Organosilicon compounds and low temperature curing organosiloxane compositions containing same

Abstract: The present invention relates to organosiloxane compositions that are reaction products of 1) a silane containing at least 3 hydrolyzable groups per molecule, 2) a monohydric or polyhydric alcohol containing at least one organofunctional group and 3) a polyhydric alcohol containing no organofunctional groups or ethylenic unsaturation, wherein said reaction products contain at least two silicon atoms. The organosiloxane compositions are particularly useful as adhesion promoting additives for curable organosiloxane compositions, particularly those that cure by a platinum group metal-catalyzed hydrosilation reaction.

Description: This invention relates to a novel class of organosilicon compounds that are useful adhesion promoting additives. It also relates to organosiloxane compositions that cure by a platinum group metal catalyzed hydrosilation reaction which contains these additives. Our inventions are particularly useful for achieving adhesion to a variety of substrates at curing temperatures below 100°C. One curable organosiloxane composition comprises an organopolysiloxane containing ethylenically unsaturated organic groups and an organosilicon compound containing silicon-bonded hydrogen atoms which is curable in the presence of a catalyst that comprises a group VIII metal or a compound or complex thereof. Usually, this catalyst is a compound or complex of platinum. Unfortunately, the adhesion of these compositions is generally poor, limiting their usefulness in many applications. Several methods are known to improve the adhesion of organosiloxane compositions, however most generally have limitations. For example, primers can be used to improve the adhesion, but their use requires a separate processing step which increases process time and cost. Additionally, the primer usually requires a heat-activated cure to be effective. Adhesion additives, which are added directly to the composition to promote adhesion, have therefore received considerable attention. Useful adhesion additives typically contain at least two functional groups. U.S. Patents 3,772,026 and 3,873,334 teach acyloxy functional silanes which additionally contain silicon bonded hydrogen atoms or alkenyl radicals, respectively. Although the acyloxy functionality is very reactive, it liberates corrosive acetic acid upon reaction with hydroxyl groups present at the surface of the substrate or upon contact with water. U.S. Patent 4,196,273 shows the use of unsaturated alkoxysilanes as adhesion additives; however, adhesion is not demonstrated at temperatures below 100°C. and only adhesion to glass is demonstrated at 100°C. U.S. Patent 4,329,273 claims the use of partially hydrolyzed alkoxysilanes containing ethylenically unsaturated groups bonded to the silicon atom. While satisfactory curing of these compositions was demonstrated at 100°C., the compositions did not cure at ambient laboratory temperatures. U.S. 4,082,726 describes organosilicon compounds containing epoxy functional dialkoxysilyl groups and at least one alkenyl group or silicon-bonded hydrogen atom as adhesion additives. The exemplified compositions are cured at temperatures between 100-200°C. U.S. Patent 4,087,585 discloses physical blends of epoxy functional alkoxysilanes with silanol functional fluids containing alkenyl functionality. Cure was obtained at elevated temperatures. Multifunctional organosilanes containing ethylenic unsaturation, epoxy functionality and alkoxy functionality are revealed in U.S. Patent 4,732,932. U.S. Patent 5,106,933 uses mixtures of alkoxysilanes. U.S. Patents 4,659,851; 4,719,262 and 4,906,686 cover reaction products of 1) unsaturated alcohols or ethers derived from these alcohols and 2) alkoxysilanes. A shortcoming of these reaction products is that the resultant Si-O-C bond between the unsaturated alcohol and alkoxysilane is susceptible to hydrolysis to an extent that the adhesion may be decreased upon exposure to moisture. Organosilicon compounds obtained from the reaction of polyhydric alcohols with compounds containing silicon-bonded hydrolyzable groups are also known in the art. U.S. Patent 2,349,338 uses silicic acid esters of monohydric and polyhydric alcohols, including various glycol and glycerol silicate ester derivatives, as useful corrosion prevention additives for heat transfer liquids. The corrosion prevention is afforded by the hydrolysis product of these compounds. U.S. Patent 2,776,307 concerns silicon-containing esters of the type (R 1 O) 3 Si(XR 2 ) n OSi(OR 3 ) 3 , where X can be oxygen, and n has a value of 2, 3 or 4. The compounds are useful as hydraulic fluids and other lubricant purposes. U.S. Patent 3,992,429 pertains to novel alkoxysilane cluster compounds containing sterically hindered alkyl groups to improve hydrolytic stability. Intended uses include heat transfer fluids, hydraulic fluids, brake fluids, transmission fluids and the like. U.S. Patent 2,630,446 relates to polymeric silicates prepared from tetraalkyl orthosilicates and polyhydric alcohols. The silicates are intended as plasticizers, lubricants and hydraulic fluid additives. U. S. Patent 4,072,655 utilizes reaction products of polyhydric alcohols and silanes containing from 1 to 4 hydrolyzable groups per molecule. The reaction products are used as non-slump additives for moisture curable organosiloxane compositions. The preparation of alkoxysilanes from glycols and glycol monoethers is summarized by H.G. Emblem and K. Hargreaves in the Journal of Inorganic Nuclear Chemistry, Vol. 30 (3), p. 721, 1968). The preparation of esters derived from tetraalkyl orthosilicates and polyhydroxy alcohols by a transesterification reaction is dealt with in GB Patent 450,875. U.S. Patent 3,029,269 contains compounds of the type (RO) 3 SiOCR' 2 (CH 2 ) n CR' 2 -OSi(OR) 3 , where n is 0-16 and R' is H or a lower aliphatic radical, and R is a saturated aliphatic radical of 1-16 carbons. The compounds are suggested as lubricants and hydraulic fluids that possess low pour point, good viscosity and viscosity index properties as well as hydrolytic stability. Finally, U.S. Patent 5,424,384 has adhesion promoting additives for curable organosiloxane compositions that are reaction products of a polyhydric saturated alcohol with a silane or bis-silylalkane. The organosilicon reactant contains at least three alkoxy or enoloxy groups on each silicon atom. An objective of this