ABSORBENTS

Abstract: Absorbents, suitable for absorbing sulphur compounds such as hydrogen sulphide from gases and liquids, in the form of shaped units having an average size within the range 1-10 mm and containing at least 75 % by weight of an absorbent material comprising copper carbonate, basic copper carbonate, and/or copper hydroxide. The units preferably have a bulk density of at least 0.9 kg/l, especially at least 1.2 kg/l. The units are preferably agglomerates containing a small amount of a binder such as a cement and may also contain a proportion of alumina to catalyse hydrolysis of carbon-containing sulphur compounds such as carbonyl sulphide or carbon disulphide.

Description: Absorbents This invention relates to absorbents and in particular to compositions containing copper compounds for the absorption of sulphur compounds, such as hydrogen sulphide, which are often present as impurities in gases and liquids such as hydrocarbon streams, e g natural gas There have been numerous proposals of using composition containing copper compounds for the absorption of such sulphur compounds in many of the previous proposals the copper is present i the composition as an oxide, often together with other components such as zinc oxide anσVor alumina Often the copper oxide is reduced to the corresponding metal before use, or is used for treating gas streams containing a reducing gas such as carbon monoxide or hydrogen at such an elevated temperature that reduction of the oxide will occur in situ In our EP-A-0243 052 we demonstrate that certain compositions, containing certain copper compounds, in the form of agglomerates, e g granules, as opposed to moulded tablets or pellets, ha superior sulphur absorption characteristics and can be used without a reduction step and have good absorption characteristics at low temperatures The agglomerates were formed by mixing the composition containing the copper compounds with a cement binder and with a little water, insufficien to form a slurry, and then causing the composition to agglomerate into roughly spherical granules Alternatively the granules could be made by extruding the wetted composition In that reference, the composition contained zinc or aluminium compounds, preferably both, in addition to the copper compounds and the cement binder Preferably zinc atoms formed 10-40% of the total number of copper, zinc, and aluminium atoms Specifically we described the production of agglomerates using copper-compound containing composition produced by mixing co-precipitated copper and zinc basic carbonates, iβ a zinc-substituted malachite with a zinc aluminate precipitate We described that suc agglomerates, which had been dried but which had not been calcined at a temperature high enough t decompose the basic carbonates, were useful for absorbing hydrogen sulphide at low temperatures, and were superior to agglomerates that had been calcined US-A-4 582 819 discloses the use of agglomerates formed by extruding a mixture of alumina and basic copper carbonate, e g malachite, followed by calcination, for the absorption of sulphur compounds Under the calcination conditions disclosed, viz heating to above 500 β F (260 β C), the malachite will decompose to copper oxide The agglomerates of this reference contain substantial amounts (above 25% by weight) of alumina The amount of sulphur that can be absorbed from a gas stream depends on the absorption capacity of the absorbent, the amount of absorbent employed, and the absorption profile given by a bed of the absorbent The absorption capacity of an absorbent is the theoretical amount of sulphur that can be absorbed by a given weight of an absorbent Thus 1 kg of an absorbent composed of copper oxide or zinc oxide and containing 10% by weight of non-absorbent material, eg alumina has a theoretical capacity to absorb about 350-360 g sulphur on the other hand 1 kg of an absorbent of malachite, or zinc-substituted malachite, again containing 10% by weight of non-absorbent material, has a theoretical sulphur absorption capacity of only about 250-260 g It is generally not possible for the full theoretical capacity of the absorbent bed to be realised thus some sulphur compounds will be detected in the product stream leaving the bed before the theoretical capacity has been realised The reason for this is that the sulphur absorption front in the bed is not sharp the sharper the absorption front, the closer the theoretical capacity can be approached We have found that despite their lower theoretical capacity compared to copper oxide or copper metal, absorbents made from copper carbonate basic copper carbonate, or copper hydroxide in fact can give a greater actual