RE-Fe-B magnets and manufacturing method for the same

Abstract: A permanent magnet alloy and method for production thereof. The permanent magnet alloy has a rare earth element including Nd, B, Fe, C, and oxygen, with additions of Co and at least one of Cu, Ga and Ag. The alloy may be produced by contacting particles thereof with carbon- and oxygen-containing material to achieve desired carbon and oxygen contents.

Description: BACKGROUND OF THE INVENTION Field of the Invention The invention relates to a permanent magnet alloy for use in the production of permanent magnets. Description of the Prior Art Permanent magnet alloys, and magnets produced therefrom, are conventionally produced by combining a light rare earth element, preferably neodymium, with the transition element iron, and boron. Permanent magnets produced from these alloys exhibit outstanding magnetic properties at room temperature. The alloys, however, exhibit poor thermal stability and poor corrosion resistance, particularly in humid environments. Hence, this limits the applications for which permanent magnets of these alloy compositions may be used. Various alloy modifications have been proposed to overcome the problems of poor thermal stability and poor corrosion resistance. None of these modifications have resulted in improving these properties without sacrificing other significant properties. European Patent Application No. 0 517 355 discloses a permanent magnet alloy having improved corrosion resistance over prior art alloys comprising a Nd-Fe-B composition with alloying additions of cobalt, aluminium and zirconium in combination. OBJECTS OF THE INVENTION It is accordingly a primary object of the present invention to provide a permanent magnet alloy and method for producing the same having improved thermal stability and corrosion resistance. Another object of the invention is to provide a permanent magnet alloy and method for producing the same wherein improved stability.and corrosion resistance is achieved, while improving the intrinsic coercivity without decreasing the remanence and Curie temperature to expand the useful temperature range for magnets made from the alloy. SUMMARY OF THE INVENTION The scope of the invention is as set out in the appended claims. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a graph showing the demagnetization curves of the alloy 32.5 Nd, 0.1 Dy, 1.0 B, 66.4 Fe with oxygen contents of 0.41 and 0.24%; Figure 2 is a graph similar to Figure 1, showing demagnetization curves of a 30.5 Nd, 2.5 Dy, 62.6 Fe, 2.5 Co, 1.1 B, 0.15 Cu, 0.65 Nb, having oxygen contents of 0.22 and 0.55%; Figure 3 is a graph indicating the variation in H ci for alloys of Nd-Dy-Fe-Al-B as a function of the oxygen content of the alloys; Figure 4 is a graph similar to Figure 3, indicating the variation in H ci for an alloy containing 29 Nd, 4 Dy, 5 Co, 1.15 B and balance Fe as a function of varying the oxygen content of the alloys; Figure 5 is a graph showing the effect of varying Co with and without oxygen addition for an alloy of 30.5 Nd, 2.5 Dy, 1.1 B, 0.15 Cu, 0.65 Nb, and balance iron; Figure 6 is a graph showing the effect of zinc stearate addition in varying amounts to increase the carbon content of an alloy of 31.9 Nd, 63.2 Fe, 3.6 Co, 1.15 B and 0.15 Cu; Figure 7 is a graph showing the effect of varying the Cu content in an alloy of 33 Nd, 5 Co, 1.1 B, and balance iron; Figure 8 is a graph showing the variation in the magnetic properties as a function of varying the copper content in an alloy of 30.5 Nd, 2.5 Dy, 1.2 Co, 1.1 B, 0.5 Nb, and balance iron; and Figure 9 is a graph showing the variation of magnetic properties as a function of varying the Nb content of the alloys 30.5 Nd, 2.5 Dy, 1.2 Co, 0.15 Cu, 1.1 B, and balance iron, and 