Monomer mixture for bonding substantially sheet-shaped elements

Abstract: The invention relates to a cast resin mixture for bonding substantially sheet-shaped elements, such as glass pane or the like, with a content of at least one non-functionalized acrylic and/or methacrylic ester and at least one functionalized alkyl ester of (meth)acrylic acid, optionally at least one plasticizer, optionally at least one cross-linking agent, optionally at least one primer and optionally at least one polymerization initiator. To improve this cast resin mixture in versatility of use and ease of handling, and to allow glass panes and the like to be bonded to one another reliably and durably, while optionally embedding function elements the acrylic and/or methacrylic ester(s) comprise(s) at least one constituent from the following group: all branched and unbranched saturated aliphatic (meth)acrylic esters, in particular methyl-, ethyl-, n-propyl-, iso-propyl-, n-butyl-, iso-butyl-, sec-butyl-, tert-butyl- and 2-ethyl-1-hexyl-(meth)acrylic esters. At least one functionalized alkyl ester of acrylic or methacrylic acid in the ester group includes at least one hydroxy- or amino- and/or epoxy-function, where the alkyl chains are saturated branched or saturated unbranched.

Description: Specification The invention relates to a monomer mixture for bonding substantially sheet-shaped elements, such as glass panes, with a content of at least one non-functionalized aliphatic acrylic or methacrylic ester and at least one functionalized alkyl ester of (meth)acrylic acid, optionally at least one plasticizer, optionally at least one cross-linking agent, optionally at least one primer and optionally at least one polymerization initiator, as well as its use. For numerous applications, for example for embedding solar cells for the production of solar modules or for production of the ion conducting layer of electrochromic pane arrangements, as are known from EP-B 0 083 988, but also for production of laminated safety glass panes, cast resin mixtures are desirable which, with greater ease of handling, evidence good durability with permanently high light transmission and are suitable for reliable bonding of components, such as glass panes, delimiting a pane interspace or the like which should be filled by the cast resin mixture. In a series of publications, such as DE-B 22 23 046, DE-B 24 16 991, DE-C 25 36 312 and DE-B 26 06 569 for example, cast resin mixtures or layers made thereof are known which as the principal components incorporate at least one non-functionalized acrylic or methacrylic ester and at least one functionalized alkyl ester of acrylic or methacrylic acid with at least one hydroxy or amino function in the ester group, where however provision is made for other components - in the case of with DE-B 22 23 046 a secondary or tertiary amine salt of an ethylene/acrylic acid mixture of polymers, in the case of DE-B 24 16 991 a titanium alkoxy compound, and in the case of DE-B 26 06 569 chain transfer agents containing acrylic acid and mercapto groups, in the case of DE-C 25 36 312 an additional mixture of polymers - which are not ideally suited for bonding glass panes, in particular embedding additional elements to be located between the glass panes, such as solar cells or the like. Nowadays, one prefers a cast-in-place technology, wherein the glass panes intended for the laminated glass are brought into position relative to one another by means of a spacer frame. The adhesive agent is then filled into the gap between the glass panes, for example by means of an injection syringe. This technique requires an adhesive agent having a viscosity as low as possible. If a resin is to be used, this must be diluted in any manner which, of course, does not contribute to ease of handling. For instance, the document DE-A 33 03 784 addresses ε-caprolactone as a diluting agent for a resin composition used for painting and printing purposes. Now, monomer mixtures are similar to water in their fluidity and are therefore basically suitable for cast-in-place-techniques. The monomer mixtures as disclosed in EP-A 