invention is to provide a class of novel organosiloxanes that are particularly useful as adhesion promoting additives in organosiloxane compositions, particularly those that cure by a platinum group metal catalyzed hydrosilation reaction at temperatures of 100°C. or below. The objectives of the present invention are achieved by providing organosiloxane compositions that are reaction products of 1) a silane containing at least 3 hydrolyzable groups per molecule, 2) a monohydric or polyhydric alcohol containing at least one organofunctional group and 3) a , polyhydric alcohol that is free of organofunctional groups as defined in claim 1. The present reaction products preferably comprise molecules containing the ≡SiOR 1 OSi≡ group wherein R 1 represents an alkylene or hydroxyalkylene radical and the remaining valences of the silicon atoms are satisfied by hydrolyzable groups and at least one adhesion-promoting organofunctional group that is bonded to silicon through an oxygen atom. Examples of suitable organofunctional groups are alkenyl and (meth)acryloxyalkyl. The organosilicon compounds of this invention are products of the reaction between 1) a polyhydric alcohol of the general formula R 1 (OH) m , 2) a mono- or polyhydric alcohol of the general formula R 2 (OH) n and 3) a silane of the formula R 3 p SiX 4-p , wherein R 1 is a hydrocarbon radical having a valence of m and no organofunctional substituents; R 2 is an organic radical with a valence of n comprising carbon, hydrogen; and at least one organofunctional substituent, where said substituent is selected from the group consisting of CH 2 =CH-, acryloxy and methacryloxy; R 3 is an unsubstituted or substituted monovalent hydrocarbon radical; X represents a hydrolyzable group; m is at least 2; n is at least 1 and p is 0 or 1, and wherein each molecule of said organosilicon compounds reaction products contains at least two silicon atoms. This invention also provides curable organo-siloxane compositions as defined in claim 5 which comprise (A) a curable polyorgano-siloxane; (B) a curing agent in an amount sufficient to cure said composition; (C) a curing catalyst in an amount sufficient to promote curing of said composition; and (D) an organosilicon composition of the present invention as an adhesion promoting additive in an amount sufficient to achieve adhesion to a substrate in contact with said composition during curing thereof. The characterizing feature of the average molecule in the reaction products that constitute the present organosilicon compositions is the presence of 1) at least two residues per molecule derived from a silane containing at least three silicon-bonded hydrolyzable groups, represented by X in formula 1, and an optional monovalent hydrocarbon radical or a monovalent organofunctional group, represented by R 3 , that is bonded to silicon through carbon, 2) at least one residue derived from a monohydric or polyhydric alcohol containing an organofunctional group, and 3) at least one residue derived from a polyhydric alcohol that is free of ethylenic unsaturation or other organofunctional groups. As used herein, the term "monovalent hydrocarbon radical" includes alkyl containing from 1 to 20 carbon atoms, such as methyl, ethyl, n-hexyl and n-dodecyl; cycloalkyl such as cyclohexyl; aryl radicals such as phenyl or naphthyl; aralkyl such as benzyl and alkaryl such as tolyl or xylyl. These hydrocarbon radicals can be unsubstituted or contain relatively non-reactive substituents such as halogen or an organofunctional group. The organofunctional group present on the hydrocarbon radical represented by R 2 reacts during curing of compositions containing the present reaction products as adhesion promoting additives. These organofunctional groups contain carbon and hydrogen. The optional hydrocarbon radical R 3 on the silane reactant can be unsubstituted or can contain inert or organofunctional substituents. Relatively inert substituents like halogen atoms do not react during preparation of the present reaction products or during use of these reaction products in our curable organosiloxane compositions. When the compounds of this invention are present as the adhesion-promoting additives in a curable organosiloxane composition, the organofunctional groups react with at least one of the groups that either participate in the curing reaction of the organosiloxane composition or are present on a substrate that the composition is in contact with during curing. Examples of suitable organofunctional groups are CH 2 =CH-, and (meth)acryloxyalkyl. The present compounds will be referred to hereinafter as ingredient D of our curable compositions containing these compounds as adhesion-promoting additives. The hydrolyzable and organofunctional groups present in ingredient D can be any that will not interfere with curing of compositions containing this ingredient. Examples of suitable hydrolyzable groups that are represented by X in the formula for the silane reactant include alkoxy, enoloxy and ketoximo. The present reaction products are used as adhesion promoting additives in our organosiloxane compositions that cure using hydrosilation reactions catalyzed by platinum group metals and compounds of these metals. The term "cure" means the conversion of a liquid or semi-solid composition to a crosslinked elastomeric or resinous material by the reaction of groups present on the polyorganosiloxane (ingredient A) with the curing agent. The present adhesion-promoting additives are used with organosiloxane compositions that cure by a hydrosilation reaction catalyzed by metals from the platinum group of the periodic table and compounds of these metals. The additives are particularly useful in compositions that are cured at temperatures up to 100°C. During the formation of preferred embodiments of our adhesion additives, one alkoxy or other hydrolyzable group per molecule of the silane R 3 p SiX 4-p reacts with a hydroxyl group on the polyhydric alcohol R 1 (OH) m and a second hydrolyzable group of the silane reacts with a hydroxyl group of the organofunctional alcohol R 2 (OH) n . Preferably at least 50 percent, most preferably at least 90 percent, of the initial silane molecules react with both the organofunctional alcohol and the polyhydric alcohol R 1 (OH) m and the polyhydric alcohol reacts with 2 molecules of silane. It is possible for two or more alkoxy or other hydrolyzable groups on the initial silane to react with the same or different molecules of the polyhydric