Anti-fogging coating composition, anti-fogging coated article and method for producing same

Abstract: An anti-fogging coating composition contains (a) an inorganic alkoxide and/or a hydroxyl group-containing polymer formed therefrom by hydrolysis and polycondensation, the inorganic alkoxide being represented by the formula (I): M(OR) n (X) a-n wherein M is an inorganic element selected from the group consisting of Si, Al, Ti, Zr, Ca, Fe, V, Sn, Li, Be, B and P; R is an alkyl group; X is an alkyl group with or without functional groups or a halogen atom; a is a number representing the valence of M; and n is an integer from 1 to a; (b) a polyalkylene oxide, a weight ratio of the polyalkylene oxide to the inorganic alkoxide and/or the hydroxyl group-containing polymer being 100/1-100/150; (c) 0.5 parts by weight or less of an acid catalyst per 100 parts by weight of (a); (d) 0.01-1 part by weight of a base catalyst per 100 parts by weight of (a) + (b); (e) 100-5,000 parts by weight of an organic solvent per 100 parts by weight of (a) + (b) + (d); and (f) a stoichiometric amount or more of water for the hydrolysis of the inorganic alkoxide.

Description: BACKGROUND OF THE INVENTION The present invention relates to an anti-fogging coating composition for providing substrates needing fog resistance and dew resistance such as optical lenses, spectacles, window glasses for vehicles and films for ink jet printers with hydrophilic or water-absorbing coatings which are insoluble and have a high surface hardness. The present invention also relates to an anti-fogging coated article produced therefrom and a method for producing the same. Substrates of glass or plastics are sometimes fogged, because moisture in the air is condensed to fine water droplets on substrate surfaces, causing irregular reflection of light thereon, when their surface temperatures are lowered below their dew points. Accordingly, by suppressing the formation of fine water droplets on the substrate surfaces, it would be possible to prevent their fogging. Examples of fog-preventing methods are (A) adjustment of wettability, (B) provision of water-absorbing properties, (C) provision of water-repelling properties, and (D) adjustment of temperature by heating, etc. (A) Adjustment of wettability Anti-fogging sprays are commercially available to decrease contact angles of water droplets to substrate surfaces, but such sprays do not have long-lasting anti-fogging effects because their anti-fogging functions are achieved by surfactants. (B) Provision of water-absorbing properties Water-absorbing properties may be obtained by hydrophilic polymer coatings. Their anti-fogging effects last longer than those of the anti-fogging sprays, but fogging takes place and further coats start dissolving if water is absorbed over their water absorption capacity. (C) Provision of water-repelling properties Water-repelling properties may be obtained by applying water-repelling compounds to substrates. Particularly when water-repelling compounds are applied to inner surfaces of plastic films of green houses, fine water droplets come to contact with each other to grow larger and flow down along the film surfaces, thereby exerting anti-fogging effects. However, fine water droplets rather stick to the film surfaces, rather aggravating fogging in some cases. (D) Adjustment of temperature by heating The adjustment of temperature by heating is effective for lenses of copying machines, rear windows of automobiles, mirrors of dressers, etc. However, the application of this method is restricted because it needs a power supply. To overcome the disadvantages of the above conventional methods, attempts have been made to provide water-resistant anti-fogging coats made of organic polymers such as polyether polyols and surfactants. Coats formed from such anti-fogging coating compositions have hydrophilic properties by the function of polyether polyols in the presence of surfactants, absorbing water thereby exerting anti-fogging properties. When water is absorbed over the limits of the coats, the surfactants function to control the wetting of the coat surfaces, thereby keeping transparency thereof. However, Since the surfactants are easily dissolved in water and washed away, the anti-fogging properties of the coats rapidly decrease. In addition, the anti-fogging coats are likely to have rapidly decreasing strength. OBJECTS AND SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide an anti-fogging coating composition