Semiconductor device and its fabrication process

Abstract: The invention provides a semiconductor device having a structure wherein a layer comprising at least Al W Ga 1-W As is formed on a substrate and a second etching stop layer, a first etching stop layer and a layer comprising Al Y Ga 1-Y As are deposited on the layer comprising Al W Ga 1-W As in the described order, with a portion of the layer comprising Al Y Ga 1-Y As and a portion of the first etching stop layer being removed. This structure enables a desired ridge or groove shape to be fabricated with good quality and allows for free selection of the Al mixed crystal ratio of the layer to be etched, and makes it possible to form the re-growth interface of GaAs. Thus, the qualty of crystal of the re-grown portion can be improved.

Description: The present invention relates generally to a semi-conductor device and its fabrication process, and more specifically to a semiconductor device having a ridge or groove formed by making use of an etching stop layer and its fabrication process. Ridged or grooved semiconductor devices are fabricated by etching away a portion of an upper clad layer located above an active layer. Such semiconductor devices may be fabricated, with high reproducibility, by locating an etching stop layer between an active layer and an upper clad layer. These semiconductor devices are primarily suitable for use as optical devices. In a conventional process so far known to form ridges or grooves, AlGaAs with an Al concentration of about 0.5 or more is etched by using hot hydrochloric acid, etc., as an etchant, while GaAs is used as an etching stop layer. As proposed in JP-A 5(1993)-259574, on the other hand, there is available a semiconductor light emitting device fabricated by making use of an etching stop layer, in which a first conduction type substrate has thereon a first conduction type of lower clad layer, an active layer, a second conduction type of first upper clad layer comprising Al X Ga 1-X As, a second conduction type of etching stop layer comprising Al Y Ga 1-Y As and a second conduction type of second upper clad layer comprising Al Z Ga 1-Z As in the described order, with the first upper clad layer having a mixed crystal ratio X of 0.38 to 0.6, the etching stop layer having an Y of at least 0.6, and the second upper clad layer having an Z of 0.38 to 0.6. The formation of precisely shaped ridges or grooves may be achieved by dry etching techniques. However, the above-described process have a number of difficulties. JP-A 5-259574 mentioned just above discloses a process for the fabrication of a semiconductor optical device, which makes use of the resistance of AlGaAs having an Al concentration of at least 0.6 to an aqueous etchant of an organic acid and hydrogen peroxide, and involves the step of treating the second upper clad layer with this wet etchant to form a ridge. A problem with this process is, however, that AlGaAs having an Al concentration of at least 0.6, which is susceptible to oxidation, remain on the surface where to be regrowth performed, and the resulting epitaxial layer contains much defects. The desired ridge shape may prima facie be obtained by the dry etching techniques. However, the dry etching techniques are less suitable for optical semiconductor device fabrication, because crystal defects are likely to occur. It is thus demanded to achieve an etching stop layer that enables the desired ridge shape to be produced with good quality and allow for free selection of the Al concentration of the layer to be etched. EP-A-0 452 146 defines a semiconductor device having the features of the preamble of claim 1. An object of the present invention is to exploit the diversity of an optical semiconductor device with a ridge or groove current injection area. Another object of the present invention is to provide a process for wet etching a layer comprising Al Y Ga 1-Y As having any desired Al concentration for the precise formation of a ridge or groove having any desired shape, and to provide a semiconductor device fabricated by using such a process. The invention is defined in claims 1 and 4. Various embodiments are defined in the dependent claims. The semiconductor device of the present invention is also characterized in that the second etching stop layer comprises GaAs and the first etching stop layer comprises Al X Ga 1-X As, and by conforming to the following condition: X-Y ≥ 0.1 