RECOVERY OF CHEMICAL VALUES FROM INDUSTRIAL WASTES

Abstract: A method for the recovery of chemical values, such as metals including zinc, zinc oxide, iron-carbon feedstocks, lead and cadmium, from industrial waste streams which entails treating the waste streams with carbon and an ammonium chloride solution, separating any undissolved components from the solution, displacing metal ions including lead and cadmium from the solution using zinc metal, further treating the solution to remove zinc compounds therefrom, further treating the zinc compounds and the undissolved components with a dissolving solution, and further treating the displaced metal ions to recover lead, cadmium and zinc therein using various methods including electrolysis.

Description: "Recovery of Chemical Values from Industrial Wastes". BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates generally to a process for the recovery of chemical values, including metals, from industrial waste streams comprising zinc compounds and iron compounds. The present invention relates more specifically to a process subjecting a waste materials stream comprising zinc compounds and iron compounds, such as electric arc furnace (EAF) dust or metal wire production dust, to a combination of leaching and reducing steps, which enable the separation and recovery from the waste materials stream of zinc oxide, zinc metal, iron and carbon compounds, lead, cadmium, copper, tin, and other metals which may be in the industrial waste stream. 2. Prior Art Zinc oxide typically is a coarse white or grayish powder which has a variety of uses including as an accelerator activator, as a pigment, as a dietary supplement and in the semiconductor field. Zinc oxide is found in commercial by-products including waste materials such as fly ash and flue dust. Methods for recovering zinc oxides are known in the art, including recovering zinc oxide from industrial waste materials. Such previous methods have included leaching with mineral acid, caustic soda, ammonium hydroxide, and ammonium carbonate solutions. These methods have low yields of zinc oxide typically being contaminated with other metal salts. Therefore, to obtain pure zinc oxide, subsequent roasting and evaporation processes were necessary. Zinc And Its Alloys And Compounds, by S. W. K. Morgan (Ellis Horwood Ltd., 1985) at 103 et seq. discusses electrolytic processes for removing zinc from zinc sulfide concentrates. Roasting, leaching and neutralization are used in the pre- electrolysis of a zinc blend. However, further treatment of the zinc blend, or flue dust, to reclaim metal compounds is not discussed. For the electrolytic process to be commercially useful, a solution containing a single metallic element in the compound is necessary. For example, the electrolytic process works well in removing zinc from a relatively pure solution of zinc sulfate, in which zinc is deposited on the cathodes and sulfuric acid is formed at the anodes. The presence of iron and/or copper in the solution contaminates the zinc and causes a reduction in current efficiency, and should be removed prior to the electrolytic removal of zinc. The presence o f cadmium and lead also contaminates the zinc. Consequently, the electrolytic process is not satisfactory for removing a pure metal from a solution containing a number of different metals such as zinc, lead and tin. Electrolysis would be satisfactory fc r removing zinc from a solution if any lead and tin contained in the solution are removed prior thereto. For zinc dust, it is necessary to precipitate any copper, cobalt and cadmium in the solution prior to the electrolytic removal of zinc. Therefore, it would be desirable to have a process in which the cadmium and copper could be removed by precipitation and the zinc could be removed by a chemical process. Zinc the Science and Technology of the Metal, Its Alloys And Compounds (Reinhold Publishing Corp., 1959) a 183 et seq., discusses leaching zinc oxide by dissolving zinc oxide in dilute sulfuric acid. This simple process results in dissolving unwanted elements in compounds, which affects the electrolysis step. Consequently, leaching with sulfuric acid is not satisfactory alone for removing the various metals in zinc rich dust. The leaching process is designed to lead eventually to the removal of the zinc by the electrolytic process. This monograph shows the use of metallic zinc dust to precipitate any copper in the solution. Cadmium is removed from the solution by agitation with zinc dust or contact with metallic zinc. Consequently, it would be desirable to have a process in which the impurities can be separated from the zinc-rich leachate. Industrial Electrochemistry, by C. L. Martell (McGraw-Hill Book Company, Inc., 1940) at 321-7, discusses cadmium recovery from zinc electrolyte residues. Cadmium, copper, and zinc are dissolved during the leaching process. The Martell book discusses the use of zinc dust in the precipitation of the cadmium, copper and lead in the residue, the separation of a cadmium precipitate sponge, and the subsequent dissolving of the sponge in dilute sulfuric acid. U.S. Patent No. 3,849,121 to Burrows, now expired but which was assigned to a principal of the assignee of the present invention, discloses a method for the selective recovery of zinc oxide from industrial waste. The Burrows method comprises leaching a waste material with an ammonium chloride solution at elevated temperatures, separating iron from solution, treating the solution with zinc metal and cooling the solution to precipitate zinc oxide. The Burrows patent discloses a method to take EAF dust which is mainly a mixture of iron and zinc oxides and, in a series of steps, to separate out the iron oxides and waste metals. However, the material obtained in the last step is a mixture of a small amount of zinc oxide, hydrated zinc phases which can include hydrates of zinc oxide and zinc hydroxide, as well as other phases and a large amount of diamino zinc dichloride Zn(NH 3 ) 2 Cl 2 or other similar compounds containing zinc and chlorine ions. Currently, the Burrows method is not economically viable because of U.S. Environmental Protection Agency guidelines established subsequent to the issuance of the Burrows patent. Additionally, the Burrows method is not a continuous method and, therefore, is not economical as a continuous process. The first step in the Burrows patent is the treating of the EAF dust with an ammonium chloride solution to leach zinc oxide, lead oxide and cadmium oxide into the solution without any leaching of the iron oxides present. Twenty to fifty percent of the zinc present in the Burrows dust is in the form of an iron-zinc complex (spinel) which cannot be leached by the ammonium chloride solution. The Burrows process therefore cannot leach and recover a significant portion of zinc present in the EAF dust. The second step in the Burrows process is cementation in which the solution obtained from the initial leach is filtered to remove any remaining solids and then zinc dust is added. The zinc dust causes an electrochemical reaction which causes lead and cadmium to deposit on the zinc particles. Burrows does not teach the need to remove the lead and cadmium in this step efficiently without using a large amount of zinc. If the process requires too much zinc in this step, it is uneconomical. The zinc powder when added tends to clump together reducing the available surface area and requiring the addition of more zinc. The third step in the Burrows patent cools the filtrate from the cementation process and obtains zinc oxide crystals. Burrows indicates that these crystals range in size up to 1 cm. Burrows does not produce zinc oxide of any degree of purity; x-ray diffraction figures clearly show that upon crystallization there is a mixture of many phases. Washing the crystals is not sufficient to purify the material to zinc oxide since zinc hydroxide and hydrates are also present, so that a drying step is necessary. In addition, the control of the size of the zinc oxide along with the purity is crucial. Commercial zinc oxide normally has a requirement that 99% of the particles fit through 325 mesh (44 microns). Burrows indicates no method of cooling or controlling either purity or size, and the particles produced do not meet commercial requirements. Further, a significant portion of the ammonium chloride is lost in the crystal washing step when the diamino zinc dichloride decomposes. Waste metal process dust typically has varying amounts of lead, cadmium and other metals contained in the dust. The Burrows patent includes a method for removing dissolved lead and cadmium from the ammonium chloride leachant solutions by the addition of powdered zinc dust to the ammonium chloride solutions. The resulting electrochemical reaction forms elemental lead deposits on the surface of the powdered zinc dust. For this reaction to proceed, a large surface area of zinc must be present because as the lead covers the zinc dust particle, the particle becomes no longer available for the electrochemical reaction. For this reason, very fine powder is used which aggregates to form large clumps which sink to the bottom of the vessel. Rapid agitation does not prevent this from happening. Because of the aggregation, a large amount of zinc must be added to remove all of the lead, a poor practice for economic reasons. Further, if it is desired to separate lead and cadmium from the zinc so that these metals can be sold or reused, the higher the zinc concentration in the metals, the larger the mass to be processed per unit mass of zinc. A further limitation of the Burrows method is that it makes no provision for the separation and recovery of metals such as lead and cadmium which are byproducts of the cementation process. Recovery of these byproducts results in a reduction of waste and produces economically valuable products. U.S. Patent No. 4,071,357 to Peters discloses a method for recovering metal values from flue dust which includes a steam distillation step and a calcining step to precipitate zinc carbonate and to convert the zinc carbonate to zinc oxide, respectively. Peters further discloses the use of a solution containing approximately equal amounts of ammonia and carbon to leach the flue dust at room temperature, resulting in the extraction of only about half of the zinc in the dust, almost 7% of the iron, less than 5% of the lead, and less than half of the cadmium. Steam distillation precipitates zinc carbonate, other carbonates and iron impurities, whereas temperature lowering precipitates a number of crystalline zinc compounds. Steam distillation also results in an increase in temperature which drives off ammonia and carbon dioxide, resulting in the precipitation of iron impurities and then zinc carbonate and other dissolved metals. The purity of the zinc carbonate obtained depends on the rate of steam distillation and the efficiency of solids separation as a function of time. Calcining at temperatures between 200°C and 1100°C converts the zinc carbonate to zinc oxide, whereas washing and drying at temperatures between 100°C and 200°C converts the zinc compounds to zinc oxide. In addition to the advantages of temperature lowering, the present process employs an NH C1 solution, and has several distinct advantages over the Peters process: 1. The solubility of zinc and zinc oxide is relatively high in NH 4 C1 solution which is important to efficiency in regard to the rate of the leaching, the mass of dust that can be processed, and the ability to recycle the solution. The leaching rate is a function of the difference between the zinc concentration in solution and the saturation concentration; the higher the saturation concentration the more rapid the leaching. The present process leaches for only 1 hour, while the Peters process leaches for at least several hours. In addition, the solubility of zinc and zinc oxide in the ammonium chloride solution declines rapidly with temperature, which is the basis for the crystallization-based separation of the present process. 2. Lead and lead oxide, as well as cadmium and cadmium oxide, are soluble in the ammonium chloride solution while iron oxide is virtually insoluble. During the leaching process of the present invention, 95-100% of the zinc present as zinc oxide is extracted, compared to about 55% in Peters: 50-70% of the lead present is removed, compared to less than 5% in Peters: and 50-70% of the cadmium is removed, compared to less than half in Peters. Peters does not remove a significant amount of the impurities so as to leave an acceptably clean effluent. Peters indicates that the residue, which is high in lead and is a hazardous waste, is discarded. By leaching out a significant portion of the lead and cadmium, the present process produces a material which can be used by the steel producer as they use scrap metal. Likewise, the present process enables separation and recovery of substantially pure lead and cadmium, thereby reducing the overall volume of waste and reclaiming materials having potential economic value. In the present process the filtrate from the cementation step is already hot (90- 110°C) and contains a large amount of dissolved zinc with small amounts of trace impurities. Upon controlled cooling of the solution, crystals of zinc salts appear. Control of the cooling rate and temperature versus time profile is important in controlling the size distribution of the crystals and in reducing or eliminating many of the impurities which might occur. This is especially true of included solution; control of the crystallization can reduce this to virtually zero. In addition, since crystallization is based on differential solubility, and none of the impurities is present in a concentration which can crystallize, the zinc salts are virtually free of any metal impurities. The final purification step in Peters is a calcining of the zinc carbonate to zinc oxide at 600°C. In the present process, the mixture of zinc oxide hydrates and diamino zinc dichloride are suspended in hot (90-100°C) water. The zinc oxide is not soluble; however, the diamino zinc dichloride is very soluble and completely dissolves. The remaining solid which is zinc oxide hydrates is then filtered and dried at 100-350°C to remove the water of hydration. The result is a very pure zinc oxide powder of controlled particle size. Engitec Impianti SpA, of Milan, Italy proports to recover zinc metal and lead cement directly from EAF flue dust using electrowinning, the technique of extracting a metal from its soluble salt by an electrolytic cell. Typically, it is used in the recovery of zinc by subjecting the zinc salt in solution to electrolysis and electrodepositing the elemental metal on a zinc cathode in the electrolytic cell. In the Engitec process, the EAF flue dust is leached with a spent electrolyte, such as ammonium chloride, which dissolves the zinc, lead, copper and cadmium in the EAF dust into solution while leaving the iron in solid form. The solution containing the dissolved zinc is placed in an electrolytic cell which draws the zinc from the solution onto a cathode plate, while the other heavy metals