Multi-chip module inductor structures

Abstract: In a multichip module structure comprising a silicon, alumina or sapphire substrate carrying a plurality of layers of metallisation separated by polymer dielectric layers, with one or more inductors formed in the uppermost metallisation layer, a ferrite core for one of those inductors is located over the inductor and secured in position by flip chip solder bonding.

Description: There is a growing requirement, in the construction of very compact, low cost radios and other r.f. communications circuits, for small, high performance and cost effective inductor components. Surface mountable chip inductors have recently become available that measure 2mm by 1.25mm in area and that offer inductance values up to some 20 nH, with self resonant frequencies of 1 to 2 Ghz and quality factors that peak at about 80 at about 0.5 of the self resonant frequency. These inductors are lithographically defined and employ a copper metallisation for low resistance and high quality factor. Such components are available at typical costs of 60 cents each, with costs predicted to fall to 30 cents each as production volumes rise. Very compact inductors may also be realised in an intefgrated form within the upper metallisation layers of a multi-chip module type D (MCM-D thin film, deposited) substrate structure. Such inductors can provide inductance values between 1 and 100 nH within a 1mm square footprint (using single or multilayer spiral structures), with self resonant frequencies between 20GHz and 500 MHz. Quality factor in these MCM-D inductors is determined by the inductor resistance at low frequencies, while the peak quality factor is related to the nature and dielectric structure of the substrate employed. High resistivity silicon substrates with inductors defined in an aluminium-polyimide MCM-D structure can provide quality factors between about 5 and 20, depending upon the inductor structure and inductance value. The peak quality factor occurs at a frequency between 0.25 and 0.5 of the self resonant frequency. MCM-D inductors on sapphire or other good dielectric substrates can achieve quality factors up to 30 in the same system, with the peak quality factor occurring at about 0.5 of the self resonant frequency. The effective cost of such MCM-D inductors is directly related to the cost per unit area of the MCM-D technology, which is currently about 20 cents per square mm and will fall to 5 to 10 cents per square mm as production volumes rise. Inductors may also be defined in the related MCM technologies, including MCM-C (cofired or post-fired ceramic) and MCM-L (fine line pcb or laminated) MCM technologies. While these latter MCM technologies involve generally coarser feature sizes and greater layer thicknesses, similar inductive components may be defined. According to this invention, a multichip inductor module comprises a substantially planar substrate, a multilayer metallisation/dielectric structure formed on said substrate, a substantially planar inductor defined in an upper metallisation layer of said multilayer structure, and a substantially planar chip of ferrite material secured to said upper metallisation layer and spaced apart therefrom by flip-chip solder bonds, the ferrite chip being positioned over said inductor in spaced relationship therewith. The present application describes a structure that provides very small, accurate, high value inductor components integrated into an MCM-D substrate structure. These inductors employ a low resistivity metallisation in a linear, arc or planar spiral format (square, circular or polygonal) defined in an MCM-D substrate structure. The MCM-D substrate structure itself involves a multilayer metallisation plus organic polymer dielectric structure with typically a silicon, sapphire or alumina wafer. Copper or aluminium alloy metallisations are commonly employed for low resistivity, with a polyimide, BCB or other thermally stable, low permittivity, interlayer dielectric material. The metallisation layers are commonly allocated to provide a ground plane, a power plane or power distribution layer and one or more signal interconnection layers. Integrated thin film passive components, including resistors, capacitors and inductors may be integrated into such substrate structures. The integrated inductor components are commonly implemented in the upper signal routing metallisation layer(s). A linear, arc or planar spiral inductor geometry may be employed and the power and ground plane layers may be omitted locally to minimise stray capacitance to ground (to maximise self resonant frequency) and to eliminate the image inductance term that can significantly reduce the effective inductance value. The lithographic processes employed to pattern the metallisation layer structures ensure accurate inductance