Composition for invisible ink responsive to infrared light

Abstract: An invisible ink has been discovered that utilizes an invisible or almost invisible substituted phthalocyanine dye in combination with selected waxes and resins. The resulting ink is one that has use in thermal printing and is transparent or almost transparent in white light, but is responsive to infra-red light in the range of 720 to 1000 nm. The preferred waxes are polyethylene wax, natural paraffin wax and carnauba wax, and the preferred resin is ethyl vinyl acetate polymer.

Description: One of the by-products of the business climate being driven by technological advances is the need of greater security. This is particularly true of documents that are issued by governments, financial institutions, brokerage houses and the like. One scheme that has been proposed for providing security is to print authenticating text in invisible ink so that the same does not interfere with the document upon which such text is printed, but one, nevertheless, is able to determine the authenticity of the document and the holder of the document as well. An example is described in copending European patent application publication No. 626660 in which a scheme is described for placing a transparent label over a document with text printed on the label in invisible ink so that text covered by the label can be read. By invisible ink is meant an ink that is either not visible to the naked eye or is transparent so that one is able to distinguish anything covered by the invisible ink. In addition, the invisible ink also must be responsive to light of a particular frequency range, such as light in the infra-red range. Although there are a number of invisible inks that are commercially available, most of these inks are responsive to ultraviolet light. Although such inks are useful, having an invisible ink that is responsive to infra-red light is more advantageous as devices for reading in the infra-red range are more reliable and inexpensive. Recently, Zeneca Ltd. has developed suitable dyes that are sufficiently responsive to infra-red light. These dyes, with appropriate solvents and other components, have been used to formulate inks that have use in the ink jet printing field. Although the inks developed by Zeneca Ltd. answered a long sought need, these inks are not suitable for use in thermal printers. Thermal printers are high quality, low cost, low speed printers that use a ribbon in the form of a film which is sensitive to heat for transferring ink to a contacting surface. They are capable of printing on difficult to print surfaces such as plastics or other non-porous surfaces, because it is a non-impact contact type of printing. Clearly, it would be advantageous to have an invisible ink responsive to light in the infra-red range that can be applied by thermal printing. JP-A-2 209 975 discloses an ink composition including phthalocyanine dyes capable of absorbing light in the near infrared. The ink composition may be in the form of a heat transfer recording medium which contains a thermally soluble binder such as carnauba wax and a softening agent such as petroleum resin. EP-A-0 420 613 discloses ink compositions which may be suitable for thermal transfer and which are readable with a light source having a wavelength of 600-700 nm. The ink is prepared using a wax such as natural wax, carnauba wax, paraffin wax or microcrystalline wax in combination with a thermoplastic resin such as ethylene-vinyl acetate copolymer. The dye present in the ink may be a halogenated copper phthalocyanine which has substantial absorption at 600-700 nm. Accordingly, the present invention provides a thermal transfer ink composition that is transparent or nearly transparent to visible light having a wavelength between 400 and 700 nm and which comprises: a) 0.5 to 5% by wt. of one or more phthalocyanine dyes substituted by amine groups, hydroxyl groups, alkoxy groups or thiol groups and which absorb(s) light between 700 nm and 1200 nm and is (are) invisible or almost invisible to the naked eye; b) 60-80% by wt. of one or more of a polyethylene wax, c) 4 to 15% by wt. of a urethane derivative of an oxidized synthetic wax; d) 4 to 15% by wt. of carnauba wax; and e) 10 to 20% by wt. of ethyl vinyl