Moreover, the semiconductor device of the present invention is characterized in that the second etching atop layer comprises Al Z Ga 1-Z As or GaAs and said first etching stop layer comprises In V Ga 1-V P. The process for semiconductor device fabrication according to the present invention is characterized by involving the steps of forming a layer comprising at least Al W Ga 1-W As on a substrate and growing a second etching stop layer, a first etching stop layer and a layer comprising Al Y Ga 1-Y As on said layer comprising Al W Ga 1-W As in the described order by a epitaxial growth technique, and of etching away a portion of said layer comprising Al Y Ga 1-Y As using said first etching stop layer as an etching stop layer and then etching away a portion of said first etching stop layer using said second etching stop layer as an etching stop layer, thereby forming a ridge or groove. The process for semiconductor device fabrication according to the present invention is also characterized in that the second etching stop layer comprises GaAs and the first etching layer comprises Al X Ga 1-X As. The process for semiconductor device fabrication according to the present invention is further characterized in that the second etching stop layer comprises Al Z Ga 1-Z As or GaAs and the first etching stop layer comprises In V Ga 1-V P. FIG. 1 is a schematic of one example of the grooved epitaxial structure for the semiconductor laser diode according to the present invention. Fig. 2 is a first schematic of the process of fabricating the semiconductor laser diode shown in FIG. 1. Fig. 3 is a second schematic of the process of fabricating the semiconductor laser diode shown in FIG. 1. Fig. 4 is a third schematic of the process of fabricating the semiconductor laser diode shown in FIG. 1. Fig. 5 is a fourth schematic of the process of fabricating the semiconductor laser diode shown in FIG. 1. Fig. 6 is a fifth schematic of the process of fabricating the semiconductor laser diode shown in FIG. 1. Fig. 7 is a sixth schematic of the process of fabricating the semiconductor laser diode shown in FIG. 1. FIG. 8 is a schematic of one example of the ridged epitaxial structure of the semiconductor laser diode according to the present invention. Fig. 9 is a first schematic of the process of fabricating the semiconductor laser diode shown in FIG. 8. Fig. 10 is a second schematic of the process of fabricating the semiconductor laser diode shown in FIG. 8. Fig. 11 is a third schematic of the process of fabricating the semiconductor laser diode shown in FIG. 8. Fig. 12 is a fourth schematic of the process of fabricating the semiconductor laser diode shown in FIG. 8. Fig. 13 is a fifth schematic of the process of fabricating the semiconductor laser diode shown in FIG. 8. Fig. 14 is a sixth schematic of the process of fabricating the semiconductor laser diode shown in FIG. 8. Fig. 15 is a seventh schematic of the process of fabricating the semiconductor laser diode shown in FIG. 8. The process of the present invention may be applied to optical semiconductor devices such as FETs and HBTs, but is preferably applied to an optical semiconductor device, especially semiconductor laser diodes. In the semiconductor device of the present invention, the substrate material is usually a so-called single crystalline wafer of the III-V group compounds. The wafer is obtained by the slicing of the III-V group single crystalline compounds, especially bulk crystals of compounds of the IIIb and Vb group elements in the periodic table. The substrate material used herein is a wafer selected from the group consisting of GaP, GaAs, and InP, among which GaAs is particularly preferred in view of lattice constant matching. The semiconductor device of the present invention has a structure including a layer comprising at least Al W Ga 1-W As on a substrate and having a second etching stop layer, a first etching stop layer and a layer comprising Al Y Ga 1-Y As grown on the layer comprising Al W Ga 1-W As in the described order, with a portion of the layer comprising Al Y Ga 1-Y and a portion of the first etching stop layer being removed. The semiconductor device of the present invention has preferably the second and first etching stop layers comprising GaAs and Al X Ga 1-X As, respectively, and conforms to the following condition: X - Y ≥ 0.1 Furthermore in the semiconductor device of the present invention, it is preferable that the second