out the method according to the present invention. This apparatus is similar to the conventional apparatus shown in Fig. 5 except employment of a crucible which is provided with a B 2 O 3 containing layer according to the inventive method, and hence redundant description is omitted. Fig. 2 is an enlarge view showing a crucible 17 employed in the apparatus shown in Fig. 1, which is provided on its inner surface with a boron or boron compound containing film, and Fig. 3 is a diagram for illustrating an exemplary situation of heat treating the boron or boron compound containing layer which is formed on the inner surface of the crucible 17. As shown in Fig. 2, the exemplary crucible 17 employed in the present invention has a seed crystal holding part 23 provided on its lower portion, and consists of a tapered part 22 and a side wall which are continuous thereto, while a boron or boron compound containing film 24 is formed at least on a wall surface which comes into contact with a raw material melt. The crucible 17 shown in Fig. 2 is introduced into an annular furnace 25 shown in Fig. 3 and heat treated with feeding of oxygen or oxygen-containing gas, so that a B 2 O 3 containing film is formed on its inner surface. Fig. 4 is a diagram for illustrating another exemplary situation of heat treating the boron or boron compound containing layer which is provided on the inner surface of the crucible 17. When the heat treatment is carried out in the annular furnace 25 shown in Fig. 3, an inner surface portion of the crucible 17 which is not provided with the B 2 O 3 containing film is covered on its surface with a shielding material 26, for limiting the region to be provided with the film B 2 O 3 containing film. Description is now made on Examples which were carried out through such an apparatus for investigating the effects of the present invention. (Example 1) As shown in Fig. 2, a PBN crucible of about 80 mm in diameter and about 300 mm in height having a tapered part and a seed crystal holding part on its lower portion was employed so that a boron nitride containing layer was formed on its surface by spraying, with employment of boron nitride powder, alcohol and carbon dioxide gas. Thereafter this crucible was introduced into an annular furnace, and was heat treated at 1000°C for 5 hours with feeding of oxygen gas at a flow rate of 1 ℓ/min., thereby forming a B 2 O 3 film having a thickness of about 50 µm on its inner surface. Thereafter the crucible was cooled to the room temperature at a cooling rate of 10°C/min., with feeding of oxygen gas. The water concentration of the B 2 O 3 film obtained in the aforementioned manner was 0.02 percent by weight. Further, the thickness of this B 2 O 3 film was extremely homogeneous, with dispersion of not more than ±5 µm. Then, 3 kg of GaAs polycrystalline raw material and a dopant of solid Si were stored in the crucible which was provided with the B 2 O 3 film on its inner surface, and the crucible was vacuum-sealed in a longitudinal quartz ampoule 14 having an arsenic pressure control part 15 as shown in Fig. 1. Then, the raw material which was stored in the crucible was melted, and thereafter the temperature was reduced from the seed crystal side while controlling the arsenic pressure in the ampoule 14, thereby growing Si-doped n-type GaAs single crystals. Consequently, absolutely no polycrystallization caused by wetting was recognized in growth of 20 single crystals. (Example 2) A solution which was prepared by dissolving orthoboric acid in methyl alcohol to attain saturation concentration was applied onto an inner surface of a PBN crucible having the same shape as that in Example 1, with an atomizer. Then, the methyl alcohol contained in the solution was quickly dried with dry nitrogen gas. The application and drying steps were repeated to form an orthoboric acid film having a thickness of about 100 µm. This crucible was introduced into an annular furnace, and was heat treated at 800°C for about 2 hours with feeding of nitrogen gas at a flow rate of 1 ℓ/min., thereby forming a B 2 O 3 film having a thickness of about 50 µm on its inner surface. Then, the crucible was heated up to 1100°C and held for 1 hour for adjusting the water concentration of the B 2 O 3 film to 0.01 percent by weight, and thereafter cooled to the room temperature at a cooling rate of 10°C/min. The thickness of the B 2 O 3 film which was formed on the inner surface of the crucible obtained in the aforementioned manner was extremely homogeneous, with dispersion of not more than ±5 µm. Then, this crucible was employed to grow Si-doped n-type GaAs single crystals, similarly to Example 1. Consequently, absolutely no polycrystallization caused by wetting was recognized in growth of 20 single crystals. (Example 3) B 2 O 3 powder was charged in a PBN crucible having the same shape as that in Example 