SALINE SOLUBLE INORGANIC FIBRES

Abstract: Refractory fibres are disclosed for which a vacuum cast preform of the fibre has a shrinkage of 3.5 % or less when exposed to 1260 DEG C for 24 hours. The fibres comprise CaO, SiO2, SrO, and optionally ZrO2 any incidental impurities amounting to less than 2mol % in total. To achieve the shrinkage performance stated the SiO2 excess (defined as the amount of SiO2 calculated as remaining after the above named constituents are crystallised as silicates) exceeds 26 mol %. Preferred fibres comprise:- CaO less than 33.8 mol %, SiO2 more than 62.1 mol %, and more preferably comprise:- CaO 12.9 to 31.9 mol %, SrO 2.6 to 15.5 mol %, SiO2 63.2 to 71.3 mol %, ZrO2 0 to 5.4 mol %.

Description: SALINE SOLUBLE INORGANIC FIBRES This invention relates to saline soluble, non-metallic, amorphous, inorganic oxide, refractory fibrous materials. The invention particularly relates to glassy fibres having silica as their principal constituent. Inorganic fibrous materials are well known and widely used for many purposes (e.g. as thermal or acoustic insulation in bulk, mat, or blanket form, as vacuum formed shapes, as vacuum formed boards and papers, and as ropes, yarns or textiles; as a reinforcing fibre for building materials; as a constituent of brake blocks for vehicles). In most of these applications the properties for which inorganic fibrous materials are used require resistance to heat, and often resistance to aggressive chemical environments. Inorganic fibrous materials can be either glassy or crystalline. Asbestos is an inorganic fibrous material one form of which has been strongly implicated in respiratory disease. It is still not clear what the causative mechanism is that relates some asbestos with disease but some researchers believe that the mechanism is mechanical and size related. Asbestos of a critical size can pierce cells in the body and so, through long and repeated cell injury, have a bad effect on health. Whether this mechanism is true or not regulatory agencies have indicated a desire to categorise any inorganic fibre product that has a respiratory fraction as hazardous, regardless of whether there is any evidence to support such categorisation. Unfortunately for many of the applications for which inorganic fibres are used, there are no realistic substitutes. Accordingly there is a demand for inorganic fibres that will pose as little risk as possible (if any) and for which there are objective grounds to believe them safe. A line of study has proposed that if inorganic fibres were made that were sufficiently soluble in physiological fluids that their residence time in the human body was short; then damage would not occur or at least be minimised. As the risk of asbestos linked disease appears to depend very much on the length of exposure this idea appears reasonable. Asbestos is extremely insoluble. As intercellular fluid is saline in nature the importance of fibre solubility in saline solution has long been recognised. If fibres are soluble in physiological saline solution then, provided the dissolved components are not toxic, the fibres should be safer than fibres which are not so soluble. The shorter the time a fibre is resident in the body the less damage it can do. H. Fόrster in The behaviour of mineral fibres in physiological solutions' (Proceedings of 1982 WHO IARC Conference, Copenhagen, Volume 2, pages 27-55(1988)) discussed the behaviour of commercially produced mineral fibres in physiological saline solutions. Fibres of widely varying solubility were discussed. International Patent Application No. WO87/05007 disclosed that fibres comprising magnesia, silica, calcia and less than 10 wt% alumina are soluble in saline solution. The solubilities of the fibres disclosed were in terms of parts per million of silicon (extracted from the silica containing material of the fibre) present in a saline solution after 5 hours of exposure. The highest value revealed in the examples had a silicon level of 67 ppm. In contrast, and adjusted to the same regime of measurement, the highest level disclosed in the Fόrster paper