sulphur capacity Accordingly the present invention provides shaped absorbent units having an average size within the range 1-10 mm and containing at least 75% by weight of an absorbent material selected from copper carbonate, basic copper carbonate, and copper hydroxide and mixtures thereof The weight of absorbent that can be emDioyed depends on the volume of the vessel containing the absorbent bed and the bulk density of the absorbent It is desirable to maximise the weight of sulphur that can be absorbed by a bed of absorbent, i e by a given volume of absorbent Hence it is desirable to maximise the bulk density of the absorbent, provided the other absorption characteristics are not unduly adversely affected [The bulk density of particles is the density of a bed of the particle and is determined by filling a vessel of known volume with the particles, with tapping of the vessel to ensure settling of the particles, and then determining the weight of particles in the vessel The bulk density is of course considerably lower than the density of the particles themselves since a considerable proportion of the volume of a bed of the particles is taken up by the spaces between adjacent particles As an example, a bed of pellets made as described in Example 3 hereafter had a density of 1 07 kg/l, whereas the density of the individual pellets, i e the particle density, was about 1 85 kg/l ] We have found that it is possible to produce absorbents comprising copper carbonates, basic carbonates, or hydroxides, having a bulk density of at least 0 9 kg/l, particularly at least 1 2 kg/l. The shaped units may be in the form of tablets formed by moulding a suitable powder composition, generally containing a material such as graphite or magnesium stearate as a moulding aid, in suitably sized moulds, e g as in conventional tableting operation Alternatively, the shaped units may be in the form of extruded pellets formed by forcing a suitable composition, containing the absorbent material and often a binder and a little water and/or a moulding aid as indicated above, through a die followed by cutting the material emerging from the die into short lengths For example extruded pellets may be made using a pellet mill of the type used for pelleting animal feedstuffs, wherein the mixture to be pelleted is charged to a rotating perforate cylinder through the perforations of which the mixture is forced by a bar or roller within the cylinder the resulting extruded mixture is cu from the surface of the rotating cylinder by a doctor knife positioned to give extruded pellets of the desired length Alternatively, and preferably, the shaped units may be in the form of agglomerates formed by mixing the absorbent material with a cement binder and with a little water, insufficient to form a slurry, and then causing the composition to agglomerate into roughly spherical, but generally irregular, granules The different shaping methods have an effect on the surface area, porosity and pore structure within the shaped articles and in turn this often has a significant effect on the absorptio characteristics and on the bulk density Thus beds of absorbents in the form of moulded tablets may exhibit a relatively broad absorptio front, whereas beds of agglomerates can have a much sharper absorption front this enables a closer approach to be made to the theoretical absorption capacity On the other hand, agglomerates generally have lower bulk densities than tableted compositions however, as described hereinafter, agglomerates with an adequately high bulk density can be produced and so it is preferred to make th shaped units in the form of agglomerates Preferably the shaped units have a BET surface area of at least 10 m 2 /g In the shaped units of the invention the absorbent material comprises copper carbonate, basic copper carbonate, and/or copper hydroxide Basic copper carbonate, especially malachite, is the preferred absorbent material and the shaped units are preferably agglomerates As indicated above, the agglomerates are normally made by mixing the absorbent material with a binder and a little water and then forming the composition into granules The binder is preferably a cement such as a calcium aluminate cement Since the binder represents non-absorbent material, its proportion is preferably kept to a minimum consistent with obtaining agglomerates of strength sufficie to withstand handling and the loads encountered during normal use The amount of cement is typical 5-10% by weight of the agglomerates Similar amounts of cement may be used when the shaped articles are in the form of extruded pellets In the aforesaid EP-A-0 243 052 it was preferred that the agglomerates contain