METHOD FOR PRODUCING A SUSPENSION IN WATER OF A CELLULOSE ETHER, AND DRY MIXTURE SUITABLE FOR USE IN THE PRODUCTION OF THE SUSPENSION

Abstract: In a method for producing a suspension of a nonionic cellulose ether that has no turbidity point, the water forming part of the suspension is mixed with a dry mixture containing a cellulose ether, which is cross-linked with glyoxal, and an electrolyte salt. This electrolyte salt consists of a salt or a mixture of salts which, in water and at the concentration employed, results in a pH value below 8.0. Preferably, the cellulose ether is a hydroxyethylcellulose.

Description: METHOD FOR PRODUCING A SUSPENSION IN WATER OF A CELLULOSE ETHER, AND DRY MIXTURE SUITABLE FOR USE IN THE PRODUCTION OF THE SUSPENSION The present invention relates to a method for producing a suspension of a nonionic cellulose ether that has no turbidity point by mixing the water forming part of the suspension with a dry mixture that contains a cellulose ether, which is cross- linked with glyoxal, and an electrolyte salt. Water-soluble, nonionic cellulose ethers are used in many industrial processes as well as in various consumer goods. The fields of application include mining, paper production, water treatment, textile treatment, colour compositions, detergents and cosmetic products. However, it is difficult to dissolve pulverulent, water-soluble and nonionic cellulose ethers, owing to the powder having a tendency towards gelling and agglomeration. One way of solving this problem is to suspend the water-soluble cellulose ethers in water containing a considerable amount of electrolyte and, optionally, a dispersant and/or a stabiliser. When water is mixed in, the electrolyte content is reduced and the cellulose ethers are dissolved without any gelling or lump formation. The cellulose ethers suspended in water have proved to be well suited for use as intermediary products in industrial processes, as well as in the production of consumer goods. Thus, European Patent Application 413 274 teaches an aqueous suspension of hydroxyethylcellulose, i.e. a cellulose ether having no turbidity point in water. This suspension contains a water-soluble hydroxyethylcellulose in an amount of 8-28% by weight and further contains 20-35% by weight of potassium carbonate, based on the weight of potassium carbonate and water, 0.2-8% by weight of a detergent having a HLB value of 6-9, as well as 0.08-0.6% by weight of a water-soluble or water- swellable thickener, both contents being based on the weight of the total suspension. European Patent Application 482 533 further discloses th suspension of a nonionic cellulose ether, such as hydrophobe modified hydroxyethylcellulose, hydrophobe-modified ethyl hydroxyethylcellulose, methylcellulose and hydroxyethyl cellulose, in an aqueous sodium formate solution. It appear from the Examples that the amount of sodium formate should be a least 30% by weight, if one is to obtain a suspension. Further, European Patent Application 3 582 discloses method of reducing the electrolyte content of the suspension o water-soluble nonionic cellulose ethers. According to th European application, this is achieved by adding not only a electrolyte salt but also an aluminium oxide compound. Owing t the addition of aluminium oxide, the electrolyte content may according to the patent application, be reduced from about 25 to 10%. The presence of aluminium oxide in solid or colloida state may, however, have adverse effects when the suspension i used at a later stage. One object of the present invention is to provide method for suspending a cellulose ether, which has no turbidit point in water, together with an electrolyte salt and optionall other ingredients, such as a stabiliser and/or a dispersant directly in the aqueous phase without there being any gelling The invention thus provides a simple and reliable method fo producing the suspension. According to the invention, it has now been found tha this object can be attained by producing an aqueous suspensio of a water-soluble nonionic cellulose ether, which has n turbidity point in water. This is achieved by preparing a dr mixture which contains the nonionic cellulose ether cross-linke with glyoxal, as well as an electrolyte salt consisting of salt or a mixture of salts which, in water and at th concentration used in the suspension, results in a pH valu below 8.0, preferably below 7.5, and mixing the water formin part of the suspension with the dry mixture. Conveniently, the cellulose ether constitutes 8-25% by weight of the suspension, whereas the electrolyte salt is present in an amount of 20-45% by weight of the suspension, preferably 25-40%. Apart from the cellulose ether and the electrolyte salt, the suspension suitably contains a stabiliser, which consists of a viscosity- enhancing polymer soluble in the electrolyte solution and present in an amount of 0.01-3% by weight of the suspension. Conveniently, the suspension also contains a dispersant, such as a surfactant, in an amount of 0.05-4% by weight. As a rule, the dispersant has a stabilising and viscosity-enhancing effect. In a preferred mode of implementation of the inventive