are filtered out in solid form into cement cakes. Engitec claims to obtain a zinc yield that is 99.5% pure and a lead cake consisting of a minimum of 70% lead. Apparently, the electrolysis of the zinc amino complex in the purified solution occurs in a conventional open cell using a titanium permanent blank cathode and a proprietary graphite anode. In the electrolysis cell, the zinc plates on the titanium cathode over 24 to 48 hours, depending on the current density. In addition to the electrowinning of zinc, the electrolysis cell consumes ammonia and evolves nitrogen. Because of this, in order to maintain the pH of the electrolyte in the desired range of 6 to 6.5, additional ammonium must be added to the cell in the range of 180kg per tonne of product zinc. In the Engitec process, the use of an electrolysis cell adds additional costs to the process due to the energy consumption of an electrolysis cell, the consumption of ammonia in the electrolysis cell, additional costs in handling nitrogen evolved in the electrolysis cell, and the cost of maintaining the components of the electrolysis cell itself. The Engitec process also results in the formation of metallic zinc. Although metallic zinc has a certain value, zinc oxide has more value. The residue removed from the Engitec process is composed primarily of iron oxide and zinc ferrite. Iron oxide can be used in the steel making process. The presence of zinc ferrite injects an additional impurity into any future process. It would be more advantageous to obtain a residue comprising primarily iron oxide with an insignificant amount of zinc ferrite or other impurities. The electrowinning of metals from chloride solutions is known in the art. U.S. Patent No. 4,155,821 to Grontoft discloses and claims a method for recovering chlorine using electrolytic separation. Chlorine and zinc metal are produced from a chlorine containing electrolyte by an electrolytic process having an anode surrounded by a membrane connected to a hood. The process is maintained at a partial vacuum to remove chlorine gas generated by the anode and to control rediffussion of chlorine containing electrolyte back through the membrane into the surrounding electrolyte. The process is for use with nickel recovery where the nickel chloride containing electrolyte is introduced at such a rate that the pH is maintained below a certain level. The process also may be used for cobalt recovery. The electodeposition of zinc from chloride solutions also is known in the art. U.S. Patent No. 4,292,147 to Fray discloses and claims a method for the electrodeposition of cadmium or zinc from chloride solutions derived from chlorine leaching of materials. An aqueous solution having 15 to 30% by weight of zinc or cadmium chloride is electro lyzed at a pH of 2 to 3.5 at a temperature of below 35°C with gas agitation at a current density above 100A/m 2 to form coherent zinc or cadmium at the cathode. A typical zinc containing material such as flue dust is leached with a saturated chlorine solution, preferably in the presence of chlorine hydrate. The zinc chloride solution preferably contains up to 20% by weight alkaline metal or ammonium chloride. The electrolysis preferably is carried out at 0°C to 9°C and above 2500A/m with intermittent current reversal. Thus, there exists a need for a method which will recover zinc products, including zinc metal and zinc oxide, from industrial waste which results in a product the majority of which is either zinc or zinc oxide, and not mixtures of zinc oxide and other zinc phases. Zinc products, specifically zinc metal and zinc oxide, are desired and diamino zinc dichloride is undesired. The present method demonstrates how to increase the formation of desired zinc products and decrease the formation of diamino zinc dichloride. There also is a need for a method for the efficient reclamation of metal values from dust that contains zinc, lead, cadmium, copper, and tin or compounds thereof. In the processing of electrical cable and other types of electrical conductors, dust is produced that contains zinc, lead, cadmium, copper, and tin. For environmental and efficiency reasons, a method is needed to reclaim this dust and return it to the initial elements or to a compound containing the element. Further, the reclaimed metals and metallic compounds have value and can be sold, reused, or used in other processes. It is especially important to recycle the lead and cadmium so as to prevent its introduction into the atmosphere, as both are considered atmospheric pollutants. BRIEF SUMMARY OF THE INVENTION The present invention satisfies these needs in a method which recovers essentially pure zinc oxide from waste material containing zinc or zinc oxide and then further treats and recovers a quantity of high quality metal values from the waste material. The solutions used in the process are recycled such that the process does not have any liquid wastes. The solids recovered from the process can be used in other processes. Several such residues, including the iron oxide cake, lead metal residue, and cadmium are of such quality that they can be used directly as raw material for production of a variety of goods. In the primary process, the waste material is leached with an ammonium chloride or sulfur-based solution resulting in a product solution and undissolved materials. The product solution and the undissolved materials are separated, with both the product solution and the undissolved materials being further treated to recover valuable components. Zinc metal is added to the product solution to cement out any lead and cadmium contained in the product solution. The remaining product solution is rich in zinc compounds. The remaining product solution then can be treated in two manners. First, the remaining product solution can be cooled thereby precipitating the zinc components from the product solution as a mixture of crystallized zinc compounds. These crystallized zinc compounds are separated from the product solution, washed and then dried at elevated temperatures, resulting in a zinc oxide product of 99% or greater purity. Second, the remaining product solution can be subjected to electrolysis in which zinc metal plates onto the cathode of the electrolysis cell. Any remaining product solution after crystallization or electrolysis is recycled back to treat incoming waste material. Prior to being leached, the waste material may be roasted at temperatures greater than 500°C. The roasting causes a decomposition of the franklinite zinc oxide- iron oxide complex into zinc oxide, iron oxide and other components. While some iron oxide is reduced from Fe 2 0 3 and Fe 3 0 4 to FeO, no elemental iron is produced during the roasting step. Additionally, iron and iron oxides are not soluble to any degree in the basic leaching solution. If the waste material is first leached by a dilute sulfuric acid or ammonium bisulfate solution, zinc oxide, cadmium oxide, copper oxide and lead chloride all react with the sulfuric acid or ammonium bisulfate. Lead sulfate is formed which is insoluble and removed by filtration. Leaching can continue until all of the leachable copper and cadmium is dissolved. Zinc oxide or zinc hydroxide then can be added to the sulfur-based leach filtrate to increase the pH, which results in the formation of insoluble basic sulfate salts of iron, tin, copper and lead, which are removed as a precipitate. Once the amount of impurities in the filtrate solution has been reduced, the filtrate is subjected to a cementation using zinc metal. The zinc can be precipitated from the filtrate solution to form fine zinc sulfate crystals which are filtered from the solution. Recrystallization of the crude zinc sulfate will result in a high purity zinc sulfate product. The solution remaining after crystallization contains dissolved zinc sulfate and can be recycled. In the cementation step, lead, cadmium and copper plate out on zinc particles introducted into the solution, thereby forming a cake of waste metals which is filtered and removed from the solution. This waste metals cake may be further processed to separate and purify component elements such as lead and copper. The waste metal cake is washed with water and transferred to a vessel containing sulfuric acid which dissolves zinc, cadmium and copper present in the waste metal cake. Lead metal, however, is not soluble in sulfuric acid and any lead oxide present in the cake will dissolve and reprecipitate as lead sulfate. The resulting solid is filtered, washed with water, and dried under nitrogen. This solid is mainly lead metal having trace impurities of lead oxide, lead suli ' are, copper, zinc and cadmium. The remaining sulfuric acid solution contains cadmium and zinc with small amounts of copper. The cadmium may be removed electrochemically by placing zinc metal sheets in the solution to produce a cadmium spcnge. Alternatively, electrolysis can be used to recover the cadmium. The remaining solution is mainly zinc and sulfuric acid, which may be recycled into the primary lech solution to eventually recover the zinc as zinc oxide. The lead cake usually contains tin as well. Hot ammonium chloride (NH 4 C1) can be used to leach the lead cake that is removed after adding the sulfur-based leachant to the waste material, forming a soluble ammonium chloride complex of lead chloride (PbCl 2 ) in solution as the leachate and a tin cake precipitate. The low solubility of PbCl 2 , as well as the high solubility of ammonium chloride and other potential impurities (copper, zinc salts) allowed a high purity of lead chloride to be produced in two cold water washings of the crystalline product. Precipitation products resulting from the neutral filtration obtained by adding zinc oxide to the sulfur-based leach filtrate can be converted into soluble oxides by roasting at high temperature. These precipitation products are mostly sulfate salts of tin, copper and iron. Copper solids can be reclaimed from the sulfur-based filtrate, treated with a dilute acid, and then treated at high temperature in a furnace. Cadmium solids obtained from the cementation steps can be dissolved by sulfuric acid resulting in soluble sulfates of zinc and cadmium being formed. Tin left unleached from the lead cake is made soluble with hydroxide solutions, especially NaOH and KOH. These stannates solutions can be purified with the use of a soluble sulfhydrate salt. Zinc/tin insolubles can be treated with hot concentrated sulfuric acid. The zinc/tin insolubles can be used to produce zinc sulfate. In the leaching step, the zinc and/or zinc oxide dissolves in the leaching solution along with other metal oxides contained in the waste material, such as lead oxide and cadmium oxide. The resultant solution is filtered to remove the undissolved materials, such as iron oxides. Finely powdered zinc metal can be added to the resultant solution at a temperature of about 90°C or above. A dispersant may be added at this point to prevent the finely powdered zinc metal from flocculating and becoming less effective. Through a.ι electrochemical reaction, lead metal and some cadmium plates out on the surface of the zinc metal particles. The addition of sufficient powdered zinc metal results in the removal of virtually all of the lead and cadmium from the resultant solutio . The resultant solution is filtered to remove the solid lead, zinc and cadmium. The filtrate then is cooled to a temperature of between about 20°C and 60°C resulting in the crystallization of a mixture of zinc compounds. The crystallization step helps to achieve a high purity zinc oxide of controlled particle size. During the crystallization step, the filtrate can be cooled to its final temperature by controlling the cooling profile. The use of a reverse, natural cooling profile is preferred as its results in a more desirable nucleation to crystal growth ratio. The filtrate contains a significant amount of diamino zinc dichloride, or other complex compounds which involve zinc amino complexes, as well as hydrated zinc oxide and hydroxide species. The solid precipitate is filtered from the solution, the solution recycled, and the solid precipitate washed with water at a temperature between about 25°C and 100°C. The diamino zinc dichloride dissolves in the wash water leaving the majority of the hydrated zinc oxide species as the precipitated solid. The precipitated solid then is filtered from the solution, the resulting solution being recycled, and the solid precipitate placed in a drying oven at a temperature above 100°C and preferably between about 100°C and 350°C, resulting in a dry white zinc oxide powder. These additional steps allow the production and recovery of substantially pure zinc oxide. Alternatively, the filtrate can be subjected to electrolysis to recover zinc metal. Lead, zinc, and cadmium removed during the cementation step may be separated and purified through further processing to recover products suitable for resale. It is an object of the present invention to provide a method for recovering zinc oxide from waste materials which contain other metals, such as iron oxide, lead oxide, cadmium and other materials in which all leaching and washing solutions are recycled for further use, and no leaching or washing solutions are disposed of into the sewers or the environment. Another object of the present invention is to provide a method for recovering zinc oxide which also results in the precipitation in elemental form of any lead and cadmium metals contained in the starting materials. Another object of the present invention to provide a method for recovering zinc oxide in which all of the zinc can be recycled so that all of the zinc eventually will be converted to zinc oxide. An additional object of the present invention is to provide a method for recovering zinc metal from a waste material stream, and the separation and purification of lead and cadmium contained in the waste materials, such that these metals may be recovered and resold. Another object of the present invention is to provide a method for recovering zinc metal, zinc oxide and/or iron oxide which is economical, quick and efficient. A further object of the present invention is to provide a method for recovering iron oxide which can be used as is as a feedstock for steel production processes. Another object of the present invention is to provide a method for producing direct- reduced iron from iron oxide recovered as a residue from an ammonium chloride leached waste material, such as fly ash or flue dust. These objects and other objects, features and advantages of the present invention will become apparent to one skilled in the art when the following Detailed Description of a Preferred Embodiment is read. BRIEF DESCRIPTION OF THE DRAWING Fig. 1 is a schematic of the overall recovery process incorporating this invention. Fig. 2 is a basic flow diagram of the process of this invention. Fig. 3 is a basic flow diagram of the process of this invention using a sulfur- based leachant. Fig. 4 is a basic flow diagram of an alternative process to what is shown in Fig. 3. DETAILED DESCRIPTION OF A PREFERRED EMBODIMENT The method for recovering chemical and metal values disclosed herein is carried out in its best mode in recovering these materials from the waste streams of industrial or other processes. A typical industrial waste stream used is a flue gas where the charge contains galvanized steel, having the following percent composition: TABLE I Analysis of Flue Dust Component Weight Percent zinc oxide 39.64 iron oxide 36.74 lead oxide 5.72 inert materials 9.10 calcium oxide 2.80 potassium oxide 2.41 manganese oxide 1.29 tin oxide 1.13 aluminum oxide 0.38 magnesium oxide 0.33 chromium oxide 0.16 copper oxide 0.06 silver 0.05 unidentified materials 0.22 TOTAL 100.00 1 siliceous material, such as slag, with carbon granules occluded. 