Nonhazardous pumpable refractory insulating composition

Abstract: A granular castable refractory composition is provided which has excellent insulating properties as well as high strength and resistance to oxidation, corrosion or erosion. The refractory insulating composition can be easily transported using a pump, and avoids the potential hazards associated with asbestos and ceramic fibers. The refractory insulating composition is prepared by mixing a low density expanded granular refractory insulating material having a density of 112-801 kg/m 3 (7-50 lb/ft 3 ) with a conventional high density refractory material having a density of at least 2403 kg/m 3 (150 lb/ft 3 ) to form a dry component, and by mixing the dry component with aqueous colloidal silica to provide excellent flow properties for pumping and, ultimately, excellent binding properties.

Description: This invention relates to a pumpable castable refractory insulating composition for use in liners for ladles, heat furnaces, sub-hearths, coating furnaces, nitriding furnaces, annealing furnaces and the like, which is nonhazardous and relatively inexpensive to install. Refractory insulating materials for use in high temperature applications (260-1650°C ie. 500-3000°F) have undergone various stages of development in recent decades. Initially, asbestos was a popular insulating material. Due to health and safely concerns, asbestos was substantially replaced with ceramic fibers and other materials. Ceramic fibers are customarily used today in applications involving the iron and steel industry, and other applications. Ceramic fibers represented an expensive replacement for asbestos because the installation of ceramic fibers is expensive and labor-intensive. Also, ceramic fibers pose their own health and safety hazards in that gases which are evolved inside the furnace or other high temperature structure can sometimes pass through the layer or layers of ceramic fiber insulation. For example, corrosive gases can pass through the insulation and cause damage to the steel shell of the high temperature structure. Where a steel shell is damaged or is not present, toxic gases generated in a furnace or other structure can penetrate the ceramic fibers and affect persons standing nearby. In order to be effective as an insulator, a material should have voids or pockets which contain air or another (e.g. inert) gas having a low thermal conductivity. In order for the same material to be impermeable, it is desirable that the air pockets be substantially closed, walled or separated from each other, so that gaseous materials cannot pass through the insulating material. In order for the same material to be relatively inexpensive, it is desirable that the material lend itself to installation using continuous, automated or semi-automated equipment. Ceramic fibers meet only the first of the three criteria listed above. There is a need in the iron and steel industry, and in other industries, for a refractory insulating material that not only has a low density (i.e. high void volume), but which is impermeable and easy to install. Pumpable refractory materials (i.e. castable refractory materials which can be continuously installed using a concrete pump or similar device) are known in the iron and steel industry from U.S. Patent 5,147,830, issued to Banerjee et al. Until now, however, this highly efficient technology has not been applied to refractory insulating materials due, in large part, to the absence of a suitable refractory insulating material which can flow through a pump. By way of further background, US Patent 4,751,204 discloses a two-part gunning refractory composition comprising a refractory raw material consisting of a coarse/fine grain portion and a fine powder portion, a superfine refractory powder, and one or more of water and colloidal silica. German Patent 2632084 discloses a process for producing lightweight tiles from clay, foamed mineral products such as perlite and colloidal silica. The present invention is a nonhazardous, high temperature-resistant refractory insulating material which solves the foregoing problems associated with ceramic fiber insulation. The insulating material of the invention has a low density (high void volume) but is impenetrable to corrosive or other harmful gases because the voids do not form channels in the ultimate insulating layers. The insulating material of the invention is also pumpable using a standard concrete pump or similar pump and, therefore, is relatively inexpensive to install. Briefly, the refractory insulating material is formed by combining a solid, granular dry component and an initially wet component. The dry component includes a light weight low density expanded granular refractory insulating material having a density of about 112-801 kg/m 3 (7-50 lb/ft 3 ) mixed together with a standard high temperature-resistant