zinc compound eg basic zinc carbonate We have found that, at low absorption temperatures, eg below about 100°C copper compounds are superior absorbents for hydrogen sulphide compared to zinc compounds Accordingly it is preferred that the shaped absorbent units of the present invention contain less than 10% by weight of zinc compounds and preferably essentially no zinc compounds, although it will be appreciated that such compounds may inevitably be present as impurities in the other components For most applications the shaped units, e g agglomerates, may comprise simply an absorben material selected from copper carbonate, basic carbonate and/or hydroxide, and a binder Where th absorbent is to be used for hydrogen sulphide absorption, preferably at least 90% by weight of the shaped unit is such an absorbent material However, as described below, where the absorbent is to be used for removal of hydrolysable sulphur compounds such as carbonyl sulphide, the shaped unit preferably also contain a high surface area gamma alumina to catalyse the hydrolysis of the carbony sulphide in this case, preferably the shaped units contain 9 to 20% by weight of such alumina and s the content of copper carbonate basic carbonate or hydroxide is typically in the range 75 to 85% by weight The absorbent material eg basic copper carbonate, may be naturally occurring mineral that ha been ground to a suitable size powder, or may be a synthetic product obtained by precipitation Where it is required that alumina (in addition to any present in the cement binder) is included, the alumina may be added as a powder to the absorbent material powder or may be introduced by precipitation Thus it may be co-precipitated with the absorbent material, or the latter may be precipitated into a slurry of precipitated alumina, or the aiumina may be precipitated into a slurry of th absorbent material Alternatively slurries of separate precipitates may be mixed After such precipitation, the precipitates are filtered off, and dried However the drying conditions should be suc that the copper carbonate or basic carbonate is not decomposed to any significant extent Thus the drying should be effected at a temperature no higher than about 150 β C, and preferably at a temperature no higher than 115 β C Where the shaped units are agglomerates or extruded pellets, in order that the shaped units may be made with a high bulk density, it is desirable that the absorbent material powder used to mak the shaped units has a particle size and particle size attribution, such that the D s0 particle size is between about 4 μm and 12 μm, the D 90 particle size aDout 1 4 to 2 5 times the value of D 50 , and the particle size about 0 15 to 0 5 times the value of D 50 [By the terms D 10 , D 50 , and D M particle sizes, w mean the sizes at which 10%, 50%, and 90% by volume, respectively, of the particles have a size smaller than the quoted value] With powders of particle size, or particle size distributions, outside these ranges it may prove to be difficult to achieve high bulk density agglomerates The absorbent units of the invention are of particular use for removing hydrogen sulphide from gas or liquid streams at low temperatures The temperature at which they are employed should be ιess than about 150°C at which significant decomposition of the copper carbonate or basic carbonat may start to occur Preferably the absorption is effected at below 100 β C, particularly where the absorbent material comprises copper hydroxide The temperature is most preferably in the range -10°C to 80°C The absorption process may be effected at any suitable pressure, typical pressures range from atmospheric up to about 200 bar abs Where the gas or quiα being treated contains carbonyl sulphide and/or carbon disulphide as well as, or instead of, hydrogen sulphide, then it is desirable to employ absorbents containing a proportion of alumina, in addition to any alumina present in the binder The alumina should be a hig surface area gamma alumina, preferably having a BET surface area of at least 150 rrrVg The alumi assists the reaction of the carbonyl sulphide or carbon disulphide It is not normally necessary to ad any water to the fluid to effect such hydrolysis thus some hydroxyl groups will normally be associate with the alumina and water is evolved upon absorption of the hydrogen sulphide produced by the hydrolysis, e g COS + H.0 > CO. + H.S Cu(OH). CuC0 3 + 2H 2 S > 2CuS + C0 2 + 3H,0 and so will be available for further hydrolysis Indeed, with conventional zinc or iron absorbents, it has been found that the addition of water t the gas stream is desirable in order to maximise the amount of sulphur that a given volume of