capable of forming an anti-fogging coat with excellent hydrophilic properties and water absorption as well as excellent surface hardness. Another object of the present invention is to provide an anti-fogging coat formed from such an anti-fogging coating composition. A further object of the present invention is to provide a method for producing an anti-fogging coated article from such an anti-fogging coating composition. As a result of research in view of the above objects, it has been found that by providing a hydrophilic polymer coating with a hybrid structure in which inorganic skeletons are crosslinked with organic molecules, excellent anti-fogging properties and surface hardness can be achieved in the resultant anti-fogging coat while keeping insolubility. Thus, the anti-fogging coating composition according to the present invention comprises the components defined in claim 1. The anti-fogging coated article according to the present invention comprises a substrate and an anti-fogging coat formed on at least one surface of the substrate, the anti-fogging coat being made of the above anti-fogging coating composition. The method for producing the anti-fogging coated article according to the present invention comprises the steps of (i) applying the above anti-fogging coating composition to at least one surface of the substrate; and (ii) subjecting the resultant coated layer to a heat treatment at a temperature of 80°C or higher. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS [1] Anti-fogging coating composition The anti-fogging coating composition comprises the components defined in claim 1. [A] Inorganic alkoxides and/or hydroxyl group-containing polymers (a) Inorganic alkoxides (1) General The inorganic alkoxide used in the present invention may preferably be at least one compound represented by the general formula (I): M(OR) n (X) a-n wherein M is an inorganic element selected from the group consisting of Si, Al, Ti, Zr, Ca, Fe, V, Sn, Li, Be, B and P; R is an alkyl group; X is an alkyl group with or without functional groups or a halogen atom; a is a number representing the valence of M; and n is an integer from 1 to a. (2) M(OR) a Commonly used among the compounds represented by the general formula (I) are those having only alkoxyl groups bonded to M, namely n=a. (i) Alkoxysilanes When M is Si, the number "a" is 4. Such alkoxides may be called alkoxysilanes represented by Si(OR 1 ) 4 , wherein R 1 is an alkyl group having preferably 1-4 carbon atoms (hereinafter referred to as "lower alkyl group"). Examples of such alkoxysilanes include Si(OCH 3 ) 4 , Si(OC 2 H 5 ) 4 , Si(O-iso-C 3 H 7 ) 4 , Si(O-n-C 4 H 9 ) 4 , Si(O-t-C 4 H 9 ) 4 , etc. These alkoxysilanes may be used alone in combination. (ii) Aluminum alkoxides When M is Al, the number "a" is 3. Such alkoxides may be represented by Al(OR 2 ) 3 , wherein R 2 is preferably a lower alkyl group. Examples of such aluminum alkoxides include Al(OCH 3 ) 3 , Al(OC 2 H 5 ) 3 , Al(O-n-C 3 H 7 ) 3 , Al(O-iso-C 3 H 7 ) 3 , Al(O-n-C 4 H 9 ) 3 , Al(O-t-C 4 H 9 ) 3 , etc. These aluminum alkoxides may be used alone in combination. Such aluminum alkoxides are usually mixed with alkoxysilanes. By using the aluminum alkoxides, the resultant anti-fogging coat has improved transparency and heat resistance. The amount of the aluminum alkoxide is preferably 10 parts by weight or less, particularly about 5 parts by weight per 100 parts by weight of the alkoxysilane. If the amount of the aluminum alkoxide is more than 10 parts by weight, the resultant polymer is likely to be subjected to gelation, thereby providing cracks in the resultant anti-fogging coat. (iii) Titanium alkoxides When M is Ti, the number "a" is 4. Such alkoxides may be represented by Ti(OR 3 ) 4 , wherein R 3 is preferably a lower alkyl group. Examples of such titanium alkoxides include Ti(OCH 3 ) 4 , Ti(OC 2 H 5 ) 4 , Ti(O-n-C 3 H 7 ) 4 , Ti(O-iso-C 3 H 7 ) 4 , Ti(O-n-C 4 H 9 ) 4 , Ti(O-t-C 4 H 9 ) 4 , etc. These titanium alkoxides may be used alone in combination. Such titanium alkoxides are usually mixed with alkoxysilanes. By using the titanium alkoxides, the resultant anti-fogging coat has improved ultraviolet resistance and the substrate also is provide with improved heat resistance. The amount of the titanium alkoxide is preferably 3 parts by weight or less, particularly about 1 part by weight per 100 parts by weight of the alkoxysilane. If the amount of the titanium alkoxide is more than 3 parts by weight, the