Flame-retardant resin composition

Abstract: A flame-retardant (C) of an aromatic phosphoric acid ester of the following formula (I) (5 to 50 parts by weight) and a fluororesin (D) such as a powdery polytetrafluoroethylene (0.05 to 5 parts by weight) are added to 100 parts by weight of a mixture of thermoplastic resins comprising 50 to 95% by weight of an aromatic polycarbonate (A) and 5 to 50% by weight of a styrenic resin (B) comprising at least a rubber-modified styrenic resin: wherein (i) at least one of R¹ to R⁴ is a 2,3-dialkylphenyl group, a 3,4-dialkylphenyl group or a 3,5-dialkylphenyl group each substituted with alkyl groups each having 1 to 3 carbon atoms, A is a phenylene group, n denotes an integer of 0 to 5, and R¹ to R⁴ contain the dialkylphenyl group and a monoalkylphenyl group in a ratio of the former/the latter is 50/50 to 90/10 (% by weight); or (ii) at least one of R¹ to R⁴ is a phenyl group substituted with 1 to 5 alkyl groups each having 1 to 4 carbon atoms, A is 1,3-phenylene group and n denotes an integer of 1 to 5. The flame-retardant (C) may be a mixture of the compound (i) and the compound (ii).

Description: FIELD OF THE INVENTION The present invention relates to a polycarbonate-containing flame-retardant resin composition which is excellent in molding processability (moldability) such as melt fluidity. BACKGROUND OF THE INVENTION A mixture of a polycarbonate and a styrenic resin such as ABS resin, SAN resin and so forth has high heat resistance and impact resistance, so that it is generally used, as a polymer alloy, for various shaped or molded articles such as parts for an automobile, an electric product, an electronic product and the like. When the polymer alloy is employed for a housing, an enclosure, a chassis or the like of electric or electronic parts or office automation (OA) apparatuses or instruments, flame-retardancy or fire-resistance is required of such polymer alloy. In particular, for increasing the safety of a product, a standard qualification of V-O or 5V is frequently required of a shaped article of an OA apparatus or a home electric product recently. While the V-O or 5V standard is the highest flame-retardancy level according to the Subject 94 of Underwriter's Laboratory Co., Ltd. (hereinafter briefly referred to as UL) as the flame-retardancy standard in U.S.A. On the other hand, in order to decrease the using amount of a material, not only miniaturization but also thinning of the part or the housing is useful. Such part or housing has, however, a risk of a fire drip arising from the thinned part of the shaped article accompanied with burning (combustion), and thus spreading fire to another inflammable or combustible substance. Accordingly, a flame-retardant resin composition is also required for such a higher flame resistance or flame-retardancy as not to cause a flame drip. For imparting the flame-retardancy, a halogen-containing flame-retardant is usually added to a polymer alloy comprising a polycarbonate and a styrenic resin. As the halogen-containing flame-retardant, there may frequently be employed a combination of a bromine-containing flame-retardant exemplified as tetrabromobisphenol A or its oligomer, a brominated epoxy oligomer, and a flame-retarding-auxiliary comprising, as a main component, a metallic oxide exemplified as antimony trioxide. It is, however, pointed out by an organization for environmental protection in Europe that, among such bromine-containing flame-retardants, use of decabromodiphenyl ether (DBDPE) or octabromodiphenyl ether (OBDPE) has a possibility of generating toxic dibenzodioxin with burning of the resin composition. Therefore, a non-halogen-containing flame-retardant is useful for flame-retarding (flameproofing) of a resin. As the non-halogen-containing flame-retardant, a phosphorus-containing flame-retardant, specifically a flame-retardant comprising an aromatic phosphoric acid ester is employed. For example, U.S. Patent No. 5,061,745 corresponding to Japanese Patent Application Laid-open No. 32154/1990 (JP-A-2-32154) discloses the use of a flame-retardant comprising a monomeric phosphoric acid ester in combination with polytetrafluoroethylene as a flame-retarding-auxiliary. U.S. Patent No. 5,204,394 discloses an addition of an oligomeric phosphoric acid ester to a mixture of a polycarbonate and a styrenic resin. Further, U.S. Patent No. 5,122,556 discloses the use of a polycarbonate and a flame-retardant of a dimeric phosphoric acid ester. Moreover, an addition of such flame-retardant comprising a phosphoric acid ester to a polymer alloy comprising a polycarbonate and a styrenic resin is also disclosed in Japanese Patent Application Laid-open Nos. 62556/1986 (JP-A-61-62556), 4746/1987 (JP-A-62-4746), 115262/1990 (JP-A-2-115262), 298554/1992 (JP-A-4-298554), 179123/1993 (JP-A-5-179123), 262940/1993 (JP-A-5-262940), 279531/1993 (JP-A-5-279531) and so on. Use of these flame-retardants comprising an aromatic substituted or non-substituted phosphoric acid ester can impart flame-retardancy and impact resistance suitably to a polymer alloy comprising a polycarbonate and a styrenic resin. Therefore, some of such resin composition as a molding material for a home electric apparatus or an OA apparatus has been commercially implemented. The polymer alloy comprising the non-halogen-containing flame-retardant has, however, frequently poor melt fluidity during the molding process. Accordingly, a shaped article or molded article requiring not only miniaturization but also lightening and thinning can hardly be produced with high efficiency, by imparting high fluidity (flowability) to the polymer alloy. Further, the polymer alloy is liable to be attached to a mold of the molding machine and thus a frequent cleaning of the mold is required, or deterioration or degradation by residence of the resin by, for example, heat or thermal degradation of the flame-retardant is apt to occur during the molding process. Furthermore, even if using a polymer alloy having comparatively high melt fluidity, the resultant molded article may have poor light resistance (light stability) and is liable to be discolored. The heat resistance, impact resistance, mechanical strength and the like of the molded article is likely to be decreased with increasing or enhancing the melt fluidity. For instance, the heat resistance and flame-retardancy of the shaped article is'liable to be decreased with an increased ratio of the styrenic resin relative to the polycarbonate, although the melt fluidity is enhanced. Accordingly, the light resistance, heat resistance and impact resistance and the mechanical strength of the molded article can hardly be increased with maintaining high melt fluidity. SUMMARY OF THE INVENTION Thus, it is an object of the present invention to provide a flame-retardant resin composition, whereby high flame-retardancy can be imparted to a molded article, and which has high melt fluidity. It is another object of the invention to provide a flame-retardant resin composition whereby even a molded article having a thin portion can be molded with high accuracy. A still another object of the present invention is to provide, in a polymer alloy system comprising a polycarbonate and a styrenic resin, a resin composition wherein flame drip during burning can be inhibited or suppressed and which has high flame-retardancy or flame resistance. A further