castable refractory material having a density of about 2403-3204 kg/m 3 (150-200 lb/ft 3 ) or higher. The initially wet component includes an aqueous colloidal silica binder. When the components are mixed together, the granular refractory insulating material causes the ultimate composition to have a relatively low density of about 640-2082 kg/m 3 (40-130 1b/ft 3 ) and insulating properties previously not available in a refractory casting composition. The standard castable refractory material causes the ultimate insulating composition to have structural integrity, resistance to cracking or explosion during heating and drying, and excellent resistance to oxidation, corrosion and erosion. The aqueous colloidal silica component provides excellent flow characteristics which permit the insulating composition to be pumped to a destination. After the ultimate composition has been installed, set, dried and heated, the colloidal silica serves as an excellent binder which enhances the strength and structural integrity of the ultimate insulating layer. With the foregoing in mind, it is a feature and advantage of the invention to provide a castable refractory insulating composition which combines the excellent strength, temperature resistance, corrosion resistance, etc. of a castable refractory layer with the low density and high porosity of a granular insulating composition. It is also a feature and advantage of the invention to provide a castable refractory insulating composition whose porosity does not result in capillaries or other passages through the ultimate insulating layer and which therefore, blocks the passage of corrosive and other harmful gases from one side to another of an insulating layer prepared therefrom. It is also a feature and advantage of the invention to provide a castable refractory insulating composition which is pumpable and easy to install using a standard concrete or similar pump. The foregoing and other features and advantages of the invention will become further apparent from the following detailed description of the presently preferred embodiments, read in conjunction with the accompanying examples. The detailed description and examples are merely illustrative of the invention rather than limiting, with the scope of the invention being defined by the appended claims and equivalents thereof. In accordance with the invention, a non-hazardous pumpable refractory insulating composition is provided which is substantially free of asbestos and ceramic fibers. The refractory insulating composition includes a dry component and an initially wet (binder) component which later becomes dry after casting of the composition. Depending on the specific application, the wet component may be added at about 20-80 parts per 100 parts by weight of the dry component, preferably about 30-75 parts per 100 parts by weight of the dry component, most preferably about 40-70 parts per 100 parts by weight of the dry component. The dry component and initially wet component are prepared separately and are blended together prior to casting. The dry component includes a low density non-hazardous expanded refractory insulating material having a density between about 112-801 kg/m 3 (7-50 1b/ft 3 ). Examples of suitable materials include, but are not limited to, vermiculite, perlite, verilite TM , haydite TM , insulating brick grog, and combinations thereof. These insulating materials, and other preferred insulating materials, generally include about 30-60% by weight alumina, about 40-60% by weight silica, and about 3-10% of other refractory materials. The other refractory materials may include about 1-3% by weight iron oxide, about 1.3% by weight titania, about 0.5-5% by weight calcia, about 0.5-10% by weight magnesia, and about 0.5-5% by weight of an alkali metal oxide such as sodium oxide or potassium oxide. The alkali metal serves as an expanding agent which causes the insulating material to expand when heated. Alternatively, chemical foaming agents and/or mechanical techniques may be used to facilitate expansion of the insulating material. While many low density insulating materials (vermiculite, perlite, haydite TM , insulating brick grog, etc.) are commercially available in an expanded condition, expanded refractory materials may also be manufactured or enhanced using "burnout" mechanical techniques whereby a combustible material such as sawdust or woodchips is mixed with a refractory material and then heated. The heating causes the combustible material to burn, leaving a porous refractory material behind. Similarly, chemical foamers such as detergents may be entrained with air, mixed with the refractory material, and heated. For high-temperature end uses (involving exposure of the insulating material to maximum temperature of greater than 1371°C (2500°F), it is preferred that the insulating material have a high alumina