resultant polymer is likely to be brittle, whereby the anti-fogging coat formed on the substrate easily peels off. (iv) Zirconium alkoxides When M is Zr, the number "a" is 4. Such alkoxides may be represented by Zr(OR 4 ) 4 , wherein R 4 is preferably a lower alkyl group. Examples of such zirconium alkoxides include Zr(OCH 3 ) 4 , Zr(OC 2 H 5 ) 4 , Zr(O-n-C 3 H 7 ) 4 , Zr(O-iso-C 3 H 7 ) 4 , Zr(O-n-C 4 H 9 ) 4 , Zr(O-t-C 4 H 9 ) 4 , etc. These zirconium alkoxides may be used alone in combination. Such zirconium alkoxides are usually mixed with alkoxysilanes. By using the zirconium alkoxides, the resultant anti-fogging coat has improved toughness and heat resistance. The amount of the zirconium alkoxide is preferably 5 parts by weight or less, particularly about 3 parts by weight per 100 parts by weight of the alkoxysilane. If the amount of the zirconium alkoxide is more than 5 parts by weight, the resultant polymer is likely to be subjected to gelation and become brittle, whereby the anti-fogging coat formed on the substrate easily peels off. (v) Other alkoxides The other alkoxides than those described above may be Ca(OC 2 H 5 ) 2 , Fe 2 (OC 2 H 5 ) 3 , V(O-iso-C 3 H 7 ) 4 , Sn(O-t-C 4 H 9 ) 4 , Li(OC 2 H 5 ), Be(OC 2 H 5 ) 2 , B(OC 2 H 5 ) 3 , P(OCH 3 ) 3 , P(OC 2 H 5 ) 3 , etc. The total amount of these alkoxides is preferably 5 parts by weight or less per 100 parts by weight of the alkoxysilane. (3) M(OR) n (X) a-n (n≤a-1) In the inorganic alkoxides in which M is bonded to X in addition to alkoxyl groups (n≤a-1), X is preferably a halogen atom such as Cl and Br. In case where X is a halogen atom, X is converted to an OH group by hydrolysis like the alkoxyl groups, causing a polycondensation reaction as discussed in detail later. X may also be an alkyl group preferably having 1-15 carbon atoms with or without a functional group. The functional group is not subjected to hydrolysis, remaining in the resultant polymer as organic portions. Preferred examples of such functional groups include carbonyl groups, carboxyl groups, amino groups, vinyl groups and epoxy groups. These functional groups are preferable to improve the anti-fogging properties of the coatings. Examples of the inorganic alkoxides of the formula (I) having X include vinyltrichlorosilane, vinyltrimethoxysilane, vinyltriethoxysilane, γ-methacryloxypropyltrimethoxysilane, γ-glycidoxypropyltrimethoxysilane, γ-aminopropylmethoxysilane, etc. In the case of containing X, the amounts of the inorganic alkoxides may the same as described in (2) (i)-(iv) above. (b) Hydroxyl group-containing polymers Instead of adding the inorganic alkoxide itself or together therewith, it is possible to add a hydrolyzate of the inorganic alkoxide. The hydrolyzate of inorganic alkoxide is a hydroxyl group-containing polymer formed therefrom by hydrolysis and polycondensation in the presence of water and an acid catalyst. The hydrolyzate of an inorganic alkoxide may be an oligomer having a relatively low molecular weight, for instance, a polymerization degree of 3-50. The hydrolysis and polycondensation reaction of the inorganic alkoxide may generally be carried out at a temperature between room temperature and 50°C for 1 minute to 2 hours. Of course, a mixture of the inorganic alkoxide and the hydroxyl group-containing polymer may be used. [B] Polyalkylene oxide The polyalkylene oxide used in the present invention may be polyethylene oxide, polypropylene oxide, polypropylene glycol, etc. Most preferable among them is polyethylene oxide. The polyalkylene oxide has a weight-average molecular weight of preferably 30,000-1,500,000, more preferably 500,000-750,000. The weight ratio of the polyalkylene oxide to the inorganic alkoxide and/or the hydroxyl group-containing polymer is preferably 100/1-100/150, more preferably 100/5-100/100. If the weight ratio is less than 100/150, sufficient hydrophilic properties cannot be achieved. On the other hand, if the weight ratio exceeds 100/1, the surface hardness and durability of the resulting anti-fogging coat would become insufficient. [C] Catalyst The catalysts used in the present invention may be acid catalysts and base catalysts. (a) Acid catalyst The acid catalyst is used for the hydrolysis reaction of the inorganic alkoxide. Accordingly, when a hydroxyl group-containing polymer formed from the inorganic alkoxide by partial hydrolysis and polycondensation is contained, the acid catalyst may be omitted. The preferable examples of the acid catalysts are