object of the invention is to provide a flame-retardant resin composition which is useful for obtaining a shaped article excellent in the flame-retardancy, the heat resistance, the impact resistance and the mechanical strength. It is yet another object of the present invention to provide a flame-retardant resin composition which has high melt fluidity and is useful for obtaining a molded article having not only high flame-retardancy but also excellent light resistance. A yet another object of the present invention is to provide a flame-retardant resin composition which is useful for obtaining a shaped article excellent in flame-retardancy, light resistance, heat resistance, impact resistance and mechanical strength. The present inventor made intensive investigations to achieve the above objects and, as a result, found that when an aromatic phosphoric acid ester wherein an alkyl group is substituted on a specific position of the phenyl group is used as a non-halogen-containing flame-retardant, not only the flame-retardancy but also the melt fluidity can be improved and thus a shaped article (molded article) can be molded in high accuracy. Further, he found that by using a specific nucleus-substituted aromatic phosphoric acid ester having 1,3-phenylene group as the non-halogen-containing flame-retardant, a resin composition having high melt fluidity can be obtained, and whereby a shaped article having high flame-retardancy and further high light resistance can be obtained in high accuracy. The present invention has been accomplished based on these findings. Accordingly, the flame-retardant resin composition of the present invention comprises (A) an aromatic polycarbonate (B) a styrenic resin (C) an aromatic phosphoric acid ester of formula (I) wherein A is 1,3-phenylene, n is an integer of 1-5, and R 1 , R 2 , R 3 and R 4 independently represent phenyl, optionally substituted with C 1-4 -alkyl; at least one of R 1 to R 4 is a 2,6-di-(C 1-3 -alkyl)phenyl group; and (D) a fluororesin. In the compound of the formula (I), the alkyl group may be a methyl group or an ethyl group. In such case, at least one of R 1 R 2 , R 3 and R 4 may be a phenyl group substituted with 2 alkyl groups each having 1 to 3 carbon atoms, and n may be an integer of 1 to 3. The styrenic resin (B) includes, for example, a non-rubber-modified styrenic resin such as SAN resin (AS resin), and a rubber-modified styrenic resin such as ABS resin. The fluororesin (D) such as a polytetrafluoroethylene may usually be employed in a powdery or granular form. DETAILED DESCRIPTION OF THE INVENTION [Aromatic polycarbonate (A)] The aromatic polycarbonate (A) includes various polymers, for example a polycarbonate obtainable by a reaction of a dihydric phenol compound and phosgene (phosgene method), or by a reaction of a dihydric phenol compound and a carbonic diester (transesterification method). As examples of the dihydric phenol compound, there may be mentioned an optionally substituted bis(hydroxyaryl)alkane such as bis(4-hydroxyphenyl)methane, 1,1-bis(4-hydroxyphenyl)ethane, 2,2-bis(4-hydroxyphenyl)propane, 1,1-bis(4-hydroxyphenyl)butane, nyl)butane, 1,1-bis(4-hydroxyphenyl)isobutane, 2,2-bis (4-hydroxyphenyl) butane,- 2,2-bis(4-hydroxy-3-methylphenyl)propane, 2,2-bis(4-hydroxy-3-t-butylphenyl) propane, 2,2-bis(3,5-dimethyl-4-hydroxyphenyl)propane, 2,2-bis(4-hydroxy-3-cyclohexylphenyl)propane and 2,2-bis(4-hydroxy-3-methoxyphenyl)propane; an optionally substituted bis(hydroxyaryl)cycloalkane such as 1,1-bis(4-hydroxyphenyl)cyclopentane, 1,1-bis(4-hydroxyphenyl)cyclohexane, 1,1-bis(4-hydroxyphenyl)cyclohexane, and others; a dihydroxyaryl ether such as 4,4'-dihydroxyphenyl ether and 4,4'-dihydroxy-3,3'-dimethylphenyl ether; a dihydroxydiaryl sulfide such as 4,4'-dihydroxydiphenyl sulfide and 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfide; a dihydroxydiaryl sulfoxide such as 4,4'-dihydroxydiphenyl sulfoxide and 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfoxide; a dihydroxydiaryl sulfone such as 4,4'-dihydroxydiphenyl sulfone and 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfone; a dihydroxydiaryl ketone such as bis(4-hydroxyphenyl) ketone and bis(4-hydroxy-3-methylphenyl) ketone; 1,4-bis(4-hydroxyphenylsulfonyl)benzene, 4,4'-bis(4-hydroxyphenylsulfonyl)benzene, 1,2-bis(4-hydroxyphenoxy)ethane, phenolphthalein and others. These dihydric phenol compounds can be used singly or in combination. Preferred examples of the dihydric phenol compound include a bisphenol whereby an aromatic polycarbonate having high heat resistance can be obtained. As such bisphenol, there may be mentioned, for instance, a bis(hydroxyphenyl)alkane such as 2,2-bis(4-hydroxyphenyl)propane, a bis(hydroxyphenyl)cycloalkane such as bis(4-hydroxyphenyl)cyclohexane, a dihydroxydiphenyl sulfide, a dihydroxydiphenyl sulfone, a dihydroxydiphenyl ketone and so on. Typically preferred dihydric phenol compound includes, for example, 2,2-bis(4-hydroxyphenyl;propane (namely, bisphenol A) with which a bisphenol A type aromatic polycarbonate can be formed. In the preparation of the bisphenol A type aromatic polycarbonate, a part of bisphenol A can be replaced by another dihydric phenol compound insofar as the heat resistance, mechanical strength and the like are not adversely affected. The molecular weight of the polycarbonate is, for example, as a viscosity-average molecular weight measured at 20°C by using methylene chloride, about 15,000 to 50,000, preferably about 18,000 to 40,000 and more preferably about 20,000 to 30,000. When the molecular weight is less than 15,000, the impact resistance of the shaped article is liable to be decreased, and when it exceeds 50,000, the fluidity (flowability) is apt to be decreased. The limiting-viscosity of the polycarbonate is, for instance, about 0.3 to 0.7 dl/g, and preferably about 0.3 to 0.65 dl/g in methylene chloride at 20°C. [Styrenic resin (B)] The styrenic resin (B) includes a non-rubber-modified styrenic resin (B1) which does not include a rubber component and a rubber-modified styrenic resin (B2). The rubber-modified styrenic resin (B2) may be a mixed composition (B2a) of a rubber component and a styrenic resin, or a grafted polymer (B2b) obtainable by graft-polymerizing a styrenic monomer or a mixture of vinyl monomer comprising a styrenic monomer and non-styrenic vinyl monomer to a rubber component (B21). The non-rubber-modified styrenic resin (B1) include a homo- or co-polymer of an aromatic vinyl monomer (B1a) and a copolymer obtainable by polymerizing an aromatic vinyl monomer (B1a) and a copolymerizable non-styrenic vinyl monomer. As examples of the aromatic vinyl monomer (B1a), there may be mentioned a styrenic monomer such as styrene, an alkyl-substituted styrene (for instance, o-methylstyrene, p-methylstyrene, m-methylstyrene, 2,4-dimethylstyrene, p-ethylstyrene, p-t-butylstyrene and the like), an α-alkyl-substituted styrene (e.g. α-methylstyrene, α-methyl-p-methylstyrene, etc.) a halogenated styrene (for instance, o-chlorostyrene, p-chlorostyrene, etc.) and others. Preferred examples of the aromatic vinyl monomer include styrene, p-methylstyrene and α-methylstyrene, particularly, styrene and α-methylstyrene. These aromatic vinyl monomers can be employed singly or in combination. The non-styrenic vinyl monomer includes a copolymerizable vinyl monomer such as vinyl cyanide monomer (B1b) (for