was equivalent to approximately 1 ppm. Conversely if the highest value revealed in the International Patent Application was converted to the same measurement regime as the Fόrster paper it would have an extraction rate of 901,500 mg Si/kg fibre - i.e. some 69 times higher than any of the fibres Fόrster tested, and the fibres that had the highest extraction rate in the Fόrster test were glass fibres which had high alkali contents and so would have a low melting point. This is convincingly better performance even taking into account factors such as differences in test solutions and duration of experiment. International Patent Application No. WO89/12032 disclosed additional fibres soluble in saline solution and discusses some of the constituents that may be present in such fibres. Among such constituents are ZrO, and this document claims (among other things) processes using fibres of composition (in weight %):- ZrO : 0.06-10%; SiO, 35-70%; MgO 0-50%; CaO 0-64.5%. However the patent actually discloses a much more limited range of zirconia containing materials. European Patent Application No. 0399320 disclosed glass fibres having a high physiological solubility. Further patent specifications disclosing selection of fibres for their saline solubility include for example European 0412878 and 0459897, French 2662687 and 2662688, PCT WO86/04807, WO90/02713, WO92/09536, and W093/22251, and United States 5250488. The refractoriness of the fibres disclosed in these various prior art documents varies considerably. The maximum service temperature of any of the above mentioned fibres (when used as refractory insulation) is up to 815°C (1500°F). Among saline soluble commercial fibres usable at temperatures higher than 815°C are SUPERWOOL ™ a fibre manufactured by The Morgan Crucible Company pic and which has a maximum use temperature of 1050°C and a composition of Si0 2 65wt%; CaO 29wt%; MgO 5wt%; A1,0 3 lwt%. A similar fibre is JNSULFRAX ™ a fibre made by Carborundum Company which has a continuous use limit of 1000°C (1832T) and which melts at 1260°C (2300T). This has a composition of SiO- 65wt%; CaO 31.1wt%; MgO 3.2wt%; AL0 3 0.3wt% and Fe,0 3 0.3wt%. The apphcant's earlier International Patent Application WO93/15028 disclosed saline soluble fibres comprising CaO, MgO and SiO- and optionally Zr0 2 usable at temperatures in excess of 1000°C but gave no indication that fibres could be used at still higher temperatures. That same application also discloses methods of predicting the saline solubility of glasses and for screening for the refractoriness of glasses, although whether such glasses can form fibres is a complex function of many characteristics, e.g. viscosity. In discussing the above mentioned predictive methods International Patent Application W093/ 15028 mentions some compositions containing strontium oxide as a constituent but fibres of these compositions were not made. The applicants have realised that failure of fibres at high temperature occurs primarily upon devitrification of the fibre; if on devitrification insufficient silica is left the fibres will fail through having a shrinkage of greater than 3.5%. Accordingly the applicants have looked to what materials are formed on devitrification and in their earlier International Patent Application No. PCT/GB94/00053 they disclose refractory fibres comprising CaO, SiO : , MgO, optionally ZrO, , optionally less than 0.75mol% Al-0 3 and in which the Si0 2 excess (defined as the amount of SiO, calculated as remaining after the above named constituents are crystallised as silicates) exceeds 21.8mol%. The physical basis for the importance of Si0 2 excess may be that it indicates how much silica is left to maintain a glassy phase on crystallisation of the other constituents as silicate materials. Further, the silicate materials that form on devitrification may become liquid or flow at 1260°C so causing shrinkage. The applicants have found that some systems comprising strontium oxide calcium oxide and silica may form fibres usable at temperatures of up to 1260°C whereas other strontium containing systems do not