mineral acids such as hydrochloric acid, sulfuric acid, nitric acid, etc. Anhydrides of mineral acids such as a hydrochloride gas may also be used. Organic acids and their anhydrides may also be used. Examples thereof include tartaric acid, phthalic acid, maleic acid, dodecylsuccinic acid, hexahydrophthalic acid, methyl endic acid, pyromellitic acid, benzophenonetetracarboxylic acid, dichlorosuccinic acid, chlorendic acid, phthalic anhydride, maleic anhydride, dodecylsuccinic hexahydrophthalic anhydride, methyl endic anhydride, pyromellitic anhydride, benzophenonetetracarboxylic anhydride, dichlorosuccinic anhydride, chlorendic anhydride, etc. The amount of the acid catalyst is preferably 0.5 parts by weight or less, more preferably 0.01-0.5 parts by weight, most preferably 0.015-0.3 parts by weight per 100 parts by weight of the inorganic alkoxide. If the amount of the acid catalyst is less than 0.01 parts by weight, sufficient hydrolysis does not take place. On the other hand, if the amount of the acid catalyst exceeds 0.5 parts by weight, the polycondensation reaction proceeds excessively, making the viscosity of the composition too high. (b) Base catalyst The base catalyst is used mainly for the polycondensation reaction of a hydrolyzate of the inorganic alkoxide, and also for the cross-linking reaction of polyalkylene oxide and for the polycondensation and/or cross-linking reaction of the above hydroxyl group-containing polymer and polyalkylene oxide. Such base catalysts are preferably tertiary amines substantially insoluble in water and soluble in organic solvents. The preferred base catalysts are N,N-dimethylbenzylamine, tripropylamine, tributylamine, tripentylamine, etc., and N-dimethylbenzylamine is particularly preferable. The amount of the base catalyst is preferably 0.01-1 part by weight, particularly 0.05 parts by weight per 100 parts by weight of the total of the above inorganic alkoxide, the above hydroxyl group-containing polymer if any and polyalkylene oxide. If the amount of the base catalyst exceeds 1 part by weight, the polycondensation reaction proceeds excessively, making the resultant polymer less soluble in an organic solvent, resulting in an anti-fogging coat with non-uniformity and decreased strength. [D] Mixture of an organic solvent and water The organic solvents used in the present invention, which should be compatible with water, are methyl alcohol, ethyl alcohol, isopropyl alcohol, butyl alcohol, etc. The organic solvent is used together with water. The amount of the organic solvent is preferably 100-5,000 parts by weight, particularly about 3,000 parts by weight per 100 parts by weight of the total of the above inorganic alkoxide, the above hydroxyl group-containing polymer if any, polyalkylene oxide and the base catalyst. Also, a stoichiometric amount or more of water is added for hydrolysis, preferably water is 15-50 parts by weight per 100 parts by weight of the above inorganic alkoxide. [E] Other components The anti-fogging coating composition of the present invention further contains at least one polyacrylic acid or its derivative. Examples of polyacrylic acid or its derivative include polyacrylic acid, polymethacrylic acid, salts thereof, etc. The amount of polyacrylic acid or its derivative is preferably 0.1-10 parts by weight per 100 parts by weight of the anti-fogging coating composition. If the amount of polyacrylic acid or its derivative is less than 0.1 parts by weight, the coating composition does not have a high water absorption speed. On the other hand, if the amount of polyacrylic acid or its derivative exceeds 10 parts by weight, the anti-fogging coating composition becomes tacky. When the anti-fogging coating composition is applied to lenses, the amount of polyacrylic acid or its derivative is preferably 0.1-0.5 parts by weight per 100 parts by weight of the anti-fogging coating composition. If the amount of polyacrylic acid or its derivative exceeds 0.5 parts by weight, the resultant anti-fogging coat is not likely to have high hardness. [2] Anti-fogging coated article [A] Substrate The substrates used in the present invention may be glass or plastic products such as optical lenses, spectacles, window glasses, plastic films for ink jet printers, etc. [B] Method of production (a) Application of anti-fogging coating composition The above-described components are mixed to prepare an anti-fogging coating composition as a transparent or translucent liquid. The resultant anti-fogging coating