etching stop layer comprises Al Z Ga 1-Z As or GaAs and the first etching stop layer comprises In V Ga 1-V P. It is here to be noted that the removal of the etching stop layers is preferably achieved by wet etching. FIG. 1 is a schematic of a semiconductor laser diode fabricated as an example of the epitaxial structure of the semiconductor device according to the present invention. In FIG. 1 reference numeral 1 represents a substrate; 2 a buffer layer; 3 a lower clad layer; 4 an active layer; 5 a first upper clad layer; 6 a second etching stop layer; 7 a first etching stop layer; 8 a second upper clad layer; 9 a current blocking layer; 10 a cap layer; 11 a contact layer; and 12 and 13 electrodes. It is the first upper clad layer 5 that comprises Al W Ga 1-W As, and the current blocking layer 9 is a layer comprising Al Y Ga 1-Y As. The respective layers of the semiconductor device according to the present invention are formed over the substrate in the form of epitaxial thin films. A first upper clad layer 5 may be disposed directly on the substrate and preferably, a layer of an identical composition with that of the substrate is formed on the substrate as a buffer layer 2. Since the single crystals used for the substrate 1 usually have a number of defects and such defects reflect to the layer formed thereon and greatly lowers the performance as the semiconductor laser diode, the buffer layer 2 is disposed in order to inhibit these disadvantages. The lower clad layer 3 is usually made of a material having a refractive index lower than that of the active layer 4. When GaAs is used for the buffer layer 2, an AlGaAs system (Al V Ga 1-V As) is used for the lower clad layer 3, and the Al concentration may then be determined such that the refractive index of the lower clad layer 3 meets the above-described condition. The active layer 4 may be made of GaAs, AlGaAs, InGaAs, InGaAsP and other materials, and may have a structure such as various quantum well structures (SQW, MQW) comprising thin films of the above materials. The quantum well structure is ordinarily used in combination with optical guide layers. The optical guide layer arrangement used herein, for instance, may have an SCH structure wherein optical guide layers are formed on both sides of the active layer or a GRIN-SCH structure wherein the refractive index of an optical guide layer is continuously changed by the gradual changing of the composition of the optical guide layer. The material and structure of the active layer 4 may be determined depending on the desired center wavelength and output. The first upper clad layer 5 is usually made of a material having a refractive index lower than that of the active layer 4. Then, the first upper clad layer 5 is usually identical in the refractive index with the lower clad layer 3. Thus, the first upper clad layer 5 is usually made of an AlGaAs system as in the case of the lower clad layer 3, and has the same Al concentration as in the lower clad layer 3. In this structure, it is the first upper clad layer 5 that corresponds to the layer comprising Al W Ga 1-W As. The second etching stop layer 6 is made of an AlGaAs material, but it is usually preferable to use GaAs therefor. This is because MOCVD or other techniques can be used for the re-growth of the second upper clad layer, etc., on the second etching stop layer 6 with high quality of crystal. Usually, the second etching stop layer 6 has preferably a thickness of at least 2 nm. The first etching stop layer 7 has a thickness of at least 5 nm, preferably at least 10 nm. At a thickness less than 5 nm, no sufficient inhibition of etching is achieved. The composition of this layer is represented by In V Ga 1-V P or Al X Ga 1-X As. When In V Ga 1-V P is used, V = 0.5 is preferably used for a lattice matched for GaAs. However, 0 ≦ V ≦ 1 except V = 0.5 can also be used for a strained system. When Al X Ga 1-X As is used, on the other hand, the value of x may be determined in view of Al Y Ga 1-Y As forming the current blocking layer and the condition of X - Y ≥ 0.1, thereby achieving sufficient etching stop function. The current blocking layer blocks currents or conducts no currents substantially. Therefore, the current blocking layer has the same conduction type as in the lower clad layer or may be undoped. The current blocking layer has a refractive index lower than that of the second upper clad layer 8 (Al T Ga 1-T As). Hence, the Al