1 to be higher by 15 mm than a crystal as grown, and this crucible was introduced into a vertical heating furnace and heated to about 400°C, so that B 2 O 3 adhered to its inner surface in a thickness of about 100 µm. This crucible was introduced into a high-temperature heating furnace, and was heat treated at 1100°C for 30 minutes with feeding of dry argon gas, thereby forming a B 2 O 3 film having a thickness of 50 ± 5 µm with water concentration which was adjusted to 0.01 percent by weight. Thereafter this crucible was cooled to the room temperature at a cooling rate of 5°C/min. Then, this crucible was employed to grow Si-doped n-type GaAs single crystals, similarly to Example 1. Consequently, absolutely no polycrystallization caused by wetting was recognized in growth of 20 single crystals. (Example 4) A PBN crucible having the same shape as that in Example 1 was fixed into a deposition apparatus to downwardly direct its opening, and a boron nitride tablet of 20 mm in diameter and 15 mm in thickness was set on a water-cooled holder. The deposition apparatus was evacuated and sealed, and the boron nitride tablet was thereafter irradiated with an electron beam so that a boron nitride film having a thickness of 60 µm adhered to the inner surface of the crucible. Thereafter the crucible was heat treated at 1000°C for 10 hours with feeding of oxygen gas, thereby forming a B 2 O 3 film having a thickness of 50 ± 5 µm. Thereafter the crucible was cooled to the room temperature at a cooling rate of 10°C/min, with feeding of dry nitrogen gas. The crucible obtained in the aforementioned manner was employed to grow Si-doped n-type GaAs single crystals, similarly to Example 1. Consequently, absolutely no polycrystallization caused by wetting was recognized in growth of 20 single crystals. (Example 5) A mixed solution of acetone and boron nitride powder was introduced into a PBN crucible having the same shape as that in Example 1 to form a high density boron nitride film having a thickness of about 25 µm on the inner surface of the crucible, and thereafter the residual mixed solution was discharged. Further, the same mixed solution of acetone and boron nitride powder was applied onto the high density boron nitride film with an atomizer, to form a low density boron nitride film having a thickness of about 50 µm. The crucible as obtained was heat treated in an annular furnace at 1000°C for about 2 hours with feeding of mixed gas containing 50 percent of oxygen and 50 percent of argon at a flow rate of 1 ℓ/min., thereby forming a B 2 O 3 containing film having a thickness of about 50 µm. The thickness of the B 2 O 3 containing film as obtained was extremely homogeneous, with dispersion of ±5 µm. Further, the B 2 O 3 content of the B 2 O 3 containing film which was formed in the aforementioned manner was 80 percent by weight on the film surface, and 40 percent by weight in a portion which was in contact with the crucible. Then, the crucible obtained in the aforementioned manner was employed to grow Si-doped n-type GaAs single crystals, similarly to Example 1. Consequently, absolutely no polycrystallization caused by wetting was recognized in growth of 20 single crystals. Further, it was easy to remove the B 2 O 3 containing film, whereby the life of the PBN crucible was substantially doubled, with small damage in removal of the film. (Example 6) A solvent which was prepared by mixing boron nitride powder with powder of SiO 2 serving as a silicon oxide in the weight ratio of 1:3 (BN:SiO 2 = 1:3) and further mixing acetone into this mixture was applied to an inner surface of a PBN crucible having the same shape as that in Example 1 with an atomizer, to form a film containing boron nitride and SiO 2 having a thickness of about 40 µm. Further, another solution which was prepared by mixing boron nitride powder with powder of SiO 2 serving as a silicon oxide in the weight ratio of 3:2 (BN:SiO 2 = 3:2) and further mixing acetone to this mixture was applied onto this film with an atomizer, and the crucible was heat treated in an annular furnace at 1000°C for 5 hours with feeding of oxygen gas at a flow rate of 1 ℓ/min., thereby forming a B 2 O 3 containing film having a thickness of about 50 µm. The thickness of the film containing B 2 O 3 as obtained was extremely homogeneous, with dispersion of not more than ±5 µm. Further, the B 2 O 3 content of the B 2 O 3 containing film which was formed in the aforementioned manner was 70 percent by weight on the film surface, and 30 percent by weight in a portion which was in contact with the crucible. Then, the crucible obtained in the aforementioned manner was employed to grow Si-doped n-type GaAs single crystals, similarly to Example 1. Consequently, absolutely no polycrystallization caused by wetting was recognized in growth of 20 single crystals. In addition, it was easy