alcohol R 1 (OH) m . Alternatively, a given molecule of the silane can react with 0, 1, 2 or 3 moles of the organofunctional alcohol R 2 (OH) n . Other possible reaction products will be apparent to those knowledgeable in the equilibration reactions of silanes containing hydrolyzable groups with two different alcohols. The present reaction products are typically mixtures of the various possible products. When the polyhydric alcohol R 1 (OH) m is a diol, using the preferred molar ratio of silane to polyhydric alcohol to organofunctional alcohol of 1.4:1:1, the major portion of the reaction product should contain one residue from each of the two types of alcohols. A larger relative concentration of silane will be required when m in the formula for the unsubstituted polyhydric alcohol is 3. The silane used to prepare the present reaction products is represented by the formula R 3 n SiX 4-n , wherein R 3 represents a monovalent hydrocarbon radical that can be substituted or unsubstituted. When R 3 contains a substituent, it can be relatively inert, such as a halogen atom, or it can be an organofunctional group. Suitable organofunctional groups are discussed above. Preferred silane reactants that do not contain organofunctional groups are methyltrimethoxysilane, methyltriethoxysilane, tetramethylorthosilicate, tetraethylorthosilicate and methyltriisopropenyloxysilane. Examples of silanes containing organofunctional groups are vinyltrimethoxysilane, 3-methacryloxypropyltri-methoxysilane and 3-glycidoxypropyltrimethoxysilane. The polyhydric alcohol R 1 (OH) m contains from 2 to 20 carbon atoms and is free of ethylenic unsaturation or other organofunctional groups. Preferred polyhydric alcohols contain from 2 to 10 carbon atoms, two or three hydroxyl groups and are represented by ethylene glycol, propylene glycol, 1,3-propanediol, glycerol, 1,4-butanediol, neopentyl glycol, 2,2,2-trimethylolpropane and 1,10-decanediol. In preferred embodiments, R 1 of the polyfunctional alcohol is an unsubstituted aliphatic radical containing from 2 to 5 carbon atoms and has a valence of m wherein m is 2 or 3. When the number of hydroxyl groups in the polyhydric alcohol exceeds the number represented by m in formula 1, at least a portion of the additional hydroxyl groups are etherified or esterified. The organofunctional alcohol represented by the formula R 2 (OH) n contains from 3 to 20 carbon atoms, and at least one of the organofunctional groups described above. In preferred embodiments, R 2 is an alkenyl radical containing from 3 to 12 carbon atoms. Examples of preferred alcohols are allyl alcohol, 3-buten-1-ol, 5-hexen-1-ol, 1-octene-3-ol and 10-undecen-1-ol. A second class of suitable ethylenically unsaturated monohydric alcohols are half esters of dihydric alcohols wherein the acid portion of the ester is derived from an ethylenically unsaturated monocarboxylic acid such as acrylic or methacrylic acid. Examples of suitable esters of this type are ethylene glycol monoacrylate, propylene glycol monoacrylate and ethylene glycol monomethacrylate. Silanes derived from other classes of ethylenically unsaturated monohydric organic compounds are described in U.S. Patent 4,719,262. This patent is helpful as a source of the types of silanes useful as starting materials for preparing preferred embodiments of the present compounds. The reaction between the polyhydric alcohol R 1 (OH) m , the organofunctional alcohol R 2 (OH) n and the silane R 3 p SiX (4-p) is conducted under conditions that are typical for interchange reactions between alcohols and silicon-bonded hydrolyzable groups. These reactions are typically conducted under an inert, anhydrous atmosphere, such as nitrogen, at temperatures from ambient to 200°C. and may employ an organotitanium compound as a catalyst. Suitable organotitanium compounds are tetraalkyl titanates, such as tetraisopropyl titanate or tetra-n-butyl titanate and chelated organotitanium compounds such as 2,5-diisopropoxy-bis-ethylacetoacetate titanium. The weight of catalyst typically constitutes from 0.1 to 5 percent of the combined weight of all reactants. Reactions involving exchanges of silicon bonded alkoxy and enoloxy groups generate the alcohol or ketone, corresponding to the original silicon-bonded alkoxy or enoloxy group, as a by-product. Because these reactions are often reversible, it is usually desirable to remove this by-product alcohol or ketone by distillation as the reaction progresses. The course of exchange reactions involving the generation and removal of alcohol and ketone by-products is readily followed by measuring the amount of by-product collected. Methanol and ethanol are the lowest boiling alcohols and are the most easily removed during preparation of our adhesion-promoting additives. It is, therefore, preferable that the alkoxy groups of the present adhesion additives, represented by OR 4 in the foregoing formulae, be methoxy or ethoxy. For the same reason, the enoloxy group is preferably isopropenyloxy. The reactants and optional catalyst are heated for a period of time sufficient to achieve a substantially complete reaction, as indicated by the amount of by-product alcohol or ketone collected. This time period is typically from 1 to 5 hours and the reaction mixture is preferably heated from 50 to 200°C. It may be desirable to include in the reaction mixture a liquid diluent that may also function as a solvent for the reactants. Suitable diluents include aliphatic and aromatic hydrocarbons that are liquid at ambient temperature and boil within the range of from 50 to 200°C. Representative diluents include alcohols such as methanol, ethanol and isopropanol; aliphatic hydrocarbons such as hexane or heptane and liquid aromatic hydrocarbons such as toluene and xylene. The present organosilicon compositions are prepared in two stages. During the first stage the polyhydric alcohol R 1 (OH) m is reacted with the silane R 3 p SiX 4-p . The resultant reaction product is then blended with a curable organosiloxane composition, at which time the organofunctional alcohol R 2 (OH) n is added to the composition. The present organosilicon composition is formed during curing of the organosiloxane composition. The present adhesion promoting additives are particularly useful in organosiloxane compositions that cure by a platinum group metal-catalyzed hydrosilation reaction at temperatures below 100°C. The concentration of adhesion promoting ingredient D is sufficient to provide cohesive bonding