composition is applied to at least one surface of the above substrate. The application of the anti-fogging coating composition may be conducted by any know methods such as a spraying method, an immersion method, a brushing method, a roll-coating method, etc. (b) Heat treatment The applied substrate may be dried and heated at a temperature of 80°C or higher, preferably 120-200°C to provide an anti-fogging coated article. If necessary, the heat treatment may be conducted repeatedly after each application cycle of the anti-fogging coating composition. The heat treatment time may be 5 minutes to 1 hour. [C] Anti-fogging coat The thickness of the finished anti-fogging coat is preferably 0.01-1 µm, particularly about 0.1 µm in the case of optical lenses. Further, in the case of window glasses, etc., the thickness of the anti-fogging coat is preferably 1-3 µm, particularly about 1 µm. The thickness of the anti-fogging coat may be properly controlled by increasing the thickness of the anti-fogging coating composition applied or repeating the application of the anti-fogging coating composition. The resultant anti-fogging coat provides anti-fogging and anti-dewing properties to the substrate. The anti-fogging coat is insoluble in water and organic solvents, showing high surface hardness. [D] Mechanism In the anti-fogging coating composition of the present invention, the inorganic alkoxide is hydrolyzed by the function of the acid catalyst so that the alkoxyl groups (OR) and halogen atom (X) are converted to OH groups. Further the base catalyst acts to remove protons from the OH groups, resulting in the polycondensation of a hydrolyzate of the inorganic alkoxide, which in turn produces a polymer or oligomer having OH groups. At the same time, the OH groups of polyalkylene oxide reacts with the hydrolyzate of the inorganic alkoxide and the polymer or oligomer having OH groups by the action of the base catalyst, thereby producing a composite polymer having inorganic portions composed of M in the formula (I) such as Si and organic portions derived from polyalkylene oxide. These hydrolysis and polycondensation reactions partially proceed when each component is mixed. Accordingly, the anti-fogging coating composition is a dispersion of colloidal sol, which is a mixture of the inorganic alkoxide and/or a hydrolyzate thereof, a polymer or oligomer derived from the hydrolyzate by polycondensation, polyalkylene oxide, a polycondensation or cross-linking reaction product of alkoxide hydrolyzate and the polyalkylene oxide. Some functional groups represented by X in the formula (I) may participate in the above reactions. For instance, in case where X is a group containing an epoxy group, the epoxy group is opened by the function of the base catalyst to form an OH group, further proceeding reactions with the inorganic alkoxide and the polyalkylene oxide. In case where X is a group having a vinyl group, the vinyl group may be bonded to reactive monomers. By heat treatment at 80°C or higher after application and drying of the anti-fogging coating composition, the above polycondensation and cross-linking reaction proceed to form a composite polymer with a three-dimensional network structure. The composite polymer has inorganic portions and organic portions. Specifically, because of the inorganic portions which constitute insoluble skeletons, a coat produced from this polymer is insoluble in water and organic solvents, showing high surface hardness. Also, because of the organic portions which are derived from polyalkylene oxide, a coat produced from this polymer has water-absorbing, hydrophilic portions. Further, in case where the X group in the formula (I) has a carbonyl group, a carboxyl group, an amino group, a vinyl group, an epoxy group, etc., water is also attracted to these groups. Because polyacrylic acid or its derivative is contained, the anti-fogging coating composition has improved water-absorbing properties, contributing to further improvement of the anti-fogging properties of the resultant coat. The present invention is described in further detail referring to the following Examples 3 and 4 without intention of restricting the scope of the present invention. The percentages in Examples and Comparative Examples are expressed by weight unless otherwise described. Comparative Example 1 9.74 g of ethylsilicate (Si(OC 2 H 5 ) 4 ) was dissolved in 99.3 ml of methanol, and the resultant solution was mixed with 0.002 mol of hydrochloric acid as a acid