Preparation process of biodegradable block copolyesters

Abstract: The invention is a process for preparing a degradable copolymer of aliphatic polyester comprising the steps of reacting two or more kinds of aliphatic polyester homopolymer in the presence of a catalyst in a reaction mixture containing an organic solvent, and a degradable copolymer of aliphatic polyester obtained by said preparation process; the copolymer obtained has a high transparency in addition to excellent strength and elongation, can be processed into various molded articles and formed items such as films and filaments, and can provide heat resistance by heat treatment of said molded articles and formed items; and thus the copolymer can be suitably utilized for processed articles such as a film, breathable film, sheet, textile, monofilament, multifilament, yarn, non-woven fabric, flat yarn, staple, crimpt fiber, ribbed tape, split yarn, conjugate fiber, laminate, blow-bottle, sheet, stretched sheet, foam and net.

Description: The present invention relates to a preparation process of a biodegradable copolymer of aliphatic polyester useful for medical materials and substitutes of general purpose resins. More specifically, the invention relates to a process for preparing a biodegradable copolymer of aliphatic polyester compounds which is obtained by reacting two or more homopolymers of the aliphatic polyester compounds in the presence of a catalyst in a reaction mixture containing an organic solvent ; and a biodegradable copolymer of aliphatic polyester prepared by said preparation process. The biodegradable copolymer of aliphatic polyester which can be prepared by the process of the invention is excellent, as compared with homopolymers, in heat resistance, transparency, elongation, flexibility, plasticity and shaping ability, and can be processed into medical materials and substitutes of general purpose resins in the form of a molded article, film, sheet, filament, yarn and foam having strength, elongation, transparency and heat resistance which satisfy the object. The polymer of aliphatic polyester is characterized by hydrolyzing with ease in the presence of water and wasted articles can degrade without contaminating the environment when the polymer is used as a general purpose resin. Consequently, the polymer was already focused attention as an environmentally friendly substitute of general purpose resins prior to the application of the invention. Further, in the case of dwelling the polymer in a living body as a medical material, the polymer can be decomposed and absorbed in the living body after accomplishing the object without giving toxicity to the living body. Thus, the polymer was focused attention before the present application as a medical material which is friendly for the living body. In many cases, however, an aliphatic polyester homopolymer alone cannot fully satisfy desired properties as a medical material or a substitute of general purpose resins. For example, polylactic acid is brittle, hard and lacking in flexibility. These properties have led to problems when the polymer is processed into films, filaments and molded articles. That is, conventional technology could not provide with ease aliphatic polyester having softness, flexibility, transparency and high heat resistance. US 3,736,646 and 3,982,543 have disclosed to use a volatile solvent as a plasticizer in order to provide flexibility for a lactide copolymer. However, when the polymer is processed into film or molded articles and used for preservation of products, food containers or medical devices, gradual evaporation of the solvent eliminates the plasticizing effect and causes problems on the quality retention of the products. At the same time, the released solvent from the polymer is possible to give a toxic effect on the food or the living body which is in contact with the polymer and has problems in view of safety insurance. US 3,636,956 and 3,797,499 have disclosed an L-lactide/D,L-lactide copolymer which can be used for a surgical suture. The patent has also described that plasticizers such as glycerol triacetate, ethyl benzoate and diethyl phthalate are added, in order to provide plasticity, to the copolymer which lacks plasticity. When no plasticizer is added to the copolymer, it is a problem that the copolymer has a low elongation at break of only about 10 %. On the other hand, when these plasticizers are added to the copolymer, it is naturally anticipated to cause a problem that food packaging containers and medical devices under use eluate these plasticizers and give a toxic effect on the living body, or the plasticizers eluated from abandoned articles contaminate the natural environment. Polylactic acid and other polymers having a high brittleness, high hardness and low flexibility are also considered to improve physical properties by mixing with other polymers having a high ductility or plasticity, high softness and high flexibility. However, compatibility between homopolymers of different kind is generally low. Thus, it is extremely difficult to obtain a polymer alloy having improved properties by mixing two or more homopolymers of different kind in the absence of a compatibilizer. For example, when the compatibility between homopolymers is low even though two homopolymers individually have transparency, it is difficult to obtain the polymer alloy having the improved properties while maintaining transparency. US 4,057,537 has