of the cured composition to the desired substrate. This typically requires at least 0.25 weight percent of the adhesion promoter, based on the weight of the curable composition. A concentration of between 0.5 and 5 weight percent is preferred. The ability of the organosiloxane composition to cure completely under the desired conditions and/or the properties of the cured composition are adversely affected when the concentration of adhesion promoting additive exceeds 10 weight percent, based on the weight of the curable composition. For purposes of this invention, cohesive bonding is characterized by cohesive failure, which occurs when the strength of the bond between the cured organosiloxane material and the substrate exceeds the tensile strength of the cured material. In a typical adhesion test, increasing force is applied to the layer of cured material until it is removed from the substrate. Cohesive failure occurs within the body of the cured organosiloxane material rather than at the interface between the material and the substrate that the material is in contact with during the curing reaction. At least a portion of the cured material remains adhered to the substrate. The degree of cohesive failure is expressed as the level of force required to remove the cured organosiloxane composition from a substrate that it is in contact with during the curing reaction. The polyorganosiloxane ingredient, ingredient A, of the preferred curable organosiloxane compositions of this invention is a principal ingredient. Because these compositions cure by a hydrosilation reaction, ingredient A contains at least two silicon-bonded alkenyl radicals in each molecule. Suitable alkenyl radicals contain from 1 to 10 carbon atoms and are exemplified by vinyl, allyl and 5-hexenyl. The silicon-bonded organic groups other than alkenyl radicals present in ingredient A are typically monovalent hydrocarbon and halogenated monovalent hydrocarbon radicals exemplified by alkyl radicals such as methyl, ethyl and propyl; aryl radicals such as phenyl; and halogenated alkyl radicals such as 3,3,3-trifluoropropyl. The molecular structure of ingredient A is not critical and will be determined by the physical properties desired in the cured composition. To achieve a useful level of tensile properties in the elastomers and other products prepared by curing our compositions, the molecular weight of this ingredient should be sufficient to achieve a viscosity at 25°C. of greater than 0.1 Pa·s. The upper limit for the molecular weight of ingredient A is not specifically restricted, and is typically limited only by the processability of the curable organosiloxane composition. The polyorganosiloxanes range from pourable liquids to gum type polymers that are typically characterized by Williams plasticity values. As ingredient A there are used polydiorganosiloxanes represented by the general formula I where each R 5 is individually selected from monovalent hydrocarbon radicals, R 6 represents a vinyl or other alkenyl radical, and n represents a degree of polymerization equivalent to a viscosity of at least 100 centipoise (0.1 Pa·s), preferably from 0.1 to 10 Pa·s. The hydrocarbon radicals represented by R 5 are either unsubstituted or contain substituents such as halogen atoms that will not adversely affect the storage stability and curing of our compositions or the properties of cured articles prepared from these compositions. The two R 5 substituents on each of the silicon atoms in formula I are identical or different and contain from 1 to 20 carbon atoms. A range of from 1 to 10 carbon atoms is preferred based on the availability of the corresponding monomers. Most preferably, at least one of the hydrocarbon radicals on each silicon atom is methyl and any remainder are vinyl, phenyl and/or 3,3,3-trifluoropropyl. This preference is based on the availability of the reactants typically used to prepare the polydiorganosiloxane and the properties of cured elastomers prepared from these polydiorganosiloxanes. For the same reasons, R 6 is preferably vinyl or 5-hexenyl. Representative embodiments of ingredient A, containing ethylenically unsaturated hydrocarbon radicals only at the terminal positions, include dimethylvinylsiloxy-terminated polydimethylsiloxanes, dimethylvinylsiloxy-terminated polymethyl-3,3,3-trifluoropropylsiloxanes, dimethylvinylsiloxy-terminated dimethylsiloxane/3,3,3-trifluoropropylmethylsiloxane copolymers and dimethylvinylsiloxy-terminated dimethylsiloxane/methylphenylsiloxane copolymers. Methods for preparing ingredient A are by hydrolysis and condensation of the corresponding halosilanes or by condensation of the cyclic polydiorganosiloxanes. These methods are sufficiently disclosed in the patent and other literature such that a detailed description in this specification is not necessary. For applications requiring high levels of physical properties such as tear strength, it may be desirable to include in the curable organosiloxane composition a second polydiorganosiloxane containing ethylenically unsaturated hydrocarbon radicals bonded to both terminal and non-terminal silicon atoms. Our preferred curable organosiloxane compositions contain at least one organohydrogensiloxane that functions as a curing agent for ingredient A. In the presence of the hydrosilation catalyst, ingredient C, the silicon-bonded hydrogen atoms in ingredient B undergo an addition reaction, referred to as hydrosilation, with the silicon-bonded alkenyl groups in ingredient A, resulting in crosslinking and curing of the composition. Ingredient B must contain at least 2 silicon- bonded hydrogen atoms in each molecule. If ingredient A contains only two alkenyl radicals per molecule, ingredient B must contain an average of more than two silicon-bonded hydrogen atoms to achieve a crosslinked structure in the final cured product. The silicon-bonded organic groups present in ingredient B are selected from the same group of monovalent hydrocarbon and halogenated hydrocarbon radicals as the organic groups of ingredient A. The organic groups in ingredient B are preferably substantially free of ethylenic or acetylenic unsaturation. The molecular structure of ingredient B can be straight chain, branch-containing straight chain, cyclic or network. While the molecular weight of ingredient B is not specifically restricted, viscosities in the range of 3 to 10,000 centipoise (0.003 to 10 Pa·s) at 25°C. are used. The concentration of ingredient B is sufficient to provide a