Spray polyurea elastomers

Abstract: Spray polyurea elastomers are disclosed made from an (A) component and a (B) component, where the (A) component has a quasi-prepolymer made from an isocyanate and an active hydrogen-containing material, such as a polyoxyalkylenepolyamine. The (B) component includes an amine resin, such as an amine-terminated polyoxyalkylene polyol which may be the same or different from the polyoxyalkylene polyamine of the quasi-prepolymer. The viscosity of the (A) component is reduced by the inclusion of an organic, alkylene carbonate, such as ethylene carbonate, propylene carbonate, butylene carbonate, dimethyl carbonate, and the like. The alkylene carbonate also serves as a compatibilizer between between the two components, thus giving an improved mix of the system.

Description: Field of the Invention The invention relates to aliphatic and aromatic spray polyurea elastomers and processes for making the same, and, in one aspect, more particularly to methods for making aliphatic and aromatic spray polyurea elastomers containing organic carbonates. Background of the Invention Spray elastomer systems are commonly recognized as coating materials, with aliphatic and aromatic spray polyurea elastomer systems being particularly useful when employed in this capacity. This two-component technology is based on an isocyanate quasi-prepolymer and an amine coreactant, often an amine resin blend. Typically, the isocyanate quasi-prepolymer is higher in viscosity than the amine resin blend. This difference in viscosity, coupled with the fast reaction characteristics of these systems, can lead to processing problems in thin film applications. For example, it would be desirable to provide a spray elastomer system where the viscosity of the isocyanate quasi-prepolymer could be lowered. Further, it would be advantageous if such a system would permit the two components to combine more readily to quickly provide a homogeneous mixture. There is considerable published literature on the topic of polyurea elastomers. For example, see U.S. Pat. No. 5,162,388 to Dudley J. Primeaux, II, which discusses aliphatic polyurea elastomers having an (A) component and a (B) component. The (A) component includes an aliphatic isocyanate, while the (B) component includes an amine-terminated polyoxyalkylene polyol and a chain extender. The chain extender may include cis -1,4-diaminocyclohexane, isophoronediamine, m -xylenediamine, 4,4'-methylenedicyclohexylamine, methanediamine, 1,4-diaminoethylcyclohexane and substituted derivatives thereof. EP-A-0 529 791 discusses quasi-prepolymers of aliphatic diisocyanates and polyoxyalkylene mixtures useful for making polyurea elastomers. EP-A-0 350 644 relates to a reaction injection molded elastomer, wherein polyurea RIM systems having improved flow properties with cyclic alkylene carbonates have been used. Summary of the Invention Accordingly, it is an object of the present invention to provide an aliphatic and aromatic spray polyurea elastomer where the isocyanate quasi-prepolymer component has reduced viscosity from that known before. It is another object of the present invention to provide an aliphatic and/or aromatic spray polyurea elastomer where the agent that provides for reduced viscosity of the isocyanate component also acts as a compatibilizer between the two components to improve the mix of components and homogeneity of the system. A particular object of the invention is to provide an aliphatic and/or aromatic spray polyurea elastomer with the above characteristics and which has good physical properties including good surface characteristics. In carrying out these and other objects of the invention, there is provided, in one form, a spray polyurea elastomer having an (A) component which includes a quasi-prepolymer of an isocyanate and an active hydrogen-containing material; together with an alkylene carbonate. To make the elastomer, the (A) component is reacted with the (B) component which has at least one amine-terminated polyoxyalkylene polyol. In one embodiment of the invention, the (B) component is an amine resin blend. Detailed Description