disclosed a non-rubber-like copolymer having impact resistance, brittleness resistance and heat resistance which is obtained by heating an L-lactide/ε-caprolactone mixture containing 75 to 90 % of L -lactide at a temperature between the melting point of L-lactide and 200°C in the presence of a catalyst. The patent has also described that a copolymer containing 15 % or more of ε-caprolactone is soft and transparent. These copolymers however, have disadvantages of low or no crystallinity and low heat resistance. Japanese Laid-Open Patent HEI 7-173266 has disclosed a preparation process of a linear lactic acid type copolyester by subjecting lactide, that is, the cyclic dimer of lactic acid and linear aliphatic polyester consisting of an aliphatic dicarboxylic acid ingredient and an aliphatic diol ingredient to a ring-opening polymerization and ester exchange reaction in the presence of a ring-opening polymerization catalyst. The present inventors have carried out an intensive investigation in order to improve properties of a homopolymer which are difficult to fully satisfy the requirement for use in a substitute of general purpose resins or a medical material. As a result, they have found that a copolymer can be obtained with ease by reacting two or more kinds of aliphatic polyester homopolymer in the presence of a catalyst in a reaction mixture containing an organic solvent, and that the copolymer thus obtained has a highly blocked structure and can satisfy the required properties. Thus, the present invention has been completed. That is, the aspect of the invention is a process for preparing a biodegradable copolymer of aliphatic polyester comprising reacting two or more kinds of an aliphatic polyester homopolymer in the presence of a catalyst in a reaction mixture containing an organic solvent, and a degradable copolymer of aliphatic polyester which is prepared by said process. The homopolymer of aliphatic polyester which can be used as a raw material in the invention is a polyhydroxycarboxylic acid prepared from one or more kinds of hydroxycarboxylic acid such as lactic acid, glycolic acid, 3-hydroxybutyric acid, 2-hydroxybutyric acid, 3-hydroxyvaleric acid, 5-hydroxyvaleric acid and 6-hydroxycaproic acid, and an aliphatic polyester obtained by reacting a polyhydric alcohol such as ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, propylene glycol, dipropylene glycol, 1,3-butanediol, 1,4-butanediol, 3-methyl-1,5-pentanediol, 1,6-hexanediol, 1,9-nonanediol, neopentyl glycol, polytetramethyleneglycol, 1,4-cyclohexanedimethanol and 1,4-benzenedimethanol, with a polybasic acid such as succinic acid, oxalic acid, malonic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, undecanoic diacid, dodecanoic diacid, phenylsuccinic acid and 1,4-phenylenediacetic acid. The two or more kinds of the aliphatic polyester homopolymer used in the preparation process of the invention can be a combination of polyhydroxycarboxylic acid and aliphatic polyester prepared from polyhydric alcohol and polybasic acid, or a combination of two or more kinds of polyhydroxycarboxylic acid alone. Polylactic acid is particularly preferred in view of strength and transparency. Polycaprolactone, that is the polymer of 6-hydroxycaproic acid, and polybutylene succinate, that is the polymer obtained from 1,4-butanediol and succinic acid are particularly preferred in view of elongation and flexibility. Each homopolymer of aliphatic polyester which can be used in the preparation process of the invention has a weight average molecular weight of preferably 10,000 or more respectively. The weight average molecular weight less than 10,000 decreases crystallinity of the polymer obtained and reduces below described effect of heat treatment on improving heat resistance. The content of each homopolymer in the copolymer can be suitably selected depending upon the combination of each homopolymer and desired properties. For example, polylactic acid and polybutylene succinate are used as the raw material homopolymer, the proportion of polybutylene succinate unit in the copolymer is preferable in the range of 11 to 51 % by weight. When the proportion is too low, satisfactory softness, ductility or plasticity, and flexibility cannot be obtained. On the other hand, too high content unfavorably lowers transparency. The range of 21 to 37 % by weight is more preferred and a copolymer having high flexibility and transparency can be obtained in the range. When polylactic acid and polycaprolactone are used as the raw material homopolymer, the proportion of polycaprolactone unit in the copolymer is preferably in the range of 5 to 35 % by weight. A too low proportion cannot provide satisfactory softness, ductility or plasticity, and flexibility. On the other hand, too high proportion leads to lack of heat resistance. Exemplary solvents which can be used for preparing aliphatic polyester copolymer of the invention include for example, toluene, xylene, mesitylene and other hydrocarbon solvents; chlorobenzene, bromobenzene, iodobenzene, dichlorobenzene, 1,1,2,2-tetrachloroethane, p-chlorotoluene and other halogenated hydrocarbon solvents ; 3-hexanone, acetophenone, benzophenone and other ketone solvents ; dibutyl ether, anisole, phenetol, o-dimethoxybenzene, p-dimethoxybenzene, 3-methoxytoluene, dibenzyl ether, benzyl phenyl ether, methoxynaphthalene and other ether solvents; diphenyl sulfide, thioanisole and other thioether solvents; methyl benzoate, dimethyl