Plastic fats and chocolate

Abstract: A plastic fat which comprises not less than 50% by weight of LUS triglycerides, less than 10% by weight of triglycerides having the number of a total carbon atoms of constituent fatty acids (hereinafter abbreviated as TGC) of not more than 40 and less than 35% by weight of triglycerides having TGC of not less than 56 improves plasticity and reduces stickiness when used as a fat ingredient of plastic chocolate.

Description: The present invention relates to fats and chocolate having improved plasticity. The term "chocolate" is not limited to that prescribed by any law or standard and includes any chocolate and other fat processed products containing cacao butter substitutes. Most popular chocolate products are bar chocolate and cover chocolate for coating confectionery. However, in addition to them, there has been known so-called plastic chocolate which is produced by providing design to chocolate after cooling and solidification thereof and is mainly used for decoration of confectionery and cakes as ornament. For plastic chocolate, moldability and plasticity are required and, in order to provide chocolate with such properties, in general, a water-containing material such as a liquid sugar is added. However, chocolate using a liquid sugar has undesirable flavor and mouthfeel and fat blooming type appearance is caused due to evaporation of water during storage with time. In addition, there is a problem that the chocolate becomes sticky. As another method for providing chocolate with plasticity, addition of a liquid oil to a fat ingredient of chocolate has been employed. However, there is a problem that, for example, formation of cracking or breakage of chocolate is caused even by application of a slight distortion to chocolate after solidification and it is difficult to provide chocolate with sufficient plasticity by this method. Furthermore, in JP-A 5-211841, chocolate is provided with plasticity after solidification by addition of cacao butter and soybean oil to a di-saturated-monolinoleate. However, the chocolate has insufficient shaperetention at 26°C or higher because of addition of a liquid oil to the middle melting point fraction and is sticky and therefore it is required to use a high melting point ingredient together with them. Thus, fats and chocolate having excellent plasticity but free from stickiness has not been reported heretofore in the prior art. The main object of the present invention is to provide fats and chocolate having excellent plasticity with minimized stickiness. This object as well as other objects and advantages of the present invention will become apparent to a person skilled in the art from the following description. The present inventors have studied intensively to obtain fats and chocolate having excellent plasticity with minimized stickiness. As a result it has been found that triglycerides composed of long chain fatty acid, unsaturated fatty acid and short chain fatty acid residues (hereinafter referred to as LUS triglycerides, provided that the positions of the residues are not limited to specific ones) have excellent plasticity. In the LUS triglycerides used herein, the long chain fatty acid (L) represents C20:0 fatty acid (arachic acid), C22:0 fatty acid (behenic acid) or C24:0 fatty acid (lignoceric acid); the unsaturated fatty acid (U) represents C18:1 fatty acid (oleic acid or its isomer) or C18:2 fatty acid (linoleic acid or its isomer); and the short chain fatty acid (S) represents C4:0 (butyric acid). That is, according to the present invention, there is provided a plastic fat which comprises not less than 50% by weight of LUS triglycerides, less than 10% by weight of triglycerides having the number of a total carbon atoms of constituent fatty acids (hereinafter abbreviated as TGC) of not more than 40 and less than 35% by weight of triglycerides having TGC of not less than 56. The present invention also provides chocolate comprising the above plastic fat as its fat ingredient. Production of the LUS triglycerides is not limited to a specific process but, in general, they can be produced by subjecting triglycerides having L, U or S as their constituent fatty acids and L, U or S fatty acids other than the above constituent fatty acids or their mono- or trihydric alcohol esters to interesterification and, if necessary, fractionating and separating high melting point and/or low melting point fractions. Typically, the LUS triglycerides can be obtained by subjecting oils rich in oleic acid and linoleic acid together with C20:0, C22:0 and C24:0 esters and butyrate to interesterification. Examples of oils rich in oleic acid include high oleic sunflower oil and olive oil. Examples of oils rich in linoleic acid include safflower oil, sunflower oil, corn oil, rapeseed oil and soybean oil. Examples of esters of C20:0, C22:0 and C24:0 fatty acids include their methyl and ethyl esters. Examples of butyrate include ethyl butyrate and methyl butyrate. The catalyst to be used for interesterification is not limited to a specific one and, normally, an alkali metal catalyst such as sodium methylate or a lipase having 1,3-position specificity can be used. SUS, SUU and UUU (low melting point fats) as well as LUL and LUU (high melting point fats) are formed during interesterification as by-products. In the present invention, among