BONDED BODY OF ALUMINUM AND SILICON NITRIDE AND PRODUCTION METHOD THEREOF

Abstract: A bonded body of aluminum and silicon nitride firmly bonded to each other which is produced economically, and a light-weight component having an excellent lubrication characteristic as a mechanical component of an internal combustion engine of an automobile. The bonded body includes a base consisting of aluminum as its principal component and a member comprising a silicon nitride sintered body bonded substantially directly to the base. A base material (2) in a powder or bulk form containing aluminum as the principal component and a member (1) comprising a silicon nitride sintered body are put into a mold and are heated under pressure to mutually bond them.

Description: SPECIFICATION Technical Field The present invention relates to a joint body of aluminum and silicon nitride and a method of preparing the same, and more particularly, it relates to a joint body having a base material of aluminum, which is excellent in sliding property employable as a machine part and a method of preparing the same. Background Technique In recent years, attention is drawn to global environmental problems such as those of exhaust gas, disruption of the ozone layer and the like, and it is urgently necessary to improve energy efficiency in an internal combustion engine of an automobile or the like. As one of methods of improving energy efficiency, lightening of parts forming the internal combustion engine is studied. Namely, replacement of parts which have generally been prepared from iron group metals with aluminum group parts is studied. However, aluminum group materials are generally inferior in sliding property, and hence it is necessary to partially prepare the aluminum group parts from ceramics which is further superior in wear resistance. A number of materials are known as ceramics, as shown in Table 1. As a material which is excellent in sliding property and comprises necessary characteristics such as strength and toughness as a machine part without damaging the advantage of lightweightness of the aluminum group material, silicon nitride is most promising. Therefore, methods of joining aluminum group materials with silicon nitride sintered bodies have been studied in various fields. Material Specific Gravity Strength Toughness Slidability Cost Si 3 N 4 ○ ○ ○ ○ ○ SiC ○ × × ○ ○ AlN ○ × × × ○ Al 2 O 3 × × × ○ ○ ZrO 2 × ○ o ○ × ○ mullite × × ○ × ○ B 4 C o ○ × × ○ × For example, Japanese Patent Laying-Open No. 6-172052 discloses a method of engaging a ceramics part with an aluminum group material. According to such a mechanical joining method, there is such a problem that the joined members are separated by a load from the exterior since the joining strength is generally small. Further, there has been such a problem that a clearance is defined between the engaged portions in temperature rise due to the difference between the thermal expansion coefficients (that of ceramics is smaller in most case) between the ceramics part and the aluminum group material and the separation is further enlarged, while the ceramics part is displaced with respect to the aluminum group material and positional accuracy cannot be ensured. In order to solve such problems, formation of chemical bonding between the ceramics and the aluminum group material has been studied. As the most general method of joining ceramics with a metal, there is a method of metallizing a surface of ceramics by the so-called Mo-Mn method and thereafter brazing the same with a brazing material of a noble metal, or a method of performing brazing by the so-called active metal brazing material which is prepared by adding an active metal such as titanium (Ti) to a noble metal brazing material for improving reactivity with ceramics while omitting metallization. Both of these methods cannot be applied to aluminum group materials having low melting points, since it is necessary to perform heating to high temperatures of at least 700°C. On the other hand, joining by the so-called solder which is melted at a lower temperature is also conceivable. According to this method, however, it is difficult to remove a strong oxide film from a surface of an aluminum group material, and it has been impossible to join ceramics and an aluminum group material with each other. Due to such a technical background, Japanese Patent Laying-Open No. 61-209965, for example, discloses a method of arranging a metal (Fe, Co, Ni, Pt or the like) having high reactivity on a surface of a silicon nitride sintered body, metallizing the same preferably in a vacuum atmosphere of at least 1200°C, thereafter bringing the same into contact with aluminum or its alloy, and heating and joining the same at a temperature below its eutectic temperature. However, there has been such a problem that this method leads to increase of the preparation cost since this metallization step includes troublesome treatments such as application of the metal and a high temperature treatment in the vacuum. As a method of improving wear resistance of a metal surface, ceramic coating by CVD or PVD is conceivable. According to such a method, however, there have been such problems that the coating layer is separated, and that the rigidity of the coating surface is insufficient when a base material is prepared from an aluminum group material. As hereinabove described, it has been difficult to join a member consisting of silicon nitride to a base material or a backing which is mainly composed of aluminum by the prior art (see also EP-A-153 150). Accordingly, an object of the present invention is to solve the aforementioned problems, as well as to provide a joint body in which a base material mainly composed of aluminum and a member consisting of a silicon nitride sintered body are strongly joined with each