to remove the B 2 O 3 containing film, whereby the life of the PBN crucible was substantially doubled, with small damage in removal of the film. (Example 7) A solution which was prepared by mixing boron oxide powder with powder of Al 2 O 3 in the weight ratio of 2:8 (B 2 O 3 :Al 2 O 3 = 2:8) and further mixing acetone into this mixture was applied to an inner surface of a PBN crucible having the same shape as that in Example 1 with an atomizer, to form a film containing boron nitride and Al 2 O 3 having a thickness of about 40 µm. Further, another solution which was prepared by mixing boron oxide powder with powder of Al 2 O 3 in the weight ratio of 9:1 (B 2 O 3 :Al 2 O 3 = 9:1) and further mixing acetone to this mixture was applied onto this film with an atomizer, and the crucible was heat treated in an annular furnace at 1000°C for 5 hours with feeding of oxygen gas at a flow rate of 1 ℓ/min., thereby forming a B 2 O 3 containing film having a thickness of about 50 µm. The thickness of the film containing B 2 O 3 as obtained was extremely homogeneous, with dispersion of not more than ±5 µm. Further, the B 2 O 3 content of the B 2 O 3 containing film which was formed in the aforementioned manner was 90 percent by weight on the film surface, and 20 percent by weight in a portion which was in contact with the crucible. Then, the crucible obtained in the aforementioned manner was employed to grow Si-doped n-type GaAs single crystals, similarly to Example 1. Consequently, absolutely no polycrystallization caused by wetting was recognized in growth of 20 single crystals. Further, it was easy to remove the B 2 O 3 containing film, whereby the life of the PBN crucible was substantially doubled, with small damage in removal of the film. (Comparative Example 1) A PBN crucible having the same shape as that in Example 1 was heat treated in an annular furnace at 1100°C for 50 hours with feeding of oxygen gas at a flow rate of 1 ℓ/min., thereby forming a B 2 O 3 film by oxidizing the inner surface of the crucible. While the average thickness of the B 2 O 3 film as obtained was 50 µm, the thickness at a lower portion of the crucible was considerably large, with the maximum value of 200 µm. On the other hand, the thickness at an upper portion of the crucible was extremely small, with the value of substantially 0 µm. After formation of the B 2 O 3 film, the crucible was not particularly held in a dry atmosphere, but cooled to the room temperature at a cooling rate of 2°C/min. Consequently, the water concentration of the B 2 O 3 film was at an extremely high level of 1 percent by weight. The crucible which was obtained in the aforementioned manner was employed to grow Si-doped n-type GaAs single crystals, similarly to Example 1. Consequently, polycrystallization was caused by wetting on the upper portion of the crucible having the B 2 O 3 film with a small thickness, in 16 samples among 20 single crystals as grown. It is clearly understood from the above description that the following effects can be attained according to the present invention: (1) The life of the crucible can be increased since the crucible itself is not oxidized. (2) The boron or boron compound containing layer adhering to the inner surface of the crucible has a sparse structure, whereby the B 2 O 3 containing film can be formed in a short time at relatively low temperature. (3) The boron or boron compound containing layer adhering to the inner surface of the crucible has a sparse structure, whereby the oxidization inwardly progresses to facilitate formation of a thick B 2 O 3 containing film. (4) Formation of the B 2 O 3 containing film is not influenced by the state of flow of the oxygen gas and it is not necessary to apply a high temperature for increasing its thickness, whereby a homogeneous film can be readily formed. (5) When the B 2 O 3 containing film is prepared from the oxygen-containing boron compound, it is possible to form the film in an extremely short time at a low temperature. (6) It is possible to reduce damage of the crucible caused by strong adhesion of B 2 O 3 and to increase its life by reducing B 2 O 3 concentration in a portion of the B 2 O 3 containing film which is in contact with the crucible. (7) By decreasing the water concentration of the B 2 O 3 containing film, B 2 O 3 is less likely to scatter, whereby a homogenous film can be formed. (8) It is possible to increase the life of the crucible and to form the B 2 O 3 containing film in a short time at a low temperature, whereby the cost can be reduced. (9) The compound semiconductor crystal can be grown in the crucible comprising a homogenous B 2 O 3 containing film, whereby a high single crystal yield can be attained. Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the spirit and scope of the present invention being limited only by the terms of the appended claims.