catalyst and 2 mol of water per 1 mol of ethylsilicate to cause a hydrolysis reaction at 25°C for 30 minutes . The resultant ethylsilicate hydrolyzate was an oligomer having OH groups at ends. After a solution of 3% (as SiO 2 ) of the ethylsilicate hydrolyzate in methanol was mixed with methanol, N,N-dimethylbenzylamine and a solution of 5% polyethylene oxide having a weight-average molecular weight of 500,000 in methanol were added according to the formulation shown in Table 1. The resultant mixture was stirred at 25°C for 30 minutes to prepare an anti-fogging coating composition solution which was slightly cloudy. Formulation Amount Solution of ethylsilicate hydrolyzate in methanol 90.90 N,N-dimethylbenzylamine 0.01 Solution of 5% polyethylene oxide in methanol 9.09 Total 100.00 The anti-fogging coating composition solution was applied to one surface of a glass plate and heat-dried at 150°C for 10 minutes to provide a transparent coating layer having a thickness of about 0.2 µm. The above steps of application and heat treatment were repeated again in the same manner to form an anti-fogging coating having a thickness of 0.4 µm. The coated glass plate was stored in a refrigerator at about 0°C for 5 minutes, and then left to stand in an atmosphere at a temperature of 25°C and at a relative humidity of 81%. As a result, it was observed that the coated surface of the glass plate was not fogged at all. Comparative Example 1 bis The same test as in Example 1 was repeated except for not forming an anti-fogging coat on a glass plate surface. As a result, it was observed that the surface of the glass plate was fogged immediately, and that fogging did not disappear until it passed 5 minutes. Comparative Example 2 According to the formulation shown in Table 2, a solution of ethylsilicate in methanol (concentration: 28% as SiO 2 ), a solution of aluminum isopropoxide in methanol (concentration: 5% as Al 2 O 3 ), 2N hydrochloric acid, water, and N,N-dimethylbenzylamine were mixed and stirred at 25°C for 15 minutes, and a solution of 5% polyethylene oxide having a weight-average molecular weight of 500,000 in methanol and polypropylene glycol having a weight-average molecular weight of 3,000 were added and stirred at 25°C for 30 minutes. The resultant anti-fogging coating composition solution was transparent. Formulation Amount Solution of ethylsilicate hydrolyzate in methanol 8.90 Solution of aluminum isopropoxide in methanol 0.15 Methanol 74.00 N,N-dimethylbenzylamine 0.01 2N hydrochloride acid 0.22 Water 2.93 Solution of 5% polyethylene oxide in methanol 8.62 polypropylene glycol 5.17 Total 100.00 The anti-fogging coating composition solution was applied to one surface of a glass plate and dried two times in the same manner as in Example 1. The resultant anti-fogging coat was transparent and as thick as 1 µm. The coated glass plate was tested in the same manner as in Example 1. As a result, it was observed that the coated surface of the glass plate was not fogged or dewed at all. Even after further storing it in a refrigerator for 2 hours, fogging and dewing were not observed at all. Example 3 According to the formulation shown in Table 3, a solution of 10% polyethylene oxide having a weight-average molecular weight of 300,000 in methanol was mixed with a solution of 5% polyacrylic acid in methanol, N,N-dimethylbenzylamine and γ-glycidoxypropyltrimethoxysilane and stirred at 25°C for 10 minutes. Thereafter, a solution of a hydrolyzate of aluminum isopropoxide in methanol (concentration: 5% as Al 2 O 3 ) was added and stirred at 25°C for 30 minutes. The resultant anti-fogging coating composition solution was transparent and more viscous than that of Example 1. Formulation Amount Solution of 10% polyethylene oxide in methanol 81.52 Solution of 5% polyacrylic acid in methanol 0.26 N,N-dimethylbenzylamine 0.01 γ-glycidoxypropyltrimethoxysilane 13.59 Solution of aluminum isopropoxide in methanol 4.62 Total 100.00 The anti-fogging coating composition solution was applied to one surface of a glass plate and dried in the same manner as in Example 1. The resultant anti-fogging coat was transparent and as thick as 3.0 µm. The coated glass plate was tested in the same manner as in Example 1. As a result, it was observed that the coated surface of the glass plate was not fogged or dewed at all. After further storing it in a refrigerator for 2 hours, fogging and dewing were not observed at all. The same test as in Example 1 was repeated after drying the