molar ratio of silicon-bonded hydrogen atoms to alkenyl radicals in the curable composition of from 0.5 to 2. When the curable composition contains less than 0.5 moles of silicon-bonded hydrogen atoms per mole of alkenyl radicals, it is not possible to achieve the desired physical properties following curing. The physical properties of the cured article may vary with time when this molar ratio exceeds 20 moles of silicon-bonded hydrogen per mole of alkenyl radical. Curing of these compositions is catalyzed by a hydrosilation catalyst that is a metal from the platinum group of the periodic table or a compound of such a metal. These metals include platinum, palladium and rhodium. Platinum and platinum compounds are preferred based on the high activity level of these catalysts in hydrosilation reactions. Preferred curing catalysts are platinum black, platinum metal on various solid supports, chloroplatinic acid, alcohol solutions of chloroplatinic acid and complexes of chloroplatinic acid with liquid ethylenically unsaturated compounds such as olefins and organosiloxanes containing ethylenically unsaturated hydrocarbon radicals bonded to silicon. Complexes of chloroplatinic acid with the aforementioned organosiloxanes containing ethylenically unsaturated hydrocarbon radicals are described in U.S. Patent 3,419,593, which teaches particularly preferred catalysts. The concentration of ingredient C in our compositions is equivalent to a platinum concentration of from 1 to 50 parts by weight of platinum group metal, per million parts (ppm), based on the combined weight of ingredients A and B. Curing does not proceed satisfactorily at below 0.1 ppm of platinum, while using more than 500 ppm results in no appreciable increase in cure rate, and is therefore uneconomical. Mixtures of the aforementioned ingredients A, B and C may begin to cure at ambient temperature. To obtain a longer working time or "pot life", the activity of the catalyst under ambient conditions can be retarded or suppressed by addition of a suitable inhibitor. Known platinum catalyst inhibitors include the acetylenic compounds disclosed in U.S. Patent 3,445,420. Acetylenic alcohols such as 2-methyl-3-butyn-2-ol constitute a preferred class of inhibitors that will suppress the activity of a platinum-containing catalyst at 25°C. Compositions containing these catalyst inhibitors typically require heating at temperatures of 70°C. or above to cure at a practical rate. When it is desired to increase the pot life of a curable composition under ambient conditions, this can be accomplished using an alkenyl substituted siloxane of the type described in U.S. Patent 3,989,667. Cyclic methylvinylsiloxanes are preferred. Inhibitor concentrations as low as one mole of inhibitor per mole of platinum will in some instances impart satisfactory storage stability and cure rate. In other instances, inhibitor concentrations of up to 500 or more moles of inhibitor per mole of platinum are required. The optimum concentration for a given inhibitor in a given composition is readily determined by routine experimentation and does not constitute part of this invention. When it is desired to store for an extended period of time a one part composition that cures by a hydrosilation reaction and contains a platinum group metal or compound thereof as the catalyst, this can be achieved by encapsulating a finely divided form of the catalyst in a thermoplastic polymer that melts at the desired curing temperature. Typical encapsulated platinum-containing catalysts are described in U.S. Patent 4,766,176. One type of alternative organosiloxane composition suitable for use with the present adhesion promoting additives contains a polyorganosiloxane with at least two silanol groups per molecule, an organosilicon compound containing at least three silicon-bonded hydrolyzable groups or silicon-bonded hydrogen atoms as the curing agent and an optional curing catalyst. Suitable hydrolyzable groups for moisture curable compositions are alkoxy, enoloxy, ketoximo and carboxy such as acetoxy. Other types of alternative composition cure by a free radical or cationic polymerization initiated by the decomposition of a photolytically unstable compound such as a alpha-hydroxy ketone or by the use of high energy radiation. A free radical reaction may also be initiated by thermal decomposition of a free radical precursor such as an organic peroxide or an azo compound. To achieve high levels of tear strength and other physical properties, it may be desirable to include a reinforcing filler such as finely divided silica. Silica and other reinforcing fillers are often treated with one of more of the known treating agents to prevent a phenomenon referred to as "creping" or "crepe hardening" during processing of the curable composition. Finely divided forms of silica are preferred reinforcing fillers. Fumed silicas are particularly preferred because of their relatively high surface area, which is typically at least 50 m 2 /g. Fillers having surface areas of at least 200 m 2 /g are preferred for use in our method. The amount of finely divided silica or other reinforcing filler used in these compositions is at least in part determined by the physical properties desired in the cured elastomer. Liquid or pumpable polyorganosiloxane compositions typically contain from 10 to 60 percent by weight of silica, based on the weight of polydiorganosiloxane. This value is preferably from 30 to 50 percent. The filler treating agent can be any of the low molecular weight organosilicon compounds disclosed in the art as suitable for preventing creping of organosiloxane compositions during processing. The treating agents are typically liquid hydroxyl-terminated polydiorganosiloxanes containing an average of from 2 to 20 repeating units per molecule, and organosilicon compounds such as hexaorganodisiloxanes or hexaorganodisilazanes that hydrolyze and condense under the conditions used to treat the filler. Preferably at least a portion of the silicon bonded hydrocarbon radicals present on the treating agent are identical to a majority of the hydrocarbon radicals present in ingredients A and B. A small amount of water can be added together with the silica treating agent(s) as a processing aid. It is believed that the treating agents function by reacting with silicon-bonded hydroxyl groups present on the surface of the silica or other filler particles to reduce interaction between these particles and the polyorganosiloxanes present