example, acrylonitrile, methacrylonitrile), other copolymerizable vinyl monomer (B1c) [e.g. a (meth)acrylic monomer (for instance, a (meth)acrylic acid ester or (meth)acrylic ester of an alkyl having about 1 to 10 carbon atoms such as methyl methacrylate, ethyl acrylate and butyl acrylate, a (meth)acrylic ester having a functional group such as 2-hydroxyethyl methacrylate and 2-hydroxypropyl methacrylate, (meth)acrylic acid and the like), maleic anhydride, N-substituted maleimide and so on]. Preferred examples of the non-styrenic monomer include (meth)acrylonitrile, (meth)acrylic monomer (e.g., (meth)acrylic acid ester of an alkyl having about 1 to 4 carbon atoms such as methyl methacrylate), maleic anhydride, N-substituted maleimide and others, specifically acrylonitrile, an alkyl (meth)acrylate such as methyl methacrylate and so on. Such non-styrenic monomers can also be employed singly or in combination. The styrenic resin (B1) may, for example, be a homo- or co-polymer of an aromatic vinyl monomer (e.g. polystyrene), or may frequently be (1) a copolymer obtainable by polymerizing the styrenic monomer (B1a) and the vinyl cyanide monomer (B1b) such as acrylonitrile [for example, an acrylonitrile-styrene copolymer (hereinafter briefly referred to as SAN resin) and others], (2) a copolymer obtainable by polymerizing the styrenic monomer (B1a) and the alkyl (meth)acrylate (B1c) (for instance, a styrene-methyl methacrylate copolymer and so on), (3) a copolymer obtainable by polymerizing the styrenic monomer (B1a), the vinyl cyanide monomer (B1b) and the copolymerizable vinyl monomer (B1c) such as an alkyl (meth)acrylate (e.g. a styrene-acrylonitrile-methyl methacrylate copolymer, etc.), (4) a styrene-maleic anhydride copolymer, a styrene-N-substituted maleimide copolymer and others. As the preferred styrenic resin (B1), there may be mentioned, for instance, SAN resin, a styrene-acrylonitrile-(meth)acrylic acid alkyl ester copolymer and so on. The non-rubber-modified styrenic resin (B1) can be used singly or in combination. The proportion of each monomer for preparing the copolymer may be selected from a range as far as the melt fluidity, the heat resistance and impact resistance of the molded article are not impaired, and is, for example, about 50 to 90% by weight (preferably about 55 to 85% by weight and more preferably about 60 to 80% by weight) of the aromatic vinyl monomer (B1a), about 10 to 40% by weight (preferably about 15 to 35% by weight and more preferably about 20 to 30% by weight) of the vinyl cyanide monomer (B1b), and about 0 to 40% by weight (preferably about 0 to 30% by weight and more preferably about 0 to 20% by weight) of the copolymerizable vinyl monomer (B1c) such as a (meth)acrylic monomer. Use of the aromatic vinyl monomer (B1a) in an amount of less than 50% by weight may possibly cause coloring or deterioration (degradation) of.the molded article, and use in a proportion of more than 90% by weight is liable to decrease the beat resistance and the chemical resistance of the shaped article. Further, when the vinyl cyanide (B1b) is used in a proportion of less than 10% by weight, the chemical resistance of the shaped article is apt to be decreased or reduced, while when it exceeds 40% by weight, the heat stability of the shaped article is likely to be reduced. Moreover, use of the copolymerizable vinyl monomer (B1c) such as a (meth)acrylic monomer in an amount of more than 40% by weight may occasionally decrease the melt fluidity or the properties or characteristics of the shaped article. As the rubber component in the rubber-modified styrenic resin (B2), there may be mentioned, for example, a non-styrenic rubber-like polymer containing no styrene unit such as a polybutadiene rubber, a butadiene-isoprene rubber, a butadiene-acrylonitrile copolymer, an ethylene-propylene rubber, an EPDM rubber (an ethylene-propylene-nonconjugate diene rubber), a polyisoprene rubber, a polychloroprene rubber, an acrylic rubber and an ethylene-vinyl acetate copolymer; a styrenic rubber-like polymer containing a styrene unit such as a styrene-butadiene copolymer and a styrene-butadiene block copolymer. These rubber-like polymer can be employed singly or in combination. Preferred examples of the rubber component include a polybutadiene, a butadiene-acrylonitrile copolymer, an ethylene-propylene rubber, an EPDM rubber, an acrylic rubber, a styrene-butadiene copolymer and a styrene-butadiene block copolymer. A polymer containing a butadiene unit (for instance, a polybutadiene, a styrene-butadiene copolymer) may frequently be used as the rubber component. The glass-transition temperature Tg of the rubber component is not higher than about 0°C, preferably about -150°C to 0°C, and more preferably about -100°C to -10°C. Where the glass-transition temperature of the rubber component exceeds 0°C, the impact strength of the shaped article (molded article) is liable to be decreased or impaired. The rubber-modified styrenic resin may comprise a mixture of the rubber component and the styrenic resin, or may preferably be a high impact resistant styrenic resin obtainable by graft-polymerizing at least a styrenic monomer to a rubber component. As examples of the rubber-modified styrenic resin, there may be mentioned a high impact resistant polystyrene (HIPS) obtainable by polymerizing styrene to a polybutadiene, ABS resin obtainable by polymerizing acrylonitrile and styrene to a polybutadiene, AAS resin obtainable by polymerizing acrylonitrile and styrene to a acrylic rubber, ACS resin obtainable by polymerizing acrylonitrile and styrene to a chlorinated polyethylene, AES resin obtainable by polymerizing acrylonitrile and styrene to an ethylene-propylene rubber (or EPDM rubber), a terpolymer obtainable by polymerizing acrylonitrile and styrene to an ethylene-vinyl acetate copolymer, MBS resin obtainable by polymerizing methyl methacrylate and styrene to a polybutadiene and so on. These rubber-modified styrenic resins can be employed singly or as a mixture of two or more species. In the rubber-modified styrenic resin (B2), the components other than the rubber component and the proportions thereof are frequently in common with those of the non-rubber-modified styrenic resin. The ratio of the amount of the rubber component (B21) relative to the amount of the polymerizable monomer containing at least an aromatic vinyl monomer can be selected from a wide range depending on the characteristics of the rubber-modified styrenic resin, and is, for example, such that the former/the latter equals about 5/95 to 65/35 (% by weight), preferably about 10/90 to 60/40 (% by weight), more preferably about 15/85 to 50/50 (% by weight), and frequently about 10/90 to 65/35 (% by weight). Graft-polymerization in such ratio can afford a high impact resistant grafted polymer containing the rubber component corresponding to the ratio. In the rubber-modified styrenic resin (B2), the composition of the polymerizable monomers is, for instance, about 20 to 90% by weight and preferably about 21 to 85% by weight of the aromatic vinyl monomer (B1a), about 10 to 40% by weight and preferably about 14 to 38% by weight of the vinyl cyanide monomer (B1b) and about 0 to 40% by weight and preferably about 0 to 30% by weight of the copolymerizable vinyl monomer (B1c) in many cases. The mean or average particle size of the rubber component dispersed in the rubber-modified