A PROCESS FOR PRODUCING GASOLINE, DIESEL FUEL AND CARBON BLACK FROM WASTE RUBBER AND/OR WASTE PLASTICS

Abstract: The present relates to a process for producing gasoline, diesel and carbon black by employing waste rubber and/or waste plastics materials. The process comprising performing a reaction of pyrolysis, removing impurities, catalytic cracking, and fractionating. The present invention also relates to a catalyst used in the process.

Description: Field of the Invention The present invention relates to a process for treating waste rubber and/or waste plastics, and more particularly to a process employing pyrolysis and catalytic cracking of waste rubber and/or waste plastics to produce gasoline, diesel and carbon black. Background of the Invention Many methods for preparing gasoline and diesel with waste rubber and waste plastics including those disclosed in US5,414,169, US4,851,601 and EP-A-0607862 and the like have been reported. US5,414,169 teaches a method in which pyrolysis reaction of waste rubber or waste plastics is first carried out, then resultant product is fluidified, and finally catalytic cracking is practiced with a catalyst in a liquid phase. US4,851,601 discloses a process in which catalytic cracking of product from pyrolysis of waste plastics is carried out in gaseous phase with a catalyst ZSM-5. The process cannot be used to treat a polyolefine containing halogen which makes the catalyst inactive. EP-A-0607862 discloses a method, in which materials from pyrolysis undergo the reaction of catalytic cracking with a acidic solid catalyst to produce a primary product from catalytic pyrolysis which is separated by cooling, then the resultant components in gaseous phase are subjected to a catalyst such as H 3 PO 4 to give a secondary hydrocarbon oil. Summary of the Invention The invention provides a method for producing gasoline, diesel and carbon black by using waste plastics and/or waste rubber. According to the invention, waste plastics and/or waste rubber materials being properly pretreated are charged into a pyrolysis reactor with a screw feeder or a reciprocating feeder. A spiral stirrer in the pyrolysis reactor is operated to stirred the contents when the reactant are charged. After the pyrolysis reaction is completed, resulting carbon black is drained away with the spiral stirrer from the pyrolysis reactor vessel. Other resulting substances of gaseous phase having lower molecular weight are subjected to a tank of desulfurating and/or denitrinating and/or dechlorinating to desulfurate and/or denitrinate and/or dechlorinate. Residual sulfur, nitrogen and chlorine are removed through a fixed bed, while primary catalytic pyrolysis is simultaneously conducted. Materials in gaseous phase enter the device for catalytic cracking to undergo the reaction of catalytic cracking therein. The substances produced by the catalytic cracking are separated to give the desired products. The spiral stirrer arranged in the pyrolysis reactor according to the invention decreases coking of the reacting substances, and enhances the efficiency of conduction of heat. In addition, the stirrer is rotated clockwise during the pyrolysis reaction, but drains the carbon black away when rotated counterclockwise. A special catalyst is employed in the invention, and the device for desulfurating and/or denitrinating and/or dechlorinating makes the life of the catalyst longer, and the range of materials treated wider. It solves problems known in the art. Brief Description of the Drawings Figure 1 is a schematic view of the reaction apparatus according to the invention, wherein the elements are: 27 screw feeder or reciprocating feeder 1 heating furnace 5 pyrolysis reactor 2 spiral stirrer 8 a first device, for desulfurating and/or denitrinating and/or dechlorinating 9 a second device, for desulfurating and/or denitrinating and/or dechlorinating, and for simultaneously carrying out the primary recation of catalytic cracking 10 a device for catalytic cracking, and 25 a fractional column Detailed Description of the Invention According to preferred embodiments of the invention, waste rubber materials (NR, SR, SBR, BR, IR, CR, NBR, EPR, EPM and IIR ) and/or waste plastics ( PE, PP, PS, PVC, ABC, etc. ) are pretreated in known manner to remove impurities. A heating furnace 1 provides heat to a pyrolysis reactor 5 to control the temperature therein in the range of 350-500°C. The waste rubber and/or waste plastics treated are charged into the reactor 5 through a feeding inlet 3. A spiral stirrer 2 in the reactor is operated to stir when the reactive materials enter. The waste rubber and/or waste plastics undergo a reaction of pyrolysis in the range of the temperature. In