0 119 525 may be employed in so far. It is the object of the invention to develop a monomer mixture of the generic type which is already known for the production of laminated safety glass panes such that, with versatility of use and ease of handling, glass panes and the like can be bonded to one another reliably and durably, while optionally embedding function elements. This problem is solved by the monomer mixtures of claims 1 and 17. It is preferred, that the ester of acrylic or methacrylic acid which includes a hydroxy function and an additional ester function can be formed by formal condensation of a hydroxy alkyl acrylate with a lactone. Provision can also be made for the hydroxyalkyl ester(s) to be selected from the group comprising 2-hydroxyethyl acrylate, 1-hydroxypropyl acrylate, 2-hydroxypropyl acrylate, 1,4-butanediol monoacrylate and 1,6-hexanediol monoacrylate. Also, the aminoalkyl ester(s) can be selected from the group comprising dimethylaminoethyl acrylate, diethylaminoethyl acrylate and tert-butylaminoethyl acrylate. It is preferred that said epoxyalkyl ester of acrylic or methacrylic acid is 2,3-epoxypropyl acrylate or 2,3-epoxypropyl methacrylate. Furthermore the invention provides for hydroxyalkyl acrylate to be selected from the group comprising 2-hydroxyethyl acrylate, 1-hydroxypropyl acrylate, 2-hydroxypropyl acrylate, 1,4-butanediol monoacrylate or 1,6-hexanediol monoacrylate. Provision can also be made for the lactone to be selected from the group of 4-, 5-, 6- or 7-membered ring lactones, such as β-butyrolactone, γ- or δ-valerolactone, γ-, δ- or ε-caprolactone. Here, provision can be made for the ester of acrylic or methacrylic acid which incorporates a hydroxy function and an additional ester function to be formed by formal condensation of an hydroxyalkylacrylate with a lacton, for example from a) 2-hydroxyethyl acrylate with ε-caprolactone resulting in 6-hydroxy-2'-[(1-oxo-2-propenyl)-oxy]-caproic acid ethylester, or b) 1,4-butanediol monoacrylate with 6-valerolactone resulting in 5-hydroxy-4'-[(1-oxo-2-propenyl)-oxy]-butyric acid butylester. The aforementioned component a) is represented by graphic formulae as follows: 2-hydroxyethyl acrylate + ε-caprolactone => 6-hydroxy-2'-[(1-oxo-2-propenyl)-oxy]-caproic acid ethylester The aforementioned component b) can be represented by graphic formulae as follows: 1,4-butanediol monoacrylate + δ-valerolactone => 5-hydroxy-4'-[(1-oxo-2-propenyl)-oxy]-butyric acid butylester A preferred embodiment provides that 2,3-epoxypropyl acrylate or 2,3-epoxypropyl methacrylate is used together with an ester of acrylic or methacrylic acid which includes a hydroxy function and an additional ester function which can be formed by formal condensation of a hydroxy alkyl acrylate with a lactone, for example from a) 2-hydroxyethyl acrylate with ε-caprolactone resulting in 6-hydroxy-2'-[(1-oxo-2-propenyl)-oxy]-caproic acid ethyl ester, or b) 1,4-butanediol monoacrylate with δ-valerolactone resulting in 5-hydroxy-4'-[(1-oxo-2-propenyl)-oxy]-butyric acid butylester. Furthermore, the invention provides for the ester of the acrylic or methacrylic acid which incorporates an amino function and an additional ester function to be formed by formal condensation of a hydroxyalkyl acrylate with a lactam. Provision can be made for the hydroxyalkyl acrylate to be selected from the group comprising 2-hydroxyethyl acrylate, 1-hydroxypropyl acrylate, 2-hydroxypropyl acrylate, 1,4-butanediol monoacrylate or 1,6-hexanediol monoacrylate. The invention also proposes that the lactam be selected from the group comprising 4-, 5-, 6- or 7-membered ring lactams, such as β-propiolactam, β- or γ-butyrolactam, γ- or δ-valerolactam and/or γ-, δ- and/or ε-caprolactam. Provision can also be made for the ester of the acrylic or methacrylic acid to incorporate an amino function and an additional ester function, can be formed, by formal condensation of a hydroxyalkyl acrylate with a lactam, for example from a) 2-hydroxyethyl acrylate with ε-caprolactam resulting in 6-amino-2'-[(1-oxo-2-propenyl)-oxy]-caproic acid ethylester, or of b) 1,4-butanediol