phthalate, diethyl phthalate and other ester solvents, diphenyl ether, 4-methyldiphenyl ether, bis(3-methylphenyl) ether, 3-phenoxy toluene and other alkyl substituted diphenyl ether solvents; 4-bromodiphenyl ether, 4-chlorodiphenyl ether, 4-methyl-4'-bromodiphenyl ether and other halogen substituted diphenyl ether solvents; 4-methoxydiphenyl ether, bis(4-methoxyphenyl)ether, bis(3-methoxyphenyl)ether, 4-methyl-4'-methoxydiphenyl ether and other alkoxy substituted diphenyl ether solvents; and dibenzofuran, xanthene and other cyclic diphenyl ether solvents. These solvents can be used singly or as a mixture. The solvent of the invention preferably has a higher boiling point, more preferably has a boiling point higher than 180 °C. Dehydration reaction can efficiently progress without accompanying unfavorable side reactions by carrying out the reaction at decreased temperature under reduced pressure. As described below in the preparation process of the invention the reaction is preferably carried out while removing water which is formed in the reaction. Accordingly preferred solvents can separate water with ease by parting means such as separation and distillation. Particularly in order to obtain a high molecular weight copolymer, ether solvents, alkylaryl ether solvents and diphenyl ether solvents are more preferred, and alkylaryl ether solvents and diphenyl ether solvents are most preferred. The amount of these solvents is preferably in the range of 10 to 80 % which is converted to polymer concentration obtained. No restriction is imposed upon the solvent on whether or not form azeotrope with or separate from water. The catalysts which can be used in the invention are metals of the groups II, III, IV and V in the periodic Table and oxides or salts thereof. Exemplary catalysts include zinc powder, tin powder aluminum, magnesium and other metals; tin oxide, antimony oxide, zinc oxide, aluminum oxide, magnesium oxide, titanium oxide and other metal oxides; stannous chloride, stannic chloride, stannous bromide, stannic bromide, antimony fluoride, zinc chloride, magnesium chloride, aluminum chloride and other metal halogenides; tin sulfate, zinc sulfate, aluminum sulfate and other metal sulfates; magnesium carbonate, zinc carbonate and other metal carbonates; tin acetate, tin octoate, tin lactate, zinc acetate, aluminium acetate and other metal organic carboxylates; tin trifluoromethanesulfonate, zinc trifluoromethanesulfonate, magnesium trifluoromethanesulfonate, tin: methansulfonate, tin p-toluenesulfonate and other metal organic sulfonates; dibutyltin oxide and other organic metal oxides of the above metals; titanium isopropoxide and other metal alkoxide of the above metals; diethyl zinc and other alkyl metal of the above metal. These catalysts can be used singly or as a mixture. The amount in use of these catalysts is in the range of preferably 0.0001 to 5 % by weight, more preferably 0.001 to 1 % by weight in view of economy for the weight of the polymer to be obtained by using the catalyst. The copolymer of the invention can be prepared by reacting two or more kinds of aliphatic polyester homopolymer in the presence of a catalyst in a reaction mixture containing an organic solvent. In order to obtain high molecular weight copolymer, it is required to protect the polymer from hydrolysis by water which is formed in the reaction and is dissolved in the organic solvent of the reaction system. Water content in the reaction mixture is preferably 50 ppm or less, more preferably 20 ppm or less, most preferably 5 ppm or less. Accordingly, the reaction is preferably carried out while removing at least a portion of the organic solvent and charging an organic solvent which has water less than the water content of the removed organic solvent to the reaction system as an additional solvent. Alternatively, a portion of the solvent can be taken out of the reaction system, dehydrated by drying agent treatment or distillation, and successively returned again into the reaction system. Other embodiments include a process for previously charging the solvent in excess and conducting dehydration by merely distilling the solvent and a process for drying the reaction solvent by use of another solvent. Exemplary drying agents which can be used in order to obtain a copolymer having a high weight average molecular weight in the invention include molecular sieve 3A, molecular sieve 4A, molecular sieve 5A, molecular sieve 13X and other molecular sieves, alumina; ion exchange resins; silica gel, calcium chloride, calcium sulfate, diphosphorus pentoxide, concentrated sulfuric acid, magnesium perchlorate, barium oxide, calcium oxide, potassium hydroxide, sodium hydroxide; calcium hydride, sodium hydride, lithium aluminum hydride and other metal hydrides; and sodium and other alkali metals. These drying agents can be used singly or as a mixture. In these drying agents, molecular sieves and ion exchange resins (particularly cation exchange resin) are preferred in view of handling and reactivation with ease. The reaction temperature in the invention is determined in consideration of the forming velocity of the copolymer and the heat decomposition velocity of the formed copolymer and is in the range of preferably 90 to 200°C, more preferably 110 to 180 °C. The reaction is usually carried out at the reflux temperature of the used solvent. When a high boiling point solvent is used in order to carry out the reaction in a