1 molybdinum, antimony, indium, cadmium, germanium, bismuth, titanium, nickel and boron. General Process Description Generally, the present process is a continuous method for the recovery of values from waste material streams which comprise zinc compounds, comprising the steps of: a. roasting the waste material at an elevated temperature and in a reducing atmosphere; b. treating the waste material with a leaching solution at an elevated temperature to form a product solution which comprises dissolved zinc and dissolved zinc oxide whereby any iron oxide in the waste material will not go into solution; c. separating the product solution from any undissolved materials present in the product solution including any of the iron oxide and further treating the iron oxide cake to recover an iron-based product; d. adding zinc metal to the product solution whereby any lead and cadmium ions contained within the product solution are displaced by the zinc metal and precipitate out of the product solution as lead and cadmium metals; e. separating the product solution from the lead and cadmium metals which may be subjected to further processing, thus allowing their purification and recovery; f. lowering the temperature of the product solution thereby precipitating the zinc component as a mixture of crystallized zinc compounds, and separating the precipitated zinc compounds from the product solution; g. washing the zinc compounds solids with a wash water thereby solubilizing certain of the zinc compounds, and separating the remaining zinc compounds solids from the solution; h. recovering copper, tin and other values from the remaining solution; and i. drying the remaining zinc compounds solids at a temperature of at least 100°C whereby the resulting product is zinc oxide of 99% or greater purity. The present process also can comprise a two-stage leaching process for even greater yields of zinc oxide. The two-stage process comprises the additional steps of: a. treating the waste material a first time with an ammonium chloride solution at an elevated temperature to form a first product solution which comprises dissolved zinc constituents whereby any iron oxide in the waste material will not go into solution; b. separating the first product solution from the undissolved waste material compounds present in the first product solution including any of the iron oxide; c. roasting the undissolved waste material compounds at an elevated temperature and in a reducing atmosphere; d. treating the roasted undissolved waste material compounds a second time with the ammonium chloride solution at an elevated temperature to form a second product solution which comprises dissolved zinc constituents whereby any iron oxide remaining in the roasted undissolved waste material compounds will not go into solution; e. combining the first and second product solutions to form a combined product solution, and subjecting the combined product solution to the remainder of the process. Referring to Fig. 1, a preferred embodiment of the process is shown. Subprocess 100 comprises the digestion and filtration steps. Subprocess 200 comprises the direct reduced iron production steps. Subprocess 300 comprises the chemical values recovery steps. Subprocess 400 comprises the enhanced direct reduced iron production steps. Subprocess 500 comprises the feed process for using and producing and iron feedstock process. Feed streams such as iron poor waste fume streams from electric arc furnaces 12 and other furnaces such as reduction furnaces or smelters 14 are filtered in a baghouse 16. Other feed streams such as iron rich direct reduced iron and pig iron, as well as scrap iron and steel, are subjected to the iron or steel making process. Exhaust fumes from such processes, which typically include an electric arc furnace or other reduction furnace, also are filtered in a baghouse 16. The constituents filtered out in baghouse 16 comprise the waste stream feed to subprocess 100. In subprocess 100, the waste stream feed is leached in digester 18 with ammonium chloride, preferably at approximately 90°C and approximately 23% by weight concentration. Constituents soluble in ammonium chloride go into solution, while constituents insoluble in ammonium chloride, such as iron oxides, precipitate out. The precipitates are filtered from the solution in filter 20. The filtered solution is sent to cementer 22, and subjected to subprocess 200 to recover other chemical values. The precipitate, which is an iron cake (IC), is sent to subprocess 300. In subprocess 300, the precipitate is dried and crushed in dryer/crusher 24. Exhaust gases from dryer/crusher 24 may be sent to a baghouse such as baghouse 16, but more typically are sent to an air scrubber such as air scrubber 26 for cleaning, as the exhaust gases from dryer/crusher 24 typically do not have a significant quantity of recoverable constituents. The dried and rushed precipitates are compacted in compactor 28 and sent to a reduction furnace or smelter 14. In reduction furnace 14, the dried and crushed iron cake is roasted at between 980°C and 1315°C, producing an enriched iron cake (EIC) which can comprise direct reduced iron (DRI) and pig iron, which can be in liquid form. The EIC can be compacted in a second compactor 30, and then cooled by cooling water in a cooling conveyor 32, to produce the DRI. The DRI then can be used as the feed to a steel mill EAF, and the process cycle starts over. Exhaust fumes from the reduction furnace 14 are sent to scrubber 34, which preferably is a recirculating wet scrubber using water or an aqueous ammonium chloride solution. Exhaust fumes from EAFs such as EAF 12 also can be sent to scrubber 34. In scrubber 34, the exhaust fumes are scrubbed and the scrubbed off-gas released. The water or aqueous ammonium chloride solution containing the constituents scrubbed from the exhaust fumes is sent either to cementer 22 or digester 18, depending on purity; more pure solutions typically are sent to digester 18, while less pure solutions typically are sent to cementer 22. In the preferred embodiment, the furnace 12, 14 off-gases comprise ZnO and other particulate impurities. If the off-gases are scrubbed in scrubber 34, the water balance is maintained using a temperature control such as heat exchanger 36. Additionally, the concentration of ZnO and other solubles in the scrubbing liquid may be controlled by the addition of water W to the cementer 22, or ammonium chloride to the scrubber 34. As discussed above, if an ammonium chloride solution is used as the scrubbing liquid, it is preferred to maintain the solution at approximately 90°C and approximately 23% NH 4 C1. I. Initial Ammonium Chloride Leach The initial leaching solution preferably is ammonium chloride, sulfuric acid, or ammonium bisulfate. The ammonium chloride solution in water is prepared in known quantities and concentrations. If the two-stage leaching process is used, the feed material which contains the zinc species, such as the waste material flue dust described in Table I or any other feed material source which contains zinc or zinc oxide mixed with other metals, is added to the ammonium chloride solution at a temperature of about 90°C or above. Otherwise, the feed material is roasted. The zinc and/or zinc oxide dissolves in the ammonium chloride solution along with other metal oxides, such as lead oxide and cadmium oxide. A 23% by weight ammonium chloride solution in water at a temperature of at least 90°C provides the best solubility of zinc oxide. Concentrations of ammonium chloride below about 23%) do not dissolve the maximum amount of zinc oxide from the flue dust, and concentrations of ammonium chloride above about 23% tend to precipitate out ammonium chloride along with the zinc oxide when the solution is cooled. Iron oxide and inert materials such as silicates will not dissolve in the preferred solution. The zinc oxide, as well as smaller concentrations of lead or cadmium oxide, are removed from the initial dust by the dissolution in the ammonium chloride solution. The solids are then filtered from the leaching solution. The solid remaining after this leaching step contains zinc, iron, lead and cadmium, and possibly some other impurities. The remaining solid then is roasted in a reducing atmosphere, typically at a temperature greater than 420°C and often at 700°C to 900°C. The reducing atmosphere can be created by using hydrogen gas, simple carbon species gases such as carbon dioxide, or by heating the material in an oxygen containing gas in the presence of elemental carbon. The carbon preferably is in the form of dust or pellets. Typical roasting times are from 30 minutes to 4 hours. As discussed above, the waste dust first may be roasted and second may be leached, omitting the first leaching step. To recover the zinc oxide, while the filtered zinc oxide and ammonium chloride solution is still hot, that is at a temperature of 90°C or above, finely powdered zinc metal is added to the solution. Through an electrochemical reaction, lead and cadmium in solution plates out onto the surfaces of the zinc metal particles. The addition of sufficient powdered zinc metal results in the removal of virtually all of the lead of the solution. The solution then is filtered to remove the solid lead, zinc and cadmium. This cementation step is preferably carried out by adding approximately two times the stoichiometric amount of zinc and dispersant. A second polishing step may then be performed by adding a small amount of powdered zinc and dispersant as necessary. Zinc powder typically aggregates to form large clumps in the solution. Rapid agitation typically will not prevent this aggregation from occurring. To keep the zinc powder suspended in solution, any one of a number of water soluble polymers which act as antiflocculants or dispersants may be used. In addition, a number of surface active materials also will act to keep the zinc powder suspended, as will many compounds used in scale control. These materials only need be present in concentrations of 10 - 1000 ppm. Various suitable materials include water soluble polymer dispersants, scale controllers, and surfactants, such as lignosulfonates, polyphosphates, polyacrylates, polymethacrylates, maleic anhydride copolymers, polymaleic anhydride, phosphate esters and phosponates. A discussion of these various materials can be found in the literature, such as Drew, Principles of Industrial Waste Treatment, pages 79-84, which is incorporated herein by reference. Flocon 100 and other members of the Flocon series of maleic-based acrylic oligomers of various molecular weights of water soluble polymers, produced by FMC Corporation, also are effective. Adding the dispersants to a very high ionic strength solution containing a wide variety of ionic species is anathema to standard practice as dispersants often are not soluble in such high ionic strength solutions. At this stage there is a filtrate rich in zinc compounds and a precipitate of lead, cadmium and other products. The filtrate and precipitate are separated, with the precipitate being further treated to capture chemical values. The filtrate may be treated in several manners, two. of which are preferred. First, the filtrate may be cooled resulting in the crystallization and recovery of zinc oxide. Second, the filtrate may be subjected to electrolysis resulting in the generation and recovery of metallic zinc. To recover zinc oxide, the filtrate is cooled to a temperature of between about 20°C and 60°C resulting in the crystallization of a mixture of zinc compounds. The mixture contains a significant amount of diamino zinc dichloride, or other complex compounds which involves zinc amino complexes, hydrated zinc oxides and hydroxide species. Crystallization helps to achieve a high purity zinc oxide of controlled particle size, typically through control of the temperature-time cooling profile. Reverse natural cooling, that is cooling the solution slower at the beginning of the cooling period and faster at the end of the cooling period, is preferred to control the nucleation to crystal growth ratio and, ultimately, the crystal size distribution. The precipitated crystallized solid is filtered from the solution and washed with water at a temperature of between about 25°C and 100°C. The filtered solution is recycled for further charging with feed material. The diamino zinc dichloride dissolves in water. Very little of the hydrated zinc oxide dissolves in the water. This resultant solution then is filtered to remove the hydrated zinc oxide species. The solid hydrated zinc oxide species filtered from the solution is placed in a drying oven at a temperature of over 100°C. After a sufficient drying period, the resultant dry white powder is essentially pure zinc oxide. To ensure that the material is free of chloride, it is preferable to heat the zinc oxide to a higher temperature. Diamino zinc dichloride decomposes at 271°C and ammonium chloride sublimes at 340°C. Therefore, heating the zinc oxide to a temperature above 271°C is useful. The drying temperature should be kept below approximately 350°C to prevent the sublimation of significant amounts of ammonium chloride. Therefore, it is preferable to dry the zinc oxide at a temperature in the range of 271 °C to 350°C. Typically, the zinc oxide should be dried in this temperature range for approximately 2 to 60 minutes, and preferably from 5 to 20 minutes. A 10 minute drying time has been found to be a satisfactory average. As the zinc, lead and cadmium contained in the feed materials are amphoteric species, by using ammonium chloride solution these species will go into solution, while any iron oxide present in the feed material will not go into solution. Other solutions, such as strong basic solutions having a pH greater than about 10 or strong acidic solutions having a pH less than about 3, also can be used to dissolve the zinc, lead and cadmium species; however, if strong acidic solutions are used, iron oxide will dissolve into the solution, and if strong basic solutions are used, iron oxide will become gelatinous. The lead and cadmium can be removed from the ammonium chloride solution through an electrochemical reaction which results in the precipitation of lead and cadmium in elemental form. The difference in solubility between diamino zinc dichloride and zinc oxide in water and in ammonium chloride solutions allows the selective dissolution of the diamino zinc dichloride such that pure zinc oxide can be recovered. This also can be used in the crystallization step to improve the relative amounts of diamino zinc dichloride and zinc oxide species form. Significantly, all of the zinc can be recycled so that all of the zinc eventually will be converted into zinc oxide. Example 1 Prior Art A metal dust of composition listed in Table I of the Burrows patent is added to 23% by weight NH 4 C1 solution (30g NH 4 C1 per lOOg H 2 0), as discussed in the Burrows patent, in the amount of 1 gram of dust per 10 grams of solution. The solution is heated to a temperature of 90°C and stirred for a period of 1 hour, during which the zinc oxide in the dust dissolves. The remaining solid, which has a composition of approximately 60% iron oxide, 5% calcium oxide, 5% manganese, 30% other materials, is filtered out of the solution. Powdered zinc then is added to the filtrate at 90°C, causing the precipitation of waste metals, the precipitate containing about 60% lead, 40% zinc, 2% cadmium and 8% other metals. The waste metals then are filtered out and the filtrate is cooled to room temperature (between about 18°C and 30°C) over a period of about two hours. The solution then contains a white precipitate which is not essentially pure zinc oxide but is a mixture of hydrated zinc phases and diamino zinc dichloride. Example 2 A metal dust of composition listed in Table I is added to 23% weight NH 4 C1 solution (30g NH 4 C1 per lOOg H 2 0). 