monoacrylate or with δ-valerolactam resulting in 5-amino-4'[(1-oxo-2-propenyl)oxy]-butyric acid butylester. The aforementioned component a) can be represented by graphic formulae as follows: 2-hydroxyethyl acrylate + ε-caprolactam => 6-amino-2'-[(1-oxo-2-propenyl)-oxyl]-caproic acid ethylester The aforementioned component b) can be represented by graphic formulae as follows: 1,4-butanediol monoacrylate + δ-valerolactam => 5-amino-4'-[(1-oxo-2-propenyl)-oxy]-butyric acid butylester Provision can also be made for the ester of the acrylic or methacrylic acid which incorporates a hydroxy function and an additional amide function can be formed by formal condensation of an aminoalkyl acrylate with a lactone. Furthermore, the invention, as far as the monomer mixture of claim 16 is concerned, provides for the aminoalkyl acrylate to contain a primary or secondary amino group and to be selected from the group comprising 2-aminoethyl acrylate, 3-aminopropyl acrylate, 4-aminobutyl acrylate, 2-methylaminoethyl acrylate or 2-ethylaminoethyl acrylate. Provision can be made for the lactone being selected from the group comprising 4-, 5-, 6- or 7-membered ring lactones, such as β-propylactone, β- or γ-butyrolactone, γ- or δ-valerolactone, γ-, δ- and/or ε-caprolactone. The invention also proposes that the ester of the acrylic or methacrylic acid which incorporates a hydroxy function and an additional amide function can be formed by formal condensation of an amino alkyl acrylate with a lactone, for example from a) 2-aminoethyl acrylate with ε-caprolactone resulting in 6-hydroxy-2'-[(1-oxo-2-propenyl)-oxy] -caproic acid ethyl amide, or from b) 4-aminobutyl acrylate with δ-valerolactone resulting in 5-hydroxy-4'-[(l-oxo-2-propenyl)-oxy]-butyric acid butylamide. The aforementioned component a) can be represented by graphic formulae as follows: 2-aminoethyl acrylate + ε-caprolactone => 6-hydroxy-2'-[(1-oxo-2-propenyl)-oxy]-caproic acid ethylamide The aforementioned component b) can be represented by graphic formulae as follows: 4-aminobutyl acrylate + δ-valerolactone => 5-hydroxy-4'-[(1-oxo-2-propenyl)-oxy]-butyric acid butylamide Preferably, 2,3-epoxypropyl acrylate or 2,3-epoxypropyl methacrylate is used together with an ester of acrylic or methacrylic acid which includes a hydroxy function and an additional amide function which can be formed by formal condensation of an amino alkyl acrylate with a lactone, for example from a) 2-aminoethyl acrylate with ε-caprolactone resulting in 6-hydroxy-2'-[(1-oxo-2-propenyl)-oxy]-caproic acid ethyl ester, or from b) 4-aminobutyl acrylate with δ-valerolactone resulting in 5-hydroxy-4'- [(1-oxo-2-propenyl)oxy]-butyric acid butylamide. The invention also proposes that the proportion of functionalized alkyl ester of the acrylic or methacrylic acid is 5 to 25 mol%. Provision can also be made for the proportion of plasticizer(s) to be up to 30 mol%. Provision be made thereby for the proportion of plasticizer(s) to be a maximum of 25 mol%. Preferably, said plasticizer is selected from the group consisting of primary, secondary and/or tertiary alcohols carrying at least one OH group and mixtures thereof. The invention is further characterized in that said alcohol is selected from the group consisting of primary, secondary and/or tertiary aliphatic alcohols which are branched or unbranched and mixtures thereof. Examples are methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, sec-butyl alcohol, tert-butyl alcohol and higher homologues and mixtures thereof. The invention is also characterized in that said alcohol is selected from the group consisting of branched or unbranched diols, triols and alcohols comprising more than three OH groups and mixtures thereof. Examples are ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol, tetrapropylene glycol, 1,4-butane diol, 2,3-butane diol, 1,5-pentane diol, 1,6-hexane diol, 1,2,3-propane triol, trimethylol propane, pentaerythritol and mixtures thereof. Finally, the invention is characterized in that said alcohol is selected from the group consisting of saturated cyclic primary, secondary and/or tertiary alcohols