in the curable composition. When a silica filler is used, it is preferably treated in the presence of at least a portion of the other ingredients of our compositions by blending these ingredients together until the filler is completely treated and uniformly dispersed to form a homogeneous material. The ingredients that are present during treatment of the filler typically include the silica treating agents and at least a portion of the polydiorganosiloxane(s) referred to herein as ingredient A. Our organosiloxane compositions can also contain one or more additives that are conventionally present in curable compositions of this type to impart or enhance certain physical properties of the cured composition in addition to adhesion or to facilitate processing of the curable composition. Typical additives are non-reinforcing fillers such as quartz, alumina, mica and calcium carbonate; pigments such as carbon black or titanium dioxide; dyes, flame retardants, and heat and/or ultraviolet light stabilizers. Resinous organosiloxane copolymers can also be used in place of or in combination with one or more reinforcing fillers to improve the physical properties of the cured organosiloxane composition. A preferred type of resinous copolymer contains repeating units of the general formula SiO 4/2 in addition to triorganosiloxy units of the general formulae R 7 3 SiO 1/2 and diorganovinylsiloxy units of the general formula CH 2 =CH(R 8 ) 2 SiO 1/2 . In these formulae, R 7 and R 8 are individually monovalent hydrocarbon or substituted monovalent hydrocarbon radicals as previously defined for the R 5 radicals of ingredient A. The molar ratio of the combination of triorganosiloxy units and diorganovinylsiloxy units to SiO 4/2 units in the resinous copolymer is from 0.7 to 1.2, inclusive. The vinyl-containing units constitute from 2 to 8 percent by weight of the copolymer, which preferably contains at least two vinyl radicals per molecule. In preferred embodiments of the copolymer, the ranges for the molar ratio of diorganovinylsiloxy to triorganosiloxy to SiO 4/2 units is 0.08-0.1:0.06-1:1. Resinous copolymers are prepared as described in U.S. Patent 2,676,182, which teaches the preparation of and the scope of use for these resins. The copolymers described in this patent contain from 2 to 23 percent by weight of hydroxyl groups, which is considerably above the maximum level of about 0.8 weight percent preferred for precursors of the present copolymers. The hydroxyl content of the precursor is conveniently reduced to the desired level by employing a higher concentration of triorganosiloxy units than the concentration range taught by the subject patent. The compositions of this invention are prepared by combining all of ingredients at ambient temperature. Any of the mixing techniques and devices described in the prior art can be used for this purpose. The particular device used will be determined by the viscosity of the ingredients and the final curable composition. Suitable mixers include paddle type mixers, kneader type mixers and two- or threeroll rubber mills. Cooling of the ingredients during mixing may be desirable to avoid premature curing of the composition. To maximize storage stability of preferred organosiloxane compositions that cure by a hydrosilation reaction, these compositions are preferably kept in closed containers until used. If greater storage stability is desired, the compositions can be packaged in two or more containers with the organohydrogensiloxane (ingredient B) and the platinum group metal catalyst (ingredient C) in different containers. Depending upon the types and concentrations of ingredients A and B, cured organosiloxane materials prepared using the present compositions will vary in properties from brittle resins to elastomers to gels. They are useful in a variety of end-use applications as coatings or as molded or extruded articles. Unfilled curable organosiloxane compositions are particularly useful as adhesives, protective coatings, encapsulants and potting compositions for protecting delicate electronic devices such as transistors and integrated circuits from damage by moisture and other materials present in the environment that can adversely affect operation of the device. These compositions can be used to coat either the individual devices or a circuit board containing a number of these devices together with other electronic components. The present compositions are applied to substrates by spraying, dipping, pouring, extrusion or by the use of a brush, roller or coating bar. The selection of a particular application method will be determined at least in part by the viscosity of the curable composition. The viscosity of the composition can be reduced using suitable solvents or reactive diluents as known in the art. Organosiloxane compositions containing the present adhesion additives cohesively bond to a variety of organic and inorganic substrates during curing at temperatures as low as 25°C. The ability of our compositions to develop adhesion when cured at these relatively low temperatures make them suitable for application to substrates that cannot withstand the elevated temperatures of 100°C. or higher. These temperatures are often required to cure organosiloxane compositions containing prior art adhesion additives, some of which may even inhibit platinum group metal catalysts. Preferred compositions of this invention cure over a period of several hours under ambient conditions. As is true for other compositions that cure by a platinum-catalyzed hydrosilation reaction, curing can also be accelerated by heating of our compositions. Curing temperatures of from 25 to 80°C. are preferred. The following examples further describe preferred curable compositions of the present invention. Unless otherwise specified, all parts and percentages in the examples are by weight and the viscosities were measured at 25°C. The following general procedure was used to prepare the partial reaction products of polyhydric alcohols, monohydric alcohols, and alkoxysilanes: The alkoxysilane and titanate catalyst were charged into a three-necked, round bottom glass reactor. The reactor was then equipped with a stirrer, thermometer, Thermo-Watch(R) temperature control, addition funnel, distillation head, condenser, receiver flask cooled with dry ice, and a dry ice-cooled cold finger trap. The reactor was then filled with nitrogen. All the glassware had been dried at 120°C. prior to use. The addition funnel was