WET ADHESION MONOMERS WITH UREIDO FUNCTIONALITY AND POLYMERS PREPARED THEREFROM

Abstract: Compounds having formula (II) where R<1> is H or an alkyl group of up to 17 carbon atoms, R<2> is alkylene of up to 20 carbon atoms, optionally interrupted with one or more ether oxygen atoms, and A is a residue of an active hydrogen reactive compound, provided that when R<1> is H, A is a residue of an active hydrogen reactive compound which is an unsaturated isocyanate, an unsaturated anhydride, or an active hydrogen reactive compound which does not contain ethylenic unsaturation are useful for incorporating ureido and optionally nitrile functionality into polymers and as precursors to amino compounds prepared by reduction of the nitrile group thereof. Compounds having formula (III) where R<1> is H or a C1-C17 alkyl group and R<2> is C1-C20 alkylene optionally interrupted with one or more ether oxygen atoms, A and B are different groups and one of A and B is H or a group having ethylenic unsaturation and the other of A and B is a residue of an active hydrogen reactive compound, provided that said residue of said active hydrogen reactive compound does not include an active hydrogen group or ethylenic unsaturation are also disclosed. The disclosed compounds have use as chain extending or terminating monomers for polyurethane dispersions and as wet adhesion monomers in dispersions of free radically polymerized polymers of unsaturated monomers. The disclosed compounds may take the form of monomers, prepolymer and polymer compounds.

Description: ET ADHESION MONOMERS WITH UREH)O FUNCTIONALITY AND POLYMERS PREPARED THEREFROM Background of the Invention Ethylenically unsaturated compounds having imidazolidinone groups thereon which provide ureido hydrogen functionality are known as good wet adhesion monomers. References describing such compounds include: US 4,302,375; US 4,340,743; US 4,319,032; US 4,429,095; US 4,632,957; US 4,783,539; US 4,880,931; and US 4,882,873. In some disclosed structures a cyano group may also be present. Gilles, Jr., et al, "Non- VOC Modifier To Improve The Gloss Of Water-Borne Coatings", presented at the Water-borne & High solids Coating Symposium (Feburary 6-8, 1991), 268-278, U. So. Miss. Dep of Poly. Sci.; US 2,613,212; DE 2,829,198; and WO 91/12243 disclose various imidazolidinone compounds with hydroxy functional ureido groups and their physical properties as additives and reactants. Israel, Modest, JMedChem., 14 (1971), 1042, describes a diamine compound containing a ureido hydrogen as an intermediate in the formation of a polyamine. The polyamine's growth-inhibitory activity was tested against KB cells (buman epidermoid carcinoma). The diamine intermediate compound has the formula: O H N-CH 2 CH 2 CH2- H CH 2 CH 2 H H I In US 3,919,233 certain imidazolidinone diamine compounds are reported as intermediates for the synthesis of antiviral compounds. Such imidazolidinone diamine compounds, however, do not have a ureido hydrogen atom on the imidazolidionone ring. Summary Of The Invention The present invention pertains to the the synthesis, purification, and physical properties of novel compounds containing a ureido group which are useful in preparing dispersions of polymers having good wet adhesion properties. The invention in one aspect pertains to nitrile compounds useful for incorporating ureido and optionally nitrile functionality into polymers, the compounds having the formula: NC-CH C 9 .-CH-N I -R 2 -N \ / NH II where R 1 is H or an alkyl group of up to 17 carbon atoms, R 2 is alkylene of up to 20 carbon atoms, optionally interrupted with one or more ether oxygen atoms, and A is a residue of an active hydrogen reactive compound, provided that when R 1 is H, A is a residue of an active hydrogen reactive compound which is an unsaturated isocyanate, an unsaturated anhydride, or an active hydrogen reactive compound which does not contain ethylenic unsaturation. A further aspect of the invention are certian compounds described more fully herein below, which have the formula III, or are derivatives of compounds of formula III: R 1 1 HN-CHp-CH, ,-CH-N- R 2 -N NH in where R 1 is H or an alkyl group of up to 17 carbon atoms, R 2 is alkylene of up to 20 carbon atoms, optionally interrupted with one or more ether oxygen atoms, and A and B are independently H or a residue of an active hydrogen reactive compound. The compounds of the invention have low volatility and provide numerous options for incorporating ureido hydrogen functionality into a wide variety of polymers. Polymers and polymer dispersions prepared from the nitrile or amine compounds of the invention are further aspects of the present invention. Especially preferred compounds of the invention are those in which at least one of A or B are H, or at least one of A and B include free radically polymerizable ethylenic unsaturation. Detailed Description of the Invention The compounds of the invention all include a ureido hydrogen atom on the imidazolidinone ring. The ureido hydrogen atom on the imidazolidinone group contributes to improved adhesion properties obtained with polymers of the invention and also provides