ERASABLE INK COMPOSITION AND MARKING INSTRUMENT CONTAINING SAME

Abstract: An erasable ink composition contains a water-insoluble polymeric dye obtained from the polymerization of at least two coreactive polyfunctional monomers with at least one of the monomers possessing a dye moiety covalently bonded thereto. The ink is intended for use in any of a variety of marking instruments, in particular a ball-point pen.

Description: ERASABLE INK COMPOSITION AND MARKING INSTRUMENT CONTAINING SAME BACKGROUND OF THE INVENTION This invention relates to an erasable ink composition and to a marking instrument, e.g., a ball-point pen, containing the composition. More particularly, this invention relates to an erasable ink composition containing a water-insoluble polymer dye component, i.e., a polymer possessing a dye moiety covalently bonded thereto. Numerous erasable ink compositions are known, e.g., those described in U.S. Patent Nos. 3,834,823, 3,875,105, 3,949,132, 4,097,290, 4,212,676, 4,227,930, 4,256,494, 4,297,260, 4,329,262, 4,329,264, 4,349,639, 4,357,431, 4,367,966, 4,368,076, 4,379,867, 4,389,499, 4,390,646, 4,391,927, 4,407,985, 4,410,643, 4,419,464, 4,441,928, 4,509,982, 4,525,216, 4,557,618, 4,578,117, 4,596,846, 4,606,769, 4,629,748, 4,687,791, 4,721,739, 4,738,725, 4,760,104, 4,786,198, 4,830,670, 4,954,174, 4,960,464, 5,004,763, 5,024,898, 5,037,702, 5,082,495, 5,114,479, 5,120,359, 5,160,369 and 5,217,255. These inks are formulated by mixing a dye (taken herein to also include "pigment", "colorant", "chromophore" and other terms of similar meaning) with a variety of polymer and liquid carrier/solvent combinations thereby forming a flowable dye/polymer matrix. The polymer component is chosen for its film forming properties and its ability to be readily removed from the substrate to which it is applied, e.g., cellulosic paper, through the abrasive action of an eraser. However, a common problem with these erasable ink compositions concerns the residual dye which remains after erasure. Incomplete erasure may be attributed to inadequate removal of the dye/polymer matrix from the paper substrate and/or migration of dye into the pores of the substrate. SUMMARY OF THE INVENTION In accordance with the present invention an erasable ink composition is provided which comprises (a) a water-insoluble polymer dye obtained by affecting polymerization of a polymer-forming reaction medium containing at least two coreactive polyfunctional monomers with at least one of the monomers possessing a dye moiety covalently bonded thereto and (b) an evaporable liquid carrier in which the polymer dye is dissolved, dispersed or swollen, the erasable ink composition when applied to a substrate and upon drying thereon being (1) sufficiently adherent to the substrate as to resist flaking therefrom and (2) substantially erasble. Since the dye is covalently bonded to the polymer in the erasable ink composition of this invention, there is little opportunity for it to separate from the polymer and migrate into a porous substrate. Thus, the erasable ink composition of this invention is apt to leave significantly less residual dye following its erasure than known erasable ink compositions in which the dye is merely physically combined with the polymer component(s) . DESCRIPTION OF THE PREFERRED EMBODIMENTS The polymer dye component of the erasable ink composition of this invention is prepared by polymerizing at least two coreactive polyfunctional monomers with at least one of the monomers possessing a dye moiety covalently bonded thereto. At least one of the monomers must be sufficiently hydrophobic as to render the resulting polymer dye water-insoluble. Part or all of the polyfunctional monomers can be oligomeric or polymeric in nature. The expression "polyfunctional monomer" characterizes those compounds possessing at least two reactive functional groups (not counting any sites of unsaturation that may be present) such as, but not limited to, hydroxyl, sulfhydryl, carboxylic acid, amine, nitrile, acyl halide and isocyanate groups. The expression also includes compounds which, under polymerization reaction conditions, present polyfunctionality, e.g., lactones and lactams which on opening of their rings are chemically equivalent to α,ω-hydroxy-carboxylic acids and α,ω-aminocarboxylic acids, respectively. Polymeric dyes of the type that are useful in the erasable ink composition of this invention are known (but for applications other than erasable ink compositions) or can be prepared by appropriate modification of known polymer-forming procedures. Illustrative of such known polymeric dyes are those disclosed in U.S. Patent Nos. 4,778,742, 5,104,913, and 5,194,463, the contents of which are incorporated by reference herein. A preferred polymer dye for use herein is one prepared by a waterborne process, i.e., a polymerization process in which the resulting polymer is provided as an aqueous emulsion of or dispersion polymer dye particles. The polymer dye emulsion with or without the addition of other components can, if desired, be utilized directly as the erasable ink composition of this invention thus eliminating any further manufacturing operations (unlike the case of bulk polymer dyes which would require pulverization to the desired particle size followed by addition of some suitable evaporable liquid carrier) . In accordance with U.S. Patent No. 4,778,742, a polymeric dye of the general formula [—0—A—DYE—A—O—B—] n wherein A is selected from the group consisting of alkylene and arylene, B is selected from the group consisting of 0 0 0 0 0 II II II II II — C — , — C — R — C — and — CO — R — OC — wherein R is an alkylene group, an arylene segment or a polyether segment, DYE is a dye moiety and n is from about 2 to about 100 and preferably from about 5 to about 35, can be prepared by a solution or interfacial polymerization process. In solution polymerization, stoichiometric amounts of polyfunctional monomers, specifically, a bisphenoxy- functionalized dye and a diacyl halide, are reacted in a suitable solvent medium, e.g., an aliphatic halogenated hydrocarbon such as methylene chloride, in the presence of an excess amount of a tertiary amine such as triethylamine base. Polymerization is then affected at a temperature of from about 5°C. to about 30°C. and completed in about 0.5 to 3 hours. In interfacial polymerization, a bisphenoxy- functionalized dye is initially dissolved in an aqueous alkaline solution in the presence of an emulsifying agent. Thereafter, the resulting solution is stirred and treated with a solution of an appropriate bifunctional monomer such as a diacyl chloride or a bishaloformate in a water immiscible solvent such as methylene chloride to obtain, respectively, the polyester dye or the polycarbonate dye. The polymeric dyes from the solution polymerization process are then further treated by washing the reaction mixture with water