other at a low cost. Disclosure of the Invention In the present invention, a joint body of aluminum and silicon nitride, and a method of preparing the same are provided in order to solve the aforementioned problems, as described in the following (1) to (20): (1) The joint body comprises a base material which is mainly composed of aluminum and a member consisting of a silicon nitride sintered body which is substantially directly joined to the base material. Here, "substantially" means that no intermediate layer is positively introduced between the base material mainly composed of aluminum and the member consisting of a silicon nitride sintered body. For example, a coating layer of another element (Ti, Ni, Fe or the like) or a plate member thereof is not interposed on the interface between the base material and the member. Further, no adhesive or the like is employed at the interface. A surface oxide layer resulting from a heat treatment of the silicon nitride sintered body is present on the interface, however, the base material and the member are regarded as being substantially directly joined with each other. (2) The base material is made of a pure aluminum metal, an aluminum alloy, or an aluminum group composite material (for example, that reinforced with whiskers, that in which ceramics is dispersed or the like). (3) On the other hand, a sintered body containing silicon (Si) which is not bonded with nitrogen (N) may be employed for the overall sintered body as the silicon nitride sintered body forming the member, depending on the application of the joint body according to the present invention. (4) The interface on which the base material mainly composed of aluminum and the member consisting of a silicon nitride sintered body are substantially directly joined with each other consists of a layer containing oxygen which is mainly bonded with silicon (Si). (5) Particularly when the silicon nitride sintered body of the above (3) is employed, a layer containing silicon (Si) or a silicon (Si) compound is formed in the vicinity of the joining interface between the base material and member, since silicon (si) is diffused on the aluminum side. In order to prepare the aforementioned joint body of the present invention, the following preparation method is employed: (6) A powdery or bulky base material which is mainly composed of aluminum and a member consisting of a silicon nitride sintered body, which has been heated/oxidized in accordance with claim 4, are charged in a mold and heated under pressurization, thereby joining the base material and the member with each other. (7) The mold preferably has a thermal expansion coefficient of at least 0 and not more than 7 x 10 -6 K -1 . That having a thermal expansion coefficient of 0 includes a C-C composite. In this case, the thermal expansion coefficient is substantially zeroed in specific crystal orientation in the C-C composite, and design of the mold making the best use of this directivity is possible. (8) The mold preferably has a shape which is close to a final product at need. (9) As to the material for the mold, it is preferable to employ a mold having conductivity allowing rapid heating by energization. Here, conductivity means exhibition of no insulation property as a principal characteristic, and preferably the resistivity is not more than 10 3 Ω·cm. (10) While joining is performed with the aforementioned mold, it is preferable to prepare a number of molds, simultaneously perform treatments of a number of sets of base materials and members, and continuously carry out a cycle of supply to the molds, joining and removal in constant rhythm as a production system of the joining, in order to improve productivity. It is also possible to combine these in response to the situation. Namely, a joining mold or a joining holder capable of simultaneously treating a plurality of sets of base materials and members may be employed. As heating conditions for the joining, the following are preferable: (11) As to the heating time, a holding time at the maximum temperature is preferably set within 10 minutes. Further, the temperature of heating is preferably set at 500 to 800°C.The following methods are preferable as the heating system: (12) A heating method utilizing a plasma. (13) A method of heating by an induced current. (14) A method of heating by a microwave. (15) In case of employing the heating means of the above (13) and (14), it is more preferable to heat only the base material mainly composed of aluminum in particular. In the aforementioned heating means of the above (12) to (14), the heating is performed by energizing both or either of the joined bodies and feeding some energization current.As another method of preparing the joint body of the above (1) to (5), the following one can be listed. (16) The base material mainly composed of aluminum and the member consisting of a silicon nitride sintered body are arranged in a joining mold or a joining holder, so that sintering of the base material and joining of the base material and the member are simultaneously performed by hot forging. As to a supply form of the base material mainly composed of aluminum in the mold in this case, powder or a powder compact is employed. The forging temperature is preferably set at 550 to 650°C.Further, the following preparation method can be listed in addition to the aforementioned forging: (17) It is also possible to arrange the member consisting of a silicon nitride sintered body in a joining mold or a joining holder and supply the base material mainly composed aluminum in the joining mold or the joining holder in the form of a molten metal, for simultaneously performing molding and joining. As described above, first there is the preparation method of the above (6) as a method of preparing the joint body of the above (1) to (5), there is that of the above (7) to (15) as means therefor, and there are the methods of the above (16) and (17) as other methods for similarly preparing the joint body of the said (1) to (5).In the present invention, further, it is proper to employ the following one separately from that of the above (3) as the member consisting of a silicon nitride sintered body of the joined body which is supplied to the preparation methods of (6), (16) and (17): (18) That obtained by previously heat treating a silicon nitride sintered body at a temperature of at least 800°C and less than 1200°C is employed. It is assumed that the atmosphere of the heat treatment is an atmosphere containing oxygen. (19) The heat treatment is performed in an atmosphere containing oxygen. (20) A silicon nitride sintered body having an as-sintered surface is employed as such. The joint body according to the present invention is formed by a base material mainly composed of aluminum and a member consisting of a silicon nitride sintered body which is substantially directly joined to the base material as described in the above (1), dissimilarly to a conventional joint body of the same combination. In the joint body of the present invention, the base material and the member are directly joined with each other, whereby preparation of an intermediate layer, an operation of inserting the intermediate layer and the like can be omitted, and reduction of the preparation cost can be attained. Since the base material and the member are directly joined with each other, further, deterioration of the characteristics of the base material and the member on the joining interface caused by the intermediate layer and occurrence of joining defects on the interface can be avoided. Thus, according to the joint body of the present invention, a complex of aluminum and silicon nitride having higher reliability can be provided. As the material for the joined base material, various ones can be listed in response to changes of the application and use conditions. Among the same, a pure aluminum metal, an aluminum alloy or an aluminum group composite material is mainly employed as the material mainly composed of aluminum, as described in the above (2). The reasons for particularly employing the aluminum group composite material among these are enumerated as follows: For example, an aluminum group composite material containing silicon (Si) is employed in case of requiring higher rigidity and wear resistance. On the other hand, an aluminum group composite material in which whiskers of a metal or ceramics are dispersed is employed in case of requiring higher strength and toughness. Further, an aluminum group composite material in which ceramics hard grains are dispersed is employed in case of requiring wear resistance. An ingot material or a material which is prepared by powder metallurgy is employed as the base material. Selection of a method of preparing such a base material is properly performed in response to changes of the application and use conditions. The silicon nitride sintered body forming the member in the joint body according to the present invention can also be properly selected in response to the application. First, a silicon nitride sintered body obtained by performing nitriding reaction sintering from the so-called raw material mainly composed of silicon, in which the overall sintered body partially contains silicon (Si) not bonded with nitrogen (N) as described in the above (3), in order to increase joining strength. When such a silicon nitride sintered body is employed, a layer containing silicon (Si) or a silicon (Si) compound is formed in the vicinity of the joining interface by pressurization heating joining of the base material and the member, as described in the above (5). Thus, the joining strength of the joining interface is improved. Fig. 3 shows an example of an elemental analysis result of a section in the case, as explained in Example 7 described later. In order to improve the joining strength, the joining interface is formed by a layer containing oxygen (O) which is mainly bonded with silicon (Si), as described in the above (4). It is understood that oxygen is locally present on the joining interface when oxygen is present in a portion on the side of the base material mainly composed of aluminum or the side of the member consisting of a silicon nitride sintered body forming the interface in this case, as an elemental analysis result of a section of Fig. 2 explained in Example 3 described later. Thus, the joining strength of the joining interface is improved. While it is conceivable that the joining interface in which oxygen is locally present is formed as shown in Fig. 2 as a result of oxygen supply from a surface on the side of the base material mainly composed of aluminum, that resulting from the fact that oxygen is supplied from a surface of the member consisting of a silicon nitride sintered body is preferential. When a silicon nitride sintered body which is obtained by nitriding reaction sintering is employed as the base material as hereinabove described, the joining strength is further increased as compared with the case of employing another silicon nitride sintered body, since a diffusion layer containing silicon or a silicon compound is formed on the joining interface. In such a reaction-sintered silicon nitride sintered body, however, merely that having bending strength of about 600 MPa is obtained at present in an ordinary one. When it is employed as a member requiring higher bending strength, therefore, there is such a restriction that the joint body of the present invention cannot be utilized even-if the joining strength is high. In application requiring high strength, therefore, a silicon nitride sintered body containing no silicon which is not bonded with nitrogen is employed