a site for melamine crosslinking to improve heat and solvent resistance properties of polymers formed from the compounds of the invention. Compounds as in formula II except that A is Hydrogen are produced by cyanoalkylation of aminoalkyleneethyleneurea or aminoalkyleneoxyalkyJeneethyleneurea compounds of the formula. rv using acrylonitrile, 2-butenenitrile or higher 2-alkenenitriles. Particularily preferred are the compounds derived from 2-butenenitrile or 2-pentenenitrile. Other higher 2- alkenenitriles, however may also be used, in particular up to about C 20 , so that the R 1 alkyl group may have up to 17 carbon atoms. The group R 2 is an alkylene or alkylene interrupted with one or more ether oxygen atoms. The alkylene group may be linear, branched or cyclic. Suitably R 2 is a C j -C 2 o alkylene or alkyleneoxyalkylene group, more preferably C 2 -C 6 . A suitable example of an alkylene group interrupted with one or more ether oxygen atoms is alkyleneoxyalkylene, such as propyleneoxyethylene which may be provided as described in Example 10 below. Cyanoalkylation procedures are well known in the art. A representative literature example is Bruson "Cyanoethylation". Organic Reactions. Volume V, edited by R. Adams, John Wiley and Sons, Inc., New York, 1949.. Commercial cyanoalkylation service is offered by Tomah Products Co., Milton, Wisconsin and by Nova Molecular Technologies, Inc., Janesville, Wisconsin. The products of the cyanoalkylation reaction are nitrile adduct compounds of the formula: VI where R 1 and R 2 are as previously defined. Nitrile compounds as in formula VI where R 1 is alkyl, provide advantageous chemical and physical properties compared to similar compounds where R 1 is H. Such compounds may be incorporated into polymer structures by reaction of the secondary amino group, for instance by reaction with compounds having plural isocyanate or plural epoxy groups thereon. Further novel nitrile compounds of the invention are compounds of the formula II where A is: O -C-NH-R 3 S II , -C-NH-R 3 VI O II , -C-O-R 3 VII -CH -CH-R 3 VIII OH where R 3 is alkyl, suitably C -C 20 alkyl, optionally substituted with an alkoxyl group. The alkyl group may be linear, branched or cyclic. Reduction of the cyano group of such compounds yields a compound within the scope of formula m where A is a group of formulas V-Vπi and B is H. Such compounds are primary amines which can be utilized in the synthesis of poly(urethane urea) or epoxy/amine adduct polymers. Reduction of nitrile compounds disclosed herein, may be accomplished using reagents such as alkali borohydrides, H 2 /Raney nickel, etc., following procedures well known in the literature. An example of a Uterature reduction is found in Winas. U.S. Patent 2,334,140 (1943); Chem. Ahst, 38, 2666 (1944). Mono-amine compounds of the invention are provided when one, and only one, of A or B in formula UJ is hydrogen. Such compounds where A is H may be redily prepared by reaction of the corresponding diamine (i.e. where both A and B in formula III are H) with an active hydrogen compound since when R 1 is alkyl, especially ethyl or higher, the secondary amino site, A, is sufficiently less reactive than the primary amine site, B, that selective reaction at the primary amine is easily accomplished. Selective substitution at the secondary amine site, A, is possible as well, by reacting that site after formation of the nitrile but prior to reduction of the nitrile group to form the primary amine. Thus it is possible to obtain substitution, at either site. When reaction at both amine sites is desired with different reactive compounds, it is also feasible, when R 1 is alkyl, to react first the primary amine with one reactive compound and then the secondary amine with the second reactive compound. The amine compounds of the invention may be reacted in any conventional reaction of amines in polymer formation. Particular reactions within the scope of the invention are reactions with active hydrogen reactive compounds such as isocyanates, isothiocyanates, epoxies, carbonates, carboxylic or sulfonic acids, anhydrides, chloroformates, esters and alkyl halides. Chain extended polymers produced from diamine compounds of formula HI where A and B are H are characterized by the presence of a plurality of groups of the formula: IX where R 1 and R 2 are as previously defined. Such polymers are also characterized by the absence of imidazolidinone groups which do not contain ureido hydrogen. Monoamine compounds of the invention can be usefully employed as chain terminating agents in polyurethanes or epoxy/amine adduct polymers. The nitrile or amine compounds of the invention may alternatively be reacted to prepare radically polymerizable ethylenically unsaturated monomer and prepolymer compounds having pendant imidazolidinone functionality. Such compounds may be prepared by reaction of an ethylenically unsaturated active hydrogen compound, such as an unsaturated acid, isocyanate, isothiocyanate, ester, or epoxy compound, with a compound of formula II or III where at least one of A or B is H. Suitable examples of ethylenically unsaturated active hydrogen reactive compounds include, for instance, acrylic and methacrylic acids and their anhydrides or acid chlorides, isocyanatoethyl methacrylate, isocyanatoethyl acrylate, glycidyl acrylate, glycidyl methacrylate, vinyl glycidyl ether and a mono-, di-, or tri- isocyanate of the formula: X where each R 4 is independently a C,. 