THERMOSTABLE AND BIOLOGICALLY SOLUBLE FIBRE COMPOSITIONS

Abstract: Thermostable and biologically soluble man-made vitreous fibres obtainable from a melt having a low liquidus temperature and a low crystallisation rate comprising SiO2: 48-64 % by weight, Al2O3: 0.3-4 % by weight, FeO: 6-10 % by weight, CaO: 10-35 % by weight, MgO: 7-20 % by weight, Na2O: 0-10 % by weight, K2O: 0-6 % by weight, the ratio of (Na2O + K2O + 0.1.CaO) to (MgO + FeO) being > 0.15 and (MgO + FeO) being greater than 14 % by weight and (Na2 + K2O) being less than or equal to 10 % by weight.

Description: THERMOSTABLE AND BIOLOGICALLY SOLUBLE FIBRE COMPOSITIONS The present invention relates to thermostable man-made vitreous fibres (MMV fibres) and more specifically to thermostable MMV fibres which are soluble in biological fluids. The present invention also relates to products, such as insulation products and plant growth media made from such fibres as well as to fibres useful for re¬ inforcement or as fillers. MMV fibre insulation products are widely used and have been commer¬ cial products for a long period of time. The insulation products are made from raw materials which are melted and spun into fibres. Such products also comprise a binder, which holds the fibres together. The binder is usually a phenol -formaldehyde resin or a urea-modified phenol -formaldehyde resin. It is well known that rock and slag based fibre insulation products present the advantage compared to glass fibre insulations products that they exhibit a higher fire resistance, i.e. an improved thermo- stability. Typically, glass wool withstands temperatures up to around 650°C whereas stone wool is capable of withstanding tempera¬ tures up to about 1000°C. It is highly desirable to maintain this excellent property in any modification of the hitherto known rock or slag based fibre products. Recently, more attention has been put to health issues associated with various fibrous materials, including MMV fibres. It is well known that inhalation of certain types of fibres such as asbestos fibres may lead to respiratory diseases, including lung cancer. It is believed that an important factor is the tendency of the asbestos fibres to remain in the lung for extended periods of time. Although there has not yet been provided any evidence of MMV fibres being the cause of respiratory or other diseases in man, it is desirable to provide MMV fibres with an increased dissolution rate in biological fluids in order to reduce their half-time in the lungs upon inhala¬ tion. The concern for possible health effects of MMV fibres has been the reason for a number of investigations in the recent years. It is believed that apart from the fibre dimensions, also the time of residence in the lung may be an important parameter for causing disease. The residence time is influenced by the physical clearance of the fibres from the lung and by the rate of dissolution of the fibres. The rate of dissolution of fibres may be assessed in different ways. In in vitro measurements the fibres are subjected to the influence of artificial, physiological solutions (Gamble's solution, modified according to the disclosure in Scholze, H. Conradt.: An in vitro study of the chemical durability of siliceous fibres. Ann. Occ. Hyg. 31, p. 683-692, (1987)), believed to resemble the conditions in the lung fluids. The liquids used are all characterised in that they have a pH of 7.4-7.8. However, it is known from Carr, Ian: The Macrophage - A Review of Ultrastructure and Function. Academic Press, (1973), that the pH in the macrophages is lower, i.e. more acidic, than that of the lung fluid, resembled by the normally used liquids. Recent published measurements of fibre durability, including in vivo measurements of the fibre dissolution in rat lungs indicate that this difference in pH may account for different rates of dissolu¬ tion, and it has been found that the fibres, when sufficiently short, may be engulfed by the macrophages. This might explain the lower rate of dissolution observed for shorter glass wool fibres. WO 89/12032 discloses inorganic fibre compositions among which some have passed the ASTM E-119 two hour fire test as well as exhibit low durabilities in physiological saline solutions, i.e. have high dissolution rates therein. The components of the prior art compo¬ sitions may vary considerably. However, all the disclosed compo¬ sitions are made from pure metal oxides or from less pure raw materials with addition of pure oxides which make the disclosed compositions very costly. International patent application No. PCT/DK93/00435 describes a fiberisable composition which is thermostable and has a