followed by precipitation of a methylene chloride solution of the dyes from a nonsolvent such as hexane or methanol. Also, with the interfacial process, the polymeric dyes are separated by simple filtration followed by washing thoroughly with water. Examples of bisphenoxy-functionalized dye monomers that can be used to prepare the polymeric dyes of U.S. Patent No. 4,778,742 include 1,5-bis(p-hydroxyphenylthio) anthraquinone, 1,8-bis(p-hydroxyphenylythio)anthraquinone, 1,5-bis(p-hydroxyphenylthio)-4,8-bis(phenylthio) anthraquinone, 1,8-bis[2-(p-hydroxyphenyl)ethylamino] anthraquinone, 1,5-bis[2-(p-hydroxyphenyl)ethylamino] anthraquinone, 1,4-bis[2-(p-hydroxyphenylamino) anthraquinone, 1,4-bis[2-(p-hydroxyphenyl)ethylamino] anthraquinone, 1,4-bis[2-(p-hydroxyphenylthio) anthraquinone and 6-phenylthio-l,4-bis[2-(p-hydroxy¬ phenyl)ethylamino]anthraquinone. Examples of diacyl halide monomers that can be reacted with the bisphenoxy-functionalized dye monomers to provide the polymeric dye of U.S. Patent No. 4,778,742 include succinyl chloride, glutaryl chloride, adipoyl chloride, dimethylglutaryl chloride, sebacoyl chloride, phthaloyl chloride, isophthaloyl chloride, terephthaloyl chloride and the like. Examples of useful bishaloformates include diethyleneglycol bischloroformate, triethyleneglycol bischloroformate, tetraethyleneglycol bischloroformate, biphenoxy bischloroformate, propyleneglycol bischloroformate, dipropyleneglycol bischloroformate, butyleneglycol bischloroformate, ethyleneglycol bisbromoformate, propyleneglycol bisbromoformate, and the like. The polymeric dye of U.S. Patent No. 5,104,913 is obtained by polymerizing a polyfunctional monomer possessing a dye moiety covalently bonded thereto, a terephthalic and/or 2,6-naphthalenedicarboxylic acid and a branched-chain diol of the general formula R 1 wherein R 1 is hydrogen or an unsubstituted or substituted alkyl, cycloalkyl or aryl radical and R 2 is an unsubstituted or substituted alkyl, cycloalkyl or aryl radical. The dye- containing monomer can be selected from anthraquinone, methine, bis-methine, anthrapyridone, 2,5-diarylamino- terephthalic acid or ester, coumarin, quinophthalone, perylene and other thermally-stable dye compounds possessing functional groups that are reactive for the carboxylic and/or hydroxyl groups of the other monomers, i.e., hydroxyl, carboxyl, ester, amino, alkylamino, etc., groups, such that the dye will be incorporated in the resulting polyester. Examples of dye-containing monomers include anthraquinone dyes and methine dyes possessing two reactive functional groups selected from the aforementioned types. U.S. Patent No. 5,194,463 describes a polymer dye which is a polyurethane of the general formula 0 0 II II -fOCNH—R—NHCO— R^ wherein R is a divalent radical selected from optionally substituted C 2 -C 1fJ -alkylene, C 3 -C 8 -cycloalkylene, arylene, C 1 -C (t -alkylene-arylene-C--C 4 -alkylene, C,-C 4 -alkylene-C 3 -C 8 - cycloalkylene-C.-C^-alkylene or C.-C 4 -alkylene-l,2,3,4,5,6,7- octahydronaphthalene-2,6-diyl-C.-C 4 -alkylene; R 1 is a divalent organic radical comprised of about 1 to 100 mole percent of the residue of a dye bonded to two hydroxyl groups through alkylene moieties with any remainder of R 1 comprised of the residue of organic diols of the formula HO— 2 —OH in which R 2 is a divalent radical selected from C 2 -C 18 alkylene, C 3 -C 8 -cycloalkylene, C 1 -C 4 alkylene- 1,2,3,4,5,6,7,8-octahydronaphthalen-2,β-diyl-C,-^ alkylene, C^C^-alkylene-C j -Cg-cycloalkylene-C j -C^-alkylene, C 1 -C 4 alkylene-arylene-C 1 -C 4 -alkylene, C 2 -C 4 alkylene-0-C 2 -C 4 alkylene, C 2 -C 4 alkylene-S-C 2 -C 4 alkylene or C 2 -C 4 alkylene-O- C 2 -C 4 alkylene-0-C 2 -C 4 alkylene; and n is equal to or greater than 2. The dye containing the hydroxyl groups can be selected from a variety of chromophoric classes including azo, metallized azo, diazo, methine, or arylidene, polymethine, azo-methine, anthraquinone, azamethine, anthrapyridone (3H-dibenz [f,ij] isoquinoline-2,7-dione) , anthrapyridine (7H-dibenz [f,ij] isoquinoline-7-one) , phthaloylphenothiazine (14H-naphtho [2,3-a] phenothiazine- 8,13-dione), benzanthrone (7H(de)anthracene-7-one) , anthrapyrimidine (7H-benzo [e] perimidine-7-one) , anthrapyrazole, anthraisothiazole, triphenodioxazine, thiaxanthene-9-one, flourindine (5, 12-dihydroquinoxaline [2,3-b] phenazine) , quinophthalone, phthalocyanine, naphthalocyanine, nickel dithiolenes, coumarin (2H-1- benzopyran-2-one) , coumarin imine (2H-l-benzopyran-2-imine) , indophenol, perinone, nitroarylamine, benzodifuran, phthaloylphenoxazine (14H-naphtho[2,3-alphenoxazine-8,13- dione) , phthaloylacridone (13H-naphtho[2,3-c] acridine 5,8,14-trione) , anthra-quinonethioxanthone (8H-naphtho[2,3- c]thioxanthene-5,8,13-trione) , anthrapyridazone, naphthofl' ,2' ,3' :4,5]quino[2,1-b] quinazoline-5,10-dione, lH-anthra(2,1-b) (1,4) thiazin-7,12-dione, indigo, thioindigo, xanthene, acridine, azine, oxazine, 1,4- and 1,5-naphthoquinones, pyromellitic acid diimide, naphthalene- 1,4,5,8-tetracarboxylic acid diimide, 3,4,9,10-perylene- tetracarboxylic acid diimide, hydroxybenzophenone, benzotriazole, naphthotriazole, naphthoquinone, diminoisoindoline, naphthopyran (3H-naphtho[2,l-b]pyran-3- ones and 3-imines) and aminonaphthalimide. The polyurethane of U.S. Patent No. 5,194,463 can be obtained by reacting one or more of the dihydroxyl- containing dyes with a diisocyanate and, if desired, another diol, employing known procedures. Numerous modifications of the foregoing known processes for obtaining a polymeric dye that can be utilized in the erasable ink composition of this invention are possible. For example, part or all of the bisphenoxy- functionalized dye monomer of U.S. Patent No. 4,778,742, the functionalized dye monomer of U.S. Patent No. 5,104,913 or the hydroxyl-containing dye monomer of U.S. Patent No. 5,194,463 can be replaced with a polyfunctional polymer dye monomer of the general formula (R->- a - P X] b ) c wherein R is a dye moiety covalently bonded to polymer residue P, X is a functional group, a, b and c each is at least 1, provided, the product of b x c is at least 2, when c is at least 2, a is 1 and where there is more than one R, P or X, each R, P or X can be the same or different. Dye moiety R can be derived from among any of the polyfunctionalized dye monomers previously mentioned, polymer residue P can be that of a polyether, polyester, polya ide, polycarbonate or the like, and X can include hydroxyl, sulfhydryl, carboxyl, primary amine, secondary amine and isocyanate reactive groups. For example, a dihydroxyl-containing dye such as one described in U.S. Patent No. 5,194,463 or some other dihydroxyl-containing dye can be reacted with ethylene oxide, propylene oxide or a mixture thereof to provide a hydroxyl-terminated liquid polyether dye monomer. Polyether dyes of this type are known from U.S. Patent Nos. 3,157,633 and 