ORAL HYGIENE COMPOSITION

Abstract: Oral hygiene composition containing in combination chitosan and a sulphated, negatively charged polysaccharide in a biologically active amount; a process of improving oral hygiene in a mammal including man; and use of chitosan in combination with a sulphated, negatively charged polysaccharide for the manufacture of dentally active oral hygiene compositions.

Description: Oral hygiene composition The present invention relates to oral hygiene compo¬ sitions containing in combination certain polysaccharide components, a process to improve oral hygiene in mammals including man and the use of combinations of polysaccha- rides for the manufacture of dentally active oral hygiene compositions. Even if the present invention relates in general to oral hygiene it will primarily be illustrated in connec¬ tion with periodontitis, i.e. so called teeth loosening, and measures aiming at reducing active plaque, i.e. bacte¬ rial deposits on the surface of the tooth. Periodontitis is a collagen disease resulting in de- composition of the supporting tissue of the tooth, perio- dontal ligaments and bone tissue. This results in weake¬ ning of the attachment apparatus, finally resulting in loosening of the tooth. The tooth loosening procedure is inflammatoric and the cause is found in the bacterial pla- ques accumulated on the surface of the tooth and against which the immune defense of the body is not capable of adequate defense. The symptoms in periodontitis is generally in an early stage an inflammatoric change of the gingiva, i.e. the gums, which swells, reddens and becomes lightly blee¬ ding on probing. In the transit from gingivitis to perio¬ dontitis, the latter constituting the destructive part of the cause of the disease, the collagenous threads surroun¬ ding the attachment, the periodontium, are destroyed, and simultaneously plaques spread down into the periodontal pocket developed during the course of the disease. This results in deepening and inflammation of the pocket, and as the pathological periodontal pocket deepens the tooth loses more and more of its attachment thereby obtaining increased mobility. The traditional treatment of the disease conditions mainly aim towards active plaques, i.e. bacterial deposits on the surface of the tooth. The self-care of the patient in the form of thorough oral hygiene is of decisive impor- tance in this connection. Usually the mechanical oral hy¬ giene, tooth brushing, and interstitial hygiene using x thread or stick, is the most common and effective proce¬ dure. However, there are different chemical possibilities of affecting or preventing bacerial growth or bacterial adherence to the tooth. Professional tooth cleaning using a tooth hygienist and/or a dentist who removes plaque present and cleans the deep periodontal pockets inaccessible through common tooth cleaning reduces or eliminates the inflammation. If such cleaning of the tooth does not give the desired effect when carried out through the opening of the periodontal pocket a surgical treatment must be carried out. The gums are then folded aside so as to give full access to the pocket thereby enabling thorough cleaning. By means of different membranes the tissues can be kept apart during the course of healing and the tissue which is desired in healing will have precedence. This techniques are named "Guided Tissue Regeneration", abbre¬ viated GTR. GTR- reatment is presently the only way of providing periodontal healing with renewed growth of pe¬ riodontal supporting tissue. Since the healing process is controlled by a barrier giving priority to the slow perio¬ dontal ligament tissue, it is also conceivable to affect the process by means of substances that can affect the regenerative rate thereof. Oral compositions for the treatment of inter alia caries, periodontoclasia and foul breath are known. For example, GB,A, 2132889 discloses such oral compositions containing chitosan. Furthermore, oral compositions to inhibit or prevent periodontoclasia and caries containing certain sulphated polysaccharides are previously known from W0,A1, 8404453. It is also previously known to combat plaque using certain negatively charged polysaccharides, such as from EP,A1, 0 324 720 and GB,A, 2215730. Pharmaceutical compositions, inter alia in the form of a gel, for example for non-topical wound treatment con¬ taining one, two or several glycose aminoglykans, such as heparin, condroitin sulphate and chitosan, are previously known from W0,A1, 9312801. Furthermore, hypoglycaemic com¬ positions for oral administration containing oligo- or polysaccharides of natural origin and derivatives thereof, such as chitosan, condroitin sulphates and heparin, are previously known from STN International, File WPIDS, STN accesion No. 84-198108, JP,A, 59112922. Finally, from Chemical Abstracts, Vol. 121 (No. 3, 18 July 1994) ab- stract No. 26652, Vopr. Med. Khim. , 1994, 40 (2), page 