high disso¬ lution rate in biological fluids and which consists essentially of Si0 2 53.5 - 64 w/w% < 4 w/w% A1 2°3 CaO 10 - 20 w/w% MgO 10 - 20 w/w% FeO 6.5 - 8 w/w%, the total amount of FeO and Fe O, being calculated as FeO. It is believed that the amount of magnesia and ferrous/ferric oxide components in a mineral composition has a significant influence on the thermostability of the MMV fibres. The ferrous/ferric oxide plays the important role of a crystal nucleating agent in the conversion of the fibre material from an amorphous condition to a crystalline or pseudo crystalline state during external influence of heat, e.g. during fire. Accordingly, this provides certain restri¬ ctions on the minimum amount of ferrous/ferric oxide component present in the composition. It should be noted that MMV fibre material without ferrous or ferric oxide may be capable of with- standing high temperatures which are reached by slow heat-up but not the fast heat-up resulting e.g. from external fire. When MMV fibre material is subjected to fire (sudden and/or fast heat-up), the structure of the material, i.e. the stone wool, is converted from an amorphous condition to a crystalline state. Thus, the thermostability of MMV fibres depends on their ability to rapidly crystallize when they are exposed to the influence of sudden heat or fire, i.e. when they are subjected to the influence of temperatures of up to about 1000 β C, such as temperatures of 700- 800 β C. By undergoing a rapid crystallization the shrinkage of products made from such fibres is only minimal. A fibre capable of rapid crystallization is obtained by including a crystal nucleating agent in the fibre material. MMV fibres, such as the fibres described in the above-mentioned international patent application, having a relatively high concen¬ tration of FeO tend to undergo a rapid crystallization when heated to temperatures of up to about 1000°C. However, the tendency of such fibres to crystallize at such tempera¬ tures has an adverse effect on the properties of the melts from which such fibres are made. In the production of MMV fibres the starting materials are heated to a sufficiently high temperature to form a melt which through gutters or the like is passed to a spinner in which the melt is spun into fibres. Generally for rock based melt compositions an increasing content of MgO and FeO will raise the liquidus temperature. Furthermore, a FeO content of above 6% combined with a low A O content will cause high crystallization rate. Therefore substantial slag formation in the gutters and outlet of the furnace have been observed for co - positions within the limits of the prior art (PCT/DK93/00435) which makes the melt less suitable for spinning. For these compositions it has been necessary to heat the melt to a temperature of at least 200°C above the liquidus temperature of the melt, which is 50-100°C higher than in normal manufacturing conditi¬ ons. The liquidus temperature is defined as the temperature at which a melt starts to crystallize when it is cooled. The object of the invention is to provide MMV fibres which are obtainable from a melt having a relatively low liquidus temperature and a low crystallisation rate and thereby not creating substantial slag formation in the process, and which at the same time exhibit a good thermostability and a high dissolution rate in biological fluids. The fibres of the invention comprise: Si0 2 48-64% by weight A1 2 0 3 0.3-4% by weight FeO 6-10% by weight CaO 10-35% by weight MgO 7-20% by weight Na 2 0 0-10% by weight κ 2 o 0-6 % by weight the total amount of FeO and Fe^O, being calc ted as FeO, the ratio of (Na 2 0 + K 2 0 + 0.1-CaO) to (MgO + FeO) bt.ng greater than 0.15, (MgO + FeO) being greater than 14 % by weight and (Na 2 0 + K 2 0) being less than or equal to 10% by weight. The invention is based on the discovery that both the liquidus temperature and the crystallisation rate of the melts for the production of fibres according to the invention is lowered to desirable respective levels by a broad range of compositions as long as the above relations are met. Thus, a relatively high concentra¬ tion of alkali may be used or a relatively low concentration of MgO + FeO combined with an increased amount of CaO, or a combination of both. On the other hand, in order to maintain a high thermostabili¬ ty, the sum of MgO and FeO should be above 14% by weight. In addition to the oxides mentioned above the fibres of the inven¬ tion may contain other oxides, such as B^O-, BaO, PoOc * nO ? , ZrO ? and TiO . In a preferred embodiment of the invention the alkali concentration, i.e. the sum of Na 2 0 and K 2 0 is equal to