of the Invention It has been discovered that the addition of an organic, alkylene carbonate, such as TEXACAR® PC or TEXACAR EC-50, to the isocyanate quasi-prepolymer of the (A) component, will result in a lower viscosity component. The carbonate also functions as a compatibilizer between the two components, which gives an improved mix and increased homogeneity of the system. This lower viscosity and improved mix allows for paint-type application of the aliphatic and/or aromatic spray polyurea technology. The aliphatic and/or aromatic spray polyurea elastomer system of the present invention generally includes two components, an (A) component and a (B) component. In particular, the (A) component may include an aliphatic isocyanate. The aliphatic isocyanates employed in component (A) are those known to one skilled in the art. Thus, for instance, the aliphatic isocyanates are of the type described in U.S. Pat. No. 4,748,192, Accordingly, they are typically aliphatic diisocyanates, and more particularly are the trimerized or the biuretic form of an aliphatic diisocyanate, such as, hexamethylene diisocyanate, or the bifunctional monomer of the tetraalkyl xylene diisocyanate, such as the tetramethyl xylene diisocyanate. Cyclohexane diisocyanate is also to be considered a preferred aliphatic isocyanate. Other useful aliphatic polyisocyanates are described in U.S. Pat. No. 4,705,814. They include aliphatic diisocyanates, for example, alkylene diisocyanates with 4 to 12 carbon atoms in the alkylene radical, such as 1,12-dodecane diisocyanate and 1,4-tetramethylene diisocyanate. Also described are cycloaliphatic diisocyanates, such as 1,3- and 1,4-cyclohexane diisocyanate as well as any desired mixture of these isomers, 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane (isophorone diisocyanate); 4,4'-, 2,2'- and 2,4'-dicyclohexylmethane diisocyanate as well as the corresponding isomer mixtures, and the like. Aromatic isocyanates may also be employed. Suitable aromatic polyisocyanates include, but are not necessarily limited to, m -phenylene diisocyanate; p -phenylene diisocyanate; polymethylene polyphenylisocyanate; 2,4-toluene diisocyanate; 2,6-toluene diisocyanate; dianisidine diisocyanate; bitolylene diisocyanate; naphthalene-1,4-diisocyanate; diphenylene-4,4'-diisocyanate; and the like. Aliphatic/aromatic diisocyanates, such as xylylene-1,3-diisocyanate; bis (4-isocyanatophenyl)methane; bis (3-methyl-4-isocyanatophenyl)methane; and 4,4'-diphenylpropane diisocyanate. The aforestated isocyanates can be used alone or in combination. In the practice of the present invention, it is expected that the isocyanate will be at least partially reacted with an active hydrogen-containing material. The alkylene carbonates of this invention may be added to an (A) component having only a un-prereacted isocyanate therein, that is, not at least partially reacted with an active hydrogen-containing material to form a quasi-prepolymer. In such a case, the carbonates would work as a reactive diluent. However, it is anticipated that the alkylene carbonates will find a greater utility in the situation where the (A) component contains a quasi-prepolymer of a relatively high viscosity which may be lowered by the alkylene carbonate. The active hydrogen-containing materials may include, but are not necessarily limited to polyols or high molecular weight polyoxyalkyleneamines, also described herein as amine-terminated polyethers, or a combination thereof. The polyols include, but are not necessarily limited to, polyether polyols, polyester diols, triols, tetrols, etc., having an equivalent weight of at least 500, and preferably at least 1,000 up to 3,000. Those polyether polyols based on trihydric initiators of 4,000 molecular weight and above are especially preferred. The polyethers may be prepared from ethylene oxide, propylene oxide, butylene oxide or mixtures of propylene oxide, butylene oxide and/or ethylene oxide. Other high molecular weight polyols which may be useful in this invention are polyesters of hydroxyl-terminated rubbers, e.g., hydroxyl-terminated polybutadiene. Hydroxyl-terminated