37- 39 it is known that the combination of chitson sulphates and heparin affect the activity of lipoprotein lipase. The present invention has for its purpose to provide new techniques for improved oral hygiene. Another object of the invention is to provide new oral hygiene composi¬ tions which substantially improve the conditions to alle¬ viate the inflammatoric process in periodontitis and also to provide recreation of the attachment of the tooth. Yet another purpose of the invention is to provide oral hygiene compositions which reduce the formation of active plaques on the surface of the tooth. A further object of the invention is to provide a process to improve oral hygiene in mammals including man. Yet another object of the invention is to provide use of certain polysaccharides in combination for the manufac¬ ture of dentally active oral hygiene compositions. For these and other objects which will be clear from the following disclosure there is provided through the present invention an oral hygiene composition which in combination comprises chitosan and a sulphated, negatively charged polysaccharide in a biologically active amount. In the composition according to the invention it is preferred that the weight ratio chitosan:sulphated poly¬ saccharide lies within the range about 6:4 to 95.5:0.5. Among useful polysaccharides in oral hygiene composi- tions according to the present invention there may be men¬ tioned heparin, sucralfat, condroitin-6- or -4-sulphates, dermatan sulphate, keratan sulphate and pentosan sulpha¬ tes. It is particularly preferred in the oral hygiene com- position according to the invention to use chitosan in combination with heparin, the weight ratio between these two components preferably lying within the range about 10:1 to 99.5:0.5. The oral hygiene composition according to the present invention suitably contains chitosan and sulphated poly- saccaride in combination with a dentally acceptable car¬ rier. The oral hygiene composition can be presented in the form of a tooth cream, a tooth paste or in the form of a tooth powder. It may also be presented in the form of a mouth wash or in the form of a mouth spray. Finally, the oral hygiene composition according to the invention can be presented in the form of degradable films, gels, pearls or powders. The composition according to the present invention is preferably in accordance with one aspect of the invention presented in the form of a tooth cream, a tooth paste or a tooth powder. As an alternative the composition can also be presented in the form of a chewing gum, a tablet, a lo¬ zenge or the like. Compositions of these types have, in addition to the special combination of chitosan and a sul¬ phated, negatively charged polysaccharide, a composition corresponding to the conventional techniques in the art. The special combination of the chitosan and sulphated po¬ lysaccharide in accordance with the present invention is present in the composition in a suitable minor amount, preferably from about 1 to about 25 percent by weight and particularly from about 5 to about 15 percent by weight based on the composition as a whole. When the composition is presented in the form of a tooth treatment agent, such as tooth paste, it may also include a grinding agent in accordance with conventional techniques. Such grinding agents can be taken from the traditional tooth agent techniques and be constituted by for example silica, alumina, hydroxyapatite, plastic par¬ ticles or mixtures thereof. The grinding agent is present in the composition in a minor amount, preferably within the range 5 to 25 percent by weight. The composition according to the present invention may optionally contain fluoro compounds for providing fur¬ ther anticaries effect. Such fluoro-containing compounds are suitable of an ionic type and can be constituted by a fluoride salt, such as an alkali metal fluoride. Among preferred fluorides there may be mentioned sodium fluoride but also the corresponding potassium or litium salts can be used. In a conventional manner the composition may further- more contain phosphates of different types in accordance with conventional techniques. Moreover, the composition according to the invention may contain other excipients, such as surface active substances, gelling agents and other constituents, such as flavouring, sweetening and colouring agents. Furthermore, the compositions according to the invention, which are presented in the form of tooth paste, may contain gelling agents, such as a natural or synthetic material. Among such materials there may be men¬ tioned natural gums, such as locust bean gum, guar gum, xanthan gum and the like. Even if such non-ionic gums are preferred other materials may be used, for example tragant gum, sodiumcarboxymethyl cellulose, poly(vinylpyrroli- done), starch or the like. Such gelling agents are contai¬ ned in the composition in a relatively small amount, for example