or greater than 4. Thus, the liquidus temperature is reduced with increasing concentrations of alkali. However, too high concentrations of alkali have a nega¬ tive influence on the thermal stability. Within a range of levels of alkali concentrations below a level of balance with the concentration of A O, an increase in the concen¬ trations of alkali causes an increase in the melt viscosity. At levels of alkali concentration higher than the level of balance a further increase in the concentration of alkali causes a reduction of the melt viscosity. In another preferred embodiment of the invention the concentration of MgO is preferably between 7 and 10% by weight and the concentra- tion of CaO preferably between 20 and 32% by weight. The higher the content of CaO, and preferably a CaO content of more than 19% by weight, more preferably of at least 20% by weight, having an upper limit of 35% by weight, preferably 32% by weight, works like the alkalis in reduction of the liquidus temperature, however, with a somewhat lower effect per weight percentage. At the same time the lower MgO plus FeO content reduces the crystallisation rate. According to another preferred embodiment of the invention, the concentration of CaO is between 10 and 16% by weight while the concentration of alkali is larger than 4% by weight. In order to obtain a viscosity which is particularly suitable for spinning, the melt should preferably contain from 48 to 60% by weight of Si0 2 . It would be desirable to combine high concentrations of Si0 2 with very low concentrations of Al 2 0 3 , but since low Al 2 0 3 -containing raw materials are difficult to obtain it is preferred to use starting materials having a content of Si0 2 in the lower end of the above- mentioned range. The Al 2 0 3 content of the fibres of the invention should be above 0.3% by weight and preferably above 1.0% by weight in order to keep the costs of the raw materials within reasonable 1imits. The composition of the melt used for the manufacture of MMV fibres according to the invention preferably contains the following oxides in such weight percentages that CaO + MgO + Na 2 0 + ICO + BaO + B 2 0, minus 2-Al ? 0- is greater than 30. The fibres of the invention may e.g. be prepared from the following naturally occurring raw materials: Quartz sand about 36 % Olivine sand about 17 % Iron ore about 12 % and Dolomite about 11 % together with: Cement about 12 % and MMV fibre waste about 12 %. Examples of other raw materials are slags, glass, foundry sand, lime stone, magnesite, brucite, talc, serpentinite, pyroxenite and wollastonite. The mineral composit e of the present invention is particularly suitable for the manufacture of MMV fibres by the method disclosed e.g. in WO 92/06047. For the manufacturing of fibres e.g. by this method a composition having a viscosity of approximately 15 poise at the working tempera¬ ture is preferred. On the other hand a melt composition having a viscosity within the range of 4-15 poise at the working temperature is acceptable. The invention further relates to a method of maintaining the high rate of dissolution in a biological fluid of a thermostable MMV fibre material, which method comprises the use of the MMV fibres as described above. In the present specification and claims, the term "biological fluid" denotes physiological salt or saline solutions as well as any fluid present in vivo in mammals. The MMV fibre material according to the invention exhibits a sinte¬ ring temperature of at least 900°C, more preferably at least 1000°C. The MMV fibre material according to the invention which is thermo¬ stable and has a high dissolution rate in biological fluids is useful for thermal and/or acoustic insulation purposes or as a plant growing medium or substrate. The fibres are also useful as reinforcement fibres in various matrix materials such as plastics, rubber compositions and ceramics or as a filler. EXAMPLE The dissolution rate and the thermostability of MMV fibres made from various compositions was determined as described below. The fibres were made by melting the raw materials in a cupola furnace, followed by spinning the fibre material into stone wool. Binder was not applied. The constituents of each test composition is shown in Table 1. It is to be understood that in addition to the constituents mentioned in Table 1 each of the tested fibre compositions contained up to a total of 2 w/w% of other constituents (traces) forming part of the raw materials used. Such other constituents may include, for example, manganous oxide, chromium oxide, and various sulfur com¬ pounds. However, the percentages in Table 1 are standardised to a total