6 alkyl, R 5 is H or R 4 and n is 1-3. An alternative method of preparing ethylenically unsaturated imidazolidinone compounds within the scope of the invention is to react a plural isocyanate or epoxy functional compound with both an ethylenically unsaturated compound having an active hydrogen functional group, and an imidazolidinone compound of the formula III where at least one of A or B is H. Suitable examples of ethylenically unsaturated compounds having active hydrogen groups include allyl alcohol, allyl amine, acrylic acid, hydroxyethyl acrylate, hydroxypropyl acrylate, diethylene glycol monoacrylate, triethylene glycol monoacrylate, polyethylene glycol monoacrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate, diethylene glycol monomethacrylate, triethylene glycol monomethacrylate, polyethylene glycol monomethacrylate, crotonic acid, itaconic acid, maleic acid, fumaric acid and half esters of maleic and fumaric acids. Particularly preferred are compounds of formula III in which one of A or B, most preferably B, is the residue of an ethylenically unsaturated isocyanate, carboxylic acid or epoxy compound and the other of A or B, most preferably A, is the residue of an alkyl isocyanate (i.e. a residue as in formula V). Such compounds comprise two branched sites of ureido hydrogen atoms as well as ethylenic unsaturation for incorporation into free radically polymerized polymer structures. The compounds of the invention provide numerous advantageous properties to polymers into which they become incorporated. The pendant or terminal ureido hydrogen atom provided with the imidazolidinone functional group enhances polarity, improving adhesion of many polymer products of the invention. In the case of diamine compounds, by providing the imidazolidinone group on a chain extending monomer, polymer molecular weight can be built up while assuring extensive distribution of the imidazolidinone group throughout the polymer network. In reactions with isocyanates, the amine compounds of the invention provide urea linkages having improved chemical resistance over carbamate linkages, as well as better internal polymer strength and heat resistance due to hydrogen bonding. Non-volatile, water soluble diamines containing a ureido hydrogen have shown unexpected properties. Compared to similar low molecular weight, water soluble diamines the compounds of the invention exhibit extremely low vapor pressures. Reduced vapor pressures lower VOC and helps eliminate hazards through inhalation. The invention is illustrated by the following non-limiting examples. Example 1 2-Aminoethylethylene urea, corresponding to the formula XI 50 gm (.387 Eq), was dissolved in 100 ml isopropyl alcohol and heated to reflux. 2-pentenenitrile 34.53 gm (.425 Eq) was slowly added over a 2 hour period keeping the reaction mixture at reflux. This cyanoalkylation reaction forms the product diagramed below. XII Example 2 The solution containing the product of example 1 is cooled to 10 °C and 22.08 gm (.387 Eq) methyl isocyanate is slowly added keeping the reaction temperature around 10 °C. The product formed is diagramed below. XIII Example 3 To the reaction mixture from example 2 is charged an initial nickel metal catalyst, ammonia, and hydrogen gas then heated to 100 °C at 70 atm for approximately 4 hours. Solvent is stripped off. The resulting product is diagramed below. XIV Example 4 The amine product of Example 3 is dissolved in 100 gm (5.5 moles) de-ionized water. To this is slowly added 25.05 gm (.403 Eq) 96% active methacrylic anhydride and 2,000 ppm hydroquinone to form a compound: XV Example 5 To a reaction flask was charged 250 gm (3.46 moles) 2-butanone and 88.2 gm (.42 Eq) of the cyanoalkylation product of Example 1. The solution was heated to 50 °C and 125.8 gm (.42 Eq) octadecyl isocyanate was slowly added over a 15 minute period and heated an additional 15 minutes. The solution was cooled to room temperature and the precipitate was filtered. The white solid has a melting point of 94-96 °C. The nitrile was reduced as described in example 3 and the resulting product was reacted with m-TMI, i.e. (benzene, l-(l-isocyanato-l -methyl ethyl)-3-( 1 -methyl ethenyl)), to form a compound: XVI Example 6 2-Aminoethyl ethylene urea was disolved in water and heated to 100 °C. 2-pentenenitrile was slowly added over a 2 hour period keeping the reaction mixture around 100 °C. The product, a nitrile as produced in Example 1, was not isolated. To the reaction mixture was charged an initial metal catalyst, ammonia, and hydrogen gas then heated to 100 °C at 70 atm for approximately 4 hours. The resulting product was analyzed by GC/MS to give a composition described below. Compound Weieht % Amyl amines 6.53 1,3- Diaminopentane 1.46 2-aminoethyleneurea 0.566 Unknowns 0.6616 Desired product 80.47 Water 10.3 The reaction