SUBSTITUTED PHENYL COMPOUNDS AND PROCESSES FOR PREPARING THE SAME

Abstract: Substituted phenyl compounds endowed with chain extension activity for formulations such as polyurethanes are disclosed, and which have general formula (I) wherein n is 1-1000 and m is 1-100; and R1 and R2 are each independently selected from the group -C2H4- and -C3H6-; and R3 is from the group consisting of (a), and (b) and the diasteromeric salts thereof.

Description: SUBSTITUTED PHENYL COMPOUNDS & PROCESSES FOR PREPARING THE SAME This application is a Continuation-In-Part of pending patent application Serial No. 08/070,144 filed May 28, 1993. BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to novel derivatives of 4- hydroxyacetophenone (4-HAP) to processes for preparing them, to polymer compositions which contain the novel compounds, and to the use of said compositions for a wide variety of end use applications. Description of Related Art The following prior art references are disclosed in accordance with the terms of 37 CFR 1.56, 1.97, and 1.98. U.S. 5,169,848, issued December 8, 1992, to Bettarini et al., discloses new pyridazinones endowed with insecticidal and acaricidal activity. U.S. 3,520,931, issued July 21, 1970, to d'Ostrowick et al., discloses a process for resolving a mixture of optical antipodes of a primary alpha- arylalkylamine in which one of these antipodes predominates. U.S. 5,011,996, issued April 30, 1991, to Kiel et al., discloses reaction products of oxo compounds and amines or ammonia, such as α-(p- Cholorophenyl)-ethylamine (Example 1 therein). U.S. 4,394,496, issued July 19, 1983, to Paul G. Schrader, discloses polyglycidyl ethers of these (hydroxyphenyl) alkanes, their blends with other epoxy compounds, and their cured products. U.S. 4,388,250, issued June 14, 1983, to Farber et al., discloses a process for the preparation of p-Hydroxybenzyl-nitrites (note Table I, columns 7 and 8). Other U.S. patents which have related application and may be of interest include U.S. 2,298,284; U.S. 3,366,684; U.S. 3,739,026; U.S. 3,225,098; U.S. 3,928,603; and U.S. 5,047,592. All of the above-cited prior art patents are incorporated herein by reference in their entirety. Additional Background Information Compounds belonging to the class of hydroxyacetophenones, processes for preparing the same, and their end use applications are disclosed in U.S. 4,663,485; U.S. 4,524,217; U.S. 4,933,496; and U.S. 4,994,613, the entire disclosures of which patents are incorporated herein by reference. SUMMARY OF THE INVENTION The present invention provides novel substituted phenyl compounds ("SPC") endowed with chain extension activity for formulations such as polyurethanes and which have the general formula: wherein n is 0-1000; and R, and R 2 are from the group -CH 2 -CH 2 -; -CH 2 - C(CH 3 )H-; and -C(CH 3 )H-CH 2 -; and R 3 from the group consisting of: O OH -C- , and - C H and the diasteromeric salts thereof. Detailed Description of the Preferred Embodiments 10 The present invention provides novel substituted phenyl compounds (SPC) which are derivatives of 4-hydroxyacetophenone, a well-known basic building block for numerous organic compounds. These novel SPC's have the general formula as follows: wherein: > , 15 n is 0 to 1000 (preferably 0 to 100); R. equals R 2 ; R, and R 2 represent a member from the group: -CH-,-CH 2 - -CH 2 -C(CH 3 )H- -C(CH 3 )H-CH 2 -; and R 3 is from the group: O and - C - o I - c - I H The compounds having the general formula (I) can be prepared by reacting an alkali metal salt of 4-hydroxyacetophenone (4-HAP) with an oxide material such as ethylene oxide or propylene oxide in the presence of a suitable catalyst to form the novel SPC having the above formula (I). This overall reaction scheme using ethylene oxide is shown as follows: In equation (A), M is an alkali metal such as potassium. In equation (B), X represents the number of molar equivalents of the ethylene oxide (or propylene oxide) is used to form the chain, and N+l equals X. n can be 0 to 1000, but are preferably from 0 to 100. In the formulation of the