from about 0.01 to 3 percent by weight of the composition. Oral hygiene compositions according to the invention in the form of mouth washes can be presented as conven¬ tional gargles or can be presented in the form of contai¬ ners designed as oral spray devices. Additionally, the compositions according to the in¬ vention can contain as sweeteners for example saccarine, flavouring oils, such as peppermint oil, menthol, and colouring agents or white pigments, such as titanium di¬ oxide, preserving agents, for example bensoates, an ibac- terial substances, such as chlorohexidin. According to another aspect of the invention there is provided also a process for improving oral hygiene in mam¬ mals including man, and in this process there is adminis¬ tered orally to a mammal in need of treatment a biologi- cally active amount of an oral hygiene composition as de¬ fined above. The process according to the invention is suitable for the treatment of periodontitis, plaques and/or caries. According to yet another aspect of the present inven- tion it resides in the use of chitosan in combination with a sulphated, negatively charged polysaccharide for the ma¬ nufacture of a dentally active oral hygiene composition as has been defined above. It is particularly preferred in this use that the chitosan is present in combination with heparin. The expression "minor amount" used in the present disclosure in connection with proportions between cons¬ tituents present refers to an amount less than about 50 percent by weight based on the composition as a whole. The present invention will in the following be fur¬ ther illustrated by non-limiting examples, wherein percen¬ tages or proportions refer to weight unless otherwise in¬ dicated. MATERIALS USED Chitosan Chitosan is a linear 1.4-bound polysaccharide built from free and N-acetylated β-D-glucosamine units. It is manufactured by N-deacetylation of chitin, a polymer for¬ ming the shell of inter alia insects and crab fish. The degree of deacetylation can be controlled by hydrolysis using alkali. In the present case the chitosan is used in the form of commercially available hydrochloric salts of about 20%, 50% and 85% N-deacetylation. Sulphated polysaccharides The preferred polysaccharide is the proteoglycane heparin (Pig mucosa, Kabi Vitrum) and other polysaccha- rides used are of a commercial type available on the market. EXAMPLE 1 Film of chitosan-heparin 5 g HC1 salt of chitosan of 50% deacetylation (Pronova Biopolymers, Seacure Cl 411) or of 85% deacetyla¬ tion (Pronova Biopolymers, Seacure Cl 313) are dissolved in distilled water (0.5 L, 1% w/v). The film is prepared in petri-dishes having a surface of 54 cm 2 . 20 mL of the solution is poured into the bowl and the film is then al¬ lowed to dry in a drying cabinet at 70C° for 16 h. The film is then neutralized using a sodium phosphate buffer, 0.2 M, pH 9, added to the petri-dish at room temperature. The film is allowed to stay in the buffer for 3-4 h and is then washed 3-4 times using 50 mL distilled water and is allowed to dry at room temperature. A heparin solution is prepared according to the following: To 100 mL 0.15 M sodium chloride there is added 25 mg nitrite degraded heparin (Pig mucosa, Kabi Vitrum). The pH is adjusted to 3.9 using 0.1 M hydrochloric acid, and 5 mg sodium cyanoborohydride are added to the solution. The chitosan film is left in this solution under shaking over night. The film is then washed with 50 mL distilled water 3-4 times. EXAMPLE 2 Gel pearls of chitosan-heparin A solution (2% w/v) of chitosan of 85% deacetylation (Pronova Biopolymers, Seacure Cl 313) is drop-wise pumped through a capillary (0.8 mm inner diameter) down into a sodium phosphate buffer, 0.1 M, pH 7, 250 mL. Gel pearls of chitosan having a diameter of about 1.2 mm are formed. After filtering on a glass filter and drying, the diameter of the balls is reduced to about 0.8 mm. Heparin is attached to the balls by ionbinding by admixing hepa- rin, 1 g/L, in the buffer used. EXAMPLE 3 Gel of chitosan- ethyl cellulose-heparin 100 mg heparin are added to 100 mL distilled water with mixing. To the solution obtained there are added 50 mL of an aqueous solution of methyl cellulose (2% w/v) under stirring. To the solution obtained there is then added 50 mL chitosan (2% w/v, 50% deacetylation) also under stirring. Stirring is maintained for another 10 minutes, a coherent gel being obtained. EXAMPLE 4 Film of chitosan-heparin, covalently bound A neutralized chitosan film made in accordance with the description of Example 1 is immersed in 20 mL of a so¬ lution wherein it is allowed to remain for 24 h. The solu¬ tion consists of 4,4 g sodium chloride and 125 mg perio- date oxidized heparin in 0.5 L of water. The pH is adjus¬ ted to 3.9 with 0.5 M hydrochloric acid, and then 15 mg of sodium cyanoborohydride is added. The film treated in this manner is then washed with water 3-4 times and is allowed to