preferred range of temperature, the reaction can be carried out under reduced pressure. Reduction of boiling point due to formation of an azeotropic mixture between the solvent and water leads to no problem so long as the reaction is carried out at the prescribed temperature. Preparation of the copolymer in the invention is preferably carried out under vacuum or in an atmosphere of inert gas such as nitrogen and argon so as to prevent penetration of moisture from outside of the reaction system while removing the moisture generated in the system. The reaction can also be carried out while ventilating or bubbling the inert gas. The weight average molecular weight of the copolymer in the invention can be varied by changing the reaction conditions such as the molecular weight of the raw material homopolymer, kind of the solvent, kind and amount of the catalyst, reaction temperature, reaction time and treatment procedure of distilled solvent. When the copolymer is used in the form of a film, filament and other processed items, the weight average molecular weight is in the range of preferably 50,000 to 400,000, more preferably 100,000 to 400,000. The reaction for preparing the copolymer of the invention can be carried out with a continuous operation or a batch operation. Dehydration and charge of the solvent can also be conducted continuously or batchwise. After finishing the reaction, any known method can be used for the treatment of recovering the desired copolymer from the reaction mixture. Exemplary recovering method of a formed copolymer includes an operating procedure for adding isopropyl alcohol to the reaction mixture and filtering and drying precipitated crystals. The copolymer thus obtained in the invention is excellent in strength and elongation and simultaneously has a high transparency which cannot be provided by a random copolymer of aliphatic polyester or a mere blend consisting of two kinds of aliphatic polyester homopolymer. Further, the 13 C-NMR spectrum of the copolymer in the invention does not exhibit a peak caused by ester exchange. As a result, it is assumed that the copolymer of the invention has a highly blocked structure and that a portionally formed copolymer by the preparation process of the invention acts as a compatibilizer, accelerates the compatibilization of two kinds of aliphatic polyester homopolymer and provides transparency. The present invention can provide a biodegradable copolymer having properties which cannot be satisfied by one kind of aliphatic polyester homopolymer. The invention can also provide molded articles and formed items which utilize the excellent properties of the biodegradable copolymer of the invention. For example, according to the present invention, the biodegradable copolymer prepared from polylactic acid and polycaprolactone or polylactic acid and polybutylene succinate can provide a film having a very large elongation which cannot be obtained by a polylactic acid film and an extremely high transparency which cannot be obtained by a polycaprolactone film or a polybutylene succinate film. Further, heat treatment and/or stretching of the film prepared from the biodegradable copolymer of the invention can provide, in addition to transparency and flexibility, markedly high heat resistance which cannot be obtained by a heat-treated film of polylactic acid, polycaprolactone or polybutylene succinate film. The biodegradable copolymer of the invention is a suited material for processing such as injection molding, extrusion forming, calendering, blow molding, balloon forming, blow forming and vacuum forming. The biodegradable copolymer of the invention can be favorably utilized for processed articles such as a film, breathable film, sheet, textile, monofilament, multifilament, yarn, nonwoven fabric, flat yarn, staple, crimped fiber, parallel fiber, ribbed tape, split yarn, conjugate fiber, laminate, blow bottle, sheet, stretched sheet, foam and net. In the processing, additives such as lubricant, colorant, other polymer, demolding agent, filler and reinforcement can be used, when needed. The biodegradable copolymer of the invention has an excellent biodegradability and can completely decompose in a living body or soil, and thus is very useful as a safety high polymer for the living body and natural environment. Consequently, the biodegradable copolymer of the invention is greatly expected for uses such as a surgical suture, shopping bag, garbage bag, agricultural film, cosmetic container, detergent container, bleaching agent container, fishing line, fishing net, rope, tying material, suture, sanitary cover, stock material, low-temperature box and cushioning material. Particularly, the copolymer has high performance without addition of plasticizer and is very suitable for use in food packaging materials and medical devices. Evaluation methods used in those examples are as follows. Weight average molecular weight : Weight average molecular weight (Mw) of aliphatic polyester homopolymers and copolymers were measured by gel permeation chromatography at a column temperature of 40 °C in a chloroform solvent by comparing with a polystyrene standard sample. Water content in a solvent : Measured with a Karl Fischer's moisture meter MKC-210 (manufactured by Kyoto Densi Kogyo Co.) Differential thermal analysis : Analyzed with a scanning calorimeter DSC-3100 (Manufactured by Mac. Science Co.) in a temperature range of -20 to 230°C. Tensile strength: Tensile