alkali metal salt of 4-HAP, equation (A), the reactants are mixed together in a reaction vessel along with a suitable inert solvent such as isopropanol and then heated at about 30°C to about 100°C for a sufficient period of time until all the solids are dissolved into the liquid. The resultant reaction mass is then allowed to cool to room temperature and then the desired alkali metal salt is allowed to crystalize over a period of time suitable to promote crystallization from the solution. The solid material, i.e. the 4-HAP salt, is then separated from the mother liquor by any conventional means, such as filtration. The solid material is then washed with a suitable inert solvent such as heptane and then dried at a temperature of from about 30°C to about 100°C, under vacuum, where so desired. In conjunction with equation (B) above, the alkali metal salt of 4-HAP is charged into a reaction vessel along with pre-selected quantities of either ethylene oxide or propylene oxide and a suitable inert solvent such as dimethylformamide (DMF). The reaction vessel is provided with a condenser and a mechanical stirrer. The reaction mass is then slowly heated from room temperature (i.e. 20°C) to about 100°C over a period of time to insure that the ethoxylation of propoxylation takes place in the desired fashion. While this part of the process is conducted at atmospheric pressure, it is within the scope of the present invention to conduct this reaction under pressure, e.g. from about 20 psig to about 300 psig, and thus reduce the reaction times. After the reaction has taken place, the reaction mass is allowed to cool to room temperature and then a suitable de-salting agent, such as acetic acid, is added to this mass in order to remove and inactivate the alkali metal ion. This ion complex precipitates and the resultant suspension is separated from the mother liquor by any conventional means such as filtration. This liquid is then reduced under vacuum to an oil, and the oil is then distilled under vacuum and the fraction boiling between 130°C and 210°C is collected and represents the desired end product, i.e. the ethoxylated or propoxylated 4-HAP. Referring to equation (B), it was unexpectedly found that the reaction produces two separate materials which can be recovered by any conventional means such as distillation. The substituted phenyl compounds (SPC) of this invention are particularly suited for reaction with isocyanates to manufacture articles by a Reaction Injection Molding (RIM) process. RIM is a technique for the rapid mixture and molding of large, fast-curing urethane parts. RIM polyurethane parts are used in a variety of exterior body applications on automobiles where the light weight contributes to energy conservation. RIM parts are generally made by rapidly mixing active hydrogen-containing materials with polyiso- cyanate and placing the mixture into a mold where reaction proceeds. After reaction and de-molding, the parts may be subjected to an additional curing step which comprises placing the parts in an oven, held at 250°F or higher. Surprisingly, it also has been found that the substituted phenyl compounds of this invention are useful as curing agents in forming clear epoxy castings and adhesives with highly satisfactory physical properties. Such epoxy products find application in the electrical and electronic fields. These SPC's also have been found to be suitable for use in polyamides, polyesters, polycarbonates, and epoxy resins. The following specific examples are supplied for the purpose of better illustrating the invention. These examples are not intended, however, to limit or restrict the scope of the invention in any way and should not be construed as providing conditions, parameters, or values which must be utilized exclusively in order to practice the present invention. Example 1 Synthesis of Potassium Salt of 4-Hydroxyacetophenone A mixture of 4-hydroxyacetophenone (556 g), potassium hydroxide (273 g), and isopropanol (3 L) is charged to a 5 L glass reactor fitted with a condenser and mechanical stirrer. The mixture