1 gram of dust is used per 10 grams of solution. The solution is heated to a temperature of 90°C and stirred for a period of 1 hour. During this period the zinc oxide in the dust dissolves. The remaining solid, having a composition of approximately 60% iron oxide, 5% calcium oxide, 5% manganese, 30% other materials, is filtered out of the solution. Powdered zinc then is added to the filtrate at 90°C. This causes the precipitation of waste metals, the waste metal precipitate containing about 60%) lead, 40% zinc, 2% cadmium and 8% other metals. The waste metals then are filtered out and the filtrate is cooled to room temperature (between about 18°C and 30°C) over a period of about two hours. The solution then contains a white precipitate. The precipitate is a mixture of hydrated zinc phases and diamino zinc dichloride. The hydrated zinc phases are virtually insoluble in water; however, diamino zinc dichloride is quite soluble in water. A portion of the white precipitate was dried and zinc oxide and diamino zinc dichloride, as well as some other components, are present. The white precipitate then is filtered from the solution and resuspended in water at 90°C and stirred for a period of one hour. This suspension then is filtered and product dried in an oven at 140°C. The resulting white solid is 99%+ zinc oxide. The amount of zinc oxide obtained was 47.8% of the mass of the original precipitate. The ZnO recovered by this Example also had the following components: lead: 866 ppm potassium: 45 ppm calcium: < 25 ppm manganese: < 25 ppm chromium: < 25 ppm Example 3 The procedure of Example 1 is followed until the step in which the zinc containing filtrate is cooled. Since the diamino zinc dichloride is more soluble then the majority of the other possible precipitates in the ammonium chloride solution (except for zinc chloride which is so soluble that it will not appear), the diamino zinc dichloride appears as a larger fraction of the solid as the temperature declines. The filtrate was divided into fractions and each fraction cooled to a different temperature. The resulting solids were than filtered, resuspended in water at 90°C for one hour, filtered and dried. The result was 99%+ zinc oxide in all cases; however, the yield changed with the temperature to which the fraction was cooled as follows: Crystallization Percent ZnO Temp f°Q Obtained 75 65 70 60 60 60 50 50 Crystallization at temperatures from 60°C up improve the yield of ZnO. Example 4 ZnO also can be recovered from the wash water used in the process. Fifty grams of dried zinc phase precipitate (the solid obtained after cooling to room temperature) obtained using the procedure of Example 1 is added to 1 OOg of H 2 0 at 90°C. The diamino zinc dichloride dissolves while only a small amount of the other zinc phases dissolve (due to the ammonium chloride which is part of the diamino zinc dichloride). The remaining solid is filtered out and is dried resulting in 99%+ zinc oxide. The filtrate is cooled to room temperature and the solid filtered out. The solid is again a mixture of hydrated zinc phases and Zn(NH 3 ) 2 Cl 2 . The solid is washed in 90°C water, filtered and dried resulting in 99% ZnO. The yield is 40% ZnO. The yield also can be improved by crystallizing at higher temperatures. In addition, the same wash water can be used again instead of fresh water since this part of the process relies on the change in Zn(NH 3 ) 2 solubility with temperature. Example 5 The source of the zinc does not have to be dust. If pure ZnO is added to a 23% NH 4 C1 solution, the result is the same. As an example, saturated solutions of ZnO in 23% ammonium chloride solutions were prepared at temperatures ranging from 40°C - 90°C. These solutions were then cooled to room temperature over a period of 1 - 2 hours. The resulting solid was filtered, washed in 90°C water, and dried. As before, the original solid was a mixture of hydrated zinc phases and diamino zinc dichloride, the final product was 99% ZnO. The yields obtained as a fraction of the original solid precipitate are listed below: Temperature ZnO Added ZnO Obtained in Product (°C) 90 14.6 64 80 13.2 62 70 8.4 60 60 5.0 60 50 3.7 45 40 2.3 40 These results indicate that the yield of ZnO improves as the amount of dissolved ZnO increases (which also means higher temperatures). Example 6 This example shows the present procedure run in a continuous crystallization process to increase the throughput and to maximize the zinc oxide yield. The procedure of Example 1 is followed until the step in which the waste metals are precipitated out of the zinc oxide containing solution. 190 liters of the solution are used as the feedstock for a continuous crystallization process. The solution, initially at about 90°C, is pumped into a 3.8 liter jacketed crystallizer equipped with baffles and a draft tube at a rate of 3.8 liters per hour. The crystallizer jacket temperature is maintained at about 55°C by use of a constant temperature circulating bath. The solution and the product crystals are removed continuously so as to keep the volume of material present in the crystallizer constant. At steady state, the temperature in the crystallizer is maintained at about 60°C. The product solution flows through a filter which collects the solid. The solid product then undergoes the washing and drying steps as discussed in Example 2. The yield of zinc oxide from this continuous crystallization process is about 60% of the total mass of the solid crystallized. The crystallizer can be operated at lower temperatures; however, lower temperatures decrease the final yield of zinc oxide obtained as shown in Example 3. The flow rate employed also can be altered along with the crystallizer jacket temperature to minimize crystallization on the crystallizer vessel walls. In addition, these variables, along with the crystallizer jacket temperature, can be used to alter the crystal size distribution. Example 7 Metal dust of the composition shown in Table I is digested in 23% ammonium chloride solution at about 90°C. One gram of zinc metal dust is used per 10 grams of ammonium chloride solution. After one hour, the remaining solid is filtered out of the solution. 500 cc of the solution is put into each of two vessels with stirrers and the temperature of the solutions is maintained at 90°C. 500 ppm of Flocon 100 is added to one of the vessels, while nothing is added to the other vessel. Four-tenths of a gram (0.4g) of 200 mesh zinc dust then is added to each of the two solutions. In the solution containing the Flocon 100, the zinc dust remains suspended, while in the other solution containing no additive, the zinc dust flocculates. After one hour at about 90°C, the solids are filtered out of each of the solutions, weighed and analyzed. The mass of solid from the solution which contained the dispersant was 1.9 grams and comprised approximately 21% zinc, 75% lead, 2% cadmium and the remaining amount other metals. The mass of solid obtained from the solution with no dispersant was 1.2 grams and comprised approximately 33% zinc, 63% lead, 2% cadmium and the remaining amount other metals. From this example, it can be seen that the additional step of adding a dispersant increases the amount of lead and other metals removed from the waste stream in solution. Roasting Step The zinc dust obtained from various sources have shown by chemical analysis to contain from 20% - 25% zinc by weight. Certain crystalline phases exist in this dust, specifically zinc oxide. The positive identification of the iron phase is complicated by the possible structural types (i.e. spinel type iron phases showing almost identical diffraction patterns). The zinc oxide (as well as smaller concentrations of lead or cadmium oxide) are removed from the initial dust by dissolution in a concentrated ammonium chloride solution (23% ammonium chloride). Filtration and washing of the undissolved species leaves a residual powder. This powder shows a zinc concentration that is still elevated (i.e., 10 - 13% by weight), but that is not zinc oxide. All crystalline phases can be identified by spinel type phases. This powder is a combination of franklinite (Fe, Mn, Zn)(FeMn) 2 0 4 , and magnetite (iron oxide: Fe 3 0 4 ). Both of these phases have very similar spinel type structures. The zinc within the franklinite cannot be removed by dissolution with ammonium chloride. In addition, no simple extraction process will remove zinc from this stable oxide phase. Although this compound is very stable to oxidation (all elements in the highest oxidation state), it is relatively easy to destroy this compound by reduction at elevated temperatures. The reduction of the franklinite in an atmosphere that cannot readily reduce zinc oxide or allow for the rapid oxidation of zinc to zinc oxide following reduction and subsequently recover the zinc oxide by ammonium chloride extraction or sublimation (the highly volatile zinc oxide will sublime from the mixture at relatively low temperatures and recondense at the cold locations of the roaster). The alternative will be complete reduction of the franklinite to zinc metal and removal by distillation or separation of the molten zinc by settling techniques. The roasting step can be carried out prior to the initial eaching step, or between a first and second leaching step. The waste dust is heated to temperatures greater than 500°C, causing a reaction which causes a decomposition of the stable franklinite phase into zinc oxide and other components, and yet does not allow for the complete reduction of zinc oxide to zinc metal. The resulting zinc oxide can be removed by sublimation or extraction with an ammonium chloride solution, such as by following the steps detailed above under the general process. The resulting material after extraction has less than 1% by weight zinc. The dust can be roasted using many conventional roasting processes, such as, for example, direct or indirect heating and the passing of hot gases through the dust. Non-explosive mixtures of reducing gases, such as hydrogen gas, nitrogen, carbon dioxide, or simple carbon species, can be passed through the dust. Heterogeneous gas phase reductions are faster than solid state reductions at lower temperatures and therefore suggest the use of carbon monoxide. The carbon monoxide can be generated in situ by mixing the franklinite powder with carbon and heating in the presence of oxygen at elevated temperatures. The oxygen concentration is controlled to optimize CO production. The carbon monoxide may be introduced as a separate source to more clearly separate the rate of carbon monoxide preparation from the rate of Franklinite decomposition. The prepared zinc oxide then can be removed by either ammonium chloride extraction or sublimation. The roasting process also can be performed to complete reduction by using carbon at high temperatures and collecting zinc metal that will melt at very low temperatures (420°C) and boil at 907°C. In this process, zinc metal is obtained that, if desired, can be converted readily to the oxide by air roasting. Example 8 A dust containing 19.63% Zn, 27.75% Fe, 1.31% Pb, 9.99% Ca, and 0.024% Cd (analysis based on elements not oxides) was leached at 100°C in a 23% ammonium chloride solution. The solid remaining after the leaching process was dried and analyzed to contain 12.67% Zn, 4.6% Ca, 35.23% Fe, 0.7% Pb, and 0.01% Cd. This material was placed in a quartz boat in the presence of activated carbon and heated at 900°C for two hours in an atmosphere of 95% N 2 and 5% 0 2 . After two hours, the material was removed and added to a 23% ammonium chloride solution at 100°C. The material was filtered and dried at 140°C for one hour to determine its composition. Analysis of this remaining solid was 42.84%) Fe, 0.28%) Zn, < 0.1% Pb, and < 0.01%) Cd. The leached-roasted-leached material then can be subjected to the remainder of the general process to recover zinc oxide. Example 9 A dust with composition given in Table I is leached in 23% ammonium chloride solution for 1 hour at 100°C. The solid remaining (which contained 14% Zn) was placed in a quartz boat and heated to 700°C in an atmosphere of 8% H 2 and 92% Ar. The material was cooled and reheated at 100°C in 23% ammonium chloride solution at 100°C. The solid was separated, dried and analyzed for zinc. The zinc was found to be less than 1%. The leached-roasted-leached material then can be subjected to the remainder of the general process to recover zinc oxide. Crystallization Step The purpose of the crystallization/washing step is to produce a high purity zinc oxide of controlled particle size, and is accomplished through control of the temperature-time profile during cooling. The crystallization step takes the filtrate from the cementation step at 90-100°C. This filtrate contains the dissolved zinc with small amounts of trace impurities such as lead and cadmium. To prepare a pure zinc oxide it is necessary to prevent the formation of solvent inclusions inside the grown crystals. Solvent inclusions are pockets of liquid trapped as a second phase inside the crystals. Control of crystallization conditions can be employed to reduce these impurities. Example 10 A dust of the composition given in Table I is taken through the leaching and cementation steps. After cementation the filtrate is maintained at 100°C. 500 ml of this filtrate is placed in a jacketed stirred vessel with the jacket temperature at 100°C. The temperature is lowered in the crystallizer as follows: Time (minutes) Temperature (°C) 0 100 60 90 120 75 180 55 210 25 The resulting solid was washed and dried employing the procedure described above. The resulting material was analyzed as follows: ZnO 99 + % Lead < 50 ppm