for the member of the inventive joint body. It is preferable to employ a silicon nitride sintered body having bending strength of at least 1200 MPa at room temperature, when the same is utilized as a member which is employed under severe conditions requiring high wear resistance, bending strength and fatigue characteristics in particular. The method of preparing the joint body according to the present invention is now described. As described in the above (6), the base material mainly composed of aluminum and the member consisting of a silicon nitride sintered body are charged in the mold and heated under pressurization, so that the both are joined with each other. The material forming the base material mainly composed of aluminum may be either powdery or bulky. As to this selection, the most appropriate low-priced supply form may be considered depending on the type of the material forming the base material. When the material forming the base material is an ingot material, for example, a bulky one is employed. In case of employing an aluminum-silicon alloy having a silicon content of at least 20 weight % as the base material, it is economically advantageous to prepare the same in the form of atomized powder. In case of employing an aluminum group composite material in which whiskers are dispersed or an aluminum group composite material in which grains of hard ceramics are dispersed as the material for the base material, each raw material may be supplied to be sintered simultaneously with joining, or a bulky one may be previously formed to be thereafter supplied into the mold. The silicon nitride sintered body is previously arranged in the joining mold, thereafter the base material mainly composed of aluminum is charged in the mold in any form of the aforementioned ones, and pressurized/heat treated under conditions for obtaining a joint body having characteristics in consideration of a desired shape and application, so that the base material and the member are joined with each other. As to the mold employed in the preparation method of the present invention, the thermal expansion coefficient of the mold is preferably at least 0 and not more than 7 x 10 -6 K -1 , as described in the above (7). When a mold having a thermal expansion coefficient of less than 0 (i.e., negative) is employed, the mold may be broken by expansion of the silicon nitride sintered body in heating. If the thermal expansion coefficient of the mold exceeds 7 x 10 -6 K -1 , on the other hand, it may be difficult to remove the joint body or the mold may be damaged by removal of the joint body since the mold contracts when the same is cooled after joining. As to the shape of the mold, further, the working margin in later working can be reduced by employing that of a shape which is close to the shape of a final product as described in the above (8), whereby the preparation yield can be improved. Depending on the application, further, the later working can be omitted if the dimensional accuracy of the prepared joint body is within a desired range. It is not necessarily an indispensable condition that the mold has conductivity, depending on the heating system. In an external heating system of heating the mold from its outer periphery, for example, it is not necessary to employ a conductive (for example, a semiconductor or a conductor having resistivity of not more than 10 3 Ω·cm) one. In the external heating system, the member consisting of a silicon nitride sintered body and the base material mainly composed of aluminum are directly joined with each other regardless of conductivity of the mold, and a joint body having prescribed joining strength can be obtained. The heating time is not necessarily restricted either, if the base material and the member are similarly directly joined with each other and prescribed joining strength is attained. As a more preferable method of producing the inventive joint body in high efficiency at a low cost, however, it is necessary to employ the joining mold having conductivity which is described in the above (9), in order to carry out a joining method with a holding time of within 10 minutes at the maximum temperature described in the above (11), i.e., a preparation method having high productivity, by any system of the plasma heating, the induced current heating and the microwave heating described in the above (12) to (14). In the method of preparing a joint body according to the present invention, it is preferable to employ a mass production system in coincidence with a joining lead time while properly controlling the same in connection with precedent and subsequent steps as described in the above (10), in order to attain high productivity. Particularly when a conductive mold is used and heating means of any of the plasma heating, the induced current heating and the microwave heating having high efficiency is employed, it is possible to form the aforementioned production system also in the condition that the holding time at the maximum temperature is within 10 minutes. The heating temperature is preferably at least 500°C and not more than 800°C. This is because shape working of the heated base material mainly composed of aluminum is difficult if the temperature is less than 500°C. This is also because aluminum is evaporated to cause modification or a defect of the base material if the temperature is at least the melting temperature of aluminum and exceeds 800°C. In case of preparing the joint body with a heating/holding time within 10 minutes with a conductive mold, the systems of the aforementioned (12) to (14) can be employed as the heating means. In the plasma heating, a plasma is generated on the joining interface by energization, and cleaning of the surface is performed. Thus, a dense diffusion layer of silicon or a localized layer of oxygen can