Claims: A method of preparing a compound semiconductor crystal, comprising the steps of: previously forming a boron or oxygen-free boron compound containing layer on an inner surface of a crucible; heat treating said crucible being provided with said boron or boron compound containing layer under an oxygen gas or oxygen mixed gas atmosphere, thereby forming a boron oxide containing layer at least on a surface of said boron or boron compound containing layer; charging raw material in said crucible being provided with said boron oxide containing layer; melting charged said raw material for forming a melt; and solidifying said melt from an end of said crucible, thereby growing a crystal. The method of preparing a compound semiconductor crystal in accordance with claim 1, wherein said heat treatment is carried out at a temperature in the range of 700°C to 1800°C. A method of preparing a compound semiconductor crystal, comprising the steps of: previously forming an oxygen-containing boron compound containing layer on an inner surface of a crucible; heat treating said crucible being provided with said boron compound containing layer, thereby forming a boron oxide containing layer at least on a surface of said boron compound containing layer; charging raw material in said crucible being provided with said boron oxide containing layer; melting charged said raw material for forming a melt; and solidifying said melt from an end of said crucible, thereby growing a crystal. The method of preparing a compound semiconductor crystal in accordance with claim 3, wherein said heat treatment is carried out at a temperature in the range of 300°C to 1800°C. The method of preparing a compound semiconductor crystal in accordance with claim 4, further comprising a step of again heating said crucible to a temperature in the range of 1000°C to 1800°C after said heat treatment, for adjusting the water content of said boron oxide to not more than 0.5 percent by weight. The method of preparing a compound semiconductor crystal in accordance with any of claims 1 to 5, wherein the internal density of said boron or boron compound containing layer is larger than its surface density. The method of preparing a compound semiconductor crystal in accordance with any of claims 1 to 6, wherein said boron or boron compound containing layer further contains at least one substance being selected from the group consisting of a group III element, a group IV element, a group V element, a compound of said group III element, a compound of said group IV element, and a compound of said group V element. The method of preparing a compound semiconductor crystal in accordance with claim 7, wherein said group III element is Ga or Al and said compound of said group III element is a Ga compound or an Al compound. The method of preparing a compound semiconductor crystal in accordance with any of claims 1 to 8, wherein said boron compound containing layer further contains Si or an Si compound. The method of preparing a compound semiconductor crystal in accordance with any of claims 1 to 9, wherein said boron oxide containing layer is formed only on a portion of said crucible being in contact with said melt. A crucible (17) for preparing a compound semiconductor crystal by melt solidification, said crucible being provided with a boron oxide containing layer (24) having water concentration of not more than 0.5 percent by weight on its inner surface.

Inventors: KAWASE TOMOHIRO, KAWASE, TOMOHIRO, KAWASE, TOMOHIRO, C/O ITAMI WORKS OF SUMITOMO
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1995
Main classification: C30B11
IPC codes: C30B11