styrenic resin (B2), particularly in the grafted polymer, is for instance about 0.05 to 5 µm, preferably about 0.1 to 3 µm, and more preferably about 0.1 to 1 µm. When the mean particle size of the rubber component is less than 0.05 µm, the impact strength of the shaped article is liable to be decreased, and when it exceeds 5 µm, the gloss or luster and/or surface appearance of the shaped article is apt to be impaired or deteriorated. The rubber component may be dispersed as rubber disperse particles having a plurality of peaks (for example, two peaks) in the particle size distribution. The styrenic resin (B) may comprise the non-rubber-modified styrenic resin (B1) alone, but it may advantageously comprise at least the rubber-modified styrenic resin (B2), specifically the grafted polymer, for improvement or enhancement of the impact resistance. That is, the preferred examples of the styrenic resin (B) include (1) the rubber-modified styrenic resin (B2) alone, and (2) a mixed resin composition comprising the non-rubber-modified styrenic resin (B1) and the rubber-modified styrenic resin (B2). For improving or increasing the melt fluidity and molding processability, a mixture of the non-rubber-modified styrenic resin (B1) and the rubber-modified styrenic resin (B2) can frequently be used as the styrenic resin (B). The ratio of the non-rubber-modified styrenic resin (B1) relative to the rubber-modified styrenic resin (B2) may be selected from a wide range, and is, for instance, such that the former/the latter is about 0/100 to 75/25 (% by weight), preferably about 0/100 to 60/40 (% by weight), more preferably about 0/100 to 50/50 (% by weight), and frequently about 10/90 to 40/60 (% by weight). Use of the non-rubber-modified styrenic resin (B1) in a proportion of more than 75% by weight is apt to decrease the impact resistance of the shaped article, and use of the rubber-modified styrenic resin (B2) in an amount of less than 25% by weight is liable to decrease or impair the impact resistance of the shaped article. When the styrenic resin (B) is a mixed resin composition of the non-rubber-modified styrenic resin (B1) such as SAN resin, and the rubber-modified styrenic resin (B2) such as ABS resin, the content of the rubber component in the styrenic resin (B) is, for instance, about 1 to 50% by weight, preferably about 5 to 40% by weight, and more preferably about 10 to 30% by weight. When using the rubber component in a proportion of less than 1% by weight, the impact resistance of the shaped article may be decreased, and when using it in a proportion of more than 50% by weight, decrease of the melt fluidity, or gelation (gelling), coloring and/or deterioration during the molding process are liable to occur. The non-rubber-modified styrenic resin may be prepared by a conventional method such as emulsion polymerization, solution polymerization, bulk polymerization, suspension polymerization and the like. The rubber-modified styrenic resin (grafted polymer) may frequently be prepared by bulk polymerization, suspension polymerization or emulsion polymerization. In the polymerization, if necessary, an inert solvent such as benzene, ethylbenzene, toluene, xylene and a mineral oil, a molecular weight regulator, an antioxidant, a lubricant, a plasticizer and so on may be added. [Resin mixture] By melting and mixing the polycarbonate (A) and the styrenic resin (B), a shaped article having high heat and impact resistance can be obtained. It may probably be because these resins form a polymer alloy. The ratio of the polycarbonate (A) relative to the styrenic resin (B) can be selected from the range according to the species of each of the resins insofar as not impairing the heat resistance, the impact resistance, the melt fluidity and the like, and is for example such that the former/the latter is about 40/60 to 95/5 (% by weight), preferably about 50/50 to 95/5 (% by weight) and more preferably about 55/45 to 85/15 (% by weight). The proportion of the polycarbonate (A) relative to the styrenic resin (B) is frequently such that the former/the latter is about 50/50 to 90/10 (% by weight), particularly about 60/40 to 90/10 (% by weight). Use of the polycarbonate (A) in a proportion of less than 40% by weight is apt to decrease or reduce the heat resistance or the impact resistance of the shaped article, although the melt fluidity is in high level in such case. When the proportion of the polycarbonate (A) exceeds 95% by weight, the melt fluidity during the molding process is liable to be decreased. The content of the rubber component in the resin mixture is, for instance, about 1 to 30% by weight and preferably about 1 to 25% by weight. [Flame-retardant (C)] The flame-retardant (C) is an aromatic phosphoric acid ester shown by the formula (I). In the formula (I), the alkyl group which may be substituted on the phenyl group of R 1 to R 4 includes, for example, a lower alkyl group having about 1 to 4 carbon atoms such as methyl, ethyl, propyl, isopropyl, butyl, isobutyl, s-butyl and t-butyl groups. Among these alkyl groups, an alkyl group having 1 to 3 carbon atoms, particularly methyl group and/or ethyl group is preferred. Each of the phenyl groups may be substituted with about 0 to 3, preferably about 1 to 3 (for instance, 1 or 2, particularly 2) alkyl groups. The aromatic residue represented by A is 1,3-phenylene The feature of the present invention resides in the use of, as the flame-retardant, the compound shown by the formula (I). The flame-retardant (C) may frequently comprise a mixture of phosphoric acid esters differing in the repeating unit n. The mean or average value of such repeating unit n is about 0.5 to 2.0, preferably about 1.0 to 1.8 and more preferably about 1.2 to 1.7. In the mixture of phosphoric acid esters differing or varying in the repeating unit n, the proportion of the compound where n=1 is, for instance, about 40 to 90 mole percent, preferably about 50 to 80 mole percent, and more preferably about 55 to 75 mole percent. To be more concrete, a mixture of the phosphoric acid ester oligomers comprises, in many cases, about 0 to 10 mole percent, preferably about 0 to 7 mole percent and more preferably about 0 to 5 mole percent of the compound having the repeating unit n of 0, about 40 to 90 mole percent, preferably about 50 to 80 mole percent and more preferably about 55 to 75 mole percent of the compound having the repeating unit n of 1, about 5 to 40 mole percent, preferably about 7 to 35 mole percent and more preferably about 10 to 30 mole percent of the compound having the repeating unit n of 2, and about 5 to 25 mole percent, preferably about 7 to 20 mole percent and more preferably about 7 to 17 mole percent of the compound having the repeating unit n of not less than 3. The proportion of the compound having the repeating unit n of not less than 3 may be about 1 to 25 mole percent. The phenyl group substituted with 1 to 5 alkyl groups each having 1 to 4 carbon atoms includes, for instance, a monoalkylphenyl group such as 2-methylphenyl group, 3-methylphenyl group, 4-methylphenyl group, 2-ethylphenyl group, 3-ethylphenyl group, 4-ethylphenyl group, 2-propylphenyl group, 3-propylphenyl group, 4-propylphenyl group, 2-isopropylphenyl group, 3-isopropylphenyl group, 4-isopropylphenyl group, 2-butylphenyl group, 3-butylphenyl group, 4-butylphenyl group, 2-isobutylphenyl group, 3-isobutylphenyl