product was purified by short path distillation. The unit was a two stage glass distact still from UIC Inc. The first stage was run at a relatively low vacuum (60 mmHg) and temperature (140 °C) to remove low boilers (Amyl amines, 1,3 diaminopentane, 2-aminoethyl ethylene urea, and water). The second stage was run with a low vacuum (.1 mm Hg) and decreased temperatures (110 °C) to separate the desired product from high boilers (unknowns). The process recovered 87% of the desired product. The sample, a clear, colorless, semi-viscous liquid, was characterized by carbon 13 and amine titration. The carbon- 13 NMR spectra of the sample dissolved in deuterated chloroform indicated a purity level very high, nearly 100%. The measured amine number of 522 mg KOH/g material yields an approximate diamine content of 98% corresponding to the formula: XVII The physical properties of this diamine are described below: Molecular weight = 214 grams/mol Purity = Greater than 98% Appearance/odor = Clear liquid/odorless Gardner color = Less than 1 Viscosity = 800 centipoise Solubility in water = Complete Aqueous surface tension = 57.85 dynes/cm pKb's at 25 °C = 3.8 and 6.5 ph of 1% solution = 10.25 Flash point (ASTM D-93) = > 450 °F Boiling point = 160 °C at .05 torr Vapor pressure = 0.000004 torr at 25 ° Volatilization = Non-volatile (Federal Test Method #24) The list below compares several water soluble, liquid diamines and their vapor pressures. Diamine Vapor Pressure Ethylene Diamine (60.10 g/mol) 10.0 torr at 25 °C 1,3-diaminopentane (102 g/mol) 3.5 torr at 25 °C m-Xylylene diamine (136g/mol) 0.1 torr at 25 °C Diamine of formula XVII (214 g/mol) 0.000004 torr at 25 Example 7 To a reaction flask was charged 68 gm (.310 moles) of the diamine for formula XVII, 70 gm (.97 Moles) 2 butanone. This mixture was cooled to 0 °C and 62.50 gm (.310 moles) m-TMI, was slowly added keeping the reaction temperature betweem 0-5 °C. After evaporating off solvent the material was analyzed using carbon 13 NMR. The sample, a clear, colorless, viscous liquid had a composition described below. Species Relative Intensity m-TMI/primary amine 0.775 m-TMI/secondary amine 0.107 Unreacted diamine 0.118 The results indicate a majority of the product formed corresponds to the structure: Ctfc O XVIII Example 8 44.6 gm (.208 moles) of the diamine diagramed below XVII was dissolved in 34 gm (1.9 moles) de-ionized water containing 2,000ppm hydroquinone. To this solution was slowly added 32.09 gm (.208 Moles) of methacrylic anhydride keeping the temperature below 60 °C. The sample, a clear, colorless, semi-viscous liquid, was dissolved in deuterated water and analyzed by Carbon 13 NMR. Interpretation of this spectrum detected no unreacted diamine and the methacrylic anhydride reacts exclusively with the primary amine to form the compound : XIX Example 9 2-aminoethyl ethylene urea is cyanopropylated with 2-butenenitrile in the manner of example 6 to provide a nitrile compound of the formula: CH 3 O NC-CH 9 -CH-N-CH CH -N NH i 2 2 \ / H XX The nitrile is then reduced, also in the manner of example 6, to provide a diamine having the formula: XXI Example 10 Hydroxyethylethyleneurea was cyanoethylated with acrylonitrile and then reduced in a process similar to Example 6 to produce a monoamine of the formula: XXII This monoamine when cyanobutylated and reduced as in Example 6 will provide a diamine of the invention having the formula: C 2 H 5 O H N CH„ CH CH«- N-CH„ CH„ CH«- 0 -CH- CH~ — N NH H H xxm POLYMER PREPARATION EXAMPLES Example 11 - Non-ionic Polyurethane/urea Dispersion To a reaction flask was charged 65.3 gm (.1306 Eq) polyethylene glycol, 25.81 gm (.2325 Eq) isophorone dusocyanate and two drops of Metacure™ T-12 dibutyl tin dilaurate. This mixture was heated for 3 hours at 90 °C using overhead stirring. When the isocyanate content reached approximately 4.7% one hundred grams of deionized water was charged to disperse prepolymer. To 50 gm deionized water was charged 9.1 gm of the imidazolidinone diamine of the formula I and this mixture was added to reaction vessel over a 3 minute period. Properties of the dispersion and test results are as follows: pH = 8.9 Viscosity = 3,850 mPas Solids = 39.27% To this dispersion was added 5% by weight Desmodur DA (water dispersible polyfunctional isocyanate). The formulation was then applied to particle board by spraying and dried for 10 minutes. Substrates were vacuum formed using heat and aged 24 hours at ambient room temperature. 