values for these integrated inductors. Single or multilayer inductor structures may be employed, the latter giving higher inductance in a given area. In accordance with the invention a small ferrite chip is flip chip solder bonded over the inductor area on the substrate to provide a local ferrimagnetic "core" for the inductor structure. The addition of this core acts to increase the inductance value for a given inductor design or allow a higher inductor quality factor to be achieved at a given value of inductance at a particular frequency. The structure of this ferrite core MCM-D inductor is illustrated in the accompanying drawing. The choice of ferrite material for the inductor core will depend on the inductor application and, in particular, upon the frequency at which the inductor is to be employed. Such materials are described, for example, in Chapter 4 of "Ceramic Materials for Electronics" edited by R.C. Buchanan, published by Marcel Dekker, Inc. Nickel zinc ferrites and manganese zinc ferrites may be selected for inductor core applications with permeabilities ranging from around 10 to over 1000, with operating frequencies of up to around 500 Mhz. In general the lower permeability materials show greater stability with temperature variation and a wider frequency operating range. The use of the flip chip solder bonding technique for the location of the ferrite core over the MCM-D inductor structure offers a number of advantages. The highly accurate bond geometry and the self aligning nature of the flip chip bond structure, for example, ensures that the ferite chip is consistently located in both the lateral and vertical axes with respect to the inductor structure. This will ensure that the magnification of the inductance value associated with the addition of the flip chip ferrite core is also consistent and accurate. The small, controlled separation of the ferrite core from the MCM-D inductor itself (equal to the flip chip solder bond height and typically in the range from 10 to 100µ) will ensure that minimal stray capacitance is added to the inductor characteristics, whilst achieving effective magnetic coupling. The lateral dimensions of the ferrite chip may be selected to cover the full area of the MCM-D inductor as required, while the ferrite chip thickness may be selected for consistency with the height of other components in the MCM-D assembly, for example to be equal to the thickness of adjacent silicon ICs (typically 0.5mm). Established flip solder bond structures and materials may be employed, for example solder bond lateral dimensions of 10 to 125µm using a Cr-Cu-Au solderable metallisation and a 95Pb-5Sn solder composition (wt%). The flip chip ferrite core concept may be employed to extend the range of inductance values achieveable at a given MCM-D inductor geometry. If a magnification factor of 10 is assumed then, for example, a typical square spiral MCM-D inductor that provides an inductance approaching 25 nH for a 7 turn structure at 60µ spiral pitch, with a quality factor of 9 at 850 MHz, may be extended to give a 250 nH inductor for use at lower frequencies. Alternatively the 7 turn, 25 nH inductor may be replaced by a 2 turn inductor at the same pitch, given a ferrite material that has suitable characteristics at 850 Mhz. This inductor, having a significantly reduced series resistance, will also display an increase in quality factor. This general flip chip ferrite core concept may also be applied to other related MCM-D and ferrite structures where magnetic coupling effects may be exploited, for example in transformers, couplers and circulators.

Claims: A multichip module inductor structure comprising a substantially planar substrate, a multilayer metallisation/dielectric structure formed on said substrate, a substantially planar inductor defined in an upper metallisation layer of said multilayer structure, and a substantially planar chip of ferrite material secured to said upper metallisation layer and spaced apart therefrom by flip-chip solder bonds, the ferrite chip being positioned over said inductor in spaced relationship therewith. A multichip module inductor structure in accordance with Claim 1 wherein the ferrite material is a nickel zinc ferrite or a manganese zinc ferrite. A multichip module inductor structure in accordance with any preceding claim wherein a solder bond metallisation is of chromium-copper-gold and the solder composition is 95% lead 5% tin by weight.. A multichip module inductor structure in accordance with any preceding claim wherein the inductor is defined in two or more metallisation layers separated by dielectric layers and interconnected by interlayer vias.

Inventors: PEDDER DAVID JOHN, PEDDER, DAVID JOHN
Applicants: INTARSIA CORP, INTARSIA CORPORATION
Application year: 1995
Main classification: H01F17
IPC codes: H01F17