Cd < 25 ppm Fe < 25 ppm This cooling profile is known as a reverse natural cooling profile, and is the opposite shape as that which is observed by natural cooling. In a reverse natural cooling profile, the cooling is slower at the beginning and faster at the end; in a natural cooling profile, the cooling is faster at the beginning and slower at the end. This type of cooling profile also is used to control the crystal size distribution (CSD) of the zinc oxide obtained. The cooling profile controls the ratio of nucleation to crystal growth. The ratio of nucleation/growth determines the final CSD. Example 11 A 23%) ammonium chloride solution at 100°C containing 11% by weight dissolved ZnO is divided into 4 portions. Each portion is placed in a jacketed agitated vessel. The cooling profiles in each vessel are given below: Vessel A Vessel B Time (minutes) Temp. (°C) Time (minutes) Temp. (°C) 0 100 0 100 60 75 60 50 120 50 120 37.5 180 25 180 25 Vessel C Vessel D Time (minutes) Temp. (°C) Time (minutes) Temp. (°C) 0 100 0 100 60 87.5 60 87.5 120 75 120 75 180 180 62.5 270 25 The solid is washed using the usuεl procedures described previously. The average size and size distribution of these materials were measured using a laser light scattering particle size analyzer. The results were as shown below: Vessel Mean Size A 22 B 19 C 27 D 37 The results show that controlling the temperature with a reverse natural cooling curve results in a larger average size than by linear cooling (A) or natural cooling (B). This principle can be employed to design cooling profiles to produce zinc oxides of a desired average size and distribution. Recycle To produce pure zinc oxide from waste dust containing zinc efficiently and in a safe and cost effective way, the process recycles all zinc which is not removed from the leachate in the crystallization step. The diamino zinc dichloride which is redissolved in water in the washing step also is recycled. The recycle of zinc increases the overall zinc concentration in liquid solution in the process. This allows the crystallizer to operate at a higher temperature due to the rapid change in zinc oxide solubility with temperature in ammonium chloride solution. Example 12 By controlling the recycle, the steady state zinc concentration can be raised to 7g/100g of solution. If the outlet of the crystallizer is kept at 60°C, 3g/100g solution of solid will crystallize (the solid is a mixture of zinc oxide and diamino zinc dichloride). The system does not have to be cooled further since this is an efficient way to operate to conserve energy (one does not have to cool then reheat the solution). In addition, operating at the higher Zn concentration improves the ratio of ZnO/diamino zinc dichloride produced in the crystallizer. The recycle has the advantage that the solution becomes saturated relative to certain materials present in the dust, such as CaO. When this occurs, CaO no longer is leached from the dust but remains with the iron in the iron cake. This increases the value of the cake since CaO is still present and will not have to be added when the iron cake is fed to a furnace in steel making. Another important advantage in that there is no liquid effluent in this process. The only products are solid (iron cake, zinc oxide, waste metals), which are then sold for use in various industrial processes. No waste is produced since all liquid is recycled. Carbon Addition For Recovery Of Iron-Carbon And Direct-Reduced Iron Products The present process also produces a high-quality iron-carbon cake as a residual product. The iron oxide contained in the waste stream does not go into solution in the leaching solution, but is filtered from the product solution as undissolved material. This iron oxide cake can be used as is as the feedstock to a steel mill; however, it becomes more valuable if reduced by reaction with elemental carbon to produce an iron-carbon or direct-reduced iron product. One preferred method for producing such an iron-carbon or direct-reduced iron product from the waste material comprises the steps of treating the waste material with an ammonium chloride solution at an elevated temperature to form a product solution which comprises dissolved zinc and dissolved zinc oxide whereby any iron oxide in the waste material will not go into solution, adding carbon to the product solution whereby the carbon will not go into solution, and then separating the product solution from any undissolved materials present in the product solution including any of the iron oxide and the carbon. A mixture of iron oxide and carbon is used by the steel industry as a feedstock for electric arc furnaces. The iron oxide cake which is removed as undissolved material from the leaching step is primarily iron oxide, being a mixture of Fe 2 0 3 and Fe 3 0 4 . The iron cake can be made into the mixture of iron oxide and carbon by adding elemental carbon to the iron oxide cake in several manners. First, carbon can be added to the leaching tank at the end of the leaching step but before the undissolved materials are separated from the product solution. Since the carbon is not soluble in the leaching solution and will not react in an aqueous solution, the iron cake and the carbon can be separated from the product solution and made into a hard cake. Different size carbon, such as dust, granules, or pellets, may be used depending on the desires of the steel makers. Second, the carbon can be added to the iron oxide after the iron oxide has been separated from the product solution. The dried iron oxide and the carbon can be ribbon blended in a separate process. The product solution from this process can be treated similarly to the treatment of the product solution in the general method disclosed above. Separation And Recovery Of Metal Values From Waste Metals Cake The present process also can be operated to recover metal values from the waste metals cake filtered out after the cementation step. A preferred method for recovery of these metal byproducts comprises: a. washing the waste materials or the waste metals cake filtered from the solution after the cementation step with water; b. treating the waste materials or the waste metals cake with sulfuric acid or ammonium bisulfate, which will dissolve zinc, cadmium and copper present in the waste metals cake; c. removing lead metal, which is insoluble in sulfuric acid, from the solution, dissolving and reprecipitating and lead oxide as lead sulfate; d. recovering copper; e. electrochemically removing dissolved cadmium from the solution by placing zinc metal sheets into the solution onto which the cadmium plates to produce a cadmium sponge; and f. recovering tin and zinc/tin solubles. The lead solids may be filtered, washed with water, and dried under an inert gas such as nitrogen to produce a relatively pure lead metal. Some impurities are present in the form of lead oxide, lead sulfate, copper, zinc, and cadmium. Electrolysis may be used to plate out cadmium in the solution as a sponge on other cathodic materials. The solution remaining is mainly zinc in sulfuric acid, which can be recycled back to the leach solution for eventual recovery of the zinc as zinc oxide. In the preferred lead and cadmium recovery process, the waste metals cake is leached by the addition of a dilute sulfuric acid solution which forms a slurry. The reaction of the zinc oxide and sulfuric acid is an exothermic reaction. The reactions of cadmium oxide, copper oxide and lead chloride with sulfuric acid are relatively slower. Lead sulfate is formed which is insoluble and removed by filtration at this point. The cadmium solids obtained from the cementation steps can be dissolved by sulfuric acid resulting in soluble sulfates of zinc and cadmium being formed. The zinc sulfate is recycled to the acid leach. This treatment causes the following major reactions to occur: (1) ZnO + H 2 S0 4 --> Zn 4" " + S0 4 " + H 2 0 (fast, exothermic) (2) CdO + H 2 S0 4 --> Cd* 4 + S0 4 " + H 2 0 (3) CuO + H 2 S0 4 --> Cu^ + S0 4 ~ + H 2 0 (slower) (4) PbCl 2 + H 2 S0 4 --> PbS0 4 (insoluble) + HC1 Thus, metallic and sulfate ions are formed along with insoluble lead sulfate. Additional sulfuric acid may be added until the solution remains acid (pH<2 and preferably pH~l). In this way, an economical minimum of acid is consumed. The rapid rate of reaction (1) allows this to be done with little delay. Reaction (1) releases a great deal of heat, and external heating of the solution may not be required. Reactions (2) and (3) take longer to go to completion during the leach stage and the levels of Cd and Cu in solution may be monitored. Leaching may continue until all of the extractable copper is dissolved. It is preferable that the leachable Cu and Cd be removed before proceeding and that a water rinse or second dilute leach take place in order to rinse the solids clean of any entrapped ions, and prevent contamination of the next leach steps. Soluble lead oxide is converted to the highly insoluble lead sulfate. The abundance of sulfate ions present in solution greatly suppresses the solubility of lead ions. Due to reaction (4), the chloride ions are introduced into the leach liquor. Zinc sulfate targeted for the electro-chemical uses must be kept low in chloride, but even so, the high solubility of zinc chloride makes contamination unlikely, and easy to remove by recrystallization. Other reactions of minor occurrence during the leach include: (5) FeO + H 2 S0 4 — > Fe "1- " + S0 4 " " + H 2 0 (6) Al + 3/2 H 2 S0 4 — > Al^ + 3/2 S0 4 " + 3/2 H 2 (7) As 2 0 3 + 3 H 2 0 — > 2 H 3 As0 3 (soluble in strong acid and base) Potassium, sodium, calcium and magnesium compounds are rendered soluble in the leaching process and taken into solution. Traces of tin and lead also can be found in the solution. Filtering separates the leached material from the solid material. Zinc oxide or zinc hydroxide can be added to the acid leach filtrate to neutralize the solution after reaction (1) above. The addition of zinc oxide or zinc hydroxide causes the formation of the insoluble basic sulfate salts of tin, iron, copper and lead, which precipitate out. This step removes almost all of the tin, iron and lead found in solution. Potassium is removed to some extent as an iron complex salt. Heating the solution during this process will speed the formation of a precipitate, as well as increase the extent of precipitation. The pH levels of the zinc oxide or zinc hydroxide treated filtrate should be in the 5-6 range. The solid formed in this step is referred to as the "neutral precipitate". This process is referred to in the art as jarosite precipitation, or iron purification, as the precipitation of the iron co-precipitates other impurities. Conditions that can be altered include the addition of excess dissolved iron to improve co-precipitation, as well as the addition of oxidizing agents to improve the extent and quality of the iron precipitate. After filtering out the neutral precipitate, the neutral filtrate solution pH is adjusted to become slightly acidic (pH 4-5) by the addition of an acid, preferably sulfuric acid, as illustrated in Fig. 3. The solution then is measured for copper and lead content. A determined amount of finely divided zinc dust (a stoichiometric excess) is added to the neutral filtrate solution at 80-90°C with good mixing. An electrochemical exchange takes place based on the relative position of the components on the electromotive series. Major reactions include: (8) Zn° + Cu " ^ — > Zn^ + Cu° (9) Zn° + Cd 4 — > Zn * + Cd° (10) Zn° + Pb 44 — > Zn * + Pb° Heavy metal ions in the neutral filtrate are reduced to the metallic form and zinc ions enter the filtrate. Initially, these reactions are based only on random collision with zinc metal with the rates of removal being identical. However, as the surface of the zinc becomes replaced by other metals, these reactions follow: (11) Cd° + Cu * — > Cά** + Cu° (12) Cd° + Pb** — > Cd^ + Pb° Cadmium, like zinc, has the ability to replace copper and lead ions in the neutral filtrate, and, as a result, the neutral filtrate becomes almost completely depleted in lead and copper, but the cadmium tends to remain in the neutral filtrate. Advantage can be taken of this characteristic to separate all or nearly of the cadmium from the neutral filtrate in the first cementation step as shown in Fig. 3. Once copper levels have been greatly reduced, observable by the solution becoming clear or by instrumental methods, the solids obtained from the first cementation are copper metal, zinc metal and oxide, cadmium and lead. If desired, additional sulfuric acid may be added directly to the solution to selectively redissolve the zinc and cadmium present. Metallic copper and lead are not affected by dilute sulfuric acid. If additional H 2 S0 4 is added, the reactions include: (13) Zn° + H 2 SO 4 — > Zn * + S0 4 " + H 2 (14) Cd° + H 2 S0 4 — > Cd " " 4 + S0 4 " + H 2 The solution then can be titrated with ZnO to a pH of 4-5. Since the majority of the solid produced is copper, the solid precipitate is referred to as the copper solids, however the copper solids contain other compounds, particularly cadmium and zinc compounds. Due to their fine state of division, the metals in the copper solids rapidly oxidize on exposure to the air. Copper oxide is attacked readily by sulfuric acid, and therefore dissolution takes place in the solution directly after the cementation is complete. Zinc dust cementation can be repeated to remove the cadmium present. By determining the amount of cadmium in solution, a specific amount of zinc dust can be added as before, namely a stoichiometric excess. The solids generated in this step are called the cadmium solids, and are rich in zinc, zinc oxide and cadmium. After the second cementation step, the resulting zinc sulfate solution is heated to evaporate some excess water to reduce its volume in order to precipitate the fine zinc sulfate crystals of the monohydrate form, or alternately, allowed to cool in order to form the heptahydrate crystals. Sulfuric acid is added to restore the acid concentration of the cycling solution to the determined level, and the solution containing some zinc sulfate and other compounds that is not precipitated is returned to repeat the process of Step 1A. Sulfuric acid may be added before the crystallization step in order to produce a higher purity product, if it is beneficial. Recrystallization of the zinc sulfate will produce a very high purity product. The product can be dehydrated if required by heating. In place of treating the zinc rich dust with sulfuric acid as in Step 1A, the zinc rich dust can be treated with ammonium bisulfate (NH 4 HS0 4 ). Ammonium bisulfate is formed by addition of equal molar amounts of ammonia and sulfuric acid: (15) NH 4 OH + H 2 S0 4 — > NH 4 HS0 4 + H 2 0 or, alternatively, by the combination of ammonium sulfate and sulfuric acid: (16) (NH 4 ) 2 S0 4 + H 2 S0 4 — > 2 NH 4 HSO 4 The steps followed in using ammonium bisulfate to leach the zinc dust as shown in Fig. 4 (Step IB) are the same as the steps followed when sulfuric acid leaching is used. However, the presence of ammonium ions