4,284,729, the disclosures of which are incorporated by reference herein. Similarly, the dihydroxyl-containing dye can be reacted with an α,ω-hydroxycarboxylic acid or cyclic ester analog thereof, for example e-caprolactone, to provide a hydroxyl- terminated liquid polyester dye monomer. Either the polyether or polyester dye monomer can be reacted with a polyisocyanate or an isocyanate-terminated prepolymer to provide the water-insoluble polymer dye component of the erasable ink composition herein. The dye monomers utilized in the practice of this invention possess pendent dye moieties covalently bonded thereto. The dye moieties can be of any variety such as azo, tricyanovinyl, anthraquinone and methine. Azo dye moieties are generally preferred. Dye monomers which are particularly useful in carrying out the present invention include amine dye monomers possessing structural units of the general formula: wherein each A independently can be an ester or amide linkage, n can be an integer of from about 1 to about 50, preferably from about 1 to about 5, R is an aliphatic (straight-chain, branched or cyclic) or aromatic (single or fused ring) hydrocarbon with up to about 30 carbon atoms, a and b are independently from 1 to about 10, Z is an arylene group such as phenylene, diphenylene or naphthylene, optionally containing one or more substituents such as halogen, hydroxyl, -CHO, alkoxy, alkylamino, dialkylamino, amide, alkyla ide, -NH 2 , -N0 2 , phenyl, carbamyl, -CN, carbalkoxy, sulfonyl, sulfamyl and sulfamido or a single bond when Y is an anthraquinone group and Y is a dye moiety selected from (1) an azo group where Y can be -N=N-D or -N=N-G-N=N-D wherein D is an aromatic nucleus of 1 to 5 rings (fused or connected by single bonds) or a heterocyclic ring of 4, 5 or 6 members containing one to four or more atoms of -N-, -S- and nonperoxidic atoms -0- and optionally bearing one or more auxochromic groups such as -Cl, -Br, -F, -OH, alkyl, alkoxy, alkylamino, dialkylamino, -NH 2 , -N0 2 , phenyl, carbamyl, -CN, carbalkoxy, sulfonyl, sulfamyl and sulfamido and G is a phenylene or napthylene group; (2) a tricyanovinyl group where Y can be CN \ / C = C ; / \ NC CN (3) an anthraquinone group where Y can be wherein R, can be -OH, -NH 2 , alkylamine, dialkylamino or arylamino where aryl is phenyl or phenyl substituted by auxochromic groups as defined for use on D as defined in (1) above, R 2 and R 3 independently can be auxochromic groups as defined for use on D as defined in (1) above; and (4) a methine group where Y can be P \ / c = c / \ H Q wherein P and Q are independently selected from cyano, carbalkoxy, carbaryloxy, carbaralkyloxy, carbamyl, carboxy, N-alkylcarbamyl, N-alkyl-N-arylcarbamyl, N,N-diakylcarbamyl, N-arylcarbamyl, N-cyclohexylcarbamyl, aryl, 2-benzoxazolyl, 2-benzothiazoyl, 2-benzimidazolyl, l,3,4-thiadiazol-2-yl, l,3,4-oxadiazol-2-yl, S0 2 alkyl, S0 2 aryl and acyl or P and Q may be combined as wherein R 4 is alkyl, aryl or cycloalkyl and R 5 is CN, COOH, C0 2 alkyl, carbamyl or N-alkylcarbamyl, wherein each alkyl, aryl or cycloalkyl moiety or portion of a group or radical may be substituted with one or more auxochromic groups as defined for use on D as defined in (1) above. The amine dye monomer is advantageously produced by reacting an aromatic amine of the general formula: R ύ —(CH 2 ).—N—(CH 2 ) b —R 7 wherein R t and R 7 are independently COOH, COOR 8 wherein R g is an alkyl group of from 1 to about 8 carbon atoms, NH 2 and OH, a and b independently range from 1 to about 10 and Z is an aryl group such as phenyl, diphenyl, naphthyl, said aryl group optionally containing one or more substituents such as halogen, hydroxyl, -CHO, alkyl, alkoxy, alkylamino, dialkylamino, amide, alkylamide, -NH 2 , -N0 2 , phenyl, carbamyl, -CN, carbalkoxy, sulfonyl, sulfamyl and sulfamido with one or more reactants selected from the group consisting of polyhydric alcohol, polyamine and polycarboxylic acid under condensation polymerization reaction conditions to provide a polyester or polyamide containing polymerized units of the above-identified aromatic amine and groups that are reactive with isocyanate groups. Thereafter, a dye moiety is coupled to the polyester or polyamide through the pendant aromatic units derived from the aromatic amine employing any suitable technique such as diazotization. In an alternative embodiment, the dye moiety is coupled to the pendant aromatic units of the aromatic amine prior to forming the polyester or polyamide. Suitable polyhydric alcohols include those of the general formula: HO—R—OH wherein R can be an aliphatic (straight-chain, branched or cyclic) or aromatic (single or fused ring) hydrocarbon with up to 30 carbon atoms, suitable polyamines include those of the general formula H 2 N—R—NH 2 wherein R is the same as defined above for the polyhydric alcohol and suitable polycarboxylic acids include those of the general formula: O 0 LC—R—CL wherein R is the same as defined above for the polyhydric alcohol and L is halogen, hydroxyl or alkoxy. In a preferred embodiment, phenyldiethanola ine, i.e., is employed as the aromatic amine, an alkanediol such as butanediol or hexanediol is employed as the polyhydric alcohol and adipic acid is employed as the polycarboxylic acid to provide a polyester polyol dye monomer in accordance with this disclosure. In another preferred embodiment, substituted phenyldiethanolamine is employed as the aromatic amine. Particularly preferred substituted phenyldiethanolamines are those corresponding to the following formulas: which is commercially available from Henkel Corp. (Emery 5752) and which can be obtained by, e.g., nucleophilic aromatic substitution or the Vilsmeier-Haack reaction. See, e.g., U.S. Patent No. 4,757,130. The former substituted phenyldiethanolamine is useful as an intermediate for blue colorants. It will be understood by those skilled in the art that a molar excess of polyhydric alcohol starting reactants can be employed to provide hydroxyl-terminated polyester dye monomer and that a molar excess of polyamine starting reactants can be employed to provide a ine- terminated polyamide dye monomer. The amine dye monomers are preferably linear and preferably contain from 1 to about 5 dye moieties per chain length of dye monomer, more preferably 1 or 2 dye moieties per chain length. Molecular weights ranging from about 500 up to about 5000, preferably from about 2500 to about 3500, g/mol have been found to be particularly useful in the practice of this invention. The amine dye monomer is reacted under waterborne polymer-forming reaction conditions as disclosed herein with an isocyanate-group containing monomer to provide waterborne polyurethane-urea. It will be understood by those skilled in the art that uncolored monomers, for example, uncolored polyester polyol, can be combined with the dye monomer and isocyanate-group containing monomer to provide the waterborne polyurethane- urea polymer dye disclosed herein. Any suitable uncolored monomer may be employed. Any suitable isocyanate-group containing monomer can likewise be employed. Typically, such a monomer will correspond to the general formula: OCN—R—NCO wherein R is the same as defined above in connection with the polyhydric alcohol. Representative examples of such isocyanate-group containing monomers are the isomers of aromatic diisocyanates such as toluene diisocyanate (TDI) , xylene diisocyanate, 1,3-bis(l-isocyanato-l-methylethyl) benzene and the like, difunctional aliphatic or cycloaliphatic isocyanates having between 2 and 18 carbon atoms, preferably between 4 and 12 carbon atoms, such as isopherone diisocyanate and hexamethylene diisocyanate, and isomers and oligomers of di(4-isocyanatophenyl) methane (MDI) . 