and mixtures thereof. Examples are cyclopropanol, cyclobutanol, cyclopentanol, cyclohexanol, 1-cyclopropylethanol and mixtures thereof. The proportion of primary, secondary and/or tertiary alcohols carrying at least one OH group should be 0.01 to 5 mol%. The invention also provides for the proportion of non-functionalized aliphatic (meth)acrylic esters to be between 70 and 90 mol%. Provision can also be made thereby for the cross-linking agent(s) to incorporate at least one compound which possesses at least two acrylate or methacrylate groups per molecule, such as 1,4-butanediol diacrylate, 1,6-hexanediol diacrylate, ethylene glycol diacrylate, di-ethylene glycol diacrylate, tri-ethylene glycol diacrylate, propylene glycol diacrylate, di-propylene glycol diacrylate, tri-propylene glycol diacrylate, trimethylol propane triacrylate, ditrimethylol propane tetraacrylate, dipentaerythritol pentaacrylate and/or pentaerythritol tetraacrylate. The invention also proposes that the proportion of cross-linking agent be up to 10 mol%. The invention is furthermore characterized in that the proportion of cross-linking agent(s) be of 5 mol% at maximum. The invention can also be characterized in that the polymerization initiator proportion is 0.01 to 0.5 mol%. The invention can also be characterized in that the polymerization initiator proportion is 0.02 to 0.15 mol%. The invention can further be characterized in that said polymerization initiator is capable of initiating UV curing said cast resin mixture. The invention proposes that the polymerization initiator(s) be selected from the group incorporating hydroxycyclohexylphenylketone, 2-hydroxy-2-methylphenyl-1-propanone, 2,4,6-trimethylbenzoyldiphenyl phosphine oxide and/or ethyl-2,4,6-trimethylbenzoylphenylphosphinate. The invention is also characterized by a proportion of at least one primer of up to 5.00 mol%. The invention also makes provision for the proportion of the primer to be up to 2.00 mol%. The invention proposes that the primer be a silane. The invention is also characterized in that vinyl-tris(2-methoxy-ethoxy) silane, 3-acryloxypropyl-trimethoxysilane or 3-methacryloxypropyl-trimethoxysilane be used as silane. The subject of the invention is furthermore the use of the cast resin mixture for establishment of the ion conducting layer of an electrochromic pane arrangement. Furthermore, the object of the invention is also the use of the monomer mixture for embedding solar cells located between (glass) panes. Furthermore, the invention is also suitable for the production of laminated safety glass pane for vehicle or architectural glazing. Furthermore, the subject of the invention is also the use of the monomer mixture for the production of laminated glass panes with at least one individual plastic pane. Furthermore, the invention is also suitable for use for establishing a matrix for inorganic or organic redox systems, such as iodine/iodide. Finally the subject of the invention is also the use of the monomer mixture according to the invention as a matrix for acid or base-sensitive pigments. The monomer mixture according to the invention is therefore suitable in particular for embedding solar cells, as matrix for salts soluble in organic media, for example alkali salts, where, after addition of plasticizers, one obtains ionically conductive cast resins for electrochromic panes, as is the subject of German Patent Application P 44 17 220.6 of the same Application Date, and can be used as matrix for inorganic and organic redox systems, for example iodine/iodide, where such mixtures can be used as ionically conductive polymers with redox properties, with ionic conduction for both positive and negative charges. Ionically conductive redox polymer systems of this type are used in photoelectric cells. The cast resin mixture according to the invention can also be used for establishment of a plastic layer between two sheets, at least one of which is transparent, where the sheets can be of glass of other materials. Finally, attention should be drawn as an application for the cast resin mixture according to the invention to the