of 100 w/w% of the listed constituents. Tests 1-5 illustrate compositions according to the invention, whereas tests A-F are comparative compositions, test D-E being mentioned in PCT/DK93/00435. TEST METHODS Dimensions of the Fibre Samples The samples were sieved, and the fraction below 63 μm was used for the tests. For each sample, the fibre diameter distribution was determined, measuring the diameter and length of 200 individual fibres by means of an scanning electron microscope (1500 X magnification). The readings were used for calculating the specific surface of the fibre samples, taking into account the density of the fibres. Measurements of Rate of Dissolution (Stationary Set-Up) 300 g of fibres were placed in polyethylene bottles containing 500 ml of a modified Gamble's solution (i.e. with complexing agents) at pH 7.5. Once a day the pH was checked and if necessary adjusted by means of HC1. The tests were carried out during a one week period. The bottles were kept in water bath at 37°C and shaken vigorously twice a day. Aliquots of the solution were taken out after one and four days and analysed for Si on an Perkin-Elmer Atomic Absorption Spectrophoto- meter. The modi fi ed Gambl e ' s sol uti on , adjusted to pH 7.5 ± 0.2 , had the fol l owi ng composi ti on : aZl MgCl 2 .6H 2 0 0.212 NaCl 7.120 CaCl 2 -2H 2 0 0.029 Na 2 S0 4 0.079 Na 2 HP0 4 0.148 NaHC0 3 1.950 (Na 2 -tartrate)-2H 2 0 0.180 (Na 3 -citrate)-2H 2 0 0.152 90% Lactic acid 0.156 Glycine 0.118 Na-pyruvate 0.172 Formalin 1 ml Calculations Based on the dissolution of Si0 2 (network dissolution), the specific thickness dissolved was calculated and the rate of dissolution established (nm/day). The calculations were based on the Si0 2 content in the fibres, the specific surface and the dissolved amount of Si. Thermostability The thermostability expressed as the sintering temperature of the fibre compositions 1-4 and A-F was established by the following method: A sample (5 x 5 x 7.5 cm) of stone wool made of the fibre composi¬ tion to be tested was placed in a furnace pre-heated to 700°C. After o.5 hours exposure the shrinkage and the sintering of the sample was evaluated. The method was repeated each time with a fresh sample and a furnace temperature 50°C above the previous furnace temperature until the maximum furnace temperature, at which no sintering or no excessive shrinkage of the sample was observed, was determined. The test results are shown in Table 2 below. Table 1 Test...No. Composition. % by weight Si0 2 A1 2 0 3 Ti0 2 FeO CaO MgO Na 2 0 κ 2 o 1 55.6 4.0 0.8 6.8 13.9 12.8 0.6 5.4 2 57.2 2,5 0.5 6.9 13.8 12.6 6.0 0.5 3 50.7 2.9 0.2 6.7 25.7 10.1 3.0 0.6 4 52.6 3.2 0.3 6.8 25.3 11.1 0.1 0.6 5 55.0 2.1 0.2 7.5 25.6 8.4 0.8 0.3 A 52.2 4.4 0.3 8.1 29.5 4.4 0.1 1.0 B 60.4 2.7 0.6 5.5 11.0 11.3 7.9 0.6 C 53.0 3.1 0.5 5.1 28.7 8.2 0.7 0.6 D 56.4 2.7 0.5 7.3 17.0 15.1 0.4 0.6 E 46.8 13.2 2.9 6.3 17.2 9.6 2.8 1.2 F 54.9 4.0 0.6 6.8 17.2 15.3 0.5 0.7 Tabl e 2 Test No. Sintering Dissolution, Process Cha¬ temperature. °C oH = 7.5* racteristics 1 1000 5.6 No tendency 2 1000 6.0 to slag 3 900 8.1 formation 4 1000 9.2 5 >1100 19.3 A 750 3.7 B 750 4.8 C 800 6.1 D 1100 13.0 Strong ten¬ dency E 1050 3.0 No tendency F 1050 12.0 Strong ten¬ dency Di ssol uti on rate of Si (nm/day) lst-4th day The comparative examples A-C all have a low liquidus temperature and a low crystallization rate and thereby a low tendency to slag forma¬ tion due to either a relatively high content of alkali and/or high content of CaO and a relatively low concentration of MgO + FeO. However, the thermostability of the comparative examples A-C are all low due to either a low content of FeO and/or a low content of MgO. The comparative examples D and F both have a strong tendency to slagging due to the high content of (MgO + FeO) in combination with the low content of alkali and/or CaO giving a relative high liquidus temperature and crystallisation rate. Due to the high content of MgO + FeO examples D and F both have excellent thermostability. The comparative example E exhibits both excellent thermostability due to the relative high content of (MgO + FeO) and a low tendency to slagging due to the hign content of A1 2 0 3 . However, due to the high content of A1 ? 0 3 the comparative example E has a rather low dissolution rate in biological fluids. While specific embodiments of the invention have been described herein, others may practise the invention in any of the numerous ways which are suggested to one skilled in the art by this dis¬ closure. Therefore, all such practice of invention is considered to be a part hereof which falls within the scope of the appended claims.