6/18697 A particularly preferred waterborne polymer dye for use herein is a waterborne polyurethane-urea prepared by modification of any of the polymerization processes described in Frisch et al., ed. , "Advances in Urethane Science and Technology", Vol. 10, pp. 121-162 (1987), the contents of which are incorporated by reference herein. The modification referred to involves the substitution of part or all of one or more of the polyfunctional reactants employed in these processes with a polyfunctional monomer possessing covalently bonded dye in accordance with the present invention. Thus, e.g., amine dye monomer and isocyanate-group containing monomer are reacted under waterborne polymer-forming reaction conditions in a hydroxyl (or amine) to isocyanate equivalent ratio of about 0.25:1 to about 1:0.25, respectively. Where an excess of isocyanate is employed, the resulting polymer can be chain extended in accordance with well known procedures. The waterborne polymer-forming reaction conditions which can be advantageously utilized to prepare waterborne polymer dyes in accordance with this invention, respectively, the solvent, melt dispersion, prepolymer mixing and ketamine/ketazine processes, can be summarized as follows: 1. The Solvent Process The solvent process involves the steps of: a) reacting a liquid polymeric diol with a diisocyanate to provide an isocyanate group-terminated prepolymer possessing or lacking sufficient hydrophilic groups to render the prepolymer self-dispersible; b) reacting the isocyanate group-terminated prepolymer dissolved in organic solvent with an aliphatic diamine chain extender and, where the prepolymer lacks sufficient hydrophilic groups to be self-dispersible, an aliphatic diamine chain extender possessing at least one hydrophilic group, to provide an organic solvent solution of self-dispersible polyurethane-urea; and, c) adding a sufficient amount of water to the organic solvent solution of the polyurethane-urea to form a dispersion of polyurethane-urea particles, at least one of said liquid polymeric diol, diisocyanate and aliphatic diamine possessing a dye moiety covalently bonded thereto. 2. The Melt Dispersion Process The melt dispersion process involves the steps of: a) reacting a liquid polymeric diol, an aliphatic diol possessing at least one ionic group and a diisocyanate to provide an isocyanate group terminated prepolymer possessing ionic groups; b) reacting the isocyanate group-terminated prepolymer with a formaldehyde-reactive capping agent to cap the isocyanate end groups; c) dispersing the capped prepolymer in water; and, d) reacting the dispersed capped prepolymer with formaldehyde to provide dispersed polyurethane-urea particles, at least one of said liquid polymeric diol, diisocyanate and aliphatic diamine possessing a dye moiety covalently bonded thereto. 3. The Prepolymer Mixing Process The prepolymer mixing process involves the steps of: a) reacting a liquid polymeric diol, a carboxylic group-containing diol and an aliphatic diisocyanate to provide an isocyanate group-terminated prepolymer possessing free carboxyl groups; b) reacting the prepolymer with a tertiary amine to convert the carboxyl groups to ammonium carboxylate groups and render the prepolymer self-dispersible; c) dispersing the self-dispersible prepolymer in water; and, d) reacting the dispersed prepolymer with a diamine chain extender to provide an aqueous dispersion of polyurethane-urea particles, at least one of said liquid polymeric diol, carboxyl group-containing diol, aliphatic diisocyanate and aliphatic liquid diamine chain extender possessing colorant covalently bound thereto. 4. The Ketamine/Ketazine Process The ketamine/Ketazine process involves the steps of: a) reacting a liquid polymeric diol, a carboxylic group-containing diol and a diisocyanate to provide an isocyanate group-terminated prepolymer possessing free carboxyl groups; b) reacting the prepolymer with a tertiary amine to convert the carboxyl groups to ammonium carboxylate groups and render the prepolymer self-dispersible; c) reacting the self-dispersible prepolymer with at least one member of the group consisting of ketimine and ketazine in the presence of water to provide an aqueous dispersion of polyurethane-urea particles, at least one of said liquid polymeric diol, carboxyl group-containing diol, aliphatic diisocyanate and aliphatic liquid diamine chain extender possessing colorant covalently bound thereto. In a preferred embodiment of these waterborne processes, the liquid polymeric diol is one of the general formula R-fPOH) 2 wherein R is a covalently bound dye chromophore and each P is the same or different polymer residue. Examples of such liquid polymeric diols include any of the previously mentioned dihydroxyl-terminated liquid polyether or polyester dye monomers containing a covalently bonded dye moiety such as the amine dye monomer. The polymer dye component of the erasable ink composition of this invention will generally possess an average particle size of from about 25 to about 5000 nanometers and preferably from about 50 to about 2000 nanometers. Where the polymer dye component is not obtained in a particle size which is suitable for use in the erasable ink composition herein, it may be reduced to such size by any known or conventional method for obtaining polymer powders, for example, by grinding, milling, or by any of several "hot water" emulsification processes for producing polymer powders such as that described in U.S. Patent No. 3,586,654, the contents of which are incorporated by reference herein. When employed, the waterborne polyurethane-urea component of the erasable ink composition of this invention will generally possess an average particle size of from about 0.01 to about 4 microns and preferably from about 0.05 to about 0.20 microns. The fully formulated erasable ink composition, i.e., the polymeric dye component in admixture with the evaporable liquid carrier component and any optional component(s) , can possess a relatively low viscosity, e.g., from about 2 to about 80,000 