acetate polymer; wherein percentages by wt. are based upon the total weight of the composition. Preferably, the composition comprises 4-10% by wt. of carnauba wax. The basic wax vehicle (polyethylene wax) may be varied to contain natural paraffin wax or microcrystalline wax. Preferably, the one or more phthalocyanine dyes have the formula: wherein Nu represent amine groups, hydroxyl groups, alkoxy groups or thiol groups, and M is Cu, Fe or Mn. The aforementioned ink composition may be utilized to provide document security by printing authenticating text in the above invisible ink so that the invisible ink does not interfere with the document upon which such text is printed. The use of several invisible infrared phthalocyanine dyes gives an additional security advantage. For example, a combination of three phthalocyanine dyes with absorption wavelengths of 780, 830 and 900 nm as shown in the graph depicted in FIG. 2 can be used for enhanced security. The reason for this is that the ratio of different dyes that comprise the invisible ink may be varied so that scanners with specific sensitivities will detect the various ratios of the dyes. It has been found that the invisible ink composition of the instant invention has advantages as an ink for use in a heat sensitive ribbon of a thermal printer. After being applied to a surface by the thermal printing process, the ink is responsive to light in the infra-red range of 700 to 1200 nm, preferably 720 to 1000 nm, so as to be invisible to the unaided eye but detectable by a sensor. These are particularly attractive ranges, as sensors are more capable of detecting light in these two ranges. In addition, because of the double response, the invisible ink is more readily readable and detectable. In the accompanying drawings:- FIG. 1 is a graph depicting the frequency ranges in which the inventive ink is responsive; and FIG. 2 is a graph that illustrates the manner in which a visible phthalocyanine pigment is transformed by a nucleophilic substituent into a soluble dye with very strong infrared absorption. It is known that using an invisible substituted phthalocyanine dye as a part of a dye complex in an ink will render the ink made therefrom invisible to ambient light, but responsive to light in the infra-red range. It has been discovered that the combination of such dyes along with selected waxes and resins yield an invisible ink having particular utility for use in a thermal printer. Preferably, the wax portion of the ink will have a composition of 60-80% polyethylene wax. 4-15% urethane derivative of oxidized synthetic wax, and 4-10% carnauba wax. Other waxes that can be used are natural paraffin and microcrystalline waxes. The waxes and dye are combined with an ethyl vinyl acetate (EVA) polymer. The substituted phthalocyanine dye will make up 0.5-5% of the composition and the EVA resin 10-20%. All percentages in this disclosure and accompanying claims are in weight percent. The resulting ink is one that is transparent in the visible region with a slight greenish tinge, but when exposed to infra-red light, can absorb the light between 700-1200 nm, as seen in FIG 1. When donor groups such as amine (NR 2 ), hydroxyl (OH), alkoxy (OR) or thiol (SR) are added to phthalocyanine pigments, a bathocromic shift from red to infra-red occurs in a narrow band at 800 nm or a broad band between 750 nm and 1200 nm as seen in FIG. 2. FIG. 2 represents absorption specific spectra of three different insoluble IR absorbers. As it can be seen in FIG. 2, the absorption varies from 700 to 1,200 nm. The IR absorbers are Pro-Jet 780 NP, Pro-Jet 860 NT, and Pro-Jet 900 NP. The Pro-Jet 900 absorption is approximately 900 nm, and the Pro-Jet 860 NT absorption is approximately 860 nm. The Pro-Jet 780 absorption is approximately 780 nm. The aforementioned Pro-Jet absorbers are manufactured by Zeneca Specialties, P.T. Box 42, Hexagon House, Blackley, Manchester M9 8ZS, ENGLAND. The original colored pigment is transformed by the aforementioned substitution into an invisible infrared absorbing solution dye. The resulting dye has high light fastness and high extinction coefficients at the specific near IR wavelength. The substituted phthalocyanine dyes of the instant invention may be prepared as follows: wherein M is a metal such as Cu, Fe and Mn, and Nu are functional groups substituted by the nucleophilic reaction of the original phthalocyanine molecule with amine groups (NR 2 ), hydroxyl groups (OH), alcoxy groups (OR) or thiol groups (SR) as donor groups. Although there is a slight green tinge at ambient, the ink is sufficiently transparent so that when the invisible ink is placed upon a transparent label, any markings below the transparent label will be readily visible to the naked eye. Commercially available scanners have been found quite capable of detecting and reading the invisible ink of the instant invention. A primary advantage of the instant invisible ink is that the same can be used in a thermal transfer ribbon for use in the thermal transfer printing process. A preferred composition of the inventive ink is as follows. General Composition Ingredients Commercial Source Weight % 1. I.R. Dye substituted phthalocyanine dye Zeneca Ltd. 0.5 to 5% 2. Polyethylene wax average molecular weight 300 to 800 Petrolite Corp. 60 to 80% 3. urethane derivative of oxidized, synthetic wax Bareco Div., Petrolite 4 to 15% 4. carnauba wax Stahl & Petsch Inc. 4 to 10% 5. Ethyl vinyl acetate polymer Dupont Co. 10 to 20% The basic polyethylene wax vehicle can be varied to contain waxes such as natural paraffin waxes, microcrystalline waxes, and synthetic waxes, but the general composition must always include the phthalocyanine dye, the ethyl vinyl acetate polymer carnauba wax and urethane derivative of oxidized synthetic wax. An example of an ink that has been formulated in accordance with the invention is as follows: Example Ingredient Manufacturer (Trade Name) WT (gms) Diphthalo substituted soluble phthalocyanine Zeneca Ltd. 5.00 Polyethylene wax-molecular weight 500, melting (Polywax 500) point 88°C urethane derivative of Petrolite (WB-17) 64.1 synthetic wax Bareco Div.,Petrolite 7.2 carnauba wax Strahl & Patsch Inc. 8.2 Ethyl Vinyl Acetate Polymer Dupont 15.5 Ink properties Viscosity at 100C ∼90cps Melting point 65°C Max. Absorbance 880-900 nm The ink was applied to a polyethylene tetraphthalate film with the results discussed below. The inks according to preferred embodiments of the invention exhibit good adhesion to a thermal ribbon film and to a non-porous surface, such as plastic, when applied thereto in a thermal printing operation. These inks have the characteristics of a low melting point which results in good transferability, good flexibility for non-flaking, high hardness that yields high mechanical abrasion resistance and prevents smudging of the final print, water fastness and high light fastness and contrast properties. The inks were found to have good slip and are free of blocking characteristics. Thus what has been shown and described is an invisible ink that has advantages in that it is sensitive to the infra-red and can be used in a thermal transfer ribbon.

Claims: A thermal transfer ink composition that is transparent or nearly transparent to visible light having a wavelength between 400 and 700 nm and which comprises: (a) 0.5 to 5% by wt of one or more phthalocyanine dyes substituted by amine groups, hydroxyl groups, alkoxy groups or thiol groups and which absorb(s) light between 700 nm and 1200 nm and is (are) invisible or almost invisible to the naked eye; (b) 60 to 80% by wt of a polyethylene wax; (c) 4 to 15% by wt of a urethane derivative of an oxidized synthetic wax; (d) 4 to 15% by wt of carnauba wax; and (e) 10 to 20% by wt of ethyl vinyl acetate polymer; wherein percentages by wt are based upon the total weight of the composition. A thermal transfer ink composition according to claim 1, comprising 4 to 10% by wt of carnauba wax. A thermal transfer ink composition according to claim 1 or claim 2, wherein the one or more phthalocyanine dyes have the formula: wherein Nu represents amine groups, hydroxyl groups, alkoxy groups or thiol groups, and M is Cu, Fe or Mn. A thermal transfer ink composition according to claim 1, wherein the basic wax vehicle (polyethylene wax) is varied to contain natural paraffin wax or microcrystalline wax.

Inventors: AUSLANDER JUDITH D, AUSLANDER, JUDITH D.
Applicants: PITNEY BOWES INC, PITNEY BOWES INC.
Application year: 1995
Main classification: C09D11
IPC codes: C09D11