is heated until all of the solids are dissolved (80°C). The solution is then cooled to room temperature and the product is allowed to crystallize for 12 hours. The solid is isolated by filtration, washed with heptane (1 L), and dried under vacuum (60 torr., 50°C). The product is a light yellow solid and weighs 610 g (86%). This reaction is representative of equation (A) above. Example 2 A mixture of potassium 4-acetyl phenolate (313 g), propylene oxide (507 g), and DMF (900 mL) is charged to a 3 L glass reactor fitted with a condenser and a mechanical stirrer. The reaction is heated and the temperature slowly increases from 52°C to 82°C over a period of three hours. The mixture is cooled to room temperature and acetic acid (108 g) is slowly added. The suspension is filtered and the filtrate is reduced under vacuum to an oil. The oil is distilled under vacuum (0.5 torr.) and the fraction boiling between 140°C to 205°C is collected. The product is a clear, colorless liquid and weighs 284 g (63%). Typical physical properties are given in Table I. This reaction is representative of equation (B) above, except that propylene oxide is used instead of ethylene oxide. TABLE I Tvpical Properties of Propoxvlated 4-Hvdroxv- acetophenone Propoxylated Property 4-Hvdroxvacetophenone Average n (wt %) n = 0 12.58 n = l 76.08 n = 2 11.34 n = 3 Molecular Weight (Average) 251.28 Boiling Range 140-193°C (<1 torr.) Density (@ 27°C) 1.094 g/mL Color Clear, Colorless Liquid Solubility (>5 wt %) Water No Acetone Yes Methanol Yes N,N-Dimethylformamide Yes Heptane No Ethyl Acetate Yes Examples 3-18 Using the procedures set forth in Examples 1 and 2 above, the compounds reported in Table II are obtained. It is inherent that isomers of the propyl group are formed; however, NMR indicates that the indicated compounds are formed. TABLE π Example RιZE 2 n Average) E 3 3 -CH 2 -CH 2 - 2 -C(O)- 4 -CH 2 -CH 2 - 13 -C(OH)H- 5 -CH 2 -CH 2 - 81 -C(O)- 6 -CH 2 -CH 2 - 4 -C(O)- 7 -CH 2 -CH 2 - 3 -C(OH)H- 8 -CH 2 -CH 2 - 6 -C(OH)H- 9 -CH 2 -CH 2 - 10 -C(OH)H- 10 -CH 2 -CH 3 - 4 -C(O)- 11 -CH 2 -C(CH 3 )H- 5 -C(O)- 12 -CH 2 -C(CH 3 )H- 5 -C(OH)H- 13 -CH 2 -C(CH 3 )H- 9 -C(OH)H- 14 -CH 2 -C(CH 3 )H- 5 -C(OH)H- 15 -CH 2 -C(CH 3 )H- 5 -C(O)- 16 -CH 2 -C(CH 3 )H- 11 -C(O)- 17 -C(CH 3 )H-CH 2 - 3 -C(OH)H- 18 -C(CH 3 )H-CH 2 - 3 -C(O)- Example 19 Synthesis of a Polyurethane with SPC A 2.0 g sample (0.012 mole) of tolylenediisocyanate (a 80:20 mixture of 2,4 and 2,6 tolylenediisocyanate) is mixed carefully with a 2.9 g sample (0.011 mole) of the SPC prepared according to the procedure in Example 2 above. The mixture thickens and hardens to a glassy resin with the generation of heat. The material is a hard, clear, amber solid and is found to be suitable for use in automobile parts. Examples 20-36 Preparation of Polyurethanes Containing SPC Polyurethanes are prepared incorporating SPC by substitution of SPC for other polyols present in a reaction mixture. Examples are described in the Encyclopedia of Polymer Science & Engineering, Volume 1, pgs. 243-303 (2nd Edition, 1988, John Wiley & Sons). As used herein, the term, "polyurethane" refers to materials that include the carbamate function as well as other functional groups such as ester, ether, amide, and urea. Polyurethanes are usually produced by the reaction of a polyfunctional isocyanate with a polyol or other hydroxyl- containing reactant. Since the functionality of the hydroxyl-containing reactant or the isocyanate can be adjusted, a wide variety of branched or cross-linked polymers can be formed. The hydroxyl-containing component may be of a wide variety of molecular weights and types including polyester and polyester polyols. The polyfunctional isocyanates may be aromatic, aliphatic, cycloaliphatic, or polycyclic in structure and can be used directly as produced or modified. The flexibility in reactants leads to the wide range of physical properties of available materials. Present invention polymers are prepared by substituting SPC for a portion of the hydroxyl-containing reactant in a mole ratio of SPC/hydroxyl from