charged with the polyol, an equal weight of ethyl alcohol, and the unsaturated alcohol. The reaction mixture was then stirred, heated to 75°C., and the contents of the addition funnel were added slowly. Following addition completion, a stream of nitrogen was passed through the reactor and the reaction mixture was heated at 105°C. until no additional liquid collected in the receiver, which generally required from 0.5 to 1.5 hours of heating. Heating was continued while the pressure in the reactor was rapidly reduced to 5.3 kPa (40 mm Hg) and maintained there for 20 minutes. The reaction mixture was then cooled and brought to atmospheric pressure. The recovered liquid under atmospheric pressure was primarily ethyl alcohol and a mixture of ethyl alcohol and tetraethyl orthosilicate under reduced pressure. Adhesion additive D1 was prepared by reacting 64.21 parts of tetraethyl orthosilicate, 0.1 part of tetrabutyl titanate, 9.56 parts of anhydrous ethylene glycol, and 26.23 parts of undecylenyl alcohol. The polyol/monohydric alcohol solution was added over a 47 minute period and was then heated for 25 minutes before the vacuum was applied. 27.2 parts of distillate were collected prior to application of vacuum, which was shown to contain 91.6% ethyl alcohol and 8.4% tetraethyl orthosilicate by gas/liquid chromatography (GC). Following application of vacuum, 6.04 parts distillate were collected which was shown to contain 60.1% ethyl alcohol and 39.8% tetraethyl orthosilicate by GC analysis. The product (72.6 parts) was a transparent yellow/brown fluid. Adhesion additive D2c is outside the scope of the present invention and was prepared for comparative purposes by reacting tetraethyl orthosilicate (245.6 parts), tetrabutyl titanate (0.45 parts) and undecylenyl alcohol (199.6 parts). No polyol or ethyl alcohol was used in preparing this adhesion additive. The unsaturated alcohol was added over an 8 hour period at a temperature of 95°C., at which time the reaction mixture was heated to a final temperature of 140°C. Removal of volatile liquids under reduced pressure was not used in this preparation. Tetraethyl orthosilicate (TEOS) and ethyl polysilicate (EPS) were also used as adhesion additives for comparative purposes. Each of the curable compositions contained tetrabutyl titanate (TBT) as a catalyst to increase the rate of adhesion development. The two part curable organosiloxane composition used to evaluate the adhesion promoters contained the following ingredients: Part A: 46 parts of a dimethylvinylsiloxy-terminated polydimethylsiloxane having a viscosity of 0.4 Pa·s at 25°C.; 46 parts of quartz having an average particle size of 5 micrometers; 7 parts of a dispersion containing 80 weight percent of a dimethylvinylsiloxy-terminated polydimethylsiloxane having a viscosity of 0.4 Pa·s at 25°C.; 13 weight percent zinc oxide and 7 weight percent lampblack; and 0.2 part of a reaction product of hexachloroplatinic acid and sym-tetramethyldivinyldisiloxane that had been diluted with a liquid dimethylvinylsiloxy terminated polydimethylsiloxane in an amount sufficient to achieve a platinum content of 0.7 weight percent. Part B: 47 parts of a dimethylvinylsiloxy-terminated polydimethylsiloxane exhibiting a viscosity of 0.4 Pa·s at 25°C. (ingredient A); 47 parts of quartz having an average particle size of 5 micrometers; 6 parts of a trimethylsiloxy-terminated polydiorganosiloxane containing an average of five methylhydrogensiloxane units and three dimethylsiloxane units per molecule with a silicon-bonded hydrogen atom content in the range from 0.7 to 0.8 weight percent (Ingredient B); and 0.1 part of cyclic methylvinylsiloxanes. Some of the compositions contained additional quantities of the organohydrogensiloxane (Ingredient B). The amounts of parts A and B of the curable composition and the type and amounts of adhesion promoter used to prepare each of the compositions evaluated are summarized in Tables 1 and 2. The amounts are expressed as parts by weight. Composition C1 C2 C3 C4 C5 C6 Part A 7.5 7.5 7.5 7.5 4.88 4.76 Part B 7.5 7.5 7.5 7.5 4.89 4.75 TBT 0.01 0.01 0.01 0.01 0.01 0.01 5 5 5 5 0 0 Ingredient D Type EPS EPS TEOS TEOS D2c D2c Concentration 0.38 0.75 0.38 0.75 0.23 0.43 Ingredient B 0.00 0.00 0.00 0.00 0.09 0.17 Composition (Pts.) 1 2 3 4 Part A 4.89 4.88 4.75 4.74 Part B 4.89 4.90 4.79 4.76 TBT 0.010 0.010 0.010 0.010 Additive Type D1 D1 D1 D1 Additive Conc. 0.25 0.33 0.51 0.67 Ingredient B 0.07 0.09 0.13 0.17 After being placed under reduced pressure to remove entrapped air bubbles, portions of each sample were drawn down as 0.008 inch (0.2 mm) thick liquid films onto a substrate. The substrates on which the curable compositions were evaluated were glass microscope slides (glass); panels measuring 7.6 by 12.7 cm. and formed from Type 3003 H14 alloy mill finish aluminum available from Q-Panel (mill aluminum); Type 2024 T3 bare aluminum panels measuring 2.5 by 7.6 cm. (bare aluminum); epoxy-bonded fiberglass panels measuring 7.6 by 12.7 cm., available as G-10 from Almac Plastics, Inc. (epoxy); and copper plated epoxide panels measuring 2.5 by 7.6 cm (copper). The compositions were cured either at room temperature or for 30 minutes at 70°C. in a forced air oven followed by additional cure at room temperature. The adhesion test consisted of scratching the cured coatings with the blade of a metal spatula to determine whether the coating could be removed without leaving a residue on the surface (adhesive failure, AF) or whether failure occurred within the coating layer, resulting in at least a portion of the coating material in the test area adhering to the substrate (cohesive failure, CF). On some samples the coating exhibited adhesive failure in some areas and cohesive failure in others (AF/CF). Coatings exhibiting cohesive failure were further tested to determine if the residue on the substrate and the adjacent coating material could be removed by rubbing with a finger. If the coating was removed in this manner, the pressure required to remove the coating was rated on a subjective scale as slight (WE), medium (WM) or high (WD). The adhesion achieved for the coatings cured at room temperature and by heating are recorded in Tables 3 and 4. The results summarized in Tables 3 and 4 demonstrate the excellent adhesion to a variety of substrates following curing at either room temperature or for a short period of time at 70°C. using compositions containing the adhesion promoting additives of the present invention.