strength of a film specimen was measured in accordance with JIS K-6732. Elongation : Elongation of a film specimen was measured in accordance with JIS K-6732. Transparency : Transparency was shown by Haze. Haze was measured with a Haze meter TC-HIII (manufactured by Tokyo Denshoku Co.) in accordance with JIS K-6714 Heat Resistance : A film having dimensions of 3 cm × 1 cm was hung down with a dead weight of 20 g and heated at 120 °C for 10 minutes. Elongation after heating was measured. A film having a high heat resistance showed almost no elongation. A film having a low heat resistance was lengthened and deformed by heating. Example 1 (1) Reaction To a reaction vessel, 63.9 g (0.90 mole) of poly-L-lactic acid having a weight average molecular weight of 148,000, 17.2 g (0.10 mole) of polybutylene succinate having a weight average molecular weight of 141,000, 0.41 g tin powder and 324.7 g of diphenyl ether having water content of 10 ppm or less were charged. A tube was packed with 28 g of molecular sieve 3A and 69.6 g of diphenyl ether having water content of 10 ppm or less and mounted on the reaction vessel so as to return the solvent which was distilled by reflux to the reaction system after passing through the molecular sieve. The reaction was carried out at 150°C with stirring for 20 hours under reduced pressure of '5332,89 Pa (40 mmHg) while protecting the reaction system from contamination of water. The solvent after passing through the molecular sieve had water content of 2 ppm. To the reaction mixture, 800 ml of 0.7 % hydrochloric acid/isopropyl alcohol solution was added, stirred for an hour and filtered under suction. Such procedure was carried out twice to remove tin powder. Filter cake was stirred in 600 ml of isopropyl alcohol and filtered under suction. Such procedure was repeated until the filtrate becomes neutral. Successively the filter cake was washed with hexane and air dried at 60°C to obtain 62.9 g (78 % yield) of the copolymer having a weight average molecular weight of 135,000. The copolymer had a glass transition temperature of 21.9°C and two melting points of 113.1°C and 156.3°C by differential thermal analysis. A 13 C-NMR analysis of the copolymer obtained was carried out by using deuteriochloroform as a solvent. As a result, the copolymer exhibited a signal assigned to the carbonyl group of polylactic acid at around 169.68 ppm and a signal assigned to the carbonyl group of polybutylene succinate at around 172.33 ppm, and a new signal caused by ester exchange was not observed. However, as described below, the copolymer was assumed to have a considerably high block structure because the film prepared from the copolymer was transparent. (2) Preparation of a film The copolymer which was obtained by the reaction and had a weight average molecular weight of 135,000 was pressed at 180 °C to prepare a film. Properties of the film thus prepared was illustrated below. Transparency and heat resistance were measured after heat treatment at 120°C. Thickness 98 - 108µm Tensile strength 340 kg/cm 2 (yield) 260 kg/cm 2 (break) Elongation 174 % Transparency (Haze) 6.0 % Heat resistance (120°C) < 5 % The film having a high mole fraction of polylactic acid was excellent in large elongation, high transparency and high heat resistance as compared with the polylactic acid film prepared in Reference Example 1 below. Example 2 (1) Reaction The reaction and post treatment were carried out by the same procedures as described in Example 1 (1) except that 57.6 g (0.80 mole) of poly-L-lactic acid having a weight average molecular weight of 137,000, 34.4 g (0.20 mole) of polybutylene succinate having a weight average molecular weight of 141,000 and 0.3 g of stannous oxide as a catalyst. The copolymer thus obtained was 78.7 g (86 % yield) and had a weight average molecular weight of 134,000. The copolymer had two glass transition temperatures of 3.2 °C and 45.3°C, and two melting points of 106.0°C and 155.3°C, respectively, by differential thermal analysis. (2) Preparation of a film The copolymer which was obtained by the reaction and had a weight average molecular weight of 134,000 was pressed at 180°C to prepare a film by the same procedures as carried out in Example 1 (2). Properties of the film thus prepared was illustrated below. Transparency and heat resistance were measured after heat treatment at 120°C. Thickness 111 - 113µm Tensile strength 270 kg/cm 2 (yield) 280 kg/cm 2 (break) Elongation 350 % Transparency (Haze) 3.5 % Heat resistance (120°C) < 5 % The film having a high mole fraction of polylactic acid was excellent in large elongation, high transparency and high heat resistance similarly to the film prepared in Example 1 (2) which had a high mole fraction of polylactic acid. Example 3 (1) Reaction The reaction and post treatment were carried out by the same procedures as described in Example 1 (1) except that 25.2 g (0.35 mole) of poly-L-lactic acid having a weight average molecular weight of 148,000, 28.5 g (0.17 mole) of polybutylene succinate having a weight average molecular weight of 141,000 and 0.27 g of tin powder as a catalyst. The copolymer thus obtained was 42.7 g (80 % yield) and had a weight average molecular weight of 132,000. The copolymer had no glass transition temperature, and two melting points of 109.5°C and 147.4°C by differential thermal analysis. (2) Preparation of a film The copolymer which was obtained by the reaction and had a weight average molecular weight of 132,000 was pressed at 180°C to prepare a film by the same procedures as carried out in Example 1.