Apparatus for continuously dissolving metal powder for use in plating and method of dissolving nickel metal using same

Abstract: An apparatus for continuously dissolving metal powder for use in plating includes a dissolving tank (2) for dissolving metal powder for used in plating solution (7) in a solvent, a filter (3) for separating the solution containing undissolved residue into an undissolved residue and a filtrate, a recovery tank of the filtrate, and a plating solution storing tank for supplying recovered filtrate to a plating tank. The filter is a porous substance having a plurality of liquid passages in the axial direction thereof, and the filter is provided with a circuit for returning a liquid solution containing the undissolved residue passed through the passages to the dissolving tank and a pipeline for leading the filtrate to the recovery tank. A method of dissolving a nickel metal, which has a specific surface of 0.003 m²/g or more, is dissolved with the use of the above-described apparatus.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to an apparatus for manufacturing a plated steel sheet, and more particularly, to an apparatus for continuously dissolving metal powder for use in plating to supply a plating solution continuously to an electrolytic tank used for electroplating a steel sheet, and a method of dissolving metal powder using the apparatus. Description of the Related Art Conventionally, there have been two methods for replenishing metal ions consumed in a plating bath when various types of metals are electroplated on the surface of a metal sheet such as a steel sheet. One is a method in which an anode comprised of a plating metal is immersed into a plating bath, which is an electrolytic tank to dissolve the anode and to replenish the metal ions. The other is a method in which an insoluble anode is immersed into the plating bath, and the metal ions are fed to the plating bath from a dissolving device which is otherwise provided separately. In the former method, however, the anode is consumed by the passage of electric current through the electrolytic tank and the operation of replenishing the metal ions is often interrupted due to an anode exchange operation, thereby causing a number of disadvantages from an operation viewpoint. For this reason, the latter method using the insoluble anode has been a mainstream recently. From JP-A-500 9798 there is known an apparatus for continuously dissolving metal powder comprising two recirculation circuits connecting a tank with a conventional filter element such as a leaf filter which has one feed inlet for a solution containing a undissolved residue and one discharge outlet for a recovered filtrate. Said apparatus comprises two filtering devices, such that when one filter device is out of service while being cleaned, the other filter service will be on duty. In Japanese Unexamined Patent Publication No. 6-41796, there is disclosed an apparatus for continuously dissolving a plating metal (a metal to be plated) which comprises a dissolving tank of the plating metal, a cyclone for separating undissolved residue of the plating metal and a plating solution, a pump and a pipeline, and a technique for increasing a yield of using the plating metal by connecting the dissolving tank and the cyclone with a circuit to circulate the plating solution containing the undissolved residue. In Japanese Unexamined Patent Publication No. 5-33199, there is disclosed a technique for passing the plating solution containing the undissolved residue of the metal powder through a leaf filter having a pre-coated layer formed on the filter fabric thereof by mixing a filter aid into the plating solution so as to improve filtering efficiency. Furthermore, various suggestions concerning a dissolving tank or the like employing a press filter or a centrifugal separator as a filter have been made. However, a technique using a press filter or a leaf filter as the filter has the following problems. A dissolving operation should be paused to discharge the undissolved metal powder deposited on a filter fabric after filtering out of the system. When the undissolved metal powder is disposed of, unit requirement (yield) of the metal powder is deteriorated. In order to reuse the undissolved metal powder, an additional operation is required for recovering and transferring the metal powder to the dissolving tank. On the other hand, a technique using a cyclone or a centrifugal separator as the filter has the following problem. According to this technique, the particle diameter of the metal powder to be collected 100 % is 30 µm or more. Thus, when the metal powder is dissolved to have the particle diameter of 30 µm or less, or when the metal powder having the particle diameter is used for improving the dissolving ability, the undissolved metal powder is mixed into the plating solution to bring about deterioration of quality of the plating unless a secondary filter (leaf filter or the like) is used in combination with the primary filter to separate the plating solution and the undissolved metal powder. Furthermore, when nickel is used as metal powder particularly in zinc-nickel plating, there is a problem that the dissolving rate of the nickel is not necessarily sufficient from a viewpoint of practical use. SUMMARY OF THE INVENTION It is an object of the present invention to provide an apparatus for continuously