quasi-prepolymers of polyols and isocyanates are also useful in this invention. Especially preferred are amine-terminated polyether polyols, including primary and secondary amine-terminated polyether polyols of greater than 1,500 average molecular weight having from 2 to 6 functionality, preferably from 2 to 3, and an amine equivalent weight of from 750 to 4,000. Mixtures of amine-terminated polyethers may be used. In a preferred embodiment, the amine-terminated polyethers have an average molecular weight of at least 2,500. These materials may be made by various methods known in the art. The amine-terminated polyether resins useful in this invention, for example, are polyether resins made from an appropriate initiator to which lower alkylene oxides, such as ethylene oxide, propylene oxide, butylene oxide or mixtures thereof, are added with the resulting hydroxyl-terminated polyol then being aminated. When two or more oxides are used, they may be present as random mixtures or as blocks of one or the other polyether. In the amination step, it is highly desirable that the terminal hydroxyl groups in the polyol be essentially all secondary hydroxyl groups for ease of amination. Normally, the amination step does not completely replace all of the hydroxyl groups. However, the majority of hydroxyl groups are replaced by amine groups. Therefore, in a preferred embodiment, the amine-terminated polyether resins useful in this invention have greater than 50 percent of their active hydrogens in the form of amine hydrogens. If ethylene oxide is used, it is desirable to cap the hydroxyl-terminated polyol with a small amount of higher alkylene oxide to ensure that the terminal hydroxyl groups are essentially all secondary hydroxyl groups. The polyols so prepared are then reductively aminated by known techniques, for example, as described in U.S. Pat. No. 3,654,370. In the practice of this invention, a single high molecular weight amine-terminated polyol may be used. Also, mixtures of high molecular weight amine-terminated polyols, such as mixtures of di- and trifunctional materials and/or different molecular weight or different chemical composition materials, may be used. Also, high molecular weight amine-terminated polyethers or simply polyether amines are included within the scope of my invention and may be used alone or in combination with the aforestated polyols. The term "high molecular weight" is intended to include polyether amines having a molecular weight of at least 2000. Particularly preferred are the JEFFAMINE® series of polyether amines available from Huntsman Corporation; they include JEFFAMINE D-2000, JEFFAMINE D-4000, JEFFAMINE T-3000 and JEFFAMINE T-5000. As noted, the (A) component of the present spray polyurea elastomer systems include an organic alkylene carbonate. The alkylene carbonate may have the structure (I): where R 1 and R 2 are independently hydrogen or lower alkyl of 1 to 4 carbon atoms. In a particular embodiment of the invention, the alkylene carbonates are preferably chosen from the group of ethylene carbonate, propylene carbonate, butylene carbonate and dimethyl carbonate. In one embodiment of the invention, the proportion of alkylene carbonate in (A) component ranges from 1 to 20 percent, preferably from 5 to 15 percent and most preferably from 5 to 10 percent. These percentages are based on 100 volume parts in the (A) component. The use of the alkylene carbonates reduces the viscosity of the (A) component, allows slower effective reactivities in spray polyurea elastomer systems, improved properties and surface characteristics (flowability) and possibly improved adhesion to the surfaces on which the elastomer is sprayed. The polyurea elastomers of the invention can be used as protective coatings, in "paint" applications, membranes, barrier coatings, road marking coatings, decorative coatings, automotive instrument panel applications, and the like. The polyurea elastomer systems may also include chain extenders in the formulation, preferably within the (B) component. Suitable chain extenders include those aliphatic and cycloaliphatic diamine chain extenders