produces some double salts which have limited solubility. A 25% by weight solution of the bisulfate was found to be the maximum allowable concentration in order to avoid crystallization of the zinc double salt (NH 4 ) 2 Zn(S0 4 ) 2 at high temperatures. The solution leached with ammonium bisulfate can be subjected to the same treatments as were used with the sulfuric acid leach, that is the zinc oxide neutralization of the leach filtrate and the addition of zinc dust and sulfuric acid to the neutral filtrate. The filtrate then is subjected to the first and second cementation steps as indicated in Fig. 4. After these steps, cooling the solution will result in the formation of double salt crystals. These crystals can be collected and dissolved or the entire solution can be decomposed by the following treatment with ammonia: (17) (NH 4 ) 2 Zn(S0 4 ) 2 + 2 NH 4 OH — > Zn(OH) 2 + 2 (NH 4 ) 2 S0 4 This treatment also can be used with the zinc sulfate solutions: (18) ZnS0 4 + 2 NH 4 OH — > Zn(OH) 2 + (NH 4 ) 2 S0 4 In this process, an excess of ammonium hydroxide should be avoided as it will result in the formation of a soluble zincate ion under highly basic conditions. Zinc hydroxide is very insoluble. The ammonium sulfate produced remains in the solution. The insoluble zinc hydroxide is washed in hot water (approximately 150°C) and converted to zinc oxide by heating: (19) Zn(OH) 2 — > ZnO + H 2 0 The water present becomes increasingly difficult to remove, and much higher temperatures (over approximately 150°C) are required to completely dehydrate the product. The product is somewhat chalk-like and milling is required to break up the solids. Material made in this manner is ideal for the neutralization processes. A second possibility is the use of ammonium carbonate or other carbonate solution to precipitate zinc as the carbonate. This material could then be calcined at approximately 300°C to produce zinc oxide. (20) ZnC0 3 — > ZnO + C0 2 Zinc oxide made in these processes can be used for the neutralization of the acid leach filtrate as shown in Fig. 4. The ammonium sulfate solution obtained after the zinc precipitation step can be divided into two streams, one of which is used for the production of zinc sulfate product and the other recycled back into the process in Step IB as was done in Step 1A. The recycled stream is analyzed and a measured amount of sulfuric acid is added to regenerate ammonium bisulfate for the next leaching process. Ammonium sulfate can be recrystallized from the solution to produce a pure grade for sale. Any zinc that is in the solution needs to be removed by a second step of adding more ammonium carbonate to the solution. The lead cake contains mostly lead sulfate and tin oxides. Lead can be removed from the lead cake by leaching it in a hot ammonium chloride solution of high concentration (e.g. about 40%) as is shown in Fig. 3. Copper and zinc which remain after the first stage acid leaching also can be removed: (21) PbS0 4 — > Pb " ^ + S0 4 " " (22) ?b** + 2 Cl " — > PbCl 2 (23) PbCl 2 + 2 NH 4 C1 — > PbCl 2 • 2 NH 4 C1 (soluble complex) Insoluble tin compounds precipitate during this leach and are filtered from the solution. The leach filtrate solution then is cooled and lead chloride crystals of complex form are produced. Impurities such as copper are carried out of the solution. The crude complex of lead chloride crystals is washed free from the ammonium chloride salt and any impurities present using cold washes. The low solubility of PbCl 2 (Ig/lOOml at 20° C) as well as the high solubility of ammonium chloride and other potential impurities (copper, zinc salts) allow a high purity lead chloride to be reached in two cold water washings. The washing is done at cold temperatures (below approximately 40°C) to reduce the solubility of the lead and prevent the formation of the oxy chloride. The washings are then concentrated and recombined with the mother liquor in order to restore the ammonium chloride concentration. Sulfate ion tends to build up in the solution and could cause the leaching to become ineffective. At the same time that this occurs, the chloride ion is removed. To correct this imbalance, calcium chloride can be added to the ammonium chloride washings as illustrated in Fig. 3. The calcium chloride can be generated from hydrochloric acid and lime via: (23) 2 HC1 + CaO — > Ca^ + 2 CV + H 2 0 (24) 2 HC1 + Ca(OH) 2 — > Ca^ + 2 Cl " + 2H 2 0 The correct amount of calcium chloride that needs to be added depends on the amount of chloride removed via lead chloride. An excessive amount of calcium chloride should not be added so as to prevent later contamination of calcium sulfate in the lead product. Therefore, to suppress calcium solubility, a small amount of sulfate ion must be tolerated in the recycled solution. The ammonium chloride solution is heated and the correct amount of a calcium chloride solution is slowly added with good mixing. In several minutes (5- 10) the calcium sulfate hydrate proαuct begins to precipitate out of solution: (25) Ca 44 + 2 C1 " + 2 Nri 1 ++ + S0 4 " — > CaS0 4 + NH 4 + + Cl " Once the calcium ion level has fallen to a minimum, the ammonium chloride solution is filtered free from the sulfate product. The ammonium chloride is recycled by adding it to the lead cake in Sten 2. Lead also is found in this product in small amounts (< 1%) and may be removed by a second ammonium chloride wash. Water washes do not appear effective in ren loving lead from this gypsum product. The lead chloride product generated in this process is of high purity and can be used for the generation of other lead salts and compounds, using methods known in the art. The lead chloride product can be added to a cold solution of sodium carbonate. This causes the production of the highly insoluble lead carbonate. (26) PbCl 2 + Na 2 C0 3 — > PbC0 3 + 2 NaCl Neutral precipitation product., obtained from the first acid leach filtrate and second cementation steps in Step 1 are mostly insoluble basic sulfate salts of zinc, iron, tin, copper and arsenic and as such should be reclaimed. These materials can be converted into their selectively soluble oxides by roasting at high temperature (>400°C). Roasting products include Sn0 2 , CuO and Fe 2 0 3 . These products then can be returned directly to the leaching process. In this way, tin trapped in the Zn 2 Sn0 4 form eventually can be reclaimed as the stannate salt. The iron can be removed magnetically to return it to the furnace for purification into the pure metal or mixed with carbon or sold to a steel producer as a feed material. The copper solids from Step 1 are treated with a dilute H 2 S0 4 solution to remove excess cadmium and zinc as the sulfates. As indicated in Fig. 3, the remaining high copper solids are best treated at high temperatures to directly reclaim the copper. This can be done on site by returning them to the furnace for purification of the copper. They mainly contain copper metal. Copper oxide, lead and zinc metal may be present in addition to zinc oxide and some cadmium. Cadmium present in the solution may be removed electrochemically by placing a sheet of zinc metal into the solution to produce a cadmium sponge: (27) Cd 4 + Zn° — > Cd° metal (sponge) + Zn 44 Alternatively, electrolysis may be used to recover cadmium present in the solution. This cadmium sponge may be separated from the zinc metal sheet, rinsed and redissolved in sulfuric acid to produce high purity cadmium sulfate: (28) Cd° + H 2 S0 4 — > CdS0 4 + H 2 (slow) Air oxidation of the cadmium wi 1 increase the rate of attack by sulfuric acid solutions, greatly increasing the me of dissolution, and forming water as the reaction's only byproduct: (29) CdO + H 2 S0 4 — > CdS0 4 + H 2 0 (fast) The cadmium sponge product, likewise, may be removed from the zinc sheet and sold directly as cadmium metal. After removal of the cadmium sponge and zinc sheet, the remaining solution is mainly zinc and sulfuric acid. This solution may be recycled by combining it with the primary leach solution, thus enabling eventual recovery of the zinc as zinc oxide. The sulfate will react with calcium present in the primary leach solution, and will precipitate as calcium sulfate. The majority of tin found in the metal dust is in the oxide form Sn0 2 . This material is highly insoluble in acid, but is rapidly dissolved in hot, concentrated hydroxide solutions, especially NaOH and KOH. In the tin plate industry, these solutions are commonly referred to as stannates. The insoluble tin cake material from the lead sulfate leach in Step 2 (once free from extractable lead) is treated in a hot, concentrated solution of the chosen hydroxide until the leaching of the tin is acceptable. Attention has to be given to the relative levels of potassium (or sodium) and tin found in solution. Some heavy metals, especially lead and zinc, may be leached as well, and purification of the stannate solution may be required. This may be accomplished by the use of a soluble sulfhydrate salt, such as sodium sulfhydrate (NaSH). Addition of the sulfhydrate will cause the precipitation of these heavy metals from the solution. The solubility of the stannates is reduced when the free hydroxide levels are increased. This can be used to precipitate the stannate salt from solution when the solutions are replenished in hydroxide. The zinc/tin insolubles are believed to contain a majority of the compound Zn 2 Sn0 4 , which was insoluble in all of the previous treatments. This material can be treated with hot concentrated sulfuric acid and dissolved. This step is a non-selective step. Any neutralization reactions, without water, in the first dilute leach can result in a violent exothermic reaction. By the time the material reaches the Zn/Sn insoluble stage, all of the components leading to a violent reaction have been removed and heat only needs to be applied to the acid. At this stage of the process, the solid mass is only about 2% of the total dust mass to be treated. The Zn/Sn insolubles are mixed with hot concentrated sulfuric acid and allowed to react for 10 to 20 minutes. It is then filtered. The Zn Sn sulfate is made neutral with zinc oxide. A basic sulfate precipitate high in tin similar to the neutral precipitate is formed. This is filtered out and roasted. The solution remaining contains mainly zinc sulfate and is recycled to the first dilute leach for eventual recovery. The small volume of the solids at this stage may make this recovery unsuitable, and the solids can be returned directly to the furnace for eventual reentry into the process. Example 13 A sample of the mixed waste metals cake was taken fresh from the mixed metals press and placed into an air tight plastic bag. The cake was mixed within the bag and excess liquid was removed by allowing the bag to drain. Attempts were made to exclude air from the bag as well. The major elemental composition of this cake material tested to be: Element Weight % Cd 1.5 Cu 1.0 Pb 19.2 Zn 2.1 Other materials present include water and ammonium chloride, as well as oxides of the mixed metals. A sample of this mixed metals cake was taken from the bag, added to a beaker, and washed with an equal weight of warm water on a hot plate with mechanical stirring. Some white precipitate, mainly zinc oxide, formed by the decomposition of the complex diamino-zinc salt. The washing step was carried out to remove ammonium chloride, and other soluble components, if present. The wash water was decanted from the product. Fresh water was added, enough to cover the solids, to prevent any further air oxidation of the solids and a large excess of sulfuric acid added in stages over several days, during which time bubbling was noted. No heating was applied. Additional sulfuric acid was added when the pH of the mixture reached 5. The solution was mixed and then allowed to react, without further mixing. When analyzed the elemental composition was: Element Weight % Cd 0.19 Cu 4.1 Pb 43.2 Zn 0.04 The solid was observed with crossed polars under a microscope, and a great deal of crystalline-"non-metallic" material was noted. A majority of this material likely is lead sulfate, formed by the reaction of the lead metal with the acid. Remainders are likely to be copper and lead metal. The solution produced in this process also was analyzed and found to contain zinc and cadmium in large amounts, while having very low concentrations of copper and lead. This solution can be further treated by cementation processes, if desired to produce high purity cadmium metal. Example 14 A second batch of washed mixed metals was taken from the waste metals cake described in Example 13 and treated hot with a limiting amount of sulfuric acid (lOg acid/lOOg mixed metals). Reaction was allowed to continue for 4 hours. At the end of this time the pH increased to 6, meaning the acid had been completely reacted with the product. A sample of the remaining solids was collected and allowed to air dry on a warm glass slide. It was analyzed to contain: Element Weight % Cd 1.9 Cu 4.0 Pb 78 Zn 2.9 By microscopy, the product appeared to be much higher in metallic solids than the previous run. Some crystalline material similar to the previous material was noted, however. Example 15 Another typical zinc rich dust produced in the processing of electrical cables comprises: Component % by Weight Comment Zinc 40 ZnO with some Zn 2 SnO 4 Lead 25 PbS0 4 with PbCl 2 Copper 2.7 CuO assumed Tin 1.2 Sn0 2 with some Zn 2 Sn0 4 Sodium 1.0 Potassium 0.7 Calcium 0.4 Iron 0.2 Cadmium 0.07 CdO assumed Magnesium 0.05 MgO assumed Trace amounts of Li, Ni, Cr, Mn, Ba, V, Co, and Hg. Indeterminate amounts of As, Sb, Be, and Bi. lOg of the zinc rich dust produced in the processing of electrical cable was leached with 20ml distilled water for 10 minutes. 0.33g of material was found in the leachate from the dust and the chloride content was determined by AgCl titration. This dust, when washed with water, had O.lg of chloride leached out. The major components found in the leachate were lead, zinc, potassium and sodium. This water washing is only necessary in this process if there is a significant amount of chloride ion that may interfere with the remainder of the processing steps. Example 16 250g of the zinc rich dust produced in the processing of electrical cables was added to a large beaker, and 500ml of distilled water added to create a slurry. A stir- bar was added and used to mix the slurry. Concentrated sulfuric acid was added slowly, keeping note of the pH of the solution. Heat was released by the neutralization heat of reaction (1) as well as the heat from dilution of the acid. 166.2g of acid were added to maintain a constant acidity. A zinc oxide equivalent is: 166.2g/100 g/mole H 2 S0 4 x 81.35g/mole ZnO = 135g (54% mass) The acid consumed is required to react with other oxides present in the dust (CuO, K 2 O, CaO, etc.) and adding a slight excess for acidity, this slightly higher estimate is expected (measured zinc oxide levels (45-50%)). The solution was then filtered rapidly to determine relative rates of dissolution. The solution obtained by filtration was green in color, and found to contain the following elements: Component Amount L Component Amount (g) Zn 73+ Al 0.17 Cu 2.9 Mg 0.08 Na 1.5 Fe 0.07 K 1.2 Pb 0.05 Cd 0.29 Sn 0.02 Ca 0.25 The solids were washed for a time (15 min.) with warm, dilute sulfuric acid, filtered and the washings analyzed, and were analyzed to contain: Component Amount (s Component Amount (g) Zn 7.7 K 0.12 Cu 1.2 Pb 0.05 Fe 0.26 Cd 0.03 Ca 0.21 Mg 0.02 Na 0.19 Sn 0.21 Al 0.13 Based upon this data, it is clear that the dissolution of iron, copper, calcium, tin and aluminum are slower reactions than in the case of zinc. Further, it shows the need for a washing stage between separate leach steps to avoid contamination and loss of product. The weight of the air dried lead cake was 124g (-50% mass). The leach solutions were combined, and ZnO added to neutralize to a pH of 5-6. This caused the formation of a mixed basic sulfate precipitate referred to as the neutral. The dried precipitate was 2.9 lg in weight and was analyzed to contain: Component Amount (g) Wt.