about 0.001:1 to about 1:1 for the polyol in a polyurethane reaction mixture, or, in other words, from about 0.05 to about 50 mole percent of the total mixture as described above in connection with Example 19. Specifically, Example 19 is repeated using the SPC compounds from Examples 3-18. The resultant polyurethane compositions are found functional in a wide variety of automobile parts. In conjunction with the novel SPC compounds falling within the general structural formula (I) above, each of these compounds contains a chiral carbon atom and, consequently, is a racemate which consists of two mirror-image forms (enantiomers). Where one so desires to provide and/or use only one or single enantiomer thereof, it is within the scope of the present invention that this can be accomplished by means well-known in chirotechnology such as optical resolution by known resolving agents such as optically pure chiral acids. Examples of chiral acids include, without limitation thereof, tartaric acid, molic acid, camphorsulfonic acid, lactic acid, bromocamphorsulfonic acid, mandelic acid, 2- (4-isobutyl-phenyl)-propionic acid (ibuprofen), and derivatives thereof. The use of these chiral acids with the novel SPC provides the diasteromeric salts thereof. Additional general information on chirotechnology may be found in Enantiomers. Racemates. and Resolutions. Jacques et al., Krieger Publishing Company (Malabar, Florida) 1991 and which is incorporated herein by reference in its entirety. In another facet of the present invention, there is provided novel compounds and processes for preparing the same where one so desires to "end- cap" the polymer chain. In the polymer art, e.g., see Encyclopedia of Polymer Science & Engineering, Supplement Volume - 1990, page 408, John Wiley & Sons (New York) and which book is incorporated herein by reference in its entirety; there are numerous reasons to "end-cap" the chain, e.g. to prevent decomposition. Thus, in this part of the present invention, there are provided the following novel end-capped compounds: I. Substituted phenyl compounds having the structural formula: wherein n is 1-1000 and m is 1-100; and R, and R 2 are each independently selected from the group consisted of -C,H 4 - and -C 3 H 6 -; and R 3 is from the group: O and OH C - , - C - H and the diasteromeric salts thereof. Compounds falling within formula (A) above include, without limitation, (B) and (C) below. II. Substituted phenyl compounds having the structural formula: wherein n is 1-1000 and m is 1-100; and R. is from the group consisting of: O and OH - C - , - C - I H and the diastereomeric salts thereof. III. Substituted phenyl compounds having the structural formula: wherein n is 1-1000, m is 1-100; and R, is from the group consisting of: O and OH -C - C H and the diasteromeric salts thereof. In formulae (A), (B), and (C) above, m is an integer from about 1 to about 100, preferably from about 1 to about 10, and represents the "end-capping" function of the polymer. The end-capping of the polymer is accomplished by contacting the initial reaction mixture (after reaction) with either ethylene oxide or propylene oxide. This is illustrated by the following example which is basically a repeat of Example 2. Example 37 A mixture of potassium 4-acetyl phenolate (313 g), propylene oxide (507 g), and DMF (900 mL) is charged to a 3 L glass reactor fitted with a condenser and mechanical stirrer. The reaction is heated and the temperature slowly increases from 52°C to 82°C over a period of three hours. At the end of this time, ethylene oxide (406 g) is contacted with the initial reaction mixture for a period of 30 minutes. The overall mixture is cooled to room temperature and acetic acid (108 g) is slowly added. The suspension is filtered and the filtrate is reduced under vacuum to an oil. The oil is distilled under vacuum (0.5 torr.) and the fraction boiling between 140°C to 205°C is collected. The product is a clear, colorless liquid and weighs 288 g (64%). The physical properties are similar to those in Table I except that m is 1.5 (average).

