METHOD FOR MANUFACTURING CEMENT CLINKER IN A STATIONARY BURNING REACTOR

Abstract: The invention relates to a method for manufacturing cement clinker whereby the raw meal is initially subjected to preparatory processing, e.g. by comminution, homogenization and/or drying, and, eventually, nodulized and burned, with the nodulization process itself taking place in a stationary burning reactor. By the method according to the invention a sulphatic compound is added to the raw meal in a sufficient quantity before introducing the raw meal into the stationary burning reactor or directly into the stationary reactor, e.g. through the combustion air or together with the fuel. It is an essential requirement that the sulphate content of the calcined raw meal is considerably higher than the alkali oxide content.

Description: Method for manufacturing cement clinker in a stationary burning reactor. The present invention relates to a method for manufacturing cement clinker by which method the raw meal is subjected to preparatory processing, e.g. by comminution, homogenization and/or drying, whereafter the raw meal is preheated and calcined and, eventually, nodulized and burned, and where nodulization takes place in a stationary burning reactor. A stationary burning reactor is defined as a reactor with sta¬ tionary walls as opposed to a rotary kiln. The most prevalent types of stationary reactors are fluid bed or spouted bed reac¬ tors. Nodulization and clinkerization take place when the preheated and possibly calcined cement raw meal, subject to simultaneous input of heat and a consequential formation of a melting phase, is transformed from a particle-formed material with a fineness which is typically less than 15% in excess of 0.090 mm into a grained or ball-shaped material with a fineness of more than 80% in excess of 0.5 mm. In the general cement clinker manufacturing process, the formed melting phase is an oxide fusion which is formed at a tempera¬ ture of approximately 1300 β C and with a composition which is roughly as follows: 55% CaO, 6% Si0 2 , 23% A1 2 0 3 and 17% Fe 2 0 3 , and where the oxide fusion will normally constitute 15-25% of the total clinker mass. In the vast majority of existing manufacturing plants, clinkeri¬ zation takes place in a rotary kiln. Given that the costs of construction and the expenditure relating to the maintenance of the rotary kiln are very high because of the moving parts, numerous attempts have been made to eliminate the need for the rotary kiln in the cement manufacturing process. It is known practice, e.g. from the published German patent ap¬ plication No. 4219697, to manufacture cement clinker according to a method where the burning of the calcined material is effec- ted in two stages and where the first stage consists of a fluid bed or spouted bed. In this first stage the raw meal is heated to a presintering temperature, at which a melting phase is formed, and clinkerization is initiated once the melting phase 5 is present. The mate-rial is subsequently directed to the second stage where the clinker is eventually burned at a temperature of minimum 1300°C. However, practical implementation of this method is difficult 10 due to the fact that the melting phase formed occurs within a range of a few degrees, hence making it extremely difficult to maintain the process conditions necessary to ensure constant presence of a predetermined, small amount of melting phase. This may, in particular, pose problems since the amount of fused 15 material depends to a major degree on the composition of the raw meal, and not just on the temperature. In the U.S. patent application No. 2.465.420 a process is described for calcination and nodulization of calcareous sludge 20 using a salt fusion of alkali metals. Such a salt fusion is not always suitable for the manufacture of cement since an ex¬ cessively high content of alkali metals in the finished cement may give rise to the formation of expanding reaction products, which will lead to cracks in the finished concrete. 25 In Danish patent application No. 1579/85 is described a method for treatment of a used absorbent from a dry exhaust gas de- sulphurization process. Since, according to the method described in this application, presence of a certain amount of chlorides 30 is a precondition, it would not be advantageous to use this method for manufacturing cement clinker since chlorides may cause operational problems in the form of cakings in preheater and calciner. 35 It is prior art to add to the raw meal for manufacturing cement up to about 5% gypsum together with fluorine in order to lower the temperature at which C 3 S is formed, and hence also the bur¬ . ) ning temperature, but up to this point in time the nodulization and burning of these cements have been carried out in rotary kilns . By means of this invention a method is thus indicated for the manufacture of cement which will eliminate operational problems and the addition of unwanted substances, such as chlorides, while, at the same time, the nodulization and the burning of the clinker can be carried out in a stationary reactor, in which there are specific requirements with respect to the controlling of fused material formation. According to the invention, this is achieved by addition of a sulphatic compound to the raw meal in a sufficiently large quantity prior to the introduction of the raw meal into the stationary burning reactor or by addition of a sulphatic compound directly into the stationary reactor, e.g. through the combustion air or together with the fuel. It is surprising that the addition of a sulphatic compound, which does not necessarily itself have to be capable of melting, can cause a melting phase to be formed in the material in the stationary reactor and that the melting phase which is formed satisfies the requirement that it must be possible to regulate the extent of the melting phase by controlling the temperature. However, a temperature range exists between 1000 - 1300°C in which the added sulphate compound may be mixed with the natural content of alkali metals of the cement raw meal, forming a fusion which essentially consists of the added sulphate compound and a smaller quantity of alkali sulphates (K 2 S0 4 and Na 2 S0 4 ). In principle, the sulphatic compound may be selected among all types of sulphates which do not have any adverse effect on the quality of the finished cement. It would be particularly advantageous to use calcium sulphate, either naturally occurring or industrial by-products and regular waste materials, e.g. in the form of used absorbent from dry exhaust gas desulphuriza- tion. If the raw meal itself has a low content of alkali metals, a certain amount of the sulphate source can be added as alkali sulphate. Also, the sulphate compound may, to a certain extent, be introduced together with the fuel. It is a distinctive feature of this fusion that its quantity varies evenly with the temperature and that, to a major degree, it is independent of the sulphate content, as long as this content is sufficiently high. Optimum temperature conditions for nodulization of the calcined raw meal by means of this fusion exist within the temperature range 1100 - 1250". In order to carry out the method according to the invention it is an essential requirement, as mentioned in claim 1, that the sulphate content of the calcined raw meal is considerably higher than the alkali oxide content. It is preferable to ensure compliance with the following formula (the percentages indicated are percentages by weight): % S0 3 > %K 2 0 + 1.5 %Na 2 0 - where the S0 3 percentage is the total content of sulphate in the material streams into the process. The invention is explained in further details in the following with reference to the drawing which shows an example of a plant in which the method according to the invention can be used. This plant is, subject to few modifications, known from European patent No. 0380878 (December 14, 1989, F.L. Smidth & Co. , A/S). In the Figure is shown a plant for manufacturing of cement which comprises a preheater which consists of three preheater cyclones 1, 2 and 3, a calciner 4 with a separation cyclone 5, a statio¬ nary reactor 6, which is located below the calciner 4 and a unit 7 in which the final reaction of the clinker can take place, and a clinker cooler 8. The unit 7 may e.g. be a fluid bed chamber or a short rotary kiln. In operation, cement raw meal is fed to the plant through an inlet 9 and then conveyed in known manner through the preheater cyclones 1, 2 and 3 to the calciner 4 via a duct 10. The calciner 4 is fed with fuel via an inlet 11 and the sulphatic compound through an inlet 11a. Combustion air is added through one or several ducts 12 from the clinker cooler 8. In the calciner 4 the preheated raw meal is calcined in gas suspension and the suspension of exhaust gas and calcined raw meal is subsequently directed via an outlet 5a to the separation cyclone 5 from which the exhaust gas continues up through the preheater 1, 2 and 3, before it is eventually discharged through an outlet 13. The calcined raw meal is directed from the separation cyclone 5 down into the reactor 6 via a duct 14. The reactor 6 is provided with combustion air from the unit 7 through a duct 15 and with fuel via an inlet 16. The unit 7, to which the finished clinker is directed, is supplied with air and fuel to an extent necessary to allow the final reaction of the clinker to take place in an appropriate environment. Finally, the clinker passes via a duct 18 into the cooler 8. In the case where the reactor 6 is a spouted bed, the calcined raw meal will, when it is introduced via the duct 14, flow down along the conical walls in the lowermost part of the reactor 6. When the raw meal reaches the bottom of the conical part, the small particles will be entrained in the upward-flowing com¬ bustion air which is supplied via the duct 15. This will cause a spouted bed to be formed, in which the material is circulated in a characteristic pattern, with the material being converted into nodules with constantly increasing particle dimensions. When the particles have attained a weight which is such that the pull of the nodules exerted by the gravitational force is greater than the force which is generated by the upwardflowing gas, the finished nodules fall down through the conical part of the reactor and down through the duct 15 to the unit 7. In the unit 7, the generated nodules will have the necessary time to react so that the desired clinker minerals are formed. The size of the finished nodules depends on the gas volume which is drawn through the duct 15, and hence on the velocity of the gas. A test was carried out during which calcined raw meal was granulated in the reactor 6 without additional input of sulpha¬ te, exclusively using the raw meal's own oxide fusion. At a temperature of about 1325 β C it was possible to produce nodules, but it was unavoidable that a substantial part of the material was accumulated on the sides of the reactor chamber to such an extent that operation was not possible for more than 5 hours. This result is attributed to an excessive quantity of fused material during the granulation process. In a second test, the temperature was significantly reduced to about 1200"C. In the event, it emerged that the granulation process was brought to an almost complete standstill, with only sporadic quantities of nodules being discharged from the reactor 6. Instead, a violent circuit of material was established be tween calciner 4, separation cyclone 5 and the reactor 6. In a third test, 5 kg of finely ground gypsum was added per 100 kg raw meal to the calciner 4 via the inlet 11a and the tempera¬ ture in the reactor 6 was set for 1200 β C. After a certain time period, an equilibrium was established in the circuit between calciner 4, separation cyclone 5 and reactor 6, with granular material being discharged from the reactor through 15 in a flow stream equivalent to the input of raw materials at 9 and 11a. The manufactured cement clinker had a mean particle size of 3 mm.