% Zn 0.70 24.0 Fe 0.20 7.00 Sn 0.22 7.80 Cu 0.19 6.40 Pb 0.026 0.90 K 0.008 0.29 Levels of zinc in the solids can be reduced by careful addition of zinc oxide. The solution filtered free from the neutral precipitate was analyzed to contain: Component Amount (g) Component Amount (g) Zn 80 Al 0.25 Cu 3.5 Fe 0.1 Na 1.5 Mg 0.1 K 1.2 Pb 0.03 Ca 0.4 Sn 0.03 Cd 0.29 Example 17 Multiple Sulfuric Acid Leach of the Zinc Rich Dust. Leach #1. lOO.Olg of the zinc rich dust was made into a slurry with 200ml of distilled water. This formed a well suspended slurry with mixing provided by a stir bar. Concentrated sulfuric acid was added slowly to the slurry over a 7 minute period in order to alter the pH of the solution to a constant pH of ~ 1 to insure the complete dissolution of zinc and other oxides. The pH was monitored using pH paper during the acid addition. The solution remained acidic for several minutes after a total of 47.34g of sulfuric acid had been added. H 2 S0 4 (-97%) 47.34g / -1 OOg/mole = .473 mole ZnO (estimated) = .0473 mole x 81.38g/mole = 38.5g as ZnO The pH of the solution slowly lost acidity, and at 10 min., 3 additional grams of acid were added to maintain a pH of -1. 3g / -1 OOg/mole = .03 mole added total added = .503 mole H 2 S0 4 End concentration of acid : 200ml water + 50.34g H 2 S0 4 - 20% by weight. A temperature rise from 23°C to 75°C was noted in the solution, resulting from the dilution of the acid as well as from the heat of neutralization involving zinc oxide. The solution was allowed to mix for 30 minutes total time, and then vacuum filtered through paper. The resulting solution contained fine suspended particles and was re-heated and passed through a fine membrane filter, in order to remove the fine suspended material. The solid material was washed in distilled water, and collected, the washings saved. Samples of the washings and the filtered solution were collected for analysis. The solid was oven dried at 110°C. The acid leach solution was heated and 0.92g of zinc oxide added. The pH of the solution slowly rose to a pH of 4-5. Mixing of the solution using a stirbar was continued for 20 min. A sample was taken to determine the effects of the zinc oxide 47 addition, as well as to establish the proper amounts of zinc to use in the cementation steps. The neutral solids weighed 1.63g. The dry weight of the lead cake solid was 57.66g, with 42.34g of material therefore removed in the first leach step. This closely matches the zinc oxide acid equivalent stated before. Leach #2. The process was repeated using the cemented solution, too low in zinc for crystallization, using an additional lOO.OOg of zinc rich dust. The dust was added slowly to the existing solution, approximately 290ml. In order to obtain an acidic condition, slow addition of 50.19g of sulfuric acid was required. The reaction was continued for one hour. The solution was filtered crudely through paper, and the solid material rinsed in the funnel. A total of 44.44g was leached from the zinc rich dust. The neutralization step required 1.75g of ZnO and produced 2.41g of neutral solids. 1 g of zinc dust was added for cementation. Still, zinc sulfate levels were too low for crystallization to occur. Leach #3. The third leach used lOO.OOg of zinc rich dust, and required 51.4g of sulfuric acid to be added. To test the effect of iron, 1.00g of ferric sulfate was added at this time. Filtration was difficult due to the slow rate and the crystallization of the sulfate product in the filter. 6.0g of ZnO was added and generated 8.40g of neutral solids. l.Og of zinc dust was used for cementation. Components in cycled solution ( in ppm +/-4%) Leach Pb Sn Mg Ca K Na Cu Cd Fe Al Mn Zinc (%wt) la 26 <12 519 6 65 178 1723 26 74 271 2 9.0% b 13 <12 546 17 78 188 1602 19 53 92 <1 9.5% c 11 <12 463 7 85 151 11 <4 52 9 <1 8.3% 2a 448 <12 645 8 91 219 1109 17 89 201 <1 11.4% b 13 <24 703 10 101 234 1090 12 44 70 <1 12.4% c 17 <12 662 12 105 225 4 <2 32 <3 <1 12.0% 3a 1466 190 677 9 98 298 1134 20 430 173 3 14.4% b 39 14 686 11 102 288 951 14 378 89 2 14.6% c 17 <12 667 9 103 270 61 9 108 37 2 13.6% a) after leaching b) after neutralization c) after cementation step: As one can observe from the above data, little contamination of the solution was detected. The elements lead, copper, cadmium, aluminum and iron are controlled by the process steps of neutralization and cementation. Calcium is kept insoluble by the formation of calcium sulfate. Other components, such as sodium, potassium and magnesium should not cause any harmful effect on the zinc sulfate product. Example 18 Analysis of the solutions obtained during the process indicated that As was leached from the zinc rich dust in the acid leach step of Step 1. A leach was done to test methods to control the levels of arsenic present. lOO.Olg of dust was leached. The acid solution contained 425(+/-6) ppm as As. This represents about 40% of the arsenic present in the dust (-3700 ppm). The solution was divided into two volumes of equal size. Solution A was first treated with ferric sulfate and then neutralized zinc oxide, whereas solution B was treated with zinc oxide alone. The iron treatment was carried out as follows: first 2.0g of ferric sulfate, Fe 2 (S0 4 ) 3 • n H 2 0, was added to 275g of the acid leached solution, and allowed to dissolve. The solution was heated and 6g of zinc oxide slowly added to neutralize the solution. Boiling was allowed to continue to coagulate the solids as stated in Zinc, The Science and Technology of the Metal, Its Alloys and Compounds, by CH. Mathewson (Reinholt Publishing Corp., 1959) at 183-184. The reaction in solution B was done in the same manner, lacking in only the iron sulfate. After the neutralization step, the amount of As present dropped to 51(+/- 8) ppm in Solution A and 72(+/-5) ppm in Solution B. This is a removal rate of about 90%. Cementation was done as usual, using lg Zn dust, and cementation was allowed to continue for 1 hour. The As remaining in the solutions was in the 25 ppm range. Arsenic, as well as antimony, form toxic hydrides in the presence of hydrogen. Arsine, AsH 3 can form when arsenic containing compounds come in contact with zinc and sulfuric acid. Arsine is an extremely toxic gas, with some solubility in water so that normal safety precaution should be employed. Example 19 A 25 Og sample of the 40% ammonium chloride solution was prepared and reagent lead sulfate was slowly added to the solution at 105°C with mechanical stirring. The solution was able to dissolve 12.9% lead sulfate by weight. The crystalline product produced by cooling was analyzed by PD to be a lead chloride - ammonium chloride complex. Washing of the complex produced lead chloride salt, also analyzed by PD. Example 20 The lead cake generated in the first leach (124g) was added to a 40%> by weight solution of ammonium chloride (400g of NH C1/ 600g of distilled water). The ammonium chloride completely dissolved at about 83°C The solution was filtered at the end of 30 min. The solution was allowed to cool, and crystals began to form in large amounts. The crystals were a light ice-blue in color, due to a copper impurity present. The crude complex contained 33.9% as lead, 0.4% as copper, and 0.05% as zinc. Two cold water washes of the product were done to remove ammonium chloride from the product. The product was free from the blue color, as the copper was rather soluble. The washings were combined, reduced in volume and added back to the mother liquor. The final product contained 0.01% copper as impurity. A limited amount of calcium chloride was dissolved in distilled water and added to the ammonium chloride solution. Mixing was done with a stir-bar. After several minutes a white precipitate began to form, and time was allowed for complete precipitation to occur. This was separated and analyzed: 22.0% as Ca ( 23% in pure CaS0 4 • 2 H 2 0 ) 0.55% as Pb 0.20% as Na An attempt was made to wash out this lead in hot water washes, but no effect was observed. The tin cake generated retained some soluble lead and was returned to a second lead leach to insure complete lead removal. End weight of tin cake was 17g. The restored ammonium chloride solution was analyzed: 1.85% as lead 0.07%) as copper 0.08% as calcium 0.03% as zinc Example 21 A sample of the lead chloride produced in Example 16 was added to a solution containing excess sodium carbonate. The solution was mixed at room temperature for one hour. The solid was filtered free from the solution and analyzed by PD to be lead carbonate. A second sample was added to a hot - 95°C solution of excess sodium carbonate, and allowed to react for one hour. The solid material was filtered out and analyzed by PD to contain a mixture of basic lead carbonate (hydrocerussite, Pb 3 (C0 3 ) 2 (OH) 2 ) and basic sodium-lead carbonate (NaPb 2 (C0 3 ) 2 OH). 3.58g of a lead chloride product produced in a lead leach step by dilution of the ammonium chloride solution was added to 20ml of distilled water containing 1.40g of sodium carbonate. This was mixed at room temperature (about 22°C) for 40 minutes and then filtered through a membrane filter to remove the solid component. The dried solid weighed 3.2 lg and a sample was analyzed to be lead carbonate (cerussite, PbC0 3 ). Some of this solid was then washed in hot water and analyzed to be unchanged lead carbonate. Example 22 About 12g of the insoluble material from the lead leach was added to a small flask containing 50ml of distilled water and 20g of reagent potassium hydroxide. The solution was stirred and heated on a hot plate for 20 min. For testing purposes, the solution was diluted and filtered. The remaining solids weighed 4.9g (41% of original mass). By DCP, the solution was high in potassium and tin with traces of lead, zinc, aluminum, cadmium and copper. If the 59% represented tin as Sn0 2 only, 6.2g'of tin were present. Example 23 The solids from the hydroxide (tin) leach were added to a flask containing enough concentrated sulfuric acid to cover the solids. It was heated on the hot plate for 20 min. The color changed to a dark brown as the reaction proceeded. Once the mixture had cooled, distilled water was added (carefully), the solution was filtered, and the solid left was dried and weighed. This leach removed 65% of the weight of the material, and was tested via DCP to contain a large majority of zinc and tin with traces of iron, aluminum and copper. The solid was dissolved to a small degree in a mixture of perchloric / nitric / hydrochloric acids. It contained mostly Sn, Cu, Fe, Al, and Pb with traces of Ni, Zn, Mn, Cd, Ca, Mg, K, Na, Ba, and V. The tin and other components were precipitated by neutralization with zinc oxide, and the zinc remained in solution, as the sulfate. Electrolysis Step For Zinc Recovery The present process can be operated to recover zinc metal by replacing the crystallization steps with an electrolysis step. The combined product solution from the leaching steps comprises zinc ions in solution as Zn . When the combined product solution is subjected to electrolysis in an electrolytic cell containing an anode and a cathode, the zinc metal is electrodeposited on the cathode. Although it is preferable to have the cathode made from zinc metal, cathodes of other material also will allow the electrodeposition of zinc metal from the combined product solution. Any of the electrolysis cells discussed in the literature are suitable, as long as such cells are configured for the electrolysis of zinc ion containing solutions. The two electrodes of the electrolysis cells are connected externally to a power supply capable of impressing a suitable voltage across the electrodes. The zinc ions, being positive in nature, migrate toward the negative electrode, or cathode, where they combine with electrons supplied by the external circuit to form neutral zinc metal atoms. When this happens, the zinc metal, in effect, electroplates onto the cathode. By using a zinc cathode, the entire cathode can be removed and used as necessary as a source of zinc. Alternatively, a cathode on which electroplated zinc metal can be easily removed can be used. Periodic Precipitation Of Other Solubles From The Product Solution The product solution also contains sodium, potassium, magnesium, calcium, manganese, and other solubles in solution. These solubles can be recovered by introducing an electrolyte either in the leaching step or in the ammonium chloride storage tanks receiving the recycled product solution. When ammonium chloride is used as the leachant, ammonium salts in solution is the preferred electrolyte. For example, if some ammonium sulfate is added, one could precipitate out calcium sulfate. Ammonium sulfate is a preferred electrolyte to add because the process already uses ammonium in the form of ammonium chloride. The preferred electrolytes include ammonium sulfate, ammonium hydroxide, or ammonium carbonate to precipitate out various solubles. Manganese can be removed by the addition of an oxidizing agent such as potassium permanganate or hydrogen peroxide. This oxidation results in soluble Mn + being oxidized to insoluble Mn which will precipitate out as a manganese solid. Recovery of Ammonium Chloride and Wash Water Purification The wash water used to wash the zinc compounds precipitated from the product solution contains some ammonium chloride, as well as other compounds. Rather than dispose of this polluted wash water, it can be treated to produce pure water and a more concentrated solution containing ammonium chloride and other compounds. The pure water can be recycled to wash additional zinc compounds precipitated from the product solution, and the concentrated solution can be recycled back to the leaching step. The purification can be accomplished using evaporator condensers or reverse osmosis membrane technology. The above description sets forth the best mode of the invention as known to the inventor at this time, and the above Examples are for illustrative purposes only, as it is obvious to one skilled in the art to make modifications to this process without departing from the spirit and scope of the invention and its equivalents as set forth in the appended claims.