absorbent can absorb. Addition of water to hydrocarbon gas streams however is desirably avoided because of the risk of formation of hydrocarbon hydrates which, at high operating pressures, may separate out and cause blockages in pipelines In contrast, we have found that there is no need to add water where the absorbent is a copper compound as specified above. The fluid being treated may be a hydrocarbon stream, e.g. natural gas, substitute natural gas, natural gas liquids, naphtha, reforming gases, for example hydrocarbon streams such as propylene separated from the product of cracking naphtha; synthesis gas produced, for example, by the partial oxidation of a carbonaceous feedstock; organic compounds such as alcohols, esters, or chlorinated hydrocarbons; or other gases such as carbon dioxide, hydrogen, nitrogen, or helium. In order to maximise the absorption capability of a bed of absorbent, it is preferable to operate the desulphuπsation process using two beds in series. By this means it is possible that the first bed can become fully saturated with sulphur compounds before unacceptable sulphur compound break-through occurs into the effluent from the second bed. When the first bed is fully saturated, it is replaced with fresh absorbent and the order in which the fluid being treated passes through the beds reversed. Thus ' the partially saturated bed that was the second bed gas is now used as the first bed through which the fluid passes and the fresh bed becomes the bed through which the fluid passes aft passage through the partially saturated bed The invention is illustrated by the following examples in which samples of basic copper carbonate (malachite) powders of differing particle sizes and particle size distribution as follows were employed' Powder D 10 D.o D 9D Da o Dι«/D» bulk density of powder (μm) (μm) (μm) (kg/l) A 1.5 7.6 14 4 1.9 0 2 1.34 B 1 7 8.0 15.1 1.9 0.2 1.36 C 3.0 7.6 12.6 1.7 0.4 1.46 D 1.9 44 8.7 2.0 0.4 0.63 E 1 1 4.2 7.1 1.7 0.3 1.30 The bulk density (BD) was assessed by charging the material under test to a 100 ml measurin cylinder until the measuring cylinder, after tapping the side thereof to permit settling of the material, was filled to the 60 mi mark. The weight of the material in the cylinder was then determined Example 1 Shaped units in the form of agglomerates were made by mixing 93 parts by weight of the appropriate basic copper carbonate powder with 7 parts by weight of calcium aluminate cement powder and a little water, insufficient to give a slurry, and the mixture formed into roughly spherical agglomerates the bulk of which had approximate diameters within the range 3-5 mm using a laborator granulator Agglomerates of size within this range were separated from the remainder of the composition by sieving and then dried at 110°C for 4 hours The dried agglomerates made from powders A, B, and C had bulk densities in the range 1 33 to 1 37 kg/l, but the agglomerates made fro powder D had a bulk density of only 0 85 kg/l, indicating that it was desirable to employ a high bulk density powder in order to obtain high bulk density agglomerates Samples of other basic copper carbonate powders of high bulk density but of larger particle size (D 10 16 9 and 25 1 μm, 0^26 8 and 41 7 μm, and D 90 44 8 and 74 3 μm respectively) gave only low yields of agglomerates of the desired The absorption characteristics of the dried agglomerates made from powders A, B, and C respectively were determined by passing natural gas containing 1 % by volume of hydrogen sulphide atmospheric pressure and 20°C down through a vertical cylindrical bed of the appropriate agglomerates of height 12 cm and neight to diameter ratio 5 at a space velocity of about 700 h" 1 The time taken before hydrogen sulphide could be detected (at the 1 ppm level) in the exit gas was determined and is quoted in the following table as the "break-through" (B-T) time Samples were the taken from different heights of the bed (Portion 1 is the first 2 cm depth of the bed from the top, Portio 2 is the portion 2-4 cm from the top etc so that Portion 6 is the bottom portion of the bed, i e the portion 10-12 cm from the top) and analysed for the sulphur content The results are shown in the following table Sulphur content (% by weight) Powder Agglomerates Break-through Bed portion BD (kg/l) time (hrs) 1 2 3 4 5 6 Average A 1 37 20 28 30 29 28 15 2 22 B 1 35 16 17 29 28 25 12 2 19 C 1 33 15 8 25 29 26 13 3 17 The theoretical sulphur absorption capacity of the agglomerates was about 360-370 g/l At the theoretical absorption capacity each portion of the bed would have a sulphur content of about 31% b weight the actual sulphur capacity (calculated from the