tested coated glass plate with a drier. Again, no fogging and dewing were observed at all. The coated glass plate was stored in a refrigerator for 2 hours again to repeat the same test. This time too, no fogging and dewing were observed at all. The coated glass plate was measured with respect to a surface hardness under a load of 500 g according to JIS K 5400. The evaluation of its surface hardness was "H". Example 4 According to the formulation shown in Table 4, an aqueous solution of 25% polyacrylic acid which was 100% neutralized by N,N-dimethylbenzylamine and an aqueous solution of 10% lithium hydroxide was mixed with a solution of 10% polyethylene oxide having a weight-average molecular weight of 500,000 in methanol and stirred at 25°C for 5 minutes. While stirring, a solution of a hydrolyzate of ethylsilicate (concentration: 3% as SiO 2 ) was added little by little and stirred at 25°C for 30 minutes. The resultant anti-fogging coating composition solution was transparent and viscous. Formulation Amount Solution of 10% polyethylene oxide in methanol 71.84 Aqueous solution of 25% polyacrylic acid 5.75 N,N-dimethylbenzylamine 1.28 Aqueous solution of 10% lithium hydroxide 1.97 Solution of ethylsilicate hydrolyzate in methanol 19.16 Total 100.00 The anti-fogging coating composition solution was applied to a polyethylene terephthalate film having a thickness of 100 µm and dried at 150°C for 5 minutes. As a result, a coated film with a transparent anti-fogging coat having a thickness of 10 µm was obtained without any warp. Color printing was conducted by a bubble jet-type ink jet printer (Pixel Jet available from Canon) using the above coated film. The bubble jet ink was well absorbed in the coated film without reverse flow of the ink immediately after the start of printing. No tack was appreciated on a coated surface of the film, and the printed film was free from warp and blurring of color ink dots even after the lapse of time. Since this coated film is insoluble in water and organic solvents and well absorbs printed ink, it is suitable as an OHP film. As described in detail above, the anti-fogging coating composition of the present invention can form an anti-fogging coat which has hydrophilic and water absorption properties and high surface hardness without vulnerability to water and organic solvents on various substrates made of glass, plastics, etc., for instance on optical lenses, spectacles, window glasses for vehicles and films for ink jet printers which need anti-fogging properties and anti-dewing properties. Particularly, by applying the anti-fogging coating composition of the present invention to at least one surface of an OHP film for bubble jet printers to form a high-water absorption coating layer, the OHP film can absorb printed ink rapidly without suffering from reverse flow of ink and warp by the lapse of time, while keeping its surface hardness and insolubility.

Claims: An anti-fogging coating composition comprising: (a) at least one inorganic alkoxide and/or at least one hydroxyl group-containing polymer formed from said inorganic alkoxide(s) by hydrolysis and polycondensation, said inorganic alkoxide being represented by the general formula (I): M(OR) n (X) a-n wherein M is an inorganic element selected from the group consisting of Si, Al, Ti, Zr, Ca, Fe, V, Sn, Li, Be, B and P; R is an alkyl group; X is an alkyl group with at least one functional group selected from the group consisting of a carbonyl group, a carboxyl group, an amino group, a vinyl group and an epoxy group, or a halogen atom; a is a number representing the valence of M; and n is an integer from 1 to a; (b) a polyalkylene oxide; (c) a base catalyst; (d) at least one polyacrylic acid or derivative thereof; and (e) a mixture of a water-compatible organic solvent and water. A composition according to claim 1, wherein said alkoxide is at least one selected from the group consisting of Si(OC 2 H 5 ) 4 , Al(O-iso-C 3 H 7 ) 3 , Ti(O-iso-C 3 H 7 ) 4 , Zr(O-t-C 4 H 9 ) 4 , Zr(O-n-C 4 H 9 ) 4 , Ca(OC 2 H 5 ) 2 , Fe 2 (OC 2 H 5 ) 3 , V(O-iso-C 3 H 7 ) 4 , Sn(O-t-C 4 H 9 ) 4 , Li(OC 2 H 5 ), Be(OC 2 H 5 ) 2 , B (OC 2 H 5 ) 3 , P(OCH 3 ) 3 and P(OC 2 H 5 ) 3 . A composition according to claim 1 or claim 2, wherein said polyalkylene oxide is polyethylene oxide. A composition according to any preceding claim, wherein said base catalyst is a tertiary amine which is substantially insoluble in water and soluble in organic solvents. A composition according to any