the reactor 5 they are decomposed to generate hydrocarbons in gaseous substances having lower molecular weight. If the materials are waste rubber , they are entirely decomposed and carbon black residue is discharged out of the reactor through a valve 6 under the action of the spiral stirrer 2 and can be used for preparation of tires. Through the top of pyrolysis reactor 5, substances of gaseous phase having lower molecular weight are directed to device 8 for desulfurating and/or denitrinating and/or dechlorinating, in which base materials such as granular NaOH or KOH or fused forms thereof are provided. Most of the acidic gases such as HCl, SO 2 , SO 3 , H 2 S,etc. resulting from pyrolysis are absorbed in the device 8. The gaseous substances from device 8 enter a fixed bed 9, in which unabsorbed acidic gases and other odoriferous gases are removed while the primary reaction of catalytic cracking proceeds simultaneously. A particular catalyst DL, prepared by the inventor, is used in the fixed bed 9. The gaseous substances from the fixed bed 9 are charged into a device 10 which, arranged as a fixed bed, is then used for catalytic cracking. A catalyst XL used in the device 10 is also prepared by the inventor. The complete reaction of catalytic cracking of gaseous substances from the device 9 is thus carried out, along with a series of other reactions such as folding reaction, reaction of hydrogen transfer and reaction of aromatization. Gasoline, diesel and other mixed components of combustible gases are obtained from these reactions. The reactions in the fixed beds 9 and 10 are carried out at a temperature of 200-400°C, under a pressure of 0.02-0.08 MPa, and at an air speed 1-2000 m/h. The products of catalytic cracking from the device 10 are introduced into a condenser 19, in which they are cooled down to room temperature. The resulting liquid is a mixture of gasoline and diesel. The materials from the devise 19 enter a buffer vessel 21 through a separator 20. The gases are charged into a storage tank 11 from the top of the separator 20 from which the combustible gas is introduced back into the heating furnace 1 to burn. Residue gas in the tank 11 is discharged into air to burn through a water-sealed tank 12. The liquid oil mix in the buffer vessel 21 is treated with inorganic acid such as sulfuric acid for removing impurities. The oil mix is pumped into a heat exchange 24 with a pump 23 to be heated to a temperature of 250-350C, then introduced into a fractional column 25, in which gaseous and diesel are separated in different distillation cuts. Gasoline is introduced into a condenser 14 from the top of column 25, and enters a gasoline storage tank 28 through a separation facility 16 for separating oil and water. Diesel enters a stripper 26 from the middle of the fractional column 25. Diesel is introduced into a condenser 13 after treatment by the overheated vapor, then enters a diesel storage tank 17 through a separation facility 15 for separating oil and water. The catalyst DL in the fixed bed 9 is composed of a mixture of materials A and B, wherein the material A comprises 40-70% kaolin or activated clay, 10-30% aqueous solution of KOH or NaOH ( 10-20% of solid content ), 10-15% ZnO or soluble zinc salt, 3-5% CuO or soluble copper salt, and a suitable amount of a binder of silicon or aluminum such as conventional binders used in the art, for example, sodium silicate. The materials are mixed, washed, dried and calcined at a temperature of 500-700 C, and material A is thus obtained. Material B comprises 40-80% kaolin or activated clay, 10-30% aqueous solution of NaOH or KOH ( 10-20% of solid content ), 10-20% CaO or CaCO 3, and a suitable amount of a binder of silicon or aluminum such as conventional binders used in the art, for example, sodium silicate. The materials are mixed, shaped, washed, dried and not calcined or calcined at a temperature of 500-700°C, and material B is thus obtained. The ratio of the mixture of materials A and B may be varied by persons skilled in the art if desired. Preferably, it is prepared as a particulate. The catalyst XL in the device 10 for catalytic cracking comprises 10-70% synthetic carrier or semi-synthetic carrier, 10-50% HZSM-5 zeolite, 10-20% aqueous solution of NaOH or KOH ( 10-20% of solid content), 3-5% ZnO or a compound selected from the group consisting of Zn, Pt, Fe, Cu and Ni, and a suitable amount of a binder of silicon or aluminum such as conventional binders used in the art, preferably, sodium silicate. The materials are mixed, shaped, washed, dried and calcined at a temperature of 500-700°C, and catalyst XL is thus obtained. Said synthetic carrier is prepared by the method of co-gelatination or