average sulphur content) of the beds ranged from about 210 g/l (for agglomerates made from powder C) to about 270 g/l (for agglomerates made from powder A) It is seen from the above data that the sulphur content of at least portions 2 to 4 of the bed wa close to the theoretical maximum Therefore if two absorbent beds corresponding respectively to portions 1 -3 and 4-6 were utilised in series the first bed, i e corresponding to portions 1-3, would become fully saturated, i e have an average sulphur content of about 29% by weight (in the case of the agglomerates made from powder A) which is close to the theoretical maximum, before an unacceptable amount of sulphur was detected in the effluent from the second bed, corresponding to portions 4-6. At this stage the second bed (in the case of the agglomerates made from powder A) has an average sulphur content of about 15% by weight and so if then used as the first in a series of beds has the ability of absorbing about the same amount of sulphur again before it needs replenishing. Example 2 (comparative) By way of comparison agglomerates were made in accordance with the teaching of EP-A-0243 052 by mixing 93 parts by weight of an uncalcined co-precipitated zinc-substituted malachite/alumina powder (wherein the copper, zinc and aluminium were in the atomic proportions Cu 55: Zn 27: Al 18) with 7 parts by weight of calcium aluminate cement powder and granulating the mixture as described above. The D 10 , D 50 , and D g ,, particle sizes of the co-precipitated zinc-substitute malachite/alumina powder were 3.4, 7.7 and 17.5 μm respectively. The dried agglomerates had a bul density of 0.95 kg/l and a theoretical sulphur absorption capacity of about 230 g/l. The results of sulphur absorption testing of a bed of the agglomerates by the method described in Example 1 were as follows: Sulphur content (% by weight) Agglomerate bulk Break-through Bed portion density (kg/l) time (hrs) 1 2 3 4 5 6 Average 0.95 12 20.3 22.0 21.9 18.9 8.1 1.8 15.5 The calculated actual sulphur absorption capacity was only 137 g/l. Example 3 (comparative) Following the procedure of Example 1 of US 4 521 387, 2000 g of copper nitrate trihydrate, 3132 g of zinc nitrate hexahydrate, and 414 g of aluminium nitrate nonahydrate were dissolved in water and the solution diluted to 10 I. Another solution was made by dissolving 2180 g of sodium carbonate in water and diluted to 10.28 I. The two solutions were fed separately to a continuous, stirred, precipitation apparatus maintained at 80°C while controlling the rates of feed so that the pH was maintained at 7-7.5. The resulting precipitate was stirred for 45 min at 75°C and then the precipitate was filtered off and washed. The precipitate was then dried in an oven at 115°C for 12 hours and then calcined at 270°C to a constant loss on ignition (at 900°C) of 10% by weight. Analysis of the resultant powder showed the following composition (by weight): CuO 42.7% ZnO 53.3% Al 2 0 3 3.8% A portion of the calcined precipitate was then mixed with 2% by weight of graphite and the mixture moulded into cylindrical tablets of 5.4 mm diameter and 3.6 mm height using a laboratory tableting machine. The crushing strength of the resultant cylindrical tablets was assessed by applyi an increasing load between the flat faces of the cylinder until the pellets broke: the average load required to crush the tablets was 123 kg which corresponds to a crushing strength of 537 kg/cm 2 . T tablets had a buik density of 1 07 kg/l, while the density of the individual tablets, i.e the particle densit was 1.85 kg/l. Another portion of the calcined precipitate was mixed with 6.5% by weight of calcium aluminate cement and a little water and the mixture formed into spherical agglomerates of diameters ranging fro 3.35 to 4.85 mm using a laboratory granulator. The agglomerates were then dried at 115°C for 4 hours. The load required to crush the agglomerates was 0.4 kg. The bulk density of the agglomerates was 0 54 kg/l Testing beds of the tablets and agglomerates for hydrogen sulphide absorption by the method described in Example 1 gave- Sulphur content (% by weight) Sample bulk density Break-through Bed portion (kg/l) time (mm) 1 2 3 4 5 6 Avg tablets 1.07 195 6.9 5.7 4 4 2.4 1.2 0.3 3.5 agglomerates 0.54 180 7 0 7.2 7.6 7.3 7.5 2.2 6.5 The calculated theoretical and actual sulphur absorption capacities were 371 and 34 g/l respectively for the tablets and 175 and 33 g/l respectively for the agglomerates Example 4 The procedure of Example 1 was repeated using 90 parts by weight of basic copper carbonate powder E and 10 parts by weight of the calcium aluminate cement, and using a larger scale granulato which imposed