AQUEOUS FLUOROPOLYMER EMULSION

Abstract: An aqueous emulsion of fluorine-containing polymer according to the present invention contains an emulsion stabilizer represented by the formula: R-Ph-O-(CH₂CH₂O) n -CH₂CH₂-SO₃M (Ph is a phenyl radical; R is an alkyl radical having 8-12 carbon atoms; n is a number of 1-6; and M is Na, K or NH₄). The resulting emulsion has excellent mechanical stabilities and thermal stabilities as well as decreased possibility of causing ground water contamination.

Description: TECHNICAL FIELD The present invention relates to a novel aqueous emulsion of fluorine-containing polymer having excellent mechanical stability and thermal stability. BACKGROUND ART Aqueous emulsions of polytetrafluoroethylene (hereinafter referred to as PTFE) are prepared by the emulsion-polymerization method disclosed in the U.S. Patent No.2,559,752. Aqueous emulsions of other fluorine-containing polymers are also prepared by using similar process. Aqueous emulsions of fluorine-containing polymer thus prepared have being employed as coating agents e.g. for metals, impregnating agents for fibers and cloths, additives for various materials, and further as dust-preventive treating agents. For adaptation to these uses, the emulsion is generally stabilized with such nonionic surfactants as p-C 8-10 alkylphenylpolyethyleneglycolethers, as the emulsion itself is inferior in mechanical stability. However, even thus stabilized emulsions become unstable against thermal and mechanical actions they encounter during evaporation, concentration, dilution, transportation, weighing and others. It is an object of the present invention to provide an aqueous emulsion of fluorine-containing polymer having excellent mechanical stability. By use of the inventive emulsion, for example, preventions become feasible for such problems caused by inferior mechanical stability as clogging of pumps, valves and nozzles with coagulated colloidal particles of fluorine-containing polymers formed during agitation, transportation and spraying, adhesion of coagulated particles to container walls and agitators, and flotation of coagulated particles in the emulsion. It is another object of the present invention to provide an aqueous emulsion of fluorine-containing polymer having excellent thermal stability. By use of the inventive emulsion, for example, preventions become feasible for such problems caused by inferior thermal stability as deteriorated coating property and impregnation property towards metal, glass woven fabric owing to increased emulsion viscosities under high temperatures. It is a further object of the present invention to provide an aqueous emulsion of fluorine-containing polymer having reduced environmental pollutions especially in the ground water pollution. By use of the inventive emulsion, for example, preventions become feasible for such problems as pollution of ground water caused by emulsion stabilizers in the emulsion occurring when materials treated with PTFE emulsions are used for mixing with soil or filling in the ground for reclamation. Moreover, the inventive emulsion allows concentration by evaporation or dilution thereof, thanks to its increased mechanical and thermal stabilities. DISCLOSURE OF THE INVENTION An aqueous emulsion of fluorine-containing polymer according to the present invention is characterized by that it contains an emulsion stabilizer represented by the formula: R-Ph-O-(CH 2 CH 2 O) n -CH 2 CH 2 -SO 3 M in which Ph is a phenyl radical, R is a C 8 -C 12 alkyl radical, n is a number of 1-6, and M is Na, K or NH 4 . The emulsion stabilizer is added preferably not less than 1 wt% to the polymer. BEST MODE FOR CARRYING OUT THE INVENTION In the present invention, the fluorine-containing polymer includes polymers of tetrafluoroethylene, chlorotrifluoroethylene or vinylidenefluoride, or copolymers containing the aforementioned. Mention is made of the polymers including polytetrafluoroethylene, tetrafluoroethylene·hexafluoropropylene copolymer, tetrafluoroethylene·fluoroalkylvinylether copolymer, tetrafluoroethylene·ethylene copolymer, polychlorotrifluoroethylene, polyvinylidenefluoride and vinylidenefluoride·hexafluoropropylene copolymer. In the present invention, the aqueous emulsion means those containing in water 1-75 wt% of the fluorine-containing polymer in colloidal particles