mentioned in U.S. Pat. No. 5,162,388 and patent application Serial No. 08/117,962. Aromatic diamine chain extenders may also be useful. Other conventional formulation ingredients may be employed in component (A) or (B) as needed, such as, for example, foam stabilizers, also known as silicone oils or emulsifiers. The foam stabilizers may be an organic silane or siloxane. For example, compounds may be used having the formula: RSi[O-(R 2 SiO) n -(oxyalkylene) m R] 3 wherein R is an alkyl group containing from 1 to 4 carbon atoms; n is an integer of from 4 to 8; m is an integer of from 20 to 40; and the oxyalkylene groups are derived from propylene oxide and ethylene oxide. See, for example, U.S. Pat. No. 3,194,773. Pigments, for example titanium dioxide, may be incorporated in the elastomer system, preferably in the (B) component, to impart color properties to the elastomer. Reinforcing materials, if desired, useful in the practice of the invention are known to those skilled in the art. For example, chopped or milled glass fibers, chopped or milled carbon fibers and/or other mineral fibers are useful. Post curing of the elastomer of the invention is optional. Post curing will improve some elastomeric properties, such as heat sag. Employment of post curing depends on the desired properties of the end product. The (A) component and (B) component of the present spray polyurea elastomer system are combined or mixed under high pressure; most preferably, they are impingement mixed directly in the high pressure spray equipment. In particular, a first and second pressurized stream of components (A) and (B), respectively, are delivered from two separate chambers of the proportioner and are impacted or impinged upon each other at high velocity to effectuate an intimate mixing of the two components and, thus, the formulation of the elastomer system, which is then coated onto the desired substrate via the spray gun. The volumetric ratio of the (A) component to the (B) component is generally from 30 to 70 percent to 70 to 30 percent. Preferably, component (A) and component (B) are employed in a 1:1 volumetric ratio. Advantageously, the (A) and (B) components react to form the present elastomer system without the aid of a catalyst. The following Examples are provided to further illustrate the preferred embodiments of the present invention, but should not be construed as limiting the present invention in any way. Spray Work For all the spray work described in these Examples, a GUSMER® VR-H-3000 Proportioning unit (plural component) was used, fitted with a GUSMER GX-7-400 spray gun. The equipment was set so as to process each example at an isocyanate to resin blend volume ratio of 1.00. Spray processing pressures were maintained at 10 500 kPa (1500 psi) to 17 500 kPa (2500 psi) on both the isocyanate and resin blend components. Block heat, as well as hose heat, was set at 71°C (160°F). Example I This spray polyurea application used a system with the A-Component, a quasi-prepolymer of m-TMXDI®, 54.5 parts; and JEFFAMINE® D-2000, 36.4 parts. To this quasi-prepolymer, 9.1 parts of TEXACAR® PC (propylene carbonate) was added, all collectively referred to as the isocyanate component. The isocyanate component was reacted with a B-component (amine resin blend), a blend of JEFFAMINE T-5000, 24.9 parts; JEFFAMINE D-2000, 24.9 parts; JEFFAMINE T-403, 18.7 parts; JEFFAMINE D-230, 27.4 parts; and TiPure® R-900 (titanium dioxide), 4.1 parts. These components were mixed at a volume ratio of 1.00 (1.00 weight ratio) with high pressure, high temperature impingement mix spray equipment. The resulting aliphatic polyurea elastomer had an effective gel time of 2.0 seconds with a tack free time of approximately 10 seconds. Formulation and elastomer physical properties are detailed in Table I. This system was easily applied to a metal substrate with a uniform elastomer film thickness of 0,127 mm (5 mils (0.005 inches)). Example II This Example used a system with the same A-Component (isocyanate quasi-prepolymer component) as mentioned in Example I. The B-component used was a blend of JEFFAMINE T-5000, 22.8 