Claims: CLAIMS 1. Thermostable MMV fibres exhibiting a high dissolution rate in biological fluids, c h a r a c t e r i z e d in that they comprise: Si0 2 48-64% by weight A1 2 0 3 0.3-4% by weight FeO 6-10% by weight CaO 10-35% by weight MgO 7-20% by weight Na 2 0 0-10% by weight κ 2 o 0-6 % by weight the total amount of FeO and Fe 2 0 3 being calculated as FeO, the ratio of (Na 2 0 + K 2 0 + 0.1-CaO) to (MgO + FeO) being >0.15 and (MgO + FeO) being greater than 14% by weight and (Na 2 + ICO) being less than or equal to 10% by weight. 2. Thermostable MMV fibres according to claim 1, c h a r a c ¬ t e r i z e d in that Na ? 0 + K 2 0 is equal to or greater than 4. 3. Thermostable MMV fibres according to claim 1 or 2, c h a r ¬ a c t e r i z e d in that it contains the following oxides in such weight percentages that CaO + MgO + Na 2 0 + I O + BaO + B 2 0 3 minus 2«A1 ? 0 3 is greater than 30. 4. Thermostable MMV fibres according to any of the preceding claims, c h a r a c t e r i z e d in that the concentration of MgO is between 7 and 10% by weight. 5. Thermostable MMV fibres according to any of the preceding claims, c h a r a c t e r i z e d in that the concentration of CaO is between 20 and 32% by weight. 6. Thermostable MMV fibres according to any one of the preceding claims, c h a r a c t e r i z e d in that the concentration of (CaO) is between 10 and 16% by weight. 7. Thermostable MMV fibres according to any one of the preceding claims, c h a r a c t e r i z e d in that the concentration of ( a 2 0 + ICO) is greater than 7% by weight. 8. Thermostable MMV fibres according to any of the preceding claims, c h a r a c t e r i z e d in that the concentration of SiO ? is between 48 and 60% by weight. 9. Thermostable MMV fibres according to any one of the preceding claims, c h a r a c t e r i z e d in that the concentration of A1 2 0 3 is between 1% and 4% by weight. 10. Use of MMV fibres according to any of claims 1-9 for thermal and/or acoustic insulation purposes. 11. Use of MMV fibres according to any of claims 1-9 as a plant growth medium or substrate. 12. Use of MMV fibres according to any of claims 1-9 for reinforce- ment purposes. 13. Use of MMV fibres according to any one of claim 1-9 as a filler.

Inventors: CHRISTENSEN VERMUND RUST, GULDBERG MARIANNE, JENSEN SOEREN LUND, SOERENSEN LONE MOELLER, CHRISTENSEN, VERMUND, RUST, GULDBERG, MARIANNE, JENSEN, SOEREN, LUND, SOERENSEN, LONE, MOELLER
Applicants: CHRISTENSEN VERMUND RUST, GULDBERG MARIANNE, JENSEN SOEREN LUND, ROCKWOOL INT, SOERENSEN LONE MOELLER, CHRISTENSEN, VERMUND, RUST, GULDBERG, MARIANNE, JENSEN, SOEREN, LUND, ROCKWOOL INTERNATIONAL A/S, SOERENSEN, LONE, MOELLER
Application year: 1995
Main classification: C03C13
IPC codes: A01G31, C03C13