preceding claim, wherein said base catalyst is N,N-dimethylbenzylamine. A composition according to any preceding claim, further comprising at least one acid catalyst selected from the group consisting of mineral acids, organic acids and anhydrides thereof. A composition according to any preceding claim, wherein said polyacrylic acid or its derivative is at least one selected from the group consisting of polyacrylic acid, polymethacrylic acid and salts thereof. A composition according to any of claims 1 to 5 consisting essentially of: (a) at least one inorganic alkoxide as defined in claim 1: (b) a polyalkylene oxide, the weight ratio of said polyalkylene oxide to said inorganic alkoxide(s) being 100/1-100/150; (c) 0.5 parts by weight or less of at least one acid catalyst per 100 parts by weight of (a); (d) 0.01-1 part by weight of at least one base catalyst per 100 parts by weight of (a) + (b); (e) 0.1-10 parts by weight of at least one polyacrylic acid or derivative thereof per 100 parts by weight of the anti-fogging coating composition; (f) 100-5,000 parts by weight of a water-compatible organic solvent per 100 parts by weight of (a) + (b) + (d); and (g) a stoichiometric amount or more of water for the hydrolysis of said inorganic alkoxide(s). A composition according to any of claims 1 to 5 consisting essentially of: (a) at least one hydroxyl group-containing polymer formed from at least one inorganic alkoxide by hydrolysis and polycondensation, said inorganic alkoxide(s) being as defined in claim 1; (b) a polyalkylene oxide, the weight ratio of said polyalkylene oxide to said hydroxyl group-containing polymer(s) being 100/1-100/150; (c) 0.01-1 part by weight of at least one base catalyst per 100 parts by weight of (a) + (b); (d) 0.1-10 parts by weight of at least one polyacrylic acid or derivative thereof per 100 parts by weight of the anti-fogging coating composition; (e) 100-5,000 parts by weight of a water-compatible organic solvent per 100 parts by weight of (a) + (b) + (c); and (f) a stoichiometric amount or more of water for the hydrolysis of said inorganic alkoxide(s). A composition according to any of claims 1 to 5 consisting essentially of: (a) at least one inorganic alkoxide being as defined in claim 1; (b) at least one hydroxyl group-containing polymer formed from said at least one inorganic alkoxide by hydrolysis and polycondensation; (c) a polyalkylene oxide, the weight ratio of said polyalkylene oxide to said at least one inorganic alkoxide and said at least one hydroxyl group-containing polymer being 100/1-100/150; (d) 0.5 parts by weight or less of at least one acid catalyst per 100 parts by weight of (a); (e) 0.01-1 part by weight of at least one base catalyst per 100 parts by weight of (a) + (b) + (c); (f) 0.1-10 parts by weight of at least one polyacrylic acid or its derivative per 100 parts by weight of said anti-fogging coating composition; (g) 100-5,000 parts by weight of a water-compatible organic solvent per 100 parts by weight of (a) + (b) + (c) + (e) ; and (h) a stoichiometric amount or more of water for the hydrolysis of said at least one inorganic alkoxide. An anti-fogging coated article comprising a substrate and an anti-fogging coat formed on at least one surface of said substrate, said anti-fogging coat being made of an anti-fogging coating composition according to any preceding claim. A coated article according to claim 11, wherein said substrate is made of glass or plastics. A method for producing an anti-fogging coated article according to claim 11, said method comprising the steps of: (i) applying an anti-fogging coating composition according to any of claims 1 to 10 on at least one surface of said substrate; and (ii) subjecting the resultant coated layer to a heat treatment at a temperature of 80°C or higher. A method according to claim 13, wherein said base catalyst functions as a catalyst in the polycondensation of a hydrolyzate of said inorganic alkoxide, in the cross-linking reaction of said polyalkylene oxide, or in the polycondensation and/or cross-linking reaction of said hydrolyzate, said hydroxyl group-containing polymer and said polyalkylene oxide.

Inventors: IKARI HATSUMI, YAMAMOTO TOHRU, YOSHIDA SHIGEO, IKARI, HATSUMI, YAMAMOTO, TOHRU, YOSHIDA, SHIGEO
Applicants: CANON KK, NAKATO LAB INC, CANON KABUSHIKI KAISHA, THE NAKATO LABORATORY, INC.
Application year: 1995
Main classification: C03C17
IPC codes: G02B1, C09D171, B05D7, C03C14, C03C17, C09D185, C09D5, C09K3, C08K5, C09D183, B05D5