28 Nd, 6 Dy, 2.5 Co, 1.1 B, 0.15 Cu, and balance iron. For purposes of development and demonstration of the invention, various alloys were prepared by conventional powder metallurgy processing and tested. Specifically, the alloys were produced by vacuum induction melting of a prealloyed charge of high purity elements and master alloys to produce a molten mass of the selected alloy composition. The molten mass was poured into a copper book mold or alternately atomized to form prealloyed powders by the use of argon as the atomizing gas. The cast ingot or atomized powder was hydrided at 1 to 30 atmospheres. The cast ingot was then crushed and pulverized into coarse powder. The pulverized powder or atomized powder was then ground into fine powder by jet milling with an inert gas such as argon or nitrogen gas. The pulverized powder or atomized powder was blended with various amounts of zinc stearate prior to jet milling to control the carbon content thereof and improve the jet milling practice. Oxygen was added by slowly bleeding air into the system either during or after jet milling. The oxygen and carbon may also be added and controlled by exposing the powder to a CO 2 environment incident to these operations. The average particle size of the milled powders was in the range of 1 to 5 microns, as measured by a Fisher Sub-Sieve Sizer. The prealloyed powder, prepared as described above, was placed in a rubber bag, aligned in a magnetic field, and compacted by cold isostatic pressing. The pressed compacts were then sintered to approximately their theoretical (full) density in a vacuum furnace at a temperature within the range of 900 to 1100°C for one to four hours. The sintered compacts were further heat treated at about 800 to 900°C for one hour and then aged within the range of 450 to 750°C. These magnet compacts were then ground and sliced into cylindrical shapes (6 mm thick by 15 mm diameter) for testing. The magnetic properties of the magnets tested were measured with a hysteresigraph equipped with a KJS Associate's temperature probe at temperatures between room temperature and 150°C. The irreversible loss was estimated by measuring the flux difference with a Helmholtz coil before and after exposing the magnet at elevated temperatures of up to 250°C for one hour. The permeance coefficient was one (1) because the L/D was 0.4 (6/15). As may be seen from and will be explained in detail with respect to the tables and drawings, it was discovered that the addition of oxygen to permanent magnet alloy compositions in accordance with the description and claims hereof decreases the coercivity, as shown in Figure 1 with respect to the reported composition of (Nd,Dy)-Fe-B. When oxygen is added to a (Nd,Dy)-(Fe,Co)-B alloy, as shown in Figure 2, it increases the coercivity, with the remanence in both cases being increased by an oxygen addition. The causes of the increases in remanence by oxygen addition in both of these alloys were investigated. The saturation magnetization values of the magnets of these alloys measured by VSM are the same both with and without oxygen addition. To assess the grain orientation of these magnets, an experiment was performed on the alloy (Nd,Dy)-(Fe,Co)-B. A ground surface normal to the cylinder axis was placed in a Bragg reflecting configuration in an X-ray powder diffractometer. The diffraction patterns with and without oxygen addition to the alloy were obtained. When the magnet is a single crystal, or had an ideal orientation with the easy axis normal to the surface, the diffraction pattern would show only reflections (001) with even values of 1, namely (004) and (006) in the investigated range. The results are shown in Table I. REFLECTIONS WITH LOW (h,k) AND HIGH 1 hkl Intensity Misorientation (h 2 +k 2 )I 2 Angle , degree cos 004 9 0 0 1 114 9 0.125 26.1 0.898 214 89 0.31 37.8 0.790 105 50 0.04 15.5 0.966 115 25 0.08 21.4 0.931 006 25 0 0 1 116 8 0.055 18.1 0.951 The reduction of magnetization through misorientation is described by cos , which is given by cos 2 =1 2 /[(c/a) 2 (h 2 +k 2 )+1 2 ] It was observed that sample A (without oxygen addition) exhibits strong (105) and (214) and relatively weak (004) and (006) peaks, while sample B (with oxygen addition) exhibits smaller (105), very weak (214), strong (004) and (006) peaks. This indicates that oxygen addition improves the grain orientation. Therefore, magnets with oxygen addition exhibit higher remanence than magnets without oxygen addition. The effect of variation in oxygen content on the coercivity of both types of alloys was also investigated. Figure 3 shows the variation of coercivity for (Nd,Dy)-Fe-Al-B alloys, as a function of oxygen content. In this alloy system, the coercivity almost linearly decreases as the oxygen content increases. When the total rare earth content is lower, the H ci decreases more rapidly. Figure 4 shows the variation of coercivity for cobalt containing alloys, (Nd,Dy)-(Fe,Co)-Al-B, as a function of oxygen content. In cobalt containing alloys, the coercivity initially rapidly increases as oxygen content increases up to a point depending on total rare earth and other additive elements, and then starts to decrease with further increases in oxygen content. Because of this positive effect of oxygen addition in (Nd,Dy)-(Fe,Co)-B alloys, the negative effect of a Co addition reducing the coercivity will be diminished or minimized by the simultaneous addition of Co and oxygen. Therefore, a high T c and B r magnet with improved H ci can be produced by the simultaneous addition of Co and oxygen in (Nd,Dy)-Fe-B alloys. The effects of Co variation in a (Nd,Dy)-(Fe,Co)-B alloy were investigated with and without oxygen addition, and the results are listed in Table II. The variation of coercivities of the alloys with and without oxygen addition are plotted against cobalt content in Figure 5. THE EFFECT OF Co VARIATION IN A 30.5Nd-2.5Dy-BAL Fe-1.1B-0.15Cu-0.65Nb-xCo ALLOY WITH AND WITHOUT OXYGEN DOPING ∼0.2% O 2 ∼0.45% O 2 % Co B r , kG H ci , kOe B r , kG H ci , kOe 0 11.30 20.2 11.65 19.8 1.2 11.45 20.2 11.65 20.8 2.5 11.20 18.3 11.30 20.4 5.0 11.40 17.3 11.50 17.6 15.0 11.45 13.9 11.55 14.9 As shown in Table II, the remanence increases 100-350 Gauss by oxygen addition to these alloys. The coercivity of non-cobalt containing alloys slightly decreases with oxygen addition, while that of cobalt containing alloys somewhat increases with oxygen addition. In alloys without oxygen addition, the coercivity decreases as cobalt content increases. In alloys with oxygen addition, the coercivity initially increases as Co content increases from zero to 1.2%, and then starts to decrease with further increases in Co content. Therefore, simultaneous addition of oxygen and a small amount of Co (1.2-2.5%) improves both remanence and coercivity. Even at higher Co contents, the coercivities of oxygen doped alloys are still higher than those of the alloys without oxygen addition. Therefore, oxygen addition is essential for Co containing (Nd,Dy)-(Fe,Co)-B alloys. Since the T c almost linearly increases with Co content, the required Co content in the alloy depends on Curie temperature, temperature stability and temperature coefficient of B r . Generally, the Co content is preferred to be between 0.5 and 5%. CHEMICAL COMPOSITIONS OF ALLOYS A, B, AND C BY WT. % Alloy Nd Dy Fe Co B Cu Nb Al (A) 31.5 0.5 bal 1.2 1.0 0.15 - - (B) 30.5 2.5 bal 1.2 1.1 0.15 0.35 - (C) 28.0 6.0 bal 2.5 1.1 0.15 0.65 0.3 A few examples of improved magnetic properties and temperature stability (irreversible loss at elevated temperature) by oxygen addition are listed in Table IV. The chemical compositions of examined alloys are listed in Table III. MAGNETIC PROPERTIES AND IRREVERSIBLE TEMPERATURE LOSS OF VARIOUS ALLOYS WITH AND WITHOUT OXYGEN DOPING Alloy % O 2 B r kG H ci kOe BH max MGOe % Irr. Loss P.C. = 1.0 (A) 0.237 12.7 11.2 38.2 39.0% at 150°C 0.574 12.9 14.9 40.2 3.6% at 150°C (B) 0.123 11.7 16.8 33.2 20.8% at 175°C 0.495 12.1 20.0 35.3 0.3% at 175°C (C) 0.253 10.6 >20.0 (9.7 at 150°C) 27.5 8.3% at 200°C 0.558 10.9 >20.0 (11.3 at 150°C) 29.3 1.8% at 200°C As shown in Table IV, the magnetic properties (both B r and H ci ) and temperature stability (irreversible loss) are substantially improved by an oxygen addition to Co containing (Nd,Dy)-(Fe,Co)-B magnets. It is noted, however, that the coercivity starts to decrease when oxygen exceeds about 0.8% depending on the additive elements as shown in Figure 4. It is, therefore, necessary to limit oxygen content to between 0.2 and 0.8%, preferably 0.3 to 0.8%. Since the magnets of the present invention were made by blending alloys with zinc stearate prior to jet milling, it is necessary to study the effect of variations of zinc stearate (carbon) on the magnetic properties. An alloy, 31.9Nd-63.2Fe-3.6Co-1.15B-0.15Cu, was made by argon gas atomization. After hydriding, the powder was blended with different amounts of zinc stearate prior to jet milling as shown in Table V. The magnetic properties (B r and H ci ) are plotted against zinc stearate variation in Figure 6. The variation of carbon content in the sintered magnets, density, remanence, and coercivity are also listed as a function of zinc stearate in Table V. THE EFFECT OF ZINC STEARATE ADDITION TO 31.9Nd-63.2Fe-3.6Co-1.15B-0.15Cu ALLOYS % ZS % C D g/cc B r kG H ci kOe 0 0.036 7.39 12.2 9.6 0.05 0.073 7.57 12.7 12.3 0.1 0.094 7.53 13.0 12.15 0.2 0.150 7.56 13.2 11.1 0.3 0.184 7.57 13.25 9.3 0.5 0.310 7.56 13.5 7.7 0.8 - not densified As shown in Figure 6, both the B r and H ci have significantly increased with small additions of zinc stearate. When the zinc stearate addition exceeds 0.1 %, the H ci starts to decrease while the B r increases slowly. When the zinc stearate addition is 0.8%, the compact is not densified. Therefore, any zinc stearate employed for carbon addition should be limited to 0.5%. The carbon content of the sintered magnet almost linearly increases as the amount of zinc stearate added increases. Therefore, it is essential to add small amounts of zinc stearate (carbon) for improving magnetic properties (both B r and H ci ). The optimum range of zinc stearate addition is 0.05 to 0.2%, depending on the magnetic property requirements. In the following study, the zinc stearate addition was fixed at 0.1%, and oxygen was added to about 0.5% in Co containing alloys. Since it is known that the addition of 1 to 2% copper to NdFeB melt spun ribbon substantially increased the coercivity, we examined the effect of Cu variation in sintered (Nd,Dy)-(Fe,Co)-B alloys. Figure 7 and Table VI exhibit the variations of B r and H ci plotted against Cu variation in a 33Nd-1.1 B-5Co-(60.9-x)Fe-xCu alloy, and corrosion resistance as a function of weight loss in relation to the Cu content. THE EFFECT OF Cu VARIATION IN A 33Nd-1.1 B-5.0Co-(60.9-x)Fe-xCu ALLOY % Cu D g/cc B r kG H ci kOe Wt. Loss (mg/cm 2 ) 96 hr 240 hr 0 7.58 12.8 9.4 17.5 228 0.05 7.58 12.9 10.8 0.5 4.7 0.1 7.58 13.0 11.3 0.7 2.2 0.15 7.58 12.9 13.0 0.07 0.08 0.2 7.58 12.8 13.5 0.01 0.16 0.3 7.58 12.65 13.2 0.05 0.42 0.5 7.57 12.65 12.4 0.15 0.25 1.0 7.48 12.3 11.5 0.19 0.36 2.0 7.36 12.3 9.0 0.52 0.76 As the copper content increases to 0.15%, the H ci increases rapidly and reaches its maximum at 0.2% Cu. When the copper content exceeds 