dry. EXAMPLE 5 Film of chitosan-heparin, ion bound To a neutralized chitosan film made in accordance with Example 1 there is added 20 mL of a solution consis¬ ting of 125 mg heparin dissolved in 0.5 L of water contai¬ ning 4.4 g sodium chloride, the pH being adjusted to 3.9 with the use of 0.5 M hydrochloric acid. Film and solution are allowed to stand in room temperature for 14 h. The film obtained is then washed with water 3-4 times and allowed to dry. EXAMPLE 6 Tooth paste A tooth paste is prepared as follows: Ingredients Percentage Sugar solution (50% solut :ion 25 of sorbitol, saccarin) Glycerol 8 Titanium dioxide 1.5 Thickening agent, silica 5 Grinding agent, alumina 12 Surfactant 1 Flavour 0.5 Gel according to Example 3 10 Water 37 100 The ingredients above are mixed in a suitable appa¬ ratus in a conventional manner whereafter, if necessary, the pH is adjusted to about neutral. EXAMPLE 7 Tooth powder Heparin (Pig mucosa) in pulverulent form is admixed with chitosan (50% deacetylation, Pronova Biopolymers, Seacure Cl 411) to form a fine-grained dry powder useful as an oral hygiene composition. EXAMPLE 8 Mouth wash Ingredients Percentage Ethanol 8 Glycerol 4 Flavours 0.1 Gel according to Example 3 5 Water 82.9 100.0 The ingredients are mixed in the proportions given to form a slightly cloudy mouth wash. EXAMPLE 9 Clinical test of tooth powder The tooth powder according to Example 7 is used in connection with tooth brushing daily for 2 months for the purpose of studying the influence on the general tooth status and the condition of the periodontal pockets of the subject under test. The result after two months tooth brushing was the following according to the evaluation made by tooth technicians: Periodontal pockets Pocket depth 10 pockets 1 mm deeper 31 " unchanged 45 " 1 mm reduction 6 " 2 mm reduction 4 " 3 mm reduction 3 " 4 mm reduction Furthermore, no visible inflammation could be obser- ved and, in addition, X-rays taken of the front teeth of the subject indicate newly formed tissue around the teeth. Since the development of periodontal pockets to an increa¬ sed depth normally in accordance with conventional art can be retarded but rarely reversed the results presented above are unexpected and essential. EXAMPLE 10 Clinical test using tooth paste The test according to Example 9 is repeated, this time using the tooth paste manufactured according to Ex¬ ample 6. The results obtained are similar to those obtai¬ ned in Example 9. Furthermore, there is obtained as a re¬ sult of the modified brushing of the teeth a clear plaque- reducing effect in relation to normal teeth brushing using normal tooth paste. This reduction of plaque results in a clear regression of the gingival inflammation, and a dis¬ tinct mobility reduction could also be observed. EXAMPLE 11 Clinical test using film In relation to a factual periodontal pocket a surgi¬ cal incision was performed residing in cutting, after anaesthesia, with a scalpel in the gingiva along the out¬ side of the tooth and the inside the tooth in the area involved. The gingiva is folded out from the tooth and the root surface of the tooth having plaque deposited thereon is exposed. The root surface is now cleaned with an ins¬ trument for removal of plaque, and after cleaning and washing using sterile solutions the chitosan-heparin film made in accordance with Example 1 is applied locally, and the gingiva is then stitched back onto the surface of the tooth. In connection with healing reduced inflammation, re¬ duced pathological pocket depth, reduced mobility and im¬ proved attachment by X-ray could be observed. EXAMPLE 12 Clinical test using gel pearls The procedure in Example 11 is repeated, in this in¬ stance while using gel pearls of chitosan-heparin manufac¬ tured according to Example 2. Similar results are obtai- ned. EXAMPLE 13 Clinical test using gel The procedure of Example 11 is repeated, this time while using the gel of chitosan-methylcellulose-heparin prepared according to Example 3. Similar results to those of Example 11 can be observed. EXAMPLE 14 Mouth-wash Example 8 is repeated while using dermatan sulphate as a sulphated polysaccharide instead of heparin. EXAMPLE 15 Clinical test using tooth powder Example 9 is repeated in this case using a tooth pow¬ der according to Example 7 wherein heparin is replaced with condroitin-6-sulphate. EXAMPLES 16-20 Test for antibacterial activity using solutions The following solutions are prepared: 1) Dextransulphate (Pharmacia, lg) is dissolved in 200 L of distilled water. To the stirred solution are added 50 L of an aqueous solution of methylcellulose (2% w/v) and 250 L of chitosan (2% w/v, with a degree of deacetylation Of 59% ) . 2) To water (200 mL) are added 50 mL of an aqueous solu¬ tion of rnethylcellulose (2% w/v) and 250 mL of chitosan (2% w/v, with a degree of deacetylation of 59%). 