form such usable fibres. In particular the applicants have found that partial replacement of SrO for MgO in the CaO/MgO/(ZrO-)/Si0 2 fibres of their earlier application PCT/GB94/00053 does not result in success whereas substitution of SrO for MgO tends to give usable fibres. Accordingly the present invention provides a refractory fibre for which a vacuum cast preform of the fibre has a shrinkage of 3.5% or less when exposed to 1260°C for 24 hours and comprising CaO, SiO,, SrO, and optionally ZrO, any incidental impurities amounting to less than 2mol% in total, and in which the SiO, excess (defined as the amount of SiO : calculated as remaining after the above named constituents are crystallised as silicates) exceeds 26mol%. The quantity of potentially fluxing constituents such as alkali metals and other incidental impurities (e.g. iron oxides) should be kept low. From the compositions tested it appears that preferably the fibre comprises:- CaO less than 33.8 mol% SiO, more than 62.1 mol%. and more preferably comprises:- CaO 12.9 to 31.9 mol% SrO 2.6 to l5.5 mol% SiO, 63.2 to 71.3 mol% ZrO, 0 to 5.4 mol %. The applicants have investigated, for their saline solubility and refractoriness, a range of fibre compositions. These fibres were formed by blowing the molten constituents from a melt stream in a conventional manner but the invention is not limited to blown fibres and also encompasses fibres formed by spinning or any other means. Tables 1 & 2 show the results of these tests. Table 1 is divided into the CaO-SrO-ZrO,-SiO, system, the CaO-SrO-SiO, system, and some comparative examples (which were never made as fibres). Table 1 indicates for each fibre the linear shrinkages at 800, 1000, 1200, and 1260°C (not all samples measured at every temperature); mole percent composition (based on the constituents CaO, MgO, SrO, Zr0 2 , A1 2 0 3 , TiO, and SiO, ); crystalline constituents formed on devitrification (see below); SiO, excess (calculation for this figure shown below) and, for the CaO-SrO-SiO, fibres and comparative examples, the calculated CaSi0 3 to SrSi0 3 ratio. Each sample that has a satisfactory shrinkage of 3.5% or less at 1260°C is indicated by a composition shown in bold. Those compositions that fail to meet the shrinkage criterion are indicated in plain text. Table 2 shows for the CaO-SrO-ZrO,-SiO, system and the CaO-SrO-SiO, system the solubilities (as parts per million) of selected constituents of the fibres in saline solution measured by the method described below and shows the total of the named solubilities. This table is ordered in the same manner as Table 1 for convenient comparison. 3 strontium containing systems were investigated. These are:- CaO-MgO-SrO-SiO, CaO-SrO-SiO, CaO-SrO-Zrθ " ,-Si0 2 In the CaO-MgO-SrO-SiO, system very poor results were found - MgO and SrO evidently being incompatible - and so the present invention treats MgO as an incidental impurity that must be held within the 2mol% total given above. The applicants have good reason to believe that the maximum level for MgO may be as low as 1% and preferably the MgO content is kept as low as possible. To some extent therefore SrO may be treated as being in substitution of MgO in the fibres of PCT/GB94/00053. The CaO-SrO-SiO, and CaO-SrO-Zι ,-SiO, systems are discussed separately below. (l) CaO_SrO_Si0 2 This is a simple system in that only CaSi0 3 , SrSi0 3 and Si0 2 crystallise. Therefore all the CaO forms as CaSi0 3 and all the SrO forms as SrSi0 3 . The resulting excess SiO, can then be calculated. However CaSi0 3 and SrSi0 3 form a complete solid solution between them, with the melting point being 1580°C for SrSi0 3 and 1540°C for CaSiO, , and with a minimum in melting point lying between these extremes. It is reasonable to expect that compositions having significant quantities of both CaSi0 3 and SrSi0 3 will have lower melting points than either those containing high CaSi0 3 and low SrSi0 3 , or those containing high SrSi0 3 and low CaSi0 3 contents. Table 1 shows that for those fibres with a CaSi0 3 /SrSi0 3 ratio of greater than 2 (those fibres lying below line "A") a sihca excess of greater than 26mol% neatly divides the workable fibres (having preform sltrinkages of less than 3.5% and shown in bold) from those that are not. For those fibres above line "A" where the CaSi0 3 /SrSi0 3 ratio is less than 2 a sihca excess of 34mol% is required to divide the workable from the unworkable compositions. However the applicants suspect that there will be a lower limit (perhaps around CaSi0 3 /SrSi0 3 ratio 0.5) below which a lower sihca excess will prevail again. (2) CaO-SrO-ZrO T -SiO. This is a more complicated system than the CaO-SrO-SiO, system, with at least 5 components crystallising out. These are 2CaO.ZrO,.4Si0 2 , 6SrO.ZrO,.5SiO,, CaSi0 3 , SrSi0 3 and SiO,. For those compositions studied all the ZrO, crystallises as 2CaO.ZrO,.4SiO, and 6SιO.ZrO,.5SiO, (if more ZrO, is present ZrO,.SiO, will crystallise also). To fit the relative amounts of phases indicated by X-ray analysis the assumption has been made that the thermodynamics of formation of the 2CaO.ZrO,.4SiO, and 6SrO.ZrO,.5SiO, phases are very similar and that the distribution of ZrO, between these phases can be dealt with statistically. The relative ratios of these phases is then determined by the ratios of the CaO and SrO of the initial composition. The issue is further complicated by the fact that in these phases there are 2CaO's per ZrO, and 6SrO's per ZrO, respectively i__ 3 times more SrO to CaO is required to form equal amounts of 2CaO.Zr ,.4SiO, and 6SrO.ZrO,.5SiO,. Therefore to calculate how the ZrO, is split between 2CaO.ZrO,.4SiO, and 6SrO.ZrO,.5SiO, the applicants calculate the ratio of CaO/SrO and multiply by 3, because the CaO is 3 times more likely to form 2CaO.ZrO,.4SiO, than SrO is to form 6SrO.ZrO,.5SiO,. The ZrO, content is divided by this figure to give the amount of 6SrO.ZrO,.5SiO, produced. The remaining ZrO, forms 2CaO.ZrO,.4SiO,. (Of course if there is sufficient ZrO, to exhaust either the CaO or SrO the calculation must be modified accordingly). Now any remaining CaO forms CaSi0 3 and any remaining SrO forms SrSi0 3 . The remaining excess SiO, can then be calculated. With all these SrO containing compositions there will be inevitable discrepancies around the boundary areas. Small changes in the composition of only 0.1 -0.2% are usually sufficient to be the difference between failure and pass at the boundary. In these systems there are considerable difficulties in analysing for SrO, CaO and SiO, together by X-ray fluorescence (XRF) because their XRF spectra interfere with each other thereby making it difficult to construct an accurate quantitative XRF programme for these systems. This means the accuracy of the reported compositions is less than would be expected for general XRF samples. These factors may explain why two compositions (F29 and F16) in the CaO-SrO-ZrO,-Si0 2 system show as failures when their excess SiO, figure would indicate them as being potentially useful fibres. Under the heading "Comparative compositions" in Table 1 are shown two types of material. Those with the prefix "SCS" are compositions mentioned in WO/93/15028 as being potential refractory glass forming compositions. None of these fibres were made and as will be seen from the figures for excess SiO, given would not fall within the scope of the present application. The compositions shown with the prefix "BS" are fibres made containing appreciable amounts of both MgO and SrO and as can be seen these materials have an unsatisfactory shrinkage. Sihca excesses have not been calculated for these compositions. The applicants have looked to the various incidental impurities that can occur in inorganic oxide refractory fibres (e.g. alkali oxides and iron oxide) and have found that the impurity levels that can be tolerated vary according to the proportions of the main constituents of the fibre. Fibres containing high levels of ZrO, for example can tolerate higher levels of Na,0 or Fe,0 3 than fibres with low levels of ZrO,. Accordingly the applicants propose a maximum level of incidental impurities of 2mol%, the maximum level that will be tolerable will however vary as