parts; JEFFAMINE D-2000, 22.8 parts; JEFFAMINE T-403, 17.1 parts; JEFFAMINE D-230, 27.4 parts; and TiPure® R-900, 9.9 parts. These components were mixed at a volume ratio of 1.00 (1.00 weight ratio) using the same spray equipment in Example I. The resulting aliphatic polyurea elastomer had an effective gel time of 2.0 seconds with a tack free time of approximately 10 seconds. Formulation and elastomer physical properties are detailed in Table I. This system was easily applied to a metal substrate with a uniform elastomer film thickness of 0,127 mm (5 mils (0.005 inches)). Comparative Example III For comparison, this Example used a system with an A-Component (isocyanate quasi-prepolymer component) of composition: a quasi-prepolymer of m-TMXDI, 55 parts; and JEFFAMINE D-2000, 45 parts, with no alkylene carbonate. The B-component used was a blend of JEFFAMINE T-5000, 19.25 parts; JEFFAMINE D-2000, 28.87 parts; JEFFAMINE T-403, 22.86 parts; JEFFAMINE D-230, 22.86 parts; and TiPure R-900, 6.16 parts. These components were mixed at a volume ratio of 1.00 (1.00 weight ratio) using the same spray equipment in Examples I and II. The resulting aliphatic polyurea elastomer had an effective gel time of 1.5 seconds with a tack free time of less than 5 seconds. Formulation and elastomer physical properties are described in Table I. The minimum uniform film thickness obtainable was 0,635 mm (25 mils (0.025 inches)). Comparative Example IV Again, for comparison, this Example used a system with the same A-Component (isocyanate quasi-prepolymer component) as described in Example III. The B-component used was a blend of JEFFAMINE T-5000, 27.0 parts; JEFFAMINE D-2000, 27.0 parts; JEFFAMINE T-403, 17.6 parts; and JEFFAMINE D-230, 28.4 parts. These components were mixed at a volume ratio of 1.00 (1.00 weight ratio) using the same spray equipment in Examples I, II, and III. Reactivity of this system was similar to that of Example III. Formulation and elastomer physical properties are mentioned in Table I. The minimum uniform film thickness obtainable was 0,635 mm (25 mils (0.025 inches)). Elastomer Physical Properties for Examples I-IV Example I II III IV Isocyanate quasi-prepolymer m-TMXDI 54.5 54.5 55.0 55.0 JEFFAMINE D-2000 36.4 36.4 45 45 TEXACAR PC 9.1 9.1 - - NCO, % 16.8 16.8 16.6 16.6 Resin blends JEFFAMINE T-5000 24.9 22.8 19.25 27.0 JEFFAMINE D-2000 24.9 22.8 28.87 27.0 JEFFAMINE T-403 18.7 17.1 22.86 17.6 JEFFAMINE D-230 27.4 27.4 22.86 28.4 TiPure R-900 4.1 9.9 6.16 - Processing INDEX 1.05 1.05 1.05 1.05 Iso/Resin vol. ratio 1.00 1.00 1.00 1.00 Effective gel time, sec. 2.0 2.0 1.5 1.5 Tack free, sec. 10 10 <5 <5 Physical Properties Tensile strength, kPa (psi) 8400 (1200) 14245 (2035) 9905 (1415) 8750 (1250) Elongation, % 475 535 400 395 Tear strength, kN/m (pli) 37 (205) 60 (335) 46 (260) 51 (285) Shore D Hardness 35 45 40 42 100% Modulus, kPa (psi) 3675 (525) 5845 (835) 4655 (665) 4445 (635) 300% Modulus, kPa (psi) 5425 (775) 8575 (1225) 7770 (1110) 6615 (945) It may be seen that the physical properties of the elastomers of Examples I and II are the about the same as or improved over the elastomers Comparative Examples III and IV. The elastomers containing propylene carbonate also had improved processing characteristics, as noted. Examples V, VI & VII For additional illustration, three systems were prepared utilizing cycloaliphatic diamine chain extenders as well as the low molecular weight polyetheramines. These Examples used the same isocyanate component given in Examples I and II, above. Formulation and elastomer physical property information is shown in Table II. Elastomer Physical Properties for Examples V-VII Example V VI VII Isocyanate quasi-prepolymer m-TMXDI 54.5 54.5 54.5 JEFFAMINE D-2000 36.4 36.4 36.4 TEXACAR PC 9.1 9.1 9.1 NCO, % 16.8 16.8 16.8 Resin blends JEFFAMINE T-5000 24.0 32.8 25.1 JEFFAMINE D-2000 24.0 32.8 - JEFFAMINE T-403 - - 37.6 JEFFAMINE D-230 19.2 - - VESTAMIN® IPD - 30.3 5.0 XTA-110 - - 28.2 TiPure R-900 4.0 4.1 4.1 Processing INDEX 1.05 1.05 1.05 Iso/Resin vol. ratio 1.00 1.00 1.00 Effective gel time, sec. 2.0 2.0 3.0 Tack free, sec. 10 10 10 Physical Properties