method, the suspension is produced by mixing the water with a dry mixture which, apart from the cellulose ether and the electrolyte salt, contains all the dry ingredients of the suspension. In the event that one of the ingredients of the suspension is liquid, this ingredient is suitably applied to a carrier and incorporated in the dry mixture in this form. If so desired, one or more of the ingredients, excepting the cellulose ether and the electrolyte salt, may also be added to the water after and/or before the dry mixture containing the cellulose ether and the electrolyte salt has been mixed with the water. Thorough tests have shown that the inventive method cannot be implemented unless the cellulose ether is cross-linked, since minor amounts of the cellulose ether would otherwise dissolve and form a gel. A number of important advantages are gained by preparing a dry mixture of all the ingredients, excepting water, in a first stage, since a suspension of the cellulose ether can then be prepared by adding water to a single dry composition. Such a dry mixture suitably contains 20-45% by weight of the cellulose ether, preferably 30-40% by weight, and 50-80% by weight of the electrolyte salt, preferably 55-70% by weight. In addition, the dry composition may contain 0.02-6% by weight of a stabiliser and 0.1-8% by weight of a dispersant. As indicated in the foregoing, the electrolyte sal consists of a salt or a mixture of salts which, at th contemplated electrolyte content of the aqueous suspension, results in a pH value below 8.0, preferably below 7.5. Th reason for this is that the cross-linked cellulose ether i partly hydrolysed at high pH values, thus forming a gel. Examples of suitable salts are sodium formate, NaCl, Na 2 S0 4 , K 2 S0 4 , NaH 2 P0 4 , NaHC0 3 , NaN0 3 and MgS0 4 . Sodium formate i especially preferred owing to its high solubility, as are alkal salts with bivalent anions, such as Na 2 S0 4 and K 2 S0 4 . A preferre electrolyte salt contains at least 50% by weight of sodiu formate, one or more acid salts, such as a NaH 2 P0 4 , in such a amount that the suspension preferably obtains a pH value of 5.5 7.0, and 0-25% by weight of a bivalent alkali salt. By selectin an electrolyte salt which at least partly is made up of salt with bivalent anions, one is able to slightly reduce the sal content of the suspension. In addition, the amount of sal required depends on the degree of cross-linkage of the cellulos ether and on the temperature of the suspension. Thus, the sal requirement diminishes with an increasing temperature and a increasing degree of cross-linkage. Conveniently, the nonionic cellulose ether is hydroxyethylcellulose that is cross-linked with glyoxal. Apar from the hydroxyethyl substituent, the cellulose ether ma contain other substituents, such as hydroxypropyl and methy groups, provided that the content thereof is so restricted tha the cellulose ethers do not obtain any turbidity point in water, as measured in a 1% aqueous solution. The molecular substitutio of hydroxyethyl suitably is 1.0-3.0, whereas the molecula substitution of hydroxypropyl and methyl suitably is respec tively 0.0-0.4 and 0.0-0.8. The cross-linkage with glyoxal i carried out in a manner known per se. The cellulose ether has suitable degree of cross-linkage when a 1% aqueous solution o the cross-linked cellulose ether at a temperature of 20°C and pH value of 7.0 results, after 5 min of agitation, in a viscosity increase of less than 5%, preferably less than 1%, of the viscosity obtained when the cross-linked cellulose ether is completely dissolved. Cellulose ethers having a suitable degree of cross-linkage are obtained when 0.05-2 parts by weight of glyoxal is caused to react with 100 parts by weight of dry cellulose ether. In order to enhance the stability of the suspension, it has been found suitable to add polymeric stabilisers that are soluble in the electrolyte solution, such as xanthan gum and CMC. Examples of suitable dispersants are ionic low-molecular polymers having a molecular weight of 1000-15000, such as low- molecular polyacrylic acids; nonionic surfactants, such as ethyleneoxy adducts of alcohols having 10-18 carbon atoms and alkyl phenols having a total of 14-18 carbon atoms and block polymers of ethylene oxide and propylene oxide; anionic surfactants, such as linear alkylbenzene sulphonate, laurylether sulphate and phosphate esters of fatty alcohol ethoxylate; cationic surfactants, such as tertiary or quaternary mono- or di-Cg-iealkylamines; and amphoteric surfactants, such as betaines. Apart from the components indicated above, the com¬ position may contain biocides, foam inhibitors, corrosion inhibitors, pH-adjusting agents, and so forth. The present invention will now be further elucidated with the aid of a few Examples. Example l Three compositions according to the invention were produced. These compositions contained a hydroxyethylcellulose cross-linked with glyoxal and having an MS hydroxyethyi of 2.5. There was further produced a comparative composition, which contained a hydroxyethylcellulose that was not cross-linked. The compositions contained the following