group, 4-isobutylphenyl group, 2-s-butylphenyl group, 3-s-butylphenyl group, 4-s-butylphenyl group, 2-t-butylphenyl group, 3-t-butylphenyl group, 4-t-butylphenyl group and so on; a 2,3-dialkylphenyl group such as 2,3-dimethylphenyl group, 2,3-diethylphenyl group, 2,3-dipropylphenyl group, 2,3-diisopropylphenyl group, 2-ethyl-3-methylphenyl group, 3-ethyl-2-methylphenyl group and the like; a 2,4-dialkylphenyl group such as 2,4-dimethylphenyl group, 2,4-diethylphenyl group, 2,4-dipropylphenyl group, 2,4-diisopropylphenyl group, 2-ethyl-4-methylphenyl group, 4-ethyl-2-methylphenyl group and others; a 2,5-dialkylphenyl group such as 2,5-dimethylphenyl group, 2,5-diethylphenyl group, 2,5-dipropylphenyl group, 2,5-diisopropylphenyl group, 2-ethyl-5-methylphenyl group, 5-ethyl-2-methylphenyl group and so on; a 2,6-dialkylphenyl group such as 2,6-dimethylphenyl group, 2,6-diethylphenyl group, 2,6-dipropylphenyl group, 2,6-diisopropylphenyl group, 2,6-dibutylphenyl group, 2,6-diisobutylphenyl group, 2,6-di-s-butylphenyl group, 2,6-di-t-butylphenyl group, 2-ethyl-6-methylphenyl group and others; a 3,4-dialkylphenyl group such as 3,4-dimethylphenyl group, 3,4-diethylphenyl group, 3,4-dipropylphenyl group, 3,4-diisopropylphenyl group, 3-ethyl-4-methylphenyl group, 4-ethyl-3-methylphenyl group and the like; a 3,5-dialkylphenyl group such as 3,5-dimethylphenyl group, 3,5-diethylphenyl group, 3,5-dipropylphenyl group, 3,5-diisopropylphenyl group, 3-ethyl-5-methylphenyl group and so on; a trialkylphenyl group such as 2,3,4-trimethylphenyl group, 2,3,5-trimethylphenyl group, 2,3,6-trimethylphenyl group, 2,9,5-trimethylphenyl group, 2,3,5-trimethylphenyl group, 3,9,5-trimethylphenyl group, 4-ethyl-2,6-dimethylphenyl group, 2,6-diethyl-4-methylphenyl group, 4-methyl-2,6-diisopropylphenyl group and others. The phenyl group substituted with 2 alkyl groups each having 1 to 3 carbon atoms such as methyl, ethyl and propyl groups (for instance, a dimethylphenyl group such as 2,6-dimethylphenyl group, 3,5-dimethylphenyl group, 2,4-dimethylphenyl group and so on) can specifically be used among these groups. Use of such phenyl group substituted with 2 alkyl groups each having 1 to 3 carbon atoms, particularly a dimethylphenyl group can extremely improve the heat resistance of the shaped article. As the phenyl group substituted with 2 alkyl groups each having 1 to 3 carbon atoms, a phenyl group substituted with the alkyl groups on the 2- and 6-positions (e.g., 2,6-dimethylphenyl group, 2,6-diethylphenyl group, 2-ethyl-6-methylphenyl group, etc.) may frequently be employed. The substituents R 1 , R 2 , R 3 and R 4 may be independently a phenyl group substituted with 1 to 5 alkyl groups each having 1 to 4 carbon atoms. When the compound where the substituents R 1 to R 4 are the phenyl groups each substituted with 1 to 5 alkyl groups each having 1 to 4 carbon atoms, the melt fluidity, and the light resistance of the shaped article can remarkably be improved or enhanced. Use of a compound where all of the substituents R 1 to R 4 are non-substituted phenyl groups notably decrease or impair the light resistance of the shaped article. When using a compound where A is 1,4-phenylene group, the melt fluidity is decreased and the tensile elongation of the shaped article is reduced. The repeating unit n in the formula (I) may be an integer of 1 to 5. The compound of the formula (I) wherein n is an integer of 1 to 3, particularly 1 or 2, more specifically 1 can advantageously be used for constituting a flame-retardant of an oligomeric phosphoric acid ester (phosphoric ester). These flame-retardants (flame-retarders) can be employed singly or in combination. The flame-retardant shown by the formula (I) can be prepared by various methods. By way of illustration, as described in Japanese Patent Application Laid-open No. 1079/1993 (JP-A-5-1079), the flame-retardant can be prepared by allowing a phenol compound corresponding to R 1 , R 2 , R 3 and R 4 (for example, phenol, cresol, xylenol and the like) to react with phosphorus oxychloride and a dihydric phenol corresponding to the aromatic residue A (e.g., resorcinol, hydroquinone, bisphenol A, 1,4-dihydroxybenzene and so on). The ratio of the dialkylphenyl group relative to the monoalkylphenyl group or the like can easily be controlled or adjusted by selecting the species and the amount of the phenol compound corresponding to R 1 , R 2 , R 3 and R 4 . The amount of the compound (C) shown by the formula (I) may be an effective amount to impart the flame-retardancy (fire resistance) to the polycarbonate (A) and the styrenic resin (B), and is, for example, about 5 to 50 parts by weight, preferably about 10 to 30 parts by weight, and more preferably about 15 to 25 parts by weight relative to 100 parts by weight of the mixed resin composition of the polycarbonate (A) and the styrenic resin (B). Use of the flame-retardant (C) in a proportion of less than 5 parts by weight relative to 100 parts by weight of the mixed resin composition can hardly impart high melt fluidity and the high flame-retardancy suited to the UL Standard to the shaped or molded article, and the use in a proportion of more than 50 parts by weight is apt to decrease or impair the heat resistance of the shaped article, although imparting high melt fluidity and flame-retardancy. When the amount of the flame-retardant shown by the formula (I) is about 10 to 25 parts by weight relative to 100 parts by weight of the mixed resin composition, well-balanced various characteristics such as the flame-retardancy, heat resistance, impact resistance, melt fluidity and others can be obtained. [Fluororesin (D)] The use of the fluororesin (D) can suppress drip of a kindling substance and a molten mixture, thus the fluororesin (D) acts as a flame-retarding-auxiliary. The fluororesin includes, for example, a mono- or copolymer obtainable by polymerizing a fluorine-containing monomer such as tetrafluoroethylene, chlorotrifluoroethylene, vinyl fluoride, vinylidene fluoride, hexafluoropropylene, perfluoroalkyl vinyl ether and so on; a copolymer obtainable by polymerizing the fluorine-containing monomer and a copolymerizable monomer such as ethylene, propylene and acrylate. Practical examples of the fluororesin include a homopolymer such as polytetrafluoroethylene, polychlorotrifluoroethylene, polyvinylidene fluoride and others; a copolymer such as a tetrafluoroethylene-hexafluoropropylene copolymer, a tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer, a tetrafluoroethylene-hexafluoropropylene-perfluoroalkyl vinyl ether copolymer, an ethylene-tetrafluoroethylene copolymer, an ethylene-chlorotrifluoroethylene copolymer and the like. These fluororesins can be employed singly or in combination. Polytetrafluoroethylene (hereinafter referred to as PTFE) can preferably be used among these fluororesins. The fluororesin may be prepared by a conventional method such as the emulsion polymerization method described in U.S. Patent No. 2,393,967. The fluororesin may be compounded or incorporated into the resin composition by melting and mixing with the polycarbonate and the styrenic resin, or may frequently be used in a powdery form, for example as a powder or granular having a mean particle size of about 10 to 5,000 µm, preferably about 100 to 1,000 µm, and more preferably about 200 to 700 µm. The fluorine-content of the fluororesin may be selected from a