Tensile strength, kPa (psi) 6265 (895) 10815 (1545) 9800 (1400) Elongation, % 395 330 170 Tear strength, kN/m (pli) 41 (230) 62 (345) 38 (210) Shore D Hardness 34 41 41 100% Modulus, kPa (psi) 4830 (690) 8785 (1255) 7245 (1035) 300% Modulus, kPa (psi) 5705 (815) 9905 (1415) - Example VIII This Example used an isocyanate component, (A) component, of a blend of AIRTHANE® XACP-722, 45.45 parts; AIRTHANE XACP-504, 45.45 parts; and TEXACAR PC, 9.1 parts. This resulting isocyanate component had a viscosity of 1000 to 1300 cps, as compared to well over 20,000 cps without the TEXACAR PC, making it processable. The (B) component used was a blend of JEFFAMINE T-5000, 35.1 parts; JEFFAMINE D-2000, 52.6 parts, VESTAMIN IPD, 7.2 parts; and TiPure R-900, 5.1 parts. These components were mixed at a volume ratio of 1.00 (1.00 weight ratio) using the same spray equipment mentioned in previous Examples. Formulation and elastomer physical property information are seen in Table III. Elastomer Physical Properties for Example VIII Example VIII Isocyanate quasi-prepolymer AIRTHANE XACP-722 45.45 AIRTHANE XACP-504 45.45 TEXACAR PC 9.1 NCO, % 6.4 Resin blends JEFFAMINE T-5000 35.1 JEFFAMINE D-2000 52.6 VESTAMIN IPD 7.2 TiPure R-900 5.1 Processing INDEX 1.05 Iso/Resin vol. ratio 1.00 Effective gel time, sec. 3.0 Tack free, sec. >1 hr. Physical Properties Tensile strength, kPa (psi) 4830 (690) Elongation, % 300 Tear strength, kN/m (pli) 16 (90) Shore D Hardness 39 100% Modulus, kPa (psi) 2625 (375) 300% Modulus, kPa (psi) 322 (46) Examples IX, X, XI, XII & XIII These Examples illustrate the use of TEXACAR EC-50 in the isocyanate component. The elastomers will be processed as Examples I, II, V, VI and VII. Based on previous experiences, these Examples should exhibit the same characteristics as before. Formulation information is presented in Table IV. Elastomer Physical Properties for Examples IX-XIII Examples IX X XI XII XIII Isocyanate quasi-prepolymer m-TMXDI 54.5 54.5 54.5 54.5 54.5 JEFFAMINE D-2000 36.4 36.4 36.4 36.4 36.4 TEXACAR EC-50 9.1 9.1 9.1 9.1 9.1 NCO, % 16.8 16.8 16.8 16.8 16.8 Resin blends JEFFAMINE T-5000 24.9 24.9 22.8 5.1 5.0 JEFFAMINE D-2000 24.9 - 22.8 58.1 53.6 JEFFAMINE D-4000 - 24.0 - - - JEFFAMINE T-403 18.7 19.2 17.1 - - JEFFAMINE D-230 27.4 28.8 27.4 - - VESTAMIN IPD - - - 26.9 - XTA-100 - - - - 31.5 TiPure R-900 4.1 4.0 9.9 9.9 9.9 Processing INDEX 1.05 1.05 1.05 1.05 1.05 Iso/Resin vol. ratio 1.00 1.00 1.00 1.00 1.00 Examples XIV-XIX These Examples will illustrate the application of the method of this invention to formulations where the isocyanate used in the quasi-prepolymer is an aromatic isocyanate. The results are reported in Table V. Elastomer Physical Properties for Examples XIV-XIX Example XIV XV XVI XVII XVIII XIX Isocyanate quasi-prepolymer RUBINATE® X 9015 100 90 - - - - RUBINATE® X 9009 - - 100 90 - - MONDUR® ML - - - - 55 49.5 TEXOX® PPG-2000 - - - - 45 40.5 TEXACAR PC - 10 - 10 - 10 NCO, % 15.5 14.0 15.5 14.0 16.5 14.8 Resin blends JEFFAMINE D-2000 70.0 70.0 70.0 70.0 70.0 70.0 ETHACURE® 100 30.0 30.0 30.0 30.0 30.0 30.0 Processing INDEX 1.05 0.95 1.05 0.95 1.07 0.98 Iso/Resin vol. ratio 1.00 1.00 1.00 1.00 1.00 1.00 Effective gel time, sec. 2.6 2.9 2.6 3.4 4.4 5.5 Physical Properties Tensile strength, kPa (psi) 17605 (2515) 16275 (2325) 19110 (2730) 15505 (2215) 19810 (2830) 15610 (2230) Elongation, % 240 250 220 230 360 405 Tear strength, kN/m (pli) 78 (435) 70 (390) 87 (485) 71 (395) 89 (500) 83 (465) Shore D Hardness 49 52 49 42 48 51 100% Modulus, kPa (psi) 11665 (1665) 10780 (1540) 12915 (1845) 10710 (1530) 10325 (1475) 8925 (1275) 300% Modulus, kPa (psi) - - - - 16695 (2385) 13055 (1865) From reviewing Table V, it may be seen that the addition of propylene carbonate to systems of Examples XV, XVII and XIX using aromatic polyisocyanates also lengthens the gel time of the system as compared with the elastomers of Examples XIV, XVI and XVIII. The physical properties of the elastomers using propylene carbonate are about the same as those without. Many modifications may be made in the process of this invention without departing from the spirit and scope