be formed in a short time. In the induction heating, each of heating of the overall mold and heating of only the joined materials is possible through selection of the type of the mold. Also in the induction heating, a dense joining interface can be formed in a short time similarly to the plasma heating. The microwave heating can also attain an effect similar to that of the induction heating. In the aforementioned heating system, it is preferable to heat only the base material mainly composed of aluminum which is a conductive joined portion, as described in the above (15). According to such heating, more rapid heating with excellent thermal efficiency can be performed. While the preparation method described above is a method of arranging the member and the base material in the joining mold and heating/pressurizing the same, it is also possible to join the same by hot forging as application means thereof, as described in the above (16). The forging temperature in this case is preferably rendered at least 550°C and not more than 650°C. If the temperature is less than 550°C, densification by plastic deformation of the base material mainly composed of aluminum itself is difficult. If the temperature exceeds 650°C, softening of the base material mainly composed of aluminum so intensifies that shape accuracy is deteriorated. Alternatively to the aforementioned preparation method, further, a method of arranging a silicon nitride sintered body in a joining mold or a joining holder and casting the same while supplying the member mainly composed of aluminum in the form of a molten metal for molding the same simultaneously with joining, as described in the above (17). In this case, a holding time of the casting and a cooling time are properly controlled by employing the aforementioned various silicon nitride sintered bodies or a previously pretreated silicon nitride sintered body. Thus, it is possible to obtain a joint body in which the base material mainly composed of aluminum and the silicon nitride sintered body are directly joined with each other on the joining interface. In order to improve the strength of the joining interface of the inventive joint body, further, the following treatment is previously performed on the silicon nitride sintered body: As described in the above (18), the silicon nitride sintered body is heat treated at a temperature of at least 800°C and less than 1200°C so that its surface is previously modified, before the member consisting of the silicon nitride sintered body is joined to the base material mainly composed of aluminum. In the joint body according to the present invention, a layer in which at least oxygen is localized is formed on the joining interface as described above. This oxygen component may be supplied from the surface on the side of the base material mainly composed of aluminum as described above, while most part thereof is supplied from the surface of the member consisting of the silicon nitride sintered body. The heat treatment described in the above (18) is performed as means for sufficiently ensuring the oxygen quantity of the oxygen localized layer. When this heat treatment is performed, the joining strength can be improved as compared with that of an untreated one. This is because a component of a sintering aid mainly composed of an oxide on its surface surfaces on the joining surface of the silicon nitride sintered body, to form a surface which is rich in the oxygen component. As described in the above (19), silicon dioxide (SiO 2 ) is positively formed on the surface of the joining interface by preparing the atmosphere of the heat treatment from an oxygen-containing atmosphere. The temperature is rendered at least 800°C and less than 1200°C in the aforementioned heat treatment since oxidization of silicon nitride does not proceed if the temperature is less than 800°C, while surface oxidation of silicon nitride excessively proceeds and the characteristics of silicon nitride are deteriorated if the temperature is 1200°C or exceeds 1200°C. While there is also a method of finishing the joining surface as a state of the member consisting of a silicon nitride sintered body before joining as described in the above (20), the member may alternatively be prepared in a state of sintered surface (in an unmachined state) if it is not necessary to dare to finish the surface of the sintered body. Thus, the preparation cost can be suppressed low. The heat treatment described in the above (18) or (19) may be previously performed on the silicon nitride sintered body having this as-sintered surface. Brief Description of the Drawings Fig. 1 is a sectional view showing an example of a joining mold employed in Example of the present invention. Fig. 2 is a diagram showing an analytical result of element distribution of a joining interface in a joint body according to the present invention. Fig. 3 is a diagram showing an analytical result of element distribution of a joining interface in a joint body according to another Example of the present invention. Fig. 4 is a sectional view showing another embodiment of a mold employed for preparing the inventive joint body. Fig. 5 is a diagram showing a joint body obtained through the joining mold shown in Fig. 4. Best Mode for Carrying Out the Invention While Examples of the present invention are now described, the present invention is not in any way restricted by these Examples. Example 1 A silicon nitride sintered body consisting of a rectangular parallelopiped of 6 mm x 6 mm x 3 mm, and aluminum powder of 99 % in purity were set in a mold of carbon as shown in Fig. 1. A square surface of 6 mm x 6 mm was employed as a joining surface. As the silicon nitride sintered body, that prepared with addition of Y 2 O 3 of 5 weight % - Al 2 O 3 of 3 weight % as a sintering aid was employed. Bending