dissolving the metal powder for use in plating with a high dissolving yield which can avoid the mixing of the metal powder into the plating solution. It is another object of the present invention to provide specific conditions of using the apparatus when nickel is used as the metal powder in zinc-nickel plating. In terms of an apparatus, the above object is achieved by the subject matter of claim 1. Preferred embodiments and further improvements of the inventive apparatus are defined in the depending sub claims. In terms of a method, the above object is achieved by the subject matter of claim 6. Preferred embodiments and further improvements of the inventive method are defined in the depending method sub-claim. According to another aspect of the present invention, there is provided a method of dissolving a nickel metal, wherein nickel metal having a specific surface of 0.003 m 2 /g or more is used as the metal powder and dissolved under the condition of the solvent having a temperature of 75 to 100 °C. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a block diagram showing the entire plating system including an apparatus for dissolving metal powder for use in plating according to the present invention; Fig. 2 is a view showing details of a filter used in the dissolving apparatus according to the present invention; and Fig. 3 is a graph showing the dissolving test results of metal powder by the dissolving apparatus according to the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be specifically described by way of example with reference to the accompanying drawings. Fig. 1 is a block diagram showing the entire plating system including an apparatus for dissolving metal powder for use in plating according to the present invention. The dissolving operation of the metal powder with the dissolving apparatus of the present invention is performed as follows. Referring to Fig. 1, there are shown a dissolving apparatus A, a plating device B and a dissolving device C for dissolving other metal, for example, zinc. On the whole, in this embodiment, nickel is dissolved by the dissolving apparatus A, zinc is dissolved by the dissolving device C and a liquid produced thereby is fed into a plating solution storing device 1 so that the liquid has a predetermined concentration. Further, a predetermined amount of the plating solution having a predetermined concentration is fed to the plating device B. The remaining plating solution is recovered from the plating device B to the plating solution storing tank 1 to be reused. In the apparatus A, metal powder 11 is fed from a hopper 4, storing the powder, to a dissolving tank 2 by a nickel feeding device 16. A metal powder grinding device 17 may be provided upstream of the hopper 4, so that the particle size (specific surface) of the metal is adjusted for accelerating a metal dissolving operation. The metal powder fed to the dissolving tank 2 is dissolved by a plating solution which is otherwise fed separately as a solvent from the plating solution storing tank 1. At this time, the undissolved residual metal powder is passed together with the plating solution 7 through a plurality of passages (lumens) which penetrate through a filter 3 in the axial direction as shown in Fig. 2, and returned again to the dissolving tank 2 by way of a circuit 13. In the meantime, a filtrate (plating solution) 8 filtered by a porous substance of the filter 3 is fed to the plating solution storing tank 1 by way of a pipeline 12 and a filtrate recovery tank 5 (may be omitted). Numerical 9 shows stream of liquid which contains undissolved residue. The amount of plating solution in the dissolving tank 2 is replenished from the plating solution storing tank 1 as to compensate reduced amount of plating solution 8. At this time, a plating solution temperature-rise device 14 may be provided in a flow-back path 18 between the plating solution storing tank 1 and the dissolving tank 2, so as to control the temperature of the plating solution (solvent) to a predetermined temperature by a heater 15 or the like. A temperature 75 to 100°C is preferably used to get a greater dissolving rate. In the system of the present invention, the metal powder 11 is fed from the hopper 4 by way of the nickel feeding device 16 with calculating the amount of reduction of the metal powder using a gravimeter (not shown) provided in the dissolving tank 2. At least one of plating solution densitometers 6, 6' is provided in the plating solution storing tank 1 or the filtrate recovery tank 5. In this embodiment, MILLIPORE CERAFLO (trade name; manufactured by Nippon Millipore Corp.; material: alumina) is used as the filter 3. The specifications of the MILLIPORE CERAFLO including a filtering condition are shown in Table 1. Name MILLIPORE, CERAFLO Material 99.6%, alumina Routine Inner Diameter 2.7mm Number 19 lumen/element Membrane area 0.135m 2 Section area of opening 1.088cm 2 Flow rate 6.5 - 65 liter/min Filtering ability 0.2µm or more Available temperature 0°C - 120°C Allowable pH range 1 - 14 Using the filtering device shown in Table 1, nickel is continuously fed and dissolved with the use of 20 to 50 g/l of zinc ions, 50 to 100 g/l of nickel ions, and sulfuric acid solution of pH 1 to 2 with adjusting a temperature of the solution to 75 to 100 °C, and a feed rate of the plating solution to 100 to 1,000 l/min. Nickel powder for use in plating is used with