precipitate, which contains 20-80% SiO 2 as amorphous Si-Al, and Si-Mg and the like. A suitable amount of clay can be added to the synthetic carrier to adjust the bulk of the catalyst. Said semi-synthetic carrier comprises kaolin, polyhydrate kaolin or activated clay, which are used as carriers of the cracking catalyst in the art, and a binder selected from the group consisting of Al 2 O 3 , Na 2 SiO 3 , and SiO 2 •Al 2 O 3 . Preferably, the catalyst is prepared as a particulate. Example 1 1000 kg plastics waste was ground after removal of impurities. The materials were then charged into the reactor 5 for pyrolysis via the feeder inlet 3. The pyrolysis device 5 was heated with the heating furnace 1 to keep the temperature of materials in the device at 350-500°C while the pyrolysis reaction was carried out and the materials were decomposed into gaseous hydrocarbons of small molecular weight. Gas from the device 5 was charged into the device 8 to remove acidic gases. Gaseous substances from the device 8 were further treated to remove the residual sulfur, chlorine and nitrogen by the catalyst DL in the fixed bed in the device 9, where the primary reaction of the catalytic cracking proceeded. The substances from the device 9 entered the device 10 to perform the reaction of catalytic cracking. The temperature in the devices 9 and 10 was 200-400°C, and the pressure was in the range of 0.02-0.08 MPa. The materials from the device 10 were separated and fractionated to give gasoline 370 kg and diesel 370 kg. The RON of gasoline of the product was 90-93, dried point ≤ 205. The cetane ratio of diesel of the product was 45-60. The 95% distillation range of diesel in the product was less than 360°C ( freezing point ≤ -20°C). Example 2 In the same manner as in Example 1, 1000 kg waste rubber was used to give gasoline 320 kg, diesel 309 kg and carbon black 280 kg. The BP absorption value of carbon black was 47±7 cm 2 /100g, the ash content ≤ 0.3%, and the heated reduction ≤ 1.0%. Industrial Applicability According to the method of the invention, gasoline, diesel and carbon black can be produced with a higher yield by using materials of waste plastics and/or waste rubber. The method of the invention can be used to guarantee the consecutive production in the industry.

Claims: A process for producing gasoline, diesel and carbon black from waste rubber and/or plastics materials, comprising: charging the waste material into a pyrolysis device through a feeder; discharging carbon black from the pyrolysis; charging the resulting materials in gaseous phase into a device for catalytic cracking; and fractionating the resulting products through a fractional column, wherein the reactive materials are stirred with a screw stirrer in the pyrolysis device, and enter a device for desulfurating and/or denitrinating and/or dechlorinating prior to entering the device for catalytic cracking; said device for desulfurating and/or denitrinating and/or dechlorinating comprises an absorption device with a base and an absorption device with a fixed bed; said catalyst used in the device for cata-1ytic cracking is prepared as follows: 10-70 % synthetic carrier or semi-synthetic carrier, 10-50 % HZSM-5 zeolite, 10-20 % aqueous solution of NaOH or KOH (10-20 % of solid content), 3-5 % ZnO or a compound selected form the group consisting of Zn, Pt, Fe, Cu and Ni, and a suitable amount of a binder of silicon or aluminium are mixed, shaped, dried and calcined or not calcined to give the desired catalyst; said catalyst used in the fixed bed is made from A and B, in which; A is prepared by mixing 40-70 % kaolin or activated clay, 10-30 % aqueous solution, of NaOH or KOH (10-20 % of solid content), 10-15 % ZnO or a soluble zinc salt, and 3-5 % CuO or a soluble copper salt, with suitable amount of a binder of silicon or aluminium, washing, drying and calcining, and B is prepared by mixing 40-70 % kaolin or activated clay, 10-30 % aqueous solution of NaOH or KOH (10-20 % of solid content), 10-20 % CaO or CaCO 3 , with suitable amount of a binder of silicon or aluminium, shaping, drying and calcining. The process according to claim 1, wherein said absorption device with a fixed bed is also a device for catalytic cracking. The process according to claim 1, wherein the reaction temperature in the absorption device with a fixed bed or the device for catalytic cracking is in the range of 200-400C, and the pressure is in the range of 0.02-0.08 MPa. The process according to claim 1, wherein said catalyst is prepared as a particulate.

Inventors: XING LI, XING, LI
Applicants: XING LI, XING, LI
Application year: 1995
Main classification: C10G1
IPC codes: B09B3, C09C1, B01D53, C10B53, B01J21, B01J29, C10G1