strength of the silicon nitride sintered body at the room temperature was 1300 MPa (three-point bending strength in accordance with JISR1601). The surface of the silicon nitride sintered body was ground. The silicon nitride sintered body and the aluminum powder were charged as shown in Fig. 1. The silicon nitride sintered body 1 was set on a mold 3 which was arranged in a mold 4. The aluminum powder 2 was charged on this silicon nitride sintered body 1. A rod 5 was placed on the aluminum powder 2. The charging height of the aluminum powder in the mold was 18 mm. This mold of carbon was set in a furnace capable of mechanical pressurization and rapid heating with a pulsative current, heated to 670°C in a vacuum with application of a load of 200 kg, and held for 2 minutes. The temperature rise time was 4 minutes, and the cooling time was 15 minutes. The pulsative current was employed for generating a plasma. While aluminum estimated as being melted was slightly recognized in the clearance between the mold of carbon and the rod of carbon, most aluminum remained, and a joint body of silicon nitride and aluminum was obtained. The side surface of the joint body was ground to remove aluminum adhering to the side surface, thereby preparing a test piece for measurement of shearing strength. No crack resulting from thermal stress, which is generally recognized in joining, was recognized on the joint body. An aluminum portion of this joint body was fixed to measure shearing strength, which was 210 MPa, and it has been proved that excellent joining is formed. Example 2 Joining and evaluation were performed in a method similar to Example 1, except that an aluminum bulk (99 % in purity) of a cube of 6 mm each side was employed in place of the aluminum powder in Example 1. An excellent joint body was similarly obtained, and its shearing strength was 170 MPa. Example 3 Samples of the silicon nitride sintered body after grinding were heat treated under conditions (atmospheres and temperatures) shown in Table 2 for 1 hour in Example 1, and joining and evaluation were performed under conditions similar to those of Example 1, to obtain results shown in Table 2. The pressure of a vacuum atmosphere was 10 -2 torr, and every one of other gases was set at 1 atm. Heat Treatment Result Atmosphere Temperature (°C) Crack Shearing Strength (MPa) untreated no 170 vacuum 1100 no 190 argon 1200 no 180 nitrogen 700 no 170 nitrogen 800 no 180 nitrogen 900 no 200 nitrogen 1000 no 220 nitrogen 1100 no 230 nitrogen 1200 no 210 nitrogen 1300 no 170 atmosphere 700 no 180 atmosphere 800 no 250 atmosphere 900 no 280 atmosphere 1000 no 290 atmosphere 1100 no 260 atmosphere 1200 no 170 atmosphere 1300 no 120 A joint body employing a silicon nitride sintered body which was heat treated in the atmosphere at 1000°C was cut perpendicularly to its joining surface, for investigating the distribution situation of elements in the vicinity of the joining surface with EPMA. The result is shown in Fig. 2. As shown in Fig. 2, it has been proved that a layer having high oxygen concentration was present on the joining interface. Example 4 In place of the machined silicon nitride sintered body employed in Example 1, samples which were prepared by heat treating this sintered body in the atmosphere at 1000°C for 1 hour were employed, while rapidly solidified aluminum alloy powder containing silicon by 20 weight % was employed in place of the aluminum powder of 99 % in purity. Joining conditions were performed under conditions shown in Table 3. Results of evaluation of joint bodies of silicon nitride and the aluminum alloy thus obtained are also shown in Table 3. Joining Condition Result Temperature (°C) Holding Time (min.) Crack Shearing Strength (MPa) 400 2 no not joined 500 2 no 150 550 2 no 170 600 2 no 200 660 2 no 330 700 2 no 310 660 1 no 300 660 3 no 350 660 5 no 320 660 10 no 260 660 20 no 220 Example 5 An as-sintered sample was employed in place of the heat treated silicon nitride sintered body in Example 4, and joining and evaluation were performed under conditions similar to those of Example 1. An excellent joint body was obtained, and its joining strength was 180 MPa. Example 6 The heat treated silicon nitride sintered bodies and the aluminum alloy powder employed in Example 4 were set in molds of.materials shown in Table 4. These were joined by heating methods joining conditions (temperatures and applied loads) shown in Table 4, and evaluation thereof was performed. The results of the evaluation are shown in Table 4. In order to prevent adhesion of the molds and the samples, the inner walls of the molds were wrapped up with sheets of carbon before charging the samples. Mold material Heating Method Joining Condition Result Temperature (°C) Load (kg) Holding Time (min.) Crack Shearing Strength (MPa) WC high frequency induction 680 200 2 no 320 Si 3 N 4 high frequency induction 680 200 2 no 330 C dc energination 680 200 2 no 260 steel dc energination 680 200 2 no 280 Si 3 N 4 microwave 680 200 2 no 320 It is estimated that the heating was performed by induction heating of aluminum in the case of using the mold of silicon nitride in an induction furnace among the combinations of the mold materials and the heating methods shown in Table 4. When a mold of steel having a high thermal expansion coefficient was used, it was difficult to take out the joint body by contraction after cooling. Example 7 A silicon nitride sintered body (the bending strength of the sintered body was 550 MPa) containing silicon not bonded with nitrogen by 2 weight % was employed in place of the silicon nitride sintered body in Example 1, and a joint body was prepared under the same conditions as those of Example 1. However, the cooling time was set at 1 hour, in consideration of relaxation of thermal stress. No crack was