a feed rate of 1 to 2 kg/min. Approximately 100 % of the metal powder could be recovered with the use of an alumina filter having a filter mesh of 0.2 µm as the filtering device, and no trouble due to the mixing of the metal powder into the plating solution occurred. Since the filter 3 is an alumina ceramic filter, it was not corroded by the plating solution of a high temperature (40 to 100 °C) and low pH (1 to 3) plating solution. When the plating solution is sufficiently stirred by increasing the flow rate of the plating solution circulating in the system, the dissolving tank 2 may be omitted. Next, in order to compare the effect of the apparatus of the present invention in which the ceramic filter is used with that of the conventional apparatuses in which various filters are used, the dissolving and filtering tests were carried out. The results are summarized in Table 2. The yield of the metal powder was 100 % and it is apparent from Table 2 that the results obtained from the apparatus of the present invention are superior to those of the conventional apparatuses. That is to say, when the apparatus of the present invention is used, even the metal powder having the particle diameter of 100 µm, even 30 µm or less can be recovered, thereby increasing the yield of the raw material of the metal powder. In addition, substantially no metal powder is suspended or contained in the plating solution (filtrate), thereby improving the quality of the resultant metal plating. Furthermore, as shown in Fig. 3, the dissolving rate of the metal powder can be increased from the conventional rate of 0.01 kg/min to 0.5 to 2.0 kg/min. Type of filter Metal powder yield (recovery %) Content in filtrate Note Cyclone only 48 52 Poder of particle diameter of 30µm or less not collected Leaf filter only 25 (Melted during depositing on filter fabric) 2 Remaining 73 deposited on filter fabric Cyclone (primary) + Leaf filter (secondary) Cyclone 48 + Leaf filter 12 1 Remaining 39 deposited on fabric of leaf filter Ceramic filter 100 0 As regards the particle size of the metal powder, the following sizes are found to be preferable for sufficiently increasing the dissolving rate: Mean particle diameter is less than 100 µm when the metal powder is spherical in shape; and Mean particle diameter is less than 150 µm when the metal powder is non-spherical in shape. In other words, the specific surface of the metal powder is preferably 0.003 m 2 or more. In order to obtain the above particle size (specific surface), the metal powder may be ground in advance with the grinding device 17. The temperature of the solution may be preferably set to 75 to 100 °C. Conventionally, the plating solution having a temperature of 55 to 65 °C has been used. However, as a result of dissolving experiment using the apparatus of the present invention and nickel powder having the specific surface of 0.003 m 2 /g or less, it is found that the above temperature is required to obtain a sufficient dissolving rate for the nickel-zinc plating. In order to satisfy such temperature condition as described above, FRP (fiber reinforced plastic), titanium or a stainless steel may be preferably used for a material of a dissolving tank in the apparatus of the present invention. In one form of the present invention, there is provided an apparatus for continuously dissolving metal powder for use in plating, comprising: a dissolving tank for dissolving metal powder used in plating solution in a solvent; a filter separating the solution containing the undissolved residue into an undissolved residue and a filtrate; a recovery tank of the filtrate; and a plating solution storing tank for supplying recovered filtrate to a plating tank, wherein the filter is a porous substance having a plurality of liquid passages in the axial direction thereof, and the filter is provided with a circuit for returning a liquid containing the undissolved residue passed through the passages to the dissolving tank and a pipeline for leading the filtrate to the recovery tank. This feature of the invention offers the following advantage. The liquid solution containing the undissolved residue is circulated between the filter and the dissolving tank, and the metal powder is not discharged out of the system. As a result, the metal powder can be dissolved and the yield becomes approximately 100 %. In an another form of the present invention, there is provided an apparatus for continuously dissolving metal powder for use in plating, wherein the porous substance is an alumina ceramic material. This feature of the invention offers the following advantages. Mixing of the undissolved residue into the plating solution can be avoided and the particle diameter of the metal powder can be substantially reduced. Thus, the dissolving rate of the metal powder is increased to perform dissolving operation efficiently. According to the present invention, the dissolving condition of nickel is specifically determined when nickel is used as the metal powder in zinc-nickel plating. Therefore, dissolving of nickel for plating at high speed can be performed at extremely high efficiency. Moreover, according to the present invention, nickel metal is directly dissolved. This is more economical than a case where nickel salt is used. In addition to this, adverse effects of sodium, calcium or the like mixed into the plating solution from metallic salts can be avoided.