Claims: An organosilicon composition comprising at least one compound formed by the reaction between 1) a polyhydric alcohol of the general formula R 1 (OH) m , 2) an alcohol of the general formula R 2 (OH) n and 3) a silane of the formula R 3 p Six 4-p , wherein R 1 is a hydrocarbon radical having a valence of m and no ethylenic unsaturation, R 2 is an organic radical having a valence of n and comprising carbon, hydrogen, and at least one organofunctional substituent selected from the group consisting of CH 2 =CH-, acryloxy and methacryloxy, R 3 is an unsubstituted or substituted monovalent hydrocarbon radical, X represents a hydrolyzable group, m is at least 2, n is at least 1, p is 0 or 1 and wherein each molecule of said compound contains at least two silicon atoms. A composition according to claim 1 wherein R 1 contains from 2 to 20 carbon atoms; R 2 is a monovalent hydrocarbon radical containing said organofunctional substituent; R 3 is selected from the group consisting of alkyl, alkenyl, epoxyalkyl and methacryloxyalkyl; X represents an alkoxy or ketoximo group; m is 2 or 3 and n is 1, 2 or 3. A composition according to claim 1 wherein R 1 contains from 2 to 20 carbon atoms, R 2 is an alkyl radical containing said organofunctional substituent, R 3 is selected from the group consisting of alkyl, alkenyl, epoxyalkyl and methacryloxyalkyl, and X represents an alkoxy group containing from 1 to 4 carbon atoms, m is 2 or 3 and n is 1, 2 or 3. A composition according to claim 3 wherein said silane is selected from the group consisting of methyltrimethoxysilane, methyltriethoxysilane, tetramethyl orthosilicate, tetraethyl orthosilicate, methyltriisopropenyloxysilane, vinyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane and 3-glycidoxypropyltrimethoxysilane; said polyhydric alcohol is selected from the group consisting of ethylene glycol, propylene glycol, 1,3-propanediol, glycerol, 1,4-butanediol, neopentyl glycol, 2,2,2-trimethylolpropane, and 1,10-decanediol; said alcohol represented by the formula R 2 (OH) n is selected from the group consisting of allyl alcohol, 3-buten-1-ol, 5-hexen-1-ol, 1-octene-3-ol and 10-undecen-1-ol; and each molecule of said compound contains at least two silicon atoms. A curable organosiloxane composition comprising A. a curable polyorganosiloxane which exhibits a viscosity greater than 0.1 Pa·s at 25°C. and corresponds to the general formula wherein each R 5 is individually selected from monovalent hydrocarbon radicals, R 6 represents an alkenyl radical, and g represents a degree of polymerization equivalent to a viscosity of at least 0.1 Pa·s; B. an amount of a curing agent sufficient to cure said composition, wherein said curing agent is an organohydrogensiloxane exhibiting a viscosity at 25°C. of from 0.003 to 10 Pa·s; the organic groups bonded to the silicon atoms of said organohydrogensiloxane are selected from monovalent unsubstituted or substituted hydrocarbon radicals; and the concentration of said organohydrogensiloxane is sufficient to provide a molar ratio of silicon-bonded hydrogen atoms to alkenyl radicals in said composition of from 0.5 to 2; C. an amount of a catalyst sufficient to promote curing of said composition, wherein the curing catalyst is selected from platinum group metals or compounds of said metals and is present in said composition at a concentration equivalent to from 1 to 50 parts by weight of platinum group metal per million parts by weight of the combination of said polyorganosiloxane and said organohydrogensiloxane; and D. an adhesion promoting additive, characterized in that said additive is the organosilicon composition of claim 1. A composition according to claim 5 wherein g represents a degree of polymerization equivalent to a viscosity of from 0.1 to 10 Pa-s at 25°C. and said composition is packaged in at least two containers with said organohydrogensiloxane and said catalyst located in different containers.

Inventors: GENTLE THERESA EILEEN, LUTZ MICHAEL ANDREW, GENTLE, THERESA EILEEN, LUTZ, MICHAEL ANDREW
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1995
Main classification: C08K5
IPC codes: C08L83, B01J23, C08G77, C07F7