0.2%, the H ci starts to decrease. The B r also increases slightly as the copper content increases to 0.1%, and then slowly decreases with further increases in copper content. Therefore, the overall change in remanence is negligible in the range of between 0 to 0.2% copper. A small addition of copper to Nd-Fe-B does not change the Curie temperature. These data indicate that a small addition of copper (up to 0.2%) to Nd-Fe-Co-B alloys substantially improves H ci without reduction of B r or T c . The corrosion rate is significantly reduced as the copper content increases from 0 to 0.15% and the minimum corrosion rate is maintained with further increases in copper content. Another set of magnets was made with oxygen doping to approximately 0.5%. Figure 8 and Table VII exhibit the variation of magnetic properties as a function of Cu content in 30.5Nd-2.5Dy-bal Fe-1.2Co-1.1B-0.5Nb-xCu alloy. THE EFFECT OF Cu VARIATION IN A 30.5Nd-2.5Dy-BAL Fe-1.2Co-1.1B-0.5Nb-xCu ALLOY % CU B R H ci BH max 0 11.6 13.8 32.0 0.05 11.7 16.8 33.0 0.1 11.75 19.3 33.5 0.15 11.75 20.2 33.5 0.2 11.8 20.4 33.8 0.25 11.75 19.8 33.5 0.3 11.75 19.3 33.5 As the copper content increases to 0.1%, the H ci increases rapidly then slowly increases to a maximum at 0.2% Cu. When the copper content exceeds 0.2%, the H ci starts to decrease. The remanence and energy products also increase slightly as the copper content increases to 0.1 %, and then remain the same with further increases in copper content to 0.3%. This indicates that a small addition of copper (between 0.1 and 0.3%) to oxygen doped (Nd,Dy)-(Fe, Co)-B alloys substantially increases H ci with slight increases in B r and (BH) max . It is, therefore, beneficial to simultaneously add small amounts of Cu, O, C (zinc stearate) to Co containing (Nd,Dy)-(Fe,Co)-B magnets in order to effectively improve coercivity without sacrifice of remanence. It was observed that small additions of Ga or Ag to Co containing (Nd,Dy)-(Fe,Co)-B magnets might also substantially increase the coercivity similarto Cu. Examples of improved magnetic properties (H ci ) resulting from small additions of Cu, Ga, or Ag are listed in Table VIII. CHEMICAL COMPOSITION AND MAGNETIC PROPERTIES Chemical Composition (Wt. %) Alloy Nd Dy Fe Co B Cu Ag Ga B r kG H ci kOe D 31.9 - bal 3.6 1.15 - - - 12.8 10.2 E 31.9 - bal 3.6 1.15 0.15 - - 12.9 13.0 F 31.9 - bal 3.6 1.15 - 0.2 - 12.9 13.2 A 31.5 0.5 bal 1.2 1.0 0.15 - - 12.8 15.2 G 31.5 0.5 bal 1.2 1.0 - - 0.4 12.8 15.3 As shown in Table VIII, the coercivities are substantially increased by small additions (0.1 to 0.4 wt. %) of Cu, Ag, or Ga to Co containing alloys (Nd,Dy)-(Fe,Co)-B, without reduction of remanence. The effect of combined additions of the elements, Cu and Ga, was also investigated. Alloys A (0.15% Cu) and G (0.4% Ga) were blended in different ratios, as shown in Table IX. THE EFFECT OF Ga AND Cu VARIATION IN A 31.5Nd-0.5Dy-BAL Fe-1.2Co-1.0B-xGa-yCu ALLOY % Ga % Cu D g/cc B r , RT kG H ci , RT kOe 0 0.15 7.60 12.8 15.2 0.1 0.117 7.56 12.6 15.8 0.2 0.075 7.57 12.8 16.4 0.3 0.038 7.59 12.9 16.6 0.4 0 7.57 12.8 15.3 Although both alloys exhibit similar magnetic properties individually, when blended together the blended alloys exhibit higher coercivities. This indicates that when both elements Cu and Ga are used together, they effectively increase coercivity. The maximum coercivity was obtained when Ga content is 0.3% and Cu is 0.038%. This concept was applied to 9% dysprosium alloys. By fixing copper content at 0.2, the Ga content was varied from 0 to 1.0%. The coercivities of these magnets were measured at 150°C. THE EFFECT OF Ga VARIATION IN A 24Nd-9Dy-BAL Fe-2Co-1.1B-0.2Cu-0.65Nb-0.3Al-xGa ALLOY % Ga D g/cc B r , RT kG H ci , 150°C kOe Irr. Loss at 250°C (%) PC=1.0 0 7.54 10.1 15.7 