establishment of a matrix for acid or base-sensitive pigments for the production of coloured glasses, glass infill panels, and curtain wall elements. Further advantages of the invention are stated in the Specification below, in which embodiments are described in detail: Example 1 A monomer mixture for production of solar modules with solar cells located between glass panes is composed as follows: Substance mass[g] weight% mol% n-butyl acrylate 50.0 48.23 54.77 2-ethylhexyl acrylate 20.0 19.37 15.30 6-hydroxy-2'-[(1-oxo-2-propenyl) -oxy]-caproic acid ethylester 10.0 9.69 6.12 1,4-butanediol monoacrylate 10.0 9.69 9.78 di-propylene glycol diacrylate 4.0 3.87 2.32 propylene carbonate 3.0 2.91 4.15 ethylene carbonate 4.0 3.87 6.40 primer (Silane GF 58) 2.0 1.94 1.01 initiator (Darocure 4263) 0.25 0.24 0.16 As polymerization initiator is used a substance available under the trade name Darocure 4263, consisting of 70 % Irgacure 1173 and 30 % Lucirin TPO. The substance available under the trade name Irgacure 1173 is 2-hydroxy-2-methylphenyl-1-propanone; that available under the trade name Lucirin TPO is 2,4,6-trimethylbenzoyldiphenyl phosphine oxide. Other especially suitable polymerization initiators according to the invention are a substance available under the trade name Irgacure 184, chemical name hydroxycyclohexyl phenyl ketone, a substance available under the trade name Darocure 4265, consisting of 50 % Irgacure 1173 and 50 % Lucirin TPO. Especially preferred is the use of either Darocure 4263 or Irgacure 184. Example 2 A monomer mixture for the production of an ion conducting layer for an electrochromic pane system corresponding to Patent Application P 44 17 220.6 is composed as follows: Substance mass[g] weight% mol% n-butyl acrylate 983 78.55 76.21 1,4-butanediol monoacrylate 24 1.92 1.66 propylene carbonate 185 14.78 17.99 lithium perchlorate 33 2.64 3.08 lithium bromide 1.2 0.10 0.14 tripropylene glycol diacrylate 24 1.92 0.86 initiator (Darocure 4263) 1.3 0.10 0.06 As silane, which can preferably be used as primer in the case of the cast resin mixture according to the invention, particularly suitable is vinyl-tris(2-methoxy-ethoxy) silane, which can be obtained under the trade name Silane GF 58 from Wacker-Chemie GmbH or Dynasilane VTMOEO from Huls AG. In the following, examples are given which use special alcohols as plasticizers. Example 3 235 g corresponding to 77.48 weight% or 74.50 mol% n-butyl acrylate, 10 g corresponding to 3.30 weight% or 2.82 mol% 1,4-butanediol monoacrylate, 45 g corresponding to 14.84 weight% or 17.91 mol% propylene carbonate, 3 g corresponding to 1.00 weight% or 0.92 mol% trimethylol propane, 10 g corresponding to 3.30 weight% or 3.81 mol% lithium perchlorate, and 0.3 g corresponding to 0.10 weight% or 0.04 mol% polymerization initiator, namely 2,4,6-trimethylbenzoyl diphenyl phosphine oxide, acting as UV initiator. Finally, two embodiments of the present invention are illustrated in which the substance 2,3-epoxypropyl acrylate is used. Example 4 85 g corresponding to 83.25 weight% or 83.80 mol% n-butyl acrylate, 10 g corresponding to 9.79 weight% or 10.81 mol% hydroxyethyl acrylate, 5 g corresponding to 4.90 weight% or 4.90 mol% 2,3-epoxypropyl acrylate, 2 g corresponding to 1.96 weight% or 0.95 mol% 3-methacryloxypropyl trimethoxysilane, and 0.1 g corresponding to 0.10 weight% or 0.04 mol% polymerization initiator, namely 2,4,6-trimethylbenzoyl diphenyl phosphine oxide, acting as UV initiator. Example 5 60 g corresponding to 58.77 weight% or 61.43 mol% n-butyl acrylate, 20 g corresponding to 19.59 weight% or 20.48 mol% tert-butyl acrylate, 10 g corresponding to 9.79 weight% or 9.10 mol% 1,4 butandiolmonoacrylate, 5 g corresponding to 4.90 weight% or 5.12 mol% 2,3-epoxypropyl acrylate, 5 g corresponding to 4.90 weight% or 2.85 mol% 6-hydroxy-2'-[(1-oxo-2-propenyl)-oxy]-caproic acid ethylester, 2 g corresponding to 1.96 weight% or 0.99 mol% 3-methacryloxypropyl trimethoxysilane, and 0.1 g corresponding to 0.10 weight% or 0.04 mol% polymerization initiator, namely 2,4,6-trimethylbenzoyl diphenyl phosphine oxide, acting as UV initiator.