range depending on the species of the resin insofar as the flame-retardancy or flame resistance can be imparted to the shaped article, and frequently is, for instance, about 65 to 75% by weight and preferably about 70 to 74% by weight. The apparent density of the powdery or granular fluororesin is, for example, about 0.4 to 0.6 g/cm 3 , and preferably about 0.43 to 0.47 g/cm 3 . When the fluororesin is polytetrafluoroethylene, the specific gravity of the fluororesin is about 2.13 to 2.22 g/cm 3 , and the melting point is about 326°C to 328°C. The flame-retarding-auxiliary (D) may be used in an amount of, for instance, about 0.05 to 5 parts by weight, preferably about 0.1 to 2 parts by weight and more preferably about 0.2 to 1 part by weight relative to the 100 parts by weight of the resin mixture. When adding the fluororesin (D) in a proportion of less than 0.05 part by weight, sufficient inhibiting or suppressing effect on the drip of the kindling substance and/or molten drop (drip-inhibiting effect) and thus high flame-retardancy or fire resistance cannot be imparted to the shaped article. Addition of the fluororesin in a proportion of more than 5 parts by weight may increase the shrinkage of the shaped article by heat, with decreasing the dimensional accuracy during heating process as well as with increasing cost. [Other additives] The flame-retardant resin composition may be added with various additives including, for example, a degradation-inhibitor such as an antioxidant, an ultraviolet-absorber and a light-resistant stabilizer; a lubricant; an antistatic agent; a mold release agent (mold lubricant); a plasticizer; a reinforcing fiber such as a glass fiber, a carbon fiber, a polyamide fiber, an aromatic polyamide fiber, an aromatic polyester fiber and the like; a filler such as calcium carbonate and talc; and a coloring agent such as a pigment. The amount of such additive may be selected from a range according to the species of the additive insofar as not impairing, for instance, the heat resistance, the impact resistance and the mechanical strength of the shaped article. By way of illustration, the additive such as an antioxidant is frequently used in an amount of about 5% by weight or less based on the total amount of the composition, and the reinforcing agent such as a glass fiber and/or the filler is usually employed in a proportion of 50% by weight or less based on the total amount of the composition. [Preparation of the resin composition] The flame-retardant (fire resistant) resin composition may be a premixed composition obtainable by premixing the polycarbonate (A), the styrenic resin (B), the flame-retardant (C) and the fluororesin (D) with the use of a mixer such as a V-blender, a supermixer, a superfloater and a Henshell mixer. The resin composition is usually a mixture obtainable by melting and mixing the premixed composition homogeneously. Such mixture can be obtained by melting and kneading the premixed mixture, with using a kneading means, at a temperature of, for example, about 200 to 300°C and preferably about 220 to 280°C, and pelletizing the resultant mixture. As the kneading means, various melting-mixing apparatus such as a kneader, a uniaxially or biaxially extrusion machine can be employed. The resin composition may frequently be prepared by melting and extruding components for the resin composition with using a biaxially extruding machine or the like, and pelletizing the resultant using a pelletizer. The flame-retardant resin composition of the present invention has high melt fluidity, whereby not only a miniature article but also a lightweight shaped article and a shaped article having a thin portion can be molded with improved accuracy, and the shaped article can be imparted with high flame-retardancy. In particular, use of the flame-retardant resin composition comprising the flame-retardant corresponding to the case (ii) can further impart high light resistance in addition to such excellent flame-retardancy to the shaped article. Accordingly, the flame-retardant resin composition is useful as a molding material for various shaped articles such as a housing and/or enclosure of a home electric apparatus, an OA apparatus and the like, and a thin housing or casing of, for instance, a portable telephone. Such shaped article can be produced by a conventional method, for example by injection molding the pelletized flame-retardant resin composition with using an injection molding machine at, for instance, a cylinder temperature of about 220 to 280°C. The flame-retardant resin composition of the present invention, which comprises a specific flame-retardant of aromatic phosphoric acid ester, has excellent flame-retardancy and fire resistance, as well as high melt fluidity. Accordingly, by using the composition, not only a large size shaped article such as a housing but also an article having a thin portion or a thinned shaped article can be molded with high accuracy. Further, use of the composition can afford a shaped article having improved or enhanced light resistance, and therefore discoloration or discoloring of the shaped article can be inhibited or suppressed. Moreover, according to the present invention, where the specific flame-retardant in combination with the fluororesin is added to the mixed resin composition of the polycarbonate and the styrenic resin, the drip from the shaped article during burning can be suppressed and thus high flame-retardancy can be imparted to the shaped article. Further, a shaped article being excellent in the heat resistance and impact resistance and the mechanical strength can be obtained. Furthermore, a shaped article having improved or enhanced light resistance in addition to the above excellent characteristics can be obtained. EXAMPLES The following examples are merely intended to illustrate the present invention in further detail and should not be construed as defining the scope of the invention. In the following examples, the tensile strength (kg/cm 2 ) and the tensile elongation were measured according to ASTM D-638 at a crosshead speed of 5 mm/min., and the bending elasticity (kg/cm 2 ) was measured according to ASTM D-790 at a rate of 3 mm per minute. The Izod impact strength (kg·cm/cm) was determined in accordance with ASTM D-256 using a test piece having a thickness of 6.35 mm (1/4 inch) and formed with cut notches. The thermal-deforming temperature (°C) was measured according to ASTM D-256 by permitting a load of 18.56 kg/cm 2 to act on a bar having a thickness of 6.35 mm (1/4 inch). The melt fluidity (g/10 min.) was determined according to Japanese Industrial Standards (JIS) K-7210 under the conditions of a temperature of 230°C and with a load of 5 kg, and the flame resistance was evaluated in accordance with UL-94 using a test piece having a thickness of 1.59 mm (1/16 inch). The spiral flow length (bar flow length) (mm) was estimated at a cylinder temperature of 240°C, an injection pressure of 750 kgf/cm 2 , of a width of 20 mm and a thickness of 2 mm. The light resistance was evaluated by the discoloring degree (ΔE) after light-irradiation on a three steps-formed (three-high) color plate (50 mm x 30 mm x 1 mm/2 mm/3 mm-thickness) for 300 hours using a xenon lamp. Further, the water-discoloring resistance was estimated by whether a white spot on the surface of the three steps-formed color plate was formed or not after dipped