having an average particle size of 0.1-0.3µm. The average particle size of colloidal particles is measured by the centrifugal sedimentation method. In Examples and Comparative Examples of the present invention, the values were measured by use of a centrifugal sedimentation particle size distribution measuring equipment (SA-CP4L; Shimadzu Corp.). As for the emulsion stabilizer, those having the formula R-Ph-O-(CH 2 CH 2 O) n -CH 2 CH 2 -SO 3 M are used. In the formula, Ph denotes a phenyl radical, R denotes an alkyl radical having 8-12 carbon atoms being preferably an octyl radical or a nonyl radical, and n for the oxyethylene radical denotes a number of 1-6 being preferably 1-3. When n is larger than 6, excessive hydrophilic properties decrease the emulsifying efficiency to result in the aqueous emulsion of fluorine-containing polymer having inferior mechanical stability and decreased thermal stabilities caused by enhanced effects of the oxyethylene radical. M is selected from Na, K and NH4 being preferably Na due to the resulting solubility to water. The amount of emulsion stabilizer contained is not less than 1.0wt% per fluorine-containing polymer weight and is preferably in a range of 1.5-5wt%. When the amount added is less than 1.0wt%, the emulsion tends to become unstable. No upper limit exists for the amount to be added, however, over 10wt% is uneconomical and thus less than 5wt% is preferred. The amount of emulsion stabilizer in the present emulsion can be reduced to 1/2-1/3 of the amount of conventional emulsion stabilizer p-nonylphenylpolyethyleneglycolether (EP-A-0 026 932). The mechanical stability of the aqueous emulsion of fluorine-containing polymer can be assessed by observation of increased ratio of apparent sizes of associated colloidal particles resulting from collisions of particles in the emulsion during high speed agitation of the emulsion. Further, under agitation, the colloidal particles coagulate partly to form a coagulum, which may adhere to agitator rotors, vessel walls and others, or isolate from the emulsion as a flock. Under occurrence of these phenomenon, the emulsion is regarded as having an inferior stability, despite of the increase or decrease in size of colloidal particles remaining in the emulsion. In the present invention, the mechanical stability is assessed by increased ratio of particle size measured according to the following method. Into a beaker of 60mm inner diameter is charged 200ml of an emulsion having an average particle size (S 1 ). An agitator (ULTRA-TURRAX; JUNKE & KUNKEL GMBH & Co. KG) having a shaft with a generator is so disposed in the beaker as the shaft is apart by 15mm from the bottom of beaker and deviates by 5mm from the center, and the agitator is operated for 5 minutes under 20,500rpm. The average particle size (S 2 ) of emulsion after being subjected to the agitation is measured, and the increased ratio of particle size is calculated according to the following formula: Increased ratio of particle size (%) = (S 2 -S 1 )/S 1 × 100 The mechanical stability is rated under the following standard: Good: Increased ratio of particle size is >0% - <5%; Fair: Increased ratio of particle size is ≥5% - <10%; and Poor: Increased ratio of particle size is ≥10%. In addition to the above, Poor is rated when a large amount of coagulated matter is formed by the agitation. Viscosity of the aqueous emulsion increases in accordance with increase in the temperature of emulsion. Unfavorable emulsions show sharp increase in viscosity at temperatures the emulsion encounter when stored in summer, during usages or concentration by evaporation. In the Example and Comparative Example of the present invention, the viscosity was measured at 20-60°C for aqueous emulsions containing about 60wt% fluorine-containing polymer by use of a B-Type viscometer (Type BL; Tokyo Keiki). Emulsions showing vigorous increases in viscosity at 30-60°C are recognized as having poor thermal stability. [Examples 1, 2 and Comparative Example 1] To aqueous emulsions containing about 45wt% PTFE prepared by the controlled emulsion polymerization method (the emulsion is hereinafter referred to as feed stock) were added respectively 2.2wt% per PTFE of the emulsion stabilizers mentioned in Table 1. Under gentle agitation, water was added to obtain aqueous emulsions A, B and C containing