Claims: Monomer mixture to be used as casting mass for bonding substantially sheet-shaped elements, such as glass panes, comprising a) 60-99 mol% of at least one non-functionalized acrylic and/or methacrylic ester having an alkyl group in their alcohol moiety selected from the group comprising all saturated branched or unbranched isomers with up to 8 carbon atoms, in particular methyl-, ethyl-, n-propyl- , iso-propyl-, n-butyl-, iso-butyl-, sec-butyl-, tert-butyl-, and 2-ethyl-1-hexyl-(meth)-acrylic esters and b) 0,5 - 30 mol% of at least one functionalized alkyl ester of (meth)acrylic acid containing in the alcohol moiety at least one hydroxy, amino and/or epoxy function, and additionally including at least one further ester or amide function, wherein the alkyl chains are saturated branched and/or unbranched, c) optionally at least one plasticizer, d) optionally at least one cross-linking agent, e) optionally at least one primer and f) optionally at least one polymerization initiator. Monomer mixture in accordance with claim 1, characterized in that the ester of acrylic or methacrylic acid which includes a hydroxy function and an additional ester function can be formed by formal condensation of a hydroxy alkyl acrylate with a lactone. Monomer mixture in accordance with claim 2, characterized in that the hydroxyalkyl acrylate is selected from the group comprising 2-hydroxyethyl acrylate, 1-hydroxypropyl acrylate, 2-hydroxypropyl acrylate, 1,4-butanediol monoacrylate or 1,6-hexanediol monoacrylate. Monomer mixture in accordance with claims 2 and 3, characterized in that the lactone is selected from the group of 4-, 5-, 6- or 7-membered ring lactones, such as β-propiolactone, β- or γ-butyrolactone, γ- or δ-valerolactone, γ-, δ- or ε-caprolactone. Monomer mixture in accordance with one of claims 2 to 4, characterized in that the ester of acrylic or methacrylic acid which incorporates a hydroxy function and an additional ester function can be formed by formal condensation of a hydroxyalkyl acrylate with a lactone, for example from a) 2-hydroxyethyl acrylate with ε-caprolactone resulting in 6-hydroxy-2'-[(1-oxo-2-propenyl)-oxy]-caproic acid ethylester, or b) 1,4-butanediol monoacrylate with δ-valerolactone resulting in 5-hydroxy-4'-[(1-oxo-2-propenyl)-oxy]-butyric acid butylester. Monomer mixture in accordance with one of claims 1 to 5, characterized in that 2,3-epoxypropyl acrylate or 2,3-epoxypropyl methacrylate is used together with an ester of acrylic or methacrylic acid which includes a hydroxy function and an additional ester function which can be formed by formal condensation of a hydroxyalkyl acrylate with a lactone for example from a) 2-hydroxyethyl acrylate with ε-caprolactone resulting in 6-hydroxy-2'-[(1-oxo-2-propenyl)-oxy]-caproic acid ethylester, or b) 1,4-butanediol monoacrylate with 6-valerolactone resulting in 5-hydroxy-4'-[(1-oxo-2-propenyl)-oxy]-butyric acid butylester. Monomer mixture in accordance with one of claims 1 to 6, characterized in that the ester of the acrylic or methacrylic acid which incorporates an amino function and an additional ester function can be formed by formal condensation of a hydroxyalkyl acrylate with a lactam. Monomer mixture in accordance with claim 7, characterized in that the hydroxyalkyl acrylate is selected from the group comprising 2-hydroxyethyl acrylate, 1-hydroxypropyl acrylate, 2-hydroxypropyl acrylate, 1,4-butanediol monoacrylate or 1,6-hexanediol monoacrylate. Monomer mixture in accordance with claim 7, characterized in that the lactam is selected from the group comprising 4-, 5-, 6- or 7-membered ring lactams, such as β-propiolactam, β- or γ-butyrolactam, γ- or δ-valerolactam and/or γ-, δ- and/or ε-caprolactam. Monomer mixture in accordance with claims 7 to 9, characterized in that the ester of the acrylic or methacrylic acid which includes an amino function and an additional ester function, can be formed by formal condensation of an hydroxyalkylacrylate with a lactam, for example from a) 2-hydroxyethyl acrylate with ε-caprolactam resulting in 6-amino-2'-[(1-oxo-2-propenyl)-oxy]-caproic acid ethylester, or of b) 1,4-butanediol monoacrylate with δ-valerolactam resulting in 5-amino-4'-[(1-oxo-2-propenyl)-oxy]-butyric acid butylester. Monomer mixture in accordance with one of claims 1 to 10, characterized in that the ester of the acrylic or methacrylic acid which includes a hydroxy function and an additional amide function can be formed by formal condensation of an aminoalkyl acrylate with a lactone. Monomer mixture in accordance with claim 11, characterized in that the aminoalkyl acrylate contains a primary or secondary amino group and is selected from the group comprising 2-aminoethyl