16.1 0.2 7.53 10.2 16.5 2.0 0.4 7.47 10.05 16.9 3,1 0.6 7.42 10.0 16.3 2.9 0.8 7.33 9.9 15.9 4.4 1.0 7.31 9.5 15.3 9.0 As shown in Table X, the coercivity at 150°C increases as Ga content increases to 0.4%, and then starts to decrease with further increases in Ga content. The maximum coercivity was obtained when the Ga content is 0.4% and the Cu content is 0.2%. The irreversible losses at 250°C are very low when Ga content is between 0.2 and 0.6%, while magnets without Ga or with 1.0% Ga exhibit relatively large irreversible losses. As the Ga content increases, the density starts to decrease. These data indicate that the optimum Ga content required for temperature stable magnets in this alloy system is between 0.2 and 0.6%. This is much lowerthan the Ga content necessary in (Nd,Dy)-(Fe,Co)-B alloys without O, C, and Cu addition if the same coercivity and temperature stability are required. It is known to add 1 to 2 at. % (1.05-2.1 wt. %) Ga for similar enhancements. Therefore, single or combined additions as claimed of small amounts of M1 (Cu, Ga, or Ag) to the (Nd,Dy)-(Fe,Co)-(B,C,O) alloy effectively improve the coercivity without remanence reduction. Additions of other transition metals (M2) including Al, Si, Sn, Zn, Nb, Mo, V, W, Cr, Zr, Hf, Ti, Mg, etc. to this alloy system, (Nd,Dy)-(Fe,Co,M1)-(B,C,O), further improve the coercivity with some reduction of remanence. As shown in Figure 9, for example, the H ci increases and the B r decreases as Nb content increases. Table XI displays magnetic properties of these alloys with various transition metals (M2) added. EFFECT OF M2 ELEMENTS ADDED IN (Nd,Dy)-(Fe,Co,Cu)-(B,C,O) ALLOYS Alloy Wt. % H ci kOe Nd Dy Fe Co B Cu M2 B r kG H 30.5 2.5 bal 1.2 1.1 0.15 - 12.3 18.5 I 30.5 2.5 bal 1.2 1.1 0.15 0.2Al 12.0 20.4 J 30.5 2.5 bal 1.2 1.1 0.15 0.75Si 11.4 20.3 K 30.5 2.5 bal 1.2 1.1 0.15 0.65Nb 11.7 21.0 L 31.2 2.5 bal 1.2 1.1 0.15 0.2Al + 0.65Nb 11.4 21.5 A part of Nd in this alloy system can be substituted by other light rare earth elements, including Pr, La. Table XII exhibits magnetic properties of this alloy system in which Nd is partially substituted by Pr or La. MAGNETIC PROPERTIES OF RE-(Fe,Co,Cu)-(B,O,C) ALLOYS WITH PARTIAL SUBSTITUTION OF Nd WITH OTHER RARE EARTH ELEMENTS Alloy Wt. % H ci kOe Nd Pr La Dy Fe Co B Cu Nb B r kG M 30.5 - - 2.5 bal 1.2 1.1 0.15 0.35 11.9 20.2 N 26.5 4.0 - 2.5 bal 1.2 1.1 0.15 0.35 12.0 20.1 O 28.8 - 1.6 2.5 bal 1.2 1.05 0.2 - 11.9 18.3 As may be seen from the above-reported specific examples, (Nd,Dy)-(Fe, Co)-B magnets doped with small amounts of oxygen and/or carbon, which may be achieved by zinc stearate addition, exhibit much higher magnetic properties (both B r and H ci ) than (Nd,Dy)-(Fe,Co)-B magnets without oxygen and/or carbon addition. Small additions of Cu, Ga, Ag, or a combination of these as claimed (M1) to (Nd,Dy)-(Fe,Co)-(B,C,O) substantially increases the coercivity without reduction of remanence. Since the coercivity is substantially improved without reduction of T c and/or B r in this alloy system, it can be used at elevated temperatures with minimum additions of Dy. Utilization of abundant and inexpensive elements such as O, C, Cu and reduction of expensive elements such as Dy and/or Ga will reduce the total cost of producing magnets from this alloy system. The coercivity can be further improved with additions of other transition metals (M2) including Al, Si, Sn, Zn, Nb, Mo, V, W, Cr, Zr, Hf, Ti, and Mg. Additions of these elements will, however, cause reduction of remanence and energy product. Other light rare earth elements such as Pr or La can partially replace Nd in this alloy system. As used herein, all percentages are in "weight percent," unless otherwise indicated. The following conventional abbreviations are used herein with respect to the reported properties of magnets: B r - remanence H ci - intrinsic coercivity BH max - energy product T c - Curie temperature