in water at room temperature for one day. Example 1 A mixture of thermoplastic resins was prepared using 70 parts by weight of a polycarbonate resin (manufactured by Idemitsu Petroleum Chemicals Co., Ltd., IDEMITSU POLYCARBONATE FN2700, viscosity-average molecular weight of 27,000), 10 parts by weight of the following non-rubber-modified styrenic resin and 20 parts by weight of the following rubber-modified styrenic resin. The non-rubber-modified styrenic resin: a copolymer having a weight-average molecular weight of 123,000 obtained by suspension-polymerizing 75 parts by weight of styrene and 25 parts by weight of acrylonitrile in an aqueous solution of a calcium phosphate-containing dispersing agent according to the method described in Japanese Patent Publication No. 51962/1987 (JP-B-62-51962). The rubber-modified styrenic resin: a grafted polymer obtained, according to the method described in Japanese Patent Application Laid-open No. 320274/1993 (JP-A-5-320274), by emulsion-polymerizing 45 parts by weight of styrene and 15 parts by weight of acrylonitrile in the presence of a polybutadiene rubber latex (40 parts by weight as a solid basis). To 100 parts by weight of the thermoplastic resin mixture, were added 19 parts by weight of a flame-retardant of a phosphoric acid ester (manufactured by Daihachi Chemical Industries Co., Ltd., PX200), 0.4 part by weight of polytetrafluoroethylene (manufactured by Daikin Industries, Co., Ltd., POLYFLON TFE (grade name F-104), mean particle size of about 500 µm, apparent density of 0.45 g/ml, melting point of 326 to 328°C, specific gravity of 2.14 to 2.20, fluorine-content of about 76%), 0.2 part by weight of an antioxidant and 0.2 part by weight of a heat stabilizer. The mixture was premixed for 40 minutes using a V-blender, and the premixed mixture was molten and extruded with the use of a biaxially kneading-extruding machine and pelletized to give a pellet. The above-mentioned flame-retardant is the compound of the formula (I) wherein R 1 , R 2 , R 3 and R 4 are 2,6-dimethylphenyl groups, A is 1,3-phenylene group and n=1. The above-obtained pellet was dried in an oven at 80°C for 4 hours or more, and the dried pellet was injection-molded using an injection molding machine having a mold clamping force of 100 ton at a temperature of 240°C, at a screw rotating rate of 80 rpm and at a mold temperature of 80°C to give a test piece (ASTM No. 2 dumbbell piece, a bar (6.35 mm) (1/4 inch) in thickness, 126 mm in length), and a test piece for UL burning test (126 mm x 126 mm x 1.6 mm in thickness)). Further, the pellet was injection-molded using an injection molding machine having a mold clamping force (locking force) of 100 ton by a conventional injection molding method to give a three steps-formed color plate having three species of thickness (50 mm x 30 mm x 1 mm/2 mm/3 mm in thickness). Comparative Example 1 Procedure of Example 1 was repeated to obtain test pieces except for using 19 parts by weight of a flame-retardant of a non-substituted aromatic phosphoric acid ester of the formula (I) wherein R 1 , R 2 , R 3 and R 4 are non-substituted phenyl groups, A is 1,3-phenylene group and n is an integer of 0 to 4 (manufactured by Daihachi Chemical Industries Co., Ltd., CR733S), instead of the flame-retardant of aromatic phosphoric acid ester of Example 1 The flame-retardant of the non-substituted aromatic phosphoric acid ester comprises about 3% of the compound having the repeating unit n of 0, about 70% of the compound having the repeating unit n of 1, about 20% of the compound having the repeating unit n of 2 and about 7% of the compound having the repeating unit n of not less than 3. Comparative Example 2 Test pieces were obtained in the same manner as Example 1, except that 19 parts by weight of a flame-retardant of a dimeric substituted aromatic phosphoric acid ester (manufactured by Daihachi Chemical Industries, Co., Ltd., PX201) was employed in lieu of 19 parts by weight of the flame-retardant of Example 1. The flame-retardant is the aromatic phosphoric acid ester compound of the formula (I) wherein R 1 , R 2 , R 3 and R 4 are 2,6-dimethylphenyl groups, A is 1,4-phenylene group and n=1. Comparative Example 3 The procedure of Example 1 was followed to obtain test pieces except for employing 19 parts by weight of a flame-retardant of a dimeric substituted aromatic phosphoric acid ester (manufactured by Daihachi Chemical Industries, Co., Ltd., PX202) instead of 19 parts by weight of the flame-retardant of Example 1. The flame-retardant is the aromatic phosphoric acid ester compound of the formula (I) where R 1 , R 2 , R 3 and R 4 are 2,6-dimethylphenyl groups, A is 4,4'-biphenylylene group and n=1. Example 2 By using 80 parts by weight of a polycarbonate resin (manufactured by Idemitsu Petroleum Chemicals Co., Ltd., IDEMITSU POLYCARBONATE FN2700, viscosity-average molecular weight of 27,000), 10 parts by weight of the non-rubber-modified styrenic resin of Example 1, and 10 parts by weight of the rubber-modified styrenic resin of Example 1, test pieces were obtained in the similar manner as Example 1. Example 3 Procedure of Example 1 was followed to obtain test pieces except for employing 80 parts by weight of a polycarbonate resin (manufactured by Idemitsu Petroleum Chemicals Co., Ltd., IDEMITSU POLYCARBONATE FN2700, viscosity-average molecular weight of 27,000), 7 parts by weight of the non-rubber-modified styrenic resin of Example 1, and 13 parts by weight of the rubber-modified styrenic resin of Example 1. Example 4 Test pieces were obtained in the same manner as Example 1, except that 60 parts by weight of a polycarbonate resin (manufactured by Idemitsu Petroleum Chemicals Co., Ltd., IDEMITSU POLYCARBONATE FN2700, viscosity-average molecular weight of 27,000), 20 parts by weight of the non-rubber-modified styrenic resin of Example 1, and 20 parts by weight of the rubber-modified styrenic resin of Example 1 were used. Example 5 By using 70 parts by weight of a polycarbonate resin (manufactured by Idemitsu Petroleum Chemicals Co., Ltd., IDEMITSU POLYCARBONATE FN2700, viscosity-average molecular weight of 27,000), 20 parts by weight of the non-rubber-modified styrenic resin of Example 1, and 10 parts by weight of the rubber-modified styrenic resin of Example 1, test pieces were prepared in the same manner as Example 1. Example 6 The procedure of Example 1 was repeated to obtain test pieces, except for employing 70 parts by weight of a polycarbonate resin (manufactured by Idemitsu Petroleum Chemicals Co., Ltd., IDEMITSU POLYCARBONATE FN2700, viscosity-average molecular weight of 27,000), 15 parts by weight of the non-rubber-modified styrenic resin of Example 1, 15 parts by weight of the rubber-modified styrenic resin of Example 1, 25 parts by weight of the flame-retardant of Example 1, and 0.6 part by weight of polytetrafluoroethylene of Example 1 Example 7 Test pieces were prepared in the similar manner as Example 1, except that 60 parts by weight of a polycarbonate resin (manufactured by Idemitsu Petroleum Chemicals Co., Ltd., IDEMITSU POLYCARBONATE FN2700, viscosity-average molecular weight of 27,000), 20 parts by weight of the non-rubber-modified styrenic resin of Example 1, 20 parts by weight of the rubber-modified styrenic resin of Example 1, and 16 parts by weight of the flame-retardant of Example 1 were used. Example 8 Test pieces were obtained in the same