more shear on the mixture during granulation. The resultant agglomerates had a bulk density of 1 6 kg/l, and gave the following results when tested for hydrogen sulphide absorption as in Example 1 In this example the sulphur capacity of the bed portions is quoted (g/l) rather than the sulphur content (% by weight) of the bed portions. Sulphur content (g/l) Powder agglomerates Bed portion BD (kg/l) 1 2 3 4 5 6 Avg E 1.6 346 346 332 258 114 12 235 The theoretical absorption capacity of the bed was about 410-420 g/l. Example 5 Shaped units in the form of agglomerates were made by the procedure of Example 1 using 100 parts by weight of the powder E, 10 parts by weight of gamma alumina of BET surface area (SA) 185 mVg, and 7 parts by weight of a calcium aluminate cement The resultant agglomerates had a BET surface area (SA) of 27 4 m 2 /g and contained about 85.5% by weight of malachite. A bed of the agglomerates had a bulk density (BD) of 1.33 kg/l. The agglomerates were tested for hydrogen sulphide absorption as in Example 1 The break-through (B-T) time was 17 4 hours and the average sulphur content of the bed was 170 g/l. It is seen by comparison with Example 1 that the incorporatio of the alumina decreased the sulphur absorption capacity of the bed The absorption test was then repeated using a fresh sample of the agglomerates and using carbonyl sulphide in place of hydrogen sulphide. The break-through time (B-T) taken before carbony sulphide could be detected (at the 10 ppm level) in the exit gas was 16.4 hours and the average sulphur content of the discharged bed was 124 g/l. Examples 6-11 Agglomerates were made as descπbed in Example 5 with different amounts of gamma alumina and using aluminas of different types. The absorption of carbonyl sulphide was tested as described i Example 5. The results, together with those of Example 5, are as shown in the following table. Alumina agglomerates COS removal Ex (parts) SA malachite SA BD B-T time sulphur (m 2 /g) (wt%) (m 2 /g) (kg/l) (hrs) capacity (g/l) 5 10 185 85.5 27.4 1.33 16.4 124 6 20 185 78.7 45.0 1.31 20.0 163 7 5 185 89.3 18.9 1.35 3.2 25 8 10 65 85.5 14.6 1.31 0 6 5 9 10 4 85.5 12.8 1.33 0.5 3 10 10 258 85.5 18.3 1.31 9.8 83 11 10 128 85.5 23.4 1.28 3.1 24 The alumina used in examples 5-7 was gamma alumina. The aluminas used in examples 8-11 were as follows: Example 8 gamma alumina calcined at 900°C so as to reduce its surface area Example 9 alumina tπhydrate Example 10 alumina trihydrate calcined at 350°C Example 11 alumina trihydrate calcined at 700°C Results similar to those of Example 8 were obtained with gamma alumina calcined at 1100°C and 1250°C to give alumina of surface areas 32 and 8 m /g respectively. These examples indicate t it is desirable to employ a high surface area gamma alumina if carbonyl sulphide is to be effectively removed. Example 7 demonstrates that the use of a small amount of alumina, viz 4.5% by weight of the agglomerates, does not enable carbonyl sulphide to be satisfactorily removed. Examples 12-14 Cylindrical tablets of 5 4 mm diameter and 3.5 mm height were moulded using a laboratory tableting machine formed from 100 parts by weight of malachite powder E, 2 parts by weight of graphite as a lubricant, and, in examples 13 and 14, also 7 and 11 part by weight of calcium alumina cement respectively The resultant tablets were then tested for their hydrogen sulphide absorption properties as in Example 1 The results were as follows tablets Hydrogen sulphide removal Ex malachite SA BD B-T time sulphur (wt%) (m 2 /g) (kg/l) (hrs) capacity (g/l) 12 98 0 8.0 1.64 16.4 167 13 91 7 5 7 1.62 12.3 114 14 88.5 7.0 1.64 13.2 127 By comparison with Examples 1 and 4 it is seen that despite the high bulk density, the sulphur capacity is significantly inferior to that of agglomerates, probably as a result of the low surface area of the tablets. Example 15 Shaped articles in the form of extrudates of diameter about 2 mm and length 5-10 mm were made from a mixture of 90 parts of malachite powder E, 7 parts by weight of a clay extrusion aid and 7 parts by weight of calcium aluminate cement by mixing with a little water to form a paste which was then extrudes through a suitable die using a single screw extruder. The extrudates were dried at about 110°C. The resultant extrudates were then tested for their hydrogen sulphide absorption properties as in Example 1 The results were as follows. extrudates Hydrogen sulphide removal Ex malachite SA BD B-T time avg sulphur sulphur (wt%) (m 2 /g) (kg/l) (hrs) content (%wt) capacity (g/l) 15 84 1 20 3 0 95 13.3 14 8 121 It is seen that the sulphur capacity is relatively low, as a result of the relatively low bulk density.