mentioned above. The following describes in detail the methods used to measure shrinkage and solubility. Shrinkage was measured by proposed ISO standard ISO/TC33/SC2/N220 (equivalent to British Standard BS 1920, part 6,1986) with some modifications to account for small sample size. The method in summary comprises the manufacture of vacuum cast preforms, using 75g of fibre in 500cm 3 of 0.2% starch solution, into a 120 x 65mm tool. Platinum pins (approximately 0. l-0.3mm diameter) were placed 100 x 45mm apart in the 4 comers. The longest lengths (LI & L2) and the diagonals (L3 & L4) were measured to an accuracy of ±5μm using a travelling microscope. The samples were placed in a furnace and ramped to a temperature 50°C below the test temperature at 400°C/hour and ramped at 120°C/hour for the last 50°C to test temperature and left for 24 hours. The shrinkage values are given as an average of the 4 measurements. It should be noted that although this is a standard way of measuring shrinkage of fibre it has an inherent variabihty in that the finished density of the preform may vary depending on casting conditions. Further it should be noted that fibre blanket will usually have a higher shrinkage than a preform made of the same fibre. Accordingly the 3.5% figure mentioned in this specification is likely to translate as a higher shrinkage in finished blanket. Solubility was measured by the following method. The fibre was first chopped - 2.5 g of fibre (deshotted by hand) was hquidised with 250 cm 3 of distilled water in a domestic Moulinex (Trade Mark) food blender for 20 seconds. The suspension was then transferred to a 500 cm 3 plastic beaker and allowed to settle after which as much liquid as possible was decanted and the remaining liquid removed by drying in an oven at 110°C. The solubility test apparatus comprised a shaking incubator water bath, and the test solution had the following composition:- The above materials were diluted to 1 litre with distilled water to form a physiological-like saline solution. 0.500 grams ± 0.0003 grams of chopped fibre was weighed into a plastic centrifuge tube and 25 cm 3 of the above saline solution added. The fibre and saline solution was shaken well and inserted into the shaking incubator water bath maintained at body temperature (37°C ± 1°C). The shaker speed was set at 20 cycles/minute. After the desired period (usually 5 hours or 24 hours) the centrifuge tube was removed and centrifuged at 4500 revs/minute for approximately 5 minutes. Supernatant hquid was then drawn off using a syringe and hypodermic needle. The needle was then removed from the syringe, air expelled from the syringe, and the hquid passed through a filter (0.45 micron cellulose nitrate membrane filter paper [WCN type from Whatman Labsales Limited]) into a clean plastic bottle. The liquid was then analysed by atomic absorption using a Thermo Jarrell Ash Smith - Hiefje II machine. The operating conditions were as follows using a nitrous oxide and acetylene flame:- WAVELENGTH BAND CURRENT. ELEMENT (nm) WIDTH FLAME Fuel Rich Fuel Rich Fuel Lean Fuel Lean Fuel Lean The procedure and standards adopted for determining the above elements were as set out below. SiO, can be determined without dilution up to 250 ppm concentration (1 ppm lmg/Litre). Above this concentration an appropriate dilution was made volumetrically. A 0.1 % KC1 solution (0.1 g in 100 cm 3 ) was added to the final dilution to prevent ionic interference. NB If glass apparatus is used, prompt analysis is necessary. From a stock solution of 1000 ppm pure ignited silica (99.999%) (fused with Na,C0 3 at 1200°C for 20 minutes in a platinum crucible (0.2500g SiO 2g Na~C0 3 ) and dissolved in dilute hydrochloric acid (4 molar) made up to 250cm 3 with distilled water in a plastic volumetric flask) the following standards were produced:- STANDARD (ppm SiO,) STOCK SOLUTION (cm 3 ) 10.0 1.0 20.0 2.0 30.0 3.0 50.0 5.0 100.0 10.0 250.0 25.0 Add 0.1% KCl to each standard before making to 100cm 3 . Aluminium may be measured directly from the sample without dilution. Standards of 1.0, 5.0 and 10.0 ppm Al may be used. For cahbration readings are multiplied by 1.8895 to convert from Al to A1,0 3 . A standard Al atomic absorption solution (e.g. BDH 1000 ppm Al) was bought and diluted using an accurate pipette to the desired concentration. 