Claims: What is claimed is: 1. A method for the recovery of chemical values from waste material streams which comprise zinc compounds, comprising the steps of: a. roasting said waste material at an elevated temperature and in a reducing atmosphere; b. treating said waste material with an ammonium chloride solution at an elevated temperature to form a product solution which comprises dissolved zinc and dissolved zinc oxide whereby any iron oxide in said waste material will not go into solution; c. separating said product solution from any undissolved materials present in said product solution including any of said iron oxide; d. adding zinc metal to said product solution whereby any lead and cadmium ions contained within said product solution are displaced by said zinc metal and precipitate out of said product solution as lead and cadmium metals; e. separating said product solution from the lead and cadmium metals and lowering the temperature of said product solution thereby precipitating the zinc component as a mixture of crystallized zinc compounds; f. separating said precipitated zinc compounds from said product solution and washing said zinc compounds solids with a wash water thereby solubilizing certain of said zinc compounds; and g. separating the remaining zinc compounds solids from said solution and drying said remaining zinc compounds solids at a temperature of at least 100°C whereby said resulting product is zinc oxide of 99%) or greater purity. 2. The method as described in Claim 1, wherein said product solution of step d is maintained at a temperature of at least 90°C 3. The method as described in Claim 2, wherein the concentration of said ammonium chloride solution in step b is 23% by weight. 4. The method as described in Claim 3, wherein said waste materials are roasted at a temperature of at least 500°C. 5. The method as described in Claim 1, wherein the temperature of said product solution is lowered in a controlled fashion to between about 20°C and about 60°C over a predetermined period of time to precipitate the zinc component therefrom. 6. The method as described in Claim 4, further comprising the step of adding a dispersant to said product solution concurrently while adding zinc metal to said product solution, said dispersant is present in said product solution in the concentration of between about 10 to about 1000 ppm, and said dispersant is selected from the group consisting of water soluble polymers. 7. The method as described in Claim 6, wherein said dispersant is selected from the group consisting of maleic based acrylic oligomers, lignosulfonates, polyphosphates, polyacrylates, polymethacrylates, maleic anhydride copolymers, polymaleic anhydride, phosphate esters, and phosphonates. 8. The method as described in Claim 4, wherein during said step of drying said remaining zinc compounds solids, said remaining zinc compounds solids are dried at a temperature of between 100°C and 350°C 9. The method as described in Claim 8, wherein said remaining zinc compounds solids are dried at a temperature of between 271°C and 350°C 10. The method as described in Claim 9, wherein said remaining zinc compounds solids are dried for between 2 minutes and 60 minutes. 11. The method as described in Claim 10, wherein said remaining zinc compounds solids are dried for between 5 minutes and 20 minutes. 12. A method for the recovery of chemical values from waste material streams which comprise zinc compounds, comprising the steps of: a. treating said waste material a first time with an ammonium chloride solution at an elevated temperature to form a first product solution which comprises dissolved zinc constituents whereby any iron oxide in said waste material will not go into solution; b. separating said first product solution from the undissolved waste material compounds present in said first product solution including any of said iron oxide; c. roasting said undissolved waste material compounds at an elevated temperature and in a reducing atmosphere; d. treating said roasted undissolved waste material compounds a second time with said ammonium chloride solution at an elevated temperature to form a second product solution which comprises dissolved zinc constituents whereby any iron oxide remaining in said roasted undissolved waste material compounds will not go into solution; e. separating said second product solution from said roasted undissolved waste materials present in said second product solution including any of said iron oxide; f. combining said first and second product solutions to form a combined product solution, maintaining said combined product solution at a temperature of at least 90°C, and adding powdered zinc metal to said combined product solution whereby any lead and cadmium ions contained within said combined product solution are displaced by said zinc metal and precipitate out of said combined product solution as lead and cadmium metals; g. separating said combined product solution from the lead and cadmium metals and lowering the temperature of said combined product solution thereby precipitating the zinc component as a mixture of crystallized zinc compounds; h. separating said precipitated zinc compounds from said combined product solution and washing said zinc compounds solids with a wash water having a temperature of between about 25°C and 100°C thereby solubilizing certain of said zinc compounds; and i. separating the remaining zinc compound solids from said combined product solution and drying said remaining zinc compound solids at a temperature of between about 100°C and 350°C whereby said resulting product is zinc oxide of 99% or greater purity. 13. The method as describe in Claim 12, wherein the concentration of said ammonium chloride solution is 23 % by weight and said waste materials are roasted at a temperature of at least 500°C 14. A method for the recovery of chemical values from waste material streams which comprise zinc compounds, comprising the steps of: a. treating said waste material with an ammonium chloride solution at an elevated temperature to form a product solution which comprises dissolved zinc and dissolved zinc oxide whereby any iron oxide in said waste material will not go into solution; b. adding carbon to said product solution whereby said carbon will not go into solution; c. separating said product solution from any undissolved materials present in said product solution inclu ing any of said iron oxide and said carbon; d. adding zinc metal and a dispersant to said product solution whereby any lead and cadmium ions contained within said product solution are displaced by said zinc metal and precipitate out of said product solution as lead and cadmium metals and said disperssrit is selected from the group consisting of dispersants which will prevent the aggregation of said zinc metal; e. separating said product solution from the lead and cadmium metals and treating said product solution so as to remove the zinc component from said product solution. 15. The method as described in Claim 14 wherein said product solution is treated to remove the zinc component by: f. lowering the temperature of said product solution thereby precipitating the zinc component as a mixture of crystallized zinc compounds and separating said precipitated zinc compounds from said product solution; g. washing said zinc compounds solids with a wash water thereby solubilizing certain of said zinc compounds and separating the remaining zinc compounds solids from said solution; and then h. drying said remaining zinc compounds solids at a temperature of between about 100°C and 350° whereby said resulting product is zinc oxide of 99% or greater purity. 16. The method as described in Claim 14, wherein said product solution is treated to remove the zinc component by electrolysis thereby removing the zinc component from said product solution as elemental zinc. 17. The method as described in Claim 1, further comprising the steps of: h. forming said lead and cadmium metals into a waste metals cake; i. treating the waste metals cake in a dissolving solution wherein zinc and cadmium are soluble and leεd is insoluble; j. recovering thf lead by separating the lead from said dissolving solution; and k. recovering tin: cadmium from said dissolving solution by electrochemical means. 18. The method as described in Claim 17, wherein said dissolving solution is selected from the group consisting of sulfuric acid and ammonium bisulfate. 19. The method as described in Claim 18, wherein a zinc metal article is placed in said dissolving solution, whereupon cadmium dissolved in said solution deposits on the zinc metal article to form a cadmium sponge. 20. The method as described in Claim 19, wherein said cadmium is deposited by electrolysis on a cathodic surface to form a cadmium sponge. 21. A method for the recovery of chemical values from waste material streams containing zinc, copper, lead, and cadmium compounds comprising the steps of: a. treating said waste material with a leachant until at least a substantial portion of the zinc is dissolved and separating at least a substantial portion of any undissolved solids in and insoluble compounds formed from the solution; b. adding a zinc compound to said solution to increase the pH of the solution to a sufficient level to cause the formation of precipitates of basic sulfate salts and separating said basic sulfate salts from the solution; c. adding zinc metal to the solution to achieve a first cementation step whereby lead, copper, and cadmium ions contained within the solution are displaced by said zinc metal and precipitate out of the solution as a waste metals cake comprising lead, zinc, and cadmium; d. treating said waste metals cake with a dissolving solution wherein zinc and cadmium are soluble and lead is insoluble and separating at least a portion of the lead from the solution; and e. recovering at least a portion of the cadmium from said solution by electrochemical means. 22. The method as claimed in Claim 21, wherein said dissolving solution is selected from the group consisting of sulfuric acid and ammonium bisulfate. 23. The method as claimed in Claim 22, wherein cadmium metal is recovered from said cadmium compounds by treating said cadmium compounds with a sulfuric acid solution in the presence of a zinc metal article, said cadmium metal forming on said zinc metal article as a cadmium sponge. 24. The method as claimed in Claim 23, further comprising the step of adding an oxidizing agent to the solution to convert soluble manganese ions to insoluble manganese ions, said insoluble manganese ions forming a precipitate, and removing said precipitate from the solution. 25. A method for the recovery of chemical values from waste material streams which comprise zinc compounds, comprising the steps of: a) treating said waste material with a sulfur-based leachant until at least a substantial portion of the zinc is dissolved; b) separating at least a substantial portion of any undissolved solids in, and insoluble compounds formed while treating said waste material with said leachant, from the solution; c) adding a zinc compound to said solution to increase the pH of the solution to a sufficient level to cause the formation of precipitates of basic sulfate salts and separating said basic sulfate salts from the solution; d) adding zinc metal to the solution to achieve a first cementation step whereby lead and copper ions contained within the solution are displaced by said zinc metal and precipitate out of the solution as lead and copper metallic solids and separating said lead and copper metallic solids from the solution; and e) forming crystallized zinc compounds from the zinc component in the solution and separating the crystallized zinc compounds from the solution. 26. The method of Claim 25, wherein said leachant solution is selected from the group consisting of sulfuric acid and ammonium bisulfate solutions. 27. The method of Claim 26, wherein said zinc compound is selected from the group consisting of zinc oxide and zinc hydroxide. 28. The method of Claim 27, wherein lead compounds are recovered from said lead solids by further treating said insoluble compounds with an ammonium chloride solution at an elevated temperature to form a solution comprising lead chloride. 29. The method of Claim 28, further comprising separating at least a substantial portion of any undissloved solids in and insoluble compounds formed from the solution and lowering the temperature of said solution thereby precipitating the lead component as lead chloride crystals. 30. The method of Claim 29, further comprising adding calcium chloride to the solution remaining after the precipitation of the lead chloride crystals, whereby calcium sulfate is precipitated from the solution. 31. The method of Claim 30, wherein said copper metallic solids further comprises cadmium compounds and zinc compounds and said copper metallic solids are treated with sulfuric acid to remove at least a portion of said cadmium compounds and said zinc compound to produce solids with a high copper content. 32. The method of Claim 31, wherein said waste material further comprises cadmium which is removed by adding zinc metal to the solution wherein any cadmium ions contained in the solution are displaced by said zinc metal and precipitate out of the solution as cadmium metallic solids and separating said cadmium metallic solids from the solution. 33. The method of Claim 32, wherein cadmium metal is recovered from said cadmium metallic solids by treating said cadmium metallic solids with a sulfuric acid solution in the presence of a zinc metal article, said cadmium metal forming on said zinc metal article as a cadmium sponge. 34. The method of Claim 33, wherein said waste materials further comprises tin, said insoluble compounds further comprise tin compounds, and tin is recovered from said insoluble compounds by further treating said insoluble compounds with a hydroxide at an elevated temperature to form a solution comprising dissolved tin. 35. The method of Claim 34, wherein said hydroxide is selected from the group consisting of sodium hydroxide and potassium hydroxide. 36. The method of Claim 35, wherein said insoluble compounds further comprise lead and tin and said solution further comprises dissolved lead and tin, and at least a portion of said dissolved lead and tin is removed from said solution by the addition of a soluble sulfhydrate salt. 37. The method of Claim 36, wherein said soluble sulfhydrate salt is sodium sulfhydrate. 38. The method of Claim 37, wherein said insoluble compounds further comprise insoluble zinc compounds and insoluble tin compounds and at least a portion of said insoluble zinc compounds and said insoluble tin compounds are recovered from said insoluble compounds by further treating said insoluble compounds with sulfuric acid until at least a portion of said insoluble zinc compounds and said insoluble tin compounds are dissolved, adding a zinc compound to said sulfuric acid containing solution to increase the pH of said solution to a sufficient level to cause the formation of a basic sulfate precipitate high in tin, and separating said basic sulfate precipitate high in tin from said solution.

Inventors: CUDAHY MICHAEL W, MYERSON ALLAN S, CUDAHY, MICHAEL, W., MYERSON, ALLAN, S.
Applicants: METALS RECYCLING TECH, METALS RECYCLING TECHNOLOGIES CORP.
Application year: 1995
Main classification: C01G9
IPC codes: B09B3, C01G9, C21B13, C22B3, C22B5, C22B7, C22B17, C22B19, C25C1