centipoises and preferably from about 3 to about 30,000 centipoises when water is the carrier, or a relatively high viscosity, e.g. , at least about 100,000 centipoises and preferably at least about 500,000 centipoises when the carrier is an organic solvent or mixture of organic solvents which swell or dissolve the polymer dye. It will, of course, be recognized that when the erasable ink composition possesses such a high viscosity that it no longer readily flows solely under the influence of gravity, it becomes necessary to provide a pressurized delivery system for any marking instrument containing the ink. To improve or optimize one or more functional characteristics of the erasable ink composition, one or more optional components can be added in the usual amounts to the composition, e.g., one or more natural and/or synthetic polymer latices, rheological modifiers, organic solvents, hu ectants, emulsifiers, surfactants, plasticizers, spreading agents, drying agents, release agents, parting agents, preservatives, antimicrobial agents, anticorrosion agents, antioxidants, coalescing aids, and the like. With or without the addition of any optional component(s) , the erasable ink composition when applied to a substrate, and particularly a porous substrate such as a cellulosic paper, and upon drying thereon must be (1) sufficiently adherent to the substrate as to resist flaking therefrom and (2) substantially erasable. Thus, the dry erasable ink composition of this invention applied to paper and evaluated by the adherency test described infra will generally exhibit less than about 30 weight percent flaking, preferably less than about 20 weight percent flaking and even more preferably less than about 10 weight percent flaking. Erasability values delta E*ab of the erasable ink composition herein as measured by ASTM D-2244-89 will generally be on the order of less than about 4.0, preferably less than about 3.5 and even more preferably less than about 3.0. It is preferred that the erasable ink composition herein when evaluated by the smearability test described infra exhibit a subjectively determined low level of smear, e.g., a smear value of 2 or less and preferably a smear value of 1 (i.e., essentially no smearing). The erasable ink composition of this invention is intended to be used in any of a variety of marking instruments and in particular, a ball-point pen. The following -examples are illustrative of the erasable ink composition of this invention. EXAMPLES ILLUSTRATING THE PREPARATION OF POLYESTER POLYOL DYE MONOMER Polyester polyols obtained by reacting adipic acid, hexanediol and phenyldiethanolamine were obtained from Ruco (Hicksville, NY) . These polyester polyols are identified in Table 1 below: Table 1 Monomer Radio Average Polyester (Adipic acid: phenyl Hydroxyl Molecular Polyol diethanolamine: hexanediol) Number Weight A 13:1:13 44.2 2539 B 13:1:13 33.3 3369 C 13:2:12 35.1 3197 A polyester polyol dye monomer (hereinafter "DM1") derived from polyester polyol A was formed as follows: To a three neck round bottom flask equipped with a mechanical stirrer and addition funnel was added 45g of 85% H 3 P0 4 . The reaction flask was cooled to -5°C and 26.3g (0.083 moles) of 40% nitrosylsulfuric acid was added dropwise to the reaction flask while maintaining a temperature between -5 and O'C with stirring. A slurry of 11.2g (0.069 moles) 2-amino-4-methyl-3,5-dicyanothiophene and approximately 20g 85% H 3 P0 4 was added dropwise to the reaction flask via the addition funnel over a period of 30 minutes and allowed to stir at 0°C for 1.5 hours to provide a diazonium salt solution. After 1.5 hours, the presence of excess nitration species was determined qualitatively utilizing starch/iodide paper and any excess nitration species was removed by adding to the mixture a water solution of urea or sulfamic acid. The diazonium -salt solution was transferred via cannula to a solution of acetonitrile (400 ml) and 182.7g (0.072 moles) of polyester polyol A at O'C with stirring. The reaction mixture was allowed to come to room temperature and stirred for 2 hours. The reaction mixture was neutralized using caustic. The solvent was removed under vacuum and a reddish-violet solid was obtained. This polyester polyol dye monomer was washed free of salts and other soluble materials with hot water. A polyester polyol dye monomer (hereinafter "DM2") derived from polyester polyol B was formed as follows: To a three neck round bottom flask equipped with a mechanical stirrer and addition funnel was added 45g of 85% H 3 P0 4 . The reaction flask was cooled to -5'C and 15.51g (0.049 moles) of 40% nitrosylsulfuric acid was added dropwise to the reaction flask while maintaining a temperature between -5 and O'C with stirring. A slurry of 6.88g (0.042 moles) 2-amino-4-methyl-3,5-dicyanothiophene and approximately 20g 85% H 3 P0 4 was added dropwise to the reaction flask via the addition funnel over a period of 30 minutes and allowed to stir at O'C for 1.5 hours to provide a diazonium salt solution. After 1.5 hours, the presence of excess nitration species was determined qualitatively utilizing starch/iodide paper and any excess nitration species was removed by adding to the mixture a water solution of urea or sulfamic acid. The diazonium salt solution was transferred via cannula to a solution of acetonitrile (400 ml) and 500g (0.148 moles) of polyester polyol B at O'C with stirring. The reaction mixture was allowed to come to room temperature and stirred for 2 hours. The reaction mixture was neutralized using caustic. The solvent was removed under vacuum and a reddish-violet solid was obtained. This polyester polyol dye monomer was washed free of salts and other soluble materials with hot water. A polyester polyol dye monomer (hereinafter "DM3") derived from polyester polyol C was formed as follows: To a three neck round bottom flask equipped with a mechanical stirrer and addition funnel was added 45g of 85% H 3 P0 4 . The reaction flask was cooled to -5°C and 21.30g (0.067 moles) of 40% nitrosylsulfuric acid was added dropwise to the reaction flask while maintaining a temperature between -5 and O'C with stirring. A slurry of 11.16g (0.061 moles) 2,4-dinitroaniline and 30g of 85% H 3 P0 4 was added dropwise to the reaction flask via the addition funnel over a period of 30 minutes and allowed to stir at O'C for 2 hours to provide a diazonium salt solution. After 2 hours, the presence of excess nitration species was determined qualitatively utilizing starch/iodide paper and any excess nitration species was removed by adding to the mixture a water solution of urea or sulfamic acid. The diazonium salt solution was transferred via cannula to a water (500 ml) slurry of 300g (0.093 moles) of finely ground polyester polyol C at O'C with stirring. The reaction mixture was allowed to come to room temperature and stirred for 2 hours. The reaction slurry was neutralized