(2). Properties of the film thus prepared was illustrated below. Transparency and heat resistance were measured after heat treatment at 120 °C. Thickness 111~113 µm Tensile strength 67 kg/cm 2 (yield) 270 kg/cm 2 (break) Elongation 430 % Transparency (Haze) 8.0 % Heat resistance (120°C) 100 % < The film having a relatively high mole fraction of polybutylene succinate was similar in large elongation and high transparency to and different in poor heat resistance from the film of Example 1.(2) having a low mole fraction of polybutylene succinate. Example 4 (1) Reaction The reaction and post treatment were carried out by the same procedures as described in Example 1 (1) except that 13.0 g (0.18 mole) of poly-L-lactic acid having a weight average molecular weight of 137,000, 72.3 g (0.42 mole) of polybutylene succinate having a weight average molecular weight of 141,000 and 0.43 g of stannous oxide as a catalyst. The copolymer thus obtained was 81.0 g (95 % yield) and had a weight average molecular weight of 160,000. The copolymer had a glass transition temperature of 28.9°C , and a melting point of 111.9°C by differential thermal analysis. (2) Preparation of a film The copolymer which was obtained by the reaction and had a weight average molecular weight of 160,000 was pressed at 170°C to prepare a film by the same procedures as carried out in Example 1.(2). Properties of the film thus prepared was illustrated below. Transparency and heat resistance were measured after heat treatment at 120°C. Thickness 88 - 97µ m Tensile strength 270 kg/cm 2 (yield) 380 kg/cm 2 (break) Elongation 440 % Transparency (Haze) 26.0 % Heat resistance (120°C) 100 % < The film having a high mole fraction of polybutylene succinate was similar in large elongation to and different in poor transparency and poor heat resistance from the film of Example 1.(2) having a high mole fraction of polylactic acid. Example 5 (1) Reaction To a reaction vessel, 64.86 g (0.90 mole) of poly-L-lactic acid having a weight average molecular weight of 69,000, 11.42 g (0.10 mole) of polycaprolactone having a weight average molecular weight of 62,000, 0.42 g of tin powder and 333.9 g of diphenyl ether having water content of 10 ppm or less were charged. A tube was packed with 28 g of molecular sieve 3A and 69.6 g of diphenyl ether having water content of 10 ppm or less and mounted on the reaction vessel so as to return the solvent which was distilled by reflux to the reaction system after passing through the molecular sieve. The reaction was carried out at 150 °C with stirring for 28 hours under reduced pressure of 5332,89 Pa (40 mmHg) while protecting the reaction system from contamination of water. The solvent after passing through the molecular sieve had a moisture content of 2 ppm. To the reaction mixture, 800 ml of a 0.7 % hydrochloric acid/isopropyl alcohol solution was added, stirred for an hour and filtered under suction. Such procedure was carried out twice to remove tin powder. Filter cake was stirred in 600 ml of isopropyl alcohol and filtered under suction. Such procedure was repeated until the filtrate becomes neutral. Successively the filter cake was washed with hexane and air dried at 60 °C to obtain 39.52 g (52 % yield) of the copolymer having an weight average molecular weight of 127,000. The copolymer had two glass transition temperature of 23.1 °C and 35.3°C and three melting points of 51.0°C, 61.1°C, and 155.1°C by differential thermal analysis. (2) Preparation of a film The copolymer which was obtained by the reaction and had a weight average molecular weight of 127,000 was pressed at 180°C to prepare a film. Properties of the film thus prepared was illustrated below. Transparency and heat resistance were measured after heat treatment at 120°C. Thickness 197 - 218µ m Tensile strength 380 kg/cm 2 (yield) 220 kg/cm 2 (break) Elongation 290 % Transparency (Haze) 6.0 % Heat resistance (120°C) < 5 % The film having a high mole fraction of polylactic acid was excellent in a large elongation, high transparency and high heat resistance as compared with the polylactic acid film prepared in Reference Example 1. Example 6 (1) Reaction The same procedures as described in Example 5 (1) were carried out except that 57.6 g (0.80 mol) of poly-L-lactic acid having a weight average molecular weight of 69,000, 22.8 g (0.20 mole) of polycaprolactone having a weight average molecular weight of 62,000 and 0.29 g of tin powder were used, that diphenyl ether was replaced by 68.4 g of o-dichlorobenzene that the reaction was carried out at 130 °C for 23 hours under reduced pressure of '26664,47 Pa (200 mmHg), and that post treatment was carried out by using 320 g of a 0.7 % hydrochloric acid/methyl tert-butyl ether solution in place of a 0.7 % hydrochloric acid/ispropyl alcohol solution. The copolymer thus obtained was 61.2 g (76 % yield) and had a weight average molecular weight of 126,000. The copolymer had two glass transition temperatures of -45.8°C and 43.9°C, and three melting points of 51.0°C, 61.1°C, 159.8°C by differential thermal analysis. (2) Preparation of a film The copolymer which was obtained by the reaction and had an weight average molecular weight of 126,000 was pressed at 180°C to prepare a film by the same procedures as carried out in Example 5 (2). Properties of the film thus prepared was illustrated below. Transparency