Claims: P A T E N T C L A I M S 1. A method for manufacturing cement clinker by which method the raw meal is subjected to preparatory processing, e.g. by comminution, homogenization and/or drying, whereafter the raw meal is preheated and calcined and eventually nodulized and burned, and where nodulization takes place in a stationary unit CHARACTERIZED IN THAT during the preparatory processing, calcination or burning of the raw meal, a quantity of sulphatic compound, which do not have any adverse effect on the quality of the finished cement, is proportionately fed to the raw meal so that the sulphate content of the raw meal is considerably higher than the content of alkali oxide, and in that clinkerization takes place at a temperature between 1000°C and 1300°C. 2. A method according to claim 1 CHARACTERIZED IN THAT the temperature during clinkerization process ranges between 1100 β C and 1250 β C. 3. A method according to claim 1 CHARACTERIZED IN THAT it is an essential requirement that the content of sulphate in the raw meal mixture must be as follows: % SO, %K 2 0 1.5 %Na 2 0 4. A method according to claim 1 CHARACTERIZED IN THAT the sulphatic compound is a calcium sulphate.

Inventors: JOENS EBBE S, JOENS, EBBE, S.
Applicants: JOENS EBBE S, SMIDTH & CO AS F L, F.L. SMIDTH & CO. A/S, JOENS, EBBE, S.
Application year: 1995
Main classification: C04B7
IPC codes: C04B7