acrylate, 3-aminopropyl acrylate, 4-aminobutyl acrylate, 2-methylaminoethyl acrylate or 2-ethylamino ethyl acrylate. Monomer mixture in accordance with claim 11, characterized in that the lactone is selected from the group comprising 4-, 5-, 6- or 7-membered ring lactones, such as β-propiolactone, β- or γ-butyrolactone, γ- or δ-valerolactone, γ-, δ-and/or ε-caprolactone. Monomer mixture in accordance with one of claims 11 to 13, characterized in that the ester of the acrylic or methacrylic acid which incorporates a hydroxy function and an additional amide function can be formed by formal condensation of an aminoalkyl acrylate with a lactone, for example from a) 2-aminoethyl acrylate with ε-caprolactone resulting in 6-hydroxy-2'-[(1-oxo-2-propenyl)-oxy]-caproic acid ethyl amide, or from b) 4-aminobutyl acrylate with δ-valerolactone resulting in 5-hydroxy-4'-[(1-oxo-2-propenyl)-oxy]-butyric acid butylamide. Monomer mixture in accordance with one of claims 1 to 14, characterized in that 2,3-epoxypropyl acrylate or 2,3-epoxypropyl methacrylate is used together with an ester of acrylic or methacrylic acid which includes a hydroxy function and an additional amide function which can be formed by formal condensation of an amino alkyl acrylate with a lactone, for example from a) 2-aminoethyl acrylate with ε-caprolactone resulting in 6-hydroxy-2'-[(1-oxo-2-propenyl)-oxy]-caproic acid ethyl amide, or from b) 4-aminobutyl acrylate with δ-valerolactone resulting in 5-hydroxy-4'-[(1-oxo-2-propenyl)oxy]-butyric acid butylamide. Monomer mixture in accordance with one of the preceding claims, characterized in that the proportion of plasticizer(s) is up to 30 mol%. Monomer mixture to be used as casting mass for bonding substantially sheet-shaped elements, such as glass panes, comprising a) 66-90 mol% of at least one non-functionalized acrylic and/or methacrylic ester having a hydroxyl substituent from the group comprising all saturated branched or unbranched isomers with up to 8 carbon atoms, in particular methyl-, ethyl-, n-propyl-, iso-propyl-, n-butyl-, iso-butyl-, sec-butyl-, and tert-butyl-, 2-ethyl-1-hexyl-(meth)acrylic esters and b) 0,5 - 30 mol% of at least one functionalized alkyl ester of (meth)acrylic acid containing in the alcohol moiety at least one hydroxy, amino and/or epoxy function, wherein the alkyl chains are saturated branched and/or unbranched, and c) up to 30 mol% of at least one plasticizer, selected from the group comprising propylene carbonate, ethylene carbonate, γ-butyrolactone, N-methylpyrrolidone, 1,3-dimethyl-2-imidazolidinone, 3-methyl-2-oxazolidinone, dimethylformamide, dimethylsulphoxide, dimethoxyethane and diethylene glycol-monomethylether, as well as mixtures of at least two of the aformentioned compounds, d) optionally at least one cross-linking agent, e) optionally at least one primer and f) optionally at least one polymerization initiator. Monomer mixture in accordance with claim 17, characterized in that the proportion of plasticizer(s) is 25 mol% at maximum. Monomer mixture in accordance with one of the preceding claims, characterized in that said plasticizer is selected from the group consisting of primary, secondary and/or tertiary alcohols carrying at least one OH group and mixtures thereof. Monomer mixture in accordance with claim 19, characterized in that said alcohol is selected from the group consisting of primary, secondary and/or tertiary aliphatic alcohols which are branched or unbranched and mixtures thereof. Monomer mixture in accordance with claim 20, characterized in that said aliphatic alcohol is selected from the group consisting of methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, sec-butyl alcohol, tert-butyl alcohol and higher homologues and mixtures thereof. Monomer mixture in accordance with claim 19, characterized in that said alcohol is selected from the group consisting of branched or unbranched diols, triols and alcohols comprising more than three OH groups and mixtures thereof. Monomer mixture in accordance with claim 22, characterized in that said alcohol is selected from the group consisting of ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol, tetrapropylene glycol, 1,4-butane diol, 2,3-butane diol, 1,5-pentane diol, 1,6-hexane diol, 1,2,3-propane triol, trimethylol propane, pentaerythritol or the like and mixtures thereof. Monomer mixture in accordance with claim 19, characterized in that said alcohol is selected from the group consisting of saturated cyclic primary, secondary and/or tertiary alcohols and mixtures thereof. Monomer mixture according to claim 24, characterized in that said alcohol is selected from the group consisting of