thereof which are defined only in the appended claims. For example, one skilled in the art may discover that particular combinations of components with the alkylene carbonates or proportions therewith may give polyurea elastomers with advantageous properties. The features disclosed in the foregoing description, in the following claims may, both separately and in any combination thereof, be material for realising the invention in diverse forms thereof. GLOSSARY AIRTHANE® XAPC-504 Isocyanate prepolymer of isophorone diisocyanate and a PTMEG polyol, with an equivalent weight of 504 and a functionality of 2.6, viscosity >40,000 cps. A product of Air Products. AIRTHANE® XAPC-722 Isocyanate prepolymer of isophorone diisocyanate and a PTMEG polyol, with an equivalent weight of 722 and a functionality of 2.0, viscosity >10,000 cps. A product of Air Products. ETHACURE® 100 A diethyltoluenediamine product of Ethyl Corp. JEFFAMINE® D-230 An amine-terminated polyoxypropylene diol of 230 molecular weight available from Huntsman Corporation, used as a chain extender. JEFFAMINE® D-2000 An amine-terminated polyoxypropylene diol of 2000 molecular weight available from Huntsman Corporation. JEFFAMINE® D-4000 An amine-terminated polyoxypropylene diol of 4000 molecular weight available from Huntsman Corporation. JEFFAMINE® T-403 An amine-terminated polyoxypropylene triol of 400 molecular weight available from Huntsman Corporation. JEFFAMINE® T-5000 An amine-terminated polyoxypropylene triol of 5000 molecular weight available from Huntsman Corporation. MONDUR® ML A liquid uretonimine-modified methylenediisocyanate product of Miles, Inc. m-TMXDI® m-Tetramethylxylene diisocyanate from Cytec Industries (American Cyanamid). RUBINATE® X 9009 An aromatic polyisocyanate quasi-prepolymer made by ICI Polyurethanes. RUBINATE® X 9015 An aromatic polyisocyanate quasi-prepolymer made by ICI Polyurethanes. TEXACAR® EC-50 A proprietary blend of ethylene and propylene carbonate from Huntsman Corporation. TEXACAR® PC Propylene carbonate from Huntsman Corporation. TEXOX® PPG-2000 A polypropylene glycol product having a molecular weight of 2000 of Huntsman Corporation. TiPure® R-900 Titanium dioxide available from E. I. du Pont de Nemours, Co. VESTAMIN® IPD Isophorone diamine from Huls America, used as a chain extender. XTA-110 Experimental cycloaliphatic diamine of 194 molecular weight from Huntsman Corporation, used as a chain extender.

Claims: A spray polyurea elastomer prepared from: an (A) component comprising a quasi-prepolymer of an isocyanate, and an active hydrogen-containing material; together with an alkylene carbonate; and a (B) component comprising at least one amine resin. The spray polyurea elastomer of claim 1 where in the (B) component the amine resin is an amine-terminated polyoxyalkylene polyol. The spray polyurea elastomer of claim 1 where the (B) component further comprises an amine resin blend having at least two amine-terminated polyoxyalkylene polyols. The spray polyurea elastomer of claim 1 where in the (A) component the alkylene carbonate has the formula where R 1 and R 2 are independently hydrogen or lower alkyl groups of 1 to 4 carbon atoms. The spray polyurea elastomer of claim 1 where in the (A) component the alkylene carbonate is selected from the group consisting of ethylene carbonate, propylene carbonate, butylene carbonate, dimethyl carbonate and mixtures thereof. The spray polyurea elastomer of claim 1 where the proportion of alkylene carbonate in the (A) component ranges from 1 to 20 % of the (A) component. The spray polyurea elastomer of claim 1 where the proportion of alkylene carbonate in the (A) component ranges from 5 to 15 % of the (A) component. The spray polyurea elastomer of claim 1 where the isocyanate is selected from the group of isocyanates consisting of aliphatic isocyanates selected from the group consisting of methylene diisocyanate, a bifunctional monomer of tetra-alkyl xylene diisocyanate, cyclohexan diisocyanate, 1,12-dodecane diisocyanate, 1,4-tetramethylene diisocyanate, isophorone diisocyanate, and dicyclohexylmethane diisocyanate; aromatic isocyanates selected