concentration should be given by Y > T. The cap layer 10 is used as a protection layer for the current blocking layer 9 at the first growth step. The cap layer 10 also helps a growth of the second upper clad layer 8. A portion of the cap layer 10 is removed during the fabrication process. For removing portions of the cap and current blocking layers 10 and 9, an organic acid and an aqueous solution of hydrogen peroxide are used in a mixed form. In this case, the mixing ratio of the organic acid and the aqueous solution of hydrogen peroxide and the concentration of the aqueous solution may be determined by the materials of which the current blocking layer 9 and the first etching stop layer 7 are made. Although not critical, however, it is preferable that the mixing ratio of hydrogen peroxide to the organic acid is selected from the range of 1/10 to 1/50 (by weight). Then, the organic acid and hydrogen peroxide are used in an aqueous solution form having a concentration of 30 to 50% by weight. It is here to be noted that etching occurs usually at normal temperature. Furthermore, a portion of the first etching stop layer is removed using the second etching stop layer 6 as an etching stop layer. Usually, the index of refraction of the second upper clad layer 8 is equal to, or lower than, that of the active layer 4. Usually, the second upper clad layer 8 is identical in the refractive index with the lower clad layer 3 and the first upper clad layer 5. On the second upper clad layer 8 there is provided the contact layer 11 used for lowering the contact resistivity to the electrode. The contact layer 11 is usually made of a GaAs material. To lower the contact resistivity to the electrode, this layer usually has a carrier concentration higher than those of other layers. Usually, the buffer layer 2 has a thickness selected from the range of 0.1 to 1 µm; the lower clad layer 3 has a thickness of 0.5 to 3 µm; the active layer 4 has a thickness of 0.005 to 0.02 µm per layer if it has a quantum well structure; the first upper clad layer 5 has a thickness of 0.05 to 0.3 µm; the second upper clad layer 8 has a thickness of 0.5 to 3 µm; the cap layer 10 has a thickness of 0.005 to 0.5 µm; and the current blocking layer 9 has a thickness of 0.3 to 2 µm. The semiconductor laser diode shown in FIG. 1 further includes electrodes 12 and 13. The electrode 12, when it is of the p-type, is typically provided on the surface of the contact layer 11 by forming Ti/Pt/Au thereon in the described order by evaporation, followed by alloying treatments. On the other hand, the electrode 13, when it is of the n-type, is typically provided on the surface of the wafer 1 by forming AuGe/Ni/Au thereon in the described order by evaporation, followed by alloying treatments. One example of the process for fabricating a semiconductor laser diode device according to the present invention will now be explained with reference to FIG. 1. According to the present invention, the buffer layer 2, lower clad layer 3, active layer 4, first upper clad layer 5, second etching stop layer 6, first etching stop layer 7, current blocking layer 9 and cap layer 10 are grown over the substrate 1 using MOCVD, MBE, LPE or other techniques, depending to the thicknesses of the layers to be grown. After an SiNx or other mask is formed on the cap layer 10, portions of the current blocking layer 9 and cap layer 10 are removed by wet etching until the first etching stop layer 7 is exposed, thereby obtaining the desired structure. In this step, any etchant which etches Al Y Ga 1-Y As and does not etch In V Ga 1-V P or Al X Ga 1-X As can be used. When the first etching stop layer is made of In V Ga 1-V P, it is preferable to use a mixture of sulfuric acid and an aqueous solution of hydrogen peroxide as the etchant. Although what ratio they are mixed at is not critical, it is preferable that water account for at least 50% by volume of the etchant to control the etching rate. When the first etching stop layer is made of Al X Ga 1-X As, the mixing ratio of an organic acid and an aqueous solution of hydrogen peroxide is determined such that a portion of the current blocking layer of Al Y Ga 1-Y As is etched away while Al X Ga 1-X As remains intact. The etchant preferable to this end is a mixture of tartaric acid and an aqueous solution of hydrogen peroxide. In this case, the mixed ratio of the tartaric acid and the aqueous solution of hydrogen peroxide is selected