content of about 50-60% by weight and a correspondingly low silica content of about 40-46% by weight. Insulating brick grog is especially useful for these high temperature applications. For intermediate temperature applications (involving exposure of the insulating material to maximum temperatures between 649-1371°C (1200-2500°F), it is preferred that the insulating material have an intermediate alumina content of about 40-50% by weight and an intermediate silica content of about 46-53% by weight. Perlite and verilite TM are especially useful for these intermediate temperature applications. For lower temperature and use applications (involving exposure of the insulatory material to maximum temperatures below 649°C (1200°F), it is preferred that the insulating material have a low alumina content of about 30-40% by weight and a high silica content of about 53-60% by weight. Vermiculite and haydite TM are especially useful for these lower temperature applications. The low density non-hazardous insulating material has a density generally between 112-801 kg/m 3 (7-50 1b/ft 3 ), preferably between about 160-640 kg/m 3 (10-40 1b/ft 3 ), mast preferably between about 160-560 kg/m 3 (10-35 1b/ft 3 ). The low density non-hazardous insulating material constitutes about 10-80% by weight of the dry component, preferably about 15-65% by weight of the dry component, most preferably about 25-50% by weight of the dry component. The dry component also includes a standard (not expanded) high strength, high temperature-resistant refractory material having a density of about 2403-3204 kg/m 3 (150-200 1b/ft 3 ) or higher. Examples of these standard refractory materials include, but are not limited to, refractory clay (e.g. flint or rock clay), kaolinite, mullite, brown fused alumina, tabular alumina, aluminasilicates (especially those having a high alumina content of 80% or greater), and combinations of the foregoing materials. The standard refractory material provides strength, structural integrity, resistance to cracking or explosion during heating, and resistance to oxidation, corrosion and erosion during use. This standard high-density refractory material constitutes about 20-90% by weight of the dry component, preferably about 35-85% by weight of the dry component, most preferably about 50-75% by weight of the dry component. The dry component may also include minor quantities of additional ingredients which are generally considered to be useful in a refractory casting composition. For example, up to 1% by weight of pulverized magnesia or another setting agent may be included. Fumed silica or microsilica may be present at about 1-10% by weight in order to provide enhanced flowability and oxidation resistance. Between about 2-10% by weight of a graphite material may be included as a nonwetting agent. The ingredients of the dry component should be present in quantities that yield an overall dry component density of about 640-2082 kg/m 3 (40-130 1b/ft 3 ), preferably about 640-1762 kg/m 3 (40-110 1b/ft 3 . The dry component, which exists in a granular or powdered form prior to mixing with the wet component, can be prepared by dry blending (for example, tumble blending) the dry components together. In addition to the dry component, the pumpable refractory insulating composition of the invention also includes an initially wet component which is colloidal silica in water. The wet component preferably contains 8-10% by weight colloidal silica in water, most preferably about 25-50% by weight colloidal silica in water. In order to form a colloidal dispersion in the water, the silica should have an average particle diameter of about 4-100x10 -9 m (4-100 millimicrons), preferably about 6-50x10 -9 m (6-50 millimicrons), most preferably about 8-20x10 -9 m (8-20 millimicrons) Prior to casting, the dry component and wet component are mixed together in the quantities stated above to form a damp mixture or slurry which is the pumpable refractory insulating composition of the invention. The damp mixture or slurry is then transported to a mold installed in the furnace or other structure being insulated, and formed into the ultimate shape of the insulating liner using the mold. The insulating liner is dried at room temperature for about 15 minutes to 5 hours to permit setting, and is then baked at a higher temperature (i.e. above 121°C 250°F) for 5-30 hours. The drying and baking times may vary considerably depending on the thickness of the insulating layer. As indicated above, the colloidal silica in the damp mixture not only aids the flow or "pumpability" of the damp mixture using a concrete pump or similar pump, but also serves as an excellent binder in the ultimate dried insulating liner. Therefore, the amount of the wet component which is added to the dry component to form the pumpable mixture depends somewhat on the amount of colloidal silica