0.1% KCl was added to prevent ionic interference. Calcium may require dilutions on the sample before determination can be carried out (i.e. x 10 and x 20 dilutions). Dilutions must contain 0.1% KCl. A standard Ca atomic absorption solution (e.g. BDH 1000 ppm Ca) was diluted with distilled water and an accurate pipette to give standards of 0.5, 4.0 and 10.0 ppm. 0.1% KCl is added to prevent ionic interference. To convert readings obtained from Ca to CaO a factor of 1.4 was used. Strontium is measured against a standard atomic absorption solution (Aldrich 970μm/ml). Three standards are prepared to which 0.1%KC1 is added (Sr [ppm] 9.7,3.9 & 1.9). Dilutions of xlO and x20 are nromally made to measure Sr level in the sample. SrO is then calculated as 1.183xSr. Magnesium may require dilutions on the sample before determinations can be made (i.e. x 10 and x 20). Add 0.1 % KCl to each dilution. To convert Mg to MgO multiply by 1.658. A standard Mg atomic absorption solution (e.g. BDH 1000 ppm Mg) was diluted with distilled water and an accurate pipette to give standards of 0.5, 1.0 and 10.0 ppm Mg. 0.1% KCl was added to prevent ionic interference. All stock solutions were stored in plastic bottles. The above has discussed resistance to shrinkage of preforms exposed to 1260°C for 24 hours. This is an indication of the maximum use temperature of a fibre. In practice fibres are quoted for a maximum continuous use temperature and a higher maximum exposure temperature. It is usual in industry when selecting a fibre for use at a given temperature to choose a fibre having a higher continuous use temperature than that nominally required for the intended use. This is so that any accidental increase in temperature does not damage the fibres. It is quite usual for a margin of 100 to 150°C to be given. Accordingly this invention extends to use of the claimed fibres at elevated temperatures (i.e. at temperatures where the refractoriness of fibres is important) and not just to use at 1260°C. It will be evident that incidental impurity levels are preferably kept as low as possible. The applicants surmise that as the various crystalline materials crystallise from the fibres impurities migrate to the grain boundaries and concentrate there. Thus a small impurity can have a very large effect. 31 -_lO/_6aθ/__Dd 8.W0/96 OΛV TABLE 1 CaO-SrO-Si02 System TABLE 2 CaO-SrO-Zr02-Si02 System CaO-SrO-Si02 System C omposiuon moi% Solubility (ppm) Comp. CaO MgO SrO Zr02 A1203 Ti02 Si02 CaO MgO/SrO Si02 Total E29 23.3 0.6 11.8 0.2: 641 33: 47 103; 183.00 E30 17.8, 0.5 15.2, 0.1 0.2. 0.1 66.2 : 23! 54! 921169.00! E19 20 : 0.6 12 0.1 0.3 i 66.9 : 32; 52: 881172.001 E4 19 0.5 11.5 0.2 0.1 0.1 68.7 32: 50 I 691151.001 E20 14.8 0.7 15.5 0.1 0.3: 68.6 20 53; 591132.001 E5 12.9 03 155 01 or 01 71 21 66' 54 i 14100

Claims: CLAIMS 1. A refractory fibre for which a vacuum cast preform of the fibre has a st-rinkage of 3.5% or less when exposed to 1260°C for 24 hours and comprising CaO, Si0 2 , SrO, and optionally Zr0 2 any incidental impurities amounting to less than 2mol% in total, and in which the SiO, excess (defined as the amount of SiO, calculated as remaining after the above named constituents are crystallised as silicates) exceeds 26mol% 2. A refractory fibre as claimed in claim 1 and comprising:- CaO less than 33.8 mol% Si0 2 more than 62.1 mol%. 3. A refractory fibre as claimed in claim 2 and comprising:- CaO 12.9 to 31.9 mol% SrO 2.6 to l5.5 mol% SiO, 63.2 to 71.3 mol% ZrO, 0 to 5.4 mol %. 4. A method of providing a saline soluble refractory fibre for use at elevated temperatures comprising selecting a fibre as claimed in any of claims 1 to 3.

Inventors: JUBB GARY ANTHONY, JUBB, GARY, ANTHONY
Applicants: JUBB GARY ANTHONY, MORGAN CRUCIBLE CO, JUBB, GARY, ANTHONY, THE MORGAN CRUCIBLE COMPANY PLC
Application year: 1995
Main classification: C03C13
IPC codes: C03C13