cyclopropanol, cyclobutanol, cyclopentanol, cyclohexanol, 1-cyclopropylethanol or the like and mixtures thereof Monomer mixture according to one of claims 19 to 25, characterized in that the proportion of primary, secondary and/or tertiary alcohols carrying at least one OH group is 0.01 to 5 mol%. Monomer mixture in accordance with claim 1 or claim 17, characterized in that the proportion of non-functionalized aliphatic (meth)acrylic esters is between 70 and 90 mol%. Monomer mixture in accordance with one of the preceding claims, characterized in that the hydroxyalkyl ester(s) is/are selected from the group comprising 2-hydroxy- ethyl acrylate, 1-hydroxypropyl acrylate, 2-hydroxypropyl acrylate, 1,4-butanediol monoacrylate and 1,6-hexanediol monoacrylate. Monomer mixture in accordance with one of the preceding claims, characterized in that the aminoalkyl ester(s) is/are selected from the group comprising dimethylaminoethyl acrylate, diethylaminoethyl acrylate and tert-butylaminoethyl acrylate. Monomer mixture in accordance with one of the preceding claims, characterized in that said epoxyalkyl ester of acrylic or methacrylic acid is 2,3-epoxypropyl acrylate or 2,3-epoxypropyl methacrylate. Monomer mixture in accordance with claim 1 or claim 17, characterized in that the proportion of functionalized alkyl ester of the acrylic or methacrylic acid is 5 to 25 mol%. Monomer mixture in accordance with one of the preceding claims, characterized in that the cross-linking agent(s) incorporate(s) at least one compound which possesses at least two acrylate or methacrylate groups per molecule, such as 1,4-butanediol diacrylate, 1,6-hexanediol diacrylate, ethylene glycol diacrylate, diethylene glycol diacrylate, tri-ethylene glycol diacrylate, propylene glycol diacrylate, di-propylene glycol diacrylate, tri-propylene glycol diacrylate trimethylol propane triacrylate, ditrimethylol propane tetraacrylate, dipentaerythritol pentaacrylate and/or pentaerythritol tetraacrylate. Monomer mixture in accordance with one of the preceding claims, characterized in that the proportion of cross-linking agent is up to 10 mol%. Monomer mixture in accordance with claim 33, characterized in that the proportion of cross-linking agent(s) is 5 mol% at maximum. Monomer mixture in accordance with one of the preceding claims, characterized in that the polymerization initiator proportion is 0.01 to 0.5 mol%. Monomer mixture in accordance with claim 35, characterized in that the polymerization initiator proportion is 0.02 to 0.15 mol%. Monomer mixture in accordance with one of the preceding claims, characterized in that said polymerization initiator is capable of initiating UV curing said monomer mixture. Monomer mixture in accordance with one of the preceding claims, characterized in that the polymerization initiator(s) is/are selected from the group comprising hydroxycyclohexylphenylketone, 2-hydroxy-2-methylphenyl-1-propanone, 2,4,6-trimethylbenzoyldiphenyl phosphine oxide and/or ethyl-2,4,6-trimethylbenzoylphenylphosphinate. Monomer mixture in accordance with one of the preceding claims, characterized by a proportion of at least one primer of up to 5.00 mol%. Monomer mixture in accordance with claim 38, characterized in that the proportion of the primer is up to 2.00 mol%. Monomer mixture in accordance with claim 39 or 40, characterized in that the primer is a silane. Monomer in accordance with claim 41, characterized in that vinyl-tris(2-methoxy-ethoxy) silane, 3-acryloxypropyltrimethoxysilane or 3-methacryloxypropyl-trimethoxysilane is used as silane. Use of the monomer mixture in accordance with one of claims 1 to 42 for establishment of the ion conducting layer of an electrochromic pane arrangement. Use of the monomer mixture in accordance with one of claims 1 to 42 for embedding solar cells located between (glass) panes. Use of the monomer mixture in accordance with one of claims 1 to 42 for the production of laminated safety glass pane for vehicle or architectural glazing. Use of the monomer mixture in accordance with one of claims 1 to 42 for the production of laminated glass panes with at least one individual plastic pane. Use of the monomer mixture in accordance with one of claims 1 to 42 for establishing a matrix for inorganic or organic redox systems, such as iodine/iodide. Use of the monomer mixture in accordance with one of claims 1 to 42 as a matrix for acid- or base-sensitive pigments.

Inventors: BATCHELOR RICHARD ANDERS DR, JOEDICKE DIRK DR, MARQUART REINHOLD DR, BATCHELOR, RICHARD ANDERS, DR., JOEDICKE, DIRK, DR., MARQUART, REINHOLD, DR., Jödicke, Dirk, Dr.
Applicants: FLACHGLAS AG, FLACHGLAS AKTIENGESELLSCHAFT
Application year: 1995
Main classification: C09J4
IPC codes: G02F1