Claims: AMENDED CLAIMS [recei ved by the Internationa l Bureau on 10 August 1995 ( 10.08.95 ) ; origi nal cl aim 1 amended ; remaini ng cl aims unchanged ( 1 page ) ] 1. Shaped absorbent units having an average size within the range 1-10 mm and containing at least 75% by weight of an absorbent material selected from copper carbonate, basic copper carbonate, and copper hydroxide and mixtures thereof. 2. Shaped absorbent units according to claim 1 having a bulk density of at least 0.9 kg/l. 3. Shaped absorbent units according to claim 2 containing at least 80% by weight of copper carbonate or basic copper carbonate and having a bulk density of at least 1.2 kg/l. 4. Shaped absorbent units according to any one of claims 1 to 3 in the form of agglomerates containing 5-10% by weight of a cement binder. 5. Shaped absorbent units according to any one of claims 1 to 4 wherein the absorbent material is basic copper carbonate. 6. Shaped absorbent units according to any one of claims 1 to 5 having a BET surface area of at least 10 m 2 /g. 7. Shaped absorbent units according to any one of claims 1 to 6 containing 9 to 20% by weight of gamma alumina having a surface area of at least 150 m /g. 8. A process for the absoφtion of hydrogen sulphide from a gas or liquid comprising passing said gas or liquid through a bed of shaped absorbent units according to any one of claims 1 to 7 at a temperature below 150°C. 9. A process for the absoφtion of carbonyl sulphide or carbon disulphide from a gas or liquid comprising passing said gas or liquid through a bed of shaped absorbent units according to claim 7 at a temperature below 150°C. 10. A process according to claim 8 or claim 9 wherein said gas or liquid is passed through the at a temperature in the range -10°C to 80°C. STATEMENT UNDER ARTICLE 19 Claim 1 has been amended by the deletion of the phrase: "said units having a bulk density of at least 1.2 kg per litre" This amendment brings the claims into conformity with the description (see page 2 lines 11-13). The deleted limitation was clearly an error as the unamended claim was narrower than the dependent claim 2.

Inventors: CARNELL PETER JOHN HERBERT, DENNY PATRICK JOHN, WILLIAMS BRIAN PETER, WOOD PETER, WOODROFFE CATHY ANNE, CARNELL, PETER, JOHN, HERBERT, DENNY, PATRICK, JOHN, WILLIAMS, BRIAN, PETER, WOOD, PETER, WOODROFFE, CATHY, ANNE
Applicants: CARNELL PETER JOHN HERBERT, DENNY PATRICK JOHN, ICI PLC, WILLIAMS BRIAN PETER, WOOD PETER, WOODROFFE CATHY ANNE, CARNELL, PETER, JOHN, HERBERT, DENNY, PATRICK, JOHN, IMPERIAL CHEMICAL INDUSTRIES PLC, WILLIAMS, BRIAN, PETER, WOOD, PETER, WOODROFFE, CATHY, ANNE
Application year: 1995
Main classification: B01J20
IPC codes: B01D15, B01D53, B01J20