using caustic. A red solid was obtained. This polyester polyol dye monomer was collected via filtration and washed several times with hot water to remove salts and other water soluble material. A polyester polyol dye monomer (hereinafter "DM4") derived from polyester polyol C was formed as follows: To a three neck round bottom flask equipped with a mechanical stirrer and addition funnel was added 45g of 85% H 3 P0 4 . The reaction flask was cooled to -5'C and 54.62g (0.1721 moles) of 40% nitrosylsulfuric acid was added dropwise to the reaction flask while maintaining a temperature between -5 and O'C with stirring. A slurry of 28.86g (0.156 moles) 2-amino-4-chlorobenzothiazole and 30g of 85% H 3 P0 4 was added dropwise to the reaction flask via the addition funnel over a period of 30 minutes and allowed to stir at O'C for 2 hours to provide a diazonium salt solution. After 2 hours, the presence of excess nitration species was determined qualitatively utilizing starch/iodide paper and any excess nitration species was removed by adding to the mixture a water solution of urea or sulfamic acid. The diazonium salt solution was transferred via cannula to water (500 ml) slurry of 500g (0.1564 moles) of finely ground polyester polyol C at O'C with stirring. The reaction mixture was allowed to come to room temperature and stirred for 2 hours. The reaction slurry was neutralized using caustic. A red solid was obtained. This polyester polyol dye monomer was collected via filtration and washed several times with hot water to remove salts and other water soluble material. A polyester polyol dye monomer (hereinafter "DM5") derived from polyester polyol C was formed as follows: To a three neck round bottom flask equipped with a mechanical stirrer and addition funnel was added 45g of 85% H 3 P0 4 . The reaction flask was cooled to -5'C and 38.2g (0.12 moles) of 40% nitrosylsulfuric acid was added dropwise to the reaction flask while maintaining a temperature between -5 and O'C with stirring. A slurry of 28.55g (0.109 moles) 2-bromo-4,6-dinitroaniline and 30g of 85% H 3 P0 4 was added dropwise to the reaction flask via the addition funnel over a period of 30 minutes and allowed to stir at O'C for 2 hours to provide a diazonium salt solution. After 2 hours, the presence of excess nitration species was determined qualitatively utilizing starch/iodide paper and any excess nitration species was removed by adding to the mixture a water solution of urea or sulfamic acid. The diazonium salt solution was transferred via cannula to a water (500 ml) slurry of 500g (0.156 moles) of finely ground polyester polyol C at O'C with stirring. The reaction mixture was allowed to come to room temperature and stirred for 2 hours. The reaction slurry was neutralized using caustic. A red solid was obtained. This polyester polyol dye monomer was collected via filtration and washed several times with hot water to remove salts and other water soluble material. Waterborne polyurethane-urea dispersions were obtained from polyester polyol dye monomers DM1, DM2, DM3, DM4 and DM5, employing the pre-polymer mixing process, as follows: EXAMPLE 1 To a 2000 mL resin kettle equipped with an addition funnel, nitrogen inlet and mechanical stirrer was added DM5 (205.58g) , dimethylolpropionic acid (DMPA) (8.99g) (dissolved in 20g N-methyl pyrollidone) and dibutyltindilaurate (Fastcat 4202) catalyst (0.38g) . The reaction mixture was heated to 60-70'C with stirring and isopherone diisocyanate (IPDI) (42.4g) was added over a period of 20-30 minutes to form a red colored isocyanate group-terminated prepolymer possessing free carboxyl groups. The prepolymer was stirred for 3-5 hours at temperature and the %NCO was monitored. When the theoretical %NCO was reached, triethylamine (5.91g) was added to the colored prepolymer and allowed to stir at temperature for 30 minutes. The self-dispersible prepolymer was dispersed in a sufficient amount of water using an impeller-type dispersion blade to provide a 35-50% solids dispersion. The dispersed prepolymer was then allowed to chain extend with water at 40°C to provide a red dispersion of polyurethane-urea particles possessing an average particle size of less than about 0.1 micron. The above-described process was repeated to form Examples 2-8 as summarized in Table 2 as follows: Table 2 Polyester polyol dye monomer/ Isocyanate/ Triethyl- Example amount (a) amount(σ. DMPAfσi amine(cr) Color 2 DM1/ m-TMXDI*/ 7.61 5.74 Violet 167.43 42.0 3 DM1/ m-TMXDI/ 8.60 6.48 Violet 194.79 42.0 4 DM2/ m-TMXDI/ 8.25 6.21 Violet 82.44 42.0 5 DM3/ IPDI/ 8.37 6.95 Red 228.36 42.4 6 DM4/ IPDI/ 8.59 6.78 Red 205.58 42.4 7 DM4/ IPDI/ 15.65 5.89 Red 129.71 42.4 8 DM5/ IPDI/ 10.60 7.99 Red 249.86 42.4 *m-TMXDI= l, 3-bis(l-isocyanato-l-methylethyl) -benzene The waterborne polyurethane-urea polymer dyes utilized in the erasable ink composition herein are less expensive to fabricate, possess superior oxidative stability and superior thermal stability compared to polyurethane-urea polymer dyes fabricated from colored polyether polyols such as the polyether polyols described in U.S. Patent No. 5,231,135. Furthermore, the polyurethane-urea dispersions fabricated from the polyester polyol dye monomers disclosed herein possess superior properties, e.g., water-fastness, compared to polyurethane-urea dispersions fabricated from the colored polyether polyols disclosed in U.S. Patent No. 5,231,135. EXAMPLES ILLUSTRATING THE PREPARATION OF POLYFUNCTIONAL PREPOLYMERS POSSESSING COVALENTLY BONDED DYE MOIETY EXAMPLE 9 Di ethylolpropionic acid (8.25g) was dissolved in N-methyl pyrollidone (13.8g). To this solution, polytetramethylene glycol (TERETHANE T-2900 from Dupont) (208.2g), polyol colorant (15.Og) corresponding to Colorant C from Table I of U.S. Patent No. 5,231,135, isopherone diisocyanate (42.40g) and dibutyltindilaurate catalyst (0.72g) were added. The solution was heated to a temperature of from about 60 to about 70*C for about 3 to about 5 hours under stirring. The color of the resulting isocyanate group- terminated prepolymer having dye covalently bonded thereto was red. EXAMPLE 10 Dimethylolpropionic acid (7.37g) was dissolved in N-methyl pyrollidone (12.31g). To this solution, polytetramethylene glycol (TERETHANE T-2900 from Dupont) (151.2g) and polybutylene glycol (BO-4800 from Dow Chemical) (84.0g), polyol colorant (5.0g) corresponding to Colorant C from Table I of U.S. Patent No. 5,231,135, isopherone diisocyanate (42.40g) and dibutyltindilaurate catalyst (0.48g) were added. The solution was heated to a temperature of from about 60 to about 70°C for about 3 to about 5 hours under stirring. The color of the resulting isocyanate group- terminated prepolymer having dye covalently bonded thereto was red. EXAMPLE 11 Dimethylolpropionic acid (3.50g) was dissolved in N-methyl pyrollidone (5.84g). To this solution, polytetramethylene glycol (TERETHANE T-2900 from