the low melting point fats, the content of triglycerides having TGC of 40 or less should be less than 10% by weight, i.e., < 10% by weight. The content of triglycerides having TGC of 56 or more should be less than 35% by weight, i.e., < 35% by weight. When the content of triglycerides having TGC of 40 or less is not less than 10% by weight, plasticity is lowered and, at the same time, thermal resistance is lowered. On the other hand, when the content of triglycerides having TGC of 56 or more is not less than 35% by weight, plasticity is lowered and, at the same time, melting properties in the mouth of chocolate using such fat are degraded. Such by-products can be removed by a known fractionation method such as pressurized filtration fractionation, and solvent fractionation. Solvent fractionation is advantageous to industrial production. From the economical viewpoint and by taking into consideration fractionation ability, it is preferred to conduct the fractionation so that the amount of LUS triglycerides becomes 50 to 80% by weight based on the total weight of the interesterified fat. The interesterified fat thus obtained can be used as it is as the plastic fat of the present invention. Alternatively, any other suitable fat or oil can be added to the interesterified fat while maintaining the above triglyceride composition, or it is subjected to hydrogenation to adjust its melting point. The plastic fat of the present invention has excellent plasticity and can be used as a substantial fat ingredient of chocolate production to utilize its excellent plasticity. By substantial fat ingredient as used herein is meant that the chocolate contains the plastic fat of the present invention in an amount of 70% by weight or more of the total fat ingredients of the chocolate. The chocolate of the present invention can be produced according to a conventional method. That is, in addition to the plastic fat of the present invention, the chocolate can contain conventional ingredients, for example, cocoa, sugars, powdered sugar, emulsifying agents, flavoring agents and coloring agents. In addition, for example, nut powder such as almond powder, peanut butter and grated cheese can be used instead of cacao ingredient to provide a flavor other than chocolate. Furthermore, so-called colored chocolate obtained by coloring a white chocolate base can be produced. Chocolate can be produced by cooling and solidifying a molten mixture of refined raw materials according to a conventional method. A tempering operation is not required. The chocolate thus obtained has good flavor and mouthfeel with minimized stickiness and also has excellent plasticity such as bending property. Thereafter, any desired design can be readily provided for a particular purpose by changing the shape to the desired one by, for example, extrusion molding or rolling with a rolling pin or roller or whittling. For example, chocolate may be molded into a sheet. The sheet can be punched out in the shape of a leaf, followed by curving it to obtain an ornament, it can be shaped as roses or it can be placed on a side wall of cake. Alternatively, several sheets of chocolate having different colors can be laminated and shaped, for example, into a roll or eddy. Additionally, the chocolate can be extrusion-molded into the shape of a bar containing a center having a different shape and extending through the bar. The following Examples and Comparative Examples further illustrate the present invention in detail but are not to be construed to limit the scope thereof. In the Examples and Comparative Examples, all percents and parts are by weight. Example 1 Deacidified high oleic sunflower oil (38 parts) and behenic acid ethyl ester (62 parts) were interesterified with a lipase having 1,3-specificity and the ethyl ester part was distilled off. The resultant triglyceride fraction was subjected to hexane single stage fractionation to remove a low melting point fraction to obtain LUL fraction. This LUL fraction (85 parts) and ethyl butyrate (15 parts) were interesterified with the same lipase and the ethyl ester part was distilled off. The resultant triglyceride fraction was subjected to hexane-acetone double stage fractionation to obtain the LUS triglyceride fraction (middle melting point fraction), yield: 17.4%, LUS content: 79.3%, iodine value (IV): 39.6, softening melting point: 27.5°C. Example 2 The middle melting point fraction obtained in Example 1 was hydrogenated to obtain a hardened oil having softening melting point of 33.0°C and IV of 31.0. Example 3 The yield of the hexane-acetone double stage fractionation of Example 1 was changed to 21.3% to obtain an LUS triglyceride fraction (middle melting point fraction), LUS content: 53.2%, IV: 33.7, softening melting point: 33.9°C. Example 4 Deacidified high oleic sunflower oil (38 parts), behenic acid ethyl ester (47 parts) and ethyl butyrate (15 parts) were interesterified with a lipase having 1,3-specificity and the ester part was distilled off. The resultant crude LUS triglycerides (38 parts), behenic acid ethyl ester (47 parts) and ethyl butyrate (15 parts) were interesterified with the same lipase again and the ester part was distilled off. The resultant triglyceride fraction was subjected to hexane-acetone double stage fractionation to obtain an LUS triglyceride fraction (middle melting point