3) Heparin (lg) is dissolved in 200 mL of distilled water. To the stirred solution are added 50 mL of an aqueous so¬ lution of rnethylcellulose (2% w/v) and 250 mL of chitosan (2% w/v, with a degree of deacetylation of 59%). 4) Heparin (Pig mucosa, Kabivitrum, lg) is dissolved in 450 L of distilled water. To the stirred solution is ad¬ ded 50 mL of an aqueous solution of rnethylcellulose (2% w/v). 5) Dextransulphate (Pharmacia, lg) is dissolved in 450 mL of distilled water. To the stirred solution is added 50 mL of an aqueous solution of rnethylcellulose (2% w/v). The solutions are tested for antibacterial activity in blood bowls coated with saliva diluted 1:10 and dried in an incubator for 30 min before use. Longitudinal grin¬ ding sections of teeth exposing enamel and cement are im- mersed in the respective test solutions for 5 min at 37°C and then transferred to sterile physiological salt water for up to 3 h. At 0 min, 15 min, 30 min, 1 h, 2 h, 3 h one grinding section from each test series is removed and pla¬ ced on two coated blood bowls. A negative control is placed in the centre of each bowl. The antibacterial activity of the respective solu¬ tions is evaluated according to a score from 0 to 3. Solu¬ tions 1, 2 and 3 of Examples 16, 17 and 18, respectively, are selectively antibacterial after 30 min rinsing and keep their antibacterial activity during the test period of 3 h. The results are summarized in the following table. TABLE Example Solution Score 16 1 3 17 2 2 18 3 3 19 4 0 20 5 0 It can be seen from the table above that using so- lutions containing only heparin or dextran sulphate in addition to ehtylcellulose express no observable anti¬ bacterial activity, whereas solutions combining either chitosan and dextran sulphate or chitosan and heparin show the highest score. Since, in addition to rnethylcellulose, solely chitosan shows a lower score the test results indi¬ cate a synergistic effect by the combination of chitosan and the sulphated negatively charged polysaccharides. As is clear from performed clinical tests the use of the techniques according to the present invention induces essential and unexpected improvements in relation to the course of healing in connection with oral problems resi¬ ding in periodontitis, formation of plaque and other in- flammatoric conditions. Even though the present invention is not regarded to be restricted to any particular scien- tific theory or mechanism of action it is conceivable that the main constituents chitosan and sulphated, negatively charged polysaccharide present in the oral hygiene compo¬ sition have such effect on the bacterial flora in the oral cavity or result in such enrichment of growth factors that the different healing processes are substantially promoted and accelerated. The invention is not restricted to the preferred embodiments as exemplified and the scope of the invention is limited only by the appended claims.

Claims: CLAIMS I. Oral hygiene composition containing in combination chitosan and a sulphated, negatively charged polysaccha¬ ride in a biologically active amount. 2. Oral hygiene composition according to claim 1, wherein the weight ratio chitosan-polysaccharide lies within the range about 6:4 to 99.5:0.5. 3. Oral hygiene composition according to claim 1 or 2, wherein the polysaccharide is selected among: heparin, sucralfat, condroitin sulphates, dermatan sulphate, kera- tan sulphate and pentosan sulphates. 4. Oral hygiene composition according to claim 3, wherein the polysaccharide is heparin. 5. Oral hygiene composition according to any prece- ding claim comprising chitosan and polysaccharide and a dentally acceptable carrier. 6. Oral hygiene composition according to claim 5 in the form of a tooth cream, tooth paste or a tooth powder. 7. Oral hygiene composition according to claim 5 in the form of a mouth wash. 8. Oral hygiene composition according to claim 5 in the form of a mouth spray. 9. Oral hygiene composition according to any of claims 1 to 4 in the form of a degradable film, in the form of a gel, in the form of pearls or in the form of a powder. 10. A process for improving oral hygiene in a mammal including man, characterized by administering orally to the mammal a biologically active amount of an oral hygiene composition according to any preceding claim. II. A process according to claim 10 for the treatment of periodontitis, plaque and/or caries. 12. The use of chitosan in combination with a sulpha¬ ted, negatively charged polysaccharide for the manufacture of a dentally active oral hygiene composition. 13. Use according to claim 12, wherein the chitosan is present in combination with a polysaccharide selected among: heparin, sucralfat, condroitin sulphates, dermatan sulphate, keratan sulphate and pentosan sulphates. 14. Use according to claim 13, wherein the chitosan is present in combination with heparin.

Inventors: LARM OLLE, LARM, OLLE
Applicants: LARM OLLE, LARM, OLLE
Application year: 1995
Main classification: A61K7
IPC codes: A61K8, A61Q11