suitable for the value of X and Y. However, it is preferable that water accounts for at least 50% by volume of the etchant to control the etching rate. Once the first etching stop layer has been exposed by etching, only an exposed portion of the first etching stop layer is etched away. The etchant used herein should not etch the materials forming the second etching stop, current blocking layer and cap layers. For this etchant, for instance, use may be made of low-concentration hydrochloric acid, hot hydrochloric acid, and hot phosphoric acid. More specifically, when the first etching stop layer is made of In V Ga 1-V P, the first etching stop layer alone can be selectively etched away by use of low-concentration hydrochloric acid. Then, the current blocking layer 9 functions as an etching mask for the first etching stop layer 7, so that high precision control of transverse dimensions can be achieved with no side-etching. When the first etching stop layer 7 is made of Al X Ga 1-X As, on the other hand, Al X Ga 1-X As where X ≥ 0.5 can be selectively etched away by use of hot hydrochloric acid, hot phosphoric acid or the like. The second upper clad layer 8 and the contact layer 11 are then formed thereon again by an epitaxial growth technique, followed by the formation of the electrode on the contact layer 11. The thus fabricated semiconductor wafer is divided into chips each for use as a laser diode (LD). While the present invention has been described typically with reference to a laser diode, it is to be understood that the present invention is applicable to various semiconductor devices required to have a precise ridge or groove shape, inclusive of light emitting diode (LED). By way of example, the present invention will now be explained at great length. Example 1 The laser diode with a groove current injecton area, shown in FIG. 1, was fabricated. This fabrication process will now be explained with reference to FIGS. 2 to 6. A buffer layer 2 or an n-type GaAs layer having a thickness of 1 µm and a carrier concentration of 1x10 18 cm -3 , a lower clad layer 3 or an n-type Al 0.35 Ga 0.65 As layer having a carrier concentration of 5x10 17 cm -3 , an active layer 4 or a layer having a single quantum well (SQW) structure of undoped In 0.2 Ga 0.8 As of 6 nm in thickness and sandwiched between undoped GaAs optical guide layers of 60 nm in thickness, a first upper clad layer 5 or a p-type of Al 0.35 Ga 0.65 As layer having a thickness of 0.1 µm and a carrier concentration of 5x10 17 cm -3 , a second etching stop layer 6 or a p-type GaAs layer having a thickness of 10 nm and a carrier concentration of 5x10 17 cm -3 , a first etching stop layer 7 or an n-type In 0.5 Ga 0.5 P layer having a thickness of 20 nm and a carrier concentration of 5x10 17 cm - 3 , a current blocking layer 9 or an n-type Al 0.4 Ga 0.6 As layer having a thickness of 0.7 µm and a carrier concentration of 5x10 17 cm -3 and a cap layer 10 or an n-type GaAs layer having a thickness of 10 nm and a carrier concentration of 5x10 17 cm -3 were grown on the wafer 1 or an n-type GaAs wafer having a carrier concentration of 1x10 18 cm -3 in the described order by an MBE technique (FIG. 2). With a silicon nitride mask deposited on place (FIG. 3), etching was carried out using the first etching stop layer as an etching stop layer (FIG. 4). The etchant used herein was a mixture of sulfuric acid (98 wt%), hydrogen peroxide (a 30 wt% aqueous solution) and water at a volume ratio of 1:1:5, and the etching temperature and time were 25°C and 30 seconds, respectively. Then, the assembly was dipped in an etchant obtained by mixing HF (49%) and NH 4 F (40%) at 1:6 for 150 seconds to remove the silicon nitride layer (FIG. 5). The first etching stop layer was further etched using the second etching stop layer as an etching stop layer (FIG. 6). The etchant used herein was a mixture of hydrochloric acid (35 wt%) and water at 2:1, and the etching temperature and time were 25°C and 2 minutes, respectively. After this, a second upper clad layer 8 or a p-type Al 0.35 Ga 0.65 As layer having a carrier concentration of 1x10 18 cm -3 was grown in the opening at a thickness of 1.5 µm by an MOCVD technique, and a contact layer 11 to maintain good-enough contact with the electrode or a p-type GaAs layer having a thickness of 2 µm and a carrier concentration of 1x10 19 cm -3 was finally grown (FIG. 7), thereby forming a semiconductor laser diode. Example 