180 degree peel results: peak reading = 1409 g/cm valley reading = 204 g/cm average peel value = 1154 g/cm The peak and average values are determined by using a slip/peel tester (Model SP-101B, IMASS Inc). The slip/peel tester measures the coefficient of friction between surfaces or peel strengths of adhesives. The test speeds were set at 2 inches (5.08 cm) per minute for 60 seconds. Example 12 - Anionic Polyurethane/urea Dispersion To a reaction flask with efficient stirring and heating was charged 423 gm (.3021 eq) butane diol adipate polyester polyol, 3.0 gm (.0671 eq) trimethylolpropane, 19 gm (.2836 eq) dimethylolpropionic acid, 141 gm (.1.156 eq) meta-tetramethylxylene dusocyanate, and 13.6 gm (.1344 Moles) triethylamine. The mixture was heated approximately 3 hours at 90°C. When the prepolymer reached 3.5% isocyanate 903.25 gm deionized water was added to disperse. To 50 gm deionized water was charged 27.92 gm of the imidazolidinone diamine of formula I, 5.22 gm monoethanolamine and 2.76 gm diethylenetriamine. This mixture of mono, di, and tri-functional amines were added to the dispersion over a 3 minute period. Physical properties of dispersion and test results are as follows: pH = 7.87 Viscosity= 3,150 mPas Solids = 40.24% Particle size: Effective diameter = 74 nanometers Mean diameter = 63 nanometers A 2 ml dry film was applied to PVC substrates which were then joined under 50 psi pressure at the temperatures given below for 30 seconds. The loads at which the bond failed when tested under T-peel conditions are given below. 125°F = 284 g/cm 150°F = 618 g/cm 175°F = 1151 g/cm 200°F = 1199 g/cm Example 13 - Emulsion Polymerized Imidazolidinone Functional Latex In a 100 ml round bottom flask was charged 95.10 gm acetone, 50.14 gm Jeffamine * ED-2001 polyethoxylated/propoxylated diamine, 6 gm of the imidazolidinone diamine of formula I and 3 gm allylamine. The mixture was heated and stirred until the ingredients were disolved and then 19.8 gm tetramethylxylenediisocyanate was added slowly. The mixture was then refluxed until isocyanate, as monitored by infrared, had substantially all been consumed. The acetone solvent was then removed by evaporation, yielding an allylic imidazolidinone functional oligomer. To a two liter flask equipped with stirrer, condenser, nitrogen inlet, temperature controlled water bath and monomer addition pump were charged 236.1 gm of deio izes water. The water bath was heated so as to provide a reaction temperature of 65°C. Five percent of a monomer mixture containing 134.5 gm deionized water, 36.8 gm of 30 mole ethoxylated octylphenol surfactant, 221 gm butyl acrylate, 157.6 gm methyl methacrylate, 5.9 gm methacrylic acid and 42.7 gm of the allylic imidazolidinone functional oligomer of the previous paragraph was charged to the reaction vessel. 1.24 gm each of ammonium persulfate and sodium metabisulfite were then added to the vessel to initiate the polymerization reaction. The remainder of the monomer mixture was added over a three hour period. Meanwhile, additional feeds of 1.29 gm ammonium persulfate in 24 gm deionized water and 1.29 gm sodium metabisulfite in 24 gm deionized water were added to the reactor vessel over a time period of 4 hours. One half hour after the addition of the catalyst was complete, the contents of the reactor were cooled and discharged. The product was an aqueous latex having a solids content of 46.0%, a pH of 6.0, a particle size of 210 nm, a Brookfield viscosity of 40 mPas, and coagulum content of only 0.1%. The polymer had an intrinsic viscosity of 0.335 and an acetone insoluble content of 61%. Example 14 To a reaction flask fitted with overhead stirrer, thermometer and nitrogen inlet is charged a polyester polyol along with 5% by weight of the imidazolidinone diamine of formula I. The mixture is heated to 85-90°C and amine number monitored to determine reaction completion. The product is a polyester/polyamide polyol. Example 15 The imidazolidinone diamine of the formula I was incorporated into a thermoforming water dispersible polyurethane and compared with a control formulation utilizing the same number of equivalents of mono, di, and triamine. The formulations are shown in Table 1. TABLE 1 Equivalents of active group Component Control Example Number Component 15 1 Hexanedioic acid/butanediol polyester diol (Rucoflex ™ S-102- 0.3021 0.3021 40) 2 Trimethylolpropane 0.0671 0.0671 3 Dimethylolpropionic acid 0.2836 0.2836 4 l,3-Bis(l-isocyanato-l- 1.156 1.156 methylethyl)-benzene 5 Monoethanolamine 0.1245 0.0856 6 Ethylenediamine 0.2463 7 Formula I diamine: Equivalents diamine 0.2463 Equivalents monoamine 0.0389 8 Diethylene triamine 0.081 1 0.0811 The respective formulations were prepared by drying component (1) under vacuum in a clean reactor at 110°C for 1 hour; adding components (2), (3) and (4) with agitation and holding the temperature at 90°C for 4 hours (NCO content approximately 3.5%); adding the amines (5)-(8) to a sufficient quantity of deionized water to provide a 39.25% solids formulation when added to the reactor; and then adding the amine/water mixture to the reactor over a 3 minute period. Properties of the respective dispersions were as follows: Control Example 15 pH = 8.0 pH = 8.0 Viscosity = 50 mPas Viscosity = 260 mPas Solids = 39.2% Solids = 39.3% Mean particle size = 89 nm Mean particle size = 63 nm Heat activating temperatures of the two polymer dispersions were tested on untreated vinyl and results indicated substantially similar heat activating properties. The two dispersions were then tested on ABS/vinyl with 5% Desmodur DA as a polyfunctional isocyanate crosslinker and a heat activation temperature of 50°C for 20 seconds was applied. After a 24-hour period at room temperature, peel values on both polymers gave vinyl failure. The two dispersions were also