which is ultimately needed as a binder. As stated above, the wet component (aqueous colloidal silica) may be added at about 20-80 parts per 100 parts by weight of the dry component, depending on the density of the dry component. Expressed in terms of colloidal silica solids (i.e. excluding the water), the initially wet component should be added at about 5-50 parts by weight colloidal silica solids per 100 parts by weight dry component, preferably about 8-40 parts by weight colloidal silica solids per 100 parts by weight dry component, most preferably about 15-35 parts by weight colloidal silica solids per 100 parts by weight dry component. An example of a concrete pump which is suitable for use with the pumpable refractory insulating composition of the invention is a Thom-Kat TVS16-2065, available from Pultzmeister, Inc., Thomsen Division, Gardena, Calif. 90248. Such a concrete pump is described in U.S. Patent No. 3,832,097, and in German Patent No. 2,162,406, the disclosures of which are incorporated herein by reference. While the use of concrete pumps and similar pumps to transport refractory compositions is known from U.S. Patent No. 5,147,830, such pumps have not previously been used to transport refractory insulating compositions (which, until now, have consisted largely of asbestos or ceramic fibers). While the embodiments of the invention disclosed herein are presently considered to be preferred, various modifications and improvements can be made without departing from the spirit and scope of the invention. The scope of the invention is indicated in the appended claims, and all changes which fall within the meaning and range of equivalents of the claims are intended to be embraced therein. EXAMPLE 1 (HIGH TEMPERATURE COMPOSITION) A non-hazardous pumpable refractory insulating composition was prepared by first preparing a dry component and a wet component. The dry component was prepared by mixing the following ingredients together in the stated weight percentages: Ingredient % By Weight Refractory brick insulating grog 40.0 Flint clay 37.3 Raw kaolinite 17.5 Fumed silica 5.0 Pulverized magnesia 0.2 TOTAL 100.0 The above dry component had a density of 1602 kg/m 3 (100 1b/ft 3 ). Next, a wet component was provided including 40% colloidal silica (average diameter 14x10 -9 m (14 millimicrons)) and 60% water. The dry component and wet component were mixed together at a ratio of 45 parts wet component per 100 parts by weight dry component to form a pumpable castable slurry. The resulting insulating composition was cast into shape, dried and baked to form an insulating layer. The insulating layer was found to provide excellent high-temperature strength and insulating properties, relative impermeability to gases, and resistance to oxidation, corrosion and erosion. EXAMPLE 2 (MEDIUM TEMPERATURE COMPOSITION) A second non-hazardous pumpable refractory insulating composition was prepared from a dry component and a wet component. The dry component was prepared by mixing the following ingredients together in the stated weight percentages: Ingredient % By Weight Verilite™ 30.0 Clay 20.0 Kaolin clay 10.0 Fumed silica 5.0 Fine calcined clay 35.0 TOTAL 100.0 The above dry component had a density of 1201 kg/m 3 (75 1b/ft 3 ). Next, a wet component of 40% colloidal silica (average diameter 14x10 -9 m (14 millimicrons) )in water was mixed with the dry component. The dry component and wet component were mixed together at a ratio of 50 parts wet component per 100 parts by weight dry component to form a pumpable castable slurry. The resulting insulating composition was cast into shape, dried and baked to form an insulating layer. The insulating layer provided excellent medium-temperature strength and insulating properties, relative impermeability to gases, and resistance to oxidation, corrosion and erosion. EXAMPLE 3 (LOW TEMPERATURE COMPOSITION) A third non-hazardous pumpable refractory insulating composition was prepared from a dry component and a wet component. The dry component was prepared by mixing the following ingredients together in the stated weight percentages: Ingredient % By Weight Haydite ™ 35.0 Calcined kaolin 20.0 Fumed silica 5.0 Clay 20.0 Fine calcined clay 20.0 TOTAL 100.0 The above dry component had a density of 801 kg/m 3 (50 1b/ft 3 ). Next, a wet component of 40% colloidal silica (average diameter 14x10 -9 m (14 millimicrons))in water was mixed with the dry component. The dry component and wet component were'mixed together at a ratio of 60 parts wet component per 100 parts by weight dry component to form a pumpable castable slurry. The resulting insulating composition was cast into shape, dried and baked to form an insulating layer. The insulating layer provided excellent low-temperature strength and insulating properties, relative impermeability to gases, and resistance to oxidation, corrosion and erosion.