manner as Example 1, except that 9.5 parts by weight of a flame-retardant of the compound of the formula (I), where, in the total amount of R 1 , R 2 , R 3 and R 4 , 70% by weight is 2,4-dimethylphenyl group, 3,4-dimethylphenyl group and 3,5-dimethylphenyl group, and 30% by weight is methylphenyl group and ethylphenyl group; and A is 1,3-phenylene group; this flame-retardant comprises less than 3% by weight of the compound having the repeating unit n of 0 and not less than 97% by weight of the compound having the repeating unit n of not less than 1, and which comprises about 70% by weight of the compound having the repeating unit n of 1, about 20% by weight of the compound having the repeating unit n of 2, and about 7% by weight of the compound having the repeating unit n of not less than 3, and 9.5 parts by weight of the flame-retardant of Example 1 were used instead of 19 parts by weight of the flame retarder of Example 1. Comparative Example 4 The procedure of Example 1 was followed to obtain test pieces, except that a thermoplastic resin composition was prepared by using (a) 40 parts by weight of a polycarbonate resin (manufactured by Idemitsu Petroleum Chemicals Co., Ltd., IDEMITSU POLYCARBONATE FN2700, viscosity-average molecular weight of 27,000), (b) as the non-rubber-modified styrenic resin, 30 parts by weight of a copolymer (weight-average molecular weight of 90,000) obtained by suspension-polymerizing 25 parts by weight of styrene, 50 parts by weight of α-methylstyrene and 25 parts by weight of acrylonitrile, and (c) as the rubber-modified styrenic resin, 30 parts by weight of a grafted copolymer obtained by emulsion-polymerizing 45 parts by weight of styrene and 15 parts by weight of acrylonitrile in the presence of a polybutadiene rubber latex (30 parts by weight as a solid basis) and a styrene-butadiene copolymer rubber latex (10 parts by weight as a solid basis), and that 19 parts by weight of the flame-retardant of phosphoric acid ester of Comparative Example 1 was employed. Comparative Example 5 By using 95 parts by weight of the polycarbonate resin of Example 1, 2.5 parts by weight of the non-rubber-modified styrenic resin of Example 1 and 2.5 parts by weight of the rubber-modified styrenic resin of Example 1, as well as 19 parts by weight of the flame-retardant of phosphoric acid ester of Comparative Example 2, test pieces were prepared in the similar manner as Example 1. Comparative Example 6 Test pieces were obtained in the same manner as Example 1, except that 15 parts by weight of the non-rubber-modified styrenic resin of Example 1, and 15 parts by weight of the rubber-modified styrenic resin of Example 1 were employed, and that the polytetrafluoroethylene was not used. The characteristics of the test pieces each obtained in Examples 1 to 8 and Comparative Examples 1 to 6 were evaluated. The results are shown in Table 1. In Table 1, the styrenic resins each used in Example 1 and Comparative Example 4 are designated in the line of "Species of styrenic resin" by the symbols "(4)" and "(5)" respectively, and the total amount of the non-rubber-modified styrenic resin and the rubber-modified styrenic resin is set forth in the line of "Amount of styrenic resin". In the line of "Species of flame-retardant", the flame-retardants each employed in Example 1, Comparative Example 1, Comparative Example 2, Comparative Example 3 and Example 8, are defined by the symbols "(4)", "(5)", "(6)", "(7)" and "(8)" Separately. As apparent from Table 1, the compositions obtained in Examples 1 to 8 have high melt fluidity and are useful for molding a shaped article having high flame-retardancy and light resistance which is large shaped or thin shaped and is not liable to be discolored. The composition obtained in Comparative Example 1 has not only low light resistance but also poor heat resistance and impact resistance in comparison with the composition obtained in Example 1. Further, the flame-retardant employed in Comparative Example 1 is in a liquid form, so that the working properties during the premixing process is decreased or reduced. As compared with the composition obtained in Example 1, the composition obtained in Comparative Example 2 has lower melt fluidity and still less smaller tensile elongation. The composition obtained in Comparative Example 3 is insufficient in the flame-resistance and has lower flowability. In the composition of Comparative Example 4, the flame-retardancy is poor although with high melt fluidity, and the composition of Comparative Example 5 has poor melt fluidity though having high heat resistance. The composition obtained in Comparative Example 6 lacks sufficient flame-retardancy and causes a drip in the flame-resistance test. In the shaped articles each obtained in Examples 1 to 8, no spot was formed in the water discoloring resistance test, and to the contrary, as for the shaped articles obtained in Comparative Examples 1 and 5, white spots were formed in the water discoloring resistance test.

Claims: Flame-retardant resin composition comprising (A) an aromatic polycarbonate (B) a styrenic resin (C) an aromatic phosphoric acid ester of formula (I) wherein A is 1,3-phenylene, n is an integer of 1-5, and R 1 , R 2 , R 3 and R 4 independently represent phenyl, optionally substituted with C 1-4 -alkyl; at least one of R 1 to R 4 is a 2,6-di-(C 1-3 -alkyl)phenyl group; and (D) a fluororesin; Composition of claim 1, wherein in formula (I) n is an integer of 1-3. Composition of any of the preceding claims, wherein in formula (I) the alkyl substituent in is methyl or ethyl. Composition of any of the preceding claims, wherein (A) is a bisphenol A type aromatic polycarbonate. Composition of any of the preceding claims, wherein (D) is a powdery polytetrafluoroethylene. Composition of any of the preceding claims, comprising 100 parts by weight (pbw) of a thermoplastic resin mixture comprising 40-95 wt.-% of (A) and 5-60 wt.-% of (B), 5-50 pbw of (C), and 0.05-5 pbw of (D). Composition of any of the preceding claims, wherein (B) comprises a non-rubber-modified styrenic resin (B1) and a rubber-modified styrenic resin (B2) in a weight ratio ranging from 0:100-75:25. Composition of claim 7, wherein (B1) is a copolymer obtainable by polymerizing 50-90 wt.-% of an aromatic vinyl monomer (B1a), 10-40 wt.-% of a vinyl cyanide monomer (B1b) and 0-40 wt.-% of a copolymerizable vinyl monomer (B1c). Composition of claim 7 or 8, wherein (B2) is a grafted copolymer obtainable by graft-polymerizing 35-95 wt.-% of a polymerizable vinyl monomer comprising at least an aromatic vinyl monomer (B1a) to 5-65 wt.-% of a rubber-like polymer (B21) having a glass transition temperature (Tg) of not higher than 0°C. Composition of claim 5, wherein (A) is a bisphenol A type aromatic polycarbonate, (C) is a compound of formula (I), wherein n is 1 or 2, and which comprises 100 parts by weight (pbw) of a thermoplastic resin mixture comprising 50-95 wt.-% of (A) and 5-50 wt.-% of (B), 10-30 pbw of (C), and 0.1-2 pbw of (D). Composition of claim 10, wherein each of R 1 -R 4 is a di(C 1-3 -alkyl)phenyl group. Composition of claim 1, wherein in formula (I) each of R 1 -R 4 is a 2,6-dimethylphenyl group and n = 1.

Inventors: KOBAYASHI MICHIO, KOBAYASHI, MICHIO
Applicants: DAICEL CHEM, DAICEL CHEMICAL INDUSTRIES, LTD.
Application year: 1995
Main classification: C08L69
IPC codes: C08K5, C08L25, C08L27, C08L69