tested at 90°C for 24 hours and results demonstrated that the dispersion employing the invention polymer with imidazolidinone functionality dramatically improved adhesion at these elevated temperatures. Example 16 To a reaction flask was charged 24.2 gm (.039 Eq) Joncryl 587 which is a hydroxy functional styrene/acrylic copolymer from S.C. Johnson Wax, 225 gm (1.717 Eq) hydrogenated MDI, and 197 gm of n-methyl pyrrolidone. This mixture was heated at 85 °C for 1 hour. To this was charged 24.2 gm (.361 Eq) dimethylolpropionic acid, 183 gm Rucoflex S- 102-1 10 (a butanediol/adipate polyester polyol). The mixture was heated for 2-3 hours at 85 °C. The diamine of formula XVII, 34.5 gm (.3224 Eq), was slowly added to this mixture over a 15 minute period. Then 17.6 gm (.174 moles) triethylamine was added and the prepolymer was dispersed in 740 gm (41.1 moles) de-ionized water. To the dispersion was charged a solution containing 3.2 gm (.094 Eq) diethylene triamine, 11.6 gm (.386 Eq) ethylene diamine, and 27 gm (1.5 moles) of de-ionized water. The aqueous and dried physical properties of the polymer are described below. Color,wet Translucent Color,Dry Clear Solids 35% Viscosity 50 cps (mPa.s) -19- Tabor Abrasion 33.8 mg loss (H-18 wheel, 100 cycles, 1 kg weights) Shore D Hardness 80 (ASTM 2240-75) Pencil Hardness 2B (ASTM D 3363-74) Gloss: 20 Degrees 92.7% 65 Degrees 90.3% 85 Degrees 99.8% Tensile Strength 1,700 psi Elongation 180% 3 -Day solvent swell (Linear) @ 60 °C Water 0% (Clear) Xylenes 10% (Clear) Skydrol 40% (Clear) Water/Ethylene glycol (50:50) 10.5% (Clear) Tg -50 °C Cahn Dynamic Contact Angle Analyzer: Wicking rate (water) 0.0120 mg/sec Dried film surface tension 35.46 dynes/cm Example 17 To a reaction flask was charged 300 gm (.294 Eq) Rucoflex S-1011-55, a diethylene glycol/adipate polyester polyol, 16.2 gm (.24 Eq) dimethylolpropionic acid, 96 gm TMXDI (.7869 Eq), 12.3 gm (.121 moles) triethylamine, and 0.14 gm Metacure T-12. The mixture was heated to 80 °C until isocyanate reached 2.3%. The prepolymer was dispersed in 599 gm (33.28 moles) de-ionized water and then slowly a mixture containing 3.15 gm (.05 Eq) monoethanolamine, 18 gm (.168 Eq) of the diamine of formula XVII, and 29 gm (1.61 moles) de-ionized water was added. The resulting polymer properties are described below. pH = 8.29 Viscosity = 180 cps Mean diameter particle size = 51 nm Solids = 40.57 Dried film = Clear and slightly tacky Example 18 To a reaction flask was charged 271.74 gm hexanediol, 311.31 gm adipic acid, .6 gm Fascat 9100, and 16.36 gm of a diamine of formula XVII. The mixture was heated to 210 °C for 3.5 hours while pulling off water. An additional hour pulling off water at 30 inches Hg and 220 °C completes the reaction. The sample, a beige, waxy solid was tested to have an acid number of 0.55 and a hydroxy value at 52.0 (Theoretical = 54.87). The melt point using a differential scanning calorimeter was Tm = 55.63. GPC weight average and number average molecular weights of high polymers are 7,600 g/mol and 4,280 g/mol. Example 19 Wet adhesion monomer (WAM) synthesis The following components were charged to a three neck round bottom flask, equipped with a thermometer and a magnetic stirring bar. Components Grams Methyl methacrylate 50.0 Methacrylic Anhydride 3.0 Diamine of formula XVII 3.91 P-Toluene Sulfonic Acid 2.91 (65% active) Methyl methacrylate and methacrylic anhydride were mixed; then the diamine of formula XVII was added slowly, keeping the temperature below 35° C. The disappearance of anhydride was monitored by IR Spectroscopy. Once the anhydride was consumed, the secondary amine was neutralized with the sulfonic acid. Other acids like acetic acid, formic acid, hydrochloric acid, and sulfuric acid may also be used. Latex Synthesis Reactor Charge Comoonents Amount fεrams) Deionized Water 370.0 Triton X-200 6.8 (Union Carbide Chemical) Glacial Acrylic Acid 6.1 Ammonia Hydroxide 6.1 Initiators Components Amount (erams Potassium Persulfate 2.0 Tert butyl hydroperoxide 0.20 Hydrosulfite 0.14 Tert butyl hydroperoxide 0.20 Hydrosulfite 0.14 Surfactants, Defoamers, and Antimicrobials Components Amount (grams) Triton X-200 6.8 Bubble Breaker 748 0.14 (Witco Corporation) Proxel GXL Antimicrobial 1.5 (Dow Corning) Monomer Charge Components Amount (grams') N-butyl acrylate 218 Methyl methacrylate 21 1 methacrylic acid 1.0 Pre-emulsion synthesis A reactor was charged with 74g water, 6.8g Triton X-200, and mixed for 15 minutes to disperse. With good agitation, N-butyl acrylate, methyl methacrylate, the wet adhesion monomer mixture described above, and methacrylic acid were charged respectively over a 30 minutes period. Polymerization To a reactor was charged water, Triton X-200, and acrylic acid. Adjust pH to 7-8 with ammonium hydroxide. The bubble breaker 748 was added and the contents heated to 80°C. Two percent of the pre-emulsion synthesis mixture was charged with the potassium persulfate catalyst and then the mixture was held for 15 minutes. The pre-emulsion mixture was then fed uniformly over a three hour period. The mixture was held an extra 30 minutes after the pre-emulsion addition was