Claims: An apparatus for continuously dissolving metal powder comprising: a dissolving tank (2) for dissolving metal powder; a filter (3) separating a filtrate (8) from a solution containing an undissolved residue (7), which is received from said dissolving tank (2), wherein said filter is a porous substance having a plurality of liquid passages (10) in an axial direction thereof, said axially oriented passages (10) being provided for passing through the solution containing said undissolved residue (7), and wherein said filter (3) is connected to a circuit (13) for retuming a solution containing an undissolved residue (9) flowing out from said liquid passages (10) to said dissolving tank (2) and wherein said filtrate (8) is withdrawn through a porous side wall of said filter (3); and further comprising a plating solution storing tank (1) receiving recovered filtrate (8) from said filter - optionally by way of a recovery tank (5) - supplying said recovered filtrate to said dissolving tank (2). An apparatus for continuously dissolving metal powder for use in plating according to claim 1, wherein said porous substance is an alumina ceramic material. An apparatus for continuously dissolving metal powder for use in plating according to claim 1, further comprising: a hopper (4) connected to the dissolving tank (2); and a grinder (17), connected to the hopper, for grinding the metal powder. An apparatus for continuously dissolving metal powder for use in plating according to claim 1, wherein the metal powder is a nickel metal having a specific surface greater than or equal to 0.003m 2 /g, and wherein the solvent has a temperature of 75 to 100°C. An apparatus for continuously dissolving metal powder for use in plating according to claim 1, wherein said filter (3) is provided with a pipeline (12) for transferring the recovered filtrate (8) to the plating solution storage tank (1) by way of a recovery tank (5). A method for continuously dissolving metal powder for use in plating, comprising the steps of: dissolving metal powder in a solvent in a dissolving tank (2); separating a filtrate (8), using a filter (3), from a solution containing an undissolved residue (7) which is received from said dissolving tank, wherein said filter is a porous substance having a plurality of liquid passages (10) in an axial direction thereof, through which the solution containing said residue is flown, whereas said recovered filtrate (8) is withdrawn through a porous side wall of said filter (3); further the step of supplying said recovered filtrate (8) to the plating solution storing tank (1); and further the step of supplying a solution containing an undissolved residue (9) to said dissolving tank (2). A method for continuously dissolving metal powder for use in plating according to claim 6, wherein the recovered filtrate (8) is supplied to the plating solution storing tank (1) by way of a recovery tank (5).

Inventors: IKENAGA TAKAO, KIYAMA SYUJI, MIZUMOTO KAORU, OGAKI HIROSHI, SAKAI NAOKI, SAKURAI AKIO, SEKITA TAKASHI, SHIN OSAMU, TANOKUCHI ICHIRO, IKENAGA, TAKAO, KIYAMA, SYUJI, MIZUMOTO, KAORU, OGAKI, HIROSHI, SAKAI, NAOKI, SAKURAI, AKIO, SEKITA, TAKASHI, SHIN, OSAMU, TANOKUCHI, ICHIRO, IKENAGA, TAKAO, C/O MIZUSHIMA WORKS, KAWASAKI, KIYAMA, SYUJI, C/O MIZUSHIMA WORKS, KAWASAKI, MIZUMOTO, KAORU, C/O MIZUSHIMA WORKS, KAWASAKI, OGAKI, HIROSHI, C/O MIZUSHIMA WORKS, KAWASAKI, SAKAI, NAOKI, C/O MIZUSHIMA WORKS, KAWASAKI, SAKURAI, AKIO, C/O MIZUSHIMA WORKS, KAWASAKI, SEKITA, TAKASHI, C/O MIZUSHIMA WORKS, KAWASAKI, SHIN, OSAMU, C/O MIZUSHIMA WORKS, KAWASAKI, TANOKUCHI, ICHIRO, C/O MIZUSHIMA WORKS, KAWASAKI
Applicants: KAWASAKI STEEL CO, KAWASAKI STEEL CORPORATION
Application year: 1995
Main classification: C25D21
IPC codes: C25D21