and heat resistance were measured after heat treatment at 120°C. Thickness 150 - 169µ m Tensile strength 430 kg/cm 2 (yield) 320 kg/cm 2 (break) Elongation 250 % Transparency (Haze) 0.4 % Heat resistance (120°C ) < 5 % The film having a high mole fraction of polylactic acid was excellent in a large elongation, high transparency and high heat resistance similarly to the film of Example 5 (2) having a high mole fraction of polylactic acid. Example 7 (1) Reaction Reaction, post treatment and recovery were carried out by the same procedures as described in Example 5 (1) except that 36.0 g (0.50 mole) of poly-L-lactic acid having a weight average molecular weight of 69,000, 57.0 g (0.50 mole) of polycaprolactone having a weight average molecular weight of 62,000, 0.18 g of tin powder as a catalyst, and 279.0 g of o-dichlorobenzene were used, and that the reaction was carried out at 130°C for 20 hours under reduced pressure of 26664,47 Pa (200 mmHg). The copolymer thus obtained was 45.6 g (49 % yield) and had an weight average molecular weight of 80,000. The copolymer had two glass transition temperatures of -63.9°C and -32.1°C and had two melting points of 55.1°C and 160.5°C by differential thermal analysis. (2) Preparation of a film The copolymer which was obtained by the reaction and had a weight average molecular weight of 80,000 was pressed at 180 °C to prepare a film. Properties of the film thus prepared was illustrated below. Transparency and heat resistance were measured after heat treatment at 120°C. Thickness 83 - 102µm Tensile strength 230 kg/cm 2 (yield) 210 kg/cm 2 (break) Elongation 350 % Transparency (Haze) 8.0 % Heat resistance (120°C) 100 % < The film having a high mole fraction of polycaprolactone was similar in large elongation and high transparency to and different in poor heat resistance from the film of Example 5 (2) having a low mole fraction of polycaprolactone. Comparative Example 1 (1) Reaction Reaction and post treatment were carried out by the same procedures as described in Example 1 (1) except that 28.8 g (0.40 mole) of poly-L-lactic acid having a weight average molecular weight of 119,000 and 17.2 g (0.10 mole) of polybutylene succinate having a weight average molecular weight of 141,000 were used in the absence of a catalyst. Copolymer thus obtained was 44.0 g (96 % yield) and had an weight average molecular weight of 147,000. The copolymer had a glass transition temperature of 53.6°C and two melting points of 111.5°C and 162.7°C by differential thermal analysis. (2) Preparation of a film The copolymer which was obtained by the reaction and had a weight average molecular weight of 147,000 was pressed at 180°C to prepare a film by the same procedures as carried out in Example 1 (2). Properties of the film thus prepared was illustrated below. Transparency and heat resistance were measured after heat treatment at 120°C. Thickness 111 - 113µm Tensile strength 360 kg/cm 2 (yield) 300 kg/cm 2 (break) Elongation 37 % Transparency (Haze) 78.0 % Heat resistance (120°C) < 5 % The film prepared from the copolymer obtained by reacting in the absence of a catalyst was excellent in high heat resistance and inferior in small elongation and low transparency as compared with the film prepared from the copolymer obtained by reacting in the presence of a catalyst. Comparative Example 2 (1) Reaction In a reaction vessel, 36.0 g (0.36 mol) of 90 % L-lactic acid and 5.3 g (0.04 mol) of 6-hydroxycaproic acid were heated at 150°C for 3 hours with stirring under reduced pressure of 6666,12 Pa (50 mmHg) while distilling water out of the reaction system. The oligomer obtained was 30.8 g. After adding 0.158 g of tin powder to the oligomer, the reaction was continued for further 2 hours at 150°C under reduced pressure of 3999,67 Pa (30 mmHg). A Dean Stark trap was mounted on the reaction vessel, 0.743 g of tin powder and 102.5 g diphenyl ether were added, and an azeotropic dehydration reaction was carried out at 150°C for an hour under reduced pressure of 4666,28 Pa (35 mmHg) while removing water. Thereafter, the Dean Stark trap was dismantled and a tube packed with 25 g of molecular sieve 3A and diphenyl ether having water content of 10 ppm or less was equipped so as to return again the distilled solvent to the reaction system after passing through the molecular sieve layer. Reaction was carried out at 130°C for 35 hours with stirring under reduced pressure of 1599,87 Pa (12 mmHg) while protecting the reaction system from contamination of water. The solvent after passing through the molecular sieve layer had water content of 2 ppm or less. To the reaction mixture, 220 g of chloroform was added and filtered under suction to remove tin powder. The chloroform solution was washed with 100 ml of 1N aqueous hydrochloric acid solution, successively washed twice with water and poured into 750 ml of methanol. Precipitated solid was filtered under suction, successively washed with methanol, then washed with hexane and dried at 30°C under reduced pressure of 666,61 Pa (5 mmHg). The copolymer thus obtained was 25.0 g (80 % yield) and had a weight average molecular weight of 115,000, and a glass transition temperature of 24.0°C by differential thermal analysis. (2) Preparation of a film The copolymer which was obtained by the reaction and had a weight average molecular weight of 115,000 was dissolved in chloroform and cast to obtain a film having dimensions of 150 mm × 150 mm. Properties of the film