complete. Then the first treat of t-butyl hydroperoxide was added, followed by hydrosulfite. The mixture was held 10 minutes then the second peroxide treat added and the mixture heated an additional 30 minutes. The reaction mixture was then cooled below 30°C and the Proxel GXL was added. The pH was adjusted to 9.5 with ammonium hydroxide. Properties of the resulting polymer dispersion are described below: pH = 9.5 Viscosity = 60 centipoise Particle size = 230 nm Example 20 Example 19 was repeated with a wet adhesion monomer synthesized with a monofunctional isocyanate. WAM synthesis To a three neck round bottom flask, equipped with a thermometer and a magnetic stirring bar, were charged the following components: Components Amount (erams) Methyl methacrylate 50.0 Methacrylic Anhydride 3.0 Diamine of formula XVII 3.91 Phenyl isocyanate 2.1 Methyl methacrylate and methacrylic anhydride were mixed together. Diamine of formula XVII was added slowly keeping the temperature below 30 Deg°C. The reaction was monitored by IR spectroscopy and was complete with the disappearance of anhydride. To this mixture was slowly added phenyl isocyanate and monitored by IR. Properties of latex obtained are described below. pH = 9.8 Viscosity = 1,800 cps Solids = 51.77% Particle size (Mean diameter)= 208 nanometer, monomodal Example 21 Polymer synthesis was repeated as described in example 19 except the wet adhesion monomer composition was varied. WAM synthesis A three neck round bottom flask, equipped with a thermometer and magnetic stirring, was charged with the following components: Components Amount (erams) Methyl methacrylate 50.0 Methacrylic Anhydride 3.0 Diamine of formula XVII 3.91 Cyclohexyl isocyanate 2.1 Methyl methacrylate and methacrylic anhydride were blended together then Diamine of formula XVII was slowly added over a 5 minute period keeping the temperature below 35° C. To this was slowly added cyclohexyl isocyanate keeping the temperature below 35° C. This latex's properties are described below. pH = 9.3 Viscosity = 80 centipoise Solids = 51.83% Particle size (Mean diameter) = 306 nm The monomer synthesis described above is the process of choice. The imidazolidinone diamine is modified in a reactive diluent eliminating the use of organic solvents. The WAM monomers generated using this process were easily synthesized in a one batch process. Example 22 A latex was formulated into a semi-gloss paint and tested for wet adhesion characteristics. Wet adhesion monomer Components Amount (grams) Methyl methacrylate 50.0 Methacrylic anhydride 3.0 Diamine of formula XVII 3.91 Phenyl isocyanate 2.1 Reactor charge Components Amount (grams) Deionized water 370.0 Triton X-200 6.8 Glacial acrylic Acid 6.1 Ammonia hydroxide 6.1 Initiators Components Amount (grams) Potassium persulfate 2.0 t-butyl hydroperoxide (0.20) x 2 Hydrosulfite (0.14) x 2 Monomer Charge Components Amount (grams) n-Butyl acrylate 218.0 Methyl methacrylate 211.0 Methacrylic acid 1.0 Surfactants, Defoamers, and Antimiccrroobbiiaallss Components Amount (grams) Triton X-200 6.8 Bubble breaker 748 0.14 Proxel GXL antimicrobial 1.5 This latex was formulated into a semi-gloss paint.

Claims: Pigment grind Components Amount (grams) Water 66.6 Colloid 226/35 (Rhone-Poulenc) 6.2 Nuosept 95 (Huls America) 1.5 AMP-95 (Angus Chemical) 1.5 Polyphase AF-1 (Troy Chemical) 4.0 Igepal C0-630 (Rhone-Poulenc) 3.5 Tiona RCL-2 (SCM Chemicals) 250.0 Atomite (ECC America) 20.0 ASP- 170 (Englehard Corporation) 30.0 Drewplus L-464 (Drew Industries) 1.8 Letdown Components\ Amount (grams) Water 218.4 Latex described above 400.5 Propylene Glycol 47.6 Texanol (Eastman Chemical) 15.1 Rheolate 278 (Rheox, Inc.) 7.0 Natrosol 250 MHBR (Aqualon Company) 2.7 Drewplus L-464 3.7 The paint (1.5 grams) described above was brushed onto an alkyd resin coated board, covered with cheese cloth, then coated again with paint(4.9 grams). This was dried at ambient room temperature for 7 days. The painted substrate was soaked in water for 1 hour and tested on an Intellect ® 500 for 180° peel adhesion. This sample had a wet adhesion peel value of 7.2 kilograms/linear inch. Example 23 To a reaction vessel was charged 345 gm (.6765 Eq) butanediol adipate polyester polyol, 37.1 gm (.5537 Eq) dimethylolproprionic acid, 320 gm (2.62 Eq) tetramethylxylene dusocyanate (TMXDI) and 26.5 gm (.262 moles) triethylamine. This mixture was heated at 80°C until percent isocyanate was 8.0. The prepolymer was dispersed in 1,254 gm de-ionized water and to this was charged a mixture containing 134 gm (1.25 Eq) of the diamine of example 6 in 275 gm deionized water. The resulting polymer dispersion properties were: pH = 7.6 Viscosity = 80 centipoise Mean Particle size = 59 nanometers Solids = 36.6% Dried film = Clear. Claims What is claimed is: 1. A compound of the formula: where R 1 is H or an alkyl group of up to 17 carbon atoms, R 2 is alkylene of up to 20 carbon atoms, optionally interrupted with one or more ether oxygen atoms, and A is a residue of an active hydrogen reactive compound, provided that when R 1 is H, A is a residue of an active hydrogen reactive compound which is an unsaturated isocyanate, an unsaturated anhydride, or an active hydrogen reactive compound which does not contain ethylenic unsaturation. 