observed in the obtained joint body, and its joining strength was 210 MPa. A sample of the obtained joint body was cut perpendicularly to its joining surface, and element distribution around the joining surface was measured. As shown in Fig. 3, a region in which silicon was gradually diffused toward the aluminum side was recognized, and it is estimated that this contributed to improvement of the joining strength. Example 8 The silicon nitride sintered body heat treated in the atmosphere at 1000°C for 1 hour, which was employed in Example 3, and aluminum powder of 99 % in purity were set in a mold of alumina, as shown in Fig. 1. In order to prevent adhesion of the mold and the sample, a carbon sheet was interposed between the mold and the sample. This mold was set in the so-called hot press furnace having a carbon heater (external heating type), and heated to 660°C with application of a load of 200 kg in a vacuum. The time required for temperature rise was 30 minutes. Holding times were set at 5 minutes, 20 minutes and 60 minutes. After cooling, a joint body having no defect such as a crack was obtained. Shearing strength values similar to that in Example 1 were measured, which were 310 MPa, 200 MPa and 150 MPa respectively with respect to the holding times. Example 9 A sample of a silicon nitride sintered body which was prepared by grinding the same material as the silicon nitride sintered body employed in Example 1 into a shape of 25 mm in diameter and 3 mm in thickness and thereafter heat treating the same in the atmosphere at 900°C for 1 hour, and rapidly solidified aluminum alloy powder containing silicon by 25 weight % were set as shown in Fig. 4. As shown in Fig. 4, these were heated by a pulsative current in an argon atmosphere with application of a load of 5 tons with a rod 6 of carbon having a convex shape, and held for 2 minutes. Holding temperatures were set at 620°C and 680°C. A joint body of a shape shown in Fig. 5 was obtained at either holding temperature. As shown in Fig. 5, the aluminum alloy 7 is joined to the silicon nitride sintered body 1. No defect such as a crack was observed in the joint body. Example 10 A mold of carbon having holes in three portions capable of simultaneously setting three samples of the same shape as Example 9 was used to simultaneously perform joining with three rods of carbon having the same shape. Joining conditions were identical to those in Example 9, except that the applied load was changed to 15 tons. Three excellent joint bodies were simultaneously obtained. Example 11 A sample of a silicon nitride sintered body which was prepared by grinding the same material as the silicon nitride sintered body employed in Example 1 into a rectangular parallelopiped of 15 mm x 15 mm x 3 mm and thereafter heat treating the same in the atmosphere at 900°C for 1 hour was set in a mold of carbon having the shape of a rocker arm of a mobile engine. The mold was preheated to 300°C, and thereafter a molten metal of an aluminum alloy containing silicon by 15 weight % was fed from an upper portion of the mold and pressurized at 5 atm. until the same was solidified. The sample was taken out by decomposing the mold, whereby a rocker arm in which the silicon nitride sintered body was joined to a sliding part was obtained. A sample of the same shape as Example 1 was prepared by the same method and subjected to measurement of shearing strength, which was 320 MPa. The obtained rocker arm was employed to perform an engine rotation test. An acceleration test by high speed rotation was executed for 120 hours by employing lubrication oil in which soot was mixed. In the rocker arm after the test, no breakage was observed in the joined part and other portions. Abrasion loss of the sliding surface was 5 µm. In a rocker arm having a sliding surface made of a sintered alloy (Cr-Mo steel), which is mainly employed at present, abrasion loss of 150 µm has been observed under the same conditions as the above. Therefore, it is understood that wear resistance is remarkably improved according to a rocker arm which is prepared from the inventive joint body. Example 12 The silicon nitride sintered body employed in Example 9 and a rapidly solidified aluminum alloy powder compact (65 % in relative density and 20 mm in height) containing silicon by 25 weight % were set in a forging mold of steel as shown in Fig. 1. These were forged at a temperature of 580°C with a load of 40 tons, whereby an excellent joint body was obtained. Example 13 The silicon nitride sintered body employed in Example 9 and each aluminum group composite material shown in Table 5 were set in a mold of silicon carbide as shown in Fig. 1, heated to 610°C by a pulsative current with application of a load of 10 tons in a vacuum, and held for 5 minutes. As to the aluminum group composite material, that having a dimensional shape of 25 mm in diameter and 6 mm in thickness was set in the mold. Whichever aluminum group composite material shown in Table 5 was employed, an excellent joint body was obtained. Samples having sectional shapes of 6 mm x 6 mm were cut out from the obtained joint bodies and subjected to measurement of shearing strength, whereby the results shown in Table 5 were obtained. Material Result Crack Shearing Strength (MPa) Al-10%SiC grain no 250 Al-20%SiC grain no 260 Al-10%SiC whisker no 300 Al-20%SiC whisker no 290 Al-20%Si 3 N 4 whisker no 310 Industrial Availability According to the present invention, as hereinabove described, a joint body in which aluminum and silicon nitride are strongly joined with each other can be provided at a low cost, whereby the present invention can be advantageously applied to a lightweight part which is excellent in sliding property as a mechanical part of an internal combustion engine of an automobile or the like and preparation thereof.