from the group consisting of m-phenylene diisocyanate, p-phenylene diisocyanate, polymethylene polyphenylisocyanate, 2,4-toluene diisocyanate, 2,6-toluene diisocyanate, dianisidine diisocyanate, bitolylene diisocyanate, naphthalene-1,4-diisocyanate, and diphenylene-4,4'-diisocyanate; and aliphatic/aromatic diisocyanates selected from the group consisting of xylylene-1,3-diisocyanate, bis(4-isocyanatophenyl)methane, bis(3-methyl-4-isocyanatophenyl)methane, and 4,4'-diphenyl-propane diisocyanate; and mixtures thereof. The spray polyurea elastomer of claim 1 where the active hydrogen-containing material is selected from the group consisting of a polyol, a polyoxyalkyleneamine or a combination thereof. The spray polyurea elastomer of claim 9 where the active hydrogen-containing material in the (A) component and the amine-terminated polyoxyalkylene polyol in the (B) component comprise polyether polyols or polyester polyols having an equivalent weight of at least 500. The spray polyurea elastomer of claim 1 where the (B) component additionally comprises an aliphatic, cycloaliphatic or aromatic diamine chain extender. A spray polyurea elastomer of claim 1 wherein the alkylene carbonate is of the formula: where R 1 and R 2 are independently hydrogen or lower alkyl groups of 1 to 4 carbon atoms, where the proportion of alkylene carbonate in the (A) component ranges from 1 to 20 % of the (A) component. The spray polyurea-elastomer of claim 12 where the (B) component further comprises an amine resin blend having at least two amine-terminated polyoxyalkylene polyols. The spray polyurea elastomer of claim 12 where the proportion of alkylene carbonate in the (A) component ranges from 5 to 15 % of the (A) component. The spray polyurea elastomer of claim 12 where the isocyanate is selected from the group of isocyanates consisting of aliphatic isocyanates selected from the group consisting of hexamethylene diisocyanate, a bifunctional monomer of tetraalkyl xylene diisocyanate, cyclohexane diisocyanate, 1,12-dodecane diisocyanate, 1,4-tetramethylene diisocyanate, isophorone diisocyanate, and dicyclohexylmethane diisocyanate, aromatic isocyanates selected from the group consisting of m-phenylene diisocyanate, p-phenylene diisocyanate, polymethylene polyphenylisocyanate, 2,4-toluene diisocyanate, 2,6-toluene diisocyanate, dianisidine diisocyanate, bitolylene diisocyanate, naphthalene-1,4-diisocyanate, and 4,4'-diphenylpropane diisocyanate; and mixtures thereof. The spray polyurea elastomer of claim 15 where the active hydrogen-containing material is selected from the group consisting of a polyol, a polyoxyalkyleneamine or a combination thereof. The spray polyurea elastomer of claim 15 where the active hydrogen-containing material in the (A) component and the amine-terminated polyoxyalkylene polyol in the (B) component comprise polyether polyols or polyester polyols having an equivalent weight of at least 500. The spray polyurea elastomer of claim 17 where the (B) component additionally comprises an aliphatic, cycloaliphatic or aromatic diamine chain extender. A spray polyurea elastomer of claim 1 wherein the alkylene carbonate is selected from the group consisting of ethylene carbonate, propylene carbonate, butylene carbonate, dimethyl carbonate and mixtures thereto, where the proportion of alkylene carbonate in the (A) component ranges from 1 to 20 % of the (A) component, and the (B) component comprises an amine resin blend having at least two amine-terminated polyoxyalkylene polyols, where the volumetric ratio of the (A) component to the (B) component is from 30 to 70 percent of the (A) component to 70 to 30 percent of the (B) component. The spray polyurea elastomer of claim 19 where the active hydrogen-containing material in the (A) component and the amine-terminated polyoxyalkylene polyol in the (B) component comprise polyether polyols or polyester polyols having an equivalent weight of at least 500.

Inventors: PRIMEAUX II DUDLEY JOSEPH, PRIMEAUX II, DUDLEY JOSEPH
Applicants: HUNTSMAN CORP, HUNTSMAN CORPORATION
Application year: 1995
Main classification: C08G18
IPC codes: C08G18, C08K5