Claims: A permanent magnet alloy comprising, in weight percent, 27 to 35 of a rare earth element, including Nd in an amount of at least 50% of the total rare earth element content, 0.8 to 1.3 B, up to 30 Co, not less than 40 Fe, 0.03 to 0.3 C, 0.2 to 0.8 oxygen, 0.02 to 0.5 of each of Cu and Ga, optionally up to 5% of at least one additional transition element selected from the group consisting of Al, Si, Sn, Zn, Nb, Mo, V, W, Cr, Zr, Hf, Ti and Mg and balance incidental impurities. A permanent magnet alloy comprising, in weight percent, 27 to 35 of a rare earth element, including Nd in an amount of at least 50% of the total rare earth element content, 0.8 to 1.3 B, up to 30 Co, not less than 40 Fe, 0.03 to 0.3 C, 0.2 to 0.8 oxygen, 0.02 to 0.5 of Ag, preferably 0.05 to 0.5, optionally up to 5% of at least one additional transition element selected from the group consisting of Al, Si, Sn, Zn, Nb, Mo, V, W, Cr, Zr, Hf, Ti and Mg and balance incidental impurities. The permanent magnet alloy of any one of the preceding claims, wherein Co is 0.5 to 5%. The permanent magnet alloy of any one of the preceding claims, wherein Cu is 0.02 to 0.5%. Use of 0.02 to 0.5 percent by weight of copper as a constituent of a permanent magnet alloy to improve corrosion resistance and increase coercivity, the permanent magnet alloy comprising, in weight percent, 27 to 35 of a rare earth element, including Nd in an amount of at least 50% of the total rare earth element content, 0.8 to 1.3 B, 0.5 to 5 Co, not less than 40 Fe, 0.03 to 0.3 C, 0.2 to 0.8 oxygen, optionally 0.02 to 0.5 of at least one of Ga and Ag, optionally up to 5% of at least one additional transition element selected from the group consisting of Al, Si, Sn, Zn, Nb, Mo, V, W, Cr, Zr, Hf, Ti and Mg and balance incidental impurities and preferably wherein B is 0.9 to 1.2, Cu is 0.05 to 0.15, and oxygen is 0.3 to 0.8. The permanent magnet alloy of claim 1 wherein B is 0.9 to 1.2, Cu is 0.05 to 0.15, and oxygen is 0.3 to 0.8. The permanent magnet alloy of claim 1 wherein at least one of Cu, and Ga, is 0.05 to 0.5. A method for producing a carbon- and oxygen- containing permanent magnet alloy, said method comprising producing an alloy comprising, in weight percent, 27 to 35 of a rare earth element, including Nd in an amount of at least 50% of the total rare earth element content, 0.8 to 1.3 B, up to 30 Co, not less than 40 Fe, 0.02 to 0.5 of at least one of Cu, Ga and Ag and optionally up to 5% of at least one additional transition element selected from the group consisting of Al, Si, Sn, Zn, Nb, Mo, V, W, Cr, Zr, Hf, Ti .and Mg and balance incidental impurities; producing prealloyed particles and/or blends thereof from said alloy, contacting said particles with a metal stearate and thereafter reducing the size of said particles by jet milling to produce a carbon content therein of 0.03 to 0.3 and contacting said particles with an oxygen-containing material to produce an oxygen content therein of 0.2 to 0.8. The method of claims 8, wherein said metal stearate is zinc stearate. The method of any one of claims 8 or 9, further comprising said oxygen containing material being air. The method of claim 10, further comprising contacting said particles with said air during or after reducing the size of said particles. The method of claim 8, wherein oxygen and carbon are also added by a exposing the particles carbon dioxide.

Inventors: CAMP FLOYD E, KIM ANDREW S, CAMP, FLOYD E., KIM, ANDREW S.
Applicants: VACUUMSCHMELZE GMBH & CO KG, VACUUMSCHMELZE GMBH & CO. KG
Application year: 1995
Main classification: H01F1
IPC codes: C22C1, H01F1