Dupont) (305.9g), polyol colorant (5.0g) corresponding to Colorant U from Table I of U.S. Patent No. 5,231,135, polyol colorant (5.0g) corresponding to Colorant G from Table I of U.S. Patent No. 5,231,135, isopherone diisocyanate (42.40g) and dibutyltindilaurate catalyst (0.12g) were added. The solution was heated to a temperature of from about 60 to about 70°C for about 3 to about 5 hours under stirring. The color of the resulting isocyanate group-terminated prepolymer having dye covalently bonded thereto was violet-blue. EXAMPLE 12 Dimethylolpropionic acid (8.08g) was dissolved in N-methyl pyrollidone (13.5g). To this solution, polytetramethylene glycol (TERETHANE T-2900 from Dupont) (184.5g), polyol colorant (5.0g) corresponding to Colorant C from Table I of U.S. Patent No. 5,231,135, isopherone diisocyanate (42.40g) and dibutyltindilaurate catalyst (0.48g) were added. The solution was heated to a temperature of from about 60 to about 70°C for about 3 to about 5 hours under stirring. The color of the resulting isocyanate group- terminated prepolymer having dye covalently bonded thereto was red. EXAMPLE 13 Dimethylolpropionic acid (8.08g) was dissolved in N-methyl pyrollidone (13.5g). To this solution, polytetramethylene glycol (TERETHANE T-2900 from Dupont) (174.6g), polyol colorant (5.0g) corresponding to Colorant C from Table I of U.S. Patent No. 5,231,135, isopherone diisocyanate (42.40g) and dibutyltindilaurate catalyst (0.48g) were added. The solution was heated to a temperature of from about 60 to about 70°C for about 3 to about 5 hours under stirring. The color of the resulting isocyanate group- terminated prepolymer having dye covalently bonded thereto was red. EXAMPLE 14 Isopherone diisocyanate (42.40g) and polytetramethylene glycol (TERETHANE T-2900 from Dupont) (174.6g) were admixed. To this mixture, polyol colorant (5.0g) corresponding to Colorant U from Table I of U.S. Patent No. 5,231,135, was added. The mixture was dissolved in methylenthylketone (120g) and dibutyltindilaurate catalyst (0.24g) was added to the solution which was stirred at room temperature overnight. The color of the resulting isocyanate group-terminated prepolymer having dye covalently bonded thereto was violet. EXAMPLES ILLUSTRATING THE PREPARATION OF POLYMER DYES EXAMPLE 15 The prepolymer mixing process was carried out as follows: the prepolymer of Example 9 was reacted with triethyl amine (6.22g) neutralizing agent to convert the carboxyl groups in the prepolymer to ammonium carboxylate groups and render the prepolymer self-dispersible. Thereafter, the self-dispersible prepolymer was dispersed in water (241g) using an impeller-type dispersion blade. The dispersed prepolymer was then reacted at room temperature with hydrazine (3.93g) chain extender to provide a dispersion of polyurethane-urea particles of approximately 55.0 weight percent solids. EXAMPLE 16 The prepolymer mixing process was carried out as follows: the prepolymer of Example 10 was reacted with triethyl amine (5.60g) neutralizing agent to convert the carboxyl groups in the prepolymer to ammonium carboxylate groups and render the prepolymer self-dispersible. Thereafter, the self-dispersible prepolymer was dispersed in water (300g) using an impeller-type dispersion blade. The dispersed prepolymer was then reacted at about 76° with hydrazine (5.76g) chain extender to provide a dispersion of polyurethane-urea particles of approximately 50.7 weight percent solids. EXAMPLE 17 The prepolymer mixing process was carried out as follows: the prepolymer of Example 11 was reacted with triethyl amine (2.64g) neutralizing agent to convert the carboxyl groups in the prepolymer to ammonium carboxylate groups and render the prepolymer self-dispersible. Thereafter, the self-dispersible prepolymer was dispersed in water (436g) using an impeller-type dispersion blade. The dispersed prepolymer was then reacted at room temperature with hydrazine (1.49g) chain extender to provide a dispersion of polyurethane-urea particles of approximately 45.9 weight percent solids. EXAMPLE 18 The prepolymer mixing process was carried out as follows: the prepolymer of Example 12 was reacted with triethyl amine (6.09g) neutralizing agent to convert the carboxyl groups in the prepolymer to ammonium carboxylate groups and render the prepolymer self-dispersible. Thereafter, the self-dispersible prepolymer was dispersed in water (300g) using an impeller-type dispersion blade. The dispersed prepolymer was then reacted at room temperature with hydrazine (5.82g) chain extender to provide a dispersion of polyurethane-urea particles of approximately 46.4 weight percent solids. EXAMPLE 19 The prepolymer mixing process was carried out as follows: the prepolymer of Example 13 was reacted with triethyl amine (6.09g) neutralizing agent to convert the carboxyl groups in the prepolymer to ammonium carboxylate groups and render the prepolymer self-dispersible. Thereafter, the self-dispersible prepolymer was dispersed in water (300g) using an impeller-type dispersion blade. The dispersed prepolymer was then reacted at room temperature with hydrazine (5.82g) chain extender to provide a dispersion of polyurethane-urea particles of approximately 46.9 weight percent solids. EXAMPLE 20 The solvent process was carried out as follows: the prepolymer of Example 14 dissolved in methyleneketone wa reacted at room temperature with hydrazine (2.15g) chain extender to provide an organic solvent solution of polyurethane-urea of approximately 64.9 weight percent solids. The properties of the polymer dyes of Examples 15-20 are presented in Table 3 as follows: Table 3 Average Particle Example Size (Dry) (nm) Color (Dry) V°C) 15 50 - 500 Red <60 16 250 Red <60 17 250 - 2000 Violet-blue <60 18 150 Red <60 19 150 Red <60 20 N/A Violet <60 (solution) The polymer dye compositions of Examples 15-20 can be directly employed as erasable ink compositions or be combined with one or more optional components such as an emulsion prior to being employed as erasable ink compositions. To further illustrate the erasable ink composition of this invention, the polymer dye of Example 15 was combined with a silicone emulsion, i.e., SWS-233 Silicone Emulsion from Wacker Chemical Corp., to provide an erasable ink composition (Example 21) containing 90 weight percent polymer dye and 10 weight percent silicone emulsion. In another example, the polymer dye of Example 17 was combined with an emulsion containing 25.0 weight percent sorbitan sesquaoleate, i.e., Glycomol SOC from Lonza, 1.67 weight percent sodium dodecylbenzenesulfonate, i.e., Rhodocal DS4 from Rhone Poulenc, and 71.66 weight percent water to provide an erasable ink composition (Example 22) containing 90 weight percent polymer dye and 10 weight percent of the emulsion. The properties of the erasable ink composition of Examples 21 and 22 were evaluated. In particular, the color intensity, viscosity, adherency, erasability and smearability of the erasable ink composition were evaluated. Color intensity was evaluated by a subjective visual evaluation of script. Adherency was determined by performing a drawdown on preweighed Linetta drawdown paper with approximately 0.8g of sample (spread over an area of inch x W inch) and drawn down with a #6 eater-bar. The sample was allowed to dry completely (approximately 5 minutes at room temperature) and the paper was weighed again. The paper was then crumpled by hand to approximately the same extent for each sample tested, thereafter uncrumpled, any flakes were blown off and the paper was reweighed. This test was also performed with erasable ink made according to U.S.. Patent Nos. 5,120,359 and 5,203,913 (Comparative Example 1) . 