Claims: A pumpable refractory insulating composition, characterized by : a dry component including about 20 to 90% by weight of a high-density alumina-containing refractory material and about 10 to 80% by weight of a low-density alumina-containing refractory insulating material, the high-density alumina-containing refractory material having a density of at least about 2403 kg/m 3 (150 lb/ft 3 ), the low-density alumina-containing refractory insulating material having a density of about 112-801 kg/m 3 (7 to 50 lb/ft 3 ), the dry component having an overall density of about 641-2082 kg/m 3 (40 to 130 lb/ft 3 ); and a binder component including aqueous colloidal silica being present in sufficient amount to provide about 5 to 50 parts by weight colloidal silica solids per 100 parts by weight of the dry component. The pumpable refractory insulating composition according to Claim 1, further characterized by the colloidal silica having an average particle diameter of about 4-100 x 10 -9 m (4 to 100 millimicrons). The pumpable refractory insulating composition according to Claim 2, further characterized by the colloidal silica having an average particle diameter of about 6-50 x 10 -9 m (6 to 50 millimicrons). The pumpable refractory insulating composition according to Claim 2, further characterized by the colloidal silica having an average particle diameter of about 8-20 x 10 -9 m (8 to 20 millimicrons). The pumpable refractory insulating composition according to Claim 1, further characterized by the aqueous colloidal silica having about 8 to 70% by weight colloidal silica in water. The pumpable refractory insulating composition according to Claim 5, further characterized by the binder component having about 25 to 50% by weight colloidal silica in water. The pumpable refractory insulating composition according to Claim 1, further characterized by the binder component having about 20 to 80 parts by weight aqueous colloidal silica per 100 parts by weight of the dry component. The pumpable refractory insulating composition according to Claim 7, further characterized by the aqueous colloidal silica being present at about 30 to 75 parts by weight aqueous colloidal silica per 100 parts by weight dry component. The pumpable refractory insulating composition according to Claim 7, further characterized by the aqueous colloidal silica being present at about 40 to 70 parts by weight aqueous colloidal silica per 100 parts by weight dry component. The pumpable refractory insulating composition according to Claim 1, further characterized by the low-density refractory insulating material having about 30 to 60% by weight alumina and about 40 to 60% by weight silica. The pumpable refractory insulating composition according to Claim 10, further characterized by the low-density refractory insulating material having about 50-60% by weight alumina and about 40 to 46% by weight silica. The pumpable refractory insulating composition according to Claim 10, further characterized by the low-density refractory insulating material having about 40 to 50% by weight alumina and about 46 to 53% by weight silica. The pumpable refractory insulating composition according to Claim 10, further characterized by the low-density refractory insulating material having about 30 to 40% by weight alumina and about 53 to 60% by weight silica. The pumpable refractory insulating composition according to Claim 1, further characterized by the low-density refractory insulating material having an expanding agent. The pumpable refractory insulating composition according to Claim 14, further characterized by the expanding agent including at least one of an alkali metal oxide, a chemical foaming agent, and a combustible material. The pumpable refractory insulating composition according to Claim 1, further characterized by the low-density refractory insulating material including at least one of vermiculite, perlite, hayditem TM , and insulating brick grog. The pumpable refractory insulating composition according to Claim 1, further charactrized by the high-density refractory material including at least one of refractory clay, kaolinite, mullite, brown fused alumina, tabular alumina, and aluminasilicates. The pumpable refractory insulating composition according to Claim 1, further characterized by the dry component including at least one of a setting agent and a nonwetting agent. The pumpable refractory insulating composition according to Claim 1, further characterized by the dry component having about 15 to 65% by weight of the low-density refractory insulating material and about 35 to 85% by weight of the high-density refractory material. The pumpable refractory insulating composition according to Claim 1, further characterized by the dry component having about 25 to 50% by weight of the low-density refractory insulating material and about 50 to 75% by weight of the high-density refractory material. The pumpable refractory insulating composition according to Claim 1, further characterized by the dry component having an overall density of about 641-1762 kg/m 3 (40 to 110 lb/ft 3 ) .

Inventors: ANDERSON MICHAEL W, BANERJEE SUBRATA, ANDERSON, MICHAEL W., BANERJEE, SUBRATA
Applicants: MAGNECO METREL INC, MAGNECO/METREL, INC.
Application year: 1995
Main classification: C04B35
IPC codes: C04B35