Claims: A joint body of aluminum and silicon nitride, said joint body being obtainable by the method of any one of claims 4 to 16 and comprising: a base material being mainly composed of aluminum; and a member consisting of a silicon nitride sintered body being substantially directly joined to said base material, wherein the joining interface between said base material and said member consists of a layer containing oxygen (O) being mainly bonded with silicon (Si) and wherein oxygen is locally present on the joining interface. The joint body in accordance with claim 1, wherein said base material consists of at least one being selected from a group consisting of pure aluminum, aluminum alloys and aluminum group composite materials. The joint body in accordance with claim 1, wherein a layer containing silicon (Si) or a silicon (Si) compound is formed in the vicinity of the joining interface between said base material and said member. A method of preparing a joint body of aluminum and silicon nitride in accordance with claim 1, charging a powdery or bulky base material (2) being mainly composed of aluminum and a member (1) consisting of a silicon nitride sintered body in a mold and heating the same under pressurization, thereby joining said base material and said member with each other, wherein said heating is performed at a temperature of at least 500°C and not more than 800°C, said silicon nitride sintered body being a sintered body being heated/oxidized in an oxygen-containing atmosphere at a temperature of at least 800°C and less than 1200°C. The method of preparing a joint body in accordance with claim 4, wherein said mold has a thermal expansion coefficient of at least 0 and not more than 7 x 10 -6 K -1 . The method of preparing a joint body in accordance with claim 4, wherein said mold has a shape being close to a final product. The method of preparing a joint body in accordance with claim 4, wherein said mold has electrical conductivity. The method of preparing a joint body in accordance with claim 4, wherein said mold includes a joining mold or a joining holder being capable of simultaneously treating a plurality of sets of said base materials and said members. The method of preparing a joint body in accordance with claim 4, wherein a holding time at the maximum temperature for joining is within 10 minutes in said heating time. The method of preparing a joint body in accordance with claim 9, wherein said heating is performed through a plasma. The method of preparing a joint body in accordance with claim 9, wherein said heating is performed by an induced current. The method of preparing a joint body in accordance with claim 9, wherein said heating is performed by a microwave. The method of preparing a joint body in accordance with claim 11, wherein said heating is adapted to heat only said base material. A method of preparing a joint body of aluminum and silicon nitride in accordance with claim 1, arranging a base material being mainly composed of aluminum and a member consisting of a silicon nitride sintered body in a joining mold or a joining holder, and simultaneously performing sintering of said base material and joining of said base material and said member by hot forging, said silicon nitride sintered body being a sintered body being heated/oxidized in an oxygen-containing atmosphere at a temperature of at least 800°C and less than 1200°C. A method of preparing a joint body of aluminum and silicon nitride in accordance with claim 1, arranging a member consisting of a silicon nitride sintered body in a joining mold or a joining holder, and supplying a base material being mainly composed of aluminum in said joining mold or said joining holder in the form of a molten metal, thereby forming a joint body, said silicon nitride sintered body being a sintered body being heated/oxidized in an oxygen-containing atmosphere at a temperature of at least 800°C and less than 1200°C. The method of preparing a joint body in accordance with claim 4, wherein said silicon nitride sintered body has an as-sintered surface.

Inventors: MATSUURA TAKASHI, NISHIOKA TAKAO, SOGABE KOICHI, TAKEUCHI HISAO, YAMAKAWA AKIRA, MATSUURA, TAKASHI, NISHIOKA, TAKAO, SOGABE, KOICHI, TAKEUCHI, HISAO, YAMAKAWA, AKIRA, SOGABE, Koichi Itami Works, Sumitomo El. Ind. Ltd.
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LIMITED
Application year: 1995
Main classification: C04B37
IPC codes: B23K20, C04B37