2. A compound as in claim 1 wherein said active hydrogen reactive compound is selected from the group consisting of isocyanates, isothiocyanates, epoxies, carbonates, carboxylic or sulfonic acids, anhydrides, chloroformates, esters and alkyl halides. 3. A compound as in claim 1 wherein A is O — C-NH-R 3 . S —C-NH-R 3 ; II — C-O-R 3 or -CH 2 -CH-R 3 OH where R 3 is a linear, branched or cyclic alkyl, optionally substituted with an alkoxyl group. 4. A compound as in claim 1 wherein A is a residue of an isocyanate compound which does not include ethylenic unsaturation. 5. A compound as in claim 1 wherein A is a residue of an isocyanate, epoxy or anhydride compound which includes ethylenic unsaturation. 6. A compound of the formula: O R 1 II HN-CH -CH 9 -CH-N-R 2 -N NH B A where R 1 is H or a C,-C| 7 alkyl group and R 2 is C,-C 20 alkylene optionally interrupted with one or more ether oxygen atoms, A and B are different groups and one of A and B is H or a group having ethylenic unsaturation and the other of A and B is a residue of a active hydrogen reactive compound, provided that said residue of said active hydrogen reactive compound does not include an active hydrogen group or ethylenic unsaturation. 7. A compound as in claim 1 or claim 6 wherein said active hydrogen reactive compound is a compound having a free radically polymerizable ethylenically unsaturated group thereon. 8. A compound as in claim 7 wherein said active hydrogen reactive compound is selected from the group consisting of acrylic and methacrylic acids and their anhydrides and acid chlorides, isocyanatoethyl methacrylate, isocyanatoethyl acrylate, and a mono-, di-, or tri-isocyanate of the formula: where each R 4 is independently a C,. 6 alkyl, R 5 is H or R 4 and n is 1-3. 9. A compound as in claim 6 wherein said residue of said active hydrogen reactive compound has the formula:: o II —C-NH-R 3 . I S —C-NH-R 3 : or O II — C-O-R 3 where R J is a linear, branched or cyclic alkyl, optionally substituted with an alkoxyl group. 10. A compound as in claim 6 wherein said active hydrogen reactive compound is a compound selected from the group consisting of isocyanates, isothiocyanates, carboxylic or sulfonic acids, anhydrides, chloroformates, esters and alkyl halides. 1 1. A compound comprising a reaction product of an isocyanate or epoxy functional compound and a compound of the formula: 1 I O I I HN-CH 2 -CH 2 -CH-N-R 2 -N; NH k where R 1 is H or a C,-C I7 alkyl group and R 2 is C,-C 20 alkylene optionally interrupted with one or more ether oxygen atoms, one of A and B is H and the other of A and B is: o —C-NH-R 3 . I S —C-NH-R 3 : or O II —C-O-R 3 where R 3 is a linear, branched or cyclic alkyl, optionally substituted with an alkoxyl group. 12. A compound prepared by reaction of: a) a plural isocyanate or epoxy functional compound, b) an ethylenically unsaturated compound having an active hydrogen functional group, and c) a compound of the formula: where A is H, B is a residue of an active hydrogen reactive compound, provided that B does not include an active hydrogen group, R 1 is a C,-C 17 alkyl group and R 2 is C,-C 20 alkylene optionally interrupted with one or more ether oxygen atoms. 13. A compound as in claim 12 wherein said ethylenically unsaturated compound (b) is selected from the group consisting of allylalcohol, allylamine, acrylic acid, hydroxyethyl acrylate, hydroxypropyl acrylate, diethylene glycol monoacrylate, triethylene glycol monoacrylate, polyethylene glycol monoacrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate, diethylene glycol monomethacrylate, triethylene glycol monomethacrylate, polyethylene glycol monomethacrylate, crotonic acid, itaconic acid, maleic acid, fumaric acid and half esters of maleic and fumaric acids. 14. A compound prepared by reaction of: a) an ethylenically unsaturated acid, isocyanate, isothiocyanate, ester, or epoxy compound, and b) a compound of the formula: where one of A and B is H. and the other of A and B is a residue of an active hydrogen reactive compound, provided that said residue does not include an active hydrogen group, R' is a C^-C^ alkyl group and R 2 is C,-C 20 alkylene optionally interrupted with one or more ether oxygen atoms. 15. A compound as in claim 13 wherein said ethylenically unsaturated compound (a) is selected from the group consisting of acrylic and methacrylic acids and their anhydrides and acid chlorides, isocyanatoethyl methacrylate, isocyanatoethyl acrylate, glycidyl acrylate, glycidyl methacrylate, vinyl glycidyl ether and a mono-, di-, or tri-isocyanate of the formula: where each R 4 is independently a C,_ 6 alkyl, R 5 is H or R 4 and n is 1-3. 16. A compound as in any of claims 1-15 wherein R 1 is methyl or ethyl. 17. A compound as in any of claims 1-16 wherein R 2 is ethyl or ethyleneoxypropylene.

Inventors: DOCHNIAK MICHAEL J, DOCHNIAK, MICHAEL, J.
Applicants: FULLER H B LICENSING FINANC, H.B. FULLER LICENSING & FINANCING, INC.
Application year: 1995
Main classification: C07D233
IPC codes: C07D233, C08F290, C08G18, C08G59