6/18697 Erasability was determined by performing an actual "WRITE-TEST" (similar to a spirograph wherein ink is applied in a circular arrangement on paper with some cross-over of ink occurring) with ball-point pens containing the erasable ink composition of Examples 21 and 22 and the following commercially available pens which contain erasable ink: Pen Ink Color Comparative Example Erasermate Blue 2 Erasermate 2 Blue 3 Scripto Blue 4 Scripto Red 5 The "WRITE-TEST" write-downs were then erased and reflectance measurements were performed on the erased portion of the paper versus an unblemished/untouched portion of the paper. A quantitative value was then obtained, i.e., delta E*ab from CIE lab measurement (described in ASTM D-2244-89) . Lower values indicate more complete erasures. Smearability was subjectively evaluated for the erasable ink composition of Examples 21 and 22 and Comparative Examples 2-5 1-2 seconds after writing by attempting to smudge the ink with one's fingers. A smear value of l represents essentially no smearing and a smear value of 5 represents such a degree of smearing that legibility of the writing is significantly impaired. Table 4 below presents the properties of the erasable ink compositions: Table 4 (Wt. % of Dried Ink Composition Erasability Color Viscosity Retained on Value Smear Example Intensitv (cos) the PaDerl {delta E*abϊ Value 21 Comparable to -3-5 100% 3.17 1 Comparative Examples 22 Comparable to -3-5 100% 1.44 1 Comparative Examples Comp. Ex. 1 - - 63% - - Comp. Ex. 2 - - - 3.3 2 Comp. Ex. 3 - - - 3.63 2 Comp. Ex. 4 - - - 5.38 3 Comp. Ex. 5 - - - - 4 The data in Table 4 clearly demonstrate the superiority of the erasable ink composition of this invention relative to commercially available erasable inks. The erasable ink composition of this invention is highly adherent to a substrate as to resist flaking therefrom and substantially erasable. While this invention has been disclosed herein in connection with certain embodiments and certain procedural details, it is clear that changes, modifications or equivalents can be used by those skilled in the art. Accordingly, such changes within the principles of this invention are intended to be included within the scope of the claims below.

Claims: 6/18697 WHAT IS CLAIMED IS: 1. An erasable ink composition which comprises (a) a water-insoluble polymer dye obtained by affecting polymerization of a polymer-forming reaction medium containing at least two coreactive polyfunctional monomers with at least one of the monomers possessing a dye moiety covalently bonded thereto and (b) an evaporable liquid carrier in which the polymer dye is dissolved, dispersed or swollen, the erasable ink composition when applied to a substrate and upon drying thereon being (1) sufficiently adherent to the substrate as to resist flaking therefrom and (2) substantially erasable. 2. The erasable ink composition of Claim 1 exhibiting less than about 30 weight percent flaking and an erasability value delta E*ab of less than about 4.0. 3. The erasable ink composition of Claim 1 wherein the monomer possessing a dye moiety covalently bonded thereto corresponds to the general formula (Kτ- a -fP X] b ) c wherein R is a dye moiety covalently bonded to polymer residue P, X is a functional group, a, b and c each is at least 1, provided, the product of b x c is at least 2, when c is at least 2, a is 1 and where there is more than one R, P or X, each R, P or X can be the same or different. 4. The erasable ink composition of Claim 1 wherein the polymer dye is a waterborne polymer. 5. The erasable ink composition of Claim 1 wherein the polymer dye is a waterborne polyurethane-urea. 6. The erasable ink composition of Claim 5 wherein the waterborne polyurethane-urea is obtained by the solvent process, the melt dispersion process, the prepolymer mixing process or the ketamine/ketazine process. 7. The erasable ink composition of one of Claims 1 to 6 wherein the polymer dye includes structural units of the general formula: wherein each A independently can be an ester or amide linkage, n can be an integer of from about 1 to about 50, R is an aliphatic or aromatic hydrocarbon with up to about 30 carbon atoms, a and b are independently from 1 to about 10, Z is a substituted or unsubstituted arylene group or a single bond when Y is an anthraquinone group and Y is selected from the group consisting of an azo, tricyanovinyl, anthraquinone and methine group. 8. The erasable ink composition of one of Claims 1 to 7 wherein the composition further comprises at least one additional component selected from the group consisting of natural laticeε, synthetic latices, rheological modifiers, suspension agents, organic solvents, humectants, emulsifiers, surfactants, plasticizers, spreading agents, drying agents, release agents, parting agents, preservatives, antimicrobial agents, anticorrosion agents, antioxidants and coalescing aids. 9. A marking instrument containing the erasable ink composition of one of Claims 1 to 8. 10. A waterborne polyurethane-urea obtained by affecting polyermization of a polymer-forming reaction medium containing at least two coreactive polyfunctional monomer with at least one of the monomers possessing a dye moiety covalently bonded thereto under waterborne polymer-forming reaction conditions. 11. A polymer containing structural units of the general formula: wherein each A independently can be an ester or amide linkage, n can be an integer of from about 1 to about 50, R is an aliphatic or aromatic hydrocarbon with up to about 30 carbon atoms, a and b are independently from 1 to about 10, Z is a substituted or unsubstituted arylene group or a single bond when Y is an anthraquinone group and Y is selected from the group consisting of an azo, tricyanovinyl, anthraquinone and methine group.

Inventors: BANNING JEFFERY H, CHADWICK BARRY W, CHANDLER WAYNE A, VILLIGER DAVID C, WANG AIYING, BANNING, JEFFERY, H., CHADWICK, BARRY, W., CHANDLER, WAYNE, A., VILLIGER, DAVID, C., WANG, AIYING
Applicants: BIC CORP, BIC CORPORATION
Application year: 1995
Main classification: C09D11
IPC codes: C08G18, C08G63, C09B69, C09D11