Claims: CLAIMS What is Claimed Is: 1. Substituted phenyl compounds having the formula: wherein n is 1-1000 and m is 1-100; and R j and R 2 are each independently selected from the group consisting of -C 2 H 4 - and -C 3 H 6 -; and R 3 is from the group: O and OH II - 1 -c- , -c- I H and the diasteromeric salts thereof. Substituted phenyl compounds having the structural formula: wherein n is 1-1000, m is 1-100; and R, is from the group consisting of: O and OH II I -c- , -c- I H and the diasteromeric salts thereof. 3. Substituted phenyl compounds having the structural formula: wherein n is 1-1000 and m is 1-100; and R, is from the group consisting of: O and OH -C- , -C- I H and the diasteromeric salts thereof. 4. The compound as set forth in claim 1 wherein R 3 is: O -C- 5. The compound as set forth in claim 1 wherein R 3 is: OH I -c- I H 6. The compound as set forth in claim 2 wherein R, is: O -C- The compound as set forth in claim 2 wherein R, is: OH - C - H 8. The compound as set forth in claim 3 wherein R is: O C - 9. The compound as set forth in claim 3 wherein Rj is: OH I -c- I H 10. A process for preparing substituted phenyl compounds having the structural formula: wherein n is 1-1000 and m is 1-100; and R, and R 2 are each independently selected from the group -C 2 H 4 -; and -C 3 H 6 -; and R 3 is selected from the group consisting of: O and OH II I -c- , -c- H which comprises the steps of (a) reacting an alkali metal hydroxide with 4- hydroxyacetophenone to form the alkali metal salt of said 4- hydroxyacetophenone, (b) reacting the alkali metal salt of 4- hydroxyacetophenone with an oxide material selected from the group consisting of ethylene oxide and propylene oxide to form the compounds covered by the structural formula set forth above. 11. The process as set forth in claim 10 wherein there is provided the further step of contacting the compound of the above structural formula with an optically active chiral acid for a sufficient period of time and temperature to form a diasteromeric salt thereof. 12. The process as set forth in claim 11 wherein the chiral acid is selected from the group consisting of tartaric acid, malic acid, camphorsulfonic acid, lactic acid, bromocamphorsulfonic acid, mandelic acid, 2-(4- isobutyl-phenyl)-propionic acid, and derivatives thereof. 13. The compounds according to claim 1, the residue of which is incorporated into a polyurethane polymer. 14. A polyurethane composition containing at lest one compound having the structural formula: wherein n is 1-1000 and m is 1-100; and R, and R 2 are each independently selected from the group -C 2 H 4 -; and -C 3 H 6 -; and R 3 is from the group consisting of: O and OH - C - , - C I H and the diasteromeric salts thereof. 15. The compounds according to claim 1, the residue of which is incorporated into an epoxy resin. 16. The composition as set forth in claim 14 wherein R 3 is: O II -c- 17. The composition as set forth in claim 14 wherein R 3 is: OH I -c- H 18. The compounds according to claim 1, the residue of which is incorporated into a polyester. 19. The compounds according to claim 1, the residue of which is incorporated into a polyurethane. 20. The compounds according to claim 1, the residue of which is incorporated into a polycarbonate. 21. The process as set forth in claim 10 wherein there is provided the further step of (C) end-capping the resultant polymer formed in step (B) by treating said polymer with sufficient quantities of the oxide material which was not used in step (B). 22. The process as set forth in claim 21 wherein the oxide material in step (B) is propylene oxide and the oxide in step (C) is ethylene oxide. 23. The product produced by the process as set forth in claim 22.

Inventors: SHEEHAN MICHAEL T, SOUNIK JAMES R, WILKINSON WILLIAM B III, SHEEHAN, MICHAEL, T., SOUNIK, JAMES, R., WILKINSON, WILLIAM, B., III
Applicants: HOECHST CELANESE CORP, HOECHST CELANESE CORPORATION
Application year: 1995
Main classification: C07C49
IPC codes: C07B57, C07C43, C07C45, C07C49, C08G18, C08G63, C08G64, C08G65