2 Another laser diode was fabricated following Example 1 with the exception that: the thicknesses of the undoped GaAs guide layers were changed to 40 nm, a p-type Al 0.38 Ga 0.62 As layer was used as the first upper clad layer 5, an n-type Al 0.58 Ga 0.42 As layer was used as the first etching stop layer 7, using the first etching stop layer as an etching stop layer, etching was carried out with an etchant obtained by mixing together tartaric acid (50 wt%) and hydrogen peroxide (an 30 wt% aqueous solution) at a volume ratio of 2:1 at 25°C for 120 seconds, using the second etching stop layer as an etching stop layer, etching was carried out with an etchant consisting of hydrochloric acid (35 wt%) at 75°C for 1 minute, and the thickness of the contact layer 11 was changed to 3 µm. Example 3 The laser diode with a ridge current injection area, shown in FIG. 8, was fabricated. This fabrication process will now be explained with reference to FIGS. 9 to 15. A buffer layer 22 or an n-type GaAs layer having a thickness of 1 µm and a carrier concentration of 1x10 18 cm -3 , a lower clad layer 23 or an n-type Al 0.35 Ga 0.65 As layer having a carrier concentration of 5x10 17 cm -3 , an active layer 24 or a layer having a single quantum well (SQW) structure of undoped In 0.2 Ga 0.8 As of 6 nm in thickness and sandwiched between undoped GaAs guide layers of 60 nm in thickness, a first upper clad layer 25 or a p-type of Al 0.35 Ga 0.65 As layer having a thickness of 0.1 µm and a carrier concentration of 5x10 17 cm -3 , a second etching stop layer 26 or a p-type GaAs layer having a thickness of 10 nm and a carrier concentration of 5x10 17 cm -3 , a first etching stop layer 27 or a p-type In 0.5 Ga 0.5 P layer having a thickness of 20 nm and a carrier concentration of 5x10 17 cm - 3 , a second upper clad layer 28 or a p-type Al 0.35 Ga 0.65 As layer having a thickness of 1 µm and a carrier concentration of 1x10 18 cm -3 , and a cap layer 30 or a p-type GaAs layer having a thickness of 10 nm and a carrier concentration of 5x10 17 cm -3 were deposited on the wafer 21 or an n-type GaAs wafer having a carrier concentration of 1x10 18 cm -3 in the described order by an MBE technique (FIG. 9). With a silicon nitride mask deposited on place (FIG. 10), etching was carried out using the first etching stop layer as an etching stop layer (FIG. 11). The etchant used herein was a mixture of sulfuric acid (98 wt%), hydrogen peroxide (a 30 wt% aqueous solution) and water at a volume ratio of 1:1:5, and the etching temperature and time were 25°C and 30 seconds, respectively. Furtheremore, the first etching stop layer was etched away using the second etching stop layer as an etching stop layer (FIG. 12). The etchant used herein was a mixture of hydrochloric acid (35 wt%) and water at 2:1, and the etching temperature and time were 25°C and 2 minutes, respectively. After this, an n-type Al 0.4 Ga 0.6 As layer having a thickness of 1.5 µm and a carrier concentration of 5x10 17 cm -3 was grown in the form of a current blocking layer 29 by an MOCVD technique (FIG. 13). Following this, silicon nitride was removed by a plasma etching technique using SF 6 (FIG. 14). A p-type GaAs layer having a thickness of 2 µm and a carrier concentration of 1x10 19 cm -3 was grown in the form of a contact layer 31 again by an MOCVD technique (FIG. 15), thereby forming a laser diode. Example 4 Another laser diode was fabricated following Example 3 with the exception that: A p-type Al 0.58 Ga 0.42 As layer was used as the first etching stop layer 27, using the first etching stop layer as an etching stop layer, etching was carried out with an etchant obtained by mixing together tartaric acid (50 wt%) and hydrogen peroxide (an 30 wt% aqueous solution) at a volume ratio of 2:1 at 25°C for 120 seconds, and using the second etching stop layer as an etching stop layer, etching was carried out with an etchant consisting of hydrochloric acid (35 wt%) at 75°C for 1 minute. According to the present invention as explained above, the versatility of a semiconductor element having a ridge or groove can be much more exploited than ever before, and the ridge or groove of any desired shape can precisely be formed by the wet etching of a layer comprising Al Y Ga 1-Y As having any desired Al concentration. In addition, since the re-growing interface for re-growth can be GaAs, it is possible to improve the quality of crystal of the re-grown portion.