thus prepared was illustrated below. Transparency and heat resistance were measured after heat treatment at 120°C. Thickness 68 - 72µ m Tensile strength 84 kg/cm 2 (yield) 340 kg/cm 2 (break) Elongation 480 % Transparency (Haze) 78.0 % Heat resistance (120°C) 100 % < The film prepared from the random copolymer had large elongation, very poor heat resistance and poor transparency as compared with the film of Example 5 (2) which was prepared from the reaction product of homopolymers. Reference Example 1 (Polylactic acid) A film was prepared from polylactic acid having a weight average molecular weight of 143,000 by the same procedures as carried out in Example 1 (2). Properties of the film thus prepared was illustrated below. Transparency and heat resistance were measured after heat treatment at 120°C. Thickness 88 - 97 µm Tensile strength 660 kg/cm 2 (break) Elongation 7 % Transparency (Haze) 33.3 % Heat resistance (120°C) 100 % < The polylactic acid film obtained was inferior in elongation, transparency and heat resistance to the film prepared in Example 1 (2) from the copolymer having a high mole fraction of polylactic acid. Reference Example 2 (Polybutylene succinate) A film was prepared from polybutylene succinate having a weight average molecular weight of 134,000 by the same procedures as carried out in Example 1 (2). Properties of the film thus prepared was illustrated below. Transparency and heat resistance were measured after heat treatment at 120°C. Thickness 88 - 97 µm Tensile strength 340 kg/cm 2 (yield) 330 kg/cm 2 (break) Elongation 330 % Transparency (Haze) 33.3 % Heat resistance (120°C) 100 % < The polybutylene succinate film obtained was similar in large elongation to and different in poor transparency and inferior heat resistance from the film of Example 1 (2) or Example 2 (2) which was prepared from the copolymer having high mole fraction of polylactic acid. Reference Example 3 (Polycaprolactone) A film was prepared from polycaprolactone having a weight average molecular weight of 111,000 by the same procedures as carried out in Example 5 (2). Properties of the film thus prepared was illustrated below. Transparency and heat resistance were measured after heat treatment at 120°C. Thickness 88 - 97 µm Tensile strength 150 kg/cm 2 (yield) 130 kg/cm 2 (break) Elongation: 370 % Transparency (Haze) 33.0 % Heat resistance (120°C) 100 % < The polycaprolactone film obtained was similar in large elongation to and different in poor transparency and inferior in heat resistance from the film of Example 7 (2) which was prepared from the copolymer having a high mole fraction of polycaprolactone. Films prepared in Examples, Comparative Examples and Reference Examples were buried in compost and a biodegradation test in soil was carried out. After 30 days, all specimens were deteriorated and their strength could not be measured.

Claims: A process for preparing a biodegradable copolymer of aliphatic polyesters which comprises reacting two or more kinds of aliphatic polyester homopolymers in the presence of a catalyst in a reaction mixture containing an organic solvent, wherein the aliphatic polyester homopolymers each have a weight average molecular weight of 10,000 or more and wherein the water content in the reaction mixture is controlled to 50 ppm or less by removing a portion or most of the organic solvent from the reaction mixture and charging to the reaction system an additional organic solvent having a water content less than or equal to the water content of the removed organic solvent. The process for preparing a biodegradable copolymer of aliphatic polyesters according to claim 1 wherein the organic solvent removed from the reaction mixture is dehydrated by contacting with a drying agent and is returned to the reaction system as an additional solvent. The process for preparing a biodegradable copolymer of aliphatic polyesters according to claim 2 wherein the drying agent is a molecular sieve, an ion exchange resin, diphosphorus pentoxide or a metal hydride. The process for preparing a biodegradable copolymer of aliphatic polyesters according to any of the claims 1 to 3 wherein the organic solvent is one or more of organic solvents selected from the group consisting of a hydrocarbon solvent, halogenated solvent, ketone solvent, ether solvent, thio ether solvent and ester solvent. The process for preparing a biodegradable copolymer of aliphatic polyesters according to claim 4 wherein the organic solvent is an ether solvent. The process for preparing a biodegradable copolymer of aliphatic polyesters according to any of the claims 1 to 5 wherein the two or more kinds of the aliphatic polyester homopolymers are selected from the group consisting of aliphatic polyesters prepared from hydroxycarboxylic acids and aliphatic polyesters prepared from diols and dicarboxylic acids. The process for preparing a biodegradable copolymer of aliphatic polyesters according to claim 6 wherein the two or more kinds of the aliphatic polyester homopolymer are polylactic acid and polybutylene succinate or polycaprolactone. A biodegradable copolymer of aliphatic polyesters obtainable by the process according to any of the claims 1 to 7.

Inventors: AJIOKA MASANOBU, HIGUCHI CHOJIRO, KITADA IKUMI, YAMAGUCHI AKIHIRO, AJIOKA, MASANOBU, HIGUCHI, CHOJIRO, KITADA, IKUMI, YAMAGUCHI, AKIHIRO
Applicants: MITSUI CHEMICALS INC, MITSUI CHEMICALS, INC.
Application year: 1995
Main classification: C08G81
IPC codes: C08G63