ingredients. Table 1 11 The viscosity according to Brookfield in 2% aqueou solution at 25°C = 400 mPa s 2) The viscosity according to Brookfield in 2% aqueou solution at 25°C = 6,500 mPa s 3) The viscosity according to Brookfield in 1% aqueou solution at 25°C = 2,000 mPa s 4) The seune substitution and viscosity as in the case of th cellulose ether in composition 1. Thus, 49 parts by weight of each of the above compo sitions was dispersed in 51 parts by weight of water. Th viscosity and the stability of the aqueous formulations wer determined, and the following results were obtained. Table 2 Composition Viscosity irαPa's 23°C Stability 1 ' 11 Stability: + = stable for less than 6 h, ++ = stable for more than 6 h but less than 10 days, +++ = stable for more than 10 days. It is evident from these results that the comparative composition formed a gel and thus was useless, whereas the compositions according to the invention showed no tendency towards gelling during the 10 days of the test period. Example 2 The following compositions according to the invention were produced by mixing the ingredients listed below. Then, 49 parts by weight of each of the compositions was suspended in 51 parts by weight of water. Table 3 1) The same cellulose ether as in composition 2. 2) The same cellulose ether as in composition 1. The suspensions obtained after suspending the compo sitions in water were then tested with respect to viscosity an stability. The following results were obtained. Table 4 11 Stability: + = stable for less than 6 h, ++ = stable fo more than 6 h but less than 10 days, +++ = stable fo more than 10 days. It is evident from these results that none of the sus pensions gelled, but that all had a suitable viscosity. A regards the suspension which separated after a period o storage, a homogeneous suspension could again be obtained b slight agitation.

Claims: CLAIMS 1. A method for producing an aqueous suspension of a water- soluble nonionic cellulose ether having no turbidity point in water, characterised by preparing a dry mixture which contains the nonionic cellulose ether cross-linked with glyoxal and an electrolyte salt consisting of a salt or a mixture of salts which, in water and at the concentration used in the suspension, results in a pH value below 8.0, preferably below 7.5; and mixing the water forming part of the suspension with the dry mixture in such an amount that the cellulose ether constitutes 8-25% by weight of the suspension and the electrolyte salt constitutes 20-45% by weight of the suspension. 2. A method as claimed in claim 1, characterised by the cross-linked cellulose ether incorporated in the dry mixture resulting, in a 1% aqueous solution at a temperature of 20°C and a pH value of 7.0, in a viscosity increase which is less than 5%, preferably less than 1%, of the viscosity obtained when the cellulose ether is completely dissolved. 3. A method as claimed in claim 1 or 2 , characterised by preparing the dry mixture from an electrolyte salt which contains at least 50% by weight of sodium formate, one or more acid salts in such an amount that the suspension obtains a pH value of 5.5-7.0, and 0-25% by weight of a bivalent alkali salt; and by the cellulose ether being a hydroxyethylcellulose. 4. A method as claimed in claim 1, 2 or 3, characterised by adding all the components forming part of the aqueous phase to the dry mixture. 5. A method as claimed in claim 4, characterised by adding a dispersant and/or a stabiliser to the dry mixture. 6. A method as claimed in any one of claims 1-3, char¬ acterised by adding a dispersant and/or a stabiliser to the water. 7. A dry mixture suitable for use in the production of a suspension of a water-soluble nonionic cellulose ether, characterised in that it contains 20-45% by weight of a cellulose ether, which is cross-linked with glyoxal and has no turbidity point in water, and 50-80% by weight of an electrolyte salt, which consists of a salt or a mixture of salts which, in water and at the concentration used in the suspension, results in a pH value below 8.0, preferably below 7.5. 8. A dry mixture as claimed in claim 7, characterised in that the cross-linked cellulose ether incorporated in the dry mixture results, in a 1% aqueous solution at a temperature of 20°C and a pH value of 7.0, in a viscosity increase which is less than 5%, preferably less than 1%, of the viscosity obtained when the cellulose ether is completely dissolved. 9. A dry mixture as claimed in claim 7 or 8, characterised in that the electrolyte salt contains at least 50% by weight of sodium formate, one or more acid salts in such an amount that the suspension obtains a pH value of 5.5-7.0, and 0-25% by weight of a bivalent alkali salt, and that the cellulose ether consists of a hydroxyethylcellulose. 10. A dry mixture as claimed in any one of claims 7-9, characterised in that it contains a dispersant and/or a stabiliser.

Inventors: ANDERSSON LARS, BOSTROEM PETER, ANDERSSON, LARS, BOSTROEM, PETER
Applicants: AKZO NOBEL NV, ANDERSSON LARS, BOSTROEM PETER, AKZO NOBEL N.V., ANDERSSON, LARS, BOSTROEM, PETER
Application year: 1995
Main classification: C08L1
IPC codes: C08J3, C08L1