fraction), yield: 44.8%, LUS content: 63.6%, IV 35.7. This middle melting point fraction was hydrogenated to obtain a hardened oil having softening melting point of 31.9°C and IV of 28.1. Comparative Example 1 The interesterified oil prior to subjecting hexane-acetone fractionation in Example 4 was used, LUS content: 39.3%, SUS+SUU content: 13.6%, LUU+LUL content: 39.7%, IV: 31.4. Comparative Example 2 Safflower oil (20 parts) and ethyl stearate (80 parts) were interesterified with a lipase having 1,3-specificity and the ethyl ester part was distilled off. The triglyceride fraction was subjected to acetone single stage fractionation to obtain a high melting point fraction, yield: 60.0%. This high melting point fraction (50 parts), cacao butter (20 parts) and soybean oil (30 parts) were mixed, IV: 71.6. This high melting point fraction was mainly composed of 1,3-stearyl-2-linoleate which corresponded to the fat used in the plastic chocolate of JP-A 5-211841. The compositions of fats thus obtained are summarized in Table 1. TGC of Examples 1-3 and Comparative Examples 1-2 TGC Examples 1,2 Example 3 Example 4 Comp. Example 1 Comp. Example 2 40 (SUU) or less 7.1% 5.3% 7.4% 13.6% 0.0% 42 (LUS) 5.3 2.8 4.4 4.9 0.0 44 (LUS) 72.5 45.9 56.3 31.6 0.0 46 (LUS) 1.5 4.5 2.9 2.8 0.0 48 1.0 7.0 2.1 4.0 0.4 50 0.2 1.2 0.5 0.5 7.3 52 0.6 0.5 0.6 0.9 26.5 54 1.9 1.0 1.0 2.0 64.5 56 (LUU) 1.3 7.2 2.6 2.5 1.2 58 (LUU, LUL) 5.8 7.3 16.0 10.4 0.1 60 (LUU,LUL) 0.8 5.4 2.5 5.2 0.0 62 (LUL) or more 2.0 11.9 3.7 21.6 0.0 Chocolate test The fats obtained in Examples 1-4 and Comparative Examples 1 and 2 were used as test fats to produce chocolate and subjected to the following test. The formulation of the chocolate was cocoa powder (8.0 parts), whole milk powder (10.0 parts), skimmed milk powder (12.0 parts), powdered sugar (35.0 parts), test fat (35.0 parts) lecithin (0.4 part), vanillin (0.02 part) and flavor (0.02 part). No tempering operation was carried out and the chocolate was shaped in a sheet having 5 cm sides and 2 mm thickness and a bar of 6 cm x 2 cm and 5 mm thickness. The chocolate was cooled and solidified at 5°C for 30 minutes. Plasticity was tested by bending both ends of the above sheet-shaped chocolate with the hands so that the tangent angle of both end surfaces became 90° and observing cracking. A sticking test was carried out by maintaining the chocolate at 50°C, covering surfaces of biscuit, cooling and solidifying at 5°C for 30 minutes, aging at 20°C for 1 week and then allowing to stand at 26, 27 or 28°C for 2 hours to evaluated sticking with fingers according to the following criteria: A: no sticking B: slightly sticking C: sticking Likewise, melting in mouth was evaluated after aging at 20°C for 1 week. The results are shown in Table 2. Test fat Plasticity Sticking Melting in mouth 26°C 27°C 28°C Ex. 1 no cracking A B B very good Ex. 2 no cracking A A A very good Ex. 3 no cracking A A A good Ex. 4 no cracking A A A good Comp. Ex. 1 cracking A A A bad Comp. Ex. 2 no cracking C C C very good As seen from Table 2, the chocolate using the test fat of Comparative Example 1 wherein the LUS triglyceride content is relatively low (39.3%), the content of triglycerides having TGC of not more than 40 is relatively large (13.6%) and containing a large amount of triglycerides having TGC of not less than 56 (39.7%) shows cracking and inferior plasticity. Although the chocolate using the test fat of Comparative Example 2 mainly composed of 1,3-stearyl-2-linoleate does not show cracking and has good plasticity, it shows sticking at 26°C. To the contrary, the chocolates using the test fats of Examples 1 to 4 do not have such problems. Thus, it has been demonstrated that plasticity and sticking are improved by adjusting the triglyceride composition of a fat ingredient of chocolate to the specified range. As described hereinbefore, according to the present invention, chocolate which requires no tempering operation and has improved moldability and plasticity as well as good flavor and mouthfeel without stickiness can be obtained.

Claims: A plastic fat which comprises not less than 50% by weight of LUS triglycerides, less than 10% by weight of triglycerides having the number of a total carbon atoms of constituent fatty acids (hereinafter abbreviated as TGC) of not more than 40 and less than 35% by weight of triglycerides having TGC of not less than 56, wherein L represents a residue of 20:0 fatty acid (arachic acid), C 22:0 fatty acid (behenic acid) or C 24:0 fatty acid (lignoceric acid); U represents a residue of C 18:1 fatty acid (oleic acid or its isomer) or C 18:2 fatty acid (linoleic acid or its isomer); and S represent is the residue of C 4:0 (butyric acid). The plastic fat according to claim 1, wherein the content of LUS triglycerides is 50 to 80% by weight. Chocolate comprising the plastic fat according to claim 1 as its fat ingredient. The chocolate according to claim 3, wherein the content of the plastic fat is not less than 70% by weight based on the total weight of the fat ingredient. Confectionery and cakes when comprising the chocolate as claimed in claim 3 or claim 4.

Inventors: NISHIMOTO TSUGIO, YAMADA KAZUHISA, NISHIMOTO, TSUGIO, YAMADA, KAZUHISA
Applicants: FUJI OIL CO LTD, FUJI OIL COMPANY, LIMITED
Application year: 1995
Main classification: A23D9
IPC codes: A23G1, A23G3, A23D9, C11C3, C11B7