about 30wt% PTFE. Sample Kind of Emulsion Stabilizer A C 8 H 17 -Ph-O-CH 2 CH 2 O-CH 2 CH 2 SO 3 Na B C 8 H 17 -Ph-O-(CH 2 CH 2 O) 2 -CH 2 CH 2 SO 3 Na C C 9 H 19 -Ph-O-(CH 2 CH 2 O) 9 -CH 2 CH 2 OH Mechanical stability test: The increased ratio of particle size measured with the aforementioned method for Samples A, B and C is shown in Table 2. By comparison with Sample C (Comparative Example 1) using the conventional emulsion stabilizer p-nonylphenylpolylethyleneglycolether, Sample A (Example 1) and Sample B (Example 2) added with the emulsion stabilizer of the present invention showed better mechanical stability. Example Sample Average Particle Size, before Agitation Average Particle Size, after Agitation Increased Ratio of Particle Size Mechanical Stability Example 1 A 0.261µm 0.265µm 1.5% Good Example 2 B 0.261µm 0.263µm 0.8% Good Comparative Example 1 C 0.247µm 0.279µm 13.0% Poor [Example 3 and Comparative Examples 2 and 3] Evaporating concentration test: Samples D, E and F were prepared by adding to the feed stock respectively 3.5wt% per PTFE weight of the emulsion stabilizer shown in Table 3. The sample was subject to evaporating concentration under atmospheric pressure in a round bottom flask put on a 150W mantle heater. Sample D (Example 3) was concentrated to obtain a 60wt% PTFE aqueous emulsion though bubbling occurred. Sample E (Comparative Example 2) was impossible to be concentrated due to formation of a large amount of agglomerate. Sample F (Comparative Example 3) was impossible to be concentrated due to occurrence of vigorous bubbling. Sample Kind of Emulsion Stabilizer D C 8 H 17 -Ph-O-(CH 2 CH 2 O) 2 -CH 2 CH 2 SO 3 Na E C 9 H 19 -Ph-O-(CH 2 CH 2 O) 9 -CH 2 CH 2 OH F C 9 H 19 -Ph-SO 3 Na [Example 4 and Comparative Example 4] Thermal stability test: The thermal stability test was conducted against a 60wt% PTFE aqueous emulsion obtained in Example 3 as Sample D (Example 4) and a 60wt% PTFE aqueous emulsion Sample G (Comparative Example 4) prepared by use of 6.1wt% per PTFE of p-nonylphenylpolyethyleneglycolether (n=9) and concentration method according to the U.S. Patent No.3,037,953. The result obtained is shown in Table 4. The viscosity of Sample D increased gradually in accordance with increase in temperature, but that of Sample G increased rapidly between 40°C and 60°C. Example No. Sample Viscosity cP Thermal Stability 20°C 30°C 40°C 50°C 60°C Example 4 D 21.5 25.5 25.5 31.5 34.0 Good Comparative Example 4 G 22.5 21.5 22.5 56.0 97.0 Poor [Example 5 and Comparative Example 5] Environmental pollution test: Sample B and Sample C each were diluted with pure water to adjust the concentration of emulsion stabilizer in the emulsion to 100ppm. Into a 200ml beaker was placed 50ml of the diluted Sample, 5g of Ca(OH) 2 was added, agitated slowly for 1 hour with a 4cm magnetic stirrer, decanted and the concentration of emulsion stabilizer in the supernatant liquid was measured. The concentration of emulsion stabilizer in the supernatant liquid of Sample B (Example 5) was 0, but that of Sample C (Comparative Example 5) was 1000ppm. INDUSTRIAL APPLICATION An aqueous emulsion of fluorine-containing polymer according to the present invention has superior mechanical stability and thermal stability as well as decreased possibility of causing ground water pollution in comparison with those emulsions using a conventional emulsion stabilizer p-nonylphenylpolyethyleneglycolether.

Claims: An aqueous emulsion containing in water 1-75 wt% of a fluorine-containing polymer in colloidal particles having an average particle size of 0.1-0.3 µm and an emulsion stabilizer amounting not less than 1 wt% relative to the fluorine-containing polymer, wherein said emulsion stabilizer being represented by the formula: R-Ph-O-(CH 2 CH 2 O) n -CH 2 CH 2 -SO 3 M in which Ph is a phenyl radical, R is an alkyl radical having 8-12 carbon atoms, n is a number of 1-6, and M is Na, K or NH4. An aqueous emulsion of the fluorine-containing polymer according to claim 1, in which said emulsion stabilizer amounting 1.5-5 wt% relative to the fluorine-containing polymer.

Inventors: CHIBA SHIZUO, OGURA MASATSUNE, CHIBA, SHIZUO, OGURA, MASATSUNE
Applicants: MITSUI DU PONT FLUORCHEMICAL, DU PONT-MITSUI FLUOROCHEMICALS CO., LTD
Application year: 1995
Main classification: C08F6
IPC codes: C08L27, B01F17, C08K5, C09D127