Claims: A semiconductor device including a substrate (1; 21) and on said substrate at least the following epitaxial layers: (a) an Al w Ga 1-w As layer (5; 25), (b) a second etching stop layer (6; 26), (c) a first etching stop layer (7; 27), (d) an Al y Ga 1-y As layer (9; 28), said layers (b), (c) and (d) being deposited on said layer (a) in the described order, wherein a portion of said layer (c) and a portion of said layer (d) have been removed, and the removed portion is replaced by (e) an Al t Ga 1-t As layer (8; 29), which is also an epitaxial layer, one of said layers (d) and (e) being a current blocking layer and the other being a clad layer, characterised in that the current blocking layer has a lower refractive index than the clad layer. The semiconductor device according to claim 1, wherein said second etching stop layer comprises GaAs and said first etching stop layer comprises Al x Ga 1-x As, and which conforms to the following condition: X-Y ≥ 0.1 The semiconductor device according to claim 1, wherein said second etching stop layer comprises Al Z Ga 1-Z As or GaAs and said first etching stop layer comprises In V Ga 1-V P. A process for fabricating a semiconductor device, comprising the steps of (i) epitaxially forming an Al w Ga 1-w As layer (5; 25) on a substrate (1; 21) (ii) epitaxially growing on said Al w Ga 1-w As layer (5; 25) the following three layers in the following order: a second etching stop layer (6; 26) a first etching stop layer (7; 27) an Al y Ga 1-y As layer (9; 28) (iii) etching away a portion of said Al y Ga 1-y As layer (9; 28) using said first etching stop layer (7; 27) as an etching stop layer, and etching away a portion of said first etching stop layer (7; 27) using said second etching stop layer (6; 26) as an etching stop layer, thereby forming a ridge or groove, (iv) epitaxially growing an Al t Ga 1-t As (8;29) layer alongside said ridge or inside said groove, wherein, in the case where said Al t Ga 1-t As layer is grown alongside said ridge, it is a current blocking layer and said Al y Ga 1-y As layer is a clad layer, and, in the case where said Al t Ga 1-t As layer is grown inside said groove, it is a clad layer and said Al y Ga 1-y As layer is a current blocking layer, characterised in that the current blocking layer has a lower refractive index than the clad layer. The process according to claim 4, wherein said second etching stop layer comprises GaAs and said first etching stop layer comprises Al X Ga 1-X As. The process according to claim 4, wherein said second etching stop layer comprises Al Z Ga 1-Z As or GaAs and said first etching stop layer comprises In V Ga 1-V P. A semiconductor device according to claim 1, which is a semiconductor laser.

Inventors: FUJIMORI TOSHINARI, GOTOH HIDEKI, HORIE HIDEYOSHI, NAGAO SATORU, FUJIMORI, TOSHINARI, GOTOH, HIDEKI, HORIE, HIDEYOSHI, NAGAO, SATORU, FUJIMORI, TOSHINARI, C/O MITSUBISHI CHEMICAL CORP., Gotoh, Hideki, c/o Mitsubishi Chemical Corp., HORIE, HIDEYOSHI, C/O MITSUBISHI CHEMICAL CORP., NAGAO, SATORU, C/O MITSUBISHI CHEMICAL CORP.
Applicants: MITSUBISHI CHEM CORP, MITSUBISHI CHEMICAL CORPORATION
Application year: 1995
Main classification: H01S5
IPC codes: H01S5, H01L33, H01L21